METHOD OF COATING A LUMINESCENT MATERIAL

Abstract: The invention relates to a method of coating a luminescent material with a layer of a metalpolyphosphate wherein the metal is chosen from the group formed by Ca, Sr and Ba. According to the invention, the luminescent material is dispersed in a watery solution of sodium polyphosphate, a watery solution of nitrate of the metal M is added, after which the luminescent material is separated, dried and fired.

Description: Method of coating a luminescent material. The invention relates to a method of coating a luminescent material with a protective layer. The invention also relates to a luminescent material coated with a protective layer and to a discharge lamp equipped with a luminescent screen comprising such a luminescent material. A method as mentioned in the opening paragraph is known from EP 0476207 A2. This document describes the coating of a silicate phosphor making use of chemical vapour deposition. Coated luminescent materials show a relatively high stability in the watery slurry that is used in a lamp manufacturing process and an improved maintenance of the light output, when used for instance in the luminescent screen of a low pressure mercury discharge lamp. A drawback of chemical vapour deposition is that the equipment is very expensive. Alternatively coatings can be applied to luminescent materials by means of homogeneous precipitation from a watery solution. Such a process is described for instance in WO 96/05265 and is mainly used to apply metal oxide layers wherein the metal is chosen from the group Y and Al. This latter process is far cheaper than chemical vapour deposition but needs to be carried out at a relatively low pH to prevent the precipitation of large quantities of metal hydroxide. However, many luminescent materials (for instance materials having a silicate host lattice) are sensitive towards hydrolysis at the relatively low pH values at which the homogeneous precipitation is taking place. Additionally it has been found that the optical properties such as reflectivity and quantum efficiency of other luminescent materials that do not or hardly hydrolize in water are adversely affected by a low pH value. The invention has for its object to provide a method of coating a luminescent material by means of homogeneous precipitation from a watery solution in which hydrolysis of the luminescent material and degradation of its optical properties are to a large extent prevented. According to the invention, a method as described in the opening paragraph is for this purpose characterized in that the luminescent material is dispersed in a watery solution of water soluble polyphosphate, a watery solution of a water soluble salt of a metal M chosen from the group formed by Ca, Sr and Ba is added to the dispersion after which the luminescent material is separated from the watery dispersion and is dried and heated. The product of a method according to the invention is a luminescent material coated with a protective layer, characterized in that the layer comprises a polyphosphate of general formula (M 0.5 PO 3 ) n in which metal M is chosen from the group formed by Ca, Sr and Ba. It has been found that the precipitation of a polyphosphate of a metal M chosen from the group formed by Ca, Sr and Ba using a method according to the invention can very well be carried out at a relatively high value of the pH. As a consequence hydrolysis and degradation of the luminescent material are strongly suppressed. Good results have been obtained with a method according to the invention, wherein the water soluble polyphophate is sodium polyphosphate and/or wherein the water soluble salt of the metal M is a nitrate. Preferably the pH of the watery solution of water soluble polyphosphate is adjusted to be in the range 8-10 before the luminescent material is dispersed in it. It was found that both hydrolysis and degradation of the luminescent material were effectively suppressed. To effect a dense coating with a thin layer of polyphosphate on the surface of the particles of luminescent material, the dispersion is preferably treated with ultrasonic waves to desagglomerate the luminescent material before the watery solution of the water soluble salt of the metal M is added. The method was found to be very suitable for coating luminescent materials comprising a silicate host lattice. Good results have been obtained for BaSi 2 O 5 activated with lead and (Ba, Sr) 2 MgSi 2 O activated with lead. More in particular in case M was chosen as Ca. A luminescent material coated by means of a method according to the invention was found to be very suitable to be used in a discharge lamp, more in particular a low pressure mercury discharge lamp. The invention will now be illustrated by means of a description of three embodiments. In the first embodiment BaSi 2 O 5 with lead (BSP) is coated with calciumpolyphosphate. 2.45 gram of sodiumpolyphosphate is dissolved in 150 ml water. After filtration of the solution 1000 ml water is added. The pH is adjusted to pH 8.7 by adding NH 3 and 100 gram of BSP is is dispersed in the solution. The suspension is treated with ultrasonic waves for two minutes. A solution is prepared of 4.25 gram Ca(N0 ) 2 in 180 ml water. 20 ml of 1M NH 3 is added to this solution. The solution is then added to the phosphor suspension dropwise within 15 minutes. The coated phosphor is separated by vacuum filtration and washed two times by dispersion in 400 ml water and subsequent vacuum filtration. The clean product is dried at 100 C for 2 hours. Finally, the coated phosphor is fired at 400 C for 1 hour. The emission spectrum of coated BSP was substantially identical to that of uncoated BSP (λmax = 351 nm; FWHM = 38 nm for coated BSP and λmax = 350 nm; FWHM = 38 nm for uncoated BSP). Also the reflection coefficients for 254 nm and 350 nm radiation were almost identical (20 % and 96 % for uncoated BSP and 20 % and 98 % for coated BSP respectively). Surprisingly, however, the quantum efficiency for 254 nm radiation of the coated BSP was found to be 3 % higher than that of uncoated BSP (91 % and 88 % respectively). In a second embodiment BaSi 2 O 5 activated with lead (BSP) is coated with bariumpolyphosphate. 1.02 gram of sodiumpolyphosphate is dissolved in 100 ml water. After filtration of the solution 600 ml water is added. The pH is adjusted to pH 9.2 by adding NH 3 and 50 gram of BSP is dispersed in that solution. The suspension is treated with ultrasonic waves for two minutes. A solution is prepared of 1.96 gram Ba(N0 3 ) 2 in 180 ml water. 20 ml of 1M NH 3 is added to this solution. The solution is then added to the phosphor suspension dropwise within 15 minutes. The coated phosphor is separated by vacuum filtration and washed two times by dispersion in 200 ml water and subsequent vacuum filtration. The clean product is .dried at 100 C for 2 hours. Finally, the coated phosphor is fired at 600 C for 2 hours. The emission spectra of coated and uncoated BSP are substantially identical (λmax = 350 nm; FWHM = 38 nm). The quantum efficiency for 254 nm radiation of coated and uncoated BSP was found to be 93 % and 88 % respectively. The reflection coefficients for 254 nm and 350 nm radiation were 20 % and 96 % for uncoated BSP and 20 % and 97 % for coated BSP respectively. In a third embodiment Sr 2 MgSi 2 O 7 activated with lead (SMS) is coated with calciumpolyphosphate. 0.51 gram of sodiumpolyphosphate is dissolved in 50 ml water. After filtration of the solution 600 ml water is added. The pH is adjusted to a value of 9.4 by adding NH 3 and 25 gram of SMS is dispersed in that solution. The suspension is treated with ultrasonic waves for two minutes. A solution is prepared of 0.885 gram Ca(N0 3 ) 2 in 180 ml water. 20 ml of 1M NH 3 is added to this solution. The solution is then added to the phosphor suspension dropwise within 15 minutes. The coated phosphor is separated by vacuum filtration and washed two times by dispersion in 200 ml water and subsequent vacuum filtration. The clean product is dried at 100 C for 2 hours. Finally, the coated phosphor is fired at 600 C for 1 hour. The emission spectra of coated and uncoated SMS are very similar (λmax = 360 nm; FWHM = 60 nm for uncoated SMS and λmax = 358 nm; FWHM = 64 nm for coated SMS). The quantum efficiency of coated and uncoated SMS was found to be 76 %. The reflection coefficients for 254 nm radiation were 11 % and 10 % for uncoated SMS and for coated SMS respectively. The reflection coefficients for 360 nm radiation were 97 % and 90 % for uncoated SMS and for coated SMS respectively.

Claims: CLAIMS: 1. A method of coating a luminescent material with a protective layer characterized in that the luminescent material is dispersed in a watery solution of water soluble polyphosphate, a watery solution of a water soluble salt of a metal M chosen from the group formed by Ca, Sr and Ba is added to the dispersion after which the luminescent material is separated from the watery dispersion and is dried and heated. 2. A method according to claim 1, wherein the water soluble polyphophate is sodium polyphosphate. 3. A method as claimed in claim 1 or 2, wherein the water soluble salt of the metal M is a nitrate. 4. A method as claimed in claim 1, 2 or 3, wherein the pH of the watery solution of water soluble polyphosphate is adjusted to be in the range 8-10 before the luminescent material is dispersed in it. 5 A method as claimed in one or more of the previous claims, wherein the dispersion is treated with ultrasonic waves before the watery solution of the water soluble salt of the metal M is added. 6. Luminescent material coated with a protective layer, characterized in that the layer comprises a polyphosphate of general formula (Mo .5 PO 3 ) n in which metal M is chosen from the group formed by Ca, Sr and Ba. 7. Luminescent material according to claim 6, comprising a silicate host lattice. 8. Luminescent material according to claim 7, comprising BaSi 2 O 5 activated with lead. 9. Luminescent material according to claim 7, comprising (Ba, Sr) 2 MgSi 2 O 7 activated with lead. 10. Luminescent material according to claim 7, 8 or 9, wherein M is Ca. 11. Discharge lamp equipped with a luminescent screen comprising a luminescent material according to one or more of claims 6 - 10. 12. discharge lamp according to claim 11, wherein the discharge lamp is a low pressure mercury discharge lamp.

Inventors: JUESTEL THOMAS, MAYR WALTER, NIKOL HANS, RONDA CORNELIS R, JUESTEL, THOMAS, MAYR, WALTER, NIKOL, HANS, RONDA, CORNELIS, R.
Applicants: KONINKL PHILIPS ELECTRONICS NV, PHILIPS CORP INTELLECTUAL PTY, KONINKLIJKE PHILIPS ELECTRONICS N.V., PHILIPS CORPORATE INTELLECTUAL PROPERTY GMBH
Application year: 1999
Main classification: C09K11
IPC codes: C09K11, H01J9, H01J61