Cosmetic composition comprising associative thickener based on polyurethane

Abstract: In order to provide a cosmetic composition which is excellent in stability of viscosity and usability, the cosmetic composition of the present invention comprises an associative thickener, which is composed of a compound shown in Formula (1), and the cosmetic composition is an oil-in-water emulsion composition, which further comprises a water-soluble polymer: R 1 ―{(O―R 2 ) k ―OCONH―R 3 [―NHCOO―(R 4 ―O) n ―R 5 ] h } m wherein R 1 , R 2 , and R 4 each is a hydrocarbon group, which may be the same or different each other; R 3 is a hydrocarbon group, which may have urethane bond; R 5 is a straight chain, branched chain or secondary hydrocarbon group; m is an integer of 2 or more; h is an integer of 1 or more; and k and n each is an integer within the range of 0 to 1000, respectively.

Description: FIELD OF THE INVENTION The present invention relates to a cosmetic composition and, in particular, to an improvement of a thickener to be compounded therein. BACKGROUND OF THE INVENTION Various aqueous thickeners are compounded into the cosmetic so as to preserve the form of cosmetic. Examples of organic compound thickeners include natural polymers such as polysaccharides, casein and xanthan gum, and synthetic polymers such as acrylic polymer and carboxyvinyl polymer. Examples of inorganic compound thickeners include various clay minerals such as montmorillonite, and silica and the like. These thickeners have been suitably and selectively used according to its purposes and effects. In case of using a composition including such thickeners for the cosmetic, stable viscosity i.e., pharmaceutical form can be preserved within various temperature ranges, is required, while the feel in using, i.e., usability and the like are required because the cosmetic is mainly used to the skin as external use. However, among the cosmetic compositions, which include the conventional thickeners, the composition that sufficiently satisfies stability of viscosity and favorable usability is unknown. For example, the cosmetic compositions compounding conventional polymer thickeners such as vinyl thickeners and cellulose thickeners, which have been used in the past, are comparatively high in stability and require a small amount of thickener. However, in the case where such composition is used to the skin, sliminess feeling peculiar to polymer is occurred and the composition has unfavorable feeling of use. Also, the cosmetic composition comprising clay mineral has high thixotropic property and refreshing feeling after use, and is favorable in usability. However, such composition is unstable because syneresis occurs easily due to temperature change. EP-A-0 761 780 discloses a viscosity conditioner which comprises a compound structured to have a group of the following formula (1) where R is a hydrocarbyl group, R' is a branched or secondary hydrocarbyl group, and n ranges from 1 to 500. Also disclosed are an emulsion composition and an emulsion paint composition, each of which include the viscosity conditioner. SUMMARY OF THE INVENTION The present invention is achieved in view of the foregoing prior art, an object of the present invention is to provide a cosmetic composition which is excellent both in stability of viscosity and in usability. As the result of diligent studies of the present inventors for attaining the above-mentioned object, it has been found that a cosmetic composition, which is excellent both in stability of viscosity and in favorable usability, can be obtained by compounding a specific associative thickener as a main ingredient of thickeners. Further, the present inventors have been found that time stability of viscosity at high temperature and time stability of emulsion in case of an oil-in-water emulsion composition, are improved by using a polyhydric lower alcohol together with the associative thickener. Accordingly the present invention has been accomplished. Namely, a cosmetic composition of the present invention comprises an associative thickener, which is composed of a compound shown in Formula (1), R 1 ―{(O―R 2 ) k ―OCONH―R 3 [―NHCOO―(R 4 ―O) n ―R 5 ] h } m wherein R 1 , R 2 , and R 4 each is a hydrocarbon group, which may be same or different each other; R 3 is a hydrocarbon group, which may have urethane bond; R 5 is a straight chain, branched chain or secondary hydrocarbon group; m is an integer of 2 or more; h is an integer of 1 or more; and k and n each is an integer within the range of 0 to 1000, respectively, wherein said composition further comprises a polyhydric lower alcohol. Also, in the present invention, it is preferable that the associative thickener is an alkylene group having 2-4 carbon atoms that R 2 and/or R 4 each may be same or different or phenylethylene group. It is also preferable that R 3 is a residue of polyisocyanate which is shown as R 3 ― (NCO) h+1 . It is also preferable that the polyisocyanate which is shown as R 3 ―(NCO) h+1 is a polyisocyanate having urethane bond, which is obtained by reacting divalent to octavalent polyol with divalent to tetravalent polyisocyanate. It is also preferable that R 1 is a residue of polyol which is shown as R 1 ―(OH) m . It is also preferable that R 5 is a straight chain, branched chain or secondary hydrocarbon group having 8-36 carbon atoms. It is also preferable that the associative thickener is a resultant of one or more of polyetherpolyol that is shown as R 1 ―[(O―R 2 ) k ―OH] m , one or more of polyisocyanate that R 3 is shown as R 3 ―(NCO) h+1 , and one or more of polyether monoalcohol shown as HO―(R 4 ―O) n ―R 5 . It is also preferable that the cosmetic composition of the present invention comprises 0.01 to 10 wt% of the associative thickener and 0.1 to 30 wt% of the polyhydric lower alcohol. It is also preferable that the cosmetic composition of the present invention is an oil-in-water emulsion composition. It is also preferable that the cosmetic composition of the present invention comprises 0.1 to 5 wt% of the associative thickener, 40wt% or less of an oily ingredient, and 10 times or less of cmc (critical micellar concentration) of an ionic surfactant. It is also preferable that the cosmetic composition of the present invention comprises 0.1 to 5 wt% of the associative thickener, 40wt% or less of the oily ingredient, and 10 wt% or less of a nonionic surfactant whose HLB is 12 or less. It is also preferable that the cosmetic composition of the present invention comprises 0.1 to 5 wt% of the associative thickener, 40wt% or less of the oily ingredient, and 8 wt% or less of the nonionic surfactant whose HLB is 15 or less. It is also preferable that the cosmetic composition of the present invention comprises 0.1 to 5 wt% of the associative thickener, 40wt% or less of the oily ingredient, and 6 wt% or less of the nonionic surfactant whose HLB is 15 or more. BRIEF DESCRIPTION OF THE DRAWINGS Fig. 1 is an explanatory drawing of the associative thickener to be compounded into the cosmetic composition in accordance with the present invention. Fig. 2 shows the associative thickeners to be compounded into the cosmetic compositions of the present invention, which are manufactured by Manufacturing Examples A to G. Fig. 3 is an explanatory drawing of thickening mechanism of the associative thickener to be compounded into the cosmetic composition of the present invention, with surfactants. Fig. 4 shows percutaneous absorption promoting effect of the pharmaceutical in the cosmetic composition of the present invention. Fig. 5 shows irritation relaxation effect of the cosmetic composition of the present invention. BEST MODE FOR CARRYING OUT THE INVENTION In the following, the embodiment for carrying out the present invention will be explained in further detail. The present invention has been achieved by the following development process. A polymer thickening gelling agent is generally used for thickening an aqueous solvent. Some fundamental theories exist in thickening mechanism of the solvent by the polymer. "Chain disentanglement" theory requires that the polymer have extremely high molecular weight that will change considerably large hydrodynamic volume in dissolution condition. Thickening is effected by generating "chain disentanglement" that a solvated long polymer chains are mixed with the other polymer chains. The point of this model are: (a) interaction of water-soluble thickener polymer chain and latex particle does not exist; (b) water-soluble thickener polymer chain is drawn or become low viscosity with deforming visco-elastically under shearing condition; (c) visco-elastic polymer chain recovers and very low fluidity and leveling with respect to aqueous system occur immediately after stopping shearing. The more established thickener, i.e., usual cellulose derivatives, natural rubber, and synthetic water-soluble polymer of extremely high molecular weight, achieve their thickening mechanism by this "chain disentanglement". On the other hand, the other theory about thickening polymer in aqueous system is called "associative thickening". This theory is considered as follows. A copolymer which is composed of water-soluble monomer and hydrophobic monomer and which is relatively low molecular weight is associated in aqueous solvent with hydrophobic interaction. The copolymer is cross-linked physically, and accordingly, this action thickens the system with behaving just like one huge molecule (associative thickener is defined in, e.g., Encyclopedia of Polymer Science and Engineering, Second Edition, 17, 772-779). Also, in the case where hydrophobic particle such as latex exists in the system, the same thickening effect is shown by forming physical cross-linking that hydrophobic group of molecule chain adsorbs to the surface of particle. The important aspects of "associative thickening" theory are: (a) association of molecule hydrophobic group themselves in aqueous solvent or adsorption of polymer hydrophobic group in the surface of hydrophobic particle; (b) association of molecule themselves or decrease of viscosity by dividing and desorption of adsorption group under shearing or shearing guiding condition; and (c) when shearing force is removed, favorable flow property and leveling property are achieved by increasing viscosity in the controlled velocity by reassociation and adsorption. The present invention is to provide a cosmetic composition including advanced associative thickener, which is substantiated by this "association thickening" theory. The associative thickener compounded into the cosmetic composition of the present invention is a copolymer whose skeleton is a hydrophilic group and which has hydrophobic portion in the terminal as shown in Fig. 1. The associative thickener demonstrates thickening action by associating the hydrophobic portions themselves of the copolymer in the water-soluble medium. The associative thickener copolymer to be compounded into the present invention, to put it concretely, is a hydrophobic denatured polyurethane, which is specified in the following formula: R 1 ―{(O―R 2 ) k ―OCONH―R 3 [―NHCOO―(R 4 ―O)n―R 5 } h } m wherein R 1 , R 2 , and R 4 each is a hydrocarbon group, which may be same or different each other; R 3 is a hydrocarbon group, which may have urethane bond; R 5 is a straight chain, branched chain or secondary hydrocarbon group; m is an integer more than 2; h is an integer more than 1; and k and n each is an integer within the range of 0 to 1000, respectively. The hydrophobic denatured polyurethane shown in Formula (1), for example, can be obtained by reacting one or more of polyetherpolyol that is shown as R 1 ―[(O―R 2 ) k ―OH] m , one or more of polyisocyanate that is shown as R 3 ―(NCO) h+1 , and one or more of polyether monoalcohol shown as HO―(R 4 ―O) n ―R 5 . In here, R 1 to R 5 in Formula (1) each is determined by the adopted compound, i.e., R 1 ―[(O―R 2 ) k ―OH] m , R 3 ―(NCO) h+1 , and HO―(R 4 ―O) n ―R 5 . Though the ratio of these compounds is not restricted in particular, it is preferable that the ratio of a hydroxyl group originated in polyetherpolyol and polyether monoalcohol to an isocyanate group originated in polyisocyanate is NCO/OH=0.8:1-1.4:1. The polyetherpolyol compound shown as R 1 ―[(O―R 2 ) k ―OH] m , which can be used favorably in order to obtain the associative thickener shown in Formula 1, is manufactured with addition polymerization of alkylene oxide such as ethylene oxide, propylene oxide, butylene oxide, epichlorohydrin, styrene oxide, and the like with m-valent polyol. As the polyol, divalent to octavalent polyols are preferable, and the examples include: divalent alcohols such as ethylene glycol, propylene glycol, butylene glycol, hexamethylene glycol, and neopentyl glycol; trivalent alcohols such as glycerin, trioxyisobutane, 1,2,3-butanetriol, 1,2,3-pentatriol, 2-methyl-1,2,3-propanetriol, 2-metyl-2,3,4-butanetriol, 2-ethyl-1,2,3-butanetriol, 2,3,4-pentanetriol, 2,3,4-hexanetriol, 4-propyl-3,4,5-heptanetriol, 2,4-dimethyl-2,3,4-pentanetriol, pentamethylglycerine, pentaglycerine, 1,2,4-butanetriol, 1,2,4-pentanetriol, trimethylolethane, and trimethylolpropane; tetravalent alcohols such as pentaerythritol, 1,2,3,4-pentanetetrol, 2,3,4,5-hexanetetrol, 1,2,4,5-pentanetetrol and 1,3,4,5-hexanetetrol; pentavalent alcohols such as adonitol, arabitol and xylitol; hexavalent alcohols such as sorbitol, mannitol and iditol; and octavalent alcohols such as sucrose. Also, alkylene oxide or styrene oxide having 2-4 carbon atoms is preferable in order to demonstrate excellent effect and easiness for acquisition in consideration that R 2 is determined according to the alkylene oxide, styrene oxide and the like to be added. The alkylene oxide, styrene oxide and the like to be added each may be homopolymerization, or random polymerization or block polymerization more than two. The addition method may be a conventional method. Also, polymerization degree k is 0-1000, and preferably is 1-500, and more preferably is 10-200. The associative thickener, which is suitable for the present object, can be obtained in the case where the percentage of the ethylene group in R 2 is 50-100 wt% with respect to the whole amount of R 2 . Also, the molecular weight of R 1 ―[(O―R 2 ) k ―OH] m is preferably 500-100000, and more preferably is 1000-50000. The polyisocyanate shown as R 3 ―(NCO) h+1 , which can be used favorably in order to obtain the hydrophobic denatured polyether urethane shown in Formula 1, is not restricted in particular as long as the polyisocyanate has two or more isocyanate group in the molecule. Examples of the polyisocyanate include aliphatic diisocyanates, aromatic diisocyanates, alicyclic diisocyanates, biphenyl diisocyanates, diisocyanates of phenylmethane, triisocyanates, tetraisocyanates, and the like. Examples of aliphatic diisocyanates include methylene diisocyanate, dimethylene diisocyanate, trimethylene diisocyanate, tetramethylene diisocyanate, pentamethylene diisocyanate, hexamethylene diisocyanate, dipropylether diisocyanate, 2,2-dimethylpentane diisocyanate, 3-methoxyhexane diisocyanate, octamethylene diisocyanate, 2,2,4-trimethylpentane diisocyanate, nonamethylene diisocyanate, decamethylene diisocyanate, 3-butoxyhexane diisocyanate, 1,4-butyleneglycol dipropylether diisocyanate, thiodihexyl diisocyanate, metaxylylene diisocyanate, paraxylylene diisocyanate, tetramethylxylylene diisocyanate and the like. Examples of aromatic diisocyanates include metaphenylene diisocyanate, paraphenylene diisocyanate, 2,4-tolylene diisocyanate, 2,6-tolylene diisocyanate, dimethylbenzene isocyanate, ethylbenzene diisocyanate, isopropylbenzene diisocyanate, tolidine diisocyanate, 1,4-naphthalene diisocyanate, 1,5-naphthalene diisocyanate, 2,6-naphthalene diisocyanate, 2,7-naphthalene diisocyanate and the like. Examples of alicyclic diisocyanates include hydrogenated xylylene diisocyanate, isophorone diisocyanate and the like. Examples of biphenyl diisocyanates include biphenyl diisocyanate, 3,3'-dimethylbiphenyl diisocyanate, 3,3'-dimethoxybiphenyl diisocyanate and the like. Examples of diisocyanates of phenylmethane include diphenylmethane-4,4'-diisocyanate, 2,2'-dimethyldiphenylmethane-4,4'-diisocyanate, diphenyldimethylmethane-4,4'-diisocyanate, 2,5,2',5'-tetramethyldiphenyl-methane-4,4'-diisocyanate, cyclohexylbis (4-isocyonthophenyl) methane, 3,3'-dimethoxy-diphenylmethane-4,4'-diisocyanate, 4,4'-dimethoxydiphenylethane-3,3'-diisocyanate, 4,4'-diethoxydiphenylmethane-3,3'-diisocyanate, 2,2'-dimethyl-5,5'-dimethoxydiphenylmethane-4,4'-diisocyanate, 3,3'-dichlorodiphenyldimethylmethane-4,4'-diisocyanate, benzophenone-3,3'-diisocyanate and the like. Examples of triisocyanates include 1-methylbenzene-2,4,6-triisocyanate, 1,3,5-trimethylbenzene-2,4,6-triisocyanate, 1,3,7-naphthalenetriisocyanate, biphenyl-2,4,4'-triisocyanate, diphenylmethane-2,4,4'-triisocyanate, 3-methyldiphenylmethane-4,6,4'-triisocyanate, triphenylmethane-4,4',4''-triisocyanate, 1,6,11-undecane triisocyanate, 1,8-diisocyanate-4-isocyanatemethyloctane, 1,3,6-hexamethylene triisocyanate, bicycloheptane triisocyanate, tris (isocyanatephenyl) thiophosphate, and the like. The polyisocyanate of the present invention may be a dimer or trimer (isocyanurate bond) of these polyisocyanate compounds, and also may be used as a biuret by reacting with amine. Further, the polyisocyanate having urethane bond, that the polyol reacted with these polyisocyanate compounds, may be used. As the polyol, divalent to octavalent polyols, which were mentioned hereinbefore are preferable. Also, the polyisocyanate having urethane bond is preferable in the case where the polyisocyanates more than trivalent polyisocyanate is used as R 3 ―(NCO) h+1 . The polyether monoalcohol shown as HO―(R 4 ―O) n ―R 5 , which can be used favorably in order to obtain the hydrophobic modified polyether urethane shown in Formula 1, is not restricted in particular as long as the polyether monoalcohol is a straight, branched or secondary monohydric alcohol polyether. Such compounds can be obtained by addition polymerization of alkylene oxide such as ethylene oxide, propylene oxide, butylene oxide, epichlorohydrin, styrene oxide, and the like with the straight, branched or secondary monohydric alcohol. The straight chain alcohol mentioned here can be shown in the following Formula (2). R 6 ―OH Also, the branched chain alcohol mentioned here can be shown in the following Formula (3). Also, the secondary alcohol mentioned here can be shown in the following Formula (4). Accordingly, R 5 is a group excluding a hydroxyl group in the above-mentioned Formulae (2) to (4). In the above-mentioned Formulae (2) to (4), R 6 , R 7 , R 8 , R 10 , and R 11 each is a hydrocarbon group or fluorocarbon group, and examples of them include an alkyl group, an alkenyl group, an aryl group, and a cycloalkyl and cycloalkenyl group. Examples of the alkyl group include a methyl, ethyl, propyl, isopropyl, butyl, isobutyl, tertiary butyl, pentyl, isopentyl, neopentyl, tertiary pentyl, hexyl, heptyl, octyl, 2-ethylhexyl, nonyl, decyl, undecyl, dodecyl, tridecyl, isotridecyl, myristyl, palmityl, stearyl, isostearyl, icosyl, docosyl, tetracosyl, thoriacontyl, 2-octyldodecyl, 2-dodecylhexadecyl, 2-tetradecyl-octadecyl and monomethyl branched isostearyl groups. Examples of the alkenyl group include a vinyl, allyl, propenyl, isopropenyl, butenyl, pentenyl, isopentenyl, hexenyl, heptenyl, octenyl, nonenyl, decenyl, undecenyl, dodecenyl, tetradecenyl and oleyl group. Examples of the alkyl aryl group include a phenyl, toluyl, xylyl, cumenyl, mesityl, benzyl, phenethyl, styryl, cinnamyl, benzhydryl, trityl, ethylphenyl, propylphenyl, butylphenyl, pentylphenyl, hexylphenyl, heptylphenyl, octylphenyl, nonylphenyl, α-naphthyl, and β-naphthyl group. Examples of the cycloalkyl and cycloalkenyl group include a cyclopentyl, cyclohexyl, cycloheptyl, methylcyclopentyl, methylcyclohexyl, methylcycloheptyl, cyclopentenyl, cyclohexenyl, cycloheptenyl, methylcyclopentenyl, methylcyclohexenyl, and methylcycloheptenyl group. In the above-mentioned Formula (3), R 9 is a hydrocarbon group or fluorocarbon group, and examples of them include an alkylene group, an alkenylene group, an alkyl arylene group, and a cycloalkylene and cycloalkenylene group. Also, R 5 is a hydrocarbon group or fluorocarbon group, and preferably is an alkyl group. The total carbon atoms is preferably 8-36, and more preferably is 12-24. The alkylene oxide, styrene oxide and the like to be added each may be homopolymerization, or random polymerization or block polymerization more than two. The addition method may be a conventional method. Also, polymerization degree n is 0-1000, and preferably is 1-200, and more preferably, is 10-200. The associative thickener, which is suitable for the present object can be obtained in the case where the percentage of the ethylene group in R 4 is 50-100 wt% and more preferably is 65-100 wt% with respect to the whole amount of R 4 . As the manufacturing method of the compound shown in Formula (1), for example, the compound can be obtained by reacting polyether and isocyanate for 1-3 hours at 80-90°C as like a conventional reaction. Also, a by-product, which is not the compound having structure of Formula (1) may be produced in the case where polyether polyol (a) shown as R 1 ―[(O―R 2 ) k ―OH] m , polyisocyanate (b) shown as R 3 ―(NCO) h+1 , and polyether monoalcohol (c) shown as HO― (R 4 ―O) n ―R 5 reacted. For example, when diisocyanate is used, the by-products such as c-b―c and c―b―(a―b) x ―a―b―c compounds may be produced together with the main product of c―b―a―b―c compound, which is shown in Formula (1). In this case, such by-product can be used in the condition of the mixture, which includes the Formula (1) type compound without separating the Formula (1) compound in particular. Amount of Associative Thickener It is preferable to compound 0.01 to 10 wt% of said associative thickener into the cosmetic composition of the present invention. The effect of addition is not observed in the case where the amount of said associative thickener is less than 0.01 wt%. On the other hand, in the case where the amount of said associative thickener is more than 10 wt%, viscosity at heating and dissolution time becomes too much high and it is something wrong to handle at manufacturing time. Accordingly, it is not preferable because efficiency is deteriorated and stickiness is occurred. Polyhydric Lower Alcohol In the present invention, time stability of viscosity at high temperature of the associative thickener, and time stability of emulsion particular in the oil-in-water emulsion composition can be improved by compounding a polyhydric lower alcohol. The usual polyhydric lower alcohol compounded into cosmetic can be used as the polyhydric lower alcohol. Examples of the polyhydric lower alcohol include glycerin, propylene glycol, 1,3-butylene glycol, ethylene glycol, and sorbitol. An amount of said polyhydric lower alcohol is preferably 0.1-30 wt%. In the case where the amount of the polyhydric lower alcohol is less than 0.1 wt%, improvement of time stability of viscosity at high temperature may not be obtained, and time stability of emulsion may be inferior in the oil-in-water emulsion composition. On the other hand, in the case where the amount of the polyhydric lower alcohol is more than 30 wt%, it is unfavorable because thickening effect of associative thickener may be decreased and the feeling of use may be spoiled, e.g. stickiness feeling may occur. Oil-in-Water Emulsion Composition It is possible to use favorably approximately 40 wt% of an oily ingredient which is usually used for cosmetic in the case where the cosmetic composition of the present invention is used as an oil-in-water emulsion composition. Also, viscosity of the associative thickener can be increased by existence of proper amount of surfactant in the present invention. An ionic surfactant such as anionic surfactants, cationic surfactants, and amphoteric surfactants, and a nonionic surfactant, which are generally used in cosmetic can be used as the surfactant of the present invention. As an amount of the surfactant, in the system where 0.1-5 wt% of the associative thickener of the present invention and 40 wt% or less of the oily ingredient are comprised, it is preferable that the amount of the surfactant is ten times or less of cmc (critical micellar concentration), 10 wt% or less, 8 wt% or less and more preferably 4 wt% or less, and 6 wt% or less and more preferably 2 wt% or less in the case where the surfactant is the ionic surfactant, the nonionic surfactant whose HLB is 12 or less, the nonionic surfactant whose HLB is 15 or less, and the nonionic surfactant whose HLB is 15 or more, respectively. The excellent improvement effect of viscosity may not be obtained in the case where the amount is not within the range mentioned hereinbefore. Humectant Synergetic effect with the associative thickener in improvement of moisture retention function can be obtained by compounding a humectant into the cosmetic composition of the present invention. In addition to the above-mentioned polyhydric alcohols, the humectant which is generally used for cosmetic can be used as the humectant of the present invention. Pharmaceutical Synergetic effect with the associative thickener in improvement of percutaneous absorption promoting effect of pharmaceutical can be obtained by compounding a pharmaceutical into the cosmetic composition of the present invention. Examples of the pharmaceutical that can demonstrate percutaneous absorption promoting effect include α-hydroxy acid such as lactic acid. Relaxation effect against irritation such as smart can be obtained in the case where the pharmaceutical such as α-hydroxy acid, which is possible to involve irritation is compounded into the cosmetic composition of the present invention. Other Ingredients As for the other ingredients compounded into the cosmetic composition of the present invention, perfumes, ultraviolet absorbers, resins and the like, which are generally used in cosmetic arc listed. These ingredients can be compounded within the range that effect of the cosmetic composition of the present invention is not spoiled. In the following, the present invention will be explained in further detail according to Manufacturing Examples and Working Examples. The present invention, not tot mention, is not restricted to these Working Examples. Also, the amount will be shown as wt% without otherwise stated. First, Manufacturing Examples of Associative thickener A-G, which are compounded into the cosmetic composition of the present invention will be described. <Manufacturing Example A> To a container that is a four necks flask of 1000 mL that a thermometer, nitrogen introducing pipe, and a disperser are attached, were added 480 parts of polyethylene glycol (PEG) 6000 (molecular weight approximately 6000) (equal to R― 1 [(O―R 2 ) k ―OH] m ) and 198 parts of ethylene oxide (EO) 20 mols adduct of the branched alcohol shown in the following Formula (5) (equal to HO―(R 4 ―O) n ―R 5 ). The mixture was dehydrated for 3 hours at 90-100°C under reduced pressure and moisture content of the system was 0.03 wt%. Then, it was cooled down to 80°C. 29.6 parts of hexamethylene diisocyanate (HMDI) (equal to R 3 ―(NCO) h+1 ) was added thereto and it was reacted for 2 hours at 80-90°C under nitrogen gas atmosphere. After confirming that isocyanate is 0% and a resultant, which is light-yellow solid in normal temperature was obtained. This solid is defined as Associative thickener A. <Manufacturing Example B> A light-yellow solid resultant was obtained from 522 parts of PEG 6000, 145 parts of EO 10 mols adduct of the branched alcohol shown in the following Formula (6), and 132.2 parts of HMDI under the condition of Manufacturing Example A. This solid is defined as Associative thickener B. <Manufacturing Example C> A light-yellow solid resultant was obtained from 580 parts of PEG 20000, 109 parts of EO 35 mols adduct of the branched alcohol shown in the following Formula (7), and 11.1 parts of tolylene diisocyanate (TDI) under the condition of Manufacturing Example A. This solid is defined as Associative thickener C. <Manufacturing Example D> A light-yellow solid resultant was obtained from 360 parts of PEG 6000, 303 parts of a compound that 50 mols of EO was added to a secondary alcohol of C 11 -C 14 , and 122.2 parts of HMDI under the condition of Manufacturing Example A. This solid is defined as Associative thickener D. <Manufacturing Example E> A light-yellow solid resultant was obtained from 120 parts of PEG 2000, a compound that 100 mols of EO was added to a secondary alcohol of C 11 -C 14 , and 18.5 parts of tetramethylene diisocyanate under the condition of Manufacturing Example A. This solid is defined as Associative thickener E. <Manufacturing Example F> A light-yellow solid resultant was obtained from 550 parts of PEG 10000, 133 parts of EO 50 mols adduct of the branched alcohol shown in the following Formula (8), and 120.4 parts of HMDI under the condition of Manufacturing Example A. This solid is defined as Associative thickener F. <Manufacturing Example G> A light-yellow solid resultant was obtained from 367 parts of trimethylolpropane 100 EO adduct, 286 parts of EO 20 mols adduct of the branched alcohol shown in the following Formula (9), and 40.8 parts of HMDI under the condition of Manufacturing Example A. This solid is defined as Associative thickener G. <Manufacturing Example H> A light-yellow solid resultant was obtained from 288.2 parts of polyethylene glycol PEG-20000(molecular weight 20000), 7.0 parts of i-C16 alcohol shown in the following Formula (10), and 4.8 parts of hexamethylene diisocyanate HMDI under the condition of Manufacturing Example A. This solid is defined as Associative thickener H. Constitutions of Associative thickener of Manufacturing Examples A-G is shown in Fig. 2. The present inventors have conducted the following tests in order to study a fundamental property of these associative thickeners. Associative thickener A of the present invention, and carboxyvinyl polymer and xanthane gum were used, as the conventional water-soluble and cosmetically widely used polymer thickener. Influence of Salt Concentration on Viscosity The present inventors have examined how the viscosity (mPa · s, Brookfield viscometer, 25°C) of the composition is changed. The composition is prepared by adding 0-2 wt% of NaCl to each solution of 1 wt% of Associative thickener A, 0.1 wt% of carboxyvinyl polymer, and 1 wt% of xanthane gum. The result is shown in Table 1. NaCl amount/wt% 0 0.1 0.5 1 2 Associative thickener A 3100 3240 3120 2960 2800 Carboxyvinyl polymer 3200 20 10 10 10 Xanthane gum 3400 12000 15250 17250 17000 It is understood from the result shown in Table 1 that the viscosity of Associative thickener solution does not depend on the amount of sodium chloride. To the contrary, it is understood that the viscosity of carboxyvinyl polymer is remarkably decreased while the viscosity of xanthane gum is remarkably increased due to addition of sodium chloride. In next, the present inventors have examined the influence for viscosity affected by pH in the similar manner to the influence of salt. Influence for Viscosity Affected by pH Each solution of 1 wt% of Associative thickener A, 0.1 wt% of carboxyvinyl polymer, and 1 wt% of xanthane gum was adjusted to pH 4-8. Viscosity (mPa·s, Brookfield viscometer, 25°C) of each solution was measured. The result is shown in Table 2. PH 4 5 6 7 8 Associative thickener A 2800 2810 3050 3100 3070 Carboxyvinyl polymer 100 2020 6250 8100 9900 Xanthane gum 3920 1980 3260 3800 4200 It is understood from the result shown in Table 2 that the viscosity of associative thickener solution is never affected by pH. To the contrary, it is understood that viscosity of carboxyvinyl polymer is decreased under low pH and viscosity of xanthane gum demonstrates complicated behavior. In next, the present inventors have examined time stability of viscosity of said thickener. Time Stability of Viscosity Each solution of 1 wt% of Associative thickener A, 0.1 wt% of carboxyvinyl polymer, and 1 wt% of xanthane gum is preserved at 50°C for 0 to 8 weeks. Change of viscosity (mPa·s, Brookfield viscometer, 25°C) with time was measured. The result is shown in Table 3. Preserved term/Week(50°C) 0 2 4 8 Associative thickener A 3200 1800 1010 840 Carboxyvinyl polymer 8150 8100 8100 7700 Xanthane gum 3800 3760 3600 3560 It is understood from the result shown in Table 3 that the viscosity of associative thickener tends to decrease with passage of time in the case where the composition is preserved at high temperature. To the contrary, it is understood that carboxyvinyl polymer and xanthane gum each is excellent in time stability of viscosity. On the whole, it is understood from the result shown in Tables 1-3 that associative thickener in accordance with the cosmetic composition of the present invention has effects in stability of viscosity against external factor such as salt and pH, while it is inferior in time stability of viscosity at high temperature. To the contrary, it is understood that the viscosity of the conventional water-soluble polymer thickener such as carboxyvinyl polymer and xanthane gum is relatively excellent in time stability of viscosity while it is unstable due to external factor such as salt and pH. In next, the present inventors have studied about the ingredient that can stabilize emulsification and can improve time stability of viscosity in addition to the water-soluble polymer. Combination of Associative Thickener and Polyhydric Lower Alcohol The present inventors have studied a combination of associative thickener and a polyhydric lower alcohol in addition to the water-soluble polymer. To the oil-in-water emulsion composition of Test Example 1 was added 0-40 wt% of the following each polyhydric lower alcohol and time stability of viscosity and emulsion at 50°C were examined. The preserved term was set at 0-8 weeks. The results in case of adding dipropylene glycol, glycerin, and 1,3-butylene glycol are shown in Tables 11, 12 and 13, respectively. Chang of Viscosity (mPa·s) in Case of Adding Dipropylene Glycol Preserved Term (weeks) Amount (wt%) 0 2 4 8 0 3200 1800 1010 Separation to two phases 0.05 3200 2060 1200 Separation to two phases 0.1 3160 2900 2630 2450 1 3150 3150 2980 2700 5 3100 3010 3050 2560 10 2900 2920 3000 2900 20 2560 2600 2560 2550 30 1880 1800 1820 1790 40 780 690 700 690 Chang of Viscosity (mPa·s) in Case of Adding Glycerin Preserved Term (weeks) Amount (wt%) 0 2 4 8 0 3200 1800 1010 Separation to two phases 0.05 3220 1670 900 Separation to two phases 0.1 3100 2570 2320 2100 1 3160 2600 2480 2220 5 3300 2560 2220 2060 10 3260 3200 3300 3220 20 3010 3000 3020 3010 30 2770 2690 2700 2600 40 1140 1100 780 700 Chang of Viscosity (mPa·s) in Case of Adding 1,3-Butylene glycol Preserved Term (weeks) Amount (wt%) 0 2 4 8 0 3200 1800 1010 Separation to two phases 0.05 3240 2730 2010 Separation to two phases 0.1 3190 3030 2830 2640 1 3220 3200 3010 2880 5 3210 3210 3200 3170 10 3180 3200 3200 3190 20 2980 2960 2960 2950 30 1900 1900 1890 1900 40 560 580 500 410 As shown in Tables 11-13, when the amount of the polyhydric lower alcohol is less than 0.1 wt%, every composition becomes unfavorable because thickening effect of associative thickener weaken and stickiness is occurred in the feeling of use. Judging from the result shown hereinbefore, in the case where associative thickener is compounded as the cosmetic composition, it is preferred to combine with any of the water-soluble polymer, and the polyhydric lower alcohol in view of time stability of viscosity. Also, if the cosmetic composition is the oil-in-water emulsion composition, it is preferred to combine the same in view of time stability of emulsion. In next, the present inventors have compared the concrete cosmetic composition in accordance with the present invention with the cosmetic composition of the prior art. The result is shown in Table 15. In Comparative Example 1, carboxyvinyl polymer, which conventionally used in the cosmetic was used instead of associative thickener. Lotion Working Example Comparative Example 1 1 Stearic acid 2.0 2.0 Cetyl alcohol 1.5 1.5 Petrolatum 4.0 4.0 Squalane 5.0 5.0 Triglyceryl-2-ethylhexanoate 2.0 2.0 Sorbitan monooleate 2.0 2.0 PEG 1500 3.0 3.0 Triethanolamine 1.0 1.0 Phenoxy ethanol 0.2 0.2 Perfume 0.1 0.1 Hydroxyethylcellulose 0.3 0.3 Compound of Mfg. Ex. A (Viscosity ratio =0.11) 1.0 - Carboxyvinyl polymer - 0.1 Purified water Balance Balance Test 1 : Organoleptic test o ○ Δ Test 2 : Salt resistance of viscosity o ○ × Test 3 : Temperature stability of viscosity ○ Δ Test 4 : Stability of emulsion ○ ○ - Manufacturing Method - Humectant and alkali were added to a part of purified water and the mixture was heated up and adjusted to 70°C. After dissolving the oily ingredient, surfactant, antiseptic and perfume were added thereto and the mixture was heated up and adjusted to 70°C. Thickener was dissolved into the rest of purified water. The oil phase was added to the water phase, which was prepared in advance. The mixture was preliminary emulsified and a solution of thickener was added thereto. After uniforming the emulsion particle by a homomixer, it was deaerated, filtered and cooled. Also, Test Examples mentioned hereinbefore are based on this Manufacturing Method. It is understood from the result of Table 15 that the cosmetic composition, which includes associative thickener of the present invention is excellent in not only stability of viscosity (salt resistance and temperature stability on wide range), but also usability (moisture and less stickiness). On the other hand, it is found that the cosmetic composition of Comparative Example 1, which includes the conventional thickener, is inferior to the present invention in most tests. Amount of Associative Thickener In next, the present inventors have studied about the amount of associative thickener in the cosmetic composition in accordance with the present invention according to the following composition. The result is shown in Table 16. Cleansing Foam Test Ex. 19 Test Ex. 20 Test Ex. 21 Test Ex. 22 Test Ex. 23 Test Ex. 24 Stearic acid 15 15 15 15 15 15 Palmitic acid 20 20 20 20 20 20 Coconut oil 2 2 2 2 2 2 Potassium hydroxide 6 6 6 6 6 6 Glycerin 15 15 15 15 15 15 Polyethylene glycol 1500 10 10 10 10 10 10 Glyceryl monostearate 2 2 2 6 6 6 POE (20) sorbitan Monostearate 2 2 2 2 2 2 Associative thickener B 0.001 0.01 0.1 5 10 15 Carboxyvinyl polymer 0.05 0.05 0.05 0.05 0.05 0.05 Phenoxy ethanol 0.2 0.2 0.2 0.2 0.2 0.2 Chealating agent q.s. q.s. q.s. q.s. q.s. q.s. Purified Water Balance Balance Balance Balance Balance Balance (Viscosity mPa·s) Associative thickener B 20 40 120 58000 167000 560000 Carboxyvinyl polymer 3000 3000 3000 3000 3000 3000 Viscosity ratio ( ) 150 75 25 0.052 0.018 0.005 Test 1 : Organoleptic Test Δ ○ o ○ o ○ ○ Δ - Manufacturing Method - Fatty acid, emollient, humectant and antiseptic were heated and dissolved and the mixture was maintained at 70°C. Purified water dissolved alkali in advance was added to the oil phase which was stirred. After addition, the temperature of the mixture was kept at 70°C for a period time and neutralizing reaction was terminated. Then, surfactant, chelating agent and thickener dissolved in advance was added thereto and stirred and mixed. After deaeration and filtration, the mixture was cooled. It is understood from the result of Table 16 that the amount of associative thickener included in the cosmetic composition of the present invention is preferably 0.01-10 wt% and more preferably is 0.1-5 wt%. If the amount of associative thickener is more than 10 wt%, usability is spoiled because stickiness is occurred. On the other hand, not only the effect as the thickener is spoiled but also moisture feeling is inferior in usability even no stickiness, in the case where the amount of associative thickener is less than 0.01 wt%. Working Examples will be shown in the following. Needless to say, however, the present invention is not restricted to these Working Examples. The amount is shown by wt%. Working Example 2 Skin Lotion Humectant : Sorbitol 4.0 Dipropylene glycol 6.0 PEG 1500 5.0 Surfactant : POE (20) Oleylalcoholether 0.5 Watar-souluble polymer : Carboxyvinyl polymer (Pemulen TR-2, manufactured by Goodrich Corp.) 0.05 Associative thickener : Compound of Manufacturing Example C 0.1 Alcohol : Ethanol 10.0 Antiseptic : Methyl paraben 0.2 Perfume q.s. Chelating agent q.s. Buffering agent q.s. Purified water Balance * Viscosity ratio = Carboxyvinyl polymer (780 mPa·s)/Associative thickener C (150 mPa·s) - Manufacturing Method - Chelating agent was dissolved into a part of purified water. A viscous solution was prepared by mixed and stirred thereto. Humectant and buffering agent were added to the rest of purified water and dissolved under room temperature. The viscous solution prepared in advance was added thereto, and a uniform solution was obtained. An alcohol solution was obtained by adding antiseptic, surfactant, and perfume to ethanol and it was solubilized by adding to and mixing with the above-mentioned uniform solution. Working Example 3 Emollient Lotion Oily ingredient : Cetyl alcohol 1 Beeswax 0.5 Petrolatum 2 Squalane 6 Dimethylpolysiloxane 2 Alcohol : Ethanol 5 Humectant : Glycerin 4 1,3-Butylene glycol 4 Surfactant : POE (10) monooleate 1 Glyceryl monostearate 1 Associative thickener : Compound of Manufacturing Example D 2 Water-soluble polymer : Agar (viscosity ratio =0.011) 0.1 Antiseptic : Methyl paraben 0.2 Purified water Balance - Manufacturing Method - Humectant was added to purified water and the mixture was heated up to 70°C. Surfactant and antiseptic were added to the oily ingredients and the mixture was heated up to 70°C. Preliminary emulsification was effected by adding the latter to the former. Thickener and ethanol were added thereto and stirred. After uniforming the emulsion particle by a homomixer, it was deaerated, filtered and cooled. Working Example 4 Emollient Cream Oily ingredient : Cetyl alcohol 5 Stearic acid 3 Petrolatum 5 Squalane 10 Dimethylpolysiloxane 2 Triglyceryl-2-ethylhexanoate 7 Humectant : Dipropylene glycol 5 Glycerin 5 Surfactant : Propyleneglycol monostearate 3 POE (20) cetylalcoholether 3 Alkali : Triethanolamine 1 Associative thickener : Compound of Manufacturing Example E 3 Water-soluble polymer : Hydroxyethylcellulose (Natrosol plus 330, manufactured by Hercules Inc.) (viscosity ratio =0.138) 1 Antiseptic : Phenoxy ethanol 0.2 Antioxidant : Ionol 0.1 Perfume q.s. Purified water Balance - Manufacturing Method - Humectant, alkali, and thickener were added to purified water and the mixture was heated up to 70°C. After heating and dissolving the oily ingredients, surfactant, antiseptic, antioxidant, and perfume were added thereto and the mixture was heated up to 70°C. Preliminary emulsification was effected by adding the latter to the former. After uniforming the emulsion particle by a homomixer, it was deaerated, filtered and cooled. Working Example 5 Moisture Gel Humectant : Dipropylene glycol 7 PEG 1500 8 Associative thickener : Compound of Manufacturing Example F 1 Water-soluble polymer : Cationized Cellulose (Catinal PC-100, manufactured by Toho Chemical Industry Co.,Ltd.) 0.4 Methylcellulose (viscosity ratio =15) 0.2 Alkali : Potassium hydroxide 0.1 Antiseptic : Methyl paraben q.s. Chelating agent q.s. Perfume q.s. Purified water Balance - Manufacturing Method - After dissolving associative thickener and water-soluble polymer into purified water in uniform, PEG 1500 and chelating agent were added thereto. Surfactant was added to dipropylene glycol and the mixture was heated and dissolved at 50°C. Then, antiseptic and perfume were added thereto. The former prepared in advance was slowly added to the latter with stirring. Alkali solution was added thereto and the mixture was sufficiently stirred for neutralization. Working Example 6 Essence : Sorbitol 8.0 Humectant 1,3-Butylene glycol 5.0 PEG 1500 7.0 Hyaluronic acid 0.1 Alcohol : Ethanol 7.0 Surfactant : POE oleyl alcohol ether 1.0 Associative thickener : Compound of Manufacturing Example G (viscosity ratio =2.26) 0.5 Antiseptic : Phenoxyethanol 0.2 Perfume q.s. Buffering agent q.s. Purified water Balance - Manufacturing Method - Humectant, buffering agent, and thickener were added to purified water and the mixture was dissolved under room temperature. After dissolving surfactant, emollient, perfume, and antiseptic into ethanol, it was solubilized to the former water phase. Working Example 7 Pack Film-forming agent : Polyvinyl alcohol 15 Associative thickener : Compound of Manufacturing Example A (viscosity ratio =2.92) 5 Humectant : 1,3-Butylene glycol 5 Surfactant : POE oleyl alcohol ether 0.5 Alcohol : Ethanol 12 Antiseptic : Methyl paraben 0.2 Perfume q.s. Buffering agent q.s. Purified water Balance - Manufacturing Method - Buffering agent and humectant were added to purified water and the mixture was heated up to 70°C. Thickener and film-forming agent were added thereto and the mixture was dissolved while stirring. Perfume, antiseptic, and surfactant were added to ethanol. After dissolution, the latter was solubilized to the former water phase. Working Example 8 Liquid Foundation Powder :Talc 3 Titanium dioxide 5 Red iron oxide 0.5 Yellow iron oxide 1.4 Black iron oxide 0.1 Water Phase : Bentonite 0.5 POE sorbitan monostearate 0.9 Triethanolamine 1 Propyleneglycol 10 Associative thickener B 0.5 Carageenan (viscosity ratio =0.539) 0.1 Purified water Balance Oil Phase : Stearic acid 2.2 Isohexadecyl alcohol 7 Glyceryl monostearate 2 Liquid lanolin 2 Liquid paraffin 8 Antiseptic q.s. Perfume q.s. - Manufacturing Method - The oil phase and the water phase each was heated up to 70°C and dissolved separately. The oil phase and the powder were added to the water phase. After emulsifying the mixture by a homomixer, antiseptic and perfume were added thereto. The mixture was cooled while stirring. Working Example 9 Nail Enamel Resin : Polymer emulsion ( ) 85.0 Plasiticizer : Diisobutyl adipate 4.0 Film-forming assistant : Carbitol 4.0 Antiseptic : Methyl paraben 0.2 Defoaming agent q.s. Pigment : Red No. 220 0.3 Titanium oxide 0.2 Associative thickener : Compound of Manufacturing Example C 0.2 Ion-exchanged water 6.1 - Manufacturing Method - The associative thickener was added to ion-exchanged water and the mixture was heated and dissolved. The mixture was added to polymer emulsion. Diisobutyl adipate and carbitol were slowly added thereto and the other ingredients were also added to the mixture. After dispersing the mixture in uniform, it was deaerated. Working Example 10 Shampoo Surfactant : Sodium lauryl POE sulfate ester 9 Amide propylbetaine myristate 3 Coconut fatty acid diethanolamide 4 Humectant : Glycerin 1 Water-soluble polymer : Cationized Cellulose (Quatrisoft LM-200, manufactured by Amercol Corp.) 0.2 Associative thickener : Compound of Manufacturing Example D (viscosity ratio =0.214) 2 Perfume q.s. Coloring agent q.s. Antiseptic q.s. Sequestering agent/pH adjustor q.s. Purified water Balance - Manufacturing Method - Purified water was heated up to 70°C. The other ingredients were added thereto and dissolved in uniform. Then the mixture was cooled. Working Example 11 Rinse Oily ingredient : Silicone oil 3 Liquid paraffin 1 Cetyl alcohol 1.5 Stearyl alcohol 1 Stearyltrimethyl ammonium chloride 0.7 Humectant : Glycerin 3 Associative thickener : Compound of Manufacturing Example E 0.5 Water-soluble polymer : Poly (diallyldimethylammonium chloride) (Marqart 100, manufactured by Calgon Corp.) (viscosity ratio =0.82) 0.5 Perfume, Coloring agent, Antiseptic q.s. Purified water Balance - Manufacturing Method - The associative thickener, water-soluble polymer, stearyltrimethyl ammonium chloride, glycerin, and coloring agent were added to purified water and the mixture was kept at 70°C (Water phase). The other ingredients were mixed and the mixture was heated, dissolved and kept at 70°C (Oil Phase). Oil phase was added to water phase and the mixture was emulsified by a homomixer. Then, it was cooled while stirring. Working Example 12 Hair Gel Water-soluble polymer : Acrylic resin alkanolamine solution 2 Associative thickener : Compound of Manufacturing Example F (viscosity ratio =0.019) 2 Humectant : Glycerin 5 Alcohol : Ethanol 20 Surfactant : POE octyl dodecyl ether 1 Perfume, Chelating agent q.s. Purified water Balance - Manufacturing Method - A part of purified water was added to associative thickener and glycerin and the mixture was heated and dissolved at 70°C. The other ingredients were added to the rest of purified water and the mixture was dissolved while stirring. Working Example 13 Sun Screen Oil Phase : Octyl p-methoxycinnamate 3 Isopropyl myristate 2 Oleyl oleate 4 Petrolatum 1 Stearyl alcohol 2 Stearic acid 2 Glyceryl monostearate 2 Vitamin E acetate 0.05 Antiseptic, Perfume q.s. Water Phase : 1,3-Butylene glycol 5 Associative thickener H 1 Polyacrylamide (viscosity ratio =0.276) 0.4 Purified water Balance - Manufacturing Method - The oil phase and the water phase each was heated up to 70°C and dissolved separately. The oil phase was added to the water phase. After emulsifying the mixture by a homogenizer, it was cooled down by a heat exchanger. In next, the sample prepared by Working Examples 1-13 was tested according to Tests 1-3 mentioned hereinbefore. The result is shown in Table 29. Test 4 was also tested in the oil-in-water emulsion composition. Carboxyvinyl polymer, which was relatively excellent as the thickener for the conventional cosmetic was used for preparing the composition of Comparative Examples 1-13 instead of associative thickeners of Working Examples 1-13. The methods for manufacturing the sample of Comparative Examples are based on each Working Examples. No. Working Examples Comparative Examples Test 1 Test 2 Test 3 Test 4 Test 1 Test 2 Test 3 Test 4 1 o ○ o ○ ○ ○ Δ × × ○ 2 ○ o ○ o ○ - Δ Δ Δ - 3 ○ o ○ ○ ○ × × × ○ 4 o ○ o ○ o ○ ○ Δ × × ○ 5 o ○ o ○ ○ - Δ × Δ - 6 o ○ o ○ o ○ - × × Δ - 7 ○ o ○ o ○ - × × × - 8 o ○ o ○ o ○ ○ Δ Δ × ○ 9 o ○ o ○ o ○ - × × × - 10 o ○ o ○ ○ - Δ × × - 11 o ○ o ○ ○ ○ × × × ○ 12 ○ o ○ o ○ - Δ × Δ - 13 ○ o ○ o ○ ○ Δ × × ○ Test 1 : Organoleptic Test (moisture feeling, less stickiness) Test 2 : Test for Salt Resistance of Viscosity Test 3 : Test for Temperature Stability of Viscosity Test 4 : Test for Time Stability of Emulsion It is found from the result of Table 29 that the cosmetic preparation using associative thickener of the present invention exhibits excellence in every respect such as usability and stability of viscosity as compared with the cosmetic composition of the prior art using carboxyvinyl polymer. Time stability of emulsion is favorable in every Working Examples in the oil-in-water emulsion composition of the present invention. In addition to this, the present inventors have found the knowledge as mentioned hereinafter. Viscosity Improving Effect by Surfactant The present inventors have studied the relation between associative thickener of the present invention and surfactant in the system where no oily ingredients are existed. The present inventors have studied the combination (viscosity under coexistence with 1 wt% of associative thickener) of associative thickener (Compound of Manufacturing Example E) and surfactant. First, the relation of sodium lauryl sulfate, which is an anionic surfactant and associative thickener, was studied. The result is shown in Table 30. Anionic surfactant (Sodium lauryl sulfate) Concentration of surfactant (mmol/L) 0 1 5 10 50 100 Concentration of surfactant (wt%) 0 0.03 0.14 0.29 1.44 2.88 Viscosity (mPa·s) 3000 3900 19200 <50 <50 <50 It is understood from Table 30 that the concentration of the anionic surfactant is preferable within the range that is less than about five times of cmc (critical micellar concentration) with respect to 1 wt% of associative thickener in the system where no oily ingredient exist because cmc (critical micellar concentration) of sodium lauryl sulfate is about 8 mmol/L. However, an upper limit of the concentration of surfactant is proportional to the concentration of associative thickener. Namely the range within less than ten times of cmc is preferable with respect to 2 wt% of associative thickener. The same thing applies to the cationic and amphoteric surfactants. This phenomenon can be found from Fig. 3 mentioned hereinafter. In next, the relation of lauryl trimethyl ammonium chloride, which is a cationic surfactant and associative thickener, is shown in Table 31. Cationic surfactant (Lauryl trimethyl ammonium chloride) Concentration of surfactant (mmol/L) 0 1 5 10 50 100 Concentration of surfactant (wt%) 0 0.03 0.13 0.26 1.32 2.64 Viscosity (mPa·s) 3000 5850 7700 14200 <50 <50 It is understood from Table 31 that the concentration of the cationic surfactant is preferable within the range that is less than about five times of cmc (critical micellar concentration) with respect to 1 wt% of associative thickener in the system where no oily ingredient exist because cmc (critical micellar concentration) of lauryl trimehtyl ammonium chloride is about 14 mmol/L. In next, the relation of polyoxyethylene (7) laurylether, which is a nonionic surfactant whose HLB is 10.9 and associative thickener, is shown in Table 32. Nonionic surfactant HLB 10.9 (POE (7) laurylether) Concentration of surfactant (mmol/L) 0 0.01 0.1 1 5 10 50 100 Concentration of surfactant (wt%) 0 0.0005 0.005 0.05 0.24 0.49 2.39 4.78 Viscosity (mPa·s) 3000 3950 2750 4700 18000 34800 3050 1450 It is understood from Table 32 that the concentration of the nonionic surfactant whose HLB is 12 or less is preferable within the range that is 5 wt% or less with respect to 1 wt% of associative thickener in the system where no oily ingredient exist. In next, the relation of polyoxyethylene (15) laurylether, which is a nonionic surfactant whose HLB is 14.1 and associative thickener, is shown in Table 33. Nonionic surfactant HLB 14.1 (POE (15) laurylether) Concentration of surfactant (mmol/L) 0 0.01 0.1 1 5 10 50 100 Concentration of surfactant (wt%) 0 0.00083 0.0083 0.083 0.415 0.83 4.15 8.3 Viscosity (mPa·s) 3000 2960 3300 6800 42400 32000 <50 <50 It is understood from Table 33 that the concentration of the nonionic surfactant whose HLB is 15 or less is preferable as a cosmetic composition within the range that is 2 wt% or less with respect to 1 wt% of associative thickener in the system where no oily ingredient exist. Also, in the case where HLB of the nonionic surfactant is more than 15, the preferable concentration of the nonionic surfactant is 1 wt% or less. Also, it is found that the preferable range of the concentration of the surfactant in the case where 40 wt% or less of the oily ingredients is included in the cosmetic composition as follows. If the nonionic surfactant whose HLB is 12 or less, the nonionic surfactant whose HLB is 15 or less, the nonionic surfactant whose HLB is 15 and the ionic surfactant, the concentration of the surfactant is preferable within the range of 10 wt% or less, 8 wt% or less, 6 wt% of less and ten times or less of cmc (critical micellar concentration) with respect to 0.1 to 5 wt% of associative thickener, respectively. Namely, a large amount of the surfactant within the rate that the surfactant is spent for emulsification can be compounded into the cosmetic composition in the case where the oily ingredient is compounded. Accordingly, it is understood that associative thickener of the present invention produces remarkable thickening effect by existence of the proper amount of surfactants. Fig. 3 is an explanatory drawing of this thickening mechanism. Namely, cross-linking points are increased with forming a mixing micelle of surfactant and associative thickener by addition of the proper amount of surfactant. Accordingly viscosity of associative thickener in accordance with the present invention is further increased. However, viscosity will be decreased in the case where the surfactant is compounded over the proper amount because a hydrophobic group is saturated and cross-linking points are decreased. As a result of diligent studies based on the above-mentioned thickening mechanism, the present inventors have found the following knowledge. Remarkable thickening function can be observed in the case where a micelle of the surfactant is 2 or less with respect to one molecule of associative thickener in the system where associative thickener coexists with the surfactant. Namely, the present inventors have found it is effective as the cosmetic composition in the case where the ratio of molar concentration C p of associative thickener and molar concentration C m of surfactant micelle is 1 : 2 or less despite of the type of surfactants. In here, C m will be shown as follows. C m =(C s -cac)/N' agg C m : Molar concentration of micelle C s : Molar concentration of surfactant monomer cac : Critical concentration that surfactant forms micelle under coexistence of Associative thickener N' agg : Association number of micelle of surfactant under coexistence of association thickener Next, the present inventors have studied about the effect of using associative thickener together with humectants. Improvement of Moisturizing Function Improvement of moisturizing retention function of skin was evaluated with measurement of conductance. Associative thickener C was and was not added to a skin lotion (formulation in Table 34), which contained glycerin and dipropylene glycol as a humectant. Conductance of skin in both cases was compared. Namely, conductance of skin in the chest before processing with sample and after 1 hour and 24 hours of processing sample was measured. Improvement of moisturizing retention function was judged from this changing rate. It is possible to study the effect for water absorption properties of horny layer and water retention function with changing rate of conductance of skin. If the changing rate is high, it is not preferable in view of reduction of water in horny layer. Changing rate of conductance = conductance after processing/conductance before processing The result is shown in Table 34. Component Comp. Ex. 14 Comp. Ex. 15 Work. Ex. 14 Glycerin 5 - 5 Dipropylene glycol 5 - 5 POE (20) oleyl alcohol ether 0.5 0.5 0.5 Associative thickener C - 1 1 Ethanol 5 5 5 Methyl paraben 0.2 0.2 0.2 Perfume q.s. q.s. q.s. Purified water Balance Balance Balance Change rate of conductance 0.54±0.05 0.31±0.03 0.86±0.06 As a result of Table 34, Working Example 14 which contains associative thickener and humectant remarkably inhibits the change of conductance of skin and can improve water retention function as compared with Comparative Examples 14 and 15, which does not contain associative thickener and humectant, respectively. In next, the present inventors have studied about the effect of using associative thickener together with pharmaceuticals as the application of the composition in accordance with the present invention. Percutaneous Absorption Promoting Effect α-Hydroxy acid such as lactic acid have the effect for separating old horny layer and making skin smooth and soft. Associative thickener A mentioned hereinbefore was and was not added to a cream (formulation in Table 35), which contained 5 wt% of lactic acid. Skin transparency in both cases was compared. These tests were effected with using in vitro standard Frantz type percutaneous diffusion cell and resected skin of swine (described in the following document: T.J.Franz, J.Invest.Dermatol.,64:190-195(1975)). Component Comp. Ex. 16 Work. Ex. 15 Cetyl alcohol 2.5 2.5 Stearic acid 1.5 1.5 Petrolatum 2 2 Squalane 5 5 Dipropylene glycol 5 5 Glycerin 5 5 POE (20) cetyl alcohol ether 3 3 Triethanolamine 0.5 0.5 Associative thickener A - 2 Phenoxy ethanol 0.2 0.2 Lactic acid 5 5 Perfume q.s. q.s. Purified water Balance Balance As is clear from Fig. 4, it is understood that the cream of Working Example 15, which includes Associative thickener A can improve skin transparency with lactic acid as compared with the one of Comparative Example 16, which does not include associative thickener. Irritation Relaxation Effect α-Hydroxy acid is known to have the effect for separating old horny layer and making skin smooth and soft as mentioned hereinbefore. However, if a preparation which contains α-hydroxy acid is applied to the skin, it smarts in a part and sometimes causes irritations such as reddish of skin. A cream, which includes 1 to 10 wt% of lactic acid was prepared in the similar manner to Working Examples mentioned hereinbefore and the influence on skin irritation was examined with patch test on the case with or without the above-mentioned Associative thickener B. 0.3 mL of the preparation was pasted on the back of panelist. After 24 hours, the patch was removed and professional estimator marked irritation. As is clear from Fig. 5, it is found that the preparation which includes Associative thickener B decrease skin irritation caused by lactic acid as compared with the preparation which does not include associative thickener. As explained hereinbefore, the cosmetic composition of the present invention is excellent in stability of viscosity and usability by compounding a specific associative thickener into the cosmetic composition. Also, the cosmetic composition of the present invention can improve time stability of viscosity at high temperature by using the associative thickener together with a water-soluble polymer, a polyhydric lower alcohol and a monohydric lower alcohol. Further, time stability of emulsion can be improved by using associative thickener together with the water-soluble polymer, the polyhydric lower alcohol and the monohydric lower alcohol in the case where the cosmetic composition of the present invention is an oil-in-water emulsion composition.

Claims: A cosmetic composition comprising a compound shown in Formula (1), R 1 -{(O-R 2 ) k -OCONH-R 3 [-NHCOO-(R 4 -O) n -R 5 ] h } m wherein R 1 , R 2 , and R 4 each is a hydrocarbon group, which may be the same or different to each other; R 3 is a hydrocarbon group, which may have urethane bond; R 5 is a straight chain, branched chain or secondary hydrocarbon group; m is an integer of 2 or more; h is an integer of 1 or more; and k and n each is an integer within the range of 0 to 1000, respectively, wherein said composition further comprises a polyhydric lower alcohol. The cosmetic composition according to claim 1, wherein said composition comprises 0.01 to 10 wt% of the compound shown in Formula (1) and 0.1 to 30 wt% of the polyhydric lower alcohol. The cosmetic composition according to any one of claims 1 and 2, wherein said cosmetic composition is an oil-in-water emulsion composition. The cosmetic composition according to claim 3, wherein said composition comprises 0.1 to 5 wt% of the compound shown in Formula (1), 40 wt% or less of an oily ingredient, and ten times or less of cmc (critical micellar concentration) of an ionic surfactant. The cosmetic composition according to claim 3, wherein said composition comprises 0.1 to 5 wt% of the compound shown in Formula (1), 40 wt% or less of the oily ingredient, and 10 wt% or less of a non-ionic surfactant whose HLB is 12 or less. The cosmetic composition according to claim 3, wherein said composition comprises 0.1 to 5 wt% of the compound shown in Formula (1), 40 wt% or less of the oily ingredient, and 8 wt% or less of the non-ionic surfactant whose HLB is 15 or less. The cosmetic composition according to claim 3, wherein said composition comprises 0.1 to 5 wt% of the compound shown in Formula (1), 40 wt% or less of the oily ingredient, and 6 wt% or less of the nonionic surfactant whose HLB is 15 or more.

Inventors: KANEDA ISAMU, YANAKI TOSHIO, YOSHIDA KATSUNORI, KANEDA, ISAMU, YANAKI, TOSHIO, YOSHIDA, KATSUNORI, Kaneda, Isamu, c/o Shiseido Research Center (1), Yanaki, Toshio, c/o Shiseido Research Center (1), Yoshida, Katsunori, Shiseido Research Center (1)
Applicants: SHISEIDO CO LTD, SHISEIDO COMPANY LIMITED
Application year: 1999
Main classification: A61K7
IPC codes: C09K3, A61Q1, A61K8, A61Q3, C08K5, C08G18, C08G59, A61Q19, C08L75, A61Q5, C08G65, C08L71