Fiber glass mat for laminating to foam, foam laminate precursor, foam laminate, and methods of making the mat and the foam laminate

Abstract: A fiber glass mat especially useful for bonding to foam contains glass fibers and a "B" staged acrylic resin having a glass transition temperature above 45 degrees C., the method of making the mat, a precursor for a foam laminate, a method for making a foam laminate, and the product produced by the latter method are disclosed. The mat conforms well to any curvature on the foam layer and stiffens the foam layer resulting in a superior foam laminate for making automotive parts like headliners.

Description: The present invention involves mats having particular use in bonding to foam to stiffen the foam to use in making automotive parts such as headliners or topliners, foam laminate precursors, foam laminates and methods of making mat and foam laminates. The mats produced according to this invention are useful as reinforcement and dimensional stabilizers for making a large number of polymeric foam lamiate products. BACKGROUND It is known to use nonwoven fiber, such as glass fiber, mats bonded with a thermosetting resin, like urea formaldehyde, to laminate to polymeric foam such as polystyrene foam to act as stiffeners and stabilizers in the manufacture of automotive parts such as automobile head liners as disclosed in United States Patent No. 4,729,917. Products produced with foam laminates having one or two layers of nonwoven fiber glass mat with urea formaldehyde binder are affected by high humidity and high ambient temperature to cause an unpleasant odor and also to deteriorate the binder strength. Also, non-extendible mat, i.e. a mat bound with a resin binder that is fully cured is relatively stiff and does not conform well to curves and complex curvature, such as three dimensional curvature, and still provide excellent rigidity or stiffness to the foam laminate. It is also known to make nonwoven fiber glass mats for bonding to a layer of polymeric foam to stiffen the foam by chopping dry strands of glass fibers bound together with a binder to form chopped strand, to collect the chopped strand on a moving conveyor in a random pattern, and to bond the chopped strand together at their crossings by dusting a dry, powdered thermoplastic binder like a polyamide, polyester or ethylene vinyl acetate on wetted chopped strands followed by drying and curing the binder, as disclosed in United States Patent No. 5,565,049. While such products may work, the mat does not have as high a tensile strength as desired and as achieved with a wet laid nonwoven fiber glass mat because the bundles or chopped strands in the mat, according to the disclosure of the above cited patent, do not bond together as well as the individual fibers in a typical nonwoven mat. For example, the average sum of the machine direction tensile and the cross machine direction tensile for a chopped fiber glass strand mat made in this manner and having a basis weight of about 91.9 g/m 2 (1.88 pounds per 100 sq. ft) is about 10.9 kg/7.62 cm (24 lbs. per 3 inch) compared to at least twice this tensile for wet laid nonwoven fiber glass mats. Mats made according to the process of U.S. Patent No. 5,565,049 also are more expensive to make than a typical nonwoven mat made with known wet laid processes. It is also known to use an acrylic copolymer latex, such as a self-crosslinking acrylic copolymer of an anionic emulsifying type as one component of at least a two component binder for bonding glass fibers and particulate thermoplastic to make a glass fiber reinforced sheet that can later be hot molded into various shapes and articles, as disclosed in United States Patent No. 5,393,379. The sheet products taught by this patent would not be suitable to use for stiffening foam layers because of the presence of the substsantial amount of particulate thermoplastic in the sheet. SUMMARY OF THE INVENTION The present invention includes a fibrous nonwoven mat for laminating to a material like a polymeric foam layer, comprising dispersed and crossing glass fibers bound together with a "B" staged acrylic copolymer latex, the acrylic copolymer having a glass transition temperature of at least 45 degrees centigrade, and preferably near 55 degrees C. By near is meant +/- 1-5 degrees C., such as +/- 2 degrees C. The glass transition temperature can be as high as at least 72 degrees C. The invention also includes polymeric foam laminate precursors and laminates having a wet laid, nonwoven mat, according to the present invention, adhered or laminated to at least one major surface, and preferably both major surfaces, of a polymeric foam. The invention also includes a method of making the nonwoven mat described above comprising dispersing glass fibers in an aqueous slurry, collecting the dispersed fibers onto a moving permeable support to form a fibrous nonwoven, removing excess water from the fibrous nonwoven, applying an aqueous acrylic copolymer latex, the acrylic copolymer having a glass transition temperature of at least 45 degrees C., removing excess latex, and drying and curing the mat to only "B" stage the acrylic copolymer. The present invention also includes a precursor to a foam laminate, a method of making foam laminates by adhering a mat, according to the present inveniton, onto at least one surface of a polymeric foam part or layer and molding the precursor sandwich into a finished foam laminate or composite, and the finished foam laminate. The mats of the present invention preferably have bundles of incompletely dispersed fibers in which the fibers are preferably at least 2.79 cm (1.1 inch) long and most preferably at least 3.18 cm (1.25 inch). The mats can also contain pigments, dyes, flame retardants, and other additives so long as they do not significantly reduce the ability of the mat to bond to a foam surface. The pigments or other additives can be included in the fiber slurry, the binder slurry or can be sprayed or otherwise coated onto the mat later using known techniques. DETAILED DESCRIPTION OF THE INVENTION It is known to make reinforcing nonwoven mats from glass fibers and to use these mats as substrates in the manufacture of a large number of roofing and other products. Any known method of making nonwoven mats can be used, such as the conventional wet laid processes described in U.S. Patent No. 4,129,674, 4,112,174, 4,681,802, 4,810,576, and 5,484, 653. In such processes a slurry of glass fiber is made by adding glass fiber to a typical white water in a pulper to disperse the fiber in the white water forming a slurry having a fiber concentration of about 0.2-1.0 weight %, metering the slurry into a flow of white water to dilute the fiber concentration to 0.1 or below, and depositing this mixture onto a moving screen forming wire to dewater and form a wet nonwoven fibrous mat. The preferred technique for the making of mats of the present invention is forming a dilute aqueous slurry of fibers and depositing the slurry onto an inclined moving screen forming wire to dewater the slurry and form a wet nonwoven fibrous mat, on machines like a Hydroformer™ manufactured by Voith-Sulzer of Appleton, WS, or a Deltaformer™ manufactured by North County Engineers of Glenn Falls, NY. This wet nonwoven mat of glass fiber is then transferred to a second moving screen and passed through a binder application saturating station where an aqueous binder is applied to the mat in any one of several known ways. The binder saturated mat is then passed over a suction section while still on the moving screen to remove excess binder. The wet mat is then transferred to a wire mesh moving belt and passed through an oven to dry the wet mat and to cure (polymerize) the polymeric binder based resin binder which bonds the fibers together in the mat. Preferably, the aqueous binder solution is applied using a curtain coater or a dip and squeeze applicator, but other known methods of application such as spraying will also work. Alternative forming methods for making the mat include the use of well known paper or board making processes sucha s cylinder forming, etc. or "dry laying" using carding or random fiber distribution. When making mat of the present invention, the temperatures and time in the drying and curing oven are controlled to only "B" stage the acrylic copolymer binder, being careful not to fully cure the binder. This is critical to the performance of the mat. When the mat binder is cured to only "B" stage, the mat is softer and more flexible and molds better, particularly to a curved or complex curvature shape. Also, a substantially stiffer foam laminate results when the binder in a wet laid, nonwoven mat molded with an adhesive coated foam layer is only cured to "B" stage than if the binder is fully cured prior to molding. In the latter case the foam laminate is either not well formed or is not stiff enough for automotive headliner applications whereas is is at least equal in stiffness and superior in shape or mat conformity when the mat of this invention is used. Mats of the present invention preferably contain 70-85 weight percent fibers and 15-30 percent acrylic copolymer binder. Up to 50 weight percent binder is permissible, but up to 30 percent is generally preferred. However, in some instances, higher binder contents improve stiffness of the final composite or laminate as will be seen below. The preferred basis weight of the mat will depend upon the specific application. For stiffening foam for automotive headliners, the preferred basis weight is 78.2 g/m 2 (1.6 lbs per 100 sq. ft.), but a basis weight of 92.9 g/ m 2 (1.9 lbs./100 sq. ft.) also worked well and weights lighter than 78.2 g/m 2 (1.6 lbs. per 100 sq. ft.) also are suitable. The majority or the fibers are glass fibers and preferably all the fibers are glass fibers. The glass fibers should be at least 1.9 cm (0.75 inch) long or longer, more preferably at least 2.54 cm (one inch) long and most preferably at least 2.79, e.g. 2.86 to 3.81 cm (1.1, e.g. 1.25 to 1.5 inches) long. The glass fibers which can be used to make mats can have various fiber diameters dependent on the strength and other properties desired in the mat as is well known, but since the mat is intended to be relatively stiff, fibers having a diameter of at least 13 microns are preferred and at least 15 micron is more preferred, such as M fiber which has an average fiber diameter of about 15.5 - 16.5 microns. It is preferred that the fibers be coated with a silane containing size composition which is well known in the industry. It is preferred that the length of the chopped strands of glass fiber be such that when the chopped strand is added to the wet mat machine in the stock preparation section the fiber does not completely disperse, leaving some multi-fiber bundles in the stock. These bundles, much smaller in numbers of fibers than the chopped strand used in the prior art as discussed earlier, are beneficial to the stiffness of the present mat product and its stiffening performance when laminated to foam. This is accomplished in normal whitewater with a fiber length of at least 2.79 cm (1.1 inch) and most preferably at least 3.18 cm (1.25 inch). This can also be accomplished with shorter fiber by modifying the whitewater in known ways to reduce dispersion effectiveness, reducing agitation and/or time in the pulper and the stock tank or a combination of these. The glass fibers can be E, C, T, S or any known type glass fiber of good strength and durability in the presence of moisture and mixtures of lengths and diameters. The preferred fibers are K or M 137 and K or M 117 E glass fibers available from Johns Manville International, Inc. of Denver, CO, but many commercially wet chop glass fiber product will be suitable. While the majority of the fibers are glass fibers, a minor portion of non-glass fibers can also be used, such as man made or natural organic fibers like Nylon™, polyester, polyethlyene, polypropylene, cellulose or cellulose derivatives, etc. The binders used to bond the fibers together are cross linking acrylic copolymer resins that can be put into aqueous solution or emulsion latex, have a glass transition temperature (GTT) of at least 45 degrees centigrade and that can be "B" staged. To "B" stage these resins in the present invention, very little, or preferably no, external cure catalyst is used and the mat is cured at temperatures between about 104.44 and about 148.89 degrees C. (220 and about 300 degrees F.), preferably about 121.11 degrees C. (250 degrees F.) for very short times, such as 40 seconds or less, preferably about 10 - 20 seconds. If the cure temperature is much less than 104.44 degrees C. (220 degrees F.), the resultant mat will not have adequate strength for handling and processing in the intended uses to avoid damage. If the cure temperature is much above 148.89 degrees C. (300 degrees F.), the resin will cure too much and the mat will not bond as well to foam later. Preferably, GTT is between 50 and 72 and most preferably 55 +/- 5 degree C such as 55 +/-2 degrees C. The preferred crosslinking acrylic copolymer for use as a binder in the present invention is an aqueous carboxyl modified acrylic copolymer known as Hycar™ 26315 available from the BF Goodrich Company of Brecksville, Ohio, and having a glass transition temperature of 55 degrees C. This same company's Carbocure™ TSR-72, having a glass transition temperature of 72 degrees C. works almost as well, but the mat made using this binder may be too stiff for some applications. In the present invention, these binders can be used in amounts of up to 50 weight percent of the mat, but preferably make up to more than 30 wt. percent of the mat. Preferably, the aqueous binder solution is applied using a curtain coater of a dip and squeeze applicator. In the drying and curing oven the mat is heated to temperatures of up to 148.89 degrees C. (300 degrees F.), but this can vary from 104.44 degrees C. to as high as 148.89 degrees C. (220 degrees F. to as high as 300 degrees F.), for periods usually not exceeding 1 or 2 minutes and frequently less than 40 seconds. EXAMPLE 1 A fiber slurry was prepared in a well known manner by adding 3.18 cm (1.25 inch) long wet M 137 E type glass wet chopped fiber from Johns Manville International, Inc. having a silane containing chemical sizing on the surface, as is well known, to a known cationic white water containing Natrosol™ thickening agent available from Aqualon, Inc. of Wilmington, DE, and a cationic surfactant C-61, an ethoxylated tallow amine available from Cytec Industries, Inc. of Morristown, NJ, as a dispersing agent to form a fiber concentration of about 0.8 weight percent. After allowing the slurry to agitate for about 20 minutes to thoroughly disperse the fibers, the slurry was metered into a moving stream of the same whitewater to dilute the fiber concentration to a concentration averaging 0.05 to 0.06 weight percent before pumping the diluted slurry to a headbox of a Voith Hydroformer™ where a wet nonwoven mat was continuously formed. The wet mat was removed from the forming wire and transferred to a Sandy Hill Curtain Coater where an aqueous acrylic copolymer latex, Hycar™ 26315 was applied in an amount to provide a binder level in the cured mat of about 20 - 30 weight percent. The wet mat was then transferred to an oven belt and carried through an oven to dry the mat and to heat the mat to a temperature of 121.11 degrees C. (250 degrees F.) for about 30 seconds to "B" stage the resin binder. The basis weight of the mat produced was 78.2 g/m 2 (1.6 lbs./100 sq. ft.) . The mat had the following properties: Hot Wet Tensile (10 minutes in 82.22 degree C. (180 degree F. water)) 90+ percent Thickness 0.58 mm (23 mils) Loss On Ignition 21 wt. percent Machine Direction Tensile 13.6 Kg/7.62 cm (30 lbs./3 inch) wide sample Cross Machine Direction Tensile 11.4 kg/7.62 cm (25 lbs./3 inch) wide After further curing the above mat further at 190.56 degrees C. (375 degrees F.) for 3 minutes the mat was tested for tensile strength with the following results: MD tensile 29.1 kg/7.62 cm (64 lbs. per 3 inch) wide sample CMD tensile 20.5 kg/7.62 cm (45 lbs. per 3 inch) wide sample Hot wet tensile - No change. The higher tensiles of the post cured mat show that further curing of the binder to fully cure the binder increases its tensile strength. This mat was then laminated to foam in the following manner: The foam was a layer of urethane foam having a density of about 0.0337 g/cc. (2.1 lbs. per cubic feet) purchased from Foamex of Ft. Wayne, IN. This foam layer was coated on both major sides with B. F. Goodrich Sancure™ 815, an alphatic waterborne urethane polymer adhesive, at a rate of 30-35 g/m 2 and a sheet of mat of Example 1 was put on the adhesive layer on each side of the foam layer. This particular adhesive is only one of many heat settable adhesives that is suitable for the present invention. This sandwich was then molded at about 160 degrees C. (320 degrees F.) and just enough pressure to deform the sandwich into the shape of the hot mold, and allowed to set under pressure and temperature for one minute. The resultant molded composite or laminate, laminate A in the TABLE below, had a stiffness much higher than the foam layer itself and approximately equal to the stiffness of a chopped strand mat, foam layer, chopped strand mat composite molded in the same manner as above. EXAMPLE 2 Another mat was made in exactly the same way as in Example 1, except that the binder for the mat was replaced with B. F. Goodrich Company's Carbocure™ TSR - 72 acrylic copolymer having a glass transition temperature of about 72 degrees C. The properties of the mat after curing the binder to "B" stage only were: Thickness 0.58 mm (23 mils) Hot wet tensile 5 percent Loss on Ignition 26.8 weight percent Machine Direction Tensile 23.64 kg/7.62 cm (52 lbs./3 inch) sample Cross Machine Tensile 22.27 kg/7.62 cm (49 lbs./3 inch) sample Samples of this mat were further treated by heating them to 190.56 degrees C. (375 degrees F.) for 3 minutes and tested for tensile with the following results: Hot wet tensile 73 percent Machine direction tensile 52.73 kg/7.62 cm (116 lbs./3 inch) wide sample Cross machine dir. tensile 43.18 kg/7.62 cm (95 lbs./3 inch) wide sample The mat made in Example 2 above was used to make a laminated foam sandwich in the same manner as described in Example 1, referred to in the TABLE below as laminate B, with similar results as achieved in Example 1. Examples 3 - 5 Mats were made exactly as described in Example 1, except for the amount of binder used in the mat and the basis weight of the mat. The properties of these mats follow (the tensile strengths are in the same units and tested as the same as Examples 1 and 2) : Example No. % Binder Basis wt. MD Tensile CMD Tensile Example 3 21 86 (1.76) 12.73 (28) 12.27 (27) Example 4 33 96.77 (1.98) 27.27 (60) 24.55 (54) Example 5 15 60.12 (1.23) 12.27 (27) 12.27 (27) Laminates were made with the mats of Examples 3-5 exactly as described in Example 1 and tested to failure in a three point loading test know as S. A. E. J949A standard, of different foam laminates made the very same way except for the type of mat used. Laminate C is a foam laminate using the mat from Example 3, laminate D was made using the mat from Example 4, laminate E was made using the Mat from Example 5. The loading test results o the laminates made in the above Examples are shown in the TABLE below: A B C D E Average peak load at failure (Newtons) 14.6 13.9 17.8 19.5 13.6 Other conventional wet laid nonwoven mats, such as DURA-GLASS™ 3115, 8130, M8130 and 8422 were evaluated as mats to use to laminate to foam layers using the laminating process described in Example 1 to achieve a laminate or composite of the desired stiffness, but none of these mats produced a laminate with as high a stiffness as those of the present invention, and not high enough stiffness to meet the requirements for use in automotive headliners. For example, M8130 mat produced an average peak load of only 10 Newtons and 3015 mat produced an average peak load of only 5 Newtons. The higher tensiles of the "B" staged wet laid nonwoven mat of the present invention, compared to the currently used chopped strand mat disclosed in U.S. Patent No. 5,565,049, makes it easier to work with and apply the nonwoven mat to the foam layer and reduces tears in the mat during molding. The higher tensiles of the fully cured wet laid nonwoven mats of the present invention, compared with the molded chopped strand mat described above, makes the molded foam laminate or composite tougher and more durable. Other adhesives than the adhesive described in the Examples above can be used to help bond the fiber mat to the foam layer. For example, an ethylene vinyl acetate having a softening range of 110-121.11 degrees C. (230 - 250 degrees F.) can be used as well as many others, so long as the adhesive sets or fully cures under heat and pressure in a reasonable time. Other adhesives for this purpose are well known and it is within the skill of an artisan to select suitable adhesives for this purpose. While the preferred embodiments of the invention have been disclosed in detail, other embodiments within the described invention and having other functional additives known or obvious to those skilled in the art are considered to be part of the present invention and are intended to be included in the invention claimed below.

Claims: A fiber glass mat comprising glass fibers bonded together with up to 50 weight percent, based on the weight of said mat, of a crosslinking acrylic copolymer latex resin binder having a glass transition temperature of at least 45 degrees C. and not greater than at least 72 degrees C. wherein the resin binder is only partially cured to a "B" stage condition. A mat as described in claim 1 wherein the glass transition temperature of the acrylic copolymer is less than 72 degrees C. and the major portion of the mat is glass fibers having a length of 2.79 cm (1.1 inch) or longer. A mat as described in claim 1 wherein the crossing, unbonded fibers contain man made or natural organic fibers. A mat as described in claim 1 wherein the resin binder has a glass transition temperature in the range of 50 to 72 degrees C. A mat as described in claim 4 wherein the glass transition temperature of the resin binder is between 50 and 60 degrees C. A method of making a fiber glass mat wherein an aqueous mixture comprising a binder is applied to a nonwoven mat of unbonded, crossing glass fibers followed by drying said mat and at least partially curing said resin to form a bonded glass fiber mat, the improvement comprising using as the resin binder a crosslinking acrylic copolymer having a glass transition temperature of at least 45 degrees C., drying and curing the mat only partially to "B" stage the resin binder, said binder being present in the dried mat in amounts up to 50 weight percent of the mat. The method of claim 6 wherein the major portion of the mat is glass fibers having a length of 2.79 cm (1.1 inch) or longer. The method described in claim 7 wherein the crossing unbonded fibers also contain man made or natural organic fibers. The method of claim 7 wherein the mat is heated to temperatures below 148.9 degrees C. (300 degrees F.) for a time that will convert and keep said binder to and in a "B" stage condition. The method as described in claim 7 wherein the resin binder has a glass transition temperature in teh range of 50 to 72 degrees C. The method as described in claim 10 wherein the glass transition temperature of the resin binder is between 50 and 60 degrees C. A foam laminate precursor ready for molding comprising a layer of foam, a layer of adhesive on at least one major face of said layer of foam and wet laid, nonwoven, fibrous mat in which the majority of the fibers are glass fibers and having a binder therein cured to only a "B" stage, bonded to said layer of cured adhesive, said binder being a crosslinking acrylic copolymer having a glass transition temperature of at least 45 degrees C. A foam laminate as described in claim 12 wherein teh major portion of the mat is glass fibers at least 2.79 cm (1.1 inch) long. A foam laminate as described in claim 12 wherein the crossing, unbonded fibers contain man made or natural organic fibers. A foam laminate as described in claim 13 wherein the resin binder has a glass transition temperature in the range of 50 to 72 degrees C. A foam laminate as described in claim 15 wherein the glass transition temperature of the resin binder is 50 to 60 degrees C. A method of making a foam laminate comprising coating layer of foam with a layer of adhesive on at least one major face of said layer of foam and placing a wet laid, nonwoven, fibrous mat in which the majority of the fibers are glass fibers and having a binder therein cured to only a "B" stage, onto said at least one layer of adhesive and molding the resultant sandwich at a temperature exceeding 148.9 degrees C. (300 degrees F.) for a time sufficient to fully cure the binder in said mat and the adhesive, said mat binder being a crosslinking acrylic copolymer having a glass transition temperature of at least 45 degrees C and not greater than at least 72 degrees C. A method of making a foam laminate as described in claim 17 wherein the major portion of the mat is glass fibers at least 2.79 cm (1.1 inch) long. A foam laminate as described in claim 17 wherein the crossing, unbonded fibers contain man made or natural organic fibers. A foam laminate as described in claim 18 wherein the resin binder has a glass transition temperature in the range of 50 to 72 degrees C. A foam laminate as described in claim 20 wherein the glass transition temperature of the resin binder is 50 to 60 degrees C. A foam laminate produced by the process of claim 17.

Inventors: JAFFEE ALAN MICHAEL, JAFFEE, ALAN MICHAEL
Applicants: JOHNS MANVILLE INTERNAT INC, JOHNS MANVILLE INTERNATIONAL INC.
Application year: 1999
Main classification: C03C25
IPC codes: B32B5