Composition and tire with tread containing calcium carbonate

Abstract: The invention relates to a rubber composition containing relatively low levels of carbon black and/or silica reinforcement together with a particulate calcium carbonate and selected modifiers. The invention particularly relates to a tire having a component, particularly a tread, of such composition.

Description: Field The invention relates to a rubber composition The invention relates to a rubber composition containing relatively low levels of carbon black and/or silica reinforcement together with a particulate calcium carbonate and selected modifier(s). The invention particularly relates to a tire with a component thereof, particularly a tire tread. Background Rubber compositions are typically used for tire treads which may be optimized for various rubber composition properties to promote one or more of three tire properties; namely, traction, rolling resistance and treadwear. In this regard, typically desirable physical properties for tire tread rubber compositions may include, for example, hysteresis, hardness and modulus. Some properties are normally indicated by their rebound properties, tangent delta (Tan. delta) at 0°C, and abrasion resistance. Hysteresis is conventionally related to Hot Rebound values. Such physical properties are well known to those having skill in the rubber compounding art and, in general, are considered to be somewhat predictive of tire tread performance. More specifically, it is sometimes desired that a tire have a relatively low rolling resistance to enhance a vehicle's fuel economy. A lower hysteresis, usually evidenced by a higher hot rebound value, of a cured, or vulcanized, rubber composition is predictive of reduced heat build-up for the rubber composition and, therefore, of its utility for a relatively low rolling rubber composition for use as a tire tread. It is often an accepted practice to reduce particulate reinforcement of a rubber composition to a relatively low level to reduce its hysteresis and thus, a predictive reduction in rolling resistance for a tire tread application. For example, where it might be desired to reduce a tire's rolling resistance by reducing hysteresis increasing hot rebound values of a rubber composition for a tire tread application, particulate reinforcement such as carbon black and/or silica might conventionally be reduced from a somewhat normal range of 55 to 80 phr to a reduced amount of such reinforcement in a range of 30 to 50, and particularly 30 to 45, phr. Such reduction in particulate reinforcement for a tire tread rubber for reduction in a tire's rolling resistance is well known to those having skill in such art. However, commensurate with rolling resistance of the tire tread composition reduction by reducing reinforcing filler content, with other aspects of the rubber composition being essentially unchanged, the tire tread wear resistance often decreases, as may be evidenced by an increase in the tire's treadwear, and there is usually a degree of loss in tire tread traction. In one aspect, a tire's increase in treadwear can sometimes be predicted or somewhat correlated, reduction in the cured rubber composition's abrasion resistance. Accordingly, it is desired herein to provide a tire tread rubber composition with reduced hysteresis (increased hot rebound values) while substantially maintaining an acceptable abrasion resistance, and usually an acceptable tire tread traction. It is desired to provide such rubber composition with low levels of carbon black and/or silica reinforcement. It is recognized herein that calcium carbonate has sometimes been used as a relatively low cost filler and extender for various polyolefin resins and some elastomers. However, it is believed herein that it has not been used in tire treads with a relatively low carbon black content together with specified modifier(s). JP-A-09 150606 discloses a rubber composition for producing a tire comprising natural rubber, carbon black, silica, calcium carbonate and a silane coupler. EP-A-0 731 132 describes a rubber being reinforced with a combination of silica and/or carbon black, and also a silica coupler selected from the group of nicotinamide, dithiodipropionic acid and bis-(3-triethoxysilylpropyl)tetrasutfide). In the description of this invention, the term "phr," where used herein, and according to conventional practice, refers to "parts of a respective material per 100 parts by eight of rubber or elastomer". In the description of this invention, the terms "rubber" and "elastomer," if used herein, may be used interchangeably, unless otherwise prescribed. The terms "rubber composition," "compounded rubber" and "rubber compound," if used herein, are used interchangeably to refer to "rubber which has been blended or mixed with various ingredients and materials" and such terms are well known to those having skill in the rubber mixing or rubber compounding art. Summary and Description of the Invention In accordance with this invention, a rubber composition is provided, and particularly a tire with a component of such composition, including a tire tread, which comprises (A) 100 parts by weight of elastomer consisting essentially of a combination of diene-based elastomer and an epoxidized natural cis 1,4-polyisoprene rubber, (B) 15 to 45, alternatively 25 to 40, phr of particulate reinforcement selected from carbon black and/or precipitated silica, said silica having silanol groups on the surface thereof, (C) 5 to 50, alternatively 10 to 30, phr of particulate calcium carbonate and (D) at least one modifier comprised of at least one of dithiodipropionic acid, nicotinamide and bis-3(trialkoxysilylalkyl) polysulfide having an average of from 2.1 to 4 sulfur atoms in its polysulfide bridge and where such alkyl groups contain from two to four carbon atoms. In one aspect of the invention, said elastomers are (a) 5 to 30 phr of epoxidized diene-based rubber, preferably epoxidized natural cis 1,4-polyisoprene rubber, containing 20 to 50 percent epoxidization and (b) 95 to 70 phr of said diene based rubber. In one aspect, the said particulate reinforcement for the rubber composition may be composed of 15 to 30 phr of such carbon black without precipitated silica or 13 to 35 phr of precipitated silica and 2 to 20 phr of carbon black. For the purposes of this invention, a significant aspect is the relatively low concentration of carbon black reinforcement in combination with the use of calcium carbonate and modifier(s). The modifier may be dithiodipropionic acid. The modifier may be nicotinamide. The modifier may be a bis-3(trialkoxysilylalkyl) polysulfide having from 2 to 8, with an average of 2.1 to 4, sulfur atoms in its polysulfidic bridge. Usually an average of from 2.1 to 2.5 or from 3.2 to 4 sulfur atoms are preferred for the polysulfidic bridge. Usually the trialkoxy groups are selected from trimethoxy and triethoxy groups and the remaining alkyl groups are selected from ethyl, propyl and butyl groups. Thus, such modifier might, for example, be selected from bis-1(trimethoxysilylpropyl) polysulfide and bis-3(triethoxysilylpropyl) polysulfide. While it is recognized that such modifiers might also sometimes be known as silica couplers having a moiety reactive with silanol groups contained on the surface of the silica and another moiety, usually a polysulfide, interactive with one or more of said diene-based elastomers, in this case it appears that they serve to interact with the calcium carbonates. Usually the modifier is present as a weight ratio of modifier to calcium carbonate in a range of 1/100 to 1/1, alternatively in a range of 1/50 to 1/5 or in a more limited range of 1/20 to 1/10. Other forms of silica, including fumed silica which is different from precipitated silica, are not preferred. Usually the calcium carbonate has a particle size average diameter in a range of 50 to 14,000 nanometers (nm). In practice, the surface of the particulate calcium carbonate can be coated, if desired, to aid in its dispersion in a rubber composition. Such coating may be, for example, in a form of a polyolefinic material, particularly a saturated polyolefinic material. Further Detailed Description It is considered that this invention is particularly applicable where it is desired to endeavor to minimize tire tread rolling resistance and, namely to provide higher hot rebound values for a tire tread elastomer composition, but where it is also desired to substantially retain rubber composition physical properties such as, for example, DIN abrasion which may relate to treadwear, stiffness, tensile strength and modulus and/or tread traction. In the practice of this invention, it is believed to be a very substantial departure from past practice for rubber tire treads to utilize relatively low levels of reinforcing pigments such as carbon black and/or silica and to correspondingly use calcium carbonate as a relatively non-reinforcing filler, together with modifier(s), to increase the overall filler level to a range of 30 to 65 phr for the total amount of the carbon black and/or silica, as the case may be, and calcium carbonate, with the amount of carbon black and optional silica being restricted to a maximum of 45 phr. The carbon blacks used may be conventional rubber reinforcing carbon blacks. Such carbon blacks may, for example have a DBP (dibutylphthalate) adsorption value in a range of 70 to 150, usually 80 to 130, cc/100 g and a corresponding Iodine adsorption value in a range of 40 to 140, usually 60 to 125, g/kg. Representative of various carbon blacks, for example, that fall within the above ranges include, for example, N121, N220, N234. The aforesaid N121 and N220 carbon blacks reportedly have a DBP value of 130 and 114, respectively, and an Iodine adsorption value of 120 and 121, respectively. If desired, a combination of high reinforcing and relatively low reinforcing carbon blacks might be used such as, for example, a combination of N110 and/or N220 high reinforcing carbon black with N550 and/or N660 relatively low reinforcing carbon black wherein 60 to 80 weight percent of the carbon black is the high reinforcing carbon black. It is one important aspect of this invention that the addition of the calcium carbonate filler, and associated modifier(s), might be used exclusive of, or in the absence of silica or possibility only a relatively small amount of silica such as, for example 10 to 15 or 20 phr of silica to endeavor to achieve a reduction of rebound values for a rubber composition intended for use as a tire tread (prediction of less rolling resistance), while still maintaining a satisfactory DIN abrasion value for the cured rubber composition, as compared to using relatively low levels of carbon black alone for the rubber reinforcement. While it has been contemplated that addition of substantial and, therefore, quantitative amounts of precipitated silica, together with a silica coupler, as compared to use of a carbon black reinforcement, to a rubber composition may enhance, or promote, an increase in rebound values and, therefore, hysteresis which is predictive of a reduction in rolling resistance for a tire tread, the significance of this invention is that, for many rubber compositions contemplated for use as a tire tread, the quantitative use of silica reinforcement may not be necessary where relatively low tire tread rolling resistance is a significant consideration for the tire tread. This is accomplished by replacing at least a portion of the silica with calcium carbonate but requiring one of more of said modifiers to also be present. Thus a reduced amount of silica content in the tread rubber composition might be used and still achieve the rubber composition's rebound and DIN abrasion values. A significance of this discovery, at least in one sense, is even greater when taking into consideration that (i) the silica is considerably more expensive than the carbon black and calcium carbonate and, further, that (ii) considerably more mixing, and thus greater rubber processing, time is normally required when using relatively high concentrations of silica reinforcement for the tire tread rubber composition. Thus, it is contemplated for this invention that use of the calcium carbonate, together with the modifier(s) may enhance the rubber composition processing, namely by reducing the mixing timer, as compared to a rubber composition containing using a silica concentration of 60 phr or greater. It is understood that the DBP (dibutylphthalate) adsorption values may be determined by ASTM test D2414 and the Iodine values may be determined by ASTM test D1510. For example, the Iodine value, or number, for carbon black is a measure of its surface area and is expressed in units of g/kg. A higher Iodine value is indicative of smaller particle size which, in turn, is indicative of higher surface area for the carbon black and typically a higher reinforcing carbon black for elastomers. The DBP (dibutylphthalate) adsorption value for carbon black is a measure of its structure, or aggregate size and is higher DBP adsorption value indicative of larger aggregates which, in turn, is indicative of higher structure for the carbon black. Iodine values and DBP values together with representative ASTM designated N- numbers may be found, for example, in The Vanderbilt Rubber Handbook, Thirteenth Edition (1990), page 417. In the practice of this invention, as hereinbefore pointed out, the rubber composition is comprised of (i) at least one diene-based elastomer, or rubber or (ii) a combination of at least one diene-based elastomer with an epoxidized diene-based elastomer such as epoxidized natural rubber. Such diene-based elastomers are typically selected from homopolymers and copolymers of conjugated dienes and copolymers of conjugated diene(s) and vinyl aromatic compound such as, for example, styrene and alphamethylstyrene. Such dienes may, for example, be selected from isoprene and 1,3-butadiene and such vinyl aromatic compounds may be selected from styrene and alphamethylstyrene. Such elastomer, or rubber, may be selected, for example, from at least one of cis 1,4-polyisoprene rubber (natural and/or synthetic, and preferably natural rubber), 3,4-polyisoprene rubber, styrene/butadiene copolymer rubbers, isoprene/butadiene copolymer rubbers, styrene/isoprene copolymer rubbers, styrene/isoprene/butadiene terpolymer rubbers, cis 1,4-polybutadiene rubber, trans 1,4-polybutadiene rubber (70-95 percent trans), low vinyl polybutadiene rubber (10-30 percent vinyl), high vinyl polybutadiene rubber (30-90 percent vinyl). In one aspect, the rubber is often comprised of at least two diene-based elastomers in which one of the elastomers is cis 1,4-polybutadiene. Such combination of elastomers may also be used together with an epoxidized diene-based elastomer such as epoxidized natural rubber. For example, such combination of two or more diene-based rubbers may be cis 1,4-polyisoprene rubber (natural or synthetic, although natural is usually preferred), 3,4-polyisoprene rubber, isoprene/butadiene copolymer rubber, styrene/isoprene/butadiene rubber, emulsion and solution polymerization derived styrene/butadiene rubbers, cis 1,4-polybutadiene rubbers, medium vinyl polybutadiene rubbers (30-55 percent vinyl), high vinyl polybutadiene rubbers (55-90 percent vinyl) and emulsion polymerization prepared butadiene/acrylonitrile copolymers. The epoxidized natural rubber is known to those having a skill in the art and may be described as a modified form of natural cis 1,4-polyisoprene rubber in which some of its unsaturation is replaced by epoxidized groups. Epoxidized natural rubber which may be used in this invention may have a level of epoxidized modification ranging from 15 to 85, preferably 20 to 50, mole percent. A particularly preferred level epoxidized level for the natural rubber is 25 mole percent. As is known to those having skill in such art, epoxidized natural rubber can be obtained by epoxidizing natural rubber latex. Such epoxidized natural rubber may be obtained from Malaysian rubber producers under a designation, for example, of ENR 25 (25 percent epoxidized level) and ENR 50 (50 percent epoxidized level). In one aspect of this invention, an emulsion polymerization derived styrene/butadiene (E-SBR) might be used as a diene-based elastomer having a relatively conventional styrene content of 20 to 28 percent bound styrene or, for some applications, an E-SBR having a relatively high bound styrene content, namely a bound styrene content of 30 to 45 percent. The relatively high styrene content of 30 to 45 for the E-SBR can be considered beneficial for a purpose of enhancing traction, or skid resistance, of the tire tread. The presence of the E-SBR itself is considered beneficial for a purpose of enhancing processability of the uncured elastomer composition mixture, especially in comparison to a utilization of a solution polymerization prepared SBR (S-SBR). By emulsion polymerization prepared E-SBR, it is meant that styrene and 1,3-butadiene are copolymerized as an aqueous emulsion. Such are well known to those skilled in such art. The bound styrene content can vary, for example; from 5 to 50 percent. In one aspect, the E-SBR may also contain acrylonitrile to form a terpolymer rubber in amounts, for example, of 2 to 30 weight percent bound acrylonitrile in the terpolymer. The solution polymerization prepared SBR (S-SBR) typically has a bound styrene content in a range of 5 to 50, preferably 9 to 36, percent. The S-SBR can be conveniently prepared, for example, by organo lithium catalyzation in the presence of an organic hydrocarbon solvent. A purpose of using S-SBR is for improved tire rolling resistance as a result of lower hysteresis when it is used in a tire tread composition. The 3,4-polyisoprene rubber (3,4-PI) is considered beneficial for a purpose of enhancing the tire's traction when it is used in a tire tread composition. The 3,4-PI and use thereof is more fully described in U.S. Patent No. 5,087,668. The Tg refers to the glass transition temperature which can conveniently be determined by a differential scanning calorimeter at a heating rate of 10°C per minute. The cis 1,4-polybutadiene rubber (BR) is considered to be beneficial for a purpose of enhancing the tire tread's wear, or treadwear. Such BR can be prepared, for example, by organic solution polymerization of 1,3-butadiene. The BR may be conveniently characterized, for example, by having at least a 90 percent cis 1,4-content. The cis 1,4-polyisoprene and cis 1,4-polyisoprene natural rubber are well known to those having skill in the rubber art. A styrene/isoprene/butadiene terpolymer elastomer (SIBR) may be used in rubber composition of this invention. Representative examples of various SIBR's may be found, for example, in U.S. Patent Nos. 5,137,998, 5,159,020 and 5,272,220. It is readily understood by those having skill in the art that the rubber composition would be compounded by methods generally known in the rubber compounding art, such as mixing the various sulfur-vulcanizable constituent rubbers with various commonly used.additive materials such as, for example, curing aids, such as sulfur, activators, retarders and accelerators, processing additives, such as oils, resins including tackifying resins, coupling agent, and plasticizers, fillers, pigments, fatty acid, zinc oxide, waxes, antioxidants and antiozonants, peptizing agents and reinforcing materials such as, for example, carbon black. As known to those skilled in the art, depending on the intended use of the sulfur-vulcanizable and sulfur-vulcanized material (rubbers), the additives mentioned above are selected and commonly used in conventional amounts. The composition of the present invention may contain conventional amounts of known rubber chemicals. Typical amounts of tackifier resins, if used, may comprise 0.5 to 10 phr, usually 1 to 5 phr. Typical amounts of processing aids comprise 1 to 50 phr. Such processing aids can include, for example, aromatic, napthenic, and/or paraffinic processing oils. Typical amounts of antioxidants comprise 1 to 5 phr. Representative antioxidants may be, for example, diphenyl-p-phenylenediamine and others such as, for example, those disclosed in The Vanderbilt Rubber Handbook (1978), pages 344-346. Typical amounts of antiozonants comprise 1 to 5 phr. Typical amounts of fatty acids, if used, which are usually comprised primarily of stearic acid, comprise 0.5 to 3 phr. Typical amounts of zinc oxide comprise 2 to 5 phr. Typical amounts of waxes comprise 1 to 5 phr. Often microcrystalline waxes are used. Typical amounts of peptizers comprise 0.1 to 1 phr. Typical peptizers may be, for example, pentachlorothiophenol and dibenzamidodiphenyl disulfide. The vulcanization of the rubber composition is conducted in the presence of a sulfur-vulcanizing agent. Examples of suitable sulfur-vulcanizing agents include elemental sulfur (free sulfur) or sulfur-donating vulcanizing agents, for example, an amine disulfide, polymeric polysulfide or sulfur olefin adducts. Preferably, the sulfur-vulcanizing agent is elemental sulfur. As known to those skilled in the art, sulfur-vulcanizing agents are used in an amount ranging from 0.5 to 4 phr, or even, in some circumstances, up to 8 phr, with a range of from 1.5 to 2.5, sometimes from 2 to 2.5, being preferred. Accelerators are used to control the time and/or temperature required for vulcanization and to improve the properties of the vulcanizate. In one embodiment, a single accelerator system may be used, i.e., primary accelerator. Conventionally and preferably, a primary accelerator(s) is used in total amounts ranging from 0.5 to 4, preferably 0.8 to 2, phr. In another embodiment, combinations of a primary and a secondary accelerator might be used with the secondary accelerator being used in amounts of 0.05 to 5 phr in order to activate and to improve the properties of the vulcanizate. Combinations of these accelerators might be expected to produce a synergistic effect on the final properties and are somewhat better than those produced by use of either accelerator alone. In addition, delayed action accelerators may be used which are not affected by normal processing temperatures but produce a satisfactory cure at ordinary vulcanization temperatures. Vulcanization retarders might also be used. Suitable types of accelerators that may be used in the present invention are amines, disulfides, guanidines, thioureas, thiazoles, thiurams, sulfenamides, dithiocarbamates and xanthates. Preferably, the primary accelerator is a sulfenamide. If a second accelerator is used, the secondary accelerator is preferably a guanidine, dithiocarbamate or thiuram compound. The presence and relative amounts of most of the above additives are not considered to be an aspect of the present invention which is more primarily directed to the utilization of relatively low levels of reinforcing pigments as carbon black and/or silica together with a particulate calcium carbonate filler in rubber compositions for tire treads. The rubber composition may be prepared, for example, by thermomechanically working and mixing the diene-based rubber, epoxidized natural rubber if used, calcium carbonate, modifier(s), carbon black and/or silica and other rubber compounding ingredients, exclusive of the rubber curatives, in at least one sequential mixing step with at least one mechanical mixer, usually referred to as "non-productive" mix stage(s), to a temperature in a range of 160°C to 190° for a sufficient duration of time, usually within 4 to 8 minutes, followed by a final mix stage in which the curatives, such as sulfur and accelerators, are added and mixed therewith for 1 to 4 minutes to a temperature within a range of 90°C to 125°C. The terms "non-productive" and "productive" mix stages are well known to those having skill in the rubber mixing art.. It is to be appreciated that the rubber composition is conventionally cooled to a temperature below 40°C between the aforesaid mix stages. It is to be further appreciated that the aforesaid duration of time for the required temperature maintenance for the mixing process(es) during the non-productive mix stages can be accomplished, for example, by (i) adjusting the motor speed of the mixer, namely reducing the motor speed after the desired temperature of the rubber. composition is reached, in a variable speed mixer or by (ii) utilizing two or more mix stages sufficient to satisfy the duration requirement for the aforesaid maximum mixing temperature maintenance. Vulcanization of the rubber composition of the present invention is generally carried out at conventional temperatures ranging from 100°C to 200°C. Preferably, the vulcanization is conducted at temperatures ranging from 110°C to 180°C. Any of the usual vulcanization processes may be used such as heating in a press or mold, heating with superheated steam or hot air or in a salt bath. Upon vulcanization of the sulfur-vulcanized composition, the rubber composition of this invention can be used for various purposes. For example, the sulfur-vulcanized rubber composition may be in the form of a tread for a pneumatic tire which is the subject of this invention. Such tires can be built, shaped, molded and cured by various methods which are known and will be readily apparent to those having skill in such art. As can be appreciated, the tire may be a passenger tire, aircraft tire, truck tire and the like. Preferably, the tire is a passenger tire. The tire may also be a radial or bias, with a radial tire being preferred. The invention may be better understood by reference to the following examples in which the parts and percentages are by weight unless otherwise indicated. EXAMPLE I Control rubber compounds containing synthetic cis 1,4-polyisoprene rubber and reinforced with, variously, carbon black, silica and calcium carbonate were prepared in a three-stage Banbury mix (Table 1) and referenced herein as Ctrl. B, C and D. A further control rubber composition was prepared as Ctrl. A. Cure behavior and cured properties for these compounds are shown in Table 2. The gradual replacement of silica with 5, 10 and 15 phr calcium carbonate (Ctrl. B, C and D) illustrates a significant increase in rebound values and reduction of Tan.delta at 60°C as compared to the control (Ctrl. A) without significantly affecting cure behavior or other cured properties. The increase in rebound value and reduction of the Tan.delta (60°C) is predictive of improved (reduced) rolling resistance when used as a tire tread rubber composition. Ctrl A Exp B Exp C Exp D 1 st Non-Productive NATSYN® 2200 100 100 100 100 Carbon black 35 35 35 35 Antioxidant 2 2 2 2 Processing oil 5 5 5 5 Zinc oxide 5 5 5 5 Fatty acid 2 2 2 2 2 nd Non-Productive Silica 15 10 5 0 Si69 Coupler (50%) 3 3 3 3 Calcium carbonate 0 5 10 15 Productive Sulfenamide accelerator 1.0 1.0 1.0 1.0 Sulfur 1.4 1.4 1.4 1.4 Properties Ctrl A Exp B Exp C Exp D Max torque (MPa) 32 31.3 31.6 32 Min torque (MPa) 7.4 5.5 5.2 5.5 T 90 , min 19.5 18.0 16.5 16.0 T 25 , min 13.3 12.0 11.5 11.0 Tensile strength, MPa 20.2 19.5 19.6 19.1 Elongation @ break, % 613 593 589 573 M 100 , MPa 1.59 1.59 1.57 1.54 M 300 , MPa 7.76 7.73 7.61 7.33 Rebound, RT 48.9 51.3 54.0 57.3 Rebound, hot 61.5 63.7 66.6 69.3 Hardness, RT 53.1 53.3 52.7 52.4 Hardness, hot 52.2 52.0 51.2 51.3 E' @ 60°C, MPa 10.7 9.4 8.5 8.0 Tan. Delta @ 60°C 0.089 0.089 0.080 0.064 DIN Abrasion (cc loss) 144 165 180 167 EXAMPLE II Control rubber compounds containing emulsion polymerization prepared styrene/butadiene copolymer rubber (E-SBR), cis 1,4-polybutadiene rubber and synthetic cis 1,4-polyisoprene rubber and reinforced with carbon black and calcium carbonate were prepared in a three-stage Banbury mix (Table 3) and identified herein as Ctrl. F-K. Cure behavior and cured properties for these compounds are shown in Table 4. Compounds F, G and H contain 40 phr carbon black and 40 phr calcium carbonate, whereas compounds I, J and K contain 30 phr carbon black and 50 phr calcium carbonate. Compounds G and J also contain 3 phr and 4 phr Si69 (50%) coupler, respectively, and compounds H and K also contain 2 phr and 2.5 phr dithiodipropionic acids, respectively. The cured properties of the calcium carbonate containing compounds are observed to have been improved by the addition of either Si69 or dithiodipropionic acid. The improvement is shown in tensile strength, 100% modulus, hot rebound, hardness and DIN abrasion (lower is better). The mixing procedure was similar to Example I. The recipe is depicted in the following Table 3. The resulting physical properties after curing the rubber composition at 36 minutes at 150°C are shown in Table 4. Ctr F Ctr G Ctr H Ctr I Ctr J Ctr K 1 st Non-Productive E-SBR 68.75 68.75 68.75 68.75 68.75 68.75 BUDENE® 1207 15.0 15.0 15.0 15.0 15.0 15.0 NATSYN® 2200 35.0 35.0 35.0 35.0 35.0 35.0 Carbon black 40.0 40.0 40.0 30.0 30.0 30.0 Calcium carbonate 20.0 20.0 20.0 30.0 30.0 30.0 Antioxidant 2 2 2 2 2 2 Zinc oxide 3 3 3 3 3 3 Fatty acid 3 3 3 3 3 3 2 nd Non-Productive Calcium carbonate 20.0 20.0 20.0 20.0 20.0 20.0 Si69 Coupler (50%) 0 3 0 0 4 0 Dithiodipro-pionic acid 0 0 2 0 0 2.5 Productive Sulfenamide accelerator 3 3 3 3 3 3 Diphenyl- guanidine 2 2 2 2 2 2 Sulfur 3 3 3 3 3 3 Compounds F G H I J K Carbon black 40 40 40 30 30 30 Calcium carbonate 40 40 40 50 50 50 Si69 (50%) 0 3 0 0 4 0 Dithiodipro-pionic acid 0 0 2 0 0 2.5 Max. torque 46.0 53.0 45.0 44.0 46.4 52.3 Min. torque 4.0 5.0 5.1 4 4 11 T 90 , minute 9.5 16.0 10.0 10.0 17.5 21.5 T 25 , minute 5.5 8.5 5.5 5.5 9.0 15.8 Tensile strength, MPa 7.0 9.5 8.8 5.4 7.5 6.7 Elongation @ break, % 211 269 180 209 310 212 M 100 , MPa 2.9 3.2 3.4 2.3 2.2 2.9 Rebound, RT 57.5 53.4 57.8 62.3 57.2 63.1 Rebound, hot 67.2 69.7 67.9 68.6 72.3 70.2 Hardness, RT 62.5 67.1 65.8 60.5 61.2 61.9 Hardness, hot 61.7 64.8 65.0 59.2 59.4 61.7 DIN abrasion 216 205 208 274 243 240 EXAMPLE III Control rubber compounds containing solution polymerization prepared styrene/butadiene rubber (S-SBR) and natural rubber and reinforced with carbon black and calcium carbonate were prepared in a three-stage Banbury mix (Table 5) and referenced herein as Ctrl. L, M and N. Cure behavior and cured properties for these compounds are shown in Table 6. The compounds (rubber compositions) were cured at 150°C for 36 minutes. Compound L contains Si69 coupling agent, whereas Compound M also contains dithiodipropionic acid and Compound N also contains nicotinamide. Compounds M and N were observed to exhibit improved (increased) tensile strength at break and higher 300% modulus and hardness than Compound L. Ctrl. L Ctrl. M Ctrl. N 1 st Non-Productive S-SBR 50.0 50.0 50.0 Natural rubber 50.0 50.0 50.0 Carbon black 43.0 43.0 43.0 Antioxidant 2.2 2.2 2.2 Processing aids 5.5 5.5 5.5 Zinc oxide 3.5 3.5 3.5 Fatty acid 2.0 2.0 2.0 2 nd Non-Productive Calcium carbonate 17.0 17.0 17.0 Si69 Coupler (50%) 3.5 3.5 3.5 Dithiodipropionic acid 0 2.0 0 Nicotinamide 0 0 2.0 Productive Sulfenamide accelerator 1.0 1.0 1.0 Antioxidant 1.2 1.2 1.2 Sulfur 1.5 1.5 1.5 Diphenylguanidine 0.4 0.4 0.4 Compounds Ctrl. L Ctrl. M Ctrl. N Si69 3.5 3.5 3.5 Dithiodipropionic acid 0 2.0 0 Nicotinamide 0 0 2.0 Max torque 38.0 41.5 42.0 Min torque 5.0 5.0 5.5 T 90 , minutes 14.5 23.5 17.0 T 25 , minutes 6.5 7.3 4.3 Tensile strength, MPa 15.8 18.0 17.0 Elongation @ break, % 447 464 450 M 300 , MPa 10.2 11.6 11.1 Rebound, RT 52.4 53.3 49.7 Rebound, hot 67.4 66.5 65.7 Hardness, RT 56.9 61.7 59.8 Hardness, hot 55.0 58.4 57.2 DIN abrasion 151 148 150 EXAMPLE IV Rubber compounds containing emulsion polymerization prepared styrene/butadiene rubber (E-SBR), cis 1,4-polybutadiene rubber and, optionally, epoxidized natural rubber were prepared, similarly to Example I with carbon black reinforcement, optionally together with calcium carbonate and identified in Table 7 as Exp. S with Ctrls. P, Q and R being represented as a Control. 1 st Non-Productive Ctrl P Exp Q Exp R Exp S E-SBR 50 50 40 40 Polybutadiene 50 50 50 50 ENR 25 0 0 10 10 Carbon black 50 35 35 35 Calcium carbonate 0 15 15 15 Processing oil 5 5 5 5 Zinc oxide 5 5 5 5 Fatty acid 2 2 2 2 Antioxidant 2 2 2 2 Si69 Coupler (50%) 0 0 0 3 2 nd Non-Productive - 1 st Non-Productive mixed again without additional materials added. Productive Sulfenamide Accelerator 1.2 1.5 1.5 1.5 Diphenylguanidine 1.0 1.0 1.0 1.0 Sulfur 1.0 1.2 1.2 1.0 The rubber compositions were cured under conditions of elevated pressure and temperature (about 150°C) for 36 minutes. Physical properties for the rubber compositions are shown in the following Table 8. Ctrl P Ctrl Q Ctrl R Exp S ENR 0 0 10 10 Carbon black 50 35 35 35 CaCO 3 0 15 15 15 Si69 (50%) 0 0 0 3 Max. torque 42.2 40.4 41 42.4 Min. torque 8 6 6 6.3 T 90 , min. 17.5 18.5 14 17.5 T 25 , min. 12.3 13.8 10.3 10.8 Tensile strength, MPa 18.1 12.12 12.51 13.72 Elongation @ break, % 488 446 464 470 M 100 , MPa 2.24 1.89 1.98 2.07 M 300 , MPa 10.23 7.34 7.26 7.97 Rebound, RT 46.7 57.1 52.5 54.6 Rebound, hot 58.1 66.1 63.8 65.4 Hardness, RT 65.3 59.8 61.3 60.7 Hardness, hot 59.3 55.2 56.5 57.5 DIN abrasion 64 105 103 88 The DIN abrasion value (lower is better) for Exp. S, as compared to Ctrl P, indicates that the combination of epoxidized natural rubber and Si69 coupler, together with the calcium carbonate, is predictive of better (improved) treadwear for the rubber composition when used as a tire tread

Claims: A rubber composition characterized by comprising (A) 100 parts by weight of elastomer consisting essentially of a combination of diene-based elastomer and an epoxidized natural cis 1,4-polyisoprene rubber, (B) 15 to 45 phr of particulate reinforcement selected from carbon and/or precipitated silica, said silica having silanol groups on the surface thereof, (C) 5 to 50 phr of particulate calcium carbonate and (D) at least one modifier comprised of at least one of dithiodipropionic acid, nicotinamide and bis-3(trialkoxysilylalkyl) polysulfide having an average of from 2.1 to 4 sulfur atoms in its polysulfide bridge and where such alkyl groups contain from two to four carbon atoms. The composition of claim 1 characterized in that said elastomers are 5 to 30 phr of epoxidized diene-based elastomer as epoxidized natural rubber containing 20 to 50 percent epoxidization and 95 to 70 phr of said diene-based elastomer. The composition of any of the preceding claims characterized in that said diene-based rubber is comprised of at least one of cis 1,4-polyisoprene rubber, 3,4-polyisoprene rubber, styrene/butadiene copolymer rubbers, isoprene/butadiene copolymer rubbers, styrene/isoprene copolymer rubbers, styrene/isoprene/butadiene terpolymer rubbers, cis 1,4-polybutadiene rubber, trans 1,4-polybutadiene rubber (70-95 percent trans), low vinyl polybutadiene rubber (10-30 percent vinyl), medium vinyl polybutadiene rubber (30-50 percent vinyl), high vinyl polybutadiene rubber (50-90 percent vinyl) and emulsion polymerization prepared butadiene/acrylonitrile copolymers. The composition of any of the preceding claims characterized in that the composition is exclusive of silica and contains 15 to 30 phr of carbon black and in that the total of carbon black and calcium carbonate is 30 to 65 phr. The composition of any of the preceding claims 1 through 3 characterized by containing 13 to 35 phr of silica and 2 to 20 phr of said carbon black. The composition of any of the preceding claims characterized in that said carbon black is a combination of high reinforcing carbon black selected from N110 and N220 blacks and low reinforcing carbon blacks selected from N550 and N660 blacks with a proviso that 60 to 80 weight percent of the carbon black is the high reinforcing black. The composition of any of the preceding claims characterized in that said modifier is selected from at least one of dithiodipropionic acid, nicotinamide and a bis-3-(trialkoxysilylalkyl) polysulfide having an average of from 2.1 to 4 sulfur atoms in its polysulfidic bridge. The composition of any of the preceding claims 1-6 characterized in that said modifier is a bis-3(trialkoxysilylalkyl) polysulfide having an average of from 2.1 to 4 sulfur atoms in its polysulfidic bridge and said alkoxy groups are selected from methoxy and ethoxy groups and said alkyl groups are selected from ethyl, propyl and butyl groups. The composition of any of the preceding claims 1-6 characterized in that said modifier is a bis-3-(triethoxysilylpropyl) polysulfide having an average of 2.1 to 4 sulfur atoms in its polysulfidic bridge. A tire characterized by having a component of the composition of any of the preceding claims.

Inventors: SANDSTROM PAUL HARRY, SINSKY MARK SAMUEL, SANDSTROM, PAUL HARRY, SINSKY, MARK SAMUEL
Applicants: GOODYEAR TIRE & RUBBER, THE GOODYEAR TIRE & RUBBER COMPANY
Application year: 1999
Main classification: C08K3
IPC codes: B60C1, C08K5, C08K3, C08L9