MOLDED RESIN AND PROCESS FOR PRODUCING THE SAME

Abstract: A resin molded article having a contact angle of water of 50 degrees or less on its surface is produced by molding a thermoplastic or thermosetting resin composition containing a polymer having a perfluoroalkyl group of a (meth) acrylate having a perfluoroalkyl group and a (meth) acrylate having a hydrophilic group, or a compound having a perfluoroalkyl group which is obtained by reacting an epoxy compound having a perfluoroalkyl group with a polyalkylene oxide having a terminal hydroxyl group, and heating the molded article. The molded article has a hydrophilic surface and improved stain-proofing properties.

Description: FIELD OF THE INVENTION The present invention relates to a resin molded article and a method for producing the same. In particular, the present invention relates to a molded article of a thermoplastic or thermosetting resin having good surface hydrophilicity, which is produced by compounding a polymer or a compound having a perfluoroalkyl group in the thermoplastic or thermosetting resin, and molding the resin, and a method for producing such a molded article. The molded article of the present invention has particularly good stain-proofing properties, and thus can be used as a molded product which is severely stained such as kitchenware and bathroom ware. BACKGROUND ART In these years, the analysis of stains have been advanced from the viewpoint of the maintenance of the beauty and cleanliness of articles. Meanwhile, the function of "stain-proofing" has been sought in connection with buildings, structures, and further daily necessaries. In particular, surface treatment, which can impart a function for preventing the deposition of stains or a function for easily removing once deposited stains by washing to materials, has been sought. To improve the stain-proofing properties, it is known that it is effective to make the surface of a material hydrophilic (or to reduce the contact angle of water). For example, "KOBUNSHI" (POLYMERS), Vol. 44, page 307, May 1995 describes that the hydrophilic coating films have good stain-proofing properties in the field of exterior coating. To make the surfaces hydrophilic, in general, it is contemplated to "apply a compound which imparts hydrophilicity" to the surfaces. Apart from this, it is contemplated to "blend (internally add) a hydrophilic compound", when substrates are formed of resins. For example, in relation to the method to "apply a compound which imparts hydrophilicity", the invention of JP-A-62-196192 makes the surfaces hydrophilic with the application of a water-soluble composition containing an ethylene diamine derivative having a polyalkylene glycol group, polyvinyl alcohol a water-soluble melamine resin, etc. Furthermore, the method of JP-A-5-59203 makes a surface hydrophilic by applying a colloidal silica in an organic solvent as a dispersion medium and a surfactant to the surface and drying it. However, the method to "apply a compound which imparts hydrophilicity" has some drawbacks that it requires a further processing step of the once molded article and that the applied compound is easily removed by abrasion and so on and thus the hydrophilic effect disappears. Therefore, when the substrate is made of the resin, it is desirable that the hydrophilic effect can be imparted to the substrate by "blending a hydrophilic compound" from the viewpoint of the process steps and the practical application. As an organic compound which is compounded in the resin to impart the hydrophilicity, a compound having a polyoxyethylene group or polyvinyl alcohol is well known. When the commercially distributed polyoxyethylene compound is applied to the surface or kneaded in the resin, the surface may not have hydrophilic properties, or the hydrophilicity may be initially imparted to the surface but its durability is not good. WO-A-9815598 (US-B-6225405) discloses a water- and oil-repellent resin composition comprising 100 parts by weight of a thermoplastic resin or a thermosetting resin and 0.1-5 parts by weight of a perfluoroalkyl group-containing polymer which may be one or more of (1) a copolymer of a (meth)acrylic ester having a perfluoroalkyl group of 5-18 carbon atoms and a (meth)acrylic ester having a hydrophilic group, (2) a homopolymer of an epoxy compound having a perfluoroalkyl group of 5-18 carbon atoms, and (3) a copolymer of said epoxy compound and a monomer copolymerisable therewith. The monomers suggested for use in reacting with the epoxy compound are cyclic acid anhydrides, cyclic ethers, cyclic formals and cyclic epoxides. JP-A-7149923 discloses a plasticised polyvinyl chloride film for agriculture produced by adding 0.01 - 20 parts by weight of a fluorine compound consisting of carbon, hydrogen, oxygen and fluorine having a perfluoroalkyl group and a polyethylene glycol group to 100 parts by weight of a PVC resin. The film reportedly has improved anti-fog properties and is more rupture-resistant at lower temperatures than other films. DISCLOSURE OF THE INVENTION One object of the present invention is to provide an additive which can impart durable hydrophilicity to the surface of a resin by the internal addition of the additive, and a resin molded article having a hydrophilic surface. As a result of the extensive study, it has been found that a molded article of a thermoplastic or thermosetting resin having good hydrophilicity can be obtained by compounding a compound having a perfluoroalkyl group obtained by reacting an epoxy compound having a perfluoroalkyl group with a polyalkylene oxide having a terminal hydroxyl group in the resin, and molding the resin, and thus the present invention has been completed. According to a first aspect, the present invention provides a molded article of a resin composition comprising 100 wt. parts of a thermoplastic resin selected from the group consisting of polyethylene, polypropylene, polystyrene, acrylic resins, polyester, polycarbonate and polyamide or a thermosetting resin and 0.1 to 5 wt. parts of a compound having a perfluoroalkyl group which is obtained by reacting an epoxy compound having a C 5 -C 18 perfluoroalkyl group with a polyalkylene oxide having a terminal hydroxyl group, wherein a contact angle of water is 50 degrees or less on the surface of said molded article According to a second aspect, there is provided a method for producing a molded article having a contact angle of water of 50 degrees or less on its surface comprising the steps of: molding a resin composition comprising 100 wt. parts of a thermoplastic resin selected from the group consisting of polyethylene, polypropylene, polystyrene, acrylic resins, polyesters polycarbonate and polyamide, or a thermosetting resin and 0.1 to 5 wt. parts of a compound having a perfluoroalkyl group which is obtained by reacting an epoxy compound having a C 5 -C 18 perfluoroalkyl group with a polyalkylene oxide having a terminal hydroxyl group, and heating the molded article at a temperature in the range between 70°C and 130°C. DETAILED DESCRIPTION OF THE INVENTION The epoxy compound having a C 5 -C 18 perfluoroalkyl group to be used in the present invention is preferably an epoxy compound of the formula: wherein n is 0, 1 or 2, and Rf is a C 5 -C 18 perfluoroalkyl group. Specific examples of the above epoxy compound include and The polyalkylene oxide having a terminal hydroxyl group, which is reacted with the epoxy compound having a perfluoroalkyl group is preferably a compound of the formula: X-(CH 2 H 2 O) x -[CH(CH 3 )CH 2 O] y -Z wherein x and y are each 0 or a positive integer, for example, 1 to 30 provided that x and y are not zero at the same time and the values are consistent with the compound being a polyalkylene oxide , X is a C 1 -C 10 alkyl group, a C 1 -C 10 alkoxyl group, a hydroxyl group or a hydrogen atom, and Z is a C 1 -C 10 alkyl group or a hydrogen group provided that Z is a hydrogen atom when X is not a hydroxyl group. Specific examples of the above compound include HO-(CH 2 CH 2 O) k -H wherein k is 45 on the average, which has a number average molecular weight of about 2,000; wherein l:m is 1:1, which has a number average molecular weight of about 5,000; CH 3 O-(CH 2 CH 2 O) 8 -H; wherein a:b is 8:2, which has a number average molecular weight of about 8,000. The polyalkylene oxide having a terminal hydroxyl group may have a hydroxyl group at one end or hydroxyl groups at both ends. In the former case, one mole of the epoxy compound having a perfluoroalkyl group reacts with one mole of the polyalkylene oxide, while in the latter case, 2 moles of the epoxy compound having a perfluoroalkyl group reacts with one mole of the polyalkylene oxide. When the molecular weight of the reaction product of the polyalkylene oxide and the epoxy compound having a perfluoroalkyl group is small, the initial bleeding of the reaction product to the surface is enhanced, but the durability of the hydrophilicity deteriorates. When the molecular weight of the compound is large, the bleeding-out properties deteriorate so that the function of the reaction product to make the surface hydrophilic decreases. Accordingly, the number average molecular weight of the polyalkylene oxide used as a raw material is preferably from 1,000 to 60,000, particularly preferably from 1,000 to 10,000. The molecular weight of the reaction product can be easily adjusted by the selection of the raw materials, that is, the epoxy compound and the polyalkylene oxide having a terminal hydroxyl group. The reaction of the epoxy compound and the polyalkylene oxide having a terminal hydroxyl group is usually carried out in a solvent in the presence of a catalyst. The compound having a perfluoroalkyl group, which is prepared as described above, is added in an amount of 0.1 to 5 wt. parts to 100 wt. parts of the thermoplastic or thermosetting resin. When this amount is less than 0.1 wt. parts, the effect to make the surface hydrophilic is not sufficiently achieved. When it exceeds 5 wt. parts, the production cost of the molded article is disadvantageous. A more preferable amount is from 0.5 to 3 wt. parts per 100 wt. parts of the resin. The thermoplastic resin to be contained in the resin composition of the present invention may be any conventional thermoplastic resin. Examples of the thermoplastic resin include polyethylene, polypropylene, polystyrene, acrylic resins, polyesters, polycarbonate and polyamide. To blend the compound having a perfluoroalkyl group and the thermoplastic resin, any of a single-screw extruder, a twin-screw extruder, an open roll, a kneader or a mixer may be used. The thermoplastic resin composition of the present invention can be molded by any known method such as extrusion, injection molding, compression molding or filming to provide the molded article with hydrophilicity. The thermosetting resin to be contained in the resin composition of the present invention may be any conventional thermosetting resin. Examples of the thermosetting resin include epoxy resins, phenol resin, urea resins, melamine resins, alkyd resin, unsaturated polyester resins, diallyl phthalate resins, polyurethane and silicone resins. The compound having a perfluoroalkyl group and the thermosetting resin are directly mixed and blended prior to the molding of the thermosetting resin, that is, the addition of a curing agent. The thermosetting resin composition of the present invention can be molded by any known method such as injection molding (heating to cure), compression molding, transfer molding, etc. to provide the molded article with surface hydrophilicity. In the present invention, the molded article is further heated after molding to make the surface of the thermoplastic or thermosetting resin hydrophilic sufficiently. For example, the heat treatment is carried out by heating the molded article in an oven at a specific temperature. The heating temperature is usually from 70 to 130°C, preferably from 80 to 120°C. In addition to the compound having a perfluoroalkyl group, the resin composition of the present invention may contain known additives such as fillers, pigments, antistatic agents and antibiotics, in amounts such that the hydrophilicity is not deteriorated. Specific examples of the molded article are as follows: Bathroom wares (e.g. bathtubs, interior parts of set-in bath, washbasin, tubs, soap dishes, shampoo racks and chairs); Kitchen wares (e.g. baking sheets, kitchen sinks, washing tubs, tidies, drain baskets and detergent racks); Toilet wares (e.g. toilet seats, paper holders, toilet corner tidies, reservoirs, towel rails, toilet brushes and cases of toilet brushes); Hygienic and care goods (e.g. portable toilets, bedpans and hand rails); Wash goods (e.g. toothpaste tube racks, tooth mugs, trays, towel rails and mirror tables); Sanitary goods (e.g. buckets, compost bins, tubs and ash bins); Storage goods (e.g. dress cases, racks with casters and coat racks); Baby goods (e.g. chamber pots, baby toilet seats, stools and containers of feeding bottles). EXAMPLES The present invention will be illustrated by the following Examples, which do not limit the scope of the invention in any way. Reference Example 1 Preparation of a compound having a perfluoroalkyl group The following polyethylene glycol having terminal hydroxyl groups (3) (number average molecular weight: 2,000) (404 g), chloroform (1.3 liters) and BF 3 ether (10 ml) were charged in a 2 liter glass reactor and heated up to 70°C on an oil bath to reflux chloroform. To the mixture, the following epoxy compound having a perfluoroalkyl group (4) (244 g) was dropwise added, and reacted for 5 hours while heating and stirring. After the disappearance of the peaks assigned to the epoxy compound (4) was confirmed with gas chromatography, the reaction, was terminated. After the termination of the reaction, chloroform was recovered with a rotary evaporator. The obtained compound was solid at room temperature. (3) HOCH 2 -(OCH 2 CH 2 ) r -OCH 2 OH (number average molecular weight: 2,000); Reference Example 2 Preparation of a compound having a perfluoroalkyl group The polyethylene glycol (3) (404 g), chloroform (1.3 liters) and BF 3 ether (10 ml) were charged in a 2 liter glass reactor and heated up to 70°C on an oil bath to reflux chloroform. To the mixture, the following epoxy compound having a perfluoroalkyl group (5) (212 g) was dropwise added, and reacted for 5 hours while heating and stirring. After the disappearance of the peaks assigned to the epoxy compound (5) was confirmed with gas chromatography, the reaction was terminated. After the termination of the reaction, chloroform was recovered with a rotary evaporator. The obtained compound was solid at room temperature. Example 1 The compound having a perfluoroalkyl group prepared.in Reference Example 1 (1 wt. part) was added to polypropylene (K1016 manufactured by NIPPON TISSO) (100 wt. parts), and melt blended at 180°C with a twin-screw extruder. Then, the resin composition was press molded to obtain a sheet-form molded article (20 cm x 20 cm x 2 mm), and the molded article was heated at 100°C for 1 hour. Example 2 A molded article was produced in the same manner as in Example 1 except that 1 wt. part of the compound having a perfluoroalkyl group prepared in Reference Example 2 was used in place of the compound having a perfluoroalkyl group prepared in Reference Example 1. Example 3 A molded article was produced in the same manner as in Example 1 except that 1 wt. part of the compound having a perfluoroalkyl group prepared in Reference Example 1 was added to 100 wt. parts of polyethylene (M-6454 manufactured by ASAHIKASEI SUNTEC). Example 4 The compound having a perfluoroalkyl group prepared in Reference Example 1 (1 wt. part) was added to an unsaturated polyester resin (AP 301B manufactured by TOSHIBA CHEMICAL) (100 wt. parts) and well kneaded to uniformly disperse the compound in the resin. Then, the resin composition was molded in a mold at a mold temperature of 145°C for a curing time of 3 hours to obtain a round sheet-form test piece having a diameter of 8 cm and a thickness of 2 mm. Then, the test piece was heated at 100°C for 1 hour. Comparative Example 1 A molded article was produced in the same manner as in Example 1 except that no compound having a perfluoroalkyl group was used. A contact angle of water against each of the molded articles obtained in Examples and Comparative Examples was measured by a droplet method with a contact angle meter (Type CA-DT A manufactured by KYOWA INTERFACE SCIENCE KABUSHIKIKAISHA). The results are shown in Table 1. Example No. Contact angle of water (degrees) 1 31 2 28 3 30 4 28 C. 1 102

Claims: A molded article of a resin composition comprising 100 wt. parts of a thermoplastic resin selected from the group consisting of polyethylene, polypropylene, polystyrene, acrylic resins, polyester, polycarbonate and polyamide, or a thermosetting resin and 0.1 to 5 wt. parts of a compound having a perfluoroalkyl group which is obtained by reacting an epoxy compound having a C 5 -C 18 perfluoroalkyl group with a polyalkylene oxide having a terminal hydroxyl group, wherein a contact angle of water is 50 degrees or less on the surface of said molded article. A method for producing a molded article having a contact angle of water of 50 degrees or less on its surface comprising the steps of: molding a resin composition comprising 100 wt. parts of a thermoplastic resin selected from the group consisting of polyethylene, polypropylene, polystyrene, acrylic resins, polyester, polycarbonate and polyamide, or a thermosetting resin and 0.1 to 5 wt. parts of a compound having a perfluoroalkyl group which is obtained by reacting an epoxy compound having a C 5 -C 18 perfluoroalkyl group with a polyalkylene oxide having a terminal hydroxyl group, and heating the molded article at a temperature in the range between 70°C and 130°C.

Inventors: HONDA YOSHITAKA, YAMAGUCHI FUMIHIKO, HONDA, YOSHITAKA, YAMAGUCHI, FUMIHIKO
Applicants: DAIKIN IND LTD, DAIKIN INDUSTRIES, LTD.
Application year: 1999
Main classification: C08L101
IPC codes: C08J7, C08G65, C08L71, C08L63, C08L101, C08J5