METHOD AND APPARATUS FOR THE DIRECT REDUCTION OF IRON OXIDES

Abstract: Method for the direct reduction of mineral iron inside a vertical reduction furnace (10) of the type with a gravitational load, wherein the reduction gas flows in counter-flow with respect to the material introduced into the furnace, comprising the following steps: the mineral iron is fed from above into the furnace (10), a mixture of high temperature gas consisting of reducing gas based on H2 and CO is injected, and the reduced mineral is removed from the furnace (10), the mixture of gas being introduced in at least two zones (12, 14) of the furnace (10) arranged one above the other so as to achieve, in a controlled manner, a first stage of pre-heating and pre-reduction in the upper part (12) of the furnace (10) and a second stage of final reduction in the lower part (14) of the furnace (10). An apparatus comprising the features to conduct the process as described herewith, is claimed as well.

Description: METHOD AND APPARATUS FOR THE DIRECT REDUCTION OF IRON OXIDES FIELD OF THE INVENTION This invention concerns a process to produce metallic iron starting from mineral iron, wherein the iron is present in the form of oxides, and the relative apparatus which comprises a reduction furnace with multiple inlets for the reducing gas and inside which the process of direct reduction of the iron (DRI) is carried out. The reduced iron may exit from the reduction furnace either hot or cold and may be subsequently sent to a melting furnace to produce liquid steel, or converted into hot briquette steel (HBI) . BACKGROUND OF THE INVENTION The state of the art includes processes of direct reduction which use the injection of hydrocarbons into the current of reducing gas to allow the reaction of reforming the methane in the furnace with the H 2 O and CO 2 in the gas; there are also known processes of direct reduction which use the injection of hydrocarbons with C>5 directly into the furnace in the zone between the injection of the reducing gas and the outlet from above of the burnt gas . From the following patent documents other processes are known for the direct reduction of mineral iron: US-A-2,189,260, US-A-3 , 601, 381, US-A-3 , 748 , 120 , US-A-3,749,386, US-A-3 , 764, 123 , US-A-3 , 770 , 421, US-A-4,054,444, US-A-4, 173 , 465, US-A-4, 188, 022 , US-A-4,234,169, US-A-4, 201, 571, US-A-4, 270 , 739 , US-A-4, 374, 585, US-A-4, 528, 030 , US-A-4, 556, 417 , US-A-4, 720,299, US-A-4, 900, 356, US-A-5, 064 , 467 , US-A-5,078,788, US-A-5 , 387 , 274, and US-A-5 , 407 , 460. The state of the art also includes processes wherein the hot metallic iron is produced in a reduction furnace of the shaft type, with a vertical and gravitational flow of the material, which is subsequently sent to the melting furnace by means of a closed pneumatic transport system in an inert atmosphere . SUMMARY OF THE INVENTION The method to produce metallic iron by the direct reduction of iron oxides and the relative apparatus according to the invention are set forth and characterised in the respective main claims, while the dependent claims describe other innovative features of the invention. The method according to the invention consists in bringing into contact the mineral iron, of various granulometry, with a feed gas in a reduction furnace of the shaft type, wherein both the gas and the material are fed continuously, so that a vertical and gravitational flow of material is created and the direct reduction of the mineral is achieved. The material may be discharged from the reactor either cold or preferably hot to be sent subsequently to a melting furnace or so that it may be converted into hot briquette iron (HBI) or cooled and converted into direct reduction iron (DRI) . The reduction furnace is equipped with means to feed the mineral iron and means to discharge the reduced metallic iron; it is equipped with at least two inlet collectors to inject the reducing gas in correspondence with different reduction zones inside the furnace to ensure a greater reduction zone. The reduction gas sent into the reactor contains hydrocarbons injected into the current after the partial combustion of the hydrogen and carbon monoxide with the oxygen. In a variant, the hydrocarbons are injected before the partial combustion is achieved, with the purpose of raising the temperature of the gas introduced into the reactor. According to another variant, the hydrocarbons are at least partly injected into a zone between the reduction zone and the zone where the reduced material is discharged. In all cases, the injected hydrocarbons cooperate in reducing the iron oxide (FeO) to metallic iron, generating more H 2 and CO . The direct reduction of the iron oxides is achieved in two different continuous stages inside the reduction reactor. In a first stage, defined as the pre-heating and pre- reduction stage, the fresh iron oxides, that is, those just introduced into the furnace, come into contact with a mixture of reduction gas, consisting of partly burnt gas, arriving from the underlying part of the furnace and of fresh hot gas, that is, gas introduced from outside, arriving from a collector which brings fresh reducing gas and possibly CH 4 or other natural gas. This first stage takes place in a corresponding first zone arranged in the upper part of the furnace. In the second stage, or real reduction stage, the complete reduction of the iron oxides is achieved, due to the action on the oxides, already partly reduced in the first stage, of a mixture of reducing gas based on H 2 and CO and at least a hydrocarbon, preferably natural gas, injected in the median zone of the reduction reactor. This second stage takes place in a corresponding second zone arranged below the first zone. The two inlets to the furnace, through which the gas is introduced, can be independently regulated both in the flow of fresh reducing gas and in the addition of natural gas in the current introduced. Moreover, the inlet temperature of the two currents of reducing gas can be independently regulated by injecting O 2 before they enter the reduction reactor. The oxidation reaction needed to raise the temperature of the gas leads to a change in the level of oxidation of the gas, from normal values of 0.04-0.08 to 0.06-0.15. The following ratio is intended for the level of oxidation of the reducing gas: Nox = (H 2 0+C0 ) / (H 2 0+CO 2 +H 2 +C0) In the second reaction zone of the furnace, wherein the reduction of the iron oxides is completed, a gas is generated with a high content of H 2 and CO and with an oxidation level of between 0.15 and 0.25 due to the reduction reactions of the iron oxides with H 2 , CO and CH 4 . Once this gas has left the second reaction zone, it enters the first reaction zone, located higher up, and mixes with the hot gas injected into the first zone to pre-heat and pre-reduce the iron oxides. The gas emerging from the reduction reactor is partly recircled and partly used as fuel. The recircled gas has a volume composition within the following fields: H 2 =20-41%, CO=15-28%, C0 2 =15-25%, CH =3-10%, N 2 =0-8%, H 2 0=2-7%. According to one characteristic of the invention, the gas feeding the reduction reactor consists of a mixture of natural gas, recircled gas from the reactor itself and reformed gas; the recircled gas is pre-heated to a temperature of between 650°C and 950°C; the gas emerging from the pre-heater is in turn mixed with fresh reformed gas and subsequently with air, or air enriched with oxygen, or pure oxygen, to carry out a partial combustion of the H 2 and CO in the reducing gas in order to raise the temperature to values of between 800°C and 1150°C, preferably between 1000°C and 1150°C; and the oxidation level of the resulting gas feeding the furnace is between 0.06 and 0.15. The methane represents between 6 and 20% in volume of the mixture of reducing gas . When the feed gas comes into contact in the reduction zone with the hot, partly reduced material, which therefore consists partly of metallic iron and partly of iron oxides, a highly endothermic reaction is produced. There is a also an endothermic reaction in the pre-heating and pre-reducing zone when the gas comes into contact with the iron oxide . One advantage of this invention is that the first preheating and pre-red cing zone is extended, which allows to start the transformation of the Ematite (Fe 2 θ 3 ) into Wustite (FeO) more quickly. The whole reactor works at a higher average temperature and above all which is constant along both zones, both the pre-reduction and reduction zones, encouraging a higher reaction speed, with a consequent effect of reducing consumption and increasing productivity. The first inlet for the reducing gas is located at a set distance (x) with respect to the second inlet, which is located in the median part of the furnace, in correspondence with the second reduction zone. This distance (x) is suitably included between 1 and 6 meters, preferably between 2 and 4 metres, to_ encourage the reactions in the most suitable zone between the reducing gas and the iron oxides. The first gas inlet also has the function of pushing the gases arriving from the second reduction zone towards the centre of the furnace so as to create a uniform distribution of the gas in the section of the reactor. According to a variant, there are multiple inlets for the reducing gas into the furnace, or more than two. The first current of reducing gas is injected into the middle of the reactor, into the reduction zone proper, while the other currents are introduced into the zone between the injection of the first current of gas and the outlet of the burnt gas, in the upper part o ' f the furnace. This intermediate zone will be called the pre-heating and pre-reducing zone for the iron oxide based material . The flow of gas into the reactor thus composed allows to have the whole reduction and pre-reduction zone at as constant a temperature as possible, and to have a gas inside the furnace which always has a high reducing power, encouraging a greater productivity and a lower consumption of gas; this also allows to improve the final metalisation of the product. In this way, moreover, the iron oxides arrive at the reduction zone already partly reduced, thus encouraging the completion of the final reduction reaction from FeO to Fe. BRIEF DESCRIPTION OF THE DRAWINGS These and other characteristics of the invention will become clear from the following description of a preferred form of embodiment, given as a non-restrictive example with the aid of the attached Figures wherein: Fig. 1 shows in diagram form an apparatus for the direct reduction of iron oxides according to the invention; Fig. 2 is a first variant of a furnace employed in the apparatus in Fig. 1; Fig. 3 is a diagram showing the temperature inside the furnace shown in Figs . 1 and 2 ; Fig. 4 shows a second variant of a furnace employed in the apparatus in Fig . 1 ; Fig. 5 is a diagram showing the temperature inside the furnace shown ' in Fig. 4; and Fig. 6 shows another variant of the apparatus in Fig. 1. DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS With reference to Fig. 1, an apparatus for the direct reduction of iron oxides according to the invention comprises a reduction furnace of the shaft type or reduction reactor 10, comprising in turn an upper mouth 11 for feeding from above, through which the mineral (iron oxides) is able to be introduced, a first pre-heating and pre-reduction zone 12, a second zone, or median zone 14 wherein the final reduction reaction of the iron oxides takes place, and a lower zone, or discharge zone 15, shaped like a truncated cone, terminating at the bottom in a lower aperture 16 through which the iron is discharged. The iron-based metal oxides are introduced into the reactor 10 in the form of pellets or crude mineral in the appropriate sizes; the iron contained therein is usually between 63% and 68% in weight. At the end of the process according to the invention, the iron contained in the reduced material exiting from the reactor 10 is normally between 80% and 90% in weight. In correspondence with the two zones 12 and 14 of the reactor 10 there are two independent inlets 17, respectively 18, through which a mixture of gas is suitable to be introduced, as will be described in greater detail hereafter. In its upper part, above zone 12, the reactor 10 is provided with an aperture 19 through which the burnt gas exits. This gas normally has the following characteristics: composition: H 2 =20-41%, CO=15-28%, C0 =12-25%, CH =2-10%, N 2 =0-8%, H 2 0=2-15%; temperature between 500°C and 700°C; oxidation level between 0.3 and 0.50, preferably between 0.40 and 0.45; and a reduction ratio R of between 1 and 1.8 where reduction ratio is taken as: R= (H 2 +CO)/(H 2 0+C0 2 ) • The burnt gas emerging from the reactor 10 is sent through a pipe 20 to a cooling unit 21, suitable to recover the heat which can be given up; from the cooling unit 21, through another pipe 22, it arrives at a cooling and condensing unit 24. In this unit 24 the burnt gas is washed in water at a temperature of between 40°C and 65°C and the quantity of water present in the gas itself is partly removed. The percentage of water remaining in the gas at outlet from the unit 24 is between 2% and 7%. The gas at outlet from the unit 24 is sent through a pipe 30 partly to a pre-heater 36, partly to a catalytic reformer 44, to be used as fuel, and partly to a compressor 26. The gas emerging from the compressor 26 is in turn used partly as a recircling gas and sent, through a pipe 28, inside the unit 21, and partly, through a pipe 46, mixed with a natural gas comprising methane (CH 4 ), or pure methane, arriving from a pipe 34 in a proportion of about 4:1 (that is to say, for every part of natural gas there are about four parts of gas arriving from the pipe 46) and introduced into the reformer 44 so that the reforming reaction of the methane (CH 4 ) with H 2 O and CO 2 can begin. The part of gas which is sent to the unit 21 through the pipe 28 is pre-heated, and is then sent through a pipe 32 to the pre-heater 36, where it is further pre-heated to a temperature of between 650°C and 950°C. CH 4 may also be injected into the pipe 32. The gas emerging from the pre-heater 36, which has a delivery rate of between 600 Nm 3 /ton DRI and 1500 Nm 3 /ton DRI, is mixed in a pipe 38 with the gas arriving from the reformer 44 through a pipe 50. The gas resulting from this mixture is divided into two parts and distributed into two pipes 40 and 41, connected to the inlets 17 and 18 of the furnace 10. The delivery of reducing gas is controlled in each zone 12, 14 by means of regulation valves 55 and 56. Into each pipe 40 and 41 air is injected, or air enriched with oxygen or pure oxygen and natural gas in variable percentages, in order to achieve a partial combustion of the CO and the H 2 and raise the temperature of the gas. A current of CH 4 or natural gas is injected into the gas before it is introduced into the reactor. In a variant, shown by a line of dashes in Fig. 1, the CH 4 is injected before achieving the partial combustion, with the purpose of raising the temperature of the gas introduced into the reactor. The CH 4 may also be introduced in a zone between the reduction zone 14 and the discharge cone of the material, through a pipe 81. In this case, before entering into the zone 14 where the reduction reactions are carried out, the CH 4 injected partially cools the reduced iron, before the latter is discharged. Valves Vl-Vll are located in correspondence with the different conduits of the plant so that the flow can be selectively controlled. The resulting mixtures are introduced into the pre-heating and pre-reduction zone 12 and respectively into the reduction zone 14. Therefore, for each zone 12 and 14 the corresponding mixture of gas is regulated in an autonomous and independent manner . To be more exact, the flow of gas in the first zone 12 is between 500 NmVton DRI and 800 Nm 3 /ton DRI and enters the reduction reactor 10 with a temperature of between 800°C and 1150°C, preferably between 1000°C and 1150°C, while the flow of gas in the second zone 14 is between 1000 Nm 3 /ton DRI and 1500 Nm 3 /ton DRI and also enters the reduction reactor 10 with a temperature of between 800°C and 1150°C, preferably between 1000°C and U50°C. The consumption of oxygen, which is necessary to raise the temperature of the reducing gas from 650°C-950°C to 800°C- 1150°C, intended as pure oxygen plus that contained in the air, if air is also injected, is between 8 Nm 3 /ton DRI and 60 Nm 3 /ton DRI, preferably between 20 and 60 Nm 3 /ton DRI. The consumption of CH 4 is between 50 and 120 Nm 3 /ton DRI, preferably between 90 and 110 Nm 3 /ton DRI. In volume the CH 4 represents between 6 and 20% of the mixture of reducing gas introduced into the reactor. The reactions involved in the reduction zone 14 are as follows; FeO + CH = Fe + 2H 2 + CO (1) Simultaneously, in the same zone 14, the following reduction reactions take place with hydrogen and carbon monoxide : FeO + H 2 = Fe + H 2 0 (2) FeO + CO = Fe + C0 2 (3) The consequence of these endothermic reactions is that the temperature of the gas in the reduction zone decreases from 800°C-1150°C to 700°C-900°C, yet still maintains the reaction temperature higher than in furnaces in the state of the art, and the gas leaving the reduction zone 14 has an oxidation level of between 0.15 and 0.35 and a reducing power of between 1.1 and 2.8. The reactions involved in the pre-reduction zone 12 are as follows: Fe 2 0 3 + H 2 = 2FeO + H 2 0 (4) Fe 2 0 3 + CO = 2FeO + C0 2 (5) In the lower zone 15, shaped like a truncated cone, it is also possible to introduce gas containing natural gas to control the final carbon in the hot reduced iron to values of between 1.5% and 3.0%. In a first variant as shown in Fig. 2, instead of having a single lower part shaped like a truncated cone, the furnace 10 has at least two, and preferably three or four lower ends, shaped like a cone or truncated cone 15a, 15b and 15c, through which the reduced metallic iron is discharged in a controlled and independent manner. In this case the CH 4 may also be introduced by means of devices located on the zone of intersection of the truncated cone ends 15a, 15b and 15c, thus exploiting the geometric conformation of the system. The development of the temperature inside the furnace 10, both in the version shown in Fig. 1 and also in the variant shown in Fig. 2, is shown in Fig. 3, from which it can be seen how the temperature is higher and more constant in the segment affected by the two zones 12 and 14. According to a second variant shown in Fig. 4, instead of having two inlets to introduce reducing gas, the furnace 10 is provided with a plurality of inlets, more than two. In this case a first current of gas is introduced into the lower inlet 18 through the pipe 41, a second current of gas is introduced into the inlet 17 through the pipe 40 and other currents of gas, each of which can be autonomously regulated, are introduced through pipes 42 and corresponding inlets 43 arranged between the inlet 17 and the upper aperture 19. The development of the temperature inside the furnace 10, in the variant shown in Fig. 4, is shown in the diagram in Fig. 5, from which it can be seen how the temperature is higher and more constant in the whole segment affected by the pipes 40, 41 and 42. According to another variant, shown in Fig. 6, the reducing processing gas may be recircled without passing through a catalytic reformer, but a part of the gas exiting from the reduction furnace 10 is pre-heated in the exchanger 21 and, by means of the pipe 32, mixed with natural gas, for example CH 4 , and sent to the pre-heater 36. In this variant, the gas exiting the furnace 10 has a temperature of between 500°C and 600°C and has the following composition: H 2 =30-36%, CO=20-25%, CO 2 =20-25%, CH 4 =2-7%, H 2 θ=15-25%; with an oxidation level of between 0.4 and 0.5. The gas, thus pre-heated and mixed with natural gas, exits the pre-heater 36 at a temperature of between 650°C and 950°C, it is subsequently divided into several currents of reducing gas, into each of which oxygen and natural gas are injected before they enter the reduction furnace 10, so as to raise the temperature of the inlet gases to a value of between 800°C and 1150°C. Another part of the gas exiting the reduction furnace 10 is used as fuel to generate heat in the pre-heater 36, by means of the pipe 30. The reactions which take place in the reduction furnace 10 are to pre-heat and pre-reduce the mineral in the upper zone 12 and to reduce the Wustite (FeO) with CH 4 , H 2 and CO in the reduction zone 14. In a variant, CH 4 may be injected into the zone between the reduction zone 14 and the truncated-cone-shaped discharge end 15; in this way the CH 4 is pre-heated, cools the reduced material, and arrives in the reduction zone 14 cooperating with the methane contained in the reduction gas injected in the reaction zone 14. With this system it is possible to eliminate the catalytic reformer 44, and at the same time the plurality of gas inlets allows to improve the profile of the temperature of the reduction furnace 10, making it more uniform and accelerating the reduction reactions . Obviously, it is possible to make modifications and additions to the method for direct reduction of mineral iron and the relative apparatus as described heretofore, but these will remain within the field and scope of the invention.

Claims: CLAIMS 1 - Method for the direct reduction of mineral iron inside a vertical reduction furnace (10) of the type with a gravitational load, wherein the reduction gas flows in counter-flow with respect to the material introduced into the furnace, comprising the following steps: the iron is fed from above into the furnace (10), a mixture of high temperature gas consisting of reducing gas based on H 2 and CO is injected, and the reduced mineral is removed from said furnace (10), the method being characterised in that said mixture of gas contains at least a hydrocarbon and is introduced in at least two zones (12, 14) of said furnace (10) arranged one above the other so as to achieve, in a controlled manner, a first stage of pre-heating and pre- reduction in the upper part (12) of said furnace and a second stage of final reduction in the lower part (14) of said furnace (10) . 2 - Method as in Claim 1, characterised in that said hydrocarbon consists of methane and in that said methane represents between 6 and 20% in volume of said mixture of gas . 3 - Method as in Claim 1, characterised in that the delivery, in different percentages, of said mixture of gas is controlled in the different zones (12, 14) along the length of said furnace (10) in which it is injected. 4 - Method as in Claim 1, characterised in that said hydrocarbon consists preferably of natural gas and in that said hydrocarbon in said mixture of gas is proportioned and controlled independently in the different zones (12, 14) along the length of said furnace (10) in which it is injected. 5 - Method as in any claim hereinbefore, characterised in that the mixture of gas, before being injected into said furnace (10), is heated to a temperature of between 800°C and 1150°C, advantageously between 1000 and 1150°C. 6 - Method as in any claim hereinbefore, characterised in that said mixture of gas is heated independently in the different zones (12, 14) along the length of said furnace (10) . 7 - Method as in Claim 4 or 5 , characterised in that said mixture of gas is heated by making it partly interact with o 2 . 8 - Method as in any claim hereinbefore, characterised in that said reducing gas consists of a mixture consisting in a variable and controlled percentage of process gases arriving from a reactor, suitably treated and heated to a temperature of between 650°C and 950°C, and of gases arriving from outside processes. 9 - Method as in any claim from 1 to 7 inclusive, characterised in that said mixture of gas consists exclusively of suitably treated process gas and of hydrocarbons, preferably natural gas or CH 4 , the mixture being pre-heated to a temperature of between 650°C and 950°C. 10 - Method as in any claim from 1 to 7 inclusive, characterised in that said reducing gas consists of a mixture consisting in a variable and controlled percentage of process gases arriving from a reactor, suitably treated and heated to a temperature of between 650°C and 950°C, and of gas arriving from an outside catalytic reformer. 11 - Method as in Claim 8, 9 or 10, characterised in that the mixture of gas injected into said reactor has an oxidation level of between 0.06 and 0.25. 12 - Method as in any claim hereinbefore, characterised in that further CH 4 is partly injected into said furnace (10) in a zone between said lower part (14) and an underlying discharge zone (15) . 13 - Apparatus for the direct reduction of mineral iron comprising a vertical reduction furnace (10) of the type with a gravitational load to achieve therein reactions of reduction of the iron mineral, means (11) to feed the mineral iron into said furnace (10) from above, means to raise the temperature of a reducing gas, mixing means suitable to obtain a mixture of said reducing gas with at least a hydrocarbon means to inject said mixture of high temperature gas, and means to remove (15) the reduced mineral from the lower part of said furnace (10) , characterised in that said furnace (10) is provided with at least two zones (12, 14), arranged vertically distanced, into each of which said mixture of high temperature gas is suitable to be introduced so as to achieve the reduction reactions in a controlled manner, and in that at least an element to mix said reducing gas with at least a hydrocarbon is provided upstream of at least one of the inlets to said furnace (10) in correspondence with at least one of said zones (12, 14), to supply a mixture wherein the hydrocarbon is proportioned and controlled in an independent and autonomous manner in at least one of said zones (12, 14) , and in that means to heat said reducing gas are provided upstream of said mixing element to cause said mixture of gas to be heated. 14 - Apparatus as in Claim 13, characterised in that means to control the delivery (55, 56) of said mixture of high temperature gas are provided in correspondence with said zones (12, 14) . 15 - Apparatus as in Claim 13 or 14, characterised in that at least two elements to mix the reducing gas and hydrocarbon are provided upstream of the inlets to said furnace (10) in correspondence with said zones (12, 14), in order to supply a . mixture wherein the hydrocarbon is proportioned and controlled independently and autonomously in each of said zones (12, 14) . 16 - Apparatus as in Claim 15, characterised in that means to heat said reducing gas are suitable to heat the mixture of gas to a temperature of between 800°C and 1150°C, advantageously between 1000 and 1150°C. 17 - Apparatus as in Claim 16, characterised in that regulation means are associated to said heating means to regulate each of said heating means in an independent manner . 18 - Apparatus as in Claim 16 or 17, characterised in that said heating means consist of devices wherein said reducing gas is made to partly react with O 2 before being sent to said mixing means . 19 - Apparatus as in any claim from 13 to 18 inclusive, characterised in that said reducing gas consists of a mixture consisting in a variable and controlled percentage of process gases arriving from said furnace (10), suitably treated and heated to a temperature of between 650°C and 950°C and of gases arriving from outside processes. 20 - Apparatus as in any claim from 13 to 19 inclusive, characterised in that said mixture of gas consists exclusively of suitably treated process gas and of hydrocarbons, preferably natural gas or CH 4 , the mixture being pre-heated to a temperature of between 650°C and 950°C and subsequently sent to means to mix it with O 2 or O 2 - enriched air in order to raise the temperature to a value of between 800°C and 1150°C before being injected into said furnace (10) . 21 - Apparatus as in any claim from 13 to 19 inclusive, characterised in that said reducing gas consists of a mixture consisting in a variable and controlled percentage of process gases arriving from said furnace (10), suitably treated and heated to a temperature of between 650°C and 950°C and of gas arriving from an outside catalytic reformer. 22 - Apparatus as in any claim from 13 to 21 inclusive, characterised in that said removal means (15) comprise at least two ends (15a-15c) shaped like a cone or a truncated cone. 23 - Apparatus as in Claim 22, characterised in that said ends (15a-15c) shaped like a cone or a truncated cone taper downwards and each is provided with a corresponding lower aperture (16a-16c) through which said reduced metallic iron can be selectively discharged in a controlled and independent manner. 24 - Apparatus as in any claim from 13 to 23 inclusive, characterised in that injection means (81) are suitable to inject at least partly CH 4 into said furnace (10) in a zone between said removal means (15) and the lower of said zones (14) . 25 - Apparatus as in. Claims 22 and 24, characterised in that said injection means (81) are arranged in a zone of intersection between said ends (15a-15c) shaped like a cone or a truncated cone .

Inventors: BENEDETTI GIANPIETRO, BUENO HENRY RAFAEL, RABASCALL DAVID, BENEDETTI, GIANPIETRO, BUENO, HENRY, RAFAEL, RABASCALL, DAVID
Applicants: DANIELI OFF MECC, DANIELI & C. OFFICINE MECCANICHE SPA
Application year: 1999
Main classification: C21B13
IPC codes: C21B13