Production of polyethylene

Abstract: A process for producing a linear low density polyethylene resin, the process comprising copolymerising ethylene and a comonomer comprising at least one alpha-olefin having from 3 to 8 carbon atoms in the presence of a chromium-based catalyst to make polyethylene copolymer in a first polymerisation reactor and in a second polymerisation reactor downstream of the first polymerisation reactor copolymerising ethylene in the presence of the chromium-based catalyst and a co-catalyst from ethylene monomer, a comonomer which has been fed into the second polymerisation reactor and comprises at least one alpha-olefin having from 3 to 8 carbon atoms and comonomer generated in-situ in the second polymerisation reactor to make polyethylene copolymer.

Description: The present invention relates to a process for producing polyethylene, in particular linear low density polyethylene (LLDPE) having improved mechanical properties. Polyethylene is known for use in the manufacture of a wide variety of articles. The polyethylene polymerisation process can be varied in a number of respects to produce a wide variety of resultant polyethylene resins having different physical properties which render the various resins suitable for use in different applications. In particular, it is known to use polyethylene for use in applications where the polyethylene is required to have crack resistance, both resistance to rapid and to slow crack growth. For example, polyethylene is known for use in the manufacture of pipes where it is required that the material of the pipe has sufficient crack resistance so as to avoid inadvertent fracture in service. Polyethylene is also known for use in the manufacture of blow moulded articles where a high environmental stress cracking resistance (ESCR) is required. Chromium-based catalysts used for the production of polyethylene have been known for some time. It is known in the art that the physical properties, in particular the mechanical properties, of a polyethylene product can vary depending on what catalytic system was employed to make the polyethylene. This is because different catalyst systems tend to yield different molecular weight distributions in the polyethylene produced. It is further known in the art that the mechanical properties of a polyethylene resin, for example the ESCR for blow moulding resins, the impact resistance for film forming resins, and slow crack growth resistance for pipe forming resins, tend to be better when the high molecular weight fraction of the polyethylene is copolymerised. US-A-5208309 discloses the manufacture of linear very low density polyethylene in which a copolymer of ethylene and a higher alpha-olefin is produced using an activated and subsequently carbon monoxide reduced chromium containing catalyst system and an alkyl aluminium or alkyl boron co-catalyst. The specification states that in the process disclosed therein, it is believed that additional comonomers, i.e. in addition to those added to the polymerisation reactor, can be generated in-situ in the polymerisation reactor or in the reaction zone. Such comonomer is incorporated into the copolymer. EP-A-0307907 discloses a process for olefin polymerisation in which in-situ comonomer production is employed using a carbon monoxide reduced polymerisation catalyst system. The addition of hydrogen to the reactor enables the regulation and control of the characteristics of the resultant polymer. The processes disclosed in those two patent specifications suffer from the disadvantage that the resultant polymer does not have particular broad molecular weight distribution or a particularly high shear response (SR), the shear response being the ratio of the high load melt index (HLMI) and the melt index (MI 2 ). EP-A-0832905 discloses a process for preparing polyethylene having a large molecular weight distribution employing two reactors in series and in which a polyethylene homopolymer is produced in the first reactor and a polyethylene copolymer with 1-hexene is produced in the second reactor by the addition of 1-hexene into the second reactor. EP-A-0739909 discloses the production of ethylene polymers using, for example, a single reactor having two separated stages simulating two reactors in series. The first polymer is a copolymer of ethylene with hexene and the second polymer is produced by additionally adding hydrogen into the reactor. The present invention aims in one aspect to provide a process for producing polyethylene having improved mechanical properties. Accordingly, the present invention provides a process for producing a linear low density polyethylene resin, the process comprising copolymerising ethylene and a comonomer comprising at least one alpha-olefin having from 3 to 8 carbon atoms in the presence of a chromium-based catalyst to make polyethylene copolymer in a first polymerisation reactor and in a second polymerisation reactor downstream of the first polymerisation reactor copolymerising ethylene in the presence of the chromium-based catalyst and a co-catalyst from ethylene monomer, a comonomer which has been fed into the second polymerisation reactor and comprises at least one alpha-olefin having from 3 to 8 carbon atoms and comonomer generated in-situ in the second polymerisation reactor to make polyethylene copolymer. The chromium-based catalyst has preferably been chemically reduced, for example by carbon monoxide, prior to the introduction thereof into the first polymerisation reactor. More preferably, the chromium-based catalyst additionally contains titanium. The present invention is predicated on the surprising discovery by the present inventors that the use of a two-stage polymerisation process using a chromium-based catalyst, wherein ethylene is introduced as a monomer and the catalyst systems present in the first and second stages are controlled so as to produce in the first stage a copolymer and the in the second stage a copolymer in which additional comonomer generated in-situ in the second stage is incorporated into the copolymer, can in turn yield a broader molecular weight distribution and a higher shear response for the resultant polyethylene resin, in turn yielding improved mechanical properties for the resin. The chromium-based catalyst preferably comprises a supported chromium oxide catalyst having a titania-containing support, for example a composite silica and titania support. A particularly preferred chromium-based catalyst may comprise from 0.5 to 5wt% chromium, preferably around 1wt% chromium, such as 0.9wt% chromium based on the weight of the chromium-based catalyst. The support comprises from 2 to 5wt% titanium, more preferably around 2 to 3wt% titanium, yet more preferably around 2.3wt% titanium based on the weight of the chromium-based catalyst. The chromium-based catalyst may have a specific surface area of from 200 to 700 m 2 /g, preferably from 400 to 550 m 2 /g and a volume porosity of greater than 2 cc/g preferably from 2 to 3 cc/g. A particularly preferred chromium-based catalyst ("catalyst 1") for use in the present invention has an average pore radius of 190A, a pore volume of around 2.1 cc/g, a specific surface area of around 510 m 2 /g and a chromium content of around 0.9wt% based on the weight of the chromium-containing catalyst. The support comprises a composite silica and titania support. The amount of titania in the support provides that the catalyst as a whole comprises around 2.3wt% titanium. The catalyst may be subjected to an initial activation step in air at an elevated activation temperature. The activation temperature preferably ranges from 500 to 850°C, more preferably around 650°C. The chromium-based catalyst is preferably subjected to a chemical reduction process in which at least a portion of the chromium is reduced to a low valence state. Preferably, the chromium-based catalyst is reduced in an atmosphere of dry carbon monoxide in nitrogen gas, typically 8% CO in N 2 at a temperature of from 250 to 500°C, more preferably around 340°C, for a period typically around 30 minutes. Optionally, the catalyst has been fluorinated, for example using NH 4 BF 4 as a fluorine source, so as to provide a fluorine content of around 1wt% in the catalyst, based on the weight of the catalyst. In the preferred polymerisation process of the present invention, the copolymerisation processes are carried out in the liquid phase, the liquid comprising ethylene in an inert diluent. The inert diluent is preferably isobutane. The copolymerisation processes are typically carried out at a temperature of from 80 to 110°C, more preferably from 90 to 100°C, and at a pressure of from 20 to 42 bars, more preferably at a minimum pressure of around 24 bars. The temperature is selected so as to obtain a particular molecular weight distribution in each of the copolymers produced in the first and second reactors respectively. Typically, in the copolymerisation processes, the ethylene monomer comprises from 0.5 to 8% by weight, typically around 6% by weight, of the total weight of the ethylene in the inert diluent. Since the comonomer is generated in-situ in the second reactor, only a portion of the required comonomer is fed to the second reactor. In the first stage of the polymerisation process the chromium-based catalyst is used alone in the absence of a co-catalyst. In the second stage of the polymerisation process a co-catalyst comprising at least one metal alkyl and/or at least one alkyl metal oxane is introduced together with further ethylene monomer. The metal alkyl preferably comprises triethyl boron (TEB), triethyl aluminium (TEA), dibutyl magnesium (MgBu 2 ), diethyl zinc DEZ) or butyl lithium (BuLi). The alkyl metal oxane preferably comprises diethyl aluminium ethoxy (DEALE) or methyl aluminium oxane (MAO). Preferably, the co-catalyst is introduced into the second polymerisation reactor in an amount of at least 1ppm, more preferably from 2 to lOppm, based on the weight of the inert diluent. The amount of co-catalyst employed is selected so as to provide in the copolymer produced in the second polymerisation reactor a selected density for the copolymer. In accordance with the process of the invention, the chromium-based catalyst, preferably having been reduced by carbon monoxide, is introduced into a first polymerisation reactor together with ethylene monomer and as comonomer an alpha-olefin having from 3 to 8 carbon atoms, such as 1-butene, 1-pentene, 1-hexene, 4-methyl 1-pentene, 1-heptene and 1-octene. The comonomer is typically present in a weight ratio of from 0.2 to 0.3 based on the weight of ethylene in the first reactor. The ethylene copolymerises to form polyethylene and typically the resultant polyethylene, if discharged from the first polymerisation reactor, has an HLMI of from around 10 to around 30g/10min, more typically from around 15 to 25g/10min (the HLMI being measured using the procedures of ASTM D 1238 using a load of 21.6kg at 190°C), and a density of around 0.94g/cc. The copolymer produced in the first reactor comprises the relatively high density, relatively low molecular weight, fraction of the resultant polyethylene resin. The product from the first polymerisation reactor is then fed into the downstream second polymerisation reactor and the metal alkyl and additional ethylene are introduced into the second polymerisation reactor. A comonomer comprising an alpha-olefin having from 3 to 8 carbon atoms, such as 1-butene, 1-pentene, 1-hexene, 4-methyl 1-pentene, 1-heptene and 1-octene is also fed into the second reactor. The comonomer is typically present in a weight ratio of from 0.1 to 0.2, more typically around 0.15 based on the weight of the ethylene in the second reactor. The provision of the co-catalyst of at least one metal alkyl and/or at least one alkyl metal oxane causes in-situ generation of comonomer from the ethylene whereby such comonomer is introduced into the polyethylene resin to form a polyethylene resin blend. As for the first reactor, the polymerisation temperature in the second reactor can be selected for targeting a particular molecular weight distribution in the resultant polyethylene resin. The resultant polyethylene resin is discharged from the second reactor and then separated from the diluent which can be recycled. The resultant polyethylene resin typically comprises from 40 to 60wt% copolymer produced in the first reactor and from 60 to 40wt% copolymer produced in the second reactor. A most typical polyethylene resin comprises equal amounts by weight of the polymers produced in the first and second reactors. The resultant polyethylene resin tends to have a lower density and a lower HLMI than the copolymer produced in the first polymerisation reactor. This is because in the second polymerisation reactor, as a result of the in-situ generation of comonomer, a copolymer is produced which tends to have a relatively high molecular weight and a relatively low density as compared to the copolymer produced in the first polymerisation reactor even though less comonomer is introduced into the second reactor than into the first reactor. This yields in turn for the composite polyethylene resin a broad molecular weight distribution and a high shear response, providing improved mechanical properties for the resin. Typically, in the resultant high or medium density polyethylene resin the density is from around 0.925 to around 0.940g/cc, more typically around 0.93g/cc, and an HLMI ranging from around 10 to around 30g/10min. The process of the invention can provide polyethylene resins having improved mechanical properties. The copolymer produced in the first polymerisation reactor has a relatively low molecular weight and the copolymer produced in the second polymerisation reactor has a relatively high molecular weight, the amount of comonomer which has been generated in-situ in the second reactor and has been introduced into the copolymer tending to have a distribution thereof in the copolymer which decreases at increasing molecular weight. When the two resin fractions are mixed together in the resultant polyethylene resin, the two molecular weight distributions overlap, thereby yielding in the resultant polyethylene resin a broad molecular weight distribution and a high shear response. This in turn provides improved mechanical properties, such as environmental stress crack resistance, impact resistance and slow crack growth resistance. The present invention will now be described with reference to the following non-limiting Example. EXAMPLE 1 In this Example, a polyethylene resin was produced by the polymerisation process of the present invention, in which a two-stage polymerisation process was employed with two serially-connected polymerisation reactors. In the first reactor, ethylene in isobutane as an inert diluent was introduced into the reactor together with the chromium-based catalyst identified as catalyst 1 above which had been activated in dry air at a temperature of around 650°C and had been subjected to carbon monoxide reduction at a temperature of around 370°C for a period of around 30 minutes in an atmosphere comprising 8% CO in nitrogen gas. The catalyst had a pore volume of 2.lcc/g and a specific surface area of 510m 2 /g. The catalyst comprised 0.9% Cr and 2.3% Ti, each based on the weight of the catalyst. The ethylene was present in the isobutane as an inert diluent in an amount of around 6wt%. The polymerisation temperature was around 95°C, and the polymerisation pressure was around 30 bars. This Example was performed at this pressure on a bench-scale reactor. In liquid-full reactors, typically used in commercial production, the pressure would be around 40 bars. In the first polymerisation reactor, a polyethylene copolymer was formed as a result of a weight ratio of 0.25 1-hexene based on the weight of the ethylene in the first reactor having been introduced together with the ethylene. The so-formed polyethylene was then fed as polyethylene fluff to the second serially connected reactor downstream of the first reactor. The chromium-based catalyst was also conveyed to the second reactor and an additional metal alkyl or alkyl metal oxane co-catalyst was introduced into the second reactor, together with additional ethylene monomer and 1-hexene and comonomer. In the second polymerisation reactor, the ethylene comprised around 6wt% ethylene in the isobutane inert diluent. The reaction temperature was around 85°C and the pressure was slightly lower than that for the first reactor to provide throughput of the reactants and the catalyst from the first reactor to the second reactor. Table 1 shows the type of co-catalyst introduced into the second reactor, together with the amount of such co-catalyst. Table 1 also shows the properties, namely the HLMI, the MI 2 and the density, of the polyethylene copolymer produced in the first reactor in Example 1, together with the properties, namely the HLMI, the MI 2 and the density, of the resultant LLDPE polyethylene resin produced following production of the polyethylene copolymer in the second reactor. The polyethylene copolymer produced in the first reactor comprised around 50wt% of the resultant polyethylene resin. The MI 2 values were measured in accordance with the procedures of ASTM D 1238 using a load of 2.16kg at a temperature of 190°C. REACTOR 1 EXAMPLE 1 Temperature °C 95 Ethylene wt% 6 Hexene/ethylene (wt/wt) 0.25 PRODUCT HLMI (g/10') 20 MI 2 (g/10') 0.32 density (g/cc) 0.940 REACTOR 2 Temperature °C 85 Ethylene wt% 6 Hexene/ethylene (wt/wt) 0.15 METAL ALKYL CO-CATALYST type TEB ppm 6 PRODUCT HLMI (g/10') 17 MI 2 (g/10') 0.22 density (g/cc) 0.930

Claims: A process for producing a linear low density polyethylene resin, the process comprising: (i) copolymerising ethylene and a comonomer comprising at least one alpha-olefin having from 3 to 8 carbon atoms in the presence of a chromium-based catalyst to make polyethylene copolymer in a first polymerisation reactor and (ii) in a second polymerisation reactor downstream of the first polymerisation reactor copolymerising, in the presence of the chromium-based catalyst coming from the first polymerisation reactor and of a co-catalyst, ethylene monomer and a comonomer which has been fed into the second polymerisation reactor and which comprises at least one alpha-olefin having from 3 to 8 carbon atoms and a comonomer generated in-situ in the second polymerisation reactor. A process according to claim 1 wherein the comonomer in the first polymerisation reactor is added in a weight ratio of from 0.2 to 0.3 based on the weight of ethylene added to the first polymerisation reactor. A process according to claim 1 or claim 2 wherein in the second polymerisation reactor the comonomer is added in a weight ratio of from 0.1 to 0.2 based on the weight of ethylene fed to the second polymerisation reactor. A process according to any foregoing claim wherein the chromium-based catalyst has a titania-containing support. A process according to any foregoing claim wherein the chromium-based catalyst comprises around 1wt% chromium and from 2 to 5wt% titanium, each based on the weight of the chromium-based catalyst. A process according to claim 5 wherein the chromium-based catalyst comprises from 2 to 3wt% titanium, based on the weight of the chromium-based catalyst. A process according to any foregoing claim wherein the co-catalyst is selected from at least one of a metal alkyl and an alkyl metal oxane. A process according to claim 7 wherein the co-catalyst comprises at least one metal alkyl selected from at least one of triethyl boron, triethyl aluminium, dibutyl magnesium, diethyl zinc and butyl lithium. A process according to claim 7 wherein the alkyl metal oxane is selected from at least one of diethyl aluminium ethoxy and methyl aluminium oxane. A process according to any one of claims 7 to 9 wherein the co-catalyst is present in an amount of from 2 to lOppm based on the weight of an inert diluent for the ethylene monomer in the polymerisation reactors. A process according to any foregoing claim wherein the polyethylene produced in the first reactor comprises from 40 to 60wt% of the polyethylene resin. A process according to any foregoing claim wherein the polyethylene resin has an HLMI of from 10 to 30g/10min. A process according to any foregoing claim wherein the polyethylene resin has a density of from 0.925 to 0.940g/cc. A process according to any foregoing claim wherein the polyethylene produced in the first polymerisation reactor has a density of around 0.94g/cc. A process according to any foregoing claim wherein the catalyst has been chemically reduced.

Inventors: DEBRAS GUY, DEBRAS, GUY
Applicants: TOTAL PETROCHEMICALS RES FELUY, TOTAL PETROCHEMICALS RESEARCH FELUY
Application year: 1999
Main classification: C08F210
IPC codes: C08F297, C08F2, C08F210, C08F4