An oxide phosphorescent glass capable of exhibiting a long lasting afterglow and photostimulated luminescence

Abstract: The present invention provides an oxide glass capable of exhibiting a long lasting afterglow and photostimulated phosphorescence, whereby energy can be accumulated by radiation excitation, for example, by γ-rays, X-rays and UV-rays, light emission can be continued for a long time even after stopping the excitation. Furthermore, the long lasting afterglow and photostimulated luminescence oxide glass capable of exhibiting photostimulated luminescence by irradiation of infrared rays or visible rays can be used not only as a material for confirming an infrared laser or controlling an optical axis, but also as a material for recording or reproducing of γ-ray, X-ray or UV-ray images and further can be used as an optical recording material of a type that can be read. This glass material is represented, in term of atoms making up the glass, by the following chemical composition (mol %): GeO 2 21 to 80 % ZnO 0 to 50 % Ga 2 O 3 0 to 55 % (ZnO + Ga 2 O 3 = 3 to 55 %) Tb 2 O 3 0 to 10 % MnO 0 to 2 % (Tb 2 O 3 + MnO = 0.01 to 10 %) R 2 O 0 to 45 % (R: at least one atom selected from Li, Na, K and Cs) R'O 0 to 40 % (R': at least one atom selected from Mg, Ca, Sr and Ba) R 2 O + R'O 0.5 to 45 % SiO 2 0 to 50 % B 2 O 3 0 to 20 % Al 2 O 3 0 to 20 % Yb 2 O 3 0 to 7 % and Ln 2 O 3 0 to 5 % (Ln: at least one atom selected from Sm, Dy, Tm, Pr, Y, La, Gd, Lu and Nd)

Description: This invention relates to an oxide glass capable of exhibiting a long lasting afterglow and photostimulated luminescence, whereby energy can be accumulated by radiation excitation, for example, by γ-rays, X-rays and UV-rays, light emission can be continued for a long time even after stopping the excitation, so that the oxide glass can be used as a phosphorescent material for night illumination or night signal, and furthermore, photostimulated luminescence can be exhibited by irradiation of visible rays or infrared rays, which is useful for confirming an infrared laser or controlling an optical axis of a laser beam, so that recording or reproducing of γ-ray, X-ray or UV-ray images can be effected, and which can be used as an optical recording material capable of reading and writing. Phosphorescent materials or photostimulated luminescence phosphor using rare earth elements have widely been used up to the present time. As a phosphorescent material, there can practically be used e.g. SrAl 2 O 4 :Eu 2+ or Dy 3- and as a photostimulated luminescence phosphor, there has already been developed e.g. BaFBr:Eu 2+ These are opaque materials only exhibiting superficial phosphorescence, generally obtained by coating a suitable carrier with a powdered phosphorescent material or photostimulated luminescence phosphor. On the other hand, a glass capable of exhibiting a photostimulated luminescence without coating a photostimulated luminescence phosphor has been disclosed in Japanese Patent Laid-Open Publication No. 221336/1997. In addition, Japanese Patent Application Nos. 346362/1997 and 88674/1998 respectively disclose obtaining phosphorescent glasses of the SiO 2 -B 2 O 3 -ZnO-Tb 2 O 3 system and SiO 2 -Ga 2 O 3 -Na 2 O-Tb 2 O 3 system. When coating a powdered phosphorescent material or photostimulated luminescent phosphor, dispersion of the coating thickness or peeling-off of the coated surface occurs thereby causing light and shade of the phosphorescence. In order to increase the emission intensity, it is necessary to coat a phosphorescent material or photostimulated luminescence phosphor with a larger thickness, but the coating is limited by increase in opaqueness. Since phosphorescence emitted from a grain boundary in the phosphorescent material or photostimulated luminescence phosphor is scattered, furthermore, no clear image can be obtained. A photostimulated luminescent glass described in Japanese Patent Laid-Open Publication No. 221336/1997 utilizes Ce 3+ or Eu 2+ as an active ion for emission. In order to obtain these active ions, it is necessary to add a reducing agent or to melt in a reducing atmosphere. Furthermore, observation of the emission is difficult because it is UV light or blue light. It is an object of the present invention to provide a Tb- or Mn-containing oxide phosphorescent glass whereby the above described problems of the prior art can be solved. It is another object of the present invention to provide an oxide glass capable of exhibiting a long lasting afterglow and photostimulated luminescence of green or red emitted light readily observable, which can be melted without using any reducing agent or reducing atmosphere by utilizing Tb or Mn as a phosphorescent or luminescent agent. These objects can be attained by an oxide glass capable of exhibiting a long lasting afterglow and photostimulated luminescence by excitation with radiations such as γ-rays, X-rays or UV-rays, having a constitutional composition as defined in the claim. The accompanying drawings illustrate the principle and merits of the present invention. Fig. 1 is a graph, Curves (a) and (c) showing phosphorescent spectra of the glasses prepared respectively in Example 1 and Example 17, excited by an UV-ray of 330 nm. Fig. 2 is a graph, Curves (a), (b), (c), (d) and (e) showing a change of emission intensity with time as to the glasses prepared, respectively in Examples 1, 3 and 17 and Comparative Examples 1 and 2, excited by a UV-ray of 330 nm. Generally, rare earth ions in excited state tend to emit light in about one second to lose its energy. Thus, it is considered in an oxide glass containing a large amount of zinc, for example, glass of SiO 2 -B 2 O 3 -ZnO-Tb 2 O 3 type as formerly proposed in Japanese Patent Application No. 346362/1997 that energy is accumulated on the trapping level of zinc ion by a high energy of a radiation such as γ-rays, X-rays or UV-rays and the inventors have reached the present invention based on the knowledge that the energy on the trapping level is released by a stimulus such as by heat, visible rays or infrared rays and removed to terbium ion to exhibit a long lasting afterglow and photostimulated luminescence Furthermore, a similar phenomenon appears also in the system SiO 2 -Ga 2 O 3 -Na 2 O-Tb 2 O 3 of Japanese Patent Application No. 88674/1998. In the glass system of the present invention, on the other hand, GeO 2 is used as an essential component of the glass to obtain a longer lasting afterglow and photostimulated luminescence than the systems SiO 2 -B 2 O 3 -ZnO-Tb 2 O 3 and SiO 2 -Ga 2 O 3 -Na 2 O-Tb 2 O 3 . Furthermore, a long lasting afterglow can be obtained by an ordinary fluorescent lamp or sunlight without using any special excitation light source, because accumulation of light can be made by a low energy light of longer wavelength. That is, according to the present invention, there is provided an oxide glass capable of exhibiting a long lasting afterglow and photostimulated luminescence by excitation with radiations such as γ-rays, X-rays or UV-rays, which is represented, in term of atoms making up the glass, by the following chemical composition (mol %): GeO 2 21 to 80 % ZnO 0 to 50 % Ga 2 O 3 0 to 55 % (ZnO + Ga 2 O 3 = 3 to 55 %) Tb 2 O 3 0 to 10 % MnO 0 to 2 % (Tb 2 O 3 + MnO = 0.01 to 10 %) R 2 O 0 to 45 % (R: at least one atom selected from Li, Na, K and Cs) R'O 0 to 40 % (R': at least one atom selected from Mg, Ca, Sr and Ba) R 2 O + R'O 0.5 to 45 % SiO 2 0 to 50 % B 2 O 3 0 to 20 % Al 2 O 3 0 to 20 % Yb 2 O 3 0 to 7 % and Ln 2 O 3 0 to 5 % (Ln: at least one atom selected from Sm, Dy, Tm, Pr, Y, La, Gd, Lu and Nd) In the present invention, as a radiation, there can be used charged particle rays in addition to γ-rays, X-rays or UV-rays, described above. The reasons for limiting the composition range of each component of this oxide phosphorescent glass to those described above are as follows: GeO 2 is a component serving glass formation, which is present in a proportion of 21 to 80 %, since if less than 21 % or if more than 80 %, the melting temperature is so high that preparation of the glass is difficult. The preferred range is 21 to 75 %. ZnO is a component for accumulating energy, improving the melting property of the glass and rendering glass formation easy, which is present in a proportion of 0 to 50 %, since if more than 50 %, glass formation is difficult. The preferred range is 0 to 45 %. Ga 2 O 3 is a component for improving the lasting afterglow effect of the glass, which is present in a proportion of 0 to 55 %, since if more than 55 %, the glass is unstable and tends to be crystallized. The preferred range is 0 to 50 %. The sum of ZnO + Ga 2 O 3 should be 3 to 55 %, since if less than 3 %, the emission intensity is lower, while if more than 55 %, the melting temperature is so high that preparation of the glass is difficult. The preferred range of the sum is 5 to 50 %. Tb 2 O 3 is a component for presenting green phosphorescence, which is present in a proportion of 0 to 10 %, since if more than 10 %, it is difficult to obtain the glass. The preferred range is 0 to 8 %. MnO is a component capable of presenting red phosphorescence, which is present in a proportion of 0 to 2 %, since if more than 2 %, it is difficult to obtain the glass. The preferred range is 0 to 1 %. The sum of Tb 2 O 3 and MnO should be 0.01 to 10 %, since if less than 0.01 %, the emission intensity is lower, while if more than 10 %, it is difficult to obtain the glass. The preferred range is 0.05 to 8 %. R 2 O (R: at least one atom selected from Li, Na, K and Cs) acts to lower the melting temperature of the glass melt, which is present in a proportion of 0 to 45 %, since if exceeding 45 %, the water resisting property is lowered and the devitrification tendency is increased, thus rendering the glass unstable. The preferred range is 0 to 40 %. R'O (R': at least one atom selected from Mg, Ca, Sr and Ba) are components for improving the melting property of the glass, which are present in a proportion of 0 to 40 %, since if more than 40 %, the glass is unstable and tends to be crystallized. The preferred range of R'O is 0 to 35 %. The sum of R 2 O + R'O should be 0.5 to 45 %, since if less than 0.5 %, the melting temperature is so high that preparation of the glass is difficult and if more than 45 %, the glass is unstable and tends to be crystallized. The preferred range of the sum is 1 to 40 %. SiO 2 is a glass-forming component, which is present in a proportion of 0 to 50 %, since if more than 50 %, the glass melting temperature is too high to prepare the glass. The preferred range is 0 to 45 %. B 2 O 3 is a glass-forming component, which is present in a proportion of 0 to 20 %, since if more than 20 %, the emission intensity is reduced. The preferred range is 0 to 15 %. Al 2 O 3 is a component for improving the durability of the glass, which should be present in a proportion of 0 to 20 %, since if more than 20 %, the melting temperature of the glass is too high to prepare the glass. The preferred range is 0 to 15 %. Yb 2 O 3 acts as a sensitizer to further increase the lasting afterglow effect of the glass, which is present in a proportion of 0 to 7 %, since if more than 7 %, the effect thereof is reduced. The preferred range is 0 to 5 %. Ln 2 O 3 (Ln: at least one atom selected from Sm, Dy, Tm, Pr, Y, La, Gd, Lu and Nd) is a component for increasing the viscosity of the glass and suppressing crystallization. This component should be present in a proportion of 0 to 5 %, since if more than 5 %, the above described effect is adversely affected. The preferred range is 0 to 3 %. Cleaning agents such as Sb 2 O 3 or As 2 O 3 and the commonly used auxiliary components, for example, P 2 O 5 , WO 3 , TeO 2 , Bi 2 O 3 , Nb 2 O 5 , Ta 2 O 5 , TiO 2 , CdO, SnO, PbO, Tl 2 O, CoO, F, Cl and Br can optionally be added, in such amounts that the effects of the present invention are not adversely affected to the glass composition. Production of an oxide phosphorescent glass capable of visually exhibiting a long lasting afterglow and photostimulated luminescence is carried out by mixing the corresponding raw material compounds to a proportion of the object composition, for example, germanium oxide, zinc oxide, gallium oxide, terbium oxide or manganese oxide, melting the resulting mixture in the air at a temperature of 1100 to 1500 °C for 1 to 3 hours and allowing the mixture to flow out in a metallic mold, followed by shaping. In the oxide phosphorescent glass of the present invention, the afterglow time is generally in a range of about at least one second, preferably about one second to two hours. Preferred embodiments of the present invention are summarized below: (I) Oxide glasses each capable of exhibiting a long lasting afterglow and photostimulated luminescence, as described in the foregoing (1), which is represented, in term of atoms for making up the glass, by the chemical composition (mol %) shown in Table 1: GeO 2 21 to 75 % ZnO 0 to 45 % Ga 2 O 3 0 to 50 % ZnO + Ga 2 O 3 5 to 50 % Tb 2 O 3 0 to 8 % MnO 0 to 1 % Tb 2 O 3 + MnO 0.05 to 8 % R 2 O 0 to 40 % R'O 0 to 35 % R 2 O + R'O 1 to 40 % SiO 2 0 to 45 % B 2 O 3 0 to 15 % Al 2 O 3 0 to 15 % Yb 2 O 3 0 to 5 % Ln 2 O 3 0 to 3 % The present invention will now be illustrated in detail without limiting the same: Example 1 Raw materials were mixed according to the weight ratios of Example No. 1 shown in Table 2 to give a composition of Example No. 1 shown in Table 3. The thus prepared raw materials were melted at a temperature of 1100 to 1500 °C for 1 to 3 hours, allowed to flow into a metallic mold and shaped to obtain a glass in stable manner. When the resulting glass was excited by an ultraviolet ray of 330 nm, green afterglow phosphorescence was exhibited to give the phosphorescent spectrum shown in Fig. 1 (a). A change of emission intensity with time as to the glass excited by the UV ray of 330 nm is shown in Fig. 2 (a). When this glass was irradiated by X-rays and then by a semiconductor laser of 800 nm or 980 nm, a green photo-stimulated luminescence was visually observed. Examples 2 to 16 Raw materials were mixed according to weight ratios of Example Nos. 2 to 16 shown in Table 2 and melted in the similar manner to Example 1 to obtain various glass compositions (Example Nos. 2 to 16) shown in Table 3 in stable manner. When the resulting glasses in Examples 2 to 16 were excited by an ultraviolet ray of 330 nm, there were obtained similar spectra to Fig. 1 (a) exhibiting green photostimulated luminescence similar to Example 1 and change of emission intensity of thereof with time, similar to Fig. 2 (a). The change in the case of Example 3 is shown in Fig. 2 (b). When these glasses were irradiated by X-rays in the similar manner to Example 1 and then by a semiconductor laser of 800 nm, a green photostimulated luminescence was visually observed. Example 17 Raw materials were mixed according to weight ratios of Example No. 17 shown in Table 2 to give a composition of Example No. 17 shown in Table 3. The thus prepared raw materials were melted at a temperature of 1100 to 1500 °C for 1 to 3 hours, allowed to flow into a metallic mold and shaped to obtain a glass in stable manner. When the resulting glass was excited by an ultraviolet ray of 330 nm, red afterglow phosphorescence was exhibited to give a phosphorescent spectrum shown in Fig. 1 (c). A change of emission intensity with time as to the glass excited by the UV ray of 330 nm is shown in Fig. 2 (c). When this glass was irradiated by X-rays and then by a semiconductor laser of 800 nm or 980 nm, a red photostimulated luminescence was visually observed. Examples 18 to 21 Raw materials were mixed according to weight ratios of Example Nos. 18 to 21 shown in Table 2 and melted in the similar manner to Example 17 to obtain various glass compositions (Example Nos. 18 to 21) shown in Table 3 in stable manner. When the resulting glasses in Examples 18 to 21 were excited by an ultraviolet ray of 330 nm, there were obtained similar spectra to Fig. 1 exhibiting red photostimulated luminescence similar to Example 17 and change of emission intensity of thereof with time, similar to Fig. 2. When these glasses were irradiated by X-rays in the similar manner to Example 17 and then by a semiconductor laser of 800 nm or 980 nm, a red photo-stimulated luminescence was visually observed. Comparative Examples 1 and 2 Glasses having compositions shown in Comparative Examples 1 and 2 of Table 2, as a comparative example, were prepared in the similar manner to Example 1. When the resulting glasses were excited by an ultraviolet ray of 330 nm under the similar condition to Example 1, any afterglow phosphorescence was not observed and the change of the emission intensity with time was shown in Fig. 2 (d) and (e). Advantages of the Invention According to the present invention, there can be provided an oxide glass capable of exhibiting a long lasting afterglow and photostimulated luminescence, whereby energy can be accumulated by radiation excitation, for example, by γ-rays, X-rays and UV-rays, light emission can be continued for a long time even after stopping the excitation and photostimulated luminescence can be exhibited by irradiation of visible rays or infrared rays. That is, the long lasting afterglow and photostimulated luminescence oxide glass of the present invention can be used not only as a phosphorescent material for night illumination or night signal, but also as a material for confirming an infrared laser or controlling an optical axis because of exhibiting photostimulated luminescence by irradiation of infrared rays. When this glass is converted into fibers, an emitted light in the fiber can efficiently be guided to the end surface of the fiber. In addition, this glass is useful for recording or reproducing of γ-ray, X-ray or UV-ray images without coating the photostimulated luminescent material and can be applied to an optical recording material of a type that can be read.

Claims: An oxide fluorescent or phosphorescent glass capable of exhibiting a long lasting afterglow and photostimulated luminescence which is represented, in term of atoms making up the glass, by the following chemical composition (mol %): GeO 2 21 to 80 % ZnO 0 to 50 % Ga 2 O 3 0 to 55 % (ZnO + Ga 2 O 3 = 3 to 55 %) Tb 2 O 3 0 to 10 % MnO 0 to 2 % (Tb 2 O 3 + MnO = 0.01 to 10 %) R 2 O 0 to 45 % (R: at least one atom selected from Li, Na, K and Cs) R'O 0 to 40 % (R': at least one atom selected from Mg, Ca, Sr and Ba) R 2 O + R'O 0.5 to 45 % SiO 2 0 to 50 % B 2 O 3 0 to 20 % Al 2 O 3 0 to 20 % Yb 2 O 3 0 to 7 % and Ln 2 O 3 0 to 5 % (Ln: at least one atom selected from Sm, Dy, Tm, Pr, Y, La, Gd, Lu and Nd)

Inventors: NAGAHAMA SHINOBU, SAWANOBORI NARUHITO, YAMAMOTO YOSHINORI, YAMAZAKI MASAAKI, NAGAHAMA, SHINOBU, SAWANOBORI, NARUHITO, YAMAMOTO, YOSHINORI, YAMAZAKI, MASAAKI
Applicants: SUMITA OPTICAL GLASS CO LTD, SUMITA OPTICAL GLASS CO., LTD.
Application year: 1999
Main classification: C03C3
IPC codes: C09K11, G01T1, C03C3, C03C4