MULTI-LAYER ENGINE BEARINGS AND METHOD OF MANUFACTURE

Abstract: A multi-layer engine bearing (26) includes a steel backing (36) having a liner (38) of bearing metal of either copper-lead or aluminum alloys formed on the backing (36) and a thin layer (44) of either copper or nickel plated on the liner (38) to define a base lining member (40) of the bearing (26). A multi-layer overplate (46) is formed on the base lining member (40) and includes an underlayer (48) of a lead-tin-copper alloy having a thickness of about 10 mu m and an overlayer (50) of tin having a thickness of about 5 mu m. The multi-layer overplate (46) exhibits exceptional fatigue resistance under high dynamic loading conditions and retains good conformability and embedibility characteristics.

Description: MULTI-LAYER ENGINE BEARINGS AND METHOD OF MANUFACTURE BACKGROUND OF THE INVENTION 1. Technical Field The present invention relates generally to plain bearings and to their method of manufacture and more particularly to multilayer engine bearings ofthe type having a metal backed layer of copper-lead or aluminum alloy lining oveφlated with a softer bearing metal for use in internal combustion engines. 2. Related Prior Art Plain engine journal bearings for use in high load engine applications, such as connecting rod, main and accessory or balance crankshaft bearings of high torque diesel or high performance gasoline engines, typically include a base lining member having a lining of either copper-lead or aluminum alloy formed on a surface of a steel backing. The lining is oveφlated with a softer bearing metal typically comprising a single layer of a lead-tin-copper alloy having a thickness of about 25 μm. Often, a nickel diffusion barrier or copper bonding layer is inteφosed between the lining and oveφlate. As a final step, the bearing is typically coated with a micro-thin layer of tin or lead-tin flash plating having a thickness of about 1 μm or less. The flash plating is primarily cosmetic, giving the product a bright, pleasing appearance. It also provides a level of corrosion protection to the steel backing. The micro-thin flash plating applied to the oveφlate quickly dissipates within the first few hours of engine break-in, and as such does not contribute to the bearing properties ofthe oveφlate. In service, such multilayer crankshaft bearings are subjected to dynamic loads that vary in magnitude and direction due to the inertial loads applied by the piston and connecting rod mechanism and by the cylinder gas. The softer oveφlate layer enables the bearing surface to continually change and conform under high load forces to any misalignments or changes in profile or loading ofthe member being journaled, so that the loads are distributed across a greater surface area of the bearing. This property is generally known as "conformability". The oveφlate also allows any foreign particles of dirt or metal that may come between the bearing surface and the member it journals to become embedded or absorbed into the bearing surface, so as to protect the bearing and journal from excessive wear or damage. This property is known as "embedibility". It is generally accepted that conformability and embedibility are dependant upon oveφlate thickess, with a thicker oveφlate being preferred. It is also generally known that as the thickness ofthe oveφlate increases, so does the susceptibility to bearing fatigue (i.e., the fracturing ofthe bearing surface when under load). Resistance to fatigue cracking requires that the bearing surface exhibit sufficient tensile strength to enable it to undergo minor configuration changes without cracking. Thus, it is necessary to balance the competing properties of conformability/embedibility and fatigue resistance when designing an engine bearing, particularly one that is to be subjected to high dynamic loading. For many high load engine applications, it has been found that the single layer, 25 μm thick lead-tin-copper oveφlate described above provides excellent conformability and embedibility characteristics and good fatigue resistance. However, as the output and efficiency of engines continually increases, the dynamic loads placed on the crankshaft bearings also increase, as does the potential for bearing fatigue. It has been found that under extreme loading conditions the conventional bearings described above having a single layer oveφlate of lead-tin- copper are prone to fatigue. Efforts to alleviate fatigue by simply decreasing the thickness ofthe lead-tin-copper oveφlate layer to less than the 25 μm thickness while at the same time preserving an acceptable level of conformability and embedibility have been largely unsuccessful to date. Thus, there exists a need in the industry for an improved journal bearing that can perform under such extreme high dynamic loading conditions without experiencing fatigue and while maintaining good conformability and embedibility characteristics. SUMMARY OF THE INVENTION According to the invention, a multilayer engine bearing is provided comprising a base lining member having a rigid metal backing and a lining of bearing metal formed on the backing, and is characterized by a multilayer oveφlate formed on the base lining member including an underlayer of lead-tin-copper alloy having a predetermined thickness of about 10 μm and a functional overlayer of tin having a predetermined thickness of about 5 μm. Such a bearing is able to withstand extreme high dynamic loading conditions without fatigue and while providing good conformability and embedibility characteristics. In comparative testing under extreme high dynamic loading conditions, bearings according to the invention having the characteristic multilayer oveφlate exhibited no observable signs of fatigue cracking, whereas conventional bearings formed with the traditional 25 μm single layer lead-tin-copper oveφlate exhibited extensive fatigue cracking. Unlike the microthin tin flash plating employed in traditional engine bearings, the tin overlayer ofthe invention is puφosely thicker so that it remains in place over the lead-tin-copper underlayer when in service so as to contribute to the bearing properties ofthe oveφlate. The properties of underlayer and overlayer compliment one another in a way that, when combined, provides the desired fatigue-free bearing surface characteristics under extreme high dynamic loading conditions, while preserving conformability and embedibility. A method is also provided for fabricating a multilayer engine bearing according to the invention and comprises the steps of preparing a base lining member by forming a lining of bearing metal on a rigid backing, and is characterized by forming a multilayer oveφlate on the base lining member including forming an underlayer of lead-tin-copper alloy having a predetermined thicknes of about 10 μm and an overlayer of tin having a predetermined thickness of about 5 μm. These aspects ofthe invention share the same advantages over the known prior art as those discussed above. BRIEF DESCRIPTION OF THE DRAWINGS These and other advantages and features will be readily appreciated as the same becomes better understood by reference to the following detailed description when considered in connection with the accompanying drawings, wherein: Figure 1 is a fragmentary sectional view of an internal combustion engine having a rotatable member shown journaled by a bearing constructed in accordance with a presently preferred embodiment ofthe invention; Figure 2 is an enlarged perspective view of a bearing according to the invention; Figure 3 is a fragmentary sectional view taken generally along line 3-3 of Figure 2; and Figure 4 is a graph showing fatigue performance as a function of oveφlate thickness for bearings having different oveφlates. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS Turning now in more detail to the drawings, Figure 1 schematically illustrates an internal combustion engine, generally shown at 10, having an engine block 12 formed with a plurality of piston cylinders 14 (only one shown) in which pistons 16 reciprocate. Each piston 16 is coupled to an upper end of an associated connecting rod 18 by a wrist pin 20. Each connecting rod 18, in turn, is drivingly coupled at an opposite lower end 22 thereof to a crankshaft 24. A multilayer plain bearing 26 constructed according to the invention is disposed between each connecting rod 18 and the crankshaft 24 to establish journaled connections between the connecting rods 18 and crankshaft 24. Each bearing 26 includes an upper half 28 and a lower half 30 adapted for mounting in respective upper and lower bearing seats 32, 34 ofthe connecting rod 18 in conventional manner to collectively encircle the crankshaft 24. Multilayer bearings 26 ofthe same type (i.e., the main bearings, not shown) may also be disposed in the usual manner in the block 12 adjacent the ends ofthe crankshaft 24, and in many engine applications at spaced points along the length ofthe crankshaft 24 between adjacent cylinders 14 as well to provide journalled support to the crankshaft 24 for rotation about its axis relative to the block 12. For puφoses ofthe invention, such multilayer bearings 26 may be generally referred to as journal bearings or sleeve bearings, and in the illustrated example crankshaft bearings, and include connecting rod bearings, main bearings as well as other high dynamic loading applications where a plain multilayer bearing is employed to journal a rotatable component of a working system. The term multilayer bearing also is understood to include within its scope multilayer bushings. With reference to Figures 2 and 3, the bearing 26 ofthe invention includes a rigid metal support backing 36 and a liner 38 of metallic bearing material formed on the backing to collectively provide a base lining member 40 which forms the foundation ofthe bearing 26. The backing 36 preferably comprises an arcuate, semi-circular strip of steel and includes a convex outer surface 41 adapted for seating in a mating concave support structure and an opposite concave inner surface 42. The liner 38 may be formed of either a copper-lead or aluminum alloy of conventional compositions, which may be cast or otherwise formed on the inner surface 42 ofthe backing 36 according to well known practice. The base lining member 40 may also include a thin barrier layer or film 44 (i.e., about 1-2 μm thick) of either nickel or copper which may be electroplated onto the liner 38 accordingly to conventional practice to serve as a migration barrier or as a bonding layer for the oveφlate to be described below. The construction described thus far with respect to the base lining member 40 is conventional. Where the invention departs from conventional practice is that following the fabrication ofthe base lining member 40, a multilayer oveφlate 46 is formed on the base lining member 40 having a combined thickness of about 15 μm. In contrast, the oveφlate of a conventional high load engine bearing is typically formed of a single layer of lead-tin-copper alloy having a thickness of about 25 μm. As shown best in Figure 3, the multilayer oveφlate 46 ofthe invention includes an underlayer 48 of lead-tin-copper and an overlayer 50 of tin. The underlayer 48 is preferably fabricated ofthe same lead-tin- copper alloy material as that used for conventional single layer oveφlates, but having a reduced thickness of about 10 um. The underlayer 48 may be electrodeposited onto the layer 44 according to conventional practice. A preferred composition ofthe lead-tin-copper underlayer 48, expressed in weight percentage, includes 10% tin, 2% copper and the balance lead, although other lead-tin-copper alloys commonly used in overlay bearing applications may be used having tin typically ranging from about 8-16% wt. and copper typically ranging from 0-10% wt., with the balance lead. The overlayer 50 of tin is preferably pure tin electrodeposited onto the underlayer 46 to a thickness of about 5 μm to yield the combined oveφlate thickness of about 15 μm. The tin overlayer 50 may be formed using conventional tin plating equipment. It is preferred that the tin overlayer 50 be plated from a tin fluoborate electrolyte plating solution at a current density exceeding 20 amps/ft 2 , and preferably exceeding about 50 amps/ft 2 . Results consistent with those shown in the graph of Figure 4 with respect to the bearings 26 ofthe invention were achieved by plating the tin overlayer 50 from a tin fluoborate electrolyte plating bath at current density of about 75 amps/ft 2 . According to a method of fabricating a multilayer bearing 26 of the invention, the base lining member 40 is prepared according to conventional practice by bonding the metallic liner 38 to the inner surface 42 ofthe backing 36 and then plating the liner 38 with the barrier layer 44 in preparation to receive the multilayer oveφlate 46. The oveφlate 46 is applied by first electrodepositing the lead-tin-copper underlayer onto the barrier layer 44 to a thickness of about 10 μm and then electrodepositing the tin overlayer 50 onto the underlayer 48 to a thickness of about 5 μm. As a final step, the bearing surface 41 is coated with a thin layer of tin flash plating 52 having a thickness of about 1 μm or less. Lead-tin flash plating may also be used. The flash plating 52 covers the exposed outer surface 41 and sides ofthe steel backing 36 in order to protect the backing 36 from corrosion and gives the bearing 26 a bright, attractive appearance that is advantageously uniform in appearance with the tin overlayer 50 of the invention. Bearings 26 manufactured according to ofthe invention were tested under conditions representative of extreme high dynamic loading service environment in an engine application. Other bearings were tested under the same conditions for comparison puφoses and the results are shown in Figure 4. Each ofthe bearings had the same base lining construction and differed only by the composition and thicknesses of their oveφlate layers. B-l represents the bearings 26 ofthe invention having the 15 μm multilayer oveφlate 46. B-2 represents conventional engine bearings having a 25 μm thick single layer oveφlate of a conventional lead-tin-copper alloy (i.e., PbSn 10 Cu 2 ). B-3 represents an engine bearing like that of B-2 but prepared with only a 15 μm oveφlate layer. Finally, B-4 represents an engine bearing having a 15 μm thick oveφlate of pure tin. The test apparatus employed was a heavy duty diesel engine (i.e., 7.2 Liter 16 275 HP) representative of that shown at 10 in Figure 1 coupled to a dynamometer. The bearings tested were connecting rod bearings and each were installed in the engine in conventional manner between the connecting rods and the crankshaft. The engine was operated under conditions applying about 70 Mpa unit load on the bearings (68.6 Mpa actual). The duration of each test was about 75 hours which equates to about 4.95 x 10 6 load cycles on the bearings. It will be seen from the results given in Figure 4 that the B-l bearings ofthe invention clearly out performed the conventional B-2 10 bearings. Upon close visual inspection following testing, the bearing surface ofthe B-l bearings showed no visible signs of fatigue cracking, whereas about 30% ofthe bearing surface area ofthe B-2 bearings showed fatigue cracking. For puφoses of comparison, B-3 bearings were prepared and tested and showed some improvement in fatigue performance in the B-3 bearings (about 15% area fatigued) as expected on account ofthe decrease in the oveφlate thickness to 15 μm from 25 μm. Suφrisingly, however, the multilayer oveφlate ofthe B-l bearings having the same 15 μm oveφlate thickness far out performed even the B-3 bearings, demonstrating that the results achieved by the B-l bearings accounts for more than just oveφlate thickness. The B-4 bearings were also prepared and tested for puφoses of comparison with the results ofthe B-l bearings and, similarly to B-3, exhibited fatigue cracking (about 10% area fatigued) far in excess ofthe multilayer oveφlate 46 ofthe B-l bearings ofthe same thickness. The results thus show that the fatigue-free performance ofthe B-l bearings of the invention is attributed to the particular combination ofthe oveφlate materials used and their relative thickness. Also suφrising was to find that the remarkable improvements achieved in the fatigue resistance ofthe B-l bearings ofthe invention were achieved without sacrificing other important properties of engine bearings, namely conformability, embedibility, wear resistance and 11 seizure resistance. All properties were found to be within acceptable limits, including conformability and embedibility. The invention has been described in an illustrative manner with regard to particular embodiments, and it is to be understood that the terminology which has been used is intended to be in the nature of words of description rather than of limitation. For example, it will be appreciated that the thickness expressed for the layers 48, 50 ofthe multilayer oveφlate 46 are to be considered nominal or average thicknesses within normal manufacturing limitations, and that in some cases the oveφlate 46 may be thicker in some regions ofthe bearing 46 and thinner in others. Accordingly, it is to be understood that multilayer oveφlates that may be somewhat thicker or thinner than 15 μm, and lead- tin-copper underlayers 48 and tin overlayers 50 that likewise may be somewhat thicker or thinner than 10 μm and 5 μm, respectively, and yet achieve the same or similar results are contemplated within the scope and spirit ofthe invention as equivalent structures Obviously, many modifications and variations ofthe present invention are possible in light ofthe above teachings. It is, therefore, to be understood that within the scope ofthe appended claims wherein parenthetical reference numerals are merely for convenience and are not in any way to be limiting, the invention may be practiced as otherwise than as specifically described. 12

Claims: What is claimed is: 1. A multilayer plain bearing comprising: a base lining member (40) including a rigid metal backing (36) and a liner (38) of bearing metal formed on said backing (36); and characterized by a multilayer oveφlate (46) formed on said base lining member (40) including an underlayer (48) of lead-tin-copper alloy having a predetermined thickness of about 10 μm and a functional overlayer (50) of tin having a predetermined thickness of about 5 μm. 2. The bearing of claim 1 further characterized by said tin overlayer (50) comprising essentially pure tin. 3. The bearing of claim 2 further characterized by said tin overlayer (50) comprising an electrodeposited tin layer (50) plated from a fluoborate electrolyte solution at a current density greater than about 20 amps/ft 2 . 4. The bearing of claim 2 further characterized by said tin overlayer (50) comprising an electrodeposited tin layer (50) plated from a fluoborate electrolyte solution at a current density of about 75 amps/ft 2 . 5. The bearing of claim 1 further characterized by said lead- tin-copper alloy of said underlayer (48) having about 8-16% by wt. tin, 0- 10% by wt. copper, and the balance lead. 6. The bearing of claim 1 further characterized by said lead- tin-copper alloy of said underlayer (48) having about 10% by wt. tin, 2% by wt. copper, and the balance lead. 13 7. The bearing of claim 1 further characterized by said liner (38) comprising a material selected from a group of materials consisting essentially of copper-lead, and aluminum alloys. 8. The bearing of claim 1 further characterized by said base lining member (36) including a metallic layer (44) inteφosed between said liner (38) and said oveφlate (46). 9. The bearing of claim 8 further characterized by said metallic layer (44) comprising a material selected from a group consisting essentially of nickel and copper. 10. The bearing of claim 1 further characterized by including a flash plating (52) having a predetermined thickness substantially less than that of said overlayer (50) applied to at least said backing (36) of said bearing. 11. A multilayer plain engine bearing comprising: a base lining member (40) including a steel backing (36), a liner (38) of copper-lead bearing metal formed on said backing (36), and a diffusion barrier layer (44) of nickel formed on said liner (38); and characterized by a multilayer oveφlate (46) applied to said barrier diffusion layer (44) including an underlayer (48) of lead-tin-copper alloy having a predetermined thickness of about 10 μm and an overlayer 50 of tin having a predetermined thickness of about 5 μm. 12. An internal combustion engine assembly comprising: at least one rotatable component (24); 14 at least one plain bearing (26) journaling said rotatable component (24), said bearing (26) including a base lining member (40) having a rigid metal backing (36) and a liner (38) of bearing material formed on said backing (36); and characterized by a multilayer oveφlate (46) formed on said base lining member (40) including an underlayer (48) of a lead-tin-copper alloy having a predetermined thickness of about 10 μm and an overlayer (50) of tin having a predetermined thickness of about 5 μm. 13. A method of fabricating a multilayer plain engine bearing comprising the steps of: preparing a base lining member (40) including forming a rigid metal backing (36) and forming a liner (38) of metallic bearing material on the backing (36); and characterized by forming a multilayer oveφlate (46) on the base lining member (40) including forming an underlayer (48) of a lead- tin-copper alloy having a predetermined thickness of about 10 μm and forming a functional overlayer (50) of tin on the underlayer (48) having a predetermined thickness of about 5 μm. 14. The method of claim 13 further characterized by forming the tin overlayer (50) by electrodepositing the overlayer (50) from a fluoborate electrolyte plating bath at a current density of greater than about 20 amps/ft 2 . 15 15. The method of claim 13 further characterized by forming the tin overlayer (50) by electrodepositing the overlayer (50) from a fluoborate electrolyte plating bath at a current density of about 75 amps/ft 2 . 16. The method of claim 13 further characterized by forming a flash plating (52) to at least the metal backing (36) having a predetermined thickness substantially less than that ofthe overlayer (50). 16

Inventors: DUGAN DANIEL E, LYTWYNEC MICHAEL D, TOTH JAMES R, DUGAN, DANIEL, E., LYTWYNEC, MICHAEL, D., TOTH, JAMES, R.
Applicants: FEDERAL MOGUL CORP, FEDERAL-MOGUL CORPORATION
Application year: 1999
Main classification: F16C33
IPC codes: B32B15, C25D7, F16C9, F16C33