HIGH PURITY TANTALUM AND PRODUCTS CONTAINING THE SAME LIKE SPUTTER TARGETS

Abstract: High purity tantalum metals and alloys containing the same are described. The tantalum metal preferably has a purity of at least 99.995 % and more preferably at least 99.999 %. In addition, tantalum metal and alloys thereof are described, which either have a grain size of about 50 microns or less, or a texture in which a (100) intensity within any 5 % increment of thickness is less than about 15 random, or an incremental log ratio of (111):(100) intensity of greater than about -4.0, or any combination of these properties. Also decribed are articles and components made from the tantalum metal which include, but are not limited to, sputtering targets, capacitor cans, resistive film layers, wire, and the like. Also disclosed is a process for making the high purity metal which includes the step of reacting a salt-containing tantalum with at least one compound capable of reducing this salt to tantalum powder and a second salt in a reaction container. The reaction container or liner in the reaction container and the agitator or liner on the agitator are made from a metal material having the same of higher vapor pressure of melted tantalum. The high purity tantalum preferably has a fine and uniform microstructure.

Description: HIGH PURITY TANTALUM AND PRODUCTS CONTAINING THE SAME LIKE SPUTTER TARGETS BACKGROUND OF THE INVENTION The present invention relates to metals in particular tantalum, and products made from tantalum as well as methods of making and processing the tantalum In industry, there has always been a desire to form higher purity metals for a variety of reasons With respect to tantalum, higher purity metals are especially desirable due to tantalum's use as a sputtering target and its use in electrical components such as capacitors Thus, impurities in the metal can have an undesirable effect on the properties of the articles formed from the tantalum When tantalum is processed the tantalum is obtained from ore and subsequenth crushed and the tantalum separated from the crushed ore through the use of an acid solution and density separation of the acid solution containing the tantalum from the acid solution containing niobium and other impurities The acid solution containing the tantalum is then crystallized into a salt and this tantalum containing salt is then reacted with pure sodium in a vessel having an agitator typically constructed of nickel alloy material, wherein tungsten or molybdenum is part of the nickel alloy The vessel will typically be a double walled \ essel with pure nickel in the interior surface The salt is then dissolved in water to obtain tantalum powder However, during such processing, the tantalum powder is contaminated by the various surfaces that it comes in contact with such as the tungsten and/or molybdenum containing surfaces Many contaminants can be volatized during subsequent melting, except highly soluble refractory metals (e g , Nb. Mo. and W) These impurities can be quite difficult or impossible to remove, thus pre\entιng a very high purity tantalum product Accordingly, there is a desire to obtain higner purity tantalum products which substantially avoid the contaminations obtained during the processing discussed above Also, there is a desire to have a tantalum product ha\ ιng higher purity, a fine grain size, and/or a uniform texture Qualities such as fine grain size can be an important for sputtering targets made from tantalum since fine grain size can lead to ιmpro\ed uniformity of thickness of the sputtered deposited film Further, other products containing the tantalum having fine grain size can lead to improved homogeneity of deformation and enhancement of deep drawability and stretchability which are beneficial in making capacitors cans, laboratory crucibles, and increasing the lethality of explosively formed penetrators (EFP's). Uniform texture in tantalum containing products can increase sputtering efficiency (e.g., greater sputter rate) and can increase normal anisotropy (e.g., increased deep drawability), in perform products. SUMMARY OF THE PRESENT INVENTION A feature of the present invention is to provide a high purity tantalum product exhibiting a fine grain structure and/or uniform texture. Another feature of the present invention is to provide articles, products, and/or components containing the high purity tantalum. An additional feature of the present invention is to provide processes to make the high purity tantalum product as well as the articles, products, and/or components containing the high purity tantalum. Additional features and advantages of the present invention will be set forth in part in the description which follows, and in part will be apparent from the description, or may be learned by practice of the present invention. The objectives and other advantages of the present invention will be realized and attained by means of the elements and combinations particularly pointed out in the description and appended claims. To achieve these and other advantages, and in accordance with the purpose of the present invention, as embodied and broadly described herein, the present invention relates to tantalum metal having a purity of at least 99.995% and more preferably at least 99.999%. The tantalum metal preferably has a fine grain structure and/or uniform texture. The present invention further relates to an alloy or mixture comprising tantalum, wherein the tantalum present in the alloy or mixture has a purity of at least 99.995% and more preferably at least 99.999%. The alloy or mixture (e.g., at least the tantalum present in the alloy or mixture) also preferably has a fine grain structure and/or uniform texture. The present invention also relates to a high purity tantalum, e.g., suitable for use as a sputtering target, having a fully recrystallized grain size with an average grain size of about 150 μm or less and/or having a primary (1 1 l)-type texture substantially throughout the thickness of the tantalum and preferably throughout the entire thickness of the tantalum metal and/or having an absence of strong (100) texture bands within the thickness of the tantalum. The present invention further relates to manufacturing plate and sheet from the above- mentioned tantalum by flat-forging the tantalum, machining into rolling slabs, annealing rolling slabs, rolling into plate or sheet, then annealing the plate or sheet. Final products such as sputtering targets can be then machined from the annealed plate or sheet. The present invention also relates to a sputtering target comprising the above-described tantalum and/or alloy. The sputtering target can also be formed by radial forging and subsequent round processing to produce billets or slugs, which are then forged and rolled to yield discs, which can then be machined and annealed. The present invention further relates to resistive films and capacitors comprising the above- described tantalum and/or alloy. The present invention also relates to articles, components, or products which comprise at least in part the above-described tantalum and/or alloy. Also, the present invention relates to a process of making the above-described tantalum which involves reacting a salt-containing tantalum with pure sodium or other suitable salt in a reactive container or pot and an agitator which both are made from or have a liner comprising a metal or alloy thereof which has the same or higher vapor pressure as tantalum at the melting point of tantalum. The present invention further relates to processing tantalum powder by melting the tantalum powder in a high vacuum of 10 "" torr or more. The pressure above the melt is lower than the vapor pressures of the impurities existing in the tantalum. Preferably, the melting of the tantalum powder is accomplished by electron beam melting. It is to be understood that both the foregoing general description and the following detailed description are exemplary and explanatory only and are intended to provide further explanation of the present invention, as claimed. BRIEF DESCRIPTION OF THE DRAWINGS Figures 1(A-B)-11(A-B) are graphs and corresponding data relating to texture gradient (incremental thickness vs. random) and log ratio (111):(100) gradients (incremental thickness vs. Ln (1 11/100)) of high purity tantalum plates of the present invention. DETAILED DESCRTPTION OF THE PRESENT INVENTION The present invention relates to a tantalum metal having a purity of at least 99.995%. Preferably, the tantalum metal has a purity of at least 99.999% and can range in purity from about 99.995% to about 99.999% or more. Other ranges include about 99.998% to about 99.999% and from about 99.999% to about 99.9992% and from about 99.999% to about 99.9995%. The present invention further relates to a metal alloy which comprises the high purity tantalum metal, such as a tantalum based alloy or other alloy which contains the high purity tantalum as one of the components of the alloy. The impurities that may be present in the high purity tantalum metal are less than or equal to .005% and typically comprise other body-centered cubic (bcc) refractory metals of infinite solubility in tantalum, such as niobium, molybdenum, and tungsten. The tantalum metal and alloys thereof containing the tantalum metal preferably have a texture which is advantageous for particular end uses, such as sputtering. In other words, when the tantalum metal or alloy thereof is formed into a sputtering target having a surface and then sputtered, the texture of the tantalum metal in the present invention leads to a sputtering target which is easily sputtered and, very few if any areas in the sputtering target resist sputtering. Further, with the texture of the tantalum metal of the present invention, the sputtering of the sputtering target leads to a very uniform sputtering erosion thus leading to a sputtered film which is therefore uniform as well. It is preferred that the tantalum having any purity, but preferably a purity of at least about 99.995%), has a grain size of about 150 microns or less. Preferably, the tantalum metal is at least partially recrystallized, and more preferably at least about 80% of the tantalum metal is recrystallized and even more preferably at least about 98% of the tantalum metal is recrystallized. Most preferably, the tantalum metal is fully recrystallized. Also, it is preferred that the tantalum metal have a fine texture. More preferably the texture is such that the (100) peak intensity within any 5% incremental thickness of the tantalum is less than about 15 random, and/or has a natural log (Ln) ratio of (11 1):(100) center peak intensities within the same increment greater than about - 4.0 (i.e., meaning, -4.0, -3.0, -2.0, -1.5, -1.0 and so on) or has both the (100) centroid intensity and the ratio. The center peak intensity is preferably from about 0 random to about 10 random, and more preferably is from about 0 random to about 5 random. Other (100) centroid intensity ranges include, but are not limited to, from about 1 random to about 10 random and from about 1 random to about 5 random. Further, the log ratio of (1 1 1):(100) center peak intensities is from about - 4.0 to about 15 and more preferably from about -1.5 to about 7.0. Other suitable ranges of log ratios, include, but are not limited to, about -4.0 to about 10, and from about -3.0 to about 5.0. Most preferably, the tantalum metal has the desired purity of at least about 99.995% and the preferred grain size and preferred texture with regard to the (100) incremental intensity and the (1 11):(100) ratio of incremental centroid intensities. The method and equipment that can be used to characterize the texture are described in Adams et al., Materials Science Forum, Vol. 157-162 (1994), pp. 31-42; Adams et al., Metallurgical Transactions A, Vol. 24A, April 1993-No. 4, pp. 819-831 : Wright et al., International Academic Publishers, 137 Chaonei Dajie, Beijing, 1996 ("Textures of Material: Proceedings of the Eleventh International Conference on Textures of Materials); Wright, Journal of Computer-Assisted Microscopy, Vol. 5, No. 3 (1993), all incorporated in their entirety by reference herein. The high purity tantalum metal of the present invention can be used in a number of areas. For instance, the high purity tantalum metal can be made into a sputtering target or into chemical energy (CE) munitions warhead liner which comprises the high purity metal. The high purity metal can also be used and formed into a capacitor anode or into a resistive film layer. The tantalum metal of the present invention can be used in any article or component which conventional tantalum is used and the methods and means of making the various articles or components containing the conventional tantalum can be used equally here in incorporating the high purity tantalum metal into the various articles or components. For instance, the subsequent processing used in making sputtering targets, such as the backing plate, described in U.S. Patent Nos. 5,753,090, 5,687,600, and 5,522,535 can be used here and these patents are incorporated in their entirety by reference herein. Generally, a process that can be used to make the high purity tantalum metal of the present invention involves a refining process, a vacuum melting process, and a thermal mechanical process. In this process or operation, the refining process involves the steps of extracting tantalum metal preferably in the form a powder from ore containing tantalum and preferably the ore-containing tantalum selected has low amounts of impurities, especially, low amounts of niobium, molybdenum, and tungsten. More preferably, the amount of niobium, molybdenum, and tungsten is below about 10 ppm, and most preferably is below about 8 ppm. Such a selection leads to a purer tantalum metal. After the refining process, the vacuum melting process is used to purge low melting point impurities, such as alkyde and transition metals from the tantalum while consolidating the tantalum material into a fully dense, malleable ingot. Then, after this process, a thermal mechanical process can be used which can involve a combination of cold working and annealing of a tantalum which further ensures that the preferred grain size and/or preferred texture and uniformity are achieved, if desired. The high purity tantalum metal preferably may be made by reacting a salt-containing tantalum with at least one agent (e.g., compound or element) capable of reducing this salt to the tantalum metal and further results in the formation of a second salt in a reaction container. The reaction container can be any container typically used for the reaction of metals and should withstand high temperatures on the order of about 800°C to about 1,200°C. For pu oses of the present invention, the reaction container or the liner in the reaction container, which comes in contact with the salt-containing tantalum and the agent capable of reducing the salt to tantalum, is made from a material having the same or higher vapor pressure as tantalum at the melting point of the tantalum. The agitator in the reaction container can be made of the same material or can be lined as well. The liner can exist only in the portions of the reaction container and agitator that come in contact with the salt and tantalum. Examples of such metal materials which can form the liner or reaction container include, but are not limited to, metal-based materials made from nickel, chromium, iron, manganese, titanium, zirconium, hafnium, vanadium, ruthenium, cobalt, rhodium, palladium, platinum, or any combination thereof or alloy thereof as long as the alloy material has the same or higher vapor pressure as the melting point of tantalum metal. Preferably, the metal is a nickel or a nickel-based alloy, a chromium or a chromium- based alloy, or an iron or an iron-based alloy. The liner, on the reaction container and/or agitator, if present, typically will have a thickness of from about .5 cm to about 3 cm. Other thicknesses can be used. It is within the bounds of the present invention to have multiple layers of liners made of the same or different metal materials described above. The salt-containing tantalum can be any salt capable of having tantalum contained therein such as a potassium-fluoride tantalum. With respect to the agent capable of reducing the salt to tantalum and a second salt in the reaction container, the agent which is capable of doing this reduction is any agent which has the ability to result in reducing the salt-containing tantalum to just tantalum metal and other ingredients (e.g. salt(s)) which can be separated from the tantalum metal, for example, by dissolving the salts with water or other aqueous sources. Preferably, this agent is sodium. Other examples include, but are not limited to, lithium, magnesium, calcium, potassium, carbon, carbon monoxide, ionic hydrogen, and the like. Typically, the second salt which also is formed during the reduction of the salt-containing tantalum is sodium fluoride. Details of the reduction process which can be applied to the present invention in view of the present application are set forth in Kirk-Othmer, Encyclopedia of Chemical Technology, 3 rd Edition, Vol. 22, pp. 541-564, U.S. Patent Nos. 2,950,185; 3,829,310; 4,149,876; and 3,767,456. Further details of the processing of tantalum can be found in U.S. Patent Nos. 5,234,491 ; 5,242,481 ; and 4,684,399. All of these patents and publications are incorporated in their entirety by reference herein. The above-described process can be included in a multi-step process which can begin with low purity tantalum, such as ore-containing tantalum. One of the impurities that can be substantially present with the tantalum is niobium. Other impurities at this stage are tungsten, silicon, calcium, iron, manganese, etc. In more detail, low purity tantalum can be purified by mixing the low purity tantalum which has tantalum and impurities with an acid solution. The low purity tantalum, if present as an ore, should first be crushed before being combined with an acid solution. The acid solution should be capable of dissolving substantially all of the tantalum and impurities, especially when the mixing is occurring at high temperatures. Once the acid solution has had sufficient time to dissolve substantially, if not all, of the solids containing the tantalum and impurities, a liquid solid separation can occur which will generally remove any of the undissolved impurities. The solution is further purified by liquid-liquid extraction. Methyl isobutyl ketone (MIBK) can be used to contact the tantalum rich solution, and deionized water can be added to create a tantalum fraction. At this point, the amount of niobium present in the liquid containing tantalum is generally below about 25 ppm. Then, with the liquid containing at least tantalum, the liquid is permitted to crystallize into a salt with the use of vats. Typically, this salt will be a potassium tantalum fluoride salt. More preferably, this salt is K 2 TaF 7 . This salt is then reacted with an agent capable of reducing the salt into 1) tantalum and 2) a second salt as described above. This compound will typically be pure sodium and the reaction will occur in a reaction container described above. As stated above, the second salt byproducts can be separated from the tantalum by dissolving the salt in an aqueous source and washing away the dissolved salt. At this stage, the purity of the tantalum is typically 99.50 to 99.99% Ta. Once the tantalum powder is extracted from this reaction, any impurities remaining, including any contamination from the reaction container, can be removed through melting of the tantalum powder. The tantalum powder can be melted a number of ways such as a vacuum arc remelt or an electron beam melting. Generally, the vacuum during the melt will be sufficient to remove substantially any existing impurities from the recovered tantalum so as to obtain high purity tantalum. Preferably, the melting occurs in a high vacuum such as IO "4 torr or more. Preferably, the pressure above the melted tantalum is lower than the vapor pressures of the metal impurities in order for these impurities, such as nickel and iron to be vaporized. The diameter of the cast ingot should be as large as possible, preferably greater than 9 '/. inches. The large diameter assures a greater melt surface to vacuum interface which enhances purification rates. In addition, the large ingot diameter allows for a greater amount of cold work to be imparted to the metal during processing, which improves the attributes of the final products. Once the mass of melted tantalum consolidates, the ingot formed will have a purity of 99.995% or higher and preferably 99.999% or higher. The electron beam processing preferably occurs at a melt rate of from about 300 to about 800 lbs. per hour using 20,000 to 28,000 volts and 15 to 40 amps, and under a vacuum of from about 1 X 10 " to about 1 X 10 " Torr. More preferably, the melt rate is from about 400 to about 600 lbs. per hour using from 24,000 to 26,000 volts and 17 to 36 amps, and under a vacuum of from about 1 X 10 to 1 X IO "3 Torr. With respect to the VAR processing, the melt rate is preferably of 500 to 2.000 lbs. per hour using 25-45 volts and 12,000 to 22.000 amps under a vacuum of 2 X 10 "" to 1 X 10 Torr, and more preferably 800 to 1200 lbs. per hour at from 30 to 60 volts and 16,000 to 18,000 amps, and under a vacuum of from 2 X 10 "" to 1 X lO^ Torr. The high purity tantalum ingot can then be thermomechanically processed to produce the high purity tantalum containing product. The fine, and preferably fully recrystallized, grain structure and/or uniform texture is imparted to the product through a combination of cold and/or warm working and in- process annealing. The high purity tantalum product preferably exhibits a uniform texture of mixed or primary ( 1 1 1) throughout its thickness as measured by orientation imaging microscopy (OIM) or other acceptable means. With respect to thermomechanical processing, the ingot can be subjected to rolling and/or forging processes and a fine, uniform microstructure having high purity can be obtained. The high purity tantalum has an excellent fine grain size and/or a uniform distribution. The high purity tantalum preferably has an average recrystallized grain size of about 150 microns or less, more preferably about 100 microns or less, and even more preferably about 50 microns or less. Ranges of suitable average grain sizes include from about 25 to about 150 microns; from about 30 to about 125 microns, and from about 30 to about 100 microns. The resulting high purity metal of the present invention, preferably has 10 ppm or less metallic impurities and preferably 50 ppm or less O 2 , 25 ppm or less N 2 , and 25 ppm or less carbon. If a purity level of about 99.995 is desired, than the resulting high purity metal preferably has metallic impurities of about 50 ppm or less, and preferably 50 ppm or less O2, 25 ppm or less N 2 , and 25 ppm or less carbon. With respect to taking this ingot and forming a sputtering target, the following process can be used. In one embodiment, the sputtering target made from the high purity tantalum metal can be made by mechanically or chemically cleaning the surfaces of the tantalum metal, wherein the tantalum metal has a sufficient starting cross-sectional area to permit the subsequent processing steps described below. Preferably the tantalum metal has a cross-sectional area of at least 9 ] Λ inches or more. The next step involves flat forging the tantalum metal into one or more rolling slabs. The rolling slab(s) has a sufficient deformation to achieve substantially uniform recrystallization after the annealing step immediately following this step as described below. The rolling slab(s) is then annealed in vacuum and at a sufficient temperature to achieve at least partial recystallization of the rolling slab(s). Preferred annealing temperatures and times are set forth below and in the examples. The rolling slab(s) is then subjected to cold or warm rolling in both the perpendicular and parallel directions to the axis of the starting tantalum metal (e.g., the tantalum ingot) to form at least one plate. The plate is then subjected to flattening (e.g., level rolling). The plate is then annealed a final time at a sufficient temperature and for a sufficient time to have an average grain size of equal to or less than about 150 microns and a texture substantially void of (100) textural bands. Preferably, no (100) textural bands exist. The plate can then be mechanically or chemically cleaned again and formed into the sputtering target having any desired dimension. Typically, the flat forging will occur after the tantalum metal is placed in air for at least about 4 hours at temperatures ranging from ambient to about 370°C. Also, preferably before cold rolling, the rolling slabs are annealed at a temperature (e.g., from about 950°C to about 1500°C) and for a time (e.g., from about '/_ hour to about 8 hours) to achieve at least partial recrystallization of the tantalum metal. Preferably the cold rolling is transverse rolling at ambient temperatures and the warm rolling is at temperatures of less than about 370°C. With respect to annealing of the tantalum plate, preferably this annealing is in a vacuum annealing at a temperature and for a time sufficient to achieve complete recrystallization of the tantalum metal. The examples in this application set forth further preferred details with respect to this processing. Another way to process the tantalum metal into sputtering targets involves mechanically or chemically clean surfaces of the tantalum metal (e.g., the tantalum ingot), wherein the tantalum metal has a sufficient starting cross-sectional area to permit the subsequent processing as described above. The next step involves round forging the tantalum metal into at least one rod, wherein the rod has sufficient deformation to achieve substantially uniform recrystallization either after the annealing step which occurs immediately after this step or the annealing step prior to cold rolling. The tantalum rod is then cut into billets and the surfaces mechanically or chemically cleaned. An optional annealing step can occur afterwards to achieve at least partial recrystallization. The billets are then axially forged into performs. Again, an optional annealing step can occur afterwards to achieve at least partial recrystallization. However, at least one of the optional annealing steps or both are done. The performs are then subjected to cold rolling into at least one plate. Afterwards, the surfaces of the plate(s) can be optionally mechanically or chemically clean. Then, the final annealing step occurs to result in an average grain size of about 150 microns or less and a texture substantially void of (100) textural bands, if not totally void of (100) textural bands. The round forging typically occurs after subjecting the tantalum metal to temperatures of about 370°C or lower. Higher temperatures can be used which results in increased oxidation of the surface. Preferably, prior to forging the billets, the billets are annealed. Also, the performs, prior to cold rolling can be annealed. Typically, these annealing temperatures will be from about 900°C to about 1200°C. Also, any annealing is preferably vacuum annealing at a sufficient temperature and for a sufficient time to achieve recrystallization of the tantalum metal. Preferably, the sputtering targets made from the high purity tantalum have the following dimensions: a thickness of from about 0.080 to about 1.50", and a surface area from about 7.0 to about 1225 square inches. The high purity tantalum preferably has a primary or mixed (111) texture, and a minimum (100) texture throughout the thickness of the sputtering target, and is sufficiently void of (100) textural bands. The tantalum metal of the present invention can be used in any application or product that uses conventional tantalum metal as a component or as part of a component. For instance, the tantalum metal can be a component or part of a component in integrated circuits, such as semiconductors and the like. The designs described in U.S. Patent Nos.: 5,987,635; 5,987,560; 5,986,961; 5,986,960; 5,986,940; 5,986,496; 5,986,469; 5,986,410; 5,986,320; 5,986,299; 5,986,294; 5,985,697; and 5,982,218 can be used as well as other conventional designs and each of these patents are incorporated herein in their entireties by reference. The tantalum metal can be present in any device which typically uses sputtering techniques to deposit metal to form a component or part of a component on a device. The present invention will be further clarified by the following examples, which are intended to be purely exemplary of the present invention. EXAMPLES Example 1 Numerous sublots of sodium-reduced commercial-grade tantalum powder, each weighing about 200-800 lbs., were chemically analyzed for suitability as 99.999% Ta feedstock for electron beam melting. Representative samples from each powder lot were analyzed by Glow Discharge Mass Spectrometry (GDMS): powder sublots having combined niobium (Nb), molybdenum (Mo), and tungsten (W) impurity content less than 8 ppm were selected for melting. The selected Ta powder sublots were then blended in a V-cone blender to produce a homogeneous 4000 pound powder master lot. which was again analyzed by GDMS to confirm purity. Next, the powder was cold isostatically pressed (CIP'ed) into green logs approximately 5.5"- 6.5" in diameter, each weighing nominally 300 pounds. The pressed logs were then degassed by heating at 1450°C for 2 hours at a vacuum level of about 10 " -10 ' torr. For this operation, the logs were covered with tantalum sheets to prevent contamination from the furnace elements. The degassed logs were then side fed into a 1200KW EB furnace and drip melted at a rate of 400 lbs./hr. into a 10" water-cooled copper crucible under a vacuum less than IO "3 torr. Once cooled, the resulting first-melt ingot was inverted, hung in the same furnace, and remelted using the same EB melting parameters. The 2" melt ingot was again inverted and remelted a third time, but into a 12" crucible at a melt rate of 800 lbs./hr. A sample was taken from the sidewall of the resulting ingot for chemical analysis by Glow Discharge Mass Spectrometry (GDMS). Results confirmed that the Ta ingot was 99.9992% pure. Example 2 A potassium fluotantalate (K 2 TaF ) was obtained and upon spark source mass spec analysis, the K 2 TaF 7 exhibited 5 ppm or less niobium. Levels of Mo and W were also analyzed by spectrographic detection and levels were below 5 ppm for Mo and below 100 ppm for W. In particular, the K?TaF 7 had levels of Nb of 2 ppm or less, of Mo of less than 1 ppm and of W of less than or equal to 2 ppm. In each sample, the total recorded amount of Nb, Mo, and W was below 5 ppm. Four lots of 2,200 lbs. each were analyzed. One of the lots was transferred to KDEL reactor which used a pure nickel vessel and a Hastelloy X agitator. The Hastelloy X agitator contained 9% Mo and 0.6% W. The shaft and paddles of the agitator were then shielded with 1/16" nickel sheet using welding to clad all surfaces exposed to the reaction. A standard sodium reduction process was used except as noted below. The lot was subjected to the agitator in the presence of pure sodium to form tantalum powder. The tantalum powder was then washed with water and subjected to acid treating and then steam drying and then screening to - 100 mesh. A sample from each batch was then submitted for glow discharge mass spec analysis. The two tables (Tables 1 and 2) below show the starting analysis for the ^TaF? and the final analysis of the tantalum recovered. Table 1 K 2 TaF 7 Spark Source Mass Spec (SSMS) Analysis (metal to salt basis) Table 2 As can be seen in the above tables, a high purity tantalum powder suitable for electron beam melting into an ingot can be obtained and purities on the order of 99.999% purity can be obtained by the processing shown in Example 1. Example 3. Two distinct process methodologies were used. First, a 99.998% pure tantalum ingot was used which was subjected to three electron beams melts to produce a 12 inch nominal diameter ingot. The ingot was machined clean to about 1 11 inch diameter and then heated in air to about 260°C for 4-8 hours. The ingot was then flat forged, cut, and machined into slabs (approximately 4 inch by 10 inch with a length of approximately 28 inch to 32 inch) and then acid cleaned with HF/HNO 3 /water solution. The slabs were annealed at 1050, 1 150, and 1300°C under vacuum of 5 X IO "4 Torr for 2 hours, then cold rolled into plate stock of 0.500 and 0.250" gauge. This cold rolling was accomplished by taking a 4 inch thick by 10 inch wide by 30 inch long slab and rolling it perpendicular to the ingot axis at 0.200 inch per pass to 31 inches wide. The plate was then rolled parallel to the ingot axis at 0.100 inch per pass to 0.650 inch thick or 0.500 inch thick. Both rollings were done on a 2-High breakdown rolling mill. Each of the plates were rolled by multiples passes of 0.050 inch per pass and then 0.025 inch per pass with final adjustments to meet a finish gauge of 0.500 inch plate or 0.250 inch plate, using a four high finishing rolling mill. The plates were then subjected to a final annealing at temperatures of from 950 - 1 150°C. The alternative process began with a 99.95 % pure Ta which was subjected to three electron beam melts to produce an ingot as described above prior to being forged. The ingot was then round forged using a GFM rotary forge to 4" diameter after multiples passes of about 20%> reduction in area per pass. From this intermediate stock, 4 billets (3.75"0 x 7" long) were machined, and 2 billets (labeled A and B) were annealed at 1050°C while billets C and D remained unannealed. Next, the billets were upset forged to performs of height of 2.5", after which performs A and C were annealed at 1050°C. The performs were then clock rolled to a thickness of about 0.400" to yield discs of a diameter of approximately 14". This was accomplished by taking multiple passes of 0.200 inch per pass to about 0.5250 inch thick. The discs were then rolled to about 0.5 inch thick by multiple passes of 0.100 inch per pass. Then, the discs were clocked rolled on a four high finishing mill in three passes of 0.050 inch, 0.025 inch, and 0.015 inch reductions per pass to yield a disc of about 0.400 inch thick by about 14 inch diameter. A quarter of the disc was cut into four wedges and final annealed at temperatures of 950-1100°C. Table 4 below summarizes this processing. Metallographic and texture analysis was conducted on longitudinal sections of the plate material (measurement face parallel to the final rolling direction) and on radial sections of the forged and rolled discs (measurement face parallel to the radius of the discs). METALLURGICAL ANALYSIS Grain size and texture were measured along the longitudinal or radial directions of samples taken from rolled plate and forged and rolled discs, respectively. Grain size was measured using ASTM procedure E-1 12. Results from the annealing studies on products produced via the flat and round processes are given in Tables 3 and 4, respectively. Intermediate annealing treatments had no noticeable influence on the grain size of the finished product. Also, for plate, the final grain sizes of 0.500 and 0.250" thick tantalum were comparable. The only variable found to significantly effect the grain size of the materials was the final anneal temperature: the higher the final anneal temperature, the larger the resulting grain size. In plate, grain sizes of ASTM 6.5 - 7.0 were measured in samples from product annealed at 1000 and 950°C. However, each of these samples showed evidence of elongated and/or unrecrystallized regions at or near the surface, and recrystallization values were reported to be 98- 99%. For plates annealed at 1050, 1 100, and 1 150°C, ASTM grain sizes ranged from 5.3 to 3.7, with all samples being 100% recrystallized. For the round-processed discs, all samples were reported to be 100%o recrystallized, with the exception of Disc C annealed at 950°C which was 99% recrystallized. Grain sizes of ASTM 7.1- 7.2, 6.1-6.8, and 5.9-5.9 were measured in the disc samples annealed at 950, 1000, and 1050°C, respectively. Annealing at 1 100°C produced grain sizes of ASTM 4.0-4.5. For both processes, these findings demonstrate that a fully recrystallized grain size of 50 μrn or finer is achievable using either the plate rolling or the billet forging process at a preferred final anneal temperature of from about 950 to about 1050°C. Should the unrecrystallized areas be limited to only the surface regions of the plate, then they can be removed by machining. Texture Measurement Technique: A limited number of samples (chosen based on metallurgical results) were used for texture analysis. Mounted and polished samples, previously prepared for metallurgical analysis, were employed as texture samples after being given a heavy acid etch prior to texture measurement. Orientation Imaging Microscopy (OIM) was chosen as the method of texture analysis because of its unique ability to determine the orientation of individual grains within a polycrystalline sample. Established techniques such as X-ray or neutron diffraction would have been unable to resolve any localized texture variations within the thickness of the tantalum materials. For the analysis, each texture sample was incrementally scanned by an electron beam (within an SEM) across its entire thickness; the backscatter Kikuchi patters generated for each measurement point was then indexed using a computer to determine the crystal orientation. From each sample, a raw-data file containing the orientations for each data point within the measurement grid array was created. These files served as the input data for subsequently producing grain orientation maps and calculating pole figures and orientation distribution functions (ODFs). By convention, texture orientations are described in reference to the sample-normal coordinate system. That is, pole figures are "standardized" such that the origin is normal to the plate surface, and the reference direction is the rolling (or radial) direction; likewise, ODFs are always defined with respect to the sample-normal coordinate system. Terminology such as "a (1 1 1) texture" means that the (1 1 1) atomic planes are preferentially oriented to be parallel (and the (1 1 1) pole oriented to be normal) with the surface of the plate. In the analyses, the crystal orientations were measured with respect to the sample longitudinal direction. Therefore, it was necessary to transpose the orientation data from the longitudinal to sample-normal coordinate system as part of the subsequent texture analysis. These tasks were conducted through use of computer algorithms. Grain Orientation Maps: Derived from principles of presenting texture information in the form of inverse pole figures, orientation maps are images of the microstructure within the sample where each individual grain is "color-coded " based on its crystal lographic orientation relative to the normal direction of the plate of disc from which it was taken. To produce these images, the crystal axes for each grain (determined along the longitudinal direction of the texture sample by OIM) were tilted 90° about the transverse direction so to align the crystal axes to the normal direction of the sample. Orientation maps serve to reveal the presence of texture bands or gradients through the thickness on the product; in tantalum, orientation maps have shown that large, elongated grains identified by optical microscopy can be composed of several small grains with low-angle grain boundaries. Analysis of the Texture Results: OIM scans were taken along the thickness of each sample provided; for the 0.500" plate samples, separate measurements were made for the top and the bottom portions of the plate and reported separately. The orientation maps were visually examined to qualitatively characterize the texture uniformity through the sample thickness. To attain a quantifiable description of the texture gradients and texture bands in the example materials, the measured EBSD data was partitioned into 20 subsets, with each representing a 5% increment of depth through the thickness of the sample. For each incremental data set, an ODF was first calculated, then (100) and (1 1 1) centroid intensities determined numerically using techniques reported elsewhere. The equipment and procedures described in S. Matthies et al., Materials Science Forum, Vol. 157-162 (1994), pp. 1647-1652 and S. Matthies et al., Materials Science Forum, Vol. 157-162 (1994), pp. 1641-1646 were applied, and these publications are incorporated in their entirety herein by reference. The texture gradients were then described graphically by plotting the (100) and (1 1 1 ) intensities, as well as the log ratio of the (100):(1 1 1 ). as a function depth of the sample. These results are set forth in Figures 1 (A and B) through Figures 1 1 (A and B). The heavy-gauge tantalum plate exhibited the most uniform through-thickness texture; the only sample containing texture bands was that processed with a slab anneal of 1300°C and a final anneal of 1000°C. In addition, the 0.500" plate materials also had a relative weak (most random) texture base on pole figure and ODF analysis. Compared to the heavy plate, the 0.250' sheets contained a slight to moderate texture gradient and some evidence of texture banding. Also, the thin-gauge plates showed a more defined (1 1 1) texture in the ODFs and an increased prominence of (100). The greatest variability in terms of texture uniformity and banding was found in the forged and rolled discs. Unlike the metallurgical properties, the texture of forged and rolled discs was effected by the use of intermediate annealing. For discs A, B, and C, each of which were processed with one or two intermediate annealing steps, the texture gradients ranged from negligible to strong (depending to processing parameters) with slight - if any - banding. However, for disc D, which was worked from ingot to final discs without intermediate annealing, the resultant product contained less desirable strong texture gradients and sharp texture bands. Similarly, disc C, which was also forged from unannealed billet but then annealed prior to cold rolling, also showed a strong texture gradient and banding in the sample final annealed at 950°C. For disc C, increasing the final anneal temperature to 1 100°C acted to diminish the gradient, eliminated the bands, but strengthening the intensity of (100) texture component. These effects from increasing final annealing temperatures were also evident, but to a lesser degree, in both the other disc materials and the heavy gauge plate. From the microstructural and textural observations, the following conclusions could be made regarding the optimum processing for fabricating tantalum sputtering targets: • For flat products, slab anneal temperatures preferably do not exceed 1 150°C (1050°C is more preferred) and the final anneal temperature is preferably kept at 950-1000°C, more preferably 1000°C. The resulting product is characterized as having a recrystallized average grain size of less 50 μ . and a (100) incremental intensity of less than 15 random and a log ratio of ( 1 1 1 ):( 100) of less than -4.0. • For round processing, billets preferably are annealed prior to forging and rolling into disc without use of an intermediate anneal at perform level. Final anneal temperature is preferably 950-1 100°C, and more preferably is 1050°C. The resulting product is characterized as having a recrystallized average grain size below 50 μm, and a (100) incremental intensity of less than 15 random and a log ratio of (1 1 1):(100) of less than -4.0. Table 3 Metallurgical Characteristics Process Table 3 (con't) Table 4 BILLET A BILLET B BILLET C BILLET D PC.WEIGHT Anneal Anneal Unannealed Unannealed 46.4 lbs 7" Long 1050 C 1050 C Upset Upset Forge Upset Forge Upset Forge Forge 2.5" Thick 2.5" Thick 2.5" Thick 2.5" Thick 6.25" Diameter Anneal Anneal 1050C 1050C Machine Machine Machine Machine Clean Clean Clean Clean 42 lbs 6" Diameter X-Roll to X-Roll to X-Roll to X-Roll to Gauge Gauge Gauge Gauge 0.400" 0.400" 0.400" 0.400" 15" Diameter Saw Cut Saw Cut Saw Cut Saw Cut 10.5 Ibs/qtr. Quarters Quarters Quarters Quarters Anneal Anneal Anneal Study Anneal Study Study Study ANNEAL ASTM TEMP(°C) GRAIN SIZE (REX) 950 7.1 (100%) 7.2(100%) 7.1 (99%) 7.2(100%) 1000 6.1 (100%) 6.5(100%) 5.9(100%) 6.8(100%) 1050 5.8(100%) 5.9(100%) 5.9(100%) 5.9(100%) 1100 4.5(100%) 4.5(100%) 4.5(100%) 4.0(100%) REX = % Recrystallization 0.500" PLATE 139 Slab Anneal 1050 Plate Anneal 950 Grain Size 6 7 Increment 0 025" ncrement (111) (100) ln(ratιo) 1 1257 1908 -042 0703 1456 -073 3 1127 111 002 4 1554 1543 001 5 0279 1146 -141 6 1159 1774 -043 7 1481 1335 010 8 327 1086 110 9 0996 1072 -007 10 2337 1634 036 11 481 1011 156 12 3321 2885 014 13 2294 273 -017 14 1477 1329 011 15 0607 1229 -071 16 102 0281 129 17 1536 0634 088 18 1771 4277 -088 19 1057 1921 -060 20 0097 1051 -238 0.500" PLATE 142 Slab Anneal 1050 Plate Anneal 1000 Grain Size 6 5 Increment 0 025" nt (111) (100) ln(ratιo) 1 3502 3495 000 2 0848 2988 -126 3 0412 3998 -227 4 0304 0676 -080 5 052 0717 -032 6 1167 1401 -018 7 1493 1691 -012 8 2071 1445 036 9 2039 177 014 10 219 1643 029 11 1541 0327 155 12 6722 0091 430 13 4228 0131 347 14 1904 1455 027 15 1514 2136 -034 16 1366 126 008 17 1388 0904 043 18 0709 1504 -075 19 0615 0395 044 20 1027 0499 072 - .5- 0.500" PLATE 140 Slab Anneal 1150 Plate Anneal 1000 Increment 0 025" ncrement (111) (100) ln(ratιo) 1 1786 1286 033 2 1745 0433 139 3 1948 0782 091 4 3232 23 034 5 2892 3517 -020 6 1061 3701 -125 7 3501 0522 190 8 1026 1944 -064 9 4783 0608 206 10 2402 0535 150 11 3097 2547 020 12 0859 2571 -110 13 2585 0897 106 14 0872 2955 122 15 1439 128 012 16 1657 2131 -025 17 1395 1765 -024 18 2506 1105 082 19 1541 1381 011 20 0593 1696 -105 0.500" PLATE 141 Slab Anneal 1300 Plate Anneal 1000 Grain Size 6 5 Increment 0 025" ncrement (111) (100) Irι(ratιo) 1 1577 3039 -066 1125 1032 009 3 1007 1824 -059 4 2001 0698 105 5 2091 2748 -027 6 4892 1906 094 7 0886 4336 -159 8 6052 0882 193 9 3392 0317 237 10 2177 1376 046 11 3431 2973 014 12 3628 1589 083 13 3458 0637 169 14 2095 1368 043 15 1869 1023 060 16 1371 2226 -048 17 2032 1 143 058 18 1949 1754 011 19 2175 3521 -048 20 5092 2802 060 0.250" PLATE 125D Slab Anneal 1050 Plate Anneal 1000 Grain Size 6 5 Increment 0 0125" ncrement (111) (100) lii(ratιo) 1 2241 4137 -061 2 1411 4259 -1 10 3 0823 3941 -157 4 082 779 -225 5 1734 4658 -099 6 2812 7527 -098 7 5245 4266 021 8 6196 2283 100 9 8892 1248 196 10 8531 1082 206 11 5261 1857 104 12 1439 1097 027 13 2445 2493 -002 14 2057 5962 -106 15 1173 2213 -063 16 1767 2609 -039 17 055 4066 -200 18 2921 4855 -051 19 4431 3684 018 20 6313 1898 120 0.250" PLATE 125B Slab Anneal 1 150 Plate Anneal 1000 Grain Size 6 5 Increment 0 0125" ncrement (111) (100) In(ratιo) 1 4159 2577 048 2 606 027 311 3 4407 0964 152 4 2336 1175 069 5 2023 2155 -006 6 3733 2091 058 7 4117 2131 066 8 4718 2721 055 9 5367 2604 072 10 2876 5519 -065 11 4952 2886 054 12 412 3362 020 13 2752 1715 047 14 0949 493 -165 15 1108 4827 -147 16 1 3157 -1 15 17 2357 6294 -098 18 0846 10654 -253 19 1628 5369 -1 19 20 0866 4458 -164 0.250" PLATE 125C Slab Anneal 1300 Plate Anneal 1000 Gram Size 6 5 Increment 0 0125" Increment 011 ) (100) ln(ratιo) 1 2154 1516 035 2 1174 1282 -009 3 079 5846 -200 4 0981 2736 -103 5 1938 355 -061 6 2302 3179 -032 7 5221 1661 115 8 3636 26 034 9 2982 1083 101 10 6161 0322 295 11 7636 0623 251 12 7336 046 277 13 4415 6945 -045 14 237 1953 019 15 2516 3636 -037 16 199 1976 001 17 2696 0769 125 18 3155 5257 -051 19 4558 0879 165 20 1788 0595 110 0.400" FORGING 950A Billet Anneal 1050 PreformAnneal 1050 FinishAnneal 950 Grain Size 7 1 Increment 0 020" ncrement (111) (100) liπ(ratιo) 1 2127 6911 -118 2 4289 4447 -004 3 3421 4819 -034 4 3065 467 -042 5 3879 4672 -019 6 233 5309 -082 7 8206 1239 189 8 9086 057 277 9 9615 0425 312 10 10558 157 191 11 1283 0883 268 12 9168 2094 148 13 8395 2002 143 14 11219 3961 104 15 2512 3816 -042 16 5044 4613 009 17 3898 6144 -046 18 2297 6159 -099 19 5796 6809 -016 20 2799 672 -088 0.400" FORGING 950B Billet Anneal 1050 PreformAnneal N/A FinishAnneal 950 Grain Size Increment 0 020" Increment (111) (100) ln(ratιo) 1 8364 6765 021 2 8193 6839 018 3 6576 6901 -005 4 4947 6953 -034 5 3246 8833 -100 6 5807 7248 -022 7 7812 5491 035 8 974 5358 060 9 1163 3748 113 10 11544 2258 163 11 11965 3086 136 12 9512 6106 044 13 8558 9762 -013 14 10727 584 061 15 6759 8025 -017 16 6212 9528 -043 17 3868 8796 -082 18 6368 8333 -027 19 6336 745 -016 20 4463 6201 -033 0.400" FORGING 950C Billet Anneal N/A PreformAnneal 1050 FinishAnneal 950 Grain Size Increment 0 020" Increment (111) (100) Irι(ratιo) 1 3589 9599 -098 2 3214 6069 -064 3 2869 6976 -089 4 3991 8405 -074 5 4737 3069 043 6 7163 4567 045 7 797 2348 122 8 15184 0506 340 9 18894 0058 579 10 16416 0084 528 11 12528 0215 407 12 13644 1074 254 13 9229 1141 209 14 4285 6858 -047 15 2067 4102 -069 16 3938 4881 -021 17 3391 10311 -1 11 18 5302 6265 -017 19 5755 6608 -014 20 4701 8166 -055 0.400" FORGING 950D Billet Anneal N/A PreformAnneal N/A FinishAnneal 950 Grain Size Increment 0 020" Increment (111) (100) ln(ratιo) 1 1836 965 -166 2 4837 7584 -045 3 5785 5354 008 4 1468 10297 -195 5 0781 17101 -309 6 8097 9559 -017 7 18984 1486 255 8 25471 0166 503 9 31554 0053 639 10 29911 0075 599 11 25476 0055 614 12 21407 1494 266 13 6505 2777 085 14 0065 1665 -324 15 0052 42 -439 16 0528 9288 -287 17 1122 8954 -208 18 267 8715 -1 18 19 5137 8222 -047 20 1453 10944 -202 Other embodiments of the present invention will be apparent to those skilled in the art from consideration of the present specification and practice of the present invention disclosed herein. It is intended that the present specification and examples be considered as exemplary only with a true scope and spirit of the invention being indicated by the following claims.

Claims: WHAT IS CLAIMED IS: 1. Tantalum metal having a purity of at least about 99.995%, and an average grain size of about 150 microns or less. 2. The tantalum metal of claim 1, wherein said metal is fully recrystallized. 3. The tantalum metal of claim 1, wherein said metal is at least partially recrystallyzed. 4. The tantalum metal of claim 1, wherein about 98% or more of said metal is recrystallyzed. 5. The tantalum metal of claim 1, wherein about 80% or more of said metal is recrystallyzed. 6. The tantalum metal of claim 1, wherein said metal has a) a texture in which a (100) pole figure has a center peak intensity less than about 15 random or b) a log ratio of (111 ):(100) center peak intensities of greater than about -4.0, or c) both. 7. The tantalum metal of claim 6, wherein said center peak intensity is from about 0 random to about 15 random. 8. The tantalum metal of claim 6, wherein said center peak intensity is from about 0 random to about 10 random. 9. The tantalum metal of claim 6, wherein said log ratio is from about -4.0 to about 15. 10. The tantalum metal of claim 6, wherein said log ratio is from about -1.5 to about 7.0. 11. The tantalum metal of claim 6, wherein said center peak intensity is from about 0 random to about 15 random, and said log ratio is from about -4.0 to about 15. 12. The tantalum metal of claim 1 having a purity of from 99.995% to about 99.999%. 13. A metal alloy comprising the tantalum metal of claim 1. 14. A metal alloy comprising the tantalum metal of claim 6. 15. A metal alloy comprising the tantalum metal of claim 3. 16. A sputtering target comprising the tantalum metal of claim 1. 17. A sputtering target comprising the tantalum metal of claim 6. 18. A sputtering target comprising the tantalum metal of claim 3. 19. A capacitor can comprising the tantalum metal of claim 1. 20. A capacitor can comprising the tantalum metal of claim 6. 21. A capacitor can comprising the tantalum metal of claim 3. 22. A resistive film layer comprising the tantalum metal of claim 1. 23. A resistive film layer comprising the tantalum metal of claim 6. 24. A resistive film layer comprising the tantalum metal of claim 3. 25. An article comprising at least as a component the tantalum metal of claim 1. 26. An article comprising at least as a component the tantalum metal of claim 6. 27. An article comprising at least as a component the tantalum metal of claim 3. 28. Tantalum metal having a) an average grain size of about 50 microns or less, or b) a texture in which a (100) pole figure has a center peak intensity equal to or less than about 15 random or c) a log ratio of (11 1):( 100) center peak intensities of greater than about -4.0, or combinations thereof. 29. The tantalum metal of claim 28 having an average grain size of from about 25 to about 50 microns. 30. The tantalum metal of claim 28 having a ratio of (11 1):(100) center peak intensities of greater than about -4.0. 31. The tantalum metal of claim 28, having both a) and b). 32. The tantalum metal of claim 28, wherein said metal has purity of at least 99.995% tantalum. 33. The tantalum metal of claim 28, wherein said metal has a purity of 99.999% tantalum. 34. The tantalum metal of claim 28, wherein said metal is fully recrystallized. 35. The tantalum metal of claim 32, wherein said metal is fully recrystallized. 36. The tantalum metal of claim 33, wherein said metal is fully recrystallized. 37. The tantalum metal of claim 28, wherein about 80% or more of said metal is fully recrystallized. 38. The tantalum metal of claim 28, wherein said center peak intensity is from about 0 random to about 15 random. 39. The tantalum metal of claim 28, wherein said log ratio is from about -4.0 to about 15. 40. An article comprising the tantalum metal of claim 28. 41. An article comprising the tantalum metal of claim 33. 42. A sputtering target comprising the tantalum metal of claim 28. 43. A sputtering target comprising the tantalum metal of claim 33. 44. A process for making the tantalum metal of claim 1, comprising reacting a salt containing tantalum with at least one agent capable of reducing the salt to tantalum and a second salt in a reaction container having an agitator, wherein the reaction container or a liner in the reaction container and the agitator or a liner on the agitator are made from a metal material having the same or higher vapor pressure of tantalum at the melting point of the tantalum. 45. The process of claim 44, wherein the salt containing tantalum comprises a potassium-fluoride tantalum and the agent comprises sodium. 46. The process of claim 45, wherein the second salt comprises sodium fluoride and/or sodium chloride. 47. The process of claim 44, wherein prior to reacting said salt containing tantalum, said process comprising forming an acid solution comprising tantalum and impurities and conducting a density separation of the acid solution containing tantalum from the acid solution containing the impurities; and crystallizing the acid solution containing the tantalum to form the salt containing tantalum. 48. The process of claim 47. wherein the tantalum and impurities are crushed ore comprising tantalum and impurities. 49. The process of claim 47, wherein the acid solution comprising tantalum and impurities are formed by combining acid solution with crushed ore comprising tantalum. 50. The process of claim 44, wherein the reaction occurs at about 800°C to about 1 100°C while stirring. 51. The process of claim 44, wherein the reaction container or liner and the agitator or liner on the agitator are metal-based, wherein said metal is nickel, chromium, iron, manganese, titanium, zirconium, hafnium, vanadium, technetium, ruthenium, cobalt, rhodium, palladium, platinum, or any combination thereof. 52. The process of claim 51 , wherein the metal is nickel or a nickel-based alloy. 53. The process of claim 51 , wherein the metal is chromium or a chromium-based alloy. 54. The process of claim 51, wherein the metal is iron or an iron-based alloy. 55. The process of claim 44, further comprising recovering tantalum by dissolving the second salt in an aqueous solution. 56. The process of claim 55, further comprising melting said recovered tantalum in a sufficient vacuum to remove substantially any existing impurities in said recovered tantalum and obtain high purity tantalum. 57. The process of claim 56, wherein the vacuum is 10 torr or more. 58. The process of claim 56, wherein the pressure above the melted recovered tantalum is lower than the vapor pressures of substantially all of the impurities. 59. The process of claim 56, wherein the impurities are removed by vaporization of the impurities. 60. The process of claim 56, wherein said melting is accomplished by electron beam melting. 61. The process of claim 56, wherein said melting is accomplished by vacuum arc remelt processing. 62. The process of claim 56, wherein the high purity tantalum is allowed to form a solid and subjected to a rolling process, a forging process, or both. 63. The tantalum metal of claim 1 , wherein the tantalum metal has a substantially fine and uniform microstructure. 64. The tantalum metal of claim 1, wherein the tantalum metal has an average grain size of from about 25 to about 150 microns. 65. The tantalum metal of claim 64, wherein the tantalum metal has an average grain size of from about 25 to about 100 microns. 66. The tantalum metal of claim 65, wherein the tantalum metal has an average grain size of from about 25 to about 75 microns. 67. A process of making a sputtering target from tantalum metal having a purity of at least 99.995%, comprising: a) mechanically or chemically clean surfaces of the tantalum metal, wherein the tantalum metal has a sufficient starting cross-sectional area to permit steps b) through g); b) flat forging the tantalum metal into at least one rolling slab, wherein the at least one rolling slab has sufficient deformation to achieve substantially uniform recrystallization after annealing in step d); c) mechanically or chemically clean surfaces of the at least one rolling slab; d) annealing the at least one rolling slab at a sufficient temperature and for a sufficient time to achieve at least partial recrystallization of the at least one rolling slab; e) cold or warm rolling the at least one rolling slab in both the perpendicular and parallel directions to the axis of the starting tantalum metal to form at least one plate; f) flattening the at least one plate; and g) annealing the at least one plate to have an average grain size equal to or less than about 150 microns and a texture substantially void of (100) textural bands; 68. The process of claim 67, wherein the tantalum metal has a purity of at least 99.999%. 69. The process of claim 67, wherein the flat forging occurs after the tantalum metal is placed in air for at least about 4 hours and from temperatures ranging from ambient to about 1200°C. 70. The process of claim 67, wherein the cold rolling is transverse rolling at ambient temperatures and the warm rolling is at temperatures of less than about 370°C. 71. The process of claim 67, wherein the annealing of the plate is vacuum annealing at a temperature and for a time sufficient to achieve recrystallization of the tantalum metal. 72. A process of making a sputtering target from tantalum metal having a purity of at least 99.995%, comprising: a) mechanically or chemically clean surfaces of the tantalum metal, wherein the tantalum metal has a sufficient starting cross-sectional area to permit steps b) through i); b) round forging the tantalum metal into at least one rod, wherein the at least one rod has sufficient deformation to achieve substantially uniform recrystallization after annealing in step d) or step f); c) cutting the rod into billets and mechanically or chemically clean the surfaces of the billets; d) optionally annealing the billets to achieve at least partial recrystallization; e) axially forging billets into performs; f) optionally annealing the performs to achieve at least partial recrystallization; g) cold rolling the performs into at least one plate; and h) optionally mechanically or chemically clean the surfaces of the at least one plate; and i) annealing the at least one plate to have an average grain size equal to or less than about 150 microns and a texture substantially void of (100) textural bands, wherein annealing occurs at least in step d) or f) or both. 73. The process of claim 72, wherein the tantalum metal has a purity of at least 99.999%. 74. The process of claim 72, wherein the round forging occurs after subjecting the tantalum metal to temperatures of about 370°C or lower. 75. The process of claim 72 wherein prior to forging the billets, the billets are annealed. 76. The process of claim 72, wherein prior to cold rolling of the performs, the performs are annealed. 77. The process of claim 72, wherein the annealing of the performs is vacuum annealing at a sufficient temperature and for a time to achieve recrystallization.

Inventors: HUBER LOUIS E JR, KAWCHAK MARK N, MAGUIRE JAMES D JR, MICHALUK CHRISTOPHER A, HUBER, LOUIS, E., JR., KAWCHAK, MARK, N., MAGUIRE, JAMES, D., JR., MICHALUK, CHRISTOPHER, A.
Applicants: CABOT CORP, CABOT CORPORATION
Application year: 1999
Main classification: C22B34
IPC codes: B22F9, C22B3, C22B9, C22B34, C22C27, C22F1, C23C14