Paint of high weather resistance

Abstract: A paint composition possessing ultraviolet absorbability and a curing function comprises an isocyanate compound (A) having a functional group with ultraviolet absorbability on a side chain and containing a residual isocyanate group, the compound (A) being obtainable by submitting a portion of the isocyanate groups of an isocyanate prepolymer or monomer having at least two free isocyanate groups to reaction with an ultraviolet absorber having an active hydrogen. By reacting such a composition with a polymeric compound having an active hydrogen, a paint with long-term weather resistance is obtained.

Description: The present invention relates to a paint which is used for waterproofing of rooftops, floors and outer walls of buildings, building materials, sports facilities such as tennis courts and athletic sports stadia, automobiles, household appliances, woodworking products or plastic molded articles, and which can form a paint film excellent in weather resistance, for example, gloss retention, discoloration resistance, and crack resistance in long term outdoor use. Hitherto, there have been known two-pack curing type paint compositions which comprise a composition containing active hydrogen and a composition having a functional group which reacts with active hydrogen. These paint compositions are excellent in chemical properties such as chemical resistance and, besides, can form a paint film superior in adhesion and strength and have been used as top coats of rooftops of buildings for waterproofing, outer walls of buildings, building materials and sports facilities. Especially, when an acrylic polyol is used in the composition to provide active hydrogen and an isocyanate is used as the functional group which reacts with active hydrogen, a paint film excellent in gloss, chemical properties and mechanical strength can be produced and these paint compositions have been generally used as outdoor paints However, when the paint films comprising the above paint compositions are used for a long period of time, they suffer from problems of weather resistance, such as decrease of gloss, discoloration and cracking due to exposure to ultraviolet rays. For the solution of these problems, an ultraviolet absorber or a light stabilizer is added to the paint compositions. However, when used for a long time, the bleeding phenomenon of the ultraviolet absorber or light stabilizer coming to the surface is caused, and the effects of the additives cannot be retained for a long period of time. In order to solve the above problems, attempts have been made to fix an ultraviolet absorber or a light stabilizer in the paint compositions. Thus, there has been proposed a method of copolymerizing an ultraviolet absorber or a light stabilizer which comprises an acrylic polyol having a polymerizable skeleton, and paint compositions comprising a polyisocyanate compound and a resin composition obtained by copolymerization of an acrylic polyol with an unsaturated monomer having a hydroxyl group, an unsaturated monomer having a cycloalkyl group, or the like have been reported (JP-A 9 (1997)-3393). However, according to the above method, if the polyisocyanate compound is inferior in weather resistance or the content of the polyisocyanate in the paint composition is high; the whole paint film sometimes deteriorates in weather resistance. Furthermore, in the case of the acrylic polyol of the above composition, dispersibility of pigments is inferior, and when pigment is contained, a chalking phenomenon of the paint film occurs after the lapse of a long time, and the weather resistance cannot be sufficiently retained for a longer period of time. EP-A-0029598 relates to a coating composition comprising at least 50% by weight of a binder which comprises an organic polyisocyanate crosslinking agent and an acrylic polymer having a number average molecular weight of from 500 to 10,000, a hydroxyl content of at least 2% by weight and which contains about 2 to 10% per weight of the chain transfer agent. This composition also comprises an ultraviolet light stabiliser. DE 2648367 provides a UV-curable resin, for example one in which an organic urethane is reacted with a UV absorber. JP 57/049655 provides a polyurethane composition comprising a polyurethane which may comprise terminal NCO groups and a benzotriazole UV absorber. The object of the present invention is to provide a paint in which the ultraviolet absorber or light stabiliser added to the two-pack curing type paints does not bleed and which can provide a paint film excellent in long-term weather resistance such as gloss retention and discolouration resistance in long-term outdoor use by imparting weather resistance to both the isocyanate component and the component reacting with the isocyanate component, without damaging physical properties and chemical properties of the paint. The inventors have contained research on paint compositions in an attempt to retain long-term weather resistance of paints. As a result, they have succeeded in obtaining an isocyanate compound having ultraviolet absorbability by reacting a polyisocyanate compound with an ultraviolet absorber having active hydrogen, and by reacting the resulting compound with a polymeric compound having active hydrogen and a pendant functional group having ultraviolet absorbability, it has become possible to impart ultraviolet absorbability to both of these reacting compounds. Thus, a paint excellent in weather resistance has been provided, and the present invention has been accomplished. The invention provides a paint composition which is obtainable by a process which comprises reacting a polymeric compound having an active hydrogen; and an isocyanate compound (A) having a functional group with ultraviolet absorbability on a side chain and containing a residual isocyanate group, the compound (A) being obtainable by a process which comprises submitting a portion of the isocyanate groups in an isocyanate prepolymer or monomer having at least two free isocyanate groupes to reaction with an ultraviolet absorber of the following formula (1) or formula (2): wherein each of R 1 and R 2 , which are the same or different, is hydrogen, a C 1 -C 10 hydrocarbon group or C 1 -C 10 alkoxy, R 3 is hydrogen, a halogen, C 1 -C 10 alkoxy, cyano or nitro, R 4 is hydrogen, a halogen, C 1 -C 10 alkoxy or a C 1 -C 10 hydrocarbon group and R 5 is hydrogen, C 1 -C 10 alkoxy or a C 1- C 10 hydrocarbon group, and wherein the polymeric compound having an active hydrogen, is an acrylic polyol in which the monomer component constituting the acrylic polyol is a polymerizable unsaturated monomer having a hydroxyl group; a polymerizable unsaturated monomer having a cycloalkyl group; a polymerizable light stable monomer; a polymerizable ultraviolet absorbing monomer; and a prepolymer which is a monomer having a polymerizable unsaturated ethylene group and a weight-average molecular weight of 1000-30000, and which has 30% by weight or more of a basic functional group and/or 30% by weight or more of an acidic functional group based on the weight of the prepolymer. The C 1 -C 10 hydrocarbon group may be, for instance, a C 1 -C 10 alkenyl group, a C 2 -C 10 alkenyl group or a C 2 -C 10 alkynyl group. The C 1 -C 10 alkyl group is typically C 1 -C 8 alkyl, or C 1 -C 6 alkyl. Preferably it is C 1 -C 4 alkyl. Examples of C 1 -C 10 alkyl include methyl, ethyl, i-propyl, n-propyl, t-butyl, s-butyl, n-butyl, pentyl, hexyl, heptyl, octyl, nonyl and decyl groups. The C 2 -C 10 alkenyl group is typically C 2 -C 8 alkenyl or C 2 -C 6 alkenyl. It may also be C 2 -C 4 alkenyl. Examples of C 2 -C 10 alkenyl include ethenyl, propenyl, butenyl, pentenyl, hexenyl, heptenyl, octenyl, nonenyl and decenyl groups. The C 2- C 10 alkynyl group is typically C 2 -C 8 alkynyl, or C 2 -C 6 alkynyl. It may also be C 2 -C 4 alkynyl. Examples of C 2 -C 10 alkynyl include ethynyl, propynyl, butynyl, pentynyl, hexynyl, heptynyl, octynyl, hexynyl, heptynyl, octynyl, nonynyl and decynyl groups. The C 1 -C 10 alkoxy group may be, for instance, a C 1 -C 8 alkoxy group or a C 1 -C 6 or C 1 -C 4 alkoxy group. Examples of C 1 -C 10 alkoxy include methoxy, ethoxy, i-propoxy, n-propoxy, t-butoxy, s-butoxy, n-butoxy, pentoxy, hexoxy, heptoxy, octoxy, nonoxy and decoxy groups. As the isocyanate prepolymers or monomers used in the present invention, mention may be made of, for example, hexamethylene diisocyanate, isophorone diisocyanate, tolylene diisocyanate, m-xylylene diisocyanate, xylylene diisocyanate, hydrogenated xylylene diisocyanate, cyclohexylmethane diisocyanate, and naphthalene diisocyanate; their isocyanurate compounds, biuret compounds, trimethylolpropane adducts, adducts with compounds having active hydrogen, such as amines, carboxylic acids, and alcohols, and adducts with derivatives thereof. These may be used each alone or in combination of two or more. The ultraviolet absorbers having active hydrogen are those which are represented by the formulae (1) and (2) above. Examples thereof include benzotriazole ultraviolet absorbers such as 2-(2'-hydroxy-5'-methylphenyl)benzotriazole, 2-(2'-hydroxy-5'-t-butylphenyl)benzotriazole, 2-(2'-hydroxy-3'-t-butyl-5'-methylphenyl)-5-chlorobenzotriazole, and 2-(2'-hydroxy-4'-octoxyphenyl)benzotriazole, and benzophenone ultraviolet absorbers such as 2-hydroxy-4-octoxybenzophenone, 2-hydroxy-4-ethoxybenzophenone, 2-hydroxy-4-methoxybenzophenone, 2-hydroxy-4-octoxy-2'-chlorobenzophenone, and 2-hydroxy-4-octoxy-3' -methylbenzophenone. These may be used alone or in combination of two or morse. Furthermore, the reaction of the isocyanate prepolymer or monomer with the ultraviolet absorber having active hydrogen can be carried out with addition of compounds having active hydrogen, such as amines, carboxylic acids, alcohols and derivatives thereof, either alone or in combination, whereby the chemical properties and the physical properties of the products can be freely controlled. Solvents can be used for the reaction, and examples of preferred solvents include aromatic solvents, such as toluene and xylene; ketones, such as acetone, methyl ethyl ketone and methyl isobutyl ketone; esters, such as ethyl acetate, butyl acetate and iso-butyl acetate; cellosolve acetate and propylene glycol monomethyl ether acetate. These may be used alone or in combination. However, solvents having active hydrogen, such as alcohols, should not be used because they react with isocyanates. Moreover, for acceleration of the reaction, urethane reaction catalysts may be used, and examples of the catalysts include organic metal catalysts such as dibutyltin diacetate and dibutyltin dilaurate, and amine catalysts such as 1,4-diazabicyclo(2,2;2)octane, triethylamine, N,N,N',N'-tetramethylethylenediamine triethylenediamine and dimethylaminoethanol. These may be used alone or in combination. The isocyanate prepolymer (B) to be mixed:with the component (A) is not limited. Monomers which constitute the prepolymer include, for example, isocyanate monomers such as hexamethylene diisocyanate, isophorone diisocyanate, tolylene diisocyanate, m-xylylene diisocyanate and diphenylmethane diisocyanate, their isocyanurate compounds, biuret compounds, adducts with compounds having active hydrogen, such as amines, carboxylic acids, alcohols and derivatives thereof. These may be used alone or in combination. The reaction process is not limited, and general processes can be used. However, it is desirable that the. reaction is effected in the absence of water. For example, solvents of urethane grade or water removers may be used. As the water removers, tosyl isocyanate, molecular sieves, etc. can be used. In order to obtain especially excellent weather resistance and better properties, it is preferred to use isocyanurate compounds or biuret compounds of hexamethylene diisocyanate as the starting materials for the compound (A). The reaction with the ultraviolet absorber is preferably carried out in such a manner that two or more on average of isocyanate groups remain per one molecule in the isocyanate compound (A). If it is less than two on average, when the compound (A) is reacted with a curing component, crosslinking occurs insufficiently and the properties of the paint may deteriorate. As the isocyanate prepolymer (B), preferred are non-yellowing isocyanate prepolymers such as hexamethylene diisocyanate type and isophorone diisocyanate type. The isocyanate prepolymer (B) can be mixed with the isocyanate compound (A) obtained by polymerization with the ultraviolet absorber so that the amount of (B) is from 0 to 99% based on the total amount of (A) and (B). If the amount of (A) is less than 1%, the amount of the ultraviolet absorber is conspicuously small and the desired effects cannot be obtained. The isocyanate compound or composition comprising (A) or (A) and (B) shows no bleeding out of the ultraviolet absorber which has occurred in conventional techniques because the ultraviolet absorber is incorporated into the isocyanate compound (A) in the present invention, and this is very effective for retaining long-term weather resistance. Next, polymeric compounds having active hydrogen which are reacted with the above isocyanate compound or composition will be explained. The polymeric compounds can crosslink with the isocyanate to form a paint film. The polymeric compound having an active hydrogen is an acrylic polyol, and in the paint composition of the invention, a paint film excellent in weather resistance is provided. In the acrylic polyol, the monomer component is a polymerizable unsaturated monomer having a hydroxyl group; a polymerizable unsaturated monomer having a cycloalkyl group; a polymerizable light stable monomer; a polymerizable ultraviolet absorbing monomer; and a prepolymer which is a monomer having a polymerizable unsaturated ethylene group and a weight-average molecular weight of from 1000 to 30000, and having 30% by weight or more of basic functional groups and/or 30% by weight or more of acidic functional groups based on the weight of the prepolymers. In more detail, as the monomer component having a cycloalkyl group, mention may be made of, for example, cyclohexyl (meth)acrylate, methylcyclohexyl (meth)acrylate, and tert-butylcyclohexyl (meth)acrylate. These may be used alone or in combination. As the unsaturated monomer component having a hydroxyl group, mention may be made of, for example, hydroxyethyl (meth)acrylate, hydroxypropyl (meth)acrylate, and caprolactone-modified hydroxy (meth)acrylate. These may be used alone or in combination. As the polymerizable ultraviolet absorbing monomer component, mention may be made of, for example, benzotriazole type polymerizable ultraviolet absorbers such as 2-[2'-hydroxy-5'-(methacryloyloxymethyl)phenyl]-2H-benzotriazole, 2-[2'-hydroxy-5'-(methacryloyloxyethyl)phenyl]-2H-benzotriazole, 2-[2'-hydroxy-5'-t-butyl-3'-(methacrylpyloxyethyl)phenyl]-2H-benzotriazole, and 2-[2'-hydroxy-5'-(methacryloyloxyethyl)phenyl]-5-chloro-2H-benzotriazole, and benzophenone type polymerizable ultraviolet absorbers such as 2-hydroxy-4-(3-acryloxy-2-hydroxypropoxy)benzophenone, 2-hydroxy-4-(3-methacryloxy-2-hydroxypropoxy)benzophenone and 2'-dihydroxy-4-(3-methacryloxy-2-hydroxypropoxy)benzophenone. These may be used alone or in combination, and the amount of the component is preferably from 0.1 to 7% by weight based on the polymerizable monomer components. As the polymerizable light stable monomer component, mention may be made of, for example, hindered amine light stabilizers such as 4-(meth)acryloyloxy-2,2,6,6-tetramethylpiperidine, 4-(meth)acryloylamino-2,2,6,6-tetramethylpiperidine, 4-(meth)acryloyloxy-1,2,2,6,6-pentamethylpiperidine, and 4-(meth) acryloylamino-1,2,2,6,6-pentamethylpiperidine. These may be used alone or in combination, and the amount of the component is preferably from 0.1 to 7% by weight based on the polymerizable monomer components. In the case of the prepolymer which is a monomer having a polymerizable unsaturated ethylene group and a weight-average molecular weight of from 1000 to 30000, and having 30% by weight or more of basic functional groups and/or 30% by weight or more of acidic functional groups based on the weight of the prepolymer, the prepolymer is prepared in the following manner. As for the prepolymer having an amino group, an amino-group containing monomer such as dimethylaminomethyl methacrylate, diethylaminomethyl methacrylate, dibutylaminomethyl methacrylate, or dihexylaminomethyl methacrylate each alone or in combination is used as the polymerizable compound having an amino group in an amount of 30% or more based on the prepolymer constituents, and one or more of them are polymerized using a polymerization initiator having a carboxyl group at an end. Then, the resulting product is subjected to an addition reaction with a polymerizable monomer having an epoxy group in the presence of a polymerization inhibitor and a tertiary amine. As for the prepolymer having a carboxylic acid group, a polymerizable monomer having a carboxylic acid group such as acrylic acid, maleic acid, itaconic acid, 2-acryloyloxyethylsuccinic acid, or 2-acryloyloxyethylphthalic acid each alone or in combination is used as the polymerizable compound having a carboxyl group in an amount of 30% or more based on the prepolymer constituents, and one or more of them are polymerized using a conventional polymerization initiator. Then, the resulting product is subjected to an addition reaction with a polymerizable monomer having an epoxy group in the presence of a polymerization inhibitor and a tertiary amine. As other polymerizable monomers, mention may be made of, for example, methyl (meth)acrylate, ethyl (meth)acrylate, propyl (meth)acrylate, isopropyl (meth)acrylate, butyl (meth)acrylate, isobutyl (meth)acrylate, sec-butyl (meth)acrylate, tert-butyl (meth)acrylate, isopentyl (meth)acrylate, neopentyl (meth)acrylate, hexyl (meth)acrylate, heptyl (meth)acrylate, octyl (meth)acrylate, 2-ethylhexyl (meth)acrylate, stearyl (meth)acrylate, benzyl (meth)acrylate, styrene, α-methylstyrene, vinyltoluene, vinylidene chloride, and vinyl acetate. These may be used alone or in combination. The method of copolymerizing the above monomer compositions is not limited, but solution polymerization is preferred. The solvents used in the copolymerization include, for example, aromatic solvents such as toluene and xylene, ketones such as acetone, methyl ethyl ketone, and methyl isobutyl ketone, esters such as ethyl acetate and butyl acetate, cellosolve acetate, and propylene glycol monomethyl ether acetate. These may be used alone or in combination. Polymerization initiators are used in the copolymerization of the above monomer compositions, and they may be the usual polymerization initiators, e.g., azo type such as azobisisobutyronitrile, and peroxide type such as benzoyl peroxide. These may be used alone or in combination. Since the prepolymer having a polymerizable ethylenically functional group which is a constituent of the polymeric compound having active hydrogen contains a basic functional group and/or an acidic functional group, the finally obtained paint is excellent in dispersibility for any pigments such as basic pigments, acidic pigments, or mixtures thereof, and consequently weather resistance of the paint composition can be improved. The paint composition of the present invention can optionally contain accelerators for the reaction with isocyanate, organic solvents, additives, inorganic pigments, organic pigments, and extender pigments. The reaction accelerators include, for example, organic metal catalysts such as butyltin diacetate and dibutyltin dilaurate, and amine catalysts such as 1,4-diazabicyclo(2,2,2)octane, triethylamine, N,N,N',N'-tetramethylethylenediamine, triethylenediamine, and dimethylaminoethanol. These may be used alone or in combination of two or more. The organic solvents include, for example, aromatic solvents such as toluene and xylene, ketones such as acetone, methyl ethyl ketone, and methyl isobutyl ketone, esters such as ethyl acetate and butyl acetate, cellosolve acetate, and propylene glycol monomethyl ether acetate. These may be used alone or in combination. The additives include one or more of various additives for paints, such as antifoaming agents, dispersants, levelling agents, adhesion improvers, plasticizers, stabilizers, and anti-settling agents. The inorganic pigments include, for example, titanium oxide, zinc oxide, chrome yellow, red iron oxide, yellow iron oxide, iron black, and carbon black. The organic pigments include, for example, azo compounds and phthalocyanine compounds. The extender pigments include, for example, calcium carbonate, silicon oxide, clay, organic bentonite, and silica powder. These may be used alone or in combination. The materials which can be coated with the paint composition of the present invention are not limited. Examples of the materials to be coated are plastics such as urethane, FRP (fiber-reinforced plastics), polypropylene, polycarbonate, and acrylic resin, woods, metals, glasses, and ceramics. The long-term weather resistance of these materials can be retained by coating the surface with the paint composition of the present invention. That is, the paint composition of the present invention can be widely used as coating agents for plastic molded articles, household appliances, metallic articles, automobiles, constructions, building materials, sports facilities, woodworking, etc. The present invention will be explained by the following examples. Example 1 (Preparation of ultraviolet absorber-containing isocyanate polymer (component A)): 24 Parts by weight of butyl acetate, 12 parts by weight of hexamethylene diisocyanurate, 2 parts by weight of 2(2'-hydroxy-5'-methylphenyl)benzotriazole, and 0.01 part by weight of dibutyltin dilaurate were charged in a flask equipped with a stirrer, a condenser tube, and a thermometer, and heated to 70°C in a nitrogen atmosphere to carry out the reaction for 3 hours. The reaction product was cooled to room temperature and mixed with 38 parts by weight of an isocyanate prepolymer (Trade mark: ACRIT 8XA-012 manufactured by Taisei Kako Co., Ltd.; nonvolatile content: 50%; isocyanate content: 3.1%) to obtain a composition. Examples 2 to 8 Isocyanate prepolymers were obtained in the same manner as in Example 1 according to the formulations shown in Table 1. The properties of the resulting prepolymers are shown Table 2. Formulations of isocyanate prepolymers (Examples) Example 2 3 4 5 6 7 8 Isocyanurate compound of HMDI 12 TMP adduct of HMDI 12 12 Biuret compound of HMDI 12 12 HMDI monomer 12 12 2 (2'-hydroxy-5'-methylphenyl)benzotriazole 2 2 1 2-hydroxy-4-n-octoxybenzophenone 2 2 2 1 PPG (average molecular weight: 1000, containing 3 hydroxyl groups in one molecule) 23 23 Butyl acetate 24 24 24 24 24 36 36 Dibutyltin dilaurate 0.01 0.01 0.01 0.01 0.01 0.01 0.01 Isocyanate prepolymer 38 38 38 38 38 72 72 In the above table, "TMP", "PPG" and "HMDI" are abbreviations of "trimethylolpropane", "polypropylene glycol" and "hexamethylene diisocyanate", respectively. Properties of isocyanate prepolymers Example 1 2 3 4 5 6 7 8 Appearance Transparent Transparent Transparent Transparent Transparent Transparent Transparent Transparent Nonvolatile content (%) 43 43 43 43 43 43 50 50 Viscosity (mPa.s) 20 22 25 25 21 19 60 60 Content of NCO group (%) 4.3 4.5 3.0 3.2 4.8 4.9 3.4 3.5 Comparative Examples 1-4 Isocyanate prepolymers were obtained in the same manner as in Example 1 according to the formulations shown in Table 3. The properties of the resulting prepolymers are shown in Table 4. Formulations of isocyanate prepolymers (Comparative Examples) Comparative Example 1 2 3 4 Isocyanurate compound of HMDI 12 TMP adduct of HMDI 12 Biuret compound of HMDI 12 HMDI monomer 12 2(2'-hydroxy-5'-methyl-phenyl)benzotriazole 2-hydroxy-4-n-octoxy-benzophenone PPG (average molecular weight: 1000, containing 3 hydroxyl groups in one molecule) 23 Butyl acetate 24 24 24 35 Dibutyltin dilaurate 0.01 Isocyanate prepolymer 36 36 36 70 Properties of isocyanate prepolymer Comparative Example 1 2 3 4 Appearance Transparent Transparent Transparent Transparent Nonvolatile content (%) 42 42 42 50 Viscosity (mPa.s) 18 20 22 60 Content of NCO group (%) 5.0 3.6 5.5 3.7 Example 9 (Preparation of acrylic polyol): 10 parts by weight of butyl acetate and 10 parts by weight of xylene were charged in a flask equipped with a stirrer, a dropping funnel, a condenser tube, and a thermometer, and heated to 120°C in a nitrogen atmosphere. Polymerizable monomers were charged in the dropping funnel according to the following formulation and added dropwise at an equal rate over a period of 2 hours. Part by weight Cyclohexyl methacrylate 25 Methyl methacrylate 6 Butyl acrylate 10 2-hydroxyethyl methacrylate 7 Acrylic acid 0.3 2-[2'-hydroxy-5'-(methacryloyl)phenyl] enzotriazole 0.5 Methacryloylamino-2,2,6,6-tetramethyl piperidine 0.5 Basic prepolymer 2 Acidic prepolymer 2 Azobisisobutyronitrile 1 After lapse of 1 hour from completion of the addition, a mixed solution comprising 0.2 part by weight of azobisisobutyronitrile and 10 parts by weight of xylene was added dropwise at an equal rate over a period of 2 hours. After completion of the addition, the content was kept at 120°C for 1 hour and, after cooling, diluted with 15.5 parts by weight of xylene to obtain an acrylic polyol having a viscosity of 2500 mPa s, a nonvolatile content of 50%, and a weight-average molecular weight of 32000. The acidic prepolymer (oligomer) and the basic prepolymer (oligomer) were prepared in the following manner. Preparation of the basic prepolymer: 47 parts by weight of butyl acetate was charged in a flask equipped with a stirrer, a dropping funnel, a condenser tube, and a thermometer, and heated to 120°C in a nitrogen atmosphere. A mixture comprising 4.3 parts by weight of 4,4'-azobis-4-cyanovaleric acid, 1.4 part by weight of triethylamine and 22.0 parts by weight of cellosolve acetate, and a mixture comprising 17.3 parts by weight of dimethylaminoethyl methacrylate and 5 parts by weight of butyl acetate were separately charged in the dropping funnel and-added dropwise at an equal rate over a period of 3 hours. After 30 minutes from completion of the addition, 0.01 part by weight of hydroquinone was added, and then 3.6 parts by weight of glycidyl methaerylate was added, followed by reaction for further 2 hours to prepare the basic prepolymer. Preparation of the acidic prepolymer: 35 parts parts by weight of butyl acetate were charged in a flask equipped with a stirrer, a dropping funnel, a condenser tube, and a thermometer, and heated to 120°C in a nitrogen atmosphere. A mixture comprising 20 parts by weight of 2-methacryloyloxyethylphthalic acid, 4 parts by weight of azobisisobutyronitrile and 10 parts by weight of butyl acetate was charged in the dropping funnel and added dropwise at an equal rate over a period of 3 hours. After 30 minutes from completion of the addition, 0.01 part by weight of hydroquinone was added, and then 2.0 parts by weight of glycidyl methacrylate and 0.6 part by weight of triethylamine were added, followed by reaction for a further 2 hours to prepare the acidic prepolymer. Comparative Example 5 Polymerization was carried out in the same manner as in Example 9 according to the following formulation of the polymerizable monomers. Part by weight Cyclohexyl methacrylate 25 Methyl methacrylate 6 Butyl acrylate 10 2-hydroxyethyl methacrylate 7 Acrylic acid 0.3 Azobisisobutyronitrile 1 The above acrylic polyol had a viscosity of 2200 mPa s, a nonvolatile content of 49%, and a weight-average molecular weight of 30000. Example 10 Using the varnish obtained in Example 9, pigments were dispersed at the following formulation by a sand mill to obtain black and white paints. Mill base formulation (white): Titanium oxide 20 parts by weight Varnish 10 parts by weight Xylene 5 parts by weight 35 parts by weight Mill base formulation (black): Carbon 5 parts by weight Varnish 10 parts by weight Xylene 10 parts by weight 25 parts by weight Let down formulation (white): Mill base (white) 35 parts by weight Varnish 50 parts by weight Xylene 15 parts by weight 100 parts by weight Let down formulation (black): Mill base (black) 25 parts by weight Varnish 50 parts by weight Xylene 15 parts by weight 100 parts by weight A paint comprising the above white paint and the above black paint at a ratio of 8:2 was mixed with the isocyanate prepolymers obtained in Examples 1 to 8 so as to give a ratio of NCO group/OH group=1/1. The resulting mixtures were coated on an urethane plate and subjected to an accelerated test for 2000 hours by a carbon sunshine weather meter, and a gloss retention rate was calculated on the basis of initial gloss value. Moreover, the paints were applied to a glass plate at a film thickness of 200 microns by an applicator. Just before drying to the touch, the films were subjected to rubbing test with fingers, and color difference between the rubbed portion and the unrubbed portion was measured to evaluate the dispersibility. The results are shown in Table 5. Comparative Example 6 White and black paints were prepared in the same manner as in Example 10 using the varnish obtained in Comparative Example 5. A paint obtained by similarly mixing the white paint and the black paint at 8:2 was similarly mixed with the isocyanate prepolymers obtained in Comparative Examples 1 to 4, was subjected to the same tests as in Example 10. The results are shown in Table 5. Formulations of paints and test results Example Comparative Example 1 2 3 4 5 6 7 8 1 2 3 4 Isocyanate composition (part by weight) 31 30 45 42 28 27 39 39 27 38 24 36 Paint obtained in Example 10 (part by weight) 100 100 100 100 100 100 100 100 Paint obtained in Comparative Example 6 (part by weight) 100 100 100 100 Gloss retention after acceleration (%) 86 83 84 82 85 80 82 81 69 65 68 62 Pigment separation ○ ○ ○ ○ ○ ○ ○ ○ × × × × The results of evaluation on pigment separation as floating or flooding are shown by the following grades. Color difference ΔE Grade Less than 0.5 ○ 0.5-1.5 × It can be seen that the systems using the isocyanate compositions and the acrylic polyols of the Examples of the present invention were superior in gloss retention, dispersibility and weather resistance. According to the present invention, there is provided a paint excellent in long-term weather resistances such as gloss retention and discoloration resistance in long-term outdoor use. When the ultraviolet absorber-polymerized type isocyanate composition of the present invention is used, long-term weather resistance of the paint film can be improved without damaging properties, by selecting a composition which is capable of reacting with the said isocyanate composition and is superior in pigment dispersibility and weather resistance. Thus, the composition can be used for paints and inks which are required to have weather resistance.

Claims: A paint composition which is obtainable by a process which comprises reacting a polymeric compound having an active hydrogen; and an isocyanate compound (A) having a functional group with ultraviolet absorbability on a side chain and containing a residual isocyanate group, the compound (A) being obtainable by a process which comprises submitting a portion of the isocyanate groups in an isocyanate prepolymer or monomer having at least two free isocyanate groups to reaction with an ultraviolet absorber of the following formula (1) or formula (2): wherein each of R 1 and R 2 , which are the same or different, is hydrogen, a C 1 -C 10 hydrocarbon group or C 1 -C 10 alkoxy, R 3 is hydrogen, a halogen, C 1 -C 10 alkoxy, cyano or nitro, R 4 is hydrogen, a halogen, C 1 -C 10 alkoxy or a C 1 -C 10 hydrocarbon group and R 5 is hydrogen, C 1 -C 10 alkoxy or a C 1- C 10 hydrocarbon group, and wherein the polymeric compound having an active hydrogen is an acrylic polyol in which the monomer component constituting the acrylic polyol is a polymerizable unsaturated monomer having a hydroxyl group; a polymerizable unsaturated monomer having a cycloalkyl group; a polymerizable light stable monomer; a polymerizable ultraviolet absorbing monomer; and a prepolymer which is a monomer having a polymerizable unsaturated ethylene group and a weight-average molecular weight of 1000-30000, and which has 30% by weight or more of a basic functional group and/or 30% by weight or more of an acidic functional group based on the weight of the prepolymer. A composition according to claim 1 which is obtainable by further reacting an isocyanate prepolymer (B) which is different from the isocyanate compound (A) with the polymeric compound having an active hydrogen and isocyanate compound (A). A composition according to claim. 1 or 2, wherein the isocyanate prepolymer or monomer having at least two free isocyariate groups is hexamethylene diisocyanate, an isocyanurate trimer or biuret compound of hexamethylene diisocyanate, an adduct compound of a polyol, or a prepolymer thereof. An article coated with a composition as defined in any one of the preceding claims.

Inventors: YAMAZAKI TAKAYOSHI, YANAUCHI KAZUO, YAMAZAKI, TAKAYOSHI, YANAUCHI, KAZUO
Applicants: TAISEI CHEMICAL IND LTD, TAISEI CHEMICAL INDUSTRIES LTD
Application year: 1999
Main classification: C08G18
IPC codes: C09D5, C09D175, C08G18