A method for producing a supported catalyst for ethylene polymerization and ethylene/alpha-olefin copolymerization

Abstract: The present invention relates to a method for producing a supported catalyst useful in polymerization of ethylene and copolymerization of ethylene and α-olefin. The method of the present invention comprises a treatment of the magnesium-containing carrier with a titanium compound containing oxygen atom(s), wherein said carrier is obtained by reaction of an organomagnesium compound of the structure of MgPh 2 · nMgCl 2 · mR 2 O (n=0.37~0.7; m≥1; R 2 O=ether; Ph=phenyl) with an organic chloride compound in a mole ratio of organic chloride compound/Mg≥0.5, at -20~80°C. According to the present invention a specific catalyst is provided whose activity is low in the beginning but slowly rises to a sufficient degree as the process of polymerization progresses, the polymer produced with the use of said catalyst having high bulk density, a well adjusted particle size distribution, and a narrow molecular weight distribution.

Description: [Background of the Invention] The present invention relates to a method for producing a catalyst for use in polymerization of ethylene and copolymerization of ethylene and α-olefin, and more particularly to a method for producing a catalyst containing a transition metal supported on a magnesium-containing carrier whose initial activity is low but slowly increasing to an optimal level as the polymerization progresses. By some of the co-inventors of the subject invention a method was developed some time ago for producing a supported catalyst for polymerization of ethylene and copolymerization of ethylene and α-olefin, by following the way of coating catalysts with a transition metal compound, that is, first reacting an organomagnesium compound having the structure of MgPh 2 · nMgCl 2 · mR 2 O (here, n = 0.37∼0.7; m≥2; R 2 O = ether; Ph = phenyl) with an organic halide, and next coating the thus produced carrier with such transition metal compounds as TiCl 4 , VCl 4 , or VOCl 3 (Application No. 330675/1995 for a Japanese patent). However, the catalyst produced by the publicly known art above, particularly the catalyst produced by the way of coating the carrier with TiCl 4 , is found having such problems as a broad molecular weight distribution and high initial activity, though it has the polymerization process partly improved by producing a polymer having a narrow particle size distribution and an increased bulk density. A way of effectively preventing generation of lumps in the reactor by adjusting the initial polymerization activity to a low point in the process of gaseous fluidized bed polymerization is publicly known. It is also a public knowledge that the quality of products can be improved by decrease of the output of polymers of low molecular weights to be extracted by hexane, if the polymer in use is of a narrow molecular weight distribution, especially in the case of products of linear low-density polyethylene produced by copolymerization of ethylene and α-olefin. In view of all this, a catalyst is particularly demanded whose activity'is low in the initial stage but slowly increases to the optimal height as the polymerization progresses. [Summary of the Invention] The objective of the present invention is to provide a method for producing a catalyst, which will make it possible to produce a polymer of a narrow particle size distribution and an increased bulk density, has a low activity in the initial stage but slowly increasing to an optimal level accordingly as the ethylene polymerization or ethylene/α-olefin copolymerization by slurry or gaseous process progresses, and is useful in ethylene polymerization or ethylene/α-olefin copolymerization, especially in the gaseous environment. [Brief Description of the Drawing] Fig. 1 shows the reaction rate curves in the ethylene polymerization by the use respectively of the catalyst produced in examples of the present invention and the catalyst by a comparative example. [Detailed Description of the Invention] The method for producing the catalyst of the present invention is characterized in that the carrier obtained by reacting an organomagnesium compound, MgPh 2 · nMgCl 2 · mR 2 O (here, n=0.37∼0.7; m≥1; R 2 O= ether; Ph=phenyl) with an organic chloride compound, is treated with a titanium compound containing oxygen atom(s). The organomagnesium compound used when the magnesium-containing carrier is produced is obtained by reacting magnesium in powder form and chlorobenzene in the presence of more than one electron-donating compounds. The electron-donors may include aliphatic ether and cyclic ether. The aliphatic ethers, here, can be represented by a general formula of R 2 OR 3 , where R 2 or R 3 is identical or different alkyl radical with two to eight carbons, and preferably an aliphatic ether having four to five carbons. The cyclic ethers are those having three or four carbons. The most preferable as electron donors are dibutyl or diisoamylethers. The magnesium-containing carrier is produced by reacting, at -20 to 80°C, a solution of said organomagnesium compound with one or more organic chlorides, preferably carbon tetrachloride, in a mole ratio of organic chloride compound/Mg≥0.5. The suspension of the carrier powder containing magnesium, obtained at this stage, has a particular particle size and a narrow particle size distribution. For the organic chlorides, the present invention uses such compounds of a general formula CR' n Cl (4-n) (here, n is an integer from 0 to 3), wherein R' is an alkyl radical, the number of whose carbons ranging from 1 to 12. The catalyst of the present invention is obtained by treating the magnesium-containing carrier produced by the method given above with an oxygen atom-containing titanium compound, in a mole ratio of Ti/Mg=0.01∼2.0, preferably 0.04∼0.5, in a hydrocarbon solvent, at 20∼100°C preferably 40∼80°C. If, on the one hand, the Ti/Mg mole ratio is higher than 2.0, it generally becomes necessary to remove the extra quantity of a titanium compound which has not been fixed on the supporter (carrier) during the process of washing the catalyst, and this removal of a titanium compound is invariably costly and troublesome because of its toxic and corrosive properties. If, on the other hand, the Ti/Mg mole ratio is lower than 0.01, the activity is proven to be insufficient. The oxygen atom-containing titanium compound used in the present invention has the general formula, Ti(OR) a X 4-a . R represents an aliphatic or aromatic hydrocarbon group having 1 to 14 carbons, or alternatively, COR'(here, R' represents an aliphatic or aromatic hydrocarbon group having 1 to 14 carbons), X represents Cl, Br, or I, and "a" represents 1, 2, or 3. The titanium compound of the above formula is made by mixing Ti(OR) 4 and TiX 4 , the mixture ratio being preferably 1:1. The preferable titanium compounds are titanium alcoxychlorides, e.g. Ti(OC 3 H 7 ) 2 Cl 2 , Ti(OC 3 H 7 )Cl 3 , Ti(OC 3 H 7 ) 3 Cl, Ti(OC 4 H 9 ) 2 Cl 2 , Ti(OC 4 H 9 )Cl 3 , Ti(OC 4 H 9 ) 3 Cl, Ti(OCH 2 CH(C 2 H 5 )(CH 2 ) 3 CH 3 ) 2 Cl 2 , and Ti(OCH 2 CH(C 2 H 5 )(CH 2 ) 3 CH 3 )Cl 3 . Before treatment of titanium or after production of the catalyst it is possible, when necessary, before washing, to treat with an organoaluminum compound in a mole ratio of Al/Ti= 0.1~2. The preferable Al/Ti mole ratio is 0.5~1.5, the preferable temperature 30∼80°C. In case too much organic aluminum is used, the carrier can be destroyed, giving rise to fine particles. For the organoaluminum compound, such an organoalkylaluminum having the general formula of AlR' n X (3-n) or an organic aluminum halogen compound can be used. Here, R' stands for an alkyl group having 1 to 16, more preferably, 2 to 12 carbons, X for chlorine, bromine, and other halogen compounds, and n an integer from 0 to 3, or fractions. Such organic aluminum compounds within the category include triethylaluminum, triisobutylaluminum, trihexylaluminum, trioctylaluminum, ethylaluminum chloride, methylaluminum chloride, ethylaluminum sesquibromide, isobutylaluminum sesquichloride, dimethylaluminum chloride, diethylaluminum chloride, diethylaluminum bromide, diethylaluminum iodide, dinormalpropylaluminum chloride, dinormalbutylaluminum chloride, diisobutylaluminum chloride, dinormaloctylaluminum iodide, methyl aluminum dichloride, ethylaluminum dichloride, isobutylaluminum dichloride, normalbutylaluminum dichloride, etc. Of all these, the more profitable organic aluminum compound can be chosen from dialkylaluminum chlorides or from ethylaluminum sesquichlorides. In the method for production of the catalyst in the present invention, in the process of forming the magnesium-containing carrier, a complex of organomagnesium compounds [MgPh 2 · nMgCl 2 · mR 2 O] is used in the state of solution, dissolved in chlorobenzene, ether (R 2 O), or a mixture of chlorobenzene and ether, or a mixture of chlorobenzene and aliphatic or aromatic compounds. The aforesaid organomagnesium compound in the state of solution is chlorinated with organic chloride in the mole ratio of the organic chloride compound/Mg ≥ 0.5, at -20 to 80°C. The organic chloride diluted in a hydrocarbon solvent can be used in the chlorination of organomagnesium compound. And in this way, a carrier with the magnesium in powder form suspended in the solvent is produced. The carrier obtained in this way possesses a narrow particle size distribution. The particle sizes of the carrier and the catalyst can be adjusted in the range from 5 to 150µm according to the conditions of the composition of the organomagnesium compounds and of the reaction of the organomagnesium compounds and the organic chloride compound. The magnesium-containing carrier obtained as above mainly contains, magnesium dichloride (80∼90wt%), ether (7∼15wt%), and a hydrocarbon complex (1∼5wt%). The catalyst is produced by treating the carrier with a titanium compound (Ti(OR) a X 4-a ) solvent, in a hydrocarbon solution. If, when producing the catalyst, the mole ratio of Ti(OR) a X 4-a /Mg is raised from 0.01 to 2.0, the Ti content of the catalyst rises from 1wt% to 10wt%, the activity per g-catalyst also rising. If TiCl 4 is used alone as the titanium compound, the Ti content in the catalyst only rises from 1wt% to 3wt% and stops there, increasing no more, even if the mole ratio of TiCl 4 /Mg is raised from 0.01 to 2.0. And when TiCl 4 is used alone for the titanium compound the initial activity of the catalyst becomes high, while the catalyst's initial activity is kept low if the titanium compound of Ti(OR) a X 4-a is used according to the present invention, thus, possibly preventing formation of lumps by the hot spot inside the gaseous fluidized bed reactor. The method in the present invention provides a catalyst which is highly-active, has a narrow particle size distribution and various average granule sizes, and is thus useful for various purposes. For example, the present invention can produce a catalyst with the particle size of 5∼10µm and 10∼15µm, useful in slurry polymerization of ethylene, and of 25∼150µm, useful in gaseous polymerization of ethylene. When a titanium compound, Ti(OR) a X 4-a is used for the active substance of the catalyst, a polyethylene having a narrow molecular weight distribution is obtained. The narrow molecular weight distribution is characterized by the melt index ratio, MI 21.6 /MI 2.16 < 30. The catalyst of the present invention can be coated, for pre-polymerization, with 3∼150g of an ethylene monopolymer or a copolymer of ethylene and α-olefin per one gram of the catalyst for polymerization. The catalyst of the present invention is used in both ethylene polymerization and ethylene/α-olefin copolymerization. The catalyst of the present invention can be used together with one or more organic aluminum compounds, or preferably trialkylaluminum, as its cocatalyst. The usable organic aluminum compound has a general formula: AlR n X 3-n . Here, R is an alkyl radical having 1 to 12 carbons; X a hydrogen atom, halogen atoms such as chlorine or fluorine and an alkoxy radical having 1 to 12 carbons; and n an integer of 1 to 3 or a fraction. For example, triisobutylaluminum, triethylaluminum, trimethylaluminum, tri-n-hexylaluminum, tri-n-octylaluminum, ethylaluminum sesquichloride, and diethylaluminum chloride, etc. can be used. The polymerization can be performed either in a hydrocarbon solvent (e.g., hexane or heptane) at 50∼100°C by a slurry polymerization process, or in the absence of a hydrocarbon solvent at 60∼120°C and under 2~40atm pressure by a gaseous polymerization process. As an agent for adjusting the molecular weights of polymers hydrogen (5∼90 bulk %) is used. Propylene, butene-1, hexene-1, 4-methylpentene-1, and other α-olefin are useful in an ethylene/ α -olefin copolymerization. The gaseous polymerization reaction is performed in a fluidized bed reactor using the publicly known fluidization process (See. C.Y.Wen and Y.H.Yu "Mechanics of Fluidization". Chemical Engineering Progress Symposium Series Vol. 62, p.100∼111 (1962)). Generally, a mixture for gaseous reaction flows out from the upper part of the reactor to recycle through a recycling tube, thermo-exchanger, and a compressor. During this recycling process, the mixture that has reacted in gaseous phase is generally cooled by the use of the thermo-exchanger to remove the heat generated while polymerization reaction. The polymerization is generally performed at the temperature between 0°C and 120°C. The mixture for gaseous reaction may contain hydrogen and an inert gas selected from nitrogen, methane, ethane, propane, butane, isobutane, etc. as molecular weight adjuster as well as such monomers as ethylene and such comonomers as α-olefin. When a fluidized bed reactor is used, the rate at which the mixture for gaseous reaction passes the fluidized bed is preferably twice to eight times as much as the minimum fluidization rate, namely 20~80cm/sec in general. The produced polymer is removed from the reactor continuously or intermittently, or preferably, at a constant rate. Below, the present invention is described in further detail, referring to examples of its embodiment. Yet, the following examples do not limit the scopes of the present invention. Example 1 <A> Production of organomagnesium compounds Inside a 1-liter glass reactor equipped with stirrer and temperature controller, 29.2g of magnesium powder (1.2mol) and 450ml of chlorobenzene (4.4mol) were reacted in the presence of a solution in which 203ml of dibutylether (1.2mol), 3ml of butylchloride and 0.05g of iodine as initiator were dissolved. The reaction was performed, while stirring, at 80∼100°C in an inactive gaseous environment (nitrogen, argon) for 10 hours. Next, the reacted mixture was left alone, without stirring, for 12 hours, and then the liquid was separated from the precipitate. The liquid was a solution of the organomagnesium compound having the formula, MgPh 2 · 0.49MgCl 2 · 2(C 4 H 9 ) 2 O, dissolved in chlorobenzene (the concentration of Mg being 1.1mol per liter). <B> Production of carrier 100ml (Mg of 0.11mol) of the solution obtained in <A> above was put in a reactor equipped with a stirrer, and 21.2ml of CCl 4 (0.22mol of CCl 4 ) dissolved in heptane of 42ml was added to it at 20°C, in the period of an hour. The mixture was stirred at the same temperature for 60 minutes, the solvent was removed, and the precipitate was washed in 100ml of n-hexane at 60°C four times. In this way, 11.8g of magnesium containing carrier in powder form was obtained in a state of suspension in n-hexane. <C> Production of catalyst To the n-hexane suspension of the magnesium containing carrier was added so much titanium alkoxychloride, which was produced by mixing 6ml of TiCl 4 and 15.1ml of titanium propoxide(Ti(OC 3 H 7 ) 4 ), that the Ti/Mg mole ratio reached 1, the mixture was then heated to 60°C, stirred for two hours, and the solid precipitate thus obtained was washed in 100ml of n-hexane at 60°C four times. Thus a catalyst containing Ti by 5.9wt% was produced. The average particle size of the catalyst was 55µm. <Polymerization> The ethylene polymerization was performed inside a 2-liter steel reactor equipped with a stirrer and a temperature controller. N-hexane (1000mol) was used as hydrocarbon solvent, and 2mmol of Al(i-Bu) 3 as cocatalyst. The polymerization was performed under 7.5atm of ethylene pressure, 4.5atm of hydrogen pressure, at 80°C for one hour. The curves showing the reaction rate according to the different activities of the catalyst were analyzed by the use of a meter for calculating the mass flux of ethylene and a computer for translating the measured flux speed into curves. The data on the results of the polymerization are given in Table 1. For the experiments so much of the catalyst as amounted to 0.015mmol of Ti was taken, the catalytic activity confirmed being 4.0kg PE per gram of catalyst. The melt index (MI) of the polyethylene was determined to be 1.6g/10min under the load of 2.16kg at 190°C and the MI fraction for 21.6kg and 2.16kg was 29. The bulk density of polyethylene powder was 0.37g/cm 3 and it had a narrow particle size distribution. The SPAN value calculated by the following formula from the analyses of the powdery form was 0.6 or less. SPAN = (d90-d10)/d50. Here, d90, d50, and d10 indicate the respective sizes of polyethylene particles with their total respective particle contents of 90wt%, 50wt%, and 10wt%. Example 2 A catalyst was produced in exactly the same way as in Example 1, except that so much of TiCl 2 (OC 3 H 7 ) 2 produced by mixing 1.5ml of TiCl 4 and 3.8ml of titanium propoxide(Ti(OC 3 H 7 ) 4 ), was added to the n-hexane suspension of the magnesium containing carrier obtained in Example 1 that the Ti/Mg mole ratio reached 0.25. Consequently, a catalyst containing Ti by 3.3wt% was obtained. The polymerization of ethylene was performed in the same way as in Example 1. The results of the ethylene polymerization are given in Table 1. Example 3 <A> Production of organomagnesium compounds Inside a 6-liter glass reactor equipped with a stirrer and a temperature controller, 145.4g of magnesium powder (6mol) and 1,512ml of chlorobenzene (15mol) were reacted in the presence of a solution in which 2,435ml of diisoamyl ether (12mol), 21ml of butylchloride and 1.45g of iodine as initiator were dissolved. The reaction was performed, while stirring, at 80∼100°C in an inactive gaseous environment (nitrogen, argon) for 10 hours. Next, the reacted mixture was left alone, without stirring, for 12 hours, and then the liquid was separated from the precipitate. The liquid was a solution of the organomagnesium compound of the formula, MgPh 2 · 0.49MgCl 2 · 1.5(C 6 H 13 ) 2 O, dissolved in chlorobenzene (the concentration of Mg being 0.83mol per liter). <B> Production of carrier 2,500ml (2.1mol of Mg) of the obtained solution was put in a reactor equipped with a stirrer, and 200ml of CCl 4 (2.1mol of CCl 4 ) dissolved in 200ml of heptane was added to it at 50°C, in the period of an hour. The mixture was stirred at the same temperature for 60 minutes, the solvent was removed, and the precipitate was washed in 2,000ml of n-hexane at 60°C four times. In this way, 219g of the magnesium containing carrier in powder form was obtained in a state of suspension in n-hexane. <C> Production of catalyst To the n-hexane suspension of the magnesium containing carrier (0.35 mol of MgCl 2 ) was added so much TiCl 2 (OC 3 H 7 ) 2 which was produced by mixing 18.8ml of TiCl 4 and 47.6ml of titanium propoxide (Ti(OC 3 H 7 ) 4 ), that the Ti/Mg mole ratio reached 1, the mixture was then heated to 60°C, stirred for two hours, and the solid precipitate thus obtained from it was washed in 350ml of n-hexane at 60°C four times. Thus a catalyst containing Ti by 9.7wt% was produced. The average particle size of the catalyst was 50µm. The ethylene polymerization was performed in the same way as in Example 1. The results of ethylene polymerization are given in Table 1. Example 4 A catalyst was produced in the same manner as in Example 3 except that to the n-hexane suspension of the magnesium containing carrier obtained in Example 3 was added so much of the TiCl 2 (OC 3 H 7 ) 2 produced by mixing 4.7ml of TiCl 4 and 11.9ml of titanium propoxide (Ti(OC 3 H 7 ) 4 ) that the Ti/Mg mole ratio reached 0.25, and the catalyst obtained in this way contained Ti by 3.5wt%. The ethylene polymerization was performed in exactly the same way as in Example 1, the results being given in Table 1. Example 5 A catalyst was produced in the same way as in Example 3 except that to the n-hexane suspension of the magnesium containing carrier obtained in Example 3 was added so much of the TiCl 2 (OC 3 H 7 ) 2 produced by mixing 4.7ml of TiCl 4 and 11.9ml of titanium propoxide (Ti(OC 3 H 7 ) 4 ) that the Ti/Mg mole ratio reached 0.25 and that the product was treated with 0.088mol of diethylaluminum chloride (Al/Ti mole ratio=1), before washing, and thereupon, a catalyst containing Ti by 8.2wt% was obtained. The ethylene polymerization was performed in exactly the same way as in Example 1. The results of the ethylene polymerization are given in Table 1, and the reaction rate curves in Fig. 1. Example 6 A catalyst was produced in the same manner as in Example 3 except that to the n-hexane suspension of the magnesium containing carrier obtained in Example 3 was added so much of the TiCl 3 (OC 3 H 7 ) produced by mixing 7.1ml of TiCl 4 and 6.0ml of titanium propoxide (Ti(OC 3 H 7 ) 4 ) that the Ti/Mg mole ratio reached 0.25. The catalyst thus obtained contained Ti by 2.5wt%. The ethylene polymerization was performed in exactly the same way as in Example 1, the results being given in Table 1, and the reaction rate curves in Fig. 1. Example 7 Making use of the catalyst obtained in Example 3, a copolymerization of ethylene and 1-hexane was performed. The polymerization was performed in the same way as in Example 3, with the only exception that 150cc of 1-hexane was used before the polymerization. As a result of the polymerization, a copolymer of ethylene and 1-hexane with a concentration of 0.947g/cc was obtained. The results of this copolymerization are given in Table 1. Example 8 A catalyst was produced in exactly the same way as in Example 1, except that to the n-hexane suspension of the magnesium containing carrier obtained in Example 1 was added so much of TiCl 2 (OC 4 H 9 ) 2 produced by mixing 1.5ml of TiCl 4 and 4.7ml of titanium butoxide (Ti(OC 4 H 9 ) 4 ) that the Ti/Mg mole ratio reached 0.25; in consequence, a catalyst containing Ti by 2.7 wt% was obtained. The polymerization of ethylene was performed in the same way as in Example 1. The results of the ethylene polymerization are given in Table 1. Comparative Example 1 A catalyst was produced in the same way as in Example 3 with the only exception that, in place of TiCl 2 (OC 3 H 7 ) 2 , so much TiCl 4 was added that the Ti/Mg mole ratio reached 1, and the catalyst thus obtained contained Ti by 0.7wt%. The ethylene polymerization was performed in exactly the same way as in Example 1, the results being given in Table 1 and the reaction rate curves in Fig. 1. Examples 5 and 6, where compounds of TiCl 2 (OC 3 H 7 ) 2 and TiCl 3 (OC 3 H 7 ) were used, each displays a low initial activity, but Comparative Example 1 shows a high initial activity. Results of Experiments for Polymerization Capability Exmp. Ti(wt%) Activity Kg-PE/Gcat · hr MI(2.16) MI(21.6)/MI(2.16) BD(g/cc) Span Ratio 1 5.9 4.0 1.57 29 0.37 < 0.6 2 3.3 2.6 5.27 25 0.36 < 0.6 3 9.7 4.0 3.22 29 0.40 < 0.6 4 3.5 3.2 3.95 26 0.41 < 0.6 5 8.2 6.7 3.29 27 0.39 < 0.6 6 2.5 5.3 3.15 29 0.40 < 0.6 7 4.6 4.8 3.52 23 0.37 < 0.6 8 2.7 1.44 2.3 30 0.33 < 0.6 Comp. 1 0.7 4.4 7.5 27 0.42 < 0.6 Example 9 <A> Production of organomagnesium compounds Inside a 5-liter glass reactor equipped with a stirrer and a temperature controller, 146.0g of magnesium powder (6.0mol) and 2,250ml of chlorobenzene (22mol) were reacted in the presence of a solution in which 1,015ml of dibutylether (6.0mol), 15ml of butylchloride and 0.25g of iodine as initiator were dissolved. The reaction was performed, while stirring, at 80∼100°C in an inactive gaseous environment (nitrogen, argon) for 10 hours. Next, the reacted mixture was left alone, without stirring, for 12 hours, and then the liquid was separated from the precipitate. The liquid was a solution of the organomagnesium compound having the formula, MgPh 2 · 0.49MgCl 2 · 2(C 4 H 9 ) 2 O, dissolved in chlorobenzene (the concentration of Mg being 1.1mol per liter). <B> Production of carrier 2000ml (Mg of 2.2mol) of the solution obtained in <A> above was put in a reactor equipped with a stirrer, and 424.0ml of CCl 4 (4.4mol of CCl 4 ) dissolved in heptane of 840ml was added to it at 20°C, in the period of an hour. The mixture was stirred at the same temperature for 60 minutes, the solvent was removed, and the precipitate was washed in 2000ml of n-hexane at 60°C four times. In this way, 236g of the magnesium containing carrier in powder form was obtained in a state of suspension in n-hexane. <C> Production of catalyst To the n-hexane suspension of the magnesium containing carrier was added so much titanium alkoxychloride which was produced by mixing 30ml of TiCl 4 and 76ml of titanium propoxide (Ti(OC 3 H 7 ) 4 ) that the Ti/Mg mole ratio reached 0.25. The reacted mixture was then heated to 60°C, stirred for two hours, and the solid precipitate thus obtained was washed in 2000ml of n-hexane at 60°C four times. Thus, a catalyst containing Ti by 3.3wt% was produced. The average particle size of the catalyst was 55µ m. <D> Pre-polymerization The pre-polymerization of ethylene was performed inside a 200-liter steel reactor equipped with a stirrer and a temperature controller. N-hexane (150ℓ ) was used as hydrocarbon solvent, and 932ml of Al(n-Octyl) 3 with the concentration of 894mMAl/liter, as cocatalyst was put into the reactor. Then, 2410ml of the main catalyst with the concentration of 53.7mMTi/liter was also put into the reactor. The pre-polymerization was performed, while stirring, by providing with an ethylene of 1.64Kg/Hr and a hydrogen of 0.3g/Hr, at 60°C for 10 hours. After pre-polymerization, dried nitrogen was provided to obtain 16.4Kg of dried pre-polymer which is in free-flowing state. The properties of the pre-polymer were as follows: Bulk density : 0.41g/cc Average size of pre-polymer : 224µ m Span ratio : 0.41 Distribution of particle sizes : 71.9 vol% < 250µ m 0.15 vol% < 125µ m 0.0 vol% < 80µ m <E> Polymerization in gaseous fluidized bed A polymerization was performed in a polymerization reactor with the fluidized bed, which was composed of a perpendicular cylinder of 43cm in diameter and 6.5m in height. The pressure of the gaseous mixture to be reacted was kept 20Kgf/cm 2 and this mixture was passed through the fluidized bed of polyethylene powder, with an upward fluidizing speed of 47cm/sec. The pre-polymer produced in <D> was provided at regular intervals of time to the fluidized bed reactor, to produce 10Kg/Hr of polymer. 80kg of seed powder was initially put into the fluidized bed reactor. The reaction temperature, the gaseous composition and the properties of the polymer produced are given in Table 2. As a result of observing the polymerization for seven consecutive days, it was found that production of polymer was kept constantly by 10Kg/Hr without creating agglomerate or sheet. The quality of an ethylene copolymer produced by the above process was kept uniform and highly satisfactory. Comparative Example 2 A catalyst was produced in the same way as in Example 9 with an exception that, in place of titanium alkoxychloride, 120ml of TiCl 4 was added to the magnesium containing carrier produced in Example 9 with the Ti/Mg mole ratio being 1. The thus obtained catalyst contained 0.9 wt% of Ti. The pre-polymerization was performed in the same way as in Example 9 with an exception that the main catalyst with the concentration of 14.6mMTi/liter was used instead of the one with 53.7mMTi/liter. As a result of pre-polymerization, 16.4Kg of dried pre-polymer was obtained in a state of free-flowing. The properties of the pre-polymer were as follows: Bulk density: 0.36g/cc Average size of pre-polymer: 240µ m Span ratio: 0.5 Distribution of particle sizes: 70.1 vol% < 250µ m 0.12 vol% < 125µ m 0.0 vol% < 80µ m The pre-polymer produced above was supplied to the fluidized bed reactor introduced in Example 9 at regular intervals of time, to produce a polymer of 10Kg/Hr. 80kg of seed powder was initially put into the fluidized bed reactor. The reaction temperature, the gaseous composition and the properties of the polymer produced are given in Table 2. As a result of observing the polymerization for consecutive days, on the second day from when the polymerization reaction started, the polymer removal path was blocked because it was full stuffed with agglomerate so that further polymerization was impossible. In the course of polymerization, the fluctuation of the polymerization temperature by hot spot was observed. Results of Experiments on Gaseous Polymerization Division Exm. 9 Comp. 2 Conditions C4/C2 mole ratio 0.3 0.26 H2/C2 mole ratio 0.25 0.25 Fluidizing linear velocity cm/sec 45 45 Polymerization temperature °C 78 78 Properties of Polymer Melt Index 1.0 1.0 Melt flow ratio 28 26 Density 0.920 0.920 Ti ppm 3 1 Characteristics of Polymer Particle Bulk density 0.4 0.36 Average particle size 1200 1200 Span ratio 0.45 0.5 [Effects of Invention] According to the present invention, a catalyst is obtained which has a narrow particle size distribution and a high activity and when a polymerization is performed with the use of the catalyst obtained in the present invention, its initial activity is low but it slowly rises to reach an optimal degree, thereby the polymerization can be performed without generation of agglomerate in a gaseous fluidized bed reactor. The polymer produced with the use of this catalyst possesses a narrow distribution of molecular weights.

Claims: A method for producing a catalyst for polymerization of ethylene and for copolymerization of ethylene and α-olefin, comprising the steps of reacting an organomagnesium compound having the structure of MgPh 2 · nMgCl 2 · mR 2 O, wherein Ph = phenyl, n = 0.37∼0.7, m ≥ 1, and R 2 O-ether, and an organic chloride compound in the organic chloride compound/Mg mole ratio of 0.5 or more at - 20~80 °C, and treating the thus obtained magnesium-containing carrier with a titanium compound containing oxygen atom(s) in the Ti/Mg mole ratio of 0.01~2.0, wherein said titanium compound is represented by Ti(OR) a X 4-a wherein R represents an aliphatic or an aromatic hydrocarbon group having from 1 to 14 carbons, or COR' which is an aliphatic or aromatic hydrocarbon group, whose R' has from 1 to 14 carbons, X standing for Cl, Br, or I, and "a" for 1,2 or 3. The method according to Claim 1, wherein said organomagnesium compound is produced by reacting metallic magnesium with chlorobenzene in the presence of dibutyl ether or diisoamylether. The method according to Claim 1, wherein said organic chloride compound is carbon tetrachloride. The method according to Claim 1 wherein said titanium compound is titanium alkoxychloride. The method according to Claim 1, wherein the method further comprises a treatment of the carrier treated with the titanium compound with an organoaluminum compound in a Al/Ti mole ratio of from 0.1 to 2. A method for producing a polymer of ethylene or a copolymer of ethylene and α -olefin in the process of gaseous polymerization by the use of the catalyst produced by the method of Claim 1. The method according to Claim 6, wherein the catalyst is coated, for pre-polymerization, with 3∼150g of an ethylene monopolymer or a copolymer of ethylene and α-olefin per one gram of the catalyst for the gaseous polymerization.

Inventors: CHANG HO-SIK, KANG YOUN-KYUNG, NIKITIN VALENTIN EVGENIEVICH, ZAKHAROV VLADIMIR ALEXANDROVIC, CHANG, HO-SIK, KANG, YOUN-KYUNG, NIKITIN, VALENTIN EVGENIEVICH, ZAKHAROV, VLADIMIR ALEXANDROVICH, Kang, Youn-Kyung 231 South 34 Street
Applicants: SAMSUNG GENERAL CHEMICALS CO, SAMSUNG GENERAL CHEMICALS CO., LTD.
Application year: 1999
Main classification: C08F10
IPC codes: C08F4, C08F2, C08F210, C08F110, C08F10