CRAYONS CONTAINING ESTER WAXES

Abstract: Disclosed is a marking composition suitable for preparing crayons having improved properties. For example, the composition provides excellent smoothness and great color delivery. Embodiments of the composition comprise a fatty acid, a hard wax, an emollient, and a colorant. In some embodiments, the marking composition may also contain a soft wax. In some other embodiments, the marking composition comprises a fatty acid, a hard wax, a soft wax, and a colorant. The composition is also substantially free of tackiness to the touch.

Description: CRAYONS CONTAINING ESTER WAXES TECHNICAL FIELD OF THE INVENTION The present invention relates to a marking composition and to a writing instrument such as a crayon fabricated from such a marking composition. In particular, this invention relates to a marking composition useful as crayons that have desirable laydown characteristics when applied on substrates such as paper. BACKGROUND OF THE INVENTION Marking compositions are well known in the art that are formulated from combinations of waxes, fatty acids, colorants, color extenders, and other additives. These marking compositions can be used to fabricate crayons, which can be used to draw, write, or color on porous and non-porous substrates. Crayons are most often used by children on various types of paper, such as notebook paper, art paper, and posterboard. Furthermore, crayons are available in a wide selection of colors, ranging from primary colors to fluorescent colors. A variety of crayons and marking compositions have been disclosed in the patent literature. See, for example, U.S. Patents 3,409,574, 3,933,708, 4,212,676, 4,990,013, and 5,383,954. Despite this, consumers desire crayons with improved properties to obtain better laydown and better drawing qualities as well as less flaking from completed drawings using the crayons. Laydown is a measure of the smoothness qualities with which the writing composition transfers to the writing surface. Children prefer crayons having improved laydown since they can produce marks and crayon drawings while exerting minimal pressure on the crayon. Smooth and slick color laydown is especially important to children who are mentally or physically impaired. An added benefit that is especially desired by children is that a crayon having improved laydown characteristics yields marks having richer and more brilliant colors. While the crayons of U.S. Patent 5,383,954 are excellent crayons, in use the crayons yield a considerable amount of flaking. Flaking, or loose particles of crayon material, can present a clean-up problem in the home when children use crayons which flake since the flakes can be ground into the working surface or, as is often the case, home carpeting. Others have proposed that laydown of crayons may be improved by increasing the amounts of emollients, for example, oils such as castor oil, in the crayon formulation. This approach is not without drawbacks. For example, the emollient adversely affects other desirable properties of the marking composition. For example, the strength of the writing instrument made from such compositions decreases resulting in manufacturing problems as well as problems in the use of these writing instruments. For example, writing instruments such as crayons formed from such compositions break or crumble rather easily, especially when used by children. The use of greater amounts of emollients also adversely affects the tackiness of the writing instrument. For example, the writing instrument becomes excessively tacky to the touch, especially when held between the fingers during writing. This excessive tackiness creates an unpleasant feeling for the user. There may also be excessive transfer of some of the components of the writing composition, for example, the pigment, to the user's hands or clothes. The excessive transfer of materials, besides creating an unpleasant feeling to the user, can cause unnecessary stains to the hands and clothes as well as in areas such as carpets where children use the crayons. A better crayon is found in U.S. Patent 5,383,954 by the present inventor. The glitter crayon disclosed in the patent excels at trapping glitter on a page when a mark is made. The crayons made according to this patent exhibit significant levels of product laydown. Thus, there remains a need for a marking composition that has the desirable laydown characteristics. More particularly, there is a need for a marking composition that minimizes friction between the crayon and the substrate to allow for a smooth and slick laydown of color with minimal exertion of pressure by the user. There also remains a need for a marking composition with improved laydown properties that is not overly tacky to the touch and does not exhibit excessive flaking. There further remains a need for a marking composition which does not excessively transfer materials to the hands or clothes of the user. There further remains a need for a marking composition having improved laydown characteristics that has the desirable mechanical strength to withstand use by children. These and other advantages of the present invention, as well as additional inventive features, will become apparent from the description of the present invention provided herein. BRIF SUMMARY OF THE INVENTION Many of the foregoing needs have been fulfilled by the present invention which provides a marking composition that exhibits improved color coverage, color intensity and uniformity, and smooth or slick laydown. The marking composition is also substantially free of tackiness to the touch. The crayons of the present invention provide increased color delivery. The present invention further provides smooth crayons characterized, e.g., by increased wear rate. Certain embodiments of the marking composition of the present invention comprise combinations of a fatty acid, an emollient, a colorant, a hard wax, and a soft wax, wherein at least a portion of the waxes are ester waxes in such amounts that the composition has the desired smooth laydown characteristics when applied on substrates. In some other embodiments, the marking composition of the present invention comprises a fatty acid, a hard wax, a soft wax, and a colorant. While the invention has been described and disclosed below in connection with certain preferred embodiments and procedures, it is not intended to limit the invention to those specific embodiments. Rather it is intended to cover all such alternative embodiments and modifications as fall within the spirit and scope of the invention. DETAILED DESCRIPTION OF EMBODIMENTS The present invention provides marking compositions having improved smoothness, laydown, color delivery, and/or increased transfer or wear rate. Writing instruments comprising the marking compositions such as crayons provide added coloring enjoyment to the users, particularly children. In accordance with one embodiment of the present invention, the marking composition comprises a fatty acid, an emollient, a colorant, a hard wax and a soft wax wherein at least a portion of the waxes are ester waxes in amounts such that the composition has the smooth laydown characteristics when applied on substrates. In another embodiment of the present invention, the marking composition comprises a fatty acid, a hard wax, a soft wax, and a colorant. The compositions also have the advantage that they are substantially free of tackiness to the touch. The present inventive composition is particularly well suited for use in preparing crayons. A detailed discussion of each of the ingredients used in making the marking compositions of the invention is set forth below. The marking composition contains a suitable fatty acid or fatty acids. The fatty acid may be a saturated fatty acid, an unsaturated fatty acid, or a mixture or combination thereof. Preferably, the fatty acid is one that adds strength to the composition, especially when the composition is fabricated as a crayon. Longer carbon chain fatty acids generally impart greater hardness and mechanical strength to the composition. The fatty acid generally has from about 12 to about 30 carbon atoms, and preferably from about 16 to about 24 carbon atoms. Suitable fatty acids include lauric acid, myristic acid, palmitic acid, stearic acid, and mixtures thereof. Stearic acid is a preferred fatty acid. The amount of fatty acid that can be used depends to some extent on the amount of other materials constituting the marking composition, particularly the amount of hard wax employed. The fatty acid content can be lowered if the hard wax content is suitably increased to provide the desired mechanical strength. The fatty acid may be present in any suitable amount, for example, it can be present in an amount up to about 60% by weight of the composition. In certain embodiments, the fatty acid is present in an amount of from about 3% by weight to about 25% by weight of the marking composition, and in certain other embodiments, the fatty acid is present in an amount of from about 15% by weight to about 30% by weight of the marking composition. Some other embodiments include a fatty acid in an amount of from about 30% by weight to about 55% by weight of the marking composition. The marking composition of the present invention comprises at least one hard wax. The hard wax also imparts desired hardness and mechanical strength to the crayon. Any suitable hard wax can be used. Preferably a wax having a penetration of about 40 mm or less at 25°C, as determined by the needle penetration method set forth in ASTM D1321 is used. Examples of suitable hard waxes include candelilla wax, carnauba wax, beeswax, modified beeswax such as PEG modified beeswax, microcrystalline wax, fatty acid esters, and alkali and alkaline earth metal and ammonium salts of fatty acids, and combinations thereof. Any other appropriate hard wax may be used. Several hard waxes are commercially available. Examples include the synthetic candelilla wax having a melting point of 72.5-82.5°C, an acid value of 14-25, a saponification value of 44-66, and a needle penetration of 1-4 mm (lOOg, 5 sec, 25°C) , and available from Koster Keunen, Inc. in Watertown, Connecticut. This wax has the general composition of 50% hydrocarbons, 40% esters and 10% acids by weight. Other examples of hard waxes available from Koster Keunen, Inc. are set forth in Table I below along with their physical properties. Natural hard waxes such as paraffin wax, candelilla wax, beeswax, carnauba wax, ceresine wax, and ozokerite wax which are suitable for use in the composition of the present invention can also be obtained from Koster Keunen, Inc. Natural candelilla wax contains approximately 50% hydrocarbons, 28% esters, 12% neutral resins, and 7% acids. The natural beeswax contains about 70% esters, 13% hydrocarbons, 12% fatty acids, and 4% fatty alcohols. Natural carnauba wax contains about 70% monoesters, 15% free alcohols, 5% fatty acids, 5% resins, and 5% other materials. Natural ceresine wax is a blend of hydrocarbon mineral waxes mainly consisting of paraffin waxes, and has a melting point of 130-170°F. Ozokerite wax is a blend of hydrocarbon mineral waxes mainly consisting of microcrystalline wax and has a melting point of 160-180°F. Microcrystalline wax may be a hard wax or a soft wax. A hard microcrystalline wax suitable for use in the present invention can be obtained from Witco in Greenwich, Connecticut, as MULTIWAX W445, having a melting point of 54-102°C. Examples of other commercially available hard waxes include the Polymer Wax AV518 having a drop point of 50-55°C (ASTM D3 954) and a zero acid content is available from Hoechst Celanese, Somerville, New Jersey. Hoechst Wax LP is a hard acid wax having a drop point of 82-89°C (ASTM D 566) and an acid number of 113-130. Hoechst Wax S is also a hard acid wax having a drop point of 81-87°C (ASTM D 566) and an acid number of 130-150. Hoechst Wax E is an ester derived from Montan wax having a drop point of 79-85°C (ASTM D 566) and an acid number of 15-20. Hoechst Wax F has a drop point of 77-83°C (ASTM D 566) and an acid number of 6-10. Hoechst Wax KSL is a hard ester wax having a drop point of 80-85°C (ASTM D 566) and an acid number of 28-38. LIPOWAX™ KB2- 46-2 is a hard, cream-colored wax produced by Lipo Chemicals, Inc. in Paterson, New Jersey, and has a melting point of approximately 60°C. The composition of LIPOWAX KB2-46-2 is believed to be a trade secret. Table I describes, but does not in any way limit, hard waxes suitable for use in the present invention is presented below. Table I details various properties of the hard waxes set forth therein. Table I Some Examples of Commercially Available Waxes Kester Wax 1 A.V. E.V. H.V. M.P. Pen. <M> <n> I.V. K-48 <2 116-120 <4 47-49°C <10 478 32.3 <2 K-56 <2 101-105 <4 54-56°C <10 538 37 <2 K-59 <2 97-102 <4 57-59°C <10 553 37.4 <2 K-62 <2 93-97 <4 61-63°C <10 580 39.3 <2 K-72 <2 78-90 <4 70-74°C <10 650 44 <2 Synthetic Beeswax 17-24 70-80 <15 60-65°C »15 658 45.6 <15 co Synthetic Carnauba 2-7 75-85 <40 82-86°C <2 750 54 <12 K-82 <5 70-85 <10 82-86°C <2 732 50 <4 K-100 <5 65-85 <10 95- <2 980 68 <4 105°C K-82D 2 <5 50-70 <5 78-83°C >10 1350 92 <5 A.V. = acid value <M> = average molecular weight E.V. = ester value <n> = average carbon chain length H.V. = hydroxy value I.V. = iodine value M.P. = melting point Pen. = penetration, mm at 25C by ASTM D1321 1. Available from Koster Keunen, Inc., Watertown, Connecticut 2. K-80D22 is a hard wax comprising straight chain even numbered diesters , Any suitable amount of the hard wax can be included in the composition of the present invention. The hard wax can be present in an amount of up to about 64% by weight of the marking composition. In certain embodiments, the hard wax is present in an amount of from about 39% by weight to about 64% by weight of the marking composition, and preferably in an amount of from about 45% by weight to about 55% by weight of the marking composition. In certain other embodiments, the hard wax is present in an amount of from about 10% by weight to about 35% by weight, and in some other embodiments, the hard wax is present in an amount of from about 40% by weight to about 50% by weight of the marking composition. Excessive amounts of hard wax can adversely affect the laydown property. In certain other embodiments, for example, where the amount of emollient is low or none, the hard wax can be present in an amount of from about 10% by weight to about 30% by weight of the marking composition, and preferably in an amount of from about 15% by weight to about 25% by weight of the marking composition. Generally, the compositions of the invention can include an emollient, a soft wax, or a combination of an emollient and a soft wax. When both a soft wax as described below and an emollient are used, the hard wax preferably is used in an amount that is substantially equal to the amount of soft wax, and more preferably in amount greater than that of the soft wax. It is desirable to include an emollient in compositions of the invention to enable the marking composition to be more readily and easily transferred to a substrate through normal application of the marking composition to the substrate. The emollient thus provides a lubricant effect or slipperiness to the marking composition to facilitate the gliding of the marking composition across the surface of a substrate and to ensure a smooth laydown of the marking composition onto the substrate. The emollient also assists in ensuring the retention of certain other ingredients such as glitter in the marking composition transferred to the substrate. As such, the emollient typically is a liquid or paste at room temperature and is preferably miscible with the other components in the composition, particularly the wax or the fatty acid. In certain embodiments however, the emollient may be a solid such as a flake. Any suitable emollient may be used in the present inventive marking composition. Emollients such as lanolin oil and its derivatives, mineral oil, fatty esters, fatty acid esters, fatty alcohols, mono- and di-esters of propylene glycols, glycerol di-esters, mono- and di-esters of polyethylene glycols, petrolatum, vegetable shortenings, dimers and trimers of fatty acids, plant oils, silicones, and mixtures thereof are suitable for use in compositions of the invention. Suitable lanolin derivatives include acetylated lanolin, acetylated lanolin alcohol, hydrogenated lanolin, lanolin alcohol, lanolin acids, isopropyl lanolate, lanolin wax, and hydroxylated lanolin. Suitable fatty esters and fatty acid esters include isopropyl myristate, myristyl myristate such as that marketed as LIPONATE MM by Lipo Chemicals of New Jersey, and esterified fatty acid propoxylates such as polyoxypropylene (2) myristyl ether propionate. Also suitable is tridecyl trimellitate such as that marketed as LIPONATE TDTM by Lipo Chemicals. Suitable fatty alcohols include oleyl alcohol, and suitable vegetable shortenings include KREMIT® (Armour, Omaha, Nebraska) . Suitable plant oils include castor oil, coconut oil, olive oil, peanut oil, safflower oil, sesame oil, soybean oil, wheat germ oil, corn oil, avocado oil, almond oil, grape seed oil, jojoba oil, apricot kernel oil, palm oil, and sunflower seed oil. Suitable silicones include DOW-CORNING® 556, 593, and 1107 fluids (Dow- Corning, Midland, Michigan) . Other possible emollients include longer chain hydrocarbons, particularly alkenes, such as ' polyoxypropylene-polyoxyethylene block copolymers such as PLURONIC® 25R4 and PLURONIC 25R8 (BASF, Parsippany, New Jersey) . The emollient may be present in any suitable amount, for example, in an amount of up to 45% by weight of the marking composition, and preferably in an amount of from about 5% to about 25% by weight of the marking composition. Excessive amounts of emollients can increase the tackiness adversely. In certain embodiments, especially the embodiments having a large amount of a soft wax, the emollient can be present in a low amount or omitted while still maintaining the desired improved laydown characteristics. As noted above, either an emollient or a soft wax, or a combination of emollient and soft wax is included in compositions of the invention. Soft waxes suitable for use in compositions of the invention generally have a needle penetration of greater than about 40 mm at 25°C, according to ASTM D1321. Examples of soft waxes suitable for use in the invention include Lanolin Wax having a melting point of 52°C maximum and 0.56% maximum free fatty acid content and available from the Fanning Corporation in Chicago, Illinois. Other examples of suitable soft waxes include hydrogenated lanolin available under the name of FANCOL HL™ which is a mixture of fatty alcohols also available from the Fanning Corporation; hydrogenated castor oil available from Caschem, Inc. in Bayonne, New Jersey, as CASTORWAX™ MP-70, and having a freezing/melting point of 158°F; and LIPOWAX KB2444 produced by Lipo Chemicals which is a cream-colored wax having a melting point of about 90°C. The exact composition of LIPOWAX KB2444 is believed to be a trade secret of Lipo Chemicals. Another example of a soft wax is a hydroxy polyester which is 7-hydroxy isohexanol polyester having a melting point of 74-84°C, an acid value of less than 5, an ester value of 50-70, a hydroxyl value of 35-50, a needle penetration of greater than 50 mm at 25°C by ASTM D1321, an average molecular weight of about 1000, an average carbon length of 66, and an iodine value of less than 5, and is available from Koster Keunen, Inc. Certain soft waxes, particularly the hydroxy polyester, help to hold emollients used in compositions of the invention in place, thereby acting as gelling agents. These soft waxes help make the marking composition less oily to the touch. Any suitable amount of the soft wax can be used to prepare the marking composition. The soft wax can be present in an amount of up to about 60% by weight of the marking composition. In certain embodiments, for example, where the amount of emollient is low or none, the soft wax can be present in an amount of from about 20% by weight to about 60% by weight of the marking composition. In certain other embodiments, for example, where an emollient is present in a significant amount, the soft wax can be present in an amount of up to about 4% by weight of the marking composition, e.g., from about 1% by weight to about 4% by weight of the composition. In other embodiments, the soft wax can be present in an amount of from about 5% by weight to about 10% by weight of the composition. As can be seen above, certain of both the hard waxes and the soft waxes are termed ester waxes. Ester waxes may be naturally occurring waxes such as beeswax, carnauba wax or rice wax. In addition, some synthetic waxes, such as the Kester Waxes™ marketed by Koster Keunen, Inc., are ester waxes. The Kester Waxes™ are composed of various esters which are prepared by esterification of natural plant fatty acids and natural plant fatty alcohols. By means of this process, saturated ester mixtures are obtained which can have a carbon chain length from 22 to 46 atoms. Ester waxes may be mono-ester waxes, di-ester waxes, poly-ester waxes, and hydroxy acid ester waxes. The ester waxes may be saturated, unsaturated or branched ester ' s ranging from about C 22 through about Cioo. The marking composition preferably contains a colorant which can be a pigment or dye. The pigment may be an inorganic pigment, an organic pigment, or a mixture thereof. The inorganic pigment is preferably iron blue, iron oxide, zinc oxide, ultramarine blue, titanium dioxide, or a mixture thereof. The organic pigment is preferably an azo, a naphthol, a dianisidine orange, a lithol, a diarylide yellow, methyl violet, or a phthalo pigment. The pigment may be combined with a clay carrier, if desired. Dyes, either acidic or basic, can be used in the present inventive marking composition. The pigment can have any suitable particle size, however, a preferable particle size is from about 0.1 micron to about 25 microns. More preferably, the pigment has a particle size of about 0.3 micron to about 20 microns, and, even more preferably, the pigment particle size is in the range of about 0.5 micron to about 15 microns. Examples of suitable dyes include the polymeric colorants REACTINT™ brand Blue x 3LV, Orange x 38, and Violet x 80LT, available from the Milliken Chemical Co. in Inman, South Carolina. These are dark viscous liquids containing the dyes Blue x 3LV, Orange x 38, and Violet x 80LT. The colorant may be present in any suitable amount. The present inventive marking composition preferably contains pigment in an amount of from about 0.5% to about 20% by weight of the marking composition, more preferably from about 2% to about 15% by weight of the marking composition. Where a dye colorant is used, it may be included in an amount of from about 1% by weight to about 3% by weight of the marking composition. The marking composition of the present invention can. contain additional ingredients, for example, the marking composition may additionally include a filler. The filler preferably functions as a pigment dispersant or extender, if pigment is added to the marking composition. Any suitable filler may be utilized, such as calcium carbonate, titanium dioxide, talc, silica, clay (e.g., kaolin clay) , feldspar, cornstarch, mica, and mixtures thereof. Examples of preferred fillers include talc and kaolin clay. The particle size of the filler is preferably 50 microns or less, more preferably 25 microns or less, although if mica is used, the particle size is preferably about 25-75 microns. Talc of about 3-6 microns average diameter particle size is preferred for use in certain embodiments of the present invention. Modified, e.g., coated, talcs are further preferred. An example of coated talc is NYTAL™ 400, which is available from The Vanderbilt Co. in Norwalk, Connecticut. A further example of a coated talc is MEARL Talc TCA sold by The Mearl Corporation in Charleston, SC. In certain embodiments, the filler acts to provide a shimmering effect to the composition. Filler can also be included in compositions of the invention when a pigment is not used. In cerain embodiments, the filler improves the strength of the marking composition and the marking instrument . Two or more fillers can be combined for use in compositions of the invention. For example, the mica particles can be coated with titanium dioxide. Such a coated mica is available as MAGNAPEARL™ from The Mearl Corporation. MAGNAPEARL can improve the smooth laydown as well as provide a shimmering effect to the marking composition. MAGNAPEARL can also provide added strength to the marking composition and the writing instrument. The filler may be present in any suitable amount. Preferably filler is used in an amount up to about 20% by weight of the marking composition, and more preferably in an amount of from about 5% to about 15% by weight of the marking composition. The marking composition of the present invention can include a gelling agent. The gelling agent may stabilize the composition, e.g., by arresting the sweating or blooming to the surface of low molecular weight materials, for example, oils. The gelling agent may also improve the smoothness or creaminess of the marking composition. Any suitable gelling agent can be used. For example, a gelling agent comprising a polyamide, preferably an ester terminated polyamide such as the Union Camp Corporation's polyamide resin No. X35-879-48, can be used. A cleanability additive can also be included in the marking composition of the present invention to aid in the removal of the composition, preferably with mild soap and water, from non-porous surfaces, such as table tops, counter tops, etc. Suitable cleanability additives include polyoxypropylene-polyoxyethylene block copolymers, polyoxyethylene alcohols, polyoxyethylene esters, polyoxyethylene ethers, and derivatives and mixtures thereof. The marking composition of the present invention preferably contains a cleanability agent such as polyoxyethylene (12) tridecyl ether or alcohol, polyoxyethylene (10) alkyl aryl ether, polyoxyethylene (40) stearate, or polyoxyethylene (20) stearyl alcohol. The marking composition more preferably contains polyoxyethylene (40) stearate (available as LIPOPEG® 39S (Lipo Chemicals, Patterson, New Jersey) ) or polyoxyethylene (12) tridecyl ether alcohol (available as RENEX® 30 (ICI America, Wilmington, Delaware)), most preferably a mixture of the two. Certain emollients may also act as cleanability additives or aid in cleanability, such as polyoxypropylene-polyoxyethylene block copolymers, e.g., PLURONIC® 25R4 or 25R8. The cleanability additive may be present in any suitable amount. Preferably it is present in an amount up to about 5% by weight of the marking composition, and more preferably in an amount from about 1% to about 4% by weight of the marking composition. Other additives may be incorporated into the marking compositions of the present invention in minor amounts. For example, processing aids such as foam inhibitors and mold release agents, as well as oxidation and UV stabilizers may be added. These additives are typically used in an amount of from about 0.01% to about 5% by weight of the marking composition, and preferably in an amount of from about 0.1% to about 1% by weight of the marking composition. Examples of suitable foam inhibitors include petroleum hydrocarbons such as FOAMKILL® 614 (Crucible Chemical Co., Greenville, South Carolina) and cetyl dimethicone. Examples of suitable mold release agents include the Group IIA metal salts of fatty acids, particularly calcium stearate. Examples of suitable oxidation stabilizers include sterically hindered phenols. Examples of suitable UV stabilizers include hindered amine light stabilizers and benzotriazoles . The marking composition of the present invention may be prepared by heating the components to a semisolid, or preferably, liquid, state and mixing them together. Generally, a portion of the waxes and fatty acid, is heated above its melting temperature, e.g., to about 104-116°C (220-240°F) . Then, the remainder of the waxes and the fatty acid is added to the liquified waxy material, while stirring the composition with suitable stirring means, such as, for example, a disperser head mixer. The filler and colorant are then added in sequence to the composition under continued stirring of the composition. The emollient, along with any other additives such as cleanability agents and the like, are added to the liquified material, while continuing to stir the composition. The composition is then appropriately molded such as by pouring the composition into flatbed molds. The mold is cooled and the composition is shaped into suitable forms such as crayons . The present invention provides a crayon that offers increased color delivery, e.g., when applied to substrates such as paper. The crayon of the present invention has increased wear rate. The color delivery or the wear rate can be measured by any suitable method, for example, by preparing rubouts under a suitable application pressure or load. For example, rubouts can be prepared by applying the crayon on a substrate such as paper using a load of 800 grams. The color patch produced from the crayon of the present invention has a greater coverage than crayons such as the CRAYOLA crayons or the glitter crayons. The crayon of the present invention provides a color delivery greater than the standard crayon and the glitter crayon. Thus, for example, the crayon of the present invention delivers color that is up to about 50% greater than that of the standard crayon. Crayons according to certain embodiments of the present invention deliver color that is from about 20% to about 50% greater than that of the standard crayon. Crayons according to some embodiments of the present invention deliver color that is from about 30% to about 50% greater than that of the standard crayon. Crayons according to certain other embodiments of the present invention deliver color that is from about 40% to about 50% greater than that of the standard crayon. The color delivery can be determined by any suitable method, for example, from the lightness (L) values measured on the color patches based on the L.a.b. color scheme. The lightness value provides a measurement of the amount of white paper that shows through in a color crayon rubout. The difference in the lightness values (or delta L) between a color patch and the white paper substrate is a measure of the coverage or color delivery by the crayon. A crayon providing an excellent coverage would produce a rubout having a large delta L. The crayon of the present invention wears at a rate higher than the standard crayon and the glitter crayon. Thus, for example, the crayon of the present invention has a wear rate that is up to about 50% greater than that of the standard crayon. Crayons according to certain embodiments of the present invention have a wear rate that is from about 20% to about 50% greater than that of the standard crayon. Crayons according to some embodiments of the present invention have a wear rate that is from about 30% to about 50% greater than that of the standard crayon. Crayons according to certain other embodiments of the present invention have a wear rate that is from about 40% to about 50% greater than that of the standard crayon. The wear rate of the crayon can be determined by any suitable method, e.g., by measuring the weights of the crayon before and after a rubout of a predetermined area is made. The difference in the measured weights relative to the weight before making the rubout provides the wear rate. The marking composition of the present invention is hard enough for children to handle and resists breaking, yet is soft enough to allow for the smooth and slick laydown of the composition on a substrate with minimal pressure in the course of the normal marking of a substrate with the composition. Rich and substantially uniform color is also achieved with the marking composition of this invention. Under certain conditions, there is less flaking than occurs with the "soft" glitter crayons disclosed in U.S. Patent 5,383,954. Thus, the laydown characteristics of compositions of the present invention are improved over such characteristics of previously available compositions. The marking composition of the present invention is suitable for use in writing instruments, in particular, crayons, and may be applied to a variety of porous and non-porous writing surfaces or substrates. It will be appreciated by those skilled in the art that the marking compositions of the present invention can be varied, depending upon the selection of certain of the major components and the amounts of those components. This allows the composition to be modified to achieve the desired laydown. Thus, where the preferred components include a hard wax, a soft wax and an emollient, the fatty acid may be included in an amount of from about 30 to about 55% by weight of the entire composition; the hard wax may be included in an amount of from about 10 to about 35% by weight of the entire composition; the soft wax may be included in an amount of from about 1 to about 4% by weight of the entire composition; and the emollient may be included in an amount of from about 10 to about 40% by weight of the entire composition. A filler may be included in compositions of the invention in amounts of from about 0 to about 20% by weight of the entire composition and colorant, such as pigment, may be included in amounts of from about 0 to about 15% by weight of the entire composition. Preferably, in such compositions of the inventions, of the waxes included, from about 10% by weight to about 30% by weight of the total composition are ester waxes. Specifically, where these various component classes are used in such a relationship, specific ingredients such as the following will yield a composition of the invention set forth in Table II: Table II Component Preferred Range, wt% Stearic acid about 30-about 55 Paraffin wax about 3-about 10 Syn. Carnauba wax about 8-about 20 KESTER WAX K80D22 about 1-about 4 Hydroxy polyester about 1-about 4 Myristyl myristate about 2-about 5 Tridecyl trimellitate about 3-about 10 Castor oil about 5-about 25 MAGNAPEARL 2000 about 0-about 20 Colorant about 2-about 15 Example 1 This example illustrates an embodiment of the composition of the invention, prepared as follows: Component wt% Stearic acid 41.8 Paraffin wax 6.8 Syn. Carnauba wax 13.6 KESTER WAX 80D22 1.7 Hydroxypolyester 1.7 LIPONATE MM 3.4 LIPONATE TDTM 5.4 Castor oil 8.2 MAGNAPEARL 2000 6.8 Ultramarine Blue 10.6 Total 100.0 A crayon was formed from the coloring composition of Example 1. The crayon exhibited the desired smooth laydown characteristics. Compositions of the invention may also be prepared using a fatty acid, a hard wax, soft wax, and an emollient in a composition where the fatty acid is present in an amount of from about 3 to about 25% by weight of the entire composition; the hard wax is present in an amount of from about 39 to about 64% by weight of the entire composition; the soft wax is included in an amount of from about 1 to about 4% by weight of the entire composition; and the emollient is present in an amount of from about 5 to about 15% by weight of the entire composition. In such a composition, filler is included in amounts of from about 1 to about 15% by weight of the entire composition and a colorant is included in amounts of from about 1 to about 15% by weight of the entire composition. Where a dye colorant is used, typically from about 1% to about 3% by weight of the total composition is included. Preferably, in such compositions of the inventions, of the waxes included, from about 10% by weight to about 25% by weight of the total composition are ester waxes. Specifically, where these various component classes are used in such a relationship, specific ingredients such as the following will yield a composition of the invention set forth in Table III: Table III Component preferred range, wt% Stearic acid about 3-about 25 Paraffin wax about 30-about 45 Syn. Carnauba wax about 8-about 15 KESTER WAX K80D22 about 1-about 4 Hydroxypolyester about 1-about 4 Castor Oil about 5-about 15 MAGNAPEARL 2000 about 1-about 15 Colorant about 1-about 3 Example 2 This example illustrates the preparation of such an embodiment of the marking composition of the present invention. The following ingredients were combined and melt mixed to obtain a marking composition having smooth laydown characteristics. Component wt% Stearic acid 22.2 Paraffin wax 37.5 Syn. Carnauba wax 12.1 KESTER WAX K80D22 1.5 Hydroxypolyester 1.5 Castor oil 12.6 MAGNAPEARL 2000 12.6 Liquid Dye (Milliken Color) 1.5 Total 100.0 A third embodiment of the invention may be prepared where only the primary components of a fatty acid, a hard wax, and a soft wax are used. In such a composition, the fatty acid is present in an amount of from about 15 to about 30% by weight of the entire composition; the hard wax is present in an amount of from about 10 to about 30% by weight of the entire composition; the soft wax is included in an amount of from about 20 to about 60% by weight of the entire composition. In such a composition, filler may be included in amounts of from about 5 to about 20% by weight of the entire composition and a colorant is typically included in amounts of from about 1 to about 15% by weight of the total composition and more preferably from about 1% to about 5% by weight of the entire composition. Specifically, where these various component classes are used in such a relationship, specific ingredients such as the following will yield a composition of the invention set forth in Table IV: Table IV Component preferred range, wt% Stearic Acid about 15-about 30 LIPOWAX KB2444 about 20-about 60 LIPOWAX KB2462 about 5-about 15 Paraffin wax about 5-about 15 FOAMKILL 614 about 0.1-about 1 NYTAL 400 (talc) about 5-about 20 Colorant about 1-about 5 Example 3 Example 3 illustrates a preparation of such an embodiment marking composition of the present invention. The following ingredients were combined and melt mixed to obtain a marking composition having smooth laydown characteristics . Component wt-ι Stearic Acid 19. LIPOWAX KB2444 43. LIPOWAX KB2 62 9. Paraffin wax 9. FOAMKILL 614 0. NYTAL 400 14 Phthalo green pigment 2. Total 100.0 Examples 4-15 Further examples of compositions of the present invention (Examples 4-7) were prepared to enable a comparison with certain other crayons. The following examples of compositions of the invention were prepared: Ex. 4 Ex. 5 Ex. 6 Ex. 7 Red Green Yellow Orange Component wt% wt% wt% wt% Stearic acid 18.0 17.8 19.6 18.8 Paraffin wax 33.5 33.23 36.41 35.02 Syn. Candelilla wax 8.2 8.0 8.8 8.5 KESTER WAX K82D wax 1.6 1.6 1.7 1.7 Hydroxypolyester wax 2.7 2.7 2.9 2.8 PEG-40 Stearate 1.6 1.6 1.7 1.7 Castor oil 10.9 10.7 11.8 11.3 Mearl Talc TCA (coated 13.6 13.4 14.7 14.2 talc) Colorant - Pigment 9.6 10.7 2.1 5.7 Cetyl Dimethicone defoamer 0.3 0.27 0.29 0.28 Total 100.0 100.0 100.0 100.0 For comparison, four CRAYOLA TM crayons typically manufactured for use by children and commercially available from the assignee of the present invention under the Catalog No. 52-3008 were tested. Each of the CRAYOLA crayons of Examples 8-11 was composed of stearic acid, paraffin wax, talc and a colorant. Example 8 was a red crayon, Example 9 was green, Example 10 was yellow, and Example 11 was orange. For a further comparison, four glitter crayons made according to U.S. Patent 5,383,954 were prepared as follows : Ex. 12 Ex. Ex. 14 Ex. 15 13 Red Green Yellow Orange Component wt% wt% wt% wt% Stearic acid 22.8 21.5 23.8 22.7 Paraffin wax 42.3 39.74 44.22 42.13 Witco W835 wax 2.7 2.6 2.8 2.7 PEG-40 Stearate 2.2 2.1 2.3 2.2 Mineral Oil 2.8 2.6 2.8 2.7 Castor oil 10.9 10.3 11.3 10.8 Nytal 400 Talc 6.8 6.5 7.0 6.8 Colorant - Pigment 4.8 10.3 1.0 5.4 Silver Glitter 4.4 4.1 4.5 4.3 Cetyl Dimethicone defoamer 0.3 0.26 0.28 0.27 Total 100.0 100.0 100.0 100.0 Compositions of each of the formulations of Examples 4 through 15 were molded into crayons. Rubouts were then made using the crayons according to a standard test procedure as follows: Four sheets of sixty-pound bond paper are stacked one on top of the other and positioned on a slough tester such that a rubout will be made near the top of the first sheet of paper. The paper is then locked in position. The crayon is then weighed and the weight is recorded. The crayon is then inserted into the slough tester holder so that the point of the crayon is touching the paper without putting pressure on the paper. The crayon holder is tightened to hold the crayon in place. The slough tester arm is then pulled down with an 800-gram weight and the pressure is applied to the crayon. The slough tester is then turned on and is left on until the machine completes a second pass on the paper with the crayon. The crayon is then locked in the up position and the paper is re- positioned so that another rubout can be made next to the two-pass rubout. The crayon is then adjusted so that the point rests on the paper with no pressure and the crayon is locked in place. The 800-gram weight is again applied to the slough tester arm and the machine is turned on until the crayon makes three passes on the paper. At this point, rubouts from a total of five passes have been made. The tester is then turned off and the crayon is removed from the tester. The crayon is then weighed. The paper on which the rubouts have been made is then carefully removed from the slough tester and weighed taking care not to knock any flakes off the paper. Any flakes on the paper are then lightly brushed off and the paper is reweighed. At this point, three measurements of the crayon being tested may be assessed. First, the wear rate of the crayon may be calculated by subtracting the final weight of the crayon from the crayon's original weight. Second, the amount of flaking may be calculated by subtracting the weight of the paper with the rubout after the flakes are brushed off from the weight of the paper, rubout and flakes. Third, the transfer weight may be calculated by subtracting the weight of the flakes from the wear rate. The data for the crayons prepared from Examples 4 through 15, is set forth in Table V, below. Table V Wear Rate Flaking Transfer Weight gram gram gram Example 4 0.0260 0.0024 0.0236 Example 5 0.0263 0.0030 0.0233 Example 6 0.0194 0.0020 0.0174 Example 7 0.0244 0.0025 0.0219 Example 8 0.0256 0.0010 0.0246 Example 9 0.0196 0.0020 0.0176 Example 10 0.0257 0.0015 0.0242 Example 11 0.0178 0.0008 0.0170 Example 12 0.0435 0.0099 0.0336 Example 13 0.0467 0.0150 0.0317 Example 14 0.0475 0.0143 0.0332 Example 15 0.0457 0.0134 0.0323 Easily seen from the data in Table V is that the crayons of the present invention as prepared in Examples 4 through 7 provided better laydown of crayon than the traditional crayon of Examples 8 through 11. While providing this better laydown, the crayons of Examples 4 through 7 produced substantially less flaking than the glitter crayons of Examples 12 through 15. In addition, the marks made by the crayons of the present invention were of substantially higher quality than those made by the regular crayons (Examples 8-11) or the glitter crayons (Examples 12-15) . The color was richer and more uniform in appearance. Example 16 This Example illustrates a preparation of a marking composition according to another embodiment of the present invention. The following ingredients were used to prepare the pink colored marking composition: Component wt% Paraffin Wax 41.4 Stearic Acid 22.5 Ester Terminated Polyamide Resin 2.5 (Union Camp Corp. #x35-879-48) CERA BELLINA (PEG-3 Beeswax) 1.5 Vegetable Wax Blend (Koster 6.1 Keunen Inc. ) Branched Ester Wax (Koster Keunen 2.5 Wax #240) NYTAL 400 12.9 ABILWAX 9840 (defoamer) 0.6 Colorant (Calcium Rubine and 10.0 Ti0 2 ) Total 100.0 Example 17 This Example illustrates a preparation of a marking composition according to another embodiment of the present invention. The following ingredients were used to prepare the red colored marking composition: Component wt% Paraffin Wax 41.2 Stearic Acid 22.4 Ester Terminated Polyamide Resin 2.5 (Union Camp Corp. #x35-879-48) CERA BELLINA (PEG-3 Beeswax) 1.5 Vegetable Wax Blend (Koster 6.1 Keunen Inc. ) Branched Ester Wax (Koster Keunen 2.5 Wax #240) NYTAL 400 12.8 ABILWAX 9840 (defoamer) 0.5 Colorant (Lithol Rubine and 10.4 Calcium Lithol) Total 100.0 Example 18 This Example illustrates a preparation of a marking composition according to another embodiment of the present invention. The following ingredients were used to prepare the violet colored marking composition: Component wt% Paraffin Wax 42.6 Stearic Acid 23.1 Ester Terminated Polyamide Resin 2.6 (Union Camp Corp. #x35-879-48) CERA BELLINA (PEG-3 Beeswax) 1.6 Vegetable Wax Blend (Koster 6.3 Keunen Inc. ) Branched Ester Wax (Koster Keunen 2.6 Wax #240) NYTAL 400 13.2 ABILWAX 9840 (defoamer) 0.6 Colorant (Methyl Violet and 7.4 Violet Lake) Total 100.0 Example 19 This Example illustrates a preparation of a marking composition according to another embodiment of the present invention. The following ingredients were used to prepare the orange colroed marking composition: Component wt% Paraffin Wax 43.0 Stearic Acid 23.4 Ester Terminated Polyamide Resin 2.6 (Union Camp Corp. #x35-879-48) CERA BELLINA (PEG-3 Beeswax) 1.6 Vegetable Wax Blend (Koster 6.4 Keunen Inc. ) Branched Ester Wax (Koster Keunen 2.6 Wax #240) NYTAL 400 13.4 ABILWAX 9840 (defoamer) 0.6 Colorant (Dianisidine Orange) 6.4 Total 100.0 Examples 20-23 These examples serve as comparative examples. Standard crayons were prepared from the following ingredients in which in Examples 20-23 pink, red, violet, and orange colored crayons were produced, respectively. Component Ex. 20 Ex. 21 Ex. 22 Ex. 23 wt% wt% wt% wt% Paraffin wax 47.3 44.7 49.0 48.4 Stearic Acid 31.5 29.8 32.7 32.3 Talc 13.9 13.1 14.4 14.2 Colorant (Calcium Rubine + 7.3 — — — Ti0 2 ) Colorant (Lithol Rubine + 12.4 Calcium Lithol) Colorant (Methyl Violet + 3.9 Violet Lake) Colorant (Dianisidine Orange) 5.1 Total 100.0 100.0 100.0 100.0 Examples 24-27 These examples also serve as comparative examples. Glitter crayons according to the ' 954 patent were prepared from the following ingredients except that the glitter was omitted from the composition. Examples 24-27 produced pink, red, violet and orange colored glitter crayons, respectively. Component Ex. 24 Ex. 25 Ex. 25 Ex. 26 wt% Wt% wt% wt% Paraffin wax 44.3 44.7 46.1 45.5 Stearic Acid 23.7 23.9 24.6 24.3 Talc 7.7 7.8 8.0 7.9 K82D Ester Wax 3.0 3.0 3.2 3.1 Myristyl Myristate 3.0 3.1 3.2 3.1 Hydroxy Polyester 1.8 1.8 1.9 1.9 LIPOPEG 39S (PEG Stearate) 1.8 1.8 1.9 1.9 Cetyl Dimethicone (defoamer) 0.3 0.3 0.3 0.3 MICROWAX W835 - Witco 6.1 6.1 6.3 6.2 Colorant (Calcium Rubine + 8.3 — — — Ti0 2 ) Colorant (Lithol Rubine + — 7.5 Calcium Lithol) Colorant (Methyl Violet + — -- 4.5 Violet Lake) Colorant (Dianisidine Orange) 5.8 Total 100.0 100.0 100.0 100.0 Example 28 This Example illustrates the superior color coverage produced by the marking composition of the present invention. Color patches (1.75 inch x 1.75 inch) were produced by the crayons of Examples 16-27. Each patch was produced by a single pass of the crayon under a load of 800 grams. Each crayon was placed in a holder with its sharp tip on the white paper. During the production of the rubouts, the base of the rubout machine moved back and forth as the crayon moved in the opposite direction. The lightness values of the patches were measured on an X-Rite SP68 Spectrophotometer, and the results obtained are set forth in Table VI: Table VI: Lightness (delta L) values of color patches Lightness Values Color Standard Glitter Present crayon crayon Inven. (Ex. 20-23) (Ex. 24-27) Crayon (Ex. 16-19) Violet -45.25 -50.31 -58.90 Red -41.50 -44.75 -46.81 Orange -22.32 -25.93 -26.94 Pink -11.79 -18.45 -20.94 The foregoing shows that the crayons of the present invention provides a greater coverage of the paper as a result of delivering a greater amount of color relative to the standard and glitter crayons. Example 29 This Example illustrates the superior softness or smoothness of the marking composition of the present invention. The marking composition of the present invention showed high wear rates. The weights of the crayons in Examples 16-27 were measured before and after the preparation of the rubouts. The results obtained are set forth in Table VII: Table VII: Wear Rates of Crayons Weights Color Standard Glitter Present crayon crayon Inven. (Ex. 20-23) (Ex. 24-27; Crayon (Ex, 16-19) grams grams grams Violet Before 4.4672 4.3586 4.5467 After 4.4490 4.3389 4.5242 Difference 0.0182 0.0197 0.0225 Red Before 4.4862 4.1973 4.6033 After 4.4679 4.1755 4.5812 Difference 0.0183 0.0218 0.0227 Orange Before 4.5415 4.1824 4.4040 After 4.5234 4.1613 4.3806 Difference 0.0181 0.0211 0.0234 Pink Before 4.5683 4.1290 4.5654 After 4.5512 4.1068 4.5410 Difference 0.0171 0.0222 0.0244 The difference between the weights before and after preparing of the rubouts is the crayon wear rate. The increase or improvement in the wear rate of the crayons of the present invention relative to the wear rate of the standard crayon is 100 x (Wp-Wo) /Wo, wherein Wp is the wear rate of the crayons of the present invention and Wo is the wear rate of the standard crayon. The increases in wear rates were calculated for both glitter crayons and the crayons of the present invention, and the crayons of the present invention had the highest increases in wear rates as set forth in Table VIII: Table VIII: Percent increase in wear rates relative to the standard crayon Percent increase in wear rate Color Glitter Present crayon Inven. Crayon (Ex. 24-27) (Ex. 16-19) Violet 8.2 23.6 Red 19.1 24.0 Orange 16.6 29.3 Pink 29.8 42.7 While this invention has been described with emphasis upon a preferred embodiment, it will be obvious to those of ordinary skill in the art that the preferred composition may be varied. It is intended that the invention may be practiced otherwise than as specifically described herein. Accordingly, this invention includes all modifications encompassed within the spirit and scope of the following claims.

Claims: WHAT IS CLAIMED IS: 1. A marking composition comprising a fatty acid in an amount of from about 30% by weight to about 55% by weight of the composition, a hard wax in an amount of from about 10% by weight to about 35% by weight of the composition, a soft wax in an amount of from about 1% by weight to about 4% by weight of the composition, and an emollient in an amount of from about 10% by weight to about 40% by weight of the composition, wherein of said hard waxes and said soft waxes from about 10% to about 30% by weight of said composition are ester waxes. 2. A marking composition comprising a fatty acid in an amount of from about 3% by weight to about 25% by weight of the composition, a hard wax in an amount of from about 39% by weight to about 64% by weight of the composition, a soft wax in an amount of from about 1% by weight to about 4% by weight of the composition, and an emollient in an amount of from about 5% by weight to about 15% by weight of the composition, wherein of said hard waxes and said soft waxes from about 10% to about 25% by weight of said composition are ester waxes. 3. A marking composition comprising a fatty acid in an amount of from about 15% by weight to about 30% by weight of the composition, a hard wax in an amount of from about 10% by weight to about 30% by weight of the composition, and a soft wax in an amount of from about 20% by weight to about 60% by weight of the composition. 4. A marking composition comprising a fatty acid in an amount of from about 3% by weight to about 25% by weight of the composition, a hard wax in an amount of from about 39% by weight to about 64% by weight of the composition, and a soft wax in an amount of from about 1% by weight to about 10% by weight of the composition. 5. A marking composition comprising a fatty acid in an amount of from about 15% by weight to about 30% by weight of the composition, a hard wax in an amount of from about 40% by weight to about 50% by weight of the composition, and a soft wax in an amount of from about 5% by weight to about 10% by weight of the composition. 6. The marking composition of any of claims 1-5, wherein said fatty acid has from about 16 to about 30 carbon atoms. 7. The marking composition of any of claims 1-6, wherein said fatty acid is stearic acid. 8. The marking composition of any of claims 1-2 and 5-7, wherein said ester wax is selected from the group consisting of mono-ester waxes, di-ester waxes, poly-ester waxes, branched ester waxes, and hydroxy acid ester waxes having a carbon chain length of from about 22 to about 100. 9. The marking composition of any of claims 1-2 and 5-8, wherein said ester wax is selected from the group consisting of hydroxy polyester, beeswax, PEG modified beeswax, rice wax, synthetic beeswax, carnauba wax, synthetic carnauba wax, and an ester wax having an acid value less than 5, an ester value between 50 and 70, and a melting point between 78 and 83°C. 10. The marking composition of any of claims 1-9, wherein said hard wax is selected from the group consisting of paraffin wax, candelilla wax, carnauba wax, ester waxes, beeswax, PEG modified beeswax, microcrystalline wax, fatty acid esters, and alkali and alkaline earth metal and ammonium salts of fatty acids, and combinations thereof. 11. The marking composition of any of claims 1-10, wherein said hard wax has a needle penetration of less than about 40 mm at 25°C by ASTM D1321. 12. The marking composition of any of claims 1-11, wherein said soft wax is selected from the group consisting of microcrystalline wax, vegetable fats, animal fats, ester waxes, fatty acid esters, and alkali and alkaline earth metal and ammonium salts of fatty acids, and hydroxy polyesters, and combinations thereof. 13. The marking composition of any of claims 1-2 and 6-12, wherein said emollient is selected from the group consisting of lanolin oil and its derivatives, mineral oil, fatty esters, fatty acid esters, fatty alcohols, mono- and di-esters of propylene glycols, glycerol di-esters, mono- and di-esters of polyethylene glycols, petrolatum, vegetable shortening, dimers and trimers of fatty acids, plant oils, silicones, and combinations thereof. 14. The marking composition of any of claims 1-2 and 6-12, wherein said emollient is selected from the group consisting of castor oil, tridecyl trimellitate, myristyl myristate, and combinations thereof. 15. The marking composition of any of claims 1-2 and 3-14, said composition including a colorant in an amount of from about 1% by weight to about 15% by weight of the composition. 16. The marking composition of any of claims 3-5, said composition including a colorant in an amount of from about 1% by weight to about 15% by weight of the composition. 17. The marking composition of any of claims 1-16, which includes a filler. 18. The marking composition of claim 16, wherein said filler is selected from the group consisting of calcium carbonate, talc, nylon modified talc, titanium dioxide, silica, clay, feldspar, corn starch, mica, and combinations thereof. 19. The marking composition of any of claims 1-18, which includes a gelling agent. 20. The marking composition of claim 19, wherein said gelling agent comprises a polyamide resin. 21. The marking composition of claim 19 or 20, wherein said gelling agent is an ester terminated polyamide resin. 22. The marking composition of any of claims 1-21, which is substantially free of glitter. 23. A crayon comprising the marking composition of any of claims 1-22. 24. A method of making the marking composition of claim 15, comprising combining and mixing said fatty acid, said hard wax, said soft wax, and said emollient at an elevated temperature to obtain a melt mix, and combining and mixing said melt mix and said colorant. 25. A method of making the marking composition of claim 16, comprising combining and mixing said fatty acid, said hard wax, and said soft wax, at an elevated temperature to obtain a melt mix, and combining and mixing said melt mix and said colorant. 26. A crayon that provides an increased color delivery. 27. The crayon of claim 26, which provides said increased color delivery when it is applied on a substrate under a load of 800 grams. 28. The crayon of claim 26 or 27, wherein said crayon provides a color delivery that is up to about 50% greater than the standard crayon. 29. The crayon of any of claims 26-28, wherein said crayon provides a color delivery that is from about 20% to about 50% greater than the standard crayon. 30. The crayon of any of claims 26-29, wherein said crayon provides a color delivery that is from about 30% to about 50% greater than the standard crayon. 31. The crayon of any of claims 26-30, wherein said crayon provides a color delivery that is from about 40% to about 50% greater than the standard crayon. 32. A crayon that provides an increased wear rate. 33. The crayon of claim 32, which provides said increased wear rate when it is applied on a substrate under a load of 800 grams. 34. The crayon of claim 32 or 33, wherein said crayon has a wear rate that is up to about 50% greater than that of the standard crayon. 35. The crayon of any of claims 32-34, wherein said crayon has a wear rate that is from about 20% to about 50% greater than that of the standard crayon. 36. The crayon of any of claims 32-34, wherein said crayon has a wear rate that is from about 30% to about 50% greater than that of the standard crayon. 37. The crayon of any of claims 32-34, wherein said crayon has a wear rate that is from about 40% to about 50% greater than that of the standard crayon. 38. The crayon of any of claims 32-34, wherein said crayon has a wear rate that is from about 20% to about 30% greater than that of the standard crayon. 39. The crayon of any of claims 26-38, wherein said crayon comprises a fatty acid in an amount of from about 15% by weight to about 30% by weight of the composition, a hard wax in an amount of from about 40% by weight to about 50% by weight of the composition, and a soft wax in an amount of from about 5% by weight to about 10% by weight of the composition. 40. The crayon of any of claims 26-38, wherein said crayon comprises a fatty acid in an amount of from about 30% by weight to about 55% by weight of the composition, a hard wax in an amount of from about 10% by weight to about 35% by weight of the composition, a soft wax in an amount of from about 1% by weight to about 4% by weight of the composition, and an emollient in an amount of from about 10% by weight to about 40% by weight of the composition, wherein of said hard waxes and said soft waxes from about 10% to about 30% by weight of said composition are ester waxes. 41. The crayon of any of claims 26-38, wherein said crayon comprises a fatty acid in an amount of from about 3% by weight to about 25% by weight of the composition, a hard wax in an amount of from about 39% by weight to about 64% by weight of the composition, a soft wax in an amount of from about 1% by weight to about 4% by weight of the composition, and an emollient in an amount of from about 5% by weight to about 15% by weight of the composition, wherein of said hard waxes and said soft waxes from about 10% to about 25% by weight of said composition are ester waxes. 42. The crayon of any of claims 26-38, wherein said crayon comprises a fatty acid in an amount of from about 15% by weight to about 30% by weight of the composition, a hard wax in an amount of from about 10% by weight to about 30% by weight of the composition, and a soft wax in an amount of from about 20% by weight to about 60% by weight of the composition. 43. The crayon of any of claims 26-38, wherein said crayon comprises a fatty acid in an amount of from about 3% by weight to about 25% by weight of the composition, a hard wax in an amount of from about 39% by weight to about 64% by weight of the composition, and a soft wax in an amount of from about 1% by weight to about 10% by weight of the composition. 44. The crayon of any of claims 39-43, wherein said fatty acid has from about 16 to about 30 carbon atoms. 45. The crayon of claim 44, wherein said fatty acid is stearic acid. 46. The crayon of any of claims 39-45, which includes an ester wax. 47. The crayon of claim 46, wherein said ester wax is selected from the group consisting of mono-ester waxes, di-ester waxes, poly-ester waxes, and hydroxy acid ester waxes having a carbon chain length of from about 22 to about 100. 48. The crayon of claim 46 or 47, wherein said ester wax is selected from the group consisting of hydroxy polyester, beeswax, PEG modified beeswax, branched ester wax, rice wax, synthetic beeswax, carnauba wax, synthetic carnauba wax, and an ester wax having an acid value less than 5, an ester value between 50 and 70, and a melting point between 78 and 83°C. 49. The crayon of any of claims 39-48, wherein said hard wax is selected from the group consisting of paraffin wax, candelilla wax, carnauba wax, ester waxes, branched ester waxes, branched ester wax, beeswax, PEG modified beeswax, microcrystalline wax, fatty acid esters, and alkali and alkaline earth metal and ammonium salts of fatty acids, and combinations thereof. 50. The crayon of any of claims 39-49, wherein said hard wax has a needle penetration of less than about 40 mm at 25°C by ASTM D1321. 51. The crayon of any of claims 39-50, wherein said soft wax is selected from the group consisting of microcrystalline wax, vegetable fats, vegetable waxes, animal fats, ester waxes, fatty acid esters, and alkali and alkaline earth metal and ammonium salts of fatty acids, and hydroxypolyesters, and combinations thereof. 52. The crayon of any of claims 39-51, said composition includes a colorant in an amount of from about 1% by weight to about 15% by weight of the composition. 53. The crayon of any of claims 39-52, which includes a filler. 54. The crayon of claim 53, wherein said filler is selected from the group consisting of calcium carbonate, talc, nylon modified talc, titanium dioxide, silica, clay, feldspar, cornstarch, mica, and combinations thereof. 55. The crayon of any of claims 39-54, which includes a gelling agent. 56. The crayon of claim 55, wherein said gelling agent comprises a polyamide resin. 57. The crayon of claim 56 or 57, wherein said gelling agent is an ester terminated polyamide resin. 58. The crayon of any of claims 39-57, which is substantially free of glitter. 59. The crayon of claim 22, which provides an increased color delivery. 60. The crayon of claim 22, which provides an increased wear rate.

Inventors: CRAIG MICHAEL S, CRAIG, MICHAEL, S.
Applicants: BINNEY & SMITH INC, CRAIG MICHAEL S, BINNEY & SMITH INCORPORATED, CRAIG, MICHAEL, S.
Application year: 1999
Main classification: C09D11
IPC codes: C09D11, C09D13