MULTILAYER PLASTIC ARTICLES

Abstract: Multilayer plastic composite articles comprising a thermoplastic resin substrate which can be a polycarbonate, an ABS or ASA resin, a polyphenylene ether or polyphenylene ether/polystyrene blend, a polyester or an admixture of polycarbonate with ABS, ASA or polyester and at least one surface layer comprising a cycloaliphatic polyester or cycloaliphatic polyester blend which is adherent to at least one surface of the substrate. Decorative layers can be located between the substrate and the surface layers.

Description: 1 MULTILAYER PLASTIC ARTICLES FIELD OF THE INVENTION This invention is directed to multilayer plastic articles, their properties and methods for making such articles. More particularly the articles comprise a substrate or base layer of an injection molded, blow molded or extruded thermoplastic and a top and/or bottom layer of acycloaliphatic polyester. BACKGROUND OF THE INVENTION There is subst-antial commercial interest in the use of plastic materials in various product forms such as sheet, film, shaped products, thermoformed articles, packaging, and architectural products. Many different plastics are used for such products in order to take advantage of particular physical, chemical, and mechanical properties. SUMMARY OF THE INVENTION Thermoplastic resins are provided with a surface film which improves weatherability, and solvent resistance, and which can be used to modify the color .and appearance of the thermoplastic material. The surface film comprises a thin film of a cycloaliphatic polyester which is applied to the thermoplastic substrate by lamination, coextrusion or by an in-mold process known in the art as "in-mold decoration" in which the surface film is placed in the mold and the thermoplastic melt, which forms the substrate or base layer, is injection molded to the exposed surface or surfaces of the film. The substrate or base layer can be any suitable thermoplastic resin including polycarbonates; polyesters; acrylonitrile-butadiene-styrene resins, referred to as ABS resins; acrylonitrile-styrene-acrylate resins , referred to as ASA resins, a polyphenylene ether or polyphenylene ether /polystyrene blend and blends comprising polycarbonate in a mixture with one or more ABS, ASA or polyester resins In one embodiment of the invention a cycloaliphatic polyester layer can be laminated or adhered to both sides, i.e., top and bottom of the injection molded substrate, thereby making a three layer structure in which the substrate is protected on both sides by the same or different cycloaliphatic polyester layers. Various intermediate layers can be applied for decorative or functional purposes, or the cycloaliphatic polyester resin itself can be colored or modified to be the decorative layer. The structures of this invention can be transparent, opaque, or non- transparent, or combinations of transparent and opaque layers as desired. Transparent products are a preferred embodiments of this invention. The composite multilayered structure or article can be stabilized by inclusion of ultra violet or infrared absorbing additives. The invention provides articles comprising a theπnoplastic substrate or base, preferably a polycarbonate resin or polycarbonate blend with other resins, and at least one surface layer comprised of a cycloaliphatic polyester or a blend of polycarbonate and cycloaliphatic polyester. The substrate can have a surface layers on both sides. The base and surface layers can be provided with compatible .functional additives. DETAILED DESCRIPTION Polycarbonates (PC) for use in the production of the multilayered articles of the invention are thermoplastic, aromatic polymers .and include homopolycarbonates, copolycarbonates and copolyestercarbonates and mixtures thereof which have average molecular weights of about 8,000 to more than 200,000, preferably of about 20,000 to 80,000 and an intrinsic viscosity (IN.) of 0.40 to 1.5 dl/g as measured in methylene chloride at 25° C. In one embodiment, the polycarbonates are derived from dihydric phenols, or bisphenols, .and carbonate precursors. Polycarbonates are a well known class of high impact resistant thermoplastic resins characterized by optical clarity and high ductility. One of the most important engineering thermoplastics in use today are the polycarbonates. Polycarbonates can be defined as polymers containing recurring carbonate groups (-0-CO-0-) in the main chain. Aromatic polycarbonates are of particular interest in the practice of this invention. These polymers are known per se and are generally prepared by reacting a dihydric phenol, or bisphenol, with a carbonate precursor, e.g., phosgene, a halogen formate, or a carbonate ester. Aromatic polycarbonates comprise multiple structural units represented by the formula: [-O-Al-O-C(O)-] Formula 1 wherein A^ is a divalent aromatic hydrocarbon radical. Suitable aromatic hydrocarbon radicals for inclusion as A^ include m-phenylene, p-phenylene, 4,4'-biphenylene, 4,4'-bi(3,5-dimethyl)-phenylene, 2,2-bis(4-phenylene)propane and similar radicals such as those which correspond to the dihydroxy- substituted aromatic hydrocarbons disclosed by name or formula in U.S. Patent 4,217,438. The Al radical preferably has the formula: -A2-Y-A3- Foπnula 2 wherein each of A^ and A^ is a mono cyclic divalent aromatic hydrocarbon radical and Y is a bridging hydrocarbon radical in which one or two atoms separate A^ from A^. The free valence bonds in formula 2 are usually in the meta or para positions of A^ and A^ in relation to Y. Compounds in which A has formula 1 are bisphenols, and for the sake of brevity the term "bisphenol" is sometimes used herein to designate the dihydroxy-substiruted aromatic hydrocarbons; it should be understood, however, that non-bisphenol compounds of this type may also be employed as appropriate. In formula 2, the A^ and A^ values may be unsubstituted phenylene or hydrocarbon-substituted derivatives thereof, illustrative substituents (one or more) being alkyl and alkenyl. Unsubstituted phenylene radicals are preferred. Both A^ and A^ are preferably p-phenylene, although both may be o- or m- phenylene or one o- or m-phenylene and the other p-phenylene. The bridging radical, Y, is one in which one or two atoms, preferably one, separate A^ from A^. Illustrative radicals of this type are methylene, cyclohexylmethylene, . 2-[2.2J]-bicycloheptylmethylene, ethylene, isopropylidene, neopentylidene, cyclohexylidene, cyclopentadecylidene, cydododecylidene and adamantylidene; gem-alkylene (alkylidene) radicals are preferred. .Also induded, however, are unsaturated radicals. For reasons of availability and particular suitability for the purposes of this invention, the preferred bisphenol is 2,2-bis(4-hydroxyphenyl)propane ("bisphenol A"), in which Y is isopropylidene and A^ and A^ are each p-phenylene. Cycloaliphatic polyesters suitable for use in the present invention are those which are characterized by optical transparency, improved weatherablity compared to the substrate alone, chemical resistance, and low water absorption. The cycloaliphatic polyester layers also have good melt compatibility with the substrate resins allowing easy recycling of the multilayer structures by simply re- melting the multilayer article and reforming one of the layers as a combination of the substrate layer and the cycloaliphatic cap layer. Other cap layers, for instance chlorinated polyolefins may react on re-melting causing degradation of the substrate resin particularly if the substrate resin is a high melting condensation polymer like polycarbonate. This compatibility of the cap layer and the substrate of the multilayered articles of this invention allows recycling of scrap during manufacture or simple recovery of the resins after the useful lifetime of the artide. This is espedally benefidal in articles containing polycarbonate or polycarbonate blends. Cydoaliphatic polyesters useful in the practice of the invention are prepared by reaction of a diol with a dibasic acid or derivative. The diols useful in the preparation of the cycloaliphatic polyester resins for use as the surface films of the present invention are straight chain, branched, or cydoaliphatic, preferably straight chain or branched alkane diols, and may contain from 2 to 12 carbon atoms. Examples indude, but are not limited to, ethylene glycol, propylene glycol, i.e., 1,2- and 1,3-propylene glycol, butane diol, i.e., 1,3- and 1,4-butane diol, diethylene glycol, 2,2-dimethyl-l,3-propane diol, 2- ethyl, 2-methyl, 1,3-propane diol, 1,3- and 1,5-pentane diol, dipropylene glycol, 2- methyl-l,5-pentane diol, 1,6-hexane diol, 1,4-cydohexane dimethanol and particularly its ds- and trans-isomers, triethylene glycol, 1,10-decane diol, and mixtures of any of the foregoing. Particularly preferred is dimethanol bicyclo octane, dimethanol decalin, a cycloaliphatic diol or chemical equivalent thereof and particularly 1,4-cyclohexane dimethanol or its diemical equivalents are to be used as the diol component, it is preferred that a mixture of ds- to trans-isomer thereof, ranging from 1:4 to 4:1, and preferably, a ratio of about 1:3 is used. Chemical equivalents to the diols include esters, such as dialkylesters, diaryl esters, and the like. The diadds useful in the preparation of the cycloaliphatic polyester resins of the present invention are aliphatic diadds. This is meant to include carboxylic adds having two carboxyl groups each of which is attached to a saturated carbon in a saturated ring. A preferred diadd is 1,4-cydohexanedicarboxylic add and most preferred is trans-l,4-cyclohexanedicarboxylic add as tether explained above. Other cycloaliphatic adds include decahydro naphthalene dicarboxylic add, norbornene dicarboxylic adds, bicyclo octane dicarboxylic adds. Linear aliphatic diadds are also useful provided the polyester has at least one monomer containing a cycloaliphatic ring. Illustrative examples of linear aliphatic diadds are succinic add, adipic add, dimethyl succinic add, and azelaic add. Mixtures of diadd and diols may also be used to make the cycloaliphatic polyesters of the invention. Cydohexanedicarboxylic adds and their diemical equivalents can be prepared, for example, by the hydrogenation of cydoaromatic diadds and corresponding derivatives such as isophthalic add, terephthalic add of naphthalenic add in a suitable solvent, water or acetic add at room temperature and at atmospheric pressure using suitable catalysts such as rhodium supported on a suitable carrier of carbon or alumina. See, Friefelder et al., Journal of Organic Chemistry, 31, 34-38 (1966); U.S. Patent Nos. 2,675,390 and 4,754,064. They may also be prepared by the use of an inert liquid medium in which a add is at least partially soluble under reaction conditions and a catalyst of palladium or ruthenium in carbon or silica. See, U.S. Patent Nos. 2,888,484 and 3,444,237. Typically, during hydrogenation, two or more isomers are obtained in which the carboxylic add groups are in cis- or trans-positions. The ds- and trans- isomers can be separated by crystallization with or without a solvent, for example, n-heptane, or by distillation. The cis-isomer tends to. blend better; however, the trans-isomer has higher melting .and crystallization temperatures and is espedally preferred. Mixtures of the ds- and trans-isomers are useful herein as well, and preferably when such a mixture is used, the trans-isomer will comprise at least about 75 parts by weight and the ds-isomer will comprise the remainder based upon 100 parts by weight of cis- and trans-isomers combined. When a mixture of isomers or more than one diadd is used, a copolyester or a mixture of two polyesters may be used as the cycloaliphatic polyester resin in the present invention. Chemical equivalents of these diadds indude esters, alkyl esters, e.g., dialkyl esters, diaryl esters, anhydrides, add chlorides, add bromides, and the like. The preferred chemical equivalents comprise the dialkyl esters of the cycloaliphatic diadds, and the most preferred chemical equivalent comprise the dimethyl ester of the add, particularly dimethyl- trans-1, 4- cydohexanedicarboxylate. Dimethyl-l,4-cydohexanedicarboxylate can be obtained by ling hydrogenation of dimethylterephthalate, and two isomers having the carboxylic add groups in the ds- .and trans-positions are obtained. The isomers can be separated, the trans-isomer being especially preferred. Mixtures of the isomers are suitable as explained above and preferably in the ratios as explained above. The polyester resins of the present invention are typically obtained through the condensation or ester interchange polymerization of the diol or diol equivalent component with the diacid or diadd diemical equivalent component and having recurring units of the Formula 3: 0 O O-R 13 — O-C-R 14 — C- Formula 3 wherein R 13 represents an alkyl or cycloalkyl radical containing 2 to 12 carbon atoms and which is the residue of a straight chain, branched, or cycloaliphatic alkane diol having 2 to 12 carbon atoms or chemical equivalents thereof; and R 14 is an alkyl or a cycloaliphatic radical which is the decarboxylated residue derived from a diadd, with the proviso that at least one of R 13 or R 14 is a cycloalkyl group. A preferred cycloaliphatic polyester is poly(l,4-cydohexane-dimethanol- 1,4-cydohexanedicarboxylate) (PCCD) having recurring units of formula 4: CH . -^^-CH 2 -0-C— ζ^ — c— - Formula 4 wherein R 13 is a cydohexane ring, and wherein R 14 is a cydohexane ring derived from cydohexanedicarboxylate or a chemical equivalent thereof and is selected from the ds- or trans-isomer or a mixture of cis- and trans-isomers thereof. Cydoaliphatic polyester resins of the instant invention can be generally made following the teachings of, for example, U.S. Patent 2,465,319. The reaction is generally run in the presence of a suitable catalyst such as a tetra(2-ethyl hexyl)titanate, in a suitable amount, typically about 50 to 400 ppm of titanium based upon the final product. Poly(l,4-cyclohexanedimethanol-l / 4-cyclohexanedicarboxylate), herein abbreviated as PCCD, film shows excellent adhesion to polycarbonate resin substrates, induding polycarbonate blends with other thermoplastics, without using a primer. BPA polycarbonates are preferred substrate resins for use in this invention. Films comprising blends of PCCD and polycarbonates also be used as the cap layers of this invention. They exhibit excellent primerless adhesion to a polycarbonate substrate when the film is bonded to the polycarbonate by lamination, hot pressing, in mold decoration, melt extrusion of the polycarbonate on to a PCCD film, coextrusion of both resins, or any similar bonding or joining technique known to those in the art. An In mold decoration process is described in "Modem Plastics " Feb. 1998, p34. The cap layer of the invention may also comprise a blend of polycarbonate resin with cydoaliphatic polyester resin. Addition of the PC resin to the cycloaliphatic polyester allows retention of clarity and increases the heat distortion temperature (HDT) of the cap layer allowing it be used in a wider range of artides. PC addition to the cycloaliphatic cap layer resin may also benefidally alter its melt strength and crystallization behavior. A preferred embodiment provides a blend of cydoaliphatic polyester resin, and cydoaliphatic polyesters with increased stiffness containing rigid segments such as adamantane, neopentyl or norbornene segments. A preferred embodiment provides a composition wherein the polycarbonate is bisphenol-A polycarbonate, the cydoaliphatic polyester resin is derived from a cydoaliphatic diol and a cycloaliphatic diadd. The preferred cydoaliphatic resin being poly (l,4-cydohexanedimethanol-l,4- cydohexanedicarboxylate) (PCCD), and further, wherein the ratio of the polycarbonate to PCCD is from about 60:40 to about 75:25. Blends of polymers such as polycarbonate and cydoaliphatic polyesters generally contain catalyst quenchers. Catalyst quenchers are agents which inhibit activity of any catalysts which may be present in the resins. Catalyst quenchers 10 are described in detail in U.S. Patent 5,441,997. It is critical to chose the correct quencher to avoid color formation and loss of clarity in the cap layer when it consists of a cycloaliphatic polyester blended with PC resin. A preferred class of quenchers are those which provide a transparent and colorless product. Typically, such stabilizers are used at a level of 0.001-10 weight percent and preferably at a level of from 0.005-2 weight percent. The preferred stabilizers indude an effective amount of an acidic phosphate salt; an add, alkyl, aryl or mixed phosphite having at least one acidic hydrogen; a Group IB or Group IIB metal phosphate salt; a phosphorus oxo add, a metal add pyrophosphate or a mixture thereof. The suitability of a particular compound for use as a stabilizer and the determination of how much is to be used as a stabilizer may be readily determined by preparing a mixture of the polyester resin component, and polycarbonate resin with and without the particular compound and determining the effect on melt viscosity, gas generation, color or the formation of interpolymer. The addic phosphate salts indude sodium dihydrogen phosphate, mono zinc phosphate, potassium hydrogen phosphate, caldum dihydrogen phosphate and the like. The phosphites may be of the formula: RiO- OR2 OR3 where R 1 , R 2 and R 3 are independently selected from the group consisting of hydrogen, alkyl and aryl with the proviso that at least one of R 1 , R 2 and R 3 is hydrogen. The phosphate salts of a Group IB or Group IIB metals of the periodic table indude zinc phosphate, copper phosphate and the like. The phosphorus 11 oxo adds indude phosphorous add, phosphoric add, polyphosphoric add or hypophosphorous add. The polyacid pyrophosphates may be of the formula: M Z χ H y P n 0 3n+ ι wherein M is a metal, x is a number ranging from 1 to 12 and y is a number ranging 1 to 12, n is a number from 2 to 10, z is a number from 1 to 5 and the sum of (xz) + y is equal to n + 2. The preferred M is an alkaline or alkaline earth metal. The most preferred quenchers are oxo adds of phosphorous or addic organo phosphorus compounds. Inorganic addic phosphorus compounds may also be used as quenchers, however they may result in haze or loss of darity. Most preferred quendiers are phosphoric or phosphorous add. CydoaHphatic polyester resins have been found to have better weatherability than polycarbonate alone. Ultraviolet light absorbers are used to improve the polycarbonate light stability. Indusion of a light stabilizer in a cydoaliphatic polyester layer on the polycarbonate surface has been found to provide additional light stability for the polycarbonate resin. The ultraviolet light absorbers (UNA) useful in the present invention are those which are generally compatible with polycarbonates. Preferred are benzotriazole, benzophenone, triazine, cyanoacrylate, dibenzoylresordnol, and oxanilide based UNA Incorporation of a light stabilizing additive in the PCCD composition, i.e., cydoaliphatic polyester alone or a polycarbonate - cydoaliphatic polyester blend, provides additional benefits in weatherability. h addition to UN absorbers, hindered amine light stabilizers (HALS) also contribute to increased weatherability of the structure. 12 Illustrative ultraviolet radiation absorbing compounds indude 2- (benzotriazol-2-yl)-4-(lJ,3,3-tetramethylbutyl)phenol, 2-(benzotriazol-2-yl)-4- methylphenol, 2-hydroxy-4-octyloxy benzophenone, 2-hydroxy-4- methoxybenzophenone, ethyl-2,2-diphenyl-l-cyanoacrylate, 2'-ethylhexyl - 2, 2- diphenyl-1-cyanoacrylate, 2-(2'-hydroxy-4'-octyloxy) bis-4,6-(2',4'- dimethylphenyl) triazine, 2-ethyl- 2'- ethoxy oxalanide, bis [ 2-hydroxy-5-methyl- 3- (benzotriazol-2-yl) phenyl ] - methane, bis[ 2 - hydroxy- 5 -t - octyl -3 - ( benzotriazol -2 -yl) phenyl] methane, 2,2' - ( 1,4 - phenylene ) bis [ 4 H - 3, 1 - benzoxazin -4 - one], and 2 - ( 2' - hydroxy-4-hexyloxy) - 4,6 - diphenyltriazine. Light stabilizers are incorporated in the cycloaliphatic polyester e.g., PCCD, resin in amounts of about 0.05 to about 10 weight percent. Blends comprising polycarbonate and cydoaliphatic polyester components form one class of resin compositions which can be used to form the multilayer artides of this invention. Sud blends generally contain various additives such as colorants , light stabilizers, ultraviolet absorbers, and the like, in addition to quenchers. In preferred examples, the polycarbonate and the cydoaliphatic polyester resin, taken together, comprise (a) from about 70% to about 99.94% by weight of the total composition, the ratio of the polycarbonate to the cydoaliphatic polyester resin being from about 50:50 to about 90:10; (b) the benzotriazole, benzophenone, triazine, cyanoacrylate, dibenzoylresordnol, and oxanilide based UN absorber comprises from about 0.05% to about 10% by weight of the total composition; and (c) the catalyst quencher comprises from about 0.001% to about 3% by weight of the total composition. Other preferred embodiments of the instant invention provide a composition wherein the benzotriazole, benzophenone, triazine, cyanoacrylate, dibenzoylresordnol, and oxanilide based UNA comprises from about 0.3% to about 10% by weight of the total composition of the film layer. Another preferred embodiment provides a composition wherein the benzotriazole, 13 benzophenone, triazine, cyanoacrylate, dibenzoylresordnol, and oxanilide based UNA comprises from about 0.3% to about 1% by weight of the total composition. .Hindered amine light stabilizers, which are well known in the art, may optionally be added at 0.01 to about 1% of the total composition. In another embodiment of the invention the support layer or substrate comprises an ABS type polymer or an ABS -PC blend. In general, ABS type polymers contain two or more polymeric parts of different compositions which are bonded chemically. The polymer is preferably prepared by polymerizing a conjugated diene, such as butadiene or a conjugated diene with a monomer copolymerizable therewith, such as styrene, to provide a polymeric backbone. After formation of the backbone, at least one grafting monomer, and preferably two, are polymerized in the presence of the prepolymerized backbone to obtain the graft polymer. These resins are prepared by methods well known in the art. Related ASA resins (Acrylonifrile-Styrene-Acrylate ) are made in a similar fashion in some cases by grafting acrylonitrile, styrene and an optionally an alkyl acrylate to an acrylic rubber. ASA may also be blended with polycarbonate to form a substrate resin. In ABS the backbone polymer, as mentioned, is preferably a conjugated diene polymer such as polybutadiene, polyisoprene, or a copolymer, such as butadiene-styrene, butadiene-aαylonitrile, or the like. Examples of dienes that may be used are butadiene, isoprene, 1,3-heptadiene, methyl-l,3-pentadiene, 2,3- dimethyl-l,3-butadiene, 2-ethyl-l,3-pentadiene; 1,3- and 2,4-hexadienes, chloro and bromo substituted butadienes such as dichlorobutadiene, bromobutadiene, dibromobutadiene, mixtures thereof, and the like. A preferred conjugated diene is butadiene. One monomer or group of monomers that may be polymerized in the presence of the prepolymerized backbone are monovinylaromatic hydrocarbons. SUBSTITUTE SHEET (KULH. O) 14 Examples of the monovinylaromatic compounds and alkyl-, cydoalkyl-, aryl-, alkaryl-, aralkyl-, alkoxy-, aryloxy-, and other substituted vinylaromatic compounds include styrene, 3-methylstyrene; 3,5-diethylstyrene, 4-n- propylstyrene, alpha-methylstyrene, alpha-methyl vinyltoluene, alpha- chlorostyrene, alpha-bromostyrene, did lorostyrene, dibromostyrene, tetra- dilorostyrene, mixtures thereof, and the like. The preferred monovinylaromatic hydrocarbons used are styrene and alpha -methylstyrene. A second group of monomers that may be polymerized in the presence of the prepolymerized backbone are acrylic monomers such as acrylonitrile, substituted acrylonitrile and /or acrylic acid esters, exemplified by acrylonitrile, and alkyl acrylates such as methyl methacrylate. Examples of such monomers indude acrylonitrile, ethacrylonitrile, methacrylonitrile, alpha chloroacrylonitrile, beta -chloroacryloni.trile, alpha -bromoaαrylonitrile, and beta -bromoacrylonitrile, methyl acrylate, methyl methacrylate, ethyl acrylate, butyl acrylate, propyl acrylate, isopropyl acrylate, and mixtures thereof. The preferred acrylic monomer is acrylonitrile and the preferred acrylic add esters are ethyl acrylate and methyl methacrylate. In the preparation of the graft polymer, the conjugated diolefin polymer or copolymer exemplified by a 1,3-butadiene polymer or copolymer comprises about 50% by weight of the total graft polymer composition. The monomers polymerized in the presence of the backbone, exemplified by styrene and acrylonitrile, comprise from about 40 to about 95% by weight of the total graft polymer composition. The second group of grafting monomers, exemplified by acrylonitrile, ethyl acrylate or methyl methacrylate, of the graft polymer composition, preferably comprise from about 10% to about 40% by weight of the total graft copolymer composition. The monovinylaromatic hydrocarbon exemplified bv 15 styrene comprise from about 30 to about 70% by weight of the total graft polymer composition. In preparing the polymer, it is normal to have a certain percentage of the polymerizing monomers that are grafted on the backbone combine with each other and occur as free copolymer. If styrene is utilized as one of the grafting monomers and acrylonitrile as the second grafting monomer, a certain portion of the composition will copolymerize as free styrene-acrylonitrile copolymer. In the case where alpha -methylstyrene (or other monomer) is substituted for the styrene in the composition used in preparing the graft polymer, a certain percentage of the composition may be an alpha -methylstyrene-acrylonitrile copolymer. Also, there are occasions where a copolymer, such as alpha - methylstyrene-acrylonitrile, is added to the graft polymer copolymer blend. When the graft as polymer-copolymer blend is referred to herein, it is meant optionally to include at least one copolymer blended with the graft polymer composition and which may contain up to 90% of free copolymer. Optionally, the elastomeric backbone may be an acrylate rubber, such as one based on n-butyl acrylate, ethylacrylate, 2-ethylhexylacrylate, and the like. Additionally, minor amounts of a diene may be copolymerized in the acrylate rubber backbone to yield improved grafting with the matrix polymer. The preferred ABS material for the support layer is Cycolac® resin available from the GE Plastics component of General Electric Company. Additional material for the support layer indude polycarbonate and ABS blends. The polycarbonate and ABS, respectively, are as before described with Lexan® resin and Cycolac® resin being available from GE Plastics component of General Electric Company. The ABS/polycarbonate resin is also available from GE Plastics as Cycoloy® resin. Suitable blends contain about 15 to about 85 16 weight percent polycarbonate and about 15 to about 85 weight percent ABS resin. Other preferred substrate layers are polyester components indude crystalline polyesters such as polyesters derived from aliphatic or cydoaliphatic diols, or mixtures thereof, containing from 2 to about 12 carbon atoms and at least one aromatic dicarboxylic acid. Preferred polyesters are derived from an aliphatic diol and an aromatic dicarboxylic acid having repeating units of the following general formula: O O O (CH 2 )— O C Ar — C wherein n is an integer of from 2 to 6. Ar is a C6-C20 aryl radical comprising a decarboxylated residue derived from an aromatic dicarboxylic add. Examples of aromatic dicarboxylic adds represented by the decarboxylated residue Ar are isophthalic or terephthalic add, l,2-di(p- carboxyphenyl)ethane, 4,4'-dicarboxydiphenyl ether, 4,4' bisbenzoic add and mixtures thereof. All of these adds contain at least one aromatic nudeus. Adds containing .fused rings can also be present, such as in 1,4- 1,5- or 2,6- naphthalene dicarboxylic adds. The preferred dicarboxylic adds are terephthalic add, isophthalic add, naphthalene dicarboxylic acid or mixtures thereof. The most preferred polyesters are poly(ethylene terephthalate) (PET), and poly(butylene terephthalate) (PBT), poly(ethylene naphthanoate) (PEN), poly(butylene naphthanoate) (PBN), poly(propylene terephthalate) (PPT), or mixtures of these resins. .Also contemplated herein are the above polyesters with minor amounts, e.g., from about 0.5 to about 15 percent by weight, of units derived from aliphatic 17 adds and/or aliphatic polyols to form copolyesters. The aliphatic polyols indude glycols, such as poly(ethylene glycol) or poly(butylene glycol). Such polyesters can be made following the teachings of, for example, U.S. Pat. Nos. 2,465,319 and 3,047,539. The preferred poly(l,4-butylene terephthalate) resin used in this invention is one obtained by polymerizing a glycol component at least 70 mol %, preferably at least 80 mol %, of which consists of tetramethylene glycol and an add component at least 70 mol %, preferably at least 80 mol %, of which consists of terephthalic acid, and polyester-forming derivatives therefore. The polyesters used herein have an intrinsic viscosity of from about 0.4 to about 2.0 dl/gm. measured in a 60:40 phenol /tetrachloroethane mixture or similar solvent at 23-30° C. VALOX ®315 polyester is particularly suitable for this invention. Preferably intrinsic viscosity is about 1.1 to about 1.4 dl/gm. Blends of polyesters may also be employed in the composition. Preferred polyesters blends contain poly(ethylene terephthalate) and poly(l,4-butylene terephthalate). When blends of these preferred components are employed the polyester resin component can comprise from about 5 to about 50 parts by weight poly(ethylene terephthalate) and from about 95 to about 50 part by weight poly(l,4-butylene terephthalate) based on 100 parts by weight of both components combined. Also, blends of relatively low molecular weight polybutylene terephthalate resin may be used with a relatively high molecular weight polybutylene terephthalate as set forth in U.S. patent 5,589,530 to Walsh. The low molecular weight polybutylene terephthalate is a PBT resin having a melt viscosity of less than 600 poise at 250°C. 18 The aromatic polyesters are the reaction products of aliphatic diols and aromatic dicarboxylic adds, or their derivatives. Preferred diols are C2-C12 diols; espedally preferred are ethylene glycol, propylene glycol and butylene glycol. Preferred dicarboxylic acid are derived from benzene or naphthalene rings. Most preferred diadds are iso and tere phthalic add or naphthalene dicarboxylic acid, especially the 2, 6 naphthalene dicarboxylate. Blends of polycarbonate with polyesters are also preferred substrates. As indicated earlier, the preferred polycarbonate is bisphenol-A polycarbonate. When blends of these preferred components are employed the polyester resin component can comprise from about 1 to about 99 parts by weight polyester and from about 99 to about 1 part by weight polycarbonate based on 100 parts by weight of both components combined. These materials espedally when further blended with rubbery impact modifiers provide resins with excellent impact and stiffness. The preferred polycarbonate resins are as described previously with BPA-PC being most preferred. Impact modifiers espedally suitable for optional indusion in the aromatic polyester polycarbonate blends are core shell modifiers such and MBS (methacrylate-butadiene-styrene)copolymers and methylmethaαrylate-butyl acrylate (acrylic rubber) core shell rubbers as well as acrylonitrile styrene graft polybutadiene rubbers (ABS rubber). Thermoplastic resins comprising a blend of polycarbonate and polyesters resin are available from General Electric Company Plastics Division under the trademark Xenoy®. Artides of the invention may also use polyphenylene ether and polyphenylene ether /polystyrene blends as the substrate. The polyphenylene either resins can be homopolymers or copolymers and are preferably derived from the polymerization of alkyl or aryl substituted phenols, 2,6 xylenol and 19 2,3,6 trimethyl phenol are espedally preferred. The polystyrene resins used in blends with the polyphenylene ethers can be alkyl, aryl or halogen substituted. They may further be modified with rubber especially butadiene based rubber. Most preferred are polystyrene, alpha-methyl polystyrene, para-methyl polystyrene and high impact modified polystyrene known as HIPS. Polyphenylene ether polystyrene blends are sold by GE Plastics under the Noryl® trade name. The composite article comprising a base or substrate of a thermoplastic resin such as a polycarbonate, polyester, or an ABS resin or a polycarbonate resin blend and an adherent layer of cycloaliphatic polyester film is preferably, optically transparent and has improved weather resistance when compared to the substrate, e.g., polycarbonate, surface alone. In addition to a transparency of greater than 87%, the polycarbonate cycloaliphatic polyester composite is characterized by other properties such as good impact strength, low water absorption, chemical resistance to methanol, ethyl acetate, and MEK, low shrinkage, good prbcessability, printability, and cutability. The substrate resin may also contain other additives such as colorants, flame retardant chemicals, glass fibers, mineral fillers such as talc, day, barium sulfate, mica, glass spheres as well as thermal stabilizers , lubricants and other processing aids. In a preferred method for forming the multilayer articles of this invention a surface layer is formed by coextruding polycarbonate and cydoaliphatic as a composite film. The substrate is then injected onto the polycarbonate side of the composite during a subsequent molding operation. The resulting multilayer artide comprises a substrate (in this case PC), an intermediate film of the same material as the substrate, e.g., polycarbonate, and a top layer of a cydoaliphatic polyester, sudi as PCCD. The composite film can be any suitable and convenient 20 thickness. For example the polycarbonate film can be about 10 mils thick and the PCCD film can be about 5 mils thick, the substrate can be thicker. Any ink or decorative layer can be printed on the surface of the laminated polycarbonate or cycloaliphatic polyester film. The articles of the invention can be formed by various processes: for instance; compression molding, multilayer blow molding, coextrusion of sheet or film, injection over molding, insertion blow molding and other methods. The multilayer articles of the invention can have a variety of uses in business equipment, hand held communication devices, pagers, telephones, automobiles in applications such as body panels , interior and exterior trim and bumpers. The articles can also be used , glazing, membrane switches, packaging, building and construction. The following examples are presented to illustrate the invention and should not be construed to limit the scope of the invention. Example 1. A blend of 60% PCCD and 40 % PC film 13-15 mil thick was prepared with 0.05% [45%] aqueous phosphorous acid. The extrusion conditions are listed in Table 1. Table 1. Example of Extrusion Conditions for PC /PCCD Blend Extruder Diameter 2 in. Drying Temperature (°F) 200 Drying Time (Hours) 6 Moisture Content (%) <0.020 Extruder Temperatures (°F) Set/Actual Zone 1 440/441 Zone 2 460/462 Zone 3 470/473 21 Zone 4 485/486 Zone 5 485/486 Pipes and Clamps Temperature (°F) 480/477 Melt Temperature (°F) 487 Pressure (psi) 1450 Screw RPM 30 Extruder Amps 18 Line Speed (fps) 8J Die Lips (F) 480 Roll Stack Temp (°F) 170/171 Feed Block Adapter Temperature (°F) 480/481 The resulting 13-15 mil film was optically transparent with good appearance. Example 2: A 10 mil optically transparent 100 % PCCD film was also prepared. Prior to extrusion the PCCD resin was dried at 200°F for 4-5 hours. The dry resin was then put into a 1.25" diameter single stage screw extruder with barrel settings set between 425°F and 450°F. The L/D ratio was 24 andthesαrew had a compression ratio of 3.5, the screw speed was 55 RPMs and power was at 27 amps on a line moving at a rate of 7.2 fpm. Short residence times were desirable to avoid thermal degradation. The resulting film was optically transparent. In Mold Decorating: The PCCD film sample from the prior example was treated with Teflon tape on both sides for the first one inch along the width of a 4" x 6" film. The film was then placed into the mold of an injection molding machine. Lexan 140 grade polycarbonate resin was then injected into the mold to form a layered composite of PC resin and PCCD film. The experimental conditions for the Nissei 160 ton press injection molder are shown in Table 2. Table 2. Experimental Conditions for In Mold Decorating PCCD Film 22 Injection Molding Conditions: Barrel set Temps: Nozzle 585° F Front 585° F Middle 585° F Rear 525° F Tool set Temps: Moveable 175° F/Fixed 175° F Times: Inject 10 sec. Cool 22 sec. Cycle 1 sec. .Injection Velodty -4.5 in. /sec (ram) (75%) Hold Pressure 30% Mach. Cap. (625 psi) Velodty to Pressure Switch Point 10 mm Shot Size 42 mm Cushion 9 mm Screw Speed 80 rpm Screw decompression 1 mm Screw Back Pressure 0 Adhesion Testing: Once the layered structure was made the adhesion could be tested. A one inch wide adhesion test sample was cut from the plaque and mounted in a screw driven model 6025 Instron running Acquilin software. The Teflon PTFE flap provided a flap wliich. could be easily grasped by the Instron whidi was used to perform 90 degree peel tests. The rate of peel was 0.0067 in/sec. The adhesion test showed that the PCCD to PC adhesion was greater than 22 lb. /in., before the film failed by breaking. In addition, upon viewing the film under magnification a dean interface is observed which would indicate low distortion upon printing .and thermoforming. Tear Strength: 23 The tear strength of a 10 mil 100 % PCCD film was tested along with a PC film and a PC/PCCD blend all of the same thickness. It was found that the PCCD film showed a better tear strength of 69 g/mil than did PC film which had a tear strength of 42 g/mil. A blend of 90% PC and 10% PCCD film was also tested and found to have an intermediate tear strength of 48 g/mil. A 15 mil multilayer artide of PCCD coextruded over PC also showed good tear resistance in practical tests. Heat Deflection Temperature (HDT) Since PCCD has a low heat deflection temperature of 125° F for a 10 mil film, it is shown that it can be blended with higher heat resistant materials to improve its HDT. Table 3. Shows PCCD being blended with polycarbonate resin to reach heat deflection temperatures of 250F with only 50 weight percent polycarbonate. Table 3. The-HI-π , ofrcCD<^beImprovedwithSmaflAmσu Run PCCD PC HDT # (wt%) (wt%) (°F) 1 100 0 125 2 0 100 250 3 90 10 150 4 70 30 180 5 50 50 250 Oxygen (T0__) Barrier Performance: The amount of PCCD in the PCCD /PC blend formulation can be used to control the rate of oxygen fransmittance through the film, while maintaining overall darity and diemical resistance. Table 4. Shows the relative performance of PC film, PCCD film and a 90/10 PC/PCCD film to oxygen fransmittance rates. 24 Table 4. Oxygen Transmittance Rates of .PCCD, PC and Blend Films Film material T0 2 (73 F) cc O2 * mil/100 in 2 /day PC 219 PCCD 147 90/10 PC/PCCD 145 Example 3: .Ink Adhesion / Diecutability A 60 PCCD/ 40 PC blend film was screen printed with a black ink made by Nazdar Company (Black, 9624). No adhesion promoters or treatments were used. The print adhesion was then tested by a Crosshatch adhesion test (ASTM D3559) and was found to have a 5B rating. The diecutting process involves stamping out the film into the shape of the mold. Failure is marked by hairline cracks along the edges or slivers of polymer along the cut surface, often referred to as 'angel hair' by those skilled in the art. The film printed and cut according to acceptable standards. Example 4. An ABS resin (Cycolac ® GPM5500) and an ABS/PC (Cycoloy ® C6200) blend made by the General Electric Company was used to in mold decorate a 60 % PCCD with 40 % 130 grade PC blend film (60/40 PCCD/PC). The 60/40 PCCD/PC film was thermoformed and diecut to fit within a three dimensional mold. In mold decorated samples were prepared with each the Cycolac GPM5500 and the Cycoloy C6200 resins. The resulting parts were laminated parts containing the 60/40 PCCD/PC film on one side. The final parts had an 25 acceptable aesthetic appearance. The conditions for in mold decorating the film are shown in table 5, below. Table 5. In Mold Decorating Conditions for Cycolac ABS and Cycoloy ABS/PC Resins Cycolac GPM Cycoloy C6200 5500 Barrel set Temps: Nozzle 465° F 585° F Front 455° F 585° F Middle 450° F 585° F Rear 440° F 525° F Tool set Moveable 175°F Temps: Fixed 175° F Times: First 2.81 sec 2.85 sec. Injection Second 1.02 sec. 1.02 sec. Injection Cure 16 sec 16 sec. Mold Open 4 sec 4 sec. Total Cycle 41 sec 41 sec. I .njection 1.2 in. /sec 1.2 in. /sec Velodty Pressure, psi " First 1700 2000 Injection Second 200 200 Injection Back 75 75 Clamp 200 200 Shot Size 1.65 1.80 Extruder 150 rpm 150 rpm Rate 26 The samples were tested to determine the adhesion between the base resin and the film using a one-inch strip cut from the laminate and an Instron. A 90 degree adhesion peel test showed that the Cycolac GPM 5500 resin with the 60/40 PCCD/PC film had an average adhesion of 1.2 lb/in while the Cycoloy C6200 had an average adhesion of 11.2 lb/in. Example 5. A 50% Polycarbonate (PC)/50% PCCD film blend and a 100 % PCCD film both containing benzotriazole stabilizer, Cyasorb UV 5411® as a UV light absorber (UNA) were prepared. The UNA was thoroughly mixed into the resin pellet with 0.05% phosphorous add quencher and extruded under the conditions listed in table 6. Table 6. Composition and Extrusion Conditions for Making PCCD Film and 50/50 PC/PCCD Film Resin Composition PCCD Film: PCCD (pellets) 99.0 pbw 2247.3 g Cyasorb 5411. 1.00 pbw 22.7 g Phosphorous acid 0.05 pbw 1.14 g Extruder conditions PCCD Film: Resin dried at 90C >4 lir. Temperature sets: Rear 400F Middle 440F Front 440F Nozzle 450F Melt-Temp. 446F Other Conditions: Motor amps - 3.0 Roll stack 145F RPM's 75 Feeder speed 5.0 Roll speed 5.0 27 Die press. 0-500psi Sheet Die 450F Film thickness -0.005" Resin Composition PC/PCCD Film: PC-135 (pellets) 49.48 pbw 1123.1 g PCCD (pellets) 49.48 pbw 1123.1 g Cyasorb 5411 1.00 pbw 22.7 g Phosphorous acid 0.05 pbw 1J4 g Extruder conditions: Resin dried at 100C >4 hr. Temperature sets: Rear 450F Middle 470F Front 470F Nozzle 500F Melt-Temp. 496F Other Conditions: Motor amps - 3.0 Roll stack 175F RPM's 75 Feeder speed 3.0 Roll speed 5.0 Die press. 0-500ρsi Sheet Die 470F Film thickness -0.005" .After the .films were prepared the thickness, tτansmitt.ance, YI, and haze were measured The results are shown in the table below. The transmittance, YI and haze were measure using a Gardner Colorimeter in the fransmittance mode. 28 Table 7. Film Thickness, Transmittance, YI and Haze of the PCCD and 50/50 PC/PCCD films prepared. Tansmittance YI % Haze Thickness (mil) PCCD Film 92.1 3.1 0.8 8.8 PC/PCCD Film 91.4 2.0 6.2 8.3 These film samples were then in mold decorated with Lexan® 125 Resin (PC), Xenoy ® 1102 Resin (46/40/14 PC /Polybutylene terephthalate /MBS blend, Noryl PX1005® resin ( a polystyrene (PS) modified polyphenylene oxide (PPO)blend )) and Nalox 315® resin (PBT) to make 4" x 6" x 0.0625" plaques. A Nissei 160 ton press under the conditions shown in table 8 was used to make these samples. Table 8. Conditions for In Mold Decorating Films with a Nissei 160 tons Injection Molding Machine. Resin Barrel Set Temperatures Tool Temperature PBT (unpigmented) Nozzle- 490 F 170 F/170 F Front- 490 F Middle- 490 F Rear- 490 F PC/PBT/MBS (Black) Nozzle- 500 F 150 F/150 F Front- 500 F Middle- 500 F Rear- 475 F PPO/PS (Black) Nozzle- 540 F 160 F/ 160 F Front- 540 F Middle- 540 F Rear- 525 F PC (Clear, unstabilized) Nozzle- 555 F 170 F/ 170 F Front- 555 F Middle- 555 F Rear- 525 F 29 The laminate samples produced from this experiment were tested for chemical resistance, interlayer part adhesion and weatherability. Chemical Resistance The laminated plaque was tested for chemical resistance using a 50% Ethyl Acetate/50% Methanol mixture. The test was performed by placing a saturated piece of filter paper approximately 1" in diameter on the plaque (film side). The sample was then covered with a watch glass to prevent evaporation. After 5, 15, 30, 45 and 60 minutes the samples were checked for failure i.e. blistering or cracking. The table below shows the results of each laminated plaques performance. Table 9. Results of Chemical Resistance Testing using a 50% Ethyl Acetate/50% Methanol Mixture Controls: Material Chemical Resistance PC Failed @ 5 min. PPO/PS Discolored @ 5 min PC/PBT/MBS Some Pitting @ 30 minutes PBT Pass @ 30 & 60 min Laminated Samples 100% PCCD Film with UNA over: PC Pass @ 30 & 60 min PPO/PS Pass @ 30 & 60 min PC/PBT/MBS Pass @ 30 & 60 min PBT Pass @ 30 & 60 min 50/50 PC/PCCD Film with UNA over: PC Pass @ 30 & 60 min (some discoloration) PPO/PS Pass @ 30 & 60 min PC/PBT/MBS Pass @ 30 & 60 min 30 (some discoloration) PBT Pass ® 30 & 60 min Interlayer Adhesion Tests An Instron 90 degree adhesion peel test was utilized to test the adhesion between the film and the injection molding resin. .An area of the plaque was masked before in mold decorating to provide a tab to grab for the adhesion tests. One inch sfrips were cut from the center of each plaque. The samples was then mounted in the Insfron and pulled apart at a rate of 0.016" per sec. The adhesion was reported in pounds per linear inch. The following table shows the results of these adhesion tests. Table 10. Results of 90 Degree Adhesion Tests Average Maximum Adhesion Adhesion 100% PCCD Film with UNA (lb/in) (lb/in) over: PC* 3.76 13.75 PPO/PS 0.35 1.00 PC/PBT/MBS* 7.30 32.63 PBT 0.76 1.62 50/50 PC/PCCD Film with UNA over: PC* 3.87 22.49 PPO/PS 0.40 1.46 PC/PBT/MBS* 18.11 35.90 PBT 0.51 1.29 * Last reported measurement before sample broke 31 Weatherability The xenon arc accelerated testing was performed on a Ci35a xenon arc Weather-ometer ® using a modified SAE J1960 protocol. The modification consisting of using a type S borosilicate filter as the inner and outer filters. The irradiance level was 0.77 W/m 2 at 340 nm, the black panel temperature was between 70-73° C, the dry bulb temperature was 45° C with a wet bulb depression of 10° C (50% relative humidity). The cyde was 160 min. light, 5 minutes dark, 15 minutes dark with water spray. This cyde accumulates 2.46 KJ/m 2 at 340 nm per hour of operation. Samples were exposed to 598.5 KJ/m 2 under these conditions. The yellowness index (YI), haze and transmittance measurements were taken using a Gardner XL-835 colorimeter. Gloss measurements were also collected at a 60 degree angle on the irradiante/ cycloaliphatic polyester side as per ASTM D523. The results of these tests are shown in table 11. Table 11. Weathering Results of Prepared Samples after 589.5 KJ/m2 Exposure in Xenon Arc Sample Initial Gloss 598.5 KJ/m2 % Gloss Retention Gloss PC/PBT/MBS Control 98.5 0.9 less than 1% with PCCD laminate 92.2 99.7 100% with PC/PCCD laminate 94.3 96.9 100% PBT Control 105.9 68.0 64% with PCCD laminate 88.0 91.0 100% with PC/PCCD laminate 104.5 95.2 91.1% PPO/PS Control 99.4 0.1 less than 1% with PCCD laminate 89.3 89.8 100% with PC/PCCD laminate 93.5 96.9 100% 32 Change in YI (Final - Initial) PC Control 6.8 with PCCD laminate 4.3 with PC/PCCD laminate 3.6 Example 6. A sheet was coexfruded having a 70 wt. % PCCD/30 wt. % 130 grade PC blend cap layer and a 100% 100 grade PC substrate. The cap layer was 0.005 in. thick and the PC substrate was 0.095 in. thick. The resulting sheet was fransparent and colorless. The layers showed excellent adhesion, good toughness and solvent resistance. Table 12. Coextrusion Conditions for 70/30 PCCD/PC Cap Layer Over 100 % PC Substrate. Main Extruder: Diameter 1.25" L/D 24 Barrel Temp (F) 470-490 Residence Time (min) 3-6 Satellite Extruder: Diameter 1.00" L/D 30 Barrel Temp (F) 360 Residence Time (min) 15-20 Line Speed (fpm) 1.4 .In a preferred embodiment of the invention a thin .film of top layer material such as PCCD is coexfruded with a thicker substrate material such as PC. The bottom of the polycarbonate layer is imprinted with an ink image. The decorative two layer composite is then placed in a mold and a layer of substrate 33 material, in this case, the PC is injection molded to the printed side of what is now the layer of a four layer structure.

Claims: 34 WHAT IS CLAIMED IS: 1. A multilayer article whidi comprises a thermoplastic resin substrate layer and an adherent layer comprising a cycloaliphatic polyester on at least one surface of the substrate. 2. A multilayer article which comprises a substrate comprising a thermoplastic resin layer and an adherent layer comprising a cydoaliphatic polyester on at least one surface of the substrate wherein the cydoaliphatic polyester surface layer shows a 60 degree gloss change of less than or equal to 50% after 600 KJ/m2 exposure to a J1960 weathering test using borosilicate glass filtered xenon arc light. 3. A multilayer article which comprises a substrate comprising a thermoplastic resin layer and an adherent layer comprising a cydoaliphatic polyester on at least one surface of the substrate wherein the peel strength between the layers is greater than or equal to 5 lbs/in. A multilayer artide whidi comprises a substrate comprising a thermoplastic resin layer and an adherent layer comprising a cydoaliphatic polyester on at least one surface of the substrate where in the cydoaliphatic polyester surface of the artide resists cracking or blistering after 60 minutes exposure to a 1:1 mixture of ethyl acetate and methanol. 5. An artide according to claim 1 in which the thermoplastic resin substrate layer is a polycarbonate resin, an ABS resin, an ASA resin, a polyester, a polyphenylene ether or polyphenylene ether/polystyrene blend, or a blend comprising a polycarbonate resin with an ABS, ASA or aromatic polyester resin. 6. An article according to claim 5 in whidi the substrate layer is polycarbonate or a polycarbonate containing blend. 35 7. An article according to claim 6 in which the substrate layer blend comprises from about 15 to about 85 weight percent polycarbonate and from about 15 to about 85 weight percent ABS, ASA or polyester resin. 8. An article according to claim 1 in which the substrate layer further contains 1-50% of the cycloaliphatic polyester cap layer. 9. .An article according to claim 1 where the adherent cap layer is a blend of polycarbonate with cycloaliphatic polyester. 10. An article according to claim 1 in which the adherent cap layer is a blend of polycarbonate and cycloaliphatic polyester derived from a cydoaliphatic diol and a cydoaliphatic diacid. 11. An article according to claim 1 in which the cydoaliphatic polyester is poly(l,4 - cydohexane dimethanol - 1,4 cydohexanedicarboxylate) 12. An article according to claim 9 in which the amount of polycarbonate in the polycarbonate - cycloaliphatic poly ester blend of the adherent cap layer is from about 1 to about 50 percent by weight of the blend. 13. An artide according to claim 9 which further comprises an addic phosphorus quendier, 14. An artide according to claim 13 wherein the addic phosphorus quencher is chosen form the following group: phosphorous add, phosphoric add, addic organo phosphates, and acidic organo phosphites. 36 15. .An article of claim 1 wherein the substrate layer is a polycarbonate or a blend of polycarbonate with ABS, ASA or a polyester resin. 16. An article according to claim 9 in which the blend comprises polycarbonate, a cycloaliphatic polyester, and a UN absorber. 17. An article according to claim 16 in which the UN absorber is selected from the group consisting of 2-(benzotriazol-2-yl)-4-(l,l,3,3- tetramethylbutyl)phenol, 2-(benzofriazol-2-yl)-4-methylphenol, 2-hydroxy-4- octyloxy benzophenone, 2-hydroxy-4-methoxybenzophenone, ethyl-2,2- diphenyl-1-cyanoacrylate, 2'-ethylhexyl - 2, 2-diphenyl-l-cyanoacrylate, 2-(2'- hydroxy-4'-octyloxy) bis-4,6-(2',4'-dimethylphenyl) triazine, 2-ethyl- 2'- ethoxy oxalanide, bis [ 2-hydroxy-5-methyl-3- (benzofriazol-2-yl) phenyl ] - methane, bis[ 2 - hydroxy- 5 -t - octyl -3 - ( benzofriazol -2 -yl) phenyl] methane, 2,2' - ( 1,4 - phenylene ) bis [ 4 H - 3, 1 - benzoxazin -4 -one], and 2 - ( 2' - hydroxy) - 4,6 - diphenyltriazine. 18. An artide according to claim 16 in which the UV absorber is a benzotriazole, a benzophenone, a triazine, a cyanoacrylate, a dibenzoylresordnol, or an oxanilide. 19. An artide according to claim 16 in which the UV absorber is a dibenzoylresordnol. 20. An artide according to daim 19 in whidi the dibenzoyl rescorcinol is 4,6-dibenzoylresorcinol, bis(2,6-dihydroxy-3,5- dibenzoylphenyl)methane, or 2-(3-triethoxysilyl propyl)-4,6-dibenzoyl resorcinol. 37 21. A multilayer plastic artide according to daim 1 comprising an intermediate decorative layer between the substrate and the cycloaliphatic polyester layer. An article according to claim 21 in which the intermediate layer is printed on at least a portion of the inner surface of the cycloaliphatic polyester layer. 23. An article according to claim 1 comprising an thermoplastics resin, a first film of the same resin bonded to at least one surface of the substrate, and a second film comprising a cycloaliphatic polyester bonded to the outer surface of the first film. 24. An artide according to daim 23 comprising a polycarbonate substrate, a polycarbonate film bonded to at least one surface of the substrate, a cycloaliphatic polyester surface film bonded to the outer surface of the polycarbonate film. 25. An artide according to claim 24 in which the surface film is a blend of polycarbonate and a cydoaliphatic polyester. 26. An artide according to claim 25 in which the cydoaliphatic polyester is PCCD. 27. An artide of daim 5 wherein the polycarbonate -aromatic polyester substrate further contains a rubbery impad modifier. 28. An article of daim 27 wherein the rubbery substrate is chosen from the group consisting of MBS, Acrylic rubber, ASA or ABS rubbers. 29. .An .artide of daim 1 made by a blow molding, sheet , .film or profile extrusion, in mold decoration or injection molding_process. 38 30. An article of claim 29, made by coextruding the substrate layer material and the top layer material, decorating the bottom surface of the substrate layer, and injection or blow molding another layer of substrate material to the decorative surface of the substrate. 31. A multilayer artide comprising a substrate comprising a thermoplastic resin layer and an adherent layer comprising a cydoaliphatic polyester on at least one surface of the substrate wherein the polyester layer has a tear strength of 69 grams /mil.

Inventors: AYERS CECIL EDWARD, GILLETTE GREGORY RONALD, HOEFFLIN FRANK A, LEGRAND DONALD GEORGE, LILLY KENNETH, MACGREGOR AMY KATHLEEN, PICKETT JAMES EDWARD, SEEGER GEORGE THOMAS, AYERS, CECIL, EDWARD, GILLETTE, GREGORY, RONALD, HOEFFLIN, FRANK, A., LEGRAND, DONALD, GEORGE, LILLY, KENNETH, MACGREGOR, AMY, KATHLEEN, PICKETT, JAMES, EDWARD, SEEGER, GEORGE, THOMAS
Applicants: GEN ELECTRIC, GENERAL ELECTRIC COMPANY
Application year: 1999
Main classification: B32B27
IPC codes: B32B27