STABILIZED AQUEOUS PHENOLIC BINDER FOR MINERAL WOOL AND PRODUCTION OF MINERAL WOOL PRODUCTS

Abstract: A stabilized aqueous phenolic binder for mineral wool comprising an emulsified phenolic resin consisting essentially of a phenolic resin having a degree of conversion of phenol of 99 % or more, said binder containing a protective colloidal agent in a concentration of less than 0.1 % by weight based on the solid content of the binder. A method of producing an emulsifiable phenolic resin; an emulsifiable phenolic resin obtainable by the method; a method of producing a stabilized phenolic binder for mineral wool; a stabilized phenolic binder obtainable by the method; use of said binder in production of mineral wool products; methods of producing mineral wool products; and mineral wool products obtainable by the methods.

Description: STABILIZED AQUEOUS PHENOLIC BINDER FOR MINERAL WOOL AND PRODUCTION OF MINERAL WOOL PRODUCTS DESCRIPTION 1. BACKGROUND OF THE INVENTION The present invention relates to a stabilized aqueous phenolic binder for mineral wool; a method of producing an emulsifiable phenolic resin; an emulsifiable phenolic resin obtainable by the method; a method of producing a stabilized phenolic binder for mineral wool; a stabilized phenolic binder obtainable by the method; use of said binder in production of mineral wool products; methods of producing mineral wool products; and mineral wool products obtainable by the methods. The Technical Field It is known that phenolic resins and binders may contain low-reacted and unreacted reactants, e.g. phenol and formaldehyde, which evaporate during the making of the mineral wool and cause pollution problems and reduced efficiency and performance of the binder in various bonding applications. Accordingly, it is desired that the resin is as free as possible from any unconverted starting materials or residues thereof while its useful qualities are preserved. Methods to achieve this include reacting e.g. phenol with excess of e.g. formaldehyde in presence of an alkaline catalyst to ensure a low content of free phenol and then reacting the excess formaldehyde with an aldehyde scavenger e.g. a nitrogen-containing compound such as urea, melamin or ammonia. Addition of ammonia further stabilizes the phenolic resin and prevents it from separating into two liquid phases or precipitating out in a solid or crystal phase. Such solid or crystal phases are difficult to dissolve later. Furthermore, the amount of ammonia helps to stabilize the solution in order to achieve a better water dilutability when the resin is to be used in a binder. Any excess of ammonia, however, causes an undesired emission of ammonia during the application of the binder and the curing such a binder. Thus, there is a need for a stabilized phenolic binder for mineral wool which does not exhibit this drawback. Prior Art Disclosures WO 96/26 164 discloses a phenolic binder comprising phenol, formaldehyde, a sugar compound, and ammonia for mineral wool products for which emission of ammonia is lowered by adding the sugar compound before addition of ammonia. US 5 371 140 discloses a stable emulsifiable phenolic resin and a binder for mineral wool products exemplified to have 0.01% by weight of free phenol and 0.6% by weight of formaldehyde. The emulsifying agent is a proteinaceous material such as casein and soya protein in an amount about 0.25% to about 10% by weight. Other emulsifiers include gum arabic, guar gum, Karaya gum, ammonium alginate, polyvinyl alcohol, polyvinyl acetate and carboxylated methylcellulose. Also, combinations of gum arabic and polysaccharides consisting essentially of mannose and galactose units, or D-mannuronic and L- guluronic acid units may be used. The emulsifier prevents crystallisation and makes it possible to store the resin before use. Nothing is indicated or suggested about how to provide a low ammonia emission when curing such binders, nor about use of such emulsifying agents in amounts less than 0.1% by weight. On the contrary, it is stated that below 0.1% by weight, the phenolic resin system loses its water emulsifiability. US 4 060 504 discloses use of casein as an emulsifier in concentrations from 1 to 12% by weight. JP 7 268 181 discloses a phenolic resin composition comprising a casein emulsifier, for use for the impregnation and reinforcement of paper- or cloth-based materials, or as a binder for glass fibre and wood chips. Casein may be present in concentrations from 0.1 to 5% by weight together with an anionic surfactant which ensures a stable solution. Shay et al . , A new class of alkali-swellable association thickeners", JOCCA, Nov. 1993, Journal of the Oil & Color Chemists' Association, discloses so-called HEURASE thickeners combining the chemistries of both alkali- swellable emulsions (ASE) and hydrophobic modified ethoxylate urethanes (HEUR) thickeners. HEURASE thickeners provided under the trade mark Polyphobe® by Union Carbide are known as rheological modifiers in paints but have not been used in binders for mineral wool . DE 2 330 852 discloses water dilutable aqueous emulsion- and protective colloid-containing dispersions of phenolic resin comprising non-ionic emulsifiers and protective colloids, such as poly vinyl alcohol, added after the formation of the emulsion to protect it, and use thereof e.g. as a binder for mineral wool plates. 2. DISCLOSURE OF THE INVENTION Object of the Invention It is an object of the present invention to provide an aqueous phenolic binder for mineral wool which during the making of the mineral wool exhibits a low emission of polluting low molecular weight compounds such as free phenol and free ammonia. It is another object to provide a phenolic resin for a binder that is stable for transportation and storage for a suitable period of time. It is still another object to provide an aqueous phenolic binder for the production of mineral wool products which exhibits a low amount of free phenol and free ammonia, and which exhibits a high binding capacity and ensures a good product quality of the mineral wool products. It is a further object of the present invention to provide an aqueous binder which can be used in the normal processes of applying binders in the production of mineral wool products, and which results in a reduced need of cleaning process equipment. A stabilized phenolic binder In an aspect of the invention, these objects are fulfilled by providing a stabilized aqueous phenolic binder for mineral wool comprising an emulsified phenolic resin consisting essentially of a phenolic resin having a degree of conversion of phenol of 99% or more, said binder containing a protective colloidal agent in a concentration of less than 0.1% by weight based on the solid content of the binder. It surprisingly turns out that a stabilized aqueous phenolic binder for mineral wool according to the invention, comprising an emulsified phenolic resin having a degree of conversion of phenol of about 99% or more, i.e. a phenolic resin of relatively high molecular weight, can be obtained with a low content of unreacted components, e.g. phenol and formaldehyde, and that the emulsified phenolic resin can be stabilized for a sufficient time for transportation and storage thereof for use in the normal production of mineral wool products; said effects being obtained by adding to the binder a protective colloidal agent, in a concentration of less than 0.1% and preferably between 0.1% and 0.005% by weight based on the solid content of the binder. This method of stabilizing the emulsified phenolic resin only requires addition of a small amount of ammonia, beyond the amount to be added to react with excess formaldehyde, and therefore, the emission of ammonia can be lowered or even avoided. Also, since the amount of protective colloidal agent is less than 0.1% by weight, good product properties are obtained. Furthermore the use of only a small amount of protective colloidal agent is an economical advantage. In a preferred embodiment, the content of free phenol is below 0.5% by weight. Protective colloidal agents are such compounds that are able to surround wholly or partly phenolic resin droplets but which do not invade the internal phase thereof. In a preferred embodiment, the protective colloidal agent is a polymeric emulsifier and/or a copolymeric emulsifier containing at least one of the groups acryl and urethane. In another preferred embodiment, the protective colloidal agent is a polymeric emulsifier and/or a copolymeric emulsifier selected from the group consisting of: a) polymers including: polyethylene compounds; poly (vinyl acetate); poly (vinyl alcohol); polycarboxylic acid, such as polyacrylate; polysulfonic acids, such as poly (styrenesulfonic acid) ; polyesters, such as glycol polyacrylate; polyamids, such as polyacrylamide; polyurethanes, such as polyurethane elastomers containing ionic groups, such as -COO " , S0 3 " , and quaternary ammonium, and polyurethanes elastomers containing nonionic hydrophilic groups; polyvinylpyrrolidone; poly (ethylene oxide); polymeric cationic compounds, and mixtures thereof; and b) copolymers including: styrene copolymers, such as styrene-acrylate polymers and styrene-ethylene oxide polymers; copolymers of polyvinyl and maleic acid compounds, such as styrene-maleic anhydride polymers and vinyl acetate- aleic acid ester polymers; polyvinyl-polyalkylene copolymers, such as vinylacetate- ethylene polymers, ethylene-acrylic acid-acrylic acid ester polymers, and ethylene acrylic acid-acrylonitril polymers; other vinyl copolymers such as vinyl acetate polymers, acrylic acid- acrylonitrile polymers, acrylic acid- acrylamide polymers, and butadiene-acrylonitril polymers; acrylonitrile-butadiene-styrene polymers (ABS polymers) ; and mixtures thereof; and mixtures of said polymers (a) and copolymers (b) In a particularly preferred embodiment, the protective colloidal agent is an addition terpolymer consisting of a carboxylic functional monomer X, a relative water- insoluble monomer Y, and a urethane functional associative monomer Z having the formula -[X]-[Y]-[Z]- wherein I X = -CH 2 -C(R)-CO-0 " ,NH 4 + wherein R is H, methyl or ethyl, Y = -CHz-CfR^-CO-O-R 2 wherein R 1 is H, methyl or ethyl, and R 2 is methyl, ethyl, propyl or butyl, and Z = -CH 2 -C ( R 3 ) -C 6 H 4 -C ( CH 3 ) 2 -NH-CO-0-R n 4 -C6H 4 -R 5 wherein R 3 is H, methyl or ethyl, R 4 is a C 2 -C 4 oxylalkylene group and R 5 a is C 5 -Cι 5 group and n is 6- 150, preferably 40-60 and more preferably 50. Within the groups of Z the internal alkoxy group as well as the whole group can be repeated. In a preferred embodiment, the protective colloidal agent is a modified ethoxalate urethane, such as Polyphobe®. Examples of such agents available under the trade mark Polyphobe ® are preferably Polyphobe® 102, 103, and TR117 supplied by Union Carbide Corporation. In another preferred embodiment, the protective colloidal agent is a natural emulsifier selected from the group consisting of: lanolin; lecithins, albumines and cholesterols, sυch as egg yolk; waxes, such as bees wax; lignosulfonates, cellulose and cellulose derivatives, such as cellulose ethers; proteins, such as casein, whey protein or gelarin; polysaccharides such as starch, dextrin and pectin; types of rubber, such as natural rubber latex, gum arabic, mastics, tragacanth and guar gum; mucilages from algea and lichen (alginates), such as carregheenan, agar-agar; saponins; and locust bean flower; and mixtures thereof. The concentration of the protective colloidal agent is chosen in any suitable amount providing sufficient stability of the emulsified phenolic binder and which amount does not impair its binding properties. In a preferred embodiment the concentration of the protective colloidal agent is between 0.05 and 0.02% by weight whereby suitable stabilities and binding properties are obtained. In a binder according to the invention, the phenolic resin may consist of any suitable phenolic components. In a preferred embodiment, the phenolic resin consists essentially of the reaction product of phenol and aldehyde in a phenol to aldehyde molar ratio of less than 1:1. Generally, in the binder according to the invention, the concentration of the preferred phenol and aldehyde is adjusted to a suitable level depending on the application. In a preferred embodiment, the molar ratio of phenol to aldehyde is in the range of 1:2 to 1:6, preferably 1:3 to 1:4.5. The content of solids depends on the particular application. In a preferred embodiment, the content of solids is 15 to 60% by weight, preferably 20 to 45% by- weight of the resin. The pH of the binder depends on the application. In an aspect, the pH is chosen so as to avoid separation of the emulsified phenolic resin. In a preferred embodiment, the pH is larger than 7 and most preferred in the range of 8 to 10. Emulsifiable phenolic resins according to the invention ordinarily have a higher molecular weight than the state of the art phenolic resins, such known resins normally having a degree of conversion of phenol less than 99% and typically often a water dilutability larger than 5.5. In an preferred embodiment the degree of conversion of phenol is equal to or above 99.4%. Preferably equal to or above 99.6%. Generally, the water dilutability of the phenolic resin is less than or equal to 5. In a preferred embodiment, it is in the range of 0.5 to 5, preferably in the range of 1 to 4, particularly 2 to 4. Suitable phenolic resins can be prepared by methods known in the art, such methods comprising reacting phenolic components, e.g. phenol with excess of formaldehyde, in the presence of an effective amount of alkaline catalyst for a sufficient reaction time and at a suitable temperature to provide a water dilutability of less than or equal to 5; said preparation optionally being further modified by an additional reaction with urea, melamin and/or dicyandiamide; see e.g. DK-A-4982/88, EP-A- 0148050, and US 5 371 140 the contents of which relating to the preparation of phenolic resins are incorporated herein by reference. Suitable phenols of the phenolic resin according to the invention include (see US 5 371 140) ortho-, para- directing hydroxy or amino aromatic compounds having 6 to 24 carbon atoms such as phenol itself (C 6 H 5 OH) , naphthol, anthranol and substituted derivatives thereof. The substituents on the aromatic compound are independently selected from hydrogen; halogen, such as CI, Br, and F; NH 2 ; and hydrocarbon radicals, such as: (a) alkyl groups or radicals of 1 to 12 carbon atoms, preferably of 1 to 9 carbon atoms, and their various isomeric forms and substituted on the aromatic nucleus in the ortho- and para- position; (b) cycloalkyl groups of 5 to 12 carbon atoms such as cyclohexyl, cyclopentyl, methylcyclohexyl, butylcyclo- hexyl, and so forth; (c) aryl ketonic groups wherein the hydrocarbon portion is as defined below in (e) ; (d) alkyl, aryl and cycloalkyl carboxylic groups wherein the hydrocarbon portion is defined as above in (a) and (b); (e) aryl groups of 6 to 24 carbon atoms such as phenyl, naphthyl, anthryl, and the like; (f) aryl substituted alkyl wherein the aryl is phenyl which may contain lower alkyl and/or hydroxy substituents so that the resulting hydroxy aromatic is, for example, a bisphenol; (g) the oxyhydrocarbon radicals corresponding to the foregoing hydrocarbon radicals; and (h) mixtures of the aforesaid hydroxy aromatics, Suitable substituted phenols include meta-cresol, m- propyl phenol, m-isobutyl phenol, m-sec-butyl phenol, m- tert-butyl phenol, m-bromo phenol, m-chlorc phenol, m- phenyl phenol, m-benzyl phenol, m-cetyl phenol, m-cumyl phenol, m-hydroxyacetophenone, m-hydroxybenzophenone, m- d-limonene phenol. The corresponding phenols substituted in the ortho- and para-positions can be used in part but are not preferred. Mixtures of various hydroxy aromatic compounds mentioned herein also may be used. Included among the phenolic reactants which may be used are those known as the "cresylic acids" and these often comprise heterogeneous mixtures having two reacting hydrogen positions on each of them; that is, compounds unsubstituted in the ortho- and para-positions, and hence, yield relatively unreactive resins. These compounds may include the following: 3, 5-xylenoI, m- cresol, 3,4-xylenol, 2,5-xylenol, 2,3-xylenol, phenol, p- cresol, o-cresol, 2,4-xylenol, and 2,6-xylenol. Cresylic acids or tar acids may include phenol and its homologs which may include cresols, xylenols, trimethyl phenols, ethyl phenols, and higher boiling materials such as dihydroxy phenols, polycyclic phenols and the like. They are often obtained by a low-temperature trimerization of coal, lignite, and the like, or a conventional high- temperature coke oven tar, or the liquid product of petroleum cracking both thermo and catalytic, shell oil, coal hydrogenation products, and the like. Polyhydroxyaromatic reactants, such as resorcinol, may also be used. Also useful in this invention are mixtures of aniline and phenol to react with an aldehyde or ketone to produce a resole. Additionally, sodium lignosulfonate may also be substituted for a portion of the phenol. Suitable aldehydes of the phenolic resin according to the invention include (see US 5 371 140) formaldehyde and any of its variations, such as higher concentrations of formalin, such as 30 percent or higher concentrations of formalin, or paraldehyde, acetaldehyde, propionaldehyde, isobutyraldehyde, isopentaldehyde, and the like. The aldehyde should have not more than 8 carbon atoms and should not detrimentally affect the resinification of the resin. Preferred aldehydes are those having from 1 to 4 carbon atoms, such as formaldehyde, which may be in aqueous solution (e.g. 30 percent or higher), or in any of its low polymeric forms such as paraformaldehyde or trioxane. Other aldehydes include para-aldehydes, furfuraldehyde, 2-ethylhexanal, ethylbutyraldehyde, heptaldehyde, benzaldehyde and crotonaldehyde . Glyoxal may also be used. These other aldehydes and mixtures thereof may be used in place of formaldehyde or in partial substitution thereof; but preferably, formaldehyde in one of its commercially available forms is used. A method of producing an emulsifiable phenolic resin In an aspect of the invention, the objects of the invention are fulfilled by providing a method of producing an emulsifiable phenolic resin as defined in claim 1, said method comprising the steps as claimed in claim 14. It has surprisingly turned out that by reacting the phenolic component, e.g. phenol with formaldehyde, in the presence of an effective amount of alkaline catalyst for a sufficient reaction time and at a suitable temperature to provide a degree of conversion of phenol of 99% or more, a high molecular weight phenolic resin can be produced which upon curing exhibits a low emission of polluting compounds such as free phenol and free ammonia, and which upon addition of 0.1% by weight of a protective colloidal agent can be stabilized for a sufficient time for the phenolic resin to be kept in solution without separation and without loosing its binding capacity before its use. Preferred embodiments are claimed in claims 15 and 16. In a preferred embodiment, ammonia is added in an amount of 60 to 120 1 per 1000 kg dry solids, whereby it is ensured that the tendency to separate or form solids or crystals in the resin during storage is reduced, and thereby improving the stability of the formed resin. An emulsifiable phenolic resin obtainable by the method In another aspect according to the invention the objects of the invention are fulfilled by providing an emulsifiable phenolic resin obtainable by the method as claimed in claim 17. A method of producing a stabilized phenolic binder In still another aspect according to the invention the objects of the invention are fulfilled by providing a method of producing a stabilized aqueous phenolic binder for mineral wool as claimed in claim 18. Preferred embodiments are claimed in claims 19, 20 and 21. A stabilized phenolic binder obtainable by the method In still another aspect according to the invention the objects of the invention are fulfilled by providing a stabilized aqueous phenolic binder obtainable by the method as claimed in claim 22. Use of a stabilized phenolic binder for mineral wool In still another aspect according to the invention the objects of the invention are fulfilled by providing use of a stabilized phenolic binder for mineral wool in the production of a mineral wool product as claimed in claim 23. A method of producing a mineral wool product In still another aspect according to the invention the objects of the invention are fulfilled by providing a method of producing a mineral wool product as claimed in claims 24-25 and 28. A mineral wool product obtainable by the method In still another aspect according to the invention the objects of the invention are fulfilled by providing a mineral wool product obtainable by the method as claimed in claim 26. 3. DETAILED DESCRIPTION Degree of conversion During the condensation process of the phenolic components samples are taken out in order to measure the content of free phenol. The amount of free phenol is measured by gas chromatography. From these data the degree of conversion is calculated. Water dilutability tests A 5 ml sample of the reaction mixture of phenol and aldehyde is slowly added deionised water to a permanent haze develops in the reaction mixture-water mixture. The volume of added water divided by five is taken as a measure of the water dilutability. Mineral wool product Generally the mineral wool product is consolidated as a slab, sheet or other shaped article. Products according to the invention may be formulated for any of the conventional purposes of MMV fibres, for instance as slabs, sheets, tubes or other shaped products that are to serve as thermal insulation, fire insulation and protection or noise reduction and regulation, or in appropriate shapes for use as horticultural growing media. 4. EXAMPLES The invention is further illustrated in examples. Example A - Production of a stabilized phenolic resin" In a 1.5 liters double-sided reactor vessel mounted with reflux, thermometer, agitator and inlets was supplied 94 g (1 mol) 60 °C warm phenol, and then 278 g 20 °C formalin having a formaldehyde content of 37% , i.e. corresponding to a formaldehyde-phenol ratio of 3.43:1. At a temperature of about 35 °C of the mixture, 3.7 g Ca(OH) 2 was added. Then the temperature was increased up to about 80 °C. Following about 10 to 20 minutes the temperature increased to about 84 to 86 °C caused by exothermal reactions. After about 85 minutes from addition of the catalyst, samples were taken for the determination of the degree of conversion of the phenol. After reaching a degree of conversion of 99.4 %, 60 g of urea was added and the reaction mixture was cooled to about 60 °C and the solution was kept at 60 °C for 30 minutes and hereafter cooled to 35 °C with a cooling rate of 0, 5 °/minute. After cooling the urea-containing solution, 11 g 25% ammonia solution was added. The process was stopped by precipitating the alkaline catalyst by addition of ammonium bi-carbonate . 0.019 g corresponding to 0,01 g Polyphobe® based on solid was added to form an emulsifiable stabilized resin. Test of stability of the resin Example A was repeated with various amounts of casein and Polyphobe® (see the following Table 1). The products obtained showed very good stability for amounts of less than about 0.10% of protective colloidal agent based on solid content. Various amounts of alkaline catalyst were tested, all showing very good stability. Examples were carried out with different amounts of urea all showing very good stability. Table 1 * The stability is satisfactory, if the emulsions are stable for at least 20 min. Test of phenol and ammonia emission from binders full scale test Resin binders with protective colloids were prepared as described in example A by stopping the condensation reaction at a degree of conversion at 99.4%. Water was added to the resin in order to form a binder. The binders were prepared in a 5 m 3 reactor equipped with a jacket, stirrer and reflux. Emission of phenol and ammonia from production of mineral wool were determined by collecting samples in the exhaust gas and measuring the samples by gas chromatography and ion chromatography. The results of average emissions are shown in Table 2. It can be concluded that extension of the reaction time in the production of the phenolic resin followed by stabilisation of the phenolic resin of the larger molecular weight by addition of protective colloidal agent according to the invention simultaneously reduces the emissions of both phenol and ammonia. Table 2 Binder strength test - laboratory test Standard bars of 25 x 10 x 150 mm were prepared of 3% by solid weight of resin as described in example A. Water was added to the resin in order to form a binder. The binder, silane and mineral wool fiber shots were mixed (i.e. mineral wool residues in form of e.g. beads) and cured. Results of tensile strengths on standard bars under dry and humid conditions are shown in Table 3. Table 3 Example B - Production of mineral wool products full scale test Test of product quality Stone wool products with a density of 150 kg/m 3 and containing 3.5% by weight of standard binder including silane or silane-containing binder according to the invention were tested for delamination strength, both for fresh and aged products, i.e. products subjected to 15 minutes in 100% humidity at 121 °C and 1 ato. Results of delamination strength (kPa) are shown in Table 4. The binders with protective colloids were prepared as described in example A. The binders without protective colloids were prepared as described in example A but the reaction of the phenol was stopped at a degree of conversion of 98.4% phenol and no protective colloids were added. Also the amount of ammonia added was increased from 11 g to 59 g in order to achieve sufficient stability of the binder. Table 4 It appears from table 4 that the addition of protective colloidal agent for achieving a suitable stabilisation of the binder lowers the delamination strength of the tested products compared to products containing no protective colloids . However, when the protective colloidal agent is added in an amount of less than 0.1% by weight the reduction of the delamination strength is insignificant.

Claims: CLAIMS 1. A stabilized aqueous phenolic binder for mineral wool comprising an emulsified phenolic resin consisting essentially of a phenolic resin having a degree of conversion of phenol of 99% or more, said binder containing a protective colloidal agent in a concentration of less than 0.1% and preferably between 0.1% and 0.005% by weight based on the solid content of the binder. 2. A binder according to claim 1, wherein the phenolic resin has a water dilutability of less than or equal to 5. 3. A binder according to claims 1 or 2, wherein the protective colloidal agent is a polymeric emulsifier and/or a copolymeric emulsifier containing at least one of the groups acryl and urethane. 4. A binder according to any one of claims 1-3, wherein the protective colloidal agent is a polymeric emulsifier and/or a copolymeric emulsifier selected from the group consisting of: a) polymers including: polyethylene compounds; poly (vinyl acetate); poly (vinyl alcohol); polycarboxylic acid, such as polyacrylate; polysulfonic acids, such as poly (styrenesulfonic acid); polyesters, such as glycol polyacrylate; polyamids, such as polyacrylamide; polyurethanes, such as polyurethane elastomers containing ionic groups, such as -COO " , S0 3 ~ , and quaternary ammoniumion, and polyurethanes elastomers containing nonionic hydrophilic groups; polyvinylpyrrolidone; poly (ethylene oxide); polymeric cationic compounds, and mixtures thereof; and b) copolymers including: styrene copolymers, such as styrene-acrylate polymers and styrene-ethylene oxide polymers; copolymers of polyvinyl and maleic acid compounds, such as styrene-maleic anhydride polymers and vinyl acetate- maleic acid ester polymers; polyvinyl-polyalkylene copolymers, such as vinylacetate- ethylene polymers, ethylene-acrylic acid-acrylic acid ester polymers, and ethylene acrylic acid-acrylonitril polymers; other vinyl copolymers such as vinyl acetate polymers, acrylic acid- acrylonitrile polymers, acrylic acid- acrylamide polymers, and butadiene-acrylonitril polymers; acrylonitrile-butadiene-styrene polymers (ABS polymers) ; and mixtures thereof; and mixtures of said polymers (a) and copolymers (b) . 5. A binder according to claims 1 or 2, wherein the protective colloidal agent is an addition terpolymer consisting essentially of a carboxylic functional monomer X, a relative water-insoluble monomer Y, and a urethane functional associative monomer Z having the formula -[X]-[Y]-[Z]- wherein I X - -CH 2 -C(R)-CO-0 " ,NH 4 + wherein R is H, methyl or ethyl, wherein R 1 is H, methyl or ethyl, and R 2 is methyl, ethyl, propyl or butyl, and Z = -CH 2 -C(R 3 )-C 6 H 4 -C(CH 3 )2-NH-CO-0-R n 4 -C 6 H,-R 5 wherein R 3 is H, methyl or ethyl, R 4 is a C 2 -C 4 oxylalkylene group and R 5 is a C5-C15 group and n is 6- 150, preferably 40-60 and more preferably 50. 6. A binder according to claims 5, wherein the protective colloidal agent is a modified ethoxalate urethane, such as Polyphobe®. 7. A binder according to claims 5 or 6, wherein the protective colloidal agent is Polyphobe® 102, 103 or TR117. 8. A binder according to claims 1 or 2, wherein the protective colloidal agent is a natural emulsifier selected from the group consisting of: lanolin; lecithins, albumins and cholesterols, such as egg yolk; waxes, such as bees wax; lignosulfonates, cellulose and cellulose derivatives, such as cellulose ethers; proteins, such as casein, whey protein or gelatin; polysaccharides such as starch, dextrin and pectin; types of rubber, such as natural rubber latex, gum arabic, mastics, tragacanth and guar gum; mucilages from algea and lichen (alginates), such as carregheenan, agar-agar; saponins; and locust bean flower; and mixtures thereof. 9. A binder according to any one of claims 1-8, wherein the phenolic resin consists essentially of the reaction product of phenol and aldehyde in a phenol to aldehyde molar ratio is less than 1:1. 10. A binder according to any one of claims 1-9, wherein the molar ratio of phenol to aldehyde is in the range of 1:2 to 1:6, preferably 1:3 to 1:4.5. 11. A binder according to any one of claims 1-10, wherein the resin contains 15% to 60% by weight of solids, preferably 20 to 45% by weight. 12. A binder according to any of claims 1-11, wherein the pH is larger than 7. 13. A binder according to any one of claims 1-12, wherein the content of free phenol is below 0.5% by weight. 14. A method of producing an emulsifiable phenolic resin comprising: a) reacting a phenolic component, such as phenol with formaldehyde, in the presence of an effective amount of an alkaline catalyst for a sufficient reaction time and at a suitable temperature to provide a degree of conversion of phenol of 99% or more, b) cooling the reaction mixture to stop further condensation, and c) adding less than 0.1% by weight of a protective colloidal agent. 15. A method according to claim 14, wherein the water dilutability of the cooled reaction mixture of step b) is in the range of 0.5 to 5, preferably in the range of 1 to 4, in particular 2 to 4. 16. A method according to claim 14 or 15, further comprising neutralizing the alkaline catalyst. 17. An emulsifiable phenolic resin obtainable by the method as claimed in claims 14-16. 18. A method of producing a stabilized aqueous phenolic binder for mineral wool comprising providing an emulsifiable phenolic resin as defined in claims 1-13, or obtainable by the method as claimed in claims 14-16; adjusting the pH in the range of 7 to 10 and adding an effective amount of water to form a two-phase system. 19. A method according to claim 18 further comprising adding an aldehyde scavenger. 20. A method according to claim 18, further comprising adding a silane. 21. A method according to claim 18, further comprising adding ammonium sulphate . 22. A stabilized phenolic binder obtainable by the method as claimed in claims 18-21. 23. Use of a binder according to claims 1-13 and 18-22 in the production of mineral wool products. 24. A method of producing a mineral wool product, said method comprising the steps of: a) providing a stabilized phenolic binder according to claims 1-13 and 18-22; b) applying the binder to the mineral wool; and c) curing the binder in the mineral wool. 25. A method according to claim 24, wherein the stabilized aqueous phenolic binder is produced immediately before being applied to said mineral wool. 26. A mineral wool product obtainable by the method as claimed in claims 24-25. 27. A mineral wool product containing 0.5 to 12% by weight, preferably 0.5 - 6% by weight of binder according to claims 1-13 or obtainable by the method as claimed in claim 22. 28. A method according to claim 24 further comprising adjusting the pH of the binder in the range of 7 to 10 and adding an effective amount of water to form a two- phase system. 29. A mineral wool product obtainable by the method as claimed in claims 24-25 and 28.

Inventors: HANSEN ERLING LENNART, NISSEN POUL CHRISTIAN, HANSEN, ERLING, LENNART, NISSEN, POUL, CHRISTIAN
Applicants: HANSEN ERLING LENNART, NISSEN POUL CHRISTIAN, ROCKWOOL INT, HANSEN, ERLING, LENNART, NISSEN, POUL, CHRISTIAN, ROCKWOOL INTERNATIONAL A/S
Application year: 1999
Main classification: C08G8
IPC codes: C03C25, C08L61, C09J161