NAIL POLISH KITS

Abstract: The present invention relates to kits and films formed from the kits which are useful as cosmetic or therapeutic agent, as well as methods of their use. The films and kits herein are particularly useful as polishes for mammalian nails. More particularly, the present invention relates to kits and films which, when applied to mammalian nails exhibit long wear.

Description: NAIL POLISH KITS TECHNICAL FIELD The present invention relates to kits useful as cosmetic or therapeutic agents and films formed therefrom. The kits and films herein are particularly useful as polishes for mammalian nails. BACKGROUND OF THE INVENTION Consumers use nail polishes to cosmetically enhance their nails or protect the nails from everyday conditions and stressors. However, these nail polishes are deficient in many respects, including their inability to provide long wear. Nail polishes which are known or currently available often exhibit deterioration, particularly in the form of chipping or peeling, in as few as one or two days. Such deterioration is exhibited primarily at the tip of the nail. The occurrence of this deterioration often forces consumers to remove their nail polish soon after original application and reapply additional nail polish to the nails. Consumers may also attempt to correct the unsightly appearance of the deteriorating nail polish by "touching-up" the areas of the nail which exhibit the deterioration, a practice which actually impairs the overall look of the nail polish. Finally, consumers may choose to do nothing about the deterioration and allow, for example, chipping and peeling to progress, resulting in nails which are not only minimally protected from the environment but are unsightly as well. The art is replete with nail polish compositions which are promoted as having long wear, good adhesion, and / or resistance to chipping. While some nail polish compositions provide better wear than others, a need remains for nail polishes which provide long wear. Extreme examples of nail polish compositions which exhibit inadequate wear are those which are easily and completely peeled or stripped off the nails without the use of a solvent. See, e.g.. EP 0,680,742, Mellul et al.. assigned to L'Oreal. Still further, other nail polish compositions are completely removable with water and, therefore, are not practical for normal use and do not provide long wear under everyday conditions. See, e.g.. JP 05-155,737, Itsumi et al.. assigned to Yuho Chemical Co. and EP 0,679,384, Ramin et al.. assigned to L'Oreal. It would therefore be desirable to provide nail polishes having improved wear properties. The present inventors have surprisingly discovered kits and films which, when applied to mammalian nails, exhibit long wear at a superior level not provided by the nail polishes which are presently known and used. SUMMARY OF THE INVENTION The present invention relates to kits and films formed from the kits which, when applied to mammalian nails, exhibit long wear. The present kits comprise two or more compositions, preferably a basecoat composition, a topcoat composition, and, optionally, a midcoat composition. Each composition comprises a film-forming polymer, a liquid diluent, and, optionally, other components. The present film-forming polymers are selected from polyurethanes, polyacryls, polymethacryls, cellulosic polymers, styrene- acryl copolymers, polystyrene-polyacryl mixtures, polysiloxanes, polyesters, urethane- acryl copolymers, siloxane-urethane copolymers, polyurethane-polymethacryl mixtures, silicone-acryl copolymers, vinyl acetate polymers, and mixtures thereof. DETAILED DESCRIPTION OF THE INVENTION The essential components of the present invention are herein described below. Also included are non-limiting descriptions of various optional and preferred components useful in the kits ofthe present invention. The present invention can comprise, consist of, or consist essentially of any ofthe required or optional components and / or limitations described herein. All percentages and ratios are calculated by weight unless otherwise indicated. All percentages are calculated based on the total composition unless otherwise indicated. All component or composition levels are in reference to the active level of that component or composition, and are exclusive of impurities, for example, residual solvents or by-products, which may be present in commercially available sources. Referred to herein are trade names for materials including, but not limited to, polymers and optional components. The inventors herein do not intend to be limited by materials under a certain trade name. Equivalent materials (e.g., those obtained from a different source under a different name or catalog (reference) number) to those referenced by trade name may be substituted and utilized in the kits, films, and methods herein. All documents referred to herein, including all patents, patent applications, and printed publications, are hereby incorporated by reference in their entirety. The kits and films ofthe present invention are suitable for use as a nail polish for mammalian nails. As used herein, the term "suitable for use as a nail polish for mammalian nails" means that the compositions, kits, or films thereof are suitable for use in contact with mammalian nails without undue toxicity, incompatibility, instability, allergic response, and the like. As used herein, the term "nail polish" is a comprehensive term describing a nail polish composition, product (including coloring products), system, kit, or the like, which is useful for providing, for example, aesthetic, therapeutic, or prophylactic benefits to the nail. As used herein, the term "mammalian nail" means a keratinaceous plate present at the upper surface of the end of a fmger or toe of a primate, most preferably a human, or the homologous claw or hoof of another mammal. The layers and films herein may be joined to mammalian nails. As used herein, the terms "joined to", "joined to mammalian nails", or the like means in contact with or applied to a mammalian nail through physical forces in such a manner that the layer or film is contiguous to either the nail itself, a preceding layer, a succeeding layer, or matter previously applied to or existing on the nail. The layer or film may be "joined to" a mammalian nail, preceding layer, or succeeding layer even though other matter (such as another preceding or succeeding layer) intervenes. Accordingly, matter which is "joined to", for example, a mammalian nail, need not actually be contiguous to that mammalian nail. As used herein, the term "contiguous to" means directly joined to by physical forces through touching and boundary sharing with essentially no intervening matter. As used herein, the term "film" means one or more layers of a nail polish suitable for use on mammalian nails which forms when one or more compositions of the kit is applied to, and dries on, mammalian nails. As used herein, the term "layer" means one substantially dry coat of nail polish which forms when a composition ofthe kit is applied to, and dries on, a mammalian nail. As used herein, the term "preceding layer" means a layer which is joined to a nail and is closer in proximity to the nail as compared to a reference layer joined to the same nail. For example, wherein a basecoat and a topcoat are joined to a nail, the basecoat is a preceding layer relative to the topcoat. Similarly, wherein a basecoat, midcoat, and topcoat are joined to a nail, the basecoat and midcoat are preceding layers relative to the topcoat, and the basecoat is a preceding layer relative to both the midcoat and topcoat. As used herein, the term "succeeding layer" means a layer which is joined to a nail and is further in proximity from the nail as compared to a reference layer joined to the same nail. For example, wherein a basecoat and a topcoat are joined to a nail, the topcoat is a succeeding layer relative to the basecoat. Similarly, wherein a basecoat, midcoat, and topcoat are joined to a nail, the midcoat and topcoat are succeeding layers relative to the basecoat, and the topcoat is a succeeding layer relative to both the basecoat and midcoat. As used herein, the term "substantially dry" in reference to a film or a layer means that the film or layer feels dry, smooth, or not tacky when it is touched with a human fingertip. Kits and Films ofthe Present Invention The kits ofthe present invention, when applied to mammalian nails, provide films exhibiting long wear. The kits comprise two or more compositions, preferably a basecoat composition, a topcoat composition, and, optionally, a midcoat composition. Each composition comprises a film-forming polymer, a liquid diluent, and, optionally, one or more other suitable components as described herein. As used herein, the term "film-forming polymer" means a homopolymer, copolymer, or mixture thereof which forms an adherent continuum from a composition when applied to mammalian nails. See, e.g.. Polymer Colloids. Robert M. Fitch, ed., New York: Plenum Press, pp. 173-183 (1971). As used herein, the term "copolymer" includes linear, block, branched, graft, comb, and star copolymers. Although the term "film-forming polymer" is used herein to describe a polymer in a composition, in some circumstances, polymerization may not actually take place until application ofthe composition (to the nail, for example) is performed. Accordingly, as used herein, the term "film-forming polymer" is meant to encompass monomers which have not yet polymerized but will upon application to the nail. The film-forming polymers herein are preferably self-curing polymers. That is, the preferred polymers do not require chemical reaction or introduction of energy (e.g., exposure to ultraviolet rays) to form the adherent continuum. The film-forming polymers herein can be selected from nonionic, ionic (anionic or cationic), and amphoteric (including zwitterionic) polymers. Wherein the film- forming polymer is water-borne, the polymer is preferably anionic. The film-forming polymers herein are preferably, but are not limited to, solvent- borne or water-borne polymers. As used herein, the term "water-borne", with reference to a film-forming polymer, means that the polymer was prepared in a mixture comprising water and is preferably added to the composition which it comprises as a mixture (preferably a dispersion) in water. As used herein, the term "solvent-borne", with reference to a film-forming polymer, means that the polymer was prepared under substantially anhydrous conditions and is preferably added to the composition which it comprises as a substantially anhydrous mixture (preferably a solution). Preferred film-forming polymers of the present invention are selected from polyurethanes, polyacryls, polymethacryls, cellulosic polymers, styrene-acryl copolymers, polystyrene-polyacryl mixtures, polysiloxanes, polyesters, urethane-acryl copolymers, siloxane-urethane copolymers, polyurethane-polymethacryl mixtures, silicone-acryl copolymers, vinyl acetate polymers, and mixtures thereof. The term "polyacryl" includes polyacrylates, polyacrylics, and polyacrylamides. The term "polymethacryl" includes polymethacrylates, polymethacrylics, and polymethacrylamides. The term "cellulosic polymers" includes all cellulose polymers, including esters thereof. Examples of preferred polyacryls, polymethacryls, and styrene-acryl copolymers include Gelva ® 2497 (commercially available from Monsanto Co., St. Louis, MO), Duraplus ® 2 (commercially available from Rohm & Haas Co., Philadelphia, PA), Joncryl ® 95 (commercially available from S.C. Johnson Polymer, Sturtevant, WI), SCX- 1537 (S.C. Johnson Polymer), SCX-1959 (S.C. Johnson Polymer), SCX-1965 (S.C. Johnson Polymer), Joncryl ® 530 (S.C. Johnson Polymer), Joncryl ® 537 (S.C. Johnson Polymer), Glascol LS20 (commercially available from Allied Colloids, Suffolk, VA), Glascol C37 (Allied Colloids), Glascol LS26 (Allied Colloids), Glascol LS24 (Allied Colloids), Glascol LE45 (Allied Colloids), Surcol 441 ® (Allied Colloids), Carboset ® CR760 (commercially available from BFGoodrich, Cleveland, OH), Carboset ® CR761 (BFGoodrich), Carboset ® CR763 (BFGoodrich), Carboset ® 765 (BFGoodrich), Carboset ® 19X2 (BFGoodrich), Carboset ® XL28 (BFGoodrich), Hycar 26084 (BFGoodrich), Hycar 26091 (BFGoodrich), Carbobond 26373 (BFGoodrich), Neocryl ® A-601 (commercially available from Zeneca Resins, Wilmington, MA), Neocryl ® A-612 (Zeneca Resins), Neocryl ® A-6044 (Zeneca Resins), Neocryl ® A-622 (Zeneca Resins), Neocryl ® A-623 (Zeneca Resins), Neocryl ® A-634 (Zeneca Resins), and Neocryl ® A-640 (Zeneca Resins). An example of a preferred polysiloxane is PSA 590 (commercially available from General Electric, Waterford, NY). Examples of preferred urethane-acryl copolymers include Sancure ® AU-4000 (commercially available from BFGoodrich), Sancure ® AU-4010 (BFGoodrich), Witcobond A- 100 (commercially available from Witco Performance Chemicals, Houston, TX), Witcobond W-610 (Witco Performance Chemicals), NeoPac R-9000 (commercially available from Zeneca Resins), NeoPac R-9030 (Zeneca Resins), and NeoPac R-9699 (Zeneca Resins). Preferred polyurethanes are selected from aromatic polyether polyurethanes, aliphatic polyether polyurethanes, aromatic polyester polyurethanes, aliphatic polyester polyurethanes, aromatic polycaprolactam polyurethanes, and aliphatic polycaprolactam polyurethanes. The more preferred polyurethanes are selected from aromatic polyether polyurethanes, aliphatic polyether polyurethanes, aromatic polyester polyurethanes, and aliphatic polyester polyurethanes. Examples of preferred polyurethanes include Sancure 2710 ® and / or Avalure UR 445 ® (which are equivalent copolymers of polypropylene glycol, isophorone diisocyanate, and 2,2-dimethylolpropionic acid, having the International Nomenclature Cosmetic Ingredient name "PPG-17/PPG-34/IPDI/DMPA Copolymer"), Sancure 878 ® , Sancure 815 ® , Sancure 1301 ® , Sancure 2715 ® , Sancure 1828 ® , Sancure 2026 ® , Sancure 1818 ® , Sancure 853 ® , Sancure 830 ® , Sancure 825 ® , Sancure 776 ® , Sancure 850 ® , Sancure 12140 ® , Sancure 12619 ® , Sancure 835 ® , Sancure 843 ® , Sancure 898 ® , Sancure 899 ® , Sancure 1511 ® , Sancure 1514 ® , Sancure 1517 ® , Sancure 1591 ® , Sancure 2255 ® , Sancure 2260 ® , Sancure 2310 ® , Sancure 2725 ® , and Sancure 12471 ® (all of which are commercially available from BFGoodrich, Cleveland, OH), Bayhydrol DLN (commercially available from Bayer Corp., McMurray, PA), Bayhydrol LS-2033 (Bayer Corp.), Bayhydrol 123 (Bayer Corp.), Bayhydrol PU402A (Bayer Corp.), Bayhydrol 110 (Bayer Corp.), Witcobond W-320 (commercially available from Witco Performance Chemicals), Witcobond W-242 (Witco Performance Chemicals), Witcobond W-160 (Witco Performance Chemicals), Witcobond W-612 (Witco Performance Chemicals), Witcobond W-506 (Witco Performance Chemicals), NeoRez R-940 (commercially available from Zeneca Resins), NeoRez R-960 (Zeneca Resins), NeoRez R-962 (Zeneca Resins), NeoRez R-966 (Zeneca Resins), NeoRez R-967 (Zeneca Resins), NeoRez R-972 (Zeneca Resins), NeoRez R-9409 (Zeneca Resins), NeoRez R-9637 (Zeneca), NeoRez R-9649 (Zeneca Resins), and NeoRez R-9679 (Zeneca Resins). Preferred solvent-borne polyurethanes include Sanres EX499 ® (hexylene glycol/neopentyl glycol/isophorone diisocyanate copolymer, Sanres 12711 ® , Sanres 6010 ® , and Sanres 6012 ® (all of which are available from BFGoodrich). The most preferred solvent-borne polyurethane is Sanres EX499 ® . Examples of preferred water-borne polyester polyurethanes include Sancure ® 2060 and Sancure ® 815 (both of which are commercially available from BFGoodrich). The most preferred water-borne polyurethanes are aliphatic polyether polyurethanes. Examples of preferred aliphatic polyether polyurethanes include Sancure 2710 ® and / or Avalure UR 445 ® , Sancure 878 ® , NeoRez R-966, NeoRez R-967, and Witcobond W-320. Preferred cellulosic polymers include, for example, nitrocellulose, cellulose acetate butyrate, and cellulose acetate propionate. The most preferred cellulosic polymer is nitrocellulose. Exemplary nitrocellulose polymers are nitrocellulose RS types (nitrogen content of 11.5% to 12.2%), commercially available from Hercules, such as nitrocellulose RS l A second, nitrocellulose RS ! second, nitrocellulose RS 1/8 second, and nitrocelluose RS 1/16 second, and the like. Wherein a composition comprises a cellulosic polymer, the composition preferably comprises a plasticizer. The compositions ofthe present invention further comprise a carrier comprising a liquid diluent. The liquid diluent comprises water, organic solvent, or mixtures thereof. Preferred organic solvents include those which are volatile. Preferred volatile organic solvents, at atmospheric pressure, have a boiling point of from about 50 °C to about 140 °C, more preferably from about 56 °C to about 125 °C, and most preferably from about 56 °C to about 98 °C. Wherein the film-forming polymer utilized is water-borne, the organic solvent is preferably water-miscible. Preferred organic solvents are selected from alcohols, esters, ketones, aromatic hydrocarbons, aliphatic hydrocarbons, ethers, and mixtures thereof. Alcohols and esters are more preferred. Preferred alcohols are monohydric. The most preferred monohydric alcohols are ethanol, wo-propanol, and «-propanol. The most preferred esters are ethyl acetate and butyl acetate. Other non-limiting examples of suitable organic solvents are benzyl alcohol, amyl acetate, propyl acetate, acetone, heptane, wo-butyl acetate, iso- propyl acetate, toluene, methyl acetate, wø-butanol, n-amyl alcohol, «-butyl alcohol, hexane, and methyl ethyl ketone. The kits ofthe present invention may further comprise information which informs a user of the kit, by words, pictures, and / or the like, that use of the kit will provide one or more long wear benefits, including, but not limited to, resistance to chipping, peeling, denting, and / or peeling. The films herein are formed when a kit of the present invention is applied to mammalian nails. The films of the present invention comprise two or more layers formed from two or more different compositions, most preferably two or three layers formed from two or three different compositions, respectively. The preferred films are those which are comprised of a basecoat and a topcoat, and those which further comprise a midcoat. The films herein are not peelable from the nails. That is, the films herein, when joined to the nail, cannot be stripped off the nail by simply peeling the film off the nail in a substantially intact form. The multi-layer films herein form when two or more compositions of the kit, as described herein, are applied to and substantially dry on mammalian nails. The compositions useful herein may be described as basecoat compositions, midcoat compositions, or topcoat compositions, depending on their intended positioning on the nail. A. Basecoat Compositions As used herein, a "basecoat composition" is a composition which is suitable for application to a mammalian nail to form a basecoat, which is a layer of nail polish. A basecoat composition is preferably applied contiguously to a mammalian nail with or without, more preferably with, one or more succeeding layers applied to the resulting basecoat. The basecoat composition is preferably applied contiguously to a mammalian nail with one or more, more preferably one (topcoat), and most preferably two (midcoat and topcoat), succeeding layers joined to the resulting basecoat. Without intending to be limited by theory, it is believed that the basecoats of the present invention are beneficial to long wear because they provide a preferred level of adhesion to the nail. Such adhesion is believed to be due to physical forces, rather than chemical bonding to the nail. As is known in the art, these physical forces include non- covalent interactions such as polar, non-polar, hydrogen bonding, and charged interactions as well as physical interactions such as mechanical interlocking. 10 The present basecoat compositions comprise a film-forming polymer, a liquid diluent, and, optionally, one or more other suitable components as described herein. The basecoat compositions preferably comprise from about 0.1% to about 40%, more preferably from about 0.1% to about 20%, still more preferably from about 0.1% to about 15%, still more preferably from about 1% to about 10%, and most preferably from about 2% to about 6% ofthe film-forming polymer (polymer solids), and preferably from about 10% to about 90%, more preferably from about 40% to about 90%, even more preferably from about 50% to about 90%, and most preferably from about 70% to about 90% of the volatile organic solvent (as described herein above), by weight of the composition. The balance of the compositions is substantially water, preferably at least about 4%, more preferably from about 4% to about 85%, still more preferably from about 10% to about 80%, and most preferably from about 25% to about 80%, by weight of the composition, of water. The film-forming polymers of the basecoat compositions are preferably water- insoluble at ambient temperature and pressure. Preferred film-forming polymers for use in the basecoat compositions are selected from polyurethanes, polyacryls, polymethacryls, urethane-acryl copolymers, styrene- acryl copolymers, cellulosic polymers, polysiloxanes, and mixtures thereof. The more preferred polymers of basecoat compositions are selected from cellulosic polymers, polyurethanes, polyacryls, polymethacryls, polysiloxanes, and mixtures thereof. Even more preferred polymers of basecoat compositions are selected from polyurethanes, polyacryls, polymethacryls, urethane-acryl copolymers, styrene-acryl copolymers, and mixtures thereof. The most preferred polymers for use in the basecoat compositions are polyurethanes. The most preferred polyurethane for use in basecoat compositions is Sancure 2710 ® and / or Avalure UR 445 ® . Preferred types of each of these polymer classes, and examples thereof, are described herein above. The film-forming polymers of the basecoat compositions are preferably solvent- borne or water-borne, most preferably water-borne. Especially preferred water-borne polymers are selected from polyurethanes, polyacryls, polymethacryls, urethane-acryl copolymers, styrene-acryl copolymers, and mixtures thereof. Especially preferred 11 solvent-borne polymers are selected from cellulosic polymers, polyurethanes, polyacryls, polymethacryls, polysiloxanes, and mixtures thereof. Preferred polyacryls, polymethacryls, and styrene-acryl copolymers for use in the basecoat compositions are those having a glass transition temperature (T g ) of from about -30 °C to about +60 °C, more preferably from about -20 °C to about +20 °C, surface energies from about 32 mJ/m 2 to about 43 mJ/m 2 , calculated using the harmonic mean equation (as determined by the Wilhelmy Technique described by A.W. Neumann and R.J. Good, Surface and Colloid Science. Vol. 2, R.J. Good and R.R. Stromberg, Eds., Plenum Press (1979)), and / or polarities from about 0.19 to about 0.29. The most preferred polyacryls and polymethacryls for use in basecoat compositions include Glascol LS20, Glascol C37, Joncryl ® 95, and SCX-1965. B. Topcoat Compositions As used herein, a "topcoat composition" is a composition which is suitable for application to a mammalian nail to form a topcoat, which is a layer of nail polish. The topcoat composition is preferably applied contiguously to, or applied to, one or more preceding layers. The topcoat composition is more preferably applied contiguously to one or two, preferably one (basecoat), and most preferably two (basecoat and midcoat), preceding layers. Without intending to be limited by theory, it is believed that the topcoats are beneficial to long wear because they deflect environmental stressors by virtue of their hardness, toughness, durability, rigidity, and resistance to chipping. The present topcoat compositions comprise a film-forming polymer, a liquid diluent, and, optionally, other suitable components as described herein. The film-forming polymers of the topcoat compositions are preferably either solvent-borne or water-borne and are preferably water-insoluble. Preferred film-forming polymers for topcoat compositions have glass transition temperatures (T g ) from about +20 °C to about +100 °C, more preferably from about +30 °C to about +80 °C. The preferred film-forming polymers of topcoat compositions of the present invention are selected from polyurethanes, polyacryls, polymethacryls, styrene-acryl copolymers, cellulosic polymers, polyesters, vinyl acetate polymers, polysiloxanes, 12 polystyrene-polyacryl mixtures, siloxane-urethane copolymers, polyurethane- polymethacryl mixtures, silicone-acryl copolymers, and mixtures thereof. The more preferred film-forming polymers of topcoat compositions are selected from cellulosic polymers, polyurethanes, polyacryls, polymethacryls, polysiloxanes, and mixtures thereof. Even more preferred film-forming polymers of topcoat compositions are selected from polyurethanes, polyacryls, polymethacryls, polystyrene-polyacryl mixtures, styrene-acryl copolymers, siloxane-urethane copolymers, cellulosic polymers, polyesters, polyurethane-polymethacryl mixtures, silicone-acryl copolymers, vinyl acetate polymers, and mixtures thereof. The most preferred film-forming polymers of topcoat compositions are polyacryls and polyurethane-cellulosic polymer mixtures. The most preferred polyacryl for use in topcoat compositions is Duraplus 2 ® . Preferred types of each of these polymer classes, and examples thereof, are referred to herein above. Preferred solvent-borne film-forming polymers include polyurethane- polymethacryl mixtures, polyurethane-cellulosic polymer mixtures, polyurethanes, polyacryls, polymethacryls, silicone-acryl copolymers, and mixtures thereof, more preferably, polyacryls and polyurethane-cellulosic polymer mixtures, and most preferably polyacryls. Wherein the film-forming polymer of the topcoat composition is solvent-borne, the topcoat composition preferably comprises from about 1% to about 50%, more preferably from about 10% to about 25% of the film-forming polymer (polymer solids), by weight of the composition. The topcoat composition comprising the solvent-borne polymer preferably further comprises from about 50% to about 99%, more preferably from about 75% to about 90%, by weight of the composition, of a volatile organic solvent (as described herein above). Wherein the topcoat composition comprises a solvent-borne film-forming polymer, preferred optional components include thickeners, plasticizers, pigments or dyes, resins, and slip aids. Preferred water-borne film-forming polymers are selected from polyurethanes, polyacryls, polymethacryls, styrene-acryl copolymers, siloxane-urethane copolymers. and mixtures thereof. More preferred water-borne film-forming polymers are selected 13 from polyacryls and styrene-acryl copolymers and the most preferred water-borne film- forming polymers are polyacryls. Wherein the film-forming polymer ofthe topcoat composition is water-borne, the topcoat composition preferably comprises from about 1 % to about 40%, more preferably from about 5% to about 30%, and most preferably from about 10% to about 25%, by weight ofthe composition, ofthe film-forming polymer (polymer solids). The topcoat composition comprising the water-borne polymer preferably further comprises a coalescent. Preferably, the topcoat composition comprising the water-borne polymer comprises from about 0.1 % to about 30%, more preferably from about 1% to about 20%), by weight of the composition, of a coalescent. Preferably, the ratio of water- borne film-forming polymer to coalescent is from about 1:1 to about 4:1. Wherein the topcoat composition comprises a water-borne film-forming polymer, other preferred optional components include plasticizers, slip aids (especially waxes and surfactants containing siloxanes), thickeners, and pigments or dyes. Topcoat compositions comprising water-borne film-forming polymers may also optionally contain up to about 50%, more preferably from about 5% to about 40%, and most preferably from about 10% to about 30%, by weight of the composition of a volatile organic solvent. Preferred organic solvents are described herein above. Wherein the topcoat composition comprises a water-borne polymer, the balance ofthe composition is substantially water. The film-forming polymers of the present topcoat compositions may be cross- linked polymers. The present inventors have surprisingly discovered that film-forming polymers which are cross-linked provide properties which are particularly advantageous for topcoat compositions and topcoats including, for example, chip-resistance and superior hardness. Cross-linking may occur either in the composition itself or after application and film formation. However, as used herein, polymers which are not actually cross-linked in the composition but may become cross-linked (i.e., "cross- linkable" polymers) due to the presence of a basic moiety (as described herein) are referred to herein as cross-linked polymers. 14 As used herein, a "cross-linked polymer" is a polymer which is ionically linked either intramolecularly to itself and / or intermolecularly to one or more other polymers wherein the linkage is formed through an ionic bridge between a metallic ion and a basic moiety comprising the polymer. Cross-linked polymers are preferably intermolecularly linked. Suitable metallic ions include those with an oxidation state of +2, +3, +4 or higher and which are soluble in water. Preferred metallic ions are selected from Zn + Mg + 2, Ca + 2, Fe + 2, Fe + 3, Al + 3, Mn + 2, Co + 2, and Ni + 2. More preferred metallic ions are selected from Zn + 2, Mg + 2, Ca + 2, Fe + 2, Fe + ^, and Al + 3. The most preferred metallic ion is Zn + 2. The basic moieties herein are negatively charged or otherwise basic. The basic moieties may be either present in, or pendant from, the film-forming polymer backbone. Preferred basic moieties are selected from carboxylates, sulfonates, sulfates, phosphates, phosphonates, hydroxymates, borate esters, imidazoles, a-thioketones, thioacids, and alkyl amines. More preferred basic moieties are selected from carboxylates, sulfonates, sulfates, phosphates, phosphonates, and alkyl amines. Even more preferred basic moieties are selected from carboxylates, sulfonates, sulfates, phosphates, and phosphonates. The most preferred basic moieties are carboxylates. The most preferred cross-linkable polymers are selected from polyacryls, polymethacryls, styrene-acryl copolymers, styrene-methacryl copolymers, and mixtures thereof. Cross-linked polymers may be commercially obtained (for example, Duraplus 2 ® ). Cross-linked polymers may alternatively be produced by obtaining or synthesizing a polymer comprising a pendant basic moiety and adding to that polymer a metal ion solution such as, for example, Zinc Oxide Solution #1 (containing about 15% metal ion solids, commercially available from S.C. Johnson & Sons, Inc.) or Bacote 20 (commercially available from Magnesium Elektron, Inc., Flemington, NJ). Wherein a metal ion solution is added, the solution is added in an amount sufficient to react substantially completely with the available basic moieties present on the film-forming polymer. Preferably, the amount of metal ion solids, relative to the polymer solids present in the composition, is from about 0.2% to about 0.7%, more preferably from 15 about 0.3%) to about 0.6%, and most preferably from about 0.4% to about 0.5%, by weight ofthe composition. Wherein the film-forming polymer is cross-linked, the polymer is most preferably water-borne. Wherein a topcoat comprises a cross-linked polymer, the topcoat may be removed from the nail by a wash treatment with a chelator solution which selectively pulls metal cross-linking ions out of the film and destroys the film. Suitable chelator solutions are selected based on the type of metal ion utilized. Exemplary solutions include, for example, aqueous solutions of ethylenediamine disuccinic acid. C. Midcoat Compositions As used herein, a "midcoat composition" is a composition which is suitable for application to a mammalian nail to form a midcoat, which is a layer of nail polish. The midcoat composition is preferably applied contiguously to a preceding layer, either a basecoat or another midcoat, most preferably a basecoat. One or more succeeding layers is applied to the layer formed by the midcoat composition. Preferably, a topcoat is applied contiguously to the layer formed by the midcoat composition. The use of midcoats is preferred wherein there are significant differences between the physical and / or mechanical properties of the basecoat and the topcoat. For example, midcoats preferably relax stress between flexible basecoats and tough topcoats and / or provide color. The present midcoat compositions comprise a film-forming polymer, a liquid diluent, and, optionally, other suitable components as described herein. Preferred optional components for midcoat compositions are selected from plasticizers, pigments, and dyes. Midcoat compositions preferably comprise from about 10% to about 25%, more preferably from about 10% to about 18% of a film-forming polymer, from about 60% to about 85%, more preferably from about 60% to about 80% of a volatile organic solvent (as described herein above), and preferably 0% to about 13%), more preferably from about 5% to about 13%, and most preferably from about 6% to about 12% of a plasticizer, by weight ofthe composition. 16 Film-forming polymers comprising the midcoat compositions are selected from cellulosic polymers, polyurethanes, polyacryls, polymethacryls, polysiloxanes, and mixtures thereof. More preferred film-forming polymers are polyacryls and cellulosic polymers, with cellulosic polymers being the most preferred. Preferred types of each of these polymer classes, and examples thereof, are described herein above. Preferred polyacryls for the midcoat compositions are those which are hydrophobic and / or exhibit a glass-transition temperature (T g ) of from about -10 °C to about +30 °C. Wherein the polyacryl has a T g higher than about +30 °C, the midcoat composition preferably comprises a plasticizer. Exemplary compositions suitable for use as midcoat compositions are commercially available such as, for example, those marketed under the Max Factor ® or Cover Girl ® trade names. Optional Components The compositions of the kits of the present invention may, independently, comprise additional optional components to enhance their performance as a nail polish. For example, antifoams, buffers, chelating agents, coalescents, dispersing agents, dyes, epoxies, fillers, pigments, preservatives, resins, therapeutic and prophylactic agents, thickeners, wax additives, wetting agents, and the like can be included in the compositions herein. Such optional components may be dispersed, solubilized, or otherwise mixed in the carrier and / or the liquid diluent of the compositions. These components may be added to the compositions herein provided they do not substantially hinder the long wear of the kits. Non-limiting examples of optional components are given below. Coalescents Coalescents may optionally be added to the compositions to enhance film- formation, most preferably wherein the film-forming polymer is water-borne. Such coalescing aids are known in the art and are typically glycol ethers or glycol ether esters such as C,_, 0 straight or branched chain alkyl glycol alkyl ethers, ., 0 straight or 17 branched chain alkyl ether acetates, di-C,. 10 alkyl ether acetates, and C,. 10 alkyl glycol phenyl ethers. Preferred coalescing aids include, for example, ethylene glycol ethers (e.g., Dowanol EB®, commercially available from Dow Chemical Co.), diethylene glycol ethers, triethylene glycol ethers, propylene glycol ethers (e.g., Dowanol PnP®, Dow Chemical Co.), dipropylene glycol ethers (e.g., Dowanol DPnP®, Dow Chemical Co.), tripropylene glycol ethers, terpenes, camphor, methyl cellusolve, butyl cellusolve, hexyl cellusolve, methyl carbitol, butyl carbitol, and dibutyl phthalate. Preferably, a composition comprises from 0% to about 10%, more preferably from about 0.1 % to about 10%, by weight ofthe composition, of a coalescent. Pigments or Dyes Pigments and other suitable coloring agents, such as dyes, may be incorporated into the compositions. Suitable pigments are inorganic or organic pigments known as, for example, the FD&C and D&C colors, lakes, and iron oxides. Such pigments are disclosed in the C.T.F.A. Cosmetic Ingredient Handbook. First Edition, 1988. Organic pigments include, for example, D and C Red, Nos. 10, 11, 12, and 13, D and C Red No. 7, D and C Red Nos. 5 and 6, D and C Red Nos. 30 and 34, lacquers such as D and C Yellow No. 5 and D and C Red No. 2, and guanine. Inorganic pigments include, for example, titanium dioxide, bismuth oxychloride, brown iron oxide, and the red iron oxides. Preferably, the present compositions comprise from 0% to about 5%, more preferably from 0% to about 2%, and most preferably from 0% to about 1%, by weight of the composition, of a pigment or dye. Plasticizers Without intending to be limited by theory, plasticizers cause a composition to become more easily deformed. One or more plasticizers may optionally be added to the present compositions. Suitable plasticizers include those disclosed in WO 97/00664, Chen et al. assigned to Eastman Chemical Co. Suitable plasticizers include phthalates, nonionic surfactant polymers, camphor, castor oil, sucrose acetate isobutyrate, alkyl 18 toluenesulfonamides, e.g., ethyl toluenesulfonamide (e.g., Uniplex PX-45, commercially available from Unitex Chemical Corp., Greenboro, NC), and polyester acid derivatives (e.g., Uniplex 670P, commercially available from Unitex Chemical Corp.), particularly polyester di- and tri-acids. Preferred plasticizers include diethyl phthalate, dibutyl phthalate, dioctyl phthalate, diethyl tartrate, dibutyl tartrate, diethyl phosphate, dibutyl phosphate, polyester sebacates, such as Paraplex G-25® (commercially available from C.P. Hall, Bedford Park, IL) polyester adipates, such as Paraplex G-50® (C.P. Hall) and tetraethylene glycol di-2-ethylhexoate, available as Tegmer® (C.P. Hall). The most preferred plasticizers include dibutyl phthalate, Paraplex G-25®' Paraplex G-50®, camphor, Uniplex PX-45, and Tegmer®. A composition preferably comprises from 0% to about 15%, more preferably from 0% to about 10%, and most preferably from 0% to about 5%, by weight of the composition, of a plasticizer. Preservatives One or more preservatives may optionally be added to the present compositions to prevent, inhibit, or retard microbial growth in the composition. Preferred preservatives include methyl paraben, ethyl paraben, propyl paraben, benzyl alcohol, benzoic acid, benzoates (preferably sodium benzoate), sorbates (preferably potassium sorbate), sodium dehydroacetate, 1 -(3 -chloroallyl)-3 ,5 ,7-triaza- 1 -azoniaadamantane chloride (which may be obtained commercially as Quaternium-15® from Dow Chemical Co., Midland, MI), a mixture of 95% l,3-dimethylol-5,5-dimethyl hydantoin and 5% 3- iodo-2-propynyl butyl carbamate (which mixture is commercially available as Glydant Plus® from Lonza, Inc., Fair Lawn, NJ), l,3-dimethylol-5,5-dimethyl hydantoin (commercially available as Glydant® from Lonza, Inc.), diazolidinyl urea (commercially available as Germall II® from Sutton Laboratories, Chatham, NJ), imidazolidinyl urea (commercially available as Germall 115® from Sutton Laboratories), phenoxyethanol, and Kathon® (commercially available from Rohm and Haas Co., Philadelphia, PA). The most preferred preservatives include methyl paraben, ethyl paraben, propyl paraben, 19 benzyl alcohol, benzoic acid, benzoates (preferably sodium benzoate), sorbates (preferably potassium sorbate), and sodium dehydroacetate. A composition preferably comprises from 0% to about 10%, more preferably from 0% to about 5%, and most preferably from 0% to about 1%, by weight of the composition, of a preservative. Resins Resins including, for example, epoxies and polyacrylics, may optionally be added. Examples of suitable resins include Polytex E75® (commercially available from Estron Chemical, Inc., Calvert City, KY) and Acryloid B66® (commercially available from Rohm and Haas, Philadelphia, PA). A composition preferably comprises from 0% to about 15%, more preferably from about 0.5% to about 10%, by weight ofthe composition, of a resin. Slip Aids Slip aids may optionally be added to improve surface friction, water resistance, abrasion resistance, and mechanical properties. Slip aids which may be used include wax additives including, for example, animal, fossil, vegetable, mineral, or synthetic waxes. Preferred wax additives include beeswax, carob, candelilla, ozocerite, polyethylene waxes, paraffin waxes, polypropylene waxes, polytetrafluoroethylene (commercially available as Teflon ® from DuPont, Wilmington, DE), nylons, and polyamides. Specifically, preferred wax additives include, but are not limited to, Jonwax ® 26 (commercially available from S.C. Johnson Polymer, Sturtevant, WI) Jonwax ® 120 (S.C. Johnson Polymer), Chemcor 325N35, Chemcor 43N40, Glaswax ® E-l (commercially available from Allied Colloids, Suffolk, VA), Glaswax ® E-l 235 (Allied Colloids), Drewax ® E-3030 (commercially available from Ashland Chemical, Boontown, NJ), Drewax ® E-7030 (Ashland Chemical), Lanco ® PP1362D (commercially available from Lubrizol, Wichliffe, OH), Lanco ® A1601 (Lubrizol), and Lanco ® TF1780 (Lubrizol). Other slip aids include materials containing silicone such as copolymers of polyether and polysiloxane. Examples of such slip aids include, for example, Glide 450 20 and Abil B-8830 (both of which are commercially available from Goldschmidt Chemical, Hopewell, VA). The present compositions preferably comprise from 0% to about 10%, more preferably from about 0.1 % to about 10%, even more preferably from about 0.5% to about 8%, and most preferably from about 0.5%) to about 3% of a slip aid. Stabilizers One or more stabilizers may be added to the compositions herein, e.g., to prevent pigment from settling or to achieve desired application properties. Preferably, stabilizers are added to compositions comprising a solvent-borne film-forming polymer. Preferred stabilizers include clays, e.g., organically modified bentonites and hectorites such as stearalkonium bentonite and stearalkonium hectorite (commercially available from Rheox, Inc., Hightstown, NJ). Wherein a stabilizer is added, the composition preferably comprises from about 0.25% to about 3%, still more preferably from about 0.25% to about 2.5%, and most preferably from about 1% to about 2% ofthe stabilizer, by weight ofthe composition. Therapeutic and Prophylactic Agents Therapeutic and / or prophylactic agents such as, for example, vitamins, proteins, anti-fungal and anti-microbial agents, and sunscreens (including UV-A, UV-B, and broad spectrum solar filters) may optionally be added to the present compositions for the further care and protection ofthe nails. Thickeners Thickeners may optionally be added to the compositions and films herein to achieve desired rheology and application properties. Preferably, thickeners are utilized wherein the composition comprises a water-borne film-forming polymer or at least 4% water. Preferred thickeners include hydroxyethyl cellulose, hydroxypropyl cellulose, methyl cellulose, and other conventional cellulosic polymers, associative thickeners (e.g., hydrophobically modified cellulosic polymers, nonionic urethanes, and alkali swellable urethanes) including Aculyn ® 44 (commercially available from Rohm & Haas, 21 Philadelphia, PA), clays (e.g., laponite and hydrophilic montmorillonite (commercially available as Bentone ® from Rheox, Hightstown, NJ), and natural rubbers and gums (e.g., guar gum, quaternized guar gum sold under the name Jaguar ® C-13-S by Rhone-Poulenc, Shelton, CT), hydroxypropyl guar gum, gum arabic, carob gum, carrageenan. and xanthan gum). The present compositions preferably comprise from 0% to about 10%. more preferably from about 0.1% to about 10%, and even more preferably from about 0.1%) to about 5% of a thickener, by weight ofthe composition. Preferred Kits ofthe Present Invention The kits herein are comprised of two or more separate and different compositions, most preferably two or three separate and different compositions. Preferably, the kits are comprised of at least one of a basecoat composition, a midcoat composition, and / or a topcoat composition. More preferably, the kits are comprised of a basecoat composition, a topcoat composition, and, optionally, a midcoat composition. A preferred kit ("Kit 1") having two separate and different compositions comprises a basecoat composition and a topcoat composition. The basecoat composition of Kit 1 comprises a film-forming polymer, preferably a water-insoluble polymer, which is selected from polyurethanes, polyacryls, polymethacryls, urethane-acryl copolymers, styrene-acryl copolymers, and mixtures thereof. The topcoat composition of Kit 1 comprises a film-forming polymer, preferably a water-insoluble polymer, which is selected from polyurethanes, polyacryls, polymethacryls, polystyrene-polyacryl mixtures, styrene-acryl copolymers, siloxane-urethane copolymers, cellulosic polymers, polyesters, polyurethane-polymethacryl mixtures, silicone-acryl copolymers, vinyl acetate polymers, and mixtures thereof. Another preferred kit ("Kit 2") having three separate and different compositions comprises the basecoat composition and topcoat composition as described for Kit 1 , and further comprises a midcoat composition. The midcoat composition of Kit 2 comprises a film-forming polymer, preferably a water-insoluble polymer, which is selected from 22 cellulosic polymers, polyurethanes, polyacryls, polymethacryls, polysiloxanes, and mixtures thereof. Another preferred kit ("Kit 3") having two separate and different compositions comprises a basecoat composition and a topcoat composition. The basecoat composition of Kit 3 comprises a film-forming polymer, preferably a water-insoluble polymer, which is selected from polyurethanes, polyacryls, polymethacryls, urethane-acryl copolymers, styrene-acryl copolymers, and mixtures thereof. The topcoat composition of Kit 3 comprises a film-forming polymer, preferably a water-insoluble polymer, which is selected from cellulosic polymers, polyurethanes, polyacryls, polymethacryls, polysiloxanes, and mixtures thereof. Another preferred kit ("Kit 4") having two separate and different compositions comprises a basecoat composition and a topcoat composition. The basecoat composition of Kit 4 comprises a film-forming polymer, preferably a water-insoluble polymer, which is selected from cellulosic polymers, polyurethanes, polyacryls, polymethacryls, polysiloxanes, and mixtures thereof. The topcoat composition of Kit 4 comprises a film- forming polymer, preferably a water-insoluble polymer, which is selected from polyurethanes, polyacryls, polymethacryls, polystyrene-polyacryl mixtures, styrene-acryl copolymers, siloxane-urethane copolymers, cellulosic polymers, polyesters, polyurethane-polymethacryl mixtures, silicone-acryl copolymers, vinyl acetate polymers, and mixtures thereof. Method of Making and Using The compositions of the present invention are made using conventional formulation and mixing techniques. A layer of nail polish may be prepared by standard application of a composition to mammalian nails using a standard brush-applicator as is commonly utilized in the art and removing sufficient liquid diluent (through evaporation of volatiles, most preferably at ambient pressures and temperatures) to form the substantially dry layer. The multi-layer films of the present invention are prepared in a 23 similar manner by standard application of one or more additional compositions contiguously to the preceding layer. Such application is well-known in art. The present invention includes a method of coating mammalian nails with a nail polish film, wherein the film comprises two or more layers. The method comprises the steps of: (i) applying a basecoat composition contiguously to the nail, wherein the basecoat composition comprises a film-forming polymer and a liquid diluent; (ii) removing sufficient liquid diluent from the basecoat composition to form a substantially dry basecoat; (iii) optionally applying a midcoat composition to the basecoat, wherein the midcoat composition comprises a film-forming polymer and a liquid diluent; (iv) removing sufficient liquid diluent from the midcoat composition to form a substantially dry layer; (v) applying a topcoat composition to the basecoat (or the layer formed by the midcoat composition, if used), wherein the topcoat composition comprises a film-forming polymer and a liquid diluent; and (vi) removing sufficient liquid diluent from the topcoat composition to form a substantially dry topcoat. Examples The following examples further describe and demonstrate embodiments within the scope of the present invention. The examples are given solely for the purpose of illustration and are not to be construed as limitations of the present invention, as many variations thereof are possible without departing from the spirit and scope of the invention. In the examples below, all polymer component percentages are expressed in weight percent of solid polymer (based on the total composition). 24 Examples 1A - IH The compositions of Examples 1A - IH are suitable for use as basecoat 1A IB 1C ID IE IF 1G IH Sancure 2710 ® 5.5 % 4 % 5.8 % 5.81 % 5.4 % - 5.74 % 5.74 % Glascol LS20 ® - - - - 5.7 % - - - NeoRez 5.87 % R967 ® Ethanol 7.9 % - - - - - - - wo-Propanol 32.13 44.9 % 65.8 % 65.83 46.99 % % % Ethyl Acetate 78.1 % - - - - - - - M-Propanol - 71.6 % 70.0 % - - - - - Methyl 0.1 % 0.21 % 0.1 % 0.2 % 0.2 % Paraben Propyl 0.1 % 0.2 % Paraben Water 8.5 % 24.4 % 24.0 % 61.85 43.8 % 28.23 28.23 47.07 % % % % compositions: 25 Examples 2A - 2E The compositions of Examples 2A - 2E are suitable for use as topcoat compositions: 2A 2B 2C 2D 2E Duraplus 2 ® 21% - - 21% - Nitrocellulose 15% 6.75 % RS l A second Sanres ® EX499 - 3.6 % - - - Sanres ® 12711 - 1.5% 15.5% - - Sanres ® 6012 - - - - 8.25 % Surcol ® 441 - - 4.5 % - - Dowanol DPnP ® 10% - - 10% - Dibutyl Phthalate 3.9 % - - 1.6% - Glide 450 ® 0.3 % - - 0.3 % - Aculyn 44 ® 0.5 % - - - - Polytex E-75 ® - 1% - - - Drewax E-3030 ® - - - 1.2% - Paraplex G-50 ® - 7.6 % - - - 26 Butyl Acetate - 30.9 % 28% - 38% Ethyl Acetate - 27.4 % 10% - - wo-Propanol - 11% 30% - 35% Toluene - - - - 10% Acetone - - 10% - - Pigment - 1% 1% - 1% Clay - 1% 1% - 1% Water 64.3 % - - 65.9 % - Example 3 27 The following composition may be used as either a midcoat composition or a Component Supplier Slurry Code* Source Percentage Solid Nitrocellulose 50-C3-690 Akzo Nobel, Somerset, NJ 7.05% RS second (available as a slurry) Solid Nitrocellulose 5528 Scholle Corp., College Park, 7.00% RS V2 second GA (available as a slurry) Clay** (available as a Bentone slurry Kirker Enterprises Inc., 1.04% slurry) Paterson, NJ Red #7 Solid Red #7 slurry 6R381 Penn Color, Doylestown, PA 0.60% (available as a slurry) Butyl Acetate J.T. Baker, Phillipsburg, NJ 27.77% Ethyl Acetate J.T. Baker, Phillipsburg, NJ 24.00% MO-Propanol J.T. Baker, Phillipsburg, NJ 6.55% Uniplex 600 Unitex, Greensboro, NC 11.12% Toluene E.M. Science, Gibbstown, NJ 6.44% Camphor Universal Preservachem, 1.43% Edison, NJ Dibutyl Phthalate Eastman Kodak, Kingsport, 7.00% TN Total 100% topcoat composition. *The slurries contain, in addition to the component indicated, other components which are listed in the above formula (such as, for example, butyl acetate and wo-propanol). The percentage given for each component is the percentage of that component only (for example, Solid Nitrocellulose RS X second is present in the control formula at a solids level of 7.05%, exclusive of other components). The levels of the other components in each slurry are combined and reflected in the formula given above. For example, the 28 levels of butyl acetate in Nitrocellulose RS l Λ second slurry, Nitrocellulose RS V_ second slurry, clay, and Red #7 Solid are combined and reflected in the percentage given for the butyl acetate component. **Clay is 50/50 (weight percent ratio) stearalkonium hectorite/stearalkonium bentonite solids. The composition of Example 3 may be prepared as follows. Weigh all components together into a sealable jar to hold a 100 gram batch with minimal head- space. Add six stainless steel balls, each of which are 3/16 inches in diameter. Mix on a conventional paint shaker for thirty minutes. Transfer to conventional nail polish bottles. Example 4 A kit comprising two separate nail polish compositions is prepared. The compositions are a basecoat composition of Example 1 and a topcoat composition of Example 2. The basecoat composition is applied contiguously to mammalian nails using a standard brush-applicator. A basecoat is allowed to form over a period of five minutes. The topcoat composition is applied contiguously to the basecoat using a standard brush- applicator. The topcoat composition is allowed to form a topcoat over a five minute time period, resulting in a film having two layers. Example 5 A kit comprising two separate nail polish compositions is prepared. The compositions are a basecoat composition of Example 1 and a topcoat composition which is a conventional nail polish such as Max Factor ® International (comprising butyl acetate, ethyl acetate, nitrocellulose, toluenesulphonamide formaldehyde resin, dibutyl phthalate, toluene, zsø-propanol, camphor, benzophenone, stearalkonium hectorite, and polyester resin). The basecoat composition is applied contiguously to mammalian nails using a standard brush-applicator. A basecoat is allowed to form over a period of five minutes. The topcoat composition is applied contiguously to the basecoat using a standard brush- applicator. The topcoat composition is allowed to form a topcoat over a five minute time period, resulting in a film having two layers. 29 Example 6 A kit comprising two separate nail polish compositions is prepared. The compositions are a basecoat composition which is a conventional nail polish, such as Max Factor ® International (comprising butyl acetate, ethyl acetate, nitrocellulose, toluenesulphonamide formaldehyde resin, dibutyl phthalate, toluene, MO-propanol, camphor, benzophenone, stearalkonium hectorite, and polyester resin) and a topcoat composition of Example 2. The basecoat composition is applied contiguously to mammalian nails using a standard brush-applicator. A basecoat is allowed to form over a period of five minutes. The topcoat composition is applied contiguously to the basecoat using a standard brush-applicator. The topcoat composition is allowed to form a topcoat over a five minute time period, resulting in a film having two layers. Example 7 A kit comprising three separate nail polish compositions is prepared. The compositions are a basecoat composition of Example 1 , a midcoat composition which is a conventional nail polish, such as Max Factor ® International (comprising butyl acetate, ethyl acetate, nitrocellulose, toluenesulphonamide formaldehyde resin, dibutyl phthalate, toluene, wø-propanol, camphor, benzophenone, stearalkonium hectorite, and polyester resin) and a topcoat composition of Example 2. The basecoat composition is applied contiguously to mammalian nails using a standard brush-applicator. A basecoat is allowed to form over a period of five minutes. The midcoat composition is applied contiguously to the basecoat using a standard brush-applicator. The midcoat composition is allowed to form a layer over a period of five minutes, resulting in a film having two layers. The topcoat composition is applied contiguously to the layer formed from the midcoat composition using a standard brush-applicator. The topcoat composition is allowed to form a topcoat over a period of five minutes, providing a film having three layers. Example 8 30 A kit comprising two separate nail polish compositions is prepared. The compositions are a basecoat composition of Example 1 and a topcoat composition of Example 3. The basecoat composition is applied contiguously to mammalian nails using a standard brush-applicator. A basecoat is allowed to form over a period of five minutes. The topcoat composition is applied contiguously to the basecoat using a standard brush- applicator. The topcoat composition is allowed to form a topcoat over a five minute time period, resulting in a film having two layers.

Claims: 31 WHAT IS CLAIMED IS 1. A kit suitable for use as a nail polish for mammalian nails characterized b> (I) a basecoat composition characterized by (a) from about 0 1% to about 20%, by weight of the composition, of a water- msoluble film-forming polymer selected from the group consisting of polyurethanes, polyacryls, polymethacryls, urethane-acr\ 1 copohmers styrene-acryl copolymers, and mixtures thereof, and (b) a liquid diluent characterized by (i) from about 10% to about 90%. b\ weight of the composition, of a volatile organic solvent, and (ii) water, and (II) a topcoat composition characterized b (a) from about 0 1 % to about 40%, b\ weight of the composition of a watei - msoluble film-forming water-borne polvmer selected tiom the group consisting of polyurethanes, polyacryls, polvmethacryls. sty rene-acr l copolymers, siloxane-urethane copolymers, and mixtures thereof, and (b) a liquid diluent characterized by (i) from 0% to about 30%, by weight of the composition, of a volatile organic solvent, and (ii) water 2. A kit suitable for use as a nail polish for mammalian nails characterized b> (I) a basecoat composition characterized by (a) from about 0 1% to about 20%, by weight of the composition, of a water- insoluble film-forming polymer selected from the group consisting of polyurethanes. polyacryls. polymethacryls. urcthane-acrx l copolvmers styrene-acp, 1 copolymers. and mixtures thereof and (b) a liquid diluent characterized by (i) from about 10% to about 90%. by weight of the composition, of a volatile organic solvent, and (ii) water, and 32 (II) a topcoat composition characterized by a water-insoluble solvent-borne film- forming polymer selected from the group consisting of cellulosic poh mers polyurethanes, polyacryls, polymethacryls, silicone-acryl copoKmers polysiloxanes, and mixtures thereof 3. A kit suitable for use as a nail polish for mammalian nails characterized b\ (I) a basecoat composition characterized by a water-insoluble solvent-borne film- forming polymer selected from the group consisting of cellulosic polymers polyurethanes, polyacryls, polymethacryls, polysiloxanes. and mixtures thereof, and (II) a topcoat composition characterized b (a) from about 1 % to about 40%, by weight of the composition, of a water- lnsolublc film-forming water-borne polymer selected from the group consisting of polyurethanes, polyacryls, poh methacry ls, st\rene-acr\ l copolymers, siloxane-urethane copolymers, and mixtures thereof, and (b) a liquid diluent characterized by (i) from about 0% to about 30%. by weight of the composition, of a volatile organic solvent, and (ii) water 4 A kit according to any of the preceding claims wherein the polymer of the topcoat composition is a cross-linked polymer 5. A kit according to any of the preceding claims further characterized b\ a midcoat composition characterized by a liquid diluent and a water-insoluble solvent-borne film-forming polymer selected from the group consisting of cellulosic polymers, poKurethanes poKacryls. polymethacryls, polysiloxanes, and mixtures thereof 6 A kit according to any of the preceding claims wherein the polymer of the basecoat composition is a polyurethane 7 A kit according to any of the preceding claims wherein the polymer of the topcoat composition is a cellulosic polymer 33 8 A kit according to any of Claims 1 , 2, 3, 4. 5, or 6 wherein the poK mer of the topcoat composition is a polyacryl 9. A method of coating mammalian nails with a kit according to any of the preceding claims, wherein the method is characterized by the steps of (i) applying the basecoat composition contiguously to the nail, (ii) removing sufficient liquid diluent from the basecoat composition to form a substantially dry basecoat. (iii) optionally applying a midcoat composition characterized b\ a film-forming poK ei and a liquid diluent contiguously to the basecoat. (IV) removing sufficient liquid diluent from the midcoat composition to form a substantially dry midcoat. (v) applying the topcoat composition contiguously to the basecoat or midcoat. and (vi) removing sufficient liquid diluent from the topcoat composition to form a substantially dry topcoat

Inventors: ELLINGSON PETER CHRISTOPHER, FLYNN KATHERINE ELEANOR, GIRET MICHEL JONES, JONES STEVAN DAVID, SMITH EDWARD DEWEY III, ELLINGSON, PETER, CHRISTOPHER, FLYNN, KATHERINE, ELEANOR, GIRET, MICHEL, JONES, JONES, STEVAN, DAVID, SMITH, EDWARD, DEWEY, III
Applicants: PROCTER & GAMBLE, THE PROCTER & GAMBLE COMPANY
Application year: 1999
Main classification: A61K7
IPC codes: A61K8, A61Q3, C08L83