DIMENSIONALLY STABLE ELECTRODE FOR TREATING HARD-RESOLUBLE WASTE WATER

Abstract: An electrode for treating hard-dissoluble waste water requires high oxygen overvoltage, lower price and durability. Conventional electrode can not satisfy all of the above three conditions. The present invention provides an electrode capable of satisfying all of the above conditions comprising of novel substrate and novel electrode catalyst. The novel electrode catalyst is a three-element catalyst composed of the oxides of Sn-Pt-Ru, and the novel substrate is a ceramic Ti407. Such system satisfies durability, cost and electrode voltage characteristics.

Description: DIMENSIONA LY STABLE ELECTRODE FOR TREATING HARD-RESOLUBLE WASTE WATER Technical Field The present invention relates to a dimensionally stable electrode for treating hard-resoluble waste water. Backcrround Art Waste water such as industrial waste water that has many different properties and shapes, high concentration of organic compounds and sometimes strong colors has negative effects to the environment should it not be treated properly. Specifically, the hard-resoluble compounds are extremely slow to decompose because of its complicate molecular structure, but also nearly removable by conventional active slurry process, biochemical, chemical or physical method, or multi-processing thereof because of its poisonous property. Therefore, in the case of treating waste water containing hard-resoluble or harmful organic compounds by slurry processing, a proper pre-treatment technique capable of securing process stability, reducing the lord imposed on an aeration container, and increasing bioanalysis yield are essential. So far, Electrochemical or ozone oxidation method has been widely known as an effective method for treating such waste water. There are many patent applications with regard to the electrochemical method such as Korean Patent application titled "Multi-step electrolytic agglutination system (application number: 98-001790) , "Method for treating dyeing waste water and pigments waste water using electrolysis and heat-energy" (application number : 97- 020062, publication number : 98-001852), "Reagent for treating dyeing waste water using electrolysis" (application number : 96-022480, publication number : 98-001851) , "Apparatus for decoloring dyeing waste water" (application number : 96-018074, publication number : 97-074671), "Method for decoloring dyeing waste water using chroline compound and electrolysis" (application number : 96-014619, publication number 97-074670) , "carbon electrode using a ceramic binder" (application number : 97-033560) and so on. The electrochemical systems disclosed in the above applications comprise of anode (s) on which oxidation occurs and cathode (s) wherein reduction occurs. The anodes used for oxidation reaction can be divided into soluble anode and non-soluble anode. The soluble anode is inexpensive but it is hard to purify because second contamination occurs thereon in a large quantity. Most common non-soluble anode is titanium substrate coated with platinum- family oxide (s) . Electrodes for treating waste water requires higher oxygen overvoltage than chroline generating voltage. Since conventional electrodes have low chroline overvoltage, Cl- is easily oxidized to be chroline. The chroline easily reacts with the waste water to secondarily contaminate it. Furthermore, a catalyst for high oxygen overvoltage such as Ru, Pt and Ir is expensive. Especially, an electrode composed of platinum-system catalyst is subject to the following reaction (1) and therefore, its activity disappears. Ru02 (s) + 02 - Ru04 (sol) (1) Wherein, "s" represents solid state and "sol" represents the state of being gushed from the solution. When the Ru02 starts to gush, the electrode starts to be damaged, the titanium substrate is subjected to the corrosion and finally, holes occur thereon. Therefore, the life time of the electrode is extremely short. Incidently, when electrolytic container system stops, Pb02 electrode, which is the second most commonly used electrode, is reduced to be Pb by an instant reverse reaction. Such gushed Pb gives rise to another contaminatio . An electrochemical electrode requires the satisfaction of the following three conditions. (1) cost (2) voltage (3) life time The present invention provides for an electrode that satisfy the above mentioned three conditions. The oxides of Ru, Ir, Pt, Ti, Pb, etc. can be used as an electrochemical catalyst. However, because such substances are expensive, a substitute electrode is required. Sn can be considered as an electrode substance for treating waste water according to the present invention, because it is non-platinum type, relatively cheap and has higher oxygen generating voltage than chroline generating voltage . The two factors affecting the durability are (i) oxidation-resist property of a substrate and (ii) compatibility of an electrode. Titanium, a common substrate, is susceptible to be easy oxidation and reduced by oxygen and hydrogen respectively. Therefore, titanium oxide (TiO x ) having strong resistance to oxidation and reduction can be considered as a substitute of Ti . Herein, x is between 1.1 to 2, more preferred, between 1.1 to 1.9, and most preferred, between 1.5 to 1.8. Considering durability, an electrode catalyst requires higher oxygen overvoltage because platinum- family oxides are oxidized by oxygen to be dissolved. As such catalyst, there are Ti02 , Pt02 , carbon, Ru02, Sn02 and so on, each of which has good adhesiveness. With regard to voltage, the electrode catalyst substance having high oxygen overvoltage should be selected. Among conceivable substances, Sn02 is most preferable. If the content of Sn02 is rapidly increased, conductivity also rapidly increases. However, If the content of Sn02 is rapidly increased, at the same time, Sn02 is relatively easily oxidized to be gushed into an electrolyte . Therefore, considering the characteristics of each electrode catalyst, a two-element or three-element catalyst system is desirable. For example, a catalyst can be considerable which is based on Sn02 having relatively good durability, reasonable price and desirable voltage, and contains more than one additive element capable of intensifying durability. In case of two-element system of Ti02 and Sn02 , if content of Sn02 is over 90 mole%, oxygen overvoltage rapidly decreases and therefore, the durability of the electrode is deteriorated. With respect to conductivity alone, Pt02 can be considered but it has a problem of stability. Also, carbon has a problem in compatibility with metal elements. Disclosure of the Invention The object of the present invention is to provide an electrode having high oxygen overvoltage so as to treat waste water more effectively. To achieve the object of the present invention, an electrode is provided which comprising Sn02 as the main element, Ru02 lower than 10 mole% and Pt lower than 5 mole%, wherein said Sn02 is to control oxygen overvoltage and said Ru02 is to increase conductivity and durability. Best Mode for Carrying out the Invention The method for coating three-element electrode catalyst of Sn02-Ru02-Pt on Ti407 substrate is as follows. (a) Etching step This step is for removing organic and inorganic compounds on the substrate by primarily using 1N-HC1. (b) Washing step After etching, acids on the substrate are removed using pure water. (c) Dipping step The substrate is coated with an electrode catalyst by dipping the substrate into the electrode catalyst solution. (d) Incinerating step The substrate coated with the electrode catalyst is incinerated at a high temperature . (e) Quality checking step Quality check is performed on the coated electrode. Hereinafter, the present invention will be more explicitly described through the following examples. Example 1 (1) Ti407 substrate is prepared as follows. (a) A substrate was etched in IN-HC1 solution at 80 Celsius degree for 1 hour. (b) The etched substrate was washed with pure water. The surface of the substrate was sufficiently dried. (2) Electrode catalyst solution was prepared as follows. (a) H2PtCl6-6H20 as a pre-substance of Pt, RuCl4 as a pre-substance of Ru02 and SnCL4 as a pre-substance of Sn02 were prepared. (b) Each pre-substance was measured off so that the mole ratio of Pt : Ru02 : Sn02 was 10 : 10 : 80 respectively. (c) Such measured pre-substances i.e., SnCl4 , RuC14 and H2PtCl6 were put into isopropyl alcohol (IPA) solvent and then, subjecting the solution to ultra-sonic distribution . (3) Electrode coating step (a) The electrode substrate prepared by (1) was dipped into the solution prepared by (2) for 5 seconds and dried by far-infrared ray at 70 Celsius degrees for 10 minutes . (b) The electrode coated with electrode catalyst was incinerated at 480 Celsius degrees for 1 hour at room atmosphere. (c) After incineration, it was dried at atmosphere. (d) The above processes from a) to c) were repeated. (e) By repeating 5 times, the completed electrode was obtained. (4) Analysis of electrode. (a) Oxygen overvoltage was analyzed using potentionstat . (i) Oxygen overvoltage was detected using three- electrode analyzing system employing (i) the electrode obtained from (3) as a working electrode, (ii) carbon electrode as a counter electrode and (iii) saturated calomel electrode (SCE) as a auxiliary electrode. (ii) 1 Mole of H2S04 was used as electrolyte. (b) The life time was detected by an acceleration experiment . (i) The voltages according to time were detected under the condition of employing the electrode obtained from (3) as an anode, stainless steel as a cathode and 1 Mole H2S04 as an electrolyte respectively and imposing 20KA/m 2 of voltage. Life time is determined at the time when voltage increases . Example 2 (1) Substrate was prepared in the same way as the Example 1. (2) Electrode catalyst solution was prepared as follows. (a) The same procedure as the (2) -(I) of Example 1 was performed. (b) Each pre-substance was measured off so that the mole ratio of Pt : Ru02 : Sn02 was 10 : 10 : 80 respectively . (c) The same procedure as the (2) -(c) was performed. (3) Electrode coating step was perfomed in the same way as (3) of Example 1. (4) The same analysis process as (4) of Example 1 was performed. Example 3 (1) The pre-treatment was done in the same way as (1) of Example 1. (2) An electrode catalyst was prepared as follows. (a) SnCl4 and RuCl4 were prepared as pre-substance of Sn02 and Ru02. (b) The pre-substances are measured off so that the weight ratio of Sn02 : Ru02 was 20 : 80 respectively. (c) The measured SnCl4 and RuCl4 were immersed into IPA solvent and then subject to ultra-sonic distribution. (3) Electrode coating step (a) The electrode was washed and dipped in the solution prepared in step (2) for 5 seconds. Thereafter, the electrode was dried at atmosphere level for 10 minutes. (b) The dried electrode was incinerated at 480 Celsius degrees for 10 minutes. (c) Thereafter, the electrode was again washed with pure water and dried. Then, the above-described processes from (a) to (c) were identically repeated. After repeating the steps 5 times, a completed electrode was obtained. (4) Analysis of the electrode obtained from (3) was performed in the same way as (4) of Example 1. Example 4 (1) A substrate made of titanum was prepared and pre- treated in the same way as (1) of Example 1. (2) An electrode catalyst solution was prepared in the same way as (2) of Example 1. (3) Electrode coating process was completed in the same way as (3) of Example 1. (4) Electrode analysis was performed in the same way as (4) of Example 1. Comparative example (1) A substrate made of titanium was pre -treated in the same way as (1) of Example 1. (2) An electrode catalyst solution was prepared as follows. (a) RuCl4 and TPT were prepared as pre-substances of Ru02 and Ti02 , respectively. (b) RuCl4 and TPT were measured off so that the weight ratio of Ru02 : Ti02 was 50:50. (c) The RuCl4 measured in step (b) was added into IPA(iso propyl alcohol) of same weight as the sum of RuCl4 and TPT mesured step (b) . Thereafter, the solution was subject to ultra-sonic distribution for 1 hour. (d) The resultant solution was stirred for 1 hour while TPT was added. (e) After further adding IPA of the volume at 50 times as that of the solution of (d) thereto, the solution was stirred for 1 day. (3) Electrode coating process was performed in the same way of (3) of Example 1. (4) Analysis of the electrode was conducted in the same way as (4) of Example 1. The results obtained from Examples and Comparision are as follows.

Claims: WHAT IS CLAIMED IS: 1. An electrode for treating waste water comprising a substrate and an electrode catalyst coated on the surface of said substrate wherein, said electrode catalyst is a multi-element catalyst comprising at least Ru02 and Sn02. 2. The electrode according to claim 1, wherein said electrode catalyst further comprises Pt . 3. The electrode according to Claim 2, wherein the ratio of said Pt : Ru02 : Sn02 is 0-20 : 10-20 : 80 with respect to mole weight % . 4. The electrdoe according to Claim 1, said substrate is made of Ti407.

Inventors: KIM HEE JUNG, KIM, HEE, JUNG
Applicants: KYUNGWON ENTERPRISE CO LTD, KYUNGWON ENTERPRISE CO., LTD.
Application year: 1999
Main classification: C02F1
IPC codes: C02F1, C25B11