Optically transparent hydrogels and processes for their production

Abstract: The invention provides hydrogels for use in the production of biomedical devices. In particular, the invention provides hydrogels formed from siloxane prepolymers and a hydrophilic monomer, which hydrogels are optically transparent.

Description: Field of the Invention The invention relates to hydrogels for use in the production of biomedical devices. In particular, the invention provides hydrogels formed from siloxane prepolymers and a hydrophilic monomer, which hydrogels are optically transparent. Background of the Invention The use of hydrogels for the manufacture of biomedical devices is known. Hydrogels that are copolymers of siloxane prepolymers and hydrophilic monomers offer certain advantages in comparison with conventional hydrogels. However, it is difficult to produce optically transparent, homogeneous hydrogels from these prepolymers and monomers making the use of the hydrogels limited. Known methods for making homogeneous hydrogels from siloxane prepolymers include using diluents to compatabilize the siloxane with the hydrophilic monomer and using siloxanes into which hydrophilic groups are incorporated. However, the use of diluents is disadvantageous because of their volatility and their use may result in polymers of inferior quality. Incorporation of hydrophilic groups is disadvantageous in that it requires the use of complicated syntheses and the resulting polymer may not be optically transparent. Therefore, a need exists for a method of polymerizing siloxane prepolymers and hydrophilic monomers that overcome these disadvantages. Description of the Invention and Preferred Embodiments It is a discovery of the invention that homogeneous, optically transparent hydrogels can be formed from the polymerization of siloxane prepolymers and/or monomers with a hydrophilic monomer without incorporation of hydrophilic groups into the siloxane and with a reduction in the amount of diluents needed or, in some cases, without the use of diluents. The hydrogels of the invention are useful in the manufacture of biomedical devices, meaning devices designed to be used while in or on either or both human tissue or fluid. Examples of such devices include, without limitation, stents, implants, catheters, and ophthalmic lenses. In a preferred embodiment, the biomedical device is an ophthalmic lens including, without limitation, contact or intraocular lenses. More preferably, the device is a contact lens. According to the present invention there is provided a process for producing a hydrogel, as defined in the accompanying claims and a hydrogel as defined in the accompanying claims. The "hydrophobic siloxane prepolymer" and "hydrophobic siloxane monomer" used in the present invention is a siloxane prepolymer or siloxane monomer, respectively, that does not have an amount of hydrophilic groups, such as a hydroxyl group, incorporated into the main chain or a side chain to allow for blends to be made of it with a hydrophilic monomer absent the use of high levels of diluent. The hydrophobic siloxane prepolymers are of the formula: wherein R 1 is hydrogen or an alkyl of 1 to 5 carbon atoms, R 2 is an alkyl of 1 to 5 carbon atoms, n = 1 to 12, and z = 1 to 500. Preferably, the prepolymer is a macromer, such as: wherein n and m are each independently 0 to 500 and (n + m) = 10 to 500, R 4 , R 6 , R 7 , R 8 , and R 9 are each independently a monovalent alkyl of 1 to 5 carbon atoms, or aryl group that may be further substituted with alcohol, ester, amine, ketone, carboxylic acid, or ether groups, and R 3 , R 5 , and R 10 are each independently a monovalent alkyl or 1 to 5 carbon atoms or aryl group that may be further substituted with alcohol, ester, amine, ketone, carboxylic acid or ether groups or have the structure: providing that at least one of R 3 , R 5 , and R 10 are according to this structure wherein R 11 is a divalent alkyl group of 1 to 5 carbon atoms, R 12 and R 13 are independently H, a monovalent alkyl of 1 to 5 carbon atoms or aryl group that may be further substituted with an alcohol, ester, amine, ketone, carboxylic acid or ether group, or have the structure: wherein R 16 is H or a monovalent polymerizable group containing acryloyl, methacryloyl, styryl, vinyl, allyl, or N-vinyl lactam; R 18 is H, a monovalent alkyl of 1 to 5 carbon atoms or aryl group that can be further substituted with alcohol, ester, amine, ketone, carboxylic acid, or ether groups, or a polymerizable group containing acrylate, methacrylate, styryl, vinyl, allyl or N-vinyl lactam; R 14 , R 15 , and R 16 are independently H, or a monovalent alkyl of 1 to 5 carbon atoms or aryl that can be further substituted with alcohol, ester, amine, ketone, carboxylic acid or ether groups, or R 14 and R 17 , or R 17 and R 15 can be bonded to form a ring structure, providing that at least one of the Structure B groups on the monomer contains polymerizable groups. Preparation of such macromers is known in the art. Preferred hydrophobic prepolymers are α, ω -bismethacryloxypropyl macromers. More preferred is α, ω -bismethacryloxypropyl polydimethylsiloxane. Other hydrophilic prepolymers that can be used include linear or branched polymers or copolymers made from hydrophobic monomers such as 3-methacryloxypropylbis(trimethylsiloxy)silane, said prepolymers having polymerizable functional groups such as methacrylate or styryl. Preparation of such prepolymers is described in U.S. Patents 5,010,141; 5,057,578; 5,314,960; 5,371,147 and 5,336,797. In the process of the invention, the prepolymer may be used alone or in combination with a hydrophobic siloxane monomer. The hydrophobic siloxane monomers are of the formula: wherein R 19 and R 20 are each independently hydrogen or methyl, R 21 , R 22 , and R 23 are each independently a monovalent alkyl of 1 to 5 carbon atoms or aryl, j = 1 to 10 and k = 0 to 3. Examples of useful siloxane monomers include, without limitation, polysiloxyanylalkyl(meth)acrylates, preferably, 3-methacryloxypropylbis(trimethylsiloxy)silane or 3-methacryloxypropylbis(trimethylsiloxy)methylsilane. Hydrophobic siloxane monomers useful in the invention are commercially available or may be synthesized through known methods. In the process of the invention, the siloxane prepolymer alone, or in combination with the siloxane monomer, is polymerized with a silylated hydrophilic monomer. The silylated monomer used is of the formula; wherein R 24 is hydrogen or methyl, R 25 is hydrogen or methyl, and R 26 is a monoalkyl, preferably methyl. More preferably, the silylated monomer is a polyalkylsilyl ether of a hydroxyalkyl(meth)acrylamide. Most preferably, the silylated monomer is 2-hydroxymethacrylamide trimethylsilyl ether. The silylated monomer may be prepared by silylating the hydroxyl groups of a hydrophilic monomer by any known method. For example, the hydroxyl groups may be reacted with a silylating agent such as a trialkylsilyl halogenide, hexamethyldisilizane, trimethylsilyldiethylamine, or the like. Solvents and catalysts useful in the silylation, as well as reaction conditions, are well known in the art. The siloxane prepolymer, alone or in combination with a siloxane monomer, are polymerized with the silylated hydrophilic monomer by any convenient method, including without limitation, heat, ultraviolet light, radiation, polymerization, or a combination thereof. Preferably, the polymerization is carried out in the presence of a suitable initiator present in an amount of about 0.01 to about 2.0 weight percent based on the weight of the reactants. More preferably, the polymerization is carried out UV light using a UV polymerization initiator. The preferred UV polymerization initiator is 2-hydroxy-2-methyl-1-phenyl-propan-1-one. The amount of siloxane prepolymer used is about 0 to about 90 weight percent, preferably about 5 to about 70 weight percent, based on the weight of the polymerizable components. The amount of siloxane monomer used is from about 0 to about 70 weight percent, preferably from about 0 to about 40 weight percent. The amount of silylated monomer used is from about 2 to about 60 weight percent, preferably from about 15 to about 50 weight percent. After polymerization is completed to the desired degree, the resulting polymer may be washed in an organic solvent to remove unreacted reactants. Suitable solvents include, without limitation, hexane, ethanol, isopropyl alcohol, n-and t-butyl alcohol, n-amyl alcohol, n-hexyl alcohol, as well as chlorinated solvents and the like, and mixtures thereof. The polymer then may be desilylated by hydrolyzing to eliminate the silyl groups and to regenerate the hydroxyl group. The hydrolysis may be carried out in any suitable hydrolyzing agent. Preferably, hydrolysis is carried out by placing the lenses in a borate-buffered saline solution. Optionally, an acid or base may be used in the hydrolyzing agent to speed the hydrolysis. One ordinarily skilled in the art will recognize that any number of a wide variety of additional components may be added to the mixture to be polymerized. Examples of such additives include, without limitation, ultra-violet absorbers, antioxidants, tints, and the like. Any molding process may be used to form lenses from the hydrogels of the invention. For example, the siloxane prepolymer, silylated hydrophilic monomer and, optionally, the hydrophobic monomer may be blended together along with a polymerization initiator and the blend then placed into a lens mold. After polymerization is completed, the lens undergoes desilylation. The invention will be clarified further by a consideration of the following, non-limiting examples. Examples Example 1 214.2 g methacryloyl chloride were added dropwise to a solution of 128 g methanol, 249 g potassium carbonate, and 122.2 g ethanolamine in a three-necked flask cooling to between 5 and 15° C in an ice bath. Addition took approximately 3 hours after which the reaction mixture was left to stir for approximately 2 days after removal of the ice bath. The reaction mixture was poured into CH 2 Cl 2 and vacuum filtered to remove all solids, which solids were rinsed with CH 2 Cl 2 . The liquid was inhibited with 100 ppm hydroquinone monomethyl ether and the solvent removed by rotary evaporation. Residual oil was distilled under reduced pressure in a distilling flask equipped with an air ebulator. after addition of 150 ppm CuCl. 56.62 g of hydroxyethyl methacrylamide was recovered as a light yellow liquid at 0.5 mm Hg and 125 to 135° C. Air was bubbled through the distilled product. 23 g trimethylsilyl chloride were added dropwise over an approximately 2 hour period to a solution of 25.3 g of the above product, 30.6 g triethylamine and 75 ml CH 2 Cl 2 in a three-necked flask equipped with a drying tube and a magnetic stirrer. The mixture was kept at room temperature. After the addition, the reaction mixture was heated to 40° C and stirred for approximately 5 hours. The mixture was then filtered to remove salt and the residual liquid was then rotovapped until the weight ceased to fall. The product was distilled under reduced pressure after addition of 500 ppm HQMME. 2-hydroxyethylmethacrylamide trimethylsilyl ether ("TMS-HMA") was collected as a clear liquid at 95 to 105° C and 0.25 mm Hg in a yield of 42 percent. Example 2 A blend was made of 20 parts of α,ω-bismethacryloxypropyl polydimethylsiloxane (5,000 average molecular wt), 45 parts of the TMS-HMA of Example 1 and 34 parts methacryloxypropyl tri(trimethylsiloxy)silane ("TRIS"), 1 part DAROCUR™ 1173, a photoinitiator that is 2-hydroxy-2-methyl-1-phenylproan-1-one, and 11 parts t-butanol. The blend was placed in polypropylene lens molds and irradiated for 30 min with UV light, then released in ethanol, and transferred into a borate buffered saline to produce soft, optically clear, oxygen permeable contact lenses.

Claims: A process for producing a hydrogel comprising: a) polymerizing a hydrophobic siloxane prepolymer of formula I wherein R 1 is hydrogen or an alkyl of 1 to 5 carbon atoms, R 2 is an alkyl of 1 to 5 carbon atoms, n = 1 to 12 and z = 1 to 500; with a silylated hydrophilic monomer of the formula III wherein R 24 is hydrogen or methyl, R 25 is hydrogen or methyl and R 26 is a monoalkyl; and b) hydrolyzing the resulting polymer. The process of claim 1 wherein the hydrophobic siloxane prepolymer and the silylated hydrophilic monomer are polymerized with a hydrophobic siloxane monomer of the formula II wherein R 19 and R 20 are each independently hydrogen or methyl, R 21 , R 22 and R 23 are each independently a monovalent alkyl of 1 to 5 carbon atoms or aryl, j = 1 to 10 and k = 0 to 2. The process of claim 1 or 2 wherein the hydrophobic siloxane monomer is α,ω-bismethacryloxypropyl polydimethylsiloxane and the silylated hydrophilic monomer is 2-hydroxymethacrylamide trimethylsilyl ether. The process of any one of claims 1 to 3 wherein the hydrophobic siloxane prepolymer is present is an amount of 0 to 90 weight percent and the silylated hydrophilic monomer is present in an amount of 2 to 60 weight percent. A hydrogel comprising the hydrolysed product of the reaction of a hydrophobic siloxane prepolymer of the formula I wherein R 1 is hydrogen or an alkyl of 1 to 5 carbon atoms, R 2 is an alkyl of 1 to 5 carbon atoms, n = 1 to 12 and z = 1 to 500 with a silylated hydrophilic monomer of the formula III. wherein R 24 is hydrogen or methyl, R 25 is hydrogen or methyl and R 26 is a monoalkyl. The hydrogel of claim 5 further comprising a hydrophobic siloxane monomer of the formula II wherein R 19 and R 20 are each independently hydrogen or methyl, R 21 , R 22 and R 23 are each independently a monovalent alkyl of 1 to 5 carbon atoms or aryl, j = 1 to 10 and k = 0 to 2. The hydrogel of claim 5 or 6 wherein the hydrophobic siloxane prepolymer is α,ω-bismethacryloxypropyl polydimethylsiloxane and the silylated hydrophilic monomer is 2-hydroxymethacrylamide trimethylsilyl ether. The hydrogel of any of claims 5 to 7 wherein the hydrophobic siloxane prepolymer is present in an amount of 0 to 90 weight percent and the silylated hydrophilic monomer is present in an amount of 2 to 60 weight percent. The hydrogel of claim 6 wherein the hydrophobic siloxane monomer is 3-methacryloxypropyltris(trimethylsiloxy)silane. The process of any of claims 2 to 4 wherein the hydrophobic siloxane monomer is 3-methacryloxypropyltris(trimethylsiloxy)silane.

Inventors: FRUZZETTI GIANCARLO, MOLOCK FRANK, VANDERLAAN DOUGLAS G, FRUZZETTI, GIANCARLO, MOLOCK, FRANK, VANDERLAAN, DOUGLAS G.
Applicants: JOHNSON & JOHNSON VISION PROD, JOHNSON & JOHNSON VISION PRODUCTS, INC.
Application year: 1999
Main classification: C08F230
IPC codes: C08L83, C08F8, C08F230, C08F220, C08F290, C08J3