A process for the manufacture of hydrophobic paper or hydrophobic board, and a sizing composition

Abstract: The invention relates to a process for the manufacture of hydrophobic paper or board by using rosin sizing, an organic complexing agent being used together with the rosin size. The invention also relates to a sizing composition.

Description: The present invention relates to a process for the manufacture of hydrophobic paper or hydrophobic board by using rosin sizing. The invention also relates to a sizing composition which contains rosin size. Rosin and rosin-based sizes have long been used for the sizing of board and paper when the stock is acidic or almost neutral. Size is used by adding it to the fiber stock from which a web is later formed on the wire. The purpose of the use of size is to increase the hydrophobicity of the paper or board. Rosin sizing is based on the forming of electrostatic bonds between the size and the cellulose or other fibers or solids in the stock or the paper web. With the present-day reaction products of anhydrides and rosinous substances a better sizing result is obtained than with products which contain only rosinous substances. Such reaction products are called reinforced rosin sizes. In general, an aqueous dispersion is formed of the sizes in order to facilitate dosing. Stable dispersions of rosin or rosin-based products are well known. Rosin is a solid substance present in the pitch of pine trees, Its principal component is abietic acid, which can react with fumaric acid, maleic acid or its anhydride, whereby the active agent of reinforced sizes is formed. These reinforced sizes can be treated further with formaldehyde and alcohols. The preparation of rosin sizes is generally known technology. The preparation and formulation of a rosin size is described in, for example, patent FI-C-77884. To add an complexing agent to a paper pulp is known from EP-A-0 073 872. Rosin sizes are in general stabilized with substances which form a shielding colloid around the resin particles. Usually there is used for this purpose a modified starch or natural polymers or synthetic polymers, such as polyvinyl alcohols, polyvinyl pyrrolidone or cellulose derivatives, such as carboxymethyl cellulose. The use of rosin size stabilization agents is generally known technology. Aluminum salts, which may be of any type which is commonly known to be usable for the sizing and hydrophobification of cellulose and other fibers, such as aluminum sulfate, aluminum chloride, polyaluminum chloride, polyaluminum sulfate, and mixtures thereof, are essential for the use and performance of a rosin size. It is generally known that the amount of alum required in rosin sizing is approx. 1.5 times that of the rosinous substance (W.F. Reynolds, The Sizing of Paper, second edition, 1989, pages 1-31), and the highest possible cationic charge is obtained when 1-1.5 equivalents of the Al 3- ion are neutralized with the OH ion. In this case the pH is 4-5. It is known that Ca 2- and Mg 2+ ions weaken the sizing effect by decreasing the negative charge of the rosin size and by forming disadvantageous precipitates. Problems appear in particular when the pulps are prepared in hard water or when calcium carbonate is used as a filler. Calcium carbonate buffers the pulp within a pH range of 7-8. Efforts have been made to improve the performance of rosin size in this environment by using dispersion sizes of very small particle size. By means thereof, rosin sizes can be caused to react with aluminum only in the drying section, where water no longer serves as the continuous phase and the size is no longer in contact with carbonate. On the other hand, efforts have been made to increase the interaction between aluminum and rosin size by dosing them at the same location into the short cycle of diluted pulp. The quality properties of board for the packaging of liquids include not only hydrophobicity of the board, which is generally defined as Cobb numbers, but also resistance to the penetration of lactic acid from the edge of the board (lactic acid REP) and resistance to the penetration of hydrogen peroxide (peroxide REP). The numbers illustrate the penetration of the said solutions from the board edge towards its cross-sectional area. Resistance to peroxide is necessary since the board is treated in a hot hydrogen peroxide bath before the manufacture of packaging. Resistance to lactic acid is necessary or the packaging being resistant to the milk and other liquid food products to be stored therein. In general, in order to achieve effective sizing, an AKD (alkyl ketene dimer) size is also used in the manufacture of liquid packaging board. An AKD size which can be used together with a rosin size is usually an aqueous dispersion. The concentration of AKD in the products may be 0.5-30 % by weight. In general there are used for the formulation of AKD various starches, which are generally cationated either with quaternary amines, in which case the starch retains its cationic charge even in alkaline conditions, or with primary, secondary or tertiary amines, the charge of which is dependent on the pH. The amount of starch may be 0.1-10 times the proportion of AKD. In general there are used for the dispersing of an AKD wax various anionic compounds, such as lignosulfates, aliphatic or aromatic sulfonates, nonionic surfactants such as fatty acid or fatty alcohol ethoxylates, or cationic surfactants such as fatty acid amines or imidazolines. It is also possible to use, for the stabilization of an AKD dispersion, polymers such as polyethylene imine, polyepiamine, polydimethyldiallyl or dicyandiamide compounds, polyacrylamide or polyacrylic acid and its salts. It is generally known that the amount of stabilization chemicals is 1-200 % by weight of the amount of AKD. By the use of polymers it is possible not only to improve the stability of the product but also to fect the performance of the product in paper or board. The adding of stabilizing chemicals is prior art commonly used in the formulation of AKD products. It is generally known that rosin sizing is used specifically for affecting the peroxide resistance of board, whereas alkyl ketene dimer (AKD) primarily affects its lactic acid resistance. AKD size can be dosed to the pulp in the board machine before, after or simultaneously with resin size, depending on the manner in which the board machine is run. The dosing order does not affect the performance of the invention. It has been observed, surprisingly, that peroxide resistance specifically derived from rosin sizing can be increased by using complexing agents which are dosed together with the rosin size or are incorporated into the product. Complexing agents suitable for this purpose include agents which react slowly with aluminum compounds and rapidly with alkaline earth metal ions. According to the invention there is thus provided a process for the manufacture of hydrophobic paper or board by using rosin sizing, the process being characterized in that an organic complexing agent is used together with a rosin size in on amount of 0.1-20% by weight of the active ingredient of the rosin size, and in that in addition to the rosin size there is used an other hydrophobicity-enhancing agent, which is an alkyl ketene dimer size. The term chelating agent is also used for complexing agents. According to the invention, the organic complexing agent can be incorporated into the rosin size or it can be dosed at the same location in the paper or board machine as the rosin size. The process according to the invention is especially suitable for sizing together with an aluminum compound, such as aluminum sulfate, aluminum chloride, polyaluminum chloride, polyaluminum sulfate or mixtures of these. Suitable complexing agents which can be used in accordance with the invention include a) aminopolycarboxylic acids b) N-bis- or tris-[(1,2-dicarboxylethoxy)ethyl]amines and c) phosphonic acids. The complexing agents cited above may be in the form of an acid or a salt. Suitable salts include alkali metal salts and ammonium salt. Sodium and potassium salts are preferred salts. Preferred complexing agents of group a) include amino polycarboxylic acids having the following general Formula I. where A is -CH 2 COOH, B is -CH 2 COOH or -CH 2 CH 2 OH, x is 0-6, preferably 0-3, y is 0-6, preferably 0-2, a is 2-10, preferably 2-4, and b is 2-10, preferably 2-6. Especially preferable compounds according to Formula I include ethylene diamine tetra-acetic acid, i.e. EDTA (B=A, x=0, b=2 and y=1), diethylene triamine penta-acetic acid, i.e. DTPA (B=A, x=1, a=2, b= 2 and y=1), and nitrilotriacetic acid, i.e. NTA (B=A, x=0 and y=0). Preferred complexing agents of group b) include N-bis- or tris-[(1,2-dicarboxylethoxy)ethyl]amines having the general Formula II where R is hydrogen, an alkyl group having 1-30 carbon atoms, an alkyl group having 1-30 carbon atoms and additionally 1-10 carboxylic acid groups, an alkyl group having 1-30 carbon atoms and additionally 1-10 carboxylic acid ester groups, a (poly)ethoxylated hydrocarbon group having 1-20 ethoxyl groups, or a carboxylic acid amide group having 1-30 carbon atoms, in which case the N-R bond is an amide bond. Especially preferable complexing agents in Formula II include the following compounds according to Formulae A, B and C: A = N-bis[(1,2-dicarboxylethoxy)ethyl]amine (hereinafter the acronym BCEEA will be used) B = N-bis[(1,2-dicarboxylethoxy)ethyl]aspartic acid (hereinafter the acronym BCEEAA will be used) C = N-tris[(1,2-dicarboxylethoxy)ethyl]amine (hereinafter the acronym TCEEA will be used) These complexing agents A, B and C and their preparation have been described in patent application FI-962261. It is also possible to use mixtures of compounds A and B. Preferred complexing agents of group c include phosphonic acids having the general Formula III where R 1 is hydrogen, a lower alkyl such as -CH 3 or -(CH 2 ) n -CH 3 , an amino group -NH 2 , hydroxy methyl -CH 2 OH, a lower carboxylic acid group -(CH 2 ) n -COOH, a lower alkyl phosphonic acid group -(CH 2 ) n -PO 3 H 2 , or a group having the formula R 2 is hydrogen, hydroxyl -OH, a phosphonic acid group -PO 3 H 2 , a lower carboxylic acid group -(CH 2 ) n -COOH or a group having the formula or R 3 is hydrogen, hydroxyl -OH, an amino group -NH 2 , a lower alkyl such as -CH 3 or -(CH 2 ) n -CH 3 , a lower carboxylic acid group -(CH 2 ) n -COOH or a group having the formula -NH-(CH 2 ) n -PO 3 H 2 -NH-CH 2 -COOH or or n is 0-6, preferably 0-3. Complexing agents or their mixtures can be used in their acid forms or as their salts, as stated above. If the complexing agents are used in a salt form, the salt is not of substantial importance for the performance of the invention. The amount of the organic complexing agent is 0.1-20 % by weight, preferably 1-10 % by weight, of the amount of the active ingredient of the rosin size. According to the invention there is in addition to rosin size, used another agent which enhances hydrophobicity, which agent is alkyl ketene dimer size (AKD size). This agent can be incorporated into the rosin size or it can be added together with the rosin size or it can be dosed in the paper or board machine at a different location than the rosin size. According to the invention there is also provided a sizing composition which contains rosin size and an organic complexing agent incorporated therein in an amount of 0.1-20% by weight of the active ingredient of the rosin size, and additionally another hydrophobicity-enhancing agent which is an alkyl ketene dimer size, incorporated into the rosin size. The suitable complexing agents have been defined above. The said sizing composition is preferably in the form of a dispersion. The invention additionally relates to the use of the organic complexing agent defined above together with a rosin size and an alkyl ketene dimer size in the manufacture of hydrophobic paper or board. The essential idea of the invention is that the organic complexing agent is used together with a rosin size, incorporated into it or dosed at the same location in the paper or board machine as the rosin size, in which case the performance of the substance is targeted close to the formation of a rosin-Al reaction product. If the said substances were dosed directly into the circulation water, their concentration should be so high that it would disturb the rest of the operation of the machine. When the complexing agent is dosed together with the rosin size, its preferred amount is 0.01-1 kg per one metric ton of board or paper. In this case the concentration of the complexing agent in the product is 0.1-20 % by weight of the active ingredient of the rosin size. The process according to the invention is suited for use for chemical pulps, mechanical pulps and chemimechanical pulps, and mixtures of these. The invention is described below with the help of an example. The percentages are percentages by weight, unless otherwise indicated. Example For a sheet test, which was performed according to the instructions by Scan-C 26:76, there were used a chemithermomechanical pulp (CTMP) 50 % and a chemical softwood pulp 50 %. The mixture was ground to a Schopper number of 38°. Cooked starch was added to the mixture in an amount of 1 kg/t. The dry matter content of the stock was set at 0.3 %. The chemicals were dosed in the following order: calcium chloride, alum 1 kg/t, AKD size 2 kg/t, rosin size 3.5 kg/t, complexing agent, sodium sulfate, alum 2 kg/t, cationic starch 5 kg/t. The complexing agent was contained in the rosin size dispersion. In the final product the pH was approx. 6. Complexing Agent 1, which contains BCEEA and BCEEAA at a molar ratio of 2:3, was used in the tests. The grammage of the sheets was 138 g/m 2 . Calcium chloride was added to the stock before the adding of the first alum batch and sodium sulfate was added after the adding of the rosin size, in accordance with Table 1. Determination of peroxide REP: Tape-coated paper strips (2.5 cm x 7.5 cm), the edges of which were left free, were immersed for the duration of 10 min in a 70 °C hydrogen peroxide solution having a concentration of 30 %. The strips were weighed and the amount of penetrated liquid per cross-sectional area of the strip was measured. Determination of lactic acid REP: Tape-coated paper strips (4.5 cm x 12 cm), the edges of which were left free, were immersed for the duration of 1 hours in a 25 °C lactic acid solution having a concentration of 1 %. The strips were weighed and the amount of penetrated liquid per cross-sectional surface of the strip was measured. Test Compl. agent 1 Na 2 SO 4 CaCl 2 H 2 O 2 REP 10 min Lactic acid REP 1h kg/t kg/t kg/t kg/m 2 kg/m 2 1 0 0 0 2.52 0.50 2 0.2 0 0 1.03 0.42 3 0 3 0 2.24 0.48 4 0.2 3 0 1.06 0.46 5 0 3 3 2.33 0.55 6 0.2 3 3 1.09 0.55 The test results show that Complexing Agent 1 (tests 2, 4 and 6) considerably improves specifically the peroxide solution penetration, dependent on rosin sizing, inwards from the edge of board. The adding of sulfate improves the result without a complexing agent but disturbs somewhat the action of the complexing agent. The adding of calcium degrades the result.

Claims: A process for the manufacture of hydrophobic paper or board by using rosin sizing, characterized in that an organic complexing agent is used together with a rosin size in an amount of 0.1-20% by weight of the active ingredient of the rosin size, and in that in addition to the rosin size there is used another hydrophobicity-enhancing agent, which is an alkyl ketene dimer size. A process according to Claim 1, characterized in that the organic complexing agent is incorporated into the rosin size or is dosed at the same location in the paper or board machine as the rosin size. A process according to Claim 1 or 2, characterized in that an aluminum compound is used for sizing. A process according to any of the above claims, characterized in that the organic complexing agent is a) aminopolycarboxylic acid, b) N-bis- or tris-[(1,2-dicarboxylethoxy)ethyl]amine or c) phosphonic acid. A process according to Claim 4, characterized in that the organic complexing agent of group a) is diethylene triamine penta-acetic acid (DTPA), ethylene diamine tetra-acetic acid (EDTA) or nitrilotriacetic acid (NTA), or a salt thereof or a mixture thereof, and the organic complexing agent of group b) is N-bis[(1,2-dicarboxylethoxy)ethyl]amine (BCEEA), N-bis[(1,2-dicarboxylethoxy)ethyl]aspartic acid (BCEEAA) or N-tris[(1,2-dicarboxylethoxy)ethyl]amine (TCEEA), or a salt thereof or a mixture thereof. A process according to any of the above claims, characterized in that the amount of the organic complexing agent is 1-10 % by weight of the active ingredient of the rosin size. A process according to any of the above claims, characterized in that the alkyl ketene dimer size is incorporated into the rosin size or is added together with the roin size or is dosed at a different location in the paper or board machine than the rosin size. A sizing composition which contains a rosin size and an organic complexing agent incorporated therein in an amount of 0.1-20% by weight of the active ingredient of the rosin size, and additionally another hydrophobicity-enhancing agent, which is an alkyl ketene dimer size, incorporated into the rosin size. A composition according to Claim 8, characterized in that it is in the form of a dispersion. A composition according to Claim 8 or 9, characterized in that the organic complexing agent is an organic complexing agent defined in Claim 4 or 5. Use of an organic complexing agent together with a rosin size and another hydrophobicity-enhancing agent, which is an alkyl ketene dimer size, in the manufacture of hydrophobic paper or board, the amount of the complexing agent being 0.1-20% by weight of the active ingredient of the rosin size. Use according to Claim 11, characterized in that the organic complexing agent is a complexing agent defined in Claim 4 or 5.

Inventors: JUPPO ARI, PAREN AARTO, JUPPO, ARI, PAREN, AARTO
Applicants: KEMIRA OYJ
Application year: 1999
Main classification: D21H17
IPC codes: D21H17, D21H21