Manganese-containing catalyst for lower alkane oxidative dehydrogenation and a process for producing olefins

Abstract: A catalyst of formula (1): Mn α E 1 β E 2 γ O x wherein E 1 is at least one element selected from P, As, Sb, B, S, Se, Te, F, Cl, Br, I, Nb, Ta, W, Re and Cu; E 2 is at least one element selected from Cr, Fe, Co, Ni, Ag, Au, Zn, Tl, Sn, Pb, Bi, Li, Na, K, Rb, Cs, Mg, Ca, Sr, Ba, Y, La, Ce, Nd and Sm; α = 1, β = 0.01-10, γ = 0-5, and x is a numerical value determined by the oxidation states of the elements other than oxygen.

Description: [Technical field to which the invention belongs] This invention relates to lower alkane oxidative dehydrogenation catalysts and a production process of olefins using said catalysts. More specifically, the invention relates to the catalysts which are suitable for use in vapor phase oxidative dehydrogenation of C 2 -C 5 lower alkanes (hereinafter occasionally referred to simply as "lower alkanes") in the presence of molecular oxygen to produce corresponding olefins, and a process for oxydizing and dehydrogenating lower alkanes with molecular oxygen to produce corresponding olefins at high yields, with the use of said catalysts. The invention also relates to a process for producing, from the olefins which have been obtained through vapor phase oxidative dehydrogenation of C 2 -C 5 lower alkanes in the presence of molecular oxygen, the corresponding unsaturated aldehydes and/or unsaturated carboxylic acids. [Prior art] As a production process for lower olefins, in particular, propylene and isobutene, simple dehydrogenation process of lower alkanes is recently reduced to industrial practice. However, this process is subject to an essential problem that it is incapable of giving high conversion due to the equilibrium limitation and furthermore requires high temperatures. Still in addition, deterioration of the catalyst within a short period is inavoidable in said process, which necessitates frequent regeneration of the catalyst using a switch converter or the like. In consequence, plant construction costs and utility costs for running the process are high and, depending on the conditions of location, it is unprofitable and its industrial application is restricted. Whereas, attempts to produce lower olefins from lower alkanes through oxidative dehydrogenation which is free from the limitation by equlibrium have been made since long, and various catalyst systems therefor have been proposed. Among those known, there are Co-Mo oxide catalyst (USP 4,131,631), V-Mg oxide catalyst (USP 4,777,319), Ni-Mo oxide catalyst (EP 379, 433 A1) CeO 2 /CeF 3 catalyst (CN 1,073,893A), Mg-Mo catalyst [Neftekhimiya (1990), 30(2) 207-10], V 2 O 5 /Nb 2 O 5 catalyst [ J . Chem. Commun. (1991) (8) 558-9], rare earth vanadates catalyst [ Catal. Lett. (1996), 37, (3,4), 241-6] and B 2 O 3 /Al 2 O 3 catalyst [ACS Symp. Ser. (1996), 638 (Heterogeneous Hydrocarbon Oxidation) 155-169). Those known catalysts, however, invariably show very low level oxidative dehydrogenation performance, the property of the prime importance, and are far short of industrial practice. Japanese Laid-open (KOKAI) Patent Application, KOKAI No. 245494/1996 furthermore contains a disclosure on a process for further oxidizing propylene, which was formed through dehydrogenation of propane, to produce acrylic acid. This process, however, necessitates removal of the hydrogen formed during the dehydrogenation of propane from the reaction gas. Japanese KOKAI Nos. 045643/1998, 118491/1998, 62041/1980 and 128247/1992, etc. disclose processes for forming unsaturated aldehydes and/or acids from lower alkanes, in particular, acrolein and/or acrylic acid from propane and methacrolein and/or methacrylic acid from isobutane. However, yield of these object products indicated in these publications are very low, and the processes need to be improved in various aspects including the catalyst to be used. US 4, 370, 259 relates to the oxidative dehydrogenation of hydrocarbons in the presence of a catalyst comprising a mixture of oxides of manganese, phosphorus and then alkali metal which is optionally supported on a refractory oxide. These catalysts are said to be particularly suitable for the oxidative dehydrogenation of paraffinic hydrocarbons. US 3,925,498 also relates to oxidative dehydrogenation of organic compounds and employs a metal ferrite, and in particular a magnesium ferrite, as a catalyst. The method described in this document involves passing the organic compound and oxygen through a fixed bed whilst adding incremental amounts of oxygen. This method is said to provide better control and to improve the yield of the reaction. EP-A-0 557 790 describes the oxidative dehydrogenation of isobutene to produce isobutylene. The catalyst used in this reaction comprises an oxide of phosphorus and an oxide of an additional metal. The use of such catalysts is said to allow the reaction to proceed with a high selectivity. Kinet. Catal., 1998, 29, 195-198 describes oxidative dehydrogenation of propane in the presence of various binary metal sulphates. From the sulphates of d-elements studied, manganese sulphate is said to be the least active. However, this compound is also said to be of interest due to its efficiency in the formation of propylene with significant conversions of propane. [The problem to be solved by the invention] An object of this invention is to provide novel oxidative dehydrogenation catalysts useful for vapor phase oxidative dehydrogenation of lower alkanes with molecular oxygen to produce corresponding lower olefins at high yield; and also to provide a process for producing from lower alkanes the corresponding olefins at high yield, by the use of said catalysts. Another object of the invention is to provide a process for producing from lower alkanes corresponding unsaturated aldehydes and/or unsaturated carboxylic acids at high yield. [Means for solving the problem] We have made concentrative studies in search of the catalysts suitable for oxidizing and dehydrogenating lower alkanes with molecular oxygen to produce the corresponding lower olefins, to discover that a catalyst containing manganese as the indispensable component, or a catalyst in which said catalytically active component is supported on a refractory inorganic carrier exhibit excellent oxidative dehydrogenation performance; and that lower olefins could be produced at high yield with the use of said catalyst. The present invention has been completed based on these discoveries. Thus, the present invention provides catalysts for oxidative dehydrogenation of lower alkanes, said catalysts being suitable for use in vapor phase oxidative dehydrogenation of C 2 -C 5 lower alkanes in the presence of molecular oxygen to produce corresponding olefins and characterized by having a composition expressed by a general formula (I) below: Mn α E 1 β E 2 γ Ox (in which Mn denotes manganese, and 0, oxygen; wherein E 1 is at least one of As, Sb, S, Se, Te, F, Cl, Br, I, Nb, Ta, W, Re and Cu; E 2 is at least one of Cr, Co, Ni, Ag, Au, Zn, TI, Sn, Pb, Bi, Li, Na, K, Rb, Cs, Mg, Ca, Sr, Ba, Y, La, Ce, Nd and Sm; α = 1, β = 0.05-0.4, γ = 0-1, and x is a numerical value determined by the oxidation states of Mn, E 1 and E 2 . The present invention furthermore provides a process for producing olefins which comprises vapor phase oxidative dehydrogenation of C 2 -C 5 alkanes in the presence of molecular oxygen to form corresponding olefins, characterized by the use of the above-described catalyst. The present invention, may be used in a process for producing, from lower alkane, unsaturated aldehyde and unsaturated acid at high yield in which an olefin obtained through vapor-phase oxidative dehydrogenation of C 2 -C 5 lower alkanes in the presence of molecular oxygen using the above-defined catalyst is further oxidized at vapor phase in the presence of oxygen to provide unsaturated aldehyde and unsaturated acid. The invention may further be used in a process for producing unsaturated acid from lower alkane at high yield, in which the unsaturated aldehyde obtained as above is further oxidized at vapor phase in the presence of molecular oxygen to provide unsaturated acid. [Embodiments of the invention] More specifically, C 2 -C 5 lower alkanes signify ethane, propane, n-butane, isobutane, n-pentane and isopentane. The catalysts of the present invention are used in oxidative dehydrogenation reactions of these lower alkanes to produce corresponding olefins, more specifically, ethylene from ethane, propylene from propane, n-butene from n-butane, isobutene from isobutane, n-pentene from n-pentane and isopentene from isopentane. These lower alkanes may be used either singly or as a mixture of more than one. The oxidative dehydrogenation catalysts of the present invention are useful for the production of, in particular, propylene and isobutene from propane and isobutane, respectively. For improving the selectivity for, and yield of, the product, the catalysts of the general formula (I) in which E 1 component is P, Sb, B, S, Nb, W or Re and E 2 component is Cr, Fe, Sn, Na, Mg or Ce are preferred. The method of preparation of the oxidative dehydrogenation catalysts of the present invention is not subject to any critical limitations, but any of conventionally practiced methods or known methods for preparation of this type of catalysts can be used. For example, the catalysts may be prepared by the procedures comprising adding to a slurry of manganese dioxide powder antimony trioxide powder and aqueous solutions of phosphoric acid, boric acid, ammonium sulfate, telluric acid, ammonium chloride, niobium oxalate, ammonium tungstate, rhenium oxide and copper nitrate, etc. as E 1 component; if necessary further adding aqueous solution of at least one element selected from the E 2 component: condensing the mixture under heating with agitation for a prescribed period, drying the resultant paste at 80-300°C; pulverizing and molding the same; if necessary further crushing the same for size adjustment or re-drying at 80-300°C; and if necessary further firing the dry product at 300-800°C. The firing atmosphere is subject to no limitation, and the firing may be conducted in air, an atmosphere of high or low oxygen concentration, a reducing atmosphere, in an inert gas such as nitrogen, helium, argon or the like, or in vacuum. In most desirable practice, the catalyst is not firing at the high temperatures but is contacted with the reaction gas containing the alkane or alkanes and oxygen as it has undergone the drying treatment or treatments at not higher than 300°C. In that occasion, the reaction may be started at a temperature not lower than the prescribed level by way of a pre-treating reaction, or directly at the prescribed temperature. In the latter case changes in catalytic activity may be observed at the initial stage of the reaction, but normally a stable activity level is reached within an hour. The starting materials for catalyst preparation are not critical, but may be any of nitrate, sulfate, oxide, hydroxide, chloride, carbonate, acetate, oxygen acid, ammonium salt of oxygen acid, etc. of the elements. As Mn source, besides powders of various oxides thereof or molded products which are useful as they are, manganese hydroxide slurries obtained upon treating an aqueous solution of, eg., manganese nitrate, with aqueous ammonia or the like are conveniently used. Any means used for catalyst preparation in general, for example, co-precipitation of a manganese compound with compounds of other additive elements from their aqueous solution, are applicable. As sulfur source, aqueous sulfuric acid or ammonium sulfate may be used, or the whole or a part thereof may be introduced in the form of sulfate(s) of other additive element(s). Similarly, halogen may be introduced as aqueous hydrogen halide or ammonium halide, or in the form of halide(s) of other additive element(s). Again the use form of refractory inorganic carrier is subject to no critical limitation, which allows versatile selection according to the form of use of the catalyst, such as, besides molded products, powder of oxide or hydroxide, gel or sol. The starting gas to be subjected to the vapor phase oxidative dehydrogenation reaction according to the present invention may if necessary contain a diluent gas, besides lower alkane(s) and molecular oxygen. As the molecular oxygen, air or pure oxygen is used, normally at a ratio of 0.1-5 mols per mol of alkane. As the diluent gas, an inert gas such as nitrogen, helium or carbon dioxide or steam is conveniently used. The reaction conditions for carrying out the vapor phase oxidative dehydrogenation of the present invention are subject to no critical limitation. For example, the starting gas as described above is contacted with an oxidative dehydrogenation catalyst of the present invention under such conditions as: at a space velocity of 300-30,000 hr -1 at a temperature between 250 and 650°C. While the reaction is normally conducted under atmospheric pressure, a reduced or elevated pressure may be used. The reaction system again is not critical, which may be a fixed bed system, moving bed system or fluidized bed system. It may also be one-pass system or recycling system. The olefines (alkenes) which are obtained through the vapor phase oxidative dehydrogenation of C 2 -C 5 lower alkanes (alkane oxidative dehydrogenation step) using the catalyst of the present invention can be further oxidized to produce unsaturated aldehydes and unsatuated acids (alkene oxidation step). The unsaturated aldehydes can further be oxidized to produce unsaturated acids (aldehyde oxidation step). Thus formed unsaturated aldehydes and/or unsaturated acids are trapped with an absorption column (absorbing step). As the oxygen source in the present invention, air and/or oxygen produced by such methods as cryogenic method, P.S.A. (pressure swing adsorption) method and the like can be used. According to the present invention, it is possible to form from lower alkanes the corresponding olefins, without side-production of hydrogen. If necessary oxygen and/or steam may be added to the gases to be introduced in each of the above steps, and such additional oxygen and/or steam are supplied by, for example, air, above-described oxygen, water and/or the gas discharged of said absorbing step. As one specific example of useful catalyst in the alkene oxidation step, those expressed by following general formula (2) may be named: Mo a Bi b Fe c A d B e C f D g O x in which Mo is molybdenum; Bi is bismuth; Fe is iron; A is at least one element selected from the group consisting of cobalt and nickel; B is at least one element selected from the group consisting of alkali metals and thallium; C is at least one element selected from the group consisting of silicon, aluminium, zirconium and titanium; D is at least one element selected from the group consisting of tungsten, phosphorus, tellurium, antimony, tin, cerium, lead, niobium, manganese, arsenic and zinc; and 0 is oxygen: and the ratio of those elements is, when a = 12, b=0.1-10, c=0.1-20, d=2-20, e=0.001-10, f=0-30, g=0-4 and x is a numerical value determined by the state of oxidation of those elements other than oxygen. Also as one specific example of useful catalyst in the aldehyde oxidation step, those expressed by following general formula (3) may be named: Mo h V i W j E k F l G m H n O x in which Mo is molybdenum; V is vanadium; W is tungsten; E is at least one element selected from the group consisting of copper, cobalt, bismuth and iron; F is at least one element selected from the group consisting of antimony and niobium; G is at least one element selected from the group consisting of silicon, aluminium, zirconium and titanium; H is at least one element selected from the group consisting of alkaline earth metals, thallium, phosphorus, tellurium, tin, cerium, lead, manganese and zinc; and 0 is oxygen: and the ratio of those elements is, when h=12, i=0.1-10, j=0-10, k=0.1-20, l=0-10, m=0-10, n=0-30, and x is a numerical value determined by the state of oxidation of those elements other than oxygen. [Effect of the invention] The lower alkane oxidative dehydrogenation catalysts according to the present invention excel in the oxidative dehydrogenation ability and enable the production from lower alkanes of corresponding olefins at high yield. Furthermore, due to their higher activity level than that of known catalyst system, the amount of the catalyst necessary for securing the same level of STY (space time yield) is far less than that of conventional catalysts, such as from 1/3 to 1/10. Also according to the present invention, unsaturated aldehyde and/or unsaturated acid can be produced from lower alkanes stably at high yield. [Examples] Hereinafter the invention is explained in further details referring to working examples, in which percentage are by weight, unless otherwise specified, and the conversion, one-pass yield and selectivity are indicated following the definitions below, inclusive of the side products: conversion (mol %) = (mol number of reacted alkane) (mol number of fed alkane) x 100 selectivity (mol %) = (mol number of each of formed compounds) (mol number of reacted alkane) x (carbon number of each of formed compounds) (carbon number of fed alkane) x 100 one-pass yield (mol %) = (mol number of each of formed compounds) (mol number of fed alkane) x (carbon number of each of formed compounds) (carbon number of fed alkane) x 100 = conversion x selectivity 100 Example 1 Into a 500-ml beaker, 4.35 g of manganese dioxide powder(MnO 2 , Kishida Chemical, purity 99.9%) and 200 ml of water were fed and heated under agitation. Further 1.09 g of antimony trioxide powder (Wako Pure Chemical Industry LTD., purity 99.9%) was added to the system which was then heated to about 80°C, and stirred for 2 hours while being maintained at a constant liquid volume. Then the temperature was raised to 90°C and stirring was continued for about 4 hours allowing concentration by evaporation of water content. The resulting paste was dried for 14 hours at 120°C, pulverized, molded and crushed to uniformize the size to 9-20 mesh. The resulting catalyst had a composition of Mn 1 Sb 0.15 Ox, 0.6 g of which was charged in an ordinary flow type reactor. The reaction was conduced under the following conditions; Reaction gas: C 3 H 8 /O 2 /N 2 = 1/1/8 (molar ratio) Feed rate: 112.5 ml/min. SV: equivalent to 12,000 hr -1 (In the subsequent Examples, indication of SV is omitted. As the catalyst weight was constant, SV underwent fluctuation more or less dependent on its packing density.) Reaction temperature: 450°C The results were as shown in Table 1. Example 2 The catalyst preparation was conducted in the same manner as in Example 1, except that the amount of the antimony trioxide powder was changed to 1.82 g. The resulting catalyst had a composition of Mn 1 Sb 0.25 Ox. Using 0.6 g of this catalyst, the reaction was conducted under identical conditions with those of Example 1. The results were as shown in Table 1. Example 3 (not according to the invention) The catalyst preparation was conducted in the same manner as in Example 1, except that the antimony trioxide powder was replaced with 0.58 g of 85% phosphoric acid (H 3 PO 4 , special grade reagent manufactured by Kanto Chemical) as dissolved in 50 ml of water. The resulting catalyst had a composition of Mn 1 P 0.1 Ox. Using 0.6 g of this catalyst, the reaction was conducted under identical conditions with those of Example 1, except that the reaction temperature was raised to 490 °C. The results were as shown in Table 1. Example 4 (not according to the invention) The catalyst preparation was conducted in the same manner as in Example 3, except that the amount of the 85% phosphoric acid was changed to 1.15 g. The resulting catalyst had a composition of Mn 1 P 0.2 Ox. Using 0.6 g of this catalyst, the reaction was run under identical conditions with those of Example 3. The results were as shown in Table 1. Example 5 (not according to the invention) The catalyst preparation was conducted in the same manner as in Example 1, except that the antimony trioxide powder was replaced with 0.31 g of boric acid (H 3 BO 3 , special grade reagent manufactured by Kanto Chemical) as dissolved in 50 ml of water. The resulting catalyst had a composition of Mn 1 B 0.1 Ox. Using 0.6 g of this catalyst, the reaction was run under identical conditions with those of Example 3. The results were as shown in Table 1. Example 6 The catalyst preparation was conducted in the same manner as in Example 1, except that the antimony trioxide powder was replaced with 0.66 g of ammonium sulfate (special grade reagent manufactured by Kanto Chemical) as dissolved in 50 ml of water. The resulting catalyst had a composition of Mn 1 S 0.1 Ox. Using 0.6 g of this catalyst, the reaction was run under identical conditions with those of Example 3. The results were as shown in Table 1. Example 7 The catalyst preparation was conducted in the same manner as in Example 1, except that the antimony trioxide powder was replaced with 1.62 g of niobium oxalate (a product of C.B.M.M. Co., containing 20.5% of Nb 2 O 5 upon conversion) as dissolved in 100 ml of water. The resulting catalyst had a composition of Mn 1 Nb 0.05 Ox. Using 0.6 g of this catalyst, the reaction was run under identical conditions with those of Example 3. The results were as shown in Table 1. Example 8 The catalyst preparation was conducted in the same manner as in Example 1, except that the antimony trioxide powder was replaced with 1.16 g of aqueous ammonium meta-tungstate solution, MW-2 (a product of Nippon Inorganic Colour and Chemical Co., LTD., containing 50% of WO 3 ) as diluted with 50 ml of water. The resulting catalyst had a composition of Mn 1 W 0.05 Ox. Using 0.6 g of this catalyst, the reaction was run under identical conditions with those of Example 3. The results were as shown in Table 1. Example 9 The catalyst preparation was conducted in the same manner as in Example 1, except that the antimony trioxide powder was replaced with 0.61 g of rhenium oxide (Re 2 O 7 , Kishida Chemical, purity 99.99%) as dissolved in 50 ml of water. The resulting catalyst had a composition of Mn 1 Re 0.05 Ox. Using 0.6 g of this catalyst, the reaction was run under identical conditions with those of Example 3. The results were as shown in Table 1. Example 10 The catalyst preparation was conducted in the same manner as in Example 1, except that the antimony trioxide powder was replaced with 1.21 g of copper nitrate (Wako Pure Chemical Industry LTD., purity 99.9%) as dissolved in 50 ml of water. The resulting catalyst had a composition of Mn 1 Cu 0.1 Ox. Using 0.6 g of this catalyst, the reaction was run under identical conditions with those of Example 3. The results were as shown in Table 1. Example 11 The catalyst preparation was conducted in the same manner as in Example 1, except that the antimony trioxide powder was replaced with 1.07 g of ammonium chloride (special grade reagent manufactured by Kanto Chemical) as dissolved in 50 ml of water. The resulting catalyst had a composition of Mn 1 Cl 0.4 Ox. Using 0.6 g of this catalyst, the reaction was run under identical conditions with those of Example 3. The results were as shown in Table 1. Example 12 The catalyst preparation was conducted in the same manner as in Example 1, except that 2.00 g of chromium nitrate [Cr(N0 3 ) 3. 9H 2 O, Wako Pure Chemical Industry LTD., purity 99.9%] as dissolved in 50 ml of water was added following the addition of the antimony trioxide powder. The resulting catalyst had a composition of Mn 1 Sb 0.15 Cr 0.1 Ox. Using 0.6 g of this catalyst, the reaction was run under identical conditions with those of Example 1. The results were as shown in Table 1. Example 13 (not according to the invention) The catalyst preparation was conducted in the same manner as in Example 1, except that 2.02 g of iron nitrate [Fe(NO 3 ) 3 .9H 2 O, Wako Pure Chemical Industry LTD., special grade reagent] as dissolved in 50 ml of water was added following the addition of the antimony trioxide powder. The resulting catalyst had a composition of Mn 1 Sb 0.15 Fe 0.1 Ox. Using 0.6 g of this catalyst, the reaction was run under identical conditions with those of Example 1. The results were as shown in Table 1. Example 14 The catalyst preparation was conducted in the same manner as in Example 1, except that 0.42 g of sodium nitrate (Wako Pure Chemical Industry LTD., special grade reagent) as dissolved in 50 ml of water was added following the addition of the antimony trioxide powder. The resulting catalyst had a composition of Mn 1 Sb 0.15 Na 0.1 Ox. Using 0.6 g of this catalyst, the reaction was run under identical conditions with those of Example 1. The results were as shown in Table 1. Example 15 The catalyst preparation was conducted in the same manner as in Example 1, except that 1.28 g of magnesium nitrate [Mg(NO 3 ) 2 .6H 2 O, Wako Pure Chemical Industry LTD., special grade reagent] as dissolved in 50 ml of water was added following the addition of the antimony trioxide powder. The resulting catalyst had a composition of Mn 1 Sb 0.15 Mg 0.1 Ox. Using 0.6 g of this catalyst, the reaction was run under identical conditions with those of Example 1. The results were as shown in Table 1. Example 16 The catalyst preparation was conducted in the same manner as in Example 1, except that 2.22 g of cerium nitrate [Ce(NO 3 ) 3 .6H 2 O, Wako Pure Chemical Industry LTD., special grade reagent, purity 98%] as dissolved in 50 ml of water was added following the addition of the antimony trioxide powder. The resulting catalyst had a composition of Mn 1 Sb 0.15 Ce 0.1 Ox. Using 0.6 g of this catalyst, the reaction was run under identical conditions with those of Example 1. The results were as shown in Table 1. Example 17 The catalyst preparation was conducted in the same manner as in Example 1, except that the antimony trioxide powder was replaced with 1.11 g of chromium sulfate [Cr 2 (SO 4 ) 3 .4H 2 O, Kanto Chemical, first grade reagent] as dissolved in 50 ml of water. The resulting catalyst had a composition of Mn 1 S 0.15 Cr 0.1 Ox. Using 0.6 g of this catalyst, the reaction was run under identical conditions with those of Example 3. The results were as shown in Table 1. Example 18 The catalyst preparation was conducted in the same manner as in Example 1, except that the antimony trioxide powder was replaced with 1.75 g of stannic chloride (SnCl 4 .5H 2 O, Wako Pure Chemical Industry LTD., special grade reagent) as dissolved in 50 ml of water. The resulting catalyst had a composition of Mn 1 Cl 0.4 Sn 0.1 Ox. Using 0.6 g of this catalyst, the reaction was run under identical conditions with those of Example 3. The results were as shown in Table 1. Example 19 The catalyst preparation was conducted in the same manner as in Example 1, except that 1.16 g of aqueous ammonium meta-tungstate solution MW-2 as diluted with 50 ml of water and 2.00 g of chromium nitrate as dissolved in 50 ml of water were added following the addition of the antimony trioxide powder. The resulting catalyst had a composition of Mn 1 Sb 0.15 W 0.05 Cr 0.1 Ox. Using 0.6 g of this catalyst, the reaction was run under identical conditions with those of Example 1. The results were as shown in Table 1. Example 20 Using 0.6 g of the catalyst which was used in Example 19, the reaction of Example 19 was repeated except that the reaction temperature was raised to 490 °C. The results were as shown in Table 1. Example 21 The catalyst preparation was conducted in the same manner as in Example 1, except that 1.16 g of aqueous ammonium meta-tungstate solution as diluted with 50 ml of water and 1.11 g of chromium sulfate as dissolved in 50 ml of water were added following the addition of the antimony trioxide powder. The resulting catalyst had a composition of Mn 1 Sb 0.15 W 0.05 S 0.15 Cr 0.1 Ox. Using 0.6 g of this catalyst, the reaction was run under identical conditions with those of Example 3. The results were as shown in Table 1. Example 22 Using 0.6 g of this catalyst which was used in Example 21, the reaction of Example 21 was repeated except that the reaction temperature was raised to 530 °C. The results were as shown in Table 1. Example 23 The catalyst preparation was repeated except that 1.16 g of aqueous ammonium meta-tungstate solution MW-2 as diluted with 50 ml of water, 1.62 g of niobium oxalate as dissolved in 100 ml of water and 2.00 g of chromium nitrate as dissolved in 50 ml of water were added following the addition of the antimony trioxide powder. The resulting catalyst had a composition of Mn 1 Sb 0.15 W 0.05 Nb 0.05 Cr 0.1 Ox. Using 0.6 g of this catalyst, the reaction was run under identical conditions with those of Example 3. The results were as shown in Table 1. Example 24 Using 0.6 g of the same catalyst as used in Example 23, the reaction of Example 23 was repeated except that the reaction temperature was raised to 530 °C. The results were as shown in Table 1. Comparative Example 1 The same manganese dioxide powder as the one used in Example 1 was pulverized, molded and crushed to a uniform size of 9-20 mesh. Using 0.6 g of this catalyst, the reaction was run under identical conditions with those of Example 1. The results were as shown in Table 1. Comparative Example 2 The reaction of Example 1 was repeated except that 0.6 g the catalyst same to that used in Comparative Example 1 was used and the reaction temperature was raised in 490°C. The results were as shown in Table 1. Example 25 Using isobutane instead of propane, isobutene was synthesized, assisted by the same catalyst as the one used in Example 19. An ordinary flow type reactor was charged with 0.6 g of the catalyst of 9-20 mesh in size, and through which a reaction gas composed of i-C 4 H 10 /O 2 /N 2 = 1/1/8 (molar ratio) was passed at a rate of 112.5 ml/min. The reaction temperature was 450°C. The results were: isobutane conversion 26.5%, isobutene selectivity 27.5%, methacrolein selectivity 0.9% and one-pass yield of isobutene 7.3%. Reaction Temp. (°C) Propane Conversion (%) Selectivity (%) One-Pass Yield (%) Propylene Propylene Acrolein Example 1 450 27.3 27.1 0.3 7.4 Example 2 450 26.9 26.7 0.7 7.2 Example 3 490 31.2 33.4 0.3 10.4 Example 4 490 30.9 33.7 0.3 10.4 Example 5 490 9.7 47.3 1.4 4.6 Example 6 490 17.9 36.3 0.4 6.5 Example 7 490 30.3 29.6 0.2 9.0 Example 8 490 29.7 29.4 0.2 8.7 Example 9 490 8.4 53.8 0.2 4.5 Example 10 490 25.3 22.2 0.1 5.6 Example 11 490 27.1 16.1 0.1 4.4 Example 12 450 30.0 28.0 0.5 8.4 Example 13 450 28.1 27.8 0.6 7.8 Example 14 450 26.5 28.7 0.3 7.6 Example 15 450 27.4 28.1 0.3 7.7 Example 16 450 29.2 26.7 0.4 7.8 Example 17 490 28.8 23.8 0.1 6.9 Example 18 490 25.5 19.8 0.1 5.0 Example 19 450 29.8 35.2 0.1 10.5 Example 20 490 32.8 37.9 0.3 12.4 Example 21 490 31.6 42.9 2.0 13.6 Example 22 530 36.5 42.6 1.8 15.5 Example 23 490 33.6 39.9 0.7 13.5 Example 24 530 35.5 41.7 0.8 14.8 Comparative Example 1 450 18.0 10.5 0 1.9 Comparative Example 2 490 23.7 13.4 0 3.2 Example 26 Each independently temperature-controllable single-pipe flow type reactors (A), (B) and (C) were connected in such a manner that gas would flow by the order of (A) to (B) to (C), with the piping so designed that the gas formed in the reactor (C) is introduced into an absorption column to allow absorption of condensed component and introduction of the uncondensed gas flowing out of the absorption column into the reactor A through its gas inlet portion, and the reaction was conducted with the following particulars. The piping also was so connected that fresh air could be introduced into the reactor (B) through its gas inlet portion. (Preparation of catalyst) 9 g of the catalyst as used in Example 21 was packed in the reactor (A), while the reactor (B) was packed with 32 g of a catalyst of the following composition (excepting oxygen) as described in Example 1 of Japanese Patent Publication No. 42241/1972: Mo 10 Co 4 Bi 1 Fe 1 W 2 Si 1.35 K 0.05 . The reactor (C) was packed with 52 g of a catalyst of the following composition (excepting oxygen) as described in Example 1 of Japanese KOKAI No. 206504/1996: Mo 12 V 6.1 W 1 Cu 2.3 Sb 1.2 . The flow rates of propane, air and recovered gas from absorption column were so controlled at the gas inlet portion of the reactor (A) as to give the reaction gas composition of 15 vol% C 3 H 8 , 15 vol% O 2 and 70 vol% of inert gases comprising nitrogen, carbon oxide, etc. In that occasion, the space velocity to the oxidative dehydrogenation catalyst was 3000 hr -1 . The product gas from the reactor (A) was fed into the reactor (B) while adding air thereto at such a rate that O 2 /C 3 H 6 ratio therein should become 2.5 at the entrance portion of the reactor (B), and the product gas from the reactor (B) was fed into the reactor (C). The reaction temperatures in the reactors (A), (B) and (C) during the run were 480°C, 325°C and 250°C, respectively. Analysis of the product gas from the reactor (C) indicated: C 3 H 8 conversion, 45.5 mol% and acrylic acid yield, 20.7 mol%. Example 27 To the reactor assembly used in Example 26, piping was connected to allow introduction of fresh air and steam into the gas inlet portion of the reactor (C), and the reaction was carried out with the particulars as follows. The flow rates of propane and gaseous oxygen were so controlled at the gas inlet portion of the reactor (A) as to give the reaction gas composition of 30 vol% C 3 H 8 , 30 vol% O 2 and 40 vol% of inert gases comprising nitrogen, carbon oxide, etc. The space velocity to the oxidative dehydrogenation catalyst in that occasion was 4,000 hr -1 . The product gas from the reactor (A) was fed into the reactor (B) while adding air thereto at such a rate that the O 2 /C 3 H 6 ratio therein should become 1.5 at the gas inlet portion of the reactor (B). The product gas from the reactor (B) was fed into the reactor (C), while adding air and steam thereto at such rates that the O 2 /acrolein ratio and steam concentration therein should become 1.3 and 35 vol%, respectively, at the gas inlet portion of the reactor (C). Other conditions were identical with those of Example 26. Analysis of the product gas from the reactor (C) indicated: C 3 H 8 conversion, 44. 1 mol% and acrylic acid yield, 20.1 mol%.

Claims: Catalyst of formula (1): Mn α E 1 β E 2 γ O x wherein E 1 is at least one of As, Sb, S, Se, Te, F, Cl, Br, I, Nb, Ta, W, Re and Cu; E 2 is at least one of Cr, Co, Ni, Ag, Au, Zn, Tl, Sn, Pb, Bi, Li, Na, K, Rb, Cs, Mg, Ca, Sr, Ba, Y, La, Ce, Nd and Sm; α = 1, β = 0.05-0.4, γ = 0-1, and x is a numerical value determined by the oxidation states of Mn, E 1 and E 2 . A catalyst according to claim 1, wherein E 1 is S, Nb, W or Re and E 2 is Cr, Sn, Na, Mg or Ce. A catalyst according to either claim 1 or claim 2, wherein E 1 is sulfur. A catalyst according to claim 3, wherein E 1 is a sulfate ion (SO 4 2- ) which is added in the form of a sulfate. Use of a catalyst according to any one of the preceding claims in a process for the vapor phase oxidative dehydrogenation of a C 2 -C 5 alkane. A process for the production of a catalyst according to any one of claims 1 to 4, which process comprises drying the catalyst at a temperature of not higher than 300°C, and does not comprise firing the catalyst at a temperature exceeding 300°C. A process for the production of an olefin which process comprises oxidizing and dehydrogenating a C 2 -C 5 alkane, in the vapor phase, in the presence of molecular oxygen and of a catalyst according to any one of claims 1 to 4. A process according to claim 7 which further comprises oxidizing the olefm in the vapor phase, in the presence of molecular oxygen, to produce an unsaturated aldehyde. A process according to claim 8 which further comprises oxidising the unsaturated aldehyde in the vapor phase, in the presence of molecular oxygen, to produce an unsaturated acid.

Inventors: KISHIMOTO NOBUJI, MATSUNAMI ETSUSHIGE, KISHIMOTO, NOBUJI, MATSUNAMI, ETSUSHIGE
Applicants: NIPPON CATALYTIC CHEM IND, NIPPON SHOKUBAI CO., LTD
Application year: 1999
Main classification: B01J23
IPC codes: C07C45, C07C51, B01J23, C07C5