A METHOD FOR MECHANICAL WORKING IN THE PRESENCE OF A COBALT-CONTAINING METAL

Abstract: The present invention relates to a method for mechanically working of cobalt-containing metals or performing metalworking with a tool made of a metal containing cobalt. The method is carried out in presence of an aqueous cooing lubricant containing a combination of an alkanolamine, a mono- or diphosphate ester and a mono- or dicarboxylic acid. The combination is capable of reducing both the release of cobalt ions and the corrosion of iron. In addition it also contributes essentially to the lubrication.

Description: A METHOD FOR MECHANICAL WORKING IN THE PRESENCE OF A COBALT- CONTAINING METAL The mechanical working of cemented carbides is usually carried out in the presence of an aqueous cooling lubricant which frequently contains an iron corrosion inhibitor, such as salts of monoethanolamine, diethanolamine or triethanolamine, and a lubricant, such as salts of fatty acids with 14-18 carbon atoms When the large amounts of chips produced during the mechanical working and the piece of work itself are exposed to the aqueous cooling lubricant, corrosion processes take place which generate a high level of ionic cobalt in the aqueous cooling lubricant The corrosion processes have a negative effect on the appearance and the dimension tolerances of the work piece or a work tool containing cobalt, while the high content of ionic cobalt constitutes a serious health problem for humans who come in contact herewith US patent 4 315 889 discloses a method of reducing the release of cobalt by performing the metal working in the presence of a cooling lubricant containing, as an active component, a specific triazole or thiadiazole compound However, since these active compounds are consumed in the presence of ethanolamines, the aqueous cooling lubricant has to be regularly upgraded EP-A-0180561 describes the use of a tertiary alkanol amine compound for reducing the release of cobalt and simultaneously maintaining the corrosion on a low level According to the application the tertiary alkanol amine compound can advantageously be combined with carboxylic acids for further protection against the release of cobalt and the corrosion of iron According to the present invention it has now been found possible to further reduce the release of cobalt and corrosion of iron in comparison with the prior art, if the metal working is performed in the presence of an aqueous cooling lubricant havmg a pH between 6 and 10 and containing a) a phosphate ester of the formula Rι(oxyalkylene) n OP(O)(X)(OH) (I), or (HO) 2 (O)P-(oxyalkylene) m -OP(O)(OH) 2 (II), where Ri is an alkyl group with 1-12 carbon atoms, X is hydroxyl or the group RiO, where Ri has the above mention meaning, oxyalkylene is a group containing 2-4 carbon atoms, n is a number from 1-15 and m is a number from 4- 20, or a salt thereof, b) a carboxylic acid of the formula R 2 (COOH) P (III), where R 2 is an alkyl group with 4-10 carbon atoms and p is 1 or 2, or a salt thereof, and c) an alkanol amine of the formula N(R 3 )(R 4 )(R 5 ) (IV), where R 3 , R 4 and R 5 independently of each other designate a group (AO)„H, where AO is an ethyleneoxy group or a propyleneoxy group and n is a number from 2-6, the total number of ethyleneoxy groups to the total number of propyleneoxy groups being between 2 1 and 1 3, in an amount of a) being 5-85 % by weight, b) 5-85% by weight and c) 10-90% by weight, calculated on the total weight of a), b) and c) The combination of the phosphate ester, the carboxylic acid and the alkanol amine according to the present invention results in an essential reduction in the amount of released cobalt in comparison with a corrosion inhibitor consisting of a carboxylic acid and an alkanol amine The compounds I, II, III and IV also contribute to the lubrication The alkanol amine of formula IV always contains at least 2 propyleneoxy groups Preferably the alkanol amines are produced by ethoxylation of ammonia with 2-4 moles ethylene oxide followed by propoxylation with 4-7 moles per mole ammonia The hydroxyl groups of these alkanol amines will consist of only secondary hydroxyl groups the relationship between the number of ethyleneoxy groups and the number of propyleneoxy groups is from 1 1 to 1 3 The carboxylic acid of formula III contains an aliphatic group which can be saturated or unsaturated, straight or branched Preferably the aliphatic group of monocarboxylic acids contains 5-9 carbon atoms, while the dicarboxyhc acids preferably have an aliphatic group with 6-10 carbon atoms Suitable examples of carboxylic acids are azelaic acid, pelargonic acid, sebacic acid, isononanoic acid, neodecanoic acid, n- octanoic acid, n-decanoic acid and dodecandioic acid The carboxylic acids having a branched aliphatic group of the preferred size are often utilized, since they are low foaming. In the phosphate esters of formulae I and II, the (oxyalkylene) n group and (oxyalkylene) m group respectively, are suitable selected in such a way that the esters will be water-soluble or easily dispersible in water. The aliphatic group Ri can be saturated or unsaturated, straight or branched and contains preferably 2-8 carbon atoms Preferably the phosphate ester component with formula I consists of at least 50% by weight of monoesters In formula II the polyoxyalkylene chain preferably consists at least partially of oxyalkylene groups with 3-4 carbons atoms and m preferably is at least 6, since these diphosphates beside the corrosion inhibiting effect give a considerable contribution to the lubrication Especially suitable are those diphosphate esters, which contains a polyoxypropypene chain with 5-10 oxypropylene units The content of the components a), b) and c) may vary within wide limits, but is normally between 0 1 and 10% by weight, preferably between 1 and 7% by weight of the cooling lubricant ready for use The cooling lubricant can also contain a number of other additives, such as additional corrosion-inhibiting additives and lubricants, pH-regulating or controlling additives, bactericidal agents, viscosity-increasing additives, solubilizers, perfumes, colourants etc Examples of suitable additional corrosion inhibitors are amines compounds, such as triazole and thiadiazole compounds and inorganic compounds, such as alkali metal hydroxides and boric acid, and reaction products between boric acid and/or carboxylic acids with organic compounds, such as alkanol amines The content of these additional corrosion inhibitors may be up to 3% by weight of the cooling lubricant Although the cooling lubricant containing a), b) and c) has an adequate lubrication ability for many applications it may be occasions where improved lubrication is desired Examples of suitable lubricants to be incorporated into a cooling lubricant according to the invention are those selected from the group consisting of esters or amides of mono- or dicarboxylic acids having at least 12 carbon atoms in the acyl groups, mono- and dicarboxylic acids having more than 12 carbon atoms, organic aliphatic phosphate esters containing one or two aliphatic groups with 6-18 carbon atoms, nonionic alkylene oxide adducts with a molecular weight above 400, such as polypropylene glycols, glycols of randomly distributed propylenoxy and ethyleneoxy groups and block polymers of propylene oxide and ethylene oxide, and mixtures thereof The content of these additional lubricants may be up to 3% by weight of the cooling lubricant ready for use The solubilizers are usually low molecular compounds containing at least one hydroxyl The molecular weight is normally below 400 Examples of suitable solubilizers are propypeneglycol, ethylene diethyleneglycol, butyl diethyleneglycol and butyl triethyleneglycol. When preparing a cooling lubricant according to the invention, it is suitable to first prepare a concentrate, for example by adding the components a), b) and c) and, if so desired water, and then any supplementary ingredients The amount of water is suitably between 5-80% by weight of the concentrate A typical concentrate according to the invention has the following composition components a+b+c 20-95, preferably 50-90% by weight additional corrosion inhibitors 0-30, preferably 0-15% by weight additional lubricants 0-30, preferably 0-15% by weight water 5-80, preferably 10-50% by weight other ingredients 0-30, preferably 0-15% by weight The total amount of the additional corrosion inhibitors and lubricants and other ingredients is often 5-40% by weight of the concentrate Before the concentrate is used, it is diluted with water so that the cooling lubricant ready for use will have a total content of a), b) and c) of 0 5-20% by weight, preferably 2-10% by weight The present invention is further illustrated by the following Example Example Cooling lubricants ready for use were prepared from the aqueous concentrates in the Table 1 below The content of water was 30% by weight The pH of the concentrates was adjusted to 9 by adding KOH before they were diluted with water to an active content of 4% by weight The corrosion inhibiting effects on cobalt and iron of these fluids were determined at an ambient temperature of 22°C by the following test methods Fe-corrosion tests were done by placing 30 grams of cast iron chips evenly spread on a circular filter paper with a diameter of 90 mm 1 25 gram of one of the cooling lubricants was dispensed at the center of the filter paper, which was placed in a plastic Petri dish and covered by a lid. The corrosion taken place after 24 hours was determined by visually inspection of the rust staining according to a scale, where 0= no corrosion, 1= one stain, 2= two or three stains, 3= more than three stains up to to 10% of the paper surface discolored, 4- between 10 and 25% of the paper surface discolored, and 5= more than 25% of the paper surface discolored Co-corrosion tests were performed by assessing the amount of leached cobalt obtained, when a 20 ml glass vial containing 5 glass beads, 5 mg of fine powder of cobalt and 10 ml of one of the fluids was shaken for 7 days The amount of cobalt dissolved was measured by use of an atomic absorption spectrophotometer (AAS) Initial screening of the fluids was done by using analytical sticks from Merck and only samples, which were found to contain less than 30 ppm of cobalt were subjected to AAS analysis The results obtained from the corrosion tests are shown in Table 2 Table 1. Aqueous concentrates Components % by weight I II III IV V VI VII VIII Composition 1 20 - - - 50 2 20 - - - 50 3 20 - - - 50 4 20 - - - 50 5 - 20 - - 50 6 - 20 - - 50 7 - 20 - - 50 8 - 20 - - 50 9 - - 20 - 50 10 - - 20 - 50 11 - - 20 - 50 12 - - 20 - 50 13 - - - 20 50 14 - - - 20 50 15 - - - 20 50 16 - - - 20 50 17 10 - 10 - 50 18 10 - 10 - 50 19 10 - 10 - 50 20 10 - 10 - 50 21 10 - - 10 50 22 10 - - 10 50 23 10 _ _ 10 50 24 10 10 50 25 10 10 - 50 26 10 10 - 50 27 10 10 - 50 28 10 10 - 50 29 10 - 10 50 30 10 - 10 50 31 10 - 10 50 32 10 _ 10 50 Component 1= phosphate ester, where Ri = hexyl, oxyalkylene= oxyethylene, n=5, X=hydroxyL Component 11= diphosphate, where oxyalkylene=oxypropylene, m=9, Component 111= isononanoic acid, Component IV= neodecanoic acid, Component V= triethanolamine Component VI= triethanolamine+4 propylene oxide, Component VII= triethanolamine+5 propylene oxide, and Component VTII= triethanolamine+ 6 propylene oxide Table 2 Corrosion test results Composition 1 2 3 4 5 6 7 8 Fe-corrosion 0 0 1 3 0 0 2 3 Co-corrosion ppm 200 15 0 0 30 0 0 0 Composition 9 10 11 12 13 14 15 16 Fe-corrosion 0 0 1 0 0 1 1 2 Co-corrosion ppm 150 70 0 5 50 100 100 70 Composition 17 18 19 20 21 22 23 24 Fe-corrosion 0 0 1 0 0 0 0 1 Co-corrosion ppm 350 0 0 0 100 0 0 0 Composition 25 26 27 28 29 30 31 32 Fe-corrosion 0 0 0 1 0 0 0 0 Co-corrosion ppm 30 0 0 0 30 0 0 0 From the results it is evident that the metal working fluids formulated according to the invention, namely compositions 18, 19, 20, 22, 23, 24, 26, 27, 28, 30, 31 and 32, have excellent corrosion inhibiting properties as regards both cobalt and iron and are superior to the comparison fluids

Claims: CLAIMS 1 A method for mechanically working a cobalt-containing metal or performing metal working of metals with a tool made of a metal containing cobalt in the presence of an aqueous cooling lubricant having a pH between 6 and 10 and containing a) a phosphate ester of the formulae R 1 (oxyalkylene) n OP(O)(X)(OH) (I), or (HO) 2 (O)P-(oxyalkylene) ιn -OP(O)(OH) 2 (II), where Ri is an alkyl group with 1-12 carbon atoms, X is hydroxyl or the group RjO, where R t has the above mention meaning, oxyalkylene is a group containing 2-4 carbon atoms, n is a number from 1-15 and m is a number from 4- 20, or a salt thereof, b) a carboxylic acid of the formula R 2 (COOH) P (III), where R 2 is an alkyl group with 6-12 carbon atoms and p is 1 or 2, or a salt thereof, and c) an alkanol amine of the formula N(R 3 )(R 4 )(R 5 ) (IV), where R 3 , P and R5 independently of each other designate a group (AO)nH, where AO is an ethyleneoxy group or a propyleneoxy group and n is a number from 2-6, the number of ethyleneoxy groups in relation to the number of propyleneoxy groups is between 2 1 and 1 3, the amount of a) being 5-85% by weight, b) 5-85% by weight and c) 10-90% by weight, calculated on the total weight of a), b) and c) 2. A method according to claim 1, characterized in that the alkanol amine IV has three secondary hydroxyl groups. 3 A method according to claims 1 or 2, characterized in that the diphosphate ester II contains a polyoxyalkylene chain, which at least partially consists of oxyalkylene groups with 3-4 carbon atoms, and the phosphate ester I consists of at least 50% by weight of monoesters. 4 A method according to any one of claims 1-3, characterized in that the carboxyUc acid of formula III is a monocarboxyUc acid, where R 2 is a branched aUphatic group with 5-9 carbon atoms or a dicarboxylic acid, where R 2 is a branched aliphatic group with 6-10 carbon atoms. 5. A method according to any one of claims 1-4, characterized in that in the alkanol amine of formula IV the number of ethyleneoxy groups to the number of propyleneoxy groups is between 1 : 1 and 1:3. 6. A concentrate, characterized in that it has the foUowing composition: components a+b+c 20-95?^ by weight additional corrosion inhibitors 0-30% by weight additional lubricants 0-30% by weight water 5-80% by weight other ingredients 0-30 % by weight where components a), b) and c) have the meaning defined in claims 1-5 and the amount of a) is 5-85% by weight, b) 5-85% by weight and c) 10-90% by weight, calculated on the total amount of a), b) and c) 7. A concentrate according to claim 6, characterized in that it has the following composition components a+b+c 50-90% by weight additional corrosion inhibitors 0-15% by weight additional lubricants 0- 15% by weight water 10-50% by weight other ingredients 0-15% by weight 8. A concentrate according to any of the claims 6-7, characterized in that the amount of the additional corrosion inhibitors and lubricants and other ingredients is between 4 and 40% by weight of the concentrate 9. Use of a mixture containing a phosphate of the formula I or II, a carboxylic acid of formula III and an alkanol amine IV as these components are defined in claims 1-5 as a corrosion inhibitor for cobalt.

Inventors: SKOELD ROLF, SKOELD, ROLF
Applicants: SKOELD ROLF, SKOELD, ROLF
Application year: 1999
Main classification: C10M173
IPC codes: C10M173, C23F11