CORROSION INHIBITOR FOR CEMENT COMPOSITIONS

Abstract: An anti-corrosion agent for use with a cementitious composition which is to be reinforced, comprising one or more species selected from a group consisting of alkyldiamines represented by the general formula RHN-(CH2)n-NH2 (in which R is an alkyl having C8-22 atoms, and n is an integer of 1-5) and alkylamines represented by the general formula R-NH2 (in which R is an alkyl having C8-22 atoms). The agents give good anti-corrosion performance which does not decline with time and exposure to the elements to the same extent as is the case with conventional anti-corrosion agents.

Description: CORROSION INHIBITOR FOR CEMENT COMPOSITIONS The invention relates to an anti-corrosion agent for use with reinforced cementitious compositions. More precisely, the invention relates to an anti-corrosion agent for a cementitious composition, which agent suppresses the corrosion of steel materials such as reinforcing bars, steel frames and PC steel wires in a concrete structure. Currently, corrosion inhibition of reinforcing bars or steel frames is achieved by the addition to mortar or concrete of anti-corrosion agents such as nitrites (see JP, B, H2-28532) or alkanolamines (see JP, A, H7-173650), calcium nitrite being particularly effective. Because cementitious compositions such as mortar or concrete contain water, water-soluble anti-corrosion agents are often used. The problem with water-soluble materials is that, on exposure of a cement product, a concrete product or a reinforced concrete structure containing such agents to wind and rain, water gradually permeates the material and the added anti-corrosion agents are gradually leached out. As a result, the initial corrosion resistance performance decreases over time. Moreover, as nitrites can accelerate concrete setting, it is necessary to adjust for this by also using a retarding agent, especially in hot weather. Thus, the object of the invention is to provide an anti-corrosion agent for use with a reinforced cementitious composition which solves the abovementioned problems without having an adverse effect on the cement setting or strength, and whose anti- corrosion performance does not diminish prematurely with time. It has now been found that, although alkyldiamines and alkylamines are slightly soluble in water, they quite unexpectedly demonstrate excellent anti-corrosion properties in a cementitious composition. Accordingly, the invention provides an anti-corrosion agent for use with a cementitious composition which is to be reinforced, comprising one or more species selected from a group consisting of alkyldiamines represented by the general formula RHN- (CH 2 )n-NH 2 (in which R is an alkyl having C 8-22 atoms, and n is an integer of 1- 5) and alkylamines represented by the general formula R-NH 2 (in which R is an alkyl having C 8-22 atoms). The anti-corrosion agent for a cementitious composition of the invention not only gives excellent anti-corrosion performance, but also has low toxicity and does not have an adverse effect on cement setting or strength; therefore, it is easy to handle. Furthermore, as alkyldiamines and alkylamines are basically hydrophobic, they do not leach out even on the exposure to rainfall and do not lose their anti-corrosion effect over time to the same extent as do known anti-corrosion agents. By "ajJ yldiamines" and "alkylamines" is meant not only the compounds themselves but also their salts with inorganic or organic acids. The inorganic acid may be, for example, nitrous acid, nitric acid, sulfuric acid, boric acid, phosphoric acid, pyrophosphoric acid or phosphonic acid. The organic acid may be, for example, formic acid, acetic acid, benzoic acid, citric acid, adipic acid, lactic acid, gluconic acid, heptonic acid, ascorbic acid, sulfanilic acid or salicylic acid. It is possible to use both an alkyldiamine/alkylamine and a salt of one or both compounds in the same anti-corrosion agents. The anti-corrosion agents of the present invention may also contain known anti- corrosion agents such as nitrites, chromates, phosphate, benzotriazoles or alkanolamines. Suitable alkanolamines include N,N-dimethyl-ethanolamine, N-methyl- ethanolamine, monoethanloamine, diethanloamine, triethanloamine and the like. Cementitious compositions in which the agent of the present invention may be used include cement milk, grout, mortar, concrete or the like which contain at least cement. They are not necessarily mixed with water and can be a dry-mix for the preparation of cement milk, grout, mortar or concrete. Suitable cements include normal cement, high-early-strength cement, moderate heat cement, ultra-rapid-hardening cement, blast furnace slag cement, fly ash cement and the like. The anti-corrosion agent of the present invention may be used by adding to a cementitious mix such as cement milk, grout, mortar or concrete in a range of 0.05-5.0 wt.% on the basis of the cement weight in the cementitious composition. Additionally, the anti-rust agents for the cementitious compositions of the present invention may be used together with other known additives for mortar or concrete, including water-reducing agents, air-entraining agents, setting accelerators, retarders, expansive agents, plastic emulsions, and so on. The invention further provides a method of preventing corrosion of steel reinforcing elements in cementitious structures, comprising the addition to a cementitious mix which will form the structure of an anti-corrosion agent which consists of at least one species selected from a group consisting of alkyldiamines represented by the general formula RHN- (CH 2 )n-NH 2 (in which R is an alkyl having C 8-22 atoms, and n is an integer of 1-5) and alkylamines represented by the general formula R-NH 2 (in which R is an alkyl having C 8-22 atoms). The invention further provides a reinforced cementitious structure comprising a hard cementitious composition which has within it steel reinforcing members, the reinforcing members being protected from corrosion by the incorporation in the cementitious composition prior to hardening of an anti-corrosion agent which consists of at least one species selected from a group consisting of alkyldiamines represented by the general formula RHN- (CH 2 )n-NH 2 (in which R is an alkyl having C 8-22 atoms, and n is an integer of 1-5) and alkylamines represented by the general formula R-NH 2 (in which R is an alkyl having C 8-22 atoms). The invention is further described with reference to the following non-limiting examples. 1. Mortar test 1) Mix proportion ad preparation of mortar Mortar for testing is obtained by mixing sand/cement ratio of 2.0, water/cement ratio of 0.40 and superplasticiser, mainly consisting of formalin condensates of napthalenesulfonate, at a rate of 0.5 wt.% on cement. In all mortars except the comparative example 1, there is added sodium chloride at a rate of 1.5 wt.% on cement in order to accelerate the rusting of reinforcing bars. 2. Test method 1) Setting time: According to JIS A 6204 Annex 1. 2) Compressive strength: According to JIS R 5201. 3) Corrosion suppression test Table 1 4. Test results The test results are shown in Table 2. Comparative example 1 in Table 2 is the case in which there is no sodium chloride and no anti-corrosion agent, comparative example 2 is a case in which sodium chloride is added and the anti-corrosion agent is not added, comparative example 3 is a case in which sodium chloride and calcium nitrite are added, and examples 1-12 are cases in which sodium chloride and the anti-corrosion agents of the present invention are added, and the results of these cases are shown. 1) Setting time The setting time of comparative example 2 is faster than that of comparative example 1. The setting time of comparative example 3 is faster again than that of comparative example 2. The setting times of the examples 1-12 are almost the same as that of comparative example 2, showing that the anti-corrosion agents of the present invention have no effect on the setting. 2) Compressive strength The compressive strength at age 3 days in comparative examples 2 and 3 and the examples 1-12 is higher than that in comparative example 1 owing to the early-strength action of sodium chloride. The compressive strength at ages 3 days and 28 days in the examples 1-12 is of the same degree as that of comparative example 2, showing that the anti -corrosion agents for the cementitious compositions of the present invention have no effect on the compressive strength. Table 2 Note) The added amounts of sodium chloride and the anti-corrosion agents are % by weight on cement. 3) Corrosion suppression The test results are shown in Fig. 1. In comparison to the case in which sodium chloride is added and the anti-corrosion agent is not added (comparative example 2), the case in which sodium chloride and calcium nitrite are added (comparative example 3), shows the larger electrode potential value, and the corrosion is suppressed. Examples 2, 4, 6, 8, 10, 12 show larger electrode potential value than that of comparative example 2, demonstrating corrosion suppression. It can be seen that the anti-corrosion agents of the invention do not have the adverse effect on the manifestation of the cement setting or strength and demonstrate the excellent anti-corrosion effect on reinforcement bars even in an environment which contains a large quantity of sodium chloride. Brief Description of Drawing [Fig. 1] The graph showing the degree of corrosion by the electrode potential value against the current density.

Claims: Claims: 1. An anti-corrosion agent for use with a cementitious composition which is to be reinforced, comprising one or more species selected from a group consisting of alkyldiamines represented by the general formula RHN- (CH 2 )n-NH 2 (in which R is an alkyl having C 8 . 22 atoms, and n is an integer of 1-5) and alkylamines represented by the general formula R-NH 2 (in which R is an alkyl having C 8-22 atoms). 2. An anti-corrosion agent according to claim 1, wherein the alkyldiamines and alkylamines are in the form of their salts of organic or inorganic acids. 3. An anti-corrosion agent according to claim 2, wherein the acid is selected from the group consisting of nitrous acid, nitric acid, sulfuric acid, boric acid, phosphoric acid, pyrophosphoric acid, phosphonic acid, formic acid, acetic acid, benzoic acid, citric acid, adipic acid, lactic acid, gluconic acid, heptonic acid, ascorbic acid, sulfanilic acid and salicylic acid. 4. An anti-corrosion agent according to any one of claims 1-3, wherein the anti- corrosion agent is present in the proportion of 0.05-50% by weight solids on cement. 5. A method of preventing corrosion of steel reinforcing elements in cementitious structures, comprising the addition to a cementitious mix which will form the structure of an anti-corrosion agent which consists of at least one species selected from a group consisting of alkyldiamines represented by the general formula RHN- (CH 2 )n-NH 2 (in which R is an alkyl having C 8 . 22 atoms, and n is an integer of 1-5) and alkylamines represented by the general formula R-NH 2 (in which R is an alkyl having C 8 . 22 atoms). 6. A reinforced cementitious structure comprising a hard cementitious composition which has within it steel reinforcing members, the reinforcing members being protected from corrosion by the incorporation in the cementitious composition prior to hardening of an anti-corrosion agent which consists of at least one species selected from a group consisting of alkyldiamines represented by the general formula RHN- (CH 2 )n-NH 2 (in which R is an alkyl having C 8-22 atoms, and n is an integer of 1-5) and alkylamines represented by the general formula R-NH 2 (in which R is an alkyl having C 8 . 22 atoms).

Inventors: FURUSAWA TAKAO, HAGIWARA YUKI, HAMABE KENKICHI, OZAWA TAKEO, FURUSAWA, TAKAO, HAGIWARA, YUKI, HAMABE, KENKICHI, OZAWA, TAKEO
Applicants: FURUSAWA TAKAO, HAGIWARA YUKI, HAMABE KENKICHI, MBT HOLDING AG, OZAWA TAKEO, FURUSAWA, TAKAO, HAGIWARA, YUKI, HAMABE, KENKICHI, OZAWA, TAKEO
Application year: 1999
Main classification: C04B24
IPC codes: C04B24, C04B103