MULTILAYERED CATALYST AND METHOD FOR PREPARATION THEREOF

Abstract: The present invention includes a catalyst that has at least four layers, (1) porous support, (2) buffer layer, (3) interfacial layer, and optionally (4) catalyst layer. The buffer layer provides a transition of thermal expansion coefficient from the porous support to the interfacial layer thereby reducing thermal expansion stress as the catalyst is heated to high operating temperatures. The method of the present invention for making the at least three layer catalyst has the steps of (1) selecting a porous support, (2) solution depositing an interfacial layer thereon, and optionally (3) depositing a catalyst material onto the interfacial layer; wherein the improvement comprises (4) depositing a buffer layer between the porous support and the interfacial layer.

Description: MULTILAYERED CATALYST AND METHOD FOR PREPARATION THEREOF FIELD OF THE INVENTION The present invention relates to a catalyst useful for hydrocarbon conversion and specifically to a catalyst structure that exhibits longer life especially under high temperature conditions. BACKGROUND OF THE INVENTION Hydrogen and hydrocarbon conversion reactions including but not limited to steam reforming, water-gas shift reactions, methanol synthesis and catalytic combustion are well known. These reactions are usually carried out at temperatures between 200 and 1000 °C. Currently these reactions are industrially run using catalyst pellets which consist of an active catalytic metal or metal oxide deposited on high surface area ceramic pellets. Known foam or monolith catalysts are known to have three layers (1) porous support, (2) interfacial layer, and (3) catalyst metal as described in [1]. In making these catalysts, the interfacial layer has been deposited by various methods including solution impregnation techniques. The catalyst layer may be deposited by solution impregnation techniques. The interfacial layer has greater surface area than the porous support whereas the porous support has greater mechanical strength than the interfacial layer. The porous support may be a metal or ceramic foam. Metal foams are highly thermally conductive and easy to machine. The sponge-like mechanical properties allow convenient sealing in a reaction chamber via mechanical contact. The closely matched thermal expansion between the metal foam and the housing reaction chamber minimizes cracking of the porous support and minimizes gas channeling around the porous support at higher reaction temperatures. Pestryakov et al prepared metal foam supported transition metal oxide catalysts with [1] and without [2] an intermediate gamma-alumina layer for the oxidation of n-butane. Kosak [3] examined several approaches to disperse precious metals on various metal foams where the surface was pre-etched with HCI solution, and reported that electroless deposition provides the best adhesion of precious metals to the foam supports. Podyacheva et al. [4] also synthesized foam metal supported LaCoθ 3 perovskite catalyst with a porous alumina intermediate for methane oxidation. Despite all of the potential advantages with metal foam supported catalysts, metal foam has low corrosion resistance and its nonporous and smooth web surfaces have provided poor adhesion to ceramic materials. In order to increase corrosion resistance, methods such as diffusion alloying with Al, Cr, and Si have been used to fabricate ferritic steels, which are typically used for the manufacturing of high temperature furnace elements (about 1200°C) [5]. When the aluminum containing ferritic steels are appropriately heat- treated, aluminum migrates to the alloy surface and forms a strongly adhering oxide film which is resistant to oxygen diffusion. Such ferritic steel foils have been used to fabricate metal monoliths with >10 ppi (pores per inch) open cells [6]. However, the search for the similar alloy foams with pores suitable for catalytic applications (<20ppi, 80ppi preferred) has been fruitless. This has been attributed to both the immature methods for making the finer Al-ferritic steel foams and the lack of the alloy precursors for making the foams. Hence, there is a need in the art of supported catalysts for a porous support of a foam that is resistant to corrosion or oxidation and resists cracking of the interfacial layer. References 1. A.N.Pestryakov, A.A.Fyodorov, V.A.Shurov, M.S.Gaisinovich, and I.V.Fyodorova, React.Kinet.Catal.Lett, 53 [2] 347-352 (1994). 2. A.N.Pestryakov, A.A.Fyodorov, M.S.Gaisinovich, V.P.Shurov, I.V.Fyodorova, and T.A.Gubaykulina, React.Kinet.Catal.Lett., 54 [1] 167-172 (1995). 3. J.R.Kosak. A Novel Fixed Bed Catalyst for the Direct Combination of H 2 and O 2 to H 2 O 2 , M.G.Scaros and M.L.Prunier, Eds., Catalysis of Organic Reactions, Marcel Dekker, Inc. (1995), p115-124. 4. O.Y.Podyacheva, A.A.Ketov, Z.R.Ismagilov, V.A.Ushakov, A.Bos and H.J.Veringa, React.Kinet.Catal.Lett., 60 [2] 243-250 (1997). 5. A.N.Leonov, O.L.Smorygo, and V.K.Sheleg, React.Kinet.Catal.Lett., 60 [2] 259-267 (1997). 6. M.V.Twigg and D.E.Webster. Metal and Coated-Metal Catalysts, A Cybulski and J.A.Moulijn, Eds., Structured Catalysts and Reactors, Marcel Dekker, Inc. (1998), p59-90 . SUMMARY OF THE INVENTION The present invention includes a catalyst that has at least three layers, (1) porous support, (2) buffer layer, (3) interfacial layer, and optionally (4) catalyst material. The buffer layer provides a transition of thermal expansion coefficient from the porous support to the interfacial layer thereby reducing thermal expansion stress as the catalyst is heated to high operating temperatures. The buffer layer also reduces corrosion and oxidation of the porous support. The method of the present invention for making the multi-layer catalyst (at least four layers) has the steps of (1) selecting a porous support, (2) solution depositing an interfacial layer thereon, and optionally (3) depositing a catalyst material onto the interfacial layer; wherein the improvement comprises (4) depositing a buffer layer between the porous support and the interfacial layer. The subject matter of the present invention is particularly pointed out and distinctly claimed in the concluding portion of this specification. However, both the organization and method of operation, together with further advantages and objects thereof, may best be understood by reference to the following description taken in connection with accompanying drawings wherein like reference characters refer to like elements. BRIEF DESCRIPTION OF THE DRAWINGS FIG. 1 is an enlarged cross section of a catalyst. FIG. 2 is a graph of weight gain (via oxidation) versus time. DESCRIPTION OF THE PREFERRED EMBODIMENT(S) The catalyst of the present invention is depicted in FIG. 1 having a porous support 100, a buffer layer 102, an interfacial layer 104, and, optionally, a catalyst layer 106. Any layer may be continuous or discontinuous as in the form of spots or dots, or in the form of a layer with gaps or holes. The porous support 100 may be a porous ceramic or a metal foam. The interfacial layer 104 is a solution deposited metal oxide. The solution deposited metal oxide includes but is not limited to γ-AI 2 0 3 , SiO 2 , ZrO 2 , TiO 2 , magnesium oxide, vanadium oxide, chromium oxide, manganese oxide, iron oxide, nickel oxide, cobalt oxide, copper oxide, zinc oxide, molybdenum oxide, tin oxide, calcium oxide, aluminum oxide, lanthanum series oxide(s), zeolite(s) and combinations thereof. Typically the porous support 100 has a thermal coefficient of expansion different from that of the interfacial layer 104. Accordingly, for high temperature catalysis (T > 150 °C) a buffer layer 102 is needed to transition between the two coefficients of thermal expansion. Another advantage of the buffer layer 102 is avoiding side reactions such as coking or cracking caused by a bare metal foam surface. For chemical reactions which do not require large surface area supports such as catalytic combustion, the buffer layer 102 stabilizes the catalyst metal due to strong metal to metal-oxide interaction, in chemical reactions which require large surface area supports, the buffer layer 102 provides stronger bonding to the high surface area interfacial layer 104. The interfacial layer 104 may serve as a catalyst without any further catalyst layer deposited thereon. The buffer layer 102 is a metal oxide that is AI 2 O 3 , TiO 2 , SiO 2 , and ZrO 2 and combinations thereof. More specifically, the AI 2 O 3 is α-AI 2 03, γ-AI 2 O 3 and combinations thereof. The structure of the α-AI 2 0 3 is preferred because TiO 2 is not as good as alumina against oxygen diffusion. Therefore, it is expected that resistance against high temperature oxidation can be improved with alumina coated on the porous support 100. When the porous support 100 is metal foam, for example a stainless steel foam, a preferred embodiment has a buffer layer 102 formed of two sub-layers (not shown). The first sublayer (in contact with the porous support 100) is TiO 2 for good adhesion and bonding of the ceramic layers to the porous support 100. The second sublayer is α-AI 2 03 which is used for passivating the metal foam and is placed upon the TiO 2 . Deposition of the buffer layer 102 may be by vapor deposition including but not limited to chemical vapor deposition, physical vapor deposition or combinations thereof. Because the vapor deposition is conducted at high temperatures, polycrystalline phases are formed providing good adhesion of the metal oxide to the metal foam surface. Alternatively, the buffer layer 102 may be obtained by solution coating. For example, the solution coating has the steps of metal surface functionalization via hydroxide formation, followed by surface hydrolysis of alkoxides to obtain the polycrystalline phases. This solution coating may be preferred as a lower cost method of depositing the buffer layer 102. Polycrystalline metal oxides resist flaking of layers after several thermal cycles. Because metal foam has web surfaces that are nonporous and smooth, deposition of the interfacial layer may be impeded. One way to mitigate this problem is to rough the metal foam surface via chemical etching. The adhesion of high surface area gamma-alumina supported metal catalysts to metal foam is significantly improved when metal foam is roughed via chemical etching using mineral acid solutions, for example HCI. Roughed web surface also shows improved resistance to the spalling of catalyst layer under thermal cyclings. The open cells of a metal foam may range from about 20 ppi to about 1000 ppi and is preferably about 80 ppi. The catalyst layer 106 (when used) is deposited onto the interfacial layer 104. The catalyst layer may be any catalyst metal including but not limited to noble metal, transition metal and combinations thereof, or a catalyst metal oxide or transition metal oxide including but not limited to magnesium oxide, titanium oxide, vanadium oxide, chromium oxide, manganese oxide, iron oxide, nickel oxide, cobalt oxide, copper oxide, zinc oxide, zirconium oxide, molybdenum oxide, tin oxide, calcium oxide, aluminum oxide, silicon oxide, lanthanum series oxide(s), zeolite(s) and combinations thereof. The method of making the catalyst has the steps of selecting a porous support 100, and solution depositing an interfacial layer 104 thereon; wherein the improvement is obtained by depositing a buffer layer 102 between the porous support 100 and the interfacial layer 104. In a preferred embodiment, wherein a metal foam is used as the porous support 100, the metal foam is etched prior to vapor depositing the buffer layer 102. Etching is preferably with an acid, for example HCI. Optionally a catalyst layer 106 may be deposited onto the interfacial layer 104. Example 1 An experiment was conducted to demonstrate the catalyst layer of the present invention. A stainless steel foam was coated with 1000 Angstroms TiO 2 via chemical vapor deposition. SEM (scanning electron microscope) analysis showed that the stainless steel foam supported gamma-alumina with a TiO 2 buffer layer did not show spalling after several (3) thermal cycles from room temperature to 600 °C. In a control experiment with a stainless steel foam support coated with gamma- alumina without the TiO 2 buffer layer, severe flaking or spalling of the gamma alumina under the identical testing conditions was observed. Resistance to high temperature oxidation is shown in FIG. 2 CLOSURE While a preferred embodiment of the present invention has been shown and described, it will be apparent to those skilled in the art that many changes and modifications may be made without departing from the invention in its broader aspects. The appended claims are therefore intended to cover all such changes and modifications as fall within the true spirit and scope of the invention.

Claims: CLAIMS We claim: 1. A catalyst comprising a porous support having an interfacial layer thereon; wherein the improvement comprises a buffer layer between the porous support and the interfacial layer. 2. The catalyst as recited in claim 1 , further comprising a catalyst layer upon the interfacial layer. 3. The catalyst as recited in claim 1 , wherein said porous support is a metal foam. 4. The catalyst as recited in claim 1 , wherein said porous support is a porous ceramic. 5. The catalyst as recited in claim 1 , wherein said interfacial layer is a solution deposited metal oxide. 6. The catalyst as recited in claim 5, wherein said solution deposited metal oxide is selected from the group consisting of γ-AI 2 03, SiO 2 , ZrO 2 , TiO 2 , magnesium oxide, vanadium oxide, chromium oxide, manganese oxide, iron oxide, nickel oxide, cobalt oxide, copper oxide, zinc oxide, molybdenum oxide, tin oxide, calcium oxide, aluminum oxide, lanthanum series oxide(s), zeolite(s) and combinations thereof. 7. The catalyst as recited in claim 2, wherein said catalyst layer is a metal selected from the group of noble metal, transition metal and combinations thereof. - i ■ 8. The catalyst as recited in claim 2, wherein said catalyst layer is a metal oxide or transition metal oxide selected from the group consisting of magnesium oxide, titanium oxide, vanadium oxide, chromium oxide, manganese oxide, iron oxide, nickel oxide, cobalt oxide, copper oxide, zinc oxide, zirconium oxide, molybdenum oxide, tin oxide, calcium oxide, aluminum oxide, silicon oxide, lanthanum series oxide(s), zeolite(s) and combinations thereof. 9. The catalyst as recited in claim 1 , wherein said buffer layer is a metal oxide. 10. The catalyst as recited in claim 9, wherein said metal oxide is selected from the group of AI 2 O3, TiO 2 , SiO 2 , ZrO 2 and combinations thereof. 11. The catalyst as recited in claim 9, wherein said AI 2 O 3 is selected from the group consisting of α-AI 2 O 3 , γ-AI 2 O 3 and combinations thereof. 12. The catalyst as recited in claim 1 wherein said buffer layer comprises a plurality of sublayers. 13. A method of making a catalyst comprising the steps of selecting a porous support, solution depositing a interfacial layer thereon, wherein the improvement comprises depositing a buffer layer between the porous support and the interfacial layer. 14. The method as recited in claim 13, further comprising depositing a catalyst layer onto the interfacial layer. 15. The method as recited in claim 13, wherein said buffer layer is a metal oxide. 16. The method as recited in claim 15, wherein said metal oxide is selected from the group consisting of AI 2 O 3 , TiO 2 , SiO 2 , ZrO 2 and combinations thereof. 17. The method as recited in claim 15, wherein said AI 2 O 3 is selected from the group consisting of α-AI 2 03, γ-AI 2 O 3 and combinations thereof. 18. The method as recited in claim 13, wherein depositing the buffer layer is by vapor deposition. 19. The method as recited in claim 13, wherein depositing the buffer layer is by solution deposition.

Inventors: GAO YUFEI, TONKOVICH ANNA LEE Y, WANG YONG, GAO, YUFEI, TONKOVICH, ANNA, LEE, Y., WANG, YONG
Applicants: BATTELLE MEMORIAL INSTITUTE
Application year: 1999
Main classification: B01J37
IPC codes: B01J21, B01J33, B01J37, C07B61, C23C28