Preferred process for silicon hydride addition and preferred degree of polymerization for silicon hydride for thermoplastic vulcanizates

Abstract: An improved process for the preparation of thermoplastic elastomers by hydrosilylation crosslinking, in which a hydrosilylation crosslinking agent with a low degree of polymerization and/or a hydrosilylation crosslinking agent diluted in oil is used.

Description: FIELD OF THE INVENTION This invention relates to thermoplastic elastomer compositions prepared using hydrosilylation crosslinking of the elastomer component of the composition. A thermoplastic elastomer is generally defined as a polymer or blend of polymers that can be processed and recycled in the same way as a conventional thermoplastic material, yet has properties and functional performance similar to that of vulcanized rubber at service temperatures High performance thermoplastic elastomers in which a highly vulcanized rubbery polymer is intimately dispersed in a thermoplastic matrix are generally known as thermoplastic vulcanizates. BACKGROUND OF THE INVENTION Polymer blends, which have a combination of both thermoplastic and elastic properties, are generally obtained by combining a thermoplastic resin with an elastomeric composition in a way such that the elastomer component is intimately and uniformly dispersed as a discrete particulate phase within a continuous phase of the thermoplastic. Early work with vulcanized rubber components is found in U.S.-A-3,037,954 which discloses both static vulcanization of the rubber, as well as the technique of dynamic vulcanization wherein a vulcanizable elastomer is dispersed into a molten resinous thermoplastic polymer and the elastomer is cured while continuously mixing and shearing the blend. The resulting composition is a micro-gel dispersion of cured elastomer in an uncured matrix of thermoplastic polymer. In U.S.-A-32,028 polymer blends comprising an olefin thermoplastic resin and an olefin copolymer are described, wherein the rubber is dynamically vulcanized to a state of partial cure. The resulting compositions are reprocessible. U.S.-A- 4,130,534 and 4,130,535 further disclose thermoplastic vulcanizates comprising butyl rubber and polyolefin resin, and olefin rubber and polyolefin resin, respectively. The compositions are prepared by dynamic vulcanization and the rubber component is cured to the extent that it is essentially insoluble in conventional solvents. A range of crosslinking, or curing, agents for the vulcanization of the rubber are described in the early art, including peroxides, sulfurs, phenolic resins, radiation, and the like. U.S.-A-4,803,244 generally discusses the use of multifunctional organosilicon compounds in conjunction with a catalyst as an agent for crosslinking the rubber component of a thermoplastic elastomer by hydrosilylation. Hydrosilylation involves the addition of a silicon hydride across a multiple bond, often with a transition metal catalyst. This patent describes a rhodium catalyzed hydrosilylation of EPDM rubber in a blend with polypropylene to produce thermoplastic elastomers having a gel content of up to 34% (after correction for the plastic phase). This degree of vulcanization was achieved only with a high level of catalyst. A further modification of hydrosilylation crosslinking of the rubber in a thermoplastic elastomer composition is disclosed in EP-A-0776,937 and EP-A-651,009. A compatibilizing agent, containing in the same molecule a component having an affinity for the rubber and a component having an affinity for the thermoplastic resin, is incorporated into the composition and is said to improve adhesion between the rubber and resin in order to prevent agglomeration. SUMMARY OF THE INVENTION The present invention is based on the discovery that the process for hydrosilylation crosslinking of the rubber in a thermoplastic vulcanizate (TPV) can be improved by either employing a hydrosilylation crosslinking agent of low degree of polymerization (i.e. up to 30) or diluting the hydrosilylation crosslinking agent in oil before adding it to the TPV or combinations thereof. This combination provides rapid crosslinking of the elastomer to a fully vulcanized state, yet requires an unexpectedly low concentration of the hydrosilylation crosslinking agent and catalyst in order to achieve the cure. In the instant invention no compatibilizer is required in order to produce compositions with excellent mechanical properties. In a first embodiment the present invention relates to a process for forming a thermoplastic vulcanizate comprising a) blending a thermoplastic resin and a rubber in the molten state, b) mixing with said blend a 25 to 55 weight percent blend of hydrosilylation crosslinking agent in an oil, said hydrosilylation crosslinking agent having a degree of polymerization from 2 to 10, c) adding a hydrosilylation catalyst to the mixture from step (b), and d) crosslinking said rubber. In a further embodiment the present invention relates to a vulcanizate formed by the process according to the invention. Additives, which react with residual silicon hydride functionality in the thermoplastic elastomer, are incorporated into the process. This results in a composition which has further improved long term heat aging characteristics. The compositions produced by the improved process have utility as replacements for thermoset rubber compounds in a variety of applications, particularly where molding or extrusion is involved and the combination of thermoplastic and elastomeric properties provides an advantage. Typical uses include molded articles for automobile underhood parts, engineering and construction materials, mechanical rubber goods, industrial parts such as hose, tubing and gaskets, electrical applications and household goods. BRIEF DESCRIPTION OF DRAWINGS Figure 1 is a plot of the oil swell value of a TPV versus the degree of polymerization of the silicone hydride. DESCRIPTION OF THE PREFERRED EMBODIMENTS Thermoplastic elastomer compositions may generally be prepared by blending a thermoplastic resin and a rubber, then melting the thermoplastic component and mixing the melt until the blend is homogeneous. If a composition of vulcanized rubber in a thermoplastic matrix is desired, crosslinking agents (also referred to as curatives or vulcanizing agents) are added to the blend and crosslinking occurs during the mixing. This latter process is described as dynamic vulcanization. A wide range of thermoplastic resins and rubbers and/or their mixtures have been used in the preparation of thermoplastic elastomers, including polypropylene, HDPE, LDPE, VLDPE, LLDPE, cyclic olefin homopolymers or copolymers as well as olefinic block copolymers, polystyrene, polyphenylene sulfide, polyphenylene oxide and ethylene propylene copolymer (EP) as the thermoplastics, with ethylene propylene diene rubber (EPDM), acrylonitrile butadiene rubber (NBR), various isobutylene copolymers and/or natural rubber (NR) as the elastomer. When the elastomer component is crosslinked, agents such as sulfur, peroxide, phenolics and ionic compounds are often used. Hydrosilylation Agents Hydrosilylation has also been disclosed as a crosslinking method. In this method a silicon hydride having at least two SiH groups in the molecule is reacted with the carbon-carbon multiple bonds of an unsaturated (i.e. containing at least two carbon-carbon double bonds) rubber component of the thermoplastic elastomer, in the presence of the thermoplastic resin and a hydrosilylation catalyst. Siiicon hydride compounds useful in the process of the invention include methylhydrogen polysiloxanes, methylhydrogen dimethyl-siloxane copolymers, alkyl methyl polysiloxanes, bis(dimethylsilyl)alkanes and bis(dimethylsilyl)benzene. Preferred silicon hydride compounds may be described by the formula where each R is independently selected from the group consisting of alkyls comprising 1 to 20 carbon atoms, cycloalkyls comprising 4 to 12 carbon atoms and aryls. In formula (1) it is preferred that each R be independently selected from a group consisting of alkyls comprising 1 to 12 carbon atoms. Even more preferred is R = methyl; R' represents a hydrogen atom, an alkyl or alkoxy group having from 1 to 24 carbon atoms; and R" represents R or a hydrogen atom. D represents the group D' represents the group T represents the group m is an integer having a value ranging from 1 to 50, n is an integer having a value ranging from 1 to 50, and p is an integer having a value ranging from 0 to 6. For the purpose of this application the sum of m, n and p will be defined as the degree of polymerization. Preferred degrees of polymerization are up to 30, more preferably from 2 to 20 or 30and most preferably from 2 or 3 to 10 or 15 wherein each molecule on average contains at least 2 Si-H bonds. Particularly preferred polyorganosiloxanes are those in which the silicon atom of the silicon hydride functionality is bound by heteroatoms/atoms having lone pairs of electrons. The preferred polyorganosiloxanes may also be substituted with appropriate functionality permitting solubility in the reaction media. A type of this functionalization is described in U.S.-A-4,046,930 which teaches alkylation of polyorganosiloxanes. Weight percent of alkylation should not exceed a level that may retard or prevent the crosslinking reaction rates due to steric constraints. It has been discovered that higher gel content in the rubber phase and better physical properties, such as low compression and tension set and low oil swell, can be achieved by diluting the hydrosilylation crosslinking agent in an inert mobile component such as oil prior to addition of it to the components of the thermoplastic vulcanizate. The oil is believed to increase the mobility and diffusion rate of the crosslinking agent in the rubber portion of the thermoplastic vulcanizate. Desirably, the hydrosilylation crosslinking agent is prediluted in oil so that it is from 20 to 80 weight percent active, more desirably from 25 to 75, preferably from 40 to 60, and more preferably from 45 to 55 weight percent active crosslinking agent with the remainder being substantially oil. As previously set forth, the oil increases the mobility of the hydrosilation crosslinking agent (silicon hydride) in the rubber(s) so that it is better dispersed and more effective in generating crosslinks. It has also been discovered that lower molecular weight hydrosilylation crosslinking agents are more efficiently dispersed in the components of the TPV and their use results in higher gel content and/or more efficient crosslinking of the rubber component. A popular hydrosilylation crosslinking agent has been Dow Corning's DC 2-2822 product having, structure where m+n is defined as the degree of polymerization and equals 42 on average and 30 mole percent of the m+n units are n units. The repeat units with an n subscript can be created by alkylating a repeat unit with a subscript m. The n units make the crosslinking agent more soluble in hydrocarbon rubbers. It has been discovered that silicone hydride crosslinkers having a DP of 6 or 8 are more effective than higher DP silicone hydride crosslinkers at equivalent Si-H concentrations. Desirably, the degree of polymerization of the crosslinking agent is up to 30, more desirably from 2 to 20 or 30, and preferably from 2 or 3 to 10 or 15. The amount of silicon hydride compound useful in the process of the present invention can generally range from 0.1 to 10.0 mole equivalents of SiH per carbon-carbon double bond in the rubber, and preferably is in the range of 0.5 to 5.0 mole equivalents of SiH per carbon-carbon double bond in the rubber component of the thermoplastic elastomer. Thermoplastic Resins Thermoplastic resins useful in the compositions produced by the invention. include crystalline polyolefin homopolymers and copolymers. They are desirably prepared from monoolefin monomers having 2 to 20 carbon atoms, such as ethylene, propylene, 1-butene, 1-pentene as well as copolymers derived from linear and cyclic olefins, with propylene being preferred. As used in the specification and claims the term polypropylene includes homopolymers and copolymers of propylene as well as reactor copolymers of polypropylene which can contain 1 to 20 wt% of ethylene or an -olefin comonomer of 4 to 20 carbon atoms, and mixtures thereof. The polypropylene can be crystalline, isotactic or syndiotactic polypropylene. Commercially available polyolefins may be used in the practice of the invention. Other thermoplastic resins which are substantially inert to the rubber, the silicon hydride and the hydrosilylation catalyst would also be suitable. Blends of thermoplastic resins may also be used. The amount of thermoplastic resin found to provide useful compositions is generally from 5 to 90 weight percent, based on the weight of the rubber and resin (total polymer). Preferably, the thermoplastic resin content will range from 20 to 80 percent by weight of the total polymer. Rubbers Unsaturated rubbers useful to prepare thermoplastic elastomers according to the invention include monoolefin copolymer rubbers comprising non-polar, rubbery copolymers of two or more monoolefins (EPR rubber), preferably copolymerized with at least one polyene, usually a diene (EPDM rubber). EPDM is a polymer of ethylene, propylene and one or more non-conjugated diene(s), and the monomer components may be polymerized using Ziegler-Natta or metallocene catalyzed reactions, among others. Typically an EPDM rubber has from 0.5 to 6 or 10 weight percent of a diene (based on the weight of the polymer) and has a molar ratio of repeat units from ethylene to propylene of from 25:75 to 75:25. Satisfactory non-conjugated dienes include 5-ethylidene-2-norbornene (ENB); 1,4-hexadiene (HD); 5-methylene-2-norbornene (MNB); 1,6-octadiene; 5-methyl-1,4-hexadiene; 3,7-dimethyl-1,6-octadiene; 1,3-cyclopentadiene; 1,4-cyclohexadiene; dicyclopentadiene (DCPD); 5-vinyl-2-norbornene (VNB) or a combination thereof. In one embodiment of the invention, it has been found that rubber having a structure in which the diene monomer has carbon-carbon multiple bonds which are predominately unencumbered, i.e. bonds which are sterically unhindered such as terminal or pendant double bonds, provide a greatly improved rate of cure in the hydrosilylation curing process of the invention. Included in this embodiment are structures in which the bonds either normally are unencumbered or are easily isomerized to form a sterically unencumbered double bond, which is then rapidly hydrosilylated, e.g. structures from 1,4-hexadiene or ENB. This improvement is particularly significant where a fully cured rubber component is desired. The use of rubber in which the diene component is selected from the group consisting of 5-ethylidene-2-norbomene, 5-methyl-1,4-hexadiene, 1,4-hexadiene and 5-vinyl-2-norbomene is preferred. A structure from 5-vinyl-2-norbornene is particularly preferred as a diene component of such rubber. Butyl rubbers are also useful in the compositions of the invention. As used in the specification and claims, the term "butyl rubber" includes copolymers of an isoolefin and a conjugated monoolefin, terpolymers of an isoolefin, a conjugated monoolefin and divinyl aromatic monomers, and the halogenated derivatives of such copolymers and terpolymers. The useful butyl rubber copolymers comprise a major portion of isoolefin and a minor amount, usually less than 30 wt%, of a conjugated multiolefin. The preferred copolymers comprise 85-99.5 wt% of a C 4-7 isoolefin such as isobutylene and 15-0.5 wt% of a multiolefin of 4-14 carbon atoms, such as isoprene, butadiene, dimethyl butadiene, 4-methyl-1,4-pentadiene and piperylene. Commercial butyl rubber, useful in the invention, is a copolymer of isobutylene and minor amounts of isoprene. Other butyl co- and terpolymer rubbers are illustrated by the description in U.S.-A-4,916,180. Isobutylene/divinylbenzene is particularly preferred as an elastomer suitable for hydrosilylation crosslinking, as are the halogenated derivatives of butyl rubber such as chlorobutyl and bromobutyl. Copolymer and terpolymers including isobutylene (an isoolefin) and aromatic divinyl monomers are particularly preferred as an elastomer suitable for hydrosilylation crosslinking due to the greater reactivity towards crosslinking of the residual carbon to carbon double bonds from aromatic divinyl monomers. A highly preferred subset of butyl rubbers are those having carbon to carbon double bonds with greater reactivity towards crosslinking reactions than is typically achieved with residual double bonds derived from conjugated dienes. Examples of these double bonds are the residual double bond in aromatic divinyl compounds such as divinylbenzene monomers after copolymerization with isobutylene. The copolymer of at least an isoolefin and an aromatic divinyl monomer desirably comprises from 80 to 99.8 weight percent repeating units from an isoolefin (e.g. isomonoolefin) of 4 to 7 carbon atoms, from 0 to 19.8 weight percent repeating units from an aliphatic polyene (e.g. diene) of 4 to 14 carbon atoms and from 0.2 to 5 weight percent repeating units from an aromatic divinyl compound other than said aliphatic polyene of the formula where the symbol X represents an aromatic nucleus and the symbols R which may be the same or different represent hydrogen atoms or alkyl groups of 1 to 5 carbon atoms. X, the aromatic nucleus, can be any aromatic group including those represented by the benzene ring, the naphthalene rings, pyridine ring, and mono or poly alkyl substituted versions thereof. The preferred isoolefin is isobutylene, the preferred polyene is isoprene, and the preferred aromatic divinyl compound is divinylbenzenc. U.S.-A-3,584,080 discloses a more detailed description of the copolymer. Preferably the repeating units from the polyene is from 0.1 to 5 weight percent of the copolymer. Preferably the repeating units from aromatic divinyl compound is from 0.2 to 4 weight percent (2000 to 40,000 ppm) and more preferably from 0.5 to 3 weight percent (5000 to 30,000 ppm) of the copolymer. It is noted that a large portion of the unsaturated rcpeat units from the aromatic divinyl compound are consumed in reactions during polymerization and are not available as unsaturated units (e.g. they are converted to saturated units) for hydrosilation crosslinking. A preferred butyl rubber thus comprises a copolymer of at least an isoolefin and an aromatic divinyl compound. The repeat units therein with residual unsaturation from an aromatic divinyl compound are desirably present from 50 to 5000 ppm (0.005 to 0.5 wt% based on the total amount of butyl rubber) and more desirably from 200 to 2500 ppm. The repeat units from an isoolefin desirably are from 85 to 99.5 wt% and repeat units from a multiolefin (polyene) of 4-14 carbon atoms can be absent or present in an amount from 0.5 to 15 wt% based on the total amount of repeat units in the butyl rubber copolymer. A percentage of the repeat units from divinylbenzene may be present as repeat units without residual unsaturation. As the repeat units from aromatic divinyl compounds (e.g. divinylbenzene) are very reactive to crosslinking, it is sometimes desirable to dilute the copolymers of isobutylene and aromatic divinyl compounds with more conventional butyl rubbers described in the previous paragraph. A commercial example of a copolymer of isobutylene and divinylbenzene is Polysar Butyl XL 10000 available from Bayer Corporation. Said Polysar Butyl XL 10000 has a Mooney viscosity 1+8 @ 125°C of 60 -75 and 20-30 wt% of the polymer is soluble in cyclohexane. XL 10000 starts with 2000 ppm unsaturated repeat units from divinylbenzene. Butyl rubbers are also available from Bayer as XL 68102 having 1500 ppm unsaturated repeat units from divinylbenzene and Mooney viscosity of 59-75 and as XL 30102 having 600 ppm unsaturated repeat units from divinylbenzene and a Mooney viscosity from 67-83. The products with designations XL 68102 and XL 30102 are believed to be blends of two different butyl rubbers, one with repeat units from divinylbenzene and one without such repeat units (e.g. a butyl rubber of isobutylene and a conjugated diene). An unsaturated repeat unit from an aromatic divinyl compound will desirably have the structure: Where X and R are as previously defined. A close examination of this repeat units reveals that the carbon to carbon double bond has little steric hindrance and mobility with respect to the polymer backbone which may facilitate its reaction with hydrosilation crosslinking agents. Another preferred rubber is an acrylic or alkacrylic group functionalized (modified by adding the functional group) copolymer of at least isobutylene and paramethylstyrene. By the term acrylic or alkacrylic group, applicant means acrylic or alkacrylic or combinations thereof. The term alkacrylic is intended to express that the acrylic can have an alkyl or alkenyl substituent thereon of 1 to 5 carbon atoms, preferably methyl or ethyl. The functionalization reaction involves halogenating the copolymer of isobutylene and paramethyl styrene as set forth in EP-A-0 344 021 (preferably by bromination) and then reacting the brominated polymer with R 2 R 3 C=CR 1 COO - M + such as illustrated below. + R 2 R 3 C=CR 1 COO - M + forms where R 1 and R 2 are H or an alkyl of 1 to 5 carbon atoms and R 3 is H, an alkyl or an alkenyl of 1 to 5 carbon atoms and M + is a counterion such as H + , Na + , K + , etc. The amount of acrylic or alkacrylic groups per polymer chain can vary depending on the properties desired. Desirably, the number of moles of acrylic or alkacrylic or combinations thereof, if both are present, is from 0.1 to 5 mole %, more desirably from 0.3 to 1.5 mole % based on the total moles of repeat units. Desirably, the copolymer of isobutylene and paramethylstyrene comprises repeat units from at least isobutylene and paramethylstyrene. Other copolymerizable monomers can be present in small amounts. The amount of repeating units from isobutylene is desirably from 80 to 99 weight percent, more desirably from 89 to 98 weight percent and the amount of repeat units from paramethylstyrene is from 1 to 20 weight percent and more desirably from 2 to 11 weight percent. While a preferred embodiment is using the acrylic or alkacrylic group, or combinations thereof, functionalized copolymer of isobutylene and paramethylstyrene as the entire rubber component, it is possible to use a blend of said copolymer with the rubbers described herein. Desirably in a blend of the copolymer with other rubbers the copolymer is a majority by weight of the total rubbers in the thermoplastic vulcanizate. A further rubber suitable in the invention is natural rubber. The main constituent of natural rubber is the linear polymer cis-1,4-polyisoprene. It is normally commercially available in the form of smoked sheets and crepe. Synthetic polyisoprene can also be used, with the particularly preferred synthetic polyisoprene elastomers being those that contain vinyl functionality pendant to the main polymer chain, i.e. 1,2-enchainments. Polybutadiene is also a suitable elastomer for hydrosilylation curing with polybutadienes that contain vinyl functionality being the most preferred. Blends of any of the above rubbers may also be employed, rather than a single olefinic rubber. In preparing the compositions of the invention, the amount of rubber generally ranges from 95 to 10 weight percent based on the weight of the rubber and thermoplastic resin (total polymer). Preferably, the rubber content will be in the range of from 80 to 20 weight percent of total polymer. Hydrosilylation Catalysts It has previously been understood that any catalyst, or catalyst precursor capable of generating a catalyst in situ, which will catalyze the hydrosilylation reaction with the carbon-carbon bonds of the rubber can be used. Such catalysts have included transition metals of Group VIII such as palladium, rhodium, platinum and the like, including complexes of these metals. Chloroplatinic acid has been disclosed as a useful catalyst in U.S.-A-4,803,244 and EP-A-651,009, which further disclose that the catalyst may be used at concentrations of 5 to 10,000 parts per million by weight and 100 to 200,000 parts per million by weight based on the weight of rubber, respectively. It has been found in the process of the present invention that significantly lower concentrations of platinum-containing catalyst can be used, while obtaining improvement in both the speeds of the reaction and the efficiency of the crosslinking. Concentrations of catalyst in the range of 0.01 or 0.1 to 10, 20 or 40 parts per million by weight of rubber, expressed as platinum metal are effective in rapidly and completely curing the rubber in the process of dynamically vulcanizing blends of thermoplastic resin and rubber. These low catalyst concentrations are particularly effective in combination with a diene-containing rubber having carbon-carbon multiple bonds which are predominately sterically unhindered. Catalyst concentrations of 0.1 to 4 or 25 parts per million by weight based on the weight of rubber, expressed as platinum metal, are particularly preferred. Platinum-containing catalysts, which are useful in the process of the invention, are described, for example, in U.S.-A-4,578,497; U.S.-A-3,220,972; and U.S.-A-2,823,218. These catalysts include chloroplatinic acid, chloroplatinic acid hexahydrate, complexes of chloroplatinic acid with symdivinyltetramethyldisiloxane, dichloro-bis(triphenylphosphine) platinum (II), cis-dichloro-bis(acetonitrile) platinum (II), dicarbonyldichloroplatinum (II), platinum chloride and platinum oxide. Zero valent platinum metal complexes such as Karstedt's catalyst are particularly preferred, as described in U.S.-A-3,775,452; U.S.-A-3,814,730; and U.S.-A-4,288,345. In order for the catalyst to function most efficiently in the dynamic vulcanization environment, it is important that it is inherently thermally stable, or that its activity is inhibited to prevent too rapid a reaction or catalyst decomposition. Appropriate catalyst inhibitors that are suitable to stabilize the platinum catalyst at high temperatures include 1,3,5,7-tetravinyl-1,3,5,7-tetramethylcyclotetrasiloxane and its higher analogs such as vinyl cyclic pentamer. However, other olefins that are stable above 165° C are also useful. These include maleates, fumarates and the cyclic pentamer. It is also particularly preferred in the invention to use a catalyst that remains soluble in the reaction medium. Additives The thermoplastic elastomer may contain conventional additives, which can be introduced into the composition in the thermoplastic resin, the rubber, or in the blend either before, during or after the hydrosilylation and curing. Examples of such additives are antioxidants, processing aids, reinforcing and nonreinforcing fillers, pigments, waxes, rubber processing oil, extender oils, antiblocking agents, antistatic agents, ultraviolet stabilizers, plasticizers (including esters), foaming agents, flame retardants and other processing aids known to the rubber compounding art. Such additives may comprise from 0.1 to 300 percent by weight based on the weight of the rubber and thermoplastic in the final thermoplastic elastomer product. Fillers and extenders, which can be utilized, include conventional inorganics such as calcium carbonate, clays, silica, talc, titanium dioxide, carbon black and the like. Additives, fillers or other compounds, which may interfere with the hydrosilylation, should be added after curing reaches the desired level. Extender Oil The rubber processing or extender oils used in thermoplastic elastomers generally are paraffinic, naphthenic or aromatic oils derived from petroleum fractions. The type will be that ordinarily used in conjunction with the specific rubber or rubbers present in the composition, and the quantity may range from zero to several hundred parts per hundred parts by weight rubber. Important to the efficiency of the catalyst is that the oils and other additives contain no or very low concentrations of compounds that are catalyst inhibitors or that interfere with the activity of the catalyst. These compounds include phosphines, amines, sulfides, thiols or other compounds that may be classified as Lewis bases. Lewis bases, or other compounds that have a pair of electrons available for donation, will react with the platinum catalyst, effectively neutralizing its activity. It has been discovered that the presence of such compounds has a surprisingly detrimental impact on hydrosilylation curing in the process of dynamic vulcanization of the rubber component of the thermoplastic elastomer compositions. If the concentration of compounds which have the chemical reactivity of Lewis bases, such as compounds containing sulfur or nitrogen, is maintained at or below a level which provides less than 1000 ppm and 300 ppm of sulfur and nitrogen respectively, then the amount of platinum catalyst required to promote efficient hydrosilylation curing in dynamic vulcanization can be substantially reduced, usually to the range of 4 ppm or less, without impact on the cure state of the rubber or the tensile properties of the thermoplastic elastomer product. Concentrations of sulfur and nitrogen below 500 and 200 ppm respectively are more preferred, and concentrations of less than 30 ppm sulfur and less than 100 ppm nitrogen are most preferred. It has been discovered that, even at catalyst concentrations as low as 0.25 ppm, full cure of the elastomer can be achieved if the concentration of sulfur and nitrogen is within the most preferred ranges. Most paraffinic petroleum oils for the rubber industry are derived from a crude oil distillation stream. A typical refining history would include some type of dewaxing to reduce the pour point, a solvent extraction to physically remove aromatic compounds and a hydrotreating process to chemically modify aromatic structures. Both extraction and hydrotreating result in a net increase in the total concentration of saturated hydrocarbon structures and a net decrease in the total aromatic, sulfur and nitrogen-containing compound concentration. The degree of reduction in concentration of these compounds in the oil is dependent upon the type and severity of the refining employed, and the nature of the crude oil. White and paraffinic oils have been treated more extensively than aromatic and napthenic oils and would contain a smaller concentration of aromatic, sulfur and/or nitrogen compounds. It is difficult to elucidate the exact chemical structure of these compounds due to their complexity. The tendency of an oil to interfere with platinum catalyzed hydrosilylation is directly related to the concentration of sulfur and nitrogen containing compounds, as well as compounds which contain phosphorus, tin, arsenic, aluminum and iron. Processing The rubber component of the thermoplastic elastomer is generally present as small, i.e. micro-size, particles within a continuous thermoplastic resin matrix, although a co-continuous morphology or a phase inversion is also possible depending upon the amount of rubber relative to plastic and the degree of cure of the rubber. The rubber is desirably at least partially crosslinked, and preferably is completely or fully crosslinked. It is preferred that the rubber be crosslinked by the process of dynamic vulcanization. As used in the specification and claims, the term "dynamic vulcanization" means a vulcanization or curing process for a rubber blended with a thermoplastic resin, wherein the rubber is vulcanized under conditions of shear at a temperature at which the mixture will flow. The rubber is thus simultaneously crosslinked and dispersed as fine particles within the thermoplastic resin matrix, although as noted above other morphologies may exist. Dynamic vulcanization is effected by mixing the thermoplastic elastomer components at elevated temperatures in conventional mixing equipment such as roll mills, Banbury mixers, Brabender mixers, continuous mixers, mixing extruders and the like. The unique characteristic of dynamically cured compositions is that, notwithstanding the fact that the rubber component is partially or fully cured, the compositions can be processed and reprocessed by conventional plastic processing techniques such as extrusion, injection molding and compression molding. Scrap or flashing can be salvaged and reprocessed. The terms "fully vulcanized" and "fully cured" or "fully crosslinked" as used in the specification and claims means that the rubber component to be vulcanized has been cured or crosslinked to a state in which the elastomeric properties of the crosslinked rubber are similar to those of the rubber in its conventional vulcanized state, apart from the thermoplastic elastomer composition. The degree of cure can be described in terms of gel content, or conversely, extractable components. Gel content reported as percent gel (based on the weight of crosslinkable rubber) is determined by a procedure which comprises determining the amount of insoluble polymer by soaking the specimen for 48 hours in organic solvent at room temperature, weighing the dried residue and making suitable corrections based upon knowledge of the composition. Thus, corrected initial and final weights are obtained by subtracting from the initial weight the weight of soluble components, other than rubber to be vulcanized, such as extender oils, plasticizers and components of the composition soluble in organic solvent, as well as that rubber component of the product which is not intended to be cured. Any insoluble polyolefins, pigments, fillers, and the like are subtracted from both the initial and final weights. The rubber component can be described as fully cured when less than 5%, and preferably less than 3%, of the rubber which is capable of being cured by hydrosilylation is extractable from the thermoplastic elastomer product by a solvent for that rubber. Alternatively the degree of cure may be expressed in terms of crosslink density. All of these descriptions are well known in the art, for example in U.S.-A-4,593,062, 5,100,947 and 5,157,081. The following general procedure was used in the preparation of thermoplastic elastomers (vulcanizates) by the process of the invention, as set forth in the examples. The thermoplastic resin and oil extended rubber were placed in a heated internal mixer with the hydrosilylation agent and hydrosilylation catalyst. The hydrosilylation agent and catalyst can be incorporated into the composition by any suitable technique, for example by injection as solutions in oil or as neat components, although a dilute hydrosilylation solution in oil and a dilute catalyst solution are preferred. Additives such as antioxidants, ultraviolet stabilizers and fillers may also be added as a slurry in oil. Masterbatches of the components may also be prepared to facilitate the blending process. The mixture was heated to a temperature sufficient to melt the thermoplastic component, and the mixture was masticated, with added processing oil if desired, until a maximum of mixing torque indicated that vulcanization had occurred. Mixing was continued until the desired degree of vulcanization was achieved. The order of addition of the hydrosilylation agent and hydrosilylation catalyst was found to be important. Maximum catalyst efficiency was obtained when the hydrosilylation agent was added first to the blend, followed by the hydrosilylation catalyst. The mechanical properties of the thermoplastic elastomer products, as well as the degree of cure, were improved when this order of addition was followed. The invention will be better understood by reference to the following examples, which serve to illustrate but not limit the present process. In the examples, the following test methods were used to determine the properties of the thermoplastic elastomer products. Hardness (Shore A/D) ASTM D 2240 Ultimate tensile strength (UTS - kPa (psi)) ASTM D 412 Ultimate elongation (UE - %) ASTM D 412 Modulus at 100/300% elongation (M1 or M3 - kPa (psi)) ASTM D412 Tension set (TS - %) ASTM D 412 Oil swell (OS - %) ASTM D 471 Heat aging ASTM D 573 The rubber component used in the compositions prepared according to the examples is further identified as follows. Rubber "A" EPDM - 2.1% ENB; 52% ethylene Rubber "B" EPDM - 5% HD; 55% ethylene Rubber "F" EPDM - 3% VNB; 55% ethylene Rubber "G" EPDM - 5.5% ENB; 60% ethylene Rubber "K" EPDM - 1.1% VNB; 64% ethylene Rubber "L" EPDM - 0.7% VNB; 62.6 % ethylene Rubber M Butyl XL 10,000 from Polysar Rubber N Butyl XL 30,102 from Polysar Polypropylene A Polypropylene MFI=0.7 Polypropylene B Homopolypropylene MFI=20 Extender Oil A Sunpar 150M from Sun Chemical 585 ppm sulfur, 164 ppm nitrogen Extender Oil B Sunpar LW 150M from Sun Chemical 19 ppm sulfur, 103 ppm nitrogen Extender Oil C White Oil D-200 from Lyondell 1.0 ppm sulfur, 1.0 ppm nitrogen EXAMPLE 1 Compositions were prepared by the method of the invention as generally described above, using polypropylene resin and EPDM rubber containing various diene components. The plastic and rubber components were melt mixed in a Brabender mixer at 180°C until the polypropylene was melted. Silicone hydride (alkylated methyl hydrogen polysiloxane) was added dropwise to the melt mix, followed by addition of an oil solution containing platinum [platinate (II) hexachloro, dihydrogen reaction product with 2,4,6,8-tetraethenyl-2,4,6,8-tetramethyl cyclotetrasiloxane]. The rubber was dynamically vulcanized by mixing the blend until the maximum torque was reached. The product was removed from the mixer, then returned to the mixer and masticated at 180°C for an additional minute. Plaques were prepared by compression molding the products of the dynamic vulcanization at 200°C to a thickness of 1.524mm (60 mil) and cooling under pressure, and the physical properties were determined using these plaques. All of the products were elastomeric, as defined by ASTM D1566, i.e. all had tension set values of less than 50%. The compositions and their properties are set forth in Table I. Example 1 of U.S.-A-4,803,244 is set forth in comparison to several EPDM rubbers crosslinked with a platinum catalyst. In this comparative example, (Example 1 of U.S.-A-4,803,244) similar resin and rubber components were dynamically vulcanized by hydrosilylation, but the equivalent of 35 ppm of rhodium metal was used as the catalyst COMPOSITION I Patent Ex. 1 of U.S.-A-4,803,244 II III IV Polypropylene A (parts) 67 50 67 41 41 EPDM Rubber "A" (parts) 100 100 -- -- -- EPDM Rubber "B" (parts) -- -- 100 -- -- EPDM Rubber "F" (parts) -- -- -- 100 -- EPDM Rubber "G" (parts) -- -- -- -- 100 Si-H A (phr) 2.5 6.7 3 2.2 3 Rhodium (ppm) -- 35 -- -- -- Platinum (ppm) 15 -- 7.6 4 13 Physical Properties Hardness (A/D) 93/40 88/26 39 D 69 A 63 A UTS, kPa (psi) 17,237 (2500) 5,302 (769) 15, 237(2210) 7,446 (1080) 6,240 (905) UE (%) 405 240 330 211 406 M1 1750 305 1510 636 408 TS (%) 22 43 24 -- -- Gel (5) (corrected for plastic phase) 95 15 92 99 90 The compositions III and IV also contained 130 phr paraffin oil, 42 phr clay, 5 phr wax, 2 phr ZnO It can be seen that the use of much lower levels of platinum catalyst in the hydrosilylation crosslinking of Rubbers A, B, F and G (EPDM rubbers containing 2.1% ENB, 5% HD, 3% VNB, and 5.5% ENB) results in a marked increase in the level of crosslinking (as reflected by gel content) and improved tensile properties in the thermoplastic elastomer, as compared to the use of rhodium as the catalyst. EXAMPLE 2 In order to study the effect of extender oil, compositions were prepared as generally described above using polypropylene resin and EPDM rubber. Masterbatches of rubber were prepared containing three different extender oils with progressively lower aromatic fractions and lower sulfur and nitrogen concentrations. The masterbatch composition was 100 parts rubber, 100 parts extender oil, 42 parts clay, 2 parts zinc oxide and 5 parts wax. The polypropylene (41 parts) was added to this masterbatch of rubber "K" and mixed in a Brabender mixer at 180° C until the polypropylene was melted. Silicone hydride (3 phr) was added dropwise to the mix, followed by addition of an oil solution containing platinum catalyst at various levels. The rubber was dynamically vulcanized by mixing the blend until maximum torque was reached. Additional processing oil (30 parts) was added after the cure. The product was removed from the mixer, then returned to the mixer and masticated at 180° C for an additional minute. Test specimens were prepared by compression molding the products at 200° C, and the oil swell properties were determined by the test method of ASTM D471, using IRM 903 oil at 125°C for 24 hours. The results, expressed as percent swell (or weight gain) of the specimen, are set forth in Table II. Extender Oil A Extender Oil B Extender Oil C Pt Catalyst OS S:Pt N:Pt OS S:Pt N:Pt OS S:Pt N:Pt 0.25 ppm 339 14300 8942 - - - 119 24 55 0.5 285 7150 4471 105 227 2808 92.3 12 23 1.0 222 3575 2236 86.4 114 1404 85.3 6 12 1.9 140 1882 1177 85.8 60 739 85.6 3.2 6 2.4 98 1490 932 93.4 48 585 - - - The relative degree of swelling in oil is representative of the crosslink density of the vulcanized rubber, i.e. higher crosslink density in the rubber results in lower oil swell values. The data in Table II clearly shows that materials prepared using extender oil which has low amounts of sulfur and nitrogen, and where the mole ratio of sulfur or nitrogen to the platinum in the catalyst is low, results in a thermoplastic elastomer product which is much more effectively crosslinked by hydrosilylation. This effect is seen even at extremely low concentrations of catalyst. EXAMPLE 3 The following Table III illustrates the benefit of prediluting the hydrosilylation crosslinker in oil. Effect of Diluting Hydrosilylation Crosslinking Agent Composition 1 Cntrl 2 Cntrl 3 4 5 6 TPV masterbatch (g) 290 290 290 290 290 290 Oil added with crosslinker phr -- -- 1 3 3 9 Crosslinker phr 3 3 3 3 3 3 Pt catalyst (ppm ) 6.2 6.6 7.5 6.2 6.2 6.9 Oil added to masterbatch phr 30 30 29 27 27 21 Physical Properties Shore A 55 54 54 55 54 55 TS% 8.5 8.5 8.0 6.0 6.0 7.0 UTS (kPa (psi)) 5550 (805) 5309 (770) 4688 (680) 6219 (902) 5516 (800) 4688 (680) M100 (kPa (psi)) 2241 (325) 2137 (310) 2206 (320) 2703 (392) 2413 (350) 2620 (380) M300 (kPa (psi)) 4613 (669) 4275 (620) 4275 (620) 5461 (792) 4964 (720) -- UE% 444 460 360 378 360 260 OS% 172 161 159 123 117 119 Gel% 91.6 89.3 93.5 97.6 96.6 96.0 The TPV masterbatch included measured by weight 100 parts EPDM, 41 parts polypropylene A, 100 parts oil, 42 parts clay, 2 parts ZnO, and 5 parts wax. A 53.4g portion of this masterbatch was processed in a Brabender mixer using the recipes in Table III. The EPDM included 3-3.5 wt % repeating units from ethylidene norbomene and 0.25 wt % repeating units from vinylidene norbomene. The examples 1 - 6 illustrate that simple addition of concentrated hydrosilylation crosslinker results in 90% gel while predilution in oil results in 96% gel and desirable changes in other properties. Compositions where the hydrosilylation crosslinker was added in a 50% or 25% active solution in oil had higher gel content than a composition where it was added as a 75% active solution. EXAMPLE 4 Table IV below gives the results of oscillating disc rheometer results on hydrosilylation crosslinking of a blend of rubber L and oil with hydrosilylating agents (silicone hydride) of different degrees of polymerization (DP). The rubber is present as 100 parts by weight and the oil is present at 100 parts by weight. The compositions include 2 phr silicon hydride and 0.75 ppm of platinum as catalyst from United Chemical Technology near Philadelphia expressed as platinum metal per total rubber. The results in this example are associated only with the rubber phase as a plastic phase is not present. Compositions prepared using the lower molecular weight silicone hydrides (DP6 and DP8) show more rapid crosslinking and higher crosslink densities as indicated by shorter TS1 times and larger torque rises as compared to the higher molecular weight silicone hydrides (DP42 and DP54). The compositions for this example were prepared by mixing the rubber and additives in a Brabender mixer at a temperature not exceeding 70°C to prevent premature crosslinking. The oscillating disc rheometer was operated at 200°C. The effect of silicone hydride degree of polymerization on reaction kinetics and total torque rise. DP of silicone hydride TS1 (minutes) TS2 (minutes) Torque Rise (dN/M) 6 0.85 3.27 2.55 8 0.86 3.53 2.53 42 2.21 ---- 1.79 54 3.18 ---- 1.87 EXAMPLE 5 Thermoplastic vulcanizates were prepared from 100 parts EPDM rubber L, 41 parts of polypropylene, 100 parts of oil, 42 parts of clay, and 0.75 ppm of platinum catalyst (expressed as parts by weight platinum metal per a million parts by weight of rubber), wherein all parts are by weight. The amount of hydrosilylation crosslinking agent was an amount that contained the same number of equivalents of silicon hydride bonds as the DP42 crosslinker present at 2 parts by weight per 100 parts by weight rubber. These results in Table V indicate that the compositions resulting from the use of DP6 and 8 silicon hydrides have lower weight gain in the Oil Swell Test and also lower compression set. Both of these tests indicate a generally higher level of crosslinking with equivalent amounts of reactive Si-H bonds from the DP6 and. 8 silicon hydride materials as compared to that achieved with DP42 and 97 silicon hydride materials. The oil swell values versus degree of polymerization of the silicon hydride are also shown in Figure 1. Degree of polymerization of silicon hydride Shore A Hardness UTS kPa (psi) M100 kPa (psi) UE% Oil Swell Weight Gain% Compression Set 6 58 5461 (792) 3427 (497) 188 84 17 8 61 6440 (934) 3206 (465) 267 98 --- 42 60 5571 (808) 3089 (448) 257 106 26 97 57 4826 (700) 2765 (401) 343 155 37 EXAMPLE 6 Thermoplastic vulcanizates were prepared from 100 parts of EPDM rubber L, 50 parts of polypropylene A, 168 parts of oil, 42 parts of clay, and 0.9 ppm of platinum catalyst. The parts are parts by weight. The amount and type of hydrosilylation agent varied as shown in Table VI. While the physical properties (Shore A, M100, UE, UTS and TS did not vary much in Table VI, the oil swell weight gain, ESR, and ACR improved with lower degrees of polymerization (DP) in the hydrosilylation crosslinker. ESR is an extrusion surface rating test ASME D 46.1 where lower values indicate a smoother surface. ACR is similar to ASTM D 3835-96 and stands for automatic capillary rheometer. A lower ACR value indicates that a shorter time is required to extrude a specified amount of TPV through a specified orifice diameter. Lower ESR and ACR values for any formulation are desirable. Historically, as one more tightly crosslinked the rubber phase of a TPV, the ESR and ACR properties worsened dramatically (values increased). As seen in Table VI when the amount of DP8 or DP42 crosslinker is increased the ESR and ACR values worsen (increase). A comparison between compositions prepared with DP8 crosslinkers and DP42 crosslinkers reveals that the oil swell values are lower for compositions prepared from DP8 crosslinkers. Lower oil swell values in the DP8 crosslinked samples indicate higher crosslink density in the rubber phase of the TPV. Consequently, one would expect higher ACR and ESR values in DP8 crosslinked samples. Quite unexpectedly this was not observed. In fact, the ACR and ESR values of the DP8 (2 phr) crosslinked sample were about 30% lower than those of the DP42 (2 phr) crosslinked sample even though the DP8 crosslinked sample had lower oil swell (higher crosslink density). DP 42 2.0 phr DP 42 1.5 phr DP 42 1.0 phr DP 8 2.0 phr DP 8 1.5 phr DP 8 1.0 phr Shore A 66 69 70 67 68 70 M100 (kPa (psi)) 2510 (346) 2606 (378) 2441 (354) 2627 (381) 2379 (345) 2882 (331) UE% 593 505 534 540 516 561 UTS (kPa (psi)) 5392 (782) 5109 (741) 4440 (644) 5757 (835) 4916 (713) 4475 (649) TS% 13 13 15 10.5 13 15 Oil Swell% 128 134 152 111 133 138 ESR 88 66 53 61 39 32 ACR 113 105 71 80 76 59 EXAMPLE 7 This example is a high rubber content TPV comprising 100 parts EPDM rubber L with 5 vinyl-2-norbomene as the diene, 30 parts polypropylene A, 115 parts oil, 10 parts clay, 0.89 ppm of platinum in the form of a platinum catalyst and either 2, 2.5 or 3 phr of a DP42 or DP8 hydrosilylation crosslinker. The physical properties reflect that the DP8 hydrosilylation crosslinker is more efficient on a weight basis than the DP42 material. The Shore A value is generally higher, the M100 is higher, the UE is lower the tension set is the same or lower, and the compression set is lower. More dramatic improvements are seen in the ESR and ACR. The improvement in ESR indicates that more elastic compounds may be prepared using DP8 crosslinkers without sacrificing surface smoothness. The improvement in ACR indicates that compositions.crosslinked with DP8 extrude faster with an equivalent amount of rubber. DP42 2 phr DP8 2 phr DP8 2. 5 phr DP8 3 phr Shore A 58 60 59 58 M100 (kPa (psi)) 1786 (259) 1931 (280) 1903 (276) 1910 (277) UE% 462 426 398 418 UTS (kPa (psi)) 5612 (814) 5612 (814) 5330 (773) 5785 (839) TS% 10 10 10 8.75 CompSet% 26.6 23 25 25.2 ESR 113 54 67 67 ACR 490 392 462 457 EXAMPLE 8 Copolymers of isobutylene and divinylbenzene (Butyl Rubber M & N) were crosslinked with a hydrosilation crosslinking having a degree of polymerization (DP) of 6 in Table VIII. A control (7) using a hydrosilation crosslinking agent of DP 42 was included for comparison purposes. A comparison of compositions 8-11 to composition 7 illustrates that the DP 6 hydrosilation crosslinking agent of compositions 8-11 is much more effective than the DP-42 hydrosilation crosslinking agent of composition 7. Further the amount of hydrosilation crosslinking agent and hydrosilation catalyst was gradually reduced in compositions 9, 10 and 11 by a factor of two thirds and one half respectively. Composition 12 varied in physical properties because the relative amount of polypropylene was increased, resulting in a harder, less elastic composition. Composition 13 varied in physical properties due to the substitution of butyl rubber N for butyl rubber M. Butyl rubber M is Butyl XL 10,000 rubber from Polysar and butyl rubber N is Butyl XL 30,102 rubber from Polysar. The catalyst is PC-085 from Dow-Corning diluted to 1 weight percent active in paraffin oil. The polybutene oil is Parapol 450 from Exxon. ORGANOSILOXANE CURED BUTYL TPV Composition 7 8 9 10 11 12 13 Butyl rubber M 50.00g 50.00 50.25 50.51 50.76 34.01 Buryl rubber N 50.25 Polypropylene B 22.50 22.50 22.61 22.73 22.84 30.61 22.61 Si-H DP= 42 1.50 Si-H DP=6 1.50 1.01 1.01 0.51 0.68 1.01 Catalyst 1.00 1.00 1.01 0.51 0.51 0.68 1.01 (Polybutene) Oil 25.00 25.00 25.13 25.25 25.38 34.01 25.13 Total 100.00 100.00 100.00 100.00 100.00 100.0 100.00 PHYSICAL PROPERTIES Hardness A 5 sec 67 74 74 73 68 87 74 UE% 271 322 252 327 313 249 283 UTS, kPa (psi) 3578 (519) 7577 (1099) 6116 (887) 7074 (1026) 4606 (668) 8081 (1172 3420 (496) M-100, kPa (psi) 2358 (342) 3337 (484) 3351 (486) 3110 (451) 2469 (358) 5722 (830) 2861 (415) Tear Strength, kN/m (pli) 17,519 (100) 23,30 (133) 20,32 (116) 19,62 (112) 18,044 (103) 32,23 (184) 22,60 (129) TensionSet, % 20 13 13 15 15 25 36 Comp.Set, 22 hrs, 70 °C 39 27 28 29 32 43 70

Claims: A process for forming a thermoplastic vulcanizate comprising a) blending a thermoplastic resin and a rubber in the molten state, b) mixing with said blend a 25 to 55 weight percent blend of hydrosilylation crosslinking agent in an oil, said hydrosilylation crosslinking agent having a degree of polymerization from 2 to 10, c) adding a hydrosilylation catalyst to the mixture from step (b), .and d) crosslinking said rubber. A process according to claim 1, wherein said hydrosilylation crosslinking agent is a silicon hyd ride compound. A process according to claim 1, wherein said hydrosilylation catalyst is a platinum containing compound. A process according to claim 1, wherein said thermoplastic resin is polypropylene and said rubber is a monoolefin copolymer rubber. A process according to claim 1, wherein said crosslinking step (d) is carried out dynamically under conditions of heat and shear. A thermoplastic vulcanizate formed by the process of claim 1.

Inventors: GILBERTSON GARY W, MEDSKER ROBERT E, SHEN KUO-SHEIN, WANG DONALD S T, ZHAO JIANQUN, GILBERTSON, GARY W., MEDSKER, ROBERT E., SHEN, KUO-SHEIN, WANG, DONALD S.T., ZHAO, JIANQUN
Applicants: ADVANCED ELASTOMER SYSTEMS, ADVANCED ELASTOMER SYSTEMS, L.P.
Application year: 1999
Main classification: C08L23
IPC codes: C08L101, C08L25, C08L83, C08F8, C08L23, C08L21, C08J3