NANOPARTICLES WITH POLYMER SHELLS

Abstract: The invention provides a method of preparing nanoparticles having at least one polymer shell attached to them, each polymer shell having a selected property or properties. The method comprises attaching initiation monomers to the surfaces of the nanoparticles, contacting the nanoparticles having the initiation monomers attached to them with a transition metal ring-opening metathesis catalyst to activate the initiation monomers, and contacting the nanoparticles with one or more types of propagation monomers of the formula P-L-N under conditions effective so that the monomers are polymerized to form the one or more polymer shells. In the formula P-L-N, N is a cyclic olefin-containing group, P is a moiety which gives each polymer shell a selected property or properties, and L is a bond or linker. The invention also provides polymers formed by polymerizing the propagation monomers. The invention further provides the nanoparticles, the initiation monomers, and propagation monomers of formula P-L-N wherein P is a moiety having a property selected from the group consisting of redox activity, optical activity, electrical activity and magnetic activity, and L and N are defined above. The invention also provides binding monomers of formula B-L-N, wherein B is a binding moiety that binds specifically to an analyte, and N and L are defined above. Finally, the invention provides methods and kits for detecting or quantitating an analyte.

Description: NANOPARTICLES WITH POLYMER SHELLS This application claims benefit of provisional application 60/110,327 filed November 30, 1998. This invention was made with support from ARO through MURI, grant number DAAG55 -97- 1-0133. The U.S. government may have rights in the invention. FIELD OF THE INVENTION This invention relates to nanoparticles having polymer shells attached to them, the polymer shells imparting one or more selected properties to the nanoparticles. This invention also relates to a method of making the nanoparticles which utilizes a transition- metal, ring-opening metathesis polymerization of cyclic olefin derivatives, preferably norboraene derivatives, having a selected property. The method allows for the growth of the polymers off the surfaces of the nanoparticles. The invention also relates to certain novel monomers and polymers and to methods and kits for the detection or quantitation of an analyte. BACKGROUND In recent years, there has been considerable interest in developing methods for assembling nanoscale building blocks into periodic, functional materials. See Storhoff et al., J. Clust. Sci., 8: 179 (1997) and references cited therein, and Brousseau et al., J. Am. Chem. Soc, 120:7645 (1998). These methods rely on access to both novel building block compositions and assembly strategies. With regard to the former, both inorganic and organic compositions are now available. Importantly, some of these building blocks are accessible in macroscopic quantities and in monodisperse form. For example, a variety of methods exist for preparing monodisperse samples of CdS and CdSe particles (Murray et al., J. Am. Chem. Soc, 115:8706 (1993); Weller, Angew. Chem., Int. Ed Engl., 32:41 (1993); Wang and Herron, J. Phys. Chem., 95:525 (1991)) and gold particles (Grabar et al., J. Anal. Chem., 67:735 (1995); Frens, Nature Phys. Sci., 241:20 (1973); Hayat, M.A. (ed.), Colloidal Gold: Principles, Methods and Applications (Academic, San Diego, 1991)) with diameters ranging from 1 to 40 nm. Studies involving these well-defined inorganic particles not only have led to a greater understanding of quantum confinement effects but also the development of new and useful spectroscopic methods (Freeman et al., Science, 267:1629 (1995); Zhu et al., J. Am. Chem. Soc, 119:235 (1997)) and detection technologies (Mirkin et al., Nature, 382:607 (1996); Elghanian et al., Science, 277: 1078 (1997); Storhoff et al., J. Am. Chem. Soc, 120: 1959 (1998)). Similarly, a great deal has been learned from the synthesis, characterization, and study of polymer particle compositions. Goodwin et al., Colloid Polym. Sci., 525:464 (1974); Goodwin et al., Colloid Polym. Sci., 257:61 (1979); Schmitt et al., Adv. Mater., 9:61 (1997); Jose- Yacaman et al., Appl. Phys. Lett., 7:913 (1969); Olsen and Kafafi, J. Am. Chem. Soc, 113:7758 (1991); Spatz et al., Adv. Mater., 8:337 (1996) However, far less is known about such systems with nanoscale dimensions (<100 nm). The development of synthetic methods for preparing structures consisting of nanoparticle cores and organic polymer shells on this size scale would give entry into a new and versatile class of hybrid nanoparticle building blocks. Importantly, if it were possible to control the composition and thicknesses of the polymer shells, one would have unprecedented control over the chemical and physical properties of these novel materials. SUMMARY OF THE INNENTION The invention provides a method of preparing nanoparticles having at least one polymer shell attached thereto, each polymer shell having a selected property or properties. The method comprises attaching initiation monomers to the surfaces of the nanoparticles. Then, the nanoparticles having the initiation monomers attached to them are contacted with a transition metal, ring-opening, metathesis catalyst to activate the initiation monomers. The nanoparticles are also contacted with one or more types of propagation monomers of the formula P-L-N under conditions effective so that the monomers are polymerized to form one or more polymer shells attached to the nanoparticles. In the formula P-L-N, N is a cyclic olefin-containing group, P is a moiety which gives each polymer shell a selected property or properties, and Lisa bond or linker. The invention also provides the nanoparticles, the initiation monomers, and propagation monomers wherein P is a moiety having a property selected from the group consisting of redox activity, optical activity, electronic activity and magnetic activity. The invention further provides a method for detecting or quantitating an analyte comprising contacting a type of the nanoparticles of the invention with a sample suspected of containing the analyte and detecting or measuring the property or properties of the nanoparticles in order to detect or quantitate the analyte. The invention also provides a kit for detecting or quantitating an analyte comprising a container holding a type of the nanoparticles of the invention. In addition, the invention provides a binding monomer. The binding monomer has the formula N - L - B, wherein B is a binding moiety that binds specifically to an analyte, and N and L are defined above. The invention also provides a polymer formed by polymerizing one or more types of the propagation monomers of the invention. These polymers may be used to detect or quantitate an analyte when L comprises a binding moiety B. Thus, the invention also provides a method for detecting or quantitating an analyte comprising contacting a sample suspected of containing the analyte with the polymer and detecting or measuring the property or properties of the polymer in order to detect or quantitate the analyte. In addition, the invention provides a kit for detecting or quantitating an analyte comprising a container holding a polymer of the invention wherein L comprises a binding moiety B. Finally, the invention provides a method of detecting or quantitating an analyte comprising contacting the analyte with a type of binding monomers of the invention so that the binding monomers bind to the analyte. Then, a type of propagation monomers of the invention is added so that the propagation monomers polymerize to form a polymer attached to the analyte. Then, the property(ies) of the polymer attached to the analyte is(are) detected or measured in order to detect or quantitate the analyte. Finally, the invention provides a kit for detecting or quantitating an analyte comprising a container holding a type of binding monomers of the invention, a container holding a type of propagation monomers of the invention, or both. BRIEF DESCRIPTION OF THE DRAWINGS Figure 1: Schematic diagram of the preparation of nanoparticles with block copolymer shells. Shown are the formulas of compounds 1, 2, 3 and 4. In the formula of 1, Ph = phenyl and Cy = cyclohexyl. Figures 2A-H: Figures 2A-E show the H NMR spectra of gold nanoparticles (GNPs) functionalized with a 3 : 1 mixture of 1 -dodecanethiol and 2 (δ 7 to 0 ppm) (Figure 2A), GNPs functionalized with a 3 : 1 mixture of 1-dodecanethiol and 2 (δ 6.3 to 5.2 ppm) (Figure 2B), 2-modified GNPs after treatment with one equivalent of 1 (δ 6.3 to 5.2 ppm) (Figure 2C), 2-modified GNPs after the addition of 20 equiv. of 3 to the ring-opening metathesis polymerization (ROMP) activated GNPs (δ 6.3 to 5.2 ppm) (Figure 2D), and the GNP - poly 3 - poly 4 hybrid system (δ 7 to 0 ppm) (Figure 2E). Figures 2F-H show cyclic voltammetry of the GNP - poly 3 system (Figure 2F), the GNP - poly 3 - poly 4 hybrid (Figure 2G), and poly 3 (Figure 2H). All cyclic voltammetry experiments utilized a gold working electrode, a platinum-gauze counter electrode, and a silver-wire reference electrode. Ferrocene (bis(cyclopentadienyl)iron) was used as an internal reference. Figures 3A-B: Transmission electron microscopy (TEM) images of 2- functionalized GNPs (Figure 3 A) and GNP - poly 3 (Figure 3B). Figure 4: Diagram showing the structures of norbornenyl-containing monomers. Figure 5A: Diagram of an assay for the detection of nucleic acid (Target) using GNP - poly 3. Figure 5B: Diagram of an assay for the detection of nucleic acid using a fluorescent norbornenyl-containing monomer. Figure 6: Graphs of fluorescence emission versus wavelength for monomer 9 (graph A) and GNP - poly 9 (graph B). Figures 7A-B: Diagrams showing cross-linking of polymer-nanoparticle hybrids to produce nanoparticle polymer composites. Figures 8A-B: Formulas of compounds 10-16. DETAILED DESCRIPTION OF THE PRESENTLY PREFERRED EMBODIMENTS Nanoparticles useful in the practice of the invention include metal (e.g., gold, silver, copper, and platinum), semiconductor (e.g., Si, CdSe, CdS, and CdS coated with ZnS), polymer (e.g., polystyrene and polymethylmethacrylate), magnetic (e.g., ferromagnetite), insulator (e.g., SiO 2 ), and superconductor (e.g., colloidal materials. Other nanoparticles useful in the practice of the invention include ZnSe, ZnS, ZnO, TiO 2 , Agl, AgBr, Hgl 2 , PbS, PbSe, PbTe, ZnTe, SiO 2 , CdTe, In 2 S 3 , In 2 Se 3 , In 2 Te 3 , Cd 3 P 2 , Cd 3 As 2 , InAs, InP, GaP, and GaAs. Presently preferred are gold nanoparticles. The size of the nanoparticles is preferably from about 1 nm to about 150 nm (mean diameter). More preferably the nanoparticles are from about 2 to about 100 nm. Most preferably the nanoparticles are from about 2 to about 30 nm. Methods of making metal, semiconductor, and magnetic nanoparticles are well- known in the art. See, e.g., Schmid, G. (ed.) Clusters and Colloids (NCH, Weinheim, 1994); Hayat, M.A. (ed.) Colloidal Gold: Principles, Methods, and Applications (Academic Press, San Diego, 1991); Massart, R, IEEE Transactions OnMagnetics, 17, 1247 (1981); Ahmadi, T.S. et al., Science, 272, 1924 (1996); Henglein, A. et al., J. Phys. Chem., 99, 14129 (1995); Curtis, AC, et al., Angew. Chem., Int. Ed. Engl, 27, 1530 (1988); Brust et al., J. Chem. Soc, Chem. Commun., 801 (1994); PCT application WO 98/21587. Methods of making ZnS, ZnO, TiO 2 , Agl, AgBr, Hgl 2 , PbS, PbSe, ZnTe, CdTe, In 2 S 3 , In 2 Se 3 , Cd 3 P 2 , SiO 2 , Cd 3 s^, InAs, ZnSe, InP, GaP, and GaAs nanoparticles are also known in the art. See, e.g., Weller, Angew. Chem., Int. Ed. Engl, 32, 41 (1993); Henglein, A., Top. Curr. Chem., 143, 113 (1988); Henglein, Chem. Rev., 89, 1861 (1989); Brus, Appl. Phys. A., 53, 465 (1991); Bahncmann, in Photochemical Conversion and Storage of Solar Energy (eds. Pelizetti and Schiavello 1991), page 251; Wang and Herron, J. Phys. Chem., 95, 525 (1991); Olshavsky et al., J. Am. Chem. Soc, 112, 9438 (1990); Ushida et al., J. Phys. Chem., 95, 5382 (1992); PCT application WO 98/21587; Xu et al., Mater. Res. Soc. Symp. Proc, 536, 401-405 (1999); Malik et al., J. Mater. Chem., 8, 1885-1888 (1998); Haggata et al., J. Mater. Chem., 7, 1969-1975 (1997); Pickett et al., J. Mater. Chem., 7, 1855-1865 (1997); Micic et al., J. Lumin., 70, 95-107 (1996); Micic et al., J. Phys. Chem., 99, 7754-9 (1995); and Niano et al., Nanostruct. Mater., 3, 239-44 (1993). In addition, methods of making polymer nanoparticles are well known in the art. See, e.g., PCT application WO 98/21587; Gao, et al., Chin. J. Polym. Sci., 17, 595-601 (1999); Okubo et al., ColloidPolym. Sci., 277, 900-904 (1999); Cairns et al., Langmuir, 15, 8052-8058 (1999); Puig, Rev. Mex. Fis., 45, 18-20 (1999); Chen et al., J. Polym. Sci., Part A: Polym. Chem., 37, 2155-2166 (1999); Landfester et al., Macromolecules, 32, 5222-5228 (1999); Stork et al., Polym. Mater. Sci. Eng., 80, 8-9 (1999); Xiangling et al., Radiat. Phys. Chem., 54, 279-283 (1999); Charreyre et al., J. Bioact. Compat. Polym., 14, 64-90 (1999); Sabel et al., PCT application WO 98/56361; Ming et al., Macromolecules, 32, 528-530 (1999); Schaertl et al., Prog. Colloid Polym. Sci., 110, 285-290 (1998); Li et al., Macromolecules, 31, 6841-6844 (1998); Ming et al., Macromol. Chem. Phys., 199, 1075-1079 (1998); Fritz et al., J. Colloid Interface Sci., 195, 272-288 (1997); Zhang et al., Macromolecules, 30, 6388-6390 (1997); Cammas et al., J. Controlled Release, 48, 157-164 (1997); Larpent et al., React. Fund. Polym., 33, 49-59 (1997); Huang et al., Int. J. Polym. Mater., 35, 13-19 (1997); Holderle et al., Polym. Prepr. (Am. Chem. Soc, Div. Polym. Chem.), 38, 479-480 (1997); Hoelderie, et al., Book oj Abstracts, 213th ACS National Meeting, San Francisco, April 13-1 ', 1997, OLY-206 (1 97); Larpent et al., Macromolecules, 30, 354-362 (1997); Nenier- Julienne et al., Pharm. Ada Helv, 71, 121-128 (1996); Levy et al., PCT applications WO 96/20698 and WO 99/53903; Banerjee et al., Macromolecules, 28, 3940-3 (1995); Maruyama et al., Biomaterials, 15, 1035-42 (1994); Stolnik et al., J. Controlled Release, 30, 57-67 (1994); Paulke et al., Ada Polym., 43, 288-91 (1992); and Mueller, R. H.; Wallis, K. H. Int. J. Pharm., 89, 25-31 (1993). Finally, methods of making superconductor nanoparticles are also well known in the art. See, e. .,Geohegan et al., Appl. Phys. Lett., 74, 3788-3790 (1999); Fukunaga et al., Mater. Trans., JIM, 40, 118-122 (1999); Awano et al., WorldCongr. Part. Technol, 3, 1692-1699 (1998); Fukunaga et al., J. Mater. Res., 13, 2465-2471 (1998); Terrones et al., Appl. Phys. A: Mater. Sci. Process., A66, 307-317 (1998); Reverchon et al., Ind. Eng. Chem. Res., 37, 952-958 (1998); Chhabra et al., Tenside, Surfactants, Deterg., 34, 156-158,160-162,164-168 (1997); Maser et al., Adv. Mater. (Weinheim, Ger.J, 9, 503- 506 (1997); Fukunaga et al., Proc - Electrochem. Soc, 97-2, 24-35 (1997); Eastoe et al., Curr. Opin. Colloid Interface Sci., 1, 800-805 (1996); Chhabra et al., World Surfactants Congr., 4th, 1, 67-99 (1996); Pillai et al., Adv. Colloid Interface Sci., 55, 241-69 (1995); Kumar et al., Mater. Lett., 16, 68-74 (1993); Kumar et al., Appl. Phys. Lett., 62, 765-7 (1993); and Pillai et al, Surfactant Sci. Ser., 66, 227-246 (1997). Suitable nanoparticles are also commercially available from, e.g., Ted Pella, Inc. (gold), Amersham Corporation (gold) and Νanoprobes, Inc. (gold), BBI (gold), Bangs Laboratories (gold, polymers, silica, magnetic), Nector Laboratories (magnetic biopolymer), Polysciences (silica, polymers), Dynal, Inc. (polymer, magnetic), Accurate Polymers (polymer), Polymer Laboratories (polymer), PolyMicrospheres (polymer, magnetic), Sphereotech (polymer, fluorescent, magnetic), Xenopore (polymer), and Interfacial Dynamic Corp. (polymer). Each nanoparticle will have a plurality of initiation monomers attached to it. An "initiation monomer" is a compound comprising a functional group, which allows the initiation monomer to be attached to the nanoparticles, and a cyclic olefin group. The cyclic olefin group is located on the initiation monomer so that, when the initiation monomer is attached to the nanoparticles, the olefin functionality will be accessible to participate in the polymerization of subsequently-added cyclic olefin-containing propagation monomers (described below). This is accomplished by having the cyclic olefin group spaced apart from the functional group on the initiation monomer; preferably the cyclic olefin and the functional groups are at opposite ends of the initiation monomer. Thus, the immobilized initiation monomers, once activated by the addition of a suitable catalyst (described below), provide sites for the polymerization of the subsequently-added propagation monomers and allow for the selective growth of polymer blocks off the surfaces of the nanoparticles. As used herein, "cyclic olefin" means a compound containing 1-3 rings, each ring containing 3 or more carbon atoms, preferably 5-8 carbon atoms, and the compound further containing at least one carbon-carbon double bond in a ring (the "olefin functionality"). The cyclic olefin must be capable of undergoing ring-opening metathesis polymerization (ROMP). A cyclic olefin is capable of undergoing ROMP when it contains sufficient strain in the ring(s) so that a ring-opening reaction will release the strain and provide the thermodynamic driving force for the formation of the polymer. For an estimate of ring strain, consult Greenberg & Liebman, Strained Organic Molecules, page 94 (Academic Press 1978). Preferably the cyclic olefin is norbornene, 7-oxonorbornene, cyclooctene, cyclooctadiene, cyclopentene, or cyclobutene. Most preferably, the cyclic olefin is norbornene. Many compounds are known which can be attached to nanoparticles by means of a functional group (referred to hereinafter as "attachment compounds"). Methods of making these attachment compounds and attaching them to nanoparticles are well known. Preferably, the attachment compounds are stably attached to the surfaces of the nanoparticles by chemisorption of the molecules of the compound onto the nanoparticles or by covalent linkage of the molecules of the compound to the nanoparticles. Suitable attachment compounds for use in the practice of the invention, and the corresponding type(s) of nanoparticles to which they attach, include: a. Compounds ofthe formulaR^H, R X SSR 2 , R'SR 2 , R X NC, R X CN, R'CO.H, or ArSH can be attached to gold nanoparticles; b. Compounds of formula R X SH, ArSH, or (R X ) 3 N can be attached to silver, copper, palladium, and semiconductor nanoparticles; c. Compounds of the formula R^C, R 2 SH, R^SR 2 , or R X SR 2 can be attached to platinum nanoparticles; d. Compounds of the formula R*SH can be attached to GaAs and InP nanoparticles; e. Organosilanes, including compounds of the formula R^iCl j and R 1 Si(OR 2 ) 3 , (R'COO)^ R 1 CH=CH 2 , R x Li and R'MgX, can be attached to Si and SiO 2 nanoparticles; f. Compounds of the formula R^OOH or R^ONHR 2 can be attached to metal oxide nanoparticles; g. Compounds of the formula R^H, R 1 NH 2 , ArNH 2 , pyrrole, or pyrrole derivatives, wherein R 1 is attached to one ofthe carbons ofthe pyrrole ring, can be attached to cuprate high temperature superconductor nanoparticles; h. Compounds of the formula R^OOH can be attached to aluminum, copper, silver, and platinum nanoparticles; and i. Compounds that are unsaturated, such as azoalkanes (R 3 NNR 3 ) and isothiocyanates (R 3 NCS), can be attached to silicon nanoparticles. In the above formulas: R 1 and R 2 each has the formula X(CH 2 ) n and, if a compound is substituted with both R 1 and R 2 , R 1 and R 2 may be the same or different; R 3 has the formula CH^CILJ,,; n is 0-30; Ar is an aryl; and X is -CH 3 ,-CHCH 3 , -COOH, -CO 2 (CH 2 ) m CH 3 , -OH, -CH 2 OH, ethylene glycol, hexa(ethylene glycol), -O(CH 2 ) m CH 3 , -NH 2 , -NH(CH 2 ) m NH 2 , halogen, glucose, maltose, fullerene C60, a cyclic olefin, or a nucleic acid, where m is 0-30. For a description of attachment compounds and their preparation and use, see Xia and Whitesides, Angew. Chem. Int. Ed, 37, 550-575 (1998) and references cited therein; Bishop et al., Curr. Opinion Colloid & Interface Sci., 1, 127-136 (1996); Calvert, J. Vac. Sci. Technol. B, 11, 2155-2163 (1993); Ulman, Chem. Rev., 96:1533 (1996) (alkanethiols on gold); Dubois et al, Annu. Rev. Phys. Chem., 43:437 (1992) (alkanethiols on gold); Ulman, An Introduction to Ultrathin Organic Films: From Langmuir-Blodgett to Self- Assembly (Academic, Boston, 1991) (alkanethiols on gold); Whitesides, Proceedings of the Robert A. Welch Foundation 39th Conference On Chemical Research Nanophase Chemistry, Houston, TX, pages 109-121 (1995) (alkanethiols attached to gold); Mucic et al. Chem. Commun. 555-557 (1996) (describes a method of attaching 3* thiol DNAto gold surfaces); U.S. Patent No. 5,472,881 (binding of oligonucleotide-phosphorothiolates to gold surfaces); Burwell, Chemical Technology, 4, 370-377 (1974) and Matteucci and Caruthers, J. Am. Chem. Soc, 103, 3185-3191 (1981) (binding of oligonucleotides- alkylsiloxanes to silica and glass surfaces); Grabar et al., Anal. Chem., 67, 735-743 (binding of aminoalkylsiloxanes and for similar binding of mercaptoalkylsiloxanes) ; Nuzzo et al., J. Am. Chem. Soc, 109, 2358 (1987) (disulfides on gold); Allara and Nuzzo, Langmuir, 1, 45 (1985) (carboxylic acids on aluminum); Allara and Tompkins,J. Colloid Interface Sci., 49, 410-421 (1974) (carboxylic acids on copper); Her, The Chemistry Of Silica, Chapter 6, (Wiley 1979) (carboxylic acids on silica); Timmons and Zisman, J. Phys. Chem., 69, 984-990 (1965) (carboxylic acids on platinum); Soriaga and Hubbard, J. Am. Chem. Soc, 104, 3937 (1982) (aromatic ring compounds on platinum); Hubbard, Ace Chem. Res., 13, 177 (1980) (sulfolanes, sulfoxides and other functionalized solvents on platinum); Hickman et al., J. Am. Chem. Soc, 111, 7271 (1989) (isonitriles on platinum); Maoz and Sagiv, Langmuir, 3, 1045 (1987) (silanes on silica); Maoz and Sagiv, Langmuir, 3, 1034 (1987) (silanes on silica); Wasserman et al., Langmuir, 5, 1074 (1989) (silanes on silica); Eltekova and Eltekov, Langmuir, 3, 951 (1987) (aromatic carboxylic acids, aldehydes, alcohols and methoxy groups on titanium dioxide and silica); and Lee et al, J. Phys. Chem., 92, 2597 (1988) (rigid phosphates on metals); Lo et al, J. Am. Chem. Soc, 118, 11295-11296 (1996) (attachment of pyrroles to superconductors); Chen et al., J. Am. Chem. Soc, 117, 6374-5 (1995) (attachment of amines and thiols to superconductors); Chen et al., Langmuir, 12, 2622-2624 (1996) (attachment of thiols to superconductors); McDevitt et al., U.S. Patent No. 5,846,909 (attachment of amines and thiols to superconductors); Xu et al, Langmuir, 14, 6505-6511 (1998) (attachment of amines to superconductors); Mirkin et al, Adv. Mater. (Weinheim, Ger.), 9, 167-173 (1997) (attachment of amines to superconductors); Hovis et al, J. Phys. Chem. B, 102, 6873-6879 (1998) (attachment of olefins and dienes to silicon); Hovis et al, Surf. Sci., 402-404, 1-7 (1998) (attachment of olefins and dienes to silicon); Hovis et al, J. Phys. Chem. B, 101, 9581-9585 (1997) (attachment of olefins and dienes to silicon); Hamers et al, J. Phys. Chem. B, 101, 1489-1492 (1997) (attachment of olefins and dienes to silicon); Hamers et al, U.S. Patent No. 5,908,692 (attachment of olefins and dienes to silicon); Ellison et al, J. Phys. Chem. B, 103, 6243-6251 (1999) (attachment of isothiocyanates to silicon); Ellison et al, J. Phys. Chem. B, 102, 8510-8518 (1998) (attachment of azoalkanes to silicon); Ohno et al., Mol. Cryst. Liq. Cryst. Sci. Technol, Sect. A, 295, 487-490 (1987) (attachment of thiols to GaAs); Reuter et al, Mαter. Res. Soc. Symp. Proc , 380, 119-24 ( 1995) (attachment of thiols to GaAs); Bain, Adv. Mαter. (Weinheim, Fed Repub. Ger.), 4, 591-4 (1992) (attachment of thiols to GaAs); Sheen et al, J Am. Chem. Soc, 114, 1514-15 (1992) (attachment of thiols to GaAs); Nakagawa et al., Jpn. J. Appl. Phys., Part 1, 30, 3759-62 (1991) (attachment of thiols to GaAs); Lunt et al., J. Appl. Phys., 70, 7449-67 (1991) (attachment of thiols to GaAs); Lunt et al., J. Vac. Sci. Technol, B, 9, 2333-6 (1991) (attachment of thiols to GaAs); Yamamoto et al, Langmuir ACS ASAP, web release number Ia990467r (attachment of thiols to InP); Gu et al, J. Phys. Chem. B, 102, 9015-9028 (1998) (attachment of thiols to InP); Menzel et al, Adv. Mater. (Weinheim, Ger.), 11, 131-134 (1999) (attachment of disulfides to gold); Yonezawa et al, Chem. Mater, 11, 33-35 (1999) (attachment of disulfides to gold); Porter et al, Langmuir, 14, 7378-7386 (1998) (attachment of disulfides to gold); Son et al, J. Phys. Chem., 98, 8488-93 (1994) (attachment of nitriles to gold and silver); Steiner et al, Langmuir, 8, 2771-7 (1992) (attachment of nitriles to gold and copper); Solomun et al., J Phys. Chem., 95, 10041-9 (1991) (attachment of nitriles to gold); Solomun et al., Ber. Bunsen-Ges. Phys. Chem., 95, 95-8 (1991) (attachment of nitriles to gold); Henderson et al., Inorg. Chim. Ada, 242, 115-24 (1996) (attachment of isonitriles to gold); Hue et al., J. Phys. Chem. B, 103, 10489- 10495 ( 1999) (attachment of isonitriles to gold); Hickman et al, Langmuir, 8, 357-9 (1992) (attachment of isonitriles to platinum); Steiner et al., Langmuir, 8, 90-4 (1992) (attachment of amines and phospines to gold and attachment of amines to copper); Mayya et al, J. Phys. Chem. B, 101, 9790-9793 (1997) (attachment of amines to gold and silver); Chen et al., Langmuir, 15, 1075- 1082 (1999) (attachment ofcarboxylates to gold); Tao, J. Am. Chem. Soc, 115, 4350-4358 (1993) (attachment ofcarboxylates to copper and silver); Laibinis et al, J. Am. Chem. Soc, 114, 1990-5 (1992) (attachment of thiols to silver and copper); Laibinis et al, Langmuir, 7, 3167-73 (1991) (attachment of thiols to silver); Fenter et al, Langmuir, 7, 2013-16 (1991) (attachment of thiols to silver); Chang et al, Am. Chem. Soc, 116, 6792-805 (1994) (attachment of thiols to silver); Li et al, J Phys. Chem., 98, 11751-5 (1994) (attachment of thiols to silver); Li et al, Report, 24 pp (1994) (attachment of thiols to silver); Tarlov et al, U.S. Patent No. 5,942,397 (attachment of thiols to silver and copper); Waldeck, et al, PCT application WO/ 99/48682 (attachment of thiols to silver and copper); Gui et al, Langmuir, 7, 955-63 (1991) (attachment of thiols to silver); Walczak et al., J. Am. Chem. Soc, 113, 2370-8 (1991) (attachment of thiols to silver); Sangiorgi et al, Gazz. Chim. Ital, 111, 99-102 (1981) (attachment of amines to copper); Magallon et al, Book of Abstracts, 215th ACS National Meeting, Dallas, March 29-April 2, 1998, COLL-048 (attachment of amines to copper); Patil et al, Langmuir, 14, 2707-2711 (1998) (attachment of amines to silver); Sastry et al, J. Phys. Chem. B, 101, 4954-4958 (1997) (attachment of amines to silver); Bansal et al., J. Phys. Chem. B, 102, 4058-4060 (1998) (attachment of alkyl lithium to silicon); Bansal et al, J. Phys. Chem. B, 102, 1067-1070 (1998) (attachment of alkyl lithium to silicon); Chidsey, Boole of Abstracts, 214th ACS National Meeting, Las Vegas, NV, September 7- 11, 1997, I&EC-027 (attachment of alkyl lithium to silicon); Song, J. H., Thesis, University of California at San Diego (1998) (attachment of alkyl lithium to silicon dioxide); Meyer et al, J. Am. Chem. Soc, 110, 4914-18 (1988) (attachment of amines to semiconductors); and Brazdil et al. J. Phys. Chem., 85, 1005-14 (1981) (attachment of amines to semiconductors). Suitable initiation monomers for use in the practice ofthe invention include cyclic olefin-containing derivatives of these known attachment compounds having the formula: N - L - A wherein: N is a cyclic olefin-containing group; L is a bond or a linker whereby N is attached to A; and A is an attachment compound-containing group. The identity of A will depend on the identity of the material of which the nanoparticles are composed (see above). In addition to being a bond, L can be a linker. As a linker, L can be any desired chemical group. For instance, L can be a polymer (e.g., polyethylene glycol, polymethylene, protein, peptide, oligonucleotide, or nucleic acid), — COO — , -CH 2 (CH 2 ) m COO-, -OCO-, -R^CH^-NR 1 -, -O(CH 2 ) m - -(CH 2 ) m - O- o o o o c— o— (CHΛ-— o— c— o ; _ R i N __ C H 2 ) m _ R 1 N 66— ( (CCHϋ))m, C- O R' R 1 O n R < _ll I I II ii c_ N _ ( c H 2)m -^— c or c — A (CH 2)m , where R 1 is defined above and m is 0-30. L may also be or comprise a binding moiety B that binds specifically to an analyte (e.g., an antibody or oligonucleotide) (see below). The initiation monomers can be synthesized by methods well known in the art. In particular, the synthesis of the initiation monomers utilizes standard organic chemistry synthetic procedures whereby the cyclic olefin-containing group, N, and the attachment compound-containing group, A, are coupled to each other through a bond or are sequentially coupled to the linker, L. See, e.g., Larock, Comprehensive organic transformations : a guide to functional group preparations (VCH Publishers, New York, NY, 1989) and Comprehensive organic functional group transformations (Katritzky et al., eds., Pergamon Press, New York, 1995). Presently preferred as the initiation monomers for use on a variety of nanoparticles are norbornenyl-containing alkanethiols. Example 1 below describes a method which can be used for the preparation of such initiation monomers. The initiation monomers can be attached to the nanoparticles in the same manner as the attachment compounds are attached to nanoparticles. Such methods are well known in the art. See, e.g., the references cited in the above discussion of attachment compounds. Generally, the nanoparticles and the initiation monomers are simply brought into contact and allowed to remain in contact for a sufficient time so that initiation monomers attach to the nanoparticles. Preferably a mixture of initiation monomers and corresponding attachment compounds (as diluent) are attached to the nanoparticles to reduce crosslinking ofthe initiation monomers and the propagating polymer during the subsequent polymerization. The ratio of initiation monomer to attachment compound that gives optimum results can be determined empirically and will depend on the type of initiation monomer, the type of attachment compound, and the type and size of the nanoparticles. By "corresponding attachment compound" is meant that the initiation monomers and attachment compounds are preferably, but not necessarily, ofthe same general type (e.g., alkanes) and preferably, but not necessarily, have the same functional group (e.g., thiol). After the initiation monomers have been attached to the nanoparticles, the resulting nanoparticles are contacted with a catalyst to initiate the polymerization. The catalyst is a transition metal ring-opening metathesis catalyst. Many such catalysts suitable for use with cyclic olefin derivatives are known. See, e.g., U.S. Patents Nos. 4,250,063, 4,727,215, 4,883,851, 4,945,135, 4,945,141, 4,945,144, 5,146,033, 5, 198,511, 5,266,665, 5,296,566, 5,312,940, 5,342,909, 5,728,785, 5,750,815, 5,831,108, 5,849,851, and references cited therein; Schwab et al, Angew. Chem. Int. Ed. Engl, 34:2039 (1995); Lynn et al, J. Am. Chem. Soc, 120:1627 (1998). Preferred are a family of function-group tolerant catalysts having the following formula: wherein: M may be osmium (Os) or ruthenium (Ru); R 1 is hydrogen; X 1 and X 2 may be different or the same and are any anionic ligand; L 1 and L 2 may be different or the same and are any neutral electron donor; and R 2 may be hydrogen, substituted or unsubstituted alkyl, or substituted or unsubstituted aryl. X 1 and X 2 are most preferably the same and are -Cl L 1 and L 2 are preferably phosphines of the formula PhosR 3 R 4 R 5 , where Phos is phosphine, R 3 is a secondary alkyl or cycloalkyl, and R 4 and R 5 (which may be the same or different) are aryl, C,-C 10 primary alkyl, secondary alkyl, or cycloalkyl. L 1 and L 2 are most preferably the same and are -Phos(cyclohexyl) 3 ,-Phos(cyclopentyl) 3 , or - Phos(isopropyl) 3 . Preferably, R 2 is hydrogen, C,-C 20 alkyl, or aryl. The C J -C JO alkyl may optionally be substituted with one or more aryl, halide, hydroxy, C,-C 20 alkoxy, or C 2 -C 20 alkoxycarbonyl groups. The aryl may optionally be substituted with one or more C r C 20 alkyl, aryl, hydroxyl, C,-C 5 alkoxy, amino, nitro, or halide groups. The most preferred catalyst is compound 1 shown in Figure 1. The preparation of these catalysts and conditions for their use are described in Schwab et al, Angew. Chem. Int. Ed Engl, 34:2039 (1995), Lynn et al, J. Am. Chem. Soc, 120:1627 (1998), and U.S. Patent No. 5,831,108, the complete disclosures of which are incorporated herein by reference. These catalysts produce a living polymerization having numerous attributes, including exceptional control over polymer length and chemical composition, and particle size, solubility, and shape. Also preferred is a family of catalysts comprising a rhenium (Nil) atom centrally linked to an alkylidene ligand (CR 1 ), an alkylidyne ligand (CHR 2 ), and two other ligands (R 3 and R 4 ), at least one of which is an electron withdrawing ligand which is sufficiently electron withdrawing to render the rhenium atom electrophilic enough for metathesis reactions. Thus, the catalysts have the formula Re(CR x )(CHR 2 )(R 3 )(R 4 ). R 1 is selected from the group consisting of an alkyl having 1-20 carbon atoms, an aryl having 6-20 carbon atoms, an araalkyl having 7-30 carbon atoms, halogen substituted derivatives of each, and silicon-containing analogs of each. R 2 is selected from the group consisting of R 1 or is a substituent resulting from the reaction ofthe Re=CHR 2 moiety ofthe catalyst with an olefin that is being metathesized. Examples of R 1 and R 2 include phenyl, t-butyl, trimethylsilyl, triphenyl, methyl, triphenylsilyl, tri-t-butyl, tri-t-butylsilyl, 2,6- diisopropylphenyl, 2,4,6-triisopropylphenyl, and2,6-dimethylphenyl R 3 andR 4 canbeany group which is sufficiently electron withdrawing to render the rhenium atom electrophilic enough for metathesis reactions. While it is preferably that both R 3 and R 4 be electron withdrawing, the catalysts may contain only one electron withdrawing ligand. R 3 and R 4 can be individually selected from groups consisting of R 1 , a halogen, triflate, and concatenated combinations of R 3 and R 4 , wherein R 3 and R 4 individually may contain alkoxide oxygen atoms which are bound to the rhenium atom, provided that when R 1 and R 2 are t-butyl and R 3 and R 4 are the same, then R 3 and R 4 are groups other than t- butoxide, trimethylsiloxide, neopentyl or a halogen. Preferably R 3 and R 4 are both alkoxide ligands in which the alcohol corresponding to the electron withdrawing alkoxide ligands should have a pKa of about 9 or below. Suitable ligands which fall within this range include phenoxide, hexafluoro-t-butoxide and diisopropylphenoxide. Examples of concatenated R 3 and R 4 groups are pinacolate, 2,6-dimethyl-2,6-heptanediolate and propan-l,3-diolate. The catalysts are typically monomers. However, they can form dimers, oligomers or polymers if the R 3 and R 4 groups are small enough to permit bridging of two or more metal centers. These rhenium catalysts and their synthesis and use are described in U.S. Patent No. 5, 146,033, the complete disclosure of which is incorporated herein by reference. An additional group of preferred catalysts are those having the formula: M(NR 1 )(OR 2 ) 2 (CHR 3 ). M is molybdenum or tungsten; R 1 and R 2 are alkyl, aryl, aralkyl, haloalkyl, haloaryl, haloaralkyl or a silicon-containing analog thereof; and R 3 is alkyl, aryl, aralkyl or a substituent resulting from the reaction ofthe M=CHR 3 moiety of said catalyst with an olefin being metathesized. The alkyls contain 1-20 carbon atoms, the aryls contain 6-20 carbon atoms, and the araalkyls contain 7-20 carbon atoms. Examples of R 1 include 2,6-diisopropylphenyl, 2,4,6-trimethylphenyl, 2,6-di-t-butylphenyl, pentafluorophenyl, t- butyl, trimethylsilyl, triphenylmethyl, triphenylsilyl, tri-t-butylsilyl, and perfluoro-2-methyl- 2-pentyl Examples ofR 2 include t-butyl, trifluoro-t-butyl, perfluoro-t-butyl, perfluoro-2- methyl-2-pentyl, 2,6-diisopropylphenyl, pentafluorophenyl, trimethylsilyl, triphenylsilyl, tri-t-butylsilyl, and hexafluoro-t-butyl R 3 is initially t-butyl or phenyl but, since the M=CHR 3 moiety ofthe catalyst is intimately involved in the catalytic reaction, the CHR 3 ligand is replaced by another alkylidene fragment from the olefins that are being metathesized. This family of catalysts and their synthesis and use are described in U.S. Patent No. 4,727,215, the complete disclosure of which is incorporated herein by reference. The initiation monomers are activated with the catalyst by methods known in the art. See, e.g., those references cited above. Other suitable conditions and optimum conditions can be determined empirically. After activation of the initiation monomers with the catalyst, a cyclic olefin- containing propagation monomer is added, and the propagation monomers are polymerized. The propagation monomers have the formula: N - L - P wherein: N is a cyclic olefin-containing group; L is a bond or a linker whereby N is attached to P; and P is any moiety which provides a selected property to the resulting polymer. L is the same as described above for the initiation monomers. P will impart a desired property to the resulting polymer and polymer-nanoparticle hybrids. Such properties include hydrophilicity, hydrophobicity, optical properties (e.g. , fluorescence, color, or non-linear optical character), magnetic activity (e.g., unpaired electron), electronic activity (e.g., conducting polymer), selective ion binding (e.g., binding of Na + , Pb 2+ , etc.,) using crown-ethers, and redox activity (e.g., ferrocene derivatives). Preferably, the property is an optical property or redox activity. Many suitable cyclic olefin-containing propagation monomers are known. See, e.g., U.S. Patents Nos. 4,250,063, 5,064,919, 5,117,327, 5,198,511, 5,200,470; Davies et al, J. Chem. Soc. Per/an I, 433 (1973); Posner et al, Tetrahedron, 32, 2281 (1976). Other cyclic olefin-containing propagation monomers can be synthesized by standard organic chemistry synthetic procedures. In particular, the cyclic olefin moiety, N, and the moiety, P, are coupled to each other through a bond or are sequentially coupled to the linker, L, using well-known methods. See, e.g., Larock, Comprehensive organic transformations : a guide to functional group preparations (NCH Publishers, New York, NY, 1989) and Comprehensive organic functional group transformations (Katritzky et al, eds., Pergamon Press, New York, 1995). The synthesis of some propagation monomers is described in the Examples below. Suitable conditions for polymerizing the propagation monomers include those known in the art for polymerizing cyclic olefin and cyclic olefin derivatives. See, e.g., U.S. Patents Nos. 4,883,851, 4,945, 135, 4,945,141, 4,945,144, 5,198,511, 5,266,665, 5,296,437, 5,296,566, 5,312,940, 5,342,909, 5,728,785, 5,750,815, 5,831,108, 5,849,851, and references cited therein; Schwab et al, Angew. Chem. Int. Ed. Engl, 34:2039 (1995); Lynn et al., J. Am. Chem. Soc, 120:1627 (1998). Other suitable conditions and optimum conditions can be determined empirically. In the polymerization, a single propagation monomer having a particular P group or a mixture of monomers having different P groups can be used to form a single polymer shell having a single or a plurality of properties. Also, polymerization of a single monomer or a mixture of monomers can be followed by polymerization of one or more additional monomers, together or singly, to form a plurality of polymer shells attached to the nanoparticles, each shell having a different property or properties. The polymerization, and the resulting size(s) and properties ofthe polymer shell(s), can be controlled by suitable choices ofthe reaction conditions, including the catalyst, solvent, temperature, the type(s)of propagation monomer(s), the order of addition ofthe propagation monomer(s), and the amount(s) ofthe propagation monomer(s). Preferably, for greater control, the polymerization is halted by the addition of a compound that terminates polymerization. Suitable compounds are known in the art. See, e.g., those references cited above. The polymer-nanoparticle hybrids of the invention have a variety of uses. For instance, they can be used as probes to detect or quantitate analytes. See, e.g., PCT application WO 98/04740; PCT application WO 98/21587; Storhoff et al, J. Clust. Sci., 8:179 (1997); Brousseau et al, J. Am. Chem. Soc, 120:7645 (1998); Freeman et al., Science, 267: 1629 (1995); Zhu et al, J. Am. Chem. Soc, 119:235 (1997); Mirkin et al, Nature, 382:607 (1996); Elghanian et al, Science, 277:1078 (1997); Storhoff et al, J. Am. Chem. Soc, 120:1959 (1998). Analytes that can be detected or quantitated according to the invention include polysaccharides, lipids, lipopolysaccharides, proteins, glycoproteins, lipoproteins, nucleoproteins, peptides, oligonucleotides, and nucleic acids. Specific analytes include antibodies, immunoglobulins, albumin, hemoglobin, coagulation factors, peptide and protein hormones (e.g., insulin, gonadotropin, somatotropin), non-peptide hormones, interleukins, interferons, other cytokines, peptides comprising a tumor-specific epitope (i.e., an epitope found only on a tumor-specific protein), cells (e.g., red blood cells), cell- surface molecules (e.g., CD antigens, integrins, cell receptors), microorganisms (viruses, bacteria, parasites, molds, and fungi), fragments, portions, components or products of microorganisms, small organic molecules (e.g., digoxin, heroin, cocaine, morphine, mescaline, lysergic acid, tetrahydrocannabinol, cannabinol, steroids, pentamidine, and biotin), etc. Nucleic acids and oligonucleotides that can be detected or quantitated include genes (e.g., a gene associated with a particular disease), viral RNA and DNA, bacterial DNA, fungal DNA, mammalian DNA (e.g., human DNA), cDNA, mRNA, RNA and DNA fragments, oligonucleotides, synthetic oligonucleotides, modified oligonucleotides, single-stranded and double-stranded nucleic acids, natural and synthetic nucleic acids, etc. To serve as probes, the polymer-nanoparticle hybrids must have a binding moiety, B, attached to them that allows the polymer-nanoparticle hybrids to bind specifically to the analyte. Suitable binding moieties and methods of making them are well known in the art. For instance, essentially any analyte can be detected or quantitated using antibodies specific for the analyte. In addition, any molecule which binds specifically to the analyte can be used, and many such molecules are known in the art. For instance, nucleic acids can be detected or quantitated using oligonucleotides having a sequence which is complementary to at least a portion ofthe analyte nucleic acid. Also, lectins can be used to detect or quantitate polysaccharides and glycosylated proteins. As another example, a receptor can be used to detect its ligand and vice versa. Many other suitable binding moieties, B, are known. The binding moiety B can be attached to the polymer-nanoparticle hybrids in a variety of ways. For instance, as noted above, the linker L ofthe initiation monomer or propagation monomer may be any desired chemical group. Thus, the linker L in the propagation monomer and/or the initiation monomer may comprise a binding moiety B, such as a protein (e.g., antibody), an oligonucleotide, etc., and the binding moiety will be incorporated into the polymer shell(s) attached to the nanoparticles. Preferably, when the polymer-nanoparticle hybrids are used as probes, at least some of the propagation monomers have a linker L which comprises a desired binding moiety B. Alternatively, or in addition, a separate binding monomer may be attached to the polymer-nanoparticle hybrids after the polymerization ofthe propagation monomers has been completed. The binding monomers have the formula: N - L - B, wherein: N is a cyclic olefin-containing group; L is a bond or a linker whereby N is attached to B; and B is a binding moiety. L is the same as described above for the initiation monomers and propagation monomers. Preferably, however, L does not comprise a binding moiety B. The binding monomers are synthesized and attached to the polymer-nanoparticle hybrids in the same manner as the propagation monomers. The binding monomers or, preferably, a mixture of binding monomers and propagation monomers having a desired property or properties may be attached to the polymer-nanoparticle hybrids to form a final polymer shell on the nanoparticles. The ratio of binding monomers to propagation monomers in such a mixture is preferably as low as possible. In this manner, even a single instance ofthe binding of B to its analyte can lead to a large detectable signal. To perform an assay according to the invention, a sample suspected of containing an analyte is contacted with a type of polymer-nanoparticle hybrids having binding moieties B attached thereto. Any type of sample can be used. For instance, the sample may be a biological fluid (e.g., serum, plasma, blood, saliva, and urine), cells, cell lysates, tissues, libraries of compounds (e.g., organic chemicals or peptides), solutions containing PCR components, etc. Conditions and formats for performing such assays are well known in the art (see, e.g. , the references cited above) or can be determined empirically by those of ordinary skill in the art. Finally, the property or properties ofthe polymer attached to the nanoparticles is (are) detected or measured in order to detect or quantitate the analyte. The properties are those described above. Preferably, the property is redox activity or optical activity (e.g., fluorescence or color). Methods of detecting and measuring these properties are well known in the art. One format for detecting or quantitating nucleic acids is illustrated in Figure 5A. As illustrated in Figure 5 A, capture oligonucleotides (Capture Strand) are attached to a gold substrate (e.g., a gold electrode). Methods of attaching oligonucleotides to gold and other substrates are known. See, e.g., those references cited above describing functional groups, particularly PCT application WO 98/0470. The capture oligonucleotides have a sequence complementary to at least a portion ofthe sequence of a nucleic acid analyte (Target), and the analyte nucleic acid is contacted with the substrate so that it binds to the capture oligonucleotides attached to the substrate. Then, polymer-nanoparticle hybrids having oligonucleotides attached to them are contacted with the analyte nucleic acid attached to the substrate. The oligonucleotides on the polymer-nanoparticle hybrids have a sequence complementary to at least a portion ofthe sequence ofthe analyte nucleic acid and bind to the analyte nucleic acid attached to the substrate. After removing unbound materials, the property of the polymer attached to the nanoparticles is detected or measured. As illustrated in Figure 5 A, the polymer is poly 3, a polymer which has redox activity, and this activity can be measured by cyclic voltammetry (see Example 1). The invention further provides a kit for performing the assays for detecting or quantitating analytes. The kit comprises a container holding polymer-nanoparticle hybrids having binding moieties, B, attached to them. The kit may also contain other reagents and items useful for performing the assays. The reagents may include controls, standards, PCR reagents, hybridization reagents, buffers, etc. Other items which be provided as part of the kit include reaction devices (e.g., test tubes, microtiter plates, solid surfaces (possibly having a capture molecule attached thereto), syringes, pipettes, cuvettes, containers, etc. The polymer-nanoparticle hybrids ofthe invention are also a new and versatile type of building block that chemists and material scientists can easily incorporate into many existing particle assembly strategies. See, e.g., PCT application WO 98/04740; Storhoff et al, J. Clust. Sci., 8:179 (1997). For instance, after forming the desired polymer shell(s) on the nanoparticles, the polymers could be reacted with a small amount of either a termination monomer or a propagation monomer containing a functional group so that at least some ofthe polymers on the nanoparticles would be capped with functional groups that would allow the polymer-nanoparticle hybrids to be attached to other nanoparticles (made of the same or a different material) or to solid substrates made of metal, magnetic or semiconductor materials (see above description ofthe materials from which the nanoparticles are made). "Termination monomers" are the same as the initiation monomers described above, and the "functional groups" referred to in this paragraph are the same ones referred to in the discussion of initiation monomers. The novel cyclic olefin-containing monomers of the invention can also be polymerized alone (i.e., not attached to nanoparticles) in the same manner as described above. Such polymers can be used in a variety of ways. For instance, polymers composed of propagation monomers wherein L comprises a binding moiety B (e.g., an oligonucleotide) can be used to detect and/or quantitate analytes by detection of the property or properties ofthe P groups. The invention further provides a kit for performing the assays for detecting or quantitating analytes. The kit comprises a container holding polymers formed from propagation monomers wherein L comprises a binding moiety B . The kit may also contain other reagents and items useful for performing the assays. Further, propagation monomers wherein L comprises a binding moiety B can be used to detect and/or quantitate analytes by detection ofthe property or properties ofthe P groups. For instance, a format useful for the detection or quantitation of nucleic acids is illustrated in Figure 5B. In this format, a single strand of DNA, F, is synthesized and modified at its 3' end to incorporate a functional group (e.g., an amino group) which is used for attachment ofthe DNA to a substrate (e.g., a transparent glass slide). See the discussion above of functional groups and their attachment to substrates. The sequence of F is complementary to at least a portion ofthe sequence of a target DNA, F'-H-G'. The G' sequence ofthe target DNA is complementary to a third DNA strand G which has been modified with a cyclic olefin-containing group (e.g. , as illustrated, a norbornene group, prepared using the phosphoramidite D). After contacting the substrate having capture DNA F attached thereto with a sample suspected of containing the target DNA for a time sufficient to allow the target DNA to hybridize to F, the substrate is then contacted with G. After a time sufficient to allow G to hybridize to the target DNA, the substrate is then treated with a ROMP catalyst (e.g, catalyst 1, Figure 1), followed by exposure to a cyclic olefin-containing fluorescent monomer (e.g., norbornene-modified fluorescein monomer E in hexanes) to produce fluorescent polymers attached to the DNA attached to the substrate. Since the cyclic olefin-modified DNA strand G is not complementary to the capturing strand F, exposing the substrate to the catalyst and then the fluorescent monomers will yield immobilized fluorescent polymer only if the target strand is present in the initial sample. Since a large excess of fluorescent monomer is used, the degree of polymerization on the substrate is dependent upon the reaction time, which is a tailorable quantity. The fluorescence can be readily detected using a fluorescence microscope. This strategy allows for the high sensitivity and flexibility for DNA detection and quantitation for a number of reasons. First, any target can be detected as long as the sequences ofthe ends of the strand (F' and G') are known. Second, by using two shorter DNA strands, F and G, complementary to the target, the DNA synthetic chemistry becomes easier and more quantitative than using a longer strand (e.g., F-G or F-H-G). Finally, since a single hybridization event can lead to the surface attachment of hundreds of fluorescent monomers, this technique can be ultra-sensitive (i.e., capable of detecting sub-femtomolar levels of DNA). Of course, other propagation monomers comprising different binding moieties and/or having different properties can also be used in this format for the detection of DNA and other analytes. Finally, the invention provides a kit for performing the assays for detecting or quantitating analytes. The kit comprises a container holding propagation monomers wherein L comprises a binding moiety B. The kit may also contain other reagents and items useful for performing the assays. As used herein, "a type of refers to a plurality ofthe specified material having the same properties. For instance, "a type of nanoparticles refers to nanoparticles which are the same (e.g., gold nanoparticles of a particular size). Similarly, "a type of polymer- nanoparticle hybrids having binding moieties B attached to them refers to a plurality of nanoparticles having the same polymer(s) and binding moieties attached to them. EXAMPLES Example 1 This example describes the preparation of new metal-organic hybrid nanoparticles by the controlled growth of polymers from the surface of gold nanoparticle templates by ring-opening metathesis polymerization (ROMP) as illustrated in Figure 1. In this methodology, a norbornenyl-terminated linear alkanethiol (2) is used to modify the surfaces of organic-soluble gold nanoparticles (GNPs). Then, a functional group tolerant ROMP catalyst (1) is used to initiate polymerization directly from the particle surface, after which a norbornenyl-containing monomer feedstock is injected into the solution with the initiated nanoparticles. Two proof-of-concept systems are presented. The first involves GNPs with a polymerized shell of a redox-active norbornenyl-functionalized ferrocene 3. The second involves GNPs functionalized with an initial block of 3 followed by a second block of another redox-active norbornenyl-containing monomer 4. The redox-potential of 4 is 220 mV more negative than that of 3, and the two can be easily differentiated by cyclic voltammetry. 1 HNMR spectroscopy, cyclic voltammetry, and transmission electron microscopy (Figures 2A-H and Figures 3A-B) have been used to characterize the polymerization process and the resulting polymer-modified nanoparticles. These studies indicate that the synthesis strategy can be used to prepare a new class of metal-organic hybrid nanoparticles that can be functionalized with polymeric layers of virtually any norbornenyl-containing or cyclic olefin-containing monomer. Since the process is a living polymerization, the attributes of this strategy are numerous, including exceptional control over polymer length and chemical composition, and particle size, solubility and shape. A. Materials And General Methods Unless otherwise noted, all reactions were carried out under a dry nitrogen atmosphere using standard Schlenk techniques or in an inert-atmosphere glovebox. Acetonitrile and dichloromethane were distilled over calcium hydride. Tetrahydrofiiran (THF), benzene and diethyl ether were distilled over sodium/benzophenone. All solvents were distilled under nitrogen and saturated with nitrogen prior to use. Deuterated solvents were purchased from Cambridge Isotope Laboratories and used without further purification, except for CDC1 3 , which was distilled over calcium hydride and vacuum transferred into an air-tight solvent bulb prior to transfer into the inert-atmosphere glovebox. Compounds 1, 2, 3, and 4 were synthesized as described below. All other reagents were purchased from Aldrich Chemical Company and used without further purification, unless otherwise noted. 1 HNMR and 13 CNMR spectra were recorded on a Narian Gemini 300 MHz FT-ΝMR spectrometer. For 1 HΝMR of samples containing gold nanoparticles, the line broadening was set at 1 Hz. GC-MS experiments were recorded on a Hewlett-Packard HP 6980 Series instrument equipped with an HP 5 column (the initial temperature was set at 50°C for 2 minutes with a ramp of 20°C per minute and a final temperature of 280°C). Transmission electron microscopy (TEM) was performed on a Hitachi 8100 microscope. High resolution mass spectroscopy (HRMS) was performed on a NG 70-SE instrument. Elemental analysis was performed by Atlantic Microlab Inc. All flash column chromatography was performed using a 56 mm inner- diameter column using a 200 cm-long column of silica gel under a positive pressure of nitrogen, unless otherwise noted. B. Synthesis of Catalyst 1 Catalyst 1 was synthesized using published procedures. Schwab et al, Angew. Chem., Int. Ed. Engl, 34:2039 (1995); Lynn et al., J. Am. Chem. Soc, 120: 1627 (1998). C. Synthesis of l-mercapto-10-(exo-5-norbornen-2-oxyVdecane (2) There are two key steps in the synthesis of metathesis-ready GΝPs. The first involves the synthesis and characterization of l-mercapto-10-(exo-5-norbornen-2-oxy)- decane, 2, which contains a ROMP-active norbornene segment attached to a long-chain alkanethiol Theexo- rather than the endo-isomer was chosen to optimize ROMP activity. Wolfe, P.S., Ph.D. dissertation, University of Florida (1997). To prepare 2, exo-5-norbornen-2-ol (Posner et al, Tetrahedron, 32:2281 (1976); Davies et al, J. Chem. Soc. Perkinl, 433 (1973); 1.00 g, 9.1 mmol) was weighed into a 50 mL Schlenk flask in an inert atmosphere glovebox. THF (15 ml) was added, and the solution was stirred vigorously while oil-free sodium metal (250 mg, 10.8 mmol) was added. The mixture was then taken out ofthe glovebox, refluxed for 12 hours under a positive stream of nitrogen, and allowed to cool to room temperature. In a separate 100 mL Schlenk flask, 10-chloro-decyltoluene-4 sulfonate (Tomohiro et al, Synthesis, 7:639 (1992)) (2.95 g, 9.5 mmol) was dissolved in THF (15 mL), and the flask was capped with a pressure-equalizing dropping funnel. The cooled solution of deprotonated exo-5- norbornen-2-ol was then transferred to the pressure-equalizing dropping funnel by cannula (excess Na was quenched with isopropanol) and slowly added to the decyl sulfonate ester solution with vigorous stirring over a period of 10 minutes. The dropping funnel was then replaced with a condenser, and the mixture was refluxed for an additional 12 hours under a positive stream of nitrogen. Upon cooling to room temperature, the reaction mixture was poured into ether (50 mL) and washed successively with water (50 mL), 0.1 M NaOH (50 mL), and brine (50 mL). The organic layer was collected, dried over sodium sulfate and filtered through a Buchner funnel. The solvent was removed on a rotary evaporator. Column chromatography ofthe slightly yellow oil on silica gel with 8% ether in hexanes as the eluent gave 1.94 g (6.9 mmol, 81 %) of 1 -chloro- 10-(exo-5-norbornen-2- oxy)-decane as a clear oil 1 HNMR (CDC1 3 ): 1.05 (m, 20H), 3.56 (s, 1H), 3.72 (s, 1H), 3.95 (m, 5H), 5.80 (m, 1H), 6.31 (m, 1H). 13 CNMR(CDC1 3 ): 26.33, 26.92, 28.92, 29.45, 29.49, 29.52, 30.12, 32.69, 34.48, 40.40, 45.26, 45.99, 46.44, 69.34, 80.22, 133.32, 140.61. GC-MS: One peak, retention time, 10.16 min; M + : 284 m/z. Potassium thioacetate (240 mg, 2.1 mmol) and the l-chloro-10-(exo-5-norbornen- 2-oxy)-decane (500 mg, 1.8 mmol) were weighed into separate 50 mL Schenk flasks in an inert atmosphere glovebox. The flasks were taken out ofthe glovebox, and degassed ethanol (lOmL) was transferred to each flask by cannula. The solution of 1 -chloro- 10- (ejrø-5-norborn-2-oxy)-decane was then transferred to the potassium thioacetate solution by cannula, and the mixture was refluxed for 20 hours under a positive stream of nitrogen. Upon cooling to room temperature, the mixture was poured into H 2 O (50 mL) and extracted with CH 2 C1 2 (3 x 50 mL). The combined organic extracts were washed with brine (3 x 50 mL), dried over sodium sulfate, and filtered through a Buchner funnel. The solvent was removed on a rotary evaporator. Column chromatography ofthe yellow oil on silica gel with CH 2 C1 2 as the eluent gave 488 mg of l-(exo-5 norbornen-2-oxy)-10- (thioacetyl)-decane(1.5 mmol, 85%)asaclearoil 1 HNMR(CHC1 3 ): 1.35 (m, 15H), 1.58 (m, 4H), 1.72 (d, 1H), 2.83 (s, 1H), 2.9 (t, 3H), 3.48 (m, 3H), 5.93 (m, 1H), 6.20 (m, 1H). GC-MS: One peak, retention time, 11.34 min; M + :324 m/z. Sodium methoxide (8.1 mg, 0.15 mmol) and the l-(ejrø-5-norbornen-2-oxy)-10- (thioacetyl)-decane (488 mg, 1.5 mmol) were weighed into separate 50 mL Schenk flasks in an inert atmosphere glovebox. The two flasks were taken out of the glovebox, and degassed methanol (10 mL) was transferred to each flask by cannula. The solution of 1- (norborn-2-en-5-exo-ol)-10-(thioacetyl)-decane was then transferred by cannula to the sodium methoxide solution, and the mixture was refluxed for six hours under a positive stream of nitrogen. Upon cooling to room temperature, the mixture was poured into 1.0 M HCl (50 mL) and extracted with ether (3 x 50 mL). The combined organic extracts were washed with brine (3 x 50 mL), dried over sodium sulfate, and the solvent was removed on a rotary evaporator to give 361 mg of l-mercapto-10-(eco-5-norbornen-2- oxy)-decane (1.23 mmol, 85%) of sufficient purity for further manipulations. 1 HNMR (C 6 D 6 ): 1.25 (m, 18H), 1.61 (q, 4H), 1.88 (d, 1H), 2.28 (q, 2H), 2.63 (s, 1H), 2.90 (s, 1H), 3.35 (m, 3H), 5.94 (m, 1H). GC-MS: One peak, retention time, 10.43 min; M + :282 m/z. D. Synthesis of ejco-5-norbornen-2-yl ferrocenecarboxylate (3) Ferrocenecarboxylic acid (0.511 g, 2.22 mmol) was weighed into a 100 mL Schlenk flask. The flask was placed under nitrogen using standard Schlenk techniques. Dry dichloromethane (50 mL) was added by cannula, and oxalyl chloride (0.291 mL, 3.34 mmol) was syringed into the reaction vessel . The mixture was stirred at room temperature for 2 hours. The solvent and excess oxalyl chloride were removed by rotary evaporation, and dry benzene (50 mL) was added by cannula. Next, β o-5-norbornen-2-ol (0.244 g, 2.22 mmol) was weighed into a 250 mL round-bottom flask and placed under nitrogen using standard Schlenk techniques. Dry benzene (50 mL) was added by cannula, and triethylamine (0.62 mL, 4.44 mmol) was syringed into the reaction vessel. The acid chloride solution in the Schlenk flask was then transferred into the round-bottom flask containing the alcohol solution by cannula, and the mixture was refluxed under nitrogen for 12 hours. The solution was diluted with brine (100 mL) and extracted with benzene (3 x 100 mL). The benzene layers were combined, dried over magnesium sulfate, and the solvent was removed by rotary evaporation. Column chromatography on silica gel with pentane/ether (8:1) as the eluent gave 0.215 g (0.668 mmol, 30%) of desired product as a yellow solid. X HNMR (C 6 D 6 ): 1.58 (m, 4H), 2.59 (s, 1H), 2.98 (s, 1H), 4.02 (m, 7H), 4.85 (d, 2H), 4.97 (d, IH), 5.79 (m, IH), 5.98 (m, IH). 13 CNMR(CDC1 3 ): 34.78, 40.69, 46.37, 47.58, 69.69, 70.08, 71.19, 74.87, 132.85, 132.87, 141.15, 175.60. HRMS (El) (M + ): calcd. for C lg H lg O 2 Fe: 322.066 m/z; found: 322.066 m/z. Anal: calcd. for C 18 H lg O 2 Fe: C: 67.1; H: 5.63; Found: C: 66.9; H: 5.76. E. Synthesis of gχo-5-norbornen-2-yl ferroceneacetate (4) Ferroceneacetic acid (0.401 g, 1.64 mmol) was weighed into a 100 mL Schlenk flask. The flask was placed under nitrogen using standard Schlenk techniques. Dry dichloromethane (50 mL) was added by cannula, and oxalyl chloride (0.232 mL, 2.66 mmol) was syringed into the reaction vessel. The mixture was stirred at room temperature for 2 hours. The solvent and excess oxalyl chloride were removed by rotary evaporation, and dry benzene (50 mL) was added by cannula. Next, exo-5-norbornen-2-ol (0.181 g, 1.64 mmol) was weighed into a 250 mL round-bottom flask and placed under nitrogen using standard Schlenk techniques. Dry benzene (50 mL) was added by cannula, and triethylamine (0.46 mL, 3.29 mmol) was syringed into the reaction vessel. The acid chloride solution in the Schlenk flask was then transferred into the round-bottom flask containing the alcohol solution by cannula, and the mixture was refluxed under nitrogen for 12 hours. The solution was diluted with brine (100 mL) and extracted with benzene (3 x 100 mL). The benzene layers were combined, dried over magnesium sulfate, and the solvent was removed by rotary evaporation. The benzene layers were passed through a short plug of silica gel (30 mm long, in a Pasteur pipette), and removal ofthe solvent on a rotary evaporator gave 0.281 g (0.84 mmol, 51%) ofthe desired product as a brown liquid. 1 HNMR (C 6 D 6 ): 1.58 (m, 4H), 2.59 (s, IH), 2.90 (s, IH), 3.19 (d, 2H), 3.95 (d, 2H), 4.02 (s, 5H), 4.19 (d, 2H), 4.80 (m, IH), 5.75 (m, IH), 5.98 (m, IH). 13 CNMR (CDC1 3 ): 34.45, 36.01, 40.35, 46.15, 47.36, 67.95, 68.46, 75.63, 80.95, 132.43, 141.50, 141.52, 171.55. HRMS (El) (M + ): calcd. for C 19 H 20 O 2 Fe: 336.081 m/z; Found: 336.082 m/z. F. Immobilization of 2 on GNPs and characterization ofthe 2-modified GNPs The second key step in the preparation of metathesis-ready GNPs involves immobilization of 2 on 3 nm GNPs. The method of Schiffrin (Brust et al, J. Chem. Soc, Chem. Commun., 801 (1994)) was modified for preparing 3 nm GNPs capped with linear alkanethiols by reducing HAuCl 4 (2.24 mmoles) in the presence of a 3:1 mixture of 1- dodecanethiol (1.68 mmoles), and 2 (0.56 mmoles) to yield GNPs modified with the two adsorbates. The dodecanethiol diluent molecule was employed to minimize surface crosslinking of norbornenyl groups and propagating polymer. The GNPs can be precipitated from CH 2 C1 2 by the addition of ethanol and redispersed in various organic solvents such as hexanes, ether, and CH 2 C1 2 . The 1 HNMR spectrum ofthe modified particles in CDC1 3 confirms that the norbornene adsorbates are indeed attached to their surfaces, Figures 2A-B. The two resonances at approximately δ 5.9 and 6.2 are highly diagnostic ofthe two norbornenyl olefinic protons and compare well with those observed in the X HNMR spectrum of 2 (δ 5.9 and 6.2) in CDC1 3 . The UN- visible spectrum of these particles in hexanes exhibits a weak plasmon band at 518 nm, which is characteristic of gold nanoparticles of this size. Duff et al, J. Chem. Soc. Chem. Commun., 96 (1993). G. Synthesis and characterization of GΝP - poly 3 Inside an inert atmosphere glovebox, 3 nm GΝPs modified with 2 (10 mg) were weighed into a screw-top ΝMR tube, and 100 μL of CDC1 3 was added. Catalyst 1 (1.5 mg, 1.8 μmol) was dissolved in 200 μL of CDC1 3 and syringed into the ΝMR tube containing the 2-modified GΝPs. The ΝMR tube was capped and placed on a shaker for 10 minutes. Next, a solution of 3 (12 mg, 37 μmol in 200 μL of CDC1 3 ) was added, and the NMR tube was recapped and shaken for a further 30 minutes, after which time an 1 HNMR spectrum was taken. The catalyst was quenched with ethyl vinyl ether (about 100 μL). Isolation ofthe particle-polymer hybrids (21 mg) was achieved by pouring the CDC1 3 solution into a vigorously stirring solution of hexanes (100 mL). The mother liquor was decanted, and the resulting dark brown precipitate was washed with hexanes (3 x 50 mL) and dried under vacuum. The precipitate was redispersable in numerous organic solvents, such as CH 2 C1 2 and THF. Ring-opening metathesis ofthe norbornene rings on the GNPs with catalyst 1 (1 equivalent; the number of norbornenyl rings on the particles was estimated from elemental analysis and NMR titrations) was achieved in less than 10 minutes in CDC1 3 . Evidence for this activation process is the loss ofthe olefinic resonances at δ 5.9 and 6.2, Figure 2C. Subsequent addition of 20 equivalents of the redox-active complex 3 to this solution led to polymerization of 3, as evidenced by the appearance of broad resonances at δ 5.7-5.2 in the 1 HNMR spectrum of the particle-polymer hybrids (GNP - poly 3), Figure 2D. These resonances are characteristic of polymers synthesized from norbornenyl-containing starting materials. Schwab et al, Angew. Chem., Int. Ed. Engl, 34:2039 (1995); Lynn et al, J. Am. Chem. Soc, 120: 1627 (1998). After 30 minutes there is no evidence of monomer 3, indicating that polymerization is complete. The polymers could be terminated irreversibly by the addition of a slight excess of ethyl vinyl ether, a known ROMP termination agent for catalysts such as 1. Wu et al, J. Am. Chem. Soc, 117:5503 (1995). Significantly, the GNP - poly 3 hybrids could be precipitated from CDC1 3 with hexanes, a solvent in which the 2-modified GNPs were completely redispersable. Once washed thoroughly with hexanes, the GNP - poly 3 hybrids could be redispersed in a variety of more polar organic solvents, such as CH 2 C1 2 and THF. These solubility properties mirror those of the untethered ferrocenyl homopolymer, which was independently synthesized from 1 and 3 under nearly identical conditions (poly 3; see below). Cyclic voltammetry ofthe GNP - poly 3 hybrids cast onto the surface of an Au/Si electrode in 0.1 M TBAPF 6 /CH 3 CN (TBAPF 6 = tetrabutyl ammonium hexafluorophosphate) exhibited a reversible wave associated with ferrocenyl oxidation/ reduction at 180 mV versus FcH/FcH + (ferrocene/ferricinium), Figure 2F. Finally, TEM analysis of the GNP - poly 3 hybrids indicated that the hybrid particles maintained their 3± 1 nm diameter gold cores, but the polymer shell layers could not be imaged by TEM due to the low density of their atomic constituents, Figures 3 A-B. H. Synthesis and characterization of GNP - poly 3 - poly 4 As a further demonstration of the generality and scope of the strategy for preparing hybrid nanoparticles, block copolymers of two different norbornenyl ferrocenyl derivatives, 3 and 4, were grown successively from the surfaces of 2-modified particles treated with catalyst 1. Inside an inert atmosphere glovebox, 3 nm GNPs modified with 2 (10 mg) were weighed into a screw-top NMR tube, and 100 μL of CDC1 3 was added. Catalyst 1 (1 equivalent, 1.5 mg, 1.8 μmol) was dissolved in 200 μL of CDCL, and syringed into the NMR tube containing the 2-modified GNPs. The NMR tube was capped and placed on a shaker for 10 minutes. Next, a solution of 3 (20 equivalents, 12 mg, 37 μmol, in 200 μL of CDC1 3 ) was added, and the NMR tube was recapped and shaken for a further 20 minutes, after which time an 1 HNMR spectrum was taken. Then, a solution of 4 (20 equivalents, 37 μmol, in 200 μL of CDC1 3 ) was added, and the NMR tube was recapped and shaken for another 20 minutes, after which time another 1 HNMR spectrum was taken. The catalyst was quenched with ethyl vinyl ether (~ 100 μL). Isolation ofthe particle-polymer hybrids (32 mg) was achieved by pouring the CDC1 3 solution into a vigorously stirring solution of hexanes (100 mL). The mother liquor was decanted, and the resulting dark brown precipitate was washed with hexanes (3 x 50 mL) and dried under vacuum. The precipitate was redispersable in numerous organic solvents, such as CH 2 C1 2 and THF. Compound 4 was chosen as the second polymer building block because it can be easily differentiated from 3 by cyclic voltammetry. The methylene group located between the carbonyl and ferrocenyl moiety in 4 makes it approximately 220 mV easier to oxidize than 3. Moreover, this methylene group provides a spectroscopic tag that allows allows one to follow the polymerization reaction by 1 HNMR, Figure 2E (note the asterisked resonance). The growth ofthe broad resonance at δ 3.3, coupled with the complete loss of resonances associated with the starting monomer 4, indicates complete conversion of 4 to a block of poly 4 (GNP - poly 3 - poly 4). The GNP - poly 3 - poly 4 system exhibited reversible electrochemistry with the expected two distinguishable waves associated with oxidation/reduction of the two different types of ferrocenyl moieties within the particle immobilized block copolymer shell (E 1/2s = -40 mV for the block of poly 4 and 180 mN for the block of poly 3 vs FcH/FcH + ), Figure 2G. A comparison ofthe integrated current associated with these two waves allows one to evaluate the relative amounts of 3 and 4 in the GΝP - poly 3 - poly 4 structure. Based on this analysis, a 1.4:1 ratio was calculated for 3 and 4 in the block copolymer. The reason that this is not a 1:1 ratio may be due to small differences in polymer solvation and, therefore, different degrees of electrochemical accessibility for the two layers or, alternatively, to stoichiometry errors due to the small amounts of reagents used. The ideal response associated with these waves (the peak current is linearly dependent upon the scan rate) and the lack of evidence for mediated electron transfer between the interior block of 3 and the electrode surface indicates that in these structures both polymer blocks are accessible to the electrode surface and solvated to the extent that ions can move in and out of the block copolymer structure. Significantly, both the homopolymers and the block copolymers formed from the polymerization of 3 and 4 exhibit broad waves characteristic of sluggish electron transfer and poor polymer solvation, Figure 2H (poly 3 is given as an example). Finally, TEM analysis of the GNP - poly 3 - poly 4 hybrids indicated that the hybrid particles maintained their 3±1 nm diameter gold cores, but the polymer shell layers could not be imaged by TEM due to the low density of their atomic constituents. I. Synthesis of poly 3 A solution of 3 (12 mg, 37 μmol in 200 μL of CDC1 3 ) was syringed into a screw- top NMR tube, followed by the addition of a solution of 1 (1.5 mg, 1.8 μmol in 300 μL of CDC1 3 ). The NMR tube was capped and placed on a shaker for 30 minutes. The catalyst was quenched with ethyl vinyl ether (-100 μL). Isolation ofthe polymer (11 mg) was achieved by pouring the CDC1 3 solution into a vigorously stirring solution of hexanes (50 mL). The mother liquor was decanted, and the resulting light brown precipitate was washed with hexanes (3 x 25 mL) and dried under vacuum. The precipitate was redispersable in numerous organic solvents, such as CH 2 C1 2 and THF. J. Control experiment As a control experiment, a solution consisting of the untethered ferrocenyl- containing poly 3 and 2-modified GNPs in a ratio comparable to that used for the GNP - poly 3 experiment (see section G above) was prepared. When a precipitation experiment was carried out for this control system, the 2-modified GNPs remained soluble in hexanes (as evidenced by 'HNMR), while the homopolymer (poly 3) precipitated as expected. The difference in solubility between the 2-modified GNPs and the GNP - poly 3 hybrids is strong evidence that the polymers formed by surface polymerization are indeed tethered to the surfaces ofthe GNPs. Taken together, the data unambiguously confirm that the polymers grown off the surfaces ofthe GNPs remain attached to the particle surfaces. These proof-of-concept results indicate that the particle synthesis strategy reported herein can be used to prepare a new class of nanoparticles that can be functionalized with polymeric layers of virtually any norbornenyl-containing monomer. Indeed, the strategy could be easily extended to other inorganic nanoparticle templates as well as optically active or electroactive norbornenyl groups. Traditional inorganic nanoparticles already have become the basis for many useful probe-type applications. Storhoff et al., J Clust. Sci., 8: 179 (1997); Brousseau et al, J. Am. Chem. Soc, 120:7645 (1998); Freeman et al, Science, 267:1629 (1995); Zhu et al, J. Am. Chem. Soc, 119:235 (1997); Mirkin et al., Nature, 382:607 (1996); Elghanian et al, Science, 277:1078 (1997); Storhoff et al, J Am. Chem. Soc, 120:1959 (1998). The hybrid structures presented herein, with their high degree of synthetic tunability, are likely to become equally or even more important as diagnostic probes in chemical and biochemical detection strategies. Moreover, they are a new and versatile type of building block that chemists and material scientists can easily incorporate into many existing particle assembly strategies. Example 2 This example describes the synthesis of compound 5 (see Figure 4). To a 100 mL Schlenk flask 2-norbornene-5-eico-ol (1.10 g, 10 mmol), 3-thiopheneacetic acid (1.42 g, 10 mmol), and ?-toluenesulfonic acid monohydrate (80 mg, 0.42 mmol) were added. The three solids were dissolved in toluene (60 mL) and a Dean/Stark trap was fitted to the top of the flask. A water condenser was placed on top of the Dean/Stark trap, and the mixture was heated to reflux. Over a period of six hours, the reaction volume was reduced to 20 mL by occasionally collecting solvent from the bottom ofthe Dean/Stark trap. The mixture was cooled to room temperature, poured into water (50 mL), and extracted with ether (3 x 50 mL). The organic portions were combined, washed with brine (50 mL), dried over sodium sulfate, and filtered into a 500 mL round bottom flask. The solvent was removed under vacuum using a rotary evaporator. The pale yellow oil was chromatographed on silica using a 1:1 mixture of CH 2 C1 2 and hexanes as an eluent to yield the desired product (1.68 g, 7.2 mmol, 72 %) as a clear oil. Η NMR (CDC1 3 ): 1.40 (m, IH), 1.60 (m, 2H), 1.71 (m, IH), 2.87 (b, 2H), 3.65 (s, 2H), 4.70 (d, IH), 5.97 (m, IH), 6.24 (m, IH), 7.05 (d, IH), 7.15 (b, IH), 7.30 (m, IH). 13 C NMR (CDC1 3 ): 34.7, 36.3, 40.7, 46.3, 47.3, 75.8, 122.7, 125.7, 128.5, 132.6, 133.9, 141.2, 171.3. GCMS: Retention time 10.86 min, m/e + 234. Anal: cald. for C 13 H 14 O 2 S: C: 66.64; H: 6.02; S: 13.68; Found: C: 66.91; H: 6.15; S: 13.86. Example 3 This example describes the synthesis of compound 6 (see Figure 4). In an inert atmosphere glovebox, exo-5-norbornen-2-ol (710 mg, 6.45 mmol) was weighed into a 50 mL Schlenk flask. THF (15 mL) was added, and the solution was stirred vigorously while oil-free sodium metal (160 mg, 6.96 mmol) was added. The mixture was then taken out ofthe glovebox, refluxed for 12 hours under a nitrogen bubble, and allowed to cool to room temperature. In a separate 100 mL Schlenk flask, 2,5-dibromo-3-bromo- methyl-thiophene (2.01 g, 6.00 mmol) was dissolved in THF (15 mL), and the flask was capped with a pressure-equalizing dropping funnel. The cooled solution of deprotonated exo-5-norbornen-2-ol was then transferred to the pressure-equalizing dropping funnel by cannula (excess Na was quenched with isopropanol) and slowly added to the thiophene solution with vigorous stirring over a period of 10 minutes. The dropping funnel was then replaced with a condenser, and the mixture was refluxed for an additional 12 hours under a positive stream of nitrogen. Upon cooling to room temperature, the reaction mixture was poured into ether (50 mL) and washed successively with water (50 mL), 0.1 M NaOH (50 mL), 1 M HCl (50 ml), and brine (50 mL). The organic layer was collected, dried over sodium sulfate and filtered through a Buchner funnel The solvent was removed on a rotary evaporator. Column chromatography ofthe slightly yellow oil on silica gel with 20% CH 2 C1 2 in hexanes as the eluent gave 1.88 g (5.16 mmol, 86%) ofthe desired product as a clear oil. Η NMR (CDC1 3 ): 1.41 (m, IH), 1.58 (m, 2H), 1.71 (m, IH), 2.82 (b, IH), 2.93 (b, IH), 3.56 (m, IH), 4.40 (m, 2H), 5.93 (m, IH), 6.20 (m, IH), 6.99 (m, IH). 13 C NMR (CDC1 3 ): 34.53, 40.47, 46.06, 65.12, 80.31, 109.59, 111.21, 131.03, 133.10, 139.80, 140.87. GCMS: Retention time 12.26 min, m/( 364. Example 4 This example describes the preparation of compound 7 (see Figure 4). In a 100 mL Schlenk flask was added 2-norbornene-5-exo-acetic acid (450 mg, 3.0 mmol). The flask was placed under nitrogen using standard Schlenk techniques. Dry CH 2 C1 2 (20 mL) was added by cannula, followed by oxalyl chloride (5 mL of a 2 M solution in CH 2 C1 2 , 10 mmol). The mixture was allowed to stir for 2 hours at room temperature. The solvent and excess oxalyl chloride were removed under vacuum and the resulting acid chloride was redissolved in dry diethyl ether (20 mL). To a separate 100 mL Schlenk flask was added 3 , -(2-hydroxyethyl)-2,2':5 , ,2"-terthiophene (850 mg, 2.91 mmol). The flask was placed under nitrogen, and diethyl ether (20 mL) was added followed by triethyl amine (0.84 mL, 6 mmol). The flask was fitted with a pressure equalizing dropping funnel The norbornenyl-acid chloride solution was transferred to the dropping funnel by cannula and subsequently added to the stirring solution ofthe terthiophene solution dropwise over a period of ten minutes. The mixture was stirred for an additional 10 minures at room temperature and then poured into water (50 mL) and extracted with ether (3 x 50 mL). The organic portions were collected, washed with brine (50 mL), dried over sodium sulfate, and filtered into a 500 mL round bottom flask. The solvent was removed under vacuum using a rotary evaporator. The resulting oil was chromatographed on silica using 1:1 CH 2 C1 2 and pentane as an eluent to yield the desired product (1.15 g, 2.79 mmol, 96%) as a light green oil. ΗNMR^D^): 1.32 (m, 2H), 1.45 (m, IH), 1.86 (m, IH), 2.87 (b, IH), 2.98 (b, IH), 3.10 (t, 2H), 4.32 (t, 2H), 6.11 (m, 2H), 7.05 (m, IH), 7.10 (m, 2H), 7.19 (m, 2H), 7.26 (d, IH), 7.37 (d, IH). HRMS: calcd. for C 22 H 20 O 2 S 3 : 412.06; Found: 412.06. Example 5 This example describes the preparation of compound 8 (see Figure 4). PdCl 2 (l, -bis(diphenylphosphino)ferrocene) (39 mg, 0.05 mmol) was weighed into a 100 ml Schlenk flask containing a magnetic stir bar and fitted with a reflux condenser and an addition funnel. The flask was evacuated to remove air, and a solution of 6 (1.00 g, 2.75 mmol) in dry diethyl ether (20 mL) was added by cannula. The flask was cooled to -20 °C in an acetone/ice bath, and a solution of (2-thienyl)magnesiumbromide (8.22 g, 1.54 mmol) in dry diethyl ether (20 mL) was added by addition funnel over a 30 min period. The reaction was allowed to warm to room temperature and was then refluxed overnight under a positive stream of nitrogen. The excess Grignard was consumed by the slow addition of a saturated solution of aqueous ammonium chloride to the organic layer, followed by three consecutive water washes (50 mL). The organic layer was collected, dried over sodium sulfate, and filtered into a 500 mL round bottom flask. The solvent was removed under vacuum using a rotary evaporator. The resulting dark brown oil was chromatographed on silica using 1 : 1 CH 2 C1 2 and hexanes as an eluent to yield the desired product (870 mg, 86 %) as a green oil. Η NMR (CDC1 3 ): 1.47 (m, IH), 1.59 (m, 2H), 1.78 (m, IH), 2.84 (b, IH), 2.98 (b, IH), 3.65 (m, IH), 4.56 (m, 2H), 5.94 (m, IH), 6.20 (m, IH), 7.03 (m, IH), 7.09 (m, IH), 7.18 (m, IH), 7.21 (m, IH), 7.22 (m, IH), 7.24 (m, IH), 7.35 (m, IH). 13 C NMR (CDC1 3 ): GCMS: Retention time 18.73 min, m/e + 370. Monomers such as 5, 7, and 8 are doubly polymerizable monomers that can undergo ROMP chemistry followed by a second cross-linking reaction to give a conducting graft copolymer composite. With these new monomers, new nanoparticles/conducting polymer composites can be made (see Figures 7A-B). Example 6 This example describes the synthesis of exo-5-norbornen-2-yl pyrenecarboxylate (compound 9 in Figure 4). Pyrenecarboxylic acid (0.547 g, 2.22 mmol) was weighed into a 100 mL Schlenk flask. The flask was placed under nitrogen using standard Schlenk techniques. Dry dichloromethane (50 mL) was added by cannula, and oxalyl chloride (0.291 mL, 3.34 mmol) was syringed into the reaction vessel. The mixture was stirred at room temperature for 2 hours. The solvent and excess oxalyl chloride were removed by rotary evaporation, and dry benzene (50 mL) were added by cannula. Next, exo-5-norbornen-2-ol (0.244 g, 2.22 mmol) was weighed into a 250 mL round-bottom flask and placed under nitrogen using standard Schlenk techniques. Dry benzene (50 mL) was added by cannula, and triethylamine (0.62 mL, 4.44 mmol) was syringed into the reaction vessel. The acid chloride solution in the Schlenk flask was then transferred into the round-bottom flask containing the alcohol solution by cannula. The mixture was then refluxed under nitrogen for 12 hours. The solution was diluted with brine (100 mL) and extracted with benzene (3 x 100 mL). The benzene layers were combined, dried over magnesium sulfate, and the solvent was removed by rotary evaporation. Column chromatography on silica gel with pentane/ether (8:1) as the eluent gave 0.215 g (0.668 mmol, 30%) ofthe desired product as a yellow solid. ΗNMR Dg): 1.62 (m, 2H), 1.79 (m, 2H), 2.62 (b, IH), 3.05 (b, IH), 5.20 (m, IH), 5.94 (m, IH), 6.05 (m, IH), 7.70 (m, 2H), 7.81 (m, 2H), 7.87 (m, 2H), 7.99 (m, IH), 8.72 (m, IH), 9.79 (m, IH). HRMS (El) (M + ): calcd. for C 24 H 18 O 2 : 338.13 m/z Found: 338.13 m/z. Compound 9 is fluorescent, and the fluorescence emission spectra ofthe monomer and of poly 9 are shown in Figure 6. As expected, the fluorescence of poly 9 occurs at a lower wavelength, and is broader and less intense, than that of monomer 9 itself. These behaviors suggest the formation of intramolecular excimers in poly 9 due to the close proximity ofthe chromophores. Example 7 This example describes the synthesis of α-bromo-α'-(exo-5-norbornene-2-ol)-p- xylene (10) (see Figure 8A). In an inert atmosphere glovebox, e o-5-norbornene-2-ol (820 mg, 7.44 mmol) was weighed into a 50 mL Schlenk flask. Dry THF (15 mL) was added and the solution was stirred vigorously while oil-free sodium metal (250 mg, 10.9 mmol) was added. The mixture was then taken out ofthe glovebox, refluxed for 12 hours under a positive stream of nitrogen, and allowed to cool to room temperature. In a separate 100 mL Schlenk flask, α,α'-dibromo-/?-xylene (2.11 g, 8.00 mmol) was dissolved in dry THF (15 mL) and the flask was capped with a pressure-equalizing dropping funnel. The cooled solution of deprotonated exo-5-norbornen-2-ol was then transferred to the pressure-equalizing dropping funnel via cannula filtration and slowly added to the thiophene solution with vigorous stirring over a period of 10 minutes. The dropping funnel was then replaced with a condenser and the mixture was refluxed for an additional 12 hours under a positive stream of nitrogen. Upon cooling to room temperature, the reaction mixture was poured into benzene (50 mL) and washed successively with water (50 mL), 1.0 M NaOH (50 mL), 1.0 M HCl (50 mL), and brine (50 mL). The organic layer was collected, dried over sodium sulfate and filtered into a 500 mL round bottom flask. The solvent was removed on a rotary evaporator. Column chromatography on silica gel with 30% CH 2 C1 2 in hexanes as the eluent gave the desired product 10 (1.13 g, 3.87 mmol, 52 %) as a clear oil. ΗNMR (C 6 D 6 ): 1.42 (m, 2H), 1.60 (m, IH), 1.85 (m, IH), 2.61 (m, IH), 2.84 (m, IH), 3.44 (m, IH), 3.99 (m, 2H), 4.24 (m, 2H), 5.76 (m, IH), 6.26 (m, IH), 7.02 (m, 2H), 7.13 (m, 2H). 13 CNMR(C 6 D 6 ): 33.6, 35.2, 41.2, 46.7, 71.1, 80.7, 129.6, 133.7, 137.5, 140.3, 141.2. Example 8 This example describes the synthesis of N-α-(N, N-dimethylammonium- methylferrocenebromide)-a'-(exo-5-norbornene-2-ol)-p-xylene (11) (see Figure 8A). In a 100 mL round bottom flask was added 10 (293 mg, 1.00 mmol), anhydrous diethyl ether (25 mL) and a magnetic stirring bar. To this stirring solution of 10 was added a solution ofN, N-dimethylaminomethylferrocene (243 mg, 1.00 mmol) in anhydrous diethyl ether (25 mL). The mixture was stirred for 6 hours, during which time a yellow precipitate formed. After this time, a cannula filtration apparatus was used to removed the ether from the flask and the resulting yellow powder was washed with ether (4 x 50 mL). The solid was dried overnight under vacuum to yield the desired product 11 (391 mg, 0.73 mmol, 73 %). ΗNMR(D 2 O): 13 CNMR(CDC1 3 ): 34.7, 40.6, 46.2, 46.7, 48.3, 65.8, 66.9, 69.8, 70.7, 70.8, 72.5, 80.9, 126.7, 128.3, 133.2, 133.5, 141.0, 142.0. Example 9 This example describes a general polymerization procedure for 10 or 11. Polymerization of 11 is described. In an inert atmosphere glovebox, 11 (110 mg, 0.21 mmol) was weighed into a 25 mL round bottom flask equipped with a magnetic stirring bar and dry MeOH (4 mL). To the stirring solution of 11 was added a solution of catalyst 1 (7.0 mg, 0.0085 mmol, 4 mole %) in dry CH 2 C1 2 (0.5 mL). The mixture was stirred for 30 minutes, after which time it was removed from the dry box and the polymerization was terminated with ethyl vinyl ether (1 mL). The polymer (ROMP-polyll, 101 mg, 92%) was isolated by pouring the mixture into anhydrous diethyl ether ( 100 mL) and repeatedly filtering and washing with fresh diethyl ether (4 x 50 mL). Example 10 This example describes the synthesis of 12-14 (see Figure 8A). The synthesis of 12 is representative. A mixture of 10 (440 mg, 1.5 mmol) and 9-NN-dimethyl- aminomethylanthracene (235 mg, 1.0 mmol) inDMF (25 mL) was refluxed for 16 hours. After this time, the mixture was poured into diethyl ether (250 mL). The yellow solid which precipitated from solution was filtered and washed successively with diethyl ether (4 x 50 mL) to yield the desired product 12 (432 mg, 0.82 mmol, 82 %). Example 11 This example describes the synthesis of 15 (see Figure 8B). A mixture of exo-5- norbornene-2-ol (500 mg, 4.54 mmol), 2-cyanoethyl diisopropylchlorophosphoramidite (1.00 g, 4.22 mmol), and N, N-diisopropylethylamine (0.87 mL, 5.0 mmol) was stirred in dry THF under an atmosphere of nitrogen for a period of 3 hours. After this time, the mixture was poured into a cold solution of 1.0 M ΝaHCO 3 (100 mL) and extracted with CH 2 C1 2 (3 x 50 mL). The solvent was removed under vacuum to yield the desired product 15 (1.24 g, 95%). Example 12 This example describes the synthesis of 16 (see Figure 8B). Amixture of 10 (1.40 g, 4.77 mmol), fluorescein (800 mg, 2.40 mmol), and potassium carbonate (665 mg, 4.80 mmol) in acetone (25 mL) was refluxed for 36 hours. After this time, the mixture was poured into ice water (100 mL), filtered, and washed with water (400 mL). Recrystalization from DMF with acidic water yielded the desired product 16 (727 mg, 0.96 mmol, 40 %).

Claims: WE CLAIM: 1. A method of preparing nanoparticles having at least one polymer shell attached thereto comprising: providing a type of nanoparticles; and attaching a type of initiation monomers to the surfaces ofthe nanoparticles. 2. The method of Claim 1 wherein the initiation monomer comprises a cyclic- olefin-containing group. 3. The method of Claim 2 wherein the initiation monomer comprises a norbornenyl group. 4. The method of Claim 1 wherein the nanoparticles are gold nanoparticles. 5. The method of Claim 4 wherein the initiation monomer is a norbornenyl- containing alkanethiol 6. The method of Claim 5 wherein the initiation monomer is 1 -mercapto- 10- (exo-5-norbornen-2-oxy)-decane. 7. The method of Claim 1 wherein the initiation monomers are mixed with a type of attachment compounds, and both the imtiation monomers and the attachment compounds are attached to the surfaces ofthe nanoparticles. 8. The method of Claim 1 further comprising: contacting the nanoparticles having the initiation monomers attached to them with a transition metal ring-opening metathesis catalyst to activate the initiation monomers; and contacting the nanoparticles with one or more types of propagation monomers of the formula P-L-N under conditions effective so that the propagation monomers are polymerized to form one or more polymer shells attached to the nanoparticles, wherein: N is a cyclic olefin-containing group; P is a moiety which gives each polymer shell a selected property or properties; and L is a bond or linker whereby N is attached to P. 9. The method of Claim 8 wherein L is a polymer, — COO — , — CH 2 (CH 2 ) m COO— , — OCO— , — R^CH^— NR 1 — — O(CH 2 ) m — — (CH 2 ) m — o >1 -c II- -(CH 2 ) m — * - or JU. or comprises a binding moiety B that binds specifically to an analyte; wherein: R 1 has the formula X(CH 2 ) m ; X is -CH 3 ,-CHCH 3 , -COOH, -CO 2 (CH 2 ) m CH 3 , -OH, -CH 2 OH, ethylene glycol, hexa(ethylene glycol), -O(CH 2 ) m CH 3 , -NH 2 , -NH(CH 2 ) m NH 2 , halogen, glucose, maltose, fullerene C60, a cyclic olefin, or a nucleic acid; and m is 0-30. 10. The method of Claim 8 wherein N is a norbornenyl-containing group. 11. The method of Claim 8 or 10 wherein the catalyst has the formula: wherein: M is osmium or ruthenium; R 1 is hydrogen; X 1 and X 2 , which may be different or the same, are any anionic ligand; L 1 and L 2 , which may be different or the same, are any neutral electron donor; and R 2 is hydrogen, substituted or unsubstituted alkyl, or substituted or unsubstituted aryl. 12. The method of Claim 11 wherein M is ruthenium, R 1 is hydrogen, R 2 is phenyl, X 1 and X 2 are both -Cl, and L 1 and L 2 are both tricyclohexylphosphine. 13. The method of Claim 8 or 10 wherein the catalyst has the formula: wherein: Re is rhenium (NH); R 1 is selected from the group consisting of an alkyl having 1-20 carbon atoms, an aryl having 6-20 carbon atoms, an araalkyl having 7-30 carbon atoms, halogen substituted derivatives of each, and silicon-containing analogs of each; R 2 is R 1 or is a substituent resulting from the reaction of the Re=CHR 2 moiety ofthe catalyst with an olefin that is being metathesized; R 3 and R 4 are ligands which individually or together are sufficiently electron withdrawing to render the rhenium atom electrophilic enough for metathesis reaction; and n is 1 or more. 14. The method of Claim 8 or 10 wherein the catalyst has the formula: M(ΝR 1 )(OR 2 ) 2 (CHR 3 ), wherein: M is molybdenum or tungsten; R 1 and R 2 each individually may be an alkyl containing 1-20 carbon atoms, an aryl containing 6-20 carbon atoms, an araalkyl containing 7-20 carbon atoms, a halogen substituted derivative ofthe alkyl, aryl, or araalkyl, or a silicon-containing analog of one ofthe alkyl, aryl, or araalkyl; and R 3 is an alkyl containing 1-20 carbon atoms, an aryl containing 6-20 carbon atoms, an araalkyl containing 7-20 carbon atoms, or a substituent resulting from the reaction ofthe M=CHR 3 moiety of said catalyst with an olefin being metathesized. 15. The method of Claim 8 or 10 wherein the nanoparticles are contacted with a single type of propagation monomers under conditions effective so that the monomers are polymerized to form a single polymer shell attached to the nanoparticles. 16. The method of Claim 15 wherein the polymer shell has redox activity. 17. The method of Claim 16 wherein the propagation monomer is exo-5- norbornen-2-yl ferrocenecarboxylate or exo-5-norbornen-2-yl ferroceneacetate. 18. The method of Claim 8 or 10 wherein: the nanoparticles are contacted with a plurality of types of propagation monomers under conditions effective so that the monomers are polymerized to form one or more polymer shells attached to the nanoparticles, each polymer shell having one or more selected properties. 19. The method of Claim 18 wherein: the nanoparticles are contacted with a first type of propagation monomers under conditions effective so that the monomers are polymerized to form a first polymer shell attached to the nanoparticles, the first polymer shell having a first selected property; and then the nanoparticles are contacted with a second type of propagation monomers under conditions effective so that the monomers are polymerized to form a second polymer shell attached to the first polymer shell, the second polymer shell having a second selected property which is different from the first selected property ofthe first polymer shell. 20. The method of Claim 19 wherein one of the polymer shells has redox activity. 21. The method of Claim 20 wherein the propagation monomer polymerized to form the shell is exø-5-norbornen-2-yl ferrocenecarboxylate or exo-5-norbornen-2-yl ferroceneacetate. 22. The method of Claim 19 wherein the both polymer shells have redox activity. 23. The method of Claim 22 wherein the two polymer shells have different redox activities. 24. The method of Claim 23 wherein the propagation monomer polymerized to form the first polymer shell is exo-5-norbornen-2-yl ferrocenecarboxylate and the propagation monomer polymerized to form the second polymer shell is exø-5-norbornen- 2-yl ferroceneacetate. 25. The method of Claim 8 or 10 wherein the polymerization is stopped by adding a compound that terminates polymerization. 26. Nanoparticles having initiation monomers attached to them. 27. The nanoparticles of Claim 26 wherein the initiation monomers comprise cyclic olefin-containing groups. 28. The nanoparticles of Claim 27 wherein the initiation monomers comprise norbornenyl groups. 29. The nanoparticles of Claim 28 wherein the initiation monomers are norbornenyl-containing alkanethiols. 30. The nanoparticles of Claim 29 wherein the initiation monomers are 1- mercapto- 10-(exø-5-norbornen-2-oxy)-decane. 31. Nanoparticles comprising one or more polymer shells attached to them, the polymer shells being formed by polymerizing one or more types of propagation monomers ofthe formula P-L-N, wherein: P is a moiety which provides a desired property or properties to each of the polymer shells; N is a cyclic olefin-containing group; and L is a bond or a linker whereby N is attached to P. 32. The nanoparticles of Claim 31 wherein L is a polymer, — COO — , -CH 2 (CH 2 ) m COO— , -OCO-, -R^CH^-NR 1 - -O(CH 2 ) m - -(CH 2 ) m - R' M U N ' - (CH2)m , — O — ( CH 2 ) m — O — , — o— ! c— CH Λ.— S o— o — s R ι N D — (C4)m — J — N , II I I II || | 2 m , c ' c H 2)m , or comprises a binding moiety B that binds specifically to an anlalyte, wherein: R 1 has the formula X(CH m ; X is -CH 3 ,-CHCH 3 , -COOH, -CO 2 (CH 2 ) m CH 3 , -OH, -CH 2 OH, ethylene glycol, hexa(ethylene glycol), -0(CΑ m CΑ 3 , -NH 2 , -NH(CH 2 ) m NH 2 , halogen, glucose, maltose, fullerene C60, a cyclic olefin, or a nucleic acid; and m is 0-30. 33. The nanoparticles of Claim 31 wherein N is a norbornenyl-containing group. 34. The nanoparticles of Claim 31 or 33 having a single polymer shell attached to them. 35. The nanoparticles of Claim 31 or 33 having a plurality of polymer shells attached to them. 36. The nanoparticles of Claim 35 having two polymer shells attached to them, the first polymer shell and the second polymer shell having different properties. 37. The nanoparticles ofClaim 34 wherein the polymer shell has redox activity. 38. The nanoparticles of Claim 35 wherein one ofthe polymer shells has redox activity. 39. The nanoparticles of Claim 36 wherein the first polymer shell has redox activity and the second polymer shell has redox activity different than that of the first polymer shell. 40. The nanoparticles of Claim 31, 32 or 33 wherein a polymer shell comprises a binding moiety B that binds specifically to an analyte. 41. The nanoparticles of Claim 40 wherein the polymer shell comprising the binding moiety B is formed by polymerizing one or more types of binding monomers of the formula N-L-B, wherein N, L and B have the same meanings as in Claim 40. 42. The nanoparticles of Claim 41 wherein the polymer shell comprising the binding moiety B is formed by polymerizing a mixture of one or more types of binding monomers and one or more types of propagation monomers. 43. A propagation monomer having the formula P-L-N, wherein: P is a moiety having a desired property selected from the group consisting of redox activity, optical activity, electronic activity, and magnetic activity; N is a cyclic olefin-containing group; L is a bond or linker whereby N is attached to P. 44. The monomer of Claim 43 wherein L is a polymer, — COO — , -CH 2 (CH 2 ) m COO— , -OCO-, -R^CH^-NR 1 -, _O(CH 2 ) m - -(CH 2 ) m - — O — ( C H 2 ) m — O — , O— O— (CHΛ— C— O- o o _ C _c— (C HΛ-— O — C— O— ) _ R 1 N _( CH2 ) _ R 1 — ( Crt ) m -J— - o R 1 -c II- -(C H 2 )-, or comprises a binding moiety B which binds specifically to an analyte; wherein: R 1 has the formula X(CH 2 ) m ; X is -CH 3 ,-CHCH 3 , -COOH, -CO 2 (CH 2 ) m CH 3 , -OH, -CH 2 OH, ethylene glycol, hexa(ethylene glycol), -O(CH 2 ) m CH 3 , -NH 2 , -NH(CH 2 ) m NH 2 , halogen, glucose, maltose, fullerene C60, a cyclic olefin, or a nucleic acid; and m is 0-30. 45. The monomer of Claim 43 wherein N is a norbornenyl-containing group. 46. The monomer of Claim 43 or 45 wherein P is a moiety having redox activity. 47. The monomer of Claim 46 wherein P is a ferrocene derivative. 48. The monomer of Claim 47 which is exø-5-norbornen-2-yl ferrocenecarboxylate or exø-5-norbornen-2-yl ferroceneacetate. 49. An initiation monomer having the formula: N - L - A wherein: N is a cyclic olefin-containing group; A is an attachment compound-containing group comprising a functional group suitable for attaching the initiation monomer to a nanoparticle; and L is a bond or a linker whereby N is attached to A. 50. The initiation monomer of Claim 49 wherein L is a polymer, — COO — , -CH 2 (CH 2 ) m COO- -OCO-, -R^CH^-NR 1 -, -O(CH 2 ) m - -(CH 2 ) m - R 1 -N C ~~-(CH 2 ) m ^ — O — ( C H 2 ) m — O — , o—C— (CH 2 *-— C— O- o II C— C— (CH^— o— c— 0 ^R l N^CH^ -R 1 N C 1 (Crt) m O R 1 R 1 O -(CH 2 ) m u. <C H, , or comprises a binding moiety B which binds specifically to an analyte; wherein: R 1 has the formula X(CH 2 ) m ; X is -CH 3 ,-CHCH 3 , -COOH, -CO 2 (CH 2 ) m CH 3 , -OH, -CH 2 OH, ethylene glycol, hexa(ethylene glycol), -©(CH^CH,, -NH 2 , -NH(CH 2 ) m NH 2 , halogen, glucose, maltose, fullerene C60, a cyclic olefin, or a nucleic acid; and m is 0-30. 51. The initiation monomer of Claim 49 comprising a norbornenyl-group. 52. The initiation monomer of Claim 51 which is a norbornenyl-containing alkanethiol 53. The initiation monomer of Claim 52 which is l-mercapto-10-exø-5- norboraen-2-oxy-decane. 54. A method of detecting or quantitating an analyte comprising: (a) contacting a sample suspected of containing the analyte with the nanoparticles of Claim 40; and (b) detecting or measuring the property or properties of the nanoparticles in order to detect or quantititate the analyte. 55. The method of Claim 54 wherein the analyte is a nucleic acid and B is an oUgonucleotide with a sequence complementary to at least a portion ofthe sequence of the analyte nucleic acid. 56. The method of Claim 54 wherein the analyte is an antigen or a hapten and B is an antibody specific for the antigen or hapten. 57. The method of Claim 54 wherein the property detected or measured is fluorescence. 58. The method of Claim 54 wherein the property detected or measured is color. 59. The method of Claim 54 wherein the property detected or measured is redox activity. 60. A kit for detecting or quantitating an analyte comprising a container holding the nanoparticles of Claim 40. 61. The kit of Claim 60 wherein the analyte is a nucleic acid and B is an oligonucleotide with a sequence complementary to at least a portion ofthe sequence of the analyte nucleic acid. 62. The kit of Claim 60 wherein the analyte is an antigen or a hapten and B is an antibody specific for the antigen or hapten. 63. The kit of Claim 60 wherein the property is fluorescence. 64. The kit of Claim 60 wherein the property is color. 65. The kit of Claim 60 wherein the property is redox activity. 66. A binding monomer having the formula: N - L - B wherein: N is a cyclic olefin-containing group; B is a binding moiety that binds specifically to an analyte; and L is a bond or a linker whereby N is attached to B. 67. The binding monomer of Claim 66 wherein N is a norbornenyl-containing group. 68. The binding monomer of Claim 66 or 67 wherein B is an oligonucleotide. 69. The binding monomer of Claim 66 or 67 wherein B is an antibody. 70. A polymer formed by polymerizing one or more types of propagation monomers ofthe formula P-L-N, wherein: P is a moiety which provides a desired property or properties to the polymer; N is a cyclic olefin-containing group; and L is a bond or a linker whereby N is attached to P. 71. The polymer of Claim 70 wherein N is a norbornenyl-containing group. 72. The polymer of Claim 70 or 71 wherein L comprises a binding moiety B that binds specifically to an analyte. 73. A method of detecting or quantitating an analyte comprising: contacting a sample suspected of containing the analyte with the polymer of Claim 72; and detecting or measuring the property or properties ofthe polymer in order to detect or quantitate the analyte. 74. The method of Claim 73 wherein the analyte is a nucleic acid and B is an oligonucleotide. 75. A kit for detecting or quantitating an analyte comprising a container holding the polymer of Claim 72. 76. A method of detecting or quantitating an analyte comprising: (a) contacting the analyte with a type of binding monomers having the formula: N - L - B wherein: N is a cyclic olefin-containing group; B is a binding moiety that binds specifically to the analyte; and L is a bond or a linker whereby N is attached to B; so that the binding monomers bind to the analyte; (b) then adding a type of propagation monomers having the formula P-L-N, wherein: P is a detectable or measurable property; N is a cyclic olefin-containing group; and L is a bond or linker whereby N is attached to P; so that the propagation monomers polymerize to form a polymer attached to the analyte; and (c) detecting or measuring the property or properties ofthe polymer attached to the analyte in order to detect or quantitate the analyte. 77. The method of Claim 76 wherein N is a norbornenyl-containing group. 78. The method of Claim 76 or 77 wherein the analyte is a nucleic acid and B is an oligonucleotide. 79. The method of Claim 78 further comprising: (i) providing a substrate having a type of capture oligonucleotides attached thereto which have a sequence complementary to at least a portion of the sequence ofthe analyte nucleic acid; and (ii) contacting the analyte nucleic acid with the substrate so that the analyte nucleic acid hybridizes to the capture oligonucleotides prior to performing steps (a) through (c). 80. The method of Claim 76 or 77 wherein P is fluorescence. 81. The method of Claim 78 wherein P is fluorescence. 82. The method of Claim 79 wherein P is fluorescence. 83. A kit for detecting or quantitating an analyte comprising; (a) a container holding a type ofbinding monomers having the formula: N - L - B, wherein: N is a cyclic olefin-containing group; B is a binding moiety that binds specifically to the analyte; and L is a bond or a linker whereby N is attached to B; (b) a container holding a type of propagation monomers having the formula: P-L-N, wherein: P is a detectable or measurable property; N is a cyclic olefin-containing group; and L is a bond or linker whereby N is attached to P; or (c) both (a) and (b). 84. The kit of Claim 83 wherein N is a norbornenyl-containing group. 85. The kit of Claim 83 or 84 wherein P is fluorescence.

Inventors: MIRKIN CHAD A, NGUYEN SONBINH T, MIRKIN, CHAD, A., NGUYEN, SONBINH, T.
Applicants: MIRKIN CHAD A, NANOSPHERE LLC, NGUYEN SONBINH T, MIRKIN, CHAD, A., NGUYEN, SONBINH, T.
Application year: 1999
Main classification: G01N33
IPC codes: A61K47, B01J19, C08G61, G01N33