Porous coating pigment and a method for its production

Abstract: The invention is based on the idea of preparing porous calcium carbonate particles via a degradation reaction from a crystalline initial material which contains the initial components for forming calcium carbonate and additionally initial components for forming the reaction products to be removed from the initial material. In the reaction a substantial portion of the calcium carbonate forms a porous frame in the space occupied by the initial material, around the open space left by the matter leaving the initial material. The invention is also based on the use of such porous calcium carbonate particles as a pigment absorbing printing inks or their solvents on the surface of a printing substrate.

Description: The invention relates to coating pigments. The invention also relates to a printing substrate according to the preamble of Claim 4. The pigments to which the invention relates are commonly used for the coating of a material web, such as paper or board. The printing substrates to which the invention relates are, for their part, used as substrates in forming text, pictures or other such symbols by adding printing ink onto the substrate. Typical printing techniques include techniques using liquid-containing printing inks, in particular inkjet printing. Typical printing substrates include paper and board. The printing substrate may also be an inkjet printing paper. "Inkjet printing paper" denotes paper which is used as the printing substrate when the inkjet printing technique is used. Inkjet printing paper may be, for example, a strongly or weakly stock-sized paper, a wood-free stock-sized or surface-sized paper or a paper developed specifically for inkjet printing. Producing a good print quality by the inkjet printing technique sets both structural and physicochemical requirements on the surface part of the paper. The main objective regarding the paper is that ink should dry as rapidly as possible on the paper surface and should not penetrate into the fibre layer. Thus better colour density and contrast are achieved and, furthermore, print through is reduced. The most important requirements set on successful inkjet printing are: the ink must dry very rapidly on the surface of the printing substrate; the density of the print must be high; the side walls must be sharp; dot gain must be controllable; and the print must be well resistant to water, light and rubbing. The most important property of inkjet printing paper in meeting the above-mentioned requirements in colour printing is ink absorbency, which includes absorption speed, absorption capacity and the orientation of absorption. The absorption speed must in particular in colour printing be so high that a preceding drop has time to become absorbed before the following ink drop is printed into contact with it. Thus the mixing of the colours can be reduced and the print quality be improved. The absorption time of a drop should preferably be at maximum a few milliseconds. High absorption capacity on the surface of paper for its part helps to bind a sufficient amount of ink in the vicinity of the paper surface. If too little ink is absorbed, the resistance to rubbing of the print decreases, and if the ink is absorbed too strongly, density is reduced and print through may increase. The orientation of absorption for its part affects the ink dot gain. In single-colour printing, the requirements set on absorption properties are not as high as in colour printing. In single-colour printers the setting time for a drop may be up to 1 - 10 seconds, whereas in multi-colour printers a setting time of even less than 1 ms may be required in order that the ink drops should not become mixed. If the paper surface is sufficiently porous, rapid setting may be achieved, in which case the solvent in the ink drop does not have time to spread the drop too much and, also, successively printed drops will not become mixed together. The porosity of the paper surface should also be uniform in order that absorption should be as homogeneous as possible. The surface of the printing substrate should preferably have densely and evenly distributed narrow pores in the orientation of the substrate thickness. In the manufacture of a printing substrate, it is known to apply, to the surface of the substrate, coating compositions which contain pigments in order to improve, for example, its printing and optical properties. In prior art there has not been available an inexpensive mineral-based pigment by means of which a sufficiently high absorbency on paper could be obtained economically. Synthetic, silicate-based porous pigments have been used for increasing the absorbency of paper and board. These pigments are, however, quite expensive. It is an object of the invention to eliminate the deficiencies described above and to provide a pigment of a completely novel type and a method for its production. It is also an object of the invention to provide a printing substrate of a completely novel type. The invention is based on the idea that, in order to produce a pigment with good absorbency, porous calcium carbonate particles are produced through a degradation reaction from a crystalline initial material which contains the initial components for the forming of calcium carbonate and additionally initial components for the forming of reaction products to be removed from the initial material. In the reaction, a substantial portion of the calcium carbonate forms a porous frame in the space occupied by the initial material, around the open space left by the matter leaving the initial material. Calcium carbonate crystals, particularly calcite crystals which include capillary pores, are formed in the reaction. The invention is also based on the use of such porous calcium carbonate particles on the surface of a printing substrate as a pigment which absorbs printing inks or their solvents. Porous calcium carbonate products have been disclosed, for example, in U.S. Pat. No. 5,007,964. These products, however, consist of agglomerated particles of calsium carbonate, resembling a bunch of grapes, or of aggregates which have been grown in several directions around the primary cores to form rosette-like crystal structures, as opposed to the particles according to the present invention, i.e. the unitary calcite crystals which include capillary pores. According to the invention, it has been discovered that calcite crystals with desired structure are obtained as a result of a heat treatment, in which crystalline calcium oxalate is heated to a sufficient temperature for degrading it to calcium carbonate and to carbon monoxide. During a heat treatment, the temperature of the starting material is raised from a starting temperature to a target temperature, this temperature being maintained for at least two hours, after which the produced calcite is allowed to cool slowly, whereupon the desired capillary pores remain in the material. European Patent Application Publication No. 0 515 757 describes a method for the preparation of porous calcium carbonate particles having ink bottle-shaped pores therein. In this method calcium carbonate powder is blended with sodium chloride, after which the powder blend is calcined at 900 °C for producing calcium oxide particles. The calcium oxide particles are then slaked and carbonated, whereupon the desired product is achieved. The above described method is quite complicated and the structure of its end product does not correspond to the structure of the crystals according to the present invention. More precisely, the invention is characterized in what is stated in Claim 1. The printing substrate according to the invention is for its part characterized in what is stated in the characterizing clause of Claim 4. Considerable advantages are gained through the invention. Thus, with the help of the invention it is possible to produce crystalline pigment particles which are substantially made up of calcium carbonate and which have a higher pore volume than in prior art and thus a more advantageous specific surface area to mass ratio. A preferred embodiment the invention has the additional advantage that the porous particles according to the invention increase the speed of ink absorption into the substrate surface as compared with calcium carbonate particles according to prior art. This has an advantageous effect in printing by techniques which utilize liquid-containing printing inks. One significant technique of this type is inkjet printing. When the present invention is applied to inkjet printing substrates it is possible to improve the absorbency of the printing substrate and thereby improve the print quality, in particular in colour printing, in particular when soluble printing inks are used. In addition to soluble printing inks it is also possible to use in inkjet printing, for example, pigmented or so-called hotmelt inks. In colour printing, cyan, magenta and yellow are commonly used as colouring ingredients. The inkjet printing technique is also used in certain colour copiers, colour fax machines and multi-purpose machines which are, for example, combinations of a printer, a copier, a fax machine and a scanner. In a preferred embodiment of the invention it is also possible to reduce the grammage of paper without weakening the other properties, such as strength or optical properties, of the paper. The invention will be examined below in greater detail with the help of a detailed description with reference to the accompanying drawings. Figure 1 depicts the mass of a material which is initially calcium oxalate monohydrate and later its degradation product, as a function of temperature when the material is heated. Figure 2 is an electron microscope photograph of calcium oxalate monohydrate at 20 °C. Figure 3 is an electron microscope photograph of a material produced from the material of Figure 2 in accordance with Figure 1, in an air atmosphere by heating it to 550 °C. Figure 4 is an electron microscope photograph of a material produced from the material of Figure 2 in accordance with Figure 1, in an air atmosphere by heating it to 570 °C. Figure 5 is an electron microscope photograph of a material produced from the material of Figure 2 in accordance with Figure 1, in an air atmosphere by heating it to 600 °C. Figure 6 is an electron microscope photograph of a material produced from the material of Figure 2 in accordance with Figure 1, in an air atmosphere by heating it to 700 °C. Figure 7 is an electron microscope photograph of a material produced from the material of Figure 2 in accordance with Figure 1, in an air atmosphere by heating it to 800 °C. Porous calcium carbonate particles are prepared from a solid calcium oxalate Ca(OX) 2 •H 2 O by heating. As described above, it is preferable that the temperature of the material is risen fairly rapidly from a starting temperature to a target temperature and that the target temperature is maintained for a sufficient time for the formation of crystalline calcium carbonate. Typical starting temperatures are in the range from 0 °C to 40 ° C, and the heating time in a target temperature is typically in the range from 0.1 hours to 10 hours, preferably in the range from 0.5 hours to 3 hours. After the heat treatment, porous crystals of calcite are slowly cooled back to a temperature of the environment. The cooling can, for instance, be effected by leaving the product in the heating appliance which is being switched off. Thus, the cooling times are typically and approximately 1.01 to 20 times, preferably 1.1 to 5 times, longer than the used heating times. If a continuous process is used, processing times shorter than mentioned above may be preferred. Figure 1 shows the mass of the solid as a function of temperature when a solid which is calcium oxalate is heated. The mass of the solid is depicted as heated in nitrogen, air and carbon dioxide atmospheres. When the solid is heated to a temperature slightly above 100 °C, a reaction in which the crystallization water separates from the solid begins to take place. As the reaction progresses, the mass of the solid respectively decreases in accordance with reaction equation I: Ca(OOC) 2 •H 2 O → Ca(OOC) 2 + H 2 O. Water leaves as vapour, and the mass of the solid theoretically drops to 87.7 % of the initial mass. When the temperature has risen to 160 °C, the crystallization water has become removed. When the temperature is further raised to approx. 440 °C, there begins to occur the following reaction, in which carbon monoxide leaves the solid, and porous calcium carbonate remains. Reaction equation II is as follows: Ca(OOC) 2 → CaCO 3 + CO. Ca(OOC) 2 has degraded completely when the temperature has risen in a nitrogen or air atmosphere to approx. 480 °C and in a carbon dioxide atmosphere to approx. 510 °C. At this time the mass of the solid is theoretically 68.5 % of the initial mass. When the formed calcium carbonate is heated further to above approx. 580 °C, there begins to occur in a nitrogen or air atmosphere a reaction according to reaction equation III, in which carbon dioxide leaves the solid. CaCO 3 → CaO + CO 2 . The final product of this reaction is calcium oxide, which is not suitable for use as a coating pigment. For this reason, when calcium carbonate particles are produced in a nitrogen or air atmosphere by heating, the temperature must not be raised above 580 °C. However, when the heating is carried out in a carbon dioxide atmosphere, the degradation of calcium carbonate to calcium monoxide according to reaction equation III does not occur, and higher temperatures can be used. The calcium oxalate initial material is preferably in a hydrous form, containing one or two water molecules per one calcium oxalate molecule. The initial material is preferably at least 50 % pure. Figure 2 shows the structure of one initial material seen through an electron microscope, and Figures 3 - 7 show the structures of the materials formed from the initial material by heating it to different temperatures. The heating was done in a nitrogen atmosphere. There form open pores inside the structure at those sites from which water or carbon monoxide is evaporated and vaporized. The figure shows that the porosity of the material increases as a function of heating temperature. For this reason, considering the porosity of the calcium carbonate particles, it is advantageous to heat the material to a temperature of 480 - 800 °C, highly advantageous to heat it to 550 - 650 °C. Heating to above 580 °C must be carried out in a carbon dioxide atmosphere. In consequence to the heat treatment, the specific surface area of the material multiplies. The specific surface area of a pigment according to the invention is at least 4.0 m 2 /g, preferably approx. 5.0 - 100.0 m 2 /g and highly preferably above approx. 10 m 2 /g. Calcium carbonate particles can be prepared by grinding the calcium oxalate initial material to such a particle size that, when this powder is heated, a suitable calcium carbonate particle size is obtained. In a preferred process for the production of porous calcium carbonate particles the procedure is as follows: Powder consisting of calcium oxalate monohydrate is taken. The powder is heated in order to remove the crystallization water and to degrade the calcium oxalate by raising the temperature of the powder from room temperature to approx. 600 °C, and by maintaining this temperature for approx. 140 - 200 minutes. Heating to above 550 °C is carried out in a carbon dioxide atmosphere. At temperatures lower than this, an atmosphere of, for example, air can be used. The formed calcium carbonate material is cooled to room temperature in approx. 150 - 300 minutes. The carbon dioxide atmosphere is maintained until the temperature has dropped below 500 °C. Optionally, the calcium carbonate material is ground further to the desired particle size. For a continuous process the above parameters could be modified so that the high heating temperature is maintained for approx. 5 - 400 minutes and the cooling to an end temperature is effected in 10 - 300 minutes. Thereafter the powder of a porous calcium carbonate material can be slurried and used for the preparation of a coating material. Examples of pigments which can be used in the coating composition in addition to calcium carbonate particles according to the present invention include ground calcium carbonate, precipitated calcium carbonate, calcium sulfate, aluminium silicate, kaolin (hydrous aluminium silicate), aluminium hydroxide, magnesium silicate, talc (hydrous magnesium silicate), titanium dioxide and barium sulphate, and mixtures of these. Synthetic pigments can also be used. Special kaolins and calcium carbonates, as well as barium sulphate and zinc oxide, can also be mentioned as examples of special pigments. In principle, any known binding agents commonly used in paper manufacture can be used as binders in the coating composition. In addition to individual binders it is also possible to use mixtures of binding agents. Examples which can be mentioned of typical binding agents include synthetic latex-type binders consisting of polymers or copolymers of ethylenically unsaturated compounds, such as butadiene-styrene type copolymers which may additionally contain a comonomer having a carboxylic group, such as acrylic acid, itaconic acid or maleic acid, and poly(vinyl acetate) which contains comonomers having carboxylic groups. In combination with the above-mentioned agents it is further possible to use as binders, for example, water-soluble polymers, starch, CMC, hydroxy ethyl cellulose and poly(vinyl alcohol). In the coating composition there can further be used conventional additives and adjuvants, such as dispersing agents (e.g. sodium salt of poly(acrylic acid)), substances for adjusting the viscosity and water retention of the composition (e.g. CMC, hydroxyethyl cellulose, polyacrylates, alginates, benzoate), so-called lubricating agents, hardeners for improving the water resistance, optical agents, anti-foaming agents, pH regulating agents and substances for preventing product degradation. The lubrication agents include sulphonated oils, esters, amines, calcium or ammonium stearates; the agents improving water resistance include glyoxal; the optical agents include diaminostilbene and derivatives of disulphonic acid; the anti-foaming agents include phosphate esters, silicones, alcohols, ethers, vegetable oils; the pH regulating agents include sodium hydroxide, ammonia; and finally, the anti-degradation agents include formaldehyde, phenol and quaternary ammonium salts. The coating compositions according to the present invention can be used both as so-called pre-coat pastes and as surface coating pastes. A coating composition according to the invention contains mainly 100 parts by weight of at least one pigment, 0.1 - 50 parts by weight of at least one binder and 0 - 10 parts by weight of other additives known per se . 1 - 100 parts by weight of the pigment is a pigment made up of porous calcium carbonate particles according to the present invention. The typical composition of a coating mixture is as follows: Porous calcium carbonate pigment 20 - 100 parts by weight Conventional calcium carbonate pigment 80 - 0 parts by weight Thickener 0.1 - 2.0 parts by weight Binder 1 - 20 parts by weight Additives and adjuvants 0.1 - 10 parts by weight Water balance The components of the compositions are typically added in the following order: 1. Main pigment 2. Other pigments 3. Water-soluble binders 4. Latexes 5. Additional water and pH regulating agents The pigments are usually mixed with the coating composition in a slurry. In the present invention, "printing substrate" denotes a material web or a material web coated with a coating agent. "Material web" for its part denotes paper or board or a corresponding cellulose-containing material which is derived from a lignocellulosic raw material, in particular from wood or from annual or perennial plants. Said material may be wood-containing or wood-free, and it may be produced from mechanical, semi-mechanical (chemi-mechanical) or chemical pulp. The pulp may be bleached or unbleached. The material may also contain recycled fibres, in particular reclaimed paper or reclaimed board. The grammage of the material web typically ranges from 30 to 250 g/m 2 , in the manufacture of coated paper it is preferably approx. 30 - 100 g/m 2 . In the manufacture of a printing substrate according to the invention there is applied to the first, second or both sides of the cellulose-containing material web a coating composition which contains a pigment component consisting of porous calcium carbonate. The porous calcium carbonate particles present in the pigment may be prepared, for example, by a method similar to that in the preceding example. The porous calcium carbonate particles are deemed to be particles which substantially consist of calcium carbonate and which comprise pores so that the mass of these particles is at least 10 %, preferably 20 - 80 %, highly preferably 40 - 70 %, of the mass of a particle produced of a continuous calcium carbonate crystal having a corresponding outer volume. The specific surface area of the porous calcium carbonate particles is at least 10 m 2 /g, preferably more than 15 m 2 /g, and highly preferably more than 30 m 2 /g. According to the invention, such particles should make up at least 1 %, preferably more than 10 %, highly preferably more than 40 %, and most suitably 80 % - 100 %, of the calcium carbonate particles in the printing substrate. When a pigment such as this is used instead of a conventional calcium carbonate pigment, the absorbency of the printing substrate can be improved by at least 10 %, and advantageously by at least 30 %. Options deviating from the embodiments described above are also conceivable within the framework of the present invention. Calcium carbonate particles and pigment substances can also be used for the absorption of a liquid substance in, for example, blotting papers. The pigment may also be added to other coating substances, such as paints. The following, non-limiting examples illustrate the invention: Example 1. Preparation of calcium carbonate particles In this experiment, 2 - 4 g of an analytically pure calcium oxalate (CaC 2 O 4 •H 2 O) was taken, and it was divided and placed in porcelain crucibles. The samples were heated each in turn in a muffle furnace in an air atmosphere from room temperature so that the temperature of the first sample was raised to 510 °C, that of the second to 530 °C, and those of the subsequent samples respectively to 550 °C, 570 °C, 600 °C, 700 °C and 800 °C. The samples were each kept at the maximum temperature for approx. 2 - 3 hours, whereafter they were cooled inside the furnace slowly to room temperature. A portion of each sample was coated with a very thin gold layer, whereafter the samples were examined using an electron microscope. Some photographs are shown at a magnification of approx. 10,000 times in Figures 3 - 7. Of the cooled samples, the samples heated to 550 °C and to 800 °C were selected for an analysis by X-ray diffraction measurement. Samples of the original calcium oxalate and of a finely-divided calcite were selected as reference samples. The analysis of the samples showed that the sample heated to 550 °C was calcite. The sample heated to 800 °C, for its part, was calcium oxide. The calcium oxide was in an amorphous form so that the granules were clearly separate one from another. The sample heated to 550 °C was crystalline calcite. Furthermore, the sample heated to 600 °C was analyzed by measuring the specific surface area of the sample by using a Micromeritics 2200 & 2205 type surface area analyzer. The specific surface area obtained for the sample by assuming that the specific weight of calcite was 2.71 g/cm 3 was 15 m 2 /g. Example 2. Coating of a paper web A coating composition is produced by mixing together 70 parts by weight of a porous calcium carbonate pigment produced according Example 1, 30 parts by weight of kaolin, 0.4 parts by weight of CMC, and 12 parts by weight of a styrene-butadiene latex. The coating paste is used for the coating of a paper web in a Heli-coater laboratory coater (blade coater). The paper web used is a wood-free paper having a grammage of 60 g/m 2 , and the coating composition is applied to it at a rate of 10 g per square metre. The coated paper has an excellent ink and solvent absorbency, which prevents the spreading of inks in connection with inkjet printing and speeds up the drying of ink.

Claims: Use of a porous calcium carbonate produced by heating from calcium oxalate as a substance absorbing printing ink or solvent on the surface of a cellulose-containing material web. Use according to Claim 1, wherein the cellulose-containing material web is paper or board. Use according to Claim 1, wherein the cellulose-containing material web is inkjet printing paper. A cellulose-containing printing substrate which has a coating layer which contains calcium carbonate particles, characterized in that it comprises porous calcium carbonate particles obtainable by heating from calcium oxalate. A printing substrate according to Claim 4, characterized in that at least 5 % of the calcium carbonate particles are porous calcium carbonate particles having capillary pores and a specific surface area of at least 10 m 2 /g and a mass of 20 - 80 % of the mass of a particle of a dense continuous calcium carbonate having the corresponding outer volume. A printing substrate according to Claim 5, characterized in that the specific surface area of the porous particles is at least 20 m 2 /g. A printing substrate according to Claim 5 or 6, characterized in that the mass of the porous particles is 40 - 70 % of the mass of a particle of a continuous calcium carbonate having the corresponding outer volume. A printing substrate according to any of Claims 5 - 7, characterized in that at least 10 % of the calcium carbonate particles are porous particles. A printing substrate according to any of Claims 5 - 8, characterized in that at least 20 - 80 % of the calcium carbonate particles are porous particles. A printing substrate according to any of Claims 5 - 9, characterized in that the cellulose-containing substrate is a paper or board having a grammage of 30 - 500 g/m 2 . A printing substrate according to any of Claims 5 - 10, characterized in that it is an inkjet printing paper. A printing substrate according to any of Claims 5 - 11, characterized in that , in addition to calcium carbonate particles and porous calcium carbonate particles, the coat contains particles of at least one third kind. A printing substrate according to Claim 12, characterized in that the coat contains particles of calcium sulphate, aluminium silicate, kaolin, aluminium hydroxide, magnesium silicate, talc, titanium dioxide, barium sulphate and/or zinc oxide. A printing substrate according to Claim 12 or 13, characterized in that the coat contains synthetic pigment particles.

Inventors: SILENIUS PETRI, SILENIUS, PETRI
Applicants: M REAL OYJ, M-REAL OYJ
Application year: 1999
Main classification: C09C1
IPC codes: C01F11, B41J2, B41M5, D21H21, C09C1, D21H19