New use of a high strength stainless steel

Abstract: The invention relates to the use of a ferritic-austenitic stainless steel as construction material for components in the chemical industry, more particularly for components which will come into direct contact with caustic soda. Said steel is essentially consisting of, in weight -%: C ≤ 0,05 Si ≤ 0,8 Mn 0,3 - 4 N 0,2 - 0,6 Cr 28 - 35, pref. 29 - 33 Ni 3 - 10, pref. 3 - 7 Mo 1,0 - 4.0, pref. 1 - 3 Cu ≤ 1,0 W ≤ 2,0 S ≤ 0,010 Ce ≤ 0,2 and the remainder Fe with the unavoidable impurities. The steel is used for NaOH evaporators in form of tube, sheet, bar, welding material or casting.

Description: The present invention relates to the use of a high strength stainless construction steel for making of components for the process industry, especially components intended to be exposed to caustic soda. Ferritic-austenitic (duplex) stainless steels are today widely used as construction material in a number of industrial applications. The duplex steel, which is described in Swedish patent application 9302139-2 and which is characterised in 28-35% Cr, 3-10% Ni, 1,0-4,0% Mo and 0,2-0,6% N, has been found to have especially favourable and in some cases surprisingly good properties as a construction material in specific applications. The present invention relates to the use of the steel grade as a construction material within areas where sodium hydroxide (NaOH) and solutions thereof are used or prepared, and where especially favourable properties have been achieved. The alloy according to SE-9302139-2 is further on indicated as SAF 2906, which preferably contains 29-33% Cr, 3-7% Ni and 1-3% Mo. High corrosion rates can arise when steel and also other metals, such as titanium, are exposed to NaOH. In solutions with 30-48% NaOH, and at temperatures between 100 and 200°C, the corrosion rate of chromium steels diminishes with increasing chromium content of 24% and above. The corrosion rate of chromium steels can also be reduced by the addition of sodium chlorate (NaClO 3 ), which has been proved for instance for 48% NaOH and a chromium content of at least 5% in the chromium steel, and an addition of 0-1% NaClO 3 . content of at least 5% in the chromium steel, and an addition of 0-1% NaClO 3 . When using austenitic stainless steels in solutions containing NaOH exists, apart from high corrosion rates, also a great risk of stress corrosion cracking, which risk diminishes with an increasing amount of nickel in the material. Caustic soda is produced, among other methods, by electrolysis of sodium chloride solutions, whereby also chlorine gas is produced. When the diaphragm method is used, the achieved sodium hydroxide has a concentration of about 12% after the electrolysis and it contains also chlorides and in some cases chlorate. The concentration of the solution is increased by evaporation in several steps in so called NaOH evaporators. The solution is heated in these under pressure, steam evaporates and chlorides are removed (after crystallisation). The concentration of NaOH reaches up to 47% and higher in the last evaporation steps. In spite of the fact that chlorides have been removed in several steps remaining amounts of both solid (up to 8%) and dissolved chloride (up to 7%) have been proved. The temperature in the NaOH evaporators with the highest NaOH concentration is 160-170°C. The corrosion rates in a NaOH evaporator can vary heavily, above all depending on temperature and flow rates. Regarding the temperature, variations in the same part of an apparatus, for instance an evaporator tube or a wear plate, can cause so high corrosion rates locally that an unacceptable low length of life is achieved, at the same time as the major part of the material only shows insignificant corrosion. At the normally occurring temperature differences, inside for instance a NaOH evaporator tube, or at temperature alteration in connection with process changes, materials which have previously shown good length of life can therefore show high corrosion rates, which result in a substantially reduced length of life for the material. Especially high flow rates exist, apart from inside the evaporator tubes, also at the propeller of the circulation pump and at the air diffuser. These parts therefore runs the risk of being exposed to erosion corrosion, which is further aggravated with increasing amounts of undissolved salt in the solution, and consequently show high corrosion rates. Several materials, which have been used in the construction of NaOH evaporators, have in many cases an unacceptable low length of life in these exposed parts. The materials that now dominate in construction of NaOH evaporators are 26-1 (UNS S44626), Nickel 200 (UNS N02200) and Sanicro 28 (UNS N08028). Certain problems with high corrosion rates and erosion corrosion exist however, which lead to shortened life of length of the construction. Nickel 200, which essentially contains 0,15 C (max), 99 Ni, 0,10 Cu (max) and 0,20 Mg (max), is today the dominating choice of material thanks to its high resistance to corrosion by the process solution in NaOH evaporation. Tests with Sanicro 28 have been done, but the material has a limited length of life due to corrosion. Nickel 200 has however the limitation that its erosion resistance is reduced compared to stainless steels as Sanicro 28. The combination of high erosion resistance and at the same time high resistance to the process solution in NaOH evaporation would therefore be optimal. It is an object of this invention to avoid or alleviate the problems of the prior art. It is further an object of this invention to provide a high strength stainless construction steel for making of components for the process industry. It is an aspect of the invention to provide in the use of construction materials as process chemistry components to be used in caustic soda environments, the improvement which at least of the portion of the components is made of a fertitic-austinitic stainless steel alloy consisting essentially of, in weight-%: C max 0.05 Si max 0.8 Mn 0.3-4 Cr 28-35 Ni 3-10 Mo 1.0-4.0 N 0.2-0.6 Cu max 1.0 W max 2.0 S max 0.010 Ce max 0.2 and the rest Fe with normally occurring impurities and additions and wherein the ferrite content is 30-70 volume-%, balance austenite. In order to find out about the resistance and properties of the ferritic-austenitic material at exposure in different caustic soda environments a number of tests have been performed. In parallel with our new material, which we have chosen to mark SAF 2906, a number of other commercial materials have been included. The principal analysis of our new material SAF 2906 as well as of the other comparing materials are brought up in Table 1 below. Chemical analysis, in weight-%, of the testing alloys. Steel No C Si Mn Cr Ni Mo N Cu Co SAF 2906 0,02 0,3 1,0 29,0 6,7 2,2 0,37 max 0,5 SAF 2205 0,02 0,5 0,85 22,1 5,6 3,1 0,17 0,5 0,5 SAF 2304 0,03 0,5 1,0 22,5 4,8 0,3 0,1 0,5 0,5 SAF 2507 0,02 0,4 0,6 25,4 6,8 3,8 0,3 0,5 0,5 Sanicro 28 0,02 0,45 1,75 27 31 3,3 0,06 1,0 254 SMO 0,02 1,0 1,0 20 18 6,1 0,20 0,7 The tests have included corrosion testing in boiling NaOH with different concentration. The result is illustrated in Fig. 1. The duplex stainless steels have a recognised good resistance to stress corrosion cracking. Environments with up to 50% NaOH are achieved at NaOH evaporation, where for instance the duplex steels SAF 2205, SAF 2304 and SAF 2507 show high corrosion rates. Sanicro 28 discloses a better resistance than these steel grades. The new steel grade of patent 9302139-2 has been corrosion tested in boiling NaOH of different concentrations. It surprisingly shows that a very low corrosion rate is achieved, better resistance than of hitherto known duplex steels is achieved and also better than of Sanicro 28. In parallel with this, further testing of our new material SAF 2906 in solutions of NaOH/NaCl/NaClO 3 at two different concentrations has been done; one containing 10% NaOH and 2% NaCl, the other containing 50% NaOH and 7% NaCl. The solutions have contained 800 ppm ClO 3 in all cases. The results have been received as amount corroded material in mm/year, which is shown in Table 2 below. Alloy Environment Temperature °C Corrosion rate mm/year SAF 2906 10% NaOH, 2% NaCl, 800 ppm ClO 3 100 0,001 Boiling 0,001 50% NaOH, 7% NaCl, 800 ppm ClO 3 100 0,001 Boiling 0,016 Sanicro 28 10% NaOH, 2% NaCl, 800 ppm ClO 3 100 0,001 Boiling 0,001 50% NaOH, 7% NaCl, 800 ppm ClO 3 100 0,007 Boiling 0,34 Ni 200 10% NaOH, 2% NaCl, 800 ppm ClO 3 100 0 Boiling 0,001 50% NaOH, 7% NaCl, 800 ppm ClO 3 100 0,003 Boiling 0,15 It has surprisingly been shown, as can be seen from the table, that the new material marked SAF 2906 is considerably better than the hitherto best materials Sanicro 28 and Ni 200. Austenitic-ferritic steels have in addition to that a recognised good resistance to erosion corrosion. The results accounted for show, as can be seen, the possibility of a substantial increase in length of life at selection of materials for NaOH evaporators. This increase in length of life is foreseen to be possible in the use of the material (SAF 2906) as tube, sheet, bar, welding material and casting. The principles, preferred embodiments and modes of operation of the present invention have been described in the foregoing specification. The invention which is intended to be protected is defined by the appended claims.

Claims: Use of a ferritic-austenitic stainless steel alloy consisting of, in weight-%: -C max 0,05 -Si max 0,8 -Mn 0,3-4 -Cr 28-35 -Ni 3-10 -Mo 1,0-4,0 -N 0,2-0,6 -Cu max 1,0 -W max 2,0 -S max 0,010 -Ce max 0,2 and the rest Fe with normally occurring impurities and additions, where the ferrite content is 30-70 volume-%, as material for the production of apparatus, which shall meet demands for good erosion and corrosion resistance to NaOH/ NaCl/NaclO 3 process solutions in the making of caustic soda. Use of a ferritic-austenitic steel according to claim 1, characterised in that the alloy contains -C 0,02 -Si 0,3 -Mn 1,0 -Cr 29 -Ni 6,7 -Mo 2,2 -N 0,37 -Cu max 0,5. Use of a ferritic-austenitic steel according to claim 1 or 2, characterised in that the material is used for NaOH evaporators in form of tube, sheet, bar, welding material or casting.

Inventors: DELBLANC-BAUER ANNA, KANGAS PASI, NYSTROEM MAGNUS, DELBLANC-BAUER, ANNA, KANGAS, PASI, NYSTROEM, MAGNUS, Nyström, Magnus
Applicants: SANDVIK AB, SANDVIK AKTIEBOLAG
Application year: 1999
Main classification: C22C38
IPC codes: C22C38, B23K35