Method of manufacturing lightweight glazing by multilayer glass/plastic sheets

Abstract: A method of manufacturing a multilayer glass/plastic sheet for lightweight automotive glazing is disclosed. The sheet is build up with two thin glass layers, one inner (1) and one outer (2), and a thick middle layer (3) of thermoplastic. Raw sheets are manufactured as flat plates. Final process for achieving curved window panes is applying temperature (T) on the sheet and fit it to a mould (4) so that bending occurs mainly due to plastic transverse shear deformation of the plastic layer. Glass bending is limited to elastic bending of the single glass layers (1,2). Residual bending stresses in the glass layers (1,2) are avoided by incorporating pre-bending stresses in the flat glass layers (1,2). Strengthening of the final glass layers (1,2) is achieved by incorporating compression stresses on the bent pane through heat treatment and having different thermal expansion coefficients of glass and plastic.

Description: The present invention relates to a method of manufacturing glazing by multilayer glass/plastic sheets as lightweight glazing for automotive applications. At present four main types of automotive glazing are of interest for weight reduction: (1) overall reduced thickness of the glass, (2) bi-layer laminated glass/plastic sheet, (3) plastic sheets with hard and scratch resistant coating, (4) multilayer glass/plastic glazing. Weight reduction by reduced overall glass thickness is limited because of manufacturing, noise and security requirements: The glass pane must be manageable during the whole manufacturing process. The manufacturing process for laminated windshields disclosed in EP 0 245 175 B1 will allow only slight reduction in thickness. Furthermore thickness reduction will increase the interior noise level. Thinner glass transforms windnoise as well as body vibrations more directly to the interior. That means also sidelites, mostly affected by windnoise, are limited with regard to thickness reduction. At last all glazing must withstand security requirements. This requires a certain thickness of glazing all around the vehicle. To overcome the situation described above one approach is to build glazing from bi-layer sheets made from glass and plastic. Main disadvantage is the minor scratch resistance of the plastic surface, which is not satisfying for automotive applications at the moment. Lightweight glazing could also be achieved by fully plastic sheets, covered with scratch resistant surfaces. Several disclosures are dealing with the subject, but at the moment none of these technologies has been introduced on high volume products. A very efficient approach for lightweight glazing is a "Sandwich" glazing with a multilayer sheet: Two thin glass layers, one inner and one outer, combined with a thick middle layer made of plastic. Disadvantage at the moment is the manufacturing process. Handling of the thin glass layers is very difficult, that means size of sheets is limited, especially for curved panes. Such a multilayer sheet is disclosed in EP 0669205. The sheets are provided either as flat plates or as curved panels. The manufacturing process discussed for curved panels uses preformed inner and outer glass layers, which are either bonded together with a plastic layer in the middle or are filled with melted plastic to create the middle plastic layer. But, as both glass layers are very thin and therefore subjected to breakage, handling of the pre-curved glass layers is even more difficult as it is for the flat glass layers of the flat panels. Therefore, it is a primary object of the present invention to provide a method of manufacturing lightweight automotive glazing based on the Sandwich approach with multilayer sheets with none of the above mentioned drawbacks. According to the present invention, there is provided a method of manufacturing multilayer glass/plastic panes for lightweight automotive glazing according to claim 1, comprising: a multilayer sheet with thin inner and outer glass layers, both layers have 1/5 or less of total sheet thickness, to face inside and outside the vehicle; a thermoplastic layer in between said glass layers joined by bonding or welding to the glass layers; a raw sheet manufactured as flat plate; a pre-bending stress incorporated in each flat glass layer to avoid residual bending stresses in the final curved glass layers; a bending process to match curved shapes of automotive glazing by using thermal deformation of the thermoplastic layer; a post heat treatment of the final panel to strengthen the glass layers by incorporating compression stresses in the glass layers. The above and other objects, features and advantages of the present invention will become more apparent from the following description when taken into conjunction with the accompanying drawings. FIG. 1 is a cross-sectional view on the single flat raw layers and the pre-bending stresses in the glass layers. FIG 2 is a cross-sectional view of the flat pane in a mould and the stresses in each layer. Fig. 3 is a cross-sectional view of the pane bent to it's final shape in the mould and the resulting stresses. Fig. 4 is a cross-sectional view on the finished pane showing the final cutting lines of the pane's edges and incorporated compression stresses in the glass layers. Figure 1 shows the structural principle of the new compound before the manufacture with inner glass layer 1, outer glass layer 2 and the middle thermoplastic layer 3. All three layers are joined either by an additional film of adhesive between each layer or by welding both glass layers to the thermoplastic layer by melting the plastic of the thermoplastic layer. For handling and process reasons such a structure is to be manufactured as flat plate. Therefore all raw sheets are flat before joining. To avoid residual bending stresses in the glass layers after bending to their final shape, pre-bending stresses are incorporated in the glass layers as it is done for tempered glass. Principal stress distribution is also shown in figure 1. For further work an initial pane is cut out of the flat sheet for further forming. Next step is the bending of the initial pane in a mould 4 as shown in Figure 2. The whole pane is heated to the glass temperature T of the thermoplastic layer. Both glass layers are not affected from thermal deformation because their glass temperature is much higher. Then a load F is applied to fit the pane to the mould 4, see Figure 3. The load can be gravity load, heated air streams or anything other applicable. Under such conditions bending of the pane results mainly from the shear deformation of the thermoplastic layer 3 due to it's thermal weakness. Both glass layers 1, 2 can not act as counterparts like the flanges on an H-beam, because of the shear weakness of the middle layer 3. Their only contribution to bending stiffness is the bending stiffness of each single glass layer. Due to the low thickness of the glass proposed here bending radii of less than 1 m could be achieved without exceeding strength of the glass. Stress distribution before and after bending are shown both in Figure 2 and 3: Before bending the pre-bending stresses in both glass layers are as shown in Figure 2. Stresses from the resulting counter bending moment to achieve static equilibrium of bending moments are neglected because of the much higher bending stiffness of the complete pane which is acting as a structural Sandwich. After bending the pre-bending stresses in both glass layers disappear, see Figure 3. Also no shear and bending stresses results in the plastic layer because of complete plastic thermal deformation. In some cases, especially if there is a slight crown in the pane, shell stresses may appear somewhere in the glass layers. Then local heat can be applied on the glass layers for a very short time at these high stressed areas so that stress peaks can be reduced by plastic thermal deformation. Last step of the process as shown in Figure 4 is cutting the edges of the pane to it's final shape. As can be seen at the cutting lines 5 the cut off from the inner glass layer 1 is longer than the cut off from the outer glass layer 2, which is a result of the said shear bending. To achieve a better strength of the glass surface a compression stress can be introduced in both glass layers during cooling the pane. When heated and cooled in a defined way, the plastic layer is drawing more than the glass layers which induces a favourable compression stress to the glass. Final stress distribution is also shown in Figure 4.

Claims: A method of manufacturing multilayer glazing sheets for automotive applications with an outer and inner layer (1,2) with very thin glass, each 1/5 or less of total sheet thickness, to face outside and inside the vehicle; and a thermoplastic layer (3) between the glass layers with specific weight less than glass to achieve overall weight reduction, with all layers bonded together by two additional films of adhesive, one between inner glass and plastic layer and one between outer glass and plastic layer, or with the glass layers (1, 2) joined to the thermoplastic layer (3) by melting of the thermoplastic layer (3), whereby a raw sheet is manufactured as flat plate, characterised by the following bending process: The flat pane is heated to process temperature which is glass temperature of plastic layer (3), bending curvature of final shape is applied, whereby bending of the pane is a result mainly of the plastic transverse shear deformation of the plastic layer (3) due to thermal deflection, and only elastic bending in glass layers, (1,2) but no plastic deformation occurs because process temperature is far below glass temperature of glass. A method according to claim 1, characterised by incorporating pre-bending stresses in both glass layers in such a way that bending stresses disappears in the glass layers (1, 2) after bending the sheet to its final shape. A method according to claim 2, characterised by cutting the sheet to a preliminary shape of the pane. A method according to claim 3, characterised by bending the flat pane in a mould by applied forces or gravity. A method according to claim 1, characterised by heating glass layers (1,2) during bending locally to glass temperature of glass for a short time to achieve defined locally plastic deformation in the glass layers (1, 2). A method according to claim 1 and 5, characterised by post heat treatment to achieve an overall compression stress in both glass layers (1, 2) by having different thermal expansions coefficients of glass and plastic layers.

Inventors: DOERFLER THOMAS, DOERFLER, THOMAS
Applicants: FORD GLOBAL TECH LLC, FORD GLOBAL TECHNOLOGIES, LLC
Application year: 1999
Main classification: B32B17
IPC codes: B32B17