Polyisocyanate compound, process for producing the same and optical resin materials using the same

Abstract: Provided are novel polyisocyanate compounds of the general formula (I) (wherein Z represents a direct bond or -CH 2 -) which are useful as starting compounds for optical resin materials having excellent optical characteristics such as a high refractive index and a low dispersion, and a process for producing this compound at good efficiency. Further provided is a process for producing the desired polyisocyanate compounds through a tricarboxylic acid ester and a tricarbonyl hydrazide using a dihalogeno-aliphatic carboxylic acid lower alkyl ester and a thioglycolic acid lower alkyl ester as starting materials. According to a second process the compounds (I) wherein Z is -CH 2 - are prepared through a tricarboxylic acid ester and a tricarbonyl hydrazide using a propiolic acid lower alkyl ester and a thioglycolic acid lower alkyl ester as starting materials.

Description: The present invention relates to a polyisocyanate compound and a process for producing the same. More specifically, the present invention relates to a novel polyisocyanate compound useful as a starting material for the production of an optical resin material which has excellent optical characteristics such as a high refractive index and a low dispersion, and a process for producing the same at good efficiency. Moreover the present invention relates to an optical resin material using the same. More specifically, it relates to an optical resin material which has excellent optical characteristics such as a high refractive index, a low dispersion, an excellent transparency, lack of optical distortion and the like, and which is also good in a heat resistance, a solvent resistance and a weatherability. This optical resin material is excellently suited for the production of high performance optical products, such as a lens, a prism, optical fibers, a substrate for a recording medium, a filter, a glass, a vase and the like. Prior Art In comparison with a glass, plastics are lightweight, hard to break, and easy to dye. Therefore, in recent years plastics have been applied to a broad range of uses in optical products like various lenses and others, as well as in ornamental products having an improved optical appearance. As optical plastic materials, polyethylene glycol bisallyl carbonate (CR-39) and polymethyl methacrylate (PMMA) are commonly known. However, these plastic materials have a low refractive index of 1.50 or less. Therefore, when they are used as lens materials, for example, the thickness of the lenses largely increases with the increase of the required refractive power of the lens. Consequently, not only the superiority of plastics regarding their low weight is impaired, but also their aesthetic properties become undesirable. Furthermore, concave lenses in particular have been problematic in that their circumferetial thickness (edge thickness) is increased and the phenomenon of birefringence or chromatic aberration is liable to occur. Thus, in order to decrease the thickness of the lens upon making the most of the characteristics of plastics having a low specific gravity, a plastic material having a high refractive index has been in demand. As materials having such a performance several proposals were made heretofore. For example, (1) JP-A-63-46213 discloses a polymer comprising a xylylene diisocyanate compound and a polythiol compound, (2) JP-A-2-153302 proposes a resin comprising an aliphatic linear sulfur-containing difunctional isocyanate and a polythiol compound, and (3) JP-A-10-45707 describes a polymer comprising an aliphatic branched sulfur-containing difunctional isocyanate compound and a polythiol compound. Although the above-mentioned polymer (1) and resin (2) have an increased refractive index by limiting the possible compounds to be polymerized with the polythiol compound, they give rise to problems in that the Abbe number is decreased and the chromatic aberration is increased in polymer (1) and that the heat resistance is decreased in resin (2). Furthermore, the above-mentioned polymer (3) has a high refractive index and the chromatic aberration and the heat resistance are improved, while the heat resistance is not yet satisfactory, and the solvent resistance is also poor. In addition, these polymers are uncrosslinked polymers obtained from difunctional isocyanate compounds, so that a special crosslinking agent is needed separately to improve the heat resistance and the solvent resistance. Thus, there is a problem that the type of polythiol compounds to be polymerized is unavoidably limited. Problem Under these circumstances it is an object of the present invention to provide a novel polyisocyanate compound which can give an optical resin material having a high refractive index, a low dispersion, an excellent heat resistance and an excellent solvent resistance, and a process for producing this compound at good efficiency. It is a further object of the present invention to provide an optical resin material which has excellent optical characteristics such as a high refractive index, a low dispersion, an excellent transparency, lack of optical distortion and the like, and which is also good in a heat resistance, a solvent resistance and a weatherability, and an optical product formed of this optical resin material. Summary of the Invention The present inventors have assiduously conducted investigations to achieve the above-mentioned object, and have consequently found that a polyisocyanate compound having sulfur atoms contributing to a high refractive index and a low dispersion in the main skeleton and having three isocyanate groups as polymerization functional groups is capable to solve the problem outlined above, and that this compound can be obtained at good efficiency by a specific process. Moreover it was found that an optical resin material formed of a poly(thio)urethane obtainable by polyaddition reaction of a component containing a specific polyisocyanate compound and a component containing a compound having two or more of hydroxyl groups or mercapto groups or both of these groups in the molecule overcomes the disadvantages connected to the prior art as discussed above. Thus, the present invention provides a polyisocyanate compound of the general formula (I) wherein Z represents a direct bond or -CH 2 -. This polyisocyanate compound can be produced by the following processes (production processes 1 and 2) of the present invention. First, the production process 1 of the present invention is a process for producing a polyisocyanate compound represented by general formula (I) wherein Z represents a direct bond or -CH 2 -, comprising (a) reacting a dihalogeno-aliphatic carboxylic acid lower alkyl ester of the general formula (II) wherein X is a halogen atom, Z is as defined above, and R 1 represents a lower alkyl group, with a thioglycolic acid lower alkyl ester (III) HS―CH 2 -COOR 2 wherein R 2 is a lower alkyl group, to obtain a tricarboxylic acid ester of the general formula (IV) (b) transferring compound (IV) into the corresponding tricarbonyl hydrazide of the general formula (V) and (c) converting the carbonyl hydrazide groups into isocyanate groups. Next the production process 2 of the present invention is a process for producing 1,5-diisocyanato-3-isocyanatomethyl-2,4-dithiapentane of the formula (I-a) comprising (a) the reaction of a propiolic acid lower alkyl ester of the general formula (VI) HC≡C-COOR 3 wherein R 3 represents a lower alkyl group, with a thioglycolic acid lower alkyl ester of the general formula (III) HS―CH 2 -COOR 2 to obtain a tricarboxylic acid ester represented by general formula (VII) (b) transferring compound (VII) into the corresponding tricarbonyl hydrazide of the general formula (VIII) and (c) converting the carbonyl hydrazide groups into isocyanate groups. Further, the present invention provides an optical resin material formed of a poly(thio)urethane obtainable by polyaddition reaction of a monomer mixture comprising (A) a component containing at least a polyisocyanate compound of the general formula (I) wherein Z represents a direct bond or -CH 2 -, and (B) a component containing at least one compound having two or more groups in the molecule, each of which is individually and independently selected from a hydroxyl group and a mercapto group. Further, the present invention provides an optical product formed of the above-mentioned optical resin material. Brief Description of the Drawings Fig. 1 is an 1 H-NMR spectrum of 1,5-diisocyanato-3-isocyanatomethyl-2,4-dithiapentane obtained in Example 1. Fig. 2 is an IR spectrum of 1,5-diisocyanato-3-isocyanatomethyl-2,4-dithiapentane obtained in Example 1. Detailed Description of the Invention The polyisocyanate compound of the present invention is a novel compound represented by general formula (I) wherein Z is a direct bond or -CH 2 - As is clear from the formula (I), this novel compound has a structure based on a 2,4-dithiapentylene group as a basic skeleton branched at the 3-position thereof, and has three isocyanate groups. Since compound (I) contains sulfur atoms in the basic skeleton, the refractive index and the Abbe number of the compound itself are increased. Accordingly, when an optical resin material is produced using this polyisocyanate compound, the refractive index and the Abbe number of the optical resin material are also increased. Further, since this compound has the three isocyanate groups, it itself can act as a crosslinking agent. Accordingly, when the optical resin material is produced using this polyisocyanate compound, a high heat resistance, a high solvent resistance and excellent mechanical properties can be imparted to the optical resin material without adding any other crosslinking agent as a secondary component. A process for producing the polyisocyanate compounds of the general formula (I) is available, and there is no particular limitation in this regard. However, They can be produced at especially good efficiency according to the processes 1 and 2 according to the invention mentioned below. Production process 1 : In the process 1 the group Z in the general formula (I) may be a direct bond or -CH 2 -. Firstly, a dihalogeno-aliphatic carboxylic acid lower alkyl ester of the general formula (II) wherein X is a halogen atom, Z is -CH 2 - or a direct bond, and R 1 represents a lower alkyl group, with a thioglycolic acid lower alkyl ester (III) HS―CH 2 -COOR 2 wherein R 2 is a lower alkyl group, to obtain a tricarboxylic acid ester of the general formula (IV) In this reaction, it is preferred that 1 mol of the dihalogeno-aliphatic acid carboxylic acid lower alkyl ester (II) is reacted with substantially 2 mol of the thioglycolic acid lower alkyl ester (III) in the presence of a hydrogen halide trapping agent. An appropriate solvent can be used as required. Next, the thus-obtained tricarboxylic acid ester (IV) is reacted with hydrazine monohydrate or the like, thus transferring it into a tricarbonyl hydrazide of the general formula (V) and In this reaction a solvent such as a lower alcohol or the like can be used as required. Finally, the thus-obtained tricarbonyl hydrazide (V) is reacted with nitrous acid in, for example, a hydrochloric acid aqueous solution, and subsequently thermal rearrangement is conducted, thereby converting the carbonyl hydrazide groups into isocyanate groups. Thus, the desired polyisocyanate compound of the general formula (I) is obtained Production process 2 : The production process 2 is a process for producing 1,5-diisocyanato-3-isocyanatomethyl-2,4-dithiapentane (I-a), which is a compound of the general formula (I) wherein Z is -CH 2 -. Of course, this compound can also be produced by the above-mentioned production process 1. In production process 2, first, a propiolic acid lower alkyl ester represented by general formula (VI) HC≡C-COOR 3 wherein R 3 represents a lower alkyl group, is reacted with a thioglycolic acid lower alkyl ester of the general formula (III) HS―CH 2 -COOR 2 to obtain a tricarboxylic acid ester of the formula (VII) In this reaction, it is preferred that 1 mol of the propiolic acid lower alkyl ester (VI) is reacted with substantially 2 mol of the thioglycolic acid lower alkyl ester (III) in the presence of a radical or anionic catalyst, preferably an anionic quaternary ammonium salt. In this reaction an appropriate solvent can be used as required. Subsequently, the tricarboxylic acid ester (VII) is, as in the production process 1, reacted with hydrazine monohydrate, yielding 1,5-bis(hydrazinocarbonyl)-3-hydrazinocarbonylmethyl-2,4-dithiapentane (formula (VIII)) Finally, the carbonyl hydrazide groups of compound (VIII) are converted into isocyanate groups as in the production process 1 to obtain the desired 1,5-diisocyanato-3-isocyanatomethyl-2,4-dithiapentane of the formula (I-a) According to the present invention, the term lower alkyl group used for R 1 , R 2 and R 3 preferably and independently means an alkyl group of 1 to 6 carbon atoms, further preferred a methyl group, an ethyl group, an n-propyl group, or an isopropyl group. Besides the above-mentioned processes of the present invention the polyisocyanate compounds of the general formula (I) can also be produced by a phosgene method. This phosgene method will be described by way of example in the following. First, 1 mol of a dihalogenoacetonitrile represented by general formula (IX) wherein X represents a halogen atom, is reacted with substantially 2 mol of a thiocyanic acid salt of the general formula (X) MSCN wherein M represents an alkali metal or ammonium, in the presence of a hydrogen halide trapping agent, thereby obtaining dithiocyanatoacetonitrile (formula (XI)) Then, this is subjected to hydrogenation to lead the same to 1,5-diamino-3-aminomethyl-2,4-dithiapentane represented by formula (XII) Subsequently, the compound (XII) it is reacted with phosgene to obtain 1,5-diisocyanato-3-isocyanatomethyl-2,4-dithiapentane (I-a). The optical resin material of the present invention is formed of a poly(thio)urethane. As one of the starting materials of the poly(thio)urethane, i.e. component (A), a component containing a polyisocyanate compound of the general formula (I) as defined above is used. In order to appropriately improve the properties of the optical resin material according to the invention, the component (A) may further contain one or more types of a compound having two or more isocyanate groups in the molecule other than the compounds of the general formula (I). ,Specific examples of these compounds include o-, m- and p-xylylene diisocyanate, α,α,α',α'-tetramethyl-p-xylylene diisocyanate, α,α,α',α'-tetramethyl-m-xylylene diisocyanate, 1,3,5-tris(isocyanatomethyl)benzene, hexamethylene diisocyanate, 1,4-diisocyanatobutane, isophorone diisocyanate, norbornene diisocyanate, bis(4,4'-isocyanatocyclohexyl)methane, 1,3-bis (isocyanatomethyl) cyclohexane, 1,3,5-tris(isocyanatomethyl)cyclohexane, 1,4-diisocyanatocyclohexane, 1,3,5-triisocyanatocyclohexane, lysine triisocyanate, 2,5-bis(isocyanatomethyl)-1,4-dithian, 1,3-dithiolan-4,5-diisocyanate, 4,5-bis(isocyanatomethyl)-1,3-dithiolan, isocyanatomethyl sulfide, 2-isocyanatoethyl sulfide, bis(isocyanatomethylthio)methane, 1,2-bis(isocyanatomethylthio)ethane, bis(2-isocyanatoethylthio) methane, 1,2-bis(2-isocyanatoethylthio)ethane, 1,7-diisocyanato-2,4,6-trithiaheptane, 1,5-diisocyanato-2-isocyanatomethyl-3-thiapentane, 1,4-diisocyanato-2-isocyanatomethyl-3-thiabutane and the like. The content of the polyisocyanate compound of the general formula (I) in the component (A) is preferably 0.1 mol-% or more, especially preferably 5 mol-% or more. As the component (B), another starting material of the poly(thio)urethane, a component containing at least one compound having two or more groups in the molecule, each of which is individually and independently selected from a hydroxyl group and a mercapto group is used. This compound may be (a) a compound having two or more mercapto groups (b) a compound having two or more hydroxyl groups or (c) a compound having one or more hydroxyl groups and one or more mercapto groups. Examples of compounds having two or more mercapto groups in the molecule include 2,5-bis(mercaptomethyl)-1,4-dithian, 2,5-bis(mercaptomethyl)-1,4-dithian dimer and polymer (trimer · or higher polymer), 1,2,3-trimercaptopropane, tetrakis(7-mercapto-2,5-dithiaheptyl)methane, 1,2-ethanedithiol, 1,3-propanedithiol, tetrakismercaptomethylmethane, 2-mercaptoethyl sulfide, pentaerythritol tetrakismercaptopropionate, pentaerythritol tetrakismercaptoacetate, 1,2-benzenedithiol, 1,3-benzenedithiol, 1,4-benzenedithiol, 1,3,5-benzenetrithiol, 1,2 dimercaptomethylbenzene, 1,3-dimercaptomethylbenzene, 1,4-dimercaptomethylbenzene, 1,3,5-trimercaptomethylbenzene, toluene-3,4-dithiol, tris(3-mercaptopropyl) isocyanurate, 1,3-bis(mercaptomethyl)cyclohexane, 1,4-bis(mercaptomethyl) cyclohexane, 2,2-bis(mercaptomethyl)-1,3-propanedithiol, 1,2-bis(2-mercaptoethylthio)-3-mercaptopropane, 4,8-bis(mercaptomethyl)-3,6,9-trithia-1,11-undecanedithiol and the like. Examples of compounds having two or more hydroxyl groups in the molecule include ethylene glycol, trimethylolpropane, glycerin, dihydroxybenzene, catechol, 4,4'-dihydroxyphenyl sulfide, 2-hydroxyethyl sulfide, bisphenol A·propylene oxide 5-mol adduct, glycerin.propylene oxide 3-mol adduct and the like. Examples of compounds having one or more hydroxyl groups and one or more mercapto groups in the molecule include 2-mercaptoethanol, 2,3-dimercaptopropanol, 1,2-dihydroxy-3-mercaptopropane, 4-mercaptophenol and the like. Preferred compounds to be used in component (B) are the compounds having two or more mercapto groups in the molecule. More preferred are 2,5-bis(mercapto-methyl)-1,4-dithian compounds of the general formula (XIII) wherein n is an integer of from 1 to 20, and especially preferable are oligomers of 2,5-bis(mercapto-methyl)-1,4-dithian. With respect to the ratio of the component (A) to the component (B) in the present invention, it is preferable that the molar ratio of the isocyanate groups in component (A) to the total amount of mercapto groups and hydroxyl groups in component (B) [NCO]/([SH]+[OH]) is in the range of 0.95 to 1.05. In order to appropriately modify and improve the properties of the optical resin material the monomer mixture comprising the component (A) and the component (B) may contain one or more types of compounds having two or more vinyl groups in the molecule in addition to the components (A) and (B). In this case the ratio of these compounds used is preferably such that the molar ratio of isocyanate groups and vinyl groups to mercapto groups and hydroxyl groups ([NCO]+[vinyl])/([SH]+[OH]) is in the range of 0.95 to 1.5 and the molar ratio of vinyl groups to isocyanate groups [vinyl]/[NCO] is 0.7 or less, and that polymerizable functional groups contained in the component (B) are all mercapto groups. Examples of these compounds include 2,5-bis(2-thia-3-butenyl)-1,4-dithian, divinylbenzene, ethylene glycol di(meth)acrylate, polyethylene glycol di(meth)acrylate, a urethane-modified (meth)acrylate containing at least two (meth)acryloxy groups in a molecule and the like. The term "(meth)acrylate" includes both acrylate and methacrylate, and the term "(meth)acryloxy" includes acryloxy as well as methacryloxy. If required, an ultraviolet(UV)-absorber, a coloring matter, a pigment and the like for improving light absorption characteristics, an antioxidant, a coloration inhibitor and the like for improving a weatherability, and a release agent and the like for improving a moldability can be added to the optical resin material of the present invention. Examples of the UV-absorber include benzotriazole type, benzophenone type, salicylic acid type UV-absorbers and the like. Examples of the coloring matter and the pigment include anthraquinone type and azo type colorants and/or pigments and the like. Examples of the antioxidant and the coloration inhibitor include monophenol type, bisphenol type, high-molecular phenol type, sulfur type and phosphorus type antioxidants and the like. Examples of the release agent include fluorine-type surfactants, silicone-type surfactants, acidic phosphates, higher fatty acids and the like. Further, a catalyst may be used, as required, to improve the polymerization reactivity. In this regard amine compounds, organic metal compounds and the like are effective. Specific examples include triethylenediamine, hexamethylenetetramine, N,N-dimethyloctylamine, N,N,N',N'-tetramethyl-1,6-diaminohexane, 4,4'-trimethylenebis(1-methylpiperidine), 1,8-diazabicyclo-(5,4,0)-7-undecene, dimethyltin dichloride, dimethyltin bis(isooctylthioglycolate), dibutyltin dichloride, dibutyltin dilaurate, dibutyltin maleate, dibutyltin maleate polymer, dibutyltin diricinoleate, dibutyltin bis(dodecylmercaptide), dibutyltin bis(isooctylthioglycolate), dioctyltin dichloride, dioctyltin maleate, dioctyltin maleate polymer, dioctyltin bis(butylmaleate), dioctyltin dilaurate, dioctyltin diricinoleate, dioctyltin dioleate, dioctyltin di(6-hydroxy)caproate, dioctyltin bis(isooctylthioglycokate), didodecyltin diricinoleate, copper oleate, copper acetylacetonate, iron acetylacetonate, iron naphthenate, iron lactate, iron citrate, iron gluconate, potassium octanate, 2-ethylhexyl titanate and the like. The above-mentioned catalysts are effectively used either singly or in combination of two or more types. If a vinyl compound is contained in the monomer mixture, the use of organic peroxides, azo compounds or the like other than the above-mentioned catalyst is also effective. For example, the production of the optical resin material of the invention using the polyisocyanate compounds (I) of the invention is as follows. The uniform mixture of the component (A), the component (B), the additives and the catalyst is subjected to a known cast polymerization method, e.g. it is cast into a die which is a combination of a glass or metal mold and a gasket made of a resin, and is cured by heating. In order to facilitate the withdrawal of the resin after molding the mold may previously be subjected to a release treatment, or a release agent may be added to the mixture before cast molding. The polymerization temperature may vary depending on the compound used. It is usually in the range of -20 to +150°C. The polymerization time is from 0.5 to 72 hours. The optical resin material of the present invention can easily be dyed in water or an organic solvent using an ordinary disperse dye. To facilitate and expedite the dyeing a carrier may be added and/or heating may be conducted. The thus-obtained optical resin material can be used for a broad range of applications, preferably for the production of optical elements, especially preferably for plastic lenses. Examples In the following the present invention is illustrated more specifically by referring to Examples. However, the present invention is not limited at all to these Examples. The physical properties of the resulting polyisocyanate compounds and optical resin materials (polymers) were evaluated according to the following methods. (1) 1 H-NMR spectra (proton nuclear magnetic resonance . spectra) were measured using an FT-NMR Device Model EX 270 of JEOL. (2) IR spectra (infrared absorption spectra) were measured using a MAGNA-IR Spectrometer Model 560 of Nicolet. (3) The refractive index (n D ) and the Abbe number (ν D ) were measured at 20°C using a precision refractometer Model KPR-200 of Kalnew. (4) The appearance was observed visually. (5) The heat resistance was evaluated by measuring the dynamic viscoelasticity with a static tension of 100 g and a frequency of 10 kHz by means of a dynamic viscoelasticity-measuring device of Toyo Seiki Seisakusho. The heat resistance was determined as a temperature of a decreasing point in a chart of the modulus of elasticity obtained at a rate of temperature rise of 2°C/min. (6) The weatherability was measured by mounting a lens (optical product using an optical resin material) on a weather meter fitted with a sunshine carbon arc lamp. After 200 hours had passed, the lens was taken out, and the color thereof was compared with that of the lens before the test. The weatherability was evaluated according to the following standard. o: unchanged Δ: slightly yellowed x: yellowed (7) The solvent resistance was determined by conducting a wiping test using acetone, and was evaluated according to the following standard. o: unchanged x: The surface is roughened or swollen. (8) The optical distortion was visually observed by the Schlieren method. The optical distortion was evaluated according to the following standard. o: No distortion is observed. x: Distortion is observed. Synthesis Example Production of 1,5-diisocyanato-3-isocyanatomethyl-2,4-dithiapentane Ethyl propiolate (14.7 g, 0.15 mol) and methyl glycolate (31.8 g, 0.3 mol) of were dissolved in 125 ml of benzene. Tetrabutylammonium fluoride (0.78 g, 0.003 mol) was added as a catalyst in an ice bath, and the solution was then stirred at room temperature for 70 hours. Subsequently, the reaction solution was washed with a dilute aqueous sodium hydroxide solution and then with water, and dried. Benzene was distilled off under reduced pressure, and the residue was distilled under reduced pressure to obtain 31.1 g (0.10 mol) 1,5-bis (methyloxycarbonyl) -3-ethyloxy-carbonylmethyl-2,4-dithiapentane (melting point: 127-129°C/ 2.67 Pa(0.02 mmHg). This ester compound was dissolved in 30 ml of methanol, and added dropwise to a mixed solution of of hydrazine hydrate (45.0 g, 0.90 mol) and methanol (170 ml) at room temperature. After the completion of the dropwise addition the mixture was stirred at 70°C for 2 hours. Upon allowing the mixture to cool white crystals precipitated which were collected by filtration and recrystallized from methanolwater to obtain 22.0 g (0.075 mol) of 1,5-bis(hydrazinocarbonyl)-3-hydrazinocarbonylmethyl-2,4-dithiapentane. This hydrazide compound was dissolved in 160 g of an aqueous 7.2 wt.-% hydrochloric acid solution and suspended in 150 ml of toluene. Thereto 16.6 g (0.24 mol) of sodium nitrite were added. After the completion of the addition the stirring was continued for 1 1 hour. The organic phase was withdrawn from the suspension, washed with water, dried over magnesium sulfate, and then heated to complete the rearrangement reaction. The Toluene was fully removed from the reaction solution to obtain 11.1 g (0.045 mol) of a colorless transparent reaction product. This reaction product was identified to be the desired polyisocyanate compound from the 1 H-NMR spectrum and the IR spectrum. The 1 H-NMR spectrum of this novel polyisocyanate compound is shown in Fig. 1, and the IR spectrum thereof in Fig. 2. Example 1 A mixture of 0.08 mol of 1,5-isocyanato-3-isocyanatomethyl-2,4-dithiapentane (DS-1 in Table 1) obtained in the Synthesis Example 1, 0.12 mol of 2,5-bis(mercapto-methyl)-1,4-dithian dimer (DBMD in Table 1) and 1.2 x 10 -4 mol of dibutyltin dilaurate (DBTDL in Table 1) was uniformly stirred and then cast into glass molds for forming a lens. The mixture was heat-polymerized at 50°C for 10 hours, then at 60°C for 5 hours and further at 120°C for 3 hours to obtain a plastic lens. The properties of the resulting plastic lens are shown in Table 1. The polymer obtained by using the polyisocyanate compound of Example 1 was colorless and transparent, the refractive index (n D ) was as high as 1.70, the Abbe number (ν D ) was also as high as 35 (low dispersion), the heat resistance (116°C), the weatherability and the solvent resistance were excellent, and no optical distortion was observed. Examples 2 to 4 The same procedure as in Application Example 1 was followed to obtain a plastic lens except that monomer compositions were used as shown in Table 1. The properties of these plastic lenses are shown in Table 1. The resulting plastic lenses were colorless and transparent, the refractive index (n D ) was as high as between 1.65 and 1.69, the Abbe number (ν D ) was also as high as between 35 and 39 (low dispersion), the heat resistance (114-138°C), the weatherability and the solvent resistance were excellent, and no optical distortion was observed. Comparative Example 1 A mixture of 0.06 mol pentaerythritol tetrakismercaptopropionate (PETMP in Table 1), 0.12 mol of m-xylylene diisocyanate (XDI in Table 1) and 1.2 x 10 -4 mol of dibutyltin dilaurate (DBTDL in Table 1) was uniformly stirred and then cast into glass molds for forming a lens. The mixture was heat-polymerized at 50°C for 10 hours, then at 60°C for 5 hours and further at 120°C for 3 hours to obtain a plastic lens. The properties of the resulting plastic lens are shown in Table 1. It was found that the plastic lens was colorless and transparent, no optical distortion was observed, and the solvent resistance was excellent. However, the refractive index was as low as 1.59, and the heat resistance (86°C) was also poor. Comparative Examples 2 and 3 The same procedure as in Application Comparative Example 1 was followed except using monomer compositions as shown in Table 1 to obtain plastic lenses. The properties of these plastic lenses are shown in Table 1. It was found that the plastic lens of Comparative Application Example 2 had a high refractive index of 1.68 and was excellent in the heat resistance (128°C) and the solvent resistance. However, it was colored yellow, the Abbe number was low (25), the weatherability was poor, and the optical distortion was observed. Further, the plastic lens of Comparative Application Example 3 was colorless and transparent, the refractive index was as high as 1.68, and no optical distortion was observed. However, the Abbe number was low (29), and the heat resistance (89°C) and the solvent resistance were also poor. In Table 1 the following abbreviations were used: DS-1: 1,5-diisocyanato-3-isocyanatomethyl-2,4-dithiapentane, IMTM: bis(isocyanatomethylthio)methane, CHTI: 1,3,5-triisocyanatocyclohexane, IPDI: -isophorone diisocyanate, DBMD: 2,5-bis(mercaptomethyl)-1,4-dithian dimer, BMMD: 2,5-bis(mercaptomethyl)-1,4-dithian, BMMC: 2,5-bis(mercaptomethyl)cyclohexane, TMP: 1,2,3-trimercaptopropane, DBTDL: di-n-butyltin dilaurate, DMTDC: di-methyltin dichloride, DBTDC: di-n-butyltin dichloride, XDI: m-xylylene diisocyanate, TDI: tolylene diisocyanate, TPDI: 2,4-dithiapentane-1,3-diisocyanate PETMP: pentaerythritol tetrakis(3-mercaptopropionate), XDT: m-xylylene dithiol, PETMA: pentaerythritol tetrakis(2-mercaptoacetate) Effects of the Invention Since the novel polyisocyanate compounds of the present invention have an aliphatic chain containing sulfur atoms as a basic skeleton, the refractive index and the Abbe number are high. They have three isocyanate groups, and are easily polymerized with at least one compound having two or more hydroxyl groups in a molecule each individually and independently selected from a mercapto group and a hydroxyl group to provide a three-dimensionally crosslinked optical resin material. In addition, since the optical resin material obtained by using this polyisocyanate compound contains the sulfur atoms in the main chain and is further crosslinked, the refractive index and the Abbe number are high, the heat resistance, the weatherability, the solvent resistance and the transparency are excellent, and no optical distortion is observed. Accordingly, it is preferably used in optical products, e.g. in optical elements like lenses such as spectacle lenses or camera lenses, prisms, optical fibers, substrates for a recording medium used in optical disks or magnetic disks, filters and the like. Further, it is used in ornamental optical products such as glasses, vases and the like which are obtained by making the most use of the property of the high refractive index.

Claims: Polyisocyanate compound of the general formula (I) wherein Z represents a direct bond or -CH 2 -. Process for producing a polyisocyanate compound of the general formula (I) wherein Z represents a direct bond or -CH 2 -, comprising (a) reacting a dihalogeno-aliphatic carboxylic acid C 1 -C 6 alkyl ester of the general formula (II) wherein X is a halogen atom, Z is as defined above, and R 1 represents a C 1 -C 6 alkyl group, with a thioglycolic acid C 1 -C 6 alkyl ester (III) HS―CH 2 -COOR 2 wherein R 2 is a C 1 -C 6 alkyl group, to obtain a tricarboxylic acid ester of the general formula (IV) (b) transferring compound (IV) into the corresponding tricarbonyl hydrazide of the general formula (V) and (c) converting the carbonyl hydrazide groups into isocyanate groups. Process for producing 1,5-diisocyanato-3-isocyanatomethyl-2,4-dithiapentane of the formula (I-a) comprising (a) the reaction of a propiolic acid C 1 -C 6 alkyl ester of the general formula (VI) HC≡C-COOR 3 wherein R 3 represents a C 1 -C 6 alkyl group, with a thioglycolic acid C 1 -C 6 alkyl ester of the general formula (III) HS―CH 2 -COOR 2 wherein R 2 represents a C 1 -C 6 alkyl group, to obtain a tricarboxylic acid ester represented by general formula (VII), wherein R 2 represents a C 1 -C 6 alkyl group, (b) transferring compound (VII) into the corresponding tricarbonyl hydrazide of the general formula (VIII) and (c) converting the carbonyl hydrazide groups into isocyanate groups. Optical resin material formed of a poly(thio)urethane obtainable by polyaddition reaction of a monomer mixture comprising (A) a component containing at least a polyisocyanate compound of the general formula (I) wherein Z represents a direct bond or -CH 2 -, and (B) a component containing at least one compound having two or more groups in the molecule, each of which is individually and independently selected from a hydroxyl group and a mercapto group, which is selected from the group consisting of 2,5-bis(mercaptomethyl)-1,4-dithian, 2,5-bis(mercaptomethyl)-1,4-dithiandimer and polymer (trimer or higher polymer), 1,2,3-trimercaptopropane, tetrakis(7-mercapto-2,5-dithiaheptyl)methane, 1,2-ethanedithiol, 1,3-propanedithiol, tetrakismercaptomethylmethane, 2-mercaptoethyl sulfide, pentaerythritol tetrakismercaptopropionate, pentaerythritol tetrakismercaptoacetate, 1,2-benzenedithiol, 1,3-benzenedithiol, 1,4-benzenedithiol, 1,3,5-benzenetrithiol, 1,2-dimercapto-methylbenzene, 1,3-dimercaptomethylbenzene, 1,4-dimercaptomethylbenzene, 1,3,5-trimercaptomethylbenzene, toluene-3,4-dithiol, tris(3-mercaptopropyl) isocyanurate, 1,3-bis(mercaptomethyl)cyclohexane, 1,4-bis(mercaptomethyl) cyclohexane, 2,2-bis(mercaptomethyl)-1,3-propanedithiol, 1,2-bis(2-mercaptoethylthio)-3-mercaptopropane, 4,8-bis(mercaptomethyl)-3,6,9-trithia-1,11-undecanedithiol, ethylene glycol, trimethylolpropane, glycerin, dihydroxybenzene, catechol, 4,4'-dihydroxyphenyl sulfide, 2-hydroxyethyl sulfide, bisphenol A·propylene oxide 5-mol adduct, glycerin·propylene oxide 3-mol adduct, 2-mercaptoethanol, 2,3-dimercaptopropanol, 1,2-dihydroxy-3-mercaptopropane, 4-mercaptophenol. Optical resin material according to claim 4, wherein the component (B) contains at least one compound of the general formula (XIII) wherein n is an integer of from 1 to 20. Optical resin material according to any of claims 4 and 5, wherein the optical resin material has the form of a lens, a prism, an optical fiber, an optical filter or a substrate for a recording medium. Use of a polyisocyanate compound according to claim 1 for the production of an optical resin material according to any of the claims 4 to 6. Use of the optical resin material according to any of claims 4 to 6 for the production of an optical product. Use according to claim 8 wherein the optical product is an optical element selected from a lens, a prism, an optical fiber, an optical filter or a substrate for a recording medium.

Inventors: JIANG JIAN, KITAHARA YOSHITAKA, JIANG, JIAN, KITAHARA, YOSHITAKA
Applicants: HOYA CORP, HOYA CORPORATION
Application year: 1999
Main classification: C07C323
IPC codes: C08G18, C07C323, G02B1