THIN-LAMINATE PANELS FOR CAPACITIVE PRINTED-CIRCUIT BOARDS AND METHODS FOR MAKING THE SAME

Abstract: The present invention provides thin-laminate panels (i.e., thin-laminate panels (2) having dielectric layers (8) about 0.006 inches (0.15 mm) or less and conductive layers (6) on either side of the dielectric layer (8)), wherein the edges of the dielectric layers of the panels are free of conductive material, such as copper. The thin-laminate panel is designed to provide necessary capacitance for all or a substantial number of the integrated circuits to be formed thereon. The thin-laminate panels of the present invention may be tested for manufacturing defects, such as short circuits, before further processing of the panels to produce PCBs. "Finishing" methods for shearing sheets of unfinished thin-laminate into the finished thin-laminate panels of the present invention in a manner that does not cause smearing of the conductive material onto the dielectric layer are also provided.

Description: DESCRIPTION THIN-LAMINATE PANELS FOR CAPACITIVE PRINTED-CIRCUIT BOARDS AND METHODS FOR MAKING THE SAME Technical Field The present invention concerns thin-laminate panels used to form capacitive printed-circuit boards, and more particularly copper-clad thin-laminate panels and methods for making the same. Background Art Conductor plates ("layers") or printed circuit boards (PCBs) are typically made of one or more panels of insulating or dielectric material having a continuous thin-layer of a conducive material, such as copper, laminated one or both sides thereof. A desired layout or pattern of conducting paths and connection areas of printed circuits is then made by removing selected regions of the conductive layer from the dielectric material, to produce a PCB. One or more devices (typically integrated circuits) are then formed on or mounted on the PCB. More specifically, each panel of the PCB typically includes a dielectric material, such as resin-impregnated fiberglass cloth layer ("dielectric layer"). The panel further includes thin conductive layers (e.g., copper foil) laminated to each side of the dielectric layer. The thin-laminate panels provide necessary capacitance for all or a substantial number of the integrated circuits formed on the "capacitive" PCB. Conventional PCBS are made of multiple, thick panels (termed "thick laminates") having a thickness of about 0.059 inches or more (i.e., about 1.5 mm). However, electrical engineers are designing integrated circuits that require thinner and thinner dielectric spacing between the conductive layers that form the printed circuits. Accordingly, the thickness of the dielectric material in such panels (and thus the distance between the conductive layers) has become relatively small, typically about 0.006 inches (i.e., about 0.15 mm) or less. The actual thickness of a particular dielectric layer of a thin-laminate panel is determined based on the level of capacitance necessary for the particular integrated circuits to be formed on the capacitive PCB made from the panel. Such laminate panels are termed "thin laminates" or thin-laminate panels." The failure rate of the thin-laminate panels used to make capacitive PCBs is often high due to manufacturing defects in the thin-laminate panels themselves. The thin-laminate panels are often defective due to various factors, such as impurities in the material comprising the dielectric layers of the panels. Conductive material introduced into the dielectric layers typically causes shorts between the conductive layers forming the circuit layers (defined by the selective removal of the conductive layers). Thus, the panels would be preferably tested for such manufacturing defects prior to processing the panels to produce the capacitive PCBs. Unfortunately, the prior art thin-laminate panels cannot be accurately tested prior to processing of the PCBs due to the presence of conductive material on the edges of the dielectric layers of the panels. Specifically, thin-laminate panels are initially made in large sheets and the sheets are then sheared into relatively small panels from which PCBS are made. With reference to the prior art thin-laminate panel illustrated in Fig. 1(a), as the large sheets of thin laminate are cut or sheared to provide multiple thin-laminate panels, the relatively soft conductive layer 6 of the laminate typically smears and spreads conductive material 6a across one or more edges 12 of the panel. The connection of the two conductive layers 6 formed via the smeared conducive material 6a makes it difficult to accurately test such panels for electrical deficiencies. More particularly, the panels would preferably be tested for undesirable electrical connection between the two conductive layers of the panel due to the presence of conductive material within the dielectric layers. Such an electrical connection through the dielectric layer will not be removed with subsequent processing of the PCB. Thus, the connection through the dielectric layer may result in a defective PCB. When testing the panels for such impurities, electrical connection between the two conductive layers due to conductive material on the edge(s) of the dielectric layer, results in false failures. That is, the conductive material on the panel edges make it appear as though there is electrical conductance through the dielectric layer. Put another way, the smeared conductive material on the dielectric layer edge(s) results in short circuits between the conductive layers of the panel, signifying that the panel is defective due to electrical conductance through the dielectric layer, even though the thin-laminate panel may not be defective. The short circuits at the edges of the panels may be avoided by subsequent PCB processing of the panels. However, because conductive material on the edges of the thin-laminate panels cause short circuits that provide false failures, the panels are not tested before processing the panels to produce the PCBs. That is, if the panels are tested before processing the PCB, otherwise non-defective thin-laminate panels are discarded as being defective due to false failures caused by the smeared conductive material. PCB processing of the panels is both expensive and time consuming as are the laminate panels themselves. Thus, effective and accurate testing of the thin-laminate panels before processing the PCBs and the avoidance of false failures provide distinct advantages. Referring to the prior art thin-laminate panel illustrated in Fig. 1(b), cutting of the panel need not result in conductive material 6a being smeared completely across an edge 12 of the dielectric layer 8 to cause problems. That is, smeared conductive material that only partially covers an edge 12 of a dielectric layer 8 reduces the already small distance between the conductive layers 6 of the panel 2. This reduced distance between the conductive layers makes it difficult to accurately test such panels for electrical deficiencies. When testing the panels, the reduced distance typically allows conduction of electricity from one conductive layer to the other, making it appear as though there is electrical conductance through the dielectric layer. Such panels are then discarded as defective because it is impossible to determine whether the "short circuit" is due to conductive impurities in the dielectric layer or is simply due to conductive material on the edges of the dielectric layer (which would be eliminated during processing of the PCBs). Accordingly, with thin-laminate panels even a minor amount of conductive material on the edge of the dielectric layer may be detrimental. Because conventional PCBs are made from thick-laminate panels (e.g., about 0.059 inches (about 1.5 mm)), conductive impurities in the dielectric material is typically not a problem due to the relatively thick layer of dielectric material. In other words, the relatively large mass of dielectric material of the dielectric layer typically limits any deleterious affects of such conductive impurities. As a result, conductive material on the edges of the dielectric layer of thick-laminate panels typically is not a problem as the thick-laminate panels need not be tested. In the past, bevelers have been used to give the edges of thick-laminate panel PCBs a rounded profile. The rounded profile makes the thick-laminate panel PCBs safer to handle. Such beveling does not (and was not intended to) produce any electrical benefits. That is, once the laminate panels are processed to define the PCBs, there is not any conductive material located at regions of the laminates that would result in smearing. Additionally, current beveling processes require that the thick-laminate PCBs be beveled one at a time. Accordingly, there is a need for thin-laminate panels for the production of PCBs, wherein the thin-laminate panels have edges that have been finished so that the edges are free of conductive material. The absence of conductive material on the edges of the dielectric layers of the panels allows testing of the panels for manufacturing defects prior to processing of the PCBs and avoids discarding non-defective thin-laminate panels due to false failures. Further, there is a need for methods for finishing edges of thin-laminate panels in a manner that does not cause smearing of conductive material along the edges of the dielectric layers and apparatus for performing the same. Summary of the Invention In light of the deficiencies of the prior art, the present invention provides "finished" thin-laminate panels having dielectric layers of about 0.006 inches (0.15 mm) or less. Thin conductive layers (e.g., copper) are laminated on either side of the dielectric layers and the edges of the dielectric layers of the thin-laminate panels are finished to be free of conductive material. As discussed above, the thin-laminate panels are designed to provide necessary capacitance for all or a substantial number of integrated circuits to be mounted on or formed on a PCB made from one or more of the panels. The finished thin-laminate panels of the present invention may be tested for manufacturing defects, such as short circuits, before further processing of the panels to produce PCBs. Further, such testing may be done without the risk of false failures resulting in discarding of non-defective panels, because the edges of the dielectric layers of the panels of the present invention are free of conductive material. The present invention further provides "finishing" methods for removing conductive material from the edges of the unfinished thin-laminate panels in a manner that does not cause further smearing of the conductive material onto the dielectric layer. Preferably a CNC router having a vertically mounted router bit is used. To assure that conductive material from the conductive layers of an unfinished thin-laminate panel is not smeared onto the edges of the dielectric layer as a portion of the edge of the panel is removed, the rotation of the router bit is made to coincide with the plane defined by the surface of the panel. Additionally, the router bit has cutting edges that extend axially rather than spirally or helically, so that the cutting action is in the direction of the router bit rotation. Further, the router bit is not moved vertically relative to the plane of the panel at any point during the shearing process. The present invention further provides securing apparatus or fixtures for securing one or more unfinished thin-laminate panels to a surface for removal of conductive material from the dielectric layer edges. The thin-laminate panels are mounted in the securing apparatus to shear the edges of the panels and produce the finished thin-laminate panels of the present invention. Such securing apparatus of the present invention allows the panels to be secured to a surface during the shearing process without the need to drill holes through or otherwise diminish useful portions of the panels. The foregoing and other objects, features, and advantages of the invention will become more apparent from the following detailed description of preferred embodiments which proceed with reference to the accompanying drawings. Brief Description of the Drawings Fig. 1 (a) is a side view of a prior art thin-laminate panel. Fig. 1(b) is a side view of another prior art thin-laminate panel. Fig. 2 is a perspective view of a preferred embodiment of the finished thin-laminate panel of the present invention. Fig. 3 is a perspective view of a first embodiment of the thin-laminate panel securing apparatus of the present invention. Fig. 4 is a perspective view of a second embodiment of the thin-laminate panel securing apparatus of the present invention. Fig. 5 is an oblique view that illustrates the vertical orientation of a router relative to a stack of thin-laminate panels, used to practice the method of the present invention. Fig. 6 is a partial plan view of blades of a router bit used to practice the method of the present invention. Fig. 7(a) and 7(b) are side sectional views of third and fourth embodiments of a finished thin-laminate panel of the present invention Description of the Invention The present invention provides "finished" thin-laminate panels. The thin-laminate panels include dielectric layers having thickness of about 0.006 inches (0.15 mm) or less and, preferably about 0.002 inches (0.05 mm) or less. The dielectric layers have conductive layers on either side thereof. The edges of the dielectric layers of the finished thin-laminate panels are free of conductive material. As used herein, the term "finished" refers to the mechanical or abrasive removal of a portion of one or more edges of a thin-laminate panel or the mechanical, chemical, or abrasive removal of conductive maternal from one or more edges of the dielectric layer of a thin-laminate panel, such that the edges of the dielectric layer of the finished thin-laminate panel are free of conductive material. More specifically, referring to Fig. 2, the thin-laminate panel 2 of the present invention preferably includes two sheets or layers 6 of conductive material and an intermediate sheet or layer 8 of dielectric material. The conductive layers 6 and dielectric layer 8 are joined together such as by lamination, to form a structurally firm assembly to form the thin-laminate panel 2. The thin-laminate panel 2 is sufficiently firm to facilitate manufacture of the panel, preferably by lamination of separate layers and also to facilitate the manufacture of capacitive printed-circuit boards therefrom. The structurally firm assembly of the thin-laminate panel 2 may be substantially rigid, flexible, or resilient depending upon the intended end use of the panel. Although only a single thin-laminate panel is shown in Fig. 2, one or more of the thin-laminate panels may be used as the internal components of a PCB. As discussed above, the thin-laminate panel 2 is designed to provide necessary capacitance for all or a substantial number of integrated circuits 14 to be mounted on or formed on a capacitive PCB made of the thin-laminate panel(s). In general, the materials chosen to form the conductive layers 6 and the dielectric layer 8 and the thickness of the individual layers, are chosen according to state-of-the-art technology. Particularly, to provide the necessary level of capacitance, the dielectric layer 8 of the thin-laminate panel 2 has carefully controlled values of thickness. Further, materials suitable to form the dielectric layer 8 are chosen to have dielectric constants sufficient to satisfy the capacitance requirements. The dielectric materials may comprise any suitable capacitive material as known to those persons skilled in the art. The choice of dielectric material in part depends upon the extent of flexibility or rigidity desired for the resulting thin-laminate panel. For example, the dielectric material may comprise a plastic film, such as acrylics or polyimides, e.g., KAPTON® available from DuPont. The dielectric materials may alternatively comprise a reinforcement impregnated with a resin. The dielectric material reinforcement is preferably chosen from the group consisting of woven or non-woven fiberglass, quartz, cellulose, paper, aromatic polyamide fibers, (such as KEVLAR® or THERMOUNT® - both available from DuPont), and mixtures thereof. The resin is preferably chosen from the group consisting of thermoplastic resins, thermoset resins, and mixtures thereof. For the present invention, the dielectric layer has a thickness of from about 0.0005 inches (0.012 mm) to about 0.01 inches (0.25 mm) , and preferably from about 0.001 inches (0.025 mm) to about 0.006 inches (0.15 mm). A dielectric layer having a thickness of about 0.002 inches (0.51 mm) has been found to be especially useful. The conductive layer 6 is provided with sufficient conductive material, either in terms of mass per unit area or in terms of thickness, to permit adequate current flow necessary to provide each integrated circuit formed on the PCB with sufficient capacitance for its proper operation. The conductive material is preferably formed from any of a variety of conductive material, such as conductive metals and conductive inks. Preferably, the conductive material comprises a conductive metal, such as aluminum, silver, gold, copper, and mixtures thereof. For the present invention, the conductive layers are most preferably formed of copper because of its superior conductive characteristics compared to all other non-precious metals. The conductive layers 6 preferably have a thickness of from about 0.0001 inches (0.0025 mm) to about 0.01 inches (0.025), and more preferably about 0.0014 inches (i.e., about 0.036 mm). The distance between the conductive layers 6, throughout the conductive layers and at the edges of the panel, is precisely controlled by controlling the thickness of the dielectric layer 8 and the conductive layers 6. The thin-laminate panels of the present invention further include an "edge finish" wherein the edges of the dielectric layers have been mechanically, abrasively, or chemically treated to be free of conductive material. The absence of conductive material on any portion of the edges of the dielectric layer 8 allows the thin-laminate panel to be tested for electrical conductance, such as by high-potential testing (described below), to determine the presence or absence of conductive impurities within the dielectric layer 8 or to detect other electrical defects within the thin-laminate panel, without the loss of discarded panels due to false failures. Further, the interfaces between the dielectric layer 8 and each of the conductive layers 6, are distinct to control the thickness between the conductive layers 6. The thin-laminate panel 2 of the present invention may be tested for electrical defects, such as the presence of conductive impunities within the dielectric layer 8, by use of standard tests for electrical conductance as known to those persons skilled in the art. For example, a high-potential (high-voltage) test may be performed using a megohm meter (e.g., a Hipotronics HMA3A Megohm Meter). A relatively high voltage is applied to the conductive layer 6 on a first surface 16 of the thin-laminate panel 2. Any corresponding voltage at the conductive layer 6 on a second surface 20 of the panel 2 is then detected. A defective thin-laminate panel will conduct current from the first surface 16 of the pane to the second surface 20. As discussed above, if the thin-laminate panel 2 has conductive material on the edges 12 of the dielectric layer 8, as does the prior art thin-laminate panels, such a test for electrical defects in the panel could not be performed to accurately determine whether the panel is defective. The present invention also provides methods for finishing the edges of thin-laminate panels to produce the thin-laminate panels of the present invention. A preferred method of the present invention provides a process for removing relatively small edge portions of an unfinished thin-laminate panel. The finishing method removes any conductive material present on one or more edges of the dielectric layer 8. Additionally, the finishing method is performed in a manner that does not cause further smearing of conductive material from the conductive layers 6 of the panel onto one or more edges 12 of the dielectric layer 8. First, relatively large sheets (not shown) of thin-laminate are made according to state-of-the-art technology, e.g., according to the methods disclosed in U.S. Pat. No. 5,079.069 issued Jan. 7, 1992 to Howard et al., U.S. Pat. No. 5,155,655 issued Oct. 13, 1992 to Howard et al., U.S. Pat. No. 5,161,086 issued Nov. 3, 1992 to Howard et al., and U.S. Pat. No. 5,261,153 issued November 16, 1993 to Lucas, all of which are incorporated herein by reference. The large thin-laminate sheets are then cut into multiple (unfinished) thin-laminate panels. As discussed above, as the panels are cut from the large laminate sheets, conductive material is typically smeared from one or more of the conductive layers of the thin-laminate sheet onto the dielectric layer edge. The smeared conductive material forms a thin region of conductive material 6a on one or more edges 12 of the dielectric layer 8 of the thin-laminate panel (e.g., see prior art Figs. 1 (a) and 1(b)). A preferred finishing method of the present invention provides a process for milling or abrading a small portion of the panel edges to remove conductive material from the edges 12 of the dielectric layer 8 of the unfinished panel. Referring to Fig. 4, one or more thin-laminate panels may be finished at one time. In finishing the edges, a single thin-laminate panel 2 or a stack 32 of thin-laminate panels, is held in place using a securing apparatus 24. The securing apparatus 24 may comprise a pair of metal plates 28 connected to a supporting surface 26. The stack 32 of unfinished thin-laminate panels is placed between the pair of metal plates 28 and the underlying table or supporting surface 26. The metal plates 28 are preferably bolted to the supporting surface 26 at one or both ends so that the stack 32 of unfinished panels is held securely between the metal plates 28 and the supporting surface 26 without the need to tool holes in the panels. Alternatively, referring to Fig. 3, the securing apparatus 24 of the present invention may comprise a lower backer board 36a used in conjunction with an upper backer board 36b. The lower backer board 36a is comprised of a material or has a surface that has sufficient friction such that an unfinished thin-laminate panel placed directly on the lower backer board 36a is held securely in place with the aid of the upper backer board 36b, as the edges of the panels are sheared. The lower backer board 36a preferably comprises a relatively thin sheet of a material that is sufficiently pliant that it does not damage the conductive layer 6 of the thin-laminate panel 2. For example, the lower-backer board 36a may comprise a closed-cell foam (e.g., NEOPRENE® available from Denka Chemical Corporation of Houston, Texas). The upper backer board 36b acts as a weight placed on the top of the stack 32 of panels to help hold the stack in place as the panels are treated. The upper backer board 36b preferably is of a sufficient weight to securely hold the stack 32 of panels in place without causing damage to the panels. The upper backer board 36b is sized smaller in area relative to the area of the unfinished thin-laminate panels so that the edges of each panel may be finished (as described below) without interference with the upper backer board 36b. The upper backer board 36b preferably comprises a one inch (25.4 mm) steel plate (e.g., weighing about 30 lbs (13.6 Kg)). In an alternative embodiment, a protective layer 38, preferably comprising a composition hardboard such as MASONITE®, is positioned between the stack 32 of panels and the upper backer board 36b. The protective layer 38 protects the conductive layer 6 of the uppermost panel in the stack from being damaged by the upper backer board 36b. The protective layer 38 is preferably of a size that the upper backer board does not directly contact the stack 32. In operation, the lower backer board 36a is placed on the supporting surface 26. A stack 32 of unfinished thin-laminate panels is then placed on the lower backer board 36a. The protective layer 38 and the upper backer board 36b are then placed on top of the stack 32 in a manner such that the edges of the panels may be finished without interference with the upper backer board or the protective layer. It is noted that other securing apparatus may be used to perform the methods of the present invention. For example, the securing apparatus may comprise attachment of one or more unfinished thin-laminate panels to a surface by use of clamps, straps, various weights, suction devices (i.e., vacuum), adhesives, magnets, etc. Referring to Fig. 5, preferably, a standard computer numerical control (CNC) router 40 is used to finish the thin-laminate panels. A router bit 44 is oriented vertically as shown. In Fig. 5, the Z-axis is parallel to the vertically oriented router bit, the X-axis extends in a direction horizontal with the plane of the page, and the Y-axis extends in a direction perpendicular to the plane of the page. The CNC router 40 is operable to move the router bit 44 in both the X-axis and the Y-axis directions. The router bit 44 is moved along the edge portions of the stack 32 to cut, mill, or abrade off a relatively small portion of each edge of each of the panels in the stack (e.g., typically about 0.125 inches (3.18 mm) to about 0.250 inches (6.35 mm) of the panel edges are removed). To assure that conductive material from the conductive layers 6 of the unfinished thin-laminate panels is not smeared onto the edges 12 of the dielectric layers 8 as the stack 32 of panels is trimmed, the axis of rotation of the routed bit 44 is perpendicular to the plane defined by the surface 48 of the stack 32 of panels. To further assure "clean" dielectric layer edges, the router bit 44 has cutting edges or blades that extend axially, rather than helically or spirally (Fig. 6). In other words, the router bit 44 has cutting surfaces that extend only in the X, Y plane. Accordingly, the cutting action of the router bit is in the direction of the router bit rotation R only. Additionally, referring back to Fig. 5, the router bit 44 is not moved along the Z-axis at any point during the finishing of the edges of the panels. A preferred router bit 44 for performing the method of the present invention is a 1/8 inch (3.18 mm) router bit, such as Router Part No. RI1250, available from Megatool of Buena Park, California. When a stack 32 of unfinished thin-laminate panels is mounted in the securing apparatus 24 illustrated in Fig. 4, a pair of opposing edges (A and B) of the stack 32 of panels is first finished by moving the router bit 44 along the Y-axis on both sides of the stack. The stack 32 of partially finished panels is then WO 00/22895 . \ . PCT/JP99/05626 removed from the securing apparatus 24, rotated 90° and secured again. The two remaining edges of the stack of panels are then finished in the same manner. When a stack 32 of unfinished thin-laminate panels is mounted in the securing apparatus 24 illustrated in Fig. 3, all four edges of the stack may be finished or sheared (i.e., milled, cut, or abraded) without the need to remove and rotate the stack of panels as is required with the securing apparatus shown in Fig. 4. Other preferred finishing methods of the present invention for removal of conductive material from the dielectric layer edges employ tools such as water-jet cutting apparatus, laser cutting apparatus, beveling apparatus, and filing, sanding, or milling apparatus, etc., or use chemical etching, rather than use of a router as described above. In a second embodiment of the thin-laminate panel 2 (shown in Fig. 7(a)), as with the first embodiment shown in Fig. 2, conductive material is removed from the edges of the dielectric layer 6. In addition, a small end portion of one or more of the conductive layers 6 is removed from the end portions 40 of the dielectric layer 8. In a third embodiment of the thin-laminate panel 2 (shown in Fig. 7(b)), conductive material is removed from the edges of the dielectric layer 8 by removing one or more corner portions of both the conductive layer 6 and the dielectric layer 8. The third embodiment of the thin-laminate panel 2 may be "finished" by removing one or both of the corner portions of the conductive layers 6 and the dielectric layer 8, using a router bit designed to cut at approximately a 45° angle relative to the plane defined by the surface of the panel. The router bit may include spiral cutting edges positioned to pull material from the dielectric layer 8 to the conductive layer 6 rather than pulling conductive material from the conductive layers 6 to the edges of the dielectric layer 8. Whereas the invention has been described with reference to several embodiments, it will be understood that the invention is not limited to those embodiments. On the contrary, the invention is intended to encompass all modifications, alternatives, and equivalents as may be included within the spirit and scope of the invention as defined by the appended claims.

Claims: WO 00/22895 . jg - PCT/JP99/05626 CLAIMS: 1. A thin-laminate panel for making capacitive printed-circuit boards, the thin-laminate panel comprising: a dielectric layer having a first surface and a second surface; a first conductive layer joined to the first surface of the dialectic layer; and a second conductive layer joined to the second surface of the dielectric layer such that the first and second conductive layers and the dielectric layer together form a structurally firm assembly, wherein the dielectric layer includes finished edges that are substantially free of conductive material. 2. The thin-laminate panel of claim 1, wherein the dielectric layer has a thickness of from about 0.0005 inches (0.018 mm) to about 0.01 inches (0.25 mm). 3. The thin-laminate panel of claim 1, wherein the dielectric layer has a thickness of from about 0.001 inches (0.025 mm) to about 0.006 inches (0.15 mm). 4. The thin-laminate panel of claim 1, wherein the dielectric layer has a thickness of about 0.002 inches (0.51 mm). 5. The thin-laminate panel of claim 1, wherein the first conductive layer is laminated to the first surface of the dielectric layer. 6. The thin-laminate panel of claim 1, wherein the dielectric material is selected from a group consisting of resin impregnated fiberglass cloth, acrylics, polyimides, aromatic polyamides, and mixtures thereof. 7. The thin-laminate panel of claim 1, wherein the conductive material comprises a conductive metal. 8. The thin-laminate panel of claim 1, wherein the conductive layer is made of conductive material chosen from the group consisting of aluminum, silver, gold, copper, and mixtures thereof. 9. The thin-laminate panel of claim 1, wherein the finished edges of the dielectric layer are substantially perpendicular relative to planes defined by the first and second surfaces of the dielectric layer. 10. The thin-laminate panel of claim 1, wherein the finished edges of the dielectric layer further comprise finished edges wherein portions of the edges have been removed such that the remaining edges of the dielectric layer are substantiality free of conductive material. 11. The thin-laminate panel of claim 1 , wherein the finished edges of the dielectric layer further comprise finished edges wherein portions of the edges have been routed such that the remaining edges of the dielectric layer are substantially free of conductive material. 12. A thin-laminate panel for making capacitive printed-circuit boards, the thin-laminate panel comprising: a conductive layer formed of a conductive material; and a first surface of a dielectric layer joined to a first surface of the conductive layer, the dielectric layer having a thickness of from about 0.0005 inches (0.18 mm) to about 0.01 inches (0.25 mm), wherein the dielectric layer includes finished edges that are free of conductive material. 13. A thin-laminate panel for making capacitive printed-circuit boards, the thin-laminate panel comprising: a dielectric layer having a first surface and a second surface; a first conductive layer joined to the first surface of the dielectric layer; and a second conductive layer joined to the second surface of the dielectric layer such that the first and second conductive layers and the dielectric layer together form a structurally firm assembly, wherein the structurally firm assembly has edges that have been finished with a cutting motion that took place only in a plane defined by the first and second surfaces of the dielectric layer so that edges of the dielectric layer are free of conductive material. 14. A finishing method for producing a thin-laminate panel for making capacitive printed-circuit boards, the finishing method comprising: providing a thin dielectric layer having a first surface and a second surface; joining a first conductive layer to the first surface of the dielectric layer; joining a second conductive layer to the second surface of the dielectric layer to form a structurally firm assembly; and removing a relatively small portion from one or more edges of the structurally firm assembly such that edges of the dielectric layer are free of conductive material. 15. The method of claim 14, wherein removing a relatively small portion from one or more edges of the structurally firm assembly is performed in a manner such that conductive material from the first conductive layer or from the second conductive layer does not extend to any edge of the dielectric layer. 16. The method of claim 14, wherein one or more edges of the structurally firm assembly are routed to remove a relatively small portion from one or more edges thereof. 17. The method of claim i6, wherein one or more edges are routed with a router bit that rotates only in the plane defined by the first and second surfaces of the dielectric layer so that edges of the dielectric layer are free of conductive material. 18. The method of claim 14, further including: placing a weight on the structurally firm assembly to secure the structurally firm assembly in a single position for the removing of a relatively small portion from one or more edges thereof. 19. The method of claim 14, further including: placing the structurally firm assembly between a supporting surface and a plate; and connecting a first end or a second end of the plate to the supporting surface such that the structurally firm assembly is secured for the removing of a relatively small portion from one or more edges thereof.

Inventors: FILLION ARTHUR J, KOGAMI OSAMU, KURATA KANJI, MURRAY JEFFREY A, SMITH TERRENCE A, FILLION, ARTHUR, J., KOGAMI, OSAMU, KURATA, KANJI, MURRAY, JEFFREY, A., SMITH, TERRENCE, A.
Applicants: MATSUSHITA ELECTRIC WORKS LTD, MATSUSHITA ELECTRIC WORKS, LTD.
Application year: 1999
Main classification: H05K1
IPC codes: H05K1, H05K3