PROCESS FOR REMOVING IONIZABLE SPECIES FROM CATALYST SURFACE TO IMPROVE CATALYTIC PROPERTIES

Abstract: This invention relates to a process for the preparation of a catalyst having improved properties, said process comprising selecting a carrier, lowering the concentration of ionizable species present on the surface of the carrier, and depositing a catalytically effective amount of one or more catalytically reactive metals on the carrier. The invention further relates to catalysts made from the process and to the use of such catalysts in alkene epoxidation processes. In the examples the lowering of the concentration of ionizable species is obtained by washing the alpha alumina carrier with boiling water. Then the dried carrier is impregnated with a promotor and silver.

Description: PROCESS FOR REMOVING IONIZABLE SPECIES FROM CATALYST SURFACE TO IMPROVE CATALYTIC PROPERTIES Field of the Invention __ The invention relates to a process for the preparation of catalyst with improved catalytic properties . Background of the Invention The presence of certain species contained m the carriers of catalysts can be detrimental to the catalytic metal deposition tnereon and/or catalyst performance and t is commoni believed that the concentration of these detrimental species must be controlled throughout the bulk of carrier. One way of controlling the amount of impurities through the bulk, although expensive, is by the use of purer raw materials. For example, US Patent No. 4,79^,270 discloses water washing to reduce the sodium content of an alumina powder. The pH of the wash water may need to be adjusted for extraction of other metals and Japanese patent JP56164013 discloses the use of a low pH 'acid) to extract uranium and thorium from a calcined α-aumina raw material. Several procedures in the art teach that washing after deposition of the catalytic metal .S helpful. US Patent Nos . 4,361,504 and 4,366,092 suggest that ethylene oxide catalyst be water washed after the deposition of silver or silver/gold on the carrier. EP-A 211521 discloses washing of a catalyst with hot water to remove basic materials left on the catalyst from a silver impregnation process or the physical depositn .on of alkali metals. US Patent No. 4,367,167 discloses a process for preparing a supported catalyst wherein an impregnated support is immersed in an inert water immiscible organic solvent containing a dissolved aliphatic amine . US Patent No. 4,810,689 discloses depositing a silver compound, decomposing the silver compound to silver in the presence of an alkali metal_ compound, removing organic deposits by washing and introducing fresh alkali metal by impregnation during or after the washing stage. U.S. Patent Nos . 4,186,106 and 4,125,480 disclose washing with an inert liquid after deposition of the catalytic metal and before deposition of a promoter material. U.S. Patent No. 4,908,3^3 teacnes that _t mav be desirable to remove cations whicn are exchangeable witn the alkali and alkaline earth metals contained m the impregnating solution, to allow for ease of repeatability m the use and reuse of the impregnating solution. No methods are taught for such removal; however, it is commonly known in the art that acids are highly effective cation removal solutions . The prior art remains concerned with the total amount of impurities; i.e., impurities throughout the bulk. Unfortunately, the impurity removal techniques taught typically attack the carrier itself. It has now been found that the metal deposition and/or catalytic properties of a catalyst may be greatly improved by controlling the purity of the surface of the carrier rather than the purity of the carrier bulk, such that the total amounts of impurities may actually be high as long as the surface amounts of impurities are maintained at a low level. Summary of the Invention According to one embodiment of the invention, there is provided a process for improving the properties of a carrier for a catalyst oy a treatment, which treatment is oerformed on one or more of the materials from which the carrier is formed and/or on the complete carrier and which treatment is effective m lowering the concentration of one or more ionizable species present on the surface of tne complete carrier, the lowering being expressed as the lowering of the relative concentration of Na and/or Si atoms, as measured by X-ray Photoelectron Spectroscopy (XPS) performed on the untreated and treated carrier . Preferably the concentration, as measured oy XPS, of Na on the surface of the carrier is lowered by at least 5 percent and/or the Si concentration is lowered by at least 5 percent. More preferaoly the concentration of Na is lowered by at least 40% and/or the concentration of S is lowered by at least 10%. Optionally the concentration lowering treatment is followed by a drying step. There is further provided a process for preparing a catalyst, especially an olefin epoxidation catalyst, by depositing a catalytically effective amount of one or more catalytically reactive metals and optionally one or more promoter materials on a carrier prepared by a process as defined above. There is yet further provided a for tne vapor phase catalytic epoxioation of an alkene with an oxygen containing gas, using a catalyst prepared by a process as defined above. Description of the Preferred Embodiments It has been found that carriers which have been treated to reduce certain undesirable ionizable species, particularly anionic species, which are present on the surface of the carrier provide catalysts with improved catalytic properties, when compared with the performance of catalysts maoe from carriers which have not been so treated. The process is believed to work to improve the properties of most catalysts, no matter how impure the bulk carrier material, compared to a catalyst made with an untreated carrier. Further, the process will work for organic or inorganic carriers . The process is effective in improving at least one the catalytic properties of a catalyst wherein a _ catalytically reactive metal is deposited or impregnated upon a carrier whicn contains ionizable species on its surface. "Improvement in catalytic properties" as used herein means the properties of the catalyst are improved as compared to a catalyst made from the same carrier which has not been treated to lower surface ionizable species. Catalytic properties include catalyst activity, selectivity, activity and/or selectivity performance over time, operability (resistance to runaway), conversion and work rate. The process requires that the concentration of undesirable ionizable species present on the surface of the carrier be reduced. As used herein, tne "surface" of the carrier is that area of the carrier wnicn may be measured by the standard method of Brunauer, Emmett and Teller (BET) . Specifically, the surface of the carrier _s the site at wnich reaction taKes place. An "ionizable" species is a species wnicn is capable of being rendered ionic, where the term "ionic" or "ion" refers to an electrically cnarged chemical moiety. The solubilization rate of silicates may be measured by inductively coupled plasma (ICP) tecnniques and the amount of sodium and silicon species on a surface may De measured by x-ray photoelectron spectroscopy (XPS). In defining the present invention the amounts of sodium and/or silicon, present on tne surface of the carrier, as measured by XPS, oefore ano after treatment according to tne invention, nave been chosen as an indicator for the amounts of ionizable soecies. Anotner measurement technique is to measure the cnange in electrical conductivity of the treatment solution. Carriers are commonly inorganic materials sucn as, for example, alumina-, silica-, or titania-based compounds, or combinations thereof, such as alumina- _ silica carriers. Carriers may also be made from carbon- based materials such as, for example, charcoal, activated carbon, or fullerenes. Ionizable species typically present on the inorganic type carriers include sodium, potassium, alummates, soluble silicate, calcium, magnesium, alummosilicate , oesium, _ιthιum, ano combinations thereof. Of particular concern are the lonizaPle anionic species present on the surface, particularly lonizaole silicates. Lowering the undesirable ionizable species concentration may be accomplished by any means (i) which is effective in rendering the ionizable species ionic and removing that species, or (n) which renders the ionizable species insoluble, or (in) which renders the ionizable species immobile; however, use of aggressive media is discouraged as these media tend to dissolve the carrier, extract too mucn material from the oulk, and generate acidic or Dasic sites i" the pores. Aciαs, oesioes being aggressive media, will remove the cations on a carrier but are fairly ineffectual in removing the undesira le anions, such as silicates. Effective means of lowering concentration include washing tne carrier; ion exchange; volatilizing, precipitating, or sequestering the impurities; causing a reaction to make the ionizable species on tne surface insoluble; and combinations thereof. Examples of wasn and ion exchange solutions include aqueous and/or organic solvent-based solutions which may also contain tetraethylammonium hydroxide, ammonium acetate, lithium caroonate, barium acetate, strontium acetate, crown ether, metnano , ethanol, dimethylformamide, and mixtures thereof. The termed carrier may oe treated, or the materials used to form the carrier may oe treated before the carrier is manufactured. When tne carrier materials are treated before the carrier is formed, still further improvement may be seen by also treating the surface of the formed carrier. The carrier may be dried following tne lomzaole species reduction treatment. To make a catalyst from the carrier, the carrier is typically impregnated witn metal compound(s), complex(es) ano/or salt (s dissolved m a suitaole solvent sufficient to deposit or impregnate a catalytically effective amount of metal on tne carrier. As used herein, "catalytically effective amount" means an amount of metal that provides a measurable catalytic effect. For example, a catalytically effective amount of metal wnen referring to an olefm epoxidation catalyst is that amount of metal which provides a measurable conversion of olefm and oxygen to alkylene oxide. Further improvement in the catalyst properties are seen when tne metal deposition is effected by contacting tne carrier with an impregnation solution whose hydrogen ion activity has been lowered. "Hydrogen ion activity" as used herein is the hydrogen ion activity as measured by the potential of a hydrogen ion selective electrode. As used herein, a solution with "lowered" hydrogen ion activity refers to a solution whose nydrogen activity has oeen altered by the addition of a base, sucn tnat the hydrogen ion activity of tne altered solution is lowered compared to the hydrogen ion activity of the same solution in an unaltered state. The base selected to alter the solution may be cnosen from any base or compound with a pKb lower than the original impregnation solution. It s particularly desirable to choose a base which does not alter the formulation of the impregnation solution; i.e., wnich does not alter the desired metals concentration present in the impregnation solution and deposited on the carrier. Organic bases will not alter the impregnation solution metals concentrations, examples of which are tetraalkylammonium hydroxides and 1,8-bιs- (dimethylamino) -naphthalene . If changing the metals concentration of the impregnation solution is not a concern, metal hydroxides may be used. When the impregnation solution is at least partially aqueous, an indication of the change m the hydrogen activity may be measured with a pH meter, with the understanding that the measurement obtained is not pH by a true, aqueous definition. '"Measured pH" ' as used herein shall mean such a non-aqueous system pH measurement using a standard pH probe. Even small changes in the "measured pH" from the initial impregnation solution to that with added base are effective and improvements in catalytic properties continue as the "measured pH" change increases with base addition. High base additions do not seem to adversely affect catalyst performance; however, high additions of hydroxides have been seen to cause sludging of the impregnation solution, creating manufacturing difficulties. When the base addition is too low, the hydrogen ion activity will not be affected. The hydrogen ion activity lowering procedure is also quite effective when used by itself; i.e., when no ionizable species concentrations are lowered prior to impregnation. The impregnated carrier, also known as a catalyst precursor, can oe dried in the presence of an atmosphere which also reduces the catalytic metal. Drying methods known in the art include steam drying, drying in an atmosphere with a controlled oxygen concentration, drying in a reducing atmosphere, air drying, and staged drying using a suitable ramped or staged temperature curve. By way of example, the process will be described in more detail for a catalyst suitable for the vapor phase production of epoxides, also known as an epoxidation — catalyst . First, a carrier is selected. In the case of an epoxidation catalyst the carrier is typically an inorganic material, such as for example, an alumina-based carrier such as α-alumina . In the case of α-alumina-contaming carriers, preference is given to those having a specific surface area as measured by the B.E.T. method of from 0.03 to 10 m 2 /g, preferably from 0.05 to about 5 m 2 /g, more preferably from 0.1 to 3 m 2 /g, and a water pore volume as measured by conventional water absorption techniques of from 0.1 to 0.75 ml/g by volume. The B.E.T. method for determining specific surface area is described in detail in Brunauer, S., Emmett, P. Y. and Teller, E., J. Am. Chem. Soc, 60, 309-16 (1938). Certain types of α-alumina containing carriers are particularly preferred. These α-alumma carriers have relatively uniform pore diameters and are more fully characterized by having B.E.T. specific surface areas of from 0.1 to about 3 m 2 /g, preferably from 0.1 to about 2 m 2 /g, and water pore volumes of from 0.10 ml/g to about 0.55 ml/g. Manufacturers of such carriers include Norton Chemical Process Products Corporation and United Catalysts, Inc. (UCI) . The concentration of undesirable ionizable species present on the surface of tne carrier are reduced to create a "cleansed" carrier. Or, alternatively, the concentration of ionizable species in the materials used to make the carrier may oe reduced prior to formation of tne carrier. If the carrier raw materials are treated, the formed carrier may be retreated for further improvement . Ionizable species present on an a-alumma carrier, for example, typically include sodium, potassium, __ aluminates, soluble silicates, calcium, magnesium, alummosilicates , and combinations thereof. It has been found that silicates, and certain other anions, are particularly undesirable ionizable species in an epoxidation catalyst. After the concentration of tne surface ionizable species are lowered, the carrier is optionally cried. When aqueous or organic solvent washing is used, drying or some similar method is recommended to displace the wash solution from the carrier pores. The carrier is now ready for a catalytically reactive metal to be deposited or impregnated thereon. The carrier having the controlled solubilization rate is impregnated with metal ions or compound (s), complex (es) and/or salt(s) dissolved in a suitable solvent sufficient to cause the desired deposition on the carrier. When silver is the deposition material, a typical deposition is from 1 to 40 wt%, preferably from 1 to 30 wt% of silver, basis the weight of the total catalyst. The impregnated carrier is subsequently separated from the solution and the deposited metal (s) compound is reduced to metallic silver. One or more promoters may be deposited either prior to, comcidentally with, or subsequent to the deposition of the metal. Promoters for epoxidation catalysts are typically selected from sulfur, pnosphorus, ooron, fluorine, Group IA through Group VIII metals, rare earth metals, and combinations thereof. The promoter material is typically compound(s) and/or salt's) of the promoter dissolved in a suitable solvent. For olefin epoxidation oxide catalysts, Group 1A metals are typically selected from potassium, rubidium, cesium, lithium, sodium, and combinations thereof; with, potassium and/or cesium and/or rubidium being preferred. Even more preferred is a combination of cesium plus at least one additional Group IA metal, such as cesium plus potassium, cesium plus rubidium, or cesium plus lithium. Group IIA metals are typically selected from magnesium, calcium, strontium, barium, and combinations thereof, Group VIII transition metals are typically selected from cobalt, .ron, nicke , ruthenium, rhodium, palladium, and combinations tnereof; and rare earth metals are typically selected from lanthanum, cerium, neodymium, samarium, gadolinium, dysprosium, erbium, ytterbium, and mixtures thereof. Non-limiting examples of other promoters include perrnenate, sulfate, molybdate, tungstate, chromate, phosphate, borate, sulfate anion, fluoride anoin, oxyanions of Group IIIB to VIB, oxyanions of an element selected from Groups III through VIIB, alkali (net metal salts with anions of halides, and oxyanions selected from Groups IIIA to VIIA and IIIB through VIIB. The amount of Group IA metal promoter is typically in the range of from 10 ppm to 1500 ppm, expressed as the metal, by weight of the total catalyst, and the Group Vllb metal is less than 3600 ppm, expressed as the metal, by weight of the total catalyst. For further improvement in catalytic properties, the nydrogen ion activity of the impregnation solution is optionally lowered, such as by the addition of a base. The typical impregnation solution for an epoxidation catalyst begins quite oasic, so a strong base is used to further lower the hydrogen ion activity. Examples of stronq bases include, alkyl ammonium nydroxides such as tetraethylammonium hydroxide, lithium hydroxide and cesium hydroxide. In order to maintain the desired impregnation solution formulation and metal loading, a organic base is preferred. Base additions in these systems typically result m a "measured pH" change _ ranging up to about 2, realising that the "measured pH" is not a true pH since the impregnation system is not aqueous . If an excess of impregnation solution is used, the impregnated carrier is subsequently separated from the solution before the deposited metal compound is reduced. Promoters, components which work effectively to provide an improvement m one or more of the catalytic properties of the catalyst when compared to a catalyst not containing such components, may also be deposited on the carrier either prior to, comcidentally with, or subsequent to the deposition of the catalytically reactive metal. The resulting epoxidation catalysts just described are used for the vapor phase production of epoxides, such as in the production of ethylene oxide from ethylene and an oxygen containing gas. In this epoxidation process on or more nitrogen oxides 'NO may also oe added to the feedstock to boost catalyst conversion performance. Other embodiments of the invention provide catalysts made by the processes just described. Having generally described the invention, a further understanding may be obtained by reference to the following examples. Examples Carriers Table I shows the carriers used for the Examples TABLE I a Method of Brunauer, Emmett and Teller, loc. cit. b Flat Plate Crush Strength, single pellet. c Determined by mercury intrusion to 3.8 x 10 8 Pa using Micromeritics Autopore 9200 or 9210 (130° contact angle, 0.473 N/m surface tension of Hα) . - .3 - Carrier Water-Washinσ Procedures for Examples 1, 2, 3, 4, 5, 7, 8, 10, 11, 13 Carrier wasning was carried out by immersing 100 grams of carrier in 300 grams of boiling de-ionized water for 15 minutes. The carrier was tnen removed and placed in a fresh 300 grams of ooilmg water for another 15 minutes. This procedure was repeated once more for a total of three immersions, at which point the carrier was separated from the water and dried m a well ventilated oven at 150 °C for 18 hours. The dried carrier was then used for preparation of a catalyst by the procedures outlined in the following Examples. Impregnation Solution A silver-amme-oxalate stock solution was prepared by the following procedure: 415 g of reagent-grade sodium hydroxide were dissolved in 2340 ml de-ionized water and the temperature was adjusted to 50 °C. 1699 g high purity " Spectropure" silver nitrate were dissolved in 2100 ml de-ionized water and the temperature was adjusted to 50 °C. The sodium hydroxide solution was added slowly to the silver nitrate solution, with stirring, while maintaining a solution temperature of 50 °C. The mixture was stirred for 15 minutes, then the temperature was lowered to 40 °C. Water was removed from the precipitate created in the mixing step and the conductivity of the water, which contained sodium and nitrate ions, was measured. An amount of fresh deionized water equal to the amount removed was added back to the silver solution. The solution was stirred for 15 minutes at 40 °C. The process was repeated until the conductivity of the water removed was less than 90 μmho/cm. 1500 ml fresh deionized water was then aoded. 630 g of high-purity oxalic acid dihydrate were added in approximately 100 g increments. The temperature was keep at 40 °C and the pH was kept above 7.8. Water was removed from the mixture to leave a highly concentrated silver-containing slurry. The silver __ oxalate slurry was cooled to 30 °C. 699 g of 92 %w ethylenediamme (8% de-ionized water) was added while maintaining a temperature no greater than 30 °C. The resulting solution contained approximately 27-33 %w silver. Enough 45 %w aqueous CsOh and water was added to this solution to give a finished catalyst having 1-..5 %w silver and a desired cesium loading (see Examples) . Sodium and Silicate Measurement Procedures The XPS analayses were performed in a VG ESCALAB mkll X-ray photoelectron spectrometer. Non-monochromatized Al Kα (1484.6 eV) X-rays were used as the excitation source. The electron kinetic energy analyzer was a 150 degree spherical sector analyzer equipped with a three channeltron detection system. All spectra were obtained in the constant analyzer pass energy mode with the pass energy set at 50 eV. Prior to analysis, samples were lightly crushed in a mortar and mounted onto a sample stub using double-sided tape. The analysis region was roughly 3 mm x 5 mm. The Al2s peak was used for charge correction and was corrected to 118.5 eV. Linear oaselmes were used for measuring the peak heights of the A12s, Sι2s, and Nals lines, and a horizontal baseline starting at a bonding energy of 105.5 eV was used for measuring the height of the Sι2p line due to an interference with an aluminum Auger line. Peak intensities were converted to relative molar values using the following empirically derived sensitivity factors: Al2s 0.22, Sι2p 0.32, Sι2s 0.24 and Nals 1.72 and the following relationship: Relative number or atoms = (peak intensity/ sensitivity factor) * 100 (A12s ιntensιty/0.22 The results of the XPS measurements are given m Table II. The numbers reported for XPS measurements are the number of atoms detected relative to 100 aluminum atoms. The XPS silicon values reported are tne average of the Sι2p and Sι2s values. TABLE II. Na and Si XPS for Selected α-Alumina Carriers pH Measurement Procedures Silver solution pH measurements were done using a Metrohm model 744 pH meter, employing a model 6.0220.100 combination electrode and a Pt 100 model 6.1110.100 resistance thermometer for temperature compensation. The meter was calibrated with commercially available buffer solutions before each use. In a typical measurement, a 50 ml aliquot of the doped silver solution to be used for a catalyst impregnation was filtered into a 100 ml glass beaker through a 2 micrometer filter attached m-line to a plastic syringe. The pH probe was lowered into the magnetically stirred solution, and the reading ootameo after 3 minutes was recorded as the equilibrated pH . The probe was cleaned between each measurement with deionized water, and checked for calibration. Special care was taken to prevent accumulation of AgCl solids on the electrode membrane. Such accumulation was removed by __ soaking the probe in ammonium hydroxide solution, as recommended by the manufacturer. Example 1 A catalyst pre-cursor was prepared from Carrier A by first subjecting the carrier to carrier washing. Following the wash, approximately 30 grams of washed Carrier A were placed under a 3.33 kPa vacuum for 1 minute at ambient temperature. Approximately 50 grams of the impregnating solution was then introduced to submerse the carrier, and the vacuum was maintained at 3.33 kPa for an additional 3 minutes. The cesium target was 450 ppm/gram finished catalyst. The vacuum was then released and the excess impregnating solution was removed from the catalyst pre-cursor by centrifugation at 500 rpm for two minutes. The catalyst pre-cursor was then dried while being shaken at 240 °C for 4 minutes in a stream of air flowing at 11.3 m 3 /hr. Example la (Comparative) Carrier A was impregnated as described in Example 1; however, the carrier was not subjected to carrier washing. The cesium target was 400 ppm/gram finished catalyst . Example 2 Carrier B was subjected to carrier washing and impregnation as described in Example 1. The cesium target was 450 ppm/gram finished catalyst. Example 2a (Comparative) Carrier B was impregnated as described in Example 1; however, the carrier was not subjected to carrier washing. The cesium target was 400 ppm/gram finished catalyst . Example 3 Carrier C was subjected to carrier washing and impregnation as described in Example 1. The cesium __ target was 300 ppm/gram finished catalyst. Example 3a (Comparative) Carrier C was impregnated as described in Example 1; however, the carrier was not subjected to carrier washing. The cesium target was 360 ppm/gram finished catalyst . Example 4 Carrier D was subjected to carrier wasmng and impregnation as described in Example 1. The cesium target was 400 ppm/gram finished catalyst. Example 4a (Comparative) Carrier D was impregnated as described Example 1; however, the carrier was not subjected to carrier washing. The cesium target was 400 ppm/gram finished catalyst. Example 5 Carrier A was suojecteo to carrier washing and impregnation as described in Example 1. The cesium target was 450 ppm/gram finished catalyst. In addition, 35 %w aqueous tetraethylammonium hydroxide (TEAH) was added to the stock impregnation solution at a target of 117.8 micromoles OH ~ /ml Ag solution, to lower the hydrogen ion activity to a "measured pH" of 13.2. Example 6 100 g of Carrier A were immersed in 300 ml of boiling 5% TEAH for 15 mm, then immersed six times 300 ml of boiling de-ionized water for 15 minutes each. The carrier was then removed and dried a well ventilated oven at 150 °C for 18 hours. The carrier was then impregnated with a cesium target of 400 ppm/gram finished catalyst. In addition, 35 %w TEAH was added to the stock impregnation solution at a target of 117.8 micromoles OH ~ /ml Ag, to lower the hydrogen ion activity to a "measured pH" of 13.6. Example 7 — Carrier A was subjected to carrier washing and impregnation as described in Example 1. The cesium target was 720 ppm/gram finished catalyst. In addition, TEAH was dissolved in water and added to the stock solution at a target of 117.8 micromoles OHNml Ag, to lower the hydrogen activity to a "measured pH" of 13.2, and NH 4 ReOd was dissolved in water and added to the stock solution to provide 1.5 micromoles Re/gram finished catalyst . Example 8 Carrier A was subjected to carrier washing and impregnation as described in Example 1. The cesium target was 450 ppm/gram finished catalyst. In addition, LiOH was dissolved in water and added to the stock impregnation solution to lower the hydrogen ion activity to a "measured pH" of 13.2. Example 8a (Comparative) Carrier A was impregnated as described in Example 5; however, the carrier was not subjected to carrier washing. The cesium target was 400 ppm/gram finished catalyst . Example 9 300 g of Carrier A were immersed in 900 ml of a boiling 0.1 M solution of ammonium acetate for 15 mm, then immersed in 300 ml of de-ionized water at 25 °C for 15 minutes, followed by immersion three times in 300 ml of boiling de-ionized water for 15 minutes each. The carrier was then removed and dried in a well ventilated oven at 150 °C for 18 hours. The carrier was then impregnated as described in Example 1. The cesium target was 450 ppm/gram finished catalyst. In addition, LiOH was dissolved in water and added to the stock impregnation solution to lower the hydrogen ion activity to a "measured pH" of 13.2. _ Example 10 The α-alumma source material for Carrier A was washed with de-ionized water at 25 °C, then homogenized with the same ingredients used to form Carrier A before extruding, drying, and firing m a muffle furnace. The resulting carrier was designated Carrier E. A catalyst was prepared from Carrier E in the same manner as outlined in Example 1. The cesium target was 360 ppm/gram finished catalyst. In addition, LiOH was dissolved in water and added to the stock impregnation solution to lower the hydrogen ion activity to a "measured pH" of 13.2. Example 11 Carrier E was used to prepare a catalyst in the same manner as described in Example 10; however, the carrier was subjected to the carrier washing procedure before impregnation. The cesium target was 510 ppm/gram finished catalyst. In addition, LiOH was dissolved in water and added to the stock impregnation solution to lower the hydrogen ion activity to a "measured pH" of 13.2. Example 12 100 g of Carrier A were immersed in 300 ml of a boiling 0.1 M solution of barium acetate at 25 °C for 15 mm, then immersed in 300 ml of de-ionized water at 25 °C for 15 minutes, followed by immersion three times 300 ml of boiling de-ionized water for 15 minutes each. The carrier was then removed and dried in a well ventilated oven at 150 °C for 18 hours. The carrier was then impregnated as described Example 1. The cesium target was 400 ppm/gram finished catalyst. In addition, LiOH was dissolved in water and added to the stock impregnation solution to lower the hydrogen ion activity to a "measured pH" of 13.2. — Example 13 Carrier A was subjected to carrier washing and impregnation as described Example 1. The cesium target was 650 ppm/gram finished catalyst. In addition, LiOH was dissolved in water and added to the stock impregnation solution to lower the hydrogen ion activity to a "measured pH" of 13.2 and NH 4 Re0 4 was dissolved in water and added to the stocK impregnation solution to provide 1.5 micromoles Re/gram finished catalyst. The catalysts of Examples 1-13 were used to produce ethylene oxide from ethylene and oxygen. 3 to 5 grams of crushed catalyst were loaded into a 6.35 mm inside diameter stainless steel U-shaped tube. The U tube was immersed in a molten metal bath (heat medium) and the ends were connected to a gas flow system. The weight of the catalyst used and the inlet gas flow rate were adjusted to achieve a gas hourly space velocity of 6800 ml of gas per ml of catalyst per hour. The inlet gas pressure was 1450 kPa. The gas mixture passed through the catalyst bed (in a once-through operation) during the entire test run (including start-up) consisted of 25% ethylene, 7.0% oxygen, 5% carbon dioxide, 63% nitrogen, and 2.0 to 6.0 ppmv ethyl chloride. The initial reactor (heat medium) temperature was 180 °C. The temperature was ramped at a rate of 10 °C per hour from 180 °C to 225 °C, and then adjusted so as to achieve a constant ethylene oxide level of 1.5 %v in the outlet gas stream. Performance data at this conversion level are usually obtained when the catalyst has been on stream for a total of at least 1-2 days. Due to slight differences feed gas composition, gas flow rates, and the calibration of analytical instruments used to determine the feed and product gas compositions, the measured selectivity and activity of a given catalyst may vary slightly from one test run to the next. The initial performance values for selectivity at 1.5% ethylene oxide were measured and are reported m Table III. TABLE III. Performance Characteristics of Catalysts Prepared From Unwashed and Washed α-Alumina It can be seen that significant improvement in catalyst properties are seen when the carrier is washed before the catalytic metal is deposited on the carrier. Even further improvement is seen when the material used to make the carrier is washed before the carrier is — formed . The hydrogen ion activity of the deposition solution for catalysts m Examples 5-13 was lowered by the addition of a base. It can be seen that lowering the hydrogen ion activity of the deposition solution further improves the catalytic properties. It is also evident that the phenomenon of the pH effect is not restricted to a particular catalyst formulation, as best illustrated in Examples 7 and 13, where a selectivity enhancing dopant, such as rhenium, is added to the impregnating solution. It will be apparent to one of ordinary skill in the art that many changes and modifications may be made to the invention without departing from its spirit or scope as set forth herein.

Claims: C L A I M S 1. A process for improving the properties of a carrier for a catalyst by a treatment, which treatment is performed on one or more of the materials from which the carrier is formed and/or on the complete carrier and which treatment is effective in lowering the concentration of one or more ionizable species present on the surface of the complete carrier, the lowering being expressed as the lowering of the relative concentration of Na and/or Si atoms, as measured by X-ray Photoelectron Spectroscopy (XPS) performed on the untreated and treated carrier . 2. A process according to claim 1 characterized m that the treatment is performed by means effective m rendering the ionizable species ionic, or rendering the ionizable species insoluble, or rendering the ionizable species immobile. 3. A process according to claim 2 characterized m that said means is selected from washing, ion exchange, volatilization, precipitation, sequestration, and combinations thereof. 4. A process according to claim 3, characterized in that said washing is performed with an aqueous and/or organic solvent-based solution, selected from water, tetraethylammonium hydroxide, ammonium acetate, lithium carbonate, barium acetate, strontium acetate, crown ether, methanol, ethanol, dimethylformamide, and mixtures thereof . 5. A process according to any one of claims 1-4, characterized in that the concentration, as measured by XPS, of Na on the surface of the carrier is lowered by at least 5 percent and/or the Si concentration is lowered by at least 5 percent. 6. A process according to any one of claims 1-5, characterized in that the concentration lowering treatment is followed by a drying step. 7. A process for preparing a catalyst, by depositing a catalytically effective amount of one or more catalytically reactive metals and optionally one or more promoter materials on a carrier prepared by a process according to any one of claims 1-6. 8. A process according to claim 7, characterized in that said catalytically reactive metal and optional promoter material deposition is effected by submerging said carrier m an impregnation solution wherein a hydrogen ion activity of said solution is lowered. 9. A process according to claim 7 or 8, characterized in that the catalyst is suitable for the vapor phase epoxidation of an alkene. 10. A process according to claim 9, characterized in that the catalyst is suitable for the epoxidation of ethylene to ethylene oxide, containing silver as the mam catalytically reactive metal on an alumina-based carrier. 11. A process for the catalytic epoxidation of an alkene with an oxygen containing gas, wherein a catalyst as prepared according to claim 7 or 8 is used. 12. A process according to claim 11, characterized m that at least one of the nitrogen oxides is added to the oxygen containing gas.

Inventors: LOCKEMEYER JOHN ROBERT, LOCKEMEYER, JOHN, ROBERT
Applicants: SHELL INT RESEARCH, SHELL INTERNATIONALE RESEARCH MAATSCHAPPIJ B.V.
Application year: 1999
Main classification: B01J23
IPC codes: B01J21, B01J23, B01J33, B01J37, C07B61, C07D301