Non-magnetic metallic substrate for high-temperature superconductors and process for manufacture thereof

Abstract: Nonmagnetic metallic substrate, consisting of a Nickel-Vanadium alloy having a Vanadium atom concentration within the range 8-12%. Said alloy possesses a cubic-shaped texture and a Curie temperature lower than the operative temperature of the so-called high temperature superconductors. The manufacture process is described as well.

Description: The present invention relates to a nonmagnetic metallic substrate of cubic-shaped texture for the manufacture of high-temperature superconducting tapes, and to the production process thereof. According to the invention, such tape consists of a flexible tape realised with a nonmagnetic Nickel-Vanadium metallic alloy, having a cubic-shaped texture from a crystallographic point of view. The substrates most commonly used for superconductors consist of pure Ni (purity >99.9%). This is so because in pure Ni the cubic-shaped texture can easily be induced with a thermo-mechanical treatment. Further, Ni possesses suitable chemical and mechanical properties, having a high oxidation resistance and a sufficient flexibility even after a thermal recrystallization treatment. The main drawback of the Ni lies in its being ferromagnetic, with a Curie temperature of 358°C, and therefore well over the operative temperature of the superconducting tapes (approx. -195°C). A superconducting tape onto a ferromagnetic metallic substrate would have high losses under alternating current due to the magnetisation energy of the substrate itself. Accordingly, an energy dissipation would follow, with the consequent significant decrease of the tape electrical properties. In the case of application in high magnetic fields (e.g. magnetic storage accumulators, superconducting magnets, etc.) the magnetic field-forces would limit the use of the cable in this field. Another metal that can easily be provided with a cubic-shaped texture is copper. It is not ferromagnetic, but its mechanochemical properties, particularly its low resistance to oxidation, do not allow an easy use thereof. The Ni-V tape according to the invention is a support suitable for the manufacture of high critical temperature superconducting tapes based on thick biaxially-oriented films, in particular of the superconductor YBaCu 3 O 7x (YBCO) or ReBa 2 Cu 3 O 7-x , wherein Re are rare earths. The Ni-V tape maintains the chemical, mechanical and crystalline properties of the Ni tape, having the further advantage that its Curie temperature can be controlled through the vanadium concentration. For instance, for an alloy having a 12% of vanadium atoms the Curie temperature is of approximately 10 K, well below the operative temperature of the superconductor cable. In short, the Ni-V tape possesses the desired properties of the Ni-Cu tapes. In this sense, the Ni-V tape represents an ideal metallic substrate for the epitaxial growth of the thick superconducting films for the manufacture of the second generation SAT tapes. The superconductor cables based on thick YBCO films deposited on flexible metallic substrates represent the second generation of superconducting tapes having a high critical temperature for applications on a large scale. A method for the preparation of such tapes foresees the use of metallic supports of cubic-shaped texture having suitable magnetic, mechanic, thermal and chemical characteristics. To date, the support used has been the nickel; such metal possesses the above mentioned properties, save the fact that it is ferromagnetic at the operative temperatures of the superconducting cable (64-80K). The main drawback of the nickel support lies in this latter property, as it limits the potential applications of the superconductor YBCO cable. Another metal, having crystalline and magnetic characteristics suitable for such applications, is the copper, that however possesses utterly unsuitable mechanochemical properties. According to the present invention a tape-shaped substrate base is provided, suitable for the realisation of superconducting tapes possessing the properties described in the characterising part of the product claims. Further according to the present invention, a process for the manufacture of a Nickel-Vanadium tape of a cubic-shaped texture is provided, using the steps as disclosed in the characterising part of the process claims. The present invention will be disclosed hereinafter with reference to one of its presently preferred embodiments, reported by way of example and not for limiting purposes, and making reference to the figures of the annexed drawings, wherein: figure 1 shows the magnetic characteristics of a solid Ni-V solution: Curie temperature (temperature below which the material is ferromagnetic) of the nickel, with the increase of the concentration; figure 2 shows an X-ray (-2) diffraction pattern for a Ni-V sample subjected to a thermo-mechanical treatment; figure 3 shows polar figures of the planes (111) and (200) obtained by X-ray measurement for a Ni-V sample subjected to a thermo-mechanical treatment; figure 4 shows an X-ray (-2) diffraction pattern for a Ni sample subjected to a thermo-mechanical treatment; figure 5 shows polar figures of the planes (111) and (200) obtained by X-ray measurements for a Ni sample subjected to a thermo-mechanical treatment. According to the present invention a flexible metallic substrate is provided, having a preferential orientation (100)[001] and suitable magnetic, chemical, mechanical properties for the manufacture of superconducting tapes of high critical temperature: for a cubic-shaped texture (100)[001] the grains of which the material is composed have the crystalline plane (100) parallel to the rolling surface and the crystalline direction [100] parallel to the rolling direction, i.e. the grains are biaxially oriented. Such support consists of a solid Ni-V solution, with the atomic concentration of the Vanadium in the range 8-12%. The vanadium lowers the Curie temperature (temperature below which the material is ferromagnetic) of the nickel, with the increasing of the concentration thereof, as shown in figure 1. Moreover, being a solid solution, it maintains to a great extent the crystalline and chemical properties of the nickel, improving the mechanical ones thereof. For the sake of simplicity, the solid Ni-V solution will be referred to hereinafter as Ni-V alloy. The Ni-V metallic tape is obtained by thermo-mechanical treatments, as will be disclosed hereinafter. From a crystallographic point of view, it exhibits a cubic-shaped texture (100)[001], as can be derived from the polar figures of the planes (111) and (200). In general, in the X-ray spectrum (-2) only those peaks related to the planes parallel to the diffractometer plane are highlighted, overlapping in the case at issue to the rolling plane (tape surface). In figure 2 only those peaks related to the parallel planes (200) and (400) are present: this means that all the grains are lined up with the plan (100) parallel to the surface ("off-plane" orientation). Concerning the polar figures, in general they provide information related to the distribution of the grain orientation with respect to an arbitrary direction; in the case at issue such direction is the rolling direction: for a non orientated polycrystalline sample the poles are uniformly distributed onto the figure plane, while figure 3 clearly indicates that the tape poles according to the invention are well localised, their position overlapping with that of a centred-face cubic crystal (FCC). This means that all the tape grains are oriented with the direction [100] parallel to the rolling direction ("in-plane" orientation). The measurements reported in figures 2 and 3 also show that the Ni-V alloy has a texture comparable to that of the pure metals as nickel and copper. In comparison, the spectrum -2 and the polar figures for a Nickel support are represented in figures 4 and 5, respectively. The process according to the invention for the manufacture of the Ni-V tape provided with a cubic-shaped texture foresees the following steps: during the first step the preparation of a Nickel-Vanadium solid solution takes place, with the atomic concentration in the range 8-12%; the Ni and V ingots are placed in a smelter (arc furnace, plasma, etc.), and the smelting process takes place in a controlled atmosphere, with a water-cooled ingot mold in order to avoid a contamination of the alloy by the ingot mold material, typically consisting of copper; in the second step the material is mechanically subdivided by machining in bars (e.g., approximately of a 4 x 4 mm 2 section and approx. of a 10 cm length); the bars are treated at 900°C for 1 hour to eliminate the work hardening effects; the third step foresees the cold-rolling of the bars with a consequent thickness reduction of over 95%; thus yielding thicknesses thinner than 200 µm; the fourth and final step consists of a thermal recrystallization treatment of the tape, preferably in an high-vacuum furnace (approx. 5x10 -7 Torr) to avoid the tape oxidation, at temperatures typically comprised in the range 800-1000°C for at least one hour. Preferably, the upward and downward thermal ramps have a speed of approx. 1000°C/hour The tape thus obtained exhibits a surface having a cleaning rate sufficient to be used as substrate for the deposition of the YBCO superconductor, with no need of further special cleaning processes. Therefore, the main innovation of the invention lies in the decrease of the Curie temperature, by the alloying of nickel with nonmagnetic elements (vanadium), while maintaining all the properties of the analogous nickel support. Industrial usefulness The invention is needed for the manufacture of thick films provided with a crystalline structure. The present nonmagnetic metallic substrate of cubic-shaped texture was developed in particular for the epitaxial growth of thick films (d≅1÷5 µm) of ReBa 2 Cu 3 O 7-x (Re = Y, Nd, Sm, etc.) for the manufacture of tapes superconductor at a high temperature: through the epitaxial growth process, the cubic-shaped texture of the substrate is passed to the superconducting film. Thus, a superconducting film with a controlled grain edge is obtained, that can carry a current density of approximately 10 6 A/cm 2 at the liquid nitrogen temperature (77 K) and in a null magnetic field. Superconducting films with a controlled grain edge deposited onto a substrate are called "second-generation high temperature superconducting tapes (SAT)". The potential applications of the second-generation SAT tapes are several: superconducting magnets, power transmission lines, superconducting transformers, short-circuit current limiters, magnetic storage accumulators (SMES), etc. The "quasi-crystal" metallic substrate might also constitute an alternative to the single-crystal substrates for the growth of oriented ferroelectric films like PbTiO 3 and PbZr x Ti 1-x O 3 , and films of ferromagnetic materials. Therefore, the importance of the invention lies essentially in the possibility of disposing of a nonmagnetic metallic support provided with a crystalline structure and with great potential, in particular in the manufacture of superconducting tapes of high critical temperature, piezoelectric and ferroelectric films.

Claims: A nonmagnetic metallic tape or substrate, characterised in that it consists of a Nickel-Vanadium alloy with an atomic concentration percentage of vanadium in the range 8-12%, and in that said alloy possesses a cubic-shaped texture and a Curie temperature lower than the operative temperature of the so-called high temperature superconductors. The nonmagnetic metallic tape or substrate according to claim 1, characterised in that it constitutes a support for the so-called high temperature superconductors. The tape or substrate according to claim 2, characterised in that said high-temperature superconductors are of the type ReBCu 3 O 7-x where Re indicates rare earths. The tape or substrate according to claim 2, characterised in that said high-temperature superconductor consists of YBa 2 Cu 3 O 7-x . The tape or substrate according to claim 1, characterised in that it possesses a quasi-crystalline structure suitable for the growth of piezoelectric or oriented ferroelectric films, of the titanate class, such as PbTiO 3 and PbZr x Ti 1-x O 3 . A process for the manufacture of the tape or of the Ni-V substrate provided with a cubic-shaped texture, according to one or more of the preceding claims, foreseeing the following steps: a) a first step wherein the preparation of a solid Nickel-Vanadium solution takes place, with the atomic concentration in the range 8-12%; the Ni and V ingots being placed in a smelter (arc furnace, plasma, etc.), and the smelting process taking place in a controlled atmosphere, with a water-cooled ingot mold in order to avoid a contamination of the alloy by the ingot mold material, typically consisting of copper; b) a second step wherein the material is mechanically subdivided by machining in bars approximately of a 4 x 4 mm 2 section and approx. of a 10 cm length); the bars being treated for at 900°C for 1 hour to eliminate the work hardening effects; c) a third step entailing the cold-rolling of the bars with a consequent thickness reduction of over 95%; thus yielding thicknesses thinner than 200 µm; d) a fourth and final step consisting of a thermal recrystallization treatment of the tape preferably in an high-vacuum furnace (approx. 5x10 -7 Torr) to avoid the tape oxidation, at temperatures typically comprised in the range 800-1000°C for at least one hour, the upward and downward thermal ramps preferably having a rate of approx. 1000°C/hour.

Inventors: BOFFA VINCENZO, CERESARA SERGIO, PETRISOR TRAIAN, BOFFA, VINCENZO, CERESARA, SERGIO, PETRISOR, TRAIAN
Applicants: ENEA ENTE NUOVE TEC, ENEA ENTE PER LE NUOVE TECNOLOGIE
Application year: 1999
Main classification: H01L39
IPC codes: H01L39