METHOD FOR ELIMINATING WRINKLING IN COMPOSITE COLOR-PLUS-CLEAR COATINGS, AND COMPOSITIONS FOR USE THEREIN

Abstract: The curable coating composition of the invention comprises a film forming component (A) and a wrinkle reducing catalyst (B) comprising a compound of the formula: My(L)x; wherein M is a metal having an empty or full d orbital and wherein the pk2 of the aqua ion of M is less than or equal to 12; L is a ligand wherein the pka of the parent acid is >/=-10 and is </=4; and x is an integer which is a multiple of the charge of M, y is an integer which is a multiple of the charge of L, x and y selected so that ML is charge balanced. Film forming component (A) has first component (a) with a compound having appended thereto at least one carbamate or urea functional group, or a group convertible to a carbamate or urea group, and a second component (b) with a compound reactive with said carbamate or urea groups on component (a). The method of the invention requires applying a first coating to a substrate; applying a second coating to the first coating to provide a composite coating, the second coating comprising the composition of the invention, and curing the composite coating.

Description: METHOD FOR ELIMINATING WRINKLING IN COMPOSITE COLOR-PLUS- CLEAR COATINGS, AND COMPOSITIONS FOR USE THEREIN FIELD OF THE INVENTION This invention relates to composite color-plus-clear coatings having improved appearance, especially with respect to wrinkling and color, and to methods and compositions for providing such coatings. BACKGROUND OF THE INVENTION Composite color-plus-clear coatings are widely utilized in the coatings art. They are particularly desirable where exceptional gloss, depth of color, distinctness of image, or special metallic effects are required. The automotive industry has made extensive use of color-plus-clear composite coatings for automotive body panels. As used herein, the term ..composite color-plus-clear" relates to composite coating systems requiring the application of a first coating, typically a colored basecoat coating, followed by the application of a second coating, generally a clearcoat, over the noncured or „wet" first coating. The applied first and second coatings are then cured. Thus, such systems are often described as „wet on wet" or „two coat/one bake". Drying processes which fall short of complete cure may be used between the application of the coatings. Clearcoats used in color-plus-clear systems must have an extremely high degree of clarity in order to achieve the desired visual effects. High gloss coatings also require a low degree of visual aberrations at the surface in order to achieve the desired visual effect such as high distinctness of image (DOI). As a result, clearcoats of color-plus-clear systems are especially susceptible to the phenomenon known as environmental etch, i.e., spots or marks on or in the clear finish that often cannot be rubbed out. Although many compositions have been proposed for use as the clearcoat of a color-plus-clear composite coating, prior art clearcoat coatings often suffer from disadvantages such as coatability problems, compatibility problems with the colored basecoat, solubility problems, and/or insufficient resistance to environmental etch. Clearcoat coating compositions exhibiting many advantages over prior art compositions, especially with respect to environmental etch, were disclosed in US Patents 5,474,811 and 5,356,669. The disclosed clear coating compositions comprise a first component comprising a polymer backbone having appended thereto at least one carbamate functional group, and a second component comprising a compound having a plurality of functional groups that are reactive with said carbamate groups. However, regardless of the foregoing improvements, the application of a clear coating composition over a colored basecoat in a wet-on-wet or two coat/one bake system may sometimes result in an undesirable phenomenon known as -wrinkling". Wrinkling often manifests as one or more small furrows or ridges in the cured clearcoat. Most often, there appears a plurality of furrows, often in areas of low clearcoat film build and high basecoat film build. It is theorized that such imperfections are caused by folding or "wrinkling" of the clearcoat during the curing process. While not wishing to be bound to a particular theory, it is believed that wrinkling may occur as a result of the presence of or reaction between volatilized amines and acid catalysts. Such a combination can result from the use of a basecoat composition employing waterbome technology, especially anionic stabilized waterbome systems requiring the use of volatile amines, and a solvent borne clearcoat composition utilizing strong acid catalyzed melamine formaldehyde crosslinkers. Cured color-plus-clear composite coatings exhibiting wrinkling do not possess the required appearance and/or degree of clarity. Composite coatings vulnerable to wrinkling are viewed unfavorably by the automotive industry. Thus, there is a need for a curable coating composition suitable for use in a color-plus-clear composite coating which possesses desirable curing, performance, and appearance properties but which does not exhibit wrinkling upon cure of the composite coating. Desirable performance properties are good solvent resistance, hardness and environmental etch resistance. The coating should also cure at commercially acceptable curing conditions. Advantageous appearance properties are a color resulting solely from the desired pigmentation, high DOI, and a glossy appearance over a wide range of basecoat and clearcoat film thickness. In particular, it would be advantageous to provide curable coating compositions comprising carbamate functional resins which, when used in a color-plus-clear composite coating, do not exhibit wrinkling upon cure of the composite coating. Most particularly, it would be desirable to provide clearcoat coating compositions which, when used as the clear in a color-plus-clear composite coating, provide composite coatings having advantageous performance and environmental etch properties but which are substantially free of wrinkling. Finally, it would be desirable to provide a method for providing substantially wrinkle free color-plus-clear composite systems. SUMMARY OF THE INVENTION It is thus an objective of the invention to provide a curable coating composition and a method for using the same to produce color-plus-clear composite coatings which have advantageous performance and appearance properties and which are substantially free of wrinkling upon cure. More particularly, it is an objective of the invention to provide curable coating compositions comprising a first component which is a compound having appended thereto at least one carbamate or urea functional group, or a group convertible to a carbamate or urea group, and a second component which is a compound reactive with said carbamate or urea groups on component (a), which coating compositions do not exhibit wrinkling when used as the clearcoat in a color-plus-clear composite coating. It has now been unexpectedly discovered that the foregoing can be achieved with the use of a particular curable coating composition including a film forming component (A) which includes a first component (a) comprising a compound having appended thereto at least one carbamate or urea functional group, or a group convertible to a carbamate or urea group, and a second component (b) comprising a compound reactive with said carbamate or urea groups on component (a), and a wrinkle reducing catalyst (B) comprising a compound of the formula: M y (L) x wherein M is a metal having an empty or full d orbital and wherein the pk a of the aqua ion of M is less than or equal to 12; L is a ligand wherein the pk a of the parent acid is > -10 and is < 4; and x and y being integers such that ML is charge balanced. The method of the invention achieves the foregoing objectives by applying a first coating to a substrate, applying a second coating to the first coating to provide a composite coating, the second coating comprising a film forming component(A) which includes a first component (a) comprising a compound having appended thereto at least one carbamate or urea functional group, or a group convertible to a carbamate or urea group, and a second component (b) comprising a compound reactive with said carbamate or urea groups on component (a), and a wrinkle reducing catalyst (B) comprising a compound of the formula: M y (L) x wherein M is a metal having an empty or full d orbital and wherein the pk a of the aqua ion of M is less than or equal to 12; L is a ligand wherein the pk a of the parent acid is > -10 and is < 4; and x and y being integers such that ML is charge balanced , and subjecting the composite coating to a temperature between 200°F/93°C and 350°F/176.6 °C for a time sufficient to effect cure of the composite coating, wherein the cured composite coating is substantially wrinkle free. DETAILED DESCRIPTION The present inventions provide a curable coating composition for use in obtaining color-plus-clear composite coatings having improved appearance with respect to wrinkling and color, and a method of providing such cured composite coatings. The curable coating composition of the invention comprises a film forming component (A) and a wrinkle reducing catalyst (B) comprising a compound of the formula: M y (L) x wherein M is a metal having an empty or full d orbital and wherein the pk a of the aqua ion of M is less than or equal to 12; L is a ligand wherein the pk a of the parent acid is > -10 and is < 4; and x and y being integers having numerical values such that ML is charge balanced. The term ,,film forming component (A)" as used herein refers to the binder or solid material which forms the polymeric film portion of the cured film. Film forming component (A) of the curable coating composition of the invention includes a first component (a) which comprises a compound having appended thereto at least one carbamate or urea functional group, or a group convertible to a carbamate or urea group and a second component (b) comprising a compound reactive with said carbamate or urea groups on component (a). First component (a)comprises a compound selected from the group consisting of oligomers and polymers having appended thereto more than one carbamate group or more than one urea group, or more than one group convertible to a carbamate or urea group. Oligomers typically have a molecular weight of between 148 and 2000, the preferred molecular weight for the oligomers is between 900 and 1092; polymers typically have a molecular weight of between 2,000 and 20,000, the preferred molecular weight for the polymers is between 4000 and 6000. Mixtures of said oligomers and polymers may be used as component (A). Molecular weight can be determined by the GPC method using a polystyrene standard. The carbamate or urea content of the polymer, on a molecular weight per equivalent of carbamate or urea functionality, will generally be between 200 and 1200, and preferably between 300 and 800. Carbamate groups can generally be characterized by the formula -0-C(0)-NHR wherein R is H or alkyl, preferably of 1 to 4 carbon atoms. Preferably, R is H or methyl, and more preferably R is H. Urea groups can generally be characterized by the formula -NR'-C(0)-NHR", wherein R' and R" each independently represent H or alkyl, preferably of 1 to 4 carbon atoms, or R' and R" may together form a heterocyclic ring structure (e.g. where R' and R" form an ethylene bridge). Groups that can be converted to carbamate include cyclic carbonate groups, epoxy groups, and unsaturated bonds. Cyclic carbonate groups can be converted to carbamate groups by reaction with ammonia or a primary amine, which ring-opens the cyclic carbonate to form a β-hydroxy carbamate. Epoxy groups can be converted to carbamate groups by first converting to a cyclic carbonate group by reaction with C0 2 . This can be done at any pressure from atmospheric up to supercritical C0 2 pressures, but is preferably under elevated pressure (e.g. 60-150 psi). The temperature for this reaction is preferably 60-150°C. Useful catalysts include any that activate an oxirane ring, such as tertiary amine or quaternary salts (e.g. tetramethyl ammonium bromide), combinations of complex organotin halides and alkyl phosphonium halides (e.g., ((CH) 3 Snl, BU 4 Snl, Bu 4 PI, and (CH 3 ) 4 PI), potassium salts (e.g., K 2 C0 3 , Kl), preferably in combination with crown ethers, tin octoate, calcium octoate, and the like. The cyclic carbonate group can then be converted to a carbamate group as described above. Any unsaturated bond can be converted to carbamate groups by first reacting with peroxide to convert to an epoxy group, then with C0 2 to form a cyclic carbonate, and then with ammonia or a primary amine to form the carbamate. Oligomeric compounds useful as first component (a), and having more than one carbamate functional group, have the general formula -X-C(0)-NHRι, wherein X is 0, S or NH, R-] is H or alkyl of 1 to 4 carbon atoms. The compounds useful as oligomeric component (a) according to the invention can be prepared in a variety of ways. The carbamate can be primary, terminating in an NH2 group, or secondary, terminating in an NHR group. In a preferred embodiment, the carbamate is primary. One way to prepare oligomeric compounds useful as component (a) is to react an alcohol ('alcohol' is defined herein as having one or more OH groups) with more than one urea to form a compound with carbamate groups. This reaction is accomplished by heating a mixture of the alcohol and ureas. This reaction is also performed under heat, preferably in the presence of a catalyst as is known in the art. Another technique is the reaction of an alcohol with cyanic acid to form a compound with primary carbamate groups (i.e., unsubstituted carbamates). Carbamates may also be prepared by reaction of an alcohol with phosgene and then ammonia to form a compound having primary carbamate groups, or by reaction of an alcohol with phosgene and then a primary amine to form a compound having secondary carbamate groups. Another approach is to react an isocyanate (e.g., HDI, IPDI) with a compound such as hydroxypropyl carbamate to form a carbamate-capped isocyanate derivative. Finally, carbamates can be prepared by a transcarbamylation approach where an alcohol is reacted with an alkyl carbamate (e.g., methyl carbamate, ethyl carbamate, butyl carbamate) to form a primary carbamate group-containing compound. This reaction is performed under heat, preferably in the presence of a catalyst such as an organometallic catalyst (e.g., dibutyltin dilaurate). Other techniques for preparing carbamates are also known in the art and are described, for example, in P. Adams & F. Baron, "Esters of Carbamic Acid", Chemical Review, v. 65, 1965. Various alcohols can be used in the preparation of carbamate compounds useful as first component (a) according to the invention. They generally have from 1 to 200 carbon atoms, preferably 1 -60 carbon atoms, and may be monofunctional or polyfunctional (preferably a functionality of 2 to 3), aliphatic, aromatic, or cycloaliphatic. They may contain just OH groups, or they may contain OH groups plus heteroatoms such as O, S, Si, N, P, and other groups such as ester groups, ether groups, amino groups, or unsaturated sites. Examples of useful alcohols include 1 ,6-hexanediol,1 ,2- hexanediol, 2-ethyl-1 ,3-hexanediol, ethyl-propyl-1 ,5-pentanediol, 2-methyl- 2,4-pentanediol, 2,2,4-trimethyl-1 ,3-pentanediol, 2,4,7,9-tetramethyl-5-decyn- 4,7-diol, 1 ,3-dihydroxyacetone dimer, 2-butene-1 ,4-diol, pantothenol, dimethyltartrate, pentaethylene glycol, dimethyl silyl dipropanol, and 2,2'- thiodiethanol. Polymeric compounds suitable for use in first component (a) are selected from the group consisting of polyester, epoxy, alkyd, urethane, acrylic, polyamide, and polysilane polymers and mixtures thereof, wherein the polymer has more than one carbamate functional group appended thereto. In a preferred embodiment, first component (a) comprises a carbamate functional acrylic polymer represented by the randomly repeating units according to the following formula: - CH 2 -CR(CO-0-L * -=-CO-NHR) ■ ); -( A ^ , wherein In the above formula, R represents H or CH3. R' represents H, alkyl, preferably of 1 to 6 carbon atoms, or cycloalkyl, preferably up to 6 ring carbon atoms. It is to be understood that the terms alkyl and cycloalkyl are to include substituted alkyl and cycloalkyl, such as halogen-substituted alkyl or cycloalkyl. Substituents that will have an adverse impact on the properties of the cured material, however, are to be avoided. For example, ether linkages are thought to be susceptible to photo-induced hydrolysis, and should be avoided in locations that would place the ether linkage in the crosslink matrix. The values x and y represent weight percentages, with x being 10 to 90 % and preferably 20 to 50 %, and y being 90 to 10 % and preferably 80 to 50 %. In the formula, A represents repeat units derived from one or more ethylenically unsaturated monomers. Such monomers for copolymerization with acrylic monomers are known in the art. They include alkyl esters of acrylic or methacrylic acid, e.g., ethyl acrylate, butyl acrylate, 2-ethylhexyl acrylate, butyl methacrylate, isodecyl methacrylate, hydroxyethyl methacrylate, hydroxypropyl acrylate, and the like; and vinyl monomers such as unsaturated m-tetramethyl xylene isocyanate (sold by American Cyanamid as TMI®), vinyl toluene, styrene, styrenic derivatives such as α-methyl styrene, t-butyl styrene, and the like. L represents a divalent linking group, preferably an aliphatic of 1 to 8 carbon atoms, cycloaliphatic, or aromatic linking group of 6 to 10 carbon atoms. Examples of L include -(CH2)-, -(CH2 . 2-, -(CH2)4-, and the like. In one preferred embodiment, -L- is represented by -COO-L'- where U is a divalent linking group. Thus, in a preferred embodiment of the invention, polymeric first component (a) is represented by randomly repeating units according to the following formula: - CH 2 -CR(CO-0-L'-=-CO-NHR) -^ -^A )ζ .wherein In this formula, R, R', A, x, and y are as defined above. U may be a divalent aliphatic linking group, preferably of 1 to 8 carbon atoms, e.g., -(CH2)-, -(CH2 . 2-, -(CH2)4~, and the like, or a divalent cycloaliphatic linking group, preferably up to 8 carbon atoms, e.g., cyclohexyl, and the like. However, other divalent linking groups can be used, depending on the technique used to prepare the polymer. For example, if a hydroxyalkyl carbamate is adducted onto an isocyanate-functional acrylic polymer, the linking group L' would include an -NHCOO- urethane linkage as a residue of the isocyanate group. This carbamate functional acrylic polymer is described in U. S. Patent No. 5,356,669. . The first component (a) polymer used in the composition of the invention can be prepared in a variety of ways. One way to prepare such polymers is to prepare an acrylic monomer having a carbamate functionality in the ester portion of the monomer. Such monomers are well-known in the art and are described, for example in U.S. Patents 3,479,328, 3,674,838, 4,126,747, 4,279,833, and 4,340,497. One method of synthesis involves reaction of a hydroxy ester with urea to form the carbamyloxy carboxylate (i.e., carbamate-modified acrylic). Another method of synthesis reacts an a,b-unsaturated acid ester with a hydroxy carbamate ester to form the carbamyloxy carboxylate. Yet another technique involves formation of a hydroxyalkyl carbamate by reacting ammonia, or a primary or secondary amine or diamine with a cyclic carbonate such as ethylene carbonate. The hydroxyl group on the hydroxyalkyl carbamate is then esterified by reaction with acrylic or methacrylic acid to form the monomer. Other methods of preparing carbamate-modified acrylic monomers are described in the art, and can be utilized as well. The acrylic monomer can then be polymerized along with other ethylenically-unsaturated monomers, if desired, by techniques well-known in the art. An alternative route for preparing an acrylic polymer for use as component (a) in the composition of the invention is to react an already- formed polymer such as an acrylic polymer with another component to form a carbamate-functional group appended to the polymer backbone, as described in U.S. Patent 4,758,632, the disclosure of which is incorporated herein by reference. One technique for preparing such acrylic polymers involves thermally decomposing urea (to give off ammonia and HNCO) in the presence of a hydroxy-functional acrylic polymer or co-polymer to form a carbamate-functional acrylic polymer. Another technique involves reacting the hydroxyl group of a hydroxyalkyl carbamate with the isocyanate group of an isocyanate-functional acrylic or vinyl monomer to form the carbamate- functional acrylic. Isocyanate-functional acrylics are known in the art and are described, for example in U.S. Patent 4,301 ,257. Isocyanate vinyl monomers are well-known in the art and include unsaturated m-tetramethyl xylene isocyanate (sold by American Cyanamid as TMI®). Yet another technique is to react the cyclic carbonate group on a cyclic carbonate-functional acrylic with ammonia in order to form the carbamate-functional acrylic. Cyclic carbonate-functional acrylic polymers are known in the art and are described, for example, in U.S. Patent 2,979,514. A more difficult, but feasible way of preparing the polymer would be to trans-esterify an acrylate polymer with a hydroxyalkyl carbamate. Groups capable of forming urea groups include amino groups that can be converted to urea groups by reaction with a monoisocyanate (e.g., methyl isocyanate) to form a secondary urea group or with cyanic acid (which may be formed in situ by thermal decomposition of urea) to form a primary urea group. This reaction preferably occurs in the presence of a catalyst as is known in the art. An amino group can also be reacted with phosgene and then ammonia to form a compound having primary urea group(s), or by reaction of an amino group with phosgene and then a primary amine to form a compound having secondary urea groups. Another approach is to react an isocyanate with a hydroxy urea compound to form a urea-capped isocyanate derivative. For example, one isocyanate group on toluene diisocyanate can be reacted with hydroxyethyl ethylene urea, followed by reaction of the other isocyanate group with an excess of polyol to form a hydroxy carbamate. Second component (b) comprises a compound having functional groups reactive with said carbamate or urea groups on component (a). Suitable reactive groups include active methylol or methylalkoxy groups on aminoplast crosslinking agents or on other compounds such as phenol/formaldehyde adducts, acrylamide groups, isocyanate groups, siloxane groups, cyclic carbonate groups, and anhydride groups. Examples of (b) compounds include melamine formaldehyde resin (including monomeric or polymeric melamine resin and partially or fully alkylated melamine resin), urea resins (e.g., methylol ureas such as urea formaldehyde resin, alkoxy ureas such as butylated urea formaldehyde resin), polymers having acrylamide groups, polymers having methylol or alkoxymethyl groups, polyanhydrides (e.g., polysuccinic anhydride), and polysiloxanes (e.g., trimethoxy siloxane). Aminoplast resin such as melamine formaldehyde resin or urea formaldehyde resin are especially preferred. Even more preferred are aminoplast resins where one or more of the amino nitrogens is substituted with a carbamate group for use in a process with a curing temperature below 150°C, as described in U.S. patent application Serial No. 07/965,510 entitled "Carbamate-Defunctionalized Aminoplast Curing for Polymer Compositions" in the names of John W. Rehfuss and Donald L. St. Aubin. The curable coating composition of the invention further requires the use of a wrinkle reducing catalyst (B)which is one of a particular group of Lewis acids. It has been found that when curable coating compositions which include certain compounds of the structure M y (L) x , are used as the clearcoat in a composite coating process, composite coatings having an improved appearance with respect to wrinkling are obtained, even when waterbome anionically stabilized basecoats are utilized. Compounds suitable for use as wrinkle reducing catalyst (B) are those having the formula M y (L) x where M is a suitable metal and L a suitable ligand. x is an integer equal to a multiple of the numerical charge of M and y is an integer equal to a multiple of the numerical charge of L, x and y such that M y (L) x is charge balanced. Suitable metals M are those metals which are stable and have no partially filled d orbitals, i e , have empty or full d orbitals In addition, it has been found that M must be a stable metal which has an aqua ion having a pK a < 12 and more preferably a pK a < 9,5, and most prefereably, a pK a of about 9 0 or less Values for pK a may be found in Lange's Handbook of Chemistry, 13th Edition Illustrative metals are Lι +1 , Na +1 , K + , Be +2 , Mg +2 , Ca +2 , Sc +3 , Tι +4 , Zn +2 , Al +3 , Cd +2 , Hg +2 , Zn + \ Sn +2 and Sn +4 Preferred metals are Sn +2 , Sn +4 , Zn +2 and Al +3 Zn +2 and Al +3 are most preferred, with respective pK a 's of 8 96 and 5 01 , per Lange's Handbook of Chemistry, 13th Edition Suitable ligands L are those ligands having a parent acid with a pK a within the range of -10 < pK a < 4 More preferably, the ligand L is selected from the group of ligands having a parent acid with a p , within the range of -10 < pK a < 2, and most preferably a pKa within the range of -2 < pK, within the range of -2 < p , < 2 The term "parent acid" refers to the protonated form of the ligand L pK a ιs determined by the following relationship where HA + H 2 O^H 3 0 + +A κ» = ΓH.O ' I FAT [HA] pK a = - log K a Those skilled in the art will appreciate that ligand L may be a single atom or a group of atoms Illustrative examples of suitable ligands L are N0 3 alkyl, aryl, and arylalkyl substituted sulfonates, sulfates, phosphates and phosphonates Preferred ligands L are N0 3 "2 and arylalkyl substituted sulfonates and phosphates. Most preferred as L are N0 3 "2 and the anions of dodecylbenzenesulfonic acid (DDBSA) and phenyl acid phosphate (PAP). Compounds suitable as M y (L) x are Al (N0 3 ) 2 , Zn (N0 3 ) 2 and the Al +3 and Zn +2 salts of DDBSA and phenyl acid phosphate. Most preferred compounds for use as M y (L) x are Zn(N0 3 ) 2 and the Al +3 salt of DDBSA . Wrinkle reducing catalyst M y (L) x may be used in a blocked or unblocked state. Traditional blocking agents such as amines are suitable. An illustrative blocking agent is Adogen 188, an amine based blocking agent commercially available from Sherex Chemical of Dublin, Ohio. Wrinkle reducing catalyst M y (L) x may be used as the sole catalyst or as a wrinkle reducing catalyst used in combination with traditional catalysts known to wrinkle. It is most preferrd that wrinkle reducing catalyst M y (L) x be used as the sole catalyst. When wrinkle reducing catalyst M y (L) x is used as the sole catalyst in the coating composition, it must be used in an amount sufficient to effect complete cure of the composition when the composition is subjected to conditions of elevated heat, temperature, radiation etc.,. Typically, wrinkle reducing catalyst M y (L) x is used in an amount of from about 1.0 to 5.0 weight percent, based on the total nonvolatile of film forming component (A). More preferably, wrinkle reducing catalyst M y (L) x is used in an amount from about 1.0 to 2.0 weight percent, based on the total nonvolatile of film forming component (A). If wrinkle reducing catalyst M y (L) x is present in combination with catalysts traditionally used to enhance the cure reaction, wrinkle reducing catalyst M y (L) x is used in an amount from about 30 to 60 weight percent of total catalyst, most preferably in an amount from about 50 to 60 weight percent of total catalyst. The total catalyst amount should be about 3.0 to 5.0 weight percent, based on the total nonvolatile of film forming component (A). Traditional catalysts used to enhance the cure reaction are strong acid catalysts. Such catalysts are well-known in the art and include, for example, g-toluenesulfonic acid, dinonylnaphthalene disulfonic acid, dodecylbenzenesulfonic acid, phenyl acid phosphate, monobutyl maleate, butyl phosphate, and hydroxy phosphate ester. However, it is most preferred that the use of such strong acid catalysts be minimized as much as possible, since such acids are believed to contribute to the wrinkling problem. If a strong acid is used, dodecylbenzenesulfonic acid is preferred. A coating composition according to the present invention may be utilized, for example, in the form of substantially solid powder, or a dispersion, and optionally solvent may be utilized in the composition of the present invention. It is often desirable that the composition is in a substantially liquid state, which can be accomplished with the use of a solvent. In general, depending on the solubility characteristics of component (A), the solvent can be any organic solvent and/or water. In a preferred embodiment, the solvent is a polar organic solvent. More preferably, the solvent is a polar aliphatic solvent or polar aromatic solvent.Still more preferably, the solvent is a ketone, ester, acetate, alcohol, aprotic amide, aprotic sulfoxide, or aprotic amine. Examples of useful solvents include methyl ethyl ketone, methyl isobutyl ketone, n-amyl acetate, ethylene glycol butyl ether-acetate, propylene glycol monomethyl ether acetate, xylene, n- methylpyrrolidone (NMP), isobutanol (iBuOH), methanol (MeOH), propylene carbonate (PC), or blends of aromatic hydrocarbons. Alternatively, the solvent may be water or a mixture of water with small amounts of aqueous co-solvents. Additional ingredients may be added to the coating composition, such as, but not limited to pigments, rheology control agents, flow control additives, ultraviolet absorbers, and hindered amine light stabilizers. In a preferred embodiment of the invention, the composition of the invention is utilized as a pigmented coating composition or clearcoat coating composition. In such a composition, the solvent may be present in the composition of the invention in an amount of from about 0.01 weight percent to about 99 weight percent, preferably from about 10 weight percent to about 60 weight percent, and more preferably from about 30 weight percent to about 50 weight percent. In a particularly preferred embodiment, the composition of the invention is used as a clear and/or colorless coating composition over a pigmented basecoat as part of a composite color-plus-clear coating. Such composite coatings are popular for their depth of color and liquid glossy surface appearance. They have found particularly wide acceptance in the field of automotive coatings. The composition of the invention may also be used as the basecoat of a composite color-plus-clear coating. The invention further provides a method for providing a composite coating having an improved appearance, especially with respect to wrinkling. The method requires that a first coating be applied to a substrate. The first coating will generally be a cured composition, such as a primer, basecoat or clearcoat composition. Preferably, the first coating will be a pigmented basecoat composition, and most preferably a water borne basecoat composition such as is described in US Re. 34,730, hereby incorporated by reference. Other pigmented basecoat compositions for such composite coatings are well-known in the art, and do not require explanation in detail herein. Polymers known in the art to be useful in basecoat compositions include acrylics, vinyls, polyurethanes, polycarbonates, polyesters, alkyds, and polysiloxanes. A preferred polymer is an acrylic polymer. After the first coating is applied to the substrate, a second coating is applied to the substrate previously coated with the first coating. The second coating is applied directly onto the first coating. Preferably the second coating is applied to the first coating before the first coating is cured. Drying of the first coating short of complete cure may occur. The second coating comprises the coating composition of the instant invention comprising components (A) and (B) discussed above. Substrates may be plastic, metal, wood and mixtures thereof. Preferred substrates are plastic and metal automotive substrates, especially metal automotive body panels. Coating compositions can be coated on the article by any of a number of techniques well-known in the art. These include, for example, spray coating, dip coating, roll coating, curtain coating, and the like. For automotive body panels, spray coating is preferred. After an article is molded, casted, or coated with the above-described layers, the composition is subjected to conditions so as to cure the coating layers. Although various methods of curing may be used, heat-curing is preferred. Generally, heat curing is effected by exposing the coated article to elevated temperatures provided primarily by radiative heat sources. Curing temperatures will vary depending on the composition of first and second components (a) and (b)used, however they generally range between about 200°F/93°C and 395°F/201 °C, preferably between 240°F/116°C and 350°F/177°C, and most preferably between 250°F/121 °C and 286°F/141 °C. The curing time will vary depending on the particular components used and physical parameters such as the thickness of the layers, however, typical curing times range from 15 to 60 minutes, in particular 18 to 25 minutes. The invention is further described in the following nonlimiting examples. EXAMPLE 1 Clearcoat compositions A-F were prepared according to the following formulations. Compositions A and D served as controls. TABLE 1 A waterbome silver metallic anionically stabilized polyester based basecoat was sprayed onto 12730.48 cm by 18 45.72 cm electrocoated steel panels (APR17438) from ACT of Hillsdale, Ml. The basecoat film build varied from .2mil/5.08μm at the top of the panel to 1.4 mil/35.56μm at the bottom of the panel while the clearcoat film build varied from 1.0/25.4μm at the left side of the panel to 2.0/50.8μm mil at the right sideof the panel. The basecoat was dried for 5 minutes at 120°F/48,9°C followed by application of a clearcoat 1 The resin was a carbamate functional acrylic resin made according to US Patent 5,356,669. 2 The melamine was a monomeric methylated melamine sample The clearcoats were flashed for 5 minutes at ambient and baked for 20 minutes at 270°F/132,2°C Panels A,B,C,D, respectively containing Zn(CI0 4 ) 2 , AI(CI0 4 ) 3 and DDBSA showed wrinkling Panel E did not show any wrinkling Panel F showed wrinkling in that portion of the wedge having thick basecoat and thin clearcoat Example 2 Clearcoat compositions G-L were prepared according to the following formulations Composition K was the control The effect of an amine based blocking agent on catalysts was studied 30 grams of solutions G-T of Table 2 were individually added to 575 grams of Ureclear® clearcoat 3 (made without catalyst) to make clearcoat compositions G-T The blocking agent was Adogen 188, commercially available from Sherex Chemical of Dublin, Ohio Clearcoat compositions G-T were reduced to an initial viscosity 4 of 35 sec using 16 grams of oxo-hexyl acetate (OHA) Stability was evaluated by measuring change in color, i e , the degree of yellowing, and change in viscosity after 16 hours at 140°F/60°C The results are set forth in Table 2 3 A commercially available solvent borne carbamated acrylic/melamine based clearcoat sold by BASF Corporation Southfield, Ml 4 All viscosities measured at 80°F/26 6°C on a #4 Ford cup Table 2 The sample panels were prepared in accorance with Example 1 The results are set forth in Table 3 3 1= Best 10 = Worst 6 13 5 g of DDBSA was added to 600 grams of the above noted solvent borne carbamated acrylic/melamine clearcoat 7 13 5 g of PAP was added to 600 grams of the above noted solvent borne carbamated acrylic/melamine clearcoat Table 3 8 1=Best, 10=Worst 9 Tukon Hardness in Knoops according to ASTMD1474 10 Humιdιty test according to Ford Motor Co Test method FLTM Bl 4-2 11 Quantιtatιve assessment of reactable carbamate functionality present in the clearcoat - the smaller the number, the greater the degree of cure 12 Thιs result is believed to be an anomaly and is not illustrative of the normal behavior of a control sample Panels P, Q, & R, and M, N, & 0 (respectively aluminium perchlorate and zinc perchlorate at varying levels of blocking agent) showed wrinkling at low clearcoat film builds/high basecoat film builds. Panels containing aluminium nitrate and zinc nitrate did not wrinkle. The lack of wrinkling in control S is unusual and is considered an anomaly which may be attributable to basecoat film build, flash time of the basecoat, and/or heat up rate of the panel relative to oven position, etc. All of the films cured but the lower the amount of blocking agent, the harder the coating. Example 3 Preparation of Al/DDBSA A five percent solution of aluminum isopropoxide in xylene was prepared by mixing 76 grams of xylene and 4 grams of aluminum isopropoxide. The mixture was heated to and 27.4 grams of Nacure® 13 5076 solution (70%) added. The resulting solution had a %nonvolatile of 21.6%. Preparation of AI/PAP A five percent solution of aluminum isopropoxide in xylene was prepared by mixing 76 grams of xylene and 4 grams of aluminum isopropoxide. The mixture was heated to and 14.6 grams of phenyl acid phosphate (mono) added. The resulting solution had a % nonvolatile of 12.91 %. 13 A commercially available solution of DDBSA in n-butyl alcohol from King Industries of Norwalk.CT. Preparation of Clearcoat Compositions The selected catalysts of the following formulations were added to 500 grams of Ureciear® clearcoat 14 made without catalyst to produce clearcoat compositions U-X The samples were reduced to a final viscosity of 31 -35 sec on a # 4 Ford cup with a 50/50 blend of OHA/Methyl Isomyl Ketone Table 4 The appearance test panels were prepared by spraying the silver anionically stabilized waterbome polyester based basecoat of Example 1 onto ecoated 10" /25 4cm x 10725 4cm steel panels (APR26073) obtained from ACT of Hillsdale, MT The basecoat film builds were approximately .3/7 62μm to 7/17 78μm mils The basecoat and clearcoat samples were otherwise applied as indicated in Example 1 Cure properties were evaluated using ecoated 4 10 16 cm x 12730 48 cm steel panels, followed by application of a polyester acrylic melamine thermoset primer surfacer at a film build of about 1 0 mιl/25 4μm The primer surfacer was baked for 20 minutes at 300°F/148 88°C The basecoat and clearcoats were then applied and cured as indicated for the appearance panels. 14 A commercially available solvent borne carbamated acrylic/melamine based clearcoat sold by BASF Corpration, Southfield, Ml. 15 Except for samples U and V, these solutions had the % NV indicated in Example 3. 16 Viscosity taken on a # 4 Ford cup, at 80°F/26.6°C The results are set forth below in Table 5. Table 5 Tukon Hardness for the clearcoat and the basecoat/clearcoat was measured according to ASTM D1474. Sample U with an aluminium/DDBSA salt shows improvement over the DDBSA control (W) with respect to wrinkling. All panels displayes passing adhesion.

Claims: WHAT IS CLAIMED IS: 1. A method for providing a composite coating having an improved appearance, comprising: applying a first coating to a substrate; applying a second coating to the first coating to provide a composite coating, the second coating comprising, (A) a film forming component comprising (a) a first component comprising a compound having appended thereto at least one carbamate or urea functional group, or a group convertible to a carbamate or urea group, and (b) a second component comprising a compound reactive with said carbamate or urea groups on component (a), and (B) a wrinkle reducing catalyst comprising a compound of the formula: M y (L) x wherein M is a metal having an empty or full d orbital wherein the pk a of the aqua ion of M is less than or equal to 12, L is a ligand wherein the pk a of the parent acid is > -10 and is < 4, x is an integer which is a multiple of the charge of M, y is an integer which is a multiple of the charge of L. x and y selected so that ML is charge balanced, and subjecting the composite coating to a temperature between about 200°F/93°C to 3395°F/200°C for a time sufficient to provide a cured composite coating. 2. The method of claim 1 wherein first component (a) comprises a compound selected from the group consisting of oligomers having appended thereto more than one functional group selected from the group consisting of carbamate groups, urea groups and groups subsequently converted to carbamate or urea groups, said oligomers having a molecular weight of between 148 and 2000, and/or polymers having appended thereto more than one functional group selected from the group consisting of carbamate groups, urea groups and functional groups convertible to carbamate or urea groups, said polymers having a molecular weight of greater than 2000, and mixtures of said polymers and oligomers. 3. The method of claim 2 wherein said first component (a) comprises a carbamate or urea functional polymer selected from the group consisting of polyester, epoxy, alkyd, urethane, acrylic, polyamide and polysiiane polymers and mixtures thereof. 4. The method of claim 3 wherein first component (a) comprises a polymer backbone having appended thereto more than one carbamate functional group, said first component being represented by randomly repeating units according the formula: ^CH 2 -CR(CO-0-U-=-CO-NHR) - x -( A ^ R represents H or CH3, R' represents H, alkyl, or cycloalkyl, L represents a divalent linking group, in particular a divalent linking group of the formular -COOL', where L' is a divalent linking group A represents repeat units derived from one or more ethylenically unsaturated monomers, in particular acrylic monomeres x represents 10 to 90 weight %, and y represents 90 to 10 weight %. 5. The method of claim 4 wherein A represents repeat units derived from more than one ethylenically unsaturated monomers, more than one monomer having appended thereto a carbamate group. 6. The method of claim 4 or 5 wherein 10-90% of said ethylenically unsaturated monomers are acrylic monomers. 7. The method of any one of the claims 1 to 6, wherein film forming component (A) further comprises (b) a second component comprises a compound selected from the group consisting of melamine formaldehyde resins, urea resins, polymers having acrylamide groups, polymers having methylol or alkoxymethyl groups, polyanhydrides and polysiloxaπes, in particular a compound selected from the group consisting of melamine formaldehyde resins and urea resins. 8. The method of any one of the claims 1 to 7, wherein wrinkle reducing catalyst (B) comprises a compound of the formula: wherein M is a metal having an empty or full d orbital wherein the pk a of the aqua ion of M is less than or equal to 10, L is a ligand wherein the pk a of the parent acid is > -2 and is < 2, and x is an integer which is a multiple of the charge of M, y is an integer which is a multiple of the charge of L, x and y selected so that ML is charge balanced. 9. The method of claim 8, wherein wrinkle reducing catalyst (B) comprises Zn(N0 3 ) 2 . 10. The method of any one of the claims 1 to 9, wherein the second coating further comprises (C) one or more solvents, (D) additives, and (E) optionally, pigments. 11. The method of claim 1 wherein the first coating is a pigment containing basecoat, in particular a water borne pigment containing basecoat. 12. The method of any one of the claims 1 to 11 wherein the second coating is a solvent borne coating in particular clear coating. 13. The method of any one of the claims 1 to 12 wherein the second coating further comprises a catalyst (B) further comprising decylbenzenesulfonic acid. 14. The method of any one of the claims 1 to 13 comprising subjecting the composite coating to a temperature between 200°F/93°C and 95°F/201 °C, in particular to a temperature between 240°F/116°C and 350°F/177°C for a time between 18 to 25 minutes. 15. The method of claim 1 wherein the first coating is not cured prior to the application of the second coating. 16. A curable coating composition comprising, (A) a film forming component comprising (a) a first component comprising a compound having appended thereto at least one carbamate or urea functional group, or a group convertible to a carbamate or urea group, and (b) a second component comprising a compound reactive with said carbamate or urea groups on component (a), and (B) a wrinkle reducing catalyst comprising a compound of the formula: M y (L) x wherein M is a metal having an empty or full d orbital wherein the pk a of the aqua ion of M is less than or equal to 12, L is a ligand wherein the pka of the parent acid is > -10 and is < 4, and x is an integer which is a multiple of the charge of M, y is an integer which is a multiple of the charge of L, x and y selected so that ML is charge balanced.

Inventors: BRIGGS RODNEY, CAMPBELL DONALD, HARMON HERBERT, BRIGGS, RODNEY, CAMPBELL, DONALD, HARMON, HERBERT
Applicants: BASF CORP, BASF CORPORATION
Application year: 1999
Main classification: C09D5
IPC codes: B05D1, B05D7, C09D5, C09D201