SORBENT, METHOD FOR PRODUCING THE SAME AND USE OF THE SAME FOR IMMOBILISATION OF HEAVY METALS AND PHOSPHATES

Abstract: This invention is dealing with a method for producing a sorbent for removing and immobilisation of cations of the heavy metals and/or phosphates in contaminated solids and/or liquids. The sorbent according to this invention is a composite granular material consisting of a carrier of schistous nature or related to the wastes from coal dressing, an active component - thermally modified dolomite with a high content of MgO.CaCO3, and a binding agent - preferably cement. First of all, carrier and an active component with grain's size less than 0.2 mm are mixed together; then cement is added and a dry three-component mixture with a composition given by the mass ratio (carrier):(active component):(binder)=(1.3 to 4.3):(1.0 to 1.3):(1.0 to 1.5) is prepared. After adding a certain amount of a water, a mass of paste-like consistency with a composition given by the mass ratio (solids):(water)=(1):(0.38 to 0.60) is obtained. The latter one - after previous setting and hardening (3 to 10 days) - is crushed and screened into fractions with defined grain size, preferably (1.0 to 3.0), (0.3 to 1.0) and (0.0 to 0.3) mm. Grading of used sorbent is determined by its assumed application for purification of contaminated solids or liquids. The sorbent according to this invention is used as a filter body (matrix) material for purification of contaminated liquids in dynamic conditions, as an additive to contaminated liquids in settling tanks in static conditions, or - in a pulverized form - as an additive for removing and immobilisation of the heavy metals and/or phosphates in contaminated solids.

Description: SORBENT, METHOD FOR PRODUCING THE SAME AND USE OF THE SAME FOR IMMOBILISATION OF HEAVY METALS AND PHOSPHATES Technical field of the invention This invention relating to a composite sorbent of inorganic nature and method for producing the sorbent, and particularly to use of the same for removing and immobilisation of cations of the heavy metals and/or phosphates from contaminated aqueous, or soils, sediments or solid wastes (sludges). Background art of the invention Various sorbents functioning on a principle of cation exchange (ion exchangers) such as natural zeolites or alurnino-silicates with a very low sorption capacity are known and commonly used in practice. These materials are mostly selective either to individual ions or to particular classes of ions, and their sorption capacity can be exhausted very quickly after reaching the equilibrium. Many natural materials functioning on principles of ion exchange, physical adsorption or chemisorption can be used only in a powder-like form. Finely milled, powdered organic materials, powdered coal, bentonite, various clays, natural zeolites, coal ashes or slags are typical representatives of the latter class of sorbents. However, these materials cannot be directly used as the filter body (matrix), have a very low sorption capacity, and flocculation and separation of these fine materials from contaminated water by filtration after their active service life may cause serious problems in an actual technological process. Also a very efficient method for fixation of cations of the heavy metals, directly using lime or portland cement is known. However, the application of this direct method is limited by some technical problems (e.g. using lime or portland cement as the filter body (matrix) material and, from a chemical point of view, very high pH values reached in the system can lead to repeated dissolution of precipitated salts. The term sorbent is used herein this invention for any representative of the class of materials characterised by their ability to immobilise cations of the heavy metals and or phosphates by absorption, adsorption or chemisorption, or by any other mechanism. The sorbent is able to change pH in the system, to act as a buffer at the solid-contaminated liquid interface and to precipitate cations of the heavy metals in the bulk liquid. This is accompanied by formation of hydroxysalts, hydrated oxides or hydroxides of individual heavy metals, resulting in a physico-chemical fixation of a part of precipitated metal cations on a rough surface of the porous sorbent. Technical solutions using adsorbents for fixation of cations of the heavy metals are referred to in the patent Uterature (PCT WO 93/16797): the adsorbent consists of complexes created by smectites (minerals of the montmorillonite group), aluminium hydroxide and a phosphate, functioning at pH values of about 5 to 6. This adsorbent is dried at temperature of 40°C and used in form of a powder; in filters it is used in combination with fibrous or granular body (matrix)-forming materials. This adsorbent can be mixed with contaminated soils to immobilise cations of the heavy metals, as well. Form in which the heavy metals are present in the contaminated soil can be changed by this method in such a way, that biological accessibility of the cations for plants is dramatically reduced - hence, such soils can be assumed to be purified. Values of the effectiveness of immobilisation between 74 and 82 % can be reached by this method. Because of their relatively low permeability for an aqueous phase, adsorbents based on soils (clay minerals) can be rather used as sealing materials (passive inhibition) than the filter body (matrix). The principle of another known technical solution of this problem (WO 94/06717) is as follows: a contaminated aqueous phase is brought into contact with particles of an inert carrier (mineral grains or iron particles) of diameter 0.1 to 2.5 mm, with density lg.cm "3 , in presence of dissolved ferrous ions (Fe 2+ ) and a gaseous oxidising agent (oxygen or ozone), at pH between 2.5 and 8.5. The surface of carrier particles, which are suspended in an agitated purified aqueous phase, is activated by adsorption of ferrous ions from the liquid phase, which consequently results in more intensive fixation of other metal cations - including also cations of the heavy metals. This adsorbent and method of its application are appropriate to purification of waters containing iron as well as those with high contents of chromium. Flowing rate of the aqueous phase used was 3 m/h ( meters per hr) at filtration capacity approx. 24 1 h ( litres per hr). This method can be also used to remove arsenic from contaminated waters. However, it does not deal with a complex removal or fixation of the most of cations of the heavy metals and requires special technological equipment: a reactor keeping the carrier particles in a whirling motion through an aqueous phase, supplied by inflows of ferrous ions and an oxidising agent. This method can't be used neither for consolidation, nor for purification of contamined soils, sludges or sediments, i.e. for purification of contaminated solids. T e most related known solution of the problem is the method for preparing an active absorbing material (EP 0337 047 Al). This material is produced by roasting of alurnino-silicates at moderate temperatures between 350 and 800°C using a static oxidising (air or oxygen) atmosphere. Final contents of residual mineral coal admixtures (including dolomites or slaty materials) in these thermally modified alurnino-silicates are min. 17 wt. %. Formaldehyde-urea or an aqueous suspension of another appropriate binder (e.g. 10 wt. % of cement) is then continuously added in small amounts to the fine burned aluminosilicate. An adsorbent commercially known as „Beringite" can be prepared by this method. Altered Westphalian schists which are used as the raw-materials for producing this adsorbent undergo severe changes after being heated up to 800°C - most of minerals are converted to a, so called, X-ray amorphous phase. Active components of this class of adsorbents are products of thermal decomposition of carbonates such as calcite, dolomite and siderite. The adsorbent is usually applied in two forms: coarse (grain size about 1 to 2 mm) and fine (grain size minus 1 mm - so called „aqueous Beringite"). Very fine adsorbent (grain size minus 0.25 mm - so called „soil Beringite") is used for remediation of soils. Chemical reactions such as neutralisation and precipitation play the key role in removing and/or immobilisation of cations of the heavy metals using „Beringite" adsorbent. Also a method for producing an improved „Beringite" is available in the literature (EP 0455 621 Al). Values of the sorption coefficient of a schistous material containing alurnino-silicates can be increased by the addition of cement as a binder and/or aluminium metal powder or aqueous suspension containing aluminium, by the addition of hydroxides to the mixture to adjust the pH value between 10 and 14, and by hydrothermal processing at temperatures 70 to 120°C during several hours. Alternatively, a certain amount of aqueous solution of sodium silicate can be added. Improved Beringite can be used in industrial applications as a material for the filter body (matrix) for filtration of contaminated waters in amounts from 1,500 up to 1,800 the body volumes (V/V 0 ), reaching the standards of purity. All above mentioned non-composite sorbing materials are selective and can be applied only as additives. They are not suitable to be used simultaneously as active components and as granular, filter body (matrix) forming material carriers in purification of contaminated liquids, and as pulverised additives for immobilisation of cations of metals in solids. Main disadvantages of sorbents of Beringite type are as follows: schistous (slaty) raw-materials are not commonly available and they must be thermally treated at temperatures up to 600 or 800 °C to increase their specific surface as well as their buffering capacity, what results in serious technical and energetical requirements. Also additions of various special components, e.g. aluminium metal, sodium silicate or calcium hydroxide have to be used and the mixture must be consequently processed hydrothermally to reach higher efficiency of removal of cations of the heavy metals. Serious technical and economical requirements make this method disadvantageous for producing the sorbent. Disclosure of the invention Disadvantages of all known methods discussed in previous paragraphs can be in a great extent eliminated using the solution according to this invention. It is relating to a composite sorbent for 100 removing and immobilisation of heavy metals and/or phosphates in contaminated liquid and solid phases. A granular composite sorbent according to this invention is prepared by mixing a body forming component - ( carrier ) related on its origin to natural schists and/or wastes from coal dressing, with an active component - thermally modified dolomites with high contents of MgO.CaC0 3 and a binding agent ( binder) in the mass ratio = (1.3 to 4.3):(1.0 to 1.3):(1.0 to 1.5). A mixture prepared by this way is 105 further processed by physico-mechanical methods to obtain a composite sorbent with defined grain size for various applications in purification of contaminated solids or liquids. The method for producing a composite sorbent according to this invention is characterised by mixing natural schists and/or wastes from coal dressing, representing the carrying component (carrier), with thermally modified dolomites with high contents of MgO.CaC0 3 , representing the active 110 component. First of all, these two major components are crushed and/or milled individually or together to reach a grain size minus 0.2 mm. In a further step, a binding agent ( binder) is added to this originally two-component mixture in an appropriate amount, to reach the mass ratio the carrier : the active component : the binder = (1.3 to 4.3):(1.0 to 1.3):(1.0 to 1.5). Consequently, a water is added in the ratio S : L = 1: (0.38 to 0.60) and a mass of paste-like consistency (so called cement mortar) is prepared. After 115 a short setting period and 10 days of ageing, the hardened cement mortar is crushed and/or milled and sorted to fractions with defined grain size for various applications in purification of contaminated solids or liquids. The most important raw-materials for producing the body forming component (carrier) of the sorbent include various natural schistous raw-materials such as sericitic chlorite schists or black shales (e.g. those 120 of upper triassic age of Reingraaben type or from Mariathaal deposit), or tails from coal washing and/or dressing which are available at waste disposal sites, or combinations of these raw-materials. Alternatively, also other natural materials such as tuffs, sandstones, clays, kaolines or diatomites, or their combinations can be used for the latter purpose. As an active component for preparing the sorbent according to this invention, thermally modified 125 (calcined) dolomite prepared by burning of natural dolomites to the first stage at temperatures about 720 to 750 °C using static conditions can be preferably applied. Alternatively, also a calcined dolomite prepared by burning of natural dolomites at temperatures about 750 to 780 °C using dynamic conditions can be used. As a binding agent for preparing the sorbent according to this invention, a portland cement (PC) - 130 preferably a white one is used. The sorbent according to this invention in its final form can be obtained by crushing and/or milling of the hardened cement mortar, followed by sorting the crushed/milled material to fractions with defined grain size - preferably = (1.0 to 3.0), (0.3 to 1.0) and (0.0 to 0.3) mm - for various applications in purification of contaminated solids or liquids. 135 When the sorbent according to this invention is applied to remove and immobilise cations of the heavy metals and/or phosphates from a contaminated liquid phase, the sorbent is used as a filter body (matrix) with a contaminated liquid phase passing through it. Certain amounts of this sorbent with defined grain size can be also added to a contaminated liquid phase into the settling tanks before the filtration. 140 When the composite sorbent according to this invention is applied to immobilise cations of the heavy metals and/or phosphates in a contaminated solid phase ( i.e. soils), certain amount of a pulverised sorbent is mixed with a contaminated solid before its disposal to limit possible washing-out of hazardous species specified above at a waste disposal site. 145 Examples of carrying out the invention The raw materials for producing the sorbent have been chosen after analysing the results of preliminary tests and belong to one of the following groups: • the raw-materials which are a source of an „active component" of the sorbent; • the raw-materials offering the body forming component, i.e. the carrier (so called skeleton or 150 matrix) of the sorbent; and • binding agents used to keep both major components specified above together. This invention is relating to a non-thermal method for preparing a composite sorbent. The method according to this invention assumes the addition of such a binding agent to the mixture of the body forming ( carrier) and active components, which can ensure an appropriate strength of both dry and 155 wet sorbent, and which can bring a synergic effect resulting in an improved functioning of active components. In examples presented in this invention, schistous natural materials and waste materials from coal-dressing were used as major raw-materials for preparing the body forming component. Schists from the Slovak deposits in Raztoka, Marianka and Hnilcik were used as well as a solid waste material from 160 coal washing and dressing, coming from a waste disposal site in Handlova, Slovakia. Though the latter one being different in nature, it contains tufrϊtic-clayey and organic components, and can be alternatively used instead of schists for producing of the carrying component of the sorbent according to this invention. Thermally modified (semi-calcined) dolomite from Hubina deposit, Slovakia was used as an active component, because it offered the best results. Semi-calcined dolomite (SCD) can be prepared by 165 burning of natural dolomite to the first stage at temperatures 750±30°C. SCD with grain size about 2 to 11 mm obtained by this method is of high purity and its typical mineralogical composition is as follows: calcite (CaC0 3 ) = approx. 70 %, periclase (MgO) = 28 %, residual dolomite = 1 % and less than 1% of silicates (coming mostly from schists, quartz and feldspar, and containing Si0 2 , AI2O3, Fe 2 0 3 , etc.). Calcite and residual dolomite contents were determined by manometric analysis of milled product. SCD 170 with grain size 2 to 11 mm was consequently crushed, milled and screened (3-stage crusher, vibrating mill, vibrating screen) to a grain size minus 0.2 mm, and this final material has been used for producing the composite sorbent. Black shales, namely those of „Lunz" type (BS) seem to be - according to their simple mechanical treatment (milling), relatively low content of the heavy metals and an appropriate content of 175 organic compounds - the best raw-materials for producing of the carrying component. Bulk density of the wet and dry rock is approx. 2,545 kg.m "3 and 2,050 kg.m "3 , respectively. Portland cement has been used as a binding agent for preparing the composite sorbent by method according to this invention. Along with its binding effect, portland cement also partially acts as an active component (due to calcium silicates, calcium aluminates and/or small amounts of free lime present). 180 Generally, it is possible to use any portland cement of grade equal to 350 or more. However, white cement is preferably used, because it is ecologically more acceptable and neither chromium nor other heavy metals are present in amounts typical for ordinary portland cements. White portland cement (PC) produced by Hirocem Rohoznik, Slovakia was used in examples presented in this invention. Mineralogical and chemical composition of the raw-materials specified above was determined 185 using methods of X-ray diffraction and chemical analyses. The results are summarised in Tables 1, 2 and 3. Table 1: Chemical and mineralogical composition of the used active component 190 (semi-calcined dolomite) Table 2: Chemical and mineralogical composition of the raw-materials used for preparing the body forming component ( carrier) 195 Table 3: Chemical and mineralogical composition of the used binding agent (white portland cement) In the examples presented in the invention, two different mixtures of major components (Mixture 1 and Mixture 2) were used for preparing the granular composite sorbent. The composition of Mixture 1 and Mixture 2 was as follows: Mixture 1 = BS (50 %) + PC (30 %) + SCD (20 %), Mixture 2 = CH (50 %) + PC (30 %) + SCD (20 %), where: BS = black shales; CH = waste material from brown Handlova coal dressing; PC = (white) portland cement; SCD = semi-calcined dolomite; and Figures in brackets correspond to contents of individual components in wt. %. Example 1 In this example, the sorbent according to this invention was prepared, using various kinds of raw- materials. Individual raw-materials were treated separately: they were crushed using a three-stage crusher, milled in a vibrating mill and screened on a vibrating screen, and major components with grains smaller than 0.2 mm were obtained. To prepare Mixture 1, BS and SCD were mixed together and then white portland cement (PC) was added to this two-component mixture. Mixture 2 was prepared in the same way, just CH - instead of BS - was used. By adding water to each of the three-component mixtures of solid raw-materials in amounts corresponding to the mass solid : water ratio (S : L) = 1.25 to 2.0, mass of 220 a paste-like consistency, so called cement mortar, was prepared. This cement mortar was moulded by various methods to prepare briquettes, bricks (shaped bodies) or pellets. These were, during further period of ageing (7 days), periodically sprayed with water. After setting, hardening and drying, the materials were crushed in 2 or 3 stages and screened, and three kinds of grains - 1 to 2.5 mm, 0.3 to 1 mm and below 0.3 mm - were prepared for Mixture 1 and Mixture 2. Since the same crusher and screen were 225 applied, the grain size distributions of Mixture 1 and Mixture 2 were rather similar - Table 4. Chemical and mineralogical composition of both mixtures are summarised in Table 5. Table 4: Grading of the used sorbent Note: For purification of contaminated aqueous phase in dynamic conditions, also screens with hole diameter 0.25, 0.315 or 0.35 mm - instead of 0.3 mm - can be used for screening of the sorbent, 230 according to the nature of the filter body (matrix) applied. Table 5: Mineralogical composition of the used composite sorbent Explanations to Table 5; * * Fylosilicates = chlorite + sericite + illite (Mixture 1) or montmorillonite + sericite + illite + calcite (Mixture 2); 235 „+" = stands for traces up to 0.X % mineral content; Volcanic tuff = amorphous phase of volcanic origin (volcanic glass, ash, etc.); Organic phase = finely distributed organic carbon and organic species (Mixture 1), or finely distributed coal and related organic components (Mixture 2). 240 Properties of the sorbent according to this invention are specified in more details in the following examples (Examples 2 to 4). Methods for preparing the sorbent and its apphcations for removing and fixation of the heavy metals from model solutions of copper (Cu 2+ ), zinc (Zn 2+ ), lead (Pb 2+ ), cadmium (Cd 2+ ), mercury 0^Ig 2+ ), iron (Fe 3+ ), manganese (Mn 2+ ) and phosphates ( PO , " ) in static and dynamic conditions are presented; results of tests carried out in static conditions are summarised in Table 6. 245 It can be also seen from Table 6 that samples of the composite sorbent with additions of natural zeolite into Mixture 1 were tested for their ability to remove ammonium cations (NH 4 ) from contaminated solutions. 250 255 Table 6: Removal of individual ions from model contaminated solutions by using selected samples of the sorbent and a comparative sample of Beringite in static conditions 260 Note: A modified sorbent according to this invention was used for testing its ability to remove ammonium cations fNH * For its preparation, a part (20 %) of black shales (BS) was substituted bv natural zeolite. Example 2 265 In this example, the composite sorbent according to this invention with grain size 1.0 to 3.0 mm was prepared. Its composition (in wt. %) was as follows: black shales (BS) 50 %, white portland cement (PC) 30 %, thermally modified dolomite (SCD) 20%. Water in amounts corresponding to the ratio S: L = 1.25 was added to prepare a cement mortar. After a certain ageing period (about 7 days), hardened dry mass was crushed and screened to three fractions. In further experiment, 15 ml of composite sorbent 270 with a grain size about 1.0 to 3.0 mm were used as the filter body (matrix). A model solution with Cu 2+ concentration 9 mg.l '1 has been passed up-stream through a column; an average rate it was passing the filter body (matrix) was 2.76 m.h "1 . For a total amount of purified solution V/V 0 = 267 (filter body volumes = V 0 ) the effectiveness of Cu 2+ ions removal was 97 rel. %. Concentration of Cu 2+ ions in a purified solution was found to be 0.29 mg.l "1 . An average filter load was 18 V/V 0 .h "1 - this corresponds to 275 the value 2.76 πrlm '2 .!- "1 . Example 3 In this example, the composite sorbent was prepared by the same method as in Example 2. The only difference was, that 50 % of a dry waste material from brown Handlova coal dressing (CH) - instead 280 of black shales - has been used as a carrier. As in the previous example, the carrier was mixed together with 30 % of portland cement (PC) as a binder and 20% of thermally modified dolomite (SCD) as an active component. Water in amounts corresponding to the ratio S : L = 2.0 was added to obtain a cement mortar. After setting and hardening (cca 10 days), dry mass was crushed and screened, and a composite sorbent with grain size about 1.0 to 3.0 mm was prepared for further tests; in each of them 15 ml of this 285 sorbent were used as a filter body. Model solution with Cu 2+ concentration 8.7 mg.l "1 has been passed upstream through a column. For a total amount of a purified solution V/Vo = 267, concentration of Cu 2+ ions in a purified solution was 0.106 mg.l '1 . The effectiveness of Cu 2+ ions removal was found to be 98.8 rel. % at an average filter load 12 V/Vo .h "1 , corresponding to the value 1.84 m 3 .m "2 .h "1 . 290 Example 4 Sorbent according to this invention and a solution with content of PO 3 ^ ions were mixed together in static (batch) conditions in a ratio 1 g of the sorbent per 1000 ml of solution. Both phases were agitated for 60 min. and consequently separated by filtration. It was found out that concentration of PO 3 ^ ions decreased from its initial value 9.7 mg.l "1 to a final one 0.01 to 0.16 mg.l "1 , and values of the 295 effectiveness of PO ions removal from 98.3 to 99.9 rel. % have been reached. Example 5 A sorbent according to this invention and model solutions with concentrations of Cu 2+ ions between 10.52 and 91.68 mg.l "1 were mixed together in static (batch) conditions in a ratio 1 g of the 300 sorbent per 1000 ml of solution. Both phases were agitated for 60 min. and consequently separated by filtration. Contents of Cu 2+ in purified solutions were found to be 0.103 to 16.227 mg.l "1 Cu 2+ , in dependence of an initial value of the Cu 2+ concentration, i.e. the content of Cu 2+ ions in purified solutions has been reduced by 99.02 to 82.3 rel. %. In some comparative tests carried out in the same conditions with Beringite. typical values of the effectiveness of Cu 2+ ions removal between 61.69 and 22.02 rel. % 05 were reached. Example 6 Tests were carried out with model solutions containing zinc. Initial concentrations of Zn 2+ ions varied from 10.90 to 105.40 mg.l "1 and these solutions were treated in the same way as those in the 10 previous example, using sorbent according to this invention. It was found out that contents of Zn 2+ ions in purified solutions were reduced by 99.42 to 60.92 rel. %., with values of the Zn 2+ concentration in purified solutions being inversely proportional to the initial ones. Example 7 315 A set of comparative tests was carried out in this experiment to compare: • effects of the method used for preparing the sorbent on absorbing capacity of the sorbent; and • the sorbent according to this invention with an absorbent of Beringite type. A composite sorbent with composition according to this invention was prepared in two forms: as pellets (form A) and granules (form B). 320 Sorbent A with pellet size 0.2 to 5 mm was prepared from a mixture containing 50 % of a carrier (BS and/or CH), 30 % of a portland cement (PC) and 20 % of a semi-calcined dolomite (SCD). First of all, dry mixture of raw-materials was finely sprayed with a water to prepare wet pellets. After setting and hardening (cca 5 days), the pellets were ready for further application. Sorbent B in a granular form according to this invention was prepared from a mixture containing 325 50 % of a carrier (BS and/or CH), 30 % of a portland cement (PC) and 20 % of a semi-calcined dolomite (SCD). A granular material with defined grain size was obtained by consequent crushing of these raw- materials and mixing them together, and by the addition a certain amount of a water to the dry mixture to obtain a cement mortar, which was crushed after ageing, and screened. A composite sorbent with typical grain size about 1.0 to 2.5 mm was prepared by this method. 330 Samples of individual sorbents were used for purification of model solutions with content of a copper and zinc in static (batch) conditions - the results are summarised in Table 7. These results can be compared with those reached by using a comparative sample of the Beringite with grain size 1 to 2 mm (so called „aqueous Beringite" prepared from alurnino-silicates by thermal methods). 335 Table 7: Removal of Cu 2+ or Zn 2+ ions from contaminated model solutions by using samples of the sorbent (both forms A and B) and a comparative sample of Beringite in static conditions Highest values of the effectiveness of Cu 2+ and Zn 2+ ions removal (99 to 60 rel. %) were reached in those tests, where samples of the granular sorbent according to this invention (form B) were used. The 340 values for Zn 2+ ions were in all cases higher than corresponding values reached with form A of the sorbent (45 to 15 rel %), and much higher when compared with those reached with the Beringite absorbent. For comparison, values of the effectiveness of Zn 2+ ions removal for the Beringite absorbent were found to be only 25 to 10 rel. % in the same experimental conditions. Average values of effectiveness of the filter body prepared from the sorbent according to this 345 invention and used in dynamic conditions were 97 and 99 rel. % at lower and higher flow rates, respectively. Example 8 The sorbent according to Example 1 was tested for applications in purification of actual 350 contaminated aqueous solutions. The sorbent was used as a filter body in a continuous flow system. An actual waste solution from a plating shop doped with certain amounts of Cu and Pb salts, with chemical composition shown in Table 8, was used in this experiment. Table 8: Concentrations of the heavy metals in used waste solution 355 These tests were carried out using 400 mm long and 30 mm in dia. glass columns with filtering cloth (type LN 61) and settling tanks with volume 3 litres. Contaminated solution was pumped by a rotary pump up the top of a down-stream column and passed down in direction to the filtering cloth. Filter load was 15 V/Vo.hod '1 . The filter was regenerated each 30 min. by an up-stream washing and values up to 770 V/Vo-hod "1 were reached with the same filter body (matrix), i.e. without any change of the sorbent. 360 Using a periodic regeneration of the filter body (matrix) by washing, mechanical life times of order 1,500 V/V can be expected for this kind of granular sorbent. It was observed, that pH values of used solutions were from an interval between 12.8 and 8.7. The results documenting possibility of purification of such a waste solution by using the sorbent according to this invention in dynamic conditions are summarised in Table 9. 365 Table 9: Purification of a waste solution from a plating shop in dynamic conditions Industrial utilisation of the invention A composite sorbent produced according to this invention can be used for removal and 370 immobilisation of the heavy metals and/or phosphates both in liquids and solids. The following examples can be used to illustrate typical applications of this sorbent: 1. material for use as the filter body (matrix) with grain size 1.0 to 3.0 mm, occasionally also 0.3 to 1.0 mm, for purification and final cleaning of contaminated waste waters from cations of the heavy metals and/or phosphates in dynamic conditions; 375 2. pulverised additive with grain size less than 0.3 mm for purification and final cleaning of contaminated waste waters from cations of the heavy metals and/or phosphates, which can be consequently separated from a purified aqueous phase in two stages: (i) by sedimentation or, occasionally, by flocculation and sedimentation in settling tanks, and (ii) by filtration, using a mechanical filter (e.g. a sand filter); 380 3. an additive, mostly in a powdered form, with grain size less than 0.3 mm for immobilisation of cations of the heavy metals and/or phosphates in contaminated soils, sediments and solid wastes (sludges), which can limit washing-out of these hazardous species from the above mentioned contaminated solids. However, these examples do not limit other possible applications of the sorbent according to this 385 invention. 390

Claims: PATENT CLAIMS 1. Method for producing a composite sorbent for removing and immobilisation of cations of the heavy metals and/or phosphates in contaminated solids and/or liquids characterised in that a gradual (consequent or simultaneous) crushing andor milling of a carrier of schistous nature or 0 related to the wastes from coal dressing, and an active component - thermally modified dolomite with a high content of MgO.CaCOs - to grain size less than 0.2 mm; are mixing together; then are adding a binding agent to prepare a three-component mixture with a composition defined by the mass ratio (carrier) : (active component) : (binder) = (1.3 to 4.3) : (1.0 to 1.3) : (1.0 to 1.5); adding water to prepare a cement mortar with a composition given by the mass ratio 5 (solids) : (water) = (1):(0.38 to 0.60); crushing the dried cement mortar after its setting and hardening within 3 to 10 days, and sorting crushed material into fractions with defined grain's size, according to assumed applications of the sorbent for purification of contaminated solids or liquids. 2. Method for producing the sorbent according to claim 1 characterised in that using sericitic chlorite schists or black shales (e.g. those of upper triassic age of Reingraaben type or 0 from Mariathaal deposit) and/or tails from coal washing or dressing which are available at waste disposal sites, or combinations of these materials as raw-materials for preparing a carrier of the sorbent. 3. Method for producing the sorbent according to claim 1 characterised in that using tuffs, sandstones, clays, kaolines or diatomites, or combinations of these materials as raw- 5 materials for preparing the carrier of the sorbent. 4. Method for producing the sorbent according to claim 1 characterised in that using semi-calcined dolomite - obtained by burning of a natural dolomite to the first stage at temperatures 720±30°C in either static or dynamic conditions - as an active component of the sorbent. 0 5. Method for producing the sorbent according to claim 1 characterised in that using portland cement, preferably white portland cement, as a binding agent. 6. Method for producing the sorbent according to claims lto5 characterised in that sorting crushed hardened cement mortar into, at least, three fractions, namely (1.0 to 3.0), (0.3 to 1.0) and (0.0 to 0.3) mm. 425 7. Sorbent for removing and immobilisation of the heavy metals and/or phosphates in contaminated liquids or solids characterised in that a method for its producing according to the previous claims, was prepared as a composite granular material consisting of : > a carrier (body forming) component of schistous nature and/or the wastes from coal dressing, > an active component - thermally modified dolomite with a high content of MgO.CaC0 3 , and 430 > a binding agent - preferably cement , where the main components and agent are in the defined mass ratio: (carrier):(active component):(binder) = (1.3 to 4.3) : (1.0 to 1.3) : (1.0 to 1.5), with defined grain's size, according to assumed applications of the sorbent for purification of contaminated solids or liquids. 435 8. Method for removing and immobilisation of the heavy metals and/or phosphates in contaminated liquids characterised in that using the sorbent according to claim 7 in defined grain's size of (1.0 to 3.0) mm and/or (0.3 to 1.0) mm as a filter body (matrix material) in dynamic systems. 9. Method and immobilisation of the heavy metals and/or phosphates in contaminated liquids characterised in that using the sorbent according to claim 7 in a powdered form with 440 the defined grain's size minus 0.3 mm as an additive to contaminated solutions, which can be consequently separated from the liquid phase by sedimentation, occasionally by flocculation and sedimentation in settling tanks before the final stage of water cleaning by filtration using a mechanical filter. 10. Method for removing and immobilisation of the heavy metals and/or phosphates in contaminated 445 solids characterised in that using the sorbent according to claim 7 in a powdered form with the defined grain's size mostly minus 0.3 mm as an additive to contaminated soils, sediments or solid wastes (sludges), which is mixed with contaminated solid phase before its disposal. 450

Inventors: KOREC STEFAN, KOREC, &SCARON
Applicants: IPRES INZINIERING S R O, IPRES IN&ZCARON
Application year: 1999
Main classification: C02F1
IPC codes: B01J20, B09C1, C02F1, C04B18