WOUND DRESSINGS AND MATERIALS SUITABLE FOR USE THEREIN

Abstract: Carboxymethylated cellulosic articles having degree of substitution in the range from 0.12 to 0.35 and in which the carboxymethyl groups are believed to be predominantly within the amorphous regions to the exclusion of the crystalline regions have usefully non-adherent properties as wound dressings. Such wound dressings may be made by carboxymethylating a cellulose fabric so that its absorbency is little greater after carboxymethylation than beforehand and the degree of substitution is as stated above. Carboxymethylation can be carried out by contacting cellulose II fibres or other articles with a solution containing sodium hydroxide, sodium chloroacetate, water and ethanol. The solution may contain from 4 to 8 percent by weight sodium hydroxide and from 50 to 60 percent by weight water (including water in the fibre) or the weight ratio of sodium hydroxide to water (including water in the article) may be from 0.095 to 0.115 and the weight ratio of cellulose in the article to water (including water in the article) may be from 0.22 to 0.28.

Description: WOUND DRESSINGS AND MATERIALS SUITABLE FOR USE THEREIN Field of the invention This invention relates to wound dressings, in particular to dressings in fabric form and other forms suitable as contact layers for exuding wounds, and to methods for the manufacture of such dressings and of materials for use therein. Commonly-used wound dressings include foams, sponges and fibre-based materials such as gauzes and waddings, for example of cotton or viscose rayon. Such fibre-based materials tend to adhere to the wound surface and are accordingly difficult to remove, after use, in one piece and without causing trauma to the patient. Known wound dressings also include advanced dressings based for example on alginates or on various kinds of hydrocolloids or hydrogels, but such dressings are relatively expensive and are accordingly used in general only when clinical needs so recommend. There exists a desire for wound dressings which possess at least some degree of absorbency, but which are sufficiently non-adherent that they are capable of being removed from a wound in a single piece without shedding fibre fragments and without trauma to the patient, and which are inexpensive in comparison with advanced dressings. Background art WO-A-94/16746 discloses a wound dressing in which the wound- contacting surface comprises carboxymethylcellulose (CMC) filaments capable of absorbing at least 15 times, preferably at least 25 times, their own weight of 0.9% by weight aqueous saline solution (as measured by a defined free-swell absorbency test) to form a swollen transparent gel, the thusly-swollen dressing retaining sufficient fibrous character to be removed as a coherent dressing from a wound. The degree of substitution (D.S.) of the CMC filaments is preferably at least 0.15, more preferably from 0.2 to 0.5, although it may be up to for example 1.0. The CMC filaments may generally be prepared by reacting cellulose filaments in the presence of strong alkali with chloracetic acid or a salt thereof. The cellulose filaments may be viscose rayon, cuprammonium rayon or cotton, but they are preferably solvent-spun and may accordingly be lyocell . WO-A- 95/19795 discloses a wound dressing which comprises a blend of textile fibres and gel-forming fibres. The textile fibres may be natural or synthetic but are preferably cellulosic fibres such as viscose rayon or cotton. The gel-forming fibres may for example be carboxymethylcellulose or alginate fibres. The gel-forming fibres can be of the type which retain their structural integrity on absorption of exudate or can be of the type which lose their fibrous form and become a structureless gel or a solution on absorption of exudate. The absorbency of the gel-forming fibre (measured by the free-swell met: od) is desirably at least 2 g/g of 0.9% saline solution, preferably at least 15 g/g, more preferably between 25 and 50 g/g. The D.S. of a carboxymethylcellulose fibre is desirably at least 0.05, preferably at least 0.2, more preferably between 0.3 and 0.5. Such dressings are said to have the advantage that the fibres they contain are not engulfed by new tissue formed during the healing process, so that they can be removed without causing wound injury. Disclosure of the invention According to a first aspect of the invention, there is provided a process for the manufacture of a wound dressing comprising the step of carboxymethylating a cellulosic fabric such that the absorbency (as defined hereinafter) of the fabric after carboxymethylation is no more than 3 g/g, preferably no more than 2.5 g/g, further preferably no more than 2 g/g or 1 g/g, greater than the absorbency (as defined hereinafter) of the fabric before carboxymethylation and such that the degree of substitution of cellulose by carboxymethyl groups in the carboxymethylated fabric measured by IR spectroscopy (as defined hereinafter) is m the range from 0.12 to 0.35, preferacly from 0.2 to 0.3. The invention also includes wound dressings which comprise 5 such carboxymethylated fabric . By the absorbency of the fabric, before and arter treatment, we mean the absorbency figures assessed by the method described m British Pharmacopoeia 1993, Addendum 10 1995, page 1706 for Algmate Dressings, but with substitution of the fabric under test for the algmate specified therein, which method yields absorbency m terms of weight per unit area, and then converted to absorbency m terms o weight ratio (g/g) . 15 The cellulosic fabric preferably consists solely cf cellulosic fibre but may contain a proportion ot non cellulosic textile fibre or of gel-forming fibre. 'ne cellulosic fibre is of known kind and may be a natural fibre such as cotton or a manmade fibre such as lyocell or viscose 20 rayon, blends of such fibres may be used. We have observed that dressings according to the invention made from cellulosic fibres of low wet strength such as viscose rayon may tend to shed fragments when wetted, and accordingly use of such fibres is generally less preferred. The celJuLoεic 25 fabric may comprise continuous filament yarn and/ox staple fibre A fabric of continuous filament yarn may be preferred, on the ground that such fabrics are less liable to shed fibre fragments on handling or on removal from a wound. We have nevertheless surprisingly found that 30 dressings according to the invention composed of staple fibres have a low tendency to shed fragments. The cellulosic fabric s of known kind and may oe made m known manner. The basis weight of the fabric is generally m the range from 30 to 250 g/m 2 . The cellulosic fabric may 35 be a woven or knitted fabric or a nonwoven fabric such as a hydroentangled fabric or a needlefelt . A nonwoven fabi'ic should be of sufficiently robust construction - for example, having sufficiently high fibre entanglement - that the carboxymethylated fabric after absorption of aqueous liquors possesses sufficient mechanical integrity to permit it to be removed from a wound in a single piece. The carboxymethylation step is generally performed by- contacting the fabric with strong alkali, for example sodium hydroxide, and a carboxymethylating agent such as chloracetic acid or a salt thereof such as the sodium salt. These reagents may be applied to the fabric separately or together. The reaction is conveniently performed in an aqueous system. This system preferably comprises a water- miscible organic solvent such as ethanol or industrial methylated spirit, in order to suppress swelling and dissolution of carboxymethylated cellulose. Reference may be made to WO-A-94/16746 for general discussion of the carboxymethylation reaction. A preferred method of performing such a carboxymethylation step is as follows, and such a method of carboxymethylating a fibre of cellulose II forms a second aspect of the invention. Regenerated or reconstituted cellulose fibre (cellulose II) is contacted with a solution containing from 4 to 8 percent by weight sodium hydroxide, the amount of sodium chloracetate necessary to achieve the desired degree of substitution, from 50 to 60 percent by weight water, and the balance ethanol. For calculation purposes, the solution is considered to consist of the substances applied to the fibre and any moisture introduced with the fibre and/or ethanol. The solution may contain a small proportion of methanol if industrial methylated spirit is used as the source of ethanol. We have found that the presence of lower proportions of water than the specified minimum tends to result in uniform carboxymethylation, which is undesirable in the manufacture of dressings according to the invention. We have found that the presence of greater proportions of water than the specified maximum tends to result in too low a degree of reaction and too low a degree of slipperiness of the carboxymethylated fibre when wetted. We have further found that lesser proportions of water than those specified above are generally required for satisfactory results on fibres of cellulose I such as cotton. The method is preferably performed at from 40 to 80°C, more preferably from 50 to 60°C. The method is preferably performed for from 20 to 90 min. , more preferably from 30 to 60 min. Ethanol may be substituted by another alcohol of the C^ group. It will be appreciated that in general the more hydrophobic the alcohol, the lower the proportion of water that is desirable in the solution. Suitable proportions for alcohols other than ethanol can readily be determined by experiment. The method of the second aspect of the invention may be performed on loose fibre, yarn or fabric. As explained hereinafter, it is thought that the large majority of the carboxymethyl groups in the carboxymethylated material according to the invention is located in the amorphous regions and that only a small minority is located in the crystalline regions. It is thought that the crystalline regions act as entanglement points in the polymeric structure, thus advantageously providing a fabric with good wet strength and also suppressing dissolution of carboxymethylcellulose. It is also thought that the relatively low absorbency is in part a consequence of this phenomenon; but it is one which does not detract from performance in the intended use. It will therefore be understood that severe carboxymethylation conditions, in particular the use of alkali at such a strength or temperature or for such a time that it converts the crystalline regions of cellulose to alkali cellulose thereby enabling reaction in the crystalline regions, are to be avoided. According to a third aspect of the invention, there is provided a carboxymethylated cellulose article wherein the degree of substitution of cellulose groups measured by IR spectroscopy (as defined hereinafter) is in the range from 0.12 to 0.35, preferably from 0.15 to 0.3 or from 0.2 to 0.3, and wherein the degree of crystallinity measured by NMR (as defined hereinafter) is in the range from 10 to 70 percent, preferably from 15 to 60 or from 20 to 65 percent, more preferably from 30 to 55 percent. The article may take the form of a film, including a perforated film, a foam or sponge, or preferably a fibre. The invention also includes fabrics and dressings which comprise such articles. Wound dressings which comprise fibre according to the third aspect of the invention may conveniently be made by the process and method of the first and second aspects of the invention. The 13 C NMR spectrum of cellulose contains features in the 80-90 ppm region attributable to crystalline cellulose I and/or II. These features are essentially absent from the spectrum of fully carboxymethylated cellulose, such as that disclosed in WO-A-93/12275 and in WO-A-94/16746 , and such material is accordingly thought to be amorphous . In contrast, spectra of carboxymethylated cellulose according to the third aspect of the invention exhibit these features to a significant extent, although generally at a somewhat lesser level than do spectra of cellulose I or II. This observation is consistent with the theory that the carboxymethyl groups are mainly located in amorphous rcit e than crystalline regions. According to a fourth aspect of the invention, there is provided a method of carboxymethylating an article of cellulose II, wherein the article is contacted with a solution containing sodium hydroxide, sodium chloracetate, ethanol and water, characterised in that the weight ratio of sodium hydroxide to water is in the range from 0.095 to 0.115, preferably from 0.10 to 0.11, and in that the weight ratio of cellulose to water is in the range from 0.22 to 0.28, preferably from 0.24 to 0.26. The method is preferably performed at from 40 to 80 °C, more preferably from 50 to 60 °C. The method is preferably performed for from 20 to 90 min. , more preferably from 30 to 60 min. It is thought that the sodium hydroxide concentration may correspond to a swelling maximum for cellulose. The article may be for example a fibre, an article containing a fibre such as a woven, knitted or nonwoven fabric, a film or a sponge. The amount of sodium chloracetate is chosen so as to achieve the desired degree of substitution. The amount of ethanol is chosen so as to achieve a suitable liquor-to-goods ratio. It will be appreciated that a high liquor-to-goods ratio is desirable for voluminous articles such as sponges and bulky nonwovens . Articles made by the method of the fourth aspect of the invention are useful in the manufacture of wound dressings, and the invention includes such dressings. The method of the fourth aspect of the invention can be used to make articles according to the third aspect of the invention. A carboxymethylated fibre according to the third aspect of the invention made from lyocell or a carboxymethylated fibre made by the methods of the first, second or fourth aspects of the invention from lyocell may have an absorbency of at least 8 g/g of 0.9% (by weight) saline solution, as measured by the free swell method of WO-A- 93/12275 , and a tenacity of at least 10 cN/tex. Upon wetting, a fabric dressing according to the invention retains its textile character, swells to a moderate degree and exhibits a desirable surface slipperiness or "gel feel" . We have surprisingly found in some cases that such a fabric dressing according to the invention may exhibit a lower absorbency than that of the cellulosic fabric, but that nevertheless when wetted it may exhibit a desirable degree of slipperiness (lubricity) when rubbed between the fingers. By way of guidance, a desirable degree of slipperiness in the present context is somewhat comparable to that observed when fingers wetted with weak soap solution or with dilute aqueous alkali (e.g. 0.01-O.lM NaOH) are rubbed together. A dressing according to the invention which consists solely of carboxymethylated cellulose fibres has the advantage that it presents a homogeneous surface to the wound. The dressings according to the invention may include or be used in conjunction with a secondary or backing layer of known type, for example an absorbent layer or a layer designed to maintain the wound environment, for example by keeping the wound moist. A backing layer may be affixed before or after the carboxymethylation step. Advantageously, the dressings of the invention may comprise a backing layer of a fusible thermoplastic fibre such as polypropylene, to permit thermal bonding to a further backing layer. Such a fusible backing layer may be incorporated in a fabric dressing by processes known in the manufacture of nonwoven fabrics such as needle bonding, stitchbonding and preferably hydroentanglement . The dressings according to the invention may be medicated. The dressings of the invention may comprise two or more plies of the fabric of the invention. The dressings according to the invention find use particularly as coverings for exuding wounds, more particularly for chronic wounds. IR Spectroscopy The degree of substitution of cellulose by carboxymethyl groups (D.S.) was measured by IR spectroscopy as follows. IR spectra were recorded of viscose rayon (D.S. zero), of commercial samples of CMC of known D.S. (0.3, 0.6, 0.85 and 1.05), of a fabric made according to WO-A-94/ 16746 (D.S. 0.4), and of fabrics in accordance with the invention. Analysis of the spectra of the samples of known D.S. yielded the linear equation: D.S. = 0.678 * I + 0.05 where I is the ratio of the integrated peak intensity over the range 1600-1700 cm "1 (C=0 stretch) to the integrated peak intensity over the range 1200-1000 cm "1 (C-0 stretch) . By D.S. in relation to the invention we mean the figure estimated using this equation. The surface and bulk IR spectra of fabrics according to the invention were very similar. This suggests that carboxymethylation had taken place throughout the whole fibre rather than only in the surface regions. The spectra of the fabric according to WO-A-94/16746 and of fabrics of the invention exhibited differences in detail: in particular, the shapes of the broad peak in the O-H stretch region (3500-3000 cm "1 ) differed, and the C-0 stretch region (1200-1000 cm "1 ) of the fabric of the invention exhibited additional features. These differences could be seen most clearly from second-derivative spectra. The fabrics of the invention derived from rayon and lyocell exhibited sharp peaks at 3445 and 3480 cm "1 , attributable to crystalline cellulose II, whereas the sample according to WO-A-94/16746 did not. NMR Spectroscopy The degree of crystallinity of carboxymethylated cellulose was measured by NMR spectroscopy as follows. Solid state 1 C NMR spectra were obtained at 75 MHz using a Bruker AC3000 (Trade Mark) spectrometer. Measurements were performed on samples packed into 7 mm zirconia rotors using proton-to-carbon cross-polarisation and magic angle spinning (CPMAS) . Conditions employed were a magic angle spinning speed of 5.0-5.5 kHz and a 90° proton preparation pulse followed by 2 ms contact time with a pulse recycle time of 3 s. Typically, a thousand scans were acquired on each sample; this is a preferred minimum number. Intensity over the range 50 to 120 ppm was integrated, with background correction. Percentage crystallinity was calculated using the formula 100(S-R)/S, where S is the integrated intensity of the sample under test and R is the integrated intensity of a reference sample of CMC prepared according to Example 1 of WO-A-94/16746. Without wishing to be bound by theory, the results on articles according to the invention are consistent with substantially uniform carboxymethylation in the amorphous regions but little or no carboxymethylation in the crystalline regions. In contrast, the results on the fabric of WO-A-94/16746 are consistent with substantially uniform carboxymethylation of the whole fibre. The invention is illustrated by the following Examples, in which parts and proportions are by weight unless otherwise specified: - Example 1 The following cellulosic fabrics were tested: A. Continuous filament viscose rayon, warp-knit (Tricotex, Trade Mark of Smith & Nephew) , 150 g/m 2 , B. Spun cotton yarn, woven gauze, 227 g/m 2 , C. Lyocell staple fibre, apertured hydroentangled fabric, 60 g/m 2 , D. Lyocell spun yarn, warp-knit, 50 g/m 2 , E. Continuous filament lyocell, weft-knit, ca. 100 g/m 2 , F. Continuous filament lyocell, warp-knit, 40 g/m 2 , G. Continuous filament lyocell, warp-knit, 44 g/m 2 (tighter fabric construction than F) , H. Continuous filament lyocell, warp-knit, 68 g/πr . Lyocell staple fibre was supplied by Courtaulds pic under the Trade Mark COURTAULDS LYOCELL and is now available from the same entity under its new name Akzo Nobel UK Limited. Continuous filament lyocell was supplied by Akzo Nobel AG under the Trade Mark NEWCELL. These cellulosic fabrics were carboxymethylated using the following general method. ' Sodium hydroxide and sodium chloracetate are separately dissolved in equal volumes of water. The two solutions are added to a reaction vessel together with a weighed quantity of industrial methylated spirit (IMS) and the mixture is stirred to yield a. homogeneous solution. A sample of fabric is immersed in the solution and the vessel is sealed. The vessel is then stored with occasional agitation in a preheated waterbath for the required time. The fabric is next removed from the vessel and squeezed by hand to remove excess liquor. Glacial acetic acid is added to the vessel to make the solution acidic, and the fabric is replaced in the solution. The vessel is then replaced in the waterbath for ten minutes with agitation. The liquor is then discarded. The fabric is placed in a crystallising dish and a first wash liquor is added; the fabric and liquor are then transferred into the reaction vessel in the waterbath for washing with hot wash liquor. The fabric is treated in similar manner with a second wash liquor and with a final wash liquor containing soft finish, after which it is set aside to dry at room temperature. Detailed conditions for the two methods referred to hereinafter as Methods I and II are given in Table 1: Table 1 Method I Method II Reaction Fabric weight g (air-dry) 50 50 Fabric moisture content % 10 10 Temperature °C 70 60 Sodium hydroxide g 19.1 19.1 Sodium chloracetate g 28.7 28.7 Water g (including fibre moisture) 117.5 175 IMS g 167.5 110 NaOH/water g/g 0.163 0.109 Cellulose/water g/g 0.383 0.257 Neutralisation Acetic acid ml 35 First Wash Liquor Water ml 118 118 IMS ml 192. .5 192. .5 Citric acid g 1.6 1.6 Second Wash Liquor Water ml 118 118 IMS ml 192. .5 192. c; Soft Finish Wash Liquor Water ml 29 2S IMS ml 307, .5 307. .5 Tween finish g 1, .7 1. .7 (TWEEN is a Trade Mark of ICI Americas, Inc.) The method referred to below as II* is method II, but with the temperature in the reaction step being 70 °C. The carboxymethylated fabrics were wetted with saline solution, and their slipperiness or "gel feel" was assessed manually and ranked on an arbitrary numerical scale, in which higher values represent greater slipperiness and a value in the range of around 4 to 10, preferably 5, represents a subjectively desirable degree of slipperiness for a wetted non-adherent dressing based on experience. The results shown in Table 2 were obtained: Table 2 Fabr: Lc A B B c D D E E F G H Method II I II II I II I II II* II* II* Time min 0 0 0 0 0 0 0 0 0 - - - 15 2 5 0 4 - 2 - 1 - - - 30 5 5 0 6 - 5 - 1 - - - 45 7 5 1 5 12 7 15 4 - - - 60 9 6 2 8 - 9 - 8 - - - 70 - - - - - - - - 5 5 5 75 10 6 3 6 - - - 6 - - - 90 13 6 ' 3 6 _ .- - 6 _ _ - A dash in this and subsequent Tables indicates that no measurement was made . The absorbency of the fabrics was measured, and the results shown in Table 3 were obtained: Table 3 Fabric A B C D F G H Method II I II II II* II* j.i '■ Time min 0 (control 2.5 8.0 9.4 6.2 2.6 2.9 ... fc 15 7.6 9.7 30 7.0 10.1 5.0 45 2.4 6.5 9.6 60 7.5 10.2 70 4.4 5.0 4.8 75 10.3 90 12.3 D.S. measurements on treated fabrics are recorded in Table 4: Table 4 Fabric A B C D F G H Method II I II II II* II* II* Time min 15 0.17 0.14 0.17 0.18 30 0.22 0.18 0.16 0.21 - 45 0.22 0.14 0.20 0.23 - 60 0.31 0.20 0.26 - 70 - - - - 0.21 0.24 0.20 75 0.38 0.25 0.20 - - 90 0.35 0.30 0.21 - - The relationship between D.S. and gel feel is thus broadly linear. Example 2 Samples of lyocell tow were carboxymethylated according to Method II of Example 1, with the differences and further details indicated in Table 5, which also reports experimental results: Table 5 Reaction Reaction Water in NaOH/ Cellulose/ FSA Gel feel temp . time min solution water water g/g °C min wt . % g/g g/g - - - - - 17.8 0 70 65 36.8 0.154 0.362 36.4 15 70 65 47.0 0.120 0.203 29.0 1 70 65 51.8 0.109 0.257 21.0 9 70 65 53.6 0.106 0.248 18.0 10 60 65 53.6 0.106 0.248 16.4 5 60 30 53.6 0.106 0.248 17.3 5 60 65 61.7 0.092 0.216 17.4 3 60 65 68.3 0.083 0.195 11.4 2 The first entry in Table 5 represents an untreated control. Free-swell absorbency (FSA) was measured according to WO-A-94/16746. Solution weight was maintained constant throughout this series of experiments. Example 3 The degree of crystallinity of samples of carboxymethylated cellulose was measured by 13 C NMR. The results shown in Table 6 were obtained: Table 6 Sample Method Time min C Crryystallinity A II 75 24 B I 30 53 B I 75 48 B II 60 63 C II 50 42 C II 60 37 CMC - - 0 These measurements were made on the samples described in Example 1, except that (1) the "C" samples were additional to Example 1, and (2) the CMC sample was a carboxymethylated fibre prepared according to the teachings of WO-A-94/16746, as described more fully below. It can be seen by comparing Tables 2 and 6 that decreasing crystallinity generally corresponds with increasing gel feel. The CMC sample was prepared as follows. Air-dry lyocell fibre, an aqueous solution of sodium hydroxide, ethanol, and an aqueous solution of sodium chloracetate were charged into a reactor to yield a mixture containing bone-dry cellulose (9 kg), sodium hydroxide (3.8 kg), sodium monochloracetate (5.7 kg), water (24.3 kg, including water introduced with the fibre) and ethanol (26.1 kg) . Thus, the NaOH/water ratio was 0.156 and the cellulose/water ratio was 0.370. The reactor was heated at 70 °C for 65 min. Acetic acid (7 1) was added to the mixture and the temperature was maintained at 70°C for 10 min. Excess liquor was removed by blowing down with nitrogen. The fibre was washed with a solution of citric acid (0.3 kg) in water (23 kg) and ethanol (30 kg) at 70 °C for 10 min. Excess liquor was removed by blowing down with nitrogen. The washing and blowing-down stages were repeated. The fibre was then washed with a solution of soft finish (0.3 kg) in water (6 kg) and ethanol (48 kg) at 70 °C for 10 min. Excess liquor was removed by blowing down with nitrogen, and the CMC fibre was dried in an air dryer. Example 4 A laminate was made by laying-up a web of lyocell staple fibre (33 g/m 2 ) and a nonwoven polypropylene backing scrim (7.5 g/m 2 ) followed by hydroentangling (6 heads: pressure 2x40 and 4x60 bar) from the lyocell side. The lyocell fibre in the resulting laminate was carboxymethylated by method II of Example 1. The polypropylene side of the carboxymethylated laminate was readily adhered to a nonwoven fabric backing of viscose staple fibre (330 g/m 2 ) by application of heat using a domestic iron. Similar results were obtained using a web of lyocell staple fibre (48 g/m 2 ) and a polypropylene scrim (12 g/m 2 ) hydroentangled together (8 heads; pressure 2x40, 4x60 and 2x80 bar) . Example 5 Cellulose sponge (25 g,- in the form of a sheet roughly 5 mm thick, as used for domestic cleaning purposes; bulk density 0.08 g/ml) was placed in a 1000 ml flask. To the flask was added a solution of 9.55 g sodium hydroxide in 40 g water and a solution of 14.35 g sodium chloracetate in a mixture of 44 g water and 270 g IMS. The total amount of water (including that originating from the sponge) was 89.2 g. Thus, the NaOH/water ratio was 0.107 and the cellulose/water ratio was 0.252. The flask was heated at 70 °C for 1 hr . To the flask was added 17.5 ml glacial acetic acid. The flask was allowed to stand for 5-10 min. The liquor was discarded, and the sponge was washed with a solution of 0.8 g citric acid in a mixture of 84 ml water and 137 ml IMS. The wash- liquor was discarded and the washing step repeated. The wash liquor was again discarded and the sponge washed with a mixture of 0.85 g Tween finish, 25 ml water and 265 ml IMS. The liquor was discarded and the sponge washed with a mixture of 30 g glycerol, 30 ml water and 40 ml IMS. The liquor was discarded and the sponge dried at ambient temperature . The glycerol served as softening agent to prevent the sponge becoming hard and board- like on drying. These reaction conditions differ from those of Example 1 essentially in the use of greater liquid volumes to cater for the low bulk density of the sponge. Reaction volumes may be reduced if a compressed sponge is used. The "gel feel" of the sponge before and after carboxymethylation was 0 and 5 respectively. The D.S. of the carboxymethylated sponge was 0.30 and the crystallinity 30%. Example 6 A sample of fabric A of Example 1 (50 g air-dry) was carboxymethylated according to the general procedure of Example 1. The treatment solution contained 19.1 g NaOH, 28.7 g sodium chloracetate, 121.2 g IMS and 171.0 g water (including moisture from the fabric). Thus, the NaOH/water ratio was 0.112 and the cellulose/water ratio was 0.263. The reaction was conducted for 40 min at 70°C. The "gel feel" of the resulting product was 5, the D.S. 0.15 and the crystallinity 17%. Example 7 A roll of fabric A of Example 1 (1250 g air-dry; 10% moisture; 17 cm diameter x 22 cm long) was carboxymethylated in a kier according to the general procedure of Example 1. The treatment solution contained 478.1 g NaOH, 717.2 g sodium chloracetate, 4241.8 g IMS and 4275 g water (including moisture from the fabric). Thus, the NaOH/water ratio was 0.112 and the cellulose/water ratio was 0.263. The reaction was conducted for 40 min at 70 °C. The "gel feel" of the resulting product was 6, the D.S. 0.23 and the crystallinity 24%. Example 8 A sample of a bulky apertured nonwoven fabric of lyocell fibre (50 g air-dry; 10% moisture; basis weight 65 g/m 2 ) was carboxymethylated according to the general procedure of Example 1. The treatment solution contained 19.1 g NaOH, 28.7 g sodium chloracetate, 231.2 g IMS and 171.0 g water (including moisture from the fabric). Thus, the NaOH/water ratio was 0.112 and the cellulose/water ratio was 0.263. The reaction was conducted for 30 min at 65°C. The "gel feel" of the resulting product was 5, the D.S. 0.31 and the crystallinity 26%. Example 9 A roll of the fabric used in Example 8 (4.50 kg air-dry; 39 cm diameter x 28 cm long) was carboxymethylated in a Icier according to the general procedure of Example 1. The treatment solution contained 1.72 kg NaOH, 2.58 kg sodium chloracetate, 44.89 kg IMS and 15.77 kg water (including moisture from the fabric) . Thus, the NaOH/water ratio was 0.109 and the cellulose/water ratio was 0.257. The reaction was conducted for 30 min at 60 °C. The "gel feel" of the resulting product was 4, the D.S. at the outside and inside of the roll was 0.18 and 0.17 respectively and the crystallinity at the outside and inside of the roll was 28% and 31% respectively. Example 10 A roll of cotton gauze (23 g/m 2 ; 7.50 kg air-dry, 6.75 kg bone-dry) (cellulose I) was carboxymethylated in a kier according to the general procedure of Example 1. The treatment solution contained 2.87 kg NaOH, 4.30 kg sodium chloracetate, 19.60 kg IMS and 18.23 kg water (including moisture from the fabric) . Thus, the NaOH/water ratio was 0.157 and the cellulose/water ratio was 0.370. The reaction was conducted for 65 min at 70°C. The "gel feel" of the resulting product was 6, the D.S. ranged from 0.16 to 0.21, and the crystallinity was 42%.

Claims: CLAIMS 1. A process for the manufacture of a wound dressing comprising the step of carboxymethylating a cellulosic fabric such that the absorbency (as defined) of the fabric after carboxymethylation is no more than 3 g/g greater than the absorbency (as defined) of the fabric before carboxymethylation and such that the degree of substitution of cellulose by carboxymethyl groups in the carboxymethylated fabric measured by IR spectroscopy (as defined) is in the range from 0.12 to 0.35. 2. A process according to claim 1, characterised in that the absorbency (as defined) of the fabric after carboxymethylation is no more than 2.5 g/g greater than the absorbency (as defined) of the fabric before carboxy- methylation. 3. A process according to claim 1, characterised in that the absorbency (as defined) of the fabric after carboxymethylation is no more than 1 g/g greater than the absorbency (as defined) of the fabric before carboxymethylation. 4. A process according to any one of the preceding claims, characterised in that the degree of substitution of cellulose by carboxymethyl groups in the carboxymethylated fabric measured by IR spectroscopy (as defined) is in the range from 0.2 to 0.3. 5. A process according to any one of the preceding claims, characterised in that the fabric comprises cellulosic continuous filament yarn. 6. A process according to any one of the preceding claims, characterised in that the fabric comprises lyocell fibre. 7. A method of carboxymethylating a fibre of cellulose II, wherein the fibre is contacted with a solution containing from 4 to 8 percent by weight sodium hydroxide, sodium chloracetate, from 50 to 60 percent by weight water, and the balance ethanol, such that the degree of substitution of cellulose by carboxymethyl groups in the carboxymethylated fibre measured by IR spectroscopy (as defined) is in the range from 0.12 to 0.35. 8. A method according to claim 7, wherein the degree of substitution of cellulose by carboxymethyl groups in the carboxymethylated fibre measured by IR spectroscopy (as defined) is in the range from 0.2 to 0.3. 9. A carboxymethylated cellulose article wherein the degree of substitution of cellulose groups measured by IR spectroscopy (as defined) is in the range from 0.12 to 0.35 and wherein the degree of crystallinity measured by NMR (as defined) is in the range from 10 to 70 percent. 10. A carboxymethylated article according to claim 9, characterised in that the degree of substitution measured by IR spectroscopy (as defined) is in the range from 0.2 to 0.3. 11. A carboxymethylated article according to one of claim 9 and claim 10, characterised in that the degree of crystallinity measured by NMR (as defined) is in the range from 15 to 60 percent. 12. A carboxymethylated article according to any one of claims 9 to 11, characterised in that it is the form of a fibre or of a fabric comprising such fibre. 13. A carboxymethylated article according to any one of claims 9 to 12, characterised in that it is made from lyocell and has an absorbency of at least 8 g/g of 0.9% (by weight) saline solution as measured by the free swell method of WO-A-93/12275, and a tenacity of at least 10 cN/tex. 14. A carboxymethylated article according to any one of claims 9 to 11 or 13, characterised in that it is the form of a foam or sponge. 15. A method of carboxymethylating an article of cellulose II wherein the article is contacted with a solution containing sodium hydroxide, sodium chloracetate, ethanol and water, characterised in that the weight ratio of sodium hydroxide to water is in the range from 0.095 to 0.115, and in that the weight ratio of cellulose to water is in the range from 0.22 to 0.28. 16. A method according to claim 15, characterised in that the weight ratio of sodium hydroxide to water is in the range from 0.10 to 0.11. 17. A method according to one of claims 15 and 16, characterised in that the weight ratio of cellulose to water is in the range from 0.24 to 0.26. 18. A method according to any one of claims 15 to 17, characterised in that the article is a fibre. 19. A method according to any one of claims 15 to 17, characterised in that the article is a sponge. 20. A wound dressing made by the process of any one. of claims 1 to 6 or comprising fibre made by the method of one of claim 7 and claim 8 or comprising an article according to any one of claims 9 to 14 or comprising an article made by the method of any one of claims 15 to 19. 21. A wound dressing according to claim 20, characterised in that it includes a backing layer. 22. A wound dressing according to claim 21, characterised in that the backing layer comprises a fusible thermoplastic fibre.

Inventors: BRAY ROGER, PATEL CHAMPA, BRAY, ROGER, PATEL, CHAMPA
Applicants: AKZO NOBEL UK LIMITED, BRAY ROGER, PATEL CHAMPA, BRAY, ROGER, PATEL, CHAMPA
Application year: 1999
Main classification: A61L15
IPC codes: A61F13, A61L15, C08B11