Room temperature vulcanizing silicone rubber compositions and process for making

Abstract: A one-component room temperature vulcanizable silicone rubber composition comprising (A) silanol end-terminated polyorganosiloxane base polymer, (B) organotriacyloxysilane cross-linker, (C) polysiloxane-polyether copolymer rheology modifier and (D) particulate silica. The rheology modifying agent is particularly useful for adjusting the viscosity and plateau stress of the silicone rubber compositions.

Description: The present invention is a one-component room temperature vulcanizing silicone rubber composition comprising a silanol end-terminated polyorganosiloxane base polymer, an organotriacyloxysilane, a polysiloxane-polyether copolymer as a rheology modifying agent and a particulate silica. The rheology modifying agent is particularly useful for controlling the viscosity and plateau stress of such silicone rubber compositions. One-component room temperature vulcanizing (RTV) silicone rubber compositions are well known in the art. Examples of such silicone RTV compositions are described in U.S. Patents 3,035,016, 3,133,891 and 3,296,161. These silicone RTV compositions generally consist of a silanol end-terminated polydiorganosiloxane polymer, a silica filler, an organotriacyloxysilane as a cross-linking agent and a metal salt of a carboxylic acid as a catalyst. The silicone RTV compositions cure to a solid elastic state at room temperature upon exposure to moisture commonly present in the atmosphere. Silicone RTV compositions are very useful in sealing and caulking applications where strong adhesion to various surfaces is important. Such uses of silicone RTV compositions often required that the compositions be placed in cracks and on surfaces having a vertical orientation or positioned overhead, therefore it is important that such compositions have viscosity and slump properties that allow them to be extruded freely into or onto cracks and surfaces and after placement the composition has limited slump. Silica is used as a primary rheology control agent in many silicone RTV compositions. However, silica is often the most expensive component of said compositions, and therefore it is desirable to reduce the amount of silica in such compositions while maintaining the desired rheology properties. The present compositions comprise a novel group of polysiloxane-polyether copolymers as rheology modifiers. The degree of polymerization of the polysiloxane segment of the copolymers as well as the size and functionality of the polyether components can be varied within the described ranges to provide for silicone RTV compositions having rheology properties desirable for a particular application. Furthermore, these rheology additives allow for the reduction of silica levels in silicone RTV compositions while maintaining desired rheology properties. U.S. Patent 4,261,758 teaches a silicone RTV composition with sag-control comprising a silanol end-terminated polydiorganosiloxane polymer, at least 3 parts by weight of a fumed silica and as the sag-control ingredient, from 0.03 to 2 parts by weight of a polyether. U.S. Patent 4,304,897 describes a silicone RTV composition having improved flow characteristic consisting of a silanol end-terminated linear polydiorganosiloxane base polymer, a filler, an organotriacyloxysilane cross-linker, a catalyst and a polyorganosiloxane copolymer consisting of a polysiloxane chain and a polyether chain which are linked together through various carboxyl alkyl radicals. The present invention is a one-component room temperature vulcanizable silicone rubber composition comprising (A) silanol end-terminated polyorganosiloxane base polymer, (B) organotriacyloxysilane cross-linker, (C) polysiloxane-polyether copolymer rheology modifier and (D) particulate silica. The rheology modifying agent is particularly useful for adjusting the viscosity and plateau stress of the silicone rubber compositions. The composition comprises (A) 100 parts by weight of a silanol end-terminated polyorganosiloxane base polymer having a viscosity within the range of 200 to 500,000 mPa·s at 25°C containing an average of from 1.85 to 2 organic radicals per silicon atom and containing from 0.02 to 2 weight percent silicon-bonded hydroxyl radicals, (B) 0.5 to 10 parts by weight of an organotriacyloxysilane cross-linker described by formula R 2 Si(OY) 3 (1) where R 2 is a monovalent hydrocarbon radicals comprising 1 to 18 carbon atoms and Y is a saturated monoacyl radical of carboxylic acid, (C) 0.2 to 10 parts by weight of a polysiloxane polyether copolymer described by formula R 3 Si((OSiR 3 2 ) x OSiR 3 2 R 4 ) 3 (2) where each R 3 is an independently selected monovalent hydrocarbon radical comprising 1 to 18 carbon atoms, x=0 to 1000 and R 4 is described by formula -(CH 2 ) a O(CH 2 CH 2 O) b (CH 2 CHR 5 O) c R 6 (3) where R 5 is an alkyl radical comprising 1 to 6 carbon atoms, R 6 is selected from hydrogen, monovalent hydrocarbon radicals comprising 1 to 12 carbon atoms and saturated monoacyl radicals of a carboxylic acid; a=3 to 12, b=0 to 100, c=0 to 100 and b+c>0, and (D) 1 to 70 parts by weight of a particulate silica. The polyorganosiloxanes comprising component (A) of the present invention are well known in the art and form the "base polymer" for the room temperature curable silicone rubber composition. These base polymers, which can comprise a single specie or a plurality of species, are liquids having a viscosity of from 200 to 500,000 mPa·s at 25°C. and contain an average of 1.85 to 2 silicon-bonded organic radicals per silicon atom, with the organic radicals being selected from the group consisting of monovalent hydrocarbon radicals and halogenated monovalent hydrocarbon radicals with the organic radicals being attached to silicon through silicon-carbon linkages and with there being present in the base polymer from 0.02 to 2 weight percent silicon-bonded hydroxyl radicals. In general the polyorganosiloxane base polymers comprise primarily diorganosiloxane units, with minor amounts of monoorganosiloxane units and triorganosiloxane units. The preferred polyorganosiloxane base polymer has the formula HO(R 1 2 SiO) n H (4) where R 1 is selected from monovalent hydrocarbon radicals and halogenated monovalent hydrocarbon radicals and n is a value within a range of 20 to 3,000 or more. The preferred organic radicals represented by R 1 are selected from methyl, ethyl, phenyl and 3,3,3-trifluoropropyl, with methyl being most preferred. The polyorganosiloxane base polymer can comprise a variety of molecules of different molecular weights and of different R 1 substituents as long as the average formula for the polyorganosiloxane base polymer falls within the limitations of component (A) as described above. In addition to the linear silanol-terminated polyorganosiloxanes described by formula (1), the base polymer can also contain polyorganosiloxanes which are terminated at one end with triorganosiloxy units described by formula R 1 3 SiO 0.5 , with the other end of the polymer chain being terminated by a silanol group, where R 1 is as previously described. The base polymer chains can also contain mono-organosiloxy units described by formula R 1 SiO 1.5 , where R 1 is as previously described. In the present invention the polyorganosiloxane base polymer has a viscosity in the range of 200 to 500,000 mPa·s at 25°C. It is preferred that the polyorganosiloxane base polymer have a viscosity in the range of 200 to 100,000 mPa·s at 25°C. The organotriacyloxysilane cross-linkers comprising component (B) as described by formula (1) are well known in the art. 0.5 to 10 parts by weight of the organotriacyloxysilane per 100 parts by weight of the polyorganosiloxane base polymer is added to the present composition. Preferred is when 2 to 8 parts by weight of the organotriacyloxysilane is added, on the same basis. The acyl radical represented by Y is a saturated monoacyl radical of a carboxylic acid. The preferred Y radicals are those containing up to 12 carbon atoms, with up to 8 carbon atoms being most preferred. It is preferred that Y be acetyl. In formula (1), R 2 is a monovalent hydrocarbon radical comprising 1 to 18 carbon atoms. R 2 is a substituted monovalent hydrocarbon radical such as 3,3,3-trichloropropyl, chloromethyl and chloromethyltolyl. It is preferred that R 2 be a lower alkyl such as methyl, ethyl, propyl, butyl, octyl or an aryl radical such as phenyl or tolyl. Preferred is when the organotriacyloxysilane is methyltriacetoxysilane. The present composition comprises 0.2 to 10 parts by weight, per 100 parts by weight of the polyorganosiloxane base polymer, of a polysiloxane-polyether copolymer described by formula (2). Preferred is when the present composition comprises 1 to 5 parts by weight of the polysiloxane-polyether copolymer, on the same basis. In formula (2), each R 3 is an independently selected monovalent hydrocarbon radical comprising 1 to 18 carbon atoms. R 3 is an unsubstituted or substituted monovalent hydrocarbon radical. Preferred is when each R 3 is a monovalent hydrocarbon radical comprising 1 to 6 carbon atoms. R 3 is, for example, alkyls such as methyl, ethyl, propyl; aryls such as phenyl and tolyl; substituted alkyls such as 3,3,3-trifluoropropyl and chloromethyl; and substituted aryls such as chloromethyltolyl. Preferred is when each R 3 is an independently selected alkyl radical comprising one to 6 carbon atoms, with methyl being most preferred. In formula (2), R 4 is described by formula -(CH 2 ) a O(CH 2 CH 2 O) b (CH 2 CHR 5 O) c R 6 (3). In formula (3), R 5 is an alkyl radical comprising 1 to 6 carbon atoms. R 5 is, for example methyl, ethyl, propyl and tert-butyl. It is preferred that R 5 be selected from methyl and ethyl. In formula (3), R 6 is selected from hydrogen, monovalent hydrocarbon radicals comprising 1 to 12 carbon atoms and saturated monoacyl radicals of a carboxylic acid. When R 6 is a monovalent hydrocarbon radical it is, for example, an alkyl such as methyl, ethyl, propyl and tert-butyl. When R 6 is a monoacyl radical of a carboxylic acid it is the same as described for Y in formula (1). When R 6 is a monoacyl radical of a carboxylic acid, it is preferred that R 6 be acetyl. It is preferred that R 6 be hydrogen. In formula (3), a=3 to 12. It is preferred that a=3 to 6, with a=3 being most preferred. In formula (3), b=0 to 100. It is preferred that b=12 to 30, with b=18 or b=24 being most preferred. In formula (3), c=0 to 100. It is preferred that c=6 to 24, with c=12 or c=18 being most preferred. In formula (3), b+c>0, with b+c=36 being preferred. Preferred examples of polysiloxane-polyether copolymers useful in the present invention are described by average formula PrSi((OSiMe 2 ) 25 OSiMe 2 R 4 ) 3 where Me is methyl, Pr is n-propyl and R 4 is selected from -(CH 2 ) 3 O(CH 2 CH 2 O) 18 (CH 2 CH(CH 3 )O) 18 H and -(CH 2 ) 3 O(CH 2 CH 2 O) 18 (CH 2 CH(CH 2 CH 3 )O) 18 H. Methods for preparing such polymers are known in the art and are effected by reaction of a hydridosiloxane and polyether or olefin in the presence of a platinum or platinum compound catalyst. The present composition requires 1 to 70 parts by weight of a particulate silica per 100 parts by weight of component (A). Preferred is when the composition comprises 5 to 50 parts by weight of the particulate silica, on the same basis. Even more preferred is 5 to 10 parts by weight of the particulate silica, on the same basis. The particulate silica can be either precipitated silica or fumed silica. Preferred is when the particulate silica is a fumed silica. Preferred is a particulate silica having a surface area of 50 m 2 /g to 750 m 2 /g. Even more preferred is a silica having a surface area of 100 m 2 /g to 500 m 2 /g. Although the particulate silica may be treated with standard treating agents known for treating silicas to make them hydrophobic such as linear and cyclic siloxanes, silanes and silazanes; it is preferred that the particulate silica not be treated for use in the present compositions. We believe that in the present composition a principal role of the polysiloxane-polyether copolymer is the treatment of the silica filler and that this treatment in large measure provides the observed effects on the rheology properties of the compositions. Various extenders and non-reinforcing fillers can be added to the present compositions as long as they do not adversely effect the desired rheology properties of the compositions. Examples of such fillers include titanium dioxide, zinc oxide, calcium carbonate, magnesium oxide, calcined clay, carbon, graphite and quartz. Additional conventional ingredients can also be included in the present compositions such as adhesion promoters, flame retardants, stabilizing agents and pigments, provided such ingredients to not adversely affect desired properties of the composition such as rheology properties. The cure of the present composition is accelerated by adding to it a catalyst. The catalyst may be a carboxylic acid salt of a metal ranging from lead to manganese, inclusive, in the electromotive series of metals. Such metals include lead, tin, nickel, cobalt, iron, cadmium, chromium, zinc and manganese, with tin being preferred. The carboxylic acids from which the salts of the metal catalyst are derived can be monocarboxylic acids or dicarboxylic acids and the metallic salts can be either soluble or insoluble in the polyorganosiloxane base polymer. Preferably, the metals salts used as catalyst are soluble in the polyorganosiloxane base polymer to facilitate the uniform dispersion of the metal salt in the present composition. Examples of metal salts which are used in the present composition as catalyst include zinc-naphthenate, lead-naphthenate, cobalt-naphthenate, cobalt octoate, zinc-octoate, lead-octoate, chromium-octoate, tin-octoate, carbomethyoxyphenyl tin trisuberate, isobutyl tin triceroate, cyclohexenyl lead triacotinate, xenyl lead trisalicylate, dimethyl tin dibutyrate, dibutyl tin diacetate, dibutyl tin dilaurate, divinyl tin diacetate, dibutyl tin dibenzoate, dibutyl tin dioctate, dibutyl tin maleate, dibutyl tin adipate and diisoamyl tin bistrichlorobenzoate. Examples of other metal compounds which may be useful as catalyst in the present composition are described is U.S. Patent 4,304,897. A preferred catalyst for use in the present composition is dibutyl tin diacetate. The amount of catalyst added to the present composition varies depending upon the particular catalyst and the desired cure rate. Generally, 0.01 to 5 parts by weight of the catalyst per 100 parts by weight of the polyorganosiloxane base polymer is considered useful. Preferred is a catalyst concentration of 0.1 to 2 parts by weight of the catalyst, on the same basis. In a preferred embodiment of the present invention, a mixture of the reinforcing particulate silica (component (D)) and the polysiloxane polyether-copolymer (component (C) is formed and then added to the polyorganosiloxane base polymer (component (A)) or in the alternative the reinforcing particulate silica and the polysiloxane-polyether copolymer are added simultaneously to the polyorganosiloxane base polymer. It is generally preferred that the reinforcing particulate silica not be added to the polyorganosiloxane base polymer followed by the sequential addition of the polysiloxane-polyether copolymer, since this method of addition may reduce the desired effects of the copolymer in the composition. The following examples are provided to illustrate the present invention. These examples are not intended to limit the scopes of the claims herein. EXAMPLES One-component room temperature vulcanizable silicone compositions were formed comprising 86 weight percent of hydroxy end-terminated polydimethylsiloxane polymer having a viscosity of 16,500 mPa·s at 25°C., 6 weight percent of approximately a 1:1 weight percent mixture of methyltriacetoxysilane and ethyltriacetoxysilane, 8.5 weight percent of silica filler, 0.025 weight percent of dibutyltin dilaurate and polysiloxane-polyether copolymer additives as described in Tables 1 and 2. The compositions were formed by placing the hydroxy end-terminated polydimethylsiloxane polymer in a mixer followed by the addition, where added, of the copolymer additive and mixing for 15 seconds. The methyltriacetoxysilane/ethyltriacetoxysilane mixture was then added to the mixer followed by one-half of the silica filler and mixing continued for another 15 seconds. Then, the second-half of the silica filler was added to mixer, mixing continued for 15 seconds and the dibutyltin dilaurate added followed by an additional 15 second mixing. The compositions were centrifuged to remove air and allowed to age for 6-7 days under anhydrous conditions at room temperature before measuring the rheology properties. The rheological properties of the aged compositions were measured using a CarriMed® CS50 rheometer (TA Instruments, New Castle, DE) with a two centimeter diameter cone fixture (0.5 degree angle, 13 µm truncation). Since the compositions start curing upon exposure to air, the upward portion of the stress sweep was eliminated to reduce the time for the measurement. The stress sweep protocol consisted of (1) a 30 second hold at 2500 Pa and (2) a ramp stress down from 2500 Pa to 100 Pa over 5 minutes. The values reported in Tables 1 and 2 are the viscosity at the end of the 30 second hold and the last value of stress for which flow was detectable (Plateau Stress). The polysiloxane-polyether siloxanes tested as rheological modifying agents were of the general formula Pr-Si((OSiMe 2 ) x OSiMe 2 R 4 ) 3 where Pr is n-propyl, Me is methyl, x is as described in Tables 1 and 2, R 4 is either hydrogen or represented by the formula -(CH 2 ) a (CH 2 CH 2 O) b (CH 2 CHR 5 O) c H where R 5 is methyl (Me) or ethyl (Et) and the values for a, b and c are as described in Tables 1 and 2. Rheology Results for Compositions Comprising Undensified Silica Having a BET of 195 m 2 /g. Sample No. Additive (Wt.%) R 4 R 5 x a b c Visc. (Pa·s) Plat.Stress Pa 1-1 2.6 H - 25 - - - 1,485 981.3 1-2 2.6 H - 100 - - - 1,865 1074.0 1-3 0.9 H - 100 - - - 1,800 990.0 1-4 2.6 formula Me 25 3 18 18 3,624 1017.0 1-5 2.6 formula Me 100 3 18 18 4,973 1196.0 1-6 0.9 formula Me 100 3 18 18 2,390 1026.0 1-7 none - - - - - - 1,650 870.0 Rheology Results for Compositions Comprising Densified Silica Having a BET Surface Area of 200 m 2 /g. Sample No. Additive (Wt.%) R 4 R 5 x a b c Visc. (Pa·s) Plat. Stress Pa 2-1 2.6 H - 25 - - - 1301 865.2 2-2 2.6 H - 100 - - - 1448 964.1 2-3 2.6 formula Me 25 3 18 18 1922 981.3 2-4 2.6 formula Me 100 3 18 18 2403 1074.0 2-5 2.6 formula Me 250 3 18 18 2631 998.9 2-6 2.6 formula Et 100 3 24 12 2476 1074.0 2-7 none - - - - - 1557 881.0 Samples of the compositions described in Tables 1 and 2 were cured under ambient conditions for a period of 7 days and then tested for physical properties. Tensile strength, Modulus at 100% and Elongation were tested by ASTM D412 test methods and Shore A durometer (Duro.) by ASTM 2240 test method. The results of this testing are reported in Tables 3 and 4. Physical Property of Cured Silicone Compositions Sample No. Tensile (MPa) Modulus (MPa) Elongation (%) Durometer (Shore A) 1-1 1.50 0.407 648 25 1-2 1.54 0.414 679 25 1-4 1.34 0.338 668 22 1-5 1.52 0.393 694 21 1-7 1.79 0.427 617 - Physical Property of Cured Silicone Compositions Sample No. Tensile (MPa) Modulus (MPa) Elongation (%) Durometer (Shore A) 2-1 1.19 0.352 540 27 2-2 1.25 0.365 550 26 2-3 1.37 0.310 686 23 2-4 1.37 0.338 632 26 2-6 1.39 0.338 640 26 2-7 1.57 0.379 658 25

Claims: A one-component room temperature vulcanizable silicone rubber composition comprising (A) 100 parts by weight of a silanol end-terminated polyorganosiloxane base polymer having a viscosity within the range of 200 to 500,000 mPa·s at 25°C. containing an average of 1.85 to 2 organic radicals per silicon atom and containing 0.02 weight percent to 2 weight percent silicon-bonded hydroxyl radicals, (B) 0.5 to 10 parts by weight of an organotriacyloxysilane cross-linker described by formula R 2 Si(OY) 3 where R 2 is a monovalent hydrocarbon radical comprising 1 to 18 carbon atoms and each Y is an independently selected saturated monoacyl radical of carboxylic acid, and (C) 0.2 to 10 parts by weight of a polysiloxane-polyether copolymer described by formula R 3 Si((OSiR 3 2 ) x OSiR 3 2 R 4 ) 3 where each R 3 is an independently selected monovalent hydrocarbon radical comprising 1 to 18 carbon atoms, x=0 to 1000 and R 4 is described by formula -(CH 2 ) a O(CH 2 CH 2 O) b (CH 2 CHR 5 O) c R 6 where R 5 is an alkyl radical comprising 1 to 6 carbon atoms, R 6 is selected from hydrogen, monovalent hydrocarbon radicals comprising 1 to 12 carbon atoms and saturated monoacyl radicals of a carboxylic acid; a=3 to 12, b=0 to 100, c=0 to 100 and b+c>0, and (D) 1 to 70 parts by weight of particulate silica. A composition according to claim 1 where the silanol end-terminated polyorganosiloxane base polymer is described by formula HO(R 1 2 SiO) n H where R 1 is selected from monovalent hydrocarbon radicals and halogenated monovalent hydrocarbon radicals and n is a value of 20 to 3,000. A composition according to claims 1 or 2 where the polysiloxane-polyether copolymer is described by average formula PrSi((OSiMe 2 ) 25 OSiMe 2 R 4 ) 3 where Me is methyl, Pr is n-propyl and R 4 is selected from - (CH 2 ) 3 O(CH 2 CH 2 O) 18 (CH 2 CH(CH 3 )O) 18 H and - (CH 2 ) 3 O(CH 2 CH 2 O) 18 (CH 2 CH(CH 2 CH 3 )O) 18 H. A composition according to any of claims 1 to 3 further comprising a catalyst comprising a carboxylic acid salt of a metal ranging from lead to manganese, inclusive, in the electromotive series of metals. A composition according to claim 4 where the catalyst is dibutyl tin diacetate. A method for preparing a one-component room temperature vulcanizable silicone rubber composition comprising mixing components (A), (B), (C), and (D) as defined in any of claims 1 to 5 in any order with the proviso that a mixture of the particulate silica (D) and the polysiloxane-polyethercopolymer (C) is formed and then added to the silanol end-terminated polyorganosiloxane base polymer (A). A method for preparing a one-component room temperature vulcanizable silicone rubber composition comprising mixing components (A), (B), (C), and (D) as defined in any of claims 1 to 5 in any order with the proviso that the particulate silica (D) and the polysiloxane-polyether copolymer (C) are added simultaneously to the silanol end-terminated polyorganosiloxane base polymer (A). A one-component room temperature vulcanizable silicone rubber composition obtainable by the methods of claims 6 or 7.

Inventors: DEGROOT JR JON VIERLING, FAIRBANK CARL ALLEN, DEGROOT, JR., JON VIERLING, FAIRBANK, CARL ALLEN
Applicants: DOW CORNING, DOW CORNING CORPORATION
Application year: 1999
Main classification: C08L83
IPC codes: C08K5, C08K3, C08L83