METHOD FOR MAKING A CROSS TIE AND A VEHICLE CHASSIS PROVIDED WITH SUCH A CROSS TIE

Abstract: Method for making a cross tie (9) for a vehicle chassis (3) and a vehicle chassis provided with such a cross tie, according to which method the cross tie (9) is at least partially made of composite material, characterised in that the cross tie (9) is made with an almost cylindrical centre part (10) and a part (11) connected to both ends thereof which widens towards the end of the cross tie (9), whereby the above-mentioned parts (10 and 11) are made in one piece by means of filament winding, and the filaments are provided in the central part (10) at an angle which is larger than 45 DEG in relation to the longitudinal direction of the cross tie (9), and whereby they are transformed into an angle which is smaller than 45 DEG in the widening parts (11).

Description: Method for making a cross tie and a vehicle chassis provided with such a cross tie. The present invention concerns a method for making a cross tie for a vehicle chassis, according to which method the vehicle chassis is made at least partially of composite material . By composite material is meant here a plastic such as polyester, reinforced with fibres, in particular glass fibres, carbon fibres, aramid fibres and such. With their far ends, the cross ties are for example glued to longitudinal runners made of composite material or to trestles which are also made of composite material and with which the cross ties are carried by wheels. A known method whereby cross ties are made of composite material is described in Belgian patent No. 1.010.366. Cross ties are made consisting of a round, tubular body which is provided with round flanges on both ends. The body is made by means of pull winding or filament winding, whereas the flanges are made by means of what is called hot press moulding and are glued to the body. Pull winding is a method whereby one or several layers of reinforcement fibres are wound on an arbor which are soaked with plastic, either before and/or after the plastic is applied in its liquid state, after which the whole is pulled through an extrusion nozzle, and the plastic cures. Filament winding is a method whereby reinforcement fibres or ribbons soaked with plastic are wound on a rotating arbor or cylinder, after which the plastic cures. In the case of hot press moulding, plastic and reinforcement fibres, possibly in the shape of a pre- impregnated fibre mat, are put in a heated mould and are pressed in the required shape under a very large pressure, for example of 100 tons/m 2 , and they are cured. It was found that, especially when the vehicle contains a superstructure on the chassis, the above-mentioned known cross ties sometimes cannot resist the torques to which they are subjected when said vehicle takes a bend. The invention aims to provide a method for making a cross tie with which is obtained a cross tie which remedies the above-mentioned disadvantages and which cannot only resist the bending forces well, but which can also resist the torques particularly well . This aim is reached according to the invention in that the cross tie is made with an almost cylindrical centre part and a part connected to both ends thereof which widens towards the end of the cross tie, whereby the above- mentioned parts are made in one piece by means of filament winding, and the filaments are provided in the central part at an angle which is larger than 45° in relation to the longitudinal direction of the cross tie, and whereby they are transformed into an angle which is smaller than 45° in the widening parts . In the centre part, filaments can be provided in two directions which cross one another which are directed clockwise and anticlockwise respectively at an angle which is larger than 45° but smaller than 80° in relation to the longitudinal direction of the cross tie. Preferably, at least one hard piece, for example a flange, is provided on the broadest end of the widening parts, worked into the composite material. In this piece can be provided one or several openings in which a thread is tapped. In these openings can be screwed bolts with which the cross ties are retained in relation to a part such as a longitudinal runner or a trestle of the vehicle chassis as the glue hardens, with which this end is glued to a longitudinal runner or a trestle. The invention also concerns a vehicle chassis provided with at least one cross tie made according to any of the preceding embodiments, whereby the widening parts of this cross tie are glued with their ends to parts made of composite material of the chassis, for example directly to two longitudinal runners or to two trestles which are connected to these longitudinal runners . In order to better explain the characteristics of the invention, the following preferred embodiment of a method and a vehicle chassis according to the invention is described as an example only without being limitative in any way, with reference to the accompanying drawings, in which: figure 1 schematically represents a side view of a vehicle provided with a chassis according to the invention; figure 2 represents a section according to line II-II in figure 1 to a larger scale, whereby only the chassis and a cross tie are represented; figure 3 shows a graph of the maximum moment of torsion, bending moment respectively, over the length of the cross tie from figure 2 ; figure 4 shows a longitudinal section of the cross tie from figure 2, drawn to a larger scale. Figure 1 shows a combination of a lorry 1 and a trailer 2, whereby the trailer 2 in the conventional manner consists of a chassis 3 which rests on two wheel sets 4 in the back, for example via trestles, and which carries a superstructure 5. The chassis 3 contains two longitudinal runners 6 made of composite material, for example of polyester reinforced with glass fibres, which as represented in figure 2, consist of a central profile 7 with an almost rectangular section and two U-shaped profiles 8 which are glued against the latter with their cores. These profiles 7 and 8 are made by means of pulltrusion, whereby the fibres soaked with plastic are thus extruded. These longitudinal runners 6 are connected to one another by means of cross ties 9, of which only one is represented in the figures for the sake of simplicity. Every cross tie 9 contains a tubular or cylindrical centre part 10 and two hollow parts 11 connected to the far ends thereof and which are trumpet-shaped or, as represented in figure 2, which widen conically towards the far ends of the cross tie 9. The parts 10 and 11 are entirely made in one piece out of plastic reinforced with filaments or fibres by means of filament winding, whereby the filaments are directed differently in the widening parts 11 than in the centre part 10. In the centre part 10 are provided filaments which cross one another under gradients, clockwise and anticlockwise respectively, forming an angle which is smaller than 45°, in the given example an angle of about 52°, together with the longitudinal direction of the part 10. On the widening parts 11, this gradient is transformed into an angle which is smaller than 45°, and even into an angle of 10° or less on de broadest ends of these parts 11. In this way, the resistance to torque of the centre part 10 is very large, especially in the middle, where the torques are the largest when the vehicle is in use, and the curve 12 in figure 3 represents the maximum torque over the length of the cross tie 9. The parts 11, however, resist the bending well. The curve 13 in figure 3 represents the maximum bending moment over the length of the cross tie 9. Due to the increase of the addendum line towards the end of the parts 11, said bending resistance of these parts is even increased, and moreover the transformation of the angle of the fibres is simplified. As becomes clear from this figure 3, the bending resistance is maximal and relatively large on the far ends of the cross tie 9, i.e. there where the largest bending moments may occur when the vehicle is in use. The cross tie 9 should be seen as clamped in between the longitudinal runners 6, so that in case of torsion on the chassis 3, shearing forces are created between the longitudinal runners 6 and the far ends of the cross tie 9 which are glued onto them. The far ends of the cross tie 9 are glued against a core of a profile 8 of a longitudinal runner 6 by means of for example a polyurethane or epoxy glue, and in order to enlarge the contact surface, the cross tie 9 contains an edge 14 on the broadest end of the parts 11 directed to the geometrical axis of the cross tie 9, as represented in detail in figure 4. These edges 14 are thus made by means of filament winding together with the parts 11. Moreover, a hard piece 15 is worked into the edge 14 of every part 11 made of composite material, in the given example in the shape of a flange, in which, opposite openings in the edge 14 , have been provided openings 16 provided with screw thread. This flange, which is for example situated on the inner side of the edge 14, can be made of metal such as steel or aluminium, or of composite material by means of hot press moulding . The openings 16 make it possible to keep the far ends of the cross tie 9 temporarily in place by means of bolts 17 after they have been glued in. These bolts 17, as represented in figure 2, are put through a longitudinal runner 6 and are screwed in an opening 16, so that one end of the cross tie 9 is held against the core of a profile 8 of the longitudinal runner 6. The invention is by no means limited to the above-described embodiments represented in the accompanying drawings; on the contrary, such a method and such a vehicle chassis can be made in all sorts of variants while still remaining within the scope of the invention as set out in the accompanying claims .

Claims: Claims . 1. Method for making a cross tie (9) for a vehicle chassis (3) according to which method the cross tie (9) is at least partially made of composite material, characterised in that the cross tie (9) is made with an almost cylindrical centre part (10) and a part (11) connected to both ends thereof which widens towards the end of the cross tie (9) , whereby the above-mentioned parts (10 and 11) are made in one piece by means of filament winding, and the filaments are provided in the central part (10) at an angle which is larger than 45° in relation to the longitudinal direction of the cross tie (9) , and whereby they are transformed into an angle which is smaller than 45° in the widening parts (11) . 2. Method according to claim 1, characterised in that in the centre part (10) , the filaments are provided in two directions which cross one another which are directed clockwise and anticlockwise respectively at an angle which is larger than 45° but smaller than 80° in relation to the longitudinal direction of the cross tie (9) . 3. Method according to any of the preceding claims, characterised in that the widening parts (11) can be made hollow with an edge (14) on their broadest end directed to the geometrical axis of the longitudinal runner (9) which is made by means of filament winding together with the parts (11) . 4. Method according to any of the preceding claims, characterised in that on the broadest end of the widening parts (11) is worked in at least one hard piece (15) in the composite material. 5. Method according to claim 4, characterised in that, before or after the hard piece (15) has been worked in in a far end, at least one opening (16) is provided in the latter in which thread is tapped. 6. Method according to claim 4 or 5, characterised in that the hard piece (15) is made of one of the following materials: steel, aluminium and composite material made by means of hot press moulding. 7. Method according to any of claims 4 to 6, characterised in that a hard piece (15) in the shape of a flange is worked in . 8. Method according to claim 3 and 6 , characterised in that this flange is provided on the inner side of the edge (14) . 9. Vehicle chassis with at least one cross tie (9), characterised in that this cross tie (9) contains an almost cylindrical centre part (10) and a part (11) connected to both ends thereof which widens towards the end of the cross tie (9) , whereby these parts (10 and 11) are made by means of filament winding, and the filaments are provided in the central part (10) at an angle which is larger than 45° in relation to the longitudinal direction of the cross tie (9), and whereby they are transformed into an angle which is smaller than 45° in the widening parts (11) , whereby the widening parts (11) of this cross tie (9) are glued with their ends to parts made of composite material of the chassis (3), for example directly to two longitudinal runners (6) or to two trestles which are connected to these longitudinal runners (6) . 10. Vehicle chassis according to claim 9, characterised in that the widening parts (11) are hollow and in that the cross tie (9) has an edge (14) on the broadest ends of these parts (11) directed towards the geometrical axis of the cross tie (9) . 11. Vehicle chassis according to claim 9 or 10, characterised in that in the far ends of the widening parts (11) of the cross tie (9) has been worked in at least one metal piece (15) in which is provided at least one opening (16) provided with screw thread in which is screwed a bolt (17) which protrudes through the part of the chassis (3).

Inventors: VERHAEGHE JAN, VERHAEGHE, JAN
Applicants: GROEP STEVENS INTERNATIONAL NA, VERHAEGHE JAN, GROEP STEVENS INTERNATIONAL, NAAMLOZE VENNOOTSCHAP, VERHAEGHE, JAN
Application year: 1999
Main classification: B62D21
IPC codes: B62D21, B62D29