Thermal shock resistant luminescent glass

Abstract: A luminous glass comprising, in percent by weight, the following components: SiO 2 46-66 Al 2 O 3 18-30 MgO 0-12 CaO 0-16 ZnO 0-21 P 2 O 5 0-10 Li 2 O 0-8 BaO 0-9 As 2 O 3 + Sb 2 O 3 0-2 wherein a ratio of Al 2 O 3 to SiO 2 is 0.32-0.56, a total amount of MgO, CaO, and ZnO is 2-34 wt.%, a total amount of P 2 O 5 , Li 2 O, and BaO is 0-21 wt.%, and one or more rare earth elements are added to the glass on an oxide basis of 0.1-30 wt.% to an total amount of the components, PbO, B 2 O 3 , BeO, Na 2 O, and K 2 O are not essentially contained, and the glass has a thermal shock resistance | Δt|°C of not less than 150, which is obtained by following equation, | Δt|=[flexural strength] × (1-[Poisson's ratio])/([coefficient of thermal expansion] × [Young's modulus]).

Description: BACKGROUND OF THE INVENTION Field of the Invention The present invention relates to luminescent glass containing rare earth ions, wherein the characters of thermal expansion and mechanical strength, of the luminescent glass are improved. In particular, the invention relates to the luminescent glass which can be suitably applied to an oscillation medium for laser oscillation, an excitation light filter or the like. Description of Related Art For materials which are applied as the luminescent materials in earlier technology, a glass material, a single crystal material, and a ceramic material have been known. For the glass material, for example, various laser glasses such as quartz laser glass, phosphate system laser glass or the like, which contain rare earth ions and are applied to oscillation medium for laser oscillation have been known. The luminescent glass material is not only applied to the laser glass. For example, Japanese Patent Application No. 9-188543 laid open discloses blue emission glass which can be applied to; optical detector which applied to confirmation of radiation beam position such as ultraviolet beam, X-ray or the like, mode pattern recognition, spatial distribution state; an element for optical power meter; an image displaying sensor; and the like. However, there are problems of the thermal resistance in the glass material in earlier technology. That is, because the glass material has a high coefficient of thermal expansion, when the glass material is subjected to irradiation by an excitation light with high intensity, the glass material breaks under thermal expansion thereof. When the glass material is used under such environmental circumstances, temperature of which is largely or rapidly changed, the glass material breaks under thermal fatigue thereof. Accordingly, there is a problem that the condition and circumstances, for using the glass material are limited. Therefore, for example, it is required for the luminescent glass material which is applied to the oscillation medium for laser oscillation or the wavelength conversion filter for excitation light of laser to prevent occurring large or rapid change of temperature, or to change the glass material to another one before the glass material thermally fatigues. On the other hand, there are problems for the luminescent single crystal material that it is difficult to uniformly dope the optically active elements to the single crystal material and to produce a product of the single crystal material having practically large size. It is suitable for the glass material to produce a product having large size compared with the single crystal material. There is a problem that the ceramic material is liable to occur a light scattering caused by grain boundaries and pores, of the ceramic material, which is character thereof. Therefore, it is difficult to apply the ceramic material to such an application requiring transparent luminescent material. SUMMARY OF THE INVENTION The present invention has been developed in view of the problems. An object of the present invention is to provide a luminescent glass which can solve the problems of luminescent materials in earlier technology, that is, the problems of thermal properties, for example, the break under the locally thermal expansion thereof or a heat shock, or the like, caused by the high coefficient of thermal expansion. Another object of the invention is to provide a luminescent glass which can solve the problems in the non-uniform distribution of the optically active element in the single crystal material in earlier technology and in the occurrence of the light scattering caused by the grain boundaries and the pores, of the ceramic material in the earlier technology. Further object of the invention is to provide a luminescent glass which can be easily produced. Still further object of the invention is to provide a method for producing luminescent glass having the superior thermal properties above-described. The inventors have made various efforts to solve the problems above-described. As a result, it is developed that the glass having a rare earth element has superior thermal character and optical homogeneity and can be easily produced. Then, the inventors have achieved the invention In order to accomplish the above objects, the invention provides a luminescent glass in accordance with claim 1 of the appended claims. In one aspect of the invention, a luminescent glass is provided having a thermal shock resistance Δt°C of not less than 150°C, wherein the thermal shock resistance Δt is obtained by following equation, Δt= [flexural strength] × (1-[Poisson's ratio])/([coefficient of thermal expansion] × [Young's modulus]). The luminescent glass is essentially free from PbO, B 2 O 3 , BeO, Na 2 O, and K 2 O. According to the luminescent glass of the invention, because the thermal shock resistance Δt°C thereof is not less than 150°C, even though the glass is subjected to the irradiation by the high intense excitation light, it is possible to resist the locally thermal expansion thereof caused by heat generation, the heat shock, the thermal fatigue with the passage of time under the intermittent irradiation by excitation light, or the like. Therefore, it is possible to apply the luminescent glass of the invention to various optical products without limitation of the condition and circumstances, for using the luminescent glass, for example, the luminescent glass can be suitably applied to oscillation medium for laser oscillation and the wavelength conversion filter for excitation light. The luminescent glass consists of the following components: Wt. % SiO 2 46-66 Al 2 O 3 18-30 MgO 1-12 CaO 0-12 ZnO 0-18 P 2 O 5 0-10 Li 2 O 0-7 BaO 1-9 As 2 O 3 + Sb 2 O 3 0-2 SrO + CoO + NiO + MnO 2 + Cr 2 O 3 0-15 F 2 + La 2 O 3 + Nb 2 O 5 + MoO 3 + Ta 2 O 5 + Bi 2 O 3 + WO 3 + Fe 2 O 3 + SnO 2 + CuO 0-8 wherein the ratio of Al 2 O 3 to SiO 2 is 0.32 - 0.56, the total amount of MgO, CaO, and ZnO is 2 - 28 weight percent and the total amount of P 2 O 5 , Li 2 O, and BaO is 1 - 20 weight percent, and 0.1 to 30 parts by weight of one or more rare earth elements on an oxide basis are added to the base components based on 100 parts by weight of a total amount of the base components and the luminescent glass is essentially free from PbO, B 2 O 3 , BeO, Na 2 O and K 2 O. The luminescent glass preferably consists of the following components: Wt. % SiO 2 46-66 Al 2 O 3 18-30 MgO 1-10 CaO 0-8 ZnO 0-16 P 2 O 5 0-10 Li 2 O 2-6 BaO 1-6 As 2 O 3 + Sb 2 O 3 0-2 SrO + CoO + NiO + MnO 2 + Cr 2 O 3 0-15 F 2 + La 2 O 3 + Nb 2 O 5 + MoO 3 + Ta 2 O 5 + Bi 2 O 3 + WO 3 + Fe 2 O 3 + SnO 2 + CuO 0-8 wherein the ratio of Al 2 O 3 to SiO 2 is 0.32-0.56, the total amount of MgO, CaO, and ZnO is 2-23 wt.%, the total amount of P 2 O 5 , Li 2 O, and BaO is 3-19 wt.%, and 0.1 - 30 parts by weight of one or more rare earth elements on an oxide basis are added to the base components based on 100 parts by weight of a total amount of the base components. According to the luminescent glass of the invention, the luminescent glass is close and have superior homogeneity, high mechanical strength, and chemical durability. Further, the luminescent glass of the invention has lower coefficient of thermal expansion and larger flexural strength in comparison to the luminescent glass in earlier technology. As a result, the luminescent glass has high thermal shock resistance. In addition, because it is glass, the luminescent glass of the invention has superior formability. Therefore, it is possible to apply the luminescent glass of the invention to extremely various application as luminescent material substituted for the glass material, the single crystal material, and the ceramics material. The invention further provides a method for producing a luminescent glass in accordance with claims 3 of the appended claims. In accordance with another aspect of the invention, a method for producing a luminescent glass having a thermal shock resistance Δt°C of not less than 150°C, the method comprises the steps of: mixing raw materials of components of the glass; charging the resulting mixture into a melting apparatus; melting the mixture at temperature of about 1530-1570°C for about 8 hours and homogenizing by agitating; and casting the homogenized mixture in an iron board, annealing and cooling to room temperature. In the method, the luminescent glass is essentially free from PbO, B 2 O 3 , BeO, Na 2 O, and K 2 O. In the method, the luminescent glass consists of the following components Wt. % SiO 2 46-66 Al 2 O 3 18-30 MgO 1-12 CaO 0-12 ZnO 0-18 P 2 O 5 0-10 Li 2 O 0-7 BaO 1-9 As 2 O 3 + Sb 2 O 3 0-2 SrO + CoO + NiO + MnO 2 + Cr 2 O 3 0-15 F 2 + La 2 O 3 + Nb 2 O 5 + MoO 3 + Ta 2 O 5 + Bi 2 O 3 + WO 3 + Fe 2 O 3 + SnO 2 + CuO 0-8 wherein the ratio of Al 2 O 3 to SiO 2 is 0.32 - 0.56, the total amount of MgO, CaO, and ZnO is 2 - 28 weight percent and the total amount of P 2 O 5 , Li 2 O, and BaO is 1 - 20 weight percent, and 0.1 to 30 parts by weight of one or more rare earth elements on an oxide basis are added to the base components based on 100 parts by weight of a total amount of the base components. According to the method of the invention, because the luminescent glass can be produced by the method for producing glass, the luminescent glass has superior formability and easiness of production. PREFFERED EMBODIMENT OF THE INVENTION The luminescent glass according to the embodiment of the present invention will be explained as follows. At first, the reasons for limiting the range of the thermal shock resistance Δt°C and the composition, of the luminescent glass to that above-described will be explained as follows. The thermal shock resistance Δt is an index to a heat-resistance impact, which is represented by the following equation, Δt=[flexural strength] × (1-[Poisson's ratio])/([coefficient of thermal expansion] × [Young's modulus]) and which is stated in "New Glass Handbook" edited by editorial committee of New Glass Handbook, published by Maruzen, pages 405-406. It is judged that the larger the thermal shock resistance becomes, the larger the resistance to the difference in temperature, of the glass becomes. Applicant carried out various tests and found that it is required for the glass that the value of Δt thereof is not less than 150 to be applied to the oscillation medium for laser oscillation or the wavelength conversion filter for excitation light, which is subjected to irradiation by the high intense excitation light. Preferably, it is required the value of Δ t is not less than 200. The thermal shock resistance of almost luminescent glasses in earlier technology are not more than 100, and the largest value thereof are not more than 130. On the contrary, the luminescent glass of the invention has the thermal shock resistance of not less than 150 which is remarkably larger than the glass in earlier technology. Further, it is easy to obtain the glass having such high thermal shock resistance because the glass possesses ranges of compositions described as follows. According to the luminescent glass of the invention, because the luminescent glass has extremely high thermal shock resistance Δt, even though the luminescent glass is subjected to irradiation by the high intense excitation light, the luminescent glass can resist the locally thermal expansion thereof caused by the heat generation, the heat shock, or the thermal fatigue with the passage of time by the excitation light irradiated intermittently. As described above, according to the luminescent glass of the invention, because the luminescent glass has the thermal shock resistance Δt of not less than 150, it is possible to suitably apply the luminescent glass to optical glass for oscillation medium for laser oscillation, the wavelength conversion filter for excitation light or the like. The compositions of the luminescent glass according to the embodiment of the invention will be explained as follows. The luminescent glass is essentially free from PbO, B 2 O 3 , BeO, Na 2 O, and K 2 O, because PbO has unfavorable effects on humans and the environment, B 2 O 3 makes chemical durability and emission intensity, of the glass low, BeO has unfavorable effects on the environment, and because Na 2 O and K 2 O make chemical durability of the glass low. Regarding the SiO 2 component, when the SiO 2 content is less than 46 wt.%, the thermal shock resistance Δt of obtained glass is deteriorated. On the other hand, when the SiO 2 content is more than 66 wt.%, the raw materials of the glass are difficult to melt and the glass melt is difficult to refine so that the chemical homogeneously of the product is deteriorated. When the Al 2 O 3 content is less than 18 wt.%, it is difficult to melt the raw materials of the glass and the resistance to devitrification thereof is deteriorated. On the other hand, when the Al 2 O 3 content is more than 30 wt.%, it is also difficult to melt the raw materials of the glass and the resistance to devitrification thereof is deteriorated. The weight ratio of the Al 2 O 3 component to the SiO 2 component is 0.32-0.56. Because when the ratio is less than 0.32, it is difficult to melt the raw materials of the glass and the resistance to devitrification thereof is deteriorated. Further, a coefficient of thermal expansion of the glass becomes large, so that the glass having desired thermal shock resistance can not be obtained. Three components of MgO, ZnO, and CaO have effects of improving the melting of raw materials of the glass and the refining of the glass melt. Further, when the weight ratio of the Al 2 O 3 component to the SiO 2 component is within in the range of 0.32-0.56, these components have effect of reducing the coefficient of thermal expansion and improving the thermal shock resistance. However, when the MgO content is more than 12 wt.%, the CaO content is more than 16 wt.%, the ZnO content is more than 21 wt.%, respectively, the effects described above can not be obtained, the resistance to devitrification of the glass is deteriorated. The range of the MgO content is 1-12 wt. %, the CaO content is 0-12 wt.%, and the ZnO content is 0-18 wt.%. More preferable range of the MgO content is 1-10 wt.%, the CaO content is 1-8 wt.%, and the ZnO content is 0-16 wt.%. Further, when the total amount of three components is less than 2 wt.%, the effects described above can not be obtained. On the contrary, when the total amount of three components is more than 34 wt.%, the effects described above can not be obtained, like the case of each component, and the resistance to devitrification of the glass is deteriorated. The range of the total amount of the three components is 2-28 wt.%, more preferably, 2-23 wt.%. Each component of P 2 O 5 , Li 2 O, and BaO has effects of improving melting of the raw materials of the glass, refining of the glass melt, and emission intensity of the glass. However, when the P 2 O 5 content is more than 10 wt.%, the Li 2 O content is more than 8 wt.%, the BaO content is more than 9 wt.%, respectively, the effects described above can not be obtained, and the resistance to devitrification of the glass is deteriorated. Further, the coefficient of thermal expansion of the glass becomes large, so that the glass having desired thermal shock resistance can not be obtained. The range of the Li 2 O content is 0-7 wt.% and the BaO content is 1-9 wt.%. More preferable range of the Li 2 O content is 2-6 wt.% and the BaO content is 1-6 wt.%. When the total amount of three components is more than 21 wt.%, the effects described above can not be obtained, like the case of each component, and the resistance to devitrification of the glass is deteriorated. Further, the coefficient of thermal expansion of the glass becomes large, so that the glass having desired thermal shock resistance can not be obtained. The range of the total amount of the three components is 1-20 wt.%, more preferably, 3-19 wt.%. As 2 O 3 and Sb 2 O 3 can be added as refining agents in the melting process of the raw materials of the glass to obtain the chemically homogenous products, however, the total amount of them are sufficient up to 2 wt.%. Oxide components of rare earth elements are important as optically active components. Added amount of one or more rare earth components on an oxide basis must be 0.1-30 parts by weight based on 100 parts by weight of a total amount of the base components described above. The preferable components which have particularly emission property are Dy 2 O 3 , Nd 2 O 3 , Eu 2 O 3 , Er 2 O 3 , Sm 2 O 3 , Tb 2 O 3 , Ce 2 O 3 , and Yb 2 O 3 . It is preferable for the glass to have the total amount of one or more these components on an oxide basis of 0.1-30 parts by weight based on 100 parts by weight of a total amount of the base components described above. The oxide components of rare earth elements which are added to the glass should be carefully selected the types and amount, thereof, which are not limited, when the glasses are for applying to the ultraviolet sensor, the laser medium, the scintillator for radiation, the cover glass for the solar battery, the fluorescent substance for illuminating or displaying, the electro luminescent materials, decorating glass or the like to prevent the quenching, that is, the decrease of emission efficiency when the optically active components are high concentration or by the interactions of the optically active components with each other. It is possible to control the emission colors by selecting the types, combination of types, and amount of added oxide components of rare earth elements. It is also possible to add other ingredients in the range of maintaining the desired property of the glass of the invention. For example, the ingredients which are SrO, CoO, NiO, MnO 2 , and Cr 2 O 3 can be added in total amount of one or more types thereof up to 15 wt.%, and the components for improving resistance to ultraviolet and radiation, which are F 2 , La 2 O 3 , Nb 2 O 5 , MoO 3 , Ta 2 O 5 , Bi 2 O 3 , WO 3 , Fe 2 O 3 , SnO 2 , CuO, or the like can be added in total amount of one or more than two types thereof up to 8 wt.%, respectively. The luminescent glass according to the embodiment of the invention is produced by mixing the raw materials of the glass to have the composition above-described, melting the raw materials at predefined temperature for predefined times, thereafter, forming the melted mixture, and annealing the formed mixture. As a result, the luminescent glass is obtained. EXAMPLES The invention is further explained below with reference to examples. However, the invention is, of course, not limited to the examples. Tables I, II and III show compositions by weight % and some properties, of the luminescent glasses according to the examples 3 to 10 of the invention, and examples 1 and 2 (outside of the invention) and a compared example. The properties given in Tables I, II and III are the melting temperature of the raw materials of the glasses, the emission color and the wavelength of main emission, when the excitation light is irradiated to the glasses, the coefficient α of thermal expansion, the Poisson's ratio, the Young's modulus, the flexural strength, and the thermal shock resistance Δt, of the luminescent glasses according to the examples 1 to 10 and the compared example. EXAMPLES 1 2 3 4 SiO 2 56.7 53.5 56.5 57.7 P 2 O 5 -- -- 8.2 8.4 Al 2 O 3 24.1 22.7 24.6 25.2 Li 2 O -- -- 4.1 4.2 MgO -- 5.7 1.0 1.0 CaO -- -- 1.0 1.0 BaO -- -- 1.0 1.0 ZnO 19.2 18.1 0.5 0.5 La 2 O 3 -- -- 2.1 -- As 2 O 3 -- -- 1.0 0.5 Sb 2 O 3 -- -- -- 0.5 Subtotal (Parts by weight) 100.0 100.0 100.0 100.0 Ratio of added amount of the rare earth oxide to total amount of the others Tb 2 O 3 1.0 Tb 2 O 3 1.0 Ce 2 O 3 4.1 Ce 2 O 3 4.2 Total (Parts by weight.) 101.0 101.0 104.1 104.2 Melting temperature (°C) 1570 1570 1530 1530 Emission color Green Green Blue Blue Wavelength of main emission (nm) 485, 550 485, 550 420 420 Coefficient of thermal expansion α × 10 -7 /°C (100°C to 300°C) 31 36 48 47 Poisson's ratio 0.207 0.214 0.227 0.226 Young's modulus (× 10 8 N/m 2 ) 914 901 861 858 Flexural strength (× 10 6 N/m 2 ) 121 118 107 106 Thermal shock resistance Δt(°C) 339 286 200 203 EXAMPLES 5 6 7 8 SiO 2 57.7 56.5 61.9 61.6 P 2 O 5 8.4 8.2 -- -- Al 2 O 3 25.2 24.6 25.8 25.6 Li 2 O 4.2 4.1 4.6 4.6 MgO 1.0 1.0 2.1 2.1 CaO 1.0 1.0 -- 1.0 BaO 1.0 3.1 4.1 4.1 ZnO 0.5 0.5 0.5 -- La 2 O 3 -- -- -- -- As 2 O 3 -- -- 1.0 2.0 Sb 2 O 3 2.0 -- -- -- Subtotal (Parts by weight) 100.0 100.0 100.0 100.0 Ratio of added amount of the rare earth oxide to total amount of the others Tb 2 O 3 4.2 Tb 2 O 3 4.1 Ce 2 O 3 4.1 Sm 2 O 3 4.1 Total (Parts by weight) 104.2 104.1 104.1 104.1 Melting temperature (°C) 1530 1530 1550 1550 Emission color Green Green Blue Orange Wavelength of main emission (nm) 485, 485, 560, 550 550 420 605, 650 Coefficient of thermal expansion α × 10 -7 /°C (100°C to 300°C) 47 49 49 48 Poisson's ratio 0.225 0.219 0.228 0.230 Young's modulus (× 10 8 N/m 2 ) 848 831 837 838 Flexural strength (× 10 6 N/m 2 ) 107 105 106 105 Thermal shock resistance Δt(°C) 208 201 200 201 EXAMPLES Compared example 9 10 SiO 2 60.9 60.4 46.0 P 2 O 5 -- -- 7.0 Al 2 O 3 26.4 26.1 18.0 Li 2 O 4.6 4.5 6.0 MgO 2.0 2.0 6.0 CaO 1.0 2.0 8.0 BaO 4.1 4.0 6.0 ZnO -- -- 2.0 La 2 O 3 -- -- -- As 2 O 3 1.0 1.0 1.0 Sb 2 O 3 -- -- -- Subtotal (Parts by weight) 100.0 100.0 100.0 Ratio of added amount of the rare earth oxide to total amount of the others Eu 2 O 3 4.1 Dy 2 O 3 4.0 Tb 2 O 3 4.0 Total (Parts by weight) 104.1 104.0 104.0 Melting temperature (°C) 1550 1550 -- Emission color Pink Yellow -- Wavelength of main emission (nm) 580, 485, -- 615 575 Coefficient of thermal expansion α × 10 -7 /°C (100°C to 300°C) 48 49 66 Poisson's ratio 0.229 0.231 0.233 Young's modulus (× 10 8 N/m 2 ) 839 824 814 Flexural strength (× 10 6 N/m 2 ) 105 106 94 Thermal shock resistance Δt(°C) 201 202 134 The glasses according to the examples 1 to 10 shown in Tables I, II and III are produced as follows. The raw materials which are such as oxides, carbonates, nitrates, or the like are mixed to have the compositions in Tables I, II and III respectively. The resulting mixture is charged in a general melting apparatus, such as a platinum crucible, melted at the temperature of about 1530-1570°C, for about 8 hours, and homogenized by agitating. The homogenized mixture is cast in an iron board, annealed and cooled to room temperature, thus formed luminous glasses are obtained. Each obtained glass has the transparency. Each glass emits light of the colors shown in Tables I , II and III when the glass is subjected to irradiation by the excitation light at wavelength of 365nm. Accordingly, it is shown that these glasses according to the examples have optical activity. In the luminescent glasses according to the examples 1 to 10, the colors of luminescence are differ according to the types of added oxides of rare earth elements. Therefore, it is exhibited that the colors of luminescence can be changed by changing the types or the like, of added rare earth elements. Comparing examples 3 to 10 of the invention with the comparative example, even though these have similar range of compositions, the examples of the invention have lower coefficient of thermal expansion and larger flexural strength so that the examples of the invention have large thermal shock resistance Δt. That is, the glass is not always satisfied the desired properties above-described, just having the similar range of compositions. It is required for the luminescent glass to have the desired properties above-described in the specific range of composition. Table IV shows measured results of the mechanical properties of the luminescent glasses according to the examples 1 and 2 (outside of the invention) and OHARA-made optical glass products. Example* 1 Example* 2 OHARA -made glass FPL53 OHARA -made glass BSL-7 OHARA-made glass TIH-53 Coefficient of thermal expansion α × 10 -7 /°C (100°C to 300°C) 31 36 163 86 102 Young's modulus (× 10 8 N/m 2 ) 914 901 694 802 970 Poisson's ratio 0.207 0.214 0.302 0.207 0.262 Flexural strength (× 10 6 N/m 2 ) 121 118 49 94 76 Δt (°C) 339 286 30 108 57 The coefficient of thermal expansion of the luminescent glasses according to examples 1 and 2 (outside of the invention) is exceedingly low and the flexural strength thereof is large, so that the thermal shock resistance Δt thereof is exceedingly high, compared with the optical glass products as comparative examples, as shown in Table IV. That is, the thermal shock resistance Δt of the comparative examples are at highest about 100, while the thermal shock resistance Δt of the luminescent glasses according to the examples 1 and 2 (outside of the invention) is not less than 150. It is apparent that the luminescent glasses according to the examples of the invention have superior thermal properties such as heat resistance and the like. As described above, because the luminescent glass of the invention has superior thermal shock resistance, it is hard to break even if the luminescent glass is used under the environmental circumstances, temperature of which is largely or rapidly changed. As a result, it is possible to use the luminescent glass of the invention under various conditions and circumstances. Accordingly, because the luminescent glass has superior homogeneity, low thermal expansivity, superior mechanical strength, and chemical durability and it is possible to drastically improve the melting property of the raw materials of the glass with having the good valance of these superior properties of the luminescent glass, the luminescent glass has superior formability and easiness of production. Therefore, the luminescent glass of the invention is preferable luminescent materials to be applied to such a case that it is required to subjected to irradiation by the high-energy light, the temperature of the environmental circumstances is largely or rapidly changed, or it is required the chemical durability, or the like. In particular, the luminescent glass is preferable when the transparency is required. For example, the luminescent glass of the invention can be applied to the oscillation medium for laser oscillation, the wavelength conversion filter for excitation light, the scintillator for radiation, standard sample for fluorescent substance, the fluorescent displaying board, decorative lighting, the cover glass for the solar battery, adjusting of optical axis for an extra-high pressure mercury lamp, excimer laser or the like, the fluorescent optical fiber, the ultraviolet ray-to-visible ray conversion image sensor. Because it is possible to control the wavelength of emission, that is, luminescent color by selecting the types, amount and combination of types, of the rare earth elements, it is possible to apply the luminescent glass to the fluorescent substance for illuminating or displaying and the electro luminescent materials. According to the luminescent glass of the invention, the glass is produced by the method for producing glass. Therefore, it is possible to form the glass in various forms such as plate shape, thin plate shape, fiber shape, thin layer tube shape, or the like. The glass can be applied as powder by grinding the produced glass. As described above, the luminescent glass has superiority of such as physical properties to heat, ease of producing, transparentity, and the like compared with luminescent glass in earlier technology. From the foregoing description, one skilled in the art can easily ascertain the essential characteristics of this invention, and without departing from the scope thereof, can make various changes and modifications of the invention to adapt it to various usage and conditions.

Claims: A luminescent glass characterised in that it consists of the following base components and one or more rare earth elements: Wt. % SiO 2 46-66 Al 2 O 3 18-30 MgO 1-12 CaO 0-12 ZnO 0-18 P 2 O 5 0-10 Li 2 O 0-7 BaO 1-9 As 2 O 3 + Sb 2 O 3 0-2 SrO + CoO + NiO + MnO 2 + Cr 2 O 3 0-15 F 2 + La 2 O 3 + Nb 2 O 5 + MoO 3 + Ta 2 O 5 + Bi 2 O 3 + WO 3 + Fe 2 O 3 + SnO 2 + CuO 0-8 wherein the ratio of Al 2 O 3 to SiO 2 is 0.32 - 0.56, the total amount of MgO, CaO, and ZnO is 2 - 28 weight percent and the total amount of P 2 O 5 , Li 2 O, and BaO is 1 - 20 weight percent, the weight percent used to define the contents of the base materials being based on the total amount except the rare earth elements; and further characterised in that : the luminescent glass is essentially free from PbO, B 2 O 3 , BeO, Na 2 O, and K 2 O; 0.1 - 30 parts by weight of the one or more rare earth elements on an oxide basis are added to the base components based on 100 parts by weight of a total amount of the base components; and the composition of the luminescent glass is selected such that the luminescent glass has a thermal shock resistance Δt°C of not less than 150°C, the thermal shock resistance Δt being obtained by the following equation: Δt = [flexural strength] x (1 - [Poisson's ratio]) / ([coefficient of thermal expansion] x [Young's modulus]) wherein a temperature range of the coefficient of thermal expansion is 100 to 300°C. The luminescent glass as claimed in claim 1, the glass consisting of the following base components and the one or more rare earth elements: Wt. % SiO 2 46-66 Al 2 O 3 18-30 MgO 1-10 CaO 0-8 ZnO 0-16 P 2 O 5 0-10 Li 2 O 2-6 BaO 1-6 As 2 O 3 + Sb 2 O 3 0-2 SrO + CoO + NiO + MnO 2 + Cr 2 O 3 0-15 F 2 + La 2 O 3 + Nb 2 O 5 + MoO 3 + Ta 2 O 5 + Bi 2 O 3 + WO 3 + Fe 2 O 3 + SnO 2 + CuO 0-8 wherein the total amount of MgO, CaO, and ZnO is 2 - 23 wt.% and the total amount of P 2 O 5 , Li 2 O, and BaO is 3 - 19 wt.%, the weight percent used to define the contents of the base materials being based on the total amount except the rare earth elements. A method for producing a luminescent glass as claimed in claim 1 or claim 2, comprising the steps of: mixing raw materials of components of the glass; charging the resulting mixture into a melting apparatus; melting the mixture at temperature of about 1530-1570°C for about 8 hours and homogenizing by agitating; and casting the homogenized mixture in an iron board, annealing and cooling to room temperature.

Inventors: OHARA KAZUO, OHARA, KAZUO
Applicants: OHARA KK, KABUSHIKI KAISHA OHARA
Application year: 1999
Main classification: C03C3
IPC codes: C03C3, C03C4