INTERMEDIATE TRANSFER RECORDING MEDIUM, METHOD OF FORMING PRINT, AND PRINT

Abstract: An intermediate transfer recording medium is comprised by providing a transfer portion having a receptor layer on a substrate film. The transfer portion is printed with the image and thereafter transferred on a surface of a transfer-receiving material. In the first aspect of the intermediate transfer recording medium, the transfer portion is provided with plural hologram patterns 21 with a hologram mark 22 allocated to each the hologram pattern. According to the first aspect of the invention, since an image is formed on the receptor layer through positioning process using the hologram mark and then the transfer portion is transferred to the surface of the transfer-receiving material, no joint of a print plate appears in the hologram pattern and accuracy of transfer is remarkably excellent. On the other hand, In the second aspect of the intermediate transfer recording medium, peeling strength required to peel the transfer portion from the substrate film at the time when transferring the transfer portion to the transfer-receiving material is controlled in the range of 10 to 150 gf/inch. According to the second aspect of the invention, any transfer failure such as tail-extension or chip of the transfer portion is not caused.

Description: Technical Field The present invention relates to an intermediate transfer recording medium used for forming printed products by recording an image beforehand in a receptor layer and thereafter transferring the receptor layer to a transfer-receiving material and to a method for forming printed products by using the intermediate transfer records medium. Moreover, the present invention relates to an intermediate transfer recording medium whose peeling strength in a transfer step is controlled to transfer a receptor layer, in which an image is recorded, to a transfer-receiving material without transfer failures. Background Art An intermediate transfer recording medium is conventionally used to form printed products by recording an image beforehand in a receptor layer and thereafter transferring the receptor layer to a transfer-receiving material. Because, in this receptor layer, the image is stored by a thermal transfer recording method using a thermal transfer sheet provided with a colorant layer, a high quality image can be formed depending upon the structural materials of the receptor layer. The intermediate transfer recording medium also allow the receptor layer to have superior adhesion to the transfer-receiving material and to be transferred to the transfer-receiving material very adhesively by interposing an adhesive layer. It is therefore preferably used in the case of using transfer-receiving materials which are so resistant to the transfer of colorants that a high quality image cannot be directly formed and which tend to fuse with colorant layers in a thermal transfer step. Fig. 4 shows a illustrative sectional view of an example of a typical intermediate transfer recording medium. An intermediate transfer recording medium 101 comprises a substrate film 102 and a transfer portion 112 having at least a receptor layer 105. On the receptor layer 105, an image 106 is formed by thermal transfer using a thermal transfer sheet provided with a colorant layer. The transfer portion 112 with the image 106 formed on the receptor layer 105 is peeled from the substrate film 102 and transferred to a transfer-receiving material to form the objective image 106 on the transfer-receiving material. The intermediate transfer recording medium 101 is provided with, for instance, a protect layer 104 to prevent deterioration of the image 106 which has been transferred to the transfer-receiving material, thereby improving each weather resistance and finger print resistance of the image 106 and the receptor layer 105. It is also provided with a peelable layer 103 to make it easy to peel the receptor layer 105 and other necessary layers from the substrate film 102. For instance, in an intermediate transfer recording medium 101 as shown in Fig. 12, a receptor layer 105 on which an image 106 is formed is transferred to a transfer-receiving material together with a protect layer 104 and a peelable layer 103. At this time, the receptor layer 105 and other necessary layers (hereinafter called "transfer portion 112") are peeled at the boundary between the peelable layer 103 and the substrate film 102 and are transferred to a transfer-receiving material. The use of such an intermediate transfer recording medium renders it possible to transfer and form a high quality image with high resolution on a transfer-receiving material. Also, printed products can be made by writing and printing necessary matter such as a signature in advance on a transfer-receiving material and thereafter transferring the transfer portion, on which images such as characters and photographs are formed, from an intermediate transfer recording medium. Hence, the intermediate transfer recording medium may be preferably used for producing printed products including identification cards such as passports, credit cards, ID cards, and the like. It is required for printed products such as passports and credit cards as aforementioned to give security, specifically, high reliability and safety to resist forgery and falsification. Therefore, various ideas have been developed to resist forgery and falsification made by copying. The applicant of the present invention has filed with the Japanese Patent Office an application for patent on an intermediate transfer recording medium provided with a hologram pattern, micro-characters and the like in its transfer portion and on a printed product obtained by transferring the transfer portion to a transfer-receiving material to prevent forgery and falsification of printed products such as passports and credit cards. This application is Japanese Patent Application No. H10 (1999)-185354, which was not open to public on the priority date of the application of this case. According to the invention, the hologram pattern and the micro-characters formed on the transfer portion are transferred to the transfer-receiving material together with an image thereby making it difficult to forge and falsify the images such as characters and a photograph of face formed on a printed product, giving high reliability and safety. In the invention of Japanese Patent Application No. H10 (1999)-185354, preferably the transfer portion has a hologram layer and micro-characters are formed in the hologram layer. It is also preferable that the micro-characters be formed by embossing processing. When micro-characters are formed in the hologram layer, it is extremely difficult to forge. Moreover, when the micro-characters are formed by embossing processing, the micro-characters never appear in the case of copying and hence the invention is more reliable and safer. Preferably the micro-characters are 0.2 point or less in size. Further formation of a lathe or scroll work-pattern in the transfer portion has a better effect on the prevention of falsification. In the invention of Japanese Patent Application No. H10 (1999)-185354, other than the micro-characters and the lathe or scroll work-pattern, a fluorescent latent image is preferably formed by using materials which absorb light in the range of wavelengths of non-visible light including ultraviolet rays and infrared rays, especially materials which absorb light in the ultraviolet ray range. In the case where the fluorescent latent image is formed in the transfer portion, if the transfer portion is released from the transfer-receiving material with the intention of falsifying particulars printed on the transfer-receiving material, the fluorescent latent image is also broken. When a fluorescent latent image is formed on the transfer-receiving material, the adhesion of the surface of the transfer-receiving material does not become uniform and hence the transfer failure and adhesion failure of the transfer portion tend to be caused. If a fluorescent latent image is formed on the transfer portion of the intermediate transfer recording medium, such a problem is not posed. However, in such an intermediate transfer recording medium, the joints formed in a processing of a hologram pattern, that is, the joints between hologram patterns at which a hologram pattern ends, when a hologram pattern is processed one after another, appear at constant intervals. Since an image is formed on the receptor layer of the intermediate transfer recording medium without any consideration given to avoid such a joint between hologram patterns, in some cases, an image is formed on the joints between hologram patterns. When the intermediate transfer recording medium on which an image is formed in this manner is used to produce a printed product, the joints between hologram patterns are found in the image. The resulting printed product is thereby reduced in product value and hence the use of such an intermediate transfer recording medium is undesirable, particularly in the case of producing printed products such as passports for which high reliability and safety are required. In order to solve such a problem, the applicant has made a trial to prevent an image from being formed on the joints of hologram patterns by forming a detection mark, for setting the position where an image is to be formed, on each individually formed hologram pattern and by detecting the detection mark. However, if the detection mark is formed by, for instance, printing or ink-jetting in the processing of a hologram pattern, an apparatus for printing the detection mark must be incorporated in a step of processing a hologram pattern. This renders the process complicated, giving rise to many manufacturing problems which are probably a cause of increased cost. Also, if the detection mark is formed by, for instance, printing and the like after a hologram pattern is processed, the step of processing the hologram pattern is separated from the step of forming the detection mark. There is the case where the problem is posed that the intermediate transfer recording medium is elongated in the step of forming the detection mark so that the position of the hologram mark is not constant relative to the position of the detection mark and hence there is the case where the detection mark is not formed on the exact position where it must be formed. In the case of forming a complicated hologram pattern in particular, the inconstant position of the hologram mark relative to the position of the detection mark probably affects the positional relation between the hologram pattern and the image in the subsequent formation of the image on the intermediate transfer recording medium. Also, in an actual operation, the formation of the detection mark in a separate step is undesirable because it makes the manufacturing step complicated, which is a cause of increased cost. The intermediate transfer recording medium has other problems also. The peelable layer of the intermediate transfer recording medium is formed for the purpose of peeling the transfer portion from the substrate film with ease to improve the effect of transferring the transfer portion to the transfer-receiving material. The peelable layer is usually formed of a resin, such as polymethacrylates and polyacrylates, having a molecular structure of an acrylic skeleton. The peelable layer is improved in transfer efficiency with the peeling ability thereof from the substrate film. Hence, it is desirable that the peelable layer adhere to the substrate film with necessary and minimum adhesive strength. On the other hand, if the adhesive strength between the peelable layer and the substrate film is excessively weak, excessive extension of the transferred portion, such as tail-extension or burr is caused. Therefore, a polyester resin such as polyethylene terephthalate is usually contained in the peelable layer to adjust the adhesive strength to the extent that the peelable layer is supported in moderation by the substrate film. In the meantime, the intermediate transfer recording medium has come to be provided with multi-layers including a protective layer and an ultraviolet absorbing layer or the like between the receptor layer and the peelable layer in response to recent diversified demands. The thickness of the transfer portion to be transferred to the transfer-receiving material has come to be very thick. Since such an increase in the thickness of the transfer portion makes it difficult to cut (namely, difficult layer-cuttability) the transfer portion at the boundary between the portion to be transferred and the portion whose transfer is not required, the transferred portion is accompanied by a part of the portion whose transfer is not required, causing transfer failures such as tail-extension or burr. Moreover, the tail-extended portion and the burred portion fall down from the printed product during conveyance within the printer and adhere to products which are thereafter conveyed, causing product failures such as dusty products. An object of the present invention is to provide an intermediate transfer recording medium which controls the force required to separate a transfer portion from a substrate film (hereinafter called "peeling strength") so that the transfer portion on which an image is formed can be transferred without transfer failures while transfer efficiency of the transfer portion is maintained. JP 08300859 discloses an information recording medium wherein a magnetic data layer, a reflection thin film layer, a hologram forming layer and a protective layer are sequentially laminated on a base material. JP 07186515 discloses an intermediate transfer film formed by successively laminating a releasable protective layer, a hologram forming layer, a transparent membrane and a image receiving adhesive layer to a support. JP 07089226 discloses a transfer sheet consisting of a heat resistant base film, a release layer, a hologram forming layer, a transparent membrane layer and a image receiving adhesive layer. JP 06255268 discloses a thermal transfer sheet composed of a base sheet of a biaxially oriented polyethylene film, a release layer, a hologram performing layer, a transparent thin film layer and a image receiving adhesive layer. JP 63137287 discloses a transfer foil formed using a polyester film as a base material forming a thin layer providing an embossed hologram and superposing a vapour deposited aluminium layer and adhesive layer thereon. EP 0723875A discloses a method for heat transfer recording by forming plural items of image wise information on the surface of a substrate by a heat transfer technique and heat transfer image receiving sheets. EP 0677400A discloses a transfer foil having a base film, a release layer, a thermoplastic resin layer, a reflecting layer and a heat sensitive adhesive layer. US 5421618 discloses a plastic card provided with a magnetic stripe, the magnetic stripe comprising an adhesive layer, a first magnetic recording layer, a second magnetic recording layer, a metallic reflecting layer and a hologram forming layer. Disclosure of the Invention In a first aspect, the present invention provides an intermediate transfer recording medium comprising at least a substrate film (2) and a transfer portion (12) disposed on the substrate film (2) to be peelable therefrom, the transfer portion (12) having at least a receptor layer (5), on which an image is to be formed, wherein the transfer portion (12) is provided with a hologram layer (7), and the hologram layer (7) is positioned between the receptor layer (5) and the substrate film (2); characterised in that peeling strength required to peel the transfer portion (12) from the substrate film (2) when the transfer portion (12) is transferred to a transfer-receiving material is in a range of 10 to 150 gf/inch (0.039 to 0.58 N/cm); and the transfer portion (12) further has a peelable layer (3) disposed at a facemost portion of a side near the substrate film (2), and the peelable layer (3) comprises as a main component, a resin having an acrylic molecule structure, and contains a polyester resin at an amount in a range of 3 to 10 parts by weight to 100 parts by weight of the resin having an acrylic molecule structure. According to the invention, the transfer portion with the receptor layer on which an image has been formed is peeled from the substrate film by a peeling strength of 10 to 150 gf/inch (0.039 to 0.58 N/cm). When the transfer portion is transferred to the transfer-receiving layer, the efficiency in transferring the transfer portion is kept and transfer failures, such as, tail-extension and chips are not caused. Optionally, the transfer portion has a thickness in a range of not less than 3 µ m and not more than 5 µ m, and the peeling strength is in a range of not less than 10 gf/inch (0.039 N/cm) and not more than 50 gf/inch (0.19 N/cm). Alternatively, the transfer portion has a thickness in a range of not less than 5 µ m, and not more than 10 µ m, and the peeling strength is in a range of not less than 50 gf/inch (0.19 N/cm) and not more than 100 gf/inch (0.39 N/cm). As a further alternative, the transfer portion has a thickness in a range of not less than 10 µ m and not more than 20 µ m, and the peeling strength is in the range of not less than 100 gf/inch (0.39 N/cm) and not more than 150 gf/inch (0.58 N/cm). The peeling takes place primarily between the peelable layer containing an acrylic skeleton resin as it major component and the substrate film. Hence, the transfer portion can be transferred to the transfer-receiving material without any transfer failure. Also, when the transfer portion is formed using a resin having the above composition, the transfer portion is layer-cut thoroughly at the boundary between the portion to be transferred and the portion whose transfer is not required and hence the transfer portion can be transferred without transfer failures and product failures even if the thickness of the transfer portion is increased to 3 µm or more. A hologram layer, which is frequently arranged when high security is needed, specifically, it is needed to make it difficult to commit any forgery and falsification and high reliability and safety are needed as in the case of passports and identification cards, is formed as part of the transfer portion of the intermediate transfer medium. The hologram layer can be thereby transferred to the transfer-receiving material, for which security is required, without transfer failures, such as tail-extension and chips. In a second aspect, the present invention provides a method of forming a printed product using an intermediate transfer recording medium as claimed in any one of the preceding claims, comprising the steps of: transferring an image (6) by a thermal transfer method, on to the receptor layer (5); and transferring the transfer portion (12) of the intermediate transfer recording medium to a transfer receiving material. Brief Description of the Drawings Figure 1 is an illustrative sectional view showing an example of an intermediate transfer recording medium according to the present invention; Figure 2 is an illustrative sectional view showing another example of an intermediate transfer recording medium according to the present invention; Figure 3 is a view for explaining a peeling strength test using an intermediate transfer recording medium of the present invention; Figure 4 is an illustrative sectional view showing the structure of a typical intermediate transfer recording medium; Figure 5 is Table 2 in which the test results of Example B series are listed. Best Mode for Carrying Out the Invention The present invention will be hereinafter explained with reference to the drawings. Parts common to all figures are represented by the same symbols. Figure 1 is a sectional view showing an example of an intermediate transfer recording medium according to the present invention. An intermediate transfer recording medium 1F is a sheet-like laminate material consisting of a substrate film 2 and a transfer portion 12 which is formed on the substrate film 2 in a peelable manner. The transfer portion 12 has a multi-layer structure provided with at least a receptor layer 5 to which an image is to be transferred. In the transfer portion 12, a peelable layer 3, a protect layer 4, a hologram layer 7, a transparent deposition layer 8, an anchor layer 9 and the receptor layer 5 are laminated in this order from the side close to the substrate film 2. This intermediate transfer recording medium 1F is used to transfer the transfer portion 12, on which an image 6 has been formed, to a transfer-receiving material. When the transfer portion 12 is transferred to the transfer-receiving material, the peeling strength allowing the transfer portion 12 to separate from the substrate film 2 is preferably 10 to 150 gf/inch (0.039 to 0.58 N/cm) and particularly preferably 30 to 100 gf/inch (0.12 to 0.39 N/cm). The peeling of the transfer portion 12 from the substrate film 2 usually arises at the boundary between the transfer portion 12 and the substrate film 2 when the peelable boundary between the peelable layer 3 and the substrate film 2 when the peelable layer 3 is formed. When the peelable layer 3 is formed, alternatively, layers such as the receptor layer 5, which must be transferred may be transferred to the transfer-receiving material by utilising the cohesive failure of the peelable layer 3. The peeling strength in the present invention means such strength required for peeling, that is, any one of the strength required to peel the transfer portion 12 at the boundary between the transfer portion 12 and the substrate film 2 and the strength required to separate the peelable layer 3 by cohesive failure. A discussion will hereinafter be followed on the premise that the peeling arises at the boundary between the transfer portion 12 and the substrate film 2, namely at the boundary between the peelable layer 3 and the substrate film 2 as far as it is not otherwise noted. However, the same effect is obtained in the case of the cohesive failure of the peelable layer 3. When the peeling strength is less than 10 gf/inch (0.039 N/cm), the transfer portion 12 is easily peeled from the substrate film 2 and hence a better efficiency in transferring to the transfer-receiving material is obtained. However, in a transfer step, it is hard to cut neatly (namely, difficult layer-cuttability) the transfer portion 12 at the boundary between the portion to be transferred and the portion whose transfer is not required. As a result, the transferred portion is accompanied by a part of the transfer portion 12 whose transfer is not required, causing transfer failures such as tail-extension or burr. Moreover, the tail-extended portion and the burred portion fall down from the printed product during conveyance in the printer and adhere to products which are thereafter conveyed, causing product failures such as dusty products. When the peeling strength exceeds 150 gf/inch (0.58 N/cm), the layer-cuttability is improved. However, the transfer portion 12 cannot be easily peeled from the substrate film 2 and hence the efficiency in transferring the transfer portion is impaired and the transfer receiving material to be subjected to transfer is broken and torn by the side o the intermediate transfer recording medium 1, causing transfer failures, what is called, peeling of the surface of the transfer-receiving material and chips of the transfer-receiving material. Accordingly, the peeling strength required to peel the transfer portion 12 from the substrate film 2 is limited to 10-150 gf/inch (0.039 to 0.58 N/cm). This makes it possible to transfer the transfer portion 12 including the receptor layer 5 to the transfer-receiving material without impairing the transfer efficiency and without transfer failures as mentioned above. Except the receptor layer 5, layers provided in the transfer portion 12, for example, the release layer 3, the protect layer 4, the hologram layer 7, and the anchor layer 9 are not necessarily essential layers and are respectively formed by adequate selection according to, for instance, the quality of the transfer-receiving material and the purpose and working condition of the resulting printed product. No particular limitation is imposed on these layers. However, corresponding to recent various needs, any one or more of these layers are formed appropriately to constitute the transfer portion 12 with multi-layers. It is to be noted that in place of these layers or in addition to these layers, other layers having a particular function, for example, an ultraviolet absorbing layer may be formed based on adequate selection. If other than the receptor layer 5, various layers are formed as a part of the transfer portion 12 corresponding to each object, the thickness of the transfer portion 12 is increased more greatly than in a conventional case. This imposes the problem of difficulty cuttability of the transfer portion 12 which has not been taken into account so far. On the contrary, in the present invention, sinc ethe peeling strength required to peel the transfer portion 12 from the substrate film 2 is designed to be 10 to 150 gf/inch (0.039 to 0.58 N/cm) in consideration of a variation in the thickness of the transfer portion and the transfer efficiency, the transfer can be made with high layer-cuttability. The transfer portion 12 is, as shown in Figure 9, usually peeled from the substrate film 2 at the boundary between the peelable layer 3 formed on the facemost surface of the transfer portion 12 at the side of the substrate film 2 (namely, the position closest to the substrate film 2) and the substrate film 2. The peelable layer 3 is usually formed of an acrylic skeleton resin. Given as examples of the acrylic skeleton resin are polymethascrylate, polyacrylate, polyacrylnitrile and sodium polyacrylate. It is desirable that a polyester resin is contained in the peelable layer 3 to regulate the peeling strength required to peel the transfer portion 12 from the substrate film. The polyester resin can serve to control the peeling strength between the substrate film 2 and the peelable layer 3 and also the strength of cohesive failure of the peelable layer 3. To design the peeling strength to be 10 to 150 gf/inch (0.039 to 0.58 N/cm), the polyester resin is contained in a content of 3 to 10 parts by weight in 100 parts by weight of the acrylic skeleton resin. The polyester resin, when it is contained in the acrylic skeleton resin, can control the peeling strength between the peelable layer 3 and the substrate film 2 and can hence easily control the peeling strength, when the transfer portion 12 is transferred, in the aforementioned range. If the content of the polyester resin is less than 3 parts by weight based on 100 parts by weight of the acrylic skeleton resin, there is the case where the peeling strength defined in the above range is made smaller than 10 gf/inch (0.039 N/cm) when other than the receptor 5, multi-layers are formed in the transfer portion 12 whereby the thickness of the transfer portion 12 is thick. There is possibility that transfer failures can not be prevented sufficiently. On the other hand if the content of the polyester resin exceeds 10 parts by weight based on 100 parts by weight of the acrylic skeleton resin, the adhesive strength between the peelable layer 3 and the substrate film 2 becomes too large and hence there is the case where the peeling strength defined in the above range exceeds 150 gf/inch (0.58 N/cm). There is the possibility of transfer failures, that is, peeling the chipes of paper. Therefore, the content of the polyester resin is limited to a range between 3 and 10 parts by weight based on 100 parts by weight of the acrylic skeleton resin. The present invention enables it possible to transfer the transfer portion 12 without any transfer failure even when the transfer portion is made into multi-layers and the thickness thereof becomes larger than 3 µm. The following relation is established between the thickness of the transfer portion 12 and peeling strength. When the thickness of the transfer portion 12 containing two or more layers including at least a receptor layer is in a range between 3 and 5 µm, the peeling strength of the transfer portion is preferably in a range between 10 and 50 gf/inch (0.039 to 0.19 N/cm). The peeling strength in the above range enables the transfer portion 12 with the above thickness to be layer-cut thoroughly. To obtain the peeling strength in the above range, the polyester resin is preferably contained in an amount of 3 to 4 parts by weight based.on 100 parts by weight of the acrylic skeleton resin. When the thickness of the transfer portion 12 is in a range between 5 and 10 µ m, the peeling strength of the transfer portion is preferably in a range between 50 to 100 gf/inch (0.19 to 0.39 N/cm). When the peeling strength is in the above range, the transfer portion 12 with the above thickness is layer-cut thoroughly. The polyester resin is preferably contained in an amount of 4 to 6 parts by weight based on 100 parts by weight of the acrylic skeleton resin to obtain the peeling strength falling in the above range. When the thickness of the transfer portion 12 is in a range between 10 and 20 µ m, the peeling strength of the transfer portion is preferably in a range between 100 and 150 gf/inch (0.39 to 0.58 N/cm). When the peeling strength falls in the above range, the transfer portion 12 with the above thickness is layer-cut thoroughly. The polyester resin is preferably contained in an amount of 6 to 10 parts by weight based on 100 parts by weight of the acrylic skeleton resin to obtain the peeling strength falling in the above range. If the relation between the thickness of the transfer portion 12 and peeling strength and the content of each component for providing prescribed peeling strength are designed to be in the above ranges, tail-extension, burr and failures in layer cuttability which are caused by excessively small peeling strength are not produced and peeling and chips of paper which are caused by large peeling strength are not produced even in the transfer portion 12 which has a multilayer structure and a thickness more than 3 µ m. The peelable layer 3 may be formed, for instance, by dissolving or dispersing each prescribed amount of an acrylic skeleton resin and a polyester resin in an adequate solvent to prepare a coating solution for peelable layer and by applying the coating solution on the substrate film 2 by a gravure printing method, screen printing method or reverse coating method using a gravure plate, followed by drying. The thickness of the peelable layer 3 after it is dried is usually 0.1 to 10 µ m. Even in the transfer portion 12 provided with no peelable layer 3, adequate peeling strength as aforementioned is provided between the protect layer 4 and the substrate film 2 by providing the protect layer 4 with a peeling ability. Also, even in the transfer portion 12 provied with no protect layer 4, the same function as aforementioned can be given by providing a layer facing the substrate film 2 with a peeling ability. Figure 2 is a sectional view showing another example of an intermediate transfer recording medium according to the present invention. An intermediate transfer recording medium 1G comprises a substrate film 2, a release layer 13 provided on the substrate film 2 and a transfer portion 12 provided on the release layer 13. The transfer portion 12 has a multilayer structure comprising at least a receptor layer 5 to which an image 6 is to be transferred. In the transfer portion 12, a protect layer 4, a hologram layer 7, a transparent deposition layer 8, an anchor layer 9 and the receptor layer 5 are laminated in this order from the side close to the substrate film 2. The intermediate transfer recording medium 1G is, unlike the intermediate transfer recording medium 1F shown in Figure 1, provided with the release layer 13 on the outermost surface of the substrate film 2 at the side of the transfer portion 12 instead of providing the peelable layer 3 on the outermost surface of the transfer portion 12 at the side of the substrate film 2. In this case, as shown in Figure 2, the peeling of the transfer portion 12 from the substrate film 2 arises at the boundary between the protect layer 4 formed on the outermost surface of the transfer portion 12 at the side of the substrate film 2 and the release layer 13 formed on the outermost surface of the substrate film 2 at the side of the transfer portion 12. The peeling in this case can be achieved by the same effect as aforementioned, that is, the transfer portion 12 formed on the substrate film 2 can be peeled from the interface between itself and the release layer 13 by a peeling strength of 10 to 150 gf/inch (0.039 to 0.58 N/cm). It is hence possible to make the transfer free from transfer failures such as tail-extension and chips. In this case, the peeling strength between the transfer portion 12 and the release layer 13 is controlled in a range between 10 and 150 gf/inch (0.039 to 0.58 N/cm). The release layer 13 is usually formed of a binder resin and a releasing material. Given as examples of materials which may be used as the binder resin are thermoplastic resins including: acrylic resins such as polymethyl methacrylate, polyethyl methacrylate and polybutyl acrylate; vinyl type resins such as polyvinyl acetate, vinyl chloride-vinyl acetate copolymers, polyvinyl alcohol and polyvinyl butyral; and cellulose derivatives such as ethyl cellulose, nitrocellulose and cellulose acetate. Examples of the binder resin for the release layr further include heatcurable resins such as unsaturated polyester resins, polyester resins, polyurethane resins and aminoalkyde resins. As the releasing material, waxes, silicon wax, silicone type resins, melamine resins, fluororescins, micropowders of talc or silica, or lubricants such as surfactants or metal soaps may be used. The aforementioned peeling strength can be controlled by regulating the content of the releasing material in the release layer. The release layer 13 may be formed, for instance, by dissolving or dispersing the above resin in an adequate solvent to prepare a coating solution for release layer and by applying the coating solution to the substrate film 2 by a gravure printing method, screen printing method or reverse coating method using a gravure plate, following by drying. The thickness of the release layer 13 after it is dried is usually 0.1 to 10 µm. Next, each layer constituting the intermediate transfer recording medium according to the invention will be explained. As the substrate film 2, there may be used the same substrate film that is used for a conventional intermediate recording medium as it is and there is no limitation to a material of the substrate film 2. Given as specific examples of materials used preferably as the substrate film 2 are then paper such as glassine paper, condenser paper or paraffin paper; or oriented or nonoriented film of plastics such ass highly heat resistant polyesters (e.x. polyethylene terephthalate, polyethylene naphthalate, polybutylene terephthalate, polyphenylene sulfide, polyether ketone or polyether sulfone),polypropylene, polycarbonate, cellulose acetate, polyethylene derivatives, polyvinyl chloride, polyvinylidene chloride, polystyrene, polyamide, polyimide, polymethylpentene or ionomers. Also, composite films produced by laminating two or more of these materials may be used. The thickness of the substrate film 2 may be adequate selected depending upon the type of material such that appropriate strength and heat resistance of the material can be obtained. Usually, a substrate film having a thickness of 1 to 100 µm is preferably used. The peeling strength between the substrate film 2 and the transfer portion 12 differs depending upon the surface condition of the substrate film 2. In this case, the peeling strength is controlled by regulating the composition and content of materials contained in the transfer portion 12. A rear layer may be formed as required on the surface of the substrate film 2 on the opposite side of the transfer portion 12. The rear layer may be provided by using the same resin that is currently used to prevent the fusion of the substrate film 2 and a heating device, such as a thermal head, and to improve the slidability when the transfer portion 12 is transferred to the transfer-receiving material by using the intermediate transfer recording medium. The receptor layer 5 is provided, as a part of the transfer portion 12 constituting the intermediate transfer recording medium, on the outermost surface on the opposite side of the substrate film 2. On the receptor layer 5, the image 6 is thermally transferred from a thermal transfer sheet provided with a colorant layer by a thermal transfer method. The transfer portion 12 of the intermediate transfer recording medium 1F or 1G on which the image 6 has been formed is transferred to the transfer-receiving material, and as a result, a printed product is formed. In the light of this, as materials for forming the receptor layer 5, conventionally well-known resin materials which easily accept colorants such as sublimation dyes or heat-meltable inks may be used. Examples of materials used for the receptor layer 5 include: polyolefin type resins such as polypropylene; halogenated resins such as polyvinyl chloride and polyvinylidene chloride; vinyl type resins such as polyvinyl acetate, vinyl chloride-vinyl acetate copolymers, ethylene-vinyl acetate copolymers or polyacrylates; polyester resins such as polyethylene terephthalate or polybutylene terephthalate; polystyrene type resins; polyamide type resins; copolymer type resins obtained by polymerising an olefin such as ethylene or propylene with other vinyl polymers; ionomers; cellulose type resins such as cellulose diastase and polycarbonate. Particularly, vinyl chloride type resins, acryl-styrene type resins or polyester type resins are preferable. When the receptor layer 5 is transferred to and laminated on the transfer-receiving material through an adhesive layer, the adhesion of the receptor layer 5 is not necessarily required. However, when the receptor layer 5 is laminated on the transfer-receiving material without interposing an adhesive layer, it is desirable to form the receptor layer 5 by using an adhesive resins material such as vinyl chloride-vinyl acetate copolymers. The receptor layer 5 is formed by the following method. A single material or plural materials selected from the above materials are blended, to which various additives are added as required. The resulting mixture is dissolved or dispersed in an adequate solvent such as water or an organic solvent to prepare a coating solution for receptor layer. The coating solution is applied to the substrate film 2 or to the protect layer 4 or the like, if the protect layer 4 or the like is formed, by a gravure printing method, screen printing method or reverse coating method using a gravure plate, followed by drying. The thickness of the receptor layer 5 is about 1 to 10 µm in dry condition. The protect layer 4 is provided as a part of the transfer portion 12 if necessary. The receptor layer 5 is coated with the protect layer 4 after the transfer portion 12 is transferred to the transfer-receiving material to maintain the qualities of the image 6. As material used to form the protect layer 4, conventionally known materials for the protect layer may be used. It is desirable to select a resin composition having desired properties, for instance, fingerprint resistance, required for a surface protect layer. When, specifically, wear resistance, chemical resistance and staining resistance are required, an ionising radiation hardenable resin may be used as the resin for protect layer. The protect layer 4 may be formed by using materials for protect layer to which lubricants for improving the abrasion resistance of the image-formed products, surfactants for protecting from staining, ultraviolet absorbers for improving weather resistance and antioxidants area added appropriately. Also, as stated above, in the case where no peeling layer 3 is formed, the structural components of the protect layer are regulated such that the peeling strength required to peel the transfer portion 12 from the substrate film 2 should be in the above range, thereby controlling the adhesion between the protect layer 4 and the substrate film 2. The protect layer 4 can be formed in the same method that is used to form the peelable layer 3. The thickness of the protect layer 4 is preferably 0.1 to 10 µ m. The hologram layer 7 is provided as part of the transfer portion 12 as required. The receptor layer 5 is coated with the hologram layer 7 after the transfer portion 12 is transferred to the transfer-receiving material, thereby obtaining a printed product which accompanies a hologram pattern. The printed product provided with the hologram pattern has a decorative effect and is forged by copying with difficulty. It is therefore preferably used for those requiring security such as credit cards and passports. As materials used for the production of the hologram layer 7, conventionally known materials may be used and there is no particular limitation to the material used for the hologram layer 7. Also, the hologram layer 7 may be formed by the same method that is currently used. The transparent deposition layer 8 is usually formed in contact with the hologram layer 7 on the side close to the receptor layer 5. Because this transparent deposition layer 8 has a refractive index differing from those of other layers, it has the effect of embossing the pattern of the hologram in the formed printed product. As materials for forming the transparent deposition layer 8, conventionally well-known materials, for example, metal oxides or sulfides such as ZnS, TiO 2 and Cr 2 O 3 may be used though there is no particular limitation to the material of the transparent deposition layer 8. Also, the transparent deposition layer 8 may be formed by the same method that is currently used such as a vacuum deposition method or a sputtering method. The anchor layer 9 is, in Figure 2 for example, provided to adhere the hologram layer 7 provided with the transparent deposition layer 8 on its surface with the receptor layer 5. As materials used for the production of the anchor layer 9, conventionally known materials may be used and there is no particular limitation to the material used for the anchor layer 9. Also, the anchor layer 9 may be formed by the same method that is currently used. The ultraviolet absorbing layer may be formed at an appropriate position between the receptor layer 5 and the substrate film 2 as a part of the transfer portion 12 as required. The receptor layer 5 after being transferred is coated with the ultraviolet absorbing layer to protect the printed product from ultraviolet rays among natural light thereby preventing the deterioration of the image 6 of the printed product. As materials used for the production of the ultraviolet absorbing layer, conventionally known materials may be used and there is no particular limitation to the material used for the ultraviolet absorbing layer. Also, the ultraviolet absorbing layer may be formed by the same method that is currently used. In addition, it is preferable to provide an alignment detection mark on the intermediate transfer recording medium to transfer portion 12 of the intermediate transfer recording medium 1F or 1G to a designated position of the transfer-receiving material or to transfer the image 6 to the receptor layer 5 of the transfer portion 12 by using a thermal transfer sheet without misregistration and colour shift. The detection mark may have any form as far as it can be recognised optically. For instance, a well-known detection mark, for example, a print mark or a though-hole each having a circular, rectangular or line form may be formed. The print detection mark may be formed one or more places of one surface of the substrate film 2 of the intermediate transfer recording medium 1F or 1G by using a well-known printing method or the like. When the detection mark is formed by printing, the ink to be used may be those which are conventionally used and there is no particular limitation to the ink material. The transfer portion 12 of the intermediate transfer recording medium 1F or 1G according to the above aspect is transferred to the transfer-receiving material, and as a result, a printed product is obtained. Like the first aspect, no particular limitation is imposed on the transfer-receiving material to which the intermediate transfer recording medium according to the present invention is applied. Also, the types of shape and application of the transfer-receiving material may be optional. The intermediate transfer recording medium according to the present invention can be utilised to make a passport. If the intermediate transfer recording medium 1F or 1G in which the peeling strength of the transfer portion 12 is regulated is used in the case where a full-coloured photograph of face and other necessary particulars are required, no transfer failure is caused and a printed product which has a high quality image free from partial chips and peeling is obtained. In the case of using the intermediate transfer recording medium according to the present invention, the peeling strength required to peel the transfer portion from the substrate film is adjusted to 10 to 150 gf/inch (0.039 to 0.58 N/cm), when the transfer portion formed with an image is transferred to the transfer-receiving material. Therefore, tail-extension and burr which arise when the peeling strength of the transfer portion is too small are not produced and peeling and chips of paper which arise when the peeling strength is too large are not produced. Examples Experimental examples will be hereinafter explained. (Example B series) (Example B1) Firstly, a transparent polyethylene terephthalate with a thickness of 12 µ m was used as a substrate film 2 and the coating solution for peelable layer shown below was applied to the substrate film and dried to form a peelable layer 3 with thickness of 1.5 µ m on the substrate film 2. <Coating solution for peelable layer> Acrylic resin: 100 parts by weight Polyester resin: 5 parts by weight Methyl ethyl ketone: 100 parts by weight Toluene: 100 parts by weight Next, the coating solution for hologram layer shown below was applied to the above peelable layer 3 and dried to form a hologram layer 7 with thickness of 1.0 µm. <Coating solution for hologram layer> Acrylic resin: 40 parts by weight Melamine resin: 10 parts by weight Cyclohexane: 50 parts by weight Methyl ethyl ketone: 50 parts by weight Furthermore, a titanium oxide with thickness of 500 x 10 -10 m was formed as a transparent deposition layer 8 on the above hologram layer 7 by a vacuum deposition method. The coating solution for receptor layer shown below was further applied to the transparent deposition layer 8 and dried to form a receptor layer 5 with thickness of 2.0 µ m, thereby producing an intermediate transfer recording medium of Example B1. The transfer portion 12 of the resulting intermediate transfer recording medium was a laminate of the peelable layer 3, the hologram layer 7, the transparent deposition layer 8 and the receptor layer 5. The thickness of the laminate was 5.55 µ m. <Coating solution for receptor layer> Vinyl chloride-vinyl acetate copolymer: 40 parts by weight Acrylic silicone: 1.5 parts by weight Methyl ethyl ketone: 50 parts by weight Toluene: 50 parts by weight (Example B2) In the above Example B1, the coating solution for peelable layer was altered to the composition shown below to form a peelable layer 3 with a thickness of 1.5 µ m. <Coating solution for peelable layer> Acrylic resin: 100 parts by weight Polyester resin: 7.5 parts by weight Methyl ethyl ketone: 100 parts by weight Toluene: 100 parts by weight Next, on the resulting peelable layer 3, a hologram layer 7 with thickness of 3.0 µm, a titanium oxide deposition film with thickness of 500 x 10 -10 m as a transparent deposition layer 8 and a receptor layer 5 with thickness of 6.0 µm were sequentially formed in the same manner as in Example B1 to make an intermediate transfer recording medium of Example B2. The thickness of a transfer portion 12 was 10.55 µm. (Comparative Example B1) In the above Example B1, the coating solution for peelable layer was altered to the composition shown below to form a peelable layer 3 with a thickness of 1.5 µm. <Coating solution for peelable layer> Acrylic resin: 100 parts by weight Polyester resin: 2.5 parts by weight Methyl ethyl ketone: 100 parts by weight Toluene: 100 parts by weight In the above Example B1, the coating solution for peelable layer was altered to the composition shown below to form a peelable layer 3 with a thickness of 1.5 µm. <Coating solution for peelable layer> Acrylic resin: 100 parts by weight Polyester resin: 20 parts by weight Methyl ethyl ketone: 100 parts by weight Toluene: 100 parts by weight Next, on the resulting peelable layer 3, a hologram layer 7, a titanium oxide depostion film as a transparent deposition layer 8 and a receptor layer 5 were sequentially formed in the same thickness in the same manner as in Example B1 to make an intermediate transfer recording medium of Comparative Example B3. The thickness of a transfer portion was 5.55 µ m. (Evaluation of Example B series and results) These intermediate transfer recording medium obtained in Examples B1, B2 and Comparative Examples B1 to B3 were, as shown in Figure 3(a), cut into a strip-shaped test piece 41 such that the test piece had a width of 1 inch (2.54 cm). A test piece 42 made of a hard vinyl chloride sheet with the same size as the test piece 41 was heat-bonded to the receptor layer 5 of the test piece 41 to produce a test piece 40 for peeling test. As shown in Figure 3(b), the test piece 41 was peeled from the test piece 42 to detect the strength produced between the substrate film 2 and the transfer portion 12 by means of a load cell thereby measuring peeling strength (gf/inch). The results obtained are shown in Table 2 as Fig. 5. Next, an image 6 was formed on the receptor layer 5 of the intermediate transfer medium by a thermal transfer method using a thermal transfer sheet. The transfer portion on which the image had been formed was thermally transferred to natural fabric paper used as a transfer-receiving material to observe presence or absence of tail-extension, chips and paper peeling in the transfer step. The results were rated as follows: "○": all of those failures were not observed, "×": any one of those failures was observed. Here, the term "tail-extension" means the phenomenon that in the transfer of the transfer portion 12, the transfer portion 12 whose transfer is not required is partly transferred together on account of too-small peeling strength. The term "chips" means the phenomenon that a part of the transfer portion which should be transferred is left untransferred on the substrate film 2 on account of too-large peeling strength. The term "paper peeling" means the condition that the transfer-receiving material is torn by the side of the intermediate transfer recording medium on account of too large peeling strength and too-large adhesive strength between the transfer-receiving material and the transfer portion 12. The results obtained are shown in Table 2 as Fig. 5. In Examples B1 and B2, adequate peeling strength was obtained in relation to the thickness of the transfer portion. Hence, a high transfer ability was obtained and tail-extension, chips and paper peeling were not produced. In Comparative Example B1, on the other hand, the amount of the polyester was small and the peeling strength was thereby reduced, causing the production of tail-extension in the transfer step. In Comparative Example B2, the transfer portion was thick, causing difficult layer-cuttability and the production of tail-extension. In Comparative Example B3, the amount of the polyester was large and the peeling strength was thereby increased, leading to the production of chips and paper peeling.

Claims: An intermediate transfer recording medium comprising at least a substrate film (2) and a transfer portion (12) disposed on the substrate film (2) to be peelable therefrom, the transfer portion (12) having at least a receptor layer (5), on which an image is to be formed, wherein the transfer portion (12) is provided with a hologram layer (7), and the hologram layer (7) is positioned between the receptor layer (5) and the substrate film (2); characterised in that peeling strength required to peel the transfer portion (12) from the substrate film (2) when the transfer portion (12) is transferred to a transfer-receiving material is in a range of 10 to 150 gf/inch (0.039 to 0.58 N/cm); and the transfer portion (12) further has a peelable layer (3) disposed at a facemost portion of a side near the substrate film (2), and the peelable layer (3) comprises as a main component, a resin having an acrylic molecule structure, and contains a polyester resin at an amount in a range of 3 to 10 parts by weight to 100 parts by weight of the resin having an acrylic molecule structure. An intermediate transfer recording medium as claimed in Claim 1, wherein the transfer portion (12) has a thickness of 3 µm or more. An intermediate transfer recording medium as claimed in Claim 2, wherein the transfer portion (12) has a thickness in a range of not less than 3 µm and not more than 5 µm, and the peeling strength is in a range of not less than 10 gf/inch (0.039 N/cm) and not more than 50 gf/inch (0.19 N/cm). An intermediate transfer recording medium as claimed in Claim 2, wherein the transfer portion (12) has a thickness in a range of not less than 5 µm, and not more than 10 µm, and the peeling strength is in a range of not less than 50 gf/inch (0.19 N/cm) and not more than 100 gf/inch (0.39 N/cm). An intermediate transfer recording medium as claimed in Claim 2, wherein the transfer portion (12) has a thickness in a range of not less than 10 µm and not more than 20 µm, and the peeling strength is in the range of not less than 100 gf/inch (0.39 N/cm) and not more than 150 gf/inch (0.58 N/cm). A method of forming a printed product using an intermediate transfer recording medium as claimed in any one of the preceding claims, comprising the steps of: transferring an image (6) by a thermal transfer method, on to the receptor layer (5); and transferring the transfer portion (12) of the intermediate transfer recording medium to a transfer receiving material.

Inventors: KUROKAWA SHINICHI, ONISHI JIRO, OSHIMA KATSUYUKI, KUROKAWA, SHINICHI, ONISHI, JIRO, OSHIMA, KATSUYUKI, Kurokawa, Shinichi, Dai Nippon Printing Co., Ltd., ONISHI, Jiro, Dai Nippon Printing Co., Ltd., OSHIMA, Katsuyuki, Dai Nippon Printing Co., Ltd.
Applicants: DAINIPPON PRINTING CO LTD, DAI NIPPON PRINTING CO., LTD.
Application year: 1999
Main classification: B41M5
IPC codes: B42D15, B44C1, B41M3, G03H1, B41M5, B41M7, B44F1