MODIFIED POLYSTYRENE SPHERICAL RESIN AND PROCESS FOR DECONTAMINATING WASTE WATER BY USING THE SAME

Abstract: An absorbent, polystyrene spherical resin grafted with polyethylene glycol characterized in that polystyrene resin is crosslinked with 1 to 10 wt.% of devinylbenzene, the content of polyethylene glycol is more than 50 wt.% and the molecular weight of polyethylene glycol part is more than 500 Da, is described. In addition processes for decontaminating dye contained in waste water of dye industry, heavy metal ion contained in waste water, surfactant, humic substance contained in trash sediment effectively and quickly by using the said adsorbent, are disclosed.

Description: MODIFIED POLYSTYRENE SPHERICAL RESIN AND PROCESS FOR DECONTAMINATING WASTE WATER BY USING THE SAME Technical Field The present invention relates to a modified polystyrene spherical resin and a process for decontaminating waste water by using the modified polystyrene spherical resin. More particularly, the present invention directed to a process for decontaminating process by using polystyrene spherical resin grafted with polyethylene glycol as an adsorbent, and a process for elutriate an adsorbent from the adsorbent adsorbing contaminant through a simple process to resuscitate the adsorbent. Background Art Industrial waste water is a malignant water pollutants. For example, waste water of dye industry, heavy metal ion contained in waste water, surfactant, humic substance contained in trash sediment cause serious environmental problems. Up to now, several methods for treating such malignant pollutants have been suggested, that is, chemical, physical and biological treating process are known to a public. Among such methods, chemical treatment processes employ chemical unit processes, for example, oxidation process which decomposes chromopohore of dye by using oxidation agent and thereby decolourizes waste water. Hydrogen peroxide, etc., are used in this oxidation process [Yamasaki, K.; Sakata, K.; Yokotani, A; Japanese Patent Appln. No. 10-080,693(1998): Hirotsuji, J.; Kaai, Y.; Ikeda, A.; Japanese ' Patent Appln. No. 08-267,077(1996): Taoda, H. Japanese Patent Appln. No.05-253, 581 (1993) : Saito, S.; Murayama, K. ; Misawa, K. Japanese Patent Appln. No. 03- 188,992(1991): Mizutani, K. ; Inoue, H. JP 51,144,060(1976)]. Recently, 0 3 , etc., are reported as a new oxidation agent. [Kataoka, K. Japanese Patent Laid-Open Publication No.10- 137,780(1998): Ueno, S. Japanese Patent Laid-Open Publication No. 10-151,471(1998): watanabe, M. ; Hayashi, F.; Dazai, K. Japanese Patent Laid-Open Publication No. 10- 165,757(1998): Hayashi, F. ; Watanabe, M.; Nishino, Y.; Dazai, H. Japanese Patent Appln. No.10-118, 144(1998): fischer, W. G. European Patent Publication No. 822, 271 (1998) ] . The oxidation process decolourizes waste water, however, may creates toxic by-products which remains in waste water, and thereby cannot lower COD value. In addition, when 0 3 or electron beam is used as an oxidant, energy consumption is enormous. The biological process, in general, employs microorganism in aeration tank. However, this method requires spacious plant site, long process time, intricate conditions and operation for activation of microorganism. Meanwhile, the physical process employs active carbon adsorption method. [Nikolaevsky, R.; Monosov, M.; Monosov, E.; Sharony, E.; Gurevich, D. U. S. Patent No.5, 792, 336 (1998) : Maesaki, M.; Nakajima, M. ; Hasegawa, H. Japanese Patent Appln. No.09-253, 669(1997) : Matsumoto, Y.; Sugano, N.; Inui, T.; Akao, K. Japanese Patent Appln. No.09-248 , 562 : Hatano, Y.; Shirama, S.; Ishikawa, T.; Yobiko, Y.; Takaoka, S. Japanese Patent Appln. No. 08-281,271(1996): Sugiura, W.; Tanaka, S . ; Shimotomai, K. Japanese Patent Appln. No. 08- 000,261(1996): Tamatoshi, K. ; Morishima, K. Japanese Patent Appln. No. 07-047359(1995): McCollam, F. M. J. British Patent Appln. No.2, 280, 430 (1995) : Michna, M. ; Puppe, L. German Patent Appln. No. 4,213,163(1993)] However, these physical processes have also some demerits. That is, active carbon which has been used in adsorption process, cannot be regenerated, and therefore, should be destructed by incineration. The incinertion process employs bunker-C oil, which leads to energy consumption and air contamination. Therefore, in order to overcome the above described drawbacks of the prior arts, the inventors of the present invention have conducted an extensive research for many years for developing polystyrene adsorbent which can be used repeatedly in ' waste water treatment process. Finally, the present inventors have prepared a novel polystyrene adsorbent and a novel waste water treatment process which can substitute entirely traditional active carbon process and which can save utility expense for waste water treatment remarkably. The preparation methods of the adsorbent of the present invention are described in detail in present inventor's U.S. Patent No. 5,466,758(1995), Korean Patent No. 119,262 (1997), Korean Patent No. 119,263(1997) and Korean Patent Appln. No. 98-47748. Disclosure of The Invention It is therefore objects of the present invention to provide a novel adsorbent resin which can be used in novel processes which can substitute entirely traditional granular active carbon adsorption method for waste water treatment. The capacity of adsorption of the polystyrene resin grafted with polyethylene glycol of the present invention can be controlled by adjusting the content and molecular weight of polyethylene glycol. Also, the adsorption efficiency of the adsorbent of the present invention are varied depends on grafting method. The present inventors have widely researched the cross linking ratio and size of the polystyrene spherical resin which can be used repeatedly in adsorption/desorption /regeneration processes without loss of physical and mechanical properties thereof. As a result, the present inventor discovered that the polystyrene spherical resin which is cross linked with 1 to 10 wt%, preferably 1 to 8 wt%, more preferably 1 to 6 wt% of divinylbenzene, is appropriate to be used as a substrate for making the adsorbent for waste water which contains dye, heavy metal ion, surfactant, humic substance and etc.. Also, the present inventors have found that the polystyrene spherical resin of which size is 100 to 500 mesh, preferably 100 to 200 mesh, is desirable to be used as a substrate for making the adsorbent for waste water which contains dye, heavy metal ion, surfactant, humic substance and etc.. In addition, the present inventor have further researched several methods for introducing a hydroxy group on the surface of polystyrene spherical resin without using propylene oxide or ethylene oxide (as to the method for introducing β hydroxy group on the surface of polystyrene spherical resin by using propylene oxide or ethylene oxide, please refer the present inventor's U.S. Patent No. 5, 466, Through the above research project, the present inventor have found out that a hydroxy group can also be introduced on the surface of polystyrene spherical resin by reacting polystyrene directly with 2-methyltetrahydrofuran, or by hydrolysis of chloromethylpolystyrene with metal hydroxide, or by aminolysis of chloromethylpolystyrene with ethanol amine or diethanol amine. Polystyrene spherical resin of the present invention, which is having a hydroxy group, may also be used as a intermediate material for making the .polystyrene spherical resin grafted with polyethylene glycol. Further, the present inventor have studied the proper content and proper molecular weight of polyethylene glycol of the polystyrene-g-poylethylene glycol adsorbent which has maximum adsorption capacity and efficiency to be used as an adsorbent for waste water which contains dye, heavy metal ion, surfactant and etc.. As a result, the present inventor have found that the appropriate content of polyethylene glycol of the polystyrene-g-polyethylene glycol spherical resin to be used as a adsorbent, is more than 50 wt%, preferably 60 to 95 wt% in case that the polystyrene core is crosslinked with 1 wt% of divinylbenzen, and is 70 to 90 wt% in case that the polystyrene core is cross linked with 2 to 3 wt% of divinylbenzene . Moreover, the present inventor have found that, for the purpose of using the polystyrene-g-polyethylene glycol spherical resin as the adsorbent which has best adsorption capacity and efficiency against dye, heavy metal ion, surfactant, humic substance contained in waste water or trash sediment water, it is desirable that the molecular weight of polyethylene glycol part of the polystyrene-g- polyethylene glycol is more than 500 Da, preferably more than 900 Da, most preferably 900 to 3,000 Da. Therefore, it is an object of the present invention to provide a polystyrene spherical resin grafted with polyethylene glycol characterized in that polystyrene resin is cross linked with 1 to 10 wt% of divinylbenzene, the content of polyethylene glycol is more than 50 wt% and the molecular weight of polyethylene glycol part, is more than 500 Da. Another object of the present invention is to provide a process for decontamination of dye, surfactant, heavy metal ion, humic substance contained in waste water or trash sediment water by using the polystyrene spherical resin grafted with polyethylene glycol. Still another object of the present invention is to provide a process for recovering dye by using organic solvent from a polystyrene spherical resin grafted with polyethylene glycol, whereon dye is adsorbed. Still further object of the present invention is to provide a process for recovering a polystyrene spherical resin adsorbe'nt grafted with polyethylene glycol through a elutriate process by using organic solvent. Best Mode for Carrying Out the Invention The present invention will be more specifically illustrated by the following examples but it should be understood that the present invention is not limited to these examples in any manner. Example 1. Spherical polystyrene resin (200-400 mesh) crosslinked with 2 wt% of divinylbenzene, was reacted with propylene oxide in the presence of Lewis acid catalysts. The resulting resin was reacted with ethylene oxide in high pressure reactor to prepare polystyrene grafted with polyethylene glycol spherical resin. 200 Mg of the spherical resin thus obtained, of which polyethylene glycol content is 68 to 87%, was used for dye adsorption test. The spherical resin thus prepared and 10 ml of Yellow 5GL dye (manufactured by NOVARTIS in Switzerland) 10 "4 M solution were added into a reactor. After lhour, light absorbency of the dye solution was measured. Example 2 Spherical polystyrene resin (200-400 mesh) crosslinked with 1 wt% of divinylbenzene, was reacted with propylene oxide in the presence of Lewis acid catalysts. The resulting resin was reacted with ethylene oxide in high pressure reactor to prepare polystyrene grafted with polyethylene glycol spherical resin. 200 Mg of the spherical resin thus obtained, of which polyethylene glycol content is 60 to 94%, was used for dye adsorption test by the method described in Example 1. Example 3 , Hydroxy radical was introduced on the surface of spherical polystyrene resin (200-400 mesh) crosslinked with 1 wt% of divinylbenzene, by using ozone (0 3 ). The polystyrene spherical resin on which hydroxy radical introduced, was reacted with vinylmonomer which contains polyethylene glycol, to prepare polystyrene spherical resin grafted with polyethylene glycol. 200 Mg of spherical resin thus obtained, was used for dye adsorption test by the method described in Example 1. Example 4. 200 Mg of polystyrene adsorbent resin grafted with polyethylene glycol (200-400 mesh, polyethylene glycol content: 82%, average molecular weight of polyethylene glycol: 2,400) was added into a reactor and 10 ml of Blue 4GL dye (manufactured by NOVARTIS is Switzerland) 10 "4 M solution was added thereto. After 1 hour, the light absorbency of the dye solution was measured. The result are described in Table 1. Comparative Example 1 200 Mg of Zeolite adsorbent for water treatment manufactured by Wangpyo Chemical in Korea, was added into a reactor and 10ml of Blue 4GL dye 10 ~4 M solution was added thereto. After 1 hour, the light absorbency of the dye solution was measured by the method described in Example 1. Comparative Example 2. 200 Mg of Celite adsorbent manufactured by Shinyo Pure Chemical, was added into a reactor and 10ml of Blue 4GL dye 10 "4 M solution was added thereto. After lhour, the light absorbency of the dye solution was measured. Comparative Example 3. 200 Mg of granular active carbon adsorbent manufactured by Duksan Chemical in Korea was added into a reactor and 10 ml of Blue 4GL dye 10 "4 M solution was added thereto. After 1 hour, the light absorbency of the dye solution was measured. Example 5. Spherical polystyrene resin (100-200 mesh) crosslinked with 5 wt% of divinylbenzene, was reacted with propylene oxide in the presence of Lewis acid catalysts. The resulting resin was reacted with ethylene oxide in high pressure reactor to prepare polystyrene grafted with polyethylene glycol spherical resin. 200 Mg of the spherical resin thus obtained, of which polyethylene glycol content is 65 to 90%, was used for dye adsorption test by the method described in Example 1. Example 6. Spherical polystyrene resin (100-200 mesh) crosslinked with 8 wt% of divinylbenzene, was reacted with propylene oxide in the presence of Lewis acid catalysts. The resulting resin was reacted with ethylene oxide in high pressure reactor to prepare polystyrene grafted with polyethylene glycol spherical resin. 200 Mg of the spherical resin thus obtained, of which polyethylene glycol content is 60 to 92%, were added to. in a reactor and 10 ml of Yellow 5GL dye 10 "4 M solution was added into a reactor. After 1 hour, light absorbency of the dye solution was measured. The result are described in Table 1. Example 7. Spherical polystyrene resin (80-150 mesh) crosslinked with 10 wt% of divinylbenzene, was reacted with propylene oxide in the presence of Lewis acid catalysts. The resulting resin was reacted with ethylene oxide in high pressure reactor to prepare polystyrene grafted with polyethylene glycol spherical resin. 200 Mg of the spherical resin thus obtained, of which polyethylene glycol content is 55 to 90%, was used for dye adsorption test by the method described in Example 1. The result are described in Table 1. Comparative Example 4. 200 Mg of polystyrene adsorbent resin grafted with polyethylene glycol (200-400 mesh, polyethylene glycol content: 45%, average molecular weight of polyethylene glycol: 400) was added into a reactor and 10 ml of Blue 4GL dye 10 "4 M solution was added thereto. After 1 hour, the light absorbency of the dye solution was measured. The result was that 50% of dye was removed from the solution. Table 1 As seen in the above Table 1, the adsorbent resins prepared in Examples 1, 2, 4 - 6 and 7 represent distinguished dye adsorption efficiencies in comparison with those of active carbon adsorbents. Moreover, the time required for decontamination of dye, of the present adsorbent resins were remarkably shortened than those of the adsorbents of Comparative Examples. Example 8. Polystyrene spherical resin adsorbing Blue 4GL dye of Example 2, was added into a reactor and 10 ml N,N- dimethylformamide was added thereto. After 1 hour, the light absorbency of the solution thus obtained was measured. The result was that 70% of adsorbed dye was desorbed and eluted into the eluent, i.e., N,N-dimethylformamide by the first washing, and that 80% of adsorbed dye was desorbed by the second washing and thereby, the adsorbent resin was decolourized. Example 9. Polystyrene spherical resin adsorbing Blue 4GL dye of Example 2, was added into a reactor and 10 ml N,N- dimethylacetamide was added thereto. After 1 hour, the light absorbency of the solution thus obtained was measured. The result was that 69% of adsorbed dye was desorbed and eluted into the eluent, i.e., N,N-dimethylacetamide by the first washing; and that 80% of adsorbed dye was desorbed by the second washing and thereby, the adsorbent resin was decolourized. Example 10. Polystyrene spherical resin adsorbing Blue 4GL dye of Example 2, was added into a reactor and 10 ml N-methyl-2- pyrrolidinone was added thereto. After 1 hour, the light absorbency of the solution thus obtained was measured. The result was that 71% of adsorbed dye was desorbed and eluted into the eluent, i.e., N-methyl-2-pyrrolidinone by the first washing, and that 80% of adsorbed dye was desorbed by the second washing and thereby, the adsorbent resin was decolourized. Comparative Example 5. The granular active carbon adsorbing Blue 4GL dye of Comparative Example 3, was added into a reactor and 10 ml of dimethylformamide was added thereto. After lhour, light absorbency of the solution was measured. The result was that the dye adsorbed was scarcely eluted. Example 11. Adsorption-desorption tests were repeated more than twenty times by using the polystyrene-g-polyethylene glycol resin adsorbing Blue 4GL dye, of Examples 4 and 8. The results were that the differences between the adsorption efficiencies of the fresh adsorbent resin and those of regenerated adsorbent resin were 0 to 10%. As can be seen in the result of Example 8 to 11 and that of Comparative Example 5, the dye adsorbed on polystyrene-g- polyethylene glycol spherical resin could be desorbed and recovered by using the methods of the present invention. Example 12. Spherical polystyrene resin (200-400 mesh) crosslinked with 2 wt% of divinylbenzene, was reacted with propylene oxide in the presence of Lewis acid catalysts. The resulting resin was reacted with ethylene oxide in high pressure reactor to prepare polystyrene grafted with polyethylene glycol spherical resin. 200 Mg of the spherical resin thus obtained, of which polyethylene glycol content is 68 to 87%, were added into a reactor and 10 ml of Yellow 5 GL dye 10 "4 M solution were added thereto. After 1 hour, light absorbency of the dye solution was measured. The result was that 89 to 99% of dye was decontaminated from the solution. Example 13 . Spherical polystyrene resin (200-400 mesh) crosslinked with 1 wt% of divinylbenzene, was reacted with propylene oxide in the presence of Lewis acid catalysts. The resulting resin was reacted with ethylene oxide in high pressure reactor to prepare polystyrene grafted with polyethylene glycol spherical resin. 200 Mg of the spherical resin thus obtained, of which polyethylene glycol content is 60 to 94%, was added into a reactor and 10 ml of Yellow 5 GL dye 10 "4 M solution were added thereto. After 1 hour, light absorbency of the dye solution was measured. The result was that 78 to 98% of dye was decontaminated from the solution. Example 14. Spherical chloromethylpolystyrene resin (200-400 mesh) crosslinked with 3 wt% of divinylbenzene, was hydrolyzed by metal hydroxide, or aminolyzed by ethanolamine, diethanolamine to introduce hydroxy group thereon. The resulting resin was reacted with ethylene oxide in high pressure reactor to prepare polystyrene grafted with polyethylene glycol spherical resin. 200 Mg of the spherical resin thus obtained, of which polyethylene glycol content is 55 to 92%, were added into a reactor and 10 ml of Yellow 5 GL dye 10 "4 M solution were added into thereto. After 1 hour, light absorbency of the dye solution was measured. The result was that 70 to 95% of dye was decontaminated from the solution. Example 15. Spherical polystyrene resin (200-400 mesh) crosslinked with 1 wt% of divinylbenzene, was reacted with 2-methyltetra hydrofuran in the presence of Lewis acid catalysts. The resulting resin was reacted with ethylene oxide in high pressure reactor to prepare polystyrene grafted with polyethylene glycol spherical resin. 200 Mg of the spherical resin thus obtained, of which polyethylene glycol content is 57 to 91%, was added into a reactor and 10 ml of Yellow 5 GL dye 10 "4 M solution were added thereto. After 1 hour, light absorbency of the dye solution was measured. The result was that 72 to 96% of dye was decontaminated from the solution. Example 16. Spherical polystyrene resin (100-200 mesh) crosslinked with 2 wt% of divinylbenzene, was reacted with propylene oxide in the presence 'of Lewis acid catalysts. The resulting resin was reacted with ethylene oxide in high pressure reactor to prepare polystyrene grafted with polyethylene glycol spherical resin. 200 Mg of the spherical resin thus obtained, of which polyethylene glycol content is 70 to 90%, was added into a reactor and 10 ml of humic acid 250 ppm. solution were added thereto. After 1 hour, chromaticity and COD (Chemical Oxigen Demand) of the dye solution were measured. The result was that 40 to 50% of humic acid was decontaminated from the solution. Example 17. Spherical polystyrene resin (200-400 mesh) crosslinked with 1 wt% of divinylbenzene, was reacted with propylene oxide in the presence of Lewis acid catalysts. The resulting resin was reacted with ethylene oxide in high pressure reactor to prepare polystyrene grafted with polyethylene glycol spherical resin. 200 Mg of the spherical resin thus obtained, of which polyethylene glycol content is 60 to 94%, was added into a reactor and 10 ml of humic acid 250 ppm. solution were added into a reactor. After 1 hour, chromaticity and COD of the dye solution was measured. The result was that 50 to 60 % of humic acid was decontaminated from the solution. Example 18. Spherical polystyrene resin (200-400 mesh) crosslinked with 2 wt% of divinylbenzene, was reacted with propylene oxide in the presence of Lewis acid catalysts. The resulting resin was reacted with ethylene oxide in high pressure reactor to prepare polystyrene grafted with polyethylene glycol spherical resin. 200 Mg of the spherical resin thus obtained, of which polyethylene glycol content is 68 to 87%, were added into a reactor and 10 ml of dodecyl benzene sulfonic acid sodium 10 "4 M solution were added thereto. After 2 hour, light absorbency of the surfactant solution was measured. The result was that 55 to 65 % of surfactant was decontaminated from the solution. Example 19. Spherical polystyrene resin (200-400 mesh) crosslinked with 1 wt% of divinylbenzene, was reacted with propylene oxide in the presence of Lewis acid catalysts. The resulting resin was reacted with ethylene oxide in high pressure reactor to prepare polystyrene grafted with polyethylene glycol spherical resin. 200 Mg of the spherical resin thus obtained, of which polyethylene glycol content is 60 to 94%, were added into a reactor and 10 ml of La(OTf) 3 50 ppm. solution were added thereto. After 2 hour, ICP (inductively coupled plasma) of the metal ionic solution was measured. The result was that 50 to 55% of metal ion was decontaminated from the solution. Example 20 . By using 10ml of Cr 2 (S0 4 ) 3 50 ppm. solution, decontamination of metal ion was measured through the method described in Example 8. The result was that 50 to 60% metal ion was decontaminated from the solution. Example 21. Polystyrene graft polyethylene glycol spherical resin adsorbing Yellow 5GL dye of Example 13, was added into a reactor and 10 ml N,N-dimethylformide was added thereto. After 1 hour, the light absorbency of the solution thus obtained, was measured. The result was that 69% of adsorbed dye was desorbed and eluted into the eluent, i.e., N,N- dimethylformide by the first washing, and that 80% of adsorbed dye was desorbed by the second washing and thereby, the adsorbent resin was decolourized. Example 22. Polystyrene graft polyethylene glycol spherical resin adsorbing Yellow 5GL dye of Example 13, was added into a reactor and 10 ml N,N-dimethylacetamide was added thereto. After 1 hour, the light absorbency of the solution thus obtained, was measured. The result was that 69% of adsorbed dye was desorbed and eluted into the eluent, i.e., N,N- dimethylacetamide by the first washing, and that 80% of adsorbed dye was desorbed by the second washing and thereby, the adsorbent resin was decolourized. Example 23. Polystyrene graft polyethylene glycol spherical resin adsorbing Yellow 5GL dye of Example 13, was added into a reactor and 10 ml N-methyl-2-pyrrolidinone was added thereto. After 1 hour, the light absorbency of the solution thus obtained was measured. The result was that 69% of adsorbed dye was desorbed and eluted into the eluent, i.e., N,N-dimethyl-2-pyrrolidinone by the first washing, and that 80% of adsorbed dye was desorbed by the second washing and thereby, the adsorbent resin was decolourized. Example 24. Polystyrene graft polyethylene glycol spherical resin adsorbing humic acid of Example 17, was added into a reactor and 10 ml N,N-dimethylformide was added thereto. After 1 hour, the light absorbency of the solution thus obtained was measured. The result was that 75% of adsorbed humic acid was desorbed and eluted into the eluent. Example 25 , Polystyrene graft polyethylene glycol spherical resin adsorbing humic acid of Example 5, was added into a reactor and 10 ml N,N-dimethylacetamide was added thereto. After 1 hour, the light absorbency of the solution thus obtained, was measured. The result was that 70% of adsorbed humic acid was desorbed and eluted into the eluent. Example 26. Polystyrene graft polyethylene glycol spherical resin adsorbing humic acid of Example 17, was added into a reactor and 10 ml of N-methyl-2-pyrrolidinone was added thereto. After 1 hour, the light absorbency of the solution thus obtained was measured. The result was that 71% of adsorbed humic acid was desorbed and eluted into the eluent. Example 27. Adsorption-desorption tests as described above were repeated more than twenty times by using the polystyrene resin grafted with polyethylene glycol, which is adsorbing Yellow 5GL dye, of Examples 13 and 21. The results were that the differences between the adsorption efficiencies of the fresh adsorbent resin and those of regenerated adsorbent resin were within 0 to 10%. Example 28. Adsorption-desorption tests as described above were repeated more than twenty times by using the polystyrene resin grafted with polyethylene glycol, which is adsorbing humic acid, of Examples 17 and 24. The results were that the differences between the adsorption efficiencies of the fresh adsorbent re≤in and those of regenerated adsorbent resin were within 0 to 10%. Comparative Example 6. 200 Mg of Zeolite adsorbent for water treatment was added into a reactor and 10 ml of Yellow 5GL dye 10 "4 M solution was added thereto. After 1 hour, the light absorbency of the dye solution was measured. The result was that 1.5% of dye was decontaminated from the solution. Comparative Example 7. 200 Mg of Celite adsorbent was added into a reactor and 10 ml of Yellow 5GL dye 10 "4 M solution was added thereto. After 1 hour, the light absorbency of the dye solution was measured. The result was that 15.5% of dye was decontaminated from the solution. Comparative example 8. 200 Mg of granular active carbon was added into a reactor and 10 ml of Yellow 5GL dye 10 "4 M solution was added thereto. After 1 hour, the light absorbency of the dye solution was measured. The result was that 67.9% of dye was decontaminated from the solution. Comparative Example 9 , 200 Mg of Zeolite adsorbent for water treatment was added into a reactor and 10 ml of humic acid 250 ppm. solution was added thereto. After 1 hour, the COD of the dye solution was measured. The result was that 3% of humic acid was decontaminated from the solution. Comparative Example 10. 200 Mg of Celite adsorbent was added into a reactor and 10 ml of humic acid 250 ppm. solution was added thereto. After 1 hour, the COD of the dye solution was measured. The result was that 15% of humic acid was decontaminated from the solution. Comparative Example 11. 200 Mg of granular active carbon adsorbent was added into a reactor and 10 ml of humic acid 250 ppm. solution was added thereto. After 1 hour, the COD of the dye solution was measured. The result was that 70% of humic acid was decontaminated from the solution. Comparative Example 12. Granular active carbon adsorbing Yellow 5GL dye of Comparative Example 8, was added into a reactor and 10 ml N, N-dimethylformide was added thereto. After 1 hour, the light absorbency of the solution thus obtained, was measured. The result was that dye was scarcely eluted into the solvent. Comparative Example 13. Granular active carbon adsorbing humic acid of Comparative Example 11, ,was added into a reactor and 10 ml N,N- dimethylformide was added thereto. After 1 hour, the light absorbency of the solution thus obtained was measured. The result was that humic acid was scarcely eluted into the solvent. According to the methods of the present invention, dye contained in waste water of dye industry, heavy metal ion cotained in waste water, surfactant, humic substance contained in trash sediment can be decontaminated effectively and quickly by using polystyrene grafted with polyethylene glycol. The polystyrene adsorbent of the present invention represents superior adsorption efficiency than that of traditional inorganic adsorbent. Moreover, in comparison with active carbon, the polystyrene adsorbent of the present invention represents same or superior adsorption efficiency, and particularly, represents excellent properties in adsorption/desorption process of humic acid and in regeneration process of adsorbent, which have never been acknowledged and expected in granular active carbon adsorption method. The more pertinent important features of the present invention have been outlined above in order that the detailed description of the invention which follows will be better understood and that the present contribution to the art can be fully appreciated. Those skilled in the art can appreciate that the conception and the specific Examples disclosed herein may be readily utilized as a basis for modifying or designing other structures for carrying out the same purposes of the present invention. Further, those skilled in the art can realize that such equivalent constructions do not depart from the spirit and scope of the invention as set forth in the claims.

Claims: What is claimed is: 1. A polystyrene spherical resin grafted with polyethylene glycol characterized in that polystyrene resin is crosslinked with 1 to 10 wt% of divinylbenzene, the content of polyethylene glycol is more than 50 wt% and the molecular weight of polyethylene glycol is more than 500 Da. 2. The polystyrene spherical resin grafted with polyethylene glycol of Claim 1, wherein the polystyrene resin is crosslinked with 1 to 8 wt% of divinylbenzene. 3. The polystyrene spherical resin grafted with polyethylene glycol of Claim 1, wherein the polystyrene resin is crosslinked with 1 to 6 wt% of divinylbenzene. 4. The polystyrene spherical resin grafted with polyethylene glycol of Claim 1, wherein the content of polyethylene glycol is 50 wt% to 99 wt%. 5. A process for decontamination of dye from waste water by adsorption and desorption method, wherein an adsorbent is _ a polystyrene spherical resin grafted with polyethylene glycol characterized in that the polystyrene resin is crosslinked with 1 to 10 wt% of divinylbenzene, the content of polyethylene glycol is more than 50 wt% and the molecular weight of polyethylene glycol is more than 500 Da. 6. A process for recovering dye by using organic solvent from a polystyrene spherical resin grafted with polyethylene glycol characterized in that the polystyrene resin is crosslinked with 1 to 10 wt% of divinylbenzene, the content of polyethylene glycol is more than 50 wt% and the molecular weight of polyethylene glycol is more than 500 Da, whereon dye is adsorbed. 7. The process of Claim 6, wherein the organic solvent is selected from the group consisting of dimethylformamide, dimethylacetamide and N-methyl-2- pyrrolidinone . 8. A process for decontamination of humic substance, surfactant and heavy metal ion contained in trash sediment water by adsorption and desorption method, wherein an adsorbent is a polystyrene spherical resin grafted with polyethylene glycol charaterized in that the polystyrene resin is crosslinked with 1 to 10 wt% of divinylbenzene, the content of polyethylene glycol is more than 50 wt% and the molecular weght of polyethylene glycol is more than 500 Da. 9. A process for recovering a polystyrene spherical resin adsorbent grafted with polyetylene glycol charaterized in that the polystyrene resin is crosslinked with 1 to 10 wt% of divinylbenzene, the content of polyethylene glycol is more than 50 wt% and the molecular weght of polyethylene glycol is more than 500 Da, through a elutriate process by using organic solvent selected from the group consisting of dimethylformamide, dimethylacetamide and N-methyl-2- pyrrolidinone.

Inventors: LEE YOON SIK, RYOO SUN JONG, LEE, YOON, SIK, RYOO, SUN, JONG
Applicants: BEADTECH INC, LEE YOON SIK, RYOO SUN JONG, BEADTECH INC., LEE, YOON, SIK, RYOO, SUN, JONG
Application year: 1999
Main classification: C08F257
IPC codes: B01D15, B01J20, C02F1, C08G65