CONTROL OF HYDROGEN AND CARBON MONOXIDE PRODUCED IN PARTIAL OXIDATION PROCESS

Abstract: A process for enhancing H2 or CO production in a partial oxidation reaction by feeding H2O or CO2 with the feed hydrocarbon and oxygen over a transition metal monolith catalyst such as unsupported Ni monolith or alternatively contacting the hydrocarbon/oxygen first with a noble metal then with a transition metal with the H2O or CO2 being added before or after the noble metal catalyst. The addition of H2O suppresses CO and enhances H2 production and the addition of CO2 suppresses H2 and enhances CO production. Little steam or CO2 reforming occurs with the addition of up to 32 % H2O or CO2 respectively. Thus, the ratio of H2:CO which is about 2 in a conventional partial oxidation is manipulated by the addition of either water or CO2 to the partial oxidation.

Description: CONTROL OF HYDROGEN AND CARBON MONOXIDE PRODUCED IN PARTIAL OXIDATION PROCESS BACKGROUND OF THE INVENTION Field of the Invention The present invention relates to a process and apparatus for production of H2 or CO by the partial oxidation of hydrocarbons, preferably methane. In particular the partial oxidation is carried out in the presence of water or carbon dioxide under water-gas shift reaction conditions. The invention was made with government support under DOE Grant No. DE-FG02-88ER13878-A02. The government has certain rights in the invention. Related Art Catalytic steam reforming of methane is currently the main industrial process to produce synthesis gas (CO and H 2 ) • The steam reforming reaction may be represented as: CH + H 2 0 ► CO + 3H 2 Reforming is highly endothermic, requiring energy input and also requiring contact times on the order of seconds. The resultant high H 2 /CO ratio is also unsuitable for methanol and Fischer-Tropsch synthesis. Therefore additional downstream reactors are usually required to adjust this ratio by water-gas shift reaction at contact time of «1 second as: CO + H 2 0 < ► H 2 + C0 2 Partial oxidation, on the other hand, is an exothermic reaction which can be represented by the reaction of methane with oxygen as follows: CH 4 + 0 2 ► CO + 2H 2 To produce synthesis gas by steam reforming, high temperature heat input is primarily required at two process steps. First, sufficient steam at a high temperature and high pressure must be generated for mixing with the hydrocarbon feedstock and, second, the steam reforming of the steam and hydrocarbon mixture must take place at relatively high temperatures and pressures through a bed of solid catalyst. The equipment needed for these two heat transfers at high temperature and high pressure is necessarily quite expensive. The equipment for the steam reforming step is also costly because it must be adapted to permit the changing of the solid catalyst when that catalyst is spent or poisoned. Heat sources appropriate for the above two process steps are typically provided by fired heaters at high, continuing utility costs, also with high fluegas NO x production consequential to the high temperatures required in the furnace firebox. The production of synthesis gas by partial oxidation is considered a desirable alternative to steam reforming since it overcomes some of the problems of steam reforming, see for example PCT publication WO 90/06282 and WO 90/06297. U.S. Pat. No. 4,844,837 to Heck et al discloses a catalytic partial oxidation method for methane using a monolith catalyst with platinum-palladium, palladium- rhodium, or platinum-rhodium coatings. U.S. Pat. No. 4,087,259 to Fujitani et al describes a monolith catalyst with a rhodium coating to perform catalytic partial oxidation on gasoline and heavier petroleum fractions. U.S. Pat. No. 5,648,582 to Schmidt et al discloses the partial oxidation of methane at short residence times using metal deposited on a ceramic monolith. In these conventional partial oxidations, methane (natural gas) is converted to high purity H 2 and CO with a mole ratio of H 2 :CO ^2.0, which is the desired feed ratio for methanol and Fischer-Tropsch plants. However, many other applications require different ratios of H 2 :C0. The present synthesis gas shift reactor modifies the prior processes to obtain either high purity H 2 or CO. Recent advancements in fuel cell technology have spurred an interest in converting natural gas into hydrogen. Pure hydrogen streams can be produced by steam reforming followed by high temperature shift using an Fe based catalyst, and low temperature shift using a Cu based catalyst. For natural gas to be an effective H source for fuel cells, the present natural gas conversion technology must be simplified, preferably to a single, highly selective small catalytic reactor. Other applications include acetic acid production, which requires pure CO feeds. We have discovered that the H 2 :CO product ratio can be altered by the addition of C0 2 or H 2 0 through the water- gas shift reaction while the conversion of CH 4 remains constant, indicating negligible reforming is occurring. SUMMARY OF THE INVENTION Briefly, the present invention is a process for the partial oxidation of hydrocarbons such as methane (natural gas) by contacting a feed containing the hydrocarbon and oxygen and H 0 or C0 2 through a catalyst zone containing a catalytically effective amount of at least one transition metal monolith catalyst under partial oxidation conditions. A preferred monolith catalyst is a nickel metal monolith. When H 2 0 is fed, the product shifts toward the H 2 and when C0 2 is present the product shifts toward CO, thus the presence of either water or C0 2 provides the means to adjust the H 2 :C0 ratio, preferably in the range of more than about 2 to about 6 when water is added and in the range of less than about 2 to about 0.5 when C0 2 is added. It appears that the presence of water or C0 2 in the reaction zone according to the present invention produces a water-gas shift rather than reforming. In a further embodiment the process comprises a first contacting a feed comprising methane and oxygen feed with or without H 2 0 or C0 2 with a noble metal coated onto a monolith. The H 2 0 or C0 2 may be fed through the noble metal monolith or between the noble metal monolith and the transition metal monolith. Because partial oxidation reactions are exothermic, it is not necessary to add external heat to the system other than to obtain ignition of the catalyst. BRIEF DESCRIPTION OF THE DRAWINGS Fig. 1 shows the conversion of CH 4 and selectivities to H 2 with C0 2 addition over Ni. Fig. 2 shows the conversion of CH4 and selectivities to H 2 with C0 addition over Rh. Fig. 3 shows the conversion of CH 4 and selectivities to H 2 with C0 2 addition over Pt. Fig. 4 shows the conversion of CH 4 and selectivities to CO with H 2 0 addition over Ni. Fig. 5 shows the conversion of CH 4 and selectivities to CO with H 2 0 addition over Rh. Fig. 6 shows the conversion of CH 4 and selectivities to CO with H 2 0 addition over Pt. Fig. 7 compares the selectivity to CO in the product with the addition of H 2 0 over Ni, Rh, and Pt. Fig. 8 compares the ratio of the H 2 in the product to the CH 4 in the feed with the addition of H 2 0 over Ni, Rh, and Pt. Fig. 9 compares the ratio of CO/C0 2 in the product with the addition of H 2 0 over Ni, Rh and Pt. Fig. 10 compares the conversion of CH 4 with the addition of H 2 0 over Ni, Rh, and Pt. Fig. 11 discloses a single bed catalyst reaction system according to the present invention. Fig. 12 discloses a multibed catalyst reaction system according to the present invention. Fig. 13 discloses an alternative multibed catalyst reaction system according to the present invention. DETAILED DESCRIPTION The present catalyst is comprised of a monolith structure either composed of the metal of the catalyst or coated with the metal of the catalyst. The metals may be in the oxide form during use in the present process. The thickness of the monolith through which the feed gas mixture must pass is from 1 mm to 2 cm. Catalyst contact time ranges from 0.1 to 20 milliseconds when using a monolith of 50% porosity and 0.2 to 1 cm in depth. Under operating conditions, this corresponds to Gas Hourly Space Velocity (GHSV) of 60,000 to 3,000,000 hr "1 . Ceramic foam monoliths have been found in the present invention to create the superior mass transfer characteristics necessary if high space velocities are to be used. The metal monolith may be prepared as metal foam or sintered particles of metal. The solid metal monoliths exhibit superior heat transfer properties but may require substantial amounts of very expensive metals in some embodiments. Thus, in some applications the metal coated ceramics will be the catalyst of choice. As used herein the term "metal monolith" shall include both the solid metal monoliths and the metal coated ceramic monoliths. The solid metal monoliths may be produced by any method, for example foaming, sintering and fusing. The reactor is started from ambient temperature through the use of a mixture of light hydrocarbons or ammonia and air preheated to about 200°C and then introduced to the monolith catalyst at an appropriate temperature at which combustion will occur. After combustion has established a monolith catalyst temperature of near 1000 °C, preheat and ammonia is stopped. The feed gas mixture of hydrocarbons (methane) and oxygen is then fed to the catalyst zone at a temperature of from 25° ' to 450 °C. Thus, the gas feed mixture of the present invention does not require preheating to near its ignition temperature prior to introduction to the catalyst, thereby avoiding the production of C0 2 and H 2 0 and the concurrent reduction of the selectivity for H 2 and CO. With the introduction of water or carbon dioxide to the reaction in accordance with the present invention, the preheat of the feed is adjusted to maintain the established outlet temperature. The amounts of hydrocarbon, H 2 0, C0 2 and oxygen introduced into the partial oxidation (catalyst zone) are controlled to provide 0 2 :C ratios of from about 0.2 to 0.8 and H 2 0 or C0 2 :C ratios of about 0.5 to 5. The process is carried out from about atmospheric pressure to about 2000 psig. The amount of water or C0 2 added is preferably up to 45%, more preferably 5 to 35% of the gaseous feed. Because the hydrocarbon conversion remains constant with or without the H 2 0 or C0 2 it appears that little or no reforming is occurring. Thus the present partial oxidation in the presence of H 2 0 or C0 2 is characterized as occurring in the substantial absence of reforming. The predominant reaction in the presence of water or C0 2 is characterized as a water-gas shift reaction. In a preferred embodiment of the present invention, catalytic partial oxidation, an exothermic reaction, takes place in a catalyst monolith having a specified transition metal alone or preceded by a noble metal dispersed to produce a gas which is rich in carbon monoxide and hydrogen. The reaction in the catalytic partial oxidation zone is exothermic and the zone is therefore also referred to as an exothermic catalyst zone. The exothermic, catalytic partial oxidation zone comprises either solid metal monolith and/or a monolithic catalyst carrier or carriers on which transition or transition and noble metal catalyst is dispersed. Such catalyst can effectively catalyze the partial oxidation of, in addition to, gaseous and lighter hydrocarbon liquids such as natural gas or paraffinic naphtha, heavier hydrocarbon liquids such as diesel oil, number 2 fuel oil, and coal derived liquids. As compared to a non-catalytic combustion process such as conventional, non-catalytic partial oxidation, catalytic partial oxidation as described above enables the utilization of lesser amounts of oxygen and lower temperature levels to both oxidize a portion of the feed and crack heavier feedstocks to lighter hydrocarbon fractions while raising the temperature of the reactant mass for subsequent treatment. Generally, at least about half the hydrocarbon feed stock is partially oxidized in the catalytic partial oxidation zone to produce primarily carbon monoxide and hydrogen and heat. Substantially all of the oxygen introduced into the catalytic partial oxidation zone is consumed in the partial oxidation step. The oxygen introduced into the catalytic partial oxidation zone is consumed in the catalytic partial oxidation step. The oxygen may be provided by any suitable "oxygen-containing oxidant gas" which term is used in the claims to include air, air enriched with oxygen, oxygen or oxygen mixed with other gases. The effluent gas from the catalytic partial oxidation zone contains primarily CO, H 2 , H 2 0, N 2 , C 2 to C 4 and other lighter hydrocarbons, including olefins, and, depending upon the sulfur content of the feedstock, H 2 S and COS. Methane is the preferred feed for H 2 or CO production. The presence of H 2 0 (steam) results in a favorable shift in the product of the H 2 :CO ratio to H 2 , whereas the presence of C0 2 shifts the ratio in favor of CO. The combination of features provided by the present invention provides a highly efficient and flexible method of converting various types of hydrocarbonaceous feeds to a hydrogen-rich gas. For example, the combination of features provided by the process of the present invention provides a highly efficient process of manufacturing a synthesis gas by converting various types of hydrocarbonaceous feeds, including hydrocarbon feeds, to a nitrogen and hydrogen-rich gas suitable for use in ammonia synthesis. By utilizing the catalytic partial oxidation process as described, a wide variety of hydrocarbonaceous feeds may be efficiently and economically converted into a hydrogen-rich gas. The Monolithic Partial Oxidation Catalysts The partial oxidation catalyst either comprises or is supported on a monolithic carrier, that is, a carrier of the type comprising one or more monolithic bodies having a plurality of finely divided gas flow passages extending therethrough. Such monolithic carrier members are often referred to as "honeycomb" type carriers and are well known in the art. A preferred form of such carrier is made of a refractory, substantially inert, rigid material which is capable of maintaining its shape and a sufficient degree of mechanical strength at high temperatures, for example, up to about 3,373°F. (l,856 β C). Typically, a material is selected for the support which exhibits a low thermal coefficient of expansion, good thermal shock resistance and, though not always, low thermal conductivity. Two general types of material for construction of such carriers are known. One is a ceramic-like porous material comprised of one or more metal oxides, for example, alumina, alumina-silica, alumina-silica-titania, mullite, cordierite, zirconia, zirconia-spinal, zirconia-mullite, silicon carbide, etc. A particularly preferred and commercially available material of construction for operations below about 2,000°F. (1,093°C.) is cordierite, which is an alumina-magnesia-silica material. For applications involving operations above 2,000°F. (1,093°C) an alumina-silica-titania material is preferred. Honeycomb monolithic supports are commercially available in various sizes and configurations. Typically, the monolithic carrier would comprise, e.g., a cordierite member of generally cylindrical configuration (either round or oval in cross section) and having a plurality of parallel gas flow passages or regular polygonal cross section extending therethrough. The gas flow passages are typically sized to provide from about 50 to 1,200, preferably 200 to 600, gas flow channels per square inch of face area. Various honeycombed (reticulated) ceramic structures are described in the art: U.S. Pat. No. 4,251,239 discloses fluted filter of porous ceramic having increased surface area; U.S. Pat. No. 4,568,595 discloses honeycombed ceramic foams with a surface having a ceramic sintered coating closing off the cells; U.S. Pat. No. 3,900,646 discloses ceramic foam with a nickel coating followed by platinum deposited in a vapor process; U.S. Pat. No. 3,957,685 discloses nickel or palladium coated on a negative image ceramic metal/ceramic or metal foam; U.S. Pat. No. 3,998,758 discloses ceramic foam with nickel, cobalt or copper deposited in two layers with the second layer reinforced with aluminum, magnesium or zinc; U.S. Pat. No. 4,863,712 discloses a negative image honeycombed (reticulated) foam coated with cobalt, nickel or molybdenum coating; U.S. Pat. No. 4,308,233 discloses a reticulated ceramic foam having an activated alumina coating and a noble metal coating useful as an exhaust gas catalyst; U.S. Pat. No. 4,253,302 discloses a foamed ceramic containing platinum/rhodium catalyst for exhaust gas catalyst; and U.S. Pat. No. 4,088,607 discloses a ceramic foam having an active aluminum oxide layer coated by a noble metal containing composition such as zinc oxide, platinum and palladium. The foam structure is characterized by the number of pores per linear inch and typical foams are produced with 10 to 100 pores per linear inch. The ceramic supports employed in the present invention are generally of the type disclosed in U.S. Pat. No. 4,810,685 using the appropriate material for the matrix and are generally referred to in the art and herein as "monoliths". Generally any organic liquid in which the metal salt is soluble may be used to deposit metals on to monolith supports. The metals may also be deposited from aqueous solutions using the water soluble salts. Generally from 0.5 to 20 wt % of the metal will be deposited on the monolith (based on the weight of monolith) . A suitable high surface area refractory metal oxide support layer may be deposited on the carrier to serve as a support upon which finely dispersed catalytic metal may be distended. As is known in the art, generally, oxides of one or more of the metals of Groups II, III, and IV of the Periodic Table of Elements having atomic numbers not greater than 40 are satisfactory as the support layer. Preferred high surface area support coatings are alumina, beryllia, zirconia, baria-alumina, magnesia, silica, and combinations of two or more of the foregoing. The most preferred support coating is alumina, most preferably a stabilized, high-surface area transition alumina. One or more stabilizers such as rare earth metal oxides and/or alkaline earth metal oxides may be included in the transition alumina (usually in amounts comprising from 20 to 10 weight percent. The metal monolith may be prepared as metal foam or sintered particles of metal at high temperature. Monolithic supports may also be made from materials such as nickel or stainless steel by placing a flat and a corrugated metal sheet, one over the other, and rolling the stacked sheets into a tubular configuration about an axis parallel to the corrugations, to provide a cylindrical- shaped body having a plurality of fine, parallel gas flow passages extending therethrough. The transition metals useful in the present invention are selected from the groups consisting of Fe, Os, Co, Rh, Ir, Ni Cu, Pd, Pt and mixtures thereof, with Fe, Co, Ni or Cu forming a preferred grouping, more preferably Ni and more preferably as a solid nickel monolith. Nickel supported on alumina monoliths was not found to be useful in the present process. The noble metals useful in the present invention are selected from the group consisting of Ru, Rh, Pd, Pt and mixtures thereof preferably Pt or Pd. For Figs. 1-10 runs were carried out in a quartz tube continuous reactor with 18 mm diameter. Identical α-Al 2 0 3 monoliths without metal were positioned before and after the catalyst to reduce radiation losses. The catalyst and radiation shields were sealed in the quartz reactor by silica-alumina cloth. The temperatures of the front and back sides of the catalyst were measured with Pt-Pt/Rh thermocouples placed between the catalyst and the radiation shields. Rh and Pt catalysts were ignited with a Bunsen burner at a CH 4 /0 2 ratio of 1.8. The fresh Ni spheres were more difficult to ignite, and therefore NH 3 was added to the feed to lower ignition temperature. After ignition, the reactor was insulated by wrapping it in high temperature insulation. Rh and Pt catalysts were prepared by impregnating α- Al 2 0 3 foam monoliths (18 mm diameter by 10 mm long) with concentrated metal salt solutions (rhodium chloride in acetone or chloroplatinic acid in H 2 0) which were added dropwise to the monolith and allowed to dry overnight. The samples were further dried at 390 K for 2 hours and then calcined at 870° K for 2 hours in He and reduced at the same temperature in 10% H 2 /Ar for 7 hrs. However, spheres of sintered Ni activated over a period of 6 hours (at normal reaction conditions) catalyzed an oxidation reaction in which the conversion and selectivities steadily increased. Therefore pure sintered Ni metal spheres (Alfa, -40 mesh, deposition grade, 99.9%) packed to 1 cm deep were used directly. Similar results were obtained with foamed nickel monolith. Flow rates of high purity 0 2 , N 2 , C0 2 and CH 4 were controlled by mass flow controllers with an accuracy of +0.01 standard liters per minute (slpm) . Initial experiments with no C0 2 or H 2 0 added to the feed were conducted at 4 slp , CH 4 /0 2 = 1.8 and 35% dilution, which is optimal fuel/oxygen ratio for syngas production. For all of the C0 results presented here, the N 2 was replaced by C0 2 to maintain a constant contact time within the catalyst. The exit temperature of the catalyst was held constant by preheating the feed gases. Runs were repeated where C0 2 was added to a constant flow of CH 4 , 0 2 and N 2 . These results are nearly identical and show the same trends as the data presented here and are omitted. For runs in which steam was added to the feed, water was supplied by a syringe pump through a two stage vaporizer and a back pressure regulator to eliminate system pulsing. In all results reported, H 2 0 was added to a constant flow of CH 4 , 0 2 and N 2 . Product gases were analyzed by a HP 5890 gas chromatograph with a thermal conductivity detector and integrated by an on-line computer. The detected reaction products were H 2 , CO, C0 2 and H 0 on all catalysts, and over Pt up to 1% C 2 products were observed. CH 4 conversion and products selectivities were calculated as described previously. For C0 2 addition, the selectivities to CO and C0 2 are not reported (the only carbon containing product that is not a reactant is CO) . Similarly H 2 and H 2 0 selectivities are not reported for H 2 0 addition. In all runs the carbon and hydrogen balances closed with an accuracy better than 97%. Figs. 1-3 show the conversions of CH 4 and selectivities to H 2 with C0 2 addition on Ni, Rh and Pt catalysts. The reaction temperatures on Ni, Rh and Pt catalysts were held constant with C0 2 addition, 1240°, 1250° and 1500° K, respectively. The equilibrium predictions of CH 4 conversion and H 2 selectivities at these temperatures are shown by the dashed lines. Since Pt produces a lower H 2/ H 2° ratio, its temperature is ~250°C hotter than Ni or Rh. The CH 4 conversions were nearly constant up to 30% C0 2 addition on all three catalysts, but significantly lower than the equilibrium CH 4 conversions which is nearly 100%. These results imply that little C0 reforming of CH 4 occurs at contact times of «5 ms and «1300°K. Fig 1 also shows that the conversion of CH 4 is higher on Rh (80%) than on Ni (72%) with Pt (54%) being much less active. The addition of C0 2 decreases the selectivity to H 2 over all three catalysts, but to very different amounts. With 24% Cθ 2 addition on Ni, the H 2 selectivity decreases from 80% to 55%, on Rh it decreases from 84% to 67%, and on Pt it decreases from 59% to 41%. The H selectivities are roughly parallel to, but lower than, the calculated equilibrium H 2 selectivities. These results indicate that C0 2 reacts with H 2 in the reverse water-gas shift reaction to a greater extent on Ni and least on Pt. Addition of H 2 0 The results of H 2 0 addition with a constant flow of CH 4 , 0 , and N 2 over Ni, Rh or Pt are shown in Figs. 4-6. In these runs, the temperature was kept constant at the adiabatic temperature in the absence of H 2 0 by preheating the gas stream. Because of preheat limitations, maintaining a constant temperature on the Pt catalyst at greater than 12 Vol% H 0 feed was difficult and therefore is not reported. Figs. 4-6 show that the CH 4 conversions were nearly constant over the entire range of H 2 0 addition on all three catalysts, indicating that negligible steam reforming of CH 4 is occurring under these conditions. As H 2 0 is added to the feed the selectivity to CO decreases on Ni and Rh but remains essentially constant over Pt. On Ni, the selectivity to CO decreases from 88% to 50% while on Rh the selectivity only drops from 94% to 87%. The H 2 0 seems to be reacting with CO by the water-gas shift reaction over Ni and Rh but not over Pt. The present results exhibited no catalyst deactivation on unsupported Ni and on supported Pt and Rh for over 100 hours of operation at atmospheric pressure. The present data also show that as the concentration of C0 2 in the feed increases, the conversion of CH 4 remains constant. This clearly shows that C0 2 reforming is not occurring significantly at temperatures near 1300° K, at contact times near 1 ms and in the presence of oxygen. Although these results may seem contradictory to previous literature, three distinct factors differentiate this work from previous results. First, the present reactor runs adiabatically and autothermally, therefore the reaction temperature is controlled by the catalyst selectivity and the temperatures typically run 250 to 500" hotter than typical C0 2 reforming runs. Second, the contact time over the catalyst in our runs is approximately 1 s, corresponding to a gas hourly space velocity GHSV of -lxl0 5 h _1 , which is approximately a factor of 10 higher than most previous C0 2 reforming work. Finally, the presence of 0 2 may inhibit C0 reforming reactions. The CH 4 is probably reacting with 0 2 very rapidly, and the extremely short contact times prevent the remaining CH 4 from reacting with C0 2 . Similar results have been reported by Choudhary et al , Catal. Lett. 32 (1995) 391-396 over NiO-CaO catalyst at space velocities of up to 5xl0 5 cm 3 g -1 h -1 and temperatures up to 900 °C. For C0 2 reforming in the absence of 0 2 , the NiO-CaO catalyst coked very rapidly, but when 0 2 is added to the feed, the catalyst showed no deactivation due to coke formation. They used their results to show that the addition of 0 2 overcomes the endothermic limitations of C0 2 reforming by initially combusting part of the CH 4 . The energy released by combustion can then be immediately used to drive the reforming reactions. They confirmed this by calculating the ratio of C0 2 reforming to oxidative conversion of CH 4 based on the chemistry being controlled by three reactions: 1) partial oxidation of CH 4 with 0 2 to syngas, 2) complete combustion of CH 4 , 3) and C0 2 reforming of CH 4 . Although, this may be a valid explanation of the product distribution in these experiments, it is believed that present results are better described by the direct oxidation of CH 4 to syngas followed by water-gas shift. Figs. 1-3 show that as C0 2 is added to the feed, the conversion of CH 4 does not change when the outlet temperature is held constant, for example by preheating the feed, indicating that C0 2 reforming of CH 4 is probably not active at these contact times and temperatures. However, as C0 2 is added the selectivity to H 2 decreases over all three metals. This implies that C0 2 is reacting with H 2 in the reverse water-gas shift. The present results show that the water-gas shift reaction is being affected by the addition of H 2 0, particularly over the Ni monolith. H 2 0 seems to be reacting with CO in the forward water-gas shift to form C0 2 and H 2 . The combination of the C0 2 and H 2 0 addition results strongly confirm the activity of the water-gas shift reaction and its reverse at >1000° K and 1 ms contact time. As with C0 2 reforming, steam reforming seems to be inactive over Ni, Rh or Pt at high temperatures and millisecond contact times. This is probably because the CH 4 preferentially reacts with 0 2 first, and the remaining CH 4 does not react with the H 2 0 at these extremely short contact times. This is. expected from the relatively low sticking coefficients of C0 2 and H 2 0 compared to 0 2 . The present results show that addition of C0 2 or H 2 0 to the feed stream affects the selectivity to H 2 and CO but leaves the conversion of CH 4 unaffected. The short contact times, 10 to 10 ms, do not allow significant C0 2 or steam reforming on any of the three metals, and the dominant reaction is the direct oxidation of CH 4 to CO and H 2 . Since the H 2 selectivity decreases with the addition of C0 2 (or CO selectivity decreases with the addition of H 2 0) , the water-gas shift reaction or its reverse must be active at present reaction temperatures and contact times. Therefore, it is believed that the direct partial oxidation of CH 4 to syngas followed by the water-gas shift reaction are the dominant reactions in the present invention. Figs. 1-6 show that at contact times near 1 ms, the direct partial oxidation of methane to syngas appears to be followed by water-gas shift or its reverse. Because the water-gas shift reaction is active at 1300° K and 1 ms, the product selectivities can be tuned from high CO to high H 2 content by introducing C0 2 or H 2 0 respectively into the feed stream. The negligible steam or C0 2 reforming occurs in the presence of 0 2 over unsupported Ni and α-Al 2 03 supported Rh and Pt catalysts at contact times of 1-10 ms and 1300 K. However, the water-gas shift reaction and the reverse shift reaction are active over Ni and Rh, with Pt being less active. Over Ni, the C0/C0 2 ratio decreases to 1 at 30% H 2 0 addition, which tranlates to a H 2 /C0 ratio of 5. This demonstrates the addition of H 2 0 or C0 2 can be used to manipulate the ratio of H 2 /CO in the product stream. In Fig. 11 an apparatus with a single transition metal catalyst is illustrated. Hydrocarbon/0 2 flow 8 is in the direction of the arrow into tubular reactor 10. H 2 0 (as steam) or C0 2 enters via line 12 into a bead packing 22. The tubular reactor 10 is wrapped with heating tape and the catalyst 14 is sandwiched between two heat shields 16 and insulated by 18. In Fig. 12 an apparatus with a multi-catalyst zone is shown in tubular reactor 100. Hydrocarbon/0 2 feed enters 108 in the direction of the arrow to flow through the reactor. H 2 0 (steam) or C0 enter into beads 122 via 112 and the mixture contacts noble metal catalyst 114 then transition metal (preferred group) 115. The two catalyst monoliths are associated with heat shields 116 and insulated by 118. The front portion of the reactor containing the beads is wrapped with heating tape 120. Fig. 13 is a modification of the apparatus of Fig. 12. The hydrocarbon/0 2 feed 208 enters the tubular reactor 200 and passes through noble metal monolith catalyst 214 which is sandwiched between heat shields 216. That section is insulated by 218. The reaction has been initiated by igniting the catalyst 214. The product from this partial oxidation passes into the bead packing 222 where it mixes with H 2 0 (steam) or C0 entering via 212. The mixture proceeds through transition metal (preferred group) monolith catalyst 215. Heating tape is provided to maintain the temperature from the exothermic partial oxidation. It has been found that unsupported metal monoliths such as nickel monolith is advantageous over ceramic supported metals. Because of the high thermal conductivity of Ni, the monolith is a better thermostat and higher flow rates can be achieved with similar selectivities and conversions. By using unsupported Ni, the possibility of nickel- aluminate formation and therefore a deactivation route is eliminated. These two advantages combined allow for operation over wider range of inlet conditions. The multiple catalyst bed design takes advantage of a more selective catalyst for synthesis gas formation. In this design the first bed is a supported noble metal catalyst, preferably Rh. This catalyst is supported by a reticulated or extruded ceramic structure and the weight loadings of catalyst can range from 0.1% to in excess of 10%. Steam or C0 2 is injected immediately following the first catalyst bed prior to entering the second bed. The second bed requires energy input to maintain reaction. This catalyst can be a noble metal, transition metal or metal oxide, like Ni, Fe, or Cu. To initiate reaction, the feed gases are introduced to the reactor at the desired flow rate and composition. Energy is added to the catalyst either electrically or thermally until the catalyst ignites. After catalyst ignition the energy source is removed, and preheat is the only external energy source required to maintain reaction temperatures between 800° and 1000°C. For the multi-bed reactor, the second and beyond stages may need to be maintained at temperature either by external heating or from the energy released in the first stage. Gas hourly space velocities -10 5 h -1 have been used for the process. Inlet compositions of fuel and oxygen were taken from literature sources for the optimal production of synthesis gas. Natural gas was simulated by CH 4 , the dominant component of natural gas. The inlet compositions ranged from 64% fuel, 36% oxidant to 35% fuel, 20% oxidant and 45% H 2 0 or C0 2 . The introduction of H 2 0 into the feed stream results in a decrease in the CO/C0 2 ratio. With no H 2 0 the CO:C0 2 ratio is 8:1, but with 40% H 2 0 feed the ratio is reduced to 1.3:1 when using an unsupported bed of nickel. Adding C0 2 instead of H 2 0 results in a decrease in the H 2 :H 2 0 ratio from 9:1 to 1:1 again over a nickel catalyst. Similar results have been demonstrated over Rh and Pt catalysts.

Claims: The invention claimed is: 1. A process for the partial oxidation of hydrocarbons by feeding a stream containing hydrocarbon, oxygen and H 2 0 or C0 2 through a catalyst zone containing a catalytically effective amount of at least one transition metal monolith catalyst under partial oxidation conditions wherein said transition metal is selected from the group consisting of Fe, Ru, Os, Co, Rh, Ir, Ni, Cu, Pd, and Pt. 2. The process according to claim 1 wherein the transition metal is Ni or Rh. 3. The process according to claim 1 wherein said catalyst comprises a nickel metal monolith. 4. The process according to claim 1 wherein said catalyst zone contains one transition metal catalyst. 5. The process according to claim 4 wherein the transition metal is Ni or Rh. 6. The process according to claim 1 wherein H 2 0 is fed with said hydrocarbon and oxygen. 7. The process according to claim 1 wherein C0 2 is fed with said hydrocarbon and oxygen. 8. The process according to claim 1 wherein at least said hydrocarbon and said oxygen are contacted with a noble metal monolith catalyst under partial oxidation conditions prior to contacting said transition metal monolith catalyst wherein said noble metal is selected from the group consisting of Ru, Rh, Pd, Ir, and Pt. 9. The process according to claim 8 wherein H 2 0 is fed with said hydrocarbon and oxygen to contact said noble metal catalyst. 10. The process according to claim 8 wherein C0 2 is fed with said hydrocarbon and oxygen to contact said noble metal catalyst. 11. The process according to claim 8 wherein said H 2 0 is fed to said stream after said noble metal monolith catalyst and prior to said transition metal monolith catalyst. 12. The process according to claim 8 wherein said C0 2 is fed to said stream after said noble metal monolith catalyst and prior to said transition metal monolith catalyst. 13. The process according to claim 1, 4, 6, 7, 8, 9, 10, 11, or 12, wherein said transition metal is selected from the group consisting of Fe, Ru, Os, Co, Rh, Ir, Ni, and Cu. 14. The process according to claim 13 wherein said transition metal is Fe, Cu, or Ni. 15. The process according to claim 14 wherein said transition metal is Cu. 16. The process according to claim 14 wherein said transition metal is Ni. 17. The process according to claim 8, 9, 10, 11, or 12, wherein said noble metal is selected from the group consisting of Pd and Pt. 18. The process according to claim 17 wherein said noble metal is Pt. 19. The process according to claim 17 wherein said noble metal is Pd. 20. The process according to claim 3 wherein said nickel monolith comprises a foam. 21. The process according to claim 3 wherein said nickel monolith comprises sintered nickel particles. 22. The process according to claim 1 wherein the feed gas to the reaction is preheated to a temperature in the range of 25-450°C. 23. The process according to claim 22 wherein the pressure of the process is in the range of atmospheric to 2000 psig.

Inventors: SCHMIDT LANNY D, WITT PAUL M, SCHMIDT, LANNY, D., WITT, PAUL, M.
Applicants: UNIV MINNESOTA, REGENTS OF THE UNIVERSITY OF MINNESOTA
Application year: 1999
Main classification: C01B3
IPC codes: C01B3