AIR ENTRAINMENT WITH POLYOXYALKYLENE COPOLYMERS FOR CONCRETE TREATED WITH OXYALKYLENE SRA

Abstract: The present invention relates to a method and air entraining admixtures (AEAs) for achieving satisfactory levels of air entrainment in a hydraulic cementitious composition, such as concrete or mortar, in which an oxyalkylene shrinkage reduction admixture (SRA) is used with, or to be used in combination with, a water soluble salt, such as a calcium salt. Addition of exemplary polyoxyalkylene copolymers, preferably nonionic and substantially di-block in structure, and preferably having a molecular weight of at least 1,000 and more preferably at least 2,000, are described for controlling air entrainment. Increased air entrainment effect is further realized when such polymers are used with conventional AEAs, such as tall oils and vinsol resin.

Description: AIR ENTRAINMENT WITH POLYOXYALKYLENE COPOLYMERS FOR CONCRETE TREATED WITH OXYALKYLENE SRA Inventors: Noah D. Budiansky, Brent S. Williams, and Byong-Wa Chun Field of the Invention The present invention relates to the field of concrete admixtures, and more particularly to controlling air entrainment in hydraulic cementitious compositions treated with oxyalkylene shrinkage reducing admixtures ("SRAs") and/or water soluble salts such as calcium nitrite and/or calcium nitrate. Background of the Invention Air entrainment is important for increasing resistance of hydraulic cementitious compositions, such as mortar, masonry, and concrete, to frost attack and deterioration due to repeated freezing and thawing. Entrained air is desirable, therefore, for long-term durability of concrete or mortar in adverse freeze-thaw conditions. Technically speaking, air entraining agents or admixtures (AEAs) do not generate air in the concrete, but merely stabilize the air either (1) infolded and mechanically enveloped during mixing, (2) dissolved in the mix water, (3) originally present in the intergranular spaces in the dry cement and aggregate; or (4) in the pores of the aggregate. While it is true that the entrained air is within the total mass of concrete, it is only entrained in the paste portion of the mix. Entrained air is fundamentally different than "entrapped" air. Most of the air that is in concretes, in the absence of admixtures, is often referred to as "entrapped" air. Entrained air is characterized by uniformly dispersed, spherical spaces in cement paste; whereas entrapped air is characterized by irregularly shaped voids which are not generally uniformly sized but generally larger than "entrained" air voids. See e.g., Concrete Admixtures, Vance Dodson (Van Nostrand Reinhold, New York 1990), P. 129 et seq. The present inventors have discovered an air entrainment problem that arises when oxyalkylene based shrinkage reducing admixtures (SRAs), in concrete and mortar, are used in conjunction with water soluble salts. Oxyalkylene SRAs are known in the art. For example, U.S. Patent 5,413,634 of Shawl et al., incorporated herein by reference, discloses an alkyl ether derivative of an aliphatic polyhydroxy compound containing an oxyalkylene group. When an oxyalkylene SRA is used with a water soluble salt (such as calcium nitrite), however, sufficient and controllable levels of entrained air are difficult to attain. This was found to be the case even when the SRAs were used in combination with conventional air entraining agents, such as tall oil and vinsol resin. Accordingly, a novel air entraining admixture or system is needed. Summary of the Invention In surmounting the difficulties of the prior art, the inventors have discovered that polyoxyalkylene copolymers provide stable and controllable entrained air, in concrete and mortar, with oxyalkylene shrinkage reducing admixtures (SRAs) and particularly for such SRAs used in combination with water soluble salts, such as alkali or alkaline earth metal salts, preferably calcium salts such as calcium nitrite, calcium nitrate, or a mixture thereof. An exemplary method of the invention, for improving air entrainment in a hydraulic cementitious composition having an oxyalkylene SRA, comprises introducing to the oxyalkylene SRA a polyoxyalkylene copolymer. Preferably, the copolymer is a nonionic block copolymer, preferably having a predominantly di- block structure, and having a molecular weight of at least 1000. Further exemplary methods include introducing into a hydraulic cementitious composition an oxyalkylene SRA, a water soluble salt, (preferably a calcium salt, e.g., calcium nitrite), and a polyoxyalkylene di-block copolymer. These can be added separately or combined as one or two components. Exemplary admixtures of the invention comprise a mixture of an oxyalkylene SRA, optionally a water soluble salt (e.g. , calcium nitrite), and a polyoxyalkylene copolymer. In further exemplary embodiments, an additional and conventional AEA, such as tall oil, vinsol resin, can be used to improve air . ~> .. entrainment further. The present invention further relates to cement compositions comprising an oxyalkylene SRA, a water soluble salt (e.g., calcium nitrite), and a polyoxyalkylene copolymer. In especially preferred methods and admixtures, an oxyalkylene SRA comprising di-propylene-t-butyl ether is added to the cementitious composition with a polyoxyalkylene copolymer which comprises a block-like structure comprised substantially of polyethylene oxide and another block-like structure comprised substantially of a higher polyalkylene (such as oxypropylene and/or oxybutylene) groups, the copolymer having a molecular weight of at least 1000, preferably at least 2000, and more preferably at least 4000. Further features and advantages of the invention are described hereinafter. Detailed Description of the Invention The term "cement composition" as may be used herein refers to pastes, mortars, grouts such as oil well cementing grouts, and concrete compositions comprising a hydraulic cement binder. The terms "paste" , "mortar" and "concrete" are terms of art: pastes are mixtures composed of a hydraulic cement binder (usually, but not exclusively, Portland cement, Masonry cement, or Mortar cement and may also include limestone, hydrated lime, fly ash, blast furnace slag, and silica fume or other materials commonly included in such cements) and water; mortars are pastes additionally including fine aggregate, and concretes are mortars additionally including coarse aggregate. The cement compositions tested in this invention are formed by mixing required amounts of certain materials, e.g., a hydraulic cement, water, and fine or coarse aggregate, as may be applicable to make the particular cement composition being formed. The present invention allows for air entrainment in concrete containing oxyalkylene SRAs in conjunction with water soluble salts (especially calcium salts, and particularly calcium nitrite). It has been unexpectedly found that small doses of relatively higher molecular weight (e.g. , at least 1,000) polyoxyalkylene copolymers (non-ionic, primarily di-block) provide stable, controllable, and desirable degrees of entrained air in concrete containing the above durability enhancing admixtures. Exemplary polyoxyalkylene copolymers suitable for use in the invention preferably have substantially block, more preferably predominantly di-block. structures. A preferred polyoxyalkylene copolymer, having approximately 4000 molecular weight (50% by weight polyethylene, 50% by weight polypropylene, di- block polymer) was obtained from Arco Chemical under the tradename POLYOL R2633, and tested as described further below. Other exemplary polyoxyalkylene copolymers suitable for use in the present invention have the following general formula: R 1 - [OA 1 ],,. - [OA 2 ] n - OR 2 ; or R 1 - [OA 2 ] n - [OA 1 ] m - OR 2 wherein R 1 and R 2 comprise a hydrogen, an alkyl group (e.g. , C, - C 7 ), a cyclo alkyl group (e.g. , C 5 - C 6 ), or an aryl group; OA 1 is a generally hydrophilic oxyalkylene group wherein O represents oxygen and A 1 comprises primarily ethylene groups; and OA 2 is a generally hydrophobic oxyalkylene group wherein O represents oxygen, and A 2 comprises primarily propylene groups (including isopropylene), butyl groups (including t-butyl), or a mixture thereof; m is an integer of 5 - 200; and n is an integer of 5 - 200. Preferably, the sum of m and n is in the range of 10 to 400. More preferably, m and n are each an integer of about 30 - 60. R 1 and R 2 are preferably a hydrogen or methyl group. The polyoxyalkylene copolymer may have a molecular weight of about 100-10,000 (EO/PO block form), and preferably at least 1,000; more preferably, at least 2,000; and most preferably at least 4,000 mol. weight. The foregoing statement that A 1 comprises primarily ethylene groups is an acknowledgment that "OA 1 " may not be purely ethylene oxide, but may include a small portion (less than 50% and preferably less than 20%) larger alkylenes such as propylene or butylene. In other words, the ethylene oxide group should predominate in OA 1 because this is believed to confer hydrophilicity to the copolymer. Similarly, the foregoing statement that A 2 comprises predominantly higher alkylene groups, namely propyl and/or butyl groups, is an acknowledgment that OA 2 may not be pure but may contain some ethylene groups but the propyl and/or butyl groups should predominate since these higher alkyl groups are believed to confer hydrophobicity to the copolymer. The combination of hydrophilicity and hydrophobicity is therefore desired. Exemplary oxyalkylene shrinkage reduction admixtures (SRAs) which are believed to be suitable for purposes of the present invention include alkyl ether derivatives of aliphatic polyhydroxy compounds such as glycerin. Dialkyl ether derivatives, especially tertiary butyl ethers of glycerin are preferred. An especially preferred SRA is di-propylene glycol tertiary-butyl ether ("DTBE"), combined with di-propylene glycol, which is available from W. R. Grace & Co. -Conn., Cambridge, Massachusetts, under the tradename ECLIPSE™. US Patents 3.663,251 and 4,547,223, for example, suggest the use of compounds of the general formula RO(AO) n H in which R may be a C, - C 7 alkyl or C 5 - C 6 cycloalkyl radical, A may be a C, - C 3 alkylene radical, and n is 1-10, as shrinkage reducing additives for cement. The references are incorporated as if fully set forth herein. A further oxyalkylene SRA suitable for use in the invention is disclosed in U.S. Patent 5,556,460 of Berke et al. , which is incorporated herein by reference. Berke et al. disclosed an SRA admixture comprising a low molecular weight oxyalkylene compound and a comb polymer having carboxylic acid groups and oxyalkylene units therein. More particularly, such an exemplary SRA comprises: (A) at least one oxyalkylene glycol, oxyalkylene ether glycol or mixtures thereof having a molecular weight up to about 4000; and (B) a comb polymer of a molecular weight of from 2,000 to 100,000 having (i) carboxylic acid anhydride, free carboxylic acid or its ammonium, alkali or alkaline earth metal salt and (ii) C 2 - C 5 oxyalkylene units or mixtures of said units, wherein said units (i) or (ii) being pendant from the polymer backbone chain and said units (ii) provide the majority of the molecule. The at least one oxyalkylene compound may be selected from (i) oxyalkylene glycols represented by the formula HOAOH or HO(AO) n H wherein A represents a C 2 - C ]0 alkylene group, O represents an oxygen atom, and n represents an integer of from 1 to about 80; (ii) oxyalkylene adducts of monoalcohols represented by the formula RO(AO) m H wherein R represents a C, - C 7 alkyl or a C 5 - C 6 cycloalkyl group, A represents a C 2 - C 4 alkylene group, O represents an oxygen atom and m represents an integer of from 1 to about 10; and (iii) oxyalkylene adducts of polyols represented by the formula Q[(OA) p OR'] x wherein Q represents a C 3 - C 12 aliphatic hydrocarbon residual group of a polyhydroxyalkane, each R' independently represents a C, - C 14 alkyl or cycloalkyl group or hydrogen atom provided at least one R' of said adduct represents a C, - C 14 alkyl or cycloalkyl group; A represents a C 2 - C 4 alkylene group; O represents an oxygen atom; p represents an integer of from 0 to about 10; and x represents an integer of from 3 to 5; and (iv) mixtures of said oxyalkylene compounds. Still further exemplary oxyalkylene SRAs suitable for use in the invention may comprise oxyalkylene ether adducts with higher alkylene diols, as described in U.S. Patent 5,618,344 of Kerkar et al. , incorporated herein by reference. It is further known in the art to combine oxyalkylene SRAs with alkylene glycols, as discussed for example in Taiwan Patent No. NI-076751 issued June 13, 1996, to Arco Chemical Technology, L.P., which is incorporated herein by reference. The Taiwan patent disclosed a mixture of (a) at least one alkyl ether oxyalkylene adduct represented by the formula RO(AO) π H wherein A is an alkylene (e.g., C 2 - C 4 ) group, O is an oxygen atom, R is an alkyl group (e.g. , C 3 - C 5 ), and n is an integer from 1 to 3; and (b) an oxyalkylene glycol represented by the formula HO(AO) m H wherein A is an alkylene radical (e.g. , C 2 - C 4 ), O is an oxygen atom, and m is an integer of 1 to 3. Preferred SRAs of component (a) include, therefore, dipropylene glycol t-butyl ether, tripropylene glycol t-butyl ether, and mixtures thereof. Preferred oxyalkylene glycols of component (b) include dipropylene glycol, tripropylene glycol, and mixtures thereof. Accordingly, the present invention includes combinations of oxyalkylene SRAs, such as the ones described above, with conventional AEAs such as dipropylene glycol or other short chain glycols. in addition to the polyoxyalkylene copolymers described herein as part of the novel AEA admixtures. Exemplary water soluble salts which may be used in the invention include cations such as Ca + + , Na + , H + , K + , Mg + + , Cs + , Rb + , Fr + , or a mixture thereof, in combinations with anions such as nitrates (-NO 3 ), nitrites (NO 2 ), chlorides (-C1), and thiocyanates (-SCN). Preferred salts are calcium nitrite, calcium nitrate, or a mixture thereof. Other exemplary salts include CaCl 2 , NaNO 3 , NaS 2 O 4 , and NaCl. In exemplary methods and admixture compositions of the present invention, the amounts of the various components may be used in the general ranges, depending upon the nature of the mix and quality of the cement: oxyalkylene SRA and water soluble salt, each in the range of about 0.01 - 10% s/s (percentage weight solids based on weight of cement), and more preferably 0.05-5% s/s; and polyoxyalkylene copolymer in the range of about 0.005-5.0% s/s, and more preferably 0.01-0.5% s/s. The invention may be more readily comprehended when the following examples are considered. Example 1 A series of micro-concrete mixes were prepared to determine air entrainment characteristics of samples having a conventional air entrainer and an oxyalkylene SRA with a water soluble salt, such as calcium nitrite. The micro-concrete was made by blending 1500 parts Type I Portland Cement (170-1) with a mixture of the following ASTM-graded sands: 1040 parts F- 95 sand, 945 parts C-109 sand, 945 parts C-185 sand, and 1796 parts Q-Rok sand. The dry blending was conducted in a Hobart mixer for approximately 30 seconds to attain a uniform blend having an aggregate to cement ratio of 3: 15. A 0.50 water/cement (w/c) ratio with no additional superplasticizers, air entrainers or other admixtures was used as a baseline for a level (4.4%) of total entrapped air (See #1 mix, "control"). To the dry blend of aggregate and cement, 750g of water was added during the first 40 seconds of mixing time. A mixing schedule proceeded as follows: 0-40 seconds (water, admixtures added), 0-5 minutes mixing at the lowest speed setting, 5-8 minutes rest (covered), 8-9 minutes mixing (uncovered). After 9 minutes, air content was determined by ASTM C-185 test protocol. Slump was determined by JIS Standard # A- 1173. The above procedure was repeated for the remaining mixes in which an oxyalkylene SRA (available from Grace under the name "ECLIPSE™") was added (mix #2), a water soluble salt such as calcium nitrite (sold by Grace under the tradename "DO ® ") was added (mix #3), each with a conventional tall oil air entraining agent (DAREX ® II). The water/cement ratio was reduced when naphthalene sulphonate based superplasticizers were used to keep the flow the same as the reference (control) mix. A water cement ratio of 0.45 was used. A sample mix was made using both the oxyalkylene SRA and calcium nitrite (#4), and the entrained air fell to 1.5%, which was a remarkable drop from sample #2 (SRA alone) and #3 (salt alone). In each of samples #5 through #8, the amount of the conventional air entraining admixture (tall oil) was increased; but the percentage of entrained air did not return to the level of either SRA or salt alone (# 3, #4). The amount of tall oil was measured in terms of percentage weight solids based on 100 parts weight of cement. The results are tabulated in Table 1 below. Table 1 As seen in Table 1 , when a conventional air entrainer such as tall oil at a dosage of 0.0133 % s/s is used to entrain air in mortar containing typical doses of the oxyalkylene SRA ("ECLIPSE™" brand)and water soluble salt ("DCI ® " brand calcium nitrite sold as a corrosion inhibitor), it was found that only 1.5% air was entrained (See mix #4). At higher doses, slightly more air (up to 3.1 % in mix #8) was entrained but not enough for optimum freeze thaw resistance in mortar. Example 2 Further testing was done on SRA/salt mixtures along the lines described above using a polyoxyalkylene copolymer (Arco Polyol R2633, 4000 molecular weight, 50% by weight polyethylene, 50% by weight polypropylene, di-block). This revealed a surprising and unexpected effect on air entrainment. In sample mix #9, the SRA ("ECLIPSE™") and salt ("DCI ® ") were mixed and dosed with ARCO POLYOL R2633, and 5.2% entrained air was obtained. This was substantially larger than the 3.1% air entrained by the conventional air entrainer (see mix #8, example 1). In a further sample mix (#10), the polyethylene-polypropylene glycol AEA was also used with a conventional tall oil AEA (available from Grace under the tradename DAREX ® II), and the entrained air was 21.5% ; this was surprising. In yet a further sample mix (#11), the polyoxyalkylene copolymer AEA was used with a conventional vinsol resin (available from Grace under the tradename DARAVAIR ® 1000), and the entrained air was 19.3% which was surprising. The data clearly indicates that the use of the polyoxyalkylene copolymer AEA in conjunction with conventional AEAs has a synergistic effect resulting in controllable and desirable levels of entrained air in mortar. The results are provided in Table 2 below. Table 2 In view of mix nos. 10 and 1 1, which contained conventional AEAs, the present invention further comprises the use of conventional AEAs in combination with the polyoxyalkylene copolymer. a combination which is seen to provide synergistic increases in the level of air entrainment. Accordingly, the present invention is also directed at novel AEA combinations for oxyalkylene SRAs, comprising a polyoxyalkylene copolymer as described above (preferably nonionic, predominantly di-block in structure, with a molecular weight of at least 1000), and a second AEA which has a different structure than the copolymer. The second AEA may, for example, comprise one or more known AEAs, such as a fatty alkanolamids, ethoxylated fatty amine, ethoxylated fatty acid, ethoxylated triglyceride, ethoxylated alkylphenol, ethoxylated alcohol, alkyl ethoxylate, alkylaryl ethoxylate; a cationic AEA such as amine ethoxylate and amine oxide; an amphoteric AEA such as a betaine; an anionic AEA such as a fatty alkyl ether sulfate, a fatty alkylaryl ether sulfate, a alkyl benzene sulfonate, a sulfosuccinate, a fatty sulfonate, or a mixture thereof. As previously mentioned, di-propylene glycol and or tripropylene glycol may be used as, or with, other conventional AEAs. The present invention is also directed to novel cement compositions which comprise an oxyalkylene SRA (preferably di-propylene glycol t-butyl ether), a calcium salt (preferably calcium nitrite); a polyoxyalkylene copolymer; and optionally one or more conventional AEAs, such as dipropylene glycol, tripropylene glycol (or other short chain oxyalkylene polymers), or other AEAs as previously described above. The foregoing examples are provided by way of illustration only and are not intended to limit the scope of the invention. Example 3 Further testing was conducted in laboratory concrete. Mixes containing: 611 lbs./yd of cement, 1229 lbs./yd fine aggregate, 1700 lbs./yd coarse aggregate, 270 lbs./yd water (0.44 W/C) were mixed according to laboratory practices. Slump, air content (by pressure method), and unit weight were tested immediately after mixing. As seen in Table 3, mixes containing the SRA, water soluble salt (DCI * brand sold as a corrosion inhibitor), superplasticizer, and conventional air entrainer produced unacceptable air contents (Mixes 1 and 2). As seen in these microconcrete mixes, the addition of a small amount of oxyalkylene copolymer (ARCO * R2633) aided in producing acceptable entrained air contents. In Table 3, mixes 3, 4, and 5 show these results Table 3 Example 4 Concrete testing was further tested in field applications. Six sites were used for field testing opportunities of oxyalkylene copolymer (ARCO * R2633) when SRAs and water-soluble salt admixtures were required. Concrete mixes ranged in cement, pozzolan, coarse aggregate, fine aggregate, and water/cement ratio (W/C). Mix proportions are shown in Table 4. In all mixes, SRA, water-soluble salt admixture, superplasticizer, and conventional air entrainer were added prior to imtial air tests. In Trial 1, Tests 1 and 2, the oxyalkylene copolymer (ARCO R2633) was added up front in the truck before air tests were conducted. Additional copolymer was added after initial air tests to desired air was attained. In trials two through six, an initial air reading was taken prior to copolymer addition. As in seen mixes two through six, significant increases in entrained air were seen with the addition of the oxyalkylene copolymer. The results are shown below. Table 4 Table 5

Claims: It is claimed: 1. A method for improving air entrainment in a hydraulic cementitious composition having an oxyalkylene shrinkage reduction admixture (SRA), comprising introducing to the SRA a polyoxyalkylene copolymer. 2. The method of claim 1 wherein said polyoxyalkylene copolymer has a predominantly di-block structure. 3. The method of claim 2 wherein a first block-like structure of said di- block structure comprises predominantly ethylene oxide groups, and a second blocklike structure of said di-block structure comprises higher alkylene oxide groups comprising propylene oxide, butylene oxide, or a mixture thereof. 4. The method of claim 1 further comprising adding an alkali or alkaline earth metal salt into said composition. 5. The method of claim 4 wherein said salt comprises a calcium salt. 6. The method of claim 3 wherein said calcium salt comprises calcium nitrite, calcium nitrate, or a mixture thereof. 7. The method of claim 1 wherein said SRA comprises has the general formula RO(AO) n H in which R is H, an alkyl, a cycloalkyl, or an aryl group; A is an alkylene radical, and n is an integer 1-10. 8. The method of claim 1 wherein said SRA comprises an alkyl ether derivative of an aliphatic polyhydroxy compound of the formula Q-[(A) n -OR)] x wherein Q is a C 3 - C 12 aliphatic hydrocarbon group, R is hydrogen or C, - C 16 alkyl, at least one R being the - C 16 - alkyl group, A is C 2 - C 4 oxyalkylene, n is 0-10, and x is 3-5. 9. The method of claim 1 wherein said polyoxyalkylene copolymer has the general formula R 1 - [OA 1 ] m - [OA 2 ] n - OR 2 ; or R 1 - [OA 2 ] n - [OA 1 ] m - OR 2 wherein R 1 and R 2 comprise a hydrogen, an alkyl group, a cyclo alkyl group, or an aryl group; OA 1 is a generally hydrophilic oxyalkylene group wherein O represents oxygen and A 1 comprises primarily ethylene groups; and OA 2 is a generally hydrophobic oxyalkylene group wherein O represents oxygen and A 2 comprises primarily propylene groups, butylene groups, or a mixture thereof; m is an integer of 5 - 200; and n is an integer of 5 - 200. 10. The method of claim 9 wherein the sum of m and n is in the range of 10 to 400. 11. The method of claim 10 wherein m and n are each an integer of about 20 - 70. 12. The method of claim 9 wherein R 2 m and n are each an integer of 30 - 60. 13. The method of claim 9 wherein both R 1 and R 2 are selected from hydrogen or methyl. 14. The method of claim 1 wherein said polyoxyalkylene copolymer has a molecular weight of at least 1000. 15. The method of claim 1 wherein said polyoxyalkylene copolymer has a molecular weight of at least 2000. 16. The method of claim 1 wherein said oxyalkylene SRA is di-propylene glycol t-butyl ether, and said polyoxyalkylene copolymer has a molecular weight of at least 2000. 17. The method of claim 16 further comprising adding a conventional AEA comprising an alkylene glycol polymer. 18. The method of claim 16 further comprising adding a conventional AEA comprising dipropylene glycol, tripropylene glycol, a tall oil, vinsol resin, or a mixture thereof. 19. The method of claim 16 further comprising adding a further air entraining agent comprising a fatty alkanolamide, ethoxylated fatty amine, ethoxylated fatty acid, ethoxylated triglyceride, ethoxylated alkylphenol, ethoxylated alcohol, alkyl ethoxylate, alkylaryl ethoxylate; a cationic AEA such as amine ethoxylate and amine oxide; an amphoteric AEA such as a betaine; and an anionic AEA such as a fatty alkyl ether sulfate, a fatty alkylaryl ether sulfate, a alkyl benzene sulfonate, a sulfosuccinate, and a fatty sulfonate. 20. A method for modifying the properties of a hydraulic cementitious composition, comprising: adding an oxyalkylene SRA, a water soluble calcium salt, and a polyoxyalkylene copolymer having a molecular weight of at least 1000. 21. The method of claim 20 wherein said copolymer is nonionic and has substantially a di-block structure wherein a first of said block structures confers a hydrophobic nature to the copolymer and a second of said block structures confers a hydrophilic nature to the copolymer. 22. The method of claim 1 further comprising adding a further AEA that is different from said polyoxyalkylene copolymer. 23. A composition for entraining air in a hydraulic cementitious composition having an oxyalkylene SRA, comprising: a polyoxyalkylene copolymer and at least one AEA comprising a polyoxyalkylene polymer that has a molecular weight less than 1,000, tall oil, vinsol resin, as a fatty alkanolamids, ethoxylated fatty amine, ethoxylated fatty acid, ethoxylated triglyceride, ethoxylated alkylphenol, ethoxylated alcohol, alkyl ethoxylate, alkylaryl ethoxylate; a cationic AEA such as amine ethoxylate and amine oxide; an amphoteric AEA such as a betaine; an anionic AEA such as a fatty alkyl ether sulfate, a fatty alkylaryl ether sulfate, an alkyl benzene sulfonate, a sulfosuccinate, a fatty sulfonate, or a mixture thereof. 24. A hydraulic cementitious composition comprising at least one oxyalkylene SRA, a water soluble salt, a polyoxyalkylene copolymer, and optionally an AEA selected from the group comprising an oxyalkylene glycol polymer, a tall oil, vinsol resin, or a mixture thereof.

Inventors: BUDIANSKY NOAH D, CHUN BYONG-WA, WILLIAMS BRENT S, BUDIANSKY, NOAH, D., CHUN, BYONG-WA, WILLIAMS, BRENT, S.
Applicants: BUDIANSKY NOAH D, CHUN BYONG WA, GRACE W R & CO, WILLIAMS BRENT S, BUDIANSKY, NOAH, D., CHUN, BYONG-WA, W. R. GRACE & CO.-CONN., WILLIAMS, BRENT, S.
Application year: 1999
Main classification: C04B24
IPC codes: C04B24, C04B28, C08G65, C08L71