Bearing material

Abstract: A material for use as a bearing sliding surface and a bearing having the material are described, the material comprises tin and having therein from 1 to 5wt% of a metal selected from the group comprising nickel, cobalt and iron.

Description: The present invention relates to plain sliding bearings and particularly, though not exclusively, to bearings having a so-called overlay alloy layer which is deposited on the surface of a second, thicker layer of bearing alloy. Plain bearings such as half bearing shells for internal combustion engine crankshaft connecting rod and main bearings for example frequently comprise at least three distinct layers: a first layer of a strong supporting material such as steel; a second layer of a bearing alloy bonded to the backing layer comprising a copper-lead based alloy or an aluminium-tin based alloy for example; and, a third, thinner layer and generally softer than the second layer, of a so-called overlay alloy which endows the bearing with properties of inter alia conformability and dirt embedability. Many known overlay alloy systems contain high proportions of lead and include such systems as lead-indium, lead-tin and lead-tin-copper for example. It is a possibility that environmental legislation will render the use of lead in overlay alloys unacceptable at some time in the future. The problem is two-fold: firstly; there is the problem of dealing with lead containing effluents and residues generated as a result of electro-deposition of the overlays from electrolytes; and secondly there is the problem of the lead containing bearings themselves which may present an environmental hazard when vehicles are scrapped. Pure tin coatings have been used in the past as so-called sacrificial coatings on the surface of plain bearings. These coatings have been very thin, about 2 to 3µm, which is intended to wear away as a new engine "beds in". However, such sacrificial tin coatings have been deposited on top of other conventional overlay coatings such as those described above which are intended to remain for the life of the engine. EP-A-0 254 355 describes an overlay alloy for a plain bearing, the overlay alloy consisting of tin having from 0.5 to 15wt% of cobalt therein. Tin-nickel electro-deposits have been known for decades, principally as decorative coatings to replace chromium coatings. The deposits are hard, intermediate between nickel and chromium, and have good corrosion resistance. Such coatings generally contain 30 to 35wt% of nickel and comprise mainly the intermetallic compound, Ni 3 Sn 4 . It is an object of the present invention to provide a lead-free material which may be used as a sliding bearing material for a plain bearing. It is a further object to provide a plain bearing having a lead-free sliding bearing material coating thereon. According to the present invention there is provided a plain bearing having a bearing sliding surface, the sliding surface comprising tin and having therein from 1 to 5wt% of nickel apart from unavoidable impurities. Preferably, the nickel content may be from 1.5 to 3.5 wt%. More preferably still, the nickel content may be from 2 to 3 wt%. The lower limit of 1wt% nickel is chosen because below this level the strengthening effect of the nickel is insufficient to endow adequate fatigue and/or wear resistance. Above 5wt% nickel, the alloy becomes relatively hard and brittle for use as a soft bearing material, particularly where used as an overlay coating, and also the fatigue strength thereof tends to decline above this level. The material may be deposited directly on to a strong supporting material backing such as steel but more preferably may be deposited on a layer of another harder (harder than the overlay alloy) bearing material which is itself bonded to a strong backing material such as steel for example. The harder bearing material may be any known bearing material suitable for the intended operating application. However, an aluminium alloy based bearing material is preferred since this combination may provide a completely lead-free bearing. The material according to the present invention may be deposited by an electroplating route or by a physical vapour deposition route such as cathodic sputtering for example. The form of the alloy in its as-deposited state is a solid solution of the nickel in the tin matrix. However, this is a metastable form and the stable form is a tin matrix having a dispersion of Ni 3 Sn 4 intermetallic compound therein. The intermetallic compound does precipitate out at temperatures in excess of 100°C. X-ray diffraction work has shown that some Ni 3 Sn 4 is present after 14 hours at 160°C but not after 10 hours at this temperature. However, the size of the precipitate is very small which tends to strengthen the coating providing good fatigue and wear resistance but still endowing the coating with a low hardness of 18 H k (1g Knoop indenter) so that the desired properties of conformability and dirt embedability are not impaired. For comparison, the hardness of lead-9wt%tin is 8H k and that of lead-10wt%tin-2wt%copper is 15H k . When used as a bearing sliding surface directly on a steel backing for example, the thickness may lie in the range from 50 to 75µm for example. When used as an overlay coating on a substrate of another, harder bearing material, the thickness may lie in the range from about 5 to 50µm with a range of about 10 to 20µm being preferred. If used as a thin sacrificial surface coating as described above, the thickness may be in the range from about 1 to 5µm. When deposited onto the surface of another bearing alloy there may be an interlayer of pure nickel, copper or copper alloy (eg copper-zinc) for example to act either as a diffusion barrier and/or to enable the bearing material according to the present invention to be more adherent to the surface thereof. In order that the present invention may be more fully understood, an example will now be described by way of illustration only with reference to the accompanying drawings, of which: Figure 1 shows a histogram of fatigue test results for a material according to the present invention compared with other known overlay materials; and Figure 2 which shows a histogram of wear test results of materials according to the present invention compared with other known bearing overlay materials. Bearings having deposits of tin-2.2/2.5 wt% nickel were produced by electroplating in a plating bath having an electrolyte comprising: Stannous chloride 28g/l Nickel chloride 2.5g/l Potassium pyrophosphate 192g/l Glycine 20g/l Anode material nickel The plating conditions were: Cathode current density 1.0 ASD Temperature 50°C pH 8.4 The bearings produced comprised a steel backing having a layer of aluminium-silicon alloy based bearing material thereon and also having an approximately 1µm thick pure nickel interlayer thereon and on which the overlay bearing material according to the present invention was deposited according to the conditions described above. The wall thickness of the bearings was approximately 1.8mm and included a layer of the inventive alloy about 20µm thick. The bearings produced were tested for fatigue strength in a known "Sapphire" testing machine. The results of theses tests is given in Table 1 below: Sapphire Fatigue Strength- MPa Overlay Hard Tin Tin-2.2Nickel Tin-5Nickel Substrate Al/Si alloy Al/Si alloy Al/Si alloy Fatigue Strength Mpa 76 97 83 55 83 62 55 90 62 0 83 55 83 83 79 76 83 55 Average Fatigue Strength- MPa 6.9 86.5 64 As may be seen from Table 1, the overlay comprising tin-2.2wt% nickel has an average fatigue strength of 86.5 MPa which is greater than the so-called hard tin coating known in the prior art and also the tin-5wt% nickel overlay coating also tested. These results are shown in the histogram of Figure 1 where it may be seen that the tin-2.2wt% material is also stronger than both lead-7wt% indium and lead-10wt% tin-2wt% copper overlays which have heretofore been considered to be amongst the strongest of the available overlay alloys known in the art. Figure 2 shows a histogram comparing wear test results of alloys comprising tin-2.5wt% nickel according to the present invention; lead-10wt% tin-4wt% copper and lead-10wt% tin-2wt% copper. It may be seen that over several tests the wear rate of the alloy according to the present invention is a factor of at least 5 or more lower than the two comparative alloys. Experience has shown that in bearing tests in actual engines the difference is likely to be closer to a factor of 2. The test conditions were: Imposed load 2.7kg Oil type Visco 15W40 Oil temp. 140°C Duration 30 min. Shaft speed (rev/min) 1000 Surface finish (Ra) 0.11 Shaft diameter 45mm Bearing internal diameter 52.8mm

Claims: A plain bearing having a bearing sliding surface, the sliding surface comprising a tin matrix and having therein from 1 to 5wt% of nickel apart from unavoidable impurities. A plain bearing according to claim 1 wherein the nickel content is from 1.5 to 3.5 wt%. A plain bearing according to claim 2 wherein the nickel content is from 2 to 3 wt%. A plain bearing according to any one preceding claim wherein the sliding surface is an overlay alloy deposited either by an electroplating route or by a physical vapour deposition route A plain bearing according to claim 4 wherein the physical vapour deposition technique is cathodic sputtering. A plain bearing according to any one preceding claim wherein the nickel is in solid solution in the tin matrix. A plain bearing according to any one of preceding claims 1 to 5 wherein the nickel is in the form of an intermetallic precipitate in the tin matrix. A plain bearing according to either claim 4 or claim 5, the bearing comprising a strong backing material, a layer of a bearing material on the backing material and said overlay alloy on the bearing material.

Inventors: LYON JOHN, RUTHERFORD FATIMA, LYON, JOHN, RUTHERFORD, FATIMA
Applicants: DANA CORP, DANA CORPORATION
Application year: 1999
Main classification: C22C13
IPC codes: C25D7, C25D3, C22C13, C23C14, F16C33