Flame-retarded transparent plastics

Abstract: Flame-retarded transparent plastic composition comprising polyhalogenated trimethylphenyl indan. The polyhalogenated trimethylphenyl indan is a mixture of polyhalogenated trimethylphenyl indanes having each 3 to 9 halogen atoms. The halogen may be bromine or a mixture of bromine and chlorine. The transparent plastic is selected from polycarbonate, polymethylmethacrylate, polystyrene, styrene-acrylonitrile copolymer, and poly (vinyl chloride). The polyhalogenated trimethylphenyl indan is present in an amount of up to about 40% by weight. The transparent plastic flame-retarded material is prapared by mixing the plastic material with a flame-retardant effective amount of a polyhalogenated trimethylphenyl indan.

Description: Field of the Invention This invention relates to new flame-retarded transparent plastics. More specifically, the invention relates to the use of polyhalogenated trimethylphenyl indanes in transparent plastics. Background of the Invention Flame retardants (FR) are the most important family of plastic additives. Synthetic polymers and copolymers are often compounded with the fire retardant compounds in order to improve their FR properties. Typical FRs comprise inorganic and organic compounds, particularly aromatic compounds. Halogenated compounds are the most effective, and bromine is often the preferred halogen. The addition of FR compounds also affects the mechanical properties of the plastic material, often negatively. European Patent No. 571036 claims thermally stable fire retardants which also impart good impact properties. The fire retardants of said application are additives of polyhalogenated trimethylphenyl indanes. The preparation of 1,1,5-trimethyl-3-phenyl indan (TMPI) is disclosed in DE 2,906,294, DE 2,659,597 and USP 3,161,692. Providing FR transparent plastic materials is an important goal. However, most FR materials available in the art present severe drawbacks. For instance, some of them are based on brominated diphenyloxide nuclei (such as, decabromodiphenyl oxide), which is suspected of releasing dioxins under some conditions. Other FR compounds cannot be incorporated in sufficient amounts without severely affecting the transparency of the resulting composition. It is therefore an object of the present invention to provide FR additives for use in transparent plastic materials, which overcome the aforesaid drawbacks of prior art additives. It is another object of the invention to provide transparent FR thermoplastic compositions containing a very high (greater than 15% by weight) load of FR material. Such compositions are useful in a variety of applications, as will be further described below. SUMMARY OF THE INVENTION The invention is directed to flame-retarded transparent plastic composition comprising polyhalogenated trimethylphenyl indan. According to a preferred embodiment of the invention, polyhalogenated trimethylphenyl indanes having each 3 to 9 halogen atoms are utilized. Also according to a preferred embodiment of the invention, the number of halogen atoms of at least a part of the polyhalogenated trimethylphenyl indan in the mixture is 7 or 8, and the halogen is bromine. Illustrative examples of such polyhalogenated trimethylphenyl indanes are a mixture of hexa-, hepta-, and octabromotrimethylphenyl indan, which mixture is also known as FR-1808 ex Bromine Compounds Ltd. The halogen can be bromine, or a mixture of bromine and chlorine. Any suitable plastic material can be employed. According to a preferred embodiment of the invention the transparent plastic is selected from polycarbonate, polymethylmethacrylate, polystyrene and styrene-acrylonitrile, copolymer poly (vinyl chloride) (PVC). The amount of polyhalogenated trimethylphenyl indan which can be present in the plastic material varies with the intended use. For instance, for rendering transparent plastic materials flame-retarded, with acceptable impact strength of the resulting products, total contents of up to about 8% are usually preferred. For other uses, such as for the manufacturing of transparent elements such as lens, light guides, optical fibers and compact disks, having a high refractive index, much higher contents, up to about 40% by weight, are needed, preferably in an amount of up to about 15% by weight. Throughout this specification, unless specifically otherwise stated, all percentages are by weight. The invention is also directed to a method for the preparation of transparent plastic flame-retarded material comprising mixing said plastic material with a flame-retardant effective amount of a polyhalogenated trimethylphenyl indan. According to a preferred embodiment of the invention, the polyhalogenated trimethylphenyl indan is a mixture of brominated derivatives containing 70-75% bromine. The invention also encompasses the use of polyhalogenated trimethylphenyl indanes in the preparation of transparent plastic materials having a higher refractive index. The mixture of brominated derivatives containing 70-75% bromine, such as FR-1808, is a particularly suitable compound for this purpose, since it permits to provide very high percentages of bromine in the plastic composition, which is needed in order to obtain high refractive indexes. Contents of FR-1808 as high as 40% are easily obtained, with only minor yellowing of the plastic composition, while maintaining complete transparency. These amounts are outstanding, in view of the known art which typically incorporates amounts not higher than 15%. Other additives can also be present, such as Stabilizers, Antioxidants, Lubricants, Pigments, cross linking agents, FR synrengists. All the above and other characteristics and advantages of the invention will be better understood through the following illustrative and non-limitative examples of preferred embodiments. Example 1 Tested specimens where prepared according to the following steps: 1) Plastic drying was carried out at the appropriate temperature for each material: Polycarbonate (PC) - 120°C Polymethylmethacrylate (PMMA) - 105°C Polystyrene (PS) - 80°C The time of drying for all plastics was three hours. The plastic pellets and of FR-1808 powder were then manually mixed and compounded in a twin-screw extruder ex Berstorff at the following temperatures: PS: 40-80-190-200-210-210-210-210°C PMMA: 40-180-190-200-220-220-220-220°C PC: 40-180-220-240-260-260-260-260-260°C Injection molding in Allrounder 221-75-350 ex. Arburg at temperatures: PS: 170-210-210-210°C PMMA: 180-220-220-220°C PC: 220-260-260-260°C The formulations so obtained are given in Table I. Properties of Transparent Plastics Formulations → Components ↓ Unit 1 2 3 4 5 6 PS 102E ex Carmel Olefin % 100 85 PMMA Oroglas V826 ex Rohm & Haas % 100 85 PC Makrolon 2405 ex Bayer % 100 85 FR-1808 % 15 15 15 Flammability UL-94 3.2 mm NR V-2 NR V-2 V-2 V-0 Flammability UL-94 1.6 mm NR V-2 NR V-2 V-2 V-0 Izod notched impact (ASTM D-256-81) J/m 19 25 52 49 780 41 MFI (ASTM D-1238-82) g/10 min 5 13 7 4 19 32 Example 2 Operating as in Example 1, polybromotrimethylphenyl indan (FR-1808) was compared with other commercial FR materials polycarbonate. Tested specimens where prepared according to the following steps: Plastics drying at temperature 120°C. The time of drying for all plastics was 3 hours. Manual mixing of plastics pellets and of FR powder. Compounding in twin-screw extruder ex Berstorff at temperatures: 40-180-220-240-260-260-260-260-260°C All compounds were dried at 120°C for 3 hours. Injection molding in Allrounder 221-75-350 ex. Arburg at temperatures:220-260-260-260°C. The formulations and the results so obtained are given in Table II. Formulations → Components ↓ Unit 1 2 5 3 4 6 PC Makrolon 2405 ex Bayer % 85 70 60 85 85 100 FR-1808 % 15 30 40 Saytex 8010 % 15 F-2400E % 15 Transparency yes yes yes no no yes Example 3 Operating as in Example 1, Octachlorotrimethylphenyl indan and Pentabromotrimethylphenyl indan were compounded with polystyrene. The formulation and properties are given in Table III. FORMULATION → COMPONENTS ↓ Units 1 2 PS 102E ex Carmel Olefin % 95 95 Octachlorotrimethylphenyl indan % 5 Pentabromotrimethylphenyl indan % 5 Transparency yes yes

Claims: Flame-retarded transparent plastic composition comprising polyhalogenated trimethylphenyl indan, the transparent plastic being selected from polycarbonate, polymethylmethacrylate, polystyrene, styrene-acrylonitrile copolymer and poly (vinyl chloride). A composition according to claim 1, wherein the polyhalogenated trimethylphenyl indan is a mixture of polyhalogenated trimethylphenyl indanes having each 3 to 9 halogen atoms. A composition according to claim 2, wherein the number of halogen atoms of at least a part of the polyhalogenated trimethylphenyl indanes in the mixture is 7 or 8. A composition according to claim 2 or 3, wherein the halogen is bromine or a mixture of bromine and chlorine. A composition according to any one of claims 1 to 4, wherein the polyhalogenated trimethylphenyl indan is present in an amount of up to about 40% by weight. A composition according to claim 5, wherein the polyhalogenated trimethylphenyl indan is present in an amount of up to about 15% by weight. A method for the preparation of transparent plastic flame-retarded material according to any one of claims 1 to 4, comprising mixing the plastic material according to any one of claims 1-4 with a flame-retardant effective amount of polyhalogenated trimethylphenyl indan. Use of polyhalogenated trimethylphenyl indanes in the preparation of transparent plastic materials according to any one of claims 1 to 6, having a high refractive index. Use according to claim 8, wherein the polyhalogenated trimethylphenyl indan is present in an amount of up to about 40% by weight. Use according to claim 9, wherein the polyhalogenated trimethylphenyl indan is present in an amount greater than 10% by weight.

Inventors: FINBERG ITA, UTEVSKI LEV, FINBERG, ITA, UTEVSKI, LEV
Applicants: BROMINE COMPOUNDS LTD, BROMINE COMPOUNDS LTD.
Application year: 1999
Main classification: C08K5
IPC codes: C08L25, C08L101, C08K5, C08L27, C08L69, C08L33