INORGANIC VISIBLE LIGHT REFLECTION POLARIZER

Abstract: An inorganic visible light reflective polarizer formed by applying layers of dielectric material on one or more surfaces of a transparent substrate. The resulting polarizer exhibits polarizing performance over the entire visible spectrum. A miniaturized polarizer is formed by assembling and binding together several single-layer-coated substrates.

Description: INORGANIC VISIBLE LIGHT REFLECTION POLARIZER BACKGROUND OF THE INVENTION The present invention relates to optical polarizers, in particular, to an inorganic visible light polarizer. In the liquid crystal display (LCD) industry, particularly for projection color television applications, it is required to polarize the light of the projection light source prior to its impingement on the LCD panel that in turn blocks or transmits the light via selective polarization by sub-pixel cells in the LCD panel. The transmitted light passes through the sub-pixel color filters thus creating a projected color image. Recently, there has developed a trend towards larger screen sizes in the projection color television technology. This, in turn, has created a need for more intense light sources to maintain sufficiently bright projected images on these larger screens. The use of more intense light sources on the other hand, places such a high energy load (thermal and photonic), on the light polarizer that organic polarizers, which are sometimes used in projection televisions, degrade over time leading to degradation of image quality. In order to address this problem, pre-polarizers made of inorganic materials have been placed between the light source and the main (organic) polarizer. The inorganic pre-polarizer is able to withstand the increased energy of the light source while at the same time reducing the load, which is placed on the organic polarizer. Various types of polarizers are known, including, dichroic, wire grid, anisotropic crystal, as well as reflective and transmissive Brewster's angle polarizers. The differences between these polarizers are described in High-quality Brewster's angle polarizer for broadband infrared application, APPLIED OPTICS, Vol. 37, No. 7, pp. 1194-1204 (March 1, 1998). As described therein, Brewster angle polarizers rely on the different transmission and reflection coefficients for s- and p- wave polarization at the interface between two materials. The Brewster angle of a polarizer is the angle of maximum polarization with respect to the incident radiation, and depends on the angle of incidence and the refractive index of the material. Brewster angle polarizers are known which utilize transmissive substrates with multiple coatings made of optically transparent dielectric materials which are alternated with material of different indices of refraction, e.g., alternate layers of magnesium fluoride and zinc sulfide layers. In many of these polarizers light is incident on the dielectric coating so that the Brewster angle is dependent on the refractive index of the dielectric material. Multi-layered dielectric optical polarizers abound in the prior art. One illustrative example is U.S. 4,515,441 which discloses a dielectric optical polarizer formed by applying to each of two surfaces of a fused quartz substrate, three layers of dielectric material. The resulting dielectric polarizer operates at the Brewster angle of the dielectric layer. Furthermore, it has been suggested that multi-layer dielectric polarizers are damaged due to localized heating in the multiple layers caused by multiphoton absorption. There are also other examples. For example, in U.S. 4,553,822, a Brewster angle polarizer is disclosed in which multiple layers of dielectric material are sandwiched between two transparent substrates. Other types of inorganic, visible light polarizers, such as Glan-Thompson calcite prisms or broad band splitter cubes have not found widespread application in the LCD industry. Therefore, there continues to be a need for the development of durable and effective inorganic, visible light polarizers. Accordingly, it is the object of the present invention to provide a simple and effective, visible light polarizer. SUMMARY OF THE INVENTION Briefly, the object of the present invention is achieved by the design and production of a polarizer unit which consists of a glass substrate that is coated on one surface with a single thin layer of dielectric material and on the other surface, with a fully reflecting metal film. Preferably, the dielectric material exhibits a high reflectivity that stems from the real part of the refractive index of the material. More preferably, the refractive index of the material is appreciably higher than that of the transparent substrate. In addition, the material has a low absorption, and its refractive index and absorption are relatively constant over the visible wavelength spectrum. In another aspect, the invention relates to a visible light polarizer including a transparent substrate having two opposite planar coated surfaces and two opposite edges (an entrance and exit edge), cut and polished to be parallel to each other, the plane of the entrance edge being cut and polished to form an angle equivalent to the Brewster angle relative to the plane of the surface of the substrate having a film of dielectric material, the plane of the second edge being cut and polished to form an angle equivalent to the Brewster angle relative to the plane of surface of the substrate having a fully reflective metal film, such that the distance between the planes of the two edges is a function of the type dielectric material used, the thickness of the substrate. In a further aspect, the invention relates to a bi-directional polarizer characterized in that equal polarizer performance is obtained regardless of the direction on light entry. In still another aspect, the invention relates to visible light polarizer designed to have a light path that has the incident light enter the first edge and travel through the transparent substrate prior to striking the dielectric film on one surface of the substrate. The inventive light path design pairs the index of refraction of the transparent substrate with the higher index of refraction of the dielectric film. Since the refractive index of the transparent substrate is greater than the refractive index of air, this inventive pairing of the refractive index of the substrate and the refractive index of the dielectric film results in superior polarization relative to pairing of the index of refraction of air with the index of refraction of said first film. The preferred optical polarizer of the present invention is a miniaturized polarizer made by assembling several polarizer units as described below. BRIEF DESCRIPTION OF THE DRAWINGS Figure 1 is a graph showing the calculated P and S polarization components reflected from an uncoated sheet of glass over the full range of incident angles. Figure 2 is a graph showing the calculated P and S polarization components reflected from a film of polycrystalline silicon on a glass substrate. - Figure 3 is a graph showing the reflectance of the P and S polarization components in an inventive configuration of the silicon-coated substrate of Figure 2 in which incident light first passes through glass, is then reflected off the silicon film coating, and then travels through the glass and out into the air. Figure 4 is a schematic drawing showing the light path described in Figure 3. Figure 5 is a schematic diagram showing a stack of coated glass substrates assembled to form a miniaturized polarizer according to the invention. Figure 6 is graph of transmittance versus wavelength for the P and S polarization components of the polarizer of Figure 5. Figure 7 is a graph showing the contrast ratio versus wavelength for the polarizer of Figure 5. Figure 8 is a graph showing the theoretical performance of an optimized polarizer according to Figure 5. DETAILED DESCRIPTION OF THE INVENTION One particularly useful method of producing a miniaturized polarizer according to the invention is by: a) preparing a plurality of substrates having two opposite planar surfaces; b) applying to one surface of the substrates a thin film or layer of dielectric material, and optionally, applying a layer of a light-absorbing material such as carbon or graphite over the thin film of dielectric material; c) applying to the second surface of each substrate, a film of highly reflecting metal or a dielectric film; d) assembling the substrates in parallel with the graphite film of each substrate in contact with the metal film of an adjacent substrate to form a boule; and e) cutting the boule into individual polarizer devices. Any suitable transparent material may be used as the substrate. Particularly useful substrates are those characterized by having low light absorption at desired wavelengths, appropriate indices of refraction so that when paired with the indices of refraction of the dielectric material, yield optimum polarization performance. Examples of useful substrate materials include, fused silica, glass and glass-ceramics. Other desirable properties may be imparted to the polarizer by selecting as the substrate, materials having desired properties. For example, glasses which absorb light of selected wavelengths, such as UV absorbing glasses may. be used as the substrate. Finally, the length, width and thickness of the substrate will depend on the nature of the desired polarizer. Examples of useful dielectric materials for the polarizer include, polycrystalline silicon, amorphous silicon, gallium phosphide, aluminum arsenide, aluminum phosphate, silicon carbide, zinc selenide, zinc sulfide, zinc telluride and other similar materials. The thickness of the dielectric layer will vary, depending on the refractive index and light absoφtion of the dielectric material. For any given dielectric material, the optimum thickness of the dielectric layer will vary and therefore, will be determined by experimentation. The optimum thickness is that thickness outside which throughput of the S polarization component decreases. Above the optimum thickness, optical absorption of the S polarization component increases, and below it optical reflection of the S polarization component decreases. For the polycrystalline silicon material used in the example, the optimum thickness was found to be in the range of 26 to 36 nm. Similarly, the thickness of the highly reflecting material may vary depending on the material. The thickness must be such as to effectively turn or redirect substantially all the light which is reflected from the first dielectric layer. Polycrystalline silicon is a particularly useful dielectric material for enhancing the polarization effect because of its high index of refraction relative to glass, its low absoφtion, and the fact that both its index of refraction and its absoφtion are relatively constant over the visible wavelength spectrum. The combinations of high index of refraction and low absoφtion significantly enhance the separation of p- and s- polarization components. Any effective light-absorbing material can be applied over the surface of the dielectric film. Examples of useful light-absorbing materials include, carbon and graphite. The thickness of the light absorbing material will depend in part on the thickness of the dielectric material but should be sufficient to prevent or control light transmission through the dielectric layer. Any highly reflective metal can be applied to the opposite planar surface of the substrate. Useful examples include, silver and aluminum. In its most basic form, the inventive polarizer is constructed by coating one of the surfaces of the substrate with a dielectric material. In a preferred embodiment, the second surface of the substrate is coated with a highly reflecting material such as a silver or aluminum. In another embodiment, the highly reflecting material is replaced with the same or a different dielectric material as that coated on the first surface. In either case, the dielectric material is selected so that when paired with the refractive index of the substrate, gives optimum polarizing performance. For example, we have found that for a substrate having a refractive index of about 1.5, optimal polarizing performance can be obtained dielectric material having refractive index in the range of 3.5 to 4.5. The refractive index of polycrystalline silicon is about 4. The invention will now be described with reference to the drawings. It is known that light polarization can be obtained by directing non-polarized light at nonnormal incident angle onto a reflective surface such as that of a glass sheet. Even though the reflected light in such a system is nearly 100% plane polarized, the intensity of the light that is reflected is significantly less than that of the incident light. The reason for this is that there is an absence of one plane of polarization - the P polarization component. In addition, in such a system, the S polarization component is not fully reflected and passes through the glass sheet along with the P polarization component. As a result, such a polarizer is not practical due to the excessive loss of the desired S polarization via transmission. Conversely, while the intensity of the light that is transmitted through the glass is much higher, it consists of both P and S polarization components with the S component being somewhat lower because a certain amount has been reflected. Thus, the transmitted light, although partly polarized, is not sufficiently polarized to give a high contrast ratio. Figure 1 shows the calculated P and S polarization components reflected from an uncoated sheet of glass over the full range of incident angles. As indicated, at incident angles in the 50° region, the P polarization component appears not to be reflected. Specifically, at 56° the P polarization component disappears. This is the Brewster or polarizing angle for the glass. It has been shown by others that potentially useful non-normal incidence reflection and transmission polarizers can be obtained by "enhancing" the above phenomenon by applying thin films of metals or dielectric materials to the surface of the transparent substrate to modify overall reflectivity, transmission and absoφtion. We have found that a single thin layer of polycrystalline silicon film is a particularly useful dielectric material for the inventive polarizer. It enhances the polarization effect because of its high index of refraction relative to glass, it is WO 99/50693 _-, PCT/US99/06598 reflective, and both its index of refraction and absoφtion are relatively constant over the visible wavelength spectrum. The combination of high index of refraction and low absoφtion significantly enhances the separation of P and S polarization components. Figure 2 shows the calculated P and S polarization components reflected from a 36 nm thick polycrystalline silicon film on a glass substrate. Compared to Figure 1, the reflection of the S polarization component has increased significantly over the entire range of incident angles. The reflection of the P polarization component has also increased, however, there is a minimum increase in the 79 degree region. This also shows that the optimum polarizing angle (relative to uncoated glass) is shifted by the addition of the silicon film. The degree of polarization at 79 degrees would give a contrast ratio of about 5:1. We have found that the contrast ratio can be improved significantly by having the incident light pass through glass first, and then be reflected off a silicon film coating on the back or rear surface of the glass substrate. Figure 3 shows the reflectance of the P and S polarization components in this inventive configuration. Here, the P polarization component is less than 1 % at the 70° incident angle and the reflection of the S polarization component has decreased only slightly. As shown, the optimum polarization angle has shifted back toward the polarizing angle for uncoated glass. With the very low level of reflection of the P polarization component at the optimum incident angle, a high polarization contrast ratio could be obtained along with an acceptable level of reflected S polarization component. In order to exploit the above phenomenon we designed a unique polarizer whose basic application is illustrated in Figure 4. As used herein, a polarizer "unit" consists of glass substrate that is coated on one surface with a thin polycrystalline silicon film and on the other surface with a fully reflecting metal film. Also, an additional film of light-absorbing material such as carbon or graphite may be coated over the silicon film. The thickness and the length of the substrate, along with the "bevel" of the entrance and exit edges are chosen to form a parallelogram with acute angles of 70°. With reference to Figure 4, we have demonstrated that this geometry accomplishes the following: a) light enters the polarizer unit normal to the air-glass interface thus avoiding refraction and reflection; b) the light travels through the glass substrate before impinging on the silicon surface at the optimum Brewster polarizing angle of 70 degrees from normal; c) after reflection off the silicon surface, the light is turned or deflected by the silver surface; and d) finally, the light exits the polarizer through the exit edge, normal to the glass-air interface thus avoiding refraction and reflection. The length of the polarizer unit is sized to have only one reflection of the light beam off the silicon and silver surfaces. Also, we have designed the polarizer to be bi- directional. By bi-directional we mean that equal polarizer performance is obtained regardless of the direction in which the light beam enters the substrate. That is, whether the light impinges on the silicon surface first and is turned by the silver surface, or whether light beam first impinges the metal surface before striking and being turned by the silicon surface. The Brewster angle of a polarizer depends on the index of refraction and absoφtion of the dielectric material as well as that of the substrate, and the thickness of the dielectric layer. We have discovered a unique method for making a miniaturized polarizer by combining several polarizer units as described above. The unique design and construction of the present miniaturized polarizer is best illustrated with reference to an illustrative application which requires the use of a pre-polarizer having an aperture of about 40 x 40 mm. Clearly, the overall size of a single glass substrate required to construct such a polarizer would have to be impractically large due to the wide aperture and required light path of the substrate. Suφrisingly, we have found that the polarizer can be significantly miniaturized by reducing the thickness of the substrate and also by using a number of substrates stacked in parallel. Thus, by stacking forty (40) glass substrates each measuring 1 mm in thickness, a polarizer with a 40 mm square aperture and on overall thickness of about 5 mm can be produced. Figure 5 and the example below illustrate this unique design and construction. EXAMPLES In the following example, we illustrate one preferred method for producing a miniaturized polarizer device having a 40mm x 40mm square entrance and exit aperture, and requiring, as an example, a 70 degree Brewster angle that is dependent on the dielectric material chosen. 1) Forty substrates each measuring one millimeter thick by 40mm wide by 100mm long were prepared. 2) The substrates were each coated as follows: the first surface of each substrate was first coated with a thin layer (about 36 nm) polycrystalline silicon film, a highly reflecting silver film (about 100 nm) was coated on the second surface of each substrate, and then a light-absorbing film (graphite) was coated over the silicon film. 3) All 40 substrates were stacked in parallel with the graphite film of each substrate incontact with the metal film of the adjacent substrate. 4) The substrate assembly was bound together at each end of the long (100mm) dimension, using wire or plastic "cable ties." 5) The bound substrate assembly was placed centrally in a mold having a square cavity measuring 50mm square by 100mm deep, such that the substrate assembly rested on the 40mm by 40mm dimension "end" of the assembly. 6) The annular space between the interior mold walls and the substrate assembly was filled with an epoxy polymer and allowed to set to form a polarizer "boule". 7) Upon setting, the polarizer boule was cut into individual polarizer devices by placing the boule with its long (100) dimension resting horizontally on a cutting table and also having the substrates standing on edge. The boule was then cut horizontally across its 40mm dimension and at an angle of 70 degrees relative to the plane of the long (100mm) axis of the boule using a diamond saw. We have found that using this process, and accounting for cutting and other losses, at least 12 polarizer devices, each measuring 5 mm in thickness and having an aperture of 40 by 40 mm can be obtained.

Claims: CLAIMS: I. Inorganic visible light reflection polarizer comprising a transparent substrate having one surface coated with a single dielectric layer, characterized in that said polarizer exhibits polarization in the entire visible spectrum. 2. Polarizer according to Claim 1, wherein the coating on said surface comprises a dielectric material. 3. Polarizer according to Claim 2, wherein said dielectric material is selected from the group consisting of polycrystalline silicon, amoφhous silicon, gallium phosphide, aluminum arsenide, aluminum phosphide, silicon carbide, zinc selenide, zinc sulfide and zinc telluride. 4. Polarizer according to Claim 1, further comprising a second surface coated with a single layer of material selected from the group consisting of a high reflecting metal and a dielectric material. 5. Polarize according to Claim 1, characterized in that the dielectric material has a refractive index higher than that of the transparent substrate. 6. Polarizer according to Claim 5, wherein the dielectric material is further characterized by having a low light absoφtion. 7. Polarizer according to Claim 6, wherein the refractive index and light absoφtion of the dielectric material are characterized by being substantially constant over the entire visible wavelength spectrum. 8. Polarizer according to Claim 4, wherein the second surface of the substrate is coated with a film of a highly reflecting metal. 9. Polarizer according to Claim 8, further comprising two opposite edges, wherein the plane of said edges form angles equivalent to the Brewster angle relative to the planes of the coated surfaces. 10. Polarizer according to Claim 9 having a light path such that incident light enters the substrate through a first edge and travels through the substrate prior to striking a coated surface. I I. Polarizer according to Claim 10, wherein after striking the coated surface, the light is reflected off said surface to the second surface where said light is turned or redirected by said second surface and exits the polarizer through the second edge in the same direction as it had entered the substrate. 12. Polarizer according to Claim 11, characterized by exhibiting equal polarizing performance regardless of which of the two edges the incident light first enters the substrate. 13. Polarizer according to Claim 11, characterized by exhibiting equal polarizing performance regardless of which of the two surfaces the incident light first strikes. 14. Polarizer according to Claim 10, wherein the coated surface is selected from the group consisting of polycrystalline silicon, amoφhous silicon, gallium phosphide, aluminum arsenide, aluminum phosphide, silicon carbide, zinc selenide, zinc sulfide and zinc telluride. 15. Polarizer according to Claim 10, wherein the coated surface comprises a film or layer selected from the group consisting of silver and aluminum. 16. Polarizer according to Claim 10, wherein the refractive index of the transparent substrate is greater than the refractive index of air, and the light path is such that the index of refraction of the transparent substrate is paired with the higher index of refraction of the dielectric material. 17. Polarizer according to Claim 10, wherein said edges are essentially peφendicular to the direction of the entering light beam such that the alignment of said edges do not cause refraction of the incident light at said edges. 18. Polarizer according to Claim 10, wherein the coated surfaces and edges are aligned to produce a quasi-straight path optical device. 19. Polarizer according to Claim 9, wherein said edges further comprise a coating of anti-reflective material. 20. Polarizer according to Claim 1 , further comprising a film of light absorbing material on top of one of said coated surfaces. 21. Polarizer according to Claim 20, wherein said light absorbing material comprises carbon. 22. Polarizer according to Claim 21, wherein said light absorbing material comprises graphite. 23. Polarizer according to Claim 1, wherein said coated surfaces comprise the same dielectric material. 24. Polarizer according to Claim 1, wherein the substrate is selected from the group consisting of glasses and glass-ceramics. 25. Polarizer according to Claim 24, wherein the substrate is characterized by having a low light absoφtion at certain wavelengths. 26. Polarizer according to Claim 25, wherein the substrate is characterized by having an index of refraction such that when paired with the indices of refraction of the coated surfaces, polarization performance is optimized. 27. Polarizer according to Claim 25, wherein the substrate is a UV absorbing glass. 28. A polarizer device comprising a plurality of the polarizer unit of Claim 1. 29. Polarizer device according to Claim 28, wherein each polarizer unit comprises a transparent substrate having two surfaces, one surface being coated with a layer of dielectric material selected from the group consisting of polycrystalline silicon, amoφhous silicon, gallium phosphide, aluminum arsenide, aluminum phosphide, silicon carbide, zinc selenide, zinc sulfide and zinc telluride; a film of carbon or graphite coating over the surface of the dielectric layer; and a second surface having a coated layer selected from the group consisting of a highly reflecting metal and dielectric material. 30. Polarizer device according to Claim 29, wherein the polarizer units are assembled in parallel such that the carbon or graphite film of polarizer unit abuts the light reflecting film of an adjacent polarizer unit. 31. Apparatus comprising the polarizer device according to Claim 28. 32. A method of forming a miniaturized polarizer by: a) preparing a plurality of substrates having two opposite surfaces by coating a first surface of said substrate with a first layer of dielectric material, applying a coating of carbon or graphite over the dielelctric layer, and coating a second surface of said substrate with a second layer selected from the group consisting of a highly reflecting metal film and a dielectric material; b) stacking the substrates in parallelin such that the carbon or graphite film of each substrate abuts the second layer of an adjacent substrate to form a substrate assembly; c) binding the stacked substrates together and placing the bound stack in a mold such that there is annular space between the interior mold walls and the substrate assembly; d) pouring an encapsulating compound into the mold to completely fill the annular space, and allowing the compound to set to form a polarizer boule; and e) removing the polarizer boule from the mold and cutting said boule to form a plurality of polarizer devices. 3. Method according to Claim 32, wherein the encapsulating material is selected from the group consisting of epoxy polymer, sorel cement, and low melting point metal alloy.

Inventors: BORRELLI NICHOLAS F, DAWSON-ELLI DAVID, GROSSMAN DAVID G, VISOVSKY NICHOLAS, BORRELLI, NICHOLAS, F., DAWSON-ELLI, DAVID, GROSSMAN, DAVID, G., VISOVSKY, NICHOLAS
Applicants: BORRELLI NICHOLAS F, CORNING INC, DAWSON ELLI DAVID, GROSSMAN DAVID G, VISOVSKY NICHOLAS, BORRELLI, NICHOLAS, F., CORNING INCORPORATED, DAWSON-ELLI, DAVID, GROSSMAN, DAVID, G., VISOVSKY, NICHOLAS
Application year: 1999
Main classification: G02B5
IPC codes: G02B5