INORGANIC CEMENTITIOUS MATERIAL

Abstract: A method of producing a new type of cement, hereafter called Conch-krete. Conch-krete is created by adding sodium carbonate (also known as soda ash, natron, etc.) and one or more minerals from the calcium carbonate group (including aragonite, limestone, calcite, marble, dolomite, etc.) and the addition of water to the mix that will harden into a cement-like material. The combination of sodium carbonate and calcium carbonate can be either layered or in a mixed state. An exothermic reaction starts after the addition of water. The composition of Conch-krete can vary between 20% sodium carbonate and 80% calcium carbonate to 80% sodium carbonate and 20% calcium carbonate. Conch-krete can be used in a variety of applications not inclusive of forming bricks, interior architecture, table or counter tops, ornaments, repairing damaged cement products, casting and other applications not mentioned above.

Description: INORGANIC CEMENTITIOUS MATERIAL BACKGROUND OF THE INVENTION 1. Field of the Invention This invention relates to a new form of inorganic cementitious material which finds utility as a binder for aggregate. The invention also relates to a method of forming the cementitious material by mixing an inorganic material with either fresh or seawater, creating an exothermic reaction by which the inorganic material hardens. In some instances, aggregate is added prior to, subsequent to, or simultaneous with the addition of water to create a concrete-like material. 2. Description of the Related Art Hydraulic cements are known, the most widely encountered being Portland Cement, in which an inorganic material is heat treated at high temperatures, generally in a kiln, to activate the cement. When subsequently mixed with water, this cement hardens. When aggregate is added to the cement, it is generally known as concrete. The invention relates to a new type of cementitious material formed of inorganic substances that do not require the high temperature heat treatment associated with Portland Cement. Ancient Egyptians described using block or mud brick to build many structures, such as scenes of mud bricking in the Rehkmire tomb at Sheikh abd el-Qurna area of Egypt. Other formulas for making structures or casting are detailed on the Famine Stele located on the island of Sehel, Egypt. However, abandonment of this process would be applicable if this prior art does describe the use of a cementitious material created by adding sodium carbonate (also known as soda ash, natron, etc.) and one or more materials for the calcium carbonate group (including aragonite, limestone, calcite, marble, dolomite, etc.) which when mixed with water will harden. I have named this new type of cement Conch-krete. The strength and final set of the product of this process depend on the combination of sodium carbonate, calcium carbonate and water. To achieve a long lasting set, additional water needs to be available to the product after the initial set, as the product absorbs water after the initial set that will increase the length of the set. SUMMARY OF THE INVENTION It is thus an object of the invention to provide a new type of inorganic cementitious material that will harden upon addition of water. It is a further object of the invention to provide methods of using this new cementitious material as a binder for aggregate, to make bricks, blocks, cast stonework, cultured marble, retaining walls, pipe, grout, mortar, gunnite, stucco and similar or other products. These and other objects of the invention will be more fully understood in connection with the detailed description of the embodiments of the invention. DESCRIPTION OF THE PREFERRED EMBODIMENTS In one embodiment, a cementitious material is formed by mixing a source of sodium carbonate with a calcium carbonate material, adding water and inducing an exothermic reaction to harden the cement. The amounts of components can vary between 20 and 80 wt% sodium carbonate to 80-20 wt% calcium carbonate as active ingredients. The sodium carbonate can be in the form of sodium carbonate or as sodium carbonate decohydrate, sodium carbonate anhydrous, etc. As sources of sodium carbonate can be natural soda ash, natron, etc. Sources of calcium carbonate include calcium carbonate or as one of the known forms or a source as aragonite, limestone, calcite, marble, dolomite, etc. When water is added to the mixture of inorganic materials hardening generally starts quickly. The fineness and grain size of the calcium carbonate and sodium carbonate components not only affects the overall appearance of the final product, but also its strength. The calcium carbonate and sodium carbonate used in the invention can vary in particle size from that of powder, common sand, to dust, chips or larger chunks of material. The particle size will normally be selected for the effect to be achieved in the finished product, and mixtures of particle sizes can be used in combination. A coloring agent or dye may be introduced at the time of mixing the ingredients of the cementitious material of the invention that will affect the final color of the resulting product, thereby allowing the ability to individually tailor the final appearance of the cementitious products. The following is a list of minerals and compounds that can be added to the cement mixture (under 5% by weight of the cement) that will enhance the final product: halides, sodium chloride, borates, oxides, phosphates, silicates, sulfates, sulfides, fly ash, silica fume, sand, pozzolonas, mastics, thermoplastics, thermosetting elastomers, epoxy, polyurethane, poly sulfides, silicones, polysulfide coal tars, thermosetting sealants, neoprene, butyl-rubber, lead, rubber, asphalt, rubber coal tar, acrylic, vinyl, oleo-resins, polybutene, asphalt, carbon steel, stainless steel, steel, copper, flurosilicates, free lime, hydrated lime, chlorinated rubber, bentonite, micro-silicas, metahaolin, cuprovivante, wollastonite, magnesium carbonate, silicon dioxide, asphalt, copper salts, iron, iron oxide, potash, potassium carbonate, superplasticizers, bitumen, synthetic fibers, straw, slag, glass fibers, galvanized steel, cellulose ethers, sulfonated copolymers, aluminum, aluminum salts, carbon, sulfuric acid, magnesium, magnesium salts, thiocyanic acids, alkanolamine, rhodanides, urea, aldehydes, monomethylolurea, triisopropanolamine, metal nitrates, metal thiocyanates, thiosulfates, triethanolamine, gluconic acid, lignosulfonic acid, sodium nitrite, calcium fomate, sodium benzoate, formaldehyde, silicoaluminates, geopolymeric binders, zeolites, polyacrylates, geopolymers, ammonium salts, calcium oxide, borax, potassium hydroxide, potassium carbonate, sodium hydroxide, citric acid, carboxylic acid, lignosulfate, gypsum dehydrate, gypsum hemihydrate, anhydrous gypsum, sodium bicarbonate, hydrogen peroxide, boric acid, lithium, lithium carbonate, calcium sulfate, alkali bicarbonate, sulfonated lignin, lignosulfonates, fluoride, tricalcium silicates, tricalcium aluminate, chromium oxide, wood, natural fibers, synthetic textile fibers, anhydrite, titanium, sandstone, rhyolites, volcanic ash, dolomite, thiocyanates, calcium nitrite and air-entraining admixtures, hydrogen sulfide, iron sulfide, ferrous sulfide, sulfur, magnesium silicate. As noted above, the resulting cementitious material can be employed as a filler, grout, mortar, gunnite, masonry, bricks or blocks, decorative effect, architectural or cast stonework, ornamental or cultured marble or granite, retaining walls, wall claddings, paneling, counter panels, roof and floor tiles, pavers, precast stone, cobblestones and agglomerated stones, pipe, reinforced, including prestressed, concrete products, extruded and molded products and composites. It can be used as insulated sheathing, thermal insulation, packing material and in housewares and appliances. It may be used as a component of canoes, boats, kayaks, temporary casts, table or countertops, bioabsorbable devices, etc. alone or with other materials. It also finds utility as temporary fillings, temporary roads, temporary facilities, temporary shoring, temporary barriers, temporary support, temporary scaffolding, temporary walls, temporary docks, etc. Aggregates which can be included within the cement include bedrock, traprock, quartz and quartzites, granite, chyrscolla, malachite, biotite and feldspar. It may be formed of a mixed homogeneous material or may take the form of a layered mix. It is to be understood that variations and improvements may be made to the invention without departing from the spirit and scope of the appended claims.

Claims: I Claim: 1. A cementitious product formed from an uncalcined mixture of a source of sodium carbonate and a source of calcium carbonate and water. 2. The cementitious product of claim 1, wherein the source of calcium carbonate includes at least one material selected from the group consisting of calcium carbonate, aragonite, limestone, calcite, marble, dolomite, etc. 3. The cementitious product of claim 1 further including an aggregate. 4. The cementitious product of claim 3 which undergoes an exothermic reaction upon addition of water in the presence or absence of a hardener. 5. The cementitious product of claim 1 further comprising a coloring agent or dye. 6. The cementitious product of claim 1, wherein the source of calcium carbonate is present in the form of a material selected from the group consisting of powder, dust, sand, clumps, larger chunks or a combination thereof. 7. A method of forming a cementitious product comprising: providing a mixture of a source of calcium carbonate and sodium carbonate in uncalcined form, mixing with water in the presence or absence of aggregate; including an exothermic reaction in the resulting mixture, and recovering a hardened product. 8. The method of claim 7, wherein the method further includes shaping the mixture prior to hardening thereof. 9. The method of claim 7, wherein the exothermic reaction is induced in the presence or absence of a hardener. 10. The method of claim 7, wherein the product is selected from the group consisting of filler, grout, mortar, gunnite, stucco, masonry, decorative or architectural stonework, bricks, blocks, roof or floor tiles, cobblestones and pavers. 11. The method of claim 7, wherein the product is selected from the cultured marble, paneling, retaining walls, wall claddings, counter panels, flooring masonry, pipe and reinforced or pre-stressed concrete. 12. The method of claim 7, wherein the water is fresh water or seawater. 13. The method of claim 7, wherein the mixture further includes adding a synthetic resin, or other petroleum based residue. 14. The method of claim 7, wherein the mixture further includes adding at least one inorganic additive to the mixture.

Inventors: MCNULTY WILLIAM J JR, MCNULTY, WILLIAM, J., JR.
Applicants: MCNULTY WILLIAM J JR, MCNULTY, WILLIAM, J., JR.
Application year: 1999
Main classification: C04B7
IPC codes: B28B1, C04B7, C04B12, C04B28