HIGH PRODUCTIVITY PROCESS TO PRODUCE MALEIC ANHYDRIDE FROM N-BUTANE

Abstract: In producing maleic anhydride by catalytic oxidation of n-butane in vapor phase using oxygen or enriched air as oxidation medium, the reaction mixture consists of butane, oxygen and a recycling exhaust gas recovered from the absorption stage by a solvent of the maleic anhydride produced in the reaction. In the instant process the carbon monoxide and the carbon dioxide concentration in the reactor mixture are held to on optimum level by performing the reaction on a suitable V.P.O. catalyst, and by feeding to the recycling gases, in addition to butane and oxygen, a carbon dioxide rich gas stream.

Description: HIGH PRODUCTIVITY PROCESS TO PRODUCE MALEIC ANHYDRIDE FROM N-BUTANE FIELD OF INVENTION The present invention relates to a process for the production of maleic anhydride by oxidation of n-butane with molecular oxygen or a molecular oxygen containing gas in the vapor phase in the presence of a suitable phosphorous-vanadium mixed oxide catalyst. BACKGROUND OF THE INVENTION It is well known that in the reactor, alongside the conversion reaction of butane into maleic anhydride: C 4 H 10 + 3.5 0 2 → C 4 H 2 0 3 + 4H 2 0 other secondary reactions take place, among which the main ones are butane combustion reactions forming carbon monoxide and carbon dioxide: C 4 Hιo + 4.5 0 2 → 4C0 + 5H 2 0 C 4 H 10 + 6.5 0 2 -» 4C0 2 + 5H 2 0 Carbon monoxide is normally produced in excess and the molar ratio between carbon dioxide and carbon monoxide typically ranges between 0.6 and 1.0. Reactions are strongly exothermic and the heat of reaction is suitably removed by circulating a coolant (usually molten salts) in the reaction section which thereafter release heat to a steam generator. Conversion, selectivity and reaction yield depend on reaction conditions, mainly on feed composition, pressure, temperature and space velocity (the latter measured as standard volume of gas fed per hour per catalyst volume unit) By conversion it is meant the butane percentage in weight fed to the reactor, which is transformed into the product or by-products. By selectivity it is meant the amount of maleic anhydride expressed as the percentage (w/w) of the butane converted. The conversion product by selectivity determines yield, which identifies the amount of maleic anhydride produced, expressed as total butane percentage in weight fed to the reactor . Non-converted butane is present in the reaction effluent. The maleic anhydride produced is recovered by selective absorption of maleic anhydride from reaction gases by means of an absorption medium which may be water or a selective organic solvent for instance preferably chosen among diesters of phthalic acid such as dibutyl phthalate and dioctyl phthalate. Conventionally, absorption is carried out at a pressure which is slightly higher than atmospheric pressure, and which is sufficient to ensure exhaust gas transfer to an incinerator where organic compounds (mostly butane) are burnt and, after heat recovery, are exhausted into the atmosphere . The result is that non-converted butane jeopardises the process both in terms of yield, therefore higher raw material costs, and in terms of a higher carbon dioxide release into the air. In order to increase yield, a fraction of the exhaust gases may be taken into consideration for recycling into the reaction . Recycling of exhaust gases - containing non-converted raw materials - is a well-known procedure which has been used in various industrial processes, including catalytic oxidations in the vapour phase. For example, this procedure is normally used in the catalytic oxidation of ethylene to ethylene oxide. In the field of maleic anhydride production from butane, reaction gas recycling is detailed in the article "Oxida tion of Butane to Maleic Anhydride " , by Bissot and Benson, found at pages 57 - 60 of Industrial Engineering Chemistry, Book 2, no. 1, March 1963. However, the article describes recycling within a process including a number of reactors connected in series with maleic anhydride separation between them. This process received no industrial interest because of its complexity and the high investments that it involved. Recycling was also reported in a number of patents (such as U.S. Pat. No. 3.899.516, U.S. Pat. No. 3.904.652, U.S. Pat. No. 4.222.945, U.S. Pat. No. 4.342.699; U.S. Pat. No. 5.011.945), all of them featuring use of oxygen or enriched air as oxidizing medium. In all processes using oxygen, exhaust gas recycling to the reaction is an essential factor, it being anyhow necessary to dilute oxygen and prevent explosion hazards. Moreover, these processes are characterized by the operating conditions which remarkably differ from processes wherein air is used. A typical use is high butane charge concentrations, obtaining low conversions per pass, so as to limit formation of gaseous by-product such as carbon monoxide and carbon dioxide which should be removed by releasing a fraction of exhaust gases. U.S. Pat. No. 4.231.943 discloses exhaust gas recycling combined with use of air as oxidizing medium. The process described in this latter patent is inspired by principles which are typical of processes based on use of oxygen, i.e. low butane conversions per pass, relatively high concentration of butane and low concentration of oxygen in the feed. Process chemistry shows that, even under optimum conditions, when using air, at least 4 tons of inert gas (nitrogen) should be released per each ton of maleic anhydride produced. Considering the high inlet and outlet butane concentrations with regard to the reactor, this operation involves very high butane losses in the released gases. In order to prevent this, U.S. Pat. No 4.231.943 provides a unit for the removal of butane from the released gases by absorption on activated carbon. Butane absorption by activated carbon - due to the large gas deliveries to be treated at low pressure - is complicated and requires very high and costly amounts of absorption medium. U.S. Pat. No 5.011.945 describes a total recycle process wherein the oxidizing medium is oxygen mixed with exhaust reaction gases, to a large extent consisting of carbon monoxide and carbon dioxide, in molar proportion of at least 1 to 1, where the butane oxidation catalyst is a catalyst of the V.P.O. type with addition of a co-metal comprising molibdenum. In the mentioned process the recycling gas contains a high concentration of carbon monoxide, presenting inherent risks of loss of control and of deflagration in the butane oxidation reactor. U.S. Pat. No 5.688.970 describes a process where the oxidizing medium is a mixture of air and a fraction of reaction exhaust gases, characterized by the fact that the recovery of maleic anhydride (and consequently the recycle of exhaust gases) is carried out under pressure. Compared to the conventional technology, the above mentioned process, makes it possible to get an improved selectivity and a higher yield (and consequently a lower butane consumption) , a lower power consumption, and also a reduction in the carbon dioxide release to the atmosphere. Although in principle the process described in said U.S. Pat. No. 5.688.970 might be applied to use enriched air or oxygen as oxidizing medium, the potential advantages of the use of oxygen is limited by the fact that an increase of the percentage of exhaust gases being recycled, consequent to the use of oxygen, increases the concentration of carbon monoxide in the feed to the reactor, with enhanced risk of deflagration . US Pat. No. 5.126.463 describes a process where the oxidizing medium is pure oxygen mixed into exhaust gases of reaction, characterized by the fact that the carbon monoxide produced in the reaction is converted into carbon dioxide reacting over an oxidation catalyst (copper oxide- manganese oxide) . The advantages of such process appear to be limited by the fact that the exhaust gases of reaction contain a high concentration of carbon dioxide, specified to be not less than 60% by volume, preferably about 80% by volume, which may adversely influence the activity and lifetime of conventional V.P.O. catalysts. Furthermore, since the concentration of carbon monoxide in the recycling gases is low, a large volume of recycling gases, shown to be about 18 ton of gas per ton of maleic anhydride produced in Table II of said U.S. Pat. No 5.126.463, is to be processed in the catalytic converter of carbon monoxide. The above mentioned features may have a significant impact on the performances and economics of the process described in the abovementioned patent. DESCRIPTION OF THE INVENTION Therefore, a first and foremost aim of the present invention is that of providing a process for an efficient and safe production of maleic anhydride wherein the above mentioned problems and troubles are substantially overcome in an industrially feasible manner. According to the present invention, the above aim has been accomplished by providing a process for the production of maleic anhydride by the oxidation in vapour phase of n- butane, wherein the oxidizing medium is pure oxygen (or enriched air) mixed in recycled reaction gases, reacting over a suitable phosphorus vanadium mixed oxide (V.P.O.) catalyst, with or without modifying components, to afford maleic anhydride with a high yield and a high productivity, characterized by the fact that the concentration of the by product carbon oxides in the maleic anhydride reactor feed will be controlled in way to maintain a carbon dioxide to carbon monoxide molar ratio, optimized to allow the production of maleic anhydride with high yield and high productivity associated with a high degree of safety in operation . The V.P.O. catalyst used in the instant process is preferably, but not limited to, a catalyst characterized by the fact that the precursor, prior to calcination, is pretreated by contact with an aliphatic anhydride, preferably acetic anhydride, and by the fact that the temperature rise during calcination is inferior to 1°C per minute . The process of the instant invention, is characterized by the following operations: a) Preparing the reaction mixture consisting of oxygen, butane, carbon dioxide and a recycle gaseous stream being adjusted in such a way that the oxygen concentration in the reaction mixture ranges between 5% and 16 % by volume, the butane concentration in the reaction mixture ranges between 2% and 20 % by volume, the carbon dioxide concentration in the reaction mixture does not exceed 60 % by volume and is in a molar ratio to carbon monoxide of at least 1.5 to 1.0. b) Feeding the reaction mixture to an oxidation reactor operating at inlet pressure between 2.03 to 6.03 bar where a suitable V.P.O. type catalyst causes butane to react at moderate conversion per pass rate, producing maleic anhydride with high selectivity and high productivity. c) Cooling the reaction gases comprising oxygen, non converted butane, organic by products, carbon dioxide, carbon monoxide, water steam, inerts and maleic anhydride produced. d) Recovering maleic anhydride by absorption into a solvent, preferably a selective organic solvent, operating the absorption at an outlet pressure ranging from 1.21 to 4.5 bar. e) Water scrubbing the recycling exhaust gases after removal of maleic anhydride, so as to eliminate all organics present, except butane. f) Compressing the recycling exhaust gases after the water scrubbing to the pressure of reaction. g) Purging a fraction of the compressed exhaust gas in order to avoid accumulation of inerts (as nitrogen, argon) and of carbon oxides. h) Washing said purge of the recycling exhaust gases with the selective organic solvent referred at point d) above in order to remove by absorption a large fraction of the butane contained in said purge gas stream. The absorbed butane is followingly desorbed in the maleic anhydride absorber and recovered in the recycling exhaust gases after the removal of maleic anhydride . i) Adding fresh butane, a carbon dioxide rich stream and oxygen (or enriched air) to the compressed recycling stream of exhaust gases to form the reaction mixture having the characteristics described in step a) above. j ) Using as carbon dioxide rich stream either one of the follow±ng_s-ources--of—carbon-dioxide-: - 1) Carbon dioxide produced by selective absorption and desorption from the gaseous purge of the recycling exhaust gases. 2) Carbon dioxide rich stream produced by selective separation by membranes from a gaseous purge of the recycling exhaust gases. 3) Carbon dioxide rich stream produced by - selective oxidation of carbon monoxide to carbon dioxide of the gaseous purge from the recycling exhaust gases. 4) Carbon dioxide from an external source. 5) Carbon dioxide produced from a combination of the abovementioned sources. The improvement in the performances of the process object of the present invention is due to the following major factors : a) The concentration of butane, oxygen, carbon monoxide, carbon dioxide in the feed to the reactor is controlled in such a way as to assure a high selectivity and high productivity at the operating conditions of pressure and temperature of the reaction, over the V.P.O. catalyst used in the present process. b) The relatively high concentration of carbon dioxide and the relatively high molar ration between carbon dioxide and carbon monoxide in the feed to the reactor, are beneficial towards lowering any possible risk of explosion and improving the transfer of heat in the reactor . c) The non converted butane in the exhaust gases is recycled and is recovered to the reaction. The relatively high butane concentration makes it possible to operate the reaction with a relatively low conversion per pass rate and, consequently, with a higher selectivity. d) The amount of butane lost in the purge gas is minimized by special absorption and desorption technique. e) A relatively small volume of gas, the purge of the process, is to be processed in one auxiliary unit (either a carbon dioxide selective absorption and desorption unit, or a membrane separation unit, or a catalytic converter of carbon monoxide) . The amount of purge gas to be processed in the auxiliary unit, tipically about 1 ton of gas per ton of maleic anhydride produced, is by far inferior to the amount of gas to be processed in the auxiliary units in other processes . f) By using a suitable catalyst optimized to work under recycling conditions, it was found that the process object of the present invention leads to a safe operation, a better control on temperature peaks during reaction, a better heat transfer, a better selectivity and consequently a higher yield and higher productivity. Summarizing, compared with the traditional technology or with the gas recycle technology, like for instance the technology described in U.S. Pat No. 5.688.970, the process object of the present invention has the following advantages : a) Best selectivity and yield (consequently a lower butane consumption) b) Higher productivity (consequently higher production capacity in identical reactor) c) Safe operation d) Improved environmental friendly feature, with a remarkable reduction in the carbon dioxide released into the environment, compared with other technologies in use. DESCRIPTION OF PREFERRED EMBODIMENTS The process of this invention is shown in the attached drawings wherein: Fig. 1 shows a total recycle process using as co-feedstock carbon dioxide produced by selective absorption of carbon dioxide from a gaseous stream purged from the recycling exhaust gases of reaction. Fig. 2 shows a total recycle process using as co-feedstock a carbon dioxide rich stream produced by selective separation by membranes from a gaseous stream purged from the recycling exhaust gases of reaction. Fig. 3 shows a total recycle process using as co-feedstock carbon dioxide produced by selective catalytic oxidation of carbon monoxide to carbon dioxide from a gaseous stream purged from the recycling exhaust gases of reaction. Fig. 4 shows a total recycle process using as co-feedstock carbon dioxide from an external source. With reference to Fig. 1, compressed exhaust gases (line 1) blend with the butane feed (line 2), with oxygen (line 3) and carbon dioxide (line 22), at a pressure ranging between 2.03 and 6.03 bar. The mixture thus obtained (line 4) is fed to the reactor (5), which is preferably of the longitudinal flow fixed bed type, ever. Though the features of the present invention make it applicable to other types of reactors, for example fluidized bed reactors. By means of a suitable V.P.O. catalyst, espectally designed to operate in gas recycling conditions, butane is oxidized to maleic anhydride and by products in the reactor. A suitable V.P.O. catalyst is, but not limited to, a catalyst prepared according the following steps: a) contacting a phosphorus compound and a vanadium compound in an organic solvent under conditions which will provide a catalyst precursor having a phosphorus to vanadium atom ratio between about 0.9 to 1.4, and having more than 90 atom percent of the vanadium in the tetravalent state; b) recovering the precursor; c) drying the precursor, limiting the maximum temperature, in an oxygen containing atmosphere, to a value which will not substantially oxidize the residual organic materials arising from the organic solvent used; d) submitting the precursor, prior to calcination, to a treatment by contacting with a stream of dry inert gas containing vapors of an aliphatic anhydride, having from 4 to 8 carbon atoms, preferably acetic anhydride, at a temperature not to exceed about 200°C. e) providing an atmosphere selected from the group consisting of air, steam, inert gases and mixture thereof, and calcining the precursor in said atmosphere, by raising the temperature, as measured in the precursor, above 200°C at less than 1°C per minute to a temperature greater than 350°C, but no greater than 550 °C and maintaining the temperature for a time effective in giving a vanadium oxidation state not greater than +4.5 and in completing the conversion to generate an active catalyst. Effluent gases from reactor comprises non converted butane, maleic anhydride, carbon monoxide, carbon dioxide, steam, by-product organic compounds such as acetic acid and acrylic acid, and inerts (such as nitrogen and argon) present in the oxygen feed. Effluent gases from the reactor (line 6) are cooled in unit (7) and conveyed (line 8) to an absorber stripper unit (9) where the maleic anhydride product is recovered (line 10) . The absorber-stripper unit preferably uses an organic solvent as absorbing medium, or even better, a solvent as described in U.S. Pat. No. 5.069.687. The recycling gases (line 11) are fed to a water-scrubber column (12) where water-soluble organic compounds are separated in the form of condensate (line 13) . Since butane is insoluble in the recycle gas, it is retained by the gas after scrubbing. The recycling gases after scrubbing are fed (line 14) to a compressor (15) . The largest fraction of gases leaving the compressor (line 1) are recycled to the reactor (5), while a small fraction (line 16) is purged out. The purge gas (line 16) is fed to an absorber (17) where is washed with a stream of lean organic solvent (line 18) being fed to the absorber from the maleic anhydride absorber stripper unit (9) . A large fraction of the butane present in the purge gas is recovered by absorption in the solvent. The solvent leaving the absorber flows (line 19) to the maleic anhydride absorber (9) where butane is desorbed and recovered into the recycling gases (line 11) . The purge gas leaving the butane absorber (line 20) is fed to a conventional carbon dioxide recovery unit (21) preferably of the absorption type, where the carbon dioxide is separated. A fraction of carbon dioxide (line 22) is recycled to the reaction loop to adjust its concentration in the recycling gases. In this way the molar concentration of carbon dioxide in the recycling gases is at least 1.5 times higher the molar concentration of carbon monoxide. The excess of the recovered carbon dioxide (line 24) may be used as inert gas or for other industrial uses. The purge gas leaving the carbon dioxide recovery unit (line 23) may be conveyed to an incinerator. The advantages offered by this invention are evidenced by Example A hereinafter. In order to make the comparison easier, Example A refers to a plant that has an identical capacity as the plant of Example 1 and Example 2 given in US Pat. No. 5.688.970, which means 3100 Kg/hr maleic anhydride produced. Compared with the partial recycle process using air as oxidant, described in said US Pat No 5.688.970 (CASE A), the process object of the present invention (CASE B) presents the following global rates: CASE A CASE B Total yield (Kg of maleic anhydride per Kg of butane) 1.03 1.18 Productivity (Kg/hr of maleic anhydride per Mc of catalyst) 78 130 In the process shown in Fig.2 the purge gas leaving the butane absorber (line 20) is fed to a membrane unit (21) which separates selectively as permeate a carbon dioxide rich stream (line 22) which is recycled to the process, while the reitentate stream (line 23) is purged to an incinerator. The process shown in FIG. 3 differs for a different treatment of the purge gas stream. Here the purge gas leaving the butane absorber (line 20) with added oxygen (line 23) is fed to a catalytic converter (21) designed to oxidize selectively carbon monoxide into carbon dioxide. A stream of oxygen (line 23) is added to the purge gas as necessary to complete the selective oxidation of carbon monoxide. The catalytic converter (21) will be preferably of the tubular type, with a cooling medium in the shell to control the temperature rise due to the exothermic heat of oxidation . A fraction of the converter effluent (line 24) will be conveyed to an incinerator, while the remaining fraction, rich in carbon dioxide, will be recycled to the process (line 22) . The process shown in FIG. 4 differs from the processes shown in FIG. 1, FIG. 2 and Fig.3 for the fact that it uses as feed a carbon dioxide rich stream from an external source . No treatment is provided for the purge gas except the washing with lean organic solvent as previously described. The purge gas leaving the butane absorber (line 20) is conveyed to an incinerator. The compressed exhaust gases (line 1) blend with the butane feed (line 2), oxygen (line 3) and carbon dioxide from an external source (line 17) to form the mixture feeding the maleic anhydride reactor (5) . EXAMPLE A With reference to Fig. 1 annexed hereto, the process object of this invention typically runs as follows: 75356 Kg/hr of recycle gases (line 1) at 4.5 bar are mixed with 1300 Kg/hr of carbon dioxide (line 22), 5832 Kg/hr of pure oxygen (line 2) and 2630 Kg/hr of butane (line 3) . The total mixture (line 4) makes up the feed to the reactor (5) . The feed is 85118 Kg/hr and consists of: Oxygen 12 . 3 9, o by volume Water steam 3 . 0 w Butane 5 . 6 \\ Carbon monoxide 24 . 0 w Carbon dioxide 55 . 1 Inerts traces The oxidation reactions take place in the longitudinal flow reactor (5) . The composition of the gases exiting the reactor (line 6) is as follows (typical values) : Oxygen 4.1 % by volume Water steam 11.3 Butane 3.6 Carbon monoxide 24.6 Carbon dioxide 55.0 Maleic anhydride 1.4 Organic by products traces Inerts traces After cooling in unit (7) the reactor effluent (stream 8) is fed to a maleic anhydride recovery unit (9) where maleic anhydride is absorbed by a selective organic solvent (preferably dibutylphthalate) (line 19) containing about 144 Kg/hr of butane absorbed from the purge gas. The maleic anhydride recovered from the solvent (line 10) amounts to 3100 Kg/hr. In the maleic anhydride absorber (9) the butane contained in the solvent is stripped and recovered in the gases leaving the absorber (9). The gases leaving the absorber, 82162 Kg/hr, are conveyed (line 11) to a water scrubbing column (12) where water and organic compounds are condensed (line 13) . The gases leaving the water scrubbing column, 78767 Kg/hr, recycle (line 14) to the suction of the compressor (15) . A relatively small fraction of the compressed gases, 3411 Kg/hr, is conveyed (line 16) to a butane absorber (17), where is washed with a stream of lean solvent (line 18) being fed to the absorber from the maleic anhydride absorber stripper unit (9) . About 144 Kg/hr of butane present in the purge gas is recovered in the solvent (line 19) . The gaseous effluent from the butane absorber, 3291 Kg/hr, flows (line 20) to a carbon dioxide recovery unit (21) . The carbon dioxide recovery unit separates 2236 Kg/hr of carbon dioxide, of which 1300 Kg/hr are returned (line 22) to the reactor feed while the remaining 936 Kg/hr may be recovered (line 24) for use as inert gas or for other uses. The purge gas leaving the carbon dioxide recovery unit, 1055 Kg/hr, is conveyed to an incinerator (line 23). Totally the following rates are obtained: Maleic anhydride produced 3100 Kg/hr Butane feed 2630 Kg/hr Oxygen feed 5832 Kg/hr Yield 1.18 Kg/Kg Gas conveyed to incinerator 1055 Kg/hr Examples 1 and 2 of U.S. Pat. 5.688.970 show the following rates : Comparing the performances, the advantages offered by the process of this invention are evident. In particular the following is obtained: a) Reduced consumption of butane, from 122 to 212 kg per ton of maleic anhydride produced, b) Safer operating conditions due to the antideflagration influence of the relatively high concentration of carbon dioxide in the gas mixture. c) Very remarkable reduction in gas conveyed to incineration Furthermore the process of this invention offers a substantially higher productivity allowing an important reduction of the dimensions of the maleic anhydride reactor, witr. substantial savings on investment. The performances and rates don't differ significantly in case the process is operated according the embodiments of FIG. 2, FIG.3 or of FIG. 4.

Claims: Claim 1. A process for the production of maleic anhydride by the oxidation of n-butane with molecular oxygen or a molecular oxygen containing gas in the vapor phase at a temperature of about 300°C to 550°C in the presence of a suitable phosphorous-vanadium mixed oxide catalyst, with or without modifying components, characterized by the following steps : a) Preparing the reaction mixture consisting of pure oxygen, butane, carbon dioxide and a recycle gaseous stream being regulated so that the oxygen concentration in the reaction mixture ranges from 5 to 16 % by volume, the butane concentration in the reaction mixture ranges from 2 to 20 % by volume, the carbon dioxide concentration in the reaction mixture does not exceed 60 % by volume and is in a molar ratio to carbon monoxide of at least 1.5 to 1.0. b) Feeding the reaction mixture to an oxidation reactor operating at inlet pressure between 2.03 to 6.03 bar where a suitable V.P.O. type catalyst causes butane to react at moderate conversion per pass producing maleic anhydride with high selectivity and high productivity. c) Cooling the reaction gases comprising oxygen, non converted butane, organic by products, carbon dioxide, carbon monoxide, water steam and maleic anhydride produced. d) Recovering maleic anhydride by absorption in a solvent selected, preferably a selective organic solvent, operating the absorption at an outlet pressure ranging from 1.21 to 4.5 bar. e) Water scrubbing the recycling exhaust gas after removal of maleic anhydride, so as to eliminate all organics present, except butane. f) Compressing the recycling exhaust gases after the water scrubbing to the pressure of reaction. g) Purging a fraction of the compressed exhaust gases in order to avoid accumulation of inerts (as nitrogen, argon) and of carbon oxides. h) Washing said purge of the recyling exhaust gases with the selective organic solvent referred at point d) above, in order to remove by absorption a large fraction of the butane contained in said purge gas stream ; the absorbed butane being followingly desorbed in the maleic anhydride absorber and recovered in the recycling exhaust gases after the removal of maleic anhydride. i) Adding fresh butane, a carbon dioxide rich stream and oxygen (or enriched air) to the compressed recycling stream of exhaust gases to form the reaction mixture having the characteristics described in step (a) above. 2. A process according to claim 1, wherein it is used as carbon dioxide rich stream either one of the following sources of carbon dioxide: I) Carbon dioxide produced by selective absorption and desorption from a gaseous stream purged from the recycling exhaust gases. II) Carbon dioxide rich stream produced by selective separation by membranes from a gaseous purge of the recycling exhaust gases . III) Carbon dioxide rich stream produced by selective oxidation to carbon dioxide of the carbon monoxide contained in a gaseous stream purged from the recycling exhaust gases. IV) Carbon dioxide from an external source. V) Carbon dioxide produced from a combination of the abovementioned sources. 3. A process according to claim 1, wherein said oxidation reactor is selected from the group consisting of a fixed bed reactor or a fluidized bed reactor. 4. A process according to claims 1,2 and 3, wherein the catalytic reactions are carried out at a reaction temperature of 370-449 °C. 5. A process according to claim 4 wherein said reaction temperature is 400 °C. 6. A process according to claims 1,2 and 3, wherein the reaction mixture is fed to the inlet of said oxidation reactor at an inlet pressure from 2.03 to 6.03 bar . 7. A process according to claim 6 wherein said reactor inlet pressure is from 3.0 to 4.5 bar. 8. A process according to claims 1,2 and 3, wherein the oxygen content in the gases feeding the reactor is from 8 to 14% by volume. 9. A process according to claims 1,2 and 3, wherein the carbon dioxide to carbon monoxide molar ratio in the gases feeding the reactor is from 1.5 to 10.0. 10. A process according to claims 1,2 and 3, wherein the butane content in the gases feeding the reactor is from 3 to 8 % by volume. 11. A process according to claims 1,2 and 3, wherein said catalytic reaction is carried out a space velocity from 1000 to 4000 hr _1 . 12. A process according to claim 11 wherein said space velocity is from 2000 to 3000 hr _1 ' 13. A process according to claims 1,2 and 3, wherein a volatile phosphorus compound, preferably an organophosphorus compound, is added to the reaction feed mixture to control the activity of the catalyst. 14. A process according to claim 13 wherein the content of phosphorus in the reaction feed is between 1 and 20 ppm by volume . 15. A process according to claims 1,2,3,11,12,13 and 14 wherein the catalyst is of a phosphorus-vanadium mixed oxide type, with or without modifying components. 16. A process according to claim 1 wherein the organic solvent referred at steps d and h) is selected from diesters of phthalic acid. 17. A process according to claim 16 wherein said diesters of phthalic acid are selected among the group consisting of dibutylphthalate and dioctylphthalate . 18. A process according to claim 2, sub I), wherein carbon dioxide is recovered from the purge stream of the recycling gases by selective absorption and desorption in a carbon dioxide recovery unit. 19. A process according to claim 18 wherein the carbon dioxide recovery unit is a sodium carbonate, potassium carbonate, amine, Sulfinol, Rectisol, Purisol or other similar processes. 20. A process according to claim 2, sub II), wherein a carbon dioxide rich stream is produced by selective oxidation to carbon dioxide of the carbon monoxide contained in a purge stream of the recycling gases . 21. A process according to claim 20, wherein the selective oxidation unit uses a catalyst capable to oxidize selectively carbon monoxide to carbon dioxide in a gas having a oxygen to carbon monoxide molar ratio from 0.5 to 3.0. 22. A process according to claims 20 and 21 wherein the carbon monoxide oxidation catalyst is, but not limited to, a supported precious metal catalyst, as platinum, rhodium, ruthenium, platinum-rhodium, palladium. 23. A process according to claim 1 and 2 wherein the absorption of butane from the purge gas mentioned at step h) is provided after the selective absorption of carbon dioxide mentioned at claim 2 sub 1) or is provided after the selective oxidation to carbon dioxide of carbon monoxide mentioned at claim 2 sub 3) or after the selective separation by membranes mentioned at claim 2 sub 2) . 24. A process according to claim 2 sub .2 ) wherein a carbon dioxide rich stream is recovered by selective separation by membranes from a gaseous purge of the recycling exhaust gases . 25. A process according to claim 1 wherein water is used as solvent for the recovery of maleic anhydride and/or wherein the sequence of operations does not include the absorption of butane from the purge gas mentioned at step h) .

Inventors: BERTOLA ALDO, CASSARINO SALVATORE, BERTOLA, ALDO, CASSARINO, SALVATORE
Applicants: PANTOCHIM SA, PANTOCHIM S.A.
Application year: 1999
Main classification: C07C51
IPC codes: B01J27, B01J37, C07C51, C07D307