LEAD-FREE GLASSES

Abstract: This invention relates to lead-free silicate glasses that find use in producing fine crystal glassware and in laminated ware applications. The glasses consist essentially, in weight percent, of: SiO2 52-66; Al2O3 0-4; Li2O 0-4; Na2O 3-16; K2O 0-12; ZnO 15-30; BaO 0-7; MgO+CaO+SrO 0-4; ZrO2 0-4; B2O3 0-4.

Description: LEAD-FREE GLASSES FIELD OF THE INVENTION Lead-free glasses having properties that render them useful for production of crystal glassware and laminated ware. BACKGROUND OF THE INVENTION Silicate glasses, having a relatively high content of lead oxide in their compositions, have unique properties that particularly adapt them to use in production of crystal glassware. The properties of interest include a low liquidus temperature and a long viscosity range. These properties avoid the occurrence of devitrification during forming processes. Environmental and health concerns have led to a desire to eliminate, insofar as possible, use of toxic oxides, in particular lead oxide, in glass compositions. United States Patent No. 5,270,269 (Hares et al.) describes one approach to meeting this desirable end in the production of crystal glassware. The present invention provides a different approach. The production of crystal glassware is usually a hand crafting operation. This involves several cycles of working and reheating a glass shape. It is, of course, desirable to complete as much of the shaping operation as possible during each cycle. This requires a low, liquidus temperature and a long, viscosity curve. The latter property translates into a long working range of temperatures without devitrification, that is, without any crystal formation in or on the glass. Other properties of interest in crystal glassware include high refractive index, dispersion, and density values; also, good scratch resistance, and high chemical durability, that is, resistance to chemical attack and weathering. Another property of particular interest in thin-walled artware is the resonating sound that occurs when the rim of an article is lightly struck with another body such as a table utensil. This resonating sound is commonly known as the sonority, or ring, of a thin-walled article, such as a vase or goblet. It is a purpose of the present invention to provide a family of glass compositions possessing properties useful both for crystal glassware and for laminated ware. It is another purpose to provide a family of glass compositions free of toxic materials, in particular, free from lead compounds. It is a further purpose to provide glasses having a CTE of 70-110 x 10 " 7 /°O, a density of at least 2.70 g/cm 3 , a long viscosity curve, and a low liquidus value, such glasses being especially suited to production of crystal glassware. It is a still further purpose to provide a family of glasses, as an alternative to the family disclosed in United States Patent No. 5,270,269, for the production of crystal glassware. SUMMARY OF THE INVENTION The invention resides in part in a glass that is essentially lead-free, that exhibits a density of at least 2.70 g/cm 3 , a liquidus below 1000° C, a long viscosity curve, a CTE of 70-110 x 10 "7 /° O, good scratch resistance, and chemical durability, and that has a composition, expressed in terms of weight percent on an oxide basis, consisting essentially of: SiO 2 52-66 ZnO 15-30 AI 2 O 3 0-3 BaO 0-7 Li 2 O 0-4 MgO+CaO+SrO 0-5 Na 2 O 3-16 Zr0 2 0-4 K 2 O 0-12 The invention further resides in an article of crystal glassware molded from the above glass; also, in an article in which surfaces of two bodies are joined by laminating. DESCRIPTION OF THE INVENTION The glass family of the present invention was developed for use in production of crystal glassware. It represents an alternative to the glass family disclosed in the -269 patent for that purpose. While the present glass family is well-suited to that purpose, it has also been found to have properties adapted to certain glass laminating processes. The glass composition of the earlier Hares et al. patent, is characterized by substantial contents of BaO and SrO with lesser amounts of ZnO. The present glass family requires neither BaO or SrO. At most, the presence of these oxides is permitted in limited amounts. Rather, the present glasses contain a relatively large amount of ZnO in contrast to the earlier glasses. The present glasses are characterized by a low, liquidus temperature and a long, viscosity curve. The optimum viscosity for working an art glass is accepted as about 10 4 Pa.s (10 5 poises). This may also be stated as Log Viscosity in Pa.s equals 4. The present glasses will have this viscosity at temperatures in the range of 850° C. to 900° C. A long viscosity curve is measured in terms of the temperature range over which the glass viscosity varies by no more than a factor of 10 from the optimum value of 10 4 Pa.s. e.g., a temperature range of 750° to 975° C. The single FIGURE in the accompanying drawing is a graphical representation showing the viscosity/temperature curves for three different glasses. In the FIGURE, temperature (T), in degrees C, is plotted on the horizontal axis. Log viscosity, in Pa.s, is plotted on the vertical axis. Curve A is the viscosity-temperature curve for the glass of Example 17 in TABLE I, infra. It illustrates a long, shallow curve typical of the present glasses. Curve B is the curve for a borosilicate glass having a typical, steep viscosity-temperature, curve. Curve C is the curve for a typical, soda lime silicate glass. It will be observed that the curvatures of Curves A and C are very similar with Curve C being a bit elevated. This indicates a slightly harder glass, that is a glass that is a bit more viscous at any given temperature. Thus, the two glasses would match well for coating or laminating purposes. In addition, for art glass purposes, the present glasses have a liquidus below about 1000° C, preferably below 900° C. They also exhibit good chemical durability, and scratch resistance, as measured by Knoop hardness, with values preferably above 430. They should also have a density of at least 2.7 g/cm 3 , and a high refractive index. A property of particular interest, the sonority, or ring, of the glass, is facilitated by having the alkali metal oxides Na 2 0 and K 2 0 present in equal molar amounts. Likewise, if Li 2 0 is present, all three alkali metal oxides are preferably present in equal moiar amounts. In terms of weight percent, the preferred alkali metal oxide ratios approximate 3K 2 0:2Na 2 0:1 Li 2 O. For laminating purposes, the important properties are CTEs of 70-110 x 10 "7 /° O, a low liquidus temperature and freedom of the composition from toxic oxides, particularly lead oxide. The glasses should also have closely matching viscosity-temperature curves. Preferably, the Log viscosity values differ by not more than about 0.5 over the entire temperature range. The glasses are basically silicates with Si0 2 being the primary glass former. Broadly, glasses having properties suitable for present purposes consist essentially of, in weight percent as calculated from the batch on the oxide basis: 52-66% Si0 2 , 0-3% Al 2 0 3 . 0-4% Zr0 2 . 0-4% B 2 0 3 , 0-4% Li 2 0, 3- 16% Na 2 O, 0-12% K 2 0, 15-30% ZnO. 0-7% BaO and 0-5% MgO+CaO+SrO. In addition, up to 5% of one or more oxides selected from Y 2 0 3 , La 2 0 3 , Nb 2 O 5 , and Ta 2 0 5 may be present, primarily to improve density and/or refractive index. A feature of the invention is the replacement of lead oxide by zinc oxide. This replacement, in conjunction with control of the alkali metal oxides, provides the desired viscosity and liquidus characteristics previously attained with lead oxide. The present glasses, containing zinc oxide, have much better scratch resistance than prior glasses containing lead oxide. They also provide improved chemical and weathering durability. At least 3% Na 2 0 is required and up to 16% may be present. The alkali metal oxides contribute a relatively high CTE. While K 2 O and Li0 2 are not required, it is highly desirable to have a mixture of the three alkaline metal oxides present to provide the sonority property; also good electrical resistance where that property is a factor. Al 2 0 3 stabilizes the glass and improves chemical durability. Accordingly, at least 0.5% and preferably 1% are present. However, it stiffens the glass and pushes the viscosity curve higher. ZrO 2 has a similar effect and must be limited. B 2 0 3 lowers the CTE and may be used for that purpose. However, it is preferably absent, and the total R 2 0+B 2 O 3 preferably does not exceed about 16%. While not required, BaO serves to increase CTE and density. Accordingly, up to 7% BaO may be employed. The remaining alkaline earth metal oxides, MgO, CaO and SrO add nothing in particular to the present glasses, but may be present up to about 4-5%. As indicated subsequently in TABLE I, compositions in which at least 97% consists of the following, somewhat narrower, component ranges, in weight %, are preferred for optimum properties: Si0 2 56-63% ZnO 15-25% AI 2 O 3 1 -3% BaO 0-7% Li 2 O 0-3% MgO+CaO+SrO 0-4% Na 2 0 4-16% B 2 0 3 0-2% K 2 0 0-11 % SPECIFIC EMBODIMENTS TABLE I records a group of glass compositions, expressed in terms of weight percent on the oxide basis, illustrating the compositional parameters of the present invention. TABLE I wt% 1 2 3 4 5 6 7 8 9 10 SiO z 61.7 61.7 59.4 59.4 57.2 57.2 52.7 59.2 58.2 62.2 Al 2 0 3 2.0 2.0 2.0 2.0 2.0 2.0 2.0 2.0 1.0 1.6 Li 2 0 0.0 2.6 0.0 2.5 0.0 2.5 0.0 0.0 2.5 2.3 Na 2 0 16.0 5.3 15.8 5.3 15.5 5.2 15.0 7.7 5.2 4.8 κ 2 o 0.0 8.1 0.0 8.0 0.0 7.8 0.0 11.6 7.8 7.3 ZnO 20.0 20.0 22.5 25.0 25.0 25.0 30.0 19.1 25.0 21.4 Liquid Temp (°C) 890 840 855 885 880 995 1025 940 945 900 Soft. Pt. (°C) 713 652 709 655 703 647 684 737 644 678 Anneal Pt. (°C) 537 483 544 487 542 489 544 544 486 498 Strain Pt. (°C) 494 443 503 447 501 450 506 499 447 457 CTE (x10 ■7 /°C) 91.6 87.4 90.6 86.9 90.3 87.2 90.4 103.6 88.5 81.1 Density (g/cm 3 ) 2.74 2.73 2.79 2.76 2.82 2.82 2.93 2.73 2.87 2.74 TABLE I (cont'd) wt% 11 12 13 14 15 16 17 18 Si0 2 67.2 63.6 63.9 62.2 61.6 61.0 62.0 61.8 Al 2 0 3 1.7 1.6 1.6 1.5 2.1 1.5 1.6 1.5 Li z O 7.4 2.6 2.8 0.0 2.6 2.2 2.3 0.9 Na 2 0 - 5.3 5.8 14.2 5.3 4.6 4.7 7.5 κ 2 o - 8.1 8.8 0.0 8.1 7.0 7.2 7.1 ZnO 18.7 18.4 16.5 17.4 19.9 18.2 17.3 18.5 BaO 5.0 0.0 0.0 4.7 0.0 0.0 4.7 2.3 La 2 0 3 - - - 0.0 0.0 4.9 0.0 0.0 Liquid Temp (°C) 1230 860 855 975 890 880 810 870 Soft. Pt. c 'C) - 660 647 698 658 679 674 699 Anneal Pt. (°C) 481 481 469 531 483 501 483 504 Strain Pt. (°C) 449 442 430 491 445 459 441 461 CTE (x10 ■7 /°C) 66.4 88.9 93.5 90.8 89.2 81.7 88.7 92.6 Density (g/cm 3 ) 2.73 2.70 2.67 2.75 2.72 2.79 2.77 2.75 The TABLE also reports the softening point (S.P.), annealing point (A.P.), and strain point (St. P.) in ° C, the linear coefficient of thermal expansion (CTE) over the temperature range of 25-300° C. expressed in terms of x 10 "7 /° C, and the density (Den) in grams/cm 3 , as determined in accordance with measuring techniques conventional in the glass art. Compositions 7 and 11 are comparative examples. Composition 7 illustrates the effect of a low Si0 2 content with maximum Na 2 0 and ZnO contents. Composition 11 illustrates the effect of a high Si0 2 content in conjunction with no Na 2 0 content. The glass of composition 11 phase separated during an attempt to measure the softening point. The sound, or ring, of a glass, like any musical sound, is a matter of individual taste. Nevertheless, we have found that the degree, or efficiency, of glass resonance can be quantified. In such quantifications, the principles of resonant ultrasound spectroscopy (RUS), as described in a publication by Migliori and Sarrao, Resonant Ultrasound Spectroscopy, John Wiley and Sons, Inc., New York (1997), were employed. The resonant quality (Q) of a material may be measured by various techniques. However, we have found that RUS equipment provides a simple means of obtaining experimental data having a high quality. The Q value is determined at a given frequency by a peak-fitting procedure. Effectively, the resonant frequency is divided by the width of a peak at one half maximum power. The scan range is narrowed to focus on a single peak. The equipment scans display peaks at a constant phase angle. This angle is adjusted to obtain a symmetric peak prior to measurement of the peak width. Numerous, resonant frequencies can be measured by scanning an appropriate, frequency range. It was found adequate to use an average of the first three modes for comparative purposes. Test pieces of glass, in the form of 10x8x6 mm, rectangular prisms, were prepared and tested. TABLE II sets forth the average Q values determined for several glasses having compositions in the R 2 0-ZnO-BaO-Si0 2 family. The ratio of the R 2 0 oxides, in the order of Li0 2 :Na 2 0:K 2 0 in mol %, is shown for each composition. The compositions are identified by the numercial designation employed in TABLE I. Measurements made on two different glasses, designated NIST 711 and HPFS, are shown for reference purposes. NIST 711 is a lead glass used as a viscosity standard by the National Institute of Standards and Technology. HPFS is a high purity, fused silica glass. TABLE II Glass Q Value R 2 O Ratio 19 4000 1:1:1 14 3935 1:1:1 20 3887 1:4:2.5 11 3446 1:0:1 8 3112 0:1:1 13 1854 0:0:1 12 1833 1:0:0 16 1016 0:1:0 NIST 3600 - HPFS 6600 - It is apparent that efficiency is favored by a mixture of the three R 2 0 oxides. A mixture of two is not as efficient, but adequate. A single alkali metal oxide is generally not adequate regardless of the alkali metal. As a rule of thumb, a glass should have a Q value of at least 3,000 to be considered efficient. Preferably, the value is above 3,500. The chemical durability of the glasses against acids is defined in terms of weight loss (W.L.A.). Values were determined by immersing polished plates of known weight for 24 hours in an aqueous bath of 5% by weight HCI operating at 95° C. After withdrawal from the bath and drying, the plates were re-weighed and the weight loss measured in terms of mg/cm 2 . The chemical durability of the glass against bases is defined in terms of weight loss (W.L.B.). Values were determined by immersing plates of known weight for six hours in an aqueous bath of 0.02 N Na 2 C0 3 operating at 95° C. After withdrawal from the bath and drying, the plates were re-weighed and the weight loss measured in terms of mg/cm 2 . Three of the glasses shown in TABLE I, and the first glass shown in the Hares et al. -269 patent, were melted Test pieces were prepared for determining acid and basic durability by the methods just described. The results are shown in TABLE III TABLE III Durability 19 20 8 -269 Acid 0.032 0.083 0.60 0.13 Basic 0.038 0.060 0.062 0.087 The actual, batch ingredients for preparing the glasses can comprise any materials, either oxides or other compounds, which, when melted together, will be transformed into the desired oxide in the proper proportions. For example, K 2 C0 3 , and Na 2 C0 3 can provide the sources of K 2 0 and Na 2 0, respectively. Sb 2 0 3 (not shown) may be included to perform its conventional function in glass melting as a fining agent. The batch components were mixed together very thoroughly to assist in securing a homogeneous melt, and that mixture was charged into platinum crucibles. The crucibles were moved into a furnace operating at about 1450D C. and the batches melted for about three hours. Thereafter, the melts were poured into steel molds to form rectangularly-shaped slabs of glass having dimensions of about ~ 25.4 x 10, 16 x 1.27cm (10" x 4 x 0.5"). Those slabs were transferred immediately to an annealer operating ?t about 500° C. Whereas the above description reflects laboratory melting and forming practice only, it must be appreciated that the compositions recited in TABLE I, complying with the terms of the subject invention, can be melted and formed in much larger quantities utilizing conventional, commercial melting units and glass forming techniques.

Claims: WE CLAIM: 1. A glass that is essentially free from lead, that exhibits a density of at least 2.70 g/cm 3 , a liquidus below 1000° O, and a long viscosity curve, a coefficient of thermal expansion in the range 70-110 x 10 "7 /° C, good scratch resistance and chemical durability, and that has a composition, expressed in terms of weight percent on an oxide basis of: SiO 2 52-66 ZnO 15-30 AI 2 O 3 0-4 BaO 0-7 Li 2 O 0-4 MgO+CaO+SrO 0-5 Na 2 O 3-16 Zr0 2 0-4 K 2 O 0-12 B 2 0 3 0-4 2. A glass in accordance with ciaim 1 which contains at least 0.5% Al 2 0 3 . 3. A glass in accordance with claim 1 in which the total of Na 2 0+K 2 0+Li 2 0+B 2 0 3 does not exceed about 16%. 4. A glass in accordance with ciaim 1 which contains the three alkali metal oxides, K 2 0, Na 2 0 and Li 2 0 in the molar ratio of 1 : 1 : 1. 5. A glass in accordance with claim 1 having a composition, expressed in weight percent on an oxide basis, in which at least 97% consists essentially of 56-63% Si0 2 , 1-3% Al 2 0 3 , 0-4 Li 2 0, 4-16% Na 2 0, 0-11 % K 2 0, 15-25% ZnO, 0- 7% BaO, 0-4% MgO+CaO+SrO and 0-2% B 2 0 3 . 6. An article of crystal glassware in which the glass is essentially free from lead, that exhibits a density of at least 2.70 g/cm 3 , a liquidus below 1000° C, and a long viscosity curve, a coefficient of thermal expansion in the range 70- 110 x 10 "7 /° C, good scratch resistance and chemical durability, and that has a composition, expressed in terms of weight percent on an oxide basis of: Si0 2 52-66 ZnO 15-30 AI 2 O 3 0-4 BaO 0-7 Li 2 O 0-4 MgO+CaO+SrO 0-5 Na 2 0 3-16 ZrO 2 0-4 K 2 O 0-12 B 2 O 3 0-4 7. An article in accordance with claim 6 in which the glassware has a sonority efficiency of at least 3,000. 8. An article in accordance with claim 6 in which the glass contains at least 0.5% Al 2 0 3 . 9. An article in accordance with claim 6 in which the total content of Na 2 0+K 2 0+Li 2 0+B 2 0 3 does not exceed 16%. 10. An article in accordance with claim 6 in which the glass composition contains the three alkali metal oxides, K 2 0, Na 2 0 and Li 2 0 in a molar ratio of 1 :1 :1. 11. An article in accordance with claim 6 in which the glass has a composition, expressed in weight percent on an oxide basis, in which at least 97% consists essentially of 56-63% Si0 2 , 1-3% Al 2 0 3 , 0-4 Li 2 0, 4-16% Na 2 0, 0-11 % K 2 0, 15-25% ZnO, 0-7% BaO, 0-4% MgO+CaO+SrO and 0-2% B 2 0 3 . 12. A laminated, glass article comprising two glass components joined directly to each other, one component being a glass that is essentially free of lead, that exhibits a density of at least 2.70 g/cm 3 , a liquidus below 1000° C, and a long viscosity-temperature curve, a coefficient of thermal expansion in the range 70-110 x 10 "7 /° C, good scratch resistance and chemical durability, and that has a composition, expressed in terms of weight percent on an oxide basis of: SiO 2 52-66 ZnO 15-30 AI 2 O 3 0-4 BaO 0-7 Li 2 O 0-4 MgO+CaO+SrO 0-5 Na 2 O 3-16 ZrO 2 0-4 K 2 O 0-12 B 2 0 3 0-4, the other component being a glass having a different composition, but having a long viscosity-temperature curve that closely matches that of the first glass over the entire temperature range.

Inventors: HARES GEORGE B, KOHLI JEFFREY T, WEBB JAMES E, HARES, GEORGE, B., KOHLI, JEFFREY, T., WEBB, JAMES, E.
Applicants: CORNING INC, HARES GEORGE B, KOHLI JEFFREY T, WEBB JAMES E, CORNING INCORPORATED, HARES, GEORGE, B., KOHLI, JEFFREY, T., WEBB, JAMES, E.
Application year: 1999
Main classification: C03C3
IPC codes: C03C3, C03C4