Method and apparatus for making glass and particularly ceramic frits

Abstract: A method for making glass and particularly ceramic frits, comprising the steps of: introducing in a wet grinding unit (5), after a metering step according to chosen proportions, materials which constitute a mixture to be melted, to produce a slurry; screening and collecting said slurry in a storage tank (7); introducing the collected slurry in a melting furnace (10) to make a liquid component of the slurry evaporate; and forming a melted paste o vitreous material, adapted to be converted into a ceramic frit.

Description: The present invention relates to a method and an apparatus for making glass and particularly ceramic frits. Conventional methods for producing glass-like materials, such as sheet glass, bottle glass and ceramic frits, entail feeding the melting furnaces with mixtures of various materials in powder form with controlled particle size and humidity. The raw materials that compose the mixture must be first dry-ground, transferred to the glass-making site, stored and then metered with the aid of machines such as vibrating hoppers or fluids for extraction from the storage silos, screw feeders or belts, dosage chambers mounted on load cells, mixers, and finally conveyed with the aid of a pneumatic conveyance systems. The various steps of this production process have several financial and production-related drawbacks, linked to the dry grinding of the individual raw materials, to the steps for transferring and storing the powders, and to their mixing; theses production plants are further burdened by a high level of management complexity. Methods for making glass are described in the prior documents DD 94 237A, DD 122 620A and DD 112 638A. The aim of the present invention is to obviate the above-described drawbacks of the known methods, i.e., to provide a method for making glass which allows reduced costs, higher effectiveness and flexibility in the management of the treatment system. Within the scope of this aim, an object of the present invention is to carry out the above method with an apparatus which has a simple structure, is relatively easy to provide in practice, safe in use, effective in operation and relatively modest in cost. This aim, this object and others which will become more apparent hereinafter, are achieved by a method for making glass, according to the present invention, comprising the steps set forth in claim 1. The characteristics of the apparatus for performing the glass-making method are defined in the claims 5-11. Further characteristics and advantages of the present invention will become better apparent and evident from the following detailed description of a method for making glass according to the invention, illustrated only by way of non-limitative example in the accompanying drawings, wherein: Figure 1 is a diagram of the steps of the method according to the present invention; Figure 2 is a diagram of the apparatus according to the invention for carrying out the method; Figure 3 is a view of a detail of the melting furnace of the apparatus of Figure 2. With reference to the above figures, 1 generally designates an apparatus for making glass and particularly ceramic frits with the method according to the invention. The raw materials are stored proximate to the apparatus 1, in a coarse particle size and with their natural moisture content; accordingly, it is necessary to take into account the hygrometric characteristics of each component in calculating the doses to be mixed. Once the doses of raw materials (M) to be used have been established, in the first step (A) of the method, the mixture is composed with conventional methods which use conveyor belts 2, hoppers 3 and weight-decrease load cells to draw the raw materials from storage silos 4, meter them in chosen proportions and convey them to a wet grinding unit 5. The grinding unit 5 is a known drum mill, of the continuous or discontinuous type, with grinding media made of sintered alumina, which performs wet grinding and produces a slurry with controlled residue. During the second step (B) of the method, the slurry produced by the mill is filtered by means of a screen 6 and is then accumulated in storage tanks 7 provided with agitation vanes 8. The slurry in the storage tanks has a water content which can vary between 26 and 40% of the weight, a density between 1550 and 1900 g/l, and a viscosity between 7-25·10 - 6 m 2 .s -1 (1.5 and 3.5 Engler degrees). In the third step (C) of the method, the slurry is conveyed by means of a pump 9 from the storage tanks 7 to a melting furnace 10, which is of the tank type and in which water evaporation and melting of the materials of the compound occur, producing the frit (F). Figure 3 illustrates a detail of the melting furnace 10. The furnace 10 is provided with a particularly long stack 11 on which there is provided an opening 12 from which a pipe 13 for feeding the slurry into said furnace protrudes. The end part of the pipe 13 has a jacket and is water-cooled in order to prevent it from deteriorating due to the high heat level inside the stack 11; the end of the pipe 13 is provided with a nozzle 14 which is directed downward so as to spray the slurry toward a tank 15 of the furnace 10. The distance that the slurry must cover before depositing on the tank 15 of the furnace allows most of the water present in the slurry to evaporate along the way. Conveniently, the pipe 13 can be arranged at a higher or lower level along the stack 11, depending on the characteristics of the slurry being produced. Advantageously, the nozzle 14 can be provided with a single or multiple opening. Advantageously, if none of the components of the slurry is watersoluble, the slurry can be partially or fully filter-pressed and introduced in the furnace 10 in a plastic form instead of through the nozzle 14. It should be noted that thanks to the limited size of the particles ground in the drum mill 5, which works with moist material, the amount of heat required to achieve melting is considerably lower than the amount required for conventional dry mixes. In order to ascertain this property of the method, a test was conducted with a ceramic frit thus constituted: Quartz 34.5% Potash soda feldspar 25.5% Borax pentahydrate 10.0% Colemanite 15.0% Alumina 2.0% Zinc oxide 3.0% Calcite 5.0% Dolomite 5.0% After wet grinding, a slurry was obtained which had a 28% water content by weight, a viscosity of 20cSt ≃ 20·10 -6 m 2 s -1 (3 Engler degrees) and a particle size of less than 63 µm, or with a solid residue through a screen with a net mesh size of 63 µm equal to 0.5% by weight with respect to the solid contained in the slurry. By introducing a slurry with the above-described characteristics in a furnace provided with a burner having the maximum power of 1,465·10 3 kj/hr (350,000 kcal/h) and a curved tile-like bottom formed in the melting surface, a frit was obtained whose chemical and physical composition is within the standards of those composed with conventional methods. The specific consumption values ascertained by experiments are 10,460 kj/kg (2,500 kcal/kg) of frit; this consumption is comparable to the typical consumption of conventional productions of this type and can be improved further. Moreover, with this method it is not necessary to include in the energy balance the additional consumption due to the preliminary drying of the components of the mixture to be melted and to the dry grinding. It has thus been shown that the invention achieves the intended aim and objects. The invention thus conceived is susceptible of numerous modifications and variations, all of which should be within the scope of the appended claims. In practice, the materials employed, as well as the shapes and the dimensions, may be any according to requirements without thereby abandoning the scope of the protection of the appended claims. Where technical features mentioned in any claim are followed by reference signs, those reference signs have been included for the sole purpose of increasing the intelligibility of the claims and accordingly, such reference signs do not have any limiting effect on the interpretation of each element identified by way of example by such reference signs.

Claims: A method for making glass and particularly ceramic frits, characterized in that it comprises the steps of: introducing in a wet grinding unit (5) constituted by a continuous or discontinuous drum mill with grinding media made of sintered alumina, after a metering step according to chosen proportions, materials in a coarse particle size, which constitute a mixture to be melted, to produce a water slurry with a water content of 26-40% by weight and a viscosity of 7-25·10 -6 m 2 .s -1 (1.5-3.5 Engler degrees); screening and collecting said slurry in a storage tank (7); introducing the collected slurry in a melting furnace (10) to make a liquid component of the slurry evaporate; and forming a melted paste of vitreous material, adapted to be converted into a ceramic frit. The melting method according to claim 1, characterized in that said slurry is composed of a suspension of heterogeneous solid particles in an aqueous solution containing solutes of different kinds. The melting method according to claim 1, characterized in that said slurry is constituted by solid materials whose particle size is between 5 and 100 µm and water. The melting method according to any of the claims 1-3, characterized in that said solid materials are constituted by quartz, potash soda feldspar, borax pentahydrate, colemanite, alumina, zinc oxide, calcite and dolomite, taken in suitable quantities. An apparatus for carrying out the method according to claim 1, characterized in that it comprises: a unit (5) adapted for wet grinding of raw coarse particle size materials (M) to produce a water slurry with a water content of 26-40% by weight and a viscosity of 7-25·10 -6 m 2 .s -1 (1.5-3.5 Engler degrees), said unit (5) being constituted by a continuous or discontinuous drum mill with grinding media made of sintered alumina; a system for metering and conveying said raw materials (M) inside said grinding unit (5); at least one tank (7) for storing the ground mixture provided with vane agitators (8) and with a discharge control screen (6), a system (9) for pumping said mixture, a melting furnace (10), a nozzle (14) for feeding the slurry pumped into the furnace (10), pipes and unions (11, 12, 13), for the mutual connection of the various components. The apparatus according to claim 5, characterized in that said melting furnace (10) is of the tank type (15). The apparatus according to claim 5, characterized in that said melting furnace (10) is constituted by a melting tank (15) provided with a discharge stack (11) and with a heat exchanger. The apparatus according to claim 5, characterized in that said pumping system (9) is constituted by a membrane or piston or peristaltic pump provided with delivery pressure control. The apparatus according to claim 5, characterized in that said pumping system (9) is adapted to allow filter-pressing of said mixture, which is introduced in said furnace (10) in a plastic form. The apparatus according to claim 5, characterized in that said nozzle (14) is provided with at least one outlet hole. An apparatus according to claim 5, characterized in that said nozzle (14) is arranged in an opening (12) of said stack (11) of the furnace (10).

Inventors: ACERBI PIERUGO, BRESCIANI ANDREA, ACERBI, PIERUGO, BRESCIANI, ANDREA
Applicants: SACMI, SACMI COOPERATIVA MECCANICI IMOLA S.C.R.L.
Application year: 1999
Main classification: C03B3
IPC codes: C03B19, C03B5