Phase change ink formulation with organoleptic maskant additive

Abstract: A phase change ink carrier composition comprising an organoleptic maskant. Preferably the phase change ink carrier composition comprises: a) a urethane resin that is the reaction product of at least one alcohol and an isocyanate, the at least one alcohol being a monohydric aliphatic alcohol, a monohydric aromatic alcohol, a monohydric aliphatic/aromatic alcohol, a monohydric fused ring alcohol, a polyol or mixtures thereof; and/or a mixed urethane/urea resin that is the reaction product of at least one alcohol, an isocyanate, and at least one monoamine; and b) a mono-amide. The organoleptic maskant is preferably a fragrance and/or an ester, a lactone, an aldehyde, a ketone, an alcohol, an ether, an acetal, a ketal, a heterocycle, a composition having cumulated double bonds including pheromones, an acetylene, an amine or a mixture thereof.

Description: The present invention relates generally to phase change inks. More particularly, the present invention relates to a phase change carrier composition containing the combination of at least one urethane resin, and/or at least one mixed urethane/urea resin, at least one mono-amide, and at least one organoleptic maskant. Additionally, the present invention relates to inks useful for printing applications formed by adding colorant materials to such carrier compositions. Still further, the present invention relates to processes of using these phase change ink compositions in a printing device. In general, phase change inks (sometimes referred to as "hot melt inks") are in the solid phase at ambient temperature, but exist in the liquid phase at the elevated operating temperature of an ink jet printing device. At the jet operating temperature, droplets of liquid ink are ejected from the printing device and, when the ink droplets contact the surface of the printing media, they quickly solidify to form a predetermined pattern of solidified ink drops. Phase change inks have also been investigated for use in other printing technologies such as gravure printing as referenced in U.S. Patent No. 5,496,879 and German patent publications DE 4205636AL and DE 4205713AL assigned to Siegwerk Farbenfabrik Keller, Dr. Rung and Co. Phase change inks are desirable for ink jet printers since they remain in a solid phase at room temperature during shipping and long-term storage. Also, the problems associated with nozzle clogging due to ink evaporation are largely eliminated, thereby improving the reliability of ink jet printing. Furthermore, in the above-noted prior art phase change ink jet printers where the ink droplets are applied directly onto the printing medium the droplets solidify immediately upon contact with the substrate, migration of ink along the printing medium is prevented and dot quality is improved. This is also true of the processes and ink compositions described herein. EP-A-0307551 discloses an ink composition comprising an aqueous alkaline solution of a polyamide resin, a fragrance capable of being carried by said polyamide resin, an aqueous solvent, and a pigment. Suitable fragrances or perfumes include various natural essential oils such as lavender oils which are generally aromatic aldehyds or ketones. It is an aspect of the present invention that phase change carrier compositions comprise an admixture of (1) at least one urethane resin; and/or (2) at least one mixed urethane/urea resin; and (3) at least one mono-amide; and (4) at least one organoleptic maskant that adds a pleasing fragrance to the melted composition to avoid offensive aromas in use or to achieve a desired aroma. It is another aspect of the present invention that phase change ink compositions comprise the admixture of (a) the above-noted phase change carrier composition with (b) a phase change ink compatible colorant. It is yet another aspect of the present invention that a method for producing a layer of a phase change colored ink on the surface of a substrate by either direct or indirect printing is obtained wherein the phase change ink composition in the solid phase comprises an admixture of (a) the above-noted phase change carrier composition and (b) a phase change ink compatible colorant. It is a feature of the present invention that the phase change carrier composition and the colored inks have no odor or possess a pleasant odor upon melting. It is an advantage of the present invention that for phase change carrier compositions and inks of the present invention a pleasant fragrance is released upon melting and remain . if left in a printer for an extended period of time. Organoleptic maskant materials suitable for use in the present invention include all materials that are compatible with phase change inks and phase change ink carrier compositions and which will mask any unpleasant odours associated therewith, either by preventing the perception of any odours at all (ie the inks or carriers will appear to be odourless); by imparting a pleasant odour which overrides the unpleasant odour or by altering the unpleasant odour so that it becomes pleasant. Such materials will include fragrances per se as well as other materials which act to alter or suppress odours. The term "nucleophile" in the present specification and claims is used as defined on page 179 of "Advanced Organic Chemistry", 3rd Edition by Jerry March, ©1985 by John Wiley and Sons, to describe a reagent that brings an electron pair to a reaction to form a new bond. The preferred nucleophiles of this invention are alcohols or amines, but it is understood that other nucleophilic functional groups that are capable of reacting with the isocyanate moiety could also be used in the invention. The term "oligomer" in the current specification and claims is used as defined on page 7 of "Polymer Chemistry - The Basic Concepts" by Paul Hiemenz, 81984 by Marcel Dekker, Inc., to describe a term coined to designate molecules for which n (representing the number of repeating monomer units) is less than 10. The term "isocyanate-derived resin" as used in the present specification and claims is defined as any monomeric, oligomeric or non-polymeric resinous material derived from the reaction of mono-, di-, or poly-isocyanates with suitable nucleophilic molecules. The terms "isocyanate-derived wax" as used in the present specification and claims is defined as any crystalline or semicrystalline waxy material derived from the reaction of a fatty isocyanate with a suitable nucleophile, or the reaction of a fatty nucleophile with a suitable isocyanate, or the reaction of a fatty nucleophile with a fatty isocyanate. The term "urethane resin" or "urethane isocyanate-derived resin" as used in the present specification and claims is defined as any resin that is a urethane that is the product of the reaction of an isocyanate and an alcohol. The term "mixed urethane/urea resin" or "urethane/urea isocyanate-derived resin" as used in the present specification and claims is defined as any resin that is a mixed urethane/urea that is the product of the reaction of an isocyanate, an alcohol and an amine. Any suitable reaction condition for making urethane resins or mixed urethane/urea resins by condensing alcohols and/or amines with isocyanates may be employed in the practice of the present invention. Preferably, the reaction is carried out at elevated temperatures (e.g. 60°C to 160°C) in the presence of a urethane reaction catalyst such as dibutyltindilaurate, bismuth tris-neodecanoate, cobalt benzoate, lithium acetate, stannous octoate or triethylamine. The reaction conditions preferably are conducted in an inert atmosphere, such as argon or nitrogen gas or other suitable atmosphere, to prevent oxidizing or yellowing the reaction products and to prevent undesirable side reactions. The mole ratio of reactants is adjusted so that the isocyanate functionalities are completely consumed in the reaction with a slight molar excess of alcohol or amine typically remaining. Conceptually the reactants can be added together in any order and/or added to the reaction as physical mixtures. However, in the preferred embodiments of the invention, reaction conditions and the order of the addition of reactants are carefully controlled for several reasons. First, reaction conditions and reactant additions are chosen to provide a controlled exothermic reaction. Secondly, when reacting mixtures of alcohols and/or amines with diisocyanates such as isophorone diisocyanate (IPDI), the order of addition of the isocyanate and the different nucleophiles to the reaction is chosen to tailor the distribution of diurethane molecules, and/or mixed urethane/urea molecules, and/or diurea molecules in the final resin. When doing this, the different reactivities to isocyanates of alcohols versus amines are employed, as are the different reactivities of the two separate isocyanate groups on IPDI. See J.H. Saunders and K.C. Frisch's "Polyurethanes Part I, Chemistry" published by Interscience of New York, New York in 1962 and Olin Chemicals' Luxate™ IM isophorone diisocyanate technical product information sheet which provide further explanation of this chemistry. This control of the reaction conditions and order of addition of the reactants is done to specifically tailor or customize the different types of molecular species in the finished resin so that the resin will: (1) have a controlled viscosity that is designed for a specific application, (2) have a controlled glass transition temperature and/or melting point, and (3) have consistent properties from batch to batch. The isocyanate-derived resins from these reactions are generally transparent solids having melting points in the range of 20°C to 150°C, viscosities in the range of 10 cPs to 5000 cPs at 150°C and T g 's of -30°C to 100°C. The isocyanate-derived waxes from these reactions are generally opaque waxy solids having sharp melting points from 50°C to 130°C, and viscosities of 1 cPs to 25 cPs at 140°C. The isocyanate-derived resins and waxes display properties such that the higher the T g and the melting point, the higher is the viscosity. While the structural activity relationships are not fully understood, it is known that the T g of the isocyanate-derived resins is controlled by the proper choice of the mixture of nucleophiles in the reaction as illustrated in Table 3 in European Patern Application No 97 304727 Varying one or more of the readily available commodity chemicals used as chemical precursors will permit custom-tailoring of the properties of the isocyanate-derived resin and wax materials. Preferred alcohols to react with difunctional and higher isocyanates to make either the urethane resins or the urethane/urea resins of this invention include any monohydric alcohol. For instance, the monohydric alcohol could be any aliphatic alcohol [e.g., a C 1 -C 22 or higher linear alcohol, any branched alcohol or any cyclic aliphatic alcohol such as methanol, ethanol, (n- and iso)-propanol, (n-, iso-, t-) butanol, (n-, iso-, t-) pentanol, (n-, iso-,t-) hexanol, (n-, iso-, t-) octanol, (n-, iso-, t-) nonanol, (n- and branched) decanols, (n- and branched) undecanols, (n- and branched) dodecanols, (n- and branched) hexadecanols, (n- and branched) octadecanols, 3-cyclohexyl-1-propanol, 2-cyclohexyl-1-ethanol, cyclohexylmethanol, cyclohexanol, 4-methyl cyclohexanol, 4-ethylcyclohexanol, and 4-t-butylcyclohexanol]; an aliphatic/aromatic alcohol [e.g., benzyl alcohol, octyl, nonyl, and dodecylphenol alkoxylates of octyl, nonyl, and dodecylphenol, and alkoxyphenol]; aromatic alcohols such as phenol, naphthol, and their derivatives; fused ring alcohols (e.g., rosin alcohols, hydroabietyl alcohol, cholesterol, vitamin E) and other suitable alcohols (e.g., N,N-dimethyl-N-ethanolamine, stearamide-monoethanolamine, tripropyleneglycol monomethylether, hydroxybutanone, menthol, isoborneol, terpineol and 12-hydroxy stearyl stearamide). It will be obvious to those skilled in the art that small amounts (on a molar basis) of polyols could also be incorporated into the reaction mixture to produce oligomeric species in the resins if so desired. The preferred alcohols are hydroabietyl alcohol, octylphenol ethoxylate and octadecyl alcohol. Preferred amines to react with difunctional and higher isocyanates to make the mixed urethane/urea resins of this invention include any monofunctional amine, with the exception of tertiary amines void of other nucleophilic functional groups (e.g., triethylamine). For instance, the mono-amine could be any aliphatic primary or secondary amine (e.g., a C 1 -C 22 or higher linear amine, any branched amine or any cyclic aliphatic amine) such as methyl amine, ethyl amine, (n- and iso-)propyl amine, (n-, iso-, and t-) butyl amine, (n-, iso-, t-) pentyl amine, (n-, iso-, t-) hexyl amine, (n-, iso-, t-) octyl amine, (n-, iso-, t-, ) nonyl amine, (n- and branched) decyl amine, (n- and branched) undecyl amines, (n- and branched) dodecyl amines, (n- and branched) hexadecyl amines, (n- and branched) dodecyl amines, dimethyl amine, diethyl amine, di(n- and iso-)propyl amines, di(n-, iso-, t-)butyl amine, di(n-, iso-, t-)pentyl amine, di(n-, iso-, t-)hexyl amine, di(n-, iso-, t-)cyclohexyl amine, di(n-, iso-, t-)heptyl amine, di(n-, iso-, t-)octyl amine, di(n-, iso-, t-)decyl amine, di(n-, iso-, t-)dodecyl amine, di(n-, iso-, t-)octadecyl amine, cyclohexyl amine, 2,3-dimethyl-1-cyclohexylamine, piperidine and pyrrolidine; an aliphatic/aromatic amine (e.g., benzyl amine or analogues with longer or additional alkyl chains); aromatic amines such as aniline and anisidine; fused ring amines such as rosin amine, dehydroabietyl amine, dihydroabietyl amine and hydroabietyl amine ; and miscellaneous amines (e.g., adamantyl amine, isonipecotamide, polyoxyalkylenemonoamines, such as M-series Jeffamines available commercially from Huntsman Chemical Company of Austin, Texas; and 3,3'-diamino-N-methyl-dipropylamine). It will be obvious to those skilled in the art that small amounts (on a molar basis) of polyamines could also be incorporated into the reaction mixture to produce oligomeric species in the resins if so desired. The preferred amine is octadecyl amine. Preferred alcohols to react with monofunctional isocyanates to make the mixed urethane/urea resins of this invention include any monohydric alcohol. For instance, the monohydric alcohol could be any aliphatic alcohol [e.g., a C 1 -C 22 or higher linear alcohol, any branched alcohol or any cyclic aliphatic alcohol such as methanol, ethanol, (n- and iso-)propanol, (n-, iso-, and t-) butanol, (n-, iso-, t-) pentanol, (n-, iso-, t-) hexanol, (n-, iso-, t-) octanol, (n-, iso-, t-) nonanol, (n- and branched) decanols, (n- and branched) undecanols, (n- and branched) dodecanols, (n- and branched) hexadecanols, (n- and branched) octadecanols, 3-cyclohexyl-1-propanol, 2-cyclohexyl-1-ethanol cyclohexylmethanol, cyclohexanol, 4-methyl cyclohexanol, 4-ethylcyclohexanol and 4-t-butylcyclohexanol ); an aliphatic/aromatic alcohol (e.g., benzyl alcohol, octyl, nonyl, and dodecylphenol alkoxylates or octyl, nonyl, and dodecylphenol, alkoxyphenol); aromatic alcohols such as phenol, naphthol, and their derivatives; fused ring alcohols (e.g., rosin alcohols, hydroabietyl alcohol, cholesterol, vitamin E) and other suitable alcohols (e.g., N,N-dimethyl-N-ethanolamine, stearamide-monoethanolamine, tripropyleneglycol monomethylether, hydroxybutanone, menthol, isoborneol, terpineol and 12-hydroxy stearyl stearamide), as well as multifunctional alcohols such as ethylene glycol, diethylene glycol, triethylene glycol, dimethylolpropionic acid, sucrose, polytetramethylene glycol (MW < ∼ 3000), polypropylene glycol (MW < ∼ 3000), polyester polyols (MW < ∼ 3000), polyethylene glycol (MW < ∼ 3000), pentaerythritol, triethanol amine, glycerin, 1,6-hexanediol, N-methyl-N,N-diethanol amine, trimethylol propane and N,N,N',N'-tetrakis(2-hydroxypropyl)ethylenediamine. The preferred alcohol is octadecanol. Preferred amines to react with monofunctional isocyanates to make the isocyanate-derived waxes and resins of this invention include any monofunctional amine, with the exception of tertiary amines void of other nucleophilic functional groups (e.g., triethylamine). For instance, the monoamine could be any aliphatic primary or secondary amine [e.g., a C 1 -C 22 or higher linear amine, any branched amine or any cyclic aliphatic amine such as methyl amine, ethyl amine, (n- and iso-)propyl amine, (n-, iso-, and t-) butyl amine, (n-, iso-, t-) pentyl amine, (n-, iso-, t-) hexyl amine, (n-, iso-, t-) octyl amine, (n-, iso-, t-) nonyl amine, (n- and branched) decyl amine, (n- and branched) undecyl amine, (n- and branched) octadecyl amine, (n- and branched) hexadecyl amine, (n- and branched) dodecyl amine, dimethyl amine, diethyl amine, di(n-, and iso-)propyl amine, di(n-, iso-, t-)butyl amine, di(n-, iso-, t-)pentyl amine, di(n-, iso-, t-)hexyl amine, di(n-, iso-, t-)cyclohexyl amine, di(n-, iso-, t-)heptyl amine, di(n-, iso-, t-)octyl amine, di(n-, iso-, t-)decyl amine, di(n-, iso-, t- )octadecyl amine, di(n-, iso-, t-)dodecyl amine, cyclohexyl amine, 2,3-dimethyl-1-cyclohexylamine, piperidine, and pyrrolidine; any aliphatic/aromatic amines (e.g., benzyl amine or analogues with longer or additional alkyl chains); aromatic amines such as aniline and anisidine; fused ring amines such as rosin amine, dehydroabietyl amine, dihydroabietyl amine and hydroabietyl amine; and miscellaneous amines (e.g., adamantyl amine, isonipecotamide, polyoxyalkylenemono-, di-, or triamines, such as M-, D-, and T-series Jeffamines available commercially from Huntsman Chemical Company of Austin, Texas; 3,3'-diamino-N-methyl-dipropylamine, as well as multifunctional amines such as polyethylene imine; ethylene diamine; hexamethylene diamine; isomers of cyclohexyldiamines; 1,3-pentadiamine; 1,12-dodecanediamine; 3-dimethylamino-propylamine; 4,7,10-trioxa-1,13-tridecanediamine; diethylene triamine; 3,3-diamino-N-methyldipropylamine; and tris(2-aminoethyl)amine. The preferred amine is octadecylamine. Additionally, hydroxyl/amino containing compounds can be employed (with di- and higher functionality isocyanates taking advantage of the difference in reactivity of the amine over the hydroxyl group, or with monoisocyanates reacting with the amine preferentially or with both the amine and the hydroxyl groups). Examples of this include ethanolamine and diethanolamine. Additionally, amides or other nucleophile containing compounds can be reacted with the isocyanates (mono, di). Some examples include: urea, oleamide and stearamide. Preferred precursors to the urethane resins and urethane/urea resins of the present invention include mono-, di- and other poly-isocyanates. Examples of monoisocyanates include octadecylisocyanate; octylisocyanate; butyl and t-butylisocyanate; cyclohexyl isocyanate; adamantyl isocyanate; ethylisocyanatoacetate; ethoxycarbonylisocyanate; phenyliso-cyanate; alphamethylbenzyl isocyanate; 2-phenylcyclopropyl isocyanate; benzylisocyanate; 2-ethylphenylisocyanate; benzoylisocyanate; meta and para-tolylisocyanate; 2-, 3-, or 4-nitrophenylisocyanates; 2-ethoxyphenyl isocyanate; 3-methoxyphenyl isocyanate; 4-methoxyphenylisocyanate; ethyl 4-isocyanatobenzoate; 2,6-dimethylphenylisocyante; 1-naphthylisocyanate; and (naphthyl)ethylisocyantes. Examples of diisocyanates include isophorone diisocyanate (IPDI); toluene diisocyanate (TDI); diphenylmethane-4,4'-diisocyanate (MDI); hydrogenated diphenylmethane-4,4'-diisocyanate (H 12 MDI); tetra-methyl xylene diisocyanate (TMXDI); hexamethylene-1,6-diisocyanate (HDI); hexamethylene-1,6-diisocyanate; napthylene-1,5-diisocyanate; 3',3'-dimethoxy-4,4'-biphenyldiisocyanate; 3,3'-dimethyl-4,4'-bimethyl-4,4'-biphenyldiisocyanate; phenylene diisocyanate; 4,4'-biphenyldiisocyanate; trimethylhexamethylene diisocyanate; tetramethylene xylene diisocyanate; 4,4'-methylenebis(2,6-diethylphenyl isocyanate); 1,12-diisocyanatododecane; 1,5-diisocyanato-2-methylpentane; 1,4-diisocyanatobutane; and cyclohexylene diisocyanate and its isomers; and uretidione dimers of HDI. Examples of triisocyanates or their equivalents indude the trimethylolpropane trimer of TDI, isocyanurate trimers of TDI, HDI, IPDI, and biuret trimers of TDI, HDI, IPDI. Examples of higher isocyanate functionalities include copolymers of TDI/HDI as well as MDI oligomers. Phase change inks of this invention contain a phase change carrier system or composition. The phase change carrier composition is generally designed for use in either a direct printing mode or use in an indirect or offset printing transfer system. In the direct printing mode, the phase change carrier composition is generally made up of one or more chemicals that provide the necessary properties to allow the phase change ink (1) to be applied in a thin film of uniform thickness on the final receiving substrate when cooled to the ambient temperature after printing directly to the substrate; (2) to be ductile while retaining sufficient flexibility so that the applied image on the substrate will not fracture upon bending; and (3) to possess a high degree of lightness, chroma, transparency and thermal stability. In an offset printing transfer or indirect printing mode, the phase change carrier composition is designed to possess not only the above mentioned properties, but certain fluidic and mechanical properties necessary for use in such a system, as described in U.S. Patent No. 5,389,958. The phase change carrier composition and the inks made therefrom which collectively comprise the current invention contain a combination of urethane resins and/or urethane/urea resins, along with another critical ingredient. These critical ingredients can be supplemented with (one or more) optional ingredients to prepare commercial phase change carrier compositions. The urethane resins and mixed urethane/urea resin materials of the current invention are tailored to have the desirable properties mentioned above when used in the carrier composition of the inks of the present invention by varying one or more of the readily available commodity chemical precursors. The phase change carrier compositions of the current invention may be used in combination with conventional phase change ink colorant materials such as Color Index (C.I.) Solvent Dyes, Disperse Dyes, modified Acid and Direct Dyes, Basic Dyes, Sulphur Dyes, Vat Dyes, and/or polymeric dyes such as those disclosed in U.S. Patent No. 5,621,022, and/or pigments to produce a phase change ink. Alternatively, the phase change carrier compositions of the current invention may employ colored urethane resins or urethane/urea resins or other isocyanate-derived colored resins as described in European Patent Application no. 97 304729.3 and assigned to the assignee of the present invention, to produce a phase change ink. The third preferred critical ingredient of the phase change carrier compositions and the inks made therefrom of the present invention is a mono-amide. A mono-amide compound typically comprises either a primary or secondary mono-amide, but is preferably a secondary mono-amide. Of the primary mono-amides, stearamide, such as KEMAMIDE S, manufactured by Witco Chemical Company, can be employed herein. As for the secondary mono-amides, behenyl benenamide (KEMAMIDE EX-666), and stearyl stearamide (KEMAMIDE S-180), both manufactured by Witco Chemical Company, are extremely useful mono-amides. However, stearyl stearamide (KEMAMIDE S-180) is the mono-amide of choice in producing the phase change ink compositions of the present invention The phase change carrier compositions and the inks made therefrom of the present invention may contain at least one polyethylene wax. Preferably, the polyethylene wax has a molecular weight of 500 to 5,000; more preferably, of 700 to 2,000; and, most preferably, of 800 to 1,200. Preferred polyethylene waxes are Polywax 850, Polywax 1000 or Polywax 2000, all available from Petrolite. Preferably, the total amount of urethane resin or resins in the phase change carrier composition and the inks made therefrom will comprise 10% to 40%, more preferably, 15-35% and most preferably, 20-30%, by weight of the carrier composition. Preferably, the total amount of mixed urethane/urea resin or resins in the phase change carrier composition will likewise comprise 10% to 40%, more preferably 15-35% and most preferably, 20-30%, by weight of the carrier composition. Preferably, the total amount of mono-amide wax and polyethylene wax, if used, combined will comprise 40% to 70%, more preferably, 45-60% and most preferably 48-57% by weight of the carrier composition. Prior art phase change inks for use in direct and indirect transfer printing systems are described in U.S. Patent Nos. 4,889,560 and 5,372,852. These inks consist of a phase change ink carrier composition comprising one or more fatty amide-containing materials, usually consisting of a mono-amide wax and a tetra-amide resin, one or more tackifiers, one or more plasticizers and one or more antioxidants, in combination with compatible colorants. A preferred tetra-amide resin is a dimer acid based tetra-amide that is the reaction product of dimer acid, ethylene diamine, and stearic acid. The typical mono-amide is stearyl stearamide. A preferred tackifier resin is a glycerol ester of hydrogenated abietic (rosin) acid and a preferred antioxidant is that provided by Uniroyal Chemical Company under the tradename Naugard 524. The urethane and urethane/urea resins employed in this invention can replace one or more of the ingredients in this prior art carrier composition or inks employing the resin components of the present invention can have all of these prior art ingredients replaced by the urethane and/or urethane/urea resins disclosed herein and/or by isocyanate derived waxes. Upon melting inks employing urethane and/or mixed urethane/urea resins and mono-amide admixture can release potentially offensive aromas, such as sharp pungent or mildewy odors. The use of selected organoleptic maskant constitutents, such as fragrances, from 0.0005% to 0.25% by weight, and more preferably from 0.001% to 0.01% by weight, is effective to either eliminate completely or change the odor of the ink to a more pleasant and identifiable fragrance. Effective organoleptic maskant constituents have been obtained from International Flavors and Fragrances of Union Beach, New Jersey identified as 8125-HAZ Golden Forest and 8126 and 8127 HAZ Maskants. All are liquids and possess thermal stability at about 140°C in the carrier composition, are not extremely volatile, are oil soluble and are chemically inert. Flashpoints ranged from 91,1°C to 89,3°C to 61,1°C (196°F to 182°F to 142°F), respectively. All contain active ingredients selected from the group consisting of esters, lactones, aldehydes, ketones, alcohols, ethers, acetals, ketals, heterocycles, compositions having cumulated double bonds including pheromones, acetylenes, amines and mixtures thereof. These functional groups are represented in natural product fragrance extracts, such as Brazilian peppermint. The advantages of inks formulated with the combination of the aforementioned preferred critical ingredients (urethane resin, mixed urethane/urea resin, mono-amide) and the organoleptic maskant constituent over the prior art phase change inks are: (1) The urethane resins and mixed urethane/urea resins of this invention are very pure, being free of salts and other insoluble contaminants. This makes the inks made from these materials easy to filter and provides for high reliability in ink jet printing devices. This is a major advantage. (2) The urethane resins and mixed urethane/urea resins of this invention may be specifically tailored to give certain physical properties that optimize the performance of the inks of this invention in ink jet printing devices and on the output substrate. These desirable ink properties include melting point, viscosity, transparency and the dynamic mechanical properties referenced in U.S. Patent No. 5,389,958. (3) The urethane resins and mixed urethane/urea resins of this invention are used in combination with the mono-amide wax and polyethylene wax to give ink compositions that display an improved yield stress versus temperature curve over prior art ink compositions. This enables ink droplets to be spread and fused at elevated temperatures during the fusing and transfer steps in an indirect printing process, but at a lower pressure than was possible with prior art inks. (4) The ink formulations with the added organoleptic maskant disclosed herein exhibit no offensive odors, such as sharp, pungent or mildewy odors upon melting and/or provide a pleasing aroma. Many other patents describe other materials for use in phase change ink jet inks. Some representative examples include U.S. Patent Nos. 3,653,932; 4,390,369; 4,484,948; 4,684,956; 4,851,045; 5,006,170; 5,151,120; EP Application Nos. 0187352 and 0206286; and PCT Patent Application WO 94/04619. These other materials can include paraffins, microcrystalline waxes, ester waxes, amide waxes, fatty acids, fatty alcohols, fatty amides and other waxy materials, sulfonamide materials, resinous materials made from different natural sources (tall oil rosins and rosin esters are an example) and many synthetic resins, oligomers, polymers, co-polymers, and ionomers. It will be obvious to those skilled in the art that the phase change carrier composition of this invention could optionally contain any of the optional other materials. . The aforementioned U.S. Patent No. 5,496,879 and German patent publications DE 4205636AL and DE 4205713AL, assigned to Siegwerk Farbenfabrik Keller, Dr. Rung and Co., describe materials used for phase change or hot melt gravure printing. It will be obvious to those skilled in the art that the isocyanate-derived materials of this current invention would be compatible with those materials and could also be used in that application or other similar printing methods that employ hot melt ink technology. It also will be obvious to those skilled in the art that other ink colors besides the subtractive primary colors are desirable for applications, such as postal marking or industrial marking and labeling using phase change printing, and that this invention is applicable to these needs. Infrared (IR) or ultraviolet (UV) absorbing dyes can also be incorporated into the inks of this invention for use in applications such as "invisible" coding or marking of products. The inks of the present invention can be equally well employed in apparatus for direct or indirect (offset) printing applications. When employed in direct printing applications a suitable method of printing or producing a layer of a phase change colored ink directly on the surface of a substrate can comprise: (1) forming a phase change ink composition in the solid phase, comprising an admixture of(a) a phase change carrier composition containing at least one isocyanate-derived resin or wax, (b) an organoleptic constituent, and (c) a phase change compatible colorant. (2) transferring the solid phase, phase change colored ink composition to a phase change ink application means or print head; (3) raising the operating temperature of the application means or print head to a level whereby a liquid phase, phase change colored ink composition is formed; (4) providing a substrate in proximity to the application means; (5) applying a predetermined pattern of the liquid phase, phase change colored ink composition to at least one surface of the substrate; and (6) lowering the temperature of the applied ink composition to form a solid phase, phase change ink pattern on the substrate. An appropriate direct printing process is described in greater detail in U.S. Patent No. 5,195,430. When employed in indirect or offset printing applications a suitable method of printing or producing a layer of a phase change colored ink indirectly on the surface of a substrate by transferring from an intermediate transfer surface can comprise: (1) forming a phase change ink composition in the solid phase, comprising an admixture of (a) a phase change carrier composition containing at least one isocyanate-derived resin or wax, (b) an organoleptic constituent, and (c) a phase change compatible colorant. (2) transferring the solid phase, phase change colored ink composition to a phase change ink application means or a print head; (3) raising the operating temperature of the application means or print head to a level whereby a liquid phase, phase change colored ink composition is formed; (4) providing an intermediate transfer surface in proximity to the application means; (5) applying a predetermined pattern of the liquid phase, phase change colored ink composition to the intermediate transfer surface; (6) lowering the temperature of the applied ink composition to form a solid phase, phase change ink pattern on the intermediate transfer surface at a second, intermediate temperature; (7) transferring said phase change ink composition from the intermediate transfer surface to a final substrate; and (8) fixing the phase change ink composition to the substrate to form a printed substrate, the phase change ink composition having (a) a compressive yield strength which will allow it to be malleable to spread and deform without an increase in stress when compressive forces are applied thereto at the second operating temperature, and sufficient internal cohesive strength to avoid shear banding and weak behavior when said phase change ink composition is transferred and fixed to said substrate, and (b) a ductility on the substrate after fixing. An appropriate offset or indirect printing process is described in greater detail in U.S. Patent No. 5,389,958. The present invention is further described in detail by means of the following Examples and Comparisons. All parts and percentages are by weight and all temperatures are degrees Celsius unless explicitly stated otherwise. EXAMPLE 1 Cyan Ink Made From Amide Wax, Mixed Urethane/Urea Resin and Cyan Colored Urethane Resin In a stainless steel beaker are combined about 250grams of the cyan colored resin from Example 2 of co-pending European Patent Application No97 304729.3(see below) and assigned to the assignee of the present invention, about 250grams of the reaction product urethane/urea mixture material from Example 2 of US Patent No 5,830,942 (see below) about 540grams of Witco S-180 stearyl stearamide 1 , about 2.0 grams of Uniroyal Naugard 445 antioxidant 2 , and about 0.01 grams of an IFF 8125 HAZ organoleptic maskant constituent 3 . The materials are melted together at a temperature of 140°C in an oven, then blended by stirring in a temperature controlled mantle at about 115°C for about 1/2 hour. After stirring for about 1/2 hour, the cyan ink is filtered through a heated Mott apparatus (available from Mott Metallurgical) using #3 Whatman filter paper and a pressure of about 15 psi. The filtered phase change ink is poured into molds and allowed to solidify to form ink sticks. The ink sticks formed are placed in an oven at about 125°C and covered with foil. A 1 cm 2 hole is poked in each ink cover and the melted ink emitted a pervasive clean soapy fragrance. The odor persists after the samples are retained in an oven at the same temperature overnight. This final ink product is characterized by the following physical properties: viscosity of about 13.0 cPs as measured by a Ferranti-Shirley cone-plate viscometer at about 140°C, a melting point of about 89°C as measured by differential scanning calorimetry using a DuPont 2100 calorimeter, and a T g of about 27.5°C as measured by Dynamic Mechanical Analysis using a Rheometrics Solids Analyzer (RSAII). The spectral strength of the ink is determined using a spectrophotographic procedure based on the measurement of the colorant in solution by dissolving the solid ink in butanol and measuring the absorbance using a Perkin Elmer Lambda 2S UV/VIS spectrophotometer. The spectral strength of the ink is measured as about 1069 milliliters-Absorbance Units per gram at λ max . EXAMPLE 2 Cyan Ink Made From Amide Wax, Mixed Urethane/Urea Resin and Cyan Colored Urethane Resin In a stainless steel beaker are combined about 250grams of the cyan colored resin from Example 2 of co-pending European Patent Application No97 304729.3(see below) and assigned to the assignee of the present invention, about 250grams of the reaction product urethane/urea mixture material from Example 2 of US Patent No 5,830,942 (see below) about 540grams of Witco S-180 stearyl stearamide1 , about 2.0 grams of Uniroyal Naugard 445 antioxidant 2 and about 0.01 grams of an IFF 8127 HAZ organoleptic maskant constituent 3 . The materials are melted together at a temperature of 140°C in an oven, then blended by stirring in a temperature controlled mantle at about 115°C for about 1/2 hour. After stirring for about 1/2 hour, the cyan ink is filtered through a heated Mott apparatus (available from Mott Metallurgical) using #3 Whatman filter paper and a pressure of about 15 psi. The filtered phase change ink is poured into molds and allowed to solidify to form ink sticks. The ink sticks formed are placed in an oven at about 125°C and covered with foil. A 1 cm 2 hole is poked in each ink cover and the melted ink emitted a pervasive clean soapy fragrance. The odor persists after the samples are retained in an oven at the same temperature overnight. This final ink product is characterized by the following physical properties: viscosity of about 13.0 cPs as measured by a Ferranti-Shirley cone-plate viscometer at about 140°C, a melting point of about 89°C as measured by differential scanning calorimetry using a DuPont 2100 calorimeter, and a T g of about 27.5°C as measured by Dynamic Mechanical Analysis using a Rheometrics Solids Analyzer (RSAII). The spectral strength of the ink is determined using a spectrophotographic procedure based on the measurement of the colorant in solution by dissolving the solid ink in butanol and measuring the absorbance using a Perkin Elmer Lambda 2S UV/VIS spectrophotometer. The spectral strength of the ink is measured as about 1069 milliliters·Absorbance Units per gram at λ max . EXAMPLE 3 Cyan Ink Made From Amide Wax, Mixed Urethane/Urea Resin and Cyan Colored Urethane Resin In a stainless steel beaker are combined about 250grams of the cyan colored resin from Example 2 of co-pending European Patent Application No97 304729.3(see below) and assigned to the assignee of the present invention, about 250grams of the reaction product urethane/urea mixture material from Example 2 of US Patent No 5,830,942 (see below) about 540grams of Witco S-180 stearyl stearamide 1 , about 2.0 grams of Uniroyal Naugard 445 antioxidant 2 , and about 0.01 grams of an IFF 8126 HAZ organoleptic maskant constituent 3 . The materials are melted together at a temperature of 140°C in an oven, then blended by stirring in a temperature controlled mantle at about 115°C for about 1/2 hour. After stirring for about 1/2 hour, the cyan ink is filtered through a heated Mott apparatus (available from Mott Metallurgical) using #3 Whatman filter paper and a pressure of about 15 psi. The filtered phase change ink is poured into molds and allowed to solidify to form ink sticks. The ink sticks formed are placed in an oven at about 125°C and covered with foil. A 1 cm 2 hole is poked in each ink cover and the melted ink emitted a pervasive light fruity fragrance. The odor persists after the samples are retained in an oven at the same temperature overnight. The ink stick final ink product is characterized by the following physical properties: viscosity of about 13.0 cPs as measured by a Ferranti-Shirley cone-plate viscometer at about 140°C, a melting point of about 89°C as measured by differential scanning calorimetry using a DuPont 2100 calorimeter, and a T g of about 27.5°C as measured by Dynamic Mechanical Analysis using a Rheometrics Solids Analyzer (RSAII). The spectral strength of the ink is determined using a spectrophotographic procedure based on the measurement of the colorant in solution by dissolving the solid ink in butanol and measuring the absorbance using a Perkin Elmer Lambda 2S UV/VIS spectrophotometer. The spectral strength of the ink is measured as about 1069 milliliters·Absorbance Units per gram at λ max . EXAMPLE 4 Black Ink Made From Amide Wax, Mixed Urethane/Urea Resin and Black Colored Urethane Resin In a stainless steel beaker are combined about 301grams of the colored resin from Example 3 of co-pending European Patent Application No97 304729.3(see below) and assigned to the assignee of the present invention, about 374grams of the reaction product urethane/urea mixture material from Example 2 of US Patent No 5,830,942 (see below) about 802grams of Witco S-180 stearyl stearamide 1 , about 3.0 grams of Uniroyal Naugard 445 antioxidant 2 , and about 0.02 grams of IFF 8125 HAZ organoleptic maskant constituent 3 . The materials are melted together at a temperature of about 140°C in an oven, then blended by stirring in a temperature controlled mantle at about 115°C for about 1/2 hour. The black ink is then filtered through a heated Mott apparatus (available from Mott Metallurgical) using #3 Whatman filter paper and a pressure of about 15 psi. The filtered phase change ink is poured into molds and allowed to solidify to form ink sticks. The ink sticks formed are placed in an oven at about 125°C and covered with foil. A 1 cm 2 hole is poked in each ink cover and the melted ink emitted a pervasive clean soap fragrance. The odor persists after the samples were retained in an oven at the same temperature overnight. This final ink product is characterized by the following physical properties: viscosity of about 13.3 cPs as measured by a Ferranti-Shirley cone-plate viscometer at about 140°C, a melting point of about 89°C as measured by differential scanning calorimetry using a DuPont 2100 calorimeter, and a T g of about 16°C as measured by Dynamic Mechanical Analysis using a Rheometrics Solids Analyzer (RSAII). The spectral strength of the ink is determined using a spectrophotographic procedure based on the measurement of the colorant in solution by dissolving the solid ink in butanol and measuring the absorbance using a Perkin Elmer Lambda 2S UV/VIS spectrophotometer. The spectral strength of the ink is measured as about 869 milliliters·Absorbance Units per gram at λ max. EXAMPLE 5 Black Ink Made From Amide Wax, Mixed Urethane/Urea Resin and Black Colored Urethane Resin In a stainless steel beaker are combined about 301 grams of the colored resin from Example 3 of co-pending European Patent Application No97 304729.3(see below) and assigned to the assignee of the present invention, about 374grams of the reaction product urethane/urea mixture material from Example 2 of US Patent No 5,830,942 (see below) about 802grams of Witco S-180 stearyl stearamide 1 , about 3.0 grams of Uniroyal Naugard 445 antioxidant 2 , and about 0.02 grams of IFF 8126 HAZ organoleptic maskant constituent 3 . The materials are melted together at a temperature of about 140°C in an oven, then blended by stirring in a temperature controlled mantle at about 115°C for about 1/2 hour. The black ink is then filtered through a heated Mott apparatus (available from Mott Metallurgical) using #3 Whatman filter paper and a pressure of about 15 psi. The filtered phase change ink is poured into molds and allowed to solidify to form ink sticks. The ink sticks formed are placed in an oven at about 125°C and covered with foil. A 1 cm 2 hole is poked in each ink cover and the melted ink emitted a pervasive clean soap fragrance. The odor persists after the samples were retained in an oven at the same temperature overnight. This final ink product is characterized by the following physical properties: viscosity of about 13.3 cPs as measured by a Ferranti-Shirley cone-plate viscometer at about 140°C, a melting point of about 89°C as measured by differential scanning calorimetry using a DuPont 2100 calorimeter, and a T g of about 16°C as measured by Dynamic Mechanical Analysis using a Rheometrics Solids Analyzer (RSAII). The spectral strength of the ink is determined using a spectrophotographic procedure based on the measurement of the colorant in solution by dissolving the solid ink in butanol and measuring the absorbance using a Perkin Elmer Lambda 2S UV/VIS spectrophotometer. The spectral strength of the ink is measured as about 869 milliliters·Absorbance Units per gram at λmax. EXAMPLE 6 Black Ink Made From Amide Wax, Mixed Urethane/Urea Resin and Black Colored Urethane Resin In a stainless steel beaker are combined about 301 grams of the colored resin from Example 3 of co-pending European Patent Application No97 304729.3(see below) and assigned to the assignee of the present invention, about 374grams of the reaction product urethane/urea mixture material from Example 2 of US Patent No 5,830,942 (see below) about 802grams of Witco S-180 stearyl stearamide 1 , about 3.0 grams of Uniroyal Naugard 445 antioxidant 2 , and about 0.02 grams of IFF 8127 HAZ organoleptic maskant constituent 3 . The materials are melted together at a temperature of about 140°C in an oven, then blended by stirring in a temperature controlled mantle at about 115°C for about 1/2 hour. The black ink is then filtered through a heated Mott apparatus (available from Mott Metallurgical) using #3 Whatman filter paper and a pressure of about 15 psi. The filtered phase change ink is poured into molds and allowed to solidify to form ink sticks. The ink sticks formed are placed in an oven at about 125°C and covered with foil. A 1 cm 2 hole is poked in each ink cover and the melted ink emitted a pervasive light fruity fragrance. The odor persists after the samples were retained in an oven at the same temperature overnight. This final ink product is characterized by the following physical properties: viscosity of about 13.3 cPs as measured by a Ferranti-Shirley cone-plate viscometer at about 140°C, a melting point of about 89°C as measured by differential scanning calorimetry using a DuPont 2100 calorimeter, and a T g of about 16°C as measured by Dynamic Mechanical Analysis using a Rheometrics Solids Analyzer (RSAII). The spectral strength of the ink is determined using a spectrophotographic procedure based on the measurement of the colorant in solution by dissolving the solid ink in butanol and measuring the absorbance using a Perkin Elmer Lambda 2S UV/VIS spectrophotometer. The spectral strength of the ink is measured as about 869 milliliters·Absorbance Units per gram at λ max . For information, Examples 2 and 3 of co-pending European Patent Application No 97 304729.3 and Example 2 of US Patent No 5,830,942, as referred to in Examples 1 to 6 of the present application, are set out below: EXAMPLE 2 (European Patent Application No 97 304729.3) The Reaction Product of Octylphenol Ethoxylate, Isophorone Diisocyanate and Cyan Reactive Colorant About 525.0 grams (4.73 equiv.) of isophorone diisocyanate 1 , about 1.5 grams of dibutyltindilaurate 2 catalyst, and about 992.0 grams (3.91 equiv.) of octylphenol ethoxylate 3 were added to a 3000 ml three-neck resin kettle equipped with a Trubore stirrer, a N 2 atmosphere inlet, and a thermocouple-temperature controller. The reaction mixture was heated to about 135°C and held for approximately 3.5 hours with stirring under nitrogen. About 240.6 grams (0.473 equiv.) of a cyan polymeric colorant 4 then were added and the mixture was heated to about 135°C for 2 hours. An additional about 110.0 grams (0.433 equiv.) of octylphenol ethoxylate 3 were added and the reaction mixture was heated at about 150°C for approximately 2 hours. An FT-IR of the product was obtained to insure all of the isocyanate (NCO) functionality was consumed. The absence (disappearance) of a peak at about 2285 cm -1 (NCO) and the appearance (or increase in magnitude) of peaks at about 1740-1680 cm -1 and about 1540-1530 cm -1 corresponding to urethane frequencies were used to confirm this. The diurethane reaction product was poured into aluminum molds and allowed to cool and harden. This final colored resin product was characterized by the following physical properties: viscosity of about 181.8 cPs as measured by a Ferranti-Shirley cone-plate viscometer at about 140°C, a melting point of about 59.9-70.2°C as measured by electrothermal capillary melting point apparatus, and a T g of about 23.1°C as measured by differential scanning calorimetry using a DuPont 2100 calorimeter at a scan rate of 20°C/minute, and a spectral strength of about 5588 milliliters·Absorbance Units per gram at λmax as measured by dilution in n-butanol using a Perkin Elmer Lambda 25 UV/VIS spectrophotometer. EXAMPLE 3 (European Patent Application No 97 304729.3) The Reaction Product of Octylphenol Ethoxylate, Isophorone Diisocyanate and Blended Black Reactive Colorants About 150.0 grams (0.295 equiv.) of a cyan polymeric reactive colorant 1 , about 225.0 grams (0.147 equiv.) of a violet polymeric colorant corresponding to Colorant U from Table I of U.S. Patent No. 5,231,135; about 345.0 grams (0.552 equiv.) of an orange polymeric reactive colorant corresponding to Colorant B from Table I of U.S. Patent No. 5,231,135; about 450.0 grams (4.054 equiv.) of isophorone diisocyanate 2 and about 0.18 grams of dibutyltindilaurate catalyst 3 were added to a 3000 ml three-neck resin kettle equipped with a Trubore stirrer, a N 2 atmosphere inlet, and a thermocouple-temperature controller. The reaction mixture was heated to about 90°C with stirring under nitrogen. After 3.5 hours at about 90°C, about 1.0 gram of additional dibutyltindilaurate catalyst and about 805.0 grams (3.012 equiv.) of octylphenol ethoxylate 4 were added and the temperature was raised to about 130°C and held for approximately 3.5 hours. An FT-IR of the product was obtained to insure all of the isocyanate (NCO) functionality was consumed. The absence (disappearance) of a peak at about 2285 cm -1 (NCO) and the appearance (or increase in magnitude) of peaks at about 1740-1680 cm -1 and about 1540-1530 cm -1 corresponding to urethane frequencies were used to confirm this. The diurethane reaction product was poured into aluminum molds and allowed to cool and harden. This final colored resin product was characterized by the following physical properties: viscosity of about 163.0 cPs as measured by a Ferranti-Shirley cone-plate viscometer at about 140°C, a melting point of below ambient temperature and not measurable by electrothermal melting point apparatus, a T g of about 3.8°C as measured by differential scanning calorimetry using a DuPont 2100 calorimeter at a scan rate of 20°C/minute, and a spectral strength of about 4667 milliliters · Absorbance Units per gram at λmax as measured by dilution in n-butanol using a Perkin Elmer Lambda 25 UV/VIS spectrophotometer. EXAMPLE 2 (US Patent No 5,830,942) The Reaction Product of 1.5 Parts Hydroabietyl Alcohol, 0.5 Parts Octadecyl Amine, and Isophorone Diisocyanate About 240.2 grams (0.676 moles) of hydroabietyl alcohol 1 was added to a 1000ml four-neck resin kettle equipped with a Trubore stirrer, an N 2 atmosphere inlet, 200 ml addition funnel, and a thermocouple-temperature controller. About 100.0 grams (0.45 moles) of isophorone diisocyanate 2 was added to the addition funnel. Agitation of the hydroabietyl alcohol first was begun and then all of the isophorone diisocyanate was added over approximately 5 minutes. About 0.22 grams of dibutyltindilaurate 3 catalyst was added and the reaction mixture heated to about 125°C under an N 2 atmosphere. After 4 hours at 125°C, about 59.95 grams (0.225 moles) of octadecyl amine 4 was added and the temperature raised to about 150°C and held for approximately 2 hours. An FT-IR of the reaction product was run to insure all of the NCO functionality was consumed. The absence (disappearance) of a peak at about 2285 cm -1 (NCO) and the appearance (or increase in magnitude) of peaks at about 1705-1635 cm -1 and about 1515-1555 cm -1 corresponding to urea frequencies and about 1740-1680 cm -1 and about 1540-1530 cm -1 corresponding to urethane frequencies were used to confirm this. The final mixed urethane/urea resin product was poured into aluminum molds and allowed to cool and harden. This final product was a clear solid resin at room temperature characterized by the following physical properties: viscosity of about 314.8 cPs as measured by a Ferranti-Shirley cone-plate viscometer at about 140°C, a melting point of from about 67.9°C to about 87.0°C as measured by an electrothermal capillary melting point apparatus, and a T g of about 23°C as measured by differential scanning calorimetry using a DuPont 2100 calorimeter at a scan rate of 20°C/minute.

Claims: A phase change ink carrier composition comprising: a) a urethane resin that is the reaction product of at least one alcohol and an isocyanate, the at least one alcohol being a monohydric aliphatic alcohol, a monohydric aromatic alcohol, a monohydric aliphatic/aromatic alcohol, a monohydric fused ring alcohol, a polyol or mixtures thereof; and/or a mixed urethane/urea resin that is the reaction product of at least one alcohol, an isocyanate, and at least one monoamine; b) a mono-amide; and c) an organoleptic maskant. A phase change ink carrier composition as claimed in claim 1 wherein the organoleptic maskant comprises from about 0.0005 to about 0.25% by weight of the composition. A phase change ink carrier composition as claimed in claim 2 wherein the organoleptic maskant comprises from about 0.001 to about 0.01 % by weight of the composition. A phase change ink carrier composition as claimed in any preceding claim wherein the organoleptic maskant is a fragrance. A phase change ink carrier composition as claimed in any preceding claim wherein the organoleptic maskant is an ester, a lactone, an aldehyde, a ketone, an alcohol, an ether, an acetal, a ketal, a heterocycle, a composition having cumulated double bonds including pheromones, an acetylene, an amine or a mixture thereof. A phase change ink carrier composition as claimed in claim 1 wherein the isocyanate employed in making the urethane resin is a monoisocyanate, a diisocyanate, a triisocyanate, a copolymer of a diisocyanate or a copolymer of a triisocyanate. A phase change ink carrier composition as claimed in claim 6 wherein the isocyanate is isophorone diisocyanate. A phase change ink carrier composition as claimed in claim 1 wherein the at least one alcohol, employed in making the urethane resin is hydroabietyl alcohol, octylphenol ethoxylated or octadecyl alcohol. A phase change ink carrier composition as claimed in claim 8 wherein the at least one alcohol is octylphenol ethoxylate. A phase change ink carrier composition as claimed in claim 1 wherein the at least one alcohol employed in making the mixed urethane/urea resin is a monohydric aliphatic alcohol, a monohydric aromatic alcohol, a monohydric aliphatic/aromatic alcohol, a monohydric fused ring alcohol, a polyol or mixtures thereof. A phase change ink carrier composition as claimed in claim 10 wherein the at least one alcohol is hydroabietyl alcohol, octylphenol ethoxylate or octadecyl alcohol. A phase change ink carrier composition as claimed in claim 1 wherein the isocyanate employed in making the mixed urethane/urea resin is a monoisocyanate, a diisocyanate, a triisocyanate, a copolymer of a diisocyanate or a copolymer of a triisocyanate. A phase change ink carrier composition as claimed in claim 12 wherein the isocyanate is isophorone diisocyanate. A phase change ink carrier composition as claimed in claim 1 wherein the at least one amine employed in making the mixed urethane/urea resin is an aliphatic monoamine, an aromatic monoamine, an aliphatic/aromatic monoamine, a fused ring system monoamine, a multifunctional monoamine, or a hydroxyl/amino containing compound. A phase change ink carrier composition as claimed in claim 14 wherein the amine is octadecyl amine. A phase change ink carrier composition as claimed in claim 1 further comprising an anti-oxidant. A phase change ink composition comprising a phase change ink carrier composition as claimed in any preceding claim and at least one phase change compatible colourant. A phase change ink composition as claimed in claim 17 wherein the phase change compatible colorant is a dye, a colored resin or a pigment. A method for producing a layer of a phase change ink on a surface of a substrate, which comprises: (1) forming a phase change ink composition in the solid phase, comprising an admixture of (a) a phase change carrier composition containing at least one isocyanate-derived resin or wax, (b) an organoleptic maskant, and (c) a phase change compatible colorant; (2) transferring the solid phase, phase change ink composition to a phase change ink application means; (3) raising the operating temperature of the application means to a level whereby a liquid phase, phase change ink composition is formed; (4) providing a substrate in proximity to said application means; (5) applying a predetermined pattern of the liquid phase, phase change ink composition to at least one surface of said substrate; (6) lowering the temperature of the applied ink composition to form a solid phase, phase change ink pattern on the substrate A method for producing a layer of a phase change ink on the surface of a substrate, which comprises: (1) employing in a printing apparatus a phase change ink composition in the solid phase comprising an admixture of (a) a phase change carrier composition containing at least one isocyanate-derived resin or wax, (b) an organoleptic maskant, and (c) a phase change compatible colorant; (2) applying the phase change ink composition in a desired pattern to an intermediate transfer surface; (3) transferring the desired pattern of the phase change ink composition to the surface of the substrate. The use of a phase change ink carrier composition comprising an organoleptic maskant in an ink jet printer.

Inventors: BANNING JEFFERY H, BRIDGEMAN RANDALL R, KING CLIFFORD R, TITTERINGTON DONALD R, BANNING, JEFFERY H., BRIDGEMAN, RANDALL R., KING, CLIFFORD R., TITTERINGTON, DONALD R.
Applicants: XEROX CORP, XEROX CORPORATION
Application year: 1999
Main classification: C09D11
IPC codes: C09D175, C09D11, B41J2, B41M5