SMALL PARTICLE TERBIUM ACTIVATED YTTRIUM GADOLINIUM BORATE PHOSPHORS AND METHOD OF MAKING

Abstract: A method of forming a phosphor having the empirical formula: (Y1-x-y-zGdxTbyCez)BO3 wherein: 0.0</=x</=0.2; 0.01</=y</=0.1; and 0.0</=z</=0.1; which method comprises: thermally decomposing a xerogel at a temperature below a solid state reaction temperature to obtain said phosphor; wherein the xerogel has been formed by drying a gel obtained from a dilute acidic solution comprising a source of yttrium, a source of terbium, optionally a source of gadolinium and optionally a source of cerium and an organic precursor providing a source of boron.

Description: SMALL PARTICLE TERBIUM ACTIVATED YTTRIUM GADOLINIUM BORATE PHOSPHORS AND METHOD OF MAKING FIELD OF THE INVENTION This invention relates to improved yttrium borate and yttrium gadolinium borate phosphor particles doped with terbium as an activator and optionally, with cerium as a sensitizer, .and a method for forming such particles. More specifically, this invention relates to novel phosphor particles and method of forming such particles from oxides, nitrates, hydroxides and organic precursors, which method forms small particles that provide the improved performance (higher brightness, shorter persistence, better stability, longer life time and good color saturation) required for flat panel display (FPD) and lamp applications. BACKGROUND OF THE INVENTION Plasma display panels (PDP), as used in high definition televisions (HDTV) and projection television (PTV) applications, conventionally use manganese activated zinc silicate phosphor as a green emitting component due to its availability and high quantum efficiency. However, compared with red and blue emitting phosphors, zinc silicate exhibits a wide spectrum of emission with low color purity, long persistence and fast saturation with vacuum ultra violet (VUV) flux. Therefore, many efforts have been made to develop a phosphor that provides improved performance characteristics and can be used to replace Mn activated zinc silicate. In addition, the red phosphor, green phosphor and blue phosphor currently used in PDP's have different physical characteristics and each requires a different phosphor paste rheology and screening process. Also, after screening, these phosphors exhibit different optical and electrical characteristics. These different characteristics affect the design and performance of the display. Therefore, to provide for compatible physical characteristics, it would be advantageous to form all three phosphors from a common host material that exhibits suitable red, green and blue emission under Xenon plasma excitation. HDTV and similar types of display devices should have high resolution and high brightness for better performance. This can be achieved only with thin phosphor screens formed with very small phosphor particles (1-2 microns) in a close rib structure. Screens with small particles have a higher packing density and also require a lower binder content. HDTV and other such devices also require phosphors to display short persistence (between 5 .and 10 ms) in order to prevent the formation of ghost images. It is known that lanthanide borates provide high quantum efficiency, good stability at operating temperatures and long life time with various activators, coactivators and sensitizers, particularly under VUV excitation. However, very limited information is available on the preparation and luminescence of lanthanide borates, and particularly, rare earth (RE) activated yttrium borate and yttrium gadolinium borate phosphors. SUMMARY OF THE INVENTION Accordingly, it is an object of the present invention to provide a Tb + activated yttrium borate and yttrium gadolinium borate phosphors, optionally sensitized by doping with cerium in the form of Ce 3+ ; the phosphors having the empirical formula: (Yι.χ. y . z Gd x Tb y Ce z )BO 3 wherein: 0.0<x<0.2; 0.01< y < 0.1; and 0.0< z < 0.1. It is also an object of the present invention to provide a method of forming such phosphors, which method provides the phosphor in the form of a powder that has a small particle size and displays improved brightness. The phosphors of the present invention can be synthesized using any of three different processes, specifically, a solid state reaction, a solution process and a sol-gel process. The preferred process will depend on the required particle size distribution. The sol-gel process provides very fine particles (0.1 to 2 microns). The solution process forms fine particles (1 to 4 microns); and the solid state reaction results in conventional particle sizes (2 to 6 microns). In the case of the solution process, low molar concentration solutions of salts of the respective elements are mixed and subjected to reflux in an acid medium. Very fine powders result from the slow drying of such solutions. In all cases, it is preferable that the powders contain uniform, substantially spherical particles. Sols are dispersions of colloidal particles in a liquid. The gravitational forces on the particles are negligible. From a sol, a gel is formed with an interconnected, rigid network, having sub-micrometer pores and a polymeric chain having an average length on the order of microns. The particle size of the finished product is a function of the initial concentration of the starting sols, the gelation process, the manner in which the gels are dried, calcination temperature and the rate of cooling. The sol-gel and solution processes offer many advantages over conventional methods in the synthesis of fine powders and particularly in the synthesis of fine phosphor powders. Since all of the starting materials are mixed at the molecular level in a solution, a high degree of homogeneity is achievable. Doping of impurities (activators/ coactivators/ sensitizers) through solutions is straightforward, easy and effective. The pores in properly dried gels are often extremely small and the components of a homogenous gel are intimately mixed. The surface area of powders produced from sol-gel is very high, allowing for the use of lower processing temperatures. Phosphor materials are extremely sensitive to impurities; even in ppb levels. The low-temperatures of the solution process and sol-gel process minimize the potential for cross contamination. Some of the unwanted impurities left in the materials from conventional methods may pose a threat to the performance of a phosphor. For example, fluoride from a flux (MgF 2 ) can attack the glass surface of the display during operation. As the size of the phosphor particle decreases, the probability of electron and hole capture due to the presence of impurities increases and the electron/hole localization enhances the recombination rate via the impurity. The optimum impurity concentration (activator) level can be further increased with small particle size. The present invention is related to the growth of Tb 3+ and optionally Ce 3+ doped yttrium borate and yttrium, gadolinium borate phosphors by sol-gel, solution and solid state processes. More specifically, the present invention provides a process for forming a Tb 3+ and Ce 3+ doped yttrium borate or yttrium, gadolinium borate phosphor having the empirical formula: (Y 1 1 . y . I Gd x Tb y Ce I )B0 3 wherein: 0.0<x<0.2; 0.0 l<y<0.1 ; and 0.0.<z_<0.1 ; which method includes the steps of: (1) reacting a dilute solution comprising a source of yttrium, optionally a source of gadolinium, a source of terbium, optionally a source of cerium and an organic precursor providing a source of boron, in an acid medium to form a sol and/or a gel; and (2) thermally decomposing the powders obtained from the above, at a temperature below a solid state reaction temperature; or (3) mixing powdered sources of yttrium, optionally gadolinium, terbium, optionally cerium and an organic precursor providing a source of boron to form a mixed powder; and (4) firing the mixed powder at a temperature equal to or greater than the solid state reaction temperature. The term "solid state reaction temperature" refers to the temperature required to react two or more solids to produce a material (complex). This temperature is typically close to the melting point of the solids to be reacted i.e. a high temperature is generally required for a solid state reaction. Previously phosphor materials have typically been synthesised commercially by a solid state reaction between oxides or similar materials. The method of the present invention requires the use of a lower temperature than that used in these solid state reactions. BRIEF DESCRIPTION OF THE DRAWINGS FIG.1 provides a Thermo-Gravimetric Analysis (TGA) of rare earth (RE) borate xerogel powder. FIG.2 shows X-ray diffraction pattern of (a) Tb and (b) Tb and Ce doped Y, Gd borate phosphor. -4- FIG. 3 illustrates scanning electron micrographs of Tb and Ce doped Y, Gd borate phosphors prepared from (a) (b) RE hydroxides; (c) RE nitrates; and (d) RE oxides. FIG. 4 graphs the particle size distribution of Tb, Ce doped Y, Gd borate phosphors prepared from (a) RE hydroxides, (b) RE nitrates and (c) RE oxides. FIG. 5 provides spectral distribution of radiation energy from Xe lamps with MgF windows and suitable band pass filters at wavelengths of (a) 147 nm and (b) 173 nm. FIG. 6 shows emission spectra of Tb, Ce doped Y, Gd borate of present invention and Mn activated zinc silicate (best commercial) phosphors at 147 nm excitation, recorded at room temperature (A) without and (B) with an optical filter. FIG. 7 shows persistence (afterglow decay) of (a) Tb, and (b) Tb, Ce doped Y, Gd borate phosphors, recorded at room temperature. DETAILED DESCRIPTION OF THE INVENTION There are a number of display applications where a green phosphor with high brightness, shorter persistence, color purity (saturation), better stability and long life (time of operation) would significantly improve the performance of the display. The green component is very important as the human eye perceives more towards green in the visible spectrum. Since commercially available zinc silicate based phosphors fail to satisfy all the above requirements, a new phosphor and process for synthesizing such a phosphor has been developed to overcome the above limitations. The small size phosphor particles are particularly suitable for use in applications in which a high packing density is required. The result of this development effort is the basis of the present invention. This invention provides a method of synthesizing yttrium borate and yttrium, gadolinium borate phosphors incorporating high concentrations of activator ion (Tb 3+ ) and optionally, sensitizer ion (Ce 3+ ). The formation of a yttrium or yttrium, gadolinium solid solution which is critical, depends mainly on the reaction temperature and conditions. In a solid state reaction, respective oxides, nitrides or hydroxides are reacted at higher temperatures in the presence of excess boric acid. At these high temperatures, other phases can form, such as individual borate 's and unreacted oxides, nitrides or hydroxides of yttrium, gadolinium, etc. Proper doping of impurity ions into the lattice of the complex is less certain at higher temperatures. Also, the high temperature process leads to growth of larger particles. The sol-gel and solution processes of the present invention can be divided into two categories: (1) aqueous-based processes that starts from a solution of a metal salt and (2) alcohol-based processes that starts from a metal alkoxide. Selection of the most suitable process will be based primarily on the cost and availability of the starting chemicals. Since the purity of the starting chemicals is very important to the synthesis of phosphors, the starting chemicals are of 99.99 to 99.9999% purity. Because metal alkoxides are expensive, nitrates of yttrium, gadolinium, terbium and cerium are particul.arly suitable metal sources and trimethyl borate is a particularly suitable source of boron. Initially, a trimethyl borate stock solution is prepared by mixing trimethyl borate and ethanol in a ratio of about 1 :10. To better underst.and these materials, a number of phosphors are prepared at different conditions. Metal precursors are synthesized by adopting the following routes: By using ion exch.ange resin, stable sol-gels are prepared. Yttrium nitrates of (99.9999% purity) are dissolved in deionized (DI) water to obtain a clear 0.01M solution. This solution is then p.assed through an ion (OH) " exchange column with Dowex 1X4 (50-100 mesh) resin at room temperature. The flow of the solution is controlled to maintain the pH of the collected solution at about 11.0. Since the resultant solution contains only a small quantity of yttrium it is preferable to increase the concentration of nitrates up to about 0.1M. A yttrium hydroxide sol collected at the bottom of the resin column is clear but becomes opalescent with .an increase in yttrium concentration, as well as upon storage. Sols prepared at lower yytrium concentrations remain stable for months. Sols of other metal (Gd, Tb and Ce) hydroxides were prepared similarly. The required metal solutions can also be prepared by mixing appropriate amounts of respective metal nitrates in luke warm DI water to obtain 0.05 to 0.1 M solutions. Stoichiometric quantities of metal (Y, Gd, Tb and Ce) solutions and trimethyl borate are added together so that the metal to borate ratio is maintained in the range of about 0.95 to 1.05. The metal^orate solution is transferred to a round bottom flask provided with a stirrer mantle and peptized at 80 to 100°C for 9 to 18 • hours. Gelation can be carried out with acid catalyzed sols (pH=l .0 to 2.0) or base catalyzed sols (pH=8.0 to 9.0). For low pH sols, pepitization requires a critical amount of certain acids to be introduced into the solution. Acid additions are generally specified in terms of acid type and pH. In the present invention, boric acid has been found to be an appropriate acid as it acts as an acid catalyzer and compensates for the loss of boron during calcination. After pepitization, sol/gels are left in a container until they thicken (3 to 5 days). The thickened gels are then dried in a lab oven at 60 to 70°C to form xerogels. These xerogels are transferred into a high grade alumina crucible and subjected to two heat cycles. In the first heat cycle, the sample is soaked for 2 hours at 300°C and then heated to 800 to 1000°C for 2 to 12 hours. After cooling to room temperature, the mass is crushed gently (e.g., in a mortar and pestal). The crushed powder is then washed with deionized water and dried at 100°C for 4 to 6 hours. Thermal analysis of phosphor samples containing various proportions of metal provides insight into the reaction kinetics. The thermal analysis data on one of these samples is presented in Fig. 1. The data reveals that the samples have undergone two to three successive weight changes in three different temperature regions. The first weight change occurs around 100°C and corresponds to the loss of free water molecules associated with the respective metal salt solutions. The second weight loss occurs around 200 to 300°C and is due to the loss of -CH 0 through oxidation. X-ray powder diffraction data on samples fired at 950°C are shown in Fig. 2. Samples fired at 800°C show some the lines corresponding to a yttrium, gadolinium borate phase. Since there is no stand.ard data on these new materials, XRD lines are compared with the data of starting materials as well as possible compositions, such as nitrates and oxides of respective metals. All the prominent lines corresponding to yttrium, gadolinium borate phase are observed in samples fired above 850 C. This indicates that the samples are completely converted to borate as no lines corresponding to any of the metal nitrates or oxides are observed. This conclusion is also supported by TGA data. The lines corresponding to metal borate phase become more prominent with increased firing temperatures. Since the luminescence of a phosphor depends on each of the shape, size, crystallinity, defects, grain boundaries, the morphology and PSD of samples prepared under various conditions were studied. Scanning electron micrographs of phosphor samples prepared under various conditions are shown in Fig. 3. From the micrographs one can observe that the phosphor particles are uniform and exhibit spherical shapes. The PSD of phosphors prepared at different temperatures are shown in Fig. 4. The samples are washed with water after calcination to eliminate very small particles (<0.05 microns) as well as organic residues and allowed to dry prior to determination of PSD. The emission characteristics of these phosphors are carried out on powders at room temperature. Fig. 5 represents the spectral distribution of radiation energy from different custom made 147 and 173 nm Xenon lamps provided with a MgF 2 windows and suitable band pass filters. The emission spectra of Tb and Ce doped yttrium, gadolinium borate phosphors prepared from metal nitrates and the emission spectrum of a commercially available Mn activated ZnSi0 are shown in Fig. 6. The spectral energy distribution of Tb emission strongly depends on Tb concentration. At lower concentrations of Tb, a weak emission in the blue region is observed which corresponds to 5 D 3 -> 7 F j . With increases in Tb concentration, the emission in blue region decreases. The emission spectra observed in samples activated at higher Tb concentrations can be divided into six groups corresponding to 5 D 4 - 7 F j transitions where J=6 to 1. With higher Tb concentrations, the cross relaxation mechanism produced rapid population of the 5 D state at the expense of 5 D 3 giving strong emission in the green region. The physical process of energy transfer between senstizer-S (Gd 3+ or Ce 3+ ) to activator-A (Tb 3+ ) in the present phsophor can be explained as follows: Exc Emission — -» S - Gd 3+ -» Gd 3+ -» A - For display applications, particularly televisions, it is preferable to have a single peak at 543 nm to obtain good color purity. By incorporating a blue absorption dye in a filter (used to eliminate unwanted colors, anti reflection, EMF, .anti static, etc.), the blue peak can be eliminated completely. For lamp applications, both the peaks are quite acceptable. A particularly suitable phosphor can contain from about 32 wt. % to about 45 wt. % yttrium, from about 9 wt. % to about 18 wt. % gadolinium, from about 4 wt. % to about 8 wt. % terbium, from about 0 wt. % to 5 wt. % cerium and about 6.6 wt. % to about 7 wt. % boron, with all weights percentages being based on the total weight of the phosphor. Further details of this invention will be described with reference in the following examples. EXAMPLE I The preparation of a terbium doped yttrium gadolinium borate phosphor employing the hydroxides of yttrium, gadolinium and terbium .and an acid catalyzer using a sol-gel process is described in this example. The following starting materials were used. The amounts of respective hydroxide solution (semi-gels) prepared from ion exchange column and borate solutions, in terms of both volume and percentage by weight per batch, are described in Table I. Table I Chemical Quantity (CC) Element (Gm) Mol. % Yttrium Hydroxide (0.01 M) 1640 ϊ~453 82 Gadolinium Hydroxide (0.01M) 200 0.314 10 Terbium Hydroxide (0.01 M) 160 0.237 8 Trimethyl Borate(0.08M) 200 Boric Acid (0.65M) 15 The above hydroxide solutions are mixed in a round bottom flask. The required quantity of trimethyl borate solution is added slowly to the hydroxide solution while stirring at 45°C. Boric acid is added drop wise after the solution attains the maximum required temperature (90 - 95°C) and the mixed solution peptized at that temperature for about 9 - 12 hours. A water condenser column is maintained at 20°C throughout the pepitization by use of a circulating chiller. After cooling the flask to room temperature, the solution (semi-gel) is transferred to a crystallizing dish (3L capacity) and left in an open atmosphere. After 5 to 6 days, the solution becomes a gel. These transparent hard gels are dried at 45 to 50°C for 12 hours in a lab oven. The dried product appears like soft glass, called xerogel. The loose mass from the glass dish is gently crushed with a glass mortar and pestle. A fine powder is collected into a crucible and fired at 300°C for 2 hours (rate of heating is 2°/min.) and then at 900°C for 6 hours, with the same rate of heating, in a box furnace. The sample is left in the furnace until it cools to room temperature. A hard mass is obtained after cooling. A small quantity of water pulps the hard mass into very fine particles. These fine phosphor powders are subjected to ultrasonic agitation in water. Ultrasonic treatment helps to break the clusters into very small particles. After washing with water, these powders are dried at 100°C for 6 hours. To recover sub-micron size particles (<0.1 micron) the phosphor solution is centriftiged. The weight percents of carbon, hydrogen and nitrogen were determined by CHN analysis and an elemental analysis was conducted using plasma emission spectroscopy. The compositional analysis of the above phosphor is shown in Table II. Table II Element % by wt. C 0.06 H 0.00 N 0.05 B2O3 23.00 Gd 2 0 3 11.30 Tb 2 0 3 9.04 Y 2 0 3 56.55 The emission characteristics of these phosphors and a commercially available phosphor for PDP applications, studied separately by exciting with 147 and 173nm excitation sources (Xe lamps), are shown in Table XL For purposes of comparison, the average particle sizes are also provided in the table. EXAMPLE II The preparation of terbium doped yttrium, gadolinium borate phosphor using a solution method in accordance with the present invention and employing yttrium nitrate, gadolinium nitrate, terbium nitrate and trimethyl borate in an acid catalyzer is described in this example. Starting materials used in the present example are listed in Table III. The amounts of starting materials in terms of both grams and percentage by weight per a batch, are shown in Table III. Table III Chemical Quantity (CC) Element (Gm) Mol. % Yttrium Nitrate (0.02M) 1450 2.564 82 Gadolinium Nitrate (0.02M) 176 0.554 10 Terbium Nitrate (0.02M) 140 0.418 8 Trimethyl Borate (0.08M) 350 Boric Acid (0.65M) 27 The above nitrate solutions were mixed in a round bottom flask. The required quantity of methyl borate solution is added slowly to the nitrate solution 1 1 while stirring at 45°C. The solution is peptized at 90°C for about 12 hours. The remaining preparative procedure is the same as mentioned in Example I. The CHN analysis of the above phosphor is shown in Table IV: Table IV Element % by wt. c 0.12 H 0.00 N 0.26 The emission characteristics of these phosphors and commercially available phosphors for PDP applications, studied separately by exciting with 147 and 173nm excitation sources (Xe lamps), are given in Table XL For the purposes of comparison, the average particle size of each sample is also provided in the table. EXAMPLE III The preparation of terbium and cerium doped yttrium, gadolinium borate phosphor using a solution method in accordance with the present invention, and employing yttrium nitrate, gadolinium nitrate, terbium nitrate, cerium nitrate and trimethyl borate in an acid catalyzer is described in this example. Starting materials used in the present example are listed in Table IV. The amounts, in terms of both grams and percentage by weight per a batch, are also shown in Table IV. Table IV Chemical Quantity (CC) Element (Gm) Mol. % Yttrium Nitrate (0.02M) 1415 2.501 80 Gadolinium Nitrate (0.02M) 123 0.388 7 Terbium Nitrate (0.02M) 140 0.418 8 Cerium Nitrate (0.02M) 88 0.232 5 Trimethyl Borate (0.08M) 350 12 Boric Acid (0.65M) 27 The above nitrate solutions were mixed in a round bottom flask. The required quantity of methyl borate solution is added slowly to the nitrate solution while stirring at 45°C. The solution is peptized at 90°C for about 12 hours. The remaining preparative procedure is the same as mentioned in Example I. The CHN analysis of the above phosphor is shown in Table IV: Table IV Element % by wt. c 0.03 H 0.00 N 0.02 The emission characteristics of these phosphors and commercially available phosphors for PDP applications, studied separately by exciting with 147 and 173nm excitation sources (Xe lamps), are provided in Table XL For the purpose of comparison, the average particle size of each sample is also noted in the table. EXAMPLE IV The preparation of terbium and cerium doped yttrium, gadolinium borate phosphor using a solid state reaction in accordance with the present invention, and employing yttrium oxide, gadolinium oxide, terbium oxide, cerium oxide and boric acid is described in this example. Starting materials used in the present example are listed in Table VII. The amounts, in terms of both grams and percentage by weight per batch, are also shown in Table VII. Table VII Chemical Quantity (Gm) Element (Gm) Mol. % Yttrium Oxide 7.000 JTl 85 13 Gadolinium Oxide 1.322 1.146 10 Terbium Nitrate 0.628 0.579 5 Boric Acid 3.00 — ~ The above oxides are mixed and ground with an alumina mortar and a pestle. The resultant mixture is fired at a high temperature. The remaining preparative procedure is the same as mentioned in Example I. The CHN analysis of the above phosphor is shown in Table VIII: Table VIII Element % by wt. C δ!θ3 H 0.00 N 0.01 The emission ch>aracteristics of these phosphors and commercially available phosphors for PDP applications, studied separately by exciting with 147 and 173nm excitation sources (Xe lamps), are given in Table IX. For comparison, average particle size for each sample is also noted in the table. Table IX Phosphor Relative Intensity Relative Persistence Color Coordinates Particle @ Excitation Integrated Area (10%) W/Filter W/O Filter Size 147 nm 173 nm W/O F W/F (ms) x y x y (μm) P Phhoosspphhoorr 11 7788 7 722 8 0.279 .707 .282 .633 0.1 - 2 Phosphor 2 100 100 130 111 8 0.279 .709 .282 .633 1.0 - 4 Phosphor 3 83 75 7 0.281 . 704 .292 .594 1.0 - 4 Phosphor 4 66 53 10 0.283 .699 .284 .630 2.0 - 6 Com. 1 21 38 100 100 140.226 .709 .258 .697 3.0 - 8 Phosphors 1 through. 4 are materials formed in accordance with the above Examples 1 through 4, respectively, and are representative of the present invention. Commercial 1 is the best commercially available Mn activated zinc silicate phosphor for plasma displays. Relative intensities are measured at maximum peak (borate at 543.5 nm and silicate at 530 nm). As the data of Table IX demonstrate, the phosphors of Example 1 through 4, formed by the sol/gel, sol/sol and solid state reaction processes of the present invention, provide various particle size ranges, while also generally providing a higher level of brightness, shorter persistence and longer life time. It should be understood that the foregoing description is only illustrative of the invention. Various alternatives and modifications can be devised by those skilled in the art without departing from the invention. Accordingly, the present invention is intended to embrace all such alternatives, modifications and variances that fall within the scope of the appended claims. 15

Claims: CLAIMS 1 A method of forming a phosphor having the empirical formula (Y 1 . x - y - z Gd x Tb y Ce z )B0 3 wherein: 0.0<x<0.2; 0.01<y<0.1; and 0 0<z<0 1; which method comprises thermally decomposing a xerogel at a temperature below a solid state reaction temperature to obtain said phosphor; wherein the xerogel has been formed by drying a gel obtained from a dilute acidic solution comprising a source of yttrium, a source of terbium, optionally a source of gadolinium and optionally a source of cerium and an organic precursor providing a source of boron. 2. A method according to claim 1, wherein said source of each of yttrium, terbium, gadolinium .and cerium is independently selected from their salts; and said organic precursor comprises boric acid. 3 A method according to claim 2, wherein each said salt is independently a nitrate or a hydroxide. 4 A method according to any one of the preceding claims, wherein said terbium activates said phosphor. 5 A method according to any one of the preceding claims, wherein said xerogel is thermally decomposed in an open atmosphere, at a temperature of from about 800 to 1000°C for from about 2 to 12 hours. 6 A method according to any one of the preceding claims, wherem said xerogel is crushed to form a powder prior to thermal decomposition 7 A method according to any one of the preceding claims, wherein said phosphor comprises particles having a particle size of from about 0 1 to about 2 0 microns 8 A method according to any one of the preceding claims, wherein said phosphor comprises from about 32 wt % to about 45 wt % yttrium, from about 9 wt % to about 18 wt % gadolinium, from about 4 wt. % to about 8 wt % terbium, from about 0 wt % to 5 wt. % cerium and from about 6 6 wt % to about 7 wt % boron 9 A phosphor obtainable by a process according to any one of the preceding claims 10 A phosphor having the empirical formula -16- (Y 1 . x - y - 2 Gd Tb y Ce z )B0 3 wherein 0 0<x<0 2, 0 01<y<0 1, and 0 0<z<0 1, formed by a process which comprises thermally decomposing a xerogel at a temperature below a solid state reaction temperature to obtain said phosphor, wherein the xerogel has been formed by drying a gel obtained from a dilute acidic solution compπsing a source of yttrium, a source of terbium, optionally a source of gadolinium and optionally a source of ceπum and an organic precursor providing a source of boron 11 A phosphor according to claim 10, wherein said source of each of yttrium, terbium, gadolinium and cerium is independently selected from their salts, and said organic precursor comprises boric acid 12 A phosphor according to claim 11, wherein each said salt is independently a nitrate or a hydroxide 13 A phosphor according to any one of claims 10 to 12, wherein said xerogel is thermally decomposed in an open atmosphere, at a temperature of from about 800 to 1000°C for from about 2 to 12 hours 14 A phosphor according to any one of claims 10 to 13, wherein said xerogel is crushed to form a powder prior to thermal decomposition 15 A phosphor according to any one of claims 10 to 14, wherein said phosphor comprises spherical particles having a particle size of from about 0 1 to about 2 0 microns 16 A phosphor according to any one of claims 10 to 15, comprising from about 32 wt % to about 45 wt % yttrium, from about 9 wt % to about 18 wt % gadolinium, from about 4 wt % to about 8 wt % terbium, from about 0 wt % to 5 wt % cerium and from about 6 6 wt % to about 7 wt % boron 17 A method of forming a phosphor having the empirical formula (Y 1 . x - y . z Gd Tb y Ce z )B0 3 wherein 0 0<x<0 2, 0 01<y<0 1, and 0 0 <z <0 1, which method comprises firing a mixed powder at a temperature equal to or greater than a solid state reaction temperature to obtain said phosphor, wherein the mixed powder has been formed by mixing a powdered source of each of yttrium and terbium and optionally -17- gadolinium and/or cerium and an organic precursor providing a source of boron; wherein said source of each of yttrium, terbium, gadolinium and cerium is independently selected from their salts and said organic precursor comprises boric acid and trimethyl borate. 18. A method according to claim 17, wherein each said salt is independently a nitrate, an oxide or a hydroxide. 19. Use of a phosphor according to any one of claims 9 to 16 in a flat panel display or in a lamp. 20. A television or a lamp comprising a phosphor according to any one of claims 9 to 16. -18-

Inventors: RAVILISETTY RAO PADMANABHA, RAVILISETTY, RAO, PADMANABHA
Applicants: MATSUSHITA ELECTRIC IND CO LTD, SENIOR ALAN MURRAY, MATSUSHITA ELECTRIC INDUSTRIAL CO., LTD., SENIOR, ALAN, MURRAY
Application year: 1999
Main classification: H01J29
IPC codes: C09K11, H01J1, H01J29, H01J61