IMPROVED MICROLENS UPON A PHOTODETECTOR

Abstract: An array of photosensitive devices may be formed with improved fill factors by including a diffractive microlens (14) which may have a stepped configuration. The microlens may be formed of a sol-gel material having a photoinitiator, or other materials that may be defined wiht low temperature techniques commonly used in connection with photoresist. In particular, a gray scale mask (24) may be used to define a plurality of steps (14a) in the resulting microlens (14) which have different diffractive characteristics.

Description: Improved Microlens And Photodetector Background This invention relates generally to microlenses and to photodetectors which may be used, for example, for digital imaging devices including cameras and scanners. Photodetectors are used to detect light in a digital imaging device. A large number of photodetectors may each detect a light intensity value for a given pixel. These light intensity values are digitized and used to form a digital depiction of a particular image. Such imaging devices are used in digital cameras, scanners and other devices. The imaging device may be formed, for example, using complementary metal oxide semiconductor (CMOS) technology. Imaging devices made using CMOS technology include active pixel sensors (APS) and passive pixel sensors (PPS). Alternatively, the imaging device may use charge coupled device (CCD) technology. All of these devices can be made of particularly small size. Imaging arrays of particularly small size may have a fill factor problem. The fill factor is the amount of light that falls on any given photodetector. Ideally, the amount of light that falls on each photodetector is designed to be as high as possible to improve the signal to noise ratio. In order to improve the fill factor with small photodetectors, a microlens may be situated over the photodetector. The microlens focuses all the light incident on a pixel onto the photodetector and therefore improves the fill factor of the photodetector. However, with conventional microlenses, formation of these relatively small microlenses with high precision and tolerance may be difficult. For example, the devices may require elaborate temperature or etching conditions which make their fabrication time consuming and expensive. In addition, the optical clarity of some microlenses adversely affects the incoming light. Therefore, it would be desirable to have a microlens with improved characteristics. Summary In accordance with one embodiment, a photodetector includes diffractive lens elements. A photosensitive device is arranged to receive the light through the lens elements. Description of the Drawings Figure 1 is an enlarged cross-sectional view taken vertically through a photodetector in accordance with one embodiment of the present invention; Figure 2 is a top plan view taken generally along the line 2-2 in Figure 1 ; Figure 3 shows the UV light exposure step used in one method of forming the device as shown in Figure 1 ; Figure 4 shows the result of the UV light exposure step illustrated in Figure 3; Figure 5 shows the structure that results from developing the structure shown in Figure 4; and Figure 6 is an enlarged cross-sectional view of a package for a integrated circuit package in accordance with one embodiment of the present invention. Detailed Description A photosensitive array 10 may include a plurality of photodetectors 12 which convert an input light signal into an analog signal carrying information about the intensity of the light incident on the photodetectors. The signals from a plurality of photodetectors can be digitized and combined to prepare a digital recreation of the exposed image. This digital representation may then be used in digital cameras and scanners and other imaging devices to reproduce a representation of the exposed scene. Centered on top of each photodetector 12 is a microlenses 14. Elements 14b and 14a of adjacent microlenses serve to diffract light so that more light falls on the exposed, underlying photodetector 12. A color filter array (CFA) 16 and a silicon oxide layer 18 may be formed between the photodetector 12 and the microlens 14. Metal vias 20 may extend upwardly beneath the microlens 14 through the silicon dioxide layer 18. Referring to Figure 2, the microlens 14 may be symmetrical and circular in shape viewed from above and may have an overall pyramidal configuration. The microlens may be formed of a plurality of steps 22 which create a stepped configuration when viewed from the side, as illustrated in Figure 1. While four steps are shown in the illustrated embodiment, the number of steps is subject to considerable variability and would depend on the design of a particular photosensitive array. The effect of the microlens 14 is to receive and diffract incident light, thereby collecting additional light which may be focused on the photodetector 12. This improves the effective fill-factor of the photodetectors 12 improving the light collection efficiency of the pixel and the array 10. One advantageous material for forming the microlens 14 is a sol-gel hybrid glass. Advantageous sol-gel hybrid glasses for use in the present invention may be formed using low temperature formation processes. Thus, the glasses may be shaped and formed using techniques comparable to those utilized in connection with forming photoresists. That is, UV light may be used to expose a portion of the sol-gel material and to develop that material so that the remaining portion may be removed. Also, the sol-gel may exhibit advantageous transmissivities compared to conventional materials used to form microlenses. Sol-gel glasses may be formed, for example, by hydrolysis of tetraethylorthosilicate (TEOS) and/or tetramethylorthosilicate (TMOS). After hydrolysis, these materials may be subjected to oxolation or oxygen bridge formation and polycondensation. The result is a silicon oxide complex which is solvent swollen to form a polymerized network. If a photoinitiator is included in the complex, the material may be shaped using conventional photoresist patterning techniques. In accordance with one embodiment, a sol-gel hybrid glass can be prepared by hydrolysis polycondensation of the mefhacrylate group substituted silane in the presence of water. The gel synthesis happens, allowing the methylacryloxypropyl trimethoxysilane or glysidoxypropyltrimethylsilane precursor material to react with diluted acid or base water solution, for example, in a molar ratio of 1 :2 respectively for several hours. Before spin coating, propriety amounts of 1-hydroxycyclohexyl phenyl ketone may be added as a photoinitiator to initiate polymerization of unsaturated glass hybrid polymer. The gel may be filtered by an 0.1 millimeter filter to remove aggregated polymer particles and to form a film with good surface quality. Films may then be then deposited on top of previously fabricated color filter polymer used to form the CFA or on other substrates and pre-baked at 60°C for 15 minutes. The resulting film thickness is adjustable by varying spinning speed and use of solvents such as methanol, ethanol or xylene. The spin coated films may be cured by a mercury UV lamp or other light source through an opening in a photomask, for example, for 1 to 30 minutes to form patterns, as shown in Figure 3. In particular, a UV mask 24 may be situated over the hybrid sol-gel 26 located over the CFA 16 to create a graded exposure pattern in the sol-gel 26 as indicated by lines 30 in Figure 4. The patterned structures 28 may be obtained by developing the sol-gel 26 in isopropanol to remove unexposed parts of the sol-gel to form the steps 32, as shown in Figure 5. After this removal step, the film may be postbaked at 100° to 200°C for 10 to 60 minutes to harden the film. The sol-gel 26 may be formed of a plurality of discrete layers having distinct optical properties. Each layer or combination of layers may form a different step 22, as indicated in Figure 5. If particular material properties are necessary, titanium, silicon or zirconium, or the prehydrolysed alkoksides of these materials can be added to the solution of the methacrylate group substituted silanes. For example, titanium(IV)-propoxide and zirconium(IV)- propoxide may be used. Methacrylic acid may be used to prevent zirconium propoxide precipitation. To produce the microlens shape shown in Figure 2, a gray scale mask may be used. See Suleski, T. J.and Oshea, D.C.I 995, "Gray Scale Mask For Diffractive Optics Fabrication," Appl. Optics 34 ,7507. A conventional mask material, which may be quartz or glass, is coated conventionally with chromium. In this way the sol-gel may be deposited and patterned at a temperature of less than 200°C. This avoids adversely affecting the CFA. The same sol-gel material may also be patterned at low temperatures using a photoinitiator to form anti-reflective coatings, coloration, selective reflectors, electrochromism and photochromism selective absorption. For example, a window 34 may be formed in the package 36 of an integrated circuit imaging device 38, as shown in Figure 6. This window may be coated with a sol-gel material to form an anti-reflective coating 40. The material may be formed in more than one layer, each layer having different optical properties. For example, different layers may be effective for different light wavelengths. Alternatively, reflectivity may be changed by creating graded porosity in the sol-gel. The graded porosity may be achieved by depositing the sol-gel and then etching the sol-gel using known techniques. Alternatively, an optically clear, stable positive photoresist may be used to form the microlens and photodetector, using low temperature processing conventionally used with photoresists in semiconductor manufacturing processes. For example, MFR-324 made by JSR Microelectronics, Inc., Sunnyvale, California, may be used to form the microlens. While the present invention has been described with respect to a limited number of embodiments, those skilled the art will appreciate numerous modifications and variations therefrom. It is intended that the appended claims cover all such modifications and variations which fall within the true spirit and scope of the present invention. What is claimed is:

Claims: 1. A photodetector comprising: diffractive lens element; and a photosensitive device arranged to receive light through said lens element. 2. The photodetector of claim 1 wherein said element is symmetrical and centered on the photosensitive device. 3. The photodetector of claim 1 wherein said elements have a stepped configuration. 4. The photodetector of claim 3 wherein said elements are formed of a sol-gel. 5. The photodetector of claim 4 wherein said sol- gel includes a photoinitiator. 6. The photodetector of claim 1 wherein said element is formed of a clear photoresist. 7. A method of forming a microlens comprising: depositing a sol-gel; exposing the sol-gel to light; developing the sol-gel; and removing portions of said sol-gel so as to define a stepped structure. 8. The method of claim 7 wherein said depositing step includes depositing said sol-gel on a color filter material. 9. A photodetector comprising: a photosensitive device; and a microlens arranged over said photosensitive device, said microlens formed of a sol-gel material including a photoinitiator. 10. The photodetector of claim 9 wherein said microlens has a stepped configuration. 11. The photodetector of claim 9 including an anti-reflective coating formed of said sol-gel material. 12. The photodetector of claim 9 including a color filter, said microlens being formed over said color filter. 13. A microlens comprising: a first portion having a first edge; a second portion having a second edge, said first and second edges being offset from one another; and said first and second portions being formed of a light transmissive, light diffracting material. 14. The microlens of claim 13 wherein said material is a sol-gel. 15. The microlens of claim 14 wherein said sol-gel includes a photoinitiator. 16. The microlens of claim 13 having a circular shape. 17. The microlens of claim 16 formed on a color filter. 18. The microlens of claim 13 having a stepped configuration. 19. The microlens of claim 13 formed of photoresist. 20. The microlens of claim 19 formed of clear, positive photoresist.

Inventors: ASSADI AZAR, RAJ KANNAN, ASSADI, AZAR, RAJ, KANNAN
Applicants: ASSADI AZAR, INTEL CORP, RAJ KANNAN, ASSADI, AZAR, INTEL CORPORATION, RAJ, KANNAN
Application year: 1999
Main classification: H01L31
IPC codes: G02B3, G02B5, G03F7, H01L27, H01L31, H04N1, H04N5