Steel cord for reinforcement of a radial tyre and a radial tyre employing the same

Abstract: A steel cord for reinforcement of a radial tyre and a radial tyre employing the same are disclosed. The steel cord is made of three or more steel filaments of which one or two filaments are regularly twisted, the other filaments are open-twisted and each filament is twisted in same direction. Each steel filament using carbon steel has the carbon content of 0.7 to 0.96 wt%, the tensile strength of the filament is in the range of 260 to 380 kgf/mm 2 , the twisting pitch is 10 to 20 mm, and each filament is plated with brass. The topping characteristic is improved and the uniformity of tyre is enhanced.

Description: The present invention relates to a steel cord for use in the reinforcement of rubber products such as pneumatic radial tyres, particularly to a steel cord made of three steel filaments of which one filament is regularly twisted, two filaments are open-twisted and each filament is twisted in the same direction, which improves the topping processability of rubber and enhances the uniformity of the tyres. The present invention also relates to a radial tyre employing the same steel cord. In general, in steel cords with a so-called 1x3, 1x4 or 1x5 construction, for example, steel cords with a so-called 1x3 construction, each steel filament has the same diameter and is open-twisted. In Fig. 3 - Fig. 4, conventional steel cords such as an open-twisted cord 101 and a regular-twisted cord 102 are shown. In Fig. 5, the conventional filaments 100a, 100b, 100c for open-twisting are shown in an untwisted condition. These steel filaments are open-twisted in order to enhance the rubber penetration into the steel cord in comparison to a regular or close-twisted cord. Further the open-twisted cord is used after being rolled once more so that the cord has an oval section (Roll Forming), or at least one of the three filaments is rolled on or through a polygonal roll before being twisted (Pre-Forming). The open-twisted cord or the oval sectioned cord improves the rubber penetration into the cord when rubber topping. However, the low load elongation (LLE) of the open-twisted or oval sectioned cord which has its untwisted filaments having high shape maintenance property is far higher in comparison to a regular or close cord which has its untwisted filaments having low shape maintenance property. For example, in the low load range of 0.3-1.6kgf, the elongation of the regular twisted cord is usually less than 0.08% and that of the open-twisted or oval sectioned is about 0.3%. As a result, in the open-twisted or the oval sectioned cord, a special treatment in adjusting a cord pay off tension for maintaining the open-cord shape is needed during the rubber topping procedure, and the space due to the open-twisting is reduced by causing a little more tension. Further, in the event of manufacturing a rubber sheet using the open-twisted cord, the diameter of the cord and the thickness of the topping sheet increase or vary and finally the weight of the tyre increases. To solve the above described problem, conventionally, one or two of three filaments were pre-formed by a polygonal roll before being twisted to a steel cord. This made it possible to increase the pay off tension of steel cords during the rubber topping procedure which facilitated the rubber topping procedure. However, in this case, a stress concentration was induced at the angled points by the angled filaments formed during pre-forming and so the durability of the tyre was reduced. In order to prevent a belt separation, EP-A-0392366 discloses a steel cord comprising three steel filaments all having different diameters from one another, the small-diameter and medium-diameter ones of said three filaments having internal stresses adapted to be released when the cord is cut at both ends thereof, so that owing to said stresses the diameters of the cord before and after cut at both ends thereof will satisfy the formulas and after the cord has been cut at both ends thereof, said medium-diameter filament will retract from the ends of the large-diameter filament and said small-diameter filament will retract from the ends of said medium-diameter filament, whereby the cord ends are formed of only said large-diameter filament. It could provide a steel cord preventing belt edge separation, however, it could not improve the flatness of rubber topping sheet to enhance maneuvering stability and fuel efficiency of a car. It is therefore the object of the present invention to provide a steel cord for the reinforcement of a radial tyre to resolve the above problems having improved topping characteristics and enhancing the uniformity of tyre. Furthermore, it is another object of the present invention to provide a radial tyre employing the above steel cord. These objects of the present invention are achieved through use of a steel cord made of three steel filaments of which one filament is regularly twisted, the other filaments are open-twisted, and each filament is twisted in the same direction. As a result, the topping processability of rubber is improved and the uniformity of the tyre is enhanced. According to the present invention there is provided a steel cord for reinforcement of a radial tyre, wherein the steel cord is made of three steel filaments, and characterised in that two filaments have 90 - 120% of shape maintenance property respectively within 5% difference and are open-twisted, one filament has 70 - 90% of shape maintenance property and is regularly twisted, each filament is twisted in the same direction, the diameter of each of said two open-twisted filaments is d1 and that of the regularly twisted filament is d2, and wherein d1 is 0.25 to 0.35mm and d2 is 0.75d1 -1.25d1. The invention also includes a radial tyre comprising a plurality of steel cords, a rubber sheet covering said steel cords, wherein each steel cord is made of three steel filaments, and characterised in that one filament is regularly twisted, the other filaments are open-twisted, each filament is twisted in the same direction, the diameter of each of said two open-twisted filaments is d1 and that of the regularly twisted filament is d2, and wherein d1 is 0.25 to 0.35mm and d2 is 0.75d1 - 1.25d1. The foregoing objects, features and advantages of the present invention are set out in the following detailed description thereof in conjunction with the accompanying drawings in which: Fig. 1 is a perspective view of a steel cord according to the present invention, Fig. 2 is an elevation view of each filament untwisted according to the present invention, Fig. 3 is a conventional open-twisted cord corresponding to Fig.1, Fig. 4 is a conventional close or regular-twisted cord corresponding to Fig. 1, Fig. 5 comprises conventional filaments corresponding to Fig. 2. In Fig. 1, a steel cord 1 is illustrated which is twisted in three filaments 1a, 1b, 1c according to the present invention. P1, P2 and P3 are the wave heights of the filaments 1a, 1b and 1c respectively in twisted state. The steel cord 1 consists of three steel filaments of which one filament 1c is regularly twisted, the other filaments 1a, 1b are open-twisted, and each filament is twisted in the same direction. Fig. 2 shows the three filaments 1a, 1b and 1c untwisted. The wave heights of the filaments 1a, 1b and 1c are directed as H1, H2 and H3 respectively in the untwisted state. The factor K=H/P(%) is defined as a shape maintenance property of a filament. That is, the shape maintenance property of each filament 1a, 1b and 1c is K1=H1/P1 x 100, K2=H2/P2 x 100 and K3=H3/P3 x 100 respectively. The two filaments 1a,1b have 90 120% of high shape maintenance property respectively, wherein the difference of the shape maintenance property is less than 5%. The other filament 1c has 70 - 90% of low shape maintenance property. The shape maintenance properties of three filaments above-mentioned are summarized as follows. K1 = K2 = 90 - 120%, |K1 - K2| < 5%, K3 = 70 - 90%, K3 < K1, or K2. The open-twisted filaments 1a, 1b having high shape maintenance property provide rubber coating with a space to permeate therebetween, while the regularly twisted filament 1c having low shape maintenance property makes it possible to raise the pay off tension of cords during the rubber topping procedure which facilitates the rubber topping procedure. That is, it is possible in this filament twisting system to raise the pay off tension of cords during the rubber topping procedure without reducing the rubber penetration space. In detail, during the rubber topping procedures, if a pay off tension is imposed on a steel cord, the tension is mainly charged on the regularly twisted filament 1c having low shape maintenance property. This means that the open-twisted filaments 1a, 1b having high shape maintenance property maintain their shape during the pay off tension, then the space for the rubber coating to penetrate is almost not reduced. Thus, according to the construction of the present invention, the working time is reduced due to raising the pay off tension and the rubber topping on the steel cord is easily accomplished. The carbon content of a steel filament using carbon steel is 0.7 to 0.96 wt%, and the tensile strength level of the filament is in the range of 260 to 380 kgf/mm 2 before twisting. Each steel filament has all the same twisting pitch of 10 to 20mm. The diameter of the open-twisted filaments is d1 and that of the regularly twisted filament is d2, wherein d2 is 0.75d1 - 1.25d1. For example, d1 is 0.25 to 0.35mm then d2 is 0.19 to 0.44mm. The steel filaments are preferably plated with brass. This increases the adhesion force between the steel cords and the rubber. Also the steel cord of present invention has small elongation in the low load range than the conventional open steel cord because the constitutional elongation which contributes largely to low load elongation of present invention steel cord is much lower than that of open steel cord due to the regularly twisted filament 1c having low shape maintenance property and thus makes it possible to produce rubber topping sheet which has better flatness and dimensional stability. As a result of that the uniformity of tyres improved. Thus, the penetration of rubber topping into the steel cord is improved due to the open-twisted filaments. Further, it is possible to raise the pay off tension of the steel cords during the rubber topping procedure. Then the rubber topping speed may be elevated, and the uniformity of the tyre is greatly improved.

Claims: A steel cord for reinforcement of a radial tyre, wherein the steel cord is made of three steel filaments (1a, 1b, 1c) and characterised in that two filaments (1a, 1b) have 90 - 120% of shape maintenance property respectively within 5% difference and are open-twisted, one filament (1c) has 70 - 90% of shape maintenance property and is regularly twisted, each filament is twisted in the same direction, the diameter of each of said two open-twisted filaments (1a, 1 b) is d1 and that of the regularly twisted filament is d2, and wherein d1 is 0.25 to 0.35mm and d2 is 0.75d1 - 1.25d1. A steel cord according to claim 1, wherein each steel filament using carbon steel has a carbon content of 0.7 to 0.96 wt%, the tensile strength of said filament before twisting is in the range of 260 to 380 kgf/mm 2 , the twisting pitch is 10 to 20 mm, and each filament is plated with brass. A radial tyre comprising a plurality of steel cords, a rubber sheet covering said steel cords, wherein each steel cord is made of three steel filaments (1a, 1b, 1c) and characterised in that one filament (1c) is regularly twisted, the other filaments (1a, 1b) are open-twisted, each filament is twisted in the same direction, the diameter of each of said two open-twisted filaments (1a, 1b) is d1 and that of the regularly twisted filament (1c) is d2, and wherein d1 is 0.25 to 0.35mm and d2 is 0.75d1 - 1.25d1. A radial tyre according to claim 3, wherein each steel filament using carbon steel has a carbon content of 0.7 to 0.96 wt%, the tensile strength of said filament before twisting is in the range of 260 to 380 kgf/mm 2 , the twisting pitch is 10 to 20 mm, and each filament is plated with brass.

Inventors: HAN YONG SIK, HAN, YONG SIK
Applicants: HANKOOK TIRE CO LTD, HANKOOK TIRE CO., LTD.
Application year: 1999
Main classification: B60C9
IPC codes: B60C9, D07B1