Metallic cord and pneumatic tyre

Abstract: A steel cord characterised by a zigzag filament which is zigzagged two dimensionally or in a plane by a zigzag pitch length (Pw) and a zigzag wave height (h) and made up of straight segments each extending between zigzag peak points, each of the zigzag pitch lengths (Pw) and zigzag wave heights (h) being ccnstant along the longitudinal direction thereof and either a second zigzag filament of the same type but having a different pitch length (Pw) or a straight filament such that the cord has an open construction so that rubber can penetrate it. The cord may be a single bunch or a twisting together of two or more bunches each comprising zigzag filaments. The cord may have zigzag filaments of at least two different zigzag pitch lengths. In each of tnese constructions the result is to give an open cord construction and the invention also includes a tyre incorporating such cord in the carcass breaker or the like.

Description: The present invention relates to a metallic cord for reinforcing rubber articles such as pneumatic tyres in which penetration of rubber into the cord is improved. Many rubber articles such as pneumatic tyres and the like are generally reinforced with steel cords. As shown in Fig. 15, a conventional steel cord is formed by compactly twisting straight steel filaments together. This type of steel cords however has a defect in that closed spaces not filled with rubber are formed among the filaments and thus the steel filaments are liable to rust and so the adhesion between the cords and rubber in which the cord is embedded becomes insufficient. As a result, the cord strength greatly decreases and the cord is broken finally. Recently, in order to improve the penetration of rubber into cords to solve the above-mentioned problems, there have been proposed a steel cord (b) in which straight filaments (f) are loosely twisted as shown in Fig. 16, and a steel cord (c) in which spiral filaments (fl) and straight filaments (f2) are twisted together as shown in Fig. 17. Such cords however, necessitate a relatively large cord diameter in order to secure stable rubber penetration. Further, such cords tend to show a large initial elongation. As a result, it is difficult to use the cords for applications such as to reinforce the carcass or beads of a pneumatic tyres. A steel cord according to the preamble of claim 1 is disclosed in document US 5, 135, 039. It is therefore, an object of the present invention to provide a steel cord in which the rubber penetration is improved without increasing the cord diameter and initial elongation. According to on aspect of the present invention a steel cord according to claim 1 is provided. The steel cord may comprise a single bunch of filaments but more preferably it comprises a plurality of bunches each including zigzag filaments twisted together and the bunches of plurality are also twisted together to form the cord. In one preferred arrangement a steel cord comprises a steel cord which is a plurality of bunches of zigzag filaments twisted together at a twisting pitch (Pc), each of said bunch being formed by zigzag filaments twisted together at a twisting pitch (Pf), said zigzag filaments including at least two kinds of zigzag filaments having different zigzag pitch lengths (Pw), the zigzag pitch length (Pw) and zigzag wave height (h) of each said zigzag filament being constant along the longitudinal direction thereof, each said bunch made up of at least two kinds of zigzag filaments, the number of the filaments in each bunch being 2 or 3, the total number of the filaments being 8 to 10, said zigzag filaments having a diameter (d) of 0.30 to 0.45 mm, the twisting pitch (Pc) being 10 to 40 mm, the twisting pitch (Pf) being 3 to 20 times the twisting pitch (Pc), the zigzag pitch length (Pw) being 5.0 to 30.0 times the diameter (d), the zigzag wave height (h) being 0.2 to 3.0 times the diameter (d), the product of the diameter (d) and height (h) being in 0.014 to 0.028 times the pitch length (Pw) The steel cord may be a plurality of bunches of filaments and a non-zigzag filament twisted together at a twisting pitch (Pc), each said bunch being formed by twisting one zigzag filament and one or two non-zigzag filaments together at a twisting pitch (Pf), all the zigzag filaments being substantially the same zigzag pitch length (Pw) and the same zigzag wave height (h), the number n of all the filaments being 5 or 6, the number of zigzag filaments being at least 2 but at most (n-3), all the filaments having a diameter (d) of 0.25 to 0.45 mm, the twist pitch Pc being 10 to 25 mm, the twist pitch (Pf) being 3 to 20 times the twist pitch (Pc), the zigzag pitch length (Pw) being 5.0 to 30.0 times the diameter (d), the zigzag wave height (h) being 0.2 to 3.0 times the diameter (d), the product of the diameter (d) and height (h) being in 0.014 to 0.028 times the pitch length (Pw). Yet another aspect provides a steel cord comprising zigzag filaments twisted together at a twisting pitch (Pc), said zigzag filaments including at least two kinds of zigzag filaments having different zigzag pitch lengths (Pw), the zigzag pitch length (Pw) and zigzag wave height (h) of each said zigzag filament being constant along the longitudinal direction thereof, the filaments being twisted together by changing their relative positions so that a central core is not formed by a specific filament and the lengths of all the filaments are substantially equal to each other, the number of all the filaments being 8 to 12, all the filaments having the same diameter (d) of 0.15 to 0.30 mm, the twist pitch (Pc) being 10 to 25 mm, the zigzag pitch length (Pw) being 10.0 to 35.0 times the diameter (d), the zigzag wave height (h) being 0.5 to 4.0 times the diameter (d), in each filament, the quotient (h/Pw) of the zigzag pitch length (Pw) and zigzag wave height (h) being 0.75 to 1.25 times h1/Pw1, wherein Pw1 is the minimum zigzag pitch and h1 is the zigzag wave height of the filament having said minimum zigzag pitch. Still another arrangement provides a steel cord comprising a filament bunch and a wrapping wire, said filament bunch being formed by twisting together zigzag filaments, said zigzag filaments including at least two kinds of zigzag filaments having different zigzag pitch lengths (Pw), the zigzag pitch length (Pw) and zigzag wave height (h) of each said zigzag filament being constant along the longitudinal direction thereof, the filaments being twisted together by changing their relative positions so that a central core is not formed by a specific filament and the lengths of all the filaments are substantially equal to each other, the number of all the filaments being 9, all the filaments having a diameter (d) of 0.17 to 0.25 mm, the twist pitch (Pc) being 10 to 20 mm, the zigzag pitch length (Pw) being 10.0 to 35.0 times the diameter (d), the zigzag wave height (h) being 0.5 to 4.0 times the diameter (d), in each filament, the quotient (h/Pw) of the zigzag pitch length (Pw) and zigzag wave height (h) being 0.75 to 1.25 times h1/Pw1, wherein Pw1 is the minimum zigzag pitch and h1 is the zigzag wave height of the filament having said minimum zigzag pitch, said wrapping wire having a diameter of 0.13 to 0.17 mm, and wound around the filament bunch at a pitch of 3.0 to 7.0 mm in the reverse direction to the direction of twisting the filaments. Finally the invention also includes a pneumatic tyre characterised by a reinforcing layer embedded in rubber, the reinforcing layer being made of steel cords as above. According to the present invention, a steel cord is formed by compactly twisting steel filaments together, the steel filaments including a plurality of zigzag filaments and optionally a non-zigzag filament, the zigzag filament being zigzagged two-dimensionally and made up of straight segments each extending between the zigzag peak points, the non-zigzag filament being straight. In case the cord is composed of only the zigzag filaments, the zigzag filaments include at least two kinds of zigzag filaments having different zigzag pitch lengths. In case the cord is composed of both the zigzag filaments and non-zigzag filaments, some of the zigzag and non-zigzag filaments are first loosely twisted together into a bunch, and then a plurality of bunches are twisted together into the cord. In any case, the zigzag pitch length and zigzag wave height of each zigzag filament are substantially constant along the length thereof. Another aspect of the invention provides a tyre comprising a reinforcing layer such as a tread reinforcing belt layer, carcass, bead reinforcing layer or the like comprising the above-mentioned steel cords. Embodiments of the present invention will now be described in detail in conjunction with the accompanying drawings. Fig. 1(A) and Fig. 1(B) show zigzag filaments having different zigzag pitch lengths; Fig. 2 is a schematic view for explaining a method of making a cord (Embodiment 1) according to the present invention; Fig. 3(A) to Fig. 5(B) are cross sectional views each showing a combination of the number of filaments and the number of filament bunches in Embodiment 1; Fig. 6(A) and Fig. 6(B) are cross sectional views each showing a cord (Embodiment 1) according to the present invention; Fig. 7 is a graph showing cord strength reduction and rubber penetration as a function of dXh/Pw value; Fig. 8 is a schematic view for explaining a method of making a cord (Embodiment 2) according to the present invention; Fig. 9(A) to Fig. 10(D) are cross sectional views each showing a cord (Embodiment 2) according to the present invention; Fig. 11(A) and Fig. 11(B) are cross sectional views each showing a cord (Embodiment 3) according to the present invention; Fig. 12 is a cross sectional view showing a cord (Embodiment 4) according to the present invention; Fig. 13 is a cross sectional view showing a tyre according to the present invention; Fig. 14 is a diagram for explaining a coincidence of the zigzag phases of zigzag filaments; Fig. 15 is a cross sectional view of a conventional compact cord; Fig. 16 is a cross sectional view of a conventional open cord; and Fig. 17 is a cross sectional view of a known cord comprising spiral filaments. In the drawings, steel cords 1 according to the present invention are each formed by compactly twisting steel filaments 2 together. The steel filaments 2 include a plurality of zigzag filaments 2A and optionally a non-zigzag filament 2B. The zigzag filament 2A is, before twisting into the cord, zigzagged two-dimensionally, i.e. in a plane. It is made up of straight segments 3 each extending between zigzag peak points U and D (peak U, dip D) as shown in Fig. 1(A) and Fig. 1(B). The distance between the zigzag peak points (D and D) or (U and U) measured in the longitudinal direction of the filament defines a zigzag pitch length Pw. The distance between the adjacent peak points U and D measured normally to the longitudinal direction of the filament defines a zigzag wave height h. On the other hand, the non-zigzag filament 2B is straight before the cord is twisted. Preferably, the steel filaments 2 are made of a high carbon steel including 0.65 to 0.88 wt% of carbon. The steel filaments are plated with a metal or coated with resin to improve corrosion resistance and adhesion to rubber. If the carbon content is less than 0.65 wt%, the strength of the filament becomes insufficient. If the carbon content is more than 0.88 wt%, the strength of the filament is greatly decreased when bent into the zigzag form. When the finished cord 1 is composed of only zigzag filaments 2A, the zigzag filaments 2A should include at least two kinds of zigzag filaments 2A1-2An having different zigzag pitch lengths Pw in order to avoid coincidence of the zigzag phases as shown in Fig. 14 which lowers the rubber penetration. When the cord 1 is composed of both zigzag filaments 2A and non-zigzag filaments 2B, some of the zigzag and non-zigzag filaments are first loosely twisted together into a bunch, and then a plurality of such bunches are twisted together (last-twist or final twist) into the cord, whereby concentration of a cord load on the non-zigzag filaments 2B is mitigated. Furthermore spaces are formed between the filaments between the bunches and to avoid the coincidence of the zigzag phases, which further improve the rubber penetration. During last-twisting, it is preferable to twist every bunch itself. (hereinafter, bunch-twist) In any case, the zigzag pitch lengths Pw and zigzag wave height h of each zigzag filament 2A are substantially constant along the length thereof. If a zigzag filament has a variable zigzag pitch and a variable zigzag wave height, the strength of the cord has a tendency to decrease. * Cord Embodiment 1 This embodiment is designed for a belt reinforcing a tread portion of a pneumatic radial tyre, which can be suitably used as a substitute for a conventional steel cord of a 3+9+15 construction widely used in heavy duty radial tyres for trucks, buses and the like. The cord 1 in this embodiment is composed of 8 to 10 zigzag filaments 2A having a diameter d of from 0.30 to 0.45 mm. The zigzag filaments 2A include at least two kinds of zigzag filaments 2A1-2An having different zigzag pitch lengths Pw1-Pwn. As shown in Fig. 2, the cord 1 is formed by twisting bunches 4 of filaments 2A together at a twist pitch Pc of 10 to 40 mm (last twist). Each bunch 4 is formed by twisting together two or three zigzag filaments 2A including at least two kinds of zigzag filaments 2A1 and 2An at a twist pitch Pf of 3 to 20 times the pitch Pc of the last twist. In each zigzag filament 2A, the filament diameter d, zigzag pitch lengths Pw and zigzag wave height h are set to satisfy the following conditions: Pw is 5.0 to 30.0 times d; h is 0.2 to 3.0 times d; and d X h/Pw is 0.014 to 0.028 preferably 0.020 to 0.025. Figs.3(A) to Fig. 5(B) show preferable combinations of the number of bunches 4 and the number of filaments 2A. In Fig. 3(A), the cord is composed of four bunches 4A of one zigzag filament 2A1 and one zigzag filament 2An. In Fig. 3(B), the cord is composed of two bunches 4B of one zigzag filament 2A1 and two zigzag filaments 2An and one bunch 4A of one zigzag filament 2A1 and one zigzag filament 2An. In Fig. 4(A), the cord is composed of one bunch 4B of one zigzag filament 2A1 and two zigzag filaments 2An and three bunches 4A of one zigzag filament 2A1 and one zigzag filament 2An. In Fig. 4(B), the cord is composed of three bunches 4B of one zigzag filament 2A1 and two zigzag filaments 2An. In Fig. 5(A), the cord is composed of five bunches 4A of one zigzag filament 2A1 and one zigzag filament 2An. In Fig. 5(B), the cord is composed of two bunches 4B of one zigzag filament 2A1 and two zigzag filaments 2An and two bunches 4A of one zigzag filament 2A1 and one zigzag filament 2An. Further, Fig. 6(A) shows a cross sectional view of a cord composed of six zigzag filament 2A1 and three zigzag filaments 2An. Fig. 6(B) shows a cross sectional view of a cord composed of five zigzag filament 2A1 and three zigzag filaments 2An. In the above-mentioned examples shown in Fig. 3(A) to Fig. 5(B), type (B) is more preferable than the type (A) because two or more bunches 4B of three filaments are included therein. In the illustrated examples, the direction of twisting the filaments is the same as the direction of twisting the bunches. However, it is also possible to twist in the reverse direction. Further, all the filaments 2A are the same diameter d, but, they may have two or more different diameters. With respect to the zigzag pitch length Pw and zigzag wave height h, the zigzag filament 2An is larger than the zigzag filaments 2A1. If the diameter d is less than 0.30 mm, it becomes difficult to obtain the rigidity required for a belt layer of heavy duty tyres, the zigzag shape is apt to return to a straight shape during twisting, and the rubber penetration decreases. If the diameter d is more than 0.45 mm, the strength of the filament tends to decrease when shaped into a zigzag, and the suppleness required during making tyres is lost. If the twist pitch Pf is less than 3 times the last twist pitch Pc, the spaces formed between the filaments becomes narrow and the rubber penetration decreases. If the twist pitch Pf is more than 20 times the last twist pitch Pc, the zigzag phases are liable to coincide with each other and the rubber penetration decreases. It is not necessary for improving the rubber penetration to shorten the twist pitch, and a relatively long pitch of 10 to 40 mm can be employed. Thus, the production efficiency of the cord can be improved. If the zigzag pitch length Pw is less than 5.0 times the diameter d, the strength of the filament tends to decrease when shaped into a zigzag. If more than 30 times, the rubber penetration decreases. If the zigzag wave height h is less than 0.2 times the diameter d, it becomes difficult to increase the rubber penetration. If more than 3.0 times, the strength of the filament tends to decrease when shaped into a zigzag. Fig. 7 shows the cord strength reduction (%) and rubber penetration (%) as a function of the dXh/Pw value. As can be seen therefrom, by setting dXh/Pw in the range of 0.014 to 0.028 more preferably 0.020 to 0.025, both the rubber penetration and cord strength are improved. * Comparison tests Various experimental steel cords were made, and test tyres having a belt layer made of the experimental cords were also made, and the following comparison tests were conducted. The results of the tests are shown in Table 1. * Cord strength reduction In this test, a reduction (%) in the strength of an object cord (Ex.) from a conventional compact cord (Ref.) was obtained, wherein the object cord and the compact cord were the same with respect to the material, number of filaments and last-twist pitch, but the compact cord is composed of non-zigzag filaments only. * Bending rigidity The bending rigidity of each cord was measured with a TABER "V-5 Rigidity Tester" (USA). * Rubber penetration The cord was taken out of the tyre together with the surrounding topping rubber, and the topping rubber was carefully removed from the surface of the cord. Then, two adjacent filaments were taken out 10 cm long using a knife, and the length of a part surrounded by the two removed filaments and the remaining filaments into which the rubber completely penetrated was measured to obtain the percentage of this length to the total length of 10 cm as a rubber penetration. * Rust and Reserved strength The tyre was disassembled after running about 200,000 km, and the steel cords were checked for rust. The results are indicated by an index based on the conventional cord being 100. The smaller the index, the smaller the rusting. Further, the steel cords were taken out and the cord strength was measured. The results are indicated as percentages to the original strength. All the cords had a twist pitch Pf of 10 times the last twist pitch Pc. The direction of twisting filaments into a bunch was the same as the last twist. Ref.A1, A14, A15, A16 A17 were conventional cords composed of compactly twisted straight filaments. Ref.A3 was composed of only spiral filaments. Ref.A4 was composed of one kind of zigzag filaments twisted together without forming any bunch. * Cord Embodiment 2 This embodiment is again designed for a belt reinforcing a tread portion of a pneumatic radial tyre, which can be suitably used as a substitute for a conventional steel cord of a 3+6 or 2+7 construction widely used in heavy duty radial tyres for trucks, buses and the like. The cord in this embodiment is composed of a number (n) of steel filaments 2 having a diameter d of 0.25 to 0.45 mm, wherein the number n is 5 or 6. The steel filaments 2 include at least two but at most (n-3) of zigzag filaments 2A and the remaining two or three non-zigzag filaments 2B. All the zigzag filaments 2A have substantially the same zigzag pitch length Pw and same zigzag wave height h. Further, in the illustrated examples, all the steel filaments are the same diameter d. When a steel filament having a relatively large diameter such as this embodiment is shaped into a zigzag, the strength of the filament tends to decrease. Thus, in this embodiment, in order to provide a strong cord, some of the zigzag filaments comprise straight filaments. This provides openness and the necessary strength. The cord 1 is formed as shown in Figure 8 by twisting together a plurality of bunches of filaments or a non-zigzag filament 2B and a plurality of bunches of filaments. In either case, each bunch 4 is formed by twisting together one zigzag filament 2A and one or two non-zigzag filaments 2B at a twisting pitch Pf of 3 to 20 times the last-twisting pitch Pc. The last-twisting pitch Pc is in the range of from 10 to 25 mm. The direction of twisting the filaments into a bunch is the same as the last-twisting direction, but it may be reversed. In this embodiment, also the diameter d, zigzag pitch lengths Pw and zigzag wave height h in each zigzag filament 2A satisfy the following conditions: Pw is 5.0 to 30.0 times d, preferably 10.0 to 25.0 times d; h is 0.2 to 3.0 times d, preferably 0.5 to 2.0 times d; and dXh/Pw is 0.014 to 0.028, preferably 0.020 to 0.025. Fig. 9(A) shows a cord formed by last-twisting one non-zigzag filament 2B and two bunches 4C of one zigzag filament 2A and one non-zigzag filament 2B. Fig. 9(B) shows a cord formed by last twisting one bunch 4C of one zigzag filament 2A and one non-zigzag filament 2B and one bunch 4D of one zigzag filament 2A and two non-zigzag filaments 2B. Fig. 10(A) shows a cord formed by last twisting three bunches 4C. Fig. 10(B) shows a cord formed by last twisting two bunches 4D. Fig. 10(C) shows a cord formed by last twisting two bunches 4C and two non-zigzag filaments 2B. Fig. 10(D) shows a cord formed by last twisting one bunch 4C, one bunch 4D and one non-zigzag filament 2B. In each of the example cords, all the filaments are the same diameter, but may have two or more different diameters. If the diameter d is less than 0.25 mm, it becomes difficult to obtain the rigidity required for a belt layer of the heavy duty tyres, and the zigzag shape is apt to return to a straight shape during twisting, and the rubber penetration decreases. If the diameter d is more than 0.45 mm, the strength of the filament tends to decrease when shaped into a zigzag, and a suppleness required during making tyres is lost. If the twist pitch Pf is less than 3 times the last twist pitch Pc, the spaces formed between the filaments become narrow and the rubber penetration decreases. If the twist pitch Pf is more than 20 times the last twist pitch Pc, the zigzag phases are liable to coincide with each other and the rubber penetration decreases. It is not necessary for improving the rubber penetration to shorten the twist pitch, and a relatively long pitch of 10 to 25 mm can be employed. Thus, the production efficiency of the cord can be improved. If the zigzag pitch length Pw is less than 5.0 times the diameter d, the strength of the filament tends to decrease when shaped into a zigzag. If more than 30 times, the rubber penetration decreases. If the zigzag wave height h is less than 0.2 times the diameter d, it becomes difficult to increase the rubber penetration. If more than 3.0 times, the strength of the filament tends to decrease when shaped into a zigzag. * Comparison tests Various experimental steel cords were made, and test tyres having a belt layer made of the experimental cords were also made, and the following comparison tests were conducted. The results of the tests are shown in Table 2. * Cord strength reduction test Same as above * Bending rigidity test Same as above * Rubber penetration test Same as above * Rust and Reserved strength test Same as above Ex.B1 to Ex.B9 had a cord structure shown in Fig. 9(A). Ex.B14 to 17 had a cord construction shown in Fig. 10(B). The direction of twisting filaments into a bunch was the same as the last twist. (S direction) The twist pitch Pf was 10 times the last twist pitch Pc. Ref.B1, B10, B11, B14, B15 and B16 were conventional compact cords composed of straight filaments. Ref.B3 was an open cord composed of loosely twisted non-zigzag filaments. Ref.B6 had two kinds of zigzag filaments. * Cord Embodiment 3 This embodiment is designed as a carcass cord for reinforcing the carcass of a pneumatic radial tyre, which can be suitably used as a substitute for a conventional steel cord of a 3+9 or 3+9+15 construction widely used in heavy duty radial tyres for trucks, buses and the like. The cord 1 in this embodiment is composed of 8 to 12 zigzag filaments 2A. All the filaments are the same diameter d of 0.15 to 0.30 mm. The zigzag filaments 2A include at least two kinds of zigzag filaments 2A1-2An having different zigzag pitch lengths Pw1-Pwn. The number (n) of the kinds is preferably two. The number of zigzag filaments in each kind is at least two, preferably at least three. The cord 1 is formed by twisting all the zigzag filaments 2A together at a twist pitch of 10 to 25 mm (last twist). During twisting the zigzag filaments 2A, the relative positions thereof are changed repeatedly along the length so that a central filament (core filament) is not formed by a specific filament, and all the zigzag filaments 2A are substantially same length when measured along the zigzag of each filament. More specifically, the "changing of the relative positions" means that any one of the filaments may be positioned in the centre of the cord in a place but in another place positioned on the outside. For example, two of the filaments are interlaced at predetermined intervals along the cord length, wherein the two interlaced filaments are changed or replaced in a predetermined regular or irregular order. As the zigzag filaments 2A are interlaced, a problem of loosening of the filaments can be solved. If there is a large difference in the filament lengths, some filaments tends to break out during rubberising the cords. In each zigzag filament 2A, the filament diameter d, zigzag pitch lengths Pw and zigzag wave height h are set to satisfy the following conditions: Pw is 10.0 to 35.0 times, preferably 15.0 to 30.0 times d; and h is 0.5 to 4.0 times, preferably 1.0 to 3.0 times d. Further, a zigzag filament 2A1 having a minimum zigzag pitch Pw1 and the remaining zigzag filament 2An having a larger zigzag pitch Pwn satisfy the following condition: hn/Pwn is 0.75 to 1.25 times h1/Pw1, wherein: h1 is the zigzag wave height of the zigzag filament 2A1; and hn is the zigzag wave height of the zigzag filament 2An. However, if there are plural zigzag filaments having the same minimum zigzag pitch lengths Pw1 but different heights, the minimum height is used as h1. Fig. 11(A) shows a cord composed of six zigzag filaments 2A1 having a small zigzag pitch Pw1 and three zigzag filaments 2An having a larger zigzag pitch Pwn, which are twisted together by changing the relative positions. Fig. 11(B) shows a cord composed of five zigzag filaments 2A1 having a small zigzag pitch Pw1 and three zigzag filaments 2An having a larger zigzag pitch Pwn, which are twisted together by changing the relative positions. If the diameter d is less than 0.15 mm, the zigzag shape is apt to return to a straight shape during twisting, and the rubber penetration decreases. If the diameter d is more than 0.30 mm, it is difficult to provide the suppleness required in a tyre carcass, and the fatigue resistance of the cord is lowered. If the twist pitch is less than 10 mm, the initial elongation of the cord is too large for the carcass of a pneumatic tyre, and thus it becomes difficult to keep a stable tyre shape. If the twist pitch is more than 25 mm, the filaments are liable to loosen at cut ends, and thus tyre durability is liable to decrease. If the zigzag pitch length Pw is less than 10.0 times the diameter d, the strength of the filament tends to decrease when shaped into a zigzag. If more than 35.0 times, the rubber penetration decreases. If the zigzag wave height h is less than 0.5 times the diameter d, it becomes difficult to increase the rubber penetration. If more than 4.0 times, the strength of the filament tends to decrease when shaped into a zigzag. If hn/Pwn is less than 0.75 times h1/Pw1 or more than 1.25 times h1/Pw1, it becomes difficult to equalise the filament lengths, and thus the cord load is liable to concentrate on a particular filament, and as a result the cord strength is liable to decrease. * Comparison tests Various experimental steel cords were made, and test tyres having a carcass made of the experimental cords were also made, and the following comparison tests were conducted. The results of the tests are shown in Table 3. * Cord strength reduction test Same as above * Bending rigidity test Same as above * Rubber penetration test Same as above * Rust and Reserved strength test Same as above * Filament breaking-out During rubberising a carcass ply for a heavy duty tyre, the cords were investigated if the filaments broke out from the cord. * Cord-cut-end looseness In this test, the degree of looseness at cut ends of the cord was evaluated. Ref.C1, C14, C15, C16 and C17 were conventional compact cords composed of straight filaments twisted together without changing the relative positions. Ref.C2 and C4 were composed of one kind of zigzag filaments. * Cord Embodiment 4 This embodiment is designed as a cord of a bead reinforcing layer for reinforcing bead portions of a pneumatic radial tyre, which can be suitably used as a substitute for a conventional steel cord of a 3+9 or 3+9+15 construction widely used in heavy duty radial tyres for trucks, buses and the like. The cord in this embodiment is composed of nine zigzag filaments 2A having the same diameter d of 0.17 to 0.25 mm. The zigzag filaments 2A include at least two kinds of zigzag filaments 2A1-2An having different zigzag pitch lengths Pw1-Pwn. The number (n) of the kinds is preferably two. The number of zigzag filaments in each kind is at least two, preferably at least three. In each zigzag filament 2A, the filament diameter d, zigzag pitch lengths Pw and zigzag wave height h are set to satisfy the following conditions: Pw is 10.0 to 35.0 times d; and h is 0.5 to 4.0 times d. Further, a zigzag filament 2A1 having a minimum zigzag pitch Pw1 and the remaining zigzag filament 2An having a larger zigzag pitch Pwn satisfy the following condition: hn/Pwn is 0.75 to 1.25 times h1/Pw1, wherein h1 is the zigzag wave height of the zigzag filament 2A1, and hn is the zigzag wave height of the zigzag filament 2An. However, if there are zigzag filaments having the same minimum zigzag pitch lengths Pw1 but different heights, the minimum height is used as h1. The cord is formed by twisting all the zigzag filaments 2A together at a twist pitch of 10 to 20 mm (last twist). As explained in the formed Embodiment 3, during twisting the zigzag filaments 2A, the relative positions thereof are changed so that a central filament or core is not formed by a specific filament, and all the zigzag filaments 2A are the substantially same length when measured along the zigzag of each filament. In this embodiment, further, a wrapping wire is wound around the resultant bunch 4 of the twisted filaments 2A. Preferably, the wrapping wire 5 is a single filament made of a high carbon steel including 0.65 to 0.88 wt% of carbon. The diameter of the wrapping wire is 0.13 to 0.17 mm. The winding direction is reverse to the twisting direction, and the winding pitch is 3.0 to 7.0 mm. If the winding pitch is less than 3.0 mm, the production efficiency is greatly decreased. If the winding pitch is more than 7 mm and/or the diameter of the wrapping wire is less than 0.13 mm, the cord-shape-retaining function decreases to decrease the dimensional accuracy of a rubber reinforcing layer. If the diameter of the wrapping wire is more than 0.17 mm, as the cord diameter and weight increase, it is not preferable. If the carbon content of the steel wire 5 is lower than 0.65 wt%, the strength tends to decrease. If the carbon content is higher than 0.88 wt%, the wire becomes too hard and the bending strength decreases. Fig. 12 shows a cord composed of six zigzag filaments 2A1 having a small zigzag pitch Pw1 and three zigzag filaments 2An having a larger zigzag pitch Pwn. If the filament diameter d is less than 0.17 mm, it becomes difficult to obtain the rigidity required for a bead reinforcing layer of the heavy duty tyres, and as a result, tyre durability decreases. Further, the zigzag shape is apt to return to a straight shape during twisting, and the rubber penetration decreases. If the diameter d is more than 0.25 mm, it is difficult to provide a bead reinforcing layer with the suppleness required during applying to the bead portion. If the twist pitch is less than 10 mm, the initial elongation of the cord is too large for the bead reinforcing layer of a pneumatic tyre, and thus the reinforcing effect becomes insufficient. If the twist pitch is more than 20 mm, the filaments are liable to loosen at cut ends, and thus tyre durability is liable to decrease. If the zigzag wave height h is less than 0.5 times the diameter d, it becomes difficult to increase the rubber penetration. If more than 4.0 times, the strength of the filament tends to decrease when shaped into a zigzag. If the zigzag pitch length Pw is less than 10.0 times the diameter d, the strength of the filament tends to decrease when shaped into a zigzag. If more than 35.0 times, the rubber penetration decreases. If hn/Pwn is less than 0.75 times h1/Pw1 or more than 1.25 times h1/Pw1, it becomes difficult to equalise the filament lengths, and thus the cord load is liable to concentrate on a particular filament, and as a result the cord strength is liable to decrease. * Comparison tests Various experimental steel cords were made, and test tyres having a bead reinforcing layer of the experimental cords were also made, and the following comparison tests were conducted. The results of the tests are shown in Table 4. * Cord strength reduction test Same as above * Bending rigidity test Same as above * Rubber penetration test Same as above * Rust and Reserved strength test Same as above * Filament breaking-out Same as above * Cord-cut-end looseness Same as above * Shape retention test A length of cord of 1,000 mm long was coiled into a loop of 200 mm diameter. The loop was collapsed gradually in fifteen seconds as follows: the loop was put on a horizontal plane; and one of two oppositely opposed points was fixed. The other point then was pressed towards the fixed point so that the two points contacted each other. The collapsed state was maintained for ten seconds. Then, the pressing force was decreased gradually in fifteen seconds to allow the loop to return to its original shape. The distance L between the two points was measured to obtain the shape retention rate E =(L/200)X100. The shape retention rate E of each cord was divided by that of Ex.D1 and converted into the reciprocal number and further multiplied by 100. The larger the value, the better the shape retention. * Cord pull-out resistance test From the tyre, a specimen of the bead cord reinforcing layer was cut out, and a force required to pull a cord 15 mm out of the specimen was measured. Ref.D1 and D3 were conventional compact cords composed of non-zigzag filaments. Ref.D2 had a layered structure having a specific core filament. Ref.D4 was formed by twisting one kind of zigzag filaments and non-zigzag filaments together. Ref.D5 was formed by twisting one kind of zigzag filaments together. In the cord pull-out resistance test, the filaments of every Example cord were broken without some of them coming out, which shows that the adhesion to the rubber was excellent. In the cord-cut-end looseness test, Ex.D5 and D9 caused slight looseness by which no problem would be causes with tyre making processes. * Tyre Embodiment Next, a pneumatic tyre according to the present invention is described according to Fig. 13. In Fig.13, a pneumatic tyre T is a radial tyre for heavy duty vehicles such as trucks, buses and the like. The tyre T comprises a tread portion 12, a pair of axially spaced bead portions 13 with a bead core 15 therein, a pair of sidewall portions 13 extending between the tread edges and the bead portions 14, a carcass C extending between the bead portions 14, and a belt 17 disposed radially outside the carcass C in the tread portion 12. The carcass C comprises at least one ply of radially arranged cords extending between the bead portions through the tread portion and the sidewall portions, and turned up around the bead cores 15 to form two turned up portion and one main portion therebetween. For the carcass cords, the above-mentioned Embodiment 3 is used. Between the turned up portion and main portion in each bead portion 14 is provided with a rubber bead apex 16. The belt 17 comprises at least two plies of parallel cords, wherein the cords of one ply cross the cords of the other ply. For the belt cords, the above-mentioned Embodiment 1 or 2 is used. Each bead portion 14 is provided with a bead reinforcing layer G. The layer G is composed of a single ply of parallel cords. For the bead reinforcing cords, the above-mentioned Embodiment 4 is used. In Fig.13, the layer G extends along the axially outside of the carcass ply turned up portion.

Claims: A steel cord comprising a zigzag filament which is zigzagged two dimensionally or in a plane by a zigzag pitch length (Pw) and a zigzag wave height (h) and made up of straight segments each extending between zigzag peak points, each of the zigzag pitch lengths (Pw) and zigzag wave heights (h) being constant along the longitudinal direction thereof characterised by a second zigzag filament of the same type but having a different pitch length (Pw) such that the cord has an open construction so that rubber can penetrate it. A steel cord according to claim 1, comprising a plurality of bunches of zigzag filaments twisted together at a twisting pitch (Pc), each of said bunch being formed by zigzag filaments twisted together at a twisting pitch (Pf), said zigzag filaments including at least two kinds of zigzag filaments having different zigzag pitch lengths (Pw), the zigzag pitch length (Pw) and zigzag wave height (h) of each said zigzag filament being constant along the longitudinal direction thereof, each said bunch made up of at least two kinds of zigzag filaments, the number of the filaments in each bunch being 2 or 3, the total number of the filaments being 8 to 10, said zigzag filaments having a diameter (d) of 0.30 to 0.45 mm, the twisting pitch (Pc) being 10 to 40 mm, the twisting pitch (Pf) being 3 to 20 times the twisting pitch (Pc), the zigzag pitch length (Pw) being 5.0 to 30.0 times the diameter (d), the zigzag wave height (h) being 0.2 to 3.0 times the diameter (d), the product of the diameter (d) and height (h) being in 0.014 to 0.028 times the pitch length (Pw) The steel cord according to claim 2, characterised by two bunches of three zigzag filaments. A steel cord according to claim 1, characterised by zigzag filaments twisted together at a twisting pitch (Pc), said zigzag filaments including at least two kinds of zigzag filaments having different zigzag pitch lengths (Pw), the zigzag pitch length (Pw) and zigzag wave height (h) of each said zigzag filament being constant along the longitudinal direction thereof, the filaments being twisted together by changing their relative positions so that a central core is not formed by a specific filament and the lengths of all the filaments are substantially equal to each other, the number of all the filaments being 8 to 12, all the filaments having the same diameter (d) of 0.15 to 0.30 mm, the twist pitch (Pc) being 10 to 25 mm, the zigzag pitch length (Pw) being 10.0 to 35.0 times the diameter (d), the zigzag wave height (h) being 0.5 to 4.0 times the diameter (d), in each filament, the quotient (h/Pw) of the zigzag pitch length (Pw) and zigzag wave height (h) being 0.75 to 1.25 times h1/Pw1, wherein Pw1 is the minimum zigzag pitch and h1 is the zigzag wave height of the filament having said minimum zigzag pitch. A steel cord according to claim 1, comprising a filament bunch and a wrapping wire, said filament bunch being formed by twisting together zigzag filaments, said zigzag filaments including at least two kinds of zigzag filaments having different zigzag pitch lengths (Pw), the zigzag pitch length (Pw) and zigzag wave height (h) of each said zigzag filament being constant along the longitudinal direction thereof, the filaments being twisted together by changing their relative positions so that a central core is not formed by a specific filament and the lengths of all the filaments are substantially equal to each other, the number of all the filaments being 9, all the filaments having a diameter (d) of 0.17 to 0.25 mm, the twist pitch (Pc) being 10 to 20 mm, the zigzag pitch length (Pw) being 10.0 to 35.0 times the diameter (d), the zigzag wave height (h) being 0.5 to 4.0 times the diameter (d), in each filament, the quotient (h/Pw) of the zigzag pitch length (Pw) and zigzag wave height (h) being 0.75 to 1.25 times h1/Pw1, wherein Pw1 is the minimum zigzag pitch and h1 is the zigzag wave height of the filament having said minimum zigzag pitch, said wrapping wire having a diameter of 0.13 to 0.17 mm, and wound around the filament bunch at a pitch of 3.0 to 7.0 mm in the reverse direction to the direction of twisting the filaments. A pneumatic tyre characterised by a reinforcing layer embedded in rubber, the reinforcing layer made of steel cords according to any one of claims 1 to 5. A heavy duty tyre characterised by a belt layer made of the steel cords according to claim 1, 2 or 3. A heavy duty tyre characterised by a carcass made of the steel cords according to claim 4. A heavy duty tyre characterised by a bead reinforcing layer made of the steel cords according to claim 5.

Inventors: MIYAZAKI SHINICHI, SAKAI YASUO, YAMAZAKI, MIYAZAKI, SHINICHI, SAKAI, YASUO, YAMAZAKI,
Applicants: SUMITOMO ELECTRIC INDUSTRIES, SUMITOMO RUBBER IND, SUMITOMO ELECTRIC INDUSTRIES, LTD., SUMITOMO RUBBER INDUSTRIES LTD.
Application year: 1999
Main classification: B60C9
IPC codes: B60C15, B60C9, D07B1