ELASTIC FILMS MADE FROM ALPHA-OLEFIN/VINYL AROMATIC AND/OR ALIPHATIC OR CYLCOALIPHATIC VINYL OR VINYLIDENE INTERPOLYMERS

Abstract: The present invention pertains to elastic films having at least one layer comprising; (A) at least one substantially random interpolymer, which comprises; (1) polymer units derived from; (i) at least one vinyl aromatic monomer, or (ii) at least one aliphatic or cycloaliphatic vinyl or vinylidene monomer, or (iii) a combination of at least one aromatic vinyl monomer and at least one aliphatic or cycloaliphatic vinyl or vinylidene monomer, and (2) polymer units derived from ethylene or at least one C3-20 alpha -olefin, or combination thereof; and optionally (3) polymer units derived from one or more ethylenically unsaturated polymerizable monomers other than those of (1) and (2); or (B) a blend of Component A with at least one polymer other than that of Component A; and wherein said elastic film has a recovery in the cross direction of greater than or equal to 80 percent and has a recovery in the machine direction of greater than or equal to 60 percent. The present invention also pertains to a multilayer film comprising at least two layers wherein at least one of said layers has a recovery in the cross direction of greater than or equal to 80 percent and has a recovery in the machine direction of greater than or equal to 60 percent and comprises a polymer composition which comprises; (A) at least one substantially random interpolymer, which comprise; (1) polymer units derived from; (i) at least one vinyl aromatic monomer, or (ii) at least one aliphatic or cycloaliphatic vinyl or vinylidene monomer, or (iii) a combination of at least one aromatic vinyl monomer and at least one aliphatic or cycloaliphatic vinyl or vinylidene monomer, and (2) polymer units derived from ethylene or at least one C3-20 alpha -olefin, or combinations thereof; and optionally, (3) polymer units derived from one or more ethylenically unsaturated polymerizable monomers other than those of (1) and (2); or (B) at least one polymer other than that of Component A.

Description: ELASTIC FILMS MADE FROM ALPHA-OLEFIN/VINYL AROMATIC AND/OR ALIPHATIC OR CYCLOALIPHATIC VINYL OR VINYLIDENE INTERPOLYMERS This invention pertains to elastic films prepared from polymers which comprise at least one substantially random interpolymer comprising polymer units derived from ethylene or one or more α-olefin monomers, or combinations thereof with specific amounts of one or more vinyl aromatic monomers or aliphatic or cycloaliphatic vinyl or vinylidene monomers, or combinations thereof, or blend compositions therefrom with other polymers. Films prepared from such interpolymers exhibit a unique balance of properties including, good elasticity as measured by high strain recovery (> 80 percent Recovery in the cross direction (CD) and > 60 percent Recovery in the machine direction (MD). The invention covers films, sheets, and multi-layer laminates. The films according to the invention may be obtained also as co-extruded and multi-layer films, such as one side sealable films, two sides sealable films, coated films, tinted films, cavitated films, untreated films, one side treated films, two sides treated films, and metallized plastic films. The inventive films can also be laminated to polyester films, styrenic polymer films, polyethylene films, non-woven fabrics, fibers, foams, and conventional oriented polypropylene films, and others to impart elastic properties to such multilayer composite structures. Materials with excellent stretchability and elasticity are needed to manufacture a variety of disposable and durable articles, such as tapes, bandages, incontinence garments, disposable diapers, disposable and protective clothing and fabrics. Stretchability and elasticity are desirable characteristics to effectuate a closely conforming fit to the body of the wearer or to the frame of the item. It is also desirable to maintain the conforming fit during repeated use, extensions and retractions. For incontinence articles, stretchability and elasticity are particularly desirable to insure comfort and provide security against unwanted leaks. Elastic films may also be of value for food wraps, meat wraps and household wraps where recovery- is of value. Disposable articles are typically prepared by the combination of polymer fibers, films, sheets and absorbent materials. Whereas the fibers are prepared by well known processes such as spunbonding, melt blown and continuous filament wounding, the film and sheet forming processes typically involve known extrusion and coextrusion processes, for example, blown bubble extrusion, extrusion casting, profile extrusion, injection molding, extrusion coating and extrusion sheet. The resultant elastic film, coating or sheet may be subsequently cut or slit to short lengths or narrow widths to prepare strips, tapes, bands, ribbons or the like. There are at least two ways elastic films are employed to manufacture disposable and durable articles. Elastic films, strips and sheets are used as uncombined elastic components (panels or portions), or they are constructed as or into multilayer structures to provide elastic composite materials with enhanced elasticity and stretchability. In a diaper, for example, experimental and commercial uses include in or as side panels, waist bands, backsheets, leg bands, and even topsheets where the elastic material is rendered pervious or "breathable" by such methods as apperturing, slitting, or microperforating as suggested by Lippert et al. in USP 4,861,652. An example of the use of elastic films to construct elastic composite materials is provided by Van Gompel et al. in USP 4,940,464, USP 4,938,757 and USP 4,938,753. Van Gompel et at. disclose disposable incontinence garments containing elastic gathering means and stretchable side panels. The gathering means and stretchable side panels are made from film of block or graft copolymers such as butadiene, isoprene, styrene, ethylene-methyl acrylate, ethylene-vinyl acetate, ethylene-ethyl acrylate or blends thereof. An example of use of elastic films to construct composites with the particular benefit of enhanced stretchability is a stretchable fastening tape for a disposable diaper disclosed by Gesp in USP 5,057,097. There has been a persistent need for extrudable materials suitable for producing films, strips, sheets and composites with excellent stretchability and elasticity. Although there are a variety of elastic films currently available, these known solutions require blending or additive incorporation to meet desire levels of extrusion processability, stretchability or elasticity. Still other proposed solutions such as the method disclosed by Butin in USP 3,849,241, require "controlled thermal and oxidative degradation" of the elastic material to affect viscosity adjustments prior to extrusion. Moreover, prior art elastic films can involve elastomers such as styrene butadiene copolymers, polyether block amides, polyether esters and polyurethanes which typically necessitate blending with polyolefins for adequate extrusion processability. Where polyolefins themselves have been previously employed as elastic films, other problems have arisen. For example, ethylene/α,β-unsaturated copolymers are known to possess improved elasticity as a function of increased comonomer levels. Daponte in USP 4,803,117, discloses ethylene vinyl ester copolymers where high vinyl ester levels are requisite to effectuate adequate elasticity for disposable articles. However, these high vinyl ester levels invariably render the polymer susceptible to undue thermal degradation. In the modern distribution and marketing of food products, a multitude of different packaging materials are used. One principal category of food packaging materials is plastic film. Many different kinds of plastic film exist, both in composition and structure, and some are tailored to specific applications while others are more generic in nature. Currently, polyvinyl chloride (PVC) film is the predominate plastic film used to wrap retail-cut red meat and similar products, for example fresh fish, poultry, vegetables, fruits, etc., due to its many desirable properties and its low cost relative to other plastic films. Representative of these desirable properties are clarity, oxygen transmission, flexibility, toughness, heat sealability, elastic recovery, and processability. However, most PVC films include a plasticizer to obtain the desired flexibility, and a growing concern exists as to the carcinogenic properties of the most commonly used PVC film plasticizer and the tendency of this plasticizer to migrate from the film to the food product. A growing concern also exists regarding the use in food wrapping applications of any plastic film comprising one or more chlorinated polymers. The concern includes the tendency for chlorinated polymers to yield corrosive acid when thermally degraded or incinerated, as well as concern regarding the general difficulty involved in recycling chlorinated polymers. In the search for alternatives to PVC film, various monolayer olefin films, particularly polyethylene films, have been considered but none have been found to be without at least one major flaw that has blocked its utility. High density polyethylene (HDPE) is much too inelastic to be useful as a commercial wrap, while the various low density polyethylenes, for example low density polyethylene (LDPE), linear low density polyethylene (LLDPE), ultra low density polyethylene (ULDPE), etc., do not possess sufficient elastic recovery, and the film retains impressions or dents caused by handling of the packaged goods by potential purchasers while inspecting its contents. Various multilayer films have also been considered (for example those taught in USP 5,112,674 and in EPO 0 243 965, EPO 0 333 508, and EPO 0 404 969), and significant among these are films made by co-extrusion of polyethylene with an ethylene/α,β-ethylenically unsaturated carbonyl copolymer, such as ethylene vinyl acetate (EVA) or ethylene acrylic acid (EAA). These ethylene/α,β-ethylenically unsaturated carbonyl copolymers are considered difficult to fabricate, have a tendency to impart an offensive taste or odor to the food product, and are known to interfere with anti-fogging agents. Obijeski et al., in US Patent No. 5,472,775 disclose elastic films, particularly films, strips, coatings, ribbons and sheets made from at least one substantially linear ethylene polymer are disclosed which can be fabricated on conventional polyolefin extrusion equipment. They can be used to produce elastic composite structures that are stretchable and have recycle compatibility between elastic and non-elastic components. Chum et al., in US Patent No. 5,427,807 disclose food packaging comprising a film having at least one film layer comprising a substantially linear ethylene polymer, preferably a polymer comprising ethylene and at least one α-olefin comonomer, for example 1-octene. The film structures can be either mono- or multi-layered, oriented or non-oriented, oxygen permeable or impermeable, filled with certain inorganic fillers, and prepared by any conventional technique. Bradfute et al., in U.S. Patent No. 5,658,625 disclose film and sheet materials, and articles made therefrom, such as bags, pouches, trays, etc., comprising one or more layers of a thermoplastic, homogeneous alpha-olefin/vinyl aromatic copolymer, preferably an ethylene/styrene copolymer but does not indicate the optimum amounts of ethylene/vinyl and α-olefin monomers in the ethylene/vinyl aromatic interpolymer blend component. Thus there remains a requirement for elastic film which, as well as exhibiting the required degree of elasticity, also; a) exhibits an excellent balance in other mechanical properties such as tensile strength and elongation as well as softness and flexibility indicated by low modulus values; b) has good processability without the requirement of blending or additive incorporation such as processing aids; c) is not susceptible to undue thermal degradation; d) does not require a plasticizer to improve softness; e) does not contain corrosive chloride residues; f) does not impart an offensive taste or odor to foodstuffs; and; g) does not interfere with known antifogging agents. We have now found that elastic films can be prepared having the desired elasticity, processability and mechanical properties, if such films comprise at least one substantially random interpolymer and if the amount of the vinyl aromatic or aliphatic or cycloaliphatic vinyl or vinylidene monomer or a combination thereof, incorporated into the substantially random interpolymer is within a specific range which results in said elastic film having a recovery in the cross direction of greater than or equal to 80 percent and a recovery in the machine direction of greater than or equal to 60 percent. The present invention pertains to elastic films having at least one layer comprising; (A) at least one substantially random interpolymer, which comprises; (1) polymer units derived from; (i) at least one vinyl aromatic monomer, or (ii) at least one aliphatic or cycloaliphatic vinyl or vinylidene monomer, or (iii) a combination of at least one aromatic vinyl monomer and at least one aliphatic or cycloaliphatic vinyl or vinylidene monomer, and (2) polymer units derived from ethylene or at least one C 3 . 20 α-olefin, or combination thereof; and optionally (3) polymer units derived from one or more ethylenically unsaturated polymerizable monomers other than those of (1) and (2); or (B) a blend of Component A with at least one polymer other than that of Component A; and wherein said elastic film has a recovery in the cross direction of greater than or equal to 80 percent and has a recovery in the machine direction of greater than or equal to 60 percent. The present invention also pertains to a multilayer film comprising at least two layers wherein at least one of said layers has a recovery in the cross direction of greater than or equal to 80 percent and has a recovery in the machine direction of greater than or equal to 60 percent and comprises a polymer composition which comprises; (A) at least one substantially random interpolymer, which comprises; (1) polymer units derived from; (i) at least one vinyl aromatic monomer, or (ii) at least one aliphatic or cycloaliphatic vinyl or vinylidene monomer, or (iii) a combination of at least one aromatic vinyl monomer and at least one aliphatic or cycloaliphatic vinyl or vinylidene monomer, and (2) polymer units derived from ethylene or at least one C 3.20 α-olefin, or combination thereof; and optionally, (3) polymer units derived from one or more ethylenically unsaturated polymerizable monomers other than those of (1) and (2); or (B) at least one polymer other than that of Component A. The elastic films can be used in applications including, but not limited to, dispoasable diapers, fabrics, medical bandages, tapes, food wrap films, household wraps, stretch packaging films, labels, bands . Definitions All references herein to elements or metals belonging to a certain Group refer to the Periodic Table of the Elements published and copyrighted by CRC Press, Inc., 1989. Also any reference to the Group or Groups shall be to the Group or Groups as reflected in this Periodic Table of the Elements using the IUPAC system for numbering groups. Any numerical values recited herein include all values from the lower value to the upper value in increments of one unit provided that there is a separation of at least 2 units between any lower value and any higher value. As an example, if it is stated that the amount of a component or a value of a process variable such as, for example, temperature, pressure, time is, for example, from 1 to 90, preferably from 20 to 80, more preferably from 30 to 70, it is intended that values such as 15 to 85, 22 to 68, 43 to 51, 30 to 32 etc. are expressly enumerated in this specification. For values which are less than one, one unit is considered to be 0.0001, 0.001, 0.01 or 0.1 as appropriate. These are only examples of what is specifically intended and all possible combinations of numerical values between the lowest value and the highest value enumerated are to be considered to be expressly stated in this application in a similar manner. The term "hydrocarbyl" as employed herein means any aliphatic, cycloaliphatic, aromatic, aryl substituted aliphatic, aryl substituted cycloaliphatic, aliphatic substituted aromatic, or aliphatic substituted cycloaliphatic groups. The term "hydrocarbyloxy" means a hydrocarbyl group having an oxygen linkage between it and the carbon atom to which it is attached. The term "interpolymer" is used herein to indicate a polymer wherein at least two different monomers are polymerized to make the interpolymer. This includes copolymers, terpolymers, etc. As used herein, the phrase "outer layer" refers to any film layer of a multilayer film having only one of its principal surfaces directly adhered to another layer of the film. As used herein, the phrase "inside layer" refers to the outer layer, of a multilayer film packaging a product, which is closest to the product, relative to the other layers of the multilayer film. As used herein, the phrase "outside layer" refers to the outer layer, of a multilayer film packaging a product, which is furthest from the product relative to the other layers of the multilayer film. As used herein, the term "extrusion" is used with reference to the process of forming continuous shapes by forcing a molten plastic material through a die, followed by cooling or chemical hardening. Immediately prior to extrusion through the die, the relatively high-viscosity polymeric material is fed into a rotating screw of variable pitch, which forces it through the die. As used herein, the term "coextrusion" refers to the process of extruding two or more materials through a single die with two or more orifices arranged so that the extrudates merge and weld together into a laminar structure before chilling, that is, quenching. Coextrusion can be employed in film blowing, free film extrusion, and extrusion coating processes. As used herein, the phrase "machine direction", herein abbreviated "MD", refers to a direction "along the length" of the film, that is, in the direction of the film as the film is formed during extrusion or coating. As used herein, the phrase "cross direction", herein abbreviated "CD", refers to a direction across the film, perpendicular to the machine or longitudinal direction. Elasticity can be described by the "permanent set" of the film. Permanent set is the converse of elasticity. A film is stretched to a certain point and subsequently released to the original position, and then stretched again. The point at which the elastic material begins to exert a force (that is show a non-zero force reading) is designated as the percent permanent set. The term "stretchable" is used herein in reference any material which, upon application of a biasing force, elongates at least 60 percent (that is, to a stretched, biased length which is at least 160 percent of its relaxed unbiased length), and which, will recover at least 55 percent of its elongation upon release of the stretching, elongating force. As used herein, the terms "recover" and "recovery" refer to a contraction of a stretched material upon termination of a biasing force following stretching of the material by application of the biasing force. Thus a sample is pulled on a tensile testing machine with a 50 mm gauge length setting at 250 mm/min to 100 percent of its original length. The sample is then held at that elongation for 30 seconds. The sample is then unloaded at the same speed to the original 50 mm gauge length. After a 60 second hold, sample is pulled again to determine the point at which it exerts a force again. The percent recovery: (average of five measurements) is obtained initially measuring the percent elongation or percent set. This is obtained by measuring the distance to where the second load cycle begins to show a non-zero force reading. This distance is the percent set or percent elongation where; percent elongation = (elongated length-original length)/original length x 100/1. The percent recovery is then calculated as; percent recovery = (100 - percent elongation). The term "good elasticity" as used herein is used to describe films having > 80 percent recovery in the CD and > 60 percent recovery in the MD. As used herein, the term "nonelastic" refers to any material which does not fall within the definition of "elastic" or "stretchable" above. As used herein, the term "less-elastic" includes "nonelastic" and any material referenced apposite an "elastic material". The term "elastic material" as used herein refers to the films, strips, coatings, tapes, webs, ribbons, bands, sheets as well as the "elastic composite materials" disclosed herein unless specifically distinguished as pertaining to the prior art. The term "article" as used herein refers to fabricated composite items comprising elastic films disclosed herein. Articles include disposable infant care and adult incontinence care items such as incontinence garments, training pants and diapers. The term also includes packages or films used for packaging,or wrapping goods such as meat, vegetables and commercial goods. Also included are combinations of trays, bowls or other containers covered sealed or protected by such elastic films. The term "structure" as used herein is defined as a polymer composition which has undergone a molding, film-, fiber-, or foam-forming process. The term "fabricated article" as used herein is defined as a polymer composition in the form of a finished article which may be formed directly from said polymer composition or be formed from an intermediate comprising one of the films described herein. The term " film " as used herein is defined as having a thickness less than or equal to 12 mils. The term " sheet " as used herein is defined as having a thickness greater than 12 mils. The term "substantially random" (in the substantially random interpolymer comprising polymer units derived from ethylene or one or more α-olefin monomers or combinations thereof, with one or more vinyl aromatic monomers or aliphatic or cycloaliphatic vinyl or vinylidene monomers or combinations therof) as used herein means that the distribution of the monomers of said interpolymer can be described by the Bernoulli statistical model or by a first or second order Markovian statistical model, as described by J. C. Randall in POLYMER SEQUENCE DETERMINATION, Carbon- 13 NMR Method. Academic Press New York, 1977, pp. 71-78. Preferably, substantially random interpolymers do not contain more than 15 percent of the total amount of vinyl aromatic monomer in blocks of vinyl aromatic monomer of more than 3 units. More preferably, the interpolymer is not characterized by a high degree of either isotacticity or syndiotacticity. This means that in the carbon "13 NMR spectrum of the substantially random interpolymer the peak areas corresponding to the main chain methylene and methine carbons representing either meso diad sequences or racemic diad sequences should not exceed 75 percent of the total peak area of the main chain methylene and methine carbons. The present invention provides elastic films prepared from at least one substantially random interpolymer comprising polymer units derived from ethylene or one or more α-olefin monomers or combinations therof with specific amounts of one or more vinyl aromatic monomers or aliphatic or cycloaliphatic vinyl or vinylidene monomers or combinations therof. The present invention also provides elastic films prepared from blends of the substantially random interpolymers with one or more other polymer components which span a wide range of compositions. The other polymer component of the blend can include, but is not limited to, one or more of an engineering thermoplastic, an α-olefin homopolymer or interpolymer, a thermoplastic olefin, a styrenic block copolymer, a styrenic homo- or copolymer, an elastomer, a thermoset polymer, or a vinyl halide polymer. The Substantially Random Interpolymers The interpolymers used to prepare the elastic films of the present invention include interpolymers prepared by polymerizing ethylene or one or more α-olefins or combinations thereof with one or more vinyl aromatic monomers or one or more aliphatic or cycloaliphatic vinyl or vinylidene monomers or combinations thereof, and optionally other polymerizable monomers. Suitable α-olefins include for example, α-olefins containing from 3 to 20, preferably from 3 to 12, more preferably from 3 to 8 carbon atoms. Particularly suitable are ethylene, propylene, butene-1, 4-methyl-l-pentene, hexene-1 or octene-1 or ethylene in combination with one or more of propylene, butene- 1 , 4-methyl- 1 - pentene, hexene-1 or octene-1. These α-olefins do not contain an aromatic moiety. Other optional polymerizable ethylenically unsaturated monomer(s) include strained ring olefins such as norbornene and C,. 10 alkyl or C 6 . 10 aryl substituted norbornenes, with an exemplary interpolymer being ethylene/styrene/norbornene. Suitable vinyl aromatic monomers which can be employed to prepare the interpolymers include, for example, those represented by the following formula: Ar I (CH 2 ) n R i — c = C(R 2 ) 2 wherein R 1 is selected from the group of radicals consisting of hydrogen and alkyl radicals containing from 1 to 4 carbon atoms, preferably hydrogen or methyl; each R 2 is independently selected from the group of radicals consisting of hydrogen and alkyl radicals containing from 1 to 4 carbon atoms, preferably hydrogen or methyl; Ar is a phenyl group or a phenyl group substituted with from 1 to 5 substituents selected from the group consisting of halo, C M -alkyl, and C -haloalkyl; and n has a value from zero to 4, preferably from zero to 2, most preferably zero. Exemplary vinyl aromatic monomers include styrene, vinyl toluene, α-methylstyrene, t-butyl styrene, chlorostyrene, including all isomers of these compounds, . Particularly suitable such monomers include styrene and lower alkyl- or halogen-substituted derivatives thereof. Preferred monomers include styrene, α-methyl styrene, the lower alkyl- (C, - C 4 ) or phenyl-ring substituted derivatives of styrene, such as for example, ortho-, meta-, and para-methylstyrene, the ring halogenated styrenes, para-vinyl toluene or mixtures thereof, . A more preferred aromatic vinyl monomer is styrene. By the term "aliphatic or cycloaliphatic vinyl or vinylidene compounds", it is meant addition polymerizable vinyl or vinylidene monomers corresponding to the formula: A R i _ C = C(R 2 ) 2 wherein A 1 is a sterically bulky, aliphatic or cycloaliphatic substituent of up to 20 carbons, R 1 is selected from the group of radicals consisting of hydrogen and alkyl radicals containing from 1 to 4 carbon atoms, preferably hydrogen or methyl; each R 2 is independently selected from the group of radicals consisting of hydrogen and alkyl radicals containing from 1 to 4 carbon atoms, preferably hydrogen or methyl; or alternatively R 1 and A 1 together form a ring system. Preferred aliphatic or cycloaliphatic vinyl or vinylidene compounds are monomers in which one of the carbon atoms bearing ethylenic unsaturation is tertiary or quaternary substituted. Examples of such substituents include cyclic aliphatic groups such as cyclohexyl, cyclohexenyl, cyclooctenyl, or ring alkyl or aryl substituted derivatives thereof, tert- butyl, norbornyl, . Most preferred aliphatic or cycloaliphatic vinyl or vinylidene compounds are the various isomeric vinyl- ring substituted derivatives of cyclohexene and substituted cyclohexenes, and 5-ethylidene-2-norbornene. Especially suitable are 1-, 3-, and 4-vinylcyclohexene. The substantially random interpolymers may be modified by typical grafting, hydrogenation, functionalizing, or other reactions well known to those skilled in the art. The polymers may be readily sulfonated or chlorinated to provide functionalized derivatives according to established techniques. Although not a requirement for elastic behavior, the substantially random interpolymers or the elastic films comprising at least one layer of said substantially random interpolymers, may also be modified by various chain extending or cross- linking processes including, but not limited to peroxide-, silane-, sulfur-, radiation-, or azide-based cure systems. A full description of the various cross-linking technologies is described in copending U.S. Patent Application No's 08/921,641 and 08/921,642 both filed on August 27, 1997. Dual cure systems, which use a combination of heat, moisture cure, and radiation steps, may be effectively employed. Dual cure systems are disclosed and claimed in U. S. Patent Application Serial No. 536,022, filed on September 29, 1995, in the names of K. L. Walton and S. V. Karande. For instance, it may be desirable to employ peroxide crosslinking agents in conjunction with silane crosslinking agents, peroxide crosslinking agents in conjunction with radiation, sulfur-containing crosslinking agents in conjunction with silane crosslinking agents, etc. The substantially random interpolymers may also be modified by various other cross-linking processes including, but not limited to the incorporation of a diene component as a termonomer in its preparation and subsequent cross linking by the aforementioned methods and further methods including vulcanization via the vinyl group using sulfur for example as the cross linking agent. The substantially random interpolymers can be prepared as described in EP-A- 0,416,815 by James C. Stevens et al. and US Patent No. 5,703,187 by Francis J. Timmers. Such a method of preparation of the substantially random interpolymers includes polymerizing a mixture of polymerizable monomers in the presence of one or more metallocene or constrained geometry catalysts in combination with various cocatalysts. Preferred operating conditions for such polymerization reactions are pressures from atmospheric up to 3000 atmospheres and temperatures from -30°C to 200°C. Polymerizations and unreacted monomer removal at temperatures above the autopolymerization temperature of the respective monomers may result in formation of some amounts of homopolymer polymerization products resulting from free radical polymerization. Examples of suitable catalysts and methods for preparing the substantially random interpolymers are disclosed in U.S. Application Serial No. 702,475, filed May 20, 1991 (EP-A-514,828); as well as U.S. Patents: 5,055,438; 5,057,475; 5,096,867; 5,064,802; 5,132,380; 5,189,192; 5,321,106; 5,347,024; 5,350,723; 5,374,696; 5,399,635; 5,470,993; 5,703,187; and 5,721,185. The substantially random α-olefin/vinyl aromatic interpolymers can also be prepared by the methods described in JP 07/278230 employing compounds shown by the general formula where Cp 1 and Cp 2 are cyclopentadienyl groups, indenyl groups, fluorenyl groups, or substituents of these, independently of each other; R 1 and R 2 are hydrogen atoms, halogen atoms, hydrocarbon groups with carbon numbers of 1 -12, alkoxyl groups, or aryloxyl groups, independently of each other; M is a group IV metal, preferably Zr or Hf, most preferably Zr; and R 3 is an alkylene group or silanediyl group used to crosslink Cp 1 and Cp 2 ). The substantially random α-olefin/vinyl aromatic interpolymers can also be prepared by the methods described by John G. Bradfute et al. (W. R. Grace & Co.) in WO 95/32095; by R. B. Pannell (Exxon Chemical Patents, Inc.) in WO 94/00500; and in Plastics Technology, p. 25 (September 1992). Also suitable are the substantially random interpolymers which comprise at least one α-olefin/vinyl aromatic/vinyl aromatic/α-olefin tetrad disclosed in U. S. Application No. 08/708,809 filed September 4, 1996 and WO 98/09999 both by Francis J. Timmers et al. These interpolymers contain additional signals in their carbon- 13 NMR spectra with intensities greater than three times the peak to peak noise. These signals appear in the chemical shift range 43.70 - 44.25 ppm and 38.0 - 38.5 ppm. Specifically, major peaks are observed at 44.1, 43.9, and 38.2 ppm. A proton test NMR experiment indicates that the signals in the chemical shift region 43.70 - 44.25 ppm are methine carbons and the signals in the region 38.0 - 38.5 ppm are methylene carbons. It is believed that these new signals are due to sequences involving two head- to-tail vinyl aromatic monomer insertions preceded and followed by at least one α- olefin insertion, for example an ethylene/styrene/styrene/ethylene tetrad wherein the styrene monomer insertions of said tetrads occur exclusively in a 1 ,2 (head to tail) manner. It is understood by one skilled in the art that for such tetrads involving a vinyl aromatic monomer other than styrene and an α-olefin other than ethylene that the ethylene/vinyl aromatic monomer/vinyl aromatic monomer/ethylene tetrad will give rise to similar carbon- 13 NMR peaks but with slightly different chemical shifts. These interpolymers can be prepared by conducting the polymerization at temperatures of from -30°C to 250°C in the presence of such catalysts as those represented by the formula wherein: each Cp is independently, each occurrence, a substituted cyclopentadienyl group π-bound to M; E is C or Si; M is a group IV metal, preferably Zr or Hf, most preferably Zr; each R is independently, each occurrence, H, hydrocarbyl, silahydrocarbyl, or hydrocarbylsilyl, containing up to 30 preferably from 1 to 20 more preferably from 1 to 10 carbon or silicon atoms; each R is independently, each occurrence, H, halo, hydrocarbyl, hyrocarbyloxy, silahydrocarbyl, hydrocarbylsilyl containing up to 30 preferably from 1 to 20 more preferably from 1 to 10 carbon or silicon atoms or two R' groups together can be a C 0 hydrocarbyl substituted 1,3- butadiene; m is 1 or 2; and optionally, but preferably in the presence of an activating cocatalyst. Particularly, suitable substituted cyclopentadienyl groups include those illustrated by the formula: wherein each R is independently, each occurrence, H, hydrocarbyl, silahydrocarbyl, or hydrocarbylsilyl, containing up to 30 preferably from 1 to 20 more preferably from 1 to 10 carbon or silicon atoms or two R groups together form a divalent derivative of such group. Preferably, R independently each occurrence is (including where appropriate all isomers) hydrogen, methyl, ethyl, propyl, butyl, pentyl, hexyl, benzyl, phenyl or silyl or (where appropriate) two such R groups are linked together forming a fused ring system such as indenyl, fluorenyl, tetrahydroindenyl, tetrahydrofluorenyl, or octahydrofluorenyl. Particularly preferred catalysts include, for example, racemic- (dimethylsilanediyl)-bis-(2-methyl-4-phenylindenyl))zirconium dichloride, racemic- (dimethylsilanediyl)-bis-(2-methyl-4-phenylindenyl))zirconium 1 ,4-diphenyl- 1,3- butadiene, racemic-(dimethylsilanediyl)-bis-(2-methyl-4-phenylindenyl))zirconium di-C 1 -4 alkyl, racemic-(dimethylsilanediyl)-bis-(2-methyl-4-phenylindenyl)) zirconium di-C 1-4 alkoxide, or any combination thereof . It is also possible to use the following titanium-based constrained geometry catalysts, [N-(l, l-dimethylethyl)-l, l-dimethyl-l-[(l,2,3,4,5-η)-l,5,6,7-tetrahydro-s- indacen-l-yl]silanaminato(2-)-N]titanium dimethyl; (l-indenyl)(tert-butylamido) dimethyl- silane titanium dimethyl; ((3-tert-butyl)(l,2,3,4,5-η)-l-indenyl)(tert- butylamido) dimethylsilane titanium dimethyl; and ((3-iso-propyl)(l,2,3,4,5-η)-l- indenyl)(tert-butyl amido)dimethylsilane titanium dimethyl, or any combination thereof . Further preparative methods for the interpolymers used in the present invention have been described in the literature. Longo and Grassi (Makromol. Chem.. Volume 191, pages 2387 to 2396 [1990]) and D'Anniello et al. (Journal of Applied Polymer Science, Volume 58, pages 1701-1706 [1995]) reported the use of a catalytic system based on methylalumoxane (MAO) and cyclopentadienyltitanium trichloride (CpTiClj) to prepare an ethylene-styrene copolymer. Xu and Lin (Polymer Preprints. Am. Chem. Soc. Div. Polvm. Chem Volume 35, pages 686,687 [1994]) have reported copolymerization using a MgCl 2 /TiCl 4 /NdCl 3 / Al(iBu) 3 catalyst to give random copolymers of styrene and propylene. Lu et al (Journal of Applied Polymer Science, Volume 53, pages 1453 to 1460 [1994]) have described the copolymerization of ethylene and styrene using a TiCl 4 /NdCl 3 / MgCl 2 /Al(Et) 3 catalyst. Sernetz and Mulhaupt, (Macromol. Chem. Phys.. v. 197, pp. 1071-1083, 1997) have described the influence of polymerization conditions on the copolymerization of styrene with ethylene using Me 2 Si(Me 4 Cp)(N-tert-butyl)TiCl 2 /methylaluminoxane Ziegler-Natta catalysts. Copolymers of ethylene and styrene produced by bridged metallocene catalysts have been described by Arai, Toshiaki and Suzuki (Polymer Preprints, Am. Chem. Soc. Div. Polvm. Chem.) Volume 38, pages 349, 350 [1997]) and in United States patent number 5,652,315, issued to Mitsui Toatsu Chemicals, Inc. The manufacture of α-olefin vinyl aromatic monomer interpolymers such as propylene/styrene and butene/styrene are described in United States patent number 5,244,996, issued to Mitsui Petrochemical Industries Ltd or United States patent number 5,652,315 also issued to Mitsui Petrochemical Industries Ltd or as disclosed in DE 197 11 339 Al to Denki KAGAKU KOGYO KK. While preparing the substantially random interpolymer, an amount of atactic vinyl aromatic homopolymer may be formed due to homopolymerization of the vinyl aromatic monomer at elevated temperatures. The presence of vinyl aromatic homopolymer is in general not detrimental for the purposes of the present invention and can be tolerated. The vinyl aromatic homopolymer may be separated from the interpolymer, if desired, by extraction techniques such as selective precipitation from solution with a non solvent for either the interpolymer or the vinyl aromatic homopolymer. For the purpose of the present invention it is preferred that no more than 30 weight percent, preferably less than 20 weight percent based on the total weight of the interpolymers of atactic vinyl aromatic homopolymer is present. Blend Compositions Comprising the Substantially Random Interpolymers The present invention also provides films prepared from blends of the substantially random interpolymers with one or more other polymer components, which span a wide range of compositions. The other polymer component of the blend can include, but is not limited to, one or more of an engineering thermoplastic, an α-olefin homopolymer or interpolymer, a thermoplastic olefin, a styrenic block copolymer, a styrenic copolymer, an elastomer, a thermoset polymer, or a vinyl halide polymer. Engineering Thermoplastics The third edition of the Kirk-Othmer Encyclopedia of Science and Technology (Volume 9, p 118 - 137), defines engineering plastics as thermoplastic resins, neat or unreinforced or filled, which maintain dimensional stability and most mechanical properties above 100°C and below 0°C. The terms "engineering plastics" and "engineering thermoplastics", can be used interchangeably. Engineering thermoplastics include acetal and acrylic resins, polyamides (for example nylon-6, nylon 6,6,), polyimides, polyetherimides, cellulosics, polyesters, poly(arylate), aromatic polyesters, poly (carbonate), poly(butylene) and polybutylene and polyethylene terephthalates, liquid crystal polymers, and selected polyolefins, blends, or alloys of the foregoing resins, and some examples from other resin types (including for example polyethers) high temperature polyolefins such as polycyclopentanes, its copolymers, and polymethylpentane.). An especially preferred engineering thermoplastic are the acrylic resins which derive from the peroxide-catalyzed free radical polymerization of methyl methacrylate (MMA). As described by H. Luke in Modern Plastics Encyclopedia, 1989, pps 20-21, MMA is usually copolymerized with other acrylates such as methyl- or ethyl acrylate using four basic polymerization processes, bulk, suspension, emulsion and solution. Acrylics can also be modified with various ingredients including butadiene, vinyl and butyl acrylate. The α-Olefin Homopolvmers and Interpolymers The α-olefin homopolymers and interpolymers comprise polypropylene, propylene/C 4 -C 20 α- olefin copolymers, polyethylene, and ethylene/C 3 -C 20 α- olefin copolymers, the interpolymers can be either heterogeneous ethylene/α-olefm interpolymers or homogeneous ethylene/α-olefin interpolymers, including the substantially linear ethylene/α-olefin interpolymers. Also included are aliphatic α- olefins having from 2 to 20 carbon atoms and containing polar groups. Suitable aliphatic α-olefin monomers which introduce polar groups into the polymer include, for example, ethylenically unsaturated nitriles such as acrylonitrile, methacrylonitrile, ethacrylonitrile, etc.; ethylenically unsaturated anhydrides such as maleic anhydride; ethylenically unsaturated amides such as acrylamide, methacrylamide etc.; ethylenically unsaturated carboxylic acids (both mono- and difunctional) such as acrylic acid and methacrylic acid, etc.; esters (especially lower, for example C,-C 6 , alkyl esters) of ethylenically unsaturated carboxylic acids such as methyl methacrylate, ethyl acrylate, hydroxyethylacrylate, n-butyl acrylate or methacrylate, 2-ethyl-hexylacrylate, or ethylene-vinyl acetate copolymers etc.; ethylenically unsaturated dicarboxylic acid imides such as N-alkyl or N-aryl maleimides such as N-phenyl maleimide, etc. Preferably such monomers containing polar groups are acrylic acid, vinyl acetate, maleic anhydride and acrylonitrile. Halogen groups which can be included in the polymers from aliphatic α-olefin monomers include fluorine, chlorine and bromine; preferably such polymers are chlorinated polyethylenes (CPEs) Heterogeneous interpolymers are differentiated from the homogeneous interpolymers in that in the latter, substantially all of the interpolymer molecules have the same ethylene/comonomer ratio within that interpolymer, whereas heterogeneous inteφolymers are those in which the interpolymer molecules do not have the same ethylene/comonomer ratio. The term "broad composition distribution" used herein describes the comonomer distribution for heterogeneous interpolymers and means that the heterogeneous inteφolymers have a "linear" fraction and that the heterogeneous inteφolymers have multiple melting peaks (that is, exhibit at least two distinct melting peaks) by DSC. The heterogeneous inteφolymers have a degree of branching less than or equal to 2 methyls/ 1000 carbons in 10 percent (by weight) or more, preferably more than 15 percent (by weight), and especially more than 20 percent (by weight). The heterogeneous inteφolymers also have a degree of branching equal to or greater than 25 methyls/ 1000 carbons in 25 percent or less (by weight), preferably less than 15 percent (by weight), and especially less than 10 percent (by weight). The Ziegler catalysts suitable for the preparation of the heterogeneous component of the current invention are typical supported, Ziegler-type catalysts. Examples of such compositions are those derived from organomagnesium compounds, alkyl halides or aluminum halides or hydrogen chloride, and a transition metal compound. Examples of such catalysts are described in U.S. Pat Nos. 4,314,912 (Lowery, Jr. et al.), 4,547,475 (Glass et al.), and 4,612,300 (Coleman, III). Suitable catalyst materials may also be derived from a inert oxide supports and transition metal compounds. Examples of such compositions are described in U.S. Pat No. 5,420,090 (Spencer, et al.). The heterogeneous polymer component can be an α-olefin homopolymer preferably polyethylene or polypropylene, or, preferably, an inteφolymer of ethylene with at least one C3-C2O α-olefin or C4-C18 dienes or combinations thereof. Heterogeneous copolymers of ethylene, and propylene, 1-butene, 1-hexene, 4-methyl- 1-pentene and 1-octene are especially preferred. The relatively recent introduction of metallocene-based catalysts for ethylene/α-olefin polymerization has resulted in the production of new ethylene inteφolymers known as homogeneous inteφolymers. The homogeneous inteφolymers useful for forming the compositions described herein have homogeneous branching distributions. That is, the polymers are those in which the comonomer is randomly distributed within a given inteφolymer molecule and wherein substantially all of the inteφolymer molecules have the same ethylene/comonomer ratio within that inteφolymer. The homogeneity of the polymers is typically described by the SCBDI (Short Chain Branch Distribution Index) or CDBI (Composition Distribution Branch Index) and is defined as the weight percent of the polymer molecules having a comonomer content within 50 percent of the median total molar comonomer content. The CDBI of a polymer is readily calculated from data obtained from techniques known in the art, such as, for example, temperature rising elution fractionation (abbreviated herein as "TREF") as described, for example, in Wild et al, Journal of Polymer Science. Poly. Phvs. Ed.. Vol. 20, p. 441 (1982), in U.S. Patent 4,798,081 (Hazlitt et al.), or as is described in USP 5,008,204 (Stehling). The technique for calculating CDBI is described in USP 5,322,728 (Davey et al. ) and in USP 5,246,783 (Spenadel et al.). or in U.S. Patent 5,089,321 (Chum et al.). The SCBDI or CDBI for the homogeneous inteφolymers used in the present invention is preferably greater than 30 percent, especially greater than 50 percent. The homogeneous inteφolymers used in this invention essentially lack a measurable "high density" fraction as measured by the TREF technique (that is, the homogeneous ethylene/α-olefm inteφolymers do not contain a polymer fraction with a degree of branching less than or equal to 2 methyls/1000 carbons). The homogeneous inteφolymers also do not contain any highly short chain branched fraction (that is, they do not contain a polymer fraction with a degree of branching equal to or more than 30 methyls/1000 carbons). The substantially linear ethylene/α-olefin polymers and inteφolymers of the present invention are also homogeneous inteφolymers but are further herein defined as in U.S. Patent No. 5,272,236 (Lai et al.), and in U.S. Patent No. 5,272,872. Such polymers are unique however due to their excellent processability and unique rheological properties and high melt elasticity and resistance to melt fracture. These polymers can be successfully prepared in a continuous polymerization process using the constrained geometry metallocene catalyst systems. The term "substantially linear" ethylene/α-olefin inteφolymer means that the polymer backbone is substituted with 0.01 long chain branches/1000 carbons to 3 long chain branches/1000 carbons, more preferably from 0.01 long chain branches/1000 carbons to 1 long chain branches/1000 carbons, and especially from 0.05 long chain branches/1000 carbons to 1 long chain branches/1000 carbons. Long chain branching is defined herein as a chain length of at least one carbon more than two carbons less than the total number of carbons in the comonomer, for example, the long chain branch of an ethylene/octene substantially linear ethylene inteφolymer is at least seven (7) carbons in length (that is, 8 carbons less 2 equals 6 carbons plus one equals seven carbons long chain branch length). The long chain branch can be as long as the same length as the length of the polymer back-bone. Long chain branching is determined by using ^C nuclear magnetic resonance (NMR) spectroscopy and is quantified using the method of Randall (Rev. Macromol. Chem. Phys., C29 (2&3), p. 285-297). Long chain branching, of course, is to be distinguished from short chain branches which result solely from incoφoration of the comonomer, so for example the short chain branch of an ethylene/octene substantially linear polymer is six carbons in length, while the long chain branch for that same polymer is at least seven carbons in length. The catalysts used to prepare the homogeneous inteφolymers for use as blend components in the present invention are metallocene catalysts. These metallocene catalysts include the bis(cyclopentadienyl)-catalyst systems and the mono(cyclopentadienyl) Constrained Geometry catalyst systems (used to prepare the substantially linear ethylene/α-olefin polymers). Such constrained geometry metal complexes and methods for their preparation are disclosed in U.S. Application Serial No. 545,403, filed July 3, 1990 (EP-A-416,815); U.S. Application Serial No. 547,718, filed July 3, 1990 (EP-A-468,651); U.S. Application Serial No. 702,475, filed May 20, 1991 (EP-A-514,828); as well as US-A-5,055,438, US-A-5,057,475, US-A-5,096,867, US-A-5,064,802, US-A-5, 132,380, US-A-5,721,185, US-A-5,374,696 and US-A- 5,470,993. For the teachings contained therein, the aforementioned pending United States Patent applications, issued United States Patents and published European Patent Applications are herein incoφorated in their entirety by reference thereto. In EP-A 418,044, published March 20, 1991 (equivalent to U.S. Serial No. 07/758,654) and in U.S. Serial No. 07/758,660 certain cationic derivatives of the foregoing constrained geometry catalysts that are highly useful as olefin polymerization catalysts are disclosed and claimed. In U.S. Serial Number 720,041, filed June 24, 1991, certain reaction products of the foregoing constrained geometry catalysts with various boranes are disclosed and a method for their preparation taught and claimed. In US-A 5,453,410 combinations of cationic constrained geometry catalysts with an alumoxane were disclosed as suitable olefin polymerization catalysts. For the teachings contained therein, the aforementioned pending United States Patent applications, issued United States Patents and published European Patent Applications are herein incoφorated in their entirety by reference thereto. The homogeneous polymer component can be an α-olefin homopolymer preferably polyethylene or polypropylene, or, preferably, an inteφolymer of ethylene with at least one C3-C20 α-olefin or C4-C18 dienes or combinations thereof. Homogeneous copolymers of ethylene, and propylene, 1-butene, 1-hexene, 4-methyl- 1-pentene and 1-octene are especially preferred. Thermoplastic Olefins Thermoplastic olefins (TPOs) are generally produced from propylene homo- or copolymers, or blends of an elastomeric material such as ethylene/propylene rubber (EPM) or ethylene/propylene diene monomer teφolymer (EPDM) and a more rigid material such as isotactic polypropylene. Other materials or components can be added into the formulation depending upon the application, including oil, fillers, and cross- linking agents. Generally, TPOs are characterized by a balance of stiffness (modulus) and low temperature impact, good chemical resistance and broad use temperatures. Because of features such as these, TPOs are used in many applications, including automotive facia and instrument panels, and also potentially in wire and cable The polypropylene is generally in the isotactic form of homopolymer polypropylene, although other forms of polypropylene can also be used (for example, syndiotactic or atactic). Polypropylene impact copolymers (for example, those wherein a secondary copolymerization step reacting ethylene with the propylene is employed) and random copolymers (also reactor modified and usually containing 1.5-7 percent ethylene copolymerized with the propylene), however, can also be used in the TPO formulations disclosed herein. In-reactor TPO's can also be used as blend components of the present invention. A complete discussion of various polypropylene polymers is contained in Modern Plastics Encvclopedia/89. mid October 1988 Issue, Volume 65, Number 11, pp. 86-92. The molecular weight of the polypropylene for use in the present invention is conveniently indicated using a melt flow measurement according to ASTM D- 1238, Condition 230°C/2.16 kg (formerly known as "Condition (L)" and also known as 12). Melt flow rate is inversely proportional to the molecular weight of the polymer. Thus, the higher the molecular weight, the lower the melt flow rate, although the relationship is not linear. The melt flow rate for the polypropylene useful herein is generally from 0.1 grams/10 minutes (g/10 min) to 35 g/10 min, preferably from 0.5 g/10 min to 25 g/10 min, and especially from 1 g/10 min to 20 g/10 min. Styrenic Block Copolymers Also included are block copolymers having unsaturated rubber monomer units including, but not limited to, styrene-butadiene (SB), styrene-isoprene(SI), styrene- butadiene-styrene (SBS), styrene-isoprene-styrene (SIS), α-methylstyrene-butadiene- α-methylstyrene and α-methylstyrene-isoprene-α-methylstyrene. The styrenic portion of the block copolymer is preferably a polymer or inteφolymer of styrene and its analogs and homologs including α-methylstyrene and ring-substituted styrenes, particularly ring-methylated styrenes. The preferred styrenics are styrene and α-methylstyrene, and styrene is particularly preferred. Block copolymers with unsaturated rubber monomer units may comprise homopolymers of butadiene or isoprene or they may comprise copolymers of one or both of these two dienes with a minor amount of styrenic monomer. Preferred block copolymers with saturated rubber monomer units comprise at least one segment of a styrenic unit and at least one segment of an ethylene- butene or ethylene-propylene copolymer. Preferred examples of such block copolymers with saturated rubber monomer units include styrene/ethylene-butene copolymers, styrene/ethylene-propylene copolymers, styrene/ethylene- butene/styrene (SEBS) copolymers, styrene/ethylene-propylene/styrene (SEPS) copolymers. Styrenic Homo- and Copolymers In addition to the block copolymers are the various styrene homopolymers and copolymers and rubber modified styrenics. These include polystyrene, high impact polystyrene and copolymers such as acrylonitrile-butadiene-styrene (ABS) polymers, styrene-acrylonitrile (SAN). Elastomers The elastomers include, but are not limited to, rubbers such as polyisoprene, polybutadiene, natural rubbers, ethylene/propylene rubbers, ethylene/propylene diene (EPDM) rubbers, styrene/butadiene rubbers, thermoplastic polyurethanes. Thermoset Polymers The thermoset polymers include but are not limited to, epoxies, vinyl ester resins, polyurethanes and phenolic resins. Vinyl Halide Polymers Vinyl halide homopolymers and copolymers are a group of resins which use as a building block the vinyl structure CH 2 =CXY, where X is selected from the group consisting of F, Cl, Br, and I and Y is selected from the group consisting of F, Cl, Br, I and H. The vinyl halide polymer component of the blends of the present invention include but are not limited to homopolymers and copolymers of vinyl halides with copolymerizable monomers such as α-olefins including but not limited to ethylene, propylene, vinyl esters of organic acids containing 1 to 18 carbon atoms, for example vinyl acetate, vinyl stearate and so forth; vinyl chloride, vinylidene chloride, symmetrical dichloroethylene; acrylonitrile, methacrylonitrile; alkyl acrylate esters in which the alkyl group contains 1 to 8 carbon atoms, for example methyl acrylate and butyl acrylate; the corresponding alkyl methacrylate esters; dialkyl esters of dibasic organic acids in which the alkyl groups contain 1 - 8 carbon atoms, for example dibutyl fumarate, diethyl maleate, and so forth. Preferably the vinyl halide polymers are homopolymers or copolymers of vinyl chloride or vinylidene chloride. Poly (vinyl chloride) polymers (PVC) can be further classified into two main types by their degree of rigidity. These are "rigid" PVC and "flexible" PVC. Flexible PVC is distinguished from rigid PVC primarily by the presence of and amount of plasticizers in the resin. Flexible PVC typically has improved processability, lower tensile strength and higher elongation than rigid PVC. Of the vinylidene chloride homopolymers and copolymers (PVDC), typically the copolymers with vinyl chloride, acrylates or nitriles are used commercially and are most preferred. The choice of the comonomer significantly affects the properties of the resulting polymer. Perhaps the most notable properties of the various PVDC's are their low permeability to gases and liquids, barrier properties; and chemical resistance. Also included in the family of vinyl halide polymers for use as blend components of the present invention are the chlorinated derivatives of PVC typically prepared by post chlorination of the base resin and known as chlorinated PVC, (CPVC). Although CPVC is based on PVC and shares some of its characteristic properties, CPVC is a unique polymer having a much higher melt temperature range (410 - 450°C) and a higher glass transition temperature (239 - 275°F) than PVC. The compositions comprising at least one substantially random inteφolymer used to prepare the elastic films of the present invention in addition to optionally comprising one or more of another polymer components can optionally comprise one or more additives. Other Additives Additives such as antioxidants (for example, hindered phenols such as, for example, Irganox® 1010, and phosphites, for example, Irgafos™ 168, (both are registered trademarks of, and supplied by Ciba-Geigy Coφoration, NY), u.v. stabilizers (including Tinuvin™ 328 and Chimassorb™ 944, both are registered trademarks of, and supplied by Ciba-Geigy Coφoration, NY), cling additives (for example, polyisobutylene), slip agents (such as erucamide or stearamide or combinations therof), antiblock additives, colorants, pigments, can also be included in the inteφolymers blends employed to prepare the elastic films of the present invention, to the extent that they do not interfere with the elastic properties of the films comprising the substantially random inteφolymers. Processing aids, which are also referred to herein as plasticizers, are optionally provided to reduce the viscosity of a composition, and include the phthalates, such as dioctyl phthalate and diisobutyl phthalate, natural oils such as lanolin, and paraffin, naphthenic and aromatic oils obtained from petroleum refining, and liquid resins from rosin or petroleum feedstocks. Suitable modifiers which can be employed herein as the plasticizer include at least one plasticizer selected from the group consisting of phthalate esters, trimellitate esters, benzoates, adipate esters, epoxy compounds, phosphate esters (triaryl, trialkyl, mixed alkyl aryl phosphates), glutarates and oils. Particularly suitable phthalate esters include, for example, dialkyl C4-C18 phthalate esters such as diethyl, dibutyl phthalate, diisobutyl phthalate, butyl 2-ethylhexyl phthalate, dioctyl phthalate, diisooctyl phthalate, dinonyl phthalate, diisononyl phthalate, didecyl phthalate, diisodecyl phthalate, diundecyl phthalate, mixed aliphatic esters such as heptyl nonyl phthalate, di(n-hexyl, n-octyl, n-decyl) phthalate (P610), di (n-octyl, n- decyl) phthalate (P810), and aromatic phthalate esters such as diphenyl phthalate ester, or mixed aliphatic-aromatic esters such as benzyl butyl phthalate or any combination thereof . Exemplary classes of oils useful as processing aids include white mineral oil (such as Kay do 1™ oil (available from Witco), and Shellfiex™ 371 naphthenic oil (available from Shell Oil Company). Another suitable oil is Tuflo™ oil (available from Lyondell). Antifogging or antistatic agents can be added to the films and sheets of the present invention to increase surface conductivity and prevention of water droplet formation and attraction of dust and dirt on the film surface. These antifogging agents include, but are not limited to, glycerol mono-stearate, glycerol mono-oleate, lauric diphthalamides, ethoxylated amines, ethoxylated esters, and other additives known in the industry. Tackifiers can also be added to the polymer compositions used to prepare the films or sheets of the present invention in order to alter the Tg and thus extend the available application temperature window of the film. Examples of the various classes of tackifiers include, but are not limited to, aliphatic resins, polyteφene resins, hydrogenated resins, mixed aliphatic- aromatic resins, styrene/α-methylene styrene resins, pure monomer hydrocarbon resin, hydrogenated pure monomer hydrocarbon resin, modified styrene copolymers, pure aromatic monomer copolymers, and hydrogenated aliphatic hydrocarbon resins. Exemplary aliphatic resins include those available under the trade designations Escorez™, Piccotac™, Mercures™, Wingtack™, Hi-Rez™, Quintone™, Tackirol™, etc. Exemplary polyteφene resins include those available under the trade designations Nirez™, Piccolyte™, Wingtack™, Zonarez™, etc. Exemplary hydrogenated resins include those available under the trade designations Escorez™, Arkon™, Clearon™, etc. Exemplary mixed aliphatic-aromatic resins include those available under the trade designations Escorez™, Regalite™, Hercures™, AR™, Imprez™, Norsolene™ M, Marukarez™, Arkon™ M, Quintone™, Wingtack™, etc. One particularly preferred class of tackifiers includes the styrene/α -methylene stryene tackifiers available from Hercules. Particularly suitable classes of tackifiers include Wingtack™ 86 and Hercotac™ 1149, Eastman H-130, and styrene/α-methyl styrene tackifiers. Also included as a potential component of the polymer compositions used in the present invention are various organic and inorganic fillers, the identity of which depends upon the type of application for which the elastic film is to be utilized. Representative examples of such fillers include organic and inorganic fibers such as those made from asbestos, boron, graphite, ceramic, glass, metals (such as stainless steel) or polymers (such as aramid fibers) talc, carbon black, carbon fibers, calcium carbonate, alumina trihydrate, glass fibers, marble dust, cement dust, clay, feldspar, silica or glass, fumed silica, alumina, magnesium oxide, magnesium hydroxide, antimony oxide, zinc oxide, barium sulfate, aluminum silicate, calcium silicate, titanium dioxide, titanates, aluminum nitride, B 2 O 3 , nickel powder or chalk. Other representative organic or inorganic, fiber or mineral, fillers include carbonates such as barium, calcium or magnesium carbonate; fluorides such as calcium or sodium aluminum fluoride; hydroxides such as aluminum hydroxide; metals such as aluminum, bronze, lead or zinc; oxides such as aluminum, antimony, magnesium or zinc oxide, or silicon or titanium dioxide; silicates such as asbestos, mica, clay (kaolin or calcined kaolin), calcium silicate, feldspar, glass (ground or flaked glass or hollow glass spheres or microspheres or beads, whiskers or filaments), nepheline, perlite, pyrophyllite, talc or wollastonite; sulfates such as barium or calcium sulfate; metal sulfides; cellulose, in forms such as wood or shell flour; calcium terephthalate; and liquid crystals. Mixtures of more than one such filler may be used as well. These additives are employed in functionally equivalent amounts known to those skilled in the art. For example, the amount of antioxidant employed is that amount which prevents the polymer or polymer blend from undergoing oxidation at the temperatures and environment employed during storage and ultimate use of the polymers. Such amount of antioxidants is usually in the range of from 0.01 to 10, preferably from 0.05 to 5, more preferably from 0.1 to 2 percent by weight based upon the weight of the polymer or polymer blend. Similarly, the amounts of any of the other enumerated additives are the functionally equivalent amounts such as the amount to render the polymer or polymer blend antiblocking, to produce the desired result, to provide the desired color from the colorant or pigment. Such additives can suitably be employed in the range of from 0.05 to 50, preferably from 0.1 to 35, more preferably from 0.2 to 20 percent by weight based upon the weight of the polymer or polymer blend. When a processing aid is employed, it will be present in the composition of the invention in an amount of at least 5 percent. The processing aid will typically be present in an amount of no more than 60, preferably no more than 30, and most preferably no more than 20 weight percent. Preparation of the Blends Comprising the Substantially Random Inteφolymers The blended polymer compositions used to prepare the elastic films of the present invention can be prepared by any convenient method, including dry blending the individual components and subsequently melt mixing or melt compounding in a Haake torque rheometer or by dry blending without melt blending followed by part fabrication, either directly in the extruder or mill used to make the finished article (for example, the automotive part), or by pre-melt mixing in a separate extruder or mill (for example, a Banbury mixer), or by solution blending, or by compression molding, or by calendering. Preparation of the Elastic Films of the Present Invention The elastic films of the present invention can be made using conventional fabrication techniques, for example simple bubble extrusion, simple cast/sheet extrusion, coextrusion, lamination, etc. Conventional simple bubble extrusion processes (also known as hot blown film processes) are described, for example, in The Encyclopedia of Chemical Technology. Kirk-Othmer, Third Edition, John Wiley & Sons, New York, 1981, Vol 16, pp. 416-417 and Vol. 18, pp. 191-192. Injection molding, thermoforming, extrusion coating, profile extrusion, and sheet extrusion processes are described, for example, in Plastics Materials and Processes, Seymour S. Schwartz and Sidney H. Goodman, Van Nostrand Reinhold Company, New York, 1982, pp. 527-563, pp. 632-647, and pp. 596-602. The strips, tapes and ribbons of the present invention can be prepared by the primary extrusion process itself or by known post-extrusion slitting, cutting or stamping techniques. Profile extrusion is an example of a primary extrusion process that is particularly suited to the preparation of tapes, bands, ribbons . The elastic films of the present invention can also be rendered pervious or "breathable" by any method well known in the art including by apperturing, slitting, microperforating, mixing with fibers or foams, or the like and combinations thereof. Examples of such methods include, USP 3,156,242 by Crowe, Jr., USP 3,881,489 by Hartwell, USP 3,989,867 by Sisson and USP 5,085,654 by Buell, the disclosures of all of which are incoφorate herein by reference. The film structure and the substantially random inteφolymer selected for use in the practice of this invention will depend in large part upon the particulars of the application, for example the preferred properties of a film used in a shrink wrap are different than the preferred properties of a film used in a stretch overwrap. The present elastic film structures can be monolayer film or a multilayer film in which one or more film layers comprises at least one substantially random inteφolymer. In those embodiments in which the film structure is multilayer, it can be of any conventional structure, for example 2-ply, 3-ply, 4-ply, 5-ply, 6-ply, 7-ply, etc. The structure will generally have an odd number of layers, and the film layer(s) comprising a substantially random inteφolymer can be one or both outer layers or one or more core layers or both. Those layer(s) constructed from polymer other than a substantially random inteφolymer can comprise any suitable material generally compatible with a film constructed from a substantially random inteφolymer, for example one or more conventional LDPE, LLDPE, ULDPE, EVA, EAA, . Additives such as those described above with respect to monolayer films can also be used in these multilayer films, and these additives can be incoφorated into any of the film layers as desired, for example tackifiers and slip agents into one or both outer layers, fillers in one or more core layers, etc. Other multilayer film manufacturing techniques for food packaging applications are described in Packaging Foods With Plastics by Wilmer A. Jenkins and James P. Harrington (1991), pp. 19-27, and in "Coextrusion Basics" by Thomas I. Butler, Film Extrusion Manual: Process. Materials. Properties, pp. 31 -80 (published by TAPPI Press (1992)). Other desirable properties of the plastic films used in this invention include, depending on the nature of the other film layers in the structure, ease of fabrication and good oxygen permeability (particularly with respect to films made from such copolymers as EVA and EAA), oxygen impermeability (particularly with respect to films containing an oxygen barrier such as SARAN or ethylene vinyl alcohol), dart impact, puncture resistance, tensile strength, low modulus, tear resistance, shrinkability, high clarity and a low affect on the taste and odor properties of the packaged food. The plastic films of this invention are well suited for stretch overwrap packaging various fresh foods, for example retail-cut red meats, fish, poultry, vegetables, fruits, cheeses, and other food products destined for retail display. These films are preferably prepared as nonshrink films (for example, without biaxial orientation induced by double bubble processing), with good stretch, elastic recovery and hot tack characteristics, and can be made available to wholesalers and retailers in any conventional form, for example stock rolls, and used on all conventional equipment. Other plastic films of this invention can be used as shrink, skin and vacuum form packages for foods. The films comprising the shrink packages are typically biaxially oriented, exhibit low shrink tension, are of a density greater than 0.89 g/cm^, and are typically 0.6 to 2 mil in thickness. The elastic film structures used in vacuum skin packaging can be multilayered, are typically 5 to 12 mil in thickness. The elastic films of the present invention can also be formed by extrusion processes and, most preferably, by art-known coextrusion methods. Following coextrusion the film is cooled to a solid state by, for example, cascading water or chilled air quenching. For some structures a precursor film layer or layers may be formed by extrusion with additional layers thereafter being extrusion coated thereon to form multilayer films. Two multilayer tubes may also be formed with one of the tubes thereafter being coated or laminated onto the other. Preparation of the Fabricated Composite Articles Comprising the Elastic Film of The Present Invention. Fabricated articles which can be made using the novel elastic films disclosed herein include composite fabric articles (for example, disposable incontinence garments and diapers) that are comprised of one or more elastic component or portion. For example, elastic components are commonly present in diaper waist band portions to prevent the diaper from falling and leg band portions to prevent leakage (as shown in USP 4,381,781 (Sciaraffa)). Often, the elastic component promotes better form fitting or fastening systems for a good combination of comfort and security. The novel elastic films disclosed herein can also produce fabric composite structures which combine elasticity with breathability by utilization of a technique that renders the elastic film pervious or "breathable" such as suggested by Lippert et al. in USP 4,861,652 and indicated above. The novel elastic films disclosed herein can also be used in various structures as described in USP 2,957,512 (Wade). For example, layer 50 of the structure described in USP '512 (that is, the elastic component) can be replaced with the novel elastic film, especially where flat, pleated, creped, etc., nonelastic films are made into elastic or semi-elastic structures. Attachment of the novel elastic films to nonelastic or less-elastic films can be done with heat bonding or with adhesives. Gathered or shirred elastic composite materials can be produced from the new elastic film described herein and nonelastic components by pleating the non-elastic component (as described in USP '512) prior to attachment, prestretching the elastic component prior to attachment, or heat shrinking the elastic component after attachment. The novel elastic films described herein can also be used to make other novel structures. For example, USP 4,801,482 (Goggans), discloses an elastic sheet which can now be made with the novel materials described herein. The novel elastic films described herein can also be used to make breathable portion or breathable elastic composite materials. For example, USP 5,085,654 (Buell) discloses a leg band with a breathable portion, a breathable topsheet, a breathable backsheet, elastic elements, a breathable element, and a breathable sub- element all or any combination of which can now be made with the elastic films disclosed herein in either pervious or impervious forms. The novel elastic films disclosed herein also have adjustable stretchability and elasticity that can be achieved by specific combinations of elastic films and less- elastic material or by adjusting the inteφolymer composition or by specific combination of different substantially random inteφolymers, which enables design flexibility for variable stretchability or retractive force in the same garment, as described for example in USP 5,196,000 (Clear et al). USP 5,037,416 (Allen et al.), describes the advantages of a form fitting top sheet by using elastic ribbons and an elastic backsheet. Pervious novel elastic films described herein could serve the function of the elastic ribbons and impervious elastics materials of this invention could function as the elastic backsheet, or disclosed elastic films could be used in an elastic composite fabric form. In USP 4,981 ,747 (Morman), the novel elastic films disclosed herein can be substituted for elastic sheets to construct an elastic composite material which includes a reversibly necked material. Elastic panels, elements, portions or the like can also be made from the novel elastic films disclosed herein, and can be used, for example, as members described in USP 4,940,464 (Van Gompel). The novel elastic films described herein can also be used, for example, as elastic composite side panels (for example, layer) or as elastic ribbons. Properties of the Elastic Film of The Present Invention. Where the elasticity of the novel films of the present invention varies with respect to the thickness of the material, thicknesses less than 22 mils, preferably from 0.1 mils to 20 mils, and more preferably, from 0.4 mils to 15 mils are considered to be within the purview of this invention. The elastic films of the present invention films have a recovery in the CD of > 80 percent, preferably > 90 percent, more preferably > about95 percent, and a recovery in the MD of > 60 percent, preferably > 70 percent, more preferably > 75 percent. For the novel elastic films disclosed herein, the melt index of the substantially random inteφolymer can be widely varied, with little impact on elasticity. This allows more design flexibility for elastic composites and finished articles because the strength and retractive force of the elastic film can be changed independently of its elasticity. For example, the tensile strength properties of an elastic film can be changed by changing the polymer's melt index (decreasing the melt index increases the tensile strength properties), rather than by changing the thickness of the film, thus permitting a better optimization of the "hand" (that is, feel) of an elastic composite fabric with the desired elastic/strength performance of the composite fabric. The melt index of the substantially random inteφolymers disclosed herein is limited in traditional ways as requirements respecting specific extrusion processes. As examples, extrusion coating and injection molding processes typically require high melt indices to avoid excessive extrusion pressures and polymer shearing as well as to provide adequate melt flow characteristics, while blown film processes generally require lower melt indices to achieve adequate bubble stability. Properties of the Inteφolvmers and Blend Compositions Used to Prepare the Elastic Films of the Present Invention The polymer compositions used to prepare the elastic films of the present invention comprise from 50 to 100, preferably from 75 to 100, more preferably from 90 to 95 wt percent, (based on the combined weights of this component and the polymer component other than the substantially random inteφolymer) of one or more inteφolymers of ethylene or one or more α-olefins or combinations thereof, and one or more vinyl aromatic monomers or one or more aliphatic or cycloaliphatic vinyl or vinylidene monomers or combinations thereof. It has been discovered that elastic properties in the resultant films are observed when these substantially random inteφolymers contain from 10 to 40 preferably from 13 to 33, more preferably from 15 to 29 mole percent of at least one vinyl aromatic monomer or aliphatic or cycloaliphatic vinyl or vinylidene monomer or combinations thereof, and from 60 to 90, preferably from 67 to 87, more preferably from 71 to 85 mole percent of ethylene or at least one aliphatic α-olefin having from 3 to 20 carbon atoms or combinations thereof. The melt index (I 2 ) of the substantially random inteφolymer used to prepare the elastic films of the present invention is 0.1 to 1 ,000, preferably of from 0.5 to 200, more preferably of from 0.5 to 100 g/10 min. The molecular weight distribution (M ^ JM of the substantially random inteφolymer used to prepare the elastic films of the present invention is from 1.5 to 20, preferably of from 1.8 to 10, more preferably of from 2 to 5. The density of the substantially random inteφolymer used to prepare the elastic films of the present invention is greater than 0.930, preferably from 0.930 to 1.045, more preferably of from 0.930 to 1.040, most preferably of from 0.930 to 1.030 g/cm 3 . The polymer compositions used to prepare the elastic films of the present invention can also comprise from 0 to 50, preferably from 0 to 25, even more preferably 5 to 10 percent of by weight of at least one polymer other than the substantially random inteφolymer (based on the combined weights of this component and the substantially random inteφolymer) which can comprise a homogenous α- olefin homopolymer or inteφolymer comprising polypropylene, propylene/C 4 -C 20 α- olefin copolymers, polyethylene, and ethylene/C 3 -C 20 α- olefin copolymers, the inteφolymers can be either heterogeneous ethylene/α-olefin inteφolymers , preferably a heterogenous ethylene/ C 3 -C 8 α-olefin inteφolymer, most preferably a heterogenous ethylene/ octene-1 inteφolymer or homogeneous ethylene/α-olefm inteφolymers, including the substantially linear ethylene/α-olefin inteφolymers, preferably a substantially linear ethylene/α-olefin inteφolymer, most preferably a substantially linear ethylene/C 3 -C 8 α-olefin inteφolymer; or a heterogenous ethylene/α-olefm inteφolymer; or a thermoplastic olefin, preferably an ethylene/propylene rubber (EPM) or ethylene/propylene diene monomer teφolymer (EPDM) or isotactic polypropylene, most preferably isotactic polypropylene; or a styreneic block copolymer, preferably styrene-butadiene (SB), styrene-isoprene(SI), styrene-butadiene-styrene (SBS), styrene-isoprene-styrene (SIS) or styrene- ethylene/butene-styrene (SEBS) block copolymer, most preferably a styrene- butadiene-styrene (SBS) copolymer; or styrenic homopolymers or copolymers, preferably polystyrene, high impact polystyrene, polyvinyl chloride, copolymers of styrene and at least one of acrylonitrile, meth-acrylonitrile, maleic anhydride, or α- methyl styrene, most preferably polystyrene, or elastomers, preferably polyisoprene, polybutadiene, natural rubbers, ethylene/propylene rubbers, ethylene/propylene diene (EPDM) rubbers, styrene/butadiene rubbers, thermoplastic polyurethanes, most preferably thermoplastic polyurethanes; or thernoset polymers, preferably epoxies, vinyl ester resins, polyurethanes, phonolic resins, most preferably polyurethanes; or vinyl halide homopolymers and copolymers, preferably homopolymers or copolymers of vinyl chloride or vinylidene chloride or the chlorinated derivatives therefrom, most preferably poly (vinyl chloride) and poly (vinylidene chloride); or engineering thermosplastics, preferably poly(methylmethacrylate) (PMMA), cellulosics, nylons, poly(esters), poly(acetals); poly(amides),the poly (ary late), aromatic polyesters, poly(carbonate), poly(butylene) and polybutylene and polyethylene terephthalates, most preferably poly(methylmethacrylate) (PMMA), and poly(esters). The elastic films according to the present invention may be successfully employed for packaging in general and for packaging small items in particular. Other potential applications include, but are not limited to, meat over-wrap, paper replacement, table cloths and shower curtains . The following examples are illustrative of the invention, but are not to be construed as to limiting the scope thereof in any manner. EXAMPLES Test Methods a) Melt Flow and Density Measurements The molecular weight of the polymer compositions for use in the present invention is conveniently indicated using a melt index measurement according to ASTM D-1238, Condition 190°C/2.16 kg (formally known as "Condition (E)" and also known as 12) was determined. Melt index is inversely proportional to the molecular weight of the polymer. Thus, the higher the molecular weight, the lower the melt index, although the relationship is not linear. Also useful for indicating the molecular weight of the substantially random inteφolymers used in the present invention is the Gottfert melt index (G, cmVlO min) which is obtained in a similar fashion as for melt index (I 2 ) using the ASTM D1238 procedure for automated plastometers, with the melt density set to 0.7632, the melt density of polyethylene at 190°C. The relationship of melt density to styrene content for ethylene-styrene inteφolymers was measured, as a function of total styrene content, at 190°C for a range of 29.8 percent to 81.8 percent by weight styrene. Atactic polystyrene levels in these samples was typically 10 percent or less. The influence of the atactic polystyrene was assumed to be minimal because of the low levels. Also, the melt density of atactic polystyrene and the melt densities of the samples with high total styrene are very similar. The method used to determine the melt density employed a Gottfert melt index machine with a melt density parameter set to 0.7632, and the collection of melt strands as a function of time while the 12 weight was in force. The weight and time for each melt strand was recorded and normalized to yield the mass in grams per 10 minutes. The instrument's calculated I2 melt index value was also recorded. The equation used to calculate the actual melt density is δ = δ 07632 x l2 /l2 Gottfert where δ 07632 = 0.7632 and 12 Gottfert - displayed melt index. A linear least squares fit of calculated melt density versus total styrene content leads to an equation with a correlation coefficient of 0.91 for the following equation: δ = 0.00299 x 5 + 0.723 where S = weight percentage of styrene in the polymer. The relationship of total styrene to melt density can be used to determine an actual melt index value, using these equations if the styrene content is known. So for a polymer that is 73 percent total styrene content with a measured melt flow (the "Gottfert number"), the calculation becomes: x=0.00299*73 + 0.723 = 0.9412 where 0.9412/0.7632 = I 2 / G# (measured) = 1.23 The density of the substantially random inteφolymers used in the present invention was determined in accordance with ASTM D-792. b Styrene Analyses Inteφolymer styrene content and atactic polystyrene concentration were determined using proton nuclear magnetic resonance (Η N.M.R). All proton NMR samples were prepared in 1, 1, 2, 2-tetrachloroethane-d 2 (TCE-d 2 ). The resulting solutions were 1.6 - 3.2 percent polymer by weight. Melt index (I 2 ) was used as a guide for determining sample concentration. Thus when the I 2 was greater than 2 g/10 min, 40 mg of inteφolymer was used; with an I 2 between 1.5 and 2 g/10 min, 30 mg of inteφolymer was used; and when the I 2 was less than 1.5 g/10 min, 20 mg of inteφolymer was used. The inteφolymers were weighed directly into 5 mm sample tubes. A 0.75 mL aliquot of TCE-d 2 was added by syringe and the tube was capped with a tight-fitting polyethylene cap. The samples were heated in a water bath at 85°C to soften the inteφolymer. To provide mixing, the capped samples were occasionally brought to reflux using a heat gun. Proton NMR spectra were accumulated on a Varian VXR 300 with the sample probe at 80°C, and referenced to the residual protons of TCE-d 2 at 5.99 ppm. The delay times were varied between 1 second, and data was collected in triplicate on each sample. The following instrumental conditions were used for analysis of the inteφolymer samples: Varian VXR-300, standard Η: Sweep Width, 5000 Hz Acquisition Time, 3.002 sec Pulse Width, 8 μsec Frequency, 300 MHz Delay, 1 sec Transients, 16 The total analysis time per sample was 10 minutes. Initially, a Η NMR spectrum for a sample of the polystyrene, Styron™ 680 (available from and a registered trademark of the Dow Chemical Company, Midland, MI) was acquired with a delay time of one second. The protons were "labeled": b, branch; a, alpha; o, ortho; m, meta; p, para, as shown in Figure 1. Figure 1. Integrals were measured around the protons labeled in Figure 1 ; the 'A' designates aPS. Integral A 7 , (aromatic, around 7.1 ppm) is believed to be the three ortho/para protons; and integral A 66 (aromatic, around 6.6 ppm) the two meta protons. The two aliphatic protons labeled α resonate at 1.5 ppm; and the single proton labeled b is at 1.9 ppm. The aliphatic region was integrated from 0.8 to 2.5 ppm and is referred to as A_. The theoretical ratio for A 7 ,: A 66 : A al is 3: 2: 3, or 1.5: 1 : 1.5, and correlated very well with the observed ratios for Styron™ 680 (available from and a registered trademark of the Dow Chemical Company, Midland, MI for several delay times of 1 second. The ratio calculations used to check the integration and verify peak assignments were performed by dividing the appropriate integral by the integral A 66 Ratio A r is A 7 , / A 66 . Region A 66 was assigned the value of 1. Ratio Al is integral A a , / A 66 . All spectra collected have the expected 1.5: 1: 1.5 integration ratio of (o+p): m: (α+b). The ratio of aromatic to aliphatic protons is 5 to 3. An aliphatic ratio of 2 to 1 is predicted based on the protons labeled α and b respectively in Figure 1. This ratio was also observed when the two aliphatic peaks were integrated separately. For the ethylene/styrene inteφolymers, the Η NMR spectra using a delay time of one second, had integrals C 7 „ C 66 , and C al defined, such that the integration of the peak at 7.1 ppm included all the aromatic protons of the copolymer as well as the o & p protons of aPS. Likewise, integration of the aliphatic region C al in the spectrum of the inteφolymers included aliphatic protons from both the aPS and the inteφolymer with no clear baseline resolved signal from either polymer. The integral of the peak at 6.6 ppm C 66 is resolved from the other aromatic signals and it is believed to be due solely to the aPS homopolymer (probably the meta protons). (The peak assignment for atactic polystyrene at 6.6 ppm (integral A 66 ) was made based upon comparison to the authentic sample Styron™ 680 (available from and a registered trademark of the Dow Chemical Company, Midland, MI)). This is a reasonable assumption since, at very low levels of atactic polystyrene, only a very weak signal is observed here. Therefore, the phenyl protons of the copolymer must not contribute to this signal. With this assumption, integral A 66 becomes the basis for quantitatively determining the aPS content. The following equations were then used to determine the degree of styrene incoφoration in the ethylene/styrene inteφolymer samples: (C Phenyl) = C 7 , + A 7 , - ( 1.5 x A (C Aliphatic) = C a , - ( 1 5 x A 66 ) s c = (C Phenyl) IS e c = (C Aliphatic - (3 x s c )) 14 E = e c / (e c + s c ) S c = s c / (e c + sj and the following equations were used to calculate the mol percent ethylene and styrene in the inteφolymers. and where: s c and e c are styrene and ethylene proton fractions in the inteφolymer, respectively, and S c and E are mole fractions of styrene monomer and ethylene monomer in the inteφolymer, respectively. The weight percent of aPS in the inteφolymers was then determined by the following equation: The total styrene content was also determined by quantitative Fourier Transform Infrared spectroscopy (FTIR). Preparation of ESI Inteφolymers Used in Examples and Comparative Experiments of Present Invention ) Preparation of ESI #'s 1-6 ESI #'s 1 - 6 are substantially random ethylene/styrene inteφolymers prepared using the following catalyst and polymerization procedures. Preparation of Catalyst A ( dimeihvirN-fi -dimethylelfaylVl-1-dimeihyl-l-rf 1.2.3.4.5- η)- 1.5.6.7-tetrahydro-3 -phenyl-s-indacen- 1 -yl] silanaminato(2-)-N] - titanium') 1 ) Preparation of 3 ,5 ,6,7-Tetrahydro-s-Hydrindacen- 1 (2H)-one Indan (94.00 g, 0.7954 moles) and 3-chloropropionyl chloride (100.99 g, 0.7954 moles) were stirred in CH 2 C1 2 (300 mL) at 0°C as A1C1 3 (130.00 g, 0.9750 moles) was added slowly under a nitrogen flow. The mixture was then allowed to stir at room temperature for 2 hours. The volatiles were then removed. The mixture was then cooled to 0°C and concentrated H 2 SO 4 (500 mL) slowly added. The forming solid had to be frequently broken up with a spatula as stirring was lost early in this step. The mixture was then left under nitrogen overnight at room temperature. The mixture was then heated until the temperature readings reached 90°C. These conditions were maintained for a 2 hour period of time during which a spatula was periodically used to stir the mixture. After the reaction period crushed ice was placed in the mixture and moved around. The mixture was then transferred to a beaker and washed intermittently with H 2 O and diethylether and then the fractions filtered and combined. The mixture was washed with H 2 O (2 x 200 mL). The organic layer was then separated and the volatiles removed. The desired product was then isolated via recrystallization from hexane at 0°C as pale yellow crystals (22.36 g, 16.3 percent yield). 1H NMR (CDC1 3 ): d2.04-2.19 (m, 2 H), 2.65 (t, 3 JHH=5.7 HZ, 2 H), 2.84-3.0 (m, 4 H), 3.03 (t, 3 JHH=5.5 HZ, 2 H), 7.26 (s, 1 H), 7.53 (s, 1 H). 13 C NMR (CDC1 3 ): d25.71, 26.01, 32.19, 33.24, 36.93, 118.90, 122.16, 135.88, 144.06, 152.89, 154.36, 206.50. GC-MS: Calculated for C 12 H 12 O 172.09, found 172.05. 2) Preparation of l,2,3,5-Tetrahydro-7-phenyl-s-indacen. 3,5,6,7-Tetrahydro-s-Hydrindacen-l(2H)-one (12.00 g, 0.06967 moles) was stirred in diethylether (200 mL) at 0°C as PhMgBr (0.105 moles, 35.00 mL of 3.0 M solution in diethylether) was added slowly. This mixture was then allowed to stir overnight at room temperature. After the reaction period the mixture was quenched by pouring over ice. The mixture was then acidified (pH=l) with HC1 and stirred vigorously for 2 hours. The organic layer was then separated and washed with H 2 O (2 x 100 mL) and then dried over MgSO 4 . Filtration followed by the removal of the volatiles resulted in the isolation of the desired product as a dark oil (14.68 g, 90.3 percent yield). 'H NMR (CDC1 3 ): d2.0-2.2 (m, 2 H), 2.8-3.1 (m, 4 H), 6.54 (s, 1H), 7.2-7.6 (m, 7 H). GC-MS: Calculated for C lg H 16 232.13, found 232.05. 3) Preparation of 1,2,3, 5-Tetrahydro-7-phenyl-s-indacene, dilithium salt. l,2,3,5-Tetrahydro-7-phenyl-s-indacen (14.68 g, 0.06291 moles) was stirred in hexane (150 mL) as nBuLi (0.080 moles, 40.00 mL of 2.0 M solution in cyclohexane) was slowly added. This mixture was then allowed to stir overnight. After the reaction period the solid was collected via suction filtration as a yellow solid which was washed with hexane, dried under vacuum, and used without further purification or analysis (12.2075 g, 81.1 percent yield). 4) Preparation of Chlorodimethyl(l,5,6,7-tetrahydro-3-phenyl-s-indacen-l-yl)silane. l,2,3,5-Tetrahydro-7-phenyl-s-indacene, dilithium salt (12.2075 g, 0.05102 moles) in THF (50 mL) was added dropwise to a solution of Me 2 SiCl 2 (19.5010 g, 0.1511 moles) in THF (100 mL) at 0°C. This mixture was then allowed to stir at room temperature overnight. After the reaction period the volatiles were removed and the residue extracted and filtered using hexane. The removal of the hexane resulted in the isolation of the desired product as a yellow oil (15.1492 g, 91.1 percent yield). Η NMR (CDC1 3 ): d0.33 (s, 3 H), 0.38 (s, 3 H), 2.20 (p, 3 JHH=7.5 HZ, 2 H), 2.9-3.1 (m, 4 H), 3.84 (s, 1 H), 6.69 (d, 3 JHH=2.8 Hz, 1 H), 7.3-7.6 (m, 7 H), 7.68 (d, 3 JHH=7.4 Hz, 2 H). 13 C NMR (CDC1 3 ): dθ.24, 0.38, 26.28, 33.05, 33.18, 46.13, 116.42, 119.71, 127.51, 128.33, 128.64, 129.56, 136.51, 141.31, 141.86, 142.17, 142.41, 144.62. GC-MS: Calculated for C 20 H 21 ClSi 324.11 , found 324.05. 5) Preparation of N-( 1 , 1 -Dimethylethyl)- 1 , 1 -dimethyl- 1 -( 1 ,5 ,6,7-tetrahydro-3- phenyl-s-indacen- 1 -yl)silanamine. Chlorodimethyl(l,5,6,7-tetrahydro-3-phenyl-s-indacen-l-yl)silane (10.8277 g, 0.03322 moles) was stirred in hexane (150 mL) as NEt 3 (3.5123 g, 0.03471 moles) and t-butylamine (2.6074 g, 0.03565 moles) were added. This mixture was allowed to stir for 24 hours. After the reaction period the mixture was filtered and the volatiles removed resulting in the isolation of the desired product as a thick red-yellow oil (10.6551 g, 88.7 percent yield). Η NMR (CDC1 3 ): d0.02 (s, 3 H), 0.04 (s, 3 H), 1.27 (s, 9 H), 2.16 (p, JHH=7.2 Hz, 2 H), 2.9-3.0 (m, 4 H), 3.68 (s, 1 H), 6.69 (s, 1 H), 7.3-7.5 (m, 4 H), 7.63 (d, 3 JHH=7.4 Hz, 2 H). 13 C NMR (CDC1 3 ): d-0.32, -0.09, 26.28, 33.39, 34.11, 46.46, 47.54, 49.81, 115.80, 119.30, 126.92, 127.89, 128.46, 132.99, 137.30, 140.20, 140.81, 141.64, 142.08, 144.83. 6) Preparation of N-( 1 , 1 -Dimethy lethyl)- 1 , 1 -dimethyl- 1 -( 1 , 5 ,6 ,7-tetrahydro-3 - phenyl-s-indacen-1-yl) silanamine, dilithium salt. N-( 1 , 1 -Dimethylethyl)- 1 , 1 -dimethyl- 1 -( 1 ,5 ,6,7-tetrahydro-3-phenyl-s-indacen- l-yl)silanamine (10.6551 g, 0.02947 moles) was stirred in hexane (100 mL) as nBuLi (0.070 moles, 35.00 mL of 2.0 M solution in cyclohexane) was added slowly. This mixture was then allowed to stir overnight during which time no salts crashed out of the dark red solution. After the reaction period the volatiles were removed and the residue quickly washed with hexane (2 x 50 mL). The dark red residue was then pumped dry and used without further purification or analysis (9.6517 g, 87.7 percent yield). 7) Preparation of Dichloro[N-(l , 1 -dimethylethyl)- 1 , 1 -dimethyl-1 -[(1 ,2,3,4,5-η)- l,5,6,7-tetrahydro-3-phenyl-s-indacen-l-yl]silanaminato(2-)-N]titanium N-( 1 , 1 -Dimethylethyl)- 1 , 1 -dimethyl- 1 -( 1 ,5 ,6,7-tetrahydro-3 -phenyl-s-indacen- l-yl)silanamine, dilithium salt (4.5355 g, 0.01214 moles) in THF (50 mL) was added dropwise to a slurry of TiCl 3 (THF) 3 (4.5005 g, 0.01214 moles) in THF (100 mL). This mixture was allowed to stir for 2 hours. PbCl 2 (1.7136 g, 0.006162 moles) was then added and the mixture allowed to stir for an additional hour. After the reaction period the volatiles were removed and the residue extracted and filtered using toluene. Removal of the toluene resulted in the isolation of a dark residue. This residue was then slurried in hexane and cooled to 0°C. The desired product was then isolated via filtration as a red-brown crystalline solid (2.5280 g, 43.5 percent yield). Η NMR (CDC1 3 ): dθ.71 (s, 3 H), 0.97 (s, 3 H), 1.37 (s, 9 H), 2.0-2.2 (m, 2 H), 2.9- 3.2 (m, 4 H), 6.62 (s, 1 H), 7.35-7.45 (m, 1 H), 7.50 (t, 3 JHH=7.8 HZ, 2 H), 7.57 (s, 1 H), 7.70 (d, 3 JHH=7.1 HZ, 2 H), 7.78 (s, 1 H). ! H NMR (C 6 D 6 ): dθ.44 (s, 3 H), 0.68 (s, 3 H), 1.35 (s, 9 H), 1.6-1.9 (m, 2 H), 2.5-3.9 (m, 4 H), 6.65 (s, 1 H), 7.1-7.2 (m, 1 H), 7.24 (t, 3 JHH=7.1 HZ, 2 H), 7.61 (s, 1 H), 7.69 (s, 1 H), 7.77-7.8 (m, 2 H). 13 C NMR (CDC1 3 ): dl.29, 3.89, 26.47, 32.62, 32.84, 32.92, 63.16, 98.25, 118.70, 121.75, 125.62, 128.46, 128.55, 128.79, 129.01, 134.11, 134.53, 136.04, 146.15, 148.93. 13 C NMR (C 6 D 6 ): dθ.90, 3.57, 26.46, 32.56, 32.78, 62.88, 98.14, 119.19, 121.97, 125.84, 127.15, 128.83, 129.03, 129.55, 134.57, 135.04, 136.41, 136.51, 147.24, 148.96. 8) Preparation of Dimethyl[N-( 1 , 1 -dimethylethyl)- 1 , 1 -dimethyl- 1 -[( 1 ,2,3 ,4,5-η)- l,5,6,7-tetrahydro-3-phenyl-s-indacen-l-yl]silanaminato(2-)-N]titanium Dichloro[N-(l,l-dimethylethyl)-l,l-dimethyl-l-[(l,2,3,4,5-η)-l,5,6,7- tetrahydro-3-phenyl-s-indacen-l-yl]silanaminato(2-)-N]titanium (0.4970 g, 0.001039 moles) was stirred in diethylether (50 mL) as MeMgBr (0.0021 moles, 0.70 mL of 3.0 M solution in diethylether) was added slowly. This mixture was then stirred for 1 hour. After the reaction period the volatiles were removed and the residue extracted and filtered using hexane. Removal of the hexane resulted in the isolation of the desired product as a golden yellow solid (0.4546 g, 66.7 percent yield). *HNMR (C 6 D 6 ): d0.071 (s, 3 H), 0.49 (s, 3 H), 0.70 (s, 3 H), 0.73 (s, 3 H), 1.49 (s, 9 H), 1.7-1.8 (m, 2 H), 2.5-2.8 (m, 4 H), 6.41 (s, 1 H), 7.29 (t, 3 HH=7.4 HZ, 2 H), 7.48 (s, 1 H), 7.72 (d, 3 JHH=7.4 Hz, 2 H), 7.92 (s, 1 H). 13 C NMR (C 6 D 6 ): d2.19, 4.61, 27.12, 32.86, 33.00, 34.73, 58.68, 58.82, 118.62, 121.98, 124.26, 127.32, 128.63, 128.98, 131.23, 134.39, 136.38, 143.19, 144.85. Preparation of Catalyst B;(lH-cyclopenta[l]phenanthrene-2-yl)dimethyl(t- butylamido)-silanetitanium 1 ,4-diphenylbutadiene) 1) Preparation of lithium lH-cvclopenta[l]phenanthrene-2-yl To a 250 ml round bottom flask containing 1.42 g (0.00657 mole) of 1H- cyclopenta[l]phenanthrene and 120 ml of benzene was added dropwise, 4.2 ml of a 1.60 M solution of n-BuLi in mixed hexanes. The solution was allowed to stir overnight. The lithium salt was isolated by filtration, washing twice with 25 ml benzene and drying under vacuum. Isolated yield was 1.426 g (97.7 percent). 1H NMR analysis indicated the predominant isomer was substituted at the 2 position. 2) Preparation of (lH-cvclopenta[l]phenanthrene-2-yl)dimethylchlorosilane To a 500 ml round bottom flask containing 4.16 g (0.0322 mole) of dimethyldichlorosilane (Me 2 SiCl 2 ) and 250 ml of tetrahydrofuran (THF) was added dropwise a solution of 1.45 g (0.0064 mole) of lithium lH-cyclopenta[l]phenanthrene- 2-yl in THF. The solution was stirred for approximately 16 hours, after which the solvent was removed under reduced pressure, leaving an oily solid which was extracted with toluene, filtered through diatomaceous earth filter aid (Celite™), washed twice with toluene and dried under reduced pressure. Isolated yield was 1.98 g (99.5 percent). 3. Preparation of ( 1 H-cvclopenta[11phenanthrene-2-yl)dimethyl(t-butylamino)silane To a 500 ml round bottom flask containing 1.98 g (0.0064 mole) of (1H- cyclopenta[l]phenanthrene-2-yl)dimethylchlorosilane and 250 ml of hexane was added 2.00 ml (0.0160 mole) of t-butylamine. The reaction mixture was allowed to stir for several days, then filtered using diatomaceous earth filter aid (Celite™), washed twice with hexane. The product was isolated by removing residual solvent under reduced pressure. The isolated yield was 1.98 g (88.9 percent). 4. Preparation of dilithio (lH-cvclopenta[11phenanthrene-2-yDdimethyl(t- butylamido silane To a 250 ml round bottom flask containing 1.03 g (0.0030 mole) of (1H- cyclopenta[l]phenanthrene-2-yl)dimethyl(t-butylamino)silane) and 120 ml of benzene was added dropwise 3.90 ml of a solution of 1.6 M n-BuLi in mixed hexanes. The reaction mixture was stirred for approximately 16 hours. The product was isolated by filtration, washed twice with benzene and dried under reduced pressure. Isolated yield was 1.08 g (100 percent). 5. Preparation of ( 1 H-cvclopenta[l]phenanthrene-2-yl)dimethyl(t- butylamido lanetitanium dichloride To a 250 ml round bottom flask containing 1.17 g (0.0030 mole) of TiCl3*3THF and 120 ml of THF was added at a fast drip rate 50 ml of a THF solution of 1.08 g of dilithio (lH-cyclopenta[l]phenanthrene-2-yl)dimethyl(t- butylamido)silane. The mixture was stirred at 20 °C for 1.5 h at which time 0.55 gm (0.002 mole) of solid PbCl2 was added. After stirring for an additional 1.5 h the THF was removed under vacuum and the reside was extracted with toluene, filtered and dried under reduced pressure to give an orange solid. Yield was 1.31 g (93.5 percent). 6. Preparation of ( 1 H-cvclopenta[l]phenanthrene-2-yl)dimethyl(t- butylamido)silanetitanium 1 ,4-diphenylbutadiene To a slurry of (lH-cyclopenta[l]phenanthrene-2-yl)dimethyl(t- butylamido)silanetitanium dichloride (3.48 g, 0.0075 mole) and 1.551 gm (0.0075 mole) of 1 ,4-diphenyllbutadiene in 80 ml of toluene at 70 °C was add 9.9 ml of a 1.6 M solution of n-BuLi (0.0150 mole). The solution immediately darkened. The temperature was increased to bring the mixture to reflux and the mixture was maintained at that temperature for 2 hrs. The mixture was cooled to -20 °C and the volatiles were removed under reduced pressure. The residue was slurried in 60 ml of mixed hexanes at 20 °C for approximately 16 hours. The mixture was cooled to -25 °C for 1 h. The solids were collected on a glass frit by vacuum filtration and dried under reduced pressure. The dried solid was placed in a glass fiber thimble and solid extracted continuously with hexanes using a soxhlet extractor. After 6 h a crystalline solid was observed in the boiling pot. The mixture was cooled to -20 °C, isolated by filtration from the cold mixture and dried under reduced pressure to give 1.62 g of a dark crystalline solid. The filtrate was discarded. The solids in the extractor were stirred and the extraction continued with an additional quantity of mixed hexanes to give an additional 0.46 gm of the desired product as a dark crystalline solid. Preparation of Cocatalyst E, (Bis(hydrogenated-tallowalkyl)methylamine Methylcyclohexane (1200 mL) was placed in a 2L cylindrical flask. While stirring, bis(hydrogenated-tallowalkyl)methylamine (ARMEEN ® M2HT, 104 g, ground to a granular form) was added to the flask and stirred until completely dissolved. Aqueous HC1 (1M, 200 mL) was added to the flask, and the mixture was stirred for 30 minutes. A white precipitate formed immediately. At the end of this time, LiB(C 6 F 5 ) 4 • Et 2 O • 3 LiCl (Mw = 887.3; 177.4 g) was added to the flask. The solution began to turn milky white. The flask was equipped with a 6" Vigreux column topped with a distillation apparatus and the mixture was heated (140 °C external wall temperature). A mixture of ether and methylcyclohexane was distilled from the flask. The two-phase solution was now only slightly hazy. The mixture was allowed to cool to room temperature, and the contents were placed in a 4 L separatory funnel. The aqueous layer was removed and discarded, and the organic layer was washed twice with H 2 O and the aqueous layers again discarded. The H 2 O saturated methylcyclohexane solutions were measured to contain 0.48 wt percent diethyl ether (Et 2 O). The solution (600 mL) was transferred into a 1 L flask, sparged thoroughly with nitrogen, and transferred into the drybox. The solution was passed through a column (1" diameter, 6" height) containing 13X molecular sieves. This reduced the level of Et 2 O from 0.48 wt percent to 0.28 wt percent. The material was then stirred over fresh 13X sieves (20 g) for four hours. The Et 2 O level was then measured to be 0.19 wt percent. The mixture was then stirred overnight, resulting in a further reduction in Et^O level to approximately 40 ppm. The mixture was filtered using a funnel equipped with a glass frit having a pore size of 10-15 μm to give a clear solution (the molecular sieves were rinsed with additional dry methylcyclohexane). The concentration was measured by gravimetric analysis yielding a value of 16.7 wt percent. Polymerization ESI #'s 1 - 6 were prepared in a 6 gallon (22.7 L), oil jacketed, Autoclave continuously stirred tank reactor (CSTR). A magnetically coupled agitator with Lightning A-320 impellers provided the mixing. The reactor ran liquid full at 475 psig (3,275 kPa). Process flow was in at the bottom and out of the top. A heat transfer oil was circulated through the jacket of the reactor to remove some of the heat of reaction. At the exit of the reactor was a micromotion flow meter that measured flow and solution density. All lines on the exit of the reactor were traced with 50 psi (344.7 kPa) steam and insulated. Toluene solvent was supplied to the reactor at 30 psig (207 kPa). The feed to the reactor was measured by a Micro-Motion mass flow meter. A variable speed diaphragm pump controlled the feed rate. At the discharge of the solvent pump, a side stream was taken to provide flush flows for the catalyst injection line (1 lb/hr (0.45 kg/hr)) and the reactor agitator (0.75 lb/hr ( 0.34 kg/ hr)). These flows were measured by differential pressure flow meters and controlled by manual adjustment of micro- flow needle valves. Uninhibited styrene monomer was supplied to the reactor at 30 psig (207 kpa). The feed to the reactor was measured by a Micro-Motion mass flow meter. A variable speed diaphragm pump controlled the feed rate. The styrene stream was mixed with the remaining solvent stream. Ethylene was supplied to the reactor at 600 psig (4,137 kPa). The ethylene stream was measured by a Micro-Motion mass flow meter just prior to the Research valve controlling flow. A Brooks flow meter/controller was used to deliver hydrogen into the ethylene stream at the outlet of the ethylene control valve. The ethylene/hydrogen mixture combines with the solvent styrene stream at ambient temperature. The temperature of the solvent/monomer as it enters the reactor was dropped to ~5 °C by an exchanger with - 5°C glycol on the jacket. This stream entered the bottom of the reactor. The three component catalyst system and its solvent flush also entered the reactor at the bottom but through a different port than the monomer stream. Preparation of the catalyst components took place in an inert atmosphere glove box. The diluted components were put in nitrogen padded cylinders and charged to the catalyst run tanks in the process area. From these run tanks the catalyst was pressured up with piston pumps and the flow was measured with Micro-Motion mass flow meters. These streams combine with each other and the catalyst flush solvent just prior to entry through a single injection line into the reactor. Polymerization was stopped with the addition of catalyst kill (water mixed with solvent) into the reactor product line after the micromotion flow meter measuring the solution density. Other polymer additives can be added with the catalyst kill. A static mixer in the line provided dispersion of the catalyst kill and additives in the reactor effluent stream. This stream next entered post reactor heaters that provide additional energy for the solvent removal flash. This flash occurred as the effluent exited the post reactor heater and the pressure was dropped from 475 psig (3,275 kPa) down to ~250mm of pressure absolute at the reactor pressure control valve. This flashed polymer entered a hot oil jacketed devolatilizer. Approximately 85 percent of the volatiles were removed from the polymer in the devolatilizer. The volatiles exited the top of the devolatilizer. The stream was condensed with a glycol jacketed exchanger and entered the suction of a vacuum pump and was discharged to a glycol jacket solvent and styrene/ethylene separation vessel. Solvent and styrene were removed from the bottom of the vessel and ethylene from the top. The ethylene stream was measured with a Micro-Motion mass flow meter and analyzed for composition. The measurement of vented ethylene plus a calculation of the dissolved gasses in the solvent/styrene stream were used to calculate the ethylene conversion. The polymer separated in the devolatilizer was pumped out with a gear pump to a ZSK-30 devolatilizing vacuum extruder. The dry polymer exits the extruder as a single strand. This strand was cooled as it was pulled through a water bath. The excess water was blown from the strand with air and the strand was chopped into pellets with a strand chopper. The various catalysts, co-catalysts and process conditions used to prepare the various individual ethylene styrene inteφolymers (ESI #'s 1 - 6) are summarized in Table 1 and their properties are summarized in Table 2. *N/A = not available a Catalyst A is dimethyl[N-(l,l-dimethyIethyl)-l,l-dimethyl-l-[(l,2,3,4, 5 -η)-l, 5 , 6 ,7-tetrahydro-3-phenyl-s-indacen-l- yl]silanaminato(2-)-N]- titanium. b Catalyst B is ;(lH-cyclopenta[l]phenanthrene-2-yl)dimethyl(t-butylamido)-silanetitanium 1 ,4-diphenylbutadiene) c Catalyst C is (t-butylamido)dimethyl(tetramethylcyclopentadienyl)silane-titanium (II) 1,3-pentadiene prepared as described in U.S. Patent * 5 , 5 56,928, Example 17 d Cocataiyst D is tris(pentafluorophenyl)borane, (CAS# 001109-15-5),. e Cocataiyst E is bis-hydrogenated tallowal yl methylammonium tetrakis (pentafluorophenyl)borate. f a modified methylaluminoxane commercially available from Akzo Nobel as MMAO-3A (CAS# 146905-79-5) Table 2. Properties of ESI #'s 1-6 *N/A = Not Available Example 1 A sample ESI 1 containing 15.4 mol percent styrene (40.3 wt percent) and having a Gottfert melt index (G#) of 1.4 cm 3 / 10 min was fabricated into film using a 1.25 in diameter extruder with a 12/6/6 24:1 L/D screw operating at a melt temperature of 415 °F. The die was 3" in diameter with a 60 mil die gap. (the extrusion conditions are summarized in Table 3). The film (having a thickness of 1 - 3 mils) was submitted for percent recovery testing as a measure of elastic film properties as described herein. The results are summarized in Table 4 and demonstrate the desired percent recovery of greater than 80 percent in the CD and greater than 60 percent in the MD. Example 2 A sample ESI 2 containing 38.4 mol percent styrene (69.8 wt percent) and having a Gottfert melt index (G#) of 0.9 cm 3 / 10 min was fabricated into film and tested as for Example 1. The results are summarized in Table 4 and demonstrate the desired percent recovery of greater than 80 percent in the CD and greater than 60 percent in the MD. Example 3 A sample ESI 5 containing 26.2 mol percent styrene (56.9 wt percent) and having a Gottfert melt index (G#) of 1.2 cmVlO min was fabricated into film and tested as for Example 1. The results are summarized in Table 4 and demonstrate the desired percent recovery of greater than 80 percent in the CD and greater than 60 percent in the MD. Example 4 A sample ESI 6 containing 17.2 mol percent styrene (43.6 wt percent) and having a Gottfert melt index (G#) of 1.0 cm 3 /l 0 min was fabricated into film and tested as for Example 1. The results are summarized in Table 4 and demonstrate the desired percent recovery of greater than 80 percent in the CD and greater than 60 percent in the MD. Example 5 A sample ESI 4 containing 10.5 mol percent styrene (30.3 wt percent) and having a Gottfert melt index (G#) of 1.6 cm 3 / 10 min was fabricated into film and tested as for Example 1. The results are summarized in Table 4 and demonstrate the desired percent recovery of greater than 80 percent in the CD and greater than 60 percent in the MD. Comparative Experiment 1. A sample ESI 3 containing 43.6 mol percent styrene (74.6 wt percent) and having a Gottfert melt index (G#) of 1.3 cm 3 / 10 min was fabricated into film and tested as for Example 1. The results are summarized in Table 4 and do not demonstrate the desired percent recovery of greater than 80 percent in the CD and greater than 60 percent in the MD. Comparative Experiment 2. This was a film made from Affinity™ PL 1880, a substantially linear ethylene/ 1 -octene inteφolymer available from the Dow Chemical Company, prepared using a metallocene catalyst, and having melt index, I 2 = 1.6 g/10 min, a density = 0.8965 g/cm 3 a an I ]0 /I 2 of 10 and containing 500 ppm Irganox™ 1076 and 800 ppm PEPQ™ and submitted to the percent recovery as described herein. The results are summarized in Table 4 and do not demonstrate the desired percent recovery of greater than 80 percent in the CD and greater than 60 percent in the MD. Comparative Experiment 3 This was a film made from Attane™ 4201, an ethylene/ 1-octene inteφolymer available from the Dow Chemical Company, having melt index, I 2 = 1.0 g/10 min, a density = 0.912 g/cm 3 a an I 10 /I 2 of 8.5 and submitted to the percent recovery tests as described herein. The results are summarized in Table 4 and do not demonstrate the desired percent recovery of greater than 80 percent in the CD and greater than 60 percent in the MD. Table 3. Fabrication Conditions of Films of Example #'s 1 - 5 and Comparative Experiments 1 - 3. Test Methods Elastic Recovery MD (machine direction) sample dimension was 25 mm wide in CD (cross direction) and 127 mm long in MD. Elastic Recovery: CD (cross direction) sample dimension was 25 mm wide in MD (machine direction) and 127 mm long in CD. Thus a sample was pulled on a tensile testing machine with a 50 mm gauge length setting at 250 mm/min to 100 percent of its original length. The sample was then held at that elongation for 30 seconds. The sample was then unloaded at the same speed to the original 50 mm gauge length. After a 60 second hold, sample was pulled again to determine the point at which it exerts a force again. The percent recovery: (average of five measurements) was obtained initially measuring the percent elongation or percent set. This was obtained by measuring the distance to where the second load cycle begins to show a non-zero force reading. This distance was the percent set or percent elongation where; percent elongation = (elongated length-original length)/original length x 100/1. The percent recovery was then calculated as; percent recovery = (100 - percent elongation). The films of the present invention possess good elasticity shown by their having ≥ 80 percent recovery in the CD and > 60 percent recovery in the MD. Table 4. percent Recovery as an Indication of Elastic Film Properties of Examples #'s 1 - 5 and Comparative Experiments 1 - 3 Examples 1 and 4 both show excellent film elasticity with high recovery in both the CD and MD. Examples 2 and 3 also show good elasticity having high recovery in the CD and acceptable recovery in the MD. Example 5 shows acceptable recovery in both the CD and MD. Comparative Example 1 shows poor elasticity and had low recovery in the both the CD and MD due to the high styrene content. Comparative Examples 2 and 3 also shows poor elasticity and a low recovery in the CD and MD. The data in Table 5 demonstrate the good tensile strength and elongation of the elastic films of the present invention and their softness and flexibility as indicated by their low modulus values.

Claims: CLAIMS WHAT IS CLAIMED IS: 1. An elastic film having at least one layer comprising; (A) at least one substantially random inteφolymer, which comprises; (1) polymer units derived from; (i) at least one vinyl aromatic monomer, or (ii) at least one aliphatic or cycloaliphatic vinyl or vinylidene monomer, or (iii) a combination of at least one aromatic vinyl monomer and at least one aliphatic or cycloaliphatic vinyl or vinylidene monomer, and (2) polymer units derived from ethylene or at least one C 3 . 20 α-olefin, or combination thereof; and optionally (3) polymer units derived from one or more ethylenically unsaturated polymerizable monomers other than those of (1) and (2); or (B) a blend of Component A with at least one polymer other than that of Component A; and wherein said elastic film has a recovery in the cross direction of greater than or equal to 80 percent and has a recovery in the machine direction of greater than or equal to 60 percent. 2. The elastic film of Claim 1 wherein; (I) said substantially random inteφolymer, Component A, is present in an amount from 50 to 100 wt percent (based on the combined weights of Components A and said polymer other than that of Component A) and has an I 2 of 0.1 to 1,000 g/10 min and an MJM„ of 1.5 to 20, and comprises; (1) from 10 to 40 mol percent of polymer units derived from; (i) at least one vinyl aromatic monomer, or (ii) at least one aliphatic or cycloaliphatic vinyl or vinylidene monomer, or (iii) a combination of at least one aromatic vinyl monomer and at least one aliphatic or cycloaliphatic vinyl or vinylidene monomer, and (2) from 60 to 90 mol percent of polymer units derived from ethylene or at least one C 3 . 20 α-olefin, or combination thereof; and (3) from 0 to 20 mol percent of polymer units derived from one or more of said ethylenically unsaturated polymerizable monomers other than those derived from (1) and (2); and (II) said polymer other than that of Component A is present in an amount from 0 to 50 wt percent (based on the combined weights of Components A and said polymer other than that of Component A). 3. The elastic film of Claim 1 wherein; (I) said substantially random inteφolymer Component (A) is present in an amount of 75 to 100 wt percent (based on the combined weights of Components A and said polymer other than that of Component A) and has an I 2 of 0.5 to 200 g/10 min and an MJM n of 1.8 to 10; and comprises (1) from 13 to 33 mol percent of polymer units derived from; (i) said vinyl aromatic monomer represented by the following formula; Ar I (CH 2 ) n Ri C = C(R 2 ) 2 wherein R 1 is selected from the group of radicals consisting of hydrogen and alkyl radicals containing three carbons or less, and Ar is a phenyl group or a phenyl group substituted with from 1 to 5 substituents selected from the group consisting of halo, C -alkyl- and C -haloalkyl, and n has a value from zero to 4; or (ii) said aliphatic or cycloaliphatic vinyl or vinylidene monomer is represented by the following general formula; A R l _ C = C(R 2 ) 2 wherein A 1 is a sterically bulky, aliphatic or cycloaliphatic substituent of up to 20 carbons, R 1 is selected from the group of radicals consisting of hydrogen and alkyl radicals containing from 1 to 4 carbon atoms; each R 2 is independently selected from the group of radicals consisting of hydrogen and alkyl radicals containing from 1 to 4 carbon atoms; or alternatively R 1 and A 1 together form a ring system; and (2) from 67 to 87 mol percent of polymer units derived from ethylene or said α-olefin which comprises at least one of propylene, 4- methyl-1-pentene, butene-1, hexene-1 or octene-1; and (3) said ethylenically unsaturated polymerizable monomers other than those derived from (1) and (2) comprises norbornene, or a C 0 alkyl or C 6.10 aryl substituted norbornene; and aid polymer other than that of Component A is present in amount from 0 to 25 wt percent (based on the combined weights of Components A and said polymer other than that of Component A) and comprises one or more of a) a homogeneous inteφolymer; b) a heterogeneous inteφolymer; c) a thermoplastic olefin; d) a styrenic block copolymer; e) a styrenic homo- or copolymer; f) an elastomer; g) a thermoset polymer; h) a vinyl halide polymer; or i) an engineering thermoplastic. tic film of Claim 1 wherein; said substantially random inteφolymer, Component (A), is present in an amount from 90 to 95 wt percent (based on the combined weights of Components A and said polymer other than that of Component A) and has an I 2 of 0.5 to 100 g/10 min and an M w /M n from 2 to 5; and comprises (1) from 15 to 29 mol percent of polymer units derived from; i) said vinyl aromatic monomer which comprises styrene, α- methyl styrene, ortho-, meta-, and para-methylstyrene, and the ring halogenated styrenes, or ii) said aliphatic or cycloaliphatic vinyl or vinylidene monomers which comprises 5-ethylidene-2-norbornene or 1-vinylcyclo-hexene, 3-vinylcyclo-hexene, and 4- vinylcyclohexene; (2) from 71 to 85 mol percent of polymer units derived from ethylene or said α-olefin which comprises at least one of propylene, 4- methyl-1-pentene, butene-1, hexene-1 or octene-1, or combinations thereof; or (3) said ethylenically unsaturated polymerizable monomers other than those derived from (1) and (2) is norbornene; and said polymer other than that of Component A is present in amount from 5 to 10 wt percent (based on the combined weights of Components A and said polymer other than that of Component A) and comprises one or more of; a) a substantially linear ethylene/α-olefin inteφolymer; b) a heterogeneous ethylene/C 3 -C 8 α-olefin inteφolymer; c) an ethylene/propylene rubber (EPM), ethylene/propylene diene monomer teφolymer (EPDM) , isotactic polypropylene; d) a styrene/ethylene-butene copolymer, a styrene/ethylene- propylene copolymer, a styrene/ethylene-butene/styrene (SEBS) copolymer, a styrene/ethylene-propylene/styrene (SEPS) copolymer; e) the acrylonitrile-butadiene-styrene (ABS) polymers, styrene-acrylonitrile (SAN), polystyrene, high impact polystyrene; f) polyisoprene, polybutadiene, natural rubbers, ethylene/propylene rubbers, ethylene/propylene diene (EPDM) rubbers, styrene/butadiene rubbers, thermoplastic polyurethanes; g) epoxies, vinyl ester resins, polyurethanes, phenolic resins; h) homopolymers or copolymers of vinyl chloride or vinylidene chloride; or i) poly(methylmethacrylate), polyester,nylon-6, nylon-6,6, poly(acetal); poly(amide), poly(arylate), poly(carbonate), poly(butylene) and polybutylene, polyethylene terephthalates. 5. The elastic film of Claim 4 wherein Component Al(i) is styrene, Component A2 is ethylene, and said polymer other than that of Component A is polystyrene. 6. The elastic film of Claim 4 wherein Component Al(i) is styrene; and Component A2 is ethylene and at least one of propylene, 4-methyl-l-pentene, butene-1, hexene-1 or octene-1 ; and said polymer other than that of Component A is polystyrene. 7. A fabricated article comprising the elastic film of Claim 1. 8. A fabricated article comprising the elastic film of Claim 5. 9. A fabricated article comprising the elastic film of Claim 6. 10. The fabricated article of Claims 7 - 9 in the form of a tape, bandage, incontinence garment, disposable diaper, disposable and protective clothing and fabrics, a food wrap, meat wrap or a household wrap. 11. A multilayer film comprising at least two layers wherein at least one of said layers has a recovery in the cross direction of greater than or equal to 80 percent and has a recovery in the machine direction of greater than or equal to 60 percent and comprises a polymer composition which comprises; (A) at least one substantially random inteφolymer, which comprises; (1) polymer units derived from; (i) at least one vinyl aromatic monomer, or (ii) at least one aliphatic or cycloaliphatic vinyl or vinylidene monomer, or (iii) a combination of at least one aromatic vinyl monomer and at least one aliphatic or cycloaliphatic vinyl or vinylidene monomer, and (2) polymer units derived from ethylene or at least one C 3 . 20 α-olefin, or combination thereof; and optionally, (3) polymer units derived from one or more ethylenically unsaturated polymerizable monomers other than those of (1) and (2); or (B) at least one polymer other than that of Component A. 12. The multilayer film of Claim 11 wherein; (I) said substantially random inteφolymer, Component A, is present in an amount from 50 to 100 wt percent (based on the combined weights of Components A and said polymer other than that of Component A) and has an I 2 of 0.1 to 1 ,000 g/10 min and an M ^ /M- of 1.5 to 20, and comprises; (1) from 10 to 40 mol percent of polymer units derived from; (i) at least one vinyl aromatic monomer, or (ii) at least one aliphatic or cycloaliphatic vinyl or vinylidene monomer, or (iii) a combination of at least one aromatic vinyl monomer and at least one aliphatic or cycloaliphatic vinyl or vinylidene monomer, and (2) from 60 to 90 mol percent of polymer units derived from at least one C 2.20 α-olefm; or (3) from 0 to 20 mol percent of polymer units derived from one or more of said ethylenically unsaturated polymerizable monomers other than those derived from (1) and (2); and (II) said polymer other than that of Component A is present in an amount from 0 to 50 wt percent (based on the combined weights of Components A and said polymer other than that of Component A). 13. The multilayer film of Claim 11 wherein; (I) said substantially random inteφolymer Component (A) is present in an amount of 75 to 100 wt percent (based on the combined weights of Components A and said polymer other than that of Component A) and has an I 2 of 0.5 to 200 g/10 min and an M w /M n of 1.8 to 10; and comprises (1) from 13 to 33 mol percent of polymer units derived from; (i) said vinyl aromatic monomer represented by the following formula; Ar I (CH 2 ) n R 1 — C = C(R ) 2 wherein R 1 is selected from the group of radicals consisting of hydrogen and alkyl radicals containing three carbons or less, and Ar is a phenyl group or a phenyl group substituted with from 1 to 5 substituents selected from the group consisting of halo, C -alkyl, and C -haloalkyl, and n has a value from zero to 4; or (ii) said aliphatic or cycloaliphatic vinyl or vinylidene monomer is represented by the following general formula; A R 1 - C = C(R 2 ) 2 wherein A 1 is a sterically bulky, aliphatic or cycloaliphatic substituent of up to 20 carbons, R 1 is selected from the group of radicals consisting of hydrogen and alkyl radicals containing from 1 to 4 carbon atoms; each R 2 is independently selected from the group of radicals consisting of hydrogen and alkyl radicals containing from 1 to 4 carbon atoms; or alternatively R 1 and A 1 together form a ring system; and (2) from 67 to 87 mol percent of polymer units derived from said α- olefin which comprises ethylene, or ethylene and at least one of propylene, 4-methyl- 1 -pentene , butene- 1 , hexene- 1 or octene- 1 ; (3) said ethylenically unsaturated polymerizable monomers other than those derived from (1) and (2) comprises norbornene, or a C,. 10 alkyl or C 6 . 10 aryl substituted norbornene; and said polymer other than that of Component A is present in amount from 0 to 25 wt percent (based on the combined weights of Components A and said polymer other than that of Component A) and comprises one or more of a) a homogeneous inteφolymer; b) a heterogeneous inteφolymer; c) a thermoplastic olefin; d) a styrenic block copolymer; e) a styrenic homo- or copolymer; f) an elastomer; g) a thermoset polymer; h) a vinyl halide polymer; or i) an engineering thermoplastic. 14. The multilayer film of Claim 11 wherein; (I) said substantially random inteφolymer, Component (A), is present in an amount from 90 to 95 wt percent (based on the combined weights of Components A and said polymer other than that of Component A) and has an I 2 of 0.5 to 100 g/10 min and an M-^M,, from 2 to 5; and comprises (1) from 15 to 29 mol percent of polymer units derived from; i) said vinyl aromatic monomer which comprises styrene, α- methyl styrene, ortho-, meta-, and para-methylstyrene, and the ring halogenated styrenes, or ii) said aliphatic or cycloaliphatic vinyl or vinylidene monomers which comprises 5-ethylidene-2-norbornene or 1-vinylcyclo-hexene, 3-vinylcyclo-hexene, and 4- vinylcyclohexene; (2) from 71 to 85 mol percent of polymer units derived from said α- olefin, which comprises ethylene, or ethylene and at least one of propylene, 4-methyl-l-pentene, butene-1, hexene-1 or octene-1; or (3) said ethylenically unsaturated polymerizable monomers other than those derived from (1) and (2) is norbornene; and II) said polymer other than that of Component A is present in amount from 5 to 10 wt percent (based on the combined weights of Components A and said polymer other than that of Component A) and comprises one or more of; a) a substantially linear ethylene/α-olefin inteφolymer; b) a heterogeneous ethylene/C 3 -C 8 α-olefin inteφolymer; c) an ethylene/propylene rubber (EPM), ethylene/propylene diene monomer teφolymer (EPDM) , isotactic polypropylene; d) a styrene/ethylene-butene copolymer, a styrene/ethylene- propylene copolymer, a styrene/ethylene-butene/styrene (SEBS) copolymer, a styrene/ethylene-propylene/styrene (SEPS) copolymer; e) the acrylonitrile-butadiene-styrene (ABS) polymers, styrene-acrylonitrile (SAN), polystyrene, high impact polystyrene; f) polyisoprene, polybutadiene, natural rubbers, ethylene/propylene rubbers, ethylene/propylene diene (EPDM) rubbers, styrene/butadiene rubbers, thermoplastic polyurethanes; g) epoxies, vinyl ester resins, polyurethanes, phenolic resins; h) homopolymers or copolymers of vinyl chloride or vinylidene chloride, or i) poly(methylmethacrylate), polyester,nylon-6, nylon-6,6, poly(acetal); poly(amide), poly(arylate), poly(carbonate), poly(butylene) and polybutylene, polyethylene terephthalates. 15. The multilayer film of Claim 14 wherein Component A 1 (i) is styrene, Component A2 is ethylene, and said polymer other than that of Component A is polystyrene. 16. The multilayer film of Claim 14 wherein Component Al(i) is styrene; and Component A2 is ethylene and at least one of propylene, 4-methyl-l-pentene, butene- 1 , hexene- 1 or octene- 1 ; and said polymer other than that of Component A is polystyrene. 17. A fabricated article comprising the multilayer film of Claim 11. 18. A fabricated article comprising the multilayer film of Claim 15. 19. A fabricated article comprising the multilayer film of Claim 16. 20. The fabricated article of Claims 17 - 19 in the form of a tape, bandage, incontinence garment, disposable diaper, disposable and protective clothing and fabrics, a food wrap, meat wrap or a household wrap. 21. The elastic film of Claim 1 wherein Component A is cross-linked. 22. The multilayer film of Claim 11 wherein Component A is cross-linked.

Inventors: CHEUNG YUNWA W, GUEST MARTIN J, VAN VOLKENBURGH WILLIAM R, CHEUNG, YUNWA, W., GUEST, MARTIN, J., VAN VOLKENBURGH, WILLIAM, R.
Applicants: CHEUNG YUNWA W, DOW CHEMICAL CO, GUEST MARTIN J, VOLKENBURGH WILLIAM R VAN, CHEUNG, YUNWA, W., GUEST, MARTIN, J., THE DOW CHEMICAL COMPANY, VAN VOLKENBURGH, WILLIAM, R.
Application year: 1999
Main classification: C08J5
IPC codes: B32B25, B32B27, C08J5, C08L53, C08L101