Process for making tin-coupled rubbery polymers

Abstract: Tire rubbers which are prepared by anionic polymerization are frequently coupled with a suitable coupling agent, such as a tin halide, to improve desired properties. It has been unexpectedly found that greatly improved properties for tire rubbers, such as lower hysteresis, can be attained by asymmetrically coupling the rubber. This invention discloses a process for preparing an asymmetrical tin-coupled rubbery polymer which comprises: (1) continuously polymerizing in a first reactor at least one diene monomer to a conversion of at least about 90 percent, utilizing an anionic initiator to produce a polymer cement containing living polydiene rubber chains; (2) continuously feeding the polymer cement produced in the first reactor into a second reactor; (3) adding a tin halide to the polymer cement in a second reactor under conditions of agitation to produce a polymer cement having the tin halide homogeneously dispersed therein, wherein the residence time in the second reactor is within the range of about 15 minutes to about 4 hours; (4) continuously feeding the polymer cement having the tin halide homogeneously dispersed therein into a plug flow reactor having a residence time of about 15 minutes to about 1 hour to produce a polymer cement of the asymmetrically tin-coupled rubbery polymer; and (5) continuously withdrawing the polymer cement of the asymmetrically tin-coupled rubbery polymer from the plug flow reactor. The asymmetrically tin-coupled rubbery polymer made by this process exhibits improved stability on aging.

Description: Background of the Invention Tin-coupled polymers are known to provide desirable properties, such as improved treadwear and reduced rolling resistance, when used in tire tread rubbers. Such tin-coupled rubbery polymers are typically made by coupling the rubbery polymer with a tin coupling agent at or near the end of the polymerization used in synthesizing the rubbery polymer. In the coupling process, live polymer chain ends react with the tin coupling agent, thereby coupling the polymer. For instance, up to four live chain ends can react with tin tetrahalides, such as tin tetrachloride, thereby coupling the polymer chains together. The coupling efficiency of the tin coupling agent is dependant on many factors, such as the quantity of live chain ends available for coupling and the quantity and type of polar modifier, if any, employed in the polymerization. For instance, tin coupling agents are generally not as effective in the presence of polar modifiers. The amount of coupling which is attained is also, of course, highly dependent upon the quantity of tin coupling agent employed. Each tin tetrahalide molecule is capable of reacting with up to four live polymer chain ends. However, since perfect stoichiometry is difficult to attain, some of the tin halide molecules often react with less than four live polymer chain ends. For instance, if more than a stoichiometric amount of the tin halide coupling agent is employed, then there will be an insufficient quantity of live polymer chain ends to totally react with the tin halide molecules on a four to one basis. On the other hand, if less than a stoichiometric amount of the tin halide coupling agent is added, then there will be an excess of live polymer chain ends and some of the live chain ends will not be coupled. Conventional tin coupling results in the formation of a coupled polymer which is essentially symmetrical. In other words, all of the polymer arms on the coupled polymer are of essentially the same chain length. All of the polymer arms in such conventional tin-coupled polymers are accordingly of essentially the same molecular weight. This results in such conventional tin-coupled polymers having a low polydispersity. For instance, conventional tin-coupled polymers normally having a ratio of weight average molecular weight to number average molecular weight which is within the range of 1.01 to 1.1 FR-A-2 759 703 discloses that greatly improved properties for tire rubbers, such as lower hysteresis, can be attained by asymmetrically coupling the rubber. For instance, such asymmetrically coupled polymers can be utilized in making tires having greatly improved rolling resistance without sacrificing other tire properties. These improved properties are due in part to better interaction and compatibility with carbon black. The asymmetrical tin coupling also normally leads to improve the cold flow characteristics of the rubbery polymer. Tin coupling in general also leads to better processability and other beneficial properties. The asymmetrical tin-coupled rubbery polymers that can be used to improve the performance characteristics of tire tread compounds are comprised of a tin atom having polydiene arms covalently bonded thereto. At least one of the polydiene arms bonded to the tin atom will be a low number molecular weight arm having a number average molecular weight of less than 40,000. It is also critical for the asymmetrical tin-coupled rubbery polymer to have at least one high molecular weight polydiene arm bonded to the tin atom. This high molecular weight arm will have a number average molecular weight which is at least 80,000. The ratio of the weight average molecular weight to the number average molecular weight of the asymmetrical tin-coupled rubbery polymers of this invention will also be within the range of 2 to 2.5. FR-A-2 759 703 further reveals a process for preparing asymmetrical tin-coupled rubbery polymers which comprises: (1) continuously polymerizing at least one diene monomer to a conversion of at least 90 percent, utilizing an anionic initiator to produce a polymer cement containing living polydiene rubber chains, wherein some of the living polydiene rubber chains are low molecular weight polydiene rubber chains having a number average molecular weight of less than 40,000, and wherein some of the living polydiene rubber chains are high molecular weight polydiene rubber chains having a number average molecular weight of greater than 80,000; and (2) continuously adding a tin halide to the polymer cement in a separate reaction vessel to produce the asymmetrically tin-coupled rubbery polymer, wherein said asymmetrical tin-coupled rubbery polymer has a polydispersity which is within the range of 2 to 2.5. According to FR-A-2 759 703, the stability of the asymmetrical tin-coupled rubbery polymers can be improved by adding a tertiary chelating amine thereto, subsequent to the time at which the tin-coupled rubbery polymer is coupled. N,N,N',N'-tetramethylethylenediamine (TMEDA) is a representative example of a tertiary chelating amine which is preferred for utilization in stabilizing such asymmetrical tin-coupled rubbery polymers. However, there is a desire to further improve the stability of such asymmetrical tin-coupled rubbery polymers. Summary of the Invention By utilizing the process of this invention, the stability of asymmetrical tin-coupled rubbery polymers can be greatly improved. This invention more specifically reveals a process for preparing an asymmetrical tin-coupled rubbery polymer having improved stability which comprises: (1) continuously polymerizing in a first reactor at least one diene monomer to a conversion of at least 90 percent, utilizing an anionic initiator to produce a polymer cement containing living polydiene rubber chains; (2) continuously feeding the polymer cement produced in the first reactor into a second reactor; (3) adding a tin halide to the polymer cement in a second reactor under conditions of agitation to produce a polymer cement having the tin halide homogeneously dispersed therein, wherein the residence time in the second reactor is within the range of 15 minutes to 4 hours; (4) continuously feeding the polymer cement having the tin halide homogeneously dispersed therein into a plug flow reactor having a residence time of 15 minutes to 1 hour to produce a polymer cement of the asymmetrically tin-coupled rubbery polymer; and (5) continuously withdrawing the polymer cement of the asymmetrically tin-coupled rubbery polymer from the plug flow reactor. Detailed Description of the Invention Virtually any type of rubbery polymer prepared by anionic polymerization can be asymmetrically tin-coupled in accordance with this invention. The rubbery polymers which can be asymmetrically coupled will typically be synthesized by a solution polymerization technique utilizing an organolithium compound as the initiator. These rubbery polymers will accordingly normally contain a "living" lithium chain end. The polymerizations employed in synthesizing the living rubbery polymers will normally be carried out in a hydrocarbon solvent which can be one or more aromatic, paraffinic or cycloparaffinic compounds. These solvents will normally contain from 4 to 10 carbon atoms per molecule and will be liquid under the conditions of the polymerization. Some representative examples of suitable organic solvents include pentane, isooctane, cyclohexane, methylcyclohexane, isohexane, n-heptane, n-octane, n-hexane, benzene, toluene, xylene, ethylbenzene, diethylbenzene, isobutylbenzene, petroleum ether, kerosene, petroleum spirits, petroleum naphtha, and the like, alone or in admixture. In the solution polymerization, there will normally be from 5 to 30 weight percent monomers in the polymerization medium. Such polymerization media are, of course, comprised of the organic solvent and monomers. In most cases, it will be preferred for the polymerization medium to contain from 10 to 25 weight percent monomers. It is generally more preferred for the polymerization medium to contain 15 to 20 weight percent monomers. The rubbery polymers which are asymmetrically coupled in accordance with this invention can be made by the homopolymerization of a conjugated diolefin monomer or by the copolymerization of a conjugated diolefin monomer with a vinyl aromatic monomer. It is, of course, also possible to make living rubbery polymers which can be asymmetrically tin-coupled by polymerizing a mixture of conjugated diolefin monomers with one or more ethylenically unsaturated monomers, such as vinyl aromatic monomers. The conjugated diolefin monomers which can be utilized in the synthesis of rubbery polymers which can be asymmetrically tin-coupled in accordance with this invention generally contain from 4 to 12 carbon atoms. Those containing from 4 to 8 carbon atoms are generally preferred for commercial purposes. For similar reasons, 1,3-butadiene and isoprene are the most commonly utilized conjugated diolefin monomers. Some additional conjugated diolefin monomers that can be utilized include 2,3-dimethyl-1,3-butadiene, piperylene, 3-butyl-1,3-octadiene, 2-phenyl-1,3-butadiene, and the like, alone or in admixture. Some representative examples of ethylenically unsaturated monomers that can potentially be synthesized into rubbery polymers which can be asymmetrically tin-coupled in accordance with this invention include alkyl acrylates, such as methyl acrylate, ethyl acrylate, butyl acrylate, methyl methacrylate and the like; vinylidene monomers having one or more terminal CH2=CH- groups.; vinyl aromatics such as styrene, α-methylstyrene, bromostyrene, chlorostyrene, fluorostyrene and the like; α-olefins such as ethylene, propylene, 1-butene and the like; vinyl halides, such as vinylbromide, chloroethane (vinylchloride), vinylfluoride, vinyliodide, 1,2-dibromoethene, 1,1-dichloroethene (vinylidene chloride), 1,2-dichloroethene and the like; vinyl esters, such as vinyl acetate; α,β-olefinically unsaturated nitriles, such as acrylonitrile and methacrylonitrile; α,β-olefinically unsaturated amides, such as acrylamide, N-methyl acrylamide, N,N-dimethylacrylamide, methacrylamide and the like. Rubbery polymers which are copolymers of one or more diene monomers with one or more other ethylenically unsaturated monomers will normally contain from 50 weight percent to 99 weight percent conjugated diolefin monomers and from 1 weight percent to 50 weight percent of the other ethylenically unsaturated monomers in addition to the conjugated diolefin monomers. For example, copolymers of conjugated diolefin monomers with vinylaromatic monomers, such as styrene-butadiene rubbers which contain from 50 to 95 weight percent conjugated diolefin monomers and from 5 to 50 weight percent vinylaromatic monomers, are useful in many applications. Vinyl aromatic monomers are probably the most important group of ethylenically unsaturated monomers which are commonly incorporated into polydienes. Such vinyl aromatic monomers are, of course, selected so as to be copolymerizable with the conjugated diolefin monomers being utilized. Generally, any vinyl aromatic monomer which is known to polymerize with organolithium initiators can be used. Such vinyl aromatic monomers typically contain from 8 to 20 carbon atoms. Usually, the vinyl aromatic monomer will contain from 8 to 14 carbon atoms. The most widely used vinyl aromatic monomer is styrene. Some examples of vinyl aromatic monomers that can be utilized include styrene, 1-vinylnaphthalene, 2-vinylnaphthalene, α-methylstyrene, 4-phenylstyrene, 3-methylstyrene and the like. Some representative examples of rubbery polymers which can be asymmetrically tin-coupled in accordance with this invention include polybutadiene, polyisoprene, styrene-butadiene rubber (SBR), α-methylstyrene-butadiene rubber, α-methylstyrene-isoprene rubber, styrene-isoprene-butadiene rubber (SIBR), styrene-isoprene rubber (SIR), isoprene-butadiene rubber (IBR), α-methylstyrene-isoprene-butadiene rubber and α-methylstyrene-styrene-isoprene-butadiene rubber. The polymerizations employed in making the rubbery polymer are initiated by adding an anionic initiator, such as an organolithium initiator, to an organic polymerization medium which contains the monomers. The polymerization is carried out by continuously adding the monomers, the initiator and solvent to a first polymerization reactor with the rubbery polymer synthesized being continuously withdrawn. This polymerization results in the production of living polydiene rubber chains. This polymerization step can be carried out in a single reactor or in a multiple reactor system. The organolithium initiators which can be employed in synthesizing rubbery polymers which can be asymmetrically coupled in accordance with this invention include the monofunctional and multifunctional types known for polymerizing the monomers described herein. The multifunctional organolithium initiators can be either specific organolithium compounds or can be multifunctional types which are not necessarily specific compounds but rather represent reproducible compositions of regulable functionality. The amount of organolithium initiator utilized will vary with the monomers being polymerized and with the molecular weight that is desired for the polymer being synthesized. However, as a general rule, from 0.01 to 1 phm (parts per 100 parts by weight of monomer) of an organolithium initiator will be utilized. In most cases, from 0.01 to 0.1 phm of an organolithium initiator will be utilized with it being preferred to utilize 0.025 to 0.07 phm of the organolithium initiator. The choice of initiator can be governed by the degree of branching and the degree of elasticity desired for the polymer, the nature of the feedstock and the like. With regard to the feedstock employed as the source of conjugated diene, for example, the multifunctional initiator types generally are preferred when a low concentration diene stream is at least a portion of the feedstock, since some components present in the unpurified low concentration diene stream may tend to react with carbon lithium bonds to deactivate initiator activity, thus necessitating the presence of sufficient lithium functionality in the initiator so as to override such effects. The multifunctional initiators which can be used include those prepared by reacting an organomonolithium compounded with a multivinylphosphine or with a multivinylsilane, such a reaction preferably being conducted in an inert diluent such as a hydrocarbon or a mixture of a hydrocarbon and a polar organic compound. The reaction between the multivinylsilane or multivinylphosphine and the organomonolithium compound can result in a precipitate which can be solubilized, if desired, by adding a solubilizing monomer such as a conjugated diene or monovinyl aromatic compound, after reaction of the primary components. Alternatively, the reaction can be conducted in the presence of a minor amount of the solubilizing monomer. The relative amounts of the organomonolithium compound and the multivinylsilane or the multivinylphosphine preferably should be in the range of 0.33 to 4 moles of organomonolithium compound per mole of vinyl groups present in the multivinylsilane or multivinylphosphine employed. It should be noted that such multifunctional initiators are commonly used as mixtures of compounds rather than as specific individual compounds. Exemplary organomonolithium compounds include ethyllithium, isopropyllithium, n-butyllithium, sec-butyllithium, tert-octyllithium, n-eicosyllithium, phenyllithium, 2-naphthyllithium, 4-butylphenyllithium, 4-tolyllithium, 4-phenylbutyllithium, cyclohexyllithium and the like. Exemplary multivinylsilane compounds include tetravinylsilane, methyltrivinylsilane, diethyldivinylsilane, di-n-dodecyldivinylsilane, cyclohexyltrivinylsilane, phenyltrivinylsilane, benzyltrivinylsilane, (3-ethylcyclohexyl) (3-n-butylphenyl)divinylsilane and the like. Exemplary multivinylphosphine compounds include trivinylphosphine, methyldivinylphosphine, dodecyldivinylphosphine, phenyldivinylphosphine, cyclooctyldivinylphosphine and the like. Other multifunctional polymerization initiators can be prepared by utilizing an organomonolithium compound, further together with a multivinylaromatic compound and either a conjugated diene or monovinylaromatic compound or both. These ingredients can be charged initially, usually in the presence of a hydrocarbon or a mixture of a hydrocarbon and a polar organic compound as a diluent. Alternatively, a multifunctional polymerization initiator can be prepared in a two-step process by reacting the organomonolithium compound with a conjugated diene or monovinyl aromatic compound additive and then adding the multivinyl aromatic compound. Any of the conjugated dienes or monovinyl aromatic compounds described can be employed. The ratio of conjugated diene or monovinyl aromatic compound additive employed preferably should be in the range of 2 to 15 moles of polymerizable compound per mole of organolithium compound. The amount of multivinylaromatic compound employed preferably should be in the range of 0.05 to 2 moles per mole of organomonolithium compound. Exemplary multivinyl aromatic compounds include 1,2-divinylbenzene, 1,3-divinylbenzene, 1,4-divinylbenzene, 1,2,4-trivinylbenzene, 1,3-divinylnaphthalene, 1,8-divinylnaphthalene, 1,3,5-trivinylnaphthalene, 2,4-divinylbiphenyl, 3,5,4'-trivinylbiphenyl, m-diisopropenyl benzene, p-diisopropenyl benzene, 1,3-divinyl-4,5,8-tributylnaphthalene and the like. Divinyl aromatic hydrocarbons containing up to 18 carbon atoms per molecule are preferred, particularly divinylbenzene as either the ortho, meta or para isomer and commercial divinylbenzene, which is a mixture of the three isomers, and other compounds, such as the ethylstyrenes, also is quite satisfactory. Other types of multifunctional initiators can be employed such as those prepared by contacting a sec- or tert-organomonolithium compound with 1,3-butadiene, at a ratio of 2 to 4 moles of the organomonolithium compound per mole of the 1,3-butadiene, in the absence of added polar material in this instance, with the contacting preferably being conducted in an inert hydrocarbon diluent, though contacting without the diluent can be employed if desired. Alternatively, specific organolithium compounds can be employed as initiators, if desired, in the preparation of polymers in accordance with the present invention. These can be represented by R(Li)x wherein R represents a hydrocarbyl radical containing from 1 to 20 carbon atoms, and wherein x is an integer of 1 to 4. Exemplary organolithium compounds are methyllithium, isopropyllithium, n-butyllithium, sec-butyllithium, tert-octyllithium, n-decyllithium, phenyllithium, 1-naphthyllithium, 4-butylphenyllithium, p-tolyllithium, 4-phenylbutyllithium, cyclohexyllithium, 4-butylcyclohexyllithium, 4-cyclohexylbutyllithium, dilithiomethane, 1,4-dilithiobutane, 1,10-dilithiodecane, 1,20-dilithioeicosane, 1,4-dilithiocyclohexane, 1,4-dilithio-2-butane, 1,8-dilithio-3-decene, 1,2-dilithio-1,8-diphenyloctane, 1,4-dilithiobenzene, 1,4-dilithionaphthalene, 9,10-dilithioanthracene, 1,2-dilithio-1,2-diphenylethane, 1,3,5-trilithiopentane, 1,5,15-trilithioeicosane, 1,3,5-trilithiocyclohexane, 1,3,5,8-tetralithiodecane, 1,5,10,20-tetralithioeicosane, 1,2,4,6-tetralithiocyclohexane, 4,4'-dilithiobiphenyl and the like. The polymerization temperature utilized can vary over a broad range of from -20°C to 180°C. In most cases, a temperature within the range of 30°C to 125°C will be utilized. It is typically most preferred for the polymerization temperature to be within the range of 60°C to 85°C. The pressure used will normally be sufficient to maintain a substantially liquid phase under the conditions of the polymerization reaction. The polymerization in the first reactor is conducted under conditions of agitation, such as stirring, for a length of time sufficient to permit substantially complete polymerization of monomers. In other words, the polymerization is normally carried out until high conversions are attained. For instance, the monomer conversion attained in the polymerization reactor or reactors will typically be greater than 90 percent. It will typically be preferred for the monomer conversion attained in the first reactor to reach at least 95 percent with conversions in excess of 98 percent being most preferred. The polymerization in the first reactor or series of agitated polymerization reactors results in the formation of a polymer cement containing living polydiene rubber chains. This polymer cement of the rubbery polymer is then continuously fed into a second reactor. A tin halide is also continuously fed into the second reactor. The polymerization is terminated by the continuous addition of a tin coupling agent in the second reactor. The tin coupling agent can be added in a hydrocarbon solution, e.g., in cyclohexane, to the polymerization admixture with suitable mixing for distribution and reaction. The residence time in the second reactor will be within the range of 15 minutes to 4 hour. It is normally preferred for the residence time in the second reactor to be within the range of 30 minutes to 2 hours. It is normally most preferred for the residence time in the second reactor to be within the range of 45 minutes to 90 minutes. The tin coupling agent will normally be a tin tetrahalide, such as tin tetrachloride, tin tetrabromide, tin tetrafluoride or tin tetraiodide. However, tin trihalides can also optionally be used. In cases where tin trihalides are utilized, a coupled polymer having a maximum of three arms results. To induce a higher level of branching, tin tetrahalides are normally preferred. As a general rule, tin tetrachloride is most preferred. Broadly, and exemplary, a range of 0.01 to 4.5 milliequivalents of tin coupling agent is employed per 100 grams of the rubbery polymer. It is normally preferred to utilize 0.01 to 1.5 milliequivalents of the tin coupling agent per 100 grams of polymer to obtain the desired Mooney viscosity. The larger quantities tend to result in production of polymers containing terminally reactive groups or insufficient coupling. One equivalent of tin coupling agent per equivalent of lithium is considered an optimum amount for maximum branching. For instance, if a tin tetrahalide is used as the coupling agent, one mole of the tin tetrahalide would be utilized per four moles of live lithium ends. In cases where a tin trihalide is used as the coupling agent, one mole of the tin trihalide will optimally be utilized for every three moles of live lithium ends. The tin coupling agent can be added in a hydrocarbon solution (e.g., in cyclohexane) to the polymerization admixture in the reactor with suitable mixing for distribution and reaction. The polymer cement having tin halide homogeneously dispersed therein is continuously withdrawn from the second reactor after the desired residence time. It is then continuously fed into a plug flow reactor having a residence time of 15 minutes to 1 hour to produce a polymer cement of the asymmetrically tin-coupled rubbery polymer. The plug flow reactor will preferably have a residence time which is within the range of 20 minutes to 45 minutes and will most preferably have a residence time which is within the range of 25 minutes to 35 minutes. The plug flow reactor is characterized by the flow of fluid through the reactor being orderly with essentially no element of fluid overtaking or mixing with any other element of fluid ahead or behind it. Actually, there may be lateral mixing of fluid in a plug flow reactor; however, there must be essentially no mixing or diffusion along the flow path. The necessary and sufficient condition for plug flow is for the residence time in the reactor to be the same for all elements of fluid passing through it. It should be noted that plug flow reactors are sometimes also known as slug flow reactors, piston flow reactors, ideal tubular reactors or unmixed flow reactors. The polymer cement of the asymmetrically tin-coupled rubbery polymer is, of course, continuously withdrawn from the plug flow reactor. Then, a shortstop and antioxidant is typically added to the polymer cement. A tertiary chelating alkyl 1,2-ethylene diamine can optionally be added to the polymer cement to further stabilize the asymmetrically tin-coupled rubbery polymer. The tertiary chelating amines which can be used are normally chelating alkyl diamines of the structural formula: wherein n represents an integer from 1 to 6, wherein A represents an alkylene group containing from 1 to 6 carbon atoms and wherein R 1 , R 2 , R 3 and R 4 can be the same or different and represent alkyl groups containing from 1 to 6 carbon atoms. The alkylene group A is the formula (CH 2 ) m wherein m is an integer from 1 to 6. The alkylene group will typically contain from 1 to 4 carbon atoms (m will be 1 to 4) and will preferably contain 2 carbon atoms. In most cases, n will be an integer from 1 to 3 with it being preferred for n to be 1. It is preferred for R 1 , R 2 , R 3 and R 4 to represent alkyl groups which contain from 1 to 3 carbon atoms. In most cases, R 1 , R 2 , R 3 and R 4 will represent methyl groups. A sufficient amount of the chelating amine should be added to complex with any residual tin coupling agent remaining after completion of the coupling reaction. In most cases, from 0.01 phr (parts by weight per 100 parts by weight of dry rubber) to 2 phr of the chelating alkyl 1,2-ethylene diamine will be added to the polymer cement to stabilize the rubbery polymer. Typically, from 0.05 phr to 1 phr of the chelating alkyl 1,2-ethylene diamine will be added. More typically, from 0.1 phr to 0.6 phr of the chelating alkyl 1,2-ethylene diamine will be added to the polymer cement to stabilize the rubbery polymer. The asymmetrical tin-coupled rubbery polymer can be recovered from the organic solvent utilizing conventional techniques. For instance, the asymmetrical tin-coupled rubbery polymer can be recovered from the organic solvent and residue by decantation, filtration, centrification and the like. It is often desirable to precipitate the asymmetrically tin-coupled rubbery polymer from the organic solvent by the addition of lower alcohols containing from 1 to 4 carbon atoms to the polymer solution. Suitable lower alcohols for precipitation of the rubber from the polymer cement include methanol, ethanol, isopropyl alcohol, normal-propyl alcohol and t-butyl alcohol. The utilization of lower alcohols to precipitate the asymmetrically tin-coupled rubbery polymer from the polymer cement also "kills" any remaining living polymer by inactivating lithium end groups. After the asymmetrically tin-coupled rubbery polymer is recovered from the solution, steam-stripping can be employed to reduce the level of volatile organic compounds in the asymmetrically tin-coupled rubbery polymer. The asymmetrical tin-coupled rubbery polymers of this invention are comprised of a tin atom having at least three polydiene arms covalently bonded thereto. At least one of the polydiene arms bonded to the tin atom has a number average molecular weight of less than 40,000 and at least one of the polydiene arms bonded to the tin atom has a number average molecular weight of at least 80,000. The ratio of the weight average molecular weight to the number average molecular weight of the asymmetrical tin-coupled rubbery polymer will also be within the range of 2 to 2.5. The asymmetrical tin-coupled rubbery polymers of this invention are of the structural formula: wherein R 1 , R 2 , R 3 and R 4 can be the same or different and are selected from the group consisting of alkyl groups and polydiene arms (polydiene rubber chains), with the proviso that at least three members selected from the group consisting of R 1 , R 2 , R 3 and R 4 are polydiene arms, with the proviso that at least one member selected from the group consisting of R 1 , R 2 , R 3 and R 4 is a low molecular weight polydiene arm having a number average molecular weight of less than 40,000, with the proviso that at least one member selected from the group consisting of R 1 , R 2 , R 3 and R 4 is a high molecular weight polydiene arm having a number average molecular weight of greater than 80,000, and with the proviso that the ratio of the weight average molecular weight to the number average molecular weight of the asymmetrical tin-coupled rubbery polymer is within the range of 2 to 2.5. It should be noted that R 1 , R 2 , R 3 and R 4 can be alkyl groups because it is possible for the tin halide coupling agent to react directly with alkyl lithium compounds which are used as the polymerization initiator. In most cases, four polydiene arms will be covalently bonded to the tin atom in the asymmetrical tin-coupled rubbery polymer. In such cases, R 1 , R 2 , R 3 and R 4 will all be polydiene arms. The asymmetrical tin-coupled rubbery polymer will often contain a polydiene arm of intermediate molecular weight as well as the low molecular weight arm and the high molecular weight arm. Such intermediate molecular weight arms will have a molecular weight which is within the range of 45,000 to 75,000. It is normally preferred for the low molecular polydiene arm to have a molecular weight of less than 30,000 with it being most preferred for the low molecular weight arm to have a molecular weight of less than 25,000. It is normally preferred for the high molecular polydiene arm to have a molecular weight of greater than 90,000 with it being most preferred for the high molecular weight arm to have a molecular weight of greater than 100,000. Benefits with tin-coupled IBRs, as compared to the linear IBRs, are demonstrated by the following examples. These benefits include: (1) Improvements in processability, particularly extrudability/extrudate quality. (2) Treadwear improvement and rolling resistance reduction due to improved carbon black dispersion with the tin-coupled IBR. Good dispersion of carbon black prevents carbon particles from forming a network of carbon black in the vulcanizate and reduces hysteresis resulting from carbon black aggregates. This is known as Payne effect. The higher the Payne effect, the better the carbon black dispersion. The Payne effect can be measured as follows: Payne effect = G' at 10% strain G' at 1% strain x 100 This invention is illustrated by the following examples which are merely for the purpose of illustration and are not to be regarded as limiting the scope of the invention or the manner in which it can be practiced. Unless specifically indicated otherwise, parts and percentages are given by weight. Comparative Example 1 In this example, a coupled isoprene-butadiene rubber (IBR) was prepared in a one-gallon (3.8 liters) batch reactor at 70°C. In the procedure used, 2,000 grams of a silica/molecular sieve/aluminum dried premix containing 19.0 weight percent of a mixture of isoprene and 1,3-butadiene in hexanes at the ratio of 10:90 was charged into a one-gallon (3.8 liters) reactor. After the amount of impurity in the premix was determined, 4.0 ml of a 1.0 M solution of n-butyl lithium (in hexane) was added to the reactor. The target Mn (number averaged molecular weight) was 100,000. The polymerization was allowed to proceed at 70°C for three hours. An analysis of the residual monomer indicated that monomers were all consumed. Then, 1.0 ml of a 1 M solution of tin tetrachloride (in hexane) was added to the reactor and the coupling reaction was carried out at the same temperature for 30 minutes. At this time, 1.5 phr (parts per 100 parts by weight of rubber) of 4-t-butylcatechol and 0.5 phr of TMEDA was added to the reactor to shortstop the polymerization and to stabilize the polymer. After the hexane solvent was evaporated, the resulting SIBR was dried in a vacuum oven at 50°C. The coupled IBR was determined to have a glass transition temperature (Tg) at -95°C. It was also determined to have a microstructure which contained 7 percent 1,2-polybutadiene units, 87 percent 1,4-polybutadiene units, 1 percent 3,4-polyisoprene units and 9 percent 1,4-polyisoprene units. The Mooney viscosity (ML-4) of the coupled IBR made was determined to be 99. Comparative Examples 2-4 The procedure described in Example 1 was utilized in these examples except that the isoprene to 1,3-butadiene ratio were changed from 10:90 to 15:85, 20:80 and 30:70. The Tgs, Mooney viscosities (ML-4) and microstructures of these tin-coupled IBRs are listed in Table I. The 30/70 IBR (Example 4) was determined to have an Mn (number averaged molecular weight) of 386,000 and a Mw (weight averaged molecular weight) of 430,000. The precursor of Example 4 (ie, base polymer prior to coupling) was also determined to have an Mn of 99,000 and an Mw of 112,000. Ex. Isoprene/Bd Composition Tg (°C) ML-4 Microstructure (%) 1,2-PBd 1,4-PBd 3,4-PI 1,4-PI 1 10/90 -95 99 7 83 2 8 2 15/85 -93 91 8 77 1 14 3 20/80 -90 82 8 72 1 19 4 30/70 -87 84 7 63 3 27 Comparative Examples 5-8 In these examples, linear IBRs were prepared in a one-gallon reactor. The procedure described in Example 1 was utilized in these examples except that no coupling agent (tin tetrachloride) was used in these experiments and the target Mn was changed to 300,000 from 100,000. The isoprene to 1,3-butadiene ratios were 10:90, 15:85, 20:80 and 30:70. The Tgs, Mooney viscosities (ML-4), Mns (number averaged molecular weights), Mws (weight averaged molecular weights) and microstructures of these linear IBRs are listed in Table II. Ex. Isoprene/Bd Composition Tg (°C) ML-4 Mn Mw Microstructure (%) 1,2-PBd 1,4-PBd 3,4-PI 1,4-PI 5 10/90 -96 88 308K 326K 7 83 1 9 6 15/85 -94 81 307K 329K 7 77 1 15 7 20/80 -92 82 317K 338K 7 72 1 20 8 30/70 -89 87 313K 332K 6 62 2 30 Comparative Example 9 The tin-coupled IBR prepared in this experiment was synthesized in a three-reactor (10 gallons each) continuous system at 90°C. A premix containing isoprene and 1,3-butadiene in hexane was charged into the first reactor continuously at a rate of 65.6 grams/minute. The premix monomer solution contained a ratio of isoprene to 1,3-butadiene of 30:70 and had a total monomer concentration of 14 percent. Polymerization was initiated by adding 0.128 M solution of n-butyl lithium into the first reactor at a rate of 0.4 grams per minute. Most of the monomers were exhausted at the end of the second reactor and the resulted polymerization medium containing the live ends was continuously pushed into the third reactor where the coupling agent, tin tetrachloride (0.025 M solution in hexane), was added at a rate of 0.34 grams per minute. The residence time for all three reactors was set at 1.5 hours to achieve complete monomer conversion in the second reactor and complete coupling in the third reactor. The polymerization medium was then continuously pushed over to a holding tank containing the TMEDA and an antioxidant. The resulting polymer cement was then steam-stripped and the recovered IBR was dried in an oven at 60°C. The polymer was determined to have a glass transition temperature at -85°C and have a Mooney ML-4 viscosity of 90. It was also determined to have a microstructure which contained 8 percent 1,2-polybutadiene units, 60 percent 1,4-polybutadiene units, 29 percent 1,4-polyisoprene units and 3 percent 3,4-polyisoprene units. The polymer was determined to have a Mn (number averaged molecular weight) of 185,000 and a Mw (weight averaged molecular weight) of 276,000. The precursor of this polymer (i.e., base polymer prior to coupling) was also determined to have an Mn of 88,000 and an Mw of 151,000. Unlike the Example 4 (prepared and coupled in a batch process) which showed a symmetrical coupling of four linear precursor polymers, the polymer produced in this example via the continuous process had unsymmetrical coupling base on GPC molecular data shown above. Comparative Example 10-12 The isoprene-butadiene rubbers made in Example 4, 8 and 9 were then compounded, utilizing a standard tire tread test formulation. The tire tread test formulations were made by mixing 100 parts of rubber being tested with 50 parts of carbon black, 5 parts of processing oil, 2 parts of stearic acid, 3 parts of zinc oxide, 1 part of microcrystalline wax, 0.5 part of paraffin wax, 1 part of a mixed aryl-p-phenylenediamine antioxidant, 2 parts of N-(1,3-dimethyl butyl)-N'-phenyl-p-phenylene diene and 1.4 parts of sulfur. The physical properties of the compounded tire tread formulations are reported in Table III. Example 8 4 9 Rubber Type Linear Batch coupled Continuous coupled Rheometer, 150°C ML,dNm 1.21 1.49 1.67 MH, dNm 24.06 25.71 23.71 ts1, min 4.06 4.86 5.39 T25, min 5.62 5.78 6.50 T90, min 10.36 9.71 9.88 Autovibron, 11 Hz tan delta at 60°C 0.113 0.083 0.072 G' at 10% 2.494 2.294 2.195 G° at 1% 3.435 2.732 2.566 Payne effect 72.6 84.4 85.5 Examples 10-11 and Comparative Examples 12-14 In this series of experiments, living isoprene-butadiene rubber cements were continuously synthesized in a first reactor. The premix monomer solution had a ratio of isoprene to 1,3-butadiene of 30:70 and had a total monomer concentration of 14 percent. Polymerization was initiated by the continuous addition of n-butyl lithium and was carried out at a temperature of 90°C. The living polymer cements and tin tetrachloride were continuously fed into a second reactor. The second reactor provided agitation (stirring) and had an average residence time of 1 hour. Some of the asymmetrically tin-coupled rubbery polymer made in the second reactor was withdrawn directly with a shortstop, antioxidant and a 20 percent molar excess of TMADA (1.2 moles of TMEDA per mole of butyl lithium) being added thereto. In some cases, the polymer cement of asymmetrically tin-coupled rubbery polymer was passed through a plug flow reactor (PFR) having a residence time of 30 minutes before the shortstop, antioxidant and TMEDA was added. The polymer samples were then recovered from the polymer cements and evaluated to determine stability. Table IV shows the loss in Mooney ML(1+4) viscosity that was experienced after the samples were aged in an oven at 150°F (66°C) for various periods of time. The molar ratio of tin tetrachloride to butyl lithium employed in each of these experimental runs is also reported in Table IV. As an additional control, a linear isoprene-butadiene rubber which was not coupled was also evaluated. Example 10 11 12 13 14 PFR Yes Yes No No No Sn/Li 0.2 0.16 - 0.3 0.24 Δ Mooney - 0 days 0.0 0.0 0.0 0.0 0.0 Δ Mooney - 1 day 0.1 -1.3 0.7 -0.6 - Δ Mooney - 5 days 0.1 -1.4 0.8 3.6 3.9 Δ Mooney - 11 days 1.2 1.55 2.8 6.7 8.6 Δ Mooney - 18 days 2.4 3.1 - 10.7 10.1 Δ Mooney - 22 days 3.8 3.6 - 14.1 12.2 As can be seen from Table IV, the asymmetrically tin-coupled polymers made with the plug flow reactor (PFR) in the line had much better stability than did the rubbery samples made without using it. For instance, the rubber samples made with the PFR in the line showed a loss in Mooney ML(1+4) viscosity after 22 days at 150°C (66°C) of only 3.8 and 3.6 as compared to losses of 14.1 and 12.2 for the rubbers made without utilizing the PFR. It should also be noted that the rubbers made with the PFR in the line also showed better stability than the linear control which was not tin-coupled (see Example 12). It should be further noted that no TMEDA was added in making the tin-coupled rubber sample of Example 11. This series of experiments shows that the insertion of a PFR into the continuous line after the second reactor, but before the shortstop is added, greatly improves the stability of the rubber made. It also shows that the inclusion of a PFR in the line may eliminate the need for the addition of a tertiary chelating 1,2-ethylene diamine, such as TMEDA, to attain satisfactory stability. Variations in the present invention are possible in light of the description of it provided herein. While certain representative embodiments and details have been shown for the purpose of illustrating the subject invention, it will be apparent to those skilled in this art that various changes and modifications can be made therein without departing from the scope of the subject invention. It is, therefore, to be understood that changes can be made in the particular embodiments described which will be within the full intended scope of the invention as defined by the following appended claims.

Claims: A process for preparing an asymmetrical tin-coupled rubbery polymer having improved stability which comprises: (1) continuously polymerizing in a first reactor at least one diene monomer to a conversion of at least 90 percent, utilizing an anionic initiator to produce a polymer cement containing living polydiene rubber chains; (2) continuously feeding the polymer cement produced in the first reactor into a second reactor; (3) adding a tin halide to the polymer cement in a second reactor under conditions of agitation to produce a polymer cement having the tin halide homogeneously dispersed therein, wherein the residence time in the second reactor is within the range of 15 minutes to 4 hours; (4) continuously feeding the polymer cement having the tin halide homogeneously dispersed therein into a plug flow reactor having a residence time of 15 minutes to 1 hour to produce a polymer cement of the asymmetrically tin-coupled rubbery polymer; and (5) continuously withdrawing the polymer cement of the asymmetrically tin-coupled rubbery polymer from the plug flow reactor. A process as specified in claim 1 wherein a shortstop and an antioxidant are continuously added to the polymer cement of the asymmetrically tin-coupled rubbery polymer after it is withdrawn from the plug flow reactor. A process as specified in claim 1 or 2 wherein said asymmetrical tin-coupled rubbery polymer has a polydispersity which is within the range of 2 to 2.5. A process as specified in claim 1, 2, or 3 wherein some of the living polydiene rubber chains are low molecular weight polydiene rubber chains having a number average molecular weight of less than 40,000, and wherein some of the living polydiene rubber chains are high molecular weight polydiene rubber chains having a number average molecular weight of greater than 80,000. A process as specified in any of the preceding claims wherein the anionic initiator, the monomer and an organic solvent are continuously fed into the first reactor; wherein the anionic initiator is an organolithium compound; wherein the tin halide is a tin tetrahalide; wherein said process as conducted at a temperature which is within the range of 30°C to 125°C; wherein the residence time in the second reactor is within the range of 30 minutes to 2 hours; and wherein the residence time in the plug flow reactor is within the range of 20 minutes to 45 minutes. A process as specified in any of the preceding claims wherein the tin halide is tin tetrachloride. A process as specified in any of the preceding claims wherein the residence time in the second reactor is within the range of 45 minutes to 90 minutes; wherein the residence time in the plug flow reactor is within the range of 25 minutes to 35 minutes; and wherein the polymer cement further contains intermediate molecular weight living polydiene rubber chains having a number average molecular weight which is within the range of 45,000 to 75,000. A process as specified in any of the preceding claims wherein the low molecular weight polydiene chains have a number average molecular weight of less than 30,000; wherein the high molecular weight polydiene chains have a number average molecular weight of greater than 90,000; wherein the monomer conversion attained in the first reactor is at least 95 percent. A process as specified in any of the preceding claims wherein the asymmetrical tin-coupled rubbery polymer is a styrene-butadiene rubber. A process as specified in any of the preceding claims wherein said process as conducted at a temperature which is within the range of 60°C to 85°C.

Inventors: FIEDLER RONALD DAVID, JOHNSON EDWARD LEE, FIEDLER, RONALD DAVID, JOHNSON, EDWARD LEE
Applicants: GOODYEAR TIRE & RUBBER, THE GOODYEAR TIRE & RUBBER COMPANY
Application year: 1999
Main classification: C08C19
IPC codes: C08C19, C08F36, C08F8