Process for preparing usable products from an impure ferric sulfate solution

Abstract: The invention relates to a process for preparing a usable product, in particular a water treatment solution which contains ferric iron, from an impure ferric sulfate solution which contains as an impurity at least one other metal, the process comprising a first precipitation step in which a base is added to the said impure ferric sulfate solution in order to raise the pH to approx. 2-5, preferably approx. 3-4, whereupon ferric hydroxide precipitates; following the first precipitation step, a second precipitation step in which there are added to the solution an oxidant and a base to raise the pH to approx. 6-10, preferably approx. 8-9, whereupon the said impurity metal precipitates; and one or more separation steps to separate from the sulfate solution the solids precipitated in the first and the second precipitation steps; as well as possibly an additional step in which the said separated solids, or a portion thereof, are treated further in order to form a usable product.

Description: Field of the invention The invention relates to a process for preparing usable products, in particular a water treatment solution which contains ferric iron, from an impure ferric sulfate solution, in particular a ferric sulfate solution formed in the process for preparing hydronium jarosite. State of the art US 3 816 593 discloses a process for regenerating a waste pickling liquor containing as impurity iron-sulfur compounds comprising ferrous sulfate. This process comprises the step (a) of oxidizing said iron-sulfur compounds comprising ferrous sulfate to ferric sulfate, and the step (b) of adding a caustic material to bring the pH to at least 2 to form precipitates comprising ferric hydroxide. Subsequently the precipitates are separated and the generated pickling liquor is returned to pickling service. The applicant's earlier patent application WO 97/38944 discloses a process for preparing a pure product which contains ferric iron. In this process, the initial substance is hydrous ferrous sulfate produced as a byproduct in the process for preparing titanium dioxide. The ferrous sulfate is oxidized with oxygen in a pressurized vessel at an elevated temperature. During the oxidation the ferrous salt dissolves in its own crystal water, and simultaneously hydronium jarosite begins to precipitate. The reaction equation is 5 FeSO 4 x H 2 O + 11/4 O 2 → H 3 OFe 3 (OH) 6 (SO 4 ) 2 (s) + Fe 2 (SO 4 ) 3 During the oxidation step, an equilibrium forms between the ferric sulfate solution and the hydronium jarosite. At this time approximately one-half of the iron is in the solution and the other half is in the form of precipitated hydronium jarosite. The solid jarosite is filtered out, and it is used for the preparation of pure water treatment chemicals. A solution containing ferric sulfate is left. The use of this solution has proved to be problematic, since it forms in a considerable amount in proportion to the amount of hydronium jarosite. Its storage is cumbersome and expensive. There is the additional difficulty that the solution contains most of the impurities of the original ferrous sulfate, in particular manganese. Object of the invention The problem is thus the further treatment of the impure ferric sulfate solution and its potential exploitation. It is therefore an object of the invention to find a method for the exploitation of the impure ferric sulfate solution in such a manner that no materials to be stored and/or eliminated are left from the process for the preparation of hydronium jarosite. It is thus an object to improve the profitability of the process for the preparation of hydronium jarosite. Invention According to the invention, there is provided a process for preparing a product, in particular a water treatment solution which contains ferric iron, from an impure ferric sulfate solution which contains at least one other metal as an impurity,; the process being characterized in that it comprises a first precipitation step, in which a base is added to the said impure ferric sulfate solution in order to raise the pH to 2-5, preferably approx. 3-4, whereupon ferric hydroxide precipitates; following the first precipitation step, a second precipitation step, in which there are added to the solution an oxidant and a base in order to raise the pH to 6-10, preferably approx. 8-9, whereupon the said impurity metal precipitates; and one or more separation steps for separating from the sulfate solution the solids precipitated during the first and the second precipitation steps; and possibly an additional step, in which the said separated solids, or a portion thereof, are treated further in order to form a usable product. In the process according to the invention there is preferably used as the initial substance an impure ferric sulfate solution which is formed as a byproduct of the process for the preparation of hydronium jarosite and which contains as an impurity manganese, which precipitates as manganese oxide in the second precipitation step. Thus the process according to the invention comprises two separate precipitation steps, ferric hydroxide being precipitated in the first precipitation step and the impurity metal, such as manganese dioxide, being precipitated in the second precipitation step. Alongside or in addition to manganese the impurity metal may be, for example, nickel and/or zinc. At the pH concerned, these impurity metals precipitate as hydroxide. According to one embodiment of the invention, the base added to the first precipitation step is added in the form of a solution or an aqueous suspension, which contains in part or entirely the sulfate solution obtained from the separation step. In this manner the amount of water circulating in the process can be regulated and thereby the concentration of the sulfate solution can be affected. The base may be MgO, Mg(OH) 2 , MgCO 3 , NH 3 , NaOH, KOH. In this case the said sulfate solution respectively contains soluble MgSO 4 , (NH 4 ) 2 SO 4 , Na 2 SO 4 or K 2 SO 4 . One usable magnesium-containing base is an aqueous suspension prepared from calcined and ground magnesite. Another option is a suspension which contains magnesium hydroxide. As was pointed out, the suspending can be carried out in water or in the sulfate solution obtained as the final product of the process, or in a suitable mixture of these. Thus there is obtained a basic suspension, which is added to the ferric sulfate solution in order to precipitate iron. The pH of the ferric sulfate solution is originally approx. 1, and in the first precipitation step it is raised to the range of approx. 2-5, preferably approx. 3-4, at which iron precipitates in the form of ferric hydroxide. When magnesium oxide is used as the base in the first precipitation step, there thus occurs the reaction The precipitated ferric hydroxide is in an amorphous state, in which state its solubility in acids is at its best. In the second precipitation step, the pH of the solution is raised to approx. 6-10, preferably approx. 8-9, by adding a base, such as NaOH, KOH, Na 2 CO 3 or NH 3 , to the solution. In addition, an oxidant, such as H 2 O 2 , is added to the solution, whereupon the Mn 2+ oxidizes and precipitates as manganese dioxide. Thus the reaction occurring in the second precipitation step is: Mn 2+ + 2 H 2 O 2 → MnO 2 + 2 H 2 O As the oxidant it is possible to use oxygen oxidants such as hydrogen peroxide, other peroxy compounds, or ozone. In addition it is possible to use chlorine, chlorine dioxide, chlorite, hypochlorite or chlorate. According to one embodiment of the invention, the process comprises a joint separation step, in which the solids formed in both the first and the second precipitation steps are separated together from the sulfate solution. According to another embodiment of the invention, the process comprises a first separation step, in which the solids precipitated in the first precipitation step are separated from the sulfate solution, and a second separation step, in which the solids precipitated in the second precipitation step are separated from the sulfate solution. The solids precipitated in the first and second precipitation steps are preferably separated by filtration, but also other separation methods can be used. The filtrate is a Mg sulfate solution the Mg content of which ranges from 0.5 to 5 %, depending on the composition of the basic suspension of the first step. Such a solution is suitable for use, for example, for the bleaching of cellulose. If the Mg content of the solution is sufficiently high, the magnesium sulfate can be separated from the solution by crystallization. Crystalline magnesium sulfate can be used, for example, as a trace element in fertilizers. The separated solids contain as the principal component a ferric hydroxide precipitate which can be used for preparing an iron chemical suitable for the treatment of waste water. Since ferric hydroxide is a solid product, it can easily be transported to distant places, where it is dissolved in an acid in order to prepare a solution chemical suitable for waste water applications. Nitric acid is especially suitable. Ferric nitrate solutions are suitable for uses in which the water chemical is required to have oxidizing properties, for example, in the deodorization of waste waters which contain hydrogen sulfide. In that embodiment of the process according to the invention which contains a joint separation step, the use of nitric acid is advantageous also for the reason that manganese dioxide present in ferric hydroxide does not readily dissolve in nitric acid. Thus most of the manganese dioxide remains undissolved and settles at the bottom of the container. Thus a solution is obtained which has a lower concentration of manganese. Another option is to remove the undissolved portion by filtration. In addition to nitric acid it is also possible to use hydrochloric acid, sulfuric acid or an organic acid such as formic acid for the dissolving of the ferric hydroxide precipitate. The selection of the acid depends on the purpose for which the iron chemical is needed. For example in treatment use which includes a biologic treatment, ferric hydroxide dissolved in an organic acid would be highly usable, since both the anion and the cation present in the chemical would be exploited in the treatment process. The invention is described below with the help of preparation examples, with reference to the accompanying drawings, in which Figure 1 depicts a block diagram of an embodiment of the process according to the invention and Figure 2 depicts a block diagram of another embodiment of the process according to the invention. Figure 1 depicts one embodiment of the process according to the invention, having first two successive precipitation steps and thereafter one separation step. The solid material obtained in the separation step contains in the main ferric hydroxide, but also manganese dioxide and possibly other impurities. The solid material is used for the preparation of an iron chemical by dissolving it in a suitable acid. The solution obtained from the separation step is a pure solution containing magnesium sulfate. Figure 2 depicts another embodiment of the process according to the invention, having two precipitation steps and two separation steps in such a manner that a separation of solids is carried out after each precipitation step. Ferric hydroxide is separated after the first precipitation step. The ferric hydroxide precipitate thus obtained does not contain impurities and is therefore a highly useful raw material for the preparation of a pure iron chemical. The manganese and other impurities, if any, present in the solution are precipitated in the second precipitation step. They are separated in the second separation step and a waste precipitate is obtained which can be disposed of, for example, by taking it to a dump. What is left is a pure solution containing magnesium sulfate. Example 1 Precipitation of iron The experiments were carried out as continuous-working laboratory-scale processes. The initial solution was obtained from the process for the preparation of hydronium jarosite and its analysis was as follows: Fe 4 %, Fe 2+ 0.08 % and Mn 490 ppm. For the precipitation of iron, a suspension having a Mg concentration of 2.4 % was prepared from a MgO powder and a water solution containing magnesium sulfate. This suspension was added to the solution continuously while maintaining the pH at 3.5, whereupon Fe(OH) 3 precipitated. The reaction vessel was an open reactor equipped with a stirrer and a heating mantle. The temperature was maintained at 40 °C and the retention time was 1 h. A specimen taken from the reactor was filtered, and the filtrate was analyzed: Mg 1.9 %, Mn 311 ppm, Ni 1.9 ppm, Fe 2+ < 0.01 %. The filter cake was dried and analyzed: Fe 47.4 %, Mg 1.5 %, state amorphous. The concentration of manganese in the precipitate was not analyzed, but a calculation showed that all of the Mn had passed into the filtrate. The experiments carried out showed that the lower the temperature of the precipitation step, the higher the reactivity of the hydroxide precipitate obtained. The suitable temperature range was 20-40 °C and the most preferable range was 20-30 °C. Example 2 Precipitation of manganese To the suspension of Example 1, NaOH (25 % solution) and H 2 O 2 (10 % solution) were added in order to precipitate the manganese. The base was fed deep under the surface of the solution, whereas the hydrogen peroxide was added directly to the surface. The pH was adjusted to 8-9. The retention time was approx. 1 h and the temperature was 40 °C. After the second precipitation step the solids were separated from the suspension by using a laboratory filter, and the filtrate was analyzed: Mg 1.1 %, Mn < 0.3 ppm, pH 9.15. The filtrate had thus been purified of impurities. Example 3 Dissolving of iron precipitate The following experiment was carried out to dissolve the ferric hydroxide precipitate obtained above. Water (30.3 g), ferric hydroxide precipitate (115.7 g, solids content 66 %) and nitric acid (172 g, concentration 65 %) were placed in a laboratory vessel. Owing to an exothermal reaction, the temperature rose to 50 °C, from which it was raised further to approx. 80 °C by heating the vessel. After approx. 15 min almost all of the ferric hydroxide had dissolved, and free acid remained in an amount of only 1.1 %. The dissolving was, however, continued until the total dissolving time was 2 h. The solution was analyzed: Fe 7.8 %, Mg 2.6 %, Mn 530 ppm, Ni 13 ppm, N 8 % (NO 3 35.4 %), free HNO 3 0.4 %, undissolved 0.13 %. The undissolved material was analyzed semi-quantitatively by X-ray fluorescence: Fe was the principal component, Mg and Mn were present in an amount of approx. 5-10 %. This shows that the iron precipitate dissolved well in nitric acid.

Claims: A process for the preparation of a product, in particular a water treatment solution which contains ferric iron, from an impure ferric sulfate solution which contains at least one other metal as an impurity, characterized in that the process comprises a first precipitation step, in which a base is added to the said impure ferric sulfate solution in order to raise the pH to 2-5, preferably approx. 3-4, whereupon ferric hydroxide precipitates; following the first precipitation step, a second precipitation step, in which there are added to the solution an oxidant and a base to raise the pH to 6-10, preferably approx. 8-9, whereupon the said impurity metal precipitates; and one or more separation steps for separating from the sulfate solution the solids precipitated in the first and second precipitation steps; and possibly an additional step, in which the said separated solids, or a portion thereof, are treated further in order to form a usable product. A process according to Claim 1, characterized in that the impure ferric sulfate solution is a byproduct formed in the process for the preparation of hydronium jarosite. A process according to Claim 1 or 2, characterized in that the said impurity metal is manganese, which precipitates as manganese dioxide in the second precipitation step. A process according to any of the above claims, characterized in that the base added to the first precipitation step is magnesium oxide, magnesium hydroxide or magnesium carbonate, ammonia, sodium hydroxide or potassium hydroxide. A process according to any of the above claims, characterized in that the oxidant added to the second precipitation step is an oxygen oxidant such as hydrogen peroxide, some other peroxy compound or ozone; chlorine, chlorine dioxide, chlorite, hypochlorite, or chlorate. A process according to any of the above claims, characterized in that the base added to the second precipitation step is sodium hydroxide, potassium hydroxide, sodium carbonate or ammonia. A process according to any of the above claims, characterized in that it comprises a joint separation step in which the solids precipitated during both the first and the second precipitation steps are separated together from the sulfate solution. A process according to any of Claims 1-6, characterized in that it comprises a first separation step in which the solids precipitated in the first precipitation step are separated from the sulfate solution and a second separation step in which the solids precipitated in the second separation step are separated from the sulfate solution. A process according to any of the above claims, characterized in that in the separation step or steps the solids are separated from the sulfate solution by filtration. A process according to any of Claims 7-9, characterized in that the sulfate solution obtained from the joint separation step or the second separation step is recycled in part or entirely to the first precipitation step. A process according to Claim 7, characterized in that the process comprises an additional step, in which the solids obtained from the joint separation step, containing ferric hydroxide and the impurity metal such as manganese dioxide, are dissolved in an acid in order to form a water treatment solution which contains ferric iron, the impurity metal such as manganese dioxide remaining undissolved. A process according to Claim 11, characterized in that the water treatment solution which contains ferric iron is separated from the undissolved material. A process according to Claim 8, characterized in that the process comprises an additional step in which the solids obtained from the first separation step, containing ferric hydroxide, are dissolved in an acid in order to form a water treatment solution which contains ferric iron. A process according to Claim 11-13, characterized in that the acid is nitric acid, in which case the formed water treatment solution is a solution of ferric nitrate.

Inventors: JAEFVERSTROEM STEFAN, JOKININ SIMO, KENAKKALA TIMO, JAEFVERSTROEM, STEFAN, JOKININ, SIMO, KENAKKALA, TIMO, JÄFVERSTRÖM, Stefan
Applicants: KEMIRA CHEMICALS OY
Application year: 1999
Main classification: C01G49
IPC codes: C01G49, C02F1