POLYMER VALVE LEAFLETS WITH MOLDED FREE EDGES

Abstract: A valve (10) and a method for manufacturing the valve, the valve (10) including an elastic valve body (12) and leaflet (14) coupled to the valve body. The leaflet has a free edge (18) that is molded.

Description: Polymer Valve Leaflets With Molded Free Edges Description Background Art The present invention pertains to valves and in particular to tri-leaflet heart valve prostheses. Ever since 1950, when blood oxygenators made open heart surgery feasible, it has been possible to treat some forms of heart disease by replacing one of the patient's heart valves with a prosthetic valve. Early heart valve prostheses included ball-and-cage valves and disc-and-cage valves in which a ball or a disc was housed in a cage. One side of the cage provided an orifice through which blood flowed either into or out of the heart, depending on the valve being replaced. When blood flowed in a forward direction, the energy of the blood flow forced the ball or disc to the back of the cage allowing blood to flow through the valve. When blood attempted to flow in a reverse direction, or "regurgitate", the energy of the blood flow forced the ball or disc into the orifice in the valve and blocked the flow of blood. A bi-leaflet valve comprised an annular valve body in which two opposed leaflet occluders were pivotally mounted. The occluders were substantially rigid and moved between a closed position, in which the two leaflets were mated and blocked blood flow in the reverse direction, and an open position, in which the occluders were pivoted away from each other and did not block blood flow in the forward direction. The energy of blood flow caused the occluders to move between their open and closed positions. A tri-leaflet valve comprised an annular elastic valve body in which three flexible leaflets were mounted to a portion of the valve body, called a "stent," located at the circumference of the annulus. Some tri-leaflet valves used rigid leaflets. When blood flowed in the forward direction, the energy of the blood flow deflected the three leaflets away from the center of the annulus and allowed blood to flow through. When blood flowed in the reverse direction, the three leaflets engaged each other in a coaptive region, occluded the valve body annulus and prevented the flow of blood. The valve leaflets were made from tissue, such as specially treated porcine or bovine pericardial tissue, or from a man-made material such as polyurethane or another biocompatible polymer. Durability is a desirable characteristic of prosthetic heart valves, including tri-leaflet heart valves, because replacing such a valve is both expensive and dangerous for the patient. Another desirable characteristic of a prosthetic heart valve design is a reduction in thrombus accumulation on the valve. Disclosure of Invention The invention improves the durability of elastic heart valves by having molded, rather than cut, free edges. This removes the requirement to cut the free edge during the manufacturing process which reduces the likelihood that cracks will develop in the free edge and subsequently cause the valve to fail. Further, by removing the requirement to cut the free edge, the chance of thrombus accumulation on the valve is reduced. In one aspect, the invention features a valve comprising an elastic valve body, a leaflet having an attachment edge and a free edge, the leaflet being coupled to the valve body on the attachment edge and the free edge of the leaflet having an uncut edge. Implementations of the invention may include one or more of the following. The valve may further comprise a mold separation point on an inflow face of the leaflet away from the free edge. The free edge may have a full radius. The free edge may comprise a filleted edge. In another aspect, the invention features an elastic valve body, a leaflet having an attachment edge and a free edge, the leaflet being coupled to the valve body on the attachment edge, and the free edge being molded. Implementations of the invention may include one or more of the following. The mold separation point may be on an inflow face of the leaflet. The mold separation point may be on the free edge. The mold separation point may be on an outflow face of the leaflet. The leaflet may be molded in a partially open position. The leaflet may be molded in a fully open position. In another aspect, the invention features a method of manufacturing a valve comprising forming an elastic valve body and a leaflet integral with the valve body, the leaflet having a free edge, the free edge having an uncut edge. Implementations of the invention may include one or more of the following. Forming may comprise compression molding, injection molding or dip casting. The method may further comprise cutting an opening in the valve, the cutting occurring away from the free edge. Forming may comprise molding the leaflet in a partially open position. Forming may comprise molding the leaflet in a fully open position. Brief Description of Drawings Fig. 1 is a plan view of a polymer valve. Fig. 2 is a top view of the polymer valve of Fig. 1. Fig 3 is a plan view of a polymer valve. Fig 4 is a top view of the polymer valve of Fig. 3. Fig. 5 is a section view of a prior art mold. Fig. 6 is a section view of a prior art valve. Fig. 7 is a section view of a mold according to the present invention. Fig. 8 is a section view of a mold according to the present invention. Fig. 9 is a section view of a mold according to the present invention. Fig. 10 is a section view of a mold according to the present invention. Fig. 11 is a section view of a leaflet according to the present invention. Fig. 12 is a section view of a leaflet according to the present invention. Best Mode for Carrying Out the Invention A tri-leaflet heart valve prosthesis 10 comprises an annular elastic valve body 12 and three flexible leaflets 14 made of a biocompatible polymer such as silicone or polyurethane, as shown in Fig. 1. Each leaflet has an attachment edge by which it is coupled to the valve body along an attachment curve 16. Each leaflet has a free edge 18 that is not coupled to the valve body. A sewing ring 20 is coupled to the base of the valve body 12 and provides a place for sutures to be applied when the valve is implanted. The valve body comprises an annular base 22 and a leaflet support, comprising three shaped posts 24, that supports the leaflets 14. When fluid flow is in the forward direction, i.e. in the direction of the arrow shown in Fig. 1 , the pressure of the blood flow causes the leaflets 14 to deflect away from a central longitudinal axis 26 of the valve body that is generally parallel to the three posts 24. In this "open" position, the leaflets 14 define a large flow orifice, as shown in Fig. 2. With the leaflets in the open position shown in Figs. 1 and 2, the valve presents little resistance to fluid flow. When the pressure of blood flow is insufficient to overcome the elastic force biasing the valve toward a closed or partially closed position, the leaflets deflect toward axis 26, as shown in Figs. 3 and 4. In this "closed" position, each leaflet would occlude more than one-third of the valve body's orifice were it not for the presence of the other leaflets. Consequently, when the three leaflets deflect toward axis 26, they engage each other and form coaptive areas along the free edges 18, which help the valve seal against reverse flow. Further, when the leaflets press together, each leaflet forms a "triple point" 28 at the point where the three leaflets come together, as shown in Fig. 4. The place where the leaflets 14 come together adjacent the posts 24 is called the "commissure" 30, as shown in Fig. 3. The first efforts at developing a heart valve for orthotopic implantation began in the early 1950s with single flap valves that were usually made from a cloth that was encapsulated by silicone rubber or polyurethane. These devices were implanted into animals and humans, without the benefit of invitro testing, by passing sutures or pins through the body of the valve and the heart tissue where they were joined. Such heart valves invariably failed from structural degradation. Often the failure point emanated from the sutures or pins used to attach the leaflets. To avoid this mode of failure, complete valves were constructed so the sutures did not pass directly through the leaflets where they were bending with every cardiac cycle. Many of these complete valves were constructed by dip casting polyurethane or silicone on a dip casting mold that modeled the inflow surfaces of the valve. The inflow mold 32 was constructed so that the free edges 18 were molded together, as shown in Fig. 5. After the valve was separated from the mold, as shown in Fig. 6, the free edges of the valve were cut with a blade 34 to separate them. When these valves were taken to the point of structural failure, the failure typically emanated from the free edge 18 of the leaflet 14 where the leaflets 14 had been separated by the blade 34. In another prior art approach to manufacturing tri-leaflet valves, the valves were compression molded of silicone with the metal stent fully encapsulated, but the leaflets were molded in the closed position and were cut apart to separate the free edges. In another prior art approach, silicone valves were compression molded without a stent with the leaflets molded in the closed position and then cut open. Valves manufactured using these two techniques suffered from structural failure with cracks emanating from the cut free edge. In another prior art manufacturing technique, the valves were dip cast with the leaflets being in the partially open position. Again, however, the free edges of the leaflets were cut with a blade to separate them after molding. Accelerated invitro testing and post mortem analysis of elastic valves constructed to allow opening and closing of the valve through elastic deformation have shown that failure emanates from the areas that combine high stresses, abrasive wear and cut edges. The free edges of such a valve encounter high stresses because of the movement and flexing associated with opening and closing as well as the stresses borne by the leaflets when fully open or fully closed. Further, as discussed above, in the prior art the free edges were separated by cutting the molded valve with a blade, leaving a rough and structurally damaged edge. These conditions increase the likelihood that the valve will fail at the free edges. The invention comprises an elastic valve without cut edges or discontinuities in the structure of the valve in the areas of high stress. In particular, the invention is an elastic valve in which the free edges are molded rather than cut. Valves according to the invention will have improved durability because the sources of initial cracks have been removed from the design. In valves according to the invention, the rough areas that can promote the accumulation of thrombus are away from the flow separation areas. An outflow mold 36, shown in Fig. 7, has a recess 38, which is designed in the shape of a leaflet free edge 18 and the portion of the leaflet 14 adjacent the free edge 18. An inflow mold 40 is shaped so that when it is mated with the outflow mold 36, as shown in Fig. 7, a recess 42 will form in the shape of a valve with a leaflet 14 in a partially closed position. Alternatively, the molds could be shaped so that the recess would be in the shape of a leaflet in a fully closed position. A mold separation point 44 is preferably located on an inflow side 46 of the leaflet away from free edge 18. This is the preferred location because the mold separation point usually results in a discontinuity on the material surface, for example at point 48, which is better located on the inflow face of the valve where the velocity of blood is fairly high and the accumulation of thrombus is unlikely. Alternatively, a mold separation point 50 between outflow mold 52 and inflow mold 54 could be located on an outflow side 56 of the leaflet 14 away from free edge 18, as shown in Fig. 8. Alternatively, a mold separation point 58 between an inflow mold 60 and an outflow mold 62 could be located on the free edge 18 of the leaflet, as shown in Fig. 9. A valve formed with such molds would have improved durability as compared to prior art valves. The valve can be compression molded or injection molded using the molds illustrated in Figs. 7, 8 and 9. An outflow mold 64, illustrated in Fig. 10, could also be dipped into polymer material to form a valve. A dip cast valve formed in such a manner would require trimming at point 66, but the cut would be away from the free edge 18 which would allow the free edge 18 to have a full radius and be less susceptible to failure than a valve with a cut free edge 18. Dip cast valves would have to be molded in the open position, as shown in Fig. 10, to allow the cut edge to be away from the molded edge. The molded free edge 18 of a leaflet 14 can have a full radius R = t/2, where t is the thickness of the leaflet, as shown in Fig. 11. Preferably, the molded free edge 18 of the leaflet 14 will include a generally flat region 68 linked to the two faces 70 of the leaflet 14 by filleted edges 72. Each filleted edge has a radius R < t/2, where t is the thickness of the leaflet. The foregoing describes preferred embodiments of the invention and is given by way of example only. The invention is not limited to any of the specific features described herein, but includes all variations thereof within the scope of the appended claims.

Claims: WHAT IS CLAIMED IS: 1. A valve (10) comprising an elastic valve body (12); a leaflet (14) having an attachment edge and a free edge (18), the leaflet (14) being coupled to the valve body (12) on the attachment edge; and characterized by the free edge (18) of the leaflet having an uncut edge. 2. The valve of claim 1 further comprising a mold separation point on (44) an inflow face (46) of the leaflet (14) away from the free edge (18). 3. The valve of claim 1 wherein the free edge (18) has a full radius. 4. The valve of claim 1 wherein the free edge (18) comprises a filleted edge(72). 5. A valve (10) comprising an elastic valve body (12); a leaflet (14) having an attachment edge and a free edge (18), the leaflet (14) being coupled to the valve body (12) on the attachment edge; and characterized by the free edge (18) being molded. 6. The valve of claim 5 further comprising a mold separation point (44) on an inflow face (46) of the leaflet (14). 7. The valve of claim 5 further comprising a mold separation point (58) on the free edge (18). 8. The valve of claim 5 further comprising a mold separation point (50) on the outflow face (56) of the leaflet (14). 9. The valve of claim 5 further comprising the leaflet (14) being molded in a partially open position. 10. The valve of claim 5 further comprising the leaflet (14) being molded in a fully open position. 11. A method of manufacturing a valve (10) comprising forming an elastic valve body (12) and a leaflet (14) integral with the valve body (12); characterized by the leaflet (14) having a free edge (18), the free edge (18) having an uncut edge. 12. The method of claim 11 wherein forming comprises compression molding. 13. The method of claim 11 wherein forming comprises injection molding. 14. The method of claim 11 wherein forming comprises dip casting. 15. The method of claim 14 further comprising cutting an opening in the valve (10), the cutting occurring away from the free edge (18). 16. The method of claim 11 wherein forming comprises molding the leaflet (14) in a partially open position. 17. The method of claim 11 wherein forming comprises molding the leaflet (14) in a fully open position.

Inventors: CAMPBELL LOUIS A, MOE RIYAD, SARNOWSKI EDWARD J, CAMPBELL, LOUIS, A., MOE, RIYAD, SARNOWSKI, EDWARD, J.
Applicants: SULZER CARBOMEDICS INC, SULZER CARBOMEDICS INC.
Application year: 1999
Main classification: A61F2
IPC codes: A61F2