PRIMER FOR PVC-PLASTISOL

Abstract: A carboxy- and hydroxy-functional acrylic polymer cross-linked with a polyisocyanate and an amino resin is used as primer for PVC-plastisol. Preferred amino resins are melamine resins, and preferred melamine resins contain imino groups and are alkylated. The primer is particularly useful for steel substrates, more particularly in coil coating.

Description: PRIMER FOR PVC-PLASTISOL The present invention relates to a primer for polyvinylchloride (PNC)-plastisol. More particularly, it relates to a primer for PVC-plastisol on a steel substrate. One of the most successful products in coil coating is steel coated with PNC-plastisol. Other applications include the coating of steel cord. Steel as used herein comprises steel, surface-treated steel (such as phosphated steel) and galvanised steel (such as hot dipped galvanised steel). PNC-plastisol is a top coating of plastified PNC. It has however practically no adherence to steel. A primer is thus required, which must provide • adhesion to the steel substrate; • corrosion protection for the steel substrate; and • intercoat adhesion between the primer and the PVC-plastisol. Those properties must be resistant to weathering (particularly exposure to UN light and/or cold temperatures) and/or mechanical deformation. Acrylate primers are used today as primers for PNC-plastisol; they are based on (co)polymers of alkyl (meth)acrylate(s). Whilst such primers provide good intercoat adhesion and reasonably good adhesion to the steel substrates, they have an insufficient resistance. Typically, adhesion to the steel substrate deteriorates strongly after about 500 hours of QUN B exposure (a definition of QUV B exposure appears in the examples). There is thus a need in the art for a primer for PVC-plastisol on a steel substrate that would provide a more resistant coated system. The term "coated system" is used herein to describe the composite system < consisting of the substrate, the primer and the PVC-plastisol topcoat. The Applicant has previously proposed to use a primer based on a carboxy- and hydroxy-functional acrylic polymer, cross-linked with a polyisocyanate, which was thought to provide excellent properties and 10 resistance. It was later found that those properties though indeed excellent, were greatly dependent on the heating conditions; more particularly, it was found that when the peak metal temperature (PMT) was either slightly lower or reached but for a slightly shorter period of time, the properties were negatively affected. The Applicant has now surprisingly found that a primer based on a carboxy- and hydroxy-functional acrylic polymer, cross-linked with a polyisocyanate and an amino resin, provides excellent properties and resistance. ?0 The primer of the invention is particularly useful for steel substrates to which it both adheres excellently and provides excellent anti-corrosion protection. It is more particularly useful in coil coating, where it has additional (mainly economical) benefits. 2" The primer of the invention is based on a carboxy- and hydroxy-functional acrylic polymer. The term "acrylic polymer" as used herein represents any (co)polymer of alkyl (meth) acrylate (s) and mixtures thereof, with alkyl groups up to C ^Q- The carboxy- 30 functionality is provided by using the desired amount of one or more carboxy-functional (meth) acrylic monomers in the preparation of the acrylic polymer. The hydroxy-functionality is similarly provided by using the desired amount of one or more hydroxy-functional (meth) acrylic monomers in the preparation of the acrylic polymer. Monomer selection for obtaining the desired properties is known in the art and need not be described herein. Exemplary textbook references are: • chapter 8 at pages 95- 1 13 in "Protective Coatings" by Clive H. Hare, Technology Publishing Company, Pittsburgh, PA, 1994; • chapter 15 at pages 144- 157 in "Surface Coatings", vol. I, O.C.C.A, Chapman and Hall, London, 1983; • "Waterborne and Solvent Based Acrylics and their End User Applications", Oldring and Lam ed. , SITA Technology, 1996. The hydroxy- and carboxy-functional acrylic polymer should have the following properties: a) a hydroxyl number of 5 to 40 mg KOH/g, preferably of 10 to less than 20 mg KOH/g, more preferably of 10 to 15 mg KOH/g, most preferably of about 10 mg KOH/g; b) an acid number of 2 to 20 mg KOH/g, preferably of 5 to 10 mg KOH/g; c) a glass transition temperature (Tg, measured by differential scanning calorimetry) of 50 to 1 10°C, preferably of 70 to 90°C; and d) a weight average molecular weight Mw of 10,000 to 260,000, preferably of 50,000 to 80,000. The hydroxy-functionality is required for the cross-linking; an excessive hydroxyl number would adversely affect the resistance of the coated system. The more preferred hydroxy-functionality is of 10 to 15 mg KOH/g. The carboxy-functionality is required for obtaining excellent and resistant adhesion on the substrate, particularly en steel substrates. An excessive acid number would impart water sensitivity to the primer coating; it would also impart a higher viscosity to the primer paint, which would have to be compensated by a lower solids content (resulting in an undesired higher solvent content) An appropriate Tg is required for providing the desired balance between mechanical performance at low temperature and OUV B resistance. A weight average molecular weight Mw (measured by gel permeation chromatography, GPC) of 10,000 to 260,000 (preferably of 50,000 to 80,000) provides a balance between the properties imparted to the dry primer coating and to the wet primer paint. The primer of the invention also contains a polyisocyanate cross-linker. Isocyanates for use in polyurethane coatings are well known in the art. An exemplary textbook reference is Chapter 16 at pages 239-266 in "Protective Coatings" by Clive H. Hare, Technology Publishing Company, Pittsburgh, PA, 1994 (with numerous examples in Tables 16-3 and 16-4) . The functionality of the polyisocyanate is preferably 2 or 3, most preferably 3. The equivalent weight of the polyisocyanate is preferably between 84 and 500, most preferably between 150 and 300. The polyisocyanate is preferably aliphatic or cycloaliphatic, most preferably cycloaliphatic. The molar ratio of NCO functions in the polyisocyanate to the OH functions in the acrylic polymer is of 0.5: 1 to 5: 1 , preferably of 1.5: 1 to 4: 1 , most preferably of about 3: 1. The isocyanate is preferably blocked to allow a one-pot formulation of the primer. As known in the art, it is preferable to use a catalyst for the unblocking reaction. The nature and amount of catalyst required are well known in the art and need not be described here. There is typically used dibutyl tin dilaurate. The primer of the invention further contains an amino resin. Amino resins for use as cross-linkers of polyesters are well known in the art. Exemplary textbook references are: • chapter 9 at pages 87-97 in "Surface Coatings", vol. I., O.C.C.A., Chapman and Hall, London, 1983; • pages 99- 101 in "A Manual of Resins for Surface Coatings", vol. Ill, M.J. Husbands et al., SITA Technology, London, 1987; • pages 82-86 in "Paint and Surface Coatings", R. Lambourne ed. , Ellis Horwood, Chichester, 1987. The major amino resin types are those derived from melamine, urea, benzoguanamine, thiourea and glycoluril. The amino resin is preferably partially alkylated and more preferably fully alkylated, to improve solubility in the primer; iso-butylated, n-butylated and methylated resins are generally used, methylated ones being preferred. The amount of amino resin is such that the molar ratio of amino functions to the OH in the acrylic is of 0. 1 : 1 to 10: 1 , preferably about 1 : 1. It is preferred to use one or more melamine resins in the compositions of the invention. It is more preferred that the melamine resin be an oligomer, with imino groups, most preferably alkylated. Examples of melamine resins include partially methylated melamine resins, highly methylated melamine resins, highly alkylated melamine resins, high imino melamine resins and methylated high imino melamine resins. Hexamethoxymethylol melamine (known as HMMM) is the best known example of highly methylated melamine resin; HMMM is a more preferred amino resin. Other examples include the highly methylated melamine formaldehyde condensates sold under the trade names Cymel 300, Cymel 301 and Cymel 303 (Cymel is a trademark) and believed to consist predominantly of HMMM. Examples of methylated high imino melamine resins include the products sold under the trade names Cymel 323, Cymel 325, Cymel 327 and Cymel 328. As known in the art, it is possible (but not always required) to use an acid catalyst to lower the cure temperature of the melamine resin; the nature and amount of catalyst (when used) are well known in the art and need not be described here. A topcoat layer of PVC-plastisol is then applied on the primed substrate by any appropriate means known in the art, generally by reverse roller coating. The dry film thickness may range from 50 to 500 mm, preferably from 100 to 200 mm. The wet PVC-plastisol layer is then gelled in an oven, at a PMT of 180 to 250°C, preferably of 220 to 240°C; in a typical coil coating line operating at 120 m/s, this corresponds to heating for about 30 s. Examples The following apply to all examples and comparative examples. Preparation of a carboxy- and hydroxy-functional acrylic polymer The monomers used were: • 86.92 wt% methyl methacrylate (MMA) • 10.00 wt% butyl acrylate (BA) • 02.32 wt% hydroxyethyl methacrylate (OH-EMA) • 00.76 wt% methacrylic acid (MA-acid) There was prepared a mixture of 1000 g of monomers (according to the above composition) and 10 g of tert-butyl-peroxy-2-ethylhexanoate (TBPEH) as initiator. In a 5 litres flask provided with a reflux condenser, 666 g of xylene were heated to 90° C under nitrogen. The mixture of monomers and initiators was then added continuously over a period of 4 hours. One hour thereafter, there was added 334 g of xylene and 0.8 g of TBPEH. Yet another hour thereafter, there was made a second addition of 0.8 g of TBPEH. Throughout the polymerisation, the reactor content was kept at about 90°C under nitrogen while stirring. After a total of six hours at about 90°C, the temperature was raised to 105°C during 30 minutes to end the polymerisation reaction. The final polymer solution was diluted to a solids content of 35 wt% by adding 878 g of a mixture of methyl esters of succinic, adipic and glutaric acids as solvents (hereinafter the ester mixture). The following properties were determined: viscosity 20 dPa.s (Haake; 23°C) solids content 35 wt% molecular weight 57700 acid number 5 mg KOH/g of polymer hydroxyl number 10 mg KOH/g of polymer (hydroxyl equivalent 56100/iOH = 5610) Tg 78.8°C Preparation of a PVC-plastisol A PVC-plastisol was prepared which had the following composition: • pigments and fillers : 56 parts by weight (pbw r ) • PVC : 28 pbw • phthalate plastifiers : 9 pbw • stabilisers : 3 pbw • solvent : 4 pbw Preparation of a composite A coil of 0.6 mm thick Galfan steel was passed through a coil coating line with the following steps: » roller coating of a 6 mm (dry film thickness) layer of primer; • heating to a PMT as stated in each example; • reverse roller coating of a 200 mm (dry film thickness) layer of PVC-plastisol • heating to a PMT of 216°C. The following properties were determined: A. Impact resistance ISO 1520- 1973 standard method was used, with the following notation: • 5 = no cracks visible with naked eyes • 4 = slight cracks visible with naked eyes • 3 = cracks; no delamination t 2 = delamination (brittle layer) «• 1 = delamination (peeling) • nd = not determined B Cut edge adhesion The coated panel was cut, the blade cutting the panel from the coated side. The coating was then removed from the cut edge, using a finger. Cut edge adhesion was measured by the extent of delamination measured from the cut edge. C. QUV B exposure ASTM G53-88 standard method was used. The apparatus used was the apparatus sold by The Q-Panel Company, using UV-B lamps n° UVB-313. The cycle consisted of a succession of 4 hours periods of UN exposure at 60°C, each followed by 4 hours periods of condensation at 40°C. A square pattern was made in the coating before exposure, using a cutter blade; adhesion was tested after exposure using the tip of the cutter blade. D. Boiling water test Two double cross patterns (# #) were made in the coating of 4 panels, using a cutter blade; the spacing between the parallel lines was of 5 mm. An 8 mm Erichsen deformation was made in the centre of each double cross pattern. One panel was evaluated as such, while the others were dipped in boiling water respectively during 2, 4 and 8 hours before evaluation. Adherence of each of the four stripes created by the double cross pattern was evaluated by inserting the tip of a cutter blade between the coating and the substrate and slowly delaminating the stripe. Adhesion is reported as 5 (or 5/5) when no delamination occurs, as 0 (or 0/5) when delamination is observed down to the Erichsen deformation limit, and as 1 , 2, 3 or 4 between those extremes; the average determinations are reported. Examples 1 and 2 Preparation of a primer The following components were added into a ball mill then milled together: • the above polymer solution : 22.6 pbw • strontium chromate : 7.34 pbw • titanium dioxide : 4.52 pbw • additives : 0.34 pbw • solvents (methoxypropyl acetate /xylene) : 5.65 pbw After milling, the following components were further adcied : • the above polymer solution : 33. 18 pbw • polyisocyanate (75 wt% in naphtha) : 6.51 pbw (blocked; equivalent weight = 378; trifunctional) • dibutyltin dilaurate : 0.56 pbw • solvents : 19.21 pbw (methyl isobutyl ketone (MIBK) and methoxypropyl acetate) • highly methylated high imino melamine : 2.00 pbw (80 wt% in isobutanol, DIN 53019/53214 viscosity 3.5 Pa. s at 23°C, 0.7 wt% free formaldehyde ISO 9020) Accordingly, the primer paint had a pigment to binder weight ratio of 0.469: 1 , a NCO : OH molar ratio of 3.7: 1 and an amino : OH molar ratio of 1 : 1. Preparation of a composite The composite was prepared as described above, the primer being heated to a PMT of 232°C in a conventional coil coating line (Example 1) or of 241°C in the induction oven of a coil coating line with induction ovens (Example 2) . Comparative examples A, B and C Preparation of a primer The following components were added into a ball mill then milled together : the above polymer solution : 22.6 pbw strontium chromate : 7.34 pbw titanium dioxide : 4.52 pbw additives : 0.34 pbw solvent (ester mixture) : 5.65 pbw After milling, the following components were further added: • the above polymer solution : 33. 18 pbw • polyisocyanate (75 wt% in naphtha) : 6.51 pbw (blocked; equivalent weight = 378; trifunctional) • dibutyltin dilaurate : 0.56 pbw • solvents (MIBK and ester mixture) : 19.21 pbw Accordingly, the primer paint had a pigment to binder weight ratio of 0.486 and a NCO : OH molar ratio of 3.7. Preparation of a composite The composite was prepared as described above; the primer was heated to a PMT of 241°C in a conventional coil coating line (Comparative Example A), of 232°C in a conventional coil coating line (Comparative Example B), or of 241°C in the induction oven of a coil coating line with induction ovens (Comparative Example C). Results A. Impact resistance Table 1 : resistance notation after a 150 kg. cm impact B. Cut edge adhesion Table 2: delamination from cut edge (mm) C. QUV B exposure No delamination was observed after 2000 hours exposure. D. Boiling water test Table 3: adhesion after boiling water exposure

Claims: CLAIMS 1. Primer for PVC-plastisol based on a carboxy- and hydroxy-functional acrylic polymer cross-linked with a polyisocyanate and an amino resin. 2. Primer according to claim 1 , wherein the acrylic polymer has a) a hydroxyl number of 5 to 40 mg KOH/g, preferably of 10 to less than 20 mg KOH/g, more preferably of 10 to 15 mg KOH/g, most preferably of about 10 mg KOH/g; b) an acid number of 2 to 20 mg KOH/g, preferably of 5 to 10 mg KOH/g; c) a glass transition temperature (Tg, measured by differential scanning calorimetry) of 50 to 1 10°C, preferably of 70 to 90°C; and d) a weight average molecular weight Mw of 10,000 to 260,000, preferably of 50,000 to 80,000. 3. Primer according to either of claim 1 and 2, wherein the polyisocyanate has i) a functionality of 2 or 3; ii) an equivalent weight of from 84 to 500; and iii) an aliphatic or cycloaliphatic structure. 4. Primer according to any one of claims 1 to 3, wherein the amino resin is a melamine resin. 5. Primer according to any one of claims 1 to 4, wherein the molar ratio of NCO functions in the polyisocyanate to the OH functions in the acrylic polymer is of 0.5: 1 to 5: 1. 6. Primer according to any one of claims 1 to 5, wherein the molar raiio of amino functions in the melamine resin to the OH functions in the acrylic polymer is of 0.1 : 1 to 10: 1. 7. Primer according to any one of claims 1 to 6, wherein the is cyanate functions in the polyisocyanate are blocked. 8. Primer according to any one of claims 1 to 7, wherein the melamine resin is alkylated. 9. Primer according to any one of claims 1 to 8, wherein the melamine recin contains imino groups. 10. Use of the primer according to any one of claims 1 to 9 in coil coating. 1 1. Use according to claim 10 in the coil coating of a steel substrate with PVC-plastisol.

Inventors: BELLADONE MICHEL, BONFITTO NAZZARIO, BELLADONE, MICHEL, BONFITTO, NAZZARIO
Applicants: BELLADONE MICHEL, BONFITTO NAZZARIO, FINA RESEARCH, BELLADONE, MICHEL, BONFITTO, NAZZARIO, FINA RESEARCH S.A.
Application year: 1999
Main classification: C09D5
IPC codes: C08G18, C09D5, C09D133, C09D161, C09D175