PROCESS FOR PRODUCING POLYOLEFINS

Abstract: A process for producing homopolymers and interpolymers of olefins which involves contacting an olefin and/or an olefin and at least one or more other olefin(s) under polymerization conditions with an olefin polymerization catalyst and dinitrogen monoxide in an amount sufficient to reduce the electrostatic charge in the polymerization medium. Also provided is a process for reducing electrostatic charge in the polymerization of an olefin by adding dinitrogen monoxide.

Description: TITLE OF THE INVENTION Process For Producing Polyolefins FIELD OF INVENTION The present invention relates to a polymerization process for the production of polyolefins utilizing a catalyst suitable for polymerizing olefins and dinitrogen monoxide in amounts sufficient to reduce the electrostatic charge in the polymerization reactor. The use of dinitrogen monoxide as a catalytic agent further provides polyolefins that are suitable for molding and film applications. BACKGROUND OF INVENTION Polyolefins such as polyethylene are well known and are useful in many applications. In particular, linear polyethylene polymers possess properties which distinguish them from other polyethylene polymers, such as branched ethylene homopolymers commonly referred to as LDPE (low density polyethylene). Certain of these properties are described by Anderson et al, U.S. Patent No. 4,076,698. A particularly useful polymerization medium for producing polyethylene and polypropylene polymers is a gas phase process. Examples of such are given in U.S. Patent Nos. 3,709,853; 4,003,712; 4,011,382; 4,302,566; 4,543,399; 4,882,400; 5,352,749 and 5,541,270 and Canadian Patent No. 991,798 and Belgian Patent No. 839,380. There are known various catalysts for polymerizing olefins. Exemplary of such catalysts are as follow: 1. Chromium oxide catalysts which polymerize ethylene to high molecular weight high density polyethylenes (HDPE) having a broad molecular weight distribution. These catalysts are typically based on Cr(6+) and are supported on a carrier. 2. Organochromium catalysts such as bis(triphenylsilyl)chromate supported on silica and activated with organoaluminum compounds, and bis(cyclopentadienyl)chromium supported on silica. 3. Ziegler-Natta catalysts which typically consist of a transition metal component and an organometallic co-catalyst that is typically an organoaluminum compound. 4. An olefin polymerization catalyst that polymerizes olefins to produce homopolymers and interpolymers of olefins having a molecular weight distribution (MWD) of from 1 to 2.5. 5. Metallocene catalysts which typically consist of a transition metal having at least one substituted or unsubstituted cyclopentadienyl or cyclopentadienyl moiety, and an organometallic co-catalyst that is typically alkyl aluminoxane, such as methyl aluminoxane, or an aryl substituted boron compound. 6. Group 13 catalysts of this type described in U.S. Patent No. 5,777,120, such as cationic aluminum alkyl amidinate complexes with an organometallic co- catalyst that is typically alkylaluminoxane, such as methylaluminoxane, or an aryl substituted boron compound. 7. Catalysts of the type described in U.S. Patent No. 5,866,663, such as cationic nickel alkyl diimine complexes with an organometallic co-catalyst that is typically alkylaluminoxane, such as methylaluminoxane, or an aryl substituted boron compound. 8. Catalysts of the type described in Organometallics, 1998, Volume 17, pages 3149-3151, such as neutral nickel alkyl salicylaldiminato complexes. 9. Catalysts of the type described in the Journal of the American Chemical Society, 1998, Volume 120, pages 7143-7144, such as cationic iron alkyl pyridinebisimine complexes with an organometallic co-catalyst that is typically alkylaluminoxane, such as methylaluminoxane, or an aryl substituted boron compound. 10. Catalysts of the type described in the Journal of the American Chemical Society, 1996, Volume 1 18, pages 10008-10009, such as cationic titanium alkyl diamide complexes with an organometallic co-catalyst that is typically alkylaluminoxane, such as methylaluminoxane, or an aryl substituted boron compound. The above catalysts are, or can be, supported on inert porous particulate carrier. A generally encountered problem in polymerization processes, in particular gas phase polymerization processes, is the formation of agglomerates. Agglomerates can form in various places such as the polymerization reactor and the lines for recycling the gaseous stream. As a consequence of agglomerate formation it may be necessary to shut down the reactor. When agglomerates form within the polymerization reactor there can be many adverse effects. For example, the agglomerates can disrupt the removal of polymer from the polymerization reactor by plugging the polymer discharge system. Further, if the agglomerates fall and cover part of the fluidization grid a loss of fluidization efficiency may occur. This can result in the formation of larger agglomerates which can lead to the loss of the entire fluidized bed. In either case there may be the necessity for the shutdown of the reactor. It has been found that agglomerates may be formed as a result of the presence of very fine polymer particles in the polymerization medium. These fine polymer particles may be present as a result of introducing fine catalyst particles or breakage of the catalyst within the polymerization medium. These fine particles are believed to deposit onto and electrostatically adhere to the inner walls of the polymerization reactor and the associated equipment for recycling the gaseous stream such as, for example, the heat exchanger. If the fine particles remain active, and the polymerization reaction continues, then the particles will grow in size resulting in the formation of agglomerates. These agglomerates when formed within the polymerization reactor tend to be in the form of sheets. Several solutions have been proposed to resolve the problem of formation of agglomerates in gas phase polymerization processes. These solutions include the deactivation of the fine polymer particles, control of the catalyst activity and the reduction of the electrostatic charge. Exemplary of the solutions are as follows. European Patent Application 0 359 444 Al describes the introduction into the polymerization reactor of small amounts of an activity retarder in order to keep substantially constant either the polymerization rate or the content of transition metal in the polymer produced. The process is said to produce a polymer without forming agglomerates. U.S. Patent No. 4,739,015 describes the use of gaseous oxygen containing compounds or liquid or solid active-hydrogen containing compounds to prevent the adhesion of the polymer to itself or to the inner wall of the polymerization apparatus. In U.S. Patent No. 4,803,251 there is described a process for reducing sheeting utilizing a group of chemical additives which generate both positive and negative charges in the reactor, and which are fed to the reactor in an amount of a few parts per million(ppm) per part of the monomer in order to prevent the formation of undesired positive or negative charges. Other processes and other additives that may be used to neutralize electrostatic charge in the fluidized-bed reactor are found in U.S. Patents Nos. 4,792,592; 4,803,251 ; 4,855,370; 4,876,320; 5,162,463; 5,194,526 and 5,200,477. Additional processes for reducing or eliminating electrostatic charge include (1) installation of grounding devices in a fluidized bed, (2) ionization of gas or particles by electrical discharge to generate ions which neutralize electrostatic charge on the particles and (3) the use of radioactive sources to produce radiation capable of generating ions which neutralize electrostatic charge on the particles. It would be desirable therefore to provide a process for producing polyolefins, particularly polyethylene, wherein the problems associated with electrostatic charge are reduced. SUMMARY OF THE INVENTION The polymerization process of the present invention comprises the introduction into a polymerization medium comprising an olefin, particularly ethylene, and optionally at least one or more other olefin(s), an olefin polymerization catalyst and dinitrogen monoxide (N 2 O) in an amount sufficient to reduce the electrostatic charge in the polymerization medium to a level lower than would occur in the same polymerization process in the absence of dinitrogen monoxide. The present invention also relates to a process for reducing electrostatic charge in the polymerization of an olefin, particularly ethylene, and optionally at least one or more other olefin(s) in a polymerization medium, particularly gas phase, in the presence of an olefin polymerization catalyst, and dinitrogen monoxide (N 2 O) in an amount sufficient to reduce electrostatic charge in the polymerization medium to a level lower than would occur in the same polymerization process in the absence of the dinitrogen monoxide. All mention herein to elements of Groups of the Periodic Table are made in reference to the Periodic Table of the Elements, as published in "Chemical and Engineering News", 63(5), 27, 1985. In this format, the Groups are numbered 1 to 18. DETAILED DESCRIPTION OF THE INVENTION The polymerization process of the present invention comprises the introduction into a polymerization medium comprising an olefin, particularly ethylene, and optionally at least one or more other olefm(s), an olefin polymerization catalyst and dinitrogen monoxide (N 2 O) in an amount sufficient to reduce the electrostatic charge in the polymerization medium to a level lower than would occur in the same polymerization process in the absence of the dinitrogen monoxide. The present invention also relates to a process for reducing electrostatic charge in the polymerization of an olefin, particularly ethylene, and optionally at least one or more other olefin(s) in a polymerization medium, particularly gas phase, in the presence of an olefin polymerization catalyst, and dinitrogen monoxide (N 2 O) in an amount sufficient to reduce electrostatic charge in the polymerization medium to a level lower than would occur in the same polymerization process in the absence of the dinitrogen monoxide. Optionally a halogenated hydrocarbon may be added to the polymerization medium. Any halogenated hydrocarbon may be used in the process of the present invention. If desired more than one halogenated hydrocarbon can be used. Typical of such halogenated hydrocarbons are monohalogen and polyhalogen substituted saturated or unsaturated aliphatic, alicyclic, or aromatic hydrocarbons having 1 to 12 carbon atoms. Preferred for use in the process of the present invention are dichloromethane, chloroform, carbon tetrachloride, chlorofluoromethane, chlorodifluromethane, dichlorodifluoromethane, fluorodichloromethane, chlorotrifluoromethane, fluorotrichloromethane and 1,2- dichloroethane. Most preferred for use in the process of the present invention is chloroform. In the present invention, any catalyst for polymerizing olefins may be used. Preferably the olefin polymerization catalyst comprises at least one metal selected from Groups 3, 4, 5, 6, 7, 8, 9, 10, 1 1 , 12 and/or 13 of the Periodic Table of the Elements, as defined herein. The olefin polymerization catalyst may be neutral or cationic. Exemplary metals of the olefin polymerization catalyst are titanium, zirconium, vanadium, iron, chromium, nickel and aluminum. Exemplary of such polymerization catalysts are: 1. Any compound containing a Group 6 element. Preferred are chromium containing compounds. Exemplary are chromium oxide catalysts which polymerize ethylene to high molecular weight high density polyethylenes (HDPE) having a broad molecular weight distribution. These catalysts are typically based on Cr(6+) and are supported on a carrier. Further exemplary are organochromium catalysts such as bis(triphenylsilyl)chromate supported on silica and activated with organoaluminum compounds, and bis(cyclopentadienyl)chromium supported on silica. 2. Ziegler-Natta catalysts which typically consist of a transition metal component and an organometallic co-catalyst that is typically an organoaluminum compound. 3. An olefin polymerization catalyst that polymerizes olefins to produce interpolymers of olefins having a molecular weight distribution (MWD) of from 1 to 2.5. 4. Metallocene catalysts which consist of a transition metal component having at least one moiety selected from substituted or unsubstituted cyclopentadienyl, substituted or unsubstituted pentadienyl, substituted or unsubstituted pyrrole, substituted or unsubstituted phosphole, substituted or unsubstituted arsole, substituted or unsubstituted boratabenzene, and substituted or unsubstituted carborane, and an organometallic co-catalyst that is typically alkyl aluminoxane, such as methyl aluminoxane, or an aryl substituted boron compound. 5. Any compound containing a Group 13 element. Preferred are aluminum containing compounds. Exemplary are catalysts of the type described in U.S. Patent No. 5,777,120, such as cationic aluminum alkyl amidinate complexes with an organometallic co-catalyst that is typically alkylaluminoxane, such as methylaluminoxane, or an aryl substituted boron containing compound. 6. Any compound containing a Group 10 element. Preferred are nickel containing compounds. Exemplary are catalysts of the type described in U.S. Patent No. 5,866,663, such as cationic nickel alkyl diimine complexes with an organometallic co-catalyst that is typically alkylaluminoxane, such as methylaluminoxane, or an aryl substituted boron containing compound. Further exemplary are catalysts of the type described in Organometallics, 1998, Volume 17, pages 3149-3151, such as neutral nickel alkyl salicylaldiminato complexes. 7. Any compound containing a Group 8 element. Preferred are iron containing compounds. Exemplary are catalysts of the type described in the Journal of the American Chemical Society, 1998, Volume 120, pages 7143-7144, such as cationic iron alkyl pyridinebisimine complexes with an organometallic co- catalyst that is typically alkylaluminoxane, such as methylaluminoxane, or an aryl substituted boron containing compound. 8. Any compound containing a Group 4 element. Preferred are titanium and zirconium containing compounds. Exemplary are catalysts of the type described in the Journal of the American Chemical Society, 1996, Volume 118, pages 10008-10009, such as cationic titanium alkyl diamide complexes with an organometallic co-catalyst that is typically alkylaluminoxane, such as methylaluminoxane, or an aryl substituted boron containing compound. The above catalysts are, or can be, supported on inert porous particulate carriers. The above olefin polymerization catalysts can be introduced in the process of the present invention in any manner. For example, the catalyst component(s) can be introduced directly into the polymerization medium in the form of a solution, a slurry or a dry free flowing powder. The catalyst if requiring a co- catalyst can be premixed to form an activated catalyst prior to addition to the polymerization medium, or the components can be added separately to the polymerization medium, or the components can be premixed and then contacted with one or more olefins to form a prepolymer and then added to the polymerization medium in prepolymer form. When the catalyst components are premixed prior to introduction into the reactor, any electron donor compound may be added to the catalyst to control the level of activity of the catalyst. Furthermore during the polymerization reaction being carried out in the presence of the olefin polymerization catalyst, as above described, there may be added additional organometallic compound(s). The additional organometallic compounds may be the same or different from that used as co-catalyst. Any or all of the components of the olefin polymerization catalysts can be supported on a carrier. The carrier can be any particulate organic or inorganic material. Preferably the carrier particle size should not be larger than about 200 microns in diameter. The most preferred particle size of the carrier material can be easily established by experiment. Preferably, the carrier should have an average particle size of 5 to 200 microns in diameter, more preferably 10 to 150 microns and most preferably 20 to 100 microns. Examples of suitable inorganic carriers include metal oxides, metal hydroxides, metal halogenides or other metal salts, such as sulphates, carbonates, phosphates, nitrates and silicates. Exemplary of inorganic carriers suitable for use herein are compounds of metals from Groups 1 and 2 of the Periodic Table of the Elements, such as salts of sodium or potassium and oxides or salts of magnesium or calcium, for instance the chlorides, sulphates, carbonates, phosphates or silicates of sodium, potassium, magnesium or calcium and the oxides or hydroxides of, for instance, magnesium or calcium. Also suitable for use are inorganic oxides such as silica, titania, alumina, zirconia, chromia, boron oxide, silanized silica, silica hydrogels, silica xerogels, silica aerogels, and mixed oxides such as talcs, silica chromia, silica/chromia/titania, silica/alumina, silica/titania, silica/magnesia, silica/magnesia/titania, aluminum phosphate gels, silica co-gels and the like. The inorganic oxides may contain small amounts of carbonates, nitrates, sulfates and oxides such as Na 2 C0 3 , K 2 C0 3 , CaC0 3 , MgCO 3 , Na 2 SO , Al 2 (SO 4 ) 3 , BaS0 4 , KN0 3 , Mg(NO 3 ) 2 , Al(NO 3 ) 3 , Na 2 O, K 2 0 and Li 2 O. Carriers containing at least one component selected from the group consisting of MgCl 2 , Si0 2 , Al 2 O 3 or mixtures thereof as a main component are preferred. Examples of suitable organic carriers include polymers such as, for example, polyethylene, polypropylene, interpolymers of ethylene and alpha- olefins, polystyrene, functionalized polystyrene, polyamides and polyesters. The Ziegler-Natta catalysts are well known in the industry. The Ziegler- Natta catalysts in the simplest form are comprised of a component comprising at least one transition metal and a co-catalyst comprising at least one organometallic compound. The metal of the transition metal component is a metal of Groups 4, 5, 6, 7, 8, 9 and/or 10 of the Periodic Table of the Elements, as published in "Chemical and Engineering News", 63(5), 27, 1985. In this format, the groups are numbered 1-18. Exemplary of such transition metals are titanium, zirconium, vanadium, chromium, manganese, iron, cobalt, nickel, and the like, and mixtures thereof. In a preferred embodiment the transition metal is selected from the group consisting of titanium, zirconium, vanadium and chromium, and in a still further preferred embodiment, the transition metal is titanium. The Ziegler-Natta catalyst can optionally contain magnesium and/or chlorine. Such magnesium and chlorine containing catalysts may be prepared by any manner known in the art. The co-catalyst used in the process of the present invention can be any organometallic compound, or mixtures thereof, that can activate the transition metal component in a Ziegler-Natta catalyst in the polymerization of olefins. In particular, the organometallic co-catalyst compound that is reacted with the transition metal component contains a metal of Groups 1, 2, 1 1, 12, 13 and/or 14 of the above described Periodic Table of the Elements. Exemplary of such metals are lithium, magnesium, copper, zinc, boron, silicon and the like, or mixtures thereof. Preferably the co-catalyst is at least one compound of the formula, X n ER 3 _ n , or mixtures thereof, wherein, X is hydrogen, halogen, or mixtures of halogens, selected from fluorine, chlorine, bromine and iodine; n ranges from 0 to 2; E is an element from Group 13 of the Periodic Table of Elements such as boron, aluminum and gallium; and R is a hydrocarbon group, containing from 1 to 100 carbon atoms and from 0 to 10 oxygen atoms, connected to the Group 13 element by a carbon or oxygen bond. Exemplary of the R group suitable for use herein is C MOO alkyl, Cι_ιoo alkoxy, C 2 . 10 o alkenyl, C _ιoo dienyl, C 3 _IQO cycloalkyl, C 3 . 10 o cycloalkoxy, C 3 . 10 o cycloalkenyl, C 4 _ 1 oo cyclodienyl, C 6 _ιoo aryl, C -ιoo aralkyl, C 7 .ι 00 aralkoxy and C . t oo alkaryl. Also exemplary of the R group are hydrocarbons containing from 1 to 100 carbon atoms and from 1 to 10 oxygen atoms. * Exemplary of the co-catalyst used in the process of the present invention where n=0 are trimethylaluminum; triethylborane; triethylgallane; triethylaluminum; tri-n-propylaluminum; tri-π-butylaluminum; tri-n- pentylaluminum; triisoprenylaluminum; tri-π-hexylaluminum; tri-n- heptylaluminum; tri-π-octylaluminum; triisopropylaluminum; triisobutylaluminum; tris(cylcohexylmethyl)aluminum; dimethylaluminum methoxide; dimethylaluminum ethoxide; diethylaluminum ethoxide and the like. Exemplary of compounds where n=l are dimethylaluminum chloride; diethylaluminum chloride; di-n-propylaluminum chloride; di-n-butylaluminum chloride; di-π-pentylaluminum chloride; diisoprenylaluminum chloride; di-n- hexylaluminum chloride; di-n-heptylaluminum chloride; di-π-octylaluminum chloride; diisopropylaluminum chloride; diisobutylaluminum chloride; bis(cylcohexylmethyl)aluminum chloride; diethylaluminum fluoride; diethylaluminum bromide; diethylaluminum iodide; dimethylaluminum hydride; diethylaluminum hydride; di-n-propylaluminum hydride; di-n-butylaluminum hydride; di-n-pentylaluminum hydride; diisoprenylaluminum hydride; di-n- hexylaluminum hydride; di-n-heptylaluminum hydride; di-n-octylaluminum hydride; diisopropylaluminum hydride; diisobutylaluminum hydride; bis(cylcohexylmethyl)aluminum hydride; chloromethylaluminum methoxide; chloromethylaluminum ethoxide; chloroethylaluminum ethoxide and the like. Exemplary of compounds where n=2 are methylaluminum dichloride; ethylaluminum dichloride; n-propylaluminum dichloride; n-butylaluminum dichloride; n-pentylaluminum dichloride; isoprenylaluminum dichloride; n- hexylaluminum dichloride; n-heptylaluminum dichloride; n-octylaluminum dichloride; isopropylaluminum dichloride; isobutylaluminum dichloride; (cylcohexylmethyl) aluminum dichloride and the like. Also exemplary are alkylaluminum sesquialkoxides such as methylaluminum sesquimethoxide; ethylaluminum sesquiethoxide; n-butylaluminum sesqui-n-butoxide and the like. Also exemplary are alkylaluminum sesquihalides such as methylaluminum sesquichloride; ethylaluminum sesquichloride; isobutylaluminum sesquichloride; ethylaluminum sesquifluoride; ethylaluminum sesquibromide; ethylaluminum sesquiiodide and the like. Preferred for use herein as co-catalysts are trialkylaluminums such as trimethylaluminum, triethylaluminum, tri-n-propylaluminum, tri-n- butylaluminum, triisobutylaluminum, tri-n-hexylaluminum, triisohexylaluminum, tri-2-methylpentylaluminum, tri-n-octylaluminum, tri-π-decylaluminum; and dialkylaluminum halides such as dimethylaluminum chloride, diethylaluminum chloride, dibutylaluminum chloride, diisobutylaluminum chloride, diethylaluminum bromide and diethylaluminum iodide; and alkylaluminum sesquihalides such as methylaluminum sesquichloride, ethylaluminum sesquichloride, n-butylaluminum sesquichloride, isobutylaluminum sesquichloride, ethylaluminum sesquifluoride, ethylaluminum sesquibromide and ethylaluminum sesquiiodide. Most preferred for use herein as co-catalysts are trialkylaluminums such as trimethylaluminum, triethylaluminum, tri-n-propylaluminum, tri-n- butylaluminum, triisobutylaluminum, tri-n-hexylaluminum, triisohexylaluminum, tri-2-methylpentylaluminum, tri-n-octylaluminum and dialkylaluminum halides such as dimethylaluminum chloride, diethylaluminum chloride, dibutylaluminum chloride, diisobutylaluminum chloride and alkylaluminum sesquihalides such as methylaluminum sesquichloride, ethylaluminum sesquichloride, n-butylaluminum sesquichloride and isobutylaluminum sesquichloride. Mixtures of the above co-catalysts also can be utilized herein as the co- catalyst. Furthermore there may be added to the Ziegler-Natta catalysts any electron donor. The electron donor compound preferably is selected from the group consisting of ethers, thioethers, esters, thioesters, amines, amides, ketones, nitriles, phosphines, silanes, acid anhydrides, acid halides, acid amides, aldehydes, and organic acid derivatives. More preferred as electron donors are compounds containing from 1 to 50 carbon atoms and from 1 to 30 heteroatoms of an element, or mixtures thereof, selected from Groups 14, 15, 16 and 17 of the Periodic Table of Elements. The Ziegler-Natta catalyst may be prepared by any method known in the art. The catalyst can be in the form of a solution, a slurry or a dry free flowing powder. The amount of Ziegler-Natta catalyst used is that which is sufficient to allow production of the desired amount of the polyolefin. Metallocene catalysts are well known in the industry and are typically comprised of a transition metal component and a co-catalyst. The transition metal component has at least one moiety selected from substituted or unsubstituted cyclopentadienyl, substituted or unsubstituted pentadienyl, substituted or unsubstituted pyrrole, substituted or unsubstituted phosphole, substituted or unsubstituted arsole, substituted or unsubstituted boratabenzene, and substituted or unsubstituted carborane. The transition metal is selected from Groups 3, 4, 5, 6, 7, 8, 9 and 10 of the Periodic Table of the Elements. Exemplary of such transition metals are titanium, zirconium, hafnium, vanadium, chromium, manganese, iron, cobalt, nickel, and the like, and mixtures thereof. In a preferred embodiment the transition metal is selected from Groups 4, 5 or 6 such as, for example, titanium, zirconium, hafnium, vanadium and chromium, and in a still further preferred embodiment, the transition metal is titanium or zirconium or mixtures thereof. The co-catalyst component of the metallocene catalyst can be any compound, or mixtures thereof, that can activate the transition metal component of the metallocene catalyst in olefin polymerization. Typically the co-catalyst is an alkylaluminoxane such as, for example, methylaluminoxane (MAO) and aryl substituted boron compounds such as, for example, tris(perfluorophenyl)borane and the salts of tetrakis(perfluorophenyl)borate. There are many references describing metallocene catalysts in great detail. For example, metallocene catalysts are described in U.S. Patent Nos. 4,564,647; 4,752,597; 5,106,804; 5,132,380; 5,227,440; 5,296,565; 5,324,800; 5,331,071 ; 5,332,706; 5,350,723; 5,399,635; 5,466,766; 5,468,702; 5,474,962; 5,578,537 and 5,863,853. In carrying out the polymerization process of the present invention, the co- catalyst(s), if utilized, is added to the polymerization medium in any amount sufficient to effect production of the desired polyolefm. It is preferred to utilize the co-catalyst(s) in a molar ratio of co-catalyst(s) to metal component(s) of the olefin polymerization catalyst ranging from about 0.5: 1 to about 10000: 1. In a more preferred embodiment, the molar ratio of co-catalyst(s) to metal component(s) ranges from about 0.5: 1 to about 1000: 1. The polymerization process of the present invention may be carried out using any suitable process, for example, solution, slurry and gas phase. A particularly desirable method for producing polyolefin polymers according to the present invention is a gas phase polymerization process preferably utilizing a fluidized bed reactor. This type reactor and means for operating the reactor are well known and completely described in U.S Patents Nos. 3,709,853; 4,003,712; 4,011,382; 4,012,573; 4,302,566; 4,543,399; 4,882,400; 5,352,749; 5,541,270; Canadian Patent No. 991,798 and Belgian Patent No. 839,380. These patents disclose gas phase polymerization processes wherein the polymerization medium is either mechanically agitated or fluidized by the continuous flow of the gaseous monomer and diluent. The entire contents of these patents are incorporated herein by reference. In general, the polymerization process of the present invention may be effected as a continuous gas phase process such as a fluid bed process. A fluid bed reactor for use in the process of the present invention typically comprises a reaction zone and a so-called velocity reduction zone. The reaction zone comprises a bed of growing polymer particles, formed polymer particles and a minor amount of catalyst particles fluidized by the continuous flow of the gaseous monomer and diluent to remove heat of polymerization through the reaction zone. Optionally, some of the recirculated gases may be cooled and compressed to form liquids that increase the heat removal capacity of the circulating gas stream when readmitted to the reaction zone. A suitable rate of gas flow may be readily determined by simple experiment. Make up of gaseous monomer to the circulating gas stream is at a rate equal to the rate at which particulate polymer product and monomer associated therewith is withdrawn from the reactor and the composition of the gas passing through the reactor is adjusted to maintain an essentially steady state gaseous composition within the reaction zone. The gas leaving the reaction zone is passed to the velocity reduction zone where entrained particles are removed. Finer entrained particles and dust may be removed in a cyclone and/or fine filter. The gas is passed through a heat exchanger wherein the heat of polymerization is removed, compressed in a compressor and then returned to the reaction zone. In more detail, the reactor temperature of the fluid bed process herein ranges from about 30°C to about 150°C. In general, the reactor temperature is operated at the highest temperature that is feasible taking into account the sintering temperature of the polymer product within the reactor. The process of the present invention is suitable for the production of homopolymers of olefins, particularly ethylene, and/or copolymers, terpolymers, and the like, of olefins, particularly ethylene, and at least one or more other olefin(s). Preferably the olefins are alpha-olefins. The olefins, for example, may contain from 2 to 16 carbon atoms. Particularly preferred for preparation herein by the process of the present invention are polyethylenes. Such polyethylenes are preferably homopolymers of ethylene and interpolymers of ethylene and at least one alpha-olefin wherein the ethylene content is at least about 50%by weight of the total monomers involved. Exemplary olefins that may be utilized herein are ethylene, propylene, 1-butene, 1-pentene, 1-hexene, 1-heptene, 1-octene, 4- methylpent-1-ene, 1-decene, 1-dodecene, 1-hexadecene and the like. Also utilizable herein are polyenes such as 1,3-hexadiene, 1,4-hexadiene, cyclopentadiene, dicyclopentadiene, 4-vinylcyclohex-l-ene, 1,5-cyclooctadiene, 5-vinylidene-2-norbornene and 5-vinyl-2-norbornene, and olefins formed in situ in the polymerization medium. When olefins are formed in situ in the polymerization medium, the formation of polyolefins containing long chain branching may occur. In carrying out the polymerization process of the present invention the dinitrogen monoxide used to reduce electrostatic charge in the polymerization medium is added in any manner. For example, the dinitrogen monoxide may be added to the preformed catalyst, to the prepolymer during the prepolymerization step, to the preformed prepolymer and/or to the polymerization medium. The dinitrogen monoxide may optionally be premixed with the co-catalyst when utilized. The dinitrogen monoxide is added in any amount sufficient to reduce the electrostatic charge in the polymerization medium to a level lower than would occur in the same polymerization process in the absence of the dinitrogen monoxide. It is preferred to incorporate the dinitrogen monoxide in the polymerization medium in an amount ranging from about 1 ppm to about 10,000 ppm by volume. In carrying out the polymerization process of the present invention, the halogenated hydrocarbon may be added to the polymerization medium in any amount sufficient to effect production of the desired polyolefin. It is preferred to incorporate the halogenated hydrocarbon in a molar ratio of halogenated hydrocarbon to metal component of the olefin polymerization catalyst ranging from about 0.001 : 1 to about 100: 1. In a more preferred embodiment, the molar ratio of halogenated hydrocarbon to metal component ranges from about 0.001 : 1 to about 10: 1. The dinitrogen monoxide and the optional halogenated hydrocarbon may be added to the polymerization medium in any manner. The dinitrogen monoxide and the halogenated hydrocarbon may be added to the olefin polymerization catalyst just prior to addition to the polymerization medium, or added separately from the catalyst to the polymerization medium in any manner known in the art. For example, the dinitrogen monoxide may optionally be premixed with the halogenated hydrocarbon prior to addition to the polymerization medium. If a gas phase fluidized bed process is utilized for polymerization of the olefin, it may be advantageous to add the dinitrogen monoxide prior to the heat removal means, e.g., the heat exchanger, to slow the rate of fouling of said heat removal means in addition to reducing the electrostatic charge in the polymerization reactor. The molecular weight of the polyolefin produced by the present invention can be controlled in any known manner, for example, by using hydrogen. The molecular weight control of polyethylene, for example, may be evidenced by an increase in the melt index (I 2 ) of the polymer when the molar ratio of hydrogen to ethylene in the polymerization medium is increased. Molecular weight distribution (MWD), or polydispersity, is a well known characteristic of polymers. MWD is generally described as the ratio of the weight average molecular weight (Mw) to the number average molecular weight (Mn). The ratio Mw Mn can be measured directly by gel permeation chromatography techniques. The MWD of a polymer is determined with a Waters Gel Permeation Chromatograph Series 150C equipped with Ultrastyrogel columns and a refractive index detector. In this development, the operating temperature of the instrument was set at 140°C, the eluting solvent was o-dichlorobenzene, and the calibration standards included 10 polystyrenes of precisely known molecular weight, ranging from a molecular weight of 1000 to a molecular weight of 1.3 million, and a polyethylene standard, NBS 1475. Any conventional additive may be added to the polyolefins obtained by the present invention. Examples of the additives include nucleating agents, heat stabilizers, antioxidants of phenol type, sulfur type and phosphorus type, lubricants, antistatic agents, dispersants, copper harm inhibitors, neutralizing agents, foaming agents, plasticizers, anti-foaming agents, flame retardants, crosslinking agents, flowability improvers such as peroxides, ultraviolet light absorbers, light stabilizers, weathering stabilizers, weld strength improvers, slip agents, anti-blocking agents, antifogging agents, dyes, pigments, natural oils, synthetic oils, waxes, fillers and rubber ingredients. The polyolefins, particularly polyethylenes, of the present invention may be fabricated into films by any technique known in the art. For example, films may be produced by the well known cast film, blown film and extrusion coating techniques. Further, the polyolefins, particularly polyethylenes, may be fabricated into other articles of manufacture, such as molded articles, by any of the well known techniques. The invention will be more readily understood by reference to the following examples. There are, of course, many other forms of this invention which will become obvious to one skilled in the art, once the invention has been fully disclosed, and it will accordingly be recognized that these examples are given for the purpose of illustration only, and are not to be construed as limiting the scope of this invention in any way. Examples In the following examples the test procedures listed below were used in evaluating the analytical properties of the polyolefins herein. a) Density is determined according to ASTM D-4883 from a plaque made according to ASTM D 1928 ; b) Melt Index (MI), I 2 , is determined in accord with ASTM D-1238, condition E, measured at 190°C, and reported as decigrams per minute; c) High Load Melt Index (HLMI), I 21 , is measured in accord with ASTM D-1238, Condition F, measured at 10.0 times the weight used in the melt index test (MI) above; d) Melt Flow Ratio (MFR) = I 21 /I 2 or High Load Melt Index/Melt Index; e) Residual Titanium Content in the Product. The residual titanium content in the product is measured by X-Ray Fluorescence Spectroscopy (XRF) using a Philips Sequential X-Ray Spectrometer Model PW 1480. The samples of the polymer to be evaluated were compression molded into a circular shaped plaque approximately 43 mm in diameter so as to fit the sample holder on the spectrometer and 3 to 5 mm in thickness and having a smooth flat surface. The molded test specimens were then placed in the XRF unit and the x-ray fluorescence arising from the titanium in the test specimen was measured. The residual titanium content was then determined based on a calibration curve obtained by measurements from polyethylene calibration specimens containing a known amount of titanium. The residual titanium content is reported as parts per million (ppm) relative to the polymer matrix. The Ziegler-Natta catalyst used in Example 1 was prepared in accordance with Example 1-a of European Patent Application EP 0 703 246 Al. The catalyst was used in prepolymer form and was prepared in accordance with Example 1-b of European Patent Application EP 0703 246 Al. A prepolymer containing about 34 grams of polyethylene per millimole of titanium was thus obtained. Polymerization Process The polymerization process utilized in Example 1 herein was carried out in a fluidized-bed reactor for gas-phase polymerization, consisting of a vertical cylinder of diameter 0.74 meters and height 7 meters and surmounted by a velocity reduction chamber. The reactor is provided in its lower part with a fluidization grid and with an external line for recycling gas, which connects the top of the velocity reduction chamber to the lower part of the reactor, at a point below the fluidization grid. The recycling line is equipped with a compressor for circulating gas and a heat transfer means such as a heat exchanger. In particular the lines for supplying ethylene, 1-hexene, hydrogen and nitrogen, which represent the main constituents of the gaseous reaction mixture passing through the fluidized bed, feed into the recycling line. Above the fluidization grid, the reactor contains a fluidized bed consisting of a polyethylene powder made up of particles with a weight-average diameter of about 0.5 mm to about 1.4 mm. The gaseous reaction mixture, which contains ethylene, olefin comonomer, hydrogen, nitrogen and minor amounts of other components, passes through the fluidized bed under a pressure ranging from about 280 psig to about 300 psig with an ascending fluidization speed, referred to herein as fluidization velocity, ranging from about 1.6 feet per second to about 2.1 feet per second. In Example 1 the Ziegler-Natta catalyst, as described above in prepolymer form, was introduced intermittently into the reactor. The said catalyst contained magnesium, chlorine and titanium. The prepolymer form contained about 34 grams of polyethylene per millimole of titanium and an amount of tri-n- octylaluminum (TnOA) such that the molar ratio, Al/Ti, was about 1.1 : 1. The rate of introduction of the prepolymer into the reactor was adjusted to achieve the desired production rate. During the polymerization the additional co-catalyst, when utilized, was introduced continuously into the line for recycling the gaseous reaction mixture, at a point situated downstream of the heat transfer means. The feed rate of additional co-catalyst is expressed as a molar ratio of trialkylaluminum to titanium (Al/Ti), and is defined as the ratio of the co-catalyst feed rate (in moles of trialkylaluminum per hour) to the prepolymer feed rate (in moles of titanium per hour). A solution of chloroform (CHC1 3 ) in n-hexane, at a concentration of about 0.5 weight percent, was introduced continuously into the line for recycling the gaseous reaction mixture. The feed rate of the optional halogenated hydrocarbon is expressed as a molar ratio of CHC1 3 to titanium (CHC1 3 /Ti), and is defined as the ratio of the CHC1 3 feed rate (in moles of CHC1 3 per hour) to the catalyst or prepolymer feed rate (in moles of titanium per hour). Dinitrogen monoxide (N 2 O), when utilized in the following examples, was utilized to reduce the electrostatic charge in the polymerization medium. The gaseous dinitrogen monoxide was introduced continuously into the line for recycling the gaseous reaction mixture. The concentration of dinitrogen monoxide in the polymerization medium is expressed in units of ppm by volume. The electrostatic charge of the fluidized bed was measured by a Correflow Model 3400 Electrostatic Monitor (ESM) supplied by Auburn International, Inc. of Danvers, Massachusetts. The electrostatic probe was installed in the vertical cylindrical section of the reactor at a height such as to be within the fluidized bed of polymer particles. The electrostatic probe measures the current flow between the polymerization medium and the ground. A reduction in electrostatic charge is defined as a reduction in the absolute magnitude of the measured current and/or a reduction in the variability of the measured current. EXAMPLE 1 The initial process conditions are given in Table 1. The polymerization reactor was lined out producing a interpolymer of ethylene and 1-hexene having a melt index of 0.6 dg/min and a density of 0.920 g/cc. The level of electrostatic charge was measured. Thereafter, dinitrogen monoxide was added to the reactor loop at a level of 60 ppm by volume. Trimethylaluminum was added to maintain the production rate at 160 pounds per hour. The level of electrostatic charge in the polymerization reactor was measured and it was found that the level of electrostatic charge was reduced as a result of adding the dinitrogen monoxide. Table 1: Initial Reactor Conditions for Example Reactor Pressure (psig) 296 Reactor Temperature (°C) 86 Fluidization Velocity (ft/sec) 2.1 Fluidized Bulk Density(lb/ft 3 ) 16.1 Reactor Bed Height (ft) 10.9 Ethylene (mole%) 26 H 2 /C 2 (molar ratio) 0.145 C 6 /C 2 (molar ratio) 0.146 Prepolymer Rate (lb/h) 0.8 Production Rate (lb/h) 160 Residual Titanium (ppm) 8.5 Density (g/cc) 0.920 Melt Index, I 2 (dg/min) 0.6 Melt Flow Ratio (I 21 /I 2 ) 29 EXAMPLE 2 The process of Example 1 is followed with the following exceptions. The Ziegler-Natta catalyst used in Example 2 is obtained from Toho Titanium Company, Limited under the product name THC-C. The catalyst is a titanium- based catalyst supported on magnesium chloride. This catalyst is added directly to the polymerization medium. Trimethylaluminum is added as co-catalyst to the polymerization medium. The catalyst addition rate and the co-catalyst addition rate is adjusted to produce about 200 pounds of polymeric product per hour having a residual titanium content of about 1 ppm. Furthermore the C 6 /C and the H 2 /C 2 molar ratios are adjusted to produce an ethylene/1-hexene interpolymer having a target melt index of about 0.6 dg/min and a target density of about 0.920 g/cc. The level of electrostatic charge in the polymerization reactor is measured. Thereafter, dinitrogen monoxide is added to the polymerization medium and the level of electrostatic charge is expected to be reduced. EXAMPLE 3 The process of Example 1 is followed with the following exceptions. The Ziegler-Natta catalyst used in Example 3 is obtained from Grace Davison, Baltimore, Maryland under the product name XPO-5021. The catalyst is a titanium-based catalyst supported on silica. This catalyst is added directly to the polymerization medium. Triethylaluminum is added as co-catalyst to the polymerization medium. The catalyst addition rate and the co-catalyst addition rate are adjusted to produce about 200 pounds of polymeric product per hour having a residual titanium content of about 1 ppm. Furthermore the Cβ/C 2 and the H 2 /C 2 molar ratios are adjusted to produce an ethylene/ 1-hexene interpolymer having a melt index of about 0.6 dg/min and a density of about 0.920 g/cc. The level of electrostatic charge in the polymerization reactor is measured. Thereafter, dinitrogen monoxide is added to the polymerization medium and the level of electrostatic charge is expected to be reduced. EXAMPLES 4-6 The process of Example 1 is followed with the exception that in place of the Ziegler-Natta catalyst, there is used a metallocene catalyst supported on silica, as follows: Example 4 bis(l-butyl-3-methylcyclopentadienyl)zirconium dichloride and methylaluminoxane, Example 5 bis(l-butyl-3-methylcyclopentadienyl)dimethyl zirconocene and tris(perfluorophenyl)borane, Example 6 (tert-butylamido)dimethyl(tetramethyl-η 5 - cyclopentadienyl)silanetitaniumdimethyl and triphenylmethylium tetrakis(perfluorophenyl)borate. The C 6 /C 2 and the H 2 /C 2 molar ratios are adjusted to produce an ethylene/ 1-hexene interpolymer having a target melt index of about 0.6 dg/min and a target density of about 0.920 g/cc. The level of electrostatic charge in the polymerization medium is measured. In each of the above Examples 4-6 the level of electrostatic charge in the polymerization medium is expected to be reduced as a result of adding dinitrogen monoxide. Films can be prepared from the polyolefins of the present invention. Articles such as molded items can also be prepared from the polyolefins of the present invention. It should be clearly understood that the forms of the invention herein described are illustrative only and are not intended to limit the scope of the invention. The present invention includes all modifications falling within the scope of the following claims.

Claims: CLAIMS We claim: 1. A process for polymerizing an olefin and/or an olefin and at least one or more other olefin(s) comprising contacting, under polymerization conditions, the olefin and/or the olefin and at least one or more other olefin(s) with an olefin polymerization catalyst and dinitrogen monoxide, wherein the dinitrogen monoxide is present in an amount sufficient to reduce electrostatic charge in the polymerization medium to a level lower than would be obtained in the absence of dinitrogen monoxide. 2. The process according to Claim 1 wherein the olefin polymerization catalyst comprises at least one metal selected from Groups 3, 4, 5, 6, 7, 8, 9, 10, 1 1, 12 and/or 13 of the Periodic Table of the Elements, as defined herein. 3. The process according to Claim 2 wherein the metal is selected from the group consisting of titanium, zirconium, vanadium, iron, chromium, nickel and aluminum. 4. The process according to Claim 3 wherein the metal is selected from the group consisting of titanium, zirconium and vanadium. 5. The process according to Claim 1 wherein the olefin polymerization catalyst is supported on a carrier. 6. The process according to Claim 5 wherein the carrier is selected from the group consisting of silica, alumina, magnesium chloride and mixtures thereof. 7. The process according to Claim 2 wherein the olefin polymerization catalyst is selected from the group consisting of chromium oxide catalysts, organochromium catalysts, Ziegler-Natta catalysts, olefin polymerization catalysts that polymerize olefins to produce homopolymers and interpolymers of olefins having a molecular weight distribution (MWD) of from 1 to 2.5, metallocene catalysts, cationic aluminum alkyl amidinate catalysts, cationic nickel alkyl diimine catalysts, neutral nickel alkyl salicylaldiminato catalysts, cationic iron alkyl pyridinebisimine catalysts and cationic titanium alkyl diamide catalysts. 8. The process according to Claim 7 wherein the olefin polymerization catalyst is selected from the group consisting of chromium oxide catalysts, organochromium catalysts, Ziegler-Natta catalysts, metallocene catalysts and olefin polymerization catalysts that polymerize olefins to produce homopolymers and interpolymers of olefins having a molecular weight distribution (MWD) of from 1 to 2.5. 9. The process according to Claim 8 wherein the olefin polymerization catalyst is selected from the group consisting of chromium oxide catalysts, Ziegler- Natta catalysts and metallocene catalysts. 10. The process according to Claim 1 further comprising adding a halogenated hydrocarbon to the polymerization medium. 11. The process according to Claim 10 wherein the halogenated hydrocarbon is selected from the group consisting of dichloromethane, chloroform, carbon tetrachloride, chlorofluoromethane, chlorodifluromethane, dichlorodifluoromethane, fluorodichloromethane, chlorotrifluoromethane, fluorotrichloromethane and 1,2-dichloroethane. 12. The process according to Claim 11 wherein the halogenated hydrocarbon is chloroform. 13. The process according to Claim 1 wherein the dinitrogen monoxide is added in an amount ranging from about 1 ppm to about 10,000 ppm by volume. 14. The process according to Claim 1 wherein the polymerization medium is gas phase. 15. The process according to Claim 1 wherein the polymerization medium is slurry phase. 16. The process according to Claim 1 wherein the olefin is ethylene and the at least one or more other olefin(s) is selected from the group consisting of olefins having 3 to 16 carbon atoms. 17. The process according to Claim 16 wherein the at least one or more other olefin(s) is selected from the group consisting of 1-octene, 1-hexene, 4- methylpent-1-ene, 1-pentene, 1-butene and propylene. 18. The process according to Claim 16 wherein the interpolymer resulting from the polymerization of ethylene and at least one or more olefin(s) comprises ethylene in an amount of at least about 50%by weight of the interpolymer. 19. A process for reducing electrostatic charge in the polymerization of an olefin and/or an olefin and at least one or more other olefin(s) in a polymerization medium in the presence of an olefin polymerization catalyst, comprising introducing into the polymerization medium dinitrogen monoxide in an amount sufficient to reduce electrostatic charge in the polymerization medium to a level lower than would be obtained in the absence of dinitrogen monoxide. 20. The process according to Claim 19 wherein the olefin polymerization catalyst comprises at least one metal selected from Groups 3, 4, 5, 6, 7, 8, 9, 10, 1 1, 12 and/or 13 of the Periodic Table of the Elements, as defined herein. 21. The process according to Claim 20 wherein the metal is selected from the group consisting of titanium, zirconium, vanadium, iron, chromium, nickel and aluminum. 22. The process according to Claim 21 wherein the metal is selected from the group consisting of titanium, zirconium and vanadium. 23. The process according to Claim 19 wherein the olefin polymerization catalyst is supported on a carrier. 24. The process according to Claim 23 wherein the carrier is selected from the group consisting of silica, alumina, magnesium chloride and mixtures thereof. 25. The process according to Claim 20 wherein the olefin polymerization catalyst is selected from the group consisting of chromium oxide catalysts, organochromium catalysts, Ziegler-Natta catalysts, olefin polymerization catalysts that polymerize olefins to produce homopolymers and interpolymers of olefins having a molecular weight distribution (MWD) of from 1 to 2.5, metallocene catalysts, cationic aluminum alkyl amidinate catalysts, cationic nickel alkyl diimine catalysts, neutral nickel alkyl salicylaldiminato catalysts, cationic iron alkyl pyridinebisimine catalysts and cationic titanium alkyl diamide catalysts. 26. The process according to Claim 25 wherein the olefin polymerization catalyst is selected from the group consisting of chromium oxide catalysts, organochromium catalysts, Ziegler-Natta catalysts, metallocene catalysts and olefin polymerization catalysts that polymerize olefins to produce homopolymers and interpolymers of olefins having a molecular weight distribution (MWD) of from 1 to 2.5. 27. The process according to Claim 26 wherein the olefin polymerization catalyst is selected from the group consisting of chromium oxide catalysts, Ziegler- Natta catalysts and metallocene catalysts. 28. The process according to Claim 19 further comprising adding a halogenated hydrocarbon to the polymerization medium. 29. The process according to Claim 28 wherein the halogenated hydrocarbon is selected from the group consisting of dichloro methane, chloroform, carbon tetrachloride, chlorofluoromethane, chlorodifluromethane, dichlorodifluoromethane, fluorodichloromethane, chlorotrifluoromethane, fluorotrichloromethane and 1,2-dichloroethane. 30. The process according to Claim 29 wherein the halogenated hydrocarbon is chloroform. 31. The process according to Claim 19 wherein the dinitrogen monoxide is added in an amount ranging from about 1 ppm to about 10,000 ppm by volume to the polymerization medium. 32. The process according to Claim 19 wherein the polymerization medium is gas phase. -BO¬ SS. The process according to Claim 19 wherein the polymerization medium is slurry phase. 34. The process according to Claim 19 wherein the olefin is ethylene and the at least one or more other olefin(s) is selected from the group consisting of olefins having 3 to 16 carbon atoms. 35. The process according to Claim 34 wherein the at least one or more other olefin(s) is selected from the group consisting of 1-octene, 1-hexene, 4- methylpent-1-ene, 1-pentene, 1-butene and propylene. 36. The process according to Claim 34 wherein the inteφolymer resulting from the polymerization of ethylene and at least one or more olefin(s) comprises ethylene in an amount of at least about 50%by weight of the interpolymer. 37. A film fabricated from the polyolefin produced in accordance with Claim 19. 38. An article fabricated from the polyolefin produced in accordance with Claim 19.

Inventors: FORD RANDAL RAY, MOORE GLENN EDWARD, VANDERBILT JEFFREY JAMES, WHITFIELD ROXANNA LEA, FORD, RANDAL, RAY, MOORE, GLENN, EDWARD, VANDERBILT, JEFFREY, JAMES, WHITFIELD, ROXANNA, LEA
Applicants: EASTMAN CHEM CO, EASTMAN CHEMICAL COMPANY
Application year: 1999
Main classification: C08F10
IPC codes: C08F4, C08F10, C08F210, C08J5