RECLAIMED PET RESIN COMPOSITION, MOLDED ARTICLE THEREOF, AND FLAME-RETARDANT RESIN COMPOSITION AND MOLDED ARTICLE THEREOF

Abstract: In the present invention, the No. I invention relates to a regenerated PET resin composition which comprises formulating 0.5-100 part by weight of a lactone polymer (B) with 100 parts by weight of a regenerated PET resin (A), in which there is improved a molding processability such as an injection moldability and extruding molding, and relates to a molded article therefrom and, the No. II invention relates to a flame retardant resin composition containing a thermoplastic resin (E) and a flame retardant (F), in which bleeding of the flame retardant is suppressed without a decline of a flame retardancy, and relates to a molded article therefrom.

Description: TECHNICAL FIELD The present invention relates to a regeneration of a PET, and it relates to a regenerated PET resin composition in which there is improved a molding processability such as an injection moldability and extrusion processability, and a molded article therefrom. BACKGROUND TECHNOLOGY Thermoplastic resins are produced in a large amount because those are light and tough, excellent in water resistance, chemical resistance, and an electric insulation property, and easy in molding and processing. Particularly, a polyethylene terephthalate which is usually called a PET is mass-produced as bottles for beverages because it is light and tough and, further, excellent in transparency. Recently in Japan, Recycling Law for Vessels and Wrapping materials is enforced, and there is proceeded a measure of a shift to a recycling society in relation to plastics. Further, recycling of PET bottles is desired because of a worldwide trend. However, since the regenerated PET resin includes a problem of a poor moldability, it is difficult to obtain a molded article by an injection molding method which is usually employed for general-purpose resins such as a polyolefin resin. For that reason, there is limited a use of the regenerated PET, and regeneration of PET is not progressed. Further, since the regenerated PET resin is a crushed resin from recollected bottles for beverages, textiles, and films, etc., it is usually unsettled in shapes and a flake-state, whereby, it is bulky and worse in transport efficiency. Accordingly, it is desired that the regenerated PET resin is pellet-state in consideration of transport efficiency. However, since moldability is poor, it is difficult to prepare uniform pellets. It is an existing circumstance that there are not methods by which there can be solved the above-described various problems in the regenerated PET resin. JP 03 064351 A Abstract discloses a resin composition for moulded articles which contains a polyethylene terephthalate (PET), a polycaprolactone (PCL), and a nucleating agent. JP 60 240754 A Abstract discloses a resin composition for moulded articles in which a PCL (or a derivative) having a number average molecular weight of not more than 5000 is mixed with a polyester such as a PET or PBT (a polybutylene terephthalate). JP 03 157473 A Abstract discloses a polyester-based hot-melt adhesive in which a lactone compound is copolymerised as a polyester-based resin. JP 01 168768 A Abstract discloses a resin composition for coatings in which a PCL is mixed with a copolymer such as a PBT or PBT-PET copolymer. JP 61 040355 A Abstract discloses a resin composition for moulded articles in which a polyester block copolymer is mixed with a polyolefin containing carboxylic groups and/or epoxy groups. The Abstract describes that the polyester block copolymer may contain molecular units derived from poly-ε-caprolactone. However, none of the above-mentioned Abstracts teach the use of a "once-moulded, used, and recovered or reclaimed PET" or a "waste PET" such as in the present invention, as defined by the claims as amended and filed herewith. The present invention aims to provide a regenerated PET resin composition in which there is improved a molding processability such as an injection moldability and extrusion moldability, and to provide a molded article therefrom. Hereinafter, the invention illustrated. DISCLOSURE OF THE INVENTION The inventors of the present invention, as a result of an intensive investigation for solving the above-mentioned problems in the invention, found out that the above-mentioned problems can be effectively solved by mixing a specified amount of an organic ester compound for regenerating a PET resin, and attained to the invention. That is, the invention relates to a regenerated PET resin composition which comprises 100 parts by weight of a regenerated PET resin (A) and 0.5-100 part by weight of a lactone polymer (B). The present invention further relates to a regenerated PET resin composition further containing a polyolefin resin (C). The present invention relates to a regenerated PET resin composition further containing other additives (D) composed of an inorganic compound or an organic compound. The present invention relates to a regenerated PET resin molded article which comprises molding the regenerated PET resin composition. BEST MODE FOR CARRYING OUT THE INVENTION Hereinafter, embodiments for carrying out the invention are illustrated in order. [Constructing components] <Regenerated PET resin (A)> The PET to be employed in the present invention is an abbreviation of a polyethylene terephthalate, and it is a resin obtained by a polymerization reaction of a glycol ester of terephthalic acid until a fixed polymerization degree under the presence of a catalyst, and the glycol ester is obtained by a thermal reaction under the presence of a catalyst using terephthalic acid or an ester-formable derivative (for example, a lower alkyl ester such as a dimethyl ester and monoester) and ethylene glycol or the ester-formable derivative as starting raw materials. The regenerated PET resin (A) in the present invention means a resin recycled and treated in order to utilize after the PET was molded and used as a product such as bottles for beverages, textiles, films, and a large-sized molded article such as container, and it is usually called a regenerated PET materials or a recycled PET. The regenerated PET resin (A) to be employed in the present invention is not limited to a product form of a PET to be regenerated and, specifically, there can be exemplified bottles for beverages, textiles, films, and a molded article, etc. Further, it also includes a PET material such as chips of films and gates or runners in injection-molded articles which are produced in the preparation of final products, even though those are not employed as the final products. <Lactone polymer (B)> The lactone polymer (B) to be employed in the present invention can be obtained by a ring-opening polymerization of a lactone having a carbon number of 4-11. Specifically, a poly-ε-caprolactone is preferred. Further, there can be employed a copolymer in which there are employed comonomers such as valerolactone, glycolide, and lactide other than ε-caprolactone monomer. As a lactone polymer other than the above-described ones, there may be also employed a polycaprolactone in which terminal groups are capped. The lactone polymer (B) in the present invention is obtained by a continuous or batchwise reaction at 120-230°C, preferably 140-220°C while agitating for several hours, in which a polymerization initiator is added to a lactone monomer and, preferably, and a catalyst is optionally employed. The polymerization initiator to be employed in the preparation of a lactone polymer (B) described in the present invention is water or a compound having hydroxyl groups at terminals and, as the compound having hydroxyl groups at terminals, there can be exemplified, for example, a monovalent alcohol such as n-hexyl alcohol, n-heptyl alcohol, n-octyl alcohol, n-nonyl alcohol, lauryl alcohol, and mylistyl alcohol, glycols such as ethylene glycol, propylene glycol, ethylethylene glycol, 1,4-butanediol, 2,3-butylene glycol, 2-methyl-1,2-propane diol, pinachol, β-butylene glycol, diethylene glycol, pentamethylene glycol, tetramethylene glycol, neopentyl glycol, and 1,4-cyclohexane dimethanol, trivalent alcohols such as glycerine, 1,2,3-butane triol, 1,2,3-pentane triol, trimethylol propane, and ditrimethylol propane, or derivatives thereof, tetravalent alcohols such as erythrit and pentaerythritol, aromatic alcohols such as phenol, bisphenol A, 2,4,6-tribromophenol, and tetrabromobisphenol A, monovalent carboxylic acids such as benzoic acid, p-methyl benzoic acid, lauric acid, myristic acid, 2,3,4-tribromobenzoic acid, pentabromobenzoic acid, divalent carboxylic acids such as isophthalic acid, phthalic acid, terephthalic acid, 2,6-naphthalene dicarboxylic acid, 4,4'-diphenoxyethane dicarboxylic acid, succinic acid, adipic acid, sebasic acid, azelaic acid, decadicarboxylic acid, cyclohexane dicarboxylic acid, tetrachlorophthalic acid, and tetrabromophthalic acid, trivalent carboxylic acids such as tricarbaryl acid, trimerysic acid, and trimeritic acid, tetravalent carboxylic acids such as pyromeritic acid, oxycarboxylic acids such as e-oxycarboxylic acid and hydroxyethoxy benzoic acid, etc. Further, as the catalyst for the polymerization, there can be employed a variety of organic or inorganic metal compounds, etc. and, specifically, there can be enumerated tetrabutyl titanate, tetraisopropyl titanate, tetraethyl titanate, dibutyltin oxide, dibutyltin laurate, stannous octylate, and stannous chloride, etc. Use amount of the catalysts is 0.1-1,000 ppm, and preferably 0.5-500 ppm based on starting raw materials. A molecular weight of the lactone polymer (B) to be employed in the present invention is 1,000-500,000, preferably 5,000-200,000, and more preferably 10,000-100,000 as a number average molecular weight. In the case that the number average molecular weight is less than 1,000, there is not shown an effect for improving a molding processability of the regenerated PET resin and, in the case of more than 500,000, it cannot be melt-kneaded into the regenerated PET resin. The number average molecular weight described herein is a number average molecular weight measured using a liquid chromatograph. <Polyolefin resin (C)> The polyolefin resin (C) to be employed in the composition of the present invention can be freely selected from an olefin polymer such as a low density polyethylene, a high density polyethylene, a linear-state polyethylene, a polybutadiene, a polypropylene, a poly-1-butene, a poly-1-pentene, a poly-4-methyl-1-pentene, and a mixture thereof, an ethylene-vinyl acetate copolymer, a copolymer of ethylene, propylene, 1-butene, 1-pentene, and a mixture thereof, a polyolefin-based elastomer such as an ethylene-propylene rubber (EPM, EPR), an ethylene-propylene-diene terpolymer (EPDM, EPD, EPT), and a mixture thereof, a mixture of the polyolefin-based elastomer with an olefin polymer such as polyethylene, a polypropylene, and an ethylene-propylene copolymer, a copolymer of other vinyl-based monomer primarily containing an olefin, or a mixture of two or more kinds of the above-described ones, and it includes a polyolefin resin (P) which is described hereinafter. Specifically, the polyolefin (C) resin includes a polyolefin resin (P), and there can be enumerated a vinyl chloride-based resin such as a vinyl chloride, a vinylidene chloride, a vinyl chloride copolymer, for example, a vinyl chloride-vinyl acetate copolymer, a vinyl chloride-ethylene copolymer, a copolymer in which vinyl chloride is grafted on an ethylene-vinyl acetate copolymer, a polystyrene, a styrene-based resin such as an acrylonitrile-butadiene-styrene copolymer, an acrylic-based resin, engineering plastic resins such as a polycarbonate, a polyethylene terephthalate, a polybutylene terephthalate, a polyphenylene oxide, and a polyphenylene sulphide, etc. Further, there is also included a resin containing at least one of the above-described various polymers. <Additives (D)> In the composition of the present invention, as the other additives (D), there can be mixed the inorganic compounds, the organic compounds, or the other additives for resins, etc. As the additives for resins, there are enumerated a stabilizer, a coloring agent, a weatherability agent (an ultraviolet ray absorbent), a lubricant, an antistatic agent, an extender, and other additives. There can be also added to the polyolefin resin (C) in addition to a case of being originally contained in the regenerated PET resin. <Formulating amount of respective components> In the regenerated PET resin composition of the present invention, 0.5-100 parts by weight of a lactone polymer (B) is preferably formulated based on 100 parts by weight of a regenerated PET resin (A), and 1-20 parts by weight of a lactone polymer (B) is more preferably formulated based on 100 parts by weight of a regenerated PET resin (A). In the case that the lactone polymer (B) is less than 0.5 part by weight, there is not shown an effect for improving a molding processability of the regenerated PET resin composition and, in the case of more than 100 parts by weight, there is caused a disadvantage of decline in a strength of a molded article. Formulation of 1-20 parts by weight in the lactone polymer (B) is particularly effective in a viewpoint of an improvement of moldability. The polyolefin resin (C) is preferably formulated in 1-100 parts by weight, preferably 20-100 parts by weight based on 100 parts by weight of a regenerated PET resin. By the formulation of the polyolefin resin (C), although there is shown an effect that moldability is improved, in the case of less than 1 part by weight, there is not shown an effect that moldability is improved and, on the other hand, in the case of more than 100 parts by weight, strength of a molded article tends to lower. <Method for the preparation and Method for molding of the regenerated PET resin composition> The composition of the present invention is usually prepared by publicly-known methods. For example, there is enumerated a method in which there are melt-kneaded the regenerated PET resin (A), the lactone polymer (B), and optionally, the polyolefin resin (c) and other additives (D) in an extruder, a kneader, a roll, and a Banbury mixer, or a method in which particle-state substances are mechanically and uniformly mixed each other, and then, molding is conducted together with mixing in an injection molding machine. Although thus-obtained regenerated PET resin composition may be once extruded to prepare pellets, preferably, it is simultaneously or subsequently molded to prepare a molded article by an extrusion molding, an injection molding, and compression molding, etc. together with mixing. The molded article is also excellent in heat resistance and an electric insulation property in addition to mechanical properties. <Uses of the regenerated PET resin composition> The regenerated PET resin composition of the present invention can be employed for a variety of molded articles in place of conventional thermoplastic resins. For example, it is useful for home electric appliances, specifically, a cover for a refrigerator, a condenser cover for a washer, a backside cover for a TV, a speaker box for a TV, a deflecting york for a TV, a plug and socket, a socket for a christmas light, a CRT monitor body, an impeller in a blowing outlet for an air conditioner, a wind-direction plate and a cover for a body, a cover for a moisture conditioner, a door for a microwave oven, a seat for a water closet and a hot water tank, a motor cover and a control panel for an electric fan, a connector, a toner box for a PPC, a cover for a ventilating fan, materials for civil engineering and construction, specifically, a trough, a cover for buried electric cables, a pipe cover, monofilaments for flat yarns and a laminate film, a chair and backside cover in an athletic field, a flower pot for plants, an OA floor, materials for cars, specifically, a corrugate tube for electric cables, a floor mat, a door rim, a seat and a lining for a trunk room, a battery case, a cooling fan for a radiator, a protecting plate in an engine room, an instrument panel, a trim for internal decoration, a globe box, a console box, a fan shroud, a housing for an air cleaner, a seat frame, a connector, an ash tray, others, a PP band, a variety of connectors, a pallet, a container, and tray, etc. <Examples> Hereinafter, although the invention is specifically illustrated by Examples and Comparative Examples, the present invention is not limited thereto. It is to be noted that a variety of test methods conducted in the Examples and Comparative Examples were according to the following methods. <Pelletizing property test> Pelletizing was conducted using a twin-screw extruder having a screw diameter of 30 mm. Conditions in pelletizing were visually observed, and a pelletizing property was judged by the following standards. o ○: exceedingly excellent, ○: excellent, Δ: slightly worse, ×: worse, ××: incapable of pelletizing <Injection moldability test> Test pieces having 127 x 12.7 x 1.6 mm were prepared using an injection molding machine having a locking pressure of 40 tons. Outer appearance of molded articles was visually observed, and an injection moldability was judged by the following standards. o ○: exceedingly excellent, ○: excellent, Δ: slightly worse, ×: worse, ××: incapable of molding <Strength test> According to JIS K7113, tensile strength and tensile elongation were measured. <Number average molecular weight of an improver (a lactone polymer)> In the lactone polymer employed, a number average molecular weight was measured by the following conditions. Apparatus: HPLC MODEL LC-6A (manufactured by Shimadzu Seisakusyo, Ltd.) Guard column: SHODEXKF-800P (10 mm x 4.6 mmø) 1 piece Column: SHODEX KF-804 (0.3 mm x 8 mmø) 1 piece, KF-802.5 (0.3 m x 8 mmø) 1 piece, KF-801 (0.3 m x 8 mmø) 1 piece Detector: Shodex RI SE-51 (manufactured by Showa Denko, Ltd.) Solvent: tetrahydrofran, chloroform or hexafluoroisopropanol Solvent flow speed: 1 ml/min. Column temperature: 40°C Sample volume: 20 µl which is 10 times-diluted by a solvent <Examples and Comparative Examples of the invention (Examples 1-3 and Comparative Examples 1-3)> In Examples 1-3, as the lactone polymer (B), 5 parts by weight of respective lactone resins (B1-B3) described hereinafter were blended with 100 parts by weight of a regenerated PET resin (A) (a trade name: PET-BTL, manufactured by Taisei Jushi, Ltd.) as illustrated in Table 1-1 described hereinafter. Accordingly, addition amount of the lactone polymer (B) is 5 parts by weight based on 100 parts by weight of the regenerated PET resin (A). Mixture obtained was pelletized at a molding temperature of 255°C by melt-kneading using the twin-screw extruder having a screw diameter of 30 mm. Further, test pieces having a fixed shape were molded from pellets obtained at a molding temperature of 255°C and a mold temperature of 25°C using the injection molding machine having a locking pressure of 40 tons, and strength was measured according to a JIS regulation. Results are shown in Table 1-1. (Comparative Example 1) In the Comparative Example 1, the same procedures were likewise followed as in the Example 1 except that the lactone polymer (B) was not added. Example 1 Example 2 Example 3 Comparative Example 1 Regenerated PET resin (A) 100 100 100 100 Improver (B1) 5 0 0 0 Improver (B2) 0 5 0 0 Improver (B3) 0 0 5 0 Pelletizing property ○ ○ ○ x Injection moldability o ○ o ○ o ○ xx Tensile Strength (kg/cm 2 ) 578 594 624 - Tensile elongation (%) 140 145 150 - In the Table, the lactone polymer is represented as an improver. Further, the Table represents an improver (B1)=trade name: PLACCEL H1P (a poly-ε-caprolactone having a number average molecular weight of 10,000 manufactured by Daicel Chemical Industries, Ltd.), an improver (B2)=trade name: PLACCEL H4 (a poly-ε-caprolactone having a number average molecular weight of 40,000 manufactured by Daicel Chemical Industries, Ltd.), and an improver (B3)=trade name: PLACCEL H7 (a poly-ε-caprolactone having a number average molecular weight of 70,000 manufactured by Daicel Chemical Industries, Ltd.) (the same in the Tables 1-2 and 1-3). (Examples 4-6 and Comparative Example 2) Test pieces were likewise prepared as in the Example 1 except that the fixed amount of the lactone polymer was changed as shown in Table 1-2, respectively, to evaluate the pelletizing property, injection moldability, and strength test. Results are shown in Table 1-2. In the Examples 4-6, the lactone polymer (B) is 10 parts by weight based on 100 parts by weight of the regenerated PET resin (A). In the Comparative Example 2, the same procedures were likewise followed as in the Example 1 except that the lactone polymer (B) was not added. Example 4 Example 5 Example 6 Comparative Example 2 Regenerated PET resin (A) 100 100 100 100 Improver (B1) 10 0 0 0 Improver (B2) 0 10 0 0 Improver (B3) 0 0 10 0 Pelletizing property o ○ o ○ o ○ x Injection moldability ○ ○ ○ xx Tensile Strength (kg/cm 2 ) 564 578 594 - Tensile elongation (%) 140 145 145 - (Examples 7-8 and Comparative Example 3) Test pieces were likewise prepared as in the Example 1 except that a polypropylene (a trade name: MA4 manufactured by Mitsubishi Kagaku, Ltd.) was formulated in respective fixed amount shown in Table 1-3 as a polyolefin resin (C), and at a processing temperature of 240°C in a pelletizing property and injection molding, followed by evaluating an extruding processability, injection moldability, and strength. Results are shown in Table 1-3. It is to be noted that in the Example 7, the lactone polymer (B) is 5 parts by weight based on 100 parts by weight of the regenerated PET resin (A) and, in the Example 8, it is 10 parts by weight. In the Comparative Example 3, the lactone polymer (B) is not added. Example 7 Example 8 Comparative Example 3 Regenerated PET resin (A) 100 100 100 Improver (B3) 5 10 0 Polypropylene 100 100 100 Pelletizing property o ○ o ○ x Injection moldability o ○ o ○ xx Tensile Strength (kg/cm 2 ) 328 315 - Tensile elongation (%) 180 185 - As being distinct from the Table 1-1 to Table 1-3, pelletizing and injection molding are possible without any problems in the Examples 1-8 in which the resin composition of the present invention is employed, and strength was also excellent in molded articles obtained. In the Comparative Examples 1-3, a pelletizing property is problematic, and molding was not able to conduct by an injection molding machine. POSSIBILITY OF UTILIZATION IN INDUSTRY According to the invention, pelletizing and injection molding are possible in the regenerated PET resin, and there can be obtained a regenerated PET resin composition and a molded article therefrom which have an excellent mechanical strength.

Claims: A regenerated PET resin composition which comprises 100 parts by weight of a regenerated PET resin (A) and 0.5-100 part by weight of a lactone polymer (B). A regenerated PET resin composition as claimed in claim 1, wherein it further contains a polyolefin resin (C). A regenerated PET resin composition as claimed in claim 1 or 2, wherein it further contains other additives (D) which are an inorganic compound or an organic compound. A regenerated PET resin composition according to any one of claims 1 to 3, wherein said regenerated PET resin (A) is a resin recycled and treated in order to utilize after the PET was molded and used as a product such as bottles for beverages, textiles, films, and a large-sized molded article such as container, and it is usually called a regenerated PET material or a recycled PET. A regenerated PET resin composition according to any one of claims 1 to 4, wherein said regenerated PET resin (A) is selected from the group consisting of bottles for beverages, textiles, films, a molded article, and a PET material such as chips of films and gates or runners in injection-molded articles which are produced in the preparation of final products, even though those are not employed as the final products. A regenerated PET resin molded article which is molded from the regenerated PET resin composition as claimed in any one of claims 1-5.

Inventors: ENDO SHUNICHI, MIZUTANI YOSHINOBU, OCHIAI GENICHIRO, ENDO, SHUNICHI, MIZUTANI, YOSHINOBU, OCHIAI, GENICHIRO
Applicants: DAICEL CHEM, DAICEL CHEMICAL INDUSTRIES, LTD.
Application year: 1999
Main classification: C08L67
IPC codes: C08K5, C08L23, C08L101, C08L67