ONE-PART ORGANOPOLYSILOXANE RUBBER COMPOSITION FOR USE AS A CORROSION PROTECTION COATING

Abstract: The present invention relates to a one-part room temperature vulcanisable organopolysiloxane rubber composition which crosslinks in the presence of moisture to form a coating for the corrosion protection of metals. The one-part organopolysiloxane rubber composition comprises the product which is obtained by mixing the following: a) from about 20 to about 50 weight percent of one or more polydiorganosiloxane fluids of the formula R"[(R)2SiO]nR'; b) from 0 to about 40 weight percent of a cycloorganosiloxane of the formula [(R)2SiO]n; c) from 0 to about 40 weight percent of an inorganic extending or non-reinforcing filler; d) from about 0.5 to about 10 weight percent of an amorphous SiO2 reinforcing filler; e) from about 1 to about 7 weight percent of an oximosilane cross-linking agent of the formula: RSi(ONR'2); f) from about 0.2 to about 3 weight percent of an adhesion promoter of formula (I); g) from about 0.02 to about 3 weight percent of an organotin salt as a condensation catalyst.

Description: TITLE : ONE-PART ORGANOPOLYSILOXANE RUBBER COMPOSITION FOR USE AS A CORROSION PROTECTION COATING FIELD OF THE INVENTION This invention relates to a one-part room temperature vulcanizable organopolysiloxane rubber composition that does not contain volatile organic compounds (VOC) and which crosslinks in the presence of moisture to form a coating for use as a corrosion protection, waterproofing, anti-fouling or weathering protection of surfaces, or for secondary containment of liquid spills, or high voltage insulator coating. BACKGROUND OF THE INVENTION The protection of surfaces against environmental effects is important in many different applications. For example, metal and other surfaces such as concrete exposed to moisture such as rain or fog in combination with contaminated atmospheres as are found in industrial locations may be subject to extensive corrosion unless protected in some way from exposure to the corrosive atmosphere. Other potentially corrosive environments include along sea coasts where salt spray is found and in areas where agricultural chemicals are widely distributed. In addition, metal and concrete surfaces directly exposed to water such as marine structures and vessels are also subject to the potential for extensive corrosion. Currently, such surfaces are most commonly protected by being painted with alkyd based paints. Such paints form a relatively rigid coating on the surface which can become brittle and when subjected to stress, can flake or chip off, thereby exposing the underlying surface to the corrosive elements. In addition, such paints generally are susceptible to UV damage thereby further reducing their effective life. Two-part organopolysiloxane rubber compositions for use as a corrosion protection coating on metals have been developed. For example, Lampe describes in U.S. Patent No. 4,341,842 a two-part room temperature vulcanizable composition for coating the underside of vehicles to protect the metal from rusting or being corroded by road salts or other similar compounds. However, such two-part compositions have a major disadvantage in that they require the use of complex dual mixing and spray nozzle apparatus or require pre-mixing and immediate use on site when used with conventional spray equipment. If conventional spray equipment is used, the amount of material pre-mixed must also be exact to prevent wastage as the composition has a finite pot life. One part compositions for coating of surfaces have also been described. Such compositions generally utilize a volatile organic solvent such as petroleum naphtha, toluene, petroleum ether and chlorinated hydrocarbons as a diluent to improve the working efficiency and ease of application of the coating composition. If no solvent is utilized, the coating compositions are difficult to apply due to high viscosity. The use of solvent creates environmental pollution and potential danger to the health of workers as it evaporates. Yaginurua et al in US Patent No. 5,445,873 describe a solventless coating that cures at room temperature through a condensation reaction. The coating is designed for packaging circuit boards and does not require high physical strength. The composition utilizes a low molecular weight organopolysiloxane with a viscosity in the range of 20 to 500 centipoise. Another solventless coating composed of silicone resin and polydiorgano-silicone fluid has been described in US Patent 4,780,338. The coating requires elevated temperatures for curing which requires the heating of the substrate or oven drying after the coating is applied. US Patent 4,929,703 also describes a solventless coating composed of A) silicone resin reaction product prepared by hydrolyzing, then neutralizing an equilibrated mixture of a silane and a diorganopolysiloxane, B) a silane and C) diorganopolysiloxane fluid. The coating cures when exposed to moisture as a result of condensation reaction of siloxane to form a matrix. Many other applications where silicone coatings are used include waterproofing, anti fouling and high voltage insulating coatings among others. Such applications generally use either a one part or two part composition as described above, which are subject to the same problems. There still remains a need for a one part room temperature vulcanizable silicone coating composition which is easily applied to surfaces as a protective coating and which does not contain volatile organic components (VOC) . SUMMARY OF THE INVENTION The present invention provides a VOC free, one part room temperature vulcanizable coating for easy and convenient application by conventional methods such as dipping, flow or spraying. The coating provides a guard against environmental effects along with high physical strength and adhesion achieved with a suitable blend of reinforcing and extending fillers. In one aspect, the present invention provides for a one-part room temperature vulcanizing organopolysiloxane rubber composition for use as a protection coating surfaces. The composition comprises the product which is obtained by mixing the following: a) fromabout 20 to about 60 weight percent of one or more polydiorganosiloxane fluids of the formula R"0[ (R) 2 SiO] n R' in which R is a monovalent alkyl or alkylene radical having 1 to 8 carbon atoms or a phenyl radical, R' is a monovalent alkyl or alkylene radical having 1 to 8 carbon atoms or a phenyl radical, R" is OH or a monovalent alkyl or alkylene radical having 1 to 8 carbon atoms or a phenyl radical and n has an average value such that the viscosity is from about 1 to about 100,000 centipoise at 25 °C, wherein at least one of the polyorganosiloxane fluid has R" equal to OH and n has an average value such that the viscosity is in the range from 1,000 to 100,000 centipoise at 25°C, preferably from 3,000 to 40,000 centipoise at 25°C; b) from 0 to about 40 weight percent of a cyclo- organosiloxane of the formula [(R) 2 SiO] n in which R is a monovalent alkyl or alkylene radical having 1 to 8 carbon atoms or a phenyl radical which may optionally be substituted with an alkyl radical having 1 to 8 carbon atoms and n has an average value of 3 to 10 c) from 0 to about 40 weight percent of an inorganic extending or non-reinforcing filler d) from about 0.5 to about 10 weight percent of an amorphous Siθ2 reinforcing filler having a surface area of between about 100 to 250 m 2 /g and a particle size range between about 0.01 and 0.03 microns; e) from about 1 to about 7 weight percent of an oximosilane cross-linking agent of the formula; RSi (ON=CR' 2 ) 3 in which R and R' are independently selected from monovalent alkyl or alkylene radicals having 1 to 8 carbon atoms or a phenyl radical which may optionally be substituted with an alkyl radical having 1 to 8 carbon atoms ; f) from about 0.2 to about 3 weight percent of an adhesion promoter of the formula 1 (R 2 0) 3 _ b SiR 1 2 3 in which R and R are independently selected from monovalent alkyl or alkylene radicals having 1 to 8 carbon atoms or a phenyl radical which may optionally be substituted with an alkyl radical having 1 to 8 carbon atoms, b is an integer between 0 and 3, and R is a saturated, unsaturated or aromatic hydrocarbon radical having 1 to 10 carbon atoms which may optionally contain a functional group; and g) from about 0.02 to about 3 weight percent of an organotin salt as a condensation catalyst. In an aspect of the invention, the composition is for coating high voltage electrical insulators and further includes about 36 to about 48 weight percent of alumina trihydrate, the alumina trihydrate having a median particle size of 13. μm, containing 65.1 percent Al 2 0 3 , 34.5 percent combined H 2 0, 0.3 percent Na 2 0, 0.02 percent CaO, 0.01 percent Si0 2 and having a specific gravity of 2.42, the aluminum trihydrate being present in a proportion of 90 to 110 parts by weight per 100 parts by weight of the polyorganosiloxanes . The present invention also provides for a method of protecting exposed surfaces particularly metal or concrete surfaces from environmental effects. The method comprises applying to the surface a thin layer of the above one-part organopolysiloxane rubber composition and allowing the layer of the one-part organopolysiloxane rubber composition to cure at room temperature to a silicone elastomer. The present invention also provides for the surfaces coated with the silicone elastomer formed from the curing of the one-part organopolysiloxane rubber composition. DETAILED DESCRIPTION OF THE INVENTION The one-part organopolysiloxane rubber compositions of the present invention are ideally suited for protection of surfaces from environmental effects. Such protection includes corrosion protection of metal or concrete surfaces and structures against salt spray and chemical environments including direct exposure to salt water, salt fog, gases and other industrial pollutants. The compositions of the present invention can also be used to coat metal surfaces of motor vehicles which may be exposed to high salt condition during the winter season. The compositions with suitable additives also provide protection against the effects of weathering from exposure to among others UV radiation. The compositions of the present invention are particularly useful on marine installations, such as anti-fouling coatings of ship hulls, oil rigs, docks, piers, buoys, water intake pipes and various submerged structures. The coating composition of the present invention is also useful for coating electric transmission towers and bridges for corrosion protection of metal or concrete structures directly exposed to salt water and industrial pollution, especially sulfur based. The composition containing alumina trihydrate can be utilized as a protective coating on electrical insulators providing both corrosion and leakage current protection. The coating composition can also be utilized for forming an impervious layer by coating textiles such as Geo Tech or nylon, cotton or other fabrics to be used as chemical containment or as tents, awnings, canopies, etc. The absence of volatile organic components (VOC) in the coating composition makes it ideal for use in contained areas where minimum levels of VOC is required. The one-part organopolysiloxane rubber compositions of the present invention for use as a protective coating contain about 20 to about 60 weight percent of one or more polydimethylsiloxane fluids of the formula: R"0[(R) 2 SiO] n R' in which R is a monovalent alkyl or alkylene radical having 1 to 8 carbon atoms or a phenyl radical, R' is a monovalent alkyl or alkylene radical having 1 to 8 carbon atoms or a phenyl radical, R" is OH or a monovalent alkyl or alkylene radical having 1 to 8 carbon atoms or a phenyl radical and n has an average value such that the viscosity is from about 1 to about 100,000 centipoise at 25 °C. At least one of the polyorganosiloxane fluids is a higher viscosity siloxane having reaction groups in which R" is equal to OH and n has an average value such that the viscosity is in the range from 1,000 to 100,000 centipoise at 25°C, preferably from 3,000 to 40,000 centipoise at 25°C. The polydimethylsiloxanes may contain small amounts of monomethylsiloxane units and methyl radical replaced with other radicals in small amounts as impurities such as is found in commercial products, but the preferred fluid contains only polydimethylsiloxane. The composition may contain a second linear dimethyl polysiloxane of low molecular weight to act as a viscosity reducer for the composition for ease in applying the composition to the surface. The low molecular weight linear dimethyl polysiloxanes are end blocked oligomeric compounds of the above formula where R, R' and R" may be the same or different and are independently selected from a monovalent alkyl or alkylene radical having 1 to 8 carbon atoms or phenyl radical . The average value of n ranges between 4 and 24, preferably between 4 and 20. If the composition contains the two different polysiloxanes set out above, the total of the polysiloxanes is generally about 40 to 60 weight percent with the relative amounts of the two polysiloxanes being selected based upon the desired characteristics of the final coating. Generally each of the polysiloxanes will be present in a ratio of from about 30 weight percent to about 70 weight percent based upon the total weight of the polysiloxane fluids. In addition to, or in place of the low molecular weight linear dimethyl polysiloxanes, the composition may contain up to about 40 weight percent, more preferably 20 to 30 weight percent of a cyclo-organosiloxane of the formula: [(R) 2 SiO] n in which R is a monovalent alkyl or alkylene radical having 1 to 8 carbon atoms or a phenyl radical which may optionally be substituted with an alkyl radical having 1 to 8 carbon atoms and n has an average value of 3 to 10. The preferred cycloorganosiloxane is a cyclic dimethylsiloxane and is used in a similar manner to the low molecular weight linear dimethyl polysiloxanes to lower the viscosity of the composition for convenient application by spraying, brushing or dipping. The composition also contains 5 to 40 weight percent, more preferably 15 to 30 weight percent of inorganic extending or non-reinforcing fillers to increase the resistance of the coating to environmental effects, including high temperature stability of the cured product. The extending fillers are preferably selected from inorganic materials such as calcium carbonate, barium sulfate, iron oxide, diatomaceous earth, melamine, quartz, crystalline silica, titanium dioxide, alumina trihydrate, zinc oxide, zirconium oxide and chromic oxide. The selection of the filler will be based upon the required properties and the final usage of the composition. Thus, for applications where high temperature resistance is not required, such as corrosion protection coating of electrical power systems, roof coatings, etc., the preferred filler will be calcium carbonate, diatomaceous earth or quartz. For applications where high temperature stability is required, such as coating exhaust pipes and mufflers of motor vehicles, the preferred filler will be melamine, iron oxide, zinc oxide, titanium dioxide, zirconium oxide or zinc chromate. For coatings requiring higher strength crystalline silica is utilized while for coatings for electrical insulators, the composition will contain alumina trihydrate to provide leakage current protection. In an aspect of the invention, the composition is for coating high voltage electrical insulators and further includes about 36 to about 48 weight percent of alumina trihydrate, the alumina trihydrate having a median particle size of 13. μm, containing 65.1 percent Al 2 0 3 , 34.5 percent combined H 2 0, 0.3 percent Na 2 0, 0.02 percent CaO, 0.01 percent Si0 2 and having a specific gravity of 2.42, the aluminum trihydrate being present in a proportion of 90 to 110 parts by weight per 100 parts by weight of the polyorganosiloxanes . The amount of filler may be increased within the range to improve the desired properties. The composition also contains about 0.5 to 5 weight percent of an amorphous Si0 2 reinforcing filler having a surface area of between about 100 to 250 m 2 /g and a particle size range between about 0.01 and 0.03 microns. The specific gravity of the filler is preferably about 2.2 The composition also contains about 1 to 7 weight percent, preferably 2 to 5 weight percent of an oximinosilane cross linking agent. Preferably the oximinosilane cross linking agent is of the formula RSi (ON=CR' 2 ) 3 in which R and R' each represent a monovalent alkyl or alkylene radical having 1 to 8 carbon atoms or a phenyl radical, preferrably an alkyl radical such as methyl, ethyl, propyl, butyl, or an alkylene radical such as vinyl, allyl, or a phenyl radical. The preferred R and R' are alkyl or vinyl radicals, most preferably methyl and ethyl radicals. The composition also contains about 0.2 to 3 weight percent of an organo functional silane as an adhesion promoter. Preferably the organo functional silane has the formula wherein R 2 and R 3 are independently selected from monovalent alkyl or alkylene radicals being 1 to 8 carbon atoms or a phenyl radical, b is an ** from 0 to 3 , preferably 0, and R is a saturated, unsaturated or aromatic hydrocarbon radical being 1 to 10 carbon atoms, which may be further functionalized by a member selected from the group consisting of amino, ether, epoxy, isocyanate, cyano, acryloxy and acyloxy and combinations thereof . R 2 and R 3 are preferably an alkyl radical such as, for example, methyl, ethyl, propyl, butyl, or an alkylene radical such as vinyl and allyl. More preferably R 2 and R 3 are alkyl radicals, most preferably methyl, ethyl or propyl radicals. Preferably R is an alkyl group, more preferably further functionalized by one or more amino group. The most preferred organo-functional silane is N- (2-aminoethyl-3-aminopropyl) trimethoxysilane. In all of the above compounds, the alkyl includes straight, branced or cyclic radicals. Among the alkyl groups are Cι_ 8 straight or branched-chain alkyl such as, for example, methyl, ethyl, propyl, isopropyl, n-butyl, isobutyl, tert-butyl, pentyl, isopentyl, hexyl, etc., the cycloalkyl are C 3 -. 8 cycloalkyl such as, for example, cyclopropyl, cyclobutyl, cyclohexyl, etc., the alkylene groups are Cι_ 8 alkylene such as, for example, vinyl and allyl. The above groups as well as the phenyl radicals may be further functionalized by including in the chain or ring structure, as the case may be, a group selected from the class consisting of amino, ether, epoxy, isocyanate, cyano, acryloxy, acyloxy and combinations, so long as the functionalization does not adversely affect the desired properties of the compound. The composition additionally contains about 0.02 to 3 weight percent of an organotin salt of a carboxylic acid as a condensation catalyst, which accelerate the aging of the composition. Preferably the organotin salt is selected from the group dibutyltin diacetate, stannous octoate, dibutyltin dioctoate and dibutyltin dilaurate. Most preferably the organotin salt is dibutyltin dilaurate of the formula: (C 4 H 9 ) 2 Sn (OCOCιoH 20 CH 3 ) 2 . The composition may contain other optional ingredients such as pigments and other fillers in minor amounts provided that the addition of the ingredients does not cause degradation of the desired properties of the cured coating made from the composition. One commonly utilized optional ingredient is a pigment, preferably a gray pigment, most preferably present in amounts up to about 1 weight percent . The organopolysiloxane composition of the present invention is prepared by mixing the ingredients together in the absence of moisture. The silane is moisture sensitive and will undergo cross-linking in the presence of moisture such that the mixture must be essentially absent of free moisture when the silane is added and maintained in a moisture free state until cure is desired. A preferred method of mixing comprises mixing the polysiloxane fluids with the extending and reinforcing fillers and other optional fillers and pigments. Thereafter, the oximinosilane and organo-functional silane are added and mixed under a nitrogen atmosphere. The organotin salt is added to the mixture and the mixture is then dispensed in sealed containers for storage prior to use. The surface to be protected is coated with the composition by conventional methods such as dipping, brushing or spraying. Preferably, the surface to be protected is coated by spraying one or more applications of the composition of the present invention. The thickness of the coating will depend upon the specific requirements of the application and the desired level of protection. The coating generally has an average thickness of 250 to 1500 microns more preferably, an average thickness of 500 to 1000 microns, most preferably about 500 to 750 microns After the coating is formed on the surface, the surface is exposed to normal atmosphere for cross-linking and cure of the coating. The improved coating of the present invention is capable of protecting surfaces from environmental effects including metal and concrete surfaces from corrosion in the presence of moisture such as rain or fog in combination with contaminated atmospheres, salt spray or fog or direct exposure to salt water. The improved coating of the present invention is particularly useful for protecting metal surfaces which are directly exposed to salt water. Such surfaces include the hulls of ships and other vessels, oil drilling rigs, harbour and pier structures, etc. When the coating is used on the hulls of ships, further benefits such anti-fouling in addition to the corrosion protection are achieved. The coating does not allow marine animals, such as barnacles, to easily attach to the surface. Any such animals which attempt to attach to the surface are generally removed from the surface by high pressure washers. Additionally, clean up of the surface is generally accomplished by high pressure wash and/or hand or mechanical wiping and does not require the scraping operations commonly utilized during hull cleaning of ships, or other marine installations. As clean up of surfaces coated with the composition of the present invention is easily accomplished, the composition can also be used as an anti-graffiti coating on surfaces. The following examples are included to illustrate preferred embodiments of the invention and to demonstrate the usefulness of the coating and are not intended to limit in any way the scope of protection for the invention. EXAMPLE 1 To 36 parts by weight of dimethyl polysiloxane fluid having a viscosity of 16,750 centipoise at 25°C and 22 parts by weight of dimethyl siloxane cyclic is added 35 parts by weight of a mixture of amorphous and crystalline silica fillers having a specific gravity of 2.2 and surface area of about 130m 2 /g. Then 2 parts by weight of pigment is added and the composition is mixed in a mixer to a uniform consistency. Then 3 parts by weight of methyl tris- (methyl ethyl ketoxime) silane and 1 part by weight of N- (2-aminoethyl-3 aminopropyl) trimethoxysilane are added and mixed under a nitrogen atmosphere. Finally, 0.1 part of dibutyltin dilaurate is added to the dispersion and mixed until a uniform consistency is achieved. Coupon samples prepared from stainless and carbon steel and aluminum sheet were coated with the composition prepared according to Example 1 by dipping into the mixture and exposing the samples to normal atmosphere for crosslinking. The coupon samples, having an average coating thickness of 300 microns, were exposed to salt-fog testing in an electrical (ozone producing) environment. After 2000 hours of continuous exposure, the coating showed no evidence of deterioration or separation from the virgin metal surfaces . Uncoated samples of both metals showed severe etching and corrosion. Carbon steel sheet samples were coated with the composition according to Example 1 by dipping into the mixture and exposing the samples to normal atmosphere for crosslinking. The samples, having an average coating thickness of 320 microns, were exposed to accelerated heat aging at 260°C. After 7 days of continuous exposure, the coating showed no evidence of deterioration or separation from the virgin metal surface . Carbon steel coupons coated with the composition of Example 1 to a thickness of 500 microns were immersed 30 days in an algae producing environment of ocean water at room temperature. Considerable deposits of algae were present which were easily removed by wiping with a damp cloth. The original surface of the coating showed no changes, scratches or deformations. The improved flexibility of the coating and its resistance to cracking was confirmed utilizing carbon steel coupons coated with 300 microns thick coating. The samples were bent 180° along a curve showed no cracks or separation from substrate. EXAMPLE 2 A composition useful for high temperature protection was prepared by using 37 parts by weight of dimethyl polysiloxane fluid having a viscosity of 3,300 centipoise at 25 °C and 20 parts of dimethyl siloxane cyclics and 4 parts by weight of titanium dioxide was then added. Then 3 parts by weight of methyl tris- (methyl ethyl ketoxime) silane, 1 part by weight of N- (2-aminoethyl-3 aminopropyl) trimethoxysilane and 0.05 part by weight of dibutyltin dilaurate are added under a nitrogen atmosphere. Then 32 parts by weight of mixture of amorphous and crystalline silica fillers having a specific gravity of 2.2 and surface area of 150 m 2 /g was added. Finally, 6 parts by weight of melamine was added and mixed well to uniform consistency. Adhesion tests of the above formulation were performed by applying a thin coating on the stainless steel, carbon steel, aluminum, wood and glass. The coating was cured at standard conditions (room temperature 25 °C and 50 relative humidity) for 7 days and then peeled by applying a cut on the surface. The coating exhibited excellent adhesion of all tested materials. Several sheets of 200-micron thickness were prepared from the above product and cured for 7 days at standard conditions. Physical properties, such as elongation, tensile stress, tear resistance and hardness of the each sheet were tested before and after immersion into engine oils at 150°C e.g. Mobile 10W-30, Valvoline 10W-30 and automatic transmission fluid. No degradation or significant decrease in any physical property was observed. The product showed excellent oil resistance at elevated temperature . Results of Oil Resistance Test of the Cured Product The formulation was also tested for flame retardancy by Underwriter Laboratories Inc. (UL 94-V-O) and the product successfully passed the flame retardancy test. EXAMPLE 3 A first composition for coating electrical insulators was prepared by mixing 30 parts by weight of dimethyl polysiloxane fluid having a viscosity of 20,000 centipoise at 25 * C and 20 parts by weight of cyclic dimethyl siloxane then adding 2 parts by weight of amorphous silica having a specific gravity of 2.2 and surface area of about 150 m 2 /g. Then 2 parts by weight of methyl tris- (methyl ethyl ketoxime) silane and 1 part by weight of N- (2-aminoethyl-3 aminopropyl) trimethoxy silane are added and mixed under nitrogen atmosphere. Then 35 parts by weight of alumina trihydrate are added and mixed well to uniform consistency. The viscosity and sag of the mixture was checked and adjusted to 1000 ± 300 centipoise and 35 ± 10 on Leneta Scale by adding extra amount of dimethoxy polysiloxane cyclics and amorphous silica respectively. Finally, 0.1 part by weight of dibutyltin dilaurate is added and mixed thoroughly. EXAMPLE 4 A second electrical insulator coating composition was prepared by mixing 30 parts by weight of dimethyl polysiloxane fluid having a viscosity of 20,000 centipoise at 25 °C and 29 parts by weight of linear dimethyl polysiloxane of viscosity of 50 centipoise at 25 °C, then adding 2 parts by weight of amorphous silica having a specific gravity of 2.2 and surface area of about 150 m 2 /g. Then 2 parts by weight of methyl tris- (methyl ethyl ketoxime) silane and 1 part by weight of N- (2-aminoethyl-3 aminopropyl) trimethoxy silane are added and mixed under nitrogen atmosphere. Then 35 parts by weight of alumina trihydrate are added and mixed well to uniform consistency. The viscosity and sag of the mixture was checked and adjusted to 1000 ± 300 centipoise and 35 ± 10 on Leneta Scale by adding extra amount of dimethoxy polysiloxane linears and amorphous silica respectively. Finally, 0.1 part by weight of dibutyltin dilaurate is added and mixed thoroughly . Compositions of the present invention are also useful for protecting other types of surfaces from corrosive environments. For example, compositions of the present invention are particularly useful for protecting surfaces for spillage containment around tank farms and the like. The composition may be coated onto a heavy-duty fabric which is then utilized to line the interior of the spillage catch basins around the tank farm. Samples of heavy-duty Geo fabric were sprayed with the composition of the present invention to coat the fabric . Treated and untreated samples of fabric were exposed to caustic soda solution, diesel oil, furnace oil by placing samples of these materials on the surface of the fabric for up to seven days . No deterioration of the treated fabric was observed and the deposits of the material were easily able to be cleaned up without any noticeable loss of weight of the material. In contrast, untreated fabric did not retain the material on the surface and the caustic soda solution caused deterioration of the untreated fabric material within 24 hours. The compositions of the present invention are useful in many instances where protection of surfaces against environmental effects is desired. These compositions include the composition of the above examples as well as other compositions, the formulation of which is well within the skill of the ordinary workman in the art. The selection of the various components and their proportions would be immediately apparent depending upon the desired properties of the final coating. The compositions of the present invention overcome many of the problems associated with prior art compositions being a one part coating composition, which is easy to apply using any of the commonly employed methods and which is VOC free, thus satisfying the elimination or reduction in environmental pollution and potential danger to the health of workers caused by VOC containing compositions. While the invention has been described in reference to specific embodiments it should be understood by those skilled in the art that various changes can be made and equivalents may be substituted without departing from the true spirit and scope of the invention. All such modifications are intended to be within the scope of the claims appended hereto .

Claims: THE EMBODIMENTS OF THE INVENTION IN WHICH AN EXCLUSIVE PROPERTY OR PRIVILEGE IS CLAIMED ARE AS FOLLOWS: 1. A one-part organopolysiloxane rubber composition for use as a corrosion protection coating on metals comprising the product which is obtained by mixing the following: a) from about 20 to about 50 weight percent of one or more polydiorganosiloxane fluids of the formula R" [ (R) 2 SiO] n R' in which R is a monovalent alkyl or alkylene radical having 1 to 8 carbon atoms or a phenyl radical, R' is a monovalent alkyl or alkylene radical having 1 to 8 carbon atoms or a phenyl radical, R" is OH or a monovalent alkyl or alkylene radical having 1 to 8 carbon atoms or a phenyl radical and n has an average value such that the viscosity is from about 1 to about 100,000 centipoise at 25 °C, wherein at least one of the polyorganosiloxane fluid has R" equal to OH and n has an average value such that the viscosity is in the range from 1,000 to 100,000 centipoise at 25°C, preferably from 3,000 to 40,000 centipoise at 25°C; b) from 0 to about 40 weight percent of a cyclo- organosiloxane of the formula [ (R) 2 SiO] n in which R is a monovalent alkyl or alkylene radical having 1 to 8 carbon atoms or a phenyl radical which may optionally be substituted with an alkyl radical having 1 to 8 carbon atoms and n has an average value of 3 to 10; c) from 0 to about 40 weight percent of an inorganic extending or non-reinforcing filler; d) from about 0.5 to about 10 weight percent of an amorphous Si0 2 reinforcing filler having a surface area of between about 100 to 250 m 2 /g and a particle size range between about 0.01 and 0.03 microns; e) from about 1 to about 7 weight percent of an oximosilane cross-linking agent of the formula; RSi(ON=CR' 2 ) 3 in which R and R' are independently selected from monovalent alkyl or alkylene radicals having 1 to 8 carbon atoms or a phenyl radical which may optionally be substituted with an alkyl radical having 1 to 8 carbon atoms; f) from about 0.2 to about 3 weight percent of an adhesion promoter of the formula in which R and R are independently selected from monovalent alkyl or alkylene radicals having 1 to 8 carbon atoms or a phenyl radical which may optionally be substituted with an alkyl radical having 1 to 8 carbon atoms, b is an integer between 0 and 3, and R is a saturated, unsaturated or aromatic hydrocarbon radical having 1 to 10 carbon atoms which may optionally contain a functional group; and g) from about 0.02 to about 3 weight percent of an organotin salt as a condensation catalyst. 2. A composition according to claim 1 wherein the composition contains only one polyorganosiloxane fluid in which R and R'are each alkyl and from about 20 to about 30 weight percent of the cycloorganosiloxane. 3. A composition according to claim 2 wherein R and R" are methyl. 4. A composition according to claim 3 wherein the adhesion promoter is a compound of the formula 3 wherein Me is the methyl radical. 5. A composition according to claim 4 wherein the organotin salt is an organotin salt of a carboxylic acid selected from the group consisting of dibutyltindiacetate, stannous octoate and dibutyltin dioctoate. 6. A composition according to claim 5 wherein the organotin salt of a carboxylic acid is a compound of the formula (C 4 H 9 ) 2 Sn(OCOCιoH 2 oCH 3 ) 2 . 7. A composition according to claim 6 wherein the inorganic extending or non-reinforcing filler is one or more materials selected from calcium carbonate, barium sulfate, iron oxide, diatomaceous earth, melamine, quartz, crystalline silica, titanium dioxide, alumina trihydrate, zinc oxide, zirconium oxide and chromic oxide. 8. A composition according to claim 7 wherein the inorganic extending or non-reinforcing filler is a combination of about 0.5 to about 5.0 weight percent of crystalline silica and about 36 to about 48 weight percent of alumina trihydrate, the alumina trihydrate having a median particle size of 13. μm, containing 65.1 percent Al 2 0 3 , 34.5 percent combined H 2 0, 0.3 percent Na 2 0, 0.02 percent CaO, 0.01 percent Si0 2 and having a specific gravity of 2.42, the aluminum trihydrate being present in a proportion of 90 to 110 parts by weight per 100 parts by weight of the polyorganosiloxanes . 9. A composition according to claim 7 wherein the inorganic extending or non-reinforcing filler is one or more materials selected from melamine, iron oxide, zinc oxide, titanium dioxide, zirconium oxide or zinc chromate . 10. A composition according to claim 9 wherein the inorganic extending or non-reinforcing filler is melamine. 11. A composition according to claim 1 comprising: a) about 36 weight percent of a hydroxyl terminated dimethyl polysiloxane fluid having a viscosity of 10,000 to 20,000 Centipoise at 25 °C; b) about 35 weight percent of a mixture of amorphous and crystalline Si0 2 fillers having a specific gravity of 2.2 and surface area of up to about 130m 2 /g; c) about 3 weight percent of methyl tris- (methyl ethyl ketoxime) silane; d) about 1 weight percent of N-(2 aminoethyl-3 aminopropyl) trimethoxysilane; e) about 0.1 weight percent of dibutyltindilaurate; f) about 22 weight percent of dimethylsiloxane cyclics; and g) about 0.8 weight percent of a gray pigment. 12. A composition according to claim 1 wherein the composition contains a first polydiorganosiloxane fluid wherein R and R' are each alkyl, R" is OH and n has an average value such that the viscosity is from about 3000 to 30,000 centipoise at 25 °C and a second polydiorganosiloxane fluid wherein R, R' and R" are each alkyl and the average volume of n is between 4 and 20. 13. A composition according to claim 12 wherein R and R' of the first polydiorganosiloxane and R, R' and R" of the second polydiorganosiloxane are all methyl. 14. A composition according to claim 13 wherein the adhesion promoter is a compound of the formula / NHCH 2 CH 2 NH 2 CH 2 CH 2 CH 2 Si (OMe) 3 wherein Me is the methyl radical. 15. A composition according to claim 14 wherein the organotin salt of a carboxylic acid is a compound of the formula (C 4 H 9 ) 2 Sn (OCOCi 0 H 20 CH 3 ) 2 . 16. A composition according to claim 15 wherein the inorganic extending or non-reinforcing filler is one or more materials selected from calcium carbonate, barium sulfate, iron oxide, diatomaceous earth, melamine, quartz, crystalline silica, titanium dioxide, alumina trihydrate, zinc oxide, zirconium oxide and chromic oxide. 17. A composition according to claim 7 wherein the inorganic extending or non-reinforcing filler is a combination of about 0.5 to about 5.0 weight percent crystalline silica and about 36 to about 48 weight percent of alumina trihydrate, the alumina trihydrate having a median particle size of 13. μ , containing 65.1 percent Al 2 0 3 , 34.5 percent combined H 2 0, 0.3 percent Na 2 0, 0.02 percent CaO, 0.01 percent Si0 2 and having a specific gravity of 2.42, the aluminum trihydrate being present in a proportion of 90 to 110 parts by weight per 100 parts by weight of the polyorganosiloxanes . 18. A method of protecting a surface from the effects of a corrosive atmospheric environment comprising (1) applying to the surface a thin layer of a one- part organopolysiloxane rubber composition comprising the product which is obtained by mixing the following: a) from about 20 to about 50 weight percent of one or more polydiorganosiloxane fluids of the formula R"0[ (R) 2 SiO] n R' in which R is a monovalent alkyl or alkylene radical having 1 to 8 carbon atoms or a phenyl radical, R' is a monovalent alkyl or alkylene radical having 1 to 8 carbon atoms or a phenyl radical, R" is OH or a monovalent alkyl or alkylene radical having 1 to 8 carbon atoms or a phenyl radical and n has an average value such that the viscosity is from about 1 to about 100,000 centipoise at 25 °C, wherein at least one of the polyorganosiloxane fluid has R" equal to OH and n has an average value such that the viscosity is in the range from 1,000 to 100,000 centipoise at 25°C, preferably from 3,000 to 40,000 centipoise at 25°C; b) from 0 to about 40 weight percent of a cyclo- organosiloxane of the formula [(R) 2 SiO] n in which R is a monovalent alkyl or alkylene radical having 1 to 8 carbon atoms or a phenyl radical which may optionally be substituted with an alkyl radical having 1 to 8 carbon atoms and n has an average value of 3 to 10 c) from 0 to about 40 weight percent of an inorganic extending or non-reinforcing filler d) from about 0.5 to about 10 weight percent of an amorphous Si0 2 reinforcing filler having a surface area of between about 100 to 250 m 2 /g and a particle size range between about 0.01 and 0.03 microns; e) from about 1 to about 7 weight percent of an oximosilane cross-linking agent of the formula; RSi (ONR' 2 ) in which R and R' are independently selected from monovalent alkyl or alkylene radicals having 1 to 8 carbon atoms or a phenyl radical which may optionally be substituted with an alkyl radical having 1 to 8 carbon atoms ; f) from about 0.2 to about 3 weight percent of an adhesion promoter of the formula 2 \ , (R 0) 3 _ b SiR 1 2 3 in which R and R are independently selected from monovalent alkyl or alkylene radicals having 1 to 8 carbon atoms or a phenyl radical which may optionally be substituted with an alkyl radical having 1 to 8 carbon atoms, b is an integer between 0 and 3, and R is a saturated, unsaturated or aromatic hydrocarbon radical having 1 to 10 carbon atoms which may optionally contain a functional group; and g) from about 0.02 to about 3 weight percent of an organotin salt as a condensation catalyst. and (2) allowing the layer of the one-part organopolysiloxane rubber composition to cure at room temperature to a silicone elastomer. 19. A method according to claim 18 wherein the one part organopolysiloxane rubber composition comprises: a) about 35 weight percent of a hydroxyl terminated dimethyl polysiloxane fluid having a viscosity of 10 Centipoise at 25 °C; b) about 35 weight percent of a mixture of amorphous and crystalline Si0 2 fillers having a specific gravity of 2.2 and surface area of up to about 130m 2 /g; c) about 4.3 weight percent of methyl tris- (methyl ethyl ketoxime) silane; d) about 2.2. weight percent of N-(2 aminoethyl-3 aminopropyl) trimethoxysilane; e) about 0.8 weight percent of dibutyltindilaurate; f) about 22 weight percent of petroleum based solvent; and g) about 0.8 weight percent of a gray pigment.

Inventors: AHMED FAROOQ, BARR JOHN, HUDA FAISAL, HUDA SERAJ UL, AHMED, FAROOQ, BARR, JOHN, HUDA, FAISAL, HUDA, SERAJ, UL
Applicants: AHMED FAROOQ, BARR JOHN, CSL SILICONES INC, HUDA FAISAL, HUDA SERAJ UL, AHMED, FAROOQ, BARR, JOHN, CSL SILICONES INC., HUDA, FAISAL, HUDA, SERAJ, UL
Application year: 1999
Main classification: C09D183
IPC codes: C09D183