Polymers and processes thereof

Abstract: A process for the preparation of polymers which comprises generating a solution of water and polyvinyl alcohol with acetate groups; adding thereto a mixture of an alkali metal iodide and iodine; adding thereto initiator, and optional crosslinking agent; adding monomer, a mixture of monomers, or a monomer/polymer mixture; homogenizing, and polymerizing; and wherein there is formed an iodide/iodine/acetate complex prior to said polymerizing.

Description: This invention is generally directed to processes for the preparation of polymers. The process of the present invention in embodiments relates to the preparation of a polymer, which polymer can be selected as a carrier powder coating, and more specifically a process for the preparation of polymeric particles with for example, a volume average particle size diameter of from 0.05 to 5 µm (microns), and preferably from 1 to 5 µm (microns) in volume average diameter, as determined for example by known methods, such as a Coulter Counter. More specifically the present invention is directed to processes for the preparation of polymers wherein there is formed a complex between for example, polyvinyl acetate, iodine, and iodide, and there is eliminated, or minimized, undesirable foaming and fouling of the reactors selected, thereby enabling the process to be very useful on a large manufacturing scale. The carrier particles containing the polymer generated as illustrated herein, and a second polymer, such as polyvinylidene fluoride, or enable a wide carrier triboelectric range. Developer compositions comprised of the carrier particles illustrated herein and prepared, for example, by a dry coating process are useful in electrostatographic or electrophotographic imaging systems, especially xerographic imaging, digital imaging, and printing, inclusive of color printing processes. Furthermore, in the aforementioned imaging systems the triboelectric charge on the carrier particles can be preselected depending on for example, the polymer composition and dispersant component applied to the carrier core. With the process of the present invention there can be formulated developers with selected triboelectric charging characteristics and/or conductivity values in a number of different combinations. Thus, for example, there can be formulated in accordance with the invention of the present application developers with conductivities of from 10 -6 to 10 -17 ohm-cm, and preferably from 10 -8 to 10 -6 ohm-cm, which conductivities are determined in a magnetic brush conducting cell, and a wide carrier triboelectric charging value of from -30 to +70, and in embodiments of from -15 to +20 microcoulombs per gram on the carrier particles as determined by the known Faraday Cage method. Thus, developers can be formulated with constant conductivity values with different triboelectric charging characteristics, or with constant triboelectric charging values and different conductivities. The preparation of polymeric particles can be accomplished by grinding or attrition, and precipitation and in situ particle polymerizations. Grinding or attrition, especially fluid energy milling, of large polymeric particles or polymeric composite particles containing fillers of the size needed for powder coating, for example 1 to 5 microns, is often not desirable both from an economic and functional viewpoint. These particles are for example, difficult to grind and, therefore, grinding or attrition for coating with present milling equipment is costly primarily because of the very low processing yield, for example in the range of 5 to 10 weight percent. Precipitation processes can also be selected to prepare polymericlpolymeric composite particles. In one process, the polymer solution is heated to above its melting temperature and then cooled to form particles. In another process, the polymer solution is precipitated using a non-solvent, or the polymer solution is spray dried to obtain polymeric/polymeric composite particles. With these precipitation processes, it can be difficult to achieve low cost, pure polymer, that is, for example, with no or substantially no impurities, such as solvents or precipitants in the resulting polymer particles. It is also difficult with these processes to obtain particles with small particle size and narrow particle size distribution. The object of the present invention resides in the provision of processes for the preparation of polymer carrier coatings, such as PMMA (polymethyl methacrylate). This object is achieved by the process in accordance with the appended claims. The polymers obtained by the process of the present invention are preferably substantially pure, for example with a purity of from 95 to 99.95 percent, clean and dry small, for example from 0.05 to 5 µm (microns) in volume average diameter, wherein product agglomeration is minimized, or avoided. With the process of the present invention submicron to micron sized polymeric composite particles with an average particle diameter size of from 0.05 to 5 µm (microns) can be generated. By the process of the present invention there can be provided small polymeric particles, and more specifically from 1 to 5 µm (micron) size (volume average throughout) polymeric particles. Another feature of the present invention resides in simple and economical polymerization processes for the preparation of low cost, clean, and dry small polymeric particles, and more specifically submicron or micron-size polymeric particles useful as carrier powder coatings. Additionally, in another feature of the present invention there are provided, processes for the preparation of polymeric particles that can be selected for carrier powder coating with a triboelectric charge in the range, for example, of from -30 to +70, or from -10 to +40 microcoulombs per gram as determined by the known Faraday Cage process. The present invention in embodiments relates to a process for the preparation of polymers which comprises generating a solution of water and polyvinyl alcohol with acetate groups; adding thereto a mixture of an alkali metal iodide and iodine; adding thereto initiator, and an optional crosslinking agent; adding monomer, a mixture of monomers, or a monomer/polymer mixture; homogenizing, and polymerizing; and wherein there is formed an iodide/iodine/acetate complex prior to said polymerizing. Preferably, said monomer is comprised of a mixture of comonomers. The present invention is also directed to a process for the preparation of a polymer which process comprises the mixing of an alkali metal iodide, iodine, a solution of water and polyvinyl alcohol with acetate groups, and monomer, comonomers or a monomer/polymer mixture, initiator, and an optional crosslinking agent; heating to polymerize and thereafter optionally cooling, followed by isolating, washing and drying said polymer. For this process, the following embodiments are preferred: Prior to heating to polymerize homogenizing is accomplished and there is selected a mixture of monomer and polymer, the alkali metal iodide is potassium iodide, the polyvinyl alcohol possesses a hydroxyl number of from 60 to 98 and contains acetate groups thereon, and an iodine/iodide/acetate complex forms between the potassium iodide, iodine, and said polyvinyl alcohol. The water is present in an amount of from 95 to 99 percent and wherein there is selected a mixture of monomer and polymer, or a monomer. Heating to polymerize is from 60 to 150°C, cooling is to a temperature of from 20 to 30°C, isolating washing and drying is accomplished, and washing is accomplished with an aliphatic alcohol and water mixture to remove said polyvinyl alcohol, said iodine, and said alkali metal iodide, and there is selected a mixture of monomer and polymer, or a monomer. There is selected in place of said alkali metal iodide and said iodine, a mixture of a peroxide initiator and said alkali metal iodide. There is selected in place of said alkali metal iodide and said iodine a mixture of a peroxide initiator and iodine. The peroxide is benzoyl peroxide. Polymerization is accomplished by heating at a temperature of from 60 to 150°C. Said potassium iodide is present in an amount of from 0.1 to 2 weight percent, and said iodine is present in an amount of from 0.01 to 0.1 weight percent. There results a polymer product of polymethyl methacrylate by semisuspension polymerization which comprises: 1) forming an aqueous phase by mixing from 95 to 99 weight percent of water with from 1 to 5 weight percent polyvinyl alcohol, which alcohol has a degree of hydrolysis of from 60 to 98 percent, and adding: a) from 0.1 to 2 weight percent alkali metal iodide and from 0.01 to 0.1 weight percent iodine, or adding b) from 0.1 to 2 weight percent alkali metal iodide and from 0.1 to 5 weight percent peroxide initiator, or adding c) from 0.01 to 0.1 weight percent iodine and from 0.1 to 5 weight percent peroxide initiator, thus forming a complex; (2) forming an organic phase by mixing a monomer, comonomers, or a monomer:polymer mixture in a ratio of from 100:0 to 60:40, with an initiator in an amount of from 1 to 15 weight percent and an optional crosslinking agent from 0 to 5 weight percent; (3) thereafter mixing the aqueous and organic phases in a ratio of from 10:90 to 40:60 organic phase:aqueous phase, and homogenizing at a suitable speed of from 1,000 to 20,000 rpm with a high shear mixer; (4) subsequently heating the resulting mixture between from 60°C and 150°C until from 80 to 100 weight percent of monomer or comonomers has been polymerized; (5) cooling; (6) washing the mixture with a mixture of an aliphatic alcohol and water with a wateralcohol ratio of from 10:90 to 100:0, and said washing is accomplished with a decanting centrifuge to thereby separate the wet cake, which is comprised of from 50 weight percent polymer product and 50 weight percent of liquid washing mixture; and (7) drying the wetcake to enable the polymer product. The polyvinyl alcohol possesses a hydroxyl number or degree of hydrolysis of from 75 to 85. A crosslinking agent is selected. There is selected in an amount of from 0 to 5 weight percent a crosslinking agent; and from 1 to 15 weight percent initiator, or mixtures of initiators. The polymer formed is polymethyl methacrylate. The present invention provides also a semisuspension polymerization process for the preparation of polymer which comprises: 1) forming an aqueous phase by mixing water and polyvinyl alcohol, which polyvinyl alcohol contains acetate groups, and adding: a) iodine and an alkali metal iodide, or adding b) an alkali metal iodide and a peroxide initiator, or adding c) iodine and a peroxide initiator, thereby forming a complex; (2) forming an organic phase by mixing a monomer, comonomers, or a monomer:polymer mixture with an initiator and an optional crosslinking agent; (3) thereafter mixing the aqueous and organic phases and optionally homogenizing; (4) subsequently heating the resulting mixture; optionally (5) cooling; (6) washing the mixture with a mixture of an aliphatic alcohol and water; separating the wet cake and (7) drying the wetcake. The present invention is further directed to a process which comprises mixing a solution of polyvinyl alcohol and which alcohol contains acetate groups, an alkali metal iodide, iodine, initiator, and monomer; and polymerizing. Preferably there is formed an iodide/iodine/acetate complex prior to polymerizing; said monomer is comprised of a mixture of monomers, or a monomer/polymer mixture; subsequent to said mixing homogenization is accomplished; and polymerizing is by heating. Preferably, there results a polymer, which is further preferred to be polymethyl methacrylate. A polymer or polymers can be prepared in accordance with embodiments of the present invention by providing, or forming a mixture of water and polyvinyl alcohol, for example, 60 to 98, and preferably 75 to 85 percent hydrolyzed, that is the polyvinyl alcohol contains sufficient acetate groups thereon to enable it to form a complex; adding an alkali metal iodide, such as potassium iodide, and iodine thereby forming a complex between the acetates of the polyvinyl alcohol and the alkali metal iodide and the iodine, and which complex is usually red in color; adding, or mixing, i) monomer, such as methyl methacrylate monomer, or ii) one to five comonomers, preferably two, for example methyl methacrylate and acrylic acid, or iii) adding a mixture of monomer(s) and polymer(s), for example 70 to 95 weight percent monomer such as methyl methacrylate and 5 to 30 weight percent polymer such as polymethyl methacrylate; homogenizing the resulting mixture, and thereafter polymerizing, preferably by suspension polymerization or semisuspension polymerization and which polymerization involves heating; cooling; separating the polymer product; washing and drying, the washing being accomplished primarily to remove residual polyvinyl alcohol. In place of the alkali metal iodide and iodine there may be selected for the processes of the present invention in embodiments thereof a mixture of an initiator, such as a peroxide, like benzoyl peroxide, and iodine, or a mixture of alkali metal iodide and an initiator such as benzoyl peroxide, or other similar suitable peroxide. The suspension process can be accomplished by: 1) forming an aqueous phase by for example, mixing 95 to 99 weight percent, or parts of water with 1 to 5 weight percent of polyvinyl alcohol which has a degree of hydrolysis between 60 and 98 percent, and preferably between 75 and 85 percent, and adding a) from 0.1 to 2 weight percent of alkali metal iodide and 0.01 to 0.1 weight percent iodine, or b) from 0.1 to 2 weight percent alkali metal iodide and 0.1 to 5 weight percent peroxide initiator, or c) from 0.01 to 0.1 weight percent iodine and 0.1 to 5 weight percent peroxide initiator, thus forming a complex in a), b) or c), that is an iodine-iodide-acetate complex, which acetate is contained on the polyvinyl alcohol, and which complex is usually red in color; (2) forming an organic phase by mixing a monomer or comonomers, or a monomer:polymer mixture (ratio of from 100:0 to 60:40), with an initiator or initiators, from 1 to 15 weight percent, and an optional crosslinking agent, which agent functions primarily to strengthen the resulting polymer, and which agent is selected for example, in an amount of from 0 to 5 weight percent; (3) mixing the resulting phases together in a ratio of from 10:90 to 40:60 organic phase:aqueous phase, and homogenizing at a suitable speed, for example, from 1,000 to 20,000 rpm, and preferably from 5,000 to 12,000 rpm with a high shear mixer such as a Brinkmann Polytron; (4) heating the mixture resulting, for example, to between 45°C and 120°C (Centigrade) until from 80 to 100 weight percent of monomer or comonomers has been polymerized; (5) cooling to room temperature; (6) washing the mixture with for example a mixture of an aliphatic alcohol such as methanol and water, water:alcohol ratio between 10:90 and 100:0, using a decanting centrifuge for each washing stage to separate the wet cake, which is comprised of for example, 50 weight percent solids (polymer product) and 50 weight percent liquid (washing mixture), and using for example from two to six washing stages; and (7) drying the separated wetcake to enable the polymer product. The invention polymerization process possesses improvements over other suspension or semisuspension polymerization processes by eliminating undesirable foam and fouling in the polymerization reactor. When the aforementioned red complex is observed, no reactor foaming or fouling are observed. When the red complex is not observed, major foaming and fouling occurs in the reactor. Thus, antifoaming agents which may affect product properties or be difficult to remove are not needed. Illustrative examples of monomer, or comonomers, that is for example, mixtures of monomers, from one to five for example, present in an amount of, for example, from 80 to 99 weight percent, and more preferably from 80 to 90 weight percent include vinyl monomers comprised of styrene and its derivatives such as styrene, α-methylstyrene, p-chlorostyrene; monocarboxylic acids and their derivatives such as acrylic acid, methyl acrylate, ethyl acrylate, butyl acrylate, dodecyl acrylate, octyl acrylate, phenyl acrylate, methacrylic acids, methyl methacrylate, ethyl methacrylate, butyl methacrylate, octyl methacrylate, dimethylaminoethyl methacrylate, diethylaminoethyl methacrylate, diisopropylaminoethyl methacrylate, tert-butylaminoethyl methacrylate, glycidyl methacrylate, acrylonitrile, acrylamide, dimethylacrylamide, and isopropylacrylamide; dicarboxylic acids with a double bond and its derivatives such as maleic acid, monobutyl maleate, dibutylmaleate; vinyl esters such as vinyl chloride, vinyl acetate and vinyl benzoate; vinyl ketones such as vinyl methyl ketone and vinyl ether ketone; and vinyl ethyl ether and vinyl isobutyl ether; vinyl naphthalene; unsaturated mono-olefins such as isobutylene; vinylidene halides such as vinylidene chloride; N-vinyl compounds such as N-vinyl pyrrole and fluorinated monomers such as pentafluoro styrene, allyl pentafluorobenzene; and mixtures thereof. Preferably one monomer is selected; for mixtures various suitable amounts of each comonomer can be selected, for example from 1 to 99, preferably from 40 to 65 percent by weight, or parts, of a first monomer, and from 1 to 99, and preferably from 60 to 35 percent by weight, or parts of a second comonomer, and wherein the total for the two comonomers is 100 parts, or 100 percent. Other known monomers may be selected. Illustrative examples of polymerization initiators present in an amount of, for example, from 0.1 to 20 weight percent of monomer, and more preferably from 1 to 5 weight percent include azo compounds such as 2,2'-azobis(2,4-dimethyl valeronitrile), 2,2'-azobis(2-methyl butyronitrile), of 1,1'-azobis(cyanocyclohexane), , and peroxides such as benzoyl peroxide, lauryl peroxide, 1-1-(t-butylperoxy)-3,3,5-trimethylcyclohexane, n-butyl-4,4-di-(t-butylperoxy) valerate, dicumyl peroxide. For the mixtures from 2 to 5 initiators can be selected, and preferably 2 initiators, and wherein the amounts of each initiator can vary, providing the total thereof is 100 percent. For example, from 1 to 99 parts, or weight percent of a first initiator, and from 99 to 1 parts, or weight percent of a second different initiator can be selected, with preferred amounts in embodiments being for example from 40 to 60 for one initiator, and from 60 to 40 for the second dissimilar initiator. Crosslinking agents selected for the process of the present invention are known and can be comprised of compounds having two or more polymerizable double bonds. Examples of such compounds include aromatic divinyl compounds such as divinylbenzene and divinylnaphthalene; carboxylic acid esters having two double bounds such as ethylene glycol diacrylate, ethylene glycol dimethylacrylate; and divinyl compounds such as divinyl ether, divinyl sulfite, divinyl sulfone, such as other known crosslinking agents. Among these, divinylbenzene is particularly useful. The crosslinking component, or compound is preferably present in an amount of from 0.1 to 5 parts by weight in 100 parts and, more preferably, from 0.2 to 1 part by weight of the monomer or comonomers. Various polymerizations illustrated herein can be selected to convert monomers and the like to polymers, and more specifically polymerization is accomplished by heating such as by heating the reaction mixture at a temperature of from abut 60 to 150°C. Isolating, washing, and drying of the product can be accomplished by a number of known methods. For example isolation can be effected by filtration, drying by heating or with an oven dryer, and washing by mixing. Various washing components can be selected as indicated herein, such as water, aliphatic alcohols, mixtures thereof. Examples of alcohols include those with from 1 to 25 and preferably from 1 to 12 carbon atoms, such as methanol, ethanol, propanal and butanol. Examples of alkali metal iodides are compounds of ammonium iodide, barium iodide, calcium iodide, cuprous iodide, lithium iodide, potassium iodide and sodium iodide, and the amount of alkali metal iodide selected can vary, and more specifically is preferably for example, from 0.1 to 2 weight percent based on the weight of water selected for the reaction, or reaction mixture. Examples of products generated with the processes of the present invention, and with a size diameter range of for example, from 0.05 to 5 µm (microns), and preferably from 1 to 5 µm (microns) include polymethyl methacrylate (PMMA), polystyrene, poly-α-methylstyrene, poly-p-chlorostyrene; monocarboxylic acid polymers and their derivatives such as polyacrylic acid, polymethyl acrylate, polyethyl acrylate, polybutyl acrylate, polydodecyl acrylate, polyoctyl acrylate, polyphenyl acrylate, polymethacrylic acids, polyethyl methacrylate, polybutyl methacrylate, polyoctyl methacrylate, polydimethylaminoethyl methacrylate, polydiethylaminoethyl methacrylate, polydiisopropylaminoethyl methacrylate, polytert-butylaminoethyl methacrylate, polyglycidyl methacrylate, polyacrylonitrile, polyacrylamide, polydimethylacrylamide, and polyisopropylacrylamide; polymers from dicarboxylic acids with a double bond and their derivatives such as polymaleic acid, polymonobutyl maleate, and polydibutylmaleate; polymers obtained from vinyl esters such as polyvinyl chloride, polyvinyl acetate and polyvinyl benzoate; polymers obtained from vinyl, ketones such as polyvinyl methyl ketone and polyvinyl ether ketone; and polyvinyl ethyl ether and polyvinyl isobutyl ether; polyvinyl naphthalene; polymers from unsaturated mono-olefins such as polyisobutylene; vinylidene halides such as polyvinylidene chloride; N-vinyl compounds such as poly-N-vinyl pyrrole and fluorinated polymers such as polypentafluoro styrene, polyallyl pentafluorobenzene; and mixtures thereof. The following Examples are being provided to further illustrate the present invention. Comparative Examples and data are also provided. Parts and percentages are by weight unless otherwise indicated. EXAMPLES 1. Semisuspension Polymerization In a 500 mL glass reactor, 114 g (grams) of methyl methacrylate (MMA), 0.75 g of divinylbenzene (dvb) crosslinking agent, and 28 grams of Elvacite-2008 polymethyl methacrylate were stirred at 210 rpm overnight, 18 hours. Initatiators, 4.9 g (grams) of Vazo-52, which is (2,2'-azobis(2,4-dimethylvaleronitrile), 2.5g of Vazo-67, which is (2,2'-azobis(2-methylbutyronitrile), and Lucidol 75 benzoyl peroxide (BPO) (see Table 1 below for quantities) were added the next morning, 18 hours later. This resulting organic phase was stirred for 1 hour to dissolve the initiators. An aqueous phase mixture of 11.44 g Airvol 603 polyvinyl alcohol obtained from Air Products, and which polyvinyl alcohol is 80% hydrolyzed (20% acetate groups), potassium iodide (KI) and iodine (I 2 ) (see Table 1 below for quantities) in 458.56 g deionized water was stirred at 350 rpm in a 2 L stainless steel beaker. A red colored complex was observed in the aqueous phase for combinations of KI/I 2 /BPO (see Table 1). The above organic phase was poured into the aqueous phase, and the resulting slurry was mixed for 3 minutes. The slurry was then homogenized in an ice bath at 8,000 rpm for 5 minutes using a Brinkmann Polytron homogenizer. The resulting slurry was poured into a 1 L Parr reactor that was then sealed and pressurized to 100 kPa with nitrogen. Stirring was started in the reactor at 230 rpm with a pitch blade impeller. The reactor was heated to 60°C for 90 minutes and then to 80°C for 90 minutes, and was then cooled by removing the heat source. The final slurry was washed by dispersing it in 420 g of methanol and 50 g of deionized water (DIW), followed by centrifugation and decanting of the centrate. The resulting wet cake was then redispersed in methanol/DIW as above and the centrifugation was repeated. This cycle was repeated four times, and then a final wash step was accomplished using 480 g DIW. The excess water was then dried off in an oven at 80°C, and the product of polymethyl methacrylate (99.5 percent pure) was ground in a coffee grinder, and vacuum drying was accomplished at 80°C for 4 hours to complete the drying step. Particle size of the final product was measured on a Coulter LS230 laser diffraction device. No foam, fouling, and minimal fouling, was determined by visual observation. Formulation Particle Size (Coulter LS 230) Expt. # Kl (g) I 2 (g) BPO(g) Volume Median (µm) % >10 (µm) Red Complex Observed in Aqueous Phase Notes 1 5 0.15 3.1 5.35 40.5 Yes No foam; minimal fouling 2 5 0.15 0 2.54 0 Yes No foam; minimal fouling 3 5 0 3.1 2.69 4.24 Yes No foam; minimal fouling 4 5 0 0 2.44 0 No Major foaming and fouling 5 0 0.15 3.1 2.36 0 No No foam; minimal fouling 6 0 0.15 0 2.14 0 No Major foaming and fouling 7 0 0 3.1 2.76 3.03 No Major foaming and fouling 8 0 0 0 2.39 0.26 No Major foaming and fouling The results in Table 1 indicate that at least three combinations eliminated foaming and fouling in the reaction: (1) KI and I 2 , or (2) KI and BPO, or (3) BPO and I 2 . A red colored complex (an iodine/iodide/acetate complex) was observed in the aqueous phase when these combinations were present There is no red colored complex observed with the other combinations, and large amounts of foaming and fouling are present in the final mixture. Three of the above prepared polymers were tested as carrier coatings as shown in Table 2. Carriers were prepared in 5" kiln inserts, and which carriers were comprised of Nuclear Metals 100mm diameter core and 1% coating weight of the aforementioned polymethyl methacrylate, PMMA prepared by the invention process. The core and polymers were mixed in an M5R blender (30min @ 50 rpm, 10 Ib. loading) and fused (30 min. residence time) at 400°F. Developers were prepared by mixing 194 grams of the above prepared carrier with 6 grams of a toner composition comprised of 87 percent by weight of a 30 percent (by weight) gel content partially crosslinked polyester resin, obtained by the reactive extrusion of a linear polyester, 5 percent by weight of carbon black, 4 percent by weight of a polypropylene wax, and 4 percent by weight of a compatibilizing agent comprised of KRATON™ (a styrene-ethylene/butylene-styrene block copolymer) obtained from Shell Chemicals. Thereafter, the triboelectric charge on the carrier particles was determined by the known Faraday Cage process, and voltage breakdown (Vb) was measured by forming a 0.1 inch long magnetic brush and measuring the voltage needed to produce a potential difference of 10 Volts across a resistor. The results are shown in Table 2. Experiment # Vb (V) Tribo (µC/g) 3 >1500 22.2 1 >1500 21.4 2 >1500 24.0 The resulting carriers had a voltage breakdown greater than 1,500 volts which indicates excellent surface coverage for the coating. 2. Suspension Polymerization Four of the above experiments were repeated without using Elvacite 2008 polymethyl methacrylate (DuPont) in the organic phase: In a 500 mL glass reactor, 140 g MMA (methyl methacrylate), 0.75 g dvb, 6.04 g of Vazo-52, 2,2'-azobis(2,4-dimethylvaleronitrile), 3.02 g of Vazo-67 (2,2'-azobis(2-methylbutyronitrile) and Lucidol-75 BPO (see Table 1 for quantity) were stirred at 210 rpm for 30 minutes to create an organic phase. More specifically in a 500 mL glass reactor, 140 g methyl methacrylate (MMA) and 0.75 g divinylbenzene (dvb) crosslinking agent were stirred at 210 rpm for 30 minutes. 6.04 Grams Vazo-52, 3.02 g Vazo-67, and Lucidol 75 benzoyl peroxide (see Table 3 below for quantities) initiators were added, and this organic phase was stirred for 1 hour to dissolve the initiators. An aqueous phase mixture of 11.44 g Airvol 603 polyvinyl alcohol obtained from Air Products, and which alcohol is 80% hydrolyzed (i.e., 20% acetate groups), potassium iodide (Kl) and iodine (I 2 ) (see Table 3 below for quantities) in 458.56 g deionized water was stirred at 350 rpm in a 2 L stainless steel beaker. The organic phase was poured into the aqueous phase and the resulting slurry was mixed for 3 minutes. The mixture was then homogenized in an ice bath at 8,000 rpm for 5 minutes using a Brinkmann Polytron homogenizer. The resulting slurry was poured into a 1 L Parr reactor that was then sealed and pressurized to 100 kPa with nitrogen. Stirring was started at 230 rpm. The reactor was heated to 60°C for 90 minutes and then to 80°C for 90 minutes, and was then cooled. The final slurry was washed by dispersing it in 420 g methanol and 50 g DIW, followed by centrifugation and decanting of the centrate. The resulting wet cake was then redispersed in methanol/DIW as above and the centrifugation was repeated. This cycle was repeated four times, and then a final wash step was accomplished using 480 g DIW. The excess water was then dried off in an oven at 80°C, the product was ground in a coffee grinder, and vacuum drying was done at 80°C for 4 hours to complete the drying step. Particle size of the final polymethyl methacrylate product (99.5% pure) was measured on a Coulter LS230 laser diffraction device. Formulation Particle Size (Coulter LS 230) Exp t. # KI (g) I 2 (g) BPO (g) Volume Median (µm) % >10 (µm) Notes 9 5 0.15 3.1 1.78 0.05 No foam; minimal fouling 10 0 0.15 3.1 2.57 3.78 No foam; minimal fouling 11 5 0.15 0 2.25 0 No foam; minimal fouling 12 0 0 0 2.70 3.67 Major foaming and fouling

Claims: A process for the preparation of polymers comprising: mixing a solution of polyvinyl alcohol containing acetate groups, an initiator and monomer; and a) an alkali metal iodide and iodine; b) an alkali metal iodide and a peroxide initiator; or c) iodine and a peroxide initiator; and polymerizing said mixture. The process in accordance with claim 1 wherein: there is formed an iodide/iodine/acetate /acetate complex prior to polymerizing; said monomer comprises a mixture of monomers, or a monomer/polymer mixture; subsequent to said mixing homogenization is accomplished; and polymerizing is by heating. The process in accordance with claim 1 comprising in the following steps: generating a solution of water and polyvinyl alcohol with acetate groups; adding thereto a mixture of an alkali metal iodide and iodine; adding thereto initiator forming an iodide/iodine/acetate complex; adding monomer, a mixture of monomers, or a monomer/polymer mixture; and polymerizing. The process in accordance with claim 1 comprising the following steps: mixing of an alkali metal iodide, iodine, a solution of water and polyvinyl alcohol with acetate groups, and monomer, comonomers or a monomer/polymer mixture, initiator; and heating to polymerize. The process in accordance with claim 4 wherein homogenizing is accomplished prior to the heating and wherein there is selected a monomer or a mixture of monomer and polymer, the alkali metal iodide is potassium iodide, the polyvinyl alcohol possesses a hydroxyl number of from 60 to 98 and contains acetate groups thereon, and wherein an iodine/iodide/acetate complex forms between the potassium iodide, iodine, and said polyvinyl alcohol. The process in accordance with claim 5 wherein said potassium iodide is present in an amount of from 0.1 to 2 weight percent, and said iodine is present in an amount of from 0.01 to 0.1 weight percent. The process in accordance with any of claims 4 to 6 wherein there results a polymer product of polymethyl methacrylate by semisuspension polymerization which comprises: 1) forming an aqueous phase by mixing from 95 to 99 weight percent of water with from 1 to 5 weight percent polyvinyl alcohol, which alcohol has a degree of hydrolysis of from 60 to 98 percent, and adding: a) from 0.1 to 2 weight percent alkali metal iodide and from 0.01 to 0.1 weight percent iodine; or adding b) from 0.1 to 2 weight percent alkali metal iodide and from 0.1 to 5 weight percent peroxide initiator, or adding c) from 0.01 to 0.1 weight percent iodine and from 0.1 to 5 weight percent peroxide initiator, thus forming a complex; (2) forming an organic phase by mixing a monomer, comonomers, or a monomer:polymer mixture in a ratio of from 100:0 to 60:40, with an initiator in an amount of from 1 to 15 weight percent and an optional crosslinking agent from 0 to 5 weight percent; (3) thereafter mixing the aqueous and organic phases in a ratio of from 10:90 to 40:60 organic phase:aqueous phase, and homogenizing at a suitable speed of from 1,000 to 20,000 rpm with a high shear mixer; (4) subsequently heating the resulting mixture between from 60°C and 150°C until from 80 to 100 weight percent of monomer or comonomers has been polymerized; (5) cooling; (6) washing the mixture with a mixture of an aliphatic alcohol and water with a wateralcohol ratio of from 10:90 to 100:0, and wherein said washing is accomplished with a decanting centrifuge to thereby separate the wet cake, which is comprised of from 50 weight percent of polymer product and 50 weight percent of liquid washing mixture; and (7) drying the wetcake to enable the polymer product. The process in accordance with claim 1, said process being a semisuspension polymerization process for the preparation of a polymer which comprises: 1) forming an aqueous phase by mixing water and polyvinyl alcohol, which polyvinyl alcohol contains acetate groups, and adding: a) iodine and an alkali metal iodide, or adding b) an alkali metal iodide and a peroxide initiator, or adding c) iodine and a peroxide initiator, thereby forming a complex; 2) forming an organic phase by mixing a monomer, comonomers, or a monomer:polymer mixture with an initiator; 3) thereafter mixing the aqueous and organic phases; 4) subsequently heating the resulting mixture; 5) optionally cooling; 6) washing the mixture with a mixture of an aliphatic alcohol and water; separating the wet cake and 7) drying the wet cake.

Inventors: ENRIGHT THOMAS E, HENDERSON K DEREK, KELLY BERNARD A, LIEBERMANN GEORGE, MAHABADI HADI K, SILENCE SCOTT M, ENRIGHT, THOMAS E., HENDERSON, K. DEREK, KELLY, BERNARD A., LIEBERMANN, GEORGE, MAHABADI, HADI K., SILENCE, SCOTT M.
Applicants: XEROX CORP, XEROX CORPORATION
Application year: 1999
Main classification: C08F2
IPC codes: C08F291, C08F2, G03G9, C08J3, C08F6