A METHOD FOR MANUFACTURING A FOAM PANEL

Abstract: An insulated foam board is manufactured by leading a first facing (1) from a reel and laying down liquid foam reactants. A second facing (2) from a supply reel is laid over the reactants forming a sandwich. The foam is expanded in an oven (12) and the board is cut to a desired length. One or both facings (21, 22) are removed and re-wound onto a reel (24, 25) for re-use. A coating in the form of a metallised paint is applied (30, 35) in-line to one or both faces of the foam core (23), after removal of the facings (21, 22). The painted boards have enhanced heat insulation properties.

Description: "A METHOD FOR MANUFACTURING A FOAM PANEL" Introduction The invention relates to insulated board and in particular to a method for manufacturing a foam panel. In conventional reactive foam panel manufacture a first facing is delivered to an area at which liquid foam reactants are delivered onto the first facing. A second facing is led over the liquid foam reactants. The foam is then heated and allowed to rise to a predetermined height. Such manufacturing processes are widely used and are generally successful. There is however an increasing need to maintain competitiveness by reducing manufacturing costs whilst producing a high quality board. This invention is therefore directed towards producing an improved manufacturing process of this type. Statements of Invention According to the invention there is provided a method for manufacturing a foam panel comprising the steps of: leading a first facing from a first facing supply to a foam lay down area; laying liquid foam reactants on the first facing; leading a second facing from a second facing supply over the liquid foam reactants; allowing the foam to expand between the facings to form a foam panel; removing at least one of the facings from the foam; and applying a coating to one or both faces of the foam from which the facings have been removed. Most preferably the coating is applied in-line. The coating is preferably in a liquid form. Preferably the coating is a paint. In one case the paint contains non-gas permeable flake-like particles or platelets such as metal or glass flakes. The paint may contain aluminium flakes. In a preferred embodiment the paint contains nanocomposites. In one embodiment the coating is applied by a calendering roll. Alternatively or additionally the coating is applied by passing the panel with the facings removed through a curtain of the coating material. Alternatively or additionally the coating is applied by spray coating. Alternatively the coating is applied electrostatically. In a particularly preferred embodiment of the invention the method includes the step, after applying the coating, of curing the coating on the foam. Preferably the curing is carried out in-line. Most preferably, the coating is cured by heating and/or by application of radiation. The coating may be cured by localised application of heat and/or radiation. In one arrangement the method includes the step after coating, of passing the coated panels through an accumulator. The method may include the step, before or after coating, of turning the panel to lie on an edge thereof. Ideally the method includes the step, after coating, of cutting the panel to a desired length. Preferably the method includes the step, after at least partial curing of the coating, of cutting the panel to a desired length. The paint may be a leafing or non-leafing paint. Ideally the coating is of low gas permeability, especially to C0 2 , 0 2 , N 2 and/or H 2 0. In one embodiment of the invention both facings are removed from the foam for re-use. In a preferred arrangement one or both facings is/are peeled from the foam and coiled onto a take-off reel for re-use either as the first or second facing supply. Typically the upper facing is coiled onto an upper facing recycle coil to provide a facing supply for the second facing. Preferably the upper facing recycle coil is delivered to a second facing feeding station. Preferably the lower facing is coiled onto a lower facing recycle coil to provide a facing supply for the first facing. Typically the lower facing recycle coil is delivered to a first facing feed station. In a preferred embodiment of the invention the first and/or second facings are removed from the foam core after at least partial curing of the foam core. Ideally, the first and/or second facings are removed from the core in advance of cutting of the foam to a desired length. In one arrangement release means is provided between the inner face of the first and/ or second facing and the foam core. Typically the release means is provided on the inner face of the first and/or second facing. In one embodiment of the invention the first and/ or second facing is selected from: polyolefin films (such as polypropylene, high or medium density polyethylene, low or linear low density polyethylene), poly halogenated polyolefins (such as polytetrafluoro ethylene), waxed paper and waxed plastic films, other suitably treated paper, plastic, metal foil or glass films and facings and combinations thereof such that the facing can be continuously removed from the foam without significant damage to either facing or foam during or just following the production process. The foam is preferably selected from polyurethane, polyisocyanurate and phenolic. Preferably the foam has significant cellular structure for use in thermal and/or acoustic insulation applications. The invention further provides a foam panel whenever manufactured by a method of the invention. The panel is free from a facing on one or both faces thereof. At least one of the faces of the panel is coated with a coating material, preferably a paint. The invention also provides a foam panel comprising a foam core having a first face and a second face, at least one of the faces having a coating applied thereto. Preferably the coating is a paint. Most preferably the foam core is of polyurethane, polyisocyanurate or phenolic material. The panel may for example, be used as an underfloor insulation panel. Alternatively the panel may be an insulation liner panel, for example for use in refrigeration applications such as for a refrigerated transport vehicle. Brief Description of Drawings The invention will be more clearly understood from the following description thereof given by way of example only with reference to the accompanying drawing which is a schematic side view of a method for manufacturing a panel according to the invention. Detailed Description This invention provides a highly cost efficient method for manufacturing an insulated foam board or panel. As in conventional processes, a first facing 1 is led from a supply reel to a foam lay down area and liquid foam reactants are laid down from a lay down head 3 and spread across the facing 1. A second facing 1 from a second facing supply reel is laid down over the liquid foam reactants forming a sandwich. The sandwich may be passed through a nipping means 10 to evenly spread and to set the thickness of the foam. The sandwich is then passed through an oven 12 in which the foam expands under a free or controlled rise technique. The output from the oven 12 is a continuous length of panel comprising outer and inner facings 21, 22 with a foam core 23 therebetween. The panel is then cut to a desired length and, generally, palletised and stacked ready for delivery to a customer. panel is then cut to a desired length and, generally, palletised and stacked ready for delivery to a customer. In the invention at least one of the facings 21, 22 is removed from the panel and preferably re-wound onto a reel 24, 25 for re-use. Preferably, both of the facings 21, 22 are separately removed from the core 23 and re-wound onto separate reels for re-use as illustrated. A coating is applied in-line to one or both faces of the foam 23 after removal of the facing(s) 21, 22. The coating is a paint, containing a non-gas permeable flakelike particles or plateletes such as metal or glass flakes. The paint may be an aluminium flaking or non-flaking paint or a nano-composite. Such paint coatings provide a barrier to provide low gas permeability. Thus, the panels are resistant to C0 2 permeating from within the cells of the foam and from air permeating in. The net effect of the painting of the foam faces is to substantially maintain the thermal conductance or λ value of the foam over prolonged periods of use. Thus, such paints provide a gas barrier to reduce gas transfer between the cells of the foam when exposed to atmospheric conditions and hence provide improved aged thermal conductivity properties. This is especially important for polyurethane and polyisocyanurate foams, and, to a lesser extent, for phenolic foams. The paint may be formulated to have specific properties. For example the paint may be fire resistant. The paint is preferably applied in-line just after facing removal. The application rate is at least 0.5g/m 2 and is preferably 10 to 50g/m 2 . The upper limit will be determined by the application and the economics of the process. The paint may be applied by passing the panel between calendering rollers 30 to apply paint to both faces. Alternatively the foam panel may be passed through a curtain of paint, for application. The paint may also be spayed onto one or both faces by spray heads 35. Electrostatic techniques may also be used to apply the paint. For example, the frame along which the foam passes may be charged to repel paint which is consequently preferentially attracted to the faces of the foam. After coating, the paint is cured. For example, a localised heat or radiation source may be applied in the form of a directed hot air source, an IR source, a UV source, a microwave source or the like. The foam may also be cured in an oven. To provide additional curing time, in-line, the panel may be passed through an accumulator. To assist coating and/or curing the panel may be turned on edge. Ideally, the facings 21, 22 are removed when the panel exits the oven 12 and in advance of cutting. Alternatively, it may be possible to remove the facings 21, 22 from the panel as the panel passes through the oven 12. The removal within the oven would be at a stage where the foam has sufficiently cured but before final cooling as one or both facings may be more easily removed at this stage. Indeed, both facings may not have to be removed at the same stage. The re- wound removed facings 21, 22 are coiled and the coils 24, 25 may then be re-used at the infeed either as a first or second facing. If desired, the facing may be reversed for re-use and/or a cleaning means may be provided for the collected facing before re-use. To facilitate removal one or both facings may be treated with a release means on the foam-engaging face of the facing. For example, silicone or wax may be applied. In order to improve facing removal, preferably the outer foam layers are not corona treated. Example 1 A typical foam formulation which may be used in the process of the invention is as follows: pph polyol (by wt) Polyester polyol 70 Polyether polyol 30 Silicone surfactant 2 Dimemylcyclohexylamine 0.6 Potassium acetate in monoethyleneglycol 3.0 Water 1.3 141 b 34 Crude diphenyl isocyanate (MDI) 214 (e.g. Suprasec 2085 supplied by ICI) Fire Retardant 10 The foam preferably has a significant cellular structure for use in thermal and/ or acoustic insulation applications. The foam is preferably polyurethane, polyisocyanurate, or phenolic. The first and/or second removable facings are typically selected from: polyolefin films (such as polypropylene, high or medium density polyethylene, low or linear low density, polyethylene), poly halogenated polyolefins (such as polytetrafluoro ethylene), waxed paper and waxed plastic films, other suitably treated paper, plastic, metal foil or glass films and facings and combinations thereof such that the facing can be continuously removed from the foam without significant damage to either facing or foam during or just following the production process. For example, the facing may be of polypropylene or a silicone treated polyethylene terephthalate (PET) film material. Example 2 An insulation board was produced using a conventional fixed-gap polyurethane foam laminator. The precursors were prepared as components A and B in the ratios shown below (parts by weight per hundred parts total reactive polyol). A and B were then mixed at high pressure (>100 bar g) in an impingement mixer and laid down onto the lower facings. This facing consisted of polypropylene film of 50 μm thickness. The lay-down method was a conventional oscillating gas-poker giving an approximately even spread of foam pre-polymer across the width of the board. Density of the foam was targeted at 32kg/m 3 . Composition of pre-polymer: (parts by weight) Component A Component B Polyester Polyol Mix 100 Fire Retardant 10 Silicone Surfactant 1.5 Water 0.5 Potassium acetate in monoethylene ϊglycol 1.2 Dabco TMR (Air Products) 3.0 Pentamemyldiethylenetriamine 0.3 Dimethylcyclohexylamine 0.4 HCFC 141b 32 Crude diphenyl isocyanate (MDI) 191 (e.g. suprasec 2086 from ICI) The upper facing was introduced over the lower as the reacting mix was moved continuously into a conventional fixed gap laminator (set at 60 mm) heated to 45°C. At the exit of the laminator the facings were continuously removed from the board top and bottom, and the solid insulation board cut to size. Board A was left uncoated whilst board C was then sprayed with an aluminised (metal flake) automotive refinish paint [Halford Chrome Finish Paint] both sides. By weight difference, the coating application rate was approximately 35g/m 2 . Samples 30cm square were then cut from boards A and C, these were left for 24 hours at room temperature and the thermal conductivity measured per ISO 8302 (1991) standard for steady-state thermal resistance measurement. The samples were then placed into an oven at 70°C to accelerate gas-interchange and simulate long term ageing performance. The following data were recorded. All results give λ in mW/m.K: Time period (from initial) Sample A (uncoated) Sample C (painted) Initial λ (mW/m.K) 18.0 18.2 After 2 weeks 19.0 18.9 4 weeks 20.2 19.0 8 weeks 21.3 20.0 10 weeks 21.5 20.0 15 weeks 22.5 20.8 20 weeks 22.8 21.6 25 weeks 23.1 21.6 Total delta λ 5.1mW/m.K 3.4 mW/m.K Thus the unexpected effect of the paint is to give an improved aged λ result, indicating significant reduction of gas interchange. As it is recognised that 25 weeks at 70°C can approximate to a 25 year aged result for polyurethane insulation (Ball, Simpson & Fleming, Cellular Polymers, pp. 110-149, volume 16, no. 2, 1997), this equates to a significant improvement in thermal efficiency over the lifetime of the product. Thus, the invention provides an efficient manufacturing method with significant cost reduction. Because a foam is produced with one or both faces exposed the foam can be readily treated depending on its intended application. For example, for underfloor or wall insulation a paint may be applied to one face. For fire applications, at least one of the faces may be coated with a fire resistant material. Most importantly the coating/painting of one and preferably both faces provides improved aged thermal conductivity properties. These and many other modifications to the invention will be readily apparent and accordingly the invention is not limited to the embodiments hereinbefore described which may be varied in detail.

Claims: CLAΓMS 1. A method for manufacturing a foam panel comprising the steps of: leading a first facing from a first facing supply to a foam lay down area; laying liquid foam reactants on the first facing; leading a second facing from a second facing supply over the liquid foam reactants; allowing the foam to expand between the facings to form a foam panel; removing at least one of the facings from the foam; and applying a coating to one or both faces of the foam from which the facing(s) has (have) been removed. 2. A method as claimed in claim 1 wherein the coating is applied in-line. 3. A method as claimed in claim 2 wherein the coating is applied in a liquid form. 4. A method as claimed in claim 2 or 3 wherein the coating is a paint. 5. A method as claimed in claim 4 wherein the paint contains non-gas permeable flake-like particles or platelets such as metal or glass flakes. 6. A method as claimed in claim 5 wherein the paint contains aluminium flakes. 7. A method as claimed in 5 or 6 wherein the paint is a leafing or non-leafing paint. 8. A method as claimed in any of claims 4 to 7 wherein the paint contains nanocomposites. 9. A method as claimed in any preceding claim wherein the coating is of low gas permeability, especially to C0 2 , 0 2 , N 2 and/or H 2 0. 10. A method as claimed in any preceding claim wherein the coating is applied by a calendering roll. 11. A method as claimed in any preceding claim wherein the coating is applied by passing the panel with the facing(s) removed, through a curtain of the coating material. 12. A method as claimed in any of preceding claim wherein the coating is applied by spray coating. 13. A method as claimed in any preceding claim wherein the coating is applied electrostatically. 14. A method as claimed in any preceding claim including the step, after applying the coating, of curing the coating on the foam, preferably the curing is carried out in-line. 15. A method as claimed in claim 14 wherein the coating is cured by heating and/or by application of radiation. 16. A method as claimed in claim 15 wherein the coating is cured by localised application of heat and/ or radiation. 17. A method as claimed in claim 15 or 16 wherein the coating is cured in an oven. 18. A method as claimed in any preceding claim wherein the method includes the step after coating, of passing the coated panels through an accumulator. 19. A method as claimed in any preceding claim including the step, before or after coating, of turning the panel to lie on an edge thereof. 20. A method as claimed in any preceding claim including the step, after coating of cutting the panel to a desired length. 21. A method as claimed in any of claims 14 to 20 including the step, after at least partial curing of the coating, of cutting the panel to a desired length. 22. A method as claimed in any preceding claim wherein both facings are removed from the foam. 23. A method as claimed in any preceding claim wherein one or both facings is/are peeled from the foam and coiled onto a take-off reel for re-use either as the first or second facing supply. 24. A method as claimed in any preceding claim wherein an upper facing is coiled onto an upper facing recycle coil to provide a facing supply for the second facing. 25. A method as claimed in any preceding claim wherein a lower facing is coiled onto a lower facing recycle coil to provide a facing supply for the first facing. 26. A method as claimed in claim 25 wherein the upper facing recycle coil is delivered to a second facing feeding station. 27. A method as claimed in claim 25 wherein the lower facing recycle coil is delivered to a first facing feeding station. 28. A method as claimed in any preceding claim wherein the first and/or second facings are removed from the foam core after at least partial curing of the foam core. 29. A method as claimed in any preceding claim wherein the first and/or second facings are removed from the core in advance of cutting of the foam to a desired length. 30. A method as claimed in any preceding claim wherein release means is provided between the inner face of the first and/ or second facing and the foam core. 31. A method as claimed in claim 30 wherein the release means is provided on the inner face of the first and/or second facing. 32. A method as claimed in any preceding claim wherein the first facing is selected from: polyolefin films (such as polypropylene, high or medium density polyethylene, low or linear low density, polyethylene), poly halogenated polyolefins (such as polytetrafluoro ethylene), waxed paper and waxed plastic films, other suitably treated paper, plastic, metal foil or glass films and facings and combinations thereof such that the facing can be continuously removed from the foam without significant damage to either facing or foam during or just following the production process. 33. A method as claimed in any preceding claim wherein the second facing is selected from: polyolefin films (such as polypropylene, high or medium density polyethylene, low or linear low density polyethylene), poly halogenated polyolefins (such as polytetrafluoro ethylene), waxed paper and waxed plastic films, other suitably treated paper, plastic, metal foil or glass films and facings and combinations thereof such that the facing can be continuously removed from the foam without significant damage to either facing or foam during or just following the production process. 34. A method as claimed in any preceding claim wherein the foam is selected from polyurethane, polyisocyanurate; and phenolic, 35. A method as claimed in claim 34 wherein the foam has significant cellular structure for use in thermal and/ or acoustic insulation applications. 36. A method for manufacturing a foam panel substantially as hereinbefore described. 37. A foam panel whenever manufactured by a method as claimed in any preceding claim. 38. A foam panel as claimed in claim 37 wherein the panel is free from a facing on one face thereof. 39. A foam panel as claimed in claim 37 wherein the panel is free from a facing on both faces thereof. 40. A foam panel as claimed in claim 38 or 39 wherein at least one of the faces of the panel from which the facing has been removed is coated with a coating material. 41. A foam panel as claimed in claim 40 wherein the coating material is paint. 42. A foam panel substantially as hereinbefore described. 43. A foam panel comprising a foam core having a first face and a second face, at least one of the faces having a coating applied thereto. 44. An underfloor insulation panel comprising a foam core having a first face and a second face, at least one of the faces having a coating applied thereto. 45. An insulation liner panel comprising a foam core having a first face and a second face, at lest one of the faces having a coating applied thereto. 46. A panel as claimed in any of claims 43 to 45 wherein the coating is a paint. 47. A foam panel as claimed in any of claims 43 to 46 wherein the foam core is of polyurethane, polyisocyanurate or phenolic material.

Inventors: MCCABE THOMAS, ROCHEFORT MALCOLM, MCCABE, THOMAS, ROCHEFORT, MALCOLM
Applicants: KINGSPAN RES & DEV LTD, MCCABE THOMAS, ROCHEFORT MALCOLM, KINGSPAN RESEARCH AND DEVELOPMENTS LIMITED, MCCABE, THOMAS, ROCHEFORT, MALCOLM
Application year: 1999
Main classification: B29C44
IPC codes: B29C44