Process for the autothermal reforming of a hydrocarbon feedstock containing higher hydrocarbons

Abstract: Process for preparation of a hydrogen and/or carbon monoxide rich gas by catalytic autothermal reforming of a hydrocarbon feedstock containing higher hydrocarbons in an autothermal reformer comprising the further steps of (a) passing the hydrocarbon feedstock through a reactor containing steam reforming catalyst to remove or reduce the contents of higher hydrocarbons in the hydrocarbon feedstock; (b) passing the effluent from the first reactor to an autothermal reformer; and (c) withdrawing from the autothermal reformer a product gas rich in hydrogen and carbonmonoxide.

Description: The present invention is directed to soot free autothermal reforming (ATR) of a hydrocarbon feed containing higher hydrocarbons. In the autothermal reforming, combustion of a hydrocarbon feed is carried out with substoichiometric amounts of oxygen by flame reactions in a burner combustion zone and, subsequently, steam reforming of the partially combusted feedstock in a fixed bed of steam reforming catalyst. Substoichiometric combustion of hydrocarbons leads disadvantageously to the formation of soot. Soot formation may be avoided by using a specific burner design and through controlling the operating conditions of the ATR process. Soot is formed in the flame of an autothermal reactor within certain ranges of operating conditions. When the amount of steam relative to the other components send to the ATR reactor is under a critical value, soot is formed in the reacting feed. One such burner useful in ATR is described in US-A-5,496,170. The limiting amount of steam can be expressed as the critical steam to carbon ratio, which is the molar feed flow rate of steam to the molar flow rate of carbon in the hydrocarbon feed. The hydrocarbon feedstocks can be in the form of natural gas or hydrocarbon including LPG, butane, naphtha, etc. The molar flow rate of carbon is calculated as the molar flow rate of the hydrocarbon times the carbon contents of the hydrocarbon. Examples of operation conditions, which do not result in soot formation, are summarized in an article by Christensen and Primdahl (Hydrocarbon processing, March 1994, pages 39-46). Those conditions are shown in Table 1. The tests have been conducted in a pilot plant. Due to heat loss from the relatively small pilot unit, the adiabatic ATR exit temperature will be higher than the measured ATR exit temperature. This means that if a large unit, from which the heat loss is negligible, is subjected to the exact same operating conditions, the ATR exit temperature will be close to the adiabatic ATR exit temperature. The soot precursors are formed in the combustion zone of the ATR. Most of the heat loss occurs after the combustion zone. A subsequent heat loss cannot have any influence on the reactions in the combustion zone. The oxygen to carbon ratio (O 2 /C) is also shown in Table 1. The definition of this ratio is analogue to the steam to carbon ratio, however, with steam substituted by oxygen. The exit temperature from the ATR reactor can be calculated from the O 2 /C ratio, when the heat loss from the reactor is known. Case No. Oxygen to Carbon Ratio H 2 O/C CO 2 /C Measured ATR Exit Temp.°C Adiabatic ATR Exit Temp.°C A 0.60 1.43 0 950 1013 B 0.62 0.59 0 1065 1173 C 0.60 0.86 0 1000 1073 D 0.67 0.68 0.47 1018 1147 E 0.70 0.67 0.75 1030 1147 F 0.73 0.58 0.98 1028 1177 Operation conditions which do not result in soot formation (from Christensen and Primdahl, 1994) Advantageously, the process is operated at low steam to carbon ratios, since a low ratio lowers the investment expenses for an ATR plant and reduces the necessary energy consumption in operating the plant. Additionally, a low steam to carbon ratio makes it possible to optimize the produced synthesis gas composition for the production of CO-rich gases for e.g. methanol or dimethyl ether synthesis and Fischer-Tropsch processes. The article by Christensen and Primdahl further discloses that, for processing heavy hydrocarbon feedstocks, such as naphtha, an additional adiabatic prereformer is needed. EP-A-522744 discloses a process for the production of a hydrogen containing synthesis gas from a hydrocarbon feedstock in which the hydrocarbon feedstock is divided into a first stream and a second stream. The first hydrocarbon stream is subjected to primary catalytic steam reforming, optionally subjected to secondary reforming and then cooled. The second hydrocarbon stream is subjected to a prereforming step of adiabatic low temperature steam reforming, followed by partial oxidation of the prereformed second stream using an oxygen containing gas to form a reformed second stream, and the reformed second stream is then cooled. Subsequently, the cooled reformed first stream and the cooled reformed second stream are mixed. It has been found that arranging a low temperature preforming reactor with steam reforming catalyst upstream the autothermal reformer reduces the critical steam to carbon ratio. The steam reforming reactor removes or reduces the content of higher hydrocarbons. Higher hydrocarbons are hydrocarbons that consist of two or more carbon atoms. The steam reforming catalyst will convert the higher hydrocarbons to a mixture of methane, carbonmonoxide, carbon-dioxide and hydrogen. The low temperature steam reforming reactor can be an adiabatic prereformer or a heated prereformer, e.g. in the form of a catalyzed heat exchanger coil as described in EP-A-855,366. The exit temperature of an effluent stream from the low temperature steam reforming reactor is not higher than 600°C. The present invention provides a process for the preparation of a hydrogen and/or carbon monoxide rich gas by catalytic autothermal reforming of a feedstock comprising natural gas and/or associated gas containing hydrocarbons with two or more carbon atoms, in an autothermal reformer, wherein the reforming step consists of (a) passing the feedstock through a first reactor containing steam reforming catalyst to remove or reduce the contents of hydrocarbons with two or more carbon atoms in the feedstock; (b) passing the effluent from the first reactor to an autothermal reformer; and (c) withdrawing from the autothermal reformer a product gas rich in hydrogen and carbon monoxide. The present invention is further directed to the use of a prereformer containing steam reforming catalyst upstream of an autothermal reformer to reduce the critical steam to carbon ratio. Preferred embodiments of the invention are set forth in the sub-claims. As an advantage of the invention it will be possible to operate the autothermal reactor at a lower steam to carbon ratio than when using the unconverted feed stream as feed for the autothermal reformer. As a second advantage, it is possible to preheat the feed gas for the ATR to a higher temperature when it contains no higher hydrocarbon. This results in a lower oxygen consumption by the process. The invention is in particular useful in the steam reforming of accociated gas. Associated gas is natural gas produced during oil production. This gas is usually flared at the drilling rig, since it is not economical to ship associated gas. Associated gas has a high content of higher hydrocarbons. Example 1 The test unit consists of a system for providing the feeds to the ATR reactor, the ATR reactor and equipment for post treatment of the product gas. The feed streams consist of natural gas, steam, oxygen, hydrogen and optionally butane. The composition of the natural gas is given in Table 2. All gases are compressed to the operating pressure and preheated to the operating temperature. The natural gas is desulphurized before entering the ATR reactor. The feeds are combined into two streams and send to the burner of the ATR. A first feed stream contains natural gas, hydrogen, steam, and optionally butane. This feed stream is heated to 500°C. The other feed stream contains oxygen and steam and is heated to 220°C. The pressure in the ATR reactor is 2.46 MPa. Optionally, the natural gas containing stream is passed through a prereformer before entering the ATR reactor. Also in this case, the gas stream is heated to 500°C before entering the ATR reactor. Component Mole fraction % N 2 0.42 CO 2 1.16 CH 4 94.55 C 2 2.75 C 3 0.70 C 4 0.31 C 5 + 0.11 Composition of natural gas In the ATR reactor, the substoichiometric combustion and subsequent catalytic steam reforming and shift reactions are carried out. The inlet and exit gas compositions are measured by gaschromatography. Downstream the ATR reactor, the product gas is cooled and the majority of the steam content of the product gas is condensed. If soot is formed, it is captured in the condensate. The condensate is subjected to both gravimetric and spectrophotometric examinations. The following tests were carried out to demonstrate the influence of passing the feed gas through a prereformer. In one test the feed gas was doped with butane. The butane concentration was 4.0 vol% of the total hydrocarbon. Each test was made by approaching the critical steam to carbon ratio from the steam rich side. The tests were initiated with a sufficiently high steam flow to ensure soot free conditions. The steam flow was then decreased in steps. The system was allowed to become stable, after which the condensate was examined for soot content. If the condensate was still soot free, the next step was taken. The term "soot free conditions" refers to a condition in which the soot formation is negligible. The soot amount formed at the critical steam to carbon ratio is approximately 3-5 ppm. The carbon flow rates were in the below described tests 100-103 Nm 3 /h. The hydrogen flow rate was 2 Nm 3 /h. The steam flow was adjusted to obtain the given steam to carbon ratio. The oxygen flow rate was adjusted to obtain the desired operating temperature in the range from 55 to 58 Nm 3 /h. Due to heat loss from the relatively small pilot, the adiabatic ATR exit temperature will be higher than the temperature given in Table 3. A large industrial unit will be very close to adiabatic condition and the exit temperature from such a unit will, hence, be very close to the adiabatic given in Table 3 when the industrial unit otherwise is operated at exactly the same conditions as quoted in Table 3. Test No Pre reformer Doped with butane O 2 /C ATR exit temp. Adiabatic exit temp. Critical steam to carbon ratio °C °C 1.1 No No 0.56 954 1019 0.70 1.2 Yes No 0.56 951 1011 0.64 1.3 No Yes 0.55 948 1006 0.79 The composition of the product gas from the ATR reactor in the tests of Table 3 was measured by gaschromatography. The gas compositions are shown in Table 4. Gas composition is given as dry mole percentage, which is the mole composition of the gas components when steam is not included. Test No H 2 N 2 CO CO 2 CH 4 % % % % % 1.1 64.4 0.14 26.74 6.81 1.87 1.2 65.1 0.12 25.17 6.99 2.62 1.3 64.5 0.12 26.09 7.67 1.62 Composition of product gas (dry mole%) of the test of Table 3 It is seen from Table 3, when passing the feed steam through a prereformer the critical steam to carbon ratio decreases. Furthermore, it is shown that an increased content of butane in the feed gas to the ATR causes the critical steam to carbon ratio to increase. This means that the advantage of passing the feed through a prereformer will increase, if the feed contains larger amount of higher hydrocarbon. Example 2 The same test unit as in Example 1 was used. Ethane or butane is added to the natural gas containing feed stream in test run 2 and 3. The carbon flow rates were in the below described tests 102-103 Nm 3 /h. The hydrogen flow rate was 3 Nm 3 /h. The steam flow was adjusted to obtain the given steam to carbon ratio. The oxygen flow rate was adjusted to obtain the desired operating temperature and was in the interval 58-60 Nm 3 /h. Test No Doped Hydrocarbon Concentration O 2 /C ATR exit temp. Adiabatic exit temp. Critical steam to carbon ratio Vol% of total hydrocarbon °C °C 2.1 No 0.58 1027 1109 0.33 2.2 Yes Ethane 7.2 0.58 1024 1113 0.41 2.3 Yes Butane 5.1 0.57 1023 1118 0.47 The composition of the product gas from the ATR reactor in the tests of Table 5 are shown in Table 6. Test No H 2 N 2 CO CO 2 CH 4 % % % % % 2.1 62.9 0.14 31.1 4.33 1.52 2.2 63.0 0.14 30.9 4.74 1.25 2.3 63.3 0.21 30.5 4.71 1.25 Composition of product gas (dry mole%) of the tests of Table 5 It is seen from Table 5 that a higher content of both ethane and butane causes the critical steam to carbon ratio to increase.

Claims: A process for the preparation of a hydrogen and/or carbon monoxide rich gas by catalytic autothermal reforming of a feedstock comprising natural gas and/or associated gas containing hydrocarbons with two or more carbon atoms, in an autothermal reformer, wherein the reforming step consists of (a) passing the feedstock through a first reactor containing steam reforming catalyst to remove or reduce the contents of hydrocarbons with two or more carbon atoms in the feedstock; (b) passing the effluent from the first reactor to an autothermal reformer; and (c) withdrawing from the autothermal reformer a product gas rich in hydrogen and carbon monoxide. The process of claim 1, wherein the first reactor is adiabatically operated. The process according to claim 1 or 2, wherein the temperature at the outlet of the first reactor is below 600°C. Use of a prereformer containing steam reforming catalyst upstream of an autothermal reformer to reduce the critical steam to carbon ratio, the feedstock to the prereformer comprising natural gas and/or associated gas containing hydrocarbons with two or more carbon atoms.

Inventors: CHRISTENSEN PETER SEIER, CHRISTENSEN THOMAS SANDAHL, HANSEN JENS-HENRIK BAK, PRIMDAHL IVAR IVARSEN, CHRISTENSEN, PETER SEIER, CHRISTENSEN, THOMAS SANDAHL, HANSEN, JENS-HENRIK BAK, PRIMDAHL, IVAR IVARSEN
Applicants: TOPSOE HALDOR AS, HALDOR TOPSOE A/S
Application year: 1999
Main classification: C01B3
IPC codes: C01B3, C10G35