Method of dyeing plastic lens

Abstract: A method and system for dyeing a plastic lens by printing a colored layer (2) on a print base body (3) with a dyeing solvent by using a printer (5) electrically controlled, the dyeing solvent containing a dissolved or fine-grained dispersed sublimatable dye, then, placing the print base body having the colored layer in a position where the colored layer faces a plastic lens (14) to be dyed without contact therewith, and heating the print base body in a vacuum to sublimate the dye from the colored layer and deposit the sublimated dye on the lens.

Description: The present invention relates to a method of dyeing plastic lenses, in particular, spectacle lenses. Heretofore, a dip dyeing method has been used in many cases to dye plastic lenses for spectacles. In this method, a dye solution is prepared by mixing dispersible dyes of three primary colors, i.e., red, blue, and yellow, and dispersing the mixture in water. The thus prepared dye solution is heated to about 90°C. A plastic lens is dipped in the heated dye solution, so that the lens is dyed. As an alternative to the above dip dyeing method, a vapor deposition dyeing method has been proposed. This vapor-deposition dyeing method is carried out by heating a sublimatable dye to sublimate, thereby dyeing a plastic lens which is being heated. In the above vapor-deposition dyeing method, the dyeing of lenses is effected by heating the sublimatable dye. As a result, a problem such as the disposal of waste solution after the dyeing will not arise. However, such a method has the disadvantages that it is difficult to deposit dyes at a fixed quantity to adhere on a lens surface, to prepare dyes in desired density, and to dye lenses in a deep color. The hue or tint of a dye to be used is almost artificially prepared. As a result, the prepared dye is apt to be uneven in color, which will cause a large problem in quality control. The conventional dip dyeing method mentioned above has also disadvantages that the interaction and condensation of the dispersible dyes cause variations and unevenness of hue or tint. This disables the stable provision of uniformly dyed objects. In addition, the dye solution after use has to be discharged, which causes a problem of disposal of waste solution and also prevents the effective use of dyes. In the dip dyeing method, furthermore, since the dye solution is heated, the dyeing work is carried out at high temperature and in a humid environment, in which the foul smelling resulting from the dye is also present. The use of the dip dyeing method thus causes a deteriorated working environment. From JP01-277 814 A a method of dyeing a plastic lens can be taken. A sublimate dye is used and applied onto the entire surface of a paper substrate by using a roll coater method. The paper substrate is deposited in a vacuum drying device. A white sheet wherein the central section is perforated in a predetermined shape is provided on the sheet applied with the sublimate dye. A lens holder is used having a shorter diameter at the side of the paper substrate applied with the sublimate dye and a longer diameter opposite thereto. The lens to be dyed is inserted into the lens holder. The vacuum dyeing device is heated and the pressure is reduced. According to the vacuum process under heating the dye is sublimated from the sublimate dye applied paper substrate resulting in a colour layer formed onto the surface of the plastic lens. It is the object of the present invention to overcome the initially discussed problems and to provide a dyeing method capable of facilitating preparation of dyes in desired density and also dying plastic lenses with a stabile hue or tin in every dying works, and improving working environment thereof. This object is solved by a method of dying a plastic lens as is defined in the independent claim 1. Preferred developments of the invention are given in the dependent claims. The accompanying drawings, which are incorporated in and constitute a part of this specification illustrate an embodiment of the invention and, together with the description, serve to explain the objects, advantages and principles of the invention. In the drawings, Fig. 1 is a schematic view of a print base body constructed of a white sheet of paper and two colored areas printed thereon, which is used in a first embodiment according to the present invention; Fig. 2 is a schematic internal view of a vacuum vapor-deposition transfer device to be used in the first embodiment of the invention; Figs. 3A and 3B are sectional views of a part of a lens support plate with a (left) hole used in the above embodiment; Fig. 4A is a cross sectional view of a dyeing jig used in a second embodiment according to the present invention; Fig. 4B is a schematic view of a print base body used in the second embodiment; Fig. 5 is a flow chart of a dyeing method according to the present invention; Fig. 6 is a schematic constructive view of various steps for dyeing plastic lenses in the first embodiment according to the present invention; Figs. 7A to 7D are schematic views of print base bodies produced in example 5, where Fig. 7A represents the present invention; and Fig. 8 is a graph showing the transmittance of lenses dyed using the print base bodies shown in Figs. 7A-7D. A detailed description of preferred embodiments of the dyeing method embodying the present invention will now be given referring to the accompanying drawings. In the following embodiments, the present invention is applied to spectacle plastic lenses. In a first embodiment, the production of a print base body to be used for dyeing plastic lenses is first explained and then the dyeing of the plastic lenses is described. Fig. 5 shows a flow chart of the dyeing method in the first embodiment. Fig. 6 is a schematic view of the dyeing system including a dyeing device (jig) and others for carrying out the dyeing method shown in Fig. 5. (1) Production of print base body; A print base body 3 shown in Fig. 1 is produced in the following manner. As a dyeing ink (a sublimatable dye), four colors of water-base dispersible dye inks (manufactured by Upepo Co. Ltd.), i.e., red, blue, yellow, and black inks are used. The ink is prepared by dissolving or fine-grain dispersing a sublimatable dye in a solvent. Those inks are filled in respective ink cartridges and mounted in an ink jet printer 5, e.g. manufactured by MIJ Co. Ltd. Subsequently, for outputting a print in a desired color and a density on the ink jet printer, a commercially available personal computer (referred to as "PC" hereinafter) is used to produce the hue and density of the inks (S1). This production of hue is handled by a drawing software or computer color matching (CCM) in the PC. Accordingly, data on a desired color once produced can be stored in the PC, and prints in an identical color tone and density can be output a number of times if required. For a base body on which layers of the sublimatable dye are to be formed thereon, an A4-sized white paper 1 (high-quality PPC paper), commercially available, is used. This white paper 1 is set in the printer and subjected to the printing using the dye in the hue and density predetermined by the operation of the PC (S2). On the paper 1, circular colored layers 2 are formed as shown in Fig. 1. A print base body 3 is thus completed. In the present embodiment, two colored areas 2 are formed in pairs on the white paper 1. This is because the formation in pairs is more convenient for dyeing a pair of spectacle lenses, i.e., for a right and left lenses. The diameter of the colored layer 2 is slightly larger than that of the lens to be dyed because, if the diameter of the colored layer 2 is smaller than the lens diameter the dye may not fully spread over the whole coloring surface of the lens. (2) Dyeing of plastic lenses; With the base body 3 produced as above, the dyeing of plastic lenses is effected as follows, using a vacuum vapor-deposition transfer device shown in Fig. 2 which is a schematic internal view of the device seen from its front side. The vacuum vapor-deposition transfer device 10 is provided, at its front upper portion, with an opening not shown through which the print base body 3 and plastic lenses 14 are inserted into the device 10 or removed therefrom. Reference number 11 denotes a support shaft which functions to move a support plate 12 for holding thereon the lenses 14 in a vertical direction and in a horizontal direction between the opening and a dyeing position. The movement of the support plate 12 by the support shaft 11 enables mounting or dismounting the lenses 14 on or from the support plate 12 through the opening. The support plate 12 has two circular holes 12a disposed symmetrically with respect to the support shaft 11, i.e., at a right and left sides thereof in Fig. 2. The circular hole 12a is designed to have a larger diameter than that of the lens to be mounted thereon. On the underside of the support plate 12, the print base body 3 (constructed of the white paper 1 with the colored layers 2 printed thereon) is attached so that the colored layers 2 are positioned on the upside of the body 3 and coaxially aligned with the holes 12a respectively, thereby to allow the dye of the colored layer 2 to sublimate toward the lens through the hole 12a. Fig. 3A is an enlarged view of a part of the support plate 12 with the hole 12a (a left one) in the first embodiment. A cylindrical lens holder 13 is joined with the support plate 12 so that the holder 13 is aligned with the hole 12a. This lens holder 13 is provided with, as shown in Fig. 3A, a lens holding groove 13a formed in a shape capable of holding the lens 14 to prevent the fall thereof. When the edge of the lens 14 is set in the lens holding groove 13a of the holder 13 joined with the support plate 12, the lens 14 can be held above the hole 12a. In the first embodiment, instead of the lens holder 13, another lens holder 13' having a different height shown in Fig. 3B may be used appropriately, whereby a distance from the print base body 3 to the lens 14 is changed, so that the dyeing density can be adjusted. In the present embodiment, six lens holders 13 of different heights are prepared so that the height can be adjusted in a range of 5-30 mm (in 5mm steps). Even if the identical print base body 3 is used, for example, as the height of the lens holder 13 is higher, the amount of sublimated dye which will reach the lens 14 is smaller. Accordingly, with the higher lens holder 13 selected, the lens 14 can be dyed in lighter (i.e., lower) color density. The material of the plastic lens 14 is selected from polycarbonate resin (e.g., diethyleneglycol bis-allyl carbonate polymer (CR-39)), polyurethane resin, allyl resin (e.g., allyl diglycol carbonate and its copolymer, and diallyl phthalate and its copolymer), fumaric acid resin (e.g., benzyl fumarate copolymer), styrene resin, polymethyl acrylate resin, fibrid resin (e.g., cellulose propionate) and so on. In the device 10, a heater 15 is disposed below the lens support plate 12 and serves to sublimate the dye of the layers 2 printed on the white paper 1. This heater 15 can be set to a desired temperature. The material of the heater 15 is aluminum which is high in thermal conductivity. By feeding current through a Nichrome wire not shown passing through the inside of the heater 15, the surface temperature of the heater 15 is increased. This surface temperature is detected by a temperature sensor 16 as to whether or not the temperature reaches a preset value. A rotary vacuum pump 17 is connected to the device 10 and used to lower the pressure in the device 10 for a dyeing operation. Reference numeral 18 denotes a leak valve provided to the device 10. This valve 18 is opened after the dyeing operation to take air into the device 10 maintained under vacuum, thereby to return it to atmospheric pressure. The vacuum vapor-deposition transfer device 10 configured as above is operated in the following manner to dye the plastic lens 14. First, the support shaft 11 is operated to move the support plate 12 upward and move horizontally toward the opening formed at the front side of the device 10. Then, the print base body 3 produced in the above mentioned process (1) is inserted into the device 10 and attached, placing its print surface (with the colored layers 2) up, to the underside of the support plate 12 with an adhesive tape and the like so that the colored layers 2 are aligned with the two holes 12a of the support plate 12 respectively. After the attachment of the base body 3 to the support plate 12, the lens holders 13 are fitted on the upside of the support plate 12. Subsequently, the plastic lenses 14 are set with the concave surface side down in the lens holders 13. The heater 15 is then heated to a desired heating temperature. In the present embodiment, the heating temperature of the heater 15 is preset in a range of 100-200°C. If the heating temperature is less than 100°C, the dye printed on the print base body 3 will not sublimate easily. If it is higher than 200°C, to the contrary, there are possibilities of deteriorating the quality of the dye or deforming the lens. Accordingly, the heating temperature of the heater 15 is preferably set in a range of 100-200°C and, more preferably, it is set at as high a temperature as possible within the range according to the material of the plastic lenses 14. The reason to set the heating temperature as high as possible for sublimation is that the higher temperature enables the reduction of the heating time needed for sublimating a dye in desired hue and density, and the increase of productivity in association therewith. Next, the opening of the device 10 is closed and the rotary vacuum pump 17 is activated to lower the pressure in the device 10, namely, to reduce the internal pressure of the device 10 to about 1-50 mmHg. There is no problem even if reducing the pressure lower than 1 mmHg, but a high-performance exhauster is needed in such cases. To the contrary, as the internal pressure of the device 10 is higher, the temperature required for dye sublimation is higher. Accordingly, the upper limit of the pressure is preferably 50 mmHg. The more preferable range of the pressure is 10 to 30 mmHg. When the sensor 16 detects that the heater 15 has been heated to the predetermined temperature, the support shaft 11 is operated to move the support plate 12 down until the plate 12 comes into contact with the heater 15 (S3) through the base body 3. With the support plate 12 being held in contact through the base body 3 with the heater 15, the base body 3 attached to the underside of the support plate 12 is heated by the heater 15 for the predetermined duration, e.g., 1-20 min. from the contact (S4). The sublimation of the dye applied on the base body 3 starts almost simultaneously with the contact to the heater 15. If the heating duration is less than 1 min., the dye is not enough sublimated to dye the plastic lens 14 in a predetermined color density. If the heating duration exceeds 20 min., the plastic lens 14 could be affected by the heating. Accordingly, the heating duration is preferably in a range of 1 to 20 min. and more preferably 3 to 10 min. Upon completion of the heating, the leak valve 18 is opened to return the pressure of the device 10 to normal. The support shaft 11 is operated to move the support plate 12 up to the opening of the device 10, and the plastic lens 14 is taken out through the opening. The sublimated dye is deposited on the plastic lens 14, but it could come off if left as it is. To avoid this, the plastic lens 14 is further heated in an oven 35 as shown in Fig. 6 under normal pressure to fix the deposited dye on the lens 14 (S5). Specifically, this process is carried out in the steps of first raising the temperature of the oven to a preset temperature which is as high as possible below the lens resistible temperature, heating the lens 14 in the oven 35 for α predetermined duration, and then taking the lens 14 out of the oven 35. This heating temperature in the present embodiment is in a range of 50°C to 150°C and the heating duration is in a range of 30 to 60 min. In the first embodiment, the plastic lens 14 is dyed from below with the sublimated dye heated from below in the vacuum vapor-deposition transfer device 10. Alternatively, the lens 14 may be placed with the concave surface side up so that the concave surface is dyed from above with the sublimated dye. This method of dyeing the lens from above is explained below in a second embodiment according to the present invention, referring to Fig. 4A. Fig. 4A is a schematic front sectional view of a dyeing jig used in the second embodiment. Like elements corresponding to those in the first embodiment are indicated by like numerals. Reference numeral 20 denotes a cylindrical support stand, on which a lens holder 13 provided with a lens holding groove 13a is mounted. As shown in Fig. 4A, the holder 13 holds a plastic lens 14 placed with the convex surface side down by fitting the edge of the lens 14 in the lens holding groove 13a. The lens 14 is thus supported above the support stand 20. A print base body 33 constructed of a white paper 31 with a colored layer 32 printed thereon is produced by the use of a PC and a printer in the same manner as in the first embodiment. Fig. 4B is a plane view of the print base body 33. Reference numeral 21 denotes a cylindrical support stand for supporting a print base body 33, and 22 denotes a base body holder for securely holding the print base body 33 put on the upside of the support stand 21, thereby preventing the displacement of the base body 33. In this embodiment, the base body 33 is placed so that the surface on which the colored layer 32 is printed is on the underside to allow the dye of the layer 32 to sublimate downward. The plastic lens 14 is placed so that its concave surface side is not in contact with the lens holding groove 13a. Accordingly, the whole concave surface of the lens 14 can be dyed. Reference numeral 23 denotes a halogen lamp which is disposed in a vacuum deposition device not shown and heats the base body 33 from above to sublimate the dye of the colored layer 32 formed on the base body 33. Subsequently, with the above constructed dyeing jig, the following operation is carried out to sublimate the dye from the print base body 33 in a vacuum condition, similarly to the first embodiment, thereby to dye the plastic lens 14. First, the stand 20 is put in the vacuum deposition device not shown, and the lens holder 13 is mounted on the stand 20. The plastic lens 14 is placed with the convex surface side down in the lens holding groove 13a of the lens holder 13. Thereafter, the cylindrical support stand 21 is disposed so as to enclose the lens support stand 20. The base body 33 is put on the support stand 21 as shown in Fig. 4A. The base body holder 22 is fitted on the upside of the support stand 21 to securely hold the base body 33 on the support stand 21, thereby preventing the displacement of the body 33. After setting of the plastic lens 14 and the print base body 33 in the dyeing jig in the above manner, a rotary vacuum pump is used in the same manner as in the first embodiment to reduce the pressure of the vacuum deposition device to a predetermined pressure in a range of about 1-50 mmHg, preferably, 10-30 mmHg. After detection on the predetermined pressure of the vacuum deposition device, the halogen lamp 23 is turned on to heat the print base body 33 until the surface temperature of the base body 33 reaches a predetermined temperature in a range of 100 to 220°C. When the surface temperature reaches the predetermined temperature, the halogen lamp 23 is turned off to terminate the heating. It is to be noted that turning off the halogen lamp 23 at this time is because in general the heat of a halogen lamp efficiently travels by radiation to an element being heated, i.e., the print base body 33 in the embodiment, and therefore, the dye sublimates simultaneously when the surface temperature of the base body 33 reaches the predetermined temperature. Upon completion of the heating to the base body 33, the internal pressure of the vacuum deposition device is returned to normal, and the plastic lens 14 is taken out of the deposition device. Thereafter, the lens 14 is heated for the heating time, i.e., 30-60 min. and the heating temperature, i.e., 50-150°C, thereby to finish the fixing of the dye onto the plastic lens 14. As described above, in the first and second embodiments, the dyeing of plastic lenses can be carried out in a dry working environment, not in a wet working environment caused by the conventional dip dyeing method. According to the present embodiments, the working environment can be improved, and workability can also be extremely improved. In addition, the preparation of inks is conducted under digital-control by the PC, so that the dye can also be printed to the print base body at the amount always controlled. Accordingly, the dyeing method used therein in the embodiments can reduce unevenness in the hue and density and provide the excellent effect for productions which are low in the volume and wide in the variety. Since the density of the dye to be printed on the print base body is controlled by the PC, the lens can be dyed in a desired density gradient without color unevenness and color missing. Next, description is made on various examples using the dyeing method in the first and second embodiments according to the present invention. Example 1 In Example 1, the vacuum vapor-deposition transfer device 10 in the first embodiment is used as a dyeing jig. A CR-39 lens is used as the plastic lens 14 to be dyed. For a sublimatable ink, a water-base dispersible dye manufactured by UPEPO Co. Ltd. is used. By the use of a drawing software in the PC, the color data is produced such that the hue of the dye is brown color (the combination ratio of red, blue, and yellow equals to 2-1-3) and the color density is 30% (in a light-shield rate). Thereafter, two circular colored layers 2 each having a slightly larger diameter than the diameter of a lens to be dyed are printed on the white paper 1 (high-quality PPC paper) based on the color data produced as above, thus completing the print base body 3. This print base body 3 is dried and then attached to the underside of the support plate 12 in the device 10 with an adhesive tape and the like. The lens holders 13 are mounted on the support plate 12 at respective positions of the holes 12a. Then, the plastic lenses 14 (CR-39) are set one-by-one in the lens holders 13 so that the concave surface of the lens 14 is in the underside. The lens holder 13 having a height of 15mm is used in the present example. The heater 15 is turned on and its temperature is sensed by the temperature sensor 16. When the sensor 16 detects that the temperature of the heater 15 reaches 200°C, the rotary vacuum pump 17 is activated to reduce the internal pressure of the device 10 to 10mmHg. Then, the support shaft 11 is operated to move the support plate 12 downward until the print base body 3 attached to the underside of the plate 12 comes into contact with the heater 15 to thereby start sublimation of the dye of the colored layers 2. The contact time between the base body 3 and the heater 5, i.e., the heating time, is 5 min. After a lapse of the predetermined time (5 min.), the leak valve 18 is opened to return the pressure of the device 10 to a normal pressure. The dyed plastic lenses 14 are taken out of the device 10 and then put in the oven 35 at the heating temperature of 135°C and for the heating time of 30 min., fixing the color (i.e., the deposited dye) on the plastic lenses 14. After this fixing, the dyed lenses 14 are visually checked as to whether the dyed color agrees with a desired color without inferior appearance, color unevenness, color missing. As a result of the visual observation, there is no defect in the above points. Example 2 The dyeing operation is carried out to dye plastic lenses in a (half) density gradient in the same dyeing conditions as in the Example 1. The color data is produced by the PC such that the density gradient is adjusted to have the light shield rate of 30% at a point of 10mm distant from the geometrical center of the lens. In the same way as in the Example 1, two circular colored layers 2 are printed on a white paper 1 to form a print base body 3. With this base body 3, the plastic lenses 14 are dyed to have a predetermined density gradient. The final plastic lenses 14 are excellent in colored conditions and no defect is visually observed regarding color evenness and others. Example 3 The same dyeing as in the Example 2 is carried out at each dyeing density in a range of 10% to 90% other than 30% to provide a whole colored plastic lens and other colored ones having different density gradients. No color unevenness and others are found in a visual check. Example 4 The dyeing jig shown in Fig. 4A is put in a vacuum deposition device in general use. A plastic lens 14 made of the same material as in the first embodiment is used. A print base body 33 shown in Fig. 4B and the plastic lens 14 are placed in respective positions in the dyeing jig. The rotary vacuum pump 17 is activated to reduce the internal pressure of the deposition device 10 to 10mmHg. Subsequently, a halogen lamp 23 is turned on to heat the print base body 33 until its surface temperature reaches 210°C. When the surface temperature reaches 210°C, the halogen lamp is immediately turned off. The dye is sublimated toward and deposited on the plastic lens. The pressure of the device is then returned to normal. The plastic lens 14 taken out of the device is put in an oven 35 at 135°C and for about 30 min. to fix the color (dye). After the fixing, a visual check is made as to appearance defects such as color unevenness, color missing, and others and whether the dyed color agrees with a desired color. Consequently, no problem is found in the above visual observation points. Example 5 By using the dyeing system of Fig. 2 and selecting a gradient pattern in a drawing software in the PC, four print base bodies 50A-50D shown in Figs. 7A-7D are produced. Figs. 7A and 7C have a colored layer printed in gradient (gradation) density on a white paper 40. The color (a combination of red(R), green(G), and blue(B)) of the colored layer 41 to be printed is prepared in the drawing software in the PC so that the color index numbers of R,G,B are 0, 255, 255. In this example, the color combination is determined to (R,G,B)=(0,255,255), but not limited thereto and it may be appropriately selected to suit the needs or preferences. The print base body 50A shown in Fig. 7A has a circular colored layer 41 according to the invention printed on a white paper 40, based on the gradient pattern selected in the drawing software. This selected pattern is of gradually changing gradient density over all. The print base body 50B shown in Fig. 7B has a substantially semicircular colored layer 42 on a white paper 40, the colored layer 42 is wholly constant in density. Specifically, the brightness is 255, the hue is 180, the color saturation is 255, each of which is one of 256 steps including 0 to 255. The print base body 50C shown in Fig. 7C has a substantially semicircular colored layer 43 on a white paper 40. The colored layer 43 is formed such that about two thirds of the layer 43 (corresponding to a colored layer 43a) is colored in constant density (the brightness is 255, the hue is 180, the color saturation is 255), and the remaining one-third (corresponding to a colored layer 43b) is colored in gradually changing gradient density. The print base body 50D shown in Fig. 7D has a substantially semicircular colored layer 44 on a white paper 40. The colored layer 44 is formed such that about two thirds of the layer 44 (corresponding to a colored layer 44a) is colored in dark density (the brightness is 255, the hue is 180, the color saturation is 255) and the remaining one-third (corresponding to a colored layer 44b) is colored in light density(specifically, the darkness is about half as compared with the colored layer 44a). With the use of those print base bodies 50A-50D, plastic lenses 14 are dyed with the same dyeing jig as in the Example 4. The material of lenses and the dyeing conditions are the same as in the first embodiment. After dyeing, any color unevenness and other defects are not found in a visual check on the appearance of the lenses. Furthermore, the transmittance of the plastic lenses 14 dyed using the print base bodies 50A-50D are measured. This measurement is carried out by measuring the transmittance at several points in 5mm steps on the diametrical line of the lens, starting from one point near the outer bound of the lens (for example, one point in the darkest dyed portion in Fig. 7A). A measurement device used in this example is MODEL 304 manufactured by ASAHI SPECTRA CO., LTD. The measurement result is shown in Fig. 8. The horizontal axis of the graph indicates the distance from the measurement start point and the vertical axis indicates the transmittance measured at each measurement point. It is to be noted that, as the color density of the dyed lens is lower, the transmittance is higher. Four lines A to D indicate the results of the lenses dyed by the use of the print base body 50A-50D, respectively. In the above manner, the plastic lenses 14 are dyed with respective gradient patterns by the use of the corresponding base body 50A-50D. As shown in the graph, for example, with the base body 50A according to the invention, the lens 14 is dyed with the gradient pattern having a small part colored in dark density and providing a sudden change to light density. With the base bodies 50B,50C, the lenses 14 are dyed with the gradient patterns having a constant density transition. With the base body 50D, the lens 14 is dyed with the gradient pattern having a large part colored in dark density and providing a sudden change to light density. Although it is very difficult to conduct the dyeing with the fine gradient patterns by the conventional wet method, the dyeing method in the above embodiments according to the present invention enables to dye lenses with fine gradient patterns. Specifically, a lens can be dyed with an optional gradient pattern selected from among those shown in Figs. 7A-7D or a gradient pattern of halftone between those gradient patterns. Although a water-base ink is used in the above embodiments, an oil-base ink can provide the same effect. In the case of the oil-base ink, which could be dried in the head portion of an ink cartridge and may cause clogging of the head, a piezoelectric-type ink jet printer is preferably used. In the above embodiments, although the heating to the print base body is conducted from above or below the base body, it may be carried out from side of the base body to sublimate the dye therefrom. Furthermore, the ink jet type printer is used in the above embodiment to print the colored layer on the print base body. Alternately, instead of the sublimation type printer and ink cartridges, a laser printer using toner cartridges or an output device which outputs the data from a PC such as a plotter and the like may be used. Furthermore, since the color density can be digitally controlled by the PC, the same color can be read if the color which is frequently ordered is assigned in advance to a management number of color data. This makes it possible to retain the stability of the color to be printed and also to efficiently conduct the dyeing work. As described above in detail, according to the present invention, the adjustment of color density to be provided to a plastic lens can be facilitated, and the lens can be dyed in a stable hue. In addition, the dyeing work can be carried out in a comfortable working environment without deterioration therein. invention to the precise form disclosed, and modifications and variations are possible in light of the above teachings or may be acquired from practice of the invention. The embodiment chosen and described in order to explain the principles of the invention and its practical application to enable one skilled in the art to utilize the invention in various embodiments and with various modifications as are suited to the particular use contemplated. It is intended that the scope of the invention be defined by the claims appended hereto, and their equivalents.

Claims: A method of dyeing a plastic lens, including: a step of printing a print area (2, 32, 41 - 44) on a print base body (3, 33, 50A - 50D) with an ink containing a dissolved or fine-grained dispersed sublimatable dye; a step of placing the print base body (3, 33, 50A - 50D) having the print area (2, 32, 41 - 44) printed with the ink in a vacuum vapor-deposition transfer device (10) so that the print area faces the plastic lens (14) to be dyed without contact therewith; and a step of heating the print base body (3, 33, 50A - 50D) under vacuum in the vacuum vapor-deposition device (10) thereby sublimating the dye of the print area (2, 32, 41 - 44) to vapor-deposit the sublimated dye on the lens (14); characterized by : a step of inputting data of at least one of color, density, and gradient pattern into a computer (PC); wherein a printer (5) is connected to the computer (PC) and prints the print area (2, 32, 41 - 44) on the print base body (3, 33, 50A - 50D) with the ink based on the data stored in and controlled by the computer (PC) in an almost circular form the circle having a larger diameter than that of the lens (14) to by dyed. The dyeing method according to claim 1, including a step of heating the dye lens (14) with the vapor-deposited dye up to a temperature below the lens resistible temperature to fix the dye on the lens (14). The dyeing method according to claim 1 or 2, wherein the placing step includes adjusting the distance between the print base body (3, 33, 50A - 50D) and the lens (14) to be dyed so as to adjust the density. The dyeing method according to one of claims 1 to 3, wherein the printing step includes simultaneously printing an area (2) for a right eye lens (14) and another print area (2) for a left eye lens (14) on the print base body (3) with the ink to vapor-deposit the dye onto a pair of spectacle lenses.

Inventors: INUDUKA MINORU, KAMATA KENICHI, YAMADA TETSUO, INUDUKA, MINORU, KAMATA, KENICHI, YAMADA, TETSUO
Applicants: NIDEK KK, NIDEK CO., LTD.
Application year: 1999
Main classification: B29D11
IPC codes: C23C14, D06P5, G02C7