Process for making high denier filaments of thermotropic liquid crystalline polymers and composition thereof

Abstract: The present invention discloses and claims a novel process for the formation of high denier as-spun and heat-treated multilobal filaments of a thermotropic liquid crystalline polymer. Preferred embodiments include process for the formation of as-spun and heat treated octalobal monofilaments of a few wholly aromatic polyesters and polyesteramides. The process involves (a) heating of a thermotropic liquid crystalline polymer to above its melting transition temperature; (b) passing said molten polymer through an extrusion chamber equipped with an extrusion capillary having a multilobal cross-section to form a multilobal filament; and (c) winding the filament at a suitable draw-down. The filaments so formed are of at least 50 denier per filament (dpf) and feature essentially uniform molecular orientation across their cross-section. In a final optional step, the filaments are heat treated in stages to form filaments exhibiting excellent tensile properties. Both as-spun and heat-treated filaments feature remarkably good tensile properties comparable to those of round filaments. Most importantly, the multilobal filaments of this invention feature much superior adhesion properties than the conventional round filaments.

Description: BACKGROUND OF THE INVENTION Field of the Invention The present invention relates to processes for forming multilobal filaments of a thermotropic liquid crystalline polymer. Specifically, the present invention provides processes for forming as-spun and heat-treated high denier multilobal filaments of a variety of thermotropic liquid crystalline wholly aromatic polyesters and polyesteramides. This invention also relates to as-spun and heat-treated high denier multilobal filaments of thermotropic liquid crystalline polyesters and polyesteramides. Description of the Prior Art Thermotropic liquid crystalline polymers (LCPs) are an important class of polymers, which are generally wholly aromatic molecules containing a variety of heteroatom linkages including ester and/or esteramide linkages. Upon heating to sufficiently high temperature, LCPs melt to form a liquid crystalline melt phase (often referred to as "anisotropic phase") rather than an isotropic melt. Generally, LCPs consist of linear ("rigid rod") molecules that can line up to yield the desired liquid crystalline order. As a result, LCPs feature low melt viscosity and thus improved performance and processabilities. Because LCPs orient to form "rigid rod" linear molecules, LCPs exhibit extremely high mechanical properties. Thus, it is well known in the art that LCPs can be formed into shaped articles, such as films, rods, pipes, fibers, and various other molded articles. In addition, it is also known in the art that LCPs, particularly in the fiber form, exhibit exceptionally high mechanical properties after a heat treatment process. However, all of the known methods in the art describe formation of only the low denier fibers, e.g., of about 10 deniers per filament (dpf), which exhibit high mechanical properties in their as-spun as well as heat-treated forms. Furthermore, there are no reports in the prior art that filaments having multilobal cross-section can be made from LCPs. More importantly, filaments of LCPs generally do not adhere to various other similar or dissimilar materials. Thus it is an object of the present invention to provide a process for forming uniformly oriented high denier multilobal LCP filaments. The high denier filament means a filament of higher than 50 dpf. It is also an object of the present invention to provide a process for forming high denier LCP multilobal filaments of higher than 50 dpf, which exhibit enhanced mechanical, thermal and chemical resistance properties in the as-spun as well as heat-treated form. It is further an object of the present invention to provide a process for forming high denier LCP multilobal filaments, which exhibit properties comparable to those of low denier LCP round filaments (i.e., filaments of less than 10 dpf) in their as-spun as well as heat treated states. It is also an object of the present invention to provide high denier LCP multilobal filaments of higher than 50 dpf having properties comparable to those of low denier LCP round filaments of less than 10 dpf. Finally, it is an object of the present invention to provide high denier LCP multilobal filaments that feature improved adhesion properties. It is high desirability to forming uniformly oriented high denier LCP filaments, which filaments exhibit enhanced mechanical, thermal and chemical resistance properties in the as-spun as well as heat-treated form. For example, high denier LCP filaments can replace steel wires in steel belted tires. Furthermore, since LCP filaments are of substantially lower density when compared with steel wires, LCP filaments are expected to feature properties superior to those exhibited by steel wires. In addition the prior art indicates that there is a real need for high denier LCP filaments that exhibit enhanced mechanical, thermal, and chemical resistance properties. Prior Art The following references are disclosed as background prior art. U.S. Patent No. 4,183,895 describes a process for treating anisotropic melt forming polymeric products. A process of heat treatment reportedly yielded fibers having enhanced mechanical properties, and the fiber tenacity was reported as being increased by at least 50% and to at least 10 grams per denier. U.S. Patent No. 4,468,364 describes a process for extruding thermotropic liquid crystalline polymers (LCPs). It is claimed that extrusion of an LCP through a die orifice having an L/D ratio of less than 2 (preferably 0), and at a draw-down ratio of less than 4 (preferably 1), yields filaments featuring high mechanical properties. U.S. Patent No. 4,910,057 describes a highly elongated member of substantially uniform cross-sectional configuration which is capable of improved service as a stiffening support in an optical fiber cable. U.S. Patent No. 5,246,776 describes an aramid monofilament and method of making the same. U.S. Patent No. 5,427,165 describes a reinforcement assemblage formed at least in part of continuous monofilaments of liquid crystal organic polymer(s). The polymers used therein are primarily aramids. Japanese laid open Patent No. 4-333616 describes a method of manufacturing filaments of 50 to 2000 dpf from molten liquid crystalline polymers. The heat-treated mechanical properties of these filaments were significantly inferior to the properties reported for the corresponding lower denier filaments of 5 to 10 dpf. J. Rheology 1992, Vol. 36 (p. 1057-1078) reports a study of the rheology and orientation behavior of a thermotropic liquid crystalline polyester using capillary dies of different aspect rations. J. Appl. Polym. Sci. 1995, Vol. 55 (p. 1489-1493) reports orientation distribution in extruded rods of a thermotropic liquid crystalline polyesters. The orientation function increases with increasing apparent shear rate from 166 to 270 sec -1 , but decreases with increasing apparent shear rate from 566 to 780 sec -1 . SUMMARY OF THE INVENTION Unexpectedly and surprisingly it has now been found that both as-spun and heat-treated high denier multilobal filaments of at least 50 denier per filaments can be made which feature essentially uniform molecular orientation across the filament cross-section. Furthermore, these high denier filaments feature remarkably good tensile properties, retaining at least 80 to 90 percent of the properties expected of conventional low denier - 5 to 10 dpf filaments, which properties for high denier filament were hitherto unattainable by any of the known prior art references as briefly described hereinabove. Thus, in accordance with this invention there is provided a process for forming a multilobal filament of a thermotropic liquid crystalline polymer, said polymer being selected from the group consisting of wholly aromatic polyesters, aromatic-aliphatic polyesters, aromatic polyazomethines, aromatic polyester amides, and aromatic polyester carbonates, and having the following properties: (i) denier of at least 50 denier per filament; (ii) tenacity of at least 8 grams per denier; (iii) modulus of at least 450 grams per denier; and (iv) elongation of at least 2 percent. The process of the present invention is comprised of the following steps: (a) heating a thermotropic liquid crystalline polymer to a temperature of at least 15 °C above its melting transition to form a fluid stream of said thermotropic polymer; (b) passing said stream through a heated extrusion chamber, wherein said chamber is disposed with a suitable cylindrical orifice having a multilobal cross-section to form the multilobal filament of said polymer; and (c) winding said filament at a take-up speed of at least 200 meters per minute and at a draw-down ratio from 4 to 40 so as to form the filament of essentially uniform molecular orientation across its cross-section and having a denier of at least 50 denier per filament. In another aspect of the invention there is also provided a process for forming a heat-treated multilobal filament of a thermotropic liquid crystalline polymer, said polymer being selected from the group consisting of wholly aromatic polyesters, aromatic-aliphatic polyesters, aromatic polyazomethines, aromatic polyester amides, and aromatic polyester carbonates, and having the following properties: (i) denier of at least 50 denier per filament; (ii) tenacity of at least 20 grams per denier; (iii) modulus of at least 600 grams per denier; and (iv) elongation of at least 3 percent. Thus in accordance with this aspect of the present invention, the process is comprised of the following steps: (a) heating a thermotropic liquid crystalline polymer to a temperature of 15 °C to 50 °C above its melting transition to form a fluid stream of said polymer; (b) extruding said stream of polymer through a heated cylindrical spinneret having at least one extrusion capillary of multilobal cross-section to form a multilobal filament; (c) winding said filament at a take-up speed of at least 200 meters per minute and at a draw-down ratio of 4 to 40 so as to form a filament of essentially uniform molecular orientation across its cross-section and having a denier in the range of from 50 to 1000 denier per filament; and (d) heat-treating said multilobal filament at a temperature of 10° to 30°C below the melting point of said polymer and pressure conditions for a sufficient period of time, optionally in the presence of an inert atmosphere, to form the heat-treated filament. In yet another aspect of this invention there is also provided an as-spun multilobal filament of a thermotropic liquid crystalline polymer. In a further aspect of this invention there is also provided a heat-treated multilobal filament of a thermotropic liquid crystalline polymer. Other aspects and advantages of the present invention are described further in the following detailed description of the preferred embodiments thereof. DETAILED DESCRIPTION OF THE INVENTION In accordance with this invention there is provided a process for forming a multilobal filament of a thermotropic liquid crystalline polymer, said polymer being selected from the group consisting of wholly aromatic polyesters, aromatic-aliphatic polyesters, aromatic polyazomethines, aromatic polyester amides, and aromatic polyester carbonates, and having the following properties: (i) denier of at least 50 denier per filament; (ii) tenacity of at least 8 grams per denier; (iii) modulus of at least 450 grams per denier; and (iv) elongation of at least 2 percent. The process of the present invention is comprised of the following steps: (a) heating a thermotropic liquid crystalline polymer to a temperature of at least 15 °C above its melting transition to form a fluid stream of said thermotropic polymer; (b) passing said stream through a heated extrusion chamber, wherein said chamber is disposed with a suitable cylindrical orifice having a multilobal cross-section to form the multilobal filament of said polymer; and (c) winding said filament at a take-up speed of at least 200 meters per minute and at a draw-down ratio from 4 to 40 so as to form the filament of essentially uniform molecular orientation across its cross-section and having a denier of at least 50 denier per filament. In accordance with the process of the present invention, the preferred polymers are thermotropic liquid crystalline polymers. Thermotropic liquid crystal polymers are polymers which are liquid crystalline (i.e., anisotropic) in the melt phase. Thermotropic liquid crystal polymers include wholly aromatic polyesters, aromatic-aliphatic polyesters, aromatic polyazomethines, aromatic polyesteramides, aromatic polyamides, and aromatic polyester-carbonates. The aromatic polyesters are considered to be "wholly" aromatic in the sense that each moiety present in the polyester contributes at least one aromatic ring to the polymer backbone. Specific examples of suitable aromatic-aliphatic polyesters are copolymers of polyethylene terephthalate and hydroxybenzoic acid as disclosed in Polyester X7G-A Self Reinforced Thermoplastic, by W: J. Jackson, Jr., H. F. Kuhfuss, and T. F. Gray, Jr., 30th Anniversary Technical Conference, 1975 Reinforced Plastics/Composites Institute, The Society of the Plastics Industry, Inc., Section 17-D, Pages 1-4. A further disclosure of such copolymer can be found in "Liquid Crystal Polymers: I. Preparation and Properties of p-Hydroxybenzoic Acid Copolymers," Journal of Polymer Science, Polymer Chemistry Edition, Vol. 14, pp. 2043-58 (1976), by W. J. Jackson, Jr. and H. F. Kuhfuss. Aromatic polyazomethines and processes of preparing the same are disclosed in the U.S. Patent Nos. 3,493,522; 3,493,524; 3,503,739; 3,516,970; 3,516,971; 3,526,611; 4,048,148; and 4,122,070. Specific examples of such polymers include poly(nitrilo-2-methyl-1,4-phenylenenitriloethylidyne-1,4-phenyleneethylidyne), poly(nitrilo-2-methyl-1,4-phenylene-nitrilomethylidyne-1,4-phenylenemethylidyne); and poly(nitrilo-2-chloro-1,4-phenylenenitrilomethylidyne-1,4-phenylene-methylidyne). Aromatic polyesteramides are disclosed in U.S. Patent Nos. 5,204,443, 4,330,457, 4,966,956, 4,355,132, 4,339,375, 4,351,917 and 4,351,918. Specific examples of such polymers include polymer formed from the monomers comprising 4-hydroxybenzoic acid, 2,6-hydroxynaphthoic acid, terephthalic acid, 4,4'-biphenol, and 4-aminophenol; and polymer formed from the monomers comprising 4-hydroxybenzoic acid, 2,6-naphthalene dicarboxylic acid, terephthalic acid, isophthalic acid, hydroquinone, and 4-aminophenol. Preferred aromatic polyamides are those which are melt processable and form thermotropic melt phase as described hereinabove. Specific examples of such polymers include polymer formed from the monomers comprising terephthalic acid, isophthalic acid, and 2,2'-bis(4-aminophenyl)propane. Aromatic polyester-carbonates are disclosed in U.S. Patent No. 4,107,143, which is herein incorporated by reference in its entirety. Examples of such polymers include those consisting essentially of hydroxybenzoic acid units, hydroquinone units, carbonate units, and aromatic carboxylic acid units. The liquid crystal polymers which are preferred for use in the process of the present invention are the thermotropic wholly aromatic polyesters. Specific examples of such polymers may be found in U.S. Patent Nos. 3,991,013; 3,991,014; 4,057,597; 4,066,620; 4,075,262; 4,118,372; 4,146,702; 4,153,779; 4,156,070; 4,159,365; 4,169,933; 4,181,792; and 4,188,476, and U.K. Application No. 2,002,404. Wholly aromatic polyesters which are preferred for use in the present invention are disclosed in commonly-assigned U.S. Patent Nos. 4,067,852; 4,083,829; 4,130,545; 4,161,470; 4,184,996; 4,238,599; 4,238,598; 4,230,817; 4,224,433; 4,219,461; and 4,256,624. The wholly aromatic polyesters disclosed therein typically are capable of forming an anisotropic melt phase at a temperature below approximately 350°C. The wholly aromatic polyesters which are suitable for use in the process of the present invention may be formed by a variety of ester-forming techniques thereby organic monomer compounds possessing functional groups which upon condensation form the requisite recurring moieties are reacted. For instance, the functional groups of the organic monomer compounds may be carboxylic acid groups, hydroxyl groups, ester groups, acyloxy groups, acid halides, etc. The organic monomer compounds may be reacted in the absence of a heat exchange fluid via a melt acidolysis procedure. Accordingly, they may be heated initially to form a melt solution of the reactants with the reaction continuing as solid polymer particles are suspended therein. A vacuum may be applied to facilitate removal of volatiles formed during the final stage of the condensation (e.g., acetic acid or water). In commonly-assigned U.S. Patent No. 4,083,829, entitled "Melt Processable Thermotropic Wholly Aromatic Polyester," there is described a slurry polymerization process which may be employed to form the wholly aromatic polyesters which are preferred for use in the present invention. According to such a process, the solid product is suspended in a heat exchange medium. When employing either the melt acidolysis procedure or the slurry procedure of U.S. Patent No. 4,083,829, the organic monomer reactants from which the wholly aromatic polyesters are derived may be initially provided in a modified form whereby the usual hydroxy groups of such monomers are esterified (i.e., they are provided as lower acyl esters). The lower acyl groups preferably have from about two to about four carbon atoms. Preferably, the acetate esters of organic monomer reactants are provided. Representative catalysts which optionally may be employed in either the melt acidolysis procedure or in the slurry procedure of U.S. Patent No. 4,083,829 include dialkyl tin oxide (e.g., dibutyl tin oxide), diaryl tin oxide, titanium dioxide, antimony trioxide, alkoxy titanium silicates, titanium alkoxides, alkali and alkaline earth metal salts of carboxylic acids (e.g., zinc acetate), to gaseous acid catalysts such as Lewis acids (e.g., BF 3 ), hydrogen halides (e.g., HCl), and similar catalysts known to those skilled in the art. The quantity of catalyst utilized in a process is typically about 0.001 to about 1 percent by weight based upon the total monomer weight, and most commonly about 0.01 to about 0.2 percent by weight. The wholly aromatic polyesters which are preferred for use in the present invention commonly exhibit a weight average molecular weight of 10,000 to 200,000, and preferably 20,000 to 50,000; for example, 30,000 to 40,000. Such molecular weight may be determined by commonly used techniques, for example, gel permeation chromatography or solution viscosity measurements. Other methods include end group determination via infrared spectroscopy on compression molded films or nuclear magnetic resonance spectroscopic (NMR) measurements of polymeric solutions or solid phase NMR of polymer powder or films. Alternatively, light scattering techniques in a pentafluorophenol solution (or equivolume solvent mixture of pentafluorophenol and hexafluoroisopropanol) may be employed to determine the molecular weight. The wholly aromatic polyesters or polyesteramides additionally commonly exhibit an inherent viscosity (i.e., I.V.) of at least 2.0 dL/g,; for example 2.0 to 10.0 dL/g, when dissolved in a concentration of 0.1 percent by weight in a 1:1 solvent mixture of hexafluoroisopropanol(HFIP)/pentafluorophenol (PFP)(v/v) at 25 °C. Especially preferred polymers for the process of this invention are wholly aromatic polyesters and polyesteramides. In preferred embodiments of this invention, specifically preferred polyesters are listed below: a) The wholly aromatic polyester capable of forming an anisotropic melt phase at a temperature below 350°C consisting essentially of the recurring moieties I and II wherein: I is and II is The wholly aromatic polyester as described above is disclosed in U. S. Patent No. 4,161,470. The polyester comprises 10 to 90 mole percent of moiety I, and 10 to 90 mole percent of moiety II. In one embodiment, moiety II is present in a concentration of 65 to 85 mole percent, and preferably in a concentration of 70 to 80 mole percent; e.g., 75 mole percent. In another embodiment, moiety II is present in a lesser proportion of 15 to 35 mole percent, and preferably in a concentration of 20 to 30 mole percent. b) The wholly aromatic polyester capable of forming an anisotropic melt phase at a temperature below 400°C consisting essentially of the recurring moieties I, II, III, and VII wherein: I is II is III is and VII is The polyester comprises 40 to 60 mole percent of moiety I, 2 to 30 mole percent of moiety II, and 19 to 29 mole percent each of moieties III and VII. In one of the preferred embodiments, the polyester comprises 60 to 70 mole percent of moiety I, 3 to 5 mole percent of moiety II, and 12.5 to 18.5 mole percent each of moieties III and VII. The preferred polyesteramides of the process of the present invention are summarized below: a) The wholly aromatic polyesteramide capable of forming an anisotropic melt phase at a temperature below 360°C consisting essentially of the recurring moieties II, I, and VI wherein: II is III is and VI is The wholly aromatic polyesteramide as described above is disclosed in U. S. Patent No. 4,330,457. The polyesteramide comprises 25 to 75 mole percent of moiety II, 37.5 to 12.5 mole percent each of moieties I and VI. The polyesteramide preferably comprises 40 to 70 mole percent of moiety II, and 15 to 30 mole percent each of moieties I and VI. In one of the preferred embodiments of this invention, the polyesteramide comprises 60 to 65 mole percent of moiety II, and 17.5 to 20 mole percent each of moieties I, and VI. b) The wholly aromatic polyesteramide capable of forming an anisotropic melt phase at a temperature below 380 °C consisting essentially of the recurring moieties I, II, III, VII and VI wherein: I is II is III is VII is and VI is The wholly aromatic polyesteramide as described above is disclosed in U. S. Patent No. 5,204,443. The polyesteramide comprises 40 to 70 mole percent of moiety I, 1 to 20 mole percent of moiety II, 14.5 to 30 mole percent of moiety III, 7 to 27.5 mole percent of moiety VII, and 2.5 to 7.5 mole percent of moiety VI. c) The wholly aromatic polyesteramide capable of forming an anisotropic melt phase at a temperature below 350 °C consisting essentially of the recurring moieties I, II, III, IV, V, and VI wherein: I is II is III is IV is V is and VI is The polyesteramide as described above, comprises 40 to 70 mole percent of moiety I, 10 to 20 mole percent of moiety II, 2.5 to 20 mole percent of moiety III, 0 to 3 mole percent of moiety IV, 12.5 to 27.5 mole percent of moiety V and 2.5 to 7.5 mole percent of moiety VI. According to the process of the present invention, a fluid stream of liquid crystal polymer is provided to any conventional extrusion apparatus provided that it contains an extrusion orifice having a multilobal cross-section. This is achieved by heating the thermotropic liquid crystalline polymer of the present invention to form a melt. Any of the known methods to heat the polymer to form a melt can be employed in this invention. The particular apparatus used is not critical to the operation of the process of the present invention, and any suitable apparatus may be used herein. One such apparatus which has been found to be suitable for use with thermotropic liquid crystal polymers employs a contact melting method so that melt residence time can be kept short and constant. The apparatus includes a heated surface against which a molded rod of liquid crystal polymer is pressed. The fluid stream of molten polymer is then introduced to the extrusion chamber inside of which are disposed a filter pack and an orifice having a multilobal cross-section. After being passed through the filter pack, the polymer melt is extruded through the orifice so as to form a multilobal filament. Thus, a plurality of such orifices may be disposed in an extrusion chamber if one desires to form a multilobal multifilaments. In a preferred embodiment, the extrusion chamber is comprised of a singe orifice multilobal chamber in which the polymer is heated to a temperature in the range of 20°C to 50°C above its melting transition. After the fluid stream of the liquid crystal polymer is extruded through the orifice, the polymer forms an elongated shaped article having the polymer molecules oriented substantially parallel to the flow direction. The orientation of the polymer molecules can be confirmed by determining orientation angle by X-ray analysis. The extruded shaped articles in the form of filaments are then drawn down and taken-up on a filament spool. In accordance with the process of this invention, it is critical that the appropriate draw-down ratio be used to exploit maximum benefit from the practice of this invention. Thus, in a preferred embodiment, the draw-down ratio in the range of from 4 to 20 is employed. In a more preferred embodiment, the draw-down ratio in the range of from 4 to 15 is employed. The draw-down ratio (DD) as used herein is defined as the ratio of cross-sectional area of the orifice (A 1 ) to the cross-sectional area of the filament (A 2 ). This ratio is often also expressed as the ratio of the take-up speed of the filament (V 2 ) to the extrusion speed of the filament (V 1 ). Thus, the draw-down ratio, DD, may be expressed in terms of the following equation: DD = A 1 /A 2 = V 2 /V 1 Thus, in accordance with the process of the present invention, thermotropic liquid crystalline polymeric multilobal filaments having essentially uniform molecular orientation that exhibit unusually superior mechanical properties can be made. For example, by properly practicing the process of the present invention, it is now possible to obtain a high denier multilobal filament having hitherto unattainable properties. More specifically, it has now been found that multilobal filaments having a denier in the range of from 100 to 1000 denier per filament (dpf) can readily be made by following the process of this invention. In a preferred embodiment, multilobal filaments having a denier in the range of from 150 to 500 dpf can readily be made. In another preferred embodiment, filaments having a denier in the range of from 180 to 300 dpf can readily be made. The denier as used herein is defined as a weight in grams of 9,000 meters of filament. The dpf as used herein is the denier of an individual continuous filament. The conditions of temperature and pressure under which the liquid crystal polymer can be extruded are not critical to the process of the present invention and can easily be determined by one of ordinary skill in the art. Typically, thermotropic polymers are extruded at a temperature of 280 °C to 400 °C and at a pressure of 100 p.s.i. to 5,000 p.s.i. As discussed hereinabove, liquid crystal polymers have very stiff, rod-like molecules. In the quiescent state, the polymer molecules line up in local regions, thereby forming ordered arrays or domains. The existence of domain texture within the microstructure of a liquid crystal polymer may be confirmed by conventional polarized light techniques whereby a polarizing microscope utilizing crossed-polarizers is employed. The mechanical properties of multilobal filaments produced in accordance with the process of the present invention can be improved still further by subjecting the articles to a heat treatment following extrusion. The articles may be thermally treated in an inert atmosphere (e.g., nitrogen, argon, helium). For instance, the article may be brought to a temperature 10 °C to 30 °C below the melting temperature of the liquid crystal polymer, at which temperature the filament remains as a solid object. The heat treatment times commonly range from a few minutes to a number of days, e.g., from 0.5 to 200 hours, or more. Preferably, the heat treatment is conducted for a time of 1 to 48 hours (e.g., 24 to 30 hours). The heat treatment improves the properties of the filament by increasing the molecular weight of the liquid crystalline polymer and increasing the degree of crystallinity. Thus, in accordance with one of the preferred embodiments of the present invention, there is also provided a process for forming a heat-treated multilobal filament of a thermotropic liquid crystalline polymer having the following properties: (i) denier of at least 50 denier per filament; (ii) tenacity of at least 20 grams per denier; (iii) modulus of at least 600 grams per denier; and (iv) elongation of at least 3 percent. The process for forming such a multilobal filament is comprised of the following steps: (a) heating a thermotropic liquid crystalline polymer to a temperature of 15 °C to 50 °C above its melting transition to form a fluid stream of said polymer; (b) extruding said stream of polymer through a heated cylindrical spinneret having at least one extrusion capillary having a multilobal cross-section to form a multilobal filament; (c) winding said filament at a take-up speed of at least 200 meters per minute and draw-down ratio of from 5 to 40 so as to form a multilobal filament of essentially uniform molecular orientation across its cross-section and having a denier in the range of from 50 to 1000 denier per filament; and (d) heat-treating said filament at suitable temperature and pressure conditions for a sufficient period of time, optionally in the presence of an inert atmosphere, to form the heat-treated filament. Any of the preferred thermotropic polyesters or polyesteramides described hereinabove may be used in this preferred embodiment. Furthermore, as described herein, the heat treatment can be carried out in stages at a final temperature of 15°C below the melting transition of the thermotropic polymer. In another preferred embodiment of this invention there is also provided an as-spun multilobal filament of a thermotropic liquid crystalline polymer having the following properties: (a) denier of at least 50 denier per filament; (b) tenacity of at least 8 grams per denier; (c) modulus of at least 450 grams per denier; and (d) elongation of at least 2 percent. In a particularly preferred embodiment of this invention the denier of as-spun multilobal filament is in the range of from 100 to 1000 dpf. In a more particularly preferred embodiment of this invention the denier of as-spun multilobal filament is in the range of from 150 to 500 dpf. In a most particularly preferred embodiment of this invention the denier of as-spun multilobal filament is in the range of from 180 to 300 dpf. In yet another preferred embodiment of this invention there is also provided a heat-treated multilobal filament of a thermotropic liquid crystalline polymer having the following properties: (a) denier of at least 50 denier per filament; (b) tenacity of at least 20 grams per denier; (c) modulus of at least 600 grams per denier; and (d) elongation of at least 3 percent. This invention is further illustrated by the following examples, which are provided for illustration purposes and in no way limit the scope of the present invention. Examples (General) In the Examples that follow, the following abbreviations are used: HBA = 4-Hydroxybenzoic acid HNA = 2,6-Hydroxynaphthoic acid TA = Terephthalic acid IA = Isophthalic acid NDA = 2,6-Naphthalene dicarboxylic acid BP = 4,4'-Biphenol HQ = Hydroquinone AA = 1-Acetoxy-4-acetamidobenzene IV = Inherent viscosity dL/g = deciliters per gram; an unit of measure of IV wt.% = generally used to represent the concentration of a solution to measure IV - means grams of polymer in 100 mL of a solvent mixture. wt% = weight percent MV = Melt viscosity DSC = Differential Scanning Calorimetry T = Tenacity M = Modulus E = Elongation gpd = grams per denier General Analytical Techniques used for the Characterization of the Polymer A variety of analytical techniques were used to characterize polymer(s) and the filaments formed according to the present invention, which included the following: IV : The solution viscosity of the polymer samples, IV, was measured at 25 °C in a concentration of 0.1 wt.% solution in equal parts by volume of pentafluorophenol and hexafluoroisopropanol. MV : MV of polymer samples was measured using a Kayeness Melt Rheometer Model 2052 equipped with a Hastalloy barrel and plunger tip. The radius of the die orifice was 0.015 inch and the length was 1 inch. For the purpose of determining melt viscosity, a plot of viscosity vs. shear rate was generated by measuring the viscosities at shear rates of 56, 166, 944, 2388, and 8333 sec -1 , and viscosities at 100 and 1000 sec -1 were interpolated. DSC : DSC of polymer samples was performed on a Perkin Elmer 7700 Thermal Analysis System. In all runs the samples, sealed in aluminum pans, were heated or cooled at a rate of 20 °C/min. under a nitrogen atmosphere. The DSC curves obtained from the second heating run were taken for the analysis. Light Microscopy : Samples were prepared for microscopic analysis by thin sectioning using a glass knife microtome. The sections were examined by polarized light microscopy to observe morphological behavior at ambient temperatures. Example 1 Example 1 demonstrates that the mechanical properties of an as-spun high denier multilobal filament of a liquid crystalline wholly aromatic polyester produced in accordance with the present invention are comparable to those of the round filament made by a conventional process. Multilobal filaments were formed from a thermotropic liquid crystalline wholly aromatic polyester comprising HBA units and HNA units. (VECTRA™ A, commercially available from HNA Holdings, Inc., Charlotte, N.C.) This polymer exhibited a melting temperature of 280 °C and an inherent viscosity of 6.30 dL/g when measured in a concentration of 0.1 percent by weight solution in equal parts by volume of pentafluorophenol and hexafluoroisopropanol at 25°C. A sample of the polymer was dried overnight at 130°C under vacuum. The polymer was melted in a 1 inch diameter extruder, and the extrudate was metered using a conventional polymer meter pump to the spinning pack where it was filtered through 50/80 shattered metal. The melt was then extruded through a single hole spinneret of octalobal cross-section. Crossflow quench was applied to the emerging octalobal filament to provide cooling and a stable spinning environment. The quench was situated 4 cm below the spinneret face, and was 120 cm long by 15 cm wide. The quench flow rate at the top was 30 mpm (0.5 mpsec). The octalobal monofilament of 220 denier was dressed either with water or with a spinning finish before passing around a system of godets which controlled the take-up speed. It was finally taken up on a Sahm spool winder. Mechanical properties of the monofilaments produced in accordance with this Example 1 were measured in accordance with ASTM D3822, and the results are listed in Table I. For purposes of comparison, round monofilaments were also extruded in the manner described above using a cylindrical spinneret. The mechanical properties of both round and octalobal filaments are listed in Table I. Sample No. Draw-Down Tenacity (gpd) Modulus (gpd) Elongation (%) Octalobal 1 6.2 10 577 2 Round 2 6.2 9 615 1.8 Example 2 Octalobal monofilaments of 220 denier produced in accordance with Example 1 were subjected to a heat treatment in stages as follows. Heat treatment of short lengths of the monofilament was carried out on racks under zero tension in a flow of dry nitrogen using a programmed temperature profile. The programmed temperature profiles of each of the heat treatment of octalobal monofilaments are listed in Table II. The heat-treated octalobal monofilament was tested at 10 inch gauge length; 20% strain rate and 10 filament break. Following heat treatment, the mechanical properties of the octalobal monofilaments were measured and are listed in Table II. For comparison mechanical properties of round filaments produced under similar conditions are also listed in Table II. The measurements were made using the same tests as in Example 1. The data demonstrate the increase in properties, which is obtained by subjecting the octalobal monofilaments to staged heat treatment conditions. Sample Number Preheat Condition Heat Treatment Condition Draw-Down Den. (g) Ten. (gpd) Mod. (gpd) Elong. (%) Octalobal 1 230°C/2 hr 8 hr, hold @ 270°C 6.2 220 25.7 654 3.3 Round 2 230°C/2 hr 8 hr, hold @ 270°C 6.2 220 23.7 623 3.3 The results presented in Table II clearly demonstrates that octalobal filaments of comparable properties to those of round filaments can be readily made following the process conditions of the present invention. Example 3 Examples 1 and 2 were repeated in this example except that the high denier filaments of Vectra A polymer were formed. Table III summarizes the as-spun and heat treated properties of the Octalobal filaments. Heat Treated Properties for High Denier Octalobal Vectra A Monofils Sample Number Heat Treatment Condition Jet Size (Draw-Down) Den. (g) Ten. (gpd) Mod. (gpd) Elong . (%) 38538-26-10 As-Spun (Control) 0.015" 221 10.0 597 2.00 38543-34-1 230°C/2 hr; 270°C/8 hr (6.2) 222 21.9 599 3.20 38592-16-11 As-Spun (Control) 0.015" 328 9.4 537 2.10 38543-34-2 230°C/2 hr; 270°C/8 hr (6.2) 327 20.6 564 3.19 38592-26-12 As-Spun (Control) 0.015" 432 9.8 559 2.20 38543-34-3 230°C/2 hr; 270°C/8 hr (6.2) 430 19.9 596 3.17 38592-26-13 As-Spun (Control) 0.015" 539 8.3 430 2.20 38543-34-4 230°C/2 hr; 270°C/8 hr (6.2) 532 18.4 536 3.22 Example 4 Example 4 demonstrates that octalobal filaments produced in accordance with Example 1 generally exhibit superior finish uptake when compared with the round filaments produced by the conventional methods. Octalobal filaments of about 200 dpf were produced in accordance with Example 1 and were dressed with various levels of finish. In all cases the finish was applied during spinning as described in Example 1. The finish was applied in isopropanol (IPA) solvent. After the filaments were dried, the amount of finish uptake onto the filaments was measured by an extraction method. The extraction results are listed in Table IV. Finish uptake for 200 dpf as-spun LCP monofilaments Monofilament Cross-Section FOF (Target 0.5%) FOF (Target 1.0%) FOF (Target 1.5%) Round 0.2 0.5 0.6 Octalobal 0.5 0.8 1.2 Target FOF = Amount of finish applied during spinning using a solution comprising about 10 wt% finish and about 90 wt% IPA. The results presented in Table IV clearly demonstrates that octalobal filaments produced in accordance with the process of the present invention feature remarkably superior retention of the finish than the round filaments produced by conventional methods. Example 5 Example 5 demonstrates that the octalobal filaments produced in accordance with the process of the present invention exhibit superior adhesion properties related to the round filaments produced by conventional methods. Octalobal filaments of about 200 dpf produced in accordance with Example 4, and were further treated with two epoxy based predip compositions and two Resorcinol Formaldehyde Latex (RFL) adhesive recipes by methods known to those skilled in the art. The composition of Predip A was 4.0 % by weight epoxy. Predip B was composed of 1.6% by weight epoxy and 4.1% by weight Block Isocyanurate. The RFL compositions were as following: For RFL-1, the Formaldehyde to Resorcinol molar ratio (F/R) was 1.7 and the Resin to Latex weight ratio (R/L) was 0.22. For RFL-2, the Formaldehyde to Resorcinol molar ratio (F/R) was 2.0 and the Resin to Latex weight ratio (R/L) was 0.17. RFL-2 also contained 10% by weight Block Isocyanurate in its composition. The adhesion of RFL treated filaments to rubber was measured by a H-Test (Peak). The results are listed in Table V. For RFL-1, the Formaldehyde to Redsorcinol molar ratio (F/R) was 1.7 and the Resin to Latex weight ratio (R/L) was 0.22. For RFL-2 the Formaldehyde to Resorcinol molar ratio (F/R) was 2.0 and the Resin to Latex weight ratio was 0.17. RFL-2 also contained about 10% by weight Block Isocyanurate. The adhesion of RFL treated filaments to rubber was measured by an H-test (Peak). The results are given in Table V. Rubber adhesion data for 200 dpf LCP monofilaments Sample Predip Composition RFL FOF (%) H-Peak Values (lbs.) (Std.) Octalobal A R1 0.5 15.54 1.18 A R2 0.5 15.62 1.60 B R1 0.5 12.58 1.25 B R2 0.5 13.21 1.04 Round A R1 0.5 9.96 1.91 A R2 0.5 10.32 0.86 B R1 0.5 9.83 1.15 B R2 0.5 9.35 0.57 Octalobal A R2 1.5 15.96 1.03 Round A R2 1.5 14.58 3.40 RFL = Resorcinol Formaldehyde Latex R1: F/R = 1.7 mole ratio; R/L = 0.22 weight ratio (Where F= Formaldehyde and R = Resorcinol) R2: R/L = 2.0 mole ratio; R/L = 0.17 weight ratio; Block Isocyanurate = 10 wt%. (Where R= Resin and L = Latex) The data presented in Table V clearly demonstrate that octalobal filaments feature much superior adhesion properties than compared with round filaments.

Claims: A process for forming a multilobal filament of a thermotropic liquid crystalline polymer, said polymer being selected from the group consisting of wholly aromatic polyesters, aromatic-aliphatic polyesters, aromatic polyazomethines, aromatic polyester amides, and aromatic polyester carbonates, and having the following properties: (i) denier of at least 50 denier per filament; (ii) tenacity of at least 8 grams per denier; (iii) modulus of at least 450 grams per denier; and (iv) elongation of at least 2 percent; said process comprising the steps of: (a) heating a thermotropic liquid crystalline polymer to a temperature of at least 15 °C above its melting transition to form a fluid stream of said thermotropic polymer; (b) passing said stream through a heated extrusion chamber, wherein said chamber is disposed with a suitable orifice having a multilobal cross-section to form the multilobal filament of said polymer; and (c) winding said filament at a take-up speed of at least 200 meters per minute and at a draw-down ratio from 4 to 40 so as to form the multilobal filament of essentially uniform molecular orientation across its cross-section and having a denier of at least 50 denier per filament. The process as set forth in claim 1, wherein said thermotropic liquid crystalline polymer is a wholly aromatic polyester. The process as set forth in claim 2, wherein said polyester comprises a melt processable wholly aromatic polyester capable of forming an anisotropic melt phase at a temperature below 350 °C consisting essentially of the recurring moieties I and II wherein: I is and II is wherein said polyester comprises 10 to 90 mole percent of moiety I, and 10 to 90 mole percent of moiety II. The process as set forth in claim 2, wherein said polyester comprises a melt processable wholly aromatic polyester capable of forming an anisotropic melt phase at a temperature below 400 °C consisting essentially of the recurring moieties I, II, III, and VII wherein: I is II is III is and VII is wherein said polyester comprises 40 to 70 mole percent of moiety I, 1 to 20 mole percent of moiety II, and 14.5 to 30 mole percent each of moieties III and VII. The process as set forth in claim 1, wherein said thermotropic liquid crystalline polymer is a wholly aromatic polyesteramide. The process as set forth in claim 5, wherein said polyesteramide comprises a melt processable wholly aromatic polyesteramide capable of forming an anisotropic melt phase at a temperature below 360 °C consisting essentially of the recurring moieties II, III, and VI wherein: II is III is and VI is wherein said polyesteramide comprises 40 to 70 mole percent of moiety II, 15 to 30 mole percent each of moieties III, and VI. The process as set forth in claim 5, wherein said polyesteramide comprises a melt processable wholly aromatic polyesteramide capable of forming an anisotropic melt phase at a temperature below 380 °C consisting essentially of the recurring moieties I, II, III, VII and VI wherein: I is II is III is VII is and VI is wherein said polyesteramide comprises 40 to 70 mole percent of moiety I, 1 to 20 mole percent of moiety II, 14.5 to 30 mole percent of moiety III, 7 to 27.5 mole percent of moiety VII, and 2.5 to 7.5 mole percent of moiety VI. The process as set forth in claim 5, wherein said polyesteramide comprises a melt processable wholly aromatic polyesteramide capable of forming an anisotropic melt phase at a temperature below 350°C consisting essentially of the recurring moieties I, II, III, IV, V, and VI wherein: I is II is III is IV is V is and VI wherein said polyesteramide comprises 40 to 70 mole percent of moiety I, 10 to 20 mole percent of moiety II, 2.5 to 20 mole percent of moiety III, 0 to 3 mole percent of moiety IV, 12.5 to 27.5 mole percent of moiety V and 2.5 to 7.5 mole percent of moiety VI. The process as set forth in claim 1, wherein said thermotropic liquid crystalline polymer is heated to a temperature of 20 °C to 50 °C above its melting transition. The process as set forth in claim 1, wherein said orifice has a multilobal cross-section of at least six. The process as set forth in claim 1, wherein said orifice has a octalobal cross-section. The process as set forth in claim 1, wherein said draw-down ratio is from 4 to 20. The process as set forth in claim 1, wherein said draw-down ratio is from 4 to 15. The process as set forth in claim 1, wherein said multilobal filaments are a multilobal monofilament. The process is set forth in claim 14, wherein denier of said filament is from 100 to 1000 denier per filament. The process as set forth in claim 14, wherein denier of said filament is from 150 to 500 denier per filament. The process as set forth in claim 14, wherein denier of said filament is from 180 to 300 denier per filament. A process for forming a heat-treated multilobal filament of a thermotropic liquid crystalline polymer, said polymer being selected from the group consisting of wholly aromatic polyesters, aromatic-aliphatic polyesters, aromatic polyazomethines, aromatic polyester amides, and aromatic polyester carbonates, and having the following properties: (i) denier of at least 50 denier per filament; (ii) tenacity of at least 20 grams per denier; (iii) modulus of at least 600 grams per denier; and (iv) elongation of at least 3 percent; said process comprising the steps of: (a) heating a thermotropic liquid crystalline polymer to a temperature of 15 °C to 50 °C above its melting transition to form a fluid stream of said polymer; (b) extruding said stream of polymer through a heated cylindrical spinneret having at least one extrusion capillary of multilobal cross-section to form a multilobal filament; (c) winding said multilobal filament at a take-up speed of at least 200 meters per minute and at a draw-down ratio of 4 to 40 so as to form a filament of essentially uniform molecular orientation across the cross-section and having a denier in the range of from 50 to 1000 denier per filament; and (d) heat-treating said multilobal filament at a temperature of 10° to 30°C below the melting point of said polymer and pressure conditions for a sufficient period of time, optionally in the presence of an inert atmosphere, to form the heat-treated filament. The process as set forth in claim 18, wherein said thermotropic liquid crystalline polymer is selected from the group consisting of: (i) a melt processable wholly aromatic polyester capable of forming an anisotropic melt phase at a temperature below 350°C consisting essentially of the recurring moieties I and II wherein: I is and II is wherein said polyester comprises 10 to 90 mole percent of moiety I, and 10 to 90 mole percent of moiety II; (ii) a melt processable wholly aromatic polyester capable of forming an anisotropic melt phase at a temperature below 400 °C consisting essentially of the recurring moieties I, II, III, and VII wherein: I is II is III is and VII is wherein said polyester comprises 40 to 70 mole percent of moiety I, 1 to 20 mole percent of moiety II, and 14.5 to 30 mole percent each of moieties III and VII; (iii) a melt processable wholly aromatic polyesteramide capable of forming an anisotropic melt phase at a temperature below 360 °C consisting essentially of the recurring moieties II, I, and VI wherein: II is I is and VI is wherein said polyesteramide comprises 40 to 70 mole percent of moiety II, 15 to 30 mole percent each of moieties I, and VI; (iv) a melt processable wholly aromatic polyesteramide capable of forming an anisotropic melt phase at a temperature below 380 °C consisting essentially of the recurring moieties I, II, III, VII and VI wherein: I is II is III is VII is and VI is wherein said polyesteramide comprises 40 to 70 mole percent of moiety I, 1 to 20 mole percent of moiety II, 14.5 to 30 mole percent of moiety III, 7 to 27.5 mole percent of moiety VII, and 2.5 to 7.5 mole percent of moiety VI; and (v) a melt processable wholly aromatic polyesteramide capable of forming an anisotropic melt phase at a temperature below 350 °C consisting essentially of the recurring moieties I, II, III, IV, V, and VI wherein: I is II is III is IV is V is and VI is wherein said polyesteramide comprises 40 to 70 mole percent of moiety I, 10 to 20 mole percent of moiety II, 2.5 to 20 mole percent of moiety III, 0 to 3 mole percent of moiety IV, 12.5 to 27.5 mole percent of moiety V and 2.5 to 7.5 mole percent of moiety VI. The process as set forth in claim 18, wherein said orifice has a octalobal cross-section. The process as set forth in claim 18, wherein said heat treatment in step (d) is carried out in stages at a final temperature of 15 °C below the melting transition of said thermotropic liquid crystalline polymer. The process as set forth in claim 18, wherein denier of said filament is from 150 to 500 denier per filament. The process as set forth in claim 18, wherein denier of said filament is from 180 to 300 denier per filament. An as-spun multilobal filament of a thermotropic liquid crystalline polymer, said polymer being selected from the group consisting of wholly aromatic polyesters, aromatic-aliphatic polyesters, aromatic polyazomethines, aromatic polyester amides, and aromatic polyester carbonates, and having the following properties: (a) denier of at least 50 denier per filament; (b) tenacity of at least 8 grams per denier; (c) modulus of at least 450 grams per denier; and (d) elongation of at least 2 percent. The filament as set forth in claim 24, wherein said thermotropic liquid crystalline polymer is selected from the group consisting of: (i) a melt processable wholly aromatic polyester capable of forming an anisotropic melt phase at a temperature below 350 °C consisting essentially of the recurring moieties I and II wherein: I is and II is wherein said polyester comprises 10 to 90 mole percent of moiety I, and 10 to 90 mole percent of moiety II; (ii) a melt processable wholly aromatic polyester capable of forming an anisotropic melt phase at a temperature below 400 °C consisting essentially of the recurring moieties I, II, III, and VII wherein: I is II is III is and VII is wherein said polyester comprises 40 to 70 mole percent of moiety I, 1 to about 20 mole percent of moiety II, and 14.5 to about 30 mole percent each of moieties III and VII; (iii) a melt processable wholly aromatic polyesteramide capable of forming an anisotropic melt phase at a temperature below 360 °C consisting essentially of the recurring moieties II, I, and VI wherein: II is I is and VI is wherein said polyesteramide comprises 40 to 70 mole percent of moiety II, 15 to 30 mole percent each of moieties I, and VI; (iv) a melt processable wholly aromatic polyesteramide capable of forming an anisotropic melt phase at a temperature below 380°C consisting essentially of the recurring moieties I, II, III, VII and VI wherein: I is II is III is VII is and VI is wherein said polyesteramide comprises 40 to 70 mole percent of moiety I, 1 to 20 mole percent of moiety II, 14.5 to 30 mole percent of moiety III, 7 to 27.5 mole percent of moiety VII, and 2.5 to 7.5 mole percent of moiety VI; and (v) a melt processable wholly aromatic polyesteramide capable of forming an anisotropic melt phase at a temperature below 350 °C consisting essentially of the recurring moieties I, II, III, IV, V, and VI wherein: I is II is III is IV is V is and VI is wherein said polyesteramide comprises 40 to 70 mole percent of moiety I, 10 to 20 mole percent of moiety II, 2.5 to 20 mole percent of moiety III, 0 to 3 mole percent of moiety IV, 12.5 to 27.5 mole percent of moiety V and 2.5 to 7.5 mole percent of moiety VI. The filament as set forth in claim 24, wherein denier of said filament is from 100 to 1000 denier per filament. The filament as set forth in claim 24, wherein denier of said filament is from 150 to 500 denier per filament. The filament as set forth in claim 24, wherein denier of said filament is from 180 to 300 denier per filament. A heat-treated multilobal filament of a thermotropic liquid crystalline polymer, said polymer being selected from the group consisting of wholly aromatic polyesters, aromatic-aliphatic polyesters, aromatic polyazomethines, aromatic polyester amides, and aromatic polyester carbonates, and having the following properties: (a) denier of at least 50 denier per filament; (b) tenacity of at least 20 grams per denier; (c) modulus of at least 500 grams per denier; and (d) elongation of at least 3 percent. The filament as set forth in claim 29, wherein said thermotropic liquid crystalline polymer is selected from the group consisting of: (i) a melt processable wholly aromatic polyester capable of forming an anisotropic melt phase at a temperature below 350°C consisting essentially of the recurring moieties I and II wherein: I is and II is wherein said polyester comprises 10 to 90 mole percent of moiety I, and 10 to 90 mole percent of moiety II; (ii) a melt processable wholly aromatic polyester capable of forming an anisotropic melt phase at a temperature below 400 °C consisting essentially of the recurring moieties I, II, III, and VII wherein: I is II is III is and VII is wherein said polyester comprises 40 to 70 mole percent of moiety I, 1 to 20 mole percent of moiety II, and 14.5 to 30 mole percent each of moieties III and VII; (iii) a melt processable wholly aromatic polyesteramide capable of forming an anisotropic melt phase at a temperature below 360°C consisting essentially ofthe recurring moieties II, I, and VI wherein: II is I is and VI is wherein said polyesteramide comprises 40 to 70 mole percent of moiety II, 15 to 30 mole percent each of moieties I, and VI; (iv) a melt processable wholly aromatic polyesteramide capable of forming an anisotropic melt phase at a temperature below 380°C consisting essentially of the recurring moieties I, II, III, VII and VI wherein: I is II is III is VII is and VI is wherein said polyesteramide comprises 40 to 70 mole percent of moiety I, 1 to 20 mole percent of moiety II, 14.5 to 30 mole percent of moiety III, 7 to 27.5 mole percent of moiety VII, and 2.5 to 7.5 mole percent of moiety VI; and (v) a melt processable wholly aromatic polyesteramide capable of forming an anisotropic melt phase at a temperature below 350 °C consisting essentially of the recurring moieties I, II, III, IV, V, and VI wherein: I is II is III is IV is V is and VI is wherein said polyesteramide comprises 40 to 70 mole percent of moiety I, 10 to 20 mole percent of moiety II, 2.5 to 20 mole percent of moiety III, 0 to 3 mole percent of moiety IV, 12.5 to 27.5 mole percent of moiety V and 2.5 to 7.5 mole percent of moiety VI. The filament as set forth in claim 29, wherein denier of said filament is from 100 to 1000 denier per filament. The filament as set forth in claim 29, wherein denier of said filament is from 150 to 500 denier per filament. The filament as set forth in claim 29, wherein denier of said filament is from 180 to 300 denier per filament.

Inventors: CORNETTA JOHN E, DIBIASE JOSEPH J, FLINT JOHN A, HAIDER ISHAQ M, JAFFE MICHAEL, CORNETTA, JOHN E., DIBIASE, JOSEPH J., FLINT, JOHN A., HAIDER, ISHAQ M., JAFFE, MICHAEL
Applicants: CELANESE ACETATE LLC, CELANESE ACETATE, LLC.
Application year: 1999
Main classification: D01F6
IPC codes: D01D5, D01F6