REMOVAL OF HYDROGENATION CATALYST FROM POLYMER SOLUTIONS BY TREATMENT WITH AMMONIA AND CARBON DIOXIDE

Abstract: This invention is a process comprising the steps of contacting a Group VIII metal hydrogenation catalyst residue-containing polymer solution with an aqueous solution of ammonia and carbon dioxide, separating the residue from the solution, and recovering a polymer solution preferably comprising less than 15 ppm by weight based on polymer, of the Group VIII metal. The concentration of the ammonia in the aqueous solution is from 2 to 7 % by weight, preferably 3 to 6 % by weight. The concentration of the carbon dioxide in the solution is from 1 to 7 % by weight, preferably 2 to 6 % by weight.

Description: REMOVAL OF HYDROGENATION CATALYSTFROM POLYMER SOLUTIONS BY TREATMENT WITH AMMONIA AND CARBON DIOXIDE FIELD OF THE INVENTION This invention relates to a process to prepare hydrogenated polymers. More particularly, the invention relates to the removal of residues of hydrogenation catalysts from polymer solutions. BACKGROUND OF THE INVENTION The uses of polymeric materials, including diolefin polymers, continue to grow rapidly in such diverse areas as protective paint coverings, wire insulations, structural panels for automobiles, piping and lubricating oil viscosity index improvers. In many of these applications, the stability of the polymer is of paramount importance. Hydrogenation of diolefin polymers greatly improves the stability of these polymers against oxidative, thermal, and ultraviolet degradation. Polymer hydrogenation processes have therefore been studied for many years as a method to prepare novel materials with excellent stability and other desirable properties. Early polymer hydrogenation processes utilized heterogeneous catalysts which were known to be useful for hydrogenation of low molecular weight olefins and aromatics . These catalyst systems included catalysts such as nickel on kieselguhr. A fine catalyst powder was preferred and large amounts of catalysts were required to complete the hydrogenation in a reasonable time. Such processes were only partially successful, since the reaction requires the diffusion of the polymer molecules into the pores of the catalyst, where the active nickel metal is present. This is a slow process when hydrogenating polymers. Discovery of nickel 2-ethyl-l-hexanoate/triethyl aluminum hydrogenation catalyst systems enabled rapid hydrogenation of polymers. These processes utilize the catalyst as a colloidal suspension in polymer containing solutions. This type of catalyst is referred to as a homogeneous catalyst. Such a process has been used for a number of years to prepare hydrogenated isoprene-styrene block copolymers that are used as viscosity index improvers in premium motor oils. U.S. Patent No. 3,554,991 describes an exemplary process. Besides nickel, Group VIII metals in general will function as the active metal in these systems, and in particular, iron, cobalt, and palladium are known to be acceptable. Pore diffusion is not a limitation when homogeneous catalysts are utilized. The hydrogenation process is rapid and complete in a matter of minutes. However, removal of the catalyst from the polymer product is necessary because metals, particularly nickel, which remain with the polymer catalyze degradation of the polymer product. The removal of the catalyst from the polymer solution is commonly accomplished by the addition of an acidic aqueous solution and air to oxidize the metal, e.g. to oxidize nickel to a divalent state. Nickel and aluminum salts are soluble in the aqueous phase and can then be removed from the hydrogenated polymer solution by separation of the aqueous phase. Alternative methods to remove hydrogenation catalyst residues from solutions of hydrogenated polymers include treatment with dicarboxylic acid and an oxidant, as disclosed in U.S. Patent No. 4,595,749; treatment with an amine compound wherein the amine is either a chloride salt or a diamine having an alkyl group of 1 to 12 carbon atoms as disclosed by U.S. Patent No. 4,098,991; and treatment with a non-aqueous acid followed by neutralization with an anhydrous base and filtration, as disclosed by U.S. Patent No. 4,028,485. These processes involve contacting the polymer solution with compounds which contaminate the polymer. Further process steps can be required to remove these contaminants. U.S. Patent Nos. 4,278,506 and 4,471,099 describe processes to remove such contaminants from hydrogenated polymer solutions. Some of these catalyst removal systems are undesirable because the processes require relatively expensive metallurgy due to the corrosive nature of the compounds. Many also require the consumption of a continuous stream of reactants and produce sludge containing the catalyst and residues of the treatment chemicals. The above-described processes for removing catalyst residue have the disadvantage that they leave behind acid salts and other residual catalyst components. These materials must be removed from the polymer and normally this involves multiple stage water washing. Such water washing can be quite expensive in terms of capital investment and time. Thus, there is a need for a method of removing hydrogenation catalyst which minimizes the amount of residual material left in the polymer but which also allows the extraction solution to be recycled. The present invention provides such a process. SUMMARY OF THE INVENTION This invention is a process comprising the steps of contacting a Group VIII metal hydrogenation catalyst residue-containing polymer solution with an aqueous solution of ammonia and carbon dioxide, separating the residue from the solution, and recovering a polymer solution preferably comprising less than 15 ppm by weight, based on polymer, of the Group VIII metal. The concentration of the ammonia in the aqueous solution is from 2 to 7% by weight, preferably 3 to 6% by weight. The concentration of the carbon dioxide in the solution is from 1 to 7% by weight, preferably 2 to 6% by weight. DETAILED DESCRIPTION OF THE INVENTION The polymer solutions of the present invention preferably comprise from 1 to 50 percent by weight of a polymer, and more preferably comprise from 5 to 40 percent by weight of polymer based on the total amount of solution. The polymer is a partially, selectively, or totally hydrogenated polymer. The present invention does not depend upon the type of nature of the polymer. The polymer may therefore be a thermoplastic polymer, or an elastomeric polymer and may have a molecular weight which varies between wide limits. Most typically, polymers which are benefited by hydrogenation are those comprising polymerized conjugated diolefins . These conjugated diolefin containing polymers are therefore preferred for the practice of the present invention. They may be prepared by radical, anionic or cationic polymerization and may be copolymers with other monomer units. The copolymers may be random, block, or tapered, and may have structures that are linear, branched, radial or star. In a most preferred embodiment, the polymer is an anionically polymerized conjugated diolefin polymer which was anionically polymerized in an inert solvent and then hydrogenated in the same solvent to form the hydrogenation catalyst residue containing polymer solution. The preferred polymers in this invention are block copolymers of styrene and a conjugated diene, especially butadiene or isoprene. When an anionic initiator is used, polymers will be prepared by contacting the monomers with an organoalkali metal compound in a suitable solvent at a temperature within the range from -100 °C to 300 °C, preferably at a temperature within the range from 0 °C to 100 °C. Particularly effective polymerization initiators are organolithium compounds having the general formula: RLi n wherein : R is an aliphatic, cycloaliphatic or aromatic hydrocarbon radical having from one to 20 carbon atoms; and n is an integer from 1 to . The polymer of the present invention is contacted with hydrogenation catalyst and hydrogen in a solution with an inert solvent such as cyclohexane, normal hexane, diethyl ether, toluene or benzene. The hydrogenation catalysts themselves have complex structures which are not well understood and are therefore usually described by the process used to prepare them. The hydrogenation catalyst can be prepared by combining a Group VIII metal carboxylate or alkoxide ("catalyst") with an alkyl or hydride of a metal selected from Groups I-A, II-A and III-B of Medeleev' s Periodic Table of Elements ("cocatalyst" ) . The preparation of such catalysts is taught in U.S. Patent Nos. 3,591,064 and 4,028,485, which are incorporated herein by reference. The catalyst metals which are preferred include iron, cobalt, nickel and palladium. Nickel and cobalt are particularly preferred. Aluminum is the preferred cocatalyst metal due to the excellent activity of the resulting cocatalyst. The hydrogenation catalyst is extracted from the polymer cement following hydrogenation using an aqueous solution of ammonia and carbon dioxide. The 'aqueous solution is comprised of from 2 to 7% by weight of ammonia, preferably 3 to 6% by weight, and 1 to 7% by weight of carbon dioxide, preferably 2 to 6% by weight. In a preferred embodiment, air or oxygen is added to oxidize the metal, i.e., nickel to a divalent state. The hydrogenation catalyst residue-containing polymer solution is contacted with this aqueous solution either in a continuous process or in a batch process. The contact is preferably carried out by reacting in a stirred reactor or in an in-line mixer. The extraction can be carried out at a temperature of from 20 to 100 °C and an aqueous solution to polymer cement phase ratio of from 0.1 to 1.0 for a period of time from 1 to 60 minutes. The polymer concentration of cement can range from 1 to 50% by weight. The extraction is completed by allowing the phases to separate. If the phases do not immediately separate, a phase separation agent such as isopropyl alcohol or 2-ethylhexanol is added to induce separation. The aqueous phase containing the extracted hydrogenation catalyst residue is removed by decantation, centrifugation, or other separation processes. Excess ammonia and carbon dioxide remaining in the polymer cement will be volatized during the finishing of the polymer subsequent to the extraction step. The spent extraction solution can be recycled. Devolatilization of excess ammonia and carbon dioxide from the spent extraction solution generates only water insoluble species (nickel carbonate, aluminum hydroxide and lithium carbonate, for example) which can be captured by filtration, centrifugation or other separation processes. The recovered water can be made up with recovered or fresh ammonia and carbon dioxide and reused. EXAMPLES The extractions were performed in a baffled 5-liter extraction vessel with a height to diameter ratio of 2.2:1. Mixing was provided via a shaft fitted with two 6.35 cm (2.5" ) -diameter flat-blade turbine mixers rotating at a tip speed of 427 m/min (1400 ft/min) . Each batch extraction was carried out at a constant volume of 3.5 liters. The polymer solutions consisted of a hydrogenated styrene-butadiene-styrene block copolymer with number-average molecular weight of 190,000 g/mole, of which about 30% by weight is styrene, dissolved in cyclohexane at a concentration of 14% by weight. The solutions contained varying quantities of nickel hydrogenation catalyst as indicated in Table 1. Nickel levels were determined by atomic absorption spectroscopy. Example 1 The extraction vessel was charged with 2.0 kg of polymer solution, containing 315 ppm nickel on a dry polymer basis. Next, 1.0 kg of a distilled water solution containing 5 wt% ammonia and 6 wt% carbon dioxide was charged to the vessel and the contents were heated to 50 °C. The mixture was stirred for 15 minutes, while a dilute stream of oxygen in nitrogen was bubbled through the reactor contents. The mixer was stopped and the phases were allowed to settle for 40 minutes. The organic phase was sampled, analyzed and determined to contain 25 ppm nickel on a dry polymer basis. Following centrifugation to remove any remaining aqueous phase, the polymer solution was determined to contain 6 ppm unextracted nickel on a dry polymer basis. Example 2 Example 1 was repeated except for the conditions listed in Table 1. Example 3 Example 1 was repeated except for the conditions listed in Table 1, and the polymer content was 13 wt% in cyclohexane . Example 4 Example 1 was repeated except for the conditions listed in Table 1. The two phases did not separate after mixing was stopped; 50 milliliters of isopropyl alcohol was added to the reactor contents to induce separation. Comparative Example 1 Example 1 was repeated except the aqueous solution contained no dissolved carbon dioxide. Table 1 indicates the extraction performance was inferior when compared with Examples 1 through 4. It can be seen that the Examples of the present invention, 1-4, achieve a dramatic decrease in the amount of nickel in the polymer cement. The worst of these decreased the nickel level to 10% and the best to about 2%. The Comparative Example which did not utilize carbon dioxide removed less than two thirds of the residual nickel in the polymer cement.

Claims: C L A I M S 1. A process to remove Group VIII metal hydrogenation catalyst residue from a polymer comprising: a) reacting a Group VIII metal hydrogenation catalyst residue-containing polymer solution with an aqueous solution of ammonia and carbon dioxide; and b) separating the resulting mixture into phases; and c) recovering the polymer solution. 2. The process of claim 1 wherein the concentration of the ammonia in the aqueous solution is from 2 to 7% by weight and the concentration of the carbon dioxide in the aqueous solution is from 1 to 7% by weight. 3. The process of claim 2 wherein the concentration of the ammonia is from 3 to 6% by weight and the concentration of the carbon dioxide are from 2 to 6% by weight.

Inventors: WILKEY JOHN DAVID, WILKEY, JOHN, DAVID
Applicants: SHELL INT RESEARCH, SHELL INTERNATIONALE RESEARCH MAATSCHAPPIJ B.V.
Application year: 1999
Main classification: C08F6
IPC codes: C08F6, C08F8