INHIBITING SCALE IN VINYL MONOMER POLYMERIZATION

Abstract: Disclosed is a method of inhibiting the formation of scale on reactor surfaces in contact with a polymerizing vinyl monomer comprising contacting said monomer with a terpolymer which comprises the condensation reaction product of (A) an aromatic compound that contains the group (I) or (II) where Q is OR or SR and R is hydrogen, alkyl from C1, to C15, or aryl, alkaryl, or aralkyl from C6 to C15 (B) about 0.1 to about 10 moles of a carbonyl compound per mole of said aromatic compound; and (C) about 0.1 to about 10 moles of a thiourea per mole of said aromatic compound.

Description: INHIBITING SCALE IN VINYL MONOMER POLYMERIZATION This invention relates to a method of inhibiting the formation of scale on surfaces that are in contact with polymerizing vinyl monomers When vinyl monomers are polymerized, scales of the polymer adhere to the reactor walls and to reactor components, such as stirrers The deposition of this scale reduces the yield of the polymer, reduces heat transfer efficiency during heating and cooling of the reactor, and lowers monomer efficiency and general process control Some of the scale flakes off during polymerization of the monomer and mixes with the rest of the polymer, which makes the polymer less processable and reduces its quality For example, when vinyl chloride monomer (VCM) is polymerized, scales of polyvinyl chloride (PVC) can flake off and form "fish eyes" in the PVC Cleaning the reactor to remove this scale is normally required after each batch, resulting in considerable reactor downtime as well as increased cost in producing the polymer Because VCM can become entrapped in the scale, the physical removal of the scale by an operator could result in the exposure of the operator to the harmful monomer EP 343,706 teaches that polythioureas of the general formula [NHRNHC(S)]n (where R is an arylene group substituted by a carboxylic acid group) can be used to reduce scale formation in vinyl chloride polymerization reactors JP 01 ,217,016 discloses a scale preventing compound comprising an alkali metal xanthogenate, polyethyleneimine, and a dialdehyde In JP 59,32,482, dithiocarboxylic acids or salts containing OC(=S)S or NC(=S)S groups and/or (RO)2P(S)SR derivatives are disclosed as scale preventing agents U S patent 4,431 ,783 discloses that naphthol/formaldehyde condensates formed by a base-catalyzed process are effective scale-preventing agents vinyl chloride polymerization reactors While many of these scale prevention agents are effective in preventing scale, they can alter the color of the resulting PVC, giving it a yellowish tinge Customers of high quality PVC prefer a pure white or colorless PVC and regard any color in the PVC as an indication of inferior quality According to one aspect of the present invention there is provided a method of inhibiting the formation of scale on reactor surfaces in contact with a polymerizing vinyl monomer comprising contacting said monomer with a terpolymer which comprises the condensation reaction product of (A) an aromatic compound that contains the group where Q is OR or SR and R is hydrogen alkyl from d to C 15 , or aryl, alkaryl, or aralkyl from C 6 to C 15 , (B) about 0.1 to about 10 moles of a carbonyl compound per mole of said aromatic compound; and (C) about 0.1 to about 10 moles of a thiourea per mole of said aromatic compound. Preferably a solution is prepared in a solvent of said terpolymer and said solution is applied to reactor surfaces that are exposed to said monomer. Advantageously said solvent is water containing NaOH, KOH, LiOH, or Ca(OH) 2 . Conveniently said monomer is polymerized in an aqueous suspension or an aqueous emulsion and said terpolymer is added to said aqueous suspension or said aqueous emulsion. Preferably said aromatic compound is selected from the group consisting of where Z is O or NOH, each Rj is independently selected from OH, R, S0 3 R, and CO 2 R, and each R 2 is independently selected from R-,, SH, SR, haloalkyl from C1 to C 15 , alkoxyaryl, naphthyl, and polycyclic aryl Conveniently said carbonyl compound is selected from the group consisting of compounds having the general formula where each R 2 is independently selected from Ri, SH, SR, haloalkyl from Cι to C 15 , alkoxyaryl, naphthyl, and polycyclic aryl from C 6 to C 15 , Rj is OH, R, SO3R, or CO 2 R, and n is an integer from 1 to 10 Advantageously said thiourea has the general formula where each R 2 is independently selected from Rj, SH, SR, haloalkyl from C1 to C 15 , alkoxyaryl, naphthyl, and polycyclic aryl from C 6 to C1 5 , and Rj is OH, R, S0 3 R, or C0 2 R. According to a preferred embodiment of the present invention there is provided a vinyl polymerization composition containing about 0 0001 to about 0.01 wt% of a terpolymer According to an alternative embodiment of the present invention there is provided a vinyl polymerization reactor having a coating containing a terpolymer on its inside surfaces According to a further preferred embodiment of the present invention there is provided a method of inhibiting the formation of scale on reactor surfaces in contact with polymerizing vinyl chloride monomer comprising applying to said surfaces a solution in a solvent of about 0 001 to about 20 wt% of a terpolymer which comprises the condensation reaction product of (A) an aromatic compound selected from the group consisting of compounds having the general formula (B) about 0 1 to about 5 moles per mole of said aromatic compound of a carbonyl compound selected from the group consisting of compounds having the general formula O 0 0 R 2 R 2 and i (CH 2 ) n R 2 , where n is an integer from 1 to 10; and (C) about 0.1 to about 5 moles per mole of said aromatic compound of a thiourea having the general formula where Z is 0 or NOH, each Rj is independently selected from OH, R, SO 3 R, and CO 2 R, each R 2 is independently selected from Rj, SH, SR, NH 2 , haloalkyl from C1 to C15, alkoxyaryl, naphthyl, and polycyclic aryl from C 6 to C15, and R is hydrogen, alkyl from Cj to C 15 , or aryl, alkaryl, or aralkyl from C 6 to C 15 Preferably said solvent is water According to another aspect of the present invention there is provided a method of inhibiting the formation of scale on reactor surfaces in contact with polymerizing vinyl chloride monomer comprising adding to said monomer about 0.0001 to about 0.01 wt% of a terpolymer which comprises the condensation reaction product of (A) an aromatic compound selected from the group consisting of compounds having the general formula (B) about 0.1 to about 5 moles per mole of said aromatic compound of a carbonyl compound selected from compounds having the general formula where n is an integer from 1 to 10; and (C) about 0.1 to about 5 moles per mole of said aromatic compound of a thiourea having the general formula where Z is 0 or NOH, each R is independently selected from OH, R, S0 3 R, and CO 2 R, each R 2 is independently selected from Rj, SH, SR, NH 2 ,haloalkyl from d to d 5 , alkoxyaryl, naphthyl, and polycyclic aryl from C 6 to Cj5, and R is hydrogen, alkyl from C to C 15 , or aryl, alkaryl, or aralkyl from C 6 to C 15 Preferably said solvent is an aqueous sodium hydroxide Conveniently said carbonyl compound is formaldehyde or an oligomer thereof. Preferably said thiourea is thiourea or thiosemicarbazide According to an alternative embodiment of the present invention there is provided a terpolymer comprising the reaction product of (A) an aromatic compound that contains a benzene or naphthalene ring substituted with the group OR or SR, where R is hydrogen, alkyl from Cj to Cj 5 , or aryl, alkaryl, or aralkyl from C 6 to C 1 t (B) about 0 1 to about 10 moles of a carbonyl compound per mole of said aromatic compound; and (C) about 0 1 to about 10 moles of thiosemicarbazide per mole of said aromatic compound Preferably said aromatic compound is 2'-hydroxypropiophenone and said carbonyl compound is trioxane. Advantageously said aromatic compound is 1 -naphthol and said carbonyl compound is formaldehyde. According to a further preferred embodiment of the present invention there is provided a terpolymer comprising the reaction product of (A) an aromatic compound selected from the group consisting of where R is hydrogen, alkyl from C 2 to C 15 , or aryl, alkaryl, or aralkyl from C 6 to Cj 5 , each Rj is independently selected from OH, R, S0 3 R, and C0 2 R, and each R 2 is independently selected from H, OH, alkyl from C to C 8 , aryl, alkaryl, or aralkyl from C 6 to Cj 5 , SO3R1, CO 2 Rι, SH, SR, haloalkyl from C to C1 5 , alkoxyaryl, naphthyl, and polycyclic aryl from C 6 to C 15 ; (B) about 0.1 to about 10 moles of a carbonyl compound per mole of said aromatic compound; and (C) about 0.1 to about 10 moles of thiourea per mole of said aromatic compound. According to a further preferred embodiment of the present invention there is provided a composition comprising (A) a terpolymer which comprises (1 ) the condensation reaction product of an aromatic compound that contains a benzene or naphthalene ring substituted with the group OR or SR, where R is hydrogen, alkyl from C to d 5 , or aryl, alkaryl, or aralkyl from C 6 to C 15 ; (2) about 0.1 to about 10 moles of a carbonyl compound per mole of said aromatic compound; and (3) about 0.1 to about 10 moles of a thiourea per mole of said aromatic compound; (B) about 10 to about 500 wt% of an inorganic binder; and (C) about 1 to about 100 wt% of a surface active agent. Preferably said inorganic binder is colloidal silica. A scale prevention agent for use in the polymerization of VCM and other vinyl monomers has been found that is very effective in preventing the formation of scale on reactor components that come in contact with the VCM Because there is little or no scale, there are fewer fish eyes The scale prevention agent of this invention is a terpolymer of an aromatic compound, a carbonyl compound, and a thiourea derivative It is easily prepared from commercially available, inexpensive, non-toxic materials and can be applied in an aqueous medium, thereby avoiding the use of potentially harmful and flammable organic solvents Quite unexpectedly, the scale preventing agent of this invention does not impart any color to the resulting PVC The terpolymer used in the process of this invention is the condensation reaction product of an aromatic compound, a carbonyl compound, and a thiourea The aromatic compound contains the group where Q is OR or SR and R is hydrogen, alkyl from Cj to C 15 , or aryl, alkaryl, or aralkyl from C 6 to C 1 The Q group is preferably OR and the R group is preferably hydrogen as phenols are more readily available and work well Preferred aromatic compounds include where Z is O or NOH, each Rj is independently selected from OH, R, SO 3 R, and C0 2 R, and each R 2 is independently selected from R , SH, SR, haloalkyl from C 1 to C 15 , and alkoxyaryl, naphthyl, and polycyclic aryl from C 6 to C 15 Examples of suitable aromatic compounds include salicylic acid, 1 -naphthol, thiosalicylic acid, hydroxybenzenesulfonic acid isomers, 4-hydroxybenzoιc acid, 2'-hydroxypropιophenone oxime, and 2'-hydroxypropιophenone, 2'- hydroxypropiophenone and 1-naphthol are preferred due to their low cost, low toxicity, and good performance in the terpolymer condensate Mixtures of the aromatic compounds can also be used The carbonyl compound can be an aliphatic mono or dialdehyde, an aromatic aldehyde, or an aliphatic mono or diketone Compounds, such as trioxane, that form the carbonyl compound under the reaction conditions are also contemplated Preferred carbonyl compounds have the general formula where each R 2 is independently selected from NH 2 and the heremabove definition and n is an integer from 1 to 10. Examples of suitable carbonyl compounds include acetaldehyde, glyoxal, benzaldehyde, dialkyl ketones such as acetone and methyl ethyl ketone, diaryl ketones such as benzophenone and ring-hydroxylated and sulfonated benzophenones, alkyl aryl ketones such as acetophenone, ring-hydroxylated acetophenones, and ring-sulfonated acetophenones, and formaldehyde and oligomers thereof, such as trioxane. Preferably, the carbonyl compound is formaldehyde or an oligomer thereof as those compounds have low cost, high reactivity, and are readily available. Mixtures of carbonyl compounds are also contemplated. The thiourea has the general formula where each R 2 is independently selected as heremabove defined. Examples of suitable thioureas include thiourea, thiocarbamide, monomethyl thiourea, 1 ,3-dimethyl-2-thiourea, 1 -phenyl-2-thιourea, semicarbazide, thiosemicarbazide, and thiocarbohydrazide The preferred thioureas are thiourea and thiosemicarbazide because they work the best, are inexpensive, and are readily available Mixtures of thioureas can also be used The terpolymer is made by preparing a mixture of its three components For every mole of the aromatic compound, about 0 1 to about 10 moles of the carbonyl compound and about 0 1 to about 10 moles of the thiourea can be used If less than 0 1 moles of the carbonyl compound is used, the terpolymers produced will have a lower molecular weight than desired, and if more than 10 moles of the carbonyl compound is used, the terpolymer will have low solubility If less than 0 1 moles of the thiourea is used, the terpolymer will be less effective in preventing scale formation and, if more than 10 moles of the thiourea is used, the terpolymer will be less soluble Preferably, for each mole of the aromatic compound, about 0 1 to about 5 moles of the carbonyl compound and about 0 1 to about 5 moles of the thiourea are used The condensation reaction of the terpolymer components is carried out in an acidic medium which also acts as the catalyst Mineral acids, such as hydrochloric acid and sulfuric acid, and organic acids, such as acetic acid, can be used The strength of the mineral acid can vary in the range of about 1M to about 6M Typically, about 50 to about 500 wt% of a catalyst is used, based on the total weight of the terpolymer components The condensation reaction of the terpolymer components can be performed in water or polar organic solvent such as an alcohol (e g , methanol, ethanol, propanol), a ketone (e g , acetone, methyl ethyl ketone), an ester (e g , ethyl acetate), or a dipolar aprotic solvent, such as sulfolane, tetrahydrofuran, N,N-dιmethylformamιde, N-methylpyrrolidone, cyclohexanone, dimethoxyethane, or diethyleneglycol dimethyl ether Water is the preferred solvent because it is nonflammable and is not hazardous to the operator Mixed solvent systems comprising combinations of solvents, including combinations of organic solvents with water, can also be used It is preferable to choose a solvent system such that the terpolymer product, once it is formed, is insoluble in the solution and precipitates The preparation of the terpolymer is described in the Indian Journal of Chemistry, Vol 22A, pages 1 17 to 119, (1983), herein incorporated by reference Typically, the aromatic compound the carbonyl compound, and the thiourea taken together constitute from about 5 to about 50 wt% of the reaction system weight The reaction can be effected by heating to temperatures of up to 150°C for up to 8 hours Once the terpolymer has been prepared, it can be collected and purified if desired Various other components can be mixed with the terpolymer to enhance its performance as an anti-fou ng agent For example, about 10 to about 500 wt% of an inorganic binder can be included as part of the scale prevention composition to increase the binding of the terpolymer to the reactor surfaces Examples of suitable inorganic binders include colloidal silica and alumina, titanium (IV) oxide, zirconium (IV) oxide, aluminum hydroxide, vanadium (V) oxide, and sodium silicate The preferred inorganic binder is colloidal silica because of its low cost and good performance About 1 to about 100 wt% are a surface active agent can also be included as part of the scale prevention composition to increase its adhesion to the reactor surfaces Examples of suitable surface active agents include poly(vιnyl acetate) (PVA) of varying degrees of hydrolysis, hydroxyethyl cellulose, and hydroxypropyl cellulose, phytic acid, poly(vιnyl formal), and gelatin The preferred surface active agent is PVA of varying degrees of hydrolysis because of its low cost and good performance Generally, the scale prevention composition is prepared by mixing a solution of the terpolymer, surface active agent, and the inorganic binder If the scale prevention composition is to be applied to the surfaces of the reactor, a solvent is included, forming a solution of about 0 001 to about 20 wt% solids Solutions of less solids are less effective and solutions of more solids inhibit the polymerization of the VCM Preferably, the solution contains about 0 01 to about 5 wt% solids Solvents that can be used to form the coating solution include, for example water alkaline water, and various organic solvents such as methylene chloride, tetrahydrofuran, dimethyl formamide, dimethylsulfoxide, and alcohols such as methanol and ethanol The preferred solvent is a caustic solution of, for example, about 10 wt% or less sodium hydroxide, as it has been found to work well, other inorganic bases such as KOH, LiOH, and Ca(OH) 2 are also expected to work well The terpolymer can be applied to the reactor walls and to reactor components that are in contact with the VCM by any suitable means including, for example, spraying, flooding, painting, and brushing After the application, it is not necessary to evaporate the solvent from the coating composition. Generally, the solids content of the coating on the reactor walls and components should be about 1 x 10 "5 to about 1 x 10 "3 g/square inch (about 1.6x10 "6 to about 1.6x10 "4 g/cm 2 ) as less may not be effective and more is unnecessary. The terpolymer can also be added directly to the polymerization composition. For emulsion polymerizations, the polymerization composition typically consists of water, vinyl monomer, a free radical initiator, and an emulsifier For suspension polymerizations, the polymerization composition typically consists of water, vinyl monomer, a free radical initiator, and a suspending agent Generally, about 0.0001 to about 0 01 wt% of the terpolymer is added to the polymerization composition, based on the weight of the monomer. Less terpolymer is ineffective and more terpolymer may inhibit polymerization of the monomer. The terpolymer of this invention can also be used in gas phase or bulk polymerizations of vinyl monomers. But the present invention is particularly suitable for polymerizations in an aqueous medium, such as suspension or emulsion polymerization The terpolymer can be used in both continuous and batch polymerizations. The following examples further illustrates this invention Examples 1 to 21 - Preparation of Resins Into a 100 mL flask was placed the aromatic compound and the thiourea followed by the carbonyl compound Unless otherwise stated, all reactions were carried out using 1 2 mL of 2M HCI/mmol of the carbonyl compound as the catalyst/solvent The heterogeneous mixture was heated to reflux. After refluxing for a total of 5 hours, the reaction mixture was filtered and the solids were washed thoroughly with hot water The wet filter cake was dissolved in 5 wt% aqueous sodium carbonate solution and acidified with 50% (v/v) HCI until the pH of the solution was about 1. A copious amount of solid resulted which was filtered, washed with water, and air dried. This procedure was used to prepare various terpolymer resins as described in Table 1. Table 1 a Refluxed for 2 5 hours b Used 1 2 mL of 2M sulfuric acid/mmol of carbonyl compound as the catalyst/solvent c mole ratio of 1 -naphthol/formaldehyde/thιourea was 1 10 1 Reaction mixture was heated at 85-90°C for 0 5 hours and no mineral acid catalyst/solvent was used Example 22 (Comparative) ' A commercial sample of "EVICAS-90" coating solution supplied by European Vinyls Corporation was used as such in vinyl chloride polymerization Example 23 (Comparative) A 1 -naphthol/formaldehyde condensate was prepared as described in Example 1 of U S Patent 4,431 ,783 The product was a deep blue aqueous sodium hydroxide solution of the condensate Polymerization of Vinyl Monomers The following methods were used to carry out vinyl chloride polymerization in the suspension mode in the presence of the various scale prevention agents of this invention By a proper choice of emulsifying agent and reaction apparatus, one can also carry out vinyl chloride polymerization in the emulsion mode Example 24 Suspension Polymerization of Vinyl Chloride, General Procedure A rectangular SS-304 mill finish coupon, 12 5 inches (32 cm) long, 3 inches (8 cm) wide, and 0 015 inches (0 4 mm) thick (available from Metal Samples Inc , Munford, Alabama) was rolled into a cylinder of about 3 inches (7 6 cm) long and about 3 6 inches (9 cm) in diameter, such that it would fit snugly along the walls of a 1 -liter Monel autoclave A coating candidate was dissolved in 3 wt% aqueous NaOH solutions to prepare 2 wt% solutions of the scale prevention agents These solutions were applied manually on both sides of the coupon with a brush and were allowed to dry overnight under ambient air Into a 1 -liter Monel autoclave was placed the SS-304 coupon coated with the scale prevention agent The autoclave was sealed and subjected to three cycles of evacuation followed by nitrogen purge After evacuating the autoclave again, a water solution of 0 66 g of hydroxypropyl cellulose, sold by Dow Chemical Co as "Methocell E50" in 450 mL of deaerated deminerahzed water was sucked into the autoclave The pressure inside the autoclave was brought to atmospheric by admitting nitrogen Meanwhile, about 225 g (about 0 5 mole) of vinyl chloride was condensed from a VCM lecture bottle into a dry ice-cooled overhead VCM charging bomb The VCM was charged into the autoclave under an overhead nitrogen pressure of 80 psi (553 kPa) Excess nitrogen pressure was carefully vented until the final equilibrium pressure of about 35 psi (241 kPa) at a temperature of about 16 to 18°C was attained The initiator, 0 7 mL of 75 wt% tert-butylperoxyneodecanoate in odorless mineral spirits, sold as "Luperox 10M-75" by Elf Atochem N A , was injected via a septum and the mixture was agitated at about 500 rpm The reaction mixture was heated at a uniform rate over about 45 mm until the internal reactor temperature reached 62°C After stirring for 5 hours, the heat was turned off, the excess vinyl chloride was vented off, and the PVC water slurry was filtered The PVC obtained was air dried at room temperature to a constant weight It was tested for lightness and yellowness (ASTM E1164 - standard practice for obtaining spectrophotometric data for object color evaluation) Table 2 gives the scale prevention agents tested and the results Table 2 In Table 2, 100 is a perfect lightness score and 0 is a perfect yellowness score Table 2 shows that the terpolymers of this invention (Examples 1 , 5, and 8) produced PVC comparable in yield and scale-prevention performance to the scale prevention agent of Example 23, but superior in lightness and yellowness characteristics Example 25 Suspension Polymerization of Vinyl Chloride General Procedure A 500 mL EZE SS-316 autoclave equipped with a cooling jacket and a stirrer (from Autoclave Engineers) was coated completely on its inner surfaces with the coating solution prepared above The autoclave was sealed and subjected to three cycles of evacuation followed by nitrogen purge After evacuating the autoclave again, a water solution of 0 1 g of "Methocell E50" in 190 mL of deaerated deminerahzed water was sucked into the autoclave Then 18 mL of a 1 % poly(vιnyl alcohol) (80% hydrolyzed Aldπch) in degassed, deminerahzed water was introduced via a septum into the autoclave The autoclave was then evacuated again briefly without being stirred and cooled to about 5°C Vinyl chloride gas was condensed into the autoclave with stirring until % lb (113 g) of monomer had been transferred When the internal pressure was below 20 psig, the polymerization initiator 25 (0.15 mL of 75 wt% "Luperox 10M-75" was syringed out and injected into the autoclave via a septum, and the mixture was agitated at 500 rpm The coolant fluid circulation to the reactor jacket was stopped and another circulating bath pre-heated to about 72°C was connected to the reactor jacket. The reactor temperature was set to 62°C on the control tower The internal reactor temperature reached 62°C in about 0 5 h After being stirred for 5 hours, heating was turned off, the excess vinyl chloride was vented off, and the PVC water slurry was filtered The PVC obtained was then air dried at room temperature to a constant weight It was tested for lightness and yellowness (ASTM E1164) Results obtained in evaluation of several novel coating candidates are shown in Table 3 To determine PVC resin color only one coating candidate was coated on the reactor wall The color results are shown in Table 4. In Table 4, 100 is a perfect lightness score and 0 is a perfect yellowness score. The table shows that terpolymers used in this invention produced PVC comparable in yield and scale-prevention performance to the commercial scale prevention agent (Example 41 ), but superior in lightness (L) and yellowness characteristics (lower "b" value) Example 26 Vinyl chloride polymerization was carried out using the general procedure outlined in Example 25, but no scale prevention agent was used Examples 27 to 41 Vinyl chloride polymerizations were carried out according to the general procedure outlined in Example 25 and many of the scale prevention agents described in the Examples In some experiments, two or more coatings were applied on different sections of the reactor wall Example 42 (Comparative) Vinyl chloride polymerization was carried out using the general procedure outlined in Example 25 and the scale prevention agent described in Example 22 Tables 3 and 4 give the results of the vinyl chloride polymerizations of Examples 26 to 42 All reactor coatings were formulated in an 80/20 misture of 2 wt% aqueous NaOH/ethanol unless otherwise indicated Table 3 a Formulated in 2 wt% aqueous NaOH b Coating solution contained an equal weight of "Bio-Soft D40" anionic surfactant (Stepan) 0 Coating solution contained an equal weight of "Emkal BNS" anionic surfactant (Emkay) Coating solution contained equal weights of "Bio-Soft D40" anionic surfactant and "Ludox SM-30" coloidal silica Coating solution contained an equal weight of "Ludox SM-30" coloidal silica f Coating solution contained an equal weight of "Igepal CO-880" nonionic surfactant (Rhone Poulenc) 9 Coating solution contained an equal weight of "Surfonic JL-80X" nonionic surfactant (Huntsman) Table 4 a Coating solution contained an equal weight of cetyltrimethylammonium chloride cationic surfactant (Sachem). b Supplied by European Vinyls Corporation. Tables 3 and 4 show that the terpolymers of this invention are as effective as commercial products in preventing scale and in yield, but produce PVC that is lighter and less yellow. In the present specification the word "comprise" or "comprises" means "includes or consists of and "comprising" means "including or consisting of.

Claims: CLAIMS: A method of inhibiting the formation of scale on reactor surfaces in contact with a polymerizing vinyl monomer comprising contacting said monomer with a terpolymer which comprises the condensation reaction product of (A) an aromatic compound that contains the group where Q is OR or SR and R is hydrogen, alkyl from Cj to C15, or aryl, alkaryl, or aralkyl from C 6 to C 15 ; (B) about 0.1 to about 10 moles of a carbonyl compound per mole of said aromatic compound; and (C) about 0.1 to about 10 moles of a thiourea per mole of said aromatic compound. A method according to Claim 1 wherein a solution is prepared in a solvent of said terpolymer and said solution is applied to reactor surfaces that are exposed to said monomer. A method according to Claim 2 wherein said solvent is water containing NaOH, KOH, LiOH, or Ca(OH) 2 . A method according to Claim 1 or Claim 2 wherein said monomer is polymerized in an aqueous suspension or an aqueous emulsion and said terpolymer is added to said aqueous suspension or said aqueous emulsion . A method according to any one of the preceding Claims wherein said aromatic compound is selected from the group consisting of where Z is 0 or NOH, each Rj is independently selected from OH, R, SO 3 R, and CO 2 R, and each R 2 is independently selected from Rj, SH, SR, haloalkyl from d to Cι 5 , alkoxyaryl, naphthyl, and polycyclic aryl 6. A method according to any one of the preceding Claims wherein said carbonyl compound is selected from the group consisting of compounds having the general formula R 2 , where each R 2 is independently selected from R 1 ( SH, SR, haloalkyl from Cj to C 15 , alkoxyaryl, naphthyl, and polycyclic aryl from C 6 to C 15 , Rj is OH, R, S0 3 R, or C0 2 R, and n is an integer from 1 to 10 7. A method according to any one of the preceding Claims wherein said thiourea has the general formula where each R 2 is independently selected from R SH, SR, NH 2 , haloalkyl from C to C 15 , alkoxyaryl, naphthyl, and polycyclic aryl from C 6 to Cj 5 , and R, is OH, R, S0 3 R, or CO 2 R 8. A vinyl polymerization composition containing about 0 0001 to about 0.01 wt% of a terpolymer according to any one of the preceding Claims. 9. A vinyl polymerization reactor having a coating containing a terpolymer according to any one of Claims 1 to 8 on its inside surfaces 10 A method of inhibiting the formation of scale on reactor surfaces in contact with polymerizing vinyl chloride monomer comprising applying to said surfaces a solution in a solvent of about 0 001 to about 20 wt% of a terpolymer which comprises the condensation reaction product of (A) an aromatic compound selected from the group consisting of compounds having the general formula (B) about 0.1 to about 5 moles per mole of said aromatic compound of a carbonyl compound selected from the group consisting of compounds having the general formula where n is an integer from 1 to 10; and (C) about 0.1 to about 5 moles per mole of said aromatic compound of a thiourea having the general formula where Z is 0 or NOH, each Rj is independently selected from OH, R, SO 3 R, and CO 2 R, each R 2 is independently selected from Rj, SH, SR, NH 2, haloalkyl from d to C 15 , alkoxyaryl, naphthyl, and polycyclic aryl from C 6 to Cj 5 , and R is hydrogen, alkyl from C1 to C 15 , or aryl, alkaryl, or aralkyl from C 6 to C 15 . 11. A method according to Claim 10 wherein said solvent is water. 12. A method of inhibiting the formation of scale on reactor surfaces in contact with polymerizing vinyl chloride monomer comprising adding to said monomer about 0.0001 to about 0.01 wt% of a terpolymer which comprises the condensation reaction product of (A) an aromatic compound selected from the group consisting of compounds having the general formula (B) about 0 1 to about 5 moles per mole of said aromatic compound of a carbonyl compound selected from compounds having the general formula O 0 0 R ^ 2 R 2 a an ndd R 2 ^ (CH 2 ) n R 2 , where n is an integer from 1 to 10, and (C) about 0 1 to about 5 moles per mole of said aromatic compound of a thiourea having the general formula where Z is O or NOH, each R is independently selected from OH, R, SO 3 R, and CO 2 R, each R 2 is independently selected from R , SH, SR, NH 2 , haloalkyl from Cj to C 15 , alkoxyaryl, naphthyl, and polycyclic aryl from C 6 to C 1 5, and R is hydrogen, alkyl from d to C 15 , or aryl, alkaryl, or aralkyl from C 6 to C15 A method according to Claim 12 wherein said solvent is an aqueous sodium hydroxide A method according to any one of the preceding claims wherein said aromatic compound is 2'-hydroxypropιophenone or 1 -naphthol A method according to any one of the preceding claims wherein said carbonyl compound is formaldehyde or an oligomer thereof 16. A method according to any one of the preceding claims wherein said thiourea is thiourea or thiosemicarbazide. 17. A terpolymer comprising the reaction product of (A) an aromatic compound that contains a benzene or naphthalene ring substituted with the group OR or SR, where R is hydrogen, alkyl from d to C 15 , or aryl, alkaryl, or aralkyl from C 6 to Ci; (B) about 0.1 to about 10 moles of a carbonyl compound per mole of said aromatic compound; and (C) about 0.1 to about 10 moles of thiosemicarbazide per mole of said aromatic compound. 18. A terpolymer according to Claim 17 wherein said aromatic compound is 2'-hydroxypropiophenone and said carbonyl compound is trioxane. 19. A terpolymer according to Claim 17 wherein said aromatic compound is 1-naphthol and said carbonyl compound is formaldehyde. 20. A terpolymer comprising the reaction product of (A) an aromatic compound selected from the group consisting of where R is hydrogen, alkyl from C 2 to C 1 , or aryl, alkaryl, or aralkyl from C 6 to C 15 , each Rj is independently selected from OH, R, SO 3 R, and C0 2 R, and each R 2 is independently selected from H, OH, alkyl from d to C 8 , aryl, alkaryl, or aralkyl from C 6 to C 15 , SO3R1, CO 2 Rj, SH, SR, haloalkyl from d to C 15 , alkoxyaryl, naphthyl, and polycyclic aryl from C 6 to C 15 ; (B) about 0.1 to about 10 moles of a carbonyl compound per mole of said aromatic compound; and (C) about 0.1 to about 10 moles of thiourea per mole of said aromatic compound. 21. A composition comprising (A) a terpolymer which comprises (1 ) the condensation reaction product of an aromatic compound that contains a benzene or naphthalene ring substituted with the group OR or SR, where R is hydrogen, alkyl from C 1 to C 5 , or aryl, alkaryl, or aralkyl from C 6 to C 15 ; (2) about 0.1 to about 10 moles of a carbonyl compound per mole of said aromatic compound; and (3) about 0.1 to about 10 moles of a thiourea per mole of said aromatic compound; (B) about 10 to about 500 wt% of an inorganic binder; and (C) about 1 to about 100 wt% of a surface active agent. 22. A composition according to Claim 21 wherein said inorganic binder is colloidal silica. AMENDED CLAIMS [received by the International Bureau on 24 January 2000 (24.01.00); original claims 1, 2, 9, 10, 12, 17, 18 and 20 amended; claim 18 renumbered as claim 19; other claims unchanged (9 pages)] A method of inhibiting the formation of scale on a reactor surface in contact with a polymerizing vinyl monomer comprising contacting said monomer with a terpolymer which comprises the condensation reaction product of (A) an aromatic compound that contains the group where Q is OR or SR and R is hydrogen, alkyl from d to C 15 , or aryl, alkaryl, or aralkyl from C 6 to C 15 , (B) about 0 1 to about 10 moles of a carbonyl compound per mole of said aromatic compound, and (C) about 0 1 to about 10 moles of a thiourea per mole of said aromatic compound A method according to Claim 1 wherein a solution of said terpolymer is prepared in a solvent and said solution is applied to a reactor surface that is exposed to said monomer A method according to Claim 2 wherein said solvent is water containing NaOH, KOH LiOH or Ca(OH) 2 A method according to Claim 1 or Claim 2 wherein said monomer is polymerized in an aqueous suspension or an aqueous emulsion and said terpolymer is added to said aqueous suspension or said aqueous emulsion . A method according to any one of the preceding Claims wherein said aromatic compound is selected from the group consisting of where Z is O or NOH, each Rj is independently selected from OH, R, SO 3 R, and CO 2 R, and each R 2 is independently selected from R , SH, SR, haloalkyl from d to d 5 , alkoxyaryl, naphthyl, and polycyclic aryl 6. A method according to any one of the preceding Claims wherein said carbonyl compound is selected from the group consisting of compounds having the general formula where each R 2 is independently selected from R 1 ; SH, SR, haloalkyl from C to C 15 , alkoxyaryl, naphthyl, and polycyclic aryl from C 6 to Cι 5 , Ri is OH, R, SO 3 R, or CO 2 R, and n is an integer from 1 to 10. 7. A method according to any one of the preceding Claims wherein said thiourea has the general formula where each R 2 is independently selected from Rj, SH, SR, NH 2 , haloalkyl from d to C 15 , alkoxyaryl, naphthyl, and polycyclic aryl from C 6 to C 15 , and Rj is OH, R, S0 3 R, or CO 2 R. 8. A vinyl polymerization composition containing about 0.0001 to about 0.01 wt% of a terpolymer according to any one of the preceding Claims. 9. A vinyl polymerization reactor having a coating containing a terpolymer according to any one of Claims 1 to 8 on an inside surface. 10. A method of inhibiting the formation of scale on a reactor surface in contact with polymerizing vinyl chloride monomer comprising applying to said surface a solution in a solvent of about 0.001 to about 20 wt% of a terpolymer which comprises the condensation reaction product of (A) an aromatic compound selected from the group consisting of compounds having the general formula (B) about 0.1 to about 5 moles per mole of said aromatic compound of a carbonyl compound selected from the group consisting of compounds having the general formula where n is an integer from 1 to 10; and (C) about 0.1 to about 5 moles per mole of said aromatic compound of a thiourea having the general formula where Z is 0 or NOH, each R is independently selected from OH, R, S0 3 R, and CO 2 R, each R 2 is independently selected from Rj, SH, SR, NH 2 haloalkyl from d to C 15 , alkoxyaryl, naphthyl, and polycyclic aryl from C 6 to C15, and R is hydrogen, alkyl from d to C 15 , or aryl, alkaryl, or aralkyl from C 6 to C 15 A method according to Claim 10 wherein said solvent is water A method of inhibiting the formation of scale on a reactor surface in contact with polymerizing vinyl chloride monomer comprising adding to said monomer about 0 0001 to about 0 01 wt% of a terpolymer which comprises the condensation reaction product of (A) an aromatic compound selected from the group consisting of compounds having the general formula (B) about 0.1 to about 5 moles per mole of said aromatic compound of a carbonyl compound selected from compounds having the general formula where n is an integer from 1 to 10; and (C) about 0.1 to about 5 moles per mole of said aromatic compound of a thiourea having the general formula where Z is O or NOH, each Rj is independently selected from OH, R, S0 3 R, and CO 2 R, each R 2 is independently selected from R-,, SH, SR, NH 2 , haloalkyl from d to C15, alkoxyaryl, naphthyl, and polycyclic aryl from C- 6 to C15, and R is hydrogen, alkyl from d to C 15 , or aryl, alkaryl, or aralkyl from C 6 to C 15 . 13. A method according to Claim 12 wherein said solvent is an aqueous sodium hydroxide. 14. A method according to any one of the preceding claims wherein said aromatic compound is 2'-hydroxypropiophenone or 1 -naphthol. 15. A method according to any one of the preceding claims wherein said carbonyl compound is formaldehyde or an oligomer thereof. 16. A method according to any one of the preceding claims wherein said thiourea is thiourea or thiosemicarbazide. 17. A terpolymer comprising the reaction product of (A) an aromatic compound that contains a benzene ring substituted with the group OR, SH or SR, or a naphthalene ring substituted with the group OR, OH, SH or SR; where R is alkyl from Cj to C 5 , or aryl, alkaryl, or aralkyl from C 6 to C 15 , (B) about 0.1 to about 10 moles of a carbonyl compound per mole of said aromatic compound; and (C) about 0.1 to about 10 moles of thiosemicarbazide per mole of said aromatic compound. 18. A terpolymer according to Claim 17 wherein said aromatic compound is 1-naphthol and said carbonyl compound is formaldehyde. 19. A terpolymer comprising the reaction product of (A) 2'-hydroxypropiophenone; (B) about 0.1 to about 10 moles of trioxane per mole of said 2'- hydroxypropiophenone; and (C) about 0.1 to about 10 moles of thiosemicarbazide per mole of said 2'-hydroxypropiophenone. 20. A terpolymer comprising the reaction product of (A) an aromatic compound selected from the group consisting of where R is hydrogen, alkyl from C 2 to C 15 , or aryl, alkaryl, or aralkyl from C 6 to C 15 , each Rj is independently selected from OH, R, SO 3 R, and CO 2 R, and each R 2 is independently selected from H, OH, alkyl from d to C 8 , aryl, alkaryl, or aralkyl from C 6 to C15, SO3R1, C0 2 Rj, SH, SR, haloalkyl from d to C 15 , alkoxyaryl, naphthyl, and polycyclic aryl from C 6 to C 15 , (B) about 0 1 to about 10 moles of a carbonyl compound per mole of said aromatic compound, and (C) about 0 1 to about 10 moles of thiourea per mole of said aromatic compound A composition comprising (A) a terpolymer which comprises (1 ) the condensation reaction product of an aromatic compound that contains a benzene or naphthalene ring substituted with the group OR or SR, where R is hydrogen, alkyl from Cj to C 15 , or aryl, alkaryl, or aralkyl from C 6 to d 5 , (2) about 0.1 to about 10 moles of a carbonyl compound per mole of said aromatic compound; and (3) about 0.1 to about 10 moles of a thiourea per mole of said aromatic compound; (B) about 10 to about 500 wt% of an inorganic binder; and (C) about 1 to about 100 wt% of a surface active agent. 22. A composition according to Claim 21 wherein said inorganic binder is colloidal silica.

Inventors: HICHRI HIBIB, KRISHNAMURTI RAMESH, NAGY SANDOR M, WANG QI, HICHRI, HIBIB, KRISHNAMURTI, RAMESH, NAGY, SANDOR, M., WANG, QI
Applicants: OCCIDENTAL CHEM CO, STEPHENS DINAH, OCCIDENTAL CHEMICAL CORPORATION, STEPHENS, DINAH
Application year: 1999
Main classification: C08F2
IPC codes: C08F2, C08G14, C08K3, C08L57, C08L61