SPECTACLE FRAMES, UNALTERABLE AT DIFFERENT TEMPERATURES AND THE PROCESS FOR MAKING THEM

Abstract: Spectacle frames having one or more components such as a bridge, nose rests and ear pieces of martensitic NiTi, NiTi nobium, NiTi iron alloy made by means of plastic deformation starting from a 20 % work hardening raised by hammering up to 50 % so that the final section of the material so treated maintains, within a range of temperatures from -50 DEG C to +70 DEG C, sufficient elasticity and flexibility for adaptating the frames to the different facial forms of users.

Description: Spectacle frames, unalterable at different temperatures and the process for making them The invention concerns metal frames for spectacles. Presently used techniques for making spectacle frames of NiTi alloys with a memorized shape, give the alloy a mild work-hardening treatment to facilitate processing, followed by heat treatment to memorize the shape and then further work-hardening to confer characteristics of elasticity in the range of temperatures at which the frames will be used, from -20°C to +40°C. A high rate of work-hardening would make the material fragile and it would then be impossible to obtain the complex forms needed for the spectacle frame components. The above range of temperatures is in actual fact entirely inadequate. In very cold countries a temperature of -20°C is normal and, generally speaking, in mountainous areas temperatures lower than -20°C can be quite usual. At O°C the NiTi alloy is already less rigid and loses much consistency. At a lower temperature the spectacle frames can be bent even with very little pressure. On account of the memorized shape and extreme elasticity, difficulties are encountered in adapting the frames to the faces of different users. Purpose of this invention is to overcome the above drawbacks and provide further considerable advantages as will now be explained. Subject of the invention are spectacle frames having one or more components, such as the bridge, nose rests and ear pieces made of work hardened martenistic NiTi, NiTi niobium, NiTi iron alloys. The components are made by plastic deformation starting from a 20% work-hardening of the alloy and then by hammering to reach about 50% making the ultimate section of the material, so stretched, sufficiently elastic and flexible, at temperatures ranging from -50°C to +70°C, to make the frames adaptable to the different faces of users. The shape is given by plastic deformation; this involves using mechanical means to impress folds in the material, cooling it before the operation and keeping it at a constant temperature so that the folds become even. In one advantageous type the titanium content of the alloy is between 43 and 47% by weight. Said components are connected to the other parts of the spectacles by bushes fitted into the ends of said components. The bushes are preferably of steel. To check the effects and advantages of this process, tests were made in Italy by the National Research Council (CNR) at its Institute of Metal Technology at Lecco. During these tests great attention was paid to checking, at different temperat ures, the mechanical properties of the ear pieces of the frames. comparing those available on the Italian market, the main feature of these ear pieces being their great elasticity. Special care was taken in comparing: - an ear piece made by Optigen using the process here invented, - an ear piece on sale in the market made by the firm Heschenback. The samples had uniform cross sections of about 1 .2 mm in diameter. Diameters in actual fact were: Optigen 1.19 mm, Heschenback 1.27 mm. The surface layer was removed in a mild chemical bath. Mechanical tests were made on the material using an MTS M/2 machine comprising a personal computer for checking the instruments and for acquiring data by means of specific software. Tests were made at +50°C, +30°C, 0°C, -20°C, -40°C. Each cycle consisted, for each charge, in checking stress up to 5%, and consequent release, in checking deformation to a value of "0". This made possible an evaluation of residual stress after deformation avoiding overcompression of the ear piece. After each test the sample was removed from the press and allowed to revert to residual deformation heating it up to about 80°C. In this way the initial configuration could be fully recovered for the subsequent tests. The results can be seen in Figures 1 and 2 given below. Figure 1 shows a comparison of the stress-deformation curves at 30°C. Figure 1 TEST TEMPERATURE + 30° C LO Deformation Behaviour of both samples shows a marked overall elasticity though there is a a great difference in the stress-deformation curve, The Heschenback ear piece shows a certain recovery due to memory after deformaion. Behaviour of the Optigen sample is typically superelastic maintaining its plastic deformation. In other words there is no evidence of martensitic transformation and related pseudoelastic behaviour. Figure 2 compares the stress-deformation curves of the same samples at a temperature of -40°C Figure 2 TEST TEMPERATURE - 40° C 0° 1 ° 2° V 4° 5' 6° Deformation Behaviour of the Heschenback sample is typical of a partially annealed material with marked recovery of imposed deformation but with residual pseudoplastic deformation. This deformation may be easily recovered by simply heating the sample. After deformation the sample recovers its memorized shape. Behaviour of the Optigen sample, on the other hand, is fully superelastic without any signs of martensitic transformation and pseudoplasticity. Residual plastic deformation of this sample is slight. These initial results clearly show the entirely different behaviour of the two sample. Both exhibit overall macroscopic elasticity and, after receiving a 5% deformation, can almost completely recover their initial shape. But the reason for this is totally different for the two arms. Behaviour of the Heschenback sample is that of high elasticity combined with martensitic transformation; this takes place under stress in the shape-memorized NiTi alloys, is highly sensitive to temperature changes and ensures a low degree of tension in a wide range of deformations. The Optigen product uses a different property of the NiTi alloy, namely its superelasticity. The invention offers evident advantages. The process produces spectacle frames that, without losing their elasticity, can be safely used at a much wider range of temperatures than can be obtained with other known processes, said frames being therefore utilizable at the temperatures prevailing in particularly cold countries or at high altitudes, including contact by the wearer with snow and ice. Even at such low temperatures the frames maintain the characteristics of high flexibility and resistance for which they were chosen. This has been unquestionably proved by tests carried out in CNR laboratories, at temperatures ranging from -20°C to -40 C C; these tests prove that, even subsequent to that mechanical plastic deformation needed for making the component parts of the spectacles, the treated material always maintains its typically elastic properties. Processes already known can produce frames which, using the same range of temperatures as indicated above, from -20°C to -40°C, present plastic behaviour while maintaining their deformation. It may also be noted that spectacle frames do not need to be superelastic since they are unlikely to encounter particularly high stresses in normal conditions of use. On the other hand it must be possible to modify the ear pieces and/or the bridge to adapt them to the user's facial form. In conclusion, a comparison between the frames produced by the above process and those made by others at present in use, shows that, though less elastic, these frames are always flexible enough to withstand stresses that would be sufficient to break them had they been made using presently-known processes; in addition, their characteristics remain unaltered at the different temperatures at which they are used, while they can be adapted to fit different facial forms and, once made, this adaption becomes stabilized.

Claims: CLAIMS 1. Spectacle frames having one or more components such as bridge, nose-rests and ear pieces of work hardened martensitic NiTi, NiTi nobium, NiTi iron alloys, characterized in that said components are made by plastic deformation starting from a 20% work hardening, increased to 50% by hammering, so that the final section of the material thus treated maintains sufficient elasticity, in a temperature range from -50 C C to +70 C C, and sufficient flexibility for adapting the frames to the different facial shapes of users. 2. Spectacle frames as in claim 1 , characterized in that the content of titanium in the alloiy is comprised within 43 - 47% by weight. 3. Spectacle frames as in claim 1 , characterized in that the components and other parts of the spectacles are connected by bushes fitted into the ends of said components. 4. Spectacle frames as in claim 3, characterized in that the bushes are of steel. 5. Process for component parts of spectacle frames, such as the bndge, nose rests and ear pieces of work hardened martensitic NiTi, NiTi nobium, NiTi iron alloys, characterized in that said components are made by plastic deformation starting from a 20% work hardening of the initial alloy, raised to 50% by hammering so that the final section of the treated material maintains sufficient elasticity, within a temperature range from -50°C to +70°C, and sufficient flexibility for adapting the frame to users' different facial forms. 6. Process as in claim 5, characterized that the titanium content of the alloy is between 43 and 47% by weight. 7. Process as in claim 5, characterized in that connection among the components of the frame is made by bushes fitted into the ends of said components. 8. Process as in claim 7, characterized in that the bushes are of steel.

Inventors: ROSSIN PAOLO, ROSSIN, PAOLO
Applicants: OPTIGEN SRL, ROSSIN PAOLO, ROSSIN, PAOLO
Application year: 1999
Main classification: G02C5
IPC codes: G02C5