FLUID LIGHT GUIDE

Abstract: A light guide is disclosed and includes a flexible elongated tube (12) having an inner surface and first and second ends. An aerogel film (20) is affixed to the inner surface of the tube (12) as a cladding layer, and a fluid core (14) is disposed within the tube. The fluid core (14) has a refractive index greater than the refractive index of the aerogel cladding film (20).

Description: Background of The Invention FLUID LIGHT GUIDE 1. Field of the Invention The present invention relates generally to optical waveguides and, more particularly, to fluid light guides for the transmission of a wide range of wavelengths. Specifically, the present invention relates to liquid/gel light guides having a high critical angle of acceptance for illumination purposes and a continuous process for the manufacture thereof. 2. Description of the Prior Art Numerous kinds of waveguides or optical fiber structures have been developed for the transmission of electromagnetic radiation of various wavelengths between infrared to ultraviolet, and in particular in the visible light region. These fiber-optic devices are utilized in numerous industries, in particular the medical, communication and lighting industries, for a number of different purposes. In many instances, it is desired to transmit visible light along a substantial distance to locations which are physically remote or very difficult to reach. One popular type of light waveguide which is known in the art employs the principle of total internal reflection to transmit light along a column or core of material, usually quartz or glass. For purposes of explanation, a light guide is the optical equivalent of a water pipe. It generally consists of a low refractive index cladding, which is the equivalent of the pipe in this analogy, and a high refractive index core through which light is channeled by total internal reflection. The most widely known and used light guide is glass fiber. In this instance, the outer layer of glass is made of a lower refractive index material than the core glass. Other examples of fibers used in waveguides include fused silica, acrylics and other plastic materials, polymers and liquid or gel materials. In a typical glass or quartz light guide, the fibers along the core generally consist of a central core of glass or quartz surrounded by an optical cladding layer which has a refractive index lower than that of the core material. Light incident on the junction or interface between the core and cladding will generally be totally reflected if the angle of incidence of the light, measured from a line radially normal to the junction or core surface, is greater than a certain specified critical value. Thus, light can be transmitted along the fiber and around bends, provided that the radius of the bent waveguide is not too small so as to maintain the proper angle of incidence. U.S. Patent No. 5,684,907 discloses one particular type of glass waveguide core which is coated by an aerogel cladding layer. Fiber optic devices utilizing glass cores transmit wavelengths primarily in the visible light range. Quartz, on the other hand, transmits a wide range of wavelengths from the ultraviolet to the near infrared. Unfortunately, quartz waveguides are very fragile as well as being very expensive and difficult to produce. Although ideal for communications purposes, which require the transmission of low energy radiation over long distances, quartz fibers present great difficulties for the transmission of relatively large amounts of power over shorter distances. Moreover, a principal problem with these fibers is that they must be very thin to provide required flexibility, which is a significant disadvantage when the fibers are fragile as in quartz. In addition, the power densities created in thin fibers with laser applications can be high enough to cause breakdown of the core material. In addition, it is very difficult to successfully launch broad light beams that may be 50mm or more in diameter, or large diameter laser beams, into fibers of this type without high losses. Some optical fibers of this type have been formed from finely drawn quartz capillary tubes filled with a liquid, but the same problems of fragility, alignment, and breakdown of the material generally prevent their use in any of the aforementioned applications requiring high power levels. Bonding large numbers of single glass fibers together to form flexible fiber-optic bundles of much greater diameter than single fibers has been useful for a number of applications. However, with use the individual fibers begin to fracture, leading to increasing numbers of dead spots and decreasing efficiency of the bundle. In addition, because only the cores of individual fibers transmit light, and since these make up only a percentage of the cross-sectional area of a fiber-optic bundle, light falling on the material between the fibers is not transmitted, but is rather absorbed. This results in initial losses proportional to the non- transmitting area of the bundle, and if the energy of the incident light beam is high enough, destruction of the bundle due to energy absorption. Thus, waveguides of this type cannot usually be used in the transmission of high energy radiation. Optical fibers with plastic cores have been previously described. However, because of the nature of the materials from which they are constructed, they tend to have high light losses, can generally operate only at low temperatures and are generally suitable only for non-critical, low light applications. In addition, aerogel materials have been noted for their low refractive index as illustrated in U.S. Patent No. 5,496,527 and in the previously referenced U.S. patent. Liquid and gel-core light guides, such as disclosed in U.S. Patents No. 4,045,119 and No. 5,452,395, offer the advantage that a very large core fiber can be constructed. High light throughput is possible in such light guides without the dead space between adjacent circular fibers associated with fiber bundles. The main problem with these large diameter, liquid core fibers is the availability of low refractive index cladding and high refractive index, low loss core materials. Put another way, the problem is to find workable combinations of solid cladding and fluid core materials such that the refractive index differential provides an acceptable numerical aperture for the resultant fiber. The numerical aperture is a measure of the acceptance cone of light that can be coupled into the fiber, and the objective is to achieve as high a numerical aperture as possible. Currently, liquid light guides are typically made with a calcium chloride core and fluorinated ethylene polymer (FEP) cladding. These materials are relatively expensive and require exacting manufacturing techniques and standards. Other core materials such as one of the silicones or polymer material can be used. Similarly, lower cost claddings may be used, either as a simple tube, or as a plastic tube coated with a low refractive index layer on the inside surface of the tube. However, the materials currently available are expensive or suffer from limited light transmission or wavelength range performance. Moreover, the coating procedures during manufacturing are batch processes which are very cumbersome for making such waveguides in substantial lengths such as 50-100 feet or more. Therefore, there is still a need for a very low refractive index coating that could be applied to the inner surface of a low cost plastic tube such as polyethylene or the like to form the basis for a fluid light guide wherein water or other superior transmission core liquids or gels could be used. Moreover, the coating material must be unreactive with the fluid core and readily applied to long tubular interior surfaces in a continuous process to provide substantial economic benefits. The result would be a low cost light guide with superior wavelength and transmission performance. Summary of the Invention Accordingly, it is one object of the present invention to provide a fluid light guide with improved wavelength and transmission performance. It is another object of the present invention to provide an economically viable, large core light guide for remote, energy efficient lighting applications. Yet another object of the present invention is to provide light guides of substantial length for use in passive solar-based or core-daylighting systems for routing throughout buildings and the like. Still another object of the present invention is to provide a very low refractive index coating that can be applied in a continuous process to the inner surface of a low cost tube of substantial length to provide highly efficient and inexpensive waveguides. To achieve the foregoing and other objects and in accordance with the purpose of the present invention, as embodied and broadly described herein, a light guide is disclosed and includes a flexible elongated tube having an inner surface and first and second ends. An aerogel film is affixed to the inner surface of the tube as a cladding layer, and a fluid core is disposed within the tube. The fluid core has a refractive index greater than the refractive index of the aerogel cladding film. In one application of the light guide of the invention, the fluid of the core is selected from the group consisting of liquid and gel. In another application of the invention, the aerogel film is preferably hydrophobic. In yet another application, the aerogel film comprises silica aerogel. In still another application of the invention, the aerogel film of the light guide is covalently bonded to the tube inner surface. In still another application of the invention, aerogel film of the light guide comprises a stable porous hydrophobic coating having a porosity of approximately 50-99%, and more preferably a porosity of approximately 60-90%. In yet another application of the light guide invention, the silica aerogel has a refractive index of no greater than 1.28. In another application of the invention, a light guide is disclosed and includes a flexible elongated tube having an inner aerogel cladding lining of a low refractive index and a fluid core disposed within the tube, the core having a refractive index greater than the refractive index of the aerogel lining. The tube of the light guide may be made from a fluoropolymer, and the lining may comprise a low refractive index hydrophobic aerogel cladding. In another application of this invention, the aerogel lining of the light guide comprises a stable porous hydrophobic coating having a porosity of approximately 50- 99%, and more particularly a porosity of approximately 60-90% with a refractive index of no greater than 1.28. In still another application of the invention, the fluid of the core of the light guide is selected from the group consisting of liquid and gel. Another application of the invention includes an optical fiber which comprises an elongated tube having an inner surface, an aerogel cladding layer affixed to the tube inner surface, and a fluid core disposed within the tube. In one form of this application of the invention, the aerogel film is hydrophobic. In another form of the optical fiber of the invention, the fluid of the core is selected from the group consisting of liquid and gel. Finally, in yet another form of this application of the invention, the aerogel film in the optical fiber comprises silica aerogel. Finally, a method of forming a fluid light guide is disclosed. This method includes the steps of forming an elongated tube having an inner surface and first and second ends; filling the tube with a sol, draining the filled tube at a controlled rate to form a substantially uniform film on the interior surface of the tube, curing the film to form an aerogel cladding coating on the interior surface of the tube, plugging the first end of the tube, and filling the tube with a fluid core material having a refractive index substantially greater than the refractive index of the aerogel cladding lining. In one application of the methjod of the invention, the sol is a silica sol. In another application of the method, the sol is cured by bubbling a gas in a nitrogen carrier through the drained tube, the gas being selected from the group consisting of ammonia and HCI. In yet another application, the drained tube is exposed to microwaves to cure the sol. In still another application of the method of the invention, the fluid core material is selected from the group consisting of water, hydrocarbons, silicone fluids, mineral oils, gels and solutions of salts selected from the group consisting of sodium, calcium, potassium and mixtures thereof. Finally, in still application of the method of the invention, the sol is cured to form a hydrophobic aerogel cladding layer. Brief Description of the Drawings The accompanying drawings which are incorporated in and form a part of the specification illustrate preferred embodiments of the present invention and, together with a description, serve to explain the principles of the invention. In the drawings: Fig. 1 is a partial side perspective view of a light guide constructed in accordance with the present invention; Fig. 2 is a cross-sectional view taken substantially along line 2-2 of Fig. 1 ; Fig. 3 is a side perspective view of a light guide constructed in accordance with the present invention illustrating internal light reflection angles; Fig. 4 is a cross-sectional view taken substantially along line 4-4 of Fig. 3; and Fig. 5 is a schematic of a light guide constructed in accordance with the present invention illustrating a critical angle of acceptance. Detailed Description of the Preferred Embodiments Referring to the Figs.1-5, a waveguide 10 is formed having an outer tube portion 12 which defines an annular interior cavity 14. The cavity 14 is filled with an appropriate fluid 16 such as a liquid or gel as described in detail below. The tube 12 includes an interior surface 18 onto which is formed a layer 20. It should be understood that the fluid 16 is preferably a liquid or gel, and when the term fluid or liquid is used herein, it is to be understood that this is to include gels or any other appropriate flowable material. The layer 20 is preferably an aerogel material which is highly porous but preferably highly hydrophobic to prevent interaction with the liquid 16. For the purpose of the disclosed invention, aerogels are defined as highly porous solids containing from 40 to over 90 volume percent porosity. The term aerogel preferably includes those materials prepared by a low temperature and pressure aerogel process wherein porosity is generated by dilation or springback of a gel during drying, or a surfactant-templating approach wherein an inorganic silica network is formed around an organic liquid-crystal or micellar structure followed by removal of the organic template, creating a porous silica fossil of the organic assembly. In addition, it is to be understood that the term aerogel as used herein is also to include mesoporous thin-film materials such as disclosed in the article entitled, "Continuous formation of supported cubic and hexagonal mesoporous films by sol-gel dip-coating", Nature, Vol. 389, September 25, 1997, the contents of which are specifically incorporated herein. Before the specific details of the invention are described, it is helpful to understand the dynamics of liquid light guides. The essence of any light guide is to have two concentric media with the refractive index n of the inner core being higher than the refractive index n 2 of the outer cladding material. The interface between the two media should be as smooth as possible to offer mirror-like reflection. Prior to the invention, both media should preferably be optically transparent in the preferred wavelength region for maximum transmission. For a traditional liquid light guide, the core 16 is a liquid and the cladding is generally a plastic. However, in the present invention, the plastic tubing material 12 is not the cladding. Rather, the inner surface 18 of the tube 12 is lined with a cladding layer 20, thereby enabling the tube 12 to be manufactured from any type of available and desired material without concern with respect to its refractive index or transparency. The amount of light that can be accepted by the waveguide 10 of the invention falls within an acceptance cone 22 defined by an angle A. This angle is related to the refractive indices n and n 2 through the relation sin (A) = K n ι) 2 - i n 2) 2 ] Y the quantity sin (A) being known as the Numerical Aperture (NA). Within the light guide 10, light is transmitted through total internal reflection. However, only those light rays that equal or exceed the critical angle B, which is defined between the two media (core and cladding), will be transmitted through the light guide. The critical angle B is related to the angle A of the acceptance cone through the simple relationship of B = 90° - A. The light transport efficiency of the light guide 10 is determined primarily by the combination of two factors. The first factor is that the difference between the refractive indices r/ι and n 2 should be as large as possible so as to maximize the acceptance angle A of transmitted light which will create a lower critical angle B. As stated above, only those light arrays that equal or exceed the critical angle B will be transmitted through the light guide 10. The second factor is that the absorption characteristics of the fluid 16 should be selected to transmit the desired spectral range through the light guide 10. Other factors may also be considered and include the transmission of unwanted wavelengths ranges, and the effects of the source light upon the optical properties of the fluid 16 or tubing 12 under a long term and/or highly intense exposure. A primary advantage of liquid light guides in general and the present invention in specific is the fact that a relatively large diameter (for example 5mm) single fiber-like light guide can be produced that is both flexible and inexpensive. By contrast, fiber light guides made from solid material such as plastic, glass or silica as discussed above, are generally limited to small diameters to maintain flexibility and must be bundled in order to transmit large amounts of light. The result of this latter choice makes for a flexible but inefficient and relatively expensive light guide. The use of a single core in a fluid light guide of the present invention creates an inherently efficient light transmission system. The diameter of these flexible liquid light guides can be selected from as small as 1 mm up to about 14 mm in diameter and even greater. The Numerical Aperture is an important parameter of any optical fiber but is particularly pertinent to the present invention. As particularly illustrated in Fig.3, the acceptance angle A is illustrated at both the entrance and the exit ends of the light guide 10. This is because the light guide 10 tends to preserve the angle of incidence during propagation of the light along the length of the guide 10, causing it to exit the light guide 10 at the same angle it entered. As can be particularly seen in Fig. 5, the acceptance angle A and the Numerical Aperture thereof are compared to the incident angle C from a light source 30. As can be seen, the light guide 10 is not capable of accepting all of the light from the source 30 since some of the light rays from the light source 30 are greater than the critical angle B, i.e. those rays outside the angle C less the angle 2A. The tube 10 of the present invention may be made of any suitable material. This is due to the fact that the tube 10 does not function as a waveguide cladding, which is quite different from prior light guide designs. The nature and properties of the tube 10 are not critical, although it is quite important that the inner surface 18 of the tube 10 be very smooth since the aerogel coating 20 will conform to the shape or pattern of the surface 18. Consequently, the tube 10 may be composed of a flexible plastic or the like, for example a fluoropolymer resin. Preferably, the tube 10 possesses the characteristics of being inert, inflammable and resistant to relatively high temperatures with a smooth inner surface. Specific examples of fluoropolymer resins useful with the invention as the tube 10 include FEP, KEL-F, Teflon PFA, Tefzel and 3M THV-500. Moreover, polyethylene, PVC, polycarbonate and other plastics may also be used for some applications. Since the tube 10 does not have to be transparent, it can also be made of metal. However, a transparent tube 10 may be desirable in certain applications to facilitate side lighting emission. The fluid 16 of the core 14 may be of any suitable type known to the art. In preferred form, the liquid core 14 possesses one or more of the characteristics including being non-inflammable, chemically stable and non- reactive with other components of the waveguide. In addition, the fluid 16 is preferably resistant to absorption particularly at the wavelengths of the radiation being transmitted, is temperature stable, is relatively colorless and is not toxic. Moreover, in order to prevent the formation of voids and bubbles in the fluid 16, it is preferred that the fluid 16 is in a compressed condition within the tube 12, although this does not preclude the use of non-compressed fill liquids or those of low compressibility for the core 14. The preferred fluid 16 may include water, hydrocarbons, silicone fluids, mineral and other oils, gels and various solutions including solutions of various salts such as sodium, calcium and potassium and mixtures thereof. Moreover, synthetic performance fluids may also be utilized. However, the most preferred fluid is a water/aqueous system due to the fact that silicone oils, alcohols, and the like can wet the aerogel film under certain circumstances and possibly destroy the wave guiding behavior. Therefore, when such other fluids are used as the fluid 16, the appropriate silica derivatization chemistry is preferably implemented to prevent wetting by the wave guiding fluid. In accordance with the present invention, and a critical aspect thereof, the interior lining or cladding layer 20 which is fixed to the inner surface 18 of the tube 12 is an aerogel. Aerogels are highly porous solids, often based upon a silicon-oxygen matrix, which are arranged in a sponge-like structure in which the silica framework is interspersed with a continuous network of small pores of between 100 to 200 Angstroms in diameter. The result is a very strong and flexible structure, considering that it comprises up to 95% air or other gas. For the purposes of the present invention, a principal attraction of such a light material, apart from its structural integrity, is its low refractive index. It should be noted that there are a number of reasons which would inherently tend to make aerogels appear unsuitable for use as the cladding lining 20 in the present invention. It was discovered, however, that the opposite was the fact. First, aerogels normally require supercritical extraction using autoclaves for their formation as illustrated in the previously referenced U.S. Patent No. 5,496,527. Such a process does not lend itself to the continuous application of an aerogel film over the surface of a very long structure as required in the present invention. Moreover, aerogels are generally a silicone-based structure, although the present invention is not limited to such. While the aerogel structure can be stressed, its performance under tension is generally of concern because it is inherently very brittle. Applying such a coating to the exterior of a solid glass substrate or even a glass fiber has been done previously, as illustrated in the prior referenced U.S. patent. However, applying it to the inner surface of a flexible plastic tube in accordance with the present invention is quite another situation. Nonetheless, an aerogel deposition process was specifically designed for this application which permits the application of aerogel coatings to the interior surface of flexible plastic tubing at room temperature. Finally, aerogels are inherently hydrophilic or at least are typically structured to resist permanent hydrophobicity. The reason for this is that aerogel structures are mostly air or other gas. As discussed above, an aerogel is akin to a sponge except that the members making up the structure of the "sponge" are made of rigid silicon-based materials. Mesoporous materials are similar although the pores are very structured and orientated. Consequently, if one were simply to fill an aerogel-coated tube full of water or another liquid, it is expected that the liquid would seep into the pores of the sponge-like hydrophilic aerogel over time. However, an essential feature of the invention is that the aerogel coating 20 on the inside surface of a liquid or gel light guide tube 12 must preferably be hydrophobic in order to ensure that the film 20 is not wetted by the core material, i.e. that the liquid from the core does not penetrate the aerogel film pores even at pressure. Otherwise, an unacceptable increase in the refractive index of the cladding will occur, thereby losing the benefit of having the aerogel film in the first place since the differential in refractive indices between cladding and core will have been reduced. It was discovered that an aerogel can be designed so that it is highly hydrophobic for a water- based core 16. Moreover, if another liquid is used as the core 16, then the aerogel layer 20 can be made capable of also rejecting it from its matrix. In preferred form, the film 20 is 0.1 to 4.0 μm in thickness and is preferably silica aerogel, although the aerogel film 20 may be selected from any appropriate sol particularly including Si0 2 and AL 2 0 3 based sols. In the most preferred form, the film 20 is about 2.0 μm thick and is a silica aerogel, although approximately 1.0 - 2.0 μm thick layer is preferred for a waveguide to transmit visible light. The tubes 12 are preferably long, continuous tubes of 50 to 100 feet and longer and about 5 - 14mm in diameter. Prior to the present invention, to create an aerogel layer, the liquid had to be removed above its critical temperature and pressure in an autoclave to avoid liquid vapor surface tension and the associated drying stress that would otherwise collapse the wet gel structure. In the present invention, the films 20 are preferably prepared on the inner surfaces 18 by using a drain coating procedure wherein the tube 12 is initially filled with sol, which is a colloidal dispersion of siloxane or other desired polymer in a liquid. Appropriate sols for the present invention include particulate and polymeric sols. Sol compositions include but are not limited to aqueous or alkoxylated colloidal dispersions of ceramics such as the previously mentioned Si0 and AL 2 0 3 . Additional sol compositions may include partially or fully hydrolyzed metal alkoxides (M(OR) n ), where M is a metal and R is an organic ligand preferably an alkyl group, partially or fully hydrolyzed organically substituted metal alkoxides (R'χM(OR) n- x, where R' is a non-hydrolyzable organic ligand), and other colloidal dispersions known to the art. The fluid component of the sol includes but is not limited to water, alcohol, or other organic fluids such as hexane, cyclohexane, toluene, tetrahydrofuran, acetonitrile, methoxyethanol, or multicomponent (preferably miscible) fluid mixtures. The only practical requirements of the sol are that it remains stable during the drain coating operation, i.e. it does not precipitate, and that its viscosity and concentration be appropriate for the drain coating operation. Once the tube 12 is filled, the tube 12 is then drained at a controlled rate to deposit a uniform film on the surface 18. In preferred form, a combination of tubing material and liquid is selected so that the interior surface 18 of the tube 12 swells by the contact time prior to draining. As the film is deposited, polymer interpenetration occurs at the aerogel/polymer tube interface which promotes adhesion by the film 20. By way of example, a PVC tube 12 and a hexane-based sol resulted in aerogel films that remained adherent as the tubing 12 was severely bent, up to the point of creasing the tubing 12. To form a plastic or other tubing with the low refractive index coating of the present invention, two approaches are preferred. A first preferred method of formation is a low temperature/pressure aerogel thin film formation technique (LTPA process), while a second preferred method of formation is a surfactant-templated mesoporous film formation (ST process). The first process involves the deposition of an alkyl-silyl derivatized silica sol on the tube interior surface by dip- or drain coating. As the sol is concentrated in the tube during film deposition by filling and draining (previously described), aggregation and gelation occur. The gelled film is then dried. The shrinkage and commensurate loss of porosity during the initial stage of drying is recovered at the final stage of drying by a spontaneous dilation of the gel network better known as springback. This phenomenon results from the alkyl- silyl derivatization of the network that prevents or reduces the extent of silica condensation accompanying the initial stage of drying. In other words, the gel shrinks, but because it does not react with itself, it springs back to its original larger volume at the final stage of drying when the capillary stress vanishes during the drainage. The resulting gel networks can have porosities ranging from 50 to over 90-volume %. The as-deposited films are quite hydrophobic due to the alkyl-silyl derivitizing agents. Heat treatment under reducing conditions tends to at least partially preserve this hydrophobicity. The other preferred (ST) process utilizes the tendency of amphiphiiic surfactant molecules or block copolymers to self-assemble into micelles and liquid crystalline assemblies in aqueous media. In the presence of an inorganic precursor such as silicic acid, liquid crystal formation is accompanied by organization of the inorganic precursors around the hydrophilic surfactant head groups or polymer blocks resulting in an ordered organic-inorganic nanocomposite. Removal of the surfactant or polymer creates a porous inorganic fossil of the surfactant or polymer liquid crystalline assembly. This approach results in aerogel films 20 with porosities in the range or 40-60%. Through utilization of organoalkoxysilanes R'Si (OR) 3 where R' is a hydrophobic organic group such as phenyl or fluoroalkyl (CH 2 ) n (CF 2 )χCF 3 , these ST processed films can be made hydrophobic. In addition, non-polar solvents such as trichlorobenzene can be introduced as swelling agents to increase the porosity. For these two procedures to yield robust aerogel porous coatings 20 on polymer tube interior surfaces, it is beneficial to optimize the interfacial adhesion. In one instance, interface chemistry is designed to provide a covalently-bonded organic/inorganic interface. This approach presumably requires the use of specialty polymers modified with trialkoxysilanes or vinyl groups. An alternative approach is to swell the organic polymer tube interior surface prior to application of the porous inorganic coating thereon prepared in the same polymer swelling agent. Properly designed, this approach leads to mutually interpenetrating networks that result in an adhesive physical bond. An important issue in preparing the invention involves curing of the deposited aerogel films 20 after their application on the polymer tube support surface 18. There are several approaches available to this. In one, a microwave curing process is used. The microwaves are quite efficient in coupling to the Si-OH groups of the silica coating and driving further condensation of the silica framework, i.e. 2 Si-OH yields Si-O-Si plus water. A second approach is to catalyze this condensation reaction by exposure to ammonia or HCI vapor. The ammonia or HCi is bubbled in a nitrogen carrier gas through the waveguide tubing after the coating operation. In either instance, long segments of tubing interior can be coated with the aerogel cladding film of the invention and then cured. The processes of the invention yield stable porous hydrophobic coatings on polymer surfaces. The processing conditions (curing temperature, solvent, etc.) and interfacial adhesion strategies may be designed specifically for the polymer of choice. EXAMPLE I Utilizing the LTPA process illustrated above, examples of the refractive index and critical angles of a silica aerogel layer were measured as a function of immersion time in water. Critical angle measurements of samples immersed in water indicated that the refractive index remained below 1.28 after 6 months of immersion. Spectroscopic analysis indicated that the refractive index was approximately 1.1. These results can also be reproduced on polymer surfaces using optical configurations that enable one to determine exactly the refractive index of the immersed coating. EXAMPLE II In a test similar to the above Example I, test films were prepared using the ambient temperature/pressure aerogel process that exploits reversible drying shrinkage. A silica gel was derivatized with hexamethyldisilazane, diluted with solvent and liquefied by ultrasound. The sol was then re- concentrated and dip coated onto a silicon substrate. Films were either dried at 100°C for five hours in nitrogen (film HMDS -100) or pyrolyzed to 450°C in nitrogen (film HMDS - 450). The HMDS - 100 film was measured first in air using a spectroscopic ellipsometer. The measurement results were a thickness of 761 nm and a refractive index of 1.07. The film was then put in water in the cell with the incident angle for the ellipsometer being 75°, and a total reflection was obtained. Fitting of the ellipsometric parameters gave a refractive index of only 1.09 for the film. Since the refractive index of water is 1.33, the critical angle for total reflection is 90° - sin "1 [(1.33) 2 - (1.09) 2 2 = 40°. After remaining in the water for 24 hours, the refractive index of the film is 1.08. Moreover, the HMDS film was tested in air having a thickness of 1418.1 nm while the refractive index was 1.05. The refractive index of the aerogel layer in water after immersion is about 1.06, and after remaining in water for 114 hours, the refractive index was 1.08. EXAMPLE III The refractive index of the deposited coating 20 of the invention may be tailored to a preferred range of 1.1 to 1.2 by utilizing several parameters. These included varying the extent of derivatization of the siloxane polymers in the sol with organosilyl ligands, generally R 3 Si-, where R is methyl, ethyl, propyl, phenyl, fluoroalkyl and the like. The refractive index may also be tailored by the size and extent of condensation of the siloxane polymers and the nature of the R group. In preferred form, the optimum synthesis and processing variables achieve a refractive index of 1.12 combined with an acceptance angle of greater than 90°. EXAMPLE IV The present invention is directed to producing an interiorly coated tube to be used in the creation of a liquid or gel core light guide with low loss performance on the order of about 50% loss/100 feet initially over the whole visible region of the electromagnetic radiation spectrum, and ultimately extending into the UV and IR regions of the spectrum. The tube of the invention is mechanically robust and resistant to deformation and abuse. The film 20 performs under normal wear and tear when the waveguide is bent, twisted and subjected to constant movement. In particular, silica aerogel layered on the inside surface of a polyethylene tube yielded significant results. As can be seen from the above, the present invention provides a new fluid light guide structure which is highly efficient in transmitting electromagnetic radiation, especially in the visible light range. The invention is also efficient in having a very large angle of acceptance with nominal losses. The light guides of the invention utilizing aerogel interior coatings enables the use of low cost polyethylene or similar tubing thereby enabling the production of light guides in very large quantities and lengths at relatively inexpensive costs per foot. In addition, the extremely low refractive index achievable with aerogels provides dramatically larger fluid light guide numerical apertures. Finally, by enabling the use of relatively low refractive index core materials such as water, where n =1.33, wide wavelength performance and high transmission coupled with low loss light guides are possible. The foregoing description and the illustrative embodiments of the present invention have been described in detail in varying modifications and alternate embodiments. It should be understood, however, that the foregoing description of the present invention is exemplary only, and that the scope of the present invention is to be limited to the claims as interpreted in view of the prior art. Moreover, the invention illustratively disclosed herein suitably may be practiced in the absence of any element which is not specifically disclosed herein.

Claims: We claim: 1. A light guide comprising: a flexible elongated tube having an inner surface and first and second ends; an aerogel film affixed to the inner surface of said tube as a cladding layer; and a fluid core disposed within said tube having a refractive index greater than the refractive index of said aerogel cladding film. 2. The light guide as claimed in claim 1 , wherein the fluid of said core is selected from the group consisting of liquid and gel. 3. The light guide as claimed in claim 1 , wherein said aerogel film is hydrophobic. 4. The light guide as claimed in claim 3, wherein said aerogel film comprises silica aerogel. 5. The light guide as claimed in claim 1 , wherein said aerogel film is covalently bonded to said tube inner surface. 6. The light guide as claimed in claim 1 , wherein said aerogel film comprises a stable porous hydrophobic coating having a porosity of approximately 50-99%. 7. The light guide as claimed in claim 6, wherein said aerogel film comprises silica aerogel having a porosity of approximately 60-90%. 8. The light guide as claimed in claim 8, wherein said silica aerogel has a refractive index of no greater than 1.28. 9. A light guide comprising a flexible elongated tube having an inner aerogel cladding lining of a low refractive index and a fluid core disposed within said tube, said core having a refractive index greater than the refractive index of said aerogel lining. 10. The light guide as claimed in claim 9, wherein said tube is made from a fluoropolymer, and wherein said lining comprises a low refractive index hydrophobic aerogel cladding. 11. The light guide as claimed in claim 9, wherein said aerogel lining comprises a stable porous hydrophobic coating having a porosity of approximately 50-99%. 12. The light guide as claimed in claim 9, wherein said aerogel lining comprises silica aerogel having a porosity of approximately 60-90% and a refractive index of no greater than 1.28. 13. The light guide as claimed in claim 12, wherein the fluid of said core is selected from the group consisting of liquid and gel. 14. An optical fiber comprising: an elongated tube having an inner surface; an aerogel cladding layer affixed to said tube inner surface; and a fluid core disposed within said tube. 15. The optical fiber as claimed in claim 14, wherein said aerogel film is hydrophobic. 16. The optical fiber as claimed in claim 15, wherein the fluid of said core is selected from the group consisting of liquid and gel. 17. The optical fiber as claimed in claim 16, wherein said aerogel film comprises silica aerogel. 18. A method of forming a fluid light guide comprising the steps of: forming an elongated tube having an inner surface and first and second ends; filling said tube with a sol; draining said filled tube at a controlled rate to form a substantially uniform film on the interior surface of said tube; curing said film to form an aerogel cladding coating on the interior surface of said tube; plugging the first end of said tube; and filling said tube with a fluid core material having a refractive index substantially greater than the refractive index of said aerogel cladding lining. 19. The method of claim 18, wherein said sol is a silica sol. 20. The method of claim 18, wherein said sol is cured by bubbling a gas in a nitrogen carrier through the drained tube, said gas being selected from the group consisting of ammonia and HCI. 21. The method of claim 18, wherein said sol is cured by exposing said drained tube to microwaves. 22. The method of claim 18, wherein said fluid core material is selected from the group consisting of water, hydrocarbons, silicone fluids, mineral oils, gels and solutions of salts selected from the group consisting of sodium, calcium, potassium and mixtures thereof. 23. The method of claim 18, wherein said sol is cured to form a hydrophobic aerogel cladding layer.

Inventors: BRINKER C JEFFREY, FRAVAL HANAFI R, BRINKER, C., JEFFREY, FRAVAL, HANAFI, R.
Applicants: DEV CORP ENTERPRISE, ENTERPRISE DEVELOPMENT CORPORATION
Application year: 1999
Main classification: G02B6
IPC codes: G02B1, G02B6