METHOD OF FORMING UNDERCUT IN METAL POWDER INJECTION-MOLDED ARTICLE AND METAL POWDER INJECTION-MOLDED ARTICLE HAVING UNDERCUT

Abstract: To provide a method for forming undercuts of a metal injection molded product by simple processes and metal injection molded products having undercuts formed by the forming method thereof, steps are included of injection-molding a feed stock containing metal powder and binding resin, forming undercuts to a green body obtained by the injection-molding, and sintering after debinding the green body formed with undercuts. It is preferable that undercuts are formed by deforming at least one part of a green body; it is more preferable that they are deformed by pressing with a pressing member.

Description: Technical Field The present invention relates to a method of forming undercuts of a metal injection molded product. Technical Background In orthodontics, orthodontic devices such as brackets are directly bonded to the teeth, normally by the use of adhesive or the like. Force is applied to the brackets by an orthodontic archwire, and the teeth are forcefully aligned in an appropriate position thereby. Therefore, various proposals have been made so as to provide sufficient bonding strength to firmly hold such orthodontic device in orthodontic treatment. As one proposal thereof, undercuts, for instance, are provided on the surface of an orthodontic device to be bonded to the teeth. By providing undercuts, the area of the bonding surface increases, and the bonding strength increases, since there is an improvement in the holding power of the dental adhesive. Methods of providing undercuts to a bonding surface described above include a method of forming undercuts by machining or the like as secondary work after manufacturing an orthodontic device body, a method of fixing wire mesh to an orthodontic device body by welding or the like, and so on. However, regarding the method of carrying out the above-noted secondary work, as an orthodontic device is generally relatively small, there are problems such as extremely complex working, inferior productivity and high cost. Moreover, a strong metal such as titanium is used for orthodontic devices, so that the workability is poor and undercuts are extremely hard to form. Also, in the method of bonding a wire mesh by welding or the like, there is the problem that the mesh portion is buried by brazing filler metal during welding, and the bonding force between the wire mesh and the body gradually decreases. On the other hand, orthodontic device bodies have been recently manufactured by metal injection molding that has high yield, is flexible in molding shapes and can easily mold even complex shapes. Such metal injection molding method is used for producing a metal body by debinding and sintering after injection-molding a feed stock mainly of metal powder and binding resin. With such a metal injection molding method, one-body molding even into a complex shape is possible, but since a mold is used for injection-molding, undercuts cannot be directly molded without carrying out the secondary work to the sintered body. The objective of the present invention is to provide a method for forming undercuts of a metal injection molded product by means of a simple process without the need for secondary work, and to provide metal injection molded products having undercuts. Disclosure of the Invention The invention is defined in the claims. Brief Description of Drawings FIG. 1 is a partial sectional view showing a first embodiment of a method for forming undercuts of a metal injection molded product of the present invention. FIG. 2 is a partial sectional view showing the first embodiment of a method for forming undercuts of a metal injection molded product of the present invention. FIG. 3 is a partial sectional view showing the first embodiment of a method for forming undercuts of the metal injection molded product of the present invention. FIG. 4 is a partial sectional view showing a second embodiment of a method for forming undercuts of the metal injection molded product of the present invention. FIG. 5 is a partial sectional view showing a third embodiment of a method for forming undercuts of the metal injection molded product of the present invention. FIG. 6 is a view taken on line A-A of FIG. 5. FIG. 7 is a stereoscopic perspective view of an orthodontic device prepared by the present invention. FIG. 8 is an enlarged view of the orthodontic device shown in FIG. 7. FIG. 9 is a cross-sectional view of the orthodontic device shown in FIG. 7. FIG. 10 is a plan view showing the use of an orthodontic device prepared by the present invention. Best Modes for Carrying out the Invention Methods for forming undercuts of a metal injection molded product of the present invention are explained in detail hereafter with reference to the preferred embodiments shown in the attached figures. A method for manufacturing the orthodontic device (bracket) shown in FIG. 7, as a metal injection molded product with undercuts of the present invention, will be explained as an example. FIG. 1, FIG. 2 and FIG. 3 are partial sectional views showing a first embodiment of a method for forming undercuts of the metal injection molded product of the present invention. A method for forming undercuts of a metal injection molded product of the present invention comprises the steps of injection-molding a feed stock containing metal powder and binding resin, forming undercuts to a green body obtained by the injection-molding, and sintering the green body with the undercuts after debinding. More specifically, a metal injection molded product may be manufactured by the steps described below. First, a feed stock is prepared by mixing metal powder and binding resin by means of a kneading machine. Kneading may be carried out by the use of a kneading machine such as a kneader or a heating blender and the like. The kneading conditions are appropriately selected based on various conditions such as particle diameter and the shape of the metal powder, the type of binding resin, the amount of mixed additives and the like. If necessary, the feed stock may be pelletized. It is preferable that the ratio of metal powder in the feed stock be in the range of 80 wt. % to 98 wt.%. By setting the ratio of metal powder in this range, the feed stock has moderate flowability, excellent molding properties, and can provide a preferable sintered body. There is no particular limitation on the metal powder; however, in manufacturing an orthodontic device or the like, it is preferable to use a dental metallic material such as titanium, titanium alloy and stainless steel. Titanium and titanium alloy are particularly preferable. Since an orthodontic device is forcefully pulled by a metal wire or the like, it must have a high level of strength and toughness so as not to be damaged during its use. By using titanium or titanium alloy, these conditions can be easily satisfied. Furthermore, titanium and titanium alloy are extremely high in affinity to the human body and are particularly suitable as a material for an orthodontic device. Binding resin includes, for instance, polypropylene resin, polyethylene resin, acrylic resin, polystyrene resin, various kinds of waxes, and so on, and each of these materials may be used either alone or mixed and kneaded with one or more other ones of these materials. Moreover, in addition to the above-described metal powder and binding resin, various kinds of additives such as plasticizers, lubricants, antioxidants, debinding accelerators and surface active agents may be added, depending upon the need. The feed stock prepared thereby is injection-molded by an injection-molding machine. The molding conditions of the injection-molding are not particularly limited, and are appropriately set in accordance with the composition, viscosity, and the like of the feed stock. However, it is preferable that the material temperature be about 20°C to 200°C and that the injection pressure be about 30kgf/cm 2 to 150kgf/cm 2 . As a mold for injection-molding, the same type of mold as that for plastic molding may be generally used; however, in manufacturing a fine and complex green body as, for instance, an orthodontic device, it is preferable to use a hot runner or the like. FIG. 1 is a cross-sectional view showing one part of an injection molded green body extracted from a mold for injection-molding. A plurality of protruding parts 13 are formed on the green body 10. It is preferable that about sixteen to one thousand six hundred protruding parts 13 be arranged per 1cm 2 . The protruding parts 13 each have a tapered portion 15 with a decreasing width along the extraction direction of the mold. As these protruding parts 13 of the green body 10 are pressed by a pressing member 30a, tips of the protruding parts 13 are deformed and undercuts 16 are formed. Thus, if a green body is not yet sintered, it is possible to deform at least one part thereof and to easily form the desirable undercuts. Forming undercuts by deforming the injection green body 10 is preferably done by heating and softening. The unsintered green body 10 contains binding resin and has thermoplasticity, so that it can be easily deformed by heating. Methods of heating, softening and then deforming the green body 10 are not particularly limited, and include a method of contacting the body with a hot member, a method of adding high energy such as irradiation of high-frequency, a laser beam or the like without contacting, and so on. In case of this embodiment, the pressing surface 31 of the pressing member 30a is heated, and the tips of the protruding parts 13 are heated and softened by contacting them with this pressing surface 31, thus forming undercuts 16 by pressing further. The temperature of the pressing surface 31 may be optionally selected, but is preferably 90°C to 150°C. If the temperature of the pressing surface 31 is too high, the green body 10 will be softened sharply and maintaining the shape would sometimes be difficult. Moreover, decomposition, gasfication and the like of the binding resin are likely to occur. On the other hand, when the heating temperature is too low, the green body 10 is sometimes not softened at all, and when pressed in such a condition, a part or a whole body of the green body 10 is broken, cracked and so forth, thus often damaging the shape. FIG. 2 is a cross-sectional view showing another example of molding undercuts in this embodiment. As with the above-described case, the green body 10 is formed with a plurality of protruding parts 13. These protruding parts 13 may or may not be tapered; however, in this embodiment, they are not tapered. Protrusions 33 are formed on the pressing surface 31 of a pressing member 30b so as to match the protruding parts 13. The protrusions 33 and the protruding parts 13 mutually face each other, and as they are mutually pressed, the protrusions 33 are imbedded in the protruding parts 13 and tips of the protruding parts 13 are then deformed and split. These split pieces are pushed outward relative to the pressing direction, thus forming undercuts 16. Moreover, the shape, arrangement and so forth of the protrusions 33 formed at the pressing surface 31 may be optionally selected and set. Furthermore, as the protruding parts that are formed on the pressing surface 31, pins or the like may be imbedded. As in this embodiment, the locations, arrangement and so forth of the undercuts may be arranged by forming the protrusions on the pressing surface of the pressing member. Therefore, depending upon the purpose, and objective and so forth of the injection molded product, desirable undercuts may be formed. It is preferable that the pressing surface 31 be heated at 90°C to 150°C as in the above-mentioned case. FIG. 3 is a cross-sectional view showing another example of the molded undercuts in this embodiment. The same ones as in FIG. 2 may be used for the green body 10 and the pressing member 30c. As shown in the figure, protrusions 35 are formed on the pressing surface 31 of the pressing member 30c so as to face each recessed part 14. As the tips of the protrusions 35 are pressed so as to face the recessed parts 14, the protrusions 35 are pressed into the recessed parts 14. As a result, the tips of the protruding parts 13 adjoining recessed parts 14 are pushed aside, thereby forming undercuts 16. It is preferable that the pressing surface 31 be heated at 90°C to 150°C as in the above-mentioned case. Moreover, the shape, arrangement and so forth of the protrusions 35 formed on the pressing surface 31 may be optionally selected and set. Furthermore, as the protrusions that are formed at the pressing surface 31, pins or the like may be imbedded. Additionally, in case of forming undercuts with a pressing member, pressing may be done one or more times. In pressing several times, pressing may be repeated with pressing surfaces of identical shape or with pressing surfaces of different shapes; however, it is preferable to press using pressing surfaces of different shapes. By the combination of pressing surfaces of different shapes, various undercuts may be formed. Then, the green body 10 formed with undercuts as described is debound. Debinding is carried out by means of heat treatment in a non-oxidizing atmosphere, for instance, under a vacuum or in a low-pressure condition (e.g., 1 × 10 -1 Torr to 1 × 10 -6 Torr) or in an inert gas such as nitrogen gas and argon gas, and by the evaporation or decomposition of the binding resin. Debinding conditions such as temperature increase rate, debinding temperature, and so forth may be set so as not to evaporate or decompose the binding resin rapidly, and to avoid reactions between the binding resin and the metal powder. It is preferable that the debinding temperature be in the range of, for instance, 150°C to 750°C. Finally, the brown body that results from debinding is sintered. It is preferable that sintering be carried out at a low-pressure of 1×10 -2 Torr or below (more preferably, 1×10 -2 Torr to 1×10 -6 Torr) or in a vacuum, or in an inert gas atmosphere such as nitrogen gas and argon gas at 1 Torr to 760 Torr. The sintering temperature and sintering time are set so as to diffuse and grow metal powder grains to be crystal grains by sintering, so that the powder will be a dense sintered body as a whole, in other words, a body with high density and low porosity. It is preferable that the sintering temperature be 1000°C to 1500°C, and that the sintering time be 0.5 hours to 10 hours. After sintering, a metal injection molded product with undercuts is provided. According to the method of the present invention, metal injection molded products having undercuts may be easily obtained without secondary working and with only continuous processes. Moreover, without requiring a particular injection mechanism or a mold structure, pressing members (pressing surfaces) may be exchanged, so that it is possible to mold undercuts in a preferable size, shape and arrangement depending upon the purpose. FIG. 4 is a partial sectional view showing a second embodiment of a method for forming undercuts of a metal injection molded product of the present invention. The present invention is a method for forming undercuts of a metal injection molded product comprising the steps of injection-molding a feed stock containing metal powder and binding resin, debinding a green body molded by means of the injection molding, and sintering a brown body obtained by debinding; wherein the green body is integrated with an undercut molding member in one body. Feed stock preparation and injection-molding conditions, and the like are the same as in the first embodiment. Mainly the differences from the first embodiment will be explained hereafter, and the explanation of same elements will be omitted. FIG. 4 is a partial sectional view showing a part of a green body and a brown body in this embodiment. As shown in this figure, the green body 11 is made up of a green body 41 consisting of a feed stock which contains metal powder and binding resin, and an undercut molding member 40. The green body 41 and the undercut molding member 40 are mutually joined together into one body on the protruding parts 13 of the green body 41. Such a green body 11 may be obtained by injection-molding a feed stock while first filling the undercut molding member 40 into a mold for injection-molding as a core. For materials of the undercut molding member 40, any material is acceptable as long as it is removable and does not damage the shape of the green body 41 or the brown body 42, including e.g. any material decomposable and removable by heating, dissolving or other methods. Among these, a material removable by heating is preferable, and a material removable in the debinding step is further preferable. Debinding the green body 41 and removing the undercut molding member 40 may be carried out simultaneously in one step. As such a material for the undercut molding member 40, there are no particular limitations as long as the material can hold a shape even with the injection temperature of a feed stock during injection-molding, and is removable along with binding resin in the debinding step. A material containing resin as a main component is preferable, and a resin material having a melting point of 150°C to 400°C is more preferable. Such resins include e.g. polypropylene, polyethylene, polystyrene, polyacetal, acrylic resin, and so forth. The undercut molding member 40 is removed from the green body 11 thereby, thus providing the brown body 42 that comprises the undercuts 16 as shown in the figure. By sintering the brown body 42 as in the first embodiment, a metal injection molded product having undercuts may be provided. The undercut molding member 40 that is used as in this embodiment consists of a material removable by heating or the like after injection-molding. Thus, there will be no limitations on mold-release from a mold for injection-molding, flexibility on the shapes and sizes of a green body will improve sharply; and any undercuts may be formed. FIG. 5 and FIG. 6 are partial sectional views showing a third embodiment of the method for forming undercuts of a metal injection molded product of the present invention. The present invention is a method for forming undercuts of a metal injection molded product comprising the steps of injection-molding a feed stock containing metal powder and binding resin, and sintering a green body molded by injection-molding after debinding; whereas a mold for injection-molding having a core for forming undercuts in the mold is used in the injection-molding step. The same feed stock preparation, injection-molding conditions, and so forth may be carried out as in the first embodiment and the second embodiment mentioned above. Mainly the differences between the first embodiment and the second embodiment will be explained, and explanation of same elements will be omitted. FIG. 5 is a partial sectional view showing one example of a core provided in a mold for injection-molding used in this embodiment. FIG. 6 is a view taken on line A-A of FIG. 5. The core 50 is formed with fins 52 as shown in the figure. The fins 52 each have its tips split four ways, and a green body is formed with undercuts by the shape of these fins 52. It is preferable that such a core 50 be made up of an elastic material. The fins 52 can be stretched or deformed, and may be easily released from the undercuts 16 of the green body 10. The fins 52 have open tips as shown in FIG. 5 and FIG. 6. When a fin 52 maintains this shape after injection-molding, it engages in the release direction of the core 50, so that release from the green body 10 will be extremely difficult. However, when the fin 52 has elasticity as in the present invention, the tips of the fin 52 close as the core 50 is being released, so that releasing becomes possible. By fully utilizing characteristics such as flexibility and deformation of an elastic material as described above, it is possible to easily remove, from a mold, a green body with undercuts which could not be removed solely by opening and closing the mold. As the elastic material constituting the core 50, a material having a Vickers hardness of 40 to 100 is, for instance, preferable. With a hardness below 40, sufficient rigidity and shape maintaining properties cannot be obtained as a core; and at above 100, the fins 52 cannot be fully deformed, causing problems such as scratching the green body 10 during extraction. Moreover, the tensile strength is preferably 60kg/cm 2 or more. At less than 60kg/cm 2 of tensile strength, the strength will not be sufficient to withstand stress during extraction, and extraction will be sometimes difficult. Materials of such a core 50 include EVA resin (ethylene-vinyl acetate copolymer), chlorinated polyethylene, thermoplastic elastomer, rubber material (natural rubber, synthetic rubber), and the like. Examples of synthetic rubber include e.g. polyisoprene rubber, butadiene rubber, 1,2-polybutadiene rubber, styrene-butadiene rubber, chloroprene rubber, nitrile rubber, butyl rubber, ethylene-propylene rubber, chlorosulfonated polyethylene, acrylic rubber, epichlorohydrine rubber, silicone rubber, fluoro-rubber, urethane rubber, and the like. Each of these rubber materials may be used either alone or as a mixture with one or more other ones of these rubbers; however, among these, silicone rubber is preferable. Silicone rubber is applicable in a wide temperature range and is excellent in heat resistance, oil resistance and weather resistance. Thus, it is not transformed, decomposed, etc. by temperature and pressure during injection-molding, and the shape of the fins 52 may be kept well. Moreover, it is unlikely that the rubber will react with feed stock components such as the metal powder. The core 50 may be entirely made up of an elastic material like silicone rubber in the present invention, or may be made up of an elastic material, a metal material, and so forth. In this case, it is preferable that at least fins 52 be made up of an elastic material such as silicone rubber and that other parts be made up of a metal material or the like. After the core 50 is removed, a metal injection molded product having undercuts may be obtained by debinding and sintering the green body 10 as in the first embodiment. The undercuts formed as in the above-mentioned embodiments may have a regular or an irregular pattern. Also, undercuts may be formed so as to keep the angles and sizes thereof the same, or to change angles and so forth irregularly based on a predetermined order. Moreover, a metal injection molded product with undercuts that is molded in accordance with the present invention may be for any use, but includes, for example, an orthodontic device. In the case of an orthodontic device, as shown in FIG. 7 and FIG. 9, it is preferable to form undercuts 16 to a bonding surface 6 at which the device is bonded to teeth. As a result, the surface area of the bonding surface 6 will increase, and adhesion will be fully maintained, providing excellent adhesive strength. Methods for forming undercuts of metal injection molded products having undercuts of the present invention were explained above by referring to each embodiment shown in figures, but the present invention is not limited to these. For instance, as an undercut molding member, resinous beads or the like may be used. Examples Next, specific examples of the present invention will be explained. Example 1 Titanium powder (average particle size: 15µm, 92 wt.%), polypropylene as binding resin, ethylene-vinyl acetate copolymer (EVA), and other various additives (paraffin wax, dibutylphthalate) were mixed at a predetermined ratio, and were kneaded by a kneading machine, thus preparing a feed stock. Then, this feed stock was heated to melt the binding resin and was injected into a mold for injection-molding, thus providing a green body 10. The tips of protruding portions 13 of this green body 10 were pressed with a pressing member 30a having a pressing surface 31 with the shape shown in FIG. 1 and heated at 120°C, thus forming undercuts 16. The green body 10 formed with undercuts 16 was heated for one hour at 450°C in vacuum in a predetermined debinding furnace, decomposing and removing the binding resin and the additives without damaging the shape of the green body and thus providing a brown body. Then, the brown body was shifted to a sintering furnace, and was sintered for three hours at 1,200°C in argon gas and was then cooled, providing an orthodontic bracket 1 formed with undercuts 16 at the bonding surface 6 as shown in FIG. 7 and FIG. 9. Each part of this orthodontic bracket 1 has the following shape: Size of base 2: 5mm×5mm Protruding parts 13: 100 per 1cm 2 Depth of recessed part of an undercut 16: 0.3mm Depth of a slot 7: 2.5mm, Width thereof: 1.3mm Example 2 A feed stock having the same composition as in Example 1 was prepared. Then, an undercut molding member 40 as shown in the figure (made of polystyrene; melting point of 200°C) was provided inside a mold for injection-molding. The feed stock was injected into this mold for injection-molding as in Example 1, thus providing a green body 11 as shown in FIG. 4. This green body 11 was heated for 1.5 hours in nitrogen gas in a predetermined debinding furnace; the binding resin and the additives were decomposed and removed; and at the same time, the undercut molding member 40 was removed, thus providing a brown body 42 formed with undercuts 16. Then, this brown body 42 was shifted to a sintering furnace, and was sintered for three hours at 1,200°C in vacuum and was then cooled, providing the orthodontic bracket 1 as in Example 1. Example 3 A feed stock having the same composition as in Example 1 was prepared. Then, this feed stock was heated to melt the binding resin, and was injected into a mold for injection-molding. In the mold for injection-molding, a core 50 made of silicone resin having a shape as shown in FIG. 5 was provided in advance. After the injected feed stock was solidified, the mold for injection-molding was opened and the core 50 was pulled out from the green body. The tips of the fins 52 were closed as the core 50 was pulled out of the green body, so that it was possible to extract the core without damaging the undercut shape of the green body. The green body thus formed with the undercuts was debound and sintered as in Embodiment 1, thus providing the same orthodontic bracket 1 as in Example 1. Dental adhesive was coated onto the bonding surface 6 of each orthodontic bracket 1 prepared in Examples 1 to 3, and was fixed to the surface of a tooth 9 as shown in FIG. 10. Then, a stainless wire 8 was passed through slots 7 provided at engagement parts 3 of brackets 1, and was mounted. One end of the wire 8 was fixed in this condition and sufficient tension was applied by pulling the other end. The brackets 1 were appropriately fixed to the teeth 9, and there appeared to be no shaky, separated, or so forth brackets 1. As described above, according to the method of the present invention, a metal injection molded product having undercuts can be provided without requiring unique mold structures or the like, and without requiring complex secondary processing. Furthermore, undercut patterns and the like may be easily arranged and changed. When a metal injection molded product with undercuts is an orthodontic device, a bonding area increases due to the formation of undercuts and the bonding strength to teeth may be maintained and improved. Furthermore, by selection of angles, locations and the like of undercuts, bonding strength may be preferably arranged. Industrial Application Metal injection molded products of the present invention are suitable as, for instance, an orthodontic device. Explanation of Reference Numerals 1 orthodontic bracket 2 base 3 engagement part 4 bonding surface 7 slot 8 wire 9 tooth 10 green body 11 green body 13 protruding part 14 recessed part 15 tapered portion 16 undercut 30a, 30b, 30c pressing member 31 pressing surface 33, 35 protrusion 40 undercut molding member 41 green body 42 brown body 50 core 52 fin

Claims: A method of forming a metal injection molded product provided with undercuts, the method comprising the steps of: (a) injection-molding a feed stock containing metal powder and binding resin; (b) forming undercuts (16) to an injection green body (11) provided by step (a), wherein the undercuts are formed by pressing at least one part (13) of the injection green body with a pressing member (31) having a heated pressing surface; and (c) sintering the injection green body formed with the undercuts after debinding. A method of forming a metal injection molded product provided with undercuts, the method comprising the steps of: (a) injection-molding a feed stock containing metal powder and binding resin; (b) forming undercuts (16) to an injection green body (11) provided by step (a), wherein the undercuts are formed by heating and softening the injection green body (11); and (c) sintering the injection green body formed with the undercuts after debinding. The method of Claim 2, wherein step (b) comprises pressing at least one part (13) of the injection green body (11) with a pressing member (31). The method of Claim 3, wherein a pressing surface (30a) of the pressing member (31) is heated. The method of Claim 1 or 4, wherein the temperature of the pressing surface is 90°C to 150°C. The method of Claim 1, 3, 4 or 5, wherein protrusions (33) are formed at a pressing surface (30b) of the pressing member (31). The method of any one of Claims 1 and 3 to 6, wherein the pressing is carried out a plurality of times. The method of Claim 7, wherein the pressing is repeated while changing the shape of the pressing surface. A method of forming a metal injection molded product provided with undercuts, the method comprising the steps of: (a) injection-molding a feed stock containing metal powder and binding resin; and (b) sintering an injection green body molded by step (a) after debinding; wherein a mold for injection-molding having a core (50) made up of an elastic material for forming undercuts in the mold is used in step (a). The method of Claim 9, wherein the elastic material has a Vickers hardness of 40 to 100. The method of Claim 9 or Claim 10, wherein the elastic material has tensile strength of 6 N/mm 2 (60 kg/cm 2 ) or more. The method of Claim 9 or Claim 10, wherein the elastic material consists of silicone rubber. Use of the method as defined in any one of the preceding Claims for manufacturing an orthodontic device. The use of Claim 12, wherein the undercuts (16) are provided in a tooth-bonding surface (6) of the orthodontic device (1).

Inventors: HAYASHI JUNICHI, KATO MASARU, SHIMODAIRA KENICHI, HAYASHI, JUNICHI, KATO, MASARU, SHIMODAIRA, KENICHI
Applicants: SEIKO EPSON CORP, SEIKO EPSON CORPORATION
Application year: 1999
Main classification: B22F3
IPC codes: A61C7, B22F3, A61C13, B22F5