Method of manufacturing phenol by direct oxidation of benzene

Abstract: Benzene is oxidised to phenol either with oxygen gas in acetic acid as solvent and using a catalyst consisting of zinc and vanadium on alumina, or with N 2 O in a continuous flow reactor, using a copper on zeolite catalyst.

Description: The present invention relates to a method of manufacturing phenol by a single stage direct oxidation of benzener in the liquid phase. A cumene process is widely used for manufacturing phenol. In the cumene process, phenol is obtained from the starting material benzene by the steps (I) to (III) given below: (I) Cumene is produced by the reaction between benzene and propylene in the presence of an acid catalyst. (II) Cumene hydroperoxide is produced by the reaction between cumene and oxygen. (III) Cumene hydroperoxide is decomposed in the presence of an acid catalyst into phenol and acetone. However, the cumene process, which involves three process steps, is not economical. Also, the phenol manufacture is dependent on the market price of acetone obtained as a by-product in the cumene process. Under the circumstances, the present inventor has conducted an extensive research on the method to obtain phenol by direct oxidation of benzene in the presence of a Cu-supported catalyst. However, the conventional method is not satisfactory in the phenol yield and leaves room for further improvement in the phenol manufacturing cost. An object of the present invention is to provide a method of manufacturing phenol by direct oxidation of benzener in the liquid phase. According to the present invention, there is provided a method of manufacturing phenol, comprising the steps of placing benzene and a zinc-vanadium-supported alumina catalyst in an aqueous solution of acetic acid used as a solvent, and directly oxidizing benzene in the liquid phase under an oxygen gas atmosphere to produce phenol. The present invention provides a method of manufacturing phenol by direct oxidation of benzene by a liquid phase catalytic process. In the method according to the present invention, phenol is manufactured by direct oxidation of benzene using a zinc-vanadium-supported alumina catalyst (Zn-V/Al 2 O 3 catalyst). Zinc contained in the Zn-V/Al 2 O 3 catalyst exhibits a reducing function. An ion exchange method, an impregnation method, a sol-gel method, etc., can be employed for having zinc and vanadium supported by alumina. An aqueous solution of acetic acid having a concentration of 1N is used as a solvent. The reaction is carried out under an atmosphere of an oxygen gas acting as an oxidant, the oxygen gas atmosphere having a pressure of, for example, 1 to 10 atm (0.1 to 1 MPa), preferably 3 to 10 atm (0.3 to 1 MPa). The reaction temperature should desirably be set at 293 to 333K and the reaction time should desirably be set at 10 to 25 hours. Alumina is used as a support in the method of the present invention because the amount of the vanadium elution during the reaction can be diminished, compared with the use of another support such as silica or MCM-41. The phenol yield is not high. However, since a costly reducing agent such as ascorbic acid is not used, it may be possible to lower the manufacturing cost of phenol. EXAMPLES Example 1 A zinc-vanadium-supported alumina catalyst (Zn-V/Al 2 O 3 catalyst) was prepared by impregnating an alumina support with vanadium and zinc exhibiting a reducing function. Loaded in a batch type reactor were 0.1g of the Zn-V/Al 2 O 3 catalyst prepared as above, 5.6 mmol of benzene, and 5 mL of 1N (80% by volume) aqueous solution of acetic acid used as a solvent. Reaction was carried out within the reactor for 24 hours at 333K under an oxygen atmosphere while stirring the reaction system with a magnetic stirrer. The reaction product was analyzed by a gas chromatography. Phenol was obtained with a yield of 0.1%. As described above, in the case of using Zn-V/Al 2 O 3 catalyst, phenol can be obtained without using ascorbic acid that is costly, though the phenol yield is low. Therefore, it is possible to manufacture phenol at a low manufacturing cost.

Claims: A method of manufacturing phenol, characterized by comprising the steps of: placing benzene and a zinc-vanadium-supported alumina catalyst in an aqueous solution of acetic acid used as a solvent; and directly oxidizing benzene in the liquid phase under an oxygen gas atmosphere to produce phenol. The method according to claim 1, characterized in that the pressure of the oxygen gas atmosphere is 0.1 to 1 MPa. The method according to claim 2, characterized in that the pressure of the oxygen gas atmosphere is 0.3 to 1 MPa. The method according to claim 1, characterized in that the reaction temperature is 293 to 333K. The method according to claim 1, characterized in that the reaction time is 10 to 25 hours.

Inventors: TSURUYA SHIGERU, TSURUYA, SHIGERU
Applicants: PRESIDENT OF KOBE UNIVERSITY A, PRESIDENT OF KOBE UNIVERSITY A GOVERNMENT AGENCY OF JAPAN
Application year: 1999
Main classification: C07C39
IPC codes: C07C37, B01J29, C07C39, B01J23, C07B61