HYDROPHILIC COLLOID COMPOSITION

Abstract: A hydrophilic colloid composition having hydrophobic material dispersed therein and comprising an anionic surface active agent further comprises a cationic surface active agent in an amount sufficient to reduce the viscosity of the composition, the cationic surface active agent comprising a hydrophobic moiety, a non-ionic hydrophilic moiety and a cationic hydrophilic moiety.

Description: Hydrophilic Colloid Composition Field of the Invention The present invention relates to a hydrophilic colloid composition e.g. a composition for the coating of a layer in a photographic element. Background of the Invention Photographic coating compositions containing aqueous gelatin and high levels of anionic surfactants are prone to exhibit high viscosity, either as simple melts or as more complex melts such as dispersions of relatively hydrophobic materials (e.g. oil) where the anionic surfactant is used as the dispersing aid. In the simple melt case, rheological properties tend to be Newtonian in behaviour. In the disperse system case, systems can be strongly non-Newtonian, exhibiting high viscosity at low shear and low viscosity at high shear. Such properties can adversely affect the transport and coating uniformity of these systems. The addition of certain cationic or nonionic surfactants to these systems is known to reduce their viscosity and shear thinning behaviour, and can therefore be used to overcome problems of this kind. For example, US-A-5 300 418 describes the use of specific nonionic surfactants for reducing the viscosity of photographic dispersions. GB-A-2 140 572 describes the use of specific cationic surfactants for reducing the viscosity of photographic dispersions. Problem to be solved by the Invention There is a need for rheology modifiers in the above-mentioned compositions which are much more efficient at reducing low shear viscosity and shear thinning behaviour. Summary of the Invention The invention provides a hydrophilic colloid composition having hydrophobic material dispersed therein and comprising an anionic surface active agent characterised in that the composition further comprises a cationic surface active agent in an amount sufficient to reduce the viscosity of the composition, the cationic surface active agent comprising a hydrophobic moiety, a non-ionic hydrophilic moiety and a cationic hydrophilic moiety. Advantageous Effect of the Invention Cationic surfactants containing polyethoxylate groups offer advantages over either cationic or nonionic surfactants as rheology modifiers in the above-mentioned compositions. In the simple melt case, they are more efficient at reducing viscosity than either the nonionic or cationic surfactants, and show better compatibility with the anionic surfactants than basic cationic surfactants insofar as they provide clear solutions as opposed to cloudy or phase- separating systems. In the case of disperse systems, they are much more efficient at reducing low shear viscosity and shear thinning behaviour. Detailed Description of the Invention The cationic surface active agent used in the composition of the invention as a rheology modifier comprises a hydrophobic moiety, a nonionic hydrophilic moiety and a cationic hydrophilic moiety. The cationic hydrophilic moiety is preferably a quaternised nitrogen (N + ) to which the other moieties are covalently bound. The nonionic hydrophilic moiety is preferably one or two polyethoxylate groups. The hydrophobic moiety is preferably a hydrocarbon group. Preferred cationic surface active agents include compounds having the structure R L wherein R 1 is an alkyl, alkenyl, alkylaryl or arylalkyl chain having from 8 to 20 carbon atoms or a partially or fully fluorinated alkyl, alkenyl, alkylaryl or arylalkyl chain of equivalent hydrophobic strength e.g. having from 4-14 carbon atoms; R-2 is hydrogen, alkyl having from 1 to 8 carbon atoms e.g. methyl and n-butyl, or benzyl; R 3 is hydrogen or alkyl having from 1 to 4 carbon atoms e.g. methyl (preferably R 3 is hydrogen if the sum of n and m is greater than 0; X- is halide (preferably Br ~ or Cl ~ ) ; L represents a suitable linking chemistry between R 1 and the positively charged nitrogen e.g. a covalent chemical bond or - (CH2CH2θ) x -; each m and n independently is 0 or an integer such that m + n is 2 to 30, preferably 5 to 30, more preferably 12 to 18 and most preferably 15; and, x is an integer from 2 to 30, preferably 5 to 30, more preferably 12 to 18 and most preferably 15. For preferred structures, L is -(CH2CH2θ) x - when m + n is 0, and each m and n independently is greater than 0 when L is other than - (CH2CH2θ) x -. Preferred compounds include those wherein R! is an alkyl or alkylaryl group having from 10 to 20 carbon atoms; R 2 is alkyl having from 1 to 4 carbon atoms e.g. methyl and n-butyl; R 3 is hydrogen; L represents a covalent chemical bond; and, + n is 5 to 30, preferably 15. Other preferred compounds include those wherein R 1 is an alkyl or alkylaryl group having from 10 to 20 carbon atoms; R2 is alkyl having from 1 to 8, preferably 1 to 4 carbon atoms e.g. methyl and n-butyl; R 3 is alkyl having from 1 to 4 carbon atoms e.g. methyl; each and n independently is 0; L represents - (CH2CH2θ) x -; x is an integer from 5 to 30, preferably 15. Preferably, the cationic surface active agent is present in the composition in an amount from 0.1 to 0.5, more preferably from 0.2 to 0.4 equivalents relative to the amount of anionic surfactant present in the system. A preferred hydrophilic colloid is gelatin e.g. alkali-treated gelatin (cattle bone or hide gelatin) and acid-treated gelatin (pigskin or cattle gelatin) or a gelatin derivative e.g. acetylated gelatin and phthalated gelatin. Other suitable hydrophilic colloids include naturally occurring substances such as proteins, protein derivatives, cellulose derivatives e.g. cellulose esters, polysaccharides e.g. dextran, gum arabic, zein, casein and pectin, collagen derivatives, agar-agar, arrowroot and albumin. Examples of suitable synthetic hydrophilic colloids include polyvinyl alcohol, acrylamide polymers, maleic acid copolymers, acrylic acid copolymers, methacrylic acid copolymers and polyalkylene oxides. The hydrophobic material dispersed in the hydrophilic colloid composition may be any hydrophobic photographic addenda. A number of hydrophobic photographic additives used in light sensitive photographic materials are oil-soluble and are used by dissolving them in a substantially water-insoluble, high boiling point solvent which is then dispersed in an aqueous hydrophilic colloid solution with the assistance of a dispersing aid. Such oil-soluble additives include image forming dye couplers, dye stabilizers, antioxidants and ultra-violet radiation absorbing agents. A typical solvent used to dissolve the additive is aromatic e.g. di-n-butyl phthalate. In the following discussion of suitable materials for use in the compositions and materials of this invention, reference will be made to Research Disclosure, December, 1989, Item 308119, published by Kenneth Mason Publications, Ltd., Dudley Annex, 12a North Street, E sworth, Hampshire, P010 7DQ, UK. This publication will be identified hereafter by the term Research Disclosure. Suitable methods of preparing photographic dispersions are described in Research Disclosure, Sections XIV A and XIV B. For example, homogenised oil in aqueous gelatin dispersions of photographic couplers can be prepared by dissolving the coupler in a coupler solvent and mechanically dispersing the resulting solution in an aqueous gelatin solution (see U.S. Patent No. 2,322,027). Alternatively, microprecipitated dispersions of photographic couplers prepared by solvent and/or pH shift techniques are becoming more widely used (see references: U.K. Patent No. 1,193,349; Research Disclosure 16468, Dec 1977 pp 75-80; U.S. Serial No. 288,922 (1988) by K.Chari; U.S. Patent Nos. 4,970,139 & 5,089,380 by P.Bagchi; U.S. Patent No.5,008,179 by K.Chari, .A.Bowman & B.Thomas; U.S. Patent No. 5,104,776 by P.Bagchi & S. J.Sargeant) and offer benefits in decreased droplet size and often increased reactivity relative to conventional oil-in-water homogenised dispersions. Couplers which form cyan dyes upon reaction with oxidized color-developing agents are described in such representative patents and publications as U.S. Patent Nos. 2,772,162; 2,895,826; 3,002,836; 3,034,892; 2,747,293; 2,423,730; 2,367,531; 3,041,236; and 4,333,999; and Research Disclosure, Section VII D. Couplers which form magenta dyes upon reaction with oxidized color developing agents are described in such representative patents and publications as: U.S. Patent Nos. 2,600,788; 2,369,489; 2,343,703; 2,311,082; 3,152,896; 3,519,429; 3,062,653; and 2,908,573; and Research Disclosure, Section VII D. Couplers which form yellow dyes upon reaction with oxidized and color developing agents are described in such representative patents and publications as: U.S. Patent Nos. 2,875,057; 2,407,210; 3,265,506; 2,298,443; 3,048,194; and 3,447,928; and Research Disclosures, Section VII D. Couplers which form colorless products upon reaction with oxidized color developing agents are described in such representative patents as: UK Patent No. 861,138; U.S. Patent Nos. 3,632,345; 3,928,041; 3,958,993; and 3,961,959. The couplers can be dissolved in a solvent and then dispersed in a hydrophilic colloid. Examples of solvents usable for this process include organic solvents having a high boiling point, such as alkyl esters of phthalic acid (for example, dibutyl phthalate, dioctyl phthalate, and the like) , phosphoric acid esters (for example, diphenyl phosphate, triphenyl phosphate, tricresyl phosphate, dioctyl butyl phosphate, and the like) citric acid esters (for example, tributyl acetyl citrate, and the like) benzoic acid esters (for example, octyl benzoate, and the like), alkyla ides (for example, diethyl laurylamides, and the like) , esters of fatty acids (for example dibutoxyethyl succinate, dioctyl azelate, and the like), trimesic acid esters (for example, tributyl trimesate, and the like) , or the like; and organic solvents having a boiling point of from about 30° to about 150°C, such as lower alkyl acetates (for example, ethyl acetate, butyl acetate, and the like) , ethyl propionate, secondary butyl alcohol, methyl isobutyl ketone, b-ethoxyethyl acetate, methyl cellosolve acetate, or the like. Mixtures of organic solvents having a high boiling point and organic solvents having a low boiling point can also be used. Suitable anionic surface active agents may be chosen from any known anionic surface active agents. Examples of anionic surface active agents are as follows. 1. Sulphosuccinates having the general structure V(a) : M ■ + •O .OC-CH 2 R 1 L(OCH 2 CH 2 ) n OOC-CH-S0 3 " M + or V(b) wherein each R 1 independently is an alkyl, alkenyl, alkylaryl or arylalkyl chain having from 8 to 20 carbon atoms; M + is a suitable monovalent cation e.g. an alkali metal cation such as Na + , K + , Li + ; ammonium; alkylammonium such as N(CH3)4 + ' N(C2H5)4 + and N(C3H 7 ) + ; and, n is an integer from 1 to 30. Examples of compounds having structure V(a) are: Aerosol™ 102 (Cyanamid; n = 5, L = covalent bond, Rl = a Cιo~Ci2 straight chain alkyl group) ; Sermul™ EA176 (Servo BV; n = 10, L = covalent bond, Rl = nonylphenyl) . Examples of compounds having structure V(b) are: Aerosol™ MA (Cyanamid; R 1 = hexyl) ; Aerosol™ OT (Cyanamid; R-**- = 2-ethyl-hexyl) ; and the compound described in US A-4 968 599 (R 1 = n-C 3 F 7 CH 2 ) • 2. Phosphates having the general structure VI: wherein R! is an alkyl, alkenyl, alkylaryl or arylalkyl chain having from 8 to 20 carbon atoms; L is a simple linking group such as -0- or a covalent bond; M + is a suitable monovalent cation e.g. an alkali metal cation such as Na + , K + , Li + ; ammonium; alkylammonium such as N(CU3) + ' N(C2H5)4 + and N(C 3 H 7 )4 + ; and, n is an integer from 1 to 30. Examples of compounds having structure VI are: Sermul™ surfactants EA211, EA188, and EA205 (Servo BV, R 1 = nonylphenyl, L = -0-, M + = Na + , and n = 6, 10, and 50, respectively) . 3. Sulphates having the general structure VII: R 1 L(OCH 2 CH 2 ) n — O — S0 3 " M + wherein R 1 is an alkyl, alkenyl, alkylaryl or arylalkyl chain having from 8 to 20 carbon atoms or a fluoroalkyl group having 4 to 14 carbon atoms L is a simple linking group such as -0- or a covalent bond; M + is a suitable monovalent cation e.g. an alkali metal cation such as Na + , K + , Li + ; ammonium; alkylammonium such as N (033)4+' N(C2H5)4 + and N(C 3 H 7 )4+; and, n is 0 or an integer from 1 to 30. Examples of compounds having structure VII are: sodium dodecyl sulphate (R 1 = dodecyl, n = 0) ; Sermul™ surfactants EA54, EA151, EA146 (Servo BV, R 1 = nonylphenyl, L = covalent bond, M + = Na + and n = 4, 10, and 15, respectively) ; Polystep™ B23 (R 1 = dodecyl, and n = 10) ; sulphated derivatives of Brij™ 76 and 78 (ICI, Rl = I QU^I (average) , L = covalent bond, and n = 10 and 20, respectively) . 4. Sulphonates having the general structure VIII: R 1 L(OCH 2 CH 2 ) n S0 3 * M + wherein R 1 is an alkyl, alkenyl, alkylaryl or arylalkyl chain having from 8 to 20 carbon atoms; L is a simple linking group such as -0- or a covalent bond; M is a suitable monovalent cation e.g. an alkali metal cation such as Na + , K + , Li + ; ammonium; alkylammonium such as N(CH3)4 + ' N(C2H5)4 + and N(C 3 H 7 ) + ; and, n is 0 or an integer from 1 to 30. Examples of compounds having structure VIII are: Triton™ X-200 (Rohm and Haas, R 1 = t- octylphenyl, L = covalent bond, n = 2-4 nominal and M + = Na +) ; FT248™ (Bayer, R 1 = perfluorooctyl, L = covalent bond, n = 0 and M + = N(C2H5)4 + ); and Alkanol XC™ (DuPont, R 1 = triisopropyl naphthalene, L = covalent bond, n = 0 and M + = Na + ) . 5. Fluorocarboxylates having the general structure IX: R 1 COO ' M + wherein Rl is a fluoroalkyl chain having from 6 to 9 carbon atoms e.g C 7 Fi5, C8F]_ 7 and CgF-^g; and, M + is a suitable monovalent cation e.g. an alkali metal cation such as Na + , K + , Li + ; ammonium; alkylammonium such as N(CH3)4 + ' N(C2H5)4 + and N(C 3 H 7 ) + . Preferably, the anionic surface active agent is present in the composition in an amount from 0.5 to 2.0, more preferably from 0.7 to 1.2 percent by weight based on the weight of the total system. In accordance with the invention, a method of preparing a multilayer photographic material comprises (a) simultaneously coating on a support a plurality of aqueous hydrophilic colloid layers including at least one light-sensitive silver halide emulsion layer wherein at least one of the hydrophilic colloid layers comprises a composition according to the invention and, (b) drying the coated layers. The invention is further illustrated by way of example as follows. Details of materials used in the specific examples are as follows. Surface active agents Other materials Coupler C2 Viscosity of Simple Aqueous Gelatin Melts Anionic surfactants tend to cause large increases in solution viscosity when added to aqueous gelatin melts (solutions) above their critical micelle concentration. This has been well demonstrated for a homologous series of alkyl sulphates (J Greener, B A Contestable, M D Bale, Macromolecules, 20, 2490, (1987)). It is known from the prior art references, that either nonionic or cationic surfactants can be added to such systems to lower the viscosity of the melt to aid their coating or transport. To test the materials of this invention a base standard solution was adopted as a point of reference. The base standard chosen was 1% w/w of the anionic surfactant Alkanol XC in aqueous gelatin solution containing 10% w/w deionised Type IV bone gelatin. This resulted in a base standard solution viscosity of 100 mPa s (at a shear rate of 23 s -1 ) . The molarity of the base standard solution was measured to be 23 milli-molar (iriM) by Epton titration with hyamine. Other surfactants were then incorporated into individual base standard solutions at two molar levels and the viscosities of the resultant solutions were measured. The molar levels selected were 6.9 mM and 20.7 mM which correspond to 0.3 and 0.9 equivalents wrt the anionic surfactant (Alkanol XC) in the base solution. The results are presented in Table 1. Table 1. Effect of Added Surfactants on Viscosity of Standard Anionic Surfactant/Gelatin Solution Viscosity Viscosity Sample η/mPa s η/mPa s Comments (shear rate 23 s "1 ) (shear rate 23 s '1 ) (viscosity 10% gelatin alone = 18 mPa s) (6.9 mM (20.7 mM Surfactant) Surfactant) Base Standard 100 100 Control: No Added Surfactant 1% Alkanol XC -t- 10% Gelatin (w/w) SDS 150 220 Clear solution, increased viscosity (anionic) Newtonian solutions Texofor FN15 56 35 Clear solutions, reduced viscosity (nonionic) Newtonian solutions Sermul EA146 65 43 Clear solutions with reduced viscosity (nonionic/anionic) 0.9 equivalents - shear-thinning Arquad C-50 75 27 0.3 equivalents - slightly cloudy, (cationic) 0.9 equivalents, - opaque & shear thinning DTAB 78 37 0.3 equivalents - slightly cloudy, (cationic) 0.9 equivalents, - opaque & shear thinning Ethoquad C/25 34 20 Clear solution (nonionic/cationic) Newtonian Ethoquad HT/25 35 18 Clear solution (nonionic/cationic) Newtonian C18E15DiMeBu 55 25 Clear solution (nonionic/cationic) Newtonian C18E19DiMeBu 38 23 Clear solution (nonionic/cationic) Newtonian FC8E10DiMeHx 56 28 Clear solution nonionic/cationic) Newtonian Table 1 shows clearly that the nonionic/cationic (ethoxylated cationic) class of surfactant gives certain advantages over the other surfactant classes: i) They reduce the viscosity of anionic surfactant/gelatin systems more efficiently than the cationic, nonionic or nonionic/anionic (ethoxylated anionic) classes. ii) As cationic species per se, they reduce viscosity without causing any phase separation (cloudiness), i.e. they show superior compatibility in solution with anionic surfactants than do simple cationics. The following experimental methods were used to prepare materials used in the Example of the invention: Preparation of 2 kg homogenised dispersion containing Coupler Cl 258g of coupler Cl was dissolved in a mixture of 65g di-n-butyl phthalate and 65g of solvent SI at 145 °C to make Solution A. 176g of gelatin was dissolved in 1196g of water containing 176g of an aqueous solution of Alkanol XC containing 17.6g of Alkanol XC and 31g of propionic acid/sodium propionate preservative to make Solution B. After heating Solution B to 80 °C, Solution A was added to Solution B and the whole mixture was immediately homogenised for 5 minutes at 10,000 rpm with a Kinematica Polytron homogeniser fitted with a 35mm diameter head. The homogenised mixture was then passed twice through a Microfluidics Microfluidiser (model no. 110E) which was run at 10,000 psi pressure and a water bath temperature of 75 °C to give the final dispersion. Preparation of 1.7 kg homogenised dispersion containing Coupler C2 149g of coupler Cl was dissolved in a mixture of 58.5g di-n-butyl phthalate, 22.3g of solvent SI, 79. lg of stabiliser S2 and 14.9g of scavenger S3 at 145 °C to make Solution C. 149g of gelatin was dissolved in 1032g of water containing 164g of an aqueous solution of Alkanol XC containing 16.4g of Alkanol XC and 32.7g of propionic acid/sodium propionate preservative to make solution D. After heating Solution D to 80 °C, Solution C was added to Solution D and the whole solution was immediately homogenised for 5 minutes at 10,000 rpm with a Kinematica Polytron homogeniser fitted with a 35mm diameter head. The homogenised mixture was then passed twice through a Microfluidics Microfluidiser (model no. 110E) which was run at 10,000 psi pressure and a water bath temperature of 75 °C to give the final dispersion. Sample Preparation of Disperse Systems The total amount of sample prepared was lOg. This comprised lg aqueous surfactant solution and 9 g dispersion. The surfactant solution was prepared by weighing the desired amount of surfactant to give appropriate molar equivalence to the Alkanol XC in the dispersion and making the weight up with water. The dispersion was heated at 45 °C until it had melted (approximately 20 minutes), then the surfactant solution was added and the mixture was shaken to ensure complete and rapid mixing. The resultant mixtures were heated at 45 °C for a further hour, after which time the flow curve was measured. Throughout, care was taken to ensure no air entered the system. Measurement of Viscosity The rheological measurements were made on two computer-controlled rheometers made by Bohlin Instruments, the Bohlin VOR - a controlled-strain rheometer and the Bohlin CS50 - a controlled-stress rheometer, both very versatile instruments. The small volume sample cell, C2.3/26 (bob-and-cup geometry), or the double concentric cylinder, DG 24/27 was used for the measurements. Flow curves (viscosity as a function of applied shear) were recorded to -1000 s "1 from stresses of < 0.1 Pa. For the experiments, 2 ml of sample was placed into the cup using a syringe. The bob, which was pre- war ed, was then lowered to the correct position and the sample sheared. A low viscosity silicone oil was placed on top of the sample to prevent formation of a surface film of dried gelatin. A cover was placed the measuring geometry to provide further thermal insulation. The sample was allowed to come to thermal equilibrium for a few minutes before the rheological experiments were performed. There appeared to be no shear-history dependence. All measurements were carried out at 42 °C. Example (Viscosity of Disperse Systems) Disperse systems using anionic surfactant/polymer combinations as stabiliser can possess a much higher viscosity than might be expected based on the volume of the dispersed phase. The high viscosity manifests itself at low shear rates as such systems tend to shear thin (reducing viscosity) with increasing shear rate. These effects are due to the dimensions of the adsorbed surfactant/polymer complex around the disperse phase which make the effective volume fraction of the disperse phase much larger than its base value. The greater the degree of dispersion (i.e. the smaller the dispersed droplet/particle), the more pronounced this effect. The property of high viscosity at low shear can make it difficult to pour, pump or de-bubble such systems as these actions are generally performed under conditions of low shear. In coated systems containing high effective volume fractions of disperse phase where viscosities and shear thinning are highly dependent on shear, the cross-width coating uniformity can be very poor. Avoidance of these problems means limiting the loading of the disperse phase which may not be desirable. For instance, limited loading gives the disadvantage that more drying will be necessary to remove solvent i.e. water. These particular problems are sometimes encountered in photographic systems where hydrophobic particles or droplets are dispersed in an aqueous gelatin medium. An example system is a colour coupler dispersion where the colour coupler is dispersed with solvent in aqueous gelatin. As stated in the previous section, it is known from the Prior Art references that either nonionic or cationic surfactants can be added to such systems to lower the viscosity of the disperse system, and so aid their coating, transport or loading. To compare the materials of this invention with those from the prior art, concentrated solutions of the test surfactants were added to a coupler dispersion in the proportions, 1 part concentrated surfactant to 9 parts colour coupler dispersion. The idea here was to minimise the dilution such that the rheological characteristics of the coupler dispersion were not unduly lost, i.e. to maintain the effective volume fraction of the disperse phase as far as practicable. Tables 2 and 3 show the results for colour coupler systems Cl and C2 respectively, which like Table 1 compare the added surfactants on equivalent molar bases. In these Tables, the low shear rate viscosity is represented nominally as the limiting Newtonian viscosity (η 0 ) as derived from the Cross model - η = η ∞ + f η o - η ∞ } / { 1 + <λ .γ p , which is one of several that have been put forward to describe the shear thinning between the limiting Newtonian viscosities η 0 and η^ at low and high shear rates respectively, γ is the shear rate, and λ and m are a characteristic time and exponent respectively which describe the thinning behaviour. Table 2. Reduction of Limiting Low Shear Viscosity in Dispersions of Colour Coupler Cl (18.2 mM Alkanol XC) Table 3. Reduction of Limiting Low Shear Viscosity in Dispersions of Colour Coupler C2 (19.8 mM Alkanol XC) Limiting Low Shear Viscosity η o mPa s Tables 2 and 3 both demonstrate clearly that the nonionic/cationic (ethoxylated cationic) class of surfactant show advantages in efficiency over the other surfactant classes in terms of reducing the limiting low shear viscosity of disperse systems dispersed with anionic surfactants in a polymer medium such as gelatin. Addition of these surfactants also serves to reduce shear thinning.

Claims: Claims : 1. A hydrophilic colloid composition having hydrophobic material dispersed therein and comprising an anionic surface active agent characterised in that s the composition further comprises a cationic surface active agent in an amount sufficient to reduce the viscosity of the composition, the cationic surface active agent comprising a hydrophobic moiety, a nonionic hydrophilic moiety and a cationic hydrophilic moiety. 2. A composition according to claim 1 wherein the cationic surface active agent has the structure (CH 2 CH 2 0) m R 3 wherein R 1 is an alkyl, alkenyl, alkylaryl or arylalkyl chain having from 8 to 20 carbon atoms or a partially or fully fluorinated alkyl, alkenyl, alkylaryl or arylalkyl chain of equivalent hydrophobic strength e.g. having from 4-14 carbon atoms; R-2 is hydrogen, alkyl having from 1 to 8 carbon atoms e.g. methyl and n-butyl, or benzyl; R-3 is hydrogen or alkyl having from 1 to 4 carbon atoms e.g. methyl (preferably R-3 is hydrogen if the sum of n and m is greater than 0; X ~ is halide (preferably Br ~ or Cl " ) ; L represents a suitable linking chemistry between R 1 and the positively charged nitrogen e.g. a covalent chemical bond or - (CH2CH2θ) x -; each m and n independently is 0 or an integer such that m + n is 2 to 30, preferably 5 to 30, more preferably 12 to 18 and most preferably 15; and, x is an integer from 2 to 30, preferably 5 to 30, more preferably 12 to 18 and most preferably s 15. 3. A composition according to claim 2 wherein R 1 is an alkyl or alkylaryl group having from 10 to 20 carbon atoms; R-2 is alkyl having from 1 to 4 carbon atoms e.g. methyl and n-butyl; R3 is hydrogen; L represents a covalent chemical bond; and, m + n is 5 to 30, preferably 15. 4. A composition according to claim 2 wherein R! is an alkyl or alkylaryl group having from 10 to 20 carbon atoms; R-2 is alkyl having from 1 to 8, preferably 1 to 4 carbon atoms e.g. methyl and n-butyl; R-3 is alkyl having from 1 to 4 carbon atoms e.g. methyl; each m and n independently is 0; L represents - (CH2CH2θ) x -; x is an integer from 5 to 30, preferably 15. 5. A composition according to any one of the preceding claims wherein the cationic surface active agent is present in the composition in an amount from 0.1 to 0.5 equivalents relative to the amount of anionic surfactant in the system. 6. A composition according to any one of the preceding claims wherein the hydrophilic colloid is gelatin. 7. A composition according to any one of the preceding claims wherein the anionic surface active agent is selected from sulphosuccinates, alkyl ether phosphates, alkyl sulphates, alkyl ether sulphates, alkyl sulphonates, alkyl ether sulphonates, aryl sulphonates and aryl ether sulphonates. 8. A composition according to any one of the preceding claims wherein the anionic surface active agent is present in the composition in an amount from 0.5 to 2.0 percent by weight based on the weight of the total system. 9. A composition according to any one of the preceding claims wherein the hydrophobic material is a photographic coupler. 10. A photographic material comprising a plurality of hydrophilic colloid layers including at least one light sensitive silver halide emulsion layer wherein at least one of the hydrophilic colloid layers is formed from a composition according to any one of the preceding claims.

Inventors: HOWE ANDREW, MILLER DAVID DARRELL, PITT ALAN ROBERT, HOWE, ANDREW, MILLER, DAVID, DARRELL, PITT, ALAN, ROBERT
Applicants: EASTMAN KODAK CO, HOWE ANDREW, MILLER DAVID DARRELL, PITT ALAN ROBERT, EASTMAN KODAK COMPANY, HOWE, ANDREW, MILLER, DAVID, DARRELL, PITT, ALAN, ROBERT
Application year: 1999
Main classification: C07C4
IPC codes: G03C1, G03C7