MODIFIED STARCH

Abstract: The present invention relates to a process for the preparation of a stable, chlorine free modified starch which is useful in paper coating and sizing. In the process, starch is degraded by catalyzed hydrogen peroxide oxydation, and stabilized by acetyl esterification, combined with cross-linking of the starch.

Description: Modified starch The invention relates to a way to prepare stable, chlorine free modified starch which is useful in paper coat- ing and sizing. Starches, which for the most part are modified starch derivatives, are one of the most used raw material group in paper industry, besides fibres and pigments. Starch is used either as mass starch increasing the dry strength of the paper, whereby it is added to the mass in the wet end of a paper-making machine, or as surface size, whereby the starch solution is spread onto the surface of dried paper. Additionally, starch is used in paper industry as a binder in coating pastes and colours, as a protecting colloid in AKD dispersions, and as a stem in starch based fixatives. Starch is a carbohydrate present in all plants in the nature. It is present in concentrated form in seeds, roots and tubers, where it functions as stored food for the new growing season. Starch is a glucose polymer, in which anhydroglucose units are linked to each other with α-D-glucosidic bonds. Glucose chains are either linear (amylose) or branched (amylopectin) . In a normal case the proportion of amylose is smaller than that of amylo-pec- tin, about 20 to 25 %. The size of a starch chain is also variable, depending on the plant from which the starch has been isolated, or if it is the question of amylose or amylopectin. Amylose has a shorter chain than amylopectin. The sizing properties of starch are based on the large number of its hydroxyl groups, which are able to form hydrogen bonds. In a water solution the hydrogen bonds are formed between hydroxyl groups and water molecules. Thereby the starch binds water by means of hydrogen bonds, which is an important characteristics e.g. in a coating paste and colour. During drying water molecules are removed and hydrogen bonds are formed between starch, fibres and other components used in paper making, whereby the starch functions as a dry strength size in the paper and in coating paste. Starch is insoluble in cold water. When a mixture of starch and water is heated, starch begins to dissolve, to gelate, at a certain temperature, which can be seen as the rise of the viscosity of the solution. Viscosity is raised when continuing the heating, until individual starch chains begin to detach from each other, which for its part can be seen as lowering of viscosity. When the solution is cooled, the starch chains begin to associate anew to each other by means of hydrogen bonds, whereby the viscosity again raises. In a dilute solution the associated starch chains settle onto the bottom of the container, but concentrated solutions form a three-dimensional gel. The phenomenon is called retrogradation. The gelatinizing properties of starch can be studied by a Brabender-viscograph, by the help of which the behavior of starch is detected during heating and cooling. Starch sludge is heated in the device with an even rate up to 95 °C, kept there for 15 minutes, whereafter the solution is cooled with an even rate to room temperature. All the time during the determination, viscosity and temperature are measured, and graphs for them are drawn. Starch solutions have two functional characteristics: Viscosity: As by polymer solutions in general, the viscosity of a starch solution depends on the average molecular size. In addition to the molecular size, viscosity is effected by temperature, dry matter and the ionic con- centration of the solution (pH, hardness, conductibili- ty). Stability: As concentrated solutions starch has a tendency to retrogradate when cooling, which is detected as rising of viscosity, as turbidity or as solidifying of the solution. Retrogradation is mainly caused by the linear chains, which are easily attached to each other by means of hydrogen bonds. When starch is degraded, the proportion of linear chains increases. The stability increases, when the branching and the number of side chains are increased. The modification of starches can be divided into two main types: chemical and rheological. In this connection the chemical modification means the substitution of starch with chemical groups and by means of them changing the charge condition of the starch, or increasing the stability. Since starch is a polyol, these modifications are mostly ethers or esters. Rheological modifications are made, when higher dry matter contents are desirable in solutions, which means decreasing the viscosity by hydro- lysis or oxydation. For hydrolysis, enzymes or acids can be used, and for oxydation, e.g. sodium hypochlorite or hydrogen peroxide. This kind of products include surface sizes and binders of coating paste and colour. In some cases, such as in cationic surface sizes, both modifica- tions are made. Starch products with low viscosity, used in surface sizing and as binders of coating pastes, are usually prepared by oxidizing with sodium hypochlorite. Besides hydro- lyzing starch chains to shorter fragments, hypochlorite forms carboxyl groups which stabilize the product. The stability of the products is very important in modified starches used as binders of coating paste, which starches must be prepared and used as solutions, the dry matter of which is high. As indicated above, the stability of a starch solution means in this connection such a solution which, while cooling, does not gelate to a hard gel, but retains its fluidity. A general objective in pulp and paper industry is to try to decrease formation of organic chlorine compounds (OX) in manufacturing processes, which has led to decreased use of chlorine. AOX-determination (AOX = absorbable organic halogen) is used as the measure of organic halogen compounds, which indicates the amount of elementary halogen bound to organic material. Since in this connection chlorine is the most common halogen, in practice reference can be made to organic chlorine compounds. Since starch is a raw material commonly used in paper industry, demands have been presented to use also starch modifying processes where no chlorine is used, as the risk of the formation of organic chlorine compounds is obvious also when oxidizing with hypochlorite. Compounds formed can remain in the product and be carried with the product to the paper mill, which for its part increases the amount of organic chlorine compounds in paper and is detrimental when trying to manufacture OX-free paper. Two required characteristics for the coating starch are thus: low viscosity and stability. Besides by hypochlorite oxidizing, the viscosity can be decreased with other oxidizers, such as hydrogen peroxide, or by hydrolyzing with an acid. Hydrogen peroxide oxidizing has been used e.g. in US patent 3,655,644, where viscosity has been decreased using a copper catalyst, without which hydrogen peroxide does not function as a starch degrading agent. In said patent subsequent acetylation is also disclosed. By this process a desired viscosity level is obtained, but the stability of the products is insufficient in view of paper coating, when dry matter contents is high. A sufficient stability is obtained by combining acetylation with crosslinking, which is known from modified food products, as disclosed e.g. in publication EP-A-143643. Although in said publication hydrogen peroxide is used, copper catalyst is, however, not used, whereby starch does not degrade to a low viscosity modified starch, and thus the process differs substantially from the process of the present invention. In the starch products manufactured by the process according to the invention, degradation of starch with hydrogen peroxide and copper catalyst, as well as stabilization by acetylation and cross-linking, used in modifying food products, have been combined. This way enabled the preparation of modified starch products without chlorine, corresponding to products oxidized with hypochlorite. The products according to the invention may be used as binders of coating pastes in the same way as products oxidized with hypochlorite, which appears from the examples described hereafter illustrating the invention. Although potato starch is used as a raw material in the Examples, it is to be appreciated that in the process according to the invention all known commercial starches may be used. Example 1. This example describes the preparation of modified starches according to the present invention to different viscosity levels by changing the amount of oxidizer. 1200 g of potato starch were suspended into 1200 ml of water. The suspension was heated to 40 °C and pH was adjusted to 10 with 3% NaOH solution. 0.015% of copper sulphate (CuS0 4 x5H 2 0) was added. Three different tests were made, in which a) 1%, b) 1.5% and c) 2% of active hydrogen peroxide, calculated from the amount of the starch, were added. The mixtures were allowed to react for two hours while maintaining the pH of the suspension all the time at the value of 10. After the reaction time had expired, pH of the suspension was adjusted to 8, and 6% of acetic anhydride, calculated from the amount of starch, was added, in which 0.15% of adipic acid, also calculated from the amount of starch, had been dissolved. The mixture was allowed to react for two hours maintaining pH at 8 - 9 , whereafter the suspension was neutralized to pH 5-6. A sample was taken from each of the three modified starch suspensions, which were diluted, and cooked in a microwave oven so that the dry matter was 10%. The viscosities of the cooked solutions were measured by Brookfield vis- cosi eter, 100 rpm, spindle 1. The results are in the Table below, from which it appears that the process may be used to prepare products differing in their viscosity level. Test Viscosity la 22 Pas lb 19 mPas lc 16 mPas Brabender-curves were also run from the test products in the concentration of 25%, showing that the stabilities of the products are good. The curves are given in Appendices la, lb and lc. Brookfield-viscosity of the product oxidized with commercial hypochlorite is 21 mPas. The Brabender-curve of the same product is given in the Appendix 4. Example 2 . This example describes the effect of the acetylation level to the stability of the test products. Test products were prepared as in Example 1, but using constant 2% hydrogen peroxide dosage and three different acetic anhydride dosages: a) 4%, b) 6% and c) 8%. In crosslinking 0.15% of adipic acid, calculated from the amount of starch, dissolved in acetic anhydride, was used in all three tests. The test products were analysed as in Example 1. The Brookfield-viscosity values were: Test Viscosity 2a 18 mPas 2b 18 mPas 2c 17 mPas Brabender-curves run in the concentration of 25% are given in Appendices 2a, 2b and 2c. From the curves it appears that the stability increases strongly with increasing acetic anhydride dosage from 4 to 6%, but the change between 6% and 8% is fairly small. Example 3. This example describes the effect of cross-linking to the stability of the starch solution. The test modification was carried out as in Example 1, using for oxydation 2% of hydrogen peroxide, calculated from the amount of starch, and for acetylation 6% of acetic anhydride. In test a) 0.15% of adipic acid was used for cross-linking. In test b) no cross-linking was carried out. The products were analysed by running Brabender-curves, which are given in Appendices 3a and 3b. The curves show that cross-linking stabilizes the starch solution significantly and is thus essential for obtaining a competitive result. Example 4. Preparation of coated paper means coating of paper with a paste, which contains pigments, binders and some additives. Modified, most commonly oxidized starch is used as a binder. In this example the applicability of the new starches for a binder of a coating paste was tested. The tests were carried out by preparing test pastes from the starches 2a, 2b and 2c in a laboratory, using a basic recipe, containing 7 parts of latex and 6 parts of starch per 100 parts of pigments (potassium carbonate/caolin 70/30) , and comparing them to a paste prepared from starch oxidized by hypochlorite. The dry matter of the paste was 62%. From the pastes Brookfield-viscosity was determined, 100 rpm, spindle 4, as well as Haake-viscosity, which gives a picture of the behavior of the paste in high shear forces. In addition, water retention was determined, which represents the ability of the paste to keep the wa- ter it contains. A sufficient water retention is important because of the runability, since the paste may not moisten too much the base paper to be coated. Test Starch Brookfield- Haake- Water viscosity viscosity retention mPas mPas g/m 2 4a 2a 1000 37 0.079 4b 2b 1000 35 0.074 4c 2c 1 100 36 0.088 4d ref 1 500 38 0.038 The results show that the test products are suitable for a binders of a coating paste. Example 5 , In this example organic chlorine compounds are analysed, which arise during the preparation of the products, or are included in the products themselves. In the example the analysis results of the product 2b are compared to those of a product oxidized with hypochlorite. The AOX- determination was carried out both on the filtrate water, which represents the waste water arising during the pre- paration, and on the finished dried starch. Starch AOX of the filt- AOX of the rate water mg/1 product mg/kg 2b 3.6 5 ref. 74.0 90 The results show that during the preparation of the product prepared according to the process of the invention significantly smaller amounts of organic chlorine compounds are both arising, and retained in the product it- self.

Claims: Claims 1. A process for the preparation of modified starch, comprising degrading the starch by catalyzed hydrogen peroxide oxydation, and stabilizing by acetyl esterifica- tion, combined with crosslinking of the starch. 2. The process according to claim 1, wherein 0.1 - 2% of hydrogen peroxide, calculated from the amount of the starch, is used for the starch degradation. 3. The process according to claim 1, wherein 0.01 - 0.02% of copper sulphate, calculated from the amount of the starch, is used as a catalyst in the oxydation. 4. The process according to any one of the claims 1 to 3 , comprising stabilizing the starch by esterifying with acetic anhydride, and crosslinking with adipic acid. 5. The process according to claim 4, wherein adipic acid is dissolved in the acetic anhydride before the acetylation. 6. Use of the modified starch prepared according to any one of the claims 1 to 5 in surface sizing of paper, and as a binder of a coating paste and colour.

Inventors: HAGBERG PEGGY, KETOLA HANNU, HAGBERG, PEGGY, KETOLA, HANNU
Applicants: HAGBERG PEGGY, KETOLA HANNU, RAISIO CHEM OY, HAGBERG, PEGGY, KETOLA, HANNU, RAISIO CHEMICALS OY
Application year: 1998
Main classification: C08B31
IPC codes: C08B31, D21H17, D21H19