AIRCRAFT WHEEL PART WITH CORROSION AND WEAR RESISTANCE

Abstract: A drive key (10) for an aircraft wheel comprises a hardened and tempered steel member (10) having improved wear and corrosion resistance. The steel member (10) is coated selectively with a tungsten carbide-cobalt coating (22) to provide wear resistance at side portions (18) where the drive key (10) is engaged by portions of an aircraft brake, and the entire steel member (10) including the tungsten carbide-cobalt coating can be plated with electroless nickel to provide improved corrosion resistance.

Description: AIRCRAFT WHEEL PART WITH CORROSION AND WEAR RESISTANCE The present invention relates to a steel member having improved corrosion and wear resistance, and in particular to an aircraft wheel drive key having improved corrosion resistance by means of an electroless nickel plating disposed on the drive key member and tungsten carbide-cobalt coated areas thereof. Aircraft wheels may include separate drive key members which are attached by bolts to the wheel. The drive key members are engaged by rotors of the aircraft brake. During braking, braking torque must be withstood by the drive keys as the brake rotors are engaged by the brake stators. Typically, the drive key members may be made from hardened and tempered steel to provide a high tensile strength, or a nickel alloy such as Inconel ® . Inconel ® drive keys have an inherent corrosion resistance, but are significantly more expensive than steel drive keys. Steel drive keys, while costing only a fraction of the cost of Inconel ® drive keys, are subject to corrosion which can result in cracking and failures of the steel. Typically in a steel brake, steel drive key members are coated with a chromium plating which provides sufficient corrosion resistance in that brake environment. However, for aircraft brakes using carbon-carbon composite brake discs, the carbon dust from the brake discs effects a galvanic reaction with the chromium plated steel drive keys such that cleaning agents and de-icers may breach the chromium plating and cause corrosion of the steel member. The subsequent corrosion plus the high stress level of the part results in stress corrosion cracking and finally a failure of the part. It is highly desirable to provide an aircraft wheel steel drive key member which has improved corrosion resistance in order to protect the steel drive key from the effects of carbon dust and prevent both corrosion and the resulting cracking and failure of the part. The present invention provides solutions to the above by providing a steel member having corrosion resistance, the steel member comprising a hardened and tempered steel member having a high tensile strength, at least one selected portion of said steel member coated with tungsten carbide-cobalt to provide wear resistance, and a coating of electroless nickel coating on the steel member to provide corrosion resistance. 5 The invention is described in detail below with reference to the drawings which illustrate an aircraft wheel drive key in which: Figure 1 is a top view of a typical steel drive key for an aircraft wheel; and Figure 2 is a partial cross section of the drive key of Figure 1. 0 An aircraft wheel drive key is designated generally by reference numeral 10 in Figures 1 and 2. The drive key includes an inboard end extension 12 which is received within a hole at the inboard side of the wheel, and an outboard engagement portion 14 which engages the surface of the wheel and includes a through opening 16 through which extends a bolt which 5 in combination with a nut attaches the drive key to the aircraft wheel. Alternatively, the drive key can be attached to the wheel by means of two openings and bolts and nuts. In an aircraft wheel and brake system, the side portions designated generally by reference numerals 18 are engaged by inserts located at the periphery of rotors of the aircraft brake. The rotors and 0 stators of the aircraft brake are aligned axially along the length of the drive key 10, such that the inserts of the rotors engage the side portions 18. A drive key made from a nickel alloy such as Inconel ® 718 has inherent corrosion resistance but includes a significant cost due to the expense of the material utilized. To improve the wear resistance of Inconel ® 5 drive keys, the side portions of the drive keys have been coated with tungsten carbide-cobalt. Such drive keys have been used in aircraft brakes having carbon-carbon composite brake discs which generate carbon dust therefrom. In steel brakes, that is, state-of-the-art brakes that include steel rotors and stators which include brake linings attached to the stators (or vice 0 versa), steel drive keys are used such as the drive key illustrated in Figures 1 and 2. The steel drive keys have previously been plated with chromium in order to provide corrosion resistance. However, when these steel drive keys were subsequently utilized in a carbon aircraft brake, the carbon dust generated from the carbon-carbon composite brake discs caused a galvanic reaction with the steel of the drive key. This occurs because the "throwing" power of a chromium plating system is generally not sufficient to cover the wheel attachment bolt hole or opening 16 (Figures 1 and 2) or portions of the attachment flange 14, resulting in the base steel material being exposed to the galvanic reaction from the carbon dust and subsequent corrosion. Because the steel drive key has a high stress level ( it is hardened and tempered to 260-300,000 psi ultimate tensile strength), the corrosion results in stress risers at the affected areas with a subsequent cracking followed by finally a failure of the part. Steel drive keys made of H-11 alloy steel cost only a fraction of the cost of Inconel ® drive keys, and thus it is highly desirable to provide steel drive keys that can be used in a carbon aircraft brake without subsequent failure caused by the carbon dust generated by the brake. The present invention provides the desired wear resistance and improved corrosion resistance necessary for a steel drive key to be utilized, without subsequent stress cracking and failure, in a carbon brake having carbon-carbon composite brake discs. Steel drive keys made from H-11 alloy steel forgings are initially cleaned in order to remove dirt, oxides, grease or any other material that cause subsequent coatings or platings not to form on the steel surface. If desired, masking can be applied to the steel drive key in order to apply selectively a tungsten carbide-cobalt coating to a selected area or areas of the drive key. Depending on how the tungsten carbide- cobalt coating is applied and according to the size of the area desired to be coated, masking may not be necessary. As shown in Figures 1 and 2, the side or lateral areas 18 are covered with a tungsten carbide-cobalt coating 22 which provides the desired wear resistance for the steel drive key. The side portions 18 with the coating 22 will be engaged by drive inserts located about the periphery of the rotors of the carbon brake. The tungsten carbide-cobalt coating may be applied in different forms, such as the two example forms listed below: Constituent Type I Type II Sintered Tungsten Carbide 88% ± 2% 80% ± 2% Cobalt 12% ± 2% 17% ± 2% Others 2.5% max 2.5% max The "Others" constituent typically may comprise oxides present from the manufacture of the powder. The tungsten carbide-cobalt coating is applied by means of a thermal spraying using high velocity oxygen fueled equipment to produce a coating with less than 1 % apparent porosity and a bond strength of approximately 10,000 psi minimum. The thickness of the sprayed coating is according to the desired application. Next, the tungsten carbide-cobalt coated drive key 10 is cleaned and prepared, by well known procedures, to prepare it for electroless nickel plating. After cleaning and rinse, the drive key is immersed within an electroless nickel plating solution. After the plating operation, the drive key is rinsed, dried and subsequently heated to effect baking thereof. The baking can be at a low temperature of approximately 375° ± 25°F for approximately one day to provide embrittlement relief. It has been found that the electroless nickel plating applies an appropriate plating over the entire part, including the surfaces of the bolt hole 16, and parts of the flange 14 which previously were not fully adequately coated by a chromium plating. Although it is not necessary to provide the electroless nickel coating over the side portions 18 coated previously with tungsten carbide-cobalt, the process is simplified and cost reduced by simply providing an electroless nickel plating over the entire drive key. Subsequently during use, the electroless nickel plating will wear away from the subsisting tungsten carbide-cobalt coating, which is acceptable because the purpose of the tungsten carbide-cobalt coating is to provide wear resistance while the electroless nickel coating plating is provided to provide improved corrosion resistance for areas not coated by tungsten carbide-cobalt. The base metal, H-11 alloy steel, is shielded from corrosive agents by the tungsten carbide- cobalt coating after the electroless nickel plating is worn away. Carbon dust generated by the carbon-carbon composite brake disks of the carbon brake no longer can effect a galvanic reaction with the H-11 steel drive key member because of the integrity of the electroless nickel plating. The present invention provides a new and novel process and product comprising a steel member which has improved corrosion resistance in an environment which inherently would cause corrosion and subsequent part failure for an inadequately protected member. The tungsten carbide- cobalt coating followed by an electroless nickel plating of the drive key enables the long term use of steel drive keys in carbon aircraft brakes without subsequent corrosion and failures of the drive keys. The steel drive key members provide a significant cost savings in material costs over Inconel ® drive keys used in carbon aircraft brakes.

Claims: CLAIMS 1 . A process for providing a steel member having corrosion and wear resistance, comprising the steps of cleaning a steel member (1 0) to remove undesirable materials therefrom, thermally spraying the part to provide a coating (22) of tungsten carbide-cobalt, cleaning the steel member (10) and tungsten carbide-cobalt coating (22), and providing an electroless nickel plating on the steel member, whereby the tungsten carbide-cobalt coating provides wear resistance and the electroless nickel plating provides corrosion resistance. 2. The process in accordance with claim 1 , wherein the steel member (1 0) comprises H-1 1 steel that is hardened and tempered to provide high tensile strength. 3. The process in accordance with claim 1 , wherein the spraying step selectively locates the coating (22) of tungsten carbide- cobalt at a selected area (1 8) of the drive key. 4. The process in accordance with claim 3, wherein the steel member (1 0) comprises a drive key (1 0) for an aircraft wheel, and the selected area ( 1 8) comprises a portion (1 8) of the key ( 10) to be engaged by a portion of an aircraft brake. 5. The process in accordance with claim 4, wherein the drive key (1 0) includes an opening ( 1 6) therein which extends to a depth below an outer surface of said drive key (10), and the electroless nickel plating covers surfaces of said opening (1 6). 6. The process in accordance with claim 5, wherein the opening (1 6) comprises a through hole (1 6) for receiving therein an attachment member. 7. A steel member having corrosion resistance and made according to claim 1 , the steel member (10) comprising a hardened and tempered steel member (1 0) having a high tensile strength, at least one selected portion (1 8) of said steel member coated with tungsten carbide- cobalt to provide wear resistance, and a coating of electroless nickel coating on the steel member to provide corrosion resistance. SUB l l l Ul b SI I! LT (niSLH 26) - - η 8. The steel member in accordance with claim 7, wherein said tungsten carbide-cobalt coating (22) covers lateral areas (18) of said steel member (10). 9. The steel member in accordance with claim 7, wherein said steel member (10) comprises a drive key (10) for an aircraft wheel. 10. The steel member in accordance with claim 9, wherein the drive key (10) includes the tungsten carbide-cobalt coating (22) on side portions (18) thereof, and the electroless nickel coating is disposed over the entire key (10) including the tungsten carbide-cobalt coating (22). SUBSTTTTJTb: Sllttf (HUH: 26)

Inventors: DETWILER MICHAEL R, MCGUIRE FREDERICK D JR, DETWILER, MICHAEL, R., MCGUIRE, FREDERICK, D., JR.
Applicants: ALLIED SIGNAL INC, ALLIEDSIGNAL INC.
Application year: 1998
Main classification: C23C28
IPC codes: C23C28