INITIATORS FOR CARBOCATIONIC POLYMERIZATION OF OLEFINS

Abstract: A new class of initiators for inducing the cationic polymerization of olefins was discovered. These initiators, in conjunction with Lewis acids as coinitiators, effectively initiate the carbocationic polymerization of olefins. The new initiators are epoxides with general formula (I) where R1, R2 and R3 are hydrogen, alkyl, aryl or aralkyl groups, and can be the same or different, and i is a positive whole number. The Lewis acid has the general formula of MtXn where M is titanium, aluminum, boron or tin, X is a halogen, an alkyl or an alcoxy or a mixture thereof. The process is a carbocationic process, which can be living or non-living, at a temperature of from about 0 to -80 DEG C. The polymer produced can be a homo- or copolymer (random or block) carrying hydroxy functional groups.

Description: INITIATORS FOR CARBOCATIONIC POLYMERIZATION OF OLEFINS TECHNICAL FIELD This invention relates to carbocationic polymerization of olefins. BACKGROUND ART The carbocationic polymerization of olefins is well-known and has been studied in detail. These processes can be initiated by systems producing carbocations. These initiating systems include Lewis and Bronsted acids, organic compounds such as halides in conjunction with Lewis acids, etc. (J.P.Kennedy: Cationic Polymerization of Olefins: A Critical Inventory. Wiley-Intersci). These processes produce high or low molecular weight polymers with various halide or olefmic functional groups, and can be further functionalized by post-polymerization reactions. The living carbocationic polymerization of olefins such as isobutylene and styrene is a relatively new development. Prior art describes living carbocationic polymerizations producing polymers with controlled molecular weights and molecular weight distributions as low as M u /M n = 1.05 (see United States patent no. 5,169,914). Suitable initiators include compounds with tertiary functional groups of the general formula shown below: where R,, R 2 and R 3 can be hydrogen or aliphatic or aromatic alkyl groups, or aralkyl groups, and X can be a halogen, hydroxyl, ether or ester groups, or peroxides. These initiators, in conjunction with Lewis acids, Electron Pair Donors and Proton Traps, have successfully been used to produce homopolymers and random or block copolymers. The prior art has recently been reviewed in detail (Rubber Chem. Techn. 69, 462 (1996). Multifunctional initiators carrying the above described tertiary functional groups have also been used to produce multiarm-star branched polymers (J. Polymer Sci., Chem. Oct. 1997). The above discussed living initiating systems produce halide-functionalized polymers, which can be further modified to yield other functional groups such as hydroxy- or ester. Unfortunately, these initiators are usually not available commercially and have to be synthesized by multistep synthetic routes. DISCLOSURE OF INVENTION The inventor has discovered that epoxides, when reacted with Lewis acids in the presence of olefins such as isobutylene and styrene, effectively initiate the carbocationic polymerization of those olefins. Epoxides are commercially available or can be synthesized by oxidizing olefins by a simple and fast process (e. g., reacting the olefin with m-Cl-perbenzoic acid in a polar solvent at room temperature, completing the reaction in a few minutes. P.Dreyfuss and J.P.Kennedy: Analytical Chem. 47(4), 771 (1975)). Epoxides are known to undergo polymerization themselves, by cationic, anionic or coordination mechanism, to yield polyethers containing oxygen in the main chain. Epoxi-ethane undergoes living anionic polymerization yielding a polyether, but substituted epoxides suffer side reactions. (Encyclopaedia of Polymer Science and Engineering, 2 nd Ed. , Mark, Bikales, Overberger, Menges Eds., 14, 634, John Wiley&Sons, 1985). In the present invention, epoxides, preferably substituted epoxides, initiate the living polymerization of olefms yielding hydrocarbon polymers, instead of undergoing self- polymerization. Thus the epoxide initiating systems of the present invention produce hydrocarbon polymers with hydroxy functionality; multifunctional epoxides will produce multiple hydroxy functionalities. There is no prior art for using epoxides as initiators for the cationic polymerization of olefms. Thus according to one aspect of the invention, there is provided a carbocationic polymerization process for producing a polyolefm polymer or copolymer carrying oxygen-containing functional group(s) (e.g., hydroxy or aldehyde) group(s), which comprises introducing a monomer charge, a Lewis acid as coinitiator and an organic epoxide compound as initiator into a suitable reaction vessel and polymerizing the monomer charge at a temperature of from about 0 degrees to about -120 degrees centigrade to form the terminally functional polymer. The monomer charge comprises the concurrent and/or sequential addition of isobutylene and a second monomer selected from the group consisting of conjugated diolefins and vinylidene aromatic compounds, and the epoxide initiator is charged in an amount of from 10 "6 to about 10 "1 moles per mole of the isobutylene. According to another aspect of the invention, there is provided a living carbocationic polymerization process for producing a polyolefin polymer or copolymer carrying oxygen containing functional groups (e.g., hydroxy or aldehyde group(s)), which comprises introducing a monomer charge, a Lewis acid as coinitiator and an organic epoxide compound as initiator, a proton trap to prevent protic initiation, and an electron pair donor which may or may not be necessary to achieve living conditions, into a suitable reaction vessel and polymerizing the monomer charge at a temperature of from about 0 degrees to about -120 degrees centigrade to form the terminally functional polymer. The monomer charge comprises the concurrent and/or sequential addition of isobutylene and a second monomer selected from the group consisting of conjugated diolefins and vinylidene aromatic compounds and the epoxide initiator is charged in an amount of from 10 "6 to about 10 "1 moles per mole of the isobutylene. Another view of the invention is that it provides a new class of initiators for inducing the cationic polymerization of olefins. These initiators, in conjunction with Lewis acids as coinitiators, effectively initiate the carbocationic polymerization of olefins. The new initiators are epoxides with the general formula R, O I / V R, - [ C - C ], I R, where R, , R 2 and R 3 are hydrogen, alkyl, aryl or aralkyl groups, and can be the same or different, and i is a positive whole number. The Lewis acid has the general formula of MtX n where M is titanium, aluminum, boron or tin, X is a halogen, an alkyl or an alcoxy or a mixture thereof. The process is a carbocationic process, which can be living or non-living, at a temperature of from about 0 to -80 C. The polymer produced can be a homo- or copolymer (random or block) carrying hydroxy functional groups. Further aspects of the invention and additional details and examples will be provided or will become apparent in the detailed description which follows. BEST MODE FOR CARRYING OUT THE INVENTION Tertiary carbocations that are formed by the interaction of an initiator carrying a tertiary functional group, and a Lewis acid such as BC1 or TiCl 4 , were shown to be effective initiators for the carbocationic polymerization of olefms. Such an initiator is 2,4,4-trimethylpentyl chloride in conjunction with TiCl 4 In her search for commercially available initiators the inventor has theorized that substituted epoxides may be effective initiators for living carbocationic polymerizations. It is taught that epoxides may undergo cleavage under acidic or basic conditions, and the cleavage is oriented in substituted epoxides: (Morrison&Boyd: Organic Chemistry, 6 th Ed. , 483 Prentice Hall, 1992) CH 3 CH 3 CH 3 - C I - CH 2 = *>- CH 3 - C I - CH 2 - OH Epoxides are also known to polymerize to form poly ethers. This polymerization reaction forms the base of commodity bonding compounds such as epoxy resins. The challenge was to find conditions under which tertiary carbocations forming from a substituted epoxide in conjunction with a Lewis acid would initiate the carbocationic polymerization of olefins instead of undergoing self-polymerization. The inventor has found that compounds such as 2,4,4-trimethylpentyl-l,2-epoxide, as 2,4,4- trimethylpentyl-2,3-epoxide, alpha-methylstyrene epoxide and squalene epoxide in conjunction with a Lewis acid such as TiCl 4 are effective initiators for the polymerization of olefins such as isobutylene. Without wishing to be bound by the theory, initiation is proposed to take place by the following sequence of reactions: CH 3 CH 3 CH 3 CH 3 I excess TiCl 4 CH 3 - CH - CH 2 - C - CH 2 =» CH 3 - CH - CH 2 C -ι- / - TiClj (1) ol CH, - OTiC r I + + IB = PIB The carbocation initiates the polymerization of the olefin, or may undergo competititive self- polymerization. This latter side reaction may decrease the initiator efficiency, but the side product was found not to influence the living nature of the polymerization. Since opening the epoxi ring requires at least one TiCl 4 per epoxide ring, effective initiation was found to require the use of excess Lewis acid. Upon termination of the polymerization by methanol, the following reaction is proposed to take place: CH, CH 3 CH, - C (PIB) +/- TiCl 5 CH 3 - C (PIB) - Cl (2) CH, - OTiC CH, - OH The polymer formed will then contain one hydroxy head group and one chlorine end group. By the use of di- or multifunctional initiators, polymers carrying multiple hydroxi groups can be prepared in one step. The carbocationic polymerization of olefins is carried out at low temperature (-30 to -100 C) in a single solvent or solvent mixture of suitable polarity. Single solvent can be n-butylchloride, while mixed solvents contain a nonpolar component such as hexane and a polar component such as methylchloride. It is also taught by the prior art that internal or external electron pair donors have beneficial effects on the polymerization such as narrowing the molecular weight distribution or preventing side reactions . Without wishing to be bound by the theory it is proposed that the epoxide-based initiating systems behave like internal electron pair donors due to the presence of the oxygen. However, the addition of external electron pair donors such as DMA may be beneficial, but will slow down the polymerization. The epoxide initiators of the present invention can easily be synthesized from commercially available olefins, polyolefms or terpenes . For instance, 2,4,4-trimethylpentyl-l,2-epoxide was synthesized by reacting m-chloroperbenzoic acid with 2,4,4-trimethylpentene for 10 minutes at room temperature in methylene chloride solvent. Similarly, epoxidized alpha-methylstyrene and hexaepoxy squalene was synthesized by reacting alpha-methylstyrene and squalene with m- chloroperbenzoic acid for 10 minutes at room temperature in methylene chloride solvent. The products were characterized by NMR spectroscopy and were found to be fully epoxidized. The epoxides were found to be stable for a few months when stored in a refrigerator; after 4 months only one epoxide ring cleaved in the hexaepoxi squalene. These initiators then were used to initiate the carbocationic polymerization of isobutylene. The following examples describe the present invention. All polymerizations were carried out in a dry box under dry nitrogen, in a three-neck flask equipped with an overhead stirrer, immersed in a cooling bath at -80 C. EXAMPLE 1. The reaction vessel was charged with 50 ml hexane and cooled to -80 C. 54.9 ml condensed methyl chloride was added, followed by the addition of 0.07 ml (4x 10 "4 mol) alpha-methylstyrene epoxide as an initiator, 0.16 ml 2,6-di-tert-butylpyridine (DtBP) as a proton trap to prevent protic initiation, and 16 ml isobutylene (IB) as a monomer. The polymerization was started with the addition of 0.36 ml TiCl 4 . The monomer conversion was 70% in 120 minutes, yielding a polyisobutylene (PIB) with M n = 43,000 and M n /M w = 1.2. The incorporation of the aromatic initiator was verified by SEC coupled with UV spectroscopy. The polymerization was living; the M n increased linearly with conversion, and M n /M w decreased as expected. Table 1 lists the data. Table 1. IB polymerization initiated with epoxidized alpha-methylstyrene Time M n M n /M v 5 3900 1.7 10 6100 1.7 15 8000 1.6 20 10,500 1.5 30 15,000 1.4 60 27,000 1.3 120 43000 1.2 EXAMPLE 2. The reaction vessel was charged with 50 ml hexane and cooled to -80 C. 33.4 ml condensed methyl chloride was added, followed by the addition of 0.73 ml (5.4x10 "4 mol) 2,4,4- trimethylpentyl- 1 -epoxide as an initiator, 0.2 ml 2,6-di-tert-butylpyridine (DtBP) as aproton trap to prevent protic initiation, and 13,8 ml isobutylene (IB) as a monomer. The polymerization was started with the addition of 0.13 ml TiCl 4 . The monomer conversion was complete in 40 minutes, yielding a polyisobutylene (PIB) with M n = 64,000 and M n /M w = 1.1. EXAMPLE 3. The reaction vessel was charged with 50 ml hexane and cooled to -80 C. 33.4 ml condensed methyl chloride was added, followed by the addition of 0.07 ml (4x 10 "4 mol) alpha-methylstyrene epoxide as an initiator, 0.2 ml 2,6-di-tert-butylpyridine (DtBP) as a proton trap to prevent protic initiation, and 16 ml isobutylene (IB) as a monomer. The polymerization was started with the addition of 0.5 ml TiCl 4 . The monomer conversion was 80 in 30 minutes, yielding a polyisobutylene (PIB) with M n = 66,000 and M n /M w = 1.3. The polymerization was living; M n increased linearly with conversion and M n /M w decreased as expected. Table 2 summarizes the data: Table 2. IB polymerization initiated with epoxidized alpha-methylstyrene Time M n M n /M w 2 15,000 1.6 4 25,000 1.4 6 35,000 1.3 8 43,000 1.3 10 49,000 1.3 20 64,000 1.3 30 66,000 1.3 EXAMPLE 4. The reaction vessel was charged with 50 ml hexane and cooled to -80 C. 34 ml condensed methyl chloride was added, followed by the addition of 0.7 ml (4x10 "3 mol) alpha-methylstyrene epoxide as an initiator, 0.16 ml 2,6-di-tert-butylpyridine (DtBP) as a proton trap to prevent protic initiation, and 16 ml isobutylene (IB) as a monomer. The polymerization was started with the addition of 0.72 ml TiCl 4 . The monomer conversion was 70% in 30 minutes, yielding a polyisobutylene (PIB) with M n = 11,000 and M n /M w = 1.2. The incorporation of the aromatic initiator was verified by SEC coupled with UV spectroscopy. This polymer was also subjected to GC-MS analysis, which yielded oxygen-containing aromatic residues. This indicates that the headgroup of the polymer contains oxygen as shown in reaction (2). EXAMPLE 5. The reaction vessel was charged with 153 ml methylcyclohexane and cooled to -80 C. 60 ml condensed methyl chloride was added, followed by the addition of 5x10 "4 mol hexaepoxy squalene as an initiator, 0.32 ml 2,6-di-tert-butylpyridine (DtBP) as a proton trap to prevent protic initiation, and 60 ml isobutylene (IB) as a monomer. The polymerization was started with the addition of 3x10 "2 mol TiCl 4 . The monomer conversion was 100% in 20 minutes, yielding a polyisobutylene (PIB) with M„ = 115,000 and M n /M w = 1.2 by SEC-Multiangle Light Scattering (MLS) analysis. The slope of the radius of gyration vs molecular weight plot was found to be 0.33, indicating that the polymer has a star-branched structure (spherical shape). Assuming six arms, each arm would have M n = 20,000- EXAMPLE 6. The reaction vessel was charged with 153 ml methylcyclohexane and cooled to -80 C. 60 ml condensed methyl chloride was added, followed by the addition of 4.5xl0 ~5 mol hexaepoxy squalene as an initiator, 0.32 ml 2,6-di-tert-butylpyridine (DtBP) as a proton trap to prevent protic initiation, and 43 ml isobutylene (IB) as a monomer. The polymerization was started with the addition of 2xl0 "2 mol TiCl 4 . The monomer conversion was 55% in 480 minutes, yielding a polyisobutylene (PIB) with M n = 174,000 and M n /M w = 1.2 by SEC-MLS. The radius of gyration vs molecular weight plot yielded a slope of 0.32, indicating a spherical shape star- branched polymer. Assuming 6 arms, each arm would have an M n = 30,000- EXAMPLE 7. The reaction vessel was charged with 153 ml methylcyclohexane and cooled to -80 C. 60 ml condensed methyl chloride was added, followed by the addition of 5x10 4 mol hexaepoxy squalene as an initiator, 0.32 ml 2,6-di-tert-butylpyridine (DtBP) as a proton trap to prevent protic initiation, and 43 ml isobutylene (IB) as a monomer. The polymerization was started with the addition of 3x10 2 mol TiCl 4 . The reaction was allowed to proceed for 250 minutes, at which point 0.32 ml DtBP and 0.001 mol dimethyl acetamide DMA as an Electron Pair Donor ED were added to the mixture, followed by the addition of the prechilled mixture of 9.6 g distilled styrene and 10 g methylcyclohexane. The reaction was allowed to proceed for 20 minutes, at which point methanol was added to terminate the polymerization. NMR analysis of the product showed the presence of 10.2 mol% (17.4 wt%) styrene in the block. The isobutylene conversion was found to be 78% in 35 minutes. The polyisobutylene (PIB) had M n = 106,700 and M n /M w = 1.4, measured just before the styrene incorporation by standard SEC with universal calibration. The final product had M n = 125,000 and M n /M w = 1.2, measured by SEC-MLS. The radius of gyration vs molecular weight plot yielded a slope of 0.4, indicating a star-branched block copolymer with spherical shape. Assuming six arms, each arm should have a polyisobutylene section with M n = 18,000 and a polystyrene section with M n = 2900. INDUSTRIAL APPLICABILITY The invention provides an improved process for producing polyolefin polymers or copolymers carrying one or more oxygen-containing functional groups, and such polyolefin polymers or copolymers themselves .

Claims: CLAIMS: 1. A carbocationic polymerization process for producing a polyolefin polymer or copolymer carrying oxygen-containing functional group(s) (e.g., hydroxy or aldehyde) group(s), which comprises introducing a monomer charge, a Lewis acid as coinitiator and an organic epoxide compound as initiator into a suitable reaction vessel and polymerizing the monomer charge at a temperature of from about 0 degrees to about -120 degrees centigrade to form said terminally functional polymer, wherein said monomer charge comprises the concurrent and/or sequential addition of isobutylene and a second monomer selected from the group consisting of conjugated diolefins and vinylidene aromatic compounds and said epoxide initiator is charged in an amount of from 10 ~6 to about 10 "1 moles per mole of said isobutylene. 2. The process of Claim 1 , wherein said monomer charge is polymerized at a temperature of from about -40 to about -80 C. 3. The process of Claim 2 wherein said organic epoxide compound is selected from the group of substituted epoxides. 4. The process of Claim 3 wherein said substituted epoxide is selected from the group of epoxidized aliphatic olefins. 5. The process of Claim 4 wherein said epoxide compound is 2,4,4-trimethyl-pentyl- epoxide. 6. The process of Claim 3 wherein said substituted epoxide is selected from the group of epoxidized aralkyl compounds. 7. The process of Claim 6 wherein said epoxide is alpha-methylstyrene epoxide. 8. The process of Claim 3 wherein said substituted epoxide is selected from the group of epoxidized polyolefms such as synthetic or natural polyisoprenes (terpenes). 9. The process of Claim 8 whereing said epoxide is squalene hexaepoxide. 10. The process of Claim 3 wherein the second or subsequent components of the monomer charge comprises a C4 to C8 diolefin in an amount of up to 60% of the monomer charge. 11. The process of Claim 3 wherein the second or subsequent components of the monomer charge comprises a C8 to C20 vinylidene aromatic compound in an amount of up to 100% of the monomer charge. 12. The process of Claim 11 wherein said vinylidene aromatic monomer is selected from the group of styrene, p-methylstyrene and indene. 13. The process of Claim 3 wherein said Lewis acid is selected from the group consisting of BC1 3 , TiCl 4 , A1C1 3 , VC1 4 , FeCl 3 , SnCl 4 , SbF 6 , ZnCl 2 , and BF 3 . 14. The process of Claim 13 wherein said Lewis acid is TiCl 4 . 15. The process of Claim 3, conducted in the presence of a diluent. 16. The process of Claim 15 where said diluent is selected from the group consisting of Cl to C6 halogenated hydrocarbons, C3 to C8 aliphatic hydrocarbons C5 to CIO cyclic hydrocarbons, mixtures of said halogenated hydrocarbons and one of said aliphatic hydrocarbons, and mixtures of said halogenated hydrocarbons and one of said cyclic hydrocarbons. 17. The process of Claim 16, wherein said diluent is selected from methyl chloride, methylene chloride, n-butylchloride, hexane, methylcyclohexane and mixtures thereof. 18. The process of Claim 3, wherein said monomer charge comprises the sequential or concurrent addition of isobutylene and a second or subsequent monomer(s) selected from the group consisting of isoprene, styrene, p-methylstyrene and indene, the amount of second or subsequent monomer(s) being up to 100% of the charge, aid Lewis acid is TiCl 4 , said organic epoxide compound is selected from the group consisting 2,4,4-trimethyl-pentyl-epoxide, alpha- methylstyrene epoxide and squalene hexaepoxide, said Lewis acid being from about 2 to about 100 moles per mole of epoxi compound, and the diluent selected from the group of consisting methyl chloride, hexane, methylcyclohexane and mixtures thereof. 19. A living carbocationic polymerization process for producing a polyolefin polymer or copolymer carrying oxygen containing functional groups (e.g., hydroxy or aldehyde group(s)), which comprises introducing a monomer charge, a Lewis acid as coinitiator and an organic epoxide compound as initiator, a proton trap to prevent protic initiation, and an electron pair donor which may or may not be necessary to achieve living conditions, into a suitable reaction vessel and polymerizing the monomer charge at a temperature of from about 0 degrees to about -120 degrees centigrade to form said terminally functional polymer, wherein said monomer charge comprises the concurrent and/or sequential addition of isobutylene and a second monomer selected from the group consisting of conjugated diolefins and vinylidene aromatic compounds and said epoxide initiator is charged in an amount of from 10 "6 to about 10 "1 moles per mole of said isobutylene. 20. The process of Claim 19, wherein said monomer charge is polymerized at a temperature of from about -40 to about -80 C. 21. The process of Claim 20 wherein said organic epoxide compound is selected from the group of substituted epoxides. 22. The process of Claim 21 wherein said substituted epoxide is selected from the group of epoxidized aliphatic olefins. 23. The process of Claim 22 wherein said epoxide compound is 2,4,4-trimethyl- pentyl-epoxide. 24. The process of Claim 21 wherein said substituted epoxide is selected from the group of epoxidized aralkyl compounds. 25. The process of Claim 24 wherein said epoxide is alpha-methylstyrene epoxide. 26. The process of Claim 21 wherein said substituted epoxide is selected from the group of epoxidized polyolefins such as synthetic or natural polyisoprenes (terpenes). 27. The process of Claim 26 whereing said epoxide is squalene hexaepoxide. 28. The process of Claim 21 wherein the second or subsequent components of the monomer charge comprises a C4 to C8 diolefin in an amount of up to 60% of the monomer charge. 29. The process of Claim 21 wherein the second or subsequent components of the monomer charge comprises a C8 to C20 vinylidene aromatic compound in an amount of up to 100% of the monomer charge. 30. The process of Claim 29 wherein said vinylidene aromatic monomer is selected from the group of styrene, p-methylstyrene and indene. 31. The process of Claim 21 wherein said Lewis acid is selected from the group consisting of BC1 3 , TiCl 4 , A1C1 3 , NC1 4 , FeCl 3 , SnCl 4 , SbF 6 , ZnCl 2 , and BF 3 . 32. The process of Claim 31 wherein said Lewis acid is TiCl 4 . 33. The process of Claim 21 , conducted in the presence of a diluent. 34. The process of Claim 33 where said diluent is selected from the group consisting of Cl to C6 halogenated hydrocarbons, C3 to C8 aliphatic hydrocarbons C5 to CIO cyclic hydrocarbons, mixtures of said halogenated hydrocarbons and one of said aliphatic hydrocarbons, and mixtures of said halogenated hydrocarbons and one of said cyclic hydrocarbons. 35. The process of Claim 34, wherein said diluent is selected from methyl chloride, methylene chloride, n-butylchloride, hexane, methylcyclohexane and mixtures thereof. 36. The process of Claim 21 wherein said proton trap is 2,6-di-tert.-butylpyridine. 37. The process of claim 21 wherein said electron pair donor is selected from the group consisting of dimethylacetamide, dimethylformamide, pyridine and substituted pyridines. 38. The process of Claim 21, wherein said monomer charge comprises the sequential or concurrent addition of isobutylene and a second or subsequent monomer(s) selected from the group consisting of isoprene, styrene, p-methylstyrene and indene, the amount of second or subsequent monomer(s) being up to 100% of the charge, aid Lewis acid is TiCl 4 , said organic epoxide compound is selected from the group consisting 2,4,4-trimethyl-pentyl-epoxide, alpha- methylstyrene epoxide and squalene hexaepoxide, said Lewis acid being from about 2 to about 100 moles per mole of epoxi compound, and the diluent selected from the group of consisting methyl chloride, hexane, methylcyclohexane and mixtures thereof. 39. A linear or star-branched polyolefin homo- and/or copolymer (random and/or block) produced by the process of Claim 3, containing one or more oxygen containing (e.g., hydroxy or aldehyde) functionality(s). 40. A linear or star-branched polyolefin homo- and/or copolymer (random and/or block) produced by the process of Claim 21, containing one or more oxygen containing (e.g., hydroxy or aldehyde) functionality(s). 41. A polyisobutylene polymer produced by the process of Claim 3 , containing one or more oxygen containing functional group such as primary hydroxy group at one end and one or more tertiary chloride group at the other end of the polymer. 42. A polyisobutylene polymer produced by the process of Claim 23, containing one oxygen containing group such as primary hydroxy group at one end and one tertiary chloride group at the other end of the polymer. 43. A polyisobutylene polymer produced by theprocess of Claim 25, containing one oxygen containing group such as primary hydroxy group attached to the aromatic alpha- methylstyrene initiator moiety at one end and one tertiary chloride group at the other end of the polymer. 44. A star-branched polyisobutylene polymer produced by the process of Claim 27, containing six oxygen containing groups such as primary hydroxy groups attached to the squalene multifunctional initiator moiety at the core of the polymer, and six tertiary chloride groups at the end of the arms of the star polymer. 45. A star-branched polyisobutylene-poly(vinylidene aromatic) block copolymer produced by the process of Claim 27, containing six oxygen containing groups such as primary hydroxy groups attached to the squalene multifunctional initiator moiety at the core of the polymer, and six tertiary chloride groups at the end of the arms of the star block copolypolymer. 46. A polyolefin homo- and/or copolymer (random and/or block) containing one or more oxygen containing (e.g., hydroxy or aldehyde) functionality(s). 47. A polyisobutylene polymer containing one or more oxygen containing group(s) (e.g., primary hydroxy or aldehyde) at one end and one or more tertiary chloride group at the other end of the polymer. 48. A polyisobutylene polymer containing one oxygen containing group (e.g., primary hydroxy or aldehyde) at one end and one tertiary chloride group at the other end of the polymer. 49. A polyisobutylene polymer containing one oxygen containing group (e.g., primary hydroxy or aldehyde) attached to the aromatic alpha-methylstyrene initiator moiety at one end and one tertiary chloride group at the other end of the polymer. 50. A star-branched polyisobutylene polymer containing six oxygen containing groups (e.g., primary hydroxy or aldehyde) attached to the squalene multifunctional initiator moiety at the core of the polymer, and six tertiary chloride groups at the end of the arms of the star polymer. 51. A star-branched polyisobutylene-polystyrene block copolymer containing six oxygen containing groups (e.g., primary hydroxy or aldehyde) attached to the squalene multifunctional initiator moiety at the core of the polymer, and six tertiary chloride groups at the end of the arms of the star block copolypolymer. 52. A polyolefin homo- and/or copolymer (random and/or block) containing one or more oxygen containing group(s) (e.g., primary hydroxy or aldehyde)hydroxy functionality(s), with an M n from about 500 to about 5x10 6 , and a molecular weight distribution MWD from about 1.01 to about 3. 53. A polyisobutylene polymer containing one or more one oxygen containing group(s) (e.g., primary hydroxy or aldehyde) at one end and one or more tertiary chloride group at the other end of the polymer with an M n from about 500 to about 5xl0 6 , and a molecular weight distribution MWD from about 1.01 to about 3. 54. A polyisobutylene polymer containing one oxygen containing group (e.g., primary hydroxy or aldehyde) at one end and one tertiary chloride group at the other end of the polymer with an M n from about 500 to about 5xl0 6 , and a molecular weight distribution MWD from about 1.01 to about 3. 55. A polyisobutylene polymer containing one one oxygen containing group (e.g., primary hydroxy or aldehyde) attached to the aromatic alpha-methylstyrene initiator moiety at one end and one tertiary chloride group at the other end of the polymer with an M n from about 500 to about 5xl0 6 , and a molecular weight distribution MWD from about 1.01 to about 3. 56. A six-arm star-branched polyisobutylene polymer containing six oxygen containing groups (e.g., primary hydroxy or aldehyde) attached to the squalene multifunctional initiator moiety at the core of the polymer, and six tertiary chloride groups at the end of the arms of the star polymer with an M n from about 500 to about 5x10 6 , and a molecular weight distribution MWD from about 1.01 to about 3. 57. A six-arm star-branched polyisobutylene-polystyrene block copolymer containing six oxygen containing groups (e.g., primary hydroxy or aldehyde) attached to the squalene multifunctional initiator moiety at the core of the polymer, and six tertiary chloride groups at the end of the arms of the star block copolymer, with an M n from about 500 to about 5xl0 6 , and a molecular weight distribution MWD from about 1.01 to about 3.

Inventors: PUSKAS JUDIT E, PUSKAS, JUDIT, E.
Applicants: UNIV WESTERN ONTARIO, THE UNIVERSITY OF WESTERN ONTARIO
Application year: 1998
Main classification: C08F10
IPC codes: C08F2, C08F4, C08F10, C08F297