Siloxane-modified polyamideimide resin composition adhesive film, adhesive sheet and semiconductor device

Abstract: Adhesive film useful for the production of semiconductor devices is produced from a siloxane-modified polyamideimide resin composition, comprising 100 parts by weight of a siloxane-modified polyamideimide resin and 1 to 200 parts by weight of a thermosetting resin ingredient.

Description: BACKGROUND OF THE INVENTION (a) Field of the Invention The present invention relates to a siloxane-modified polyamideimide resin composition and an adhesive film. The present invention further relates to a siloxane-modified polyamideimide resin useful for the siloxane-modified polyamideimide resin composition, and to varnish containing the siloxane-modified polyamideimide resin and composition. (b) Description of the Related Art Polyamideimide resins are mainly used for wire coating (heat-resistant enamel wire) because they are excellent in electrical properties, heat resistance, mechanical properties and abrasion resistance. However, the high boiling solvents that are usually used for the production of polyamideimide resins have hindered forming film or sheet of polyamideimide resins. For example, they need time-consuming drying at low temperatures of 150°C or lower, and the resulting film or sheet still contains at least 10% by weight of residual volatile matters. Even by drying at high temperatures above 150°C, it is difficult to produce sheets of above 100 µm thick containing not more than 5% by weight of residual volatile matters. Further, when resin compositions comprising polyamideimide resins and thermosetting resin ingredients are dried at high temperatures to produce sheets, thermal cure proceeds excessively, to make the production of B-stage sheets difficult. An application of polyamideimide resins is the production of interlaminar adhesive films for wiring boards, which are films or sheets formed by applying resin compositions comprising polyamideimide resins and thermosetting resin ingredients on appropriate substrates. The desirable content of residual volatile matters in such films and sheets is 5% by weight or less, preferably 1% by weight or less. In films and sheets containing much volatile matters, voids or bubbles may be produced during processing with heat, such as press, bonding with heat and pressure or lamination, or thermal after-cure, which deteriorate insulating properties. In addition, such films and sheets must preserve their flowability to adhere to the substrates of printed circuit boards or to fill the depressions of the thickness of the copper foil made in the circuits. Therefore, drying of coating must be carried out at low temperatures so as not to cause thermal cure. It is desirable to decrease the residual volatile matters in sheets of any thickness, for example thick sheets above 100 µm thick. It is also desirable that the films or sheets of the resin compositions strongly adhere to the substrates. In LSI-packaging technology, CSP's (chip-size-packages) have been popularized, which permit reducing the mounting area of LSI to chip sizes. CSP's have short wiring length, and produce little inductance. Therefore, they can speed up and improve the performances of LSI's, and are advantageously applied in recent cellar telephones and video cameras, and further in the DRAM of personal computers. There are various types of CSP's, including the wire-bonding type, the ceramics type, the through-hole type and the µBGA type. Wire-bonding-type CSP's are produced by connecting chips to polyimide wiring boards by wire bonding followed by sealing with resins. CSP's of this type have simple structures and can be produced by modification of the conventional BGA techniques, and are expected to be the main current of CSP's with up to 100 small pins. For example, CSP boards for wire-bonding type are produced by initially making through-holes, such as solder ball holes, in polyimide substrates coated with adhesives which can adhere to copper foil on heating, followed by lamination of copper foil by pressing or the like, circuit forming and gold plating. As the adhesives for bonding polyimide substrates and copper foil, epoxy resins, polyamic acids and mixtures of polyamic acids and bismaleimides have been used, while polyamideimide resins have been used mainly as wire coating materials because of the excellent electrical properties, heat resistance, mechanical properties and abrasion resistance. As CSP's have been downsized and the number of pins has increased, the circuit of CSP boards has become finer, requiring heat resistant adhesives which adhere to copper more strongly. Conventional epoxy resin adhesives have poor resistance against wire-bonding or solder reflow owing to lack of heat resistance. Polyamic acids and mixtures thereof with bismaleimides have excellent heat resistance, but need high curing temperatures of 300 to 400°C, and their adhesion to copper foil or molded resin is insufficient. An object of the present invention is to provide a siloxane-modified polyamideimide resin composition, which can form films containing little residual volatile matters, has high adhesion strength, appropriate flowability and superior heat resistance, strongly adheres to polyimide base layer and copper foil, exhibits excellent resistance to PCT (pressure cooker test) and, therefore, is useful for the production of interlaminar adhesive film for wiring boards. Another object of the present invention is to provide an adhesive film, produced by using the siloxane-modified polyamideimide resin composition. Another object of the present invention is to provide a siloxane-modified polyamideimide resin useful for the preparation of the siloxane-modified polyamideimide resin composition. Another object of the present invention is to provide a varnish containing the siloxane-modified polyamideimide resin or composition. Polyamideimide resins are typically produced by the isocyanate method comprising the reaction of trimellitic anhydride with aromatic diisocyanates, or by the acid chloride method comprising the reaction of aromatic diamines with trimellitic chloride followed by reaction with aromatic diisocyanates. The kinds and properties of the polyamideimide resins obtainable by the diisocyanate method are limited owing to the scarcity of the kinds of commercially available industrial aromatic diisocyanates. On the other hand, the acid chloride method needs a purification process for removing the by-product HCl, and therefore is disadvantageously costly. Japanese Patent Application Unexamined Publication No. 3-181511 discloses the production of polyamideimide resins by a two-step method comprising the reaction of aromatic tricarboxylic anhydrides with excess diamines having ether bonds, followed by reaction with diisocyanates. Japanese Patent Application Unexamined Publication No. 4-182466 discloses the production of diimidodicarboxylic acids of high purity by the reaction of aromatic diamines with trimellitic anhydride. If combined with the reaction of the product diimidodicarboxylic acids with diisocyanates, this method may enable easy production of substantially by-product-free polyamideimide resins of high molecular weights from various kinds of diamines, since it does not produce the by-product HCl that is formed in the acid chloride method. Polydimethylsiloxanes consist of highly ionic, cohesive main chains and nonionic and less cohesive side chains, and when there is no action except the interaction between polymers, they are known to have helical structure, with the siloxane bonds directed inward. It is also known that introducing siloxane structures into polymers enlarges the space occupied by polymer molecules due to the helical structure of the siloxane parts, thereby increasing the gas permeability of the polymers. Siloxane structures are also expected to improve resin properties including elasticity and flexibility because they are scarcely interactive each other in spite of their vigorous vibration with heat. If siloxane structures can be introduced into inherently heat resistant polyamideimide resins by the industrially advantageous isocyanate method, it will be possible to produce heat resistant polymers of various properties and improve the drying efficiency of polyamideimide resins, which are usually produced by using high boiling solvents. However, there have been proposed no method of producing high molecular weight polymers. The method disclosed in Japanese Patent Application Unexamined Publication No. 3-181511, wherein aromatic tricarboxylic anhydrides are allowed to react with excess diamines having ether bonds followed by reaction with diisocyanates, needs dehydration agents because the first reaction stage requires not only the reaction of acid anhydrides with amino groups but also the reaction of carboxylic acid with amino groups. Therefore, oligomerization occurs even in the first reaction stage, and, in the second reaction stage, various competing reactions occur between oligomers of different molecular weights and diisocyanates, to form by-products. It is therefore impossible to produce polyamideimide resins having sufficiently high molecular weight. If the diimidodicarboxylic acids produced by the method disclosed in Japanese Patent Application Unexamined Publication No. 4-182466 are allowed to react with diisocyanates, polyamideimides of desired properties will be obtainable by using various commercial aromatic diamines, and the absence of the by-product HCl formed in the acid chloride method will facilitate the production procedure. However, as taught in Japanese Patent Application Unexamined Publication No. 4-182466, the diimidodicarboxylic acids produced from diamines having two or less aromatic rings are insoluble in the solvents used for synthesis, and must be filtered previous to succeeding reactions, causing a costly increase of filtration or purification steps. Another drawback is that the purified diimidodicarboxylic acids have low solubility, so that the molecular weights of the reaction products thereof with aromatic diisocyanates are too low to produce film from varnish thereof. According to an improved method, high molecular weight polyamideimide resins are produced by allowing diamines having three or more aromatic rings with trimellitic anhydride in the coexistence of aprotic polar solvents and aromatic hydrocarbons azeotropic with water, to remove the by-product water by distillation, and then allowing the obtained aromatic diimidodicarboxylic acids with diisocyanates. However, when the diamines are partially replaced by siloxanediamines, this method could not produce siloxane-modified polyamideimide resins having sufficiently high molecular weights. To solve the problem, we have studied to provide a method whereby high molecular weight siloxane-modified polyamideimide resins can be produced without filtration steps, and have completed the present invention. SUMMARY OF THE INVENTION The present invention provides a siloxane-modified polyamideimide resin, which is produced by allowing a mixture (X) comprising a diamine (A) having three or more aromatic rings per molecule and a siloxanediamine (B) to react with trimellitic anhydride (C) to form a diimidodicarboxylic acid mixture (Y) comprising an aromatic diimidodicarboxylic acid derived from the diamine (A) and a siloxanediimidodicarboxylic acid derived from the siloxanediamine (B), and allowing the diimidodicarboxylic acid mixture (Y) to react with an aromatic diisocyanate (D). The present invention also provides a siloxane-modified polyamideimide resin composition, comprising 100 parts by weight of the siloxane-modified polyamideimide resin and 1 to 200 parts by weight of a thermosetting resin ingredient. The present invention further provides a varnish containing the siloxane-modified polyamideimide resin or composition of the present invention. The present invention further provides an adhesive film which is made from the siloxane-modified polyamideimide resin composition of the present invention by applying a varnish of the siloxane-modified polyamideimide resin composition on a supporting substrate. BRIEF DESCRIPTION OF THE DRAWINGS Fig. 1 is a graph showing the percentage of the siloxanediamine in all diamines used in each of Examples 1, 4, 5 and 6 and the amount of the solvents remaining in the siloxane-modified polyamideimide film of each Example. Fig. 2 is a graph showing the difference in drying speed between a polyamideimide resin containing no siloxane units and the siloxane-modified polyamideimide resin produced in Example 3. Fig. 3 is a graph showing the correlation in Examples 15 and 19 and Comparative Example 1 between the time of drying to produce film of 120 µm thick and the percentage of residual volatile matters. Fig. 4 is a graph showing the Tg of the cured films produced from the varnishes of Example 15 and Comparative Example 2. DESCRIPTION OF THE PREFERRED EMBODIMENTS The siloxane-modified polyamideimide resin composition (also referred to herein as "resin composition") comprises 100 parts by weight of the siloxane-modified polyamideimide resin of the invention and 1 to 200 parts by weight of a thermosetting resin ingredient. It permits fast evaporation of varnish solvents and reduction of residual volatile matters to 5% by weight or less even in thick film, and can produce adhesive film exhibiting good adhesion to substrates. The siloxane-modified polyamideimide resin useful for the resin composition of the present invention is produced by allowing a mixture (X) comprising a diamine (A) having three or more aromatic rings per molecule and a siloxanediamine (B) to react with trimellitic anhydride (C) to form a diimidodicarboxylic acid mixture (Y) containing an aromatic diimidodicarboxylic acid derived from the diamine (A) and a siloxanediimidodicarboxylic acid derived from the siloxanediamine (B), and allowing the diimidodicarboxylic acid mixture (Y) to react with an aromatic diisocyanate (D). The preferred among the siloxane-modified polyamideimide resins of the present invention are siloxane-modified polyamideimide resins which are produced by allowing a mixture (X) comprising a diamine (A) having three or more aromatic rings per molecule and a siloxane diamine (B) to react with trimellitic anhydride (C) to form a diimidodicarboxylic acid mixture (Y) containing an aromatic diimidodicarboxylic acid of the general formula (1) and a siloxanediimidodicarboxylic acid of the general formula (2), and allowing the diimidodicarboxylic acid mixture (Y) to react with an aromatic diisocyanate (D) of the general formula (3): wherein R 1 is and X is or wherein R 2 is wherein R 3 and R 4 are each a divalent organic group, R 5 to R 8 are each an alkyl group, phenyl or a substituted phenyl, and n is an integer of 1 to 50, OCN-R 9 -NCO wherein R 9 is Allowing the mixture (X) comprising the diamines (A) having three of more aromatic rings (A) and the siloxanediamine (B) with trimellitic anhydride (C) improves the production efficiency because the resulting diimidodicarboxylic acid mixture (Y) also has good solubility and can react with the aromatic diisocyanate (D) in a solution state. The more preferred among those are siloxane-modified polyamideimide resins which are produced by allowing the mixture (X) comprising the diamine (A) and the siloxane diamine (B) in a molar ratio (A)/(B) of 99.9/0.1 to 0.1/99.9 to react with trimellitic anhydride (C) in a molar ratio {(A)+(B)}/(C) of 1/2.05 to 1/2.20 to form the diimidodicarboxylic acid mixture (Y) containing the aromatic diimidodicarboxylic acid of the general formula (1) and the siloxanediimidodicarboxylic acid of the general formula (2), and allowing the diimidodicarboxylic acid mixture (Y) to react with the aromatic diisocyanate (D) of the general formula (3) in a molar ratio of {(A)+(B)}/(D) of 1/1.05 to 1/1.50. By using the diamine (A), the siloxanediamine (B), trimellitic anhydride (C) and the aromatic diisocyanate (D) in the ratios described above, siloxane-modified polyamideimide resins of high molecular weights can be produced without catalysts or the like. In the mixture (X), the molar ratio of the diamine (A) to the siloxanediamine (B) is preferably (A)/(B)=90/10 - 30/70, more preferably (A)/(B)=85/15 - 45/55. The molar ratio of {(A)+(B)}/(C) is preferably 1/2.07 - 1/2.15, more preferably 1/2.08 - 1/2.12. The molar ratio of {(A)+(B)}/(D) is preferably 1/1.10 - 1/1.50, more preferably 1/1.20 - 1/1.30. An example of the diimidodicarboxylic acid mixture (Y) is a mixture (Y') containing 2,2-bis[4-{4-(5-hydroxycarbonyl-1,3-dione-isoindorino)phenoxy}phenyl]propane and bis(5-hydroxycarbonyl-1,3-dione-isoindorino)propylpolydimethylsiloxane, which is produced by allowing a mixture (X') comprising 2,2-bis[4-(4-aminophenoxy)phenyl]propane as the diamine (A) and a diaminopolydimethylsiloxane as the siloxanediamine (B) to react with trimellitic anhydride (C). An example of the siloxane-modified polyamideimide resins of the present invention is produced by allowing the mixture (Y') with 4,4'-diphenylmethane diisocyanate as the aromatic diisocyanate (D). The siloxane-modified polyamideimide resin of the present invention is preferably produced by allowing the mixture (X) comprising the diamine (A) having three or more aromatic rings per molecule and the siloxane diamine (B) in a molar ratio (A)/(B) of 99.9/0.1 to 0.1/99.9 to react with trimellitic anhydride (C) in a molar ratio {(A)+(B)}/(C) of 1/2.05 to 1/2.20 in the presence of an aprotic polar solvent at 50 to 90°C, then at 120 to 180°C after addition of 10 to 50% by weight, based on the aprotic polar solvent, of an aromatic hydrocarbon which is azeotropic with water, to form the diimidodicarboxylic acid mixture (Y) containing the aromatic diimidodicarboxylic acid derived from the diamine (A) and the siloxanediimidodicarboxylic acid derived from the siloxanediamine (B), and allowing the diimidodicarboxylic acid mixture (Y) to react with the aromatic diisocyanate (D). After the production of the diimidodicarboxylic acid mixture (Y), the aromatic hydrocarbon is preferably removed from the mixture (Y) by distillation or the like prior to the reaction of the mixture (Y) with the aromatic diisocyanate (D). The product siloxane-modified polyamideimide resin may be dissolved in aprotic polar solvents to use it as varnish for various applications. Herein, examples of the divalent organic groups represented by R 3 and R 4 are alkylenes of 1 to 9 carbon atoms, arylenes of 6 to 10 carbon atoms and aralkylenes of 8 to 12 carbon atoms, including methylene, ethylene, propylenes, such as trimethylene, butylenes, such as tetramethylene and 2-methyl-1,3-propylene, methylphenylene, xylylene, methylxylylene and 2-phenyl-1,3-propylene. The particularly preferred among these is trimethylene because of the easy availability of the siloxanediamines. Examples of the alkyls represented by R 5 -R 8 include alkyls of 1 to 3 carbon atoms, and examples of the substituents on the substituted phenyls include alkyls of 1 to 3 carbon atoms, and the number of the substituents is preferably 1 to 3. "n" is an integer of 1 to 50, preferably 8 to 25. Examples of the diamines (A) having three or more aromatic rings, which are useful in the present invention, include those represented by the following general formula (4): H 2 N-R 1 -NH 2 wherein R 1 is and X is or Typical examples of such aromatic diamines (A) include 2,2-bis[4-(4-aminophenoxy)phenyl]propane (abbreviated, herein, to "BAPP"), bis[4-(3-aminophenoxy)phenyl]sulfone, bis[4-(4-aminophenoxy)phenyl]sulfone, 2,2-bis[4-(4-aminophenoxy)phenyl]hexafluoropropane, bis[4-(4-aminophenoxy)phenyl]methane, 4,4'-bis(4-aminophenoxy)biphenyl, bis[4-(4-aminophenoxy)phenyl] ether, bis[4-(4-aminophenoxy)phenyl] ketone, 1,3-bis(4-aminophenoxy)benzene, and 1,4-bis(4-aminophenoxy)benzene. These aromatic diamines (A) may be used individually or in combination of two or more. BAPP is particularly preferable to produce polyamideimide resins having balanced properties with low cost. Examples of the siloxanediamines (B) useful in the present invention include those represented by the following general formula (5): wherein R 3 and R 4 are each a divalent organic group, R 5 to R 8 are each an alkyl group, phenyl or a substituted phenyl, and n is an integer of 1 to 50. Typical examples of such siloxanediamines are those represented by the following formulae (6), (7) and (8): wherein n is an integer of 1 to 50. The amine-endcapped dimethylsiloxanes of the formula (6) are marketed as amino-modified reactive silicone oils under the trade names of X-22-161AS (amine equivalent weight: 450), X-22-161A (amine equivalent weight: 840), X-22-161B (amine equivalent weight: 1500) (all produced by Sin-Etsu Chemical Co., Ltd.), BY16-853 (amine equivalent weight: 650), BY16-853B (amine equivalent weight: 2200) (all produced by Dow Corning Toray silicone Co., Ltd.). The mixture (X) of the diamine (A) having three or more aromatic rings and the siloxanediamine (B) is allowed to react with trimellitic anhydride (C) (abbreviated, hereinafter, to "TMA"). The aprotic polar solvent and the aromatic hydrocarbon that is azeotropic with water must be non-reactive with the diamine (A), the siloxanediamine (B) and TMA (C), and the kinds and ratios of the aprotic polar solvent and the aromatic are of importance. Examples of the aprotic polar solvents useful in the present invention include dimethylacetamide, dimethylformamide, dimethyl sulfoxide, N-methyl-2-pyrrolidone, 4-butyrolactone, sulfolane and cyclohexanone. Those boiling at 150 to 210°C, particularly N-methyl-2-pyrrolidone (abbreviated, hereinafter, to "NMP"), are desirable since imide preparations require high temperatures. The water content in the aprotic polar solvent is preferably kept to 0.2 % by weight or less because hydration of TMA produces trimellitic acid, which interferes with the reaction and lowers the molecular weight of polymers. The amount of the aprotic polar solvent is preferably such that the diamine (A), the siloxanediamine (B) and trimellitic anhydride (C) make a total of 10 to 70 % by weight, more preferably 15 to 35 % by weight, based on the total of them with the aprotic polar solvent. A total of diamine (A), the siloxanediamine (B) and trimellitic anhydride (C) of less than 10 % by weight is advantageous to industrial production. If (A), (B) and (C) make a total above 70 % by weight, the solubilities of TMA (C) and the diimidodicarboxylic acid mixture (Y) will become insufficient to carry out satisfactory reaction. Examples of aromatic hydrocarbons, which are azeotropic with water and useful in the present invention, include benzene, xylene, ethylbenzene and toluene, and toluene, boiling at a relatively low temperature and being less harmful to the working environment, is particularly desirable. The amount of the aromatic hydrocarbon is preferably 10 to 50 % by weight, more preferably 10 to 30 % by weight, particularly preferably 10 to 15 % by weight based on the amount of the aprotic polar solvent. Azeotropic distillation with less than 10 % by weight of aromatic hydrocarbon cannot remove water effectively enough to accelerate the production of diimidodicarboxylic acids. If the aromatic hydrocarbon is more than 50 % by weight, the intermediate amidocarboxylic acids and the product diimidodicarboxylic acids may precipitate. In the course of the reaction, the aromatic hydrocarbon is distilled together with water by azeotrope and flows out of the reaction system. So the concentration of the aromatic hydrocarbon in solvent may decrease. To keep a uniform concentration of the aromatic hydrocarbon in the reaction system, it is desirable to feed back the effluent aromatic hydrocarbon to the reaction system after water is separated by using, for example, a water determination receptor equipped with a cock. First the reaction of the diamine (A) and siloxanediamine (B) with trimellitic anhydride (C) is carried out in the presence of an aprotic polar solvent preferably at 50 to 90°C, more preferably 80 to 90°C. This reaction is continued until solid trimellitic anhydride disappears and the muddiness due to solids is cleared, for example for 20 to 60 minutes, preferably 30 to 60 minutes. After this reaction, an aromatic hydrocarbon azeotropic with water is added, and reaction is carried out at the azeotropic temperature. The reaction temperature depends on the amount of the aromatic hydrocarbon and the size of the water determination receptor used, and is generally 120 to 180°C, preferably 160 to 175°C. The reaction is continued until the formation of water in the reaction system ceases, preferably until the removal of the theoretical amount of water is confirmed. The reaction solution containing the aromatic hydrocarbon may be used as such for the subsequent reaction, but is preferably freed of the aromatic hydrocarbon by distillation at higher temperatures so that the succeeding reaction with aromatic diisocyanate can be carried out at higher temperatures. The reaction of the resulting diimidodicarboxylic acid mixture (Y) containing the aromatic diimidodicarboxylic acid and the siloxanediimidodicarboxylic acid with the aromatic diisocyanate (D) can produce a high molecular weight aromatic polyamideimide resin. Examples of the aromatic diisocyanates useful in the present invention include those of the general formula (3), typically 4,4'-diphenylmethane diisocyanate (abbreviated, hereinafter, to "MDI"), 2,4-tolylene diisocyanate, 2,6-tolylene diisocyanate, naphthalene-1,5-diisocyanate and 2,4-2,4-tolylene diisocyanate dimer, which may be used individually or in combination of two or more. MDI is particularly desirable because it contributes to low amido or imino concentrations in the molecular structure and to high solubility. The reaction is desirably carried out at 100 to 200°C, more preferably 150 to 170°C, to prevent prolonged reaction at lower temperatures and the reaction of the aromatic diisocyanate itself at higher temperatures. The reaction period is typically 1 to 3 hours, preferably 1.5 to 2 hours. The siloxane-modified polyamideimide resin to be used in the resin composition of the present invention preferably has a weight average molecular weight (GPC, polystyrene conversion) of 40,000 to 150,000, more preferably 50,000 to 100,000. Examples of the thermosetting resin ingredients useful in the resin composition of the present invention include epoxy resins, phenolic resins, polyester resins, unsaturated polyester resins, bismaleimide resins, polyurethane resins, polyimide resins and bismaleimidetriazine resins. The preferred among these are thermosetting resins having organic groups reactive with the amido groups of the siloxane-modified polyamideimide resin, and epoxy resins having glycidyls are particularly preferable because it contributes to strong adhesion and is easy to work with. According to the present invention, the amount of the thermosetting resin ingredient is 1 to 200 parts by weight based on 100 parts by weight of the siloxane-modified polyamideimide resin. If it is less than 1 parts by weight, the resin composition will have insufficient solvent resistance, and if it is more than 200 parts by weight, unreacted thermosetting resin ingredient will cause a decrease of Tg, and make the resin composition inferior in heat resistance and flexibility. The preferred amount of the thermosetting resin ingredient is 3 to 150 parts by weight, more preferably 5 to 80 parts by weight based on 100 parts by weight of the siloxane-modified polyamideimide resin. When used as the thermosetting resin ingredient, epoxy resins have another advantage that they can be cured at 180°C or below and react with the amido groups of the siloxane-modified polyamideimide resin, thereby improving the thermal, mechanical and electrical properties. A preferred thermosetting resin ingredient is a combination of an epoxy resin having two or more glycidyls per molecule and a cure accelerator thereof, or a combination of an epoxy resin having two or more glycidyls and a curing agent thereof, or a combination of an epoxy resin having two or more glycidyls and a curing agent and a cure accelerator thereof. The more the glycidyls are, the better, preferably three or more per molecule. The necessary amount of epoxy resins depends on the amount of glycidyls, and the more the glycidyls are, the less the necessary amount is. Typical epoxy resins are polyglycidyl ethers obtainable by the reactions of polyhydric phenols, such as bisphenol A, novolac phenolic resins or o-cresol novolac phenolic resins, or polyhydric alcohols, such as 1,4-butanediol, with epichlorohydrin; polyglycidyl esters obtainable by the reactions of polybasic acids, such as phthalic acid or hexahydrophthalic acid, with epichlorohydrin; N-glycidyl derivatives of amines, amides or compounds having heterocyclic nitrogen bases; and alicyclic epoxy resins. The curing agents and cure accelerators for epoxy resins are not limited so far as they react with epoxy resins or accelerate curing reactions, and for example, amines, imidazoles, polyfunctional phenols and acid anhydrides may be used. Examples of useful amines include dicyandiamide, diaminodiphenylmethane and guanylurea; examples of useful imidazoles include alkyl-substituted imidazoles and benzimidazole; examples of polyfunctional phenols include hydroquinone, resorcinol, bisphenol A, halides thereof and condensation products thereof with formaldehyde, namely novolac phenolic resins and resol phenolic resins; and examples of acid anhydrides include phthalic anhydride, benzophenone tetracarboxylic dianhydride and methylhymic acid. The imidazoles exemplified above may be used as cure accelerators. As to the amounts of such curing agents and cure accelerators, amines are preferably used in an amount which substantially equalizes the equivalents of the active hydrogen atoms of amines to the epoxy equivalents of epoxy resins, for example, 0.9-1.1 equivalents of the active hydrogen atoms per epoxy equivalent of epoxy resins are desirable. The amount of dicyandiamide cannot be defined directly as an equivalent ratio to active hydrogen atoms, and is, based on our experience, 0.001 to 10 parts by weight, preferably 0.1 to 10 parts by weight per 100 parts by weight of epoxy resins. The amounts of polyfunctional phenols and acid anhydrides are 0.6 to 1.2 equivalents per epoxy equivalent of epoxy resins. If the amounts of curing agents and cure accelerators are too little, epoxy resins will partially remain uncured, to decrease Tg (glass transition temperature). If used in excess, they partially remain without undergoing reaction and may deteriorate insulating properties. Because epoxy groups of epoxy resins are also reactive to amino groups of the siloxane-modified polyamideimide resin, the proper epoxy equivalents is preferably calculated in consideration of such reaction. The ratio of the siloxane-modified polyamideimide resin to the thermosetting resin ingredient in the resin composition may be defined based on the siloxane content in the siloxane-modified polyamideimide resin and on the epoxy equivalents of the epoxy resin in the thermosetting resin ingredient. The more the siloxane content, the faster the evaporation speed (drying speed) of the solvents contained in resin composition varnish. Even if mixed with a large amount of thermosetting resin ingredient such as an epoxy resin, siloxane-modified polyamideimide resin with a high siloxane content can produce a varnish having high drying speed, and therefore can produce under moderate drying conditions adhesive film containing little residual volatile matters. The epoxy groups of epoxy resins are also reactive to the amido groups of the siloxane-modified polyamideimide resin. So in cases where epoxy resins are used as the thermosetting resin ingredient by themselves or in combination with cure accelerators and/or curing agents, the equivalent ratio of the epoxy groups of the epoxy resins to the amido groups of the siloxane-modified polyamideimide resin (equivalents of epoxy groups/equivalents of amide groups) is preferably 1 or less, more preferably 0.1-0.6, particularly preferably 0.1-0.4. If epoxy resins are used excessively, they will partially remain in film without undergoing cure reactions, thereby lowering the Tg of the film. Adhesive film can be cured with heat. In cases where epoxy resins are used alone as the thermosetting resin ingredient, film is preferably cured at 180°C or above, for example 180 to 250°C, more preferably 200 to 250°C, so that the glycidyl groups of epoxy resins undergo addition reaction with the amido groups of the siloxane-modified polyamideimide resin to produce three-dimensionally crosslinked resins. In cases where basic catalysts such as imidazoles are used as cure accelerators, curing can be performed at relatively low temperatures, for example at 160 to 190°C. In such cases, the glycidyl groups of epoxy resins and the amide groups of the siloxane-modified polyamideimide resin undergo insertion reaction, to produce three-dimensionally crosslinked resins. The adhesive film of the present invention may be produced by applying varnish of the resin composition of the present invention on a supporting substrate, followed by drying with heat to remove solvents. The varnish of the resin composition may be prepared by mixing the components of the resin composition in organic solvents. Any organic solvent which can dissolve all components is usable, and typical examples of such solvents include dimethylacetamide, dimethylformamide, dimethyl sulfoxide, N-methyl-2-pyrollidone, γ-butyrolactone, sulfolane and cyclohexanone. Preferred examples of the supporting substrate are peelable plastic films, such as release-treated PET (polyethyleneterephthalate) film, polytetrafluoroethylene film and by-axially oriented polypropylene film. Metal foil, such as copper foil, may also be used as the supporting substrate, to produce metal foil-clad adhesive film. In cases where metal foil is used as the supporting substrate, wiring circuits may be made from the metal foil. Further the metal foil may be etched away to produce self-standing film. For example, varnish can be applied on supporting substrates by using comma coater, lip coater, blade coater, rod coater, knife coater, squeeze coater, reverse roll coater, transfer roll coater. After coating, the varnish may be dried to various degrees depending on the use of the adhesive film. To produce adhesive film which is easy to work and shows good adhesion, adhesive film is preferably dried with heat to B-stage. The thickness of the adhesive film is not limited, and is typically 5 to 30 µm. EXAMPLE 1 In a 1-liter separable flask equipped with a 25 ml cock-equipped water determination receptor, a thermometer and a stirrer were placed 65.7 g (0.16 mol) of BAPP (2,2-bis[4-(4-aminophenoxy)phenyl]propane) as a diamine having three or more aromatic rings, 33.3 g (0.04 mol) of a reactive silicone oil X-22-161AS (trade name, produced by Shin-Etsu Chemical Co., Ltd., amine equivalent weight: 416) as a siloxanediamine, 80.7 g (0.42 mol) of TMA (trimellitic anhydride) and 560 g of NMP (N-methyl-2-pyrollidone) as an aprotic polar solvent, and were stirred at 80°C for 30 minutes. Subsequently, 100 ml of toluene as an aromatic hydrocarbon azeotropic with water was added, and the hydrocarbon azeotropic with water was added, and the temperature was then raised to carry out reflux at about 160 °C for 2 hours. After about 7.2 ml or more water was collected in the water determination receptor and the effusion of water ceased, the temperature was raised to about 190°C while removing the effluent collected in the water determination receptor, to remove toluene. After the reaction solution was cooled to room temperature, 60.1 g (0.24 mol) of MDI (4,4'-diphenylmethane diisocyanate) was added as an aromatic diisocyanate, and reaction was then carried out at 190°C for 2 hours. On completion of the reaction, an NMP solution of a siloxane-modified polyamideimide resin was obtained. The solution varnish was applied on a glass plate and dried at 150°C for 30 minutes to form a film, which was then peeled from the glass plate and heated at 180°C for 1 hour, to give a film of about 60 µm thick made of the siloxane-modified polyamideimide resin. The glass transition temperature, the tensile strength, the elongation at break and the tensile modulus at room temperature of the film were measured. The molecular weight of the siloxane-modified polyamideimide resin was also determined, and the results are listed in Table 1. The glass transition temperature of the film was measured with a DVE (wide-temperature dynamic viscoelasticity measuring instrument, measuring frequency: 10Hz) to define it as the temperature giving the maximum tanδ. The measurements of tensile strength, elongation at break and tensile modulus at room temperature were carried out with a tensile tester at a cross-head speed of 50 mm/min using a strip of 10 mm wide cut out from the film. The determination of molecular weight was carried out by GPC and conversion to standard polystyrene, using a mixture of 50 mg of the varnish with 5 ml of a solution of dimethylformamide/tetrahydrofuran=1/1 (volume ratio, phosphoric acid content: 0.06 M, lithium bromide content: 0.03 M). EXAMPLE 2 In a 1-liter separable flask equipped with a 25 ml cock-equipped water determination receptor, a thermometer and a stirrer were placed 32.8 g (0.08 mol) of BAPP (2,2-bis[4-(4-aminophenoxy)phenyl]propane) as a diamine having three or more aromatic rings, 31.7 g (0.02 mol) of a reactive silicone oil X-22-161A (trade name, produced by Shin-Etsu Chemical Co., Ltd., amine equivalent weight: 792) as a siloxanediamine, 40.3 g (0.21 mol) of TMA (trimellitic anhydride) and 315 g of NMP (N-methyl-2-pyrollidone) as an aprotic polar solvent, and were stirred at 80° C for 30 minutes. Subsequently, 100 ml of toluene as an aromatic hydrocarbon azeotropic with water was added, and the temperature was then raised to carry out reflux at about 160 C for 2 hours. After about 3.6 ml or more water was collected in the water determination receptor and the effusion of water ceased, the temperature was raised to about 190°C while removing the effluent collected in the water determination receptor, to remove toluene. After the reaction solution was cooled to room temperature, 30.0 g (0.12 mol) of MDI (4,4'-diphenylmethane diisocyanate) was added as an aromatic diisocyanate, and reaction was then carried out at 190°C for 2 hours. On completion of the reaction, an NMP solution of a siloxane-modified polyamideimide resin was obtained. Film was formed from the solution, and the measurements of properties were carried out in the same manner as in Example 1. The results are listed in Table 1. EXAMPLES 3 to 6 In a 1-liter separable flask equipped with a 25 ml cock-equipped water determination receptor, a thermometer and a stirrer were placed BAPP (2,2-bis[4-(4-aminophenoxy)phenyl]propane) as a diamine having three or more aromatic rings, a reactive silicone oil X-22-161AS (trade name, produced by Shin-Etsu Chemical Co., Ltd., amine equivalent weight: 416) as a siloxanediamine, TMA (trimellitic anhydride) and NMP (N-methyl-2-pyrollidone) as an aprotic polar solvent in the amounts as listed in Table 2, and were stirred at 80°C for 30 minutes. Subsequently, 100 ml of toluene as an aromatic hydrocarbon azeotropic with water was added, and the temperature was then raised to carry out reflux at about 160°C for 2 hours. After about 3.6 ml or more water was collected in the water determination receptor and the effusion of water ceased, the temperature was raised to about 190°C while removing the effluent collected in the water determination receptor, to remove toluene. After the reaction solution was cooled to room temperature, MDI (4,4'-diphenylmethane diisocyanate) was added in the amounts as listed in Table 2 as an aromatic diisocyanate, and reaction was then carried out at 190°C for 2 hours. On completion of the reaction, an NMP solution of a siloxane-modified polyamideimide resin was obtained. The molecular weights of the siloxane-modified polyamideimide resins were measured in the same manner as in Example 1. The results are listed in Table 2. SILOXANE CONTENT AND THE CONTENT OF VOLATILE MATTERS IN FILM The siloxane-modified polyamideimide resin solutions obtained in Examples 1, 4, 5 and 6 and a comparative solution of a polyamideimide resin produced without using siloxane diamines (trade name: KS-6000, produced by Hitachi Chemical Company, Ltd.) were applied on glass plates, dried at 150 C for 30 minutes, and peeled from the glass plates, to give films of siloxane-modified polyamideimide resin and a film of a polyamideimide resin containing no siloxane units, all being about 60 µm thick. The films were cut to 50 mm square, weighed, heated to 180°C for 1 hour, and weighed again, to determine the amounts of residual volatile matters in the films from the differences between the weights measured before and after the heating. The results are shown in Fig. 1. Fig. 1 shows that under the same drying conditions, volatile matters remaining in film decrease with an increase in the siloxanediamine units. Films were formed from the siloxane-modified polyamideimide resin solution obtained in Example 3 and the solution of the polyamideimide resin produced without using siloxane diamines, to determine the changes of the amounts of residual volatile matters remaining in the films with passage of time. The results are shown in Fig. 2, which shows that the resin containing siloxanediamine units had a higher drying speed. EXAMPLES 7 to 9 In a 1-liter separable flask equipped with a 25 ml cock-equipped water determination receptor, a thermometer and a stirrer were placed BAPP (2,2-bis[4-(4-aminophenoxy)phenyl]propane) as a diamine having three or more aromatic rings, a reactive silicone oil X-22-161AS (trade name, produced by Shin-Etsu Chemical Co., Ltd., amine equivalent weight: 416) as a siloxanediamine, TMA (trimellitic anhydride) and NMP (N-methyl-2-pyrollidone) as an aprotic polar solvent in the amounts as listed in Table 3, and were stirred at 80°C for 30 minutes. Subsequently, 100 ml of toluene as an aromatic hydrocarbon azeotropic with water was added, and the temperature was then raised to carry out reflux at about 160°C for 2 hours. After about 3.6 ml or more water was collected in the water determination receptor and the effusion of water ceased, the temperature was raised to about 190°C while removing the effluent collected in the water determination receptor, to remove toluene. After the reaction solution was cooled to room temperature, 25.0 g (0.1 mol) of MDI (4,4'-diphenylmethane diisocyanate) was added as an aromatic diisocyanate, and reaction was then carried out at 190°C for 2 hours. On completion of the reaction, an NMP solution of a siloxane-modified polyamideimide resin was obtained. Productions of films from the NMP solutions obtained in Examples 7 to 9 were tried to evaluate their properties, but the resulting films were fragile and could not be peeled from the glass plates. The determinations of molecular weights were carried out by GPC and conversion to standard polystyrene, using a mixture of 50 mg of each NMP solution with 5 ml of a solution of dimethylformamide/tetrahydrofuran=1/1 (volume ratio, phosphoric acid content: 0.06 M, lithium bromide content: 0.03 M). The results are listed in Table 3. All resins had relatively low molecular weights (Mw) ranging from 19000 to 35000. Example 1 Example 2 Glass transition temperature (°C) 245 255 Tensile strength (kg/mm 2 ) 7.3 9.3 Elongation at break (%) 1.5 1.2 Tensile modulus (MPa) 1800 1600 Molecular weight (weight average) 69500 72000 BAPP (mol) 161 AS (mol) TMA (mol) NMP (g) MDI (mol) Mw Example 3 0.08 0.02 0.22 290 0.13 63500 Example 4 0.07 0.03 0.21 290 0.12 73000 Example 5 0.06 0.04 0.21 300 0.12 59000 Example 6 0.05 0.05 0.21 310 0.12 66000 BAPP (mol) 161 AS (mol) TMA (mol) NMP (g) MDI (mol) Mw Example 7 0.08 0.02 0.20 250 0.1 35000 Example 8 0.07 0.03 0.20 270 0.1 28000 Example 9 0.05 0.05 0.20 290 0.1 19000 BAPP: 2,2-bis[4-(4-aminophenoxy)phenyl]propane 161AS: reactive silicone oil X-22-161AS (trade name, produced by Shin-Etsu Chemical Co., Ltd., amino equivalent weight: 416) TMA: trimellitic anhydride NMP: N-methyl-2-pyrollidone MDI: 4,4'-diphenylmethane diisocyanate Mw: weight average molecular weight As shown in Table 3, the siloxane-modified polyamideimide resins of Examples 7 to 9 were produced by allowing a diamine (A) having three of more aromatic rings and a siloxanediamine (B) to react with trimellitic anhydride (C) in a molar ratio {(A)+(B)}/(C) of 1/2.0 outside the preferred range of 1/2.05 to 1/2.20, and allowing the obtained diimidodicarboxylic acid mixture (Y) to react with an aromatic diisocyanate (MDI) in a molar ratio {(A)+(B)}/(D) of 1/1 outside the preferred range of 1/1.05 to 1/1.50. Their molecular weights were decreased by more than one-half compared with the siloxane-modified polyamideimide resins of Examples 3 to 6. To the contrary, the siloxane-modified polyamideimide resins produced by using a molar ratio {(A)+(B)}/(C) of 1/2.05 to 1/2.20 and a molar ratio {(A)+(B)}/(D) of 1/1.05 to 1/1.50 had high molecular weights. In spite of their low molecular weight, the siloxane-modified polyamideimide resins of Examples 7 to 9 are enough useful for the preparation of adhesives or coatings. The siloxane-modified polyamideimide resin of the present invention is useful for the production of varnish, adhesive and adhesive film which require heat resistance, and therefore have wide applications in the industries of coatings, wiring boards, electrical instruments, automobiles, buildings, building materials and so on. Further, compared with conventional polyamideimide resins, it has wider applications because not only the siloxane-modified polyamideimide resin itself but also the intermediate products, siloxanediimidodicarboxylic acids and aromatic diimidodicarboxylic acids are soluble in solvents. Further, being soluble in solvents, it can be produced without filtration or purification and has an increased molecular weight, and, therefore, is a useful industrial material having good film formability and excellent resin properties. Also it can be advantageously used for the production of film or coating because its varnish can be dried readily, and the product film has little residual solvent content. Further, when used as an interlaminar-insulating adhesive, the film forms no voids on heating, thereby decreasing interlaminar insulation resistance and improving connection reliability. SYNTHESIS EXAMPLES 1 TO 3 In a 1-liter separable flask equipped with a 25 ml cock-equipped water determination receptor, a thermometer and a stirrer were placed BAPP (2,2-bis[4-(4-aminophenoxy)phenyl]propane) as a diamine having three or more aromatic rings, a reactive silicone oil X-22-161AS (trade name, produced by Shin-Etsu Chemical Co., Ltd., amine equivalent weight: 416) as a siloxanediamine, TMA (trimellitic anhydride) and NMP (N-methyl-2-pyrollidone) as an aprotic polar solvent in the amounts as listed in Table 4, and were stirred at 80°C for 30 minutes. Subsequently, 100 ml of toluene as an aromatic hydrocarbon azeotropic with water was added, and the temperature was then raised to carry out reflux at about 160 C for 2 hours. After about 7.2 ml or more water was collected in the water determination receptor and the effusion of water ceased, the temperature was raised to about 190°C while removing the effluent collected in the water determination receptor, to remove toluene. After the reaction solution was cooled to room temperature, 60.1 g (0.24 mol) of MDI (4,4'-diphenylmethane diisocyanate) was added as an aromatic diisocyanate, and reaction was then carried out at 190°C for 2 hours. On completion of the reaction, an NMP solution of a siloxane-modified polyamideimide resin was obtained. BAPP (g) 161AS (g) TMA (g) NMP (g) MDI (g) Synthesis Example 1 65.7 (0.16 mol) 33.3 (0.04 mol) 80.6 (0.42 mol) 444 60.1 (0.24 mol) Synthesis Example 2 57.4 (0.14 mol) 49.9 (0.06 mol) 80.6 (0.42 mol) 502 60.1 (0.24 mol) Synthesis Example 3 41.0 (0.10 mol) 83.2 (0.10 mol) 80.6 (0.42 mol) 618 60.1 (0.24 mol) BAPP: 2,2-bis[4-(4-aminophenoxy)phenyl]propane 161AS: reactive silicone oil X-22-161AS TMA: trimellitic anhydride NMP: N-methyl-2-pyrollidone MDI: 4,4'-diphenylmethane diisocyanate EXAMPLES 10 TO 19 Resin composition varnishes were prepared by mixing each of the siloxane-modified polyamideimide resins of Synthesis Examples 1 to 3 with an epoxy resin ESCN195 (trade name, produced by Sumitomo Chemical Industries, Co., Ltd.) in the ratios shown in Table 5, adding 0.6 % by weight of 2-ethyl-4-methylimidazole based on the epoxy resin, stirring the mixtures for about 1 hour until uniform solutions were obtained, and then degassing by allowing them to stand at room temperature for 24 hours. Each resin composition varnish was applied on a supporting substrate (release treated PET film) and dried at 120°C for 30 minutes to produce an adhesive film of 50 µm thick cured to B-stage. Each adhesive film was peeled off from the supporting substrate, fixed to a frame of polytetrafluoroethylene resin, and then further cured by heating at 180°C for 60 minutes. The properties of the cured adhesive films were measured and listed in Table 5. The contents of residual volatile matters in the B-stage adhesive films were determined from the difference between the weights of each adhesive film measured before and after the heating. The results are also listed in Table 5. COMPARATIVE EXAMPLE 1 A resin composition varnish was produced in the same manner as in Example 15 except that the siloxane-modified polyamideimide resin was replaced by a polyamideimide resin containing no siloxane units. It was formed in the same manner as in Examples 10 to 19 into a B-stage adhesive film, which had such a large content of residual volatile matters of 11.5 % by weight. The resin composition varnishes of Examples 15 and 19 and Comparative Example 1 were applied to substrates so that they would form dry films of 120 µm thick, then the contents of residual volatile matters were determined at varied drying times. The results are shown in Fig. 3. The decrease of the residual volatile matters in the varnish of Comparative Example 1 almost stopped at 8 % by weight, while the residual volatile matters in the varnishes of Examples 15 and 19 decreased to 3 % by weight or less. COMPARATIVE EXAMPLE 2 A resin composition varnish was prepared by using the siloxane-modified polyamideimide resin of Synthesis Example 2 and ESCN-195 in a weight ratio of 60/40 (siloxane-modified-polyamideimide resin/ESCN-195). The varnish of Example 15 and the varnish of Comparative Example 2 were formed into films, which were then cured by heating at 290°C for 1 hour. The Tg's of the cured films were determined. The results are shown in Fig. 4. As shown in Fig. 4, the film produced from the varnish of Example 15 had a Tg of 260°C, while the film produced from the varnish of Comparative Example 2 exhibited a maximum tanδ at 170°C, which corresponds to the Tg of the epoxy resin which remained without reacting. Si-PAI Resin compounding ratio (*1) Content of residual volatile matters (%) Tg (°C) Dynamic elastic modulus (GPa) Adhesion strength to copper foil (kN/m) Example 10 Synthesis Ex. 1 90/10 2.1 220 1.7 2.2 Example 11 Synthesis Ex. 1 80/20 3.0 210 1.20 2.2 Example 12 Synthesis Ex. 1 70/30 4.9 200 0.81 2.0 Example 13 Synthesis Ex. 2 95/5 1.5 220 1.47 2.2 Example 14 Synthesis Ex. 2 90/10 1.8 215 1.81 2.2 Example 15 Synthesis Ex. 2 80/20 2.5 200 1.64 2.0 Example 16 Synthesis Ex. 2 70/30 4.3 200 0.62 1.7 Example 17 Synthesis Ex. 3 95/5 1.1 205 0.87 2.0 Example 18 Synthesis Ex. 3 90/10 1.5 200 0.75 1.9 Example 19 Synthesis Ex. 3 80/20 2.1 195 0.47 1.8 Si-PAI: Siloxane-modified polyamideimide resins produced in Synthesis Examples 1 to 3 Resin compounding ratio (*1): siloxane-modified polyamideimide resin/epoxy resin In Table 5, the properties of resin compositions were measured as follows. (1) Glass transition temperature (Tg) and dynamic elastic modulus The measurements of these properties were carried by using a dynamic viscoelasticity measuring instrument: DVE-V4 (trade name, produced by Rheology Co., Ltd.) under the following conditions. Jig: tension The distance between chucks: 20 mm Measuring temperature: 50 to 350°C Heating rate: 5°C/min Measuring frequency: 10 Hz Sample sizes: 5 mm wide x 30 mm long Tg: the temperature giving the maximum tan δ (2) Adhesion strength to copper foil Varnish was applied on the mat surface of a roughened electrolytic copper foil TSA-35 (trade name, produced by Furukawa Circuit Foil Co., Ltd.), dried at 150°C for 30 minutes, and then heated to 180°C for 1 hour, to form a sample. The resin surface of the sample was ground with sandpaper #600 and bonded to a resin plate with an epoxy adhesive (ARALDITE-STANDARD). Then measurement of copper foil adhesion strength was carried out in accordance with JIS C 6481 by peeling the copper foil in 10 mm wide from the layer of the dried varnish. As described above, the resin composition of the present invention allows high speed drying of solvent, and can produce, under moderate conditions, B-stage adhesive film with little content of residual volatile matters. When cured further, the adhesive film has a high Tg of 190°C or above and exhibits a high adhesion strength to copper foil. SYNTHESIS OF SILXOANE-MODIFIED POLYAMIDEIMIDE RESINS SYNTHESIS EXAMPLE 4 An NMP solution of a siloxane-modified polyamideimide resin was produced in the same manner as in Example 1. SYNTHESIS EXAMPLE 5 In a 1-liter separable flask equipped with a 25 ml cock-equipped water determination receptor, a thermometer and a stirrer were placed 41.1 g (0.10 mol) of BAPP (2,2-bis[4-(4-aminophenoxy)phenyl]propane) as a diamine having three or more aromatic rings, 41.6 g (0.10 mol) of a reactive silicone oil X-22-161AS (trade name, produced by Shin-Etsu Chemical Co., Ltd., amine equivalent weight: 416) as a siloxanediamine, 80.7 g (0.42 mol) of TMA (trimellitic anhydride) and 560 g of NMP (N-methyl-2-pyrollidone) as an aprotic polar solvent, and were stirred at 80°C for 30 minutes. Subsequently, 100 ml of toluene as an aromatic hydrocarbon azeotropic with water was added, and the temperature was then raised to carry out reflux at about 160 C for 2 hours. After about 7.2 ml or more water was collected in the water determination receptor and the effusion of water ceased, the temperature was raised to about 190°C while removing the effluent collected in the water determination receptor, to remove toluene. After the reaction solution was cooled to room temperature, 60.1 g (0.24 mol) of MDI (4,4'-diphenylmethane diisocyanate) was added as an aromatic diisocyanate, and reaction was then carried out at 190°C for 2 hours. On completion of the reaction, an NMP solution of a siloxane-modified polyamideimide resin was obtained.

Claims: A siloxane-modified polyamideimide resin, which is a resin produced by allowing a mixture (X) comprising a diamine (A) having three or more aromatic rings per molecule and a siloxanediamine (B) to react with trimellitic anhydride (C) to form a diimidodicarboxylic acid mixture (Y) comprising an aromatic diimidodicarboxylic acid derived from the diamine (A) and a siloxanediimidodicarboxylic acid derived from the siloxane diamine (B), and allowing the diimidodicarboxylic acid mixture (Y) to react with an aromatic diisocyanate (D). A siloxane-modified polyamideimide resin according to claim 1, which is a resin produced by allowing a mixture (X) comprising a diamine (A) having three or more aromatic rings per molecule and a siloxanediamine (B) in a molar ratio (A)/(B) of 99.9/0.1 to 0.1/99.9 to react with trimellitic anhydride (C) in a molar ratio {(A)+(B)}/(C) of 1/2.05 to 1/2.20 to form a diimidodicarboxylic acid mixture (Y) comprising an aromatic diimidodicarboxylic acid derived from the diamine (A) and a siloxanediimidodicarboxylic acid derived from the siloxane diamine (B), and allowing the diimidodicarboxylic acid mixture (Y) to react with an aromatic diisocyanate (D) in a molar ratio of {(A)+(B)}/(D) of 1/1.05 to 1/1.50. The siloxane-modified polyamideimide resin of Claim 2, wherein the molar ratio of {(A)+(B)}/(C) is 1/2.07 to 1/2.20, and the ratio of {(A)+(B)}/(D) is 1/1.10 to 1/1.50. The siloxane-modified polyamideimide resin of Claim 2, wherein the molar ratio of {(A)+(B)}/(C) is 1/2.08 to 1/2.20, and the ratio of {(A)+(B)}/(D) is 1/1.20 to 1/1.50. The siloxane-modified polyamideimide resin of any one of claims 1 to 4, wherein the aromatic diimidodicarboxylic acid has a structure of general formula (1), the siloxanediimidodicarboxylic acid has a structure of general formula (2), and the aromatic diisocyanate (D) has a structure of general formula (3): wherein R 1 is and X is or wherein R 2 is wherein R3 and R4 are each a divalent organic group, R5 to R8 are each an alkyl group, phenyl or a substituted phenyl, and n is an integer of 1 to 50, OCN-R 9 -NCO wherein R 9 is or The siloxane-modified polyamideimide resin of any one of claims 1 to 5, wherein the molar ratio (A)/(B) is 90/10 to 30/70, the molar ratio of {(A)+(B)}/(C) is 1/2.07 to 1/2.15, and the molar ratio of {(A)+(B)}/(D) is 1/1.10 to 1/1.50. The siloxane-modified polyamideimide resin of any one of claims 1 to 6, wherein the aromatic diimidodicarboxylic acid is 2,2-bis[4-[4-(5-hydroxycarbonyl-1,3-dione-isoindolino)phenoxy]phenyl]propane, and the siloxanediimidodicarboxylic acid is bis(5-hydroxycarbonyl-1,3-dione-isoindolino)propyl-polydimethylsiloxane. The siloxane-modified polyamideimide resin of claim 7, wherein the siloxanediimidodicarboxylic acid is represented by the following general formula: wherein n is an integer of 1 to 50. A siloxane-modified polyamideimide resin of any one of claims 1 to 8, which is a resin produced by carrying out a reaction of a mixture (X) comprising a diamine (A) having three or more aromatic rings per molecule and a siloxanediamine (B) in a molar ratio (A)/(B) of 99.9/0.1 to 0.1/99.9 with trimellitic anhydride (C) in a molar ratio {(A)+(B)}/(C) of 1/2.05 to 1/2.20, in the presence of an aprotic polar solvent, at 50 to 90 °C, then at 120 to 180 °C after addition of 10 to 50% by weight, based on the aprotic polar solvent, of an aromatic hydrocarbon, which is azeotropic with water, to form a diimidodicarboxylic acid mixture (Y) containing an aromatic diimidodicarboxylic acid derived from the diamine (A) and a siloxanediimidodicarboxylic acid derived from the siloxanediamine (B), and allowing the diimidodicarboxylic acid mixture (Y) to react with an aromatic diisocyanate (D). The siloxane-modified polyamideimide resin of Claim 9, wherein the diimidodicarboxylic acid mixture (Y) is allowed to react with the aromatic diisocyanate (D) after the aromatic hydrocarbon is removed from the diimidodicarboxylic acid mixture (Y). The siloxane-modified polyamideimide resin of claim 9 or 10, wherein the aprotic polar solvent is N-methylpyrrolidone, and the aromatic hydrocarbon that is azeotropic with water is toluene. The siloxane-modified polyamideimide resin of any one of claims 1 to 11, wherein the siloxane-modified polyamideimide resin has a weight average molecular weight (GPC, polystyrene conversion) of 40,000 to 150,000. A varnish containing the siloxane-modified polyamideimide resin of any one of claims 1 to 12. A siloxane-modified polyamideimide resin composition, comprising 100 parts by weight of the siloxane-modified polyamideimide resin of any one of claims 1 to 12, and 1 to 200 parts by weight of a thermosetting resin ingredient. The siloxane-modified polyamideimide resin composition of Claim 14, wherein the thermosetting resin ingredient comprises an epoxy resin having two or more glycidyl groups per molecule. The siloxane-modified polyamideimide resin composition of Claim 15 further comprising a cure accelerator or a curing agent thereof. The siloxane-modified polyamideimide resin composition of any one of claims 14 to 16, wherein the thermosetting resin ingredient includes epoxy resins, and the equivalent ratio of epoxy groups of the epoxy resins to amido groups of the siloxane-modified polyamideimide resin is 1 or less. A varnish comprising a siloxane-modified polyamideimide resin composition of any one of claims 14 to 17. An adhesive film which is made by applying a varnish according to claim 18 on a supporting substrate.

Inventors: NANAUMI KEN, SAITO TETSUYA, TAKEUCHI KAZUMASA, NANAUMI, KEN, SAITO, TETSUYA, TAKEUCHI, KAZUMASA
Applicants: HITACHI CHEMICAL CO LTD, HITACHI CHEMICAL COMPANY, LTD.
Application year: 1998
Main classification: C08L79
IPC codes: C09J7, C08L79, C08G18, C09J179, H01L23, B32B15, C09D183, H01L21, C08L63