Polymeric films

Abstract: Biaxially oriented polymeric films having a core layer of a voided propylene homopolymer with a density of not more than 0.70 g/cm 3 , and at least one substantially non-voided layer on each surface of the core layer, the ratio of the combined thicknesses of the non-voided layers on the respective surfaces of the core layer being from 2:1 to 1:1. Films in accordance with the present invention have low curl, particularly after having been printed.

Description: This invention concerns polymeric films and more particularly polymeric films having voided core layers for use as in-mould labels. Polymeric films having voided core layers typically consist of a core layer of a voided propylene homopolymer with one or more non-voided layers on each surface of the core layer. Such films have found wide acceptance as packaging materials and as label stock, for example for self-adhesive labels and labels which are to be applied to articles by methods such as in-mold labelling. In general, voiding of the core layer of such films makes them opaque, which in itself can be a desirable property for many end uses such as labelling, and it increases the yield of film from a given amount of propylene homopolymer since a significant proportion of the core layer consists of vacuoles which are formed during the voiding process. Significant reductions in film density can therefore be achieved compared with that calculated from the materials used to form the films. As with other polymeric films, end uses for polymeric films having voided core layers often include printing of one of their outer surfaces. However, it has been found that doing so can result in curling of the film. Whilst this may not lead to problems with films which are to be used for packaging by so-called form-fill-sealing, it can lead to serious problems with films which are to be used for labelling. This can be especially so with films which are to be used for in-mold labelling where individual labels are held within a mold and against a surface of the mold whilst an article is formed within the mold and the label is thereby incorporated into the surface of the article. Curling leads to label fold and/or the label failing to be correctly incorporated into the articles, e.g. containers lids and other surfaces. A multilayer opaque film is disclosed in US patent 4,698,261 having a three layered support film and transparent polyolefin layers covering the two surfaces of the support film. In the support film, either the inner layer or the two intermediate layers are composed of a filler-free polyolefin which is modified with a hard resin having a softening point ranging from 70°C. to 180°C. The respective non-modified polyolefin layer or layers of the support film have a filler, inducing a vacuole structure, whereby the film's density is less than 0.9 g/cm3. The production of the opaque polyolefin film comprising five layers is carried out by coextrusion and biaxial stretching, followed by heat setting the coextruded film. The film is advantageously used for packaging purposes. According to the present invention there are provided biaxially oriented polymeric films which are used as in-mould labels, comprising a core layer of a voided propylene homopolymer having a density of not more than 0.70 g/cm, and at least one substantially non-voided layer on each surface of the core layer, the ratio of the combined thicknesses of the non-voided layers on the respective surfaces of the core layer being from 2:1 to 1:1wherein said core layer and said at least substantially non-voided layers have been coextruded,. Curling is a particular problem with polymeric films with voided cores having densities of less than 0.70 g/cm, and especially so with relatively thick films such as are often used for labelling. However, by controlling the relative thicknesses of the non-voided layers on either side of the core layer, curling after printing can be brought within acceptable limits for end uses such as in mold labelling. In general, as the density of the voided core layer of prior art voided films decreases as a result of increased voiding, the problem with curling tends to increase. However, by controlling the relative thicknesses of the layers on either side of the core layer in accordance with the present invention significant reductions in the tendency to curl can be achieved after the films have been printed. For example, films in accordance with the present invention can have cores with densities of less than 0.70 g/cm, preferably less than 0.60 g/cm, more particularly less than 0.55 g/cm, and especially less than 0.50 g/cm and even lower, for example less than 0.48 g/cm. Although the ratio of the combined thicknesses of non-voided layers on the respective surfaces of the voided core layer should be in the range of from 2:1 to 1:1, it is preferably from 1.8:1 to 1:1, more preferably from 1.6:1 to 1:1, especially from 1.5:1 to 1:1, and more especially from 1.2:1 to 1:1. Films in accordance with the present invention can be of a variety of overall thicknesses. However, the benefits of the present invention tend to become particularly beneficial with films which are at least 30 µm thick, and more particularly with films which are at least 50 µm thick. Films with a thickness of 50 µm and more are often used as labels, for example as in-mold labels. The thicknesses of the non-voided layers on the core layer can also be varied within wide limits, but it is generally preferred that the total thickness of the non-voided layer or layers on one side of the core layer is at least 3.0 µm. Thicker layers can be used, but as will be appreciated this generally leads to an increased film density due to the voided core layer representing a relatively smaller proportion of the film thickness. Reductions in core density can be effected to maintain overall film density, but this may not be possible if the voided core layers represents only a small proportion of the overall film thickness. The voided core layer is formed from a propylene homopolymer, which for the purposes of the present invention include polymers containing small amounts of other alphaolefins, for example up to 2wt% of ethylene, which have had voids or vacuoles formed therein. Materials and methods which can be used to form the voided structure of the core layer of films of the present invention are well known in the polyolefin film art, suitable materials for the purpose including organic or inorganic particulates with a mean particle size in the range of from 1.0 to 10µm. Particular examples of materials which can be used to effect voiding include polyamides, such as nylons, polyesters, e.g. polyethylene terephthalate and polybutylene terephthalate, and chalk. The various non-voided layers on the voided core layer can in general be selected as desired for the particular end use of the films. They are preferably formed from polyolefins, including blends of polyolefins, and they can be formed from homopolymers, e.g. polyethylene or polypropylene, or copolymers, including terpolymers, containing units derived from two or more polyolefins. Examples of copolymers which can be used include those derived from a major amount of propylene and relatively minor amounts of ethylene and/or butene-1. If desired, at least one outer layer can be of a polar polymer, for example an ethylene/vinyl acetate copolymer, to improve the printability of the films. Although a single non-voided layer can be present on each surface of the voided core layer, more than one layer can be used. More particularly, it is particularly preferred to use an intermediate layer of a relatively inexpensive polymer such as a propylene homopolymer beneath an outer layer of a relatively expensive copolymer which is used to impart heat seal properties and/or printability to the films, and this enables the total thickness of the non-voided layers on a particular side of the core layer to be increased to a value which serves to assist in reducing the curl of the films. Although only the core layer of films of the present invention should be voided, the other layers of films of the present invention can include additives provided they don't lead to substantial voiding. For example, one or more of such layers can include a pigment, e.g. sub-micronic titanium dioxide, and they can, if desired, contain one or more additives proposed hitherto in the polyolefin film art, for example antiblock agents, antistatic agents, and slip agents. Examples of antiblock agents which can be used include silica and calcium carbonate. Slip agents which can be used can be migratory and non-migratory, for example fatty acid amides, e.g. erucamide, particulate polyamides, e.g. nylons, and particulate silicone elastomers. As will also be appreciated, the core layer can also contain pigments and/or other additives. Films in accordance with the present invention can be produced by known methods. However, it is particularly preferred to coextrude melts of the respective polymers plus additives through a slot die and then after cooling to stretch the resulting polymer web sequentially, first in the direction of extrusion and then in the transverse direction. Since the present invention is of particular value in reducing the curl of films which are to be used in printed form, they will usually be treated to improve their printability, for example by corona discharge or flame treatment. The following Examples are given by way of illustration only. In the various Examples film curl was tested by placing the film on a flat surface and making two perpendicular intersecting cuts in a sample of the film, the cuts being at 45° to the machine direction of the film, with each bisecting the other. By positioning the cuts in this manner, curl can be assessed in , both the machine and transverse directions, the degree of curl being assessed by measuring the height by which the various points formed by the cuts rise from the flat surface. If the points formed by the intersection of the cuts which point in or opposite to the machine direction of the film curl, machine direction curl is indicated. If the points formed by the intersection of the cuts which point in the transverse direction of the film curl, transverse direction curl is indicated. The film sample is then turned over and the film is again laid flat. The degree of curl in the machine and transverse directions can then be assessed as described above. Example 1 A five layer polymer web was produced by coextruding through a slot die melts of a propylene homopolymer containing 15.0wt% of chalk with a mean particle size of 3pm which formed the core layer of the web, intermediate layers of the propylene homopolymer on either side of the chalk containing layer but without chalk, and two outer layers, one consisting of a propylene/ethylene copolymer including 15wt% of sub-micronic titanium dioxide, and the other consisting of a blend of a 67.5wt% of a propylene/ethylene copolymer (4wt% ethylene) and 32.5wt% of a polyethylene. The five layer web was chilled using a chill roll and it was then sequentially stretched, first 5:1 times in the direction of extrusion by passing it over heated rollers which had different peripheral speeds, and then 9.5:1 times in the transverse direction using a stenter oven, the biaxial stretching resulting in the core layer becoming voided. The biaxially oriented film was cooled, subjected to corona discharge treatment on both surfaces, and then wound up. The film had a total thickness of 75µm with the core layer being 66.5µm thick. The intermediate layer beneath the layer containing the titanium dioxide was 3.0µm thick, the polyethylene layer being 1.5µm thick. The other intermediate layer was 2.0µm thick, and the outer layer on this intermediate layer was 2.0µm thick. The density of the core layer was 0.50 g/cm 3 , and the ratio of thicknesses of the non-voided layers on the two surfaces of the core layer was 1.125. One surface of the film was then printed using a heavy ink coverage. The degree of curl assessed using the curl test method described above was zero. Example 2 A five layer biaxially oriented film was produced as described in Example 1 but with 16wt% of chalk in the core layer, the polyethylene layer being replaced by a propylene/ethylene copolymer and the relative thicknesses of the respective layers being slightly changed. The resulting biaxially oriented film had a core layer which was 64µm thick with a density of 0.47 g/cm 3 , the intermediate layer beneath the outer layer of an unfilled propylene/ethylene copolymer containing 7.2wt% of sub-micronic titanium dioxide was 6.0µm thick and the layer of the unfilled propylene/ethylene copolymer was 1.0µm thick. The relative ratio of the combined thicknesses of non-voided layers on the voided core layer was 1.75:1. After printing as in Example 1 this film showed no curl in the curl test described above. Example 3 A five layer film was produced as described in Example 2 except that the two intermediate layers were both 6.0µm thick and the two outer layers were both 1.0µm thick, the core layer being 61µm thick. The overall film thickness was again 75µm thick. The density of the core layer was 0.49 g/cm 3 , and the ratio of the respective combined thicknesses of the non-voided layers on either side of the core layer was 1:1. The film was printed as described in Example 1, following which it exhibited zero curl in the curl test. Example 4 A four layer biaxially oriented film was produced by a method similar to that described in Example 1 for a five layer film, but without an intermediate layer between the core layer and one of the outer layers. This single layer consisted of the blend of polymers used for one of the outer layers of the film produced in Example 2. On the other surface of the core layer was an intermediate layer consisting of a blend of 92.8 wt% of a propylene homopolymer and 7.2 wt% of sub-micronic titanium dioxide. The voided core layer of the biaxially oriented film was 64µm thick (density 0.50 g/cm 3 ), and the single outer layer on one side of the core layer was 4.0µm thick. The intermediate layer on the other surface of the core layer was 6µm thick and the outer layer on this layer was 1.0µm thick. The ratio of thicknesses of the layers on the two surfaces of the core layer was 1.75:1. The film was printed as described in Example 1, following which it exhibited zero curl in the curl test. Example 5 (comparison) A four layer polymeric web consisting of a core layer of propylene homopolymer containing 8.5 wt% of chalk (mean particle size 3µm) with an intermediate layer of a propylene homopolymer containing 10.8wt% of titanium dioxide and an outer layer of a propylene/ethylene copolymer (4wt% ethylene) on one surface and a blend of 67.5wt% of the same copolymer on the other surface with 32.5wt% of polyethylene was produced in a similar manner to that described for the five layer web in Example 1 and then sequentially stretched to form a biaxially oriented film which was 80µm thick. The core layer was 67µm thick (density 0.56 g/cm 3 ), the outer layer consisting of the copolymer was 1.0µm thick, with the intermediate layer being 8µm thick, and the other layer formed from the polymer blend was 4µm thick. The ratio of thicknesses of the two non-voided outer layers on the voided core layer was 2.25:1. After corona treatment and printing on surface in a manner similar to that used for the film of Example 1 the film showed a curl towards the printed face of 6 to 10 mm in both the machine and transverse directions under substantially similar conditions.

Claims: Use of a label as an in-mould label, wherein the label is made from a biaxially oriented polymeric film comprising a core layer of a voided propylene homopolymer having a density of not more than 0.70 g/cm 3 , and at least one substantially non-voided layer on each surface of the core layer, the ratio of the combined thicknesses of the non-voided layers on the respective surfaces of the core layer being from 2:1 to 1:1, wherein said core layer and said at least substantially non-voided layers have been coextruded. Use according to claim 1, wherein the density of the voided layer of the label film is not more than 0.60 g/cm 3 . Use according to claim 2, wherein the density of the voided layer of the label film is not more than 0.55 g/cm 3 . Use according to claim 3, wherein the density of the voided layer of the label film is not more than 0.50 g/cm 3 . Use according to any of the preceding claims, wherein the ratio of the combined thicknesses of the non-voided layers on the respective surfaces of the core layer of the label film is from 1.8:1 to 1:1. Use according to claim 5, wherein the ratio of the combined thicknesses of the non-voided layers on the respective surfaces of the core layer of the label film is from 1.6:1 to 1:1. Use according to claim 6, wherein the ratio of the combined thicknesses of the non-voided layers on the respective surfaces of the core layer of the label film is from 1.5:1 to 1:1. Use according to claim 7, wherein the ratio of the combined thicknesses of the non-voided layers on the respective surfaces of the core layer of the label film is from 1.2:1 to 1:1. Use according to any of the preceding claims, wherein the overall thickness of the label film is at least 50µm. Use according to any of the preceding claims, wherein the thickness of the non-voided layer or layers of the label film is at least 3 µm. Use according to any of the preceding claims, wherein the voided core layer is formed from a propylene homopolymer including organic or inorganic particulates with a mean particle size of 1 to 10µm. Use according to claim 11, wherein the inorganic particulate is chalk. Use according to claim 11, wherein the organic particulate is polybutylene terephthalate. Use according to any of the preceding claims, wherein a non-voided layer on the voided core layer of the label film comprises a homopolymer of propylene or a copolymer. Use according to claim 15, wherein the film has been treated by corona discharge or flame treatment. (col.3, line 38 - 41). Use according to any of the preceding claims, wherein an outer surface of the label film has printing thereon. Use according to any of the preceding claims, wherein the label film has a curl of substantially zero in both the machine and transverse directions as assessed by the method described herein.

Inventors: BIDDISCOMBE HELEN ANN, BIDDISCOMBE, HELEN ANN
Applicants: TREOFAN GERMANY GMBH & CO KG, TREOFAN GERMANY GMBH & CO.KG
Application year: 1998
Main classification: B32B27
IPC codes: B32B27