Process for producing crosslinked hyaluronic acid

Abstract: A process for producing crosslinked hyaluronic acid (HA) or a salt thereof is disclosed, in which an aqueous solution of HA is crosslinked with divinyl sulphone (DVS) at a pH between 8 and 11 using a molar ratio of DVS/HA between 1 and 10%. The process results in a viscous aqueous solution of crosslinked hyaluronic acid or salt thereof, which is suitable for viscosupplementation of joints, especially for racing horses.

Description: The invention relates to a process for producing crosslinked hyaluronic acid by treating an aqueous solution of hyaluronic acid with divinyl sulphone. Hyaluronic acid (HA) is a high molecular weight, straight-chain mucopolysaccharide consisting of repeating glucuronic acid - N-acetylglucosamine disaccharide units. It has a high water-absorbing capacity. HA is a component of e.g. skin, connective tissue and vitreous humour of the eye. HA is also present in the synovial fluid of joints, where it has a function as a lubricant and as a shock absorber. A production deficiency of HA results in painful joints (osteoarthritis) in man and in lameness in horses. Apart from being a medical problem, lameness in horses is also an economical problem, especially for racing horses. For several years now, lameness has been controlled by viscosupplementation, which involves injecting a gel of HA into the joint. The injected amount of HA is usually 16-40 mg in several millilitres of neutral water. A commercially available product is a synovial viscosupplementation HA gel/fluid of 20 mg referred to as Synvisc GF20. The HA used in this product can be obtained by crosslinking HA with divinyl sulphone (DVS) at high pH (0.2 M sodium hydroxide) and at 20°C, using a HA/DVS weight ratio between 15:1 and 1:5, as described in US Patent 4,582,865. Crosslinked HA which is suitable for intra-articular injection can also be obtained by crosslinking HA with an excess of bifunctional epoxides, such as epichlorohydrine, as disclosed in EP-A-0161887. Although initially the use of the prior art HA products such as Synvisc in joint treatment of horses is satisfactory, the symptoms of joint failure return after a few months, often preceded by inflammatory responses. It has been found now that a crosslinked HA can be obtained which is in the form of a viscous solution rather than a gel and which has an improved long-term performance in joint treatment, if the crosslinking of HA is carried out under specific conditions as defined in the appending claims. An important feature of the process of the invention is the low ratio of crosslinking agent and HA. The weight ratio of HA (based on the sodium salt) to DVS should be between 20 and 200, preferably between 40 and 120. A weight ratio HA/DVS (WR HA/DVS ) of 20 corresponds to a molar percentage of DVS to HA (MP DVS/HA ) of 17% (on the basis of an anhydro[sodium glucuronate - N-acetylglucosamine] disaccharide) or 8.5% (on average anhydromonosaccharide basis). Thus, the molar percentage of crosslinking agent to HA (monosaccharide basis) should be between about 0.9 and 8.5, preferably between about 1.7 and 5. The solution to be crosslinked may contain other biopolymers (polysaccharides, proteins, glycoproteins etc.) in addition to HA, but preferably less than one third of the amount of HA, most preferably less than 5% thereof. Another important feature is the pH of the crosslinking solution. It should be below 11, preferably above 7.5 and more preferably between 8 and 11. It was found that the use of a higher pH results in HA solutions which cause allergic and inflammatory reactions, possibly due to degradation of HA. Also it is preferred that the crosslinking is carried out at relatively low temperatures, such as below 15°C, especially between 0 and 12°C. The crosslinked HA preferably has a molecular weight between 0.7 and 8 MDa, the average molecular weight preferably being between 1.2 and 5 MDa. It is further preferred that the crosslinked HA is present in a viscous solution and not in a gel. The viscosity of the solution is preferably between 15,000 and 40,000 cP, most preferably between 18,000 and 32,000 cP, as measured with a Brookfield viscosimeter. The invention also pertains to the viscous solution thus obtained and to its use in viscosupplementation of joints, especially for horses, and in ophthalmic surgery, especially as a temporary filling of the ey socket during surgery. Example 1 To 100 ml of a solution of HA (Sigma, Streptococcus zooepidemicus , 0.8% w/w in water) at pH 8.5 and 5°C, 15 mg of DVS was added (WR HA/DVS = = 53). The mixture was homogenised and allowed to stand at 4-6°C for one week. The solution was then adjusted to pH 7 using acetic acid and sterilised by filtration (0.45 µm). The solution thus obtained was injected into the joints of racing horses submitted to high stress conditions. The animals treated with this solution were free of joint problems until about 6 months after injection, when the treatment was repeated. Animals treated with prior art HA compositions (Synvisc) needed repeat of injection after 2 or 3 months. Example 2 To 100 ml of a solution of HA (Shiseido, Streptococcus zooepidemicus , 0.8% w/w in water) at pH 8.5 and 5°C, 10 mg of DVS was added (WR HA/DVS = 80). The solution was treated as described in example 1 and also performed better than the prior art material. Example 3 To 100 ml of a solution 1 g of containing HA (Sigma, Streptococcus zooepidemicus ) and 20 mg of DVS (WR HA/DVS = 50) was added 200 mg of finely powdered sodium carbonate under stirring at pH 7. After a clear solution had been obtained, stirring was discontinued. After the sodium carbonate had been added, the pH was 10. The mixture was allowed to stand for 3 days at 4-6°C. Then the solution was carefully neutralised with acetic acid (pH 7) and further treated as described in example 1. Apart from a slight swelling at about 10% of the horses, this product was equally satisfactory as the product of example 1. The viscosities and results of treatments of various crosslinked solutions is given in the table below: degree of crosslinking (mol%) viscosity (cP) number animals tested result (treatment) result (inflammatory response) 0 14,000 1000 + ++ 2 18,000 30 ++ + 3 22,000 30 ++ + 4 25,000 30 ++ + When this example was repeated using 0.2 M NaOH during crosslinking, vigorous inflammatory responses (swellings) occurred, which could only be treated with corticosteroids.

Claims: A process for producing a crosslinked hyaluronic acid (HA) or a salt thereof, by crosslinking an aqueous solution of HA with divinyl sulphone (DVS), characterised in that the crosslinking with DVS is carried out at a pH between 8 and 11 using a DVS/HA molar ratio between 1 and 10% (a mole of HA being equivalent to an average anhydromonosaccharide unit). A process according to claim 1, wherein a DVS/HA molar weight ratio between 2 and 5% is applied. A process according to claim 1 or 2, wherein the crosslinked HA has a molecular weight of between 0.7 and 8 MDa. A process according to any one of claims 1-3, wherein the crosslinking is carried out at a temperature between 0 and 12°C. A process according to any one of claims 1-4, wherein the crosslinked hyaluronic acid is produced in the form of a viscous aqueous solution. A process according to claim 5, wherein the solution has a viscosity of 15,000-40,000 cP. A viscous aqueous solution of crosslinked hyaluronic acid or salt thereof, suitable for viscosupplementation of joints, said crosslinked hyaluronic acid having a molecular weight of between 0.7 and 8 MDa and said solution having a viscosity between 15,000 and 40,000 cP. A viscous solution according to claim 7, having a viscosity between 18,000 and 32,000 cP. Use of a viscous solution according to claim 7 or 8, or obtained according to any one of claims 1-6, for use in human or veterinary therapy or surgery.

Inventors: BESEMER ARIE CORNELIS, VAN DER TUIN EVERHARDUS, BESEMER, ARIE CORNELIS, VAN DER TUIN, EVERHARDUS
Applicants: STICHTING HIPPOMEDICS
Application year: 1998
Main classification: C08B37
IPC codes: A61L31, C08B37