APPARATUS AND METHOD FOR DECOMPOSING AND RECOVERING ISOCYANATE COMPOUND

Abstract: The present invention relates to an apparatus for hydrolyzing and recycling polyisocyanate derivatives having at least one isocyanato group and/or a group derived from an isocyanato group as target compounds to be hydrolyzed into raw materials or derivatives thereof for the target compounds, the apparatus including: a hydrolyzer for bringing only pressurized water in a liquid state at a temperature of 190 to 370°C into contact with the target compounds in the reactor to hydrolyze the target compound; and a post-processor for conducting post-processings such as dewatering, addition, distillation, separation, and liquid separation for a hydrolyzed reaction product discharged from the reactor.

Description: The present invention relates to an apparatus for and process of hydrolyzing and recycling polyisocyanate derivatives, such as polyurethane resins used in wide applications including furniture, bedding, vehicles, heat insulating materials for building material and consumer electronics, shoe soles and the like, and oligomers of isocyanate compounds in distillation residues discharged in a chemical plant as by-products. Such polyisocyanate derivatives are brought into contact with water heated to high temperature and pressurized to a liquid state, thereby being hydrolyzed and recovered as raw material compounds or derivatives thereof for the target compound. In the present invention, "polyisocyanate derivatives" indicate derivatives having at least one isocyanato group and/or group derived from an isocyanato group, and include wide variety of compounds from low molecular weight compounds to polymers. In Japan, about 400,000 tons of polyurethane resins are produced in the form of soft, semi-hard, and hard urethane foams, elastomers, and Reaction Injection Moldings (RIM), and are used in various fields. Recently, public awareness of environmental protection have been heightened in all over the world, and under such a situation, studies to develop processes for recycling various kinds of plastics, including polyurethane resins, have been carried out. Known processes for recycling polyurethane resins are roughly classified in the following categories: 1) a material recycling technique; 2) a chemical recycling technique; and 3) an energy recycling technique. In the material recycling technique 1), polyurethane resins are subjected to a physical treatment such as crushing without changing their physical properties. The crushed polyurethane resins are subjected to thermal press molding or adhesion press molding into new products, or utilized as fillers for extruded products, RIM products, concrete and the like. In the chemical recycling technique 2), polyurethane resins are recovered to raw materials or chemical substances usable as raw materials. Known as chemical recycling techniques are a glycol decomposition method, an amine decomposition method, a hydrolysis method and the like. In the energy recycling method 3), polyurethane resins are utilized as energy resources. Specifically, polyurethane resins are directly used as fuels or are subjected to treatment for generating steam or fuel gases which are then used as fuels. The method of the present invention is classified in the chemical recycling technique 2). However, the conventional chemical recycling technique has drawbacks that it requires other compounds such as glycol, amine, and alkali as a decomposing agent, and in addition, it takes long reaction time which renders this technique uneconomical. Due to such drawbacks, there are only a few cases where the conventional chemical recycling technique is actually used for recycling polyurethane resins. On the other hand, studies have been carried out to develop another chemical recycling technique where polyurethane resins are hydrolyzed into polyol and amine using water as a decomposing agent. For example, Japanese Laid-Open Patent Publication No. 54-70377 discloses a method for decomposing polyurethane in the presence of superheated steam and an alkaline/alkaline earth metal compound at about 300°C or lower and 0.4 to 10 gauge pressure. In the invention disclosed in Japanese Laid-Open Patent Publication No. 54-70377, the inventors have made various studies to find out a method for hydrolyzing polyurethane by superheated steam. However, at a pressure less than 10 gauge pressure, the reaction rate is low and long time is required for reaction. Therefore, they have concluded in the disclosure that the presence of compound which exhibits an activity as catalyst, such as ammonium and alkali, is necessary. On top of methods for recycling used polyurethane resins, there are also demands for establishing methods for recycling wastes discharged in a chemical plant as by-products. Such wastes, discharged in a chemical plant as distillation residues at a purifying and distilling step of synthesizing a compound having isocyanato groups, almost always contain oligomers such as dimers and trimers of the aimed compound. However, it is impossible to utilize the oligomers. For example, in a chemical plant producing a diisocyanate compound, a diisocyanate compound having high purity is obtained as a finished product at a purifying and distilling step. Although distillation residues generated at the purifying and distilling step contains a diisocyanate compound, i.e., the aimed compound, the distillation residues cannot be recycled and are disposed of as wastes by incineration and the like. This is because the diisocyanate compound cannot be separated from the oligomers thereof or other impurities. British patent Publications No. 991387 and No. 1047101, U.S. Patents No. 3225094 and No. 4137266 respectively disclose a method for hydrolyzing and recycling isocyanate derivatives where isocyanate derivatives are recycled in the form of amine compounds. As all of these methods are batchwise methods, there are disadvantages that large amount of energy is required for raising and lowering temperature and pressure at a time of batch replacement. In addition, in terms of the scale of equipment, there is a limitation on the treating capacity of isocyanate derivatives. Therefore, these methods are not industrially suitable. Japanese Laid-Open Patent Publication No. 9-151270 discloses a method for recycling tolylenediisocyanate where tolylenediisocyanate is recovered in the form of tolylenediamine. However, there is no sufficient disclosure as to the optimum conditions of hydrolysis and of post-processings. US-A-4,051,212 relates to a continuous process for the hydrolytic degradation of plastics wherein a hydrolyzable material is introduced with water into a screw machine, and is subjected therein to a temperature of 100 to 300°C, and a pressure of 5 to 100 bars for 2 to 100 minutes. JP-A-5031000 describes the efficient decomposition of polymer compounds contained in industrial and household waste into a molecular weight capable of recycling by using water in a supercritical or subcritical state as the solvent and carrying out selective hydrolysis or thermal decomposition of a natural or synthetic polymer. US-A-3,225,094 relates to a hydrolysis process for recovering polyamines from polyisocyanate reaction products. This process involves treating said polyisocyanate reaction product with water in the liquid state at a temperature of about 160-250°C and pressure ranging from 10-40 atmospheres. US-A-5,386,055 relates to a process for depolymerizing polymers by selective, partial oxidation at supercritical or near supercritical conditions for water and wherein supercritical water or water near supercritical conditions is used as a solvent and reforming agent, which is used to produce relatively high yields of the monomers originally used to produce the polymers. In view of the above, the present invention is aimed at providing an apparatus for and process of efficiently recycling polyurethane resin and wastes discharged at a production line for producing low molecular weight polyisocyanate compounds on an industrial scale using substantially only water with no presence of any compound as a hydrolyzing agent. According to the present invention , an apparatus for hydrolyzing and recycling polyisocyanate derivatives having at least one isocyanato group and/or a group derived from an isocyanato group as target compounds to be hydrolyzed into raw materials or derivatives thereof for the target compounds, the apparatus includes: a hydrolyzer for bringing only pressurized water in a liquid state at a temperature of 190 to 370°C into contact with the target compounds in the reactor to hydrolyze the target compound; anda post-processor for conducting post-processings such as dewatering, addition, distillation, separation, and liquid separation for a hydrolyzed reaction product discharged from the reactor. Figure 1 is a diagram showing a preferable example of the hydrolyzing and recycling apparatus according to the present invention; Figure 2 is a diagram showing another example of the hydrolyzing and recycling apparatus according to the present invention; Figure 3 is a diagram showing still another example of the hydrolyzing and recycling apparatus according to the present invention; Figure 5 is a graph illustrating an influence of the reaction temperature on the hydrolysis of polyurethane resin. The apparatus for hydrolyzing and recycling polyisocyanate derivatives of the present invention is intended for use in hydrolyzing polyisocyanate derivatives having groups derived from isocyanato groups such as polyurethane resins into useful and reusable material. First, target compounds to be treated by the hydrolyzing and recycling apparatus of the present invention will be described. In the present invention, the target compound to be hydrolyzed means polyisocyanate derivatives having at least one isocyanato group (-NCO) and/or at least one group derived from isocyanato group. The target compound to be hydrolyzed includes, in addition to the compounds having isocyanato groups, compounds having groups (including bonds) derived from isocyanato groups such as urethane bond, allophanate bond, urea bond, biuret bond and amide bond, and an example of such compounds include a polyurethane resin. In addition, also included as an example of such compounds include compounds generated as a result of dimerization or trimerization of the compounds having isocyanato groups. Examples of such compounds include dimers, trimers or oligomers higher than trimers, such as carbodiimide, uretidione, urethane imine and isocyanurate , which are contained in the wastes from a chemical plant producing the compounds having isocyanato groups. From the viewpoint of recycling, it is preferable to hydrolyze a polyurethane resin or wastes from a chemical plant as a target compound. Examples of the polyurethane resin used as a target compound include chips or defective products of polyurethane generated at a molding or processing step to produce polyurethane products, wastes of polyurethane products after usage in various fields. Kinds of polyurethane resins include foams such as soft urethane foams, semi-hard urethane foams, hard urethane foams, elastomers (casted, kneaded, or thermoplastic elastomers), RIM products and ISFs (integral skin foams), all of which can be hydrolyzed by the apparatus of the present invention. A polyurethane resin is made of a compound having two or more isocyanato groups (polyisocyanate) and generally a compound having active hydrogen (polyol) as main raw materials. However, various polyurethane resins having various physical properties are also available in accordance with the combination of the kinds and the molecular weight of the main raw materials, a catalyst, a chain extension agent, and the like. Specific examples of the raw material of polyurethane resin include tolylenediisocyanate (TDI), modified TDI, diphenylmethanediisocyanate (MDI), polymeric MDI, hydrogenated MDI, modified MDI, hexamethylenediisocyanate (HDI), tolidinediisocyanate (TODI), 1, 5-naphthalenediisocyanate (NDI), isophoronediisocyanate (IPDI), p-phenylenediisocyanate, xylylenediisocyanate (XDI) and hydrogenated XDI. Examples of polyol include polyether polyol such as bifunctional, trifunctional, tetrafunctional, hexafunctional, or octafunctional polyetherpolyol derived from alkylene (ethylene or propylene) oxide and initiator having active hydrogen, polytetramethyleneglycol (PTMG), polyester polyol such as condensed-type polyester polyol, lactone-type polyester polyol, and polycarbonate diol and acryl polyl. The hydrolyzing and recycling apparatus of the present invention can hydrolyze bonds contained in an ordinary polyurethane resin such as urethane bond, allophanate bond, urea bond, biuret bond, and amide bond regardless of the molecular structure of the polyurethane resin and the kinds of units constituting the polyurethane resin. As a result of the hydrolysis, a raw material of the polyurethane resin which is a target compound to be hydrolyzed or the derivatives usable as a raw material of the polyurethane resin, that is, polyol and/or a polyamine compound corresponding to a raw material polyisocyanate, can be recovered. There may be some cases where polyol and amine, which are hydrolyzed reaction products, are hard to be separated from each other depending on the polyurethane resin. In such a case, it is preferable that a mixture of polyol and amine is subjected to addition reaction with ethylene oxide or propylene oxide to recover polyether polyol. In this manner, there is no need to forcedly separate polyol and amine from each other. Rather, polyether polyol is more preferable, because it is directly usable as a raw material of polyurethane, and as a result, the number of post processes and recycling costs are decreased. Hereinafter, the characteristics of the hydrolyzing and recycling apparatus of the present invention will be described. The hydrolyzing and recycling apparatus of the present invention includes: a hydrolyzer for bringing substantially only water at 190 to 370°C in a liquid state at high pressure into contact with a target compound to be hydrolyzed in a reactor, thereby hydrolyzing the target compound; and a post-processor for conducting post-processings such as dewatering, addition, distillation, separation, and liquid separation for the hydrolyzed reaction product discharged from the reactor. In the present invention, water in a liquid state (not in a steam state) at 190 to 370°C is brought into contact with the target compound to be hydrolyzed, thereby smoothly hydrolyzing the target compound without using any other compounds for promoting hydrolysis. The hydrolyzer includes a reactor capable of conducting high pressure reaction as an essential component. Preferable examples of the hydrolyzer include (1) a hydrolyzer for simultaneously heating and pressurizing water into a liquid state, and continuously supplying the water to the reactor, and (2) a hydrolyzer for heating water in a reactor under a pressurized condition. The hydrolyzer (1) is not specifically limited as far as it is capable of introducing water which is heated and pressurized beforehand to the reactor. For example, the hydrolyzer (1) includes a heater and a pump which are located at any position of the water supplying line extending from a water supplying source to the reactor. Either the heater or pump may be located on the reactor side (i.e., on the downstream side). The hydrolyzer (2) is not specifically limited as far as it is capable of heating and pressurizing water which has been introduced into the reactor. For example, the hydrolyzer (2) may have a structure in which water pressurized by pump is introduced into the reactor having a heater, or may have a structure in which water is introduced into the reactor having a heater and then the volume inside the reactor is diminished by being pressurized with a cylinder under a hermetically sealed state The hydrolyzers (1) and (2) may be used in combination in order to maintain the temperature and pressure during hydrolysis is proceeding in the reactor. The target compound to be hydrolyzed may be supplied to the reactor by batchwise or continuously. For example, in the case of hydrolyzing and recovering a polyurethane resin, a specific amount of polyurethane resin is put into the reactor, and then, is hydrolyzed by the hydrolyzer. In the case where the target compound to be hydrolyzed is waste such as distillation residue from a chemical plant, it is preferable that the hydrolyzing and recycling apparatus further includes a supplier for continuously supplying the target compound to be hydrolyzed into the reactor. As such waste is continuously discharged, it is wasteful to hydrolyze them batchwise. If a batchwise method is employed, an energy loss is large in raising and lowering temperature and pressure in the reactor at the time of batch replacement. In addition, a reservoir for storing wastes is required, and the change in quality of target compound to be hydrolyzed such as decomposition and polymerization during storage in the reservoir is inevitable. As will be described later, when a compressor for compressing polyurethane foam is included in the hydrolyzing and recycling apparatus, it is also preferable that the apparatus also includes a supplier for continuously supplying the compressed foam into the reactor. Specific examples of the supplier include pumps, extruder, or pressure accumulators. Or alternatively, the apparatus may include an extruder having a heater for introducing a target compound to be hydrolyzed in a heated state. A post-processor conducts post-processings such as dewatering, addition, distillation, separation and liquid separation for hydrolyzed reaction product discharged from the reactor. However, the post-processing is not limited to dewatering addition, distillation, separation, and liquid separation, but also include various other processings conducted for the hydrolyzed reaction product. Specific examples of the processors included in the post-processor are as follows: A dewatering processor: a processor which includes devices for respectively conducting distillation, contact with a dewatering agent (an agent which adsorbs water), drying and filtration ; An addition processor: a processor which includes a reactor capable of chemical reaction. A distillation processor: a processor which includes a distillation device capable of conducting distillation, extractive distillation and molecular distillation ; A separation processor: a processor which includes devices respectively capable of degassing, extraction, centrifugation, filtration, squeezing and fractionation; and A liquid separation processor: a processor which includes a liquid separation device. The above processings may be conducted under reduced or increased pressure. The post-processor may be used alone or in combination. The hydrolyzing and recycling apparatus of the present invention may include a compressor. A compressor is useful, for example, in the case of treating polyurethane foam as a target compound to be hydrolyzed. As the compressor compresses the foam to a reduced volume, the reactor can be downsized. Preferably, the compressor capable of compressing polyurethane foam while heating the polyurethane foam to 100 to 250°C is employed. The compressor is capable of compressing not only soft foam but also hard foam to a small volume (i.e., to a large density) while heating the foam to an appropriate temperature. Examples of the compressor include pressurizer having a heater, and an extruder having a heater (single shaft extruder, double shaft extruder and the like). The extruder is preferable as the compressor, because it also has a function as a supplier. In the case of using the pressurizer having a heater as the compressor, a supplier is additionally provided, or a compressed product is introduced into the reactor batchwise. Hereinafter, a preferable hydrolyzing and recycling apparatus will be described referring to Figures 1 to 3, as to the case where the target compound to be hydrolyzed is a polyurethane resin. It is to be noted that the present invention is not limited to the configurations shown in Figures 1 to 3, but modifications thereof in accordance with the scope of the invention are also within the present invention. (1) in the case where the target compound to be hydrolyzed is a polyurethane resin: Figure 1 is a diagram showing an example of a hydrolyzing and recycling apparatus used for continuously conducting hydrolysis. This apparatus is especially useful for hydrolyzing and recycling polyurethane foam. A hydrolyzer 1 includes a reactor 2, a supplying pump 3 provided between a water supplying source and the reactor 2, and a heater 4. Water in a liquid state which is pressurized by the pump 3 and heated by the heater 4 respectively is continuously supplied to the reactor 2. In the case of using a reactor having a heater, the heater 4 may be eliminated; however, the structure of the reactor becomes complicated. Either the pump 3 or the heater 4 may be located on the reactor side. Polyurethane is supplied from a reservoir 5 to the reactor 2 through a compressor made of an extruder 6. In this example, the extruder 6 has functions as a supplier and a compressor. Another supplier such as a gear pump may be further provided between the extruder 6 and the reactor 2. Polyurethane is stored in the reservoir 5. Polyurethane large in size is cut into an appropriate size and is stored in the reservoir 5. The polyurethane is compressed by the extruder 6 while being heated normally at 100 to 250°C. More preferable lower limit of the heating temperature is 120 °C, and more preferable upper limit thereof is 180 °C. It is preferable to adjust the compressing conditions so that the time required for the heating and compressing is 5 to 60 minutes in accordance with the performance of the extruder. In the case of treating ordinary soft foam, it is general the soft foam is heated and compressed so as to have a density of about 300kg/m 3 or more. In the case of treating ordinary hard foam, it is general the hard foam is heated and compressed so as to have a density of about 500kg/m 3 or more. Polyurethane resin products other than foams also may be heated by the extruder 6 and then are supplied to the reactor 2, as is the case of the aforementioned foams. This is because the heated polyurethane resin and the heated and pressurized water are brought into contact with each other in the reactor to cause prompt hydrolysis therebetween with no need of heating the polyurethane resin in the reactor. However, in the case of treating a polyurethane resin having such high hardness that it exhibits no flowability even if being heated, the polyurethane resin is finely crushed and is introduced into the reactor for hydrolysis. It is preferable that the internal pressure of the reactor 2 is adjusted to 3 to 30MPa. With low internal pressure, too long time is required for reaction. More preferable lower limit of the internal pressure is 6MPa. When the internal pressure is adjusted within the aforementioned range, the hydrolyzing rate of polyurethane reaches 100% for a short time, and therefore, there is no need to adjust the internal pressure to higher than 30MPa. More preferable upper limit of the internal pressure is 25MPa, and the most preferable 20MPa. Weight of water (hydrolysis ratio) to be brought into contact with polyurethane in the reactor 2 is 1.0 time or more the polyurethane, and it is recommended that the hydrolysis ratio is 10.0 times or less. When the hydrolysis ratio exceeds 10.0 times the polyurethane, the reactor is required to have larger size, or longer time and larger energy are required for separating the hydrolyzed reaction product from water in the post-processing step. More preferable upper limit of the hydrolysis ratio is 4.0 times. It is preferable that the water in the reactor 2 is at 200 to 370°C (reaction temperature). When the water is at a temperature exceeding 370°C, although the hydrolyzing rate of polyurethane reaches almost 100%, condensation of polyamine and decomposition of polyol are promoted, and as a result, the recovering rate of polyamine and polyol is lowered. More preferable upper limit of water temperature is 340°C. When the water is at a temperature lower than 200°C, the efficiency is lowered because long time is required for hydrolyzing polyurethane. More preferable lower limit of water temperature is 250°C. The hydrolyzed reaction product is supplied to a post-processor 7. When the target compound is a polyurethane foam, the hydrolyzed reaction product includes polyamine, polyol, water, CO 2 and unhydrolyzed substances. As there are various kinds of polyurethane foams, and polyurethane foams are made of various polyisocyanates and various polyols, the hydrolyzed reaction product includes polyamine which is a derivative of polyisocyanate used as a raw material of polyurethane foam to be hydrolyzed, and polyol which is also used as a raw material of the polyurethane foam to be hydrolyzed. In Figure 1, post-processor 7 includes a degassing device 8, a dewatering column 9, and a separator 10. In the degassing device 8, CO 2 generated when various bonds derived from the isocyanato groups in the polyurethane are hydrolyzed into amino groups (-NH 2 ) is removed from the hydrolyzed reaction product. A part of steam is also removed. In the dewatering column 9, CO 2 and water are removed. After dewatering, the obtained liquid is discharged from the dewatering column 9 to the separator 10 for separating polyol from polyamine. In the separator 10, a hydrolyzed and recovered light end containing polyamine as a main component and a hydrolyzed and recovered heavy end containing polyol as a main component are separated from each other. The post-processor 7 may include a plurality of degassing devices 8, dewatering columns 9, and separators 10, and the order in which they are provided is not limited to the positions shown in Figure 1. In addition, the post-processor 7 may further include a purifier on the downstream of the separator 10. When polymeric MDI or prepolymer-type polyisocyanate is used as a raw material polyisocyanate of polyurethane resin, polyamine and polyol in the hydrolyzed reaction product are hard to be separated from each other even if using the separator 10, and high cost will be required in an attempt to separate them from each other. In such a case, it is preferable that the post-processor 7 includes another reactor (apart from the reactor 2) instead of the separator 10. To another reactor, the resultant liquid discharged after dewatering is supplied, and alkylene oxide is added thereto to form polyether polyol. As a result, polyamine and polyol can be recovered in a form of polyether polyol. Polyamine in the discharged liquid works as an initiator for addition reaction, and a reaction in which alkylene oxide such as ethylene oxide or propylene oxide is added to polyol proceeds. As polyetherpolyol is usable as a raw material of polyurethane, this method is also capable of hydrolyzing a polyurethane resin to recover a raw material of polyurethane resin. In addition, this method is remarkably economical as compared with the case where polyamine and polyol, of which separation is difficult, are forcedly separated from each other. Therefore, it is recommended that the apparatus for hydrolyzing and recycling a polyurethane resin made of polymeric MDI and prepolymer-type polyisocyanate as raw materials includes a post-processor having a reactor capable of addition reaction. Figure 2 is a diagram showing another example of an apparatus for hydrolyzing and recycling polyurethane resin. A hydrolyzer 1 includes three reactors 21, 22, and 23, a supplying pump 3, and a heater 4. A reservoir 5, an extruder 6, and a post-processor 7 have the same configurations as those of Figure 1. In this example, after compressing polyurethane, a specific amount of the polyurethane is introduced into the reactor 21. In this case the compressed polyurethane is introduced into the reactor 21 together with heated and pressurized water, or either of them is introduced first and the rest is subsequently introduced. Then, valves 21a and 21b are closed. After the hydrolysis is completed in the reactor 21, a valve 21c is opened to supply the hydrolyzed reaction product to the post-processor 7. After the valves 21a and 21b are closed, that is, after the introduction of water and polyurethane into the reactor 21 is completed, valves 22a and 22b are opened and water and polyurethane are introduced into the reactor 22 to cause hydrolysis. After the hydrolyzed reaction product is supplied from the reactor 21 to the post-processor 7, the hydrolyzed reaction product is supplied from the reactor 22 to the post-processor 7. Similarly, hydrolysis is conducted in the reactor 23, and the hydrolyzed reaction product is supplied to the post-processor 7, while water and polyurethane are introduced into the reactor 21 and 22. As is the case of example shown in Figure 2, when a plurality (not limited to three) of reactors are used, hydrolysis and recovering can be conducted batchwise or semi-continuously in a plurality of lines simultaneously. Polyurethane may be introduced batchwise and water may be introduced continuously. In addition, each valve may be configured so that the flow rate is adjustable. Figure 3 is a diagram showing the case where a post-processor 7 includes a degassing device 8, a liquid separator 11, and a dewatering column 9. The liquid separator 11 separates a water-soluble hydrolyzed and recovered end and a non-water soluble hydrolyzed and recovered end from each other. Then, the dewatering column 9 dewaters the water-soluble hydrolyzed and recovered end to produce a dewatered hydrolyzed and recovered end. A decanter is preferable as the liquid separator 11. The present invention will be explained more specifically by way of examples. It is to be noted that the examples are for the explanatory purpose only and the present invention is not restricted to the examples. Example 1 A polyurethane soft foam (apparent density before compression: 19.5kg/m 3 ) synthesized from tol ylenediisocyanate (TDI) and polyetherpolyol (trifunctional; molecular weight of 3000) was hydrolyzed. First, an experiment for examining compression conditions was conducted using a compressor having a heater. Table 1 shows the heating temperature and the compression time, and the density of compressed product. Heating and compression temperature (°C) Compression time(min.) Density of compressed product (kg/m 3 ) 160 5 450 150 5 410 140 5 330 140 15 450 120 30 450 As is obvious from Table 1, it is understood that, when the compression was conducted at a temperature as high as 150 to 160 °C , the polyurethane soft foam was compressed to a density of 400kg/m 3 or more (about 20 times) in about 5 minutes. In addition, it is understood that, even when the compression was conducted at a temperature as low as 120°C, the polyurethane soft foam was compressed to an increased density in about 30 minutes. The compressed polyurethane resin was introduced into a reactor and was hydrolyzed and recovered under the conditions shown in Table 2. The reaction time was 30 minutes. As a result of hydrolysis, obtained were tol ylenediamine (TDA) derived from TDI and polyol. The results of experiments including the recovering rate of TDA (weight %), the recovering rate of polyol (weight %), and the hydrolyzing rate of polyurethane resin (weight %) are shown in Table 2 and Figure 5. The hydrolyzing rate of polyurethane resin shown in Table 2 was obtained from the following calculation: The recovering rate of TDA (weight %) indicates the amount of TDA actually recovered with respect to the theoretical amount of TDA obtained based on the assumption that all the amount of TDI in the polyurethane foam introduced into the reactor is recovered as TDA. Same definition is applied for the recovering rate of polyol. Experiment No. 1 2 3 4 5 6 7 Reaction temperature (°C) 200 250 270 318 320 340 370 Pressure (MPa) 10 10 20 20 20 20 20 Hydrolysis ratio (weight) 4 3 3 4 4 4 3 TDA recovering rate (weight%) 54.0 94.2 99.0 98.8 98.5 97.6 21.8 Polyol recovering rate (weight%) 21.0 84.2 94.5 99.0 97.3 93.4 13.1 Polyurethane hydrolyzing rate (weight%) 48.5 96.6 98.9 100 100 100 100 From Table 2 and Figure 5, it is understood that the hydrolyzing rate and recovering rate were excellent at 250 to 340°C. At 370°C, whereas the polyurethane recovering rate was 100%, the recovering rate of TDA and polyol was poor. This is because the condensation of TDA and decomposition of polyol proceeded. Example 2 A polyurethane hard foam (apparent density before compression: 36kg/m 3 ) synthesized from polymeric MDI and polyetherpolyol (sorbitol type; hydroxyl value of 420mgKOH/g) was hydrolyzed. As is the case of Example 1, an experiment for examining the compression conditions was conducted. Table 3 shows the heating temperature and compression time, and the density of compressed product. Heating and compression temperature (°C) Compression time(min.) Density of compressed product (kg/m 3 ) 180 5 700 170 5 700 160 10 700 150 15 570 140 30 700 140 60 700 As is obvious from Table 3, all the compressed products had a density as high as 700kg/m 3 , except for the compressed product obtained at a temperature of 150°C for 15 minutes. The compressed polyurethane resin was introduced into the reactor, and was hydrolyzed at a reaction temperature of 240 to 255°C and pressure of 10MPa. The hydrolyzed reaction product was introduced into a separator and was dewatered. Then, the liquid discharged after dewatering was put into an autoclave, to which propylene oxide was sequentially added at 110°C and 2.5kg/cm 2 (0.245MPa). As a result, polyol having hydroxyl value of 450mgKOH/g and a viscosity of 20,000Pa·s(25°C) was obtained. According to the hydrolyzing and recycling apparatus and process of the present invention, the target compounds, polyisocyanate derivatives, such as polyurethane resins can be recovered as a raw material or an intermediate material (derivatives) used for producing the target compounds. The apparatus of the present invention is capable of continuously hydrolyzing the target compound to be hydrolyzed. With this construction, the target compounds, which are discharged from a chemical plant as wastes in a molten state or in a solution state, can be continuously treated at constant conditions. In addition, as the apparatus of the present invention is capable of recovering polymer such as the polyurethane resins as polyol and polyamine, the apparatus of the present invention contributes to the promotion of recycling. The recovered amine compound can be effectively reused as a raw material for producing polyisocyanate compounds.

Claims: A process for hydrolyzing and recycling a polyurethane resin to recover polyol and/or polyamine compounds comprising the steps of: supplying the polyurethane resin as a target compound to be hydrolyzed into a reactor; hydrolyzing the polyurethane resin by bringing only water at 190 to 370°C under a high pressure in a liquid state into contact with the polyurethane resin in the reactor; and conducting post-processing including dewatering, addition, distillation, separation, and liquid separation for a hydrolyzed reaction product discharged from the reactor. A hydrolyzing and recycling process according to claim 1, wherein the supplying step includes a step of continuously supplying the polyurethane resin to be hydrolyzed to the reactor. A hydrolyzing and recycling process according to claims 1 or 2, wherein the polyurethane resin includes a polyurethane foam, the process further comprising a step of pre-compressing the polyurethane foam as the polyurethane resin. A hydrolyzing and recycling process according to claim 3, wherein the pre-compressing step includes a step of compressing the polyurethane foam while heating the same at 100 to 250 °C. A hydrolyzing and recycling process according to any one of claims 1 to 4, wherein the hydrolyzing step includes steps of heating and pressurizing the water to the liquid state, and continuously supplying the water into the reactor. A hydrolyzing and recycling process according to any one of claims 1 to 5, wherein the hydrolyzing step includes a step of heating and pressurizing the water inside the reactor. A hydrolyzing and recycling process according to any one of claims 1 to 6, wherein in the hydrolyzing step, the pressure inside the reactor is set to 3 to 30MPa, and water is brought in an amount of 1.0 to 10.0 times (weight ratio) to the polyurethane resin into contact with the polyurethane resin. A hydrolyzing and recycling process according to any one of claims 1 to 7, wherein the post-processing step includesdegassing, dewatering, and separation in the order thereof. A hydrolyzing and recycling process according to claim 8, wherein the separation is conducted by a reduced-pressure distillation. A hydrolyzing and recycling process according to any one of claims 1 to 9, wherein the post-processing step includes a step of conducting an additional reaction between a hydrolyzed reaction product and an alkylene oxide.

Inventors: FUKUZATO RYUICHI, KATO OSAMU, KODAMA KATSUHISA, MATSUDA TERUKAZU, NAGASE YOSHIYUKI, NAITO TAKAO, NISHIDA SATOSHI, SUZUKI SHIGETOSHI, YAMAGATA MASAHIRO, FUKUZATO, RYUICHI, KATO, OSAMU, KODAMA, KATSUHISA, MATSUDA, TERUKAZU, NAGASE, YOSHIYUKI, NAITO, TAKAO, NISHIDA, SATOSHI, SUZUKI, SHIGETOSHI, YAMAGATA, MASAHIRO, FUKUZATO, Ryuichi, Osaka Branch Office in Kobe, KATO, Osamu, Osaka Branch Office in Kobe, KODAMA, Katsuhisa, Takeda Chemical Ind., Ltd., MATSUDA, Terukazu, Takeda Chemical Ind., Ltd., NAGASE, Yoshiyuki, Kobe Corp. Res. Lab. in Kobe, NAITO, Takao, Takeda Chemical Ind., Ltd., NISHIDA, Satoshi, Osaka Branch Office in Kobe, SUZUKI, Shigetoshi, Takeda Chemical Ind., Ltd., YAMAGATA, Masahiro, Osaka Branch Office in Kobe
Applicants: KOBE STEEL LTD, MITSUI TAKEDA CHEMICALS INC, KABUSHIKI KAISHA KOBE SEIKO SHO, MITSUI TAKEDA CHEMICALS, INC.
Application year: 1998
Main classification: C07C211
IPC codes: C08J11, C07C209, C07C211