CAPACITOR WITH AN ELECTRODE COMPOSED OF A SINTERED BODY OF PARTIALLY NITRIDED NIOBIUM POWDER

Abstract: In a capacitor comprising a pair of electrodes and a dielectric substance intervening between the two electrodes, one of the electrodes is composed of sintered niobium nitride. Preferably, the dielectric substance is composed of niobium oxide and the electrode other than the electrode composed of sintered niobium nitride is composed of an ingredient selected from electrolytes, organic semiconductors and inorganic semiconductors. This capacitor has good environmental stability and good leak current characteristics.

Description: Technical Field This invention relates to a partially nitrided niobium powder for a capacitor electrode, a process for preparing this power and to a novel capacitor in which one of the electrodes is composed of a sintered body of said niobium powder. More particularly, it relates in one aspect to a capacitor which is inexpensive and exhibits good leak current characteristics, and a capacitor which has a large capacitance, especially a large capacitance per unit weight at a high frequency, and exhibits good leak characteristics. Background Art As an electrode of a capacitor made of a sintered metal, those which are composed of sintered aluminum, tantalum and alloys thereof are known. These capacitors have widely used in various fields. For example, for a capacitor used in a smoothing. circuit for obtaining a direct current from an alternating current, it is desired that the capacitor possesses a low impedance and a large capacitance at a high frequency for suppressing the occurrence of spike-shaped voltage and enhancing the efficiency of conversion to a direct current. The above-mentioned sintered metals used as a capacitor electrode have problems. Namely, sintered aluminum has poor environmental characteristics such as moisture resistance and chemical characteristics, and sintered tantalum is expensive. Sintered niobium is also known as a material used for a capacitor electrode, and not possessing the problems encountered with sintered aluminum and tantalum, but, it has another problem that oxygen adsorbed on its surface influences dielectrics as mentioned below, and thus, the leak current characteristics are not satisfactory and it is of poor practical use. To provide a capacitor used in a smoothing circuit and having an enhanced capacitance at a high frequency, the volume of a sintered metal substrate made of, for example, tantalum or aluminum, should be increased. The increase in volume of the sintered metal substrate is inconsistent with a requirement of miniaturization of a capacitor. Among others, tantalum gives a relatively satisfactory for the requirements of an enhanced capacitance at a high frequency and a miniaturization of a capacitor, but, it is still not completely satisfactory for these requirements. Usually a tantalum oxide is used as a dielectric substance for a capacitor with an electrode composed of sintered tantalum bodies. However, if a material having a dielectric constant larger than that of tantalum oxide is used as a dielectric substance, the capacitor can be more miniaturized. As examples of the material having a large dielectric constant, there can be mentioned titanium oxide and niobium oxide. But, these materials exhibit poor leak current (hereinafter abbreviated to "LC") characteristics. Disclosure of Invention The inventors have found, first, that sintered bodies of niobium nitride are advantageous in that the amount of oxygen deposited on the surface thereof is minor and the leak current characteristics of the capacitor are satisfactory, and secondly, that the above-mentioned problem as for LC characteristics of a capacitor with niobium oxide dielectrics is due to the fact that oxygen deposited on the surface of sintered bodies influences the dielectric substance. Based on these findings, the inventors have completed the present invention. The inventors have further found that, if an electrode other than the electrode composed of sintered niobium nitride bodies is made of at least one compound selected from organic semiconductors and inorganic semiconductors, which do not have a capability of supplying oxygen to an undue extent, a capacitor having a large capacitance at a high frequency can be obtained. Further, if, as the organic semiconductor or the inorganic semiconductor, those which have an electrical conductivity of 10 -2 S·cm -1 to 10 3 S·cm -1 are used, a capacitor having a more reduced impedance can be obtained. Thus, in one aspect of the present invention, there is provided a partially nitrided niobium powder for a capaitor electrode characterized by having a bound nitrogen content in the range of 10 ppm to 200,000 ppm by weight. The partially nitrided niobium powder preferably has a bound nitrogen content in the range of 100 ppm to 50,000 ppm by weight, and an average particle diameter of 0.5 µm to 100 µm. In another aspect of the present invention, there is provided a sintered body of a partially nitrided niobium powder having a bound nitrogen content in the range of 10 ppm to 200 , 000 ppm by weight. In a further aspect of the present invention, there is provided a capacitor comprising a pair of electrodes and a dielectric substance intervening between the electrodes, characterized in that one of the electrodes is composed of a sintered body of a partially nitrided niobium powder having a bound nitrogen content in the range of 10 ppm to 200,000 ppm by weight. The dielectric substance of the above-mentioned capacitor is preferably made of niobium oxide, more preferably made of niobium oxide prepared by electrolytic oxidation of the sintered body of partially nitrided niobium powder. The other of the two electrodes is preferably made of at least one ingredient selected from electrolytes, organic semiconductors and inorganic semiconductors, more preferably at least one ingredient selected from organic semiconductors and inorganic conductors, which have an electrical conductivity of from 10 -2 S·cm -1 to 10 3 S·cm -1 . Brief Description of the Drawing Figure 1 is a partially cutaway view in perspective specifically illustrating one example of the capacitor of the present invention. Best Mode for Carrying Out the Invention The partially nitrided niobium nitride constituting one of the electrodes in the capacitor of the invention is made by partially nitrifying metallic niobium. For example, niobium nitride of a powdery form is made by nitrifying the surfaces of particles of powdery niobium in a nitrogen gas atmosphere. In this instance, the amount of nitrogen bound to the niobium is in the range of from 10 to 200,000 ppm by weight, preferably 100 to 50,000 ppm by weight. For nitrifying niobium into partially nitrided niobium nitride having the desired nitrogen content, the temperature employed is not higher than 2,000°C and the time employed is in several tens of hours. Generally, as the temperature for nitrification becomes high, the particle surfaces of powdery niobium are nitrified in a shorter time. Even at room temperature, when powdery niobium is fluidized for several tens of hours, powdery niobium nitride containing several hundreds ppm of nitrogen is obtained. The thus-obtained partially nitrided niobium powder has a shape approximately similar to that of the powdery niobium used as the raw material. In one example, if a powdery niobium mass obtained by pulverizing a niobium lump is used as a raw material, partially nitrided niobium powder having various shapes which are peculiar to pulverized mass is obtained. In another example, if powdery niobium in the form of a secondary particle is used, which is prepared by reducing potassium fluoroniobate to give finely divided particles, and granulating the finely divided particles into secondary particles, then, partially nitrided niobium powder similar to the secondary particles is obtained. Further, for example, if powdery niobium having an average particle diameter of from 0.5 µm to 100 µm is used, partially nitrided niobium powder having a similar average particle diameter is obtained. The sintered body of partially nitrided niobium powder is obtained by sintering, for example, partially nitrided niobium powder at a high temperature in vacuo. In one example, partially nitrided niobium powder is press-molded and then the molded product is allowed to stand at a temperature of 1,000 to 2,000°C and a pressure of 13,3 to 13,3.10 -5 Pa (10 -1 to 10 -6 Torr for several minutes to several hours to give a sintered partially nitrided niobium. If the degree of vacuum is insufficient at sintering, air is entrapped in the powdery material during sintering, oxidation occurs simultaneously with nitrification with the result that the capacitor with the niobium nitride electrode has a poor performance. Generally a suitable sintering temperature varies depending upon the particle diameter of the partially nitrided niobium powder, and, the smaller the particle diameter, the lower the sintering temperature. As the dielectric substance used in the capacitor of the invention, there can be mentioned, for example, tantalum oxide, niobium oxide, polymeric substances and ceramic compounds. When tantalum oxide is used as a dielectric substance, the tantalum oxide can be prepared by depositing a tantalum-containing complex such as, for example, an alkoxy complex or an acetylacetonato complex on an electrode, and then, subjecting the deposit to hydrolysis and/or pyrolysis. When niobium oxide is used as a dielectric substance, the niobium oxide can be prepared by chemically converting a niobium nitride electrode into niobium oxide in an electrolyte, or by depositing a niobium-containing complex such as, for example, an alkoxy complex or an acetylacetonato complex on an electrode, and then, subjecting the deposit to hydrolysis and/or pyrolysis. Thus, a niobium oxide dielectrics can be formed on the surface of niobium nitride electrode by converting a niobium nitride electrode into niobium oxide in an electrolyte or subjecting a niobium-containing complex on a niobium nitride electrode to hydrolysis and/or pyrolysis. The conversion of niobium nitride into niobium oxide in an electrolyte can be effected usually by using an aqueous protonic acid, for example, an aqueous 0.1% phosphoric acid solution or sulfuric acid solution. In the case where niobium nitride is formed into the niobium dielectrics in an electrolyte, the capacitor of the invention is an electrolytic capacitor with a positive electrode composed of niobium nitride. In the case where a niobium-containing complex is subjected to hydrolysis and/or pyrolysis to yield niobium oxide, the niobium nitride has theoretically no polarity and can be used either as a positive electrode or a negative electrode. The polymeric substance dielectrics can be prepared by, as described in Japanese Unexamined Patent Publication No. H7-63045, a process wherein a gaseous or liquid monomer is introduced in voids or pores within metal, followed by polymerization; a process wherein a solution of a polymeric substance in a suitable solvent is introduced; and a process wherein a molten polymeric substance is introduced. As specific examples of the high polymeric substances, there can be mentioned a fluororesin, an alkyd resin, an acrylic resin, a polyester resin such as polyethylene terephthalate, a vinyl resin, a xylylene resin and a phenol resin. The dielectric substance composed of a ceramic compound can be prepared by a process for producing a compound with perovskite structure on a surface of metal having voids or pores, as described in Japanese Unexamined Patent Publication No. H7-85461. As specific examples of the compound with peroviskite structure, there can be mentioned BaTiO 3 , SrTiO 3 , MgTiO 3 and BaSnO 3 . The electrode other than the niobium nitride electrode of the capacitor of the invention is not particularly limited, and can be composed of at least one ingredient selected from electrolytes well known in the aluminum electrolytic capacitor industry, organic semiconductors and inorganic semiconductors. As specific examples of the electrolytes, there can be mentioned a mixed dimethylformamide/ethylene glycol liquid containing 5% by weight of isobutyltripropylammonium borontetrafluoride, and a mixed propylene carbonate/ethylene glycol liquid containing 7% by weight of tetraethylammonium borontetrafluoride. As examples of the organic semiconductors, there can be mentioned an organic semiconductor composed of benzopyroline tetramer and chloranil, an organic semiconductor predominantly comprised of tetrathiotetracene, an organic semiconductor predominantly comprised of tetracyano-quinodimethane, and organic semiconductors predominantly comprised of electrically conductive polymers represented by the following formula (1) or (2), which are doped with a dopant. wherein R 1 , R 2 , R 3 and R 4 independently represents hydrogen, an alkyl group having 1 to 6 carbon atoms or an alkoxy group having 1 to 6 carbon atoms, X represents an oxygen, sulfur or nitrogen atom, R 5 represents only when X is a nitrogen atom, and represents hydrogen or an alkyl group having 1 to 6 carbon atoms, R 1 and R 2 may form together a ring, and R 3 and R 4 also may form together a ring. As specific examples of the electrically conductive polymers of formulae (1) and (2), there can be mentioned polyaniline, polyoxyphenylene, polyphenylene sulfide, polythiophene, polyfuran, polypyrrole and polymethylpyrrole. As examples of the inorganic semiconductors, there can be mentioned inorganic semiconductors predominantly comprised of lead dioxide or manganese dioxide, and inorganic semiconductors composed of triiron tetraoxide. These semiconductors may be used either alone or as a mixture of at least two thereof. When organic semiconductors and inorganic semiconductors having an electrical conductivity of 10 -2 S·cm -1 to 10 3 S·cm -1 are used as the organic semiconductors and inorganic conductors, capacitors having a far reduced impedance and a more enhanced capacitance at a high frequency are obtained. The structure of the capacitor of the invention may be those which have heretofore been employed, provided that the capacitor comprises a pair of electrodes and a dielectric intervening between the electrodes wherein one of said electrodes is composed of a sintered body of the partially nitrided niobium powder of the present invention. One specific example of the capacitor of the invention is illustrated in Fig. 1, wherein a sintered body of partially nitrided niobium powder 1 composed of a plurality of sintered bodies of partially nitrided niobium powder is placed as an electrode and on which niobium oxide dielectric layers have been formed by chemically converting the surfaces of the sintered bodies of partially nitrided niobium nitride powder into niobium oxide in an electrolyte, or by subjecting a niobium-containing complex to hydrolysis and/or pyrolysis to produce niobium oxide on the surfaces of the sintered bodies of partially nitrided niobium powder. The other electrode is formed on the dielectric layer. Further, a carbon paste 2 and a silver paste 3 are formed in this order on the other electrode, and then, the thus-prepared laminated product is encapsulated with a sealing material such as epoxy resin to form a capacitor. The capacitor is provided with a niobium lead 4 which has been sintered in integrated with the sintered bodies of partially nitrided niobium powder or which has been welded to the sintered bodies of partially nitrided niobium powder. The capacitor is assembled together with a positive electrode lead 5 and a negative electrode lead 6 and the assembly is enclosed by an outer resin covering 7. The capacitor provided with the niobium lead 4, illustrated in Fig. 1, is a rectangular parallelopiped, but, its shape is not particularly limited thereto and may be, for example, cylindrical. The capacitor of the invention will now be described specifically by the following examples. Examples 1 to 7 Powdery niobium having an average particle diameter of 10 to 40 µm was treated at 400°C in a nitrogen atmosphere to give partially nitrided powdery niobium. The amount of nitrogen bound to niobium by nitrification was about 2,000 ppm by weight. The partially nitrided niobium powder was sintered at 1,500°C in vacuo to give sintered bodies of partially nitrided niobium powder having a diameter of 10 mm and a thickness of about 1 mm, and containing pores having an average diameter of 3 µm with a porosity of 45%. The sintered bodies of partially nitrided niobium powder were treated in an aqueous phosphoric acid solution at a voltage of 20 V to form a niobium oxide dielectric layer on the surface of each sintered body. Each of the substances for forming an electrode other than the electrode composed of the sintered bodies of partially nitrided niobium powder, as shown in Table 1, was deposited on a plurality of the dielectric layer-formed sintered bodies of partially nitrided niobium powder. Further, a carbon paste and then a silver paste were laminated in this order on the dielectric layer-formed sintered bodies of partially nitrided niobium powder. Then the thus-laminated product was encapsulated with an epoxy resin to give a capacitor. The capacitance at 100 kHz and the LC value at 4 V were measured. The results are shown in Table 2. Example No. Other electrode and electrical conductivity(S·cm -1 ) Electrode forming method Example 1 Chloranil complex of tetrathiotetracene 2 x 10 0 Repeat of immersion in solution of the compound described in the left column, and drying Example 2 Isoquinoline complex of tetracyanoquinodimethane 3 x 10 0 Repeat of immersion in solution of the compound described in the left column, and drying Example 3 Dope of polyaniline in toluensulfonic 3 x 10 1 Repeat of oxidation reaction in aniline solution Example 4 Dope of polypyrrole in toluenesulfonic acid 5 x 10 1 Repeat of oxidation rection in pyrrole solution Example 5 Dope of polythiophene in toluenesulfonic acid 4 x 10 1 Repeat of oxidation reaction in thiophene solution Example 6 Mixture of lead dioxide and lead sulfate (lead dioxide 97 wt%) 5 x 10 1 Repeat of oxidation reaction of lead acetate solution Example 7 Mixture of manganese dioxide and lead dioxide (lead dioxide 95 wt%) 5 x 10 1 Thermal decomposition of manganese nitrate (250°C twice), then repeat of oxidation reaction of lead acetate solution Examples 8 and 9 Partially nitrided powdery niobium having an average particle diameter of 40 to 80 µm and a bound nitrogen content of about 10,000 ppm by weight was sintered at 1,600°C in vacuo to give sintered bodies of partially nitrided niobium powder having a diameter of 10 mm and a thickness of 1 mm, and containing pores having an average diameter of 7 µm with a porosity of 55%. The sintered bodies of partially nitrided niobium powder were immersed in a bath of pentaethyl niobate liquid, and thereafter, the sintered bodies of partially nitrided niobium powder taken out from the bath were maintained at 85°C in a steam and then dried at 350°C whereby a dielectric layer composed of niobium oxide was formed on the sintered bodies of partially nitrided niobium powder. Each of chloranil complex of tetrathiotetracene (Example 8) and a mixture of lead acetate and lead sulfate (Example 9) for forming an electrode other than the electrode composed of the sintered bodies of partially nitrided niobium powder was deposited on a plurality of the dielectric layer-formed sintered bodies of partially nitrided niobium powder by the same procedures employed in Example 1 and Example 6, respectively. Further, a carbon paste and then a silver paste were laminated in this order on the dielectric layer-formed sintered bodies of partially nitrided niobium powder. Then the laminated product was encapsulated with an epoxy resin to give a capacitor. The properties of the capacitor were evaluated. The results are shown in Table 2. Comparative Examples 1 and 2 Powdery tantalum having an average particle diameter of 10 to 40 µm was sintered at 1,500°C in vacuo to give sintered tantalum bodies having a diameter of 10 mm and a thickness of about 1 mm, and containing pores having an average diameter of 3 µm with a porosity of 45%. The sintered tantalum bodies were treated in an aqueous phosphoric acid solution at a voltage of 20 V to form a tantalum oxide dielectric layer on the surface of each sintered body. Each of chloranil complex of tetrathiotetracene (Comparative Example 1) and a mixture of lead acetate and lead sulfate (Comparative Example 2) for forming an electrode other than the electrode composed of the sintered tantalum bodies was deposited on a plurality of the dielectric layer-formed sintered tantalum bodies by the same procedures employed in Example 1 and Example 6, respectively. Further, a carbon paste and then a silver paste were laminated in this order on the dielectric layer-formed sintered tantalum bodies, and then, the thus-laminated product was encapsulated with an epoxy resin by the same procedures as employed in the above-mentioned Examples to give a capacitor. The properties of the capacitor were evaluated. The results are shown in Table 2. Comparative Examples 3 and 4 The procedures employed in Example 1 and Example 6 were repeated wherein the powdery niobium was not nitrified and was sintered to give sintered niobium bodies, and capacitors were made from the sintered niobium bodies. The properties of the capacitors were evaluated. The results are shown in Table 2. Capacitance (100 kHz) µF LC (4V) µA Example 1 55 0.9 Example 2 50 0.8 Example 3 60 1.2 Example 4 60 1.0 Example 5 55 1.2 Example 6 62 0.8 Example 7 60 1.0 Example 8 40 0.3 Example 9 40 0.3 Comparative Example 1 24 0.02 Comparative Example 2 26 0.04 Comparative Example 3 54 14 Comparative Example 4 57 18 Example 10 The same sintered bodies of partially nitrided niobium powder as prepared in Example 1 were immersed in a bath of pentaethyl tantalate liquid, and thereafter, the sintered bodies of partially nitrided niobium powder taken out from the bath were maintained at 85°C in a steam and then dried at 450°C whereby a dielectric layer composed of tantalum oxide was formed on the sintered bodies of partially nitrided niobium powder. Then an electrolyte composed of a 5% solution of isobutyltripropylammonium borontetrafluoride electrolyte in a mixed liquid of dimethylformamide and ethylene glycol, was applied onto the sintered bodies of partially nitrided niobium powder. The electrolyte-applied sintered bodies of partially nitrided niobium powder were charged in a can, and the can was sealed to give a capacitor. The properties of the capacitor were evaluated. The results are shown in Table 3. Comparative Example 5 The procedures employed in Example 10 were repeated to make a capacitor wherein sintered niobium bodies were used instead of the sintered bodies of partially nitrided niobium powder with all other conditions remaining the same. The properties of the capacitor were evaluated. The results are shown in Table 3. Example 11 By the same procedures as employed in Example 1, sintered bodies of partially nitrided niobium powder were made and then niobium oxide dielectric layers were formed on the sintered bodies of partially nitrided niobium powder. An electrolyte was applied to the dielectric layer-formed sintered bodies of partially nitrided niobium powder, and the electrolyte-applied product was charged in a can and the can was sealed to give a capacitor by the same procedures as described in Example 10. The properties of the capacitor were evaluated. The results are shown in Table 3. Comparative Example 6 The procedures as employed in Example 11 were repeated to make a capacitor wherein sintered niobium bodies were used instead of the sintered bodies of partially nitrided niobium powder with all other conditions remaining the same. The properties of the capacitor were evaluated. The results are shown in Table 3. LC (4V) µA Example 10 0.3 Example 11 0.4 Comparative Example 5 9 Comparative Example 6 10 Example 12 By the same procedures as employed in Example 1, sintered bodies of partially nitrided niobium powder were made and then niobium oxide dielectric layers were formed on the sintered bodies of partially nitrided niobium powder. The dielectric layer-formed sintered bodies of partially nitrided niobium powder were immersed in an aqueous equimolar solution containing 0.01 mole/l of iron(II) sulfate and iron(III) sulfate, and then, an excessive amount of an aqueous sodium hydroxide solution was added whereby triiron tetraoxide as the electrode other than the partailly nitrided niobium powder electrode was formed on the dielectric layer-formed sintered bodies of partially nitrided niobium powder. A carbon paste and then a silver paste were laminated in this order on the dielectric layer-formed sintered bodies of partially nitrided niobium powder, and then, the thus-laminated product was encapsulated with an epoxy resin by the same procedures as employed in the above-mentioned Examples to give a capacitor. The triiron tetraoxide used had an electrical conductivity of 10 -3 S·cm -1 . The properties of the capacitor were evaluated. The results are shown in Table 4. Comparative Example 7 The procedures as employed in Example 12 were repeated to make a capacitor wherein sintered niobium bodies were used instead of the sintered bodies of partially nitrided niobium powder with all other conditions remaining the same. The properties of the capacitor were evaluated. The results are shown in Table 4. Capacitance (100 kHz) µF LC(4V) µA Example 12 38 0.7 Comparative Example 7 38 16 Industrial Applicability The capacitor of the invention with an electrode composed of sintered bodies of partially nitrided niobium powder exhibits excellent environmental stability and leak current (LC) characteristics. Especially the capacitor having an electrode composed of sintered bodies of partially nitrided niobium powder and the other electrode composed of at least one ingredient selected from organic semiconductors and inorganic semiconductors, and having a niobium oxide dielectric intervening between the two electrodes has an enhanced capacitance per unit weight at a high frequency as well as excellent leak current (LC) characteristics. Therefore, the capacitor of the invention is suitable for a smoothing circuit of a power source.

Claims: A partially nitrided niobium powder for a capacitor electrode characterized by having a bound nitrogen content in the range of 10 ppm to 200,000 ppm by weight. The partially nitrided niobium powder according to claim 1, wherein the content of bound nitrogen is in the range of 100 ppm to 50,000 ppm by weight. The partially nitrided niobium powder according to claim 1 or 2, which has an average particle diameter in the range of 0.5 µm to 100 µm. A process for preparing the partially nitrided niobium powder as claimed in any one of claims 1 to 3, characterized by maintaining powdery niobium in a nitrogen gas atmosphere at a temperature of not higher than 2,000°C. The process according to claim 4, wherein the powdery niobium has an average particle diameter in the range of 0.5 µm to 100 µm to prepare a partially nitrided niobium powder having an average particle diameter in the range of 0.5 µm to 100 µm. A sintered body of the partially nitrided niobium powder as claimed in any one of claims 1 to 3. The sintered body according to claim 6, which has a niobium oxide dielectric formed on a surface of the sintered body of a partially nitrided niobium powder. A process for producing a sintered body, characterized by sintering the partially nitrided niobium powder as claimed in any one of claims 1 to 3 at a temperature in the range of 1,000°C to 2,000°C under a pressure in the range of 13,3 Pa to 13,3 10 -5 Pa (10 -1 Torr to 10 -6 Torr). A capacitor comprising a pair of electrodes and a dielectric substance intervening between the electrodes, characterized in that one of said electrodes is composed of a sintered body of the partially nitrided niobium powder as claimed in any one of claims 1 to 3. The capacitor according to claim 9, wherein the dielectric substance is selected from niobium oxide, tantalum oxide, polymeric substances and ceramic compounds. The capacitor according to claim 9, wherein the dielectric substance comprises niobium oxide. The capacitor according to claim 11, wherein the dielectric substance is formed on said electrode composed of the sintered body of partially nitrided niobium powder by conversion-treating said electrode composed of the sintered body in an electrolyte, or subjecting a niobium-containing complex to hydrolysis, pyrolysis or a combination of hydrolysis with pyrolysis on the electrode composed of the sintered body. The capacitor according to any one of claims 9 to 12, wherein the electrode other than the electrode composed of the sintered body of partially nitrided niobium powder is made of at least one ingredient selected from electrolytes, organic semiconductors and inorganic semiconductors. The capacitor according to any one of claims 9 to 12, wherein the electrode other than the electrode composed of the sintered body of partially nitrided niobium powder is made of at least one ingredient selected from organic semiconductors and inorganic semiconductors, which have an electrical conductivity of 10 -2 S·cm -1 to 10 3 S·cm -1 .

Inventors: NAITO KAZUMI, NAITO, KAZUMI, Naito, Kazumi, Showa Denko K.K.
Applicants: SHOWA DENKO KK, SHOWA DENKO KABUSHIKI KAISHA
Application year: 1998
Main classification: G01R31
IPC codes: H01G9, B22F1, B22F5