REVERSE MODE ELECTRO-OPTICAL FILM COMPOSED OF ONE MUTUAL DISPERSION OF POLYMERS AND LIQUID CRYSTALS

Abstract: A new type of composite material made by liquid crystals and polymers which is naturally transparent to light and becomes opaque by application of electric fields has been invented. In this material the two components (polymer and liquid crystal) are mutually dispersed one in the other. With respect to other similar inventions, concerning mutual dispersed liquid crystal and polymers, this new type of film presents the following advantages: it is highly adhesive to glass or plastic supports since it contains more than 50 % of the polymer component; it can be produced starting from a binary emulsion of a thermotropic liquid crystal and a non liquid crystal organic compound, differently from other mutual dispersion of liquid crystals and polymers, which are produced by polymerising liquid crystals solution. It has a haze free electrooptical transmission.

Description: DESCRIPTION REVERSE MODE ELECTRO-OPTICAL FILM COMPOSED OF ONE MUTUAL DISPERSION OF POLYMERS AND LIQUID CRYSTALS A new type of composite material made by liquid crystals and polymers which is naturally transparent to light and becomes opaque by application of electric fields has been invented. In this material the two components ( polymer and liquid crystal) are mutually dispersed one in the other With respect to other similar inventions, concerning mutual dispersed liquid crystal and polymers, this new type of film presents the following advantages: 1 . It is highly adhesive to glass or plastic supports since it contains more than 50% of the polymer component. 2. It can be produced starting from a binary emulsion of a thermotropic liquid crystal and a non liquid crystal organic compound, differently from other mutual dispersion of liquid crystals and polymers, which are produced by polymerising liquid crystals solution. 3. It has a haze free electrooptical transmition BACKGROUND OF THE INVENTION In the last fifteen years many composite electrooptical films made by liquid crystals and polymers have been produced. Some of these film are made by droplets of liquid crystal dispersed in polymers and are usually defined as polymer dispersed liquid crystals (PDLC). Direct Mode PDLC, are those films being opaque in their natural state, and becoming transparent under the application of electric fields (1 ,2). In order to extend the application field of PDLC films, Reverse mode PDLC have been also invented (3,4). Another class of composite films , are those containing small percentages ( typically 3%- 10%) of polymers dispersed in liquid crystal layers (5-10 ). These films, usually defined as GELS, have the advantage to be transparent in their natural state and furthermore they are almost haze free, but they have a poor adhesive character. Recently a new class of liquid crystals and polymer composite films have been produced where comparable amounts of polymer and liquid crystals are mutually dispersed one in the other ( 1 1). No droplets of liquid crystals dispersed in polymer, or droplets of polymer in the liquid crystals are present. Despite of their complex morphology these films are almost haze free in their transparent state. The material above mentioned do not consent to optimise the full set of properties required for their application in display technology, smart windows production etc, where they must be inserted as tin films between glass or plastic supports, in order to confer a variable light transmission character to the system. Important requirements are: 1. Reverse mode character. The film has to be naturally transparent and must become opaque under the action of an electric field. 2. The optical contrast must be high. 3. In the clear state the optical transmission has to be almost constant as a function of the viewing angle ( the angle between the perpendicular to the film and the viewing direction). Such a property of the films is usually defined as "haze free" character. 4 The films must have a very good adhesion to the surface of glass or plastic supports This property is required m order to simplify the construction of optical devices and in order to confer to these devices a strong mechanical stability Electrooptical films made by polymers and liquid crystals invented since now cannot be optimised with respect to all the above requirements Reverse Mode PDLC films ( those containing molecular oriented droplets of liquid crystals dispersed in a continuos polymer matrix) can be easily optimised with respect to above 1 ,2,4 properties, but it is very difficult . due to the morphology of the svstcm, to confer them an haze tree character Films of liquid crystals containing small percentages of polymers can be easily optimised with respect to 1,2,3 properties, but they will have a poor adhesion character, since this property is directly correlated to the polymer abundance Films of mutually dispersed polymer and liquid crystals, having a high polymer concentration, have been produced until now only in the direct scattering mode configuration, in such a way that they are optimised only with respect to 2,3.4 properties π i) It is therefore an object of present invention to provide a film made by a mutual dispersion of polymer and liquid crystal where the liquid crystal domains remains in an oriented state in absence of directly applied electric field, thus having a so called reverse mode electrooptical behaviour It is another object of the present invention to provide a film made by a mutual dispersion of polymer and liquid crystals having a haze free electrooptical character, due to the morphology of the system It is another object of the present invention to provide a film made by a mutual dispersion of polymer and liquid crystals having a high electrooptical contrast. It is still another object of the present invention to provide a film made by a mutual dispersion of polymer and liquid crystal having a high polymer concentration, preferentially above 50% in weight, in order to posses a high adhesion to glass or plastic substrates. It is a further object of the present invention to provide a film made by a mutual dispersion of polymer and liquid crystals having all the above mentioned properties and where the polymer component is obtained both a) by polymerising in situ an organic monomer not belonging to liquid crystalline phases, b) by polymerising in situ an organic monomer belonging to the liquid crystal class. It is a further object of the present invention to provide new processes to prepare the above films. It is a final object of the present invention to provide an electrooptical cell where the film above mentioned it is sandwiched between two supporting conductive glass or plastic supports and where a d.c. or a.c. electric power supply it is used in order to provide an electric field to switch the film from a transparent to an opaque state. In order to achieve these objects two processes which are also object of the present invention have been developed. First process: 1. A liquid crystal and an organic monomer having the property to form a fluid emulsion, where droplets of liquid crystals are dispersed into the organic monomer, are selected. 2 The two components plus some minor component such as polymerisation activators or dyes if required are mixed together to form the emulsion 3 The emulsion is deposited above glass or plastic conductive supports 4 A magnetic field is applied to the system, in order to orient the liquid crystal contained into the droplets 5 The polymerisation of the monomer is activated by u v light or thermally, depending on the chemical nature of the monomer The chemical properties of the monomer to be used must be such that - they must form an emulsion with the liquid crvstal - they must polymerise forming a mutual irregular dispersion of the liquid crystal and polymer It has been found by the authors of the present invention that a compound that satisfies to both these condition is the Tn-Propilen-Glycol- Diacrylate (TPGD) corresponding to the following chemical formula The polymerisation of the monomer in the presence of the magnetic field will ensure a * structure of the cured film similar to that described in fig la, where the liquid crystal molecules keep naturally a common orientation If the refractive index of the polymer is matched with the no component of the liquid crystal refractive index the film will appear transparent, since no scattering of the light will be caused by the irregular distribution of the to component ( the polymer and the Liquid Crystal) In order to use the films to control the light transmission two other important conditions must be fulfilled: - The dielectric anisotropy of the liquid crystal must be negative and its refractive index anisotropy must be quite large. In this case, when an electric field is applied to the film, the liquid crystal molecules will be gradually tilted perpendicularly to their natural direction and the film will gradually become opaque due to the mismatching of the refractive indices of the polymer and liquid crystal along the viewing direction, as it is indicated in fig. lb. Second Process 1. Two low weight liquid crystals which form a homogeneous solution are mixed. One of this liquid crystals is a monomer containing double bonds in such a way that it can be polymerised by U.V. light or by thermal activation. 2. The above solution, added by some minor component such as polymerisation activators, dyes or spacers, is deposited as a tin fluid film between glass or plastic substrates being coated by a suitable tick ITO layer. 3. The polymerisation of the liquid crystal monomer is accomplished by U.V. or by thermal activation. It must be underlined that in the case of this second process no external fields or additional coatings, with respect to the conductive ITO coatings, are needed in order to ensure a stable orientation of the liquid crystal into the final solid film. The requirements for the liquid crystals remaining dispersed into the solid matrix are the same as those described above in the case of the first process. EXAMPLE 1 In the following example the preparation, according to the first of the proposed processes, and operation of the film which is the object of the present invention is described. Starting materials for film preparation were: 1. The liquid crystal ZLI4788-000 (ZLI) from MERCK 2. The thri-Propylen-glycol-Diacrylate (TPGD) from HALDRICH 3. The radical polymerisation starter IRGACURE 651 from CIBA-GEIGY. An emulsion containing 38.6 t% ZLI4788-000, 51 wt% TPGD, O.4 WT% IRGACURE was prepared and successively spread as a tin film on glass support which surface was coated by an Indium Tin Oxide (ITO) layer to ensure electric conductivity. A suitable amount of spacers was also added to the film in order to keep a 15 micron constant thickness across the film surface, once that another glass support, analogous to the one above mentioned was used to cover the bottom surface of the film. The cell prepared as above said was than placed in a 2 tesla magnetic field direct along the noπnal to the plane of the cell. The cell was than U.V. irradiated for one minute. The final structure of the cell was of the type shown in figg la and IB. The above procedure permits to fulfil the following objective: 1. To transform the starting films from a fluid emulsion, containing liquid crystal droplets, to a solid films containing a mutual dispersion of the liquid crystal and the polymer where no droplets are present, as it is illustrated into the electron microscope reported in fig 2, where the liquid crystal component as been washed out, but the polymer morphology is clearly visible. 2. To keep the liquid crystal component dispersed in the solid film in an oriented configuration where the liquid crystal molecules are oriented in the direction of the magnetic field which was applied during the polymerisation step. The electrooptical response of the cell is shown in fig 3 , where the optical transparency is reported as a function of the operational voltage. EXAMPLE 2 In this example the preparation, according to the second of the proposed processes, and operation of the film being object of the present invention are described. Starting materials for film preparation were: 1. The liquid crystal ZLI4788-000 (ZLI) from MERCK 2. The monomer (in the following indicated as monomer 2) having the following chemical formula: 3. The radical polymerisation starter IRGACURE 651 from CIBA-GEIGY. A solution of 45 wt% ZLI, 54.6 wt% monomer 2 and 0.4 wt% of Irgacure 651 was prepared and successively spread as a tin film between glass supports being coated by a suitable tick ITO layer, to ensure electric conductivity and a uniform orientation of the liquid crystal molecules perpendicularly to the supporting plane. The constancy of film thickness across the film layer was achieved by adding to the starting solution 15 micron thick spacers. The cell prepared as above described was then U.V. irradiated for one minute. The structure and morphology of the resulting solid films were found equal to that of the film obtained in example 1 (see figg. 1 ,2) Even the electrooptical response was similar to that of the films obtained in example 1. EXAMPLE 3 The only difference with respect to example 2 was that a different monomer (compound 2) has been used, that is to say the monomer (in the following indicated as monomer 3) having the chemical formula: The structure of the film and its electrooptical response were similar to those shown in the previous examples. DESCRIPTION OF THE DRAWINGS 1. Figures la-lb illustrates the morphology of the film and its operating way in absence and in the presence of an operating electric field. 2. Figure 2a is a photomicrograph, taken at the electron microscope showing the morphology of the film. 3. Figure 3 shows the electrooptical response ( transmitted light versus applied voltage) of the film. REFERENCES 1. J.L.Ferguson, U.SP. 4.435.047 (1984) 2. J.W.Doane, G.Chidichimo N.RA.Vaz, U.S.P. 4.688.900 (1987) 3. Y.D.Ma, B.G.Wu, G.Xu, SPIE, 1257, 46, (1990) 4. G.Chidichimo, G.DeFilpo, WO 9816865 (1996) 5. D.K.Yang, L.C.Chien, and J.W.Doane, Appl. Phys., Lett., 60(25), 3102 (1992) 6. N.Basturk, T.Chuard, Dechenaux, EP 0 703 287 Al ( 1996) 7. R.A.M.Hikmet, EP 0 451 905 Al (1991 ) 8. SEIKO-EPSON, EP 0 4888 1 16 A2 (1992) 9. K.Nakamura, H.Yoshida, K.FIanaoka, U.S.P. 5.189.540 (1993) lO.T.Gotoh, T.Nakata, H.Murai, E.Haregava, U.S.P. 5.674.576 (1997) 1 1. G.DeFilpo, G.Chidichimo, EP 0 799 879 A 1 (1997)

Claims: CLAIMS 1 A reverse mode electro-optical solid film consisting of a mutual dispersion of a liquid crystal and a polymer where the polymer component is contained in high concentration, from 40 to 60 wt%, where said polymers, not belonging to the liquid crystal class, is foπned by polymerising a non liquid crystal component, where the liquid crystals keeps naturally a uniform orientations even in absence of external fields Said films is transparent to light in absence of external fields and becomes gradually opaque in the presence of applied fields Said film is not only reverse mode but also haze free, due to its morphology characterised by the absence of liquid crystal droplets 2 A film of the same type claimed in 1, where the polymer component is present in high concentration, from 50 to 60 wt%, where said polymer ,even if not belonging to the liquid crystal class, is formed by polymerising a liquid crystal monomer 3 A process to obtain the film of claim 1, starting from a fluid emulsion of the liquid crystal in an organic monomer, sandwiched between glass or plastic support, according to procedure described m the example 1 In this process a magnetic field is applied, during the polymerisation of organic monomer No coatings of supports are required to ensure the orientation of the permanent orientation of the liquid crystal The polymerisation of the monomer is achieved by both thermal or U V polymerisation 4 A process to obtain the film of claim 2, starting from a homogeneous solution of two liquid crystals, sandwiched between glass or plastic support being coated by a suitable tick ITO layer, according to the procedure described in examples 2 The claimed process is particularly important for industrial production of the film since no orienting magnetic or electric field as well as other coating materials are needed during the polymerisation stage which transforms the starting fluid film into a solid type film. 5. A film of the type claimed in 1 and 2, independently of the orientation imposed to the liquid crystal with respect to the surface of the film, and independently from the specific characteristic of the liquid crystal. 6. A film of the type claimed in 1 and 2, independently from the specific property of the non liquid crystal monomer used in the preparation. 7. A film of the type claimed in 1 and 2 independently from the specific properties of the polymer contained in the system after film preparation. 8. An electrooptical cell where a film of the type above claimed is sandwiched between glassy or plastic conductive supports, independently from the specific drawing characteristic, and independently from the details of the procedure used to assemble said cell.

Inventors: CHIDICHIMO GIUSEPPE, DE FILPO GIOVANNI, CHIDICHIMO, GIUSEPPE, DE FILPO, GIOVANNI
Applicants: CHIDICHIMO GIUSEPPE, CONSORZIO PER LE TECNOLOGIE BI, FILPO GIOVANNI DE, CHIDICHIMO, GIUSEPPE, CONSORZIO PER LE TECNOLOGIE BIOMEDICHE AVANZATE TEBAID, DE FILPO, GIOVANNI
Application year: 1998
Main classification: C09K19
IPC codes: C09K19, G02F1