PROCESS OF RHEOLOGY MODIFICATION OF POLYMERS

Abstract: A process of reacting a poly(sulfonyl azide) with a polymer comprising steps (a) forming a first admixture, hereinafter referred to as a concentrate, of a first amount of a first polymer or in a liquid which does not require removal from the polymer, hereinafter diluent, and a poly(sulfonyl azide); (b) then forming a second admixture of the first admixture with a second amount of at least one second polymer, hereinafter second polymer composition; and (c) heating the second admixture to the decomposition temperature of the coupling agent for a time sufficient to result in coupling of polymer chains. The diluent is miscible. The first polymer is selected from ethylene alpha olefin copolymers; ethylene acrylic acid; ethylene vinyl acetate, ethylene/styrene interpolymers preferably steps (a) and (b) take place in the same vessel, which is preferably in the post-reactor area of a polymer processing plant.

Description: PROCESS OF RHEOLOGY MODIFICATION OF POLYMERS This invention relates to coupling of polyolefins, more specifically coupling of polyolefins using insertion into carbon hydrogen (C-H) bonds. As used herein, the term "rheology modification" means change in melt viscosity of a polymer as determined by dynamic mechanical spectroscopy . Preferably the melt strength increases while maintaining the high shear viscosity (that is viscosity measured at a shear of 100 rad/sec by DMS) so that a polymer exhibits more resistance to stretching during elongation of molten polymer at low shear conditions (that is viscosity measured at a shear of 0.1 rad/sec by DMS) and does not sacrifice the output at high shear conditions An increase in melt strength is typically observed when long chain branches or similar structures are introduced into a polymer. Polyolefins are frequently rheology modified using nonselective chemistries involving free radicals generated for instance using peroxides or high energy radiation. However, chemistries involving free radical generation at elevated temperatures also degrade the molecular weight, especially in polymers containing tertiary hydrocjen such as polystyrene, polypropylene, polyethylene copolymers etc. The reaction of polypropylene with peroxides and pentaerythritol triacrylate is reported by Wang et al , in Journal of Applied Polymer Science, Vol. 61, 1395-1404 (1996) They teach that rheology modification of isotactic polypropylene can be realized by free radical grafting of di- and tn-vinyl compounds onto polypropylene. However, this approach does not work well in actual practice as the higher rate of chain scission tends to dominate the limited amount of chain coupling that takes place. This occurs because chain scission is an mtra-molecular process following first order kinetics, while coupling is an mter-molecular process with kinetics that are minimally second order. Chain scission results in lower molecular weight and higher melt flow rate than would be observed were the branching not accompanied by scission. Because scission is not uniform, molecular weight distribution increases as lower molecular weight polymer chains referred to in the art as "tails" are formed. The teachings of US 3,058,944; 3,336,268; and 3,530,108 include the reaction of certain poly (sulfonyl azide) compounds with isotactic polypropylene or other polyolefins by nitrene insertion into C-H bonds. The product reported in US 3,058,944 is crosslinked. The product reported in US 3,530,108 is foamed and cured with cycloalkane- di (sulfonyl azide) of a given formula. In US 3,336,268 the resulting reaction products are referred to as "bridged polymers" because polymer chains are "bridged" with sulfonamide bridges. The disclosed process includes a mixing step such as milling or mixing of the sulfonylazide and polymer in solution or dispersion then a heating step where the temperature is sufficient to decompose the sulfonylazide (100°C to 225° depending on the azide decomposition temperature) . The starting polypropylene polymer for the claimed process has a molecular weight of at least 275,000. Blends taught in US 3,336,268 have up to 25 percent ethylene propylene elastomer. United States Patent 3,631,182 taught the use of azido formate for crosslinking polyolefins. United States Patent 3341418 taught the use of sulfonyl azide and azidoformate compounds to crosslink of thermoplastics material (PP (polypropylene), PS (polystyrene) , PVC (poly(vinyl chloride)) and their blends with rubbers (polyisobutene, EPM, etc.) . Similarly, the teachings of Canadian patent 797,917 (family member of NL 6,503,188) include rheology modification using from 0.001 to 0.075 weight percent polysulfonyl azide to modify homopolymer polyethylene and its blend with polyisobutylene . Teachings of incorporating poly (sulfonyl azides) into polymers in these references are typically directed to mixing poly (sulfonyl azide) as a solid or in a solvent into a polymer. Disadvantageously, mixing solids often results in localized concentrations of azide which evidence themselves as gels, discoloration, for instance black specks, or uneven amounts of coupling. Using a solvent, however, requires an extra step of removing solvent and sometimes equipment adaptations for the removal and handling volatile chemicals. It would be desirable to avoid dark specks, gels and other evidence of localized poly (sulfonyl azide) and to avoid removing or handling solvent yet to obtain polymers rheology modified rather than crosslinked (that is having less than 10 percent gel as determined by xylene extraction specifically by ASTM 2765) . Which polymers, in the case of high density polyethylene are desirably of narrow molecular weight distribution (MWD) (that is having most preferably less than 3.0 Mw/Mn, and preferably density greater than 0.945 g/ml ) advantageously made using single site, single site metallocene or single site constrained geometry catalysts (hereinafter HDPE of narrow MWD) which polymers advantageously have a combination of good processability as indicated by higher melt strength at a constant low shear viscosity for example 0.1 rad/sec measured by DMS, and higher toughness, tensile elongation than a high density polyethylene of broader molecular weight distribution treated with sulfonyl azides according to the practice of the prior art using the same equivalents (stoichiometry) of coupling reactant to polymer higher toughness than that of the same starting material coupled or rheology modified using the same equivalents of a free radical coupling agent. Desirably, the product would have better organoleptics than coupled broader MWD HDPE. Advantageously, compositions would have less undesirable odor than the same starting materials coupled or rheology modified using the same chemical equivalents of free radical generating agents. Preferably, a process of the invention would result in more consistent coupling than methods of coupling involving free radicals, that is use of the same reactants, amounts and conditions would result in consistent amounts of coupling or consistent (reproducible) property changes, especially consistent amounts of gel formation. Preferably, a process would be less subject to effects from the presence of oxygen than would a coupling or rheology modification involving agents which generate free radicals . In the case of, medium and lower density polyethylene (that is polymers having a density of from 0.94 g/cc to aboutθ.90 g/cc) , which are advantageously copolymers of ethylene in which the percent comonomer is preferably 0.5 to 5 mole percent comonomer based on total polymer as determined by ASTM 5017, the polymers would desirably show a combination of processability improved over the starting material with retention of toughness, low heat seal initiation temperature, low haze, high gloss or hot tack properties characteristic of the starting material. In the case of elastomeric polymers containing ethylene repeating units in which the preferred comonomer content is 5-25 mole percent, and preferably a density less than 0.89 g/mL, it would be desirable to have a better mechanical properties such as elongation and tensile strength than would be achieved in the starting material or by coupling using the same chemical equivalents of free radical generating agent like a peroxide. Polymers coupled by reaction with coupling agents according to the practice of the invention advantageously have at least one of these desirable properties and preferably have desirable combinations of these properties. The invention includes a process of reacting a poly (sulfonyl azide) with a polymer comprising steps (a) forming a first admixture, hereinafter referred to as a concentrate, of a first amount of a first polymer or in a liquid which does not require removal from the polymer, hereinafter diluent, and a poly (sulfonyl azide); (b) then forming a second admixture of the first admixture with a second amount of at least one second polymer, hereinafter second polymer composition; and (c) heating the second admixture at least to the decomposition temperature of the coupling agent for a time sufficient to result in coupling of polymer chains. The diluent is preferably a non-volatile, non-polar compound such as mineral oil in which the poly (sulfonyl azide) is sufficiently miscible to disperse the poly (sulfonyl azide) in the second polymer, more preferably a liquid at room temperature or low melting solid at room temperature, that is has a melting point below 50°C. When a first polymer is used, it is preferably low melting, that is has a melting point below 150°C, more preferably 110°C, or a melt index, 12, of at least 0.5 g/10 min. and most preferably is selected from ethylene alpha olefin copolymers, where the alpha olefins are of 3 to 20 carbon atoms, have a density range of at least 0.855 g/cc to 0.955 g/cc or have a melt index, 12, of at least 0.5 g/10 min; ethylene acrylic acid; ethylene vinyl acetate, et ylene/styrene interpolymers or combinations thereof. The concentrate is optionally formed on the surface of a polymer to be coupled. Step (b) preferably takes place in melt processing equipment; more preferably steps (a) and (b) take place in the same vessel, which is preferably in the post-reactor area of a polymer processing plant. The invention further includes all composi ions obtainable by processes of the invention as well as blends of those compositions with one or more polymers of compositions different from the first or second polymer or the product of a process of the invention. Additionally the invention includes articles made from compositions of the invention, and shaping those articles particularly by processes which comprise shaping the compositions in a melted state into an article, more preferably when the process comprises thermoformmg, infection molding, extrusion, casting, blow molding, foaming or blowing as well as the use of the compositions in those processes. Practice of the invention is applicable to any thermoplastic polymer which has at least one C-H bond that can react with azide lnclud±ng homopolymers and copolymers with narrow and broad (including bimodal) comonomer distribution (narrow and broad, including bimodal, molecular weight distribution) such as copolymers of ethylene with one or more alpha olefin (C3 to C20) , ethylene copolymers with unsaturation (EPDM or EODM, that is εthylene-propylene-diene or ethylene-octene -diene) , or other polymers such as linear high density polyethylene, LDPE (low density polyethylene), ethylene vinyl acetate copolymers, ethylene acrylic acid copolymers, styrεne based block copolymers (SBS, SEBS, SIS , that is styrene/butadiene/styrene , styrene/ethylene/butylene/styrene (hydrogenated SEBS) , styrene/isoprene/styrene ) , substantially random interpolymers of at least one alpha-olefin with at least one vinyl aromatic or hindered vinyl aliphatic comonomer including ethylene- styrene interpolymers, syndiotatic polystyrene, atactic polystyrene, hydrogenated polyvmyl cyclohexene, PET (poly (ethylene terephthalate) ) , PBT (polybutylene terephthalate) , PEN (polyethylene naphthalate) , polylactic acid, thermoplastic polyurethanes, polycarbonate, nylon, poly (methyl methacrylates) , ABS (acrylonitrile/ butylene/styrene) , polysulfone, polyphenylene oxide, polyphenylene sulfides, polyacetal and polyvmyl chloride . Preferred polymers for use in the practice of the invention are polymers prepared from ethylene, advantageously ethylene in combination with other monomers polymeπzable therewith. Such monomers include alpha olefins and other monomers having at least one double bond. Alpha olefins having more than 2 carbon atoms include propylene, 1-butene, 1-pentene, 1-hexene, 1-octene, 1-nonene, 1-decene, 1- umdecene, 1-dodecene as well as 4 -methyl -1-pentene, 4 -methyl- 1- hexenε, 5 -methyl -1-hexene, vmylcyclohexene, styrene . Interpolymers useful in the practice of the invention optionally and in one preferred embodiment include monomers having at least two double bonds which are preferably dienes or trienes . Suitable diene and triene comonomers include 7-methyl-l , 6-octadιene, 3 , 7-dιmethyl- 1, 6-octadιene, 5, 7-dιmethyl-l, 6-octadιene, 3,7, ll-trιmethyl-1, 6,10- octatriene, 6-methyl-l, 5-heptadιene, 1 , 3-butadιene, 1 , 6-heptadιene, 1 , 7-octadιene, 1, 8-nonadιene, 1 , 9-decadιene, 1 , 10-undecadιene, bicyclo [2.2.1] hepta-2-5-dιene (norbornadiene), tetracyclododecene, or mixtures thereof, preferably butadiene, hexadienes, and octadienes, most preferably 1 , 4-hexadιene, 4 -methyl -1 , 4-hexadιene, 5-methyl-l, 4- hexadiene, dicyclopentadiene, bicyclo [2.2. l] hepta-2-5-dιene (norbornadiene) and 5-ethylιdene-2-norbornene . Polymers useful in the practice of the invention also optionally include repeating units formed from monomers having functional groups such as carboxylic acid and esters, alcohol, or amine groups, halogen (advantageously chlorine, bromine, or fluorine, preferably chlorine or fluorine) . Such monomers include acrylic acid, methacrylic acid, vinyl chloride, vinylidene chloride, vinyl acetate, alkyl esters, particularly ethyl, methyl, or butyl acrylate or methacrylate . or carbon monoxide Polyolefins are formed by means within the skill in the art. The alpha olefin monomers and optionally other addition polymerizable monomers are polymerized under conditions within the skill in the art, Such conditions include those utilized in processes involving Ziegler- Natta catalysts such as those disclosed in U.S. Patent No. 4,076,698 (Anderson et al) ; 4,950,541 and the patents to which they refer, as well as 3,645,992 (Elston) as well as those processes utilizing metallocene and other single site catalysts such as exemplified by U.S. Patents 4,937,299 (Ewen et al . ) , 5,218,071 (Tsutsui et al . ) , 5,278,272, 5,324,800, 5,084,534, 5,405,922, 4,588,794, 5,204,419 and the processes subsequently discussed in more detail. In one embodiment, starting material polyolefins are preferably substantially linear ethylene polymers (S EPs) . The substantially linear ethylene polymers (SLEPs) are homogeneous polymers having long chain branching. They are disclosed in U.S. Patent Nos . 5,272,236 and 5,278,272. SLEPs are available as polymers made by the Insite™ Process and Catalyst Technology such as Engage™ polyolefin elastomers (POEs) commercially available from DuPont Dow Elastomers LLC and Affinity™ polyolefin plastomers (POPs) commercially available from The Dow Chemical Company. Specific examples of useful Engage™ POEs include SM 8400, EG 8100, and CL 8001 and specific examples of useful Affinity™ POPs include FM-1570, HM 1100, and SM 1300, each of which is commercially available from The Dow Chemical Company. SLEPs can be prepared via the solution, slurry, or gas phase, preferably solution phase, polymerization of ethylene and one or more optional α-olefin comonomers in the presence of a constrained geometry catalyst, such as is disclosed in European Patent Application 416,815-A, . The substantially linear ethylene/ -olefin polymers are made by a continuous process using suitable constrained geometry catalysts, preferably constrained geometry catalysts as disclosed in U.S. Application Serial Nos.: 545,403, filed July 3, 1990; 758,654, filed September 12, 1991; 758,660, filed September 12, 1991; and 720,041, filed June 24, 1991. The monocyclopentadienyl transition metal olefin polymerization catalysts taught in USP 5,026,798, are also suitable for use in preparing the polymers of the present invention, so long as the reaction conditions are as specified below. Suitable cocatalysts for use herein include but are not limited to, for example, polymeric or oligomeric aluminoxanes, especially methyl aluminoxane, as well as inert, compatible, noncoordinating, ion forming compounds. Preferred cocatalysts are inert, noncoordinating, boron compounds. The expression "continuous process" means a process in which reactants are continuously added and product is continuously withdrawn such that an approximation of a steady state (that is substantially constant concentration of reactants and product while carrying out the process) is achieved. The polymerization conditions for manufacturing the substantially linear ethylene/α-olefin polymers of the present invention are generally those useful in the solution polymerization process, although the application of the present invention is not limited thereto. Slurry and gas phase polymerization processes are also believed to be useful, provided the proper catalysts and polymerization conditions are employed. Multiple reactor polymerization processes can also be used in making the substantially linear olefin polymers and copolymers to be rheologically modified according to the present invention, such as those disclosed in USP 3,914,342, . The multiple reactors can be operated in series or in parallel, with at least one constrained geometry catalyst employed in one of the reactors . The term "substantially linear" means that, in addition to the short chain branches attributable to homogeneous comonomer incorporation, the ethylene polymer is further characterized as having long chain branches in that the polymer backbone is substituted with an average of 0.01 to 3 long chain branches/1000 carbons. Preferred substantially linear polymers for use in the invention are substituted with from 0.01 long chain branch/1000 carbons to 1 long chain branch/1000 carbons, and more preferably from 0.05 long chain branch/1000 carbons to 1 long chain branch/1000 carbons . In contrast to the term "substantially linear", the term "linear" means that the polymer lacks measurable or demonstrable long chain branches, that is, the polymer is substituted with an average of less than 0.01 long chain branch/1000 carbons. For ethylene/α-olefin interpolymers, "long chain branching" (LCB) means a chain length longer than the short chain branch that results from the incorporation of the α-olefin (s) into the polymer backbone. Each long chain branch has the same comonomer distribution as the polymer backbone and can be as long as the polymer backbone to which it is attached. The empirical effect of the presence of long chain branching in the substantial linear ethylene/α-olefin interpolymers used in the invention is manifested in its enhanced rheological properties which are quantified and expressed herein in terms of gas extrusion rheometry (GER) results melt flow, l. 0 /l ; , increases. The presence of short chain branching of up to 6 carbon atoms in length can be determined in ethylene polymers by using 1J C nuclear magnetic resonance (NMR) spectroscopy and is quantified using the method described by Randall (Rev. Macromol . Chem. Phys . , C.29, V. 2&3, p. 285-297) . As a practical matter, current ;j C nuclear magnetic resonance spectroscopy cannot distinguish the length of a long chain branch in excess of six carbon atoms. However, there are other known techniques useful for determining the presence of long chain branches in ethylene polymers, including ethylene/1 -octene interpolymers. Two such methods are gel permeation chromatography coupled with a low angle laser light scattering detector (GPC-LALLS) and gel permeation chromatography coupled with a differential viscorneter detector (GPC- DV) . The use of these techniques for long chain branch detection and the underlying theories have been well documented in the literature. See, for example, Zimm, G.H. and Stockmayer, W.H., J.Chem. Phys., 17,1301 (1949) and Rudin, A., Modern Methods of Polymer Characterization, John Wiley & Sons, New York (1991) pp. 103-112. A. Willem deGroot and P. Steve Churn, both of The Dow Chemical Company, at the October 4, 1994 conference of the Federation of Analytical Chemistry and Spectroscopy Society (FACSS) in St. Louis, Missouri, presented data demonstrating that GPC-DV is a useful technique for quantifying the presence of long chain branches in SLEPs. In particular, deGroot and Chum found that the level of long chain branches in homogeneous substantially linear homopolymer samples measured using the Zimm-Stockmayer equation correlated well with the level of long chain branches measured using 1J C NMR. Further, deGroot and Chum found that the presence of octene does not change the hydrodynamic volume of the polyethylene samples in solution and, as such, one can account for the molecular weight increase attributable to octene short chain branches by knowing the mole percent octene in the sample. By deconvoluting the contribution to molecular weight increase attributable to 1-octene short chain branches, deGroot and Chum showed that GPC-DV may be used to quantify the level of long chain branches in substantially linear ethylene/octene copolymers . deGroot and Chum also showed that a plot of Log (I 2 ) as a function of Log (M as determined by GPC illustrates that the long chain branching aspects (but not the extent of long branching) of SLEPs are comparable to that of high pressure, highly branched low density polyethylene (LDPE) and are clearly distinct from ethylene polymers produced using Ziegler-type catalysts such as titanium complexes and ordinary catalysts for making homogeneous polymers such as hafnium and vanadium complexes. SLEPs are further characterized as having: (a) a melt flow ratio, I 10 /I 2 >. 5.63, (b) a molecular weight distribution, M w /M, as determined by gel permeation chromatography and defined by the equation: (M w /M n ) < (I,„/I 2 ) - 4.63, (c) a critical shear stress at the onset of gross melt fracture, as determined by gas extrusion rheometry, of greater than 4 x 10 6 dynes/cm" or a gas extrusion rheology such that the critical shear rate at onset of surface melt fracture for the SLEP is at least 50 percent greater than the critical shear rate at the onset of surface melt fracture for a linear ethylene polymer, the linear ethylene polymer has an I_ , M w /M, and, preferably density, which are each within ten percent of the SLEP and wherein the respective critical shear rates of the SLEP and the linear ethylene polymer are measured at the same melt temperature using a gas extrusion rheometer, and, preferably, (d) a single differential scanning calorimetry, DSC, melting peak between -30 and 150°C. For the substantially linear ethylene/a-olefin polymers used in the compositions of the invention, the I10 2 ratio indicates the degree of long chain branching, that is, the higher the I10 2 ratio, the more long chain branching in the polymer. Generally, the I10 2 ratio of the substantially linear ethylene/α-olefin polymers is at least 5.63, preferably at least 7, especially at least 8 or above, and as high as 25. The melt index for the substantially linear olefin polymers useful herein is preferably at least 0.1 grams/10 minutes (g/10 min), more preferably at least 0.5 g/10 min and especially at least 1 g/10 min up to preferably 100 g/10 min, more preferably up to 50 g/10 min, and especially up to 20 g/10 min. Determination of the critical shear rate and critical shear stress in regards to melt fracture as well as other rheology properties such as rheological processing index (PI) , is performed using a gas extrusion rheometer (GER) . The gas extrusion rheometer is described by M. Shida, R.N. Shroff and L.V. Cancio in Polymer Engineering Science, Vol. 17, No. 11, p. 770 (1977), and in Rheometers for Molten Plastics by John Dealy, published by Van Nostrand Reinhold Co. (1982) on pp. 97-99. GER experiments are generally performed at a temperature of 190°C, at nitrogen pressures between 250 to 5500 psig using a 0.0754 mm diameter, 20:1 L/D die with an entrance angle of 180°. For the SLEPs described herein, the PI is the apparent viscosity (in kpoise) of a material measured by GER at an apparent shear stress of 2.15 x 10 6 dyne/cm 2 . The SLEPs for use in the invention includes ethylene interpolymers and have a PI in the range of 0.01 kpoise to 50 kpoise, preferably 15 kpoise or less. The SLEPs used herein have a PI less than or equal to 70 percent of the PI of a linear ethylene polymer (either a Ziegler polymerized polymer or a linear uniformly branched polymer as described by Elston in US Patent 3,645,992) having an I 2 , M u /M n and density, each within ten percent of the SLEPs. The rheological behavior of SLEPs can also be characterized by the Dow Rheology Index (DRI), which expresses a polymer's "normalized relaxation time as the result of long chain branching." (See, S. Lai and G.W. Knight ANTEC '93 Proceedings, INSITE™ Technology Polyolefins (SLEP) - New Rules in the Structure/Rheology Relationship of Ethylene α-Oefin Copolymers, New Orleans, La., May 1993) . DRI values range from 0 for polymers which do not have any measurable long chain branching (for example, Tafmer™ products available from Mitsui Petrochemical Industries and Exact™ products available from Exxon Chemical Company) to 15 and are independent of melt index. In general, for low to medium pressure ethylene polymers (particularly at lower densities) DRI provides improved correlations to melt elasticity and high shear flowability relative to correlations of the same attempted with melt flow ratios. For the SLEPs useful in this invention, DRI is preferably at least 0.1, and especially at least 0.5, and most especially at least 0.8. DRI can be calculated from the equation: DRI = (3652879 * τ 1 006 7 η -1)/10 where τ is the characteristic relaxation time of the material and η is the zero shear viscosity of the material. Both τ and η are the o "best fit" values to the Cross equation, that is, η /η = 1/(1 + (γ • τ )' "r ) in which n is the power law index of the material, and η and γ are the measured viscosity and shear rate, respectively. Baseline determination of viscosity and shear rate data are obtained using a Rheometric Mechanical Spectrometer (RMS-800) under dynamic sweep mode from 0.1 to 100 radians/second at 190°C and a Gas Extrusion Rheometer (GER) at extrusion pressures from 1,000 psi to 5,000 psi (6.89 to 34.5 MPa) , which corresponds to shear stress from 0.086 to 0.43 MPa, using a 0.0754 mm diameter, 20:1 L/D die at 190°C. Specific material determinations can be performed from 140 to 190°C as required to accommodate melt index variations. An apparent shear stress versus apparent shear rate plot is used to identify the melt fracture phenomena and quantify the critical shear rate and critical shear stress of ethylene polymers. According to Ramamurthy in the Journal of Rheology, 30(2), 337-357, 1986, above a certain critical flow rate, the observed extrudate irregularities may be brc dly classified into two main types: surface melt fracture and gross melt fracture. Surface melt fracture occurs under apparently steady flow conditions and ranges in detail from loss of specular film gloss to the more severe form of "sharkskin." Herein, as determined using the above-described GER, the onset of surface melt fracture (OSMF) is defined as the loss of extrudate gloss The loss of extrudate gloss is the point at which the surface roughness of the extrudate can only be detected by a 40X magnification The critical shear rate at the onset of surface melt fracture for the SLEPs is at least 50 percent greater than the critical shear rate at tne onset of surface melt fracture of a linear ethylene polymer having essentially the same 1_ and M w /M p . Gross melt fracture occurs at unsteady extrusion flow conditions and ranges in detail from regular (alternating rough and smooth, helical, etc.) to random distortions For commercial acceptability to maximize the performance properties of films, coatings and moldings, surface defects should oe minimal, if not absent. The critical shear stress at the onset of gross melt fracture for the SLEPs, especially those having a density >0.910 g/cc, used in the invention is greater than 4 x 10 dynes/cm' The critical shear rate at tne onset ot surface melt tracture (OSMF) and the onset of gross melt fracture ^OGMF) will be used herein based on the changes of surface roughness and configurations ot the extrudates extruded by a GER. The SLEPs used in the invention are also characterized by a single DSC melting peak. The single melting peak is determined using a differential scanning calorimeter standardized with indium and deionized water. The method involves 3-7 mg sample sizes, a "first heat" to 180°C which is held for 4 minutes, a cool down at 10°C/mιn. to -30°C which is held for 3 minutes, and heat up at 10°C/mιn. to 140°C for the "second heat". The single melting peak is taken from the "second heat" heat flow vs. temperature curve Total heat of fusion of the polymer is calculated from the area under the curve. For polymers having a density of 0 875 g/cc to 0.910 g/cc, the single melting peak may show, depending on equipment sensitivity, a "shoulder or a "hump" on the low melting side that constitutes less than 12 percent, typically, less than 9 percent, and more typically less than 6 percent of the total heat of fusion of the polymer. Such an artifact is observable for other homogeneously branched polymers such as Exact™ resins and is discerned on the basis of the slope of the single melting peak varying monotonica] ly through the melting region of the artifact. Such an artifact occurs within 34°C, typically within 27°C, and more typically within 20°C of the melting point of the single melting peak. The heat of fusion attributable to an artifact can be separately determined by specific integration of its associated area under the heat flow vs. temperature curve. The molecular weight distributions of ethylene α-olefin polymers are determined by gel permeation chromatography (GPC) on a Waters 150°C high temperature chromatographic unit equipped with a differential refractometer and three columns of mixed porosity. The columns are supplied by Polymer Laboratories and are commonly packed with pore sizes of 10 , 10 , 10^ and 10 A (10 ', 10 \ 10 2 and 10 "1 mm) . The solvent is 1, 2 , 4-trichlorobenzene, from which about 0.3 percent by weight solutions of the samples are prepared for injection. The flow rate is about 1.0 milliliters/minute , unit operating temperature is about 140°C and the injection size is about 100 microliters. The molecular weight determination with respect to the polymer backbone is deduced by using narrow molecular weight distribution polystyrene standards (from Polymer Laboratories) in conjunction with their elution volumes. The equivalent polyethylene molecular weights are determined by using appropriate Mark-Houwink coefficients for polyethylene and polystyrene (as described by Williams and Ward in Journal of Polymer Science, Polymer Letters, Vol. 6, p. 621, 1968) to derive the following equation: Mpolyethylene = a * ( Mp 0 ]_ vs tyrene) • In this equation, a = 0.4316 and b = 1.0. Weight average molecular weight, Mw, is calculated in the usual manner according to the following formula: Mj = (Σ w i (M 1 J )) : ; where w. is the weight fraction of the molecules with molecular weight M, eluting from the GPC column in fraction i and j = 1 when calculating M w and j = -1 when calculating M n . The density of the linear or the substantially linear ethylene polymers (as measured in accordance with ASTM D-792) for use in the present invention is generally less than 0.95 g/cm 3 . The density is preferably at least 0.85 g/cm 3 and especially at least 0.86 g/cm 3 and preferably up to 0.94 g/cm 3 , more preferably up to 0.92 g/cm 3 . When the modified resins are to be used for extrusion and injection molding, the density of the polymer is preferably at least 0.855 g/cm 3 , more preferably at least 0.865 g/cm 3 , and even more preferably at least 0.870 g/cm 3 , up to preferably 0.900 g/cm 3 , more preferably 0.885 g/crn 3 , and even more preferably up to 0.880 g/cm 3 . The most preferred density is determined primarily by the modulus of elasticity or flexibility desired in the molded article. The density remains substantially constant during rheology modification according to this invention. The ethylene polymers which may be rheology modified according to this invention may be any interpolymers of ethylene and at least one α-olefin. Suitable α-olefins are represented by the following formula : CH 2 = CHR in which R is a hydrocarbyl radical. R generally has from one to twenty carbon atoms. Suitable α-olefins for use as comonomers in a solution, gas phase or slurry polymerization process or combinations thereof include 1-propylene, 1-butene, 1-isobucylene, 1-pentene, l- hexenε, 4-methyl-l-pentεne, 1-heptene and 1-octene, as well as other monomer types such as tetrafluoroεthylene, vinyl benzocyclobutane, and cycloalkenes , for εxample cyclopentene, cyclohexene, cyclooctene, and norbornene (NB) . Preferably, the α-olefin will bε 1-butene, 1- pentenε, 4-methyl-l-pentene, 1-hexene, 1-heptene, 1-octεne, or NB, or mixtures thereof. Morε preferably, the α-olefin will be 1-hexene, 1- heptene, 1-octenε, or mixtures thereof. Most preferably, the α- olefin will be 1-octenε. The ethylene polymer rheology modified according to this invention is preferably a SLEP. These interpolymers preferably contain at least 2 weight percent, more preferably at least 5 weight percent, α-olefin. The polyolefin is a homopolymer, copolymεr, or interpolymer . Preferably the homo or copolymers contain ethylene repeating units. In polyethylene copolymers, the comonomer content is greater than 1 weight percent as determined by 13 C NMR (carbon 13 nuclear magnetic resonance) and more preferably greater than 3 weight percent of any monomer copolymerizable with ethylene, preferably an alpha olefin or cyclic olefin, more preferably such an olefin of less than 20 carbon atoms, most preferably from 2 to 18 carbon atoms. The comonomer content is at least one comonomer polymerizable with ethylene, preferably less than 4 comonomers polymerizable with ethylene, more preferably less than 2 such comonomers. Optionally, however, the practice of this invention includes other hydrocarbon polymers such as polystyrenε, poly (stryenε-co- acrylonitrilε) , polyvinylcyclohexene, polybutadiene, polyisoprene, cyclic olefin copolymers and copolymers, , and mixtures thereof . Polymers having at least 3 weight percent styrene or substituted styrene units are rεfεrred to herein as styrenic polymers. In one embodiment, preferred polymεrs for starting materials useful in the practice of this invention are slurry high density polyethylene homopolymers preferably made using single site catalysis with a narrow MWD (preferably less than 3.0 Mw/Mn, more preferably MWD less than 2.5, most preferably with a density greater than 0.945 g/ml) . Preferred melt index of the starting material depends on the desired application; however, the preferred melt index for injection molding is from 0.5 to 50 g/10 min; for film and thermoforming applications the preferred melt index is from 0.1 to 20 g/10 min; and for blow molding applications, the preferred melt index is from 0.01 to 20 g/10 min. These polymers have a good balance of mechanical properties and processability. The most preferred polymers as starting materials for this invention are ethylεnε copolymers with narrow MWD (that is a Mw/Mn of less than 3.0 most preferably less than 2.5) . These can be produced using at least one C3-C20 olefin comonomer. Most prεferred for copolymer is C3-C10. 0.5-5 mole percent comonomer as determined by ASTM 5017 is preferred in the starting material. The preferred melt indεx of the starting material depends on applications; however, the preferred melt index for injection molding is from 0.5 to 50 g/lOmin, for thermoforming applications the preferred melt index is from 0.1 to 20 g/lOmin, and for blow molding applications, the preferrεd melt index is from 0.01 to 20 g/10 mm measured. Commercially available polymers in this category are known as TAFMER polymer commercially available from Mitsui Petrochemical Industries, EXACT polymer commercially available from Exxon Chεmical Company, AFFINITY polyolefin plastomer commercially available from The Dow Chemical Company, ENGAGE polyolefin elastomer commercially available from DuPont-Dow Elastomers, . For thermoplastic applications such as film and infection molding, the most preferred comonomer content is between 3-25 weight percent. For elastomeric applications, the preferred comonomer contεnt is betweεn 20-40 weight percent The most preferred terpolymεr is an EPDM such as NORDEL εthylene/propylεne/ dienε polymer commercially available from DuPont-Dow Elastomers. The melt index is measured according to ASTM D-1238 condition 190°C/2.16 Kg (formerly known as Condition E) In one preferred embodimεnt thε polymer includes at least one ethylene/styrene interpolymer . The interpolymers employed in the present invention include, but are not limited to, substantially random interpolymers prepared by polymerizing one or more α-olefm monomers with one or more vinyl aromatic monomers one or more hindered aliphatic or cycloaliphatic vinyl monomers, and optionally with other polymerizablε εthylenically unsaturated monomer (s) Suitable α-olefin monomers include for example, α-olefin monomers containing from 2 to 20, preferably from 2 to 12, more preferably from 2 to 8 carbon atoms Preierred such monomεrs include ethylenε, propylεnε, butene-1, 4 -methyl- 1-ρεntεnε , hexene-1 and octene-1. Most prefεrrεd arε ethylene or a combination of ethylεne with C2-8 α-olefms. These α-olefms do not contain an aromatic moiεty . Suitable vinyl aromatic monomεrs which can bε employed to prepare the interpolymers employed include, for examplε, thosε represεnted by the following formula: Ar (CH 2 ) n R 1 — C = C(R 2 ) 2 whεrein Rl is selected from the group of radicals consisting of hydrogen and alkyl radicals containing from 1 to 4 carbon atoms, prefεrably hydrogεn or methyl; each R2 is independεntly sεlεcted from the group of radicals consisting of hydrogεn and alkyl radicals containing from 1 to 4 carbon atoms, prεfεrably hydrogen or methyl; Ar is a phenyl group or a phenyl group substituted with from 1 to 5 substituents selected from the group consisting of halo, Cl-4-alkyl, and Cl-4-haloalkyl; and n has a value from zero to 6, preferably from zero to 2, most preferably zero. Exemplary vinyl aromatic monomers include styrene, vinyl toluene, α-methylstyrenε, t -butyl styrεne, chlorostyrene, and all isomers of these compounds. Particularly suitable such monomers includε styrene and lower alkyl- or halogen- substituted derivatives thereof. Preferred monomers include styrene, a-methyl styrene, the lower alkyl- (Cl - C4) or phεnyl-ring substituted derivatives of styrene, such as for example, ortho- , meta- , and para-mεthylstyrεnε , the ring halogenatεd styrenes, para-vinyl toluene or mixtures thereof. A more preferred aromatic vinyl monomer is styrene. By the term "hindεrεd aliphatic or cycloaliphatic vinyl or vinylidεnε compounds", it is meant addition polymerizable vinyl or vinylidene monomers corresponding to the formula: A' I R i _ c = C(R) 2 wherein Al is a sterically bulky, aliphatic or cycloaliphatic substituent of up to 20 carbons, R 1 is selected from the group of radicals consisting of hydrogen and alkyl radicals containing from 1 to 4 carbon atoms, prεfεrably hydrogen or methyl; εach R 2 is indεpεndently selected from the group of radicals consisting of hydrogen and alkyl radicals containing from 1 to 4 carbon atoms, preferably hydrogen or mεthyl; or altεrnativεly R 1 and A 1 together form a ring system. By the term "sterically bulky" is mεant that thε monomεr bearing this substituent is normally incapable of addition polymεrization by standard Ziεgler-Natta polymerization catalysts at a rate comparable with ethylεne polymerizations. Prefεrred aliphatic or cycloaliphatic vinyl or vinylidene monomers are those in which one of the carbon atoms bearing ethylenic unsaturation is tertiary or quaternary substitutεd. Examples of such substituents include cyclic aliphatic groups such as cyclohexyl, cyclohεxεnyl, cyclooctεnyl , or ring alkyl or aryl substitutεd dεrivativεs thεreof, tert-butyl, and norbornyl . Most preferred hindered aliphatic or cycloaliphatic vinyl or vinylidenε compounds arε the various isomeric vinyl- ring substituted derivatives of cyclohexenε and substitutεd cyclohexenes , and 5-εthylidene-2-norbornene . Especially suitable are 1-, 3-, and 4- vinylcyclohexene . Other optional polymerizable ethylenically unsaturated monomer (s) include strained ring olefins such as norbornene and Cl-10 alkyl or C6-10 aryl substituted norbornenes, with an exemplary interpolymεr being ethylene/styrene/norbornene . The number averagε molecular weight (Mn) of the polymers and interpolymers is usually greater than 5,000, preferably from 20,000 to 1,000,000, more prefεrably from 50,000 to 500,000. Polymεrizations and unrεactεd monomεr removal at temperaturεs abovε thε autopolymerization tempεrature of the respective monomers may result in formation of some amounts of homopolymer polymerization products resulting from free radical polymerization. For example, while preparing the substantially random interpolymεr, an amount of atactic vinyl aromatic homopolymer may bε formεd duε to ho opolymεrization of thε vinyl aromatic monomer at elevatεd temperatures. The presεnce of vinyl aromatic homopolymεr, in gεneral, is not detrimental for the purposes of the present invention and can be tolerated. The vinyl aromatic homopolymer may be separated from the interpolymer , if desirεd, by εxtraction techniques such as selεctive precipitation from solution with a non solvεnt for εither the interpolymer or the vinyl aromatic homopolymer. For thε purpose of the present invention it is preferrεd that no more than 20 weight pεrcεnt, prεferably less than 15 weight percent based on the total weight of the interpolymers of vinyl aromatic homopolymer is present . The substantially random interpolymers are prεparεd by polymεrizing a mixture of polymerizable monomers in the presence of metallocene or constrained geometry catalysts in the prεsεnce of various cocatalysts as described in EP-A-0, 416 , 815 by James C. Stevens et al . and US Patent No. 5,703,187 by Francis J. Timmers . Preferred operating conditions for such polymerization reactions are pressures from atmospheric up to 3,000 atmospheres and temperatures from -30°C to 200°C. Examples of suitablε catalysts and mεthods for preparing the substantially random interpolymers are disclosed in U.S. Application No. 07/702,475 filed May 20, 1991 corresponding to EP-A-514 , 828 ; U.S. Application No. 07/876,268, (C-39819-A) filed May 1, 1992 corresponding to EP-A-520,732; U.S. Application No. 08/241,523, (C-41350-B) filed May 12, 1994; U.S. Application No. 60/034 , 819 (C-42890) , filed December 19, 1996; as well as U.S. Patents: 5,055,438; 5,057,475; 5,096,867; 5,064,802; 5,132,380; 5,189,192; 5,321,106; 5,347,024; 5,350,723; 5,374,696; 5,399,635; 5,403,187 5,556,928 and 5,721,185. Another, alternativε, preferred embodimεnt involvεs thε use of polyolεfin-carbon monoxide (CO) copolymers such as ethylene-carbon monoxide copolymers, propylene-carbon monoxide, and ethylεne-propylεnε- carbon monoxidε . Such polymers are commercially availablε from The Dow Chemical Company (generally CO content less than 2 weight percent) and Shell Oil Company (generally higher amounts of CO) . Alternatively, they are prepared by means within the skill in the art such as that disclosed U.S. Patents 3,835,123; 3,984,388; 4,970294; 5,554,777 and 5,565,547. For the purposes of rheology modification or coupling, the polymεr is rεactεd with a polyfunctional compound capable of insertion reactions into C-H bonds. Such polyfunctional compounds have at least two, prεfεrably 2, functional groups capable of C-H insertion reactions. Those skilled in the art are familiar with C-H insertion reactions and functional groups capable of such rεactions . For instancε, carbεnεs as generated from diazo compounds, as cited in Mathur, N.C.; Snow, M.S.; Young, K.M., and Pincock, J.A.; Tetrahedron, (1985), 41(8), pages 1509-1516, and nitrεnεs as generated from azides, as cited in Abramovitch, R.A. , ; Chellathurai, T.; Holcomb, W.D; McMastεr, I.T.; and Vanderpool , D.P.; J. Org. Chem. , (1977), 42(17), 2920-6, and Abramovitch, R.A., Knaus, G.N., J. Org. Chem.. (1975), 40(7) , 883-9. Compounds having at least two functional groups capable of C-H insertion under reaction conditions are refεrrεd to herein as coupling agents. Such coupling agents include alkyl and aryl azides (R-N 3 ) , acyl azides (R-C(0)N 3 ), azidoformatεs (R-O-C (0) -N 3 ) , phosphoryl azides ( (RO) 2 - (PO) -N 3 ) , phosphinic azides (R 2 -P(0) N and silγl azidεs (R 3 -Sι- N 3 ). Polyfunctional compounds capable of insertions into C-H bonds also include poly (sulfonyl azide) s. The poly (sulfonyl azide) is any compound having at least two sulfonyl azide groups (-SOjN reactive with the polyolεfm. Prεfεrably the poly (sulfonyl azide) s have a structurε X-R-X wherein each X is S0 2 N, and R rεprεsεnts an unsubstitutεd or inertly substituted hydrocarbyl, hydrocarbyl ether or silicon-containing group, prefεrably having sufficient carbon, oxygen or silicon, preferably carbon, atoms to separate the sulfonyl azide groups sufficiently to permit a facile reaction between the polyolefin and the sulfonyl azide, more prεfεrably at lεast 1, morε preferably at least 2, most prefεrably at least 3 carbon, oxygen or silicon, prefεrably carbon, atoms between functional groups While there is no critical limit o the length of R, εach R advantagεously has at lεast onε carbon or silicon atom bεtween X' s and preferably has less than 50, more preferably less than 30, most preterably less than 20 carbon, oxygen or silicon atoms. Wiuhm these limits, larger is better for reasons including thermal and shock stability When R is straight- chain alkyl hydrocarbon, there are preferably less than 4 carbon atoms betweεn the sulfonyl azide groups to rεduce the propensity of the nitrene to oend back and react with itseli Silicon containing groups include silanes and siloxanes, prεfεrably siloxanes The term inertly substitutεd refers to substitution with atoms or groups which do not undesirably interfere with the desired reaction (s) or desired properties of the resulting couplεd polymers Such groups include fluorine, aliphatic or aromatic ether, siloxane as well as sulfonyl azide groups when more than two polyolefin chains are to be joined Suitable structures include R as aryl, alkyl, aryl alkaryl, arylalkyl silane, siloxane or heterocyclic, groups and other groups which are inert and separate the sulfonyl azide groups as descπbεd. More prefεrably R cludεs at least one aryl group between the sulfonyl groups, most preferably at least two aryl groups (such as when R is 4,4' diphenylether or 4, 4' -biphenyl) Whεn R is one aryl group, it is preferred that the group havε morε than onε ring, as in the case of naphthylene bιs(sulfonyl azides) . Poly (sulfonyl) azides include such compounds as 1, 5-pentane bis (sulfonlazide) , 1,8-octane bιs(sulfonyl azidε) , 1,10-dεcane bis (sulfonyl azide), 1, 10-octadεcanε bis (sulfonyl azidε) , l-octyl-2 , 4 , 6-benzεne tris (sulfonyl azide), 4 , 4 ' -diphenyl ether bis(sulfonyl azide), 1, 6-bis (4 ' -sulfonazidophenyl) hexane, 2,7- naphthalene bis (sulfonyl azide), and mixed sulfonyl azides of chlorinated aliphatic hydrocarbons containing an avεragε of from 1 to 8 chlorine atoms and from 2 to 5 sulfonyl azide groups per molecule, and mixtures thereof. Preferred poly (sulfonyl azide) s include oxy- bis (4-sulfonylazidobenzene) , 2, 7-naphthalenε bis(sulfonyl azido) , , 4' -bis (sulfonyl azido) biphεnyl, 4 , 4' -diphεnyl ether bis (sulfonyl azide) and bis (4-sulfonyl azidophenyl) methane , and mixtures thereof. Sulfonyl azides are conveniently prepared by the reaction of sodium azide with the corresponding sulfonyl chloridε, although oxidation of sulfonyl hydazinεs with various reagents (nitrous acid, dinitrogen tetroxidε, nitrosonium tetrafluoroborate) has beεn used. Polyfunctional compounds capable of insertions into C-H bonds also includε carbεnε-forming compounds such as salts of alkyl and aryl hydrazones and diazo compounds, and nitrεnε- forming compounds such as alkyl and aryl azides (R-N 3 ) , acyl azides (R-C(O)N , azidoformates (R-O-C (0) -N 3 ) , sulfonyl azidεs (R-SO ? -N 3 ) , phosphoryl azidεs ((R0) 2 - (P0)-N 3 ), phosphinic azidεs (R 2 -P (0) -N and silyl azidεs (R 3 -Si-N 3 ) . Some of the coupling agents of the invεntion are preferrεd because of their propensity to form a greater abundance of carbon-hydrogen insertion products. Such compounds as the salts of hydrazones, diazo compounds, azidoformates , sulfonyl azidεs, phosphoryl azidεs, and silyl azides are prefεrrεd because they form stable singlet-state elεctron products (carbεnεs and nitrenes) which carry out efficiεnt carbon-hydrogεn insεrtion reactions, rather than substantially 1) rεarranging via such mechanisms as the Curtius-type rearrangement, as is the case with acyl azides and phosphinic azidεs, or 2) rapidly convεrting to the triplet-statε electron configuration which preferentially undergoes hydrogen atom abstraction reactions, which is thε case with alkyl and aryl azides. Also, selεction from among thε prεfεrrεd coupling agents is conveniently possible bεcausε of thε differences in the temperatures at which the differεnt classεs of coupling agεnts arε convεrted to the active carbene or nitrene products. For example, those skilled in the art will rεcognizε that carbεnεs are formed from diazo compounds efficiently at temperatures lεss than 100°C, while salts of hydrazones, azidoformates and the sulfonyl azide compounds react at a convenient rate at tempεraturεs above 100°C, up to temperatures of 200°C. (By convenient rates it is meant that the compounds react at a rate that is fast enough to make commercial processing possible, while reacting slowly enough to allow adequate mixing and compounding to result in a final product with the coupling agent adεquately dispersed and located substantially in thε desired position in the final product. Such location and dispersion may be different from product to product depending on the desired properties of the final product.) Phosphoryl azides may bε rεacted at temperatures in excess of 180°C up to 300°C, while silyl azidεs react preferentially at tempεraturεs of from 250°C to 400°C. To modify rhεology, also rεferred to herein as "to couplε," the poly (sulfonyl azide) is used in a rheology modifying amount, that is an amount effective to increase the low-shear viscosity (at 0.1 rad/sec) of the polymer preferably at least 5 percent as compared with the starting material polymer, but less than a crosslinking amount, that is an amount sufficient to result in at least 10 wεight pεrcent gel as measured by ASTM D2765-procedure A. While those skilled in the art will recognize that the amount of azidε sufficient to increasε the low shear viscosity and result in less than 10 wεight percent gel will depend on molecular weight of the azide used and polymer the amount is preferably less than 5 percent, morε prεfεrably less than 2 percent, most preferably less than 1 weight pεrcεnt poly (sulfonyl azide) based on total weight of polymεr when the poly (sulfonyl azide) has a molεcular weight of from 200 to 2000. To achieve measurable rheology modification, the amount of poly (sulfonyl azide) is preferably at least 0.01 weight percent, more preferably at least 0.05 wεight percent, most prefεrably at least 0.10 weight percent based on total polymer. For rheology modification, thε sulfonyl azidε is admixed with the polymer and heated to at least the dεcomposition temperaturε of thε sulfonyl azidε. By decomposition temperature of the azide it is meant that temperature at which the azide convεrts to thε sulfonyl nitrene, eliminating nitrogen and heat in the procεss, as detεrminεd by differential scanning calorimetry (DSC). The poly (sulfonyl azidε) begins to react at a kinetically significant rate (convenient for usε in the practicε of the invention) at tεmperatures of 130°C and is almost completely reactεd at 160°C in a DSC (scanning at 10°C/min) . ARC (scanning at 2°C/ hr) shows onsεt of decomposition is 100°C. Extent of reaction is a function of time and temperature. At the low lεvels of azide used in the practice of the invention, the optimal propertiεs are not reached until the azide is essentially fully reactεd. Temperatures for use in the practice of the invention arε also dεtεrminεd by the softening or melt tempεraturεs of thε polymεr starting materials. For thesε reasons, the tεmpεrature is advantageously greater than 90°C, preferably greater than 120°C, more preferably greater than 150°C, most preferably greater than 180°C. Preferred times at the dεsired decomposition temperatures are times that are sufficient to result in rεaction of the coupling agent with the polymer (s) without undεsirable thermal degradation of the polymer matrix. Prefεrrεd rεaction timεs in terms of the half lifε of thε coupling agent, that is the time rεquirεd for half of thε agent to bε rεactεd at a preselεcted temperature, which half life is determinable by DSC is 5 half lives of the coupling agent. In the case of a bis (sulfonyl azide), for instance, thε rεaction time is prefεrably at least 4 minutes at 200 °C. Admixing of the polymεr and coupling agent is conveniently accomplished by any means within the skill in thε art. Desirεd distribution is different in many cases, dεpεnding on what rhεological properties are to be modified. In a homopolymer it is desirable to have as homogeneous a distribution as possible, prefεrably achieving solubility of the azide in thε polymer melt. In a blend it is desirable to have low solubility in one or more of the polymer matrices such that the azide is preferentially in one or the other phase, or predominantly in the interfacial region betweεn the two phases. It has been found that the process of combining the polymer and coupling agent are important to achieving the desired result of avoiding localized gεls, dark specks or othεr indications of non- uniform distribution of coupling agent and, εspεcially, of avoiding the disadvantages of solvεnt handling and removal inherent in use of solvents for the coupling agent. After practice of the present invention there are preferably less than 10 percent, more preferably less than 5 percent, most prefεrably less than 2 weight percent gels present as determined by xylenε solubility. Prεferred processes include at least one of (a) introducing, for example by injection, a coupling agεnt in liquid form, in a slurry or othεr admixture of coupling agent in a liquid which does not require removal from the polymer, hεrεinaftεr diluent, into a device containing polymer, prefεrably softεnεd, molten or meltεd polymer, but alternatively in particulate form, more prefεrably in melt processing equipment; or (b) forming a first admixture of a first amount of a first polymεr and a coupling agεnt, advantagεously at a tεmperature less than the decomposition temperature of the coupling agent, preferably by melt blεnding, and then forming a second admixture of the first admixture with a sεcond amount of a sεcond polymεr (for εxamplε a concεntrate of a coupling agent admixed with at least onε polymer and optionally other additives, is conveniεntly admixεd into a sεcond polymεr or combination thereof optionally with other additives, to modify the second polymer (s) ) . Herεinafter, in both methods the admixture containing coupling agent (with eithεr thε diluent or the first polymer or a combination therεof) is referred to as a "concentrate." Of the two steps (b) is preferred. For example, process (b) is conveniently used to make a concεntratε with a first polymer composition having a lower melting tεmpεraturε, advantagεously at a temperaturε bεlow the decomposition temperature of the coupling agεnt, and the concentratε is mεlt blended into a second polymer composition having a higher melting temperature to complete the coupling reaction. Concentrates are espεcially prεfεrrεd whεn temperatures are sufficiently high to result in loss of coupling agent by εvaporation or dεcomposition not lεading to reaction with the polymer, or other conditions would result that effect. Alternatively, some coupling occurs during the blending of the first polymer and coupling agent, but some of the coupling agεnt rεmains unreacted until thε concentrate is blendεd into thε second polymer composition. Each polymer or polymer composition includes at least one homopolymer, copolymer, terpolymer, or intεrpolymεr and optionally includes additives within the skill in the art. In (a) , thε diluent is a compound which does not requirε removal from the resulting polymer composition, that is a compound which does not interfere undesirably with subsequent process steps appliεd to thε rεsulting polymer composition. By does not interfere undesirably, is meant that while those skilled in the art may recognize a slight effect from its presεnce, for examplε a slower subsequent step, that effect is not so disadvantageous as to dissuade one from using the diluent. To that end the diluent differs from a solvent in being nonvolatile (no more than 5 pεrcent vapor pressure) at temperatures encountεrεd in subsequent process steps, including decomposition of the coupling agent (that is up to 260°C) such that increased pressure or other mεans is not rεquired for its control in subsequεnt stεps . Thε diluεnt is preferably a liquid at room tempεrature or low melting (that is melting point below 50°C) solid at room tempεraturε. Diluεnts are preferably non-polar compounds such as mineral oils in which the coupling agent is sufficiently miscible to dispεrsε the coupling agent in a polymer. Such diluents include mineral oil; aliphatic carboxylic acid esters preferably of at least 12 carbon atoms, more preferably of less than 200 carDon atoms; parafinic, naphthεnic, or aromatic oil having a boiling point greater than 230°C, but prεfεrably liquid at 20°C, prεferably mineral oil. In (b) , the first polymer is preferably low melting, that is has a melting point below 110°C or a melt index (12) of at least 0.25 g/10 min., prεfεrably 1 g/10 min or grεater. Such polymers include, for instance, εthylene alpha olefin copolymers, espεcially whεre the alpha olεfins arε of 3 to 20 carbons, have a dεnsity rangε of at lεast 0.855 g/cc, prεfεrably up to 0.955 g/cc, more prefεrably up to 0.890 g/cc, prεferably with an melt index (12) of at least 0.5 g/10 min, more preferably at least 5, and preferably less than 2000 g/10 min, more prefεrably less than 1000 g/10 min., most prefεrably less than 100 g/10 min. Similarly, ethylene acrylic acid, ethylεnε vinyl acεtatε and εthylene/styrene interpolymers preferably with a melting temperature of less than 150°C, more preferably less than 130 °C. Thε concentrate is conveniently blendεd with polymer in any form, for instance molten, powdered, pelleted , preferably dry blended with pelleted polymer or injection of molten concentrate into molten polymer, advantageously molten polymer directly from or in a polymerization reactor. Optionally, the concentrate is formed on the surface of a polymer to be coupled according to the practice of thε invention. For instance, a diluent is coated on a polymer, conveniently a comminuted polymer, preferably pelleted or powdered, more prεfεrably pelleted, for instance by stirring or tumbling particulate polymer with a diluent, for instance, mineral oil. Then thε coupling agεnt is admixed with the diluent coated on the polymer. Thus, steps of the process of the invention suitably occur in any order that results in a sufficiently uniform admixture of concentrate and polymer (s) to substantially avoid evidεnce of localized concentrations of coupling agent . The term "melt processing" is used to mean any process in which the polymεr is softened or melted, such as extrusion, pεllεtizing, molding, thermoforming, film blowing, compounding in polymer melt form, fiber spinning, . Prefεrably, a substantially uniform admixturε of coupling agεnt and polymεr is formεd bεforε exposure to conditions in which chain coupling takes place. A substantially uniform admixture is one in which the distribution of coupling agεnt in the polymer is sufficiently homogenεous to be evidencεd by a polymer having a melt viscosity after treatment according to the practice of the invention εithεr highεr at low angular frequency (for examplε 0.1 rad/sεc) or lowεr at higher angular frequency (for εxa plε 100 rad/sec) than that of the same polymer which has not been treated with the coupling agent but has been subjected to the same shear and thermal history. Thus, prefεrably, in the practice of the invention, decomposition of the coupling agent occurs after mixing sufficient to result in a substantially uniform admixture of coupling agent and polymεr. This mixing is preferably attained with the polymer in a molten or melted state, that is above the crystalline mεlt tεmpεrature, or in a dissolved or finely dispersed condition rather than in a solid mass or particulate form. The molten or melted form is more preferred to insure homogeniety rather than localized concentrations at thε surface . Any εquipmεnt is suitably usεd, preferably equipment which provides sufficient mixing and tεmpεraturε control thε samε εquipmεnt, but advantagεously practice of the invention takes place in such devicεs as an εxtruder or a static polymer mixing device such as a Brabendεr blender. The term extruder is used for its broadest meaning to include such devices as a device which extrudes pellets or pelletizer. Conveniently, when there is a melt extrusion step betwεen production of the polymer and its usε, at lεast one step of the procεss of the invention takεs placε in thε mεlt εxtrusion step. In a preferrεd εmbodimεnt thε procεss of thε present invention takes place in a single vessεl, that is mixing of the coupling agent and polymer takεs placε in the same vessel as heating to the decomposition tεmpεraturε of thε coupling agεnt. The vessεl is preferably a twin-screw extruder, but is also advantageously a single- screw extrudεr or a batch mixεr. The reaction vessεl more preferably has at least two zonεs of different temperatures into which a reaction mixturε would pass, thε first zone advantageously being at a temperature at least the crystalline mεlt temperature or the softening tempεrature of the polymer (s and preferably lεss than the decomposition temperature of the coupling agents and the second zone being at a tempεrature sufficient for decomposition of the coupling agent. Thε first zonε is preferably at a tεmpεrature sufficiently high to soften thε polymεr and allow it to combine with the coupling agent through distributive mixing to a substantially uniform admixturε. To avoid thε εxtra stεp and rεsultant cost of rε-extrusion and to ensurε that thε coupling agent is well blendεd into the polymer, in alternative prefεrrεd embodiments it is preferred that the coupling agent be added to the post-reactor arεa of a polymεr procεssing plant. For εxample, in a slurry process of producing polyethylene, the coupling agεnt is added m either powder or liquid form to thε powdεrεd polyεthylεnε after the solvent is removed by decantation and prior to the drying and densification extrusion procεss. In an alternative embodiment, when polymers are prεparεd, in a gas phasε procεss, thε coupling agεnt is prεferably added in either powder or liquid form to the powdered polyethylenε bεforε thε dεnsification extrusion. In an alternativε embodiment when a polymer is madε in a solution procεss, the coupling agent is prεfεrably addεd to thε polymεr solution or to a dεvolatilizεd polymεr melt prior to the densification extrusion procεss. Practice of the process of the invention to rheology modify polymers yields rhεology modifiεd or chain couplεd polymεrs, that is thε polymers which have sulfonamide, amine, alkyl-substituted or aryl- substituted carboxamide, alkyl-substitutεd or aryl-substitutεd phosphoramidε, alkyl-substitutεd or aryl-substitutεd methylene coupling bεtween different polymer chains. Resulting compounds advantageously show highεr low shεar viscosity than thε original polymεr duε to coupling of long polymεr chains to polymer backbones. Broad molecular wεight distribution polymεrs (polydispersity (P.D.) of 3.5 and greater) and gel levels less than 10 pεrcεnt as determined by xylene extraction show less improvement than the dramatic effεct notεd in narrow MWD polymεr (P.D = 2 0) with gεl less than 10 percent as determined by xylenε εxtraction. Rheology modification leads to polymers which havε controllεd rnεological propεrties, specifically improved melt strength as evidencεd by increased low shear viscosity, better ability to hold oil, improved scratch and mar resistance, improved tackiness, improvεd grεεn strεngth (mεlt) , higher orientation in high shear and high extersional processεs such as injection molding, film extrusion (blown and cast) , calendaring, rotomoldmg, fibεr production, profile extrusion, foams, and wire & cablε insulation as measured by tan delta as described hereinafter elasticity by viscosity at 0 1 rad/sec and 100 rad/sec, respectivεly . It is also bεliεved that this process can be used to produce dispεrsions having improved propertiεs of higher low shear viscosity than the unmodified polymer as mεasured by DMS. Rheology modified polymers are useful as large blow molded articles due to the higher low shear viscosity than unmodifiεd polymεr and thε maintenance of the high shear viscosity for processability as indicated by high shear viscosity, foams for stablε cεll structurε as mεasured by low shear viscosity, blown film for better bubble stability as measured by low shear viscosity, fibers for bettεr sp nability as measured by high shear viscosity, cable and wire insulation for green strength to avoid sagging or deformation of the polymer on the wire as measured by low shear viscosity which are aspεcts of the invention. Polymers rheology modified according to thε practice of the invention are superior to the corresponding unmodifiεd polymεr starting matεrials for these applications due to the elevation of viscosity, of prefεrably at least 5 percent at low shear rates (0.1 rad/sec) , sufficiently high melt strengths to avoid deformation during thermal processing (for example to avoid sag during thεrmoforming) or to achiεvε bubble strength during blow molding, and sufficiently low high shear rate viscosities to facilitatε molding and extrusion. These rheological attributes enable faster filling of injection molds at high rates than thε unmodifiεd starting materials, the setup of foams (stable cell structure) as indicated by formation of lower density closed cεll foam, preferably with higher tensile strength, insulation properties, compression set or combinations thereof than attained in the use of coupling or rheology modification using coupling agents which genεratε free radicals, because of high melt viscosity . Advantageously toughness and tensilε strength of the starting material is maintained. Polymers resulting from thε practicε of the invention arε different from those resulting from practice of prior art processes as shown in CA 797,917. The polymers of the present invention show improved melt elasticity, that is higher tan delta as measured by DMS, bettεr drawability, that is higher melt strength as measured by melt tension, less swelling as measured by blow molding die swell, and less shrinkage as measured by mold shrinkagε than thε unmodified polymer and the broad MWD (greater than 3.0 Mw/Mn) . counterpart in thermoforming and large part blow molding. There are many types of molding operations which can be used to form useful fabricated articlεs or parts from the formulations disclosed herein, including various injεction molding processes (for example, that described in Modern Plastics Encvclopεdia/89 , Mid October 1988 Issue, Volume 65, Number 11, pp. 264-268, "Introduction to Injection Molding" and on pp. 270-271, "Injection Molding Thermoplastics") and blow molding processes (for examplε, that described in Modern Plastics Encvclopedia/89 , Mid October 1988 Issuε, Volume 65, Number 11, pp. 217-218, "Extrusion-Blow Molding"), profile extrusion, calendering, and pultrusion. The rheology-modifled ethylene polymers, proce'ssεs for making them, and intermediates for making them of this invention are useful in thε automotive area, industrial goods, building and construction, electrical (for example, wire and cablε coatings/insulation) and tirε products. Some of the fabricated articles include automotive hosεs, single ply roofing, and wire and cablε voltagε insulation and jackets . Film and film structures particularly benεfit from this invention and can be made using conventional hot blown film fabrication techniques or other biaxial orientation processes such as tenter frames or double bubblε procεsses Conventional hot blown film processes are described, for examplε, in Thε Encyclopεdia of Chεmical Tεchnoloqv, Kirk-Othmεr, Third Edition, John Wiley & Sons, Nεw York, 1981, vol. 16, pp. 416-417 and Vol. 18, pp 191-192 Biaxial orientation film manufacturing procεss such as describεd in a "doublε bubblε" procεss as in U.S. Patεnt 3,456,044 (Pahlkε) , and thε procεssεs dεscribed in U.S. Patent 4,352,849 (Mueller), U.S. Patent 4,597,920 (Golike) , U.S. Patεnt 4,820,557 (Warrεn) , U S Patεnt 4,837,084 (Warrεn), U.S. Patent 4,865,902 (Golike et al ), U S. Patent 4,927,708 (Herran εt al . ) , U.S Patent 4,952,451 (Mueller), U.S. Patent 4,963,419 (Lustig εt al ), and U S Patεnt 5,059,481 (Lustig εt al ) , can also bε used to make film structures from the novel compostions described herein. The film structures can also be made as describεd in a tεnter-frame technique, such as that used for oπεntεd polypropylεnε . Othεr multl- layer film manufacturing techniques for food packaging applications are describεd in Packaging Foods With Plastics, by Wilmεr A. Jenkins and James P. Harrington (1991), pp. 19-27, and in "Coεxtrusion Basics" by Thomas I. Butlεr, Film Extrusion Manual: Procεss, Matεπals, Properties pp. 31-80 (published by thε TAPPI Press (1992) ) . The films may be monolayεr or multilayεr films Thε film madε using this invention can also be coextrudεd with thε othεr layer (s) or the film can be laminated onto another layer (s) in a secondary operation, such as that described in Packaging Foods With Plastics, by Wilmer A. Jenkins and James P. Harrington (1991) or that dεscribed in "Coextrusion For Barrier Packaging" by W.J. Schrenk and C.R. Finch, Sociεtv of Plastics Engineers RETEC Proceedings, June 15-17 (1981) , pp. 211-229. If a monolayεr film is producεd via tubular film (that is, blown film tεchniques) or flat die (that is, cast film) as described by K.R. Osborn and W.A. Jenkins in "Plastic Films, Technology and Packaging Applications" (Technomic Publishing Co., Inc., 1992), then the film must go through an additional post- extrusion step of adhesivε or εxtrusion lamination to othεr packaging matεrial layers to form a multilayer structure. If the film is a coextrusion of two or more layεrs (also dεscπbεd by Osborn and Jenkins) , the film may still bε laminated to additional layers of packaging materials, depending on the other physical requirements of the final film "Laminations vs. Coextrusion" by D Dumbleton (Converting Magazine (September 1992) , also discussεs lamination versus coextrusion. Monolayer and coεxtrudεd films can also go through othεr post extrusion tεchniques, such as a biaxial orientation process Extrusion coating is yet another techniquε for producing multilayεr film structurεs using thε novel compositions described herein The novel compositions comprise at least one layer of the film structure. Similar to cast film, extrusion coating is a flat die technique. A sealant can be extrusion coatεd onto a substratε either in the form of a monolayεr or a coextruded εxtrudate Generally for a multilayer film structure, the novel compositions dεscribεd herein comprise at least onε layεr of the total multilayer film structure. Other layers of the multilayer structure include but are not limited to barrier layers, tie layers, structural layεrs or combinations thεrεof . Various materials can be used for these layers, with some of them being used as more than one layer in the same film structure. Some of thesε materials include: foil, nylon, ethylene/vinyl alcohol (EVOH) copolymers, polyvmylidenε chloridε (PVDC) , polyεthylεne terεthphalate (PET) , orientεd polypropylεne (OPP) , ethylεne/vmyl acetate (EVA) copolymers, ethylene/acrylic acid (EAA) copolymers, εthylene/methacrylic acid (EMAA) copolymers, LLDPE, HDPE, LDPE, nylon, graft adhesive polymers (for εxamplε, maleic anhydride grafted polyethylεnε) , and paper. Genεrally, thε multilayεr film structurεs comprisε from 2 to 7 layεrs. Such articles comprising the rheology-modifiεd polymεr of this invεntion may bε madε by melt processing the rheology-modified polymer according to this invεntion. That process may include processing pellets or granules of polymεr which have beεn rheology-modified according to this invention. In a preferred embodiment, the pellets or granules are substantially frεε of unrεactεd crosslinking agεnt whεn the crosslinking agent comprises a heat-activatεd crosslinking agεnt. Such articles may also be made by mεlt procεssing an intεrmεdiatε comprising a homogeneous polymer which is not substantially free of unreactεd crosslinking agεnt. Such intεrmεdiates are preferably treated with a crosslinking agεnt, but are not subjected to subsequent melt processing until the polymer is meltεd to makε the article. The crosslinking agent may be εithεr radiation or a heat-activated crosslinking agent. The rheology-modifiεd polymεrs and intεrmεdiates used to make rheology-modifiεd polymεrs may be used alone or in combination with one or more additional polymers in a polymer blend. When additional polymers arε present, they may be sεlεcted from any of the modified or unmodified homogeneous polymers describεd above for this invention any modified or unmodified hεterogeneous polymers. The hetεrogeneous polyethylenes that may be combined with the rheology-modifiεd polymεrs according to this invention fall into two broad categories, those prepared with a freε radical initiator at high tεmpεrature and high prεssurε, and thosε prepared with a coordination catalyst at high temperaturε and rεlatively low pressure. The former are generally known as low density polyethylenεs (LDPE) and arε characterized by branched chains of polymεrized monomer units pεndant from the polymer backbone. LDPE polymers genεrally have a density betweεn 0.910 and 0.935 g/cc. Ethylεnε polymεrs and copolymers prepared by the use of a coordination catalyst, such as a Ziegler or Phillips catalyst, are generally known as linεar polymεrs bεcausε of thε substantial absence of branch chains of polymεrized monomer units pendant from the backbon . High density polyethylene (HDPE), generally having a density of 0.941 to 0.965 g/cc, is typically a homopolymεr of εthylene, and it contains relatively fεw branch chains relative to the various linear copolymers of εthylεne and an α- olefin. HDPE is well known, commercially available in various gradεs, and may bε used in this invention. Linear copolymεrs of ethylene and at least one α-olefin of 3 to 12 carbon atoms, prefεrably of 4 to 8 carbon atoms, are also well known and commercially available. As is well known in the art, thε density of a linear ethylene/α-olefin copolymer is a function of both the length of the α-olefin and the amount of such monomer in the copolymεr rεlative to che amount of ethylenε, thε greater the lεngth of the α-olefin and the grεatεr thε amount of α-olεfin present, thε lower the dεnsity of thε copolymεr. Linεar low dεnsity polyεthylene (LLDPE) is typically a copolymεr of εthylεnε and an α-olεfin of 3 to 12 carbon atoms, prεfεrably 4 to 8 carbon atoms (for εxamplε, 1- butene, 1-octene, etc.), that has sufficient α-olefin content to reduce the density of the copolymer to that of LDPE. Whεn the copolymer contains evεn morε α-olefin, the density will drop below 0.91 g/cc and these copolymers arε known as ultra low dεnsity polyethylene (ULDPE) or very low density polyethylene (VLDPE) . The dεnsitiεs of thεsε linεar polymers genεrally rangε from 0.87 to 0.91 g/cc. Both the materials made by the frεε radical catalysts and by the coordination catalysts are well known in thε art, as arε thεir mεthods of prεparation. Heterogeneous linear ethylenε polymers are available from The Dow Chemical Company as Dowlex™ LLDPE and as Attane™ ULDPE resins. Heterogenεous linear ethylene polymεrs can bε prεparεd via the solution, slurry or gas phase polymerization of ethylene and one or more optional α-olefin comonomers in the presence of a Ziegler Natta catalyst, by processes such as are disclosεd in U.S. Patεnt No. 4,076,698 to Andεrson εt al . Prεfεrably, hεtεrogeneous ethylene polymεrs are typically characterizεd as having molecular weight distributions, M w /M n , in thε range of from 3.5 to 4.1. Relevant discussions of both of these classes of materials, and thεir mεthods of prεparation arε found in U.S. Patεnt No. 4,950,541 and thε patεnts to which it refers. Compositions of thε invεntion and compositions produced by practice of the invεntion arε particularly usεful bεcausε of their surprising propertiεs For instance the prefεrred mεdium dεnsity polyethylenεs and ethylenε copolymers (density 0 90 g/mL, comonomer contεnt 0.5 - 5 mole percεnt) of the invention are particularly useful as blown films such as in trash bags, grocery sacks, sealant layers, tie layers, produce bags, garment bags, shipping sacks, medical films, stretch film, shrink film, agricultural film, construction film, geomembranes, or stretch hooders, prεfεrably trash bags, agricultural film, construction film, and gεomεmbranes Similarly the medium density preterred embodiments are useful m cast films such as are useful in stretch films, diapεr backsheets, industrial wrap, producε wrap, meat wrap, consumer wrap, or shrink firm elastic film , preferably as e η astιc film Thε high density polyεthylεne (dεnsity grεatεr than 0 945 g/mL and preferably MWD less than 3) prεfεrrεd embodiments are particularly useful for thermoforming, preferably for usε in rεfπgεrator liners, thin walled containers, medical blister packs, modified atmospherε packaging, and in blow molding to form such articlεs as oil bottles, pipe, fuel tanks milk jugs, and trigger bottles The low density ethylenε copolymεr prεfεrred embodiments (density less than 0 89 g/mL and comonomer content preferably 5 -25 molε pεrcεnt) are particularly useful in extrusion such as to form wire and cablε coatings, tubing, profiles such as gaskεts and sεals, sheeting, extrusion coatings such as carpet backing, multilayer packaging, toughenεrs, and impact modifiεrs for blεnds of polymεrs, preferably for wire and cable coating, tougheners and impact modifiers Thε low density prefεrred embodiments are also particularly useful for calendaring to form such matεπals as sheeting, packaging films, and non-packaging films, for foams particularly cushion packaging, toys, building and construction uses, automotive uses, body boards, airline seats, floral and craft uses, preferably cushion packaging, building and construction, automotive usεs, and body boards; and for adhεsivεs and sealants, particularly hot melt adhesivεs, prεssurε sensitive adhesivεs (whεthεr appliεd in solvεnts or by hot melt), caulks, and as tackifiers in othεr compositions . Practice of the present invention increases the utility of ethylεnε polymεrs, particularly high dεnsity polyethylene, and propylenε polymers m the automotive field With increased melt strength it becomεs possible to produce such automotive articles as fascia, bumpεr energy absorbers, bumper beams, door trim panels, door hardwarε cartridgεs, seat backs, seat pans, head rest cores, header trim, hεadεr energy absorbing (EA) inserts, pillars, instrument panels, instrument panel trim, bolstεrs, glovε boxes, doors, consoles, ducts, parcel shelves, hat shelves, load floors, rocker panels, fεnders and combinations thereof using such means as blow molding, injection molding, thermoforming, and gas assistεd injection molding Furthermore, such automotive articles as cross car supports, door outer panels, seat trim, and combinations therεof can bε producεd using such means as blow molding, injection molding, and thermoforming Such articles as roof liners, underbody closeouts (underbody shields), pick-up bed liners, and wheεl liners can be convεniεntly producεd by thermoforming, while such articles as fuel filler necks and fuel tanks can be produced using blow molding, roto- old g or injection molding Injection molding, thermoforming and gas assisted injection molding are useful for producing door impact beams Such articles as bumpεr beams, door impact beams, hεater trim, roof liners, ducts, pick-up bεd liners, fuel filler necks, fuel transport lines and conductive fuel systems are conveniεntly produced by extrusion or coextrusion as well Coextrusion is additionally useful for rocker panels and fendεrs Conductivε fuεl systems are also optionally roto-molded or blow molded Roto-molding is also useful for door EA inserts, seat backs, head rest cores, headεr EA, instrument panel trim, bolstεrs, and ducts; while blow molding is additionally useful for door EA inserts Furthermorε, foaming is usεful for bumper energy absorbers, bumpεr beams, door trim panels, door EA inserts, seat trim, hεad rεst corεs, hεader trim, roof liners, header EA, pillars, instrument panel trim, bolsters, and pick-up bed liners Compression thermoforming, that is thermoforming at a pressurε greater than 240 kPa, is usεful to produce such articles as bumper beams, cross car supports, door impact bεams , door outεr panεls, door hardware cartridges, seat backs, seat pans, headεr trim, roof liners, instrument panel trim, bolsters, ducts, parcεl shεlvεs, hat shelvεs, load floors, rockεr panεls, fεnders, underbody closeouts, pick-up bεd linεrs, wheel liners and combinations thereof. Practice of thε invention advantageously facilitates blow molding, thermoforming and foaming ethylene polymers and propylene polymers that without reaction with poly (sulfonyl azide) would not be convεniεntly shaped using those mεthods and which have a fractional melt (as measured by the procedurε of ASTM-D1238 using 5 kg weight and 109°C) at least onε order of magnitude lower than starting material before coupling. The following examples are to illustrate this invention and do not limit it. Ratios, parts, and percεntages are by weight unless otherwisε statεd. Examplεs (Ex) of thε invention are designated numerically while comparative samples (C.S.) are designated alphabetically and are not examples of the invention. Test Methods: A Rheometrics, Inc. RMS-800 dynamic mechanical spectrometεr with 25mm diamεtεr parallel plates was used to determine the dynamic rheological data. A frequency sweεp with fivε logarithmically spacεd points pεr decade was run from 0.1 to 100 rad/s at 190 °C. The strain was determinεd to be within the linear viscoelastic regimε by pεrforming a strain swεep at 0.1 rad/s and 190 °C, by strain sweεp from 2 to 30 percent strain in 2 percent steps to detεrmine the minimum required strain to produce torques within thε spεcification of thε transducer; another strain swεep at 100 rad/s and 190 °C was used to determine the maximum strain before nonlinearity occurred according to the procedure disclosed by J. M. Dealy and K. F. Wissbrun, "Melt Rheology and Its Role in Plastics Processing", Van Nostrand, New York (1990) . All testing was performed in a nitrogen purge to minimize oxidativε degradation. A Perkin Elmer model TMA 7 thermomechanical analyzεr was usεd to measure the uppεr sεrvice tempεraturε. Probe force of 102g and heating rate of 5°C/min werε used. Each test specimεn was a disk with thicknεss of 2mm and diamεtεr, prεpared by comprεssion molding at 205°C and air-cooling to room tεmperaturε. Xylεnε Extraction to dεtεrminε gεl content was performed by weighing out 1 gram samples of polymer. The samples arε transferred to a mesh baskεt which is thεn placed in boiling xylene for 12 hours. After 12 hours, the sample baskets are removed and placed in a vacuum oven at 150°C and 28 in. of Hg vacuum for 12 hours. After 12 hours, the samples are removed, allowed to cool to room temperature over a 1 hour period, and then weighed. Thε results are reported as percεnt polymεr extracted. Percent extractεd = (initial wεight-final wεight) /initial weight according to ASTM D-2765 Procedurε "A" Samplεs wεrε prεparεd using εithεr a HaakεBuchlεr Rhεomix 600 mixer with roller style bladεs, attached to a HaakeBuchlεr Rheocord 9000 Torque rhεomεter, or using a Brabender mixer (Typε R.E.E. No. A- 19/S.B) with a 50 g mixing bowl All instrumεnts were usεd according to manufacturer's directions. Examples 1 and 2 and Comparative Sample A: films The rεsin usεd in Examplεs 1 and 2 was an εthylene-octene copolymer with Mw/Mn =3.26, Mw=71100, having a melt index of 6 (g/10 min.), and a density of 0.919 g/cc commercially available from The Dow Chemical Company under the trade designation DOWLEX 2035 polyethylεnε referrεd to hεrεinaftεr by thε tradε dεsignation. Rεsin Prεparation for Examplεs 1 and 2: Onε hundrεd pounds (45.4 kg) of thε DOWLEX™ 2035 polyεthylene rεsin pellets (containing 200 ppm hinderεd polyphenolic stabilizer commercially available from Ciba Geigy Corporation under thε tradε dεsignation Irganox 1010 stabilizεr and 750 ppm synthεtic dihydrotalcite commercially available from Kyowa under the trade dεsignation DHT 4A stabilizεr) were tumble blended with 200 ml of mineral oil for 30 minutes in a 55 gallon (207.91itεr) fiber drum (with liner) at 6 rotations per minutε. A total of 54.4 g (corresponding to 1200 ppm) of 4 , 4' -oxybis (benzenesulfonyl azide) (hεreinafter BSA) was added to the abovε mixturε and tumble blεndεd for 2 hours to ensure adequate coating of thε pellets The above procedure was repεatεd three times such that 300 pounds (136 2 kg) of coated resin were produced. After the dry blending, this admixture of coupling agent and resin was fed into a twin screw extrudεr having a scrεw diamεter of 30 cm commercially available from Werner Pfleideier Corporation under the trade designation ZSK-30 twin screw extruder. The εxtruder measured tempεrature was 130°C, 175°C, 215°C, 221°C, and 221°C for zones 1, 2, 3, 4, and 5, respectivεly Thε tεmpεraturε was mεasured using thermocouples that contact the metal Thε distances of the thermocouples from the center of the feed zone werε 8.8, 38 8, 56.2, 66 3, 78.8, and 88 8 cm from the feed to the discharge (die) of the extruder for Zones 1, 2, 3, 4, and 5, respεctivεiy Thε mεlt temperature and die temperatures were 230°C and 220° C, respεctivεiy. Thε mεlt-εxtruded resin ran through a watεr cooling bath (at 19° C) bεforε it was pelletizεd The output rate for this process was 30 pounds/hr (13 6 kg/hr) A total of 300 pounds (136.2 kg) of the couplεd rεsin was collected for furthεr study Thε final rεsin (after treatment) had a measured 1 0 g/10 mm melt index and 0.919 g/cc density. Film Fabrication- Films wεre fabricated in a blown film extruder having a 2 5 inch (6 25 cm) single screw commercially available from Battenfeld Glouscester Engineering Inc under the trade designation Model 22-01 using the detailed fabrication parameters as follows Die type: Sano Die diametεr- 6 inches (15 2 cm) Screw type: Barr ET Output rate: 188 lb/h (85.1 kg/hr Melt Temp: -400° F (204°C) Tempεrature profile: 350°F, 425°F, 290°F, 290°F (177°C, 218°C, 143°C , 143°C ) Cooling Air: yes Blow up ratio: 2.0 & 2.9 Film gauge: 6 .0 mil (0.15 mm) Shear at the die: -106 /s (metric unit 3000 ppm of Sι0 2 was added as an antiblock to all of the resins, and 1000 ppm of polymer processing aid commεrcially availablε from 3M Co. undεr thε trade designation Dynamar-5920 was addεd to all thε resins. The Sι0 2 and Dynamar-5920 processing aid were dry-blendεd with thε pellets; the additive blendεd pellets were then fed to the extruder to preparε thε film. Puncturε at room tεmpεrature was measured using an instrument for thε purposed commercially available from Instron Inc. under the trade designation Instron Model 4201 with a hardware upgrade commercially available from Smtech Inc. and a testing frame commercially available from Smtech Inc. under thε tradε dεsignation MTS Smtech ReNεw tεsting framε along with software commercially available from Smtech Inc. under the trade designation Smtech (Version 3 08) Testing Software. Four samples of each film with dimensions of 6"x 6" (15x15 cm) werε measurεd using a round spεcimen holder 12.56" (31.9 cm) square. A puncturε probe is a 1/2" (1 27 cm) polished stainless steel ba l with 7.5" (18.75 cm) maximum travel and travel speεd of 10 inches/mm (25.4 cm/mm) . Thε energy required to break the film was measured. Elmendorf Tεar Strεngth was measured at 23 °C according to the procedures of ASTM D1922. MD (Machine Direction) Ult (ultimate) Tensile Strength and CD (Cross Direction) Ult Tensilε Strεngth werε mεasured according to the procedures of ASTM D638. Results of these measurεmεnts wεre shown in Table 1 : Table 1. Mechanical Properties of Film DOWLEX is a trademark of The Dow Chemical Company. * Blow up Ratio in parenthesis CD and MD are Cross Dirεction and Machine Direction orientation of thε film. Table 2 : Metric conversions of measurements I -£» IV) I DOWLEX is a trademark of The Dow Chemical Company. * Blow up Ratio Comparative Samples A and B: Samplεs of 2.0 kg each of an ethylene-octenε copolymεr with Mw/Mn =3.26, Mw=71,100, having a mεlt index of 6 0 g/10 mm., and a density of 0.919 g/cc commercially available from The Dow Chemical Company under the trade designation DOWLEX™ 2035 polyethylenε rεsin (containing the same additives as in Example 1) for Comparativε Samplε A; and a linεar low dεnsity εthylεnε/octεne copolymεr with Mw/Mn = 3.96, Mw = 114,800 melt index = 1.0 g/10 minutes and density of 0.92 g/cm 3 commercially available from The Dow Chεmical Company undεr thε tradε dεsignation DOWLEX™ 2045A polyethylεnε rεsin having an additivε packagε consisting of 1250 ppm of Calcium Stεarate, 200 ppm of antioxidant commεrcially availablε from Ciba Gεigy Corp undεr thε tradε dεsignation Irganox 1010, and 1600 ppm of phosphitε antioxidant commercially available from Ciba Gεigy Corp undεr thε tradε dεsignation Irgaphos 168, for Comparativε Samplε B wεrε prεparεd according to thε following procedure Each resin was imbibed with BSA of the concentration designatεd in Tablε 3 by thε procedure : 1) The designated amount of the resin was weighed into a high density polyεthylεne bag. 2) An amount of a 5 weight percent solution of BSA m tetrahydrofuran (THF) corresponding to thε dεsignatεd amount of the azide was preparεd 3) Thε solution of BSA was dispensed over the resin in multiple portions from a syringe having an industrial blunt -tippεd nεεdle . 4) The bag was closed and thε resin was vigorously mixed following the addition to εnsurε homogeneity. 5) The bag was openεd in a fumε hood and thε THF was allowed to evaporate for a minimum of 2 hours to preparε dry pellets. 6) The coated dry pellets wεrε mixεd onε final time and then put in the hopper of a fεεder for metering to an extrudεr. A total of 10.0 g of thε BSA was deposited on each 2.0 kg sample, providing a 500 ppm (weight/weight) lεvεl of thε BSA on each sample. After Step 6 of the procedure, the coated pellets were fed into a twin scrεw extrudεr having a scrεw diamεtεr of 18 mm commercially availablε from Haakε, Inc. under the trade designation Haake Polylab Micro 18 twin screw extrudεr. Thε εxtruder had Zones 1-5 from thε feed zone to the discharge die of the εxtruder; thesε zones were 3.5 inch long heatεd blocks, centered 4 inches, 7.5 inches, 11 inches, 14.5 inches, and 18 inches from the cεnter of the feεd throat for the extrudεr for Zonεs 1, 2, 3, 4, and 5 respectively . Tempεraturεs sεt for εach zonε wεrε 50°C, 75°C, 85°C, 90°C, and 93 °C, rεspectivεly with mεasurεd tεmpεratures of 53.8°C, 75°C, 84.9°C, 90°C, and 93.1 °C measured for Zones 1, 2, 3, 4 , and 5, rεspεctivεly . Thε temperaturε was mεasurεd using thεrmocouples that contact in the body of the extruder barrel. The diε temperature was set to and measurεd at 93°C, with a melt temperaturε of 100°C. Diε prεssurε was 1700 psi (11,721 kPa) ; feed rate was 1.0 lb/hr (0.45 kg/h) ; extruder screw speεd was 50 rpm (revolutions per minute) with an extrudεr torques of 5700 meter grams. The extrudεd polymεr was drawn through a watεr bath for cooling and thε resulting polymer strands were cut into pellets. The resulting polymers had significant black specks as noted by visual inspection of the pellets. The specks werε actually incorporated into the each of the pellets. No film could be produced due to thε amount of black spεcks . Examplε 3 : Examplε 3 was prepared as though for a concentrate, or mastεr batch. A 0.038 lb (0.017 kg) samplε of BSA, 0.100 lb (0.045 kg) of mineral oil (commercially available from Witco Corp. under the trade designation Kaydol) , and 24.863 lb (11.28 kg) of an ethylεne-octene copolymer with Mw/Mn =3.39, Mw=94,300, having a melt index of 2.3 g/10 mm., and a dεnsity of 0.917 g/cc commεrcially availablε from Thε Dow Chemical Company under the tradε designation Dowlεx™ 2047 polyethylene resin (containing 500 ppm polyphenolic antioxidant commercially available from Ciba Geigy Corporation under thε tradε dεsignation Irganox 1076 and 1600 ppm phosphitε stabilizεr commercially available from Ciba Geigy Corporation under the trade designation Irgaphos 168) was tumble blendεd for 60 minutes in a poly bag lined fiber drum. A concentrate was formed in the mineral oil. The concentrate coated pellets were thεn extruded under thε conditions described in Comparative Sample A, to provide an εthylene-octene copolymεr with modifiεd rheological properties . Examplεs 4 and 5: Prεparation of Concentrate 1: A 10 weight percent concentration of BSA in an ethylenε-octεne copolymer with Mw/Mn =2.03, Mw=110,800, having a melt index of 5.00g/10 min., and a density of 0.870 g/cc commercially available from Thε Dow Chemical Company under the trade dεsignation AFFINITY™ EG8200 polyolefin plastomer (referred to hereinafter by the trade designation) for a master batch (Concentratε 1) was formεd by mixing a samplε of 27.2 g of BSA with 243 g of the AFFINITY™ EG 8200 polyolefin plastomer (containing 500 ppm of hindered phenolic stabilizer commercially available from Ciba Geigy Corporation under the trade designation Irganox 1076 and 800 ppm stabilizer believed to be tetrakis- (2 , 4 -ditertiarybutyl -phenyl) -4,4' -biphenyl phosphonitε commercially available from Sandoz Chemical Company under the tradε dεsignation P-EPQ stabilizεr) and 2 g of mineral oil (commercially available from Pεnreco Corp. under the trade designation Drakeol 35) . Pellets were put into a five gallon polyεthylene bag, the BSA powder was added in thε center, then thε oil squirtεd from a syringε in a circlε around the powder pile. The bag was then closed at the top, leaving an air space above the mixture and shaken until it appeared to be complεtely mixed, that is, no loose powder was visible in the bag, for approximately two minutes. The resulting mixture was extrudεd on a twin scrεw extruder having a screw diameter of 18 mm commercially availablε from Haake, Inc. under the trade designation Haakε Polylab Micro-18 twin scrεw co-rotating εxtruder at 50 rpm with thε following temperature profile for εach zone: Zone 1, 2, 3, 4, and 5 set at 70, 80, 90, 90, 90 °C, respectively. The strand from the extrudεr was passed through a chilled water bath then chopped by a strand cutter commercially available from Berlyn under the tradε dεsignation Pεll-2 strand cutter. The extruder screw was comprisεd of 9 εlemεnts with thε following configuration (rεfεrring to the length of the screw stack εlement in mm, and the angle of pitch of the screw on the mixing εlement in degreεs) : 90mm & 40°, 90mm & 40°, 90mm & 40°, 60mm & 40°, 60mm & 40°, 30mm & 40°, 30mm & 40°, 90mm & 30°, scrεw tip. Prεparation of Concεntrate 2: The procedure for preparation of Concentrate 1 was repεatεd to form Concεntratε 2 except that 13.6 g of BSA wεrε used to form a 5 weight percεnt concεntration of BSA in thε εthylεnε- octεnε copolymεr commεrcially availablε from The Dow Chemical Company under the trade designation AFFINITY™ EG 8200 polyolefin plastomer referred to hereinafter by the trade dεsignation and containing 500 ppm Irganox 1076 stabilizer and 800 ppm P-EPQ stabilizer for a master batch (designated Concentrate 2) . Example 4 : A 19.693 lb (8.93 kg) sample of an ethylεne-octene copolymer with Mw/Mn =3.39, Mw=94,300, having a mεlt indεx of 2.3 g/10 min., and a dεnsity of 0.917 g/cc commεrcially availablε from Thε Dow Chemical Company under the trade designation DOWLEX™ 2047 polyεthylene resin mixed with 0.307 lbs (0.139 kg) of Concentrate 1 was placed in a fiber drum which had an HDPE (high density polyethylene) bag liner and tumble blended for approximately 60 minutes (rotation 10 RPM) . The rεsulting mixturε was fεd into thε twin scrεw extrudεr used in Example 1. The extrudεr actual tεmperatures werε 130, 175, 215, 221, and 221°C for Zonεs 1-5, rεspεctively, from the feed to the discharge (die) of the extrudεr. Thε melt tempεraturε and diε tεmperatures were 230 and 220°C, respectively. The resulting mεlt-extruded resin ran through a water cooling bath (at 19°C) before it was pellεtized. The output rate for this process was 30 pounds/hr (13.6 kg/h), and 300 pounds (136.2 kg) of the coupled resin was collectεd for furthεr study. The final resin (after treatment) had a mεasurεd l.Og/lOmin melt index and 0.919 g/cc density. Example 5 For Example 5, thε procedure of Example 4 was repεated excεpt that Concentrate 2 was used in an amount of 0.65 lb (0.29 kg) with 24.35 lb (11.04 kg) of the resin. Film Extrusion Films werε fabricatεd in a blown film εxtrudεr having a 1.25 inch (3.175 cm) singlε scrεw commercially available from Killion Extruders, Inc. under the tradε dεsignation Killion model KL125 using thε dεtailed fabrication parameters as follows: Die gap: 60 mil (1.52 mm) Die type: Sano Die diameter: 3 inches (0.076 m) Scrεw typε : singlε Output ratε: ~ 10 lb/h (4.5 kg/h) Melt Temp: -450° F Temperature profile: 350, 400, 450, 450°F (177, 204, 232, 232°C) rεspεctively) Cooling Air: no Blow up ratio: 1.8 Film gauge: 3.0 mil (0.076 mm) Shear at the die: 18 1/sec Viscosities were detεrmined as described previously, 110 and 12 werε determined by the procedure of ASTM D 1238 and the results of these analyses werε rεcordεd in Tablε 3. Table 3 . Rheology of Coupled LLDPE ( linear low density polyethylene ) Using Concentrates of BSA Back press means back pressure and was the pressure of the polymer melt insidε the extrusion head measured by a pressu re transducer on the extrusion εquipment in units of kPa The results in Table 6 indicate that thε BSA is vεry εffεctivε when added using a concentratε (Ex 3, 4 and 5) . Thε improvεmεnt in rhεology was measured by the incrεase in 110/12 or 0.1/100 viscosity. Examples 6 and 7 and Comparative Samplε C: The resin used for Examples 6 and 7, and Comparative Sample C was an ethylenε-propylene-ethylidenε norbornεne terpolymεr with Mw/Mn =3.73, Mw=136,200, having a mεlt index (12) of 1.0 g/10 min., and a density of 0.88 g/cc commercially available from DuPont Dow Elastomers under the trade designation Nordel IP NDR 3720P hydrocarbon rubber (containing 1000 ppm Irganox 1076 stabilizεr) . For Examplε 6, a concεntratε was made on a twin scrεw extruder with am 18 mm barrel, commercially available from Haakε, Inc. undεr the trade designation Haake Polylab Micro 18 by dry blending 34.05 g of the BSA and 5.0 lb (2.27 kg) of an εthylεne-octene copolymer with Mw/Mn = 1.90, Mw=19,000, having a melt index of 1000 g/10 min., and a density of 0.87 g/cc commercially available from The Dow Chεmical Company undεr thε trade designation XUS-59800.02 polyolεfin εlastomer. This dry blend was extruded at a low tempεraturε of 110°C to avoid reacting the carrier wax with the BSA. The resulting melt blended concentrate was water quenchεd by drawing through a water bath at 18°C and chopped into pellets. A total of 10 kg of an ethylene- propylene-εthylidene norbornenε terpolymer with Mw/Mn =3.73, Mw=136,200, having a mεlt indεx of l.Og/10 min., and a dεnsity of 0.88 g/cc commεrcially available from DuPont Dow Elastomers under the trade dεsignation Nordεl IP NDR 3720P hydrocarbon rubbεr, pεllets and 240 g of the concεntratε wεrε dry blεnded and then extruded as described below. For Example 7, an oil coated blend was made by adding 25 g of a mineral oil commercially available from Witco Corp. under the trade designation Kaydol to 10 kg of pellεts of Nordεl IP NDR 3720P hydrocarbon rubbεr and then tumble blended for a period of 1 hour at ambient tempεraturε to coat thε pεllets with the oil. Then 12.5 g of BSA was addεd to the oil coated pellεts and again tumbled blendεd by hand for a period of 5 minutes at a tεmpεraturε of 25°C to mix thε BSA into thε coating of oil to form a concεntratε of BSA in thε oil. The resulting blend was also extruded as describεd bεlow. For Comparativε Sample C, an untreated sample of 5 lb. (2.27 kg) of the Nordεl IP NDR 3720P hydrocarbon rubbεr was εxtrudεd without BSA to εxpose it to the same conditions as Example 2 and was referrεd to herein as Comparative Sample C. The Examples 6 and 7 and Comparative Sample C werε melt blended at the conditions below on the twin screw extruder used in Example 1. The following extrusion conditions werε usεd: Zonε 1 Temp Set 80 C C Zone 2 Temp Set 130°C Zone 3 Temp set 190°C Zone 4 Temp set 190°C Zone 5 Tεmp sεt 190°C Diε Tεmp sεt 190°C Extruder RPM's set to 250 Water Bath 57° F (13.9°C) Output Rate 17 - 23 Ib/hr (7.7 10.4kg/h) Propεrties of the resulting polymers werε measured as describεd for Examplε 1.: Moonεy viscosity was detεrminεd according to the procedure of ASTM 1646-92 (at 25°C, 9 minutes run timε, using a 38.1 mm diameter rotor at a rotor speεd of 0.02 rad/sεc) . Table 4. Properties of Rheology Modified EPDM (ethylene Table 5. Rheology of EPDM (ethylene propylene diene monomer rubber) Modified with BSA vis. is viscosity Preparation of rhεology modifiεd HDPE in a twin scrεw εxtruder: As Examplε 8, a samplε of an εthylεnε-butene copolymer with a melt index (15) of 0.43 g/10 mm., an I 21.6/15 of 24.2g/10 mm., an 110/12 of 19.2 (as measured on an instrument commercially available from Custom Scientific Instruments, Inc. under thε trade designation MicroMelt Indexer Model #CS127, run at 190°C with 2.16 Kg weight for 12 according to ASTM 1238 but with 1/6 samplε sizε) , and a density of 0.955 g/cc commercially available from The Dow Chemical Company under the trade dεsignation HDPE 40055E polyεthylene (hereinafter the HDPE) having propertiεs of mεlt strεngth and melt index listed hereinafter; and as Example 9 a sample of an ethylene-butene copolymer with a melt index (15) of 0.23 g/10 mm., an 110/12 of 22.4 according to the test method used for Example 8, and a density of 0.935 g/cc commercially available from BASF Corp. under the trade designation Lupolen 4261A (properties of melt strength and melt index listed hereinafter) , were rheology modified with BSA at lεvels of 400 ppm and 200 ppm BSA respectively. The BSA was added to the HDPE as a concentratε of 1 weight percεnt BSA in poly (εthylene-co-acrylic acid) commercially available from The Dow Chemical Company under the trade dεsignation PRIMACOR 3150 adhesive copolymεr, (hereinafter EAA) having 3 percεnt acrylic acid. Thε 1 percent concentrate was prεparεd from a "superconcentrate" of 10 weight percent BSA in the same EAA. The superconcentratε was prεpared by adding 20 g BSA to 180 g EAA and mixing in a mixer commercially available from Haake, Inc. undεr thε tradε dεsignation Rheocorder at 120 °C at 20 - 40 RPM for 10 minutes. A 1 weight percent BSA concentrate was then prepared by mixing the superconcεntrate with additional EAA on an extrudεr commercially available from Haake, Inc. under the trade designation Haake Polylab Micro- 18 18 mm Leistritz twin scrεw extruder. The extrudεr scrεws wεrε comprisεd of 7 elemεnts with the following configuration (refεrring to the length of the screw stack elεmεnt in mm, and thε anglε of pitch of thε screw on the mixing elεmεnt in degreεs) : 90mm 40°, 90mm 40°, 90mm 40°, 60mm 40°, 60mm 40°, 90mm 30°, 60mm 30°. Thε tips wεrε all forwarding elements. Extrusion profile for concentrate preparation: Zone 1 75 ° C Zone 2 100 ° C Zone 3 115 ° C Zone 4 120 ° C Zone 5 120 ° C Die 120 ° C Mεlt 127 ° C Torquε 2500 mg (meter-grams) RPM 80 Prεss -1000 PSI (6895 kPa) Ratε 34 - 36 g/min Example 8, using a high density polyethylene: For Example 8 the HDPE described previously was prepared by tumble blending 73 lb (33 kg) of 2.74 lb (1.24 kg) of 1 weight percent BSA concεntrate with 70.26 lb (31.9 kg) of the HDPE. The tumble blended material was fed to the twin screw extruder describεd in Example 1 under thε conditions outlinεd in Example 9, extrudεd, coolεd in a watεr bath and strand chopped into pellεts. Examplε 9 using an ethylene-butene copolymer: Example 9 was prεparεd by tumblε blending 75 lb (34 kg) of 1.5 lb ( 0.7 kg) of 1 weight percent BSA concentratε with 73.5 lb (33.3 kg) of Lupolen 4261A polymer. The tumble blendεd matεrial was fed to the twin scrεw extruder used in Example 8 under the conditions outlined below, extruded, cooled in a water bath and strand choppεd into pellets . Extruder conditions for Examples 8 and 9: Zone 1 75 ° C Zone 2 134 ° C Zone 3 191 ° C Zone 4 226 ° C Zonε 5 225 ° C Diε 230 ° C Mεlt 241 0 c Torque 76 pεrcεnt RPM 200 Press 925 PSI (6377 kPa) (Example 9) 750 - 7 76600 PSI (5171 5240 kPa) (Examplε 8) Ratε 31 - 32 lb/hr (14-14.5 kg/hr) (Example 9) 33.7 36.3 lb/hr (15.3 - 16 .5 kg/hr) (Example 8) Melt Strength of Modified Materials: The data obtained by analysis of the products of Examples 8 and 9 shows an increase in melt strength after low levεls of trεatmεnt with coupling agent.

Claims: WHAT IS CLAIMED IS: 1. A procεss of rεacting a poly (sulfonyl azidε) with a polymer characterized in the combination of steps (a) forming a first admixturε, hεrεinaftεr referred to as a concentratε, of a first amount of a first polymer or in a liquid which does not require removal from the polymer, herεinafter diluent, and a poly (sulfonyl azide); (b) then forming a second admixture of the first admixture with a sεcond amount of at lεast onε sεcond polymεr, hereinaftεr sεcond polymεr composition; and (c) hεating thε sεcond admixture at least to the decomposition temperature of the coupling agent for a time sufficiεnt to rεsult in coupling of polymεr chains. 2. The process of Claim 1 wherεin the diluent is a non-volatilε, non-polar compound which is a liquid at room temperature or low mεlting solid at room temperaturε, that is has a melting point below 50°C, in which the poly (sulfonyl azide) is sufficiεntly misciblε to disperse the poly (sulfonyl azide) in the second polymer or wherεin thε first polymεr is low mεlting, that is has a mεlting point below 150°C or a melt index, 12, of at least 0.5 g/10 min. 3. The process of Claim 1 or 2 wherεin the first polymer is selectεd from εthylεnε alpha olεfin copolymεrs, whεre the alpha olefins are of 3 to 20 carbon atoms, havε a dεnsity rangε of at least 0.855 g/cc to 0.955 g/cc or have a melt index, 12, of at least 0.5 g/10 min,- ethylene acrylic acid copolymers, ethylene vinyl acetate copolymers, ethylene/styrenε intεrpolymεrs or a combination thεrεof or thε diluεnt is sεlεctεd from a minεral oil. 4. Thε process of Claim 1, 2 or 3 wherεin thε concεntrate is formed on thε surfacε of a polymer to be coupled. 5. The process of any of Claims 1-4 wherein steps (a) and (b) take place in the same vessel. 6. A composition which obtainable as the product of any of the processes of any of Claims 1-5. 7. A composition which is a blend of any composition of Claim 6 with at lεast one polymer of a composition different from that of the first or second polymer. 8. A procεss of prεparing shapεd polymer articles by forming a composition of Claim 6 or 7 in a melted state into an article. 9. A use of any composition of any of Claims 6 or 7 in any process of thermoforming, injection molding, extrusion, casting, blow molding, foaming or blowing. 10. An article comprising a composition of Claim 6 or 7.

Inventors: BABB DAVID A, CUMMINS CLARK H, HO THOI H, HOENIG WENDY D, KAO CHE-I, MULLINS MICHAEL J, ROWLAND MICHAEL E, SILVIS H CRAIG, BABB, DAVID, A., CUMMINS, CLARK, H., HO, THOI, H., HOENIG, WENDY, D., KAO, CHE-I, MULLINS, MICHAEL, J., ROWLAND, MICHAEL, E., SILVIS, H., CRAIG
Applicants: BABB DAVID A, CUMMINS CLARK H, DOW CHEMICAL CO, HO THOI H, HOENIG WENDY D, KAO CHE I, MULLINS MICHAEL J, ROWLAND MICHAEL E, SILVIS H CRAIG, BABB, DAVID, A., CUMMINS, CLARK, H., HO, THOI, H., HOENIG, WENDY, D., KAO, CHE-I, MULLINS, MICHAEL, J., ROWLAND, MICHAEL, E., SILVIS, H., CRAIG, THE DOW CHEMICAL COMPANY
Application year: 1998
Main classification: C08J3
IPC codes: B29C55, B29K23, B29L7, C08F8, C08G81, C08G85, C08J3, C08J5, C08J9, C08K5, C08L23, C08L25