LAMINATE FOR PRINTED CIRCUIT BOARDS

Abstract: The present invention relates to printed circuit board laminates which are characterized by improved thermal stability. The improved properties are attributed to the use of a novel aluminium hydroxyde which is described by the molecular representation: Al2O3.nH2O where n > 2.6 and < 2.9.

Description: Laminate for printed circuit boards The present invention relates to a thermally stable fire retardant laminate for printed circuit boards using a thermally stable aluminium hydroxide without the need for other fire retardant agents. Printed circuit board laminate types are defined by the American NEMA (National Electrical Manufacturers Association) standard, the terminology is accepted world-wide. Generally, laminates are categorized according to the type of reinforcement used, i. e., cellulose paper or glass. Typically, the type FR-2 uses paper only, CEM-1 uses paper and woven glass, while type CEM-3 contains both woven and non-woven glass. The type FR-4 contains woven glass only. To achieve the required V0 level of fire retardancy according to American Underwriters Laboratories' standard UL-94, it is necessary to add either fire retardant chemicals to the polymer system or build halogens or phosphorous into the backbone of the polymer itself. On combustion, these additives help to extinguish the fire. However, in the process of doing so they produce toxic and corrosive gases. In the case of combustion of FR-2 laminates, which contain phosphorous compounds, phosphoric acid is formed. CEM-1, CEM-3 and FR-4 laminates which contain brominated epoxy resin, produce corrosive and toxic hydrogen bromide on combustion. It is well known in the art that aluminium hydroxide may be used to improve the fire retardancy of synthetic polymer systems based on for example epoxy, polyester, and vinyl ester because the polymers decompose in the same temperature range as the aluminium hydroxide. However, the thermal stability of the gibbsite form of aluminium hydroxide (Al(OH) 3 or sometimes represented as Al O 3 .3H 2 O) is insufficient at the temperatures used to solder components to a printed circuit board laminate. This can result in blistering of the laminate thereby rendering it unusable. It is known that when gibbsite type aluminium hydroxide is heat treated in air it is partially converted to the mono hydrate form, boehmite (AlOOH or Al 2 O 3 .H 2 O) which improves thermal stability but to the detriment of fire retardancy. Japanese patent disclosure JP-A 60/203 438 describes a CEM-3 laminate containing heat treated gibbsite type aluminium hydroxide which has improved thermal stability over standard aluminium trihydroxide but which does not give the required level of fire retardancy so that brominated epoxy resin has to be used to achieve the UL 94 V0 rating. In such circumstances, and in the absence of superior fire properties, other inorganic materials such as talc or clay could also be used. The object of the present invention is to produce a CEM-3 laminate which has good thermal stability, is halogen/phosphorous free and meets the UL 94 V0 requirement. A further object of the invention is to develop a thermally stable aluminium hydroxide which impart the required characteristics to the laminate. It was possible to achieve the object of the invention by means of a laminate for printed circuit boards according to claim 1, by a method for the preparation of the laminate according to claim 7, by a printed circuit board made of the laminate according to claim 13 by a thermally stable aluminium hydroxide according to claim 16. The CEM-3 type laminates are as a rule constructed from two layers of woven fibreglass on the outsides and three layers of non- woven glass tissue in the core. According to claim 1 of the invention, the laminate for printed circuit boards has surface layers comprising curable resin-impregnated woven glass fabric and intermediate layers comprising curable resin- impregnated non-woven glass, and is characterized in that the intermediate layers contain 200 % by weight to 275 % by weight (based on the resin) of a thermally stable aluminium hydroxide of the molecular formula Al O 3 .nH 2 O wherein n has a value >2.6 to <2.9. The curable resin may be an unsaturated polyester resin, an epoxy, a vinyl ester or any suitable thermosetting compound which on combustion decomposes in the same temperature range as the thermally stable aluminium hydroxide. The laminates may be based on epoxy resin which allows a batch process to be used. The laminates may also be produced by continuous process using unsaturated polyester or vinyl ester, i. e , resins which polymerize via a free radical mechanism. The nature of the invention however does not limit the manufacturing technique for the laminate. When the production of the laminate is based on epoxy resin, as a rule two layers of woven glass preimpregnated with the epoxy resin are combined with three layers of non- woven glass preimpregnated with epoxy resin containing thermally stable aluminium hydroxide These five layers are usually then combined with one or two layers of copper foil on the outside and the assembly subjected to heat and pressure to polymerize the resin and consolidate the laminate. Most epoxy resins used for electrical and electronic applications are derived from bisphenol A or cycloaliphatic species. The most common curing agent is dicyandiamide. According to the method of the present invention, the intermediate layer comprising curable resin impregnated non-woven glass contain 200 % by weight to 275 % by weight, preferably 225 % by weight to 250 % by weight, of the thermally stable aluminium hydroxide relative to the weight of the curable resin. In the molecular formula, Al 2 O 3 .nH 2 O, n preferably has a value of 2.7 to 2.8. A feature of the halogen and phosphorous free epoxy laminate of the present invention is the use of thermally stable aluminium hydroxide as the sole fire retardant. The prior art describes the removal of a part of the water content of aluminium hydroxide as a means of improving it's thermal stability. If insufficient water is removed, the laminate containing the aluminium hydroxide does not survive the soldering operation. However, a limitation of the prior art is that if too much water is removed the resulting aluminium hydroxide may contain too little water of constitution to act effectively as a fire retardant A further complication is the formation of the more thermally stable phase aluminium hydroxide (boehmite), which not only contains one third of the amount of water as the original aluminium trihydroxide (gibbsite) it also holds it back to 520 °C before releasing it. This detracts further from fire retardant effectiveness. It is well known in the art that the finer is the aluminium hydroxide starting material, the less is the tendency to form the undesirable boehmite phase on heating. However, at the particle sizes necessary to avoid boehmite formation (<1 μm), it becomes virtually impossible to process the material in synthetic resin. On the other hand, thermally stable aluminium hydroxide which is processable will contain too much boehmite thus preventing the production of a halogen-free epoxy laminate which passes UL 94 V0. Essentially, the novel feature of the thermally stable aluminium hydroxide of the present invention is the surprisingly low boehmite content relative to the average particle size This allows lower values of n to be obtained thereby improving water stability without compromising on fire properties' effectiveness. Thus, for n <2.6, there is insufficient water (and too much boehmite) to achieve the required fire properties whereas for n >2.9, there is too much water still present to achieve the required thermal resistance to soldering. The decoupling of the relationship between boehmite formation and particle size is achieved by suitable mechanical treatment of relatively coarse particles (average size ca. 60 μm) of aluminium hydroxide prior to the thermal pretreatment step. A suitable mechanical treatment would be provided for example by the application of compressive forces to aluminium hydroxide to increase polycrystallinity. Without being bound to any particular theory, it appears that structural degradation by such means creates the conditions for a more easy diffusion of water to the exterior of the crystals thereby minimizing the tendency to build-up of hydrothermal pressure within the crystals and hence the reduced tendency to boehmite formation. In practical terms, the product of the invention can be created by a size reduction of an aluminium hydroxide agglomerate with an average particle size D50% of 40 to 80 μm, preferably of 50 to 70 μm, crystallized out from a typical Bayer process - sodium aluminate solution. Any size reduction technique, e g. ball milling, which separates the crystals present within coarser agglomerates with little or no gross fracture of the single crystals can be applied. A simultaneous broadening of the particle size distribution due to attrition and the absence of crystal breakage by gross fracture improves the processability of the thermally stable aluminium hydroxide in the respective resin system. The subsequent thermal stabilization can be achieved by simply heating the material recovered from the size reduction treatment at a temperature and during a time sufficient to reduce the water loss on ignition from 34.5 wt.% (n = 3) to a level corresponding to the n value according to the invention. The thermally stable aluminium hydroxide according to the present invention expediently has a specific surface area measured according to the BET method of from 2 to 10 m 2 /g A very essential point is the particle size distribution which combines a relatively fine average size with a breadth of particle sizes, this improves the dispersion of the thermally stable aluminium hydroxide in the resin while at the same time minimizing the tendency of the coarser particles to sediment out during processing and avoiding any filtering effects by the non-woven glass an optimum particle size distribution allow minimum viscosity of the resin/filler mix at a filling level sufficiently high to achieve the desired flame retardant properties of the laminate without the need to add any other flame retardants. The average particle size of the thermally stable aluminium hydroxide of the present invention D50% is in the range 5 to 10 μm. The breadth of the particle size distribution is indicated by the D10% range, i. e., 10 % by weight of the particles are smaller than 0.5 to 1.5 μm and the D90% range, i. e., 90 % by weight of the particles are less than 20 to 35 μm in size The oil absorption measured according to standard method DIN 53199 is within the range 25 to 35 ml/100 g The incorporation of the thermally stable aluminium hydroxide into the curable resin can be accomplished by methods known to those skilled in the art, i. e., usually by introducing the filler into the predissolved mixture of resin and curing agent using suitable equipment such as shearing head mixer. If needed, other inorganic thermally stable fillers may be added to the formulation such as fine silica, clay or talc, although none of these would significantly enhance fire properties. Further processing of the resin / filler mix to the "prepreg" stage and then to the cured laminate is common state of the art and described in the literature, an example of which is "Handbook of Epoxide Resins", published by the McGraw-Hill Book Company. The cured laminate according to the present invention shows excellent thermal stability; when immersed in molten solder at 260 °C, it shows no signs of blistering or bubbling for a period of over 90 seconds. The laminate also has excellent fire retardancy characteristics and meets the requirements of UL 94 V-0 Figures: Figure 1 shows the effect of heating aluminium hydroxides of different particle sizes (based on the measurement of the "loss on ignition, LOI") on the percent of boehmite (AlOOH) formed by X-ray diffraction. Curves 1 to 3 designate standard aluminium hydroxides (Martinal® ON-types of Martinswerk GmbH, Bergheim, Germany) with the particle sizes 60 μm (ON, curve 1 ), 10 μm (ON-3 10, curve 2) and 1.5 μm (OL-104, curve 3) in comparison with the thermally stable aluminium hydroxide of the invention (curve 4). Figure 2 shows differential scanning calorimetry of the thermally stable aluminium hydroxide of the invention (curve 1) in comparison with a standard aluminium hydroxide (Martinal® ON-310 of Martinswerk GmbH, Bergheim, Germany). Examples: Fine crystals of aluminium hydroxide (average size 1 - 2 μm) are agglomerated to ca. 60 μm average size by using a seed charge of 50 kg/dm 3 sodium aluminate solution of following concentration: Na2θ - 140 kg/dm 3 , AI2O3 - 150 kg/dm 3 , total Na2θ - 150 kg/dm 3 . The working capacity of the crystallizer was 1 m 3 . Crystallization temperature was 75°C with a retention time of 24 h. Alumina liquor productivity was ca. 40 kg/dm 3 . The product of crystallization was washed with deionized water and dried at 105°C for 4 h. Size reduction of the aluminium hydroxide particles was effected by means of a vibration mill (type Palla 200 of the KHD company). The milling conditions were as follows: motor - 1000 rpm; loading of cylpebs - ca. 65 % by volume; cylpebs dimensions - 12 mm x 12 mm aluminium oxide, mill throughput ca. 50 kg/h. Under these conditions, the feed aluminium hydroxide was reduced in size to the dimensions given in Table 1. The final step of thermal stabilization was achieved by lowering the water loss on ignition from the 34.5 wt.% of the size reduced material to ca. 31 wt.% by heating in an electric oven operating at a temperature of 220°C for a time of ca. 2h. The properties of the thermally stable material are also given in Table 1. The physical properties of the aluminium hydroxide according to the present invention are shown in comparison to a standard aluminium hydroxide of Martinswerk GmbH, Bergheim, Germany and heat treated aluminium hydroxide of the prior art as described in JP-A 60 / 203 438. Table 1 Characteristics of the thermally stable aluminium hydroxide in comparison with standard aluminium hydroxide (Martinal® ON-310, Martinswerk GmbH, Bergheim, Germany) and thermally stable aluminium hydroxide of the prior art (JP-A 60 / 203 438) Differential scanning calorimetry shows the virtual absence of any endotherm due to boehmite compared to the standard aluminium hydroxide as represented by Martinal® ON- 310 (see Figure 2). Batch Process 100 parts of an epoxy resin with epoxy equivalent of 400 - 500 (DOW DER 652) dissolved in 30 parts of acetone is mixed with 4 parts of dicyandiamide predissolved in 36 parts of 2- methoxy ethanol. To this mix is added 0.1 parts of 2-methyl imidazole to accelerate the resin cure (Mix A). Woven glass fabric (style 7628 manufactured by Interglass) is impregnated with the Mix A to a resin content of 42 %, and the resin B-staged for 2 min. at 160 °C to produce a dry prepreg. Separately, to Mix A is added 250 phr (i. e., parts per hundred resin) of the different types of aluminium hydroxide shown in Table 2. Each of these mixes are impregnated into non- woven glass (type E 105 manufactured by Owens Corning) to give weight corresponding to 90 % of the total The aluminium hydroxides are predispersed in an amount of acetone commensurate with achieving the final mix viscosity. The resin system is then B-staged for 3 in. at 160 °C to produce a dry, handlable prepreg. Three of the non-woven glass prepreg layers are sandwiched between two woven glass prepreg layers This assembly has copper foil placed on both sides and the pack laminated at 180 °C at a pressure of 50 bar for 90 min. to produce a copper clad laminate 1 6 mm thick Continuous Process In the above example, the epoxy resin may be replaced by resin systems which cure by a free radical polymerization reaction thereby leading to a negligible level of volatile emissions Examples of these are unsaturated polyester, epoxy acrylate or vinyl ester resins In the continuous process, the woven glass cloth (style 7628, Interglass) is impregnated continuously through, e g., a liquid vinyl ester resin (DOW Derakane) containing 100 parts by weight of resin and 1.5 parts of benzoyl peroxide. Separately, the non-woven glass is impregnated continuously through vinyl ester / benzoyl peroxide mix containing 250 phr of the aluminium hydroxide of the present invention. After initial curing in a tunnel oven for 10 min. at 120 °C, the layers are combined with two layers of copper foil on the outside and the seven layers consolidated under heat and pressure in a conveyorised moving platform for 15 min. at 150 °C. The continuous laminate so produced has a thickness of 1.6 mm. Test Results The thermal stability and fire retardant properties of the laminates produced by these techniques are dependent on the properties and level of the aluminium hydroxide, not on the polymer nor laminate manufacturing technique. In Table 2 are given the results obtained when using non-halogenated epoxy resin. These should be taken as typical and representative of all of the polymer types described. Comparison is made between the thermally stable aluminium hydroxide of the invention and the standard aluminium hydroxide (Martinal® ON-3 10 of Martinswerk GmbH, Bergheim, Germany) and thermally stable aluminium hydroxide of the state of the art (JP-A 60/203 438). Solder resistance is measured by fully immersing the laminate in molten solder at 260 °C When the aluminium hydroxide starts to decompose it is possible to hear the laminate blistering and the escaping water causes "waves" at the solder surface. The time is measured until the blistering / waves are detected. The flammability is defined by the American Underwriters Laboratory UL 94 standard which categorizes performance on combustion as V-0 (the best), V-l and HB (the worst) For pcb applications laminates have to meet the V-0 category. Table 2 Solder Resistance and Flammability Test Results

Claims: Claims: 1. Laminate for printed circuit boards having surface layers comprising resin impregnated woven glass fabric and intermediate layers comprising curable resin impregnated non- woven glass, characterized in that the intermediate layer contains 200 % by weight to 275 % by weight based on the resin in the intermediate layer of aluminium hydroxide of the molecular formula Al 2 O 3 .nH 2 O wherein n has a value of >2.6 to <2.9. 2 Laminate according to claim 1 , wherein the thermally stable aluminium hydroxide has a specific surface area measured by the BET method of 2 to 10 m /g. 3. Laminate according to claim 1 or 2, wherein the thermally stable aluminium hydroxide has a particle size in the D50% range of 5 to 10 μm. 4. Laminate according to one of the claims 1 to 3, wherein the thermally stable aluminium hydroxide has a particle size in the D10% range of 0.5 to 1.5 μm and in the D90% range of 20 to 35 μm. 5. Laminate according to one of the claims 1 to 4, wherein the thermally stable aluminium hydroxide has an oil absorption of 25 to 35 ml/100 g. 6. Laminate according to one of the claims 1 to 5, wherein as a curable resin an unsaturated polyester resin, an epoxy or a vinyl ester is applied 7. Method for the preparation of a laminate for printed circuit boards by composing together surface layers comprising curable resin impregnated woven glass fabric and intermediate layers comprising curable resin-impregnated non-woven glass, characterized in that the curable resin-impregnated non-woven glass contains 200 % by weight to 275 % by weight based on the resin in the intermediate layers of a thermally stable aluminium hydroxide of the molecular formula Al 2 O 3 .nH 2 O, wherein n has a value of>2.6 to <2.9. 8. Method according to claim 7, wherein the thermally stable aluminium hydroxide has a specific surface area measured by the BET method of 2 to 10 m 2 /g. 9. Method according to claim 7 or 8, wherein the thermally stable aluminium hydroxide has a particle size in the D50% range of 5 to 10 μm. 10. Method according to one of the claims 7 to 9, wherein the thermally stable aluminium hydroxide has a particle size in the D10% range of 0.5 to 1.5 μm and in the D90% range of 20 to 35 μm. 1 1. Method according to one of the claims 7 to 10, wherein the thermally stable aluminium hydroxide has an oil absorption of 25 to 35 ml / 100 g. 12. Method according to one of the claims 7 to 11, wherein as a curable resin an unsaturated polyester resin, an epoxy or a vinyl ester is applied. 13. Printed circuit board made of a laminate according to claims 1 to 6, or prepared following a method according to claims 7 to 12. 14 Thermally stable aluminium hydroxide of the molecular formula Al 2 O 3 .nH 2 O, wherein n has a value of >2 6 to <2.9. 15. Thermally stable aluminium hydroxide according to claim 14 having specific surface area measured by the BET method of 2 to 10 m /g. 16. Thermally stable aluminium hydroxide according to claim 14 or 15 having a particle size in the D50% range of 5 to 10 μm. 17. Thermally stable aluminium hydroxide according to one of the claims 14 to 16 having a particle size in the D10% range of 0.5 to 1.5 μm and in the D90% range of 20 to 35 μm. Thermally stable aluminium hydroxide according to one of the claims 14 to 17 having an oil absorption of 25 to 35 ml/ 100 g

Inventors: AGGLETON MICHAEL, BROWN NEIL, AGGLETON, MICHAEL, BROWN, NEIL
Applicants: AGGLETON MICHAEL, BROWN NEIL, MARTINSWERK GMBH, AGGLETON, MICHAEL, BROWN, NEIL, MARTINSWERK GMBH FUER CHEMISCHE UND METALLURGISCHE PRODUKTION
Application year: 1998
Main classification: B32B5
IPC codes: B32B5, B32B27, C01F7, C09K21, H05K1