Packing method and package for dry image-forming material

Abstract: A packing method and package for a full color dry image-forming material which does not cause muddy color even after storage over a long period of time is provided by: 1) A packing method and package for a dry image-forming material comprising a support and a layer, provided thereon, containing microcapsules containing at least a photocurable compound, a photo initiator and a color precursor in the internal phase, containing a color-developer in the layer containing the microcapsule or a layer adjacent thereto, wherein the dry image-forming material is packed together with a humidity-controlling material; or, 2. The packing method or package as above, wherein the dry image-forming material and a humidity-controlling material are packed with a low moisture-permeable film.

Description: Background of the Invention Field of the Invention The present invention relates to a packing method and package for a dry image-forming material using light-sensitive microcapsules. Description of Prior Art Imaging processes based on photosensitive microencapsulated materials are well known. The Meed Corporation discloses a method for forming an image through exposure-controlled release of an image-forming agent from a microcapsule containing a photohardenable composition in US-A-4,399,209, 4,440,846 and 4,772,541. In the method, a colorless image-forming agent, called leuco dye, which is released under exposure-control from a microcapsule, is reacted with a color-developer being present outside the microcapsule to form a color image. US-A-4,399,209 describes a transfer imaging system. That is, an image-forming agent is image-wise transferable to a developer sheet containing a chromogenic material and reacted with a developer to form an image. US-A-4,440,846 discloses a 'self-contained' system wherein an imaging system and a developer are present on the same support. That is, an image-forming agent is encapsulated in pressure-rupturable capsules, and upon exposure and capsule rupture the image-forming agent contacts and reacts with the developer to form an image on the support. These methods have excellent characteristics as a dry color imaging method. The above imaging material cures the internal phase of a microcapsule or increases the viscosity thereof to control a release of a color precursor in pressure-rupturing to form a positive-positive image pattern upon exposure to light. However, it has the defect that the degree of hardening of the internal phase of a microcapsule or of increasing the viscosity thereof is varied by a change in environment, particularly a variation in humidity, and as a result thereof, the photographic characteristics such as light-sensitivity, maximum density and fogging density are changed. This defect poses a serious problem in full color imaging. That is, in forming a full color image, color precursors each developing yellow, magenta and cyan colors and photo-initiators each corresponding to blue, green and red lights are encapusulated in an internal phase of microcapsules, and the three sets of the microcapsules are mixed to prepare a full color imaging material containing a developer. However, the photographic characteristics of the respective microcapsules are varied by a change in humidity to different degrees, which results in causing a problem of producing muddy color. For example, when a yellow color is developed, cyan and magenta capsules are cured by red and green lights, and only a yellow color former reacts with a color-developer to form an image. However, the cyan or magenta capsule is insufficiently cured due to a change in humidity in a certain case, and as a result thereof, muddy color in which cyan or magenta is blended with yellow is produced in some cases. This muddy color phenomenon due to a change in humidity has been a large problem in designing a processor for forming an image when an imaging material is used as a system material to integrate with hardware, particularly as is the case when an imaging material is used as an output material for an image on a personal computer. US-A-4,965,165 describes a method for storing photosensitive donor media comprising the steps of: placing the donor media in an air and humidity occlusive vessel; establishing an internal atmosphere in the vessel, the internal atmosphere containing about 1 to 5% oxygen and about 40 to 60% humidity; and sealing the donor media in the vessel. Disclosure of the Invention Summary of the Invention The present invention provides a packing method for a dry image-forming material comprising a support and a layer, provided thereon, containing microcapsules containing at least a photohardenable or photocurable compound, a photoinitiator and a color precursor in the internal phase, further containing outside the microcapsules a color-developer in either a layer containing the microcapsules or a layer adjacent thereto, which comprises packing the dry image-forming material together with humidity-controlling material containing a water-absorbing substance having an absorbed salt solution or absorbed water. The color-developer may be present outside the microcapsules. Preferred yet optional features of the method are as set out in claims 2 to 13. The present invention also provides a package comprising a dry image-forming material comprising a support and a layer, provided thereon, containing microcapsules containing at least a photocurable or photohardenable compound, a photoinitiator and a color precursor in the internal phase, further containing a color-developer in either the layer containing the microcapsules or a layer adjacent thereto, together with a humidity-controlling material containing a water-absorbing substance having an absorbed salt solution or absorbed water. Preferred yet optional features of the package are as set out in claims 15 to 26. The present invention is able to provide a packing method for a dry image-forming material which avoids or reduces muddy color production even after storage over a long period of time. The invention is also able to provide a packing method for a dry imaging material which causes less change in the photographic characteristics of the material even after storage over an extended period of time. Detailed Explanation of the Invention The present invention will be described in detail. The humidity-controlling material in the present invention includes salt-solutions, for example, aqueous solutions described in Kagaku Binran, Kisohen II (Chemical Handbook, Basic Course II) edited by Nippon Kagakukai, published by Maruzen, pp. 731 to 748 (1975), particularly, solutions giving a fixed humidity shown in Table 7·64 at p. 748. To be specific, the following salt solutions are included; BaCl 2 ·2H 2 O, CH 3 COOK, CH 3 COONa·3H 2 O, CaCl 2 ·6H 2 O, Ca(NO 3 ) 2 ·4H 2 O, CaSO 4 ·2H 2 O, CrO 3 , H 2 C 2 O 4 ·2H 2 O, H 3 PO 4 ·1/2H 2 O, KBr, KF, KHSO 4 , KI, KNO 3 , K 2 CO 3 ·2H 2 O, K 2 CrO 4 , K 2 HPO 4 , KNCS, LiCl·H 2 O, Mg(CH 3 COO) 2 ·4H 2 O, Mg(NO 3 ) 2 ·6H 2 O, NH 4 Cl, NH 4 Cl + KNO 3 , NH 4 H 2 PO 4 , (NH 4 ) 2 SO 4 , NaBr, NaBr·2H 2 O, NaBrO 3 , NaCl + KNO 3 + NaNO 3 , NaClO 3 , NaF, NaHSO 4 ·H 2 O, NaI, NaNO 2 , Na 2 CO 3 ·10H 2 O, Na 2 Cr 2 O 7 ·2H 2 O, NaHPO 4 ·12H 2 O, Na 2 SO 3 ·7H 2 O, Na 2 SO 4 ·10H 2 O, Na 2 S 2 O 3 ·5H 2 O, Pb(NO 3 ) 2 , TlCl, TlNO 3 , Tl 2 SO 4 , ZnCl 2 ·3/2H 2 O, Zn(NO 3 ) 2 ·6H 2 O and ZnSO 4 ·7H 2 O Other salts can be used as long as they are sufficiently water-soluble; the salts are not restricted to those specifically mentioned. These salt solutions, having been controlled to saturated or optional concentrations, are preferably used. Further, these salt solutions can be controlled to optional humidities by suitably selecting the kind and concentration of the salts. When it is desired to adjust to a relative humidity to 100 %, it can be achieved by adding water. A fungicide and a preservative may be used together in addition to the salt solution or water. The humidity-controlling material used in the present invention can be used repeatedly until the water content is used up, and can be prepared for further use by leaving standing under a suitable humid atmosphere even after the water content is used up. The water-absorbing substances used in the present invention are preferably used by impregnating a high water-absorbing resin, for example as usually used for a paper diaper, with salt solutions and water. Resin grains having a water absorbing ability up to 50 to 1000 times the own weight can suitably be used as well for such high waterabsorbing resin. To be specific, as described in JP-A-57-173194 and JP-A-58-24492, there can be mentioned metal salts of polyacrylic acid such as poly(sodium acrylate), poly(lithium acrylate) and poly(potassium acrylate), vinyl alcohol-acrylamide copolymers, sodium acrylate-acrylamide copolymers, cellulose-based polymers such as carboxymethyl compounds and graft polymers, starch-based polymers such as hydrolyzed products of acrylonitrile-grafted compound and acrylic acid-grafted products, isobutylene-maleic anhydride copolymer, a modified polyethylene oxide, polydiacryldimethylammonium salts, and polyacrylic acid quaternary ammonium salts. At least one kind thereof can be used. The particularly preferred high water-absorbing resins are vinyl alcohol-acrylamide copolymers and polyethylene oxide-modified products. Cotton, pulp, sponge, cloth or non-woven fabric can be used as a water-absorbing substance, alternatively or in addition to the high water-absorbing resins. The film and the non-woven fabric, used for the humidity-controlling materials in the present invention, are preferably water-impermeable and vapor-permeable. Films obtained by making numerous fine pores of 0.01 to 10 µm through films of, for example, polyethylene, polypropylene, polyurethane and a fluororesin may be used as the film. Among them, a polyethylene or polypropylene type film is preferably used in the present invention because they are inexpensive and have a heat sealing property. Espoir (trade name, manufactured by Mitsui Toatsu Kagaku KK) and Hipore (trade name, manufactured by Asahi Kasei Kogyo KK) are available in the market as these films. Non-woven fabrics obtained by weaving at random fibers of resins such as polyethylene, polypropylene and nylon, particularly polyethylene or polypropylene base non-woven fabrics having a heat sealing property are preferred as the water-impermeable and vapor-permeable non-woven fabric. Various ones are available in the market as these non-woven fabrics and, for example, Taibeck (trade name, manufactured by Du Pont) using high density polyethylene as a raw material is available. These films and non-woven fabrics have a thickness of 5 to 500 µm, preferably 10 to 200 µm. The humidity-controlling material used in the present invention preferably contains the water-absorbing substance absorbing a salt solution or water in a vessel or a bag comprising a water-impermeable and vapor-permeable film or non-woven fabric. The whole wall of the vessel or bag does not have to be composed of the film or non-woven fabric described above, and at least a part of the wall may be composed of the film or non-woven fabric described above. The other part of the wall may be reinforced by a reinforcing member. Natural or synthetic polymers usually used for vessels, cloth and non-woven fabrics are used as the reinforcing member. The humidity-controlling material used in the present invention can be produced according to production methods for sanitary napkins, paper diapers or water-absorbing sheets described in JP-A-5-31856. For example, the preceding water-absorbing resins such as poly(sodium acrylate) are dispersed on a film coated with an adhesive binder such as a heat-meltable polymer and a latex, and then covered with a cloth, a film or paper to prepare a sheet having a high water-absorbing resin-containing layer as a core, followed by impregnating it with a salt solution or water, whereby the humidity-controlling material can be prepared. In this case, a fungicide and a preservative may be used together therewith. The cloth covering the high water-absorbing resin includes cloths using various fibers such as fibers comprising pulp, cellulose and synthetic resins. The film includes water-impermeable and vapor-permeable films. The paper includes Japanese paper, normal paper and synthetic paper such as rayon paper. Further, a humidity-controlling material which is covered with a cloth, a film or paper is further covered particularly preferably with a non-woven fabric in order to prevent moisture released from the humidity-controlling material from contacting directly the dry image-forming material. The low moisture-permeable film used in the present invention includes films obtained by laminating the resins described above on resin films of fluorinated resins such as polytetrafluoroethylene and polytrifluoroethylene, chlorinated rubber, polyvinylidene chloride, a copolymer of vinylidene chloride and acrylonitrile, polyethylene and polypropylene, and on plastic films of polyesters, or films obtained by depositing metal such as aluminum and metal oxide such as silicon oxide. The films available in the market include Saran UB manufactured by Asahi Kasei Kogyo KK, Kureharon manufactured by Kureha Kagaku Kogyo KK, VM-P manufactured by Toyo Boseki KK and Metaline Film manufactured by Tosero KK. Packages for the dry image-forming material and the humidity-controlling materials include a cassette (for example, a plastic cassette case for computer image formation) and a black-colored polyethylene bag (for example, a light-shielding bag used for packing a silver halide photographic light-sensitive material). The humidity-controlling material may be allowed to exist at both sides or one side of the dry imaging material, and in the case of a cassette, the humidity-controlling material may be adhered to the inside of the case. When the dry image-forming material and the humidity-controlling material are packed with the low moisture-permeable film, this may be done directly with the low moisture-permeable film, or a separator such as synthetic paper or a plastics film may be used. Further, the dry image-forming material and the humidity-controlling material may be put in the plastic cassette case described above, and then the cassette case may be packed with the low moisture-permeable film. The photosensitive microcapsules used in the present invention can be produced according to the methods disclosed in US-A-4,399,209 and 4,440,846 described previously. That is, the light-sensitive microcapsules contain a photo initiator and a photohardenable agent in the internal phase. They are typically a photo polymerizable material and a photo cross-linkable material, and are thickened or cured by exposure. Further, a color precursor is contained in addition to the light-sensitive materials described above. The photo-curable compound used in the present invention is preferably a material capable of being cured by radical addition polymerization or ionic polymerization but will not specifically be restricted thereto. A typical photo-curable compound is an ethylenically unsaturated organic compound. These compounds are preferably liquid and contain at least one terminal ethylene group per molecule. Further preferred examples of the photo-curable material are ethylenically unsaturated organic compounds having two or more ethylene groups per molecule. Typical examples of these compounds are ethylenically unsaturated acid esters of polyhydric alcohols such as trimethylolpropane triacrylate and dipentaerythritolhydroxy pentaacrylate. Further, other examples thereof include acrylate prepolymers obtained by partial reaction of pentaerythritol with acrylic acid or acrylic acid ester, and isocyanate-modified acrylic acid esters, methacrylic acid esters and itaconic acid esters of polyhydric alcohols each disclosed in US-A-3,783,151 and 3,759,809. The photo initiator produces free radicals being capable of starting free radical polymerization of polymerizable or cross-linkable compounds by absorbing radiation. Ionic dye-counter ionic compounds shown in JP-A-62-150242, JP-A-64-60606, JP-A-3-20260 and JP-A-3-116043 are preferably used as the photo initiator according to the present invention. The preferred ionic dye-counter ionic compounds are a cationic dye borate which is a compound represented by the following formula: wherein D represents a cationic dye; R 1 , R 2 , R 3 and R 4 each represent an alkyl group, an aryl group, an aralkyl group, an alkaryl group, an alkenyl group, an alkynyl group, a cycloalkyl group or an allyl group; and R 1 , R 2 , R 3 and R 4 may be the same or different. The useful dye forms a photo-reductive complex with a borate anion and include cationic methine, polymethine, triarylmethane, indoline, thiazine, oxazine and acridine dyes. More preferably, the dye a cationic cyanine, carbocyanine, hemicyanine, Rhodamine or azomethine dye. The useful cation dye is a cyanine dye represented by the following formula: wherein n is 0, 1, 2 or 3; R 5 represents an alkyl group; and Y represents CH=CH, N-CH 3 , C(CH 3 ) 2 , O, S or Se. In the borate anion, one to three or less of R 1 , R 2 , R 3 and R 4 , are preferably alkyl groups. The alkyl group preferably has up to 20 carbon atoms, more preferably 1 to 7 carbon atoms. R 1 , R 2 , R 3 and R 4 are preferably a combination of an alkyl group, an aryl group or an aralkyl group and more preferably a combination of three aryl groups and one alkyl group (for example, triphenylbutylborate). Further, other examples thereof include, as disclosed in JP-A-5-224426, diaryl ketone derivatives, polycyclic quinones, benzoin alkyl ethers, alkoxyphenyl ketones, o-acylated oxyimino ketones, phenanthrenequinone, benzophenone, substituted benzophenones, xanthone, thioxanthone, halogenated compounds, for example, chlorosulfonyl and chloromethyl polynuclear aromatic compounds, chlorosulfonyl and chloromethyl heterocyclic compounds, chlorosulfonyl and chloromethyl benzophenone, fluorenone, and halo alkanes. A colorless electron-donating compound can be given as a dye precursor used in the present invention. Typical examples of this compound include substantially colorless compounds having a lactone, lactam, sultone, spiropyran, ester or amide structure in a partial skeleton thereof. They include, for example, triarylmethane compounds, bisphenylmethane compounds, xanthene compounds, fluoran compounds, thiazine compounds and spiropyran compounds. Next, the specific examples of the dye precursors developing colors of yellow, magenta and cyan shall be shown: Yellow color precursors: Magenta color precursors: Cyan color precursors: The light-sensitive microcapsules used in the present invention can use as a sensitizer to improve photosensitivity, for example, N,N-dialkylaniline and the like defined as an auto-antioxidant described in JP-A-62-18537 and JP-A-64-91130, disulfide compounds such as mercaptobenzothiazole disulfide described in JP-A-2-291561, and thiol compounds described in JP-A-2-868. A discontinuous walled microcapsule of the present invention, used for encapsulating the internal phase, can be produced according to known encapsulation techniques including coacervation, interfacial polymerization and polymerization of one or more monomers in an oil. Typical examples of suitable capsule wall-formers include gelatin materials (US-A-2,730,456 and 2,800,457) including gum arabic, polyvinyl alcohol and carboxymethyl cellulose; resorcinol-formaldehyde capsule wall-formers (US-A-3,755,190), isocyanate wall-formers (US-A-3,914,511), isocyanate-polyol wall-formers (US-A-3,796,669), urea-formaldehyde wall-formers, particularly urea-resorcinol-formaldehyde in which a lipophilic property is strengthened by adding resorcinol (US-A-4,001,140) and melamine-formaldehyde and hydroxypropyl cellulose (US-A-4,025,455). The microcapsules used in the present invention have an average grain diameter falling preferably in a range of 1 to 25 micron. The capsules have preferably a small and uniform grain diameter in terms of the photographic characteristics such as resolving power. Considering breakability by applying pressure and troubles such as missing in the pores or fibers of the support, the sizes are controlled preferably to 3 to 15 micron, particularly preferably 3 to 10 micron. The above microcapsules are mixed with a dispersion of the color-developer and applied on a paper or film support, whereby a self-contained type sheet can be prepared. In this case, a suitable binder such as polyvinyl alcohol and styrene-butadiene latex may be used. In such a case, the microcapsules can suitably be mixed with the dispersion of the developer in a proportion of 2/8 to 8/2 in terms of a weight ratio of the solid matters, and they are mixed particularly preferably in a proportion of 4/6 to 6/4. The above microcapsules are applied on a paper or film support using a suitable binder such as polyvinyl alcohol and styrene-butadiene emulsion, and then the dispersion of the developer is coated thereon, whereby a self-contained type sheet can be prepared. In this case, after applying the developer dispersion on the support, the microcapsule dispersion is coated thereon, whereby a self-contained type sheet can be prepared as well. Developing substances usually used for carbonless paper are suitably used as a color-developer, and included are clay substances such as acid clay, activated clay, atabargite and zeolite; and organic substances such as a phenol resin, a phenol-formaldehyde resin, and aromatic carboxylic acids and metal salts thereof, for example a metal salt of salicylic acid. The support used in the present invention includes synthetic resin films of polyethylene, polypropylene, polyethylene terephthalate, polycarbonate and cellulose acetate, synthetic papers, so-called resin-coated papers coated with resins such as polyethylene, art paper, and baryta paper. According to the present invention, there can be provided a packing method for a full color dry image-forming material which does not cause muddy color even after storage over a long period of time. The present invention will specifically be explained below with reference to examples, but not restricted only to them. Examples The present invention will be explained below based on the examples. Example 1 I. Preparation of light-sensitive microcapsules I-1 Preparation of magenta microcapsule Light-sensitive microcapsules were prepared with reference to the examples described in JP-A-2-298340. A. Preparation of internal phase 1 ○ 105 g of trimethylolpropane triacrylate (TMPTA) and 45 g of dipentaerythritolhydroxy pentaacrylate (DPHPA) were added to a beaker and heated at about 105°C for 30 minutes. 2 ○ 20 g of a dye precursor (M-1) was added and dissolved while stirring. Further, stirring was continued at 105°C for 30 minutes while heating, and then the solution was gradually cooled down to 70°C. 3 ○ 0.5 g of a photo initiator (1,1'-di-n-heptyl-3,3,3',3'-tetramethylindocarbocyanine triphenyl-n-butylborate) was added while stirring, and then stirring was further continued at 70°C for 30 minutes. 4 ○ 1.0 g of DIDMA (2,6-diisopropyl-N,N-dimethylaniline) was added while stirring, and stirring was continued for 5 minutes. 5 ○ 0.5 g of 2,2'-Dibenzothiazolyl disulfide was added, and stirring was continued for 20 minutes. 6 ○ 10 g of Duranate 24A-90PX (polyisocyanate manufactured by Asahi Kasei) was added and maintained at 70°C. B. Preparation of external phase 1 ○ 430 g of water was added to a beaker and stirred by means of an overhead mixer at 500 rpm. 2 ○ 8.0 g of Varsa TL-502 (sulfonated polystyrene manufactured by National Starch) was slowly added and further stirred at 500 rpm for 15 minutes. 3 ○ 12.65 g of pectin and 0.24 g of sodium hydrogencarbonate were mixed and added while stirring at a stirring speed controlled to 1500 rpm, and then stirring was further continued at 1500 rpm for 2 hours. 4 ○ NaOH was used to control pH to 6.0, and stirring was further continued at 3000 rpm for 10 minutes. C. Emulsification of internal phase in external phase 1 ○ The internal phase was gradually added to the external phase in about 30 seconds. 2 ○ Stirring was carried out for emulsification at 3000 rpm for 15 minutes to form an emulsion. D. Formation of melamine-formaldehyde wall 1 ○ 250 g of water was added to a beaker, and 22.2 g of melamine was gradually added while stirring. 2 ○ 36.5 g of a 37 % formaldehyde was gradually added. 3 ○ The solution was heated up to 60°C in about 30 minutes, and curing was carried out at 60°C for 60 minutes (formation of a melamine-formaldehyde preliminary condensation product). 4 ○ A stirring speed in emulsification was controlled to 1500 rpm, and the melamine-formaldehyde preliminary condensation product was added to the emulsion prepared in C. 5 ○ H 3 PO 4 was used to control pH to 6.0. 6 ○ Subsequently, curing was carried out at 70°C for 60 minutes to form internal phase-containing microcapsules. 7 ○ 46.2 g of a 25 % urea aqueous solution was added, and curing was carried out for 60 minutes. 8 ○ The stirring speed was set to 500 rpm, and 10 g of 20 % NaOH was added. Then, the solution was cooled down to room temperature. 9 ○ Further, stirring was continued overnight as it was at room temperatures to obtain a microcapsule dispersion (A). The microcapsules thus obtained had a grain diameter of 2 to 12 µ, and a great part thereof fell in a range of 6 to 7µ. The solid percent was determined by means of an electronic moisture content meter manufactured by Shimazu Seisakusho to find that it was 25.2 % by weight. I-2 Preparation of cyan microcapsules. Following the preparation of the magenta microcapsules described in I-1, 20 g of C-3 was added in place of the dye precursor M-1, and the photo initiator was changed to 0.85 g of 1,1'-di-n-heptyl-3,3,3',3'-tetramethylindodicarbocyanine triphenyl-n-butylborate, whereby a microcapsule dispersion (B) was obtained. The microcapsules(B) thus obtained had a grain diameter of 2 to 12 µ, and the solid percent was 26.3 %. I-3 Prepartion of yellow microcapsules. Following the preparation of the magenta microcapsules described in I-1, 20 g of Y-1 was added in place of the dye precursor M-1, and the photo initiator was changed to 0.8 g of 3,3-dimethyl-1-heptylindo-3'-heptylthiacyanine triphenyl-n-butylborate, whereby a microcapsule dispersion (C) was obtained. The microcapsules (C) thus obtained had a grain diameter of 5 to 10 µ, and a great part thereof fell in a range of 6 to 8 µ. The solid percent was 27.5 %. II. Preparation and coating of light-sensitive liquid The microcapsule dispersions obtained in I and a color-developer HRJ-4250 (manufactured by Schenectady Chemical Co.) described in JP-A-1-168484 and JP-A-2-95884 were mixed as shown below to prepare a light-sensitive liquid (I). Microcapsule dispersion (A) 5.6 g Microcapsule dispersion (B) 4.9 g Microcapsule dispersion (C) 4.7 g HRJ-4250 15.8 g H 2 O 9.0 g The light-sensitive liquid (I) thus prepared was applied on a transparent PET film by means of a Mayer bar of # 20. The coated amount thereof after drying was 10.2 g/m 2 . Next, an opaque adhesive film (word processor adhesive film White WT-325W, manufactured by Plus) was stuck as a protective film on the surface of the coated sample to form a sandwich structure of the PET film, whereby a sample (I) was prepared. Test 1 : The sample (I) thus prepared was irradiated with an LED (Ga, Al, As) having a main emission at 660 nm and an LED (GaN) having a main emission at 525 nm to cure the magenta capsule and the cyan capsule and then subjected to pressure development by means of a pressure roller, whereby a pure yellow color was developed on the whole surface. Then, the above sample (I) was packed in a black polyethylene bag and held under storage conditions of 20°C and a relative humidity of 20 % for 72 hours. This sample was irradiated on the same exposing conditions as with the LED described above and subjected to pressure development, but a pure yellow color was not developed, and magenta and cyan were slightly developed, so that a turbid yellow color was developed. A 50 % calcium chloride dihydrate aqueous solution was absorbed into 3 g of a high water-absorbing resin Aquapren P-815 (manufacture by Meisei Kagaku Kogyo KK), which was put in a bag made of a water-impermeable and vapor-permeable non-woven fabric Taipeck 1073B (trade name, manufactured by Du Pont) and an aluminum-deposited film Metaline Film ML-CPWH (trade name, manufactured by Tosero KK), whereby a humidity-controlling material (I) was prepared. This humidity-controlling material (I) maintained the inside of a glass sealed vessel at 60 RH at 25°C. Test 2 : Next, the humidity-controlling material described above and the above sample (I) were packed together in a black polyethylene bag and similarly maintained under storage conditions of 20°C and a relative humidity of 20 % for 72 hours. This sample was irradiated on the same exposing conditions as with the LED described above and subjected to pressure development to find that turbidity was not observed at all and a pure yellow color was developed. The respective developed color densities in a non-treating condition and after aging were measured via a red filter, a green filter and a blue filter. The results thereof are shown in Table 1. In Table 1, R shows the measured value obtained via the red filter; G shows the measured value obtained via the green filter; and B shows the measured value obtained via the blue filter. Test No. Non-treated condition Aging for 72 hours Humidity-controlling material R G B R G B 1 (Comparison) 0.20 0.21 1.50 0.55 0.47 1.50 None 2 (Invention) 0.20 0.21 1.50 0.20 0.20 1.50 Present It was found from the results shown in Table 1 that while the present invention using the humidity-controlling material (I) hardly changed at all in the density values even after maintaining at a low humidity and showed an excellent stability, the density values obtained via the red filter and the green filter increased when the humidity-controlling material was not used, so that a turbid yellow color was developed. The above comparative sample was observed under a microscope to find lump-shaped developed color matters of magenta and cyan in a developed yellow matter. Example 2 Following Example 1, a full color original image was introduced into a personal computer to expose the sample (I) by means of a red LED having a main emission at 660 nm, a green LED having a main emission at 525 nm and a blue LED (GaN) having a main emission at 470 nm, whereby a full color original image was reproduced. As a result thereof, the full color image close to the original image was obtained. Next, the sample (I) was packed in a black polyethylene bag in the same manner as in Example 1 and held under storage conditions of 20°C and a relative humidity of 20 % for 72 hours to investigate a change in the developed colors with the passage of time. Further, the humidity-controlling material was packed in the black polyethylene bag together with the sample (I), and they were held similarly under storage conditions of 20°C and a relative humidity of 20 % for 72 hours. As a result thereof, while the sample allowed to coexist with the humidity-controlling material of the present invention was not different at all from what used to be before storing for aging and showed a good full color reproducibility, the colors were apparently darkened in the comparative example using no humidity-controlling material, so that the vivid full colors developed before storing for aging could not be reproduced. Further, the samples described above were left to stand under the same conditions for 2 weeks, and the sample of the present invention gave a developed color image which was not different from what used to be before storing for aging. In the comparative example using no humidity-controlling material, however, muddy color was produced more and more, and the fog density increased, so that an image which was darkened on the whole surface and had completely no commercial value was obtained. Example 3 Test 3 : The sample (I) was packed in a black polyethylene bag together with the humidity-controlling material described above and maintained under storage conditions of 20°C and a relative humidity of 80 % for 2 weeks. It was exposed and developed in the same manners as in Example 2 to obtain a good full color image close to the original image. The fog densities in the non-treated condition and after aging were measured in the same manner as in Example 1. The results thereof are shown in Table 2. Test 4 : The samples were maintained in the same manner as described above, except that the humidity-controlling material was not used, and the resulting image did not reproduce the original full color image in terms of colors. The fog densities in the non-treated condition and after aging were measured in the same manner as in Example 1. The results thereof are shown in Table 2. Test No. Non-treated condition Aging for 72 hours Humidity-controlling material R G B R G B 3 (Invention) 0.24 0.20 0.22 0.27 0.21 0.23 Present 4 (Comparison) 0.24 0.20 0.22 0.58 0.90 0.77 None It was found from the results shown in Table 2 that while the present invention using the humidity-controlling material increased less in fog and showed an excellent stability, a marked increase in fog was shown when using no humidity-controlling material. Example 4 Test 5 : Following Example 1 described previously, a humidity-controlling material (II) obtained by absorbing about 500 ml/m 2 of water into an absorbing sheet contained in a sanitary product (trade name: Elis) manufactured by Daio Seishi KK was used in place of the humidity-controlling material prepared from Aquapren P-815 and the 50 calcium chloride aqueous solution, and the sample (I) described in Example 1 was packed in a black polyethylene bag together with it and held under storage conditions of 20°C and a relative humidity of 20 % for 72 hours. The sample was irradiated on the same exposing conditions as with the LED described previously and subjected to pressure development to find that turbidity was not observed at all and a pure yellow color was developed. The respective developed color densities in a non-treating condition and after aging were measured via a red filter, a green filter and a blue filter. The results thereof are shown in Table 3. In Table 3, R shows the measured value obtained via the red filter; G shows the measured value obtained via the green filter; and B shows the measured value obtained via the blue filter. Test No. Non-treated condition Aging for 72 hours Humidity-controlling material R G B R G B 1 (Comparison) 0.20 0.21 1.50 0.55 0.47 1.50 None 5 (Invention) 0.20 0.21 1.50 0.20 0.20 1.50 Present It was found from the results shown in Table 3 that the present invention using the absorbing sheet hardly changed at all in the density values even after maintaining at a low humidity and showed an excellent stability. Example 5 Test 6 : Following Example 2 described previously, the humidity-controlling material (II) described in Example 4 was used to form a full color image. The humidity-controlling material (II) and the sample (I) were packed together in a black polyethylene bag similarly to Example 2 and maintained under storage conditions of 20°C and a relative humidity of 20 % for 72 hours. As a result thereof, the sample allowed to coexist with the humidity-controlling material (II) prepared according to the present invention was not different at all from what used to be before storing for aging and showed a good full color reproducibility. Further, the sample was left for standing on the same conditions for 2 weeks, and a developed color image which was not different at all from what used to be before aging was obtained. Example 6 Test 7: The sample (I) was packed in a bag using an aluminum-deposited polyethylene film (trade name: Metaline Film, manufactured by Toserlo KK) together with the humidity-controlling material (II) described above and maintained under storage conditions of 20°C and a relative humidity of 20 % for 4 weeks. It was exposed and developed in the same manner as in Example 2 to obtain a good full color image close to the original image. The sample was maintained in the same manner as described above, except that a black-colored Japanese paper was used in place of the aluminum-deposited polyethylene film to find that the resulting image had apparently a darkened color and the original full color image was not reproduced.

Claims: A packing method for a dry image-forming material comprising a support and a layer, provided thereon, containing microcapsules containing at least a photocurable or photohardenable compound, a photoinitiator and a color precursor in the internal phase, further containing a color-developer in either the layer containing the microcapsules or a layer adjacent thereto, which comprises packing the dry image-forming material together with a humidity-controlling material containing a water-absorbing substance having an absorbed salt solution or absorbed water. A packing method as claimed in claim 1, wherein the dry image-forming material and the humidity-controlling material are packed with a low moisture-permeable film. A packing method as claimed in claim 2, wherein the low moisture-permeable film is a plastic film on which is deposited a metal. A packing method as claimed in claim 3, wherein the metal is aluminium. A packing method as claimed in any preceding claim, wherein the humidity-controlling material is a vessel or a bag of which at least part of the wall is composed of a water-impermeable and vapor-permeable film or non-woven fabric. A packing method as claimed in claim 5, wherein at least a part of the wall of the vessel or bag is composed of cloth, film or paper. A packing method as claimed in any preceding claim, wherein the water-absorbing substance comprises cotton, pulp, sponge, cloth or non-woven fabric. A packing method as claimed in any preceding claim, wherein the water-absorbing substance comprises a high water-absorbing resin. A packing method as claimed in claim 8, wherein the high water-absorbing resin is a vinyl alcohol-acrylamide copolymer, a modified polyethylene oxide, a metal salt of polyacrylic acid, a cellulose-based polymer or a starch-based polymer. A packing method according to any preceding claim wherein the photo-curable compound is a radical addition-polymerization product. A packing method according to any preceding claim, wherein the photo initiator is one generating free radicals being capable of absorbing radiation to initiate free radical polymerization of a polymerizable or cross-linkable compound. A packing method according to any preceding claim, wherein the color precursor is a substantially colorless, electron-donating compound having a lactone, lactam, sultone, spiropyran, ester or amide structure in at least part of its molecular skeleton. A packing method according to any preceding claim, wherein the color-developer is clay, a phenol resin, a metal salt of salicylic acid or a mixture thereof. A package comprising a dry image-forming material comprising a support and a layer, provided thereon, containing microcapsules containing at least a photocurable or photohardenable compound, a photoinitiator and a color precursor in the internal phase, further containing a color-developer in either the layer containing the microcapsules or a layer adjacent thereto, together with a humidity-controlling material containing a water-absorbing substance having an absorbed salt solution or absorbed water. A package as claimed in claim 14, wherein the dry image-forming material and the humidity-controlling material are packed with a low moisture-permeable film. A package as claimed in claim 15, wherein the low moisture-permeable film is a plastic film on which is deposited a metal. A package as claimed in claim 16, wherein the metal is aluminium. A package as claimed in any of claims 14 to 17, wherein the humidity-controlling material is a vessel or a bag of which at least part of the wall is composed of a water-impermeable and vapor-permeable film or non-woven fabric. A package as claimed in any of claims 14 to 18, wherein at least a part of the wall of the vessel or bag is composed of cloth, film or paper. A package as claimed in any of claims 14 to 19, wherein the water-absorbing substance comprises cotton, pulp, sponge, cloth or non-woven fabric. A package as claimed in any of claims 14 to 20, wherein the water-absorbing substance comprises a high water-absorbing resin. A package as claimed in claim 21, wherein the high water-absorbing resin is a vinyl alcohol-acrylamide copolymer, a modified polyethylene oxide, a metal salt of polyacrylic acid, a cellulose-based polymer or a starch-based polymer. A package as claimed in any of claims 14 to 22, wherein the photo-curable compound is a radical addition-polymerization product. A package as claimed in any of claims 14 to 23, wherein the photo initiator is one generating free radicals being capable of absorbing radiation to initiate free radical polymerization of a polymerizable or cross-linkable compound. A package as claimed in any of claims 14 to 24, wherein the color precursor is a substantially colorless, electron-donating compound having a lactone, lactam, sultone, spiropyran, ester or amide structure in at least part of its molecular skeleton. A package as claimed in any of claims 14 to 25, wherein the color-developer is clay, a phenol resin, a metal salt of salicylic acid or a mixture thereof.

Inventors: HIGUCHI TETSUYA, SUZUKI MASAO, UCHIBORI TAKAHIRO, YOSHITAKA SUGIMOTO, HIGUCHI, TETSUYA, SUZUKI, MASAO, UCHIBORI, TAKAHIRO, YOSHITAKA, SUGIMOTO, Higuchi, Tetsuya, Oriental Photo Ind. Co., Ltd., Suzuki, Masao, Oriental Photo Ind. Co., Ltd., Uchibori, Takahiro, Oriental Photo Ind. Co., Ltd., Yoshitaka, Sugimoto, Oriental Photo Ind. Co., Ltd.
Applicants: CYCOLOR SYSTEM CO LTD, CYCOLOR SYSTEM CO., LTD.
Application year: 1998
Main classification: G03F7
IPC codes: G03F7, G03C3