Injection molding apparatus having a melt bore through the front end of the pin

Abstract: Multi-cavity injection molding apparatus for three layer molding having elongated pins (110) for fixed pin gating or valve gating. Each elongated pin (110) has a central melt bore (130) extending rearwardly from its front end to a number of laterally extending bores (132). A low viscosity barrier material such as EVOH or nylon flows through these bores to the gate leading to the cavity. This allows coinjection with fixed pins and sprue gating in one embodiment and by valve gating in another embodiment.

Description: Background of the Invention This invention relates generally to multi-cavity injection molding apparatus for three layer molding according to the preamble of claim 1 and more particularly to such apparatus wherein an elongated pin extending through a central melt channel in each heated nozzle has a central melt bore extending rearwardly from its front end. Multi-cavity injection molding apparatus for making three layer protective containers for food or preforms or parisons for beverage bottles are known. One layer of a barrier material such as ethylene vinyl alcohol copolymer (EVOH) or nylon is molded between two layers of a polyethylene terephthalate (PET) type material. In some multi-cavity apparatus, the two different melts are distributed through a single melt distribution manifold having two melt passages, but preferably for materials such as these having different injection temperatures of about 204,4°C and 296,1°C (400°F and 565°F) respectively, the two melts are distributed through two different melt distribution manifolds. In some cases, the two melts are injected sequentially, while in other cases both coinjection and sequential injection are utilized. The two melts are both injected through a heated nozzle having a central melt channel and an annular melt channel extending around the central melt channel to a gate leading to the cavity. From DE 4103318 A1, an injection machine nozzle is known. The structure has a central melt and a valve pin which is subjected to pressure coming from machine nozzle 16. The valve pin has a central melt bore for centrally injecting a core material into the gate. In addition, the valve is able to obstruct the melt passage for the material of the outer layer. As seen in U.S. Patent No. 4, 717, 324 to Schad et al. which issued January 5, 1998, valve gated apparatus has been used for three layer molding. However, that apparatus has the disadvantage that it does not disclose sprue gating apparatus and also that the valve gated apparatus does not allow simultaneous or coinjection of the two melts. SUMMARY OF THE INJECTION Accordingly, it is an object of the present invention to at least partially overcome the disadvantages of the prior art by providing multi-cavity injection molding apparatus for three layer molding which allows sprue gating with fixed pins and simultaneous or coinjection by valve gating. This object is achieved by an injection molding apparatus according to claim 1. To this end, in one of its aspects, the invention provides multi-cavity injection molding apparatus for three layer molding having one or more melt distribution manifolds with a front face and a plurality of heated nozzles mounted in a mold. Each heated nozzle has a rear end abutting against the melt distribution manifold and a front end adjacent a gate leading to a cavity in the mold. Each heated nozzle has a central melt channel extending therethrough from the rear end to the front end and one annular melt channel extending around the central melt channel to the front end. An elongated pin having a rear end, a front end and an outer surface extends in the central melt channel in each heated nozzle in alignment with a gate leading to a cavity in the mold. A melt passage from the melt source branches in the melt distribution manifold and extends through the one annular melt channel in each heated nozzle to the gate. Another melt passage from another melt source branches in the melt distribution manifold and extends along the elongated pin in the central melt channel in each heated nozzle to the gate. Each elongated pin has a central melt bore and at least one lateral melt bore, both being part of the second melt passage. The central melt bore extends a predetermined distance rearwardly from the front end of the elongated pin to a rear end of the central melt bore. The lateral melt bore extends outwardly from the rear end of the central melt bore to the outer surface of the elongated pin. The elongated pin comprises a longitudinal groove to guide the second melt passage through the central melt channel along the elongated pin. BRIEF DESCRIPTION OF THE DRAWINGS Figure 1 is a sectional view of a portion of a multi-cavity injection molding apparatus having sprue gating with fixed elongated pins according to one embodiment of the invention, Figure 2 is an enlarged section of a portion of Figure 1, Figure 3 is an enlarged sectional view showing the melt flow through the central melt bore in the front end of the elongated pin seen in Figure 1, Figure 4 is an isometric view showing a front portion of the elongated pin seen in Figure 1, Figure 5 is a sectional view of a portion of a multi-cavity injection molding apparatus having valve gating elongated pins according to another embodiment of the invention, Figure 6 is an enlarged sectional view showing the valve pin seen in Figure 5 in the middle position, Figure 7 is a similar view to Figure 6 showing the valve pin in the open position, Figure 8 is a sectional view of a portion of a multi-cavity injection molding apparatus having sprue gating with fixed elongated pins according to a further embodiment of the invention, Figure 9 is an exploded isometric view showing the three layers of the melt transfer and dividing bushing as seen in Figure 8 before they are integrally joined together, Figure 10 is a similar view showing the other faces of the three layers of the same melt transfer and dividing bushing, and Figure 11 is a cut-away isometric view showing the melt conduits in the same melt transfer and dividing bushing. DETAILED DESCRIPTION OF THE INVENTION Reference is first made to Figures 1 and 2 which show a portion of multi-cavity injection molding apparatus for molding three layer preforms or other products by a combination of sequential and simultaneous coinjection through sprue gates. A number of heated nozzles 10 are mounted in a mold 12 with their rear ends 14 abutting against the front face 16 of a steel front melt distribution manifold 18. While the mold 12 can have a greater number of plates depending upon the application, in this case only a nozzle retainer plate 20, a manifold retainer plate 22 and a back plate 24 secured together by bolts 26, as well as a cavity retainer plate 28 are shown for ease of illustration. The front tip end 30 of each heated nozzle 10 is aligned with a sprue gate 32 extending through a cooled gate insert 34 to a cavity 36. This cavity 36 for making beverage bottle preforms extends between a cavity insert 38 and a mold core 40 in a conventional manner. One melt passage 42 for the PET extends from an inlet 44 through a cylindrical manifold extension 46 and branches in the front melt distribution manifold 18 to extend through a melt dividing bushing 48 received in a seat 50 in the front face 16 of the front melt distribution manifold 18 to each heated nozzle 10. The melt dividing bushings 48 are retained in proper alignment by small alignment dowels 52 extending into the front melt distribution manifold 18. While only a single heated nozzle 10 is shown for ease of illustration, it is understood that in a typical configuration there will be many heated nozzles 10 (eg. 32, 48 or 64) seated in the mold to receive melt through the melt passage 42 which will have a more complex configuration than that shown. Each heated nozzle 10 is seated in an opening 54 in the nozzle retainer plate 20 with its rear end 14 abutting against the front end 56 of the melt dividing bushing 48. The heated nozzle 10 is heated by an integral electrical heating element 58 having a terminal 60. A rear collar portion 62 of each heated nozzle 10 is received in a circular locating seat 64 extending around the opening 54. This provides an insulative air space 66 between the heated nozzle 10 and the surrounding mold 12 which is cooled by pumping cooling water through cooling conduits 68. In the configuration shown, each heated nozzle 10 has an insert portion 70 which is secured in a seat 72 by a threaded nozzle seal 73 which is screwed into place and forms the front tip end 30 of the heated nozzle 10. As can be seen, the insert portion 70 is made of several steel pieces 74 which fit together to provide an annular melt channel 76 extending around a central melt channel 78 to the front tip end 30. The insert portion 70 of the heated nozzle 10 also has an annular insulative air space 79 which extends between the central melt channel 78 and the surrounding annular melt channel 76 to provide some thermal separation between them. The central melt channel 78 extends from the rear end 14 of the heated nozzle 10, while the surrounding annular melt channel 76 extends from four spaced melt bores 80 running to the rear end 14 of the heated nozzle 10. A circle of spaced holes 82 are drilled in the rear end 14 of the heated nozzle 10 to extend between the central melt channel 78 and the surrounding spaced melt bores 80 to provide some thermal separation between them. The melt dividing bushing 48 is made of three steel layers integrally brazed together as described in co-pending Canadian Patent Application Serial No. 2,219,054 entitled, "Injection Molding Apparatus Having Melt Dividing Bushings" filed concurrently herewith. As described therein, the PET melt passage 42 divides in the melt dividing bushing 48 and extends through four spaced holes 84 which are in alignment with the four spaced melt bores 80 in the rear end 14 of the heated nozzle 10. The front melt distribution manifold 18 is heated by an integral electrical heating element 86. It is located by a central locating ring 88 and screws 90 extending into each heated nozzle 10 to have an insulative air space 92 extending between it and the surrounding cooled mold 12. In this configuration, another steel rear melt distribution manifold 94 is mounted in the mold 12 by a number of insulative and resilient spacers 96 extending between it and the back plate 24 to extend parallel to the front melt distribution manifold 18. As can be seen, the two manifolds 18, 94 are separated by thermal insulating melt transfer bushings 98 positioned between them. As described in more detail below, the rear melt distribution manifold 94 is heated by an integral electrical heating element 100 to a lower operating temperature than the front melt distribution manifold 18, and the air space 101 provided by the thermal insulating melt transfer bushing 98 between the two manifolds 18, 94 provides thermal separation between them. In this configuration, each thermal insulating melt transfer bushing 98 has an elongated stem portion 102 extending forwardly from a rear head portion 103 through a bore 104 in the front melt distribution manifold 18 and a central bore 106 in the melt dividing bushing 48 and accurately retains the melt transfer bushing 98 in place. The melt transfer bushing 98 also has a central bore 108 which extends through the stem portion 102 and receives an elongated pin 110 according to the invention. The elongated pin 110 also extends through the central melt channel 78 in the heated nozzle 10. As described in more detail below, the elongated pin 110 is fixed in place with its head 112 seated in the rear face 114 of the rear head portion 103 of the melt transfer bushing 98 and its partially tapered front end 116 adjacent to and in alignment with the gate 32. A separate melt passage 118 for the barrier material extends from another inlet 120 and branches in the rear melt distribution manifold 94 to extend through an L-shaped passage 122 drilled in the rear head portion 103 of each melt transfer bushing 98 to a longitudinal groove 124 machined to extend a predetermined distance rearwardly in each fixed pin 110. In other embodiments, the groove 124 can extend helically around the fixed pin 110. However, in view of the relatively low volume and low viscosity of the barrier material, it is preferable to have the fixed pin 110 fit in the bore 108 in the melt transfer bushing 98 and the central melt channel 78 in the heated nozzle 10 and provide the elongated or helical groove 124 in each fixed pin 110 for the barrier material to flow through. Each melt transfer bushing 98 is mounted in proper alignment by a small dowel 126 which extends between it and the front melt distribution manifold 18. The fixed pin 110 is similarly kept in proper alignment by a small dowel 128 extending from its head 112 into the surrounding rear head portion 103 of the melt transfer bushing 98. As best seen in Figures 3 and 4, each fixed pin 110 has a central melt bore 130 extending rearwardly from its front end 116 to four lateral melt bores 132 extending outwardly to the outer surface 134 of the fixed pin 110. The lateral melt bores 132 extend diagonally outward from the rear end 136 of the central melt bore 130 to the outer surface 134. In this embodiment, each fixed pin 110 has a reduced diameter portion 138 which extends forwardly from the front end of the longitudinal groove 124 to its front end 116 and fits in a reduced diameter portion 139 of the central melt channel 78 through the heated nozzle 10. The reduced diameter portion 138 of the fixed pin 110 is longer than the reduced diameter portion 139 of the central melt channel 78 which thus forms a space 140 around the reduced diameter portion 138 of the fixed pin 110. Thus, the barrier material melt passage 118 extends from the longitudinal groove 124 in each fixed pin 110 into this space 140 and then inwardly through the lateral melt bores 132 and forwardly through the central melt bore 130 to the gate 32 leading to the cavity 36. In other embodiments, the fixed pin 110 can have one or a different number of lateral bores extending inwardly from the front end of the longitudinal groove 124 to the rear end 136 of the central melt bore 130. In use, the injection molding system is assembled as shown in Figures 1 and 2 and operates to form three layer preforms or other products as follows. First, electrical power is applied to the heating element 86 in the front melt distribution manifold 18 and the heating elements 58 in the heated nozzles 10 to heat them to an operating temperature of about 296,1°C (565°F). Electrical power is also applied to the heating element 100 in the rear melt distribution manifold 94 to heat it to an operating temperature of about 204,4°C (400°F). Water is supplied to the cooling conduits 68 to cool the mold 12 and the gate inserts 34. Hot pressurized melt is then injected from separate injection cylinders (not shown) into the first and second melt passages 42, 118 through inlets 44, 120 according to a predetermined cycle. The melt injected into the first melt passage 42 is a polyethylene terephthalate (PET) type material. The first melt passage 42 branches in the front melt distribution manifold 18 and extends to each melt dividing bushing 48 where it divides into the four spaced holes 84 aligned with the four melt bores 80 in the rear end 14 of the heated nozzle 10. It then extends from these four spaced melt bores 80 through the annular melt channel 76 to the gate 32. The melt injected into the second melt passage 118 is a suitable barrier material such as ethylene vinyl copolymer (EVOH) or nylon. The second melt passage 118 branches in the rear melt distribution manifold 94 and extends through the aligned passage 122 in each melt transfer bushing 98 and the aligned longitudinal or helical groove 124 in each fixed pin 110 which extends through the central bore 108 in the melt transfer bushing 98, the central bore 106 in the melt dividing bushing 48 and the central melt channel 78 in the heated nozzle 10 into the space 140 around the reduced diameter portion 138 of each fixed pin 110. The second melt passage 118 then extends through the lateral bores 132 and the central melt bore 130 in each fixed pin 110 leading to the aligned gate 32. During each cycle, a predetermined quantity of PET is injected through the first melt passage 42 and outer layers 141 of it adhere to the sides 142 of the cavity 36. A short period of time after the start of PET injection, a predetermined quantity of the less viscous barrier material is then simultaneously injected through the second melt passage 118 and forms a central layer 144 between the two outer layers 141 of PET. When the cavities 36 are almost filled, the injection pressure of the barrier material is released which stops its flow and the PET injection is continued to completely fill the cavities 36. Injection pressure of the PET is then released and, after a short cooling period, the mold 12 is opened for ejection. After ejection, the mold 12 is closed and the cycle is repeated continuously every 15 to 30 seconds with a frequency depending upon the wall thickness and number and size of cavities 36 and the exact materials being molded. The central location of the central melt bore 130 at the front end 30 of the fixed pin 110 and the relatively small size of the groove 124 and the central melt bore 130 combine with the relatively low volume and low viscosity of the barrier material to ensure that the flow of the barrier material is reliable and a very thin layer of the barrier material can be provided. Reference is now made to Figures 5 - 7 showing injection molding apparatus according to another embodiment of the invention for molding three layer preforms or other products by a combination of sequential and simultaneous coinjection. As many of the elements are the same as described above, not all the elements common to both embodiments are described and those that are described again have the same reference numerals as before. In this embodiment, the apparatus has valve gates rather than sprue gates with fixed pins. Each elongated valve pin 110 has the same shape except that its front end 116 is cylindrical rather than partially tapered. The elongated valve pin 110 is reciprocated in the central melt channel 78 in each heated nozzle 10 by hydraulic actuating mechanism 146 according to a predetermined cycle. In this case, the thermal insulating melt transfer bushing 98 also has a neck portion 148 extending rearwardly through an opening 150 in the rear melt distribution manifold 94, and the central bore 108 extends through this rear neck portion 148. Each elongated valve pin 110 fits in the central bore 108 in the melt transfer bushing 98 which is aligned with the central melt channel 78 in the heated nozzle 10 tightly enough to prevent melt leakage around the elongated valve pin 110 as it reciprocates. The head 112 of the elongated valve pin 110 is connected to a front piston 152 seated in a cylinder 154 in the back or cylinder plate 24. The actuating mechanism 146 also includes a rear piston 156, and the two pistons 152, 156 are driven by controlled oil pressure applied through ducts 158 to reciprocate the valve pin 110 between three different positions. While hydraulic actuating mechanisms 146 are shown for ease of illustration, of course other types of actuating mechanisms such as electro-mechanical mechanisms can be used for other applications. In the first or middle position shown in Figure 6, the front end 116 of each valve pin 110 is retracted only far enough and long enough to allow a small quantity of PET to flow through the annular melt channel 76. In this embodiment, there is a double blockage of the flow of the barrier material in this middle position. As seen in Figure 6, the lateral melt bores 132 in the valve pin 110 are too far forward to connect with the space 140 around the reduced diameter portion 138 of the valve pin 110. Furthermore, as seen in Figure 5, the longitudinal or helical groove 124 in the valve pin 110 does not extend far enough rearwardly to connect with the L-shaped passage 122 in the head portion 103 of the melt transfer bushing 98 in this position. In other embodiments, it may only be necessary to use one or the other of these ways of blocking the flow of barrier material. Then, the front end 116 of each valve pin 110 is retracted further to a second or open position shown in Figure 7. In this position, the lateral melt bores 132 in the valve pin 110 are connected with the space 140 around the reduced diameter portion 138 of each valve pin 110 and the groove 124 in the valve pin 110 does connect with the L-shaped passage 122 in the melt transfer bushing 98 which allows the barrier material to flow through the melt passage 118 into the cavities 36. As mentioned above, the central location of the central melt bore 130 at the front end 30 of the fixed pin 110 and the relatively small size of the groove 124 and the central melt bore 130 combine with the relatively low volume and low viscosity of the barrier material to ensure that the flow of the barrier material is reliable to provide a uniform and very thin layer of the barrier material, which is quite an expensive material. As seen in Figure 7, the barrier material flowing simultaneously with the PET splits the PET flow in two and provides a central layer 160 of the barrier material between two outer layers 162 of PET. When the cavities 36 are almost filled, the front end of each valve member 110 is returned to the first position closing off the flow of the barrier material through the central melt bore 130. The flow of PET through the annular melt channel 76 continues until the cavities 36 are completely filled. Each valve pin 110 is then driven to the third or forward closed position in which its front end 116 is seated in the gate 32 flush with the cavity 36. After a short cooling period, the mold is opened for ejection. After ejection, the mold is closed and the cycle is repeated continuously every 15 to 30 seconds with a frequency depending upon the wall thickness and number and size of cavities 36 and the exact materials being molded. Reference is now made to Figures 8 - 11 showing injection molding apparatus according to another embodiment of the invention for molding three layer preforms or other products by a combination of sequential and simultaneous coinjection to sprue gates. In this case, the rear melt distribution manifold 94 rather than the front melt distribution manifold 18 has the manifold extension 46. Thus, the first melt passage 42 for the PET extends from the common inlet 44 in the manifold extension 46 extends through the rear melt distribution manifold 94 rather than the front melt distribution manifold 18. Furthermore, the second melt passage 118 for the barrier material extends from the second inlet 120 through the front melt distribution manifold 18 rather than the rear melt distribution manifold 94. As can be seen, a melt transfer and dividing bushing 164 is seated behind each heated nozzle 10 in a cylindrical opening 166 through the front melt distribution manifold 18 with its rear end 168 abutting against the rear melt distribution manifold 94. The rear end 14 of each of the heated nozzles 10 abuts against the front end 169 of one of the melt transfer and dividing bushings 164 as well as against the front melt distribution manifold 18. Each fixed pin 110 has a central melt bore 130 and four lateral melt bores 132 as shown in Figure 3. Referring also to Figures 9 - 11, each of the melt transfer and dividing bushings 164 is made by integrally joining together first, second and third layers 170, 172, 174. The first layer 170 is machined to have a central hole 176 extending therethrough from its rear face 178 to its front face 180. The central hole 176 has a larger diameter portion 182 adjacent the rear face 178 to receive the head 112 of the fixed pin 110. The first layer 170 is drilled to also have an off-center hole 184 extending therethrough. The second layer 172 is drilled to have two holes 186 spaced on opposite sides of a central hole 188 extending therethrough. The front face 180 of the first layer 170 and the rear face 190 of the second layer 172 are machined to have matching grooves 192, 194 which join when the three layers 170, 172, 174 are joined together to form a first curved melt conduit 196 which branches from the off-centre hole 184 through the first layer 172 to the two spaced holes 186 through the second layer 172. The third layer 174 is drilled to have four holes 198 spaced around a central hole 200 which is aligned with the central melt channel 78 in the aligned heated nozzle 10. Each of the four spaced holes 198 are in alignment with one of the four spaced melt bores 80 extending from the rear end 14 of the heated nozzle 10 to the annular melt channel 76. The third layer 174 is drilled to also have a radial bore 202 extending to the central hole 200 in alignment with the second melt passage 118 in the front melt distribution manifold 18. The front face 204 of the second layer 172 and the rear face 206 of the third layer 174 are machined to each have a pair of matching grooves 208, 210 which join when the three layers 170, 172, 174 are joined together to form a pair of second curved melt conduits 212. Each second curved melt conduits 212 branches from one of the two spaced holes 186 through the second layer 172 to two of the four spaced holes 198 through the third layer 174 in alignment with the four melt bores 80 extending from the rear end 14 of the heated nozzle 10 to the annular melt channel 76. The three layers 170, 172, 174 are also drilled to have holes 214 to receive alignment dowels 216. A quantity of nickel alloy (not shown) is applied to the front face or faces 180 of the first layer 170 and the front face 204 of the second layer 172 and the three layers 170, 172, 174 are assembled together with the dowels 216 keeping them in proper alignment. The assembled layers 170, 172, 174 are then loaded into a vacuum furnace and gradually heated to a temperature of approximately 496,1°C (925°F) which is above the melting temperature of the nickel alloy. As the furnace is heated, it is evacuated to a relatively high vacuum to remove substantially all of the oxygen and then partially backfilled with an inert gas such as argon or nitrogen. When the melting point of the nickel alloy is reached, the nickel alloy melts and flows by capillary action between the first layer 170, the second layer 172 and the third layer 174 to integrally braze them together to form an integral melt transfer and dividing bushing 164. The use of the injection molding system shown in Figure 8 is essentially the same as that described above in regard to Figures 1 - 4, except that the rear melt distribution manifold 94 and the heated nozzles 10 are heated to an operating temperature of about 296,1°C (565°F) and the front melt distribution manifold is heated to an operating temperature of about 204,4°C (400°F). Also, the PET type material is injected into the first passage 42 which branches in the rear melt distribution manifold 94 and extends through each melt transfer and dividing bushing 164 to the annular melt channel 76 in the aligned heated nozzle 10. The barrier material is now injected into the second melt passage 118 which branches in the front melt distribution manifold and extends through the radial bore 202 and along the groove 124 in each fixed pin 110. While the description of the three layer injection molding apparatus having elongated pins 110 with central melt bores 130 at their front ends 116 has been given with respect to fixed gate and valve gate embodiments, it will be evident that other various modifications are possible without departing from the scope of the invention as understood by those skilled in the art and as defined in the following claims. For instance, materials having suitable characteristics can be used rather than PET and EVOH or nylon.

Claims: A multi-cavity injection molding apparatus for three layer molding having at least one melt distribution manifold (18, 94) with a front face (16) and a plurality of heated nozzles (10) mounted in a mold (12), each heated nozzle (10) having a rear end (14) abutting against the at least one melt distribution (18, 94) manifold (18, 94) and a front end (30) adjacent a gate (32) leading to a cavity (36) in the mold (12), each heated nozzle (10) having a central melt channel (78) extending therethrough from the rear end (14) to the front end (30) and one annular melt channel (76) extending around the central melt channel (78) to the front end (30), an elongated pin (110) having a rear end (112), a front end (116) and an outer surface extending in the central melt channel (78) in each heated nozzle (10) in alignment with a gate (32) leading to a cavity (36) in the mold (12), a first melt passage (42) from a first melt source branching in the at least one melt distribution manifold (18, 94) and extending through the annular melt channel (76) in each heated nozzle (10) to the gate (32), a second melt passage (118) from a second melt source branching in the at least one melt distribution manifold (18, 94) and extending along the elongated pin (110) in the central melt channel (78) in each heated nozzle (10) to the gate (32), each elongated pin (110) has a central melt bore (130) and at least one lateral melt bore (132); both being part of the second melt passage (118), the central melt bore (130) extending a predetermined distance rearwardly from the front end (116) of the elongated pin (110) to a rear end of the central melt bore (130), the at least one lateral melt bore (132) extending outwardly from the rear end of the central melt bore (130) to the outer surface of the elongated pin (110), characterized in that the elongated pin (110) comprises a longitudinal groove (124) to guide the second melt passage (118) through the central melt channel (78) along the elongated pin (110). Injection molding apparatus as claimed in claim 1 wherein the first melt passage (42) from the first melt source branches in a front melt distribution manifold (18, 94) mounted in the mold (12) and the second melt passage (120) from the second melt source branches in a rear melt distribution manifold (18, 94) mounted in the mold (12). Injection molding apparatus as claimed in claim 2 wherein the front melt distribution manifold (18, 94) extends substantially parallel to and is spaced a predetermined distance from the rear melt distribution manifold (18, 94), each elongated pin (110) extends through a bore (166) through the front melt distribution manifold (18, 94) and the second melt passage (120) from the second melt source branches in the rear melt distribution manifold (18, 94) and then extends along each elongated pin (110) in the bores in the front melt distribution manifold (18, 94). Injection molding apparatus as claimed in claim 1 wherein each elongated pin (110) has four lateral melt bores (132) extending radially outwardly from the rear end of the central melt bore (130) to the outer surface of the elongated pin (110). Injection molding apparatus as claimed in claim 4 wherein the lateral melt bores (132) extend diagonally from the rear end of the central melt bore (130) to the outer surface of the elongated pin (110). Injection molding apparatus as claimed in one of claims 1 to 5 wherein each elongated pin (110) is fixed in position with the front end (116) of the pin (110) adjacent the gate (32). Injection molding apparatus as claimed in one of claims 1 to 5 wherein the rear end (112) of each elongated pin (110) is connected to actuating mechanism (146) whereby the elongated pin (110) is reciprocated between several different positions according to a predetermined injection cycle. Injection molding apparatus as claimed in claim 1 wherein the groove (124) extends helically around the elongated pin (110). Injection molding apparatus as claimed in claim 7 wherein the groove (124) extends a predetermined distance rearwardly whereby the groove (124) connects with the second melt passage from the second melt distribution manifold (18, 94) only in a retracted open position. Injection molding apparatus as claimed in one of claims 1 to 9, wherein a plurality of melt transfer and dividing bushings (48, 164) are provided, each dividing bushing (48) having a rear end and a front end (56, 169) and being mounted in an opening (50, 166) through the front melt distribution manifold (18, 94) with the rear ends of the melt transfer and dividing bushings (48, 164) abutting against the rear melt distribution manifold (18, 94) and the front end (56, 169) of each melt transfer and dividing bushing (48, 164) abutting against the rear end (14) of one of the heated nozzles (10), whereby a first melt passage (42) from a first melt source branches in the rear melt distribution manifold (18, 94) and extends through each melt transfer and dividing bushing (48, 164) and the annular melt channel (76) in each heated nozzle (10) to a gate (32) adjacent the front end (30) of the heated nozzle (10) leading to a cavity (36) in the mold (12), and a second melt passage (118) from a second melt source branches in the front melt distribution manifold (18, 94) and extends through the melt transfer and dividing bushing (48, 164) and along the elongated pin (110) in the central melt channel in each heated nozzle (10) to the gate (32).

Inventors: BABIN DENIS L, GELLERT JOBST ULRICH, BABIN, DENIS L., GELLERT, JOBST ULRICH
Applicants: MOLD MASTERS LTD, MOLD-MASTERS LIMITED
Application year: 1998
Main classification: B29C45
IPC codes: B29L9, B29K23, B29C45, B29K67, B29K77