Alkoxy-functional sealants with rapid development of green strength

Abstract: There is disclosed herein a room temperature vulcanizable (RTV) sealant composition comprising a polymer with silicon-containing endgroups with at least two silicon-bonded alkoxy groups, a titanium catalyst of the formula Ti(OR 2 ) (4-y) (OR 3 ) y where each R 2 is a monovalent tertiary aliphatic hydrocarbon radical or a monovalent branched-secondary aliphatic hydrocarbon radical, each R 3 is a monovalent linear aliphatic hydrocarbon radical having from 1 to 6 carbon atoms per radical, y has an average value of from 0 to 1 inclusive, a filler, and an alkoxysilane having at least two silicon-bonded alkoxy groups. These sealant compositions exhibit a rapid formation of green strength, cure rapidly and do not yellow or discolor.

Description: This invention relates to a moisture curable, room-temperature curable (RTV) composition containing silicon-bonded alkoxy functionality and a titanium catalyst. Organopolysiloxane compositions which cure to elastomeric materials at room temperature are well known. Such compositions are obtainable by mixing a polydiorganosiloxane having reactive groups, such as silanol groups, with a silane crosslinking agent for polydiorganosiloxane, for example, alkoxy silane, acetoxy silane, oximo silane or amino silane. These compositions are next cured by exposure to atmospheric moisture at room temperature, and depending upon the particular ingredients or amounts, are either stored in a container which protects said composition from moisture and are thereafter cured by moisture exposure (a one-package composition); or are stored in two or more containers which are subsequently mixed and cured immediately upon mixing (a two-package composition). Moisture curable compositions are well known for their use as sealants. It is important that sealants are capable of curing in comparatively thick layers (sometimes call thick section), to provide an elastomeric body with a thickness of greater than two millimeters (mm). Many sealant compositions preferably cure to provide a seal within several hours, but not so quickly that the surface cannot be tooled to a desired configuration after application of the sealant composition. Among the desirable attributes for such compositions are: fast surface cure rate, good elasticity of the skin formed and lack of surface tackiness after curing for 24 hours. For some applications, it is desirable to have a clear, translucent or "water white" product which retains its translucency and lack of color during use. To increase the speed of cure of alkoxy silane containing silicone compositions, it is the usual practice to employ certain organic titanium compounds as catalysts for the hydrolysis and condensation reaction. Some titanium compounds are apt to react with methoxysilane to form a white precipitate in compositions containing them and this problem gives a discoloration and further restricts the ability of the composition to cure. Also, the generally preferred titanium compounds are those derived from primary or secondary alcohols, for example, isopropyl alcohol and n-butyl alcohol. However, these titanium compounds are often inadequate to promote a sufficiently rapid and/or deep section cure. Moreover, it is a practice to employ a chelating agent, such as acetylacetonate, as an accelerator and stabilizer for the titanium compound. The acetylacetonate may also be mixed with the titanium compound or reacted with it to provide a complex. These acetylkacetonate containing materials inevitably lead to a cured silicone product which has a yellow tint. A solution to the yellowing problem has been sought for many years. EP-A 0 747 443 teaches that a restricted class of compounds, of an element having a valency of 4 and selected from Group IVB of the Periodic Table (for example titanium), will achieve the desired characteristics of speed of cure together with non-yellowing without the presence of an acetylacetonate accelerator-stabilizer. They also provide translucent, "water white" cured products. These compounds have a general formula of M[OR'] a [OR"] b where M represents a metal having a valence of 4 and is a metal selected from Group IVB of the Periodic Table, a has an average value of from 0 to 1 inclusive, b has an average value of from 3 to 4 inclusive, and a + b is 4. R" in said formula represents a monovalent, tertiary or branched-secondary aliphatic hydrocarbon group, and R' represents a monovalent linear aliphatic hydrocarbon group having from 1 to 6 inclusive carbon atoms. According to EP-A 0 747 443, it is important that R" be a bulky structure, i.e. tertiary or branched-secondary to minimize the tendency of the metal atom, M, to oligomerize via oxo bridge formation between metal atoms. A four-coordinated metallic compound can be maintained therein as a stable species towards hydrolysis and condensation reactions under mild hydrolysis conditions. This permits the avoidance of acetylacetonate as a ligand to stabilize a titanium ester catalyst, and also avoid the yellowing discoloration, while enhancing the cure speed. Preferably, there are several R" groups in each molecule of metal compound. Titanium is the preferred metal. The OR" group is derived from a tertiary or branched-secondary alcohol. Preferred R" are those represented by the general formula - CR 6 R 7 R 8 in which each R 6 , R 7 , and R 8 is a monovalent aliphatic hydrocarbon radical having from 1 to 6 inclusive carbon atoms per radical. The most preferred metallic compounds are those in which a is 0 and b is 4, and all the R" groups are tertiary aliphatic groups. A preferred group of metallic compounds therein are those represented by the general formula Ti(OR') a (OR") b where R" is -C(CH 3 ) 3 or -C(C 2 H 5 )(CH 3 ) 2 and R' is isopropyl. Furthermore, the above described metallic compounds are used in amount of from 0.2 to 10 parts by weight per 100 parts by weight of a polymeric material to be further described below. This polymeric material is typically represented by the general formula X-A-X where A may be any desired organic or siloxane molecular chain. For example, a polyoxyalkylene chain or more preferably a polydiorganosiloxane chain that includes siloxane units R 9 s SiO (4-s)/2 in which R 9 represents an alkyl radical of from 1 to 6 inclusive carbon atoms per radical, vinyl, phenyl or a fluorinated alkyl radical and s is 0, 1, or 2. The preferred linear polymeric materials are linear with units in which s is 2. These preferred linear polydiorganosiloxane chains are represented by the general formula -(R 9 2 SiO) t - in which each R 9 represents methyl and t has a value of from 200 to 1500. X of the polymeric material is silyl groups which contain silicon-bonded hydroxyl or alkoxy groups. These silyl groups are illustrated by -Si(R 9 ) 2 OH, -SiR 9 (OR 10 ) 2 , -Si(OR 10 ) 3 , -Si(R 9 ) 2 (OR 10 ), and -Si(R 9 ) 2 -R 11 -Si(R 9 ) p (OR 10 ) (3-p) where R 9 is as defined above and preferably is methyl. R 11 is a divalent hydrocarbon radical which may be interrupted by one or more siloxane spacers having up to six silicon atoms; R 10 is an alkyl or alkoxyalkyl in which the alkyl radical has from 1 to 6 carbon atoms and p is 0, 1, or 2. Additionally, EP-A 0 747 443 provides compositions which can also contain an alkoxysilane curative of the general formula R 9 (4-n) Si(OR 10 ) n in which R 9 and R 10 are defined above and n is 2, 3 or 4. The preferred alkoxysilanes are those in which R 9 is methyl, ethyl or vinyl. R 10 is methyl or ethyl and n is 3. Alkoxysilanes are thus illustrated by methyltrimethoxysilane, vinyltrimethoxysilane, methyltriethoxysilane and vinyltriethoxysilane. A sufficient amount of the alkoxysilane is employed to ensure adequate stability of the composition during storage and adequate composition crosslinking when it is exposed to atmospheric moisture. The preferred compositions of the previously mentioned application are those using the preferred catalyst materials (metallic compound) and containing no co-catalyst or chelating agent. These will expediently cure at an acceptably fast rate and will give cured translucent or water white elastomeric reaction products in thicknesses greater than 2 mm. If a more rapid cure is desired, a chelate, for example acetylacetonate, may also be added to the mixture. Acetylacetonate is used as an accelerator and/or stabilizer, but leads to yellowing of the product. Further, EP-A 0 747 443 states that these compositions optionally contain other ingredients which are conventional to the formulation of silicone sealants. For example, these optional ingredients are finely divided fillers, such as reinforcing or extending fillers, illustrated by high surface area fumed and precipitated silica, crushed quartz, diatomaceous earth, calcium carbonate, barium sulfate, iron oxide, titanium dioxide and carbon black. The amount of such fillers will depend on the properties desired in the elastomer-forming composition and the cured elastomer. Usually, the content of this composition will be within the range from 5 to 150 parts by weight per 100 parts by weight of the polymeric material. Other ingredients may also be included, such as co-catalysts for increasing the rate of cure, pigments, plasticizers, agents (usually organosilicon compounds) for treating fillers, rheological additives for improving toolability and adhesion improving substances, for example, gamma-aminopropyltriethoxysilane. Suitable co-catalysts are known in the art and include the metal salts of carboxylic acids, for example, lead octoate or dibutyltin dilaurate, dibutyl tin diacetate, and stannous octoate. Ingredients used as a plasticizer or to reduce the modulus of the cured elastomer may include polydimethylsiloxane, having terminal trioganosiloxy units where the organo groups are methyl, vinyl or phenyl and combinations of these groups. For example, the polydimethylsiloxanes used as plasticizers or modulus reducing agents normally have a viscosity of from 100 to 100,000 mPa·s measured at 25°C. and are used in amounts up to 80 parts by weight per 100 parts by weight of the polymeric material. The compositions of EP-A 0 747 443 are prepared by mixing the ingredients in any order and by employing any suitable mixing equipment. Generally, it is preferred to add the metallic compound after mixing together the polymeric material and the curative silane. Optional ingredients may be incorporated at any stage of this mixing operation but are preferably added after the catalyst. After mixing, the compositions are stored under substantially anhydrous conditions, for example, in sealed containers until required for use. These compositions can be formulated as single part formulations which are stable in storage but cure on exposure to atmospheric moisture and may be employed as coatings, caulking materials and encapsulating materials. They are particularly suitable for sealing joints, cavities, and other spaces in articles and structures which are subject to relative movement. They are useful as glazing sealants and for sealing building structures. They have cured properties with a modulus sufficiently low for most industry standards and an elongation at break which is sufficiently high for most industry standards. While EP-A 0 747 443 teaches very useful compositions which are made using the metallic compound, there is a continued need to have a sealant which quickly develops green strength to allow the packaging and shipping of assembled components soon after they are manufactured. Many of the sealant compositions used in the past, such as those silicone sealant compositions which evolve acetic acid, ketoximes or amines, may cause corrosion of sensitive metals or plastics. These former sealant compositions also have some unpleasant associated odors during the curing process, especially when used in confined areas where assemblies are manufactured, such as insulated glass window units. The use of compositions catalyzed by titanium compounds and liberating alcohols upon cure are considered to be less corrosive and they emit a more pleasant odor during the curing process than those off-gassing acetic acid, ketoximes or amines. However, alkoxy-functional silicone sealant compositions catalyzed with a titanium catalyst are known to be slow to cure. They are seldom found to have tack-free-times (TFT) of less than 20 minutes and they often have time-to-rubber (TTR) times of more than 30 minutes. Such properties clearly are not suitable to replace the previously used sealants in applications where manufacture requires rapid assembly, packaging and shipping. The immediate need is therefore to have sealant compositions which will quickly develop green strength for the purpose of maintaining the manufactured assembly's integrity, are less corrosive, do not yellow or otherwise discolor, and are compatible with more of the materials used in the construction of assemblies. In view of the prior discovery of metallic compounds with bulky alkoxy groups to make RTV sealant compositions which cure fast and do not yellow, an investigation was undertaken by us to find a way to make sealant compositions which cure fast, quickly develop green strength, do not yellow, and are less corrosive. For the purposes of this invention, a composition which rapidly develops green strength is one which exhibits a fast-forming, high-modulus skin of sufficient strength, such that elements of a construction are formed and maintain their desired configuration even if handled, packaged and shipped, after relatively short cure times and without showing permanent deformation. EP 0 747 443 A discloses a moisture curable composition capable of being cured to an elastomeric body comprising: (A) the product formed by mixing a polymeric material having not less than two groups bonded to silicon which are hydroxyl or alkoxy groups, and an alkoxysilane curative; and (B) a compound according to the general formula M[OR] x [OR'] y where M represents a metal having a valency of 4 selected from Group IVB of the Periodic Table, x has a value of from 0 to 1, y has a value of from 3 to 4 and (x+y)=4, R' represents a group selected from monovalent tertiary and branched-secondary aliphatic hydrocarbon groups and R represents a monovalent linear aliphatic hydrocarbon group having 1 to 6 carbon atoms which is different from R'. Unexpectedly, we have found that there is a class of RTV sealant compositions which provide the rapid development of green strength when cure is initiated, cure fast, do not yellow and are less corrosive. It is, therefore, an object of this invention to provide RTV compositions which are based on silicon-bonded alkoxy-functional containing compositions and which efficiently use the titanium catalyst of EP-A 0 747 443. This invention relates to a composition comprising the product obtainable by mixing (A) a polymer which contains per molecule an average of at least 1.2 (RO) (3-x) R 1 x Si- chain terminations where each R is methyl or ethyl, each R 1 is methyl, ethyl, vinyl, and x has an average value of from 0 to 1 inclusive; (B) a titanium catalyst of the average formula Ti(OR 2 ) (4-y) (OR 3 ) y where each R 2 is selected from a monovalent tertiary aliphatic hydrocarbon radical, each R 3 is a monovalent linear aliphatic hydrocarbon radical having from 1 to 6 carbon atoms per radical, y has an average value of from 0 to 1 inclusive; (C) a filler having a hydroxyl group content derived from hydroxyl groups selected from the group consisting of covalent-bonded hydroxyl radicals, adsorbed water, or both the covalent-bonded hydroxyl radicals and the adsorbed water; and (D) an alkoxysilane of the average formula R 4 z Si(OR 5 ) (4-z) in which each R 4 is methyl, ethyl, or vinyl, each R 5 is methyl or ethyl, and z has an average value of from 1 to 2 inclusive, where each of ingredients (A), (B), (C), and (D) are present in amounts such that a molar ratio (I) is from 0.9 to 5 and a molar ratio (II) is from 0.6 to 2, where molar ratio (I) = moles of titanium catalyst + moles of alkoxysilane moles of hydroxyl group in (C) and molar ratio (II) = moles of titanium catalyst moles of alkoxysilane + moles of silicon-bonded alkoxy unit chain terminations in (A). The composition of this invention is an RTV sealant composition which comprises a polymer having at least 60 percent of the endgroups (chain terminations) with a silicon atom bearing at least two silicon-bonded alkoxy groups per endgroup; a crosslinker having at least two silicon-bonded alkoxy groups per molecule where the alkoxy is methoxy or ethoxy; a filler; a titanium catalyst for promoting room temperature cure of said composition where the titanium catalyst has an average formula Ti(OR 2 ) (4-y) (OR 3 ) y and the ingredients are present in amounts such that they meet defined molar ratios (I) and (II). Polymer (A) is represented by the general formula Y-B-Y where B is any desired organic or siloxane molecular chain, for example, a polyoxyalkylene chain or a polydiorganosiloxane chain which includes siloxane units R 9 s SiO (4-s)/2 in which R 9 represents an alkyl radical of from 1 to 6 inclusive carbon atoms per radical, phenyl, or a fluorinated alkyl radical, and s is 0, 1 or 2. The preferred polymers are polydiorganosiloxanes with siloxane units in which the average value of s is 2. These preferred polydiorganosiloxanes are represented by the general formula -(R 9 2 SiO) t - in which each R 9 represents methyl and t has a value of from 200 to 1500. At least 60 percent of the number of Y groups of the polymer is a silyl group which contains at least two silicon-bonded alkoxy groups. Those polymers that contain chain terminations other than those having silicon-bonded alkoxy groups are preferably triorganosilyl, such as trimethylsilyl, dimethylvinylsilyl, or methylphenylvinylsilyl units. Those silyl groups containing silicon-bonded alkoxy groups are illustrated by -SiR 1 (OR) 2 , -Si(OR) 3 and -Si(R 1 ) 2 -R 11 -Si(R 1 ) v (OR) (3-v) where R 1 is defined above and preferably is methyl, R 11 is a divalent hydrocarbon radical which may be interrupted by one or more siloxane spacers having up to six silicon atoms, R is methyl or ethyl and v is 0 or 1. The polydiorganosiloxanes, as well as crosslinkers, fillers and other optional ingredients useful in our RTV silicone sealant compositions are well known in the art and are generally illustrated by U.S. Patents 3,151,099; 3,161,614; 3,175,993; 3,334,067; 4,871,827; 4,898,910 and 4,956,435 which show RTV silicone sealant composition ingredients and methods of their preparation. However, these prior art patents describe only some useful ingredients and those ingredients which are useful in this invention will be further identified herein by this description. The polydiorganosiloxanes of our RTV silicone sealant compositions are those polydiorganosiloxanes which have endgroups containing silicon atoms with at least two alkoxy groups per endgroup. These polydiorganosiloxanes include those in which the linkages between the silicon atoms of the polymer chain are oxygen atoms including the linkage to the chain terminating silyl unit. The polydiorganosiloxanes also include those polymers where the chain terminations contain at least one linkage of a divalent hydrocarbon radical between two silicon atoms. These polydiorganosiloxanes are well known in the art and further discussion is unnecessary. These polydiorganosiloxanes can also be mixtures of polymers, for example, mixtures of the polydiorganosiloxanes having one endgroup as a triorganosiloxy unit, such as trimethylsiloxy or vinyl-dimethylsiloxy and the other endgroup being a silicon-bonded alkoxy containing unit, where in such mixtures there is an average per molecule of at least 1.2 alkoxy-containing silyl chain terminations. Preferably, there is an average of at least 1.5 alkoxy-containing silyl chain terminations per molecule. In these mixtures, 40 percent or less of the total endgroups are triorganosiloxy, and preferably less than 25 percent of the endgroups are triorganosiloxy. The preferred endgroups are trimethylsilyl or dimethylvinylsilyl and are preferably present in less than 25 percent of the total endgroups. The alkoxy groups are methoxy or ethoxy. The polydiorganosiloxanes having endgroups containing silicon atoms with at least two silicon-bonded alkoxy groups per silicon endgroup and where the silicon atoms of the polymer chain are linked by oxygen atoms, are exemplified by the disclosure of U.S. Patent 3,161,614 and are illustrated by the general average formula or by mixtures of the polydiorganosiloxanes of formula (I) and polydiorganosiloxanes of the following general average formula In the above formulae, R is methyl or ethyl; R 2 is methyl, ethyl, or vinyl; R 9 is an alkyl radical of 1 to 6 inclusive carbon atoms, phenyl, or a fluorinated alkyl radical; g has an average value of 2 to 3 inclusive; and f has an average value of at least 200. The preferred polydiorganosiloxanes of this kind are the polydimethylsiloxanes, and especially those with viscosities at 25°C. of from 5 to 150 Pa·s. The polydiorganosiloxanes of (A) with end segments containing linkages of divalent hydrocarbon radicals between some of the silicon atoms of the polymer chain include those described in U.S. Patents 3,175,993; 4,871,827 and 4,898,910 which show polydiorganosiloxanes having end segments with at least one divalent hydrocarbon radical linkage between polymer-chain silicon atoms and their methods of preparation. Such polydiorganosiloxanes are illustrated by the following general average formula where R, R 9 , g , and f are described above, R 19 is methyl, ethyl and Z is a divalent hydrocarbon radical or a combination of divalent hydrocarbon radicals and siloxane segments of 2 to 7 silicon atoms. The divalent hydrocarbon radicals are those having from 2 to 18 inclusive carbon atoms and are illustrated by ethylene, propylene, butylene, pentylene, and hexylene, preferably ethylene. When Z is a combination of divalent hydrocarbon radicals and siloxane segments, the polydiorganosiloxanes with end segments containing divalent hydrocarbon linkages and divalent siloxane segments interrupting at least divalent hydrocarbon linkages between the polymer chain silicon atoms, have end segments which, as Z, have the following general average formula where c has an average value of 1 to 6 inclusive, R 19 is defined above, and G is a divalent hydrocarbon radical free of aliphatic unsaturation of 2 to 18 carbon atoms. These polydiorganosiloxanes are prepared by reacting a hydrogen endblocked polydiorganosiloxane with a silane having an alkenyl radical in the presence of a hydrosilylation catalyst such as a platinum compound or complex or a polydiorganosiloxane having alkenyl endgroups, such as vinyl, are reacted, in the presence of a platinum catalyst, with an endcapping silicon-containing group which has silicon-bonded hydrogen atoms. If one uses a silane of the following general average formula one will make a polydiorganosiloxane as described by U.S. Patent 3,175,993, where e is 1 to 16, d is 0 or 1, and R, R 2 , R 19 , and g are defined above. If one uses an endcapper, such as the following general average formula, those polydiorganosiloxanes described by U.S. Patents 4,871,827 and 4,898,910 will be produced, where R, R 19 and g are defined above. The preferred polydiorganosiloxanes of this kind are those described immediately above where the divalent hydrocarbon radical is ethylene and have a viscosity at 25°C. of 5 to 150 Pa·s. U.S. Patent 4,898,910 describes useful polymers for our component (A) which have both vinyl containing endgroups and endgroups as described for the polymers of formula (III). Such polymers are mixtures of at least two kinds of polymers where one kind of polymer has alkoxy functional groups on both ends and another kind of polymer has alkoxy functional groups on one end and vinyl on the other end. These polymers are represented by the following general average formula: where R 9 methyl or ethyl, each D is selected from vinyl or a radical of the general average formula where each R 19 is methyl or ethyl and g has an average value of 2 to 3 inclusive. In these polymers, when some D are vinyl, there is 40 percent or less of the total endgroups with vinyl, and preferably less than 25 percent of the total endgroups with vinyl. Polymer (A) includes organic polymers with polyalkoxy-functional silicon-containing chain terminations as described herein. One particular class of such polymers is the polyoxyalkylene, such as described by U.S. Patent 5,403,881, which shows the polyoxyalkylene polymers with polyalkoxysilyl endgroups. These polymers are polyoxyalkylenes with a number average molecular weight of 500 to 16,000, whose main chain has units with the formula -R 18 O- in which R 18 is an alkylene group having 1 to 4 carbon atoms, and the chain termination segments have a general average formula in which R, R 19 and g are defined above, R 17 is a divalent hydrocarbon group, R 21 is hydrogen atom or a monovalent hydrocarbon group, R 22 is a monovalent hydrocarbon group, W is a divalent organic group, r is zero or a positive value, preferably r is a number with a value of at least 1, and u is 0 or 1. R 18 is a C 1 - C 4 alkylene group and is exemplified by methylene, ethylene, 1-methylethylene, 1-ethylethylene, and 1,1-dimethyl-ethylene. R 17 in the preceding formula is a divalent hydrocarbon group and is exemplified by methylene, ethylene, propylene, and butylene. R 21 is the hydrogen atom or a monovalent hydrocarbon group, and the latter is exemplified by alkyl groups such as methyl, ethyl, and propyl; cycloalkyl groups such as cyclohexyl; aryl groups such as phenyl, tolyl, and xylyl; and aralkyl groups such as benzyl or phenethyl. R 22 in each case is a monovalent hydrocarbon group as defined for R 21 . The group W in the preceding formula is a divalent organic group and is exemplified by methylene, ethylene, propylene, butylene, phenylene, and substituted phenylene. The polyoxyalkylenes of U.S. Patent 5,403,881 are synthesized by an addition reaction between SiH-containing organosiloxane with the following general average formula wherein R 22 , R, R 19 , W, g and r are defined as above, and polyoxyalkylene (number average molecular weight = 400 to 15,000) that contains in each molecule in molecular chain terminal positions at least 1.1 unsaturated groups with the formula wherein R 21 is defined as above. Titanium catalyst (B) has the average formula Ti(OR 2 ) (4-y) (OR 3 ) y where each R 2 is selected from a monovalent tertiary aliphatic hydrocarbon radical, each R 3 is a monovalent linear aliphatic hydrocarbon radical having from 1 to 6 carbon atoms per radical, y has an average value of from 0 to 1 inclusive. The titanium catalysts (B) useful for this invention, for the most part, are those described in EP-A 0 747 443. Preferably, there are several R 2 groups in each molecule. The OR 2 group is derived from a tertiary alcohol. Preferred R 2 are those represented by the general formula -CR 6 R 7 R 8 in which each R 6 , R 7 , and R 8 is a monovalent aliphatic hydrocarbon radical having from 1 to 6 inclusive carbon atoms per radical. The most preferred titanium compounds are those in which y has an average value of from 0 to 1 inclusive, and all the R 2 groups are tertiary aliphatic groups. A preferred group of titanium catalysts are those represented by the general formula Ti(OR 2 ) 4-y (OR 3 ) y where R 2 is -C(CH 3 ) 3 or -C(C 2 H 5 )(CH 3 ) 2 and R 3 is isopropyl. The most preferred titanium catalysts are those in which R 2 is -C(CH 3 ) 3 or -C(CH 3 ) 2 (CH 2 CH 3 ) and y is zero. The titanium catalyst (B) is present in our RTV sealant composition in amounts such that molar ratio (I) is 0.9 to 5, preferably 1 to 2.5 and molar ratio (II) is 0.6 to 2, preferably 0.8 to 1. The moles of titanium catalyst present in the claimed RTV sealant composition is a significant factor for both molar ratios. Molar ratio (I) is the sum of the moles of titanium catalyst (B) plus the moles of the alkoxysilane (D) divided by the moles of hydroxyl group in (C). The molar ratio (II) is the moles of titanium catalyst (B) divided by the sum of the moles of alkoxysilane (D) plus the moles of silicon-bonded alkoxy unit chain terminations in (A). Thus, the amount of the titanium catalyst (B) is a significant factor in determining both molar ratios (I) and (II) because the moles of titanium catalyst appears in the numerator of both ratios. Therefore, increasing the amount of titanium catalyst increases the molar ratios if the other ingredients remain constant. Because titanium catalyst can be expensive, small amounts of the catalyst are desirable. Smaller amounts of titanium catalyst (B) are also preferred because the RTV sealant compositions of this invention have better hydrolytic stability. High amounts of titanium catalyst show poorer hydrolytic stability because at increased titanium catalyst concentrations, the amount of Ti-O-Si bonds increase and these bonds are susceptible to cleavage under wet conditions. However, molar ratio (I) and molar ratio (II) need to meet their defined parameters to have acceptable shelf-stability based on molar ratio (I), and rapid development of green strength based on molar ratio (II). For this invention, shelf-stability means in-container stability. The uncured composition maintains its rheology during storage and when cured, the properties are essentially the same over the storage period, i.e. from time of manufacture to point of exposure to moisture and cure. The amount of titanium catalyst for curing our RTV sealant composition is often present such that there is from 0.1 to 5 weight percent based on the total weight of the claimed sealant composition. The titanium catalysts (B) are prepared by reacting tetrachlorotitanium or a tetraalkoxytitanium, such as tetraisopropoxytitanium, with a selected tertiary alcohol, for example tertiary-butanol or tertiary-amyl alcohol. Such reactions by-produce hydrochloric acid or an alcohol, such as isopropanol, that are preferably removed from the reaction medium to obtain the desired titanium catalysts (B). In the alkoxy exchange method, the starting tetraalkoxytitanium is preferably selected to ensure easy removal of the by-produced alcohol by vacuum devolatilization. Thus, the by-produced alcohol will have a boiling point which permits its easy removal from the reaction mixture without interfering with the preparation of titanium catalyst (B). Accordingly, not all alkoxytitanates are suitable for use in the preparation of titanium catalyst (B) because of the closeness of the boiling points of the reacting alcohol and the by-produced alcohol. For example, the boiling points of isopropanol (iPrOH), tertiary-butanol (t-BuOH), tertiary-amyl alcohol, and n-butanol are 82°C., 83°C., 102°C. and 118°C., respectively. Reaction of tertiary-amyl alcohol favorably replaces the alkoxy groups on tetra-isopropyltitanate (TiPT), tetra-ethyltitanate, and tetra-methyltitanate to produce tetra-tertiary-amyl titanate. The replacement reaction is favored when reacting tertiary-butanol with tetra-methyltitanate to produce tetra-tertiary-butyltitanate, but not with the other alkoxytitanates. The reaction between tertiary-butanol and tetra-isopropyl titanate can be conveniently used to produce titanium catalysts (B) where all the isopropoxy groups (-OiPr) of the tetra-isopropyl titanate are not replaced by the tertiary-butoxy groups (-OtBu). The particular reaction may be illustrated as follows: TiPT + t-BuOH ↔ Ti(OiPr) y (OtBu) (4-y) + iPrOH + t-BuOH where the value of y has an average of 0 to 1 inclusive and is preferably less than 0.85 to provide more desirable results, such as faster cure rates than those with higher y values. More preferred titanium catalysts (B) where both isopropoxy and tertiary-butoxy groups are present on the titanium atom are those which have a y value of less than 0.6. Conventional titanium catalysts for promoting the curing of the prior art alkoxy-containing RTV silicone sealant compositions are those as described by U.S. Patents 3,151,099; 3,161,614 and 3,175,993. Those titanium catalysts include tetraalkoxytitanates or chelated titanium compounds, examples of which include tetraethyl titanate, tetraisopropyl titanate, tetra-n-propyl titanate, tetrabutyl titanate, bis-acetylacetonyldiisopropyl titanate, 2,5-diisopropyl-bis-ethylacetoacetate titanium, and 1,3-dioxypropane-titanium-bis(ethylacetoacetate) where the latter is described in U.S. Patent 4,722,967. The titanium catalysts described by the above patents are not useful in the RTV sealant compositions of this invention. Our RTV sealant compositions also comprise a filler, (C), which is selected from those known to be useful in RTV sealants. These fillers include calcium carbonate, both ground, precipitated and colloidal calcium carbonates which are untreated or treated with stearate; crushed quartz; ground quartz; alumina; aluminum hydroxide; titanium dioxide; diatomaceous earth; reinforcing silicas such as fumed silicas, precipitated silicas and hydrophobed reinforcing silicas; iron oxide; carbon black and graphite. The amount of filler is that amount of filler which provides the desired properties to the uncured composition, such as viscosity, thixotropy, pigmentation and UV protection. The amount of filler used in our RTV sealant compositions also depends upon the cured physical properties desired such as tensile strength, elongation and durometer. This amount of filler is preferably from 5 to 50 weight percent based on the total weight of the RTV silicone sealant composition. The amount of filler allowable further depends upon hydroxyl content of the filler. The hydroxyl content is derived from hydroxyl groups covalently bonded to the filler and adsorbed water. Covalently bonded hydroxyl to be included in the hydroxyl content are those covalent hydroxyl groups which are available for reaction and that would exclude those which might be hidden within a filler particle and thus unavailable for reaction. The hydroxyl content also includes adsorbed water which is available for reaction. Absorbed water would also include associated water on the filler surface and water which becomes available from within the filler to be available for reaction. The amount of filler used is that amount needed to provide molar ratio (I) to be 0.9 to 5, and preferably 1 to 2.5. Molar ratio (I) is obtained by taking the sum of the moles of titanium catalyst (B) and the moles of alkoxysilane (D) and dividing by the moles of hydroxyl group in filler (C). The equation for the molar ratio (I) is shown above. A particular filler may only have adsorbed water available for reaction and may not have any covalently bonded hydroxyl groups available for reaction. However, many fillers have both the covalently bonded hydroxyl groups and adsorbed water available for reaction, for example untreated fumed silica filler. The hydroxyl content available for reaction is altered by drying the filler and/or pretreating the filler with hydrophobing agents which react with covalent-bonded hydroxyl groups and adsorbed water, such as hexamethyldisilazane and the like which are well known in the art. Calcium carbonate fillers are often treated with stearic acid to reduce the hydroxyl content. These treated fillers, such as the silicas and the calcium carbonates are available commercially. It is preferred to use fillers which have a low hydroxyl content; however, practical considerations find that most fillers have some hydroxyl content and it is very expensive to eliminate all hydroxyl content. Therefore, from a practical standpoint, all fillers will have some available-for-reaction hydroxyl content. The use of fillers with low hydroxyl content can reduce the cost by minimizing the amount of titanium catalyst (B), as required to meet molar ratios (I) and (II) needed to provide the fast development of green strength, as observed by short times-to-rubber (TTR) times. The amount of polymer (A) can also be reduced. Another property observed by the use of fillers with low hydroxyl content is the improvement of adhesion of the RTV sealant to polyvinylchloride. Blends of reinforcing fumed silica filler and ground calcium carbonate provide a useful filler mixture with a low hydroxyl content while maintaining excellent uncured and cured RTV sealant properties. It is believed that RTV sealant compositions which have a molar ratio (I) of 0.9 to 5 exhibit shelf-stability. By the term "shelf-stability", we mean that an RTV sealant composition when packaged will maintain its uncured properties during the expected storage period as observed when prepared and that the cured properties will be essentially the same when cured shortly after preparation as after a storage period. Because the moles of hydroxyl group in filler (C) is in the denominator of molar ratio (I), one finds that using fillers with lower hydroxyl content permits the use of combinations of titanium catalyst (B) and alkoxysilane (D) at lower amounts in the claiemd RTV sealant composition to achieve essentially the same uncured, curing, and cured characteristics and properties, as at higher amounts of titanium catalyst (B) and alkoxysilane (D). The crosslinkers (D) for our RTV sealant compositions are alkoxysilanes which have at least two alkoxy groups per molecule wherein the alkoxy groups are either methoxy or ethoxy. These alkoxysilanes preferably contain three alkoxy groups per molecule, and are illustrate by methyltrimethoxysilane, methyltriethoxysilane, vinyltrimethoxysilane, vinyltriethoxysilane, ethyltrimethoxysilane, ethyltriethoxysilane and mixtures of these alkoxysilanes or their partial hydrolyzates. Preferably, the alkoxysilanes are methyltrimethoxysilane or mixtures with other alkoxysilanes wherein methyltrimethoxysilane comprises a majority of the alkoxysilanes in the mixture. Because the polymers used in the RTV compositions of this invention have at least two alkoxy groups in the alkoxy-containing silyl chain terminations, the crosslinker can also be one which has two silicon-bonded alkoxy groups per molecule, such as dimethyldimethoxysilane, methylvinyldimethoxysilane, dimethyldiethoxysilane and methylethyldiethoxysilane. The amount of alkoxysilane crosslinker is those amounts which do not take molar ratio (I) and molar ratio (II) outside the limits where molar ratio (I) is 0.9 to 5, preferably 1 to 2.5, and molar ratio (II) is 0.6 to 2, preferably 0.8 to 1. In meeting these molar ratios, the weight percentages of crosslinker is often found to be in the range of from 0.1 to 10 weight percent based on the total weight of the RTV sealant composition, more preferred from 0.1 to 3 weight percent. Increasing the amount of alkoxysilane (D) decreases the rate of development of green strength and slows the cure rate. For a preferred group of RTV sealant compositions, the use of less than 1.5 weight percent, based on the total weight of the composition exhibits desirable green strength development rates. Other ingredients which are conventionally used in RTV sealant compositions such as adhesion promoters, fungicides, colorants, pigments and plasticizers, can be added as long as they do not interfere with the rapid development of green strength, cause discoloration of the uncured composition or cured product; deteriorate the curing properties; damage the cured physical properties; or reduce the effective bonding between the cured sealant and the substrates. Where organo-functional trialkoxysilanes are used as adhesion promoters and their amounts are such that the moles of organo-functional trialkoxysilane may be significant with respect to the moles of alkoxysilane crosslinker (D), it may be desirable to include the moles of such adhesion promoter as part of the moles of alkoxysilane in determining molar ratios (I) and (II). The RTV sealant compositions of this invention when the molar ratios I and II are met, rapidly develop green strength as observed by lap shear values after 30 minutes of curing of at least 2700 pascal (Pa), with preferred lap shears of at least 5400 Pa. The time-to-rubber (TTR) is also less than 10 minutes. These RTV sealant compositions do not yellow and are less corrosive to many substrates. In the following working examples, "part" or "parts" refer to part by weight or parts by weight (expressed as "pbw") and all viscosities were measured at 25°C. Me represents methyl, t-Bu represents tertiary-butyl, and iPr represents isopropyl. INGREDIENTS OF THE EXAMPLES Polymer 1 = a mixture of polydimethylsiloxanes where one polymer had a formula and another polymer had a formula where the polymer mixture contained 20 percent of the endgroups as vinyl and g had an average value such that the viscosity was 60 Pa·s. Some small fraction of a polymer where both ends are vinyl may be present as a by-product from the preparation. Polymer 2 = a polydimethylsiloxane having the following formula where g has an average value such that the viscosity was 12.5 Pa·s. Polymer 3 = a polydimethylsiloxane having the formula where g had an average value such that the viscosity was 10 Pa·s. Polymer 4 = a polydimethylsiloxane having the formula where g had an average value such that the viscosity was 60 Pa·s. Polymer 5 = a polydimethylsiloxane having the formula (MeO) 3 SiO(Me 2 SiO) q Si(OMe) 3 where g had an average value such that the viscosity was 20 Pa·s. Polymer 6 = a polydimethylsiloxane blend of Polymer 3 and Polymer 4 having a viscosity of 20 Pa·s. Polymer 7 = a polydimethylsiloxane having the formula where q had an average value such that the viscosity was 20 Pa·s. Catalyst 1 = a mixture of titanium molecules having an average formula Ti(Ot-Bu) 3.6 (OiPr) 0.4 Catalyst 2 = Ti(OiPr) 4 Catalyst 3 = Alkoxysilane 1 = methyltrimethoxysilane Alkoxysilane 2 = dimethyldimethoxysilane Silica Filler = fumed silica filler having a surface area of 150 m 2 /g and a water content of 1.0 weight percent G. CaCO 3 = a ground calcium carbonate having an average particle size of 2-3 micrometers, surface treated with stearic acid and containing 0.1 weight percent adsorbed water ppt CaCO 3 = a precipitated calcium carbonate having a surface area of 22 m 2 /g, surface treated with stearic acid and an adsorbed water content of 0.4 weight percent GREEN STRENGTH MEASUREMENT BY LAP SHEAR Aluminum panels measuring 2.54 cm x 7.62 cm were assembled into lap shear joints with a 2.54 cm overlap. The glue line thickness was 0.254 cm. Samples were allowed to cure for 30 minutes by exposure to atmospheric conditions which were 25°C. and 50 % relative humidity and then the green strength values were obtained. The values were obtained by using an Instron™ Tensile Tester at a pull rate of 1.27 cm per minute. The results were obtained in pound per square inch (psi) which was converted to pascals. EXTRUSION RATE The extrusion rate was determined by test procedure MIL-S-8802D on the uncured RTV silicone sealant composition by extruding it through a nozzle with a 0.3175 cm orifice using 620.5 kPa pressure and measuring the amount extruded in grams per minute (g/min). TIME-TO-RUBBER (TTR) The time-to-rubber (TTR) is that time from the point of exposure of an RTV sealant composition to atmospheric conditions of 50% relative humidity and 25°C to the point where an elastic skin forms on the surface of the exposed composition. When the surface of the curing RTV sealant composition can be deformed 0.635 cm and then show elastic recovery without cracking, splitting or pulling away from the uncured composition, the surface has reached the time-to-rubber (TTR) or an elastic skin point. The TTR is reported in minutes. EXAMPLES 1-5 The RTV sealant compositions of Table I were made by mixing their ingredients under conditions to exclude moisture. The ingredients were mixed by first adding alkoxysilane and titanium catalyst to the polymer, adding filler, mixing and then drawing a vacuum to remove any by-produced alcohol. In Table I, the moles of groups and ingredients were based on 100 grams of the RTV sealant composition and appear in Table I in parenthesis below the weight parts. Molar ratios (I) and (II), as defined herein, are also shown in Table I. The prepared RTV sealant compositions were thereafter stored in containers sealed to prevent atmospheric moisture from entering. Testing was done after two days storage at 25°C. The extrusion rate in grams/minute (g/m) for each of the RTV sealant compositions was measured and are also shown Table I. The TTR and the green strength (lap shear) for each of the RTV sealant compositions were measured and these values are reported in Table I. Three lap shear panels were averaged and reported as the green strength in each of the examples in Table I. Example 4 illustrates the usefulness of diorganodialkoxysilanes as a crosslinker. Comparative Examples 2, 3 and 5 each had a molar ratio (II) of less than 0.6 and exhibit unacceptable green strengths of less than 2700 Pa and unacceptable TTR of greater than 10 minutes. Comparative Examples 2 and 3 show that even if the amount of titanium catalyst resulted in molar ratio (I) being within the acceptable range of 0.9 to 5, but was characterized by not using the titanium catalyst of this invention, the green strength values and the TTR values were not acceptable. Also, molar ratio (II) for Comparative Examples 2 and 3 were zero and unacceptable since the titanium catalysts were not of the present invention. EXAMPLES 6-10 RTV sealant compositions were prepared and tested in the same manner as Examples 1-5, the ingredients, their amounts and properties were measured and are listed in Table II. Example 6 showed the usefulness of silica per se as a filler and Example 7 showed the usefulness of ground calcium carbonate per se as a filler. Comparative Example 8 had a molar ratio (I) of less than 0.9 and also had an unacceptable extrusion rate of 5 g/min. Comparative Example 9 had a molar ratio (II) of less than 0.6, exhibited an unacceptable green strength of less than 2700 Pa and an unacceptable TTR of greater than 10 minutes. Comparative Example 10 showed that acceptable green strength values and TTR values were obtainable using a precipitated calcium carbonate alone. EXAMPLES 11-16 RTV sealant compositions were prepared and tested as described for Examples 1-5, except that the ingredients and their amounts are given in Table III. The results of this testing are also shown in Table III. Examples 1 and 11-16 illustrate that a variety of polymers with polyalkoxy-functional chain terminations resulted in RTV sealant compositions with acceptable green strength values and acceptable TTR values when molar ratio (I) had a value of 0.9 to 5 and molar ratio (II) had values of 0.6 to 2. EXAMPLES 17-19 RTV sealant compositions were prepared and tested in the same manner as Examples 1-5, the ingredients, their amounts and properties were then measured and are provided in Table IV. Examples 1 and 17-19 show that the addition of a rheology additive, an adhesion promoter or a combination of these additives provide acceptable green strength values and TTR values. EXAMPLES 20 and 21 RTV sealant compositions were prepared and tested in the same manner as Examples 1-5, the ingredients, their amounts and properties were then measured and are provided in Table V. In Table V, TES represents tetraethoxysilane. Comparative Examples 20 and 21 show that the substitution of tetraalkoxysilane for an alkyltrialkoxysilane resulted in a low value for green strength for Example 20 and produced both a low value for green strength and a long TTR value for Example 21. It was concluded that tetraalkoxysilanes were not useful in this invention. EXAMPLE INGREDIENT 1 2 3* 4 5* POLYMER 1, pbw (moles alkoxy Si end) 49.05 (0.00128) 49.35 (0.00129) 48.60 (0.00127) 48.84 (0.00127) 47.70 (0.00124) CATALYST 1, pbw (moles cat.) 1.80 (0.00529) 0.0 (0.0) 0.0 (0.0) 1.80 (0.00529) 1.80 (0.00529) CATALYST 2, pbw (moles cat.) 0.0 (0.0) 1.50 (0.00528) 0.0 (0.0) 0.0 (0.0) 0.0 (0.0) CATALYST 3, pbw (moles cat.) 0.0 (0.0) 0.0 (0.0) 2.25 (0.00531) 0.0 (0.0) 0.0 (0.0) ALKOXYSILANE 1, pbw (moles silane) 0.65 (0.00478) 0.65 (0.00478) 0.65 (0.00478) 0.0 (0.0) 2.0 (0.01470) ALKOXYSILANE 2, pbw (moles silane) 0.0 (0.0) 0.0 (0.0) 0.0 (0.0) 0.86 (0.00717) 0.0 (0.0) SILICA FILLER, pbw (moles OH) 3.5 (0.00385) 3.5 (0.00385) 3.5 (0.00385) 3.5 (0.00385) 3.5 (0.00385) G. CaCO3, pbw (moles OH) 45.0 (0.005) 45.0 (0.005) 45.0 (0.005) 45.0 (0.005) 45.0 (0.005) MOLAR RATIO (I) 1.14 1.14** 1.14 1.41 2.26 MOLAR RATIO (II) 0.87 0.00 0.00 0.63 0.33 EXTRUSION RATE (g/min) 54 25 55 40 40 GREEN STRENGTH, Pa 5516 689 689 4137 1379 TTR, minutes 4 12 30 5 20 EXAMPLE INGREDIENT 1 17 18 19 POLYMER 1, pbw (moles alkoxy Si end) 49.05 (0.00128) 48.55 (0.00127) 48.55 (0.00127) 48.05 (0.00125) CATALYST 1, pbw (moles cat.) 1.80 (0.00529) 1.80 (0.00529) 1.80 (0.00529) 1.80 (0.00529) ALKOXYSILANE 1, pbw (moles silane) 0.65 (0.00478) 0.65 (0.00478) 0.65 (0.00478) 0.65 (0.00478) SILICA FILLER, pbw (moles OH) 3.5 (0.00385) 3.5 (0.00385) 3.5 (0.00385) 3.5 (0.00385) G. CaCO3, pbw (moles OH) 45.0 (0.005) 45.0 (0.005) 45.0 (0.005) 45.0 (0.005) ppt. CaCO3, pbw (moles OH) 0.0 (0.0) 0.0 (0.0) 0.0 (0.0) 0.0 (0.0) RHEOLOGY ADDITIVE, pbw 0.0 0.5 0.0 0.5 ADHESION PROMOTER, pbw 0.0 0.0 0.5 0.5 MOLAR RATIO (I) 1.14 1.14 1.14 1.14 MOLAR RATIO (II) 0.87 0.88 0.88 0.88 EXTRUSION RATE (g/min) 54 56 66 57 GREEN STRENGTH, Pa 5516 6895 4137 4137 TTR, minutes 4 4 5 7 EXAMPLE INGREDIENT 1 20* 21 POLYMER 1, pbw (moles alkoxy Si end) 49.05 (0.00128) 48.70 (0.00127) 48.40 (0.00126) CATALYST 1, pbw (moles cat.) 1.80 (0.00529) 1.80 (0.00529) 1.80 (0.00529) TES, pbw (moles silane) 0.65 (0.00478) 1.00 (0.00481) 1.30 (0.00625) SILICA FILLER, pbw (moles OH) 3.5 (0.00385) 3.5 (0.00385) 3.5 (0.00385) G. CaCO3, pbw (moles OH) 45.0 (0.005) 45.0 (0.005) 45.0 (0.005) MOLAR RATIO (I) 1.14 1.14 1.30 MOLAR RATIO (II) 0.87 0.87 0.70 EXTRUSION RATE (g/min) 54 41 65 GREEN STRENGTH, Pa 5516 1379 689 TTR, minutes 4 7 21

Claims: A composition comprising the product obtainable by mixing (A) a polymer which contains per molecule an average of at least 1.2 (RO) (3-x) R 1 x Si- chain terminations where each R is methyl or ethyl, each R 1 is methyl, ethyl, or vinyl, and x has an average value of from 0 to 1 inclusive; (B) a titanium catalyst of the average formula Ti(OR 2 ) (4-y) (OR 3 ) y where each R 2 is selected from a monovalent tertiary aliphatic hydrocarbon radical, each R 3 is a monovalent linear aliphatic hydrocarbon radical having from 1 to 6 carbon atoms inclusive per radical, y has an average value of from 0 to 1 inclusive; (C) a filler having a hydroxyl group content derived from hydroxyl groups selected from the group consisting of covalent-bonded hydroxyl radicals, adsorbed water, or both the covalent-bonded hydroxyl radicals and the adsorbed water; and (D) an alkoxysilane of the average formula R 4 z Si(OR 5 ) (4-z) in which each R 4 is methyl, ethyl or vinyl, each R 5 is methyl or ethyl, and z has an average value of from 1 to 2 inclusive, where each of ingredients (A), (B), (C), and (D) are present in amounts such that a molar ratio (I) is 0.9 to 5 and a molar ratio (II) is 0.6 to 2, where molar ratio (I) = moles of titanium catalyst (B) + moles of alkoxysilane (D) moles of hydroxyl group in (C) and molar ratio (II) = moles of titanium catalyst (B) moles of alkoxysilane (D) + moles of silicon-bonded alkoxy unit chain terminations in (A). The composition according to claim 1 in which R 2 is tertiary-butyl and R 3 is isopropyl. The composition according to claim 1 in which the polymer of (A) is a polydiorganosiloxane of the general average formula where R is methyl or ethyl; R 9 is methyl, ethyl, or phenyl; R 19 is methyl or ethyl; g has an average value of 2 to 3 inclusive; f is at least 200; and Z is a divalent hydrocarbon radical free of aliphatic unsaturation of 2 to 18 carbon atoms or a divalent group of the general average formula where R 19 is defined above, G is a divalent hydrocarbon radical free of aliphatic unsaturation of 2 to 18 carbon atoms, and c has an average value from 1 to 6 inclusive. The composition according to claim 1 in which the polymer of (A) is a polydiorganosiloxane of the general average formula or a mixture of the polydiorganosiloxane of formula (I) and polydiorganosiloxanes of the following general average formula in which R is methyl or ethyl, R 2 is methyl, ethyl, or vinyl; R 9 is an alkyl radical of 1 to 6 inclusive carbon atoms, phenyl, or a fluorinated alkyl radical; g has an average value of 2 to 3 inclusive, f has an average value of at least 200. The composition according to claims 3 or 4 in which R is methyl, R 9 is methyl, and (D) is methyltrimethoxysilane. The composition according to claim 5 in which Z is ethylene, R is methyl or ethyl, R 9 is methyl, R 19 is methyl, and g has an average value of 2 or 3. The composition according to claim 1 in which (C) is a reinforcing silica filler. The composition according to claim 1 in which (C) is calcium carbonate. The composition according to claim 1 in which (C) is a combination of reinforcing silica filler and ground calcium carbonate.

Inventors: PALMER RICHARD ALAN, PALMER, RICHARD ALAN
Applicants: DOW CORNING, DOW CORNING CORPORATION
Application year: 1998
Main classification: C08L83
IPC codes: C08L83, C08K5, C09K3