Aqueous emulsion composition

Abstract: Disclosed is an aqueous emulsion composition comprising, as the dispersoid, a (co)polymer that comprises at least one monomer unit selected from ethylenic unsaturated monomers and dienic monomers, and, as the dispersant, (A) a polyvinyl alcohol polymer, and containing (B) a condensate of an alkali metal salt of an aromatic sulfonic acid with formaldehyde in a ratio, (A)/(B), of from 100/0.05 to 100/100 in terms of the solid content of the two. The composition is characterized by its fluidity of such that the apparent viscosity of the composition is prevented from being lowered relative to the increase in the shear rate of the composition and that the apparent viscosity of the composition is increased relative to the increase in the shear rate thereof. In addition, the composition is further characterized by its high initial adhesiveness and its viscosity-increasing ability.

Description: BACKGROUND OF THE INVENTION The present invention relates to an aqueous emulsion composition, an adhesive, and a method for thickening an aqueous emulsion. An aqueous emulsion comprising, as the dispersant, a polyvinyl alcohol polymer (hereinafter referred to as PVA polymer) has extremely high mechanical stability, chemical stability and miscibility with pigment, as the PVA polymer therein well acts as protective colloid. In addition, films formed from such an aqueous emulsion are extremely stiff. For many years, an aqueous emulsion of this type has had many applications in various fields of coating compositions, adhesives, fiber processing agents, and paper processing agents. Regarding its viscosity (fluidity), an aqueous emulsion comprising a PVA polymer as the dispersant is characterized by so-called shear thinning (this may be hereinafter referred to as thixotropy), which generally indicates the decrease in the apparent viscosity of a fluid with the increase in the shear rate thereof. In the practical use of such an aqueous emulsion, its shear-thinning fluidity is often preferred. Recently, however, it is desired to speed up the production line for producing products (e.g., wood bonded products, paper bonded products, and fiber products) from an aqueous emulsion comprising a PVA polymer as the dispersant, for example, by accelerating the speed of roll rotation in the line, to thereby increase the producibility therein. In this situation, conventional, shear-thinning aqueous emulsion is problematic in that the amount to be applied to rolls is difficult to control and that the emulsion having been applied to the rolls scatters around them. In order to solve these problems, an aqueous emulsion is often processed into a Newtonian one of which the apparent viscosity does not depend on its shear rate, or into a shear-thickening one of which the apparent viscosity increases with the increase in its shear rate (the latter may be hereinafter referred to as dilatant fluid). To convert a thixotropic, aqueous emulsion comprising a PVA polymer as the dispersant into a likely Newtonian one, for example, the emulsion polymerization method for producing the emulsion may be improved by controlling the amount of the initiator to be used and that of the dispersant, or the type of the PVA polymer to be used as the dispersant may be specifically defined with respect to the degree of hydrolysis and the molecular weight. Where such a Newtonian, aqueous emulsion is desired to be further converted into a dilatant one, it is generally difficult to convert the fluidity of the emulsion by merely improving the emulsion polymerization method or specifically defining the type of the PVA polymer to be used as the dispersant in the manner as above while the dispersion stability of the aqueous emulsion is still kept stable. It has, therefore, been suggested to employ a method of adding to an aqueous emulsion comprising a thixotropic PVA polymer as the dispersant, a gelling agent for the PVA polymer in the step of post-processing the emulsion to thereby convert the thixotropic emulsion into a dilatant one. However, this method is problematic in that the gelling agent used therein would not be safe and would unfavorably color the emulsion, and the use of the emulsion produced in the method will be limited. Japanese Patent Application Laid-Open (JP-A) No. Hei-6-211911 discloses an aqueous copolymer emulsion for processing paper, which is obtained by emulsion polymerization using a naphthalenesulfonate-formaldehyde condensate and a polyoxyethylene alkylphenyl ether sulfate, and is characterized by its high-speed coatability. The inventors of this laid-open patent application say that PVA may be optionally added to the emulsion, but say nothing about the meaning of the combination of PVA and the naphthalenesulfonate-formaldehyde condensate, about the compositional ratio of the two in the emulsion, and even about the amount of PVA to be larger than that of the condensate in the emulsion. SUMMARY OF INVENTION Given that situation, the first aim of the present invention is to provide an aqueous emulsion composition which is free from the problems noted above and of which the apparent viscosity relative to its shear rate is prevented from being lowered or is increased. A second aim of the invention is to provide an adhesive comprising the aqueous emulsion composition, which has excellent initial adhesiveness. A third aim of the invention is to provide a method for thickening an aqueous emulsion. The first aim is attained by providing an aqueous emulsion composition comprising: a dispersoid which is a (co)polymer of vinyl ester and at least one monomer selected from ethylenic unsaturated monomers and dienic monomers, and wherein the ethylenic unsaturated monomers and dienic monomers are selected from olefins, vinyl esters, acrylic acid, methacrylic acid, acrylates, methacrylates, acrylamide-type monomers, styrenic monomers, N-vinylpyrrolidone, butadiene and isoprene; a polyvinyl alcohol (co)polymer dispersant (A), and a condensate (B) of an alkali metal salt of an aromatic sulfonic acid with formaldehyde, wherein the weight ratio of the solid content of (A)/(B) is 100/0.05 to 100/100. The second aim is attained by providing an adhesive comprising the aqueous emulsion composition noted above. The third aim is attained by providing a method for thickening an aqueous emulsion comprising: a dispersoid which is a (co)polymer of vinyl ester and at least one monomer selected from ethylenic unsaturated monomers and dienic monomers, and wherein the ethylenic unsaturated monomers and dienic monomers are selected from olefins, vinyl esters, acrylic acid, methacrylic acid, acrylates, methacrylates, acrylamide-type monomers, styrenic monomers, N-vinylpyrrolidone, butadiene and isoprene; and a polyvinyl alcohol (co)polymer dispersant (A); by adding to the emulsion a condensate (B) of an alkali metal salt of an aromatic sulfonic acid with formaldehyde; wherein the weight ratio of the solid content of (A)/(B) is 100/0.05 to 100/100. DESCRIPTION OF PREFERRED EMBODIMENTS OF THE INVENTION The aqueous emulsion composition of the invention comprises, as the dispersoid, a (co)polymer that comprises vinyl ester and at least one monomer selected from ethylenic unsaturated monomers and dienic monomers. The ethylenic unsaturated monomers and dienic monomers, used in forming the dispersoid, are selected from olefins such as ethylene, propylene, and isobutylene; vinyl esters such as vinyl formate, vinyl acetate, vinyl propionate, and vinyl versatate; acrylic acid, methacrylic acid; acrylates such as methyl acrylate, ethyl acrylate, butyl acrylate, 2-ethylhexyl acrylate, dodecyl acrylate, and 2-hydroxyethyl acrylate; methacrylates such as methyl methacrylate, ethyl methacrylate, butyl methacrylate, 2-ethylhexyl methacrylate, dodecyl methacrylate, and 2-hydroxyethyl methacrylate; acrylamide-type monomers such as acrylamide, methacrylamide, N-methylolacrylamide, N,N-dimethylacrylamide, acrylamido-2-methylpropanesulfonic acid and its sodium salt; styrenic monomers such as styrene, α-methylstyrene, p-styrenesulfonic acid and its sodium and potassium salts; N-vinylpyrrolidone; butadiene and isoprene. Those monomers may be used either singly or as combined. As preferred examples of (co)polymers comprising at least one of those monomers for use in the invention, mentioned are vinyl ester-based (co)polymers such as typically ethylene-vinyl acetate copolymer and polyvinyl acetate, as well as (meth)acrylate-based (co)polymers, and styrene-diene-based copolymers. (A) The aqueous emulsion composition of the invention comprises a PVA polymer as the dispersant. Any type of PVA polymer is of use in the dispersant. In general, however, used is a PVA polymer to be prepared by polymerizing a vinyl ester monomer such as typically vinyl acetate followed by hydrolyzing the resulting polymer.Other than vinyl acetate, the vinyl ester monomer may include vinyl formate, vinyl propionate, vinyl versatate, or vinyl pivalate.The dispersant, PVA polymer (A) that constitutes the aqueous emulsion composition of the invention may also be a copolymer which is prepared by copolymerizing a vinyl ester monomer and a comonomer capable for copolymerizing with the monomer, so far as the comonomer does not interfere with the effect of the invention. The comonomer includes, for example, olefins such as ethylene, propylene, 1-butene, and isobutene; acrylic acid and its esters such as methyl acrylate, ethyl acrylate, n-propyl acrylate, i-propyl acrylate, n-butyl acrylate, t-butyl acrylate, 2-ethylhexyl acrylate, dodecyl acrylate, and octadecyl acrylate; methacrylic acid and its esters such as methyl methacrylate, ethyl methacrylate, n-propyl methacrylate, i-propyl methacrylate, n-butyl methacrylate, t-butyl methacrylate, 2-ethylhexyl methacrylate, dodecyl methacrylate, and octadecyl methacrylate; vinyl ethers such as methyl vinyl ether, n-propyl vinyl ether, i-propyl vinyl ether, n-butyl vinyl ether, i-butyl vinyl ether, t-butyl vinyl ether, dodecyl vinyl ether, and stearyl vinyl ether; nitriles such as acrylonitrile, and methacrylonitrile; halogenated vinyl compounds such as vinyl chloride, vinylidene chloride, vinyl fluoride, and vinylidene fluoride; allyl compounds such as allyl acetate, and allyl chloride; carboxyl group-containing compounds such as fumaric acid, maleic acid, itaconic acid, maleic anhydride, phthalic anhydride, trimellitic anhydride, and itaconic anhydride; esters of the above carboxyl group-containing compounds; sulfonic acid group-containing compounds such as ethylenesulfonic acid, allylsulfonic acid, methallylsulfonic acid, and 2-acrylamido-2-methylpropanesulfonic acid; vinylsilane compounds such as vinyltrimethoxysilane; isopropenyl acetate; 3-acrylamidopropyltrimethylammonium chloride; and 3-methacrylamidopropyltrimethylammonium chloride.Also employable herein are terminal-modified PVA polymers to be prepared by polymerizing a vinyl ester monomer such as vinyl acetate in the presence of a thiol compound such as thiol-acetic acid or mercaptopropionic acid followed by hydrolyzing the resulting polymer.The degree of polymerization of the dispersant, PVA polymer that constitutes the aqueous emulsion composition of the invention is not specifically defined, but is preferably between 50 and 8000, more preferably between 100 and 4000, and most preferably between 200 and 3500. Those having a degree of polymerisation of larger than 8000 are also unfavorable, since they increase the viscosity of aqueous emulsions and lower the dispersion stability thereof. The degree of hydrolysis of the PVA polymer for use in the invention is also not specifically defined, but may be generally not less than 50 mol%, preferably not less than 60 mol%, more preferably not less than 70 mol%, in view of the water-solubility of the polymer. The uppermost limit of the degree of hydrolysis may be 100 mol%, but is preferably up to 98 mol%, more preferably up to 96 mol%. (B) The condensate of an alkali metal salt of an aromatic sulfonic acid with formaldehyde, which is in the aqueous emulsion composition of the invention, may be selected from any and every type of condensates of an alkali metal salt of an aromatic sulfonic acid with formaldehyde. Generally used are sodium naphthalenesulfonate-formaldehyde condensate, sodium benzenesulfonate-formaldehyde condensate, and sodium lignosulfonate-formaldehyde condensate. The sodium naphthalenesulfonate includes sodium α-naphthalenesulfonate and sodium β-naphthalenesulfonate. Of those formaldehyde condensates, the best is sodium naphthalenesulfonate-formaldehyde condensate. The condensate for use in the invention shall be soluble or dispersible in water, while having at least two units of an alkali metal salt of an aromatic sulfonic acid in one molecule. The degree (n) of condensation of the condensate is preferably from 2 to 20, more preferably from 4 to 18, most preferably from 8 to 16. Also of use as component (B) is a condensate of an alkali metal salt of a heterocyclic sulfonic acid with formaldehyde, such as a condensate of an alkali metal melaminesulfonate with formaldehyde. In the aqueous emulsion composition of the invention, the ratio of the PVA polymer (A) to the condensate of an alkali metal salt of an aromatic sulfonic acid with formaldehyde (B). (A)/(B), must be from 100/0.05 to 100/100 in terms of the solid content of the two. If the amount of (B) to be in the composition is small, overstepping the ratio, (A)/(B) = 100/0.05, the invention could not attain the intended effect (that is, the effect of preventing the apparent viscosity of the aqueous emulsion composition, relative to the shear rate thereof, from being lowered, or of increasing the apparent viscosity of the composition). In addition, the initial adhesiveness of the adhesive comprising the composition is poor. On the other hand, if the amount of (B) is large, not reaching the ratio, (A)/(B) = 100/100, the water resistance of the film formed from the aqueous emulsion composition is poor, and, in addition, the composition will undesirably coagulate. Preferably, the ratio, (A)/(B) is from 100/0.1 to 100/80, more preferably from 100/0.2 to 100/50. The aqueous emulsion composition of the invention shall comprise, as the dispersoid, a (co)polymer comprising at least one monomer unit selected from ethylenic unsaturated monomers and dienic monomers, while containing (A) a polyvinyl alcohol polymer and (B) a condensate of an alkali metal salt of an aromatic sulfonic acid with formaldehyde in a ratio, (A)/(B), of from 100/0.05 to 100/100 in terms of the solid content of the two. Any method for producing the composition may be used. For example, to produce the composition, it is possible to employ a method of (co)polymerizing vinyl ester and at least one monomer selected from ethylenic unsaturated monomers and dienic monomers in the presence of a PVA polymer and a condensate of an alkali metal salt of an aromatic sulfonic acid with formaldehyde in any conventional manner of emulsion (co)polymerization; a method of adding a condensate of an alkali metal salt of an aromatic sulfonic acid with formaldehyde to an aqueous emulsion as previously prepared by (co)polymerizing vinyl ester and at least one monomer selected from ethylenic unsaturated monomers and dienic monomers in the presence of a PVA polymer in any conventional manner of emulsion (co)polymerization; or a method of adding a PVA polymer to an aqueous emulsion as previously prepared by (co)polymerizing vinyl ester and at least one monomer selected from ethylenic unsaturated monomers and dienic monomers in the presence of a condensate of an alkali metal salt of an aromatic sulfonic acid with formaldehyde in any conventional manner of emulsion (co)polymerization. Of those methods, preferred is the method of adding the condensate of an alkali metal salt of an aromatic sulfonic acid with formaldehyde (B) to the aqueous emulsion for thickening the emulsion. According to this thickening method, the aqueous emulsion is thickened, or that is, the viscosity of the emulsion is increased, resulting in that the coatability of the thus-thickened emulsion is improved and that the adhesiveness of an adhesive comprising the emulsion is also improved. Specifically, according to the thickening method, obtained is an aqueous emulsion composition especially useful in the field of adhesives that require increased viscosity for their coatability and adhesiveness. In the aqueous emulsion composition of the invention, the total of (A) and (B) is preferably from 1 to 50 parts by weight, more preferably from 2 to 30 parts by weight, relative to 100 parts by weight of the dispersoid, (co)polymer that comprises vinyl ester and at least one monomer selected from ethylenic unsaturated monomers and dienic monomers, in order to prevent the dispersion stability of the composition from being lowered, to prevent the viscosity of the composition from being too much increased, to prevent the water resistance of the film of the composition from being lowered, and to prevent the initial adhesiveness of the adhesive comprising the composition from being lowered. The emulsion (co)polymerization for obtaining the aqueous emulsion composition of the invention may be attained by adding the monomer(s) to the (co)polymerized, all at a time or continuously, to the emulsion (co)polymerization system. If desired, the monomer(s) to be (co)polymerized may be previously emulsified in an aqueous solution of the dispersant for emulsion (co)polymerization, and the resulting emulsion may, be added continuously to the emulsion (co)polymerization system. Any conventional initiator may be used in the emulsion (co)polymerization. For example, employable are any water-soluble initiators such as persulfates, hydrogen peroxide, tert-butyl hydroperoxide and the like, and even various azo-type or peroxide-type, oil-soluble initiators. These may be used singly or as combined with a reducing agent, such as tartaric acid, ascorbic acid, Rongalit, ferric ion or the like, in the form of a redox initiator system. The emulsion (co)polymerization temperature is not specifically defined, as varying depending on the type of the initiator used, but may be generally selected from the range between -20°C and 100° C. The aqueous emulsion composition of the invention thus prepared in the manner mentioned hereinabove is a Newtonian or dilatant fluid. The terminology "dilatancy" as referred to herein indicates that the ratio of the viscosity at 30° C of the fluid at 6 rpm to that at 60 rpm, (6 rpm)/(60 rpm), is smaller than 1, as concretely demonstrated in Examples to be mentioned hereinunder. The aqueous emulsion composition of the invention may contain, if desired, any conventional anionic, nonionic, cationic or amphoteric surfactants; water-soluble polymer compounds such as starch, modified starch, oxidized starch, sodium alginate, carboxymethyl cellulose, methyl cellulose, hydroxymethyl cellulose, maleic anhydride/isobutene copolymer, maleic anhydride/styrene copolymer, and maleic anhydride/methyl vinyl ether copolymer; and thermosetting resins such as urea/formaldehyde resin, urea/melamine/formaldehyde resin, and phenol/formaldehyde resin. Also if desired, the composition may further contain various additives , for example, fillers such as clay, kaolin, talc, calcium carbonate, or wood powder; vehicles such as wheat flour; pigments such as titanium oxide; and other various preservatives, rust inhibitors, or anti-foaming agents. The aqueous emulsion composition of the invention preferably has a solid content of from 20 to 75 % by weight. If its solid content is lower than 20 % by weight, the composition is often problematic in that it dries too quickly in practical use. However, if higher than 75 % by weight, the composition is also problematic in that its viscosity is too high and its dispersion stability is poor. The aqueous emulsion composition of the invention is favorably applicable to high-speed production lines for producing products from the composition. In addition, the composition is also favorably used in various fields of adhesives for paper (for example, for paper tubes, pastes for tobacco chips, or ordinary paper works), adhesives for wood works, fiber processing agents, coating compositions and others that require high initial adhesiveness. Now, the invention is described in more detail with reference to the following Examples and Comparative Examples, which, however, are not intended to restrict the scope of the invention. Unless otherwise specifically indicated, "parts" and "%" in Examples and Comparative Examples are by weight. The fluidity, the initial adhesiveness and the degree of thickening of the aqueous emulsion samples prepared herein were measured and evaluated according to the methods mentioned below. Evaluation of Fluidity of Aqueous Emulsion: Using a BM viscometer, the viscosity at 30°C of each sample was measured at 60 rpm and at 6 rpm, and the ratio, (viscosity at 6 rpm)/(viscosity at 60 rpm) was obtained, which indicates the fluidity of the sample. Evaluation of Initial Adhesiveness of Adhesive: Using an initial adhesiveness tester (ASM-01 Model, manufactured by Japan Tobacco Industry Co.), the initial adhesiveness of each sample was measured under the condition mentioned below. Material bonded: Two sheets of kraft paper (Olympus 95) were bonded together. Amount of sample applied: 100 g/m 2 (wet weight). Mode for measurement: Shearing. Speed for measurement: 300 mm/min. Time for which the coated sample was left: 1 sec. Bonding time: 5 sec. Bonding temperature: 20°C. Bonding pressure: 10 kg. Time for which the bonded sample was left: 1 sec. Evaluation of Degree of Thickening of Aqueous Emulsion: Using a BM viscometer, the viscosity at 30°C of each sample having a solid concentration of 45 % was measured at 6 rpm before and after thickening the sample. The ratio of the viscosity of the thickened sample to that of the non-thickened sample was obtained to be a viscosity-increasing magnification, which indicates the degree of thickening of the sample. Viscosity-increasing Magnification = (viscosity of thickened emulsion)/(viscosity of non- thickened emulsion) Example 1: 320 g of water and 20 g of polyvinyl alcohol (PVA-1, having a degree of polymerization of 1700 and a degree of hydrolysis of 88.0 mol%) were put into a 1-liter glass polymerizer equipped with a reflux condenser, a dropping funnel, a thermometer and a nitrogen blow inlet, and completely dissolved at 95°C. Next, the resulting aqueous PVA solution was cooled, and purged with nitrogen. Then, with stirring the solution at 140 rpm, 40 g of vinyl acetate was added thereto, and heated up to 60°C. Next, 10 g of an aqueous solution of 10 % tartaric acid was added to this, and an aqueous solution of 1 % hydrogen peroxide was continuously and dropwise added thereto to initiate the polymerization of the monomer. After 0.5 hours, the temperature of the reaction system was elevated up to 80°C, and 360 g of vinyl acetate was continuously and dropwise added to the system. The addition of vinyl acetate was finished in 2 hours, during which 50 g of an aqueous solution of 1 % hydrogen peroxide was continuously added thereto. Thus was obtained a polyvinyl acetate emulsion (Em-1) having a solid concentration of 52.0 % and a viscosity of 5000 mPas·s and containing PVA-1 as the dispersant. The PVA-1 content of the emulsion Em-1 was 5 % by weight relative to the solid content of the emulsion. An aqueous solution of 5 % sodium naphthalenesulfonate-formaldehyde condensate having a degree of condensation (n) of from 10 to 12 (Sanyo Levelon, manufactured by Sanyo Chemical Co.) was added to the emulsion in an amount of 5 parts by weight (as solid) relative to 100 parts by weight of PVA-1 in the emulsion, to which was added water to prepare an aqueous emulsion composition having a solid concentration of 45 %. The fluidity and the initial adhesiveness of the composition were measured and evaluated according to the methods mentioned above. The viscosity-increasing magnification of the composition was 20. Example 2: To the emulsion Em-1 of Example 1, added was an aqueous solution of 5 % sodium naphthalenesulfonate-formaldehyde condensate having a degree of condensation (n) of from 10 to 12 (Sanyo Levelon, manufactured by Sanyo Chemical Co.) in an amount of 0.5 parts by weight (as solid) relative to 100 parts by weight of PVA-1 in the emulsion, to which was added water to prepare an aqueous emulsion composition having a solid concentration of 45 %. The fluidity and the initial adhesiveness of the composition were measured and evaluated in the same manner as in Example 1. The viscosity-increasing magnification of the composition was 6. Example 3: To the emulsion Em-1 of Example 1, added was an aqueous solution of 5 % sodium naphthalenesulfonate-formaldehyde condensate having a degree of condensation (n) of from 10 to 12 (Sanyo Levelon, manufactured by Sanyo Chemical Co.) in an amount of 20 parts by weight (as solid) relative to 100 parts by weight of PVA-1 in the emulsion, to which was added water to prepare an aqueous emulsion composition having a solid concentration of 45 %. The fluidity and the initial adhesiveness of the composition were measured and evaluated in the same manner as in Example 1. The viscosity-increasing magnification of the composition was 25. Comparative Example 1: Water was added to Em-1 of Example 1 to prepare an aqueous emulsion having a solid concentration of 45 %. Its fluidity and initial adhesiveness were measured and evaluated in the same manner as in Example 1. Example 4: 14.4 g of polyvinyl alcohol (PVA-2, having a degree of polymerization of 1000 and a degree of hydrolysis of 94.2 mol%) was dissolved in 230 g of ion-exchanged water under heat, and the resulting solution was put into a pressure autoclave equipped with a nitrogen blow inlet and a thermometer. After the pH of the solution was adjusted to be 4.0 with diluted sulfuric acid added thereto, 300 g of vinyl acetate was added to the solution, and ethylene was introduced thereinto under an elevated pressure of 45 kg/cm 2 G. The amount of ethylene added was 60 g. After the temperature of the system was elevated up to 60°C, a redox initiator, hydrogen peroxide-Rongalit was added thereto to initiate the polymerization of the monomers. The polymerization was finished in 2 hours to give a poly(vinyl acetate-ethylene) copolymer emulsion (Em-2) having a solid concentration of 56.2 % and a viscosity of 2100 mPas·s and containing PVA-2 as the dispersant. The PVA-2 content of the emulsion Em-2 was 4 % by weight relative to the solid content of the emulsion. An aqueous solution of 5 % sodium naphthalenesulfonate-formaldehyde condensate having a degree of condensation (n) of from 10 to 12 (Sanyo Levelon, manufactured by Sanyo Chemical Co.) was added to the emulsion (Em-2) in an amount of 10 parts by weight (as solid) relative to 100 parts by weight of PVA-2 in the emulsion, to which was added water to prepare an aqueous emulsion composition having a solid concentration of 50 %. The fluidity and the initial adhesiveness of the composition were measured and evaluated according to the methods mentioned above. The viscosity-increasing magnification of the composition was 20. Example 5: A poly(vinyl acetate-ethylene) copolymer emulsion (Em-3) was prepared in the same manner as in Example 4, except that a solution of 14.4 g of PVA-2 and 13.0 g of sodium naphthalenesulfonate-formaldehyde condensate having a degree of condensation (n) of from 10 to 12 (Sanyo Levelon, manufactured by Sanyo Chemical Co.) as dissolved in 250 g of ion-exchanged water was used as the dispersant. The emulsion Em-3 contained 90 parts by weight of the sodium naphthalenesulfonate-formaldehyde condensate having a degree of condensation (n) of from 10 to 12, relative to 100 parts by weight of PVA-2 therein. Water was added to Em-3 to prepare an aqueous emulsion composition having a solid concentration of 50 %. The fluidity and the initial adhesiveness of the composition were measured and evaluated according to the methods mentioned above. Comparative Example 2: Water was added to Em-2 of Example 4 to prepare an aqueous emulsion having a solid concentration of 50 %. Its fluidity and initial adhesiveness were measured and evaluated in the same manner as in Example 1. Comparative Example 3: To the emulsion Em-3 of Example 5, further added was an aqueous solution of 5 % sodium naphthalenesulfonate-formaldehyde condensate having a degree of condensation (n) of from 10 to 12 (Sanyo Levelon, manufactured by Sanyo Chemical Co.) in an amount of 20 parts by weight relative to 100 parts by weight of PVA-2 in the emulsion, to which was added water to prepare an aqueous emulsion composition having a solid concentration of 50 %. The emulsion composition contained 110 parts by weight of the sodium naphthalenesulfonate-formaldehyde condensate, relative to 100 parts by weight of PVA-2 therein. The fluidity and the initial adhesiveness of the composition were measured and evaluated according to the methods mentioned above. Comparative Example 4: The same process as in Example 4 was repeated, except that 14.4 g of sodium naphthalenesulfonate-formaldehyde condensate having a degree of condensation (n) of from 10 to 12 (Sanyo Levelon, manufactured by Sanyo Chemical Co.) was used in place of PVA-2. In this, however, the system coagulated and did not give a stable aqueous emulsion. Comparative Example 5: The same process as in Example 4 was repeated, except that an aqueous solution of 5 % sodium naphthalenesulfonate-formaldehyde condensate having a degree of condensation (n) of from 10 to 12 (Sanyo Levelon, manufactured by Sanyo Chemical Co.) was added to the emulsion in an amount of 0.01 parts by weight (as solid) relative to 100 parts by weight of PVA-2 in the emulsion, in place of adding thereto the same aqueous solution in an amount of 10 parts by weight (as solid) relative to 100 parts by weight of PVA-2 in the emulsion. In this, however, a dilatant aqueous emulsion could not be obtained, and the initial adhesiveness of the emulsion obtained herein was poor. Comparative Example 6: The same process as in Example 4 was repeated, except that 7.2 g of sodium naphthalenesulfonate-formaldehyde condensate having a degree of condensation (n) of from 10 to 12 (Sanyo Levelon, manufactured by Sanyo Chemical Co.) and 7.2 g of sodium alkyldiphenyl ether disulfonate (Sandet BL, manufactured by Sanyo Chemical Co.) were used in place of PVA-2, to prepare a poly(vinyl acetate-ethylene) copolymer emulsion having a solid concentration of 55.3 % and a viscosity of 4800 mPas·s . This was tested in the same manner as in Example 4, resulting in that the emulsion obtained herein was not a dilatant one and that its initial adhesiveness was poor. Example 6: The same process as in Example 4 was repeated, except that sodium naphthalenesulfonate-formaldehyde condensate having a degree of condensation (n) of from 4 to 5 (Lomar D, manufactured by San Nopco Co.) was used in place of the sodium naphthalenesulfonate-formaldehyde condensate having a degree of condensation (n) of from 10 to 12, to obtain an aqueous emulsion. The fluidity and the initial adhesiveness of the aqueous emulsion obtained herein were measured and evaluated according to the methods mentioned above. The viscosity-increasing magnification of the aqueous emulsion was 14. As has been mentioned in detail hereinabove, the aqueous emulsion composition of the present invention is characterized by its fluidity of such that the apparent viscosity of the composition is prevented from being lowered relative to- the increase in the shear rate of the composition and that the apparent viscosity of the composition is increased relative to the increase in the shear rate thereof. In addition, the composition is further characterized by its high initial adhesiveness and its viscosity-increasing ability. Accordingly, the aqueous emulsion composition of the invention is applicable to high-speed coating with no problems, and is used widely and effectively in various fields of adhesives for paper, adhesives for wood works, fiber processing agents, paper-coating compositions, paints. While the invention has been described in detail and with reference to specific embodiments thereof, it will be apparent to one skilled in the art that various changes and modifications can be made therein without departing from the scope thereof.

Claims: An aqueous emulsion composition comprising: a dispersoid which is a (co)polymer of vinyl ester and at least one monomer selected from ethylenic unsaturated monomers and dienic monomers,and wherein the ethylenic unsaturated monomers and dienic monomers are selected from olefins, vinyl esters, acrylic acid, methacrylic acid, acrylates, methacrylates, acrylamide-type monomers, styrenic monomers, N-vinylpyrrolidone, butadiene and isoprene; a polyvinyl alcohol (co)polymer dispersant (A); and a condensate (B) of an alkali metal salt of an aromatic sulfonic acid with formaldehyde; wherein the weight ratio of the solid content of (A)/(B) is 100/0.05 to 100/100. An aqueous emulsion composition according to claim 1, wherein the condensate (B) has a degree of condensation of from 2 to 20. An aqueous emulsion composition according to claim 1, wherein the PVA is a copolymer. An aqueous emulsion composition according to any preceding claim, wherein the degree of polymerisation of the PVA is from 50 to 8000. An aqueous emulsion composition according to claim 4, wherein the degree of polymerisation is from 100 to 4000. An aqueous emulsion composition according to claim 4, wherein the degree of polymerisation is from 200 to 3500. An aqueous emulsion composition according to any preceding claim, wherein the ratio (A)/(B) is from 100/0.1 to 100/80. An aqueous emulsion composition according to claim 7, wherein the ratio (A)/(B) is from 100/0.2 to 100/50. An adhesive comprising an aqueous emulsion composition of claim 1. A method for thickening an aqueous emulsion comprising: a dispersoid which is a (co)polymer of vinyl ester and at least one monomer selected from ethylenic unsaturated monomers and dienic monomers, and wherein the ethylenic unsaturated monomers and dienic monomers are selected from olefins, vinyl esters, acrylic acid, methacrylic acid, acrylates, methacrylates, acrylamide-type monomers, styrenic monomers, N-vinylpyrrolidone, butadiene and isoprene; and a polyvinyl alcohol (co)polymer dispersant (A); by adding to the emulsion a condensate (B) of an alkali metal salt of an aromatic sulfonic acid with formaldehyde; wherein the weight ratio of the solid content of (A)/(B) is 100/0.05 to 100/100. An aqueous emulsion composition comprising: a dispersoid which is a (co)polymer of vinyl ester and at least one monomer selected from ethylenic unsaturated monomers and dienic monomers,and wherein the ethylenic unsaturated monomers and dienic monomers are selected from olefins, vinyl esters, acrylic acid, methacrylic acid, acrylates, methacrylates, acrylamide-type monomers, styrenic monomers, N-vinylpyrrolidone, butadiene and isoprene; and a polyvinyl alcohol (co)polymer dispersant (A); and a condensate (B) of an alkali metal salt of a heterocyclic sulfonic acid with formaldehyde; wherein the weight ratio of the solid content of (A)/(B) is 100/0.05 to 100/100.

Inventors: NAKAMAE MASATO, NAKAMAE, MASATO
Applicants: KURARAY CO, KURARAY CO., LTD.
Application year: 1998
Main classification: C08J3
IPC codes: C08L33, C08L31, C09J131, C08F2, C08L61, C08J3