SOFT TRANSPARENT POLYETHYLENE RESIN SHEET

Abstract: Polyethylene type soft transparent resin sheet according to the present invention includes a layer made of polyethylene type resin and has following characteristics: (a) tensile modulus of 20 to 1000MPa; (b) number of foreign substance having refractivity different from amorphous resin composition occupying major part of volume fraction of the sheet at any cross section of the sheet being less than or the same as 500 /mm 2 and average length of the foreign substance being less than or the same as 10 µm; and (c) surface roughness Ra of at least one surface being less than or the same as 0.2µm. The polyethylene type resin is a copolymer of ethylene and polar group substituted ethylene such as ethylene-vinyl acetate copolymer ethylene-ethylacrylate copolymer and so on.

Description: Technical Field The present invention relates to a polyethylene type soft transparent resin sheet and producing method thereof. Background Art Conventionally, polyvinyl chloride sheet has been widely used as a resin sheet (or film) having flexibility, heat-resistance, and superior strength. However, the polyvinyl chloride sheet can cause bleedout of toxic plasticizing agent or monomer during its use and can generate hydrogen chloride when it is burned, which results in environmental problem. In order to solve the above problems, a sheet having a base of low-stereoregular polypropylene (Japanese Patent Publication No. Hei 7-119290, Japanese Patent Laid-Open Publication No. Hei 7-171849 etc.) and a sheet having a base of amorphous polyolefin (Japanese Patent Laid-Open Publication No. Hei 5-77371, Japanese Patent Laid-Open Publication No. Hei 6-218892 etc.) and the like have been proposed. Such sheets are ordinarily produced by a tubular film process, an extrusion process, polishing roller process and the like. However, the sheet having base of low-stereoregular polypropylene does not have as much transparency, glossiness, heat-resistance and stiffness as the polyvinyl chloride sheet. On the other hand, moldings of the sheet having base of amorphous polyolefin produced by either one of tubular film process and T-die extrusion process are superior in low temperature heat sealability and brittle temperature and sometimes have mechanical characteristic such as rigidity and strength close to the polyvinyl chloride sheet. However, transparency such as gloss and haze comparable to the polyvinyl chloride has not been obtained yet. EP-A-0838321 is prior art under Article 54(3) EPC. It discloses a polyethylene soft transparent resin sheet including a polyethylene type resin, and which has characteristics (a) to (c) as defined in claim 1 and claim 3. EP-A-0803340 is prior art under Article 54(3) EPC. It discloses a method for producing a thermoplastic resin sheet, and apparatus for use in such a method, the apparatus comprising a metallic endless belt wound on and between a first cooling roller and a second cooling roller, and a third cooling roller which contacts the first cooling roller through a molten thermoplastic resin sheet and the metallic endless belt. GB-A-1417970 discloses a polyethylene type soft transparent resin sheet having a substantial absence of spherulites. The sheet is formed using apparatus comprising a metal chill roll and a rubber-surfaced roll which together form a nip through which a molten resin is to be passed. JP-A-08156073 discloses the preparation of a thermoplastic resin film by cooling molten resin by passing between a casting drum and a flexible metal endless belt. US 4.954.391 discloses a polyethylene soft transparent resin sheet including a polyethylene type resin, and which has characteristics (a) and (c) as defined in claims 1 and 3. Disclosure of the Invention The polyethylene type soft transparent resin sheet according to the present invention includes a layer made of an amorphous polyethylene type resin, and has following characteristics (a to c): (a) Tensile modulus of 20 to 1000MPa When the tensile modulus is smaller than 20MPa, the sheet is practically less valuable since the stiffness of the sheet is too weak. On the other hand, when the tensile modulus exceeds 1000MPa, the sheet gets hard and the handling ability is deteriorated, thereby being unsuitable for aimed purpose. Preferably, the tensile modulus is 100 to 800 MPa, more preferably 100 to 600MPa. (b) Number of foreign substance having refractivity different from amorphous resin composition which occupies major part of volume fraction of the sheet being less than or the same as 500 /mm 2 at any cross section of the sheet and average length of the foreign substance being less than or the same as 10 µm One of major factors for impairing transparency of the sheet is that incident light is dispersed by the foreign substance. By controlling the number of the foreign substance to be less than or the same as 500/mm 2 and average length of the foreign substance to be less than or the same as 10µm, the deterioration of the transparency of the sheet can be prevented.The direction of the cross section is optional and any one of perpendicular cross section and horizontal cross section relative to front surface and back surface of the sheet can be used.The average length refers to mean value of longest and shortest length of any cross section of the foreign substance, i.e. a diameter when the foreign substance is a sphere, for instance.The body of the foreign substance is, for instance, crystalline phase included in the same resin as the aforementioned the amorphous resin composition, a resin different from the aforementioned amorphous resin phase, and organic substance other than the resins, or inorganic substances (calcium carbonate, talc etc.). (c) Surface roughness Ra of at least one surface being less than or the same as 0.2µm. One of major factors for impairing the transparency of the sheet other than the dispersion by the foreign substance is reflection of the incident light by the surface of the sheet. In other words, when the surface of the sheet has concave and convex, the light is more likely to be reflected in relation to incident angle of the light, thereby causing so-called irregular reflection. Further, the concave and convex on the sheet surface exerts large influence on quality of glossiness. When the surface roughness quantitatively expressed by the center line average roughness Ra is less than 0.2µm, the irregular reflection and deterioration in glossiness can be prevented since the concave and convex on the sheet surface is largely decreased. More preferably, Ra is less than 0.05µm. The above "soft" word means that the Tensile modulus of the sheet is less than or the same as 1000MPa. Preferably, the Tensile modulus is less than or the same as 800MPa, more preferably less than or the same as 600MPa. Any layer structure can be adopted for the polyethylene type soft transparent resin sheet. For instance, single-layered structure or multi-layered structure including a layer made of other types of resin can be used. When the sheet has a multi-layered structure, the content ratio of the polyethylene type resin is preferably more than or the same as 50wt%. The multi-layered structure can be made of, for instance, co-extrusion. The sheet according to the present invention includes a relatively thin film. The polyethylene type soft transparent resin sheet of the present invention is harmless to the environment since the generation of toxic gas caused in the case of vinyl chloride can be eliminated. Further, since the resin sheet is made of soft polyethylene type resin, optical characteristics such as transparency, haze and gloss can be improved as well as mechanical strength. The polyethylene type resin is either a copolymer of ethylene and polar group-substituted ethylene or an acrylic thermoplastic elastomer. Specific example of the copolymer of ethylene and polar group- substituted ethylene is at least one selected from the group consisting of ethylene-vinyl acetate copolymer (EVA), ethylene-ethylacrylate copolymer (EEA), ethylene-acrylic acid copolymer (EAA), ethylene-methacrylic acid copolymer (EMAA), ethylene methyl acrylate copolymer (EMA), metal ion crosslinking body of ethylene-methacrylic acid copolymer (EMAA) and metal ion crosslinking body of ethylene-acrylic acid copolymer (EAA). Selected specific resin type and number or the composition ratio thereof can be optionally chosen among the above resin type. A method of producing the polyethylene type-soft transparent resin sheet of the present invention utilises production equipment including a cooling roller and a metal endless member abutting the cooling roller through the resin sheet, the production equipment further having an elastic member opposite to a side of the metal endless member to which the resin sheet is introduced between the cooling roller and the metal endless member to be cooled. The producing method is characterized in having the steps of: introducing the molten polyethylene type soft transparent resin sheet according to the first aspect of the present invention between the cooling roller and the metal endless member so that the resin sheet approximately simultaneously touches the metal endless member and the cooling roller; and sheet-pressing and cooling the soft transparent resin sheet while elastically deforming the elastic member. The molten resin sheet is, for instance, a resin sheet immediately after being extruded from the die of the extruder. Fluorine type rubber, silicone type rubber, EPDM etc. can be used as the material of the elastic member. The thickness of the elastic member is preferably more than or the same as 3mm for obtaining sufficient areal-pressure by elastic deformation. The metal endless member and a surface of the roller touching the resin sheet preferably have mirror-finished surface, which has, for instance, surface roughness of less than or the same as 0.5S. Stainless steel, carbon steel, titanium alloy etc. can be used as a material of the endless member. Though the endless member is of any thickness, a thickness of more than or the same as 0.3mm is preferable in view of strength. Since the resin sheet is sheet-pressed and cooled accompanying elastic deformation of the elastic member, the efficiency of cooling and mirror-finished surface transferring can be improved. Further, pressing and cooling of the resin sheet can be simultaneously conducted by introducing the resin sheet between the cooling roller and the metal endless member so that the resin sheet approximately simultaneously touches the cooling roller and the metal endless belt touching the cooling roller, thereby improving the transparency of the resin sheet. If the resin sheet first touches the metal endless member or the cooling roller, the resin sheet starts being cooled and solidification before the mirror-finished surface is transferred to both sides of the sheet. In the present producing method, the metal endless member may be wound around at least two rollers, and the elastic member may be formed on an outer circumference of the cooling roller composing the two rollers. In other words, the metal endless member is a metal endless belt wound around the at least two rollers in the above arrangement. Incidentally, a cooling roller or a roller for tension control may be provided in the metal endless belt as well as the two rollers. In the above producing method, one metal endless member may be wound around the cooling roller to run parallel against the other metal endless member; the molten polyethylene type soft transparent resin sheet according to the present invention may be introduced between the metal endless members to approximately simultaneously touch both of the one and the other metal endless member; and the soft transparent resin sheet may be sheet-pressed and cooled while elastically deforming the elastic member. In other words, the polyethylene type soft transparent resin sheet is sandwiched and cooled by the two metal endless member in the above arrangement. The elastic member may be formed on an outer circumference of the roller and the metal endless member may be cylindrically formed on an outer circumference of the elastic member. In other words, the metal endless member is formed as an external layer of the roller in the above arrangement. A temperature of the metal endless member and the cooling roller directly touching the resin sheet is preferably from dew point to 50°C. When the temperature of the metal endless member and the roller for cooling the resin sheet is lower than dew point, water-drop spot is generated on the sheet. On the other hand, when the temperature exceeds 50°C, good transparency cannot be obtained. Preferably, the temperature is below 30°C. An areal-pressure when the resin sheet is sheet-pressed accompanying elastic deformation of the elastic member is preferably from 0.1MPa to 20.0MPa. When the areal-pressure is lowered below 0.1MPa, the efficiency for transferring mirror-finished surface and cooling is deteriorated, and when the areal-pressure exceeds 20.0MPa, tension applied to the endless belt is increased, which is not preferable in view of life span. The elastic member preferably has a hardness of less than or the same as 95 degrees (based on JIS K6301A type). When the hardness is larger than 95 degrees, resin banks are likely to be generated on account of weak elasticity when the resin sheet approximately simultaneously touches the cooling roller and the metal endless member. Preferably, the hardness is less than or the same as 70 degrees. A producing method of polyethylene type soft transparent resin sheet according to third aspect of the present invention uses a production equipment having a water tray provided with a slit for flowing cooling water, a water tank located beneath the water tray and a pair of sandwiching roller disposed in the water tank with at least a portion thereof being sunk in water. The method is characterized in having the steps of: inserting molten polyethylene type soft transparent resin sheet according to the present invention to the slit to be cooled by the cooling water; and subsequently introducing the resin sheet into the water in the water tank through a gap between the pair of sandwiching roller. The temperature of the cooling water is preferably less than or the same as 10°C. Calcium chloride may be added in the water as necessary. Annealing treatment is preferably conducted to the resin sheet obtained by the above producing method. The annealing treatment is conducted at a temperature of 80 to 130 °C, preferably at 110 to 130°C. The hardness of the sheet surface can be increased by the annealing treatment. Brief Description of Drawings Fig. 1 is a schematic view showing a production equipment used in a producing method of soft transparent resin sheet according to first embodiment of the present invention; Fig. 2 is a schematic view showing a production equipment used in a producing method of polyethylene type soft transparent resin sheet according to second embodiment of the present invention; Fig. 3 is a schematic view showing a production equipment used in a producing method of polyethylene type soft transparent resin sheet according to third embodiment of the present invention; and Fig. 4 is a schematic view showing a production equipment used in a producing method of polyethylene type soft transparent resin sheet according to fourth embodiment of the present invention. Best Mode for Carrying out the Invention [First Embodiment] A polyethylene type soft transparent resin sheet 11 according to the present invention and a method for the production thereof will be described below with reference to Figure 1. First, an arrangement of production equipment will be described. The production equipment has a T-die 12 of an extruder (not shown), a metal endless belt 15 wound between first cooling roller 13 and second cooling roller 14, third cooling roller 16 to be in contact with the first cooling roller 13 through a resin sheet 11 and the metal endless belt 15, and fourth roller 17 provided adjacent to the second cooling roller 14. The first cooling roller 13 has an elastic member 18 such as fluorine type rubber at an outer circumference thereof. The elastic member 18 has hardness less than or the same as 95 degrees (based on JIS K6301 A type) and thickness more than or the same as 3mm. The metal endless belt 15 is made of stainless steel etc. and has a mirror-finished surface having surface roughness below or the same as 0.5S. At least one of rotational shaft 19 of the first and the second cooling roller 13 and 14 is connected to a rotational driving means (not shown). The third cooling roller 16 also has a mirror face having surface roughness less than or the same as 0.5S. The cooling roller 16 contacts the first cooling roller 13 through the resin sheet 11 and the metal endless belt 15, the cooling roller holding the resin sheet 11 pressed to the cooling roller 16 side by the endless belt 15. In other words, the metal endless belt 15 and the resin sheet 11 touching the metal endless belt 15 meander winding along a part of the outer circumference of the third cooling roller 16. The fourth roller 17 guides the resin sheet 11 so that the resin sheet 11 is pressed to the second cooling roller 14 through the endless belt 15. The first and the third cooling roller 13 and 16 are provided with a temperature controlling means (not shown) such as water cooling system, for controlling the surface temperature. The temperature controlling means is not provided to the other cooling roller 14, but may also be provided thereto. Incidentally, as shown in single dotted line in Fig. 1, an upstream portion of the endless belt 15 to reach the first cooling roller 13 may be cooled in advance by further providing a cooling roller 31 before the first cooling roller 13. The cooling roller 31 also works for controlling the tension of the endless belt 15. Next, a method for producing a polyethylene type soft transparent resin sheet 11 according to the present embodiment utilizing the above production equipment will be described below. Initially, temperature of the respective cooling rollers 13, 14 and 16 is controlled so that surface temperature of the metal endless belt 15 and the third cooling roller 16 is kept less than or the same as 50°C and more than or the same as dew point. Further, pellets composed of polyethylene type resin are prepared as material of the resin sheet to be fed to the extruder. After the material of the resin sheet 11 is thrown into the extruder to be melted and kneaded, the resin sheet 11 extruded from the T-die 12 is introduced between the first and the third cooling roller 13 and 16 so that the resin sheet 11 approximately simultaneously touches the endless belt 15 touching the first cooling roller 13 and the third cooling roller 16. The resin sheet 11 is pressed by the first and the third cooling roller 13 and 16 to be cooled below or the same as 50°C. At this time, the elastic member 18 elastically deforms by a pressing force between the first and the third cooling roller 13 and 16, so that the resin sheet 11 is sheet-pressed by both of the rollers 13 and 16 at an angle 1 portion from a center of the rollers 13 and 16 where the elastic member 18 is elastically deformed. The areal-pressure at this time is 0.1MPa to 20.0 MPa. Subsequently, the resin sheet 11 is pressed to the third cooling roller 16 by the mirror-finished endless belt 15 to be cooled less than or the same as 50°C. The resin sheet 11 pressed to the cooling roller 16 by the endless belt 15 is held to the cooling roller 16 at an angle 2 from a center of the cooling roller 16 and is sheet-pressed by the endless belt 15 and the third cooling roller 16 at the holding angle 2 portion. The areal-pressure at this time is 0.01MPa to 0.5 MPa. Next, the resin sheet 11 is moved to the second roller 14 with a rotation of the endless belt 15 while being overlapped with the endless belt 15. The resin sheet 11 is pressed to the second cooling roller 14 through the endless belt 15 to be cooled to less than or the same as 50°C to be configured into the polyethylene type soft transparent resin sheet 11 according to the present embodiment. When the resin sheet 11 is pressed to the cooling roller 14 being guided by the fourth roller 17, the resin sheet 11 is sheet-pressed through the endless belt 15 at an angle 3 portion from the cooling roller 14. The areal-pressure at this time is 0.01 MPa to 0.5 MPa. Incidentally, as shown in double-dotted line in Fig. 1, the resin sheet 11 may be immediately peeled and drawn off from the endless belt 15 after being cooled by the first and the third roller 13 and 16. According to the present embodiment, since the molten resin sheet 11 made from the polyethylene type resin extruded from the T-die 12 is: sheet-pressed and cooled by the first and the third rollers 13 and 16 having elastically deforming elastic member 18 at the angle 1 portion of both rollers; sheet-pressed and cooled by the metal endless belt 15 and the third cooling roller 16 at the angle 2 portion; and sheet-pressed and cooled by the endless belt 15 and the second cooling roller 14 at the angle 3 portion of the second cooling roller 14, the obtained sheet 11 has following characteristics (a to c). (a) Tensile modulus of 20 to 1000MPa; (b) An average length of foreign substance having refractivity different from amorphous resin composition occupying major part of volume fraction being less than or the same as 10 µm, and number of the foreign substance within any cross section of the sheet surface being less than or the same as 500 /mm 2 ; and (c) Surface roughness of at least one surface being less than or the same as 0.2µm. [Second Embodiment] With reference to Figure 2, the production equipment used to produce the polyethylene type soft transparent resin sheet has a metal endless layer 20 formed on an outer circumference of the elastic member 18 of the first cooling roller 13 as a metal endless member instead of the metal endless belt 15 wound between the first cooling roller 13 and the second cooling roller 14. The molten resin sheet 11 composed of the polyethylene type resin material extruded from the T-die 12 is sheet-pressed and cooled by the first and the third rollers 13 and 16 at the angle 1 portion of the first and the third rollers 13 and 16 where the elastic member 18 elastically deforms, thereby obtaining the sheet 11 having above-mentioned characteristics (a to c). [Third Embodiment] With reference to Figure 3, the production equipment has T-die 12 of the extruder, a metal endless belt 23 wound between first cooling roller 21 and second cooling roller 22, second metal endless belt 26 wound between third cooling roller 24 and fourth cooling roller 25, fifth roller 27 provided adjacent to the fourth cooling roller 25, and two pairs of rollers 28 and 29 provided as a pressing means of the endless belts 23 and 26. The first cooling roller 21 has the elastic member 18 such as fluorine type rubber covering the surface thereof. The elastic member 18 has hardness (based on JIS K6301 A type) of less than or the same as 95 degrees and thickness of more than or the same as 3mm. The first and the second metal endless belts 23 and 26 runs parallel sandwiching the polyethylene type soft transparent resin sheet 11 between the first and the second rollers 21 and 22 and the third and the fourth rollers 24 and 25. The endless belts 23 and 26 are respectively made of stainless steel and the like and has mirror-finished surface having surface roughness of less than or the same as 0.5S. The two pairs of rollers 28 and 29 as the pressing means oppose with each other sandwiching the endless belts 23 and 26 at an approximate intermediate portion of the first and the second rollers 21 and 22 and the third and the fourth rollers 24 and 25. The upper and lower rollers 28 and 29 are spaced apart. Incidentally, the pairing respective rollers 28 and 29 may not be opposed but be shifted with each other. The fifth roller 27 guides the resin sheet 11 so that the polyethylene type soft transparent resin sheet 11 is pressed to the fourth cooling roller 25 through the second endless belt 26. The cooling rollers 21, 22, 24 and 25 has a temperature controlling means such as water cooling system (not shown) for controlling the surface temperature. Initially, the temperature of the respective rollers 21, 22, 24 and 25 are controlled so that surface temperature of the metal endless belts 23 and 26 directly touching the polyethylene type soft transparent resin sheet 11 is kept below or the same as 50°C and above or the same as dew point. The polyethylene type soft transparent resin sheet 11 extruded from the T-die 12 of the extruder is introduced between the first and the second endless belt 23 and 26 so that the resin sheet 11 approximately simultaneously touches the first metal endless belt 23 touching the first cooling roller 21 and the second metal endless belt 26 touching the third cooling roller 24, thereby pressing and cooling the polyethylene type soft transparent resin sheet 11 to less than or the same as 50 °C. At this time, the elastic member 18 is compressed and elastically deformed by a pressing force between the first and the third cooling rollers 21 and 24, so that the resin sheet 11 is sheet-pressed by the rollers 21 and 24 at the angle 1 portion from a center of the rollers 21 and 24 where the elastic member 18 is elastically deformed. Subsequently, the polyethylene type soft transparent resin sheet 11 sandwiched by the endless belts 23 and 26 is pressed and cooled to be less than or the same as 50°C by the two pairs of rollers 28 and 29 as the pressing means at a section where the endless belts 23 and 26 run parallel. The resin sheet 11 sandwiched by the endless belts 23 and 26 between the upper and the lower rollers 28 and 29 are sheet-pressed by the pressing force of the pair of rollers 28 and 29. The areal-pressure at this time is 0.01MPa to 0.5 MPa. Next, the polyethylene type soft transparent resin sheet 11 is moved to the second and the fourth cooling roller 22 and 25 by the rotation of the endless belts 23 and 26 and the resin sheet 11 is pressed to the fourth cooling roller 25 through the second endless belt 26 to be cooled to less than or the same as 50°C. The polyethylene type soft transparent resin sheet 11 pressed to the cooling roller 25 is sheet-pressed to the endless belt 26 at the angle 3 portion from the center of the cooling roller 25 being guided by the fifth roller 27. The areal-pressure at this time is 0.01MPa to 0.5 MPa. According to the present embodiment, the sheet 11 having the above-mentioned characteristics (a to c) can be obtained by the sheet-press and cooling of the sheet 11 by the rollers 21 and 24 and endless belts 23 and 26 at the angle 1 portion of the first and the third rollers 21 and 24, sheet-press and cooling of the sheet 11 by the two pairs of rollers 28 and 29 as the pressing means, and the sheet-press and cooling of the sheet 11 by the second metal endless belt 26 and the fourth cooling roller 25 at the angle 3 portion. [Fourth Embodiment] With reference to Figure 4, the equipment has T-die 12 of an extruder, a water tray 31, a water tank 32 disposed under the water tray 31, and a pair of roller 33 for sandwiching the sheet disposed in the water tank 32. Further, a guide roller 34 for guiding the resin sheet 11 is disposed inside and adjacent to the water tank 32. The water tray 31 has a slit 35 for flowing cooling water at a center thereof. The slit 35 has a length slightly wider than the width of the resin sheet 11. The pair of roller 33 is disposed so that both of the roller opposes and a gap between the rollers 33 is located under the slit 35. The rollers 33 are disposed so that approximate half of the rollers 33 sink into water 36 in the water tank 32. The polyethylene type soft transparent resin sheet 11 is manufactured using the equipment as follows. The polyethylene type soft transparent resin sheet 11 extruded from the T-die 12 of the extruder is inserted to the slit 35 and is cooled by the cooling water 36. Subsequently, the resin sheet 11 is introduced to the water 36 in the water tank 32 through the pair of sandwiching roller 33 and is drawn out of the water tank 32 through the guide roller 34. The resin sheet 11 obtained in the above first to fourth embodiment may be processed by annealing. The annealing treatment can be conducted by a heating roller or a belt wound between the heating rollers. The heating roller or the number of the heating roller may be optionally selected. Alternatively, the resin sheet 11 may be heated and the same processing may be conducted to the molten resin sheet 11 as in the first embodiment. [Reference Experiment 1] In the above first embodiment, the producing method was conducted according to following specific condition. Diameter of extruder ··· 90mm, width of T-die ··· 800mm Polyethylene type resin ··· L-LDPE (MI : 1, density : 0.920, Tensile modulus : 430MPa), MORETEC 0138H (tradename) manufactured by IDEMITSU Petrochemical Co., Ltd. Thickness of resin sheet ··· 0.2mm Material of elastic member ··· silicone type rubber, thickness ··· 12mm, hardness ··· 55 degrees. Sheet take-up speed ··· 5m/min. Surface temperature of endless belt and roller touching the sheet ·· 15°C [Experiment 2-7] The resin sheet 11 was manufactured according to the producing method of the embodiment 1 with the composition and weight ratio of the layer being changed as shown in Table 1. Other manufacturing conditions were the same as Reference Experiment 1. Experiment 2 was a single-layered sheet of ionomer. Experiment 3 was a triple-layered sheet of L-LDPE / ionomer (IO) / L-LDPE. Experiment 4 was a double-layered sheet of IO / metallocene type E-O copolymer. Experiment 5 was a single-layered sheet of ethylene-vinyl acetate copolymer (EVA). Experiment 6 was a triple-layered sheet of styrene-butadiene-methacrylic acid copolymer (SB) / metallocene type E-O copolymer / SB. Experiment 7 was a triple-layered sheet of SB / PP / SB. Experiment 8 was a double-layered sheet of SB/metallocene type E-O copolymer. Experiment 9 was a single-layered sheet of ethylene- ethylacrylate-maleic anhydride copolymer (E-EA-MAH). [Reference Experiment 10] In the second embodiment, the producing method was conducted according to following specific condition. Diameter of extruder ··· 90mm, width of T-die ··· 800mm Polyethylene type resin ··· AFFINITY PL1880 as metallocene type E-O copolymer (tradename DOW CHEMICAL company). Thickness of resin sheet ··· 0.2mm Material of elastic member ··· silicone type rubber, thickness ··· 10mm, hardness ··· 50 degrees. Linear pressure between the elastic roller and the first roller ··· 150N/cm Sheet take-up speed ··· 5m/min. Surface temperature of the roller ··· 15 °C [Experiment 11-16] The manufacturing conditions were the same as Reference Experiment 10. Experiment 11 was a triple-layered sheet of E-EA-MAH / metallocene type E-O copolymer / E-EA-MAH. Experiment 12 was a triple-layered sheet of L-LDPE / EVA / L-LDPE. Experiment 13 was a triple-layered sheet of PP / EEA / PP. Experiment 14 was a single-layered sheet of ethylene-methacrylic acid copolymer (EMAA). Experiment 15 was a double-layered sheet of L-LDPE / EVA. [Experiment 16-23] In the above third Embodiment, the composition of the layer was defined as follows. The specific producing conditions were the same as reference Experiment 1. Experiment 16 was a triple-layered sheet of PP / E-EA-MAH / PP. Experiment 17 was a triple-layered sheet of LL/EMAA/LL. Experiment 18 was a triple-layered sheet of EMAA / metallocene type E-O copolymer / EMAA. Experiment 19 was a triple-layered sheet of PP / EAA / PP. Experiment 20 was a triple-layered sheet of PP EMAA / PP. Experiment 21 was a triple-layered sheet of PP / ethylene methyl acrylate copolymer (EMA) / PP. Experiment 22 was a double-layered sheet of EMAA / metallocene type E-O copolymer. [Experiment 23] In the above fourth embodiment, the composition of the layers was defined as follows. The specific producing conditions were the same as Reference Experiment 1. The temperature of the cooling water 36 was 6°C. Experiment 23 was a single-layered sheet of EMAA. [Evaluation of Characteristics] Surface roughness (on one side of the sheet and the other side), haze (total haze / internal haze), gloss and Tensile modulus were measured on the resin sheets obtained in Experiments 1 to 23 and Comparison 1 to 3. The results are shown in Tables 1 to 4. The surface roughness was measured using an electron-beam three-dimensional roughness analyzer (ERA-4000 manufactured by ELIONIX Corp.). The haze was calculated by the following formula according to a ratio of total light transmittance (Tt) showing entirety of the beam transmitted through the sheet after irradiating the beam to the sheet and diffused light transmittance (Td) showing light beam diffused and transmitted through the sheet using a haze measuring machine (for instance, NDH-300A manufactured by NIPPON DENSHOKKU KOGYO Co., Ltd). The total light transmittance (Tt) is a sum of parallel light transmittance (Tp) transmitting coaxially with the irradiated light and the diffused light transmittance (Td). Haze (H) = Td / Tt × 100 The total haze was calculated by Td and Tt obtained in irradiating light beam to the sheet. The internal haze was measured after coating silicone oil on both sides of the sheet and sandwiching the sheet with glass plates to eliminate the influence by the outside of the sheet. Total haze = internal haze + external haze The gloss was obtained as follows by measuring a reflected light flux ϕs after irradiating light beam to the sheet at an entry angle of 60 degrees and receiving the light beam at the same 60 degrees using an automatic colorimetric color-difference meter (AUD-CH-2Type-45, 60 manufactured by SUGA SHIKENKI Co., Ltd, for example) according to a ratio against a reflected light flux ϕos from a glass surface having refractivity 1,567. Gloss (Gs) = (ϕs / ϕos) × 100 The Tensile modulus was measured based on JIS K-7113. Layer Composition and Weight Ratio (wt%) Embodiment Thickness (µm) Reference Experiment 1 L-LDPE First 200 Experiment 2 IO First 300 Experiment 3 LDPE(33)/IO/LDPE(33) First 200 Experiment 4 IO(10)/E-O First 250 Experiment 5 EVA First 200 Experiment 6 SB(10)/E-O/SB(10) First 300 Experiment 7 SB(10)/PP/SB(10) First 300 Experiment 8 SB(10)/E-O First 300 Experiment 9 E-EA-MAH First 200 Reference Experiment 10 E-O Second 200 Experiment 11 E-EA-MAH(10)/E-O/E-EA-MAH(10) Second 200 Experiment 12 LL(10)/EVA/LL(10) Second 200 Experiment 13 PP(10)/EEA/PP(10) Second 300 Experiment 14 EMAA Second 200 Experiment 15 LL(10)/EVA Second 200 Experiment 16 PP(10)/E-EA-MAH/PP(10) Third 200 Experiment 17 LL(10)/EMAA/LL(10) Third 250 Experiment 18 EMAA(10)/E-O/EMAA(10) Third 150 Experiment 19 PP(10)/EAA/PP(10) Third 200 Experiment 20 PP(10)/EMAA/PP(10) Third 300 Experiment 21 PP(10)/EMA/PP(10) Third 200 Experiment 22 EMAA(10)/E-O Third 150 Experiment 23 EMAA Fourth 200 Surface Roughness (Ra) Total haze Internal Haze Gloss Tensile modulus (MPa) One Side The Other Side Reference Experiment1 0.036 0.028 5.0 3.0 120 200 Experiment 2 0.033 0.035 2.0 0.2 120 100 Experiment 3 0.031 0.034 1.7 0.17 110 300 Experiment 4 0.034 0.038 2.3 0.5 120 100 Experiment 5 0.031 0.032 1.5 0.4 110 100 Experiment 6 0.035 0.038 2.3 1.2 110 200 Experiment 7 0.039 0.031 3.0 1.3 110 500 Experiment 8 0.032 0.038 4.0 1.5 110 200 Experiment 9 0.036 0.032 2.0 0.5 120 100 Experiment 10 0.038 0.035 3.0 1.5 120 90 Experiment 11 0.033 0.031 2.0 1.0 110 200 Experiment 12 0.035 0.037 3.0 1.2 120 100 Experiment 13 0.038 0.032 3.0 1.2 110 100 Experiment 14 0.039 0.038 3.0 1.2 110 200 Experiment 15 0.037 0.032 2.0 1.3 120 100 Experiment 16 0.039 0.030 3.0 0.9 120 100 Experiment 17 0.033 0.036 2.0 1.1 110 100 Experiment 18 0.032 0.035 2.0 1.0 110 100 Experiment 19 0.033 0.039 3.0 1.1 120 300 Experiment 20 0.038 0.037 3.0 1.3 120 300 Experiment 21 0.036 0.033 4.0 1.5 120 300 Experiment 22 0.032 0.038 2.0 1.0 110 200 Experiment 23 0.034 0.033 2.0 1.0 110 200 The abbreviation and specific goods are as follows: EVA: ethylene-vinyl acetate copolymer [ULTRATHEN 630 (tradename) manufactured by TOSOH Corporation] EEA: ethylene-ethylacrylate copolymer [EVAFLEX A701 (tradename) manufactured by DU PONT-MITSUI POLYCHEMICALS CO., LTD.] EAA: ethylene-acrylic acid copolymer [PRIMACOR3300 (tradename) manufactured by DOW CHEMICAL Company] EMAA: ethylene-methacrylic acid copolymer [NUCREL N0903HC (tradename) manufactured by MITSUI DUPONT] EMA: ethylene-methyl acrylate copolymer [SP2205 (tradename) manufactured by CHEVRON] E-EA-MAH: ethylene-ethylacrylate maleic anhydride copolymer [ADTEX ET184 (tradename) manufactured by JAPAN POLYOLEFINS CO., LTD.] SB: styrene-butadiene methacrylic acid copolymer [SB polymer (tradename) manufactured by KURARAY Co., Ltd.] E-O: metallocene type ethylene-octane copolymer [AFFINITY PL1140 (tradename, Experiment 3) AFFINITY PL1880 (tradename, Experiments 10, 12, 14, 16, 19, 26, 31) manufactured by DOW CHEMICAL Company] PP: random polypropylene [F-744NP (tradename) manufactured by IDEMITSU Petrochemical Co., Ltd.] LDPE: low-density polyethylene [PETROTHEN 207 (tradename, Experiment 9), PETROTHEN 190 (tradename, Experiment 18) manufactured by TOSOH Corporation] LL: linear low-density polyethylene [MORETEC 0138H (tradename, Experiment 1), MORETEC 0168N (tradename, Experiment 2), MORETEC V-0398CN (tradename, Experiment 20, 23, 25) manufactured by IDEMITSU Petrochemical Co., Ltd.] Layer Composition and Weight Ratio (wt%) Embodiment Thickness (µm) Comparison 1 L-LDPE First 200 Comparison 2 PP(10)/E-O(80)/PP(10) First 200 Comparison 3 PP(35)/B1-PP(30)/PP(35) First 200 Surface Roughness (Ra) Total haze Internal Haze Gloss Tensile modulus (MPa) One Side The Other Side Comparison 1 0.5 0.4 15.0 6.0 80 400 Comparison 2 0.5 0.6 15.0 4.0 80 350 Comparison 3 0.5 0.7 18.0 5.0 80 300 As shown in Tables 1 and 2, since the single-layered or multi-layered molten resin sheet 11 manufactured from polyethylene type resin material extruded from an extruder was cooled and solidified by the production equipment in the Experiments 1 to 3, the obtained resin sheet 11 had the above a, b and c characteristics. Further, when the number of foreign substance (per 1mm 2 ) and average length were measured by naked eye using a phase-contrast microscope, the number remained 100 to 400/mm 2 and the average length was kept within a range of 1 to 5 µm. Accordingly, it can be observed that the resin sheet 11 of the respective Experiments had good transparency with low total haze and internal haze, and good glossiness with high gloss. Further, the resin sheet 11 had much flexibility with low Tensile modulus. On the other hand, as shown in Tables 3 and 4, though the material of Comparisons 1 to 3 were the same as each Experiments, the obtained resin sheet had surface roughness out of the range of the present invention since the resin sheet was produced by touch-roll type sheet forming method. The number of the foreign substance was less than 500/mm 2 observed by naked eye using the phase-contrast microscope, except for Comparison 1. Further, the average length of the foreign substance was 13µm in Comparison 2, and 12µm in Comparison 2. Accordingly, the resin sheet of the Comparisons was inferior in transparency with high total haze and internal haze and had bad glossiness with low gloss. Further, the resin sheet had low flexibility with high Tensile modulus. Industrial Availability The sheet obtained in the present invention can be used for packaging such as foods, medicine and clothing. The sheet can also be used for stationery goods (pen case, stationery case etc.), decorative sheet (building interior and exterior material, furniture and the like), portable bag (fashion bag, traveling article bag), agricultural greenhouse cover, table cloth, desk mat, partition, door curtain or the like.

Claims: A polyethylene-type transparent resin sheet having a layer comprising an amorphous polyethylene type resin, wherein (a) the sheet has a tensile modulus of 20 to 1000 MPa (b) the number of foreign substances having a refractivity different from the amorphous resin which occupies the major part of volume fraction of the sheet is less than or the same as 500/mm 2 at any cross-section of the sheet, and the average length of said foreign substances is less than or the same as 10 µm; and (c) at least one surface of the sheet has a surface roughness, Ra, of less than or the same as 0.2 µm, characterised in that the polyethylene type resin is a copolymer of ethylene and a polar group-substituted ethylene. The polyethylene type soft transparent resin sheet according to claim 1, wherein the copolymer of ethylene and a polar group-substituted ethylene is at least one selected from the group consisting of ethylene-vinyl acetate copolymer (EVA), ethylene-ethylacrylate copolymer (EEA), ethylene-acrylic acid copolymer (EAA), ethylene-methacrylic acid copolymer (EMAA), ethylene methyl acrylate copolymer (EMA), metal ion crosslinking body of ethylene-methacrylic acid copolymer (EMAA) and metal ion crosslinking body of ethylene-acrylic acid copolymer (EAA). A polyethylene-type transparent resin sheet having a layer comprising an amorphous polyethylene type resin, wherein (a) the sheet has a tensile modulus of 20 to 1000 MPa (b) the number of foreign substances having a refractivity different from the amorphous resin which occupies the major part of volume fraction of the sheet is less than or the same as 500/mm 2 at any cross-section of the sheet, and the average length of said foreign substances is less than or the same as 10 µm; and (c) at least one surface of the sheet has a surface roughness, Ra, of less than or the same as 0.2 µm, characterised in that the polyethylene type resin is an acrylic thermoplastic elastomer.

Inventors: FUJII ATSUSHI, FUJIWARA KENICHI, NAGAO TOMOHIRO, YUKUMOTO TOHRU, FUJII, ATSUSHI, FUJIWARA, KENICHI, NAGAO, TOMOHIRO, YUKUMOTO, TOHRU
Applicants: IDEMITSU PETROCHEMICAL CO, IDEMITSU PETROCHEMICAL CO., LTD.
Application year: 1998
Main classification: B29C47
IPC codes: C08J5, B29C47