SHRINKAGE-REDUCING AGENT FOR CEMENT COMPOSITIONS

Abstract: Shrinkage-reducing agent intended as additive in aqueous cement comprising compositions. The agent comprises at least one acetal, preferably a cyclic formal, of a tri- or polyhydric alcohol, which acetal comprises at least one 1,3-dioxa group. The acetal has preferably a water solubility of at least 1 %. The agent can, in addition to said acetal, comprise at least one amorphous silica, preferably a powderous silica. The invention refers in a further aspect to the use of said agent in said compositions. The agent is, when used, added to said composition in an amount of 0.1-20 % by weight.

Description: SHRINKAGE-REDUCING AGENT FOR CEMENT COMPOSITIONS The present invention relates to a shrinkage-reducing agent intended as additive in cement comprising compositions, such as a concrete, a hydraulic cement, a screed, a mortar or sealant composition. The agent comprises at least one acetal, preferably a cyclic formal, of a tri or polyfunctional alcohol, which acetal comprises at least one 1 ,3-dioxa group. The agent can, furthermore, comprise least one amorphous silica, such as a silicic acid. The invention refers in a further aspect to the use of said shrinkage-reducing agent in said compositions. Additives have for a long time been used to control and/or adjust the properties of mineral based compositions. These additives include porosity adj usting additives, flowability adjusting additives, curing accelerators, curing retardants and the like. The additives can work surface chemically as well as chemically and the various mechanisms involved are not yet fully characterised. Frequently used additives include for instance formaldehyde resins, such as sulphonated naphthlene- formaldehyde resins and sulphonated amino-formaldehyde resins, salts of alkali metals and alkaline earth metals, lignosulphonic acids, silica, polyalcohols, gypsum and similar additives. Shrinkage, such as dehydration shrinkage, in cement based compositions is today normally controlled by included amount of gypsum. Shrinkage give rise to cracking and other imperfections and other failures, which per se may result in cracking and/or weakened constructions. Optimised formulations, that is controlled shrinkage-reducing effect, means and implies that the ratio gypsum to dry cement must be kept within narrow limits. The risk that the shrinkage-reducing effect turns into a swelling effect increases markedly if for instance too high an amount of gypsum is added. Cement as well as gypsum are natural product and have thus a varying composition making it difficult to batchwise maintain a constant ratio between these. The composition as well as the properties of the final product will accordingly and to a rather large extent vary. The complexity of above can be illustrated by following exemplification related to initial hydration of Portland cement. The main components of Portland cement are the four clinker minerals tricalciumsilicate (3 CaO • SiO 2 ), dicalcium silicate (2 CaO • SiO 2 ) and tricalciumaluminate (3 CaO • Al 2 O 3 ) in an amount of 1 - 1 5% and tetracalciumaluminoferrite (4 CaO • Al 2 O 3 • Fe 2 O 3 ), and minor amounts of magnesium, calcium, sodium, and potassium oxide (MgO, CaO, Na 2 O, K 2 O). Gypsum (CaSO 4 ) is during milling of the clinker minerals added, normally in an amount of approximately 2-5% by weight calculated on said clinker minerals. A number of dissolution and hydration reactions occurs immediately after addition of water, which reaction not are known to their full extent and/or fully characterised. An initial heat emission emanating from reactions between tricalciumaluminate and gypsum occurs and results in deposition of ettringite (Ca 6 Al 2 [(OH) 4 SO 4 ] 3 • 26 H 2 O or 3 CaO • Al 2 O 3 • CaSO 4 ■ 32 H 2 O) on the surface of the tricalciumaluminate. The ettringite is only stable as long as unreacted gypsum is present in the composition. The ettringite reacts, when all gypsum is consumed, further with unreacted tricalciumaluminate to yield the monosulphate 3 CaO • Al 2 O 3 • CaSO 4 • 12 H 2 O. The reaction between tricalciumaluminate and water is spontaneous with heavy heat emission. Yielded metastable hydrates are then transformed into stable hydrates. Gypsum is, in order to retard these rapid and undesirable reactions, admixed. Formed ettringite gives a protective layer on the surfaces of the tricalciumaluminate. Gypsum per se also partly retards hydration of the tricalciumaluminate. Frequently used cement compositions wherein the dehydration shrinkage is controlled or adjusted by addition of gypsum also include aluminate cement having an aluminate content of 35-50% and mixtures of aluminate cement and Portland cement. The ratio added gypsum to cement is normally 1 :2 to 1 :3. Admixture of gypsum into a cement composition having a to the user unknown or poorly defined aluminate and/or gypsum content is thus a matter if delicate balancing of the ration aluminate to gypsum. The use of a shrinkage-reducing agent having a defined and invariable composition will substantially simplify admixture and reduce variations and problems as disclosed above. Efforts have been made to change the cement composition per se in order reduce problems with shrinkage. It is also from a number of patents and patent applications, such as EP 308950, EP 573036, JP 48043010, JP 59128240 and JP 59131552, made known that alcohols, such as secondary and tertiary polyalcohols, alkanediols, acetylenic diols and polyvinyl alcohol, optionally in combination with surface active fluorocompound and/or a silica, have a certain performance as shrinkage-reducing agents in cement compositions. Alcohols are, furthermore, used as milling additives, which is disclosed in German patent application no. 3245843. The present invention provides quite unexpectedly a shinkage-reducing agent having properties superior to known and used agents. The agent of the present invention is an acetal, preferably a cyclic acetal of a tri or polyhydric alcohol and it is unexpectedly shown that said acetals are superior to the alcohols from which they are yielded. The shrinkage-reducing agent according to the present invention exhibits a substantial shinkage-reduction compared to said alcohols as well as compared to a control without the agent of the invention and/or corresponding alcohol. The agent according to the present invention is intended to be used in aqueous cement comprising compositions, such as a concrete, a hydraulic cement, a mortar, a screed, a sealant composition or the like. The agent comprises at least one acetal of a tri or polyhydric alcohol in an amount of 1 -99%, such as 40-99% or 50-99% by weight. The acetal is in preferred embodiments a cyclic acetal comprising at least one 1 ,3-dioxa group, such as a formal, and having a water solubility of at least 0.2%, such as 0.5% or 1 %. Especially preferred embodiments include formals having a 1 ,3-dioxane structure, such as 1 ,3-dioxanes of trihydric alcohols which suitably are selected from the group consisting of trimethylol C j - C alkanes. Said trimethylol C ] - C 8 alkanes can be exemplified by trimethylolethane and trimethylpropane. Further suitable tri and polyhydric alcohols are found in the group consisting glycerol, diglycerol, ditrimethylolethane, ditrimethylolpropane, pentaerythritol, dipentaerythritol. The most preferred acetals are derived from tri or polyhydric alcohols having neopentyl structure. Acetals of carboxyfunctional alcohols, such as the trifunctional dimethylolpropionic acid having one carboxyl group and two hydroxyl groups, can also be included in the agent of the present invention. This kind of acetals can be exemplified by the cyclic acetal 5-ethyl- l ,3-dioxane-5-carboxylic acid yielded from reaction between dimethylolpropionic acid and formaldehyde. The acetal of the agent can also advantageously be an acetal, such as a cyclic formal, of an alkoxylated tri or polyfunctional alcohol. The alkoxylate is suitably prepared by reaction between said alcohol and an alkylene oxide, such as ethylene oxide and propylene oxide and in special cases butylene oxide or phenylethylene oxide as well as combinations of said alkylene oxides. Diacetals, triacetals tetraacetals, etc. of alcohols having four or more hydroxyl groups can also be included in embodiments of agent according to the present invention. The agent of the present invention comprises in the most preferred embodiments at least one acetal of glycerol, trimethylolethane, trimethylolpropane or pentaerythritol, such as 4-hydroxymethyl- l ,3-dioxolane, 5-hydroxy- l ,3-dioxane, 5-methyl-5-hydroxymethyl- l ,3-dioxane, 5-ethyl-5-hydroxymethyl- l ,3-dioxane or 5,5-dihydroxymethyl- l ,3-dioxane. Liquid acetals of tri or polyhydric alcohols can suitable and in accordance with the present invention be included in a powderous shrinkage-reducing agent. The agent is then produced by mixing a carrier comprising at least one powderous amorphous silica, such as a silicic acid, and said acetal. The percentage silica is suitably 1 -50%, preferably 10-40%, by weight of the mixture. Acetals are reaction products between at least one alcohol and at least one aldehyde and include cyclic acetals, such as 1 ,3-dioxolanes, 1 ,3-dioxanes and 1 ,3,5-trioxepanes. Acetal refers to an organic dialkoxycompound - Rompps Chemie-Lexikon 8. Aufl. 1981 - and cyclic acetal accordingly to a cyclic dialkoxycompound. Acetals are inter alia formed during synthesis and/or recovery of di, tri or polyhydric alcohols, for instance when water and excess aldehyde, such as formaldehyde, is evaporated. Cyclic acetals are inter alia yielded when a 1 ,3-diol group in for instance a di, tri or polyhydric alcohol of neopentyl structure reacts with for example formaldehyde (formal = formaldehyde acetal) to give corresponding 1 ,3-dioxane. Cyclic acetals can also be obtained by direct reaction between said alcohol and an aldehyde. These reactions can be exemplified by 1 ,3-dioxolane (glycol formal) obtained when a mixture comprising formaldehyde, ethylene glycol and an acid catalyst is heated and by 1 ,3,5-trioxepane, a cyclic glycol formal having two oxymethylene units, obtained when 1 ,3-dioxolane, formaldehyde and an acidic catalyst is heated. Glycerol, trimethylolalkanes and pentaerythritols form when reacted with formaldehyde cyclic acetals (cyclic formals), such as 4-hydroxy(alkyl)- l ,3-dioxolanes, 5-hydroxy-l ,3-dioxane, 5-alkyl-5-hydroxy(alkyl)- l ,3dioxanes, and 5,5-dihydroxy(alkyl)- l ,3-dioxanes. The present invention refers in a further aspect to the use of said shrinkage-reducing agent in aqueous cement comprising compositions, such as a concrete, a hydraulic cement, a mortar, a screed, a sealant composition or the like. The agent is preferably added to said composition in an amount of 0.1 -20%, such as 2-5%o, by weight calculated on dry cement included in said composition. Without further elaboration, it is believed that one skilled in the art can, using the preceding description, utilise the present invention to its fullest extent. The following preferred specific, embodiments as shown in Examples 1 -4, are, therefore, to be construed as merely illustrative and not limitative of the remainder of the disclosure in any way whatsoever. Example 1 : Preparation of an aqueous cement comprising composition according to EN 196- 1. The composition is a control without shrinkage-reducing agent. Example 2: Comparative example wherein trimethylolpropane is used as shrinkage-reducing agent. Example 3 : Addition of a shrinkage-reducing agent according to the present invention. The agent is of 5-ethyl-5-hydroxymethyl- l ,3-dioxane. Example 4: Preparation of a powderous shrinkage-reducing agent, according to the present invention, comprising 5-ethyl-5-hydroxymethyl- - 1 ,3-dioxane and an amorphous silica. EXAMPLE 1 (Reference) A cement based composition according to EN 196- 1 was prepared in a Hobart mixer. The composition comprised 225 g of water, 450 g of standard Portland cement and 1350 g of CEN sand. The cement was during 30 seconds and under stirring added to the water under stirring at speed 1 of the mixer. The sand was then during the following 30 seconds added and the stirring was at speed 2 allowed to continue for a further 150 minutes. The composition was now allowed to rest for 90 seconds and then stirred at speed 2 during 60 seconds. The total mixing/stirring time was 4 minutes. Four sample bodies were after mixing casted in moulds and used for measurement of dehydration shrinkage. The dimensions of the bodies were 250 x 25 x 25 mm. The bodies were cured in air at 20°C and 100% relative humidity and demoulded after 24 hours. An initial length value was after demoulding measured. The sample bodies was then stored at 20°C and 50% relative humidity. Measurement of the length was performed 21 and 49 days after the initial measurement. Recorded dehydration shrinkage is given in Table (I) below. EXAMPLE 2 (Comparative) A composition in accordance with Example 1 was prepared using trimethylolpropane (TMP) as shrikage-reducing agent. The shrinkage-reducing agent was added to the water in an amount corresponding to 1 % and 3% by weight calculated on the cement. Casting of sample bodies, storage and length measurement was carried out in accordance with Example 1. Recorded dehydration shrinkage is given in Table (II) below. EXAMPLE 3 A composition in accordance with Example 1 was prepared using 5-ethyl-5-hydroxymethyl- l ,3-dioxane as shrikage-reducing agent in accordance with the present invention. The shrinkage-reducing agent was added to the water in an amount corresponding to 3%> by weight calculated on the cement. Casting of sample bodies, storage and length measurement was carried out in accordance with Example 1 with the difference that length measurements were performed after 21 and 70 days instead of 21 and 49 days. Recorded dehydration shrinkage is given in Table (III) below. EXAMPLE 4 A powderous shrinkage-reducing agent was prepared by mixing 70% by weight of 5-ethyl-5-hydroxymethyl- l ,3-dioxane and 30% by weight of an amorphous silicic acid. A composition in accordance with Example 1 was prepared using above shrinkage agent as shrikage-reducing agent. The shrinkage-reducing agent was added in an amount corresponding to 3% by weight of 5-ethyl-5-hydroxymethyl-l ,3-dioxane calculated on the cement. Casting of sample bodies, storage and length measurement was carried out in accordance with Example 3. Recorded dehydration shrinkage corresponds with results given in Table (III).

Claims: CLAIMS 1. Shrinkage-reducing agent, which agent reduces shrinkage such as dehydration skrinkage, in an aqueous cement comprising composition ch a racte ris ed i n, that the agent comprises at least one acetal, preferably at least one cyclic acetal, of at least one tri or polyhydric alcohol, which acetal comprises at least one 1,3-dioxa group. 2. Shrinkage-reducing agent according to Claim 1 ch a racte ris ed in, that the acetal is a formal having a water solubility of at least 0.5%. 3. Shrinkage-reducing agent according to Claim 1 or 2 ch a racteris ed in, that the acetal is a 1,3-dioxolane or 1,3-dioxane of a trihydric alcohol. 4. Shrinkage-reducing agent according to Claim 1 or 2 ch a racte ris ed i n, that the acetal is a 1,3-dioxolane or 1,3-dioxane of an alkoxylated trihydric alcohol. 5. Shrinkage-reducing agent according to Claim 4 ch a racte ris ed i n, that the trihydric alcohol is alkoxylated by reacting said alcohol with at least one alkylene oxide. 6. Shrinkage-reducing agent according to Claim 5 ch aracte ris ed i n, that the alkylene oxide is ethylene oxide, propylene oxide or a combination thereof. 7. Shrinkage-reducing agent according to any of the Claims 3-6 ch a racte rised i n, that the trihydric alcohol is a trimethylol C j -C alkane. 8. Shrinkage-reducing agent according to Claim 7 c h a rac te ris ed i n, that the trimethylol C^C g alkane is trimethylolethane, trimethylolpropane or a combination thereof. . Shrinkage-reducing agent according to any of the Claims 1-8 ch aracterised in, that the acetal is a 4-hydroxyalkyl-l,3-dioxolane, a 5-alkyl-5-hydroxyalkyl-l,3- -dioxane or a 5,5-dihydroxyalkyl-l,3-dioxane or a combination thereof. 10. Shrinkage-reducing agent according to any of the Claims 1-9 c h a racte rised in, that the acetal is 4-hydroxymethyl-l,3-dioxolane, 5-hydroxy-l,3-dioxane, 5-ethyl-5-hydroxymethyl-l,3-dioxane, 5,5-dihydroxymethyl-l,3-dioxane or a combination thereof. 11. Shrinkage-reducing agent according to any of the Claims 1-10 c h a racterised in, that the agent comprises 1-99% by weight of said acetal. 12. Shrinkage-reducing agent according to any of the Claims 1-10 ch aracterised in, that the agent comprises 40-99% by weight of said acetal. 13. Shrinkage-reducing agent according to any of the Claims 1-10 c h a racte ris ed in, that the agent comprises 50-99% by weight of said acetal. 14. Shrinkage-reducing agent according to any of the Claims 1-13 c h a racteris ed in, that the agent in addition to said acetal comprises at least one silica. 15. Shrinkage-reducing agent according to Claim 14 c h aracterised in, that the silica is a powderous silica. 16. Shrinkage-reducing agent according to Claim 14 or 15 c h aracteris ed in, that the silica is a silicic acid. 17. Shrinkage-reducing agent according to any of the Claims 14-16 c h a racte rised in, that the agent comprises 1-50% by weight of said silica 18. Shrinkage-reducing agent according to any of the Claims 14-16 ch a racteris ed in, that the agent comprises 10-40%, by weight of said silica. 19. Use of a skrinkage-reducing agent according to any of the Claims 1-18 in an aqueous cement containing composition ch a racterised in, that the agent is added to the composition in an amount corresponding to 0.1-20% by weight calculated on dry cement included in said composition. 20. Use according to Claim 19 ch a racterised in, that the agent is added to the composition in an amount corresponding to 1-10% by weight calculated on dry cement included in said composition. 21. Use according to Claim 19 ch a racterised in, that the agent is added to the composition in an amount corresponding to 2-5% by weight calculated on dry cement in said composition. 22. Use according to any of the Claims 19-21 ch a rac te ris ed i n, that the cement composition is a concrete, a hydraulic cement, a screed, a mortar or a sealant composition.

Inventors: ENGSTRAND JENS, SJOEGREEN CARL-AXEL, ENGSTRAND, JENS, SJOEGREEN, CARL-AXEL
Applicants: ENGSTRAND JENS, PERSTORP AB, SJOEGREEN CARL AXEL, ENGSTRAND, JENS, SJOEGREEN, CARL-AXEL
Application year: 1998
Main classification: C04B24
IPC codes: C04B24, C04B28, C04B40, C04B103