ALUMINUM DEPOSITION SHIELD

Abstract: An aluminum deposition shield substantially improves transfer of radiated heat from within the vacuum chamber, in comparison to a stainless steel deposition shield. The aluminum deposition shield remains cooler during wafer processing and assists in cooling the chamber components.

Description: ALUMINUM DEPOSITION SHIELD Field of the Invention The present invention relates to an apparatus for processing wafers in a vacuum chamber. More particularly, the invention relates to an apparatus for removal of heat from a vacuum chamber. Background of the Related Art Connecting a power source, such as a radio frequency ("RF") power source, to a device, such as an RF antenna coil, through the wall of a vacuum chamber typically involves providing an insulated passage through one or more deposition shields. Application of RF energy to the coil tends to generate heat within the chamber. This heat is dissipated through radiation and conduction to heat sinks typically the shield, target, etc. within the chamber. Deposition shields are typically constructed of stainless steel for strength and tend to be negatively charged or grounded during wafer processing. Furthermore, the shield accumulates heat during wafer processing and chamber cooling declines unless the additional heat is removed from the shield. There is a need, therefore, for a deposition shield which avoids build up of additional heat within the vacuum chamber. Summary of the Invention The present invention provides an aluminum deposition shield which substantially improves transfer of radiated heat from within the vacuum chamber, to external chamber components in comparison to a conventional stainless steel deposition shield. The aluminum deposition shield remains cooler during wafer processing and assists in cooling the chamber components. Brief Description of the Drawings So that the manner in which the above recited features, advantages and objects of the present invention are attained and can be understood in detail, a more particular description of the invention, briefly summarized above, may be had by reference to the embodiments thereof which are illustrated in the appended drawings. The appended drawings illustrate typical embodiments of this invention and are not to be considered limiting of its scope, for the invention may admit to other equally effective embodiments. Figure 1 is a sectional view of a vacuum deposition chamber (without a target assembly) showing an external RF power source connected to a flat RF electrode coil within an aluminum deposition shield; Figure 2 compares the processing temperatures of deposition shields which are constructed from stainless steel or aluminum. Detailed Description of the Invention The present invention provides an aluminum deposition shield within a vacuum chamber to enhance removal of radiated or conducted heat from an internal heat source such as an RF electrode. The vacuum chamber can be any plasma enhanced processing chamber wherein external RF or DC power is connected to a device within the vacuum chamber. Cooling of the vacuum chamber is enhanced since aluminum has a higher heat transfer co-efficient in comparison to stainless steel. The aluminum deposition shields are especially useful for cooling an electrode within a high density plasma vacuum semiconductor processing chamber such as the VECTRA® IMP chamber available from Applied Materials, Inc. of Santa Clara, CA. The high vacuum chambers are used for physical vapor deposition (PVD) of Aluminum, Titanium, Copper, Tantalum, Tantalum Nitride, or Titanium Nitride layers to form conductors or barrier layers on semiconductor wafers. One or more VECTRA® IMP chambers are typically mounted on a semiconductor processing platform such as the ENDURA® platform manufactured by Applied Materials, Inc. The invention is further described by reference to a specific aluminum deposition shield shown in the drawings, and by reference to comparisons to deposition shields made from other materials. As shown in Figure 1, the present invention relates to a useful apparatus for processing a substrate in a semiconductor processing chamber 10. The processing chamber 10 typically includes a clamp ring 12 and a support member 14 disposed in the processing chamber 10, and a substrate alignment member 16 located on the support member 14. The substrate alignment member 16 aligns a substrate 18 with the support member 14 under gravity feed as the substrate is received on the support member 14. A substrate lift mechanism 20 moves pins 22 to receive the substrate prior to processing in the chamber. A support lift mechanism 24 raises the support member 14 so that the support member 14 picks up the substrate 18 off the pins 22 prior to processing in the chamber, or lowers the support member 14 to place the substrate on the pins 22 for removal of the substrate after processing. As the support member 14 continues moving upward in the chamber 10, the support member 14 passes into the clamp ring 12 which rests upon an aluminum deposition shield 26. An aluminum adapter 28 supports the aluminum deposition shield 26 and an insulator 30. The adapter 28 is a wall of the vacuum chamber and typically has passages (not shown) for cooling water. An external RF power source 36 supplies RF power to the antenna coil 32 which is externally grounded. The coil 32 is supported within the chamber on a plurality of standoffs 34. The coil 32 is supplied with power to enable a gas, maintained at a vacuum pressure level in the chamber, to be energized into a plasma. The coil 32 may optionally be supplied with a coolant through a central passage. To enable passage of the RF, or other, power to the coil 32, conductive elements must extend through the chamber wall, but they cannot contact the chamber wall which may be grounded, or, if contacted with the conductor, will become "hot." To provide this configuration, an insulated feed through (not shown) is typically extended though the adaptor. The aluminum deposition shield must be thicker than a comparable stainless steel shield to provide equivalent strength. However, a higher heat transfer co-efficient provides better cooling. Preferably, the shield 26 is configured to have a thin lip 25 which engages the conventional clamp ring 12. The remainder of the shield 26 is thicker than comparable stainless steel shields unless a narrow region is needed for close tolerances. Performance of aluminum deposition shields Examples 2-6 of the present invention was simulated under wafer processing conditions and compared to a stainless steel shield Example Cl. During wafer processing, the wafer was heated to 200°C. Each shield was supported by connectors which provides some convection of heat to the shield. Temperatures within the vacuum chamber were recorded at the wafer center, the shield bottom, the shield top, the shield middle, the coil bottom, the coil top, and the coil bottom. Thickness of the shields are shown in Figure 2 along with the temperature measurements. The thicker aluminum shields 5,6 provided the lowest steady state shield temperatures. While the foregoing is directed to the preferred embodiment of the present invention, other and further embodiments of the invention may be devised without departing from the basic scope thereof. The scope of the invention is determined by the claims which follow.

Claims: What Is Claimed Is: 1. A wafer processing system, comprising: a vacuum chamber; an aluminum deposition shield fastened to the vacuum chamber; and a radiated heat source positioned to radiate heat to the deposition shield. 2. The wafer processing system of claim 1, wherein the radiated heat source is an RF antenna. 3. The wafer processing system of claim 1 , wherein the vacuum chamber is an inductively coupled PND processing chamber.

Inventors: DAS ASHOK K, DELAURENTIS LEIF E, ROSENSTEIN MICHAEL, SUBRAMANI ANANTHA, DAS, ASHOK, K., DELAURENTIS, LEIF, E., ROSENSTEIN, MICHAEL, SUBRAMANI, ANANTHA
Applicants: APPLIED MATERIALS INC, APPLIED MATERIALS, INC.
Application year: 1998
Main classification: H01L21
IPC codes: C23C14, H01J37, H05H1