PROCESS FOR THE PREPARATION OF ULTRA-FINE POWDERS OF METAL OXIDES

Abstract: A novel process for the preparation of ultra-fine powders of metal oxide wherein a surfactant is added to the solution for the preparation of the metal oxide to provide nanometer metal oxide powders without the utilization of vacuum or high pressure conditions is disclosed.

Description: PROCESS FOR THE PREPARATION OF ULTRA-FINE POWDERS OF METAL OXIDES BACKGROUND OF THE INVENTION The properties of a material are influenced by the surrounding environment and can even vary with its particle size. The surface area of a material will change with its particle size. The properties such as magnetism, electric resistance and optical properties of a material with a smaller particle size will be different from those of the same material with a larger particle size due to the relative difference between their surface area. It is known that ultra-fine powders of metal oxides are useful in various fields. For example, for catalysts, the application of ultra-fine metal oxide powders can increase the surface area of catalyst; for computers and televisions, the application of ultra- fine metal oxide powders in coating the screen of a computer or a television can provide resistance to electrostatics and reflection; and in chemical mechanical polishing, ultra-fine metal oxide powders can be used as abrasives in the polishing procedure. Various processes for the preparation of metal oxide powders are known in the art. For instance, cracking, physical vapor deposition, chemical vapor deposition, spray pyrolysis, gel method and hydrothermal method have been developed (see, Carturan et al., J. Material Science 23 (1988) 3156; Xie et al., Phys. Stat. Sol. (a) 141, K59 (1994); Unaogu et al., Solar Energy Materials 20 (1990) 29; J.P. Chatelon, Terrier et al., Thin Solid Films, 247 (1994) 162 and Zuo et al., J. Appl. Phys. 75(3), 1 February 1994.) Cracking is simple but cannot provide the desired particle size and distribution because the particles prepared are not uniform. Both physical and chemical vapor depositions have to be conducted under vacuum conditions and reguire high operation costs. The particles provided by spray pyrolysis are too large to be useful. Gel method can provide a desired particle size but requires high costs because it should start with metal alkoxides which are expensive and easily flammable. Hydrothermal method is a modification of the gel method and has to use a hydrothermal apparatus which should be conducted under high temperature and high pressure conditions. Hydrothermal method can start with metal salts without the shortcomings of the gel method. However, hydrothermal method has the disadvantage of high operation costs for the high temperature and pressure conditions of the hydrothermal apparatus. Therefore, there is a necessity in the art to provide an economical process for preparing ultra-fine metal oxide powders with desired particle size and particle distribution without the utilization of vacuum or high pressure condition. SUMMARY OF THE INVENTION It is an object of the present invention to provide a process for preparing ultra-fine metal oxides without the application of high temperature and high pressure. According to the present invention, ultra- fine metal oxide powders with good quality can be prepared by way of the utilization of a surfactant. It is another object of the present invention to provide metal oxide powders in the order of nanometer without the application of flammable starting materials or a high temperature - pressure apparatus. 99/02 - 3 - The present invention relates to a process for preparing ultra-fine metal oxide powders comprising adding a surfactant to a metal compound solution and heating and calcining the gels and/or precipitates formed therefrom to provide metal oxide powders in the order of nanometer. These and other objects, advantages and features of the present invention will be more fully understood and appreciated by reference to the written specification. BRIEF DESCRIPTION OF THE DRAWINGS Fig. 1 shows a combination of surfactant and metal oxide formed during the process of the present invention wherein 1 represents a micell of surfactant and 2 represents a metal oxide shell. Fig. 2 shows the x-ray diffraction patterns of Sn0 2 powders prepared by the process of the present invention under different calcining temperatures. Figs. 3(a), 3(b) and 3(c) show the electron microscopic diffraction patterns of Sn0 2 powders prepared by the process of the present invention and calcined at 200, 400 and 800 °C respectively. Figs. 4(a), 4(b) and 4(c) show the electronic microscopy pictures of Sn0 2 powders prepared by the process of the present invention and calcined at 200, 400 and 800 °C respectively. Fig. 5 shows the x-ray diffraction patterns of Sn0 2 powders prepared by hydrothermal method under different calcining temperatures. Fig. 6 shows the plots of the particle size of Sn0 2 powders prepared by hydrothermal process and by the process of the present invention under different calcining temperatures. Fig. 7 shows the x-ray diffraction patterns of the metal oxide powders prepared by the process of the present invention at different molar ratios of surfactant to metal compound. DETAILED DESCRIPTION OF THE INVENTION The present invention provides a process for the preparation of ultra-fine metal oxide powders, especially metal oxide powders in the order of nanometer comprising the steps of: (i) providing an aqueous solution of metal compound comprising a metal moiety corresponding to the metal moiety of the metal oxide; (ii) providing a surfactant; (iii) mixing the metal compound solution and the surfactant to form gels and/or precipitates; and (iv) heating and calcining the gels and/or precipitates . In the process of the present invention, the metal moiety of the metal compound should be that of the desired metal oxide. The metal compounds can be in any type known in the art suitable for preparing metal oxides. For example, but not limited to, the metal compound can be a salt or an alkoxide. A salt is preferred because it is more economic and can avoid the problems caused by flammable alkoxides. Examples of metal salts for preparing metal oxide powders are such as, but not limited to, silicate (for preparing Siθ2 powders), the chlorides of antimony and stannum (for preparing Sb θ5 and Sn0 2 powders respectively) . Upon appropriate control, the process of the present invention can provide any desired metal oxides powders. Examples of the species of the super-fine metal oxide powders are Sn0 2 , A1 2 0 3 , Siθ 2 , Ce0 2 , Zr0 2 , Ti0 2 , ln 2 0 3 , Ru 2 0 3 , Sb 2 0 5 and V 2 0 5 . The use of a surfactant is critical to the process of the present invention. Without the limitation of theory, it is believed that the addition of surfactant primarily changes the physical morphology of metal oxide during the preparation. For example, the formation of metal oxides in hydrothermal method comprises two stages: a hydrolysis stage and a condensation stage. Metal salts are hydrolyzed into corresponding oligomer intermediates and then the intermediates condense into metal oxide condensates. The metal oxide condensates are then heated to remove solvent and calcined at high temperature to provide desired metal oxide powders. The addition of a surfactant in the process of the present invention is to change the physical morphology of the condensates. It is known that a surfactant has a hydrophilic end and a hydrophobic end. In an aqueous solution, hydrophobic ends will gather and hydrophilic ends will bind to water and thus the micells of surfactant will form. In the process of the present invention, the metal oxide at condensation stage will be propped open by the micell of surfactant and form a metal oxide shell surrounding the micell. Fig. 1 shows a specific combination of surfactant and metal oxide formed during the process of the present invention, wherein 1 - 6 - represents the rod micell of surfactant and 2 represents the metal oxide shell. Without the limitation of theory, it is believe that the driving force for binding metal oxide to surfactant is the Coulombian force between the metal oxide and the surfactant. Specifically, when the metal compound for preparing metal oxide provides a metal moiety having positive charge (s) in solution, anionic surfactants such as dococyl phosphonate, cetyl sulfonate, sodium dioctyl sulfosuccinate, sodium stearate and sodium lauryl sulfate are suitable; when the metal moiety having negative charge (s) in solution, cationic surfactants such as cetyltrimethylammonium chloride, cetyltrimethylammonium bromide, cetyl- trimethylammonium hydroxide, doctyltrimethylammonium chloride, doctyltrimethylammonium bromide and doctyltrimethylammonium hydroxide are suitable; when the metal moiety is neutral in solution, neutral surfactants such as polyethylene oxide, polypropylene oxide and hexadecylamine are appropriate. In other words, the selection of surfactant depends on the charge type of the metal moiety of used metal compound in solution. Gels or precipitates will not form unless the charge types of the metal moiety and the surfactant meet the aforementioned requirements. In the process of the present invention, the surfactant can be a single surfactant, or a mixture of surfactants. The amount of surfactant used in the process of the present invention can vary in a wide range with the proviso that the amount of surfactant is not up to the extent that a metal oxide shell cannot form around the surfactant micell. In the process of the present invention, it is preferred that the molar ratio of surfactant to metal compound is less than 20:1, more - 7 - preferred is less than 10:1 and most preferred is 5:1, especially 0.5:1. During the mixing of the metal compound solution and surfactant, any operations disadvantageous to the formation of gels or precipitates (e.g. stirring) should be avoided. It is preferred that the mixture of the solution of metal compound and surfactant is left to stand for a period of time to facilitate the aggregation of gels or precipitates. The formed gels or precipitates are then directly collected by such as filtration with suction. As known in the art, the collected gels or precipitates should not contain any Cl~ when metal chlorides are used in the preparation of metal oxide powders and this can be ensured by any conventional ways. For instance, a solution of AgN0 3 can be used to determine whether the gels or precipitates contain any residual Cl ~ . If necessary, the gels or precipitates should be washed several times with deionized water to remove any residual Cl~. In an embodiment of the present invention, the solution containing formed gels or precipitates is left to stand for a period until the upper clear phase is formed, the upper clear phase is repeatedly replaced with deionized water until no Cl ' can be detected by a AgN0 3 solution and then the solution is filtrated with suction to collect the gels or precipitates. Thereafter, the collected gels or precipitates are heated and calcined, wherein the solvent is first removed and then the surfactant is removed to leave metal oxide shells. Finally, the shells crash and form ultra-fine metal oxide powders. It is preferred that the heating and calcining are operated separately, the solvent adhering to gels or precipitates are first removed by a drying operation and the residual is put in a high temperature oven to remove the surfactant micells and to crash the metal oxide shells to obtain metal oxide powders. In other words, it is preferred that the calcining operation is carried out at a temperature up to that being able to remove the surfactant. Generally, 500°C can completely remove most suitable solvents. For instance, when SnCl 4 and Naθ3SCH(COOC g H 1 7) CH 2 C00C 8 H 1 7 are used to prepare ultra- fine Sn0 2 powders, Na0 3 SCH(C00C 8 H 17 ) CH 2 C00C 8 H 17 can be completely removed by calcining at about 400°C. The following examples are offered by way of illustration. The examples are not intended to be limit the scope of the invention in any respect and should not be so construed. EXAMPLES EXAMPLE 1: 3.2900g of SnCl4 * 5H 2 0 were dissolved in 10.0 ml of water. 2.6000g of Na0 3 SCH (C00C 8 H 17 ) CH 2 C00C 8 H 17 were added to 190 ml of water under heating and stirring until completely dissolved and then the solution was cooled at room temperature. The solution of SnCl 4 "5H 2 0 was mixed with the solution of Naθ3SCH(COOC 8 H 17 ) CH C00C 8 H 17 and a gelled solution of white precipitates was obtained. The gelled solution was left to stand for 24 h, and then the upper clear phase was repeatedly replaced with deionized water and the lower precipitate phase was filtrated with suction to remove any residual Cl~ until no Cl " can be detected by a solution of AgN0 3 . The collected precipitates were dried in an oven. The dried precipitates were put in a high temperature oven for the heat treatment and the temperature of the oven was increased at a rate of 5°C/min to 200°C to calcine the precipitates for 6 h and then cooled the oven at a rate of 5°C/min to room temperature to obtain Sn0 2 powders. - 9 - Repeating the above heat treatment procedures with the exception that the temperature of the oven was increased to 400°C, 600°C and 800°C respectively to obtain Sn0 2 powders. The crystal structure of Sn0 2 powders were determined by an x-ray diffractometer and the results were shown in Fig. 2. In Fig. 2, the ordinate represents the intensity and the abscissa represents the Bragg angle (2θ) of x-ray diffraction pattern. As shown in Fig. 2, the powders obtained at room temperature (25°C) had a relatively strong peak at low angle (2θ is about 2.4°) which corresponded to someone crystal structure. By way of electron microcopy, it was observed that the peak was resulted from the rod surfactant micells (as shown in Fig. 1) . This demonstrated that, during the process of the present invention, the prepared metal oxide adhered to the surface of surfactant micell. Further, it was observed that the intensity of the low angle diffraction peak decreased with the increase of calcining temperature and this was because the surfactant was gradually removed and the shell of Sn0 2 gradually crashed. When the calcining temperature was up to 400°C, the surfactant was completely removed and shell of Sn0 completely crashed to small pieces and no low angle (2θ is about 2.4°) diffraction peak was observed. In stead of the low angle diffraction peak, another peak corresponding to the crystals of Sn0 2 powders (2θ is 22° - 55°) was observed and its intensity increased with the increase of calcining temperature. The above phenomena that the crystals of Snθ 2 was gradually distinct can be further demonstrated by the electron diffraction patterns of Sn0 2 powders. Figs. 3(a), 3(b) and 3(c) were the diffraction patterns of - 10 - Sn0 2 powders at 200, 400 and 800°C respectively. As shown in Figs. 3(a), 3(b) and 3(c), the diffraction pattern at 200°C was a circular diffraction which corresponded to amorphous structure; the diffraction patterns at 400°C and 800°C contained diffraction points and the number of diffraction points increases with the calcining temperature and the crystal structure is gradually distinct. From the x-ray diffraction patterns, the particle size of metal oxide powders can be calculated from Sherrer Equation as below: wherein d is the particle size, k is shape factor, X is the wave length of x-ray (here, the value of X of CuK α is 1.5418 A), θ is the Bragg angle (here, 2θ = 33.9°), is half of the height of the diffraction peak (at 2θ = 33.9°). The results were shown in Table 1. Table 1 It was noted from Table 1 that the particle size was increased with increase calcining temperature. Nevertheless, even though the calcining temperature was up to 800°C, the particle size of obtained powders was 26.0 nm. The particle size of powders can be only 5.2 - 11 - nm as the calcining temperature is merely 400°C at which the surfactant can be completely removed. The average particle size of metal oxide powders can be directly determined by electron microscope. Figs. 4(a), 4(b) and 4(c) were the photos of powders calcined at 200°C (enlarge 1.5 x 10 5 times), 400°C (enlarge 1.5 x 10 5 times), and 800°C (enlarge 2 x 10 5 times) respectively. Many holes can be observed in Fig. 4(a) and they correspond to the position of surfactant. When the surfactant was completely removed, the shells of metal oxide completely crashed (as shown in Fig. 4(b)). When higher calcining temperature was used, distinct crystals can be observed (Fig. 4(c)). From the photos, the particle size of powders obtained at a calcining temperature of 800°C can be directly determined and was about 30 nm, which is close to the average particle size predicted from the corresponding x-ray diffraction pattern by Sherrer Equation. This demonstrates that the process of the present invention can provide super-fine powders in the order of nanometer. COMPARATIVE EXAMPLE C-l: This example illustrates the preparation of Sn0 2 powders by conventional hydrothermal method. 8.7876g of SnCl 4 '5H 2 0 were dissolved in 100.0 ml of water, and, 2.1 ml of 12M HN0 3 were added to obtain a solution with a molar ratio of HN0 3 to SnCl 4 being 1:1. 80 ml of the solution were put in a thermal bomb and the thermal bomb was heated in a high temperature oven at 150°C for 12 h, and then cooled to room temperature and white precipitates formed. The precipitates were repeatedly washed with deionized water and filtrated with suction until no Cl- can be - 12 - detected by a solution of AgN0 3 . The precipitates were then dried and put in a high temperature oven and the temperature of the oven was increased at a rate of 5°C/min to 200°C to calcine the precipitates for 6 h and then cooled the oven at a rate of 5°C/min to room temperature to obtain Sn0 2 powders. Repeating the above procedures with the exception that the temperature of the high temperature oven was increased to 400°C, 600°C and 800°C respectively to obtain Sn0 2 powders. Fig. 5 shows the x-ray diffraction patterns of Sn0 powders under different calcining temperatures. A comparison of Fig. 2 to Fig. 5 reveals that the x-ray diffraction patterns of the metal oxide powders prepared by hydrothermal method at low temperature (i.e. room temperature and 200 °C) are almost the same as those of the metal oxide powders prepared by the process of the present invention with the exception that the former do not have the characteristic diffraction peak at low angle. This demonstrated that the crystal type of the Sn0 2 powders prepared by the process of the present invention is the same as that prepared by hydrothermal method. Also, Sherrer Equation was used to predicted the particle size of the powders prepared by hydrothermal method and the results were shown in Table 2: - 13 - Table 2 A comparison of Table 1 and Table 2 reveals that, at the same temperature, the process of the present invention can provide metal oxide powders whose particle size is smaller than that of the metal oxide powders prepared by hydrothermal method without the use of a hydrothermal apparatus. Fig. 6 shows the plots of the particle size of Snθ 2 powders and calcining temperature shown in Tables 1 and 2. From Fig. 6, it is apparent that the process of the present invention can provide metal oxide powders with a desired particle size at a lower temperature. EXAMPLES 2~4: The procedures of EXAMPLE 1 were repeated but SnCl 4 '5H 2 0 and Na0 3 SCH (COOC 8 H 17 ) CH 2 COOC 8 H 17 were added at the amount that the molar ratios of SnCl4 ' 5H 0 to Na0 3 SCH(COOC 8 H 17 )CH 2 COOC 8 H 17 were 1:0.6, 1:1 and 1:1.6. The x-ray diffraction patterns of metal oxide powders obtained at room temperature and at different molar ratios were shown in Fig. 7. As shown in Fig. 7, the metal oxide powders obtained at each molar ratio had a diffraction peak at low angle (2θ is about 2.4°). In other words, in each case, metal oxide shells formed around the surface of rod surfactant micells and can provide the desired ultra-fine Sn0 2 powders. EXAMPLE 5: 5.3g of Na Si0 4 were dissolved in 10 ml of water. An appropriate amount of cetyltrimethylammonium bromide (C 16 TMBA) was added to water under heating and stirring to prepare a 12% solution. The solution of Na 2 Si0 4 was mixed with 30 ml of the solution of C 16 TMBA and the mixture was left to stand. Thereafter, the precipitates were collected by filtration with suction. The collected -precipitates were dried and then put in a high temperature oven and the temperature of the oven was increased at a rate of 5°C/min to 600°C to calcine the precipitates for 6 h to remove the surfactant and calcine the metal oxide shells to obtain ultra-fine powders with a particle size of about 30 nanometer. As shown in the examples, the process of the present invention can provide ultra-fine metal oxide powders without the utilization of a high temperature and pressure hydrothermal apparatus or metal alkoxides and can satisfy the need of easy processing, low cost and suitable for mass-production.

Claims: - 15 - CLAIMS 1. A process for the preparation of ultra-fine metal oxide powders comprising the steps of: (i) providing an aqueous solution of metal compound comprising a metal moiety corresponding to the metal moiety of the metal oxide; (ii) providing a surfactant; (iii) mixing the metal compound solution and the surfactant to form gels and/or precipitates; and (iv) heating and calcining the gels and/or precipitates . 2. The process of Claim 1 further comprising the step of, prior to step (iv) , standing the gels and/or precipitates formed at step (iii) . 3. The process of Claim 1, wherein the heating and calcining step (iv) comprises drying and calcining stages. 4. The process of Claim 1, wherein the metal compound is a salt or an alkoxide. 5. The process of Claim 1, wherein the surfactant comprises at least one surfactant whose charge compensating that of the metal moiety of the metal compound. 6. The process of Claim 1, wherein the metal compound is a chloride and the surfactant comprises at least one anionic surfactant. 7. The process of Claim 1, wherein the metal compound is an alkoxide and the surfactant comprises at least one neutral surfactant. 8. The process of Claim 1, wherein the molar ratio of surfactant to the metal compound is less than 10:1. 9. The process of Claim 8, wherein the molar ratio is less than 5:1. 10. The process of Claim 1, wherein the calcining operation of step (iv) is carried out at a temperature sufficient to remove the surfactant adhere to the gels and/or precipitates.

Inventors: KAO YU-HUA, LIU RU-SHI, SUEN SHICH-CHANG, KAO, YU-HUA, LIU, RU-SHI, SUEN, SHICH-CHANG
Applicants: KAO YU HUA, LIU RU SHI, MERCK PATENT GMBH, SUEN SHICH CHANG, KAO, YU-HUA, LIU, RU-SHI, SUEN, SHICH-CHANG
Application year: 1998
Main classification: C01B13
IPC codes: C01B13, C01G19