HOLDER FOR TURNING OPERATION

Abstract: A holder of blade type has been developed particularly for grooving and parting. The blade holder is manufactured in a compound material including the sub micron hard material Coronite3. This gives a considerably improved rigidity and a considerably reduced tendency to vibration.

Description: HOLDERFOR TURNING OPERATION The present invention refers to a holder of the blade type intended foremost for different turning applications, such as grooving, face grooving and parting, in accordance with claims 1. Slitting cutters and circular saw blades are also included in the term "blade . type". Cutting inserts for grooving and parting are clamped in holders of the blade type, in order to allow narrow widths of cut. Such blade holders are normally made of steel, for example tool steel, and feature a number of different clamping arrangements for the actual cutting inserts. Said inserts are made of hard material, generally cemented carbide. Different examples of various designs of clamping systems for cutting inserts in blade holders are referred to in US-A-4 801 224, US-A-4 588 333, US-A-4 195 956, EP-A-259 847, as well as the as yet unpublished Swedish patent applications 9701003- 7, 9701134-0 and 9701135-7. The cutting inserts are clamped in the free end of the blade holder, while the blade holder itself forms a part of a tool which even includes a tool shank which extends across the blade. The actual blade part can either be an integral part of the shank, such as for example is shown in the drawings in the aforementioned Swedish patent applications 9701134-0 and 9701135-7, or the blade part is clamped in the shank portion by, for example, a screw or wedge coupling, see for example SE-C-501 914. Common for all blade holders, irrespective of the design of the clamping system for the cutting insert, is that they can begin to vibrate, which naturally is a clear drawback. The vibration leads, for example, to poorer surface finish on the workpiece, damage to the cutting insert and even tool failure may occur. Another problem with a large number of blade holders, in particular with narrow width and/or long overhangs, is outward bending, respectively deflection of the blade part because of axial and tangential cutting forces. C0PIE DE CONFIRMATION The purpose of the present invention is consequently to diminish the tendency to vibration in holders of the blade type. An additional purpose with the present invention is to reduce, as far as possible, all manner of bending of the blade part. These and even other aims have been successfully achieved by designing a holder of the blade type, which comprises the features indicated in the characterizing part of claim 1. In order to illustrate but in no way limit the invention it will now be described in more detail with reference to the attached drawings. Figure 1 shows a typical blade holder according to known technique, with two insert pockets. Figures 2 a-h show cross sections of different holders of the blade type according to the present invention. Figure 1 shows a blade holder 1 for the turning of grooves and parting operations. These vary in thickness but are in general between 1 and 8 mm thick. They have a cutting insert position 2, 2' at each end, for the clamping of a cutting insert of usually coated or uncoated cemented carbide. This cutting insert is held firmly by the clamping force which the upper clamping part 3 exerts on the cutting insert. Further the holder features a transverse hole 4 at each end into which one pin of a special key intended for the installation of the cutting insert can be inserted. It should however be pointed out, that the actual type of clamping of the the cutting insert is of no importance for the present invention. The entire blade holder 1 is clamped in its turn in a tool shank which is not illustrated. Normally the cutting insert is used only in one insert pocket 2, 2' at a time for the machining of metal by cutting. Alternatively the blade holder 1 can be shorter and equipped with only one of the two insert pockets. Further the blade holder can form an integral part of a tool shank, such as in the figures to be found in Swedish patent applications 9701134-0 and 9701135-7. As mentioned above, all tool holders of the blade type suffer from a certain propensity to vibration, in particular when the free overhang of the holder is relatively large and the blade holder is relatively thin. Further a certain degree of sideways deflection respectively downwards deflection commonly occurs, among other things as a function of the blade thickness and the size of the cutting forces. The present invention has in a surprising manner succeeded in considerably reducing the tendency to such vibration, respectively considerably reduced the degree of bending, by producing the blade holder wholly or preferably partly in a hard material with 30-70% by volume sub micron hard materials in the form of carbides, nitrides and/or carbonitrides of Ti, Zr, Hf, V. Nb, Ta, Cr, Mo and/or W in a metallic matrix based on Fe, Co and/or Ni. The hard material preferably consists of 30-70 % by volume hard constituents of mainly TiN in a matrix of a high speed steel type, where the concentrated hard materials have a grain size of < 1 μm, preferably < 0,5 μm. This material is in itself previously known through, for example, SE-C-392 482. Further the compound material is known previously through, for example, SE-C-440 753, in which this sub micron material is covered. Such a material is commercially available under the trademark Coronite®. This material can be metallurgically bonded to a tougher material such as tool steel, in accordance with said patent SE-C-440 753. Nowhere in these patent documents is it intimated, however, that it may be possible to manufacture a holder of the blade type in this material and nowhere is it mentioned that the material may be able to impart an object with an anti- vibration effect. The embodiments in figure 2 a-h illustrate a number of different conceivable cross sections of a blade holder according to the present invention. References indices 5a-h show matrices of, for example, tool steel and reference indices 6a-b show different cores of sub micron hardmaterials. These profiles have been produced by force injecting a ribbon of the two materials together, with or without a subsequent rolling process. The force injection of a ribbon of material is a method well-known by a man skilled in the art of working metallic materials, which gives the possibility even to shape alloys which are relatively difficult to machine. In trials it has been shown possible to force inject hot ribbons of alloys which are extremely rich in hard material even tungsten carbide alloys with a content of hard material as high as 80% WC by weight. Further, . according to known technique, it is possible to extrude two or more material with different properties together to form machine parts in the compound material. It is specifically through such a method of force injecting a ribbon, that cross sections according to the figures 2 a-h can be produced. The different shapes are attained by milling or drilling out a cavity in a steel billet and subsequently filling the cavity with a powder of a sub micron hard material. During the force injection of a ribbon the hard constituent are sintered and enter into a metallurgical bonding with the surrounding steel. If no rolling operation is applied after the extrusion the drilled holes retain their circular shape, according to fig 2a and 2g. If however the ribbon is rolled a number of times after the force injection, the bores and thereby the hard constituents will take on a more and more elliptical shape, see fig 2F. According to fig 2h the blank has been force injected to a curved cross section, which is intended to be used for face grooving. It is possibly to force inject the blade holder directly to the final shape desired (with or without rolling), but usually a final processing is required in order to attain the dimensions and surface finish wished for. If the tool steel surrounds one or more cores of sub micron hard material it conveys the advantage, that the surface can be machined by conventional metal cutting machining, such as milling. If however the sub micron hard material lie wholly or partly at the outer surfaces, these parts must be ground. This latter requirement applies, for example, to the embodiments according to fig 2c, d and e. Through tests which have been performed it has been established, that blade holders according to this invention exhibit a considerably higher Young's modulus and considerably reduced vibration. Consequently two blade holders in accordance with figure 1 , were compared one wholly in tool steel and one in tool steel with a core of a sub micron hard material, in accordance with figure 2F. The free overhang in both cases was 32 mm and in both the cases the cross section of the blade was 30 x 4,35 mm. A tangential cutting force Fc of 2700 N, was applied at the cutting edge to give downwards deflection. Further in another test an axial force of 1250 N was applied to the cutting edge causing an outward bending force of Ff. The results obtained were as follows: Deflection downwards Deflection sideways (Fc = 2700N) (Ff= 1250 N) Standard blade 0,03 mm 0,45 mm Blade according to info. 0,025 mm 0,25 mm Thus considerably improved results were obtained for the compound blade according to the invention. A blade holder which is considerably stiffer has thus been developed. Further both the shearing frequency, natural frequency and the total frequency increased considerably, in comparison with the conventional blades on blades designed according to the invention.

Claims: CLAIMS 1. Tool holder of blade type, in particular for metal cutting machining operations such as grooving and parting, including a blade part (1), characterized thereof, that the blade part comprises a sub micron hard material which makes the blade part stiffer. 2. Holder according to claim 1 , characterized thereof, that the said hard material consists of 30-70 % by volumesub micron hard constituents in the form of carbides, nitrides and/or carbonitrides of Ti, Zr, Hf, V, Nb, Ta, Cr, Mo and/or W in a metallic matrix based on Fe, Co and/or Ni. 3. Holder according to claims 2, characterized thereof, that the hard material comprises 30-70 % by volumehard constituents of mainly TiN in a matrix of a high speed steel type, where the concentrated hard constituents have a grain size of < 1 μm. 4. Holder according to anyone of the preceding claims, characterized thereof, that the hard material is enclosed by a surrounding matrix of steel. AMENDED CLAIMS [received by the International Bureau on 13 October 1998 (13.10.98); original claims 1 and 4 replaced by amended claim 1, remaining claims unchanged (1 page)] 1. Tool holder of blade type, in particular for metal cutting machining operations such as grooving and parting, including a blade part (1 ), characterized thereof, that the blade part comprises one or more cores of a sub micron hard material which makes the blade part stiffer and which is surrounded by a matrix of steel, for example tool steel. 2. Holder according to claim 1 , characterized thereof, that the said hard material consists of 30-70 % by volume sub micron hard constituents in the form of carbides, nitrides and/or carbonitrides of Ti, Zr, Hf, V, Nb, Ta, Cr, Mo and/or W in a metallic matrix based on Fe, Co and/or Ni. 3. Holder according to claims 2, characterized thereof, that the hard material comprises 30-70 % by volume hard constituents of mainly TiN in a matrix of a high speed steel type, where the concentrated hard constituents have a grain size of < 1 μm.

Inventors: BRASK KARL-GOERAN, HANSSON PER, BRASK, KARL-GOERAN, HANSSON, PER
Applicants: SANDVIK AB, SANDVIK AKTIEBOLAG
Application year: 1998
Main classification: B23B29
IPC codes: B23B29