Method for reducing the substrate dependence of resist

Abstract: This invention relates to a substrate dependence reducing agent useful as the constituent of a chemical amplified type resist composition used for production of semiconductor devices, etc., which comprises a compound containing in the molecule at least one structure in which at least one of the direct links of -NH- is directly bonded to at least one member selected from the group consisting of -C(=O)-, -C(=S)- and -SO 2 -. When a resist composition containing said agent is used on a special substrate such as a TIN substrate or a BPSG substrate as a resist material for exposure to deep UV or KrF excimer laser beams, the resist composition can give a good profile of pattern of quarter micron order without causing footing, while retaining high resolution ability and high sensitivity.

Description: BACKGROUND OF THE INVENTION This invention relates to a method for reducing the substrate dependence of a chemical amplified type positive- or negative- working resist composition used for production of semiconductor devices, wherein said resist composition comprises a specific nitrogen-containing compound, a resist composition containing said specific nitrogen-containing compound and a pattern formation process using the resist composition. In place of a source of i-line light (365 nm), a KrF excimer laser having a shorter output wavelength of 248 nm have recently come to be used as a light source for exposure used in a lithography process because of a demand for ultramicrofabrication caused with an enhancement of the degree of integration of semiconductor devices. Consequently, conventional dissolution- inhibiting type resists which require exposure at several hundreds milli-joule have become unusable for, for example, the following reasons: no high energy can be obtained because the excimer laser is used in place of a mercury vapor lamp; and the resists strongly absorb light (namely, they are poor in transmittance) at 248 nm. Therefore, there have come to be used chemical amplified type resists which have a high transmittance even at 248 nm and permits pattern formation by exposure at several tens milli-joule. The chemical amplified type resists, however, tend to be affected by a substrate because they have a reaction mechanism in which a dissolution-inhibiting compound such as an alkali-insoluble compound or an alkali-insoluble polymer becomes alkali-soluble owing to exposure energy during pattern formation, i.e., a two-step reaction mechanism in which an acid is generated from a photosensitive compound, on account of the exposure energy, and a chemical reaction is caused by the generated acid, so that the alkali-insoluble compound or polymer becomes alkali- soluble. That is, the decrease of the exposure dose enhances the influence of a subtle difference of the exposure dose in the boundary surface portion of the substrate and the influence of a basic substance and water which are released from the substrate. Therefore, in device production using the chemical amplified type resist, it becomes impossible to attain a good profile of pattern by using a special substrate (e.g. TiN, BPSG, etc.) which has been extraordinary disadvantageous. Such substrate dependence is a serious problem. EP 0704762 discloses a photosensitive composition comprising a polymer capable of becoming alkali-soluble owing to the action of an acid, a compound capable of generating an acid upon irradiation, and acetamide. EP 0780732 (relevant under Art. 54(3) (4) EPC) discloses a specific resist composition comprising saccharine, succinimide and phthalimide as additives. However, none of these references discloses or suggests compounds having the effect of reducing the substrate dependence of a resist. For solving this problem, there have been proposed resist compositions containing an organic carboxylic acid (for example, JP-A 9-6001, JP-A 9-6002, JP-A 9-6003 and European Patent Laid- Open No. 679951), and it has been reported that the resist compositions improve a profile of pattern on a special substrate. These resist compositions containing an organic carboxylic acid, however, are disadvantageous in that since the organic carboxylic acid is utilized for causing a chemical reaction to reduce the substrate dependence, the resist compositions are strongly acidic and hence deteriorated in performance characteristics during storage. For alleviating this disadvantage, a basic compound should be added in an amount larger than that required for neutralizing the organic carboxylic acid, resulting in causing problems such as a sensitivity decrease, etc. Accordingly, there is desired the development of a highly sensitive resist composition which gives a pattern with an excellent profile even on a special substrate and has an excellent storage stability and a satisfactory throughput. SUMMARY OF THE INVENTION In view of such conditions, a problem to be solved by the present invention is to provide a resist composition which gives a fine pattern with a good profile even on a special substrate in pattern formation using the resist composition as a chemical amplified type positive- or negative- working resist composition, has an excellent storage stability, and makes it possible to form a pattern with high sensitivity. The present invention was made for solving the above problem and includes the following items: (1) A method for reducing the substrate dependence of a resist composition comprising (a) either (i) a polymer capable of becoming alkali-soluble owing to the action of an acid, or (ii) an alkali-soluble polymer and a compound capable of becoming alkali-soluble owing to the action of an acid or (iii) an alkali-soluble polymer and a compound capable of making the polymer difficultly alkali-soluble by crosslinking therewith owing to the action of an acid, (b) a compound capable of generating an acid upon irradiation with actinic radiation, and (c) a solvent capable of dissolving the above components, which method comprises incorporating into said composition a compound containing in the molecule at least one structure in which at least one of the direct links of -NH- is directly bonded to at least one member selected from -C(=O)-, -C(=S)- and -SO 2 -,said compound being a cyclic compound represented by the following formula [1], [2] or [3] : wherein X is an oxygen atom or a sulfur atom; and A is a saturated or unsaturated 5- or 6-membered ring which may contain an oxygen atom, a nitrogen atom or a sulfur atom as a constituent atom, and the carbon atoms constituting the ring may have a substituent; wherein X is an oxygen atom or a sulfur atom; D is a saturated or unsaturated 5- or 6-membered ring which may contain an oxygen atom, a nitrogen atom or a sulfur atom as a constituent atom, and the carbon atoms constituting the ring may have a substituent and the sulfur atom may have one or two oxo groups, and E is a saturated or unsaturated 6-membered ring or a fused ring polycyclic aromatic structure containing carbon atoms as constituent atoms, and a ring E is forming a fused ring with ring D; wherein G is a saturated or unsaturated 6- to 8-membered ring which may contain an oxygen atom as a constituent atom; and both J and L are independently a benzene ring, and the ring J and the ring L are independently forming a fused ring with the ring G; or an acyclic compound represented by the formula [21] or [22]: wherein X 1 and X 2 are independently a substituted or unsubstituted alkyl group or a phenyl group; n is an integer of 1 to 3; and X in a number of n are independently an oxygen atom or a sulfur atom; R 0 SO 2 NHR' wherein R 0 is a substituted or unsubstituted alkyl group or a substituted or unsubstituted aryl group; and R' is a hydrogen atom or an alkyl group. (2) The use of a compound containing in the molecule at least one structure in which at least one of the direct links of -NH- is directly bonded to at least one member selected from -C(=O)-, -C(=S)- and -SO 2 - as defined in (1) above as an agent for reducing the substrate dependence of a resist. (3) A resist composition comprising (a) a polymer capable of becoming alkali-soluble owing to the action of an acid, which is shown by the following formula [5] or [6]: wherein R and R 1 are independently a hydrogen atom or a lower alkyl group; R 2 and R 3 are independently a hydrogen atom, an alkyl group which may be substituted by one or more halogen atoms, or an aryl group, except for the case where both R 2 and R 3 are hydrogen atoms, and R 2 and R 3 may form together an alkylene ring; R 4 is an alkyl group which may be substituted by one or more halogen atoms, or an aralkyl group; R 5 is a cyano group, an esterified or non-esterified carboxyl group or a substituted or unsubstituted phenyl group; m and n' are independently a natural number; and k is zero or a natural number, provided that m > k; wherein R 6 is a hydrogen atom or a lower alkyl group; R 7 is a hydrogen atom, a lower alkyl group, a lower alkoxy group, an acyloxy group, a saturated heterocyclic oxy group, or a group represented by R 8 O-CO-(CH 2 )z-O- wherein R 8 is an alkyl group and z is zero or a naturalnumber; R 21 is a hydrogen atom or a lower alkyl group; R 22 is a cyano group, an esterified or non-esterified carboxyl group, or a substituted or unsubstituted phenyl group, provided that in the case of R 7 being a hydrogen atom or a lower alkyl group, R 22 is an alkoxy group, a 5- or 6-membered saturated heterocyclic group or a substituted phenyl group having as the substituent a group represented by R 25 O-CO-(CH 2 ) j O- wherein R 25 is a lower alkyl group and j is 0 or 1; p and r are independently a natural number; and f is zero or a natural number, provided that p > f; (b) a compound capable of generating an acid upon irradiation with actinic radiation; (c) a compound containing in the molecule at least one structure in which at least one of the direct links of -NH- is directly bonded to at least one member selected from -C(=O)-, -C(=S)- and -SO 2 - as defined in claims 1-8; and (d) a solvent capable of dissolving these three components, provided that when the compound of (c) is saccharin, succinimide or phthalimide, the composition does not contain both a polymer shown by the general formula [5] and a polymer shown by the general formula [6] whose alkali-solubilities are different from each other, and provided that when (b) is triphenylsulfonium trifluoromethanesulfonate and (c) is saccharin, then (a) is not a mixture of poly(p-1-ethoxyethoxystyrene/p-hydroxystyrene/p-tert-butoxycarbonyloxystyrene) having a Mw of 20,000 and a Mw/Mn of 1.90 and poly(p-1-ethoxyethoxystyrene/p-hydroxystyrene/p-isopropoxycarbonyloxystyrene) having a Mw of 8,300 and a Mw/Mn of 1.60. (4) A resist composition comprising an alkali-soluble polymer, a compound capable of becoming alkali-soluble owing to the action of an acid, a compound capable of generating an acid upon irradiation with actinic radiation which is not a quinonediazide, a compound containing in the molecule at least one structure in which at least one of the direct links of -NH- is directly bonded to at least one member selected from the group consisting of -C(=O)-, -C(=S)- and -SO 2 - as defined in (1) above and a solvent capable of dissolving these four components. (5) A resist composition comprising an alkali-soluble polymer, a compound capable of making the polymer difficultly alkali-soluble by crosslinking therewith owing to the action of an acid, a compound capable of generating an acid upon irradiation with actinic radiation which is not a quinonediazide, a compound containing in the molecule at least one structure in which at least one of the direct links of -NH- is directly bonded to at least one member selected from the group consisting of -C(=O)-, -C(=S)- and -SO 2 - as defined in (1) above, and a solvent capable of dissolving these four components. (6) A process for forming a pattern comprising a step of coating a semiconductor substrate with the resist composition of any one of claims 10-12, a step of heating the coating to form a resist film, a step of exposing the resist film to radiation through a mask; and a step of developing the resist film with an alkali developing solution after heating the same if necessary. BRIEF DESCRIPTION OF THE DRAWINGS Fig. 1 is a cross-sectional view of a contact hole with a good profile obtained by using a resist composition containing a present invention's compound. Fig. 2 is a cross-sectional view of a contact hole with an unsatisfactory profile obtained by using a resist composition containing no present invention's compound. Fig. 3 is cross-sectional view of a contact hole with an unsatisfactory profile obtained by using a resist composition of prior art after storage at 23 °C for 2 weeks. Fig. 4 is a cross-sectional view of a line-and-space pattern with a good profile obtained by using a resist composition containing the present invention's compound. Fig. 5 is a cross-sectional view of a line-and-space pattern with an unsatisfactory profile obtained by using a resist composition containing no present invention's compound. Fig. 6 is a cross-sectional view of a line-and-space pattern with an unsatisfactory profile obtained by using the resist composition of prior art after storage at 23 °C for 2 weeks. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS In order to obtain a chemical amplified type resist composition capable of giving a fine pattern with a good profile even on a special substrate, the present inventors earnestly investigated and consequently found that a compound containing in the molecule at least one structure in which at least one of the direct links of -NH- is directly bonded to at least one member selected from the group consisting of -C(=O)- , -C(=S)- and -SO 2 - is markedly effective in avoiding the problem of the substrate dependence of conventional resist materials (namely, said compound is very effective as an agent for reducing the substrate dependence) and that a resist composition comprising said compound can achieve the above object. Thus, the present invention has been accomplished. As the compound containing in the molecule at least one structure in which at least one of the direct links of -NH- is directly bonded to at least one member selected from the group consisting of -C(=O)- , -C(=S)- and -SO 2 - (hereinafter abbreviated as "compound"), there are cyclic compounds and acyclic compounds. As the cyclic compounds usable in the present invention (hereinafter abbreviated as "compounds C"), there can be exemplified by compounds represented by the following formula [1], [2] or [3]: wherein X is an oxygen atom or a sulfur atom; and A is a saturated or unsaturated 5- or 6-membered ring which may contain an oxygen atom, a nitrogen atom or a sulfur atom as a constituent atom, and the carbon atoms constituting the ring may have a substituent; wherein X is an oxygen atom or a sulfur atom; D is a saturated or unsaturated 5- or 6-membered ring which may contain an oxygen atom, a nitrogen atom or a sulfur atom as a constituent atom, and the carbon atoms constituting the ring may have a substituent and the sulfur atom may have one or two oxo groups; and E is a saturated or unsaturated 6-membered ring or a fused ring polycyclic aromatic structure containing carbon atoms as constituent atoms, and the ring E is forming a fused ring with the ring D; wherein G is a saturated or unsaturated 6- to 8-membered ring which may contain an oxygen atom as a constituent atom; and both J and L are independently a benzene ring, and the ring J and the ring L are independently forming a fused ring with the ring G. In the formula [1], A is a saturated or unsaturated 5- or 6-membered ring which may contain an oxygen atom, a nitrogen atom or a sulfur atom as a constituent atom in addition to the carbon atoms and the nitrogen atom. The carbon atoms constituting the ring may have a substituent. The substituent on the carbon atom includes an alkyl group, an oxo group and an oxyimino group. The alkyl group may be either linear or branched. Preferable examples thereof are alkyl groups of 1 to 6 carbon atoms, such as methyl, ethyl, n-propyl, isopropyl, n-butyl, isobutyl, tert-butyl, sec-butyl, n-pentyl, isopentyl, tert-pentyl, 1-methylpentyl, n-hexyl and isohexyl. In the formula [2], D is a saturated or unsaturated 5- or 6-membered ring which may contain an oxygen atom, a nitrogen atom or a sulfur atom as a constituent atom in addition to the carbon atom and the nitrogen atom. The carbon atoms constituting the ring may have a substituent. As the substituent on the carbon atom, there can be exemplified by an oxo group and a groups represented by the formula [4]: wherein Q is a hydrogen atom or an alkyl group. In the formula [4], the alkyl group represented by Q may be either linear or branched. Preferable examples thereof are alkyl groups of 1 to 6 carbon atoms, such as methyl, ethyl, n-propyl, isopropyl, n-butyl, isobutyl, tert-butyl, sec-butyl, n-pentyl, isopentyl, tert-pentyl, 1-methylpentyl, n-hexyl and isohexyl. The sulfur atom which constitutes the ring may have one or two oxo groups. As the saturated or unsaturated 6- membered ring comprising carbon atoms as constituent atoms which is represented by E, there can be exemplified by a benzene ring, a cyclohexane ring, a cyclohexene ring, and a cyclohexadiene ring. As the fused ring represented by E, there can be exemplified by a naphthalene ring and, an anthracene ring. In the formula [3], G is a saturated or unsaturated 6- to 8-membered ring which may contain an oxygen atom as a constituent atom in addition to the carbon atom and the nitrogen atom. The ring G forms a fused ring with each of the benzene rings represented by J and L, respectively, on different sides of the ring G. Specific examples of the compound C are compounds of the formula [1], including acid imide compounds derived from aliphatic dibasic acids, such as succinimide, maleimide and glutarimide, dimethadione, diethadione, rhodanine, hydantoin, uracil, dihydrouracil, 2,4-dioxohexahydro-1,3,5-triazine, parabanic acid, barbituric acid, alloxan, violuric acid, etc.; compounds of the formula [2], including acid imide compounds derived from aromatic dibasic acids, such as phthalimide, 1,2,3,6-tetrahydrophthalimide, 1,8-naphthalimide and 2,3-naphthalenedicarboximide, isatin, hydrocarbostyril, carbostyril, 1,4-benzoxazin-3-one, benzothiazin-3-one, oxinedole, 2-benzoxazolinone, 2-oxobenzo [c,d]indole, phthalimidine, 1-benzylphthalimidine, saccharin, and benzoylene urea; compounds of the formula [3], including 6 (5H)-phenanthridinone, dihydrodibenzoxazepinone and 5,6,11,12-tetrahydrodibenz[b,f] azocin-6-one ; compounds other than those represented by the formulae [1] to [3], including pyromellitic acid diimide and bentazone. Of these, especially preferable examples of compounds C are acid imide compounds such as succinimide and phthalimide, which can reduce the substrate dependence when added even in a small amount. As the acyclic compounds usable in the present invention, there can be exemplified by sulfonamide derivatives (hereinafter abbreviated as "compounds A") and compounds represented by the formula [21]: wherein X 1 and X 2 are independently a substituted or unsubstituted alkyl group or a phenyl group; n is an integer of 1 to 3; and X in a number of n are independently an oxygen atom or a sulfur atom (such compounds are hereinafter abbreviated as "compounds B") As the compound A, there can be exemplified by compounds represented by the formula R 0 SO 2 NHR' wherein R 0 is a substituted or unsubstituted alkyl group or a substituted or unsubstituted aryl group; and R' is a hydrogen atom or an alkyl group. In the formula R 0 SO 2 NHR', the alkyl group in the substituted or unsubstituted alkyl group represented by R 0 may be linear, branched or cyclic. Preferable examples thereof are alkyl groups of 1 to 6 carbon atoms, such as methyl, ethyl, n-propyl, isopropyl, cyclopropyl, n-butyl, isobutyl, tert-butyl, sec-butyl, n-pentyl, isopentyl, tert-pentyl, 1-methylpentyl, cyclopentyl, n-hexyl, isohexyl and cyclohexyl. The substituent of the alkyl group includes a hydroxyl group, a halogen atom (e.g. chlorine, bromine, fluorine, iodine) and an alkoxy group. The alkoxy group may be either linear or branched. Preferable examples thereof are alkoxy groups of 1 to 6 carbon atoms, such as methoxy, ethoxy, n-propoxy, isopropoxy, n-butoxy, isobutoxy, tert-butoxy, sec-butoxy, n-pentyloxy, isopentyloxy, n-hexyloxy and isohexyloxy. The aryl group in the substituted or un substituted aryl group represented by R 0 include a phenyl group and a naphthyl group. The substituent of the aryl group includes a hydroxyl group, a halogen atom (e.g. chlorine, bromine, fluorine, iodine), an alkyl group and an alkoxy group. The alkyl group may be linear, branched or cyclic. Preferable examples thereof are alkyl groups of 1 to 6 carbon atoms, such as methyl, ethyl, n-propyl, isopropyl, cyclopropyl, n-butyl, isobutyl, tert-butyl, sec-butyl, n-pentyl, isopentyl, tert-pentyl, 1-methylpentyl, cyclopentyl, n-hexyl, isohexyl and cyclohexyl. The alkoxy groups may be either linear or branched. Preferable examples thereof are alkoxy groups of 1 to 6 carbon atoms, such as methoxy, ethoxy, n-propoxy, isopropoxy, n-butoxy, isobutoxy, tert-butoxy, sec-butoxy, n-pentyloxy, isopentyloxy, n-hexyloxy and isohexyloxy. In the formula R 0 SO 2 NHR', the alkyl group represented by R' may be linear, branched or cyclic. Preferable examples thereof are alkyl groups of 1 to 6 carbon atoms, such as methyl, ethyl, n-propyl, isopropyl, cyclopropyl, n-butyl, isobutyl, tert-butyl, sec-butyl, n-pentyl, isopentyl, tert-pentyl, 1-methylpentyl, cyclopentyl, n-hexyl, isohexyl and cyclohexyl. In the formula [21], the alkyl group in the substituted or unsubstituted alkyl group represented by each of X and X 2 may be either linear or branched. Preferable examples thereof are alkyl groups of 1 to 10 carbon atoms, such as methyl, ethyl, n―propyl, isopropyl, n-butyl, isobutyl, tert-butyl, sec-butyl, n-pentyl, isopentyl, tert-pentyl, 1-methylpentyl, n-hexyl, isohexyl, heptyl, octyl, nonyl and decyl. The substituent of the alkyl group includes a halogen atom (e.g. chlorine, bromine, fluorine, iodine) and a nitro group. Specific examples of the compound of the formula R 0 SO 2 NHR' are sulfonamides such as methanesulfonamide, p- or m-toluenesulfonamide and benzenesulfonamide. Of these, especially preferable examples of said compound are p- or m-toluenesulfonamide and benzenesulfonamide . Specific examples of compound B are amides such as N-benzoylbenzamide and diacetamide; diacylurea derivatives such as diacetylurea, dipropionylurea and dibenzoylurea; and diacylthiourea derivatives such as diacetylthiourea, dipropionylthiourea and dibenzoylthiourea. Of these, especially preferable examples of the present invention's compound B are the amides such as N-benzoylbenzamide and diacetamide, which can reduce the substrate dependence when added even in a small amount. The specific nitrogen-containing compounds are used singly or in proper combination of two or more thereof. As the polymer capable of becoming alkali-soluble owing to the action of an acid which is used in the present invention, there can be exemplified by compounds represented by the following formula [5] or [6]: wherein R and R 1 are independently a hydrogen atom or a lower alkyl group; R 2 and R 3 are independently a hydrogen atom, an alkyl group which may be substituted by one or more halogen atoms, or an aryl group, except for the case where both R 2 and R 3 are hydrogen atoms, and R 2 and R 3 may form together an alkylene ring; R 4 is a an alkyl group which may be substituted by one or more halogen atoms, or an aralkyl group; R 5 is a cyano group, an esterified or non-esterified carboxyl group or a substituted or unsubstituted phenyl group; m and n' are independently a natural number; and k is zero or a natural number, provided that m > k. wherein R 6 is a hydrogen atom or a lower alkyl group; R 7 is a hydrogen atom, a lower alkyl group, a lower alkoxy group, an acyloxy group, a saturated heterocyclic oxy group, or a group represented by R 8 O-CO-(CH 2 )z-O- wherein R 8 is an alkyl group and z is zero or a natural number; R 21 is a hydrogen atom or a lower alkyl group; R 22 is a cyano group, an esterified or non-esterified carboxyl group, or a substituted or unsubstituted phenyl group, provided that in the case of R 7 being a hydrogen atom or a lower alkyl group, R 22 is an alkoxy group, a 5- or 6-membered saturated heterocyclic group or a substituted phenyl group having as the substituent a group represented by R 25 O-CO-(CH 2 )jO- wherein R 25 is a lower alkyl group and j is 0 or 1; p and r are independently a natural number; and f is zero or a natural number, provided that p > f. The lower alkyl group represented by each of R and R 1 in the formula [5] and the lower alkyl group represented by each of R 6 and R 21 in the formula [6] independently may be either linear or branched and include alkyl groups of 1 to 6 carbon atoms, such as methyl, ethyl, n-propyl, isopropyl, n-butyl, isobutyl, tert-butyl, sec-butyl, n-pentyl, isopentyl, tert-pentyl, 1-methylpentyl, n-hexyl and isohexyl. The alkyl group which may be substituted by one or more halogen atoms, represented by each of R 2 , R 3 and R 4 in the formula [5], may be linear, branched or cyclic. Preferable examples thereof are alkyl groups of 1 to 10 carbon atoms, such as methyl, ethyl, n-propyl, isopropyl, cyclopropyl, n-butyl, isobutyl, tert-butyl, sec-butyl, n-pentyl, isopentyl, tert-pentyl, 1-methylpentyl, cyclopentyl, n-hexyl, isohexyl, cyclohexyl, heptyl, octyl, nonyl and decyl. The halogen atom (s) in the alkyl group represented by each of R 2 , R 3 and R 4 includes chlorine, bromine, fluorine and iodine. Preferable examples of the alkylene ring which R 2 and R 3 may form together are an alkylene ring having 3 to 6 carbon atoms, such as a propylene ring, a butylene ring, a pentylene ring and a hexylene ring. The aralkyl group represented by R 4 includes, for example, a benzyl group, a phenethyl group, a phenylpropyl group, a methylbenzyl group, a methylphenethyl group and an ethylbenzyl group . In the formula [5], the esterified or non-esterified carboxyl group represented by R 5 includes a carboxyl group and a substituted carboxyl group having, for example, an alkyl group of 1 to 6 carbon atoms as the substituent for the hydrogen atom, such as a methyloxycarbonyl group, an ethyloxycarbonyl group, a propyloxycarbonyl group, a butyloxycarbonyl group, a pentyloxycarbonyl group and a hexyloxycarbonyl group. The substituent of the substituted or unsubstituted phenyl group represented by R 5 includes, for example, halogen atoms such as chlorine, bromine, fluorine, iodine, linear, branched or cyclic alkyl groups of preferably 1 to 10 carbon atoms, such as methyl, ethyl, n-propyl, isopropyl, cyclopropyl, n-butyl, isobutyl, tert-butyl, sec-butyl, n-pentyl, isopentyl, tert-pentyl, 1-methylpentyl, cyclopentyl, n-hexyl, isohexyl, cyclohexyl, heptyl, octyl, nonyl and decyl; linear or branched alkoxy groups of preferably 1 to 6 carbon atoms, such as methoxy, ethoxy, n-propoxy, isopropoxy, n-butoxy, isobutoxy, tert-butoxy, sec-butoxy, n-pentyloxy, isopentyloxy, n-hexyloxy and isohexyloxy; linear, branched or cyclic acyl groups of 2 to 7 carbon atoms derived from carboxylic acids, such as acetyl, propionyl, n-butyryl, isobutyryl, n-pentanoyl, pivaloly, isovaleryl and cyclohexanecarbonyl; 5- to 6-membered saturated heterocyclic oxy groups such as tetrahydrofuranyloxy and tetrahydropyranyloxy; and groups represented by R 26 O-CO-(CH 2 )jO- wherein R 25 and j are as defined above. In this formula, the lower alkyl group represented by R 25 may be liner, branched or cyclic and includes alkyl groups of 1 to 6 carbon atoms, such as methyl, ethyl, n-propyl, isopropyl, cyclopropyl, n-butyl, isobutyl, tert-butyl, sec-butyl, cyclobutyl, n-pentyl, isopentyl, tert-pnetyl, 1-methylpentyl, cyclopentyl, n-hexyl, isohexyl and cyclohexyl. Specific examples of the groups represented by R 25 O-CO-(CH 2 )jO- are a methyloxycarbonyloxy group, an ethyloxycarbonyloxy group, an isopropyloxycarbonyloxy group, a tert-butyloxycarbonyloxy group, an isobutyloxycarbonyloxy group, a tert-pentyloxycarbonyloxy group, an ethyloxycarbonylmethyloxy group, a tert-butyloxycarbonylmethyloxy group, a 1-methylcyclopentyloxycarbonylmethyloxy group and a 1-methylcyclohexyloxycarbonylmethyloxy group. In the formula [6], preferable examples of the lower alkyl group represented by R are linear or branched alkyl groups of 1 to 6 carbon atoms. Specific preferable examples thereof are an isopropyl group, an isobutyl group, a tert-butyl group, a sec-butyl group, an isopentyl group, a tert-pentyl group, a 1-methylpentyl group and an isohexyl group. Preferable examples of the lower alkoxy group represented by R 7 are linear or branched alkoxy groups of 1 to 6 carbon atoms, such as methoxy, ethoxy, n-propoxy, isopropoxy, n-butoxy, isobutoxy, tert-butoxy, sec-butoxy, n-pentyloxy, isopentyloxy, n-hexyloxy and isohexyloxy. Preferable examples of the acyloxy group represented by R 7 are linear, branched or cyclic acyloxy groups of 2 to 7 carbon atoms derived from carboxylic acids, such as acetyloxy, propionyloxy, n-butyryloxy, isobutyryloxy, n-pentanoyloxy, pivaloyloxy, isovaleryloxy and cyclohexanecarbonyloxy. The saturated heterocyclic oxy group represented by R 7 is preferably a 5- or 6-membered one and includes, for example, tetrahydrofuranyloxy group and tetrahydropyranyloxy group. As R 8 of the R 8 O-CO-(CH 2 )z-O- group represented by R 7 , there can be exemplified by a linear, branched or cyclic alkyl groups of 1 to 10 carbon atoms, such as methyl, ethyl, n-propyl, isopropyl, cyclopropyl, n-butyl, isobutyl, tert-butyl, sec-butyl, n-pentyl, isopentyl, 1-methylcyclohexyl, tert-pentyl, 1-methylpentyl, cyclopentyl, n-hexyl, isohexyl, cyclohexyl, heptyl, octyl, nonyl and decyl. Specific examples of the R 8 O-CO-(CH 2 )z -O- group are a methyloxycarbonyloxy group, an ethyloxycarbonyloxy group, an isopropyloxycarbonyloxy group, an isobutyloxycarbonyloxy group, a tert-butyloxycarbonyloxy group, a tert-pentyloxycarbonyloxy group, a 1-methylcyclohexyloxycarbonylmethyloxy group, a tert-butyloxycarbonylmethyloxy group and a 1-methylcyclopentyloxycarbonylmethyloxy group. In the formula [6], the esterified or non-esterified carboxyl group represented by R 22 includes a carboxyl group and a substituted carboxyl groups having, for example, an alkyl group of 1 to 6 carbon atoms as the substituent for the hydrogen atom, such as a methyloxycarbonyl group, an ethyloxycarbonyl group, a propyloxycarbonyl group, a butyloxycarbonyl group, a pentyloxycarbonyl group and a hexyloxycarbonyl group. The substituent of the substituted or unsubstituted phenyl group represented by R 22 includes, for example, halogen atoms such as chlorine, bromine, fluorine and iodine; linear, branched or cyclic alkyl groups of preferably 1 to 10 carbon atoms, such as methyl, ethyl, n-propyl, isopropyl, cyclopropyl, n-butyl, isobutyl, tert-butyl, sec-butyl, n-pentyl, isopentyl, tert- pentyl, 1- methylpentyl, cyclopentyl, n- hexyl, isohexyl, cyclohexyl, heptyl, octyl, nonyl and decyl; linear or branched alkoxy groups of preferably 1 to 6 carbon atoms, such as methoxy, ethoxy, n-propoxy, isopropoxy, n-butoxy, isobutoxy, tert-butoxy, sec-butoxy, n-pentyloxy, isopentyloxy, n-hexyloxy and isohexyloxy; linear, branched or cyclic acyl groups of 2 to 7 carbon atoms derived from carboxylic acids, such as acetyl, propionyl, n-butyryl, isobutyryl, n-pentanoyl, pivaloly, isovaleryl and cyclohexanecarbonyl; 5- to 6- membered saturated heterocyclic oxy groups such as tetrahydrofuranyloxy and tetrahydropyranyloxy; and groups represented by R 25 O-CO- (CH 2 )jO- wherein R 25 and j are as defined above. R 22 may be any of cyano group, the esterified or non- esterified carboxyl group or the substituted or unsubstituted phenyl group, though when R 7 is a hydrogen atom or a lower alkyl group, R 22 is an alkoxy group, a 5- or 6-membered saturated heterocyclic group or a substituted phenyl group having as the substituent a group represented by R 25 O-CO- (CH 2 )jO- wherein R 25 is a lower alkyl group and j is 0 or 1. Specific examples of the compound of the formula [5] are poly[p-(1-methoxy-1-methylethoxy)-styrene/p-hydroxystyrene], poly[p-(1-benzyloxy-1-methylethoxy)styrene/p-hydroxystyrene], poly[p-(1-ethoxyethoxy)styrene/p-hydroxystyrene],poly[p-(1-methoxyethoxystyrene)/p-hydroxystyrene],poly[p-1-n-butoxyethoxystyrene/p-hydroxystyrene], poly[p-(1,1-dimethylethoxy)-1-methylethoxystyrene/p-hydroxystyrene], poly[p-(1-methoxy-1-methylethoxy)styrene/p-hydroxystyrene/styrene], poly[p-(1-methoxy-1-methylethoxy)styrene/p-hydroxystyrene/p-chlorostyrene], poly[p-(1-methoxy-1-methylethoxy)styrene/p-hydroxystyrene/p-methylstyrene], poly[p-(1-methoxy-1-methylethoxy)styrene/p-hydroxystyrene/p-methoxystyrene], poly[p-(1-methoxy-1-methylethoxy)styrene/p-hydroxystyrene/p-tert-butoxystyrene], poly[p-(1-methoxy-1-methylethoxy)styrene/p-hydroxystyrene/p-1-methylcyclohexyloxystyrene],poly[p-(1-methoxy-1-methylethoxy)styrene/p-hydroxystyrene/methylmethacrylate],poly[p-(1-methoxy-1-methylethoxy)styrene/p-hydroxystyrene/t-butylmethacrylate],poly[p-(1-methoxy-1-methylethoxy)styrene/p-hydroxystyrene/acrylonitrile],poly[p-(1-benzyloxy-1-methylethoxy)styrene/p-hydroxystyrene/styrene],poly[p-(1-benzyloxy-1-methylethoxy)styrene/p-hydroxystyrene/p-chlorostyrene],poly[p-(1-benzyloxy-1-methylethoxy)styrene/p-hydroxystyrene/p-methylstyrene],poly[p-(1-benzyloxy-1-methylethoxy)styrene/p-hydroxystyrene/p-ethoxystyrene],poly[p-(1-benzyloxy-1-methylethoxy)styrene/p-hydroxystyrene/p-tert-butoxystyrene],poly(p-1-ethoxyethoxystyrene/p-hydroxystyrene/styrene),poly(p-1-ethoxyethoxystyrene/p-hydroxystyrene/p-chlorostyrene),poly(p-1-ethoxyethoxystyrene/p-hydroxystyrene/p-methylstyrene), poly(p-1-ethoxyethoxystyrene/p-hydroxystyrene/m-methylstyrene), poly(p-1-ethoxyethoxystyrene/p-hydroxystyrene/methylmethacrylate), poly(p-1-ethoxyethoxystyrene/p-hydroxystyrene/cyclohexylmethacrylate), poly(p-1-ethoxyethoxystyrene/p-hydroxystyrene/tert-butylmethacrylate), poly(p-1-ethoxyethoxystyrene/p-hydroxystyrene/acrylonitrile), poly(p-1-ethoxyethoxystyrene/p-hydroxystyrene/p-methoxystyrene), poly(p-1-ethoxyethoxystyrene/p-hydroxystyrene/p-ethoxystyrene), poly(p-1-ethoxyethoxystyrene/p-hydroxystyrene/p-tert-butoxystyrene), poly(p-1-ethoxyethoxystyrene/p-hydroxystyrene/acrylicacid), poly(p-1-ethoxyethoxystyrene/p-hydroxystyrene/p-methoxycarbonyloxystyrene), poly(p-1-ethoxyethoxystyrene/p-hydroxystyrene/p-ethoxycarbonyloxystyrene), poly(p-1-ethoxyethoxystyrene/p-hydroxystyrene/p-isopropoxycarbonyloxystyrene), poly(p-1-methoxyethoxystyrene/p-hydroxystyrene/p-isobutyloxycarbonyloxystyrene), poly(p-1-ethoxyethoxystyrene/p-hydroxystyrene/p-isobutoxycarbonyloxystyrene), poly(p-1-ethoxyethoxystyrene/p-hydroxystyrene/p-isoamyloxycarbonyloxystyrene), poly(p-1-ethoxyethoxystyrene/p-hydroxystyrene/p-1-methylcyclohexyloxystyrene), poly(p-1-methoxyethoxystyrene/p-hydroxystyrene/styrene), poly(p-1-methoxyetlloxystyrene/p-hydroxystyrenelp-methylstyrene), poly(p-1-methoxyethoxystyrene/p-hydroxystyrene/m-methylstyrene), poly(p-1-methoxyethoxystyrene/p-hydroxystyrene/p-chlorostyrene), poly(p-1-methoxyethoxystyrene/p-hydroxystyrene/p-methoxystyrene), poly(p-1-methoxyethoxystyrene/p-hydroxystyrenelp-ethoxystyrene), poly(p-1-methoxyethoxystyrene/p-hydroxystyrene/p-tert-butoxystyrene), poly(p-1-methoxyethoxystyrene/p-hydroxystyrene/p-1-methylcyclohexyloxystyrene), poly(p-1-methoxyethoxystyrene/p-hydroxystyrene/methylmethacrylate), poly(p-1-methoxyethoxystyrene/p-hydroxystyrene/tert-butylmethacrylate), poly(p-1-methoxyethoxystyrene/p-hydroxystyrene/acrylonitrile), poly(p-1-n-butoxyethoxystyrene/p-hydroxystyrene/p-n-butylstyrene), poly(p-1-isobutoxyethoxystyrene/p-hydroxystyrene/o-methoxystyrene), poly{p-[(1,1-dimethylethoxy)-1-methylethoxy]styrene/p-hydroxystyrene/m-methoxystyrene},poly[p-(1,1-dimethylethoxy)-1-methylethoxystyrene/p-hydroxystyrene/o-methylstyrene],poly(p-1-ethoxyethoxystyrene/p-hydroxystyrene/p-acetoxystyrene),poly(p-1-ethoxyethoxystyrene/p-hydroxystyrene/p-pivaloyloxystyrene),poly(p-1-ethoxyethoxystyrene/p-hydroxystyrene/p-cyclohexanecarbonyloxystyrene),poly[m-1-(2-chloroethoxy)-ethoxystyrene/m-hydroxystyrene/styrene],poly[m-1-(2-ethylhexyloxy)ethoxystyrene/m-hydroxystyrene/m-methylstyrene],poly[p-(1-methoxy-1-methylethoxy-α-methylstyrene/p-hydroxy-α-methylstyrene/styrene],poly[p-(1-ethoxy-1-methylethoxy)styrene/p-hydroxystyrene/p-methylstyrene], poly(p-1-n-propoxyethoxystyrene/p-hydroxystyrene/p-methoxystyrene), poly[p-(1-methyl-1-n-propoxyethoxy)styrene/p-hydroxystyrene/p-methylstyrene], poly(m-1-ethoxypropoxystyrene/m-hydroxystyrene/m-tert-butoxystyrene), poly(m-1-ethoxypropoxystyrene/m-hydroxystyrene/p-methylstyrene), poly[m-(1-methoxy-1-methylethoxy)styrene/m-hydroxystyrene/m-tert-butoxystyrene],poly[p-1-ethoxyethoxystyrene/p-hydroxystyrene/p-tetrahydrfuranyloxystyrene],poly[p-1-ethoxyethoxystyrene/p-hydroxystyrene/p-tetrahydro-pyranyloxystyrene],poly[p-1-methoxyethoxystyrene/p-hydroxystyrene/p-tetrahydropyranyloxystyrene],poly[p-1-ethoxyethoxystyrene/p-hydroxystyrene/p-tert-butoxycarbonyloxystyrene],poly[p-1-methoxyethoxystyrene/p-hydroxystyrene/p-tert-butoxycarbonyloxystyrene],poly[p-(1-methoxy-1-methylethoxy)styrene/p-hydroxystyrene/p-tert-butoxycarbonyloxystyrene],poly(p-1-ethoxyethoxystyrene/p-hydroxystyrene/tert-butylp-vinylphenoxyacetate),poly(p-1-methoxyethoxystyrene/p-hydroxystyrene/tert-butylp-vinylphenoxyacetate),poly(p-1-methoxyethoxystyrene/p-hydroxystyrene/1-methylcyclohexylp-vinylphenoxyacetate), poly[m-1-ethoxyethoxystyrene/m-hydroxystyrene/m-tert-butoxycarbonyloxystyrene], poly(m-1-ethoxyethoxystyrene/m-hydroxystyrene/m-tert-butoxystyrene), poly(m-1-methoxyethoxystyrene/m-hydroxystyrene/m-tert-butoxystyrene),poly(p-1-ethoxyethoxystyrene/m-1-ethoxyethoxystyrene/p-hydroxystyrene/m-hydroxystyrene/p-tert-butoxystyrene/m-tert-butoxystyrene),poly(p-1-methoxybutoxystyrene/p-hydroxystyrene/styrene). Specific examples of the compound of the formula [6] are poly(p-tert-butoxystyrene/p-hydroxystyrene),poly(1-methylcyclohexyloxystyrene/p-hydroxystyrene),poly(m-tert-butoxystyrene/m-hydroxystyrene), poly(p-methoxycarbonyloarystyrene/p-hydroxystyrene),poly(p-ethoxycarbonyloxystyrene/p-hydroxystyrene),poly(p-isopropoxycarbonyloxystyrene/p-hydroxystyrene), poly(p-isobutoxycarbonyloxystyrene/p-hydroxystyrene), poly(m-isobutoxycarbonyloxystyrene/m-hydroxystyrene), poly(p-tert-butoxycarbonyloxystyrene/p-hydroxystyrene), poly(m-tert-butoxycarbonyloxystyrene/p-hydroxystyrene), poly(p-isoamyloxycarbonyloxystyrene/p-hydroxystyrene), poly(m-isoamyloxycarbonyloxystyrene/m-hydroxystyrene), poly(p-tert-amyloxycarbonyloxystyrene/p-hydroxystyrene), poly(p-acetyloxystyrene/p-hydroxystyrene),poly(p-isobutyroyloxystyrene/p-hydroxystyrene),poly(p-pivaloyloxystyrene/p-hydroxystyrene), poly(p-cyclohexanecarbonyloxystyrene/p-hydroxystyrene), poly(p-sec-butoxycarbonyloxystyrene/p-hydroxystyrene), poly(p-tetrahydrofuranyloxystyrene/p-hydroxystyrene), poly(p-tetrahydropyranyloxystyrene/p-hydroxystyrene) poly(m-tetrahydropyranyloxystyrene/m-hydroxystyrene), poly(tert-butylp-vinylphenoxyacetate/p-hydroxystyrene), poly(1-methylcyclohexylp-vinylphenoxyacetate/p-hydroxystyrene), poly(styrene/p-hydroxystyrene/p-1-methoxyethoxystyrene),poly(p-methylstyrene/p-hydroxystyrene/p-1-methoxyethoxystyrene),poly(p-methoxystyrene/p-hydroxystyrene/p-1-methoxyethoxystyrene),poly(p-methylstyrene/p-hydroxystyrene/p-1-ethoxyethoxystyrene), poly (m-methylstyrene/p-hydroxystyrene/p-1-ethoxyethoxystyrene), poly (p-methoxystyrene/p-hydroxystyrene/p-1-ethoxyethoxystyrene), poly (p-tert-butylstyrene/p-hydroxystyrene/p-1-ethoxyethoxystyrene), poly (p-tert-butoxystyrene/p-hydroxystyrene/p-1-ethoxyethoxystyrene), poly (styrene/p-hydroxystyrene/p-1-methoxy-1-methylethoxystyrene), poly (p-methylstyrene/p-hydroxystyrene/p-1-methoxy-1-methylethoxystyrene), poly (p-methoxystyrene/p-hydroxystyrene/p-methoxy-1-methylethoxystyrene), poly (p-tert-butylstyrene/p-hydroxystyrene/p-methoxy-1-methylethoxystyrene), poly (p-tert-butoxystyrene/p-hydroxystyrene/p-1-methoxy-1-methylethoxystyrene), poly (styrene/p-hydroxystyrene/p-1-benzyloxyethoxystyrene), poly (p-methylstyrene/p-hydroxystyrene/p-1-benzyloxyethoxystyrene), poly (p-methoxystyrene/p-hydroxystyrene/p-1-benzyloxyethoxystyrene), poly (p-tert-butylstyrene/p-hydroxystyrene/p-1-benzyloxyethoxystyrene), poly (p-tert-butoxystyrene/p-hydroxystyrene/p-1-benzyloxyethoxystyrene), poly (p-ethoxycarbonyloxystyrene/p-hydroxystyrene/p-1-methoxyethoxystyrene), poly (p-ethoxycarbonyloxystyrene/p-hydroxystyrene/p-1-ethoxyethoxystyrene), poly (p-ethoxycarbonyloxystyrene/p-hydroxystyrene/p-1-methoxy-1-methylethoxystyrene), poly (p-tert-butoxycarbonyloxystyrene/p-hydroxystyrene/p-1-methoxyethoxystyrene), poly (p-tert-butoxycarbonyloxystyrene/p-hydroxystyrene/p-1-ethoxyethoxystyrene), poly (p-tert-butoxycarbonyloxystyrene/p-hydroxystyrene/p-1-methoxy-1-methylethoxystyrene), poly (p-tert-butoxycarbonyloxystyrene/p-hydroxystyrene/p-1-benzyloxyethoxystyrene), poly (p-acetyloxystyrene/p-hydroxystyrene/p-1-ethoxyethoxystyrene), poly (p-tetrahydropyranyloxystyrene/p-hydroxystyrene/p-1-methoxyethoxystyrene), poly (p-tetrahydropyranyloxystyrene/p-hydroxystyrene/p-1-ethoxyethoxystyrene), poly (p-tetrahydropyranyloxystyrene/p-hydroxystyrene/p-1-methoxy-1-methylethoxystyrene), poly (1-methylcyclohexyl p-vinylphenoxyacetate/p-hydroxystyrene/p-1-methoxyethoxystyrene), poly (1-methylcyclohexyl p-vinylphenoxyacetate/p-hydroxystyrene/p-1-ethoxyethoxystyrene), poly (1-methylcyclohexyl p-vinylphenoxyacetate/p-hydroxystyrene/p-1-methoxy-1-methylethoxystyrene) . The alkali-soluble polymer used in the present invention includes, for example, poly (p-hydroxystyrene), poly (m-hydroxystyrene), poly (3-methyl-4-hydroxystyrene), poly (p-tert-butoxystyrene/p-hydroxystyrene) [the number ratio of p-tert-butoxystyrene units to p-hydroxystyrene units is limited to 2 or less : 8 or more (such a ratio is hereinafter represented by 2 ↓ : 8 ↑)], poly (p-1-ethoxyethoxystyrene/p-hydroxystyrene) [the ratio of p-1-ethoxyethoxystyrene units to p-hydroxystyrene units is limited to 2 ↓ : 8 ↑], poly (p-tert-butoxycarbonyloxy-styrene/p-hydroxystyrene) [the ratio of p-tert-butoxy-carbonyloxystyrene units to p-hydroxystyrene units is limited to 2 ↓ : 8 ↑ ], poly (p-1-ethoxyethoxystyrene/p-tert-butoxystyrene/p-hydroxystyrene) the ratio of the sum of p-1-ethoxyethoxystyrene units and p-tert-butoxystyrene units to p-hydroxystyrene units is limited to 2 ↓ : 8 ↑ ], poly (p-1-ethoxyethoxystyrene/styrene/p-hydroxystyrene) [the ratio of the sum of p-1-ethoxyethoxystyrene units and styrene units to p-hydroxystyreneunits is limited to 2 ↓ : 8 ↑ ]. The compound capable of becoming alkali-soluble owing to the action of an acid which is used in the present invention includes, for example, alkali-insoluble compounds obtained by protecting at least a part or all of the phenolic hydroxyl group of an alkali-soluble compound with one or more of a tert-butoxycarbonyl group, a tert-butyl group, a 1-methoxyethyl group, a 1-ethoxyethyl group, a tetrahydropyranyl group, or a 1-methylcyclohexyloxycarbonylmethyl group. Specific examples thereof are 2,2-bis (4-tert-butyloxycarbonyloxyphenyl) propane, 2,2-bis (4-tert-butyloxyphenyl) propane, 2,2-bis (tetrahydropyranyloxyphenyl) propane, 2,2-bis [4-(1-methoxyethoxy) phenyl] propane, 2,2-bits [4-(1-ethoxyethyloxy) phenyl] propane, 2,2-bis [4-(1-methylcyclohexyloxycarbonylmethyloxy) phenylpropane], 1,1,2-tris (4-tert-butoxyphenyl) -2-methylpropane, 1,1,2-tris[4-(1-ethoxyethoxy)phenyl]-2-methylpropane and 1,1,2-tris (tert-butyloxycarbonyloxyphenyl)-2-methylpropane . As the compound capable of making the polymer hardly alkali-soluble by crosslinking therewith owing to the action of an acid which is used in the present invention, there can be exemplified by compounds represented by the formula [7]: wherein R 36 is an alkyl group; and R 37 is a hydrogen atom or a group represented by the formula [8]: -OCH 2 OR 36 wherein R 36 is as defined above, and compounds represented by the formula [9]: wherein R 38 is a hydrogen atom or an alkyl group; and R 39 is a hydrogen atom or a group represented by the formula [10]: wherein R 38 is as defined above. The alkyl group represented by R 36 in each of the formulae [7] and [8] and the alkyl group represented by R 38 in each of the formulae [9] and [10] may be linear, branched or cyclic. Preferable examples of each alkyl group are alkyl groups of 1 to 6 carbon atoms, such as methyl, ethyl, n-propyl, isopropyl, cyclopropyl, n-butyl, isobutyl, tert-butyl, sec-butyl, n-pentyl, isopentyl, tert-pentyl, 1-methylpentyl, cyclopentyl, n-hexyl, isohexyl and cyclohexyl. Specific examples of the compound capable of making the polymer hardly alkali-soluble by cross-linking therewith owing to the action of an acid are 1,2,4-tris (cyclohexyloxymethoxy)benzene, 1,2,4-tris (isobutoxymethoxy)benzene, 1,2,4-tris (isopropoxymethoxy) benzene, 1,3,5-tris (cyclohexyloxymethoxy) benzene, 1,3,5-tris (isobutoxymethoxy) benzene, 1,3,5-tris (isopropoxymethoxy) benzene, 1,3-bis (cyclohexyloxymethoxy)benzene, 1,3-bis (isobutoxymethoxy)benzene, 1,3-bis (isopropoxymethoxy) benzene, 1,4-bis (cyclohexyloxymethoxy) benzene, 1,4-bis (isobutoxymethoxy)benzene, 1,4-bis (isopropoxymethoxy)benzene, 2,4,6-tris (N,N-dimethoxymethylamino)-1,3,5-triazine, 2,4-bis (N,N-dimethoxymethylamino) -1,3,5-triazine. The polymer capable of becoming alkali-soluble owing to the action of an acid, or the alkali-soluble polymer, which is used in the present invention, can be obtained by preparing a polymer by radical polymerization using an organic peroxide or an azo compound as a polymerization initiator or living polymerization using n-butyllithium or potassium naphthalenide, and subjecting the prepared polymer to a chemical reaction if necessary. The polymer capable of becoming alkali-soluble or the alkali-soluble polymer can easily be obtained, for example, by any of the processes disclosed in JP-A 4-211258 and JP-A 5-194472. The weight-average molecular weight (Mw) of the polymer capable of becoming alkali-soluble owing to the action of an acid, or the alkali-soluble polymer, which is used in the present invention, is usually 3,000 to 50,000, preferably 5,000 to 30,000, as determined by a GPC method using a polystyrene as a standard. The dispersity (the ratio of weight-average molecular weight to number-average molecular weight) of the polymer is usually 1.00 to 3.00, preferably 1.02 to 2.00. The polymer capable of becoming alkali-soluble owing to the action of an acid which is used in the present invention can easily be obtained, for example, by the process disclosed in JP-A 4-88348. The compound capable of making the polymer hardly alkali-soluble by crosslinking therewith owing to the action of an acid which is used in the present invention can easily be obtained, for example, by the process disclosed in JP-A 6-83055. As the acid generator used in the present invention, any acid generator may be used so long as it can generate an acid upon irradiation with actinic radiation and has no undesirable influence on the formation of a resist pattern. Especially preferable examples thereof are acid generators whose light transmittance near 248.4 nm is sufficiently high to maintain the high transparency of the resist material, or is sufficiently increased by light exposure to maintain the high transparency of the resist material. As such acid generators especially preferable in the present invention, there can be exemplified by compounds represented by the following formulae [11], [12], [14], [15], [16] and [18]: wherein R 9 and R 10 are independently an alkyl group or a haloalkyl group; and A' is a sulfonyl group or a carbonyl group. wherein R 11 is a hydrogen atom, a halogen atom, an alkyl group, an alkoxy group or a haloalkyl group; and R 12 is an alkyl group, a haloalkyl group or a group represented by the formula [13]: wherein R 13 is a hydrogen atom, a halogen atom, an alkyl group, an alkoxy group or a haloalkyl group; and q is zero or an integer of 1 to 3. wherein R 14 is a hydrogen atom, a halogen atom, an alkyl group or a trifluoromethyl group; and R 15 is an alkyl group, an aralkyl group, an alkoxy group, a phenyl group or a tolyl group. wherein R 16 is an alkyl group, an unsubstituted phenyl group, a substituted phenyl group or an aralkyl group; R 17 and R 18 are independently a hydrogen atom, an alkyl group, an unsubstituted phenyl group, a substituted phenyl group or an aralkyl group; and R 19 is a fluoroalkyl group, a trifluoromethylphenyl group, a methyl group or a tolyl group. wherein R 29 is an alkyl group, a fluoroalkyl group, an unsubstituted phenyl group, a substituted phenyl group or an aralkyl group; Q 'is a sulfonyl group or a carbonyl group; R 30 and R 31 are independently a hydrogen atom, a methyl group, a methoxy group, a nitro group, a cyano group, a hydroxyl group or a group represented by the formula [17]: R 33 -Q'-O- wherein R 33 is an alkyl group, a fluoroalkyl group, an unsubstituted phenyl group, a substituted phenyl group or an aralkyl group, and Q' is a sulfonyl group or a carbonyl group; and R 32 is a hydrogen atom, a methyl group or an ethyl group. wherein R 34 is an alkyl group, a fluoroalkyl group, an unsubstituted phenyl group, a substituted phenyl group or an aralkyl group; and R 35 is a hydrogen atom, a methyl group, a fluoroalkyl group, a methoxy group, a nitro group, a cyano group, a hydroxyl group or a group represented by the above mentioned formula [17]. In the formula [11], the alkyl group represented by each of R 9 and R 10 or the alkyl group of the haloalkyl group represented by each of R 9 and R 10 may be linear, branched or cyclic. Preferable examples of each alkyl group are alkyl groups of 1 to 10 carbon atoms, such as methyl, ethyl, n-propyl, isopropyl, cyclopropyl, n-butyl, isobutyl, tert-butyl, sec-butyl, n-pentyl, isopentyl, tert-pentyl, 1-methylpentyl, cyclopentyl, n-hexyl, isohexyl, cyclohexyl, heptyl, octyl, nonyl and decyl. The halogen of the haloalkyl group includes chlorine, bromine, fluorine, iodine, etc. In the formula [12], the alkyl group represented by R 11 or the alkyl group of the haloalkyl group represented by R 11 may be either linear or branched. Preferable examples of each alkyl group are alkyl groups of 1 to 5 carbon atoms, such as methyl, ethyl, n-propyl, isopropyl, n-butyl, isobutyl, tert-butyl, sec-butyl, n-pentyl, isopentyl, tert-pentyl and 1-methylpentyl. The halogen atom represented by R 11 or the halogen of the haloalkyl group represented by R 11 includes chlorine, bromine, fluorine and iodine. The alkoxy group represented by R 11 may be either linear or branched. Preferable examples thereof are alkoxy groups of 1 to 5 carbon atoms, such as methoxy, ethoxy, n-propoxy, isopropoxy, n-butoxy, isobutoxy, tert-butoxy, sec-butoxy, n-pentyloxy and isopentyloxy. The alkyl group represented by R 12 or the alkyl group of the haloalkyl group represented by R 12 may be linear, branched or cyclic. Preferable examples of each alkyl group are alkyl groups of 1 to 10 carbon atoms, such as methyl, ethyl, n-propyl, isopropyl, cyclopropyl, n-butyl, isobutyl, tert-butyl, sec-butyl, n-pentyl, isopentyl, tert-pentyl, 1-methylpentyl, cyclopentyl, n-hexyl, isohexyl, cyclohexyl, heptyl, octyl, nonyl and decyl. The halogen of the haloalkyl group includes chlorine, bromine, fluorine and iodine. In the formula [13], the alkyl group represented by R 13 or the alkyl group of the haloalkyl group represented by R 13 may be either linear or branched. Preferable examples of each alkyl group are alkyl groups of 1 to 6 carbon atoms, such as methyl, ethyl, n-propyl, isopropyl, n-butyl, isobutyl, tert-butyl, sec-butyl, n-pentyl, isopentyl, tert-pentyl, 1-methylpentyl, n-hexyl and isohexyl. The alkoxy group of 1 to 6 carbon atoms represented by R 13 may be either linear or branched. Preferable examples thereof are alkoxy groups of 1 to 5 carbon atoms, such as methoxy, ethoxy, n-propoxy, isopropoxy, n-butoxy, isobutoxy, tert-butoxy, sec-butoxy, n-pentyloxy, isopentyloxy, n-hexyloxy and isohexyloxy. The halogen atom represented by R 13 or the halogen of the haloalkyl group represented by R 13 includes chlorine, bromine, fluorine and iodine. In the formula [14], the alkyl group represented by R 14 may be either linear or branched. Preferable examples thereof are alkyl groups of 1 to 5 carbon atoms, such as methyl, ethyl, n-propyl, isopropyl, n-butyl, isobutyl, tert-butyl, sec-butyl, n-pentyl, isopentyl, tert-pentyl and 1-methylpentyl. The halogen atom represented by R 14 ncludes chlorine, bromine, fluorine and iodine. The alkyl group represented by R 15 may be linear, branched or cyclic. Preferable examples thereof are alkyl groups of 1 to 10 carbon atoms, such as methyl, ethyl, n-propyl, isopropyl, cyclopropyl, n-butyl, isobutyl, tert-butyl, sec-butyl, n-pentyl, isopentyl, tert-pentyl, 1-methylpentyl, cyclopentyl, n-hexyl, isohexyl, cyclohexyl, heptyl, octyl, nonyl and decyl. The aralkyl group represented by R 15 includes, for example, a benzyl group, a phenethyl group, a phenylpropyl group, a methylbenzyl group, a methylphenethyl group, an ethylbenzyl group, etc. The alkoxy group represented by R 15 may be either linear or branched and includes, for example, alkoxy groups of 1 to 6 carbon atoms, such as methoxy, ethoxy, n-propoxy, isopropoxy, n-butoxy, isobutoxy, tert-butoxy, sec-butoxy, n-pentyloxy, isopentyloxy, n-hexyloxy and isohexyloxy. In the formula [15], the alkyl group represented by each of R 16 , R 17 and R 18 may be linear, branched or cyclic. Preferable examples thereof are alkyl groups of 1 to 8 carbon atoms, such as methyl, ethyl, n-propyl, isopropyl, cyclopropyl, n-butyl, isobutyl, tert-butyl, sec-butyl, n-pentyl, isopentyl, tert-pentyl, 1-methylpentyl, cyclopentyl, n-hexyl, isohexyl, cyclohexyl, heptyl and octyl. The substituted phenyl group represented by each of R 16 , R 17 and R 18 includes, for example, a tolyl group, an ethylphenyl group, a tert-butylphenyl group, a chlorophenyl group, etc. The aralkyl group represented by each of R 16 , R 17 and R 18 includes, for example, a benzyl group, a phenethyl group, a phenylpropyl group, a methylbenzyl group, a methylphenethyl group, a ethylbenzyl group, etc. The alkyl group of the fluoroalkyl group represented by R 19 may be either linear or branched. Prerable examples thereof are alkyl groups of 1 to 8 carbon atoms, such as methyl, ethyl, n-propyl, isopropyl, n-butyl, isobutyl, tert-butyl, sec-butyl, n-pentyl, isopentyl, tert-pentyl, 1-methylpentyl, n-hexyl, isohexyl, heptyl and octyl. The total number of fluorine atoms as the substituents of the fluoroalkyl group is preferably 1 to 17. In the formula [16], the alkyl group represented by R 29 may be linear, branched or cyclic. Preferable examples thereof are alkyl groups of 1 to 6 carbon atoms, such as methyl, ethyl, n-propyl, isopropyl, n-butyl, isobutyl, tert-butyl, sec-butyl, n-pentyl, isopentyl, cyclopentyl, n-hexyl and cyclohexyl. The substituted phenyl group represented by R 29 includes, for example, a tolyl group, an ethylphenyl group, a tert-butylphenyl group, a chlorophenyl group, etc. The aralkyl group represented by R 29 includes, for example, a benzyl group, a phenethyl group, a phenylpropyl group, a methylbenzyl group, a methylphenethyl group and an ethylbenzyl group . The alkyl group of the fluoroalkyl group represented by R 29 may be either linear or branched. Preferable examples thereof are alkyl groups of 1 to 8 carbon atoms, such as methyl, ethyl, n-propyl, isopropyl, n-butyl, isobutyl, tert-butyl, sec-butyl, n-pentyl, isopentyl, n-hexyl, heptyl and octyl. The total number of fluorine atoms as the substituents of the fluoroalkyl group is preferably 1 to 17. In the formula [17], the alkyl group represented by R 3 3 may be linear, branched or cyclic. Preferable examples thereof are alkyl groups of 1 to 6 carbon atoms, such as methyl, ethyl, n-propyl, isopropyl, n-butyl, isobutyl, tert-butyl, sec-butyl, n-pentyl, isopentyl, cyclopentyl, n-hexyl and cyclohexyl. The substituted phenyl group represented by R 33 includes, for example, a tolyl group, an ethylphenyl group, a tert-butylphenyl group and a chlorophenyl groups. The aralkyl group represented by R 33 includes, for example, a benzyl group, a phenethyl group, a phenylpropyl group, a methylbenzyl group, a methylphenethyl group and an ethylbenzyl group. The alkyl group of the fluoroalkyl group represented by R 33 may be either linear or branched. Preferable examples thereof are alkyl groups of 1 to 8 carbon atoms, such as methyl, ethyl, n-propyl, isopropyl, n-butyl, isobutyl, tert-butyl, sec-butyl, n-pentyl, isopentyl, n-hexyl, heptyl and octyl. The total number of fluorine atoms as the substituents of the fluoroalkyl group is preferably 1 to 17. In the formula [18], the alkyl group represented by R 34 may be linear, branched or cyclic. Preferable examples thereof are alkyl groups of 1 to 6 carbon atoms, such as methyl, ethyl, n-propyl, isopropyl, n-butyl, isobutyl, tert-butyl, sec-butyl, n-pentyl, isopentyl, cyclopentyl, n-hexyl and cyclohexyl. The substituted phenyl group represented by R 34 includes, for example, a tolyl group, an ethylphenyl group, a tert-butylphenyl group and a chlorophenyl group. The aralkyl group represented by R 34 includes, for example, a benzyl group, a phenethyl group, a phenylpropyl group, a methylbenzyl group, a methylphenethyl group and an ethylbenzyl group. The alkyl group of the fluoroalkyl group represented by each of R 34 and R 35 may be either linear or branched. Preferable examples thereof are alkyl groups of 1 to 8 carbon atoms, such as methyl, ethyl, n-propyl, isopropyl, n-butyl, isobutyl, tert-butyl, sec-butyl, n-pentyl, isopentyl, n-hexyl, heptyl and octyl. The total number of fluorine atoms as the substituents of the fluoroalkyl group is preferably 1 to 17. Specific preferable examples of the acid generator used in the present invention are as follows: The acid generators of the formula [11] include, for example, 1-cyclohexylsulfonyl-1-(1,1-dimethylethylsulfonyl) diazomethane, bis (1,1-dimethylethylsulfonyl)diazomethane, bis (1-methylethylsulfonyl)diazomethane, bis (cyclohexylsulfonyl) diazomethane, 1-cyclohexylsulfonyl-1-cyclohexylcarbonyldiazomethane, 1-diazo-1-cyclohexylsulfonyl-3,3-dimethylbutan-2-one, 1-diazo-1-methylsulfonyl-4-phenylbutan-2-one, 1-diazo-1-(1,1-dimethylethylsulfonyl) -3,3-dimethyl-2-butanone and 1-acetyl-1-(1-methylethylsulfonyl) diazomethane . The acid generators of the formula [12] include, for example, bis (p-toluenesulfonyl)diazomethane, bis (2,4-dimethylbenzenesulfonyl)diazomethane, methylsulfonyl-p-toluenesulfonyldiazomethane, bis (p-tert-butylphenylsulfonyl) diazomethane, bis (p-chlorobenzenesulfonyl) diazomethane and cyclohexylsulfonyl-p-toluenesulfonyldiazomethane. The acid generators of the formula [14] include, for example, 1-p-toluenesulfonyl-1-cyclohexylcarbonyldiazomethane, 1-diazo-1-(p-toluenesulfonyl) -3,3-dimethylbutan-2-one, 1-diazo-1-benzenesulfonyl-3,3-dimethylbutan-2-one and 1-diazo-1-(p-toluenesulfonyl)-3-methylbutan-2-one. The acid generators of the formula [15] include, for example, triphenylsulfonium · trifluoromethanesulfonate, triphenylsulfonium · perfluorooctanesulfonate, diphenyl-p-tolylsulfonium · perfluorooctanesulfonate, tris(p-tolyl) sulfonium · perfluorooctanesulfonate, tris (p-chlorobenzene) sulfonium · trifluoromethanesulfonate, tris (p-tolyl) sulfonium · trifluoromethanesulfonate, trimethylsulfonium · trifluoromethanesulfonate, dimethylphenylsulfonium · trifluoromethanesulfonate, dimethyl-p-tolylsulfonium · trifluoromethanesulfonate, dimethyl-p-tolylsulfonium · perfluorooctanesulfonate. The acid generators of the formula [16] include, for example, 2,6-di-trifluoromethanesulfonyloxyacetophenone, 2,6-di-trifluoromethanesulfonyloxypropiophenone, 2,3,4-tris-trifluoromethanesulfonyloxyacetophenone, 2,6-di-methanesulfonyloxyacetophenone, 2,6-di-methanesulfonyloxypropiophenone, 2,3,4-tris-methanesulfonyloxyacetophenone, 2-trifluoromethanesulfonyloxyacetophenone, 2-methanesulfonyloxyacetophenone, 2-n-butanesulfonyloxyacetophenone, 2,6-di-n-butanesulfonyloxyacetophenone, 2,3,4-tris-n-butanesulfonyloxyacetophenone, 2,6-di-perfluoropropanecarboxyacetophenone, 2,3,4-tris-perfluoropropanecarboxyacetophenone, 2,6-di-p-toluenesulfonyloxyacetophenone, 2,6-di-p-toluenesulfonylpropiophenone, 2,6-di-trifluoroacetyloxyacetophenone, 2-trifluoroacetyloxy-6-methoxyacetophenone, 6-hydroxy-2-perfluorobutanesulfonyloxyacetophenone, 2-trifluoroacetyloxy-6-nitroacetophenone, 2,3,4-tris-trifluoroacetyloxyacetophenone, 2,6-di-perfluoropropanoyloxyacetophenone. The acid generators of the formula [18] include, for example, 1,2,3-tris-methanesulfonyloxybenzene, 1,2,3-tris-p-toluenesulfonyloxybenzene, 1,2,3-tris-trifluoromethanesulfonyloxybenzene, 1,2,3-tris-perfluorobutanesulfonyloxybenzene, 1,2,3-tris-cyclohexylsulfonyloxybenzene, 1,2-di-methanesulfonyloxy-3-nitrobenzene, 2,3-di-methanesulfonyloxyphenol, 1,2,4-tris-p-toluenesulfonyloxybenzene, 1,2,4-tris-methanesulfonyloxybenzene, 1,2,4-tris-trifluoromethanesulfonyloxybenzene, 1,2,4-tris-cyclohexylsulfonyloxybenzene, 1,2-di-n-butanesulfonyloxy-3-nitrobenzene, 1,2,3-tris-perfluorooctanesulfonyloxybenzene, 1,2-di-perfluorobutanesulfonyloxyphenol. The acid generator used in the present invention can easily be obtained, for example, by any of the processes disclosed in JP-A 4-210960, JP-A 4-211258, and JP-A 5-249682. In the resist compositions of the present invention, the amount of the specific nitrogen-containing compound to be used is usually 0.01 to 10 parts by weight, preferably 0.1 to 1.0 part by weight relative to 100 parts by weight of either (a) the polymer capable of becoming alkali-soluble owing to the action of an acid (hereinafter abbreviated as polymer component (i)) or (b) the sum of the alkali-soluble polymer and the compound capable of becoming alkali-soluble owing to the action of an acid (this sum is hereinafter abbreviated as polymer component (ii)) or (c) the sum of the alkali-soluble polymer and the compound capable of making the polymer hardly alkali-soluble by crosslinking therewith owing to the action of an acid (this sum is hereinafter abbreviated as polymer component (iii)). When the compound capable of becoming alkali-soluble owing to the action of an acid or the compound capable of making the polymer hardly alkali-soluble by crosslinking therewith owing to the action of an acid is used together with the alkali-soluble polymer in the resist compositions of the present invention, an amount of the compound to be used is usually 10 to 50 parts by weight, preferably 15 to 40 parts by weight relative to 100 parts by weight of the alkali-soluble polymer. An amount of the acid generator to be used in the resist compositions of the present invention is usually 1 to 30 parts by weight, preferably 1 to 20 parts by weight relative to 100 parts by weight of polymer component (i), polymer component (ii) or polymer component (iii). In the present invention, any solvent may be used so long as it can dissolve any of the above-mentioned polymer components (i) to (iii), the acid generator and the present invention's compound. Usually, solvents having good film-forming properties are preferably used. Specific preferable examples of the solvent are methyl Cellosolve acetate, ethyl Cellosolve acetate, propylene glycol monomethyl ether acetate, propylene glycol monoethyl ether acetate, ethyl lactate, methyl pyruvate, ethyl pyruvate, methyl 3-methoxypropionate, N-methyl-2-pyrrolidone, 2-heptanone, cyclohexanone, diethylene glycol monoethyl ether and diethylene glycol dimethyl ether. The amount of the solvent used in the present invention is preferably 2 to 20 times, more preferably 3 to 10 times, as much as the total weight of any of polymer components (i) to (iii). Usually, the resist composition of the present invention is composed mainly of four components, i.e., any of the above-mentioned polymer components (i) to (iii), the acid generator, the present invention's compound and the solvent. If necessary, the resist composition may contain sensitivity adjustors, surfactants, ultraviolet absorbers, plasticizers, dissolving auxiliaries, etc. in addition to the four components. As the sensitivity adjustors used if necessary in the resist composition of the present invention, there can be exemplified by poly (vinylpyridine), poly-(vinylpyridine/methyl methacrylate), pyridine, N,N-bis (2-hydroxyethyl) aniline, monoalkylamine, the alkyl group including linear, branched or cyclic alkyl groups of 1 to 12 carbon atoms, specific examples thereof being 2-methylcyclohexylamine, 4-t-butylcyclohexylamine, dialkylamine, the alkyl group including linear, branched or cyclic alkyl groups of 1 to 12 carbon atoms, specific preferable examples thereof being dicyclohexylamine, di-n-octylamine, trialkylamines, the alkyl group including linear, branched or cyclic alkyl groups of 1 to 12 carbon atoms, specific preferable examples thereof being triethylamine, tri-n-propylamine, tri-n-butylamine, trihexylamine, trioctylamine, dicyclohexylmethylamine, dioctylmethylamine, dimethyloctylamine, mono-, di- or trialkanolamines, specific preferable examples thereof being triethanolamine, triisopropanolamine, tetraalkylammonium hydroxides, the alkyl group including linear, branched or cyclic alkyl groups of 1 to 12 carbon atoms, specific preferable examples thereof being tetramethylammonium hydroxide and tetra-n-butylammonium hydroxide. The sensitivity adjustors are not limited to these compounds. An amount of the sensitivity adjustors used if necessary is preferably 0.001 to 10 parts by weight, more preferably 0.01 to 5 parts by weight, per 100 parts by weight of any of polymer components (i) to (iii). As the surfactants used if necessary in the resist composition of the present invention, there can be exemplified by nonionic surfactants, e.g. polyethylene glycol distearate, polyethylene glycol dilaurate, poly (ethylene glycol), poly (propylene glycol), polyoxyethylene stearyl ether, polyoxyethylene cetyl ether, cationic surfactants and anionic surfactants. Of these surfactants, specific examples of surfactant preferably used from the viewpoint of the formation of a resist film are fluorine-containing nonionic surfactants such as Fluorad (a trade name, SUMITOMO 3M Ltd.), SURFLON (a trade name, Asahi Glass Co., Ltd.), UNIDYNE (a trade name, DAIKIN INDUSTIRIES, LTD.), MEGAFAC (a trade name, DAINIPPON INK AND CHEMICALS, INC.), EFTON (a trade name, TOHKEMPRODUCTS Corporation). An amount of the surfactants used if necessary is preferably 0.001 to 10 parts by weight, more preferably 0.01 to 5 parts by weight, per 100 parts by weight of any of polymer components (i) to (iii). As the ultraviolet absorbers used if necessary in the resist composition of the present invention, there can be exemplified by 9-diazofluorene, 9-(2-methoxyethoxymethyl)anthracene, 9-(2-ethoxyethoxymethyl) anthracene, 9-fluorenone, 2-hydroxycarbazole, o-naphthoquinone azide and 4-diazo-1,7-diphenylpentane-3,5-dione. An amount of the ultraviolet absorbers used if necessary is preferably 0.001 to 10 parts by weight, more preferably 0.01 to 5 parts by weight, per 100 parts by weight of any of polymer components (i) to (iii). As the plasticizers used if necessary in the resist composition of the present invention, there can be exemplified by di-n-butyl phthalate, bis (2-ethylhexyl)phthalate, dibutyl adipate, diethylene glycol dibenzoate, butyl oleate, methyl acetylricinoleate, chlorinated paraffin and alkyl epoxystearates. An amount of the plasticizers used if necessary is preferably 0.001 to 10 parts by weight, more preferably 0.01 to 5 parts by weight, per 100 parts by weight of any of polymer components (i) to (iii). As the dissolving auxiliaries used if necessary in the resist composition of the present invention, there can be exemplified by N,N-dimethylformamide,and N,N-dimethylacetamide. An amount of the dissolving auxiliaries used if necessary is preferably 0.01 to 20 parts by weight, more preferably 0.1 to 10 parts by weight, per 100 parts by weight of any of polymer components (i) to (iii). A pattern is formed by use of the resist composition of the present invention, for example, as follows. The resist composition of the present invention is spin-coated on a semiconductor substrate of SiO 2 , polycrystalline silicon, BPSG, TEOS, TiN or SiN, and baked on a hot plate at 50 °C to 120 °C for 0.5 to 2 minutes to obtain a resist film of 0.5 to 2 µm thick. Subsequently, the resist film is selectively exposed to radiation (e.g. KrF excimer laser beams of 248.4 nm, deep ultraviolet light of 300 nm or less, electron beams, soft X-rays) through a mask, and then, if necessary, post-baked on a hot plate at 50 C to 130 °C for 0.5 to 2 minutes. Thereafter, the resist film is developed with an alkali developing solution by a puddle method, a dip method or a spray method to dissolve away the exposed portion, whereby a positive pattern is formed. The alkali of the alkali developing solution used in any of the above various development methods includes, for example, tetramethylammonium hydroxide, choline, triethanolamine, KOH, NaOH, etc. A concentration thereof is preferably 0.1 to 10% by weight, more preferably 0.5 to 5% by weight. Surfactants may be incorporated into the alkali developing solution. When the chemical amplified type resist material containing the specific nitrogen-containing compound is used on a special substrate on which an unsatisfactory profile of pattern tends to be obtained because of the presence of a large amount of basic compounds in the substrate, the action of the basic compounds is inhibited, so that a stable and good profile of pattern can be obtained. There are known methods using an organic carboxylic acid or sulfonic acid compound for inhibiting the action of the basic compounds. These methods, however, involve the following problem: for maintaining the storage stability of a resist composition, a basic compound should be used in an amount larger than that required for neutralizing the acid, so that the resist is decreased in sensitivity and hence deteriorated in practical utility. The above problem can also be sufficiently solved using the specific nitrogen-containing compound. The present invention is explained below in detail with reference to Examples and Comparative Examples, which are not by way of limitation but by way of illustration. Some of the polymers and acid generators, which were used in the Examples and Comparative Examples, had been synthesized, for example, by the processes disclosed in JP-A 4-210960 (U.S. Patent 5,216,135); JP-A 4-211258 (U.S. Patent 5,350,660; European Patent Laid-Open No. 0,440,374); JP-A 5-249682 (European Patent Laid-Open No. 0,520,642); JP-A 4-251259; Y. Endo et al., Chem. Pharm. Bull., 29 (12), p. 3753 (1981); M. Desbois et al., Bull. Chem. Soc. France, 1974 , p. 1956; C.D. Beard et al., J. Org. Chem., 38 , p. 3673 (1973). The weight average molecular weight and the ratio of weight-average molecular weight (Mw) to number-average molecular weight (Mn) (Mw/Mn: dispersity) of each of the polymers used in Examples and Comparative Examples were determined by a gel permeation chromatography (GPC) method using a polystyrene as a standard. Example 1 A resist composition was prepared according to the following recipe: Poly[p-(1-ethoxyethoxy)styrene/p-hydroxystyrene] (Mw : 20,000, dispersity : 1.90) 4.5 g Bis(cyclohexylsulfonyl)diazomethane 0.3 g Bis(p-toluenesulfonyl)diazomethane 0.15 g Fluorine-containing nonionic surfactant (commercial product) 0.05 g Tri-n-propylamine 0.05 g Propylene glycol monomethyl ether acetate 23 g Phthalimide 0.02 g The above ingredients were mixed to effect dissolution and the resulting solution was filtered through a filter with a pore size of 0.2 µm. Using the thus obtained resist composition, a pattern was formed in the manner described below. The resist composition according to the above recipe was spin-coated on a semiconductor substrate (a BPSG substrate) obtained by forming a silicon oxide film doped with boron and phosphorus on a silicon wafer, and baked on a hot plate at 90 °C for 90 seconds to obtain a resist film of 1 µm thick. Subsequently, the resist film was selectively exposed to KrF excimer laser beams (NA:0.55) of 248.4 nm through a mask, and then post-baked on a hot plate at 105 °C for 90 seconds. Thereafter, the resist film was developed with an alkali developing solution (a 2.38% aqueous tetramethylammonium hydroxide solution) for 60 seconds by a puddle method to dissolve away only the exposed portion of the resist film, whereby a positive pattern was obtained. As shown in Fig. 1, the obtained positive pattern showed a resolution of a contact hole of 0.25 µm having a good profile. In this case, the exposure dose was 38 mJ/cm 2 . When the resist composition according to the above recipe was stored at 23 °C for 3 months and then used for forming a pattern in the same manner as above, a contact hole of 0.25 µm having a good profile was formed at an exposure dose of 38 mJ/cm 2 . Thus, the storage stability of the resist composition was confirmed. Examples 2 to 29 Resist compositions were prepared according to the respective recipes shown in Tables 1 to 12. Example 2 Poly(p-tert-butoxystyrene/p-hydroxystyrene) (Mw:15,000, dispersity:1.95) 4.5g Bis(1,1-dimethylethylsulfonyl)diazomethane 0.25g p-Toluenesulfonylcyclohexylsulfonyldiazomethane 0.05g Fluorine-containing nonionic surfactant (commercial product) 0.05g Trioctylamine 0.05g Propylene glycol monomethyl ether acetate 23g Succinimide 0.01g Example 3 Poly(p-1-tetrahydropyranyloxystyrene/p-hydroxystyrene) (Mw:20,000, dispersity:1.85) 4.5g Bis(cyclohexylsulfonyl)diazomethane 0.3g Fluorine-containing nonionic surfactant (commercial product) 0.05g Trioctylamine 0.05g Propylene glycol monomethyl ether acetate 23g Glutarimide 0.01g Example 4 Poly[p-(1-methyl-1-methoxyethoxy)styrene/p-hydroxystyrene] (Mw:10,000, dispersity:1.90) 4.5g Bis(1,1-dimethylethylsulfonyl)diazomethane 0.25g Bis(p-toluenesulfonyl)diazomethane 0.05g Fluorine-containing nonionic surfactant (commercial product) 0.03g Trioctylamine 0.05g Propylene glycol monomethyl ether acetate 23g Succinimide 0.02g Example 5 Poly(p-tert-butyloxycarbonyloxystyrene/p-hydroxystyrene) (Mw:8,000, dispersity:1.10) 4.5g Bis(cyclohexylsulfonyl)diazomethane 0.3g Bis(p-toluenesulfonyl)diazomethane 0.05g Fluorine-containing nonionic surfactant (commercial product) 0.03g Trioctylamine 0.05g Propylene glycol monomethyl ether acetate 23g Phthalimide 0.03g Example 6 Poly(tert-butyl p-vinylphenoxyacetate/p-hydroxystyrene) (Mw:15,000, dipersity:1.05) 4.5g Bis(cyclohexylsulfonyl)diazomethane 0.3g Bis(2,4-dimethylbenzenesulfonyl)diazomethane 0.1g Fluorine-containing nonionic surfactant (commercial product) 0.03g Trioctylamine 0.05g Propylene glycol monomethyl ether acetate 23g Maleimide 0.01g Example 7 Poly[p-(1-methyl-1-methoxyethoxy)styrene/p-hydroxystyrene] (Mw:20,000, dispersity:1.05) 4.5g Bis(cyclohexylsulfonyl)diazomethane 0.3g Bis(p-toluenesulfonyl)diazomethane 0.05g Fluorine-containing nonionic surfactant (commercial product) 0.03g Tetrabutylammonium hydroxide 0.05g Propylene glycol monomethyl ether acetate 23g Phthalimide 0.02g Example 8 Poly[p-(1-ethoxyethoxy)styrene/p-hydroxystyrene] (Mw:20,000, dispersity:1.05) 4.5g Bis(cyclohexylsulfonyl)diazomethane 0.3g Fluorine-containing nonionic surfactant (commercial product) 0.03g Dicyclohexylmethylamine 0.05g Propylene glycol monomethyl ether acetate 23g Succinimide 0.01g Example 9 Poly[p-(1-ethoxyethoxy)styrene/p-hydroxystyrene] (Mw:15,000, dispersity:1.10) 4.5g Bis(cyclohexylsulfonyl)diazomethane 0.3g Fluorine-containing nonionic surfactant (commercial product) 0.03g 9-Diazofluorene 0.018g Dioctylmethylamine 0.05g 2-Heptanone 23g Succinimide 0.01g Example 10 Poly[p-(1-ethoxyethoxy)styrene/p-hydroxystyrene] (Mw:8,000, dispersity:1.05) 4.5g Bis(cyclohexylsulfonyl)diazomethane 0.3g Fluorine-containing nonionic surfactant (commercial product) 0.03g Tetrabutylammonium hydroxide 0.05g 9-(2-Methoxyethoxymethyl)anthracene 0.01g Propylene glycol monomethyl ether acetate 23g Phthalimide 0.02g Example 11 Poly[p-(1-ethoxyethoxy)styrene/p-tert-butyloxycarbonyloxystyrene/p-hydroxystyrene] (Mw:8,000, dispersity:1.85) 4.5g Bis(p-toluenesulfonyl)diazomethane 0.3g n-Hexanesulfonyloxysuccinimide 0.1g Fluorine-containing nonionic surfactant (commercial product) 0.03g Tetrabutylammonium hydroxide 0.05g 2-Heptanone 23g succinimide 0.01g Example 12 Poly[p-(1-ethoxyethoxy)styrene/p-tert-butoxystyrene/p-hydroxystyrene](Mw:20,000, dispersity:1.80) 4.5g Bis(cyclohexylsulfonyl)diazomethane 0.25g Triphenylsulfonium·trifoluoromethane sulfonate 0.03g Fluorine-containing nonionic surfactant (commercial product) 0.05g Tetrabutylammonium hydroxide 0.05g Propylene glycol monomethyl ether acetate 23g Succinimide 0.01g Example 13 Poly[p-(1-ethoxyethoxy)styrene/p-tert-butoxystyrene/p-hydroxystyrene](Mw:15,000, dispersity:1.85) 4.5g Bis(cyclohexylsulfonyl)diazomethane 0.3g Fluorine-containing nonionic surfactant (commercial product) 0.03g Tetrabutylammonium hydroxide 0.03g 2-Heptanone 23g Succinimide 0.01g Example 14 Poly[p-(1-methoxyethoxy)styrene/p-tert-butoxystyrene/p-hydroxystyrene](Mw:20,000, dispersity:1.90) 4.5g Bis(1,1-dimethylethylsulfonyl)diazomethane 0.25g Bis(p-toluenesulfonyl)diazomethane 0.05g Fluorine-containing nonionic surfactant (commercial product) 0.03g Trioctylamine 0.05g Propylene glycol monomethyl ether acetate 23g Phthalimide 0.02g Example 15 Poly[p-(1-ethoxyethoxy)styrene/p-1-tetrahydropyranyloxystyrene/p-hydroxystyrene] (Mw:20,000, dispersity:1.85) 4.5g Bis(cyclohexylsulfonyl)diazomethane 0.25g Bis(benzenesulfonyl)diazomethane 0.05g Fluorine-containing nonionic surfactant (commercial product) 0.03g Trioctylamine 0.05g Propylene glycol monomethyl eteracetate 23g Succinimide 0.01g Example 16 Poly[p-(1-ethoxyethoxy)styrene/p-tert-butoxystyrene/p-hydroxystyrene](Mw:20,000, dispersity:1.95) 4.5g Bis(cyclohexylsulfonyl)diazomethane 0.25g Bis(p-toluenesulfonyl)diazomethane 0.05g Fluorine-containing nonionic surfactant (commercial product) 0.05g Dioctylmethylamine 0.05g Diethylene glycol dimethyl ether 23g Succinimide 0.01g Example 17 Poly[p-(1-tetrahydropyranyloxy)styrene/p-tert-butoxystyrene/p-hydroxystyrene](Mw:15,000, dispersity:1.05) 4.5g Triphenylsulfoniumtrifluoromethane sulfonate 0.1g Bis(benzenesulfonyl)diazomethane 0.1g Fluorine-containing nonionic surfactant (commercial product) 0.03g Trioctylamine 0.05g 2-Heptanone 23g Pthalimide 0.01g Example 18 Poly[p-(1-ethoxyethoxy)styrene/p-hydroxystyrene] (Mw:15,000, dispersity:1.10) 4.5g Poly(p-tert-butyloxycarbonyloxystyrene/p-hydroxystyrene) (Mw:15,000, dispersity:1.05) 1.5g Bis(cyclohexylsulfonyl)diazomethane 0.25g Bis(2,4-dimethylbenzenesulfonyl)diazomethane 0.05g Fluorine-containing nonionic surfactant (commercial product) 0.03g Trioctylamine 0.05g Propyrene glycol monomethyl ether acetate 30g Maleimide 0.01g Example 19 Poly[p-(1-ethoxyethoxy)styrene/p-hydroxystyrene] (Mw:20,000, dispersity::1.80) 4.5g Poly(p-tert-butoxystyrene/p-hydroxystyrene] (Mw:8,000, dispersity:1.95) 1.5g Bis(cyclohexylsulfonyl)diazomehtane 0.3g Octanesulfonyloxysuccinimide 0.3g Fluorine-containing nonionic surfactant (commercial product) 0.03g Trioctylamine 0.05g 2-Heptanone 30g Phthalimde 0.01g Example 20 Poly[p-(1-ethoxyethoxy)styrene/p-hydroxystyrene] (Mw:20,000, dispersity:1.85) 4.5g Poly(p-tert-butyloxycarbonyloxystyrene/p-hydroxystyrene) (Mw:8,000, dispersity:1.85) 1.5g Bis(cyclohexylsulfonyl)diazomethane 0.25g Bis(2,4-dimethylbenzenesulfonyl)diazomehane 0.05g Fluorine-containing nonionic surfactant (commercial product) 0.03g Trioctylamine 0.05g Diethylene glycol dimethyl ether 30g Maleimide 0.01g Example 21 Poly[p-(1-ethoxyethoxy)styrene/p-hydroxystyrene] (Mw:20,000, dispersity:1.05) 4.5g Bis(cyclohexylsulfonyl)diazomethane 0.3g Fluorine-containing nonionic surfactant (commercial product) 0.05g Tetrabutylammonium hydroxide 0.05g Cyclohexanone 23g Succinimide 0.01g Example 22 Poly(p-hydroxystyrene) (Mw:8,000, dispersity:1.85) 4.5g 2,2-Bis[4-(1-ethoxyethoxy)phenyl]propane 1.5g Bis(cyclohexylsulfonyl)diazomethane 0.3g Nonionic surfactant (commercial product) 0.03g Dicyclohexylmethylamine 0.05g Propylene glycol monomethyl ether acetate 30g Succinimide 0.01g Example 23 Poly[p-(1-ethoxyethoxy)styrene/p-hydroxystyrene] (Mw:20,000, dispersity:1.90) 4.5g Bis(cyclohexylsulfonyl)diazomethane 0.3g Bis(p-toluenesulfonyl)diazomethane 0.15g Fluorine-containing nonionic surfactant (commercial product) 0.05g Tri-n-propylamine 0.05g Propylene glycol monomethyl ether acetate 23g Diacetamide 0.02g Example 24 Poly[p-(1-ethoxyethoxy)styrene/p-hydroxystyrene] (Mw:15,000, dispersity:1.95) 4.5g Bis(cyclohexylsulfonyl)diazomethane 0.3g Fluorine-containing nonionic surfactant (commercial product) 0.03g Tetrabutylammonium hydroxide 0.05g Propylene glycol monomethyl ether acetate 23g Diacetylurea 0.02g Example 25 Poly[p-(1-methyl-1-methoxyethoxy)styrene/p-hydroxystyrene] (Mw:20,000, dispersity:1.05) 4.5g Bis(cyclohexylsulfonyl)diazomethane 0.3g Bis(p-toluenesulfonyl)diazomethane 0.05g Fluorine-containing nonionic surfactant (commercial product) 0.03g Tetrabutylammonium hydroxide 0.05g Propylene glycol monomethyl ether acetate 23g Dibenzoylurea 0.02g Example 26 Poly[p-(1-ethoxyethoxy)styrene/p-hydroxystyrene] (Mw:20,000, dispersity:1.05) 4.5g Bis(cyclohexylsulfonyl)diazomethane 0.3g Fluorine-containing nonionic surfactant (commercial product) 0.03g Dicyclohexylmethylamine 0.05g Propylene glycol monomethyl ether acetate 23g Methanesulfonamide 0.01g Example 27 Poly[p-tetrahydropyranyloxystyrene/p-hydroxystyrene] (Mw:15,000, dispersity:1.10) 4.5g Bis(cyclohexylsulfonyl)diazomethane 0.3g Fluorine-containing nonionic surfactant (commercial product) 0.03g Dioctylmethylamine 0.05g 9-Diazofluorene 0.01g 2-Heptanone 23g p-Toluenesulfonamide 0.01g Example 28 Poly[p-ethoxyethoxy)styrene/p-tert-butoxystyrene/p-hydroxytyrene](Mw:15,000, dispersity:1.85) 4.5g Bis(cyclohexylsulfonyl)diazomethane 0.3g Fluorine-containing nonionic surfactant (commercial product) 0.03g Tetrabutylammonium hydroxide 0.03g 2-Heptanone 23g Benzenesulfonamide 0.01g Example 29 Poly[p-(1-ethoxyethoxy)styrene/p-hydroxystyrene] (Mw:20,000, dispersity:1.05) 4.5g Poly(p-tert-butoxycarbonyloxystyrene/p-hydroxystyrene) (Mw:8,000, dispersity:1.85) 1.5g Bis(cyclohexylsulfonyl)diazomethane 0.25g Bis(2,4-dimethylbenzenesulfonyl)diazomethane 0.05g Fluorine-containing nonionic surfactant (commercial product) 0.03g Trioctylamine 0.05g Diethylene glycol 30g N-Benzoylbenzamide 0.01g Pattern formation was carried out in the same manner as in Example 1 except for using each of the resist compositions prepared according to the respective recipes shown in Tables 1 to 12. The results obtained are shown in Tables 13 and 14. Example No. Exposure dose (mJ/cm 2 ) Resolution (µmC/H) Profile of pattern Storage stability 2 54 0.35 Good Good 3 46 0.35 Good Good 4 33 0.25 Good Good 5 52 0.45 Good Good 6 50 0.40 Good Good 7 35 0.25 Good Good 8 38 0.25 Good Good 9 38 0.25 Good Good 10 36 0.25 Good Good 11 40 0.30 Good Good 12 40 0.30 Good Good 13 40 0.30 Good Good 14 40 0.30 Good Good 15 38 0.30 Good Good 16 36 0.25 Good Good 17 38 0.35 Good Good 18 38 0.30 Good Good 19 38 0.25 Good Good 20 38 0.25 Good Good 21 38 0.25 Good Good 22 44 0.35 Good Good Example No. Exposure dose (mJ/cm 2 ) Resolution (µmC/H) Profile of pattern Storage stability 23 38 0.25 Good Good 24 38 0.25 Good Good 25 35 0.25 Good Good 26 38 0.25 Good Good 27 38 0.25 Good Good 28 40 0.30 Good Good 29 35 0.30 Good Good Comparative Example 1 A resist composition was prepared according to the following recipe which was the same as the recipe for the resist composition of Example 1 except that the present invention's compound was omitted. Except for using the thus prepared resist composition, a pattern was formed in the same manner as described in Example 1: Poly[p-(1-ethoxyethoxy)styrene/p-hydroxystyrene] (Mwl. : 20,000, dispersity:1.90) 4.5 g Bis(cyclohexylsulfonyl)diazomethane 0.3 g Bis(p-toluenesulfonyl)diazomethane 0.15 g Fluorine-containing nonionic surfactant (commercial product) 0.05 g Tri-n-propylamine 0.05 g Propylene glycol monomethyl ether acetate 23 g As a result, a contact hole of 0.25 µm could be resolved at an exposure dose of 38 mJ/cm 2 , but the pattern had an unsatisfactory profile with footing at the bottom of a resist film as shown in Fig. 2. Comparative Example 2 A resist composition was prepared according to the following recipe using a known technology, and a pattern was formed in the same manner as decribed in Example 1 except for using said resist composition: Poly[p-(1-ethoxyethoxy)styrene/p-hydroxystyrene] (Mw:20,000, dispersity:1.90) 4.5 g Bis(cyclohexylsulfonyl)diazomethane 0.3 g Bis(p-toluenesulfonyl)diazomethane 0.15 g Fluorine-containing nonionic surfactant (commercial product) 0.05 g Tri-n-propylamine 0.05 g Propylene glycol monomethyl ether acetate 23 g Salicylic acid 0.02 g As a result, a contact hole of 0.25 µm having a good profile could be resolved at an exposure dose of 38 mJ/cm 2 . However, when the resist composition was stored at 23 °C for 2 weeks and then used for forming a pattern in the same manner as described in Example 1, also the non-exposed portion was dissolved during development, so that no desired pattern could be obtained as shown in Fig. 3. Thus, the storage stability was not good. Comparative Example 3 A resist composition was prepared according to the same recipe as in Comparative Example 2 except for increasing the amount of tri-n-propylamine to 0.1 g. A pattern was formed in the same manner as described in Example 3 except for using said resist composition. When the resist composition was used on the pattern formation just after preparation or after storage at 23 °C for 1 month, the resist composition gave a contact hole of 0.25 µm having a good profile but had such a low sensitivity that the exposure dose was 110 mJ/cm 2 . Comparative Example 4 A resist composition was prepared according to the same recipe as in Comparative Example 3 except for using phthalic acid in place of salicylic acid. A pattern was formed in the same manner as described in Example 3 except for using said resist composition. Even when used after storage at 23 °C for 1 month, the resist composition gave a contact hole of 0.25 µm but had such a low sensitivity that the exposuredose was 110 mJ/cm2, like the resist composition of Comparative Example 3. Example 30 A resist composition was prepared according to the following recipe: Poly[p-(1-ethoxyethoxy)styrene/p-hydroxystyrene] (Mw:20,000, dispersity:1.90) 4.5 g Bis(cyclohexylsulfonyl)diazomethane 0.3 g Bis(p-toluenesulfonyl)diazomethane 0.15 g Fluorine-containing nonionic surfactant (commercial product) 0.05 g Tri-n-propylamine 0.05 g Propylene glycol monomethyl ether acetate 23 g Phthalimide 0.02 g The above ingredients were mixed to effect dissolution and the resulting solution was filtered through a filter with a pore size of 0.2 µm. Using the thus obtained resist composition, a pattern was formed in the manner described below. The resist composition according to the above recipe was spin-coated on a titanium nitride substrate (a TiN substrate) and baked on a hot plate at 90 °C for 90 seconds to obtain a resist film of 1 µm thick. Subsequently, the resist film was selectively exposed to KrF excimer laser beams (NA:O.55) of 248.4 nm through a mask, and then post-baked on a hot plate at 105 °C for 90 seconds. Thereafter, the resist film was developed with an alkali developing solution (a 2.38% aqueous tetramethylammonium hydroxide solution) for 60 seconds by a puddle method to dissolve away only the exposed portion of the resist film, whereby a positive pattern was obtained. As shown in Fig. 4, the obtained positive pattern showed a resolution of 0.20 µm line-and-space having a good profile. In this case, the exposure dose was 30 mJ/cm 2 . When the resist composition according to the above recipe was stored at 23 °C for 3 months and then used for forming a pattern in the same manner as above, 0.20 µm line-and-space having a good profile could be formed at an exposure dose of 30 mJ/cm 2 . Thus, the storage stability of the resist composition was confirmed. Examples 31 to 43 Resist compositions were prepared according to the respective recipes shown in Tables 15 to 20. Example 31 Poly[p-(1-ethoxyethoxy)styrene/p-hydroxystyrene] (Mw:15,000, dispersity:1.95) 4.5g Bis(cyclohexylsulfonyl)diazomethane 0.3g Fluorine-containing nonionic surfactant (commercial product) 0.03g Tetrabutylammonium hydroxide 0.05g Propylene glycol monomethyl ether acetate 23g Succinimide 0.02g Example 32 Poly[p-(1-methyl-1-methoxyethoxy)styrene/p-hydroxystyrene] (Mw:20,000,dispersity:1.05) 4.5g Bis(cyclohexylsulfonyl)diazomethane 0.3g Bis(p-toluenesulfonyl)diazomethane 0.05g Fluorine-containing nonionic surfactant (commercial product) 0.03g Tetrabutylammonium hydroxide 0.05g Propylene glycol monomethyl ether acetate 23g Phthalimide 0.02g Example 33 Poly[p-(1-ethoxyethoxy)styrene/p-hydroxystyrene] (Mw:20,000, dispersity:1.05) 4.5g Bis(cyclohexylsulfonyl)diazomethane 0.3g Fluorine-containing nonionic surfactant (commercial product) 0.03g Dicyclohexylmethylamine 0.05g Propylene glycol monomethyl ether acetate 23g Succinimide 0.01g Example 34 Poly[p-(1-ethoxyethoxy)styrene/p-hydroxystyrene] (Mw:15,000, dispersity:1.95) 4.5g Bis(cyclohexylsulfonyl)diazomethane 0.3g Fluorineine-containing nonionic surfactant (commercial product) 0.03g Dioctylmethylamine 0.05g 9-Diazofluorene 0.01g 2-Heptanone 23g Phthalimide 0.01g Example 35 Poly[p-(1-ethoxyethoxy)styrene/p-tert-butoxystyrene/p-hydroxystyrene] (Mw:15,000, dispersity: 1.85) 4.5g Fluorine-containing nonionic surfactant (commercial product) 0.03g Tetrabutylammonium hydroxide 0.03g 2-Heptanone 23g Succinimide 0.02g Example 36 Poly[p-(1-ethoxyethoxy)styrene/p-hydroxystyrene] (Mw:20,000, dispersity:1.85) 4.5g Poly(p-tert-butyloxycarbonyloxystyrene/p-hydroxystyrene) (Mw:8,000, dispersity:1.85) 1.5g Bis(cyclohexylsulfonyl)diazomethane 0.25g Bis(2,4-dimethylbenzenesulfonyl)diazomethane 0.05g Fluorine-containing nonionic surfactant (commercial product) 0.03g Trioctylamine 0.05g Diethylene glycol dimethyl ether 30g Phthalimide 0.01g Example 37 Poly[p-(1-ethoxyethoxy)styrene/p-hydroxystyrene] (Mw:20,000, dispersity:1.90) 4.5g Bis(cyclohexylsulfonyl)diazomethane 0.3g Bis(p-toluenesulfonyl)diazomethane 0.15g Fluorine-containing nonionic surfactant (commercial product) 0.05g Tri-n-propylamine 0.05g Propylene glycol monoethyl ether acetate 23g Diacetamide 0.02g Example 38 Poly[p-(1-ethoxyethoxy)styrene/p-hydroxystyrene] (Mw:15,000, dispersity:1.95) 4.5g Bis(cyclohexylsulfonyl)diazomethane 0.3g Fluorine-containing nonionic surfactant (commercial product) 0.03g Tetrabutylammonium hydroxide 0.05g Propylene glycol monomethyl ether acetate 23g Diacetylurea 0.02g Example 39 Poly[p-(1-methyl-1-methoxyethoxy)styrene/p-hydoroxystyrene] (Mw:20,000, dispersity:1.05) 4.5g Bis(cyclohexylsulfonyl)diazomethane 0.3g Bis(p-toluenesulfonyl)diazomethane 0.05g Fluorine-containing nonionic surfactant (commercial product) 0.03g Tetrabutylammonium hydroxide 0.05g Propylene glycol monomethyl ether acetate 23g Dibenzoylurea 0.02g Example 40 Poly[p-(1-ethoxyethoxy)styrene/p-hydroxystyrene] (Mw:20,000, dispersity:1.05) 4.5g Bis(cyclohexylsulfonyl)diazomethane 0.3g Fluorine-containing nonionic surfactant (commercial product) 0.03g Dicyclohexylmethylamine 0.05g Propylene glycol monomethyl ether acetate 23g Methanesulfonamide 0.01g Example 41 Poly[p-tetrahydropyranyloxystyrene/p-hydroxystyrene] (Mw:15,000, dispersity:1.10) 4.5g Bis(cyclohexylsulfonyl)diazomethane 0.3g Fluorine-containing nonionic surfactant (commercial product) 0.03g Dioctylmethylamine 0.05g 9-Diazofluorene 0.01g 2-Heptanone 23g p-Tolenesulfonamide 0.01g Example 42 Poly[p-(1-ethoxyethoxy)styrene/p-tert-butoxystyrene/p-hydroxystyrene] (Mw:15,000, dispersity:1.85) 4.5g Bis(cyclohexylsulfonyl)diazomethane 0.3g Fluorine-containing nonionic surfactant (commercial product) 0.03g Tetrabutylammonium hydroxide 0.03g 2-Heptanone 23g Benzenesulfonamide 0.01g Example 43 Poly[p-(1-ethoxyethoxy)styrene/p-hydroxystyrene] (Mw:20,000, dispersity:1.05) 4.5g Poly(p-tert-butoxycarbonyloxy)styrene/P-hydroxystyrene (Mw:8,000, dispersity:1.85) 1.5g Bis(cyclohexylsulfonyl)diazomethane 0.25g Bis(2,4-dimethylbenzenesulfonyl)diazomethane 0.05g Fluorine-containing nonionic surfactant (commercial product) 0.03g Trioctylamine 0.05g Diethylene glycol 30g N-Benzoylbenzamide 0.01g Pattern formation was carried out in the same manner as in Example 30 except for using each of the resist compositions prepared according to the respective recipes shown in Tables 15 to 20. The results obtained are shown in Table 21. Example No. Exposure dose (mJ/cm 2 ) Resolution (µmL/S) Profile of pattern Storage stability 31 40 0.22 Good Good 32 32 0.20 Good Good 33 36 0.20 Good Good 34 36 0.20 Good Good 35 42 0.22 Good Good 36 38 0.22 Good Good 37 38 0.25 Good Good 38 40 0.22 Good Good 39 32 0.20 Good Good 40 36 0.20 Good Good 41 36 0.20 Good Good 42 38 0.22 Good Good 43 36 0.22 Good Good Comparative Example 5 A resist composition was prepared according to the following recipe which was the same as the recipe for the resist composition of Example 30 except that the present invention's compound was omitted. Except for using the thus prepared resist composition, a pattern was formed in the same manner as described in Example 30: Poly[p-(1-ethoxyethoxy)styrene/p-hydroxystyrene] (Mw:20,000, dispersity:1.90) 4.5 g Bis(cyclohexylsulfonyl)diazomethane 0.3 g Bis(p-toluenesulfonyl)diazomethane 0.15 g Fluorine-containing nonionic surfactant (commercial product) 0.05 g Tri-n-propylamine 0.05 g Propylene glycol monomethyl ether acetate 23 g As a result, 0.20 µm line-and-space could be resolved at an exposure dose of 30 mJ/cm 2 , but the pattern had an unsatisfactory profile with footing at the bottom of a resist film as shown in Fig. 5. Comparative Example 6 A resist composition was prepared according to the following recipe using a known technology, and a pattern was formed in the same manner as described in Example 30 except for using said resist composition: Poly[p-(1-ethoxyethoxy)styrene/p-hydroxystyrene] (Mw:20,000, dispersity:1.90) 4.5 g Bis(cyclohexylsulfonyl)diazomethane 0.3 g Bis(p-toluenesulfonyl)diazomethane 0.15 g Fluorine-containing nonionic surfactant (commercial product) 0.05 g Tri-n-propylamine 0.05 g Propylene glycol monomethyl ether acetate 23 g Salicylic acid 0.02 g As a result, 0.20 µm line- and-space having a good profile could be resolved at an exposure dose of 32 mJ/cm2. However, when the resist composition was stored at 23 °C for 2 weeks and then used for forming a pattern in the same manner as described in Example 30, also the non-exposed portion was dissolved during development, so that no desired pattern could be obtained as shown in Fig. 6. Thus, the storage stability was not good. Comparative Example 7 A resist composition was prepared according to the same recipe as in Comparative Example 6 except for increasing the amount of tri-n-propylamine to 0.1 g. A pattern was formed in the same manner as described in Example 30 except for using said resist composition. When the resist composition was used on the pattern formation just after preparation or after storage at 23 °C for 1 month, the resist composition gave 0.20 µm line-and-space having a good profile but had such a low sensitivity that the exposure dose was 72 mJ/cm 2 . Comparative Example 8 A resist composition was prepared according to the same recipe as in Comparative Example 6 except for using phthalic acid in place of salicylic acid. A pattern was formed in the same manner as described in Example 30 except for using said resist composition. Even when used after storage at 23 °C for 1 month, the resist composition gave 0.20 µm line-and-space having a good profile but had such a low sensitivity that the exposure dose was 72 mJ/cm 2 , like the resist composition of Comparative Example 7. As is clear from the above, when the resist composition of the present invention is used on a special substrate such as a TiN substrate or a BPSG substrate as a resist material for exposure to deep ultraviolet light (300 nm or less) or KrF excimer laser beams (248.4 nm), the resist composition can give a good profile of pattern of quarter micron order without causing footing, while retaining high resolution ability and high sensitivity. Therefore, the present invention is of great value in formation of an ultra-fine pattern in the semiconductor industry . The specific nitrogen-containing compound is effective as a substrate dependence reducing agent particularly in pattern formation using deep ultraviolet light or KrF excimer laser beams. It is sufficiently usable also for pattern formation using electron beams, X-rays, ArF excimer laser beams.

Claims: A method for reducing the substrate dependence of a resist composition comprising (a) either (i) a polymer capable of becoming alkali-soluble owing to the action of an acid, or (ii) an alkali-soluble polymer and a compound capable of becoming alkali-soluble owing to the action of an acid, or (iii) an alkali-soluble polymer and a compound capable of making the polymer difficultly alkali-soluble by crosslinking therewith owing to the action of an acid, (b) a compound capable of generating an acid upon irradiation with actinic radiation, and (c) a solvent capable of dissolving the above components, which method comprises incorporating into said composition a compound containing in the molecule at least one structure in which at least one of the direct links of -NH- is directly bonded to at least one member selected from -C(=O)-, -C(=S)- and -SO 2 -, said compound being a cyclic compound represented by the following formula [1], [2] or [3]: wherein X is an oxygen atom or a sulfur atom; and A is a saturated or unsaturated 5- or 6-membered ring which may contain an oxygen atom, a nitrogen atom or a sulfur atom as a constituent atom, and the carbon atoms constituting the ring may have a substituent; wherein X is an oxygen atom or a sulfur atom; D is a saturated or unsaturated 5- or 6-membered ring which may contain an oxygen atom, a nitrogen atom or a sulfur atom as a constituent atom, and the carbon atoms constituting the ring may have a substituent and the sulfur atom may have one or two oxo groups, and E is a saturated or unsaturated 6-membered ring or a fused ring polycyclic aromatic structure containing carbon atoms as constituent atoms, and a ring E is forming a fused ring with ring D; wherein G is a saturated or unsaturated 6- to 8-membered ring which may contain an oxygen atom as a constituent atom; and both J and L are independently a benzene ring, and the ring J and the ring L are independently forming a fused ring with the ring G; or an acyclic compound represented by the formula [21] or [22]: wherein X 1 and X 2 are independently a substituted or unsubstituted alkyl group or a phenyl group; n is an integer of 1 to 3; and X in a number of n are independently an oxygen atom or a sulfur atom; R 0 SO 2 NHR' wherein R 0 is a substituted or unsubstituted alkyl group or a substituted or unsubstituted aryl group; and R' is a hydrogen atom or an alkyl group. The method according to claim 1, wherein the cyclic compound is an acid imide compound derived from an aliphatic dibasic acid. The method according to claim 1, wherein the cyclic compound is an acid imide compound derived from an aromatic dibasic acid. The method according to claim 2, wherein the acid imide compound derived from an aliphatic dibasic acid is succinimide, maleimide or glutarimide. The method according to claim 3, wherein the acid imide compound derived from an aromatic dibasic acid is phthalimide, 1,2,3,6-tetrahydrophthalimide, 1,8-naphthalimide or 2,3-naphthalenedicarboximide. The method according to claim 1, wherein the acyclic compound is a sulfonamide derivative of the formula [22]. The method according to claim 6, wherein the sulfonamide derivative is toluenesulfonamide, benzenesulfonamide or methanesulfonamide. The method according to claim 1, wherein the compound of the formula [21] is N-benzoylbenzamide or diacetamide. Use of a compound containing in the molecule at least one structure in which at least one of the direct links of -NH- is directly bonded to at least one member selected from -C(=O)-, -C(=S)- and -SO 2 - as defined in claims 1-8 as an agent for reducing the substrate dependence of a resist. A resist composition comprising (a) a polymer capable of becoming alkali-soluble owing to the action of an acid, which is shown by the following formula [5] or [6]: wherein R and R 1 are independently a hydrogen atom or a lower alkyl group; R 2 and R 3 are independently a hydrogen atom, an alkyl group which may be substituted by one or more halogen atoms, or an aryl group, except for the case where both R 2 and R 3 are hydrogen atoms, and R 2 and R 3 may form together an alkylene ring; R 4 is an alkyl group which may be substituted by one or more halogen atoms, or an aralkyl group; R 5 is a cyano group, an esterified or non-esterified carboxyl group or a substituted or unsubstituted phenyl group; m and n' are independently a natural number; and k is zero or a natural number, provided that m > k; wherein R 6 is a hydrogen atom or a lower alkyl group; R 7 is a hydrogen atom, a lower alkyl group, a lower alkoxy group, an acyloxy group, a saturated heterocyclic oxy group, or a group represented by R 8 O-CO-(CH 2 ) Z -O- wherein R 8 is an alkyl group and z is zero or a natural number; R 21 is a hydrogen atom or a lower alkyl group; R 22 is a cyano group, an esterified or non-esterified carboxyl group, or a substituted or unsubstituted phenyl group, provided that in the case of R 7 being a hydrogen atom or a lower alkyl group, R 22 is an alkoxy group, a 5- or 6-membered saturated heterocyclic group or a substituted phenyl group having as the substituent a group represented by R 25 O-CO-(CH 2 ) j O- wherein R 25 is a lower alkyl group and j is 0 or 1; p and r are independently a natural number; and f is zero or a natural number, provided that p > f; (b) a compound capable of generating an acid upon irradiation with actinic radiation; (c) a compound containing in the molecule at least one structure in which at least one of the direct links of -NH- is directly bonded to at least one member selected from -C(=O)-, -C(=S)- and -SO 2 - as defined in claims 1-8; and (d) a solvent capable of dissolving these three components, provided that when the compound of (c) is saccharin, succinimide or phthalimide, the composition does not contain both a polymer shown by the general formula [5] and a polymer shown by the general formula [6] whose alkali-solubilities are different from each other, and provided that when (b) is triphenylsulfonium trifluoromethanesulfonate and (c) is saccharin, then (a) is not a mixture of poly(p-1-ethoxyethoxystyrene/p-hydroxystyrene/p-tert-butoxycarbonyloxystyrene) having a Mw of 20,000 and a Mw/Mn of 1.90 and poly(p-1-ethoxyethoxystyrene/p-hydroxystyrene/p-isopropoxycarbonyloxystyrene) having a Mw of 8,300 and a Mw/Mn of 1.60. A resist composition comprising an alkali-soluble polymer, a compound capable of becoming alkali-soluble owing to the action of an acid, a compound capable of generating an acid upon irradiation with actinic radiation which is not a quinonediazide, a compound containing in the molecule at least one structure in which at least one of the direct links of -NH- is directly bonded to at least one member selected from the group consisting of -C(=O)-, -C(=S)- and -SO 2 - as defined in claims 1-8 and a solvent capable of dissolving these four components. A resist composition comprising an alkali-soluble polymer, a compound capable of making the polymer difficultly alkali-soluble by crosslinking therewith owing to the action of an acid, a compound capable of generating an acid upon irradiation with actinic radiation which is not a quinonediazide, a compound containing in the molecule at least one structure in which at least one of the direct links of -NH- is directly bonded to at least one member selected from the group consisting of -C(=O)-, -C(=S)- and -SO 2 - as defined in claims 1-8, and a solvent capable of dissolving these four components. A process for forming a pattern comprising a step of coating a semiconductor substrate with the resist composition of any one of claims 10-12, a step of heating the coating to form a resist film, a step of exposing the resist film to radiation through a mask, and a step of developing the resist film with an alkali developing solution after heating the same if necessary.

Inventors: FUJIE HIROTOSHI, SOUKI TOHRU, UEHARA YUKIKO, FUJIE, HIROTOSHI, SOUKI, TOHRU, UEHARA, YUKIKO
Applicants: WAKO PURE CHEM IND LTD, WAKO PURE CHEMICAL INDUSTRIES, LTD.
Application year: 1998
Main classification: G03F7
IPC codes: G03F7