ACRYLATE RELEASE COMPOSITIONS AND SHEET MATERIALS HAVING A RELEASE COATING FORMED OF THE SAME

Abstract: Compositions having release properties include at least one cross-linking agent, at least one aliphatic acrylic ester, and at least one fluorinated compound. The composition is applied to the surface of a substrate and exposed to radiation to cross-link and cure the composition to form a polymer film on a surface of the substrate having release properties.

Description: ACRYLATE RELEASE COMPOSITIONS AND SHEET MATERIALS HAVING A RELEASE COATING FORMED OF THE SAME Field of the Invention This invention relates to release compositions and sheet materials which include a release layer formed of the release composition. Background of the Invention Silicone-containing materials are widely applied to film, paper and other substrates to impart release properties thereto. Although silicone- containing compositions can impart desirable release properties to the substrate to which it is applied, many release applications require a silicone-free release composition due to possible silicone contamination resulting from migration of silicone in the release coating onto an adjacent substrate and the subsequent contamination of other surfaces . Non-silicone release materials, such as fluorine-containing materials, can also impart desirable release properties to a substrate. Typically, however, a relatively large amount of the fluorinated material is required to provide the desired release properties. Since fluorinated materials are expensive, such coatings are not cost effective. In addition, typically conventional release compositions are solvent-based systems, which can be undesirable due to environmental concerns. Summary of the Invention The present invention is a composition which imparts release properties to a substrate to which it is applied. The compositions of the invention are not silicone-based and thus are suitable for applications in which silicone contamination is a concern. Further, the compositions of the invention are solvent-free and thus can be more environmentally acceptable. Still further, the compositions of the invention can provide effective release characteristics without requiring large quantities of expensive components. In the invention, the compositions include one or more ethylenically unsaturated cross-linking agents, preferably acrylate-containing cross-linking agents, capable of reacting upon exposure to radiation, to cross-link and form a cured coating on a substrate to which the composition has been applied. The compositions of the invention further include as a minor component, preferably about 1 to about 20 weight percent, more preferably about 1 to about 15 weight percent, and most preferably about 1 to about 7 weight percent, of at least one fluorinated compound, such as a fluorinated acrylate. In addition, the compositions of the invention include at least one aliphatic acrylic ester, preferably a long chain alkyl ester containing 10 to 24 carbon atoms, such as lauryl acrylate. The fluorinated compound and the cross- linking agent and aliphatic acrylic ester are partially incompatible so that the fluorinated compound migrates to the surface of the coating composition prior to curing. When the composition is exposed to radiation, the cross-linking agent reacts to create a cross-linked network. Although not wishing to be bound by any explanation of the invention, it is believed that the aliphatic acrylic ester can provide a synergistic effect with the fluorinated compound so that reduced quantities of the fluorinated compound can be used to achieve release properties comparable to compositions which do not include the aliphatic acrylic ester and which include the fluorinated compound in a higher weight percent. The resultant cured coating has a highly fluorinated low surface energy abhesive surface, despite the fact that only a relatively small amount of fluorinated compound is used. The present invention also provides sheet materials which include a sheet material substrate and a release coating adhered to a surface of the sheet material and formed of the radiation cured cross-linked release composition of the invention. Detailed Description of the Invention The present invention now will be described more fully as applied to several specific embodiments. It should be understood, however, that the specific embodiments are provided only for purposes of providing a better understanding of the invention and how it may be practiced in various ways. The specific embodiments described herein are merely examples and should not be construed as limiting or constricting the scope of the invention. The radiation curable release compositions of the present invention include at least one poly- ethylenically unsaturated cross-linking agent; at least one aliphatic acrylic ester; and at least one cross- linkable fluorinated compound. The ethylenically unsaturated cross-linking agent is capable of reacting and cross-linking upon exposure to radiation to form a polymer network overlaying and adhered to the surface of a substrate. The average number of functionalities, available for cross-linking, for the cross-linking agent, should be more than two. Single component cross-linking agents having three or more functional groups and any combination of mixtures of the same are possible cross-linking agent combinations. Materials with two functional groups can also be added to the above combinations. The cross-linking agents include acrylate functionalized monomers and/or oligomers. Exemplary acrylate functionalized cross- linking agents include diacrylates, such as 1,6- hexanediol diacrylate, 1, 4-butanediol diacrylate, ethylene glycol diacrylate, diethylene glycol diacrylate, tetraethylene glycol diacrylate, tripropylene glycol diacrylate, neopentyl glycol diacrylate, 1, 4-butanediol dimethacrylate, poly (butanediol) diacrylate, tetraethylene glycol dimethacrylate, 1,3 -butylene glycol diacrylate, triethylene glycol diacrylate, triisopropylene glycol diacrylate, polyethylene glycol diacrylate, and bisphenol A dimethacrylate; triacrylates , such as trimethylolpropane triacrylate, trimethylolpropane trimethacrylate, pentaerythritol monohydroxy triacrylate, and trimethylolpropane triethoxy triacrylate; tetraacrylates, such as pentaerythritol tetraacrylate, and di-trimethylolpropane tetraacrylate; and pentaacrylates, such as dipentaerythritol (monohydroxy) pentaacrylate, and the like and mixtures thereof. These multifunctional acrylate monomers are commercially available from Aldrich Chemical Company, Inc., Milwaukee, Wis. Examples of multifunctional acrylate oligomers include epoxy acrylates, such as bisphenol A epoxy diacrylate, available from Sartomer Company, Inc. of Exton, Pa. and sold under the designation CN104; urethane acrylates, such as hexafunctional aromatic urethane acrylate with an acrylated polyol diluent which is sold under the designation Ebecryl ® 220 by UBC Radcure, Inc. of Louisville, Ky. ; aliphatic urethane diacrylates, such as that which is available under the designation Ebecryl ® 230 from UBC Radcure, Inc. of Louisville, Ky. ; polyester acrylates, such as tetrafunctional polyester acrylate which is sold under the designation Ebecryl ® 80 by UBC Radcure, Inc. of Louisville, Ky. and also sold under the designation Photomer 5018 by Henkel, Inc.; polybutadiene diacrylates, such as that available from Sartomer Company, Inc. of Exton, Pa. under the designation CN300; and the like and mixtures thereof. Those skilled in the art will recognize that the terms "oligomer" and "polymer" are frequently used interchangeably. Although "oligomer" is generally used to describe a relatively short polymer, the term has no generally accepted definition with respect to the number of repeating monomer units. As used herein, then the term "oligomer" is meant to include molecules that may also be properly referred to as polymers. Typically-, the cross-linking agent is present in an amount from about 10 to about 90 weight percent based on the total weight of the composition, and more preferably from about 55 to about 75 weight percent. Aliphatic acrylic esters useful in the present invention include monomeric and/or oligomeric acrylates. The acrylic esters are characterized as having less than two acrylate functional groups per molecule in contrast to the acrylate cross-linking agents described above. Acrylic esters are derivatives of both acrylic acid and methacrylic acid. Exemplary acrylic esters include long chain alkyl esters having 10 to 24 carbon atoms, the alkyl groups of which can be straight chained or branched. Representative aliphatic acrylic esters useful in the invention include, but are not limited to, octyl acrylate, isodecyl acrylate, tridecyl acrylate, stearyl acrylate, lauryl acrylate, and the like and mixtures thereof. The compositions of the invention can include the acrylic ester in amounts ranging from about 5 to about 60 weight percent based on the total weight of the composition, and preferably from about 20 to about 40 weight percent. The fluorinated component of the compositions of the invention can be any of many fluorinated compounds known in the art . Examples of such compounds useful in the invention include but are not limited to polyfluorinated alkyl acrylates and methacrylates, poly (fluorooxyalkylene) acrylates and methacrylates, and the like and mixtures thereof. Fluoroacrylates useful as the release imparting agent in the compositions of the invention include those described in U.S. Patent No. 4,321,404, the entire disclosure of which is hereby incorporated by reference, and are commercially available from 3M. Other functionalized fluorinated compounds can also be used in the invention, such as, but not limited to, fluorinated polyurethanes, fluorinated polyamides, and the like and mixtures thereof. ' S ch functionalized compounds are commercially available. The compositions of the invention are advantageous over prior release compositions because of the decreased quantities of fluorinated compounds required to impart desirable release properties thereto as compared to conventional release compositions. Preferably, the compositions of the invention include about 1 to about 20 weight percent, more preferably about 1 to about 15 weight percent, and most preferably about 1 to about 7 weight percent, of the fluorinated compound based on the total weight of the composition. In contrast, conventionally, release compositions which include fluorinated compounds as the release imparting component require much larger quantities (for example from 25 to 100 weight percent) to impart useful release properties to a substrate to which that composition was applied. Although not wishing to be bound by any explanation of the invention, the inventors have found that incorporation of an aliphatic acrylic ester as described above in combination with a cross-linking agent and a fluorinated compound can result in decreased quantities of the fluorinated compound to be required to provide release properties comparable to that provided by compositions without an aliphatic acrylic ester and with higher quantities of a fluorinated compound. The compositions of the invention can be prepared by preheating the components to a temperature ranging from about 100°F to about 140°F, for a period of about 60 to 90 minutes, before mixing, and thereafter subjecting the composition to conditions of high shear to assure good mixture of the components. Various conventional additives as known in the art, such as anchorage agents, wetting agents, pigments, ultraviolet absorbers, dyes, and the like can be added to the compositions, in conventional amounts. When visible light or ultraviolet radiation is used to cure the release compositions of the invention, the compositions also include a source of free radicals, i.e., a material which liberates free radicals on exposure to radiation. Such compounds are also known in the art as photoinitiators. Exemplary photoinitiators include benzil dimethyl ketal, benzoin, benzoin alkyl ethers, acyloin derivatives, benzophenone, acetophenone, Michler's ketone, and derivatives of these compounds. The photoinitiator can be present in conventional amounts, typically about 1 to about 5 weight percent. While not essential to the curing process, photosensitizers may be added to make the curing process more efficient. The composition of the invention can also be cured using other radiation sources such as electron beam or X-ray radiation, in which case, typically, a photoinitiator is not required. The release composition is then applied to a suitable sheet material substrate using any of the techniques known in the art, such as, but not limited to, roll coating, gravure coating, multi-roll coating, and the like and other coating processes. After the uncured composition is applied to a surface of a sheet material substrate, the composition can be cured by exposure to radiation under conditions suitable for converting the composition into a cross-linked polymer film which is adhered to the surface of the substrate. The sheet material can be any conventional substrate to which a release coating is applied, including polymer films such as polyethylene, polypropylene and polyethylene terephthalate films, paper substrates, polyolefin-coated paper substrates, clay coated paper substrates, and the like. The present invention will be further described by the following non-limiting examples. EXAMPLES Six formulations were prepared using the materials of Table 1. TABLE 1 Notes: 1 Supplier's tradename. 2 Generalized name of the component as provided by the supplier, indicating that the component may include mixtures. The compositions of six formulations are set forth in Table 2 below. For each composition, all of the raw materials except Darocur 1173, Irgacure 907 and ITX were warmed at 140 °F prior to mixing for a period of 60 to 90 minutes, and thereafter the composition was subjected to conditions of high shear to assure good mixture of the components . TABLE 2 Note: Darocur 1173, Irgacure 907, and ITX are added to each of the formulations in the amount of 2 , 2, and 0.2 wt . %, respectively, of the total batch size. Each formulation was applied to a web of high density polyethylene coated paper using an offset gravure coating technique. The coating was cured using ultraviolet light in a nitrogen inerted chamber. Each sample was evaluated for release by several tests described below. The release force values for the different tests were measured using a release tester made by Testing Machine Inc. In the tests designated "STM 44" and "STM 45", a solvent acrylic adhesive from National Starch (80-1068) and a cross-linking adhesive from Ashland (80-1085) , respectively, were coated onto the release coating using a Byrd bar with a five mil gap and allowed to dry for five minutes in air and subsequently for ten minutes at 150°F in a forced air oven. A one mil polyethylene terephthalate film was laminated to the adhesive surface, from which were cut 2" wide, 10" long strips. The force (grams per two inch width) required to peel the polyethylene terephthalate film, together with the adhesive from the release coated substrate at an angle of 135° and at various peel rates, was measured. Such release force tests were done for laminate samples aged at room temperature and at 120°F, for different lengths of time (immediate, 1 day, 3 days and 7 days) . The test designated "STM 42" is a subsequent adhesive test based on the 80-1068 adhesive. In this test, the polyester film/adhesive strip removed from the release layer o-f Test STM 44 was applied to a stainless steel surface. The strip was peeled together with the adhesive from the stainless steel surface at an angle of 180° and at a peel rate of 12 IPM. A control sample was prepared by replacing the release layer with the polyester facestock. The control sample was prepared in a manner similar to that (described above) used to prepare the test sample for the release layer. The percent subsequent adhesion was calculated as follows: % subsequent adhesion = (Test avg., g)/(Control avg., g) X 100. In the test designated "STM 72A-D, " a rubber based tape (TESA 7476 tape) commercially available from TESA, Inc., was applied to the release coating. The release force (gm/in width) required to peel a strip of 1" width x 6" long of the tape together with the adhesive from the release layer, at an angle of 180°, was measured. Peel rates were 12 IPM, 300 IPM, 600 IPM and 1200 IPM, for results A, B, C, and D, respectively. In the test designated "J&J", a Johnson & Johnson ZONAS tape was applied to the release coating. The release force (gm/inch width) required to peel a strip of 1" width x 6" long of the tape together with the adhesive from the release layer, at an angle of 180° and at a peel rate of 12 IPM, was measured. In the test designated "TESA 7475," an acrylic based tape (TESA 7475 tape) , commercially available from TESA, Inc., was applied to the release coating. The release force (gm/inch width) required to peel a strip of 1" width x 6" long of the tape together with the adhesive from the release layer, at an angle of 180° and at various peel rates, was measured. The results shown in the following Tables are the average of three test samples . Table 3 presents "STM 44" release test results at four peel rates for coated samples (formulations 1, 2 -and 3) aged, at room temperature and at 120°F, for different lengths of time. Table 4 presents "TESA 7475" release test results at two peel rates for samples (formulations 1, 2 and 3) aged, at room temperature and at 120°F, for different lengths of time. Table 5 presents "STM 45", "STM 42", "STM 72A- D", "J&J", and "TESA 7475" release test results at the peel rates indicated in the table (formulations 1, 2 and 3) . TABLE 3 FORMULATION STM 44 STM 44 STM 44 STM 44 (room temp., 12 IPM 2 ) (room temp., 300 IPM) (room temp., 600 IPM) (room temp., 1200 IPM) Release force, g/2 in width Release force, g/2 in width Release force, g/2 in width Release force, g/2 in width Immed. Day 1 Day 3 Day 7 Immed. Day 1 Day 3 Day 7 Immed. Day 1 Day 3 Day 7 Immed. Day 1 Day 3 Day 7 1 (600 fpm') 744 1044 1386 1695 397 465 529 511 184 247 213 221 214 209 263 232 2 (600 fpm) 828 1152 1165 1143 203 586 555 753 133 179 186 156 226 158 136 139 3 (600 fpm) 912 1443 1382 1383 263 505 566 555 170 127 191 205 175 133 195 171 3 (1000 fpm) 1005 1068 1033 874 501 307 308 291 168 150 180 169 138 190 180 153 FORMULATION STM 44 STM 44 STM 44 STM 44 (120°F, 12 IPM) (120°F, 300 IPM) (120°F, 600 IPM) (120°F, 1200 IPM) Release force, g/2 in width Release force, g/2 in width Release force, g/2 in width Release force, g/2 in width Immed. Day 1 Day 3 Day 7 Immed. Day 1 Day 3 Day 7 Immed. Day 1 Day 3 Day 7 Immed. Day 1 Day 3 Day 7 1 (600 fpm) 744 1395 1098 1109 397 321 286 301 184 233 243 263 214 262 271 263 2 (600 fpm) 828 1135 1146 1189 203 258 440 700 133 205 209 241 226 156 146 148 3 (600 fpm) 912 1273 1054 1041 263 181 288 280 170 210 182 147 175 183 155 132 3 (1000 fpm) 1005 1101 997 1279 501 379 299 286 171 194 286 218 138 214 237 195 "fpm" = feet per minute. "IPM" = inches per minute. TABLE 4 TABLE 5 For each of formulations 1, 2 and 3, the above data shows that the release force is much higher at the peel rates of 12 IPM than at the higher peel rates. No release was observed with the rubber based tape 7476 for the samples prepared using formulations 1, 2 and 3. The cross-linking adhesive Ashland 1085 (STM 45) showed very high release values at 12 IPM compared to the release values shown by the solvent acrylic adhesive from National Starch 1068 (Test STM 44) and the release values shown by the solventless acrylic adhesive tape TESA 7475. Analysis of the results for the first three formulations indicated certain directions for additional formulations. Formulations 4, 5, and 6 were prepared based on this analysis and applied to a polyethylene coated paper, cured and tested for release. Each of the formulations 4, 5 and 6 were coated at 600 and 1000 FPM to provide six test results. The tests performed were STM 44 at room temperature and at 120°F, STM 42 at room temperature, STM 45 at room temperature, STM 72 at room temperature and TESA 7475 at room temperature. For each test, four stripping speeds (12 IPM, 300 IPM, 600 IPM and 1200 IPM) and four different aging times (immediately, one day, three days, and seven days) were used. The results are set forth in Table 6 below. TABLE 6 TABLE 6 (Con't) STM 45 TESA STM (Room 7475 72A-D Temp.) (120°F) FORMULATION 12 IPM 300 IMP 600 IMP 1200 IMP 12 IPM 300 IMP 600 IMP 1200 IMP 12 IPM 300 IMP 600 IMP 1200 IMP IMMED 536 184 137 1 12 210 59 44 37 281 149 189 173 4 (600 fpm) 1 DAY 495 172 115 117 223 58 46 46 3 DAY 399 161 159 113 196 61 50 40 7 DAY 503 141 134 105 191 64 52 45 IMMED 583 208 132 130 230 70 50 40 309 182 217 181 4 (1000 fpm) 1 DAY 582 175 120 102 241 78 56 43 3 DAY 594 213 140 118 268 73 57 52 7 DAY 486 213 136 146 195 84 60 51 IMMED 319 176 164 121 233 90 60 51 354 229 266 234 5 (600 fpm) 1 DAY 893 176 163 135 234 98 73 56 3 DAY 841 142 157 151 215 92 65 54 7 DAY 672 207 185 119 237 97 81 69 IMMED 683 151 131 133 228 81 67 68 293 222 273 257 5 (1000 fpm) 1 DAY 546 147 153 168 238 96 82 71 3 DAY 595 202 160 141 257 102 81 72 7 DAY 539 180 164 142 264 95 85 82 IMMED 370 146 131 120 216 75 65 52 302 200 230 252 6 (600 fpm) 1 DAY 661 130 159 148 234 81 67 64 3 DAY 537 210 183 1 15 213 89 74 58 7 DAY 727 212 145 144 232 99 82 70 IMMED 595 371 174 163 217 87 63 69 238 235 210 226 6 (1000 fpm) 1 DAY 943 239 186 167 274 89 72 74 3 DAY 485 31 1 163 96 286 91 78 63 7 DAY 593 212 151 171 240 91 82 70 In each of formulations 4, 5 and 6, the release force values decreased substantially. In addition, release was observed with the rubber based tape 7476. Aging effects for all of the samples were small and the release force values were stable over time. Further, the effect of changing speed of the web from 600 FPM to 1000 FPM on the release values was not significant. Test STM 45 with the cross-linking adhesive gave higher release values than with the other tests, and STM 44 test results showed very little impact of temperature on the release force values . The foregoing examples are illustrative of the present invention and are not to be construed as limiting thereof. The invention is defined by the following claims, with equivalents of the claims to be included therein.

Claims: THAT WHICH IS CLAIMED IS: 1. A radiation curable composition having release properties, comprising: at least one poly-ethylenically unsaturated cross- linking agent; at least one aliphatic acrylic ester; and at least one cross-linkable fluorinated compound. 2. The composition of Claim 1, wherein said composition comprises about 1 to about 20 weight percent of said at least one cross-linkable fluorinated compound . 3. The composition of Claim 2, wherein said composition comprises about 1 to about 15 weight percent of said at least one cross-linkable fluorinated compound . 4. The composition of Claim 3, wherein said composition comprises about 1 to about 7 weight percent of said at least one cross-linkable fluorinated compound . 5. The composition of Claim 1, wherein said composition comprises about 55 to about 75 weight percent of said at least one cross-linking agent and about 20 to about 40 weight percent of said at least one aliphatic acrylic ester. 6. The composition of Claim 1, wherein said at least one unsaturated cross-linking agent comprises an acrylate functionalized cross-linking agent. 7. The composition of Claim 6, wherein said functionalized acrylate cross-linking agent comprises a compound selected from the group consisting of diacrylates, triacrylates, tetraacrylates, 5 pentaacrylates, epoxy acrylates, urethane acrylates, aliphatic urethane diacrylates, polyester acrylates, polybutadiene diacrylates, and mixtures thereof. 8. The composition of Claim 7, wherein said functionalized acrylate cross-linking agent comprises a compound selected from the group consisting of 1,6- hexanediol diacrylate, 1, -butanediol diacrylate, 5 ethylene glycol diacrylate, diethylene glycol diacrylate, tetraethylene glycol diacrylate, tripropylene glycol diacrylate, neopentyl glycol diacrylate, 1, 4-butanediol dimethacrylate, poly (butanediol) diacrylate, tetraethylene glycol 10 dimethacrylate, 1,3-butylene glycol diacrylate, triethylene glycol diacrylate, triisopropylene glycol diacrylate, polyethylene glycol diacrylate, bisphenol A dimethacrylate, trimethylolpropane triacrylate, trimethylolpropane trimethacrylate, pentaerythritol ■15 monohydroxy triacrylate, trimethylolpropane triethoxy triacrylate, pentaerythritol tetraacrylate, di- trimethylolpropane tetraacrylate, dipentaerythritol (monohydroxy) pentaacrylate, bisphenol A epoxy diacrylate, hexafunctional aromatic urethane acrylate, 20 tetrafunctional polyester acrylate, polybutadiene diacrylate, and mixtures thereof. 9. The composition of Claim 1, wherein said at least one aliphatic acrylic ester comprises at least one straight chain or branched alkyl ester containing 10 to 24 carbon atoms. 10. The composition of Claim 9, wherein said at least one aliphatic acrylic ester comprises a compound selected from the group consisting of octyl acrylate, isodecyl acrylate, tridecyl acrylate, stearyl acrylate, lauryl acrylate, and mixtures thereof. 11. The composition of Claim 1, wherein said at least one cross-linkable fluorinated compound comprises at least one cross-linkable fluorinated acrylate. 12. The composition of Claim 11, wherein said at least one cross-linkable fluorinated acrylate comprises a compound selected from the group consisting of polyfluorinated alkyl acrylates and methacrylates, poly (fluorooxyalkylene) acrylates and methacrylates and mixtures thereof. 13. A radiation curable composition having release properties, comprising: about 55 to about 75 weight percent of at least one acrylate containing cross-linking agent; about 20 to about 40 weight percent of at least one straight chain or branched aliphatic alkyl ester containing 10 to 24 carbon atoms; and about 1 to about 20 weight percent of at least one cross-linkable fluorinated acrylate selected from the group consisting of polyfluorinated alkyl acrylates and methacrylates, poly (fluorooxyalkylene) acrylates and methacrylates, and mixtures thereof. 14. A sheet material comprising: a sheet material substrate; and a release coating overlying and adhered to a surface of said sheet material substrate, said coating comprising a cross-linked polymer derived from a cross- linkable composition comprising at least one poly- ethylenically unsaturated cross-linking agent, at least one aliphatic acrylic ester, and at least one cross- linkable fluorinated compound. 15. The sheet material of Claim 14, wherein said release coating is derived from a radiation cured cross-linked polymer. 16. The sheet material of Claim 14, wherein said at least one cross-linkable fluorinated compound is present in an amount of about 1 to about 20 weight percent . 17. The sheet material of Claim 16, wherein said at least one cross-linkable fluorinated compound is present in an amount of about 1 to about 15 weight percent . 18. The sheet material of Claim 17, wherein said at least one cross-linkable fluorinated compound is present in an amount of about 1 to about 7 weight percent . 19. The sheet material of Claim 14, wherein said at least one ethylenically unsaturated cross-linking agent is present in an amount of about 55 to about 75 weight percent and wherein said at least one aliphatic acrylic ester is present in an amount of about 20 to about 40 weight percent. 20. The sheet material of Claim 14, wherein said poly-ethylenically unsaturated cross-linking agent comprises at least one acrylate containing cross- linking agent. 21. The sheet material of Claim 14, wherein said at least one aliphatic acrylic ester comprises at least one straight chain or branched alkyl ester containing 10 to 24 carbon atoms. 22. The sheet material of Claim 21, wherein said at least one alkyl ester comprises a compound selected from the group consisting of octyl acrylate, isodecyl acrylate, tridecyl acrylate, stearyl acrylate, lauryl acrylate, and mixtures thereof. 23. The sheet material of Claim 14, wherein said at least one cross-linkable fluorinated compound comprises at least one cross-linkable fluorinated acrylate . 24. The sheet material of Claim 23, wherein said at least one cross-linkable fluorinated acrylate comprises a compound selected from the group consisting of polyfluorinated alkyl acrylates and methacrylates, poly (fluorooxyalkylene) acrylates and methacrylates, and mixtures thereof . 25. The sheet material of Claim 14, wherein said sheet material substrate comprises a polymer film. 26. The sheet material of Claim 25, wherein said polymer film is a polyethylene, polypropylene, or polyethylene terephthalate film. 27. The sheet material of Claim 14, wherein said sheet material substrate is a paper substrate. 28. The sheet material of Claim 14, wherein said sheet material substrate is a polyolefin coated paper substrate .

Inventors: DHOOT SUNIL M, THOMPSON DANNY C, DHOOT, SUNIL, M., THOMPSON, DANNY, C.
Applicants: DHOOT SUNIL M, REXAM RELEASE INC, THOMPSON DANNY C, DHOOT, SUNIL, M., REXAM RELEASE, INC., THOMPSON, DANNY, C.
Application year: 1998
Main classification: C08F220
IPC codes: C08F290, C09D4