Process for preparing polysulfide silanes

Abstract: Polysulfide silanes: (RO) 3 SiC 3 H 6 S x C 3 H 6 Si(OR) 3 are reacted with an anhydrous sulfur compound: M 1 2 S or M 2 S and a halogenoalkoxysilane: XC 3 H 6 Si(OR) 3 to form polysulfide silanes: (RO) 3 SiC 3 H 6 S y C 3 H 6 Si(OR) 3 wherein R is methyl or ethyl, x is a positive number of 3 to 6 on the average, M 1 is an alkali metal or ammonium, M 2 is an alkaline earth metal or zinc, X is a halogen, and y is a positive number less than x on the average. Short chain polysulfide silanes can be prepared with the industrial advantages of safety, high yields and low cost.

Description: This invention relates to a process for preparing polysulfide silanes, especially short chain polysulfide silanes. Bis(triethoxysilylpropyl) tetrasulfide is commonly used in silica-blended tires as an agent for coupling rubber with silica. This compound, however, has the problem that when it is kneaded with rubber and silica at elevated temperature, it causes the blend to increase its Mooney viscosity so that the blend becomes difficult to work. To overcome this problem, short chain polysulfide silanes such as bis(triethoxysilylpropyl) disulfide were proposed. JP-A 169774/1997 discloses a process for preparing a disulfide silane using sodium cyanide (NaCN). This process, however, uses a toxic reagent. The present invention pertains to the preparation of short chain polysulfide silanes from polysulfide silanes of the following general formula (1): (RO) 3 SiC 3 H 6 S x C 3 H 6 Si(OR) 3 wherein R is methyl or ethyl, and letter x is a positive number of 3 to 6 on the average, while changing the distribution of sulfide chains thereof, and especially a process for preparing from polysulfide silanes of formula (1) short chain polysulfide silanes having a shorter sulfide chain than the starting polysulfide silanes. Therefore, an object of the present invention is to provide a novel process for preparing, from starting polysulfide silane(s) of formula (1), product polysulfide silane(s) having a shorter average sulfide chain than the starting polysulfide silane(s), especially polysulfide silanes averaging 2 or 3-member sulfide chains. According to the invention, there is provided a process for preparing polysulfide silanes by reacting polysulfide silanes of the following general formula (1): (RO) 3 SiC 3 H 6 S x C 3 H 6 Si(OR) 3 wherein R is methyl or ethyl, and letter x is a positive number of 3 to 6 on the average, especially about 4 on the average, with at least one anhydrous sulfur compound selected from sulfur compounds of the formulae: M 1 2 S and M 2 S wherein M 1 is an alkali metal or ammonium and M 2 is an alkaline earth metal or zinc, and a halogenoalkoxysilane of the following general formula (2): XC 3 H 6 Si(OR) 3 wherein X is a halogen atom and R is methyl or ethyl, to form polysulfide silanes of the following general formula (3): (RO) 3 SiC 3 H 6 S y C 3 H 6 Si(OR) 3 wherein R is as defined above and y is a positive number less than x (that is, x > y) on the average. Preferably, the polysulfide silanes of formula (1) are first reacted with the anhydrous sulfur compound, optionally at an elevated temperature, until a polysulfide distribution reaches equilibrium, and the halogenoalkoxysilane of formula (2) is then reacted therewith, thereby forming short chain polysulfide silanes of formula (3) wherein y is a positive number of 2 to 3 on the average. The short chain polysulfide silanes can be produced in a safe manner, in high yields and at low cost. DETAILED DESCRIPTION Polysulfide silanes of formula (3) are obtained by reacting polysulfide silanes of formula (1), an anhydrous sulfur compound of the formulae: M 1 2 S or M 2 S and a halogenoalkoxysilane of formula (2). The polysulfide silanes used as the starting reactant are represented by the general formula (1): (RO) 3 SiC 3 H 6 S x C 3 H 6 Si(OR) 3 wherein R is methyl or ethyl, and x averages (on a mole basis) from 3 to 6. Polysulfide silanes of formula (1) wherein x is 4 or averages about 4 are especial suitable because they are inexpensive. The anhydrous sulfur compound is selected from sulfides of the formulae: M 1 2 S and M 2 S wherein M 1 is an alkali metal or ammonium and M 2 is an alkaline earth metal or zinc. Exemplary sulfides are Na 2 S, K 2 S, Li 2 S, (NH 4 ) 2 S, CaS, MgS and ZnS, with the Na 2 S being especially preferred. In one preferred embodiment of the invention, the polysulfide silanes of formula (1) are first reacted with the sulfide. For this reaction, a solvent may or may not be used. When used, those solvents which allow the sulfide to be partially dissolved in the reaction system are advantageous. Useful solvents include aliphatic hydrocarbon solvents such as pentane and hexane, aromatic hydrocarbon solvents such as benzene, toluene and xylene, ethers such as diethyl ether and dibenzyl ether, esters and ketones. Advantageous solvents are alcohols such as methanol, ethanol, propanol, butanol, benzyl alcohol and phenol, with the methanol and ethanol being most advantageous. The reaction temperature may range from room temperature to 150°C, preferably from 60°C to 100°C. Reaction is advantageously carried out under solvent reflux, especially under ethanol reflux. The reaction time is 30 minutes or longer although a reaction time within 2 hours is sufficient under ethanol reflux conditions. The reaction of the polysulfide silanes of formula (1) with the sulfide is an equilibration reaction. For example, when a tetrasulfide silane is reacted with Na 2 S under ethanol reflux, the reaction proceeds according to the following scheme. A x Na 2 S + B x (C 2 H 5 O) 3 SiC 3 H 6 S 4 C 3 H 6 Si(OC 2 H 5 ) 3 → A x Na 2 S c + B x (C 2 H 5 O) 3 SiC 3 H 6 S c C 3 H 6 Si(OC 2 H 5 ) 3 Herein, c is c = (A + 4B)/(A + B). For instance, when 1 mol of tetrasulfide silane is reacted with 1 mol of Na 2 S, c is equal to 2.5. It is evident from the above reaction scheme that when a tetrasulfide silane is used in the inventive process, a polysulfide silane product having a desired number of polysulfide chains in the range from an average disulfide silane to an average tetrasulfide silane can be obtained by controlling the reaction molar ratio of the tetrasulfide silane to Na 2 S. In the preferred embodiment of the present invention, after the completion of the above equilibration reaction, i.e. after substantial equilibrium is reached, the reaction product is reacted with a halogenoalkoxysilane of the following general formula (2): XC 3 H 6 Si(OR) 3 wherein X is a halogen atom and R is methyl or ethyl. The amount of the halogenoalkoxysilane added may be determined as appropriate. For example, after the completion of equilibration reaction according to the above reaction scheme, 2A mol of the halogenoalkoxysilane is reacted, thereby forming (A + B) mol of a polysulfide silane. The reaction temperature may range from room temperature to 150°C, preferably from 60°C to 100°C. Reaction is advantageously carried out in the above-described solvent, especially under ethanol reflux. Usual reaction time is 30 minutes to 20 hours, preferably 2 to 7 hours. Then solvent is removed e.g. distilled off in vacuum, and the salt formed is filtered off. The end product, that is, a polysulfide silane of the general formula (3): (RO) 3 SiC 3 H 6 S y C 3 H 6 Si(OR) 3 is obtained in high yields. Herein R is as defined above and y is a positive number satisfying x > y on the average, especially a positive number of 2 to 3 on the average. Accordingly, the process of the invention is useful in the preparation of short chain polysulfide silanes of formula (3) wherein y is a positive number of 2 to 3 on the average. According to the present invention, from polysulfide silanes of formula (1), short chain polysulfide silanes having a shorter average polysulfide chain than the starting polysulfide silanes can be prepared with industrial advantages including safety, high yields and low cost. EXAMPLE Examples of the invention are given below by way of illustration and not by way of limitation. Percentages are by weight. Example 1 A 3-liter flask was charged with 538 g (1 mol) of an average tetrasulfide silane represented by the average compositional formula: (CH 3 CH 2 O) 3 SiC 3 H 6 S 4 C 3 H 6 Si(OCH 2 CH 3 ) 3 , 78 g (1 mol) of anhydrous sodium sulfide, and 400 g of ethanol. Reaction was effected for 1 hour under ethanol reflux. Subsequently, 481 g (2 mol) of chloropropyltriethoxysilane was added dropwise under ethanol reflux. The reaction solution was ripened for 5 hours under ethanol reflux. The ethanol was distilled off in vacuum, and the sodium chloride formed was filtered off. There was obtained 940 g (yield 96%) of a polysulfide silane product having an average sulfide chain number of 2.5 represented by the following average compositional formula. (CH 3 CH 2 O) 3 SiC 3 H 6 S 2.5 C 3 H 6 Si(OCH 2 CH 3 ) 3 The starting reactant and the polysulfide silane product were analyzed by super-critical chromatography, finding that they were mixtures of polysulfide silanes as reported below. Starting reactant Disulfide silane 18% Trisulfide silane 30% Tetrasulfide silane 25% Pentasulfide silane 17% Hexasulfide silane 6% Heptasulfide silane 3% Octasulfide silane 1% Product Disulfide silane 51% Trisulfide silane 31% Tetrasulfide silane 13% Penta and higher sulfide silanes (≧ S 5 ) 5% Example 2 The procedure of Example 1 was repeated except that the average tetrasulfide silane and anhydrous sodium sulfide were replaced by 570 g (1 mol) of an average pentasulfide silane and 110 g (1 mol) of anhydrous potassium sulfide, respectively. There was obtained 950 g (yield 94%) of a trisulfide silane product having an average sulfide chain number of 3. The starting reactant and the sulfide silane product were found to be mixtures as reported below. Starting reactant Disulfide silane 4% Trisulfide silane 18% Tetrasulfide silane 33% Pentasulfide silane 29% Hexasulfide silane 14% Heptasulfide silane 5% Octasulfide silane 1% Product Disulfide silane 33% Trisulfide silane 32% Tetrasulfide silane 19% Penta and higher sulfide silanes (≧ S 5 ) 16% Example 3 The procedure of Example 1 was repeated except that the anhydrous sodium sulfide was replaced by anhydrous potassium sulfide. There was obtained 930 g (yield 95%) of a polysulfide silane product having an average sulfide chain number of 2.5. The polysulfide silane product was found to be a mixture as reported below. Product Disulfide silane 53% Trisulfide silane 31% Tetrasulfide silane 12% Penta and higher sulfide silanes (≧ S 5 ) 4% Example 4 The procedure of Example 1 was repeated except that the average tetrasulfide silane of ethoxy type was replaced by 510 g (1 mol) of an average tetrasulfide silane of methoxy type. There was obtained 920 g (yield 94%) of a polysulfide silane product having an average sulfide chain number of 2.5. The polysulfide silane product was found to be a mixture as reported below. Product Disulfide silane 55% Trisulfide silane 30% Tetrasulfide silane 11% Penta and higher sulfide silanes (≧ S 5 ) 4% Example 5 The procedure of Example 1 was repeated except that the anhydrous sodium sulfide was replaced by 72 g (1 mol) of anhydrous potassium sulfide. There was obtained 930 g (yield 95%) of a polysulfide silane product having an average sulfide chain number of 2.5. The polysulfide silane product was found to be a mixture as reported below. Product Disulfide silane 56% Trisulfide silane 29% Tetrasulfide silane 11% Penta and higher sulfide silanes (≧ S 5 ) 4% Japanese Patent Application No. 279656/1997 is incorporated herein by reference. Although some preferred embodiments have been described, many modifications and variations may be made thereto in the light of the above teachings. It is therefore to be understood that within the scope of the appended claims, the invention may be practiced otherwise than as specifically described.

Claims: A process comprising reacting starting polysulfide silanes of the following general formula (1) : (RO) 3 SiC 3 H 6 S X C 3 H 6 Si(OR) 3 wherein R is methyl or ethyl, and x averages from 3 to 6, with at least one anhydrous sulfur compound selected from sulfur compounds of the formulae M 1 2 S and M 2 S wherein M 1 is an alkali metal or ammonium and M 2 is an alkaline earth metal or zinc, and halogenoalkoxysilane of the following general formula (2) : XC 3 H 6 Si(OR) 3 wherein X is a halogen atom and R is methyl or ethyl, to form product polysulfide silanes of the following general formula (3) : (RO) 3 SiC 3 H 6 S y C 3 H 6 Si(OR) 3 wherein R is as defined above and y averages less than x. The process of claim 1 comprising first reacting the starting silanes of formula (1) with said at least one anhydrous sulfur compound until the polysulfide distribution therein reaches substantial equilibrium, and then reacting the halogenoalkoxysilane of formula (2) therewith to form said product polysulfide silanes of formula (3) wherein y averages from 2 to 3. A process of claim 2 wherein x averages about 4 and X is chloro.

Inventors: ICHINOHE SHOJI, YAMAMOTO AKIRA, YANAGISAWA HIDEYOSHI, ICHINOHE, SHOJI, YAMAMOTO, AKIRA, YANAGISAWA, HIDEYOSHI, Ichinohe, Shoji, Silicone-Elec. Materials Lab., Yamamoto, Akira, Silicone-Electron. Materials Lab., Yanagisawa, Hideyoshi, Silic.-Elec. Materials Lab.
Applicants: SHINETSU CHEMICAL CO, SHIN-ETSU CHEMICAL CO., LTD.
Application year: 1998
Main classification: C07F7
IPC codes: C07F7