Black iron-based composite particles, process for producing the same, paint and rubber or resin composition containing the same

Abstract: Black iron-based composite particles of the present invention comprise: (i) black iron oxide particles or black iron oxide hydroxide particles having an average particle size of 0.08 to 1.0 µm; (ii) a coating layer formed on the surface of said particles (i) said coating layer comprising an organosilicon compound which is: (1) an organosilane compound obtainable by drying or heat-treating an alkoxysilane compound, (2) a polysiloxane or modified polysiloxane, or (3) a fluoroalkyl organosilane compound obtainable by drying or heat-treating a fluoroalkylsilane compound; and (iii) carbon black fine particles having an average particle size of 0.005 to 0.05 µm, adhered on at least a part of said coating layer. Such composite particles have excellent dispersibility in a vehicle, or a rubber or resin composition on the basis of a small amount of the carbon black fine particles which are desorbed from the surface of the composite particles. They also have a high blackness substantially identical to a blackness of carbon black fine particles used alone, even when carbon black is contained therein only in a small amount.

Description: The present invention relates to black iron-based composite particles, a process for producing the black iron-based composite particles, and a paint and a rubber or resin composition containing the black iron-based composite particles. More particularly, the present invention relates to black iron-based composite particles not only having an excellent dispersibility in a vehicle, or a rubber or resin composition on the basis of a small amount of the carbon black fine particles which are desorbed from the surface of the black iron-based composite particles and a high blackness substantially identical to a blackness of carbon black fine particles used solely, even when carbon black is contained therein only in a small amount, but also capable of providing a paint for providing a coating film having an excellent acid resistance or a resin composition having an excellent aging resistance; a process for producing the black iron-based composite particles; a paint containing the black iron-based composite particles, which is excellent in acid resistance; and a rubber or resin composition containing the black iron-based composite particles, which is excellent in aging resistance. Carbon black fine particles or magnetite particles are well known in the art as typical black pigments, and have been hitherto widely used as colorants for paints, printing ink, cosmetics, rubber or resin compositions or the like. Among these black pigments, the carbon black fine particles are most excellent in blackness, and a coating film and rubber or resin composition prepared by using the carbon black fine particles also have an excellent acid resistance or aging resistance. However, since the carbon black fine particles have an average particle size as fine as about 0.005 to 0.05 µm, it has been difficult to disperse the particles in a vehicle, or a rubber or resin composition. Further, since the carbon black fine particles have a bulk density as high as about 0.1 g/cm 3 , it has been difficult to handle the particles, resulting in deteriorated workability. Furthermore, it is also known that the carbon black fine particles have problems concerning safety and hygiene, such as carcinogenosis. That is, as the amount of the carbon black fine particles used is increased, the blackness tends to become higher. However, when a larger amount of the carbon black fine particles is used, it is more and more difficult to disperse the particles in a vehicle, or a rubber or resin composition, resulting in not only deteriorated workability but also unfavorably causing problems concerning safety and hygiene. On the other hand, the magnetite particles have a more appropriate particle size than that of the carbon black fine particles, especially an average particle size of about 0.08 to 1.0 µm and are, therefore, excellent in dispersibility in a vehicle, or a rubber or resin composition, resulting in a high handling property. Further, the magnetite particles can show a further advantage such as non-toxicity. However, the magnetite particles are still unsatisfactory in blackness, and the coating film and the rubber or resin composition prepared by using the magnetite particles are also unsatisfactory in acid resistance and aging resistance. Further, the magnetite particles tend to be magnetically aggregated because of magnetic attracting property thereof. In consequence, in order to improve the dispersibility in a vehicle, or a rubber or resin composition, it is known to use, as non-magnetic black iron-based particles, manganese-containing hematite particles or manganese-containing iron oxide hydroxide particles. However, the blackness of these particles is inferior to that of the magnetite particles. In recent years, it has been required to improve various properties of black particles as colorants. There has been a strong demand for such black particles capable of showing useful properties of the carbon black fine particles as well as those of black iron oxide particles such as magnetite particles and black manganese-containing hematite particles or black iron oxide hydroxide particles such as black manganese-containing goethite particles. Especially, it has been strongly demand to provide such black particles capable of showing a high blackness substantially identical to a blackness of the carbon black fineparticles used solely, even when the carbon black fine particles which are deteriorated in workability such as handing property and have problems concerning safety and hygiene, are contained therein only in a small amount; capable of providing a paint for providing a coating film having an excellent acid resistance or a resin composition having an excellent aging resistance; and further capable of exhibiting an excellent dispersibility in a vehicle, or a rubber or resin composition. To satisfy these demands, it has been attempted to produce black composite particles composed of the carbon black fine particles and the magnetite particles, and having useful properties of both the particles. For example, there are known 1) a method comprising steps of adding a water dispersion containing carbon black fine particles to a water suspension containing magnetite particles precipitated from an aqueous solution and then mixing and stirring the resultant mixture, thereby causing the carbon black fine particles to be absorbed onto surfaces of the magnetite particles (Japanese Patent Publication (KOKOKU) No. 50-13300(1975)); 2) a method comprising a step of introducing an iron-containing waste sludge in which high-molecular weight organic materials such as molasses are dissolved, and a carbon black-containing hot gas into a spray reactor at a temperature of 450 to 850°C, thereby producing magnetite particles from iron salts and simultaneously bonding the carbon black onto surfaces of the obtained magnetite particles using the molasses as a binding accelerator (Japanese Patent Application Laid-open (KOKAI) No. 49-48725(1974)); 3) a method comprising steps of suspending carbon black in an iron salt-containing aqueous solution and then adding alkali to the resultant suspension to coprecipitate carbon black and magnetite particles, thereby obtaining a co-precipitated product whose surfaces are coated with carbon black (Japanese Patent Publication (KOKOKU) No. 55-39580(1980)); 4) a method comprising steps of adhering carbon black or the like on surfaces of fine plate-like particles and fixing the carbon black or the like thereon using an anionic or cationic surfactant, a nonionic surfactant and an organic functional silane compound (Japanese Patent Application Laid-open (KOKAI) Nos. 6-145556(1994) and 7-316458(1995)); or the like. At present, it have been most demanded to provide black particles having useful properties of the carbon black fine particles as well as those of the black iron oxide particles or black iron oxide hydroxide particles. However, all of the above mentioned known methods have failed to provide black particles satisfying these useful properties. Specifically, in the case of the above-mentioned method 1), the desorption percentage of the carbon black fine particles still remains high as described in Comparative Examples hereinafter. As a result, when the carbon black-adsorbed magnetite particles are dispersed in vehicle or resin compositions, the carbon black fine particles are desorbed therefrom, i.e., it becomes difficult to uniformly disperse the black particles in vehicles and resin compositions, thereby failing to sufficiently improve the blackness of a paint and rubber or resin composition prepared therefrom. In the case of the above-mentioned method 2), in order to obtain black particles having a high blackness substantially identical to a blackness of carbon black fine particles used solely, it is required to use the carbon black fine particles in an amount as large as about 280 parts by weight based on 100 parts by weight of the magnetite particles. In the case of the above-mentioned method 3), in order to obtain black particles having a high blackness substantially identical to a blackness of carbon black fine particles used solely, it is also required to use the carbon black fine particles in an amount as large as about 100 to 400 parts by weight based on 100 parts by weight of the magnetite particles. In addition, the carbon black fine particles tend to be desorbed from the surfaces of the co-precipitated product. Further, in the case of the above-mentioned method 4), the particles obtained by this method are not only deteriorated in blackness, but also show a high percentage of desorption of the carbon black fine particles therefrom. Besides, such particles obtained by the method 4) are not black particles. As a result of the present inventors' earnest studies, it has been found that by forming a coating layer composed of at least one organosilicon compound selected from the group consisting of (1) organosilane compounds obtained by drying or heat-treating alkoxysilane compounds, (2) polysiloxanes or modified polysiloxanes and (3) fluoroalkyl organosilane compounds obtained by drying or heat-treating fluoroalkylsilane compounds, on surface of specific black iron oxide particle or black iron oxide hydroxide particle, and adhering carbon black fine particles on the coating layer such that the amount of the carbon black fine particles adhered is 1 to 30 parts by weight based on 100 parts by weight of the black iron oxide particles or black iron oxide hydroxide particles, the obtained black iron-based composite particles can have an excellent dispersibility in a vehicle, or a rubber or resin composition on the basis of a small amount of the carbon black fine particles which are desorbed from the surface of the black iron-based composite particles and a high blackness substantially identical to a blackness of carbon black fine particles used solely, even when the carbon black is contained therein only in a small amount, and can provide a coating film having an excellent acid resistance and a rubber or resin composition having an excellent aging resistance. The present invention has been attained on the basis of the above finding. An object of the present invention is to provide black iron-based composite particles not only having a high blackness substantially identical to a blackness of carbon black fine particles used solely, even when carbon black is contained therein only in a small amount, but also capable of providing a paint for providing a coating film having an excellent acid resistance and a rubber or resin composition having an excellent aging resistance. Another object of the present invention is to provide black iron-based composite particles showing a low percentage of desorption of carbon black therefrom, and an excellent dispersibility in a vehicle, or a rubber or resin composition on the basis of a small amount of the carbon black fine particles which are desorbed from the surface of the black iron-based composite particles. A further object of the present invention is to provide a process for producing black iron-based composite particles not only having an excellent dispersibility in a vehicle, or a rubber or resin composition and showing a high blackness substantially identical to a blackness of carbon black fine particles used solely, even when carbon black is contained therein only in a small amount, but also capable of providing a paint for providing a coating film having an excellent acid resistance and a rubber of resin composition having an excellent aging resistance. A still further object of the present invention is to provide a paint showing less change in gloss and lightness according to an acid resistance test for coating films. A still further object of the present invention is to provide a rubber or resin composition which exhibits a small deterioration of the rubber or resin used therein. To accomplish the aims, in a first aspect of the present invention, there is provided black iron-based composite particles comprising: as a core particle black iron oxide particle or black iron oxide hydroxide particle having an average particle size of 0.08 to 1.0 µm; a coating layer formed on surface of the black iron oxide particle or black iron oxide hydroxide particle, comprising at least one organosilicon compound selected from the group consisting of (1) organosilane compounds obtained by drying or heat-treating alkoxysilane compounds, (2) polysiloxanes, or modified polysiloxanes and (3) fluoroalkyl organosilane compounds obtained by drying or heat-treating fluoroalkylsilane compounds; and carbon black fine particles having an average particle size of 0.005 to 0.05 µm, adhered (attached) onto the coating layer, the amount of the carbon black fine particles adhered being 1 to 30 parts by weight based on 100 parts by weight of the black iron oxide particles or black iron oxide hydroxide particles. In a second aspect of the present invention, there is provided black iron-based composite particles comprising: black iron oxide particles or black iron oxide hydroxide particles having an average particle size of 0.08 to 1.0 µm; an underlayer formed on surface of the black iron oxide particle or black iron oxide hydroxide particle, comprising at least one compound selected from the group consisting of hydroxides of aluminum, oxides of aluminum, hydroxides of silicon and oxides of silicon; a coating layer formed on the surface of the underlayer, comprising at least one organosilicon compound selected from the group consisting of (1) organosilane compounds obtained by drying or heat-treating alkoxysilane compounds, (2) polysiloxanes, or modified polysiloxanes and (3) fluoroalkyl organosilane compounds obtained by drying or heat-treating fluoroalkylsilane compounds; and carbon black fine particles having an average particle size of 0.005 to 0.05 µm, adhered (attached) onto the coating layer, the amount of the carbon black fine particles adhered being 1 to 30 parts by weight based on 100 parts by weight of the black iron oxide particles or black iron oxide hydroxide particles. In a third aspect of the present invention, there is provided a process for producing black iron-based composite particles defined in the first aspect, which process comprises: mixing and stirring said black iron oxide particles or black iron oxide hydroxide particles having an average particle size of 0.08 to 1.0 µm together with at least one compound selected from the group consisting of: (1) alkoxysilane compounds, (2) polysiloxanes or modified polysiloxanes, and (3) fluoroalkylsilane compounds by using an edge runner, thereby coating surfaces of said black iron oxide particles or black iron oxide hydroxide particles with said compounds; adding carbon black fine particles having an average particle size of 0.005 to 0.05 µm in an amount of 1 to 30 parts by weight based on 100 parts by weight of said black iron oxide particles or black iron oxide hydroxide particles, thereby obtaining mixed particles; mixing and stirring said mixed particles by using an edge runner, followed by drying or heat-treating, thereby adhering said carbon black fine particles on the surface of a coating layer comprising the organosilicon compounds. In a fourth aspect of the present invention, there is provided a paint comprising: said black iron-based composite particles defined in the first aspect or second aspect; and a paint base material. In a fifth aspect of the present invention, there is provided a rubber or resin composition comprising: said black iron-based composite particles defined in the first aspect or second aspect; and a base material for rubber or resin composition. In the accompanying drawings: Fig. 1 is an electron photograph (x 20,000) showing a particle structure of black manganese-containing hematite particles used in Example 1; Fig. 2 is an electron photograph (x 20,000) showing a particle structure of carbon black fine particles used in Example 1; Fig. 3 is an electron photograph (x 20,000) showing a particle structure of black iron-based composite particles obtained in Example 1; and Fig. 4 is an electron photograph (x 20,000) showing a particle structure of mixed particles of black manganese-containing hematite particles and carbon black fine particles for comparative purposes. The particle shape and particle size of the black iron-based composite particles according to the present invention are considerably varied depending upon those of black iron oxide particles or black iron oxide hydroxide particles as core particles. Specifically, the black iron-based composite particles according to the present invention are substantially similar in particle shape to that of the core particles, and have a slightly larger particle size than that of the core particles. The black iron-based composite particles according to the present invention may have such a particle size as defined below: (i) In the case where the core particles are granular particles, the lower limit of the average particle size of the black iron-based composite particles is usually 0.082 µm, preferably 0.1 µm, and the upper limit thereof is usually 1.05 µm, preferably 0.7 µm, more preferably 0.5 µm. (ii) In the case where the core particles are acicular or spindle-shaped particles, the lower limit of the average particle size (average major axis diameter) of the black iron-based composite particles is usually 0.082 µm, preferably 0.1 µm and the upper limit thereof is usually 1.05 µm, preferably 0.7 µm, more preferably 0.5 µm; and the lower limit of the aspect ratio (average major axis diameter/average minor axis diameter) of the black iron-based composite particles is usually 2, preferably 3, and the upper limit thereof is usually 20, preferably 15, more preferably 10. (iii) In the case where the core particles are plate-like particles, the lower limit of the average particle size (average plate surface diameter) of the black iron-based composite particles is usually 0.082 µm, preferably 0.1 µm, and the upper limit thereof is usually 1.05 µm, preferably 0.7 µm, more preferably 0.5 µm; and the lower limit of the plate ratio (average plate surface diameter/average thickness) of the black iron-based composite particles is usually 2, preferably 3, and the upper limit thereof is usually 50, preferably 20, more preferably 10. When the average particle size of the black iron-based composite particles is less than 0.082 µm, the intermolecular force between the particles may be increased due to the fineness thereof, so that it may become difficult to uniformly disperse the particles in a vehicle, or a rubber or resin composition. On the other hand, when the average particle size is more than 1.05 µm, it may become difficult to uniformly disperse the particles in a vehicle, or a rubber or resin composition due to the largeness thereof. The upper limit of the blackness of the black iron-based composite particles according to the present invention is preferably 18 when represented by a L* value thereof. When the L* value as the upper limit of the blackness is more than 18, the lightness of the black iron-based composite particles is increased and, therefore, the blackness thereof may become insufficient. The upper limit of the blackness is more preferably 17.8 when represented by a L* value. The lower limit of the blackness is preferably about 15 when represented by a L* value. The percentage of desorption of carbon black fine particles from the black iron-based composite particles according to the present invention is usually not more than 20 %, preferably not more than 10 %. When the desorption percentage of carbon black fine particles is more than 20 %, the desorbed carbon black fine particles tend to inhibit the composite particles from being uniformly dispersed in a vehicle, or a rubber or resin composition upon the production of a paint or a rubber or resin composition. The black iron-based composite particles according to the present invention have a BET specific surface area of usually 1.0 to 200 m 2 /g, preferably 2.0 to 150 m 2 /g, more preferably 2.5 to 100 m 2 /g. When the BET specific surface area of the black iron-based composite particles according to the present invention is less than 1.0 m 2 /g, coarse particles may be produced or sintered particles may be formed therein or therebetween, resulting in adversely affecting the dispersibility of the particles in a vehicle, or a rubber or resin composition. On the other hand, when the BET specific surface area is more than 200 m 2 /g, the intermolecular force between the particles is increased due to the fineness thereof, so that it may become difficult to disperse the particles in a vehicle, or a rubber or resin composition. Further, it is preferred that the black iron-based composite particles according to the present invention have a geometrical standard deviation of particle sizes of not more than 1.80. When the geometrical standard deviation of particle sizes is more than 1.80, coarse particles tend to be present in the composite particles, so that it may become difficult to uniformly disperse the particles in a vehicle or a rubber or resin composition. In view of uniform dispersion of the black iron-based composite particles in a vehicle, or a rubber or resin composition, the geometrical standard deviation of particle sizes of the black iron-based composite particles according to the present invention is preferably not more than 1.70. Further, in view of industrial production of the black iron-based composite particles, the lower limit of the geometrical standard deviation of particle sizes is preferably 1.01. As the black iron oxide particles used as the core particles of the black iron-based composite particles according to the present invention, there may be exemplified magnetite particles or manganese-containing hematite particles which contain manganese in an amount of 5 to 40 % by weight based on the weight of the manganese-containing hematite particles. As the black iron oxide hydroxide particles used as the core particles of the black iron-based composite particles according to the present invention, there may be exemplified manganese-containing goethite particles which contain manganese in an amount of 5 to 40 % by weight based on the weight of the manganese-containing goethite particles. Meanwhile, the particle shape of the black iron oxide particles or the black iron oxide hydroxide particles as the core particles is not particularly restricted. For example, there may be used such black iron oxide particles or black iron oxide hydroxide particles having a spherical shape, an octahedral shape, a hexahedral shape, a polyhedral shape, a granular shape, an acicular shape, a spindle-like shape, a plate-like shape or the like. The black iron oxide particles or the black iron oxide hydroxide particles as the core particles may have such a particle size as defined below. (i) In the case where the core particles have a spherical shape, an octahedral shape, a hexahedral shape, a polyhedral shape or a granular shape, the lower limit of the average particle size of the core particles is usually 0.08 µm, preferably 0.098 µm, and the upper limit thereof is usually 1.0 µm, preferably 0.68 µm, more preferably 0.48 µm. (ii) In the case where the core particles are acicular particles or spindle-shaped particles, the lower limit of the average particle size (average major axis diameter) of the core particles is usually 0.08 µm, preferably 0.098 µm, and the upper limit thereof is usually 1.0 µm, preferably 0.68 µm, more preferably 0.48 mm; and the lower limit of the aspect ratio (average major axis diameter/average minor axis diameter) of the core particles is usually 2, preferably 3, and the upper limit thereof is usually 20, preferably 15, more preferably 10. (iii) In the case where the core particles are plate-like particles, the lower limit of the average particle size (average plate surface diameter) of the core particles is usually 0.08 µm, preferably 0.098 µm, and the upper limit thereof is usually 1.0 µm, preferably 0.68 µm, more preferably 0.48 µm; and the lower limit of the plate ratio (average plate surface diameter/average thickness) of the core particles is usually 2, preferably 3, and the upper limit thereof is usually 50, preferably 20, more preferably 10. With respect of the blackness of the black iron oxide particles as the core particles, in case of the magnetic particles, the lower limit of the blackness thereof, when represented by the L* value, is usually 18, and the upper limit thereof is usually 25, preferably 24. In the case of the black manganese-containing hematite particles, the lower limit of the blackness thereof as the core particles when represented by the L* value, is usually 18, and the upper limit thereof is usually 30, preferably 28, more preferably 25. With respect to the blackness of the black iron oxide hydroxide particles as the core particles, in the case of the manganese-containing goethite particles, the lower limit of the blackness thereof, when represented by the L* value, is usually 18, and the upper limit thereof is usually 30, preferably 28, more preferably 25. When the L* value is more than the above upper limit, the blackness of the core particles is insufficient, thereby failing to obtain the black iron-based composite particles having an excellent blackness according to the present invention. The black iron oxide particles or black iron oxide hydroxide particles as the core particles may have a BET specific surface area of usually 1.0 to 200 m 2 /g, preferably 2.0 to 150 m 2 /g, more preferably 2.5 to 100 m 2 /g. Further, it is preferred that the black iron oxide particles or the black iron oxide hydroxide particles used as the core particles in the present invention have a geometrical standard deviation of particle sizes of not more than 1.8, preferably not more than 1.7. The lower limit of the geometrical standard deviation of particle sizes of the core particles is preferably 1.01. The coating layer formed on the surfaces of the core particles comprises at least one organosilicon compound selected from the group consisting of (1) organosilane compounds obtained by drying or heat-treating alkoxysilane compounds; (2) polysiloxanes, or modified polysiloxanes selected from the group consisting of (A) polysiloxanes modified with at least one compound selected from the group consisting of polyethers, polyesters and epoxy compounds (hereinafter referred to merely as "modified polysiloxanes"), and (B) polysiloxanes whose molecular terminal is modified with at least one group selected from the group consisting of carboxylic acid groups, alcohol groups and a hydroxyl group; and (3) fluoroalkyl organosilane compounds obtained by drying or heat-treating fluoroalkylsilane compounds. The organosilane compounds (1) can be produced by drying or heat-treating alkoxysilane compounds represented by the formula (I): R 1 a SiX 4-a wherein R 1 is C 6 H 5 -, (CH 3 ) 2 CHCH 2 - or n-C m H 2m+1 - (wherein b is an integer of 1 to 18); X is CH 3 O- or C 2 H 5 O-; and a is an integer of 0 to 3. The drying or heat-treatment of the alkoxysilane compounds is conducted, for example, at a temperature of usually 40 to 200°C, preferably 60 to 150°C for usually 10 minutes to 12 hours, preferably 30 minutes to 3 hours. Specific examples of the alkoxysilane compounds may include methyl triethoxysilane, dimethyl diethoxysilane, tetraethoxysilane, phenyl triethyoxysilane, diphenyl diethoxysilane, methyl trimethoxysilane, dimethyl dimethoxysilane, tetramethoxysilane, phenyl trimethoxysilane, diphenyl dimethoxysilane, isobutyl trimethoxysilane, decyl trimethoxysilane or the like. Among these alkoxysilane compounds, in view of the desorption percentage and the adhering effect of carbon black fine particles, methyl triethoxysilane, phenyl triethyoxysilane, methyl trimethoxysilane, dimethyl dimethoxysilane and isobutyl trimethoxysilane are preferred, and methyl triethoxysilane and methyl trimethoxysilane are more preferred. As the polysiloxanes (2), there may be used those compounds represented by the formula (II): wherein R 2 is H- or CH 3 -, and d is an integer of 15 to 450. Among these polysiloxanes, in view of the desorption percentage and the adhering effect of carbon black fine particles, polysiloxanes having methyl hydrogen siloxane units are preferred. As the modified polysiloxanes (A), there may be used: (a) polysiloxanes modified with polyethers represented by the formula (III): wherein R 3 is -(-CH 2 -) h -; R 4 is -(-CH 2 -) i -CH 3 ; R 5 is -OH, -COOH, -CH=CH 2 , -CH(CH 3 )=CH 2 or -(-CH 2 -) j -CH 3 ; R 6 is -(-CH 2 -) k -CH 3 ; g and h are an integer of 1 to 15; i, j and k are an integer of 0 to 15; e is an integer of 1 to 50; and f is an integer of 1 to 300; (b) polysiloxanes modified with polyesters represented by the formula (IV) : wherein R 7 , R 8 and R 9 are -(-CH 2 -) q - and may be the same or different; R 10 is -OH, -COOH, -CH=CH 2 , -CH(CH 3 )=CH 2 or -(-CH 2 -) r -CH 3 ; R 11 is -(-CH 2 -) s -CH 3 ; n and q are an integer of 1 to 15; r and s are an integer of 0 to 15; e' is an integer of 1 to 50; and f' is an integer of 1 to 300; (c) polysiloxanes modified with epoxy compounds represented by the formula (V) : wherein R 12 is -(-CH 2 -) v -; v is an integer of 1 to 15; t is an integer of 1 to 50; and u is an integer of 1 to 300; or a mixture thereof. Among these modified polysiloxanes (A), in view of the desorption percentage and the adhering effect of carbon black fine particles, the polysiloxanes modified with the polyethers represented by the formula (III), are preferred. As the terminal-modified polysiloxanes (B), there may be used those represented by the formula (VI) : wherein R 13 and R 14 are -OH, R 16 OH or R 17 COOH and may be the same or different; R 15 is -CH 3 or -C 6 H 5 ; R 16 and R 17 are -(-CH 2 -) y -; y is an integer of 1 to 15; w is an integer of 1 to 200; and x is an integer of 0 to 100. Among these terminal-modified polysiloxanes, in view of the desorption percentage and the adhering effect of carbon black fine particles, the polysiloxanes whose terminals are modified with carboxylic acid groups are preferred. The fluoroalkyl organosilane compounds (3) may be produced by drying or heat-treating fluoroalkylsilane compounds represented by the formula (VII) : CF 3 (CF 2 ) z CH 2 CH 2 (R 18 ) a' SiX 4-a' wherein R 18 is CH 3 -, C 2 H 5 -, CH 3 O- or C 2 H 5 O-; X is CH 3 O- or C 2 H 5 O-; and z is an integer of 0 to 15; and a' is an integer of 0 to 3. The drying or the heat-treatment of the fluoroalkylsilane compounds may be conducted, for example, at a temperature of usually 40 to 200°C, preferably 60 to 150°C for usually 10 minutes to 12 hours, preferably 30 minutes to 3 hours. Specific examples of the fluoroalkylsilane compounds may include trifluoropropyl trimethoxysilane, tridecafluorooctyl trimethoxysilane, heptadecafluorodecyl trimethoxysilane, heptadecafluorodecylmethyl dimethoxysilane, trifluoropropyl triethoxysilane, tridecafluorooctyl triethoxysilane, heptadecafluorodecyl triethoxysilane, heptadecafluorodecylmethyl diethoxysilane or the like. Among these fluoroalkylsilane compounds, in view of the desorption percentage and the adhering effect of carbon black fine particles, trifluoropropyl trimethoxysilane, tridecafluorooctyl trimethoxysilane and heptadecafluorodecyl trimethoxysilane are preferred, and trifluoropropyl trimethoxysilane and tridecafluorooctyl trimethoxysilane are more preferred. The coating amount of the organosilicon compounds is usually 0.02 to 5.0 % by weight, preferably 0.03 to 2.0 % by weight, more preferably 0.05 to 1.5 % by weight (calculated as Si) based on the weight of the black iron oxide particles or the black iron oxide hydroxide particles coated with the organosilicon compounds. When the coating amount of the organosilicon compounds is less than 0.02 % by weight, it may become difficult to adhere carbon black fine particles on the coating layer in such an amount enough to improve the blackness thereof. On the other hand, even when the coating amount of the organosilicon compounds is more than 5.0 % by weight, a sufficient amount of carbon black fine particles can be adhered on the coating layer. However, it is meaningless because the blackness cannot be further improved by using such an excess amount of the organosilicon compounds. As the carbon black fine particles used in the black iron-based composite particles according to the present invention, there may be exemplified commercially available carbon blacks such as furnace black or channel black. Specific examples of the commercially available carbon blacks usable in the present invention, may include MA-100, MA7, #1000, #2400B, #30, MA8, MA11, #50, #52, #45, #2200B, MA600, etc. (tradename, produced by MITSUBISHI CHEMICAL CORP.), SEAST 9H, SEAST 7H, SEAST 6, SEAST 3H, SEAST 300, SEAST FM, etc. (tradename, produced by TOKAI CARBON CO., LTD.) or the like. In view of the compatibility with the organosilicon compounds, MA-100, MA7, #1000, #2400B and #30 are preferred. The average particle size of the carbon black fine particles is usually 0.005 to 0.05 µm, preferably 0.010 to 0.035 µm. When the average particle size of the carbon black fine particles is less than 0.005 µm, the carbon black fine particles are too fine to be well handled. On the other hand, when the average particle size is more than 0.05 µm, the particle size of the carbon black fine particles may become much larger than that of the black iron oxide particles or the black iron oxide hydroxide particles as the core particles, thereby causing insufficient adhesion of the carbon black fine particles onto the coating layer composed of the organosilicon compounds and increasing the desorption percentage of the carbon black fine particles. As a result, the dispersibility of the obtained composite particles in a vehicle, or a rubber or resin composition is deteriorated. The ratio value of an average particle size of the black iron oxide particles or the black iron oxide hydroxide particles to an average particle size of the carbon black fine particles is preferably not less than 2. When the ratio value is less than 2, the particle size of the carbon black fine particles may become considerably large as compared to that of the black iron oxide particles or the black iron oxide hydroxide particles as the core particles, thereby causing insufficient adhesion of the carbon black fine particles onto the coating layer composed of the organosilicon compounds and increasing the desorption percentage of the carbon black fine particles. As a result, the dispersibility of the obtained composite particles in a vehicle, or a rubber or resin composition is deteriorated. The upper limit of the ratio value thereof is preferably 200. The amount of the carbon black fine particles adhered is 1 to 30 parts by weight based on 100 parts by weight of the black iron oxide particles or the black iron oxide hydroxide particles as the core particles. When the amount of the carbon black fine particles adhered is less than 1 part by weight, the blackness of the resultant composite particles is unsatisfactory because of insufficient amount of the carbon black fine particles adhered onto the coating layer. On the other hand, when the amount of the carbon black fine particles adhered is more than 30 parts by weight, the carbon black fine particles tend to be desorbed from the coating layer because of too much amount of the carbon black fine particles adhered thereonto, though the obtained composite particles can show a sufficient blackness. As a result, the dispersibility of the obtained composite particles in a vehicle, or a rubber or resin composition is deteriorated. In the black iron-based composite particles according to the present invention, the surfaces of the black iron oxide particles or the black iron oxide hydroxide particles as the core particles may be preliminarily coated with at least one compound selected from the group consisting of hydroxide of aluminum, oxides of aluminum, hydroxides of silicon and oxides of silicon (hereinafter referred to as "underlayer composed of hydroxides or oxides of aluminum or silicon"), if required. In this case, the dispersibility of the obtained composite particles in a vehicle, or a rubber or resin composition may become improved as compared to those having no underlayer composed of hydroxides or oxides of aluminum or silicon. The coating amount of the hydroxides or oxides of aluminum or silicon is 0.01 to 50 % by weight calculated as Al, SiO 2 or a sum of Al and SiO 2 , based on the weight of the black iron oxide particles or the black iron oxide hydroxide particles as the core particles. When the coating amount of the hydroxides or oxides of aluminum or silicon is less than 0.01 % by weight, the dispersibility of the obtained composite particles in a vehicle, or a rubber or resin composition cannot be improved. On the other hand, when the coating amount of the hydroxides or oxides of aluminum or silicon is more than 50 % by weight, the obtained composite particles can exhibit a good dispersibility in a vehicle, or a rubber or resin composition, but it is meaningless because the dispersibility cannot be further improved by using such an excess coating amount of the hydroxides or oxides of aluminum or silicon. The black iron-based composite particles having the underlayer composed of the hydroxides or oxides of aluminum or silicon may be substantially identical in a particle size, a geometrical standard deviation of particle sizes, a BET specific surface area and a blackness (L* value), to those having no underlayer composed of the hydroxides or oxides of aluminum or silicon. Next, the process for producing the black iron-based composite particles according to the present invention, is described. The granular magnetite particles as the core particles according to the present invention may be produced by a so-called wet process, i.e., by passing an oxygen-containing gas such as air through a suspension containing a ferrous hydroxide colloid obtained by reacting a ferrous salt aqueous solution with alkali hydroxide. The acicular magnetite particles or the spindle-shaped magnetite particles may be produced by first forming acicular goethite particles or spindle-shaped goethite particles by a so-called wet process, i.e., by passing an oxygen-containing gas such as air through a suspension containing either ferrous hydroxide colloid, iron carbonate or iron-containing precipitates obtained by reacting a ferrous salt aqueous solution with alkali hydroxide, alkali carbonate or both of alkali hydroxide and alkali carbonate, and then after filtering-out and washing with water, heat-treating the resultant goethite particles at a temperature of 300 to 500°C in a reducing atmosphere. The granular manganese-containing hematite particles as the core particles according to the present invention, may be produced by first forming coated magnetite particles by coating the granular magnetite particles obtained by the above-mentioned wet process, with a manganese compound such that the coating amount of manganese is 8 to 150 atomic % based on whole Fe, or forming magnetite particles containing manganese in an amount of 8 to 150 atomic % based on whole Fe by conducting the above-mentioned wet process for producing the granular magnetite particles in the presence of manganese, and then after filtering-out, washing with water and drying, heat-treating the resultant manganese-coated magnetite particles or the manganese-containing magnetite particles at a temperature of 750 to 1,000°C in an oxygen-containing gas such as air. The manganese-containing hematite particles are non-magnetic material and, therefore, free from magnetic aggregation, thereby exhibiting a good dispersibility. The acicular or spindle-shaped manganese-containing hematite particles may be produced by heat-treating acicular or spindle-shaped goethite particles containing manganese in an amount of 8 to 150 atomic % based on whole Fe which are obtained by the below-mentioned method, at a temperature of 400 to 800°C in an oxygen-containing gas such as air. The acicular or spindle-shaped manganese-containing goethite particles according to the present invention, may be produced by conducting the above-mentioned wet process for producing the acicular or spindle-shaped goethite particles, in the presence of manganese, thereby forming acicular or spindle-shaped goethite particles containing manganese in an amount of 8 to 150 atomic % based on whole Fe. The coating of the black iron oxide particles or the black iron oxide hydroxide particles with the alkoxysilane compounds, the polysiloxanes, the modified polysiloxanes, the terminal-modified polysiloxanes or the fluoroalkylsilane compounds, may be conducted by mechanically mixing and stirring the black iron oxide particles or the black iron oxide hydroxide particles together with the alkoxysilane compounds, the polysiloxanes, the modified polysiloxanes, the terminal-modified polysiloxanes or the fluoroalkylsilane compounds; or by mechanically mixing and stirring both the components together while spraying the alkoxysilane compounds, the polysiloxanes, the modified polysiloxanes, the terminal-modified polysiloxanes or the fluoroalkylsilane compounds onto the black iron oxide particles or the black iron oxide hydroxide particles. In these cases, substantially whole amount of the alkoxysilane compounds, the polysiloxanes, the modified polysiloxanes, the terminal-modified polysiloxanes or the fluoroalkylsilane compounds added can be applied onto the surfaces of the black iron oxide particles or the black iron oxide hydroxide particles. In order to uniformly coat the surfaces of the black iron oxide particles or the black iron oxide hydroxide particles with the alkoxysilane compounds, the polysiloxanes, the modified polysiloxanes, the terminal-modified polysiloxanes or the fluoroalkylsilane compounds, it is preferred that the black iron oxide particles or the black iron oxide hydroxide particles are preliminarily diaggregated by using a pulverizer. As the apparatuses for the mixing and stirring, there may be used an edge runner, a Henschel mixer or the like. The conditions for the mixing and stirring such as mixing ratio, linear load or mixing and stirring time , may be appropriately adjusted so as to coat the surfaces of the black iron oxide particles or the black iron oxide hydroxide particles with the alkoxysilane compounds, the polysiloxanes, the modified polysiloxanes, the terminal-modified polysiloxanes or the fluoroalkylsilane compounds as uniformly as possible. The mixing and stirring time for the coating treatment is, for example, preferably not less than 20 minutes. The amount of the alkoxysilane compounds, the polysiloxanes, the modified polysiloxanes, the terminal-modified polysiloxanes or the fluoroalkylsilane compounds added, is preferably 0.15 to 45 parts by weight based on 100 parts by weight of the black iron oxide particles or the black iron oxide hydroxide particles. When the amount of the organosilicon compounds added is less than 0.15 part by weight, it may become difficult to adhere the carbon black fine particles in such an amount enough to improve the blackness of the obtained composite particles. On the other hand, when the amount of the organosilicon compounds added is more than 45 parts by weight, a sufficient amount of the carbon black fine particles can be adhered on the surface of the coating layer, but it is meaningless because the blackness of the composite particles cannot be further improved by using such an excess amount of the organosilicon compounds. Next, the carbon black fine particles are added to the black iron oxide particles or the black iron oxide hydroxide particles coated with the organosilicon compounds, and the resultant mixture is continuously mixed and stirred to adhere the carbon black fine particles on the surfaces of the coating layer composed of the organosilicon compounds, and then dried. In the case where the alkoxysilane compounds (1) and the fluoroalkylsilane compounds (3) are used as the coating compound, after the carbon black fine particles are adhered on the surface of the coating layer, the resultant composite particles are dried or heat-treated, for example, at a temperature of usually 40 to 200°C, preferably 60 to 150°C for usually 10 minutes to 12 hours, preferably 30 minutes to 3 hours, thereby forming a coating layer composed of the organosilicon compounds (1) and the fluoroalkyl organosilicon compounds (3), respectively. It is preferred that the carbon black fine particles are added little by little and slowly, especially about 5 to 60 minutes. The conditions for mixing and stirring the black iron oxide particles or the black iron oxide hydroxide particles and the carbon black fine particles, such as mixing ratio, linear load or mixing and stirring time, may be appropriately adjusted so as to uniformly adhere the carbon black fine particles on the surface of the coating layer. The mixing and stirring time for the adhesion treatment is, for example, preferably not less than 20 minutes. The amount of the carbon black fine particles added, is preferably 1 to 30 parts by weight based on 100 parts by weight of the black iron oxide particles or the black iron oxide hydroxide particles. When the amount of the carbon black fine particles added is less than 1 part by weight, it may become difficult to adhere the carbon black fine particles in such an amount enough to improve the blackness of the obtained composite particles. On the other hand, when the amount of the carbon black fine particles added is more than 30 parts by weight, a sufficient blackness of the resultant composite particles can be obtained, but the carbon black fine particles tend to be desorbed from the surface of the coating layer because of too large amount of the carbon black fine particles adhered, resulting in deteriorated dispersibility in a vehicle, or a rubber or resin composition. The black iron oxide particles or the black iron oxide hydroxide particles may be coated with at least one compound selected from the group consisting of hydroxides of aluminum, oxides of aluminum, hydroxides of silicon and oxides of silicon, if required, prior to mixing and stirring with the alkoxysilane compounds, the polysiloxanes, the modified polysiloxanes, the terminal-modified polysiloxanes or the fluoroalkylsilane compounds. The coating of the hydroxides or oxides of aluminum or silicon may be conducted by adding an aluminum compound, a silicon compound or both the compounds to a water suspension in which the black iron oxide particles or the black iron oxide hydroxide particles are dispersed, followed by mixing and stirring, and further adjusting the pH of the suspension, if required, thereby coating the surfaces of the black iron oxide particles or the black iron oxide hydroxide particles with at least one compound selected from the group consisting of hydroxides of aluminum, oxides of aluminum, hydroxides of silicon and oxides of silicon. The thus obtained particles coated with the hydroxides or oxides of aluminum or silicon are then filtered out, washed with water, dried and pulverized. Further, the particles coated with the hydroxides or oxides of aluminum or silicon may be subjected to post-treatments such as deaeration treatment and compaction treatment. As the aluminum compounds, there may be exemplified aluminum salts such as aluminum acetate, aluminum sulfate, aluminum chloride or aluminum nitrate, alkali aluminates such as sodium aluminate, alumina sols or the like. The amount of the aluminum compound added is 0.01 to 50.00 % by weight (calculated as Al) based on the weight of the black iron oxide particles or the black iron oxide hydroxide particles. When the amount of the aluminum compound added is less than 0.01 % by weight, it may be difficult to sufficiently coat the surfaces of the black iron oxide particles or the black iron oxide hydroxide particles with hydroxides or oxides of aluminum or silicon, thereby failing to improve the dispersibility in a vehicle, or a rubber or resin composition. On the other hand, when the amount of the aluminum compound added is more than 50.00 % by weight, the coating effect is saturated and, therefore, it is meaningless to add such an excess amount of the aluminum compound. As the silicon compounds, there may be exemplified water glass #3, sodium orthosilicate, sodium metasilicate, colloidal silica or the like. The amount of the silicon compound added is 0.01 to 50.00 % by weight (calculated as SiO 2 ) based on the weight of the black iron oxide particles or the black iron oxide hydroxide particles. When the amount of the silicon compound added is less than 0.01 % by weight, it may be difficult to sufficiently coat the surfaces of the black iron oxide particles or the black iron oxide hydroxide particles with hydroxides or oxides of silicon, thereby failing to improve the dispersibility in a vehicle, or a rubber or resin composition. On the other hand, when the amount of the silicon compound added is more than 50.00 % by weight, the coating effect is saturated and, therefore, it is meaningless to add such an excess amount of the silicon compound. In the case where both the aluminum and silicon compounds are used in combination for the coating, the total amount of the aluminum and silicon compounds added is preferably 0.01 to 50.00 % by weight (calculated as a sum of Al and SiO 2 ) based on the weight of the black iron oxide particles or the black iron oxide hydroxide particles. Next, the paint containing the black iron-based composite particles according to the present invention is described. The solvent-based paint containing the black iron-based composite particles according to the present invention can exhibit a L* value of 15 to 19.5 when formed into a coating film and, therefore, the blackness of the paint is substantially identical to the blackness of the carbon black fine particles solely, even when carbon black is contained therein only in a small amount. In addition, the paint may exhibit a gloss of not less than 85 %, an acid resistance (ΔG value) of not more than 10.0 and a ΔL* value of not more than 1,0. In view of the blackness, the L* value is preferably 15 to 18.5, more preferably 15 to 18; the gloss is preferably not less than 87 %, more preferably 88 %; the acid resistance represented by a ΔG value is preferably not more than 9.5, more preferably not more than 9.3; and the ΔL* value is preferably not more than 0.9, more preferably not more than 0.8. The water-based paint containing the black iron-based composite particles according to the present invention can exhibit a L* value of 15 to 20 when formed into a coating film and, therefore, the blackness of the paint is substantially identical to the blackness of the carbon black fine particles solely, even when carbon black is contained therein only in a small amount. In addition, the paint can exhibit a gloss of not less than 80 %, an acid resistance (ΔG value) of not more than 10.0 and a ΔL* value of not more than 1.0. In view of the blackness, the L* value is preferably 15 to 19, more preferably 15 to 18; the gloss is preferably not less than 83 %, more preferably 85 %; the acid resistance represented by a ΔG value is preferably not more than 9.5, more preferably not more than 9.0; and the ΔL* value is preferably not more than 0.9, more preferably not more than 0.8. The blending percentage of the black iron-based composite particles in the paint according to the present invention is 1,0 to 100 parts by weight based on 100 parts by weight of a paint base material. In view of the handling property of the paint, the blending percentage of the black iron-based composite particles in the paint is preferably 2.0 to 100 parts by weight, more preferably 5.0 to 100 parts by weight. The paint may contain as paint base materials, resins, solvents and if required, a defoamer, an extender pigment, a dryer, a surfactant, a hardener, auxiliaries and the like. Examples of the resins for the solvent-based paint may include those ordinarily used therefor, such as acrylic resins, alkyd resins, polyester resins, polyurethane resins, epoxy resins, phenol resins, melamine resins, amino resins or the like. Examples of the resins for the water-based paint may also include those ordinarily used therefor, such as water-soluble alkyd resins, water-soluble melamine resins, water-soluble acrylic resins, water-soluble urethane emulsion resins or the like. Examples of the solvents for the solvent-based paint may include those ordinarily used therefor, such as toluene, xylene, butyl acetate, methyl acetate, methyl isobutyl ketone, butyl cellosolve, ethyl cellosolve, butyl alcohol, hydrocarbons or the like. As the solvents for the water-based paint, there may be exemplified those ordinarily used therefor, such as water containing butyl cellosolve, butyl alcohol or the like. As the defoamer, there may be used commercially available products such as NOPCO 8034 (tradename), SN DEFOAMER 477 (tradename), SN DEFOAMER 5013 (tradename), SN DEFOAMER 247 (tradename) or SN DEFOAMER 382 (tradename) (all produced by SUN NOPCO LTD.); ANTIFOAM 08 (tradename) or EMULGEN 903 (tradename) (both produced by KAO CO., LTD.); or the like. Next, the rubber or resin composition colored by the black iron-based composite particles according to the present invention is described. The rubber or resin composition colored by the black iron-based composite particles according to the present invention has a L* value of 15 to 21 and, therefore, can show a high blackness substantially identical to the blackness of the carbon black fine particles solely, even when carbon black is contained therein only in a small amount. In addition, the dispersibility measured by the visual observation is 4 or 5. With respect to the aging resistance, the percentage of discolored portions caused when the composition is heated at 190°C for 90 minutes is not more than 15 %. In view of the blackness, the L* value is preferably 15 to 20, more preferably 15 to 19.5. The aging resistance is preferably not more than 10 %, more preferably not more than 5 %. The blending percentage of the black iron-based composite particles in the rubber or resin composition according to the present invention is 0.5 to 200 parts by weight based on 100 parts by weight of base materials of the rubber or resin composition. In view of the handling property of the rubber or resin composition, the blending percentage of the black iron-based composite particles in the rubber or resin composition is 100 parts by weight. The rubber or resin composition may contain as base materials, rubber, or known thermoplastic resins and if required, additives such as a lubricant, a plasticizer, an antioxidant, an ultraviolet light absorber or various other stabilizers. The additives may be added in an amount of not more than 50 % by weight based on the total weight of the black iron-based composite particles and the rubber or the resin. When the amount of the additives added is more than 50 % by weight, the rubber or resin composition is deteriorated in moldability. The rubber or resin composition according to the present invention may be produced by preliminarily intimately mixing a raw rubber or resin material and the black iron-based composite particles together and applying a strong shear force to the mixture by a kneader or an extruder to diaggregate agglomerates of the black iron-based composite particles and uniformly disperse the individual black iron-based composite particles in the rubber or resin. The thus produced rubber or resin composition may be formed into an appropriate shape according to the application thereof upon use. The important feature of the black iron-based composite particles according to the present invention exists at the following point. That is, the black iron oxide particles or the black iron oxide hydroxide particles whose surfaces may be coated, if required, with at least one compound selected from the group consisting of hydroxide of aluminum, oxides of aluminum, hydroxides of silicon and oxides of silicon, are coated with the organosilicon compounds, and further carbon black fine particles having an average particle size of 0.005 to 0.05 µm are adhered on surfaces of a coating layer composed of the organosilicon compounds. The amount of the carbon black fine particles adhered is 1 to 30 parts by weight based on 100 parts by weight of the black iron oxide particles or the black iron oxide hydroxide particles. The thus obtained black iron-based composite particles are not only excellent in dispersibility in a vehicle, or a rubber or resin composition on the basis of a small amount of the carbon black fine particles which are desorbed from the surface of the black iron-based composite particles, but also can show a blackness substantially identical to or not lower than the blackness obtained by using carbon black fine particles solely, even when carbon black is contained therein only in a small amount. The reason why the black iron-based composite particles according to the present invention can show an excellent blackness, is considered as follows. That is, the carbon black fine particles which tend to be ordinarily aggregated due to the fineness thereof, can be uniformly and densely adhered on surfaces of the black iron oxide particles or the black iron oxide hydroxide particles through the organosilicon compounds applied on the core particles. For this reason, the dispersing condition of the carbon black fine particles is close to that of primary particles, thereby allowing the individual carbon black fine particles to effectively exhibit their blackness. The reason why the amount of the carbon black fine particles desorbed from the surfaces of the black iron-based composite particles is small, is considered such that the organosilicon compounds onto which the carbon black fine particles are adhered, are strongly bonded to the surface of the black iron oxide particle or the black iron oxide hydroxide particle as a core particle. Especially, in the case of using the alkoxysilane compounds or the fluoroalkylsilane compounds, metallosiloxane bonds (≡Si-O-M, wherein M represents a metal atom contained in the black iron-based core particle, such as Si, Al or Fe) are formed between the metal elements such as Si, Al or Fe which are contained within the black iron oxide particle or the black iron oxide hydroxide particle or present at the surface thereof, and alkoxy groups of the alkoxysilane compounds or the fluoroalkylsilane compounds on which the carbon black fine particles are adhered, so that the organosilicon compounds onto which the carbon black fine particles are adhered, can be more strongly bonded to the surface of the black iron oxide particle or the black iron oxide hydroxide particle. The reason why the black iron-based composite particles according to the present invention can show an excellent dispersibility in vehicles, or a rubber or resin composition, is considered as follows. That is, due to the face that the amount of the carbon black fine particles desorbed from the surface of the black iron-based composite particle is small, it is unlikely that the dispersion in the system is inhibited by the carbon black fine particles desorbed. Further, since the carbon black fine particles are adhered on the surface of the black iron-based composite particle, irregularities are formed thereon, whereby the contact between the particles can be effectively prevented. In addition, it is noted that a coating film having an excellent acid resistance and a rubber or resin composition having an excellent aging resistance can be obtained by using the black iron-based composite particles according to the present invention. The reason why such a coating film having an excellent acid resistance, or such a rubber or resin composition having an excellent aging resistance can be obtained by using the black iron-based composite particles according to the present invention, is considered as follows. That is, since the carbon black fine particles which are inherently excellent in acid resistance and aging resistance, are adhered on the surfaces of the black iron oxide particles or the black iron oxide hydroxide particles through the organosilicon compounds, the inherent properties of the black iron oxide particles or the black iron oxide hydroxide particles such as a high oxidizability and a high surface activity can be eliminated. Thus, the inherent properties of the carbon black fine particles are effectively exhibited, so that the acid resistance of the coating film and the aging resistance of the rubber or resin composition can be enhanced. The black iron-based composite particles according to the present invention can show an excellent dispersibility in a vehicle, or a rubber or resin composition on the basis of a small amount of the carbon black fine particles which are desorbed from the surface of the black iron-based composite particles and a high blackness substantially identical to the blackness of carbon black fine particles solely, even when carbon black is contained therein only in a small amount, and can provide a paint having an excellent acid resistance and a rubber or resin composition having an excellent aging resistance. As a result, the black iron-based composite particles can be advantageously used as black pigments for paints, printing ink, cosmetics, rubber or resin compositions, or the like. The paint according to the present invention can exhibit a high blackness substantially identical to the blackness of carbon black fine particles solely, even when carbon black is contained therein only in a small amount, and can form a coating film having an excellent acid resistance. Therefore, the paint according to the present invention can be suitably used as a black paint. The rubber or resin composition according to the present invention can also exhibit a high blackness substantially identical to the blackness of carbon black fine particles solely, even when carbon black is contained therein only in a small amount, and have an aging resistance. Therefore, the rubber or resin composition according to the present invention can be suitably used as a black rubber or resin composition. Further, the black iron-based composite particles according to the present invention are excellent in dispersibility in a vehicle, and a rubber or resin composition and, therefore, can show excellent handling property or workability, thereby rendering these particles industrially and economically favorable. Furthermore, since the amount of the carbon black fine particles used is small, the black iron-based composite particles according to the present invention are advantageous in view of safety and hygiene. EXAMPLES The present invention will now be described in more detail with reference to the following examples, but the present invention is not restricted to those examples and various modifications are possible within the scope of the invention. (1) The average particle sizes of black iron oxide particles, black iron oxide hydroxide particles, carbon black fine particles and black iron-based composite particles were respectively expressed by average values (measured in a predetermined direction) of about 350 particles which were sampled from a micrograph obtained by magnifying an original electron micrograph (x 20,000) by four times in each of the longitudinal and transverse directions. (2) The aspect ratio of the particles was expressed by a ratio of average major axis diameter to minor axis diameter thereof. (3) The geometrical standard deviation of particle sizes was expressed by values obtained by the following method. That is, the particle sizes were measured from the above magnified photograph. The actual particle sizes and the number of the particles were obtained from the calculation on the basis of the measured values. On a logarithmic normal probability paper, the particle sizes were plotted at regular intervals on the abscissa-axis and the accumulative number of particles belonging to each interval of the particle sizes were plotted by percentage on the ordinate-axis by a statistical technique. The particle sizes corresponding to the number of particles of 50 % and 84.13 %, respectively, were read from the graph, and the geometrical standard deviation was measured from the following formula: Geometrical standard deviation = {particle size corresponding to 84.13 % under integration sieve}/{particle size (geometrical average diameter) corresponding to 50 % under integration sieve} The smaller the geometrical standard deviation, the more excellent the particle size distribution of the particles. (4) The specific surface area was expressed by values measured by a BET method. (5) The amounts of Mn, Al and Si which were present within black iron oxide particles, black iron oxide hydroxide particles and black iron-based composite particles or on surfaces thereof, and the amount of Si contained in organosilicon compounds , were measured by a fluorescent X-ray spectroscopy device 3063 (manufactured by RIGAKU DENKI KOGYO CO., LTD.) according to JIS K0119 "General rule of fluorescent X-ray analysis". (6) The amount of carbon adhered (attached) on the black iron-based composite particles was measured by "Horiba Metal, Carbon and Sulfur Analyzer EMIA-2200 Model" (manufactured by HORIBA SEISAKUSHO CO., LTD.). (7) The blackness of black iron oxide particles, black iron oxide hydroxide particles and black iron-based composite particles, were measured by the following method. That is, 0.5 g of sample particles and 0.7 cc of castor oil were intimately kneaded together by a Hoover's muller to form a paste. 4.5 g of clear lacquer was added to the obtained paste and was intimately mixed to form a paint. The paint was applied on a cast-coated paper by using a 6-mil applicator to produce a coating film piece (having a film thickness of about 30 µm). The thus obtained coating film piece was measured according to JIS ZU8729 by a multi-light source spectrographic colorimeter MSC-IS-2D (manufactured by SUGA TESTING MACHINES MANUFACTURING CO., LTD.) to determine a L* value of colorimetric indices thereof. (8) The blackness of each of paints containing black particles, was measured with respect to a coating film produced from the paint having the same composition as that of Example 2 or 3, and the blackness of each of rubber or resin compositions containing black particles, was measured with respect to a resin plate having the same composition as that of Example 4. The respective blackness was expressed by a L* value of colorimetric indices which were measured according to JIS ZU8729 by a multi-light source spectrographic colorimeter MSC-IS-2D (manufactured by SUGA TESTING MACHINES MANUFACTURING CO., LTD.). Here, the L* value represents a lightness, and the smaller the L* value, the more excellent the blackness. (9) The dispersibility in a vehicle of paint was measured with respect to a coating film produced in the same manner as in Example 2 or 3, by examining the gloss on the surface of the coating film. The gloss was measured by irradiating light at an incident angle of 20°, using a glossmeter UGV-5D (manufactured by SUGA TESTING MACHINES MANUFACTURING CO., LTD.).The higher the gloss, the more excellent the dispersibility. (10) The viscosity (at 25°C) of the paint prepared in the same manner as in Example 2 or 3, was measured at a shear rate (D) of 1.92 sec -1 by E-type viscometer (cone plate-type viscometer) EMD-R (manufactured by TOKYO KEIKI CO., LTD.). (11) The dispersibility in rubber or resin composition was evaluated by visually counting the number of undispersed aggregate particles on a surface of the rubber or resin composition obtained in the same manner as in Example 4 and classifying the results into the following five ranks. The 5th rank represents most excellent dispersing condition. Rank 1: not less than 50 undispersed aggregate particles per 1 cm 2 were recognized; Rank 2: 10 to 49 undispersed aggregate particles per 1 cm 2 were recognized; Rank 3: 5 to 9 undispersed aggregate particles per 1 cm 2 were recognized; Rank 4: 1 to 4 undispersed aggregate particles per 1 cm 2 were recognized; Rank 5: No undispersed aggregate particles were recognized. (12) The acid resistance of a coating film was measured by the following method. That is, the paints containing the black particles, were applied onto a cold-rolled steel plate (having a size of 0.8 mm x 70 mm x 150 mm: JIS G-3141) and then dried to prepare a sample on which a coating film having a thickness of 150 µm was formed. The gloss and blackness of the thus prepared sample were measured. Next, the sample was suspended by a thread and then was immersed by about 120 mm in depth into a 5 wt. % aqueous sulfuric acid solution of a temperature of 25°C in a 1,000 cc beaker. The sample was allowed to stand in the suspended condition for 24 hours.Next, the sample was removed from the aqueous sulfuric acid solution and gently washed with flowing water. After water attached to the sample was removed by shaking, the gloss and blackness of the treated sample were measured at a central portion thereof. Based on the measured values of gloss and blackness before and after the immersion, the amount of change in gloss (ΔG value) and the amount of change in blackness (ΔL* value) between before and after the immersion were obtained, thereby evaluating the acid resistance of the sample. The smaller both the ΔG value and the ΔL* value, the more excellent the acid resistance. (13) The aging resistance of a rubber or resin composition was measured by the following method. That is, colored resin plates (each having a size of 1.5 cm in length x 1.5 cm in width x 1 mm in thickness) in which the black particles were mixed and kneaded, were heated at 190°C to determine a surface area S of discolored portions thereof caused due to deterioration of the resin. The ratios of the discolored surface area S to a surface area S 0 (1.5 cm x 1.5 cm = 2.25 cm 2 ) of the resin plate before heating were determined and represented at intervals of 5 %. That is, the condition that the percentage of (S/S 0 ) x 100 is 0 %, represents that no deterioration of resin was caused. On the other hand, the condition that the percentage of (S/S 0 ) x 100 is 100 %, represents that a whole portion of the resin was deteriorated. (14) The desorption percentage (T %) of carbon black adhered on the black iron-based composite particles was measured by the following method. That is, 3 g of the black iron-based composite particles and 40 ml of ethanol were placed in a 50-ml precipitation pipe and then was subjected to ultrasonic dispersion for 20 minutes. Thereafter, the obtained dispersion was allowed to stand for 120 minutes, and separated the carbon black desorbed from the black iron-based composite particles on the basis of the difference in specific gravity therebetween. Next, the thus separated black iron-based composite particles were mixed again with 40 ml of ethanol, and the obtained mixture was further subjected to ultrasonic dispersion for 20 minutes. Thereafter, the obtained dispersion was allowed to stand for 120 minutes, thereby separating the black iron-based composite particles and carbon black desorbed, from each other. The thus separated black iron-based composite particles were dried at 100°C for one hour, and then the carbon content thereof was measured by the "Horiba Metal, Carbon and Sulfur Analyzer EMIA-2200 Model" (manufactured by HORIBA SEISAKUSHO CO., LTD.). The desorption percentage (T %) was calculated according to the following formula: T (%) = {(W a - W e )/W a } x 100 wherein W a represents an amount of carbon black initially adhered on the black iron-based composite particles; and We represents an amount of carbon black which still remains adhered on the black iron-based composite particles after the above desorption test. The closer to zero the desorption percentage (T %), the smaller the amount of carbon black desorbed from the black iron-based composite particles. Example 1: 〈Production of black iron-based composite particles〉 20 kg of black manganese-containing hematite particles obtained according to the method described in Japanese Patent Application Laid-open (KOKAI) No. 4-144924(1992) and shown in the electron photograph (x 20,000) of Fig. 1 (particle shape: granular shape; average particle size: 0.30 µm; geometrical standard deviation of particle sizes: 1.46; BET specific surface area value: 3.6 m 2 /g; Mn content: 13.3 wt. %; and blackness (L* value): 22.6), were diaggregated in 150 liters of pure water using a stirrer, and further passed through a TK pipeline homomixer (manufactured by TOKUSHU KIKA KOGYO CO., LTD.) three times, to obtain a slurry containing the black manganese-containing hematite particles. Successively, the obtained slurry was passed through a transverse-type sand grinder (tradename "MIGHTY MILL MHG-1.5L", manufactured by INOUE SEISAKUSHO CO., LTD.) five times at an axis-rotating speed of 2,000 rpm, thereby obtaining a slurry in which the black manganese-containing hematite particles were dispersed. The black manganese-containing hematite particles in the obtained slurry, which remain on a sieve of 325 meshes (mesh size: 44 µm) was 0 %. The slurry was filtered and washed with water, thereby obtaining a wet cake composed of the black manganese-containing hematite particles. The obtained wet cake composed of the black manganese-containing hematite particles was dried at 120°C. 11.0 kg of the dried particles were then charged into an edge runner "MPUV-2 Model" (tradename, manufactured by MATSUMOTO CHUZO TEKKOSHO CO., LTD.), and mixed and stirred at 30 Kg/cm for 30 minutes, thereby lightly diaggregating the particles. 110 g of methyl triethoxysilane was mixed and diluted with 200 ml of ethanol to obtain a solution of methyl triethoxysilane. The methyl triethoxysilane solution was added to the thus diaggregated black manganese-containing hematite particles while operating the edge runner. The black manganese-containing hematite particles were continuously mixed and stirred at a linear load of 60 Kg/cm for 60 minutes. Next, 990 g of carbon black fine particles as shown in the electron photograph (x 20,000) of Fig. 2 (particle shape: granular shape; particle size: 0.022 µm; geometrical standard deviation of particle sizes: 1.68; BET specific surface area value: 134 m 2 /g; and blackness (L* value): 16.6), were added to the black manganese-containing hematite particles coated with methyl triethoxysilane for 10 minutes while operating the edge runner. Further, the particles were continuously mixed and stirred at a linear load of 60 Kg/cm for 60 minutes to adhere the carbon black fine particles on the coating layer composed of methyl triethoxysilane, thereby obtaining black iron-based composite particles. The obtained black iron-based composite particles were dried or heat-treated at 105°C for 60 minutes by using a drier. The resultant black iron-based composite particles were granular particles having an average particle size of 0.31 µm as shown in the electron photograph (x 20,000) of Fig. 3. In addition, the black iron-based composite particles showed a geometrical standard deviation of particle sizes of 1.46, a BET specific surface area value of 9.1 m 2 /g, and a blackness (L* value) of 17.6. The desorption percentage of carbon black fine particles from the black iron-based composite particles was 6.6 %. The amount of a coating organosilane compound produced from methyl triethoxysilane was 0.16 % by weight (calculated as Si). Since no carbon black fine particles were recognized on the electron photograph of Fig. 3, it was confirmed that a whole amount of the carbon black fine particles were adhered on the coating layer composed of the organosilane compound produced from methyl triethoxysilane. For a comparative purpose, the black manganese-containing hematite particles not coated with methyl triethoxysilane and the carbon black fine particles were mixed and stirred together by an edge runner in the same manner as described above, thereby obtaining treated particles as shown in the electron photograph (x 20,000) of Fig. 4. As shown in Fig. 4, it was recognized that the carbon black fine particles were not adhered on the black manganese-containing hematite particles, and the individual particles were present separately. Example 2: 〈Production of solvent-based paint containing black iron-based composite particles〉 10 g of the black iron-based composite particles produced in Example 1, were blended with an amino alkyd resin and a thinner at the following weight ratio, and charged into a 140-ml glass bottle together with 90 g of 3 mm glass beads. Next, the obtained mixture was mixed and dispersed for 90 minutes by a paint shaker, thereby preparing a mill base. Composition of Mill Base: Black iron-based composite particles 12.2 parts by weight Amino alkyd resin (AMILAC No. 1026, produced by KANSAI PAINT CO., LTD.) 19.5 parts by weight Thinner 7.3 parts by weight The above-prepared mill base was blended with an amino alkyd resin at the following weight ratio, and the obtained mixture was further mixed and dispersed for 15 minutes by a paint shaker, thereby obtaining a paint containing the black iron-based composite particles. Composition of paint: Mill base 39.0 parts by weight Amino alkyd resin (AMILAC No. 1026, produced by KANSAI PAINT CO., LTD.) 61.0 parts by weight The coating film produced from the thus obtained paint, showed a gloss of 89 % and a blackness (L* value) of 17.4. Further, as a result of an acid resistance test thereof, the amount of change in gloss (ΔG value) was 5.6 %, and the amount of change in lightness (ΔL* value) was 0.6. Example 3: 〈Production of water-based paint containing black iron-based composite particles〉 7.62 g of the black iron-based composite particles obtained in Example 1, were blended with a water-soluble alkyd resin and the like at the following weight ratio, and charged into a 140-ml glass bottle together with 90 g of 3 mm glass beads. Next, the obtained mixture was mixed and dispersed for 45 minutes or 90 minutes by a paint shaker, thereby preparing a mill base. Composition of Mill Base: Black iron-based composite particles 12.4 parts by weight Water-soluble alkyd resin (tradename: "S-118", produced by DAI-NIPPON INK KAGAKU KOGYO CO., LTD.) 9.0 parts by weight Defoamer (tradename: "NOPCO 8034", produced by SUN NOPCO LTD.) 4.8 parts by weight Water 4.8 parts by weight Butyl cellosolve 4.1 parts by weight The above-prepared mill base was blended with paint components at the following weight ratio, and the obtained mixture was further mixed and dispersed for 15 minutes by a paint shaker, thereby obtaining a water-soluble paint. Composition of paint: Mill base 30.4 parts by weight Water-soluble alkyd resin (tradename: S-118, produced by DAI-NIPPON INK KAGAKU KOGYO CO., LTD.) 46.2 parts by weight Water-soluble melamine resin (tradename: S-695, produced by DAI-NIPPON INK KAGAKU KOGYO CO., LTD.) 12.6 parts by weight Defoamer (tradename: "NOPCO 8034", produced by SUN NOPCO LTD.) 0.1 parts by weight Water 9.1 parts by weight Butyl cellosolve 1.6 parts by weight The coating film prepared from the thus obtained paint, showed a gloss of 87 and a blackness (L* value) of 17.4. Further, as a result of an acid resistance test thereof, the amount of change in gloss (ΔG value) was 5.1 %, and the amount of change in lightness (ΔL* value) was 0.6. Example 4: 〈Production of resin composition〉 2.5 g of the black iron-based composite particles obtained in Example 1, and 47. 5 g of a polyvinyl chloride resin 103EP8D (produced by NIPPON ZEON CO., LTD.) were weighed and charged into a 100 ml beaker, and intimately mixed together by a spatula, thereby obtaining mixed particles. 0.5 g of calcium stearate was added to the mixed particles. The mixed particles were intimately mixed and then slowly supplied to hot rolls heated to 160°C whose clearance was set to 0.2 mm, and continuously kneaded therebetween until a uniform resin composition was produced. The resin composition kneaded was separated from the hot rolls and used as a raw material for forming a colored resin plate. Next, the thus-produced resin composition was interposed between a pair of surface-polished stainless steel plates, placed within a hot press heated to 180°C and subjected to a pressure molding while applying a pressure of 1 ton/cm 2 thereto, thereby obtaining a colored resin plate having a thickness of 1 mm. The thus-produced colored resin plate had a blackness (L* value) of 17.9 and the dispersing condition thereof was the rank 5. The colored resin plate was cut into three 1.5 cm-square test pieces. The three test pieces were placed in Geer oven maintained heated to 190°C and taken out therefrom one by one at intervals of 30 minutes to examine whether or not the resin of each test piece was deteriorated. As a result, the test piece taken out 30 minutes after initiation of the heating showed a degree of resin-deterioration (S/S 0 x 100) of 0 %, the test piece next taken out 60 minutes after initiation of the heating showed a degree of resin-deterioration (S/S 0 x 100) of 5 %, and the test piece lastly taken out 90 minutes after initiation of the heating showed a degree of resin-deterioration (S/S 0 x 100) of 5 %. Core particles 1 to 7: Various black iron oxide particles and black iron oxide hydroxide particles produced by known methods, were prepared. The same procedure as defined in Example 1 was conducted by using these particles, thereby obtaining diaggregated black iron oxide particles and black iron oxide hydroxide particles. Various properties of the thus obtained black iron oxide particles and black iron oxide hydroxide particles are shown in Table 1. Meanwhile, the core particles 1 and 2 were produced by the method described in Japanese Patent Application Laid-open (KOKAI) No. 4-144924(1992). The core particles 3 were produced by the method described in Japanese Patent Publication (KOKOKU) No. 44-668(1969). The core particles 4 were produced by the method described in Japanese Patent Publication (KOKOKU) No. 3-9045(1991). The core particles 5 were produced by first preparing acicular goethite particles and then heat-treating the obtained acicular goethite particles at 340°C in air, followed by heat-treating the acicular goethite particles at 400°C in a hydrogen stream by the method described in Japanese Patent Publication (KOKOKU) No. 55-6579(1980). Further, the core particles 6 and 7 were produced by the method described in Japanese Patent Application Laid-open (KOKAI) No. 6-263449(1994). Core particles 8: The same procedure as defined in Example 1 was conducted by using 20 kg of the diaggregated black manganese-containing hematite particles (core particles 1) and 150 liters of water, thereby obtaining a slurry containing the black manganese-containing hematite particles. The pH value of the obtained re-dispersed slurry containing the black manganese-containing hematite particles was adjusted to 10.5, and then the concentration of the solid content in the slurry was adjusted to 98 g/liter by adding water thereto. After 150 liters of the slurry was heated to 60°C, 2722 ml of a 1.0 mol/liter NaAlO 2 solution (corresponding to 0.5 % by weight (calculated as Al) based on the weight of the black manganese-containing hematite particles) was added to the slurry. After allowing the obtained slurry to stand for 30 minutes, the pH value of the slurry was adjusted to 7.5 by using acetic acid. After further allowing the resultant slurry to stand for 30 minutes, the slurry was subjected to filtration, washing with water, drying and pulverization, thereby obtaining the black manganese-containing hematite particles whose surface was coated with hydroxides of aluminum. The thus obtained black manganese-containing hematite particles whose surface was coated with hydroxides of aluminum were granular particles having a particle size of 0.32 µm. The geometrical standard deviation of particle sizes of the obtained particles was 1.47, the BET specific surface area value was 3.8 m 2 /g, and the blackness (L* value) was 22.6. As a result of fluorescent X-ray analysis, the obtained particles had a Mn content of 13.0 % by weight and an Al content of 0.49 % by weight. Core particles 9 to 14: The same procedure as defined above for the production of the core particles 8, was conducted except that kinds of core particles and kinds and amounts of additives used in the above surface treatment were changed variously, thereby obtaining surface-treated black iron oxide particles and surface-treated black iron oxide hydroxide particles. The essential treating conditions are shown in Table 2, and various properties of the obtained surface-treated core particles are shown in Table 3. Examples 5 to 11 and Comparative Examples 1 to 5: The same procedure as defined in Example 1 was conducted except that kinds of black iron oxide particles and black iron oxide hydroxide particles, addition or non-addition of alkoxysilane, kinds and amounts of alkoxysilane added, treating conditions of an edge runner used in the alkoxysilane-coating process, kinds and amounts of carbon black fine particles adhered, and treating conditions of an edge runner used in the process for adhering the carbon black fine particles, were changed variously, thereby obtaining black iron-based composite particles. As a result of the observation by an electron microscope, no carbon black fine particles were recognized in the black iron-based composite particles obtained in Examples 5 to 11. Therefore, it was confirmed that a substantially whole amount of the carbon black fine particles used in Examples 5 to 11 were adhered on the coating layer composed of an organosilane compound produced from the alkoxysilane. Various properties of the carbon black fine particles A to C used, are shown in Table 4. The essential treating conditions are shown in Table 5, and various properties of the obtained black iron-based composite particles are shown in Table 6. Example 12: 11.0 kg of the core particles 8, i.e., the black manganese-containing hematite particles whose surface was coated with hydroxides of aluminum, were charged into an edge runner "MPUV-2 Model" (manufactured by MATSUMOTO CHUZO TEKKOSHO CO., LTD.), and mixed and stirred at 30 kg/cm for 30 minutes, thereby diaggregating the particles. 220 g of methyl triethoxysilane was mixed and diluted with 400 ml of ethanol to prepare a solution of methyl triethoxysilane. The thus prepared methyl triethoxysilane solution was added to the diaggregated black manganese-containing hematite particles whose surface was coated with hydroxides of aluminum while operating the edge runner. The black manganese-containing hematite particles were continuously mixed and stirred at a linear load of 60 kg/cm for 30 minutes. Next, 1,100 g of the carbon black fine particles A were added to the black manganese-containing hematite particles coated with methyl triethoxysilane, for 10 minutes while operating the edge runner. Further, the particles were continuously mixed and stirred at a linear load of 75 kg/cm for 30 minutes to adhere the carbon black fine particles on the coating layer composed of methyl triethoxysilane, thereby obtaining black iron-based composite particles. The obtained black iron-based composite particles were heat-treated at 105°C for 60 minutes by using a drier. The black iron-based composite particles were granular particles having an particle size of 0.32 µm. In addition, the geometrical standard deviation of particle sizes of the obtained black iron-based composite particles was 1.44; the BET specific surface area value was 4.6 m 2 /g; the blackness (L* value) was 16.5; the desorption percentage of carbon black was 4.8 %. The coating amount of the organosilane compound produced from methyl triethoxysilane was 0.31 % by weight (calculated as Si). Meanwhile, since almost no carbon black fine particles were recognized as a result of the observation by an electron microscope, it was confirmed that substantially a whole amount of the carbon black fine particles were adhered on the coating layer composed of the organosilane compound produced from methyl triethoxysilane. Examples 13 to 18: The same procedure as defined in Example 12 was conducted except that kinds of black iron oxide particles and black iron oxide hydroxide particles, kinds and amounts of alkoxysilane added, treating conditions of an edge runner used in the alkoxysilane-coating process, kinds and amounts of carbon black fine particles adhered, and treating conditions of an edge runner used in the process for adhering the carbon black fine particles, were changed variously, thereby obtaining black iron-based composite particles. As a result of the observation by an electron microscope, almost no carbon black fine particles were recognized in the black iron-based composite particles obtained in Examples 13 to 18. Therefore, it was confirmed that substantially a whole amount of the carbon black fine particles used were adhered on the coating layer composed of a organosilane compound produced from the alkoxysilane. The essential treating conditions are shown in Table 5, and various properties of the obtained black iron-based composite particles are shown in Table 6. Comparative Example 6 (Method described in Japanese Patent Publication (KOKOKU) No, 50-13300(1975)): 1,000 ml of a water suspension containing 68.3 g of the core particles 3, i.e., magnetite particles (black iron oxide particles) was prepared, and then washed with cold water five times. Next, 5 g of a water dispersion containing 1.75 g of the dried carbon black fine particles B was diluted with 500 ml of cold water. While stirring, the carbon black-containing water dispersion was added to the water suspension containing the magnetite particles, for 5 minutes. After completion of the addition, the mixed suspension was continuously stirred for 10 minutes and then allowed to stand. After about 4 hours, the obtained black precipitates were washed with water five times by an ordinary method, and then dried at 100°C in air. The obtained black particles had a blackness (L* value) of 20.0 which was substantially unchanged from those of the magnetite particles as the core particles and a carbon black desorption percentage of 50.2 %. Examples 19 to 32 and Comparative Examples 7 to 21: 〈Production of solvent-based paint〉 The same procedure as defined in Example 2 was conducted except that kinds of black particles were changed variously, thereby obtaining solvent-based paints. The essential production conditions and various properties of coating films obtained from the solvent-based paints are shown in Tables 7 and 8, respectively. Examoles 33 to 46 and Comparative Examples 22 to 36: 〈Production of water-based paint〉 The same procedure as defined in Example 3 was conducted except that kinds of black particles were changed variously, thereby obtaining water-based paints. The essential production conditions and various properties of coating films obtained from the water-based paints are shown in Tables 9 and 10, respectively. Examples 47 to 60 and Comparative Examples 37 to 51: 〈Production of resin composition〉 The same procedure as defined in Example 4 was conducted except that kinds of black particles were changed variously, thereby obtaining resin compositions. The essential production conditions and various properties of colored resin plates obtained from the resin compositions are shown in Tables 11 and 12, respectively. Example 61: 110 g of methyl hydrogen polysiloxane (tradename: "TSF484", produced by TOSHIBA SILICONE CO., LTD.) was added to the diaggregated black manganese-containing hematite particles obtained in Example 1, while operating an edge runner "MPUV-2 Model" (manufactured by MATSUMOTO CHUZO TEKKOSHO CO., LTD.), and then continuously mixed and stirred at a linear load of 60 kg/cm for 60 minutes. Next, 550 g of carbon black fine particles (particle shape: granular shape; particle size: 0.022 µm; geometrical standard deviation of particle sizes: 1.68; BET specific surface area value: 134 m 2 /g; and blackness (L* value): 16.6) were added to the black manganese-containing hematite particles coated with methyl hydrogen polysiloxane, for 10 minutes while operating the edge runner. Further, the obtained particles were continuously mixed and stirred at a linear load of 60 kg/cm for 60 minutes to adhere the carbon black fine particles on the coating layer composed of methyl hydrogen polysiloxane, thereby obtaining black iron-based composite particles. The obtained black iron-based composite particles was dried at 105°C for 60 minutes by using a drier. The obtained black iron-based composite particles were granular particles having an particle size of 0.31 µm. In addition, the geometrical standard deviation of particle sizes of the black iron-based composite particles was 1.46; the BET specific surface area value was 8.9 m 2 /g; the blackness (L* value) was 18.2; the carbon black desorption percentage was 6.4 %. The coating amount of the methyl hydrogen polysiloxane was 0.41 % by weight (calculated as Si). As a result of the observation by an electron microscope, since almost no carbon black fine particles were recognized in the obtained composite particles, it was confirmed that substantially a whole amount of the carbon black fine particles were adhered on the coating layer composed of the methyl hydrogen polysiloxane. Example 62: The same procedure as defined in Example 2 was conducted except that black iron-based composite particles obtained in Example 61 were used, thereby obtaining a solvent-based paint. A coating film obtained from the solvent-based paint had a gloss of 91 % and a blackness (L* value) of 18.6. As a result of an acid resistance test of the coating film, the amount of change in gloss (ΔG value) was 6.1 % and the amount of change in lightness (ΔL* value) was 0.7. Example 63: The same procedure as defined in Example 3 was conducted except that black iron-based composite particles obtained in Example 61 were used, thereby obtaining a water-based paint. A coating film obtained from the water-based paint had a gloss of 86 % and a blackness (L* value) of 18.8. As a result of an acid resistance test of the coating film, the amount of change in gloss (ΔG value) was 5.3 % and the amount of change in lightness (ΔL* value) was 0.7. Example 64: The same procedure as defined in Example 4 was conducted except that black iron-based composite particles obtained in Example 61 were used, thereby obtaining a colored resin plate. The thus obtained colored resin plate had a blackness (L* value) of 17.9 and the dispersion condition thereof was the rank 5. The colored resin plate was cut into three 1.5 cm-square test pieces. The three test pieces were placed in Geer oven maintained at 190°C and were taken out therefrom one by one at intervals of 30 minutes to examine whether or not the resin of each test piece was deteriorated. As a result, the test piece taken out 30 minutes after initiation of the heating showed a degree of resin-deterioration (S/S 0 x 100) of 0 %, the test piece next taken out 60 minutes after initiation of the heating showed a degree of resin-deterioration (S/S 0 x 100) of 0 %, and the test piece lastly taken out 90 minutes after initiation of the heating showed a degree of resin-deterioration (S/S 0 x 100) of 5 %. Examples 65 to 71 and Comparative Examples 52 to 54: The same procedure as defined in Example 61 was conducted except that kinds of black iron oxide particles and black iron oxide hydroxide particles, kinds and amounts of polysiloxane added, treating conditions of an edge runner used in the polysiloxane-coating process, kinds and amounts of carbon black fine particles adhered, and treating conditions of an edge runner used in the process for adhering the carbon black fine particles, were changed variously, thereby obtaining black iron-based composite particles. As a result of the observation by an electron microscope, almost no carbon black fine particles were recognized in the black iron-based composite particles obtained in Examples 65 to 71. Therefore, it was confirmed that substantially a whole amount of the carbon black fine particles used were adhered on the coating layer composed of polysiloxane. The essential treating conditions are shown in Table 13, and various properties of the obtained black iron-based composite particles are shown in Table 14. Example 72: 11.0 kg of the core particles 8, i.e., the black manganese-containing hematite particles whose surface was coated with hydroxides of aluminum, were charged into an edge runner "MPUV-2 Model" (manufactured by MATSUMOTO CHUZO TEKKOSHO CO., LTD.), and mixed and stirred at 30 kg/cm for 30 minutes, thereby diaggregating the particles. 165 g of methyl hydrogen polysiloxane (tradename: "TSF484", produced by TOSHIBA SILICONE CO., LTD.) were added to the diaggregated black manganese-containing hematite particles whose surface was coated with hydroxides of aluminum while operating the edge runner. The black manganese-containing hematite particles were continuously mixed and stirred at a linear load of 30 kg/cm for 30 minutes. Next, 550 g of the carbon black fine particles A were added to the black manganese-containing hematite particles coated with methyl hydrogen polysiloxane, for 10 minutes while operating the edge runner. Further, the particles were continuously mixed and stirred at a linear load of 75 kg/cm for 30 minutes to adhere the carbon black fine particles on the coating layer composed of methyl hydrogen polysiloxane, thereby obtaining black iron-based composite particles. The obtained black iron-based composite particles were dried at 105°C for 60 minutes by using a drier. The black iron-based composite particles were granular particles having an particle size of 0.32 µm. In addition, the geometrical standard deviation of particle sizes of the obtained black iron-based composite particles was 1.45; the BET specific surface area value was 4.1 m 2 /g; the blackness (L* value) was 16.9; the desorption percentage of carbon black was 4.9 %. The coating amount of the methyl hydrogen polysiloxane was 0.65 % by weight (calculated as Si). Meanwhile, since almost no carbon black fine particles were recognized as a result of the observation by an electron microscope, it was confirmed that substantially a whole amount of the carbon black fine particles were adhered on the coating layer composed of the methyl hydrogen polysiloxane. Examples 73 to 78: The same procedure as defined in Example 72 was conducted except that kinds of black iron oxide particles and black iron oxide hydroxide particles, kinds and amounts of polysiloxane added, treating conditions of an edge runner used in the polysiloxane-coating process, kinds and amounts of carbon black fine particles adhered, and treating conditions of an edge runner used in the process for adhering the carbon black fine particles, were changed variously, thereby obtaining black iron-based composite particles. As a result of the observation by an electron microscope, almost no carbon black fine particles were recognized in the black iron-based composite particles obtained in Examples 73 to 78. Therefore, it was confirmed that substantially a whole amount of the carbon black fine particles used were adhered on the coating layer composed of a polysiloxane. The essential treating conditions are shown in Table 13, and various properties of the obtained black iron-based composite particles are shown in Table 14. Examples 79 to 92 and Comparative Examples 55 to 57: 〈Production of solvent-based paint〉 The same procedure as defined in Example 2 was conducted except that kinds of black particles were changed variously, thereby obtaining solvent-based paints. The essential production conditions and various properties of coating films obtained from the solvent-based paints are shown in Table 15. Examples 93 to 106 and Comparative Examples 58 to 60: 〈Production of water-based paint〉 The same procedure as defined in Example 3 was conducted except that kinds of black particles were changed variously, thereby obtaining water-based paints. The essential production conditions and various properties of coating films obtained from the water-based paints are shown in Table 16. Examples 107 to 120 and Comparative Examples 61 to 63: 〈Production of resin composition〉 The same procedure as defined in Example 4 was conducted except that kinds of black particles were changed variously, thereby obtaining resin compositions. The essential production conditions and various properties of colored resin plates obtained from the resin compositions are shown in Table 17. Example 121: 110 g of polyether-modified polysiloxane (tradename "BYK-080", produced by BYK-Chemie CO., LTD.) were added to the diaggregated black manganese-containing hematite particles obtained in Example 1, while operating an edge runner "MPUV-2 Model" (manufactured by MATSUMOTO CHUZO TEKKOSHO CO., LTD.), and then continuously mixed and stirred at a linear load of 60 kg/cm for 60 minutes. Next, 550 g of carbon black fine particles (particle shape: granular shape; particle size: 0.022 µm; geometrical standard deviation of particle sizes: 1.68; BET specific surface area: 134 m 2 /g; and blackness (L* value): 16.6) were added to the black manganese-containing hematite particles coated with polyether-modified polysiloxane, for 10 minutes while operating the edge runner. Further, the obtained particles were continuously mixed and stirred at a linear load of 60 kg/cm for 60 minutes to adhere the carbon black fine particles on the coating layer composed of polyether-modified polysiloxane, thereby obtaining black iron-based composite particles. The obtained black iron-based composite particles was dried at 105°C for 60 minutes by using a drier. The obtained black iron-based composite particles were granular particles having an particle size of 0.31 µm. In addition, the geometrical standard deviation of particle sizes of the black iron-based composite particles was 1.46; the BET specific surface area value was 4.6 m 2 /g; the blackness (L* value) was 17.6; the carbon black desorption percentage was 6.2 %. The coating amount of the polyether-modified polysiloxane was 0.19 % by weight (calculated as Si). As a result of the observation by an electron microscope, since almost no carbon black fine particles were recognized in the obtained composite particles, it was confirmed that substantially a whole amount of the carbon black fine particles were adhered on the coating layer composed of the polyether-modified polysiloxane. Example 122: The same procedure as defined in Example 2 was conducted except that black iron-based composite particles obtained in Example 121 were used, thereby obtaining a solvent-based paint. A coating film obtained from the solvent-based paint had a gloss of 101 % and a blackness (L* value) of 17.2. As a result of an acid resistance test of the coating film, the amount of change in gloss (ΔG value) was 6.3 % and the amount of change in lightness (ΔL* value) was 0.6. Example 123: The same procedure as defined in Example 3 was conducted except that black iron-based composite particles obtained in Example 121 were used, thereby obtaining a water-based paint. A coating film obtained from the water-based paint had a gloss of 92 % and a blackness (L* value) of 17.8. As a result of an acid resistance test of the coating film, the amount of change in gloss (ΔG value) was 6.1 % and the amount of change in lightness (ΔL* value) was 0.8. Example 124: The same procedure as defined in Example 4 was conducted except that black iron-based composite particles obtained in Example 121 were used, thereby obtaining a colored resin plate. The thus obtained colored resin plate had a blackness (L* value) of 18.0 and the dispersion condition thereof was the rank 5. The colored resin plate was cut into three 1.5 cm-square test pieces. The three test pieces were placed in Geer oven maintained at 190°C and were taken out therefrom one by one at intervals of 30 minutes to examine whether or not the resin of each test piece was deteriorated. As a result, the test piece taken out 30 minutes after initiation of the heating showed a degree of resin-deterioration (S/S 0 x 100) of 0 %, the test piece next taken out 60 minutes after initiation of the heating showed a degree of resin-deterioration (S/S 0 x 100) of 0 %, and the test piece lastly taken out 90 minutes after initiation of the heating showed a degree of resin-deterioration (S/S 0 x 100) of 5 %. Examples 125 to 131 and Comparative Examples 64 to 66: The same procedure as defined in Example 121 was conducted except that kinds of black iron oxide particles and black iron oxide hydroxide particles, kinds and amounts of modified polysiloxane added, treating conditions of an edge runner used in the modified polysiloxane-coating process, kinds and amounts of carbon black fine particles adhered, and treating conditions of an edge runner used in the process for adhering the carbon black fine particles, were changed variously, thereby obtaining black iron-based composite particles. As a result of the observation by an electron microscope, almost no carbon black fine particles were recognized in the black iron-based composite particles obtained in Examples 125 to 131. Therefore, it was confirmed that substantially a whole amount of the carbon black fine particles used were adhered on the coating layer composed of modified polysiloxane. The essential treating conditions are shown in Table 18, and various properties of the obtained black iron-based composite particles are shown in Table 19. Example 132: 11.0 kg of the core particles 8, i.e., the black manganese-containing hematite particles whose surface was coated with hydroxides of aluminum, were charged into an edge runner "MPUV-2 Model" (manufactured by MATSUMOTO CHUZO TEKKOSHO CO., LTD.), and mixed and stirred at 30 kg/cm for 30 minutes, thereby diaggregating the particles. 220 g of polyether-modified polysiloxane (tradename "BYK-080", produced by BYK-Chemie CO., LTD.) were added to the diaggregated black manganese-containing hematite particles whose surface was coated with hydroxides of aluminum while operating the edge runner. The black manganese-containing hematite particles were continuously mixed and stirred at a linear load of 75 kg/cm for 15 minutes. Next, 550 g of the carbon black fine particles A were added to the black manganese-containing hematite particles coated with polyether-modified polysiloxane, for 10 minutes while operating the edge runner. Further, the particles were continuously mixed and stirred at a linear load of 60 kg/cm for 30 minutes to adhere the carbon black fine particles on the coating layer composed of polyether-modified polysiloxane, thereby obtaining black iron-based composite particles. The obtained black iron-based composite particles was dried at 105°C for 60 minutes by using a drier. The black iron-based composite particles were granular particles having an particle size of 0.32 µm. In addition, the geometrical standard deviation of particle sizes of the obtained black iron-based composite particles was 1.44; the BET specific surface area value was 4.6 m 2 /g; the blackness (L* value) was 16.5; the desorption percentage of carbon black was 4.1 %. The coating amount of the polyether-modified polysiloxane was 0.36 % by weight (calculated as Si). Meanwhile, since almost no carbon black fine particles were recognized as a result of the observation by an electron microscope, it was confirmed that substantially a whole amount of the carbon black fine particles were adhered on the coating layer composed of polyether-modified polysiloxane. Examples 133 to 138: The same procedure as defined in Example 132 was conducted except that kinds of black iron oxide particles and black iron oxide hydroxide particles, kinds and amounts of modified polysiloxane added, treating conditions of an edge runner used in the modified polysiloxane -coating process, kinds and amounts of carbon black fine particles adhered, and treating conditions of an edge runner used in the process for adhering the carbon black fine particles, were changed variously, thereby obtaining black iron-based composite particles. As a result of the observation by an electron microscope, almost no carbon black fine particles were recognized in the black iron-based composite particles obtained in Examples 133 to 138. Therefore, it was confirmed that substantially a whole amount of the carbon black fine particles used were adhered on the coating layer composed of a modified polysiloxane. The essential treating conditions are shown in Table 18, and various properties of the obtained black iron-based composite particles are shown in Table 19. Examples 139 to 152 and Comparative Examples 67 to 69: 〈Production of solvent-based paint〉 The same procedure as defined in Example 2 was conducted except that kinds of black particles were changed variously, thereby obtaining solvent-based paints. The essential production conditions and various properties of coating films obtained from the solvent-based paints are shown in Table 20. Examoles 153 to 166 and Comparative Examples 70 to 72: 〈Production of water-based paint〉 The same procedure as defined in Example 3 was conducted except that kinds of black particles were changed variously, thereby obtaining water-based paints. The essential production conditions and various properties of coating films obtained from the water-based paints are shown in Table 21. Examples 167 to 180 and Comparative Examples 73 to 75: 〈Production of resin composition〉 The same procedure as defined in Example 4 was conducted except that kinds of black particles were changed variously, thereby obtaining resin compositions. The essential production conditions and various properties of colored resin plates obtained from the resin compositions are shown in Table 22. Example 181: 220 g of carboxylic acid-terminal-modified polysiloxane (tradename: "TSF4770", produced by TOSHIBA SILICONE CO., LTD.) was added to the diaggregated black manganese-containing hematite particles obtained in Example 1, while operating an edge runner "MPUV-2 Model" (manufactured by MATSUMOTO CHUZO TEKKOSHO CO., LTD.), and then continuously mixed and stirred at a linear load of 60 kg/cm for 30 minutes. Next, 550 g of carbon black fine particles (particle shape: granular shape; particle size: 0.022 µm; geometrical standard deviation of particle sizes: 1.68; BET specific surface area value: 134 m 2 /g; and blackness (L* value): 16.6) were added to the black manganese-containing hematite particles coated with carboxylic acid-terminal-modified polysiloxane, for 10 minutes while operating the edge runner. Further, the obtained particles were continuously mixed and stirred at a linear load of 60 kg/cm for 30 minutes to adhere the carbon black fine particles on the coating layer composed of carboxylic acid-terminal-modified polysiloxane, thereby obtaining black iron-based composite particles. The obtained black iron-based composite particles was dried at 105°C for 60 minutes by using a drier. The obtained black iron-based composite particles were granular particles having an particle size of 0.32 µm. In addition, the geometrical standard deviation of particle sizes of the black iron-based composite particles was 1.46; the BET specific surface area value was 4.2 m 2 /g; the blackness (L* value) was 17.9; the carbon black desorption percentage was 6.7 %. The coating amount of the carboxylic acid-terminal-modified polysiloxane was 0.43 % by weight (calculated as Si). As a result of the observation by an electron microscope, since almost no carbon black fine particles were recognized in the obtained composite particles, it was confirmed that substantially a whole amount of the carbon black fine particles were adhered on the coating layer composed of carboxylic acid-terminal-modified polysiloxane. Example 182: The same procedure as defined in Example 2 was conducted except that black iron-based composite particles obtained in Example 181 were used, thereby obtaining a solvent-based paint. A coating film obtained from the solvent-based paint had a gloss of 98 % and a blackness (L* value) of 17.8. As a result of an acid resistance test of the coating film, the amount of change in gloss (ΔG value) was 7.1 % and the amount of change in lightness (ΔL* value) was 0.7. Example 183: The same procedure as defined in Example 3 was conducted except that black iron-based composite particles obtained in Example 181 were used, thereby obtaining a water-based paint. A coating film obtained from the water-based paint had a gloss of 93 % and a blackness (L* value) of 18.1. As a result of an acid resistance test of the coating film, the amount of change in gloss (ΔG value) was 7.3 % and the amount of change in lightness (ΔL* value) was 0.8. Example 184: The same procedure as defined in Example 4 was conducted except that black iron-based composite particles obtained in Example 181 were used, thereby obtaining a colored resin plate. The thus obtained colored resin plate had a blackness (L* value) of 18.0 and the dispersion condition thereof was the rank 5. The colored resin plate was cut into three 1.5 cm-square test pieces. The three test pieces were placed in Geer oven maintained at 190°C and were taken out therefrom one by one at intervals of 30 minutes to examine whether or not the resin of each test piece was deteriorated. As a result, the test piece taken out 30 minutes after initiation of the heating showed a degree of resin-deterioration (S/S 0 x 100) of 0 %, the test piece next taken out 60 minutes after initiation of the heating showed a degree of resin-deterioration (S/S 0 x 100) of 0 %, and the test piece lastly taken out 90 minutes after initiation of the heating showed a degree of resin-deterioration (S/S 0 x 100) of 5 %. Examples 185 to 191 and Comparative Examples 76 to 78: The same procedure as defined in Example 181 was conducted except that kinds of black iron oxide particles and black iron oxide hydroxide particles, kinds and amounts of terminal-modified polysiloxane added, treating conditions of an edge runner used in the terminal-modified polysiloxane -coating process, kinds and amounts of carbon black fine particles adhered, and treating conditions of an edge runner used in the process for adhering the carbon black fine particles, were changed variously, thereby obtaining black iron-based composite particles. As a result of the observation by an electron microscope, almost no carbon black fine particles were recognized in the black iron-based composite particles obtained in Examples 185 to 191. Therefore, it was confirmed that substantially a whole amount of the carbon black fine particles used were adhered on the coating layer composed of terminal-modified polysiloxane. The essential treating conditions are shown in Table 23, and various properties of the obtained black iron-based composite particles are shown in Table 44. Example 192: 11.0 kg of the core particles 8, i.e., the black manganese-containing hematite particles whose surface was coated with hydroxides of aluminum, were charged into an edge runner "MPUV-2 Model" (manufactured by MATSUMOTO CHUZO TEKKOSHO CO., LTD.), and mixed and stirred at 30 kg/cm for 30 minutes, thereby diaggregating the particles. 110 g of carboxylic acid-terminal-modified polysiloxane was added to the diaggregated black manganese-containing hematite particles whose surface was coated with hydroxides of aluminum while operating the edge runner. The black manganese-containing hematite particles were continuously mixed and stirred at a linear load of 30 kg/cm for 45 minutes. Next, 825 g of the carbon black fine particles A were added to the black manganese-containing hematite particles coated with carboxylic acid-terminal-modified polysiloxane, for 10 minutes while operating the edge runner. Further, the particles were continuously mixed and stirred at a linear load of 45 kg/cm for 45 minutes to adhere the carbon black fine particles on the coating layer composed of carboxylic acid-terminal-modified polysiloxane, thereby obtaining black iron-based composite particles. The obtained black iron-based composite particles was dried at 105°C for 60 minutes by using a drier. The black iron-based composite particles were granular particles having an particle size of 0.32 µm. In addition, the geometrical standard deviation of particle sizes of the obtained black iron-based composite particles was 1.44; the BET specific surface area value was 5.1 m 2 /g; the blackness (L* value) was 16.6; the desorption percentage of carbon black was 3.6 %. The coating amount of carboxylic acid-terminal-modified polysiloxane was 0.21 % by weight (calculated as Si). Meanwhile, since almost no carbon black fine particles were recognized as a result of the observation by an electron microscope, it was confirmed that substantially a whole amount of the carbon black fine particles were adhered on the coating layer composed of the carboxylic acid-terminal-modified polysiloxane. Examples 193 to 198: The same procedure as defined in Example 192 was conducted except that kinds of black iron oxide particles and black iron oxide hydroxide particles, kinds and amounts of terminal-modified polysiloxane added, treating conditions of an edge runner used in the terminal-modified polysiloxane-coating process, kinds and amounts of carbon black fine particles adhered, and treating conditions of an edge runner used in the process for adhering the carbon black fine particles, were changed variously, thereby obtaining black iron-based composite particles. As a result of the observation by an electron microscope, almost no carbon black fine particles were recognized in the black iron-based composite particles obtained in Examples 193 to 198. Therefore, it was confirmed that substantially a whole amount of the carbon black fine particles used were adhered on the coating layer composed of a terminal-modified polysiloxane. The essential treating conditions are shown in Table 23, and various properties of the obtained black iron-based composite particles are shown in Table 24. Examples 199 to 212 and Comparative Examples 79 to 81: 〈Production of solvent-based paint〉 The same procedure as defined in Example 2 was conducted except that kinds of black particles were changed variously, thereby obtaining solvent-based paints. The essential production conditions and various properties of coating films obtained from the solvent-based paints are shown in Table 25. Examples 213 to 226 and Comparative Examples 82 to 84: 〈Production of water-based paint〉 The same procedure as defined in Example 3 was conducted except that kinds of black particles were changed variously, thereby obtaining water-based paints. The essential production conditions and various properties of coating films obtained from the water-based paints are shown in Table 26. Examples 227 to 240 and Comparative Examples 85 to 87: 〈Production of resin composition〉 The same procedure as defined in Example 4 was conducted except that kinds of black particles were changed variously, thereby obtaining resin compositions. The essential production conditions and various properties of colored resin plates obtained from the resin compositions are shown in Table 27. Example 241: 165 g of tridecafluorooctyl trimethoxysilane (tradename "TSL8257", produced by TOSHIBA SILICONE CO., LTD.) were added to the diaggregated black manganese-containing hematite particles obtained in Example 1, while operating an edge runner "MPUV-2 Model" (manufactured by MATSUMOTO CHUZO TEKKOSHO CO., LTD.), and then continuously mixed and stirred at a linear load of 60 kg/cm for 30 minutes. Next, 550 g of carbon black fine particles (particle shape: granular shape; particle size: 0.022 µm; geometrical standard deviation of particle sizes: 1.68; BET specific surface area value: 134 m 2 /g; and blackness (L* value): 16.6) were added to the black manganese-containing hematite particles coated with tridecafluorooctyl trimethoxysilane, for 10 minutes while operating the edge runner. Further, the obtained particles were continuously mixed and stirred at a linear load of 60 kg/cm for 30 minutes to adhere the carbon black fine particles on the coating layer composed of tridecafluoro0ctyl trimethoxysilane, thereby obtaining black iron-based composite particles. The obtained black iron-based composite particles was dried or heat-treated at 105°C for 60 minutes by using a drier. The obtained black iron-based composite particles were granular particles having an particle size of 0.31 µm. In addition, the geometrical standard deviation of particle sizes of the black iron-based composite particles was 1.45; the BET specific surface area value was 5.0 m 2 /g; the blackness (L* value) was 17.8; the carbon black desorption percentage was 6.5 %. The coating amount of the fluoroalkyl organosilane compound produced from tridecafluorooctyl trimethoxysilane was 0.10 % by weight (calculated as Si). As a result of the observation by an electron microscope, since almost no carbon black fine particles were recognized in the obtained composite particles, it was confirmed that substantially a whole amount of the carbon black fine particles were adhered on the coating layer composed of the fluoroalkyl organosilane compound produced from tridecafluoroalkyl trimethoxysilane. Example 242: The same procedure as defined in Example 2 was conducted except that black iron-based composite particles obtained in Example 241 were used, thereby obtaining a solvent-based paint. A coating film obtained from the solvent-based paint had a gloss of 96 % and a blackness (L* value) of 17.3. As a result of an acid resistance test of the coating film, the amount of change in gloss (ΔG value) was 7.2 % and the amount of change in lightness (ΔL* value) was 0.7. Example 243: The same procedure as defined in Example 3 was conducted except that black iron-based composite particles obtained in Example 241 were used, thereby obtaining a water-based paint. A coating film obtained from the water-based paint had a gloss of 91 % and a blackness (L* value) of 17.9. As a result of an acid resistance test of the coating film, the amount of change in gloss (ΔG value) was 8.3 % and the amount of change in lightness (ΔL* value) was 0.7. Example 244: The same procedure as defined in Example 4 was conducted except that black iron-based composite particles obtained in Example 241 were used, thereby obtaining a colored resin plate. The thus obtained colored resin plate had a blackness (L* value) of 18.0 and the dispersion condition thereof was the rank 5. The colored resin plate was cut into three 1.5 cm-square test pieces. The three test pieces were placed in Geer oven maintained at 190°C and were taken out therefrom one by one at intervals of 30 minutes to examine whether or not the resin of each test piece was deteriorated. As a result, the test piece taken out 30 minutes after initiation of the heating showed a degree of resin-deterioration (S/S 0 x 100) of 0 %, the test piece next taken out 60 minutes after initiation of the heating showed a degree of resin-deterioration (S/S 0 x 100) of 5 %, and the test piece lastly taken out 90 minutes after initiation of the heating showed a degree of resin-deterioration (S/S 0 x 100) of 5 %. Examples 245 to 251 and Comparative Examples 88 to 90: The same procedure as defined in Example 241 was conducted except that kinds of black iron oxide particles and black iron oxide hydroxide particles, kinds and amounts of fluoroalkyl silane compounds added, treating conditions of an edge runner used in the fluoroalkyl silane compound-coating process, kinds and amounts of carbon black fine particles adhered, and treating conditions of an edge runner used in the process for adhering the carbon black fine particles, were changed variously, thereby obtaining black iron-based composite particles. As a result of the observation by an electron microscope, almost no carbon black fine particles were recognized in the black iron-based composite particles obtained in Examples 245 to 251. Therefore, it was confirmed that substantially a whole amount of the carbon black fine particles used were adhered on the coating layer composed of fluoroalkyl organosilane compounds. The essential treating conditions are shown in Table 28, and various properties of the obtained black iron-based composite particles are shown in Table 29. Example 252: 11.0 kg of the core particles 8, i.e., the black manganese-containing hematite particles whose surface was coated with hydroxides of aluminum, were charged into an edge runner "MPUV-2 Model" (manufactured by MATSUMOTO CHUZO TEKKOSHO CO., LTD.), and mixed and stirred at 30 kg/cm for 30 minutes, thereby diaggregating the particles. 660 g of tridecafluorooctyl trimethoxysilane (tradename "TSL-8257", produced by TOSHIBA SILICONE CO., LTD.) was added to the diaggregated black manganese-containing hematite particles whose surface was coated with hydroxides of aluminum while operating the edge runner. The black manganese-containing hematite particles were continuously mixed and stirred at a linear load of 75 kg/cm for 30 minutes. Next, 1,100 g of the carbon black fine particles A were added to the black manganese-containing hematite particles coated with tridecafluorooctyl trimethoxysilane, for 10 minutes while operating the edge runner. Further, the particles were continuously mixed and stirred at a linear load of 60 kg/cm for 45 minutes to adhere the carbon black fine particles on the coating layer composed of tridecafluorooctyl trimethoxysilane, thereby obtaining black iron-based composite particles. The obtained black iron-based composite particles was dried or heat-treated at 105°C for 60 minutes by using a drier. The black iron-based composite particles were granular particles having an particle size of 0.32 µm. In addition, the geometrical standard deviation of particle sizes of the obtained black iron-based composite particles was 1.48; the BET specific surface area value was 4.8 m 2 /g; the blackness (L* value) was 16.6; the desorption percentage of carbon black was 3.6 %. The coating amount of the fluoroalkyl organosilane compound produced from tridecafluorooctyl trimethoxysilane was 0.40 % by weight (calculated as Si). Meanwhile, since almost no carbon black fine particles were recognized as a result of the observation by an electron microscope, it was confirmed that substantially a whole amount of the carbon black fine particles were adhered on the coating layer composed of the fluoroalkyl organosilane compound produced from tridecafluorooctyl trimethoxysilane. Examples 253 to 258: The same procedure as defined in Example 252 was conducted except that kinds of black iron oxide particles and black iron oxide hydroxide particles, kinds and amounts of fluoroalkylsilane compound added, treating conditions of an edge runner used in the fluoroalkylsilane compound-coating process, kinds and amounts of carbon black fine particles adhered, and treating conditions of an edge runner used in the process for adhering the carbon black fine particles, were changed variously, thereby obtaining black iron-based composite particles. As a result of the observation by an electron microscope, almost no carbon black fine particles were recognized in the black iron-based composite particles obtained in Examples 253 to 258. Therefore, it was confirmed that substantially a whole amount of the carbon black fine particles used were adhered on the coating layer composed of a fluoroalkyl organosilane compound produced from fluoroalkylsilane compounds. The essential treating conditions are shown in Table 28, and various properties of the obtained black iron-based composite particles are shown in Table 29. Examples 259 to 272 and Comparative Examples 91 to 93: 〈Production of solvent-based paint〉 The same procedure as defined in Example 2 was conducted except that kinds of black particles were changed variously, thereby obtaining solvent-based paints. The essential production conditions and various properties of coating films obtained from the solvent-based paints are shown in Table 30. Examples 273 to 286 and Comparative Examples 94 to 96: 〈Production of water-based paint〉 The same procedure as defined in Example 3 was conducted except that kinds of black particles were changed variously, thereby obtaining water-based paints. The essential production conditions and various properties of coating films obtained from the water-based paints are shown in Table 31. Examples 297 to 300 and Comparative Examples 97 to 99: 〈Production of resin composition〉 The same procedure as defined in Example 4 was conducted except that kinds of black particles were changed variously, thereby obtaining resin compositions. The essential production conditions and various properties of colored resin plates obtained from the resin compositions are shown in Table 32.

Claims: Black iron-based composite particles comprising: (i) black iron oxide particles or black iron oxide hydroxide particles having an average particle size of 0.08 to 1.0 µm; (ii) a coating layer on the surface of said particles, said coating layer comprising at least one organosilicon compound selected from: (1) organosilane compounds obtainable by drying or heat-treating alkoxysilane compounds, (2) polysiloxanes or modified polysiloxanes, and (3) fluoroalkyl organosilane compounds obtainable by drying or heat-treating fluoroalkylsilane compounds; and (iii) carbon black adhered on at least a part of said coating layer, the amount of said carbon black being 1 to 30 parts by weight based on 100 parts by weight of said particles (i). Composite particles according to claim 1, which further comprise an underlayer formed between said particle (i) and said coating layer (ii), comprising a hydroxide of aluminum, oxide of aluminum, hydroxide of silicon or oxide of silicon. Composite particles according to claim 2, wherein the amount of said hydroxide of aluminum or silicon, or oxide of aluminum or silicon is 0.01 to 50 % by weight, calculated as Al or SiO 2 , based on the weight of said black iron oxide particles or black iron oxide hydroxide particles. Composite particles according to any one of the preceding claims, wherein said modified polysiloxane is (A) a polysiloxane modified with a polyether, polyester or epoxy compound; or (B) a polysiloxane whose molecular terminal is modified with a carboxylic acid group, alcohol group or a hydroxyl group. Composite particles according to claim 4, wherein said polysiloxane (A) is of formula (III), (IV) or (V) : wherein R 3 is -(-CH 2 -) h -; R 4 is -(-CH 2 -) i -CH 3 ; R 5 is -OH, -COOH, -CH=CH 2 , -CH(CH 3 )=CH 2 or - (-CH 2 -) j -CH 3 ; R 6 is -(-CH 2 -) k -CH 3 ; g and h are each independently an integer of from 1 to 15; i, j and k are each independently an integer of from 0 to 15; e is an integer of from 1 to 50; and f is an integer of from 1 to 300; wherein R 7 , R 8 and R 9 are each -(-CH 2 -) q - and may be the same or different; R 10 is -OH, -COOH, -CH=CH 2 , -CH(CH 3 )=CH 2 or -(-CH 2 -) r -CH 3 ; R 11 is -(-CH 2 -) s -CH 3 ; n and q are each independently an integer of from 1 to 15; r and s are each independently an integer of from 0 to 15; e' is an integer of from 1 to 50; and f' is an integer of from 1 to 300; or wherein R 12 is -(-CH 2 -) v -; v is an integer of from 1 to 15; t is an integer of from 1 to 50; and u is an integer of from 1 to 300. Composite particles according to claim 4 or 5, wherein said polysiloxane (B) is of formula (VI) : wherein R 13 and R 14 are each -OH, R 16 OH or R 17 COOH and may be the same or different; R 15 is -CH 3 or -C 6 H 5 ; R 16 and R 17 are each independently -(-CH 2 -) y -; y is an integer of from 1 to 15; w is an integer of from 1 to 200; and x is an integer of from 0 to 100. Composite particles according to any one of the preceding claims, wherein said alkoxysilane compound is of formula (I) : R 1 a SiX 4-a wherein R 1 is C 6 H 5 -, (CH 3 ) 2 CHCH 2 - or n-C m H 2m+1 - (wherein m is an integer of from 1 to 18); X is CH 3 O- or C 2 H 5 O-; and a is an integer of from 0 to 3. Composite particles according to claim 7, wherein said alkoxysilane compound is methyl triethoxysilane, dimethyl diethoxysilane, tetraethoxysilane, phenyl triethoxysilane, diphenyl diethoxysilane, methyl trimethoxysilane, dimethyl dimethoxysilane, tetramethoxysilane, phenyl trimethoxysilane, diphenyl dimethoxysilane, isobutyl trimethoxysilane or decyl trimethoxysilane. Composite particles according to any one of the preceding claims wherein said polysiloxane is of formula (II): wherein R 2 is H- or CH 3 -, and d is an integer of from 15 to 450. Composite particles according to claim 9, wherein said polysiloxane has methyl hydrogen siloxane units. Composite particles according to any one of the preceding claims, wherein said fluoroalkyl organosilane compound is of general formula (VII): CF 3 (CF 2 ) z CH 2 CH 2 (R 18 ) a' SiX 4-a' wherein R 18 is CH 3 -, C 2 H 5 -, CH 3 O- or C 2 H 5 O-; X is CH 3 O- or C 2 H 5 O-; and z is an integer of from 0 to 15; and a' is an integer of from 0 to 3. Composite particles according to any one of the preceding claims which have: a blackness (L* value) of 15 to 18, and/or a particle size of 0.082 to 1.05 µm, and/or a BET specific surface area value of 1 to 200 m 2 /g, and/or a geometrical standard deviation of particle sizes of 1.01 to 1.8. Composite particles according to any one of the preceding claims wherein said particles (i) are magnetite particles, manganese-containing hematite particles or manganese-containing goethite particles. Composite particles according to any one of the preceding claims, wherein the amount of said coating organosilicon compound (ii) is 0.02 to 5.0 % by weight, calculated as Si, based on the total weight of the organosilicon compound (ii) and said particles (i). Composite particles according to any one of the preceding claims, wherein said adhered carbon black is obtainable by mixing and stirring from 1 to 30 parts by weight, per 100 parts by weight of said particles (i), of carbon black fine particles having an average particle size of 0.005 to 0.05 µm with said particles (i) having a surface coating of a said alkoxysilane compound, a said polysiloxane or modified polysiloxane and/or a said fluoroalkylsilane compound, followed by drying or heat-treating. A process for producing black iron-based composite particles as claimed in any one of the preceding claims, which process comprises: (a) mixing and stirring said particles (i) together with at least one silicon-containing compound selected from: (1) alkoxysilane compounds, (2) polysiloxanes or modified polysiloxanes, and (3) fluoroalkylsilane compounds, thereby coating the surface of said particles (i) with said compound; (b) adding carbon black fine particles having an average particle size of 0.005 to 0.05 µm in an amount of 1 to 30 parts by weight based on 100 parts by weight of said particles (i), thereby obtaining mixed particles; and (c) mixing and stirring said mixed particles, followed by (d) drying or heat-treating, thereby adhering said carbon black on the surface of a coating layer comprising the organosilicon compound. A process according to claim 16, wherein said particles (i) have been coated with a hydroxide of aluminum, oxide of aluminum, hydroxide of silicon or oxide of silicon. A paint comprising: said black iron-based composite particles as claimed in any one of claims 1 to 15 or as produced by a process according to claims 16 or 17; and a paint base material. A paint according to claim 18, wherein the amount of said composite particles is 1.0 to 100 parts by weight based on 100 parts by weight of said paint base material. A rubber or resin composition comprising: said black iron-based composite particles as claimed in any one of claims 1 to 15 or as produced by a process according to claims 16 or 17; and a base material for a rubber or resin composition. A rubber or resin composition according to claim 20, wherein the amount of said composite particles is 0.5 to 200 parts by weight based on 100 parts by weight of said base material.

Inventors: HAYASHI KAZUYUKI, MORII HIROKO, TANAKA YASUYUKI, HAYASHI, KAZUYUKI, MORII, HIROKO, TANAKA, YASUYUKI
Applicants: TODA KOGYO CORP, TODA KOGYO CORPORATION
Application year: 1998
Main classification: C09C1
IPC codes: C09C1, C09C3, C09D7, C08K9