CATALYST COMPOSITION FOR THE PRODUCTION OF OLEFIN POLYMERS

Abstract: A catalyst composition comprising the reaction product of: a) a monocycloalkadienyl catalyst precursor; b) an activity enhancing cycloalkadiene; and c) an activating cocatalyst is disclosed, which has high activity in the polymerization of olefins.

Description: CATALYST COMPOSITION FOR THE PRODUCTION OF OLEFIN POLYMERS An improved catalyst composition and its use in the production of olefin polymers are provided. The catalyst composition comprises the reaction product of a) a monocycloalkadienyl catalyst precursor, b) an activity enhancing cycloalkadiene; and c) an activating cocatalyst. The catalyst composition demonstrates enhanced activity in the polymerization of olefins. BACKGROUND OF THE INVENTION A variety of single site catalyst compositions have been developed to prepare olefin polymers. Single site catalysts have been shown to be highly useful in the preparation of polyolefins, producing relatively homogeneous copolymers at good polymerization rates, allowing one to tailor closely the final properties of the polymer produced. In contrast to traditional Ziegler- Natta catalyst compositions, single site catalyst compositions comprise catalytic compounds in which each catalyst composition molecule contains one or only a few polymerization sites. Metallocenes are the most well known type of single site catalyst precursor, and are organometallic coordination complexes containing one or more pi-bonded moieties (i.e., cycloalkadienyl groups) in association with a metal atom from Groups IIIB to VIII or the Lanthanide series of the Periodic Table of Elements. Monocycloalkadienyl catalyst precursors are useful single site catalysts precursors. However, they sometimes demonstrate low activities in polymerizing olefins. To this end, applicants have discovered that when monocycloalkadienyl catalyst precursors are combined with an activity enhancing cycloalkadiene and an activating cocatalyst, a catalyst composition results having increased activity for the polymerization of olefins relative to that of a catalyst composition containing only the monocycloalkadienyl catalyst precursor and activating cocatalyst. In addition, in certain instances, the properties of the olefin polymer produced, such as its short chain branching frequency, are also improved over that of an olefin polymer produced by a catalyst composition containing only the monocycloalkadienyl catalyst precursor and activating cocatalyst. U.S. Patent Nos. 5,387,567and 5,451,555, and European Patent Application Publication Nos. 0 546 690 Al, 0 587 440 Al, and 0 694 563 Al, all assigned to Nippon Oil Company, Ltd., relate to catalyst compositions comprising transition metal compounds of the formula Me(OR)pRqX .p.q and MeR n X4-n wherein Me is a transition metal, each R is a hydrocarbon group of 1-24 carbons, X is a halogen, and p, q, and n are each 0 to 4, and organocyclic compounds having two or more conjugated double bonds. Such catalyst compositions may also include Group I-III metal compounds as well. However, the Nippon Oil publications do not teach or suggest catalyst compositions that are the reaction product of a) a monocycloalkadienyl catalyst precursor, b) an activity enhancing cycloalkadiene; and c) an activating cocatalyst, or the increased activity of such catalyst compositions. SUMMARY OF THE INVENTION The invention provides a catalyst composition comprising the reaction product of: a) monocycloalkadienyl catalyst precursor having the formula: LMX X (I) wherein: M is a metal from groups IIIB to VIII or a rare earth metal of the Periodic Table; L is a cycloalkadienyl ligand; each X is independently hydrogen, an aryl, alkyl, alkenyl, alkylaryl, or arylalkyl radical having 1-20 carbon atoms, a hydrocarboxy radical having 1-20 carbon atoms, a halide, a nitrogen containing radical having 1-20 carbon atoms, or Q2YZ, wherein each Q is independently selected from the group consisting of -O-, -NR-, -CR2- and -S-; Y is either C or S; and Z is selected from the group consisting of -OR, -NR2, -CR3, -SR, -SiR3, -PR2, -H, and substituted or unsubstituted aryl groups, with the proviso that when Q is -NR- then Z is selected from the group consisting of -OR, -NR2, -SR, -SiR3, -PR2 and -H; and x is 2, 3, or 4 depending upon the valence state of M; b) an activity enhancing cycloalkadiene; and c) an activating cocatalyst. The invention also provides a process for the polymerization of an olefin, which comprises contacting at least one olefin monomer under polymerization conditions with the above catalyst composition. DETAILED DESCRIPTION OF THE INVENTION Olefin polymers that may be produced according to the invention include, but are not limited to, ethylene homopolymers, homopolymers of linear or branched higher alpha-olefins containing 3 to about 20 carbon atoms, and interpolymers of ethylene and such higher alpha-olefins, with densities ranging from about 0.86 to about 0.96. Suitable higher alpha-olefins include, for example, propylene, 1- butene, 1-pentene, 1-hexene, 4-methyl-l-pentene, 1-octene, and 3,5,5- trimethyl-1-hexene. Olefin polymers according to the invention may also be based on or contain conjugated or non-conjugated dienes, such as linear, branched, or cyclic hydrocarbon dienes having from about 4 to about 20, preferably 4 to 12, carbon atoms. Preferred dienes include 1,4-pentadiene, 1,5-hexadiene, 5-vinyl-2-norbornene, 1,7-octadiene, vinyl cyclohexene, dicyclopentadiene, butadiene, isobutylene, isoprene, ethylidene norbornene, norbornadiene and the like. Aromatic compounds having vinyl unsaturation such as styrene and substituted styrenes, and polar vinyl monomers such as acrylonitrile, maleic acid esters, vinyl acetate, acrylate esters, methacrylate esters, vinyl trialkyl silanes and the like may be polymerized according to the invention as well. Specific olefin polymers that may be made according to the invention include, for example, polyethylene, polypropylene, ethylene/propylene rubbers (EPR's), ethylene/propylene/diene terpolymers (EPDM's), polybutadiene, polyisoprene and the like. The catalyst composition comprises the reaction product of: a) a monocycloalkadienyl catalyst precursor, b) an activity enhancing cycloalkadiene; and c) an activating cocatalyst. The monocycloalkadienyl catalyst precursor has the formula: LMX X (I) wherein: M is a metal from groups IIIB to VIII or a rare earth metal of the Periodic Table; L is cycloalkadienyl ligand, such as cyclopentadienyl, indenyl, or fluorenyl, optionally substituted with one or more hydrocarbyl groups containing 1 to 20 carbon atoms; each X is independently hydrogen, an aryl, alkyl, alkenyl, alkylaryl, or arylalkyl radical having 1-20 carbon atoms, a hydrocarboxy radical having 1-20 carbon atoms, a halide, a nitrogen containing radical having 1-20 carbon atoms, or Q 2 YZ, wherein each Q is independently selected from the group consisting of -O-, -NR-, -CR2- and -S-, preferably oxygen; Y is either C or S, preferably carbon; and Z is selected from the group consisting of -OR, -NR2, -CR3, -SR, -SiR3-, -PR2, -H, and substituted or unsubstituted aryl groups, with the proviso that when Q is -NR- then Z is selected from the group consisting of -OR, -NR2, -SR, -SiR3, -PR2 and -H, preferably Z is selected from the group consisting of -OR, -CR3 and -NR2; and x is 2, 3, or 4 depending upon the valence state of M. Illustrative but non-limiting examples of catalyst precursors represented by formula I are cyclopentadienyl titanium trichloride, methylcyclopentadienyl titanium trichloride, methylcyclopentadienyl titanium tribromide, pentamethylcyclopentadienyl titanium trichloride, indenyl titanium trichloride, cyclopentadienyl titanium trimethyl, cyclopentadienyl titanium triphenyl, cyclopentadienyl titanium tris(methoxide), pentamethylcyclopentadienyl titanium tris(methoxide), cyclopentadienyl titanium tris(dimethylamide), cyclopentadienyl titanium tris(diethylamide), cyclopentadienyl zirconium trichloride , methylcylopentadienyl zirconium trichloride, pentamethylcyclopentadienyl zirconium trichloride, indenyl zirconium trichloride, cyclopentadienyl zirconium tris(methoxide), methylcyclopentadienyl zirconium tris(methoxide), pentamethylcyclopentadienyl zirconium tris(methoxide), indenyl zirconium tris(methoxide), cyclopentadienyl zirconium trimethyl, cyclopentadienyl zirconium trineopentyl, cyclopentadienyl zirconium trimethyl, cyclopentadienyl zirconium tris (d i m ethy lamide) , methylcyclopentadienyl zirconium tris (diethylamide), indenyl zirconium tris(die thy lamide); cyclopentadienyl hafnium trichloride, methylcyclopentadienyl hafnium trichloride, pentamethylcyclopentadienyl hafnium trichloride, cyclopentadienyl hafnium triphenyl, cyclopentadienyl hafnium tri(neopentyl), cyclopentadienyl hafnium trimethyl, cyclopentadienyl hafnium tris(methoxide), cyclopentadienyl hafnium tris(diethylamide), and pentamethylcyclopentadienyl hafnium tris(diethy lamide). A preferred type of monocycloalkadienyl catalyst precursor for use in the invention is a complex of a transition metal, a substituted or unsubstituted pi-bonded hgand, and one or more heteroallyl moieties, such as those described in U.S. Patent No. 5,527,752. Preferably, such complexes have one of the following formulas: L wherein: M is a transition metal, preferably Zr or Hf; L is a substituted or unsubstituted, pi-bonded ligand coordinated to M, preferably a cycloalkadienyl hgand; each Q is independently selected from the group consisting of - O-, -NR-, -CR2- and -S-, preferably oxygen; Y is either C or S, preferably carbon; Z is selected from the group consisting of -OR, -NR2, -CR3, -SR, - SiR3, -PR2, -H, and substituted or unsubstituted aryl groups, with the proviso that when Q is -NR- then Z is selected from the group consisting of -OR, -NR2, -SR, -SiR3 ) -PR2 and -H, preferably Z is selected from the group consisting of -OR, -CR3 and -NR2; n is 1 or 2; A is a univalent anionic group when n is 2 or A is a divalent anionic group when n is 1, preferably A is a carbamate, carboxylate, or other heteroallyl moiety described by the Q, Y and Z combination; and each R is independently a group containing carbon, silicon, nitrogen, oxygen, and/or phosphorus where one or more R groups may be attached to the L substituent, preferably R is a hydrocarbon group containing from 1 to 20 carbon atoms, most preferably an alkyl, cycloalkyl, or an aryl group and one or more may be attached to the L substituent; or wherein: M is a transition metal, preferably Zr or Hf; L is a substituted or unsubstituted, pi-bonded hgand coordinated to M, preferably a cycloalkadienyl ligand; each Q is independently selected from the group consisting of -O-, -NR-, -CR2- and -S-, preferably oxygen; Y is either C or S, preferably carbon; Z is selected from the group consisting of -OR, -NR2, -CR3, -SR, - SiR3 ; -PR2 > -H, and substituted or unsubstituted aryl groups, with the proviso that when Q is -NR- then Z is selected from the group consisting of -OR, -NR2, -SR, -SiR3, -PR2 and -H, preferably Z is selected from the group consisting of -OR, -CR3 and -NR2; n is 1 or 2; A is a univalent anionic group when n is 2 or A is a divalent anionic group when n is 1, preferably A is a carbamate, carboxylate, or other heteroallyl moiety described by the Q, Y and Z combination; each R is independently a group containing carbon, silicon, nitrogen, oxygen, and/or phosphorus where one or more R groups may be attached to the L substituent, preferably R is a hydrocarbon group containing from 1 to 20 carbon atoms, most preferably an alkyl, cycloalkyl, or an aryl group and one or more may be attached to the L substituent; T is a bridging group selected from the group consisting of alkylene and arylene groups containing from 1 to 10 carbon atoms optionally substituted with carbon or heteroatoms, germanium, silicone and alkyl phosphine; and m is 2 to 7, preferably 2 to 6, most preferably 2 or 3. In formulas I, II, and II, the substituent formed by Q, Y and Z is a unicharged polydentate hgand exerting electronic effects due to its high polarizability, similar to the cyclopentadienyl group. In the most preferred embodiments of this invention, the disubstituted carbamates, N- C ( ;.- M O - * and the carboxylates -cd o ? :- M o- are employed. Examples of complexes according to formulas II and III include indenyl zirconium tris(diethylcarbamate), indenyl zirconium tris(trimethylacetate), indenyl zirconium tris(p-toluate), indenyl zirconium tris(benzoate), (l-methylindenyl)zirconium tris(pivalate), (2- methyhndenyl) zirconium tris(diethylcarbamate), (methylcyclopentadienyl) zirconium tris(trimethylacetate), cyclopentadienyl tris(pivalate), and (pentamethylcyclopentadienyl) zirconium tris(benzoate). Preferred examples are indenyl zirconium tris(diethylcarbamate), indenyl zirconium tris(trimethylacetate), and (methylcyclopentadienyl) zirconium tris(trimethylacetate). The catalyst precursor may be made by any means, and the invention is not limited thereby. For example, a method of manufacturing a preferred catalyst precursor, indenyl zirconium tris(diethylcarbamate), is first to react a source of cycloalkadienyl Hgand with a metal compound of the formula M(NR2) , in which M and R are defined above, to introduce the cycloalkadienyl Hgand onto the metal compound. The resulting product is then dissolved in an inert solvent, such as toluene, and the heterocumulene CO 2 is contacted with the dissolved product to insert into one or more M-NR 2 bonds to form a carbamate. The activity enhancing cycloalkadiene is an organocyclic compound having two or more conjugated double bonds, examples of which include cyclic hydrocarbon compounds having two or more, preferably 2-4, more preferably 2-3, conjugated double bonds and 4-24, preferably 4-12, carbons, optionally substituted with a substituting group such as alkyl or aralkyl of 1-12 carbon atoms. Examples of activity enhancing cycloalkadienes include unsubstituted and substituted cyclopentadienes, indenes, fluorenes, and fulvenes, such as cyclopentadiene, methylcyclopentadiene, ethylcyclopentadiene, t-butylcyclopentadiene, hexylcyclopentadiene, octylcyclopentadiene, 1,2-dimethylcyclopentadiene, 1,3- dimethylcyclopentadiene, 1,2,4-trimethylcyclopentadiene, 1,2,3,4-tetra- methylcyclopentadiene, pentamethylcyclopentadiene, indene, 4- methyl-1-indene, 4,7-dimethylindene, 4,5,6,7-tetrahydroindene, fluorene, methylfluorene, cycloheptatriene, methylcycloheptatriene, cyclooctatraene, methylcyclooctatraene, fulvene and dime thy lfulvene. These compounds may be bonded through an alkylene group of 2-8, preferably 2-3, carbon atoms, such as for example bis-indenylethane, bis(4,5,6,7-tetrahydro-l-indenyl)ethane, l,3-propanedinyl-bis(4, 5,6,7- tetrahydro)indene, propylene-bis(l-indene), isopropyl(l-indenyl) cyclopentadiene, diphenylmethylene(9-fluorenyl), cyclopentadiene and isopropylcyclopentadienyl-1-fluorene. Preferably, the activity enhancing cycloalkadiene is selected from the group consisting of cyclopentadiene, methylcyclopentadiene, indene, and methyl-n- propylcyclopentadiene . The amount of activity enhancing cycloalkadiene used is about 0.01 to about 10 moles per mole of catalyst precursor. Preferably, about 0.1 to about 2.0 moles of cycloalkadiene per mole of catalyst precursor are used. More preferably, about 0.2 to about 1.0 moles of cycloalkadiene per mole of catalyst precursor are used. In one embodiment of the invention, the amount of cycloalkadiene used is about 0.1 to about 2.0 moles per mole of catalyst precursor, preferably about 0.1 to about 1.1 moles per mole of catalyst precursor. Under these conditions, a 0.920 density ethylene polymer may be made having one or more of the following properties: a high number average molecular weight, i.e., in the range of about 5000 to about 200,000, preferably about 20,000 to about 100,000, a narrow molecular weight distribution (PDI), i.e., about 3 to 5, or a high short chain branch frequency, i.e., at least about 10 short chain branches per 1000 main chain carbons, preferably at least about 15 short chain branches per main chain carbons, as measured by carbon- 13 MNR. The activating cocatalyst is capable of activating the catalyst precursor. Preferably, the activating cocatalyst is one of the following: (a) branched or cyclic ohgomeric poly(hydrocarbylaluminum oxide)s which contain repeating units of the general formula -(Al(R*)O)-, where R* is hydrogen, an alkyl radical containing from 1 to about 12 carbon atoms, or an aryl radical such as a substituted or unsubstituted phenyl or naphthyl group; (b) ionic salts of the general formula [A + ][BR 4 _ ] ) where A + is a cationic Lewis or Bronsted acid capable of abstracting an alkyl, halogen, or hydrogen from the metallocene catalysts, B is boron, and R is a substituted aromatic hydrocarbon, preferably a perfluorophenyl radical; (c) boron alkyls of the general formula BR 3, where R is as defined above; or mixtures thereof. Preferably, the activating cocatalyst is a branched or cyclic ohgomeric poly(hydrocarbylaluminum oxide) or a boron alkyl. More preferably, the activating cocatalyst is an aluminoxane such as methylaluminoxane (MAO) or modified methylaluminoxane (MMAO), or a boron alkyl. Aluminoxane s are well known in the art and comprise oligomeric linear alkyl aluminoxanes represented by the formula: and oligomeric cyclic alkyl aluminoxanes of the formula: wherein s is 1-40, preferably 10-20; p is 3-40, preferably 3-20; and R*** is an alkyl group containing 1 to 12 carbon atoms, preferably methyl. Aluminoxanes may be prepared in a variety of ways. Generally, a mixture of linear and cychc aluminoxanes is obtained in the preparation of aluminoxanes from, for example, trimethylaluminum and water. For example, an aluminum alkyl may be treated with water in the form of a moist solvent. Alternatively, an aluminum alkyl, such as trimethylaluminum, may be contacted with a hydrated salt, such as hydrated ferrous sulfate. The latter method comprises treating a dilute solution of trimethylaluminum in, for example, toluene with a suspension of ferrous sulfate heptahydrate. It is also possible to form methylaluminoxanes by the reaction of a tetraalkyl- dialuminoxane containing C2 or higher alkyl groups with an amount of trimethylaluminum that is less than a stoichiometric excess. The synthesis of methylaluminoxanes may also be achieved by the reaction of a trialkyl aluminum compound or a tetraalkyldialuminoxane containing C2 or higher alkyl groups with water to form a polyalkyl aluminoxane, which is then reacted with trimethylaluminum. Further modified methylaluminoxanes, which contain both methyl groups and higher alkyl groups, i.e., isobutyl groups, may be synthesized by the reaction of a polyalkyl aluminoxane containing C2 or higher alkyl groups with trimethylaluminum and then with water as disclosed in, for example, U.S. Patent No. 5,041,584. When the activating cocatalyst is a branched or cyclic ohgomeric poly(hydrocarbylaluminum oxide), the mole ratio of aluminum atoms contained in the poly(hydrocarbylaluminum oxide) to total metal atoms contained in the catalyst precursor is generally in the range of from about 2:1 to about 100,000:1, preferably in the range of from about 10:1 to about 10,000:1, and most preferably in the range of from about 50:1 to about 2,000:1. When the activating cocatalyst is an ionic salt of the formula [A + ] [BR Δ ~ ] or a boron alkyl of the formula BR 3, the mole ratio of boron atoms contained in the ionic salt or the boron alkyl to total metal atoms contained in the catalyst precursor is generally in the range of from about 0.5:1 to about 10:1, preferably in the range of from about 1:1 to about 5:1. The catalyst composition may be impregnated onto a sohd, inert support, in Hquid form such as a solution or dispersion, spray dried, in the form of a prepolymer, or formed in-situ during polymerization. Particularly preferred among these is a catalyst composition that is spray dried as described in European Patent Apphcation No. 0 668 295 Al or in Hquid form as described in U.S. Patent No. 5,317,036. In the case of a supported catalyst composition, the catalyst composition may be impregnated in or deposited on the surface of an inert substrate such as silica, carbon black, polyethylene, polycarbonate porous crosshnked polystyrene, porous crossHnked polypropylene, alumina, thoria, zirconia, or magnesium hahde (e.g., magnesium dichloride), such that the catalyst composition is between 0.1 and 90 percent by weight of the total weight of the catalyst composition and the support. The catalyst composition may be used for the polymerization of olefins by any suspension, solution, slurry, or gas phase process, using known equipment and reaction conditions, and is not Hmited to any specific type of reaction system. Generally, olefin polymerization temperatures range from about 0°C to about 200°C at atmospheric, subatmospheric, or superatmospheric pressures. Slurry or solution polymerization processes may utihze subatmospheric or superatmospheric pressures and temperatures in the range of about 40°C to about 110°C. A useful Hquid phase polymerization reaction system is described in U.S. Patent 3,324,095. Liquid phase reaction systems generaUy comprise a reactor vessel to which olefin monomer and catalyst composition are added, and which contains a Hquid reaction medium for dissolving or suspending the polyolefin. The Hquid reaction medium may consist of the bulk Hquid monomer or an inert Hquid hydrocarbon that is nonreactive under the polymerization conditions employed. Although such an inert Hquid hydrocarbon need not function as a solvent for the catalyst composition or the polymer obtained by the process, it usuaUy serves as solvent for the monomers employed in the polymerization. Among the inert Hquid hydrocarbons suitable for this purpose are isopentane, hexane, cyclohexane, heptane, benzene, toluene, and the like. Reactive contact between the olefin monomer and the catalyst composition should be maintained by constant stirring or agitation. The reaction medium containing the olefin polymer product and unreacted olefin monomer is withdrawn from the reactor continuously. The olefin polymer product is separated, and the unreacted olefin monomer and Hquid reaction medium are recycled into the reactor. Preferably, gas phase polymerization is employed, with superatmospheric pressures in the range of 1 to 1000 psi, preferably 50 to 400 psi, most preferably 100 to 300 psi, and temperatures in the range of 30 to 130°C, preferably 65 to 110°C. Stirred or fluidized bed gas phase reaction systems are particularly useful. GeneraUy, a conventional gas phase, fluidized bed process is conducted by passing a stream containing one or more olefin monomers continuously through a fluidized bed reactor under reaction conditions and in the presence of catalyst composition at a velocity sufficient to maintain a bed of solid particles in a suspended condition. A stream containing unreacted monomer is withdrawn from the reactor continuously, compressed, cooled, optionaUy fully or partially condensed as disclosed in U.S. Patent Nos. 4,528,790 and 5,462,999, and recycled to the reactor. Product is withdrawn from the reactor and make-up monomer is added to the recycle stream. As desired for temperature control of the system, any gas inert to the catalyst composition and reactants may also be present in the gas stream. In addition, a fiuidization aid such as carbon black, silica, clay, or talc may be used, as disclosed in U.S. Patent No. 4,994,534. Polymerization may be carried out in a single reactor or in two or more reactors in series, and is conducted substantially in the absence of catalyst poisons. Organometalhc compounds may be employed as scavenging agents for poisons to increase the catalyst activity. Examples of scavenging agents are metal alkyls, preferably aluminum alkyls, most preferably triisobutylaluminum. Conventional adjuvants may be included in the process, provided they do not interfere with the operation of the catalyst composition in forming the desired polyolefin. Hydrogen or a metal or non-metal hydride, e.g., a silyl hydride, may be used as a chain transfer agent in the process. Hydrogen may be used in amounts up to about 10 moles of hydrogen per mole of total monomer feed. The foUowing examples further illustrate the invention. EXAMPLES Glossary Activity is measured in g polyethylene/mmol metal hr lOO psi ethylene. MAO is a solution of methylaluminoxane in toluene, approximately 2.0 molar in aluminum, commerciaUy available from Akzo Chemicals, Inc. MMAO is a solution of modified methylaluminoxane in hexane, approximately 2.25 molar in aluminum, commerciaUy avaUable from Akzo Chemicals, Inc. (type M). Density in g/cc is determined in accordance with ASTM 1505, based on ASTM D-1928, procedure C, plaque preparation. A plaque is made and conditioned for one hour at 100° C to approach equiHbrium crystalHnity, measurement for density is then made in a density gradient column. TIBA is trnsobutylaluminum. MI is melt index, reported as grams per 10 minutes, determined in accordance with ASTM D-1238, condition E, at 190° C. FI is flow index, reported as grams per 10 minutes, is determined in accordance with ASTM D-1238, condition F, and is measured at ten times the weight used in the melt index text. MFR is melt flow ratio, which is the ratio of flow index to melt index. It is related to the molecular weight distribution of the polymer. BBF BBF is butyl branch frequency as determined using carbon-13 NMR. An 8% weight/volume concentration was prepared by dissolving an ethylene copolymer in ortho dichlorobenzene (ODCB) in an NMR tube. A closed capillary tube of deuterium oxide was inserted into the NMR tube as a field frequency lock. Data was coUected on the Bruker AC 300 at 115°C using NOE enhanced conditions with a 30° PW and a 5 second repetition time. The number of carbon scans usuaUy varied from 1,000 to 10,000 with the more highly branched samples requiring shorter acquisitions. The area of the peaks was measured along with the area of the total aliphatic region. The areas of carbons contributed by the comonomer were averaged and ratioed to the area of the backbone to give the mole fraction. This number was then converted into branch frequency. Determination of Zr in Polyethylene Polyethylene samples were weighed into platinum crucibles, ignited, then placed in a muffle furnace (580° C) until aU the carbon had burned off. After cooHng, hydrochloric acid was added to the residue and it was heated gently to aid dissolution. The crucibles were cooled, and hydrofluoric acid was added to insure total dissolution of the siHcane. The samples were then quantitatively transferred and diluted to 15 ml with deionized water and analyzed using an Inductively-Coupled Plasma (Atom Scan 25, Thermo JarreU Ash). Catalvst Precursor Preparations: η 5 -IndZr(02CNEt2)3 and η 5 - MelndZrlYOzCCYCH s First, η -IndZr(NEt2)3 was prepared by reacting indene (in excess) with Zr(NEt2)4 either neat or in toluene solution at 100-115° for 1-4 hours. The resulting Et2NH, along with the toluene, was pumped off and the excess indene removed under high vacuum (110 0.05 mmHg/0.5 hr). This yielded an approx. 95 mole % pure η 5 - IndZr(NEt2)3 residue product. AU analyses were by ^H-NMR using dβ-toluene as solvent and NMR lock. Next, an approx. 2 wt. % solution of the η -IndZr(NEt2)3 residue product in toluene (dried over CaH2) was placed in a smaU Hoke cyHnder (25-100 ml). The solution in the Hoke cyhnder (under N2) was cooled to approx. 0° C in an ice bath. Carbon dioxide (HPLC grade) was added thereto, first at low pressure (1-5 psi) with good agitation, and then at increased pressure (60 psi) for 0.5 hr. Thus, a dUute toluene solution of η 5 -indenyl zirconium tris(diethylcarbamate) was obtained, which contained 3-7 mole % of free indene. This was stored at r.t. in a <1 ppm O2 H2O drybox in a Teflon coated, crimped topped bottle. η 5 -Methycyclopentadienyl zirconium tris(diethylamide) was prepared by a similar procedure. This, in dUute toluene solution, at - 50 to -75°, was reacted with a toluene solution of pivaHc acid (trimethyl acetic acid) resulting in the η 5 -methylcyclopentadienyl zirconium tris(trimethylacetate). This was purified by recrystalHzation from ahphatic hydrocarbons at low temperatures. AU reactions and manipulations were carried out in a <1 ppm O2/H2O drybox or on a vacuum Hne. Exceptional care was taken to exclude H2O, O2 and polar compounds. Catalyst Precursor Preparation: CpZrCla CpZrCl3 is commerciaUy avaUable from Strem Chemicals, and may also be synthesized according to Reid et al., J. Organomet. Chem., Vol. 2, p. 329 (1964). EXAMPLES 1-24 A series of ethylene/1-hexene copolymers were produced in a 1.8 Hter, stirred (275 rpm), slurry phase reactor using η 5 -indenyl zirconium tris(diethylcarbamate)/MMAO catalyst compositions. In Example 1, the catalyst composition comprised only η 5 -indenyl zirconium tris(diethylcarbamate) and MMAO. In Examples 2-24, the catalyst compositions comprised η 5 -indenyl zirconium tris(diethylcarbamate), MMAO and an activity enhancing cycloalkadiene as shown in Table 1. Examples 1-24 were carried out as follows. The reactor was baked out (110° C/N2) for approx. 1 hr. After cooHng, 1,000 ml of deoxygenated hexanes were added along with 100 ml of freshly distiUed (over CaH2) 1-hexene and 1.14 ml TIBA (in heptanes, 0.87 mole, equal to 1 mmole). The reactor was closed, brought to temperature (85°C), 100 ml H2 was added, and the reactor was pressured to 200 psi total system pressure with ethylene. At pressure equiHbrium, one micromole of catalyst composition solution containing η 5 -indenyl zirconium tris(diethylcarbamate), MMAO, and optionaUy cycloalkadiene was injected through a high pressure septum/pressure syringe. The cycloalkadiene was added to the catalyst composition such that each catalyst precursor molecule was paired with one cycloalkadiene ring. Thus, when the cycloalkadiene had two rings, the mole ratio of cycloalkadiene to catalyst precursor was 0.5. This initiated the reaction. Very active catalyst compositions typicaUy resulted in temperature increases to 90-95° C, soon brought under control to level out at 85° C ± 2° C. The ethylene flow rate, system pressure, and reactor temperature (internal and external) was monitored continuously. The reactions were run for 30 min., unless the catalyst composition proved to be too productive. In this case, the reactions were run for only 10-15 min. (no more than approx. 900 counts approx. 90 g polymer). Polymerization was terminated by injection of 1 ml anhydrous isopropanol (at temperature and pressure), and simultaneous coohng/venting. Thus, the polymerization reaction was initiated and terminated under the stated temperature and pressure conditions. After discharging the reactor the polymer/hexane slurry was mixed with 0.35 g IRGANOX in 1 ml acetone (stabilizer). The entire polymer slurry was evaporated to dryness overnight under a well ventilated hood. The dried polymer was weighed and analyzed for Zr contents. The results of Examples 1-24 are shown in Table 1. EXAMPLES 25-29 A series of ethylene/1-hexene copolymers were produced in the same manner as Examples 1-24 using an η 5 -indenyl zirconium tris(diethylcarbamate)/MMAO catalyst composition containing varying amounts of cyclopentadiene. The results are shown in Table II. EXAMPLES 30-37 A series of ethylene/1-hexene copolymers were produced in the same manner as Examples 1-24 using η 5 -methylcyclopentadienyl zirconium tris(trimethylacetate)/MMAO catalyst compositions instead. In Example 30, the catalyst composition comprised only η 5 - methylcyclopentadienyl zirconium tris(trimethylacetate) and MMAO. In Examples 31-37, the catalyst compositions comprised η 5 - methylcyclopentadienyl zirconium tris(trimethylacetate), MMAO, and an activity enhancing cycloalkadiene. The results are shown in Table III. EXAMPLES 38 AND 39 Two ethylene/1-hexene copolymers were produced in a mechanicaUy stirred, pUot scale, gas phase reactor. In Example 38, the catalyst composition comprised only η 5 -indenyl zirconium tris(diethylcarbamate) and MMAO. In Example 39, the catalyst composition comprised η 5 -indenyl zirconium tris(diethylcarbamate), MMAO, and cyclopentadiene. Examples 38 and 39 were carried out as foUows. Before both batch runs, a pre-bed was charged to the reactor, which was then pressure-purged with nitrogen three times to 100 psig. Jacket temperature was adjusted to hold the material at approximately 80° C overnight whUe under a 3-4 lb./hr nitrogen flow purge at 100 psig reactor pressure. Prior to both runs, the reactor was pressure purged once to 300 psi and then 50 ml of cocatalyst solution were then charged to further passivate the reactor. The reactor was then pressure purged four more times to 100 psig. Raw materials were charged to estabHsh the initial gas phase concentrations of ethylene, hexene, and nitrogen. Gas-phase concentrations are normaUy held near these initial values throughout the batch. Catalyst composition was fed to the reactor continuously during the polymerization using isopentane as a carrier and nitrogen as a dispersant. Catalyst feed rate was adjusted as required to maintain polymerization rates of 5-7 lbs/hr. Monomers and hydrogen were fed continuously as required to maintain gas phase composition throughout the batch. The 1- hexene/ethylene mole ratio was maintained in the range of 0.034 to 0.036. A small vent stream was used to prevent accumulation of the nitrogen added with the catalyst. The batch was terminated when the bed weight approached 25-30 lbs. by shutting off the feeds and rapidly venting the reactor to atmospheric pressure. The reactor was then pressure purged five times to 100 psi with dry nitrogen. The resin was then discharged into a product box and exposed to the atmosphere. Once in the box, a two-nozzle purging manifold was inserted deep into the resin in order to purge it out with water-saturated nitrogen overnight at ambient temperature. The results are shown in Table IV. EXAMPLES 40-48 A series of ethylene/1-hexene copolymers were produced in a 1.0 Hter, stirred (190 rpm), slurry phase reactor using cyclopentadienyl zirconium trichloride MAO catalyst compositions. In Example 48, the catalyst composition comprised only cyclopentadienyl zirconium trichloride and MAO. In Examples 40-47, the catalyst compositions comprised cyclopentadienyl zirconium trichloride, MAO and an activity enhancing cycloalkadiene as shown in Table V. Examples 40-48 were carried out as foUows. The reactor was baked out (110° C/N2) for approx. 1 hr. After cooHng, 500 ml of deoxygenated hexanes were added along with 0 to 40 ml of freshly distilled (over CaH2) 1-hexene and 0.5 to 1.0 ml TIBA (in heptanes, 0.87 mmole). The reactor was closed, brought to temperature (85°C), and the reactor was pressured to 150 psi total system pressure with ethylene. At pressure equiHbrium, a suitable amount of catalyst composition solution (formed by combining cyclopentadienyl zirconium trichloride, MAO cocatalyst in toluene solution, and an activity enhancing cycloalkadienyl, aged for a measured period of time) was introduced into the reactor in the amount shown in Table V. The reactions were run for 30 minutes, except in the case of Example 40, which was run for 15 minutes. Polymerization was terminated by injection of 1 ml anhydrous isopropanol (at temperature and pressure), and simultaneous cooHng/venting. After discharging the reactor the polymer/hexane slurry was evaporated to dryness overnight under a weU ventUated hood. The results of Examples 40-48 are shown in Table V. EXAMPLES 49-54 A series of 0.920 density ethylene/1-hexene copolymers were produced in pilot scale, fluidized bed, gas phase reactor. In Examples 49 and 50, the catalyst composition comprised only η 5 - methylcyclopentadienyl zirconium tris(trimethylacetate) and MMAO. In Examples 51-54, the catalyst compositions comprised η 5 - methylcyclopentadienyl zirconium tris(trimethylacetate) and methyl n- propyl cyclopentadiene in a 1:1 mole ratio and MMAO. Catalyst composition was fed to the reactor continuously during the polymerization using an isopentane/1-hexene mix as a carrier and nitrogen as a dispersant. Monomers and hydrogen were fed continuously as required to maintain gas phase composition. The 1- hexene/ethylene mole ratio was maintained in the range of 0.027 to 0.032. In Example 53, polymerization was conducted in condensing mode, with 6 weight percent condensed isopentane in the polymerization zone. In Example 54, polymerization was conducted in condensing mode, with 7 weight percent condensed isopentane in the polymerization zone. The results are shown in Table VI. Table I Example Cycloalkadiene Activity MI FI MFR BBF None 22,700 13.9 5.8 Cu 79,900 6.4 8.4 C 98,800 8.7 15.2 82,600 6.52 11.7 60,000 3.35 97.9 29.2 11.7 Table I (continued) Example Cycloalkadiene Activity MI FI MFR BBF Φ 82,700 1.6 32.7 24.2 7.4 Table I (continued) Example Cycloalkadiene Activity MI FI MFR BBF 45,400 0.81 39.8 32.2 6.9 32,500 0.89 32.4 28.8 8.2 Table I (continued) Example Cycloalkadiene Activity MI FI MFR BBF 16 Table I (continued) Example C y cloalkadiene Activity MI FJ MFR BBF 19 60,800 0.77 30.5 23.5 7.9 20 C "- H* * 33 91,200 1.17 25.6 22.0 9.2 1 Ωt Si(CH 3 ) 3 65,900 6.1 10.8 Table I (continued) Example Cycloalkadiene Activity MI FI MFR BBF 22 60,700 0.51 50.6 25.8 4.2 3 50,800 0.97 30.3 29.4 4.9 Table II Example CsHe/ Fja Activity BBF Catalyst Precursor Mole Ratio 25 0 0.93 6,960 8.3 26 0.1 0.84 15,700 7.8 27 0.3 0.87 19,800 8.4 28 0.5 0.84 24,500 8.5 29 1.0 0.86 37,800 9.7 a MI <0.2. Table III Cycloalkadiene/ Catalyst Precursor Mole Example Cycloalkadiene Ratio Activity FI BBF 30 None 21,200 0.51 7.0 Table III Cycloalkadiene/ Catalyst Precursor Mole Example Cycloalkadiene Ratio Activity FI BBF (Mixture of 33 3 isomers) 1:1 47,900 0.92 8.8 (Isomer 5 mixture) 1:1 43,200 1.28 9.6 Table III Cycloalkadiene/ Catalyst Precursor Mole Example Cycloalkadiene Ratio Activity FI BBF Table IV Example 38 39 Cycloalkadiene/Catalyst Precursor Mole Ratio 0 2.5 MI 20.7 4.07 FI 570 96.1 MFR 27.5 23.6 Zr (ppm) 4.9 2.1 BBF 19.1 17.9 Table V Example CycloalkaCycloalka- Activity MI FJ MFR BBF diene diene/Zr Mole Ratio 40 0^ 3.3 97000 0.60 13.1 22.0 - 41 3.3 49500 0.44 10.3 23.0 _ 42 OS 1.6 16000 0.27 5.36 19.7 - 44 3.6 53900 1.72 50.1 29.0 17.4 45 €0 1.0 18300 0.46 14.4 31.0 - 46 ft 1.0 50200 " 48 None . 4200 _ _ _ _ Tabϊe VI Example > CSΪ/CJF Al/Zr* H2, ppm MI MFR Density Activity 49 0.03 450 250 0.73 25 0.9211 4500 50 0.032 350 b 270 0.80 28 0.9190 3600 51 0.028 600 210 0.9 17 0.9170 56,000 52 0.027 650 245 1.2 17 0.9195 62,900 53 0.027 600= 210 1.2 18 0.9194 30,000 54 0.029 600 210 1.0 18 0.9180 43,400 a Nominal b 3.8 ppm Zr, Al/Zr - 381 c 0.97 ppm Zr; Al/Zr - 260

Claims: We claim: 1. A catalyst composition comprising the reaction product of: a) monocycloalkadienyl catalyst precursor having the formula: LMX, (I) wherein: M is a metal from groups IIIB to VIII or a rare earth metal of the Periodic Table; L is a cycloalkadienyl Hgand; each X is independently hydrogen, an aryl, alkyl, alkenyl, alkylaryl, or arylalkyl radical having 1-20 carbon atoms, a hydrocarboxy radical having 1-20 carbon atoms, a haHde, a nitrogen containing radical having 1-20 carbon atoms, or Q2YZ, wherein each Q is independently selected from the group consisting of -O-, -NR-, -CR2- and -S-; Y is either C or S; and Z is selected from the group consisting of -OR, -NR2, -CR3, -SR, -SiR3, -PR2, -H, and substituted or unsubstituted aryl groups, with the proviso that when Q is -NR- then Z is selected from the group consisting of -OR, -NR2, -SR, -SiR3, -PR2 and -H; and x is 2, 3, or 4 depending upon the valence state of M; b) an activity enhancing cycloalkadiene; and c) an activating cocatalyst. 2. The catalyst composition of claim 1, wherein the monocycloalkadienyl catalyst precursor has a formula selected from the group consisting of: M— "(A) n / \ Y (ID, and wherein: M is a transition metal; L is cycloalkadienyl Hgand; each Q is independently selected from the group consisting of ■ O-, -NR-, -CR2- and -S-; Y is C or S; Z is selected from the group consisting of -OR, -NR2, -CR3, -SR, - SiR3, -PR2, -H, and substituted or unsubstituted aryl groups, with the proviso that when Q is -NR- then Z is selected from the group consisting of -OR, -NR2, -SR, -SiR3, -PR2, and -H; n is 1 or 2; A is a univalent anionic group when n is 2 or A is a divalent anionic group when n is 1; each R is independently a group containing carbon, silicon, nitrogen, oxygen, and/or phosphorus, wherein one or more R groups may be attached to the L substituent; T is a bridging group selected from the group consisting of alkylene and arylene groups containing from 1 to 10 carbon atoms optionaUy substituted with carbon or heteroatoms, germanium, siHcone and alkyl phosphine; and m is 2 to 7; 3. The catalyst composition of claim 2, wherein the monocycloalkadienyl catalyst precursor is selected from the group consisting of indenyl zirconium tris(diethylcarbamate), indenyl zirconium tris(trimethylacetate), and (methylcyclopentadienyl) zirconium tris(trimethylacetate). 4. The catalyst composition of claim 1, wherein the activity enhancing cycloalkadiene is selected from the group consisting of cyclopentadiene, methylcyclopentadiene, indene, and methyl-n- propylcyclopentadiene. 5. The catalyst composition of claim 1, wherein the activity enhancing cycloalkadiene is present in an amount of about 0.01 to about 10 moles per mole of catalyst precursor. 6. The catalyst composition of claim 1, wherein the activating cocatalyst is selected from the group consisting of methylaluminoxane and modified methylaluminoxane. 7. The catalyst composition of claim 1 in Hquid form. 8. A process for the polymerization of an olefin, which comprises contacting at least one olefin monomer under polymerization conditions with a catalyst composition comprising the reaction product of: a) monocycloalkadienyl catalyst precursor having the formula: LMX X (I) wherein: M is a metal from groups IIIB to VIII or a rare earth metal of the Periodic Table; L is a cycloalkadienyl Hgand; each X is independently hydrogen, an aryl, alkyl, alkenyl, alkylaryl, or arylalkyl radical having 1-20 carbon atoms, a hydrocarboxy radical having 1-20 carbon atoms, a halide, a nitrogen containing radical having 1-20 carbon atoms, or Q2YZ, wherein each Q is independently selected from the group consisting of -O-, -NR-, -CR2- and -S-; Y is either C or S; and Z is selected from the group consisting of -OR, -NR2, -CR3, -SR, -SiR3, -PR2, -H, and substituted or unsubstituted aryl groups, with the proviso that when Q is -NR- then Z is selected from the group consisting of -OR, -NR2, -SR, -SiR3, -PR2 and -H; and x is 2, 3, or 4 depending upon the valence state of M; b) an activity enhancing cycloalkadiene; and c) an activating cocatalyst. 9. The process of claim 8, wherein the monocycloalkadienyl catalyst precursor has a formula selected from the group consisting of: (ID, and wherein: M is a transition metal; L is a cycloalkadienyl Hgand; each Q is independently selected from the group consisting of - O-, -NR-, -CR2- and -S-; Y is C or S; Z is selected from the group consisting of -OR, -NR2, -CR3, -SR, - SiR3, -PR2, -H, and substituted or unsubstituted aryl groups, with the proviso that when Q is -NR- then Z is selected from the group consisting of -OR, -NR2, -SR, -SiR3, -PR2 and -H; n is 1 or 2; A is a univalent anionic group when n is 2 or A is a divalent anionic group when n is 1; each R is independently a group containing carbon, silicon, nitrogen, oxygen, and/or phosphorus where one or more R groups may be attached to the L substituent; T is a bridging group selected from the group consisting of alkylene and arylene groups containing from 1 to 10 carbon atoms optionaUy substituted with carbon or heteroatoms, germanium, sihcone and alkyl phosphine; and m is 2 to 7. 10. The process of claim 9, wherein the monocycloalkadienyl catalyst precursor is selected from the group consisting of indenyl zirconium tris(diethylcarbamate), indenyl zirconium tris(trimethylacetate), and (methylcyclopentadienyl) zirconium tris(trimethylacetate) . 11. The process of claim 8, wherein the activity enhancing cycloalkadiene is selected from the group consisting of cyclopentadiene, methylcyclopentadiene, indene, and methyl-n-propylcyclopentadiene. 12. The process of claim 8, wherein the activity enhancing cycloalkadiene is present in an amount of about 0.01 to about 10 moles per mole of catalyst precursor. 13. The process of claim 8, wherein the activating cocatalyst is selected from the group consisting of methylaluminoxane and modified methylaluminoxane. 14. The process of claim 8 conducted in the gas phase. 15. The process of claim 8, wherein the catalyst composition is in liquid form.

Inventors: KAROL FREDERICK JOHN, REICHLE WALTER THOMAS, YANG XINMIN, KAROL, FREDERICK, JOHN, REICHLE, WALTER, THOMAS, YANG, XINMIN
Applicants: UNION CARBIDE CHEM PLASTIC, UNION CARBIDE CHEMICALS & PLASTICS TECHNOLOGY CORP
Application year: 1998
Main classification: C08F10
IPC codes: B01J31, C08F4, C08F10, C08F210