LOW PRESSURE HYDRODEALKYLATION OF ETHYLBENZENE AND XYLENE ISOMERIZATION

Abstract: A new process for the hydrodealkylation of ethylbenzene and the isomerization of xylenes at low pressure and at a low hydrogen to ethylbenzene mole ratio as well as a low hydrogen to hydrocarbon feed mole ration using a catalyst comprising (a) HZSM-5 having a particle size less than 1.0 microns, (b) a Group VIII metal such as platinum, and (c) an additional element such as magnesium.

Description: LOW PRESSURE HYDRODEALKYLATION OF ETHYLBENZENE AND XYLENE ISOMERIZATION FIELD OF THE INVENTION The present invention relates to a catalyst and process for hydrodealkylating ethylbenzene and isomerizing xylenes. Preferably, the ethylbenzene and xylenes are in a C 8 aromatics stream lean in paraxylene. BACKGROUND OF THE INVENTION The xylene isomers metaxylene, orthoxylene and, in particular, paraxylene, are important chemical intermediates. Orthoxylene is oxidized to make phthalic anhydride which is used to make phthalate based plasticizers among other things. Metaxylene is oxidized to make isophthaiic acid which is used in unsaturated polyester resins. However, paraxylene has by far the largest market of the three isomers. The largest use of paraxylene is in its oxidation to make terephthalic acid. Terephthalic acid in turn is used to make polymers such as polytrimethyleneterephthalate, polybutyleneterephthalate (PBT), and polyethyleneterephthalate (PET). PET is made via condensation polymerization of terephthalic acid with ethylene glycol. PET is one of the largest volume polymers in the world. It is used to make PET plastics (e.g., two liter PET bottles). It is also used to make polyester fiber which, in turn, is used to make clothes and other fabrics. Polyester fiber is used both as a homofiber, as well as a blended fiber, such as a blend with cotton. Given the large market for PET plastics and fibers, there is a substantial demand for high purity paraxylene. The demand for paraxylene is several times larger than the demand for ortho and metaxylene. The demand for paraxylene is also larger than the amount of paraxylene in the xylenes recovered as a by-product, such as the xylenes recovered from reformate (from catalytic reformers) and from pygas (from high temperature cracking to make light olefins). Because the demand for paraxylene is so much larger than the demand for the other xylene isomers and is larger even than the supply of paraxylene in xylenes recovered as a by-product, it has been found that isomerization of xyiene isomers is desirable to increase the amount of paraxylene production. Paraxylene is typically produced by reforming or aromatizing a wide boiling range naphtha in a reformer, for example, a CCR (Continuous Catalytic Reformer), and then separating by distillation a C 8 aromatics rich fraction from the reformer effluent. This C 8 fraction comprises near equilibrium amounts of ethylbenzene and the three xylene isomers, namely, para-, meta- and ortho-xylene. The paraxylene in this C 8 aromatics fraction is separated by either crystallization or adsorption. Rather than simply returning the paraxylene depleted C 8 aromatics stream to the refinery for a relatively low value use such as gasoline blending, the C 8 aromatics stream which is depleted in paraxylene is typically further processed by passing it over a xylene isomerization catalyst in a xylenes isomerization unit. The resulting C 8 aromatics stream, which now has an approximately equilibrium concentration of xylenes, i.e., a higher concentration of paraxylene, is recycled to the paraxylene separation process. The xylene isomerization unit typically serves at least two functions. First, it re-equilibrates the xylenes portion of the stream. Thus, in effect, it is creating paraxylene from the other xylene isomers. Second, it transalkylates or hydrodealkylates the ethylbenzene to facilitate its removal from the C 8 aromatics fraction. Since ethylbenzene boils in the same range as the xylene isomers, it is not economic to recover/remove the ethylbenzene by distillation, hence it is included in the C 8 aromatics fraction that is fed to the paraxylene separation process. Ethylbenzene is in general an inert from a para-xylene production standpoint, except for those para-xylene production Complexes which utilize a xylene isomerization process where the ethylbenzene is converted to xylenes. However, as pointed out earlier, such a process is limited in it's ethylbenzene conversion by C 8 aromatics equilibrium. Therefore, for those cases where ethylbenzene is an inert, it is highly desirable to remove as much ethylbenzene as possible per pass so that it does not accumulate in the recycle loop. If that were to occur, a bleed stream out of the para-xylene production loop would be necessary which would reduce para-xylene production. Thus, a critical function of the isomerization plant is to react-out the ethylbenzene by either hydrodealkylation or transalkylation/disproportionation depending on the type of isomerization process. Current xylene isomerization technology is based on two types of processes, high pressure processes and a low pressure process. Furthermore, within the high pressure processes, there are two types of such processes. U.S. Pat. No. 4,482,773 and U.S. Pat. No. 4,899,011 are two references dealing with one type of the high pressure process, usually carried out at 150 psig and higher and in the presence of hydrogen. U.S. Pat. No. 4,584,423 is a reference dealing with low pressure isomerization, usually carried out at less than 150 psig, for example, between about 25 and 100 psig and in the absence of hydrogen. In the 773 and '011 high pressure processes, a C 8 aromatics-rich hydrocarbon feed is contacted with a catalyst containing a ZSM-5 zeolite, xylene isomerization is carried out simultaneously with ethylbenzene hydrodealkylation to benzene and ethane. The hydrogen/hydrocarbon feed mole ratio is between 2/1 and 4/1. In both these patents, the objective is to achieve high levels of ethylbenzene conversion to isomerize the xylene to achieve a higher content of paraxylene, preferably an equilibrium content of paraxylene and to have low xylene losses. In the '773 process, ethylbenzene conversion levels are about 60% and xylene losses are about 2% yielding an ethylbenzene conversion/xylene loss ratio of about 30/1. Similar values are achieved with the '011 high pressure process, but at ethylbenzene conversions of about 70%. For both these high pressure processes, the catalyst system is very xylene selective. In U.S. Pat. No. 4,482,773, the catalyst used comprises platinum and magnesium on a ZSM-5 zeolite. The preferred catalyst is a HZSM-5 (H meaning that the ZSM-5 is predominately in the hydrogen form) with a preferred crystal size of 1-6 microns. The examples in U.S. Pat. No. 4,482,773 disclose a H 2 /HC feed mole ratio of 2/1 or higher. The high pressure process of U.S. Pat. No. 4,899,011 is similar to the '773 process but uses a dual catalyst bed system. The objective is to hydrodealkylate ethylbenzene in the first catalyst layer and complete the isomerization of xylenes in the second layer. The catalyst for both layers is a Pt containing ZSM-5, without any Group IIA metal such as Mg. The Pt ranges from 0.05-10 wt. %. The crystal size of the first layer is 1 micron minimum compared to 0.1 micron maximum for the second layer. In addition, the top layer is a more acidic ZSM-5 than the second layer. Operating conditions for the '011 process are 400-1000°F, 0-1000 psig, 0.5-100 WHSV, and a H 2 /HC feed mole ratio of 0.5/1 to 10/1. The catalysts for both U.S. Pat. No. 4,482,773 and U.S. Pat. No. 4,899,011 have good xylene isomerization activity as determined by the Paraxylene Approach To Equilibrium (PXAPE) which reaches values of 100-103%. A PXAPE of 100% indicates that the paraxylene concentration on a xylene basis is at equilibrium. The catalyst of both processes is based on ZSM-5. In the case of the 773 process, the catalyst contains Pt and possibly Mg. The catalyst has a silica/alumina ratio of about 50/1 to 100/1 and a crystal size of 1-6 microns. In the case of the '011 process, the catalyst bed consists of two catalyst layers, each of which contains Pt. Catalyst crystal size and acidity differ with the top catalyst having a crystal size of 2-4 microns and the bottom layer having a crystal size of 0.02-0.05 microns. In addition, as mentioned above, the top layer is more acidic than the bottom layer. It should be noted that within the high pressure xylene isomerization process technology, there is a sub-type of process where the objective is to eliminate the ethylbenzene by converting the ethylbenzene to xylenes. However, high levels of ethylbenzene conversion as in the 773 and '011 patents are not achieved with this type of process, as the ethylbenzene concentration is limited by the equilibrium concentration on a C 8 aromatics basis. In addition to U.S. Pat. No. 4,899,011 and U.S. Pat. No. 4,482,773 discussed above, two other patents of interest are U.S. Pat. No. 4,467,129, issued August 21 , 1984 to Iwayama et al., and U.S. Pat. No. 4,899,010, issued February 6, 1990 to Amelse et al. U.S. Pat. No. 4,467,129 is very similar to the 733 and '011 processes, in that ethylbenzene is converted by hydrodealkylation and uses a mixture of mordenite and a ZSM-5 which contains rhenium. A ZSM-5 containing Mg and Re is disclosed. Platinum is not a catalyst component. The process operates at 572-1112°F, a pressure of 0-1370 psig, and a H 2 /HC feed mole ratio of 1-50/1. The examples show a temperature of ~700°F, a pressure of 165 psig, and a H^HC feed mole ratio of 4/1. We estimate the WHSV at 3.5. U.S. Pat. No. 4,899,010 is also an ethylbenzene hydrodealkylation/xylene isomerization process. It is based on the hydrogen form of a borosilicate equivalent of ZSM-5 known as AMS-1 B. The catalyst contains 0.1-1.0 wt. % Pt. Operating conditions are 700-1000°F, 0-100 psig, and a H 2 /HC feed mole ratio of 0.25-5.0. Ethylbenzene conversions are about 25-28% and the ethylbenzene conversion/xylene loss ratio is about 29. In the low pressure xylene isomerization process, which operates without any hydrogen present, ethylbenzene conversion is achieved by the disproportionation of ethylbenzene. The products of this disproportionation reaction are benzene and di-ethylbenzene, a C 10 aromatic. Ethylbenzene is also converted by another reaction, namely, by transalkylation with the xylenes. This latter reaction produces benzene and di-methyl-ethylbenzene, also a C 10 aromatic. This reaction with xylenes results in an undesirable loss of xylenes. Another reaction mechanism which contributes to xylene loss is the disproportionation of xylenes to produce toluene and trimethylbenzenes, a C 9 aromatic. All these reactions are a function of the catalyst acidity. Operating conditions are such as to achieve ethylbenzene conversions of about 25-40%. However, the xylene losses are high, on the order of 2.5-4.0%, resulting in an ethylbenzene conversion/xylene loss ratio of 10/1. Thus, at 40% ethylbenzene conversion, the xylene losses are 4%. Furthermore, high levels of ethylbenzene conversion, in the range of 50-70% are not practical as the temperature required to achieve these levels of ethylbenzene conversion would be quite high. At 70% ethylbenzene conversion, the temperature required is about 60-70°F higher than that required to achieve 50% ethylbenzene conversion. In addition, the coking rate would also be substantially higher due to the higher operating temperature and higher level of ethylbenzene conversion. The net effect of operating at higher ethylbenzene conversion is a substantial reduction in the catalyst life. One key goal of xylene isomerization catalyst development efforts has been to reduce xylene losses at constant ethylbenzene conversion, or to achieve higher ethylbenzene conversions while reducing the xylene losses. U.S. Pat. No. 4,584,423, which describes a low pressure isomerization process, discloses that a Mg/ZSM-5 extrudate resulted in a 40% reduction in xylene loss when used in low pressure isomerization, and a Zn/ZSM-5 extrudate resulted in a 30% reduction in xylene loss when used in low pressure isomerization operating at 25% ethylbenzene conversion. However, the operating temperature for the reaction zone was higher relative to the base case using ZSM-5 catalyst. Operation to achieve 50% ethylbenzene conversion would have required even higher operating temperatures. From a catalyst stability standpoint, the high pressure processes which operate in the presence of hydrogen have catalyst systems which are an order of magnitude more stable than the low pressure process which operates in the absence of hydrogen. For high pressure processes, catalyst stability is believed enhanced by using a catalyst which contains a hydrogenation/dehydrogenation metal component, such as platinum, and by using a high hydrogen partial pressure. The high hydrogen partial pressure is achieved by combining a high system/process pressure with a high hydrogen/hydrocarbon feed mole ratio, for example, 4/1. This is equivalent to a hydrogen concentration of approximately 80 mole %. Accordingly, in a low pressure process, it would be desirable to achieve the performance parameters of the high pressure isomerization processes and achieve high levels of ethylbenzene conversion, while simultaneously achieving xylene isomerization and very low xylene losses, and achieving high stability for the catalyst. SUMMARY OF THE INVENTION According to the present invention, a process is provided for hydrodealkylation of ethylbenzene and isomerization of xylenes. The process comprises contacting, in a reaction zone, a hydrocarbon feed containing ethylbenzene and xylenes, with a catalyst comprising ZSM-5, a Group VIII metal, and a further element selected from magnesium, sodium, barium, potassium, calcium, zinc or phosphorus; and wherein the paraxylene content of the xylenes in the feed is less than an equilibrium amount, the contacting is carried out in the presence of gaseous hydrogen, and the ZSM-5 has a crystal size less than 1.0 microns; to thereby hydrodealkylate ethylbenzene to produce benzene and isomerize xylenes to produce paraxylene. Preferred reaction conditions, in the reaction zone of the present invention, include a temperature of 500°F to 1000°F, more preferably 600°F to 900°F, and still more preferably 700°F to 900°F. Preferably, the reaction zone pressure is 0 to 200 psig, more preferably 10 to 150 psig, and still more preferably below 100 psig, for example, 25 to 100 psig. Particularly preferred pressure is 10 to 50 psig for the reaction zone of the present invention. An advantage of the present invention is achievement of high ethylbenzene conversion, excellent xylene isomerization and low xylene losses at low pressure. According to an alternate embodiment of the present invention, a particularly preferred low pressure in the reaction zone is below 40 psig, and a still more preferred pressure is below 35 psig. The weight hourly space velocity (WHSV), based on the zeolite (WHSVZ), preferably is 2 to 20, more preferably 3 to 15, still more preferably 4 to 10, and most preferably 8.5 to 10.0. Preferably, the feed to the reaction zone is a hydrocarbon stream comprising mainly C 8 hydrocarbons, containing ethylbenzene, and a mixture of xylenes that is below equilibrium in paraxylene content. Preferably, the hydrogen to ethylbenzene feed mole ratio is 0.3 to 15, more preferably 0.7 to 15, and still more preferably 1.0 to 11. Particularly preferred hydrogen to ethylbenzene mole ratios are between 1.5 and 7.0, and most preferably between 1.5 and 3.0 for the feed to the reaction zone of the present invention. The Group VIII metal of the catalyst used in the reaction zone of the process of the present invention preferably is platinum, and the further element of the catalyst preferably is magnesium. Preferably, the ZSM-5 component used to make the catalyst is predominantly in the hydrogen form. Among other factors, the present invention is based on our finding that when combining use of: (a) a ZSM-5 based catalyst having a small ZSM-5 crystal size less than 1 micron, and associated with a Group VIII metal such as platinum, and a further element such as magnesium with (b) low pressure, and (c) reaction conditions including the presence of low concentrations of gaseous hydrogen, a surprisingly high ethylbenzene conversion is achieved in the reaction zone, while also achieving xylene isomerization and low xylene losses. Further, we have found that due to the relatively small amount of hydrogen needed to facilitate the hydrodealkylation reaction in the process of the present invention, in accordance with a preferred embodiment of the present invention, recycle of unused hydrogen to the reaction zone is not required. Not having to recycle hydrogen simplifies the process and allows the process to be performed with less equipment and a lower cost of operation. In particular, according to preferred embodiments, this invention eliminates the requirement for a recycle compressor in the process. Also, the present invention allows the use of relatively low pressure in the reaction zone. Accordingly, the reactors and associated piping and equipment do not have to be built to withstand high pressures required when using prior art processes. Another advantage we have found resulting from the present invention is that the low pressure isomerization process, which in the past could not utilize the hydrodealkylation type process for the removal of ethylbenzene from the C 8 aromatics and paraffins stream, can now be retrofitted to take advantage of this more efficient process. Such older low pressure isomerization plants, still in use today, were built to operate at relatively low pressures and without hydrogen. They could not be economically retrofitted to accommodate prior art hydrodealkylation processes, as these require high pressures in excess of 150 psig, as well as large volumes of hydrogen and the ability to recycle the hydrogen. Still another advantage of the present invention is that, in accordance with a preferred embodiment, effective removal of a portion of the C 8 paraffins present in the feed to the hydrodealkylation/isomerization reaction zone is achieved by hydrocracking such paraffins to lighter paraffins, which lighter paraffins are easily removed from the C 8 aromatics. Preferably, at least 15%, more preferably at least 20% of the C 8 paraffins are effectively removed in this manner. This is of particular advantage in paraxylene production processes that utilize a feed comprising unextracted, predominately C 8 hydrocarbons feed containing both aromatics and nonaromatics (paraffins) from a high octane catalytic reformer. Such unextracted reformate can include several percent nonaromatics. These nonaromatics may build up in the paraxylene processing loop requiring a bleed stream to control their concentration, unless conversion is achieved in the xylene isomerization step. Still a further advantage of the present invention is that it minimizes the system pressure and the amount of hydrogen, expressed in terms of the hydrogen to ethylbenzene mole ratio, needed for the hydrodealkylation reaction. Hydrogen is a valuable and expensive commodity in a refinery or chemical complex. In the present invention, minimal hydrogen is required. In addition, the hydrogen required preferably is used at a relatively low pressure, allowing the hydrogen from another higher pressure unit [such as from a conventional reformer using a bifunctional (acidic) reforming catalyst, or AROMAX® type reformer using a monofunctional (nonacidic) type catalyst] to be used in a "stepped" arrangement. Such a "stepped" arrangement adds to the cost savings benefits of this invention. Preferred Group VIII hydrogenation metal components for the catalyst used in the process of the present invention include platinum, palladium, and nickel. Platinum is particularly preferred as the hydrogenation metal in the catalyst used in the present invention. Preferably, the amount of hydrogenation metal is between 0.05 and 1.5 wt. %, more preferably between 0.05 to 1.0 wt. %, based on the weight of zeolite in the catalyst. For the particularly preferred hydrogenation metal platinum, the most preferred range is 0.05 to 0.5 wt. %. The catalyst also contains a further element, selected from the group consisting of magnesium, sodium, barium, potassium, calcium, zinc, and phosphorus. The amount of the further element preferably is 0.5 to 5 wt. %, based on the ZSM-5 weight, more preferably 1 to 4 wt. %, and most preferably 1.5 to 3 wt. %. As previously stated, magnesium is preferred for the further element of the catalyst. We have found that the predominantly hydrogen form of the ZSM-5 and the use of magnesium in the catalyst are particularly advantageous in achieving a moderated acidity and pore constraint catalyst for use in the process of the present invention. DETAILED DESCRIPTION OF THE INVENTION According to the present invention, a catalyst and process are provided for achieving high levels of ethylbenzene conversion, xylene isomerization and low xylene losses. Preferably, the catalyst comprises a small crystal size ZSM-5 containing both a Group VIII metal (e.g., platinum) and an element such as magnesium. It is believed that the magnesium acts to neutralize or moderate acid sites, and also to reduce accessibility to the zeolite pores. Preferred small crystal size ZSM-5 of the catalyst used in the present invention is discussed hereinbelow, as is preferred silica to alumina ratio. In a preferred catalyst, the Pt content is 0.075 to 0.3 wt. % and the Mg content is 1.5 to 3.0 wt. %. In accordance with the present invention, the process is operated at low pressure, and preferably with a low flow of hydrogen. The low flow of hydrogen may be referred to as "trickle flow". Preferably, the trickle flow is once-through, that is, with no recycle hydrogen. Ethylbenzene is converted by hydrodealkylation, preferably to benzene and ethane. The xylene losses in accordance with the process provided by the present invention are substantially reduced relative to prior low pressure processes. Also, in the process of the present invention, a high degree of xylene isomerization to paraxylene is achieved. In the process of the invention, the xylenes in the feed, which contain paraxylene on a xylene basis in an amount which is less than that at thermal equilibrium on a xylene basis, are converted (or isomerized) such that in the effluent from the isomerization reaction zone, the paraxylene content on a xylene basis preferably is at least at 90% of the thermal equilibrium content (or concentration). More preferably, in the present invention, the xylenes in the feed are converted such that in the effluent from the isomerization reaction zone, the paraxylene content on a xylene basis is at least at 95% of the thermal equilibrium content (or concentration). Still more preferably, in the present invention, the xylenes in the feed are converted such that in the effluent from the isomerization reaction zone, the paraxylene content on a xylene basis is at least at 100% of the thermal equilibrium content (or concentration). In addition, we have found that the preferred catalyst and process conditions described herein for the present invention achieve high catalyst stability relative to prior low pressure processes. As stated above, the present invention uses a catalyst comprising ZSM-5 aluminosilicate. Preferably, the ZSM-5 is in the hydrogen form. ZSM-5 can have most of the original cations associated therewith replaced by a wide variety of other cations according to techniques well known in the art. In a preferred embodiment of the present invention, most of the original cations are replaced by hydrogen by methods such as ammonium-exchange followed by calcination. The crystal size of the ZSM-5 component of the catalyst used in the process of the present invention is less than 1.0 microns, preferably less than 0.8 microns, for example, 0.1 to 0.8 microns. The silica/alumina ratio of the ZSM-5 of the catalyst used in the present invention preferably is in the range of 30 to 200, more preferably from 30 to 150, still more preferably in the range of from 60 to 100, and most preferably is in the range of 70 to 90. The preferred Group VIII hydrogenation metal for the catalyst used in the present invention is Pt. Preferably, the Pt content is from 0.05 to 0.5 wt. %, more preferably from 0.075 to 0.3, and still more preferably from 0.075 to 0.2 wt. %. Pt is believed to act as a hydrogenation/dehydrogenation component. Although not as preferred in the present invention, other Group VIII metals can be used such as palladium (Pd) or nickel (Ni). The Pt may be added by ion-exchange or by impregnation. The preferred further element of the catalyst is magnesium. Preferably, the magnesium is present in an amount from 0.5 to 5.0 wt. %, more preferably 1 to 4 wt. %, and most preferably 1.5 to 3.0 wt. % based on weight of zeolite in the catalyst. Although not as preferred in the present invention, other components can be used as the further element, such as Na, Ba, K, Ca, Zn, and P. These components can be added by ion-exchange or by impregnation. If sodium is used as the further element, preferably it is present as add back sodium, so that the form and amount of the sodium can be better controlled. By "add back" sodium, we refer to first ion exchanging sodium out of the ZSM-5 (as part of the process to make the hydrogen form of ZSM-5), and then adding sodium back to the ZSM-5 in a controlled manner and amount. The catalyst preferably comprises zeolite bound with an inorganic matrix, such as alumina. A preferred form of the catalyst is bound zeolite extruded to a 1/16-in. diameter extrudate. The feedstock for the process of the present invention is preferably obtained from a paraxylene separation process such as an adsorption process, a crystallization process, or a combination of both processes. Such processes remove paraxylene from a C 8 boiling range feedstocks, leaving a paraxylene depleted stream. The paraxylene depleted stream contains a below equilibrium level of paraxylene, preferably 0-20% by weight paraxylene, more preferably 0-12% by weight paraxylene. Feeds that are obtained predominantly from an adsorption process will typically have lower amounts of paraxylene in the feed than a feed that is obtained from a paraxylene separation process based on crystallization. According to a preferred embodiment, the process of the present invention comprises contacting the catalyst described herein with a C 8 aromatics stream which has a paraxylene concentration which is below equilibrium on a xylenes basis and which has an ethylbenzene concentration of 5-20 wt. %, preferably 10-20 wt. %, and a non-aromatic concentration of between 0 and 8 wt. %, more preferably 0-5 wt. %. In the process of the present invention, preferably, the hydrogen is added at a rate so that the mole ratio of hydrogen to ethylbenzene in the feed is preferably 1.5 to 7.0, and most preferably 1.5 to 3.0. The equivalent mole ratio of hydrogen to hydrocarbon in the feed is 0.02 to 1.0, preferably 0.05 to 1.0, more preferably 0.075 to 0.8, still more preferably 0.1 to 0.5, and most preferably 0.1 to 0.2. In a preferred embodiment of the present invention, since the rate of hydrogen addition is so small — a trickle — relative to the feed, there is no need to recycle the unused hydrogen, thus the hydrogen is added on a once-through basis. The temperature used in the reaction zone is preferably 500 to 1000°F, more preferably between 600 to 900°F. Preferably, the reaction zone of the present invention is operated to achieve an ethylbenzene conversion of 20 to 80 wt. %, more preferably 25 to 75 wt. %, and most preferably 50 to 70 wt. %. The ethylbenzene conversion/xylene loss ratio of the present process is greater than 15/1 , preferably greater than 20/1 , and more preferably greater than 25/1. Terms used in the art such as "lean in paraxylene" or "depleted in paraxylene" are generally used to indicate that a given stream contains less than an equilibrium amount of paraxylene relative to the other xylenes (metaxylene and orthoxylene). A stream that is lean in paraxylene or depleted in paraxylene is typical of a stream that has been subjected to a paraxylene separation process such as an adsorption or crystallization process in order to remove the paraxylene contained therein. Such a stream depleted in paraxylene is a typical feedstock to an isomerization type process of the present invention. An important feature of the present invention is effective removal of a portion of the ethylbenzene from the C 8 feed by hydrodealkylation in the reaction zone. We have found that, in the process of the present invention, the hydrodealkylation can be accomplished with a surprisingly small amount of hydrogen at a surprisingly low pressure. As such, we have found that a useful measure for the present invention is hydrogen to ethylbenzene feed mole ratio, since the primary purpose of the hydrogen is to participate in the hydrodealkylation of the ethylbenzene. Stoichiometrically, one mole of hydrogen is required to hydrodealkylate one mole of ethylbenzene. Thus, the theoretical minimum amount of hydrogen required to hydrodealkylate 50% of the ethylbenzene in the feed is a hydrogen to ethylbenzene mole ratio of 0.5. In practice, more hydrogen is required since all of the hydrogen does not react and some of the hydrogen reacts with molecules other than ethylbenzene. For example, the hydrogen may be used in hydrogenating cracked paraffins in the reaction zone. Hydrogen may also saturate some of the aromatic rings. The fouling rate of the catalyst used in the reaction zone is low under the process conditions of the present invention. Fouling of an isomerization catalyst is to a great extent caused by coke formation on the catalyst surface. Fouling of the catalyst decreases the performance of the catalyst. The decrease in performance can be compensated for to a great extent by increasing the process temperature. The process temperature can only be increased so far, however. It is then necessary to regenerate the catalyst by removing the coke. If the time between required catalyst regenerations is too short for a given catalyst, due to a rapid fouling rate, the catalyst is not practical for a commercial unit. The rate of fouling of the catalyst is thus an important factor in the desirability of the catalyst. The process of the invention may be carried out in a moving bed or fixed bed reactor. In a moving bed reactor and after reaching the end of a reaction cycle, the catalyst can be regenerated in a regeneration section/zone where the coke is burned off from the catalyst in an oxygen containing atmosphere such as air at a high temperature, after which the catalyst is recycled to the reaction zone for further contact with the feed. In a fixed bed reactor, regeneration can be carried out in a conventional manner by using initially an inert gas which contains a small amount of oxygen, e.g., 0.5 to 2.0%, to burn the coke off the catalyst in a controlled manner so as not to exceed a maximum temperature of 900°F to 950°F. The ZSM-5 zeolite component of the catalyst used in the process of the present invention can be prepared in various manners. Suitable preparation procedures are described in U.S. Pat. No. 3,702,886 to Argauer et al. ZSM-5 embraces a family of crystalline aluminosilicates as set forth in more detail in U.S. Pat. No. 3,702,886, the disclosure of which patent is incorporated by reference into this specification. The structure of the ZSM-5 class of zeolites is such that the pore sizes or apertures of the zeolite are in the intermediate size range of approximately 5 to 7 Angstroms, usually about 5.5 Angstroms. This is in contrast to the larger pore size zeolites, such as faujasite, or the smaller pore size zeolites such Linde Type A and erionite. The structure of ZSM-5 is described by Kokootailo et al. in Nature, Vol. 272, March 30, 1978, page 437. The pore opening into the crystalline zeolite is delineated by the atomic structure. However, the pore opening or constraints may be modified by components added to the ZSM-5. Although ZSM-5 is the preferred zeolite for use in the catalyst used in the process of the present invention, other zeolites of the ZSM-5 type are embraced within a broad embodiment of the present invention. These zeolites include ZSM-11 , which is described in U.S. Pat. Nos. 3,709,979 and 4,108,881 (alternate synthesis), the disclosures of which are incorporated by reference into the present specification. Another publication that provides a synthesis of ZSM-11 is PCT publication WO9509812-A1 (also EP 721.427-A1). According to an alternate embodiment of the present invention, besides ZSM-5, other intermediate pore zeolites having a pore size of approximately 5 to 7 Angstroms may also be used to form the catalyst used in the process of the present invention. ZSM-11 is included in such other intermediate pore size zeolites. However, the most preferred embodiment of the present invention uses ZSM-5 zeolite. The ZSM-5 zeolite can be made by preparing a solution containing water, tetrapropyl ammonium hydroxide and the elements of sodium oxide, an oxide of aluminum or gallium, an oxide of silica, and having a composition, in terms of mole ratios of oxides, falling within the following ranges: TABLE wherein R is propyl. This mixture is maintained at reaction conditions until the crystals of the zeolite are formed. Thereafter, the crystals are separated from the liquid and recovered. Typical reaction conditions consist of a temperature of from about 160°F to 400°F for a period of about 2 days to 60 days. A more preferred temperature range is from about 190°F to 235°F, with the amount of time at a temperature in such range being from about 7 days to 21 days. The digestion of the gel particles is carried out until crystals form. The solid product is separated from the reaction medium, as by cooling the whole to room temperature, filtering and water washing. ZSM-5 is preferably formed as an aluminosilicate. The composition can be prepared utilizing materials which supply the elements of the appropriate oxide. Such compositions include aluminosilicate, sodium aluminate, alumina, sodium silicate, silica hydrosil, silica gel, silicic acid, sodium hydroxide and tetrapropylammonium hydroxide. Each oxide component utilized in the reaction mixture for preparing a member of the ZSM-5 family can be supplied by one or more initial reactants. For example, sodium oxide can be supplied by an aqueous solution of sodium hydroxide, or by an aqueous solution of sodium silicate. The reaction mixture can be prepared either batchwise or continuously. Crystal size and crystallization time of the ZSM-5 composition will vary with the nature of the reaction mixture employed. The zeolite contains tetrapropylammonium cations which are removed by calcination producing the H-Na form of the zeolite. The zeolites used in the instant invention preferably have a certain proportion of the original cations associated therewith replaced by other cations. Exchange techniques known in the art may be used. Preferred replacing cations include ammonium and metal cations, including mixtures of the same. Preferably, the replacing cation is ammonium, and preferably the ammonium is converted to hydrogen by driving off ammonia to result in the replacing cation being hydrogen. Thus, as stated above preferably the ZSM-5 used to form the catalyst used in the present invention is predominantly in the hydrogen form. By predominantly in the hydrogen form, we mean that a dominant characteristic of the ZSM-5 used to form the catalyst is that the ZSM-5 is in an acidic form as opposed to a basic form. A basic form is one where the ZSM-5 has substantial amounts of the original sodium; that is, the sodium that is present in the as-synthesized ZSM-5. Accordingly, preferably at least 80% of the sodium ions in the ZSM-5 used to form the catalyst have been replaced by hydrogen ions, more preferably at least 90%, still more preferably at least 95%, and most preferably at least 98% of the sodium ions have been replaced by hydrogen ions. In accordance with these percentage removals, the amount of sodium left in the ZSM-5 will depend on the original amount present, which in turn will depend on factors such as the silica to alumina ratio. Keeping these qualifications in mind, ranges for sodium left in the ZSM-5 after it has been converted to the hydrogen form preferably are less than 0.1 wt. % of the original sodium, more preferably less than 0.06 wt. %, and most preferably less than 0.03 wt. %. Typical ion exchange techniques include contacting the zeolite with a salt of a replacing cation or cations. Although a wide variety of salts can be employed, particular preference is given to chlorides, nitrates and sulfates. In the process of the present invention, it is preferred to use the zeolite in a "bound" form, that is, with a refractory oxide as a binder for the overall catalyst particle. Suitable refractory oxide binders are alumina, silica, titania, clay, or mixtures thereof. This binder serves to hold the crystalline zeolite particles together in a catalyst particle of suitable size and suitable attrition resistance upon handling and use in the isomerization process. The amount of binder used versus zeolite is preferably between 10 and 65 percent binder by weight, more preferably between 20 and 50 percent binder. Alumina is a particularly effective binder for the catalyst used in the ethylbenzene hydrodealkylation/isomerization process of the present invention. A preferred form of the alumina is that commonly referred to as Catapal-B, available from Condea-Vista Company. A typical catalyst is in the form of a 1/16-inch diameter by 3/16-inch length extrudate. Use of the zeolite catalyst as prepared would result in too high a pressure drop in the preferred fixed bed used in the ethylbenzene hydrodealkylation/isomerization process. The added hydrogenation metal, such as the preferred platinum, palladium, or nickel used in the catalyst, and the other added metal such as the preferred magnesium, may be added to the catalyst by impregnation or ion exchange using known techniques. In general, the metals are added as salts, preferably of thermally decomposable anions such as the nitrate, nitrite, acetate, etc., or soluble metal complexes, by filling the pores of the catalyst with a solution of appropriate concentration to achieve the desired metal loading, equilibrating, drying and calcining to remove solvent, impurities and to decompose the salts to remove the volatile products. Alternatively, adsorption or other techniques well known in the art for introducing metals into porous substances may also be used. BRIEF DESCRIPTION OF THE DRAWING FIG. 1 is a schematic flow diagram illustrating the positioning of the ethylbenzene hydrodealkylation/isomerization reaction zone in a process sequence directed to producing paraxylene. DETAILED DESCRIPTION OF THE DRAWING Referring now in more detail to FIG. 1 , a mixed aromatic/paraffin feed in line 1 is combined with the line 2 effluent stream from ethylbenzene hydrodealkylation/isomerization zone 15. The combined streams are fed via line 3 to column 4 for distillation. The higher boiling aromatics — those having more than 8 carbon atoms — are taken as a bottoms fraction in line 5; the overhead comprising C 8 aromatics and lighter components is charged via a line 6 to another distillation unit column 7. In this second distillation column, the lower boiling aromatics — those having less than 8 carbon atoms — and any paraffinic components, are taken overhead in line 8. The bottoms from the second distillation, comprising C 8 aromatics, are then fed via line 9 to paraxylene separation zone 10. In separation zone 10, about 25 to 95 percent of the paraxylene is removed by crystallization or by extraction. The crystallization can be carried out by low temperature processes, and extraction can be carried out by various processes, for example, the UOP "Parex Process" or the IFP "Eluxyl Process". Separated paraxylene is withdrawn via line 11 from zone 10. The effluent (mother liquor) from the separation zone 10 is withdrawn via line 12 and is fed to ethylbenzene hydrodealkylation/xylene isomerization zone 15 which uses reaction conditions according to the present invention, as described above. Provision is made via line 13 to bleed some of the paraxylene plant mother liquor as desired. Gaseous hydrogen is fed into the ethylbenzene hydrodealkylation/xylene isomerization zone 15 via line 16. In accordance with a preferred embodiment of the present invention, only once-through hydrogen is used. Light gasses are removed from the ethylbenzene hydrodealkylation/isomerization zone 15 via line 17. Finally, the ethylbenzene depleted, xylene isomerized stream from the ethylbenzene hydrodealkylation/xylene isomerization zone 15 is withdrawn via line 2 and is recycled to be combined with the incoming fresh feed. Fresh feed to the process of the present invention preferably contains about 5 to 20 weight percent, preferably 5 to 15 weight percent, ethylbenzene based on C 8 aromatics. When operating this process in a continuous manner, the quantity of recycled C 8 aromatics is from 2 to 4 times that of the fresh feed; and the ethylbenzene in the feed to the paraxylene plant levels out at about 5 to 25 percent. EXAMPLES The hydrocarbon feeds used in all of the process examples below were feeds obtained from a commercial low pressure isomerization process. The composition of the feeds is given in the table below and was determined by gas chromatographic analysis. Table II Feed Composition Examples 1 , 2 and 3 that follow describe preparation of catalysts, including preferred catalysts for use in the process of the present invention. All of these catalysts were made using a ZSM-5 zeolite, particularly an HZSM-5. The "H" connotes that the ZSM-5 is in predominantly the hydrogen form. The HZSM-5 we used was purchased from manufacturers of this zeolitic material. The following table lists the HZSM-5 manufacturers and gives the crystal size of the ZSM-5. The crystal size measurements were made using a Scanning Electron Microscope (SEM). The number averaging method described in Example 4 was used to determine the average crystal size of the ZSM-5 crystals that were used to make the catalysts. Example 1 Preparation of Mq-Pt/ZSM-5 Catalyst Using H-ZSM-5 Powder 12 grams of CBV 8020 H-ZSM-5 from PQ Corporation was weighed out. 3.22 grams of magnesium nitrate hexahydrate, Baker 2468-1 , was dissolved in deionized water. The magnesium nitrate solution was diluted to a volume of 8.0 milliliters. The ZSM-5 powder was impregnated with the solution of magnesium nitrate by the method of incipient wetness. The sample was dried overnight at 120°C. The sample was then calcined at 500°C overnight in flowing air. The sample was then cooled in a desiccator. 10 grams of the Mg-ZSM-5 was weighed into a 250 ml plastic bottle. 80 ml of water was added and the resultant slurry was placed into a constant temperature shaker bath at 30°C and 150 rpm. 0.0178 grams of platinum tetramine dichloride, Johnson-Matthey assay 56.3% Pt, was weighed out and dissolved with 30 ml of deionized water. The Pt solution was added to the Mg-ZSM-5 slurry. The resultant slurry was mixed at 30°C and 150 rpm for 24 hours. The solid was recovered by filtering. It was then dried at 120°C for five hours. The solid was calcined in flowing air at 288°C for three hours. The calcined solid was then cooled in a desiccator. The calcined catalyst was formed using a hydraulic press and die to make 1/2" x 3/8" cylinders. The powder was then compressed at 11 ,000 psig for one minute to form pellets. The pellets were crushed and sized to 20-40 mesh (U.S. Standard Sieve) size chips. The chips were used for test reactor studies. The resultant catalyst contained 2.4% Mg and 0.1% Pt by weight. Example 2 Preparation of Mα-Pt/ZSM-5 Catalyst Using H-ZSM-5 Extrudate 120 grams of CBV 8062 bound H-ZSM-5 extrudate from PQ Corporation was weighed out. 23.26 grams of magnesium nitrate hexahydrate, Baker 2468-1 , was dissolved in deionized water. The solution was diluted to volume of 67.2 milliliters. The H-ZSM-5 extrudate was impregnated with the solution of magnesium nitrate by the method of incipient wetness. The sample was dried overnight at 120°C, then calcined at 500°C overnight in flowing air. The sample was cooled in a desiccator. 120 grams of the Mg-ZSM-5 extrudate was divided into four equal portions by weight and placed into four 500 ml plastic bottles. 240 ml of deionized water was added to each bottle. The samples were placed into a constant temperature shaker bath at 30°C and 150 rpm. Four 0.0429 gram samples of platinum tetramine dichloride, Johnson-Matthey assay 56.3% Pt, were dissolved in 90 ml portions of deionized water. Each of the Pt solutions was added to one of the Mg-ZSM-5 slurries. The resultant slurries were mixed in the shaker baths at 30°C and 150 rpm for 24 hours. The solid was recovered by filtering. The solids were dried at 120°C for five hours. The dry solids were calcined in flowing air at 288°C for two hours. That samples were cooled in a desiccator. The catalyst contained 1.9% Mg and 0.08% Pt by weight. Assuming the extrudates to consist of 80% ZSM-5 and 20% binder, the composition on a zeolite basis was 2.4% Mg and 0.1 % Pt. Example 3 Preparation of Mq-Pt/ZSM-5 Catalyst Using Large Crystal H-ZSM-5 Powder 10.5 grams of B7567 H-ZSM-5 from Zeochem was weighed out. 2.82 grams of magnesium nitrate hexahydrate, Baker 2468-1, was dissolved in deionized water. The magnesium nitrate solution was diluted to a volume of 7.3 milliliters. The H-ZSM-5 was impregnated with the solution of magnesium nitrate by the method of incipient wetness. The impregnated sample was dried for four hours at 120°C, then calcined at 500°C overnight in flowing air. The samples were then cooled in a desiccator. 10 grams of the Mg-ZSM-5 was weighed into a 250 ml plastic bottle. 80 ml of water was added to the bottle and the resultant slurry was placed into a constant temperature shaker bath at 30°C and 150 rpm. 0.0178 grams of platinum tetramine dichloride, Johnson-Matthey assay 56.3% Pt, was dissolved in 30 ml of deionized water. Pt solution was added to the slurry. The mixing was continued at 30°C and 150 rpm for 24 hours. The solid was recovered by filtering then dried at 120°C for five hours. The solid was then calcined in flowing air at 288°C for three hours, then cooled in a desiccator. The calcined catalyst was formed using a hydraulic press and die to make 1/2" x 1/2" cylinders. The powder was compressed at 8,000 psig for one minute. The pellets were crushed and sized to 20-40 mesh (U.S. Standard Sieve) size chips. The chips were used for test reactor studies. The catalyst contained 2.4% Mg and 0.1 % Pt by weight. Example 4 Measurement of ZSM-5 Crystal Size bv SEM The method used is based on scanning electron microscopy (SEM). SEM is a common analytical technique for examining the morphology of materials at high magnifications. The range of magnifications for a common SEM instrument is typically 20x to 50,000x. I. Specimen Preparation For the purpose of this specification, the SEM sample was prepared by mounting a small amount of the zeolite powder onto an SEM specimen stub. The description of the procedure can be found in many standard microscopy text books. The procedure used to determine all of the crystal sizes given herein was as follows: Step 1. A double sided sticky carbon tape, available from microscopy supplies vendors, was affixed to the specimen stub. Step 2. A small amount of zeolite powder was spread onto the carbon tape using a stainless steel spatula. Step 3. The excess zeolite powder was gently blown off using an air hose or a compressed air duster. Step 4. A Pd-Au alloy film (approximately 15 nm thick) was sputtered onto the sample to prevent the sample from charging under the electron beam. Note that (a) a representative portion of the powder was selected from the sample container, and (b) the mounting procedure was such that individual particles would be reasonably evenly spread out across the field of view at 10,000x magnification. II. SEM Imaging Step 1. The sample was surveyed at low magnifications, e.g., 500x-1000x, to look for representative areas to photograph. Step 2. At least four representative images were recorded at the 10,000x magnification. Step 3. The number of images recorded contained at least 200 zeolite crystals in total. III. Image analysis to obtain number average crystal size The analysis was performed on the SEM images of 10,000x magnification. The raw data was stored in a computer spreadsheet program, e.g., Microsoft Excel, Lotus 123, etc. The objective was to obtain the arithmetic mean crystal size (d av ) and its standard deviation (σ),where, The arithmetic mean d av = (∑ n,d | )/ (∑ n, ) The standard deviation σ = (∑ (d, - d av ) 2 / (∑ n, )) 1 2 Step 1. The recorded SEM image at 10,000x was scanned using a horizontal straight edge. Step 2. The longest dimension of the individual crystals parallel to the horizontal line of the straight edge was measured and recorded. Those particles that were clearly large polycrystalline aggregates were not included in the measurement. Step 3. 200 crystals were measured. Step 4. The arithmetic mean (d av ) and the standard deviation (σ) were reported. The results were cross-checked by transmission electron microscopy (TEM) to assure that the crystals measured in the SEM images were actually single crystals rather than polycrystalline aggregates. When referring to crystal size for the ZSM-5 component of the catalyst of the present invention, we mean crystal size as determined in accordance with this Example. Example 5 Prior Art Low Pressure Xylene Isomerization Example Ten grams of ZSM-5 powder CBV 8020, 0.7 micron crystal size, were formed to particles of 20-40 mesh. 0.6 gm of the 20-40 mesh ZSM-5 particles were then mixed with alundum and charged to a 0.5-inch diameter reactor. After dehydrating the catalyst in an inert gas, namely, nitrogen, the nitrogen flow was discontinued and hydrocarbon feed was passed over the catalyst. For this example, Feed I was used. The feed composition is shown in Table II, above. Operating conditions included a pressure of 25 psig and a WHSV of 8.8 hr 1 . The WHSV was based on the zeolite component of the catalyst. The reactor effluent was sampled periodically by an in-line sampling system and analyzed by gas chromatography. The reactor temperature was adjusted to achieve a nominal ethylbenzene conversion of 30 wt. %. Results are shown in Table III. Two operating periods are shown, 26.9 and 71.8 hours on-stream (HOS), at a temperature of 636°F and 666°F, respectively. Note that the ethylbenzene conversion varied from 30.6 to 31.7 wt. %, and the xylene loss varied from 10.1 to 4.7 wt. %. This is a high xylene loss and results in an ethylbenzene conversion/xylene loss ratio which varied from 3.0 to 6.8. In addition, the paraxylene approach to equilibrium varied from 88-92%. In other words, the xylene isomerization was not complete as an equilibrium concentration of paraxylene was not reached. Indeed, at 71.8 HOS, the paraxylene concentration on a xylene basis is 22.71 versus the equilibrium value of 23.70 wt. %. Furthermore, note that the reactor temperature had to be increased at the rate of 1.5°F/hr in order to hold an ethylbenzene conversion of -30 wt. %. Example 6 The catalyst from Example 1 was tested in the same manner as described in Example 5 and using the same feed. Note that the catalyst from Example 1 is based on a ZSM-5 with a 0.7 micron crystal size. Following the catalyst dehydration step as in Example 5, the catalyst of this example was also treated in hydrogen at 950°F for one hour. Operating conditions in the reactor included a pressure of 35 psig and a WHSV, based on the modified zeolite, of 8.8 hr 1 . Hydrogen was added to the reactor on a once-through basis at a rate equivalent to a H 2 /ethylbenzene mole ratio of 1.2. This is equivalent to a H 2 /hydrocarbon feed mole ratio of 0.076. The ethylbenzene conversion target was 50 wt. %. Results at 26.0 hours on-stream are shown in Table III. Reactor temperature was increased until a temperature of 730°F was reached at which the ethylbenzene conversion was 49.8 wt. %. The xylene loss was 1.6 wt. %, to yield an ethylbenzene conversion/xylene loss ratio of 30.6/1. The Paraxylene Approach To Equilibrium was 101.3% based on a paraxylene concentration on a xylene basis in the reactor effluent of 23.72 wt. %. The concentration of C 9 + aromatics in the reactor effluent was 2.27 wt. %. This is well below the C 9 + aromatics concentration of 4.68 wt. % in Example 5, and is indicative that substantial ethylbenzene conversion is by hydrodealkylation and not disproportionation. Another advantage was that the deactivation rate or fouling rate of the catalyst was much less than in Example 5. The reactor temperature was increased at the rate of 0.2°F/hr to hold 50% ethylbenzene conversion in contrast to 1.5°F/hr in Example 5. The low rate of temperature increase shown by Example 6 is a surprising advantage achieved by the overall process conditions of the present invention, including the catalyst conditions. Table III These examples help illustrate the benefits of the present invention, including the following: 1. Ethylbenzene conversion by hydrodealkylation occurs in the process of the present invention at a low hydrogen partial pressure, i.e., low system pressure and low H 2 /ethylbenzene or H 2 /hydrocarbon feed mole ratio. 2. Ethylbenzene hydrodealkylation is effectuated in the process of the present invention at a lower xylene loss as evidenced by a lower C 9 + aromatics make. This is in contrast to the prior art low pressure xylene isomerization processes where ethylbenzene conversion is by disproportionation and results in high xylene losses and the formation of a higher C 9 + aromatics make. 3. The process of the present invention achieves reduced xylene losses. The net effect, when combined with ethylbenzene hydrodealkylation, is a much more xylene selective process. The ethylbenzene conversion/xylene loss ratio is 30.6 for the process of this invention compared to 3-7 for the standard prior art low pressure isomerization processes. At 50% ethylbenzene conversion, the process of this invention would result in a xylene loss of 1.6 wt. % compared to ~7 wt. % for the prior art low pressure processes. This is a substantial reduction in the xylene losses. 4. As illustrated by Example 6, the catalyst and other operating conditions achieve much higher catalyst stability (that is, low deactivation rate) than the catalyst stability of prior art low pressure xylene isomerization. Accordingly, the process of the present invention can be operated for a longer period of time before the catalyst needs to be regenerated. This advantage is important from a technical and operation viewpoint. Example 7 Comparison of the Present Invention to Catalyst Based on Lame Crystal Size ZSM-5 The catalyst of Example 3 was tested as described in Example 6 and with the same feed, namely, Feed I. The catalyst of Example 3 is a ZSM-5 made by Zeochem with a crystal size of 2.5 microns. This is in contrast to the ZSM-5 of Example 1 which has a crystal size of 0.7 microns. Results are shown in Table III. Reactor temperature was adjusted to 750°F, at which temperature the ethylbenzene conversion was 48.9 wt. %. Xylene loss was 1.4 wt. % to yield an ethylbenzene conversion/xylene loss ratio of 33.9. However, the Paraxylene Approach To Equilibrium was 87.3% based on a paraxylene concentration on a xylene basis in the reactor effluent of 21.98 wt. %. The equilibrium concentration of paraxylene is 23.53 wt. %. In addition, the catalyst was significantly less temperature stable than the catalyst of Example 6. This example shows that with a large crystal ZSM-5, operation at low pressure and low hydrogen partial pressure results in poor xylene isomerization performance, as the paraxylene is not isomerized to equilibrium as in Example 6 where the small crystal, 0.7 microns, ZSM-5 was used. However, with the large crystal ZSM-5, ethylbenzene conversion by hydrodealkylation is achieved as well as low xylene losses. Example 8 Performance Comparison of a Bound Extrudate The catalyst of Example 2 was tested in the same manner as in Example 6 to demonstrate the process of the invention with a bound commercial extrudate as the starting base, namely, CBV 8062. Note that the crystal size of the ZSM-5 contained in CBV 8062 is 0.54 microns. Since this material is a bound extrudate and contains 80% zeolite and 20% binder, 0.75 grams (14-28 mesh particle size) of the catalyst from Example 2 was charged to the reactor. This equates to 0.6 gm of zeolite and is equivalent to the quantity of zeolite charged to the reactor in Example 6. This maintains the same WHSV based on the zeolite of 8.8 hr 1 as in Example 6. The feed used in this example was Feed II with the composition shown in Table II. This catalyst was tested over a 500-hour period at a nominal ethylbenzene conversion of 50 wt. %. Results at three different points during the run are shown in Table IV. Table IV The results of this example show achievement of high levels of ethylbenzene conversion at a low hydrogen partial pressure, i.e., low system pressure and low H 2 /HC feed mole ratio. In addition, while achieving these levels of ethylbenzene conversion, the xylene losses are very low, resulting in an ethylbenzene conversion/xylene loss ratio of 20-26. The xylenes isomerized to equilibrium. In particular, the paraxylene is isomerized to slightly better than equilibrium, so that the Paraxylene Approach To Equilibrium (PXAPE) is between 102.7 and 105.4%. The PXAPE is defined as the paraxylene concentration in the reaction zone effluent minus the paraxylene concentration in the feed divided by the paraxylene concentration at equilibrium (under the temperature and pressure used in the reaction zone) minus the paraxylene concentration in the feed, where all the concentrations are based on xylenes only. In addition, as in Example 6, the catalyst stability achieved in the above examples is improved relative to Example 5. In this case, reactor temperature was increased at a rate between 0.05 and 0.10°F/hr to maintain a nominal ethylbenzene conversion of 50 wt. %. In Example 5, the temperature increase was at the rate of 1.5°F/hr.

Claims: WHAT IS CLAIMED IS: 1. A process for the hydrodealkylation of ethylbenzene and the isomerization of xylenes, comprising contacting, in a reaction zone, a hydrocarbon feed containing ethylbenzene and xylenes, with a catalyst comprising ZSM-5, a Group VIII metal, and a further element selected from magnesium, sodium, barium, potassium, calcium, zinc or phosphorus, wherein the paraxylene content of the xylenes in the feed is less than an equilibrium amount, the contacting is carried out in the presence of gaseous hydrogen, and the ZSM-5 has a crystal size less than 1.0 micron; to thereby hydrodealkylate ethylbenzene to produce benzene and isomerize xylenes to produce paraxylene. 2. A process in accordance with Claim 1 wherein the ZSM-5 crystal size is less than 0.8 microns. 3. A process in accordance with Claim 2 wherein the Group VIII metal is platinum. 4. A process in accordance with Claim 3 wherein the further element is magnesium. 5. A process in accordance with Claim 1 wherein reaction conditions in the reaction zone comprise a temperature of 500°F to 1000°F, a pressure of 0 to 200 psig, a WHSV of 2 to 20, and a hydrogen to ethylbenzene feed mole ratio of 0.2 to 10.0. 6. A process in accordance with Claim 5 wherein the ZSM-5 is predominantly in the hydrogen form. 7. A process in accordance with Claim 1 wherein the feed comprises at least 70 wt. % C 8 aromatics. 8. A process in accordance with Claim 4 wherein the catalyst contains 0.05 to 5 wt. % platinum, 0.5 to 5 wt. % magnesium, and the ZSM-5 crystal size is less than 0.8 microns. 9. A process in accordance with Claim 1 where the reaction zone pressure is below 100 psig, the hydrogen to ethylbenzene mole ratio is between 0.4 and 8, the ZSM-5 crystal size is between 0.1 and 0.8 microns, the ethylbenzene content of the reaction zone effluent is reduced by at least 50% compared to the ethylbenzene content in the feed, and the xylenes are isomerized in the reaction zone so that the paraxylene content is greater than 90% of its equilibrium value on a xylene basis. 10. A process in accordance with Claim 9 wherein the ethylbenzene conversion to xylene loss ratio is greater than 20. 11. A process in accordance with Claim 9 wherein the pressure is 10 to 50 psig. 12. A process in accordance with Claim 9 wherein the hydrogen to ethylbenzene mole ratio is between 1 and 5.

Inventors: NACAMULI GERALD J, VOGEL ROGER F, NACAMULI, GERALD, J., VOGEL, ROGER, F.
Applicants: CHEVRON CHEM CO, CHEVRON CHEMICAL COMPANY LLC
Application year: 1998
Main classification: C07C15
IPC codes: C07C4, C07C5