IMPROVEMENT IN AQUEOUS STRIPPING AND CLEANING COMPOSITIONS

Abstract: An aqueous stripping composition comprising a mixture of a polar amine, an organic or inorganic amine and a corrosion inhibitor which is gallic acid, its ester or analog. The stripping composition is effective to strip photoresists, residues from plasma process generated organic, metal-organic materials, inorganic salts, oxides, hydroxides or complexes in combination with or exclusive of organic photoresist films at low temperatures without redepositing any susbtantial amount of metal ions.

Description: IMPROVEMENT IN AQUEOUS STRIPPING AND CLEANING COMPOSITIONS Background of the Invention Field of the Invention This invention relates to an improvement in aqueous stripping compositions particularly useful for stripping paints, varnishes, enamels, photoresists and the like, from various substrates. More particularly, the invention relates to improved aqueous stripping compositions comprising polar solvents and organic or inorganic amines by providing a corrosion inhibitor which is gallic acid or a gallic acid ester. The compositions do not include hydroxylamine. Description of the Prior Art Stripping compositions used for removing coatings from substrates have for the most part been highly flammable compositions, compositions generally hazardous to both humans and the environment and compositions which are reactive solvent mixtures evidencing an undesirable degree of toxicity. Moreover, these stripping compositions are not only toxic but their disposal is. costly since they must be disposed of as a hazardous waste. In addition, these stripping compositions generally have severely limited bath life and, for the most part, are not recyclable or reusable . Generally, compositions containing chlorinated hydrocarbons and/or phenolic compounds or other highly caustic and corrosive materials have been employed as stripping compositions for stripping paints, varnishes, lacquers, enamels, photoresists, powder coatings and the like, from substrates such as wood, metal or silicon wafers . Hot caustic compositions are generally employed to remove coatings from metals and methylene chloride compositions to remove coatings from wood. In many cases, the components of the stripping compositions are relatively toxic reactive solvent mixtures and thus must be subject to stringent use conditions and require hazardous chemical handling procedures and wearing of safety garments and apparel by users so as to avoid contact with the stripping compositions. Additionally, because many of the toxic components of such stripping compositions are highly volatile and subject to unduly high evaporation rates, the stripping compositions require special human and environmental safety precautions to be taken during ■ storage and use of said compositions . In photoresist stripping with the use of hydroxylamine and an amine solvent there is the problem with the substrate of titanium etching and aluminum etching. It is therefore desirable to provide 7013-23 2 a corrosion inhibitor so that such compositions can be used on a various kinds of photoresists. U.S. Patent No. 4,276,186 to Bakos et al discloses a cleaning composition which includes N-methyl-2-pyrrolidone and an alkanolamine . However, in a comparative study, applicant has found that the use of N-methyl-2-pyrrolidone does not provide a broad spectrum of cleaning as is capable with the composition of the invention. U.S. Patent No. 4,617,251 to Sizensky discloses a stripping composition which is prepared with a select amine and an organic polar solvent. The composition is formed utilizing from about 2 to about 98% by weight of amine compound and about 98 to about 2% of an organic polar solvent. U.S. Patent No. 4,770,713 to Ward discloses a stripping composition comprising an alkylamine and an alkanol amine. U.S. Patent No. 5,419,779 ' to Ward discloses a process for removing an organic coating from a substrate by applying a composition consisting of about 62% by weight of monothanolamine, about 19% by weight hydroxyl mine, a corrosion inhibitor which includes gallic acid and gallic acid esters, and water. U.S. Patent No. 5,496,491 to Ward, which is incorporated herein by reference, discloses a photoresist stripping composition comprising a basic amine, a polar solvent and an inhibitor which is the reaction product of an alkanolamine and a bicyclic compound. However, gallic acid and gallic acid esters are not disclosed as inhibitors . 7013-23 3 U.S. Patent Nos . 5,334,32 and 5,275,771 to Lee disclose a composition containing hydroxylamine, an alkanolamine and a chelating agent. However, the chelating agent is not gallic acid or its esters. U.S. Patent No. 5,597,420 to Ward discloses a stripping composition free of hydroxylamine compounds which consists essentially of monoethanolamine and water together with a corrosion inhibitor. The inhibitor includes gallic acid and its esters. Recently, OSKA, EPA and other similar federal, state and local governmental regulatory agencies have advocated a shift toward use of more human and environmentally compatible stripping compositions and stripping methods that are not subject to the aforementioned drawbacks and problems . Moreover, heretofore available photoresist stripping compositions have required unduly long residence times or repeated applications in order to remove certain coatings. In addition, various coatings have resisted removal from certain substrates with these heretofore available stripping compositions. That is, these previously available stripping compositions have not provided adequate or complete removal of certain hard-to-remove coatings from various substrates . It is, therefore, highly desirable to provide stripping compositions that exhibit substantially no human or environmental toxicity, are water miscible and are biodegradable. It is also desirable to provide stripping compositions that are substantially non-flammable, non-corrosive, evidence relatively little, if any, 7013-23 4 tendency to evaporate and are generally unreactive and also of little toxicity to humans and are environmentally compatible. Moreover, it would be desirable to provide photoresist stripping compositions that have a high degree of stripping efficacy and particularly such high degree of stripping at lower temperatures than generally required with prior stripping compositions . It is also highly desirable that photoresist stripping compositions be provided that exhibit substantially no corrosive effects on the substrate, especially those containing titanium and/or aluminum or silicone. It is also desirable that effective stripping compositions be provided that are devoid of undesirable chlorinated or phenolic components and which do not require the use of hot caustic components. Highly desirable are stripping compositions and use thereof that are not considered undesirable by regulatory agencies overseeing their production and use. It is also most advantageous that stripping compositions be provided with the above-identified desirable characteristics which evidence synergistic stripping action in that the mixtures of components provide stripping efficacy and stripping results not always obtainable with the individual components for the removal of sidewall organometallic and metal oxide residues. Summary of the Invention It has now been found that a suitable stripping and cleaning composition in which the hereinbefore mentioned disadvantages or 7013-23 5 drawbacks of corrosion are eliminated or substantially reduced and in which the range of usefulness of the stripping compositions is greatly extended can be obtained in accordance with the teachings of the present invention. In a stripping composition containing the admixture of water, a soluble polar solvent and an organic or inorganic amine, the improvement which comprises in admixture therewith an effective amount of corrosion inhibitor which is a compound of the general formula: wherein R is hydrogen or lower alkyl . The corrosion inhibitor is believed to form a 5-or 6- membered ring coordination complex with the substrate. Gallic acid is a more effective inhibitor than catechol because it is a more effective oxygen scavenger and has more sites for ligand attachment. That is, gallic acid has more effective covalent bonds. A preferred amount of inhibitor is about 0.1 to 10% by weight. The compositions can be non-aqueous or can include water. The novel stripping compositions of the invention exhibit synergistically enhanced stripping action and stripping capabilities at low temperatures not possible from the use of the individual components or in combination with other stripping components such as N-methylpyrrolidone or alkylamides without the occurrence of corrosion. 7013-23 6 The stripping compositions of the invention with the corrosion inhibitor provide an effective stripping action as well as prevent metal ion redeposition, for example, alkaline earth and alkali metal ion redeposition on the substrate. It is a general object of the invention to provide a non- corroding stripping composition which is effective at low temperatures . It is another object of the invention to provide a photoresist stripping composition which is non-corrosive especially of aluminum and silicone. It is a further object of the invention to provide a photoresist stripping composition which inhibits redeposition of metal ions. It is still another object of the invention to provide an inhibitor which is less expensive and is more effective as a corrosion inhibitor than catechol . It is yet another object of the invention to provide a method for stripping a coated substrate which can be accomplished at low temperatures which does not cause redeposition of metal ions. Other objects and advantages of the present invention will be more fully understood in view of the accompanying drawing and a description of the preferred embodiments. Brief Description of the Drawing Figures 1A-2C show a SEM comparison between a formulation of the invention with gallic acid and a similar formulation with catechol . 7013-23 7 Detailed Description of the Preferred Embodiments The stripping compositions of the invention preferably comprise an admixture of a polar solvent and an organic or inorganic amine in combination with about 0.1 to 10% by weight of a corrosion inhibitor which is a compound of the general formula: wherein R is hydrogen or lower alkyl . A preferred photoresist stripping composition consists of about 58 to 63% by weight of N-monoethanolamine, about 30 to 40% by weight of dimethyl sulfoxide, about 1 to 4% by weight of gallic acid and water. If desired, up to about 5% by weight of anthranilic acid may also be added as a corrosion inhibitor. The polar solvents which can be used in the present invention include and are not limited to water, polyhydric alcohols, for example, propylene glycol , glycol , glycerol , polyethylene glycol, and the like, dimethylsulfoxide (DMSO) , butyrolactones , glycol ethers, N-alkyl pyrolidones, for example N-methyl pyrrolidone, tetrahydrofuran (THF) glycol ethers including diethylene glycol monoalkyl ether, ethylene diamine, ethylenetriamine , dimethylacetamide (DMAC) , and the like. The amines which can be used in the present invention include but are not limited to tetralkylammonium hydroxide, a diamino or an 7013-23 8 amino hydroxy compound such as described in U.S. Patent Nos . 4,765,844 and 4,617,251 which are herein incorporated by reference, alkanolamines, which are primary, secondary or tetiary having from 1 to 5 carbon atoms, morpholine, N-methylaminoethanol, and the like. Optional ingredients includes surfactents . The stripping compositions of this invention are especially useful and advantageous for numerous reasons among which may be mentioned the following. The stripping compositions are water soluble, non-corrosive, non-flammable and of low toxicity to the environment. The stripping compositions evidence higher stripping efficiency at low temperatures for a wide variety of coatings and substrates. They are particularly suitable for removal of photoresists and residues from plasma processing used in integrated circuit fabrication since they also prevent the redeposition of metal ions, especially sodium and potassium ions. The stripping compositions are easily prepared by simply mixing the components at room temperature. The method of the invention is carried out by contacting an organic or metal -organic polymer, inorganic salt, oxide, hydroxide or complex or combination thereof as a film or residue, (i.e. sidewall polymer (SWP) ) . with the described stripping composition. The actual conditions, i.e., temperature, time, etc. depend on the nature and thickness of the complex (photoresist and/or sidewall polymer) material to be removed, as well as other factors familiar to those skilled in the art. In general, for photoresist stripping, the photoresist is contacted or dipped into a vessel 7013-23 9 containing the stripping composition at a temperature between 25- 75oC for a period of about 5-30 minutes, washed with water and then dried with an inert gas . Examplificative organic polymeric materials include photoresists, electron beam resists, X-ray resists, ion beam resists, and the like. Specific examples of organic polymeric materials include positive resists containing phenolformaldehyde resins or poly (p-vinylphenol) , polymethylmethacrylate-containing resists, and the like. Examples of plasma processing residues (sidewall polymer) include among others; metal-organic complexes and/or inorganic salts, oxides, hydroxides or complexes which form films or residues either alone or in combination with the organic polymer resins of a photoresist. The organic materials and/or SWP can be removed from conventional substrates known to those skilled in the art, such as silicon, silicon dioxide, aluminum, aluminum alloys, copper, copper alloys, etc. The effectiveness and unexpected nature of the stripping compositions of the invention is illustrated, but not limited by, the data presented in the following examples . Unless otherwise specified, all parts and percentages are by weight. Example 1 In order to demonstrate the efficiency of the different concentrations of the stripping and cleaning compositions the following tests were conducted. Metal/silicon wafer substrates containing commercial photoresists and plasma generated SWP residues labeled as "veils" 7013-23 10 were post-baked at 180°c for 60 minutes. The substrates were cooled and dipped into vessels containing a stripping composition and stirred with a magnetic stirrer. There was a vessel containing a stripping composition maintained at a temperature of 50 oc and another at 55oC. The contact time with the compositions was 20 to 30 minutes. The substrates were washed with deionized water and dried with nitrogen. The results were determined by optical microscopy and scanning electron microscopy inspection and were as follows : Example 1 % Wt Sample No. Results Sample 3 showed severe corrosion in VIAS at 75 oC. Sample 1, 3 and 5 in VIAS at 75% showed some SWP residue or corrosion. Samples 2, 4 and 7 showed better inhibitor performance against aluminum etching than other samples . 7013-23 11 Figures 1A-1C show the stripping results of composition 5 or a photoresist at 90 °C and Figures 2A-2C show the results of composition 7 on a photoresist under the same conditions. Example 2 The following stripping and cleaning compositions were prepared and tested according to the test of Example 1. % Polymeric Composition 1 Time (min) Temp. ,oC Removal Corrosion Monoethanolamine 60% 20 65 100 No DMAC 18.5% 20 90 100 No Water 18.5% Catechol 5% Composition 2 AEE 60% 20 65 100 No NNP 18.5% 20 90 100 P i ffirg Water 18.5% Catechol 5% % Polymeric Composition 3 Time (min) Temp. oC Removal Cor:rosion AEE 60% 20 65 100 No NMP 18.5% 20 90 100 No Water 18.5% Gallic Acid 5% Composition 4 Tetramethyl ammonium hydroxide 9.7° 20 65 100 ELtt±g Pentahydrate (TMAH) 20 90 100 PitTrg Dipropyleneglycol monoethylether 21.0° DMSO 69.3° % Polymeric Composition 5 Time (min) Temp. oC Removal Co:rrosion TMAH 9.7% 20 65 100 No Dipropyleneglycol 20 90 100 No monoethylether 21.0% DMSO 65.0% Gallic Acid 4.3% 7013-23 12

Claims: What is Claimed is: 1. In a stripping and cleaning composition comprising an admixture of water soluble polar solvent and an organic or inorganic amine, the improvement which comprises the admixture with an effective amount of a corrosion inhibitor of the general formula : COOR (I) HO OH OH wherein R is lower alkyl or hydrogen. 2. The stripping and cleaning composition of claim 1 wherein said corrosion inhibitor comprises about 0.1 to 10% by weight. 3. The stripping and cleaning composition of claim 1 including water. 4. The stripping and cleaning composition of claim 1 comprising about 58 to 63% by weight of N-monoethanolamine, about 30 to 40% by weight of dimethyl sulfoxide, about 1 to 4% by weight of gallic acid and the remainder being water. 5. The stripping and cleaning composition of claim 1 including up to about 5% by weight of anthranilic acid. 6. The stripping and cleaning composition of claim 1 wherein said polar solvent is dimethylsulfoxide . 7. The stripping and cleaning composition of claim 1 wherein said polar solvent is dimethylacetamide . 8. The stripping and cleaning composition of claim 1 wherein the polar solvent and the organic amine are the same . 7013-23 13 6. The stripping and cleaning composition of claim 1 wherein said polar solvent is dimethylsulfoxide . 7. The stripping and cleaning composition of claim 1 wherein said polar solvent is dimethylacetamide. 8. The stripping and cleaning composition of claim 1 wherein the polar solvent and the organic amine are the same. 9. The stripping composition of claim 1 wherein said inhibitor includes anthranilic. 10. A process for removing a coating from a coated substrate comprising applying to said coated substrate a stripping and cleaning effective amount of the composition of claim 1, permitting said stripping composition to reside on said coated substrate for a stripping effective period of time and removing the coating from said substrate. 11. A process for removing a coating from a coated substrate comprising applying to said coated substrate a stripping and cleaning effective amount of the composition of claim 3, permitting said stripping composition to reside on said coated substrate for a stripping effective period of time and removing the coating from said substrate. 7013-23 14 12. A process for removing a coating from a coated substrate comprising applying to said coated substrate a stripping and cleaning effective amount of the composition of claim 8, permitting said stripping composition to reside on said coated substrate for a stripping effective period of time and removing the coating from said substrate.

Inventors: MICHELOTTI FRANK W, WARD IRL E, MICHELOTTI, FRANK, W., WARD, IRL, E.
Applicants: ASHLAND INC, ASHLAND INC.
Application year: 1998
Main classification: B08B3
IPC codes: B08B3, C09D9, C11D3, C11D7, C11D11, C23G5, G03F7