TIN ALLOY ELECTRODE COMPOSITIONS FOR LITHIUM BATTERIES

Abstract: An electrode composition that includes (a) an electrochemically active metal element which, prior to cycling, is in the form of an intermetallic compound or an elemental metal and (b) a non-electrochemically active metal element. The electrode compositions have high initial capacities that are retained even after repeated cycling. The electrode compositions also exhibit high coulombic efficiencies.

Description: TIN ALLOY ELECTRODE COMPOSITIONS FOR LITHIUM BATTERIES This invention relates to electrode compositions useful in secondary lithium batteries Two classes of materials have been proposed as anodes for secondary lithium batteries One class includes materials such as graphite and carbon which are capable of intercalating lithium While the intercalation anodes generally exhibit good cycle life and coulombic efficiency, their capacity is relatively low A second class includes metals that alloy with lithium metal Although these alloy-type anodes generally exhibit higher capacities relative to intercalation-type anodes, they suffer from relatively poor cycle life and coulombic efficiency The invention provides electrode compositions suitable for use in secondary lithium batteries in which the electrode compositions have high initial capacities that are retained even after repeated cycling The electrode compositions also exhibit high coulombic efficiencies The electrode compositions, and batteries incorporating these compositions, are also readily manufactured To achieve these objectives, the invention features, in a first aspect, an electrode composition that includes (a) an electrochemically active metal element and (b) a non- electrochemically active metal element When incorporated in a lithium battery and cycled through one full charge-discharge cycle, the composition includes crystalline regions having at least one dimension that is no greater than about 500 angstroms (preferably no greater than about 100 angstroms, more preferably no greater than about 50 angstroms) and that does not substantially increase after a total of at least 10 cycles (preferably at least 100 cycles, more preferably at least 1000 cycles) The crystalline regions may be present prior to cycling or may appear only after one full charge-discharge cycle In the former case, the regions persist after one full charge-discharge cycle An "electrochemically active metal element" is an element that reacts with lithium under conditions typically encountered duπng charging and discharging in a lithium battery A "non-electrochemically active metal element" is an element that does not react with lithium under those conditions In both cases, the metal element may be found in the electrode composition in the form of a metal containing only the element itself (l e . an elemental metal) or a compound containing the element in combination with one or more elements which may or may not be metal elements An example of the latter is an intermetallic compound containing the metal element in combination with one or more metal elements Prior to cvchng. however, the electrochemically active metal element is in the form of an intermetallic compound or an elemental metal Where the electrochemically active metal element is part of a compound, the compound itself need not be electrochemically active, although it may be Similarly, where the non- electrochemically active metal element is part of a compound, the compound itself need not be non- electrochemically active although it may be - 2 - An example of a preferred electrochemically active metal element is tin Examples of preferred non-electrochemically active metal elements include molybdenum, niobium, tungsten, tantalum, iron, copper, and combinations thereof Particularly preferred electrode compositions are those in which (a) the electrochemically active metal element is tin and the non-electrochemically active metal element is molybdenum, (b) the electrochemically active metal element is tin and the non-electrochemically active metal element is iron, (c) the electrochemically active metal element is tin and the non-electrochemically active metal element is niobium, (d) the electrochemically active metal element is tin and the non-electrochemically active metal element is tungsten, and (e) the electrochemically active metal element is tin and the non-electrochemically active metal element is tantalum The crystalline regions are characterized by a discernible x-ray diffraction pattern characteristic of a crystalline material In terms of chemical composition, at least one of the crystalline regions preferably includes the electrochemically active metal element and at least another of the crystalline regions includes the non-electrochemically active metal element The crystalline regions are preferably separated by regions comprising the electrochemically active metal element and the non-electrochemically active metal element in which the relative proportions of the these elements vary throughout the thickness direction of the composition For cases in which the electrode composition is in the form of a thin film, the "thickness direction of the composition" refers to the direction perpendicular to the substrate on which the film is deposited Where the electrode composition is in the form of a powder representing a collection of individual particles, the "thickness direction of the composition" refers to the thickness direction of an individual particle The regions separating the crystalline regions do not exhibit an electron diffraction pattern characteristic of a crystalline material They may be present prior to cycling, after cycling, or both before and after cycling When the electrode composition is incorporated in a lithium battery and cycled to realize about 100 mAh/g of electrode composition, the electrode composition preferably exhibits a coulombic efficiency of at least about 99 0% (more preferably at least about 99 8%, even more preferably about 99 9%) after 100 full discharge cycles The electrode composition may be provided in the form of a thin film or a powder In a second aspect, the invention features an electrode composition that includes (a) an electrochemically active metal element and (b) a non-electrochemically active metal element When incorporated in a lithium battery and cycled through one full charge-discharge cycle, the composition includes crystalline regions In addition, when incorporated in a lithium battery and cycled to realize about 100 mAh/g of electrode composition, the electrode composition exhibits a coulombic efficiency of at least about 99 0% (preferably at least about 99 8%, more preferably at least about 99 9%) after 100 full discharge cycles - 3 - The crystalline regions may be present prior to cycling or may appear only after one full charge-discharge cycle In the former case, the regions persist after one full charge-discharge cycle The electrochemically active metal element and non-electrochemically metal element have the definitions described above In both cases, the metal element may be found in the electrode composition in the form of a metal containing only the element itself (I e , an elemental metal) or a compound containing the element in combination with one or more elements which may or may not be metal elements An example of the latter is an intermetallic compound containing the metal element in combination with one or more metal elements Prior to cycling, however, the electrochemically active metal element is in the form of an intermetallic compound or an elemental metal The electrode composition may be provided in the form of a thin film or a powder An example of a preferred electrochemically active metal element is tin Examples of preferred non- electrochemically active metal elements include molybdenum, niobium, tungsten, tantalum, iron, copper, and combinations thereof Particularly preferred electrode compositions are those in which (a) the electrochemically active metal element is tin and the non-electrochemically active metal element is molybdenum, (b) the electrochemically active metal element is tin and the non- electrochemically active metal element is iron, (c) the electrochemically active metal element is tin and the non-electrochemically active metal element is niobium, (d) the electrochemically active metal element is tin and the non-electrochemically active metal element is tungsten, and (e) the electrochemically active metal element is tin and the non-electrochemically active metal element is tantalum The crystalline regions are characterized by a discernible x-ray diffraction pattern In terms of chemical composition, at least one of the crystalline regions preferably includes the electrochemically active metal element and at least another of the crystalline regions includes the non-electrochemically active metal element The crystalline regions are preferably separated by regions comprising the electrochemically active metal element and the non-electrochemically active metal element in which the relative proportions of the these elements vary throughout the thickness direction of the composition (as defined, above) These regions separating the crystalline regions exhibit no discernible electron diffraction pattern characteristic of a crystalline material They may be present prior to cycling, after cycling, or both before and after cycling In a third aspect, the invention features a method of preparing an electrode composition that includes combining (a) a source comprising an electrochemically active metal element and (b) a source comprising a non-electrochemically active metal element to form an electrode composition characterized in that (I) when incorporated in a lithium battery and cycled through one full charge-discharge cycle, the electrode composition includes crystalline regions and - 4 - (n) when incorporated in a lithium battery and cycled to realize about 100 mAh/g of the composition, the electrode composition exhibits a coulombic efficiency of at least about 99 0% after 100 full discharge cycles In one preferred embodiment, the source of the electrochemically active metal element and the source of the non-electrochemically active element are sequentially sputter-deposited onto a substrate In another preferred embodiment, the two sources are combined by ball milling The above-described electrode compositions may be combined with a counterelectrode and an electrolyte separating the electrode and counterelectrode to form a lithium battery Other features and advantages of the invention will be apparent from the following description of the preferred embodiments thereof, and from the claims Fig 1 illustrates the cycling performance, in terms of reversible specific capacity (top graph) and coulombic efficiency (bottom graph), of a sputter-deposited tin-molybdenum electrode having 54 wt % tin and 46 wt % molybdenum Fig 2 illustrates the cycling performance, in terms of reversible specific capacity (top graph) and coulombic efficiency (bottom graph), of a sputter-deposited tin-molybdenum electrode having 54 5 wt % tin and 45 5 wt % molybdenum Fig 3 illustrates the cycling performance, in terms of reversible specific capacity (top graph) and coulombic efficiency (bottom graph), of a sputter-deposited tin-molybdenum electrode having 45 wt % tin and 55 wt % molybdenum Fig 4 illustrates the cycling performance, in terms of reversible specific capacity (top graph) and coulombic efficiency (bottom graph), of a sputter-deposited tin-niobium electrode having 65 5 wt % tin and 34 5 wt % niobium Fig 5 illustrates the cycling performance, in terms of reversible specific capacity (top graph) and coulombic efficiency (bottom graph), of a sputter-deposited tin copper electrode having 55 2 wt % tin and 44 8 wt % copper Fig 6 illustrates the cycling performance, in terms of reversible specific capacity (top graph) and coulombic efficiency (bottom graph), of a sputter-deposited tin-tungsten electrode having 43 7 wt % tin and 56 3 wt % tungsten Fig 7 illustrates the cycling performance, in terms of reversible specific capacity (top graph) and coulombic efficiency (bottom graph), of a full cell featuring a sputter-deposited tin- molybdenum anode having 54 wt % tin and 46 wt % molybdenum and a LιCoOτcontaιmng cathode Fig 8 is a series of x ray diffraction profiles for a tin-molybdenum film having 54 wt % tin and 46 wt % molybdenum obtained after 0, 1, 4, and 10 cycles Fig 9 reports the results of an m-situ x-ray diffraction experiment involving a tin metal electrode and an Sn 2 Fe electrode - 5 - Fig 10 is an electron diffraction pattern of the tin-molybdenum film that is the subject of Fig 1 The invention features electrode compositions that are particularly useful as anodes for secondary lithium batteries The electrode compositions feature an electrochemically active metal element and a non-electrochemically active metal element combined in a microstructure which, the inventors have discovered, results in an electrode composition that exhibits a high initial capacity that is substantially retained after repeated cycling An example of a suitable electrochemically active metal element is tin Examples of suitable non-electrochemically active metal elements are molybdenum, niobium, tungsten, tantalum, iron, copper, and combinations thereof, with molybdenum being particularly preferred These elements may be present in the form of single element metals, intermetallic compounds, or compounds featuring the metal element combined with one or more non-metallic elements In addition, the particular form in which the element is present may change over the course of repeated cycling For example, alloys may form with other material present in the electrode composition For optimum performance, however, the electrochemically active metal element is present in the form of an elemental metal (e g , tin metal) or as an intermetallic compound prior to cycling The microstructure of the electrode composition is characterized by the presence of small crystalline regions These regions give rise to x-ray and electron diffraction patterns characteristic of crystalline material In some embodiments, e g , in the case of some compositions prepared by sputtering, these regions are present prior to cycling and remain after at least one full charge-discharge cycle In other embodiments, e g , in the case of some compositions prepared by ball milling, these regions form only after the composition has been through one full charge- discharge cycle The crystalline regions are very small, three-dimensional structures characterized by x- , y-, and z-dimensions At least one of these dimensions is no greater than about 500 angstroms (preferably no greater than about 100 angstroms, more preferably no greater than about 50 angstroms), determined from examination of transmission electron micrographs of the material Upon cycling, this dimension does not substantially increase after a total of at least 10 cycles (preferably at least 100 cycles, more preferably at least 1000 cycles) The crystalline regions, therefore, remain very small even after repeated cycling It is believed that this property contributes to the ability of the electrode composition to substantially retain its initial capacity after repeated cycling Within a given electrode composition, there are preferably crystalline regions that contain the electrochemically active metal element and separate crystalline regions that contain the non-electrochemically active metal element For example, in the case of a sputter-deposited tin- molybdenum electrode composition, prior to cycling there may be crystalline regions containing tin metal and crystalline regions containing molybdenum metal - 6 - The crystalline regions are preferably separated by regions that, when examined by transmission electron microscopy, do not give rise to an electron diffraction pattern characteristic of a crystalline material Specifically, these regions do not exhibit the relatively sharp rings or spots characteristic of a crystalline material In addition, high resolution electron microscopy, which can provide structural information on an atomic (2 angstrom) scale, likewise failed to detect the presence of crystalline material Based upon electron microscopy data, these regions can be described as containing material of a highly disordered atomic arrangement on a length scale no greater than about 20 angstroms, preferably no greater than about 10 angstroms Compositional analysis using x-ray microanalysis (also referred to as x-ray energy dispersive spectroscopy) of these regions reveals that they contain both the electrochemically active metal element and the non-electrochemically active metal element, and that the relative proportions of these two elements vary throughout the thickness direction of the sample We refer to this feature as "composition modulation " The composition preferably varies on a scale no greater than about 50 angstroms, preferably no greater than about 20 angstroms Composition modulation may be present before and/or after cycling, as long as crystalline regions are also present It is believed that the presence of these composition modulated areas contributes to the ability of the electrode to retain its capacity after cycling because these areas are more flexible than the crystalline areas, enabling the composition as a whole to dissipate cycling-induced stresses that would otherwise cause the electrode to crack and fail The electrode compositions may be prepared in the form of thin films or powders according to a variety of methods Examples include sputtering, chemical vapor deposition, vacuum evaporation, melt spinning, splat cooling, spray atomization, and ball milling The choice of technique determines whether the electrode composition is prepared in the form of a thin film or a powder Sputtering, for example, produces the electrode composition in the form of a thin film, whereas ball milling produces the electrode composition in the form of a free flowing powder which can then be combined with, e g , a polymeric binder to form an electrode suitable for incorporation in a battery The preferred process for preparing the electrode composition is sputtering in which the electrochemically active metal element and the non-electrochemically active metal element are sequentially sputter-coated onto a substrate (e g , a copper substrate) Preferably, the electrode includes a sputter-deposited prelayer of one of the elements and a sputter-deposited overlayer of one of the elements In general, the substrates are placed near the edge of a nominally 25 inch diameter turntable which rotates continuously below two 6 inch diameter magnetron sputtering sources operated continuously A layer of one material is deposited as the substrate passes under the first source, and a layer of the second material is deposited as the substrate passes under the second source By knowing the rotation speed of the turntable and the sputtering rates of the two sources, the nominal thickness of each layer can be predicted and controlled By calculating the total - 7 - deposition time, the thickness of the entire sample, and the number of individual layers, can be determined In the case of samples having very thin individual layers, the final structure may not contain evidence of a layered structure On the other hand, evidence of a layered structure may be found in the case of thicker layers The electrode compositions are particularly useful as anodes for secondary lithium batteries To prepare a battery, the electrode is combined with an electrolyte and a cathode (the counterelectrode) The electrolyte may be a solid or liquid electrolyte Examples of solid electrolytes include polymeric electrolytes such as polyethylene oxide, polytetrafluoroethylene, fluorine-containing copolymers, and combinations thereof Examples of liquid electrolytes include ethylene carbonate, diethylene carbonate, propylene carbonate, and combinations thereof The electrolyte is provided with a lithium electrolyte salt Examples of suitable salts include LiPFβ, L1BF4, and L1CIO4 Examples of suitable cathode compositions for liquid electrolyte-containing batteries include L1C0O2, L1C002N108O2, and Lii 07-vInι 93O4 Examples of suitable cathode compositions for solid electrolyte-containing batteries include L1V 3 O8 and L1V2O 5 The invention will now be described further by way of the following examples EXAMPLES A. Electrode Compositions Prepared By Sputtering A series of electrodes films was prepared by sputtering and, in some instances, characterized according to the following general procedures Sputtering Procedure Electrode compositions in the form of thin films were prepared by sequential sputtering using a modified Perkin-Elmer Randex Model 2400-8SA Sputtering System The original 8 inch diameter rf sputter sources were replaced with 6 inch diameter dc magnetron sputtering sources commercially available from Materials Science of San Diego CA The sputtering sources were powered using Advanced Energy Model MDX-10 dc sputtering power supplies operating in constant current mode The turntable drive unit of the Randex System was replaced with a stepper motor to improve rotation speed range and control The System was pumped with an untrapped oil diffusion pump backed by a conventional rotary vane pump Sputtering was performed at argon pressures in the range of 3-30 mTorr The pressure was maintained by controlling the argon flow in combination with a Venetian blind-style conductance limiter placed over the diffusion pump A copper foil (thickness = 0 001 inch) was bonded to the water-cooled substrate turntable of the Randex System using double sided adhesive tape (3M Brand Y9415, commercially - 8 - available from 3M Company of St Paul, MN) The system was closed and pumped down, typically to base pressures below 1 x 10 Torr (the base pressure prior to deposition is not critical) In some cases, the samples were etched prior to deposition using the "Sputter Etch" mode of the Randex System with 13 56 MHz power applied to the substrate turntable and an argon pressure of 8 mTorr in the sputtering chamber This procedure caused the copper foil surface to be bombarded with moderate energy argon ions (100-150 eV) to further clean the copper and insure good adhesion of the sputtered film to the copper surface A typical cleaning cycle was 150W for 30 minutes, with the substrate table rotating during the cycle Following etching, the sputtering sources were started up using a mechanical shutter between the sources and the copper substrate This removed contaminants from the source surface without depositing them on the substrate surface Next, a "pre-layer" made of a single material of known identity was deposited onto the substrate The purpose of the pre-layer was to insure good adhesion between the substrate and the sputter deposited film Next, both sources were started up at pre-determined current levels and deposition initiated After a suitable deposition time, one or both sources were turned off A "post-layer" of a single material of known identity was then deposited, after which the system was vented and the sample removed Seven films (corresponding to Examples 1-7) were prepared following the above- described procedure Sputtering conditions are summarized in Table I, below In Table I, "current" refers to the current level, in amps, of the individual sputtering source "Pressure" refers to the argon pressure, in mTorr, in the sputtering chamber "Run time" refers to the amount of time required for deposition, exclusive of the pre- and post-layers TABLE I \© *-: Example Materials Currents A Rot. Pressure Run Time Pre Time Min Post Time Etch un RPM mTorr Min Layer Layer Min Time 1 Sn 1 38 15 82 Sn 5 30 Cu 1 Cu 2 2 Sn 1 38 15 80 Sn 5 30 Mo 1.54 Mo 2 3 Sn 0.2 38 15 350 Sn 5 30 Mo 0.3 Mo 2 4 Sn 1 38 15 70 Sn 5 30 I Mo 2.2 Mo 2 I 5 Sn 1 38 15 70 Sn 5 30 Nb 2.2 Nb 2 6 Sn 1 38 15 60 Sn 5 30 W 1.7 W 2 7 Sn 1.4 38 15 60 30 Mo 1.55 Mo 2 O H r - v© oo - 10 - The composition, microstructure, and cycling behavior of these films are described in further detail, below Chemical Composition The chemical composition, in wt % and vol %, was determined using a series of calibration experiments in which a single source was operated at a fixed current for a fixed period of time The thickness of the resulting sample was then determined using a profilometer The vol % of the sample was predicted based upon the calibration experiments assuming that the total thickness of any one material was linearly proportional to the deposition current and the deposition time The wt % values were calculated from the vol % values using handbook values of material densities Transmission Electron Microscopy Transmission electron microscopy ("TEM") was used to examine the microstructure of the sputtered electrode films before and after cycling This technique produces images of the microstructure using spatial variations in transmitted intensity associated with spatial variations in the structure, chemistry, and/or thickness of the sample Because the radiation used to form these images consists of high energy electrons of very short wavelength, it is possible to obtain information at the atomic scale under high resolution electron microscopy (HREM) imaging conditions Moreover, the interaction of these electrons with the sample produces information about the crystal structure (electron diffraction) and local chemistry (x-ray microanalysis) that is complementary to the information contained in the image Prior to cycling, samples were prepared from sputtered films either by crushing to powder or by cutting the film in either the radial direction (1 e , slices were taken along the radial direction of the film) or the perpendicular direction of the film (1 e , slices were taken along the tangential direction of the film) The cut samples were then embedded in 3M Scotchcast Electrical Resin #5 (commercially available from 3M Company of St Paul, MN) and ultramicrotomed to obtain slices thin enough for TEM examination Slice thickness was nominally less than about 20 nm Two types of TEM instrumentation were used to obtain microstructural data The first type consisted of a HITACHI H9000NAR transmission electron microscope which operates at an accelerating voltage of 300 kV It is capable of a point-to-point resolution of 1 75 angstroms and a microprobe resolution of 16 angstroms for x-ray microanalysis The microanalysis instrumentation consisted of a NORAN VOYAGER III Direct-to-digital image acquisition and quantitative length measurements were performed by a GAT AN slow-scan CCD (charged-couple device) camera The second type of TEM instrumentation consisted of a JEOL 4000 FEX which - 11 - operates at an accelerating voltage of 200 kV It is capable of a point-to-point resolution of 2 angstroms and a microprobe resolution of 20 angstroms for x-ray microanalysis Samples were also examined by TEM after cycling by opening up the electrochemical cell in an inert atmosphere after a specified number of cycles and removing the sputtered film from the copper substrate by repeated scoring of the electrode surface with a razor blade The resulting material, in the form of a powder, was then collected onto a carbon mesh supported by a copper grid and inserted into the microscope for structural analysis Cycling Behavior Electrodes were cut from the sputtered films with a die measuring either 7 1 or 7 5 mm in diameter Two types of cells for testing were then prepared In the first type, the sputtered film formed the cathode and a lithium foil (about 300 micrometers thick, available from Aldπch Chemical Co of Milwaukee, WI) formed both the anode and the reference electrode of a 1225 coin cell In the second type (a full cell), the sputtered film formed the anode and a LιCoθ 2 -contaιnιng composition formed the cathode The LιCoθ2-contaιmng composition was made by combining 83% wt % L1C0O2 (available from Nippon Chemical Cellseed under the designation "C-10"), 7 wt % fluoropolymer binder (available from Elf Atochem under the designation "Kynar 461 "), 7 5 wt % KS-6 carbon (available from Timcal), and 2 5% Super P Carbon (available from MMM Carbon) Both types of cells were made with a 50 micrometer thick polyethylene separator The electrolyte in all cells was 1 molal LιPF 6 in a 1 1 v/v mixture of ethylene carbonate and diethyl carbonate Spacers were used as current collectors and to fill void areas in the cells Copper or stainless steel spacers were used in all cases except when the cell included L1C0O2, in which case aluminum was used as the spacer The electrochemical performance of the cells was measured using a MACCOR cycler The cycling conditions were typically set for constant current charge and discharge at approximately a C/3 rate (0 5 mA/cm 2 ) with typical cutoff voltages of 5 mV and 1 4 V Where the anode was a lithium foil, the coulombic efficiency was determined as the charge recovery or capacity of dehthiation divided by the capacity of hthiation Where the anode was the sputtered film, the coulombic efficiency was determined as the ratio of the discharge capacity to the charge capacity In many of the sputtered films, the resistance is higher at the beginning of the cycle life and drops after 10-20 cycles This resistive effect causes the capacity of the cell to drop initially and then stabilize after 10-20 cycles The resistive effect also causes the measured coulombic efficiency to be higher than 100% in the first few cycles because the capacity for dehthiation is increasing with cycle number out to 10-20 cycles - 12 - X-Ray Diffraction X-ray studies of cycled material were performed as follows After the cell had been charged or discharged to the desired voltage and equilibrated, it was placed in an argon-filled glove box and carefully opened to ensure that short circuiting did not occur The electrode was recovered and mounted in an air-tight sample holder equipped with Kapton x-ray windows The sample was then removed from the glove box and placed in the diffractometer Powder x-ray diffraction patterns were collected using a Siemens D5000 diffractometer equipped with a copper target x-ray tube and a diffracted beam monochromator Data was collected between scattering angles of 10 degrees and 80 degrees We now describe the preparation and characterization of specific sputtered electrode films Example 1 A film containing 55 2 wt % tin and 44 8 wt % copper was prepared by sputter deposition under the conditions shown in Table I The tin was sputter deposited at a rate of 555 angstroms/minute, while the copper was sputter deposited at a rate of 367 angstroms/minute The film contained 60 vol % tin and 40 vol % copper, calculated based upon these sputter rates The film thickness was 7 1 micrometers and the film density was approximately 7 8 g/cm The film had a pre-layer of pure copper measuring approximately 600 angstroms thick and a post-layer of pure tin measuring approximately 2500 angstroms thick The cycling behavior of the electrode film was tested as described above using a coin cell featuring a lithium foil anode and the sputtered film as the cathode The first discharge or hthiation of the film was controlled by setting the cycling conditions to taper the current at 5 mV so that the cell was hthiated to at least 400 mAh g The cell was then placed under charge and discharge cycling conditions using a current of 0 5 mA/cm and cutoff voltages of 5 mV and 1 4 V The specific capacity and coulombic efficiency of the cell in shown in Fig 5 The results demonstrate that an electrode composition using tin as the electrochemically active metal element and copper as the non-electrochemically active metal element yields stable reversible capacities of 125 mAh g for at least 100 cycles, which is a longer cycle life than pure tin, although the coulombic efficiency was less than 99 0% after a few cycles Example 2 A film containing 54 wt % tin and 46 wt % molybdenum was prepared by sputter deposition under the conditions shown in Table I The tin was sputter deposited at a rate of 550 - 13 - angstroms/minute, while the molybdenum was sputter deposited at a rate of 340 angstroms/minute The film contained 62 vol % tin and 38 vol % molybdenum, calculated based upon these sputter rates The film thickness was 5 3 micrometers and the film density was approximately 7 3 g/cm The film had a pre-layer of pure molybdenum measuring approximately 700 angstroms thick and a post-layer of pure tin measuring approximately 2500 angstroms thick TEM analysis of the film prior to cycling revealed that the microstructure of the film included crystalline tin particles in a compositionally modulated matrix phase Electron diffraction patterns (Fig 10) indicated the presence of a two phase microstructure crystalline tin (as evidenced by sharp spots in a ring pattern which indexes to tetragonal tin) and a matrix phase characterized by a broad diffuse ring pattern, suggesting the absence of ordered crystalline material High resolution electron microscopy verified that the matrix phase was disordered on a 10 angstrom scale TEM analysis of the radially cut samples showed that the measured average tin particle size was 5 +/- 1 3 nm by 19 +/- 5 9 nm The measured range of particle sizes was from 3 x 17 nm (smallest) to 7 x 31 nm (largest) The tin particles had aspect ratios ranging from approximately 2 1 to 6 1 , with the long dimension parallel to the plane of the film TEM analysis of the perpendicularly cut samples showed that the measured average tin particle size was 7 +/- 2 0 nm by 33 +/- 12 7 nm The measured range of particle sizes was from 4 x 12 nm (smallest) to 8 x 67 nm (largest) The tin particles had aspect ratios ranging from approximately 1 2 1 to 7 1 , with the long dimension parallel to the plane of the film TEM analysis of the matrix phase revealed this phase to be compositionally modulated perpendicular to the plane of the film, as evidenced by wandering "stripes" in the TEM images By underfocusing the image, the contrast differences between tin-rich and molybdenum-πch regions (relative to the bulk composition) could be enhanced X-ray microanalysis of the matrix phase confirmed the presence of a compositionally modulated structure The x-ray data was obtained using a TEM probe size of 16 angstroms moved along steps adjacent to a tin particle in a direction normal to the plane of the film Two sets of data were collected The first set centered around a relatively small tin particle located near the top edge of the film using a long scan The second set centered around a relatively large tin particle located in the middle of the film using a short scan The compositional results were determined using a standardless quantitative analysis routine, and are shown in Tables II (small tin particle) and III (large tin particle) As shown in Tables II and III, both the matrix surrounding the large particle and the small particle showed compositional modulation For comparison, the average bulk composition, determined using a 100 nm probe, was 45 6 wt % tin and 54 4 wt % molybdenum 14 - TABLE II Sample Wt. % Mo Wt. % Sn Sn particle 42 3 57 7 adj xl 53 6 46 4 adj x2 57 1 42 9 ad x3 46 5 53 5 TABLE III Sample Wt. % Mo Wt. % Sn Sn particle 33 1 66 9 adj xl 42 7 57 3 adj x2 52 8 47 2 adj x3 41 3 58 7 The cycling behavior of the electrode film was tested as described above using a coin cell featuring a lithium foil anode and the sputtered film as the cathode The first discharge or lithiation of the film was controlled by setting the cycling conditions to taper the current at 5 mV so that the cell was hthiated to at least 400 mAh/g The cell was then placed under charge and discharge cycling conditions using a current of 0 5 mA/cm and cutoff voltages of 5 mV and 1 4 V The specific capacity and coulombic efficiency of the cell in shown in Fig 1 The results demonstrate that the sputtered tin-molybdenum film exhibited a reversible capacity of approximately 300 mAh/g for at least 50 cycles before the coulombic efficiency dropped below 99 0% A second sample of the film was cycled under the conditions described above for 1, 2, 10, and 30 cycles After each cycling period, a sample of the electrode film was removed as described above and subjected to TEM analysis The TEM results demonstrated that individual crystalline regions could be resolved in the material after 2, 10, and 30 cycles using the dark field technique These samples had crystallite sizes less than 150 angstroms in diameter, with the majority of the crystallites having a diameter under 100 angstroms In addition, material cycled 1, 2, and 10 cycles exhibited a high frequency spatial variation in transmitted intensity along a single specific direction with a characteristic wavelength of 20 angstroms This suggests a high frequency spatial modulation in chemical composition, with the structure being characterized by a single wave vector perpendicular to the copper substrate This is consistent with a macro-structure built up by - 15 - alternating layers of molybdenum-rich and tin-rich slabs with a periodicity of about 20 angstroms The post-cycling TEM results also demonstrated that the crystal growth process was inhibited at least up to the 30th cycle In addition, images consistent with the spatially modulated chemical composition in the original molybdenum/tin structure were observed up to the 10th cycle Full cells were constructed as described above using the sputtered film as an anode and a LιCoθ2-contaιnιng composition as the cathode The mass balance, calculated based upon the weight of L1C0O 2 portion of the cathode and the weight of the entire tin-molybdenum anode, was 3 3 1 The cell were then cycled at a constant charge and discharge current of 0 5 mA/cm from 2 2 to 4 2 V The discharge current was allowed to drop to 50 microamps/cm before onset of the charge current The specific capacity and coulombic efficiency of the cell in shown in Fig 7 The dip in the plots around cycle 15 represents a change in the current from 0 25 mA/cm to 0 50 mA cm The first charge capacity was 145 mAh g for L1C0O 2 and 450 mAh/g for the tin-molybdenum material in the anode The irreversible capacity in the first cycle was 30% The specific capacity of the tin-molybdenum is similar to what was obtained in the coin cells described above using lithium foil as the anode The specific capacity of the L1C0O2 was maintained at 100 mAh g, which is a reasonable capacity for this material The results demonstrate that the tin-molybdenum composition can be used in an electrochemical cell as an anode in combination with a cathode material (L1C0O2) typically used in lithium-ion batteries The coulombic efficiency of the cell remains above 99 0% for at least 70 cycles Next, a tin-molybdenum film identical to the above-described film was prepared with the exception that it did not contain a tin post-layer The film was then incorporated in a coin cell containing a lithium foil anode and electrochemically cycled as described above X-ray diffraction data was gathered on the film after 0, 1 , 4, and 10 full cycles The results are shown in Fig 8(a)-(d) Fig 8(a) shows the x-ray diffraction pattern of the film as it was deposited The peak near 31 degrees is from small grains of tin and the broad peak near 39 degrees is from the tin- molybdenum matrix phase The vertical line at 40 6 degrees marks the position expected for pure crystalline molybdenum Fig 8(b) shows the x-ray diffraction pattern of the film in the charged state after the completion of one full charge discharge cycle The peak from the matrix phase is similar in position and width to that of the uncycled film The solid smooth line is a calculated pattern for LiSn, calculated using the crystal structure disclosed in Z Naturforsch 28B, pp 246-248 (1973) and assuming grain sizes of 5 nm Fig 8(c) shows the x-ray diffraction pattern of the film in the charged state after the completion of four full charge discharge cycles Peaks for tin and for the matrix phase are again - 16 - observed, demonstrating that the microstructure of the film is substantially maintained during cycling Fig 8(d) shows the x-ray diffraction pattern of the film in the charged state after the completion of ten full charge-discharge cycles The electrode has begun to crack from the copper substrate, as shown by x-ray peaks attributable to the molybdenum pre-layer and the copper substrate (peak having a tail at 50 degrees) Nevertheless, comparing the results with the data in Fig 8(c), and noting the change in intensity scale between the two figures, it can be seen that the tin peak has substantially the same intensity and half-width as the film after four cycles The same can be said for the peak attributable to the matrix phase, although the results are somewhat obscured by the presence of a peak attributable to the molybdenum pre-layer Example 3 A film containing 54 5 wt % tin and 45 5 wt % molybdenum was prepared by sputter deposition under the conditions shown in Table I The tin was sputter deposited at a rate of 110 angstroms/minute, while the molybdenum was sputter deposited at a rate of 60 angstroms/minute The film contained 62 6 vol % tin and 37 4 vol % molybdenum, calculated based upon these sputter rates The film thickness was 4 1 micrometers and the film density was approximately 9 2 g/cm The film had a pre-layer of pure molybdenum measuring approximately 200 angstroms thick and a post-layer of pure tin measuring approximately 500 angstroms thick TEM analysis of the film prior to cycling did not detect the presence of any crystalline regions Electron diffraction patterns showed only broad diffuse rings If crystalhnity of any form existed, it was on a scale of less than 10 angstroms In addition, x-ray microanalysis indicated that no composition modulation could be measured on a 1 6 nm scale (the size of the probe) After one full cycle, crystalline regions of LiSn appeared The cycling behavior of the electrode film was tested as described above using a coin cell featuring a lithium foil anode and the sputtered film as the cathode The first discharge or lithiation of the film was controlled by setting the cycling conditions to taper the current at 5 mV so that the cell was hthiated to at least 400 mAh/g The cell was then placed under charge and discharge cycling conditions using a current of 0 5 mA/cm" and cutoff voltages of 5 mV and 1 4 V The specific capacity and coulombic efficiency of the cell in shown in Fig 2 The results demonstrate that the sputtered tin-molybdenum film, which was sputtered at lower tin and molybdenum rates compared to Example 2, exhibited a reversible capacity of approximately 300 mAh/g for at least 50 cycles and a coulombic efficiency of approximately 99 0% Example 4 A film containing 45 wt % tin and 55 wt % molybdenum was prepared by sputter - 17 - deposition under the conditions shown in Table I The tin was sputter deposited at a rate of 555 angstroms/minute, while the molybdenum was sputter deposited at a rate of 487 angstroms/minute The film contained 53 3 vol % tin and 46 7 vol % molybdenum, calculated based upon these sputter rates The film thickness was 5 6 micrometers and the film density was approximately 9 2 g/cm The film had a pre-layer of pure molybdenum measuring approximately 1000 angstroms thick and a post-layer of pure tin measuring approximately 2500 angstroms thick The cycling behavior of the electrode film was tested as described above using a coin cell featuring a lithium foil anode and the sputtered film as the cathode The first discharge or lithiation of the film was controlled by setting the cycling conditions to taper the current at 5 mV so that the cell was hthiated to at least 400 mAh/g The cell was then placed under charge and discharge cycling conditions using a current of 0 5 mA/cm and cutoff voltages of 5 mV and 1 4 V The specific capacity and coulombic efficiency of the cell in shown in Fig 3 The results demonstrate the sputtered tin-molybdenum film, in which the wt % of molybdenum was higher than the film of Example 2, exhibited a reversible capacity of approximately 200 mAh/g and a coulombic efficiency of approximately 99 0% for at least 400 cycles Comparing these results with the results of Example 2 demonstrates that as the wt % of molybdenum increases, the specific capacity decreases, but the cycle life (defined by the number of cycles at 99 0% coulombic efficiency) increases Example 5 A film containing 65 5 wt % tin and 34 5 wt % niobium was prepared by sputter deposition under the conditions shown in Table I The tin was sputter deposited at a rate of 555 angstroms/mmute, while the niobium was sputter deposited at a rate of 250 angstroms/minute The film contained 69 vol % tin and 31 vol % niobium, calculated based upon these sputter rates The film thickness was 4 8 micrometers and the film density was approximately 8 6 g/cm The film had a pre-layer of pure niobium measuring approximately 500 angstroms thick and a post-layer of pure tin measuring approximately 2500 angstroms thick TEM analysis of the film prior to cycling revealed that the microstructure of the film included crystalline particles (present in TEM micrographs as dark cigar-shaped regions) in a compositionally modulated matrix phase (present in TEM micrographs as striped regions) X-ray microanalysis demonstrated that the crystalline particles were tin-rich relative to the bulk composition Bulk "white' regions interspersed between the striped regions were revealed by x-ray microanalysis to be mobium-πch relative to the bulk composition Electron diffraction patterns also indicated the presence of a two phase microstructure crystalline tin and a matrix phase characterized by a broad diffuse ring pattern, suggesting the absence of crystalline material High resolution electron microscopy verified that the matrix phase - 18 - was amorphous on a 10 angstrom scale TEM analysis of the radially cut samples showed that the measured average crystalline particle size was 5 +1- 1 8 nm by 33 +/- 8 0 nm The measured range of particle sizes was from 3 x 20 nm (smallest) to 6 x 42 nm (largest) The crystalline particles had aspect ratios ranging from approximately 3 1 to 10 1 , with the long dimension parallel to the plane of the film TEM analysis of the perpendicularly cut samples showed that the measured average crystalline particle size was 8 4-/- 1 8 nm by 44 +/- 12 4 nm The measured range of particle sizes was from 6 x 26 nm (smallest) to 5 x 80 nm (largest) The tin particles had aspect ratios ranging from approximately 1 1 1 to 15 1 TEM analysis of the matrix phase revealed this phase to be compositionally modulated perpendicular to the plane of the film, as evidenced by wandering "stripes" in the TEM images X- ray microanalysis of the matrix phase confirmed the presence of a compositionally modulated structure The x-ray data was obtained using a TEM probe size of 1 6 nm moved along steps adjacent to a crystalline particle in a direction normal to the plane of the film The compositional results were determined using a standardless quantitative analysis routine, and are shown in Table IV As shown in Table IV, the matrix showed compositional modulation For comparison, the average bulk composition, determined using a 100 nm probe, was 58 9 wt % tin and 41 1 wt % niobium 19 - TABLE IV Sample Wt. % Sn Wt. % Nb cryst particle 73 73 26 27 cryst particle 82 21 17 79 adj xl 67 35 32 65 adj x2 62 56 37 44 adj x3 53 56 46 44 adj x4 63 08 36 92 adj x5 65 62 34 38 adj x6 55 18 44 82 (white region) adj x7 54 09 45 91 (white region) The cycling behavior of the electrode film was tested as described above using a coin cell featuring a lithium foil anode and the sputtered film as the cathode The first discharge or lithiation of the film was controlled by setting the cycling conditions to taper the current at 5 mV so that the cell was hthiated to at least 400 mAh/g The cell was then placed under charge and discharge cycling conditions using a current of 0 5 mA cm 2 and cutoff voltages of 5 mV and 1 4 V The specific capacity and coulombic efficiency of the cell in shown in Fig 4 The results demonstrate that films using niobium as the non-electrochemically active metal element exhibit a reversible capacity of 225 mAh g and a coulombic efficiency greater than 99 0% for at least 70 cycles Example 6 A film containing 43 7 wt % tin and 56 3 wt % tungsten was prepared by sputter deposition under the conditions shown in Table I The tin was sputter deposited at a rate of 560 angstroms/minute, while the tungsten was sputter deposited at a rate of 275 angstroms/minute The film contained 67 3 vol % tin and 32 7 vol % tungsten, calculated based upon these sputter rates The film thickness was 8 8 micrometers and the film density was approximately 6 g/cm The film had a pre-layer of pure tungsten measuring approximately 680 angstroms thick and a post-layer of pure tin measuring approximately 2800 angstroms thick The cycling behavior of the electrode film was tested as described above using a coin cell featuring a lithium foil anode and the sputtered film as the cathode The first discharge or lithiation of the film was controlled by setting the cycling conditions to taper the current at 5 mV so - 20 - that the cell was hthiated to at least 400 mAh g The cell was then placed under charge and discharge cycling conditions using a current of 0 25 mA/cm and cutoff voltages of 5 mV and 1 4 V The specific capacity and coulombic efficiency of the cell in shown in Fig 6 The results demonstrate the sputtered film, in which the non-electrochemically active metal element was tungsten, exhibited a reversible capacity of approximately 200 mAh/g and a coulombic efficiency of approximately 99 0% for at least 40 cycles Example 7 A film containing 62 wt % tin and 38 wt % molybdenum was prepared by sputter deposition under the conditions shown in Table I The tin was sputter deposited at a rate of 780 angstroms/minute, while the molybdenum was sputter deposited at a rate of 340 angstroms/minute The film contained 69 vol % tin and 31 vol % molybdenum, calculated based upon these sputter rates The film thickness was 5 1 micrometers and the film density was approximately 9 9 g/cm The film had a pre-layer of pure molybdenum measuring approximately 700 angstroms thick It did not have a post-layer B. Electrode Compositions Prepared by Ball Milling Electrode compositions were prepared by ball milling and, in some instances, characterized according to the following general procedures Ball Milling Procedure A Spex 8000 high-impact mixer mill was used to violently shake sealed hardened steel vials for periods up to 40 hours In an argon-filled glove box, the desired amounts of elemental powders or intermetallic compounds were added to a hardened steel vial, along with several hardened steel balls measuring 12 7 mm in diameter The vial was then sealed and transferred to a Spex 8000 high-impact mixer mill where it was shaken violently Milling times were generally on the order of about 20 hours - 21 - Cycling Behavior Electrodes were prepared by coating slurries of the powders onto a copper foil and then evaporating the carrier solvent Specifically, about 86% by weight powder (prepared by ball milling), 8% by weight Super S carbon black (MMM Carbon, Belgium), and 6% by weight polyvinyhdene fluoride (Atochem) were thoroughly mixed with N-methyl pyrrohdinone by stirring in a sealed bottle to make a slurry, the polyvinyhdene fluoride was pre-dissolved in the N-methyl pyrrohdinone prior to addition of the powder and carbon black The slurry was spread in a thin layer (about 150 micrometers thick) on the copper foil with a doctor-blade spreader The sample was then placed in a muffle oven maintained at 105* C to evaporate the N-methyl pyrrohdinone solvent over a 3 hour period Circular electrodes measuring 1 cm in diameter were cut from the dried film using an electrode punch The electrodes were weighed, after which the weight of the copper was subtracted and the active mass of the electrode calculated (I e , the total weight of the electrode multiplied by the fraction of the electrode made of the active electrode powder) The electrodes were used to prepare coin cells for testing A lithium foil having a thickness of 125 micrometers functioned as the anode and reference electrode The cell featured 2325 hardware, equipped with a spacer plate (304 stainless steel) and a disc spring (mild steel) The disc spring was selected so that a pressure of about 15 bar would be applied to each of the cell electrodes when the cell was crimped closed The separator was a Celgard #2502 microporous polypropylene film (Hoechst-Celanese) which had been wetted with a 1M solution of LiPFβ dissolved in a 30 70 volume mixture of ethylene carbonate and diethyl carbonate (Mitsubishi Chemical) Cycling conditions were typically set at a constant current of 37 mA/g of active material Cutoff voltages of 0 0 V and 1 3 V were used X-Ray Diffraction Powder x-ray diffraction patterns were collected using a Siemens D5000 diffractometer equipped with a copper target x-ray tube and a diffracted beam monochromator Data was collected between scattering angles of 10 degrees and 80 degrees To examine the electrode materials during cycling, m-situ x-ray diffraction experiments were performed Cells for m-situ x-ray diffraction were assembled as described above in the case of the cycling experiment with the following differences The coin cell can was provided with a circular hole measuring 18 mm in diameter A 21 mm diameter beryllium window (thickness = 250 micrometers) was affixed to the inside of the hole using a pressure sensitive adhesive (Roscobond from Rosco of Port Chester NY) The electrode material was coated directly onto the window before it was attached to the can The cell was mounted in a Siemens D5000 diffractometer and slowly discharged and - 22 - charged while x-ray diffraction scans were taken continuously Typically, a complete scan took 2-5 hours and the discharge and charge time took 40-60 hours, giving approximately 10-30 "snapshots" of the crystal structure of the electrode as a function of its state of charge The voltage of the cell was continuously monitored during cycling Specific samples were prepared and tested as follows Example 8 An intermetallic compound, Sn2Fe, was prepared by melting together stoichiometπc ratios of tin and iron (obtained in powder form from Aldπch Co of Milwaukee, WI) in a radio frequency induction furnace under inert gas After a homogeneous melt was obtained, the sample was removed from the furnace, transferred to a tube furnace, and annealed at 500EC for about 60 hours under argon flow The sample was then broken into chunks with a hammer, after which 2 grams of the sample was placed into a hardened steel vial, along with two 12 7 mm diameter hardened steel balls, and the vial sealed The loading and sealing were conducted in an argon-filled glove box The sample was then milled for 20 hours following the general procedure described above The sample contained 66 6 atomic % tin and 33 3 atomic % iron Following milling, an electrochemical cell was constructed as described above and its cycling behavior tested The irreversible capacity (in mAh/g up to 1 3 V), reversible capacity (mAh/g), and cycle life before the capacity fell to 50% of the initial reversible capacity at C/10 are reported in Table V Three samples were tested Example 9 A ball milled powder was prepared according to the procedure of Example 8 except that before being placed in the steel vial, the sample was ground using a mortar and pestle to form 50 micron-sized particles Following milling, an electrochemical cell was constructed as described above and its cycling behavior tested The irreversible capacity (in mAh g up to 1 3 V) and reversible capacity (mAh g) are reported in Table V Cycle life was not tested ("NT") - 23 - Example 10 A ball milled powder was prepared according to the procedure of Example 8 except that the powder was prepared by adding 0 402 g iron, 1 715 g tin, and 0 026 g graphite powder (mesocarbon microbeads from Osaka Gas Ltd which had been heated to 2650EC) directly to the milling vial The sample contained 60 6 atomic % tin, 30 3 atomic % iron, and 9 1 atomic % carbon X-ray diffraction data suggests that the sample contains a mixture of an Sn?Fe phase and a carbon phase Following milling, an electrochemical cell was constructed as described above and its cycling behavior tested The irreversible capacity (in mAh/g up to 1 3 V), reversible capacity (mAh/g), and cycle life before the capacity fell to 50% of the initial reversible capacity at C/10 are reported in Table V To study the reaction of S^Fe with lithium during cycling, two m-situ x-ray diffraction cells were constructed The first had an active electrode made of tin metal powder, while the second had an active electrode made of the above-described electrode powder The x-ray diffraction patterns of both electrodes were observed after the cell had been discharged to zero volts over a period of about 40 hours The results are shown in Fig 9 The broad diffraction peak near 23E and the sharper peak near 38 5E arise from the active electrode which has reacted with lithium The other peaks are attributable to the beryllium window of the cell and from small amounts of inactive electrode material The similarity between the patterns suggests that the discharge products of Li/Sn and Lι/Sn 2 Fe are similar This suggests the presence of a crystalline Li-Sn alloy phase with nanometer-scale crystallite size and a second, iron-rich, crystalline phase in which the size of the crystallites is also on a nanometer scale Example 1 1 A ball milled powder was prepared according to the procedure of Example 8 except the powder was prepared by adding 0 404 g iron, 1 711 g tin, and 0 066 g graphite powder (mesocarbon microbeads from Osaka Gas Ltd which had been heated to 2650E C) directly to the milling vial The sample contained 54 1 atomic % tin, 27 0 atomic % iron, and 18 9 atomic % carbon X-ray diffraction data suggests that the sample contains a mixture of an Sn2Fe phase and a carbon phase Following milling, an electrochemical cell was constructed as described above and its cycling behavior tested The irreversible capacity (in mAh/g up to 1 3 V), reversible capacity (mAh/g) and cycle life before the capacity fell to 50% of the initial reversible capacity at C/10 are reported in Table V Two samples were tested The cycle life of the second sample was not tested (' NT ) - 24 - Example 12 A ball milled powder was prepared according to the procedure of Example 8 except the powder was prepared by adding 0 406 g iron, 1 725 g tin, and 0 104 g graphite powder (mesocarbon microbeads from Osaka Gas Ltd which had been heated to 2650EC) directly to the milling vial The sample contained 47 6 atomic % tin, 23 8 atomic % iron, and 28 6 atomic % carbon X-ray diffraction data suggests that the sample contains a mixture of an Sn∑Fe phase and a carbon phase Following milling, an electrochemical cell was constructed as described above and its cycling behavior tested The irreversible capacity (in mAh g up to 1 3 V), reversible capacity (mAh/g), and cycle life before the capacity fell to 50% of the initial reversible capacity at C/10 are reported in Table V Two samples were tested The cycle life of the first sample was not tested ("NT") Example 13 A ball milled powder was prepared according to the procedure of Example 8 except the relative amounts of iron and tin were selected to yield a sample having 50 0 atomic % tin and 500 atomic % iron In addition, iron and tin were adding directly to the milling vial, rather than being melted together Following milling, an electrochemical cell was constructed as described above and its cycling behavior tested The irreversible capacity (in mAh/g up to 1 3 V), reversible capacity (mAh g), and cycle life before the capacity fell to 50% of the initial reversible capacity at C/10 are reported in Table V Example 14 A ball milled powder was prepared according to the procedure of Example 8 except the relative amounts of iron and tin were selected to yield a sample having 40 0 atomic % tin and 60 0 atomic % iron In addition, the sample was milled for 38 hours Following milling, an electrochemical cell was constructed as described above and its cycling behavior tested The irreversible capacity (in mAh g up to 1 3 V), reversible capacity (mAh/g), and cycle life before the capacity fell to 50% of the initial reversible capacity at C/10 are reported in Table V Two samples were tested Example 15 A ball milled powder was prepared according to the procedure of Example 8 except the relative amounts of iron and tin were selected to yield a sample having 37 5 atomic % tin and 62 5 atomic % iron In addition, the sample was milled for 19 hours Following milling, an electrochemical cell was constructed as described above and its cycling behavior tested The - 25 - irreversible capacity (in mAh/g up to 1 3 V), reversible capacity (mAh/g), and cycle life before the capacity fell to 50% of the initial reversible capacity at C/10 are reported in Table V Two samples were tested Example 16 A ball milled powder was prepared according to the procedure of Example 8 except the powder was prepared by adding 0 866 g iron, 1 277 g tin, and 0 049 g graphite powder (mesocarbon microbeads from Osaka Gas Ltd which had been heated to 2650EC) directly to the milling vial The sample contained 35 4 atomic % tin, 51 2 atomic % iron, and 13 4 atomic % carbon X-ray diffraction revealed the sample to be a mixture of Sn 2 Fe and SnFβ3C phases Following milling, an electrochemical cell was constructed as described above and its cycling behavior tested The irreversible capacity (in mAh/g up to 1 3 V), reversible capacity (mAh g), and cycle life before the capacity fell to 50% of the initial reversible capacity at C/10 are reported in Table V Two samples were tested Example 17 A ball milled powder was prepared according to the procedure of Example 8 except the powder was prepared by adding 0 866 g iron, 1 277 g tin, and 0 136 g graphite powder (mesocarbon microbeads from Osaka Gas Ltd which had been heated to 2650EQ directly to the milling vial The sample contained 28 7 atomic % tin, 41 6 atomic % iron, and 29 7 atomic % carbon X-ray diffraction revealed the sample to be a mixture of S^Fe and SnFβ3C phases Following milling, an electrochemical cell was constructed as described above and its cycling behavior tested The irreversible capacity (in mAh g up to 1 3 V), reversible capacity (mAh/g), and cycle life before the capacity fell to 50% of the initial reversible capacity at C/10 are reported in Table V Two samples were tested The cycle life of the first sample was not tested ("NT") Example 18 A ball milled powder was prepared according to the procedure of Example 8 except the powder was prepared by adding 1 017 g iron, 1 083 g tin, and 0 066 g graphite powder (mesocarbon microbeads from Osaka Gas Ltd which had been heated to 2650EC) directly to the milling vial The sample contained 27 8 atomic % tin, 55 6 atomic % iron, and 16 7 atomic % carbon X-ray diffraction revealed the sample to be a mixture of Sn2Fe and SnFeiC phases Following milling, an electrochemical cell was constructed as described above and its cycling behavior tested The irreversible capacity (in mAh/g up to 1 3 V), reversible capacity (mAh/g), and cycle life before the capacity fell to 50% of the initial reversible capacity at C/10 are - 26 - reported in Table V Example 19 A ball milled powder was prepared according to the procedure of Example 8 except the powder was prepared by adding 1 044 g iron, 1 070 g tin, and 0 164 g graphite powder (mesocarbon microbeads from Osaka Gas Ltd which had been heated to 2650EC) directly to the milling vial The sample contained 22 1 atomic % tin, 44 2 atomic % iron, and 33 6 atomic % carbon X-ray diffraction revealed the sample to be a mixture of Sn 2 Fe and SnFesC phases Following milling, an electrochemical cell was constructed as described above and its cycling behavior tested The irreversible capacity (in mAh/g up to 1 3 V), reversible capacity (mAh/g), and cycle life before the capacity fell to 50% of the initial reversible capacity at C/10 are reported in Table V Two samples were tested Example 20 A ball milled powder was prepared according to the procedure of Example 8 except the powder was prepared by adding 1 160 g iron, 1 823 g tin, and 0 084 g graphite powder (mesocarbon microbeads from Osaka Gas Ltd which had been heated to 2650EC) directly to the milling vial The sample contained 20 0 atomic % tin, 60 0 atomic % iron, and 20 0 atomic % carbon X-ray diffraction revealed the sample to be a mixture of S^Fe and SnFe3C phases Following milling, an electrochemical cell was constructed as described above and its cycling behavior tested The irreversible capacity (in mAh/g up to 1 3 V), reversible capacity (mAh g), and cycle life before the capacity fell to 50% of the initial reversible capacity at C/10 are reported in Table V - 27 - TABLE V Examples Irrev. Capacity Rev. Capacity Cycle Life 8 164 607 12 173 619 10 177 618 10 9 96 548 NT 10 120 635 13 11 100 635 10 108 657 NT 12 89 646 NT 90 646 11 13 66 328 33 14 83 193 >50 83 195 >50 15 64 156 65 60 143 65 16 61 340 37 56 343 33 17 63 358 NT 59 356 43 18 59 226 80 19 66 193 130 60 216 130 20 50 62 (increases to 100) >200 Other embodiments are within the following claims.

Claims: - 28 - What is claimed is 1 An electrode composition comprising (a) an electrochemically active metal element which, prior to cycling, is in the form of an intermetallic compound or an elemental metal and (b) a non-electrochemically active metal element, wherein said composition, when incorporated in a lithium battery and cycled through one full charge-discharge cycle, comprises crystalline regions having at least one dimension that is no greater than about 500 angstroms and that does not substantially increase after a total of at least 10 cycles 2 An electrode composition according to claim 1 wherein said dimension does not substantially increase after a total of at least 100 cycles 3 An electrode composition according to claim 1 wherein said composition comprises said crystalline regions prior to cycling 4 An electrode composition according to claim 1 wherein said electrochemically active metal element is tin 5 An electrode composition according to claim 1 wherein said non- electrochemically active metal element is selected from the group consisting of molybdenum, niobium, tungsten, tantalum, iron, copper, and combinations thereof 6 An electrode composition according to claim 1 wherein at least one of said crystalline regions comprises said electrochemically active metal element 7 An electrode composition according to claim 1 wherein at least one of said crystalline regions comprises said non-electrochemically active metal element 8 An electrode composition according to claim 1 wherein at least one of said crystalline regions comprises said electrochemically active metal element and at least another of said crystalline regions comprises said non-electrochemically active metal element 9 An electrode composition according to claim 1 wherein said crystalline regions are separated by regions comprising said electrochemically active metal element and said non-electrochemically active metal element in which the relative proportions of said electrochemically active metal element and said non-electrochemically active metal element vary - 29 - throughout the thickness direction of said composition 10 An electrode composition according to claim 3 wherein, prior to cycling, said crystalline regions are separated by regions comprising said electrochemically active metal element and said non-electrochemically active metal element in which the relative proportions of said electrochemically active metal element and said non-electrochemically active metal element vary throughout the thickness direction of said composition 11 An electrode composition according to claim 1 wherein said composition, when incorporated in a lithium battery and cycled to realize about 100 mAh/g of said composition, exhibits a coulombic efficiency of at least about 99 0% after 100 full discharge cycles 12 An electrode composition according to claim 1 wherein said composition, when incorporated in a lithium battery and cycled to realize about 100 mAh/g of said composition, exhibits a coulombic efficiency of at least about 99 8% after 100 full discharge cycles 13 An electrode composition according to claim 1 wherein said composition is in the form of a thin film 14 An electrode composition according to claim 1 wherein said composition is in the form of a powder 15 An electrode composition comprising (a) an electrochemically active metal element which, prior to cycling, is in the form of an intermetallic compound or an elemental metal and (b) a non-electrochemically active metal element, wherein said composition (a) when incorporated in a lithium battery and cycled through one full charge- discharge cycle, comprises crystalline regions and (b) when incorporated in a lithium battery and cycled to realize about 100 mAh/g of said composition, exhibits a coulombic efficiency of at least about 99 0% after 100 full discharge cycles 16 An electrode composition according to claim 15 wherein said composition comprises said crystalline regions prior to cycling 17 An electrode composition according to claim 15 wherein said - 3 0 - electrochemically active metal element is tin 18 An electrode composition according to claim 15 wherein said non- electrochemically active metal element is selected from the group consisting of molybdenum, niobium, tungsten, tantalum, iron, copper, and combinations thereof 19 An electrode composition according to claim 15 wherein at least one of said crystalline regions comprises said electrochemically active metal element 20 An electrode composition according to claim 15 wherein at least one of said crystalline regions comprises said non-electrochemically active metal element 21 An electrode composition according to claim 15 wherein at least one of said crystalline regions comprises said electrochemically active metal element and at least another of said crystalline regions comprises said non-electrochemically active metal element 22 An electrode composition according to claim 15 wherein said crystalline regions are separated by regions comprising said electrochemically active metal element and said non-electrochemically active metal element in which the relative proportions of said electrochemically active metal element and said non-electrochemically active element vary throughout the thickness direction of said composition 23 An electrode composition according to claim 15 wherein said composition, when incorporated in a lithium battery and cycled to realize about 100 mAh/g of said composition, exhibits a coulombic efficiency of at least about 99 8% after 100 full discharge cycles 24 An electrode composition according to claim 15 wherein said composition, when incorporated in a lithium battery and cycled to realize about 100 mAh/g of said composition, exhibits a coulombic efficiency of at least about 99 9% after 100 full discharge cycles 25 An electrode composition according to claim 15 wherein said composition is in the form of a thin film 26 An electrode composition according to claim 15 wherein said composition is in the form of a powder - 3 1 - 27 A lithium battery comprising (a) a first electrode comprising (I) an electrochemically active metal element which, prior to cycling, is in the form of an intermetallic compound or an elemental metal and (n) a non-electrochemically active metal element, wherein said electrode, after said battery has been cycled through one full charge- discharge cycle, comprises crystalline regions having at least one dimension that is no greater than about 500 angstroms and that does not substantially increase after a total of at least 10 cycles, (b) a counterelectrode, and (c) an electrolyte separating said electrode and said counterelectrode 28 A lithium battery comprising (A) a first electrode comprising (I) an electrochemically active metal element which, prior to cycling, is in the form of an intermetallic compound or an elemental metal and (n) a non-electrochemically active metal element, wherein said electrode (a) after said battery has been cycled through one full charge-discharge cycle, comprises crystalline regions and (b) after said battery has been cycled to realize about 100 mAh/g of said composition, exhibits a coulombic efficiency of at least about 99 0% after 100 full discharge cycles, (B) a counterelectrode, and (C) an electrolyte separating said electrode and said counterelectrode 29 A method of preparing an electrode composition comprising combining (a) a source comprising an electrochemically active metal element and (b) a source comprising a non- electrochemically active metal element to form an electrode composition characterized in that (l) prior to cycling said electrochemically active metal element is in the form of an intermetallic compound or an elemental metal, (n) when incorporated in a lithium battery and cycled through one full charge- discharge cycle, said electrode composition comprises crystalline regions and (in) when incorporated in a lithium battery and cycled to realize about 100 mAh/g of said composition, said electrode composition exhibits a coulombic efficiency of at least about 99 0% after 100 full discharge cycles 30 A method according to claim 29 comprising combining said sources by sequentially sputter-depositing said source of said electrochemically active metal element and said source of said non-electrochemically active metal element on a substrate to form said electrode - 32 - composition in the form of a thin film 31 A method according to claim 29 comprising combining said sources by ball milling to form said electrode composition in the form of a powder

Inventors: BUCKETT MARY M, DAHN JEFFERY R, KRAUSE LARRY J, MAO OU, MCCLURE DONALD J, TURNER ROBERT L, BUCKETT, MARY, M., DAHN, JEFFERY, R., KRAUSE, LARRY, J., MAO, OU, MCCLURE, DONALD, J., TURNER, ROBERT, L.
Applicants: MINNESOTA MINING & MFG, MINNESOTA MINING AND MANUFACTURING COMPANY
Application year: 1998
Main classification: H01M10
IPC codes: H01M4, H01M10