Fluorinated thermoplastic elastomers and articles therefrom

Abstract: Manufactured articles obtainable from a composition consisting of: 1) 100 phr of a fluorinated thermoplastic elastomer having a block structure with at least a fluorinated polymeric segment of B type having elastomeric properties and at least a fluorinated polymeric segment of A type having plastomeric properties, 2) from 0.1 to 40 phr of a crosslinking agent able to give peroxidic crosslinking of fluoroelastomers; and subsequent irradiation of the manufactured article by GAMMA or BETA radiations.

Description: The present invention relates to fluorinated thermoplastic elastomers having improved sealing properties, in particular at high temperatures, at least up to 150°C. As known, thermoplastic elastomers are block copolymers formed by at least a soft segment having elastomeric properties and by at least a hard segment having plastomeric properties. Such products combine therefore the properties typical of the conventional cured elastomers with those of the plastomers. In comparison with the conventional elastomers, they do not require any curing process, wherefore they result easily processable and recyclable according to the techniques usually utilized for thermoplastic polymers, with clear both economic and ecologic advantages. Fluorinated thermoplastic elastomers are known in the art. For instance in US patent 4,158,678 block fluorinated polymers, formed by alternate hard and soft segments, of which at least one is fluorinated, are described. Such products are obtained by radical polymerization of fluorinated monomers in the presence of an iodinated chain transfer agent having the formula RI n , wherein R is a fluorinated radical, optionally containing chlorine, having from 1 to 8 carbon atoms, and n is 1 or 2, thus obtaining a first fluorinated polymeric segment, with elastomeric or plastomeric characteristics depending on the monomeric composition, having an iodine atom on one or both end groups. On such segment other different fluorinated or non fluorinated segments are then grafted, considering that the terminal iodine atoms are susceptible of radical attack and can therefore produce the growth of a new polymeric chain. It is thus possible to obtain, for instance, fluorinated thermoplastic elastomers of the A-B-A type, wherein A is a plastomeric segment (for instance a homopolymer or copolymer deriving from tetrafluoroethylene and/or vinylidenefluoride), while B is an elastomeric segment (for instance a tetrafluoroethylene/vinylidene fluoride/hexafluoropropene copolymer. Other thermoplastic elastomers of this kind are described in EP 444,700. A limit of such products consists in that the mechanical and elastic properties easily worsen when the temperature rises and result quite unsatisfactory already at 50°C. In particular the compression set values are high, such as to make the products unsuitable to the manufacture of sealing elements (for instance shaft seals or O-rings or the like) to be employed at high temperatures, as requested by the motor, aerospace, plant industry. Fluorinated thermoplastic elastomers, having improved mechanical and elastic properties by the introduction in the polymeric chain of small amounts of a bis-olefin, are also known from USP 5,612,419. The resulting products are in particular characterized by improved mechanical properties and by particularly low compression set values in comparison with the fluorinated thermoplastic elastomers of the patents previously described. New fluorinated thermoplastic elastomers are also known from EP patent 683,186, which have mechanical and elastomeric properties similar to the products of US patent 5,612,419 but having in the chain instead of the bis-olefin, small amounts of a fluorinated olefin containing a terminal iodine atom. However the sealing properties of the products mentioned above are not satisfactory at high temperatures, in particular at the temperature of 150°C. The need was felt to have available thermoplastic elastomers with improved sealing properties at high temperatures, in particular the compression set (C set). An object of the present invention are manufactured articles obtainable from a composition consisting essentially of: 1) 100 phr of a fluorinated thermoplastic elastomer having a block structure with at least a fluorinated polymeric segment of type B having elastomeric properties and at least a fluorinated polymeric segment of type A having plastomeric properties, whereby in at least one among the A type or B type segments monomeric units are present which derive from a bis-olefin having the general formula: wherein: R 1 , R 2 , R 3 , R 4 , R 5 , R 6 , equal to or different from each other, are H or alkyls C 1 -C 5 ; Z is an alkylene or cycloalkylene radical C 1 -C 18 , linear or branched, optionally containing oxygen atoms, or a (per)fluoropolyoxyalkylenic radical 2) from 0.1 to 40 phr of a crosslinking agent able to give peroxidic crosslinking of fluoroelastomers; and subsequent radiation of the manufactured article by GAMMA radiations, from 1 to 50 Mrad, preferably from 1 to 30 Mrad, or BETA radiations from 10 to 500 KGy, preferably from 10 to 300 KGy. Preferably the amount of the component 2) ranges from 1 to 10 phr. The composition of the invention can contain additives such as fillers, for instance carbon black, silica, stabilizers, antioxidants, pigments, thickeners and plastifiers. The amount of these additives generally ranges from 0.5 to 40 phr, preferably from 1 to 20 phr. The crosslinking agents which can be used are for instance: 1,6-divinylperfluorohexane triallyl-cyanurate; triallyl-isocyanurate (TAIC); tris(diallylamine)-s-triazine; triallylphosphite; N,N-diallyl-acrylamide; fluorinated bis-olefins as defined hereinafter, N,N'-bisallylbicycle-oct-7-ene-disuccinimide (BOSA); N,N,N',N'-tetraallyl-malonamide; trivinyl-isocyanurate; and 2,4,6-trivinyl-methyltrisiloxane. A crosslinking agent or a mixture of the crossliniking agents above mentioned can be utilized. It has been found that the compositions of the invention subjected to treatment with BETA or GAMMA radiations give a remarkable increase of the sealing properties, even at high temperatures up to 150°C. The effect is particularly meaningful when the thermoplastic elastomer contains as plastomeric block the one essentially formed by PVDF. In this case, it is sufficient a very low amount of radiations, for instance 1 Mrad of GAMMA rays, to obtain the improved sealing properties. As preferred crosslinking agents, TAIC, 1,6-divinylperfluorohexane (bis-olefin), BOSA can be mentioned, which have the following structures: CH 2 = CH(CF 2 ) 6 CH=CH 2 1,6-DIVINYLPERFLUOROHEXANE (BO) In the formula (I A), Z is preferably a perfluoroalkylenic radical C 4 -C 12 , whereas R 1 , R 2 , R 3 , R 4 , R 5 , R 6 are preferably hydrogen. When Z is a (per)fluoropolyoxyalkylenic radical, it has preferably the formula: -(Q) p -CF 2 O-(CF 2 CF 2 O) m (CF 2 O) n -CF 2 -(Q) p - wherein: Q is an alkylenic or oxyalkylenic radical C 1 -C 10 ; p is 0 or 1; m and n are integers such that the m/n ratio is in the range 0.2-5 and the molecular weight of said (per)fluoropolyoxyalkylenic radical is in the range 500 and 10,000, preferably 1,000-4,000. Preferably, Q is selected from: -CH 2 OCH 2 -; -CH 2 O(CH 2 CH 2 O) s CH 2 -, s=1-3. The bis-olefins of formula (IA) wherein Z is an alkylenic or cycloalkylenic radical can be prepared according to what described, for instance, by I.L. Knunyants et al in Izv. Akad. Nauk. SSSR, Ser. Khim., 1964(2), 384-6, while the bis-olefins containing the (per)fluoropolyoxyalkylenic sequences of formula (II) are described in US patent 3,810,874. The amount of units deriving from such bis-olefins is generally in the range 0.01-1.0%, preferably 0.03-0.5%, still more preferably 0.05-0.2% by mole, calculated with respect to the total amount of the other monomers of the elastomer or plastomer. The bis-olefins of formula (I A) are described in US patent 5,612,419. The fluorinated elastomer and the fluorinated plastomer are obtained by (co)polymerization of olefinic monomers. With fluorinated olefinic monomers are meant all the fluorinated products having at least a double bond C=C, optionally containing hydrogen and/or chlorine and/or bromine and/or iodine and/or oxygen, capable of producing (co)polymers in the presence of radical initiators. Among them we can cite: perfluoroolefins C 2 -C 8 , such as tetrafluoroethylene (TFE), hexafluoropropene (HFP), hexafluoroisobutene; hydrogenated fluoroolefins C 2 -C 8 , such as vinyl fluoride (VF), vinilydene fluoride (VDF), trifluoroethylene, perfluoroalkylethylene CH 2 =CH-R f , wherein R f is a perfluoroalkyl C 1 -C 6 ; chloro- and/or bromo- and/or iodo-fluoroolefins C 2 -C 8 , such as chlorotrifluoroethylene (CTFE) and bromotrifluoroethylene; (per)fluoroalkylvinylethers (PAVE) CF 2 =CFOR f , wherein R f is a (per)fluoroalkyl C 1 -C 6 , for instance trifluoromethyl, bromodifluoromethyl or pentafluoropropyl; (per)fluoro-oxyalkylvinylethers CF 2 =CF-OX, wherein X is a (per)fluoro-oxyalkyl C 1 -C 12 having one or more ether groups, for instance perfluoro-2-propoxy-propyl; perfluorodioxoles. Such fluorinated olefinic monomers can also be copolymerized with non fluorinated olefins C 2 -C 8 , such as ethylene, propylene, isobutylene. The type B segments (elastomeric) can in particular be selected from the following classes (compositions expressed as % by mole): (1) VDF-based copolymers, wherein VDF is copolymerized with at least a comonomer selected from: perfluoroolefins C 2 -C 8 ; chloro- and/or bromo- and/or iodo-fluoroolefins C 2 -C 8 ; (per)fluoroalkylvinylethers (PAVE) or (per)fluorooxyalkylvinylethers above defined; non fluorinated olefins (Ol) C 2 -C 8 ; typical compositions are the following: (a) VDF 45-85%, HFP 15-45%, TFE 0-30%; (b) VDF 50-80%, PAVE 5-50%, TFE 0-20%; (c) VDF 20-30%, Ol 10-30%, HFP and/or PAVE 18-27%, TFE 10-30%; (2) TFE-based copolymers, wherein TFE is copolymerized with at least a comonomer selected from: (per)fluoroalkylvinylethers (PAVE) or (per)fluorooxyalkylvinylethers above defined; hydrogenated fluoroolefins C 2 -C 8 ; fluoroolefins C 2 -C 8 containing clorine and/or bromine and/or iodine atoms; non fluorinated olefins (Ol) C 2 -C 8 ; typical compositions are the following: (a) TFE 50-80%, PAVE 20-50%; (b) TFE 45-65%, Ol 20-55%, VDF 0-30%; (c) TFE 32-60%, Ol 10-40%, PAVE 20-40%. The type A segments (plastomeric) can in particular be selected from the following classes (compositions expressed as % by mole): (1) polytetrafluoroethylene or modified polytetrafluoroethylene containing small amounts, generally in the range 0.1-3%, preferably lower than 0.5%, of one or more comonomers such as, for instance: HFP, PAVE, VDF, hexafluoroisobutene, CTFE, perfluorolalkylethylenes; (2) TFE thermoplastic polymers containing from 0.5 to 8% of at least a PAVE, such as, for instance, TFE and perfluoropropylvinylether and/or perfluoromethylvinylether copolymers, or also TFE/perfluoroalkylethylene copolymers; (3) TFE thermoplastic polymers containing from 2 to 20% of a perfluoroolefin C 3 -C 8 , such as, for instance, FEP (TFE/-HFP copolymer), to which other comonomers having a vinylether structure CF 2 =CF-OR f or CF 2 =CF-OX defined as above can be added in small amounts (lower than 5%); (4) TFE or CTFE copolymers (40-60%) with ethylene, propylene or isobutylene (40-60%), optionally containing as third comonomer a (per)fluoroolefin C 3 -C 8 or a PAVE, in amounts in the range 0.1-10%; (5) polyvinylidenfluoride or modified polyvinylidenfluoride containing small amounts, generally comprised between 0.1 and 10%, of one or more fluorinated comonomers, such as hexafluoropropene, tetrafluoroethylene, trifluoroethylene. The thermoplastic polymers of the classes above indicated, and in particular the TFE-based polymers, can be modified with (per)fluorinated dioxoles, according to the patents US-3,865,845, US-3,978,030, EP-73,087, EP-76,581, EP-80,187. It has been found by Applicants that the mechanical and sealing properties of the manufactured articles, after GAMMA or BETA irradiation, can be further improved by subjecting the articles so obtained to a thermal treatment for 1-6 hours at a temperature 10°-30°C lower than the melting temperature of the plastomer. This treatment can be called annealing. Applicants have also found that the above properties are further incresed if the above thermal treatment is carried on the manufactured articles before subjecting them to GAMMA or BETA irradiation. The present invention will be now better illustrated by the following working examples which have a merely indicative purpose but not limitative of the scope of the present invention. REFERENTIAL EXAMPLE 1 PREPARATION OF THE THERMOPLASTIC FLUOROELASTOMER (FTPE) 1 CONTAINING PVDF AS PLASTOMERIC BLOCK A The thermoplastic fluoroelastomer having the structure A-B-A was prepared according to Example 1 of US Patent 5,612,419 but by modifying the VDF and TFE monomer feeding composition and using perfluoromethylvinylether (MVE) instead of HFP, to obtain a final composition of block B ( 19 F NMR analysis): VDF 61% by mole MVE 19% by mole TFE 20% by mole Moreover the polymer contains: Bis-olefin 0.07% by mole. The polymer Mooney viscosity is equal to 12 Mooney points (A-STM D 1646). The final thermoplastic fluoroelastomer contains, in addition to the elastomeric B phase above specified, also a thermoplastic phase based on PVDF in the amount of 20% by weight on the total amount of the two phases and obtained as described in Example 1 of the above mentioned patent. The FTPE 1 melting temperature is 160°C. The material results to be under the form of thick powder coming from the coagulation and washing of the polymerization latex. REFERENTIAL EXAMPLE 2 FTPE 2 PREPARATION CONTAINING E/TFE/MVE AS PLASTOMERIC BLOCK A The thermoplastic fluoroelastomer with A-B-A structure was prepared as in Example 1 but modifying the amounts of the fed monomers so that to obtain the compositions indicated below. In particular the fluoroelastomeric segment B has the following composition ( 19 F NMR analysis): VDF 57% by mole MVE 23% by mole TFE 20% by mole Bis-olefins 0.11% by mole Mooney viscosity = 36 The final thermoplastic fluoroelastomer contains, in addition to the elastomeric B phase, also a thermoplastic phase which instead of the PVDF of Example 1, has the following molar composition: ethylene E 41% by mole tetrafluoroethylene TFE 50% by mole perfluoromethylvinylether MVE 9% by mole The amount of plastomeric phase is 25% by weight on the total amount of the two phases. The FTPE 2 second melting temprature is 180°C. The material results to be under the form of a thick powder coming from the coagulation and washing of the polymerization latex. EXAMPLE 1A 100 phr of FTPE 1 polymer are mixed in a laboratory single screw extruder with 3 phr of TAIC (triallylisocyanurate) and then pelletized with the same equipment. With the obtained formulation, 100x100x2 mm specimen have been compression molded for the mechanical tests: M100 means 100% elongation modulus, M200 means 200% elongation modulus, CR means stress at break, AR means elongation at break, Shore A hardness. Moreover disks have been molded (13 mm of diameter and 6 mm of thickness) for compression set tests at high temperature carried out according to VDA 675 216-B standard or ASTM D 395 method B. The sheets and the disks have been then irradiated with GAMMA rays (Co-60), with dosages 1, 5 and 10 Mrad. The results are reported in Table 1 in which the comparison is carried out also with the pelletized polymer not containing crosslinking coagents and not submitted to crosslinking with radiations. after molding in press (comparison) after 3 phr TAIC 1Mrad 5 Mrad 10Mrad Mech. prop. after press 180°C x 11min (ASTM D 412-83) M 100 (MPa) 2.3 7.2 12.5 15.3 M 200 " 3 11.5 - - CR " 3.1 14.9 18.2 19 AR % 231 281 167 131 Hardness points 58 79 86 87 C disk set (VDA ) 150°C x (22+2)h % 101 78 72 70 EXAMPLE 1B One proceeds as in Example 1A except that the specimen and the disks are irradiated with BETA rays (4,5 MeV), with dosages 10.9; 28.4; 60.4; 120.9 KGy (1 Mrad = 10 KGy) The results are reported in Table 2 and the compression set data at the different temperatures in Table 3. Mechanical properties CR (MPa) AR (%) M50 (MPa) M100 (MPa) 10.9 KGy 10.5 299 1.8 3.6 28.4 " 12.7 208 2.4 5.5 60.4 " 12.5 161 2.9 7.4 120.9 " 12.9 131 3.6 9.6 Compression set according to VDA standard 100°C (%) 125°C (%) 150°C (%) 10.9 KGy 61 72 28.4 " 48 58 60.4 " 41 66 120.9 " 36 60 EXAMPLE 2A The FTPE 2 polymer is subdivided in 3 parts, each of them is mixed by means of a laboratory single screw extruder with different kinds of coagents in amounts of 3 phr. The coagents used are TAIC, BOSA and 1,6-divinylperfluorohexane (indicated with BO in the Tables). With the formulations obtained, 100x100x2 mm specimen have been compression molded for mechanical tests. Moreover disks have been compression molded for compression set tests at high temperature. The specimen and the disks have then been irradiated with GAMMA rays (Co-60) with a 5 Mrad dosage. The results are reported in Table 4 in which the comparison is carried out also with the pelletized polymer not containing crosslinking coagents. Mechanical properties and the compression set for all the samples are carried out also on non irradiated specimen and disks. COMPARATIVE 3 phr BOSA 3 phr BISOLEFIN 3 phr TAIC Mech. prop. after press 180 °C x 11 min (ASTM D412-83) M 100 (Mpa) 2.8 3 2.4 2.9 C.R. " 6.2 7.7 6.9 7 A.R. % 588 573 571 570 Hardness points 68 71 66 69 C.set at 150 °C on disks ASTM 24h % 98 102 99 101 VDA(22+2)h % 108 110 112 112 Mech. prop after radiation with 5 Mrad of GAMMA rays M 100 (Mpa) 2.6 3.6 2.2 4.3 C.R. " 7.8 12.7 7.7 14.1 A.R. % 422 383 556 283 Hardness points 67 71 62 74 C. set at 150°C on disks after radiation of 5 Mrad of GAMMA rays ASTM 24h % 75 66 87 59 VDA(22+2)h % 102 95 93 98 EXAMPLE 4 One proceeds as in Example 3 except that the sheets and the disks are radiated with BETA rays (4,5 MeV), with dosages 50, 250, 500 KGy (1 Mrad = 10 KGy). The mechanical properties are reported in Tab. 5 and the compression set data measured at the different temperatures in Tab. 6. Mechanical properties C.R. (MPa) A.R. (%) M 50 (MPa) M 100 (MPa) BO Not radiated 6.9 671 - 2.4 50 KGy 11.1 321 2.3 3.5 250 " 10.1 160 2.8 4.9 500 " 6.8 102 3.6 6.8 BOSA Not radiated 7.7 573 - 3.0 50 KGy 13.8 356 2.6 3.9 250 " 13.5 141 4.3 8.0 500 " 9.9 78 6.0 - TAIC Not radiated 7.0 570 - 2.9 50 KGy 14.4 238 3.0 4.9 250 " 8.7 89 5.0 - 500 " 8.8 66 6.8 - Compression set VDA (22+2) h 100 °C (%) 125°C (%) BO 50 KGy 88 93 250 " 61 71 500 " 58 64 BOSA 50 KGy 83 100 250 " 63 79 500 " 62 72 TAIC 50 KGy 79 90 250 " 63 73 500 " 64 73

Claims: Manufactured articles obtainable from a composition consisting of: 1) 100 phr of a fluorinated thermoplastic elastomer having a block structure with at least a fluorinated polymeric segment of B type having elastomeric properties and at least a fluorinated polymeric segment of A type having plastomeric properties, whereby in at least one among the A type or B type segments monomeric units are present which derive from a bis-olefin having the general formula: wherein: R 1 , R 2 , R 3 , R 4 , R 5 , R 6 , equal to or different from each other, are H or alkyls C 1 -C 5 ; Z is an alkylene or cycloalkylene radical C 1 -C 18 , linear or branched, optionally containing oxygen atoms, or a (per)fluoropolyoxyalkylenic radical; 2) from 0.1 to 40 phr of a crosslinking agent able to give peroxidic crosslinking of fluoro-elastomers; and subsequent radiation of the manufactured article by GAMMA radiations, from 1 to 50 Mrad, or BETA radiations from 10 to 500 KGy. Manufactured articles according to claim 1 wherein the component 2) amount ranges from 1 to 10 phr. Manufactured articles according to claims 1 and 2 wherein the composition contains additives such as fillers, stabilizers, antioxidants, pigments, thickeners and plastifiers. Manufactured articles according to claims 1-3 wherein the crosslinking agents are selected from 1,6-divinylperfluorohexane; triallyl-cyanurate; triallyl-isocyanurate (TAIC); tris(diallylamine)-s-triazine; triallylphosphite; N,N-diallyl-acrylamide; fluorinated bis-olefins, N,N'-bisallylbicycle-oct-7-ene-disuccinimide (BOSA); N,N,N',N'-tetraallyl-malonamide; trivinyl-isocyanurate; and 2,4,6-trivinyl-methyltrisiloxane. Manufactured articles according to claim 4, wherein the crosslinking agents are selected from TAIC, 1,6 divinylperfluorohexane and BOSA. Manufactured articles according to claims 1-5, wherein the bis-olefin is present in the fluorinated polymeric segment of B type having elastomeric properties. Manufactured articles according to claim 1, wherein in the bis-olefin Z is selected from a perfluoroalkylenic radical C 4 -C 12 , while R 1 , R 2 , R 3 , R 4 , R 5 , R 6 are hydrogen or (per)fluoropolyoxyalkylenic radical of the formula: - (Q) p -CF 2 O-(CF 2 CF 2 O) m (CF 2 O) n -CF 2 -(Q) p - wherein: Q is an alkylenic or oxyalkylenic radical C 1 -C 10 ; p is 0 or 1; m and n are integers such that the m/n ratio is in the range 0.2-5 and the molecular weight of said (per)fluoropolyoxyalkylenic radical is in the range 500-10,000. Manufactured articles according to claim 7, wherein the amount of units deriving from the bis-olefin is in the range 0.01-1.0% by mole, calculated with respect to the total amount of the other monomers of the elastomer or the plastomer. Manufactured articles according to claims 1-8 wherein the fluorinated elastomer and the fluorinated plastomer blocks are obtained by (co)polymerization of fluorinated olefinic monomers having at least a double bond C=C, optionally containing hydrogen and/or chlorine and/or bromine and/or iodine and/or oxygen, capable of producing (co)polymers in the presence of radical initiators. Manufactured articles according to claim 9 wherein the fluorinated olefinic monomers are selected from: perfluoroolefins C 2 -C 8 , such as tetrafluoroethylene (TFE), hexafluoropropene (HFP) and hexafluoroisobutene; hydrogenated fluoroolefins C 2 -C 8 , such as vinyl fluoride (VF) , vinylidene fluoride (VDF), trifluoroethylene and perfluoroalkylethylene CH 2 =CH-R f , wherein R f is a perfluoroalkyl C 1 -C 6 ; chloro- and/or bromo- and/or iodo-fluoroolefins C 2 -C 8 , such as chlorotrifluoroethylene (CTFE) and bromotrifluoroethylene; (per)fluoroalkylvinylethers (PAVE) CF 2 =CFOR f , wherein R f is a (per)fluoroalkyl C 1 -C 6 , such as trifluoromethyl, bromodifluoromethyl or pentafluoropropyl; (per)fluoro-oxyalkylvinylethers CF 2 =CFOX, wherein X is a (per)fluoro-oxyalkyl C 1 -C 12 having one or more ether groups, such as perfluoro-2-propoxy-propyl; and perfluorodioxoles. Manufactured articles according to claims 9-10 wherein the fluorinated olefinic monomers are copolymerized in the presence of non fluorinated olefins C 2 -C 8 , such as ethylene, propylene, isobutylene. Manufactured articles according to claims 9-11 wherein the B type segments (elastomeric) are selected from the following classes : (1) VDF-based copolymers, wherein VDF is copolymerized with at least a comonomer selected from: perfluoroolefine C 2 -C 8 ; chloro- and/or bromo- and/or iodo-fluoroolefins C 2 -C 8 ; (per)fluoroalkylvinylethers (PAVE) or (per)fluorooxyalkylvinylethers defined above; non fluorinated olefins (Ol) C 2 -C 8 ; and (2) TFE-based copolymers, wherein TFE is copolymerized with at least a comonomer chosen from: (per)fluoroalkylvinylethers (PAVE) or (per)fluoro-oxyalkylvinylethers above defined; hydrogenated fluoroolefins C 2 -C 8 ; fluoroolefins C 2 -C 8 containing clorine and/or bromine and/or iodine atoms; non fluorinated olefins (Ol) C 2 -C 8 . Manufactured articles according to claims 9-12 wherein the type A segments (plastomeric) are selected from the following classes (compositions expressed as % by moles) : (1) polytetrafluoroethylene or modified polytetrafluoroethylene with amounts in the range 0.1-3%, of one or more comonomers such as HFP, PAVE, VDF, hexafluoroisobutene, CTFE, perfluorolalkylethylenes; (2) TFE thermoplastic polymers containing from 0.5 to 8% of at least a PAVE, such as TFE/perfluoropropylvinylether copolymers and/or TFE/perfluoromethylvinylether copolymers, or also TFE/perfluoroalkyllethylene copolymers; (3) TFE thermoplastic polymers containing from 2 to 20% of a perfluoroolefin C 3 -C 8 , such as FEP (TFE/HFP copolymer), to which amounts lower than 5% of other comonomers having a vinylether structure CF 2 =CF-OR f or CF 2 =CF-OX above defined can be added; (4) TFE or CTFE copolymers (40-60%) with ethylene, propylene or isobutylene (40-60%), optionally containing as third comonomer a (per)fluoroolefin C 3 -C 8 or a PAVE, in amounts in the range 0.1-10%; (5) polyvinylidenfluoride or modified polyvinylidenfluoride with amounts in the range 0.1-10%, of one or more fluorinated comonomers, such as hexafluoropropene, tetrafluoroethylene, trifluoroethylene. Manufactured articles according to claim 13 wherein the thermoplastic polymers are modified with (per) fluorinated dioxoles. Manufactured articles according to claims 1-14 wherein the manufactured articles before being subjected to irradiation treatment are subjected to a thermal treatment for 1-6 hours at a temperature 10°-30°C lower than the melting point of plastomer A. Manufactured articles according to claims 1-15 wherein the manufactured articles after being subjected to irradiation treatment are subjected to a thermal treatment for 1-6 hours at a temperature 10°-30°C lower than the melting point of plastomer A. Manufactured articles according to claim 12 wherein the VDF-based copolymers are selected from (compositions expressed as % by moles): (a) VDF 45-85%, HFP 15-45%, 0-30% TFE; (b) VDF 50-80%, PAVE 5-50%, TFE 0-20%; (c) VDF 20-30%, Ol 10-30%, HFP and/or PAVE 18-27%, TFE 10-30%; and the TFE-based copolymers are selected from (compositions expressed as % by moles): (a) TFE 50-80%, PAVE 20-50%; (b) TFE 45-65%, Ol 20-55%, 0-30% VDF; (c) TFE 32-60%, Ol 10-40%, PAVE 20-40%. Use of a composition consisting of: 1) 100 phr of a fluorinated thermoplastic elastomer having a block structure with at least a fluorinated polymeric segment of B type having elastomeric properties and at least a fluorinated polymeric segment of A type having plastomeric properties, whereby in at least one among the A type or B type segments monomeric units are present which derive from a bis-olefin having the general formula: wherein: R 1 , R 2 , R 3 , R 4 , R 5 , R 6 , equal to or different from each other, are H or alkyls C 1 -C 5 ; Z is an alkylene or cycloalkylene radical C 1 -C 18 , linear or branched, optionally containing oxygen atoms, or a (per)fluoropolyoxyalkylenic radical 2) from 0.1 to 40 phr of a crosslinking agent able to give peroxidic crosslinking of fluoro-elastomers; for the preparation of manufactured articles having improved sealing properties at high temperatures by irradiating the composition with GAMMA radiations, from 1 to 50 Mrad, or BETA radiations from 10 to 500 KGy. Use according to claim 18 wherein the component 2) amount ranges from 1 to 10 phr. Use according to claim 18 wherein the composition contains additives such as fillers, stabilizers, antioxidants, pigments, thickeners and plastifiers. Use according to claim 18 wherein the crosslinking agents are selected from 1,6-divinylperfluorohexane; triallyl-cyanurate; triallylisocyanurate (TAIC); tris(diallylamine)-s-triazine; triallylphosphite; N,N-diallyl-acrylamide; fluorinated bis-olefins, N,N'-bisallylbicycle-oct-7-ene-disuccinimide (BOSA); N,N,N',N'-tetrallyl-malonamide; trivinylisocyanurate; and 2,4,6-trivinyl-methyltrisiloxane. Use according to claim 21, wherein the crosslinking agents are selected from TAIC, 1,6-divinylperfluorohexane and BOSA.

Inventors: ALBANO MARGHERITA, ARCELLA VICENZO, GAYER UDO, SCHUH THOMAS, ALBANO, MARGHERITA, ARCELLA, VICENZO, GAYER, UDO, SCHUH, THOMAS
Applicants: AUSIMONT SPA, DAIMLER CHRYSLER AG, AUSIMONT S.P.A., DAIMLERCHRYSLER AG
Application year: 1998
Main classification: C08L27
IPC codes: C08F293, C08F2, C08K5, C08L53, C08F4, C08J7