TITANIUM BASED METAL HEAT EXCHANGERS AND METHOD OF MANUFACTURE

Abstract: This invention relates generally to the field of light weight heat exchangers useful for operation in excess 950 DEG F and more particularly to titanium metal based heat exchangers. The light weight titanium based metal heat exchanger can be coated with an aluminum coating that is subsequently converted to a titanium aluminide surface and can operate as a heat exchanger at temperatures up to 1450 DEG F. A solgel coating can be applied as a wash coat over the titanium or the titanium aluminide surface to inhibit further oxidation and provides additional protection against scratching damage during handling. These oxidation resistant coatings may also be applied to the braze clad titanium.

Description: TITANIUM BASED METAL HEAT EXCHANGERS AND METHOD OF MANUFACTURE Field of the Invention This invention relates generally to the field of light weight heat exchangers and more particularly to titanium based metal heat exchangers This invention teac es the use of oxidation resistance titanium based metal heat exchanger components foi extended ana reliable operation in aerospace application in a temperature range in excess of the 700- 900°F the tempei ate range generally considered to be the maximum operating temperature tor titanium metal components The present invention provides a practical light weight and reliable heat exchanger comprising titanium, or alloys of titanium or braze clad titanium Background of the Invention Heat exchangers can be used as core elements in larger svstems such as the heat regenerators or recuperators that are useful to capture, transfer and recycle heat from one fluid such as an exhaust fluid, to another fluid, such as an intake fluid Valuable use of otherwise waste exhaust heat can be made by for instance, using a heat exchanger to preheat an intake fluid Light weight and reliable heat exchangers are particularly useful in aerospace applications to contribute to improved fuel efficiency In many application it is critical that the two fluids remain separated to avoid contamination or other unintended results Cracks in the heat exchanger can give rise to loss of efficiency as well as fluid contamination Titanium and its alloys comprise light weight material and can provide a reduction of up to 40% over the comparable weight of conventional high temperature heat exchangers, allowing for an even broader range of heat exchanger use in aircraft applications to for instance improve fuel effιcιenc\ However titanium is heretofore considered unsuitable for such heat exchanger applications as the oxidation oi mtπding of the titanium significantly reduces the required material properties and compromises structural integrity repeated thermal cycling of a heat exchanger between operating temperatures in excess of 700- 900 °F and ambient temperature causes the metal components to crack and heat exchanger performance to deteriorate Titanium is light weight and corrosion resistance however its operating temperatures are low Currently, titanium is not used for high temperature (in excess of 900°F ) heat exchangei applications such as aircraft applications because titanium exhibits a propensity to rapidly oxidize at the required operating temperatures Oxidation of titanium results in a reduction in ductility and then strength so that a titanium heat exchanger fabricated without a means of protection from oxidation will deteriorate in structural integrity at temperatures in excess of 700- 900 °F Objects and Summary of the Invention It is therefore, an object of the present invention to overcome the above-noted known drawbacks of titanium to produce a useful and reliable titanium metal based heat exchanger device It is another object of the present invention to provide a titanium based heat exchanger that has been specially treated to achieve oxidation resistance to thereby avoid a deterioration in the metal properties that is otherwise attributed to detrimental oxidation and or nitπding It is still another object of the present invention to provide a titanium based heat exchanger wherein that is operable in excess of the 700 -900°F a temperature range up to 1400°F It is a further object of the present invention to provide a titanium based heat exchanger wherein titanium based metal parts or core are specially treated to form an oxidation and nitride resistant surface covering In one embodiment the oxidation resistant surface covering can comprise a conversion coating such a gaseouslv deposited aluminum coating that is heat treated to form a titanium aluminide oxidation and nitride resistant surface completely covering all of the complex shapes of a heat exchanger In an alternate embodiment of the present invention provides a titanium based heat exchanger the oxidation and nitride resistant surface covering can comprise an alumina, silica 01 zircoma solgel coating In a further preferred embodiment of the present invention provides a titanium based heat exchanger having titanium aluminide surface coateα with an oxidation and nitride resistant surface covering comprising an alumina, silica or zircoma solgel coating It is a further obiect of the present invention to provide a titanium based heat exchangei wherein the titanium brazes are also protected with a oxidation and nitride resistant surface covering to avoid embπttlement and deterioration A-s is well known during assembly, a the heat exchanger parts are braze coated and stacked to form an assembK The stacked assembly is then heat treated to from a brazed and unified whole In the brazing process, titanium material can be wicked to concentrated in a braze fillet It is thus important that the fillets also be treated to form an oxidation and nitride resistant surface covering to avoid deterioration The afore described conversion coating can be applied bv various methods For instance an aluminum based conversion coating can be applied bv gaseous deposition and solgel type coatings can be applied by dip coatings, both of which have been found to be effective in achieving the desired uniform coatings for establishing oxidation and nitride resistant surface coverings for the fillets It is a further obiect of the present invention to provide a titanium based heat exchanger wherein the titanium is specially treated and covered with a solgel coating of for instance silica alumina or zircoma which is deposited from a liquid with a low viscosity so allowing the complete coverage of the complex shape of the heat exchanger Further, this solgel coating provides oxidation protection when applied either directly to the titanium titanium aluminide or brazed titanium Brief Description of the Drawings The invention will become more readily apparent from the following description of preferred embodiments thereof, illustrated, bv way of examples, in the accompanying drawings in which Fig 1 illustrates a first embodiment of a titanium based metal heat exchanger according to the present invention in a sectional view and in a schematic fashion Fig 2 illustrates how oxidation of the oxidation resistant allov but uncoateα Tι21 S results in a brittle allov with no strength Fig 3 illustrates how the aluminum coating diffuses into the titanium while the titanium diffuses out note also the aluminum oxide outer layer Fig 4 illustrates how titanium alloys treated in accordance with the invention and exposed to 1300°F even for 4 000 hours are oxidation resistant and results in an acceptable weight gam, even for the easily oxidizable alloy Ti 32 5 Fig 5 illustrates how the only a solgel coating provides oxidation protection at 1300°F for 1 92 hours to Tι21 S and how the weight gain for both the solgel zircoma coating and solgel alumina coatings are comparable Fig 6 illustrates how the weight gam of a complex honeycomb fabricated from Tι32 5 and aluminum coated is the same per unit area as for a simple shape indicating that the aluminum coating has completely covered the complex shape and can proyide oxidation protection to the complex shape The loss in weight of uncoated Ji 32 5 indicates that oxide scale has fallen off the sample Fig 7 illustrates how the coatings withstand thermal cycling between 1300°F and room temperature every 15 minutes for 500 hours and the resultant weight gam or loss is the same as for static oxidation Description of the Preferred Embodiments With reference to the drawing wherein like parts are identified bv the same reference characters it can be seen that Fig 1 illustrates in perspective and in a schematic fashion the first embodiment of a titanium based metal heat exchanger 10 in accordance with the present invention The titanium based metal heat exchanger 10 comprises a pluralm of flat parallel plates i 1 are separated from each other bv spacers or fin sheets 12 and stacked in alternation to form structure comprised of alternating plates 1 1 and spacers or fin sheets 12 The alternating plates 1 la and 1 l b define a first fluid flow passages 13 therebetween and the alternating plates 1 lb and 1 l c define a second fluid flow passages 14 therebetween The plates 1 1 are preferably fabricated of a titanium based metal material in any desired configuration although rectangular shapes are typical It is intended that the plates 1 1 be leak proof and stacked to form alternate passes for the fluids 19 and 20 to flow therebetween Surface enhancements in the form to increase surface area or roughness can be added to increase heat transrei Braze clad bonding can be used to attach the fin sheets 12 to the plates 1 i and form a unified and structurally sound heat exchanger core Before stacking, the plates 1 1 and mating surfaces of the fin sheet 12 can be brazed coated to facilitate the subsequent assembly a brazed heat exchanger core In accordance with the present invention, the fin sheets 12 are preferably formed bv foi instance die stamping a titanium based metal sheet like stock The fin sheets 12 can be inserted between alternating plate 1 1 to separate adjacent plates 1 1 and form the respective fluid flow passagewavs 1 3 and 14 Tvpicallv the fins 12 comprise a corrugated or wa\ e like structure that is preferably continuous and uniform throughout the sheet Each fin 12 has a substantially planai heat transfer surface 12a that is inserted within a fluid flow such that the plane of the fin is parallel to the direction of the fluid flow, to thereby minimize the flow resistance that the fin would otherwise impose on the flowing fluid The fin sheet 12 can be made in other geometry ' s to enhance the transfer of heat from the fluids to the heat exchanger material Surface enhancements such as artificial surface roughness or louvers may be included to improve hat transfer It is intended that the corrugated fin sheets 12 can be placed between adiacent plates 1 1 and bonded to the plates 1 1 to form an integrated structure Braze clad bonding can be used to attach the fin sheet 12 to the plate 1 1 and form a unified and structurally sound heat exchanger core In operation a fluid 19 flows between plates 1 t a and 1 l b while fluid 20 flows between plates 1 l b and 1 l c For easier understanding in this example the two passageways formed b\ the plates 1 1 are identified as the hot passageway 13 and the cold passagewav ' 4 respectively The second passagewav 14 is most frequently oriented to facilitate the flow of the second fluid 20 transverse to the flow of the first fluid 19 in the first passagewav 13 For instance the fluids 19 an d 20 can flow at an angle of approximately 90° to eacn other or the fluids can flow at an angle of approximately 180" to each other so that the flows are nearly parallel and establish a counterflow heat exchanger In a preferred embodiment the plates 1 1 can be successively stacked to form alternating first and second passageways 19 and 20 until the assembly as a whole provides the desired heat transfer or exchange capability Provision can be made to assist the fluid entry into and exit from the heat exchanger 10 Typically manifolds are used to fulfill this function Counterflow heat exchangers wherein two different fluid enter and exit on the same face of the core require the various flow control or blocking constructions to enable fluids to be delivered bv a manifolds to the desired fluid pass End bars to can be applied to an end of a passage or a portion of a passage to restrict or close a portion of the passage entrv or exit to ensure fluids flow are confined to the selected pass Othei special features can be such as those disclosed US Patent 4 246 963 to Anderson for a Heat Exchanger and US Patent 4 352.273 to Kinsell for a Fluid Conditioning A-pparatus and System assigned to the assignee of the present invention and the disclosure of which are incorpoi ated b\ reference herein can also be includes in the titanium based metal heat exchanger of the present invention In operation, the first and second fluids 19 and 20 respectively flowing in the first and second passageways 13 and 14 respectively are preferably at different temperatures to facilitate the heat transfer from one passage to the othei For instance the first fluid 19 can be hotter than the second fluid 20 When this hotter fluid 19 flows in the first passageway 13 heat is transferred from the fluid to the first fins 12 and to the plates 1 l a and 1 l b Heat is then transferred from this second plate 1 lb to the fins 12 in the passageway 14 and to the cooler fluid 20 The second fluid 14 exits and flows from the heat exchanger 10 and carries the exchanged heat awav from the heat exchanger 10 allow ing a heat energy to be continuous transferred from a continuous flow of hot fluid to continuous flow of cold fluid The two fluids 19 and 20. in addition to being at inherently unequal temperatures, are also at unequal pressures The plates 1 1 must be of a thickness sufficient to provide structural integrity between fluid passages 13 and 14 but sufficiently thin to minimize weight and not interfere with heat transfer Plate thickness must be gauged to account for the fluid pressure difference between passageways 13 and 14 as this difference tends to bend the plates The close spacing of the fins 1 results in small unsupported cross sectional areas of the plates 1 1 Therefore, the fins 12 enhance structural integrity and help keep the plates 1 1 flat The present invention maintains adequate ductility so that the piates can handle structural forces tvpicallv seen for high temperature heat transfer applications Further concerns about the overall thermal gradient of the heat exchanger 10 must also be taken into account The heat exchanger 10 transfers heat from one fluid to the othei Therefore if the hot fluid 19 enters the passagewav 13 as shown in the drawing, the inlet end of passage 1 3 is hotter than the exit end Similarly the cold fluid 20 entering the passagewav 14 is colder at the inlet and warmer at the exit Thus, the cornet 22 of the heat exchanger where the hot fluid enters and the cold fluid exits mav be at a much higher temperature than the opposite corner 24 whei e the cold fluid enters and the hot fluid exits This thermal gradient within the heat exchanger 10 structure reduces the amount of heat which can be transferred In metal heat exchangers the hot section expands much more than the cold section which sets up adverse stresses within the material and reduces heat exchanger life Repeated cycling of temperatures and pressures caused bv varying operating conditions further reduces strength and life by the repeated expansion and contraction of all parts of the heat exchanger If oxidation of the titanium is not prevented the life of the heat exchanger and its ability to withstand thermal cycling is greatly reduced The degradation of the mechanical properties of uncoated Tι21 S as a result of oxidation is shown in Fig 2 obviouslv the life of an heat exchanger would be very shoπ once oxidation has reduced the ductility of the titanium to zero Use of a titanium based metal for such severe heat exchanger application is facilitated b\ the present invention wherein the titanium based metal is specially treated to avoid embnttlement More particularly oxidation of the titanium or braze clad titanium is prevented by a coating 30 that can be applied to protect or transform the titanium surface In this example conversion coating in a gaseous phase can be applied to and deposited on an assembled and brazed heat exchanger assembK to ensure coverage ot all of the exposed pans of the complex heat exchanger configuration This coated assembly is then heat treated in a vacuum furnace ( not shown) to activate the conversion coating and transform the titanium into an oxidation resistant titanium aluminide with an alumina surface which also prevents oxidation In this example the gaseousK deposited conversion coating can be aluminum in a thickness of 1 -40 micron-, Upon heat treatment and activation the aluminum interacts with the titanium to form an oxidation resistant titanium aluminide The resultant coating provides oxidation resistance both at 1300 and 1400°F as the mechanical properties of Al coated Tι21 S after 200 hour exposure to temperature show Table 1 Table 1 The mechanical properties of uncoated and Al coated Tι21 S after exposure to 1300 & 1400 °F for 192 hours The resulting surface structure of the titanium metal component is illustrated in Fig 3 when in the aluminum migrates into the surface of the titanium metal to form transition zone when in concentration bv weight of titanium gradually decreases from 100° o in the bodv to less than 10% near the surface while the concentration bv weight of aluminum gradually decreases from 100% at the surface to less than 10% near in the bod\ The migration and transformation of titanium to titanium aluminide occurs at temperatures around 1200°F There is also a surface layer of an aluminum oxide left from the aluminum coating, which also provides oxidation protection Heating and cooling must be should be controlled to avoid cracking the aluminide laver The conversion coating can be successfully applied by mechanical processes such as roll bonding, or gaseous processes, such as physical vapor deposition (PVD) or low temperature chemical vapor deposition (LTCVD) preferably in a layer thickness in the range of ~ 1 to 40μm lavei The deposited aluminum can be transformed to titanium aluminide bv heat treatment under vacuum to around 1200 °F with a hold Typically heating is at 200°F per hour after 1000°F followed by a 30 minutes hold and the cooling rate is also around 200°F down to 1000°F Heat treatment of the conversion coating results in the establishment of an extremely oxidation resistant coating which protects the titanium from further oxidation and embπttlement even after exposure for 4 000 hours at 1300°F, as is shown in Fig 4 The present invention can provide oxidation protection not only to the oxidation resistant titanium allov such as Tι21 S, but also to pure Ti and simple alloys such as Ti 32 5, as is shown in Fig 4 The mechanical properties of these samples are given in Table 2 Table 2 The mechanical properties of Al coated Tι21 S and Ti 32 5 after exposure to 1300°F for 4 000 hours In an alternate embodiment the coating 30 can comprise a zircoma based solgel dip coating that can be applied as a wash coat, directly to the titanium or a titanium, aluminide surface, to again ensure that the entire complex shape of the heat exchanger 10 is completely coated Unlike other solgel coatings, a zircoma based coating can be applied at a low temperatures 600 - 1200°F, so oxidation of the uncoated titanium is avoided Further the zircoma coating may be rapidly heated and cooled during application The zircoma coating may be fired bv placing it directly in a pre heated furnace and after around a 30 mm hold directly removed The solgel coating 30 is preferably applied through multiple dips \ preferred process applies the solgel coating in three (3) dips wherein the coatings of the first 2 dips are fired at a low temperature 600 - 1000°F for 30 minutes (time) a temperature at which the Ti has minimum or no oxidization the final or third dip can therefore be fired in air at 600 to 1200°F for 30 minutes (time) with no oxidation of the titanium This rapid firing in air is a marked advantage over the usual 1300 to 1500°F firing which would have to have been carried out in a vacuum furnace Alternate solgel coatings are alumina or silica Alumina can be readily applied directly to the titanium alloy or to the titanium aluminide coating to provide oxidation protection Its advantage is that it has a higher thermal conductivity than zircoma A disadvantage of alumina is that the final firing preferable occurs at higher temperatures than the zircoma, 1000 to 1300°F however, because the initial coatings can also be carried out at a low temperature the final firing can be carried out in air like the zircoma with no oxidation of the titanium as for the zircoma we have reduced the firing temperature below the usual 1500°F which would have necessitated a vacuum furnace to avoid oxidation of the titanium and would also have deteriorated the mechanical properties because of metallurgical considerations such ass over aging The comparable oxidation resistance of zircoma and alumina coatings applied to bare Ti 21 S is illustrated in Fig 5 The conversion coatings not only provide oxidation resistance for an elevated temperature titanium alloy Ti 21 S but also to conventional alloys, such as Ti 3 2 5 The coatings also provide oxidation resistance at 1300°F to braze coated titanium In a method of manufacturing a light weight titanium based metal heat exchanger for operation in excess of 975°F comprising, first second and third plates at least one of which is titanium based A first spacer 12 can be inserted between the first and second plates 1 l a and 1 l b respectively for separating the first and second plates 1 l a and 1 lb respectively to form a first passage 13 for receiving a first fluid 19 there through A second spacer 12 inserted between the second and third plates 1 lb and 1 l c respectively to form a second passage 14 for receiving a second fluid 20 there through, thereby forming a heat exchanger core wherein heat is transferred from the first fluid 19 by conduction through the second plate 1 lb to the second fluids 20 The heat exchanger core 10 can then be covered with an appropriate coating that can be gaseouslv or dip deposited on all exposed titanium surfaces The zircoma solgel coating can be applied bv a wash coat The heat exchanger core is dipped m a solution with a carefully controlled viscosity and then slowly withdrawn so a thin coating is applied after drying, it is fired at 1000°F In a typical solgel process, the coated titamum based substrate are hydrolyzed and subsequently polymerized in a controlled humidity environment The polymeric films are dried and sintered at elevated temperature to pyloπze off the organic groups and form a thin protective oxide film Work on an actual heat exchanger showed that conventional solgel solutions had too high a viscosity ( -200 centipose) with the result that not onlv was complete coating of the complex shape difficult and instead of a thin coating as formed on a simple geometry the solgel could not be drained from inside the passages and so dried to a thick layer which blocked the passages Blowing air through the passages alleviated, but did not avoid this problem It was found essential that the viscosity of the solgel be carefully controlled to a low value, preferably below 100 centipose Further this solgel coating provides oxidation protection when applied either directly to the titanium titanium aluminide or brazed titanium Cracking of the aluminide layer is a particular concern as it will result in oxidation of the titamum in the cracked area, and as oxygen diffuses quickly in titanium and one crack can result in the oxidation of the complex part Our initial work on aluminum conversion coating resulted after much experimentation, in a coating which, due to these cracks, had at best onlv 1% elongation after exposure to 1300°F for 192 hours compared to the 10% we routinely obtain now These problems have been overcome by careful heating and cooling duπng conversion and transformation and by optimization of the coating thickness The resultant coatings avoid oxidation up to 1500°F rather than the 1000 °F usually investigated Solgel coatings have also been looked at previously The present zircoma and alumina coatings however have the advantage of a rapid firing cycle at a " low " temperature such as 700 - 1300°F degrees Control of coating thickness to produce a uniform thin layer has reduced the number of cracks common in solgel coatings Presumably because of these cracks, our initial work did not provide protection to "bare" titanium An important refinement of the disclosure is the fact that the aluminum and solgel coatings can be applied to either bare titanium or to braze clad titanium Heat exchangers are fabricated by brazing together sheet and tubes, therefore most of their 'tubes and "fins" are coated with the braze alloy This wide and sudden variation in surface composition is a unique situation It is therefore essential that the braze alloy can also be protected from oxidation as well as the bare metal, which usually is at the manifolds and ends of the fins An important aspect of this work is the development of coatings and thermal cycles that are compatible with the titanium alloy and also with the braze alloy Protection of one, but not the other would be of no benefit and separate coatings for each are not technically or economically desirable due to the complexity of the heat exchangers shape and the complex transitions from bare to braze clad titanium Not only do the aluminum and solgel coatings protect both from oxidation, but they are able to withstand the different thermal stresses due to thermal cycling set up by either titanium or braze clad titanium Braze clad Ti 21 S was aluminum coated using gaseous deposition and then transformed by the application of heat to an aluminde, as described The mechanical properties after exposure to 1300°F for 192 hours are excellent showing no loss in properties either from oxidation or the braze, Table 3 Table 3 The mechanical properties of Al coated braze clad Ti21 S after exposure to 1300°F for 4,000 hours To fabricate an heat exchanger it is essential that protection be obtained for a complex geometry part To demonstrate the feasibility of coating such a complex shape, honeycomb shapes were fabricated from the simple alloy Ti 32 5, these were then aluminum coated and heat treated to form the aluminide These parts were exposed to 1300°F for 192 hours with the weight gain of the part being measured Even though the honeycombs have a complex shape, their surface area is relatively well known Using this and the weight gain we calculated the weight gain per surface area It was identical to that obtained for simple flat test bars, Fig 6 showing that the aluminum coating had coated and more importantly protected the entire honeycomb Ti 32 5 was used for this honeycomb because it does oxidize easily and differences in oxidation protection would show up as a large difference in weight gain To determine if even more complex shape of an heat exchanger could be coated a sample heat exchanger made from steel was coated internal and externally with aluminum using gaseous deposition. Core holes were them drilled at different locations within the heat exchanger so as to determine the thickness of the aluminum coating both inside within the tubes and on the fins at different locations and on the exterior of the unit All the samples had an aluminum coating thickness within our preferred range Honeycomb shapes and relatively simple heat exchangers have also been coated with the solgel coating As indicated initial work using conventional solgel coating solutions in difficulty in coating all of the heat exchanger and even more in draining excess solution off with the result that the tubes and passage ways were blocked with the coating It was necessary to develop solutions that have a controlled low viscosity, preferably less than 100 centipose, and whose viscosity does not change with time or with changes in the rooms humidity Using low viscosity solutions heat exchangers have been successfully coated giving uniform zirconia and alumina coatings of less than 5 microns. It is understood that the heating and cooling rates and hold times given will need to be modified for specific furnaces and also to be extended for large complex parts such as an heat exchanger in order to ensure adequate heating of the complete structure. Often protective coatings have a short life because they can not withstand the stresses set up by thermally cycling the part. The conversion coatings of the present invention can be applied through heat treatment to become integrated with the base metal and as is illustrated , Fig. 7 cycling to 1300°F every 15 minutes for 1,000 hours results in no flaking of the transformed metal or zirconium solgel coating. In fact, examination showed no change in the surface. According the titanium aluminide and solgel coatings are understood to provide mechanical properties sufficient to provide an oxidation resistant and reliable heat exchanger. Although, the invention has been described with particular reference to the attached drawings in connection with a plate fin heat exchanger, it should be noted that other forms of heat exchanger can benefit equally from the use of titanium members without departing from the spirit and scope of the disclosed invention. Further, the invention is applicable to components other than heat exchangers and can be used on essentially any titanium component to allow the extended use of such components at temperatures above 950°F which is the general maximum temperature for titanium.

Claims: What is claimed is A light weight titanium based metal heat exchanger for operation in excess 950°F comprising first, second and third plates, a first spacer inserted between the first and second plates for separating the first and second plates to form a first passage for receiving a first fluid there through, a second spacer inserted between the second and third plates to form a second passage for receiving a second fluid there through, wherein heat is transferred from the first fluid by conduction through the second plate to the second fluid, wherein at least one plate of said group of first, second and third plates is comprised of a titanium based metal and is coated with an oxidation resistant protective layer 2 The light weight titanium based metal heat exchanger of claim 1 wherein the oxidation resistant protective layer is a titanium aluminide layer and can operate at temperatures up to 1400 3 The light weight titanium based metal heat exchanger of claim 1 wherein the titanium aluminide layer is formed by heat treating a deposited aluminum coating 4 The light weight titanium based metal heat exchanger of claim 1 wherein at least one plate includes a titanium aluminide surface with an aluminum oxide coating 5 The light weight titanium based metal heat exchanger of claim 4 wherein at least one plate further includes a based solgel coating applied as a wash coat over the titanium aluminide surfac, such coating based coating being selected from the class comprising silica, zircoma or alumina based solgel coatings 6 The light weight titanium based metal heat exchanger of claim 1 further including titanium based manifolds for directing said first and second fluids into and out from and the first and second fluid passages respectively 7 The light weight titanium based metal heat exchanger of claim 1 wherein oxidation resistant protective layer is a solgel based wash coat 8 The light weight titanium based metal heat exchanger of claim 7 wherein solgel based coating is selected from the group comprising zirco a alumina and silica based solgel coatings 9 A light weight titanium based metal heat exchanger for operation in excess 950°F comprising first, second and third titanium based plates, a first titanium based spacer inserted and brazed between the first and second plates for separating the first and second plates to form a first passage for receiving a first fluid there through, a second titanium spacer inserted and brazed between the second and third plates to form a second passage for receiving a second fluid there through wherein said first second and third plates form a brazed heat exchanger core for transferring heat, from a first fluid flowing in the first passage, by conduction through the second plate to a second fluid flowing in the second passage and brazed heat exchanger core coated with an oxidation resistant protective layer applied to the exposed surfaces of the said titanium based plates and spacer 10 The light weight titanium based metal heat exchanger of claim 9 wherein oxidation resistant protective layer comprises an aluminum coating 1 1 The light weight titanium based metal heat exchanger of claim 9 wherein the aluminum coating is heat treated to form a titanium aluminide surfaces 12 The light weight titanium based metal heat exchanger of claim 1 1 wherein a solgel based coating is applied as a wash coat over the titanium aluminide surfaces 13 The light weight titanium based metal heat exchanger of claim 10 wherein the solgel coating is selected from the class of containing silica, alumina an d zirconia containing solgel coatings 14 The light weight titanium based metal heat exchanger of claim 9 wherein oxidation resistant protective layer is a solgel based wash coat 15 A method for manufacturing a light weight titanium based metal heat exchanger for operation in excess 850°F comprising the steps of providing first, second and third plates, at least one of which is titanium based, inserting a first spacer between the first and second plates for separating the first and second plates to form a first passage for receiving a first fluid there through, inserting a second spacer between the second and third plates to form a second passage for receiving a second fluid there through, thereby forming a heat exchanger core wherein heat is transferred from the first fluid by conduction through the second plate to the second fluid, depositing an oxidation resistant protective layer applied to the exposed surfaces of the said titanium based plates and spacers 16 A method for manufacturing a light weight titanium based metal heat exchanger of claim 15 wherein the oxidation resistant protective layer comprises an aluminum coating on said heat exchanger core 17 A method for manufacturing a light weight titanium based metal heat exchanger of claim 16 wherein the aluminum coated titanium plate is heat treated to form a titanium aluminide surface having an aluminum oxide coating, 18 The method for manufacturing a light weight titanium based metal heat of claim 16 wherein the aluminum layer is gaseously deposited by low temperature chemical vapor deposition 19 The method for manufacturing a light weight titanium based metal heat exchanger foi operation in excess 950°F of claim 17 wherein the heat treating occurs at a temperature in excess of approximately 1200°F 20 The method for manufacturing a light weight titanium based metal heat exchanger for operation in excess 950°F of claim 17 wherein the heat treat transformation of said aluminum coated titanium based plate to a titanium aluminide surface occurs at controlled temperatures and the rate of heating and cooling are controlled to avoid cracking the aluminide layer 21 The method for manufacturing a light weight titanium based metal heat exchanger for operation in excess 950°F of claim 15 further including the step of applying a solgel coating as a wash coat over the titanium aluminum layer to ensure that a complex heat exchanger shape is substantially completely protected against oxidation 22 The method for manufacturing a light weight titanium based metal heat exchanger for operation in excess 950°F of claim 21 wherein the solgel based coating is selected from the group comprising zirconia, alumina and silica based solgel coatings 23. The method for manufacturing a light weight titanium based metal heat exchanger for operation in excess 950°F of claim 17 wherein the solgel coating can be applied at a temperature of approximately 1 100°F to avoid oxidation of uncoated titanium. 24. The method for manufacturing a light weight titanium based metal heat exchanger for operation in excess 950°F of claim 17 wherein the solgel coating is rapidly heated in a time period of less than one hour and cooled during application. 25. The method for manufacturing a light weight titanium based metal heat exchanger for operation in excess 950°F of claim 17 wherein the based solgel coating can be applied at a temperature of approximately 1 100°F to avoid oxidation of uncoated titanium. 26. The method for manufacturing a light weight titanium based metal heat exchanger for operation in excess 950°F of claim 15 wherein the aluminum and zirconium solgel coated heat exchanger are fabricated from metal selected from the group comprising Ti 21 S, Ti 32.5, Ti 1 100, Ti 153, Ti 6242, and IMI 834. 27. The method for manufacturing a light weight titanium based metal heat exchanger for operation in excess 950°F of claim 15 wherein the heat exchanger is braze clad prior to assembly. 28. A method for manufacturing a light weight titanium based metal heat exchanger of claim 1 5 wherein the oxidation resistant protective layer comprises a solgel based coating applied to the heat exchanger core via a wash coat dipping using a low viscosity solution, at least less than 100 centipose. 29. A method for manufacturing a light weight titanium based metal heat exchanger of claim 15 wherein the solgel coating is selected from the group comprising zirconia, alumina and silica based solgel coatings.

Inventors: FANELLI ANTHONY J, POHLMAN MATT, RAYBOULD DEREK, FANELLI, ANTHONY, J., POHLMAN, MATT, RAYBOULD, DEREK
Applicants: ALLIED SIGNAL INC, ALLIEDSIGNAL INC.
Application year: 1998
Main classification: F28F21
IPC codes: C23C26, F28D9, F28F19, F28F21