PAPER PRODUCTION PROCESS

Abstract: A paper production process, characterized by the process step of providing to the paper at some point in the production process a compound of formula (I), in which the symbols have the meaning given in claim 1, reduces the tendency of the obtained paper products, particularly those made from high-yield pulps, to yellow on exposure to light. Also claimed are the paper additives used in that process and the paper produced by such a process.

Description: PAPER PRODUCTION PROCESS This invention relates to the reduction of brightness reversion in paper products, particularly those made from high-yield pulps and to compositions for achieving same. A "high-yield" pulp is a pulp in which the papermaking fibres are separated by means which are mainly mechanical action (optionally with some chemical treatment). As the name indicates, there is relatively little waste with such a pulp, in contrast to the so-called "chemical" pulps where the fibre separation is achieved by purely chemical means. Paper made from high-yield pulp (for example, groundwood pulp, refiner pulp, thermomechanical pulp (TMP), and chemithermomechanical pulp (CTMP)) is considerably cheaper than that made from chemical pulp, even when the high-yield pulp is bleached. The problem which has restricted the use of high-yield pulps to non-archival uses such as newsprint and corrugated paper is the tendency of such paper to undergo brightness reversion (yellowing) with time, this being believed to be caused by the instability to ultraviolet light of the lignin component of high-yield pulps. It has now been found that the use of certain compounds allows the light-induced yellowing of paper to be considerably reduced, often to levels where papers not previously thought suitable for archival material may be used for such applications. The invention therefore provides a paper production process, comprising the process steps of (a) providing a paper pulp, and (b) forming a paper sheet therefrom, the process further including the process step of providing to the paper at some point in the said production process a thioether compound of formula I in which m is an integer of from 2-4; n is an integer of at least 2; p is an integer of from 1 -4; X is a bridging member and A is alkylene or arylene, optionally substituted; R, is (a) alkyl (C,-C 6 ), optionally substituted but not contaimng fluorine or silicon, (b) phenyl or benzyl, both optionally substituted or (c) a heteroaromatic residue, and if p is equal to 1 and R 2 is hydrogen or alkyl (C r C 6 ), then R, can also be another residue R 3 O[(CH 2 ) m O] n X-A-S-Z- where R 3 is hydrogen or alkyl (C,-C 6 ), and Z is selected from (CH 2 ) 2 , (CH 2 ) 3 , (CH 2 ) 4 , CH 2 CH(CH 2 OH), CH 2 CH(OH)CH(OH)CH 2 , CH 2 CH 2 OCH 2 CH 2 , 1,2-phenylene, 1,3-phenylene, 1 ,4-phenylene, 2,5-(l,3,4-thiadiazolyl), 1,3-xylylene, 1,3,5-triazinyl (optionally substituted), and R 2 is hydrogen or alkyl (C,-C 6 ), optionally substituted, or another residue R,-S-A-X-. Examples of X are -C(=O)-, -CH 2 C(=O)O-, -C(=O)NΗ-, -S(=O) 2 - or a direct bond. Examples of suitable groups R, include methyl, ethyl, CH 3 OC(=O)CH 2 -, CH 3 CH 2 OC(=O)CH 2 -, HOCH 2 CH 2 -, CH 3 CH(OH)CH 2 - and HOCH 2 CH(OH)CH 2 -. Examples of suitable groups R 2 include H-, methyl, ethyl and HOCH 2 CH 2 SCH 2 CH 2 C(=O)-. The heteroaromatic residue is selected from 2-thienyl, furfuryl, 2-pyridinyl (optionally substituted), 4- pyridinyl (optionally substituted), 2-(5-methyl-l,3,4-thiadiazolyl), 2-pyrimidyl, 2-(4-hydroxypyrimidyl), 2-(4-hydroxy-6-methylpyrimidyl), 2-(4-hydroxy-6- propylpyrimidyl), 2-(4,6-dihydroxypyrimidyl), 2-benzoxazolyl and 2-benzothiazolyl (optionally substituted). Preferably and independently of each other m is 2; n is at least 4, more preferably 4-50; P is 1; X is -C(=O)- or -CH 2 C(=O)O-; A is methylene or ethylene; R t is methyl, ethyl, HOCH 2 CH 2 -, phenyl, benzyl or 1,3,5-triazinyl; R 2 is hydrogen, methyl or HOCH 2 CH 2 SCH 2 CH 2 C(=O)-. Compounds of formula I can be produced for example by addition of a compound of the formula II HS-R, (II) to mono- or diacrylate esters of polyalkylene glycols of the formula III R 2 -[-O-[-(CH 2 ) m -O-] n -C(=O)-CH=CH 2 ] p (III) or by reaction of polyalkylene glycols with compounds of the formula IV and optionally further reaction with bridging reactants. The invention further provides a method for reducing the tendency of a paper to yellow on exposure to light, comprising the incorporation thereinto, at some stage in the manufacture thereof, of a compound according to formula I. The invention further provides a paper additive which comprises a compound of formula I. The invention further provides paper produced by a process incorporating a compound of formula I. In this description of the invention, unless otherwise stated, the description of a component in the singular also includes the possibility that more than one such component may be used. The paper may also contain other additives known in the art to control brightness reversion. Examples of such additives include ultraviolet absorbers, for example, 2,4-dihydroxybenzo- phenone, benzotriazole UV absorbers such as "Fadex" (trade mark) F liquid and "Tinuvin" (trade mark) 1130, ascorbic acid, sodium ascorbate, ethylene glycol bisthioglycolate, S-methyl-1-thioglycerol, sodium hypophosphite, poly(ethylene glycol), and poly(tetrahydrofuran). Such additives may be added either together with, or separately from, the thioether compound as hereinabove described. More preferably, the thioether is added together with an ultraviolet absorber. The paper may further contain other additives commonly employed in the papermaking industry. Examples of such additives include sizing agents (for example, rosin, starch, alkyl ketene dimer, alkenyl succinic anhydride), wet strength resins (for example, poly- aminoamide-epichlorohydrin resins), retention- and drainage aids (for example, poly- aluminium chloride, polydiallyldimethylammonium chloride), and optical brightening agents. Such additives may be added either together with, or separately from, the thioether. The invention is performed by adding the thioether to the pulp or paper sheet at some point in the paper production process, and preferably at the size-press. There are a number of possibilities, namely, (a) addition to the pulp, prior to sheet formation; (b) application to a sheet formed on the wire of a paper machine, for example by spraying or coating; (c) addition at a size-press; (d) application to the sized sheet at a stage later than the size-press. The preferred possibility is (c). In all cases, the total quantity of compound lies between 0.02% and 20% (preferably between 0.1% and 10%) by weight on dry fibre. The invention may be used with paper made from any kind of pulp, but gives especially good results with papers which are formed from high-yield pulps, whereby, with the use of the invention, the tendency to yellow is reduced to a surprising and considerable degree. This permits the use in paper of much higher quantities of high-yield pulp than was previously the case, with consequent potential for considerable cost savings. Depending on the choice of thioether, other advantages can include all of low cost, thermal stability, water-solubility, low toxicity, low odour and a bleaching effect. EXAMPLES OF THE INVENTION PREPARATIVE EXAMPLE 1 Poly(ethylene glycol) acrylate of average M n ca. 336 (33.6g) is cooled to below 10°C using an ice/water cooling bath. 2-Mercaptoethanol (7.0g) is added dropwise at such a rate that the temperature does not exceed 25°C. The cooling bath is removed, and the reaction mixture is stirred at ambient temperature for 3 hours, and then at 50°C for a further 1 hour. 30% Hydrogen peroxide (0.2g) is added, and heating is continued for a further 1 hour. The compound so-formed is a clear, colourless, odourless liquid. According to the method described in preparative example 1, further compounds can be synthesized from reactants as indicated in Table 1 TABLE 1 PREPARATIVE EXAMPLE 7 Poly(ethylene glycol) acrylate of average M n ca. 336 (33.6g) is cooled to below 10°C using an ice/water cooling bath. 2-Thiouracil (10.3g) is added in portions, followed by 30% sodium hydroxide (10.7g) at a rate such that the temperature does not exceed 25°C. The cooling bath is removed, and the reaction mixture is stirred at ambient temperature overnight. A solution of 30ml 3M hydrochloric acid is added, and the product is extracted into dichloromethane, dried over sodium sulphate and evaporated to give the above compound as a clear, colourless, odourless liquid. PREPARATIVE EXAMPLE 8 Ethyl (methylthio)acetate (26.8g) is added with stirring at 60°C to poly(ethylene glycol) of average M„ ca. 600 (75.0g). Dibutyl tin oxide (0.4g) is added. The mixture is slowly heated to 110-115°C, removing the ethanol formed in the reaction by distillation. After 1 hour at 110- 115°C, the reaction vessel is evacuated to 50mbar. Heating is continued until reaction is complete (10 hours). The vacuum is removed, to leave the above compound as a clear, faintly- coloured, viscous liquid. PREPARATIVE EXAMPLE 9 (Methylthio)acetic acid (50.4g) is added with stirring at 60°C to poly(ethylene glycol) of average M„ ca. 1500 (375g). p-Toluenesulphonic acid (2.5g) is added. The reaction vessel is evacuated to 50 mbar to remove the water formed in the reaction, and the temperature is raised to 95-98°C. After 2 hours at 95-98°C, the temperature is further raised to 130°C until reaction is complete. The vacuum is removed, to leave the above compound as a clear, faintly- coloured, viscous liquid which solidifies on cooling. PREPARATIVE EXAMPLE 10 Ethyl 2-hydroxyethyl sulphide (lό.lg) is added to a stirred solution of poly(ethylene glycol) bis(carboxymethyl) ether of average M n ca. 660 (53.0g) in toluene (160 ml). p-Toluenesulphonic acid (0.4g) is added, and the temperature is raised to reflux. The water formed in the reaction is removed using a Dean and Stark apparatus. When reaction is complete, the solvent is removed under reduced pressure to leave the above compound as a clear, faintly-coloured, viscous oil. PREPARATIVE EXAMPLE 11 Cyanuric chloride (3.7g) is added to a stirred mixture of α-mercaptoacetyl-ω-methoxy- poly(ethylene glycol) of average M n ca. 840 (50.4g), sodium bicarbonate (5.0g) and ethanol (40ml). The mixture is stirred at ambient temperature overnight, filtered and evaporated to leave the above compound as a clear, faintly-coloured, viscous liquid. PREPARATIVE EXAMPLE 12 (Methylthio)acetic acid (9.6g) is added to a stirred solution of TERATHANE® 650 polyether glycol (32.5g) in toluene (150ml). 95-98% Sulphuric acid (1 drop) is added, and the temperature is raised to reflux. The water formed in the reaction is removed using a Dean and Stark apparatus. When reaction is complete, the solution is dried over potassium carbonate, and the solvent removed under reduced pressure to leave the above compound as a waxy, white solid. The invention is illustrated with reference to the following application examples, in which all parts are by weight. The results clearly demonstrate the stabilisation of chemothermo- mechanical pulp (CTMP) against photo-yellowing provided both by the thioether alone, and by the combination of the thioether with an ultraviolet absorber (Fadex F liquid). The following coating formulations are prepared as in Table 2. TABLE 2 APPLICATION EXAMPLE 1 Each formulation is applied at the size-press to a handsheet made from bleached chemithermomechamcal pulp (CTMP). The treated handsheets are then air-dried for a minimum of 24 hours in a constant temperature and humidity environment and protected from light. Accelerated ageing experiments are conducted by irradiating handsheet samples in a modified fan-cooled "Rayonet" RPR- 100 photochemical reactor using 16 RPR-3500A lamps (Southern New England Ultraviolet Company). The yellowing process is monitored by taking CIE whiteness measurements at regular intervals using an Elrepho spectrophotometer. The results are given in Table 3; the percentage take-up on dry fibre from each formulation is shown in parentheses. TABLE 3 APPLICATION EXAMPLE 2 Five coating formulations (16, 17 and 32 to 34) are prepared as in Table 2. Each formulation is applied at the size-press to a handsheet made from bleached chemithermomechamcal pulp (CTMP). The treated handsheets are then air-dried for a minimum of 24 hours in a constant temperature and humidity environment and protected from light. The handsheet samples are then subjected to normal office light. The yellowing process is monitored by taking CIE whiteness measurements at regular intervals using an Elrepho spectrophotometer. The results are summarised in Table 4; the percentage take-up on dry fibre is shown in parentheses. TABLE 4 COMPARATIVE EXAMPLE Three coating formulations (18, 19 and 20) are prepared as in Table 2. Compound V is PGTL 2 800 as described in WO 95/35331. Each formulation is applied at the size-press to a handsheet made from bleached chemithermomechamcal pulp (CTMP). The remainder of the experiment is conducted exactly as described in Application Example 1. The results are summarised in Table 5; the percentage take-up on dry fibre from each formulation is shown in parentheses. TABLE 5 APPLICATION EXAMPLE 3 Four coating formulations are prepared as in Table 2. Each formulation is applied at the size- press to a handsheet made from bleached thermomechanical pulp (TMP). The remainder of the experiment is conducted exactly as described in Application Example 1. The results are summarised in Table 6; the percentage take-up on dry fibre from each formulation is shown in parentheses. TABLE 6 APPLICATION EXAMPLE 4 Compound of Example 12 (10% and 20% by weight dry fibre) is stirred for 15 minutes with a 2% aqueous suspension of bleached chemithermomechanical pulp (CTMP). The suspension is then diluted to a concentration of 1%, and formed into handsheets. A blank handsheet is also prepared, from CTMP completely free of test compound. The handsheets are air-dried for a minimum of 24 hours in a constant temperature and humidity environment and protected from light. The remainder of the experiment is conducted exactly as described in Application Example 1. The results are summarised in Table 7. TABLE 7

Claims: CLAIMS A paper production process, comprising the process steps of (a) providing a paper pulp, and (b) forming a paper sheet therefrom, the process further including the process step of providing to the paper at some point in the said production process a compound of formula I: in which m is an integer of from 2-4; n is an integer of at least 2; p is an integer of from 1-4; X is a bridging member and A is alkylene or arylene, optionally substituted; R, is (a) alkyl (C,-C 6 ), optionally substituted but not containing fluorine or silicon, (b) phenyl or benzyl, both optionally substituted or (c) a heteroaromatic residue, and if p is equal to 1 and R 2 is hydrogen or alkyl (C,-C 6 ), then R, can also be another residue R 3 O[(CH 2 ) m O] n X-A-S-Z- where R 3 is hydrogen or alkyl (C,-C 6 ), and Z is selected from (CH 2 ) 2 , (CH 2 ) 3 , (CH 2 ) 4 , CH 2 CH(CH 2 OH), CH 2 CH(OH)CH(OH)CH 2 , CH 2 CH 2 OCH 2 CH 2 , 1,2-phenylene, 1,3-phenylene, 1,4- phenylene, 2,5-(l,3,4-thiadiazolyl), 1,3-xylylene, 1,3,5-triazinyl (optionally substituted), and R 2 is hydrogen or alkyl (C,-C 6 ), optionally substituted, or another residue R r S-A-X-. A process according to claim 1, in which a compound of formula I is used in which X is -C(=O)-, -CH 2 C(=O)O-, -C(=O)NH-, -S(=O) 2 - or a direct bond. 3. A process according to claim 1, in which a compound of formula I is used in which R, is methyl, ethyl, CH 3 OC(=O)CH 2 -, CH 3 CH 2 OC(=O)CH 2 -, HOCH 2 CH 2 -, CH 3 CH(OH)CH 2 - or HOCH 2 CH(OH)CH 2 -. 4. A process according to claim 1, in which a compound of formula I is used in which R 2 is hydrogen, methyl, ethyl or HOCH 2 CH 2 SCH 2 CH 2 C(=O)-. A process according to claim 1 , in which a compound of formula I is used in which the heteroaromatic residue is selected from 2-thienyl, furfuryl, 2-pyridinyl (optionally substituted), 4- pyridinyl (optionally substituted), 2-(5-methyl-l,3,4-thiadiazolyl), 2-pyrimidyl, 2-(4-hydroxypyrimidyl), 2-(4-hydroxy-6-methylpyrimidyl), 2-(4-hydroxy- 6-propylpyrimidyl), 2-(4,6-dihydroxypyrimidyl), 2-benzoxazolyl and 2-benzothiazolyl (optionally substituted). A process according to any of the preceding claims, in which a compound of formula I is used in which, independently of each other m is 2; is at least 4, more preferably 4-50; is 1; is -C(=O)- or -CH 2 C(=O)O-; is methylene or ethylene; is methyl, ethyl, HOCH 2 CH 2 -, phenyl, benzyl or 1,3,5-triazinyl; is hydrogen, methyl or HOCH 2 CH 2 SCH 2 CH 2 C(=O)-. 7. A method for reducing the tendency of a paper to yellow on exposure to light, comprising the incorporation thereinto of a compound of the formula I according to claim 1. 8. A paper additive which comprises a compound of the formula I according to claim 1. 9. Paper produced by a process according to claim 1. 10. Compounds as hereinabove described with reference to any of the Examples.

Inventors: JACKSON ANDREW CLIVE, JACKSON, ANDREW, CLIVE
Applicants: CLARIANT FINANCE BVI LTD, CLARIANT INT LTD, JACKSON ANDREW CLIVE, CLARIANT FINANCE (BVI) LIMITED, CLARIANT INTERNATIONAL LTD., JACKSON, ANDREW, CLIVE
Application year: 1998
Main classification: D21H17
IPC codes: C07C323, C07D239, C07D251, D21H17, D21H21