PROCESS FOR PRODUCING A VANADIUM PHOSPHORUS OXIDE CATALYST

Abstract: A method of making a vanadium phosphorus oxide (VPO) catalyst by precipitating from a 45-65 g/l solution of V<4+> ions and V<5+> ions a vanadium- and phosphorus-containing precipitate comprising a complex of formula VOHPO4 . 1/2H2O. The precipitate is calcined under an inert atmosphere to produce a VPO catalyst whose active phase is of formula (VO)2P2O9. Said solution comprises cations of at least two of Bi, Zr, Cr, Ce, Co, Mn, Mg and Mo such that the precipitate comprises 1-25 % by mass of said dopant metal cations in total, the balance being said complex. Each dopant metal forms 0.1-20 % by mass of the precipitate.

Description: PROCESS FOR PRODUCING A VANADIUM PHOSPHORUS OXIDE CATALYST THIS INVENTION relates to vanadium phosphorus oxide (VPO) catalysts. More particularly, the invention relates to a method of making a VPO catalyst suitable for the oxidation of C^ and C 5 paraffins and olefins to maleic anhydride, phthalic anhydride and acetic acid, especially paraffins and olefins produced by Fischer-Tropsch processes, and to a VPO catalyst made in accordance with the method. According to the invention there is provided a method of making a vanadium phosphorus oxide (VPO) catalyst, the method comprising the steps of: precipitating, from a solution comprising dissolved V 4 + ions and V 5 + ions at a total concentration of 45 -65 g/l, a vanadium-containing and phosphorus- containing precipitate comprising a complex in accordance with the formula VOHP0 4 ♦ %H 2 O; and calcining the precipitate under an inert atmosphere, to produce a VPO catalyst having an active phase in accordance with the formula (VO) 2 P2θ9' the solution from which the precipitate is precipitated comprising dissolved cations of at least two dopant metals selected from the group consisting of Bi, Zr, Cr, Ce, Co, Mn, Mg and Mo, said dissolved dopant metal cations being present in the solution in proportions such that the precipitate comprises 1 - 25% by mass of dopant metal cations in total, the balance being the VOHPO • Vzr\ 2 0 complex, each dopant metal forming 0.1 - 20% by mass of the precipitate. Preferably, the proportion of dissolved V 4 + ions relative to the proportion of dissolved V ions is as high as practically feasible. Furthermore, the ratio of dissolved V + ions:V 5 + ions in the solution may be such that the molar proportion of each of the V 4 + ions and the V 5 + ions in the VPO catalyst, after calcining, is 0.1 - 10 mole %, typically 0.5 - 5%. Preferably the total concentration of dissolved V 4 + ions and V + ions in the solution is 50 - 60 g/f , the dissolved dopant metal cations being present in the solution in proportions such that the precipitate comprises 2 - 20% by mass of the dopant metals in total, each dopant metal forming 0,5 - 15% by mass of the precipitate, the ratio of dissolved V + ions.V + ions in the solution being such tthhaatt tthhee mmoollaarr pprrooppoorrttiioonn of V 5 + ions in the VPO catalyst is OJ - 10 mole % typically 0.5 - 5 mole % . The solution from which the precipitate is precipitated may comprise dissolved cations of 2 - 3 dopant metals selected from said group consisting of Bi, Zr, Cr, Ce, Co, Mr, Mg and Mo. One of the dopant metals may be Bi, Bi cations being present in the solution from which the precipitate is precipitated in a proportion such that Bi forms 1 - 1 5% by mass of the precipitate, the solution comprising, in addition to the Bi cations, cations of 1 - 2 other dopant metals selected from: Zr; Mn and Ce; Co; Ce; Zr and Ce; and Zr and Co. Instead, one of the dopant metals may be Zr, Zr cations being present in the solution from which the precipitate is precipitated in a proportion such that Zr forms 1 - 1 5 % by mass of the precipitate, the solution comprising, in addition to the Zr cations, cations of 1 - 2 other dopant metals, selected from: Bi; Cr; Ce and Cr; Ce; Co; Bi and Ce; and Bi and Co. Instead, one of the dopant metals may be Cr, Cr cations being present in the solution from which the precipitate is precipitated in a proportion such that Cr forms 1 - 1 5 % by mass of the precipitate, the solution comprising, in addition to the Cr cations, cations of 1 - 2 other dopant metals, selected from: Zr; and Ce and Zr. Instead, one of the dopant metals may be Ce, Ce cations being present in the solution from which the precipitate is precipitated in a proportion such that Ce forms 1 - 1 5% by mass of the precipitate, the solution comprising, in addition to the Ce cations, cations of 1 - 2 other dopant metals, selected from: Zr and Cr; Zr; Bi and Mn; Bi; BI and Zr; and Mn and Mg. Instead, one of the dopant metals may be Co, Co cations being present in the solution from which the precipitate is precipitated in a proportion such that Co forms 1 - 1 5% by mass of the precipitate, the solution comprising, in addition to the Co cations, cations of 1 - 2 other dopant metals, selected from: Zr; Bi; and Bi and Zr. Instead, one of the dopant metals may be Mn, Mn cations being present in the solution from which the precipitate is precipitated in a proportion such that Mn forms 1 - 1 5 % by mass of the precipitate, the solution comprising, in addition to the Mn cations, cations of 1 - 2 other dopant metals, selected from- Bi and Ce; Mg and Ce, and Mo. Instead, one of the dopant metals may be Mg, Mg cations being present in the solution from which the precipitate is precipitated in a proportion such that Mg forms 1 - 20% by mass of the precipitate, the solution comprising cations of Mn and Ce dopant metals in addition to the Mg cations. Instead, one of the dopant metals may be Mo, Mo cations being present in the solution from which the precipitate is precipitated in a proportion such that Mo forms 1 - 20% by mass of the precipitate, the solution comprising cations of Mn dopant metal in addition to the Mo cations. The solution may comprise a solvent selected from alcohols and mixtures of two or more alcohols. When the solvent is a mixture of two alcohols, the alcohols may be present in a mass ratio of 1 -2 - 2: 1 . In particular, the solvent may be anhydrous, the alcohol being selected from: isobutanol; benzyl alcohol; ethanol; octanol; 2-butanol; isopropanol; and mixtures of any two or more thereof. More particularly, the solvent may be a mixture of two said alcohols. The method may include the preliminary step of obtaining the solution of the V ions and V^ + ions in the solution by dissolving V 5 + ions in the solvent and reducing a portion of the V 5 + ions to V + ions. Reducing the V 5 + cations to the \l cations may be by using a suitable reducing agent. Dissolving the ^ + ions in the solvent may be by admixing vanadium pentoxide (VoOe) with the solvent. When the solvent is an alcohol and is anhydrous, the reducing agent may be selected from benzyl alcohol, isobutanol or isopropanol, eg so that the solvent and reducing agent are the same alcohol The reducing may be by refluxing the solution (conveniently at atmospheric pressure) , optionally followed by stirring, at a suitable temperature, followed by the precipitation. In particular, the reducing of the V 5 + ions to V + ions may be by means of a reducing agent, the method including refluxing the solvent containing the V ions dissolved therein with the reducing agent, the solvent and reducing agent optionally being the same alcohol. The precipitation may be effected by adding phosphate ions to the solution, eg by adding phosphoric acid to the solution. For the purpose of the reducing, routine experimentation can be employed to determine a suitable reducing agent and to determine a suitable proportion thereof to be used, to determine suitable periods respectively for refluxing and stirring, to determine a suitable stirring temperature, and to determine a suitable refluxing pressure and temperature if refluxing is at a pressure other than atmospheric pressure. After the refluxing has been carried out for a desired period, eg 3 - 20 hours, preferably 6 - 1 5 hours, and the stirring has been carried out for a desired period, eg 1 2 - 36 hours, preferably 1 8 - 30 hours, to take the reduction to a desired degree of completion, the solution may be cooled to room or ambient temperature, the precipitated complex then being collected and washed and dried, prior to calcining thereof. Preferably, the calcining is carried out under an inert atmosphere for example under argon, eg in an oven flushed by argon, according to a suitable heating regime. Thus, heating rates, cooling rates, maximum temperature and the temperatures and durations of any temperature holds or plateaus may be determined by routine experimentation, a maximum temperature of 400 - 500° C preferably 420-480°C, eg 450° C being suitable. Thus the calcining may include heating the precipitate under an inert atmosphere to a maximum temperature of 4QQ^ 500° C. The dopant metal cations may be dissolved in the solvent by dissolving a suitable dopant compound (also known as a promoter compound, the dopant cations also being known as promoter cations) in the solvent. Suitable dopant compounds are as follows: For Bi cations, (BιO) 2 • C0 3 , can be used; SUBSTITUTE SHEET (PW E For Zr cations, ZrOCI 2 • 8H2O, ZrOCI 2 , can be used; For Cr cations, Crθ3, can be used; For Ce cations, Ce(Nθ3)3 * 6H 2 0, can ^ e usec *; For Co cations, Co 3 (P0 4 ) 2 • 8H 2 0, can be used; For Mn cations, MnCI 2 • 4H 2 0, can be used; For Mg cations, MgO, can be used; and For Mo cations, M0O3 can be used. The invention extends to a VPO catalyst, whenever made in accordance with the method described above. The invention will now be described, by way of non-limiting illustrative example, with reference to the following Examples. In the Examples, unless otherwise specified, refluxing, stirring and calcining were carried out at atmospheric pressure ; and room (ambient) temperature was 20 - 25 °C. EXAMPLE 1 VOHPO4J/2 H2O (97.5% by mass) + 1 % Bi promoter + 1 .5% Zr promoters: A solvent comprising 90ml benzyl alcohol and 60ml isobutanol was used to dissolve 1 5g of V 2 0 5 , 0J 4g of ZrOCI 2 .8H 2 0 and 0.21 1 g of (BiO) 2 .Cθ . The solution so formed was refluxed for 7 hours at atmospheric pressure after which it was stirred for 1 6 hours at room ^ temperature. 26g of 98% by mass H3PO4 was added to the solution and the mixture was stirred under reflux for 3 hours. The solution was cooled to room temperature and a precipitate which had formed in response to the H3PO4 addition was recovered by filtration. The precipitate was washed thoroughly with water (about 5 ( ) . A blue solid was obtained which as oven-dried for 1 2 hours at 1 50 ° C to form a catalyst precursor. The catalyst precursor was calcined in an inert atmosphere in a reaction vessel in the form of an oven. Argon was used as the inert atmosphere, a flow rate of argon of approximately 6 f/min being used to flush the vessel. The temperature was steadily increased from room temperature to 300 " C over a 3-hour period, ie at a rate of roughly 100°C/hour. The temperature was maintained at 300 * C for 2 hours. The temperature was then steadily increased to 450' C over a further 3 hours at a rate of about 50°C/hour. The temperature was maintained at 450 °C for 6 hours. The temperature was then steadily reduced to room temperature over a period of 3 hours at a rate of about 150°C/hour, to form a novel VPO catalyst. A micro-reactor was loaded with the novel VPO catalyst so formed. Butane, at a concentration of 1.3% by volume in air, was fed over the catalyst in the micro-reactor at a gas hourly space velocity of 1500 - 3000 preferably 2000 - 2700 h "1 . The temperature for maximum maleic anhydride yield was found to be between 300 and 450°C, preferably between 390°C and 410°C. It was surprising to note that, when the catalyst was used to catalyze butane conversion to maleic anhydride, after one day the butane conversion was 67% and the selectivity to produce maleic anhydride was 36%. It was found that the VPO catalyst out-performed a control (standard) VPO catalyst by a considerable margin as set forth in Table 1 hereunder. TABLE 1 : Comparison of Standard and Novel VPO Catalysts at Equilibration TABLE 2: Comparison of Novel VPO Catalysts at Equilibation These novel catalysts were tested regarding their ability to catalyze the conversion of butene to maleic anhydride, pentane to maleic anhydride and phthalic anhydride, and pentene to maleic anhydride and phthalic anhydride as set forth in Table 2 hereunder. TABLE 2 EXAMPLE 2 VOHPO 4 .yaH 2 O (97% by mass) + 1.5% Zr promoter + 1.5% Cr promoter: A solvent comprising 90m£ benzyl alcohol and 60ml isobutanol was used to dissolve 15g of V 2 O 5 , 0.124g of CrO 3 and 0.4g of ZrOCI 2 .8H 2 O, The solution so formed was refluxed for 7 hours and was then stirred for 16 hours at room temperature. 24g of 98% H3PO4 was added to the solution, followed by stirring under reflux for 3 hours. The solution was then cooled to room temperature and a precipitate which had formed was recovered by filtration. The precipitate was washed thoroughly with water (about 5f). A blue solid was obtained which was oven-dried for 12 hours at 150° C to form a catalyst precursor. EXAMPLE 3 VOHPO 4 JΛH 2 O (88.5% by mass) + 8.5% Ce promoter + 1.5 % Zr promoter + 1.5 % Cr promoter: A solvent comprising 90ml benzyl alcohol and 60m£ isobutanol was used to dissolve 15g of V 2 O 5 , 0.4g of ZrOCI 2 , 0.124g of CrO 3 and 3,04g of Ce(NO3)3.6H 2 O. The solution so formed was refluxed for 7 hours and was then stirred for 16 hours at room temperature. 24g of 98% HgPO 4 was added to the solution followed by stirring under reflux for 3 hours. The solution was cooled to room temperature and a precipitate which had formed was recovered by filtration. The precipitate was washed thoroughly with water (about 5£). A blue solid was obtained which was oven-dried for 12 hours at 150°C to form a catalyst precursor. EXAMPLE 4 VOHPO 4 JΛH 2 O 90% by mass) + 1.5% Zr promoter + 8.5% Ce promoter: A solvent comprising 90ml benzyl alcohol and 60ml isobutanol was used to dissolve 15g of V 2 O 5 , 0.4g of ZrOCI 2 .8H 2 O and 3.04g of Ce(NO 3 ) 3 .6H 2 O. The solution so formed was refluxed for 7 hours and then stirred for 16 hours at room temperature. 26g of 98% H 3 PO 4 was added to the solution followed by stirring under reflux for 3 hours. The solution was then cooled to room temperature and a precipitate which had formed was recovered by filtration. The precipitate was washed thoroughly with water (about 5£). A blue solid was obtained which was oven-dried for 12 hours at 150°C to form a catalyst precursor. EXAMPLE 5 VOHPO 4 JΛH 2 O (92% by mass) + 1.5% Zr promoter + 1.5% Cr promoter + 5% Ce promoter: A solvent comprising 90ml benzyl alcohol and 60ml isobutanol was added to 15g of V 2 O 5 , 1 .79g of Ce(NO 3 ) 3 .6H 2 O, 0.4g of ZrOCI 2 .8H 2 O and 0.124g of CrO 3> The solution so formed was refluxed for 7 hours and was then stirred for 16 hours at room temperature. 23g of 98% H 3 PO was added to the solution. The solution was cooled to room temperature and a precipitate which had formed was recovered by filtration. The precipitate was washed thoroughly with water (about 5 £). A blue solid was obtained which was oven-dried for 12 hours at 150°C to form a catalyst precursor. EXAMPLE 6 VOHPO 4 . y 2 H O (90% by mass) + 1 .5% Zr promoter + 8.5% Co promoter: A solvent comprising 90ml benzyl alcohol and 60ml isobutanol was used to dissolve 15g of V 2 O 5 and 0.4g of ZrOCI 2 .8H 2 O. The solution so formed was refluxed for 7 hours and was then stirred for 16 hours at room temperature. 26g of 98% H 3 PO 4 was added to the solution followed by the addition of 1.2g of Co 3 (PO 4 ) 2 -8H 2 O after which the solution was stirred under reflux for 3 hours. The solution was then cooled to room temperature and a precipitate which had formed was recovered by filtration. The precipitate was washed thoroughly with water (about 5 £). A blue solid was obtained which was oven-dried for 12 hours at 150°C to form a catalyst precursor. EXAMPLE 7 VOHPO 4 , J4H 2 O (89% by mass) + 1 % Bi promoter + 5% Mn promoter + 5% Ce promoter: A solvent comprising 90ml benzyl alcohol and 60ml isobutanol was used to dissolve 15g of V 2 O 5 , 0.82g of MnCl 2 .4H 2 O, 1.79g of Ce(NO 3 ) 3 .6H 2 O and 0.21 1 g of (BiO) 2 .CO 3 . The solution so formed was refluxed for 7 hours and was then stirred for 16 hours at room temperature. 24g of 98% H P0 4 was then added to the solution followed by stirring under reflux for 3 hours. The solution was then cooled to room temperature and a precipitate which had formed was recovered by filtration. The precipitate was washed thoroughly with water (about 5£). A blue solid was obtained whioh was oven-dried for 12 hours at 150°C to form a catalyst precursor. EXAMPLE 8 VOHPO 4 . %H 2 O (90.5% by mass) + 1 % Bi promoter + 8.5% Co promoter: A solvent comprising 90ml benzyl alcohol and 60ml isobutanol was used to dissolve 15g of V 2 Og and 0.21 1 g of (BϊO) 2 .CO 3 . The solution so formed was refluxed for 7 hours and then stirred for 16 hours at room temperature. 26g of 98% H 3 PO was added to the solution followed by the addition of 1.2g of Co 3 (PO 4 ) 2 .8H 2 O, followed in turn by stirring under reflux for 3 hours. The solution was then cooled to room temperature and a precipitate which had formed was recovered by filtration. The precipitate was washed thoroughly with water (about 5£). A blue solid was obtained which was oven- dried for 12 hours at 150°C to form a catalyst precursor. EXAMPLE 9 VOHPO 4 , J4H 2 O (90.5% by mass) + 1 % Bi promoter + 8.5% Ce promoter: A solvent comprising 90ml benzyl alcohol and 60ml isobutanol was used to dissolve 15g of V 2 O 5 , 3.04g of Ce(NO 3 ) 3 .6H 2 O and 0.21 1 g of (BiO) 2 .CO 3 . The solvent so formed was refluxed for 7 hours after which it was stirred for 16 hours at room temperature. 26g of 98% H 3 PO 4 was added to the solution followed by stirring under reflux for 3 hours. The solution was cooled to room temperature and a precipitate which had formed was recovered by filtration. The precipitate was washed thoroughly with water (about 5£). A blue solid was obtained which was oven-dried for 12 hours at 150°C to form a catalyst precursor. EXAMPLE 1 0 VOHP0 4 J/ 2 H 2 0 (89% by mass) + 1 % Bi promoter + 1 .5 % Zr promoter + 8.5 % Ce promoter: A solvent comprising 90ml benzyl alcohol and 60ml isobutanol was used to dissolve 1 5g of V 2 0 5 , 0.4g of ZrOCI 2 .8H 2 0, 3.04g of Ce(N0 3 ) 3.6H 2 0 and 0.21 1 g of (BiO) 2 > C0 3 . The solution to formed was refluxed for 7 hours and then stirred for 1 6 hours at room temperature. 28g of 98% H3PO4 was added to the solution followed by stirring under reflux for 3 hours. The solution was cooled to room temperature and a precipitate which had formed was recovered by filtration. The precipitate was washed thoroughly with water (about 50. A blue solid was obtained which was oven-dried for 1 2 hours at 1 50°C to form a catalyst precursor. EXAMPLE 1 1 VOHP0 4 . 1 /2 H 2 0 (89%) + 1 % Bi promoter + 1 5 %Zr promoter + 8.5 % Co promoter: A solvent comprising 90ml benzyl alcohol and 60ml isobutanol was used to dissolve 1 5g of V 2 0 5 0.4g of ZrOCI 2 8H 2 0 and 0.21 1 g of (Bι0) 2 .C0 3 The solution so formed was refluxed for 7 hours and then stirred for 1 6 hours at room temperature. 27g of 98% H3PO4 was added to the solution „ __ followed by the addition of 1 .2g of Cθ3(P0 4 ) 2 .8H 2 0 followed in turn by stirring under reflux for 3 hours. The solution was cooled to room temperature and a precipitate which had formed was recovered by filtration The precipitate was washed thoroughly with water (about 5 0. A blue solid was obtained which was oven-dried for 1 2 hours at 1 50°C to form a catalyst precursor. EXAMPLE 1 2 VOHP0 4 . , / J H 2 0 (85 % by mass) + 5 % Mn promoter + 5 % Mg promoter + 5% Ce promoter: A solvent comprising 90ml benzyl alcohol and 60ml isobutanol was used to dissolve 1 5g of V 2 Og 0J 67g of MgO, 1 .79g of Ce(N0 3 )3.6H 2 0 and 0.82g of MnCI 2 .4H 2 0. The solution so formed was refluxed for 7 hours after which it was stirred for 1 6 hours at room temperature. 27g of 98% H3PO4 was added followed by the addition of 1 .2g of Cθ3<Pθ4) 2 .8H 2 0, followed in turn by stirring under reflux for 3 hours. The solution was cooled to room temperature and a precipitate was obtained which was recovered by filtration. The precipitate was washed thoroughly with water (about 50. A blue solid was oven dried for 1 2 hours at 1 50°C to form a catalyst precursor. EXAMPLE 1 3 VOHPO4J2 H2O ( 10% by mass) + 5% Mo promoter + 5 % Mn promoter: A solvent comprising of 90ml benzyl alcohol and 60ml isobutanol was used to dissolve 1 5g of V 2 0 5 0.82g of MnCI 2 -4H 2 0 and 0.6g of M0O3. The solution so formed was refluxed for 7 hours and then stirred for 1 6 hours at room temperature. 27g of 98% H3PO4 was added, followed by the addition of 1 .2g of Cθ3(Pθ4) 2 .8H 2 0, followed in turn by stirring under reflux for 3 hours. The solution was cooled to room temperature and a precipitate was obtained which was removed by filtration. The precipitate was washed thoroughly with water (about 5 0. A blue solid was oven-dried for 1 2 hours at 1 50°C to obtain a catalyst precursor. With regard to Examples 1 - 1 3 it should be noted that the benzyl alcohol and isobutanol were fully miscible and formed a solvent to which the V 2 0g was added to produce V^ + ions. The benzyl alcohol in turn acted as a reductant under refluxing to reduce the mixture of V cations and V 5 + cations to V cations. The various dopant or promoter compounds, containing the various dopant or promoter metals, were added, after the V 2 0g was added, to the solvent from which the catalyst precursor was eventually precipitated upon cooling to room temperature after the stirring and refluxing were completed. In the case of Examples 2 - 1 3 the oven-dried blue precursor was in each case calcined according to the procedure and heating regime described in Example 1 to obtain various novel VPO catalysts. These novel catalysts were tested regarding their ability to catalyze conversion of butane to maleic anhydride, butene to maleic anhydride, pentane to maleic anhydride, phthalic anhydride and acetic acid, and pentene to maleic anhydride, phthalic anhydride and acetic acid, and in each case the novel catalysts were found to out-perform the standard or control catalyst with which they were compared, with regard to one or more of percentage butane conversion, percentage selectivity to produce maleic anhydride or percentage yield. It has also been found that by varying either the temperature or gas hourly space velocity or both, the selectivity to maleic anhydride and phthalic anhydride can be varied, as set forth in Table 3 hereunder. TABLE 3: Comparison of Novel VPO Catalysts at Equilibation

Claims: CLAIMS: 1 . A method of making a vanadium phosphorus oxide (VPO) catalyst, the method comprising the steps of: precipitating, from a solution comprising dissolved V 4 + ions and V° + ions at a total concentration of 45 - 65 g/ f , a vanadium-containing and phosphorus- containing precipitate comprising a complex in accordance with the formula VOHP0 4 ' y * H 2 0; and calcining the precipitate under an inert atmosphere, to produce a VPO catalyst having an active phase in accordance with the formula (V0) 2 P 2 0g, the solution from which the precipitate is precipitated comprising dissolved cations of at least two dopant metals selected from the group consisting of Bi, Zr, Cr, Ce, Co, Mn, Mg and Mo, said dissolved dopant metal cations being present in the solution in proportions such that the precipitate comprises 1 - 25% by mass of dopant metal cations in total, the balance being the VOHPO4 • V∑ I-^O complex, each dopant metal forming OJ - 20% by mass of the precipitate. 2. A method as claimed in claim 1 , in which the total concentration of dissolved V 4"1" ions and V° + ions in the solution is 50 - 60 gi t , the dissolved dopant metal cations being present in the solution in proportions such that the precipitate comprises 2- 20 % by mass of the dopant metals in total, each dopant metal forming 0.5 - 1 5% by mass of the precipitate, the ratio of dissolved V 4 + ιons:V^ + ions in the solution being such that the molar proportion of the V 5 + loojun the VPO catalyst is OJ - 1 0 mole % . 3. A method as claimed in claim 2, in which the solution from which the precipitate is precipitated comprises dissolved cations of 2 - 3 dopant metals selected from said group consisting of Bi, Zr, Cr, Ce, Co, Mr, Mg and Mo 4. A method as claimed in claim 3, in which one of the dopant metals is Bi, Bi cations being present in the solution from which the precipitate is precipitated in a proportion such that Bi forms 1 - 1 5 % by mass of the precipitate, the solution comprising, in addition to the Bi cations, cations of 1 - 2 other dopant metals selected from: Zr; Mn and Ce; Co; Ce; Zr and Ce; and Zr and Co. 5. A method as claimed in claim 3, in which one of the dopant metals is Zr, Zr cations being present in the solution from which the precipitate is precipitated in a proportion such that Zr forms 1 - 1 5 % by mass of the precipitate, the solution comprising, in addition to the Zr cations, cations of 1 - 2 other dopant metals, selected from: Bi; Cr; Ce and Cr; Ce; Co; Bi and Ce, and 6. A method as claimed in claim 3, in which one of the dopant metals is Cr, Cr cations being present in the solution from which the precipitate is precipitated in a proportion such that Cr forms 1 - 1 5 % by mass of the precipitate, the solution comprising, in addition to the Cr cations, cations of 1 - 2 other dopant metals, selected from: Zr; and Ce and Zr. 7. A method as claimed in claim 3, in which one of the dopant metals is Ce, Ce cations being present in the solution from which the precipitate is precipitated in a proportion such that Ce forms 1 - 1 5 % by mass of the precipitate, the solution comprising, in addition to the Ce cations, cations of 1 - 2 other dopant metals, selected from: Zr and Cr; Zr; Bi and Mn; Bi; Bi and Zr; and Mn and Mg. 8. A method as claimed in claim 3, in which one of the dopant metals is Co, Co cations being present in the solution from which the precipitate is precipitated in a proportion such that Co forms 1 - 1 5 % by mass of the precipitate, the solution comprising, in addition to the Co cations, cations of 1 - 2 other dopant metals, selected from: Zr; Bi; and Bi and Zr. 9. A method as claimed in claim 3, in which one of the dopant metals is Mn, Mn cations being present in the solution from which the precipitate is precipitated in a proportion such that Mn forms 1 - 1 5% by mass of the precipitate, the solution comprising, in addition to the Mn cations, cations of 1 - 2 other dopant metals, selected from: Bi and Ce; Mg and Ce; and Mo. 1 0. A method as claimed in claim 3, in which one of the dopant metals is Mg, Mg cations being present in the solution from which the precipitate is precipitated in a proportion such that Mg forms 1 - 20% by mass of the precipitate, the solution comprising cations of Mn and Ce dopant metals in addition to the Mg cations. 1 1 . A method as claimed in claim 3, in which one of the dopant metals is Mo, Mo cations being present in the solution from which the precipitate is precipitated 5 in a proportion such that Mo forms 1 - 20% by mass of the precipitate, the solution comprising cations of Mn dopant metal in addition to the Mo cations. 1 2. A method as claimed in any one of the preceding claims, in which the solution comprises a solvent selected from alcohols and mixtures of two or more alcohols. 1 0 1 3. A method as claimed in claim 1 2, in which the solvent is a mixture of two alcohols, the alcohols being present in a mass ratio of 1 :2 - 2: 1 . 1 4. A method as claimed in claim 1 2 or claim 1 3, in which the solvent is anhydrous, each alcohol being selected from: isobutanol; 1 5 benzyl alcohol; ethanol; octanol; 2-butanol; isopropanol; and 20 mixtures of any two or more thereof. 1 5. A method as claimed in claim 1 4, in which the solvent is a mixture of two said alcohols. 1 6. A method as claimed in any one of the preceding claims, which includes the preliminary step of obtaining the solution of the V ions and V + ions in the 25 solution by dissolving V° + ions in the solvent and reducing a portion of the V b + ions to V + ions. 1 7. A method as claimed in claim 1 6, in which the reducing of the V 5 + ions to V 4 + ions is by means of a reducing agent, the method including refluxing the solvent containing the V^ + ions dissolved therein with the reducing agent. 1 8. A method as claimed in claim 1 , substantially as described herein with reference to the Examples. 1 9. A VPO catalyst, whenever made in accordance with the method of any one of the preceding claims.

Inventors: SOOKRAJ SADESH HARICHAND, SOOKRAJ, SADESH, HARICHAND
Applicants: SASOL CHEMICALS EUROP LTD, SASOL TECH PTY LTD, SOOKRAJ SADESH HARICHAND, SASOL CHEMICALS EUROPE LIMITED, SASOL TECHNOLOGY (PROPRIETARY) LIMITED, SOOKRAJ, SADESH, HARICHAND
Application year: 1998
Main classification: B01J27
IPC codes: B01J27, C07C51