Austenitic stainless steel valve

Abstract: An austenitic stainless steel valve which is used at 100°C or higher and easy to handle at the beginning of use. The valve has a valve body (1) made from an austenitic stainless steel, and a stem (4) adapted to be reciprocated to open and close the valve. The stem is made from a metal having a thermal expansion coefficient that is ten-thirteenths or less of that of an austenitic stainless steel. Such a metal may be a ferritic or martensitic stainless steel. With this arrangement, it is possible to restrict the compressive stress applied to the stem within the allowable stress of the material of the stem and thus to prevent the destruction of the seat (3) or the bending of the stem (4). The valve can thus be handled easily.

Description: BACKGROUND OF THE INVENTION This invention relates to stainless steel valve used at high temperatures in e.g. the chemical industry and which is easy to handle at the start of its use. Prior art is a valve, particularly designed compatible for use with toxic or highly flammable fluids (US-A-4 585 210). Most of the parts of this valve are made of stainless steel. Figs. 1 and 2 show Y-type globe valves, which are typical stainless steel valves used at high temperatures, typically at 100 °C or over. These valves have a valve body 1 having a passage 2 formed therethrough and provided with a seat 3. A stem 4 is axially movably mounted on the valve body 1. A gland plate 7 and a gland bolt 8 compress and retain a gland packing 6 sandwiched between the stem 4 and a cover flange 5. A yoke 9 is fixed to the valve body 1 so as to extend parallel to the stem 4. A yoke flange 10 is mounted around one end of the stem 4 and fixed to the yoke 9. Rotatably inserted in the yoke flange 10 is a sleeve 11 formed with female threads in mesh with male threads 13 formed on the stem 4. A handle 14 is fixed to the sleeve 11 to turn it. A rotation stopper 15 fixed to the stem 4 prevents rotation of the stem 4 by abutting the yoke 9. The stem 4 is moved by engagement with the sleeve 11. The valve of Fig. 1 has a separate disk 16 mounted to the tip of the stem 4. The valve of Fig. 2 has a disk 16 integrally formed at the tip of the stem 4. When the sleeve 11 is turned by turning the handle 14, the stem 4 is moved axially because it cannot rotate. When the stem 4 is advanced, the disk 16 at the tip of the stem is pressed against the seat 3, stopping the fluid flow through the passage 2. Thus, in this type of valve, while the valve is closed with the stem 4 compressed between the seat 3 and the sleeve 11 of the yoke flange 10, a compressive stress acts on the valve parts. The female threads 12 of the sleeve 11 and the male threads of the stem 4 have a smaller lead than the friction angle so that the stem 4 will not loosen under reaction force from the seat 3, i.e. thrust while the valve is closed. The valves of Figs. 1 and 2 are manual valves. But a pneumatic means or an electric motor may be used to axially move the stem 4. Structurally, such "power" valves have practically nothing different from the valves shown. If such a valve is intended to be used at high temperatures, its valve body 1 is made from an austenitic stainless steel, and a heating jacket 17 is provided around the valve body 1. To use such a valve at high temperatures, the valve has to be first heated to a predetermined temperature. An austenitic stainless steel, from which the valve body 1 is made, is high in thermal expansion coefficient. When the valve is heated in a closed state, the valve body 1 and the stem 4 are heated to higher temperatures than the yoke 9. The stem 4 is thus thermally expanded to a greater degree than the valve body 1 and the yoke 9 combined. If the valve were closed when heated, the seat 3 might be destroyed, and/or the stem 4 might be bent due to excessive compressive stress acting on the stem 4. Thus, in order to prevent excessive stress acting on the stem, the valve has to be kept slightly open while the valve is being heated. The valve body 1 is made from an austenitic stainless steel to improve corrosion resistance. Thus, if the valve body 1 is made from an austenitic stainless steel, it is an ordinary practice to also make other parts that are brought into contact with fluid, such as the stem 4, from an austenitic stainless steel. The yoke 9, which is kept out of contact with fluid, is usually made from inexpensive carbon steel. For a valve of this type, calculation was made of the compressive stress that acted on the stem 4 when the valve is heated to 300 °C with the valve closed. In our experiment, when the valve body was heated to 300°C, the temperature of the stem 4 and the yoke 9 at their exposed portion were 80 °C and 50 °C, respectively. If this valve is closed at 20 °C and heated to 300°C, then the valve body temperature changes 280 °C (= 300 - 20). The stem temperature, which is herein assumed to be the average of temperatures at its hottest and coldest portions, changes 170 °C = (300 + 80)/2 - 20. The yoke temperature changes 30°C (= 50-20). Supposing that the length from the seat of the valve body to the yoke mounting portion is L, the length of the yoke was 1.5L and the length from the seat of the stem to the driving screw portion was 2.5L. The thermal expansion amounts at the respective parts are calculated below: Stem: 170 x 1.7 x 10 -5 x 2.5L = 7.225 x 10 -3 x L Valve body and yoke combined: 280 x 1.7 x 10 -5 x L + 30 x 1.1 x 10 -5 x 1.5L = 4.810 x 10 -3 x L wherein 1.7 x 10 -5 and 1.1 x 10 -5 are thermal expansion coefficients of an austenitic stainless steel and carbon steel at the respective temperatures. From the above equations, it is apparent that the stem will expand by 2.415 x 10 -3 x L longer than the combined elongation of the valve body and yoke. Since the modulus of longitudinal elasticity of an austenitic stainless steel is about 21000 kg/mm 2 , the compressive stress that acts on the stem at this time will be: σ = 21,000 x 2.415 x 10 -3 = 50.7kg/mm 2 At 200-300°C, the allowable stress of an austenitic stainless steel is about 10kg/mm 2 at the most. Thus, it is apparent that the stem cannot withstand such a large stress. Since the seat and the stem head are tapered, the stem head will cut into the seat if the difference in thermal expansions of the respective parts is large as above, thus resulting in the seat being destroyed, and/or the stem being bent under excessive compressive stress. In either case, the valve fails. Thus, when such a valve is heated, it is essential to keep the valve slightly open. An object of the present invention is to provide an austenitic stainless steel valve which is easy to handle at the beginning of use. SUMMARY OF THE INVENTION According to this invention, there is provided a stainless steel valve comprising a stem adapted to be reciprocated to open and close the valve, and a valve body made from an austenitic stainless steel, the stem being made from a stainless steel having a thermal expansion coefficient that is ten-thirteenths or less of the thermal expansion coefficient of an austenitic stainless steel. The stem may be made from one of ferritic and martensitic stainless steels. The valve may be further provided with a jacket for heating the valve body. Other features and objects of the present invention will become apparent from the following description made with reference to the accompanying drawings, in which: BRIEF DESCRIPTION OF THE DRAWINGS Figs. 1 and 2 are sectional views of a Y type globe valve; Figs. 3 and 4 are sectional views of a flushing valve; Fig. 5 is a sectional view of a sampling valve; and Fig. 6 is a sectional view of a three-way changeover valve. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENT An embodiment of this invention is now described with reference to the drawings. Structurally, valves according to this invention are exactly the same as those shown in Figs. 1 and 2. While their valve bodies 1 are made from an austenitic stainless steel, the stem 4 is made from a stainless steel having a thermal expansion coefficient that is ten-thirteenths or less of that of an austenitic stainless steel. Such metals include ferritic stainless steels and martensitic stainless steels. Fortunately, austenitic, ferritic and martensitic stainless steels have different alloy compositions and thus different thermal expansion coefficients.' That is, as mentioned earlier, austenitic stainless steels have a thermal expansion coefficient of 1.7 x 10 -5 /°C, while ferritic and martensitic stainless steel have a thermal expansion coefficient near that of carbon steel, i.e. 1.1 x 10 -5 /°C. For a valve having a valve body made from an austenitic stainless steel, and a stem made from a ferritic or martensitic stainless steel instead of an austenitic stainless steel, the thermal expansion coefficients of the stem and the valve body + yoke are calculated as follows: stem: 170 x 1.1 x 10 -5 x 2.5L = 4.675 x 10 -3 x L valve body + yoke: 280 x 1.7 x 10 -5 x L + 30 x 1.1 x 10 -5 x 1.5L = 4.810 x 10 -3 x L As shown, there is practically no difference between the thermal expansion coefficients of the stem 4 and the valve body 1 and yoke 9 combined, so that no excessive load is applied to the stem when the valve is heated. But ferritic and martensite stainless steels are inferior in corrosion resistance to austenitic stainless steels, and thus may not be usable according to the kind of fluid used. In such a case, instead of a ferritic or martensitic stainless steel, the stem 4 may be made from a corrosion-resistant, low-thermal-expansion stainless steel such as SUS630 or SUS329J1. Although the thermal expansion coefficient of these steels is slightly higher than that of ferritic and martensitic stainless steels, i.e. 1.1 x 10 -5 /°C but are still sufficiently low, i.e. 1.2 x 10 -5 /°C. For a valve of this combination, the thermal expansions of the stem and the valve body;and yoke combined will be: stem: 170 x 1.2 x 10 -5 x 2.5L = 5.100 x 10 -3 x L valve body and yoke combined: 280 x 1.7 x 10 -5 x L + 30 x 1.1 x 10 -5 x 1.5L = 4.810 x 10 -3 x L The compressive stress on the stem 4 due to the difference between the thermal expansions will be: σ = 21,000 x (5.1000 - 4.810) x 10 -3 = 6.09kg/mm 2 This value is well within the allowable stress of these stainless steels. The inventors found out that the object of this invention is achievable by making the stem 4 from a material having a thermal expansion coefficient that is ten-thirteenths or less of that of the material of the valve body 1. Fortunately, besides the fact that these stainless steels have a thermal expansion coefficient near to that of carbon steel than to an austenitic stainless steel, they are higher in allowable stress than an austenitic stainless steel. The valve body 1 is made from an austenitic stainless steel, the yoke 9 is made from carbon steel, and the stem 4 is made from a ferritic or martensitic steel. If a corrosion resistance comparable to that of stainless steel 304 is required, the stem 4 may be made from stainless steel 630. If a corrosion resistance comparable to stainless steel 316 is required, the stem is made from stainless steel 329J. For higher safety, the yoke 9 may be made from an austenite stainless steel to further increase its thermal expansion. The concept of this invention is also applicable to flushing valves shown in Figs. 3 and 4, a sampling valve shown in Fig. 5, a three-way changeover valve shown in Fig. 6, and other valves such as gate valves, tank valves and pistons valves. As described above, according to this invention, when the valve is heated for use at high temperatures, it is possible to restrict the compressive stress applied to the stem within the allowable stress of the material of the stem. Thus, it is possible to prevent the destruction of the seat or the bending of the stem even without slightly opening the valve when it is heated. The valve can thus be handled easily.

Claims: A stainless steel valve comprising a stem (4) threadedly driven to open and close the valve, and a valve body (1) made from an austenitic stainless steel, said stem (4) being made from a stainless steel having a thermal expansion coefficient that is ten-thirteens or less of the thermal expansion coefficient of an austenitic stainless steel. A valve as claimed in claim 1 wherein said stem (4) is made from one of ferritic stainless steel and martensitic stainless steel. A valve as claimed in claim 1 or 2 further comprising a jacket (17) for heating said valve body (1).

Inventors: KANESHIGE NORITSUGU, KANESHIGE, NORITSUGU
Applicants: ASKA CORP, ASKA CORPORATION
Application year: 1998
Main classification: F16K27
IPC codes: F16K1, F16K27