Use of a heat-resisting cast steel

Abstract: This invention provides a heat-resisting cast steel which is a high-Cr steel material having excellent high-temperature strength and hence suitable for use as a high-temperature steam turbine casing material capable of being used even at a steam temperature of 600°C or above. This heat-resisting cast steel contains, on a weight percentage basis, 0.07 to 0.15% carbon, 0.05 to 0.30% silicon, 0.1 to 1% manganese, 8 to 10% chromium, 0.01 to 0.2% nickel, 0.1 to 0.3% vanadium, a total of 0.01 to 0.2% niobium and tantalum, 0.1 to 0.7% molybdenum, 1 to 2.5% tungsten, 0.1 to 5% cobalt, 0.001 to 0.03% nitrogen and 0.002 to 0.01% boron, the balance being iron and incidental impurities.

Description: BACKGROUND OF THE INVENTION 1. Field of the invention This invention relates to the use of heat-resisting cast steels as structural materials for the manufacture of pressure vessels such as the casings of steam turbines for thermal electric power generation. 2. Description of the related art Conventionally used high-temperature casing materials used in steam turbine plants for thermal electric power generation include 2.25%CrMo cast steel, CrMo cast steel, CrMoV cast steel and 12Cr cast steel. Among these cast steels, the use of cast steels comprising low-alloy steels such as 2.25%CrMo cast steel, CrMo cast steel and CrMoV cast steel is restricted to plants having a steam temperature up to 566°C because of their limited high-temperature strength. On the other hand, 12Cr cast steel (e.g., those disclosed in Japanese Patent Application No. 59-216322 and the like) have more excellent high-temperature strength than cast steels comprising low-alloy steels, and can hence be used in plants having a steam temperature up to approximately 600°C. However, if the steam temperature exceeds 600°C, 12Cr cast steel has insufficient high-temperature strength and can hardly be used for pressure vessels such as steam turbine casings. EP-A-0 691 416 and JP-A-7286246 describe wrought steels, for example, by forging and/or rolling for parts for boiler tubes and the like. EP-A-0 887 431 also describes a forged heat-resisting steel for turbine rotors and the like. However, all of the steels described in these references have compositions which may produce δ-phase in steels which are not worked after casting. SUMMARY OF THE INVENTION An object of the present invention is to provide heat-resisting cast steels which are high-Cr steel materials having excellent high-temperature strength and hence suitable for use as high-temperature steam turbine casing materials capable of being used even at a steam temperature of 600°C or above. To this end, the present inventors made intensive investigations and have now found the following excellent heat-resisting cast steels. A heat-resisting cast steel in accordance with the present invention contains, on a weight percentage basis, 0.07 to 0.15% carbon, 0.05 to 0.30% silicon, 0.1 to 1% manganese, 8 to 10% chromium, 0.01 to 0.2% nickel, 0.1 to 0.3% vanadium, a total of 0.01 to 0.2% niobium and tantalum, 0.1 to 0.7% molybdenum, 1 to 2.5% tungsten, 0.1 to 5% cobalt, 0.001 to 0.03% nitrogen and 0.002 to 0.01% boron, the balance being iron and incidental impurities. The heat-resisting cast steel in accordance with the present invention may optionally contain, on a weight percentage basis, 0.001 to 0.2% neodymium. The heat-resisting cast steel in accordance with the present invention is a heat-resisting cast steel having an index A (%) defined by the following equation on a weight percentage basis is 8% or less. Index A (%) = (Cr content) (%) + 6(Si content) (%) + 4(Mo content) (%) + 3(W content) (%) + 11(V content) (%) + 5(Nb content) (%) - 40(C content) (%) - 2(Mn content) (%) - 4(Ni content) (%) - 2(Co content) (%) - 30(N content) (%) The heat-resisting cast steel of the present invention has excellent high-temperature strength and is hence useful as a high-temperature steam turbine casing material for use in hypercritical-pressure electric power plants having a steam temperature higher than 600°C. Thus, the heat-resisting cast steel of the present invention is useful in raising the operating temperature of the current hypercritical-pressure electric power plants (having a steam temperature of about 600°C) to afford a saving of fossil fuels and, moreover, to reduce the amount of carbon dioxide evolved and thereby contribute to the improvement of global environment. The heat-resisting cast steel according to the invention contains B so that its high-temperature strength is improved. Consequently, the heat-resisting cast steel makes it possible to operate hypercritical-pressure electric power plants with higher reliability. The effects of the index A(%) in the heat-resisting cast steel of the present invention are that it provides a material in which the formation of δ-ferrite (a structure causing a reduction in high-temperature strength and also a reduction in ductility and toughness) is prevented by imposing restrictions on the contents of alloying elements. Thus, the heat-resisting cast steel of the present invention makes it possible to operate hypercritical-pressure electric power plants at higher temperatures, and is hence useful in affording a saving of fossil fuels and reducing the amount of carbon dioxide evolved. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS The present inventors made intensive investigations in order to improve high-temperature strength by using a high-Cr steel as a basic material and controlling the contents of alloying elements strictly, and have now discovered new heat-resisting cast steels having excellent high-temperature strength characteristics which have not been observed in conventional materials, especially for the use as defined in claim. The reasons for content restrictions in the heat-resisting cast steel of the present invention are described below. In the following description, all percentages used to represent contents are by weight unless otherwise stated. C (carbon): C, together with N, forms carbonitrides and thereby contributes to the improvement of creep rupture strength. Moreover, C acts as an austenite-forming element to inhibit the formation of δ-ferrite. If its content is less than 0.07% by weight, no sufficient effect will be produced, while if its content is greater than 0.15% by weight, the carbonitrides will aggregate during use to form coarse grains, resulting in a reduction in long-time high-temperature strength. In addition, high C contents will bring about poor weldability and may hence cause difficulties such as weld crack during the manufacture of pressure vessels and the like. For these reasons, C must not be added in an amount greater than that required to improve high-temperature strength by the formation of carbonitrides and to inhibit the formation of δ-ferrite. Accordingly, the content of C should be in the range of 0.07 to 0.15%. The preferred range is from 0.08 to 0.14%. Si (silicon): Si is effective as a deoxidizer. Moreover, Si is an element required to secure good melt flowability because, for cast steel materials, the melt needs to be flow into all the corners of the mold. However, since Si has the effect of causing a reduction in toughness and high-temperature strength and, moreover, promoting the formation of δ-ferrite, it is necessary to minimize its content. If its content is less than 0.05%, sufficient melt flowability cannot be secured, while if its content is greater than 0.3%, difficulties as described above will manifest themselves. Accordingly, the content of Si should be in the range of 0.05 to 0.3%. The preferred range is from 0.1 to 0.25%. Mn (manganese): Mn is an element which is useful as a deoxidizer. Moreover, Mn has the effect of inhibiting the formation of δ-ferrite. On the other hand, the addition of a large amount of this element will cause a reduction in creep rupture strength. Consequently, the addition of more than 1% of Mn is undesirable. However, with consideration for forging at the stage of steel making, an Mn content of not less than 0.1% is advantageous from the viewpoint of cost because this makes scrap control easy. Accordingly, the content of Mn should be in the range of 0.1 to 1%. Cr (chromium): Cr form a carbide and thereby contributes to the improvement of creep rupture strength. Moreover, Cr dissolves in the matrix to improve oxidation resistance and also contributes to the improvement of long-time high-temperature strength by strengthening the matrix itself. If its content is less than 8%, no sufficient effect will be produced, while if its content is greater than 10%, the formation of δ-ferrite will tend to occur and cause a reduction in strength and toughness. Accordingly, the content of Cr should be in the range of 8 to 10%. The preferred range is from 8.5 to 9.5%. Ni (nickel): Ni is an element which is effective in improving toughness. Moreover, Ni also has the effect of reducing the Cr equivalent and thereby inhibiting the formation of δ-ferrite. However, since the addition of this element may cause a reduction in creep rupture strength, it is desirable to add Ni in a required minimum amount. In the present invention, Co is added as an element for exhibiting the effects of Ni, so that the role of Ni can be performed by Co. However, since Co is an expensive element, it is necessary from an economic point of view to reduce the content of Co as much as possible. Consequently, the formation of δ-ferrite is inhibited by adding not greater than 0.2% of Ni, though this may depend on other alloying elements. Its lower limit is determined to be 0.01% with consideration for the amount of Ni which is usually introduced as an incidental impurity. Accordingly, the content of Ni should be in the range of 0.01 to 0.2%. The preferred range is from 0.01 to 0.1%. V (vanadium): V forms a carbonitride and thereby improves creep rupture strength. If its content is less than 0.1%, no sufficient effect will be produced. On the other hand, if its content is greater than 0.3%, the creep rupture strength will contrarily be reduced. Accordingly, the content of V should be in the range of 0.1 to 0.3%. The preferred range is from 0.15 to 0.25%. Nb (niobium) and Ta (tantalum): Nb and Ta form carbonitrides and thereby contribute to the improvement of high-temperature strength. Moreover, they cause finer carbides (M 23 C 6 ) to precipitate at high temperatures and thereby contribute to the improvement of long-time creep rupture strength. If their total content is less than 0.01% by weight, no sufficient effect will be produced. On the other hand, if their total content is greater than 0.2% by weight, the carbides of Nb and Ta formed during the manufacture of steel ingots will fail to dissolve fully in the matrix during heat treatment, resulting in a reduction in toughness. Accordingly, the total content of Nb and Ta should be in the range of 0.01 to 0.2%. The preferred range is from 0.03 to 0.07%. Mo (molybdenum): Mo, together with W, dissolves in the matrix and thereby improves creep rupture strength. If Mo is added alone, it may be used in an amount of about 1.5%. However, where W is also added as is the case with the present invention, W is more effective in improving high-temperature strength. Moreover, if Mo and W are added in unduly large amounts, δ-ferrite will be formed to cause a reduction in creep rupture strength. Since the addition of W alone fails to give sufficient high-temperature strength, at least a slight amount of Mo needs to be added. That is, the content of Mo should be not less than 0.1% in this cast steel. Accordingly, with consideration for a balance with the content of W, the content of Mo should be in the range of 0.1 to 0.7%. The preferred range is from 0.1 to 0.5%. W (tungsten): As described above, W, together with Mo, dissolves in the matrix and thereby improves creep rupture strength. W is an element which exhibits a more powerful solid solution strengthening effect than Mo and is hence effective in improving high-temperature strength. However, if W is added in an unduly large amount, δ-ferrite and a large quantity of Laves phase will be formed to cause a reduction in creep rupture strength. Accordingly, with consideration for a balance with the content of Mo, the content of W should be in the range of 1 to 2.5%. The preferred range is from 1.5 to 2%. Co (cobalt): Co dissolves in the matrix to inhibit the formation of δ-ferrite. Although Co has the function of inhibiting the formation of δ-ferrite like Ni, Co does not reduce high-temperature strength as contrasted with Ni. Consequently, if Co is added, strengthening elements (e.g., Cr, W and Mo) may be added in larger amounts than in the case where no Co is added. As a result, high creep rupture strength can be achieved. Furthermore, Co also has the effect of enhancing resistance to temper softening and is hence effective in minimizing the softening of the material during use. These effects are manifested by adding Co in an amount of not less than 0.1%, though it may depend on the contents of other elements. However, in the compositional system of the heat-resisting cast steel of the present invention, the addition of more than 5% of Co tends to induce the formation of intermetallic compounds such as σ phase. Once such intermetallic compounds are formed, the material will become brittle. In addition, this will also lead to a reduction in long-time creep rupture strength. Accordingly, the content of Co should be in the range of 0.1 to 5%. The preferred range is from 2 to 4%. N (nitrogen): N, together with C and alloying elements, forms carbonitrides and thereby contributes to the improvement of high-temperature strength.As described above, N, together with C and alloying elements, forms carbonitrides and thereby contributes to the improvement of high-temperature strength. On the other hand, in this heat-resisting cast steel, not only the formation of carbonitrides, but also the addition of B as will be described later is also effective in improving high-temperature strength. However, B combines easily with N in steel to form a nonmetallic inclusion, BN. Consequently, in steel containing N, the effect of B added thereto is negated by N and, therefore, B fails to bring about a sufficient improvement in high-temperature strength. In order to allow the addition of B to exhibit its effect to the fullest extent, the amount of N added must be minimized. Thus, where it is desired to make the most of the effect produced by the addition of B and thereby improve high-temperature strength, the content of N should desirably be not greater than 0.01%. However, where B is added in order to produce an effect which is not necessarily sufficient but serves to supplement the precipitation strengthening effect of carbonitrides, the addition of B can be expected to bring about an improvement in high-temperature strength at an N content of not greater than 0.03%. On the other hand, if the content of N is not less than 0.03%, sufficient high-temperature strength is secured by the formation of carbonitrides as shown in the aforesaid first and second heat-resisting cast steels. Accordingly, in the third heat-resisting cast steel in which high-temperature strength is improved by utilizing the effect of B to some extent, N contents up to 0.03% are allowed in order to minimized the formation of BN. On the other hand, the lower limit of the N content is an inevitably introduced level of not less than 0.001%. Thus, where the addition of B is taken into consideration, the content of N should be in the range of 0.001 to 0.03%. The preferred range is from 0.001 to 0.01%. B (boron): B has the effect of enhancing grain boundary strength and thereby contributes to the improvement of creep rupture strength. In particular, the heat-resisting cast steel of the present invention, which shows an improvement in creep rupture strength, is a material designed so that the effect of B may be exhibited to the utmost extent by limiting the content of N which inhibits the effect of B as has been explained in connection with N. However, if B is added in unduly large amounts exceeding 0.01%, a deterioration in weldability and a reduction in toughness will result. On the other hand, if the content of B is less than 0.002%, it will fail to produce a sufficient effect. Accordingly, the content of B should be in the range of 0.002 to 0.01%. The preferred range is from 0.003 to 0.007%. Nd (neodymium): Nd forms a carbide and a nitride which are finely dispersed into the matrix to improve high-temperature strength and, in particular, creep rupture strength. Moreover, it is believed that some Nd dissolves in the matrix and thereby contributes to solid solution strengthening. These effects are useful even when an extremely small amount of Nd is added. In fact, these effects are observed even at an Nd content of 0.001%. However, the addition of an unduly large amount of Nd will detract from the toughness of the material and thereby embrittle it. Accordingly, the content of Nd should be not greater than 0.2%. The preferred range is from 0.005 to 0.015%. The heat-resisting cast steel of the present invention is a heat-resisting cast steel wherein the above-defined index A is 8% or less. The reason why the index A is restricted to 8% or less is that, since the present invention relates to cast steel materials in which heat treatment alone, and not mechanical working, is relied on for diffusion, it is necessary to inhibit the formation of 8-ferrite positively by holding down this index A. EXAMPLES Example 1 (not according to the present invention) Example 1 is specifically described below. The chemical compositions of the test materials used therein are shown in Table 1. It is to be understood that the materials (1) used in this Example 1 correspond to the aforesaid first heat-resisting cast steel. Similarly, the materials (2) used in Example 2 correspond to the second heat-resisting cast steel, and so on. All test materials were prepared by melting the components in a 50 kg vacuum high-frequency furnace and pouring the resulting melt into a sand mold. Prior to use for various testing purposes, these test materials were subjected to a hardening treatment under conditions which simulated the central part of an air-quenched steam turbine casing having a thickness of 400 mm. Then, they were tempered at their respective tempering temperatures which had been determined so as to give a 0.2% yield strength of about 63-68 kgf/mm 2 . The mechanical properties of materials (1) and comparative materials, and their creep rupture test results (i.e., creep rupture times measured under the test conditions of 650°C x 13 kgf/mm 2 ) are shown in Table 2. As is evident from the results of room-temperature tension tests, the ductility (as expressed by elongation and reduction in area) and impact value of the materials (1) are stably higher, indicating their good weldability. Moreover, it can be seen that the creep rupture strength of the materials (1) is much more excellent than that of the comparative materials. In the as-cast state (i.e., the state not subjected to any heat treatment), the microstructure of each 50 kg test material on the casting top side of its main body was observed under an optical microscope to examine the degree of formation of δ-ferrite. The results of observation are summarized in Table 3. As contrasted with some comparative materials, no formation of δ-ferrite was noticed in the materials (1), indicating that they had a good microstructure. Example 2 (Not according to the present invention) Example 2 is specifically described below. The chemical compositions of materials (2) used for testing purposes are summarized in Table 4. The compositions of the materials (2) are based on the compositions of the materials (1) used in Example 1. That is, material No. 21 was obtained by reducing the content of Mn in material No. 1, and material No. 22 was obtained by reducing the content of Mn in material No. 2. Similarly, the compositions of other materials (2) were determined on the basis of the compositions of the corresponding materials (1). However, the contents of various components in the materials (2) are not exactly the same as those in the corresponding materials (1) because they may vary with the melting process. All test materials were prepared by melting the components in a 50 kg vacuum high-frequency furnace and pouring the resulting melt into a sand mold. Prior to use for various testing purposes, these test materials were subjected to a hardening treatment under conditions which simulated the central part of an air-quenched steam turbine casing having a thickness of 400 mm. Then, they were tempered at their respective tempering temperatures which had been set so as to give a 0.2% yield strength of about 63-68 kgf/mm 2 . In Table 5, the mechanical properties and creep rupture test results (i.e., creep rupture times measured under the test conditions of 650°C x 13 kgf/mm 2 ) of the inventive materials (2) tested in Example 2 are shown in comparison with those of the corresponding materials (1) tested in Example 1. The materials (2) do not differ appreciably in mechanical properties from the corresponding materials (1). On the other hand, the materials (2) show an increase in creep rupture time over the corresponding materials (1), indicating an improvement in creep rupture strength. It is believed that this improvement was achieved by reducing the content of Mn. When the microstructure of the inventive materials (2) was observed under an optical microscope, no formation of δ-ferrite was noticed as was the case with the inventive materials (1) tested in Example 1. Example 3 (According to the present invention) Example 3 is specifically described below. The chemical compositions of inventive materials (3) used for testing purposes are summarized in Table 6. Similarly to the materials (2), the compositions of the inventive materials (3) are based on the compositions of the materials (1), except that the content of N is reduced as compared with the materials (1) and B is added thereto. Specifically, material No. 31 was obtained by reducing the content of N in material No. 1 and adding B thereto. The compositions of other inventive materials (3) were determined in the same manner as described above. All test materials were prepared by melting the components in a 50 kg vacuum high-frequency furnace and pouring the resulting melt into a sand mold. Prior to use for various testing purposes, these test materials were subjected to a hardening treatment under conditions which simulated the central part of an air-quenched steam turbine casing having a thickness of 400 mm. Then, they were tempered at their respective tempering temperatures which had been determined so as to give a 0.2% yield strength of about 63-68 kgf/mm 2 . In Table 7, the mechanical properties and creep rupture test results (i.e., creep rupture times measured under the test conditions of 650°C x 13 kgf/mm 2 ) of the inventive materials (3) tested in Example 3 are shown in comparison with those of the corresponding materials (1) tested in Example 1. The inventive materials (3) do not differ appreciably in mechanical properties from the corresponding materials (1). On the other hand, the inventive materials (3) show a slight increase in creep rupture time over the corresponding materials (1), indicating a slight improvement in creep rupture strength. It is believed that this improvement was achieved by the addition of B. When the microstructure of the inventive materials (3) was observed under an optical microscope, no formation of δ-ferrite was noticed as was the case with the materials (1) and (2) tested in Examples 1 and 2. Example 4 (Not according to the present invention) Example 4 is specifically described below. The chemical compositions of materials (4) used for testing purposes are summarized in Table 8. Similarly to the inventive materials (3), the compositions of the materials (4) are based on the compositions of the materials (2), except that the content of N is reduced as compared with the materials (2) and B is added thereto. Specifically, material No. 41 was obtained by reducing the content of N in material No. 21 and adding B thereto. The compositions of other materials (4) were determined in the same manner as described above. All test materials were prepared by melting the components in a 50 kg vacuum high-frequency furnace and pouring the resulting melt into a sand mold. Prior to use for various testing purposes, these test materials were subjected to a hardening treatment under conditions which simulated the central part of an air-quenched steam turbine casing having a thickness of 400 mm. Then, they were tempered at their respective tempering temperatures which had been determined so as to give a 0.2% yield strength of about 63-68 kgf/mm 2 . In Table 9, the mechanical properties and creep rupture test results (i.e., creep rupture times measured under the test conditions of 650°C x 13 kgf/mm 2 ) of the materials (4) tested in Example 4 are shown in comparison with those of the corresponding materials (2) tested in Example 2. The materials (4) do not differ appreciably in mechanical properties from the corresponding materials (2). On the other hand, the materials (4) show a slight increase in creep rupture time over the corresponding materials (2), indicating a slight improvement in creep rupture strength. It is believed that this improvement was achieved by the addition of B. When the microstructure of the inventive materials (4) was observed under an optical microscope, no formation of δ-ferrite was noticed as was the case with the materials (1) to (3) tested in Examples 1 to 3. Example 5 (Samples 55 and 56 according to the present invention) Example 5 is specifically described below. The chemical compositions of inventive materials (5) used for testing purposes are summarized in Table 10. The compositions of the inventive materials (5) are based on the compositions of materials (1) to (4), except that a very small amount of Nd is added to the respective materials. Specifically, material Nos. 51 and 52 were obtained by adding Nd to material Nos. 1 and 2, respectively. Similarly, material Nos. 53, 54, [inventive 55, 56], 57 and 58 were obtained by adding Nd to material Nos. 22, 23, 34, 35, 41 and 42, respectively. Material Nos. 59 and 60, which are materials used to examine the influence of the Ni content, were obtained by increasing the content of Ni in material Nos. 22 and 41, respectively. However, as described in Examples 2 to 4, the contents of various components in the inventive materials (5) are not exactly the same as those in the corresponding materials (1) to (4) because they may vary with the melting process. All test materials were prepared by melting the components in a 50 kg vacuum high-frequency furnace and pouring the resulting melt into a sand mold. Prior to use for various testing purposes, these test materials were subjected to a hardening treatment under conditions which simulated the central part of an air-quenched steam turbine casing having a thickness of 400 mm. Then, they were tempered at their respective tempering temperatures which had been determined so as to give a 0.2% yield strength of about 63-68 kgf/mm 2 . In Table 11, the mechanical properties and creep rupture test results (i.e., creep rupture times measured under the test conditions of 650°C x 13 kgf/mm 2 ) of the inventive materials (5) tested in Example 5 are shown in comparison with those of the corresponding materials (1) to (4) tested in Examples 1 to 4. The inventive materials (5) do not differ appreciably in room-temperature tensile properties from the corresponding materials (1) to (4). Moreover, the inventive materials (5) show a slight reduction in impact value as a result of the addition of a very small amount of Nd, but this reduction is unworthy of serious consideration. On the other hand, the inventive materials (5) show an increase in creep rupture time over the corresponding materials (1) to (4), indicating that the addition of Nd brings about an improvement in creep rupture strength. When the microstructure of the inventive materials (5) was observed under an optical microscope, no formation of δ-ferrite was noticed as was the case with the inventive materials (1) to (4) tested in Examples 1 to 4. Example 6 (Not according to the present invention) Example 6 is specifically described below. The chemical compositions of materials (6) used for testing purposes are summarized in Table 12. The compositions of the materials (6) are based on the compositions of materials (1) to (4), except that a very small amount of Hf is added to the respective materials. Specifically, material Nos. 61 and 62 were obtained by adding Hf to material Nos. 1 and 2, respectively. Similarly, material Nos. 63, 64, 65, 66, 67 and 68 were obtained by adding Hf to material Nos. 22, 23, 34, 35, 41 and 42, respectively. Material Nos. 69 and 70, which are materials used to examine the influence of the Ni content, were obtained by increasing the content of Ni in material Nos. 22 and 41, respectively. However, as described in Examples 2 to 5, the contents of various components in the materials (6) are not exactly the same as those in the corresponding materials (1) to (4) because they may vary with the melting process. All test materials were prepared by melting the components in a 50 kg vacuum high-frequency furnace and pouring the resulting melt into a sand mold. Prior to use for various testing purposes, these test materials were subjected to a hardening treatment under conditions which simulated the central part of an air-quenched steam turbine casing having a thickness of 400 mm. Then, they were tempered at their respective tempering temperatures which had been determined so as to give a 0.2% yield strength of about 63-68 kgf/mm 2 . In Table 13, the mechanical properties and creep rupture test results (i.e., creep rupture times measured under the test conditions of 650°C x 13 kgf/mm 2 ) of the materials (6) tested in Example 6 are shown in comparison with those of the corresponding materials (1) to (4) tested in Examples 1 to 4. The materials (6) do not differ appreciably in room-temperature tensile properties from the corresponding materials (1) to (4). Moreover, the materials (6) show a slight reduction in impact value as a result of the addition of a very small amount of Hf, but this reduction is unworthy of serious consideration as is the case with the inventive materials (5). On the other hand, the materials (6) show an increase in creep rupture time over the corresponding materials (1) to (4), indicating that the addition of Hf brings about an improvement in creep rupture strength. When the microstructure of the materials (6) was observed under an optical microscope, no formation of δ-ferrite was noticed as was the case with the materials (1) to (5) tested in Examples 1 to 5. Example 7 (Not according to the present invention) Example 7 is specifically described below. The chemical compositions of materials (7) used for testing purposes are summarized in Table 14. The compositions of the materials (7) are based on the compositions of materials (1) to (4), except that very small amounts of Hf and Nd are added to the respective materials. Specifically, material Nos. 71 and 72 were obtained by adding Nd and Hf to material Nos. 1 and 2, respectively. Similarly, material Nos. 73, 74, 75, 76, 77 and 78 were obtained by adding Nd and Hf to material Nos. 22, 23, 34, 35, 41 and 42, respectively. Material Nos. 79 and 80, which are materials used to examine the influence of the Ni content, were obtained by increasing the content of Ni in material Nos. 22 and 41, respectively. However, as described in Examples 2 to 6, the contents of various components in the materials (7) are not exactly the same as those in the corresponding materials (1) to (4) because they may vary with the melting process. All test materials were prepared by melting the components in a 50 kg vacuum high-frequency furnace and pouring the resulting melt into a sand mold. Prior to use for various testing purposes, these test materials were subjected to a hardening treatment under conditions which simulated the central part of an air-quenched steam turbine casing having a thickness of 400 mm. Then, they were tempered at their respective tempering temperatures which had been determined so as to give a 0.2% yield strength of about 63-68 kgf/mm 2 . In Table 15, the mechanical properties and creep rupture test results (i.e., creep rupture times measured under the test conditions of 650°C x 13 kgf/mm 2 ) of the materials (7) tested in Example 7 are shown in comparison with those of the corresponding materials (1) to (4) tested in Examples 1 to 4. The materials (7) do not differ appreciably in room-temperature tensile properties from the corresponding materials (1) to (4). Moreover, the materials (7) show a slight reduction in impact value as a result of the addition of very small amounts of Nd and Hf, but this reduction is unworthy of serious consideration as is the case with the materials (5) and (6). On the other hand, the materials (7) show an increase in creep rupture time over the corresponding materials (1) to (4). The combined addition of Nd and Hf causes a slight reduction in toughness, but this reduction is unworthy of serious consideration. Rather, it can be seen that the combined addition of Nd and Hf brings about a marked improvement in creep rupture strength. When the microstructure of the inventive materials (7) was observed under an optical microscope, no formation of δ-ferrite was noticed as was the case with the inventive materials (1) to (6) tested in Examples 1 to 6. Example 8 Example 8 is specifically described below. The previously defined index A was calculated with respect to each of the above-described materials (1) to (7) and the comparative materials, and the results thus obtained are summarized in Tables 16 to 19 (Samples 31 to 35 and 55 and 56 are according to the present invention). It is evident from these tables that the index A was 8% or less for all of the materials (1) to (7). In contrast, the index A is greater than for some comparative materials (i.e., material Nos. 6, 7, 11 and 16). It can be seen by reference to Table 3 that the formation of δ-ferrite was observed in these comparative materials.

Claims: Use of a heat-resisting steel composition in the cast, hardened and tempered condition for structural materials in castings of steam turbines, the steel containing, on a weight percentage basis: 0.07 to 0.15% carbon, 0.05 to 0.30% silicon, 0.1 to 1% manganese, 8 to 10% chromium, 0.01 to 0.2% nickel, 0.1 to 0.3% vanadium, a total of 0.01 to 0.2% niobium and tantalum, 0.1 to 0.7% molybdenum, 1 to 2.5% tungsten, 0.1 to 5% cobalt, 0.001 to 0.03% nitrogen and 0.002 to 0.01% boron, optionally 0.001 to 0.2% neodymium; the balance being iron and incidental impurities, wherein an index A (%) defined by the following equation on a weight percentage basis is 8% or less: Index A (%) = (Cr content) (%) + 6(Si content) (%) + 4(Mo content) (%) + 3(W content) (%) + 11(V content) (%) + 5(Nb content) (%) - 40(C content) (%) - 2(Mn content) (%) -4(Ni content) (%) -2 (Co content) (%) -30(N content) (%)

Inventors: FUJITA AKITSUGU, KAMADA MASATOMO, FUJITA, AKITSUGU, KAMADA, MASATOMO, Fujita, Akitsugu Nagasaki Res. &amp; Developm. Center, Kamada, Masatomo, Nagasaki Res. &amp; Developm. Center
Applicants: MITSUBISHI HEAVY IND LTD, MITSUBISHI HEAVY INDUSTRIES, LTD.
Application year: 1998
Main classification: C22C38
IPC codes: C21D1, C21D6, C22C38, C22C37