Improved ink compositions for thermal ink jet printing

Abstract: Disclosed is an ink composition which comprises water, a dye selected from the group consisting of Direct Blue 199, Direct Yellow 132, Acid Yellow 17, Reactive Red 180, Acid Red 52, and mixtures thereof, and a material of the formula [(F 3 C(F 2 C) n CH=CHCH 2 OCH(OH)(CH 2 ) 2 NCH 2 COO - ][X + ], wherein X is a cation and n is an integer of from about 3 to about 20, wherein the ink is substantially free of imidazole. Also disclosed are ink jet printing processes employing the aforementioned ink.

Description: The present invention is directed to ink compositions and to processes for the preparation and use thereof. More specifically, the present invention is directed to compositions suitable for use in ink jet printing processes. U.S. Patent 5,019,166 discloses a thermal ink jet printing composition comprising a dye, a liquid medium, and a surfactant selected from the group consisting of polyoxyalkylated ethers, anionic bitail fluorothio alkyls, alkyl aryl sulfonates, alkyl amine quaternary salts, and mixtures thereof. Also disclosed is a process for generating images which comprises causing the ink compositions disclosed herein to be ejected from a thermal ink jet printer in imagewise fashion onto a substrate. U.S. Patent 5,401,303 discloses a process wherein the halo effect seen at the interface between a first ink, exhibiting sharp edge acuity, and a second ink, having low surface energy, is addressed by adding certain fluorocarbon compounds to the first ink. Edge acuity of the first ink is maintained. While known compositions and processes are suitable for their intended purposes, a need remains for ink compositions with improved characteristics. In addition, a need remains for ink compositions which exhibit reduced or no intercolor bleed when printed adjacent to other inks of different colors. Further, a need remains for ink compositions which exhibit good shelf stability. Additionally, a need remains for ink compositions having improved colorimetry. There is also a need for ink compositions which exhibit reduced intercolor bleed in combination with improved shelf stability and improved colorimetry. In addition, there is a need for ink compositions with good lightfastness characteristics. Further, there is a need for ink compositions which exhibit good waterfastness characteristics. Additionally, there is a need for ink compositions which enable the generation of prints with excellent optical density. A need also remains for ink compositions having dye colorants which exhibit reduced intercolor bleed with Ink compositions having pigment colorants, whether or not the pigmented ink compositions contain a fluorinated material. In addition, a need remains for ink compositions with improved color garnut. Further, a need remains for ink compositions which exhibit reduced showthrough when printed on paper substrates. Additionally, a need remains for ink compositions suitable for printing onto a wide variety of substrates. There is also a need for ink compositions which are relatively benign with respect to any tendency to cause degradation of common thermal ink jet printhead materials. In addition, there is a need for ink compositions which enable the generation of prints on various papers with reduced or eliminated curling of the paper. It is an object of the present invention to provide ink compositions with the above noted advantages. These and other objects of the present invention (or specific embodiments thereof) can be achieved by providing an ink composition which comprises water, a dye selected from the group consisting of Direct Blue 199, Direct Yellow 132, Acid Yellow 17, Reactive Red 180, Acid Red 52, and mixtures thereof, and a material of the formula [(F 3 C(F 2 C) n CH=CHCH 2 OCH(OH)(CH 2 ) 2 NCH 2 COO - ][X + ], wherein X is a cation and n is an integer of from 3 to 20, wherein the ink is substantially free of imidazole. DETAILED DESCRIPTION OF THE INVENTION Inks of the present invention contain an aqueous liquid vehicle. The liquid vehicle can consist solely of water, or it can comprise a mixture of water and a water soluble or water miscible organic component, such as ethylene glycol, propylene glycol, diethylene glycols, glycerine, dipropylene glycols, polyethylene glycols, polypropylene glycols, tripropylene glycol monomethyl ether, amides, ethers, urea, substituted ureas, ethers, carboxylic acids and their salts, esters, alcohols, organosulfides, organosulfoxides, sulfones (such as sulfolane), alcohol derivatives, carbitol, butyl carbitol, cellusolve, ether derivatives, amino alcohols, ketones, N-methylpyrrolidinone, 2-pyrrolidinone, cyclohexylpyrrolidone, hydroxyethers, amides, sulfoxides, lactones, polyelectrolytes, methyl sulfonylethanol, imidazole, and other water soluble or water miscible materials, as well as mixtures thereof. When mixtures of water and water soluble or miscible organic liquids are selected as the liquid vehicle, the water to organic ratio typically ranges from 100:0 to 30:70, and preferably from 97:3 to 40:60. The non-water component of the liquid vehicle generally serves as a humectant which has a boiling point higher than that of water (100°C). In the ink compositions of the present invention, the liquid vehicle is typically present in an amount of from 60 to 95 percent by weight of the ink, and preferably from 70 to 90 percent by weight of the ink, although the amount can be outside these ranges. Also contained in the ink is a material of the formula wherein X + is a cation and n is an integer of from 3 to 20, preferably from 4 to 15, and more preferably from 5 to 11. Examples of suitable cations include (HO-CH 2 CH 2 ) 2 NH 2 + , (HO-CH 2 CH 2 ) 3 NH + , an imidazolium cation such as imidazolium, N-methyl imidazolium, or N-butyl imidazolium, tris(hydroxymethyl)aminomethane hydrochloride, tris(hydroxymethyl)aminomethane hydrocitrate, protonated 1,4-diazabicyclo(2.2.2)octane, and the like. Materials of this formula are available from, for example, Ciba-Geigy, Ardsley, New York (Greensboro, NC) as LODYNE P-502, containing a mixture of compounds wherein n has varying values and has an average value of about 9. The material of this formula is present in the ink in any effective or desired amount; typically, the amount ranges from 0.1 to 10 percent by weight of the ink, preferably from 0.25 to 6 percent by weight of the ink, more preferably from 0.5 to 5 percent by weight of the ink, and even more preferably from 1 to 4 percent by weight of the ink, although the amount can be outside these ranges. Also contained in the ink composition of the present invention is a dye. The dye is selected from the group consisting of Direct Blue 199 (commercially available as, for example. PROJET CYAN 1 from Zeneca Colors, Dighton, Massachusetts), Direct Yellow 132 (commercially available as, for example, PROJET YELLOW 1G from Zeneca Colors, Dighton, Massachusetts), Acid Yellow 17 (commercially available from, for example Tricon Colors, Elmwood Park, New Jersey), Reactive Red 180 (commercially available as, for example, PROJET MAGENTA 1T from Zeneca Colors, Dighton, Massachusetts), Acid Red 52 (commercially available from, for example Tricon Colors, Elmwood Park, New Jersey), and mixtures thereof. The dye is present in the ink composition in any effective amount, typically from 0.5 to 15 percent by weight of the ink, preferably from 0.5 to 8 percent by weight of the ink more preferably from to 10 percent by weight of the ink, and even more preferably from 1 to 6 percent by weight of the ink although the amount can be outside of these ranges. Inks of the present invention containing the fluorinated material and one or more of the above dye compositions exhibit excellent shelf stability as a result of the compatibility of these dyes with the fluorinated material. In addition, the inks exhibit good compatibility with printhead hardware, improved waterfastness and lightfastness, excellent optical density, and good color quality. The ink compositions of the present invention contain substantially no imidazole. Imidazole can be used in ink compositions containing fluorinated materials such as those contained in the inks of the present invention to enhance the shelf stability of the ink. Since imidazole can cause degradation of many materials commonly used to fabricate thermal ink jet printheads, however, inks of the present invention are particularly benign with respect to ink jet printhead materials. The ink compositions are generally of a viscosity suitable for use in thermal ink jet printing processes. At room temperature (i.e., about 25°C), typically, the ink viscosity is no more than 5 centipoise, and preferably is from 10 -3 to 3.5 × 10 -3 Pa·s (1 to 3.5 centipoise) although the viscosity can be outside this range. Ink compositions of the present invention can be of any suitable or desired pH. For some embodiments, such as thermal ink jet printing processes, typical pH values are from 8 to 9.5, preferably from 8.0 to 9.0, and more preferably from 8.5 to 9.0, although the pH can be outside of these ranges. The present invention is also directed to a process which entails incorporating an ink composition of the present invention into an ink Jet printing apparatus and causing droplets of the ink composition to be ejected in an imagewise pattern onto a substrate. In a particularly preferred embodiment, the printing apparatus employs a thermal ink jet process wherein the ink in the nozzles is selectively heated in an imagewise pattern, thereby causing droplets of the ink to be ejected in imagewise pattern. Any suitable substrate can be employed, including plain papers such as Xerox® 4024 papers, ruled notebook paper, bond paper, silica coated papers such as Sharp Company silica coated paper, JuJo paper, and the like, transparency materials, fabrics, textile products, plastics, polymeric films, inorganic substrates such as metals and wood, and the like. In a preferred embodiment, the process entails printing onto a porous or ink absorbent substrate, such as plain paper. Specific embodiments of the invention will now be described in detail. All parts and percentages are by weight unless otherwise indicated. EXAMPLE I To 59.4 grams of distilled water was added 19.8 grams of 1,4-diazabicyclo(2.2.2)octane (obtained from Aldrich Chemical Co., Milwaukee, WI, D2,780-2), 7.8 grams of citric acid (obtained from Aldrich Chemical Co., C8,315-5), 13.2 grams of hexamethonium bromide hydrate (obtained from Aldrich Chemical Co., 21,967-3), and 199.8 grams of LODYNE P-502 (containing 14.9 percent by weight of the fluorinated material, obtained from Ciba-Geigy, Ardsley, New York (Greensboro, NC)). The mixture was stirred for 15 minutes, after which time it exhibited a viscosity of 6.10 × 10 -3 Pa·s (6.10 centipoise) at 25°C. Thereafter, a 25 gram portion of the mixture was placed in a 30 gram vial. The vial was placed into a 550 SONIC DISMEMBRATOR (obtained from Fisher Scientific Co.) tuned at 20 kiloHertz and the LODYNE P-502 was subjected to ultrasonification for a period of 60 minutes at an amplitude setting of 5, with the power turned on and off every 30 seconds. The resulting colorless mixture had a viscosity of 3.57 × 10 -3 Pa·s (3.57 centipoise) at 25°C, a pH of 9.16 at 25°C. a conductivity of 7.62 mS (7.62 millimhos), and a surface tension of 2.87 Pa (28.9 dynes per centimeter). EXAMPLE II An ink composition was prepared as follows. To 46.4 grams of deionized water were added 0.167 gram of DOWICIL 150/200 biocide (obtained from Dow Chemical Co.. Midland, Ml), 0.0833 gram of polyethylene oxide (bisphenol-A derivative, of the formula molecular weight 18,500, obtained from Polysciences Corp.), 20.00 grams of tripropyleneglycol monomethylether (DOWANOL TPM, obtained from Dow Chemical Co.), 41.67 grams of PROJET MAGENTA 1T dye solution (dye solution contained 10 percent by weight dye solids, obtained from Zeneca Colors, Dighton, Massachusetts), 8.33 grams of Acid Red 52 dye solution (dye solution contained 10 percent by weight dye solids, obtained from Tricon Colors, Elmwood Park, New Jersey), and an additional 9.90 grams of deionized water. The mixture thus prepared was then sonified by the process described in Example I. To the mixture were then added 3.30 grams of 1,4-diazabicyclo(2.2.2)octane (obtained from Aldrich Chemical Co., D2,780-2, Milwaukee, WI). 1.3 grams of citric acid (obtained from Aldrich Chemical Co.), 2.2 grams of hexamethonium bromide hydrate (obtained from Aldrich Chemical Co., 21,967-3), and 33.3 grams of LODYNE P-502 (solution containing 14.9 percent by weight fluorocarbon material, obtained from Ciba-Geigy, Ardsley, New York (Greensboro, NC)). The resulting magenta ink composition was then filtered through a 1.2 micron 47 mm Gelman filter at 10 pounds per square inch over a period of 55 seconds. The ink composition thus prepared exhibited a viscosity of 4.34 × 10 -3 Pa·s (4.34 centipoise) at 25°C, a pH of 8.56 at 25°C, a conductivity of 8.46 mS (8.46 millimhos), and a surface tension of 2.46 Pa (24.6 dynes per centimeter.) The ink composition thus prepared was then Incorporated into a Hewlett-Packard 1600C thermal ink jet printer and printed onto Xerox® 4024 DP paper and Xerox® Image Series Elite paper. The prints thus formed exhibited low intercolor bleed with a MFLEN value of 5. EXAMPLE III An ink composition was prepared as described in Example II except that the initial amount of deionized water was 38.1 grams (and not 46.4 grams) and that 58.33 grams of PROJET CYAN 1 dye solution (dye solution contained 10 percent by weight dye solids, obtained from Zeneca Colors, Dighton, Massachusetts) was substituted for the PROJET MAGENTA 1T and Acid Red 52 dyes. The resulting cyan ink composition was then filtered through a 1.2 micron 47 mm Gelman filter at 10 pounds per square inch over a period of 65 seconds. The ink composition thus prepared exhibited a viscosity of 3.72 × 10 -3 Pa·s (3.72 centipoise) at 25°C, a pH of 8.79 at 25°C, a conductivity of 7.07 mS (7.07 millimhos) and a surface tension of 1.88 Pa (18.8 dynes per centimeter.) The ink composition thus prepared was then incorporated into a Hewlett-Packard 1600C thermal ink jet printer and printed onto Xerox® 4024 DP paper and Xerox® Image Series Elite paper. The prints thus formed exhibited low intercolor bleed with a MFLEN value of 5. EXAMPLE IV An ink composition was prepared as described in Example II except that the initial amount of deionized water was 38.1 grams (and not 46.4 grams) and that 33.3 grams of PROJET YELLOW 1G dye solution (dye solution contained 7.5 percent by weight dye solids, obtained from Zeneca Colors, Dighton, Massachusetts) and 25.0 grams of Acid Yellow 17 dye (dye solution contained 10 percent by weight dye solids, obtained from Tricon Colors, Elmwood Park, New Jersey) were substituted for the PROJET MAGENTA 1T and Acid Red 52 dyes. The resulting cyan ink composition was then filtered through a 1.2 micron 47 mm Gelman filter at 10 pounds per square inch over a period of 50 seconds. The ink composition thus prepared exhibited a viscosity of 4.46 × 10 -3 Pa·s (4.46 centipoise) at 25°C, a pH of 8.62 at 25°C, a conductivity of 7.81 mS (7.81 millimhos) and a surface tension of 2 Pa (20 dynes per centimeter). The ink composition thus prepared was then incorporated into a Hewlett-Packard 1600C thermal ink jet printer and printed onto Xerox® 4024 DP paper and Xerox® Image Series Elite paper. The prints thus formed exhibited low intercolor bleed with a MFLEN value of 5. EXAMPLE V An ink composition was prepared by admixing the following ingredients: The ink composition thus prepared exhibited a viscosity of 2.97 × 10 -3 Pa·s (2.97 centipoise) at 25°C, a pH of 8.99 at 25.2°C, a surface tension of 2.38 Pa (23.8 dynes per centimeter), and a conductivity of 2.82 mS (2.82 millimhos). The ink composition thus prepared was then incorporated into a Hewlett-Packard 1600C thermal ink jet printer and printed onto Xerox® 4024 DP paper and Xerox® Image Series Elite paper. The prints thus formed exhibited low intercolor bleed with a MFLEN value of 5. EXAMPLE VI An ink composition was prepared by admixing the following ingredients: Ingredient Supplier Amount (grams) deionized water - - - 44.9 betaine FinnSugar Bioproducts 15 DOWICIL 150/200 Dow Chemical Co. 0.1 butyl carbitol Van Waters & Rogers 2 Reactive Red 180 dye Hoechst 3 Acid Red 52 dye Tricon Colors 5 deionized water - - - 5.94 sonicate 1 hour with stirring; setting=5; allowed to heat to 45°C 1.4-diazabicyclo(2. 2.2) octane Aldrich Chemical Co. 1.98 citric acid Aldrich Chemical Co. 0.78 hexamethonium bromide hydrate Aldrich Chemical Co. 1.32 LODYNE P-502 Ciba-Geigy 19.98 The resulting ink composition was then filtered through a 1.2 micron 47 mm Gelman filter at 7030.70 kg/m 2 (10 pounds per square inch.) The ink composition thus prepared exhibited a viscosity of 2.49 × 10 -3 Pa·s (2.49 centipoise) at 25°C, a pH of 9.02 at 25°C, and a surface tension of 2.71 Pa (27.1 dynes per centimeter). The ink composition thus prepared was then incorporated into a Hewlett-Packard 1600C thermal ink jet printer and printed onto Xerox® 4024 DP paper and Xerox® Image Series Elite paper. The prints thus formed exhibited low intercolor bleed with a MFLEN value of 5. EXAMPLE VII An ink composition was prepared by admixing the' following ingredients: The resulting ink composition was then filtered through a 1.2 micron 47 mm Gelman filter at 7030.70 kg/m 2 (10 pounds per square inch). The ink composition thus prepared exhibited a viscosity of 2.15 × 10 -3 Pa·s (2.15 centipoise) at 25°C, a pH of 8.80 at 25°C, and a surface tension of 2.68 Pa (26.8 dynes per centimeter). The ink composition thus prepared was then incorporated into a Hewlett-Packard 1600C thermal ink jet printer and printed onto Xerox® 4024 DP paper and Xerox® Image Series Elite paper. The prints thus formed exhibited low intercolor bleed with a MFLEN value of 5.

Claims: An ink composition which comprises water, a dye selected from the group consisting of Direct Blue 199, Direct Yellow 132, Acid Yellow 17, Reactive Red 180, Acid Red 52, and mixtures thereof, and a material of the formula [(F 3 C(F 2 C) n CH=CHCH 2 OCH(OH)(CH 2 ) 2 NCH 2 COO - ][X + ], wherein X is a cation and n is an integer of from 3 to 20, wherein the ink is substantially free of imidazole. An ink composition according to claim 1 wherein the material of the formula [(F 3 C(F 2 C) n CH=CHCH 2 OCH(OH)CH 2 ) 2 NCH 2 COO - ][X + ] is present in an amount of from 0.1 to 10 percent by weight of the ink. An ink composition according to claim 1 wherein X is selected from the group consisting of (HO-CH 2 CH 2 ) 2 NH 2 + , (HO-CH 2 CH 2 ) 3 NH + , tris(hydroxymethyl)aminomethane hydrochloride, tris(hydroxymethyl)aminomethane hydrocitrate, protonated 1,4-diazabicyclo(2.2.2)octane, and mixtures thereof. An ink composition according to claim 1 wherein the dye is present in an amount of from 0.5 to 15 percent by weight of the ink. An ink composition according to claim 1 wherein the dye is present in an amount of from 1 to 6 percent by weight of the ink. An ink composition according to claim 1 wherein the dye is a mixture of Reactive Red 180 and Acid Red 52. An ink composition according to claim 1 wherein the dye is Direct Blue 199. An ink composition according to claim 1 wherein the dye is a mixture of Direct Yellow 132 and Acid Yellow 17. An ink composition according to claim 1 further containing tripropylene glycol monomethyl ether. A process which comprises (i) incorporating into an ink jet printing apparatus an ink composition comprising water, a dye selected from the group consisting of Direct Blue 199, Direct Yellow 132, Acid Yellow 17, Reactive Red 180, Acid Red 52, and mixtures thereof, and a material of the formula [(F 3 C(F 2 C) n CH=CHCH 2 OCH(OH)(CH 2 ) 2 NCH 2 COO - ][X + ], wherein X is a cation and n is an integer of from 3 to 20, wherein the ink is substantially free of imidazole; and (ii) causing droplets of the ink composition to be ejected in an imagewise pattern onto a substrate. A process according to claim 10 wherein the printing apparatus employs a thermal ink jet process wherein the ink in the nozzles is selectively heated in an imagewise pattern, thereby causing droplets of the ink to be ejected in imagewise pattern.

Inventors: COLT RICHARD L, GUNDLACH KURT B, SANCHEZ LUIS A, COLT, RICHARD L., GUNDLACH, KURT B., SANCHEZ, LUIS A.
Applicants: XEROX CORP, XEROX CORPORATION
Application year: 1998
Main classification: C09D11
IPC codes: C09D11, B41M5