SILVER HALIDE MATERIAL FOR OPTICAL MEMORY DEVICES WITH LUMINESCENT READING AND METHODS FOR THE TREATMENT THEREOF

Abstract: This invention concerns a luminescent optical memory material and method of forming this material, including the encoding of information by a photographic process. The method involves the use of silver halide crystals of a defined size range, with the optional use of sensitizers, emulsion stabilizers, and other agents followed by the absorption of luminescent dyes on the developed silver particles to form a luminescent optical memory system. The method involves synthesis of a photographic emulsion with silver halide crystals of a defined size range, applying photographic emulsion to a substrate, exposing to light photochemical treatment and a process of transformation of the silver particles formed in the places exposed by light into luminescent particles. The method involves obtaining a multi-layer luminescent material for three-dimensional optical memory devices.

Description: SILVER HALIDE MATERIAL FOR OPTICAL MEMORY DEVICES WITH LUMINESCENT READING AND METHODS FOR THE TREATMENT THEREOF This application is a continuation in part of U.S. application 60/038,918 filed February 24, 1997 and herein incorporates by reference that application for all purposes. FIELD OF THE INVENTION The present invention is directed to the field of materials for optical recording, storing and reading of information, including systems for 3-D optical memory based on luminescent compounds which can be used with CD-ROM systems. The next generation of computer memories will be connected with memory systems using super dense optical memory materials to take advantage of these materials memory storage density and access speed. The optical disks of CD-ROM's are examples of optical memory systems. The disadvantages of current CD-ROM's are an insufficient density of memory, insufficient amount of memory and unfavorable ratio of signal-to-noise for the next generation of computers. Presently, some new materials, including the materials of the invention with luminescent properties for the reading of information, have been suggested for the improved optical memory systems that are under development. Such materials have an increased recording density, a high signal-to-noise ratio, and increased stability during storage and utilization. BACKGROUND OF THE INVENTION There are different prior art systems for optical recording based on the forming of fluorescent compounds from non-fluorescent precursors, including the UV-light exposed compounds of bis-diarylchloromethyl-1, 3,4-oxadiazoles which are disclosed in U.S. Patent No. 3,869,363. Moreover, many other systems are described in Zweig "Photochemical Generation of Stable Fluorescent Compounds" in Pure and Applied Chemistry, Vol. 33, 389- 410 (1973) herein incorporated by reference. The main disadvantage of systems using these compounds is the requirement to use lasers with wavelengths shorter than 500 nm for the reading of stored information in the system. Thus, these systems exclude the possible use of modern diode lasers with wavelengths over 600 nm for reading the information in the storage device. Photochromic lactams of Rhodamine B and peri-phenoxy derivatives of polycyclic p- quinones are suggested for use in these memory devices in which the luminophores are photochemically generated (U.S. Provisional Patent Application 60/03258 filed on December 10, 1996 and U.S. Provisional Patent Application 60/033709 filed on December 20, 1996, serial numbers not yet assigned, herein incorporated by reference). These compounds can be used in optical memory devices employing modern diode lasers with the wavelengths over 600 nm for reading the stored information. However, photochromic systems based on the generation of luminescent products have the common disadvantage of the destruction of the photoinduced luminescent product during the reading process. Moreover, these systems have low light sensitivities which then requires high energy densities of irradiation during the recording process which can lead to destruction of the memory material. SUMMARY OF THE INVENTION This invention provides for a super dense optical memory material for information storage and use with computers. The invention includes the formation of silver halide crystals of a defined size and the optional treatment of these silver halide crystals with sensitizers and/or spectral sensitizers. The silver halide crystals of the invention are then exposed to light, developed and fixed. The silver grains can then be treated with luminescent dyes to form the luminescent particles of the invention. Alternatively, the silver particles or the surface of the silver particles can be oxidized and luminescent dyes sorbed onto the oxidized surface or the oxidized particles can be treated to form insoluble salts which are then treated with luminescent dyes to form the luminescent particles of the invention. In addition, polyvalent cations can be sorbed onto the surface of the silver particles, the oxidized silver particles, the silver salts or the insoluble salts to form lumincent metal complex compounds. In addition, mercapto- or benzotriazoyl compounds can be used to promote the adsorption of the luminescent dyes onto the silver or other insoluble particles. The optical memory material of the invention can be formed either into a single layer of polymer with silver halide crystals or a three dimensional memory material can be formed by stacking layers of silver halide material dispersed in a polymer with layers of silver halide free material. Alternatively, relatively thick layers of silver halide material can be used to form a three dimensional material. The invention includes a two laser system for the two photon writing of information within a three dimensional optical matrix. BRIEF DESCRIPTION OF THE DRAWING FIG. 1 shows a schematic of a two laser system for the writing of information into a three dimensional optical memory. DETAILED DESCRIPTION OF THE INVENTION In the known photographic process of image registration, by light exposure of the silver halide material containing microcrystals of AgHal in the hydrophilic polymer, followed by further development of the latent photographic image in a water solution of the reducer. The process includes image fixation by dissolving non-irradiated silver halide therein leaving the exposed silver grains. (T.H. James, "The theory of the photographic process", 4th Ed. MacMillan Publish Co., N.Y., London, 1977 herein incorporated by reference). Examples of the light sensitive compounds of the invention include microcrystals of AgCl, AgCl(Br), AgCl(Br,I), AgBr and AgBr(I). The dimensions of the microcrystals of AgHal of the invention are in the range of 0.02 to 5μm. The microcrystals of the invention can be treated with gold and sulfur as well as reduction sensitization processes to increase their light sensitivity. The spectral sensitization of the silver halide microcrystals of the invention by polymethine dyes is used in all ranges of visible and near infra-red light to increase the sensitivity of silver halide. The field of spectral sensitivity encompasses the range from about 300 to 1500 nm. Gelatine or gelatine modified by polymers is used as a hydrophilic polymer in the invention. The gelatine modified with hydrophilic polymers can include gelatine modified with polyvinyl alcohol, polyvinylpyrrolidone, polyvinyl sulphate, carboxymethylcellulose, cellulose acetophthalate, phthaloylgelatine or graft polymers of gelatine with polymethoxydiethyleneglycol acrylate or with polydiacetoneacrylamide or with poly-N,N'- methylenediacrylamide and can be used as the hydrophilic polymer of the invention. The photographic layer is coated over the base, gelatinated, hardened to provide a gelatine layer with the necessary physical-mechanical properties and dried. The thickness of the dried photographic layer of the invention can be vary from 1 to 100 microns. The light sensitivity of photo materials of the invention is from about 10 "2 to 10 4 erg/cm 2 (from 10 "3 to 10 3 of ISO units), and is dependant on the crystal size. The photo- materials have resolution values of aboutlO 2 to greater than 10 4 lines/mm. The advantages of the silver halide materials of the invention are: high light sensitivity, high resolution, time stability and mainly the threshold character of the response to light in the form of a "yes - no" response indicating sufficient or insufficient exposure to light . Each of the microcrystals of AgHal need to obtain at least four quanta of light to react. Thus, the quantum sensitivity of the microcrystal has a value of n≥ 4. The threshold character of photochemical sensitivity of a single AgHal microcrystal permits the recording of information by each microcrystal both at the surface and inside the emulsion layer. In other words, the threshold value of energy can influence a predetermined microcrystal in the layer. It is possible while exposing the layer to one or two laser beams with an energy at the predetermined point of the layer above the threshold value of quantum sensitivity of the microcrystal to influence a predetermined microcrystal. The main disadvantage of the classic photomaterial is the reading of the information by only the integral light absorption on a unit of the area. In other words the information is read by the difference in light absorption by the developed film. Because of the nonselective absoφtion of light in the visible and infrared ranges by silver imaging, the information cannot be read from the depth of the exposed crystal in the photographic layer, meaning that the information recorded on each microcrystal of the AgHal cannot be read. The other disadvantage of this material is that it has a poor signal-to-noise ratio during the reading process. The signal-to-noise is determined by reading the reflected light from the film therefore, the contribution to the poor signal-to-noise ratio by light scattering is significant. The present invention is directed towards optical recording materials with luminescent reading overcoming the disadvantages of the known optical recording materials and the classical silver halide photomaterials. Such materials provide increased recording density, an increased ratio of signal-to-noise and stability of information while storing and reading the material. Moreover, such materials provide the recording and reading of information by using light sources with different wavelengths, including infrared wavelengths not only in 2- dimensional, but also in 3 -dimensional space. This is achieved by using silver halide material with high resolution ability (2,400 or more lines/mm), and with higher light sensitivity and with a wider region of spectral sensitivity from 300 to 1000 nm than known optical memory materials with luminescent reading. The further treatment and Ag transformation to the image to give particles luminescing in the spectral range from 400-850 nm, provides a great increase in the reading efficiency. Moreover, a variant of the process is possible wherein the unexposed matrix is luminescent and where the matrix has been exposed to light there is no luminescence. Methods of photographic emulsion sythesis, chemical and spectral sensitization, stabilization, hardening, and chemicophotographic treatment are described in the monograph by T.H. James The Theory of the Photographic Process, 4th Edition, MacMillan Publishing Co. N.Y., London (1977) herein incorporated by reference. For information recording, the transparent fine-grain silver halide emulsions are used with the microcrystal particle size being less then 0.2 microns, preferably 0.08-0.03 microns and with the silver halides of AgCl, AgCl(Br), AgCl(Br,I), AgBr, or AgBr(I) being suitable. The photographic emulsions are obtained by the method of two flowing controlled emulsification in the hydrophilic film forming polymer. As the hydrophilic polymer, a gelatine or its polymer modification , polyvinyl alcohol and others can be used. The microcrystals of AgHal can be subjected to chemical sensitization by compounds containing labile sulfur (for example, Na 2 S 2 0 3 , thiourea), the gold compounds (such as, HAuCl 4 , AuCNS and others), and also reduction compounds such as, SnCl 2 , dioxide of thiourea and borohydrides. The photographic emulsions can be stabilized by organic stabilizers, such as 4-hydroxy-6-methyl-l,3,3a,7-tetraazaindene, l-phenyl-5- mercaptotetrazole, 2-mercapto-5-nitro-benzimadazole, the sodium or potassium salts of 2- mercapto-5-sulphobenzoxazole, 2-mercaptobenzothiazole, 2-mercaptobenzoxazole_and thiadiazole. The photographic emulsions are subjected to the spectral sensitization by polymethine dyes (cyanine dyes) in the range of visible and near- infra-red spectrum as represented by the general chemical formula (A) where in the case of the benzothiazole derivatives (X,Y=S); benzoxazole derivative (X,Y=O); benzimidazole derivative (X,Y=NR); quinoline derivative (X,Y=-CH=CH-); indolenine derivative (X,Y=C(R 2 )) and so on. For the non-symmetrical dyes X does not equal Y (X≠Y), for example, X=0, and Y=S and are independently selected. Wherein, for each derivative R 2 and R 3 are independently selected from H , CH 3 , -OCH 3 , -SCH 3 , -N(CH 3 ) , -N(Et) 2 , -N(proρyl) 2 , -N(iso-propyl) 2 , -N(butyl) 2 , -N(iso-butyl) 2 , -N(sec-butyl) 2 , -NCO(CH 2 ) k H wherein k is 1 to 5 , F, Cl, Br, I, -CN, -C0 2 H , -C0 2 (CH 2 ) j CH 3 where j is 0 to 4 , -CONH 2 , - CF 3 , SOCF 3 , S0 2 CF 3 , -C 6 H 5 , and benzyl; n is 0, 1 or 2 and m is 0 or 1 ; when n is 0 and m is 1 then R 6 is independently selected from H , CH 3 , C 2 H 5 , C 6 H 5 , -NH 2 , -NHCOCH 3 , - OCH 3 , C0 2 CH 3 ; when n is 1 and m is 1 then R 4 and R 6 are H and R 5 H, CH 3 , C 2 H 5 , NHCOCH 3 , when R 4 and Rg are linked together and R 4 and Rg are -(CH 2 ) 2 - , -(CH 2 ) 3 - , or - CH 2 C(CH 3 ) 2 CH 2 - then R 5 is H, Cl, and C 6 H 5 ; when n is 2 and m is 1 then R 4 , R 5 and R f , are H or R 4 and Rg are H and R 5 and R 5 is linked together and R 5 is -(CH 2 ) 3 - , -CH 2 C(CH 3 ) 2 CH 2 - ; and when R and R, are independently selected from alkyl then Z " is an anion and when R and R, are independently selected from -(CH 2 ) 3 S0 3 " then Z + is a cation. Additionally, the merocyanines and merocyaninocyanines and others can be used. The layers are treated with inorganic hardeners (potassium alum or chrome-potassium alum) or with the traditional organic hardeners from the class of aldehydes, derivatives of triazoles, oxiranes, vinyl sulfonyl derivatives and others. Photographic layers are subjected to development and fixation after exposure to light. Formed image consisting of particles of Ag , oxidized and converted into the colorless or weakly colored insoluble salts with solubility products less then 10 "8 , preferably less than 10 "10 moles/liter at 25 ° C. As insoluble salts, AgSCN, AgCN, Agl, Ag 2 Cr 2 0 7 , Ag 2 W0 4 , Ag 4 [Fe(CN 6 )] are used. For this piupose the inorganic soluble salts comprising anions of SCN " , CN " , I " , Cr 2 O , WO 2" 4 , [Fe(CN 6 )] 4" and others are added to a bleaching vessel containing an oxidizer such as, K 3 [Fe(CN 6 )], salts of Fe 3+ , Cu 2+ , quinones and others. The silver oxidation can be conducted with the present of organic acids or their salts, for example, oxalates or citrates of the alkaline metals , and the benzotriazoles l-mercapto-5-phenyl triazole, 2- mercapto-5-nitrobenzamidazole, 2-mercapto-5-sulphobenzoxazole as the respective sodium or potassium salts, to obtain insoluble silver salts. The silver of an image can be transformed in a subsequent process to an insoluble salt that does not contain silver ions for example Zn 2 [Fe(CN 6 )], Cd 2 [Fe(CN 6 )], ZnS, CdS, BaSO 4 and others. The three basic methods can be used for the obtaining luminescent particles in the layer: 1. Adsoφtion of the luminescent dyes on the insoluble silver or other cationic salts. 2. Preliminary adsoφtion of polyvalent cations such as, Zn 2+ , Cd 2+ , Sr 2+ , Ni 2+ , Co 2+ , Fe 3+ , Cr 3+ , In 3+ , Bi 3+ , La 3+ , Gd 3+ , V 4+ , Cl 4+ , Th 4+ , and others on the silver salts or other insoluble salts, with the further adsoφtion of the dyes leading to the formation of luminescent metal-complex compounds. 3. Adsoφtion of luminescent dyes onto the silver salts or other insoluble salts, comprising a mercapto- or benzotriazolyl groups promoting the adsoφtion of the dye onto the silver or other insoluble salts. Alternatively, preliminary adsoφtion of polyvalent anions such as [Fe(CN) 6 ] "4 , W0 4 "2 , Mo0 4 "2 and others, followed by treatment with mercapto- compounds or benzotriazole to promote the adsoφtion of the luminescent dyes with some dyes may be preferred. Alternatively, optical memory devices wherein the matrix is luminescent and the silver particles are doped with multiply charged cations such as Cu +2 , Mn +2 and others can also be prepared. The silver particles are doped by the adsoφtion of the multiply charged cations onto the silver particles. The doped silver particle then suppress the luminescence of the luminescent dyes in the matrix adjacent to the particle. For light sensitive mediums, vacuum sublimated silver halide can be used, which is then subjected to the same treatment as the emulsion layers of AgHal. The silver halide emulsion can also be applied in layers to obtain a multi-layered material. The luminescent compounds can be selected from the following organic dyes described in Krasovitsky, B.M.; Bolotin, B.M. Organic Luminophores Moscow: Chimia 1984, 336p (Russian); . Venkataraman, 77ze Chemistry of Synthetic Dyes New York: Academic Press Inc. 1952, Vol. 2 both references herein incoφorated by refernce. 1. The xanthene dyes of the eoscin type including eosins, fluoresceins, erythrosins, and dichlorofluorescein of general structure I. wherein R is independently selected from H, Cl, Br, I, N0 2 , alkyl and others; R, is H, Na, K, Alkyl; R 2 is independently selected from H, Cl. NH 2 , Br, I, isocyanate, isothiocyanate, alkyl anf others; and R 3 is independently selected from H, Cl, Br, I, N0 2 , NH 2 , alkyl and others. 2. The xanthene dyes of the rhodamine type including the rhodamines B, 3B, C, G, 6G, 101, 123 and others having the general structure II. wherein R is H, CH 3 , C 2 H 5 , CH 2 COOH, C 2 H 4 OH and others; R, is H, Na, K, CH 3 , C 2 H 5 , Ar, Alkyl and others; R 2 is independently selected from H, Cl, Br, I,N0 2 , alkyl and others, R 3 is independently selected from H, Cl, Br, I, N0 2 , isothiocyanate, isocyanate, amines and others and X is an anion selected from Cl " , Br " , I " , C10 4 " and others. 3. The acridine dyes, including aurazine, trypaflovine, ethoxydiaminoacridine lactate and others of general structure III. wherein R is H, CH 3 , C 2 H 5 , and others; R, is H, C 6 H 5 , CO 2 H and others; R 2 is H, CH 2 CH 2 OH, alkyl and others; R 3 is independently selected from H, CH 3 , alkyl and others; and X is a anion of F, Cl, Br, I, HCOO " , CH 3 CHOHCOO\ C10 4 " and others. 4. The oxazine dyes, including the oxazines 1, 4, 9, 17, 118, nile blue, capry blue A and others having the general structure IVa and IVb: where R is selected from H, CH 3 , and others; R, is independently selected from H, CH 3 , CH 3 CH 2 alkyl and others and X is an anion selected from F, Cl, Br, I, C10 4 " , sulfates, phosphates and others. 5. The azine dyes, including magdala red, lactoflavine. of general structure V: wherein R is phenyl, naphthyl; R, is H, alkyl, C 6 H 5 , and others ; R 2 is H, alkyl, benzyl, O- benzyl; R 3 is H, SO 3 H and others; and X is an anion. 6. The indigo dyes, in the form of indigozoles, of general structure VI : wherein, Y is NH, S and R is independently selected from H, Cl, Br, O-alkyl, N0 2 , sulfate, alkyl and others. 7. The polycyclic vat dyes, including aminoanthropyrimidines, anthropyridones, oxa-and tiadiazoloaminoantroquinones, dyes from the group of benzanthrones in the form of sulfuric esters of leuco compounds of general structure VII - XI: where R is H, NH-C 6 H 5 , R, is H, NHCOAr O where R is H, alkyl, or aromatic where R is H, C 6 H„, C 2 H 5 , C 2 H 4 OH. where R is H, Ar, -S0 2 Ar and others. where R is independently selected from H, Cl, Br, OH, the structure: O' and others. 8. The dyes which are forming both the luminescent and non- luminescent complexes with polyvalent metal ions, selected from the hydroxyantraquinone derivatives: calcein, calcein blue, xanthocomplexan, methylcalcein, methylcalcein blue as shown in general structures XII -XVII. Where RisCH 3 , CH 2 COOH 9. The cyanine dyes of general structure XVIII. (XVIII) wherein n is 1,2,3 ; R is H, S0 3 H and others; Ri is alkyl, (CH 2 ) m S0 3 H and others m is 3,4 or 5 and X " is a anion. Multi-layer material for use in a three-dimensional memory can be prepared by stacking single silver halide layers on transparent, silver halide free layers with a thickness of 20 - 30 microns. Preferably, the three dimensional, multi-layered material can be prepared by the following extrusion process. The process comprises simultaneously extruding from a multi-slit filler relatively thick layers of at least one of the hydrophilic polymers previously discussed without silver halide between relatively thin layers of a hydrophilic polymer with silver halide to obtain a multi-layer structure of alternating layers of silver less and silver halide containing material. The number of layers can be varied from two to twenty or more. The thickness of the layers of hydrophilic polymer without silver halide can be varied from about 15 to about 30 microns, preferably about 20 to about 30 microns and the thickness of the layer with silver halide can range from about 0.75 to about 5 microns, preferably about 1.0 to about 1.5 microns. The silver halide material of the different layers can be spectrally sensitized to different parts of the visible and infra-red spectrum and the recording of information can then occur through the use of a mask with selective light filters. In an analogous manner, the non-silver halide gelatine layers can contain dyes that are matched or mismatched with the spectrally sensitized silver halide so as to allow the writing of information in the silver halide layers by the use of diode or other lasers. A method of producing a multi-layered optical memory material consists of producing a silver halide one-layered material by pouring the silver halide emulsion layer with thickness 0.5-1.0 micron on a base selected from cellulose acetates, polycarbonate, or polyethyleneterephthalate with thickness 20-40 microns, recording optical information thereon, further photochemical treatment and silver image transformation into image luminescing in the spectral range from 400 to 850 nm. For obtaining multi-layered materials the one-layered materials are sequentially glued one to other so that the active silver halide emulsion layers alternate with the inactive separating polymeric layers which are transparent for a reading laser beam and the resulting luminescent light. Such material can contain two or more silver halide layers. Information reading is carried out by detection of the luminescent light irradiated, when a reading laser beam is focused on the active layers in the points containing luminescent dye. For the puφose of recording three dimensional information by two sources of light , for example by the recording device shown in Fig. 1, a multi-layer material with silver halide layers having the same activity can be used. The silver halide layers of multi-layer materials can also be spectrally sensitized with polymethine dyes to different wavelengths of visible or infra-red light. Filter dyes can also be introduced into the silver halide layers or interlayers for providing color filtration. Such layers can have information recorded on them by printing through color separated masks as is well known in the printing industry. The multi-layer materials, after exposure to light, are developed and treated similarly to the monolayer materials. Another method of producing a multi-layered optical memory device consists of the extrusion of a multi-layer system on a moving polymer film with thickness 150-300 microns. The process comprises simultaneous extruding from a multi-slit filler relatively thin (0.5-1.5 microns) layers of hydrophilic polymer with silver halide and between these layers, relatively thick (20-30 microns) layers of hydrophilic polymer without silver halide to obtain a structure of alternating silver halide containing (active) and silver halide less (inactive) layers. The number of the active layers can be two or more. The following examples are provided in order to further illustrate the invention but should not be construed as limiting the scope thereof. EXAMPLE 1 - The synthesis of the AgBr-emulsion. The synthesis of the super fine grain emulsion of AgBr was conducted by two flow emulsification method at a pAg of 2.3 (ie at silver concentration of [Ag + ] = 10 "23 moles per liter) at 40°C in an apparatus with a 1.5 liter capacity. The velocity of the supply solutions of AgN0 3 (1M) and KBr (1M) was about 3 x 10 "7 g-mol/sec cm 3 . The concentration of the inert gelatin was 50 g/liter and the mixing up velocity was 1,200 rotation /min. The average size of the AgBr microcrystals was about 0.05-0.055 microns. The silver content of the emulsion was 16 g/liter. The emulsion was washed in running saltless water at 10°C for 30 min. The liquid AgBr emulsion then had pyrocatachol (0.1 g/1) and coat additives such as surfactants, glycerine and thimol and hardeners such as chromium acetate were added. The viscosity of the emulsion before the coating of the base was 5.3 centipoise at 40°C. The emulsion was coated upon gelatine laid glass to obtain a 1.5 g/m 2 surface concentration of silver and transparent layers were obtained. Photoplates were exposed by a FSR-41 sensitometer at a color temperature of 5900°C of the light source. Exposed photoplates were developed with the developer D-19 for 5 minutes at 20°C. The plates were fixed in the hardening fixative F-10 for 5 minutes, washed with water and dried. The prepared photoplates had the following characteristics: 1. The light sensitivity by the darkening density criterion of 0.85 above the density of the fog is equal to 4x10 "2 units ISO; 2. The resolution was 4000 lines per millimeter; 3. The contrast coefficient was 9.0; 4. The maximum density of darkening was over 3.0 5. The density of fog was 0.02; and 6. The region of spectral sensitivity was from 300 to 460nm. note to Dr. Agranov; WHAT IS DEVELOPER D-19 AND FIXATIVE F-10? ARE THESE TRADENAMES OR FORMULAS? EXAMPLE 2 - The synthesis of the AgBr(I) -emulsion. The super fine grain emulsion of AgBr(I) (0.7% mol. Agl) was synthesized by the two flow controlled emulsification method at pAg of 2.3 at 40°C , similarly to Example 1 but the mixture of the KBr and KI solution was added to the AgN0 3 solution. The silver content of the emulsion after being washed was 15 g/liter, and the concentration of gelatin was 3.0% by weight. The average size of the microcrystals was 0.03 to 0.04 microns. Photoplates were prepared, exposed and treated in the same manner as the photoplates of Example 1. The photoplates had the following caracteristics: 1. The light sensitivity of 6x10 "2 units ISO; 2. The resolution was 4500 lines per millimeter; 3. The contrast coefficient was 7.0; 4. The maximum density of darkening was over 3.0 5. The density of fog was 0.02; and 6. The region of spectral sensitivity was from 300 to 500nm. EXAMPLE 3 - The synthesis of the AgCl-emulsion. The super fine grain emulsion of AgCl was obtained in a similar manner as Example 1, but instead of KBr, KCl was used. The average size of the cubical microcrystals of AgCl was 0.06 to 0.07 microns. Photoplates were prepared, exposed and treated in the same manner as the photoplates of Example 1. The photoplates had the following caracteristics: 1. The light sensitivity of 0.5x10 "2 units ISO; 2. The resolution was 3000 lines per millimeter; 3. The contrast coefficient was 10.0; 4. The maximum density of darkening was over 3.0 5. The density of fog was 0.02; and 6. The region of spectral sensitivity was from 300 to 400nm. EXAMPLE 4 To the liquid AgBr-emulsion, synthesized similarly to Example 1 , at 40°C, pyrocatechol (0.1 g/liter), the disodium salt of 4, 4'-bis-(4,6-diphenoxy-l,3,5-triazinyl-2- amino)-stilbene-2,2' -disulfonic acid (1 g/liter), and 3,3'-diethyl-6,7,6',7'-dibenzo-l 1-methyl- tiatricarbocyanineiodide as an alcohol solution with a concentration of 2 x 10 "4 mol/mol of AgBr, were added. After adding the dye, the concentration of the silver ion was increased to pAg of 6.5 by IM AgNO 3 . The coat additives, including a surfactant, glycerin and thymol and a hardener, such as chromium acetate, were added before coating the base with the emulsion. The viscosity of the emulsion before coating was 5.3 centipoise at 40°C. The emulsion was coated upon the gelatine layered glass to obtain a silver surface concentration of 1.5 g/m 2 . Photoplates were exposed by a FSP-41 sensitometer behind a KS-14 light filter at a color temperature of 2,850°C of the light source. Exposed photoplates were developed in the developer D-19 for 5 minutes at 20°C degree. The plates were fixed in the hardening fixative substance F-10 for 5 minutes, washed with water and dried. The following characteristics were obtained: 1. The light sensitivity by the darkening density criterion of 0.85 above the density of the "fog" is equal to 4 x 10 "2 units ISO; 2. The resolution ability of 4000 lines/mm; 3. The contrast factor was 9.0; 4. The maximum density of darkening over 3.0; 5. The density of fog was 0.02 and 6. Maximum of spectral sensitization was 860 nm. The energy sensitivity was measured by a ESP-73 spectrum sensitometer by the darkening density criterion of 0.5 at λ = 860nm is equal to 10 3 erg/cm 2 . EXAMPLE 5 The procedure was the same as in Example 4, except that the spectral sensitizer 3,3'- diethyl-9,11- (β - methyltrimethylene)thiatricarbocyanine iodide with a concentration of 3xl0 "4 mol/mol of AgBr was used . The photo sensitivity of the photolayers at the maximum sensitivity of 820 nm was equal to 7 x 10 2 erg/cm 2 . The resolution ability was 4,000 lines/mm. EXAMPLE 6 The procedure used was the same as in Example 4, except that the spectral sensitizer 3,3'- diethyl-9,11- (β,β ! -dimethytrimethylen)tiatetracarbocyanine iodide at a concentration of 1.5 x 10 "4 mol/mol of AgBr was used. The photo sensitivity of the photolayers at the maximum sensitization of 920nm was equal to 2.0x10 3 erg/cm 2 . The resolution ability was 3500 lines/mm. EXAMPLE 7 The procedure used was the same as in Example 4, except that the spectral sensitizer 3,3',9-triethyl-4,5,4',5' -dibenzothiacarbocyan inosylate at concentration of 8 x 10 "4 mol/mol of AgBr was used. Instead of the disodium salt of 4,4'-bis-(4,6-diphenoxy-l,3,5 -triazinyl-2- amino)-stilbene-2,2' disulfo acid, the 1,10-decamethylene-o. -picoline dibromide at a concentration of 8 x 10 "4 mol/mol of AgBr was used. The photo sensitivity of the photolayers at the maximum sensitivity at 680nm was 500 erg/cm 2 . EXAMPLE 8 The procedure the same as in Example 7, except that the sensitizer, the pyridine salt of S^'-di-sulfopropyl-S^ 1 -diphenyl-9-ethyloxacarbocyanine with concentration of 10 "3 mol/mol to AgBr was used. The photo sensitivity of photolayers at the maximum of sensitivity at 545nm was 300 erg/cm 2 . EXAMPLE 9 The same as in Example 7, except that the sensitizer, the pyridine salt of 3,3'-di- sulfopropyl-4,5 benzo-5'-methoxythiamonomethinecyanine with concentration of 8 10 "4 mol/mol to AgBr is used. The photo sensitivity at the maximum of sensitivity at 475nm is 800 erg/cm 2 . EXAMPLE 10 The same as in Example 4, except that the AgCl emulsion is used. The photo sensitivity at the maximum of sensitivity at 850nm is 3,000 erg/cm 2 . The resolution ability is 3,000 lines/mm. EXAMPLE 11 The silver images which was obtained on the samples made as in the Examples 2-10, is bleached at 0.1 M water solution of K 3 [Fe(CN) 6 ]. The photolayers were washed with water, treated with 0.005%) eritrosine solution and washed with water once more. The absorbed dye luminesces in the green region of the spectrum ( max. abs. 547 nm., max. lum. 575nm.) EXAMPLE 12 The same as in Example 11, except that in the capacity of the luminescent dye , the 0.015%) water solution of the fluorescein is used. The absorbed dye is luminescing in the green range of spectrum. EXAMPLE 13 The same as in Example 11 , except that in the bleached solution the benzotriazole is used. The Rodamine 101 is used as the luminescent dye. The absorbed dye is luminescing in the orange-yellow range of spectrum ( max. abs. 560 nm, max. lum. 575 nm). EXAMPLE 14 The silver images on the samples obtained in Examples 2-10 were bleached in 0.1 M aqueous solution of K 3 [Fe(CN) 6 ], washed with water, treated with 0.3M aqueous solution of CdBr 2 , washed with water, treated with a 2.0M aqueous solution of KCNS, than washed again with water and adsorbed eritrosine on formed Cd 2 [Fe(CN) 6 ] from a 0.005% aqueous solution. The adsorbed dye is luminescent in green region of spectrum (absorbtion λmax.545nm, luminescence λmax 575nm). EXAMPLE 15 The same as in Example 14, except that after treatment with water solution of KCNS and washing with water, the samples are treated with 0.4M aqueous solution of Na^-^O, washed with water. The CdS particle then were treated with Rhodamin B in a 0.005%o aqueous solution. The adsorbed dye was luminescent in the orange-yellow range of the spectrum (absoφtion λmax. 562nm, luminescence λmax. 585nm). EXAMPLE 16 The same as Example 11, except that after bleaching in 0.1 M solution of K 3 [Fe(CN) 6 ] and washing with water, the samples were treated with a 2.0%> water-alcohol (1 :1) solution of l-phenyl-5-mercaptotetrazole, washed with water and adsorbed on formed the silver salt of 1- phenyl-5-mercaptotetrazole triethylammonium salt of 3,3'-disulfopropyl-5,5'-dichloro-9- ethyloxacarbocyaninebetaine from 1.0x10 "5 M solution. Adsorbed dye has adsoφtion λmax. 545nm and luminescence λmax 580nm. EXAMPLE 17 The same as in Example 16, except that a 2.0% water-alcohol (1:1) solution 2- mercaptobenzoxazole was used and the pyridine salt of 3,3'-disulfopropyl-5,5'-dimethoxy-9- ethylthiacarbocyaninebetaine, was adsorbed on the formed silver salt of 2- mercaptobenzoxazole from 1.0x10 "5 M solution. Adsorbed dye has absoφtion λmax. 650nm, and luminescence λmax. 665nm. EXAMPLE 18: The same as in Example 16, except that a 2.0%> water-alcohol (1:1) solution of 2- mercaptobenzimidazole was used and the potassium salt of 1,1,1', l'-tetramethyl-3,3'- disulfopropylindodicarbocyanine from 1.0x10 "5 M water solution was adsorbed on the formed Ag-salt of 2-mercaptobenzimidazole. Adsorbed dye has absoφtion λmax. 645nm and luminescence λmax. 702nm. EXAMPLE 19 The same as in Example 16, except that a 2.0% water-alcohol solution of 2- mercaptobenzothiazol was used and 1 , 1 , 1 ', l',3 ,3'-hexamethylindocarbocyanineiodide was adsorbed from a 1.0x10 "5 M water alcohol (1:1) solution on formed silver salt of 2- mercaptobenzothyazole. The places where there are particles with adsorbed salt do not luminesce and there was luminescence from the bulk polymer. The dye has an absoφtion λmax. 650nm and luminescence λmax. 682nm. EXAMPLE 20 The same as in Example 11, except that after bleaching, the layer was treated with 0.1% solution of Ga(NO 3 ) 3 washed with water and treated with 0.05% solution of 8- oxiquinoline. The dye was adsorbed on the insoluble salts that were located at the places were the photolayer was exposed to light. The adsorbed dye was luminescing in the yellow-green range of spectrum. EXAMPLE 21 The same as in the Example 20, except that after bleaching, the exposed photolayer was treated with 0.1% solution of Cu(N0 3 ) 3 washed with water and treated with 0.2%) water solution of methylcalcein. In the places where the photolayer was exposed to light and the copper salt had absorbed the dye had a yellow-green luminescence and the background was not luminescent. EXAMPLE 22 Similarly to the Example 1 , the AgBr emulsion was prepared and was divided into three parts. The first part of the emulsion was spectrally sensitized as in Example 4, the second part of the emulsion was spectrally sensitized as in Example 7 and the third one, as in Example 8. The sensitized emulsions were coated using a multi-slit filler by layers on to the gelatine coated polyethylene terephthalate base. For the information recording the photomaterial consistently exposed through the mask following the light filters, transmitting light with a wavelenghth of 860 nm, 680 nm and 545 nm . The photolayers were subjected to the photo-chemical treatment as in the Example 18 and with a 0.001% water solution of the sodium salt of lJ'-di-γ-sulfopropyl-SjS'-disulfo-S^^^'- tetramethylindodicarbocyaninebetaine. The luminescence maximum of the absorbed dye was 700nm. EXAMPLE 23 The same as in the Example 22, except that the treatment of layers was conducted with 0.001% water solution of trisodium salt of l,l'-di-γ-sulfopropyl 5,5'-disulfo-3,3,3',3'- tetramethyl-n-indotricarbocyaninebetaine. The maximum of luminescence -790nm. EXAMPLE 24 The silver halide systems are characterized of high photostability. The irradiation of the film obtained in Example 22, for 200 hours in a cuvett of a Shimadzu spectrofluorimeter at a wavelength of 640nm used for fluorescent excitability did not lead to any changes in the fluorescent intensity. During similar film irradiation, based on the bis-dianilinochloromethyl- 1,3,4-oxadiazole as in the U.S. Patent No. 3 869 363, a decrease of the fluorescent intensitivity of 2.5 times was observed. Although certain presently preferred embodiments of the present invention have been specifically described herein, it will be apparent to those skilled in the art to which the invention pertains that variations and modifications of the various embodiments shown and described herein may be made without departing from the spirit and scope of the invention. Accordingly, it is intended that the invention be limited only to the extent required by the appended claims and the applicable rules of law.

Claims: IN THE CLAIMS: 1. A luminescent material for an optical memory device comprising insoluble microparticles dispersed in a water soluble polymer, said microparticles having a particle size less than about 0.2 microns, said microparticle having a sorbed luminescent dye wherein said water soluble polymer and dispersed microparticles are applied to a substrate. 2. The microparticle material of claim 1 , wherein the insoluble microparticles comprise silver grains and insoluble metal salts. 3. The microparticles material of claims 1 and 2 wherein the water soluble polymer is selected from the group consisting of polyvinyl alcohol, polyvinyl pyrrolidone, gelatine, gelatine modified with polyvinyl alcohol, polyvinyl pyrrolidone, polyvinyl sulphate, carboxymethylcellulose, cellulose acetophthalate, phthaloylgelatine or graft polymers of gelatine with polymethoxydiethyleneglycol acrylate or with polydiacetoneacrylamide or with poly-N,N'-methylenediacrylamide, and mixtures thereof. 4. A method for making a luminescent material for an optical memory devices comprising the steps of: applying a photographic emulsion comprising microcrystals of silver halide salts and a water soluble polymer to a substrate to form a photoplate; exposing said photoplate to light; developing said photoplate with fixation of the exposed silver halide to form particles; treating the photoplate with a luminescing dye and allowing the luminescing dye to be sorbed onto the particles. 5. The method of claim 4, wherein the silver halide is selected from AgCl, AgBr, Agl, AgCl(Br), AgCl(Br,I) and AgBr(I). 6. The method of claims 4 and 5, wherein the microcrystals of silver halide are less than about 0.2 microns. 7. The method of claim 6, wherein the microcrystals are about 0.02 to 0.08 microns. 8. The method of claims 4-7, wherein the water soluble polymer is selected from the group consisting of polyvinyl alcohol polyvinyl pyrrolidone, gelatine, gelatine modified with polyvinyl alcohol, polyvinyl pyrrolidone, polyvinyl sulphate, carboxymethylcellulose, cellulose acetophthalate, phthaloylgelatine or graft polymers of gelatine with polymethoxydiethyleneglycol acrylate or with polydiacetoneacrylamide or with poly-N,N'- methylenediacrylamide, and mixtures thereof. 9. The method of claims 4-8, additionally comprising the step of chemically sensitizing the photoplate with a photoreducer before exposure to light. 10. The method of claim 9, wherein the photo reducer is selected from gold, sulphur and mixtures thereof. 11. The method of claims 4- 10, additionally comprising the step of adding a spectral sensitizer to the photoplate before exposure to light, said spectral sensitizer being selected from the group of sensitizers where in the case of the benzothiazole derivatives (X,Y=S); benzoxazole derivative (X,Y=O); benzimidazole derivative (X,Y=NR); quinoline derivative (X,Y=-CH=CH-); indolenine derivative (X,Y=C(R 2 )) and so on; for the non-symmetrical dyes X does not equal Y (X≠Y), for example, X=O, and Y=S and are independently selected; wherein, for each derivative R 2 and R 3 are independently selected from H , CH 3 , -OCH 3 , -SCH 3 , -N(CH 3 ) , -N(Et) 2 , -N(propyl) 2 , -N(iso-propyl) 2 , -N(butyl) 2 , -N(iso-butyl) 2 , -N(sec-butyl) 2 , -NCO(CH 2 ) k H wherein k is 1 to 5 , F, Cl, Br, I, -CN, -C0 2 H , -C0 2 (CH 2 ) J CH 3 where j is 0 to 4 , -CONH 2 , - CF 3 , SOCF 3 , S0 2 CF 3 , -C 6 H 5 , and benzyl; n is 0, 1 or 2 and m is 0 or 1 ; when n is 0 and m is 1 then Rg is independently selected from H , CH 3 , C 2 H 5 , C 6 H 5 , -NH 2 , -NHCOCH, , - OCH 3 , C0 2 CH 3 ; when n is 1 and m is 1 then R 4 and Rg are H and R 5 H, CH 3 , C 2 H 5 , NHCOCH 3 , when R 4 and Rg are linked together and R 4 and Rg are -(CH 2 ) 2 - , -(CH 2 ) 3 - , or - CH 2 C(CH 3 ) 2 CH 2 - then R 5 is H, Cl, and C 6 H 5 ; when n is 2 and m is 1 then R 4 , R 5 and Rg are H or R 4 and R^ are H and R 5 and R 5 is linked together and R 5 is -(CH 2 ) 3 - , -CH 2 C(CH 3 ) 2 CH 2 - ; and when R and R, are independently selected from alkyl then Z " is an anion and when R and R, are independently selected from -(CH 2 ) 3 S0 3 " then Z + is a cation; merocyanines and merocyaninocyanines and others can be used and mixtures thereof. 12. The method of claims 4-11, additionally comprising the step of oxidizing the surface of the silver particles in the photoplate. 13. The method of claim 12, additionally comprising the step of adding a solution of at least one multivalent ion to the photoplate after the surface of the silver particles is oxidized. 14. The method of claim 13, wherein the multivalent ions are selected from the group consisting of Ba +2 ,Co +2 , Zn +2 , Cd +2 and mixtures thereof. 15. The method of claims 4- 14, additionally comprising the step of treating the oxidized silver particle with metal salts to form insoluble metal complexes. 16. The method of claim 15 , wherein the metal salts are selected from the group consisting of Zn 2+ , Cd 2+ , Sr Ni 2+ , Co 2+ , Fe 3+ , Cr , In 3+ , Bi 3+ , La 3+ , Gd 3+ , V 4+ , Ce 4+ , Th 4+ , and mixtures thereof. 17. The method of claim 15, wherein the insoluble metal complexes have a solubility constant less than about 10 "8 mole/liter at 25 °C. 18. The method of claim 17, wherein the solubility constant is less than 10" 10 mole/liter at 25 °C. 19. A luminescent optical memory material made by the process of claims 4-18. 20. The method of claims 4-18, wherein the photographic emulsion is applied to the base so that there are layers of photographic emulsion separated by layers of a water soluble polymer. 21. The luminescent optical memory material of claim 19, wherein the photographic emulsion is applied to the base so that there are layers of photographic emulsion separated by layers of a water soluble polymer. 22. The material or methods of claims 1-21 wherein the luminescent dye is selected from the xanthene dyes of the eoscin type including eosins, fluoresceins, erythrosins, and dichlorofluorescein of general structure I: wherein R is independently selected from H, Cl, Br, I, N0 2 , alkyl and others; R, is H, Na, K, and alkyl; R 2 is independently selected from H, Cl. NH 2 , Br, I, isocyanate, isothiocyanate, alkyl and others; and R 3 is independently selected from H, Cl, Br, I, N0 2 , NH 2 , alkyl and others; (2) The xanthene dyes of the rhodamine type including the rhodamines B, 3B, C, G, 6G, 101, 123 and others having the general structure II: wherein R is H, CH 3 , C 2 H 5 , CH 2 COOH, C 2 H 4 OH and others; R, is H, Na, K, CH 3 , C 2 H 5 , Ar, Alkyl and others; R 2 is independently selected from H, Cl, Br, I,N0 2 . alkyl and others, R 3 is independently selected from H, Cl, Br, I, N0 2 , isothiocyanate, isocyanate, amines and others and X is an anion selected from Cl " , Br " , I " , C10 4 " and others; (3) The acridine dyes, including aurazine, trypaflovine, ethoxydiaminoacridine lactate and others of general structure III: wherein R is H, CH 3 , C 2 H 5 , and others; R, is H, C 6 H 5 , C0 2 H and others; R 2 is H, CH 2 CH 2 OH, alkyl and others; R 3 is independently selected from H, CH 3 , alkyl and others; and X is a anion of F, Cl, Br, I, HCOO " , CH 3 CHOHCOO " , C10 4 " and others; (4) The oxazine dyes, including the oxazines 1, 4, 9, 17, 118, nile blue, capry blue A and others having the general structure IVa and IVb: where R is selected from H, CH 3 , and others; R x is independently selected from H, CH 3 , CH 3 CH 2 alkyl and others and X is an anion selected from F, Cl, Br, I, C10 4 " , sulfates, phosphates and others; (5) The azine dyes, including magdala red, lactoflavine. of general structure V: (R 1 wherein R is phenyl, naphthyl; R, is H, alkyl, C 6 H 5 , and others ; R 2 is H, alkyl, benzyl, O- benzyl; R 3 is H, S0 3 H and others; and X is an anion; (6) The indigo dyes, in the form of indigozoles, of general structure VI: wherein, Y is NH, S and R is independently selected from H, Cl, Br, O-alkyl, NO 2 , sulfate, alkyl and others; (7) The polycyclic vat dyes, including aminoanthropyrimidines, anthropyridones, oxa-and tiadiazoloaminoantroquinones, dyes from the group of benzanthrones in the form of sulfuric esters of leuco compounds of general structure VII - XI: where R is H, NH-C 6 H 5 , R, is H, where R is H, alkyl, or aromatic, where R is H, C 6 H,„ C 2 H 5 , C 2 H 4 OH where R is H, Ar, -S0 2 Ar and others, where R is independently selected from H, Cl, Br, OH, the structure: and others; (8) The dyes which are forming both the luminescent and non-luminescent complexes with polyvalent metal ions, selected from the hydroxyantraquinone derivatives: calcein, calcein blue, xanthocomplexan, methylcalcein, methylcalcein blue as shown in general structures XII -XVII: Where R is CH 3 , CH 2 COOH (9) The cyanine dyes of general structure XVIII: (XVIII) wherein n is 1,2,3 ; R is H, S0 3 H and others; R, is alkyl, (CH 2 ) m S0 3 H and others m is 3,4 or 5 and X " is a anion.

Inventors: ALPEROVICH MARK A, LEVICH EUGENE B, MALKIN JACOB N, SHAPIRO BORIS M, ALPEROVICH, MARK, A., LEVICH, EUGENE, B., MALKIN, JACOB, N., SHAPIRO, BORIS M.
Applicants: ALPEROVICH MARK A, LEVICH EUGENE B, MALKIN JACOB N, SHAPIRO BORIS M, TRID STORE INC, ALPEROVICH, MARK, A., LEVICH, EUGENE, B., MALKIN, JACOB, N., SHAPIRO, BORIS M., TRID STORE INC.
Application year: 1998
Main classification: G03C1
IPC codes: G03C1, G03C9, G11B7