REDUCTION OF CHARGE LOSS IN NONVOLATILE MEMORY CELLS BY PHOSPHOROUS IMPLANTATION INTO PECVD NITRIDE/OXYNITRIDE FILMS

Abstract: A semiconductor device (400) formed in a semiconductor substrate (402) with a low hydrogen content barrier layer (432) formed over the semiconductor device (400). The barrier layer (432) is implanted with phosphorous ions (429). The semiconductor device (400) may have a hydrogen getter layer (424) formed under the barrier layer (432). The barrier layer (432) is a high temperature PECVD nitride film, a high temperature PECVD oxynitride film or a high temperature LPCVD nitride film. The hydrogen getter layer (424) is P-doped film having a thickness between 1000 and 2000 Angstroms and is a PSG, BPSG, PTEOS deposited oxide film, or BPTEOS deposited oxide film. Interconnects (438) are made by a tungsten damascene process.

Description: REDUCTION OF CHARGE LOSS IN NONVOLATILE MEMORY CELLS BY PHOSPHORUS IMPLANTATION INTO PECVD NITRIDE/OXYNITRIDE FILMS BACKGROUND OF THE INVENTION 1. Field of the Invention This invention relates generally to high performance semiconductor devices with reduced charge loss in nonvolatile memory devices having barrier layers implanted with phosphorus. More specifically, this invention relates to high performance semiconductor devices with barrier layers implanted with phosphorus and a hydrogen getter layer formed under the barrier layer. 2. Discussion of the Related Art The semiconductor industry is characterized by the dual requirements of an increase in the speed of integrated circuits and an increase in the density of elements in those integrated circuits. These two requirements have thus become the two major goals of the design engineers in their design and manufacturing efforts concerned with MOSFETs and other semiconductor devices, such as volatile and nonvolatile memory devices. Increasing the density of elements in integrated circuits means that smaller channel lengths and widths have to be used. Λs (he dimensions of semiconductor devices decreased, the existing "long-channel" performance models for MOSFET devices predicted that the decrease in the channel length, , or the gate oxide thickness, T ox , would increase lDSAT- However, as MOSFET devices were scaled below approximately 2 \\ m, effects not predicted by the existing long channel models were observed and the unexpected effects were thereafter termed "short- channel" effects. As device dimensions of MOSFETs continued to decrease, it was determined that problems associated with the short-channel effects could be placed in two general categories: ( 1 ) the problem of increased leakage current when the MOSFET is off and (2) reliability problems associated with short- channel and thin gate oxide device structures. Some of the reliability problems that arise in short-channel and thin gate oxide MOSFETs include; ( 1 ) thin gate oxide breakdown, (2) device degradation due to hot-carrier effects, (3) reliability problems associated with interconnects between MOSFETs and (4) reliability problems associated with local interconnects. One of the major problems associated with semiconductor devices other than MOSFETs involves high-temperature data retention in nonvolatile memory cells. The two problems that are of particular interest are device degradation due to hot-carrier effects and high-temperaturc data retention problems in nonvolatile memory cells. It has been observed that there are high-temperature data retention problems in nonvolatile memory cell arrays such as EPROMs, FLASH EPROMs. and E^PROMs. It has been postulated that the poor high-temperature data retention is due to mobile hydrogen atoms that diffuse to the floating gate in a nonvolatile memory cell and cause the charge on the floating gate to be lost. The reduced memory cell size and high-performance logic circuits has necessitated the use of a borderless contacts and local interconnects. The borderless contacts and local interconnects have required the use of a barrier layer such as an etch stop layer or diffusion protect layer. The prior art developed a low-temperature, damascene-tungsten local interconnect for a 0.25 μm channel CMOS technology with trench isolation. One such prior art structure is described in "A Low-Temperature Local Interconnect Process in a 0.25-μ m-channel CMOS Logic Technology with Shallow Trench Isolation," by J. Givens, S. Geissler, O. Cain, W. Clark, C Koburger, .1. Lee, 1994 VMIC Conference. However, the prior art includes the use of silicon nitride films that have high hydrogen content. The high hydrogen content has caused problems as described in the article "Effects of Silicon Nitride Encapsulation on MOS Device Stability," by R.C. Sun, .1. 1. Clemens and J. T. Nelson. IEEE 1980. This article describes a new threshold instability phenomenon observed in MOS transistors encapsulated with plasma deposited silicon nitride films and describes a series of experiments which indicated that the instability was due to a chemical effect associated with hydrogen in the silicon nitride films. The article postulated that the formation of surface states and fixed charges in the channel region was due to the interaction of hot carriers with hydrogen present at the interface and was the basic mechanism causing the instability. Therefore, what is needed are semiconductor devices that have low amounts of free hydrogen and methods of manufacturing such low hydrogen content semiconductor devices. SUMMARY OF THE INVENTION The present invention is directed to a semiconductor device with a barrier layer formed on the semiconductor device and wherein the barrier layer is implanted with phosphorus ions. The barrier layer is a high temperature PECVD silicon nitride film, a high temperature PECVD silicon oxynitride film, or a high temperature LPCVD nitride film. The present invention is further directed to semiconductor devices having a hydrogen getter layer formed under the barrier layer. The hydrogen getter layer is selected from a group including a PSG film, a BPSG film, a PTEOS deposited oxide film, or a BPTEOS deposited oxide film. The hydrogen getter layer has a thickness of approximately 1000-2000 Angstroms. The present invention is also directed to semiconductor devices having tungsten damascene interconnects. The present invention is further directed to a method of manufacturing semiconductor devices having a barrier layer formed on the semiconductor device. The barrier layer is implanted with phosphorus ions. The barrier layer is formed of a material selected from the group including a high temperature PECVD silicon nitride film, a high temperature PECVD silicon oxynitride film, and a high temperature LPCVD silicon nitride film. The method of the present invention includes forming a hydrogen getter layer under the barrier layer. The hydrogen getter layer is selected from a group including a PSG film, a BPSG film, a PTEOS deposited oxide film, and a BPTEOS deposited oxide film. The hydrogen getter layer is formed with a thickness of approximately 1000-2000 Angstroms. The present invention is better understood upon consideration of the detailed description below, in conjunction with the accompanying drawings. As will become readily apparent to those skilled in the art from the following description there is shown and described embodiments of this invention simply by way of illustration of the best modes to carry out the invention. As will be realized, the invention is capable of other embodiments and its several details are capable of modifications in various obvious aspects, all without departing from the scope of the invention. Accordingly, the drawings and detailed description will be regarded as illustrative in nature and not as restrictive. BRIEF DESCRIPTION OF THE DRAWINGS The accompanying drawings incorporated in and forming a part of the specification, illustrate the present invention, and together with the detailed description below serve to explain the principles of the invention. In the drawings: Figures 1A - ID show a portion of a prior art semiconductor device having a floating gate, a gate protect oxide layer and a barrier layer. Figures 1 A - I D also illustrate selected steps in a method of manufacturing the semiconductor device. Figures 2A - 2E show a portion of a semiconductor device manufactured in accordance with the present invention having a floating gate, a gate protect oxide layer and a barrier layer. Figures 2A -2E also illustrate selected steps in a method of manufacturing the semiconductor device. Figures 3A - 31 show a portion of a prior art semiconductor device having a tungsten damascene local interconnect (LI), with the gate protect oxide layer removed to allow salicide layers to be formed on the semiconductor device, and a local interconnect barrier layer. Figures 3A -31 also illustrate selected steps in a method of manufacturing the semiconductor device. Figures 4A - 4L show a portion of a semiconductor device manufactured in accordance with the present invention having a tungsten damascene local interconnect (LI) or an interconnect to a source or drain electrode. Figures 4A - 4L also illustrate selected steps in a method of manufacturing the semiconductor device. Figures 5A - 5J show a portion of a semiconductor device manufactured in accordance with the present invention having a tungsten damascene local interconnect (LI) or an interconnect to a source or drain electrode. Figures 5A - 5J also illustrate selected steps in a method of manufacturing the semiconductor device. Figure 6 is a diagram showing experimental measurements taken from devices manufactured with various phosphorus implant dosages. DETAILED DESCRIPTION Reference is now made in detail to specific embodiments of the present invention that illustrate the best modes presently contemplated by the inventors for practicing the invention. Figures 1A - ID show the structure and selected steps in a method of making a prior art semiconductor device 100 having a floating gate. Such a device could be used, for example, in a nonvolatile memory cell. Like numerical designations are used in each of the subsequent figures for like elements. Figure 1 A shows a semiconductor substrate 102 having a program junction region 104 formed in the semiconductor substrate 102. The floating gate 106 is separated from the program junction region 104 by a layer of gate oxide 108. The sidewall spacers 110 and 112 are formed on each side of the floating gate 106. Figure IB shows the semiconductor device 100 as shown in Figure 1 A with a thin gate protect oxide layer 114 formed on the structure 100. The gate protect oxide layer 114 utilized in the prior art is typically an undoped oxide layer having a thickness of approximately 300 Angstroms and is utilized to protect portions of the device from forming a salicide (self-aligned suicide) layer in a subsequent step. The gate protect oxide layer 114 is shown etched away at 116 and 118 to allow salicide layers to form in selected areas not protected by the gate protect oxide layer 114. Figure 1C shows the semiconductor device 100 as shown in Figure IB showing salicide layers 120 and 122. The salicide layers are typically titanium suicide, T1S12 or cobalt suicide , CoSi2- Figure ID shows the semiconductor device 100 as shown in Figure 1C with a barrier layer 124 formed on the semiconductor device 100. The barrier layer 124 in the prior art is typically a plasma deposited silicon oxynitride or nitride. A process to form such a layer is a PECVD (plasma enhanced chemical vapor deposition) at approximately 400 °C. Figures 2A - 2E show the structure and selected steps in a method of making a semiconductor device 200 having a substantially hydrogen-free floating gate in accordance with the present invention. Like numerical designations are used in each of the subsequent figures for like elements. Figure 2A shows a semiconductor substrate 202 having a program junction region 204 formed in the semiconductor substrate 202. The program junction region 204 can be formed by the ion implantation of appropriate ions into the substrate 202. The floating gate 206 is separated from the program junction region 204 by a layer of gate oxide 208. The sidewall spacers 210 and 212 are formed on each side of the floating gate 206. -5- Figure 2B shows the semiconductor device 200 as shown in Figure 2A with a hydrogen getter layer 214. The hydrogen getter layer 214 is a doped (phosphorus-doped) film such as a PSG (phosphosilicate glass) film, a BPSG (borophosphosilicate glass) film, a PTEOS (phosphorus doped tetraethyl orthosilicate) deposited oxide film, or a BPTEOS (borophosphorus doped telraethyl orthosilicate) deposited film. The purpose of the hydrogen getter layer 214 is to getter any mobile hydrogen ions present in the semiconductor device 200. The hydrogen getter layer 214 is preferably formed having a thickness of 1000-2000 Angstroms. The hydrogen getter layer 214 is shown etched away at 216 and 218 to allow a salicide layer to form in areas not protected by the hydrogen getter layer 214. Figure 2C shows the semiconductor device 200 as shown in Figure 2B showing the salicide layers 220 and 222. The salicide layers are typically titanium suicide. TiSi2, or cobalt suicide, CoSio. Methods of forming salicide are well known in the semiconductor manufacturing art and will not be discussed. Figure 2D shows the semiconductor device 200 as shown in Figure 2C with the barrier layer 224 formed on the semiconductor device 200. The barrier layer 224 is formed by a high temperature process (500°C or higher) and is typically a layer of PECVD nitride or an oxynitride film or an LPCVD (low pressure chemical vapor deposition) nitride film. The barrier layer 224 serves as an etch stop layer and, in addition, minimizes the hydrogen content in the deposited film. Figure 2E shows the semiconductor device 200 as shown in Figure 2D with a phosphorus implant indicated by arrows 226. The phosphorus is implanted at a dosage in the range of 1 El 4 to 1 El 6 ions per centimeter squared and is implanted at an implant energy in the range of 25 KeV to 35 eV. The preferable implant parameters for a barrier layer having a thickness of approximately 800 Angstroms is at a dosage of 1 El 6 ions of phosphorus per centimeter squared and at an energy of 35 KeV. The implant is heat-treated and preferably the heat treatment is a rapid thermal anneal (RTA) at 800 degrees Centigrade. Figures 3A - 31 show the structure and selected steps in a method of making a prior art semiconductor device 300. Like numerical designations are used in each of the subsequent figures for like elements. It should be appreciated that the device 300 shown in Figures 3A-3I is typically manufactured in a chip that also includes other semiconductor devices such as the semiconductor device 100 discussed in conjunction with Figures 1A-1D. Figure 3A shows a portion of the semiconductor device 300 having a semiconductor substrate 302 with trench isolation regions 304 and 306. The trench isolation regions 304 and 306 can also be field oxide regions formed by a LOCOS process. The semiconductor device 300 has a gate 308, typically a polysilicon gate, separated from the semiconductor substrate 302 by a gate oxide layer 310 with sidewall spacers 312 and 314 formed on each side of the gate 308. Lightly doped drain (LDD) regions 316 and 318 are formed in the semiconductor substrate 302. The LDD regions 316 and 318 are typically formed by masking regions of the semiconductor device 300 and implanting selected ions into the substrate 302. Ions that can be used to form the LDD regions 316 and 318 are phosphorous ions at a dosage of about 1 El 3 ions per centimeter squared. The formation of the LDD regions 316 and 318 is typically done before the formation of the sidewall spacers 312 and 314. The methods of implanting ions are well known in the art and will not be discussed. Figure 3B shows the prior art semiconductor device 300 shown in Figure 3A with a source region 320 and a drain region 322 formed in the semiconductor substrate 302. The formation of the source and drain regions 320 and 322 is typically done by ion implantation of appropriate ions. The process of implanting ions to form source and drain regions in a semiconductor device is well known in the semiconductor manufacturing art and will not be discussed. The concentration of the ions in the source and drain regions 320 and 322 is greater than the concentration of the ions in the LDD regions 316 and 318 and thus, the LDD regions 316 and 318 are shown subsumed by the source and drain regions 320 and 322. Ions that are typically implanted into the source and drain regions 316 and 318 are arsenic ions at a dosage of about 1 El 5 ions per centimeter squared. It should be appreciated that other ions can be used to form either the LDD regions or the source and drain regions. Figure 3C shows the prior art semiconductor device 300 shown in Figure 3B with a gate protect oxide layer 324 formed over the entire surface of the semiconductor device 300. The gate protect oxide layer 324 in prior art devices is typically 300 Angstroms thick. The purpose of the gate protect oxide layer 324 is to protect selected areas of the device 300 from forming a salicide layer in a subsequent step of the manufacturing process. It should be appreciated that the portion of the device 300 shown in Figures 3A - 31 is only one portion of the entire device and the gate protect oxide layer 324 can be formed over the entire surface of the device. Figure 3D shows the semiconductor device 300 shown in Figure 3C after the gate protect oxide layer 324 has been removed. Figure 3E shows the prior art semiconductor device 300 shown in Figure 3D with a salicide layer 326 formed on the source region 320, a salicide layer 328 formed on the drain region 322, and a salicide layer 330 formed on the gate region 308. The salicide is typically titanium silicide, TiSi2, or cobalt silicide, CoSi2, and is formed by methods well known in the semiconductor manufacturing art and will not be discussed. Figure 3F shows the prior art semiconductor device 300 shown in Figure 3E with a barrier layer 332 formed on the entire semiconductor device 300. The barrier layer 332 is typically a plasma silicon oxynitride or a silicon nitride film and the barrier layer is used to protect features of a semiconductor device from the typical etch materials used to etch silicon dioxide. Figure 3G shows the prior art semiconductor device 300 shown in Figure 3F with a dielectric layer 334 that has been formed on the device 300 and has been selectively etched to leave an opening, indicated at 336, that exposes a selected portion of the underlying device. A method of forming such an opening is to deposit or form a dielectric layer 334 on the entire semiconductor device 300 and then to etch selected portions of the dielectric layer 334 to expose underlying regions of the semiconductor device 300. Typical materials that are used to etch the dielectric layer are C4F8 or a combination of ^4^8 and CH3 ? - ^he purpose of barrier layer 332 is to stop the etch materials used to etch the dielectric layer from etching the material underlying the dielectric layer. The purpose of the dielectric layer 334 is to electrically insulate the underlying portions of the device 300 from other elements that may be manufactured above the dielectric layer 334. As will be shown, the opening 336 allows electrical contact between selected portions of the underlying device 300 and selected portions of any device manufactured above the dielectric layer 334. Figure 3H shows the portion of the barrier layer 332 having been etched away after being exposed by the opening 336. As is known in the semiconductor manufacturing art, the process of forming interconnects is a two-step process. The first step is to selectively etch portions of the dielectric 334. Barrier layer 332 prevents the dielectric etch material from etching the materials underlying the barrier material. When the dielectric material is etched, the barrier layer 332 is then etched to expose selected areas of the underlying material. The barrier layer 332 is typically etched by an etch material such as CH3F & O2. Figure 3H shows the surfaces of the opening 336 coated with an adhesion layer 337 such as titanium nitride or a combination of titanium and titanium nitride. Figure 31 shows the semiconductor device 300 with the opening 336 filled with a conductive material 338 after the adhesion layer 337 is formed on the surfaces of the opening 336. The se iconductor device 300 is typically planarized after the interconnect material 338 is formed so that the next layer is manufactured on a smooth flat surface. Materials that are used for interconnects are conductive materials such as tungsten. The interconnect shown and described in Figures 3A-3I electrically connects the gate 308 to the drain region 322. As can be appreciated by one of ordinary skill in the art, the region indicated as being a drain region 322 could also be a source region and the gate could also be selected to be electrically connected to the source region of the device. As can also be appreciated, any combination of elements can be electrically connected, either on the same device or other devices in the semiconductor device. It is also noted that the method of forming a dielectric layer, etching an opening in the dielectric layer, and filling the opening with a conductive material is known in the art as the damascene method. Figures 4A - 41 show the structure and the method of making a semiconductor device 400 having salicide layers in accordance with the present invention. Like numerical designations are used in each of the subsequent figures for like elements. It should be appreciated that the semiconductor device 400 is manufactured on a portion of a semiconductor chip and could be manufactured on a chip that also includes a semiconductor device 200 described above in conjunction with Figures 2A-2E. Figure 4A shows a portion of the semiconductor device 400 manufactured on a semiconductor substrate 402 with trench isolation regions 404 and 406. The trench isolation regions 404 and 406 regions can also be field oxide regions formed by a LOCOS process. The semiconductor device 400 has a gate 408, typically a polysilicon gate, separated from the semiconductor substrate by a gate oxide layer 410 with the sidewall spacers 412 and 414 formed on each side of the gate 408. The lightly doped drain (LDD) regions 416 and 418 are formed in the semiconductor substrate 402. The LDD regions 416 and 418 are typically formed by masking regions of the device 400 and implanting selected ions into the substrate 402. The formation of the LDD regions is typically done before the formation of the sidewall spacers 412 and 414. Ions that can be used to form LDD regions are phosphorous ions at a dosage of about I El 3 ions per centimeter squared. The methods of implanting ions are well known in the semiconductor manufacturing art and will not be discussed. Figure 4B shows the semiconductor device 400, as shown in Figure 4A, with a source region 420 and a drain region 422 formed in the semiconductor substrate 402. The formation of the source and drain regions 420 and 422 is typically done by ion implantation of appropriate ions and is well known in the semiconductor manufacturing art and will not be discussed. The concentration of the implanted ions in the source and drain regions 420 and 422 is greater than the concentration of the implanted ions in the LDD regions 416 and 418 and thus, the LDD regions 416 and 418 are shown subsumed by the source and drain regions 420 and 422. Ions that are typically implanted into the source and drain regions 416 and 418 are arsenic ions at a dosage of about 1 El 5 ions per centimeter squared. It should be appreciated that other ions can be used to form either the LDD regions or the source and drain regions. Figure 4C shows the semiconductor device 400 with a hydrogen getter layer 424 formed over the entire surface of the device 400. The hydrogen getter layer 424 is a film such as a PSG (phosphosilicate glass) film, a BPSG (borophosphosilicate glass) film, a PTEOS (phosphorus doped tetraelhyl orthosilicate) deposited oxide film, or a BPTEOS (borophosphorus-doped letraethyl orthosilicate) deposited oxide film. The hydrogen getter layer 424 typically has a thickness between 1000 and 2000 Angstroms. The purpose of the hydrogen getter layer 424 is to getter mobile hydrogen and to protect selected underlying areas from forming salicide layers in subsequent processing steps. The portion of the device 400 shown in Figures 4A-4L is only one portion of the entire device and the hydrogen getter layer 424 is formed over the entire surface of the device. Figure 4D shows the device 400 with the hydrogen getter layer 424 removed from the portion of the device shown in Figures 4A- 4L. The hydrogen getter layer 424 is removed from this portion of the device 400 because it is intended that selected portions of the device 400 will form salicide layers. The hydrogen getter layer 424 is not removed from portions of the device 400 that are not to form a salicide layer. Figure 4E shows the semiconductor device 400 with a salicide layer 426 formed on the source region 420, a salicide layer 428 formed on the drain region 422, and a salicide layer 430 formed on the gate region 408. The salicide layer is typically titanium silicide, TiSi2, or cobalt silicide, CoSi2, and is formed by methods well known in the semiconductor manufacturing art and will not be discussed. Figure 4F shows the semiconductor device 400 with the barrier layer 432 formed on the entire semiconductor device 400. The barrier layer 432 is typically a high temperature (500 °C or higher) plasma silicon nitride, silicon oxynitride or an LPCVD silicon nitride film. The barrier layer 432 is used to protect underlying features of the semiconductor device 400 from the typical etch materials used to etch silicon dioxide. Figure 4F illustrates the implantation of phosphorus ions, indicated by arrows 429, as described above in conjunction with Figure 2E. It should be appreciated that the complete semiconductor device is implanted with phosphorus ions. The implantation of phosphorus ions in the semiconductor device 400 prevents the gate and gate oxide region from having an overabundance of mobile hydrogen which has been shown to exacerbate the hot-carrier aging of MOSFET devices. Figure 4G shows the semiconductor device 400 with a dielectric layer 434 formed on the semiconductor device 400. The purpose of the dielectric layer 434 is to electrically insulate the underlying portions of the device 400 from other elements that may be manufactured above the dielectric layer 434. Figure 4H shows the semiconductor device 400 with the dielectric layer 434 planarized to provide a smooth surface for subsequent manufacturing processes. Figure 41 shows the semiconductor device 400 with an opening 436 etched in the dielectric layer 434. Openings, such as the opening 436, allow electrical contact between selected portions of one layer of the semiconductor device 400 and selected portions of any device manufactured above the dielectric layer 434 or allow electrical contact between selected portions on the same layer of the device 400. Figure 4J shows that the portion of the barrier layer 432 exposed by the opening 436 has been etched away and an adhesion layer 437 formed on the surfaces of the opening 436. Figure 4K shows the opening filled with a conductive material 438, such as tungsten, which electrically connects the gate 408 to the drain region 422. It is noted that the salicide is electrically conductive and the electrical contact is established through the salicide. Figure 4L shows an alternative embodiment wherein an opening etched in the dielectric layer 434 only exposes a portion of the drain region 422. The opening is filled with a conductive material such as tungsten. The electrical connection 440 to the drain region 422 connects the drain region 422 to another device or other devices in the same layer in the semiconductor device 400 or to another device or other devices in a different layer in the semiconductor device 400. The opening is coated with an adhesion layer 442. Figures 5A-5J show the structure and selected steps in a method of making a semiconductor device 500 in accordance with the present invention that docs not have salicide layers. Like numerical designations are used in each of the figures for like elements. Like numerical designations are used in each of the Figures 5A-5J for like elements shown in Figures 4A-4L. Figure 5A shows a portion of the semiconductor device 500 manufactured on the semiconductor substrate 402 with trench isolation regions 504 and 506. The trench isolation regions 504 and 506 can also be field oxide regions formed by a LOCOS process. The purpose of the trench isolation or the field oxide regions is to isolate an element from an adjacent region. The semiconductor device 500 has a gate 508, typically a polysilicon gate, separated from the semiconductor substrate by a gate oxide layer 510 with sidewall spacers 512 and 514 formed on each side of the gate 508. Lightly doped drain regions 516 and 518 are formed in the semiconductor substrate 402. The LDD regions are typically formed as described above. The formation of the LDD regions is typically done before the formation of the sidewall spacers. Ions that can be used to form LDD regions are phosphorous ions at a dosage of about 1 El 3 ions per centimeter squared. Figure 5B shows the semiconductor device 500 shown in Figure 5A with a source region 520 and a drain region 522 formed in the semiconductor substrate 502. The formation of the source and drain regions 520 and 522 is typically done by ion implantation of appropriate ions and is well known in the semiconductor manufacturing art and will not be discussed. The concentration of the implanted ions in the source and drain regions 520 and 522 is greater than the concentration of the implanted ions in the LDD regions 516 and 518 and thus, the LDD regions 516 and 518 are shown subsumed by the source and drain regions 520 and 522. Ions that are typically implanted into the source and drain regions 516 and 518 are arsenic ions at a dosage of about 1 El 5 ions per centimeter squared. Figure 5C shows the device 500 with a hydrogen getter layer 424 formed over the entire surface of the device 500. The hydrogen getter layer 424 formed over the device 500 is the same hydrogen getter layer 424 that is formed over the device 400 discussed in conjunction with Figures 4A-4I. As discussed above, the hydrogen getter layer 424 is a film such as a PSG (phosphosilicate glass) film, a BPSG (borophosphosilicate glass) film, a PTEOS (phosphorus doped tetraethyl orthosilicate) deposited oxide film, or a BPTEOS (borophosphorus doped tetraethyl orthosilicate) deposited oxide film. The hydrogen getter layer 424 typically has a thickness between 1000-2000 Angstroms. The purpose of the hydrogen getter layer 424 is to getter hydrogen and protect underlying areas from forming salicide layers in subsequent processing steps. Figure 5D shows etch protect layer 523 formed on the device 500 to protect the hydrogen getter layer 424 from being removed. Figure 5E shows the device 500 with the protect layer 523 removed and a barrier layer 432 formed on the device 500. The barrier layer 432 is formed on the entire device. The barrier layer 432 as described above is a high temperature plasma silicon nitride or silicon oxynitride or an LPCVD silicon nitride film. The barrier layer 432 is used to protect underlying features of the device 500 from the typical etch materials used to etch silicon dioxide. The arrows 519 indicate the phosphorus ions that are implanted in the entire semiconductor device. Figure 5F shows the device 500 with a dielectric layer 434 that has been formed on the entire semiconductor device as well as the semiconductor device 500. Figure 5G shows the dielectric layer 434 planarized and an opening, indicated at 536. etched to expose a selected portion of the underlying device. The purpose of the dielectric material 434 is to electrically insulate the underlying portions of the device 500 from other elements that may be manufactured above the dielectric layer 434. The purpose of the opening 536 is to allow an electrical connection to the exposed portion of the underlying portion of the device 500. Figure 5H shows that the portion of the barrier layer 432 exposed by the opening 536 has been etched away and an adhesion layer 537 formed on the surfaces of the opening 536. Figure 51 shows the opening 536 filled with a conductive material 538, such as tungsten, which electrically connects the gate 508 to the drain region 522. Figure 5J shows an alternative embodiment with an electrical connection 540 that is to connect the drain region 522 to another device either on the same layer or on a different layer. The electrical connection 540 is formed by the method described above, that is, by etching an opening in the dielectric layer 434, forming an adhesion layer 539, and filling the opening with a conductive material, such as tungsten. Figure 6 is a diagram showing experimental test results of various dosages of implanted phosphorus at various implant energies. The data clearly shows that increasing the dosage levels of phosphorus decreases the delta VTE (V) where VTE (V) is a measure of the number of electrons on a floating gate and delta VTE (V) is a measure of the change of the number of electrons on a floating gate (and is therefore a measure of the loss of charge from the floating gate). The ideal delta VTE (V) would be zero and the devices which have the lowest delta VTE (V) are the preferable devices. It can clearly be observed from the data shown in Figure 6 that a device with no implant, indicated at 600, loses a substantial amount of charge. The data indicates that after 60 hours in a temperature of 250 degrees Centigrade, the delta VTE (V) is 1 volt. The device with an implant of phosphorus ions at a dosage of 1 El 6 ions per centimeter squared at an implantation energy of 35 KeV, indicated at 602, has a delta VTE (V) of approximately .35 volts under the same test conditions. The foregoing description of the embodiments of the invention has been presented for purposes of illustration and description. It is not intended to be exhaustive or to limit the invention to the precise form disclosed. Obvious modifications or variations are possible in light of the above teachings. The embodiments were chosen and described to provide the best illustration of the principles of the invention and its practical application to thereby enable one of ordinary skill in the art to utilize the invention in various embodiments and with various modifications as are suited to the particular use contemplated. All such modifications and variations are within the scope of the invention as determined by the appended claims when interpreted in accordance with the breadth to which they are fairly, legally, and equitably entitled.

Claims: CLAIMS What we claim: 1. A semiconductor device, comprising: a first type of device (400) formed in a semiconductor substrate (402); a barrier layer (432) formed on the semiconductor device, wherein the barrier (432) layer is a film selected from the group of a high temperature PECVD nitride film, a high temperature PECVD oxynitride film and a high temperature LPCVD nitride film; and phosphorus ions (429) implanted in the barrier layer (432). 2. The semiconductor device of Claim 1, wherein the phosphorus ions (429) are implanted at a dosage in the range of 1E14 to 5E16 ions per centimeter squared. 3. The semiconductor device of Claim 2, wherein the phosphorus ions (429) are implanted with an implantation energy in the range of 20 KeV to 80 KeV. 4. The semiconductor device of Claim 1, wherein the phosphorus ions (429) are implanted at a dosage of approximately 1E16 ions per centimeter squared and at an implantation energy of approximately 35 KeV. 5. The semiconductor device of Claim 1, further comprising a hydrogen getter (424) layer formed under the barrier layer. 6. The semiconductor device of Claim 5, wherein the hydrogen getter layer (424) is a P-doped film. 7. The semiconductor device of Claim 6, wherein the P-doped film has a thickness of approximately 1000-2000 Angstroms. 8. The semiconductor device of Claim 7, wherein the hydrogen getter layer (424) comprises a material selected from the group of a PSG film, a BPSG film, a PTEOS deposited oxide film and a BPTEOS deposited oxide film. 9. The semiconductor device of Claim 8, wherein the device formed in the semiconductor substrate is a nonvolatile memory device having a floating gate. 10. The semiconductor device of Claim 9, further comprising a program junction formed in the semiconductor substrate underlying the nonvolatile memory device. 1 1. The semiconductor device of Claim 8, wherein the device formed in the semiconductor substrate is a MOSFET. 12. The semiconductor device of Claim 1 1, further comprising LDD regions (416, 418) formed in the semiconductor substrate. 13. The semiconductor device of Claim 12, further comprising a source region (420) and a drain region (422) formed in the semiconductor substrate. 14. The semiconductor device of Claim 13, further comprising a tungsten damascene interconnect (438) electrically connecting a first element (408) of the MOSFET with a second element (422) of the MOSFET. 15. The semiconductor device of Claim 14, further comprising a dielectric layer (434) formed over the barrier layer (432). 16. The semiconductor device of Claim 15, further comprising an opening (436) formed in the dielectric layer (434) exposing a portion of the gate (408) and a portion of one of either the drain (422) or source regions (420) and wherein an adhesion layer (437) is formed in the opening (436) and the opening is filled with tungsten. 17. The semiconductor device of Claim 16, further comprising a salicide layer (428) formed on the gate region. 18. The semiconductor device of Claim 17, further comprising salicide layers (430, 426) formed on the drain (422) and source regions (420). 19. A method of manufacturing a semiconductor device, the method comprising: forming a first type of device in a semiconductor substrate (402); forming a barrier layer (432) on the semiconductor device wherein the barrier layer is a film selected from the group of a high temperature PECVD nitride film, a high temperature PECVD oxynitride film and a high temperature LPCVD nitride film; and implanting phosphorus ions (429) in the barrier layer (432). 20. The method of Claim 19, wherein the phosphorus ions (429) are implanted at a dosage in the range of 1 El 4 to 5E16 ions per centimeter squared. 21. The method of Claim 20, wherein the phosphorus ions (429) are implanted at an implantation energy in the range of 20 KeV to 80 KeV. 22. The method of Claim 19, wherein the phosphorus ions (429) are implanted at a dosage of approximately 1E16 ions per centimeter squared at an implantation energy of approximately 35 KeV. 23. The method of Claim 19, further comprising forming a hydrogen getter layer (424) under the barrier layer (432). 24. The method of Claim 23, wherein forming a hydrogen getter layer (424) comprises forming a P-doped film. 25. The method of Claim 24, wherein forming a P-doped film comprises forming a P-doped film having a thickness of approximately 1000-2000 Angstroms. 26. The method of Claim 25, wherein forming a P-doped film comprises forming a P-doped film selected from the group of a PSG film, a BPSG film, a PTEOS deposited oxide film, and a BPTEOS deposited film. 27. The method of Claim 26, further comprising forming a dielectric layer (434) over the barrier layer (432). 28. The method of Claim 27, further comprising forming an opening (436) in the dielectric layer (434) exposing a portion of a first element (408) and a portion of a second element (422). 29. The method of Claim 28, further comprising forming an adhesion layer (437) in the opening (436) in the dielectric layer (434). 30. The method of Claim 29, further comprising filling the opening with tungsten thereby electrically connecting the first element (408) and the second element (422).

Inventors: MEHTA SUNIL D, NG CHE-HOO, MEHTA, SUNIL, D., NG, CHE-HOO
Applicants: ADVANCED MICRO DEVICES INC, ADVANCED MICRO DEVICES, INC.
Application year: 1998
Main classification: H01L21
IPC codes: H01L21, H01L27, H01L29