OLEFIN PURIFICATION BY ADSORPTION OF ACETYLENICS AND REGENERATION OF ADSORBENT

Abstract: Processes using heterogeneous adsorbents are disclosed for purification of olefins such as are typically produced by thermal cracking of suitable hydrocarbon feedstocks, by passing a steam of olefin having from 2 to about 8 carbon atoms, containing acetylenic impurities having the same or similar carbon content, and optionally saturated hydrocarbon gases, through a particulate bed of adsorbent comprising predominantly a support material having high surface area on which is dispersed at least one metallic element. Adsorption is carried out in an essentially dihydrogen-free atmosphere within the bed, selective and reversible adsorption and/or complexing of the contained acetylenic contaminants with the adsorbent, and thereby obtain purified effluent which contains less than a predetermined level of the acetylenic impurities. Selective and reversible adsorption and/or complexing of the contained acetylenic impurities with the adsorbent is continued until levels of acetylenic impurities in the effluent stream increase to a predetermined level. Thereafter the resulting bed of adsorbent is regenerated in the presence of a reducing gas containing dihydrogen to effect release of the contained acetylenic impurities from the adsorbent.

Description: OLEFIN PURIFICATION BY ADSORPTION OF ACETYLENICS AND REGENERATION OF ADSORBENT CROSS-REFERENCE TO RELATED APPLICATION This application claims the benefit of U.S. Provisional Application Number 60/040,383 filed March 10, 1997, and U.S. Provisional Application Number 60/046,339 filed May 13, 1997, which applications are specifically incorporated herein, in their entirety, by reference. HELD OF THE INVENTION The field of this invention relates to use of heterogeneous adsorbents in purification of relatively impure olefins such as are typically produced by thermal cracking of suitable hydrocarbon feedstocks. More particularly, this invention concerns purification by passing an olefϊnic process stream, containing small amounts of acetylenic impurities, carbon oxides and/or other organic components which are, typically, impurities in cracked gas, through a particulate bed of heterogeneous adsorbent comprising a metal supported on a high surface area carrier, under conditions suitable for reversible adsorption of alkynes. Processes according to this invention are particularly useful where the olefin being purified is ethylene and/or propylene formed by thermal cracking of hydrocarbon feedstocks. BACKGROUND OF THE INVENTION As is well known, olefins, or alkenes, are a homologous series of hydrocarbon compounds characterized by having a double bond of four shared electrons between two carbon atoms. The simplest member of the series, ethylene, is the largest volume organic chemical produced today. Olefins including, importantly, ethylene, propylene and smaller amounts of butadiene, are converted to a multitude of intermediate and end products on a large scale, mainly polymeric materials. Commercial production of olefins is, almost exclusively, accomplished by pyrolysis of hydrocarbons in tubular reactor coils installed in externally fired heaters. Thermal cracking feed stocks include streams of ethane, propane or a hydrocarbon liquid ranging in boiling point from light straight-run gasoline through gas oil. Because of the very high temperatures employed, commercial olefin processes invariably coproduce significant amounts of acetylene and methyl acetylene. Required separation of the acetylene from the primary olefin can, considerably, increase the plant cost. In a typical ethylene plant the cracking represent about 25 percent of the cost of the unit while the compression, heating, dehydration, recovery and refrigeration sections represent the remaining about 75 percent of the total. This endothermic process is carried out in large pyrolysis furnaces with the expenditure of large quantities of heat which is provided in part by burning the methane produced in the cracking process. After cracking, the reactor effluent is put through a series of separation steps involving cryogenic separation of products such as ethylene and propylene. The total energy requirements for the process are thus very large and ways to reduce it are of substantial commercial interest. In addition, it is of interest to reduce the amount of methane and heavy fuel oils produced in the cracking processor to utilize it other than for its fuel value. Hydrocarbon cracking is carried out using a feed which is ethane, propane or a hydrocarbon liquid ranging in boiling point from light straight-run gasoline through gas oil. Ethane, propane, liquid naphthas, or mixtures thereof are preferred feed to a hydrocarbon cracking unit. Hydrocarbon cracking is, generally, carried out thermally in the presence of dilution steam in large cracking furnaces which are heated by burning, at least in part, methane and other waste gases from the olefins process resulting in large amounts of NOx pollutants. The hydrocarbon cracking process is very endothermic and requires large quantities of heat per pound of product. However, newer methods of processing hydrocarbons utilizes at least to some extent catalytic processes which are better able to be tuned to produce a particular product slate. The amount of steam used per pound of feed in the thermal process depends to some extent on the feed used and the product slate desired. Typically, steam pressures are in the range of about 30 lbs per sq in to about 80 lbs per sq in, and amounts of steam used are in the range of about 0.2 pounds of steam per pound of feed to 0.7 pounds of per pound of feed. The temperature, pressure and space velocity ranges used in thermal hydrocarbon cracking processes to some extent depend upon the feed used and the product slate desired which are well known as may be appreciated by one skilled in the art. The type of furnace used in the thermal cracking process is also well known. However the ceramic honeycomb furnace which is described in U.S. Patent. Number 4,926,001, the contents of which patent are specifically incorporated herein by reference, is an example of a new type of cracking which could have a special utility for this process. Several methods are known for separation of an organic gas containing unsaturated linkages from gaseous mixtures. These include, for instance, cryogenic distillation, liquid adsorption, membrane separation and the so called "pressure swing adsorption" in which adsorption occurs at a higher pressure than the pressure at which the adsorbent is regenerated. Cryogenic distillation and liquid adsorption are common techniques for separation carbon monoxide and alkenes from gaseous mixtures containing molecules of similar size, e.g., nitrogen or methane. However, both techniques have disadvantages such as high capital cost and high operating expenses. For example, liquid adsorption techniques suffer from solvent loss and need a complex solvent make-up and recovery system. Molecular sieves which selectively adsorb carbon monoxide from gaseous mixtures by chemisorption are also known. U.S. Patent Number 4,019,879 and U.S. Patent Number 4,034,065 refer to use of high silica zeolites, which have relatively high selectivities for carbon monoxide, in the pressure swing adsorption method. However, these zeolites only have moderate capacity for carbon monoxide and more particularly require very low vacuum pressures to recover the adsorbed gases and/or to regenerate the zeolite. U.S. Patent Number 4,717,398 describes a pressure swing adsorption process for selective adsorption and subsequent recovery of an organic gas containing unsaturated linkages from gaseous mixtures by passing the mixture over a zeolite ion- exchanged with cuprous ions (Cu I) characterized in that the zeolite has a faujasite type crystalline structure (Y). Kokai JP Number 50929 - 1968 describes a method of purifying vinyl compounds containing up to about 10 percent by weight of acetylene compounds including ethyl acetylene, vinyl acetylene and phenyl acetylene whereby the acetylene compounds are adsorbed in an adsorption agent of 1-valent and/or 0-valent copper and/or silver supported on inert carrier such as δ-alumina, silica or active carbon. However, it is well known that acetylene and these acetylene compounds react with copper and/or silver to from copper acetylide or silver acetylide. Both the acetylide of copper and silver are unstable compounds. Because they are explosive under some conditions their possible formation presents safety problems in operation and in handling adsorbent containing such precipitates. More recently German Disclosure Document 2059794 describes a liquid adsorption process for purification of paraffinic, olefϊnic and/or aromatic hydrocarbons with an adsorption agent consisting in essence of a complex of a copper (Cu I)-salt with an alkanolamine such as monoethanolamine, monoisopropanolamine, diethanolamine, triethanolamine and arylalkanolmines, and optionally in the presence of a glycol or polyglycol. However, the product stream is contaminated with unacceptable levels of components of the such agents absorbed in the hydrocarbon flow. While such contamination might be removable using an additional bed of silica gel, aluminum oxide or a wide-pored molecular sieve, this would involve additional capital costs, operation expenses and perhaps safety problems. Olefin-paraffin separations represent a class of most important and also most costly separations in the chemical and petrochemical industry. Cryogenic distillation has been used for over 6Q years for these separations. They remain to be the most energy-intensive distillations because of the close relative volatilities. For example, ethane-ethylene separation is carried out at about -25°C and 320 pounds per square inch gage pressure (psig) in a column containing over 100 trays, and propane-propylene separation is performed by an equally energy-intensive distillation at about -30°C and 30 psig. Impurity refers to compounds that are present in the olefin plant feedstocks and products. Well-defined target levels exist for impurities. Common impurities in ethylene and propylene include: acetylene, methyl acetylene, methane, ethane, propane, propadiene, and carbon dioxide. Listed below are the mole weight and atmospheric boiling points for the light products from thermal cracking and some common compounds potentially found in an olefins unit. Included are some compounds which have similar boiling temperatures to cracked products and may be present in feedstocks or produced in trace amounts during thermal cracking. Mole Normal Boiling Compound Weight Point, °C Hydrogen 2.016 -252.8 Nitrogen 28.013 - 195.8 Carbon monoxide 28.010 - 191.5 Oxygen 31.999 -183.0 Methane 16.043 -161.5 Ethylene 28.054 - 103.8 Ethane 30.070 -88.7 Phosphine 33.970 -87.4 Acetylene * 26.038 -84.0 Carbon dioxide * 44.010 -78.5 Radon 222.00 -61.8 Hydrogen sulfide 34.080 -60.4 Arsine 77.910 -55.0 Carbonyl sulfide 60.070 -50.3 Propylene 42.081 -47.8 Propane 44.097 -42.1 Propadiene (PD) 40.065 -34.5 Cyclo-propane 42.081 -32.8 Methyl acetylene 40.065 -23.2 Water 18.015 100. * Sublimation temperature Recently the trend in the hydrocarbon processing industry is to reduce commercially acceptable levels of impurities in major olefin product streams, i.e., ethylene, propylene, and hydrogen. Need for purity improvements is directly related to increasing use of higher activity catalysts for production of polyethylene and proypropylene, and to a limited extent other olefin derivatives. It is known that acetylenic impurities can be selectively hydrogenated and thereby removed from such product streams by passing the product stream over an acetylene hydrogenation catalyst in the presence of dihydrogen (molecular hydrogen, H 2)- However, these hydrogenation processes typically result in the deposition of carbonaceous residues or "green oil" on the catalyst which deactivates the catalyst. Therefore, acetylene hydrogenation processes for treating liquid or liquefiable olefins and diolefins typically include an oxygenation step or a "burn" step to remove the deactivating carbonaceous residues from the catalyst followed by a hydrogen reduction step to reactivate the hydrogenation catalyst. For example, see U.S. Patent Number 3,755,488 to Johnson et al., U.S. Patent Number 3,792,981 to Hettick et al., U.S. Patent Number 3,812,057 to Morgan and U.S. Patent Number 4,425,255 to Toyoda. However, U.S. Patent Number 3,912,789 and U.S. Patent Number 5,332,705 state that by using selected hydrogenation catalysts containing palladium, at least partial regeneration can be accomplished using a hydrogenation step alone at high temperatures (600°F - 700°F) and in the absence of an oxygenation step. Selective hydrogenation of the about 2000 to 4000 parts per million of acetylenic impurities to ethylene is, generally, a crucial operation for purification of olefins produced by thermal steam cracking. Typical of a small class of commercially useful catalysts are materials containing very low levels of an active metal supported on an inert carrier, for example a particulate bed having less than about 0.03 percent (300 ppm) palladium supported on the surface skin of carrier pellets having surface area of less than about 10 m^ /gm. Many commercial olefin plants using steam crackers use, generally, front-end acetylene converters, i.e., the hydrogenation unit is fed Q > and lighter cracked gas which feed has a high enough concentration of hydrogen to easily hydrogenate the acetylenic impurities, however, when run improperly, will also hydrogenate a large fraction of the ethylene and propylene product. Both hydrogenation of acetylene and ethylene are highly exothermic as shown below: C 2 H 2 +H 2 — > C2 H 4 H = -41 kcal/mole C2 H 4 + H 2 — > C2 H 6 H = -32.7 kcal/mole Accelerated catalyst deactivation and thermal runaways caused by loss in catalyst selectivity are common problems which plague acetylene converters. Such problems result in unscheduled shutdowns and increased costs to replace deactivated catalyst. The problem of over-hydrogenation is aggravated because the rate constant for ethylene hydrogenation to ethane is 100 times faster than for the hydrogenation of acetylene to ethylene. As a means to avoid a C 2 H 4 hydrogenation thermal runaway, acetylene, carbon monoxide and diolefins concentrations must, therefore, be high enough to cover most active sites so none are left to adsorb ethylene. For example, acetylene, carbon monoxide, methyl acetylene, and propadiene have bond strengths to palladium which are stronger than the ethylene to palladium bonds. Selection of active metal, size of the metal particles and other physical and chemical factors ultimately affect the "operating temperature window" which is the delta of temperature between acetylene conversion to ethylene (typically in a range from about 100°F to about 150°F) and thermal runaway where all molecular hydrogen is converted and a large amount of the ethylene is converted to ethane (about 170°F to about 225°F). The wider the window, the safer is operation of the unit. It is therefore a general object of the present invention to provide an improved process which overcomes the aforesaid problem of prior art methods, for production of olefins from thermal cracking of hydrocarbon feed stocks which olefin can be used for manufacture of polymeric materials using higher activity catalysts. More particularly, it is an object of the present invention to provide an improved method for purification of ethylene and/or propylene containing small amounts of acetylenic impurities, carbon oxides and/or other organic components that are impurities in olefϊnic process streams, by passing the impure olefin stream through a particulate bed of heterogeneous adsorbent comprising a metal supported on a high surface area carrier, under conditions suitable for reversible adsorption of alkynes impurities. It is another object of the present invention to provide an improved aforesaid purification method that employs an adsorbent that, even after a substantial period of aging, exhibits ability to withstand repeated regenerations and yet retain useful adsorption capacity. It is further an object of this invention to provide an improved process for regeneration of adsorbent loaded with acetylenic impurities. Other objects and advantages of the invention will become apparent upon reading the following detailed description and appended claims. SUMMARY OF THE INVENTION Economical processes are disclosed for purification of a relatively impure olefins produced by thermal cracking of hydrocarbons. Processes of this invention comprise passing a gaseous mixture comprising an olefin of from 2 to about 8 carbon atoms, acetylenic and diolefin impurities having the same or similar carbon content and optionally saturated hydrocarbon gases through a particulate bed of adsorbent comprising predominantly a support material having high surface area on which is dispersed at least one metallic element selected from the group consisting of chromium, iron, cobalt, nickel, ruthenium, palladium, and platinum, to effect, in the presence of and essentially dihydrogen-free atmosphere within the bed, selective and reversible adsorption and/or complexing of the contained acetylenic contaminants with the adsorbent, and thereby obtain purified effluent which contains less than a predetermined level of the acetylenic impurities; and thereafter regenerating the resulting bed of adsorbent in the presence of a reducing gas comprising dihydrogen (molecular hydrogen) to effect release of the contained acetylenic impurities from the adsorbent. Another aspect of special significance is the separation of acetylenic impurities from ethylene or propylene containing small amounts of acetylene, i.e., less than about 5000 parts per million by weight of one or more acetylenic impurities, and provide, advantageously, purified product containing less than about 1 parts per million by weight, and frequently even less than about 0.5 parts per million by weight. In yet another aspect the invention is a process for purification of olefins produced by thermal cracking of hydrocarbons which comprises: passing a gaseous mixture comprising at least about 99 percent by volume of an olefin having two to about four carbon atoms, and acetylenic impurities having the same or similar carbon content in an amount in a range upward from about 1 to about 1000 parts per million by volume, through a particulate bed of adsorbent comprising predominantly a support material selected from the group alumina, silica, active carbon, clay and zeolites having surface area in a range of from about 10 to about 2,000 square meters per gram as measured by the BET gas adsorption method, on which is dispersed at least one metallic element selected from the group consisting of iron, cobalt, nickel, zinc, ruthenium, palladium, platinum, and potassium, to provide an effluent stream from the bed; effecting, in the presence of and essentially dihydrogen-free atmosphere within the bed, selective and reversible adsorption and/or complexing of the contained acetylenic impurities with the adsorbent, until levels of the acetylenic impurities in the effluent stream increase to a predetermined level in a range downward from about 1 parts per million by volume; and thereafter regenerating the resulting bed of adsorbent in the presence of a reducing gas, preferably comprising dihydrogen, to effect release of the contained acetylenic impurities from the adsorbent. A preferred class of adsorbents useful in processes according the invention, comprises at least about 90 weight percent of a gamma alumina having surface area in a range of from about 80 to about 500 square meters per gram as measured by the BET gas adsorption method, and contains less than 500 parts per million by weight of a sulfur-containing component, calculated as elemental sulfur. More preferred are the adsorbent which comprises at least about 90 weight percent of a gamma alumina having surface area in a range of from about 150 to about 350 square meters per gram as measured by the BET gas adsorption method, and wherein the metal dispersed on the support material is palladium, and the absorbent has a palladium content in a range of from about 0.01 to about 10 percent based on the total weight of the adsorbent. For a more complete understanding of the present invention, reference should now be made to the embodiments illustrated in greater detail in the accompanying drawing and described below by way of examples of the invention. BRIEF DESCRIPTION OF THE FIGURE The appended claims set forth those novel features which characterize the present invention. The present invention itself, as well as advantages thereof, may best be understood, however, by reference to the following brief description of preferred embodiments taken in conjunction with the annexed drawing, in which: The FIGURE is a schematic diagram of a preferred method for operating the process of this invention in the continuous mode being arranged to provide sufficient reactants for the reactions and to maintain suitable reaction temperatures in accordance with the present invention. BRIEF DESCRIPTION OF THE INVENTION Processes of this invention are particularly suitable for use in purification of aliphatically unsaturated organic compounds produced, generally, by thermal cracking of hydrocarbons. Aliphatically unsaturated compounds of most interest with regard to purification by the method of the present invention, have two to about eight carbon atoms, preferably two to about four carbon atoms, and more preferably ethylene or propylene. The separation of acetylenic impurities from ethylene or propylene which may be contained in admixtures with other normally gaseous materials, such as one or more of ethane, methane, propane and oxides of carbon is of particular importance. For example mixtures serving as a source of ethylene containing feed for the process may contain about 1 to about 99 weight percent ethylene, about 0 to about 50 weight percent ethane and/or about 0 to about 50 weight percent methane. Generally acetylenic impurities described in this invention are expressed by the formula R - C = CH where R is hydrogen or a hydrocarbon group of up to 10 carbon atoms. It is desirable to treat the gaseous mixture used in the process of the present invention to remove any gaseous hydrogen and or carbon monoxide. The amount of hydrogen in the gaseous mixture should suitably be reduced to below 10 parts per million by weight, preferably below 2 parts per million by weight and most preferably below 1 parts per million by weight, prior to contact with the adsorbent. Similarly, any mercury-containing, arsenic-containing, and sulfur-containing components, e.g., hydrogen sulfide, present in the gaseous mixture fed to the particulate bed of adsorbent should suitably be removed therefrom in any known manner in order to avoid the risk of poisoning the dispersed metal. The hydrocarbon mixture used in the process of the present invention is suitably a cracked gas from which the majority of the C5 and higher hydrocarbons have been removed. The gaseous mixture may thus comprise ethylene, propylene, butenes, methane, ethane, propane and butane. Small amounts of pentanes and pentenes can be tolerated in the gaseous mixture. In preferred embodiments of processes according to the invention, the olefin in the gaseous mixture being purified is predominantly ethylene or propylene, the gaseous mixture contains less than about 0.5 parts per million by volume of hydrogen and less than about 1 parts per million by volume of mercury-containing, arsenic-containing, and sulfur-containing components, each calculated as the element, and wherein the gaseous mixture, while passing through the bed, is at temperatures in a range upward from about - 78°C to about 100°C, preferably in a range of from about - 35°C to about 65°C, and more preferably in a range of from about - 10°C to about 55°C. The gaseous mixture used in the process of the present invention may also comprise water and may optionally be saturated with water. Broadly, according to the present invention, there is provided a particulate bed of adsorbent comprising predominantly a support material having high surface area on which is dispersed at least one metallic element selected from the group consisting of chromium, iron, cobalt, nickel, ruthenium, palladium, and platinum. Suitable adsorbents exhibit, in the presence of an essentially dihydrogen-free atmosphere within the bed, selective and reversible adsorption and/or complexing of the acetylenic impurities with the adsorbent. According to the present invention dispersed metal content is in a range of from about 0.01 to about 40 percent based on the total weight of the adsorbent. Preferably dispersed metal content is in a range of from about 0.01 to about 20 percent based on the total weight of the adsorbent. The adsorbent can, optionally, further comprise one or more elements selected from the group consisting of lithium, sodium, potassium, zinc, molybdenum, tin, tungsten, and iridium, dispersed on the support material. Preferably the adsorbent further comprises a member selected from the group consisting of lithium, sodium, potassium, zinc, molybdenum, and tin dispersed on the support material. For processes according to invention the metal dispersed on the support material is, advantageously, at least one element selected from the group consisting of iron, cobalt, nickel, and palladium and the absorbent has a dispersed metal content in a range of from about 0.05 to about 20 percent based on the total weight of the adsorbent. Another class adsorbents useful for processes according to invention comprises a dispersion of copper or silver and one metallic element selected from the group consisting of chromium, iron, cobalt, nickel, ruthenium, palladium, and platinum, preferably palladium. More preferred for processes according to this invention are adsorbents having palladium metal dispersed on the support, and the absorbent has a palladium content in a range of from about 0.05 to about 10 percent, more preferred palladium content in a range of from about 0.1 to about 5.0 percent based on the total weight of the adsorbent. High metal dispersion and loading resulted in higher metal surface area. Capacity of an adsorbent is, typically, related directly to metal surface area. Any method which increases and/or maintains high metal surface area is, therefore, beneficial to achieving high acetylene adsorption capacity. Preferred for processes according to this invention are adsorbents having a dispersion value of at least about 10 percent, preferably in a range upward from about 20 percent to about 80 percent. Dispersion is a measure of the accessibility of the active metals on the adsorbent. Such dispersion methods are discussed in H. C. Gruber's, Analytical Chemistry, Vol. 13, p. 1828, (1962). The absorbents for use in this invention were analyzed for dispersion using a pulsed carbon monoxide technique as described in more detail in the Examples. Palladium containing adsorbents having large dispersion values are desired because more of the palladium metal is available for reaction. Support materials are, advantageously, selected from the group consisting of alumina, silica, carbon, clay and zeolites (molecular sieves). Surface areas of support materials are, preferably, in a range of from about 10 to about 2,000 square meters per gram as measured by the BET gas adsorption method. A preferred class of active carbons useful herein are materials disclosed in commonly assigned U.S. Patent No. 4,082,694 to Arnold N. Wennerberg and Thomas M. O'Grady, which patent is incorporated herein by reference. Such suitable active carbon products are produced from carbonaceous material by a staged temperature process which provides improved yield and processability during manufacture. A source of carbonaceous material, such as crushed coal, coal coke, petroleum coke or a mixture thereof, is heated with agitation in the presence of a substantial weight ratio of potassium hydroxide at a first lower temperature to dehydrate the combination. Thereafter the temperature is raised to a second higher temperature to activate the combination which is thereafter cooled and washed to remove inorganic matter and form a high surface area active carbon having a cage-like structure exhibiting micro-porosity, good bulk density and Total Organic Carbon Index. Active carbon products for use as supports according to this invention have, preferably, an effective surface area greater than about 2,300 square meters per gram and, more preferably, greater than about 2,700 square meters per gram and, most preferably, above about 3,000 square meters per gram as measured by the BET method. Active carbon products for use as supports have, typically, a bulk density greater than about twenty- five hundredths grams per cubic centimeter and, preferably greater than about twenty-seven hundredths grams per cubic centimeter and, more preferably, above about . three- tenths gram per cubic centimeter. Further, useful active carbon products preferably have a Total Organic Carbon Index greater than about 300, more preferably, greater than about 500 and, most preferably, greater than about 700. Generally, the term "molecular sieve" includes a wide variety of positive-ion-containing crystalline materials of both natural and synthetic varieties. They are generally characterized as crystalline aluminosilicates, although other crystalline materials are included in the broad definition. The crystalline aluminosilicates are made up of networks of tetrahedra of Siθ4 and AIO4 moieties in which the silicon and aluminum atoms are cross-linked by the sharing of oxygen atoms. The electrovalence of the aluminum atom is balanced by the use of positive ions, for example, alkali-metal or alkaline-earth-metal cations. Zeolitic materials, both natural and synthetic, useful herein have been demonstrated in the past to have catalytic capabilities for many hydrocarbon processes. Zeolitic materials, often referred to as molecular sieves, are ordered porous crystalline aluminosilicates having a definite structure with large and small cavities interconnected by channels. The cavities and channels throughout the crystalline material are generally uniform in size allowing selective separation of hydrocarbons. Consequently, these materials in many instances have come to be classified in the art as molecular sieves and are utilized, in addition to the selective adsorptive processes, for certain catalytic properties. The catalytic properties of these materials are also affected, to some extent, by the size of the molecules which are allowed selectively to penetrate the crystal structure, presumably to be contacted with active catalytic sites within the ordered structure of these materials. In the past various molecular sieve compositions natural and synthetic have been found to be useful for a number of hydrocarbon conversion reactions. Among these are alkylation, aromatization, dehydrogenation and isomerization. Among the sieves which have been used are Type A, X, Y and those of the MFI crystal structure, as shown in "Atlas of Zeolite Structure Types," Second Revised Edition 1987, published on behalf of the Structure Commission of the International Zeolite Associates and incorporated by reference herein. Representative of the last group are ZSM-5 and AMS borosilicate molecular sieves. Prior art developments have resulted in the formation of many synthetic crystalline materials. Crystalline aluminosilicates are the most prevalent and, as described in the patent literature and in the published journals, are designated by letters or other convenient symbols. Exemplary of these materials are Zeolite A (Milton, in U.S. Pat. No. 2,882,243), Zeolite X (Milton, in U.S. Pat. No. 2,882,244), Zeolite Y(Breck, in U.S. Pat. No. 3,130,007), Zeolite ZSM-5 (Argauer, et al., in U.S. Pat. No. 3,702,886), Zeolite ZSM- II (Chu, in U.S. Pat. No. 3,709,979), Zeolite ZSM- 12 (Rosinski, et al., in U.S. Pat. No. 3.832,449), and others. Manufacture of the ZSM materials utilizes a mixed base system in which sodium aluminate and a silicon containing material are mixed together with sodium hydroxide and an organic base, such as tetrapropylammonium hydroxide and tetrapropylammonium bromide, under specified reaction conditions, to form the crystalline aluminosilicate, preferably a crystalline metallosilicate exhibiting the MFI crystal structure. A preferred class of molecular sieves useful, according to the present invention, are crystalline borosilicate molecular sieves disclosed in commonly assigned U.S. Patent No. 4,268,420, U.S. Patent No. 4,269,813, U.S. Patent No. 4,292,457, and U.S. Patent No. 4,292,458 to Marvin R Klotz, which are incorporated herein by reference. BRIEF DESCRIPTION OF PREFERRED EMBODIMENTS OF THE INVENTION While this invention is susceptible of embodiment in many different forms, this specification and accompanying drawing disclose only some specific forms as an example of the use of the invention. In particular, preferred embodiments of the invention for purification of a gaseous mixture comprising olefin preferably an olefin of from two to about eight carbon atoms having a single double bond, acetylenic impurities having the same or similar carbon content and optionally alkanes (paraffin hydrocarbons) and/or alkenes having more than one double bond (di- or tri- olefϊn hydrocarbons) produced by thermal cracking of hydrocarbons are illustrated and described. The invention is not intended to be limited to the embodiments so described, and the scope of the invention will be pointed out in the appended claims. The apparatus of this invention is used with certain conventional components the details of which , although not fully illustrated or described, will be apparent to those having skill in the art and an understanding of the necessary function of such components. More specifically with reference to the FIGURE, which illustrates an integrated olefin purification system including: one or more optional heat exchangers for controlling temperature of the gaseous feedstream to temperatures in a range from about -20°F to about 200°F, illustrated as feed exchanger 20 ; adsorption vessels containing particulate beds of a suitable solid adsorbent, illustrated as vessels 40 and 60 ; and means for analysis of feed and effluent streams, illustrated as on-line analytical system 80. During operation of the integrated olefin purification system, a gaseous mixture containing less than about 500 parts per million by weight of the acetylene and carbon monoxide impurities formed by chemical conversions in commercial thermal cracking processes, is, for example ethylene fed from the overhead of a C2 distillation tower or intermediate storage (not shown) through conduit 22 and into feed exchanger 20 to control temperature during adsorption. Effluent from feed exchanger 20 flows through, manifold 21 and, alternately, through valve 24 and manifold 42 or valve 26 and manifold 62 into one of two adsorption vessels 40 and 60 which contain beds of a suitable solid adsorbent, such as gamma alumina with 1.0 percent palladium based upon the weight of adsorbent. During operation the gaseous mixture passes though the bed of particulate adsorbent at gas hourly space velocities in a range of from about 0.05 hours- 1 to about 20,000 hours - 1 and even higher, preferably from about 0.5 hours- 1 to about 10,000 hours - 1 . Compositions of the gaseous feed and effluent of each adsorption vessel is monitored by on-line analytical system 80. While levels of acetylenic impurities in the effluent of the adsorption vessel in purification service are in a range downward from a predetermined level, purified olefin from adsorption vessel 40 and/or adsorption vessel 60 flows through manifold 41 , and valve 43 and/or manifold 61 and valve 63 , and through manifold 71 directly to pipeline for transportation of polymer grade ethylene, or to storage (not shown). When the level of acetylenic impurities in the effluent of an adsorption vessel in purification service reaches or exceeds the predetermined level, purified olefin flowing through manifold 71 is diverted to flare (not shown) while that adsorption vessel is isolated from the process flow by means of valve 24 and valve 43 , or valve 26 and 63 , and thereafter the resulting bed of loaded adsorbent is treated to effect release of the contained acetylenic impurities from the adsorbent by hydrogenation. Suitable absorbents have capacity to treat from about 300 to about 40,000 pounds of olefin feed per pound of adsorbent where the olefin feed contains about 0.5 parts per million (ppm) acetylene. Approximately 5 x 10-4 pounds of acetylene to about 1 x 10-2 pounds are, advantageously, adsorbed per pound of adsorbent before regeneration is required. During continuous operation of this embodiment, the time required for treating, alternately, of the loaded adsorbent to effect release of the contained acetylenic impurities from the adsorbent by hydrogenation, is provided by using two (as shown) or more independent adsorption vessels containing beds. Regenerations are, advantageously, performed according to this invention in three steps. At the end of each bed's adsorption cycle, the adsorption vessel which contains the loaded bed, for example vessel 60 , is isolated from the process flow by means of valve 26 and valve 63. and depressured through manifold 62 , valve 64 , and manifold 51 to suitable disposal, for example, a flare (not shown). Alternatively, vessel 40 , is isolated from the process flow by means of valve 24 and valve 43. and depressured through manifold 42 , valve 44 , manifold 51 to disposal. During the first stage of regeneration dry inert gas, such as methane, ethane, or nitrogen which is, preferably, free of carbon oxides, unsaturated hydrocarbons and hydrogen is fed, from, for example a nitrogen gas supply system (not shown), through conduit 32 , valve 52 , and manifold 56 into exchanger 30 to control temperature during regeneration. Effluent from exchanger 30 flows through, manifold 31 and, alternately, through valve 38 and manifold 61 or valve 58 and manifold 41 into one of two adsorption vessels 40 and 60 thereby purging gaseous hydrocarbons therefrom to disposal through manifold 62 , valve 64 , manifold 51 , valve 74 , and conduit 75 , or through manifold 42 , valve 44, manifold 51 , valve 74 , and conduit 75 to disposal. During the second stage of regeneration a reducing gas stream containing, predominantly, hydrogen is fed, from, for example a hydrogen gas supply system (not shown), through conduit 34 , valve 54 , and manifold 56 into exchanger 30 to control temperature during regeneration. Effluent from exchanger 30 flows through, manifold 31 and, alternately, through valve 38 and manifold 61 or valve 58 and manifold 1 into one of two adsorption vessels 40 and 60 to hydrogenate acetylene contained in the bed to, preferably ethylene. Effluent from the adsorption vessel during hydrogenation flows therefrom to intermediate storage (not shown) through manifold 62 , valve 68 , and conduit 73 or through manifold 42 , valve 44 , manifold 51 , valve 66 and conduit 73. Where heating of the regeneration gas is desired, rates of temperature increase during the second stage of regeneration are, preferably, controlled to rates of less than about l l°C per minute (about 20°F per minute) while increasing temperature in the range of from about 4°C to about 200°C (about 40°F to about 400°F). Pressures of the hydrogen-rich reducing gas during the second stage of regeneration are, advantageously, in a range from about 5 psig to about 500 psig. While the reducing gas is flowing through the adsorbent bed, effluent gas composition is, periodically, monitored with gas analyzer 80. Second stage regeneration is complete when C2+ hydrocarbon levels in the effluent gas from the bed have been reduced to C2+ hydrocarbon levels in the feed. Third stage regeneration involves purging all gaseous hydrogen from the adsorption vessel with an inert gas, e.g. nitrogen with or without a saturated hydrocarbon gas such as methane or ethane, while the vessel is at temperatures in a range upward from about 140°F. This involves blocking in valve 54 and opening valve 52 to switch from hydrogen to inert gas flow through the vessel. After the effluent gas is free of hydrogen, the effluent is directed to flare through manifold 62 via valve 64 and 74 , or manifold 42 via valve 64 and valve 74. During this third stage of regeneration flow of inert gas, at or below ambient temperature and about 5 to about 100 psig, cools the vessel to about ambient temperature thereby completing the regeneration process. Surface area of adsorbents can be determined by the Brunaur-Emmett-Teller (BET) method or estimated by a simpler Point B method. Adsorption data for nitrogen at the liquid nitrogen temperature, 77 K, are usually used in both methods. The Brunaur-Emmett-Teller equation, which is well known in the art, is used to calculate the amount of nitrogen for mono-layer coverage. The surface area is taken as the area for mono-layer coverage based on the nitrogen molecular area, 16.2 square Angstroms, obtained by assuming liquid density and hexagonal close packing. In the Point B method, the initial point of the straight portion of the Type II isotherm is taken as the completion point for the mono-layer. The corresponding amount adsorbed multiplied by molecular area yields the surface area. Dispersion and surface area of active metal sites was determined by carbon monoxide chemisorption using a Pulse Chemisorb 2700 (Micromeritics). In this procedure, approximately 4 gram samples were purged with helium carrier gas, calcined in air at 500 °C for 1 hr, purged with helium, reduced in hydrogen at 500°C, purged with helium, and cooled to room temperature. The sample was treated with 49.5 percent carbon monoxide in helium and the dosed with 0.045 mL pulses of 49.5 percent carbon monoxide (CO), balance nitrogen, and the carbon monoxide uptake was measured by a thermal conductivity cell. Palladium dispersion values were calculated assuming one carbon monoxide molecule per palladium atom. Palladium loadings are weight percent palladium metal. In characterizing the pore volume, both total pore volume and its distribution over the pore diameter are needed. The total pore volume is usually determined by helium and mercury densities or displacements. Helium, because of its small atomic size and negligible adsorption, gives the total voids, whereas mercury does not penetrate into the pores at ambient pressure and gives inter-particle voids. The total pore volume equals the difference between the two voids. Palladium on a high-surface-area γ-A^Q is a preferred adsorbent for purification of olefins in accordance with this invention. In order to introduce palladium and/or other suitable metal ions on a high-surface-area γ-Al 2 0 3 , any known technique for monolayer dispersion can be employed. The phenomenon of spontaneous dispersion of metal oxides and salts in monolayer or submonolayer forms onto surfaces of inorganic supports with high surface areas has been studied extensively in the literature (e.g., Xie and Tang, 1990). EXAMPLES OF THE INVENTION The following Examples will serve to illustrate certain specific embodiments of the herein disclosed invention. These Examples should not, however, be construed as limiting the scope of the novel invention as there are many variations which may be made thereon without departing from the spirit of the disclosed invention, as those of skill in the art will recognize. Example 1 A 50 mL TEFLON-lined stainless steel pressure vessel was loaded with 31.99 gm of commercially available adsorbent (about 44 mL of 0.29 percent palladium on γ-Al 2 C^), and a centrally disposed thermocouple system to monitor bed temperatures. After this adsorption vessel was connected into a gas adsorption unit which provided required control of feed gases, temperatures, pressures, and analytical means, the adsorbent bed was run in the down-flow mode. Nitrogen was purged through the vessel before reducing the oxidized PdO/ γ-Al 2 0 3 adsorbent by heating to 195°C in a flow of hydrogen. Electrical heating tape wrapped around the vessel was used to supply heat needed during reduction at 75 psig with hydrogen flowrates of about 250 mL/min. After 2.5 hours hydrogen flow was replaced with nitrogen flow. The vessel was cooled to room temperature and immersed in a water recirculating bath to maintain temperature at about 20.5°C during the subsequent adsorption process. After analysis of the effluent gases showed that hydrogen had been purged from the vessel, pure ethylene (less than about 0.5 ppm acetylene) was introduced at flow rates of 280 to 300 mL/min from a supply at room temperature. Pure ethylene was allowed to flow through the vessel for 15 min after vessel pressure reached 110 psig, and thereafter the flow of pure ethylene was replaced with a feed mixture which contained 191 ppm acetylene in a balance of ethylene. During adsorption the flow rate of the acetylene/ethylene mixture was 110 mL/min and operating condition of temperature and pressure were controlled to 110 psig and 20.5°C. By periodical analysis of effluent gas using an on-line gas chromatograph, acetylene was detected (less than about 0.5 ppm acetylene) breaking through the bed of adsorbent after a total of 28 L (1 atm and 21°C) of feed gas was treated. In this example the adsorbent exhibited a capacity of about 0.12 mL of acetylene per mL of adsorbent. After flow of the acetylene/ethylene mixture was stopped, the vessel was depressured to 1 atm and nitrogen was purged through the vessel for about 15 min. The vessel was again wrapped in heating tape and heated to 150°C. Adsorbent was regenerated using pure hydrogen at a flow rate of 250 mL/min at 60 psig in about 13 hours. Comparative Example This comparative example is to illustrate the essential role of transition/noble metal in acetylene captation by use of a pure gamma alumina support without any dispersed transition/noble metal. This experiment was carried out using Alcoa F-200 alumina in the form of 1/8" spheres. Another 50 mL TEFLON- lined pressure vessel was loaded with 21.98 gm (31.5 mL) of the Alcoa F-200 alumina, and the vessel was connected into a gas adsorption unit as in Example 1. Nitrogen was purged through the vessel and alumina bed which were then heated to 170°C (about 338°F) with a flow of hydrogen. A pretreatment hydrogen reduction was run at 15 psig and hydrogen flow rate of about 250 mL/minute. After 3.5 hours the hydrogen pretreatment was stopped by replacing the hydrogen flow with nitrogen flow. The vessel was allowed to cool to about room temperature and then the vessel was immersed in a water recirculating bath to maintain a constant temperature of about 22°C (about 72°F). After nitrogen had purged all hydrogen from the vessel pure ethylene (< 0.5 ppm acetylene) was then introduced at a flow rate of from about 280 to about 300 mL/minute. After several minutes the ethylene pressure in the vessel was increased to 110 psig. Pure ethylene was allowed to flow through the vessel for another 90 minutes before switching to a gas feed mixture containing 191 ppm acetylene in a balance of ethylene. Flow rate of the acetylene/ethylene mix was 1 10 mL/minute and the vessel was at 110 psig and 22°C (about 72°F). Gas effluent compositions were taken periodically using an on- line gas chromatograph to determine when acetylene started breaking through the adsorbent bed. A least 17 ppm of acetylene was observed in the gas effluent after only 18 minutes had elapsed from the time the acetylene/ethylene flow was started. This means the alumina has virtually no captation capacity for acetylene (less than 0.01 mL of acetylene per mL of adsorbent) and that the acetylene captation observed in Example 1 was due to the palladium metal dispersed on the alumina support. Flow of the gas feed mixture was then stopped, the vessel was depressured to 1 atm and nitrogen was purged through the vessel for about 10 to about 15 minutes. Regeneration was then started by flowing pure hydrogen through the vessel at 120 psig, and 250 mL/minute for about 17 hours. Example 2 This example includes several adsorption cycles to illustrate critical roles of amount of active metal and its valence state on the carrier for acetylene absorption from a feed gas mixture containing less than 500 ppm acetylene in a balance of ethylene. Absorbent for this experiment was prepared by crushing, using a mortar and pestle, of 1/8 inch spheres of gamma alumina loaded with 14 percent by weight of NiO to particle sizes in the range of 8 on 14 mesh. Example 2 - Cycle A Another 50 mL Teflon-lined pressure vessel was loaded with 22.03 gm (31.6 mL) of the 14 percent NiO on gamma alumina, and the vessel was connected into a gas adsorption unit as in Example 1. Nitrogen was purged through the vessel and bed of adsorbent which were then heated to temperatures in the range of from 140°C to 250°C with a flow of hydrogen. A pretreatment hydrogen reduction was run at 55 psig and hydrogen flow rate of about 250 mL/minute. After 3 hours the hydrogen pretreatment was stopped by replacing the hydrogen flow with nitrogen flow. The vessel was allowed to cool to about room temperature and then the vessel was immersed in a water recirculating bath to maintain a constant temperature of about 21.5°C. After nitrogen had purged all hydrogen from the vessel pure ethylene (< 0.5 ppm acetylene) was then introduced at a flow rate of from about 280 to about 300 mL/minute. After several minutes the ethylene pressure in the vessel was increased to 110 psig. Pure ethylene was allowed to flow through the vessel for another 90 minutes before switching to a gas feed mixture containing 191 ppm acetylene in a balance of ethylene. Flow rate of the acetylene/ethylene feed mixture was 114.5 mL/minute and pressure in the vessel was at 103 psig. Effluent compositions were taken periodically using an on-line gas chromatograph to determine when acetylene started breaking through the adsorbent bed. Only 16 minutes after starting flow of acetylene/ethylene feed, acetylene was observed in the effluent at about 11 ppm. Therefore the NiO/alumina was not able to satisfactorily remove acetylene from the ethylene feed with the hydrogen reduction of only 3 hour. Example 2 - Cycle B Hydrocarbon flow was stopped, the vessel depressured to 1 atm and purged with nitrogen for 10 to 15 minutes. Another regeneration was then started by flowing pure hydrogen through the vessel at 65 psig, and 250 mL/minute. During this hydrogenation/regeneration the vessel was again at about 226°C. After about 16 hours of this treatment the vessel was cooled in a nitrogen purge. A second acetylene/ethylene adsorption was carried out in the same manor as the first adsorption described in this example. Acetylene was detected in effluent from the adsorbent bed by the very first on-line GC analysis indicating minimal acetylene adsorption capacity. Another 16 hour hydrogen reduction cycle was performed at 65 psig and 226°C. After stopping the hydrogen and purging nitrogen through the vessel, it was cooled to 9.5°C. A third acetylene/ethylene adsorption was carried out at 9.5°C and 100 psig. This time the Ni/Al 2 θ 3 adsorbent was able to remove all the acetylene from the ethylene feed that contained 243 ppm acetylene. The adsorption capacity was 0.0923 mL acetylene/mL of adsorbent. It should be noted that small amounts of butenes and butadiene were also observed in the effluent when the acetylene/ethylene mixture was flowed through the adsorbent bed. This is an indication that the 14 percent NiO on alumina adsorbent caused oligomerization of acetylene and thereby formed "green oil" or unsaturated polybutadiene type polymers. Green oil formation can not be tolerated where adsorbent is used to purify polymer-grade ethylene. Example 2 - Cycle C After a 14 hour regeneration using hydrogen at 65 psig, and temperatures varying from 200°Cto 268°Cthe adsorbent bed underwent another ethylene/acetylene adsorption cycle. The adsorbent bed was held at 21.8°C using a water recirculating bath, and the feed gas contained 243 ppm acetylene in ethylene. Feed gas pressure was 103 psig and the gas flow rate was 112.2 mL/minute. Acetylene did not break through the adsorbent bed until about 1.5 hour after the acetylene/ethylene feed flow was started. This corresponded to about 0.02 mL acetylene adsorbed per mL of adsorbent. During the adsorption cycle small amounts of butenes and butadiene were also detected in the effluent, indicating green oil was being formed using this 14 percent NiO on alumina adsorbent. Example 3 This example includes several adsorption cycles to illustrate critical roles of temperature and pressure on adsorbent capacity for acetylene absorption from a feed gas mixture containing less than 500 ppm acetylene in a balance of ethylene. These runs were conducted at various preselected temperatures and pressures using a Pd/Al θ 3 adsorbent and illustrated how significantly acetylene adsorption capacity was affected. The Pd/Al 2 θ 3 adsorbent (0.3 percent palladium by weight) was prepared as in Example 2. Temperature at which adsorption occurs is believed to have an effect on both the adsorption capacity and the extent of undesirable side reactions such as green oil formation or acetylene/ethylene decomposition. In six consecutive runs three adsorption temperatures were studied, 7.4°C, 22°C and 48.4°C. All other variables were held constant: including ethylene containing about 210 ppm acetylene, feed flow rate at 198 mL/min, pressure at 200 psig, and the same 43 mL bed of Pd/Al 2 O, adsorbent (0.23 percent palladium by weight). Between cycles the adsorbent was regenerated with tail gas containing about 21 percent hydrogen, 5 percent ethylene, 300 ppm carbon monoxide, and balance of methane) at 120°F (about 49°C), 80 psig, for several hours. TABLE 1. reports average acetylene adsorption capacity in units of mL acetylene adsorbed per mL of bed at the three temperature of adsorption. TABLE 1. Temperature, °C Capacity* 48.3 0.330 23.0 0.268 7.4 0.248 * Capacity in mL acetylene adsorbed per mL of bed Example 4 As this example illustrates, pressure has a minor effect on adsorption capacity of acetylene on another Pd/Al 2 C> 3 adsorbent (0.3 percent palladium by weight). Only a minimal increase in the adsorption capacity was observed with increasing gas pressure during the adsorption cycle. Six laboratory runs were carried out at three different pressures: 100, 200 and 300 psig. Two runs were done at each pressure to provide an average. All other variables were kept constant including ethylene feed containing 218 ppm acetylene temperature at 120°F, feed flow rate at 198 mL/min, and the same 44 mL (31.6 gms) bed of the Pd/Al 2 θ 3 adsorbent. Table 2. reports average acetylene adsorption capacity at the three pressures studied. There is a slight increase in acetylene adsorption capacity with increasing pressure. Data was also obtained using a larger unit connected to a polymer grade ethylene pipeline that operated at over 1800 psig. The adsorption capacity was between 0.0204 to 0.0215 lb acetylene/cu ft adsorbent which is similar to what was observed at about 300 psig in the laboratory apparatus. TABLE 2. Pressu: re, psig Capacity* 100 0.24 200 0.30 300 0.32 * Capacity in mL acetylene adsorbed per mL of bed Example 5 Pure hydrogen has been shown in the previous examples to work well in regenerating the acetylene- saturated Pd/Al θ 3 adsorbent. In a commercial olefins unit pure hydrogen is, however, a valued and limited stream. Tail gas which comprises 15 to 35 percent hydrogen, 0.1 to 5 percent ethylene, 100 to 500 ppm CO, and the balance methane, is more plentiful and less expensive relative to pure hydrogen at an olefins unit. This example illustrates that use of tail gas to regenerate an acetylene saturated adsorbent bed is as effective as pure hydrogen. Example 6 - Cycle A A 31.96 gm (43 mL) of another Pd/Al 2 θ 3 adsorbent (0.3 percent palladium by weight) was reduced using pure hydrogen as in example 1 with the exception that the reduction temperature was held to 180°C, at 75 psig for 7 hours. After stopping the hydrogen reduction and cooling the vessel to about 49°C (120°F) in nitrogen, a stream containing 191 ppm acetylene, balance ethylene gas was passed through the adsorbent bed at 110 psig. Upon acetylene breakthrough the vessel was then depressured and purged with nitrogen. Acetylene adsorption capacity was 0.06 mL acetylene/mL adsorbent. Regeneration was then done with pure hydrogen at 75 psig, about 49°C (120°F), at 250 mL/min. After regeneration the Pd/Al 2 θ 3 bed was exposed to another acetylene/ethylene adsorption cycle and the acetylene capacity was 0.062 mL acetylene/mL adsorbent. Example 6 - Cycle B The next regeneration cycle was then done using a gas blend containing 21.32 mole percent hydrogen, 0.1440 mole percent ethylene, 0.101 mole percent carbon monoxide with the balance being methane. Tail gas was introduced at a flow rate of about 200 mL/minute and 75 psig. Temperature was held at about 49°C (120°F) for the regeneration by immersing the adsorption vessel in a water bath. After about 16 hours flow of tail gas was stopped, nitrogen was purged through the vessel for 30 minutes at about 49°C (120°F). Pure ethylene was then flowed through the vessel at 110 psig for about 1.5 hours at 110 mL/ minute flow. After this time the 191 ppm acetylene/ethylene mixture was flowed through the reactor at 110 psig, 120°F, and 1 10 mL/minute flow rate. After about 4.5 hours acetylene was detected in the bed effluent which corresponds to 0.0977 mL/acetylene adsorbed /mL of adsorbent, which surpasses the adsorption capacity observed when pure hydrogen was used for regeneration. Example 6 - Cycle C Tail gas was then used again to regenerate the adsorbent bed at the same conditions as above, only that instead of 16 hours of regeneration, only 2.75 hours of regeneration was done. When exposed to another ethylene/acetylene adsorption cycle, acetylene adsorption capacity was 0.089 mL acetylene/mL adsorbent, nearly the same as when a 16 hour regeneration was done. No deleterious green oil was formed when tail gas was used for regeneration and the adsorption capacity actually increased compared to pure hydrogen. Example 7 Larger scale testing was done at a commercial olefin steam cracking plant to demonstrate this invention under more severe conditions such as pipeline ethylene pressures of 1800 psig, ethylene flow rates in the 100 to 700 lb/hr range, and temperatures of about 27°Cto about 49°C(80°F to 120°F). The test unit consisted of a down flow reactor vessel that contained 1 ft 3 of a palladium on gamma alumina adsorbent (0.32 percent palladium by weight). Polymer-grade ethylene which contained less than 1 ppm acetylene at 1800 psig was the olefin feed. For reduction and regeneration of the adsorbent, ambient temperature tail gas was used which contained about 42 percent hydrogen, 0.8 to 5 percent ethylene, 300 to 500 ppm carbon monoxide and the balance methane. The fresh adsorbent was reduced with a 110 lb/hr flow rate of tail gas at 63 psig for about 18 hours. Temperatures increased from inlet to outlet of the bed about 30°C to 40°C (about 86°F to 104°F) due to the heat of hydrogenation of ethylene in the tail gas. After the reduction cycle flow of tail gas was stopped, nitrogen was purged through the vessel to remove all hydrogen from the adsorbent. The vessel was then pressurized with 300 to 500 psig nitrogen followed by a slow pressurization of the vessel with the 1800 psig ethylene stream. Once the vessel was at ethylene feed pressure of 1800 psig, the flow rate was adjusted to about 100 lbs/hr. Analysis of effluent ethylene indicated less than 20 parts per billion (ppb) acetylene while 0.2 to 0.65 ppm acetylene was in the feed ethylene. Flow rates were increased to 600-700 lbs/hr and held there until about 58,000 lbs of ethylene had flowed through the adsorbent bed. A slight breakthrough of 0.08 ppm acetylene was then detected in the effluent. The ethylene flow was stopped and the vessel depressurized and purged with nitrogen for 1/2 hour. Acetylene adsorption capacity was about 0.305 mL acetylene adsorbed per mL of bed. Regeneration was done using tail gas at ambient temperature and 63 psig. About 4 hours of tail gas flow through the bed at 110 lbs/hr was enough to regenerate the 1 ft 3 bed of adsorbent. Tail gas was then stopped, nitrogen purged through the unit for 1/2 hour and the next ethylene/acetylene adsorption cycle started. The second ethylene/acetylene adsorption cycle was done under identical conditions as the first cycle above, except the feed flow rate was constant at 400 lbs/hr. After over 66,000 lbs of ethylene was treated a small amount 0.06 ppm of acetylene started to break through the bed. This corresponds to an adsorption capacity of was about 0.32 mL acetylene adsorbed per mL of bed . For the purposes of the present invention, "predominantly" is defined as more than about fifty per cent. "Substantially" is defined as occurring with sufficient frequency or being present in such proportions as to measurably affect macroscopic properties of an associated compound or system. Where the frequency or proportion for such impact is not clear substantially is to be regarded as about twenty per cent or more. The term "Essentially" is defined as absolutely except that small variations which have no more than a negligible effect on macroscopic qualities and final outcome are permitted, typically up to about one percent. Examples have been presented and hypotheses advanced herein in order to better communicate certain facets of the invention. The scope of the invention is determined solely by the scope of the appended claims.

Claims: That which is claimed is: 1. A process for purification of olefins which comprises: passing a gaseous mixture comprising an olefin of from 2 to about 8 carbon atoms, acetylenic impurities having the same or similar carbon content and optionally saturated hydrocarbon gases through a particulate bed of adsorbent comprising predominantly a support material having high surface area on which is dispersed at least one metallic element selected from the group consisting of chromium, iron, cobalt, nickel, ruthenium, palladium, and platinum, to effect, in the presence of an essentially dihydrogen-free atmosphere within the bed, selective and reversible adsorption and/or complexing of the contained acetylenic contaminants with the adsorbent, and thereby obtain purified effluent which contains less than a predetermined level of the acetylenic impurities; and thereafter regenerating the resulting bed of adsorbent in the presence of a reducing gas comprising dihydrogen to effect release of the contained acetylenic impurities from the adsorbent. 2. The process according to claim 1 wherein the adsorbent further comprises at least one element selected from the group consisting of lithium, sodium, potassium, zinc, molybdenum, tin, tungsten, and iridium, dispersed on the support material. 3. The process according to claim 1 wherein the support is a material selected from the group consisting of alumina, silica, active carbon, clay and zeolites, and has surface area in a range of from about 10 to about 2,000 square meters per gram as measured by the BET gas adsorption method. 4. The process according to claim 3 wherein the metal dispersed on the support material is at least one element selected from the group consisting of iron, cobalt, nickel, zinc, ruthenium, palladium, platinum, and potassium, and the absorbent has a dispersed metal content in a range of from about 0.01 to about 10 percent based on the total weight of the adsorbent. 5. The process according to claim 4 wherein the gaseous mixture passes though the bed of particulate adsorbent at gas hourly space velocities in a range of from about 0.05 hours - 1 to about 20,000 hours - 1 measured at standard conditions of 0°C and 760 mm Hg. 6. The process according to claim 1 wherein the adsorbent comprises at least about 90 weight percent of a gamma alumina having surface area in a range of from about 80 to about 500 square meters per gram as measured by the BET gas adsorption method, and contains less than 500 parts per million by weight of a sulfur-containing component, calculated as elemental sulfur. 7. The process according to claim 6 wherein the metal dispersed on the support material is palladium, and the absorbent has a palladium content in a range of from about 0.01 to about 10 percent based on the total weight of the adsorbent. 8. The process according to claim 1 wherein the olefin in the gaseous mixture being purified is predominantly ethylene or propylene, the gaseous mixture contains less than about 0.5 parts per million by volume of hydrogen and less than about 1 parts per million by volume of mercury-containing, arsenic-containing, and sulfur-containing components, each calculated as the element, and wherein the gaseous mixture, while passing through the bed, is at temperatures in a range of from about -35°C to about 65°C 9. The process according to claim 8 wherein the adsorbent comprises at least about 90 weight percent of a gamma alumina having surface area in a range of from about 150 to about 350 square meters per gram as measured by the BET gas adsorption method, and wherein the metal dispersed on the support material is palladium, and the absorbent has a palladium content in a range of from about 0.01 to about 10 percent based on the total weight of the adsorbent. 10. The process according to claim 1 wherein the adsorbent has a metal dispersion value of at least 10 percent as measured by carbon monoxide chemisorption method. 11. A process for purification of olefins produced by thermal cracking of hydrocarbons which comprises: passing a gaseous mixture comprising at least about 99 percent by volume of an olefin having from 2 to about 4 carbon atoms, and acetylenic impurities having the same or similar carbon content in an amount in a range upward from about 1 to about 1000 parts per million by volume, through a particulate bed of adsorbent comprising predominantly a support material selected from the group alumina, silica, active carbon, clay and zeolites having surface area in a range of from about 10 to about 2,000 square meters per gram as measured by the BET gas adsorption method, on which is dispersed at least one metallic element selected from the group consisting of iron, cobalt, nickel, zinc, ruthenium, palladium, platinum, and potassium, to provide an effluent stream from the bed; effecting, in the presence of and essentially dihydrogen- free atmosphere within the bed, selective and reversible adsorption and/or complexing of the contained acetylenic impurities with the adsorbent, until levels of the acetylenic impurities in the effluent stream increase to a predetermined level in a range downward from about 1 parts per million by volume; and thereafter regenerating the resulting bed of adsorbent in the presence of a reducing gas comprising dihydrogen to effect release of the contained acetylenic impurities from the adsorbent. 12. The process according to claim 11 wherein the adsorbent further comprises at least one element selected from the group consisting of lithium, sodium, potassium, zinc, molybdenum, tin, tungsten, and iridium, dispersed on the support material. 13. The process according to claim 11 wherein the support is a material selected from the group consisting of alumina, silica, carbon clay and zeolites, and has surface area in a range of from about 10 to about 2,000 square meters per gram as measured by the BET gas adsorption method. 14. The process according to claim 13 wherein the metal dispersed on the support material is at least one element selected from the group consisting of iron, cobalt, nickel, zinc, ruthenium, palladium, platinum, and potassium, and the absorbent has a dispersed metal content in a range of from about 0.01 to about 10 percent based on the total weight of the adsorbent. 15. The process according to claim 14 wherein the gaseous mixture passes though the bed of particulate adsorbent at space velocities in a range of from about 0.05 hours - 1 to about 20,000 hours - 1 measured at standard conditions of 0°C and 760 mm Hg 16. The process according to claim 11 wherein the adsorbent comprises at least about 90 weight percent of a gamma alumina having surface area in a range of from about 80 to about 500 square meters per gram as measured by the BET gas adsorption method, and contains less than 500 parts per million by weight of a sulfur-containing component, calculated as elemental sulfur. 17. The process according to claim 16 wherein the metal dispersed on the support material is palladium, and the absorbent has a palladium content in a range of from about 0.01 to about 10 percent based on the total weight of the adsorbent. 18. The process according to claim 11 wherein the olefin in the gaseous mixture being purified is predominantly ethylene or propylene, the gaseous mixture contains less than about 0.5 parts per million by volume of hydrogen and less than about 1 parts per million by volume of mercury-containing, arsenic- containing, and sulfur-containing components, each calculated as the element, and wherein the gaseous mixture, while passing through the bed, is at temperatures in a range of from about minus 35°C to about 65°C 19. The process according to claim 18 wherein the adsorbent comprises at least about 90 weight percent of a gamma alumina having surface area in a range of from about 150 to about 350 square meters per gram as measured by the BET gas adsorption method, and wherein the metal dispersed on the support material is palladium, and the absorbent has a palladium content in a range of from about 0.01 to about 10 percent based on the total weight of the adsorbent. 20. The process according to claim 11 wherein the adsorbent has a metal dispersion value in a range upward from about 20 percent to about 80 percent as measured by carbon monoxide chemisorption method.

Inventors: KAMINSKY MARK P, PEI SHIYOU, WHITTAKER ROBERT C, WILSAK RICHARD A, KAMINSKY, MARK, P., PEI, SHIYOU, WHITTAKER, ROBERT, C., WILSAK, RICHARD, A.
Applicants: AMOCO CORP, AMOCO CORPORATION
Application year: 1998
Main classification: C10G70
IPC codes: B01D53, B01J20, C07C7, C07C11, C10G25, C10G70