Process for the removal of lower hydrocarbons in exhaust gas

Abstract: Process for the removal of lower hydrocarbons from exhaust gas comprising passing the gas over a catalyst containing an oxide of rhodium supported on a chromium oxide comprising carrier; and withdrawing a purified exhaust gas.

Description: The present invention relates to the removal of lower hydrocarbons in exhaust gas by catalytic oxidation in presence of a catalyst consisting of rhodium supported on a chromium oxide containing carrier. The invention provides a process for the removal of lower hydrocarbons and carbon monoxide from exhaust gas containing volatile sulphur compounds, comprising passing the gas over a catalyst containing an oxide of rhodium supported on a chromium oxide Cr 2 O 3 /Al 2 O 3 comprising carrier; and withdrawing a purified exhaust gas. The inventive process is in particular useful in the catalytic oxidation of the hydrocarbons in sulphur containing exhaust gases from lean-burn gas engines. Suitable carriers for use in the invention may be in any convenient shape employed in the art. Preferably, the carrier has a monolithic structure optionally enforced with silica fibres. DETAILED DESCRIPTION OF THE INVENTION Preparation of a Rhodium Catalyst supported on a Cr 2 O 3 /Al 2 O 3 A monolithic carrier of alumina enforced with silica fibres and with 350 cells per square inch was impregnated with chromium nitrate, by emerging the carrier two times in a 10% (v/v) aqueous chromium nitrate solution. The impregnated carrier was then dried and chromium nitrate oxidized by heating in air for two hours. The thus prepared Cr 2 O 3 containing carrier was impregnated with rhodium by pore saturation of the carrier surface with an aqueous solution of RhCl 3 · 2H 2 O corresponding to 6 g/l catalyst volume. The thus prepared catalyst was finally calcined at 520°C. Analysis of the final catalyst showed a content of 13% Cr and 3% Rh calculated on metallic base. Example 1 Activity test of the above prepared catalyst in the removal of methane from sulphur oxide containing exhaust gas Exhaust gas from a 1 MW caterpillar gas engine containing 10% H 2 O, 5% CO 2 , 8% O 2 , 1500 ppm CH 4 , 400 ppm CO, 150 ppm NMHC (non-methane hydrocarbons) and 0.1 ppm SO 2 with nitrogen as balance was passed at a NHSV of 10.000 h -1 through the catalyst prepared as described above at different temperatures. Conversion of CO and carbonhydrides in the effluent gas was measured at different times on stream. The above conditions and results obtained thereby are summarized in Table 1 below. Operation time h T inlet °C CO Conversion % HC Conversion % 3 438 99 92 23 439 100 87 120 420 95 77 Example 2 Sulphur resistant test of the catalyst by contact with sulphur containing exhaust gas. In a laboratorium scale test the same catalyst as in Example 1 was tested for methane oxidation activity of varying concentration of SO 2 in exhaust gas, consisting of 1500 ppm CH 4 , 10% H 2 O, air and SO 2 . The gas was passed at a NHSV of 12500h -1 through the catalyst at an inlet temperature of 450°C. The results obtained by this test are summarized in Table 2 below. Operation time h SO 2 [ppm] Conversion [%] CH 4 10 1 55 60 1 55 61 8 39 73 8 37 80 30 28 100 30 28 102 0 54 150 0 68 As apparent from the above results sulphur poisoning of the catalyst is reversible.

Claims: Process for the removal of lower hydrocarbons and carbon monoxide from exhaust gas containing volatile sulphur compounds, comprising passing the gas over a catalyst containing an oxide of rhodium supported on a Cr 2 O 3 /Al 2 O 3 comprising carrier; and withdrawing a purified exhaust gas. The process of claim 1, wherein the carrier has a monolithic structure. The process of claim 2, wherein the monolithic structure is enforced with silica fibres.

Inventors: HANSEN POUL LENVIG, JOHANSEN KELD, HANSEN, POUL LENVIG, JOHANSEN, KELD
Applicants: TOPSOE HALDOR AS, HALDOR TOPSOE A/S
Application year: 1998
Main classification: B01D53
IPC codes: B01J32, B01J33, B01J35, B01J23, B01D53