Silatrane derivative, method for manufacturing same, adhesion promoter, and curable silicone compositions

Abstract: A silatrane derivative is described and claimed herein having the formula: wherein each R 1 is independently a hydrogen atom or an alkyl group; each R 2 is independently selected from the group consisting of a hydrogen atom, an alkyl group, and an alkenyloxyalkyl group having the formula: ―R 4 -O-R 5 wherein R 4 is an alkylene group and R 5 is an alkenyl group, and each R 3 is independently selected from the group consisting of a monovalent hydrocarbon group, a C 1 to C 10 alkoxy group, a glycidoxyalkyl group, an oxiranylalkyl group, an acyloxyalkyl group, a haloalkyl group, and an aminoalkyl group, with the proviso that at least one R 2 is an alkenyloxyalkyl group

Description: The present invention relates to a silatrane derivative, a method for manufacturing the same, an adhesion promoter comprising the silatrane derivative, and a curable silicone composition containing the adhesion promoter that exhibits specific adhesion to organic resins. A silatrane compound expressed by the general formula: in which R is a methyl group, a phenyl group, a methoxy group, or an ethoxy group is known from U.S. Patent 2,953,545 and JP-A 61-69781. But, when these silatrane compounds are added to a curable silicone composition, the product does not exhibit good adhesion. The present invention is the result of research for a novel silatrane derivative that would be useful as an adhesion promoter. Specifically, an object of the present invention is to provide a novel silatrane derivative, an efficient method for its manufacture, an adhesion promoter composed therefrom, and a curable silicone composition containing this adhesion promoter which exhibits specific adhesion to organic resins. The present invention is a silatrane derivative having the formula: wherein each R 1 is independently a hydrogen atom or an alkyl group; each R 2 is independently selected from the group consisting of a hydrogen atom, an alkyl group, and an alkenyloxyalkyl group having the formula: -R 4 -O-R 5 wherein R 4 is an alkylene group and R 5 is an alkenyl group, with the proviso that at least one R 2 is an akenyloxyalkyl group; and each R 3 is independently selected from the group consisting of a monovalent hydrocarbon group, a C 1 to C 10 alkoxy group, a glycidoxyalkyl group, an oxiranylalkyl group, an acyloxyalkyl group, a haloalkyl group, and an aminoalkyl group. The present invention is further directed to a method of preparing the above silatrane derivative, to an adhesion promoter comprising said silatrane, and to a curable silicone composition containing the same. The silatrane derivative of this invention is expressed by the general formula: In this formula, each R 1 is independently a hydrogen atom or an alkyl group. Examples of the alkyl group of R 1 include methyl, ethyl, propyl, butyl, pentyl, isopropyl, isobutyl, cyclopentyl, and cyclohexyl. It is particularly favorable for R 1 to be a hydrogen atom or a methyl group. Each R 2 is independently selected from the group consisting of a hydrogen atom, an alkyl group, and an alkenyloxyalkyl group expressed by the general formula: ―R 4 ―O―R 5 with the proviso that at least one R 2 group is an alkenyloxyalkyl group. Examples of the alkyl group of R 2 are the same as those listed for R 1 . For the alkenyloxyalkyl group of R 2 , R 4 in the formula is an alkylene group, examples of which include methylene, ethylene, methylmethylene. and propylene, with methylene being preferred. R 5 is an alkenyl group, examples of which include vinyl, allyl, butenyl, pentenyl, and hexenyl, with a C 3 to C 10 alkenyl group being preferable, and an allyl group being particularly favorable. Examples of the alkenyloxyalkyl group of R 2 include an allyloxymethyl group and an allyloxypropyl group. Each R 3 is independently selected from the group consisting of substituted or unsubstituted monovalent hydrocarbon groups, C 1 to C 10 alkoxy groups, glycidoxyalkyl groups, oxiranylalkyl groups, acyloxyalkyl groups, haloalkyl groups, and aminoalkyl groups. Examples of the monovalent hydrocarbon group of R 3 include alkyl groups such as methyl, ethyl, propyl, butyl, pentyl, isopropyl, isobutyl, cyclopentyl, and cyclohexyl; alkenyl groups such as viny, allyl, butenyl, and hexenyl; aryl groups such as phenyl, tolyl, and xylyl; aralkyl groups such as benzyl and phenethyl; and haloalkyl groups such as chloromethyl, 3-chloropropyl, and 3,3,3-trifluoropropyl; examples of the alkoxy group of R 3 include methoxy, ethoxy, and propoxy; examples of the glycidoxyalkyl group of R 3 include 3-glycidoxypropyl. Further, the oxiranylalkyl group or R 3 includes 4-oxiranylbutyl or an 8-oxiranyloctyl. Examples of the acyloxyalkyl group of R 3 are selected from acetoxypropyl and 3-methacryloxypropyl. Finally, the aminoalkyl group of R 3 consists of 3-aminopropyl or N-(2-aminoethyl)-3-aminopropyl. The following compounds are examples of the silatrane derivative of the present invention: The method of preparing our silatrane derivative comprises reacting an epoxy compound having the formula: and an alkoxysilane compound having the formula: R 3 Si(OR 6 ) 3 with a compound selected from ammonia or an amine compound having the formula: NH y (CR 1 2 CR 1 2 OH) (3-y) wherein each R 1 is independently a hydrogen atom or an alkyl group, each R 3 is independently selected from the group consisting of a monovalent hydrocarbon group, a C 1 to C 10 alkoxy group, a glycidoxyalkyl group, an oxiranylalkyl group, an acyloxyalkyl group, a haloalkyl group, and an aminoalkyl group; R 4 is an alkylene group; R 5 is an alkenyl group; R 6 is a C 1 to C 10 alkyl group; and y is 1 or 2. The epoxy compound is a raw material for forming the skeleton of the above-mentioned silatrane derivative, and it is also a raw material for introducing alkenyloxyalkyl groups into molecules of said derivative. In the epoxy compound, R 1 , R 4 , and R 5 are as defined above. Preferably R 5 is a C 3 to C 10 alkenyl group, and more preferably R 5 is an allyl group. Examples of preferred epoxy compounds are allyl glycidyl ether or butenyl glycidyl ether. The alkoxysilane is also raw material for forming the silatrane derivative of the present invention. R 3 in the alkoxysilane is as defined above. R 6 is a C 1 to C 10 alkyl group, examples of which include methyl, ethyl, and propyl. Examples of this alkoxysilane compound are tetramethoxysilane, tetraethoxysilane, methyltrimethoxysilane, methyltriethoxysilane, vinyltrimethoxysilane, vinyltriethoxysilane, phenyltrimethoxysilane, 3-methacryloxypropyltrimethoxysilane, 3,3,3-trifluoropropyltrimethoxysilane, nonafluorobutylethyltrimethoxysilane, 3-aminopropyltrimethoxysilane, 3-aminopropyltriethoxysilane, and N-(2-aminoethyl)-3-aminopropyltrimethoxysilane. The ammonia or amine compound is a raw material for the silatrane derivative of the present invention. R 1 in the amine compound is as defined above and y is 1 or 2. Examples of this amine compound include 2-hydroxyethylamine, 2,2'-dihydroxyethylamine, and 2-hydroxy-2-methyl-ethylamine. In the present invention, no limit is imposed on the amounts of the epoxy compound and the alkoxysilane compound added with respect to the ammonia. However, to suppress by-product generation and obtain a good yield, the reaction is conducted under conditions in the presence of ammonia and the epoxy compound is used in amounts of 2 to 20 moles, preferably 3 to 15 moles, per mole of ammonia. The alkoxysilane compound is added in an amount of 0.5 to 50 moles per mole of ammonia, with a range of 1 to 20 moles being preferable. Thus it is recommended that the alkoxysilane compound be used in the stoichiometric amount, or in excess, with respect to the ammonia. In general, the generation of by-products is also suppressed if the alkoxysilane compound is used in an excess amount to the extent that the reaction does not slow down. However, excess alkoxysilane compound will possibly remain behind. This unreacted alkoxysilane is then separated and recovered from our silatrane derivative by distillation, or the like, following the reaction. This reaction can also be conducted while ammonia gas is blown into a mixture of the epoxy compound and the alkoxysilane compound. When such a reaction is conducted in an open system, part of the ammonia will not react and instead will be released outside the system. Therefore, ammonia must be used in an excess amount corresponding to this loss. In the present invention, no specific limit is imposed on the amounts of the epoxy and alkoxysilane compounds added with respect to the amine compound. However, to obtain our silatrane derivative at good yield, if y in the amine compound is 1, then the epoxy compound is preferably used in an amount of 0.5 to 10 moles, and more preferably 0.8 to 5 moles, per mole of amine. If y in the amine compound is 2. then the epoxy compound is preferably used in an amount of 1.5 to 20 moles, and more preferably 1.8 to 10 moles, with an amount of 2 mole being particularly favorable. Likewise, the amount in which the alkoxysilane compound is added is preferably 0.5 to 50 moles, and more preferably 1 to 20 moles, per mole of the amine compound. Thus, it is recommended that the alkoxysilane compound be used in the stoichiometric amount, or in excess, with respect to the amine compound. In general, the generation of by-products is also suppressed if the alkoxysilane compound is used in an excess amount to the extend that the reaction does not slow down. However, excess alkoxysilane compound will possibly remain behind. The unreacted alkoxysilane compound is then separately and recovered from our silatrane derivative as needed by distillation, or the like, following the reaction. With our method for preparing a silatrane derivative, the reaction will proceed either at room temperature or under heating, but heating to 100 °C or below is preferred to reduce the reaction time. The use of an organic solvent is optional, but they can be used and include aliphatic hydrocarbons such as; hexane, heptane, and octane; aromatic hydrocarbons such as toluene or xylene; alcohols such as methanol, ethanol and isopropanol; ketones such as acetone or methyl isobutyl ketone other; ethers such as diethylether or tetrahydrofuran; esters such as ethyl acetate or isoamyl acetate. The use of methanol or ethanol in particular will allow the reaction time to be shortened, and our claimed silatrane derivative to have an even better yield. When alcohol is added, it is preferable to use an alcohol having the same number of carbons as the silicon-bonded alkoxy groups in the initial alkoxysilane compound so that the alkoxy groups bonded to silicon atoms will undergo an alkoxy group exchange reaction during the above reaction. Also, when an alcohol is added in the method of this invention, the reaction is markedly shorter, and the yield of our silatrane derivative is increased, by conducting the reaction at the reflux temperature of said alcohol. The silatrane derivative of the present invention used, for example, to impart adhesive properties to silicone other curable compositions that are cured by condensation reaction, hydrosilylation reaction, UV rays and high-energy rays. Other curable compositions are represented by alkoxysilane-modified polyether-based compositions, polyurethane resin and rubber compositions, epoxy resin compositions, polysulfide resin compositions, and unsaturated polyester resin compositions. Our silatrane can also be used as a primer which increases the adhesion of the above curable compositions when applied to the surface of metal, glass, plastic, or similar substrates. Our silatrane derivative is particularly useful with silicone and other curable compositions cured by condensation, hydrosilylation, UV rays or other high-energy rays. The adhesion promoter of our invention may be composed solely of the above-mentioned silatrane derivative, or it may be a mixture of said derivative with a known adhesion promoter and/or a known organic solvent. When our silatrane derivative is used with a known adhesion promoter, it loses its specific adhesion with respect to organic resins; but it displays good adhesion with respect to a variety of materials, such as organic resins, metals, and ceramics. Examples of known adhesion promoters which are used with our silatrane derivative include methyltrimethoxysilane, vinyltrimethoxysilane, allyltrimethoxysilane, 3-methacryloxypropyltrimethoxysilane, 3-glycidoxypropyltrimethoxysilane, 3-aminopropyltrimethoxysilane, N-(2-aminoethyl)-3-aminopropyltrimethoxysilane, bis(trimethoxysilyl)propane, and bis(trimethoxysilyl)hexane. The amino group-containing alkoxysilane or epoxy compound remaining unreacted through the process of manufacturing our silatrane derivative, as well as any other reaction products, may be left in the final product. In this case, the silatrane derivative content is typically at least 10 wt%, with at least 50 wt% being preferable, and at least 70 wt% being most preferred. The reason for this is that the adhesion promotion effect will be diminished if our silatrane derivative content is below this stated range. The silatrane derivative of this invention is also conveniently included in any curable composition. The curable silicone composition of our invention is characterized by containing the claimed silatrane derivative. Examples of curable silicone compositions containing this derivative include compositions cured by a condensation reaction such as a dealcoholization reaction, a dehydration reaction, a dehydrogenation reaction, a deoxime reaction, a de-acetic acid reaction, or a de-acetone reaction; compositions cured by hydrosilylation reactions; and silicone compositions cured by high-energy rays. These latter reactions include those involving a mercapto-vinyl addition reaction, an acrylic group radical reaction, or a cationic polymerization reaction for epoxy groups or vinyl ether groups. A silicone composition cured by a hydrosilylation reaction is particularly favorable. No limit is imposed on the blend amount of our silatrane derivative in the curable composition of the present invention, but said amount is normally from 0.01 to 20 wt%, and preferably from 0.05 to 10 wt%. A range of 0.1 to 5 wt% is particularly desired. The curable silicone composition of the present invention has a variety of uses, including molding, since is contains a silatrane derivative. More particularly, it displays specific adhesion with respect to organic resins. Accordingly, our curable compositions are conveniently utilized as a production material in cast molding. For example, in the case of an integrated molded article of cured silicone and an organic resin, the silicone adheres well to the organic resin but does not stick to the metal of the mold. Example 1 31.5 g (0.3 mole) of 2,2'-dihydroxyethylamine, 81.7 g (0.6 mole) of methyltrimethoxysilane, 45.7 g (0.4 mole) of allyl glycidyl ether, and 32 g of methanol were put into a 500 mL four-neck flask equipped with an agitator, a thermometer, and a reflux condenser. This system was heated and agitated for 5 hours at the methanol reflux temperature. Next, the entire amount of reaction mixture thus obtained was transferred to a pear-shaped flask, and the low-boiling component was distilled off by a rotary evaporator, which yielded 77.6 g of a faintly yellow transparent liquid. This transparent liquid was subjected to 29 Si-nuclear magnetic resonance analysis and 13 C-nuclear magnetic resonance analysis, which confirmed that the silatrane derivative expressed by the following formula had been produced: The content of this silatrane derivative was over 90 wt%. This transparent liquid was termed an adhesion promoter. Example 2 12.2 g (0.2 mole) of 2-hydroxyethylamine, 81.7 g (0.6 mole) of methyltrimethoxysilane, 57.1 g (0.5 mole) of allyl glycidyl ether, and 32 g of methanol were put into a 500 mL four-neck flask equipped with an agitator, a thermometer, and a reflux condenser. This system was heated and agitated for 8 hours at the methanol reflux temperature. Next, the entire amount of reaction mixture thus obtained was transferred to a pear-shaped flask, and the low-boiling component was distilled off by a rotary evaporator, which yielded 63.3 g of a faintly yellow transparent liquid. This transparent liquid was subjected to 29 Si-nuclear magnetic resonance analysis and 13 C-nuclear magnetic resonance analysis, which confirmed that the silatrane derivative expressed by the following formula had been produced: The content of this silatrane derivative was over 90 wt%. This transparent liquid was termed an adhesion promoter. Example 3 31.5 g (0.3 mole) of 2,2-dihydroxyethylamine, 88.9 g (0.6 mole) of vinyltrimethoxysilane, 45.7 g (0.4 mole) of allyl glycidyl ether, and 32 g of methanol were put into a 500 mL four-neck flask equipped with an agitator, a thermometer, and a reflux condenser. This system was heated and agitated for 8 hours at the methanol reflux temperature. Next, the entire amount of reaction mixture thus obtained was transferred to a pear-shaped flask, and the low-boiling component was distilled off by a rotary evaporator, which yielded 63.5 g of a faintly yellow transparent liquid. This transparent liquid was subjected to 29 Si-nuclear magnetic resonance analysis and 13 C-nuclear magnetic resonance analysis, which confirmed that the silatrane derivative expressed by the following formula had been produced. The content of this silatrane derivative was over 90 wt%. This transparent liquid was termed an adhesion promoter. Comparative Example 1 12.2 g (0.2 mole) of 2-hydroxyethylamine, 81.7 g (0.6 mole) of methyltrimethoxysilane, 94.5 g (0.4 mole) of 3-glycidoxypropyltrimethoxysilane, and 32.0 g of methanol were put into a 500 mL four-neck flask equipped with an agitator, a thermometer, and a reflux condenser. This system was heated and agitated for 8 hours at the methanol reflux temperature. The entire amount of reaction mixture thus obtained was transferred to a pear-shaped flask, and the low-boiling component was distilled off by a rotary evaporator, which yielded 131.7 g of a faintly yellow transparent liquid. This transparent liquid was subjected to 29 Si-nuclear magnetic resonance analysis and 13 C-nuclear magnetic resonance analysis, which confirmed that the silatrane derivative expressed by the following formula had been produced. The content of this silatrane derivative was over 90 wt%. This transparent liquid was termed an adhesion promoter. Examples 4 to 6 and Comparative Examples 2 and 3 A curable silicone composition was prepared as follows. A dimethylpolysiloxane sequestering agent, terminated at both ends of the molecular chain with dimethylvinylsiloxy groups; fumed silica, whose surface had been rendered hydrophobic by hexamethyldisilazane; a dimethylsiloxane/methylhydrodienesiloxane copolymer sequestering agent, terminated at both ends of the molecular chain with trimethylmethoxy groups; phenylbutynol; and a platinum-based catalyst were uniformly mixed to prepare a hydrosilylation reaction-curable silicone composition. The adhesion promoters prepared in Examples I to 3 and Comparative Example 1 were each blended in an amount of 1 wt% into this curable silicone composition to prepare four types of a curable silicone composition. For comparison, a curable silicone composition, not containing any of the claimed adhesion promoters, was separately prepared. These latter curable silicone compositions were used to coat the surfaces of the substrates shown in Table 1, after which the coatings were cured by being heated for 30 minutes in a 120°C circulating hot air oven. The cured products thus obtained were in a rubbery form. The adhesion of the five types of silicone rubber with respect to the substrates was evaluated, with a "○" indicating that the silicone rubber adhered well to a substrate, a "Δ" that the silicone rubber partially adhered to a substrate, and a "×" that the silicone rubber peeled completely away from the substrate. The results are given in Table 1. Present invention Comparative examples Ex. 4 Ex. 5 Ex. 6 Comp. Ex. 2 Comp. Ex. 3 Type of adhesion promoter Ex. 1 Ex. 2 Ex. 3 Comp. Ex. 1 none Initial adhesion of silicone rubber Type of substrate Aluminium x x x ○ x Stainless steel x x x ○ x Glass Δ x x ○ x Polycarbonate resin ○ ○ ○ ○ x Polybutylene terephthalate resin ○ ○ ○ ○ x Phenol resin ○ ○ ○ ○ × The claimed silatrane derivative of this invention is a novel compound, and our method of preparing said silatrane is efficient. Moreover, the adhesion promoter which contains this novel silatrane, and the curable composition containing the silatrane derivative all display specific adhesion with respect to organic resins and at the same time poor adhesion to other substrates like metals and glass. The capability to give selective adhesion property (good adhesion to organic resins and poor adhesion to metals) to a silicone rubber when used as an additive makes the silatrane derivatives according to the present invention especially useful in molding applications.

Claims: A silatrane derivative comprises a compound having the formula: wherein each R 1 is independently a hydrogen atom or an alkyl group; each R 2 is independently selected from the group consisting of a hydrogen atom, an alkyl group, and an alkenyloxyalkyl group having the general formula: -R 4 -O-R 5 wherein R 4 is an alkylene group and R 5 is an alkenyl group and each R 3 is independently selected from the group consisting of a substituted or unsubstituted monovalent hydrocarbon group, a C 1 to C 10 alkoxy group, a glycidoxyalkyl group, an oxiranylalkyl group, an acyloxyalkyl group, a haloalkyl group, and an aminoalkyl group; with the proviso that at least one R 2 is an alkenyloxyalkyl group A method of preparing the silatrane derivative of claim 1 said method comprising the steps of reacting (i) an epoxy compound having the formula: and (ii) an alkoxysilane compound having the formula: R 3 Si(OR 6 ) 3 with (iii) a compound selected from ammonia or an amine compound having the formula: NH y (CR 1 2 CR 1 2 OH) (3-y) wherein each R 1 is independently a hydrogen atom or an alkyl group; each R 3 is independently selected from the group consisting of a substituted or unsubstituted monovalent hydrocarbon group, a C 1 to C 10 alkoxy group, a glycidoxyalkyl group, an oxiranylalkyl group, an acyloxyalkyl group, a haloalkyl group, and an aminoalkyl group; R 4 is an alkylene group; R 5 is an alkenyl group; R 6 is a C 1 to C 10 alkyl group; and y is 1 or 2. The method according to claim 2. wherein compound (iii) is ammonia and the epoxy compound is used in an amount from 2 to 20 moles per mole of ammonia. The method according to claim 2, wherein compound (iii) is an amine, y is 1, and the epoxy compound is used in an amount from 0.5 to 10 moles per mole of amine. The method according to claim 2, wherein compound (iii) is an amine, y is 2, and the epoxy compound is used in an amount from 1.5 to 20 moles per mole of amine. The method according to claim 2, wherein the alkoxysilane compound is used in at least a stoichiometric amount relative to compound (iii). The method according to claim 6, wherein compound (iii) is ammonia and the alkoxysilane compound is used in an amount from 0.5 to 50 moles per mole of ammonia. The method according to claim 6, wherein compound (iii) is an amine and the alkoxysilane compound is used in an amount from 0.5 to 50 moles per mole of the amine compound. The method according to claim 6, wherein the alkoxysilane compound is used in stoichiometric excess with respect to compound (iii), said method further comprising the step of separating unreacted alkoxysilane compound from the silatrane derivative. The method according to any of claims 2 to 9, wherein the reaction is conducted at a temperature not greater than 100 °C. The method according to any of claims 2 to 10, wherein the reaction is conducted in the presence of an alcohol having the same number of carbon atoms as R 6 in compound (ii). Use of the silatrane derivative of claim 1 as adhesion promoter. A curable composition comprising the silatrane derivative of claim 1. The curable composition according to claim 13, wherein the silatrane derivative of claim 1 is present in an amount from 0.01 to 20 weight percent based on the total weight of said composition. The curable composition according to claim 13, wherein said curable composition is selected from silicone compositions and other curable compositions cured by condensation reaction, hydrosilylation reaction, UV rays, and high energy rays. The curable composition according to claim 15, wherein said other curable compositions are selected from alkoxysilane-modified polyether based compositions, polyurethane resin and rubber compositions, epoxy resin compositions, polysulfide resin compositions and unsaturated polyester resin compositions.

Inventors: YOSHITAKE MAKOTO, YOSHITAKE, MAKOTO, Yoshitake, Makoto Dow Corn. Toray Sil. Comp., Ltd.
Applicants: DOW CORNING TORAY SILICONE, DOW CORNING TORAY SILICONE COMPANY, LTD.
Application year: 1998
Main classification: C07F7
IPC codes: C08K5, C07F7