HIGH-STRENGTH HIGH-WORKABILITY COLD ROLLED STEEL SHEET HAVING EXCELLENT IMPACT RESISTANCE

Abstract: The present invention relates to cold rolled steel sheet with high strength and high formability having an excellent crushing performance which is characterized in that said steel sheet contains 0.05-0.40 mass % of C, 1.0-3.0 mass % of Si, 0.6-3.0 mass % of Mn, 0.02-1.5 mass % of Cr, 0.010-0.20 mass % of P and 0.01-0.3 mass % of Al while the remained part substantially consists of Fe; that said steel sheet has ferrite (polygonal ferrite) as a major phase and has a minor phase consisting of martensite, acicular ferrite and retained austenite; that the ratio of the minor phase in the steel structure is 3-40%; and that the ratios of martensite, retained austenite and acicular ferrite in the minor phase are 10-80%, 8-30% and 5-60%, respectively. In accordance with the present invention, it is now possible to offer cold rolled steel sheet with high strength and high formability having an excellent crushing performance which not only exhibits a sufficient formability mostly as a steel sheet for automobiles but also is capable of satisfying a severe safety standard.

Description: Technical Field The present invention relates to cold rolled steel sheet with high strength and high formability having an excellent crushing performance which is suitable for use as a steel sheet for automobiles. Background Art Under the trend of making automobiles light in weight, there has been an especially brisk demand for thin steel sheet with high strength having an excellent formability. In addition, safety of automobiles has been thought to be important too and, accordingly, there has been a demand an improvement in crushing performance which is a yardstick for safety upon crash. With regard to outer and inner panels for automobiles, cold rolled steel sheets are advantageous in terms of homogeneity of surface roughness and phosphatability. Under such current circumstances, various cold rolled steel sheets with high strength have been developed already. For example, in the Japanese Examined Patent Publication Hei-05/064215 and Laid-Open Patent Publication Hei-04/333524, there are disclosures on the method for the manufacture of high strength steel having a structure of ferrite containing not less than 3% of retained austenite, bainite and retained austenite (hereinafter, referred to as TRIP steel). However, although the TRIP steel has a high elongation and a good formability (TS × El ≧ 22000 MPa.%), there is a problem that said steel does not satisfy the current requirement for severe crushing performance. In addition, there is another problem that the work hardening (WH) at press formability and the bake hardening (BH) at painting and baking thereafter are as low as about 70 MPa. When those work and bake hardenings (WH + BH) are low, there is a big disadvantage in terms of ensuring the strength after forming, painting and baking. On the other hand, the so-called dual phase steel (hereinafter, referred to as DP steel) having a dual phase of ferrite and martensite is disclosed, for example, in the Japanese Laid-Open Patent Publication Hei-09/111396 as a high strength steel sheet having an excellent crushing performance. However, although the DP steel has an excellent crushing performance, its elongation is not sufficient and there is a problem in formability. As mentioned above, no cold rolled steel sheet which satisfies both requirements of sufficient formability and severe safety standard has not been available at present and, therefore, there has been a demand for developing it. EP-A-0 719 868 discloses a steel sheet for automobiles which has high strength, is excellent in press-formability, and possesses strength against impact resistance at a high strain rate, and a method of manufacturing the steel sheet. The steel sheet comprises 0.010 - 0.10 wt% of C, not greater than 1.50 wt% of Si, 0.50 - 3.00 wt% of Mn, not greater than 0.010 wt% of S and 0.01 - 0.1 wt% of Al, and one kind or two kinds selected from 0.05 - 0.15 wt% of P and 0.5 - 1.5 wt% of Cr, and the balance being Fe and inevitable impurities and having a structure mainly composed of 2 - 30 vol% of a martensite phase and a ferrite phase containing a solution C not greater than 0.0010 wt%. The steel sheet can be made by hot rolling a steel slab under specific conditions, or cold rolling a steel sheet having been hot rolled under conventional conditions, and annealing the resultant cold-rolled steel sheet under specific conditions. Disclosure of the Invention The present invention given in the claims advantageously complies with the above requirements and its object is to offer a cold rolled steel sheet with high strength and high formability having an excellent crushing performance where said steel has both excellent formability and crushing performance (to be more specific, its tensile strength/elongation balance [TS × El] is not less than 24000 MPa % and its dynamic n-value is not less than 0.35) and, in addition, it has an excellent work hardening and bake hardening (i.e., WH + BH is not less than 100 MPa). The term "dynamic n-value" used here has been firstly found by the present inventors as an index for crushing performance and it is now possible by the use of the dynamic n-value to evaluate the crushing performance in more precise manner than before. Thus, in the past, crashworthiness was considered in relation with strength and it was simply believed that the higher the strength, the higher the crashworthiness. However, it has been found now that strength and crashworthiness are not always in such a simple relationship. The present inventors have conducted an intensive investigation on this respect and found and clarified that, when automobiles are crashed, strain rate increases up to 2 × 10 3 /s and that, when energy upon deformation at such a high rate is to be absorbed by steel sheet as much as possible or, in other words, when crashworthiness is to be improved, it is effective that the n-value upon tension deformation of steel sheet under the condition of strain rate = 2 × 10 3 /s (hereinafter, referred to as dynamic n-value) is made high. Here, the momentary n-value when the elongation is 10% is defined as a dynamic n-value. In the meanwhile, it has been also found that, when said dynamic n-value is made high, that is effective in improving the strength in the case of dynamic deformation as well. Now, the history how the present invention has been achieved will be illustrated as hereunder. Thus, in order to achieve the above-mentioned object, the present inventors have at first studied the relation between structure and characteristics in TRIP steel which is a conventional steel. As a result, it has been found that, although production of a bainite phase has been believed to be essential for obtaining a sufficient amount of retained austenite which is advantageous for improving the formability, such a bainite phase is a cause for deteriorating the crushing performance. Therefore, the present inventors suppressed the production of such a bainite phase, especially carbide, or, in other words, changed the minor phase other than the ferrite (polygonal ferrite) which is a major phase from the conventional "bainite + retained austenite" to a complex structure of "acicular ferrite + martensite + retained austenite" whereupon an unexpectedly favorable result has been achieved. The present invention is based upon the above-mentioned finding. Thus, the present invention relates to a cold rolled steel sheet with high strength and high formability having an excellent crushing performance and in having ferrite as a major phase and having a minor phase consisting of martensite, acicular ferrite and retained austenite as given in claim 1. In the present invention, the ratio of the minor phase in the steel structure is 3-40%. Further, the ratios of martensite, retained austenite and acicular ferrite in the minor phase are 10-80%, 8-30% and 5-60%, respectively. More preferably, said steel sheet contains 0.05-0.40 mass % of C; 1.0-3.0 mass % of Si; 0.6-3.0 mass % of Mn; 0.02-1.5 mass % of Cr; 0.010-0.20 mass % of P; and 0.01-0.3 mass % of Al and, if necessary, it may contain at least one component which is selected from 0.005-0.25 mass % of Ti and 0.003-0.1 mass % of Nb as component(s) for improving the strength and may further contain at least one component which is selected from not more than 0.1 mass % of Ca and not more than 0.1 mass % of Rem as component(s) for improving the formability. Brief Explanation of the Drawings Fig. 1 is a representative continuous cooling transformation diagram (CCT diagram) of the conventional TRIP steel; Fig. 2 is a representative continuous cooling transformation diagram (CCT diagram) of the component system of the present invention; Fig. 3(a) is a scheme showing a characteristic phase structure of the minor phase obtained by the present invention while Fig. 3(b) is a scheme showing a phase structure of the minor phase in the conventional TRIP steel; Fig. 4 is a graph showing the relation between the amount of Cr and the tensile strength/elongation balance taking the P-value as a parameter; Fig. 5 is a graph showing the relation between the amount of Cr and the dynamic n-value taking the P-value as a parameter; and Fig. 6 is an illustrative drawing for work hardening property (WH) and bake hardening property (BH). Best Modes for Conducting the Invention The present invention will be specifically illustrated as hereunder. A representative continuous cooling transformation diagram (CCT diagram) of the conventional TRIP steel is shown in Fig. 1. As shown in said Fig. 1, in the conventional TRIP steel, it is heated in a dual phase regions of α and γ during a continuous annealing, then subjected to a rapid cooling down to near 400°C to give rise to a bainite transformation region, retained at this temperature range for several minutes whereby bainite transformation is resulted and, at the same time, solute carbon is concentrated in a untransformed austenite to stabilize and cooled down to room temperature so that not less than several % of austenite is retained there. However, although the TRIP steel manufactured as such has excellent strength and formability, no sufficient crushing performance is achieved as mentioned already. In view of the above, the present inventors have conducted a lot of experiments and investigations for avoiding the bainite transformation and, as a result, they have found the following facts. (1) When a few amounts of Cr are added as a component for the steel, a nose in the bainite transformation region in the above-mentioned CCT diagram comes back to the long time side whereupon the formation of bainite (particularly, the precipitation of carbide) is suppressed and, in place thereof, acicular ferrite is separated out. (2) In a continuous annealing process of cold rolled steel sheets, separation into predetermined amounts of ferrite and austenite is conducted by retaining a temperature range of dual phase region. Accordingly, there is no need of producing the ferrite during cooling stage and that is a big difference from the hot rolling process. In that case however, the start point of pearlite transformation moves to the short time side when Cr is solely added thereto and, accordingly, pearlite comes into the minor phase. When pearlite contaminates as such, very satisfactory result is not achieved even if production of bainite is suppressed. (3) However, when a few amounts of P are added together with Cr, such a pearlite transformation is suppressed whereby a complex structure consisting of acicular ferrite, retained austenite and martensite is formed as the minor phase. (4) The minor phase formed as such which consists of acicular ferrite, retained austenite and martensite significantly improves the crushing performance without deteriorating the formability. A representative CCT diagram in the component system of the present invention is shown in Fig. 2. As shown in said diagram, when small amounts of Cr and P are added, nose of the bainite transformation region decreases while an acicular ferrite region significantly appears. Therefore, when such an acicular ferrite region is retained for a short while and a rapid cooling is conducted after that, it is now possible to make the minor phase in a complex structure consisting of acicular ferrite, retained austenite and martensite and to give a cold rolled steel sheet having both excellent formability and crushing performance. The acicular ferrite used here means that where a long diameter of the grain is about 10 µm or shorter, an aspect ratio is 1:1.5 or more and amount of the precipitated cementite is 5% or less. Incidentally, precipitation of much amount (10% or more) of cementite is noted in bainite of the conventional TRIP steel and, therefore, the acicular ferrite of the present invention is clearly distinguished from bainite of the TRIP steel. The phase structure which is characteristic to the minor phase obtained by the present invention is shown in Fig. 3(a) while the phase structure of the minor phase in the conventional TRIP steel is shown in Fig. 3(b) both in terms of schemes at the centers of the drawings. Around the minor phase, there is ferrite which is a major phase. The minor phase of the conventional TRIP steel has a phase structure in which retained austenite is scattered in bainite while, in the minor phase of the present invention, acicular ferrite and martensite are arranged in layers and retained austenite are scattered on their interface (at the side of martensite). Thus, one of the characteristic features of the present invention is that acicular ferrite is precipitated in the minor phase as such and it is believed that such an acicular ferrite phase increases the TS × El and also increases the dynamic n-value. In addition, when appropriate amounts of martensite and acicular ferrite are arranged in layers, (WH + BH) of as big as 100 MPa or even more can be achieved although the details reasons therefor are ambiguous. Incidentally, according to the knowledge of the present inventors, it has been confirmed that when the interfacial area rate between acicular ferrite and martensite becomes high, there is a tendency that the dynamic n-value becomes big. In the present invention, the ratio of the above-mentioned minor phase in the steel structure is 3-40%. The reason is that, when the ratio of the phase is less than 3%, a sufficient crushing performance is not achieved while, when it is more than 40%, elongation and, as a result thereof, tensile strength/elongation balance become low. More preferred ratio is 10-30%. Incidentally, in the present invention, a steel sample is polished and subj ected an etching with a solution of 2% nitric acid and ethyl alcohol and the phase ratio is calculated by means of an image analysis system of its microscopic picture. With regard to the ratio of each of the phases in the minor phase, martensite is made 10-80% (more preferably, 30-60%), retained austenite is made 8-30% (more preferably, 10-20%) and acicular ferrite is made 5-60% (more preferably, 20-50%). The reasons are as follows. Thus, when the ratio of martensite is less than 10%, a sufficient crushing performance is not achieved while, when it is more than 80%, elongation and, as a result, tensile strength/elongation balance become low. When the ratio of retained austenite is less than 8%, a sufficient elongation is not achieved while, when it is more than 30%, crushing performance lowers. Further, when the ratio of acicular ferrite is less than 5%, good crushing performance is not achieved while, when it is more than 60%, elongation lowers. With regard to the ratio of each of the phases in the whole steel structure, it is suitable that martensite and acicular ferrite is made 5-15% each and that retained austenite is made about 2-10%. In the meanwhile, in the present invention, the steel structure is not always composed of a major phase (consisting of ferrite) and a minor phase (a mixed phase consisting of martensite, acicular ferrite and retained austenite) but an undesireable bainite phase or the like may be separated to some extent. However, even when such a third phase is contaminated and undesireable therein, there is no problem at all in the characteristics of the product provided that its ratio is 10% or less of the minor phase. Now, the reason why the components and their amounts in the steel sheet are limited as mentioned above will be explained as hereunder. C: 0.05-0.40 mass % C is a useful element which not only effectively contributes in making the steel strong but also gives a retained austenite. However, when the amount is less than 0.05 mass %, the effect is poor while, when it is more than 0.40 mass %, ductility lowers. Accordingly, the amount of C is limited to a range of 0.05-0.40 mass %. Si: 1.0-3.0 mass % Si is an essential element for production of retained austenite and, for such a purpose, it must be added at least in an amount of 1.0 mass %. However, addition of more than 3.0 mass % causes not only a decrease in ductility but also a decrease in scale property resulting in a problem of surface quality. Accordingly, the amount of Si is limited to a range of 1.0-3.0 mass %. Mn: 0.6-3.0 mass % Mn is an element which is useful not only for strengthening element but also for giving a retained austenite. However, when the amount is less than 0.6 mass %, the effect is poor while, when it is more than 3.0 mass %, a decrease in ductility is resulted. Accordingly, the amount of Mn is limited to a range of 0.6-3.0 mass %. Cr: 0.02-1.5 mass % Addition of Cr characterizes the present invention and, as a result of addition of Cr, the minor phase gives acicular ferrite as mentioned already. For such a purpose, addition of at least 0.02 mass % of Cr is necessary but, when more than 1.5 mass % is added, coarse and big Cr carbide is produced and, at the same time, production of pearlite proceeds whereby ductility is deteriorated and, moreover, all of tensile strength/elongation balance, dynamic n-value and (WH + BH) become low. Accordingly, the amount of Cr is limited to a range of 0.02-1.5 mass %. Preferably, it is 0.1-0.7 mass %. P: 0.010-0.20 mass P is a useful element which not only effectively contributing to improve the strength by dissolving in ferrite but also suppressing the pearlite transformation which is a cause of deterioration of ductility upon addition of Cr solely, improving a tensile strength/elongation balance by making the minor phase in a structure mainly comprising martensite, acicular ferrite and retained austenite and improving the dynamic n-value and (WH + BH) as well. In order to achieve the above-mentioned effect, addition of at least 0.010 mass % is necessary but, when the amount of as much as more than 0.20 mass % is added, weldability is deteriorated. Accordingly, the amount of P is limited to a range of 0.010-0.20 mass %. Preferred range is 0.02-0.10 mass %. Fig. 4 and Fig. 5 show the result on the investigation for the relation of the amount of Cr with the tensile strength/elongation balance and also with the dynamic n-value taking the amount of P as a parameter. It is apparent from Figs. 4 and 5 that, within such ranges that the amount of Cr is 0.02-1.5 mass % and that the amount of P is not less than 0.010 mass %, the requirements of TS x El ≧ 24000 (MPa.%) and of dynamic n-value ≧ 0.35 are satisfied achieving excellent formability and crushing performance. Especially when the amount of P is 0.020 mass % or more, far better characteristic value is obtained where the dynamic n-value is 0.37 or more. Al: 0.01-0.3 mass % Al effectively contributes as a deoxidizer and, for such a purpose, the content of at least 0.01 mass % is necessary while, even when it is added in an amount of more than 0.3 mass %, the effect is saturated and, rather, the disadvantage in terms of cost is significant. Accordingly, the amount of Al is limited to a range of 0.01-0.3 mass %. Basic components are mentioned as hereinabove and, besides them, Ti and Nb may be added as components for improving the strength and Ca and Rem may be added as components for improving formability within a range as mentioned below. Ti: 0.005-0.25 mass %; Nb: 0.003-0.1 mass % Both Ti and Nb effectively contribute to improvement in strength and, therefore, they may be added if necessary. However, when the amount is too little, the effect by addition is poor while, when it is too much, a decrease in ductility is resulted. Accordingly, it is preferred to add them within the above-mentioned range. Ti and Nb are also useful in preventing a intergranular cracking at the edge which is apt to generate upon hot rolling of medium carbon steel of the kind of the present invention. Ca: 0.1 mass % or less; Rem: 0.1 mass % or less Ca and Rem effectively control the shape of oxides and sulfides and effectively contribute to improvement in formability, particularly in stretch flanging formability. However, when each of the amounts is more than 0.1 mass %, the effect is saturated and, moreover, cracking is apt to take place during hot rolling. Accordingly, it is preferred that each of them is added in an amount of 0.1 mass % or less. Incidentally, it is preferred that each of Ca and Rem is added in an amount of 0.0003 mass % or more for steadily achieving the above-mentioned effect. Now the method for the manufacture of the steel of the present invention will be mentioned. To sum up, a complex structure consisting of martensite, acicular ferrite and retained austenite is to be formed in the steel of the present invention as the minor phase and, therefore, cooling is to be conducted along a cooling curve as shown in Fig. 2. Thus, the hot rolled sheet obtained by means of a hot rolling by usual method is descaled by means of pickling or the like and then subjected to a cold rolling with a pressure reduction rate of not less than 30% or, preferably, 50-80% to give a cold rolled sheet. Then the resulting cold rolled sheet is heated by a continuous annealing to a dual phase region of ferrite and austenite at about 740-820°C, retained at that temperature or gradually cooled at the rate of not higher than 10°C/second, then cooled from 600°C or higher to the acicular ferrite region of 350-450°C at the rate of 20-60°C/second and kept at that temperature (or cooled gradually) for 0.5-5 minutes. After that, it is cooled down to room temperature at the rate of not higher than 50°C/second to form the minor phase consisting of acicular ferrite, martensite and retained austenite. Among the above-mentioned manufacturing steps, the characteristic feature as a cycle for continuous annealing is that a desired effect can be achieved by a relatively slow rate for cooling down to 350-450°C as compared with the cooling rate disclosed in the prior art such as the above-mentioned Japanese Examined Patent Publication Hei-05/064215 and Laid-Open Patent Publication Hei-04/333524. Thus, in the prior art, cooling is conducted at the rate of 50°C/second or higher in the former literature and at the rate of around 10-200°C/second in the latter one for forming the minor phase mainly comprising bainite and retained austenite. In manufacturing the steel sheet of the present invention however, the cooling rate is made as slow as 60°C/second or lower to give a desired structure. Thus, as a cooling means, there is no need of applying a mist cooling or a water cooling which requires a high cost but cooling by gas jet or roll is sufficient. Accordingly, the steel so manufactured is advantageous in terms of not only the cost but also the surface property. With regard to the retention time at an acicular ferrite region at 350-450°C, it is essential to make its upper limit six minutes. This is because if the retention time at the acicular ferrite is too long, bainite is produced whereby the minor phase which is a desired structure is not achieved. Incidentally, in the above-mentioned prior art literatures, the upper limits for the retention time are mentioned as 10 minutes and 20 minutes, respectively. Accordingly, it is quite apparent that the structure of the minor phase of the present invention is entirely different from that in the prior art. Examples Steel slabs of various compositions as shown in Table 1 were heated at 1200°C, then subjected to a finishing hot-rolling at 860°C and coiled at 580°C to give a hot rolled steel sheet having a thickness of 3.2 mm. Then, after the sheet was subjected to a pickling, it was subjected to a cold rolling to an extent of 1.2 mm. After that, it was heated up to 800°C at the rate of 10°C /second using a continuous annealing furnace, retained at that temperature for 40 seconds, gradually cooled down to 635°C at the rate of 4°C/second, then cooled down to an acicular ferrite region of 410°C at the rate of 43°C/second, retained at that temperature for 180 seconds and cooled down to room temperature at the rate of 10°C/second. After that, a temper rolling of 1.0% was conducted. Tensile test pieces were cut out from the resulting cold rolled sheet and each of the test pieces was subjected to a tensile test under the condition where a strain rate was 2 × 10 -2 /s to determine yield strength (YS), tensile strength (TS) and elongation (El). In addition, a material for Hopkinson bar impact tensile test ( Zairyo to Purosesu , vol. 9, (1996), pages 1108-1111) was used and subjected to a tension test under the condition where a strain rate was 2 x 10 3 /s whereupon the momentary n-value (dynamic n-value) when the elongation was 10% was determined. Further, a hole expansion test was conducted using a conical punch having a top angle of 60° under the conditions with guide hole, which is 10 mm diameter, pierced by 12.5% of clearance. Stretch flanging formability (λ) was calculated according to the following formula. λ = [(d 1 - d 0 )/d 0 ] × 100 In the formula, d 0 is diameter of a guide hole; and d 1 is diameter of a hole when cracks passing through the sheet are formed around the hole upon expansion of the hole. Furthermore, amount of work hardening (WH) upon press molding and amount of bake hardening (BH) upon painting/baking (170°C) thereafter were measured as well. Incidentally, WH and BH were determined from Fig. 6 using a tensile tester having a strain rate of 2 × 10 -2 /s. Steel structure, TS × El balance, dynamic n-value, stretch flanging formability and WH + BH were tested for each of the cold rolled steel sheets and the results are shown in Table 2 and Table 3. It is apparent from Tables 2 and 3 that all of the product where a complex structure of martensite, acicular ferrite and retained austenite was formed as the minor phase in accordance with the present invention showed excellent tensile strength/elongation balance and crushing performance which were as good as TS × El ≧ 24000 MPa.% and dynamic n-value ≧ 0.35, respectively and, in addition, it further showed a good work and bake hardenings of WH + BH ≧ 100 MPa as well. When Ca and Rem were further added, it is also possible to improve a stretch flanging formability. Industrial Applicability When a maj or phase is ferrite and a minor phase is a complex structure consisting of martensite, acicular ferrite and retained austenite in accordance with the present invention, it is now possible to afford a cold rolled steel sheet which shows both excellent formability and crushing performance. As a result thereof, under the current status where weight reduction of automobiles has been aimed and safety of automobiles has been also seriously considered, it is possible to give cold rolled steel sheet having an excellent property in terms of an object of crushing performance which has been receiving public attention in recent years as a yardstick for safety upon crash. (mass %) Steel No. C Si Mn Cr P Al Ti Nb Others Remarks 1 0.11 1.23 1.35 0.13 0.031 0.034 - - - Examples of the Invention 2 0.15 1.71 1.18 0.21 0.071 0.028 - - - " 3 0.21 1.05 2.02 0.33 0.041 0.051 - - - " 4 0.10 1.21 0.71 0.58 0.031 0.033 - - - " 5 0.13 1.02 1.51 0.23 0.027 0.022 - - - " 6 0.12 1.39 1.87 0.03 0.029 0.070 - - - " 7 0.24 1.41 1.02 1.17 0.015 0.052 - - - " 8 0.08 1.29 1.18 0.25 0.181 0.041 - - - " 9 0.11 1.25 1.50 0.12 0.049 0.035 0.008 - - " 10 0.14 1.24 0.80 0.12 0.048 0.039 0.021 - - " 11 0.15 2.18 1.99 0.19 0.049 0.029 0.051 - - " 12 0.16 2.31 2.31 0.12 0.059 0.035 - 0.007 - " 13 0.18 1.24 0.85 0.12 0.049 0.069 - 0.029 - " 14 0.11 1.22 1.57 0.12 0.049 0.035 - 0.230 - " 15 0.12 1.39 1.81 0.51 0.027 0.081 0.024 0.017 - " 16 0.12 1.31 1.43 0.25 0.041 0.051 - - Ca.0.0013 " 17 0.15 1.13 1.27 0.33 0.059 0.029 0.026 - Rem:0.009 " 18 0.04 1.21 1.51 0.19 0.044 0.035 - - - Examples for Comparison 19 0.43 1.21 1.61 0.18 0.051 0.035 - - - " 20 0.12 0.92 1.29 0.17 0.080 0.039 - - - " 21 0.11 3.30 1.33 0.24 0.099 0.035 - - - " 22 0.09 1.22 0.55 0.39 0.021 0.041 - - - " 23 0.14 1.39 3.10 0.38 0.120 0.029 - - - " 24 0.17 1.49 1.39 0.01 0.056 0.033 - - - " 25 0.16 1.51 1.39 1.67 0.061 0.029 - - - " 26 0.11 1.22 1.28 0.39 0.008 0.027 - - - " 27 0.10 1.29 1.20 0.21 0.240 0.069 - - - " 28 0.10 1.33 1.20 0.18 0.043 0.40 - - - " Steel No. Structure of the Minor Phase Ratio of the Minor Phase Ratios of Components of the Minor Phase (%) Remarks M AF γ P 1 M+AF+γ 16 72 16 12 0 Examples of the Invention 2 " 15 48 31 21 0 " 3 " 24 61 9 30 0 " 4 " 22 34 42 24 0 " 5 " 28 46 37 17 0 " 6 " 16 45 46 9 0 " 7 " 14 40 45 15 0 " 8 " 20 41 32 27 0 " 9 " 22 31 55 14 0 " 10 " 26 35 45 20 0 " 11 " 24 52 21 27 0 " 12 " 27 19 58 23 0 " 13 " 19 17 54 29 0 " 14 " 19 29 46 25 0 " 15 " 16 58 15 27 0 " 16 " 17 61 9 30 0 " 17 " 18 45 35 20 0 " 18 M+AF+B+P 11 13 35 0 2 Examples for Comparison0 19 M+AF+γ+B 13 51 2 3 0 " 20 M+AF+B 16 34 21 0 0 " 21 M+B 8 41 0 0 0 " 22 B 18 0 0 0 0 " 23 M+B+P 24 35 0 0 5 " 24 B+γ 19 0 0 10 0 " 25 M+P 27 98 0 0 2 " 26 M+AF+P 27 56 26 0 18 " 27 M+B 20 59 0 0 0 " 28 B+γ 16 0 0 13 0 " M: Martensite; AF: Acicular Ferrite; γ: Retained Austenite; B: Bainite; P: Pearlite Steel No. YS (MPa) TS (MPa) El (%) TS×El (MPa·%) Dynamic Value n- Stretch Flanging Formability WH+BH (MPa) Remarks 1 453 651 41 26691 0.42 55 134 Examples of the Invention 2 446 643 41 26363 0.41 61 128 " 3 492 704 38 26752 0.37 61 137 " 4 483 624 41 25584 0.38 70 128 " 5 469 637 42 26754 0.39 52 125 " 6 467 647 39 25233 0.39 58 124 " 7 505 697 37 25789 0.36 50 121 " 8 482 678 39 26442 0.38 51 118 " 9 472 683 36 24588 0.39 58 116 " 10 494 695 35 24325 0.39 63 107 " 11 529 739 34 25126 0.40 53 105 " 12 506 704 35 24640 0.37 67 113 " 13 514 691 37 25567 0.37 63 115 " 14 497 718 35 15130 0.37 60 105 " 15 482 684 36 24624 0.37 52 119 " 16 467 674 37 24938 0.37 84 118 " 17 501 721 37 26677 0.37 80 122 " 18 456 637 28 17836 0.32 51 88 Examples for Comparison 19 472 669 31 20739 0.30 52 81 " 20 466 653 29 18937 0.32 55 89 " 21 435 624 30 18720 0.31 55 93 " 22 531 651 24 15624 0.25 60 86 " 23 527 721 25 18025 0.30 58 91 " 24 549 645 39 25155 0.24 60 75 " 25 462 693 32 22176 0.38 47 98 " 26 509 654 30 19620 0.32 54 96 " 27 518 679 30 20370 0.33 54 91 28 523 668 39 26052 0.25 56 81

Claims: Cold rolled steel sheet with high strength and high formability having an excellent crushing performance and having ferrite as a major phase and having a minor phase consisting of martensite, acicular ferrite and retained austenite, in which the ratio of the minor phase in the steel structure is 3-40 %, and in which minor phase the ratios of martensite, retained austenite and acicular ferrite are 10-80 %, 8-30 % and 5-60 %, respectively. Cold rolled steel sheet with high strength and high formability having an excellent crushing performance according to'claim 1 in which said steel sheet contains 0.05-0.40 mass % of C, 1.0-3.0 mass % of Si, 0.6-3.0 mass % of Mn, 0.02-1.5 mass % of Cr, 0.010-0.20 mass % of P and 0.01-0.3 mass % of Al while the remained part substantially consists of Fe. Cold rolled steel sheet with high strength and high formability having an excellent crushing performance according to claim 2 in which said steel sheet contains at least one component selected from 0.005-0.25 mass % of Ti and 0.003-0.1 mass % of Nb. Cold rolled steel sheet with high strength and high formability having an excellent crushing performance according to claim 2 or 3 in which said steel sheet contains at least one component selected from 0.1 mass % or less of Ca and 0.1 mass % or less of Rem.

Inventors: FURUKIMI OSAMU, MIURA KAZUYA, OBARA TAKASHI, SAKATA KEI, TAKAGI SYUSAKU, FURUKIMI, OSAMU, MIURA, KAZUYA, OBARA, TAKASHI, SAKATA, KEI, TAKAGI, SYUSAKU, FURUKIMI, Osamu, Kawasaki Steel Corporation, MIURA, Kazuya, Head Office, Kawasaki Steel Co., Obara, Takashi, Kawasaki Steel Corporation, SAKATA, KEI, KAWASAKI STEEL CORPORATION, TAKAGI, Syusaku, Kawasaki Steel Corporation
Applicants: JFE STEEL CORP, JFE STEEL CORPORATION
Application year: 1998
Main classification: C22C38
IPC codes: C22C38