Water-soluble photoresist composition

Abstract: A water-soluble photoresist composition is provided which comprises a water-soluble photosensitive composition containing casein and a water-soluble photosensitive agent and at least one kind of calcium salt of organic acid. The composition has excellent sensitivity, resolution, and etching resistance and can be used for the production of highly refined electronic components such as shadow masks, lead frame, etc.

Description: FIELD OF THE INVENTION The present invention relates to a water-soluble photoresist composition used for the process utilizing photolithography in the production of shadow mask of the color cathode-ray tube, IC lead frame, mesh for Vacuum Fluorescent Display, color filter, black matrix, etc., which are being made fine, particularly to a water-soluble photoresist composition having improved etching resistance as well as good sensitivity and resolution. BACKGROUND OF THE INVENTION The shadow mask used for the color cathode-ray tube is usually produced by the following process. Namely, decarbonized aluminum killed steel (hereinafter referred to as AK material) having a plate thickness of 25 µm to 0.3 mm or Inver-type iron alloy (hereinafter referred to as Inver material) containing 36% of nickel having small thermal expansion coefficient is used as a substrate. Their surfaces are refined by degreasing and washing with water, and coated with a water-soluble photoresist followed by drying to make a film. Then, the mask pattern having a desired image at the position corresponding to the electron beam passing pores is brought into contact with the above film to effect exposure to ultraviolet ray. After the steps of development, hardening and heat treatment, a corrosion resistant film (resist film) with a desired pattern is formed on the substrate. After the metal part where the resist film has been removed by the development is subjected to etching using an etching solution such as ferric chloride or the like to form a number of electron beam passing pores, the remaining resist film is removed using a warm alkaline solution (for example, a 10 to 20% aqueous solution of sodium hydroxide), thereby obtaining the shadow mask. Electronic components such as IC lead frame, mesh for Vacuum Fluorescent Display, printed wiring board, and the like are also produced in the similar manner as in the production of the shadow mask using as a substrate copper, copper alloy, iron materials, 42 Ni-iron alloy (hereinafter referred to as 42 alloy), stainless steel, and the like. Photoresists that are used for etching (hereinafter referred to as resists) are water-soluble negative working resists having such advantages that they are inexpensive, are not inflammable, and can be treated in aqueous solutions over the whole steps. The photoresists are prepared by adding ammonium dichromate to an aqueous solution of water-soluble polymer such as casein, polyvinyl alcohol, fish glue, and the like in an amount of 3 to 15% based on the water-soluble polymer, thereby achieving photosensitivity. For these resists for etching, dichromate such as ammonium dichromate is used as a photosensitive agent and chromic anhydride is used as a hardener. Since these hexavalent chromium compounds are harmful, discharge of waste water containing them is strictly regulated. The water-soluble photoresists without using hexavalent chromium (hereinafter referred to as no chromium etching resist) have been reported. They include the combination of fish glue and ferric salt, polyvinyl alcohol (hereinafter referred to as PVA) and diazo resin (Japanese Patent Publication No. Sho 56-20541 and Japanese Patent Publication No. Sho 57-6098), a water-soluble photosensitive resin containing several molar percent of N-methyl-γ-(p-formylstyryl)pyridinium sulfate (Japanese Patent Application Laid-open No. Sho 55-23163), casein and water-soluble azide compound (Japanese Patent Publication No. Sho 41-7100 and U.S. Patent No. 2,692,826), water-soluble acrylic resin having ethylenic unsaturated bonding at its side chain, anthraquinone sulfonate, and water-soluble azide compound (Japanese Patent Publication No. Sho 54-12331), and the like. However, these are not still satisfactory in view of sensitivity, resolution, and etching resistance. As electronic components such as shadow masks and lead frames are produced in a large quantity and are highly refined, it has been desired to further improve sensitivity, resolution, and etching resistance of the resists. Especially, casein-based no chromium etching resist having practical sensitivity, resolution, and etching resistance has been strongly demanded. SUMMARY OF THE INVENTION As a result of intensive investigation in order to solve the above problems, the present inventors have found that a water-soluble photoresist composition that can solve the above problems can be obtained by adding at least one kind of calcium salts of organic acids to a water-soluble photosensitive composition containing casein and a water-soluble photosensitive agent. Based on this finding, the present invention was completed. DETAILED DESCRIPTION OF THE INVENTION The calcium salt of organic acid to be used in the present invention is water-soluble or a compound that can be dissolved or dispersed in a water-soluble photosensitive composition and that does not interfere its photosensitivity. Specific examples thereof include calcium aspartate, calcium acetate, calcium formate, calcium glycerophosphate, calcium gluconate, calcium glycolate, calcium lactate, calcium pantothenate, calcium lactobionate, and calcium glutamate. A preferable calcium salt of organic acid has a molecular weight of not more than 1000. According to the present invention, the calcium salts of organic acid (hereinafter referred to as the compound of the present invention) are added in the form of being dissolved in water or directly added to an aqueous solution of a water-soluble photosensitive composition containing casein and a photosensitive agent. However, the method of addition of the compounds of the present invention is not limited to the above. Metal substrate such as copper, iron, and their alloy, anodized aluminum, silicon, or non-metallic substrate such as glass, ceramics, or plastic film made of polyethylene terephthalate are coated with the photoresist compositions containing the compounds of the present invention, then dried to form a resist film having a film thickness of 0.1 to 10 µm, which is not particularly restricted. The formed resist film is subjected to an imagewise exposure, developed using an aqueous developing solution, and if necessary, hardened to form relief patterns. Though varying depending on the kind of the water-soluble photosensitive agent, the addition of the compound of the present invention improves sensitivity and resolution of the resists. One of examples of the hardening treatment comprises thermal hardening of the relief pattern at 150 to 300 °C to give a resist coating excellent in etching resistance. Though the mechanism for exhibiting these effects obtained by adding the compounds of the present invention has not been elucidated yet, it is assumed that a kind of bonding via Ca 2+ between proteins in casein micelle is formed by adding compound of the present invention to more closely contact the resist with the substrate after the photochemical reaction, thereby improving photosensitivity, resolution, and etching resistance. The compounds of the present invention may be used alone or two or more thereof in combination. The content of the compound of the present invention ranges from 0.1 to 20 wt%, preferably 1.0 to 15 wt%, based on the weight of casein contained in the water-soluble photosensitive composition. If its content is less than 0.1 wt%, a photosensitivity-improving effect is weak. If its content is more than 20 wt%, the particle size of casein micelle becomes large, which affects the stability of the resist solution. The casein component to be used in the water-soluble photosensitive composition of the present invention may be acid casein such as lactic casein, hydrochloric casein and sulfuric casein, sodium caseinate, and calcium caseinate. Particularly, in view of stability, it is preferable to use an aqueous casein solution prepared by dissolving acid casein in water containing amines such as ammonia, triethylamine, or the like or inorganic alkali agent such as borax, sodium carbonate, sodium hydroxide, or the like. Moreover, a water-soluble photosensitive composition described by Japanese Patent Publication No. Sho 60-46420 (and U.S. Patent Application No. 772,996) can be used. These are marketed as, for example, trade names, "FR-15", "FR-16", and "FR-17" (all of these manufactured by Fuji Chemicals Industrial Co., LTD.), or "MR-SLG", "MR-SMG", and "MR-SG" (all of these manufactured by The Inctec Inc.) and, therefore, are commercially available. The water-soluble photosensitive agent used in the present invention is a photosensitive agent to be dissolved in the above-described aqueous solution of casein, including, for example, dichromate such as ammonium dichromate, water-soluble azide compounds, and onium salts (e.g., 2-naphthoylmethyltetramethylenesulfoniumtrifluoromethanesulfonate). A bisazide compound or, compound containing three or more azide groups is used as a photo-crosslinking agent as for the water-soluble azide compound. The compound can also be used in the present invention. Examples of such a photo-crosslinking agent include high molecular water-soluble azide compound such as 4,4'-diazidostilbene-2,2'-disulfonate, 4,4'-diazidobenzalacetone-2,2'-disulfonate, 2,5-(4,4'-diazidobenzal)cyclohexanone-2,2'-disulfonate, or maleic acid-sodium vinylmonoazidobenzylideneacetophenonesulfonate copolymer. They are usually used as sodium salt or potassium salt, or salt of tetramethylammonium hydroxide. Two or more of the photosensitive agents may be used taking account of solubility in water and spectrum of a light source. As the water-soluble organic photosensitive agent, high molecular ones can achieve high sensitivity as compared with low molecular ones. For example, the sensitivity of the water-soluble photosensitive composition prepared by adding dimethylacrylamide-vinylazidobenzylideneacetophenonesulfonate copolymer (molar ratio, 2 : 1, weight-average molecular weight, 20000) is more than three times higher than that prepared by adding sodium 4,4'-diazidostilbene-2,2'-disulfonate. The content of the water-soluble photosensitive agent in the water-soluble photosensitive composition is in an amount within the range usually used. For example, the amount of the water-soluble azide compound dissolved in the water-soluble photosensitive composition is ranging from 1 to 10 parts by weight per 100 parts by weight of casein. The photoresist composition of the present invention is prepared by adding a calcium salt of organic acid to the water-soluble photosensitive composition containing casein and the water-soluble photosensitive agent. If necessary, the photoresist composition may further contain a preservative, an antifungal agent, a coloring material, a plasticizer, a crosslinking agent, a sensitizer (e.g., thioxanthone-4-sulfonate, etc.), and an adhesion-promoting agent. In the case of using a metal substrate having poor adhesive property to the water-soluble resist, it is possible to add one or two or more of adhesion-promoting agents selected from γ -aminopropyltrimethoxysilane, N-(β-aminoethyl)γ -propylmethyl-dimethoxysilane, and N-(β-aminoethyl)γ -aminopropyltrimethoxysilane. The substrate is coated with the water-soluble photoresist composition of the present invention to a film thickness of about 0.1 to 10 µm by the conventionally used method such as whirling coating method, dip coating method, flow coating method, and the like, followed by drying. After exposure for image, unexposed parts are removed by dissolving (water development) to form resist patterns. The thus-formed resist patterns are hardened by heating to improve resist property, then the substrate is treated with an etching solution. The water-soluble photoresist composition of the present invention shows improved sensitivity, resolution, and etching resistance by adding a calcium salt of organic acid to the water-soluble photosensitive composition containing casein and the water-soluble photosensitive agent. Therefore, the water-soluble photoresist composition can suitably be used for the production of shadow mask of the cathode-ray tube, IC lead frame, mesh for Vacuum Fluorescent Display, printed wiring board, color filter, black matrix, which are being made fine. Since the composition of the present invention is water-soluble, it has such advantages that preparation of the composition, formation of the resist film, development, etching, and the like treatment can be done in aqueous solutions. Further, a composition can be prepared without using hexavalent chromium that is a harmful substance. A chromium-free etching resist composition is obtained, which has good adhesiveness to metal materials and is practically usable. Thus, it is advantageous in safety during operation and in view of environmental hygiene. The following Examples and Comparative Examples are given to illustrate the present invention in more detail, but are not to be construed to limit the scope of the present invention. EXAMPLE 1 10 g of a 10% ammonium dichromate aqueous solution was added to 100 g of an aqueous casein solution ([FR-17] manufactured by Fuji Chemicals Industrial Co., LTD. containing 12.01 wt% of casein) to give a water-soluble resist solution. After dissolving 0.6 g of calcium acetate in the resist solution, the mixture was allowed to stand in the dark for 2 hours and subjected to defoaming treatment to prepare an aqueous solution of the water-soluble resist composition of the present invention. 42 alloy having a thickness of 0.3 mm was immersed in a 3% aqueous solution of Jusco Clean No. 5 (aqueous alkali solution manufactured by Nippon Hyomen Kagaku Kabushiki Kaisha) for 2 minutes for degreasing. It was washed with water and dried to serve as a substrate. The substrate was coated with the resist composition as prepared above to a thickness of 6 µm using whirler. The coated plate was dried (prebaked) in a hot-air thermostatic drying chamber at 60 °C for 10 minutes. The thus-formed resist film was exposed to an ultraviolet ray of not shorter than 300 nm at the dose of 400 mJ/cm 2 using a superhigh pressure mercury vapor lamp, with bringing it into close contact under vacuum with a resolution chart manufactured by Toppan Printing Co., Ltd. and Kodak Photographic Step Tablet No. 2 (hereinafter referred to as gray scale). Then, this was immersed in tap water of 25 °C for 45 seconds. Unexposed parts were dissolved, washed with water, and dried with a dryer. The resulting resist coating film was postbaked in a hot-air thermostatic drying chamber at 200 °C for 10 minutes. This resist showed so high sensitivity that the layer remained up to 7.5 steps (hereinafter expressed as gray scale sensitivity of 7.5). As to resolution, there was no fringe of the remaining film due to tail drawing of the unexposed parts and the resist pattern showed the line and space resolution of 10 µm (hereinafter referred to as 10 µm L/S). The 42 alloy plate having this resist pattern was immersed in a ferric chloride solution of 45° Be' at 70 °C for 20 minutes, and the surface of the resist film coating was observed. As a result, no swelling or peeling of the film was observed, which revealed that it had sufficient etching resistance. The results are shown in Table 1. COMPARATIVE EXAMPLE 1 A resist pattern was produced and its etching resistance was examined in the same manner as in Example 1 except for using the water-soluble resist composition (Comparative Example 1) which did not contain calcium acetate used in Example 1. The results are shown in Table 1. EXAMPLES 2 AND 3 A resist pattern was produced and its etching resistance was examined in the same manner as in Example 1 except for using the water-soluble resist composition which contained calcium gluconate or calcium lactobionate each in an equivalent amount in place of calcium acetate used in Example 1. The results are shown in Table 1. As can be seen from the results shown in Table 1, the water-soluble resist compositions of the present invention had high sensitivity and good resolution. Etching resistance of the compositions containing the calcium salt of organic acid was quite well compared with that of the composition containing no calcium salt of organic acid. Kind of additives Sensitivity (step) Resolution of L/S (µm) Etching resistance Appearance of resist solution Ex. 1 calcium acetate 7.5 10 good turbid Ex. 2 calcium gluconate 5.0 10 good same as Comparative Example 1 Ex. 3 lactobionic acid calcium salt 5.0 10 good same as Comparative Example 1 Com. Ex. 1 none 4.5 10 to 15 good whity and transparent solution (Ex. means Example and Com. Ex. means Comparative Example.) Note: The appearance of the resist solution shown in Table 1 showed preceeding states that before the photosensitive agent was added to the casein solution containing the compound of the present invention. EXAMPLE 4 In 100 g of an aqueous casein solution ([FR-17] manufactured by Fuji Chemicals Industrial Co., LTD. was dissolved 0.5 g of calcium glycolate, and then 10 g of purified water and 0.36 g of sodium 4,4'-diazidostilbene-2,2'-disulfonate as a photosensitive agent. The solution was filtrated and defoamed to obtain an aqueous solution of the water-soluble resist composition of the present invention. The 42 alloy plate which had been subjected to the degreasing treatment in the same manner as in Example 1 was coated with this solution using a whirler. The thickness of this formed film was 6 µm. The resulting plate was dried in a hot-air thermostatic drying chamber at 80 °C for 10 minutes. The thus-formed resist film was exposed to an ultraviolet ray at the dose of 400 mJ/cm 2 using a superhigh pressure mercury vapor lamp, with bringing it into close contact with the resolution chart and the gray scale. Then, this was immersed in tap water of 25 °C for 30 seconds. Unexposed parts were dissolved and washed with water. After draining water, it was dried with a dryer. The resulting resist coating film was hardened by heating at 250 °C for 10 minutes. The gray scale sensitivity of this resist was so high as 5.5 step, which compared quite well with that in the case of a photosensitive composition containing a dichromate salt. With respect to resolution, 15 µm of L/S on the resolution chart was resolved without any remaining film at the unexposed parts. Even after the 42 alloy plate having this resist pattern was immersed in a ferric chloride solution of 45° Be' at 70 °C for 20 minutes and washed with water, the resist coating film was completely durable. To examine dark reaction of this resist, the 42 alloy plate coated with the resist was allowed to stand as it is, and, after exposure, was also allowed to stand as it is. As a result, almost no change was observed in sensitivity after 10 days or more. COMPARATIVE EXAMPLE 2 A resist solution was prepared in the same manner as in Example 4 except for using the water-soluble resist composition which did not contain calcium glycolate (Comparative Example 2) used in the composition of Example 4 (no chromium etching resist composition) and examined its sensitivity, resolution, and etching resistance. The results are shown in Table 2. The sensitivity was low due to no existence of the organic calcium salt of the present invention and, since the surface of the resist pattern was swelled, even a line of 50 µm width meandered. With respect to etching resistance, the film was peeled off even at 70 °C for 10 minutes. EXAMPLES 5 to 12 A resist solution was prepared in the same manner as in Example 4 except for using the water-soluble resist composition which contained respectively calcium gluconate, calcium acetate, calcium L-aspartate, calcium glycerophosphate, calcium lactate, calcium formate, calcium glutamate, or calcium pantothenate each in an equivalent amount in place of calcium glycolate used in Example 4. The sensitivity, resolution and etching resistance were examined in the same manner as in Example 4. The results are shown in Table 2 as well as the results of Example 4 and Comparative Example 2. The water-soluble resist composition containing the compound of the present invention had high sensitivity and the resist pattern corresponding to 15 to 20 µm L/S was resolved. It was also found that etching resistance was improved to the practical level. Kind of additives Sensitivity (step) Resolution (µmm) Etching resistance immersed at 70 °C for 20 minutes Ex. 4 calcium glycolate 5.5 15 o ○ Ex. 5 calcium gluconate 3.5 20 ○ Ex. 6 calcium acetate 4.5 15 o ○ Ex. 7 calcium L-aspartate 4.0 15 o ○ Ex. 8 calcium glycerophosphate 3.5 20 ○ Ex. 9 calcium lactate 3.5 20 ○ Ex. 10 calcium formate 3.5 20 ○ Ex. 11 calcium L-glutamate 4.5 15 o ○ Ex. 12 calcium pantothenate 3.0 20 ○ Com. Ex. 2 none 1.5 surface swelled × (Ex. means Example and Com. Ex. means Comparative Example.) Note: The symbols for etching resistance shown in Table 2 had the following meanings: o ○ : The surface of the resist film was not affected by a ferric chloride solution at all. ○ : The color of the surface of the resist film was slightly changed by a ferric chloride solution × : The resist film was peeled off in a ferric chloride solution

Claims: A water-soluble photoresist composition comprising casein and a water-soluble photosensitive agent and at least one kind of calcium salt of organic acid. The water-soluble photoresist composition as claimed in claim 1, wherein said calcium salt of organic acid is contained in an amount of 0.1 to 20 parts by weight based on 100 parts by weight of casein. The water-soluble photoresist composition as claimed in claim 1, wherein said calcium salt of organic acid is calcium aspartate, calcium formate, calcium acetate, calcium glycerophosphate, calcium gluconate, calcium glycolate, calcium lactate, calcium pantothenate, calcium lactobionate or calcium glutamate.

Inventors: ASANO TAKATERU, UMEHARA HIROSHI, ASANO, TAKATERU, UMEHARA, HIROSHI
Applicants: FUJI CHEM IND CO LTD, FUJI CHEMICALS INDUSTRIAL CO., LTD.
Application year: 1998
Main classification: G03F7
IPC codes: H01J9, G03F7, C23F1, C08K5, C08L89, G02B5