GROUP 8-10 TRANSITION METAL OLEFIN POLYMERIZATION CATALYSTS

Abstract: Provided are certain transition metal complexes which are useful as catalysts in the polymerization of olefinic monomers. In particular, the invention provides complexes of certain bidentate ligands bonded to Ni, Pd, Co, or Fe, and optionally, one or more neutral Lewis acids, and their use in the polymerization of olefins.

Description: GROUP 8-10 TRANSITION METAL OLEFIN POLYMERIZATION CATALYSTS CROSS-REFERENCES TO RELATED APPLICATIONS This Application claims the benefit under 35 U.S.C. § 119 (e) of Provisional Application Serial No. 60/044691, filed April 18, 1997; Provisional Application Serial No. 60/045333, filed May 1 , 1997; and Provisional Application Serial No. 60/045355, filed May 2, 1997. Field Of The Invention The present invention is directed to olefin polymers, such as polyethylene, polypropylene, and copolymers of ethylene and propyiene, and to the preparation of such olefin polymers. These polymers include homopolymers of olefins, as well as copolymers of different olefins. The present invention is also directed to the processes of making these olefin polymers, which typically use a transition metal complex, in which the transition metal is a Group 8-10 metal, as the polymerization catalyst. The polymers have a wide variety of applications, including use as packaging materials and adhesives. In addition, the present invention is directed to catalysts for the polymerization of olefins. Bac qround of the Invention Olefin polymers are used in a wide variety of products, from sheathing for wire and cable to film. Olefin polymers are used, for instance, in injection or compression molding applications, in extruded films or sheeting, as extrusion coatings on paper, for example photographic paper and digital recording paper, and the like. Improvements in catalysts have made it possible to better control polymerization processes, and, thus, influence the properties of the bulk material. Increasingly, efforts are being made to tune the physical properties of plastics for lightness, strength, resistance to corrosion, permeability, optical properties, and the like, for particular uses. Chain length, polymer branching and functionality have a significant impact on the physical properties of the polymer. Accordingly, novel catalysts are constantly being sought in attempts to obtain a catalytic process which permits more efficient and better controlled polymerization of olefins. Conventional polyolefins are prepared by a variety of polymerization techniques, including homogeneous and heterogeneous polymerizations. Certain transition metal catalysts, such as those based on titanium compounds (e.g. T1CI3 or TiCU) in combination with organoaluminum cocatalysts, are used to make linear and linear low density polyethylenes as well as poly-α-olefins such as polypropylene. These so-called "Ziegler- Natta" catalysts are quite sensitive to oxygen and are ineffective for the copolymerization of nonpolar and polar monomers. Recent advances in non-Ziegler-Natta olefin polymerization catalysis include the following: L. K. Johnson et aL, WO Patent Application 96/23010, disclose the polymerization of olefins using cationic nickel, palladium, iron, and cobalt complexes containing diimine and bisoxazoline ligands. This document also describes the polymerization of ethylene, acyclic olefins, and/or selected cyclic olefins and optionally selected unsaturated acids or esters such as acrylic acid or alkyl acrylates to provide olefin homopolymers or copolymers; European Patent Application Serial No. 381 ,495 describes the polymerization of olefins using palladium and nickel catalysts which contain selected bidentate phosphorous containing ligands; L. K. Johnson et aL, J. Am. Chem. Soc 1995, 117, 6414, describe the polymerization of olefins such as ethylene, propylene, and 1-hexene using cationic α-diimine-based nickel and palladium complexes. These catalysts have been described to polymerize ethylene to high molecular weight branched polyethylene. In addition to ethylene, Pd complexes act as catalysts for the polymerization and copolymerization of olefins and methyl acrylate. G.F. Schmidt et aL, J. Am. Chem. Soc. 1985, 107, 1443, describe a cobalt(lll) cyclopentadienyl catalytic system having the structure [C 5 Me 5 (L)CoCH 2 CH 2 -μ-H] + , which provides for the "living" polymerization of ethylene. M. Brookhart et aK, Macromolecules 1995, 28, 5378, disclose using such "living" catalysts in the synthesis of end-functionalized polyethylene homopolymers; U. Klabunde, U. S. Patent Nos. 4,906,754, 4,716,205, 5,030,606, and 5,175,326, describes the conversion of ethylene to polyethylene using anionic phosphorous/oxygen donors ligated to Ni(ll). The polymerization reactions were run between 25 and 100°C with modest yields, producing linear polyethylene having a weight-average molecular weight ranging between 8K and 350 K. In addition, Klabunde describes the preparation of copolymers of ethylene and functional group containing monomers; M. Peuckert et al. , Organomet. 1983, 2(5), 594, disclose the oligomerization of ethylene using phosphine/carboxylate donors ligated to Ni(ll), which showed modest catalytic activity (0.14 to 1.83 TO/s). The oligomerizations were carried out at 60 to 95° C and 10 to 80 bar ethylene in toluene, to produce linear α-olefins; R.E. Murray, U.S. Patents Nos. 4,689,437 and 4,716,138, describes the oligomerization of ethylene using phosphine/sulfonate donors ligated to Ni(ll). These complexes show catalyst activities approximately 15 times greater than those reported with phosphine/carboxylate analogs. W. Keim et al., Angew. Chem. Int. Ed. Eng. 1981, 20, 116, and V.M. Mohring, et al., Angew. Chem. Int. Ed. Eng. 1985, 24,1001 , disclose the polymerization of ethylene and the oligomerization of α-olefins with aminobis(imino)phosphorane nickel catalysts; G. Wilke, Angew. Chem. Int. Ed. Engl. 1988, 27, 185, describes a nickel allyl phosphine complex for the polymerization of ethylene. K.A.O. Starzewski et aL, Angew. Chem. Int. Ed. Engl. 1987, 26, 63, and U. S. Patent 4,691 ,036, describe a series of bis(ylide) nickel complexes, used to polymerize ethylene to provide high molecular weight linear polyethylene. WO Patent Application 97/02298 discloses the polymerization of olefins using a variety of neutral N, O, P, or S donor ligands, in combination with a nickel(O) compound and an acid. Brown et aL, WO 97/17380, describes the use of Pd α-diimine catalysts for the polymerization of olefins including ethylene in the presence of air and moisture. Fink et aL, U. S. Patent 4,724,273, have described the polymerization of α-olefins using aminobis(imino)phosphorane nickel catalysts and the compositions of the resulting poly(α-olefins). Additional recent developments are described by Sugimura et al., in JP96-84344, JP96-84343, and WO 9738024, and by Yorisue et al., in JP96-70332. Notwithstanding these advances in non-Ziegler-Natta catalysis, there remains a need for efficient and effective Group 8-10 transition metal catalysts for effecting polymerization of olefins. In addition, there is a need for novel methods of polymerizing olefins employing such effective Group 8- 10 transition metal catalysts. In particular, there remains a need for Group 8-10 transition metal olefin polymerization catalysts with both improved temperature stability and functional group compatibility. Further, there remains a need for a method of polymerizing olefins utilizing effective Group 8-10 transition metal catalysts in combination with a Lewis acid so as to obtain a catalyst that is more active and more selective. SUMMARY OF THE INVENTION The present invention provides a batch or continuous process for the polymerization of olefins, comprising: contacting, at a temperature from about -100 °C to about 200 °C, one or more monomers of the formula RCH=CHR 3 with (i) a compound of the formula II, or tautomers thereof, (ii) a suitable precursor selected from Ni, Pd, Co, or Fe compounds, and, optionally, (iii) a neutral Lewis acid; II wherein R and R 3 are each, independently, hydrogen, hydrocarbyl or fluoroalkyl and may be linked to form a cyclic olefin; R 1 and R 2 are each independently hydrocarbyl, substituted hydrocarbyl, or silyl; Q is (i) C-R 4 , wherein R 4 is hydrocarbyl, substituted hydrocarbyl, heteroatom connected hydrocarbyl, or heteroatom connected substituted hydrocarbyl, (ii) P(NH 2 ) 2 , or (Hi) S(NH)(NH 2 ) or S(O)(OH). This invention also provides a batch or continuous process for the polymerization of olefins, comprising: contacting, at a temperature from -100 °C to about 200 °C, one or more monomers of the formula RCH=CHR 3 , with (i) an anionic compound of the formula III, (ii) a suitable divalent metal precursor selected from Ni(ll), Pd(ll), Co(ll), or Fe(ll) compounds, and, optionally, (iii) a neutral Lewis acid; III wherein R and R 3 are each, independently, hydrogen, hydrocarbyl or fluoroalkyl and may be linked to form a cyclic olefin; R 1 and R 2 are each independently hydrocarbyl, substituted hydrocarbyl, or silyl; Q is C-R 4 , where R 4 is hydrocarbyl, substituted hydrocarbyl, heteroatom connected hydrocarbyl, heteroatom connected substituted hydrocarbyl, or O-Si(tert-butyl)(CH 3 ) 2 . This invention also provides a batch or continuous process for the production of polyolefins, comprising: contacting, at a temperature from -100 °C to about 200 °C, one or more monomers of the formula RCH=CHR 3 with (i) a transition metal complex of formula I, and, optionally, (ii) a Lewis acid; ' wherein R and R 3 are each, independently, hydrogen, hydrocarbyl or substituted hydrocarbyl and may be linked to form a cyclic olefin; R 1 and R 2 are each independently hydrocarbyl, substituted hydrocarbyl, or silyl; Q is (i) C-R 4 , where R 4 is hydrocarbyl, substituted hydrocarbyl, heteroatom connected hydrocarbyl, or heteroatom connected substituted hydrocarbyl, (ii) P(NH 2 ) 2 , or (iii) S(NH)(NH 2 ) or S(0)(OH); L is a monoolefin or a neutral Lewis base that can be displaced by a monoolefin; T is hydrogen, hydrocarbyl or substituted hydrocarbyl, or may be taken together with L to form a π-allyl group; and M is Ni(ll), Pd(ll), Co(ll) or Fe(ll). This invention also provides a compound of formula I: I wherein R 1 and R 2 are each independently hydrocarbyl, substituted hydrocarbyl, or silyl; Q is (i) C-R 4 , where R 4 is hydrocarbyl, substituted hydrocarbyl, heteroatom connected hydrocarbyl, or heteroatom connected substituted hydrocarbyl, (ii) P(NH 2 ) 2 , or (Hi) S(NH)(NH 2 ) or S(O)(OH); L is a monoolefin or a neutral Lewis base that can be displaced by a monoolefin; T is hydrogen, hydrocarbyl or substituted hydrocarbyl, or may be taken together with L to form a π-allyl group; and M is Ni(ll), Pd(ll), Co(ll) or Fβ(ll). This invention also provides a compound of formula II. II wherein R 1 and R 2 are both sterically hindered aryl rings; Q is (i) C-R 4 , where R 4 is hydrocarbyl, substituted hydrocarbyl, heteroatom connected hydrocarbyl, or heteroatom connected substituted hydrocarbyl, (ii) P(NH 2 ) 2 , or (iii) S(NH)(NH 2 ) or S(O)(OH). This invention also provides a batch or continuous process for the polymerization of olefins, comprising: contacting one or more monomers of the formula RCH=CHR 3 with a binudeating or multinucleating ligand complexed to a Group 8-10 transition metal M and one or more Lewis acids, wherein the Lewis acid or acids are bound to one or more heteroatoms which are π-conjugated to the donor atom or atoms bound to the transition metal M; and wherein R and R 3 each, independently, represent a hydrogen, a hydrocarbyl, a fiuoroalkyl, or may be linked to form a cyclic olefin. This invention also provides a composition comprising (i) a Group 8- 10 transition metal M, (ii) one or more Lewis acids, and (iii) a binudeating or multinucleating compound of the formula II: wherein the Lewis acid or acids are bound to one or more heteroatoms which are π-conjugated to the donor atom or atoms bound to the transition metal M; R 1 and R 2 are both sterically hindered aryl rings; Q is (i) C-R 4 , where R 4 is hydrocarbyl, substituted hydrocarbyl, heteroatom connected hydrocarbyl, or heteroatom connected substituted hydrocarbyl, (ii) P(NH 2 ) 2 , or (iii) S(NH)(NH 2 ) or S(O)(OH). Detailed Description of the Invention In this disclosure certain chemical groups or compounds are described by certain terms and symbols. These terms are defined as follows: Symbols ordinarily used to denote elements in the Periodic Table take their ordinary meaning, unless otherwise specified. Examples of neutral Lewis bases include, but are not limited to, (i) ethers, for example, diethyl ether or tetrahydrofuran, (ii) organic nitriles, for example acetonitrile, (iii) organic sulfides, for example dimethylsulfide, or (iv) monoolefins, for example, ethylene, hexene or cyclopentene. Examples of neutral Lewis acids include, but are not limited to, B(C 6 F 5 ) 3 , AI(CH 3 ) 3 , methylaluminoxane, BPh 3 , B(3,5-(CF3)C 6 H 3 )3. A "sterically hindered aryl" means (i) a phenyl ring with hydrocarbyl, substituted hydrocarbyl, F, CI, Br or silyl substituents at both the 2- and 6- positions, optionally substituted elsewhere with hydrocarbyl, substituted hydrocarbyl, F, CI, Br, silyl, hydroxy, methoxy, nitro, cyano, phenylsulfonyl, CO 2 Me, CO 2 H, C(O)CH 3 , CF 3 , or fiuoroalkyl substituents, (ii) a 2-substituted napth-1-yl ring, optionally substituted elsewhere with hydrocarbyl, substituted hydrocarbyl, F, CI, Br, silyl, hydroxy, methoxy, nitro, cyano, phenylsulfonyl, CO 2 Me, CO 2 H, C(O)CH 3 , CF 3l or fiuoroalkyl substituents, (iii) an 9-anthracenyl ring, optionally substituted elsewhere with hydrocarbyl, substituted hydrocarbyl, F, CI, Br, silyl, hydroxy, methoxy, nitro, cyano, phenylsulfonyl, CO 2 Me, CO 2 H, C(O)CH 3 , CF 3 , or fiuoroalkyl substituents, or (iv) an aromatic substituted hydrocarbyl with steric properties functionally equivalent (in the context of this invention) to one or more of the following ste cally hindered aryls: 2,6-dimethylphenyl, 2,4,6-trimethylphenyl, 2,6- diisopropylphenyl, 2,6-dimethyl-4-nitrophenyl, 2,6-dimethyl-4- phenylsulfonylphenyl, 2-isopropyl-6-methylphenyl, 2,6- bis(trifluoromethyl)phenyl, 2,6-dimethyl-4-methoxyphenyl, 2-methylnapth-1- yl, 9-anthracenyl, 2,6-diclorophenyl, 2,6-dibromophenyl, 2-tert-butyl-6- methylphenyl, 2-trimethylsilylnapth-1-yl, 2-chloro-6-methylphenyl, 4-cyano- 2,6-dimethylphenyl, 2,6-diisopropyl-4-methoxyphenyl, 2,4,6-tri-tert- butylphenyl, and 2-chloro-6-tert-butylphenyl. A "hydrocarbyl" group means a linear, branched or cyclic group which contains only carbon and hydrogen atoms. Examples include: C1-C20 alkyl; C 1 -C 20 alkyl substituted with one or more groups selected from C1-C20 alkyl, C 3 -C 8 cycloalkyi or aryl; C3-C8 cycloalkyi; C 3 -C8 cycloalkyi substituted with one or more groups selected from C1-C 20 alkyl, C3-C8 cycloalkyi or aryl; C 6 -C14 aryl; and C6-C14 aryl substituted with one or more groups selected from C 1 -C 2 0 alkyl, C3-C8 cycloalkyi or aryl; where the term "aryl" preferably denotes a phenyl, napthyl, or anthracenyl group. Examples of groups useful as the group Q include (i) C-aryl, where aryl is phenyl, pentafluorophenyl, or phenyl substituted with F, CI, Br, methoxy, cyano, nitro, CO 2 H, CF 3 , fiuoroalkyl, or phenylsulfonyl, (ii) C-tert- butyl, C-CF 3 , or C-fluoroalkyl, (iii) C-S-R 5 or C-O-R 5 , where R 5 is C1-C20 alkyl, silyl, phenyl, or phenyl substituted with F, CI, Br, CF3, fiuoroalkyl, CO 2 H, methoxy, cyano, nitro, or phenylsulfonyl, (iv) C-silyl, (v) P(NH 2 ) 2 , or (vi) S(NH)(NH 2 ) or S(O)(OH). A "silyl" group refers to a SiR 6 3 group where Si is silicon and R 6 is hydrocarbyl or substituted hydrocarbyl or silyl, as in Si(SiR 6 3)3- A "heteroatom" refers to an atom other than carbon or hydrogen. Preferred heteroatoms include oxygen, nitrogen, phosphorus, sulfur, selenium, silicon, arsenic, chlorine, bromine, and fluorine. A "fiuoroalkyl" as used herein refers to a Cι-C 2 o alkyl group substituted by one or more fluorine atoms. A "substituted hydrocarbyl" refers to a hydrocarbyl substituted with one or more heteroatoms. Examples include: 2,6-dimethyl-4- methoxyphenyl, 2,6-diisopropyl-4-methoxyphenyl, 4-cyano-2,6- dimethylphenyl, 2,6-dimethyl-4-nitrophenyl, 2,6-difluorophenyl, 2,6- dibromophenyl, 2,6-dichlorophenyl, 4-methoxycarbonyl-2,6-dimethylphenyl, 2-tert-butyl-6-chlorophenyl, 2,6-dimethyl-4-phenylsulfonylphenyl, 2,6- dimethyl-4-trifluoromethylphenyl, 2,6-dimethyl-4-hydroxyphenyl, 9- hydroxyanthr-10-yl, 2-chloronapth-1-yl, 4-methoxyphenyl, 4-nitrophenyl, 9- nitroanthr-10-yl, CH 2 OCH 3 , cyano, trifluoromethyl, or fiuoroalkyl. A "heteroatom connected hydrocarbyl" refers to a group of the type Z-(hydrocarbyl), where Z is a divalent heteroatom, preferably O or S, or Z-(hydrocarbyl) 2 , where Z is a trivalent heteroatom, preferably N. Examples include: OCH 3 , OPh, N(CH 3 ) 2 , SCH 3 , or SPh. A "heteroatom connected substituted hydrocarbyl" refers to a group of the type Z-(substituted hydrocarbyl), where Z is a divalent heteroatom, preferably O or S, or Z-(substituted hydrocarbyl) 2 , where Z is a trivalent heteroatom, preferably N. Examples include: OCH 2 CF3, SC(O)CH3, and 1-morpholinyl. A "mono-olefin" refers to a hydrocarbon containing one carbon- carbon double bond. A "suitable precursor" refers to a zerovalent or divalent transition metal compound which may be combined with compound II, and optionally a neutral Lewis acid, to form an active olefin polymerization catalyst. Examples of suitable precursors include: bis(1 ,5-cycloctadiene)nickel(0) and bis[(1, 2, 3-η 3 -2-propenyl)nickel(ll)]. A "suitable divalent metal precursor" refers to a divalent transition metal compound which may be combined with compound III, and optionally a neutral Lewis acid, to form an active olefin polymerization catalyst. Examples include: (1 ,2-dimethoxyethane)nickel(ll) dibromide, bis[(μ- chloro)(1 , 2, 3-η 3 -2-propenyl)nickel(ll)], bis[(μ-chloro)(1 , 2, 3-η 3 -2- propenyl)palladium(ll)], bis[(μ-chloro)(1 , 2, 3-η 3 -1-trimethylsilyloxy-2- propenyl)nickel(ll)], CoBr 2 , FeBr 2 . A "π-allyl" group refers to a monoanionic group with three sp 2 carbon atoms bound to a metal center in a η 3 -fashion. Any of the three sp 2 carbon atoms may be substituted with a hydrocarbyl, substituted hydrocarbyl, heteroatom connected hydrocarbyl, heteroatom connected substituted hydrocarbyl, or O-silyl group. Examples of π-allyl groups include: •C 6 H 5 The term "polymer" as used herein is meant a species comprised of monomer units and having a degree of polymerization (DP) of ten or higher. As used herein, the terms "monomer" or "olefin monomer" refer to the olefin or other monomer compound before it has been polymerized; the term "monomer units" refers to the moieties of a polymer that correspond to the monomers after they have been polymerized. Described herein is a process for the polymerization of olefins. Preferred olefins include ethylene and α-olefins such as propylene, 1- butene, 1-hexene, 1-octene, and cyclic olefins such as cyclopentene. When the polymerizations are conducted in the liquid phase, said liquid phase may include solvent or neat monomer. The molar ratio of neutral Lewis acid to transition metal complex can be from 0 to 10000, preferably 0 to 100, more preferably 0 to 10. The pressure at which the ethylene polymerizations and copolymerizations take place can be from 1 atmosphere to 1000 atmospheres, preferably 1 to 100 atmospheres. While not wishing to be bound by theory, the present inventors believe that the Lewis acid may be acting to further activate the catalysts disclosed herein via coordination to one or more of those heteroatoms which are not directly bound to the transition metal M, but which are π- conjugated to the nitrogens which are bound to the transition metal M. Substituents which contain additional Lewis basic groups, including, but not limited to, methoxy groups, positioned so as to further promote the binding of the Lewis acid at such π-conjugated heteroatoms, are also included in this invention. A non-limiting example of secondary Lewis acid binding would include the following: IV wherein R 1 and R 2 are each independently hydrocarbyl, substituted hydrocarbyl, or silyl; Q is (i) C-R 4 , where R 4 is hydrocarbyl, substituted hydrocarbyl, heteroatom connected hydrocarbyl, or heteroatom connected substituted hydrocarbyl, (ii) P(NH 2 ) 2 , or (iii) S(NH)(NH 2 ) or S(O)(OH); L is a monoolefin or a neutral Lewis base that can be displaced by a monoolefin; and T is hydrogen, hydrocarbyl or substituted hydrocarbyl, or may be taken together with L to form a π-allyl group. The polymerizations may be conducted as solution polymerizations, as non-solvent slurry type polymerizations, as slurry polymerizations using one or more of the olefins or other solvent as the polymerization medium, or in the gas phase. One of ordinary skill in the art, with the present disclosure, would understand that the catalyst could be supported using a suitable catalyst support and methods known in the art. Substantially inert solvents, such as toluene, hydrocarbons, and the like, may be used. Propylene and 1-butene are excellent monomers for use in slurry-type copolymerizations and unused monomer can be flashed off and reused. Polymerization temperature and pressure have significant effects on copolymer structure, composition, and molecular weight. Suitable polymerization temperatures are preferably from about -100 °C to about 200 °C, more preferably in the 20 °C to 150 °C range. After the reaction has proceeded for a time sufficient to produce the desired polymers, the polymer can be recovered from the reaction mixture by routine methods of isolation and/or purification. High molecular weight resins are readily processed using conventional extrusion, injection molding, compression molding, and vacuum forming techniques well known in the art. Useful articles made from them include films, fibers, bottles and other containers, sheeting, molded objects and the like. Low molecular weight resins are useful, for example, as synthetic waxes and they may be used in various wax coatings or in emulsion form. They are also particularly useful in blends with ethylene/vinyl acetate or ethylene/methyl acrylate-type copolymers in paper coating or in adhesive applications. Although not required, typical additives used in olefin or vinyl polymers may be used in the new homopolymers and copolymers of this invention. Typical additives include pigments, colorants, titanium dioxide, carbon black, antioxidants, stabilizers, slip agents, flame retarding agents, and the like. These additives and their use in polymer systems are known per se in the art. The molecular weight data presented in the following examples is reported as linear poly(ethylene) equivalent molecular weights determined at 135 °C in 1 ,2,4-trichlorobenzene using refractive index detection, calibrated using narrow molecular weight distribution poly(styrene) standards, and employing the appropriate Mark-Houwink-Sakurada (MHS) relations. EXAMPLES Other features of the invention will become apparent in the course of the following descriptions of exemplary embodiments which are given for illustration of the invention and are not intended to be limiting thereof. Example 1 Λ/.Λ/'-Bis(2,6-dimethylphenyl)oxalamide 2,6-Dimethylaniline, triethylamine, and dichloromethane were dried by passage through basic alumina. A 1 L round bottom flask, equipped with a magnetic stir bar and a 125 mL pressure-equalizing dropping funnel capped by a nitrogen inlet adapter, was charged with 53.38 g of 2,6- dimethylaniline, 250 mL of dichloromethane, and 44.76 g of triethylamine. A solution of 25.34 g of oxalyl chloride in 80 mL of dichloromethane was added dropwise under nitrogen with stirring and ice-bath cooling over 1.2 hours to give a thick paste which had to be occasionally swirled by hand to effect mixing. The mixture was allowed to stir at room temperature for 14 hours, then transferred to a separatory funnel, washed 3 times with water, separated and concentrated under reduced pressure (10 mm Hg) to give 63 g of crude solid. The crude product was dissolved in a boiling mixture of 2850 mL of toluene and 1300 mL of absolute ethanol, cooled to room temperature and diluted with 260 mL of water, then allowed to crystallize for 16 hours. The resultant precipitate was isolated by vacuum filtration, washed with methanol (3 x 100 mL) and dried to give 39.1 g (66%) as white crystals. An additional 9.5 g (16.1 %) was recovered from the filtrate by further dilution with ca. 500 mL water. Field desorption mass spectrometry showed a parent ion peak at 296 m/z. 1 H NMR (300 MHz, CDCI 3 , chemical shifts in ppm relative to TMS at 0 ppm): 2.29 (12 p, s), 7.15 (6 p, m), 8.86 (2 P. br s). Example 2 Preparation of Λ/ 1 ./V 2 -bis(2,6-dimethylphenyl)oxalodiimidoyl dichloride. A 1 L round bottom flask was charged with 30.0 g of Λ/,/V-bis(2,6- dimethylphenyl)oxalamide, 58.75 g of phosphorous pentachloride and 150 mL of dry toluene, and equipped with a magnetic stir bar and a reflux condenser capped by a nitrogen inlet adapter connected to a bubbler. The mixture was heated to reflux over 30 minutes, then maintained at reflux under nitrogen for another 95 minutes to give a yellow solution. Heating was discontinued and the mixture was allowed to cool to room temperature. A short path distillation adapter and receiving flask were attached in place of the condenser, and the volatiles were removed under reduced pressure (1 mm Hg), initially at room temperature, then at 100° C, to give 20.1 g (60%) of a granular yellow solid. Field desorption mass spectrometry showed a parent ion peak at 332 m/z. 1 H NMR (300 MHz, C 6 D 6 , chemical shifts in ppm relative to TMS at 0 ppm): 2.04 (12 p, s), 6.91 (6 p, s). Example 3 Preparation of (2.6-dimethylphenylH5-(2.6-dimethylphenylimino)-2-phenyl- 5H-imidazol-4-yllamine (compound II with Q = CPh and R 1 = R 2 = 2,6- dimethylphenvπ A 100 mL, round bottom flask equipped with a magnetic stir bar and condenser capped by a nitrogen inlet adapter was charged with 347 mg of benzamidine hydrochloride hydrate, 25 mL of dry N-methylpyrrolidinone and 1.47 g of triethylamine. The mixture was stirred for 5 minutes, then treated with 499 mg of Λ/ 1 ,Λ/ 2 -bis(2,6-dimethylphenyl)oxalodiimidoyl dichloride. A nitrogen atmosphere was established, then the mixture was heated to 85° C and maintained at that temperature for 6 days. The resultant dark red-brown mixture was diluted with ether and washed with water, and the ether layer was concentrated under reduced pressure (10 mm Hg, 85° C bath) to remove most of the volatiles. Flash chromatography (SiO 2 , 12 % EtOAc/ 88% hexanes) yielded 96 mg of an orange powder. Recrystallization from CH 2 CI 2 /hexane gave 65 mg of dark violet crystals of the title compound. Field desorption mass spectrometry showed a parent ion peak at 380 m/z. 1 H NMR (500 MHz, CD 2 CI 2 , chemical shifts in ppm relative to TMS at 0 ppm): 2.28 (12 p, s), 7.10-7.25 (6 p, s), 7.38-7.48 (2 p, m), 7.35-7.63 (1 p, m), 8.25-8.3 (2 p, m). Example 4 Polyethylene Synthesis Using a Catalyst Generated In Situ from (2.6- dimethylphenylH5-(2,6-dimethylphenyliminoV2-phenyl-5H-imidazol-4- yllamine (compound II with Q = CPh and R 1 = R 2 = 2,6-dimethylphenvO and Bis(1 ,5-cvclooctadiene)nickel(0) In a drybox, a flame-dried, 200 mL, pear-shaped Schlenk flask equipped with a magnetic stir bar and capped by a septum was charged with 10 mg of (2,6-dimethylphenyl)-[5-(2,6-dimethylphenylimino)-2-phenyl- 5/-/-imidazol-4-yl]amine and 5 mg of bis(1 ,5-cyclooctadiene)nickel(0). On the Schlenk line, the flask was evacuated, refilled with ethylene, then charged with 45 mL of dry, deoxygenated toluene, introduced via syringe, with stirring. A transient violet color was observed, which rapidly changed to a dark green or red-green color. Ethylene uptake was observed. After 2 hours of stirring under 1 atm of ethylene at 21° C, the solution was golden- brown and methanol was added to precipitate the polymer as an oily gum. The volatiles were removed under reduced pressure (10 mm Hg initially, then 0.4 mm Hg) to give 0.20 g of a viscous beige polyethylene gum. GPC (relative to polystyrene standards) M n = 38,000; M w = 73,000. 1 H NMR (o- dichlorobenzene-d 4 ) showed ca. 112 branches per 1000 carbons. Example 5 Polyethylene Synthesized Using a Catalyst Generated In Situ from (2,6- dimethylphenylH5-(2,6-dimethylphenylimino)-2-phenyl-5H-imidazol-4- yllamine (compound II with Q = CPh and R 1 = R 2 = 2,6-dimethylphenyl. Bisd ,5-cyclooctadiene)nickel(0) and Tris(pentafluorophenyl)boron In the drybox, a flame-dried, 500 mL, round bottom flask equipped with a magnetic stir bar was charged with 8 mg of (2,6-dimethylphenyl)-[5- (2,6-dimethylphenylimino)-2-phenyl-5H-imidazol-4-yl]amine, 3 mg of bis(1 ,5-cyclooctadiene)nickel(0) and 120 mg of tris(pentafluorophenyl)boron, then fitted with a side-arm adapter equipped with a Kontes high vacuum valve and a 24/40 septum. On the Schlenk line, the flask was evacuated, refilled with ethylene, then charged with 200 mL of dry, deoxygenated toluene, introduced via syringe, with stirring. A dark red solution resulted, which subsequently became somewhat more brown and slightly purple over the next 10-20 minutes. Ethylene uptake was observed. After 60 minutes of stirring under 1 atmosphere of ethylene at 23° C, methanol and acetone were added to produce an off-white supernatant and a white flocculent precipitate of polyethylene. The polymer was isolated by vacuum filtration and dried under reduced pressure (250 mm Hg) at 100 C for 14 h to afford 2.6 g of a white, polyethylene powder. GPC (relative to polystyrene standards) M n = 8,200; M w = 17,900. DSC: (2nd heat) melt transition with endothermic maxima at 78 and 91 °C. 1 H NMR (o- dichlorobenzene-d 4 ) showed approximately 44 branches per 1000 carbons. Example 6 Copolvmer Synthesized From Ethylene and Propene Using a Catalyst Generated In Situ from (2,6-dimethylphenylVf5-(2,6-dimethylphenylimino)- 2-phenyl-5H-imidazol-4-yl1amine (compound II with Q = CPh and R 1 = R 2 = 2,6-dimethylphenvO, Bis(1 ,5-cyclooctadiene nickel(0) and Tris(pentafluorophenvOboron In the drybox, a flame-dried, 500 mL, round bottom flask equipped with a magnetic stir bar was charged with 10 mg of (2,6-dimethylphenyl)-[5- (2,6-dimethylphenylimino)-2-phenyl-5H-imidazol-4-yl]amine, 5 mg of bis(1 ,5-cyclooctadiene)nickel(0) and 106 mg of tris(pentafluorophenyl)boron, then fitted with an inert gas inlet adapter equipped with a Kontes high vacuum valve and a 24/40 septum. On the Schlenk line, the flask was evacuated, refilled with ethylene, then charged with 100 mL of dry, deoxygenated toluene, introduced via syringe, with stirring. A dark red solution resulted, which subsequently became somewhat more brown and slightly purple over the next 10 min, after which the ethylene was replaced by propene (1 atm). After a total of 120 min, the reaction was quenched with methanol and worked up to obtain the 1.8 g of the copolymer as an oily gum. GPC (relative to polystyrene standards) M n = 3,935; M w = 10,353. ). 1 H NMR (500 MHz, o-dichlorobenzene-d 4 ) showed approximately 160 branches per 1000 carbons. Example 7 Polyethylene Synthesized Using a Catalyst Generated In Situ from (2.6- dimethylphenylH5-(2,6-dimethylphenylimino)-2-phenyl-5H-imidazol-4- yllamine (compound II with Q = CPh and R 1 = R 2 = 2,6-dimethylphenyl), Bisd ,5-cyclooctadiene nickel(0) and TrisfpentafluorophenvOboron In the drybox, a flame-dried, 500 mL, round bottom flask equipped with a magnetic stir bar was charged with 10 mg of (2,6-dimethylphenyl)-[5- (2,6-dimethylphenyl)-2-phenyl-5H-imidazol-4-yl]amine, 5 mg of bis(1 ,5- cyclooctadiene)nickel(O) and 106 mg of tris(pentafluorophenyl)boron, then fitted with an inert gas inlet adapter equipped with a Kontes high vacuum valve and a 24/40 septum. On the Schlenk line, the flask was evacuated, refilled with ethylene, then charged with 100 mL of dry, deoxygenated toluene, introduced via syringe, with stirring. A dark red solution resulted, which subsequently became somewhat more brown and slightly purple over the next 10 min. After a total of 30 min stirring under an ethylene atmosphere, the reaction was quenched by the addition of methanol and acetone and the resultant precipitate was isolated by filtration and dried in vacuo to obtain 5.0 g of white, powdery polyethylene. GPC (relative to polystyrene standards) M n = 10,500; M w = 27,500. 1 H NMR (500 MHz, o- dichlorobenzene-d 4 ) showed approximately 70 branches per 1000 carbons. Numerous modifications and variations of the present invention are possible in light of the above teachings. It is therefore to be understood that within the scope of the appended claims, the invention may be practiced otherwise than as specifically described herein.

Claims: Claims We Claim: 1. A batch or continuous process for the polymerization of olefins, comprising: contacting, at a temperature from about -100 °C to about 200 °C, one or more monomers of the formula RCH=CHR 3 , with (i) a compound of the formula II, or tautomers thereof, (ii) a suitable precursor selected from Ni, Pd, Co, or Fe compounds, and, optionally, (iii) a neutral Lewis acid; wherein R and R 3 are each, independently, hydrogen, hydrocarbyl or fiuoroalkyl and may be linked to form a cyclic olefin; R 1 and R 2 are each independently hydrocarbyl, substituted hydrocarbyl, or silyl; Q is (i) C-R 4 , where R 4 is hydrocarbyl, substituted hydrocarbyl, heteroatom connected hydrocarbyl, or heteroatom connected substituted hydrocarbyl, (ii) P(NH 2 ) 2 , or (iii) S(NH)(NH 2 ) or S(O)(OH). 2. The process of Claim 1 wherein the suitable precursor is a zerovalent Ni compound. 3. The process of Claim 2 wherein Q is C-R 4 , where R 4 is hydrocarbyl, substituted hydrocarbyl, heteroatom connected hydrocarbyl, or heteroatom connected substituted hydrocarbyl. 4. The process of Claim 1 wherein a neutral Lewis acid is utilized. 5. The process of Claim 4 wherein the suitable precursor is a zerovalent Ni compound. 6. The process of Claim 5 wherein Q is C-R 4 , where R 4 is hydrocarbyl, substituted hydrocarbyl, heteroatom connected hydrocarbyl, or heteroatom connected substituted hydrocarbyl. 7. The process of Claim 3 or 6 wherein the monomer is selected from ethylene, propylene, 1-butene, 1-pentene, 1-hexene, 1-octene or cyclopentene. 8. A batch or continuous process for the polymerization of olefins, comprising: contacting, at a temperature from about -100 °C to about 200 °C, one or more monomers of the formula RCH=CHR 3 , with (i) an anionic compound of the formula III, (ii) a suitable divalent metal precursor selected from Ni(ll), Pd(ll), Co(ll), or Fe(ll) compounds, and, optionally, (iii) a neutral Lewis acid; wherein R and R 3 are each, independently, hydrogen, hydrocarbyl, or fluoroalkyi, and may be linked to form a cyclic olefin; R 1 and R 2 are each independently hydrocarbyl, substituted hydrocarbyl, or silyl; Q is C-R 4 , wherein R 4 is hydrocarbyl, substituted hydrocarbyl, heteroatom connected hydrocarbyl, heteroatom connected substituted hydrocarbyl, or O-Si(tert-butyl)(CH 3 )2. 9. The process of Claim 8 wherein the suitable divalent metal precursor is a Ni(ll) compound. 10. The process of Claim 9 wherein Q is C-R 4 , where R 4 is hydrocarbyl, or substituted hydrocarbyl. 11. The process of Claim 8 wherein a neutral Lewis acid is utilized. 12. The process of Claim 11 wherein the suitable divalent metal precursor is a Ni(ll) compound. 13. The process of Claim 12 wherein Q is C-R 4 , where R 4 is phenyl, pentafluorophenyl, trifluoromethyl, fluoroalkyi, O-Si(tert-butyl)(CH3)2, or SCH 3 . 14. The processes of Claim 10 or 13 wherein the monomer is selected from ethylene, propylene, 1-butene, 1-pentene, 1-hexene, 1- octene or cyclopentene. 15. A batch or continuous process for the production of polyolefins, comprising: contacting, at a temperature from about -100 °C to 200 °C, one or more monomers of the formula RCH=CHR 3 , with (i) a transition metal compound of formula I, and, optionally, (ii) a Lewis acid; I wherein R and R 3 are each, independently, hydrogen, hydrocarbyl, or fluoroalkyi, and may be linked to form a cyclic olefin; R 1 and R 2 are each independently hydrocarbyl, substituted hydrocarbyl, or silyl; Q is (i) C-R 4 , wherein R 4 is hydrocarbyl, substituted hydrocarbyl, heteroatom connected hydrocarbyl, or heteroatom connected substituted hydrocarbyl, (ii) P(NH 2 ) 2 , or (iii) S(NH)(NH 2 ) or S(O)(OH); L is a monoolefin or a neutral Lewis base that can be displaced by a monoolefin; T is hydrogen, hydrocarbyl or substituted hydrocarbyl, or may be taken together with L to form a π-allyl group; and M is Ni(ll), Pd(ll), Co(ll) or Fe(ll). 16. The process of Claim 15 wherein M is Ni(ll). 26 - 17. The process of Claim 16 wherein Q is C-R 4 , where R 4 is hydrocarbyl, substituted hydrocarbyl, heteroatom connected hydrocarbyl, or heteroatom connected substituted hydrocarbyl. 18. The process of Claim 15 wherein a neutral Lewis acid is utilized. 19. The process of Claim 18 wherein M is Ni(ll). 0 20. The process of Claim 19 wherein Q is C-R 4 , where R 4 is hydrocarbyl, substituted hydrocarbyl, heteroatom connected hydrocarbyl, or heteroatom connected substituted hydrocarbyl. 5 21. The process of Claim 17 or 20 wherein the monomer is selected from ethylene, propylene, 1-butene, 1-pentene, 1-hexene, or 1- octene. 22. A compound of formula I: 0 I wherein R 1 and R 2 are each independently hydrocarbyl, substituted hydrocarbyl, or silyl; Q is (i) C-R 4 , where R 4 is hydrocarbyl, substituted hydrocarbyl, heteroatom connected hydrocarbyl, or heteroatom connected substituted hydrocarbyl, (ii) P(NH 2 ) 2 , or (iii) S(NH)(NH 2 ) or S(O)(OH); L is a monoolefin or a neutral Lewis base that can be displaced by a monoolefin; T is hydrogen, hydrocarbyl or substituted hydrocarbyl, or may be taken together with L to form a π-allyl group; and M is Ni(ll), Pd(ll), Co(ll) or Fe(ll). 23. The compound of Claim 22 wherein M is nickel(ll). 24. The compound of Claim 23 wherein R 1 and R 2 are both sterically hindered aryl rings. 25. The compound of Claim 24 wherein Q is C-R 4 , where R 4 is hydrocarbyl, substituted hydrocarbyl, heteroatom connected hydrocarbyl, or heteroatom connected substituted hydrocarbyl. 26. The compound of Claim 22 further comprising a boron or aluminum containing neutral Lewis acid. 27. The compound of Claim 26 wherein Q is C-R 4 , where R 4 is hydrocarbyl, substituted hydrocarbyl, heteroatom connected hydrocarbyl, or heteroatom connected substituted hydrocarbyl. 28. A compound of formula II: II wherein R 1 and R 2 are both sterically hindered aryl rings; Q is (i) C-R 4 , where R 4 is hydrocarbyl, substituted hydrocarbyl, heteroatom connected hydrocarbyl, or heteroatom connected substituted hydrocarbyl, (ii) P(NH 2 ) 2 , or (iii) S(NH)(NH 2 ) or S(O)(OH). 29. The compound of Claim 28 wherein Q is C-R 4 , where R 4 is hydrocarbyl, substituted hydrocarbyl, heteroatom connected hydrocarbyl , or heteroatom connected substituted hydrocarbyl. 30. The compound of Claim 28 further comprising a boron or aluminum containing neutral Lewis acid. 31. The compound of Claim 30 wherein Q is C-R 4 , where R 4 is hydrocarbyl, substituted hydrocarbyl, heteroatom connected hydrocarbyl, or heteroatom connected substituted hydrocarbyl. 32. A batch or continuous process for the polymerization of olefins, comprising: contacting one or more monomers of the formula RCH=CHR 3 with a binudeating or multinucleating ligand complexed to a Group 8-10 transition metal M and one or more Lewis acids, wherein the Lewis acid or acids are bound to one or more heteroatoms which are π- conjugated to the donor atom or atoms bound to the transition metal M; and wherein R and R 3 each, independently, represent a hydrogen, a hydrocarbyl, a fluoroalkyi, or may be linked to form a cyclic olefin. 33. The process of Claim 32 wherein M is Ni(ll). 34. The process of Claim 33 wherein the binudeating or multinucleating ligand is: wherein R 1 and R 2 are both sterically hindered aryl rings; and Q is (i) C-R 4 , where R 4 is hydrocarbyl, substituted hydrocarbyl, heteroatom connected hydrocarbyl, or heteroatom connected substituted hydrocarbyl, (ii) P(NH 2 ) 2 , or (iii) S(NH)(NH 2 ) or S(O)(OH). 35. The process of Claim 34 wherein Q is C-R 4 , where R 4 is hydrocarbyl, substituted hydrocarbyl, heteroatom connected hydrocarbyl, or heteroatom connected substituted hydrocarbyl. 36. The process of Claim 35 wherein the Lewis acid is a boron or aluminum containing Lewis acid. 37. A composition comprising (i) a Group 8-10 transition metal M, (ii) one or more Lewis acids, and (iii) a binudeating or multinucleating compound of the formula II: wherein the Lewis acid or acids are bound to one or more heteroatoms which are π-conjugated to the donor atom or atoms bound to the transition metal M; R 1 and R 2 are both sterically hindered aryl rings; and Q is (i) C-R 4 , where R 4 is hydrocarbyl, substituted hydrocarbyl, heteroatom connected hydrocarbyl, or heteroatom connected substituted hydrocarbyl, (ii) P(NH 2 ) 2 , or (iii) S(NH)(NH 2 ) or S(O)(OH). 38. The composition of Claim 37 wherein the transition metal M is Ni(ll), the Lewis acid is a boron or aluminum containing Lewis acid, and Q is C-R 4 , where R 4 is hydrocarbyl, substituted hydrocarbyl, heteroatom connected hydrocarbyl, or heteroatom connected substituted hydrocarbyl. 39. The compound of Claim 29 wherein R 4 is phenyl, 4-methoxyphenyl, 4-cyanophenyl, trifluoromethyl, 4-nitrophenyl, or pentafluorophenyl. 40. The compound of Claim 31 wherein R 4 is phenyl, 4-methoxyphenyl, 4-cyanophenyl, trifluoromethyl, 4-nitrophenyl, or pentafluorophenyl.

Inventors: KILLIAN CHRISTOPHER MOORE, MACKENZIE PETER BORDEN, MCDEVITT JASON PATRICK, MOODY LESLIE SHANE, KILLIAN, CHRISTOPHER, MOORE, MACKENZIE, PETER, BORDEN, MCDEVITT, JASON, PATRICK, MOODY, LESLIE, SHANE
Applicants: EASTMAN CHEM CO, EASTMAN CHEMICAL COMPANY
Application year: 1998
Main classification: C08F10
IPC codes: C07C251, C07C257, C07D233, C07D241, C07D265, C07D285, C07D319, C07D339, C07D513, C07D521, C07F9, C07F15, C08F4, C08F10, C08F110, C08F210