AN OSTOMY APPLIANCE

Abstract: The invention relates to an ostomy appliance comprising a body side member comprising an adhesive wafer or pad for securing the appliance to the user's skin, said wafer or pad having a hole for receiving a stoma, and an optionally separately exchangeable receiving member or bag secured to the body side ostomy member for receiving secretions from the ostomy, said ostomy appliance further comprising a sealing member disposed in the hole of the wafer or pad surrounding the stoma wherein the sealing member disposed in the hole of the wafer or pad surrounding the stoma, said sealing member having a hole for accommodating the stoma and said sealing member having balanced plastic and elastic properties allowing an adaptation of the hole of the ostomy appliance to a stoma by a temporary enlarging the hole by everting or rolling up the inner rim of the hole for accommodating the stoma. When the ostomy appliance of the invention has been placed over and around the stoma the adhesive sealing member may recover essentially to the original form to fit snugly to the stoma. Preferably at least the area of a release liner covering the separate sealing member is provided with a guide for adaptation of the hole of an ostomy appliance to the size of an ostomy, said guide being visible from the side of the release liner facing the sealing member.

Description: TITLE An Ostomy Appliance FIELD OF THE INVENTION The present invention relates to an ostomy appliance, an ostomy appliance body side member, an ostomy sealing member and to a method of applying an ostomy appliance body side member around a stoma BACKGROUND OF THE INVENTION In connection with surgery for a number of diseases in the gastro-intestinal tract a consequence is, in many cases, that the colon, the ileum or the urethra has been exposed surgically and the patient is left with an abdominal stoma and the effluents or waste products of the body, which are conveyed through these organs, are discharged through the artificial orifice or opening and are collected in a collection bag, which is usually adhered to the skin by means of an adhesive wafer or plate having an inlet opening for accommodating the stoma Also in connection with a fistula, the patient will have to rely on an appliance to collect the bodily material emerging from such opening Ostomy appliances are well known Such appliances may be two-piece or one-piece appliances In both types of appliances, a body side member is attached to the wearer's abdomen, and optionally a receiving member or bag is attached to the body side ostomy member for receiving exudates from the ostomy in case of a two-piece appliance When using one-piece appliances, the whole appliance, including the adhesive wafer or pad securing the appliance to the skin is removed and replaced by a fresh appliance When using two-piece appliances, the body side ostomy member is let in place for several days, and only the receiving member or bag is replaced The service time of the body side ostomy member depends on the amount and aggressiveness of the exudates and of the tightness between the ostomy and the body side ostomy member In the known appliances it is necessary to change the body side member of a two- piece appliance when the centre part of the adhesive wafer or pad has been sufficiently deteriorated to allow access of the aggressive exudates to the skin surrounding the stoma, irrespective of the fact that the wafer as such has a much longer wearing time The access of aggressive exudates to the skin is causing skin problems Skin problems are common for persons having a stoma Generally about 40 % have skin problems (Pearl et al 1985 "Early local complications from intestinal stomas" Arch Surg 120, 1 145-1147 ) and the frequency is especially high for persons having an urostomy or ileostomy About 80 % of the persons having an ileostomy have skin problems (Hellman, J D , Lago, C P 1990 "Dermatologic complications in colostomy and ileostomy patients", International Journal of Dermatology, 29 (2), 129-133 ) The skin problems are mostly pronounced in a circular area about the stoma (1*4 inch from the stoma) (Hellman and Lago 1990) Frequent changing of the body side member of a two-piece appliance or the frequent exchange of a one-piece appliance is undesirable due to the irritation of the skin and the quality of life may be improved and the nuisance of the wearing of an ostomy appli- ance reduced if the intervals between exchanging of body side member can be increased It is known to place a ring on the skin before applying the body side member or to make a filling between the edge of the stoma and the shaped whole of the ostomy appliance in order to form a seal between the stoma and the ostomy appliance in order to alleviate the problems using a commercially available medical grade adhesive paste Such pastes are e g sold by Bristol-Myers Squibb under the trademark Stomahesive® or by Coloplast under the trade mark Coloplast® Paste These pastes, however, do not have a composition which has a sufficiently cohesion ensuring safe removal thereof without leaving residues on the skin and, on the other hand, the pastes often are so sticky that they cannot easily be shaped using the finger without sticking to the finger If using a paste, it should have a composition which is sufficiently tacky to secure the appliance or skin barrier to the abdomen, a cohesion ensuring safe removal thereof without leaving residues on the skin On the other hand, the paste must not be so sticky that it cannot easily be shaped by a finger or hand without sticking to the hand Furthermore, the paste must show a sufficient elasticity in order to be able to follow the movements of the patient without slipping the skin and should also show a great resistance to erosion caused by aggressive exudates from an ostomy In GB Patent Application No GB 2 290 974 is disclosed an ostomy appliance wherein a body-side is combined with a mouldable mass of non-hypoallergenic, non-memory putty-like adhesive, particularly based on hydrocolloid or hydrogel Thus, GB Patent Application No GB 2 290 974 discloses a body-side ostomy member comprising a ring to which a bag-side coupling ring or a bag can be attached, said ring comprising a rib and a flange, said flange being mounted on a wafer of medical grade adhesive having a central whole of diameter at least 65 % of the internal diameter of the ring A mouldable mass of non-hypoallergenic, non-memory putty-like adhesive, particularly based on hydrocolloid or hydrogel, is disposed radially inward of the wafer so that it forms a protective mass surrounding the stoma The mouldable mass has a thickness of 1 25 - 3 times that of the wafer and a central hole therein of a diameter no more than 1/10 th of the internal diameter of the ring Both the medical grade adhesive and the mouldable adhesive are adhered to the skin The mouldable mass of non-hypoallergenic, non-memory putty-like adhesive or flexible patch disclosed in GB Patent Application No GB 2 290 974 is secured to the rim of the hole for receiving the stoma and may be displaced to engage with the stoma The ostomy appliances disclosed in GB Patent Application No GB 2 290 974 suffers from the drawback that the mouldable sealing material is only foreseen to be changed together with the body side member of the appliance Furthermore, there is only disclosed that mouldable sealing material is to be disposed or extruded towards the stoma which still leaves a considerable risk of an insufficient sealing as a sufficient amount of sealing material must be disposed to form a cohesive layer of adhesive sealing against the stoma Thus, there is still a need for a sealing against a stoma ensuring that no leaks occur at the rim of the stoma and at the same time avoids the risk of thin spots or holes in the adhesive layer next to the stoma which may give rise to lack of protection of the skin next to the stoma and lead to a shorter service time between exchange of the body side member It has surprisingly been found that it is possible to provide an ostomy appliance having a separate or integrated sealing member disposed in the hole of the wafer or pad surrounding the stoma offering a convenient and comfortable solution to the above prob- lems and which at the same time enables a separation of the two functions, the sealing around an ostomy and the securing of a separately exchangeable receiving member or bag for receiving secretions from an ostomy to a body side ostomy member None of the above mentioned patents describes the use of a separate sealing member which may be exchanged or substituted separately This idea according to the invention differs from the above mentioned patents since the central ring (sealing member) in this case in some embodiments can be substituted without substituting the adhesive of a body side member which carries the bag and furthermore in that the adaptation of the ostomy appliance to the specific ostomy is rendered very simple and independent of the use of tools and in that the adaptation of the appliance to the actual stoma is carried out by temporary enlarging the central hole thereof and not by inward displacement of adhesive mass to cover areas not covered hitherto to provide a snug engagement with the stoma BRIEF DESCRIPTION OF THE INVENTION The invention relates in its broadest aspect to an ostomy appliance comprising a body side member, an optionally separately exchangeable receiving member or bag secured to the body side ostomy member and further a separate or integrated sealing member, said appliance having a guide for adaptation of an ostomy appliance to the size of an ostomy Furthermore, the invention relates to a separate sealing member for placing in a hole of an ostomy appliance Still further, the invention relates to an ostomy appliance body side member having a guide for adaptation of an ostomy appliance to the size of an ostomy as well as to different methods of applying an ostomy appliance body side member around a stoma by which the hole for receiving the stoma is adapted to the size of the stoma BRIEF DESCRIPTION OF THE DRAWINGS The invention is disclosed more in detail with reference to the drawings in which Fig 1 shows a cross sectional view of an embodiment of an ostomy appliance of the invention, Fig 2 shows a release liner having an indication of the size of the hole of an ostomy appliance of the invention for accommodating an ostomy, Fig 3 shows a view from the distal side of the separate sealing member of an ostomy appliance of the invention in which the separate sealing member has been partially everted to increase the size of the hole of an ostomy appliance of the invention for accommodating an ostomy and showing the indication of the size of the hole placed on the release liner below, Fig 4 shows a cross sectional view of the separate sealing member of Fig 3, Fig 5 shows a cross sectional view of an embodiment of an ostomy appliance body side member according to the invention, Fig 6 shows a cross sectional view of a further embodiment of an ostomy appliance body side member according to the invention, Fig 7 shows a cross sectional view of the embodiment of Fig 6 wherein the inner nm has been rolled up, Fig 8 shows a cross sectional view of yet a further embodiment of an ostomy appliance body side member according to the invention, and Fig 9 shows a cross sectional view of the embodiment of Fig 8 wherein the inner nm has been compressed DETAILED DESCRIPTION OF THE DRAWINGS Reference is made to Fig 1 which shows an ostomy appliance according to the invention comprising a body side member 1 comprising an adhesive wafer or pad 2 for se- curing the appliance to the user's skin, said adhesive being covered by a film 9 conventionally used, e g a LDPE film Furthermore, the body side member is secured by a sealing 10 to a flange 11 , preferably made from a foam material A receiving member or bag 4 comprises a flange 12 secured to the flange 11 sealing by a layer of an adhesive 13 The flange 12 may be welded to the receiving member either inside the member or on the outside The flange 11 preferably stretches beyond the inner nm of the wafer or pad 2 in order to prevent that a mouldable adhesive mass 7 of a separate sealing member adheres to the wafer or pad Such adherence might prevent the separate exchange of the sealing member independently of the exchange of the body side member The separate sealing member may comprise a sheet 16 for adhering to the flange of body side member and for adhering the exchangeable receiving member or bag At the outer nm of the flange 11 , the sheet 16 preferably stretches beyond the nm of the flange to provide a handle 17 for gripping for separate exchange of the sealing member Such handle preferably stretches over the full periphery in order to avoid adherence of the adhesive 13 of a separately exchangeable receiving member or bag to the body side member The handle may e g be a slit liner The adhesive 13 may be any adhesive being detachable from the two flanges in order to allow for an exchange of only the receiving member or bag leaving the body side member and the separate sealing member on the abdomen of the ostomate It is desirable that the attachment between the receiving member or bag and the separate sealing member is weaker than the attachment between the separate sealing member and the body side member The adhesive 13 may be an acrylic adhesive or any conventional skin friendly adhesive Furthermore, the separate sealing member comprises a mouldable backing 14 The backing preferably has a tensile strength of 2-5 N/m 2 at an elongation of 300% The separate sealing member may be made from a mouldable adhesive in the form of a paste of a skin-friendly adhesive being sufficiently tacky to secure the appliance or skin barrier to the abdomen and a cohesion ensuring safe removal thereof without leaving residues on the skin The sealing member may be composed of one material or may optionally be composed of two or more layers one of which being a mouldable backing and may optionally be covered with a protecting layer or film All adhesive surfaces may be protected by release liners to be removed before application The separate sealing member may be a uniform mouldable mass of a hypoallergenic, substantially non-memory adhesive or it may comprise further constituents such as a protecting film or a mouldable mesh The separate sealing member may be substituted together with the receiving member 4 leaving the body side member 1 on the skin It is contemplated that the sealing member may be substituted independently of the receiving member according to the need of the user Now referring to Fig 2 is shown a release liner having an indication of the size of the hole of an ostomy appliance of the invention for accommodating an ostomy, at the side in contact with the separate sealing member (distal as compared to the ostomy) In the alternative, the indication may be placed on the side facing away from the separate sealing member (proximal as compared to the ostomy) if the release liner is transparent Fig 3 shows a view from the distal side of the separate sealing member 5 of an ostomy appliance of the invention in which the separate sealing member has been partially everted to increase the size of the hole of an ostomy appliance of the invention for accommodating an ostomy and showing the indication of the size of the hole placed on the release liner 15 below Fig 4 shows a cross sectional view of the separate sealing member of Fig 3 wherein the sealing member 5 in the form of a uniform adhesive mass 7 has been partially everted enlarging the hole 3 and revealing a larger part of the surface of the release liner 15 below and of the indication of the size of the hole The adhesive and the adhesive wafer may be composed of a hypo-allergenic, soft easy-deformable, non-memory putty like adhesive material and is preferably a hydro- colloid based adhesive or a hydrogel A mouldable backing may e g be a Parafilm® or made from a polymer solution which is sprayed on the surface and protects the surface of the adhesive against dissolution by secretions from the stoma and prevent a tacky surface on the side facing the bag The mouldable backing stretches out beyond the outer periphery of the ring in the form of a flange or adhesive layer The mouldable backing may have a tensile strength of from 1 to 10 N/mm 2 , more preferred from 2 to 5 N/mm 2 and most preferred about 2 5 N/mm 2 at elongations up to 300% Fig 5 shows a cross sectional view of an embodiment of an ostomy appliance body side member 1 according to the invention comprising an adhesive wafer or pad 2 for securing the appliance to the user's skin, said adhesive may be covered by a film con- ventionally used Furthermore, the body side member comprises a separate sealing member 5 disposed in the hole of the wafer or pad surrounding the stoma and a release liner 15 A receiving member or bag may be secured to a coupling ring 18. In the embodiment of Fig 6 the sealing member is in the form of a uniform adhesive mass 7 which is thinner in the area next to the central hole for accommodating the stoma The sealing member is provided with a flange 8 and a release liner 15 and a mouldable backing 19 In an alternative embodiment of the invention, the adhesive wafer or pad of a body side member and the sealing member are integrated into one unit having the desired balanced plastic and elastic properties allowing an adaptation of the hole said adhesive unit being thinner in the area next to the central hole for accommodating the stoma In Fig 7, the nm of the central hole has been partially rolled up forming a torus 20 and revealing a larger part of the surface of the release liner 15 below and of the indication In the embodiment of Fig 8 the sealing member is in the form of a uniform adhesive mass 7 provided with grooves 21 encircling the central hole The sealing member is provided with a flange 8 and a release liner 15 This embodiment may also comprise a mouldable backing covering the surface of the adhesive In Fig 9 the nm of the central hole has been enlarged by partially compressing the grooves 21 revealing a larger part of the surface of the release liner 15 below and of the indication of the size of the hole The sealing member of the invention may have any desired form, e g similar to the embodiments shown in W098/17212 DETAILED DESCRIPTION OF THE INVENTION In a first aspect, the invention relates to an ostomy appliance comprising a body side member comprising an adhesive wafer or pad for securing the appliance to the user's skin, said wafer or pad having a hole for receiving a stoma, and an optionally sepa- rately exchangeable receiving member or bag secured to the body side ostomy member for receiving secretions from the ostomy said ostomy appliance further comprising a separate or integrated sealing member disposed in the hole of the wafer or pad surrounding the stoma, said sealing member having a hole for accommodating the stoma and said sealing member having balanced plastic and elastic properties allowing an adaptation of the hole of the sealing member to a stoma by an at least temporary enlarging the hole by everting or rolling the inner nm of the hole for accommodating the stoma When the ostomy appliance of the invention has been placed over and around the stoma the adhesive sealing member may recover essentially to the original form to fit snugly to the stoma The "release" may be performed using e g a finger or more or less automatically due to influence by elastic force, heat and/or humidity causing the 5 sealing member to essentially resume its original shape In a preferred embodiment of the invention at least the area of a release liner covering the separate sealing member is provided with a guide for adaptation of the hole of an ostomy appliance to the size of an ostomy, said guide being visible from the side of the release liner facing the sealing member In one embodiment, the guide is placed at the o side of the release liner facing the sealing member In another embodiment, the release liner is transparent and then the guide may be placed on either side An ostomy appliance according to this embodiment differs from known ostomy appliances comprising a guide for adaptation of the hole of an ostomy appliance to the size of an ostomy in that normally, the guide is placed on the side of the release liner facing 5 away from the sealing member and in that it is normally necessary to use scissors to cut according to the guide Thus, according to the state of the art, it is necessary to use tools in order to adapt the size of the hole of an ostomy appliance to the size of an ostomy and, furthermore, the ostomy appliances of the state of the art do not offer a manner of secure sealing after adaptation by cutting Both disadvantages of the appli- 0 ances of the state of the art are overcome by the invention rendering the indication visible from the distal side of the body side member and rendering the adaptation of an ostomy appliance to the specific ostomy very simple using only the finger and independent of the use of tools Furthermore it differs in that the balanced modulus against deformation and elasticity of the adhesive of a sealing member of an ostomy appliance 5 of the invention is a result of the combined properties of a preferably substantially water-impervious backing layer or film and a skin friendly adhesive Thus, in one extreme, the backing layer or film is elastic and the skin friendly adhesive is plastic, and in the opposite extreme, the backing layer or film is plastic, and the skin friendly adhesive is elastic Any combination of properties therebetween fulfilling the requirements 0 will be suitable according to the invention In second aspect, the invention relates to an ostomy appliance body side member comprising an adhesive wafer or pad for securing the appliance to the user's skin, said wafer or pad having a hole for receiving a stoma, and a separate or integrated sealing member disposed in the hole of the wafer or pad surrounding the stoma wherein the sealing member disposed in the hole of the wafer or pad surrounding the stoma shows balanced plastic and elastic properties allowing an adaptation of the hole of the ostomy appliance to a stoma by enlarging the hole for accommodating the stoma, and wherein at least the area covering the separate sealing member is provided with a guide for adaptation of the hole of an ostomy appliance to the size of an ostomy, said guide being visible from the side of the release liner facing the sealing member A body side member of the invention is preferably prepared so that a separately exchangeable receiving member or bag may be secured to the body side ostomy member for receiving secretions from the ostomy comprises a surface or coupling member for securing the separately exchangeable receiving member or bag In a third aspect, the invention relates to an ostomy sealing member in the form of a mouldable mass or ring which shows a sufficient adhesiveness to adhere to the skin and seal around an ostomy and between the ostomy and an ostomy appliance adapted to receive secretions from the ostomy , which sealing member shows a sufficient cohesion to be removed in one piece, independently of removal of the ostomy ap- pliance without leaving remaining adhesive on the skin or the ostomy appliance, said sealing member having a hole for accommodating a stoma and said sealing member having balanced plastic and elastic properties allowing a temporary enlarging of the hole for receiving a stoma by everting or rolling the inner nm of the hole while placing the sealing member around the stoma In a fourth aspect, the invention relates to a method of applying an ostomy appliance body side member comprising an adhesive wafer or pad for securing the appliance to the user's skin, said wafer or pad having a hole comprising a sealing member having a hole for receiving a stoma wherein the hole of the sealing member is enlarged by everting the inner nm of the hole of the sealing member adapting of the hole to the size of the ostomy, aligning the stoma and the hole of the ostomy appliance body for accommodating the stoma and placing the body side member on the abdomen of the ostomate with the stoma projecting into the hole and bringing the sealing member to seal around the stoma, e g using a finger The enlargement of the hole of the sealing member is preferably carried out by everting and rolling the inner ring forming a torus which after release will unroll and seal against the stoma without risk formation of thin spots in the area around the stoma The release may be effected manually using e g a finger or by influence of humidity causing a hydrocolloid-containing adhesive to swell Using a hydrocolloid-containing adhesive will further contribute to establish a self- sealing effect around the stoma due to the swelling of the adhesive in use In the alternative, the sealing member may be provided with grooves encircling the central opening for an enlargement of the hole by lateral displacement outwardly of the nm compressing the grooves whereafter the sealing member will expand to provide a snug fit to the stoma Two different types of adhesives can be used for the sealing member - both being adaptable to the stoma without the use of tools and having the property that they may be everted or rolled or compressed for a sufficient span of time to apply an ostomy appliance 1 Mouldable adhesives which can be adapted to the stoma by displacement of the adhesive mass inwardly or outwardly whereby it forms a protective mass surrounding the stoma 2 Flexible adhesives which can be adapted to the stoma due to the flexibility and compliance whereby it forms a protective layer on the peπstomal skin surrounding the stoma The mouldable adhesive used in the different compositions of the sealing member is preferably characterised as being a hypoallergenic putty-like adhesive The adhesive may preferably comprise some memory allowing for a displacement of adhesive to adapt an ostomy appliance to a stoma by enlarging the hole for accommodating the stoma, whereafter the adhesive recovers essentially to the original form The memory or elasticity must not, however, be so pronounced that a constriction of the stoma occurs The skm-fπendly adhesive may be a skin-friendly adhesive known per se, e g an ad- hesive comprising hydrocolloids or other moisture absorbing constituents for prolonging the time of use The adhesive may suitably be of the type disclosed in those disclosed in GB patent specification No 1 280 631 , in DK patent specifications Nos 127,578, 148,408, 154,806, 147,226 and 154,747, in EP published application Nos 0 097 846 and 0 415 183, in SE published application No 365 410, in WO publication No 88/06894, in US patent specification No 4,867,748, and in NO published application No 157,686 Especially preferred are the adhesives disclosed in US patent Nos 4,367,732 and 5,051 ,259 and DK patent specification No 169,71 1 A medical grade adhesive may be used for securing the sealing member to the peπs- tomal skin A variety of such barrier adhesives are known in the art and may be used here, one such formulation being disclosed, for example in patent DK 147035 and US 4551490 The mouldable adhesive may be composed of a hypoallergenic, soft, easy- deformable, non-memory putty like adhesive material and is preferably a hydrocolloid based adhesive or a hydrogel The mouldable backing, e g Parafilm® or a polymer solution which is sprayed on the surface, protects the surface of the mouldable mass against dissolution by secrete from the stoma and prevent a tacky surface on the side facing the bag The backing layer or film may be of any suitable material known per se for use in the preparation of ostomy appliances or wound dressings e g a foam, a non-woven layer or a film of polyurethane, polyethylene, polyester or polyamide or optionally a copoly- mer thereof In accordance with the invention it has surprisingly been found that the use of a thinner backing layer or film than is normally used when preparing ostomy appliances, an improved adaptability is obtained at the same time as the modulus is reduced The modulus may be from 1 to 10 N/mm 2 , preferably from 2 to 5 N/mm 2 These properties may be obtained using the same load of adhesive as is conventionally used, and thus, the conventional properties of the adhesive are retained as opposed to the case in which the load of adhesive was lowered generally giving a risk of insufficient tack and adhesive properties The layer of adhesive may preferably be thinner along the inner nm of the adhesive sealing member to improve the mouldabi ty Using a layer or film having a low modulus allowing an easy deformation during application but yet a sufficiently high elasticity to essentially prevent deformation after application ensures that the adhesive does not constrict the stoma when recovering to establish a snug sealing against the stoma The medical grade adhesive secures the unit to the peπstomal skin The flexible back- mg, protects the surface of the adhesive against dissolution by secretions from the stoma and prevent a tacky surface on the side facing the bag This embodiment offers the following advantages it is simple/easy to handle, it may be adapted to stoma without use of tools, it gives rise to no or very little residues on skin after removal, it gives rise to no or little erosion of adhesive, it may easily be adapted to complicated shapes of the stoma and it reduces the risk of an insufficient sealing when disposing or extruding mouldable sealing material towards the stoma The adhesive is preferably a pressure sensitive adhesive having a high degree of plasticity The ratio between plastic (viscous) modulus and elastic modulus is often referred to as the tangens delta value A tangens delta value between 0 5 and 1 2, preferably between 0 8 and 1 0 has been shown to be suitable combined with a elastic modulus (G') of at least 10 2 Pa, preferably of at least 10 4 Pa The tangens delta value of conventional PSAs is normally from 0 4 to 0 8 Adhesives of a non-memory type may e g be a homogeneous mixture of a pressure sensitive adhesive component, mineral oil, and hydrocolloid gums or cohesive strengthening agents as the mass disclosed in US patent No 4,204,540 The mass may also be a composition including one or more hydrocolloids, a film former which is butyl ester of polycarboxyhc resin formed from vinyl methyl ether and maleic anhydride, a plasticizer, a thickening agent and an alcohol solvent as disclosed in EP patent No 0 048 556 A further paste is disclosed in US patent No 5,369, 130 This composition comprises a liquid rubber component and a filler component The rubber component is a diene-type liquid rubber, preferably butadiene- or isoprene-type The filler component is selected from the groups consisting of inorganic fillers, natural polymers, semisynthetic water-soluble polymers and synthetic water-soluble polymers A further composition of a skin protective gel containing polyvinyl methylether or monoi- sopropyl ester of polyvinylmethylether maleic acid is disclosed in US patent No 3,876,771 The composition is a made up of a film forming protective colloidal material in combination with a solvent and a gelling agent Isopropanol is the solvent, monoiso- propyl ester of polyvinyl methylether/maleic acid is a film former and polyvinylpyr- rohdone, polyvinyl methylether, polyacryhc acid and hydroxypropyl cellulose are the gelling agents A hydrophilic elastomeπc pressure sensitive material is disclosed in US patent No 4,750,482 This composition is a water-insoluble, hydrophilic, pressure- sensitive adhesive including at least one irradiation cross-linked synthetic organic polymer (predominantly of derived from vinylpyrrohdone) and an adhesive plasticizer (polyethylene glycol) The composition disclosed in EP 0 048 556 B1 suffers from the drawback that it comprises a considerable amount (25% to 45% by weight) of alcohol, ethanol and isopro- panol being preferred When using such a paste, there it is to be observed that only a limited time for forming the paste after the application as the paste cures when exposed to air Furthermore, the amount of alcohol trapped in the paste must be minimised in order to avoid less attractive physical properties due to an adverse effect on the properties of the adhesive of an ostomy appliance which is placed upon the paste Still further, the considerable amount of alcohol may irritate the skin and such a composition is not advisable to use on skin which has been sensibi sed The pastes disclosed in US patent No 4 204,540 suffers from the drawback that the shapeabihty is very dependant of the content of mineral oil If an insufficient amount of mineral oil is added the composition will be too tough to shape and if too much mineral oil is added the composition becomes sticky and difficult to handle Generally, pastes consisting of polyisobutylene, butyl rubber and mineral oil may be very hard, if the content of butyl rubber is high and hence, the paste will be difficult to shape, or it will be very soft and liquid if the content of butyl rubber is low and the content of mineral oil is high A preferred adhesive composition to be used in the ostomy appliances of the invention are adhesive compositions comprising a water-dispersible polyester showing a very rapid water absorption and improving the wet tack and, at the same time, resistance to disintegration upon contact with body fluids A preferred non-memory putty-like mass to be used according to the invention is in the form of a mouldable mass of a hypo-allergenic, substantially non-memory putty-like ad- hesive comprising a) a blockcopolymer having a major content of di-block copolymer, b) a tackifying liquid constituent, and c) a waxy constituent In a preferred embodiment the sealing member has a flange stretching from the outer nm thereof Such a flange preferably has adhesive on the surface and provides an extra security against leaks and excludes direct contact between the exudates and the coupling part of the ostomy device Thus, a pollution or contamination of parts of the body side member during service or exchange of receiving member or bag is avoided Avoidance of pollution or contamination of the body side member is of great impor- tance when extending the weartime of the body side member as remains of the exu- date on the body side member which may cause odour are avoided Additionally, this embodiment renders it possible to separate the two functions of the sealing around an ostomy and the securing of a separately exchangeable receiving member or bag for receiving secretions from an ostomy to a body side ostomy mem- ber in that it is not mandatory that the securing of the separately exchangeable receiving member to the body side ostomy member impervious to liquid The separately exchangeable receiving member or bag may be secured to the body side ostomy member using an adhesive adhering to a flange or by mechanical means Mechanical fastening means for securing the separately exchangeable receiving member or bag releasably to the body side ostomy member may e g a traditional coupling system using a coupling ring or a zip-like fastener, snaps, buckles, buttons or rings A zip-like fastener may e g be of the type known for closing plastic bags, e g marketed under the trademark Minigπp® A fastening means may also be placed between the separate sealing member disposed in the hole of the wafer or pad surrounding the stoma and the body side member In a preferred embodiment of the invention, the attachment is placed between the sealing member disposed in the hole of the wafer or pad surrounding the stoma and the body side member is obtained using an adhesive This embodiment renders it simple to discriminate between the securing of the sepa- rately exchangeable receiving member or bag for receiving secretions from an ostomy and of the separate sealing member disposed in the hole of the wafer or pad surrounding the stoma Thus, it is simple to decide whether to exchange only the receiving member or bag or to exchange the receiving member or bag and the separate sealing member disposed in the hole of the wafer or pad surrounding the stoma MATERIALS AND METHODS Kraton® G1726 from Shell Styrene-ethylenebutylene-styrene copolymer (SEBS) having a molecular weight of 45,000 as determined by GPC and a content of diblock copolymer of 70% Kraton® D1118 from Shell Styrene-butadiene-styrene copolymer (SBS) having a mo- lecular weight of 103,000 (GPC) and a content of diblock copolymer of 80% Vector® 4114 from Exxon Styrene-isoprene-styrene copolymer (SIS) having a molecular weight of 130,000 and a content of diblock copolymer of 40% and 15% styrene Vistanex® LM-MH from Exxon polyisobutylene (PIB) having a molecular weight of 90,000 (GPC) AQ1045 from Eastman A branched water-dispersible polyester having a Brookfield viscosity at 177 °C of 3,000 - 6,000 cP AQ1350 from Eastman A branched water-dispersible polyester having a Brookfield viscosity at 177 °C of 28,000 - 45,000 cP Kraton® D 1 107 from Shell Chemical Company Styrene-isoprene-styrene copolymer (SIS) having a molecular weight of 212,000-260,000 as determined by GPC and 15% styrene LVSI 101 from Shell Chemical Company Styrene-isoprene diblock copolymer (SI) having a molecular weight of about 30,000 as determined by GPC and 13% styrene Wax Total 40/60 from TOTAL Petroleum jelly Vaselinum Album from Witco Dioctyladipate from International Speciality Chemicals Ltd A plastisizer METALYN 200, a methyl ester of rosin from Hercules Eastoflex E 003, E 1060 and E 1200 from Eastman propylene-ethylene copolymers Eastoflex D127 from Eastman A propylene/1-hexene copolymer Vestoplast 704, 708 and 750 amorphous propylene-πch poly-α-olefins from Huls Chemie Wingtack 10 from Goodyear A liquid polyterpene tackyfier resin Arkon P-90 from Arakawa Forest Chemical Industries Ltd A hydrogenated cyclopenta- diene resin Polybutene oil Hyvis® 10 from BP having a molecular weight of 1 ,500 Polybutene Hyvis® 2000 from BP having a molecular weight M w of 30,000 Mineral Oil PL 500 from Parafluid Mineral Oel Tackifier resin Regalite® R91 resin from Hercules or Arkon® P-90 resin from Arakawa Glycerol PEG 400 from Hoechst Polyethylene glycol Sodium carboxymethylcellulose Akucell® AF2881 from Akzo or Blanose® 9H4XF from Hercules Corp Guar gum Guar Gum FG 200 from Nordisk Gelatine Pectin Pektin LM 12CG Z from Copenhagen Pectin or Pektin USP/100 from Copenhagen Pectin Klucel HXF EP Hydroxypropyl cellulose Gelatin Gelatine P S 98 240 233 from ED Geisthch Sohne AG Zinc Oxide Zinkoxid Pharma from Hoechst AG A Z mixer Type LKB 025 from Herman-Linden was used EXPERIMENTAL PART EXAMPLE 1 Preparation of a mouldable mass to be used according to the invention 100 grams of Kraton® G1726 was used and the amounts of other ingredients used 5 correspond to the composition stated in Table 1 Equal amounts of Kraton® G1726 (SEBS) and of Vistanex® LM-MH were mixed in a Z Mixer for 20 minutes at 160 °C under a vacuum of 100 mbar Then, the vacuum was released, the mixing was continued at 160 °C for 10 minutes and the remains of Vistanex® LM-MH, the wax, and petroleum jelly were admixed and mixed for 10 minutes 0 each Then, the heating was turned off, and guar gum was added at maximum 90 °C under a vacuum of 100 mbar and mixed for 10 minutes Finally, pectin, gelatine and zinc oxide were admixed at a temperature of 90 °C and mixed for 10 minutes EXAMPLE 2 Preparation of a mouldable mass to be used according to the invention 15 100 grams of Kraton® G1726 was used and the amounts of other ingredients used correspond to the composition stated in Table 1 Equal amounts of Kraton® G1726 (SEBS) and Vistanex® LM-MH were mixed in a Z Mixer for 20 minutes at 160 °C under a vacuum of 100 mbar Then, the vacuum was released, the mixing was continued at 160 °C for 10 minutes and the remains of Vis- 20 tanex® LM-MH, the wax, and Hyvis® 10 or PL 500 were admixed and mixed for 10 minutes each Then, the heating was turned off, and guar gum was added at maximum 90 °C under a vacuum of 100 mbar and mixed for 10 minutes Finally, pectin, gelatine and zinc oxide were admixed at a temperature of 90 °C and mixed for 10 minutes EXAMPLES 3 - 5 Preparation of mouldable masses to be used according to the invention In the same manner as described in Example 2 above mouldable masses according to the invention were produced having the compositions stated in the below Table 1 Table 1 Composition of mouldable masses of the invention of Examples 1 - 5 stated in % by weight EXAMPLE 6 Preparation of a mouldable mass to be used according to the invention Equal amounts of Kraton® G1726 (SEBS) and Hyvis® 2000 were mixed in a Z Mixer for 30 minutes at 160 °C under a vacuum of 100 mbar and the Hyvis® 2000 was added in four parts to ensure homogeneity during the admixing over a period of 20 minutes Then, the remains of Hyvis® 2000 was added in four parts at 160 °C over 30 minutes and the vacuum was released The Hyvis® 10 was added in four parts and mixed for 15 minutes Wax was added and mixed for 10 minutes Then, the heating was turned off, and guar gum and CMC were added at maximum 90 °C under a vacuum of 100 mbar and mixed for 10 minutes Finally, pectin, gelatine and zinc oxide were admixed at a temperature of 90 °C and mixed for 10 minutes EXAMPLES 7 - 8 Preparation of mouldable masses to be used according to the invention In the same manner as described in the Example 2 above, mouldable masses according to the invention were produced having the compositions stated in the below Table 2 Table 2 Composition of mouldable masses of the invention of Examples 6 - 8 stated in % by weight EXAMPLES 9 - 10 Preparation of mouldable masses to be used according to the invention Equal amounts of Kraton® G1726 (SEBS) and Hyvis® 2000 were mixed in a Z Mixer for 30 minutes at 160 °C under a vacuum of 100 mbar and the Hyvis® 2000 was added in four parts to ensure homogeneity during the admixing over a period of 20 minutes Then, the remains of Hyvis® 2000 was added in four parts at 160 °C over 30 minutes and the vacuum was released The Hyvis® 10 was added in four parts and mixed for 15 minutes Resin and wax was added and mixed for 10 minutes each Then, the heating was turned off, and CMC were added at maximum 90 °C under a vacuum of 100 mbar and mixed for 10 minutes Finally, pectin, gelatine and zinc oxide were admixed at a temperature of 90 °C and mixed for 10 minutes Table 3 Composition of mouldable masses of the invention of Examples 9 - 10 stated in % by weight The pastes produced in the above Examples are ready to use but may preferably be packed in metered amounts, e g in a blister pack or rod for shipment A rod may be rolled and have a release liner on one or both sides The product is preferably produced and packed under aseptic conditions Preparation of preferred adhesives to be used according to the invention is disclosed in the below Examples Example 11 An adhesive agent having the composition stated in Table 4 was prepared in a Z-blade mixer Before the mixing, the mixing chamber was heated to 140°C by means of an oil heater AQ1045, Eastoflex D127, Eastoflex E1003, dioctyladipate and the hydrocolloids were weighed out separately Firstly Eastoflex D127 and E1003 were mixed for 15 minutes AQ1045 was added and the mixing continued for 10 minutes Dioctyladipate was added and mixed for additional 10 minutes The heat supply was turned off and the mixing chamber was cooled to 80°C The hydrocolloids (a mixture of 5 pectin, hydroxypropyl cellulose and gelatine in the ratio 1 1 5 1 ) were added and the mixing was continued in vacuum until a total mixing time of 60 minutes The adhesive agent was removed from the mixer and pressed into 1 mm thin plates between two sheets of silicon paper in a hydraulic press at 90°C Example 12 10 An adhesive agent having the composition stated in Table 4 was prepared in a Z-blade mixer Before the mixing, the mixing chamber was heated to 140°C by means of an oil heater AQ1350, Eastoflex D127, Eastoflex E1003, Wingtack 10 and dioctyladipate were weighed out separately Firstly Eastoflex D127 and E1003 were mixed for 15 minutes AQ1350 and was added and the mixing continued for 10 minutes Wingtack 5 10 was added and mixed for additional 10 minutes and finally dioctyladipate was added The adhesive agent was removed from the mixer and pressed into 1 mm thin plates between two sheets of silicon paper in a hydraulic press at 90°C Example 13 An adhesive agent having the composition stated in Table 4 was prepared in a Z-blade 20 mixer Before the mixing, the mixing chamber was heated to 150°C by means of an oil heater AQ1045, Vector 4114, LVSI101 , dioctyladipate and the hydrocolloids were weighed out separately Firstly Vector and dioctyldiadipate were mixed at 150°C for 15 minutes LVSI 101 was added and the mixing continued for 10 minutes The mixing chamber was cooled to 130°C and AQ1045 was added and the mixing was continued 25 for an additional 15 minutes The heat supply was turned off and the mixing chamber was cooled to 80°C The hydrocolloids, a mixture of pectin and hydroxypropylcellulose in the ratio 1 1 , and finally zinc oxide were added and the mixing was continued in vacuo until a total mixing time of 60 minutes The adhesive agent was removed from the mixer and pressed into 1 mm thin plates between two sheets of silicon paper in a hydraulic press at 90°C Example 14 An adhesive agent was having the composition stated in Table 4 prepared in a Z-blade mixer Before the mixing, the mixing chamber was heated to 130°C by means of an oil heater AQ1045 and glycerol and the hydrocolloids were weighed out separately Firstly AQ1045 and glycerol were mixed at 130°C for 15 minutes The heat supply was turned off and the mixing chamber was cooled to 80°C The hydrocolloids, a mixture of pectin and gelatine in the ratio 1 2, were added and the mixing continued in vacuum until a total mixing time of 40 minutes The adhesive agent was removed from the mixer and is pressed into 1 mm thin plates between two sheets of silicon paper in a hydraulic press at 90°C Example 15 An adhesive agent having the composition stated in Table 4 was prepared in a Z-blade mixer Before the mixing, the mixing chamber was heated to 130°C by means of an oil heater AQ1045 and PEG 400 and the hydrocolloids were weighed out separately Firstly AQ1045 and PEG 400 were mixed at 130°C for 15 minutes The heat supply was turned off and the mixing chamber was cooled to 80°C The hydrocolloids, a mixture of hydroxypropylcellulose and gelatine in the ratio 1 1 , were added and the mixing continued in vacuo until a total mixing time of 40 minutes The adhesive agent was removed from the mixer and pressed into 1 mm thin plates between two sheets of silicon paper in a hydraulic press at 90°C Example 16 An adhesive agent having the composition stated in Table 4 was prepared in a Z-blade mixer Before the mixing, the mixing chamber was heated to 150°C by means of an oil heater AQ1045, Vector 41 14, LVSI 101 , Arkon P-90 and the hydrocolloids were weighed out separately Firstly Vector was mixed at 150°C for 15 minutes LVSI 101 was added and the mixing continued for 15 minutes The mixing chamber was cooled to 130°C and Arkon P-90 followed by AQ1045 were added and the mixing was continued for an additional 30 minutes The heat supply was turned off and the mixing chamber was cooled to 80°C The pectin was added and the mixing was continued in vacuo until a total mixing time of 90 minutes The adhesive agent was removed from the mixer and pressed into 1 mm thin plates between two sheets of silicon paper in a hydraulic press at 90°C Table 4 EXAMPLES 17 - 21 Adhesives being suitable as pastes having the compositions stated in Table 5 were prepared in a Z-mixer in the same manner as described in Example 1 1 Table 5

Claims: CLAIMS 1 An ostomy appliance comprising a body side member comprising an adhesive wafer or pad for securing the appliance to the user's skin, said wafer or pad having a hole for receiving a stoma, and an optionally separately exchangeable receiving member or bag secured to the body side ostomy member for receiving secretions from the ostomy said ostomy appliance further comprising a sealing member disposed in the hole of the wafer or pad surrounding the stoma wherein the sealing member disposed in the hole of the wafer or pad surrounding the stoma, said sealing member having a hole for accommodating the stoma and said sealing member having balanced plastic and elastic properties allowing an adaptation of the hole to a stoma by a temporary enlarging the hole by everting or rolling the inner nm of the hole for accommodating the stoma 2 An ostomy appliance as claimed in claim 1 , characterised in that at least the area of a release liner covering the separate sealing member is provided with a guide for adaptation of the hole of an ostomy appliance to the size of an ostomy, said guide be- mg visible from the side of the release liner facing the sealing member 3 An ostomy appliance as claimed in claim 1 or 2, characterised in that the sealing member is in the form of a mouldable mass or ring of a hypo-allergenic, adhesive having a backing layer or film 4 An ostomy appliance as claimed in any of claims 1 - 3, characterised in that the sealing member has a flange stretching from the outer nm thereof 5 An ostomy appliance as claimed in any of claims 1 - 4, characterised in that a separately exchangeable receiving member or bag is secured releasably to the body side ostomy member by an adhesive or by mechanical fastening means 6 An ostomy appliance as claimed in claim 5, characterised in that the mechanical fastening means is a traditional coupling system using a coupling ring or a zip-like fastener, snaps, buckles, buttons, rings 7 An ostomy appliance body side member comprising an adhesive wafer or pad for securing the appliance to the user's skin, said wafer or pad having a hole for receiving a stoma, and an optionally exchangeable sealing member disposed in the hole of the wafer or pad surrounding the stoma wherein the sealing member disposed in the hole of the wafer or pad surrounding the stoma shows balanced plastic and elastic properties allowing an adaptation of the hole of the ostomy appliance to a stoma by a temporary enlarging the hole by everting or rolling the inner rim of the hole for accommodating the stoma 8 An ostomy appliance body side member as claimed in claim 7, characterised in that it comprises a surface or coupling member for securing a separately exchangeable receiving member or bag may be secured to the body side ostomy member for receiving secretions from the ostomy 9 An ostomy sealing member in the form of a mouldable mass or ring which shows a sufficient adhesiveness to adhere to the skin and seal around an ostomy and between the ostomy and an ostomy appliance adapted to receive secretions from the ostomy , which sealing member shows a sufficient cohesion to be removed in one piece, independently of removal of the ostomy appliance without leaving remaining adhesive on the skin or the ostomy appliance, said sealing member having a hole for accommodating a stoma and said sealing member having balanced plastic and elastic properties allowing a temporary enlarging of the hole for receiving a stoma by everting or rolling the inner nm of the hole while placing the sealing member around the stoma 10 A method of applying an ostomy appliance body side member comprising an adhesive wafer or pad for securing the appliance to the user's skin, said wafer or pad having a hole comprising a sealing member having a hole for receiving a stoma wherein the hole of the sealing member is enlarged by everting or rolling the inner nm of the hole of the sealing member adapting of the hole to the size of the ostomy, aligning the stoma and the hole of the ostomy appliance body for accommodating the stoma and placing the body side member on the abdomen of the ostomate with the stoma projecting into the hole and bringing the sealing member to seal around the stoma

Inventors: CIOK DANUTA, GOTHJAELPSEN LAILA BUSK, NIELSEN INGER MANN, OLSEN ESKIL HOEJLAND, SLETTEN CARSTEN, CIOK, DANUTA, GOTHJAELPSEN, LAILA, BUSK, NIELSEN, INGER, MANN, OLSEN, ESKIL, HOEJLAND, SLETTEN, CARSTEN
Applicants: CIOK DANUTA, COLOPLAST AS, GOTHJAELPSEN LAILA BUSK, NIELSEN INGER MANN, OLSEN ESKIL HOEJLAND, SLETTEN CARSTEN, CIOK, DANUTA, COLOPLAST A/S, GOTHJAELPSEN, LAILA, BUSK, NIELSEN, INGER, MANN, OLSEN, ESKIL, HOEJLAND, SLETTEN, CARSTEN
Application year: 1998
Main classification: A61F5
IPC codes: A61F5