COMPOSITE SUITABLE FOR USE IN ELECTROCHEMICAL CELLS

Abstract: A composite comprises Aa) at least one first layer which comprises a mixture Ia, comprising a mix IIa consisting of a) from 1 to 95 % by weight of a solid III, preferably a basic solid III, having a primary particle size of from 5 nm to 20 mu m and b) from 5 to 99 % by weight of a polymeric composition IV obtainable by polymerization of b1) from 5 to 100 % by weight, based on the composition IV, of a condensation product V of alpha ) at least one compound VI which is able to react with a carboxylic acid or a sulfonic acid or a derivative or a mixture of two or more thereof, and beta ) at least 1 mol per mol of the compound VI of a carboxylic acid or sulfonic acid VII which contains at least one free-radically polymerizable functional group, or a derivative thereof or a mixture of two or more thereof, and b2) from 0 to 95 % by weight, based on the composition IV, of a further compound VIII having a mean molecular weight (number average) of at least 5000 and polyether segments in the main chain or a side chain, where the proportion by weight of the mix IIa in the mixture Ia is from 1 to 100 % by weight, and the layer is free of an electron-conducting, electrochemically active compound, and B) at least one second layer which comprises an electron-conducting, electrochemically active compound, wherein the first layer or layers and the second layer or layers are joined to one another by one of the two methods V1 or V2: V1) Lamination of the first layer or layers with the second layer or layers under the action of heat or pressure or under the action of heat and pressure, or V2 Corona treatment of the first layer or layers, the second layer or layers or the first layer or layers and the second layer or layers and subsequent bringing together of the corona-treated first layer or layers with the corona-treated or untreated second layer or layers.

Description: Composite suitable for use in electrochemical cells The present invention relates to composites which are suitable for, inter alia, electrochemical cells having electrolytes containing lithium ions; their use in, for example, electrodes; electrodes, sensors, electrochromic windows, displays, capacitors and ion-conducting films comprising such a composite; and also electrochemical cells which comprise such a molding. Electrochemical, in particular rechargeable, cells are generally known, for example from "Ullmann's Encyclopedia of Industrial Chemistry" , 5th Ed. , Vol. A3, VCH Verlagsgesellschaft mbH, Weinheim, 1985, pages 343-397. Among these cells, a special position is occupied by lithium batteries and lithium ion batteries, in particular as secondary cells, owing to their high specific energy storage density. As described, for example, in the above citation from "Ullmann" , the cathode of such cells comprises lithiated manganese, cobalt, vanadium or nickel mixed oxides which in the stoichiometrically simplest case can be described as LiMn 2 0 4 , LiCo0 2 , iV 2 0 5 or LiNi0 2 . These mixed oxides react reversibly with compounds which can incorporate lithium ions into their lattice, for example graphite, with the lithium ions being removed from the crystal lattice and the metal ions such as manganese, cobalt or nickel ions present in the latter being oxidized. This reaction can be utilized in an electrochemical cell for storing electrical energy by separating the compound which takes up lithium ions, i.e. the anode material, and the lithium-containing mixed oxide, i.e. the cathode material, by means of an electrolyte through which the lithium ions migrate from the mixed oxide into the anode material (charging operation). The compounds suitable for the reversible storage of lithium ions are usually fixed on collector electrodes by means of a binder. When the cell is charged, electrons flow through an external voltage source and lithium cations flow through the electrolyte to the anode material. When the cell is used, the lithium cations flow through the electrolyte whereas the electrons flow through a load from the anode material to the cathode material. To avoid a short circuit within the electrochemical cell, a layer which is electrically insulating but permeable to lithium cations is located between the two electrodes. This layer can be a solid electrolyte or a conventional separator. In the production of many electrochemical cells, e.g. a lithium ion battery in the form of a round cell, the necessary battery films, i.e. cathode, anode and separator films, are combined using a rolling apparatus to produce a battery roll. In conventional lithium ion batteries, the cathode and anode film(s) are joined to collector electrodes in the form of, for example, an aluminum or copper foil. Such metal foils ensure sufficient mechanical stability. In contrast, the separator film has to withstand the mechanical stresses on its own, which presents no problem in the case of conventional separator films based on, for example, polyolefins and having the conventional thickness. To further improve the mechanical stability of such conventional separator films, JP 09-134 730 and JP 09-161 815 propose joining these separator films to the anode and/or cathode film by means of a bonding layer. In contrast to conventional separator films, the mechanical stability of separator films filled with a solid is generally not sufficient to ensure problem-free rolling of the films. It is an object of the present invention to provide a composite which has at least one layer filled with a solid and is suitable for use in electrochemical cells and is able to withstand the mechanical stresses in the production of, for example, batteries. We have found that this object is achieved by the composite of the present invention. This comprises at least one first layer which is filled with a solid, e.g. a separator layer, and at least one second layer which can be a cathode layer or an anode layer. The composite of the present invention thus comprises a separator layer/anode layer combination or separator layer/cathode layer combination or cathode layer/separator layer/anode layer combination; it is of course possible for further layers and/or support materials defined herein to be present. The present invention accordingly provides, in one embodiment, a composite comprising Aa) at least one first layer which comprises a mixture la, comprising a mix Ila consisting of a) from 1 to 95% by weight of a solid III, preferably a basic solid III, having a primary particle size of from 5 nm to 20 μm and b) from 5 to 99% by weight of a polymeric composition IV obtainable by polymerization of bl) from 5 to 100% by weight, based on the composition IV, of a condensation product V of ) at least one compound VI which is able to react with a carboxylic acid or a sulfonic acid or a derivative or a mixture of two or more thereof, and β) at least 1 mol per mol of the compound VI of a carboxylic acid or sulfonic acid VII which contains at least one free-radically polymerizable functional group, or a derivative thereof or a mixture of two or more thereof, and b2) from 0 to 95 % by weight, based on the composition IV, of a further compound VIII having a mean molecular weight (number average) of at least 5000 and polyether segments in the main chain or a side chain, where the proportion by weight of the mix Ila in the mixture la is from 1 to 100% by weight, and the layer is free of an electron-conducting, electrochemically active compound, and B) at least one second layer which comprises an electron- conducting, electrochemically active compound, wherein the first layer or layers and the second layer or layers are joined to one another by one of the two methods VI or V2: VI) Lamination of the first layer or layers with the second layer or layers under the action of heat or pressure or under the action of heat and pressure, or V2) Corona treatment of the first layer or layers, the second layer or layers or the first layer or layers and the second layer or layers and subsequent bringing together of the corona-treated first layer or layers with the corona-treated or untreated second layer or layers. The first layer or layers preferably comprise(s) a mixture la comprising a mix Ha consisting of a) from 1 to 95 % by weight of a solid III, preferably a basic solid III, having a primary particle size of from 5 nm to 20 μm and b) from 5 to 99% by weight of a polymeric composition IV obtainable by polymerization of bl) from 5 to 100% by weight, based on the composition IV, of a condensation product V of ) a polyhydric alcohol VI which has carbon and oxygen atoms in the main chain, and β) at least 1 mol per mol of the polyhydric alcohol VI of a α,jS-unsaturated carboxylic acid VII, and b2) from 0 to 95 % by weight, based on the composition IV, of a further compound VIII having a mean molecular weight (number average) of at least 5000 and polyether segments in the main chain or a side chain, where the proportion by weight of the mix Ila in the mixture la is from 1 to 100% by weight. In a further embodiment, the present invention provides a composite comprising Ab) at least one first layer which comprises a mixture lb comprising a mix lib consisting of a) from 1 to 95 % by weight of a solid III, preferably a basic solid, having a primary particle size of from 5 nm to 20 μ and b) from 5 to 99% by weight of a polymer IX obtainable by polymerization of bl) from 5 to 75 % by weight, based on the polymer IX, of a free-radically polymerizable compound X which is different from the carboxylic acid or the sulfonic acid VII or a derivative thereof, or a mixture of two or more thereof, and b2) from 25 to 95 % by weight, based on the polymer IX, of a further compound VIII having a mean molecular weight (number average) of at least 5000 and polyether segments in the main chain or a side chain, where the proportion by weight of the mix lib in the mixture lb is from 1 to 100% by weight and the layer is free of an electron-conducting, electrochemically active compound, and B) at least one second layer which comprises an electron- conducting, electrochemically active compound, wherein the first layer or layers and the second layer or layers are joined to one another by one of the two methods VI or V2: VI) Lamination of the first layer or layers with the second layer or layers under the action of heat or pressure or under the action of heat and pressure, or V2) Corona treatment of the first layer or layers, the second layer or layers or the first layer or layers and the second layer or layers and subsequent bringing together of the corona-treated first layer or layers with the corona- treated second layer or layers. The present invention further provides a composite comprising at least one first layer Aa or at least one first layer Ab or at least one first layer Aa and at least one first layer Ab, at least one second layer B, each as defined above, and C) at least one bonding layer. The components present in the respective layers of the composite of the present invention are described in more detail below. first laver A The solid III used in this layer is, first and foremost, an inorganic solid, preferably an inorganic basic solid, selected from the group consisting of oxides, mixed oxides, silicates, sulfates, carbonates, phosphates, nitrides, amides, imides and carbides of the elements of main groups I, II, III and IV and transition group IV of the Periodic Table; a polymer selected from the group consisting of polyethylene, polypropylene, polystyrene, polytetrafluoroethylene, polyvinylidene fluoride, polyamides, polyimides; a solids dispersion comprising such a polymer; and a mixture of two or more thereof. Examples which may be mentioned are, in particular: oxides such as calcium oxide, silicon dioxide, aluminum oxide, magnesium oxide or titanium dioxide, mixed oxides, for example of the elements silicon, calcium, aluminum, magnesium, titanium; silicates such as ladder, chain, sheet and framework silicates, preferably wollastonite, in particular hydrophobicized wollastonite, sulfates such as alkali metal and alkaline earth metal sulfates; carbonates such as alkali metal and alkaline earth metal carbonates, e.g. calcium, magnesium or barium carbonate or lithium, potassium or sodium carbonate; phosphates such as apatites; nitrides; amides; imides; carbides; polymers such as polyethylene, polypropylene, polystyrene, polytetrafluoroethylene, polyvinylidene fluoride; polyamides; polyimides; or other thermoplastics, thermosets, microgels, solids dispersions, in particular those comprising the abovementioned polymers, and also mixtures of two or more of the abovementioned solids. Furthermore, inorganic solids which conduct Li ions, preferably an inorganic basic solid which conducts Li ions, can be used according to the invention as solid III. Examples are: lithium borates such as Li 4 B 6 O π * xH 2 O, Li 3 (B0 2 ) 3 , Li 9 B 4 O 7 * xH 2 0, LiB0 2 , where x can be from 0 to 20; lithium aluminates such as Li 2 0 * A1 2 0 3 * H 2 0, Li 2 Al 2 0 4 , LiA10 2 ; lithium aluminosilicates such as lithium-containing zeolites, feldspars, feldspar substitutes, phyllosilicates and inosilicates, and, in particular, LiAlSi 2 O 6 (spodumene), LiAlSi 4 O 10 (petullite), LiAlSi0 4 (eucryptite), mica such as K[Li,Al] 3 [AlSi] 4 O 10 (F-OH) 2 ,/ K[Li,Al,Fe] 3 [AlSi] 4 O 10 (F-OH) 2 ; lithium zeolites, in particular those in fiber, sheet or cube form, in particular those having the formula Li 2/z O * Al 2 O 3 * xSi0 2 * yH 2 0, where z corresponds to the valence, x is from 1.8 to about 12 and y is from 0 to about 8; lithium carbides such as Li 2 C 2 , Li 4 C; Li 3 N; lithium oxides and mixed oxides such as LiA10 2 , Li 2 Mn0 3 , Li 2 0, Li 2 0 2 , Li 2 Mn0 4 , Li 2 Ti0 3 ; Li 2 NH; LiNH 2 ; lithium phosphates such as Li 3 P0 4 , LiP0 3 , LiAlFP0 4 , LiAl(OH)P0 4 , LiFePO 4 , LiMnPO 4 ; Li 2 C0 3 ; lithium silicates in ladder, chain, sheet and framework form, e.g. Li 2 SiO 3 , Li 2 Si0 4 and Li 6 Si 2 ; lithium sulfates such as Li 2 S0 4 , LiHS0 4 , LiKS0 4 ; the Li compounds mentioned in the discussion of the cathode layer, with the presence of conductive black being ruled out when they are used as solid III; and also mixtures of two or more of the abovementioned solids which conduct Li ions. Particularly suitable solids III are basic solids. For the purposes of the present invention, basic solids are those whose mixture with a liquid, water- containing diluent which itself has a pH of at most 7 has a higher pH than this diluent. The solids are preferably very largely insoluble in the liquid used as electrolyte and electrochemically inert in the battery medium. Particularly suitable solids are those which have a primary particle size of from 5 nm to 20 μm, preferably from 0.01 to 10 μm and in particular from 0.1 to 5 μm, where the particle sizes specified are determined by electron microscopy. The melting point of the solid is preferably above the operating temperature customary for the electrochemical cell; melting points of above 120°C, in particular above 150° C, have been found to be particularly useful. In terms of their external shape, the solids can be symmetrical, i.e. have an aspect ratio height: width: length of about 1 and be in the form of spheres, granules, approximately round structures, but also in the form of any polyhedra such as cuboids, tetrahedra, hexahedra, octahedra or bipyramids, or can be distorted or asymmetric, i.e. have an aspect ratio height: width: length different from 1 and be in the form of needles, asymmetric tetrahedra, asymmetric bipyramids, asymmetric hexahedra or octahedra, platelets, disks or as fibers. If the solids are in the form of asymmetric particles, the abovementioned upper limit for the primary particle size relates in each case to the smallest axis. As compound VI which is able to react with a carboxylic acid or a sulfonic acid VII or a derivative or a mixture of two or more thereof, it is possible in principle to use all compounds which fulfill this criterion. The compound VI is preferably selected from the group consisting of monohydric or polyhydric alcohols having only carbon atoms in the main chain; monohydric or polyhydric alcohols whose main chain comprises at least two carbon atoms plus at least one atom selected from the group consisting of oxygen, phosphorus and nitrogen; silicon-containing compounds; amines having at least one primary amino group; amines having at least one secondary amino group; aminoalcohols; monohydric or polyhydric thiols; compounds containing at least one thiol group and at least one hydroxyl group; and mixtures of two or more thereof. Among these, preference is in turn given to compounds VI containing two or more functional groups which can react with the carboxylic acid or sulfonic acid. When compounds VI containing amino groups as functional group are used, preference is given to using those having secondary amino groups so that after condensation/crosslinking there are either absolutely no free NH groups or only small amounts thereof present in the mixture la. Specific examples of preferred compounds are: monohydric or polyhydric alcohols which have only carbon atoms in the main chain and have from 1 to 20, preferably from 2 to 20 and in particular from 2 to 10, alcoholic OH groups, in particular dihydric, trihydric and tetrahydric alcohols, preferably having from 2 to 20 carbon atoms, e.g. ethylene glycol, 1,2- or 1,3-propanediol, 1,2- or 1,3-butanediol, 1,4-butenediol or 1,4-butynediol, 1,6-hexanediol, neopentyl glycol, 1,2- dodecanediol, glycerol, trimethylolpropane, pentaerythritol or sugar alcohols, hydroquinone, novolak, bisphenol A; it is also possible, as can be seen from the above definition, to use monohydric alcohols such as methanol, ethanol, propanol, n-, sec- or tert-butyl, etc.; use can also be made of polyhydroxyolefins, preferably those having two terminal hydroxyl groups, e.g. α,ω-dihydroxybutadiene; polyester polyols as are known, for example, from Ullmanns Encyclopadie der technischen Chemie, 4th edition, Volume 19, pp. 62-65 and are obtained, for example, by reaction of dihydric alcohols with polybasic, preferably dibasic, polycarboxylic acids; monohydric or polyhydric alcohols whose main chain comprises at least two carbon atoms plus at least one oxygen atom, preferably polyether alcohols such as polymerization products of alkylene epoxides, for example isobutylene oxide, propylene oxide, ethylene oxide, 1,2-epoxybutane, 1,2- epoxypentane, 1,2-epoxyhexane, tetrahydrofuran, styrene oxide; use can also be made of polyether alcohols which are modified at the end groups, e.g. polyether alcohols modified by NH 2 end groups; these alcohols preferably have a molecular weight (number average) of from 100 to 5000, more preferably from 200 to 1000 and in particular from 300 to 800; such compounds are known per se and are commercially available, for example under the trade names Pluriol or Pluronic (BASF Aktiengesellschaft); alcohols as defined above in which some or all carbon atoms are replaced by silicon; compounds of this type which can be used are, in particular, polys iloxanes or alkylene oxide-siloxane copolymers or mixtures of polyether alcohols and polysiloxanes as are described, for example, in EP-B 581 296 and EP-A 525 728; as regards the molecular weight of these alcohols, what has been said above also applies; alcohols as defined above, in particular polyether alcohols, in which some or all oxygen atoms are replaced by sulfur atoms; with regard to the molecular weight of these alcohols, what has been said above likewise applies; monohydric or polyhydric alcohols whose main chain comprises at least two carbon atoms plus at least one phosphorus atom or at least one nitrogen atom, e.g. diethanolamine and triethanolamine; lactones which are derived from compounds of the formula HO-(CH 2 ) z - COOH, where z is from 1 to 20, e.g. e-caprolactone, jδ-propiolactone, 7-butyrolactone or methyl-e-caprolactone; silicon-containing compounds such as dichlorosilane or trichlorosilane, phenyltrichlorosilane, diphenyldichlorosilane, dimethylvinylchlorosilane; silanols such as trimethylsilanol; amines having at least one primary and/or secondary amino group, e.g. butylamine, 2-ethylhexylamine, ethylenediamine, hexamethylenediamine, diethylenetriamine, tetraethylenepentamine, pentaethylenehexamine, aniline, phenylenediamine; polyetherdiamines such as 4,7-dioxydecane-l , 10-diamine, 4, 11- dioxytetradecane-1 , 14-diamine; monohydric or polyhydric thiols, e.g. aliphatic thiols such as methane thiol, ethanethiol, cyclohexanethiol, dodecanethiol; aromatic thiols such as thiophenol, 4-chlorothiophenol, 2-mercaptoaniline; compounds containing at least one thiol group and at least one hydroxyl group, e.g. 4-hydroxythiophenol and monothio derivatives of the abovementioned polyhydric alcohols; amino alcohols such as ethanolamine, N-methylethanolamine, N-ethylethanolamine, N-butylethanolamine, 2-amino-l-propanol, 2-amino-l- phenylethanol, monoamino or polyamino polyols having more than two aliphatically bound hydroxyl groups, e.g. tris(hydroxymethyl)methylamine, glucamine , N , N ' -b is (2-hydroxy methyl)ethy lenediamine . It is also possible to use mixtures of two or more of the above-defined compounds VI. According to the present invention, the abovementioned compounds VI are condensed with a carboxylic acid or sulfonic acid VII which contains at least one free-radically polymerizable functional group or a derivative thereof or a mixture of two or more thereof, in which reaction at least one, preferably all, of the free groups capable of condensation within the compounds VI are condensed with the compound VII. Carboxylic acids or sulfonic acids VII which can be used for the purposes of the present invention are in principle all carboxylic and sulfonic acids which contain at least one free-radically polymerizable functional group, and also their derivatives. The term "derivatives" used here encompasses both compounds which are derived from a carboxylic or sulfonic acid and in which the acid function is modified, e.g. esters, acid halides or acid anhydrides, and compounds which are derived from a carboxylic or sulfonic acid and in which the carbon skeleton of the carboxylic or sulfonic acid is modified, e.g. halocarboxylic or halosulfonic acids. Examples of compound VII are, in particular: α,β-unsaturated carboxylic acids or jβ,γ-unsaturated carboxylic acids. Particularly suitable a,/3-unsaturated carboxylic acids are those of the formula where R 1 , R 2 and R 3 are hydrogen or C 1 -C 4 -alkyl radicals; among these, preference is in turn given to acrylic acid and methacrylic acid; other suitable compounds are cinnamic acid, maleic acid, fumaric acid, itaconic acid or p-vinylbenzoic acid, and also derivatives thereof, e.g. anhydrides such as maleic anhydride or itaconic anhydride; halides, in particular chlorides, such as acryloyl or methacryloyl chloride; esters such as (cyclo)alkyl (meth)acrylates having up to 20 carbon atoms in the alkyl radical, e.g. methyl, ethyl, propyl, butyl, hexyl, 2-ethylhexyl, stearyl, lauryl, cyclohexyl, benzyl, trifluoromethyl, hexafluoropropyl or tetrafluoropropyl (meth)acrylate, polypropylene glycol mono(meth)acrylates, polyethylene glycol mono(meth)acrylates, poly(meth)acrylates of polyhydric alcohols, e.g. glyceryl di(meth)acrylate, trimethylolpropane di(meth)acrylate, pentaerythrityl di- or tri(meth)acrylate, diethylene glycol bis(mono(2-acryloxy- ethyl)carbonate), poly(meth)acrylates of alcohols which themselves in turn contain a free-radically polymerizable group, e.g. esters of (meth)acrylic acid and vinyl and/or allyl alcohol; vinyl esters of other aliphatic or aromatic carboxylic acids, e.g. vinyl acetate, vinyl propionate, vinyl butyrate, vinyl hexanoate, vinyl octanoate, vinyl decanoate, vinyl stearate, vinyl palmitate, vinyl crotonate, divinyl adipate, divinyl sebacate, vinyl 2-ethylhexanoate, vinyl trifluoroacetate; allyl esters of other aliphatic or aromatic carboxylic acids, e.g. allyl acetate, allyl propionate, allyl butyrate, allyl hexanoate, allyl octanoate, allyl decanoate, allyl stearate, allyl palmitate, allyl crotonate, allyl salicylate, allyl lactate, diallyl oxalate, diallyl malonate, allyl- and diallyl succinate, diallyl glutarate, diallyl adipate, diallyl pimelate, diallyl cinnamate, diallyl maleate, diallyl phthalate, diallyl isophthalate, triallyl benzene- 1, 3, 5-tricarboxylate, diallyl cinnatricarboxylate, allyl trifluoroacetate, allyl perfluorobutyrate, allyl perfluorooctanoate; j6,7-unsaturated carboxylic acids or their derivatives, e.g. vinylacetic acid, 2-methylvinylacetic acid, isobutyl 3-butenoate, allyl 3-butenoate, allyl 2-hydroxy-3-butenoate, diketene; sulfonic acids such as vinylsulfonic acid, allylsulfonic and methylylsulfonic acids, and also their esters and halides, vinyl benzenesulfonate, 4-vinylbenzenesulfonamide. It is also possible to use mixtures of two or more of the above-described carboxylic and/or sulfonic acids. Specific examples of compound X which is capable of free-radical polymerization and can be used for preparing the polymer IX are: olefinic hydrocarbons such as ethylene, propylene, butylene, isobutene, hexene or higher homologues and vinylcyclohexane; (meth)acrylonitrile; halogen-containing olefinic compounds such as vinylidene fluoride, vinylidene chloride, vinyl fluoride, vinyl chloride, hexafluoropropene, trifluoropropene, 1 ,2-dichloroethylene, 1,2-difluoroethylene and tetrafluoroethylene; vinyl alcohol, vinyl acetate, N-vinylpyrrolidone, N-vinylimidazole, vinylformamide; phosphonitrilic chlorides such as hexachloro(triphosphazene), and also derivatives thereof which are partially or completely substituted by alkoxy, phenoxy, amino and fluoroalkoxy groups, i.e. compounds which can be polymerized to form polyphosphazenes; aromatic, olefinic compounds such as styrene, α-methylstyrene; vinyl ethers such as methyl, ethyl, propyl, isopropyl, butyl, isobutyl, hexyl, octyl, decyl, dodecyl, 2-ethylhexyl, cyclohexyl, benzyl, trifluoromethyl, hexafluoropropyl and tetrafluoropropyl vinyl ether. It is, of course, also possible to use mixtures of the above compounds X, resulting in copolymers in which the monomers are, depending on the method of preparation, distributed randomly or arranged in blocks. Both these compounds X and the condensation products V .are polymerized by conventional methods well known to those skilled in the art, preferably polymerized by a free-radical mechanism; as regards the molecular weights obtained, what is said below for the compound VIII applies. Suitable compounds VIII are, first and foremost, compounds having a mean molecular weight (number average) of at least 5000, preferably from 5000 to 20,000,000, in particular from 100,000 to 6,000,000, which are able to solvate lithium cations and function as binders. Examples of suitable compounds VIII are polyethers and copolymers which comprise at least 30% by weight of the following structural unit, based on the total weight of the compound VIII: where R 1 , R 2 , R 3 and R 4 are aryl groups, alkyl groups, preferably methyl groups, or hydrogen and can be identical or different and contain heteroatoms such as oxygen, nitrogen, sulfur or silicon. Such compounds are described, for example, in: M.B. Armand et. al., Fast Ion Transport in Solids, Elsevier, New York, 1979, pp. 131-136, or in FR-A 7832976. The compound VIII can also consist of a mixture of two or more such compounds. The above-defined polymeric composition IV or the polymer IX can also be in the form of a foam, in which case the solid III is present as a dispersion therein. The mixes Ila should, according to the present invention, consist of from 1 to 95 % by weight, preferably from 25 to 90% by weight and in particular from 30 to 70% by weight, of a solid III and from 5 to 99% by weight, preferably from 10 to 75 % by weight and in particular from 30 to 70% by weight, of a polymeric composition IV, and the compound VIII of the polymeric composition IV should advantageously have a mean molecular weight (number average) of from 5000 to 100,000,000, preferably from 50,000 to 8,000,000. The polymeric composition IV can be obtained by reacting from 5 to 100% by weight, preferably from 30 to 70% by weight, based on the polymeric composition IV, of a compound V with from 0 to 95 % by weight, in particular from 30 to 70% by weight, based on the polymeric composition IV, of a compound VIII. The mixes lib should, according to the present invention, consist of from 1 to 95 % by weight, preferably from 25 to 90% by weight and in particular from 30 to 70% by weight, of a solid III and from 5 to 99% by weight, preferably from 10 to 75 % by weight and in particular from 30 to 70% by weight, of a polymer IX, and the compound VIII of the polymer IX should advantageously have a mean molecular weight (number average) of from 5000 to 100,000,000, preferably from 50,000 to 8,000,000. The polymer IX can be obtained by reacting from 5 to 75 % by weight, preferably from 30 to 70% by weight, based on the polymer IX, of a compound X with from 25 to 95 % by weight, in particular from 30 to 70% by weight, based on the polymer IX, of a compound VIII. In the following, the mixtures la and lb used according to the present invention and the mixes Ila and lib used according to the present invention are discussed together and referred to as "mixture used according to the present invention" and "mix used according to the present invention" respectively. To prepare the mixture used according to the present invention which should comprise a mix used according to the present invention in an amount of from 1 to 100% by weight, preferably from 35 to 100% by weight and in particular form 30 to 70% by weight, based on the mixture used according to the present invention, a mixture of a solid III, a condensation product V and, if desired, a compound VIII or a mixture of a solid III, a compound X, a compound VIII and customary additives such as plasticizers, preferably plasticizers comprising polyethylene oxide or polypropylene oxide, can be prepared. second layer B As polymeric binder used within this second layer B, particular mention may be made of the following polymers: 1) Homopolymers, copolymers or block copolymers IVa (polymers IVa) obtainable by polymerization of the above-defined mixtures la or lb. 2) Polycarbonates such as polyethylene carbonate, polypropylene carbonate, polybutadiene carbonate, polyvinylidene carbonate. 3) Homopolymers, copolymers and block copolymers prepared from a) olefinic hydrocarbons such as ethylene, propylene, butylene, isobutene, propene, hexene or higher homologues, butadiene, cyclopentene, cyclohexene, norbornene, vinylcyclohexane; b) aromatic hydrocarbons such as styrene and methylstyrene; c) esters of acrylic acid or methacrylic acid, e.g. methyl, ethyl, propyl, isopropyl, butyl, isobutyl, hexyl, octyl, decyl, dodecyl, 2-ethylhexyl, cyclohexyl, benzyl, trifluoromefhyl, hexafluoropropyl or tetrafluoropropyl aery late or methacrylate; d) acrylonitrile, methacrylonitrile, N-methylpyrrolidone, N-vinylimidazole, vinyl acetate; e) vinyl ethers such as methyl, ethyl, propyl, isopropyl, butyl, isobutyl, hexyl, octyl, decyl, dodecyl, 2-ethylhexyl, cyclohexyl, benzyl, trifluoromethyl, hexafluoropropyl or tetrafluoropropyl vinyl ether; f) halogen-containing olefinic compounds such as vinyl chloride, vinyl fluoride, vinylidene fluoride, vinylidene chloride, hexafluoropropene, trifluoropropene, 1,2-dichloroethene, 1,2-di- fluoroethene, tetrafluoroethene. 4) Polyurethanes, for example obtainable by reacting a) organic dusocyanates having from 6 to 30 carbon atoms, for example aliphatic acyclic dusocyanates such as hexamethylene 1,5- diisocyanate and hexamethylene 1,6-diisocyanate, aliphatic cyclic dusocyanates such as cyclohexylene 1 ,4-diisocyanate, dicyclohexylmethane diisocyanate and isophorone diisocyanate or aromatic dusocyanates such as tolylene 2,4-diisocyanate, tolylene 2,6-diisocyanate, m-tetramethylxylene diisocyanate, p- tetramethylxylene diisocyanate, tetrahydronaphthylene 1,5- diisocyanate and diphenylmethane 4,4'-diisocyanate or mixtures of such compounds, with b) polyhydric alcohols such as polyesterols, polyetherols and diols. The polyesterols are advantageously predominantly linear polymers having terminal OH groups, preferably those having two or three, in particular two, OH end groups. The acid number of the poly- esterols is less than 10 and preferably less than 3. The polyesterols can be prepared in a simple manner by esterification of aliphatic or aromatic dicarboxylic acids having from 4 to 15 carbon atoms, preferably from 4 to 6 carbon atoms, with glycols, preferably glycols having from 2 to 25 carbon atoms, or by polymerization of lactones having from 3 to 20 carbon atoms. Examples of dicarboxylic acids which can be used are glutaric acid, pimelic acid, suberic acid, sebacic acid, dodecanoic acid and preferably adipic acid and succinic acid. Suitable aromatic dicarboxylic acids are terephthalic acid, isophthalic acid, phthalic acid or mixtures of these dicarboxylic acids with other dicarboxylic acids, e.g. diphenic acid, sebacic acid, succinic acid and adipic acid. The dicarboxylic acids can be used individually or as mixtures. To prepare the polyesterols, it may be advantageous to use the corresponding acid derivatives such as carboxylic anhydrides or carboxylic chlorides in place of the dicarboxylic acids. Examples of suitable glycols are diethylene glycol, 1,5-pentanediol, 1, 10-decanediol and 2,2,4-trimethylpentane- 1 ,5-diol. Preference is given to using 1 ,2-ethanediol, 1 ,3- propanediol, 2-methylpropane-l ,3-diol, 1 ,4-butanediol, 1 ,6- hexanediol, 2,2-dimethylpropane-l ,3-diol, 1 ,4-dimethylolcyclohexane, 1 ,4-diethanolcyclohexane and ethoxylated or propoxylated products of 2,2-bis(4-hydroxyphenyl)propane (bisphenol A). Depending on the desired properties of the polyurethanes, the polyols can be used alone or as a mixture in various mixing ratios. Suitable lactones for preparing the polyesterols are, for example, α,α- dimethyl-β-propiolactone, γ-butyrolactone and preferably e-caprolactone. The polyetherols are essentially linear substances having terminal hydroxyl groups and containing ether bonds. Suitable polyetherols can easily be prepared by polymerization of cyclic ethers such as tetrahydrofuran or by reacting one or more alkylene oxides having from 2 to 4 carbon atoms in the alkylene radical with an initiator molecule containing two active hydrogen atoms in bound form in the alkylene radical. Examples of suitable alkylene oxides are ethylene oxide, 1,2-propylene oxid, epichlorohydrin, 1 ,2-butylene oxide and 2,3-butylene oxide. The alkylene oxides can be used individually, alternately in succession or as a mixture. Suitable initiator molecules are, for example, water, glycols such as ethylene glycol, propylene glycol, 1 ,4-butanediol and 1,6- hexanediol, amines such as ethylenediamine, hexamethylenediamine and 4,4'-diaminodiphenylmethane and aminoalcohols such as ethanolamine. Suitable polyesterols and polyetherols and their preparation are described, for example, in EP-B 416 386; suitable polycarbonatediols, preferably those based on 1,6-hexanediol, and their preparation are described, for example, in US-A 4 131 731. Use can advantageously be made of up to 30% by weight, based on the total mass of the alcohols, of aliphatic diols having from 2 to 20, preferably from 2 to 10, carbon atoms, e.g. 1,2-ethane- diol, 1,3-propanediol, 1,4-butanediol, 1,6-hexanediol, 1,5- pentanediol, 1 , 10-decanediol, 2-methylpropane-l,3-diol, 2,2- dimethylpropane-1 ,3-diol, 2-methyl-2-butylpropane-l ,3-diol, 2,2- dimethylbutane-l ,4-diol, 1,4-dimethylolcyclohexane, neopentyl glycol hydroxypivalate, diethylene glycol, triethylene glycol and methyldi- ethanolamine or aromatic-aliphatic or aromatic-cycloaliphatic diols having from 8 to 30 carbon atoms where possible aromatic structures are heterocyclic ring systems or preferably isocyclic ring systems, for example naphthalene or, in particular, benzene derivatives such as bisphenol A, symmetrically diethoxylated bisphenol A, symmetrically dipropoxylated bisphenol A, higher ethoxylated or propoxylated bisphenol A derivatives or bisphenol F derivatives, and also mixtures of such compounds. Use can advantageously be made of up to 5 % by weight, based on the total mass of the alcohols, of aliphatic triols having from 3 to 15, preferably from 3 to 10, carbon atoms, for example trimethylolpropane or glycerol, the reaction product of such compounds with ethylene oxide and/or propylene oxide, and also mixtures of such compounds. The polyhydric alcohols may bear functional groups, for example neutral groups such as siloxane groups, basic groups such as, in particular, tertiary amino groups or acid groups or their salts or groups which are easily converted into acid groups; these groups are introduced via a polyhydric alcohol. Preference is given to using diol components which bear such groups, e.g. N-methyldiethanolamine , diethyl N , N-bis(hydroxy- 5 ethyl)aminomethylphosphonate or 3-sulfopropyl N,N- bis(hydroxyethyl)-2-aminoacetate, or dicarboxylic acids which bear such groups and can be used for the preparation of polyesterols, for example 5-sulfoisophthalic acid. o Acid groups are, in particular, the phosphoric acid, phosphonic acid, sulfur ic acid, sulfonic acid, carboxyl or ammonium group. Groups which are easily converted into acid groups are, for example, ester groups or salts, preferably of the alkali metals 5 such as lithium, sodium or potassium. 5) The above-described polyesterols themselves; care should be taken to ensure that molecular weights in the range from 10,000 to 2,000,000, preferably from 50,000 to 1,000,000 are obtained. 0 6) Polyamines, polys iloxanes and polyphosphazenes, in particular those which have already been discussed in the description of the polymer IVb. 7) Polyetherols as have been described, for example, in the above discussion of the polymer IVa as compound IX or in the discussion of the polyurethanes. If the layer B is a cathode layer, it comprises an electron-conducting, electrochemically active compound customarily used for cathodes (cathode compound) which is able to release lithium ions on charging, preferably a lithium compound. Particular examples which may be mentioned are: LiCoO 2 , LiNiO 2 , LiNi x CO y O 2 , LiNi x CO y Al z 0 2 , where 0<x,y,z<l, Li x MnO 2 (0<x≤l), Li x Mn 2 O 4 (0<x<2), Li x Mo0 2 (0<x<2), Li x Mn0 3 (0<x<l), Li x Mn0 2 (0<x<2), Li x Mn 2 0 4 (0<x<2), Li x V 2 O 4 (0<x<2.5), Li x V 2 O 3 (0<x<3.5), Li x VO 2 (0<x<l), Li x W0 2 (0<x<l), Li x W0 3 (0<x≤l), Li x Ti0 2 (0<x<l), Li χ Ti 2 0 4 (0<x<2), Li χ RuO 2 (0<x<l), Li x Fe 2 θ 3 (0<x<2), Li x Fe 3 0 4 (0<x<2), Li x Cr 2 0 3 (0<x<3), Li x Cr 3 0 4 (0<x<3.8), Li x V 3 S 5 (0<x<1.8), Li x Ta 2 S 2 (0<x<l), Li x FeS (0<x<l), Li x FeS 2 (0<x<l), Li x NbS 2 (0<x<2.4), Li x MoS 2 (0<x<3), Li x TiS 2 (0<x<2), Li x ZrS 2 (0<x<2), Li χ NbSe 2 (0<x 3), Li χ VSe 2 (0<x<l), Li x NiPS 2 (0<x 1.5), Li x FePS 2 (0<x<1.5). If the layer B is an anode layer, it comprises a customary electron- conducting electrochemically active compound known from the prior art 5 (anode compound) which is able to take up lithium ions on charging; particular examples which may be mentioned are: lithium, lithium-containing metal alloys, micronized carbon black, natural and synthetic graphite, synthetic graphitized carbon powder and carbon fibers, oxides such as titanium oxide, zinc oxide, tin oxide, molybdenum oxide, o tungsten oxide, carbonates such as titanium carbonate, molybdenum carbonate and zinc carbonate. When the layer B is used as anode layer, it further comprises up to 20% by weight, based on the total weight of materials present in it (polymeric binder plus anode compound), of conductive black and, if desired, the abovementioned customary additives. When the layer B is used as cathode or for producing a cathode, it further comprises, based on the total weight of the materials present in it (polymeric binder plus cathode compound), from 0.1 to 20% by weight of conductive black. Bonding layer C As bonding layer C, it is possible in principle to use all materials which are able to join the first layer or layers, as defined above, and the second layer or layers, as defined above, to one another. The bonding layer is, in particular if the layers in question are joined to one another by hot lamination, generally a material which has a melting point which is lower, preferably from 20 to 50°C lower, than those of the first layer or layers or the second layer or layers or the first layer or layers and the second layer or layers. The melting point of these materials is generally from 25 to 250°C, preferably from 50 to 200 °C and in particular from 70 to 180°C. The bonding layer can also comprise a solid III. The amounts of the solid correspond essentially to the amounts specified for the layers A and B, in each case based on the material forming the bonding layer. As such materials forming the bonding layer, it is possible to use all materials customarily used as adhesives. Of course, it has to be possible to apply these materials to the layers A and/or B by customary methods of layer formation, for example printing on, casting on, spraying on, extruding, doctor blade coating, etc. Preference is given to using polymeric compounds as materials forming the bonding layer. Mention may here be made of: melt adhesives such as those based on ethylene-vinyl acetate copolymers which are generally additionally mixed with resins and/or waxes or paraffins so as to vary their melt flow index, those based on low molecular weight (co)polyethylene, atactic (co)polypropylene, ethylene-acrylic ester copolymers and styrene-butadiene and styrene-isoprene block copolymers, polyisobutylene and also poly(meth)acrylates and polyesters such as polyethylene terephthalate which can likewise in each case be mixed with plasticizers, in particular those mentioned herein, in order to vary their melt flow index; adhesive plastisols which are essentially mixed from a dispersion of finely divided polyvinyl chloride in plasticizers and low molecular weight materials which are reactive under the action of heat and act as bonding agents, e.g. epoxy resin compounds, phenolic resins, etc; heat-sealing adhesives such as those based on copolymers of vinyl chloride or vinylidene chloride, copolymers of vinyl acetate, polymethacrylic esters, polyurethanes and polyesters which can in turn likewise be mixed with other polymers or resins; contact adhesives such as those based on natural rubber, synthetic rubber in admixture with resins and solutions of high molecular weight polyurethane elastomers, where the rubber components used are mostly polychloroprene, nitrile or SBR rubbers and the resins used are mainly phenolic resins, rosins and also hydrocarbon resins; pressure sensitive adhesives such as those based on synthetic and natural rubbers, poly(meth)acrylic esters, polyvinyl ethers and polyisobutylene, in each case again in combination with modified natural resins, phenol- formaldehyde resins or hydrocarbon resins; pressure sensitive dispersion adhesives such as those based on poly(meth)acrylic esters; cold-curing, warm-curing (at from about 80 to about 100°C) and hot-curing (at from about 100 to about 250 °C) reaction adhesives such as one- component or two-component polymerization adhesives, where the polymers used for the two-component polymerization adhesives are, in particular, synthetic rubbers such as polychloroprene, styrene-butadiene rubber, butyl rubber, polystyrene, polymethacrylates with accelerators such as those based on amines and, for example, benzoyl peroxide as hardener, and examples of one-component polymerization adhesives are those based on cyanoacrylate; epoxy adhesives such as those based on condensation products of epichlorohydrin and polyhydric phenols such as bisphenol A; aminoplastics; phenolic resin adhesives; reactive polyurethane adhesives; polymethylol compounds; silicone adhesives; and polyimides and polyimidazoles such as polyaminamide and polybenzimidazole. Specific examples are: polyethylene oxide; polyvinyl ethers such as poly(vinyl methyl ether), poly(vinyl ethyl ether), poly(vinyl propyl ether), poly(vinyl butyl ether), poly (vinyl isobutyl ether); (co)polyacrylates and (co)polymethacrylates, with preference being given to those having relatively long alkyl chains, e.g. polybutyl (meth)acrylate or polyhexyl (meth)acrylate; polyvinylpyrrolidone; polyurethanes, where the abovementioned polyurethanes can likewise be used; wax-like (co)polyolefins such as polyethylene, polypropylene and polyisoprene waxes; rubber-like materials; polyisobutylene; and also mixtures of two or more thereof. Further details regarding the materials which can be used according to the present invention in the bonding layer may be found in an article entitled "Kleben und Klebestoffe" (Chemie in unserer Zeit, number 4 (1980), and also Ullmann, Encyklopadie der technischen Chemie, 4th edition (1977), volume 14, pp. 227-268 and also the literature cited therein, whose contents relating to materials having adhesive properties are incorporated by reference into the present application. The layers A and/or B and/or C can further comprise a plasticizer. Plasticizers which can be used are aprotic solvents, preferably those which solvate Li ions, for example dimethyl carbonate, diethyl carbonate, dipropyl carbonate, diisopropyl carbonate, dibutyl carbonate, ethylene carbonate, propylene carbonate; oligoalkylene oxides such as dibutyl ether, di-tert-butyl ether, dipentyl ether, dihexyl ether, diheptyl ether, dioctyl ether, dinonyl ether, didecyl ether, didodecyl ether, ethylene glycol dimethyl ether, ethylene glycol diethyl ether, l-tert-butoxy-2-methoxyethane, l-tert-butoxy-2- ethoxyethane, 1,2-dimethoxypropane, 2-methoxyethyl ether, 2-ethoxyethyl ether, diethylene glycol dibutyl ether, dimethylene glycol tert-butyl methyl ether, triethylene glycol dimethyl ether, tetraethylene glycol dimethyl ether, 7-butyrolactone, dimethylformamide; hydrocarbons of the formula C n H 2n+2 where 7 < n < 50; organic phosphorus compounds, in particular phosphates and phosphonates such as trimethyl phosphate, triethyl phosphate, tripropyl phosphate, tributyl phosphate, triisobutyl phosphate, tripentyl phosphate, trihexyl phosphate, trioctyl phosphate, tris(2-ethylhexyl) phosphate, tridecyl phosphate, diethyl n-butyl phosphate, tris(butoxyethyl) phosphate, tris(2-methoxyethyl) phosphate, tris(tetrahydrofuryl) phosphate, tris(lH, lH,5H- octafluoropentyl) phosphate, tris(lH,lH-trifluoroethyl) phosphate, tris(2- (diethylamino)ethyl) phosphate, diethyl ethylphosphonate, dipropyl propylphosphonate, dibutyl butylphosphonate, dihexyl hexylphosphonate, dioctyl octylphosphonate, ethyl dimethyl phosphonoacetate, methyl diethyl phosphonoacetate, triethyl phosphonoacetate, dimethyl (2-oxo- propyl)phosphonate, diethyl (2-oxopropyl)phosphonate, dipropyl (2-oxopropyl)phosphonate, ethyl diethoxyphosphinylformate, trimethyl phosphonoacetate, triethyl phosphonoacetate, tripropyl phosphonoacetate, tributyl phosphonoacetate; organic sulfur compounds such as sulfates, sulfonates, sulfoxides, sulfones and sulfites, e.g. dimethyl sulfite, diethyl sulfite, glycol sulfite, dimethyl sulfone, diethyl sulfone, diethylpropyl sulfone, dibutyl sulfone, tetramethylene sulfone, methylsulfolane, dimethyl sulfoxide, diethyl sulfoxide, dipropyl sulfoxide, dibutyl sulfoxide, tetramethylene sulfoxide, ethyl methanesulfonate, 1,4-butanediol bis(methanesulfonate), diethyl sulfate, dipropyl sulfate, dibutyl sulfate, dihexyl sulfate, dioctyl sulfate, S0 2 CIF; nitriles such as acrylonitrile; dispersants, in particular those having a surfactant structure; and also their mixtures. Furthermore, at least one ester of the formulae (El) to (E5), as shown below, can be used as plasticizer: ORl B OR2 OR3 (E1 ) ORl O OR2 (E2) ORl o - OR2 OR3 (E3) ORl OR2 (E ) R 4 O OR 1 \ / Si R 3 0 OR 2 (E5) where R 1 , R 2 , R 3 , R 4 are identical or different and are each, independently of one another, a linear or branched C r C 4 -alkyl group, (-CH 2 -CH 2 -0) n -CH 3 where n = 1 to 3, a C 3 -C 6 -cycloalkyl group, an aromatic hydrocarbon group which may in turn be substituted, with the proviso that at least one of the groups R 1 , R 2 , R 3 or R 4 is (-CH 2 -CH 2 -0) n -CH 3 where n = 1 to 3. Among the abovementioned esters of the formulae (El) to (E5), preference is given to using the phosphoric esters of the formula (E3). Examples of the groups R 1 , R 2 and, if present, R 3 and/or R 4 are the methyl, ethyl, n- and iso-propyl, n- and tert-butyl, cyclopentyl, cyclohexyl and benzyl groups, and also (-CH 2 -CH 2 -0) n -CH 3 where n = 1 to 3; however, as already mentioned above, it has to be ensured that at least one of the groups R 1 , R 2 , R 3 or R 4 is (CH 2 -CH 2 -O) n -CH 3 where n = 1 to 3, preferably 1 or 2. Further preference is given to using esters of the formulae (El) to (E5) in which R 1 , R 2 and, if present, R 3 and/or R 4 are identical and are -CH 2 - CH 2 O-CH 3 or (-CH 2 -CH 2 -O) 2 -CH 3 , with preference again being given to the corresponding phosphoric esters. Examples of particularly preferred compounds are the compounds of the formulae (El a) to (E5a): B ( OCH j CH j OCH^ (Eia) O = C ( OCH j CH j OOy j (E 2a) O = P( — O — CH j — CH j — 0 — 013 )3 (E3a) and o \ S ( OCH j CH j OCH^ <E4a) Si(-O-CH 2 -CH 2 -OCH 3 ) 4 (E5a) The esters used herein are, in terms of their properties, extraordinarily well suited as plasticizers for the layers in question and generally have a viscosity at room temperature of ≤ lOmPas, preferably < 5 mPas and in particular < 3 mPas. They generally have boiling points of about 200 °C or above, preferably about 250 °C or above and in particular about 300 °C or above, in each case measured at atmospheric pressure, and have a sufficiently low vapour pressure of from about 10 "5 to about 10° mbar at the temperatures occurring during their use, viz. from about -50 °C to about 150° C. As a result of their boiling points, they can be distilled and can thus be produced in high purity. Furthermore, these esters are liquid over a wide temperature range at atmospheric pressure, and are generally still liquid down to a temperature of about -30° C, preferably down to about -40°C. The esters described here can be used as plasticizers and as solvents in electrolyte systems for Li ion accummulators at at least about 80°C, preferably at least about 120°C, more preferably at least about 150°C. Of course, the esters used according to the invention can also be employed as a mixture with the previously mentioned plasticizers. Preference is given to combinations which have a sufficiently low viscosity, are able to strongly solvate the ions of the conducting salts, are liquid over a wide temperature range and are sufficiently electrochemically and chemically stable and are also resistant to hydrolysis. The esters used according to the present invention are prepared by conventional methods, as are described, for example, in K. Mura Kami in Chem. High Polymers (Japan), 7 (1950), pp. 188-193 and in H. Steinberg Organoboron Chemistry, Chapter 5, J. Wiley & Sons, N.Y. 1964. In these preparations, the acids, acid anhydrides or chlorides such as boric acid, C(0)C1 2 , POCl 3 , SO 2 Cl 2 and SiCl 4 are used as starting materials and are reacted in a known manner with the appropriate monohydric or polyhydric alcohols or etherols. The plasticizer content of the respective layer is, based on the mix present therein or the material making up the layer (polymeric binder plus cathode or anode material), from 0 to 200% by weight, preferably from 0 to 100% by weight and more preferably from 0 to 70% by weight. The starting materials used for the respective layers can be dissolved or dispersed in an inorganic or preferably organic liquid diluent, where the resulting solution should have a viscosity of preferably from 100 to 50,000 mPas, and subsequently applied in a known manner, for example by spray coating, casting, dipping, spin coating, roller coating or latterpress, gravure, planographic or screen printing or by extrusion, if desired to a support material, i.e. shaped to form a film-like structure. Further processing can be carried out in a customary way, e.g. by removing the diluent and curing the materials. Suitable organic diluents are aliphatic ethers, in particular tetrahydrofuran and dioxane, hydrocarbons, in particular hydrocarbon mixtures such as petroleum spirit, toluene and xylene, aliphatic esters, in particular ethyl acetate and butyl acetate, and ketones, in particular acetone, ethyl methyl ketone and cyclohexanone. It is also possible to use combinations of such diluents. Suitable support materials are the materials customarily used for electrodes, preferably metals such as aluminum and copper. It is also possible to use coated glass substrates, in particular ITO-coated glass substrates or temporary intermediate supports such as films, in particular polyester films such as polyethylene terephthalate films. Such films can advantageously be provided with a release layer, preferably of polysiloxanes. Likewise, the production of the individual films which then form the layers within the composite of the present invention can be carried out thermoplastically, for example by injection molding, melt casting, pressing, kneading or extrusion, if desired with a subsequent calendering step. After film formation, volatile components such as solvents or plasticizers can be removed. If crosslinking of the layers is desired, this can be carried out in a manner known per se, for example by irradiation with ionic or ionizing radiation, an electron beam, preferably at an acceleration voltage of from 20 to 2000 kV and a radiation dose of from 5 to 50 Mrad, UV or visible light, where, in a customary manner, an initiator such as benzil dimethyl ketal or 1,3,5-trimethylbenzoyl-triphenylphosphine oxide can be advantageously added in amounts of, in particular, at most 1 % by weight based on the constituents to be crosslinked in the starting materials and the crosslinking can advantageously be carried out over a period of, in general, from 0.5 to 15 minutes, advantageously under inert gas such as nitrogen or argon; by thermal free-radical polymerization, preferably at above 60°C, where an initiator such as azobisisobutyronitrile can advantageously be added in amounts of, in general, at most 5 % by weight, preferably from 0.05 to 1 % by weight, based on the constituents to be crosslinked in the starting materials; by electrochemically induced polymerization; or by ionic polymerization, for example by acid-catalyzed cationic polymerization, where suitable catalysts are, first and foremost, acids, preferably Lewis acids such as BF 3 or, in particular, LiBF 4 or LiPF 6 . Catalysts containing lithium ions, for example LiBF 4 or LiPF 6 , can advantageously remain in the solid electrolyte or separator as conducting salt. The layers described herein can also comprise a dissociable compound containing lithium cations, viz. a conducting salt, and, if desired, further additives such as, in particular, organic solvents, viz. an electrolyte. Some or all of these materials can be added to the mixture during the production of the layer or can be introduced into the layer after production of the latter. Conducting salts which can be used are the generally known conducting salts which are described, for example, in EP-A 0 096 629. According to the present invention, the conducting salt used is preferably LiPF 6 , LiBF 4 , LiClO 4 , LiAsF 6 , LiCF 3 S0 3 , LiC(CF 3 S0 2 ) 3 , LiN(CF 3 SO 2 ) 2 , LiN(S0 2 C n F 2n+ 1 ) 2 , LiC[(C n F 2n+ 1 )S0 2 ] 3 , Li(C n F 2n+ 1 )S0 3 , where n is in each case from 2 to 20, LiN(S0 2 F) 2 , LiAlCl 4 , LiSiF 6 , LiSbF 6 or a mixture of two or more thereof, with particular preference being given to using LiBF 4 or LiPF 6 as conducting salt. These conducting salts are used in amounts of from 0.1 to 50% by weight, preferably from 0.1 to 20% by weight, in particular from 1 to 10% by weight, in each case based on the material forming the respective layer. The films/layers forming the composite of the present invention generally have a thickness of from 5 to 500 μm, preferably from 10 to 500 μm, more preferably from 10 to 200 μm. The composite, preferably in the form of a film, generally has a total thickness of from 15 to 1500 μm, in particular a total thickness of from 50 to 500 μm. Furthermore, the present invention also provides a process for producing a composite, which comprises joining the first layer or layers A and the second layer or layers B and, if present, the bonding layer or layers to one another by lamination under the action of heat or pressure or heat and pressure, preferably by hot lamination. It should be ensured that, depending on the material used for the bonding layer, joining can always be carried out at room temperature or at temperatures up to 50 °C or by hot lamination. In the hot or cold lamination, all customary techniques such as roller melt methods, simple pressing and extrusion lamination can be employed. In the case of hot lamination, the temperatures used are generally from about 50°C to about 250°C, preferably from about 70°C to about 200°C and more preferably from about 100°C to about 180°C. A process is also provided for producing a composite, which comprises subjecting the first layer or layers or the second layer or layers or the first layer or layers and the second layer or layers to a corona treatment and subsequently joining the first corona-treated layer or layers to the second corona-treated or untreated layer or layers, preferably by hot lamination. Corona treatment is a method widely used in surface treatment for roughening/functionalizing surfaces. In this method, the roughening/functionalization is achieved by electrical charging of the surfaces. A generator produces an AC voltage of from about 10 to about 20 KV at a frequency of from about 20 to about 40 KHz and the generator energy is discharged via an electrode system onto the surface of the substrate to be treated, here the layer or layers as defined above, resulting in functionalization/roughening of the treated surface of the layer. According to the present invention, it is preferred for both layers to be corona-treated on the surfaces via which they are to be joined. Further details regarding the equipment necessary for corona treatment and the procedure for carrying out such treatment may be found in articles in Papier + Kunststoffverarbeitung, number 8 (1980), entitled "Flexible Anpassung der effektiven Kontaktflache" and Papier + Kunststoffverarbeitung, number 7 (1981), entitled "Ober- flachenbehandlungsmethoden zur Haftverbesserung" and the literature cited therein. The present invention further provides a process for producing a composite, which comprises applying at least one bonding layer to the first layer or layers, the second layer or layers or the first layer or layers and the second layer or layers and subsequently joining the first layer or layers to the second layer or layers via the bonding layer or layers, preferably by hot lamination. Furthermore, the present invention provides for the use of a composite, as defined above, for producing an electrochemical cell, in a sensor, an electrochromic window, a display, a capacitor or an ion-conducting film. It additionally provides an electrochemical cell comprising a composite of the present invention or a combination of two or more thereof. Suitable organic electrolytes for this purpose are the compounds discussed above under "plasticizers", with preference being given to using the customary organic electrolytes, preferably esters such as ethylene carbonate, propylene carbonate, dimethyl carbonate and diethyl carbonate or mixtures of such compounds. As can be seen from the above, it is thus readily possible to produce a composite composed of a first electrode layer (e.g. cathode)/if desired, a bonding layer/separator layer/second electrode layer (e.g. anode). Of course, the bonding layer can here also assume the function of a separator, so that the latter can be omitted. The procedure is, for example, as follows: An anode material, e.g. graphite, conductive black and PVDF copolymer are first mixed with one another and the resulting mixture is cast onto a Cu foil and subsequently dried (layer 1). Subsequently, a cathode material, e.g. LiMn 2 O 4 or LiCoO 2 , conductive black and PVDF copolymer are mixed with one another and cast onto an aluminum foil and dried (layer 2). Bringing together the two above-described layers and a separator layer plus, if desired, at least one bonding layer by hot lamination gives a composite which can be used, in combination with any solid and/or liquid electrolyte, as an electrochemical cell. The filling of such composites with an electrolyte and conducting salt can be carried out either before or preferably after bringing together the layers, if desired after provision of suitable collector electrodes, e.g. a metal foil, and even after introduction of the composite into a battery housing. The particular microporous structure of the layers when using the mixture of the present invention, in particular as a result of the presence of the above- defined solid in the respective layers, makes it possible for the electrolyte and the conducting salt to be taken up and the air in the pores to be displaced. Filling can be carried out at from 0°C to about 100°C, depending on the electrolyte used. The electrochemical cells of the present invention can be used, in particular, as automobile batteries, instrument batteries, planar batteries or polymer batteries. EXAMPLES Production of an anode foil 400 g of MCMB (Osaka Gas), 35 g of Kynar ® 2801 (Elf Atochem), 35.6 g of ethylene carbonate and 35.6 g of dimethyl carbonate were added to 460 g of THF. This mixture was milled for a few days and subsequently applied to a copper foil which had previously been painted with an anchor coat. After drying, this foil was used as anode foil for the following examples. Example 1 75 g of a wollastonite hydrophobicized with epoxysilane (Tremin ® 800 EST, from Quarzwerke Frechen) having a particle size of 3 μm was dispersed in 300 g of toluene using a high-speed stirrer. Subsequently, 12.5 g of a polyethylene oxide having a mean molecular weight of M w = 2,000,000 (Polyol , from Union Carbide), 12.5 g of the methacrylic diester of a propylene oxide-ethylene oxide block copolymer (Pluriol PE 6000 from BASF AG) and 0.02 g of a UV photoinitiator (Lucirin ® BDK, from BASF AG) were added to the mixture. The mixture was then applied at 60°C to a silicone-treated polyethylene terephthalate film by means of a doctor blade having a casting slit of 300 μm, the toluene was removed over a period of 5 minutes and peeling off the dried coating gave a film having a thickness of about 30 μm (separator film). Example 2 ® The anode foil was powdered with Kynar 2811 (copolymer of vinylidene fluoride and hexafluoropropene, from Elf Atochem) and subsequently, at 160°C, intimately joined to the separator film using a model IL12HR laminator from Ibico. Example 3 The separator film was powdered on one side with Kynar 2811. The powdered side was laid on the anode foil. The two sheets were subsequently intimately joined to one another at 160°C using the laminator described in Example 2. Example 4 An aqueous polyethylene dispersion (Polygen WI1 , solids content 35% , from BASF) was applied by means of a doctor blade to an untreated polyethylene terephthalate film. The polyethylene layer applied in this way had a thickness of 2 μm. Subsequently, the dispersion described in Example 1 was cast onto the PET film which had been pretreated in this way. After drying, the separator film formed was detached from the PET film. The polyethylene-coated side of the separator was laid on the anode foil. The two sheets were subsequently intimately joined to one another at 160°C using the laminator. Example 5 The procedure of Example 4 was repeated, but 5 % of Aerosil R812 (Degussa), based on the dispersion, were added to the polyethylene dispersion. Example 6 The procedure of Example 4 was repeated, but 5 % of titanium dioxide T805 (Degussa), based on the dispersion, were added to the polyethylene dispersion. Example 7 ® The procedure of Example 4 was repeated, but 5 % of wollastonite Tremin 939 (Quarzwerke), based on the dispersion, were added to the polyethylene dispersion. Example 8 A solution of polyethylene oxide in THF was applied by means of a doctor blade to a silicone-treated polyethylene terephthalate film. The polyethylene oxide layer applied in this way had a thickness of 2 μm. Subsequently, the dispersion described in Example 1 was cast onto the PET film which had been pretreated in this way. After drying, the separator film was detached from the PET film. The polyethylene oxide-coated side of the separator was laid on the anode foil. The two sheets were subsequently intimately joined to one another at 160°C using the laminator described in Example 2. Example 9 The procedure of Example 8 was repeated, but 5 % of Aerosil R812 (Degussa), based on the solution, were added to the polyethylene oxide solution. Example 10 The procedure of Example 8 was repeated, but 5 % of titanium dioxide T805 (Degussa), based on the solution, were added to the polyethylene oxide solution. Example 11 The procedure of Example 8 was repeated, but 5 % of wollastonite Tremin 939 (Quarzwerke), based on the solution, were added to the polyethylene oxide solution. Example 12 The procedure of Example 8 was repeated, but 3% of propylene carbonate, based on the solution, were added to the polyethylene oxide solution. Example 13 The procedure of Example 8 was repeated, but 3 % of tris(2-ethylhexyl) phosphate, based on the solution, were added to the polyethylene oxide solution. Example 14 The procedure of Example 8 was repeated, but 5 % of wollastonite Tremin 939 (Quarzwerke) and 3 % of tris(2-ethylhexyl) phosphate, based on the solution, were added to the polyethylene oxide solution. Example 15 A solution of Acronal 102 (BASF, polybutyl aery late solution in toluene) was applied by means of a doctor blade to a silicone-treated polyethylene terephthalate film. The polybutyl acrylate layer applied in this way had a thickness of 2 μm. Subsequently, the dispersion described in Example 1 was cast onto the PET film which had been pretreated in this way. After drying, the separator film was detached from the PET film. The polybutyl aery late-coated side of the separator was laid on the anode foil. The two sheets were subsequently intimately joined to one another at 160°C using the laminator. Example 16 ® The procedure of Example 14 was repeated, but 5 % of Aerosil R812 (Degussa), based on the solution, were added to the polybutyl acrylate solution. Example 17 The procedure of Example 14 was repeated, but 5 % of titanium dioxide T805 (Degussa), based on the solution, were added to the polybutyl acrylate solution. Example 18 ® The procedure of Example 14 was repeated, but 5 % of wollastonite Tremin 939 (Quarzwerke), based on the solution, were added to the polybutyl acrylate solution. Example 19 A solution of Oppanol B200 (BASF, polyisobutylene dissolved in n-hexane) was applied by means of a doctor blade to a silicone-treated polyethylene terephthalate film. The polyisobutylene layer applied in this way had a thickness of 3 μm. Subsequently, the dispersion described in Example 1 was cast onto the PET film which had been pretreated in this way. After drying, the separator film was detached from the PET film. The polyisobutylene-coated side of the separator was laid on the anode foil. The two sheets were subsequently intimately joined to one another at 160°C using the laminator. Example 20 _ ® The procedure of Example 18 was repeated, but 5 % of Aerosil R812 (Degussa), based on the solution, were added to the polyisobutylene solution. Example 21 The procedure of Example 18 was repeated, but 5 % of titanium dioxide T805 (Degussa), based on the solution, were added to the polyisobutylene solution. Example 22 The procedure of Example 18 was repeated, but 5 % of wollastonite Tremin 939 (Quarzwerke), based on the solution, were added to the polyisobutylene solution. The qualitative results of testing the composites as described in Examples 1 to 22 are shown in the following table. unsatisfactory acceptable 0 satisfactory + good + + excellent

Claims: We claim: 1. A composite comprising Aa) at least one first layer which comprises a mixture la, comprising a mix Ila consisting of a) from 1 to 95 % by weight of a solid III, preferably a basic solid III, having a primary particle size of from 5 nm to 20 μm and b) from 5 to 99% by weight of a polymeric composition IV obtainable by polymerization of bl) from 5 to 100% by weight, based on the composition IV, of a condensation product V of ) at least one compound VI which is able to react with a carboxylic acid or a sulfonic acid or a derivative or a mixture of two or more thereof, and β) at least 1 mol per mol of the compound VI of a carboxylic acid or sulfonic acid VII which contains at least one free-radically polymerizable functional group, or a derivative thereof or a mixture of two or more thereof, and b2) from 0 to 95 % by weight, based on the composition IV, of a further compound VIII having a mean molecular weight (number average) of at least 5000 and polyether segments in the main chain or a side chain, where the proportion by weight of the mix Ila in the mixture la is from 1 to 100% by weight, and the layer is free of an electron-conducting, electrochemically active compound, and B) at least one second layer which comprises an electron- conducting, electrochemically active compound, wherein the first layer or layers and the second layer or layers are joined to one another by one of the two methods VI or V2: VI) Lamination of the first layer or layers with the second layer or layers under the action of heat or pressure or under the action of heat and pressure, or V2) Corona treatment of the first layer or layers, the second layer or layers or the first layer or layers and the second layer or layers and subsequent bringing together of the corona-treated first layer or layers with the corona-treated or untreated second layer or layers. 2. A composite comprising Ab) at least one first layer which comprises a mixture lb comprising a mix lib consisting of a) from 1 to 95 % by weight of a solid III, preferably a basic solid, having a primary particle size of from 5 nm to 20 μm and b) from 5 to 99% by weight of a polymer IX obtainable by polymerization of bl) from 5 to 75 % by weight, based on the polymer IX, of a free-radically polymerizable compound X which is different from the carboxylic acid or the sulfonic acid VII or a derivative thereof, or a mixture of two or more thereof, and b2) from 25 to 95 % by weight, based on the polymer IX, of a further compound VIII having a mean molecular weight (number average) of at least 5000 and polyether segments in the main chain or a side chain, where the proportion by weight of the mix lib in the mixture lb is from 1 to 100% by weight and the layer is free of an electron-conducting, electrochemically active compound, and B) at least one second layer which comprises an electron- conducting, electrochemically active compound, wherein the first layer or layers and the second layer or layers are joined to one another by one of the two methods VI or V2: VI) Lamination of the first layer or layers with the second layer or layers under the action of heat or pressure or under the action of heat and pressure, or V2) Corona treatment of the first layer or layers, the second layer or layers or the first layer or layers and the second layer or layers and subsequent bringing together of the corona-treated first layer or layers with the corona-treated or untreated second layer or layers. 3. A composite comprising at least one first layer Aa or at least one first layer Ab or at least one first layer Aa and at least one first layer Ab, at least one second layer B, each as defined in claim 1 or 2, and C) at least one bonding layer. 4. A composite as claimed in claim 3, wherein the bonding layer or layers C has/have a melting point which is lower than the melting point of the first layer or layers or the second layer or layers or the first and second layer or layers. 5. A composite as claimed in claim 3 or 4, wherein the bonding layer or layers C is/are a polyethylene oxide, a polyvinyl ether, a polyacrylate, a polymethacrylate, polyvinylpyrrolidone, a polyurethane, a wax-like (co)polyolefin, a rubber-like material, polyisobutylene or a mixture of two or more thereof. 6. A composite as claimed in any of claims 3 to 5, wherein the bonding layer or layers C comprise(s) a solid III, a plasticizer or a combination of two or more thereof. 7. A process for producing a composite as claimed in any of claims 1 to 6, which comprises joining the first layer or layers and the second layer or layers and, if present, the bonding layer or layers to one another by hot lamination. 8. A process for producing a composite as claimed in claim 1 or 2, which comprises subjecting the first layer or layers or the second layer or layers or the first layer or layers and the second layer or layers to a corona treatment and subsequently joining the first corona- treated layer or layers to the second corona-treated or untreated layer or layers. 9. A process for producing a composite as claimed in any of claims 3 to 6, which comprises applying at least one bonding layer to the first layer or layers, the second layer or layers or the first and second layer or layers and subsequently joining the first layer or layers to the second layer or layers via the bonding layer or layers. 10. The use of a composite as claimed in any of claims 1 to 6 for producing an electrochemical cell, in a sensor, an electrochromic window, a display, a capacitor or an ion-conducting film. 11. An electrochemical cell comprising a composite as claimed in any of claims 1 to 6 or a combination of two or more thereof. 12. The use of the electrochemical cell as claimed in claim 11 as an automobile battery, instrument battery, planar battery or polymer battery.

Inventors: BAUER STEPHAN, BRONSTERT BERND, MOEHWALD HELMUT, STEPHAN OSKAR, TUKAMOTO HISASHI, BAUER, STEPHAN, BRONSTERT, BERND, MOEHWALD, HELMUT, STEPHAN, OSKAR, TUKAMOTO, HISASHI
Applicants: BASF AG, BAUER STEPHAN, BRONSTERT BERND, GS JAPAN STORAGE, MOEHWALD HELMUT, STEPHAN OSKAR, TUKAMOTO HISASHI, BASF AKTIENGESELLSCHAFT, BAUER, STEPHAN, BRONSTERT, BERND, MOEHWALD, HELMUT, STEPHAN, OSKAR, TUKAMOTO, HISASHI
Application year: 1998
Main classification: H01M
IPC codes: C09K9, H01B5, H01G9, H01M2, H01M4, H01M6, H01M10