POLYESTER CONTAINING BENZYLIDENE HAVING REDUCED FLUORESCENCE

Abstract: A polymer composition having naphthalenedicarboxylic residue includes a fluorescence quenching benzylidene compound capable of absorbing ultraviolet light radiation. In a preferred embodiment, the composition includes at least a 0.1 mole percent of naphthalene-2,6-dicarboxylate and about 0.01 mole percent to about 5 mole percent of a benzylidene compound having structure (I), wherein R is selected from the group consisting of hydrogen, C1-C8 alkyl, substituted C1-C8 alkyl, C3-C8 alkenyl, C3-C8 alkynyl, C3-C8 cycloalkyl, C3-C8 cycloalkenyl and -R2-X, wherein R2 is selected from the group consisting of C1-C8 alkylene, C2-C8 alkylene-O-C2-C8 alkylene, C2-C8 alkylene-S-C1-C8 alkylene, C2-C8 alkylene, C2-C8 alkylene-S-C2-C8 alkylene, C2-C8 alkylene-N(SO2 C1-C8 alkyl)-C2-C8 alkylene and X is selected from the group consisting of hydroxy, carboxy, carboalkoxy and acyloxy; R1 is hydrogen or has 1-3 groups independently selected from the group consisting of hydroxy, C1-C8 alkyl, C1-C8 alkoxy and halogen; Y is selected from the group consisting of carbalkoxy, cyano, carbamoyl, substituted carbamoyl, aryl, aroyl, C1-C8 alkylsulfonyl and arylsulfonyl.

Description: POLYESTER CONTAINING BENZYLIDENE HAVING REDUCED FLUORESCENCE RELATED APPLICATION This application claims the benefit of the United States provisional application having U S Seπal No 60/059,416 filed June 18, 1997, the entire disclosure being incorporated herein by reference BACKGROUND OF THE INVENTION This invention relates to a polymer composition having reduced fluorescence, and particularly to a polymer blend composition containing naphthalenedicarboxyhc acid residues and having incorporated therein benzylidene compounds The invention further relates to a method for prepaπng the blend It is well known that dicarboxyhc acids and dicarboxyhc esters can be reacted with glycols to prepare polyesters Polyesters are used in the fabπcation of vaπous articles for household, commercial or industrial use Such uses included appliance parts, containers, and auto parts A major drawback of many polyesters is their inherent bluish fluorescence For example, articles prepared with the polyester poly(ethylene-2,6-naphthalene dicarboxylate), also known in the art as "PEN", have a hazy and bluish appearance This phenomenon is of concern especially in packaging of products when their appearance is to be as close to their natural state as desired For example, in the packaging of foods and beverages, if the food or beverages were inside a PEN container they may appear unnatural Typically, poly(ethylene 2,6-naphthalene dicarboxylate) contains repeat units from a dicarboxyhc acid and a diol The poly(ethylene 2,6-naphthalene dicarboxylate) can be prepared by conventional polycondensation procedures well-known m the art Such procedures can include a combination of melt phase and solid state polymenzation Melt phase descπbes the molten state of PEN during the initial polymenzation process The initial polymenzation process includes direct condensation of the naphthalene-2,6-dιcarboxylιc acid with the dιol(s) or by ester interchange using naphthalene-2,6-dιcarboxyhc ester The melt phase is concluded by extruding the PEN polymer into strands and pelletizing Solid state polymenzation involves heating PEN pellets to a temperature in excess of 200°C, but well below the crystalline melt point, either in the presence of an inert gas stream or in a vacuum to remove a diol Fluorescence is a type of luminescence in which an atom or molecule emits radiation, i.e , a photon, in passing from a higher to a lower electron state. The term is restπcted to phenomena m which the time interval between absorption and emission energy is extremely short (10 10 to 10 " * second). Quenching fluorescence eliminates or reduces the ability for photon emission by providing an alternative pathway for the excited state energy such as vibromc or heat loss, or mtersystem crossing to the excited tnplet state. Methods to quench fluorescence m PEN have been disclosed by Chen Shangxian, et al. in an article entitled, "Fluorescence Spectra of Poly(Ethylene 2,6-Naphthalene Dicarboxylate)" which appeared in SCIENTIA SINICA, Vol. XXTV, No 5, May 1981, and by CAO Ti, et al. in an article entitled, "Intermolecular Excimer Interaction in Poly(Polytetramethylene Ether Glycol Aryl Dicarboxylate)" which appeared in ACTA CHIMICA SINICA, Vol. 42, No. 1, 1984 Both of the references disclose the use of o-chlorophenol to quench PEN fluorescence in a chloroform solution. Dissolving PEN in a chloroform solution to disperse the fluorescence quencher therein, however, is not practical since the PEN must have a low molecular weight to dissolve in the chloroform solution and only very dilute PEN solutions can be prepared Japanese Patent 08225672 discloses the use of coatings containing UV absorbers benzotnazoles, cyanoacrylates, benzophenones, and benzoxazinones to suppress the fluorescence of a molded product consisting mamly of polyalkylenenaphthalene-2,6-dιcarboxylate. A disadvantage of using a coating to reduce fluorescence of PEN is the additional processing steps required to apply the coating to the molded article. The cost of coating adds significantly to the cost of the article. European Patent 0711803 discloses mixing cyclic lmu o esters or quinoxahnes with PEN as a method of reducing fluorescence m the polyalkylenenaphthalene-2,6-dιcarboxylate. Blending the cyclic immo esters and qumoxalines with the polyalkylenenaphthalene-2,6-dιcarboxylates resulted m moderate changes m the relative fluorescence intensity (37% to 58%) which is not enough to significantly improve the appearance of containers made from polymer compositions containing naphthalenedicarboxyhc acid residues. European Patent 0711803 further discloses using UV absorbing coatings in combination with the above blends to reduce the relative fluorescence intensity to an adequate level. U S. Patents 4,617,374 and 4,707,537 disclose the use of vanous benzylidene compounds as UV screens for polyesters. These patents teach that incorporating the benzylidene compounds in various polyesters at a concentration of 1 to 5000 ppm with a maximum absorbance of 320 nm to about 380 nm is effective in screening UV light. The patents do not disclose the use of the benzylidene compounds in polymer compositions containing naphthalenedicarboxyhc acid residues Polymer compositions containing naphthalenedicarboxyhc acid residues such as poly(ethylene 2,6- naphthalenedicarboxylate) can absorb UV light up to 390 nm, thus, making UV absorbers ineffective as UV screens. U.S. Patents 4,617,374 and 4,707,537 are unclear as to the effect the benzylidene compounds would have on the fluorescence intensity of polymer compositions containing naphthalenedicarboxyhc acid residues. U S Patent 5,310,857 discloses reducing the fluorescence of a poly(ethylene 2,6- naphthalenedicarboxylate) polymer using from 0.1 to 5 mole percent of a copolymenzable aromatic ketone. The aromatic ketone has at least one acyl group directly attached to the aromatic ring U. S. Patent 5,352,761 discloses certain naphthalene derivatives having substituted aroyl groups which are useful in providing reduced fluorescence m polyesters such as PEN and are copolymenzable with other polyesters. U.S. Patent 5,391,701 discloses using difunctional halo-aromatic compounds copolymeπzed with PEN to reduce the polymer's fluorescence. U.S. Patents 5,391,702 and 5,391,330 disclose a process for prepaπng PEN or dimethyl 2,6-naphthalene dicarboxylate containing copolyesters/fluorescence quencher blends via melt blending. U.S. Patent 5,393,862 discloses using nonhalogenated copolymenzable aromatic compounds such as benzene, naphthalene and biphenyl having at least one acyl group directly attached to the aromatic nng to reduced the fluorescence in polymers of dimethyl 2,6-naphthalene dicarboxylate U.S. Patent 5,418,318 discloses the use of dimethyl 2,6-naphthalene dicarboxylate copolyesters or copolyamides having a copolymeπzed halo-aromatic compound and having reduced fluorescence. Accordingly, there is a need for poly(ethylene 2,6-naphthalene dicarboxylate) having a reduced fluorescence without deleteπously affecting the physical properties of the polymer. SUMMARY OF THE INVENTION Broadly, the present invention is for a polyalkylenenaphthalene-2,6-dιcarboxylate composition comprising residues of naphthalenedicarboxyhc acid, a diol or diamine and a benzylidene compound capable of absorbing ultraviolet light radiation. Desirably, the composition has a reduced fluorescence relative to a polyalkylene naphthalene-2,6- dicarboxylate composition without the benzylidene compound It is another aspect of the invention to provide a method for prepanng a polymer blend containing poly(ethylene 2,6-naphthalene dicarboxylate) having a reduced fluorescence. The method includes the step of prepanng a blend having residues of a dicarboxyhc acid component, a diol component and a fluorescence quenching compound selected from a benzylidene compound. It is an object of the invention to provide a polyalkylenenaphthalene-2,6-dιcarboxylate composition having a reduced fluorescence It is another object of the invention to provide a poly(ethylene 2,6-naphthalene dicarboxylate) composition having a reduced fluorescence that is satisfactory for manufacturing goods where heat resistance, high glass transition temperature and gas barner properties are desirable. It is another object of the invention to provide a method of making a compositional blend having a naphthalenedicarboxyhc acid containing polymer having reduced fluorescence These and other objects and advantages of the invention will become more fully appreciated by following the detailed descnption of the invention and the appended claims. DETAILED DESCRIPTION OF THE INVENTION The polymers of the present invention contain a polyester having naphthalenedicarboxyhc acid residues and a fluorescence quenching compound. The polymers contain repeat units from a dicarboxyhc acid, a diol or diamine, and a benzylidene compound. As used herein the fluorescence quenching compound is a benzylidene compound capable of absorbing ultraviolet light radiation. In a preferred embodiment, the polymer composition compnses repeat units from a dicarboxyhc acid component having at least 0 1 mole percent of 2,6-naphthalenedιcarboxyhc acid or 2,6- naphthalenedicarboxylate esters, a diol or diamine component, and from about 0 01 to about 5 mole percent, based on 100 mole percent dicarboxyhc acid and 100 mole percent diol, of a benzylidene compound and preferably, a copolymenzable benzylidene compound containing an acid, diacid, ester, diester, hydroxyl or diol functional moiety. More preferably, the polymer is a polyester containing repeat units from 0 1 to 100 mole percent of 2,6-naphthalenedιcarboxylιc acid or 2,6- naphthalenedicarboxylate ester, and 0 to 99 9 mole percent of terephthahc acid or dimethyl terephthalate, and at least 90 mole percent ethylene glycol The polyester dicarboxyhc acid component may optionally be modified with 0 1 mole percent to about 30 mole percent of a difunctional acid selected from aromatic dicarboxyhc acids desirably having 8 to 14 carbon atoms, aliphatic dicarboxyhc acids desirably having 4 to 12 carbon atoms, or cycloahphatic dicarboxyhc acids desirably having 8 to 12 carbon atoms As used herein the term "dicarboxyhc acid" includes the corresponding acid anhydndes, esters, and acid chlondes of the acids Nonhmiting examples of such dicarboxyhc acids to be included with 2,6- naphthalenedicarboxyhc acid, or 2,6-naphthalenedιcarboxylate ester either alone or in combination are phthahc acid, lsophthahc acid, terephthahc acid, cyclohexanedicarboxyhc acid, dιphenyl-4,4'- dicarboxyhc acid, succinic acid, glutaπc acid, adipic acid, fumaπc acid, azelaic acid, sebacic acid, 2J-naphthalenedιcarboxyhc acid, 1,4-cyclohexanedιcarboxyhc acid, resorcmoldiacetic acid, diglycohc acid, 4,4'-oxybιs(benzoιc) acid, biphenyldicarboxyhc acid, 1,12-dodecanedιcarboxyhc acid, 4,4'-sulfonyldιbenzoιc acid, 4,4'-methylenedιbenzoιc acid, trans-4,4'-stιlbenedιcarboxyhc acid, and the like Accordingly, the polyester may be prepared from one or more of the above dicarboxyhc acids, esters of the acids or combinations thereof Diols suitable for forming the poly(ethylene 2,6-naphthalene dicarboxylate) having a reduced fluorescence include cycloahphatic diols preferably having 6 to 20 atoms or aliphatic diols preferably having 2 to 20 carbon atoms. Nonhmiting examples of such diols include ethylene glycol, diethylene glycol, tnethylene glycol, 1,4-cyclohexanedιmethanol, propane- 1,3-dιol, butane- 1,4-dιol, pentane- 1,5-dιol, hexane-l,6-dιol, 2,2-dιmethyl-l,3-propanedιol, 1,10-decanedιol, 2,2,4,4-tetramethyl-l,3- cyclobutanediol, 3-methylpentanedιol-(2,4), 2-methylpentanedιol-( 1 ,4), 2,2,4-tnmethylpentane-dιol- (1,3), 2-ethylhexanedιol-(l,3), 2,2-dιethylpropane-dιol-(l ,3), hexanedιol-(l,3), 1,4-dι- (hydroxyethoxy)-benzene, 2,2-bιs-(4-hydroxycyclohexyl)-propane, 2,4-dιhydroxy-l,l,3,3- tetramethyl-cyclobutane. 2,2-bιs-(3-hydroxyethoxyphenyl)-pτopane, and 2,2-bιs-(4- hydroxypropoxypheny 1 )-propane . Naphthalenedicarboxyhc acid containing polyamides can be formed from adipic acid, isophthalic acid, terephthahc acid, 1,3- or 1,4-cyclohexanedιcarboxyhc acid, aliphatic diacids containing 6 to 12 carbon atoms, 1,6-hexanedιamιne, meta- or para-xylylenediamme, 1,3- or l,4-cyclohexane(bιs)methylamιne, aliphatic diammes with 4 to 12 carbon atoms, other polyamide forming diacids and diammes and mixtures thereof. The polyester may also contain small amounts of tnfunctional or tetrafunctional comonomers such as tπmelhtic anhydride, tnmethylolpropane, pyromellitic dianhydnde, pentaerythntol, and other polyester forming polyacids or polyols generally known m the art. The polymer may also contain polycarbonate repeat units formed form the reaction of a carbonic acid denvative with a diol such as bisphenol A. The polymer may be a blend of the above- described polyesters, polyamides, polycarbonates, or polyesteramides The polymer of the present invention further includes a fluorescence quenching compound compnsmg from about 0.01 to about 5 mole percent and preferably, from about 0.1 to about 2 mole percent of a benzylidene compound. Benzylidene compounds useful in the practice of the invention are disclosed m U.S. Patents 4,845,287, 4,826,903, 4J49J74, 4,749,773, 4,707,537, 4,617,374, 4,338,247, 5,057,594, 4,950,732 and 4,845,188, the entire disclosures of each being incorporated herein by reference. Preferably, the benzylidene compounds of this invention contain at least one polyester reactive group selected from carboxy, carbalkoxy, acyloxy and hydroxy and have the following structure. wherein R is selected from hydrogen, C r C g alkyl, substituted C,-C 8 alkyl, C 3 -C 8 alkenyl, C 3 -C 8 alkynyl, C 3 -C 8 cycloalkyl, C 3 -C 8 cycloalkenyl and -R 2 -X, wherem R 2 is selected C,-C 8 alkylene, C 2 - C g alkylene-O- C 2 -C 8 alkylene, C 2 -C 8 alkylene-S- C C s alkylene, C 2 -C 8 alkylene, C 2 -C 8 alkylene-S- C 2 -C 8 alkylene, C 2 -C 8 alkylene-N(S0 2 C,-C 8 alkyl)- C 2 -C 8 alkylene and X is selected from hydroxy, carboxy, carboalkoxy and acyloxy; R, is hydrogen or has 1-3 moieties independently selected from hydroxy, C,-C 8 alkyl, C,-C 8 alkoxy and halogen; Y is selected from carbalkoxy, cyano, carbamoyl, substituted carbamoyl, aryl, aroyl, C,-C 8 alkylsulfonyl and arylsulfonyl. As used herein, the term "C,-C 8 alkyl" refers to straight and branched hydrocarbon radicals containing one to eight carbon atoms The term "substituted C,-C 8 alkyl" refers to straight and branched chain hydrocarbon radicals containing one to eight carbon atoms and which are further substituted with a vanety of common groups such as those disclosed m the definition of R in U.S. Patent 4,617,374, column 12, line 49 to column 13, line 30, the disclosure being incorporated herein by reference The preferred substituents are C,-C 8 alkyl, C,-C 8 alkoxy, hydroxy, cyano, C 3 -C 8 cycloalkyl, acyloxy and halogen. The term "C,-C 8 alkoxy" is used to descπbe C,-C 8 alkyl groups attached to oxygen, wherein, the C,-C 8 alkyl portion is defined above. The term "C 3 -C 8 cycloalkenyl" is used to descnbe saturated cycloahphatic radicals which contain three to eight carbon atoms. The terms "C 3 -C 8 alkenyl" and "C 3 -C 8 alkynyl" are used to refer to unsaturated hydrocarbon radicals containing at least one carbon-carbon double bond and carbon-carbon tπple bond, respectively. The terms "C,-C 8 alkylene" and "C 2 -C 8 alkylene" are used to descnbe saturated divalent straight and branched chain hydrocarbon radicals and these substituted with at least one substituent selected from C r C g alkoxy, halogen, aryl, hydroxy and acyloxy. The terms "carbalkoxy" and "acyloxy" are used to descnbe the radicals -C0 2 R 3 and R^CO,-, respectively, wherein R 3 and R < are mdependently selected from C,-C 8 alkyl, substituted C,-C 8 alkyl, C 3 -C 8 cycloalkyl, C 3 -C 8 alkenyl, C 3 -C 8 alkynyl and aryl. The term "halogen" is used to refer to fluonne, chlonne, bromine and iodine. The terms "aryl" and "aroyl" are used to descnbe phenyl and naphthyl radicals optionally substituted with one or more groups selected from C,-C 8 alkyl, C,-C 8 alkoxy, hydroxy and halogen and these radicals attached to a carbonyl moiety, respectively. The terms "carbamoyl" and "substituted carbamoyl" are used to descnbe the radicals -C0NH 2 and -C0N(R 3 )R 4 , respectively, wherein R 3 and R, are as defined previously The polymer compositions containing naphthalenedicarboxyhc acid residues with the fluorescence quenching compound can be prepared by conventional polycondensation procedures well-known in the art which generally include a combination of melt phase and solid state polymenzation discussed herein. For example, dιmefhyl-2,6-naphthalenedιcarboxylate is ester interchanged with ethylene glycol at elevated temperatures in the presence of the copolymenzable benzylidene compound and a catalyst. In a preferred embodiment, the benzylidene compound is copolymenzed in the polymer backbone. Typical catalyst which may be used include titanium alkoxides, dibutyl tin dilaurate, combinations of zinc, manganese, or magnesium acetates or benzoates with antimony oxide or antimony triacetate. Optionally, the benzylidene compound, either with or without copolymenzable groups, can be added to the polyester by direct melt blending the polymer compositions containing naphthalenedicarboxyhc acid residues and the benzylidene compound. Although not preferred, a "master batch" of the polyester having the benzylidene compounds at much higher than desired concentrations can be melt blended with the polymer composition containing naphthalenedicarboxyhc acid residues to obtain the desired composition Although not wishing to be bound by any theory, it is believed that using more than 5 mole percent of the fluorescence quenching compound hinders the crystallization of the polyester and results in mfenor physical properties The inherent viscosity of the polymer compositions containing naphthalenedicarboxyhc acid residues should be 0.3 to 1.5 dL/g. However, inherent viscosities of from 0.4 to 1.1 are preferred, as measured at 25 C using 0.25 grams of polymer per 50 ml of a solvent consisting of 60% by weight pentafluorophenol and 40% by weight 1,3,5-tnchlorobenzene. The polymer compositions of the invention may be further melt blended with other polymers, and desirably, compatible polyesters. Compatible polyesters which may be blended with the polymer compositions of the invention are generally based on terephthahc acid, 1 ,4-cyclohexanedιcarboxylιc acid, isophthahc acid, naphthalenedicarboxyhc acid and the like, and one or more glycols containing 2 to about 12 carbon atoms. Preferred glycols include ethylene glycol, 1,4-butanedιol, 1,6- hexanediol, 1,4-cyclohexanedιmethanol, and 2,2-dιmethyl-l ,3-propanedιol Homo and copolyesters may be used. The copolyesters may contain up to about 50 mole % of modifying dibasic acids and/or glycols. Typical modifying dibasic acids include isophthahc, adipic, glutanc, azelaic, sebacic, and the like while modifying glycols will include those having 2 to 12 carbon atoms and may be aliphatic or alicychc in nature. Useful polyesters include PET, PET copolyester containing up to 20 mole % isophthahc acid, PET copolyester containing up to 70 mole % 1 ,4-cyclohexanedιmethanol, PET copolyester containing up to 37 mole % diethylene glycol, PET copolyester containing up to 50 mole % 1,4-butanedιol, poly( 1 ,4-butyleneterephthalate)(PBT), PBT copolyester containing up to 15 mole % ethylene glycol, poly(ethylene 1 ,4-cyclohexanedιcarboxylate), poly(l,4-cyclohexyldιmethylene terephthalate) (PCT), PCT copolyester containing up to 18 mole % ethylene glycol, PCT copolyester containing up to 40 mole percent isophthahc acid, polycarbonate and the like All of these polyesters are readily prepared by methods well known to those skilled in the art Blends of the polymer composition with other polyesters generally contain about 0 1 weight percent to about 99 9 weight percent of the naphthalene dicarboxylate polymer composition Such blends are readily prepared using conventional melt processing equipment such as a Brabender extruder, single-screw extruder, twin-screw extruder and the like The blends are generally processed at temperatures in the range of about 260°C to about 330°C. Properties of the blends may be altered significantly depending on the mixing temperature and mixing time Generally, processing times m the range of about 0 4 to about 5 minutes are useful to achieve the desired results The polymer compositions of the invention serve as excellent starting mateπals for the production of moldings of all types The polymer compositions containing naphthalenedicarboxyhc acid residues may also be blended with other polymers. Specific applications include food packaging such as bottles, trays, lids and films, medical parts, appliance parts, automotive parts, tool housings, recreational and utility parts. The molding compositions of the present invention are especially useful in applications that require transparent molded parts. Additionally, the polymers can be used to prepare extruded sheets for thermoforming applications. The polymers are readily extruded into films or processed into monolayer or multi layer food and beverage containers. Potential methods for producing containers mclude: (1) injection stretch blow molding usmg either one or two stage technology, (2) injection blow molding, (3) extrusion blow molding, (4) pipe extrusion, and (5) co- injection or co-extrusion where the polymers can serve as either the structural layer or barner layer depending upon end use requirements Fibers, melt-blown webs, extruded sheets, vacuum-drawn trays/parts, injection molded parts, and extrusion coated wires may also be made from these polymers Many other ingredients can be added to the compositions of the present invention to enhance the performance properties of the naphthalene dicarboxylate resin containing an ultraviolet absorber For example, surface lubncants, denesting agents, stabilizers, antioxidants, mold release agents, metal achvators, colorants such as black iron oxide and carbon black, nucleating agents, phosphate stabilizers, zeolites, fillers and the like can be included All of these additives and the use thereof are well known in the art Any of these can be used so long as they do not hinder the present invention from accomplishing its objects The present invention will be further illustrated by a consideration of the following examples, which are intended to be exemplary of the invention All parts and percentages in the examples are on a molar basis unless otherwise stated The matenals and testing procedures used for the results shown herein are as follows The fluorescence intensities, I and I 0 , of examples 1-4 and 7- 12 were measured on a LS-5B Luminescence Spectrometer using a Xenon Lamp as the light source The slit width was 10 for excitation and 20 for emission The emission spectra were measured from 360 nm to 700 nm at an excitation wavelength of 350 nm The fluorescence intensities, I and I 0 , of examples 5 and 6 were measured on a Perkin Elmer Luminescence Spectrometer LS50B with Front Surface Accessory The slit width was 5 for excitation and 4 for emission The emission spectra were measured from 360 nm to 650 nm with a excitation wavelength of 350 nm In Examples 1-6 amorphous 15 mil ( 015 of an inch) films were used to determine the specified matenal's fluorescence intensity In prepanng a film, the specified polymer was ground to a dimension of less than 3 millimeters, l e the matenal would pass through a 3 millimeter mesh screen Approximately, 13 grams of the ground polymer was melt pressed at 1000 psi between feme plates at a temperature of about 300 °C and for about two minutes The films were cooled using cold water Fluorescence measurements were taken as noted above The fluorescence intensities of examples 7-12 were measured on crystalline powders Sample preparation for determining fluorescence intensity involved grinding the polyester to a particle size of about 3-4 millimeters The samples were then micro pulvenzed in an analytical grinding mill and passed through a 120 mesh screen. Except for Example 7, the powders were dried for 24 hours at 140°C. Approximately 0.5 of a gram of the powder was packed into a sample holder and measurements were taken as noted above. Inherent viscosity (IhV) measurements were made at 25 °C. 0.25 grams of the sample mateπal were dissolved in 50 ml of a 60/40 (w/w) pentafluorophenol/l,3,5-tnchlorobenzene (PFP/TCB) solvent system. EXAMPLE 1 Poly(ethylene 2,6-naphthalenedιcarboxylate) was prepared by the following procedure. Dimethyl 2,6-naphthalenedιcarboxylate (0.25 mol, 61 g), ethylene glycol (0 5 mol, 31 g) and catalyst metals were placed in a 500 milhhter (mL) polymenzation reactor under a nitrogen atmosphere The mixture was stirred and heated to 200 °C. The temperature was maintained steady for 90 minutes The temperature was increased to 220°C and maintained steady for 80 minutes. The temperature was increased to 285 °C over a penod of about 20 minutes, at which point the nitrogen flow was stopped and vacuum was applied. The polymer was stirred under vacuum ( about 0.3 mm Hg) for 30 minutes. The polymer was cooled, ground and a compression molded film prepared. The polymer had an inherent viscosity of 0 48 dL/g IhV. The fluorescence data is summanzed in Table 1. EXAMPLE 2 Poly(ethylene 2,6-naphthalenedιcarboxylate) containing 0.5 mole percent copolymeπzed methyl 2-cyano-3(4-methoxyphenyl)propenoate was prepared by the following procedure. Dimethyl 2,6-naphthalenedιcarboxylate (0.25 mol, 61 g), methyl 2-cyano-3(4- methoxypheny propenoate (0.00125 mol, 0.27 g), ethylene glycol (0.5 mol, 31g) and catalyst metals were placed in a 500 mL polymenzation reactor under a nitrogen atmosphere. The mixture was stirred and heated to 200°C. The temperature was maintained steady for 90 mm. The temperature was increased to 220°C and maintained steady for 80 mm. The temperature was increased to 285 °C over a penod of about 20 minutes, at which point the nitrogen flow was stopped and vacuum was applied. The polymer was stirred under vacuum (about 0 3 mm Hg) for 30 minutes. The polymer was cooled, ground and a compression molded film prepared. The polymer had an inherent viscosity of 0J1 dL/g IhV. The fluorescence data is summaπzed in Table 1. EXAMPLE 3 Poly(ethylene 2,6-naphthalenedιcarboxylate) containing 0.5 mole percent copolymeπzed methyl 2-cyano-3(3-phenoxyphenyl)propenoate was prepared by the following procedure Dimethyl 2,6-naphthalenedιcarboxylate (0.25 mol, 61 g), methyl 2-cyano-3(3- phenoxyphenyl)propenoate (0 00125 mol, 0.35 g), ethylene glycol (0.5 mol, 31g) and catalyst metals were placed in a 500 mL polymenzation reactor under a nitrogen atmosphere. The mixture was stirred and heated to 200° C The temperature was maintained steady for 90 min. The temperature was increased to 220°C and maintained steady for 80 mm. The temperature was increased to 285 °C over a penod of about 20 minutes, at which point the nitrogen flow was stopped and vacuum was applied. The polymer was stirred under vacuum (0.3 mm Hg) for 30 minutes. The polymer was cooled, ground and a compression molded film prepared The polymer had 0.53 dL/g IhV The fluorescence data is summaπzed in Table 1. EXAMPLE 4 Poly(ethylene 2,6-naphthalenedιcarboxylate) containing 0 5 mole percent copolymeπzed ethyl 2-cyano-3[4-(carbethoxymethyloxy)phenyl]propenoate was prepared by the following procedure. Dimethyl 2,6-naphthalenedιcarboxylate (0.25 mol, 61 g), ethyl 2-cyano-3[4- (carbethoxymethyloxy)phenyl]propenoate (0.00125 mol, 0.34 g), ethylene glycol (0.5 mol, 31g) and catalyst metals were placed in a 500 mL polymenzation reactor under a nitrogen atmosphere. The mixture was stirred and heated to 200°C. The temperature was maintained steady for 90 mm. The temperature was increased to 220 °C and maintained steady for 80 mm. The temperature was mcreased to 285^0 over a penod of about 20 minutes, at which point the nitrogen flow was stopped and vacuum was applied. The polymer was stirred under vacuum (0.3 mm Hg) for 30 minutes. The polymer was cooled, ground and a compression molded film prepared. The polymer had 0.72 dL/g D V. The fluorescence data is summanzed in Table 1. EXAMPLE 5 Poly(ethylene terephthalate) containing 10 mole percent copolymeπzed 2,6- naphthalenedicarboxylate (90PET-co- 1 OPEN) was prepared by the following procedure Dimethyl terephthalate (0.225 mol, 43.7 g), dimethyl 2,6-naphthalenedιcarboxylate (0.025 mol, 6.1 g), ethylene glycol (0.5 mol, 31 g), and catalyst metals were placed in a 500 mL polymenzation reactor under a nitrogen atmosphere. The mixture was stirred and heated to 200 C C. The temperature was maintained steady for 90 mm. The temperature was increased to 220 °C and maintained steady for 80 min. The temperature was increased to 285 °C over a penod of about 20 minutes, at which point the nitrogen flow was stopped and vacuum was applied. The polymer \ . as stirred under vacuum (0.3 mm Hg) for 30 minutes. The polymer was cooled, ground and a compression molded film prepared. The polymer had 0.45 dL/g IhV. The fluorescence data is summanzed in Table 1. EXAMPLE 6 Poly(ethylene terephthalate) containing 10 mole percent copolymeπzed 2,6- naphthalenedicarboxylate and 0.5 mole percent methyl 2-cyano-3(4-methoxyphenyl)propenoate was prepared by the following procedure. Dimethyl terephthalate (0.225 mol, 43.7 g), dimethyl 2,6-naphthalenedιcarboxylate (0.025 mol, 6.1 g), methyl 2-cyano-3(4-methoxyphenyl)propenoate (0.00125 mol, 0.27 g), ethylene glycol (0.5 mol, 31 g), and catalyst metals were placed in a 500 mL polymenzation reactor under a nitrogen atmosphere. The mixture was stirred and heated to 200°C. The temperature was maintained steady for 90 mm. The temperature was increased to 210°C and maintained for 60 mm. The temperature was increased to 280 °C, at which point the nitrogen flow was stopped and vacuum applied. The polymer was stirred under vacuum (0.2 mm Hg) for 40 mm. The polymer was cooled, ground and a compression molded film prepared. The polymer had 0.48 dL/g IhV. The fluorescence data is summaπzed in Table 1. TABLE 1. Fluorescence Intensity of PEN Homopolymers and PET-co-PEN Copolymers With and Without Fluorescence Quencher Quencher Maximum Fluorescence Example Polymer Mole % Wavelength, Intensity yι* ; nm 1 PEN none 424 1120 1.0 2 PEN 0.5 432 218 5.1 3 PEN 0.5 427 890 1.3 4 PEN 0.5 429 380 2.9 5 90PET-CO- none 395 275* 1 10PEN 6 90PET-CO- 0.5 388 3* 92 10PEN * The fluorescence intensities of examples 5 and 6 were measured on a different instrument and cannot be compared to examples 1 - 4. ** Io is the intensity of polymer without a fluorescencmg quencher and I is the intensity of the corresponding polymer with a fluorescencmg quencher EXAMPLE 7 Melt extrusion of poly(ethylene-2,6-naphthalate). PEN homopolymer pellets were dned overnight at 140 °C in a forced air drying unit The dπed PEN pellets (297 grams) were added to a 19 mm Brabender single-screw extruder with an L/D ratio of 25/1. The extruder was equipped with a mixing screw with a 3: 1 compression ratio and six rows of staggered pms near the nozzle. The average residence time m the extruder was 1.5 minutes All zones were set at 300°C. The actual melt temperature was 305 °C - 310°C. The extruded rod was quenched in water and chopped. The pellets were then crystallized at 200 °C in a forced air oven for two hours. The crystallized pellets were pulveπzed into a powder form and fluorescence intensity measurements taken. The fluorescence data is summaπzed in Table 2. EXAMPLE 8 Melt blend of poly(ethylene-2,6-naphthalate) with methyl 2-cyano-3(4- methoxyphenyl)propenoate. PEN homopolymer pellets were dπed overnight at 140° C in a forced air drying unit. The dπed PEN pellets (297 grams) and methyl 2-cyano-3(4-methoxyphenyl)propenoate (3 grams) were blended in a bag, extruded, crystallized and ground as descnbed above. The fluorescence data is summanzed in Table 2. EXAMPLE 9 Melt blend of poly(ethylene-2,6-naphthalate) with methyl 2-cyano-3(4- hydroxyphenyl)propenoate. PEN homopolymer pellets were dned overnight at 140 °C m a forced air drying unit. The dned PEN pellets (297 grams) and methyl 2-cyano-3(4-hydroxyphenyl)propenoate (3 grams) were blended in a bag and extruded, crystallized and ground as described in Example 7. The fluorescence data is summaπzed in Table 2. EXAMPLE 10 Melt extrusion of poly(ethylene terephthalate) containing 8 mole percent copolymeπzed 2.6- naphthalenedicarboxylate. 92PET-co-8PEN pellets were dπed overnight at 140°C in a forced air drying unit The dned PEN pellets (297 grams) were added to a 19 mm Brabender smgle-screw extruder with an L/D ratio of 25/ 1. The extruder was equipped with a mixing screw with a 3 : 1 compression ratio and six row s of staggered pins near the nozzle. The average residence time in the extruder was 1.5 minutes. All zones were set at 280 °C. The extruded rod was quenched in water and chopped. The pellets were then crystallized at 180°C in a forced air oven for two hours. The crystallized pellets were pulvenzed mto a powder form for fluorescence intensity measurements. The fluorescence data is summaπzed in Table 2. EXAMPLE 11 Melt extrusion of poly(ethylene terephthalate) containing 8 mole percent copolymeπzed 2,6- naphthalenedicarboxylate with methyl 2-cyano-3(4-methoxyphenyl)propenoate. 92PET-co-8PEN pellets were dπed overnight at 140° C m a forced air drying unit. The dned 92PET-co-8PEN pellets (297 grams) and methyl 2-cyano-3(4-methoxyphenyl)propenoate (3 grams) were blended in a bag and extruded, crystallized and ground as descnbed in Example 11 The fluorescence data is summanzed m Table 2 EXAMPLE 12 Melt extrusion of poly(ethylene terephthalate) containing 8 mole percent copolymeπzed 2,6- naphthalenedicarboxylate with methyl 2-cyano-3(4-hydroxyphenyl)propenoate. 92PET-co-8PEN pellets were dπed overnight at 140°C in a forced air drying unit. The dned 92PET-co-8PEN pellets (297 grams) and methyl 2-cyano-3(4-hydroxyphenyl)propenoate (3 grams) were blended in a bag and extruded, crystallized and ground as descnbed in Example 11. The fluorescence data is summanzed in Table 2. Table 2. Fluorescence Intensity of PEN Homopolymers and PEN Melt Blended With Fluorescence Quencher Quencher Maximum Fluorescence Example Polymer Mole % Wavelength, nm Intensity VI * 7 PEN none 427 924 1.0 8 PEN 1.1 428 245 3 8 9 PEN 1.2 426 156 5.9 10 92PET-co- none 387 1425 1.0 8PEN 11 92PET-co- 1.1 405 78 18 8PEN 12 92PET-CO- 1.2 409 52 27 8PEN * IQ is the intensity of polymer without quencher and I is the intensity of the corresponding polymer with quencher Although the present invention has been descnbed in terms of the presently preferred embodiment, it is to be understood that such disclosure is not to be mterpreted as limiting to the mvention descnbed herein. No doubt that after reading the disclosure, vanous alterations and modifications will become apparent to those skilled m the art to which the mvention pertains. It is intended that the appended claims be interpreted as coveπng all such alterations and modifications as fall within the spiπt and scope of the mvention.

Claims: We claim. 1. A polymer containing a naphthalenedicarboxyhc acid residue compnsmg a fluorescence quenching compound selected from a benzylidene compound capable of absorbing ultraviolet light radiation. 2. The polymer of claim 1 wherein said benzylidene compound includes a polyester reactive group selected from carboxy, carbalkoxy, acyloxy and hydroxy. 3. The polymer of claim 2 wherein said benzylidene compound has the following structure wherein R is selected from the group consisting of hydrogen, C,-C 8 alkyl, substituted C r C 8 alkyl, C 3 - C 8 alkenyl, C 3 -C 8 alkynyl, C 3 -C 8 cycloalkyl, C 3 -C 8 cycloalkenyl and -R 2 -X, wherein R 2 is selected from the group consisting of C,-C 8 alkylene, C 2 -C 8 alkylene-O- C 2 -C 8 alkylene, C 2 -C 8 alkylene-S- C,- C 8 alkylene, C 2 -C 8 alkylene, C 2 -C 8 alkylene-S- C 2 -C 8 alkylene, C 2 -C 8 alkylene-N(S0 2 C,-C 8 alkyl)- C 2 -C 8 alkylene and X is selected from the group consisting of hydroxy, carboxy, carboalkoxy and acyloxy, R, is hydrogen or has 1-3 moieties mdependently selected from the group consisting of hydroxy, C r C 8 alkyl, C,-C 8 alkoxy and halogen; Y is selected from the group consisting of carbalkoxy, cyano, carbamoyl, substituted carbamoyl, aryl, aroyl, C,-C 8 alkylsulfonyl and arylsulfonyl. 4. The polymer of claim 1 wherein said naphthalenedicarboxyhc acid residue is poly(ethylene 2,6-naphthalene dicarboxylate). 5. A polymer containing a naphthalenedicarboxyhc acid residue compnsmg: (a) a dicarboxyhc acid component having at least 0.1 mole percent of a dicarboxyhc acid selected from the group consisting of naphthalene-2,6-dιcarboxyhc acid, and naphthalene-2,6-dιcarboxylate ester; (b) a diol or diamine component; and (c) about 0 01 mole percent to about 5 mole percent- based on 100 mole percent dicarboxyhc acid and 100 mole percent diol or diamine, of a benzylidene compound capable of absorbing ultraviolet light radiation, wherein said polymer has a reduced fluorescence. 6. The polymer of claim 5 wherein said benzylidene compound includes a functionalizmg moiety selected from the group consisting of an acid, a diacid an ester, a diester, hydroxyl and a diol. 7. The polymer of claim 5 wherein said dicarboxyhc acid component, (a) , has from about 0.1 to about 99.9 mole percent of a dicarboxyhc acid selected from the group consisting of naphthalene-2,6- dicarboxyhc acid, and naphthalene-2,6-dιcarboxylate ester 8. The polymer of claim 7 wherein said dicarboxyhc acid component, (a) further includes a difunctional acid or acid equivalent selected from the group consistmg of aromatic dicarboxyhc acids having 8 to 14 carbon atoms, aliphatic dicarboxyhc acids having 4 to 12 carbon atoms, cycloahphatic dicarboxyhc acids having 4 to 12 carbon atoms, and c\ cloahphaπc dicarboxyhc acids having 8 to 12 carbon atoms 9. The polymer of claim 8 wherein said difunctional acid equi \alent is selected from the group consisting of acid anhydndes, esters, and acid chlondes of said acids 10. The polymer of claim 8 wherein said difunctional acid is selected from the group consisting of phthahc acid, isophthahc acid, terephthahc acid, cyclohexanedicarboxyhc acid, dιphenyl-4,4'- dicarboxyhc acid, succinic acid, glutanc acid, adipic acid f manc acid, azelaic acid, sebacic acid, 2J-naphthalenedιcarboxylιc acid, 1 ,4-cyclohexanedιcarboτvhc acid, resorcmoldiacetic acid, diglycohc acid, 4,4'-oxybιs(benzoιc) acid, biphenyldicarboxy he acid, 1,12-dodecanedιcarboxyhc acid, 4,4'-sulfonyldιbenzoιc acid, 4,4'-methylenedιbenzoιc and trans-4,4'-stιlbenedιcarboxyhc acid, and mixtures thereof. 11. The polymer of claim 5 wherein component (b) is a diol. 12 The polymer of claim 11 wherein said diol is selected from the group consisting of cycloahphatic diols having 6 to 20 atoms and aliphatic diols preferably having 2 to 20 carbon atoms 13 The polymer of claim 11 wherein said diol is selected from the group consisting of ethylene glycol, diethylene glycol, tnethylene glycol, 1,4-cyclohexanedιmethanol, propane- 1 ,3-dιol, butane- 1,4-dιol, pentane- 1,5 -diol, hexane-l,6-dιol, 2,2-dιmethyl-l,3-propanedιol, 1,10-decanedιol, 2,2,4,4- tetramethyl-l,3-cyclobutanedιol, 3-methylpentanedιol-(2,4), 2-methylpentanedιol-(l,4), 2,2,4- tnmethylpentane-dιol-(l,3), 2-ethylhexanedιol-(l,3), 2,2-dιethylpropane-dιol-(l,3), hexanedιol-(l,3), 1 ,4-dι-(hydroxyethoxy)-benzene, 2,2-bιs-(4-hydroxycyclohexyl)-propane, 2,4-dιhydroxy- 1 , 1 ,3,3- tetramethyl-cyclobutane, 2,2-bιs-(3-hydroxyethoxyphenyl)-propane, and 2,2-bιs-(4- hydroxypropoxyphenyl)-propane 14 The polymer of claim 5 wherein the diol of component (b) is at least 90 mole percent ethylene glycol 15 The polymer of claim 5 wherein said diamine of component (b) is selected from the group consisting of 1,6-hexanedιamme, meta- or para-xylylenediamine, 1,3- or l,4-cyclohexane(bιs)methylamιne, aliphatic diammes having 2 to 12 carbon atoms, and mixtures thereof 16 The polymer of claim 5 wherein said benzylidene compound includes a polyester reactive group selected from carboxy, carbalkoxy, acyloxy and hydroxy, and has the following structure wherein R is selected from the group consisting of hydrogen, C,-C 8 alkyl, substituted C,-C 8 alkyl, C 3 - C_ alkenyl, C 3 -C 8 alkynyl, C 3 -C 8 cycloalkyl, C 3 -C 8 cycloalkenyl and -R 2 -X, wherein R 2 is selected from the group consisting of C,-C 8 alkylene, C 2 -C 8 alkylene-O- C 2 -C 8 alkylene, C 2 -C 8 alkylene-S- C,- C 8 alkylene, C 2 -C 8 alkylene, C 2 -C 8 alkylene-S- C 2 -C 8 alkylene, C 2 -C 8 alkylene-N(S0 2 C,-C 8 alkyl)- C 2 -C 8 alkylene and X is selected from the group consisting of hydroxy, carboxy, carboalkoxy and acyloxy, R, is hydrogen or has 1-3 moieties mdependently selected from the group consisting of hydroxy, C,-C 8 alkyl, C,-C 8 alkoxy and halogen, Y is selected from the group consisting of carbalkoxy, cyano, carbamoyl, substituted carbamoyl, aryl, aroyl, C,-C 8 alkylsulfonyl and arylsulfonyl. 17. A poly(ethylene 2,6-naphthalene dicarboxylate) composition having a reduced fluorescence compnsmg residues from: (a) a dicarboxyhc acid component compnsmg from about 0.1 mole percent to about mole percent of a dicarboxyhc acid selected from the group consisting of naphthalene-2,6- dicarboxyhc acid, and naphthalene-2,6-dιcarboxylate ester; (b) a diol component; and (c) about 0.1 mole percent to 5 mole percent, based on 100 mole percent dicarboxyhc acid and 100 mole percent diol, of a benzylidene compound capable of absorbing ultraviolet light radiation, said benzylidene compound having a polyester reactive group selected from carboxy, carbalkoxy, acyloxy and hydroxy, and has the following structure: wherem R is selected from the group consisting of hydrogen, C,-C 8 alkyl, substituted C,-C 8 alkyl, C 3 - C 8 alkenyl, C 3 -C 8 alkynyl, C 3 -C 8 cycloalkyl, C 3 -C 8 cycloalkenyl and -R 2 -X, wherein R 2 is selected from the group consisting of C r C 8 alkylene, C 2 -C 8 alkylene-O- C 2 -C 8 alkylene, C 2 -C 8 alkylene-S- C,- C 8 alkylene, C 2 -C 8 alkylene, C 2 -C 8 alkylene-S- C 2 -C 8 alkylene, C 2 -C 8 alkylene-N(S0 2 C,-C 8 alkyl)- C 2 -C 8 alkylene and X is selected from the group consisting of hydroxy, carboxy, carboalkoxy and acyloxy; R, is hydrogen or has 1-3 moieties mdependently selected from the group consisting of hydroxy, C,-C 8 alkyl, C,-Cg alkoxy and halogen; Y is selected from the group consistmg of carbalkoxy, cyano, carbamoyl, substituted carbamoyl, aryl, aroyl, C,-C 8 alkylsulfonyl and arylsulfonyl. 18. The composition of claim 17 wherem said diol of component (b) is at least 90 mole percent ethylene glycol. 19. The composition of claim 16 further compnsmg a second polymer selected from the group consisting of PET, PET copolyester containing up to 20 mole % isophthahc acid, PET copolyester containing up to 70 mole % 1,4-cyclohexanedιmethanol, PET copolyester containing up to 37 mole % diethylene glycol, PET copolyester containing up to 50 mole % 1 ,4-butanedιol, poly(l,4- butyleneterephthalate)(PBT), PBT copolyester containing up to 15 mole % ethylene glycol, poly(ethylene 1 ,4-cyclohexanedιcarboxylate), poly(l,4-cyclohexyldιmethylene terephthalate) (PCT), PCT copolyester containing up to 18 mole % ethylene glycol, PCT copolyester containing up to 40 mole percent isophthahc acid, polycarbonate and mixtures thereof 20. A method for prepanng a polymer blend containing a naphthalenedicarboxyhc acid residue wherein the polymer exhibits reduced fluorescence compnsmg (a) melt blending a polyester compnsmg. (I) dicarboxyhc acid component having at least 0.1 mole percent of a dicarboxyhc acid group selected from the group consisting of naphthalene - 2,6-dιcarboxyhc acid and naphthalene-2,6-dιcarboxylate ester, and (n) a diol component; with (b) about 0 01 mole percent to about 5 mole percent, based on 100 mole percent of said dicarboxyhc acid and 100 mole percent of said diol, of a benzylidene compound capable of absorbing ultraviolet light radiation. 21. The method of claim 20 further compnsmg blending with said naphthalenedicarboxyhc acid residue containing blend a second polymer compnsmg: (a) an acid or acid residue selected from the group consisting of terephthahc acid, 1,4- cyclohexanedicarboxyhc acid, isophthahc acid, naphthalenedicarboxyhc acid and mixtures thereof; and (b) one or more glycols selected from the group consisting of ethylene glycol, 1 ,4- butanediol, 1 ,6-hexanedιol, 1,4-cyclohexanedιmethanol, and 2,2-dιmethyl-l,3- propanediol. 22. The method of claim 21 wherein said second polymer is selected from the group consisting of PET, PET copolyester containing up to 20 mole % isophthahc acid, PET copolyester containing up to 70 mole % 1 ,4-cyclohexanedιmethanol, PET copolyester containing up to 37 mole % diethylene glycol, PET copolyester containing up to 50 mole % 1 ,4-butanedιol, poly(l,4- butyleneterephthalate)(PBT), PBT copolyester containing up to 15 mole % ethylene glycol, poly(ethylene 1 ,4-cyclohexanedicarboxylate), poly( 1 ,4-cyclohexyldimethylene terephthalate) (PCT), PCT copolyester containing up to 18 mole % ethylene glycol, PCT copolyester containing up to 40 mole percent isophthahc acid, polycarbonate and mixtures thereof.

Inventors: CARMAN KAREN LYNN, JONES ALLAN SCOTT, ROGERS MARTIN EMERSON, WEAVER MAX ALLEN, CARMAN, KAREN, LYNN, JONES, ALLAN, SCOTT, ROGERS, MARTIN, EMERSON, WEAVER, MAX, ALLEN
Applicants: EASTMAN CHEM CO, EASTMAN CHEMICAL COMPANY
Application year: 1998
Main classification: C08K5
IPC codes: C08G63, C08K5, C08L67