NOBLE METAL HYDROCRACKING CATALYSTS

Abstract: A noble metal hydrocracking catalyst which has high selectivity for naphtha range products and a process for its preparation are provided. The hydrocracking catalyst comprises: (a) from 70 to 95 weight percent of a Y zeolite, based on the catalyst having a silica to alumina mole ratio of from 4.8 to less than 6.0, a unit cell constant in the range of 24.50 to 24.57, an Na2O level of less than or equal to 0.25 weight percent; (b) from 10 to 30 weight percent, based on the catalyst of an alumina having a mercury intrusion pore volume in the range from 0.55 to 0.85 cc/g; and (c) from 0.5 to 1 weight percent, based on the catalyst of a noble metal; wherein said hydrocracking catalyst has a dispersivity of the noble metal of equal or greater than 48 % by hydrogen chemisorption measurement, a surface area of greater than or equal to 690 m<2>/g by BET surface area measurement, a compacted bulk density in the range of from 0.40 to 0.58 g/cc, and a mercury pore volume in the range of from 0.4 to 0.7 ml/g.

Description: NOBLE METAL HYDROCRACKING CATALYSTS This invention relates to noble metal hydrocracking catalysts, a process for their preparation, and their use . Petroleum refiners produce desirable products, such as gasoline and turbine fuel, by catalytically hydrocracking high boiling hydrocarbons into product hydrocarbons of lower average molecular weight and boiling point. Hydrocracking is generally accomplished by contacting, in an appropriate reactor vessel, a gas oil or other hydrocarbon feedstock with molecular hydrogen in the presence of a suitable hydrocracking catalyst under appropriate conditions, including an elevated temperature and an elevated pressure, such that a hydrocarbon product is obtained containing a substantial proportion of a desired product boiling in a specified range. Often, hydrocracking is carried out in the presence of a catalyst containing sulfided Ni- or Ni-Mo metals. However, these catalysts produce a substantial amount of aromatic content. In some application, such as for jet fuel and diesel as such or as a blend a lower amount of aromatic content is desired. In order to obtain a lower aromatic content hydrocracked product, noble metal hydrocracking catalyst is being used. However, the conventional noble metal catalysts have a substantial gas make (Cι_ to C4), thus lowering the desired liquid yield, i.e., within the range of from C5 to hydrocarbons boiling at about 650 °F (343 °C) . It is desirable to provide a noble metal hydrocracking catalyst which will produce less gas and more liquid products under hydrocracking conditions. The present invention provides a noble metal hydrocracking catalyst which comprises: a) from 70 to 95, e.g. to 93, to 92, or to 90 w% / of a Y zeolite, based on the catalyst having a silica to alumina mole ratio of from 4.8 to less than 6.0, a unit cell constant in the range of from 24.50 to 24.57, a Na2θ level of less than or equal to 0.25 weight percent; b) from 10 to 30 weight percent, based on the catalyst of an alumina having a mercury intrusion pore volume in the range of from 0.55 to 0.85 cc/g; and c) from 0.5 to 1 weight percent, based on the catalyst of a noble metal; wherein said hydrocracking catalyst has a dispersivity of the noble metal of equal to or greater than 48%, preferably 49, most preferably 50% by hydrogen chemisorption measurement, a surface area of greater than or equal to 690, preferably 700, m^/g by BET surface area measurement, a compacted bulk density in the range of from 0.40 to 0.58 g/cc, and a mercury pore volume in the range of from 0.4 to 0.7 ml/g. It has been found that such a noble metal hydrocracking catalyst, which produces more desirable liquid product and less gas make (i.e., C1-C4 hydrocarbons), preferably at most 11 weight percent, may be prepared by the steps comprising: a) ion exchanging a noble metal on a ultrastable Y zeolite, usefully in the form of a powder, by contacting a noble metal salt solution with the zeolite powder, preferably at a pH in the range of from 8.0 to 8.5, for a time sufficient to exchange the noble metal ion to the zeolite to produce a noble metal containing Y zeolite powder; b) extruding the noble metal containing-Y zeolite powder with alumina, water , at least one peptizing aid, and at least one extrusion aid to produce an extrudate; and c) drying and calcining the extrudate at a temperature in the range of from 150 °C to about 550 °C to produce the noble metal hydrocracking catalyst. The ultrastable Y zeolite useful in the invention are Y zeolite having silica to alumina mole ratio of from 4.8, preferably from 5.0, to below 6.0, preferably to 5.8, more preferably to 5.4. The unit cell constant of the Y zeolite is in the range of from 24.50, preferably from 24.52, to 24.57, preferably to 24.55. The preferred ultrastable Y zeolite have a sodium level of less than or equal to 0.25, preferably less than or equal to 0.20 weight percent, calculated as Na2θ. The surface area of the zeolite is preferably in the range of from 750, more preferably from 780, to 830, to more preferably to 810 m^/g. The surface area is determined by BET measurement at a relative pressure, p/prj, o 0.01 to 0.05. Preferred catalysts have high total acid site concentrations (Bronsted and Lewis acid sites) of at least 650 micromoles/gram, preferably at least 680 micromoles/gram, to preferably less than 1000 micromoles/g, more preferably less than 800 micromoles/g, as measured by titration of the catalyst with pyridine, the titration of the acid sites being followed by the measuring the integrated intensities of the infrared absorption peaks in the hydroxyl group stretching region. The method for determining acid site concentrations by adsorption of ammonia at temperatures in the range 200 to 400 °C is described in the following publications: 1) M. A. Makarova and J. Dwyer, Journal of Physical Chemistry, 1993, 97, 6337; and 2) M. A. Makarova, A. Garforth, V. L. Zholobenko, J. Dwyer, G. J. Earl and D. Rawlence in Zeolites and Related Microporous Materials: State of the Art 1994, Studies in Surface Science and Catalysis, Vol. 84, 1994, Elsevier Science B.V., p. 365. The technique for acid site characterization with pyridine is similar to that described for ammonia in the indicated publications except for substitution of pyridine for ammonia. The ultrastable Y zeolite (USY) used in the preparation of the catalyst of the invention can be made by at least partially ion-exchanging a sodium Y zeolite to reduce the level of sodium to about 3 weight percent of Na2θ, based on the zeolite, by conventional ion- exchange method (ion-exchange step) then heating the zeolite in the presence of stream at a partial pressure in the range of from 0.2 to 1.0 atmospheres at a temperature in the range of from 600 to 800 °C (steam calcination step) . The ion-exchange is typically carried out by mixing the zeolite with an aqueous solution containing a dissolved ammonium salt, such as ammonium nitrate, ammonium sulphate, and ammonium chloride, then stirring the resulting slurry for between 0.5 to 4 hours at a temperature above ambient but less than about 100 °C . For a lower level of sodium content these steps are repeated at least once. The steam calcined zeolite is then ammonium ion-exchanged again to lower the Na2θ content to the desired range of less than 0.25, preferably 0.20 percent. U.S. Patent Specification No. 5,559,567 discloses these ultrastable Y-zeolites (USY) useful for the invention. Binders useful in the invention are aluminas, such as pseudoboehmite, gamma and bayerite aluminas. These binders are readily available commercially and are used to manufacture alumina-based catalysts. LaRoche Chemicals, through its VERSAL family of aluminas and Vista Chemical Company, through its CATAPAL aluminas, Criterion Catalyst Company, through its HMPA aluminas, provide suitable alumina powders which can be used as binders in preparing the instant catalysts (VERSAL and CATAPAL are trade marks) . The preferred alumina has a mercury intrusion pore volume in the range of from 0.55, preferably from 0.65, to 0.85, preferably to 0.76 cc/g. Preferred alumina binders to be used in the preparation of the catalyst, particularly when extrusion is utilized, are the high- dispersity alumina powders. Such high-dispersity aluminas have a dispersity index of greater than 50% in a aqueous acid dispersion having an acid content of 0.4 milligram equivalents of acid (acetic) per gram of AI2O3. Such high-dispersity aluminas are exemplified by Vista's CATAPAL D alumina and Criterion's HMPA alumina. The noble metal salts may be palladium salts or platinum salts. The palladium salts are preferred. The palladium salts used in the invention preferably include, for example, organic amine complex salts and chloride salts such as palladium ammonium nitrate, palladium chloride, palladium diaminoethane nitrate, and palladium ammonium chloride. The noble metal salt concentration is such as to achieve final noble metal concentration (as elemental palladium) in the catalyst in the range of from 0.5, preferably 0.55, to 1.0 weight percent, to preferably 0.9 weight percent , as reduced metal to total catalyst. The ion exchange solution is typically water but may contain a soluble ammonium salt or/and dilute aqueous ammonia . The noble metal is incorporated by mixing the zeolite with the noble metal salt-solution, then stirring the resulting slurry for a time suitably in the range of from 0.5 to 4 hours at a temperature suitably at or above ambient but less than 85 °C with the pH of the noble metal salt solution preferably in the range of from 8.0 to 8.5, then dried by conventional drying methods such as spray drying and flash drying. The noble metal containing-ultrastable Y zeolite component, alumina component, water, and extrusion aid component, and peptizing agent can be added in any order and extruded to an extrudate. The added mixture preferably contains: i) from 70 to 90 weight percent, based on the catalyst dry weight, of a noble metal containing ultrastable Y- zeolite powder (USY powder) ; ii) from 10 to 30 weight percent of alumina, based on the catalyst dry weight; iii) an amount of water such that the mixture has a volatiles content (800 °C basis) of from 48 to 55 weight percent, based on the wet mixture; iv) from 0.5, preferably from 1 to 6, preferably to 5, more preferably to 2 weight percent of an extrusion aid (flow control agent), based on the mixture dry weight; and, v) from 0.5, preferably from 1 to 6, preferably 5 weight percent of a peptizing agent, based on the mixture dry weight. The peptizing agent may be an organic acid or an inorganic acid or a mixture thereof used in the extrusion of zeolite and alumina. An inorganic acid or a C2 to Cg organic acid is preferred as the peptizing agent. Typical peptizing agents include, for example, acetic acid, nitric acid, citric acid and oxalic acid. The preferable extrusion aid component is a water soluble or dispersible polymer, notably a flocculant. Preferable extrusion aids include, for example, Superfloc 16 Plus brand of polyacrylamide available from Cytec Industries, Methocel brand of polymethylcellulose available from Dow Chemical Company, and Jayfloc 837, a polyamine available from Calloway Chemical Company. These extrusion aids are readily available commercially. The extrudate is then dried and calcined at a temperature in the range of from 150 °C to 550 °C, preferably from 450 °C to 550 °C, under conditions effective to obtain a noble metal dispersion of greater or equal to 48%, preferably 50% by hydrogen chemisorption measurement and desirably an LOI (loss on ignition) of less than about 3 weight percent. During the calcination step at a temperature above about 150 °C, the heating is most usefully conducted under oxidizing conditions. The term oxidizing conditions means the atmosphere has sufficiently high partial pressure of oxygen, i.e., under conditions that maintain at least a partial pressure of about 0.1 atmosphere (10 Kpa) . Methods of obtaining a highly dispersed noble metal are described in Regan, W. J., Chester, A. J., and Kerr, G.T., J. Catal . , 69, 89 (1981) and S. T Homeyer and W. M. H. Sachtler, J. Catal., 117, 91-101 (1989) . The resulting noble metal hydrocracking catalyst will usefully have a noble metal dispersion of greater than or equal to 48%, especially 50%, by hydrogen chemisorption measurement. The noble metal hydrocracking catalyst typically has a surface area of greater than or equal to 690, preferably 700, m 2 /g by BET measurement, a compacted bulk density in the range of from 0.40, preferably from 0.42, to 0.58, preferably to 0.57 g/cc, total mercury pore volume in the range of from 0.4 ml/g to 0.7 ml/g. Suitably, the pore size distribution by mercury intrusion method for pore sizes of 40-100 Angstrom is less than 0.1 ml/g. For preferred catalysts, the pore size distribution for 100-500 Angstrom is from 0.02 to 0.04 ml/g, for 500-1500 Angstrom is from 0.06 to 0.16 ml/g, for 1500-10,000 Angstrom is from 0.15 to 0.4 suitably to 0.25 ml/g, and for greater than 10,000 Angstrom is less than 0.15, suitably less than 0.1 ml/g. The prepared hydrocracking catalyst can be activated with hydrogen as is conventional in the art. The present invention additionally provides a hydrocracking process (for converting a hydrocarbonaceous feedstock into lower boiling materials) which comprises contacting the feedstock with hydrogen at elevated temperature in the presence of a catalyst of the invention . Hydrocracking conditions suitably comprise temperatures in the range of from 100 °C, preferably from 150 °C, more preferably from 200 °C, to 500 °C, preferably to 450 °C, more preferably to 400 °C, and pressures above 40 atmospheres (4 MPa) . The total pressure will typically range from 100 to 3500 psig (0.7 to 2.4 MPa). The hydrogen partial pressure will typically range from 100 (0.7 MPa), preferably from 300 (2 MPa), more preferably from 600 psig (4 MPa), to 3500 (2.4 MPa), preferably to 3000 psig (20 MPa) . The hydrogen feed rate will typically range from 1000, more preferably from 2000, to 15,000, more preferably to 10,000 standard cubic feet per barrel ("SCF/BBL") . The feedstock rate will typically have a liquid hourly space velocity ("LHSV") ranging from 0.05, preferably from 0.1 to 20, preferably to 15, more preferably to 10. The catalyst of the invention produces low amounts of gas and more liquid products under hydrocracking conditions. Particularly, the catalyst produces high yield of hydrocarbons boiling in the range of C5 to 530 °F (277 °C) for naphtha and jet range, particularly, at least 80 weight percent yield. The invention will now be described by the following examples . Examples : These examples demonstrate several embodiments of the invention. SAR in the examples stands for the molar Siθ2/ l2θ3 ratio. Na2θ represents the soda content in weight percent (dry basis) . Surface area in m^/g is measured by the BET method at a relative pressure, p/pr j , of 0.01 to 0.05. The palladium content is measured as elemental palladium in weight percent. Crystallinity is reported as percent relative to a reference USY standard. UCC stands for the zeolite unit cell constant in Angstroms. LOI stands for loss-on-ignition at the temperature indicated in weight percent. Catalyst Preparation Catalyst A 75.0 Pounds (34 kg) of CBV-500 USY zeolite from PQ Zeolite B.V. (LOI @ 800 °C 20.0%) was added to 55 gallons (208 1) of deionized water. The pH of the slurry was adjusted to 8.3 by addition of 10% aq. NH3. 15.6 Pounds, (7.1 kg) of Pd(NH 3 ) 4 (N0 3 ) 2 solution (3.17 %wt palladium) was added to the slurry over a 30 minute period. During the addition of the palladium solution the pH was maintained between 8.0 and 8.5 by addition of 10% aqueous NH3. After 90 minutes the zeolite was recovered by filtration; it was dried and milled in a flash dryer with an outlet temperature of 210 °F (99 °C) . Properties of Zeolite Crystallinity 95 SAR 5.3 Na20 0.00 Surface Area 848 Pd 0.82 LOI 20.9 11.8 Kg of the palladium ion exchanged CBV- 500 zeolite, prepared above, was added to a 130 litre Littleford mixer along with 3.1 kg of deionized water and mixed for 2 minutes. 2.3 Kg of HMPA alumina (LOI @ 1000 °C of 24-29%; Na 2 0 < 0.05%w; S0 4 = <0.8%w) from Criterion Catalyst Company and 3.1 kg of deionized water was added and mixed for 2 minutes. 1.5 Kg of deionized water and 187 gm of acetic acid was added and mixed for 2 minutes. 0.4 Kg of calcined fines and 91 gm of Methocel was added and mixed for an additional 2 minutes. The mixture was then transferred to a 4" (101 mm) Bonnet extruder and extruded an 1/8" (3.2 mm) dieplate containing 174 holes. The catalyst was dried for 3 hours at 250 °F (121 °C) and calcined in flowing air at 500 °C. Catalyst B 75 Pounds (34 kg) of CBV-500 USY zeolite from PQ Zeolites BV (LOI @ 800 °C 20.24%) was added to 55 gallons (208 1) of deionized water. The pH of the slurry was adjusted to 8.3 by addition of 10% aq. NH3. 16.7 Pounds (7.6 kg) of Pd(NH 3 ) 4 (NO3) 2 solution (2.98 %wt palladium} was added to the slurry over a 30 minute period. During the addition of the palladium solution the pH was maintained between 8.0 and 8.5 by addition of 10% aqueous NH3. After 90 minutes the zeolite was recovered by filtration; it was dried and milled in a flash dryer with an outlet temperature of 210 °F (99 °C) . Properties of Zeolite LOI 22.3% UCC 24.55 Crystallinity 96 Pd 0.83% 2.26 Kg of HMPA alumina from Criterion Catalyst Co. (LOI at 1000 °C 28.5%), 11.79 kg of palladium ion exchanged CBV-500, prepared above, and 0.60 kg of calcined and milled fines were mixed in a mix muller for 5 minutes. 2.9 Kg of deionized water along with 113 gm of Jayfloc 837 were added and mixed for 10 minutes. 142 Gm of Methocel was then added and mixed for 10 minutes. Finally, 4.3 kg of deionized water along with 397 gm of acetic acid was added and mixed for an additional 35 minutes. The mixture was then transferred to a 4" (101 mm) Bonnet extruder and extruded a 1/8" (3.2 mm) dieplate containing 174 holes. The catalyst was dried for 3 hours at 250 °F (121 °C) and calcined in flowing air at 500 °C. Catalyst C 75 Pounds (34 kg) of CBV-500 USY zeolite from PQ Zeolites BV (LOI @ 800 °C 20.24%) was added to 55 gallons (208 1) of deionized water. The pH of the slurry was adjusted to 8.3 by addition of 10% aq. NH3. 16.7 Pounds (7.6 kg) of Pd (NH 3 ) 4 (N0 3 ) 2 solution {2.98 %wt palladium} was added to the slurry over a 30 minutes period. During the addition of the palladium solution the pH was maintained between 8.0 and 8.5 by addition of 10% aqueous NH3. After 90 minutes the zeolite was recovered by filtration; it was dried and milled in a flash dryer with an outlet temperature of 210 °F (99 °C) . Properties of Zeolite LOI 22.3% UCC 24.55 Crystallinity 96 Pd 0.83% 2.26 Kg of HMPA alumina from Criterion Catalyst Co. (LOI at 1000 °C 28.5%), 11.79 kg of palladium ion exchanged CBV-500, prepared above, and 0.60 kg of calcined and milled fines were mixed in a 130 litre Littleford mixer for 2 minutes. 2.9 Kg of deionized water along with 113 gm of Jayfloc 837 were added and mixed for 2 minutes. 142 Gm of Methocel was then added and mixed for 2 minutes. Finally, 4.3 kg deionized water and 397 gm of acetic acid were added and mixed for an additional 16 minutes. The mixture was then transferred to a 4" (101 mm) Bonnet extruder and extruded a 1/8" (3.2 mm) dieplate containing 174 holes. The catalyst was dried for 3 hours at 250 °F (121 °C) and calcined in flowing air at 500 °C. Catalyst E 63.8 Pounds (28.9 kg) of CBV-500 USY zeolite from PQ Zeolites BV (LOI 14%) was added to 55 gallons (208 1) of deionized water. The pH of the slurry was adjusted to 8.5 by addition of 10% aq.NH3. 13.3 Pounds (6 kg) of Pd (NH3) 4 (NO3) 2 solution {3.4 %wt palladium} was added over a 30 minute period. During addition of the palladium solution the pH was maintained between 8.0 and 8.5 by addition of 10% aqueous NH3. After 90 minutes the zeolite was recovered by filtration; it was dried and milled in a flash dryer with an outlet temperature of 210 °F (99 °C) . Properties of Zeolite Crystallinity 99 SAR 5.4 Na20 0.00 Surface Area 821 LOI 23.9 12.0 Kg of palladium ion exchanged CBV-500, prepared above, and 2.26 kg of Criterion HMPA alumina were added to a mix muller and mixed for 5 minutes. 7.84 Kg of deionized water and 0.362 kg acetic acid were added and mixed for 30 minutes. 0.6 Kg of calcined fines and 57 gm of Superfloc 16 was added and mixed for 15 minutes. The mixture was transferred to a 4" (101 mm) Bonnet extruder and extruded a 1/8" (3.2 mm) dieplate containing 174 holes. The catalyst was dried for 3 hours at 250 °F (121 °C) and calcined in flowing air at 500 °C. Catalyst F 404 Grams of CP300-56D USY (LOI @ 1000 °C of 26.28%) was added to 1454 grams of deionized water. The pH of the slurry was adjusted to 8.5 by dropwise addition of 5 N aqueous ammonia solution. 6.87 Grams of Pd (NH3) 4 (NO3) 2 was dissolved in 162 grams of deionized water and added to zeolite slurry during 30 minutes. Stirring was continued for 2 hours after addition of the palladium solution was complete. The palladium ion exchanged zeolite was recovered by filtration and dried at 125 °C for 16 hours. The catalyst was prepared by adding 110.6 grams of the above palladium exchanged USY (LOI @ 1000 °C of 12.08%) to a mix muller and mulling for 10 minutes. 14.6 Grams of Vista Catapal D alumina (LOI @ 1000 °C of 26.23%) was added to the muller and the mixture mulled for 6 minutes. A solution of 1.08 grams citric acid monohydrate in 99 grams deionized water was added to the muller and mulled for 6 minutes. 4 Grams of Methocel was added to the mix muller and mulled for 3 minutes . The mixture was transferred to a 1 inch (25.4 mm) Bonnot extruder and extruded. The catalyst pellets were dried for 16 hours at 125 °C overnight and calcined in flowing air by raising the catalyst temperature from 125 to 500 °C in 4 hours and holding at 500 °C for 2 hours. During this period 10 litres air/gram catalyst were passed through the catalyst bed. Catalyst G 404 grams of CP300-56D USY (LOI @ 1000 °C of 26.28%) was added to 1454 grams of deionized water. The pH of the slurry was adjusted to 8.5 by dropwise addition of 5 N aqueous ammonia solution. 7.72 Grams of Pd (NH3) 4 (NO3) 2 was dissolved in 162 grams of deionized water and added to zeolite slurry during 30 minutes. Stirring was continued for 2 hours after addition of the palladium solution was complete. The palladium ion exchanged zeolite was recovered by filtration and dried at 125 °C for 16 hours. The catalyst was prepared by adding 111.4 grams of the above palladium exchanged USY (LOI @ 1000 °C of 12.03%) to a mix muller and mulling for 10 minutes. 33.2 Grams of Vista Catapal D alumina (LOI @ 1000 °C of 26.23%) was added to the muller and the mixture mulled for 6 minutes. A solution of 1.23 grams acetic acid in 104 grams deionized water was added to the muller and mulled for 6 minutes. 4 Grams of Methocel was added to the mix muller and mulled for 3 minutes. The mixture was transferred to a 1 inch (24.4 mm) Bonnot extruder and extruded. The catalyst pellets were dried for 16 hours at 125 °C overnight and calcined in flowing air by raising the catalyst temperature from 125 to 500 °C in 4 hours and holding at 500 °C for 2 hours. During this period 10 litres air/gram catalyst were passed through the catalyst bed. Catalyst H 397 Grams of CP300-56D USY (LOI @ 1000 °C of 24.90%) was added to 1428 grams of deionized water. The pH of the slurry was adjusted to 8.5 by dropwise addition of 5 N aqueous ammonia solution. 6.87 Grams of Pd (NH3) 4 (NO3) 2 was dissolved in 159 grams of deionized water and added to zeolite slurry during 30 minutes. Stirring was continued for 2 hours after addition of the palladium solution was complete. The palladium ion exchanged zeolite was recovered by filtration and dried at 125 °C for 16 hours. The catalyst was prepared by adding 114.6 grams of the above palladium exchanged USY (LOI @ 1000 °C of 15.32%) to a mix muller and mulling for 10 minutes. 14.6 Grams of Vista Catapal D alumina (LOI @ 1000 °C of 26.23%) was added to the muller and the mixture mulled for 6 minutes. A solution of 1.08 grams citric acid monohydrate in 90 grams deionized water was added to the muller and mulled for 6 minutes. 4 Grams of Methocel was added to the mix muller and mulled for 3 minutes. The mixture was transferred to a 1 inch (25.4 mm) Bonnot extruder and extruded. The catalyst pellets were dried for 16 hours at 125 °C overnight and calcined in flowing air by raising the catalyst temperature from 125 to 500 °C in 4 hours and holding at 500 °C for 2 hours. During this period 10 litres air/gram catalyst were passed through the catalyst bed. Catalyst I The palladium ion exchanged zeolite used in preparation of Catalyst E was used in this catalyst preparation. 11.3 Kg of the palladium ion exchanged CBV- 500 and 3.0 kg Criterion HMPA alumina were added to a mix muller and mixed for 5 minutes. 7.79 Kg deionized water and 0.363 kg acetic acid were added and mixed for 30 minutes. 0.6 Kg of calcined fines and 57 gm of Superfloc 16 was added and mixed for 15 minutes. The mixture was transferred to a 4" (101 mm) Bonnet extruder and extruded a 1/8" (3.2 mm) dieplate containing 174 holes. The catalyst was dried for 3 hours at 250 °F (121 °C) and calcined in flowing air at 500 °C. Catalyst J 71.4 Pounds (32.4 kg) of CP300-56D USY zeolite from Zeolyst International (LOI @ 800 °C 23.0%) was added to 55 gallons (208 1) deionized water. The pH of the slurry was adjusted to 8.3 by addition of 10% aqueous NH3. 13.3 Pounds (6 kg) of Pd (NH 3 ) 4 (N0 3 ) 2 solution {3.4 %wt palladium} was added to the slurry over a 30 minute period. During the addition of the palladium solution the pH was maintained between 8.0 and 8.5 by addition of 10% aq.NH3. After 90 minutes the zeolite was recovered by filtration; it was dried and milled in a flash dryer with an outlet temperature of 210 °F (99 °C) . Properties of Zeolite Crystallinity 97 SAR 7.1 Na20 0.00 Surface Area 843 Pd 0.82 8.59 Kg of the palladium ion exchanged CP300-56D, prepared above, and 2.41 kg of Criterion HMPA alumina were added to a mix muller and mixed for 5 minutes. 6.72 Kg deionized water and 0.290 kg acetic acid were added and mixed for 30 minutes. 0.45 Kg of calcined fines and 45 gm of Superfloc 16 were added and mixed for 15 minutes. The mixture was transferred to a 4" (101 mm) Bonnet extruder and extruded a 1/8" (3.2 mm) dieplate containing 174 holes. The catalyst was dried for 3 hours at 240 °F (116 °C) and calcined in flowing air at 500 °C. Catalyst Activation Step The catalyst is activated in the reactor by introducing flow of hydrogen over the catalyst at a rate of 60 litre/hr for a catalyst charge of 10 grams (ca. 20 cc) . The reactor pressure is raised to 1450 psig (10 MPa) at room temperature, after which the temperature is raised from room temperature to 750 °F (399 °C) in 12 hours and held at 750 °F (399) for 6 hours. The temperature is then lowered to 300 °F (149 °C) and the hydrogen rate adjusted to the target flow rate, 48.5 litres/hour for 8000 SCF hydrogen/bbl . Catalyst Performance Test The catalyst was tested in once-through mode with fresh hydrogen at process conditions of 1.7 LHSV (1/1-hr), 1450 psig (10 MPa) total pressure, 8000 scf hydrogen/bbl feed (100% hydrogen) with 5000 ppm sulphur added as dimethyldisulphide to the feedstock. The feedstock was second cracking reactor feed obtained from a commercial hydrocracker with a density of 0.8117 g/cc, a hydrogen content of 13.884% w, less than 1 ppm by weight organic nitrogen and sulphur with the boiling characteristics indicated in the table below: ASTM D-2887 Simulated °F (°C) Distillation % Overhead 5 336 169 30 402 206 50 441 227 70 503 262 95 653 345 Conversion to 375 °F (191 °C)- was varied over a range of about 40 to 70 %w. Catalyst activities and selectivities were compared at 60% conversion to 375 °F (191 °C)- products. % yield = weight product cut/weight feed * 100% Catalyst : A B C USY Source CBV 500 CBV 500 CBV 500 USY Amount, %w 85 85 85 Alumina Criterion Criterion Criterion HMPA HMPA HMPA Surface Area, m^/g 729 732 n . a . Palladium, %weight 0.7 0.7 0.7 Palladium 66 n . a . n. a . Dispersion, Percent Compacted Bulk 0.494 0.568 0.564 Density, g/cc Pore Volume, 0.430 0.396 n . a . Nitrogen, ml/g Pore Volume, 0.6782 0.4401 0.4171 Mercury, ml/g Pore Size Distribution, Mercury Intrusion, ml/g 40-100 A 0.0855 0.0637 0.0582 100- -500 A 0.0392 0.0311 0.0302 500- -1500 A 0.0829 0.1231 0.0975 1500-10,000 A 0.3681 0.2047 0.2095 >10, , 000 A 0.1025 0.0175 0.0217 Product Yie. Ids, %weight, at 60% 1 Conversion to 375 op (191 °C) C1-C4 9.68 9.96 10.54 C5-: L80 °F (82 °C) 15.69 15.16 16.35 180- -320 °F 30.14 29.47 29.08 (82- -160 °C) 320- -530 °F 36.34 37.20 35.81 (160-277 °C) Catalyst USY Source CBV 500 CP300-56D CP300-56D USY Amount, %w 85 90 80 Alumina Criterion Vista Vista HMPA Catapal D Catapal D Peptizing Agent Acetic Citric Acetic Acid Acid Acid Bronsted and Lewis n . a . 746 n.a. Acid Sites, micromoles/gram Surface Area, m^/g 704 n.a. n.a. Palladium, %weight 0.7 0.7 0.7 Palladium 49 68 38 Dispersion, Percent Compacted Bulk 0.532 n.a n.a, Density, g/cc Product Yields, %weight, at 60% Conversion to 375 °F (191 °C) c l "c 4 9.46 10.69 11.55 C5-I8O °F (82 °C) 14.49 15.45 16.52 180-320 °F 30.35 26.67 25.68 (82-160 °C) 320-530 °F 37.43 37.91 36.44 (160-277 °C) Catalyst : H I J 23049-007 1684-27-2 1684-30 USY Source CP300-56D CBV 500 CP300-56D USY Amount, %w 90 80 85 Alumina Vista Criterion Criterion Catapal D HMPA HMPA Peptizing Agent Citric Acetic Acetic Acid Acid Acid Bronsted and Lewis 590 n.a. n.a. Acid Sites, micromoles/gram Surface Area, m^/g i. a . 700 694 Palladium, %weight 0.7 0.7 0.7 Palladium 52 46 n.a , Dispersion, Percent Compacted Bulk n.a, 0.517 0.550 Density, g/cc Product Yields, %weight, at 60% Conversion to 375 °F (191 °C) c l _c 4 13.29 11.55 9.03 C5-I8O °F 17.57 17.41 13.93 (82 °C) 180-320 °F 24.06 27.79 30.58 (82-160 °C) 320-530 °F 35.73 34.81 38.74 (160-277 °C) As seen in the table Catalysts A, B, C, E, F and J of the invention have low C]_-C4 gas yields, less than 11 %w, based on feed. Catalysts G and I have low palladium dispersion and have high gas makes, greater than 11 %w, based on feed. Example F has a higher concentration of Bronsted and Lewis acid sites, compared to Catalyst H and has a low C1-C gas yield.

Claims: C L A I M S 1. A hydrocracking catalyst which comprises: a) from 70 to 95 weight percent of a Y zeolite, based on the catalyst having a silica to alumina mole ratio of from 4.8 to less than 6.0, a unit cell constant in the range of from 24.50 to 24.57, a Na2θ level of less than or equal to 0.25 weight percent; b) from 10 to 30 weight percent, based on the catalyst of an alumina having a pore volume (measured by the mercury intrusion method) in the range of from 0.55 to 0.85 ml/g; and c) from 0.5 to 1 weight percent, based on the catalyst of a noble metal; wherein said hydrocracking catalyst has a dispersivity of the noble metal of equal or greater than 48% by hydrogen chemisorption measurement, a surface area of greater than or equal to 690 m^/g by BET surface area measurement, a compacted bulk density in the range of from 0.40 to 0.58 g/cc, and a pore volume (measured by the mercury intrusion method) in the range of from 0.4 to 0.7 ml/g. 2. A catalyst as claimed in claim 1, wherein the noble metal is palladium. 3. A catalyst as claimed in claim 1 or claim 2, wherein the silica to alumina mole ratio of the Y zeolite is in the range of from 4.8 to 5.8. 4. A catalyst as claimed in any one of claims 1 to 3, which has one or more of the following pore size distributions (by the mercury intrusion method) for pore sizes of 40-100 Angstrom of less than 0.1 ml/g, for pore sizes 100-500 Angstrom of in the range of from 0.02 to 0.04 ml/g, for pore sizes of 500-1500 Angstrom of the range of from 0.06 to 0.16 ml/g, and for pore sizes of 1500-10,000 Angstrom of in the range of from 0.15 to 0.4 ml/g. 5. A catalyst as claimed in any one of claims 1 to 4, wherein the total acid site concentration of the catalyst is at least 650 micromoles/gram. 6. A catalyst as claimed in any one of claims 1 to 5, wherein the alumina has a dispersity index of greater than 50%. 7. A process for producing a noble metal hydrocracking catalyst comprising the steps of: a) ion exchanging a noble metal on a ultrastable Y zeolite having a silica to alumina ratio in the range of from 4.8 to less than 6.0, a unit cell constant in the range of from 24.50 to 24.57, a Na2θ level of less than or equal to 0.25, by contacting a noble metal salt solution with the zeolite for a time sufficient to exchange the noble metal ion to the zeolite to produce a noble metal containing Y zeolite; b) extruding a mixture comprising i) from 70 to 95 weight percent, based on the catalyst (dry basis), of the noble metal containing-Y zeolite, ii) from 10 to 30 weight percent based on catalyst (dry basis) of an alumina having a pore volume (by the mercury intrusion method) in the range of from 0.55 to 0.85 cc/g; iii) a sufficient amount of water such that the mixture has a volatiles content (800 °C basis) of from 48 to 54 weight percent, based on the wet mixture, iv) from 0.5 to 6 weight percent, based on the catalyst (dry basis), of an extrusion aid, and v) from about 0.5 to about 6 weight percent, based on the catalyst (dry basis) , of at least one peptizing agent to produce an extrudate; c) drying and calcining the extrudate at a temperature in the range of from 150 °C to 550° C to produce the noble metal hydrocracking catalyst. 8. A process as claimed in claim 7, wherein in step c) , calcination is carried out under oxidizing conditions. 9. A process as claimed in claim 7 or claim 8, wherein the noble metal salt solution is a solution comprising a palladium salt. 10. A process as claimed in claim 9, wherein the noble metal salt solution is an aqueous solution comprising a palladium salt. 11. A process as claimed in any one of claims 7 to 10, wherein the noble metal salt is selected from the group consisting of palladium tetrammine nitrate, palladium chloride, palladium diaminoethane nitrate, and palladium ammonium chloride. 12. A process as claimed in any one claims 7 to 11, wherein the ultrastable Y zeolite has a surface area in the range of from 750 to 830 m^/g. 13. A noble metal hydrocracking catalyst obtainable by a process as claimed in any one of claims 7 to 12. 14. A process for a hydrocracking a hydrocarbon aqueous feedstock comprising contacting the feedstock in the presence of hydrogen with a hydrocracking catalyst as claimed in claim 1 or claim 13.

Inventors: COOPER DAVID ALLEN, WINQUIST BRUCE HERMAN CHARLES, COOPER, DAVID, ALLEN, WINQUIST, BRUCE, HERMAN, CHARLES
Applicants: SHELL CANADA LTD, SHELL INT RESEARCH, SHELL CANADA LIMITED, SHELL INTERNATIONALE RESEARCH MAATSCHAPPIJ B.V.
Application year: 1998
Main classification: C10G47
IPC codes: B01J21, B01J29, B01J35, B01J37, C10G47