DURABLE, FILM-FORMING, WATER-DISPERSIVE POLYMERS

Abstract: Core-shell polymers, or polymers having at least a hydrophobic portion, are provided. The polymers also have either a hydrophilic portion, or, alternatively, one or more surfactants may be employed in conjunction with a given polymer. The polymers incorporate the following moieties: [(A)m (B)n (C)p (D)q (E)r]x wherein A, B, C, D, and E represent functionalities as follows: A = hydrophobic component controlling solubility in organic solvents selected from moieties which, when polymerized, have a glass transition temperature (Tg) in the range between -150 and +25 DEG C; B = hydrophobic and solvent barrier composed of at least one moiety which, when polymerized, has a Tg greater than 25 DEG C; C = hydrophilic dispersant, selected from a wide variety of water-soluble moieties, such as poly(ethylene glycol) units, vinyl pyrrolidones, vinyl imidazoles, and acrylamides; D = hydrophobic UV absorber; E = highly polar functional group; m = 5 to 95; n = 5 to 95; p = 0 to 60; q = 0 to 50; r = 0 to 40; m + n + p + q + r = 100; and x = 1 to 100,000. Either the C moiety or the E moiety must be present in the polymer to provide a polymer having either a hydrophilic portion or a highly polar portion. Alternatively, a surfactant may be used in conjunction with the polymer, whether in the presence or the absence of the C or E, or both, moieties.

Description: DURABLE, FILM-FORMING, WATER-DISPERSIVE POLYMERS TECHNICAL FIELD The present invention relates generally to core/shell and other polymers with hydrophobic and hydrophilic portions, which, when used by themselves or in combination with a surfactant, are useful for dispersing otherwise non-soluble materials, such as pigment and dyes, in a fluid medium, and upon drying, provide improved physical properties to the dried film. Specifically, improved ink-jet ink compositions are obtained. BACKGROUND ART Core/shell polymers are well-known; such polymers typically have a hydrophilic portion and a hydrophobic portion comprising a latex particle morphology consisting of an inner "core", surrounded by an outer "shell". Core/shell polymers are commonly used to encapsulate hydrophobic molecules or particles, such as pigments, which are ordinarily not insoluble in water, but which, after association with polymers, form stable dispersions in water. Dispersion occurs when the hydrophobic portion of the polymer associates with the water- insoluble molecule or particle, and the hydrophilic portion of the polymer disperses with water. U.S. Patent 4,597,794 discloses the dispersion of pigments in an aqueous vehicle, using aqueous binders comprising both hydrophilic and hydrophobic components. The dispersion of the pigment is followed by centrifugation to eliminate the non-dispersed components such as agglomerates. Examples of the hydro- philic component comprise polymers of monomers having a mainly additively polymerizable vinyl group, into which hydrophilic construction portions such as carboxylic acid groups, sulfonic acid groups, sulfate groups, etc. are introduced by using a predetermined amount of an α,β-unsaturated monomer such as acrylic acid, methacrylic acid, crotonic acid, itaconic acid, itaconic acid monoester, maleic acid, maleic acid monoester, fumaric acid, fumaric acid monoester, vinyl sulfonic acid, sulfoethyl methacrylate, sulfopropyl methacrylate, sulfonated vinylnaph- thalene, etc. Examples of the hydrophobic portion comprise polymers of mono- SUBST1TUTE SHEET (RULE 26) mers selected from the group consisting of styrene, styrene derivatives, vinylnaph- thalene, vinylnaphthalene derivatives, and α,β-ethylenic unsaturated carboxylate of aliphatic alcohol having C 8 -C 18 . In addition to the foregoing monomers, also included are acrylonitrile, vinylidene chloride, α,β-ethylenic unsaturated carboxylate, vinyl acetate, vinyl chloride, acrylamide, methacrylamide, hydroxyethyl methacrylate, hydroxypropyl methacrylate, glycidyl methacrylate, N-methylol acrylamide, N-butoxymethyl acrylamide, etc. U.S. Patent 5,082,757 discloses encapsulated toner compositions comprising a core and a hydroxylated polyurethane microcapsule shell derived from the polyconden- sation of a polyisocyanate and a water soluble carbohydrate. The core comprises a polymer binder, pigment, dye, or mixtures thereof. Examples of the polymer binder include polymerized monomers selected from the group consisting of acrylates, methacrylates, and olefins including styrene and its derivatives. U.S. Patent 5,461,125 discloses waterborne core-shell latex polymers useful as adhesive films, rather than super-dispersion stability. The core comprises a (co)polymer comprising a (meth)acrylate ester, while the shell comprises a copolymer, the copolymer comprising (1) a nitrogen-bearing ethylenically-unsaturated free-radically polymerizable monomer, (2) at least one (meth)acrylate ester of about a C, to C, 4 alcohol, and (3) an optional ethylenically-unsaturated free-radically polymerizable silane monomer, wherein the nitrogen-bearing ethylenically-unsaturated free-radically polymerizable monomer comprises about 15 to 60 wt% of the shell and wherein the core comprises about 40 to 85 wt% of the weight of the total core-shell latex particle. The polymers obtained by practicing the teachings of the disclosure have molecular weights of 400,000 or more, and the total low T g component (less than -10°C), where T g is the glass transition temperature, is greater than 60 wt%. U.S. Patent 5,656,071 discloses ink compositions useful for ink-jet applications. These compositions include an insoluble pigment and a polymeric dispersant. In one embodiment, the polymeric dispersant comprises block or graft copolymers comprising a hydrophilic polymeric segment (particularly an acrylate or methacrylate copolymer) .and a hydrophobic polymeric segment which includes a hydrolytically stable siloxyl substituent. Heretofore, ink-jet printers have not had printing performance and durable print properties of competitive printer technologies. The foregoing cited patents do not pro- vide for useful, durable film- forming properties upon removal of the water or solvent. Film durability includes wet and dry rub resista- nce, highlighter smearfastness, lightfast- ness, .and waterfastness (e.g., hot and cold water, under spill, soak, and rub conditions). In particular, formulating an ink-jet ink often involves compromising competing interests. For example, it is possible to enhance one property, such as durable film- forming of the color.ant. However, such enhancement usually results in the degradation of another property, such as printing stability associated in thermal inkjet with resistor fouling or nozzle clogging (kogation or decap - nozzle crusting). Thus, there is a need to provide an improved polymer exhibiting both good dis- persibility in water and durable film- forming properties upon drying. Such polymers are useful in water-based protective coatings, dispersing otherwise non-soluble molecules or aggregates thereof, including pigments and dyes, useful in ink-jet applications. DISCLOSURE OF INVENTION In accordance with the invention, core-shell polymers, or polymers having at least a hydrophobic portion, are provided. The polymers also have either a hydrophilic portion, or, alternatively, one or more surfactants may be employed in conjunction with a given polymer. These polymers provide the combined functionalities of stable water dispersibility over a wide range of operating temperatures and durable film formation at ambient conditions upon drying. Specifically, the polymers function under a wide range of temperatures and ink chemistries typical of thermal ink-jet inks. Furthermore, the polymers provide for dispersing the otherwise non-water-dispersible components, such as colorants, including pigments and dyes. According to the present invention, one or more polymers incorporate the following moieties: [(A) m (B) n (C) p (D) q (E) r ] x (I) wherein A, B, C, D, and E represent functionalities as follows: A = at least one hydrophobic component contributing to improved durable, film-forming properties selected from moieties which, when homo- polymerized to a solid state, have a glass transition temperature (T g ) in the range between -150°C to +25°C; B = at least one hydrophobic and solvent barrier moiety used to adjust the T g of the hydrophobic component of the polymer (I) which, when homo- polymerized to a solid state, has a T g greater than +25°C; C = at least one hydrophilic component, selected from a wide variety of water-soluble monomers (optional); D = at least one UV absorber (optional); E = a moiety having at least one highly polar functional group (optional); m = 5 to 95 wt%; n = 5 to 95 wt%; p = 0 to 60 wt%; q = 0 to 50 wt%; r = 0 to 40 wt%; m + n + p + q + r = 100 wt%; and x = 1 to 100,000. The molecular weight (weight average) of polymer (I) is between about 5,000 and 5,000,000. Either the C moiety or the E moiety must be present in the polymer to provide a polymer having either a hydrophilic portion or a highly polar portion. Alternatively, one or more surfactants may be used in conjunction with polymer (I), whether in the S-JBSTTOTE SHEET (RutE 26) presence or the absence of the C or E, or both, moieties. The surfactant(s) may be anionic, cationic, non-ionic, or zwitterionic. The polymers, alone or with one or more of the surfactants, of the present invention are useful in dispersing a wide variety of otherwise water-insoluble molecules or particles, such as (1) pigments used in printing on various media, including paper, plastic, and cloth and (2) magnetic particles, including those used in printing information on checks. Alternatively, the polymer(s) or polymer/surfactant system(s) are useful as a simple overcoating. Any of the foregoing A, B, C, D, and E moieties may be provided by one or more monomers. Alternatively, any one of the foregoing functionalities may be provided by more than one monomer. In all instances, the A moiety having the low T g confers a film-forming capability to the polymer. The film, after drying, is not capable of being reconstituted by water. The polymers of the invention are prepared by conventional free-radical polym- erization in water. BRIEF DESCRIPTION OF THE DRAWINGS The sole Figure is a schematic diagram of the film- forming, water-dispersive polymer of the present invention. BEST MODES FOR CARRYING OUT THE INVENTION Definitions The following definitions are made: The term "core/shell polymer" means a water-dispersive polymer comprised of a solid hydrophobic core surrounded by (either physically or chemically) a water- soluble shell component. The term "substituted" is meant to include alcohols (OH), esters (COOR), aldehydes (CHO), carboxylic acids (COOH), thiols (SH), amino groups (NH,, NHR, NR 2 ) nitro group (NO,), nitriles (CN), isocyanides (NC), cyanates (CNO), isocyanates (NCO), amido groups, epoxies, halogens, siloxanes, and pyrridinyls. The term "halogen" is meant to include fluorine, chlorine, bromine, and iodine. All concentrations are given in terms of weight percent (wt%), unless otherwise specified. All values of molecular weight of polymers are given in terms of weight average. Monomeric Moieties In accordance with the present invention, core-shell polymers or polymers having a hydrophilic portion and a hydrophobic portion have the following general structure given by formula (I) [(A) m (B) n (C) p (D) q (E) r ] x (I) wherein A, B, C, D, and E are monomers as follows: A = at least one hydrophobic component contributing to improved durable, film-forming properties selected from moieties which, when homo- polymerized to a solid state, have a glass transition temperature (T g ) in the range between -150° and +25°C, preferably -100°C to +10°C, more preferably from -60°C to 0°C; B = at least one hydrophobic and solvent barrier moiety used to adjust the T g of the hydrophobic component of the polymer (I) which, when homo- polymerized to a solid state, has a T g greater than +25°C; C = at least one hydrophilic component, selected from a wide variety of water-soluble monomers (optional); D = at least one UV absorber (optional); E = a moiety having at least one highly polar functional group (optional); m = 5 to 95 wt%; n = 5 to 95 wt%; p = 0 to 60 wt%; q = 0 to 50 wt%; r = 0 to 40 wt%; m + n + p + q + r = 100 wt%; and x = 1 to 100,000. Preferably, the final T g of the polymer(s) (I) is within the range of about -25° to +110°C, more preferably, the final T g is within the range of about -15° to +90°C, and most preferably, the final T g is within the range of -10° to +75°. The molecular weight (weight average) of polymer (I) is between about 1,000 and 2,000,000, preferably between about 5,000 and 500,000, and most preferably between about 10,000 and 70,000. The polymer of the present system is designed to have either hydrophobic and hydrophilic moieties or have only hydrophobic moieties and be associated with one or more surfactants to form a polymer/surfactant system. Thus, the polymer or polymer/surfactant system is both (1) water-dispersible, and includes water-soluble polar groups, which are present in sufficient quantity to suspend a pigment particle, and (2) hydrophobic, with a substantial fraction of the polymer containing hydrophobic moieties that are either highly water-resistant or even water-insoluble. The hydrophobic A moiety allows the polymer (I) to have a sufficiently low T„ to permit formation of a film with other polymer molecules containing the A moiety. The film formation results upon drying (removal of water). The hydrophobic B moiety in combination with the hydrophobic A moiety provide the polymer with resistance to environmental solvents, such as water and those found in highlighter pens. Additional environmental solvents can be found in rain, coffee, soda pop, body oils, soils, hot water, etc. The hydrophilic C moiety may be provided in the polymer itself, as shown in formula (I). At least one C moiety may be present, and is water-soluble. If present, such water-soluble moieties comprise an ionic or non-ionic shell of the core-shell polymer. Alternatively, the C moiety may be provided by one or more surfactants, to form a polymer/surfactant system. Any of the ionic (anionic and cationic), non-ionic, and zwitterionic (amphoteric) surfactants may be employed. A representative listing of applicable surfactant can be found in McCutcheon's Emulsifiers and Detergents, North American Edition, 1997, McCutcheon's Division, MC Publishing Co. 175 Rock road, Glen Rock, NJ 07452 USA. Examples of surfactants that may be benefi- SUBST1TUTESHEET (RULE 26) cially employed in the practice of the present invention include: TERGITOLs, which are polyethylene or polypropylene oxide ethers; alkyl phenyl polyethylene oxides available under the tradenane TRITONs; BRIJs, which are polyethylene or polypropylene oxide ethers; PLURONICs, which are also polyethylene/polypropylene oxide copolymers from BASF; and the SURFYNOLs, which are acetylenic ethoxylated diols; polyethylene oxide (POE) esters; POE diesters; POE amines; protonated POE amines; POE amides; the polypropylene analogs of the foregoing POE compounds; dimethicone copolyols; quaternary ammonium compounds; AEROSOLS, including sulfosuccinates; ethoxylates, amine oxides, and betaines. Preferred examples of non-ionic surfactants include, but are not limited to, BRIJs, which are polyethylene oxide ethers, available from ICI Surfactants (specific examples include the following BRIJs: 30, 35, 52, 56, 58, 72, 76, 78, 92, 97, and 98); TWEENs, which are derivatives of polyethylene oxides, available from ICI Surfactants (specific examples include the following TWEENs: 20, 40, 60, 80, and 85); SOLSPERSE 27,000, which is an aromatic ethoxylate, available from Zeneca; SPAN 85, which is available from Air Products; and SURFYNOLs, which are acetylenic ethylene oxides available from Air Products. Examples of anionic surfactants include AEROSOL DPOS 45, which is a sulfate, available from Cytec Industries; sodium oc- tadecyl sulfonate; dioctyl ester of sodium sulfosuccinic acid; AEROSOL OT 100%, which is a sulfate, available from American Cyanamid; and sodium lauryl sulfonate. If used, the amount of surfactant ranges from about 0.001 to 30 wt%, and the balance the polymer. Optionally, one or more UV absorber moieties D may be present. The UV absorber contains a UV blocking chromophore, which imparts lightfastness to the poly- mer (I). Also optionally, one or more ionic water-soluble, dispersible moieties E may be present. If present, such water-soluble moieties comprise an ionic shell of the core- shell polymer. One monomer may be employed to provide one or more of the foregoing functions. Alternatively, one function may be provided by one or more of the forego- ing moieties. However, in many instances, a single monomer provides a single function. Typically, the polymer(s) of the present invention is prepared by emulsifying the monomeric components, and then conducting a free-radical polymerization in water. Free-radical polymerization involves employing a free-radical initiator. A concentration of about 0.001 to 10 wt% of the initiator is employed in the total monomer system. Examples of suitable free-radical initiators include, but are not limited to, ammonium persulfate, potassium persulfate, hydrogen peroxide, benzoyl peroxide, azobisisobutyronitrile, TRIGONOX 21, and PERKADOX 16. Preferably, the result- ing polymer (I) is a random polymer. One skilled in this art would understand that the polymer(s) can also be prepared by conventional condensation techniques. Once a film is formed from the polymer and water is removed, as by dehydration under ambient conditions, the film is essentially impervious to water, and the polymer is not capable of being redispersed with water. If the polymer or polymer/surfactant system is associated with pigment particles, and the pigment with polymer or polymer/surfactant system is deposited on a surface, such as paper, then the pigment particles are trapped within or beneath the film on the surface, and are thus protected from the effects of water and environmental solvents. The sole Figure illustrates a molecule of polymer (I), containing all five moei- ties (A, B, C, D, and E). Moieties A and B form a solid core. The C moiety forms a non-ionic, water-soluble shell. The D moiety is a UV absorber. The E moiety forms an ionic, water-soluble or water-insoluble shell. As stated above, the A moiety is a hydrophobic component for controlling solubility in organic solvents selected from monomer(s) that form homopolyers having a T_ in the range between -150° and +25°C. The A moiety is preferably selected from ethylenically-substituted compounds given by (A): C(R,)(R 2 )=C(R 3 )R R 5 R 6 (A) where R, and R 2 are independently hydrogen, halogen, alkyl, aryl, or substituted alkyl or aryl, or vinyl butyral, R 3 is hydrogen, halogen, saturated or unsaturated alkyl, alkoxy, aryl, or substituted alkyl, alkoxy, or aryl, R 4 is direct bond, O, CO, NH, halogen, saturated or unsaturated alkyl, aryl, or substituted alkyl, aryl, or CN, R 5 is absent (if R 4 is alkyl, aryl, or substituted alkyl or aryl), direct bond, hydrogen, NH, O, alkyl, alkylene, aryl, or substituted alkyl, alkylene, or aryl, and R 6 is absent (if R 4 is alkyl, aryl, or substituted alkyl or aryl or if R 5 is hydro- gen, alkyl, aryl, or substituted alkyl or aryl), NH 2 , saturated or unsaturated alkyl, alkoxy, aryl. aroxy, or substituted alkyl or aryl. The alkyl, alkoxy, alkylene, and aryl chains each contain more than one carbon atom and less than 40 carbon atoms. Preferably, the R 4 functionality is an electron acceptor moiety. One preferred embodiment of formula (A) is the following general structure (Al): R\ (Al) CH 2 =C C=0 where R\ = H. halogen, alkyl, aryl or substituted alkyl or aryl; R ' j = direct bond, O, or NH; and R ' 0 = alkyl, substituted alkyl, alkylaryl or substituted alkylaryl and aralkyl in which the length of alkyl, alkylaryl or aralkyl chain is given as the number of C atoms between 2 and 40; and alkyl or aryl siloxanes. Examples for structure (Al) include, but are not limited to: (Al-1) ethyl acrylate; (Al-2) ethyl methacrylate; (Al-3) benzyl acrylate; (Al -4) benzyl methacrylate; (Al-5) propyl acrylate; (Al-6) propyl methacrylate; (A 1-7) iso-propyl acrylate; (Al-8) iso-propyl methacrylate; (Al -9) butyl acrylate; (Al-10) butyl methacrylate; (Al-11) hexyl acrylate; (Al-12) hexyl methacrylate; (Al-13) octadecyl methacrylate; (Al- 14) octadecyl acrylate; (Al-15) lauryl methacrylate; (Al-16) lauryl acrylate; (Al-17) hydroxyethyl acrylate; (Al-18) hydroxyethyl methacrylate; (Al-19) hydroxyhexyl acrylate; (Al-20) hydroxyhexyl methacrylate; (A 1-21) hydroxyoctadecyl acrylate; (Al-22) hydroxyoctadecyl methacrylate; (Al-23) hydroxylauryl methacrylate; (A 1-24) hydroxylauryl acrylate; (Al-25) phenethyl acrylate; (Al-26) phenethyl methacrylate; (Al-27) 6-phenylhexyl acrylate; (A 1-28) 6-phenylhexyl methacrylate; (Al -29) phenyllauryl acrylate; (Al-30) phenyllauryl methacrylate; (Al-31) 3-nitrophenyl-6-hexyl methacrylate; (Al-32) 3-nitrophenyl-18-octadecyl acrylate; (Al-33) ethyleneglycol dicyclopentyl ether acrylate; (Al-34) vinyl ethyl ketone; (Al-35) vinyl propyl ketone; (Al-36) vinyl hexyl ketone; (Al-37) vinyl octyl ketone; (A 1-38) vinyl butyl ketone; (Al -39) cyclohexyl acrylate; (Al -40) 3-methacryloxypropyldimethylmethoxysilane; (Al-41) 3-methacryloxypropylmethyldimethoxysilane; (Al-42) 3-methacryloxypropylpentamethyldisiloxane; (Al -43) 3-methacryloxypropyltris(trimethylsiloxy)silane; (A 1-44) 3-acryloxypropyldimethylmethoxysilane; (Al-45) acryloxypropylmethyldimethoxysilane; (Al-46) trifluoromethyl styrene; (Al-47) trifluoromethyl acrylate; (A 1-48) trifluoromethyl methacrylate; (A 1 -49) tetrafluoropropyl acrylate ; (Al-50) tetrafluoropropyl methacrylate; (Al-51) heptafluorobutyl methacrylate; (Al-52) iso-butyl acrylate; (Al-53) iso-butyl methacrylate; (A 1 -54) 2-ethylhexyl acrylate; (Al-55) 2-ethylhexyl methacrylate; (Al-56) iso-octyl acrylate; and (A 1-57) iso-octyl methacrylate. Another preferred embodiment for formula (A) is the following general struc- ture (A2): R\ CH 2 =C I C=O (A2) N Λ R 7 R 8 where R' 3 = same definition as that of structure (Al) above; and R 7 = R 8 = same or different combinations of R' 6 in structure (Al) above. An example for structure (A2) includes, but is not limited to: (A2- 1 ) N,N-dihexyl acrylamide; and (A2-2) N,N-dioctyl acrylamide. Yet another preferred embodiment for formula (A) is the following general structure (A3): I CH 2 =C C=O (A3) I R' 5 R' 6 N Λ R, R 10 where R' 3 = same definition as that of structure (Al); R' 5 = same definition as that of structure (Al); R' 6 = alkylene, arylene, substituted alkylene or arylene; and R j and R 10 are independently selected from H, alkyl, substituted alkyl, alkylaryl or substituted alkylaryl in which the length of alkyl and alkylaryl chains each comprise between 2 and 40 C atoms. Alternatively, R, and R 10 together may form a 5- or 6-mem-bered ring. Examples for structure (A3) include, but are not limited to: (A3-1) aminoethyl acrylate; (A3-2) aminopropyl acrylate; (A3-3) aminopropyl methacrylate; (A3-4) aminoisopropyl acrylate; (A3-5) aminoisopropyl methacrylate; (A3-6) aminobutyl acrylate; (A3-7) aminobutyl methacrylate; (A3-8) aminohexyl acrylate; (A3-9) aminohexyl methacrylate; (A3 -10) aminooctadecyl methacrylate; (A3-11) aminooctadecyl acrylate; (A3- 12) aminolauryl methacrylate; (A3- 13) aminolauryl acrylate; (A3-14) N,N-dimethylaminoethyl acrylate; (A3-15) N,N-dimethylaminoethyl methacrylate; (A3- 16) N,N-diethylaminoethyl acrylate; (A3-17) N,N-diethylaminoethyl methacrylate; and (A3 -18) piperidino-N-ethyl acrylate. Still another preferred embodiment for formula (A) is the following general structure (A4): I CH,=C I O (A4) R ' 6 where: R' 3 = H, halogen, alkyl, aryl, sustituted alkyl or aryl; R' 5 = direct bond, CO, alkylene, arylene, substituted alkylene or arylene; and R' 6 = alkyl, aryl, substituted alkyl or aryl. Examples for structure (A4) include, but are not limited to: (A4-1) vinyl propionate; (A4-2) vinyl acetate; (A4-3) vinyl butyrate; (A4-4) vinyl butyl ether; and (A4-4) vinyl propyl ether. As stated above, the B moiety is hydrophobic and is a solvent barrier composed of monomer(s) that form homopolymers having a T g greater than 25°C. The B moiety has the general structure given by formula (B) CRιR 2 — C(R 3 )R 4 R 5 R 6 (B) where R, and R, are independently hydrogen, halogen, or vinyl butyral, R 3 is hydrogen, halogen, saturated or unsaturated alkyl, alkoxy, aryl, or substituted alkyl, alkoxy, or aryl, R" 4 is direct bond, O, CO, NH, halogen, saturated or unsaturated alkyl, aryl, or substituted alkyl, aryl, or CN, R" 5 is absent (if R 4 is alkyl, aryl, or substituted alkyl or aryl), direct bond, hydrogen, NH, O, alkyl, alkylene, aryl, or substituted alkyl, alkylene, or aryl, and R" 6 is absent (if R 4 is alkyl, aryl, or substituted alkyl or aryl or if R 5 is hydrogen, alkyl, aryl, or substituted alkyl or aryl), NH 2 , saturated or unsaturated alkyl, alk- oxy, aryl, aroxy, or substituted alkyl or aryl. The alkyl, alkoxy, alkylene, aryl, aroxy chains each contain from 1 to 40 carbon atoms. Additionally, R, and R, and R, and R 3 can each form a ring; one example of a ring compound so formed includes, but is not limited to, polyvinyl butryal. Further, R" and R 5 can form a ring through either nitrogen or oxygen. Formula (B) is seen to be the same as formula (A), but with some differences in the substituent groups, which provide a homopolymer of these monomers with the higher T g of at least 25°C. One preferred embodiment of formula (B) is the following general structure (Bl): CH,=CR"',R"\ (Bl) where R'" 5 = hydrogen, alkyl, alkoxy, aryl or halogen; and R'" 6 = H, aryl, alkyl (with one carbon atom), amino, ester, epoxy component containing groups, and fluoroalkyl derivatives. Examples for formula (Bl) include, but are not limited to; (B 1-1) ethylene; (B 1-2) styrene; (B 1 -3) vinyl carbazole; (Bl-4) vinyl naphthalalene; (Bl-5) vinyl anthracene; (Bl-6) vinyl pyrene; (Bl-7) methyl methacrylate; (B 1 -8) methyl acrylate; (B l-9) alpha-methyl styrene; (Bl-10) dimethylstyrene; (Bl-1 1) methylstyrene; (Bl-12) vinylbiphenyl; (B 1-13) glycidyl acrylate; (Bl-14) glycidyl methacrylate; (Bl-15) glycidyl propylene; (Bl-16) 2-methyl-2-vinyl oxirane; (Bl-17) vinyl pyrridine; (B 1 - 18) aminoethyl methacrylate; and (Bl-19) aminoethylphenyl acrylate. Another preferred embodiment of formula (B) is the following general structure (B2): 10 where R 14 and R 15 are independently selected from H, halogen, alkyl, aryl, substituted alkyl and aryl; alternatively, R 14 and R 15 are in the form of a closed ring; and R 16 is H, halogen, alkyl, aryl, substituted alkyl or aryl, or unsaturated alkyl. Examples for formula (B2) include, but are not limited to: (B2-1) maleimide; (B2-2) N-phenyl maleimide; (B2-3) N-hexyl maleimide; (B2-4) N-vinylphthalimide; and (B2-5) N-vinyl maleimide. As stated above, the C moiety is an optional hydrophilic component. The C moiety is selected from a wide variety of monomers such as poly(ethylene glycol) units having general formula (CI), vinyl pyrrolidones having general formula (C2), vinyl imidazoles having general formula (C3) and acrylamides having general formula (C4), all of which polymerize to form water-soluble polymers. The general structure of formula (CI) is where R, = H, halogen, alkyl, aryl, or substituted alkyl or aryl; R 2 = direct bond, O, CO, NH, or CONH; R 3 = OH, (CH 2 CH 2 O) y R 4 , (CH 2 CH(CH 3 )O) y R 4 or (CH 2 CH(C 2 H 5 )O) y R 4 or the thioether analogs: SH, (CH 2 CH 2 S) y R 4 , (CH 2 CH(CH 3 )S) y R 4 or (CH 2 CH(C 2 H 5 )S) y R 4 ; y = 1 to 200; and R 4 = alkyl, aryl, substituted alkyl or aryl. Examples for general structure (CI) include, but are not limited to: (C 1 - 1 ) poly(ethylene glycol) methyl ether acrylate of average molecular weight 404; (Cl-2) poly(ethylene glycol) methyl ether methacrylate of average molecular weight 418; (Cl-3) poly(ethylene glycol) methyl ether methacrylate of average molecular weight 2068; (Cl-4) poly(ethylene glycol) methyl ether acrylate of average molecular weight 2054; and (Cl-5) polyvinyl alcohol. The general structure of formula (C2) is where R, and R, are independently selected from -H, halogen, alkyl, aryl, and substituted alkyl and aryl. Examples for general structure (C2) include, but are not limited to: (C2-1) vinyl pyrrolidone; (C2-2) vinyl 4-methylpyrrolidone; and (C2-3) vinyl 4-phenylpyrrolidone. The general structure of formula (C3) is where R, and R 2 are independently selected from H, halogen, alkyl, aryl, and substituted alkyl and aryl. Examples for general structure (C3) include, but are not limited to: (C3-1) vinyl imidazole; (C3-2) vinyl 4-methylimidazole; and (C3-3) vinyl 4-phenylimidazole. The general structure of formula (C4) is where R, is H, halogen, alkyl, aryl or substituted alkyl or aryl; and R, and R 3 are independently selected from H, alkyl, aryl and substituted alkyl and aryl; alternatively, R 2 and R 3 can form a ring, either aliphatic or aromatic. Examples for the general structure (C4) include, but are not limited to: (C4-1) acrylamide; (C4-2) methacrylamide; (C4-3) N,N-dimethyl acrylamide; (C4-4) N-methyl acrylamide; (C4-5) N-methyl methacrylamide; (C4-6) aryloxy piperidine; and (C4-7) N,N-diethyl acrylamide. As stated above, the D moiety is a UV absorber composed of monomer(s) having the general structure of formula (D) (11) Rt= H, Alkyl, aryl, substituted alkyl or aryl As stated above, the E moiety is a highly polar functional group composed of moieties having the general structure given by formulae (El) to (ElO). The general structure of formula (El) is CH(R,) = C(R,)R 3 COOH (El) where R, = H, COOH, COOR 4 ; R, = H, halogen, alkyl, aryl, alkoxyl, or substituted alkyl, aryl or alkoxyl; R 3 = direct bond, alkylene, arylene or sustituted alkylene or arylene; and R 4 = alkyl, aryl, substituted alkyl or aryl. Examples for structure (El) include, but are not limited to: (El-1) acrylic acid; (El -2) methacrylic acid; (El -3) chloromethacrylic acid; and (El -4) maleic acid. The general structure of formula (E2) is CH, = CHR.NR,R 3 (E2) where R, = alkylene, arylene, substituted alkylene, arylene, or -SO 2 ; and R, and R 3 are independently selected from H, alkyl, aryl, or substituted alkyl, aryl or alkoxyl; alternatively, R 2 and R 3 can be combined to form a ring, either aliphatic or aromatic. Examples for structure (E2) include, but are not limited to: (E2-1) allylamine; (E2-2) N,N-diethylallylamine; (E2-3) vinyl sulfonamide; and (E2-4) acrylamide. The general structure of formula (E3) is y (CH 2 =CHR, COO " ) W (E3) where R, = alkylene, arylene, substituted alkylene or arylene; y = 1 to 4; and M • ~ = NH 4 ~ , Li", Na " , IC, Ca 2* , Mg 2τ , Al 3" , Ti τ , triethylammonium, dieth- ylammonium, pyrridinium, etc. Examples for structure (E3) include, but are not limited to: (E3-1) sodium acrylate; (E3-2) sodium methacrylate; (E3-3) ammonium acrylate; and (E3-4) ammonium methacrylate. The general structure of formula (E4) is R, (E4) where R ] = alkylene, arylene, substituted alkylene or arylene, COO, or cyclic ring containing nitrogen; R 2 , R 3 , and R 4 are independently selected from H, alkyl, aryl, alkoxyl, or substituted alkyl, aryl or alkoxyl; z = 1 to 4; and X = halogen, BF 4 , PF 6 , ClO 4 , SCN, CNO, CNS. Examples for general structure (E4) include, but are not limited to: (E4-1) acrylamidopropanetriethylammonium chloride; (E4-2) methacrylamidopropanetriethylammonium chloride; and (E4-3) vinylpyridine hydrochloride. The general structure of formula (E5) is z CH 2 =C I o=p=o I ° " M (E5) where R, = H, alkyl, aryl, alkoxyl, substituted alkyl, aryl or alkoxyl; R 2 = direct bond, alkylene, arylene or substituted alkylene or arylene; z = 1 to 4; and M zτ = NH 4 + , Li + , Na + , K + , Ca 2+ , Mg 2+ , Al 3+ , Ti 4+ , triethylammonium, dieth- ylammonium, pyrridinium, etc. Examples for the general structure (E5) include, but are not limited to: (E5-1) sodium vinyl phosphonate; and (E5-2) sodium 1-methylvinylphosphonate. The general structure of formula (E6) is where R, ^ = H, alkyl, aryl, alkoxyl, substituted alkyl, aryl or alkoxyl; R 2 = direct bond, -COOR 3 , arylene, alkylene, or -CONHR 3 ; R 3 = alkylene, arylene, substituted alkylene or arylene, or fluoroalkylene; z = 1 to 4; and M z~ = NH , Li + , Na * , K + , Ca 2+ , Mg 2+ , Al 3 \ Ti 4" , etc. Examples for the general structure (E6) include, but are not limited to: (E6-1) sodium vinyl sulfonate; (E6-2) sodium 1-methylvinylsulfonate; (E6-3) sodium styrenesulfonate; (E6-4) sodium acrylamidopropanesulfonate; (E6-5) sodium methacrylamidopropanesulfonate; and (E6-6) sodium vinyl morpholine sulfonate. Additional E moieties include the following salts: (E7) sulfonium salts; (E8) carbonium salts; (E9) pymlinium salt and thio pymlinium salt; and (ElO) tetrazolium salt. The sulfonium salts have the following structure (E7): R, R. (E7) where R ; = H, halogen, alkyl, or aryl; R 2 = CO, O; R 3 = direct bond, NH; R 4 = alkyl or aryl; and X = CI, Br, BF 4 , ClO 4 , 1, or NO 3 . The carbonium salts have the following structure (E8): R 3 I CH,=C I R 3 R -C + -R 5 X " SUBSTITLΠΈ SHEET (RULE 26) where R, = H, halogen, alkyl, or aryl; R, = CO, O; R 3 = direct bond, NH, alkylene, or arylene; R 4 and R 5 are independently selected from alkyl or aryl; and The pyrrilinium and thiopyrrilinium salts have the following structure (E9): R, where Y = O or S; R, = H, halogen, alkyl, or aryl; R 2 = CO, O; R 3 = direct bond, NH, alkylene, or arylene; X = CI, Br, I, ClO 4 , BF 4 , etc. Polymers Polymers that fall within the scope of the formula (I) include, but are not limited to, the following examples, which may be characterized as A-B-C or A-B-C-D polymers: (1) (hexyl acrylate) 40 (methyl methacrylate) 40 (poly(ethylene glycol) methyl ether acrylate, mw=404) 20 (2) (hexyl acrylate) 30 (methyl methacrylate) 50 (poly(ethylene glycol) methyl ether acrylate, mw=404) 20 (3) (hexyl acrylate) 20 (methyl methacrylate) 60 (poly (ethylene glycol) methyl ether acrylate, mw=404) 20 (4) (hexyl acrylate) 40 (methyl methacrylate) 40 (poly(ethylene glycol) methyl ether acrylate, mw=2054) 20 (5) (hexyl acrylate) 30 (methyl methacrylate) 50 (poly(ethylene glycol) methyl ether acrylate, mw=2054) 20 (6) (hexyl acrylate) 20 (methyl methacrylate) 60 (poly(ethylene glycol) methyl ether acrylate, mw=2054) 20 (7) (hexyl acrylate) 40 (methyl methacrylate) 40 (poly(ethylene glycol) methyl ether acrylate, mw=218) 20 (8) (hexyl acrylate) 30 (methyl methacrylate) 50 (poly(ethylene glycol) methyl ether acrylate, mw=218) 20 (9) (hexyl acrylate) 20 (methyl methacrylate) 60 (poly(ethylene glycol) methyl ether acrylate, mw-=218) 20 (10) (ethyl acrylate) 40 (methyl methacrylate) 40 (poly( ethylene glycol) methyl ether acrylate, mw=404) 20 (11) (propyl acrylate) 40 (methyl methacrylate) 40 (poly(ethylene glycol) methyl ether acrylate, mw=404) 20 (12) (butyl acrylate) 40 (methyl methacrylate) 40 (poly(ethylene glycol) methyl ether acrylate, mw=404) 20 (13) (octadecyl acrylate) 40 (methyl methacrylate) 40 (poly(ethylene glycol) 4 methyl ether acrylate, mw=404) 20 (14) (lauryl methacrylate) 40 (methyl methacrylate) 40 (poly(ethylene glycol) methyl ether acrylate, mw=404) 20 (15) (octadecyl methacrylate) 0 (methyl methacrylate) 40 (poly(ethylene glycol) methyl ether acrylate, mw=404) 20 (16) (hydroxyoctadecyl acrylate) 0 (methyl methacrylate) 0 (poly(ethylene glycol) methyl ether acrylate, mw=404) 20 (17) (hydroxyethyl acrylate) 40 (methyl methacrylate) 40 (poly(ethylene glycol) methyl ether acrylate, mw=404) 20 (18) (hydroxylauryl methacrylate) 40 (methyl methacrylate) 40 (poly(ethylene glycol) methyl ether acrylate, mw=404) 20 (19) (phenethyl acrylate) 40 (methyl methacrylate) 40 (poly(ethylene glycol) methyl ether acrylate, mw=404) 20 (20) (6-phenylhexyl acrylate) 40 (methyl methacrylate) 40 (poly(ethylene glycol) methyl ether acrylate, mw=404) 20 (21) (cyclohexyl acrylate) 40 (methyl methacrylate) 40 (poly(ethylene glycol) methyl ether acrylate, mw=404) 20 (22) (acryloxypropylmethyldimethoxysilane) 30 (methyl methacrylate) 50 (poly(ethylene glycol) methyl ether acrylate, mw=404) 20 (23) (N,N-dihexyl acrylamide) 20 (methyl methacrylate) 60 (poly(ethylene glycol) methyl ether acrylate, mw=404) 20 (24) (aminopropyl acrylate) 40 (methyl methacrylate) 40 (poly(ethylene glycol) methyl ether acrylate, mw=2054) 20 (25) (aminohexyl acrylate) 30 (methyl methacrylate) 50 (poly(ethylene glycol) methyl ether acrylate, mw=2054) 20 (26) (aminolauryl methacrylate) 20 (methyl methacrylate) 60 (poly(ethylene glycol) methyl ether acrylate, mw=2054) 20 (27) (N,N-dimethylaminoethyl acrylate) 40 (methyl methacrylate) 40 (poly- (ethylene glycol) methyl ether acrylate, mw=218) 20 (28) (vinyl acetate) 30 (methyl methacrylate) 50 (poly(ethylene glycol) methyl ether acrylate, mw=218) 20 (29) (vinyl butyl ether) 20 (methyl methacrylate) 60 (poly(ethylene glycol) methyl ether acrylate, mw=218) 20 (30) (hexyl acrylate) 40 (styrene) 40 (poly(ethylene glycol) methyl ether acrylate, mw=404) 20 (31) (hexyl acrylate) 30 (dimethyl styrene) 50 (poly(ethylene glycol) methyl ether acrylate, mw=404) 20 (32) (hexyl acrylate) 20 (trifluoromethyl styrene) 60 (poly(ethylene glycol) methyl ether acrylate, mw=404) 20 (33) (hexyl acrylate) 40 (tetrafluoropropyl methacrylate) 40 (polyethylene glycol) methyl ether acrylate, mw=2054) 20 (34) (hexyl acrylate) 30 (glycidyl methacrylate) 50 (poly(ethylene glycol) methyl ether acrylate, mw=2054) 20 (35) (hexyl acrylate) 20 (glycidyl acrylate) 60 (poly(ethylene glycol) methyl ether acrylate, mw=2054) 20 (36) (hexyl acrylate) 40 (maleimide) 40 (poly(ethylene glycol) methyl ether ac- rylate, mw=218) 20 (37) (hexyl acrylate) 50 (n-hexyl maleimide) 30 (poly(ethylene glycol) methyl ether acrylate, mw=218) 20 (38) (hexyl acrylate) 40 (n-vinyl maleimide) 40 (poly(ethylene glycol) methyl ether acrylate, mw=218) 20 (39) (hexyl acrylate) 40 (methyl methacrylate) 40 (vinyl pyrrolidone) 20 (40) (hexyl acrylate) 40 (methyl methacrylate) 40 (vinyl 4-methylpyrrolidone) 20 (41) (hexyl acrylate) 40 (methyl methacrylate) 40 (vinyl imidazole) 20 (42) (hexyl acrylate) 40 (methyl methacrylate) 40 (acrylamide) 20 (43) (hexyl acrylate) 40 (methyl methacrylate) 40 (4-methyl acrylamide) 20 (44) (hexyl acrylate) 40 (methyl methacrylate) 30 (dl) 10 (poly(ethylene glycol) methyl ether acrylate, mw=404), 0 (45) (hexyl acrylate) 40 (methyl methacrylate) 30 (dl) 10 (poly( ethylene glycol) methyl ether acrylate, mw=404) 20 , where, referring to the D moiety, R 1 = H, R 2 = O, and R 3 = Dl (46) (hexyl acrylate) 0 (methyl methacrylate) 30 (dl) 10 (poly(ethylene glycol) methyl ether acrylate, mw=404) 20 , where, referring to the D moiety, R 1 = H, R 2 = O, and R 3 = Dl (47) (hexyl acrylate) 40 (methyl methacrylate) 30 (dl) 10 (poly(ethylene glycol) methyl ether acrylate, mw=404) 20 , where, referring to the D moiety, R 1 = H, R 2 = O, and R 3 = Dl (48) (hexyl acrylate) 40 (methyl methacrylate) 3O (d4) I0 (poly(ethylene glycol) methyl ether acrylate, mw=404) 20 , where, referring to the D moiety, R 1 = H, R 2 = O, and R 3 = D4 (49) (hexyl acrylate) 40 (methyl methacrylate) 30 (d4) 10 (poly(ethylene glycol) methyl ether acrylate, mw=404) 20 , where, referring to the D moiety, R 1 = H, R 2 = O, and R 3 = D4 (50) (hexyl acrylate) 40 (styrene) 30 (dl) 10 (poly(ethylene glycol) methyl ether acrylate, mw=404) 20 , where, referring to the D moiety, R 1 = H, R 2 = O, and R 3 = Dl (51) (hexyl acrylate) 40 (styrene) 30 (dl) 10 (vinyl pyrrolidone) 20 , where, refer- ring to the D moiety, R 1 = H, R 2 = O, and R 3 = Dl (52) (hexyl acrylate) 50 (methyl methacrylate) 45 (poly(ethylene glycol) methyl ether acrylate, mw=404) 5 (53) (hexyl acrylate) 50 (methyl methacrylate) 40 (poly(ethylene glycol) methyl ether acrylate, mw=404) 10 (54) (hexyl acrylate) 50 (methyl methacrylate) 35 (poly( ethylene glycol) methyl ether acrylate, mw=404) 15 (55) (methyl methacrylate) 40 (hexyl acrylate) 60 / surfactant (56) (methyl methacrylate) 40 (butyl acrylate)^ / surfactant (57) (styrene) 30 (octadecyl acrylate) 70 / surfactant Polymers that fall within the scope of the formula (I) include, but are not limited to, the following examples, which may be characterized as A-B-E polymers: (58) (hexyl acrylate) 40 (methyl methacrylate) 40 (acrylic acid), 0 (59) (hexyl acrylate) 60 (methyl methacrylate) 20 (methacrylic acid) 20 (60) (hexyl acrylate) 40 (methyl methacrylate) 0 (maleic acid) 20 (61) (hexyl acrylate) 40 (methyl methacrylate) 0 (vinyl benzoic acid) 20 (62) (hexyl acrylate) 40 (methyl methacrylate) 40 (vinyl sulfonamide) 20 (63) (hexyl acrylate) 40 (methyl methacrylate) 40 (sodium acrylate) 20 (64) (hexyl acrylate) 40 (methyl methacrylate) 40 (ammonium acrylate) 20 (65) (hexyl acrylate) 0 (methyl methacrylate) 40 (ammonium methacrylate), 0 (66) (ethyl acrylate) 40 (methyl methacrylate) 40 (acrylamidopropanetriethyl- ammonium chloride) 20 (67) (propyl acrylate) 40 (methyl methacrylate) 40 (vinyl pyridine hydrochlo- ride) 20 (68) (butyl acrylate) 40 (methyl methacrylate) 40 (sodium vinyl phosphate) 20 (69) (hexyl acrylate) 40 (methyl methacrylate) 40 (sodium styrene sulfonate) 20 (70) (hexyl acrylate) 30 (methyl methacrylate) 50 (sodium acrylamidopropane- sulfonate) 20 (71) (styrene) 75 (acrylic acid) 20 (dl) 5 , where, referring to the D moiety, R 1 = H, R 2 = O, and R 3 = Dl (72) (styrene) 55 (acrylic acid) 40 (d4) 5 , where, referring to the D moiety, R 1 = H, R 2 = O, and R 3 = D4 (73) (styrene) 40 (methyl methacrylate) 40 (acrylic acid) 20 (74) (ethyl acrylate) 55 (acrylic acid) 40 (dl) 5 , where, referring to the D moiety, R' = H, R 2 = O, and R 3 = Dl (75) (styrene) 40 (ethyl acrylate) 0 (acrylic acid) 20 (76) (methyl methacrylate) 40 (hexyl acrylate) 55 (dl) 5 , where, referring to the D moiety, R 1 = H, R 2 = O, and R 3 - Dl (77) (methyl methacrylate) 40 (butyl acrylate) 55 (dl) 5 , where, referring to the D moiety, R 1 = H, R 2 = O, and R 3 = D 1 (78) (styrene) 30 (octadecyl acrylate) 65 (dl) 5 , where, referring to the D moiety, R' = H, R 2 = O, and R 3 = Dl (79) (methyl methacrylate) 32 (hexyl acrylate) 46 (poly(ethylene glycol) methyl ether acrylate, mw=404) 12 (acrylic acid) 10 The foregoing polymers are useful in encapsulating or forming a film or matrix with or covering or surrounding pigments or dyes and rendering them soluble or dis- persible in water. EXAMPLES In the following examples, most of the monomers used were commercially available. The purity of such monomers is that found in normal commercial practice. Only the poly(ethylene glycol) methyl ether acrylate monomers of different molecular weights were prepared from the corresponding alcohol with acryloyl chloride in the presence of triethylamine by standard esterification process. Other monomers can be prepared by following conventional and well-known procedures of typical organic re- actions. Example 1. (Hexyl Acrylate) 10 (Methyl Methacrylate) 30 (Vinylpyrrolidone) 59 (Dl),. Synthesis of core-shell polymer with hexyl acrylate (A), methyl methacrylate (MMA) (B), vinylpyrrolidone (C), and UV stabilizer (Dl) (D) in the ratio of 10, 30, 59, and 1% by weight, respectively: Hexyl acrylate (8 g), MMA (24 g), vinylpyrrolidone (47.2 g) and UV stabilizer Dl(0.8 g) were mixed with BRIJ 92 (0.8 g), SOLSPERSE 27,000 (0.82 g), and isooctyhnercaptopropionate (0.8 g) in water (12 g) to form an emulsion. The emulsion was saturated with nitrogen. Then the emulsion was added over a period of 1 hour to a solution of potassium persulfate (1.71 g) in water (703.09 g) at 80°C. The reaction mixture was maintained at 80°C for 2.5 hour. The reaction mixture was then cooled to obtain the title polymer dispersed in water. The average particle size of the polymer solution was found to be 250 nm and the glass transition temperatures (T g ) of the polymer obtained were -10°C .and 65°C. Example 2. (Hexyl Acrylate) 30 (Methyl Methacrylate) 40 (Acrylamide) 30 . Synthesis of core-shell polymer derived from hexyl acrylate (A), MMA (B), and acrylamide (E) in the ratio of 30, 40, and 30% by weight, respectively: The monomers, hexyl acrylate (3 g), MMA (4 g), and acrylamide (3 g) were mixed in water (7 g) containing BRIJ 92 (0.22 g), Aerosol DPOS 45 (0.22 g), and isooctyhnercaptopropionate (0.22 g) to form an emulsion. The emulsion was saturated with nitrogen and added dropwise to a solution of potassium persulfate (0.2 g) in water (82.14 g) at 100°C. Heating was continued for a period of 4 hours and cooled to obtain the title core-shell polymer. The average particle size of the polymer solution was found to be 200 nm and the glass transition temperatures (T g ) of the polymer obtained were -10°C and 125°C. Example 3. (Lauryl Methacrylate) 10 (Methyl Methacrylate) 20 (Vinylpyrrolidone) 66 (Dl), (Sodium Styrene Sulfonate)-,. Synthesis of core-shell polymer derived from lauryl methacrylate (A), MMA (B), vinylpyrrolidone (C), UV stabilizer (Dl) (D), and sodium styrene sulfonate (E) in the ratio of 10, 20, 67, 1, .and 3% by weight, respectively: The monomers, lauryl methacrylate (8 g), MMA (16 g), vinylpyrrolidone (52.8 g), UV stabilizer (Dl) (0.8 g), and a solution of sodium styrene sulfonate (2.4 g) in water (15 g) were mixed. To this mixture were added BRIJ 92 (0.81 g) and SOLSPERSE 27,000 (0.81 g). The chain transfer agent isooctyl-3-mercaptopro-pionate (0.82 g) was subsequently added. The mixture was shaken vigorously for 3 min, followed by sonication for 3 min to form an emulsion. The emulsion was saturated with nitrogen for 0.5 hr. Meanwhile, a solution of potassium persulfate (1.71 g) in water (700.85 g) was prepared in a three-necked 500 ml round bottom flask and saturated with nitrogen. The persulfate solution was heated to 75°C. The emulsion was added dropwise from an addition funnel to the aqueous persulfate solution over a period of 1 hr. The reaction temperature was maintained at the elevated temperature for 3.5 hr. The solution was then cooled to room temperature to obtain the core-shell polymer in water with a concentration of 10% by weight. The average particle size of the polymer solution was found to be 170 nm and the glass transition temperature (T g ) of the polymer obtained was 50°C. Examples 4-6. In the above Examples 1 to 3, the water-soluble components, such as vinylpyrrolidone (C), were replaced by poly( ethylene glycol) methyl ether acrylate (C) of molecular weight 404 (PEG-Ac(404)) in the corresponding amount to obtain core-shell polymer containing PEG-Ac(404). The resulting polymers and their average particle sizes and glass transition temperatures are given in Table I below. TABLE I. Results of Examples 4-6. Example 7. (Butyl Acrylate) 20 (Methyl Methacrylate) 80 / Surfactant (2 wt%). Synthesis of polymer derived from butyl acrylate (A) and MMA (B) in the ratio of 20 and 80%) by weight, respectively: Butyl acrylate (4 g) and methyl methacrylate (16 g) were mixed with BRIJ 92 (0.2 g), SOLSPERSE 27,000 (0.2 g), and isooctylmercaptopropionate (0.2 g). An emulsion was prepared by adding water (2.0 g) to the above monomer mixture. The emulsion was saturated with nitrogen and added dropwise to a solution of potassium persulfate (0.4 g) in water (177 g) at 75°C. The reaction mixture was maintained at the same temperature for another 2 hr to obtain the title polymer/surfactant system dispersed in water. The average particle size of the polymer solution was found to be 165 nm and the glass transition temperature (T g ) of the polymer obtained was 63°C. Examples 8-11: Comparison Examples 1-2. Testing of the physical properties of several durable, film- forming, water- dispersive polymers was performed and compared to prior art polymers. The tests involved a film-forming test, a water-dispersive stability test, and a measurement of the glass transition temperature, T g . (1) Film Forming Test. The core/shell polymer of the invention was cast on a glass substrate and allowed to dry at ambient conditions for several hours. As the film-forming process oc- cured, the milky color of the polymer solution gradually turned into a transparent film. The formed film (on glass substrate) was soaked in water mixed with different solvents liquid additives (40% versus water) for 24 hrs and the weight loss was meas- SUBSTΓΓUTE SHEET (RULE 26) ured. The samples with the least weight loss samples are indicative of the most durable film. (2) Water-Dispersive Stability Test. The polymer emulsion was subjected to a centrifugation set at 4,000 rpm for 30 minutes. This is repeated twice. The amount of accumulation after centrifugation is an indication of the dispersion stability, with a higher amount of accumulation indicating less dispersion stability. (3) Measurement of T g . The glass transition temperature was measured by Differential Scanning Calo- rimetry, using a DSC available from duPont de Nemours Company as Model 2.0. The data accumulated from the foregoing tests are illustrated in the following Table II: TABLE I. Results of Tests. Example 1 1: Comparison Examples 3-4. Commercially available Cabot pigment plus polymer plus penetrating humec- tant plus- non-penetrating humectant: Example 11. In an 250 cm 3 glass jar were added 5.0 g of carbon black (Vulcan XR-72), 25.0 g of a polymer of the invention comprising (HA) 30 (MMA) 40 (PEGAc(404)) 30 (10 wt% solid), 10 g diethylene glycol (as non-penetrating humectant), 10 g N-methyl pyrroli- done (NMP, as penetrating humectant), 0.02 g of fluoro surfactant (Fluorad 99; 3M Products). The components were milled together by a paint shaker using 2 mm zirconium beads for 2 hrs. After being milled, the system was diluted with water to achieve a final ink solution of 5 wt% solid. The Zr beads were removed by 200 mesh filtering. The ink solution was centrifuged to eliminate agglomerated solids and the like and re- filtered again through a 5 μm glass filter. This solution was then ready for print testing. In order to perform the print test, the ink was filled into the black ink cartridge of a Hewlett-Packard Company DeskJet printer prototype product and printed with a frequency of 20 kHz. The optical density (OD) of the print was measured by Mac Beth densitome- ter. The decap characteristic of the pen was characterized as the number of the streak lines appearing at the right hand sited of a black solid band. As the pen prints right -to-left in the printer, this is an indication of the startup performance of the pen - how long it takes the dried nozzles to come back to full nozzle health. The stability of the ink was judged by measuring the changing of the particle size after the temperature cycle (T-cycle) between 70°C .and -40°C. The particle size measurement is carried out by a Nikon particle sizer. Kogation is a phenomenon in which the pen cannot perform due to the dete- rioration of the surface of the firing resistor in the ink chamber due to a buildup of residue. Kogation generally terminates the life of the pen. Kogation was measured by number of prints exhibiting unchanged print quality (PQ) during continuous printing process of 100 pages. The higher the number, the lower the kogation effect. The waterfastness and smearfastness were measure by dripping water across a printed area or smearing the area with a highlighter, and then measuring the optical density (in mOD) of the transferred ink. Comparison Example 3. Example 12 was repeated, except the polymer was replaced by poly(ethylene glycol) having molecular weight in the range of 5,000. Comparison Example 4. Example 12 was repeated, except the polymer was replaced by 98% hydrolyzed polyvinyl alcohol, average molecular weight = 4,000. The print tests results for Examples 12 and Comparison Examples 3 and 4 are summarized in Table III. TABLE III. Results of Example 12 and Comparison Examples 3-4. The results show the superiority of an ink containing the polymer of the invention as compared to inks that do not contain the polymer of the invention. Specifically, kogation is reduced and smearfastness and waterfastness are considerably improved. Thus, there has been disclosed a durable, film-forming, water-dispersive polymer having at least one hydrophobic portion and either a hydrophilic portion or a surfactant associated with the polymer for dispersing molecules or particles in water. It will be appreciated by those skilled in the art that various changes and modifications of an obvious nature may be made, and all such changes and modifications are considered to fall within the scope of the invention.

Claims: CLAIMS What Is Claimed Is: 1. A durable, film-forming, water-di.spersive polymer having at least one hydrophobic portion and either a hydrophilic portion or a surfactant associated with said polymer for dispersing wat-er-insoluble molecules or p.articles in water, s-aid polymer having a formula given by [(A) m (B) n (C) p (D) q (E) r ] x wherein A, B, C, D, -and E are moieties as follows: A = at least one hydrophobic component contributing to improved durable, film-forming properties selected from moieties which, when homo- polymerized to a solid state, have a glass tr-ansition temperature (T g ) in the range between -150° and +25°C; B = at le.ast one hydrophobic and solvent barrier moiety used to adjust the T g of the hydrophobic component of said polymer which, when homo- polymerized to a solid state, has a T g greater than 25°C; C = at least one hydrophilic component comprising a water-soluble monomer; D = at least one UV absorber; E = at least one moiety having at least one highly polar functional group; m = 5 to 95 wt%; n = 5 to 95 wt%; p = 0 to 60 wt%; q = 0 to 50 wt%; r = 0 to 40 wt%; m + n + p + q + r = 100 wt%; and x = 1 to 100,000, wherein said polymer has either hydrophobic and hydrophilic moieties or h.as only hydrophobic moieties and is associated with said surfactant to form a polymer/surfactant system, said polymer or polymer/surfactant system capable of forming a film from water, which, upon dehydration, is essentially resistant to water, said polymer having a T g within the range of about -25° to +110°C. 2. The polymer of Claim 1 wherein said A moiety is CR,R 2 =C(R 3 )R 4 R 5 , where R, and R 2 are independently hydrogen, halogen, alkyl, aryl, or substituted alkyl or aryl, or vinyl butyral, R 3 is hydrogen, halogen, saturated or unsaturated alkyl, alkoxy, aryl, or substituted alkyl, alkoxy, or aryl, R 4 is direct bond, O, CO, NH, halogen, saturated or unsaturated alkyl, aryl, or substituted alkyl, aryl, or CN, R 5 is absent (if R 4 is alkyl, aryl, or substituted alkyl or aryl), direct bond, hy- drogen, NH, O, alkyl, alkylene, aryl, or substituted alkyl, alkylene, or aryl, and Rg is absent (if R 4 is alkyl, aryl, or substituted alkyl or aryl or if Rj is hydrogen, alkyl, aryl, or substituted alkyl or aryl), NH 2 , saturated or unsaturated alkyl, alkoxy, aryl, aroxy, or substituted alkyl or aryl, and where said alkyl, alkylene, aryl, alkoxy, and .aroxy each contain more than 1 carbon atom and less than 40 carbon atoms. 3. The polymer of Claim 1 wherein said B moiety is where R, .and R 2 .are independently selected from hydrogen, halogen, and vinyl buty- ral, R 3 is hydrogen, halogen, saturated or unsaturated alkyl, alkoxy, aryl, or substituted alkyl, alkoxy, or aryl, R" 4 is direct bond, O, CO, NH, halogen, saturated or unsaturated alkyl, aryl, or substituted alkyl, .aryl, or CN, R" 5 is absent (if R 4 is alkyl, aryl, or substituted alkyl or .aryl), direct bond, hy- drogen, NH, O, alkyl, alkylene, aryl, or substituted alkyl, alkylene, or aryl, and R" 6 is absent (if R 4 is alkyl, aryl, or substituted alkyl or aryl or if R j is hydrogen, alkyl, aryl, or substituted alkyl or aryl), NH 2 , saturated or unsaturated alkyl, alkoxy, aryl, aroxy, or substituted alkyl or aryl. where said alkyl, alkylene, aryl, alkoxy, and aroxy each contain from 1 to 40 carbon atoms, where R, and R 2 and R 2 and R 3 can each form a ring, and where R" 4 and R" s can form a ring through nitrogen or oxygen. 4. The polymer of Claim 1 wherein said C moiety is selected, from the group consisting of (a) where R, = H, halogen, alkyl, aryl, or substituted alkyl or aryl; R 2 = direct bond, O, CO, NH, or CONH; (CH 2 CH(CH 3 )O) y R 4 , (CH 2 CH(C 2 H 5 )O) y R 4 , SH, (CH-.CH.S)^, (CH 2 CH(CH 3 )S) y R 4 , or (CH 2 CH(C 2 H 5 )S) y R 4 ; y = 1 to 200; and R 4 = alkyl, aryl, substituted alkyl or aryl; (b) where R, .and R 2 are ind-ependently selected from H, halogen, alkyl, aryl, and substituted alkyl and aryl, where said alkyl and aryl each contain from 2 to 40 carbon atoms; (c) C=CH 2 z where R, .and R 2 are independently selected from H, halogen, alkyl, aryl, and substituted alkyl and aryl; and (<j) where R, = H, halogen, alkyl, .aryl or substituted alkyl or aryl; and R 2 .and R 3 are either independently selected from alkyl, aryl, and substituted alkyl and .aryl or can form either .an aliphatic ring or .an aromatic ring. 5. The polymer of Cl.aim 1 wherein said D moiety is selected from the group consisting of 6. The polymer of Claim 1 wherein said E moiety is selected from the group consisting of (a) CH(R,) = C(R 2 )R 3 COOH where R, = H, COOH, COOR 4 ; R 2 = H, halogen, alkyl, .aryl, alkoxyl, substituted alkyl, .aryl or alkoxyl; R 3 = direct bond, .alkylene, arylene, or sustituted alkylene or arylene; and R 4 = alkyl, aryl, or substituted alkyl or aryl; (b) CH 2 = CHR,NR 2 R 3 where R x = alkylene, arylene, substituted alkylene or arylene, or SO 2 ; and R 2 and R 3 are either independently selected from H, alkyl, aryl, and substituted alkyl, aryl and alkoxyl or form either an aliphatic or aromatic ring; (c) y (CH 2 =CHR,COO ) W where R, = alkylene, arylene, substituted alkylene or arylene; y = 1 to 4; and M = NH 4 + , Li + , Na + , K + , Ca 2+ , Mg 2+ , Al 3+ , Ti 4+ , triethylam onium, dieth- ylammonium, and pyrridinium. ( ) z (CH 2 = CHR,N + R 2 R 3 R 4 ) X z" where R, = alkylene, arylene, substituted alkylene or arylene, COO, or cyclic ring containing nitrogen; R 2 , R 3 , .and R 4 are independently selected from H, alkyl, aryl, alkoxyl, .and substituted alkyl, aryl and alkoxyl; z = 1 to 4; .and X = halogen, BF 4 , PF 6 , ClO 4 , SCN, CNO, CNS; (e) where R, = H, alkyl, aryl, alkoxyl, substituted alkyl, aryl or alkoxyl; R 2 = direct bond, alkylene, arylene, or substituted .alkylene or arylene; z = 1 to 4; and M 2+ = NH 4 + , Li + , Na + , K + , Ca 2+ , Mg 2* , Al 3+ , Ti 4+ , triethylammonium, dieth- yl.ammonium, .and pyrridinium; where R j = H, alkyl, aryl, alkoxyl, or substituted alkyl, aryl or .alkoxyl; R 2 = direct bond, COOR 3 , arylene, alkylene, or -CONHR 3 ; R 3 = alkylene, arylene, or substituted alkylene or arylene, or fluoroalkylene; z = 1 to 4; and M z+ = NH 4 + , Li + , Na + , K + , Ca 2+ , Mg 2 ", Al 3+ , Ti 4+ ; (g) a sulfonium salt having the following structure: where R, = -H, halogen, alkyl, or aryl; R 2 = >CO, -O-; R 3 = direct bond, >NH; R 4 = alkyl or aryl; and X = CI, Br, BF 4 , ClO 4 , 1, or NO 3 ; (h) a carbonium salt having the following structure: R, CH,=C R, R, R 4 -C + -R 5 X " where R, = -H, halogen, alkyl, or aryl; R 2 = >CO, -O-; R 3 = direct bond, >NH, alkylene, or arylene; R 4 and R 5 are ind-ependently selected from alkyl or aryl; and X =SbF 5 \ FSO 3 -; (i) a pyrilinium salt or thiopyrrilinium s.alt having the following structure: where Y = O or S; R, = -H, halogen, alkyl, or aryl; R 2 = >CO, -O-; R 3 = direct bond, >NH, alkylene, or arylene; X = CI, Br, I, ClO 4 , or BF 4 ; and (j) a tetrazolium salt. 7. The polymer of Cl-aim 1 wherein said surfactant is selected from the group consisting of anionic, cationic, non-ionic, and zwitterionic surfactants. 8. The polymer of Claim 1 wherein said polymer is selected from the group consisting of (hexyl acrylate) 40 (methyl methacrylate) 40 (poly(ethylene glycol) methyl ether acrylate, mw=404) 20 ; (hexyl acrylate) 30 (methyl methacrylate) 50 (poly(ethylene glycol) methyl ether acrylate, mw=404) 20 ; (hexyl acrylate) 20 (methyl methacrylate) 60 (poly(ethylene glycol) methyl ether acrylate, mw=404) 20 ; (hexyl acrylate) 40 (methyl methacrylate)^ (poly(ethylene glycol) methyl ether acrylate, mw=2054) 20 ; (hexyl acrylate)^ (methyl methacrylate) 50 (poly(ethylene glycol) methyl ether acrylate, mw=2054) 20 ; (hexyl acrylate) 20 (methyl methacrylate)^ (poly(ethylene glycol) methyl ether acrylate, mw=2054) 20 ; (hexyl acrylate) 40 (methyl methacrylate) 40 (poly(ethylene glycol) methyl ether acrylate, mw=218) 20 ; (hexyl acrylate) 30 (methyl methacrylate) 50 (poly(ethylene glycol) methyl ether acrylate, mw=218) 20 ; (hexyl acrylate) 20 (methyl methacrylate)^ (poly(ethylene glycol) methyl ether acrylate, mw=218) 20 ; (ethyl acrylate)^ (methyl methacrylate)^ (poly(ethylene glycol) methyl ether acrylate, mw=404) 20 ; (propyl acrylate)^ (methyl methacrylate) 40 (poly(ethylene glycol) methyl ether acrylate, mw=404) 20 ; (butyl acrylate) 40 (methyl methacrylate) 40 (poly(ethylene glycol) methyl ether acrylate, mw=404) 20 ; (octadecyl acrylate) 40 (methyl methacryl- a e ) 4 o (poly(ethylene glycol) methyl ether acrylate, mw=404) 20 ; (lauryl methacrylate) 40 (methyl methacrylate) 40 (poly(ethylene glycol) methyl ether acrylate, mw=404) 20 ; (octadecyl methacrylate) 40 (methyl methacrylate) 40 (poly(ethylene glycol) methyl ether acrylate, mw=404) 20 ; (hydroxyoctadecyl acrylate)^ (methyl methacrylate) 40 (poly(ethylene glycol) methyl ether acrylate, mw=404) 20 ; (hydroxyethyl acrylate) 40 (methyl methacrylate) 40 (poly(ethylene glycol) methyl ether acrylate, mw=404) 20 ; (hydroxylauryl methacrylate)^ (methyl methacrylate) 40 (poly(ethylene glycol) methyl ether acrylate, mw=404) 20 ; (phenethyl acrylate) 40 (methyl - methacrylate) 40 (poly(ethylene glycol) methyl ether acrylate, mw=404) 20 ; (6-phenylhexyl acrylate) 40 (methyl methacrylate) 40 (poly(ethylene glycol) methyl ether acrylate, mw=404) 20 ; (cy- clohexyl acrylate) 40 (methyl methacrylate) 40 (poly(ethylene glycol) methyl ether acrylate, mw=404) 20 ; (acryloxypropylmethyldimethoxysilane) 30 (methyl methacrylate) 50 (poly(ethylene glycol) methyl ether acrylate, mw=404) 20 ; (N,N-dihexyl acrylamide) 20 (methyl methacrylate)^ (poly(ethylene glycol) methyl ether acrylate, mw=404) 20 ; (aminopropyl acrylate) 40 (methyl methacrylate) 40 (poly(ethylene glycol) methyl ether acrylate, mw=2054) 20 ; (aminohexyl acrylate) 30 (methyl methacrylate) 50 (poly(ethylene glycol) methyl ether acrylate, mw=2054) 20 ; (aminolauryl methacrylate) 20 (methyl methacrylate)^ (poly(ethylene glycol) methyl ether acrylate, mw=2054) 20 ; (N,N- dimethylaminoethyl acrylate) 40 (methyl methacrylate)^ (poly-(ethylene glycol) methyl ether acrylate, mw=218) 20 ; (vinyl acetate) 30 (methyl methacrylate) J0 (poly(ethylene glycol) methyl ether acrylate, mw=218) 20 ; (vinyl butyl ether) 20 (methyl methacrylate)^ (poly (ethylene glycol) methyl ether acrylate, mw=218) 20 ; (hexyl acrylate) 40 (styrene) 40 (poly(ethylene glycol) methyl ether acrylate, mw=404) 20 ; (hexyl acrylate) 30 (dimethyl styrene) 50 (poly(ethylene glycol) methyl ether acrylate, mw=404) 20 ; (hexyl acrylate) 20 (trifluoromethyl styrene)^ (poly(ethylene glycol) methyl ether acrylate, mw=404) 20 ; (hexyl acrylate)^ (tetrafluoropropyl methacrylate) 40 (poly(ethylene glycol) methyl ether acrylate, mw=2054) 20 ; (hexyl acrylate) 30 (glycidyl methacrylate) 50 (poly(ethylene glycol) methyl ether acrylate, mw=2054) 20 ; (hexyl acrylate) 20 (glycidyl acrylate)^ (poly(ethylene glycol) methyl ether acrylate, mw=2054) 20 ; (hexyl acrylate) 40 (maleimide) 40 (poly(ethylene glycol) methyl ether acrylate, mw=218) 20 ; (hexyl ac- rylate) 50 (n-hexyl maleimide) 30 (poly(ethylene glycol) methyl ether acrylate, mw=218) 20 ; (hexyl acrylate) 40 (n- vinyl maleimide) 40 (poly(ethylene glycol) methyl ether acrylate, mw=218) 20 ; (hexyl acrylate) 40 (methyl methacrylate) 40 (vinyl pyrroli- done) 20 ; (hexyl acrylate) 40 (methyl methacrylate) 40 (vinyl 4-methylpyrrolidone) 20 ; (hexyl acrylate)^ (methyl methacrylate) 40 (vinyl imid^ole) 20 ; (hexyl acrylate) 40 (methyl methacrylate) 40 (acrylamide) 20 ; (hexyl acrylate) 40 (methyl methacrylate) 40 (4- methyl acrylamide) 20 ; (hexyl acrylate)^ (methyl methacrylate) 30 (dl) 1() (poly(ethylene glycol) methyl ether acrylate, mw=404) 20 ; (hexyl acrylate) 40 (methyl methacryl- ate) 30 (dl) 10 (poly(ethylene glycol) methyl ether acrylate, mw=404) 20 ; (hexyl acrylate) 40 (methyl methacrylate) 30 (dl) 10 (poly(ethylene glycol) methyl ether acrylate, mw=404) 20 ; (hexyl acrylate) 40 (methyl methacrylate) 30 (dl) 10 (poly(ethylene glycol) methyl ether acrylate, mw=404) 20 ; (hexyl acrylate) 40 (methyl methacrylate) 30 (d4) 10 (poly(ethylene glycol) methyl ether acrylate, mw=404) 20 ; (hexyl acrylate) 40 (methyl methacrylate) 30 (d4) 10 (poly(ethylene glycol) methyl ether acrylate, mw=404) 20 ; (hexyl acrylate) 40 (styrene) 30 (dl) 10 (poly(ethylene glycol) methyl ether acrylate, mw=404) 20 ; (hexyl acrylate) 40 (styrene) 30 (dl) 10 (vinyl pyrrolidone) 20 ; (hexyl acrylate) 50 (methyl methacrylate) 4S (polyethylene glycol) methyl ether acrylate, mw=404) 5 ; (hexyl ac- rylate) 50 (methyl methacrylate) 40 (poly(ethylene glycol) methyl ether acrylate, mw=404) 10 ; (hexyl acrylate) 50 (methyl methacrylate) 35 (poly(ethylene glycol) methyl ether acrylate, mw=404), 5 ; (methyl methacrylate)^ (hexyl acrylate)^ / surfactant; (methyl methacrylate)^ (butyl acrylate)^ / surfactant; and (styrene) 30 (octadecyl ac- rylate) 70 / surfactant, where dl and d4 are UV absorbers given by the formula where R, = H, R 2 = O, and R 3 are and O OH respectively. 9. The polymer of Claim 1 wherein said polymer is selected from the group consisting of (hexyl acrylate)^ (methyl methacrylate)^ (acrylic acid) 20 ; (hexyl ac- rylate)^ (methyl methacrylate) 20 (methacrylic acid) 20 ; (hexyl acrylate)^ (methyl methacrylate)^ (maleic acid) 20 ; (hexyl acrylate) 40 (methyl methacrylate) 40 (vinyl benzoic acid) 20 ; (hexyl acrylate) 40 (methyl methacrylate) 40 (vinyl sulfonamide) 20 ; (hexyl acrylate)^ (methyl methacrylate)^ (sodium acrylate) 20 ; (hexyl acrylate) 40 (methyl methacrylate)^ (ammonium acrylate) 20 ; (hexyl acrylate)^ (methyl methacrylate) 40 (ammonium methacrylate) 20 ; (ethyl acrylate)^ (methyl methacrylate)^ (acrylamidopropane- triethyl-ammom ' um chloride) 20 ; (propyl acrylate)^ (methyl methacrylate) 40 (vinyl pyridine hydrochloride) 20 ; (butyl acrylate) 40 (methyl methacrylate)^ (sodium vinyl phosphate) 20 ; (hexyl acrylate)^ (methyl methacrylate) 40 (sodium styrene sulfonate) 20 ; (hexyl acrylate) 30 (methyl methacrylate) 50 (sodium acrylamidopropanesulfonate) 20 ; (styrene) 7J (acrylic acid) 20 (dl) 5 ; (styrene) 55 (acrylic acid) 40 (d4) 5 ; (styrene) 40 (methyl methacrylate)^ (acrylic acid) 20 ; (ethyl acrylate) 55 (acrylic acid) 40 (dl) 5 ; (styrene) 40 (ethyl acrylate) 40 (acrylic acid) 20 ; (methyl methacrylate)^ (hexyl acrylate) 55 (dl) 5 ; (methyl methacrylate)^ (butyl acrylate) 55 (dl) 5 ; (styrene) 30 (octadecyl acrylate) 65 (dl) 5 ; and (methyl methacrylate) 32 (hexyl acrylate) 46 (poly(ethylene glycol) methyl ether acrylate, mw=404) 12 (acrylic acid) 10 , where dl and d4 are UV absorber moieties given by the formula R, I where R, = H, R 2 = O, and R 3 are and O OH respectively.

Inventors: GANAPATHIAPPAN SIVAPACKIA, NGUYEN KHE C, GANAPATHIAPPAN, SIVAPACKIA, NGUYEN, KHE, C.
Applicants: GANAPATHIAPPAN SIVAPACKIA, HEWLETT PACKARD CO, NGUYEN KHE C, GANAPATHIAPPAN, SIVAPACKIA, HEWLETT-PACKARD COMPANY, NGUYEN, KHE, C.
Application year: 1998
Main classification: C08F246
IPC codes: C08F220, C08F246, C08F291, C09D11