Blue or bluish green aluminium silicate luminous storage material and manufacturing method

Abstract: A luminous storage material is provided that emits a blue or bluish green light, that has high persistence, that is thermally and structurally stable, and that exhibits a high weather resistance in chemically severe conditions. A blue aluminium silicate luminous storage material according to this invention is composed of a powdered product that has been activated by Eu 2+ and has a composition formula expressed as follows: (M 1-n-m M* n Eu m ) (Al 1-x Si ¾x □ ¼x ) 2 O 4 - wherein □ is the defective composition; M is one or more alkali earth metal elements selected from the group of magnesium, calcium, strontium and barium; M* is one or more bivalent metal elements selected from the group of manganese, zinc and cadmium; and (n), (m) and (x) are molar values in the ranges: 0 ≤ n ≤ 0.2 0 < x < 0.6 0.0001 ≤ m ≤ 0.1.

Description: The present invention relates to a blue or bluish green aluminium silicate luminous storage material and a method for its manufacture. Phosphor emits light when excited by certain external stimuli such as grain energy, electrons or light. A persistent luminous material that can maintain emission after excitation is stopped is called a luminous storage material. Due to the needs for various types of displays and advanced functions for dark places, there is a demand for luminous storage that can handle multiple colours and maintain emissions over a long period of time. In addition, greater weather resistance is also now needed. Currently, only a very small number of luminous storage materials are available, the number of colours of light and afterglow are limited, the afterglow time is short, and weather resistance is insufficient. Inorganic materials include sulfide or oxyacid-salt (such as strontiumaluminate) luminous material due to their storage capability. Sulfide phosphors include, for example, (Ca,Sr)S:Bi 3+ phosphors emitting a blue light, ZnS:Cu 2+ phosphors emitting a yellowish green light; and (Zn,Cd)S:Cu phosphors emitting a red light. oxyacid salt phosphors include, for example, alkali earth metal aluminate which has been activated by europium and which is expressed by the chemical formula MAl 2 O 4 . In this case, M is alkali earth metal of magnesium, calcium or strontium. In particular, an SrAl 2 O 4 :Eu 2+ phosphor having a stuffed tridymite structure and reported in Journal of Electrochemical Society, Vol 118, pp 930 (1971) is known to have relatively high persistence. These phosphors, however, are not good enough luminous storage or have poor weather resistance. In fact, since the host of (Ca,Sr)S:Bi 3+ phosphor has inadequate chemical stability and also has insufficient luminance and afterglow time as an emitter, it is now rarely used. In addition, (Zn,Cd)S:Cu phosphor contains Cd, which is toxic, and its luminance level and afterglow time are impractical, so it is now rarely used. ZnS:Cu 2+ phosphor is likely to be photodissociated and melanized by ultraviolet rays in the presence of humidity, and has an insufficient afterglow time, but due to its low price, it is now frequently used outdoors for clockfaces and evacuation guidance signs. Strontiumaluminate/bariumaluminate that has been mainly activated by europium is a yellowish green emitter having a maximum luminescent intensity near 520 nm/500 nm. It takes 2000 minutes or more for it to drop to 0.32 mcd/m 2 , indicating higher persistence than ZnS:Cu phosphor, which drops to this level in 200 minutes. It has been suggested, however, that this material does not meet requirements for weather resistance and multiple colours. It is an object of this invention to eliminate the above disadvantages of the conventional inorganic luminous storage materials and to provide a luminous storage material that emits a blue or bluish green light, that has high persistence, that is thermally and structurally stable, and that exhibits high weather resistance under chemically severe conditions. A further object of this invention is to provide a manufacturing method for such a material. To achieve this object, the inventors have focused on oxides containing elements in group II of the periodic table and aluminium silicate compounds and have found a new aluminium-silicate compound luminous storage material that can be obtained by using Eu 2+ , or Eu 2+ and an Ln rare earth element, to activate a reactive product of an oxide containing an element in group II and an aluminium silicate salt of a particular composition. The inventors have found that by optimising the content of Eu 2+ , which mainly contributes to emission, or Eu 2+ and the Ln rare earth element, or other contained elements (for example, boron or sodium contained as a flux to facilitate the growth of grains), a blue or bluish green luminous storage material can be obtained that has very high persistence, that is structurally and chemically stable, that has high weather resistance, and that has a maximum luminescent intensity of 460 nm or near 490 nm, respectively. The inventors have confirmed that the material meets the above object. An aluminium silicate luminous storage material according to this invention, is a blue or bluish green luminous storage material which has a composition formula expressed as follows: (1) (M 1-n-m M* n Eu m ) (Al 1-x Si ¾x □ ¼x ) 2 O 4 or (2) (M 1-n-m-k M* n Eu m Ln k ) (Al 1-x Si ¾x □ ¼x ) 2 O 4 and is mainly activated by Eu 2+ , in the case of (1) or Eu 2+ and one or more types of rare earth elements Ln in the case of (2). In the above formulae, □ is the deficiency; M is one or more alkali earth metal elements selected from a group of magnesium, calcium, strontium and barium; M* is one or more bivalent metal elements selected from a group of manganese, zinc and cadmium; Ln is a rare earth element other than Eu; and (n), (m), (k) and (x) are numerical values falling within the following ranges: 0 ≤ n ≤ 0.2 0 < x < 0.6 0.0001 ≤ m ≤ 0.1 0.0001 ≤ k ≤ 0.1. The luminous storage material exhibits thermal luminescence when excited by ultraviolet rays and/or visible light between 220 and 480 nm followed by heating up to or beyond room temperature. A method for manufacturing the blue or bluish green light-emitting aluminium silicate luminous storage material is also provided. The luminous storage material is obtained as a powder product by burning together with sodium carbonate or boron oxide, a powder mixture obtained by mixing a compound containing an M element, a compound containing an M* element, a compound containing an Al element, a compound containing an Si element or silicon and a compound containing an Eu element together in the ratio expressed by the composition formula given in Expression (1), or material powders obtained by mixing the above elements and one or more types of rare earth elements Ln at the ratio expressed by Formula (2). The burning is desirably carried out in a reducing atmosphere at 800°C to 1400°C. In addition, desirably, the material powders are moulded under a load of 1 to 5000 kg/cm 2 using a metal moulding machine, and are then burned or calcinated to obtain a product, which is then moulded under pressure using the same load and sintered. The aluminium silicate luminous storage material according to this invention has the host components expressed by Composition Formula (1) or (2). The M element included in these components is partly substituted by the M* element of manganese, zinc or cadmium. A suitable amount of M* (molar value) for improving luminance is 0 ≤ n ≤ 0.2, and preferably, 0 ≤ n ≤ 0.05. If the substitution factor exceeds 0.2, the effect of improved afterglows and luminance decreases significantly. In addition, a suitable value for m, the amount of Eu 2+ contained in the aluminium silicate luminous storage material is 0.0001 ≤ m ≤ 0.1, and preferably 0.001 ≤ m ≤ 0.01. Under 0.0001, the amount of ions that mainly emit light is so small as to prevent a target luminance from being obtained. In addition, if this value exceeds 0.1, density quenching may be caused by the interaction among the luminous ions, unwanted compounds may be generated, or material oxides may remain, thereby significantly reducing the luminance of the luminous storage material obtained. With a composition of Formula 2 where a rare earth element Ln such as Dy 3+ or Nd 2+ is used with Eu 2+ as an activating agent, a suitable value of (k) is 0.0001 ≤ k ≤ 0.1, preferably between 0 and 50 mol% relative to Eu 2+ . The resulting luminous storage material emits a bluish green light having a maximum luminescent intensity near 490 nm, in contrast to conventional strontiumaluminate, which does not contain Si. A suitable amount of (x) (molar value), the content of SiO 2 or silicon included in the composition formula is 0.1 ≤ x ≤ 0.6, and the deficiency expressed by □ occurs to the host due to the need to maintain a charge balance as the amount of Si increases. Thus, preferably, a more suitable range is 0.1 ≤ x ≤ 0.45. Beyond 0.6, the ability to improve the persistence characteristic, and thus luminance, decreases. When boron oxide is added as a flux, powdered blue or bluish green aluminium silicate luminous storage material having a specified grain size (1 to 10 µm) is obtained. It is partly substituted for Al to improve the persistence characteristic, but the amount of substitution does not exceed 0.001 mol. In addition, an excessive amount of boron oxide increases the amount of unreacted materials and does not affect the luminance or persistence characteristic despite its effect as a flux on the grain growth. The aluminium silicate luminous storage material according to this invention exhibits thermal luminescence (fluorescence) when excited by electron beams, or ultraviolet rays and/or visible light between 220 and 480 nm followed by heating up to or beyond room temperature. The aluminium silicate luminous storage material according to this invention can be manufactured as follows: The materials used comprise a compound containing M, an M* compound, an Al compound, a B compound, an Si element or silicon, a compound of Eu 2+ to serve as an activating agent, and a compound containing an Ln rare earth element - that is, oxides containing these elements, or salts such as carbonate, nitrate and chloride that can be converted into oxides easily by means of sintering. These materials are weighed so as to achieve the composition range shown in Composition Formula (1) or (2) and are sufficiently wet- or dry-mixed. The mixed powders are placed in a heat-resistant reaction container such as an aluminium or a graphite crucible directly or after they have been subjected to a pressure of 1 to 5000 kg/cm 2 , and are then sinteredonce or more in a reducing atmosphere of an inert gas containing hydrogen or in a carbon reducing atmosphere at 800° to 1400°C for 1 to 12 hours. When sintering is repeated twice or more, the first operation may be performed in air, but the finalsintering step must be executed in a reducing atmosphere. The present invention provides an aluminium silicate luminous storage material which comprises an emitter that emits a blue or bluish green light indoors, outdoors, underwater, or in other dark places when excited by electron beams, ultraviolet rays, and/or visible radiation. The material also has a long-lasting blue afterglow after excitation is stopped. The luminous storage material is mainly activated by EU 2+ , is thermally stable, and exhibits excellent chemical stability in an oxidising or reducing atmosphere. The present invention also provides a manufacturing method for this material. The invention will now be described with reference to the accompanying drawings, in which:- Figure 1 is a diagram showing a powder X-ray diffraction chart of a luminous storage material having a chemical composition according to Embodiment 1. Figure 2 is a diagram showing a powder X-ray diffraction charge of SrAl 2 O 4 for comparison. Figure 3 is a diagram showing as (a) to (f) emission spectra (excitation: 360 nm) of a luminous storage material according to Embodiments 1 to 6 of this invention. FIG. 4 is a diagram showing as (a) to (f) excitation ;spectra (emission: 460 nm) according to Embodiments 1 to 6 of this invention. FIG. 5 is a diagram showing as (a) to (f) temporal changes in luminescent intensity (persistence characteristic) according to Embodiments 1 to 6 of this invention. FIG. 6 is a diagram showing as (1) and (2) diffuse reflection spectra according to Embodiment 1 and Comparative Example 1. FIG. 7 is a diagram showing a powder X-ray diffraction chart of a luminous storage material having a chemical composition according to Embodiment 2. FIG. 8 is a diagram showing a powder X-ray diffraction chart of a phosphor having a chemical composition according to Embodiment 7. FIG. 9 is a diagram showing as (a) and (c) emission spectra (excitation: 360 nm) of samples according to Embodiments 7 and 8. FIG. 10 is a diagram showing as (b) and (d) emission spectra (excitation: 360 nm) of samples according to Comparative Examples 2 and 1. FIG. 11 is a diagram showing as (a) and (c) excitation spectra (emission: 490 nm) of samples according to Embodiments 7 and 8. FIG. 12 is a diagram showing as (b) and (d) excitation spectra (emission: 520 nm) of samples according to Comparative Examples 2 and 1. FIG. 13 is a diagram showing as (a) - (d) temporal changes in the luminescent intensity of samples according to Embodiment 7, Comparative Example 2, Embodiment 8, and Comparative Example 1. Figures 14(a) and (b) are scanning electron-microscopic photographs showing the crystal structure of a sample according to Embodiment 7 before and after burning, respectively. Figures 15(a) and (b) are scanning-electron-microscopic photographs showing the crystal structure of a sample according to Comparative Example 2 before and after burning, respectively. This invention is described below in more detail by reference to embodiments and comparative examples. Theoretically, the composition formula is as shown in Formula (1) or (2), but is adjusted to the following formulae in the embodiments: (M 1-n-m M* n Eu m ) (Al 1-x Si x ) 2 O 4 or (M 1-n-m-k M* n Eu m Ln k ) (Al 1-x Si x ) 2 O 4 In the embodiments, the amount of silica used as a flux is 1/4x greater than the amount required. Embodiment 1 To obtain a luminous storage material having a chemical composition of Sr 0.995 Eu 0.005 Al 1.85 Si 0.15 O 4 , with B 2 O 3 and Na 2 CO 3 as fluxes and the following amounts of material powders were each weighed. Then, an appropriate amount of alcohol was added and these materials were sufficiently wet-mixed in a ball mill for 24 hours. SrCO 3 2.938 g Al 2 O 3 1.886 g SiO 2 0.180 g Eu 2 O 3 0.018 g B 2 O 3 0.139 g Na 2 CO 3 0.318 g. The mixed powders were dried at 40°C and molded into a disc of diameter 13 mm under a load of 1,000 kg/cm 2 using a metal molding machine, and the disc was placed in an alumina crucible and burned in argon gas containing 3% hydrogen at 1,300°C for five hours using an electric furnace. The sintered compact obtained was ground using a pestle and a mortar and its phase was identified using a powder X-ray diffraction method. FIG. 1 shows the results of powder X-ray diffraction using CuKα rays. For comparison, FIG. 2 shows a powder X-ray diffraction chart of synthesized SrAl 2 O 4 . As shown in the figure, each peak is indexed and belongs to a monoclinic stuffed tridymite structure. These results show that the sample obtained according to this embodiment had almost a single phase and was isomorphous with SrAl 2 O 4 . FIG. 3 (a) shows an emission spectrum of a sample according to Embodiment 1 when it was excited by 360-nm ultraviolet rays. This figure shows that the peak that provided a maximum luminescent intensity was a blue light emission located near 460 nm. In addition, FIG. 4 (a) shows an excitation spectrum. Then, the sample was excited at an excitation wavelength of 250 nm for 30 seconds, and temporal changes in the luminescent intensity of a 460-nm peak (persistence characteristic) were then measured. FIG. 5 (a) shows the results of the measurement. In addition, BaSO 4 was absorbed and measured as a reference sample using diffusion reflection method. FIG. 6 (1) shows a diffuse reflection spectrum. This figure shows that this spectrum has the same profile as the diffuse reflection spectrum (shown in FIG. 6 (2)) of a sample containing no Si and obtained in Comparative Example 1, which is described below. Thus, the absorbing end of each sample can be assumed to be located in a region of wavelength smaller than 200 nm. Embodiment 2 To obtain luminous storage having a chemical composition of Sr 0.99 Zn 0.005 Eu 0.0005 Al 1.85 Si 0.15 O 4 , with B 2 O 3 and Na 2 CO 3 as fluxes, the following amounts of material powders were each weighed. Then, an appropriate amount of alcohol was added and these materials were sufficiently wet-mixed in a ball mill for 24 hours. SrCO 3 2.923 g ZnO 0.008 g Al 2 O 3 1.886 g Silicon 0.084 g Eu 2 O 3 0.018 g B 2 O 3 0.014 g Na 2 CO 3 0.518 g. The mixed powders were dried at 40°C and moulded into a disc of diameter 13 mm under a load of 1500 kg/cm 2 using a metal moulding machine, and the disc was placed in an alumina crucible and burned in argon gas containing 3% hydrogen at 1300°C for three hours using an electric furnace. The sintered compact obtained was ground to obtain luminous storage material according to this invention that emits a blue light. This luminous storage material was obtained by substituting Sr 0.99 Zn 0.005 for Sr 0.995 in material with the chemical composition of Embodiment 1. Figure 7 shows a powder X-ray diffraction chart of the sample obtained wherein CuKa rays were used. As in Embodiment 1, the figure shows that the sample obtained according to this embodiment had almost a single phase and was isomorphous with SrAl 2 O 4 . FIG. 3 (b) shows an emission spectrum of the sample when its was excited by 360-nm ultraviolet rays. This figure shows that the peak that provided a maximum luminescent intensity was a blue light emission located near 460 nm. In addition, FIG. 4 (b) shows an excitation spectrum. Then, the sample was excited at an excitation wavelength of 250 nm for 30 seconds, and temporal changes in the luminescent intensity of a 460-nm peak (persistence characteristic) were then measured. FIG. 5 (b) shows the results of the measurement. Embodiment 3 To obtain luminous storage material having a chemical composition of Ca 0.95 Eu 0.05 Al 1.80 Si 0.20 O 4 , with B 2 O 3 and Na 2 CO 3 as fluxes, the following amounts of material powders were each weighed. Then, an appropriate amount of alcohol was added and these materials were sufficiently wet-mixed in a ball mill for 24 hours. CaCO 3 1.902 g Al 2 O 3 1.836 g SiO 2 0.240 g Eu 2 O 3 0.176 g B 2 O 3 0.069 g Na 2 CO 3 0.318 g The mixed powders were dried at 40°C and molded into a disc of diameter 13 mm under a load of 2,000 kg/cm 2 using a metal molding machine, and the disc was placed in an alumina crucible and burned in argon gas containing 3% hydrogen at 1,350°C for three hours using an electric furnace. The sintered compact obtained was ground to obtain a luminous storage material according to this invention having a blue light emission. This luminous storage material was obtained by substituting Ca 0.95 for Sr 0.995 in the material of the chemical composition of Embodiment 1 and increasing the ng the content of Eu from 0.005 to 0.05. FIG. 3 (c) shows an emission spectrum of the sample when it was excited by 360-nm ultraviolet rays. This figure shows that the peak that provided a maximum luminescent intensity was the emission of a blue light emission near 460 nm. In addition, FIG. 4 (c) shows an excitation spectrum. Then, the sample was excited at an excitation wavelength of 250 nm for 30 seconds, and temporal changes in the luminescent intensity of a 460-nm peak (persistence characteristic) were then measured. FIG. 5 (c) shows the results of the measurement. Embodiment 4 To obtain an luminous storage material having a chemical composition of Ca 0.79 Ba 0.20 Eu 0.01 Al 1.80 Si 0.20 O 4 , with B 2 O 3 and Na 2 CO 3 as fluxes, the following amounts of material powders were each weighed. Then, an appropriate amount of alcohol was added and these materials were sufficiently wet-mixed in a ball mill for 24 hours. BaCO 3 0.789 g CaCO 3 1.581 g Al 2 O 3 1.836 g SiO 2 0.240 g Eu 2 O 3 0.035 g B 2 O 3 0.069 g Na 2 CO 3 0.318 g The mixed powders were dried at 40°C and molded into a disc of diameter 13 mm under a load of 1,000 kg/cm 2 using a metal molding machine, and the disc was placed in a graphite crucible and burned in argon gas containing 3% hydrogen at 1,250°C for five hours using an electric furnace. The sintered compact obtained was ground to obtain a luminous storage material according to this invention that emits a blue light. This luminous storage material was obtained by substituting Ca 0.79 Ba 0.20 for Sr 0.995 in the material of the chemical composition of Embodiment 1, and increasing the content of Eu from 0.005 to 0.01. FIG. 3 (d) shows an emission spectrum of the sample when it was excited by 360-nm ultraviolet rays. This figure shows that the peak that provided a maximum luminescent intensity was a blue light emission located near 460 nm. In addition, FIG. 4 (d) shows an excitation spectrum. Then, the sample was excited at an excitation wavelength of 250 nm for 30 seconds, and temporal changes in the luminescent intensity of a 460-nm peak (persistence characteristic) were then measured. FIG. 5 (d) shows the results of the measurement. Embodiment 5 To obtain an luminous storage material having a chemical composition of Ba 0.98 Eu 0.02 Al 1.90 Si 0.10 O 4 , with B 2 O 3 and Na 2 CO 3 as fluxes, the following amounts of material powders were each weighed. Then, an appropriate amount of alcohol was added and these materials were sufficiently wet-mixed in a ball mill for 24 hours. BaCO 3 3.868 g Al 2 O 3 1.938 g SiO 2 0.120 g Eu 2 O 3 0.070 g B 2 O 3 0.069 g Na 2 CO 3 0.415 g The mixed powders were dried at 40°C and molded into a disc of diameter 13 mm under a load of 1,000 kg/cm 2 using a metal molding machine, and the disc was placed in an alumina crucible and burned in argon gas containing 3% hydrogen at 1,350°C for four hours using an electric furnace. The sintered compact obtained was ground to obtain a luminous material storage according to this invention having a blue light emission. This luminous storage material was obtained by substituting Ba 0.98 for Sr 0.995 in the material of the chemical composition of Embodiment 1, and increasing the content of Eu from 0.005 to 0.02. FIG. 3 (e) shows an emission spectrum of the sample when it was excited by 360-nm ultraviolet rays. This figure shows that the peak that provided a maximum luminescent intensity was a blue light emission located near 460 nm. In addition, FIG. 4 (e) shows an excitation spectrum. Then, the sample was excited at an excitation wavelength of 250 nm for 30 seconds, and temporal changes in the luminescent intensity of a 460-nm peak (persistence characteristic) were then measured. FIG. 5 (e) shows the results of the measurement. Embodiment 6 To obtain a luminous storage material having a chemical composition of Mg 0.799 Ba 0.20 Eu 0.001 Al 1.90 Si 0.10 O 4 , with B 2 O 3 and Na 2 CO 3 as fluxes, the following amounts of material powders were each weighed. Then, an appropriate amount of alcohol was added and these materials were sufficiently wet-mixed in a ball mill for 24 hours. MgO 0.644 g BaCO 3 0.789 g Al 2 O 3 1.938 g SiO 2 0.120 g Eu 2 O 3 0.007 g B 2 O 3 0.069 g Na 2 CO 3 0.415 g The mixed powders were dried at 40°C and molded into a disc of diameter 13 mm under a load of 1,000 kg/cm 2 using a metal molding machine, and the disc was placed in an alumina crucible and burned in argon gas containing 3% hydrogen at 1,350°C for three hours using an electric furnace. This luminous storage material was obtained by substituting Mg 0.799 Ba 0.20 for Ba 0.98 in the material of the chemical composition of Embodiment 5, and reducing the content of Eu from 0.02 to 0.001. FIG. 3 (f) shows an emission spectrum of the sample when it was excited by 360-nm ultraviolet rays. This figure shows that the peak that provided a maximum luminescent intensity was a blue light emission located near 460 nm. In addition, FIG. 4 (f) shows an excitation spectrum. Then, the sample was excited at an excitation wavelength of 250 nm for 30 seconds, and temporal changes in the luminescent intensity of a 460-nm peak (persistence characteristic) were then measured. FIG. 5 (f) shows the results of the measurement. Embodiment 7 To obtain a luminous storage material having a chemical composition of Sr 0.9925 Eu 0.005 Dy 0.0025 Al 1.80 Si 0.20 O 4 , with B 2 O 3 and Na 2 CO 3 as fluxes, the following amounts of material powders were each weighed. Then, an appropriate amount of alcohol was added and these materials were sufficiently wet- mixed in a ball mill for 24 hours. SrCO 3 2.930 g Al 2 O 3 1.836 g SiO 2 0.240 g Eu 2 O 3 0.018 g Dy 2 O 3 0.009 g B 2 O 3 0.139 g Na 2 CO 3 0.318 g The mixed powders were dried at 40°C and molded into a disc of diameter 13 mm under a load of 1,000 kg/cm 2 using a metal molding machine, and the disc was placed in an alumina crucible and burned in argon gas containing 3% hydrogen at 1,300°C for three hours using an electric furnace. This luminous storage was obtained by substituting Sr 0.9925 Eu 0.005 Dy 0.0025 for Ca 0.95 Eu 0.05 in the material of the chemical composition of Embodiment 3. FIG. 8 shows a powder X-ray diffraction chart of the sample obtained wherein CuKα rays were used. As in Embodiment 1, the figure shows that the sample obtained according to this embodiment had almost a single phase and was isomorphous with SrAl 2 O 4 . FIG. 9 (a) shows an emission spectrum of the sample when it was excited by 360-nm ultraviolet rays. This figure shows that the peak that provided a maximum luminescent intensity was a blue light emission located near 490 nm, in contrast to the peaks in the previous embodiments. In addition, FIG. 11 (a) shows an excitation spectrum. Then, the sample was excited at an excitation wavelength of 250 nm for 30 seconds, and temporal changes in the luminescent intensity of a 460-nm peak (persistence characteristic) were then measured. FIG. 13 (a) shows the results of the measurement. This figure indicates that activation with both Eu and Dy provides a bluish green luminous storage material instead of a blue luminous aluminum silicate storage material. Embodiment 8 To obtain a luminous storage material having a chemical composition of Sr 0.9925 Eu 0.005 Nd 0.0025 Al 1.80 Si 0.20 O 4 , with B 2 O 3 and Na 2 CO 3 as fluxes, the following amounts of material powders were each weighed. Then, an appropriate amount of alcohol was added and these materials were sufficiently wet- mixed in a ball mill for 24 hours. SrCO 3 2.930 g Al 2 O 3 1.836 g SiO 2 0.240 g Eu 2 O 3 0.018 g Nd 2 O 3 0.008 g B 2 O 3 0.139 g Na 2 CO 3 0.318 g The mixed powders were dried at 40°C and molded into a disc of diameter 13 mm under a load of 1,000 kg/cm 2 using a metal molding machine, and the disc was placed in a graphite crucible and burned in argon gas containing 3% hydrogen at 1,250°C for three hours using an electric furnace. This luminous storage material was obtained by substituting Nd 0.0025 for Dy 0.0025 in the material of the chemical composition of Embodiment 7. A powder X-ray diffraction chart of the sample obtained shows that the sample had almost a single phase and was isomorphous with SrAl 2 O 4 , just as in Embodiment 1. FIG. 9 (c) shows an emission spectrum of the sample when it was excited by 360-nm ultraviolet rays. This figure shows that the peak that provided a maximum luminescent intensity was a blue light emission located near 490 nm, as in Embodiment 7. In addition, FIG. 11 (c) shows an excitation spectrum. Then, the sample was excited at an excitation wavelength of 250 nm for 30 seconds, and temporal changes in the luminescent intensity of a 490-nm peak (persistence characteristic) were then measured. FIG. 13 (c) shows the results of the measurement. This figure indicates that activation with both Eu and Dy provides a bluish green luminous storage material, just as in Embodiment 7. Embodiment 9 The luminous storage material having the chemical composition Sr 0.9925 Eu 0.005 Dy 0.0025 Al 1.80 Si 0.20 O 4 was placed in an alumina crucible and burned in air at 850°C for six hours using an electric furnace. For comparison, material powders corresponding to the chemical formula Sr 0.9925 Eu 0.005 Dy 0.0025 Al 2 O 4 containing no Si were placed in an alumina crucible and burned in argon gas containing 3% hydrogen at 1,300°C for three hours using an electric furnace. The sample obtained was then burned in the same conditions as described above, that is, in the air at 850°C for six hours. This luminous storage material was confirmed to be a bluish green emission isomorphous with SrAl 2 O 4 and located near 490 nm both before and after burning at 850°C, as shown in Embodiment 7. FIGS. 14(a) and (b) show scanning-electron-microscopic (SEM) photographs of a broken-out section of the sample of Sr 0.9925 Eu 0.005 Dy 0.0025 Al 1.80 Si 0.20 O 4 before and after burning, and FIGS. 15(a) and (b) show scanning-electron-microscopic (SEM) photographs of a broken-out section of the sample of Sr 0.9925 Eu 0.005 Dy 0.0025 Al 2 O 4 before and after burning. FIGS. 14(a) and 15(a) are both photographs of the broken-out sections of the samples prior to burning at 850°C. This figure shows that the crystal grains in the sample containing Si had grown bigger than those in the sample containing no Si and that a glass phase was formed in the grain boundary of the sample containing Si. This is because both Ba 2 O 3 and Na 2 CO 3 , which were used as fluxes, reacted with silica to generate the glass phase. FIGS. 14(b) and 15(b) are both photographs of the broken-out sections of the samples after burning at 850°C. These figures show that the sample containing Si consisted of grains of almost the same size which were combined together via a glass phase. In addition, the luminance of a bluish green light emission located near 490 nm was confirmed to remain unchanged after burning at 850°C. In the sample containing Si, the surfaces of the grains were observed to have been thermally etched by the burning at 850°C. Furthermore, the results of powder X-ray diffraction showed few yellowish green light emissions despite the absence of structural changes. These results indicate that the sample containing Si is thermally stable. Furthermore, unlike the sample containing Si, the sample containing no Si has been found to be corroded easily by phosphoric acid or dilute hydrochloric acid, thus becoming porous. In addition, the emission characteristic of the sample without Si was also significantly degraded. Comparative Example 1 As Comparative Example 1, an SrAl 2 O 4 luminous storage material having a chemical composition Sr 0.995 Eu 0.005 Al 2 O 4 was produced using Eu 2+ for activation. B 2 O 3 and Na 2 CO 3 were added as fluxes and the following amounts of material powders were each weighed. An appropriate amount of alcohol was added and these materials were then sufficiently wet-mixed in a ball mill for 24 hours. SrCO 3 2.938 g Al 2 O 3 2.040 g Eu 2 O 3 0.018 g B 2 O 3 0.139 g Na 2 CO 3 0.318 g The mixed powders were dried at 40°C and molded into a disc of diameter 13 mm under a load of 1,000 kg/cm 2 using a metal molding machine, and the disc was mm under a load of 1,000 kg/cm 2 using a metal molding machine, and the disc was placed in an alumina crucible and burned in argon gas containing 3% hydrogen at 1,300°C for six hours using an electric furnace. FIG. 10 (d) shows an emission spectrum of the sample when excited by 360-nm ultraviolet rays, and FIG. 12 (d) shows an excitation spectrum. FIG. 13 (d) shows temporal changes in the luminescent intensity of a yellowish-green peak (persistence characteristic). FIG. 6 (2) shows a diffuse reflection spectrum. Comparative Example 2 As Comparative Example 2, an SrAl 2 O 4 luminous storage material of a chemical composition Sr 0.9925 Eu 0.005 Dy 0.0025 Al 2 O 4 was produced using both Eu 2+ and Dy 3+ for activation. B 2 O 3 and Na 2 CO 3 were added as fluxes and the following amounts of material powders were each weighed. An appropriate amount of alcohol was added and these materials were then sufficiently wet-mixed in a ball mill for 24 hours. SrCO 3 2.930 g Al 2 O 3 2.040 g Eu 2 O 3 0.018 g Dy 2 O 3 0.009 g B 2 O 3 0.139 g Na 2 CO 3 0.318 g The mixed powders were dried at 40°C and molded into a disc of diameter 13 mm under a load of 1,000 kg/cm 2 using a metal molding machine, and the disc was placed in an alumina crucible and burned in argon gas containing 3% hydrogen at 1,250°C for four hours using an electric furnace. FIG. 10 (b) shows an emission spectrum of the sample when excited by 360-nm ultraviolet rays, and FIG. 12 (b) shows an excitation spectrum. FIG. 13 (b) shows temporal changes in the luminescent intensity of a yellowish-green peak (persistence characteristic). As described above in detail, the aluminum silicate compound, which has a composition expressed by Formula (1), is a blue luminous material having a maximum luminescent intensity at 460 nm. In addition, the aluminum silicate compound having the composition expressed by Formula (2) is a bluish green luminous material having a maximum luminescent intensity at 490 nm. It is clear that these compounds have a persistence characteristic that is similar to or higher than that of the strontiumaluminate luminous storage material shown in the comparative examples. In addition, as shown in Embodiment 9, the present luminous storage material is thermally or chemically stable and has a high weather resistance. The luminance or persistence characteristic of this luminous storage material is unlikely to be degraded, so it can be used in severe conditions involving high temperatures and high moisture or in a solution containing acid.

Claims: A blue aluminium silicate luminous storage material activated by Eu 2+ , wherein the material has a formula: (M 1-n-m M* n Eu m ) (Al 1-x Si ¾x □ ¼x ) 2 O 4 - wherein □ is the deficiency; M is one or more alkali earth metal elements selected from the group of magnesium, calcium, strontium, and barium; M* is one or more bivalent metal elements selected from the group of manganese, zinc, and cadmium; and (n), (m) and (x) are molar values falling within the following ranges: 0 ≤ n ≤ 0.2 0 < x < 0.6 0.0001 ≤ m ≤ 0.1. A bluish green aluminium silicate luminous storage material activated by Eu 2+ and one or more rare earth elements Ln, wherein the material has a formula: (M 1-n-m-k M* n Eu m Ln k ) (Al 1-x Si ¾x □ ¼x ) 2 O 4 - wherein □ is the deficiency; M is one or more alkali earth metal elements selected from the group of magnesium, calcium, strontium, and barium; M* is one or more bivalent metal elements selected from the group of manganese, zinc, and cadmium; Ln is a rare earth element other than Eu; and (n), (m), (k) and (x) are molar values falling within the following ranges: 0 ≤ n ≤ 0.2 0 < x < 0.6 0.0001 ≤ m ≤ 0.1 0.0001 ≤ k ≤ 0.1. An aluminium silicate luminous storage material as claimed in Claim 2, wherein the molar value (k) of the rare earth element Ln is 1 to 50 mol% relative to Eu 2+ and wherein the rare earth element is Dy 3+ or Nd 3+ . An aluminium silicate luminous storage material as claimed in any preceding claim, wherein the molar value (n) of M* is in the range 0 ≤ n ≤ 0.05. An aluminium silicate luminous storage material as claimed in any preceding claim, wherein the molar value (m) of Eu 2+ is in the range 0.001 ≤ m ≤ 0.01. An aluminium silicate luminous storage material as claimed in any preceding claim, wherein the molar value (x) of silicon is in the range 0.1 ≤ x ≤ 0.45. A method of manufacturing a blue aluminium silicate luminous storage material as claimed in Claim 1, comprising mixing compounds containing M, M*, Al, Si and Eu in the ratio of formula 1 and sintering the mixture with sodium carbonate or boron oxide to obtain the luminous storage material. A method of manufacturing a bluish green aluminium silicate luminous storage material as claimed in Claim 2, comprising mixing compounds containing M, M*, Al, Si, Ln and Eu in the ratio of formula 2 and sintering the mixture with sodium carbonate or boron oxide to obtain the luminous storage material. A manufacturing method as claimed in Claim 7 or 8, wherein sintering is carried out in a reducing atmosphere at 800° to 1,400°C. A manufacturing method as claimed in any one of Claims 7 to 9, wherein the compounds are in powdered form, and wherein the powders are molded under a load of 1 to 5,000 kg/cm 2 using a moulding machine and are sintered to obtain a product. A manufacturing method as claimed in any one of Claims 7 to 10, wherein boron oxide is added as a flux.

Inventors: ENDO TADASHI, MO PINGFAN, ENDO, TADASHI, MO, PINGFAN
Applicants: READ CO LTD, READ CO., LTD.
Application year: 1998
Main classification: C09K11
IPC codes: C09K11