Photoluminescent polydisilacyclobutanes

Abstract: Photoluminescent polydisilacyclobutanes are made herein by reacting a dialkenyldihalocarbosilane with an organolithium reagent in the presence of a solvent at 0-25°C.

Description: This invention is directed to polycarbosilanes, and to polymers in which silicon atoms are linked through substituted alkylene bridges. The substituted polysil-alkylenes used herein are polydisilacyclobutanes with two different silacyclobutane units. The literature makes reference to processes using halosilanes containing a single unsaturated linkage. See, for example, Z. Anorg. Allg. Chem., Volume 558, pages 55-86, (1988); Chem. Ber., Volume 126. pages 575-580, (1993); and J. Prakt. Chem., Volume 337, pages 79-92, (1995). By using halosilanes containing two unsaturated linkages, as exemplified in Journal of Organometallic Chemistry, Volume 377, pages 175-195, (1989), we are able to produce higher molecular weight materials, i.e., polymers. While a recent article relative to certain silacyclobutanes has been published, the article does not describe polymers which replicate the polymer described herein. In particular, reference may be made to Chem. Eur. J., Volume 3, Issue 6, "Towards 2-Silaallenes: Synthesis of Spirocyclic Precursors", pages 948-957, (June 4, 1997). This invention refers to photoluminescent polydisilacyclobutanes of the structure where a is an integer having a value of 2 to 20; R14 to R18 are alkyl or aryl groups; R19 and R20 are alkoxy groups; and R11 to R14 and R21 and R22 represent a hydrogen atom or an alkyl group containing 2 to 10 carbon atoms. Preferably at least one of R11 or R12 and at least one of R13 or R14 and R21 and R22 represent an alkyl group containing 2 to 10 carbon atoms. The present invention also refers to a method of preparing of the polysilycyclobutanes of the present invention and to the polysilycyclobutanes obtainable by this method. These polydisilacyclobutanes are made by reacting an organolithium reagent with monomer where R1 is hydrogen or an alkyl group containing 2 to 10 carbon atoms; R2 and R3 represent halogen atoms; R4 and R5 represent independently at each occurrence an alkyl or aryl group; and R6 is an alkoxy group. Preferably R1 is hydrogen, R2 and R3 are chlorine and R4 and R5 are alkyl, most preferably methyl. Such monomers are made by methods generally described in Chem. Ber., Volume 126, pages 575-580, (1993). This invention is directed to methods of preparing polymers having low to medium degrees of polymerization based on a disilacyclobutane building block. The basic reaction involves using a divinyldichlorocarbosilane and tert-butyllithium to obtain the desired products. Unexpectedly, we found that these polymers exhibit strong photoluminescence in the blue region of the visible spectrum when excited by ultraviolet (UV) light with a wavelength of 337 nm (nanometer). Polymers representative of our invention are polydisilacyclobutanes with repeating unit where a is an integer having a value of 2 to 20; R14 to R18 are alkyl or aryl groups; R19 and R20 are alkoxy groups; and R11 to R14 and R21 and R22 represent a hydrogen atom or an alkyl group containing 2 to 10 carbon atoms. Preferably at least one of R11 or R12 and at least one of R13 or R14 and R21 and R22 represent an alkyl group containing 2 to 10 carbon atoms.These are linear polymers terminated by suitable alkyl, aryl, silyl, halogen or alkoxy groups. One species (I) of this genus is: Particles of species (I) where a = 10 were irradiated with UV light at a wavelength of 337 nm generated by a pulsed nitrogen laser with 0.1 mJ per pulse. Photoluminescence was bright whiteish blue. The process for making such polymers is shown below: Tert-butyllithium is shown as the preferred organolithium reagent. An example representing this process is set forth below to illustrate our invention in more detail. EXAMPLE Into a container were combined stoichiometric amounts of the unsaturated carbosilane and tert-butyllithium (mole ratio unsaturated carbosilane:tert-butyllithium = 1:2), in pentane as solvent, at 0°C. These reactants were heated to room temperature, i.e., 20-25°C. After removing the solvent, a yellow solid resulted. The yellow solid was identified as species (I) shown above, where e had a value of 10. For purification, a portion of the sample of species (I) was extracted with methanol. As a result, terminal chlorine atoms and t-butoxy groups in species (I) were replaced by methoxy groups, yielding a white powder where a also had a value of 10. Isolation of photoluminescent polydisilacyclo-butanes was conducted by extraction or precipitation by addition of alcohol. Polymers prepared according to our invention are useful as passive or active display materials, and in electroluminescent devices. In such utility, they are readily incorporated into road signs and lane markers. The polymers also find application in various types of displays as luminescent coatings for improving their visibility.

Claims: A photoluminescent polydisilacyclobutane with a repeating unit of the formula where a is an integer having a value of 2 to 20; R14 to R18 are alkyl or aryl groups; R19 and R20 are alkoxy groups; and R11 to R14 and R21 and R22 represent a hydrogen atom or an alkyl group containing 2 to 10 carbon atoms. Photoluminescent polydisilacyclobutanes according to claim 1, wherein at least one of R11 or R12 and at least one of R13 or R14 and R21 and R22 represent an alkyl group containing 2 to 10 carbon atoms. Photoluminescent polydisilacyclobutanes according to any of the preceding claims exhibiting photoluminescence in the blue region of the visible spectrum when excited by ultraviolet light. A method of making photoluminescent polydisilacyclobutanes comprising contacting an unsaturated carbosilane containing at least two silicon atoms, with an organolithium reagent in a solvent at a temperature of 0-25°C. A method according to claim 4 in which the unsaturated carbosilane containing at least two silicon atoms has the formula where R1 is hydrogen or an alkyl group containing 2 to 10 carbon atoms; R2 and R3 represent halogen atoms; R4 and R5 represent independently at each occurrence an alkyl or aryl group; and R6 is an alkoxy group. The method of claim 5, wherein R1 is hydrogen, R2 and R3 are chlorine and R4 and R5 are alkyl, preferably methyl. Photoluminescent polydisilacyclobutanes obtainable by the method of any of claims 4-6. A carbosilane of formula where R1 is hydrogen or an alkyl group containing 2 to 10 carbon atoms; R2 and R3 represent halogen atoms; R4 and R5 represent independently at each occurrence an alkyl or aryl group; and R6 is an alkoxy group. The carbosilan of claim 8, wherein R1 is hydrogen, R2 and R3 are chlorine and R4 and R5 are alkyl, preferably methyl.

Inventors: AUNER NORBERT, PERNISZ UDO C, AUNER, NORBERT, PERNISZ, UDO C.
Applicants: DOW CORNING, DOW CORNING CORPORATION
Application year: 1998
Main classification: C08G77
IPC codes: C09K11, C07F7, C08G77