POLYMERIZATION OF OLEFINS

Abstract: Ethylene can be polymerized, and optionally copolymerized with other selected olefins, using a polymerization catalyst system containing nickel and selected t-butyl substituted phosphines. Some of the resulting polymers have novel structures. The polymers are useful for films and molding resins.

Description: TITLE POLYMERIZATION OF OLEFINS This application claims the benefit of U.S. Provisional Application No. 60/044,144, filed April 22, 1997. FIELD OF THE INVENTION Cationic nickel complexes containing selected phosphine ligands can be used as part of polymerization catalysts for making polyethylene and certain copolymers of ethylene. Some of the polymers produced are novel. TECHNICAL BACKGROUND Olefin polymers, including homo- and copolymers of ethylene are important items of commerce, billions of kilograms being produced annually. Polyolefins are useful in many applications, such as molding resins for various articles, films for packaging and construction, elastomers, etc. These polyolefins are often made by using various catalysts containing transition metals. Which catalyst is used often is important in determining what the structure of the resulting polymer is, and is an important part of the cost of the polymer. Therefore new polymerization catalysts for olefms which will produce new polymers and/or lower costs are constantly being sought. G. Wilke in M. Tsutsui, Ed., Fundamental Research in Homogeneous Catalysis, Vol. 3, Plenum Press, New York, 1979, p. 1-24, at p. 15 reports the preparation of a "high molecular weight polyethylene" in which tris-t- butylphosphine and nickel are present. European Patent Application 454,231 A2 describes certain late metal catalysts for olefin polymerization. The t-butyl containing phosphines described herein are not mentioned in this reference. European Patent Application 381,495 A2 describes certain nickel ethylene polymerization catalysts containing an aminobis(imino)phosphorane ligand which make a polyethylene having only methyl andhexyl or longer branches. The catalysts and polymers described herein are not disclosed. World Patent Applications WO 96/37552 and WO 96/37523 describe the polymerization of various olefms using certain metals in combination with certain bidentate ligands. Specific combinations of nickel compounds with the ligands disclosed herein are not mentioned. World Patent Application WO 96/375536 describe compounds of Group VIIIB metals with certain Group VA element containing ligands. These compounds are said to be useful for making ethylene/carbon monoxide copolymers. B. Bogdanovic, et al., Ind. Eng. Chem., vol. 62, p. 34-44 (1970) describe the use of certain nickel-phosphine compounds as catalysts for the dimerization, oligomerization, etc., of certain olefms. Preparation of polymers is not described. U.S. Patent 3,265,622 describes a copolymer of ethylene and 4-methyl-l-hexene in which equal amounts of methyl and ethyl branches (as herein defined) may be present. There is no description of a polymer in which more than half the branches are ethyl. SUMMARY OF THE INVENTION This invention concerns a first process for the manufacture of a polyolefin, comprising, forming a polymerization catalyst system by contacting in an inert liquid: a first compound of the formula NiAQ (I) or L 5 L 6 NiAQ (VIII); a second compound of the formula (t-butyl)2PEP(t-butyl)2 (II) or (t-butyl)3P (III); and a third compound W (IV), which is a neutral Lewis acid capable of abstracting A " or Q " to form the anion WA " or WQ " , provided that WA " or WQ " is a weakly coordinating anion; and contacting said polymerization catalyst system with ethylene or a mixture of ethylene and one or more of an α-olefin, internal olefin, cyclopentene, a norbornene, or a styrene, provided that: said contacting with ethylene or a mixture of ethylene and an α-olefin, internal olefin, cyclopentene, a norbornene or a styrene is carried out at a temperature of about -20°C to about +70°C; when (t-butyl)3P is present one or more of an α-olefin, internal olefin, a styrene, a norbornene or cyclopentene is also present; when neither of Q and A are hydrocarbyl or hydride W is capable of transferring a hydrocarbyl or hydride group toNi; and wherein: L^ and \β are each independently monodentate weakly coordinating neutral ligands or L^ and \β taken together are a bidentate weakly coordinating neutral ligand; Q is a monovalent anion; A is monovalent anion; and E is -CH -, -O-, or -NH-. This invention also concerns a second process for the manufacture of a polyolefin, comprising, contacting in an inert liquid, at a temperature of about -20°C to about +70°C, a compound of the formula [L 1 L 2 L 3 L 4 Ni] + X " (VI) with ethylene or ethylene, and one or more of an α-olefin, internal olefin, cyclopentene, a norbornene, or a styrene, wherein: L 1 and L 2 taken together are (t-butyl)2PEP(t-butyl)2 (II), L 1 and L 2 are both (t-butyl)3P (III), or L 1 is (t-butyl)3P (III) and L 2 is an empty coordination site, ethylene or a neutral monodentate ligand that can be displaced by ethylene; E is -CH2-, -O-, or -NH-; L 3 and L 4 taken together are a π-allyl or a π-benzyl group; or L 3 is ethylene and L 4 i .s monoani .oni •c -R 1 R2 ; or L 3 i .s a monoanionic group which may 4 add across ethylene, and L is a neutral coordinating group which may be displaced by ethylene or L 4 is an empty coordination site about nickel; or L 3 and L^ taken together are a monoanionic oligomeric agostic group; X is a relatively noncoordinating anion; R! is a polymeric alkylene group; and R 2 is a polymer end group; and provided that when (t-butyl)3P is present one or more of an α-olefin, internal olefin, cyclopentene, a norbornene or a styrene is also present. This invention also includes a compound of the formula [L 1 L L 3 L Ni] + X- (VI) wherein: L 1 and L 2 taken together are (t-butyl)2PEP(t-butyl)2 (II), or L 1 and L 2 are both (t-butyl)3P (III), or L 1 is (t-butyl P (III) and L 2 is an empty coordination site, ethylene or a neutral monodentate ligand that can be displaced by ethylene; E is -CH2-, -O-, or -NH-; \J> and y taken together are a π-allyl or a π-benzyl group; or Lr> is ethylene and L 4 is monoanionic -R^R 2 ; or lβ is a monoanionic group which may add across ethylene, and L 4 is a neutral coordinating group which may be displaced by ethylene or L 4 is an empty coordination site about nickel; or L 3 and 4 L taken together are a monoanionic oligomeric agostic group; X is a relatively noncoordinating anion; R is a polymeric alkylene group; and 2 R is a polymer end group; and provided that when (t-butyl)3P is present a repeat unit derived from cyclopentene, a norbornene or a styrene is also present in R . Also disclosed herein is a polyolefin containing ethyl branches, wherein at least 53 percent of said ethyl branches are part of sec-butyl ended branches, and provided that said polyolefin has at least 50 branches per 1000 methylene groups. This invention also includes polyethylene or a copolymer of ethylene and one or more of an α-olefin, internal olefin, cyclopentene, a norbornene, or a styrene in which at least 53 percent of alkyl branches are ethyl branches, and provided that said ethylene or a copolymer of ethylene and a styrene or cyclopentene has at least about 1.0 branch per 1000 methylene groups. Also disclosed herein is a copolymer of one or more norbornenes and ethylene containing at least about 2.0 methyl groups which are branch ends per one thousand methylene groups. DETAILS OF THE INVENTION Herein certain terms are used to define certain chemical groups or compounds. These terms are defined below. • A "hydrocarbyl group" is a univalent group containing only carbon and hydrogen. If not otherwise stated, it is preferred that hydrocarbyl groups herein contain 1 to about 30 carbon atoms. • By "substituted hydrocarbyl" herein is meant a hydrocarbyl group which contains one or more substituent groups which are inert under the process conditions to which the compound containing these groups is subjected. The substituent groups also do not substantially interfere with the process. If not otherwise stated, it is preferred that substituted hydrocarbyl groups herein contain 1 to about 30 carbon atoms. Included in the meaning of "substituted" are heteroaromatic rings. Suitable substituents include halo, ester, keto (oxo), amino, imino, thioether, amide, and ether. Preferred substituents are halo, ester and ether. • By an "α-olefin" is meant a compound of the formula CH2=CHR12, wherein R12 is saturated hydrocarbyl, preferably alkyl, and more preferably n-alkyl. It is preferred that R12 have 1 to 20 carbon atoms, more preferably 1 to 12 carbon atoms. • By an "internal olefin" is meant a compound of the formula R13R14C=CR15R16 wherein R13 and R15 are each independently alkyl, and R14 and R16 are each independently alkyl or hydrogen. It is preferred that R14 and R16 are hydrogen. In the internal olefin it is preferred that any alkyl groups contain 1 to 20 carbon atoms, more preferably 1 to 10 carbon atoms. • By an "inert liquid" which does not substantially interfere with active catalyst formation (if appropriate) or polymerization. The catalyst and/or catalyst ingredients and/or monomer(s) do not necessarily have to be soluble in the inert liquid but it is preferred that they be at least slightly soluble in the inert liquid. Suitable inert liquid for use herein include hydrocarbons, and perfluorocarbons. Specific useful inert liquids include toluene, benzene, cyclopentene (which may copolymerize), methylene chloride and hexane. • By an "alkyl aluminum compound" is meant a compound in which at least one alkyl group is bound to an aluminum atom. Other groups such as alkoxide, oxygen, and halogen may also be bound to aluminum atoms in the compound. • By "neutral Lewis base" is meant a compound, which is not an ion, which can act as a Lewis base. Examples of such compounds include ethers, amines, sulfides, and organic nitriles. • By "neutral Lewis acid" is meant a compound, which is not an ion, and which can act as a Lewis acid. • By a "neutral ligand" is meant a ligand which is not an ion, i.e., is electrically neutral. • By "being able to be displaced by ethylene" is meant a ligand that may be displaced from a coordinating metal atom by ethylene. • By a "weakly coordinating ligand" is meant a ligand that is relatively easily displaced from a nickel atom, as by (II) or (III). • By the "compound HX" is meant the acid of a (relatively) noncoordinating monoanion, or the equivalent thereof, i.e., a combination of compounds that will generate this acid. Noncoordinating anions are well known to the artisan, see for instance W. Beck., et al., Chem. Rev., vol. 88, p. 1405-1421 (1988), and S. H. Strauss, Chem. Rev., vol. 93, p. 927-942 (1993), both of which are hereby included by reference. Relative coordinating abilities of such noncoordinating anions are described in these references, Beck at p. 1411, and Strauss at p. 932, Table III. Also useful in this process in place of HX are "solid" acids, such as acidic aluminas, clays and zirconias, which are considered herein to be acids with relatively non-coordinating anions. Preferred relatively noncoordinating anions X are BF4", PFβ", BAF, {tetrakis[2,6-bis(trifluoromethyl)phenyl]borate} , trifluoromethanesulfonate, toluenesulfonate, and trifluoroacetate, and BAF is especially preferred. The acids of these anions are known, for instance HBF4 is commercially available, and HBAF can be made by the method described in M. Brookhart, et al., Organometallics, vol. 11, p. 3920-3922 (1992). • By a "π-allyl group" is meant a monoanionic with 3 adjacent sp2 carbon atoms bound to a metal center in an η 3 fashion. The three sp2 carbon atoms may be substituted with other hydrocarbyl groups or functional groups. Typical π-allyl groups include CO .R wherein R is hydrocarbyl. • By a "π-benzyl group" is meant π-allyl ligand in which two of the 2 sp carbon atoms are part of an aromatic ring. Typical π-benzyl groups include π-Benzyl compounds usually initiate polymerization of the olefins fairly readily even at room temperature, but π-allyl compounds may not necessarily do so. Initiation of π-allyl compounds can be improved by using one or more of the following methods: - Using a higher temperature such as about 80°C. - Decreasing the bulk of the α-diimine ligand. such as R 2 and R 5 being 2,6-dimethylphenyl instead of 2,6-diisopropylphenyl. - Making the π-allyl ligand more bulky, such as using rather than the simple π-allyl group itself. - Having a Lewis acid present while using a functional π-allyl or π- benzyl group. Relatively weak Lewis acids such a triphenylborane, tris(pentafluorophenyl)borane, and tris(3,5-trifluoromethylphenyl)borane, are preferred. Suitable functional groups include chloro and ester. "Solid" acids such as montmorillonite may also be used. The olefins polymerized herein are ethylene, a styrene, a norbornene and cyclopentene. By "a styrene" herein is meant a compound of the formula wherein R , R , R , R and R are each independently hydrogen, hydrocarbyl, substituted hydrocarbyl or a functional group, all of which are inert in the polymerization process. It is preferred that all of R , R R , R and R are hydrogen, i.e. (VII) is styrene. By "a norbornene" is meant that the monomer is characterized by containing at least one norbornene-functional group in its structure including norbornadiene as identified by the formulas below, which can be substituted or unsubstituted (XXXIV) wherein "a" represents a single or double bond. Representative monomers are compounds (XXXV) and (XXXX) as follows: (XXXIV); (XXXX) wherein R , R , R , and R independently are hydrogen halogen, or hydrocarbyl, provided that, except if the hydrocarbyl group is vinyl, if any of the hydrocarbyl are alkenyl, there is no terminal double bond, i.e., the double bond is internal; or R and R taken together can be part of carbocyclic ring (saturated, unsaturated or aromatic); or R and R and/or R and R taken together are an alkylidene group. In these structures "z" is 1 to 5. Examples of such norbomenes include norbornadiene, 2-norbornene, 5- methyl-2-norbornene, 5-hexyl-2-norbornene, 5-ethylidene-2-norbornene, vinylnorbornene, dicyclopentadiene, dihydrodicyclopentadiene, tetracyclododecene, trimers of cyclopentadiene, halogenated norbomenes wherein R , R , R and R may also be halogen or fully halogenated alkyl groups such as C w F2w+l wherein w is 1 to 20, such as perfluoromethyl and perfluorodecyl. It is also preferred that in the polymerization processes described herein that the polymer produced has an average degree of polymerization of about 10 or more, more preferably about 20 or more, and especially preferably about 50 or more. When one or more norbomenes is copolymerized with ethylene a polymer having branching in the ethylene derived segments may be produced. This branching is easily detected by determining the amount of methyl groups in the polymer present in the ethylene derived polymer segments. That is, methyl groups that were originally part of a norbornene, such as in 4,5-dimethylnorbornene are not counted for the purposes of this branching. It is preferred that there are at least about 3.0, more preferably at least about 5.0 methyl groups per 1000 methylene groups (-CH 2 -). It is also preferred that at least about 0.5 (per 1000 methylene groups) of the branches be ethyl branches, and/or at least about 1.0 of the branches be amyl or longer. These branches are readily detected by NMR methods described below. In the first polymerization process for manufacturing an olefin, the compound NiAQ (I) may be used. This is a nickel[II] compound. Useful anions for A and Q are chloride, bromide, iodide, carboxylate such as octoate or acetate, and acetylacetonate. A preferred anion for A and Q is acetylacetonate. An _r alternative compound is L L NiAQ (VIII). Preferred A and Q anions in this compound are the same as listed above, plus alkyl, especially methyl, and hydride. L and L are weakly coordinating monodentate ligands or a bidentate ligand. For instance a useful compound (VIII) is (l,2-dimethoxyethane)NiBr2- A useful __ ■ c monodentate ligand for L and L is tetrahydrofuran, while useful bidentate ligands include 1 ,2-dimethoxyethane, N,N,N'N'-tetramethylethylenediamine and 1,5-cyclooctadiene. In (II) it is preferred that E is -CH2-. The molar ratio of (II):(I) or (M):(I) in the first polymerization process is not critical, since with any reasonable concentrations active catalysts will be formed. However, in order to most efficiently utilize the starting materials it is preferred that the molar ratio of (II):(I) is about 1, and the molar ratio of (III):(I) is about 1 to about 2. The first polymerization process is carried out at a temperature of about 0°C to about 120°C, preferably about 25°C to about 100°C, when (II) is present, while the temperature is about -80°C to about 100°C, preferably about 0°C to about 80°C when (III) is present. It is also preferred that the process mixture be stirred for uniform and reasonably rapid polymerization. The (ethylene) pressure in the first polymerization process is not critical, atmospheric pressure to about 150 MPa being a useful pressure range. The third compound in the first polymerization process, W, is a neutral Lewis acid that can abstract A " or Q " from (I) to form WA " or WQ " , respectively. An equation may be written as: NiAQ + W → [NiA] + [WQ] " (1) Useful Lewis acids for this abstraction include B(C6F5)3, AICI3, MgCl2 and methyl aluminoxane. If a hydrocarbyl anion, preferably an alkyl anion, more preferably a methyl anion, or a hydride anion is not bound to the nickel atom of (I), W (or another W) must also transfer a hydrocarbyl or hydride anion to the nickel atom. Such an equation, using for instance and alkyl aluminum compound as W, may be written as: NiAQ + R2 9 A1C1 → [NiR 9 ] + [R 9 A1C1AQ] " (2) 9 This equation is shown using only one molecule of R2 A1C1. Essentially the same effect can be obtained by using one molecule of the alkyl aluminum o compound to place the R group on the nickel, and another molecule to abstract the A anion. Preferred neutral Lewis acids for transferring a hydrocarbyl group to the nickel atom are alkyl aluminum compounds. Suitable alkyl aluminum 8 compounds include alkyl aluminum sesquioxides [(R AlO) n ], especially wherein g R is methyl. Alkyl aluminum sesquioxides are preferred alkyl aluminum compounds. W can also constitute a mixture of two compounds, a strong Lewis acid such as B(C6F5)3 and an alkylating agent such as triethylaluminum. A stoichiometric or larger amount of the neutral Lewis acid is preferred, and a more preferred molar ratio of W:(I) is about 1 to about 100. The ethylene may be copolymerized with cyclopentene and/or a styrene. Styrene itself is a preferred styrenic monomer. Increasing the concentration of a comonomer (with ethylene) will usually increase the amount of repeat derived from that comonomer in the product polymer. In the second polymerization process herein the same conditions are preferred as are preferred for the first polymerization process, including the monomers used and polymers produced. It is preferred that the second polymerization process be carried out in an inert liquid, but may also be carried out by other methods, such as heterogeneously from a liquid or solid and a gas such as ethylene, or living polymer particles and a gas such as ethylene. The catalyst or active polymerization site may be on a support such as alumina or zirconia. Such methods of carrying out olefin polymerizations are known in the art. In the second polymerization process compound (VI) is used as the polymerization catalyst. (VI) may be added directly to the polymerization process, may be formed in situ before the polymerization starts, or may be formed after the polymerization starts, i.e., is a polymerization intermediate. Methods for making (VI) are analogous to those reported in World Patent Application 96/23010, published August 1, 1996. In that Application nickel complexes of α-diimines of other nitrogen ligands are made for use in polymerizations. The analogous complexes of (II) and (III) can be made by methods similar to those described in WO 96/23010. For instance, equation (2) above shows the partial formation of a compound of formula (VI). In the presence of (II) or (III), (II) or (III) would become L 1 and L2 of (VI), R 9 is L 3 , a monoanionic group which can add across 4 , ethylene, and L is an empty coordination site about nickel. If the reaction of equation (2) were carried out in a solvent such as diethyl ether, the ether may 4 become L , a neutral coordinating group which may be displaced by ethylene. Methods for making (VI) include: Reaction of the compound (XIII) with either (II) or (III) and MX, wherein M is monovalent metal such as sodium and X is a relatively non-coordinating anion. Reaction of (tmeda)NiMe2 with (II), followed by reaction either HX (wherein X is a relatively non-coordinating anion) or a Lewis base which can form a relatively non-coordinating anion upon abstraction of methyl, such as B(C6F5)3. Groups which are anionic and can add across ethylene or other olefins include hydrocarbyl including allyl, benzallyl and vinyl, and hydride. Preferred groups which can add across ethylene or other olefins are alkyl containing 1 to 4 carbon atoms and hydride, and methyl is especially preferred. W Whheenn : L 3 is ethylene and L 4 is monoanionic -R 1 R2 , (VI) may be represented as \ κ Ni H 2 C (IX) 2 and may be thought of as a "living" polymer. The R group, which is the end group for a polymer "fragment" -R 1 R 2 may be thought of as arising from the original group on nickel which added across an ethylene (or other olefin) molecule. The R part of the molecule is one or more repeat units of a polymer (or incipient polymer) such an ethylene repeat units, for example represented by the formula -(CH2CH2)χ- wherein x is an integer of 1 or more. The ethylene molecule coordinated to the nickel atom in (IX) may add across the Ni-R bond, and another olefin molecule may coordinate to the nickel atom, thereby continuing the polymerization. Another potential form of living ended polymer is a so-called agostic living end. This may be of the type (X) wherein each R is independently hydrocarbyl or substituted hydrocarbyl. It is believed that this form of living end may be favored when the olefin end group is a cyclic olefin such as cyclopentene, and both of R taken together form a ring. For instance if the end group were derived from cyclopentene, both of R taken together would be -(CH2)3-. When (III) is used in a catalyst system herein to make polyethylene or a copolymer of ethylene, the polymer may have an exceptionally high proportion of ethyl branches. When (III) is present in the catalyst system, homopolyethylene may be produced, as well as copolymers of ethylene. The homopolyethylenes are produced in essentially the same way as the ethylene copolymers. Completely linear homopolyethylene of course has no branches, but if one makes branched homopolyethylene, it usually has a distribution of branches containing 1 to many carbons. Although ethyl branches are often found in such polymers, they usually don't constitute a high percentage of the total branches present (for a method of measuring and calculating branch numbers and size, see the section on NMR polymer analysis just before the Examples). Some of the polymers made by catalysts containing (II) have been found to contain an exceptionally high proportion of ethyl branches. Novel polymers herein have at least about 1.0 or more total branches, preferably at least about 5 or more total branches per 1000 methylene groups, and at least about 50 percent of those branches, preferably at least about 65 percent of those branches are ethyl branches. Note that the percentage of ethyl branches is based on the total number of branches (methyl groups) including ethyl groups present, and not on the total number of carbon atoms in the total branches or ethyl branches present. When (II) is used in the catalysts described herein to make homopolyethylene or copolymers of polyethylene the resulting polymers sometimes have an exceptionally large proportion of ethyl branches in sec-butyl [-CH(CH3)CH2CH3] ended branches. For a definition of "branch" herein see below. The sec-butyl group may be on the end of a branch such as (XII) wherein v represents the "main chain" (in highly branched polymers what is the "main chain" may be more of a semantic argument) of the polymer, and x is an integer of 2 or more. Such polymer may have about 50 or more total branches, preferably about 75 to about 160 total branches per 1000 methylene groups, and at least about 53% percent of the ethyl branches present, preferably at least about 58 percent of those ethyl branches are part of sec -butyl ended branches. The polyethylenes with relatively high level of sec-butyl ended branches or ethyl branches may be homopolyethylenes or copolymers of ethylene with cyclopentene and/or a styrene. Neither the pendant phenyl rings nor the cyclic units derived from cyclopentene shall be considered "branches" for the purposes of calculating amounts of branches and branch types in these polymers. Similarly, if a styrene has one or more alkyl groups substituted on the phenyl ring, these alkyl groups are not considered branches or parts of branches. The polymerization processes herein may be run in the presence of various liquids, particularly aprotic organic liquids. The catalyst system, ethylene, and polyethylene may be soluble or insoluble in these liquids, but obviously these liquids should not prevent the polymerization from occurring. Suitable liquids include alkanes, cycloalkanes, selected halogenated hydrocarbons, and aromatic hydrocarbons. Specific useful solvents include hexane, toluene and benzene. The ethylene polymerizations herein may also initially be carried out in the solid state by, for instance, supporting the transition metal compound on a substrate such as silica or alumina, activating it (if necessary) with the Lewis (such as W, for instance an alkylaluminum compound) or Bronsted acid and exposing it to ethylene. Alternatively, the Lewis acid such as an alkylaluminum compound may be reacted first with a support such as silica or a magnesium halide and then the transition metal containing compound added. The support may also be able to take the place of the Lewis or Bronsted acid, for instance an acidic clay such as montmorillonite. Another method of making a supported catalyst is to start a polymerization or at least make a transition metal complex of another olefin or oligomer of an olefin such as cyclopentene on a support such as silica or alumina. These "heterogeneous" catalysts may be used to catalyze polymerization in the gas phase or the liquid phase. By gas phase is meant that the ethylene is transported to contact with the catalyst particle while the ethylene is in the gas phase. The polymerization catalyst systems described above may be used in conjunction with other types of polymerization catalysts. This could include two different polymerization catalysts as described above, but more commonly other types of catalysts may also be used for the second active polymerization catalyst. For instance so-called Ziegler-Natta and/or metallocene-type catalysts may also be used. These types of catalysts are well known in the polyolefin field, see for instance Angew. Chem., Int. Ed. Engl., vol. 34, p. 1143-1170 (1995), European Patent Application 416,815 and U.S. Patent 5,198,401 for information about metallocene-type catalysts, and J. Boor Jr., Ziegler-Natta Catalysts and Polymerizations, Academic Press, New York, 1979 for information about Ziegler- Natta-type catalysts, all of which are hereby included by reference. Suitable late metal transition catalysts will be found in World Patent Applications 96/23010 and 97/02298, both of which are hereby included by reference, and U.S. Patent Applications 08/991,372, filed December 16, 1997, and 09/006,536, filed January 13, 1998, both of which are hereby included by reference. Many of the useful polymerization conditions for these types of catalyst and the first active polymerization catalysts coincide, so conditions for the polymerizations with first and second active polymerization catalysts are easily accessible. Oftentimes the "co-catalyst" or "activator" is needed for metallocene of Ziegler-Natta-type polymerizations, much as W is sometimes needed for polymerizations using the first active polymerization catalysts. In many instances the same compound, such as an alkylaluminum compound, may be used for these purposes for both types of polymerization catalysts. The polymers made by the first active polymerization catalyst and the second active polymerization catalyst may be made in sequence, i.e., a polymerization with one (either first or second) of the catalysts followed by a polymerization with the other catalyst, as by using two polymerization vessels in series. However it is preferred to carry out the polymerization using the first and second active polymerization catalysts in the same vessel(s), i.e., simultaneously. This is possible because in most instances the first and second active polymerization catalysts are compatible with each other, and they produce their distinctive polymers in the other catalyst's presence. The polymers produced by using two or more polymerization catalysts may vary in molecular weight and or molecular weight distribution and/or melting point and/or level of crystallinity, and/or glass transition temperature or other factors. For copolymers the polymers may differ in ratios of comonomers if the different polymerization catalysts polymerize the monomers present at different relative rates. The olefin monomer(s) may also be a single olefin or a mixture of olefins to make a copolymer. Again it is preferred that they be identical, particularly in a process in which polymerization by the first and second polymerization catalysts make polymer simultaneously. In some processes with two or more catalysts a first active polymerization catalyst may polymerize a monomer that may not be polymerized by a second active polymerization catalyst, and/or vice versa. In that instance two chemically distinct polymers may be produced. In another scenario two monomers would be present, with one polymerization catalyst producing a copolymer, and the other polymerization catalyst producing ahomopolymer, or two copolymers may be produced which vary in the molar proportion or repeat units from the various monomers. Other analogous combinations will be evident to the artisan. In the Examples, and in general, the following procedure was used to quantitatively determine branching, the distribution of branch lengths in the polymers (but not necessarily the simple number of branches as measured by total number of methyl groups per 1000 methylene groups), and other microstructure information about the polymers described herein. 100 MHz ^C NMR spectra were obtained on a Varian Unity 400 MHz spectrometer using a 10 mm probe on typically 10-20 wt% solutions of the polymers and 0.05 M Cr(acetylacetonate)3 in 1 ,2,4-trichlorobenzene (TCB) unlocked at 120- 140°C using a 90 degree pulse of 16 to 18 μsec, a spectral width of 35 kHz, a relaxation delay of 5-10 s, an acquisition time of 0.64 sec and inverse gated decoupling. Samples were preheated for at least 15 min before acquiring data. Data acquisition time was typically 10 h per sample. The T^ values of the carbons were measured under these conditions to be all less than 0.9 s. The longest T^ measured was for the Bu + , end of chain resonance at 14 ppm, which was 0.84 s. Some samples were run in chloroform-dl, CDCl3-dl, (locked) at 30°C under similar acquisition parameters. T^'s were also measured in CDCI3 at ambient temperature on a typical sample with 0.05 M Cr(acetylacetonate)3 to be all less than 0.68 s. Spectra are referenced to the solvent - either the TCB high field resonance at 127.9 ppm or the chloroform-dl triplet at 77 ppm. A DEPT 135 spectrum was done on most samples to distinguish methyls and methines from methylenes. Methyls were distinguished from methines by chemical shift. EOC is end-of-chain. Assignments reference to following naming scheme: 1. xBy: By is a branch of length y carbons; x is the carbon being discussed, the methyl at the end of the branch is numbered 1. Thus the second carbon from the end of a butyl branch is 2B4. Branches of length y or greater are designated as y + . 2. xCBy: CBy is a comonomer ended branch containing y methylenes between the 'blocking carbon' (quaternary carbon, non-protonated carbon) and the next nearest methine away from the functional group, x is the carbon being discussed; the methylene closest to the blocking carbon is labeled 1. 3. The methylenes in the backbone are denoted by a capital S and with Greek letters which determine how far from a branch point methine each methylene is. Thus S beta beta denotes the central methylene in the following structure: RCHRCH2CH2CH2CHRR. Gamma+ refers to methylenes gamma and further from a branch point. 4. When x in xBy or xCBy is replaced by a T, the methine carbon of that branch is denoted. 5. A T followed by two Greek letters indicates a methine carbon and how far away the next methine is. An M followed by two Greek letters indicates a methyl branch and the distance to the two neighboring branch points. For example, the methyls and methines in a highly stereo-regular polypropylene would be denoted P beta beta and T beta beta. Integrals of unique carbons in each branch were measured and were reported as number of branches per 1000 methylenes (including methylenes in the backbone and branches, and in comonomer ended branches). These integrals are accurate to +/- 5% relative for abundant branches and +/- 10 or 20% relative for branches present at less than 10 per 1000 methylenes. Such types of analyses are generally known, see for instance "A Quantitative Analysis of Low Density (Branched) Polyethylenes by Carbon- 13 Fourier Transform Nuclear Magnetic Resonance at 67.9 MHz", D. E. Axelson, et al., Macromolecules 12 (1979) pp. 41-52; "Fine Branching Structure in High- Pressure, Low Density Polyethylenes by 50.10-MHz 13C NMR Analysis", T. Usami et al., Macromolecules 17 (1984) pp. 1757-1761; and "Quantification of Branching in Polyethylene by 13C NMR Using Paramagnetic Relaxation Agents", J. V. Prasad, et al., Eur. Polym. J. 27 (1991) pp. 251-254 (Note that this latter paper is believed to have some significant typographical errors in it). It is believed that in many of the polymers described herein which have unusual branching, i.e., they have more or fewer branches than would be expected for "normal" coordination polymerizations, or the distribution of sizes of the branches is different from that expected, that "branches on branches" are also present. By this is meant that a branch from the main chain on the polymer may itself contain one or more branches. It is also noted that the concept of a "main chain" may be a somewhat semantic argument if there are sufficient branches on branches in any particular polymer. By a polymer hydrocarbyl branch is meant a methyl group to a methine or quaternary carbon atom or a group of consecutive methylenes terminated at one end by a methyl group and connected at the other end to a methine or quaternary carbon atom. The length of the branch is defined as the number of carbons from and including the methyl group to the nearest methine or quaternary carbon atom, but not including the methine or quaternary carbon atom. If the number of consecutive methylene groups is "n" then the branch contains (or the branch length is) n+1. Thus the structure (which represents part of a polymer) -CH2CH2CH[CH2CH2CH2CH2CH(CH3)CH2CH3]CH2CH2CH2CH2- contains 2 branches, a methyl and an ethyl branch. The l^C NMR peaks for copolymers of cyclopentene and ethylene are described based on the labeling scheme and assignments of A. Jerschow et al, Macromolecules 1995, 28, 7095-7099. The triads and pentads are described as 1-cme, 1,3-ccmcc, 1,3-cmc, 2-cme, 2-cmc, l,3-eme,3-cme, and 4,5-cmc, etc, where e = ethylene, c = cyclopentene, and m = meta cyclopentene (i.e. 1 ,3 enchainment). The compound (t-Bu)2PCH2P(t-Bu)2 can be synthesized according to the following published procedure: Karsch, H. H. and Schmidbaur, Z. Naturforsch. 1977, 32b, 762. P(t-Bu)3 can be purchased from Strem Chemicals (Newburyport, MA, U.S.A.). Ni(acac)2 (acac = acetylacetonate) can be purchased from the Aldrich Chemical Company (Milwaukee, WI, U.S.A.). In the Examples, the following abbreviations are used: acac - acetylacetonate Bu - butyl DME - 1 ,2-dimethoxyethane GPC - Gel Permeation Chromatography Me - methyl Mn - number average molecular weight Mw - weight average molecular weight PD - polydispersity, Mw/Mn PE - polyethylene TCB - trichlorobenzene TCE - trichloroethylene tmeda - N,N,N',N'-tetramethylethylenediamine In the Examples, all pressures are gauge pressures unless otherwise noted. Example 1 An evacuated 100 mL autoclave was charged with a solution of Ni(acac)2 (26 mg, 0.10 mmol) and (t-Bu)2PCH2P(t-Bu)2 (30 mg, 0.10 mmol) in 40 mL of toluene under nitrogen. To this mixture was then added modified methyl aluminoxane (5.00 mmol) in toluene (10 mL) under 690 kPa of ethylene. The resulting reaction mixture was stirred at 700 rpm under 690 kPa of ethylene for 18.5 h. During this time the reaction temperature remained at 29-30°C. Ethylene pressure was then vented and the reaction mixture quenched under air by the addition of 50 mL of isopropanol. The resulting mixture was then stirred in a beaker with 100 mL of methanol plus 10 mL concentrated HCl. Finally, 200 mL of water was added and an oil separated from the solution. The mixture was then transferred to a separatory funnel and the oil separated from the aqueous phase. The aqueous phase was extracted with 3 x 100 mL of hexane, and the hexane extracts combined with the oil. The resulting solution was dried (MgSO4) and concentrated in vacuo to afford 13.4 g of amorphous polyethylene as a viscous, clear, colorless oil. The branching distribution was quantified by 13 C NMR. Branching per 1000 CH2: Total methyls (139), Methyl (82), Ethyl(22.3), Propyl (2.1), Butyl (9.7), Amyl (0.9), ≥Hex and end of chains (21.6), >Am and end of chains (23.8), >Bu and end of chains (32.6). DSC: T m = -42°C, T g = -67°C. GPC (in tetrahydrofuran vs. polystyrene): Mn = 11 ,400; M w = 16,800; M w /M n = 1.47. The following Table gives the 13 C NMR spectrum of the polymer obtained, together with known assignments. Example 2 An evacuated 100 mL autoclave was charged with a solution of Ni(acac)2 (18 mg, 0.07 mmol) and P(t-Bu)3 (29 mg, 0.14 mmol) in 42 mL of toluene under nitrogen. To this mixture was then added modified methyl aluminoxane (3.5 mmol) in toluene (10 mL) under 690 kPa of ethylene. The resulting reaction mixture was stirred at 7 min. During this time the reaction temperature increased from 27 to 45 C. Ethylene pressure was then vented and the reaction mixture quenched and the product precipitated by the addition of 25 mL of isopropanol under air. The resulting mixture was transferred to a beaker and stirred with 100 mL of methanol plus 10 mL concentrated HCl. The product polymer was filtered off and washed with methanol and a 2 wt. % solution of Irganox® 1010 in acetone. The polymer was dried to afford 4.07 g of polyethylene as a white powder. DSC: Tm = 105°C (ΔHf = 74 J/g). Quantitative 13 C NMR indicated that this sample contained 26 methyl-ended branches per 1000 methylenes. The distribution of branches was as follows (branches per 1000 methylenes): Methyl (~0), Ethyl (20.8), Propyl (not determined), Butyl (2.5), Amyl (.l), ≥Hexyl and end of chains (1.8), ≥Amyl and end of chains (2.1), ≥Butyl and end of chains (5.2). DSC: T m - 105°C (74 J/g). GPC (in tetrahydrofuran vs. polystyrene): Mn = 6,210; M w = 15,000; M w /M n = 2.42. TThhee ffoolllloowwiinngg TTaabbllee ggiivveess tthhee NMR spectrum of the polymer obtained, together with known assignments Example 3 A 100 mL autoclave was charged with a solution of Ni(acac)2 (73 mg, 0.28 mmol) and P(t-Bu)3 (1 15 mg, 0.57 mmol) in cyclopentene (50 mL). To this mixture was then added modified methyl aluminoxane (14.2 mmol) in toluene (7 mL) under 690 kPa of ethylene. The reaction mixture was stirred under 690 kPa of ethylene for 30 min, during which time the reaction temperature varied between 27 and 46 C. Ethylene pressure was then vented and the reaction worked up using the same procedure as in Example 2 to afford 5.03 g of ethylene/cyclopentene copolymer as a white solid. Quantitative 13 C NMR indicated that the polymer contained 46.7 mole % ethylene, 8.3 mole % cis- 1,2- enchained cyclopentene, and 45.0 mole % cis- 1,3 -enchained cyclopentene units. Example 4 A 100 mL autoclave was charged with a solution of Ni(acac)2 (18 mg, 0.07 mmol), P(t-Bu)3 (29 mg, 0.14 mmol), cyclopentene (10 mL, 114 mmol), and toluene (32 mL). To this mixture was then added modified methyl aluminoxane (3.54 mmol) in toluene (10 mL) under 690 kPa of ethylene. The reaction mixture was stirred under 690 kPa of ethylene for 7 min, during which time the reaction temperature varied between 23 and 39 C. Ethylene pressure was then vented and the reaction worked up using the same procedure as in Example 2 to afford 3.94 g of ethylene/cyclopentene copolymer as a white solid. DSC: Tm = 85 C (41 J/g). Quantitative 13 C NMR indicated that the polymer contained 81.8 mole % ethylene, 4.7 mole % cis-l,2-enchained cyclopentene, and 13.4 mole % cis- 1,3- enchained cyclopentene units. GPC (in trichlorobenzene vs. polyethylene): M n = 14,000; M w = 28,900; M w /M n = 2.07. Example 5 A 100 mL autoclave was charged with a solution of Ni(acac)2 (73 mg, 0.28 mmol), P(t-Bu)3 (115 mg, 0.57 mmol), styrene (5.00 g, 48.0 mmol), and toluene (50 mL). To this mixture was then added modified methyl aluminoxane (14.2 mmol) in toluene (7 mL) under 690 kPa of ethylene. The reaction mixture was stirred under 690 kPa of ethylene for 11 min, during which time the reaction temperature varied between 27 and 39 C. Ethylene pressure was then vented and the reaction mixture quenched by addition of 50 mL of isopropanol under air. The resulting mixture was transferred to a beaker with 200 mL methanol plus 20 mL concentrated HCl. The precipitated polymer was filtered, washed further with methanol, and dried to afford 2.50 g of ethylene/styrene copolymer. DSC: Tm = 86°C (45 J/g). GPC (trichlorobenzene vs. linear polyethylene, 135°C): Mn = 17,700; Mw = 34,900; PD = 1.98. Quantitative 13 C NMR indicated that the copolymer contained 91.7 mole % ethylene and 8.3 mole % styrene units. 1.8 ethyl branches per 1000 methylene groups were also observed. The following Table gives the 13 C NMR spectrum of the polymer obtained, together with known assignments. Example 6 A 100 mL autoclave was charged with a solution of Ni(acac)2 (73 mg, 0.28 mmol), P(t-Bu)3 (115 mg, 0.57 mmol), methyl-4-vinylbenzoate (1.00 g, 6.2 mmol), and toluene (50 mL). To this mixture was then added modified methyl aluminoxane (14.2 mmol) in toluene (7 mL) under 210 kPa of ethylene. The reaction mixture was stirred under 210 kPa of ethylene for 1 h, during which time the reaction temperature varied between 25 and 28 C. Ethylene pressure was then vented and the reaction worked up by the same procedure used in Example 5. The precipitated polymer was filtered, washed further with methanol, and dried to afford 0.93 g of ethylene/methyl-4-vinylbenzoate copolymer. DSC: Tm = 115°C (114 J/g). GPC (trichlorobenzene vs. linear polyethylene, 135°C): Mn = 2,620; Mw = 10,700; PD = 4.10. Quantitative 13 C NMR indicated that the copolymer contained 99.3 mole % ethylene and 0.7 mole % methyl-4-vinylbenzoate units. Experiment 1 Synthesis of f t BuV,PCH 2 Pf t Bu > An oven dried 500 mL round bottom Schlenk flask was charged with 4.4 g of (t-Bu) 2 PCH 2 Li (see below), 200 mL of THF, and the resulting yellow solution cooled to -78°C. (t-Bu) 2 PCl (5.0 mL, 5.7 g, 1.2 equiv.) was added via syringe to the stirred solution over a 10 min period. The reaction mixture was allowed to stir at -78 °C for 2h, then warm to ambient temperature. A condenser was attached to the flask and the mixture heated to reflux for 24 h. After this time the reaction mixture was allowed to cool to ambient temperature and the volatiles materials were removed in vacuo. The product was extracted with 3 x 30 mL of hexanes and filtered through a pad of Celite® under N 2 . The hexanes were removed to yield 7.85 g (97%) of a viscous yellow liquid. The only impurity detected by Η NMR was represented by small multiplet at δ 1.05 ppm. A single resonance in the 31 I P{ H} NMR at δ 18.9 ppm was observed. A crystalline product was obtained by filtering a solution of 1.1 g of the above product in 20 mL of hexanes through a pad of basic Al 2 O 3 , eluting with additional hexanes, and removing the volatile materials to give 0.95 g of clear, waxy crystals. (t-Bu) 2 PCH 2 Li In the drybox a 200 mL round bottom Schlenk flask was charged with 15.9 g of (t-Bu^PCHs (see below) and 40 mL of hexanes. t-BuLi (58.6 mL of a 1.7 M solution, 1.0 equiv), was added via syringe. The reaction mixture was heated to reflux for 9 d. During this time an off white solid had formed which was isolated on a medium porosity frit, washed with 2 x 5 mL of pentane, and dried in vacuo to yield 4.4 g of (t-Bu) 2 PCH 2 Li. The filtrate was returned to the reaction flask, 40 mL of methylcyclohexane added and the mixture heated to reflux. After 2 d reflux an additional 3.8 g of (t-Bu) 2 PCH 2 Li was isolated. NOTE: This material and the filtrate are extremely pyrophoric and should be handled with extreme caution. Η NMR (THF-d 8 ): δ 0.80 (d, J PH = 9.1, 18H), -1.42 (d, J PH = 1.3, 2H). 3I P{1H} NMR (THF): δ 45.3. (t-Bu) 2 PCH 3 In the dry box 29.66 g of (t-Bu^PCl was diluted with -50 mL of Et 2 O and added to a 500 mL round bottom Schlenk flask. A dropping funnel was charged with 152.5 mL of methyl lithium and added dropwise to the stirred solution of (t-Bu) 2 PCl over a 2 h period. As the addition continued the reaction mixture turned from a colorless, homogeneous solution to a yellow solution with a white precipitate. After addition was complete the dropping funnel was replaced with a suba seal and the mixture allowed to stir overnight. The flask was then removed from the drybox, attached to a Schlenk line, cooled to 0°C, and 5.0 mL of degassed H 2 O was carefully added via syringe over a 20 min period, followed by an additional 50 mL of degassed H 2 O. A biphasic solution resulted. The organic layer was transferred via cannula to a 500 mL round bottom Schlenk flask containing -10 g of MgSO 4 . The aqueous layer was extracted with -100 mL of degassed petroleum. The flask containing the combined organic layers was fitted with a glass stopper, cooled to -10°C, and the volatile materials removed using a Schlenk line. The flask was then transferred to a dry box and the pale yellow residue filtered through a thin pad of Celite®. The MgSO 4 and Celite ® were washed with an additional 15 mL of Et 2 O and the washings added to the initial filtrate, then transferred to a 50 mL Schlenk flask. The flask was removed from the box, attached to a Schlenk line, cooled to 0°C to remove the Et 2 O, then fitted with a distillation head. The residue was distilled under static vacuum (Variac® setting 40) into a receiving cooled in liquid N 2 , yielding a 26.3 g (89.1 % yield) of a clear distillate. Η NMR (C 6 D 6 ): 61.03 (d, J PH = 10.8, 18H), 0.82 (d, J PH = 4.7, 3H). 13 C{'H} NMR (C 6 D 6 ): d 30.26 (d, J PC = 21.95), 29.29 (d, J PC = 13.92), 4.20 (d, J PC = 25.1). 31 P{Η} NMR (hexanes): δ 12.3 Experiment 2 Synthesis of α-Bu 2 PCH 2 P-t-Bu 2 NiBr 2 (DME)NiBr 2 (0.250 g, 0.810 mmol) was suspended in 20 mL of CH 2 C1 2 under nitrogen. To this mixture was added t-Bu 2 PCH 2 P-t-Bu 2 (0.247 g, 0.810 mmol). A purple solution slowly formed. The reaction mixture was stirred at ambient temperature for 15.5 h. It was then filtered, and the filtrate concentrated to dryness in vacuo to afford a red-purple powder. Recrystallization from CH 2 Cl 2 /pentane at -40°C afforded 0.336 g of (t-Bu 2 PCH 2 P-t-Bu 2 )NiBr 2 as a purple, crystalline solid (79%). Η NMR δ 2.71 (t, 2H, CH 2 ), 1.70 (mult, 36H, t-Bu); 13 P NMR (CDC1 3 ) δ-6.42. Example 7 An evacuated 100 mL autoclave was charged with a slurry of (t-Bu 2 PCH 2 P-t-Bu 2 )NiBr 2 (52 mg, 0.10 mmol) in 40 mL of toluene under nitrogen. To this mixture was then added modified methyl aluminoxane (5.00 mmol) in toluene (10 mL) under 690 kPa of ethylene. The resulting reaction mixture was stirred at approximately 700 rpm under 690 kPa of ethylene for 24 h. During this time the reaction temperature remained at 26-28°C. Ethylene pressure was then vented and the reaction mixture quenched under air by the addition of 50 mL of isopropanol. The resulting mixture was then stirred in a beaker with 100 mL of methanol plus 10 mL concentrated HCl. Finally, 100 mL of water was added and an oil separated from the solution. The mixture was then transferred to a separatory funnel and the oil separated from the aqueous phase. The aqueous phase was extracted with 3 x 100 mL of hexane, and the hexane extracts combined with the oil. The resulting solution was dried (MgSO ) and concentrated in vacuo to afford 10.4 g of amorphous polyethylene as a viscous, clear, colorless oil. The branching distribution was quantified by C NMR. Branching per 1000 CH 2 : Total methyl-ended branches (143.6), Methyl (86.4), Ethyl(22.3), Propyl (1.3), Butyl (9.2), Amyl (0.8),≥Hex and end of chains (21.2), >Am and end of chains (23.9), ≥Bu and end of chains (33.1). GPC (TCB vs. linear PE): M n = 3,410; M w = 7,860; M w /M n = 2.3 Experiment 3 Synthesis of (P-t-Bu 2 1NiBr 2 (DME)NiBr 2 (0.500 g, 1.62 mmol) was suspended in 20 mL of CH 2 C1 2 under nitrogen. To this mixture was added P-t-Bu 3 (0.328 g, 1.62 mmol). An emerald-green solution slowly formed. The reaction mixture was stirred at ambient temperature for 19 h. It was then filtered, and the filtrate concentrated to dryness in vacuo to afford a green solid. Recrystallization from CH 2 C1 2 at -40°C afforded 0.260 g of (P'Bu 3 )NiBr 2 as a green powder (38%). Example 8 An evacuated 100 mL autoclave was charged with a solution of (P-t-Bu 3 )NiBr 2 (42 mg, 0.10 mmol) in 40 mL of toluene under nitrogen. To this mixture was then added modified methyl aluminoxane (5.00 mmol) in toluene (10 mL) under 690 kPa of ethylene. The resulting reaction mixture was stirred at 700 rpm under 100 psi of ethylene for 35 min. The reaction temperature increased from 24 to 50°C during the first 2 min of the reaction; thereafter it slowly decreased until it was 32°C after 35 min. Ethylene pressure was vented and the reaction mixture quenched under air by the addition of 50 mL of isopropanol. The resulting mixture was then stirred in a beaker with 100 mL of methanol plus 10 mL concentrated HCl. The precipitated polymer was filtered off, washed with methanol, and dried to afford 4.91 g of polyethylene. The branching distribution was quantified by C NMR. Branching per 1000 CH 2 : Total methyl-ended branches (7.5), Methyl (2.1), Ethyl (2.4), Propyl (0.3), Butyl (0.4), Amyl (0.7), > Hex and end of chains (4), >Am and end of chains (2.3), ≥Bu and end of chains (2.7). DSC: T m = 127.2°C (152 J/g). GPC (in TCB vs. linear PE): M n = 9,580; M w = 45600; M w /M n = 4.76 Example 9 An evacuated 100 mL autoclave was charged with a solution of (P-t-Bu 3 )NiBr 2 (42 mg, 0.100 mmol) and norbornene (3.00 g, 31.9 mmol) in 40 mL of toluene under nitrogen. To this mixture was then added modified methyl aluminoxane (10.00 mmol) in toluene (10 mL) under 350 kPa of ethylene. The resulting reaction mixture was stirred at 600 rpm under 350 kPa of ethylene for 6 min. The reaction temperature increased from 31 to 61°C during the first 3 min of the reaction; thereafter it decreased until it was 57°C after 6 min. Ethylene pressure was vented and the reaction mixture quenched under air by the addition of 50 mL of isopropanol. The resulting mixture was then stirred in a beaker with 100 mL of methanol plus 10 mL concentrated HCl. The precipitated polymer was filtered off, washed with methanol, and dried to afford 8.80 g of ethylene/norbornene copolymer. Quantitative C NMR indicated the copolymer to contain 9 mole % norbornene and 91 mole % ethylene units. In addition, the 1 "3 following branches (per 1000 CH 2 's) were detected by C NMR: Total methyl- ended branches (4.1), Methyl (1.2), Ethyl(l.l), Propyl (.1), Butyl (.3), Amyl (3.1), ≥Hex and end of chains (7.1), >Am and end of chains (1.3), ≥Bu and end of chains (1.7). DSC: T m = 109, 115°C (43 J/g). GPC (in TCB vs. linear PE): M n = 3,390; M w = 13,500; M w /M n = 3.98. Example 10 An evacuated 100 mL autoclave was charged with a solution of (P-t-Bu 3 )NiBr 2 (42 mg, 0.100 mmol) and norbornene (6.00 g, 63.7 mmol) in 40 mL of toluene under nitrogen. To this mixture was then added modified methyl aluminoxane (10.00 mmol) in toluene (10 mL) under 690 kPa of ethylene. The resulting reaction mixture was stirred at 600 rpm under 690 kPa of ethylene for 8 min. The reaction temperature increased from 27 to 53°C during the course of the reaction. Ethylene pressure was vented and the reaction mixture quenched under air by the addition of 50 mL of isopropanol. The resulting mixture was then stirred in a beaker with 200 mL of methanol plus 10 mL concentrated HCl. The precipitated polymer was filtered off, washed with methanol, and dried to afford 11.21 g of ethylene/norbomene copolymer. Quantitative C NMR indicated the copolymer to contain 15 mole % norbornene and 85 mole % ethylene units. In 1 ^ addition, the following branches (per 1000 CH 2 's) were detected by C NMR: Total methyl-ended branches (3.5), Ethyl (1.4), Propyl (.5), Butyl (.2), Amyl (.2), ≥Hex and end of chains (5.8), ≥Am and end of chains (1.5), ≥Bu and end of chains (2). DSC: T m = 65°C (40 J/g). GPC (in TCB vs. linear PE): Hi = 1,460; M w = 5,300; M w /M n = 3.64. Example 11 An evacuated 100 mL autoclave was charged with a solution of (P-t-Bu 3 )NiBr 2 (5 mg, 0.012 mmol) and norbornene (10.00 g, 106.2 mmol) in 40 mL of toluene under nitrogen. To this mixture was then added modified methyl aluminoxane (10.00 mmol) in toluene (10 mL) under 140 kPa of ethylene. The resulting reaction mixture was stirred at 600 rpm under 140 kPa of ethylene for 22 min. The reaction temperature remained constant at 30°C during the course of the reaction. Ethylene pressure was then vented. Methanol/HCl workup afforded 3.82 g of ethylene/norbornene copolymer. Quantitative I3 C NMR indicated the copolymer to contain 85 mole % norbornene and 15 mole % ethylene units. No branching could be detected by 13 C NMR. GPC (in TCB vs. linear PE): M n = 5,295; M w = 33,000; M w /M n = 6.29. Example 12 An evacuated 100 mL autoclave was charged with a solution of Ni(acac) 2 (26 mg, 0.100 mmol), t-Bu 3 P (40 mg, 0.200 mmol) and the dimethyl ester of endo-5-norboraene-2,3-dicarboxylic acid (3.00 g, 14.27 mmol) in 40 mL of toluene under nitrogen. To this mixture was then added modified methyl aluminoxane (20.00 mmol) in toluene (10 mL) under 350 kPa of ethylene. The resulting reaction mixture was stirred at 700 rpm under 50 psi of ethylene for 17 h at ambient temperature (~25-30°C). Ethylene pressure was then vented. 1 " Methanol/HCl workup afforded 0.640 g of copolymer. Quantitative C NMR indicated the copolymer to contain 1.36 mole % of the norbornene diester. In addition, the following branches (per 1000 CH 2 's) were detected by C NMR: Total methyl-ended branches (14.4), Methyl (8.8), Ethyl(.7), ≥Am and end of chains (5.8), ≥Bu and end of chains (5). Example 13 A 100 mL autoclave was charged with a solution ofNi(acac) 2 (18 mg, 0.070 mmol), P-t-Bu 3 (29 mg, 0.143 mmol), 1-hexene (2.50 g, 29.7 mmol), and toluene (40 mL). To this mixture was then added modified methyl aluminoxane (3.5 mmol) in toluene (10 mL) under 690 kPa of ethylene. The reaction mixture was stirred under 690 kPa of ethylene for 15 min, during which time the reaction temperature varied between 29 and 41°C. Ethylene pressure was then vented and the reaction mixture quenched by addition of 50 mL of isopropanol under air. The resulting mixture was transferred to a beaker with 200 mL methanol plus 10 mL concentrated HCl. The precipitated polymer was filtered, washed further with methanol, and dried to afford 3.43 g of ethylene/ 1-hexene copolymer as a sticky, waxy solid. GPC (trichlorobenzene vs. linear polyethylene, 135°C): M n = 2,330; M w = 5,970; PD = 2.36. Quantitative 13 C NMR indicated that this sample contained 72.6 methyl-ended branches per 1000 methylenes. The distribution of branches was as follows (branches per 1000 methylenes): Methyl (4.1), Ethyl (6.6), Propyl (1), Butyl (55.3), Amyl (.3), ≥Hex and end of chains (4.6), ≥Am and end of chains (8.9), ≥Bu and end of chains (59.7).

Claims: CLAIMS What is claimed is: 1. A process for the manufacture of a polyolefin, comprising forming a polymerization catalyst system by contacting in an inert liquid: a first compound of the formula NiAQ (I) or L 5 L 6 NiAQ (VIII); a second compound of the formula (t-butyl)2PEP(t-butyl)2 (II) or (t-butyl)3P (III); and a third compound W (IV), which is a neutral Lewis acid capable of abstracting A " or Q " to form the anion WA " or WQ " , provided that WA " or WQ " is a weakly coordinating anion; and contacting said polymerization catalyst system with ethylene or a mixture of ethylene and an α-olefin, internal olefin, cyclopentene, a norbornene, or a styrene, provided that: said contacting with ethylene or a mixture of ethylene and cyclopentene, a norbornene, or a styrene is carried out at a temperature of about -20°C to about +70°C; when (t-butyl)3P is present, one or more of an α-olefin, internal olefin, a styrene, a norbornene, or cyclopentene is also present; when neither of Q and A are hydrocarbyl or hydride, W is capable of transferring a hydrocarbyl or hydride group to Ni; and wherein: L and L are each independently monodentate weakly coordinating neutral ligands or L and L taken together are a bidentate weakly coordinating neutral ligand; Q is a monovalent anion; A is monovalent anion; E is -CH2-, -O-, or -NH-; and P is 2. A process for the manufacture of a polyolefin, comprising contacting in an inert liquid at a temperature of about -20 C to about +70 C, a compound of the formula [L 1 L2 L 3 L 4 Ni] + X - (VI) with ethylene or ethylene and an α-olefin, internal olefin, cyclopentene, a norbornene, or a styrene, wherein: L 1 and L 2 taken together are (t-butyl)2PEP(t-butyl)2 (II), or L 1 and L 2 are both (t-butyl)3P (III), or L 1 is (t-butyl)3P (III) and L 2 is an empty coordination site, ethylene or a neutral monodentate ligand that can be displaced by ethylene; E is -CH2-, -O-, or -NH-; P is L 3 and L 4 taken together are a π-allyl or a π-benzyl group; or L 3 is ethylene and L 4 is monoanionic -R 1 R2 ; or L 3 is a monoanionic group which may add across ethylene, and L is a neutral coordinating group which may be displaced by ethylene or L is an empty coordination site about nickel; or L and 4 L taken together are a monoanionic oligomeric agostic group; X is a relatively noncoordinating anion; R is a polymeric alkylene group; and R 2 i .s a polymer end group; and provided that when (t-butyl)3P is present one or more of an α-olefin, internal olefin, cyclopentene, a norbornene, or a styrene is also present. 3. A compound of the formula [L 1 L2 L 3 L 4 Ni] + X - (VI) wherein: L 1 and L 2 taken together are (t-butyl)2PEP(t-butyl)2 (II), L 1 and L 2 are both (t-butyl)3P (III), or L 1 is (t-butyl)3P (III) and L 2 is an empty coordination site, ethylene or a neutral monodentate ligand that can be displaced by ethylene; E is -CH2-, -O-, or -NH-; P L 3 and L 4 taken together are a π-allyl or a π-benzyl group; or L 3 is ethylene and L 4 is monoanionic -R 1 R2 ; or L 3 is a monoani •onic group which may 4 add across ethylene, and L is a neutral coordinating group which may be displaced by ethylene or L is an empty coordination site about nickel; or L and 4 L taken together are a monoanionic oligomeric agostic group; X is a relatively noncoordinating anion; R is a polymeric alkylene group; and 2 R is a polymer end group; and provided that when (t-butyl)3P is present, a repeat unit derived from one or more of α-olefin, internal olefin, cyclopentene, a norbornene, or a styrene is also present in R . 4. A polyolefin containing ethyl branches, wherein at least 53 percent of said ethyl branches are part of sec-butyl ended branches, and provided that said polyolefin has at least 50 branches per 1000 methylene groups. 5. A polyethylene or a copolymer of ethylene and one or more of an α-olefin, internal olefin, cyclopentene or a styrene in which at least 53 percent of alkyl branches are ethyl branches, and provided that said ethylene or a copolymer of ethylene and cyclopentene, a norbornene, or a styrene has at least about 1.0 branch per 1000 methylene groups. 6. The process as recited in claim 1 wherein A and Q are chloride, bromide, carboxylate or acetylacetonate. 7. The process as recited in claim 1 wherein said first compound is (VIII) and one or both of A and Q are each independently hydride or methyl. 8. The process as recited in claim 1 wherein E is -CH 2 -. 9. The process as recited in claim 1 wherein W is an alkylaluminum compound. 10. The process as recited in claim 2 wherein E is -CH 2 -. 11. The compound as recited in claim 3 wherein E is -CH 2 -. 12. The process as recited in claim 2 wherein A and Q are chloride, bromide, carboxylate or acetylacetonate. 13. The process as recited in claim 1 wherein at least one more polymerization catalyst is present. 14. The process as recited in claim 2 wherein at least one more polymerization catalyst is present. 15. A copolymer of one or more norbomenes and ethylene containing at least about 2.0 methyl groups which are branch ends per one thousand methylene groups.

Inventors: BROOKHART MAURICE S III, FELDMAN JERALD, HAUPTMAN ELISABETH, MCCORD ELIZABETH FORRESTER, BROOKHART, MAURICE, S., III, FELDMAN, JERALD, HAUPTMAN, ELISABETH, MCCORD, ELIZABETH, FORRESTER
Applicants: BROOKHART MAURICE S III, DU PONT, FELDMAN JERALD, HAUPTMAN ELISABETH, MCCORD ELIZABETH FORRESTER, UNIV NORTH CAROLINA, BROOKHART, MAURICE, S., III, E.I. DU PONT DE NEMOURS AND COMPANY, FELDMAN, JERALD, HAUPTMAN, ELISABETH, MCCORD, ELIZABETH, FORRESTER, UNIVERSITY OF NORTH CAROLINA AT CHAPEL HILL
Application year: 1998
Main classification: C08F10
IPC codes: C07F15, C08F4, C08F10, C08F110, C08F210