COMPOSITION FOR MANUFACTURE OF FUEL BRIQUETTES

Abstract: The present invention relates to the fields of fuel industry and utilization of waste from woodworking, paper and pulp, coal and peat mining industries; it represents composition for manufacture of fuel briquettes comprising crushed secondary carbon-containing feed stock: petroleum pitch, coal pitch, coal dust, crushed coal product, crushed peat, wood shavings, sawdust or their mixes and binder: lignin-containing product selected from the group: lignin, lignosulfonate, hydrolytic lignin, black sulfate liquor or their mixes, or mix of one or several above enumerated lignin-containing products with a-cellulose. Composition allows manufacture of ecologically clean fuel briquettes from practically any solid secondary carbon-containing feed stock featuring high calorific value (up to 7000 cal/g), density of 1.04-1.18 g/cm<3> and ash content of 0.8-1.2 %.

Description: COMPOSITION FOR MANUFACTURE OF FUEL BRIQUETTES Description Field of the invention The present invention relates to the fields of fuel industry and utilization of waste from woodworking, paper and pulp, coal and peat mining industries, and particularly to compositions for manufacture of fuel briquettes. Description of the Background Known is composition for manufacture of fuel briquettes comprising culled wood from peat mosses (75 -:-96 mass%) and peat dust (4-:-25 mass%) or culled wood from peat mosses (70 mass%) and brown coal (30%) (SU, > 1458377; SU > 1659452). For manufacture of such briquettes initial components are dried at 90- 100° C, mixed and from the resultant mixture briquettes are molded at temperature 180° C and higher under pressure 40-:-70 mPa (SU, VO 1458377). As another embodiment components are mixed, the resultant mixture is dried at 700 °C up to moisture content of 6%, then briquettes are pressed from mixture at pressure of about 90 mPa (SU, JNs 1659452). Manufactured fuel briquettes have calorific value of 5000 kcal/kg, ash content of such briquettes varies from 3-:- 12%. Known is composition for manufacture of fuel briquettes comprising wood secondary raw stock - sawdust, shavings in the quantity of 87-97 mass% and 1-5% water suspension of spoilage in the quantity of 1-13 mass%. For manufacture of fuel briquettes the said components are thoroughly mixed to obtain homogeneous mass, then briquettes are molded from mass at specific pressure of 0.03 - 0.05 mPa that are then dried to residual moisture content of 2-10% (SU, Λfe 1726498). Manufactured fuel briquettes have calorific value up to 3000 kcal kg, ash content of such briquettes makes up 5 - 6%. Known is also composition for manufacture of fuel briquettes containing 78-85 mass % of birch bark crushed to 3-20 mm particles and 15-25 mass% of water-proof protein gum, including rennin casein, albumin, lime, sodium silicate solution (SU jNfs 1715828). For manufacture of fuel briquettes from the said composition they are molded at 1 10-120° C, specific pressure 1.8-2.5 mPa per 1 mm of thickness of manufactured briquette. Density of manufactured briquettes of 300 x 60 x 30 mm is 710 kg/m^, calorific value - up to 20800 J/kg (4 964 kcal/kg), ash content does not exceed, as rule, 1.7%. The above enumerated compositions for manufacture of fuel briquettes call for their development of either rather expensive or difficultly available components or briquettes manufactured from such compositions emanate toxic substances when burning. Known is also the use of carbon-containing feed stock: sawdust, shavings, graphite, carbon black, coke and dextrin water solution of dextrin as binder, sulfite liquor in compositions for manufacture of heat insulating boards (CzSSR, M> 264665, IPC 4 C 04 B38/06, pub. 14.12.90). Summary of the invention The task of developing composition for manufacture of fuel briquettes from available ecological raw materials, of whose main consumer's parameters (calorific value, density, strength, ash content) would remain at the high level, was used as a basis for the said invention. Proposed is composition for manufacture of fuel briquettes including crushed secondary carbon-containing feed stock and binder where as secondary carbon-containing feed stock are used petroleum pitch, coal pitch, coal crushed product, crushed peat, wood shavings, sawdust, or their mixes, and as binder - lignin-containing product selected from group: lignin, lignosulfonate, hydrolytic lignin, black sulfate liquor or their mixes or mix of one or several above enumerated lignin-containing products with α-cellulose. Composition contains carbon-containing feed stock and lignin-containing product at ratio, mass%: carbon-containing feed stock 63.1 -97.6% lignin-containing product 2.4-36.9% In some cases composition comprises as binder mix of one or several lignin-containing products with a-cellulose at ratio, accordingly, (1-32) : 1. Unexpectedly it was found out that for manufacture of fuel briquettes as binder in the composition can be used lignin-containing products that are readily available production wastes. For instance, wood processing at paper and pulp enteφrises only in Russia give annually nearly 40 mill.t of lignin, 5 mill, t of lignosulfonates, 3.5 mill.t of technical hydrolytic lignin. Of this amount of lignin-containing products only 0.1% (plastic fillers, rubber articles, building materials, agriculture) are used regularly, the remaining products are either burned in the open air or dumped. The indubitable advantage of lignin- containing products from the point of view of their possible industrial processing is capacity to biodecomposition and low toxicity. The basis for composition for manufacture of fuel briquettes can be crushed secondary carbon-containing feed stock selected from group: petroleum pitch, coal pitch, coal crushed product, crushed peat, wood shavings, sawdust or their mix. Composition comprises as binder: lignin, lignosulfonate, hydrolytic lignin, black sulfate liquor, or their mixes or mix of one or several above enumerated lignin-containing products with a-cellulose at mass ratio of lignin-containing product: α-cellulose equaling (1-32) : 1 with mass ratio of secondary carbon-containing feed stock: binder equaling (63.1-97.6) : (2.4-36.9). Fuel briquettes manufactured on the basis of the proposed composition have calorific value up to 7000 cal/g, ash content 0.8- 1.2% and density of briquette - 1.04- 1.18 g/cm 3 . It is preferable to use as binder lignosulfonates with dry basis of 46.0-76.0 mass%, ash content of 0.8-1.3 mass% and insoluble substances in mass of dry products 0.8-1.3 mass%. It is the most feasible to use lignosulfonates preliminary oxidized in acid medium at 120 - 150° C. In some cases to increase strength and to improve hydrophobic properties of fuel briquettes in the open air paraffin in the quantity of 0.5-2.5 mass% is introduced in the binder. Secondary carbon-containing feed stock is used mainly as particles of whose size does not exceed 85% of the minimal size of manufactured briquettes. α-Cellulose being a binder component has the following characteristics: molecular mass of elementary link of α-cellulose is 162, polymerization - 600-1000. fl-cellulose may be present in composition as powder-like native cellulose, for instance, wood cellulose, cotton or flax cellulose, where content of α-cellulose is usually 77- 98.5 mass %. When using powder-like wood cellulose as cellulose source it is practicable to use the product with the following characteristics: content of α-cellulose 77% ash content 0.3% bulk density 140-160 g/dm 3 size of particles 100-160 μ moisture content < 0.7% Lignin, binder, is produced from black sulfate liquor by acidifying 2.5 M solution of sulfuric acid up to pH 1.8 - 4.6 with mixing (4200- 5300 r.p.m.) and temperature 60-65° C. Two minutes after precipitated lignin is filtered, washed off and dried in vacuum at 60° C. To obtain fine dispersion of lignin characterized by higher binding properties 12- 18% of lignin extracted from black sulfate liquor are mixed in water solution with 2-15 moles of ammonia, 4-12 moles of formaldehyde and 0.25-1.25 moles of NaOH or KOH per 1 mole of lignin. Solution is heated up to 65° C during time sufficient for lignin mixing and formation of colloid suspension of lignin particles of homogeneous form and size. In the process of reaction lignin becomes insoluble and precipitates. Lignosulfonates as binder components are derived in the following way: When producing cellulose according to the acid sulfϊte method wood is heated at 130-140° C with pulp cooking acid (water solution containing 2-10% of free sulfuric acid and 1.3-2.5% of calcium sulfate). In the process of cooking sulfurization of lignin occurs and all lignin and a greater part of cellulose associated carbons goes into solution. Lignosulfonates represent polydisperse system with the wide range of molecular masses (2000- 100000). They are water soluble ( - 0.6) and behave as strong mineral acids. Free acids are derived from calcium salts by treating with sulfuric acid or dialysis with subsequent ion exchange. After drying or evaporation gray-brown powder of lignosulfonate is produced. From solutions it is deposited as salts of heavy metals or aromatic amines. Sulfite-cellulose production wastes comprises mainly ammonium, sodium and calcium salts of lignosulfonates, lignosulfonic acids and sugars that after processing give sulfite-alcohol spent wash plentiful of water that is evaporated and lignosulfonates are derived. Depending 5 on content of dry substances commercial technical lignosulfonates are produced with the following brands of whose basic characteristics are given in Table 1. Table 1. Variable Lignosulfonate brands A B B r 4 E Dry basis, % (min.) 470 47.0 50.0 76.0 50.0 76.0 Mass fraction of ash in mass of dry 08 0.8 0.8 0.8 1.3 1.1 substances,% (max.) Mass fraction of insolubles in mass of dry 0.8 0.8 0.8 0.8 1.3 1.3 substances,% (max.) pH of 20% water solution 4.4 5.0 4.5 4.5 4.5 4.5 Tensile strength, MPa, (max.) 0.6 0.6 0.4 0.54 0.45 0.4 Comparison viscosity at viscosimeter B3- 1 , C 320 300 340 340 ( max.) " Density, kg/m 3 (min.) 1230 1235 1240 1280 1240 1280 During oxidation of lignosulfonates by oxygen at 120- 1500° C in acid medium content of carbonyl groups is increased (~50%), content of aliphatic and phenol OH-groups is significantly reduced. Oxidized lignosulfonates are hardened with hot pressing (110-150° C) during which low molecular fractions of lignosulfonates are self-condensed up to high- molecular particles with a large number of cross-linkages, this resulting in formation of rubber-like products featuring high water-proofness. Black sulfate liquor is produced from cooking leaf or needle wood, then treated at 65-70° C during 20-40 min. by means of orthophosphoric acid up to pH = 2.5-3.5, from reaction mass lignin is extracted by filtration or centrifuging, then it is dried to obtain commercial product. The initial black sulfate liquor has the following composition: organics 61.8 mass % (including ionogenic - 34.8% non-ionic - 27.0%) soluble mineral components 38.1 mass % insoluble mineral components (ash portion) 42.9 mass % Black sulfate liquor is derived by treating water solution with 10% CaCl2 solution, sediment is filtered, washed off and dried at 120^ C and cooled. In the proposed composition α-cellulose in mix with lignin-containing product at ratio, accordingly, 1 : (1- 32) with mass ratio of carbon-containing feed stock: binder being equal to (63.1- 97.6) : (2.4- 36.9) is used. Non-observance of such ratios affects adversely the capacity of the composition to compress, i.e. fuel briquettes will be loose, crumbly, their density will be insufficient to ensure strength that interacts directly with the calorific value of fuel. Method of manufacture of fuel briquettes on the basis of the proposed composition Wood shavings, sawdust, petroleum and/or coal pitch, their crumbs, dust with size of particles not exceeding 85% from the minimal size of the briquette and content of free moisture 16- 28% are mixed with binder selected from the group: lignin, lignosulfonate, hydrolytic lignin, black sulfate liquor or their mixes or mix of one or several above enumerated lignin-containing products with α-cellulose; mix is thoroughly agitated and molded by pressing into briquettes, for instance, as blocks of 46- 63 mm diameter and 23 mm high. Pressing is done at pressure 85 atm., min. Whenever required preheating up to 350° C is used. Pressing under pressure below 85 atm. does not allow to reach the density and strength of briquettes that have calorific value of 7000 cal/g and optimal burning kinetics. At the same time it is unpracticable to considerably raise the said pressure value due to drastic increase in consumption of utilities. Below are examples of manufacture of fuel briquettes from various compositions. Example 1. Leaf and needle wood shavings and sawdust were dried to moisture content of 16- 20 % and in the quantity of 96 kg are mixed with 4 kg of binder, lignosulfonate of brand B, with dry basis of 50%, ash content of 0.8%, fraction of insolubles in mass of dry substances of 0.8%. Before mixing 1% of paraffin was added to binder. Mixing was done with speed of 20- 60 r.p.m. to form relatively homogeneous mass that was then sent to the mold and under pressure of 85 atm. briquettes with diameter of 63 mm and height of 23 mm were molded. Example 2. Leaf and needle wood shavings and sawdust were dried to moisture content of 16- 20% and in the quantity of 96 kg were mixed with 4 kg of binder, lignosulfonate of brand B, with dry basis of 46%, ash content of 0.8%, fraction of insolubles in mass of dry substances of 0.8%. Before mixing 1% of paraffin was added to binder. Mixing was done with speed of 20- 60 r.p.m. to form relatively homogeneous mass that was then sent to the mold and under pressure of 85 atm. briquettes with diameter of 63 mm and height of 23 mm were molded. Example 3. Leaf and needle wood shavings and sawdust were dried to moisture content of 16- 20% and in the quantity of 96 kg were mixed with 4 kg of binder, lignosulfonate of brand B, with dry basis of 76%, ash content of 1.1%, fraction of insolubles in mass of dry substances of 1.3%. Before mixing 1% of paraffin was added to binder. Mixing was done with speed of 20- 60 r.p.m. to form relatively homogeneous mass that is then sent to the mold and under pressure of 85 atm. briquettes with diameter of 63 mm and height of 23 mm were molded. Example 4. Leaf and needle wood shavings and sawdust were dried to moisture content of 16- 20% and in the quantity of 96 kg were mixed with 4 kg of binder, lignosulfonate of brand B, with dry basis of 50%, ash content of 0.8%, fraction of insolubles in mass of dry substances of 0.8%. Before mixing 0.5% of paraffin was added to binder. Mixing was done with speed of 20- 60 r.p.m. to form relatively homogeneous mass that is then sent to the mold and under pressure of 85 atm. briquettes with diameter of 63 mm and height of 23 mm were molded. 8 Example 5. Leaf and needle wood shavings and sawdust were dried to moisture content of 16- 20 % and in the quantity of 96 kg were mixed with 4 kg of binder, lignosulfonate of brand B, with dry basis of 50%, ash content of 0.8%, fraction of insolubles in mass of dry substances of 0.8%. Before mixing 2.5% of paraffin was added to binder. Mixing was done with speed of 20- 60 r.p.m. to form relatively homogeneous mass that is then sent to the mold and under pressure of 85 atm. briquettes with diameter of 63 mm and height of 23 mm were molded. Example 6. Mix of coal and petroleum pitches (1 :1) were dried to moisture content of 16- 20% and in the quantity of 97.6 kg were mixed with 2.4 kg of binder, lignosulfonate, with dry basis of 76%, ash content of 1.1%, fraction of insolubles in mass of dry substances of 1.3%. Mixing was done with speed of 20- 60 r.p.m. to form relatively homogeneous mass that was then sent to the mold and under pressure of 95 atm. briquettes with diameter of 63 mm and height of 23 mm were molded. Example 7. Leaf and needle wood shavings, sawdust and coal dust (1 :1) were dried to moisture content of 16- 20% and in the quantity of 97.6 kg were mixed with 4 kg of binder, lignosulfonate with dry basis of 76%, ash content of 1.1%, fraction of insolubles in mass of dry substances of 1.3%. Before mixing 1% of paraffin was added to binder. Mixing was done with speed of 20- 60 r.p.m. to form relatively homogeneous mass that is then sent to the mold and under pressure of 95 atm. briquettes with diameter of 63 mm and height of 23 mm were molded. Example 8. Leaf and needle wood shavings, sawdust and coal dust (1:1) were dried to moisture content of 16- 20% and in the quantity of 97.6 kg were mixed with 2.4 kg of binder, lignosulfonate + α-cellulose (1:1) with dry basis of 50%, ash content of 0.8%, fraction of insolubles in mass of dry substances of 0.8%. Before mixing 1% of paraffin was added to binder. Mixing is done with speed of 20- 60 r.p.m. to form relatively homogeneous mass that was then sent to the mold and under pressure of 85 atm. briquettes with diameter of 63 mm and height of 23 mm. were molded. Example 9. Leaf and needle wood shavings, sawdust and coal dust (1 :1) were dried to moisture content of 16- 20% and in the quantity of 97.6 kg were mixed with 2.4 kg of binder, lignosulfonate + α-cellulose (1: 15) with dry basis of 50%, ash content of 0.8%, fraction of insolubles in mass of dry substances of 0.8%. Before mixing 1% of paraffin was added to binder. Mixing was done with speed of 20- 60 r.p.m. to form relatively homogeneous mass that was then sent to the mold and under pressure of 85 atm. briquettes with diameter of 63 mm and height of 23 mm were molded. Example 10. Leaf and needle wood shavings, sawdust and coal dust (1 :1) were dried to moisture content of 16- 20% and in the quantity of 97.6 kg were mixed with 2.4 kg of binder, lignosulfonate + tx-cellulose (1:32) with dry basis of 50%, ash content of 0.8%, fraction of insolubles in mass of dry substances of 0.8%. Before mixing 1% of paraffin was added to binder. Mixing was done with speed of 20- 60 r.p.m. to form relatively homogeneous mass that is then sent to the mold and under pressure of 85 atm. briquettes with diameter of 63 mm and height of 23 mm were molded. Example 11. Leaf and needle wood shavings, sawdust and coal dust (1: 1) were dried to moisture content of 16- 20 % and in the quantity of 97.6 kg were mixed with 2.4 kg of binder, lignosulfonate + ύt-cellulose (1:10 ) with dry basis of 50%, ash content of 0.8%, fraction of insolubles in mass of dry substances of 0.8%. Mixing was done with speed of 20- 60 r.p.m. and at temperature 120° C to form relatively homogeneous mass that was then sent to the mold and under pressure of 85 atm. briquettes with diameter of 63 mm and height of 23 mm were molded. Example 12. Leaf and needle wood shavings, sawdust and coal dust (1:1) were dried to moisture content of 16- 20% and in the quantity of 97.6 kg were mixed with 2.4 kg of binder, lignosulfonate + α-cellulose (1:10) with dry basis of 50%, ash content of 0.8%, fraction of insolubles in mass of dry substances of 0.8%. Mixing was done with speed of 20- 60 r.p.m. and at temperature 200° C to form relatively homogeneous mass that was then sent to the mold and under pressure of 85 atm. briquettes with diameter of 63 mm and height of 23 mm were molded. 10 Example 13. Leaf and needle wood shavings, sawdust and coal dust (1 : 1) were dried to moisture content of 16- 20 % and in the quantity of 97.6 kg were mixed with 2.4 kg of binder, lignosulfonate + β-cellulose (1 : 10) with dry basis of 50%, ash content of 0.8%, fraction of insolubles in mass of dry substances of 0.8%. Mixing was done with speed of 20- 60 r.p.m. and temperature 250° C to form relatively homogeneous mass that was then sent to the mold and under pressure of 85 atm. briquettes with diameter of 63 mm and height of 23 mm. were molded Example 14. Leaf and needle wood shavings, sawdust and coal dust (1 : 1) are dried to moisture content of 16- 20 % and in the quantity of 97.6 kg are mixed with 2.4 kg of binder, lignosulfonate + α-cellulose (1 :10) with dry basis of 50%, ash content of 0.8%, fraction of insolubles in mass of dry substances of 0.8%. Mixing is done with speed of 20- 60 r.p.m. and temperature 350° C to form relatively homogeneous mass that is then sent to the mold and under pressure of 85 atm. make briquettes with diameter of 63 mm and height of 23 mm. Example 15. Leaf and needle wood shavings, sawdust and coal dust (1:1) were dried to moisture content of 16- 20% and in the quantity of 63.1 kg were mixed with 36.9 kg of binder, lignosulfonate + α-cellulose (1 :10 ) with dry basis of 50%, ash content of 0.8%, fraction of insolubles in mass of dry substances of 0.8%. Mixing was done with speed of 20- 60 r.p.m. and temperature 200° C to form relatively homogeneous mass that was then sent to the mold and under pressure of 85 atm. briquettes with diameter of 63 mm and height of 23 mm were molded. Example 16. Leaf and needle wood sawdust, crushed coal product and crushed peat were dried to moisture content of 16- 20 % and in the quantity of 75.0 kg were mixed with 25 kg of binder, lignin. Paraffin in the quantity of 1 mass% was added and mixed with speed of 20- 60 r.p.m. and temperature 20- 24° C to form relatively homogeneous mass that was then sent to the mold and under pressure of 85 atm. briquettes with diameter of 63 mm and height of 23 mm were molded. ;/ Example 17. Crushed peat was dried to moisture content of 16- 20% and in the quantity of 75.0 kg were mixed with 25 kg of binder, hydrolytic lignin. Paraffin in the quantity of 1 mass% was added and mixed with speed of 20- 60 r.p.m. and temperature 20- 24° C to form relatively homogeneous mass that was then sent to the mold and under pressure of 95 atm. briquettes with diameter of 63 mm and height of 23 mm were molded. Example 18. Crushed coal product was dried to moisture content of 16- 20 % and in the quantity of 75.0 kg were mixed with 25 kg of binder, black sulfate liquor. Paraffin in the quantity of 1 mass% was added and mixed with speed of 20- 60 r.p.m. and temperature 20- 24° C to form relatively homogeneous mass that was then sent to the mold and under pressure of 1 10 atm. briquettes with diameter of 63 mm and height of 23 mm were molded. Example 19. Crushed coal product and coal dust were dried to moisture content of 16- 20 % and in the quantity of 75.0 kg were mixed with 25 kg of binder, mix of lignin, lignosulfonate + α-cellulose (1 : 1) with dry basis of 50%, ash content of 0.8%, fraction of insolubles in mass of dry substances of 0.8%. Paraffin in the quantity of 1% was added and mixed with speed of 20- 60 r.p.m. and temperature 20- 24° C to form relatively homogeneous mass that was then sent to the mold and under pressure of 85 atm. briquettes with diameter of 63 mm and height of 23 mm. were molded. Example 20. Leaf and needle wood shavings and sawdust were dried to moisture content of 16- 20 % and in the quantity of 75 kg were mixed with 25.0 kg of binder, lignin + lignosulfonate, with dry basis of 50%, ash content of 0.8%, fraction of insolubles in mass of dry substances of 0.8%. Mixing was done with speed of 20- 60 r.p.m. at temperature 20- 24° C to form relatively homogeneous mass that was then sent to the mold and under pressure of 85 atm. briquettes with diameter of 63 mm and height of 23 mm were molded. Example 21. Leaf and needle wood shavings and sawdust were dried to moisture content of 16- 20 % and in the quantity of 75 kg were mixed with 25.0 kg of binder, lignin + black sulfate liquor. Paraffin in the quantity of 1% was added and mixed with speed of 20- 60 r.p.m. at 12 temperature 20- 24° C to form relatively homogeneous mass that was then sent to the mold and under pressure of 85 atm. briquettes with diameter of 63 mm and height of 23 mm were molded. Example 22. Leaf and needle wood shavings and sawdust were dried to moisture content of 16- 20 % and in the quantity of 75 kg were mixed with 25.0 kg of binder, lignin + hydrolytic lignin. Paraffin in the quantity of 1% was added and mixed with speed of 20- 60 r.p.m. at temperature 20- 24° C to form relatively homogeneous mass that was then sent to the mold and under pressure of 85 atm. briquettes with diameter of 63 mm and height of 23 mm were molded. 13 Table 2 Basic quality values of briquettes manufactured from compositions according examples 1 -22. Example JM Briquette quality values Heat value, cal/g Ash content, % Density, g/cm 3 1 4874 0.91 1.12 2 4626 0.97 1.05 3 51 12 0.81 1.14 4 4923 0.92 1.1 1 5 4897 0.92 1.12 6 6985 1.30 1.18 7 6790 1.20 1.17 8 6812 0.91 1.15 9 6924 0.73 1.16 10 7036 0.84 1.12 1 1 6795 0.92 1.18 12 6913 0.86 1.16 13 6950 0.75 1.17 14 6790 0.83 1.09 15 6954 0.71 1.15 16 6124 0.95 1.07 17 5012 0.91 1.14 18 7251 0.85 1.13 19 71 17 0.82 1.14 20 4516 0.97 1.13 21 5234 0.92 1.14 22 5129 0.92 1.10 A.C.JNS 171828 4964 1.7 0.71 It should be noted that use of less than 2.4 mass% of lignin-containing products for manufacture of fuel briquettes results in drastic reduction of density and strength of ready products. Whereas concentration of lignin-containing products over 36.9 mass% becomes economically unfeasible since it does not bring further increase in efficiency of briquette combustion. Thus, the proposed composition allows manufacture of ecologically clean fuel briquettes from practically any solid secondary carbon-containing feed stock featuring high calorific value (up to 7 000 cal/g), density of 1.04- 1.18 g/cm , ash content of 0.8- 1.2 %. 14 Consumption of utilities for manufacture of such fuel might be significantly reduced as compared with the well known processes for manufacture of fuel briquettes through possible avoidance of high-temperature methods.

Claims: 75 Claims 1. Composition for manufacture of fuel briquettes including crushed secondary carbon- containing feed stock and binder, characterized in that it comprises as secondary carbon-containing feed stock petroleum pitch, coal pitch, coal dust, crushed coal product, crushed peat, wood shavings, sawdust or their mixes, and as binder - lignin- containing product selected from the group: lignin, lignosulfonate, hydrolytic lignin, black sulfate liquor or their mixes, or mix of one or several above enumerated lignin-containing products with α-cellulose. 2. Composition as per cl. 1 , char cterized in that it comprises carbon- containing feed stock and lignin-containing product at ratio, mass %: carbon-containing feed stock 63.1-97.6; lignin-containing product 2.4- 36.9. 3. Composition as per cl.1, characterized in that it comprises as binder mix of one or several lignin-containing products with α-cellulose at ratio, accordingly, (1- 32) : 1. 4. Composition as per cl. 1, characterized in that it comprises as lignin- containing product lignosulfonates pre oxidized in acid medium at 120- 150° C. 5. Composition as per cl. 1, characterized in that binder comprises as supplementary paraffin in the quantity of 0.5- 2.5 mass%.

Inventors: ARTEMOV ARSENY VALERIEVICH, MYASOEDOVA VERA VASILIEVNA, ARTEMOV, ARSENY VALERIEVICH, MYASOEDOVA, VERA VASILIEVNA
Applicants: MYASOEDOVA VERA VASILIEVNA, ARTEMOV, ARSENY VALERIEVICH, MYASOEDOVA, VERA VASILIEVNA
Application year: 1998
Main classification: C10L5
IPC codes: C10L5