Dielectric material and process for producing the same

Abstract: A dielectric material based on BaO-RE 2 O 3 -TiO 2 is disclosed, which has a relatively high relative permittivity ε r , a small absolute value of the temperature coefficient of resonance frequency τ f , and a high coefficient of unloaded quality Q u . Processes for producing the dielectric material are also disclosed. The dielectric material comprises 100 parts by weight of main ingredients having a composition represented by xBaO-yRE 2 O 3 -zTiO 2 (wherein RE represents a rare earth element and x+y+z=100 ) and up to 5 parts by weight of at least one alkali metal oxide. This alkali metal oxide serves to improve ε r and Q u without a considerable sacrifice of τ f . The RE preferably consists of samarium or a combination of samarium with neodymium and/or lanthanum. In producing the dielectric material, a dense sintered body can be obtained without fail by using a raw material containing hydroxyl groups as a starting material for the rare-earth ingredient among the main ingredients.

Description: The present invention relates to processes for producing a dielectric material. More particularly, this invention relates to a dielectric material having excellent properties, i.e., a relatively large value of relative permittivity (hereinafter referred to as "∈ r ") in a high-frequency region, a small absolute value of the temperature coefficient of resonance frequency (hereinafter resonance frequency is referred to as "f 0 " and the temperature coefficient thereof is referred to as "τ f "), and a large value of unloaded quality coefficient (hereinafter referred to as "Q u "), and to processes for producing the same. The dielectric material of the present invention is advantageously used in applications such as multilayer circuit boards, in particular, resonators and filters for use in a high-frequency region. With the recent increase in the amount of communication information, rapid progress is being made in various communication systems utilizing the microwave region, such as, e.g., car telephones, satellite communication, and satellite broadcasting, and many microwave dielectric materials have been developed therewith. Among-such microwave dielectric materials, the dielectric porcelains for use in resonators, filters, and the like are required to have the following properties (i) to (iii): (i) to have a high relative permittivity ∈ r ; (ii) to have a high unloaded quality coefficient Q u (i.e., a small dielectric loss 1/Q u ); and (iii) to have a small absolute value of the temperature coefficient τ f of resonance frequency f 0 (i.e., a small temperature dependence of f 0 ). Dielectric materials such as Ba(Mg 1/3 Ta 2/3 )O 3 and Ba(Zn 1/3 Ta 2/3 )O 3 have been known to have a small dielectric loss among those properties, while dielectric materials such as BaO-RE 2 O 3 -TiO 2 (wherein RE represents a rare earth element) have been known to have a high relative permittivity. In JP-A-6-275126 (the term "JP-A" as used herein means an "unexamined published Japanese patent application") is disclosed a dielectric porcelain composition which comprises barium (Ba), bismuth (Bi), titanium (Ti), and oxygen (O) as essential components and may contain neodymium (Nd) and samarium (Sm) as optional components. In JP-A-6-309926 and JP-A-6-325620 is disclosed a dielectric porcelain composition which has been improved in dielectric characteristics by incorporating sodium (Na), potassium (K), and lithium (Li) into the dielectric porcelain composition described above. Specifically, there is a description therein which contains "the value of Q can be improved without changing relative permittivity ∈ r ". EP-A-701981 discloses a dielectric ceramic composition mainly comprising a major component which comprises barium, titanium, neodymium, samarium and oxygen, and a minor component mainly comprising a glass powder having a softening point of from 100 to 500°C and mainly comprising PbO, ZnO and B 2 O 3 , and GeO 2 . The major component may further contain Bi 2 O 3 . JP-A-9-77556 discloses a dielectric ceramic composition comprising complex oxides of barium, titanium, lithium and rare earth elements. The maximum amount of rare earth element oxide in this composition is 0.48 mol%. An object of the present invention is to provide a dielectric material based on the composition BaO-RE 2 O 3 -TiO 2 which need not contain bismuth (Bi) as an essential component, unlike the dielectric porcelain compositions described above, and having a further improved Q u as compared with the conventional compositions. Another object of the present invention is to provide processes suitable for producing the dielectric material. The present inventors have found that the ∈ r and Q u of a BaO-RE 2 O 3 -TiO 2 dielectric material can be improved without a considerable sacrifice (deterioration) of τ f by incorporating a small amount of an alkali metal oxide, which has been regarded as an undesirable ingredient generally functions to increase dielectric loss. They have further found processes for producing, without fail, a dense sintered body having the above composition and excellent dielectric characteristics. The present invention has been completed based on these findings. The present invention provides, as described in an aspect of the present invention, a dielectric material which consists of: a composition represented by xBaO-yRE 2 O 3 -zTiO 2 as a main ingredient, wherein RE represents at least one rare earth element and x+y+z=100 mol%, wherein 5.0≤x≤27.0 mol%, 4.0≤y≤29.0 mol%, and 56.0≤z≤80.0 mol%, and at least one alkali metal oxide, wherein the content of said at least one alkali metal oxide is 0.1 to 0.5% by weight. The present invention further provides a process for producing such a dielectric material, said process comprising the steps of: mixing a starting material for the barium ingredient, a starting material for the rare-earth element containing a hydroxyl group, a starting material for the titanium ingredient and a starting material for the alkali metal ingredient to produce a mixture; compacting the mixture to produce a compact; and sintering the compact to prepare the dielectric material. Moreover, the present invention provides a process for producing a dielectric material as defined above, said process comprising the steps of: introducing a hydroxyl group into the surface of a starting material for the rare-earth element to prepare a starting material for the rare-earth element containing a hydroxyl group; mixing a starting material for the barium ingredient, the starting material for the rare-earth element containing a hydroxyl group, a starting material for the titanium ingredient and a starting material for the alkali metal ingredient to produce a mixture; compacting the mixture to produce a compact; and sintering the compact to prepare the dielectric material. The present invention also relates to a dielectric filter and a dielectric resonator each containing such a dielectric material. Preferred embodiments of the present invention are set forth in the sub-claims. Fig. 1 is an FT-IR chart of hydroxyl-containing Sm 2 O 3 used as a starting material for a rare-earth ingredient in the Examples. Fig. 2 is an FT-IR chart of hydroxyl-free Sm 2 O 3 used as a starting material for a rare-earth ingredient in the Examples. Fig. 3 illustrates a dielectric resonator utilizing the dielectric material of the present invention. Fig. 4 illustrates a dielectric filter utilizing the dielectric material of the present invention. Fig. 5A is a perspective view of a dielectric filter utilizing the dielectric material of the present invention, and Fig. 5B is a front view of taken from the open end surface of Fig. 5A. The "alkali metal oxide" for use in the present invention is preferably the oxide of lithium (Li), sodium (Na), or potassium (K) because it is inexpensive and easy to handle. By incorporating an alkali metal oxide, ∈ r and Q u can be improved without a considerable sacrifice of τ f . The incorporation of an alkali metal oxide is also effective in attaining a reduced sintering temperature. Namely, a sufficiently dense sintered body can be obtained even at a lower sintering temperature. In producing the dielectric material, the alkali metal may be added either in the form of the oxide thereof or as the carbonate, nitrate, oxalate, or sulfate thereof or the like. When x, y, and z in the main ingredient satisfy 5.0≤x≤27.0, 4.0≤y≤29.0, and 56.0≤z≤80.0, especially 10.0≤x≤22.5, 11.0≤y≤21.0, and 62.5≤z≤72.5, a dielectric material having excellent dielectric characteristics can be obtained when the content of the alkali metal oxide is 0.1 to 0.5% by weight, preferably 0.15 to 0.3% by weight. The dielectric material of the present invention has a relative permittivity of 50 or more, a product of the unloaded quality coefficient and resonance frequency of 5,700 GHz or more, and a temperature coefficient of resonance frequency of between -20 and +20 ppm/°C. In the main ingredient, RE comprises one or more rare earth elements and preferably comprises at least samarium. As a second aspect of the present invention, RE 2 O 3 among the main ingredients is preferably a rare-earth oxide represented by the composition formula {(Sm 2 O 3 ) 1-a-b (Nd 2 O 3 ) a (La 2 O 3 ) b } (wherein 0≤a<1, 0≤b<1, and a+b<1). This means that the RE 2 O 3 comprises at least an oxide of samarium (Sm), and it consists of a samarium oxide alone (a=b=0) or of a samarium oxide in which the samarium has been partly replaced by neodymium (Nd) and/or lanthanum (La). With respect to the proportion of Sm 2 O 3 , the relationship: 0.25≤1-a-b≤1 is preferred. The dielectric material of the present invention may have a value of ∈ r as large as 50 to 90. The dielectric material of the present invention has a product of the unloaded quality coefficient and resonance frequency of 5,700 GHz or more, preferably 6,500 GHz or more. The dielectric material of the present invention has a temperature coefficient of resonance frequency of between -20 and +20 ppm/°C, preferably between -10 and +10 ppm/°C. The dielectric material of the present invention may be produced by mixing the raw materials, (optionally calcining the mixture), compacting the mixture, and sintering the compact. The calcination may be conducted at a temperature of 1,000 to 1,200°C for 1 to 3 hours (e.g., 1000°C, 2 hours). The sintering may be conducted at a temperature of 1,250°C to 1,400°C for 1 to 5 hours (e.g., 1,350°C, 2 hours). The dielectric material of the present invention is produced, for example, by the process described below. In this process, a raw material containing hydroxyl groups is used as a starting material for the rare-earth ingredient among the main ingredient. The term "a starting material containing hydroxyl groups" means that the starting material, when analyzed by Fourier-transform infrared absorption spectrometry (hereinafter referred to as "FT-IR"), gives a chart having a peak assignable to hydroxyl. Examples of such a raw material include rare-earth oxides having a layer of adsorbed water on the particle surface thereof and rare-earth hydroxides. Preferred of these are rare-earth hydroxides represented, for example, by the composition formula RE(OH) 3 . By using a raw material containing hydroxyl groups as described above, a dielectric material which is dense and capable of being sufficiently analyzed for dielectric characteristics can be obtained even when a nonaqueous solvent, e.g., ethanol, is used as a dispersion medium for primary mixing/pulverization in producing the dielectric material. Although the reason for this has not been fully elucidated, it is thought that the hydroxyl groups contained in the starting material are eliminated during calcination or sintering to activate the surface of the raw material, whereby sintering reactions are accelerated and the compact becomes more apt to be densified. Also in the case where at least one member selected from rare-earth oxalates, rare-earth chlorides, rare-earth nitrates, and rare-earth sulfates is used as a starting material besides a rare-earth hydroxide, the functional groups in these rare-earth compounds are eliminated likewise during calcination or sintering, whereby sintering reactions are accelerated and a dense dielectric material can be obtained. Even when a rare-earth compound, e.g., oxide, in which no hydroxyl groups are detected, e.g., by FT-IR is used as a starting material, the dielectric material of the present invention can be produced by conducting a step of incorporating hydroxyl groups into the starting material or by using water as a dispersion medium, for example, in the step of mixing raw materials. On the other hand, if a raw material containing no hydroxyl groups is used as a starting material and a nonaqueous solvent is used as a dispersion medium for primary mixing/pulverization, the result is a problem that the densification of the dielectric material is insufficient and the dielectric characteristics thereof cannot be determined. It is especially preferred to use samarium as an essential rare-earth element in the above-described processes for producing the dielectric material of the present invention. From the standpoint of density, the dielectric material of the present invention preferably has a degree of volumetric shrinkage of 15% or more, or preferably has a coefficient of water absorption of 0.1% or less. Examples The present invention will be explained below in more detail by reference to Examples and Comparative Examples. Hereinafter, "parts by weight" is referred to simply as "parts". (1) Investigation on Dielectric Material Compositions Samples Nos. 1 to 31 of Examples each having a composition according to the present invention and samples Nos. 32 to 38 of Comparative Examples were produced by the following method. Given amounts of commercial powders of BaCO 3 , Sm(OH) 3 , TiO 2 , and A 2 CO 3 (wherein A represents an alkali metal) were weighed out so as to result in each of the compositions shown in Tables 1 and 2 in terms of oxide proportion. These compositions each corresponds to main dielectric material ingredients represented by the composition formula given in the second aspect of the present invention in which a=b=0. The powders for each composition were wet-mixed using an ethanol solvent, and the powder mixture obtained was calcined in the air atmosphere at 1,000°C for 2 hours. To each of these calcinated products were added a wax binder, a dispersant, and ethanol. These mixtures each was pulverized and mixed by means of a ball mill. The resultant slurries were dried, granulated, and then compacted at a pressure of 10 MPa into a cylindrical form having a diameter of 20 mm and a thickness of 12 mm. Subsequently, the compacts were subjected to CIP (cold isostatic pressing) at a pressure of 150 MPa and then sintered for 2 hours in the air atmosphere at each of the temperatures shown in Tables 1 and 2. Thus, dielectric material samples Nos. 1 to 38 were obtained. Sample Nos. 32 and 35-38 is a dielectric material containing no alkali metal oxide, while samples Nos. 33 and 34 are dielectric materials each containing too large an amount of an alkali metal oxide. The sintered bodies (dielectric materials) obtained were subjected to surface grinding and then examined for relative permittivity ∈ r , unloaded quality coefficient Q u , and temperature coefficient of resonance frequency τ f by the Hakki and Coleman's method in a frequency range of from 2 to 4 GHz (temperature range: 25-80°C). The results obtained are shown in Tables 1 and 2. Sample No. Main Ingredient (mol%) Alkali Metal Oxide (A 2 O) Sintering Temperature (°C) Dielectric Characteristics BaO Sm 2 O 3 TiO 2 Metal kind Amount (parts) ε r Q u ×f 0 (GHz) τ f (ppm /°C x y z Example 1 25.0 15.0 60.0 Na 1.0 1350 84 5830 +10 2 22.5 10.0 67.5 ↑ 2.7 1300 83 6120 +6 3 15.0 25.0 60.0 ↑ 2.0 1300 82 5700 -7 4 13.0 17.0 70.0 ↑ 0.3 1350 85 7600 -10 5 22.5 15.0 62.5 ↑ 1.2 1330 80 6500 +10 6 7.5 15.0 77.5 ↑ 4.5 1280 84 6800 -15 7 16.0 16.0 68.0 ↑ 0.5 1350 84 7800 0 8 16.5 16.5 67.0 Li 0.8 82 7150 +10 9 15.5 15.5 69.0 K 0.2 85 7500 -5 10 17.5 17.5 65.0 Na 0.25 66 6600 +10 11 10.0 72.5 ↑ 0.50 66 8500 0 12 ↑ 0.75 68 8200 +9 13 7.5 75.0 ↑ 0.25 57 10300 +5 14 ↑ 0.50 59 9700 +9 15 5.0 77.5 ↑ 51 10800 +13 16 ↑ 0.75 50 10200 +15 17 15.0 15.0 70.0 ↑ 0.25 75 6800 -16 18 ↑ 0.50 76 7700 -11 19 ↑ 0.75 78 7500 -6 20 12.5 72.5 ↑ 0.50 71 8100 -3 21 ↑ 0.75 71 7900 +1 Sample No. Main Ingredient (mol%) Alkali Metal Oxide (A 2 O) Sintering Temperature (°C) Dielectric Characteristics BaO Sm 2 O 3 TiO 2 Metal kind Amount (parts) ε r Q u ×f 0 (GHz) τ f (ppm /°C) x y z Example 22 15.0 10.0 75.0 Na 0.50 67 8200 +5 23 ↑ 1.00 63 7300 +10 24 7.5 77.5 ↑ 0.50 61 9000 +15 25 ↑ 0.75 60 8000 +17 26 ↑ 1.00 60 8100 +19 27 5.0 80.0 ↑ 0.50 56 8400 +20 28 12.5 15.0 72.5 ↑ 0.75 84 7400 +10 29 12.5 75.0 ↑ 79 7700 +18 30 7.5 80.0 ↑ 70 8600 +25 31 10.0 10.0 80.0 ↑ 1.00 80 6700 +18 Comp. Example 32 12.5 20.0 67.5 - - 1400 75 2510 +10 33 14.0 19.0 67.0 Na 6.0 1280 83 2500 -30 34 16.5 15.0 68.5 K 10.0 1250 90 1280 -100 35 17.5 5.0 77.5 - - 1350 Very weak resonance 36 15.0 15.0 70.0 - - 37 12.5 72.5 - - 38 7.5 77.5 - - Tables 1 and 2 show the following. Samples Nos. 1 to 31, which were dielectric materials according to the present invention, each had a value of ∈ r as large as 50 to 90, a high Q u value and an absolute value of τ f as small as 30 ppm/°C or below. Especially, when z was less than 80 mol%, each of absolute values of τ f was 19 ppm/°C or less, which were not lowered so much compared with sample No. 32, a comparative sample containing no alkali metal oxide, and at least, either ∈ r or Q u ×f 0 value was improved compared with sample No. 32. Furthermore, samples Nos. 1 to 31 were capable of being sintered at lower temperatures than sample No. 32, and each gave a sufficiently dense sintered body. On the other hand, samples Nos. 33 and 34, which were dielectric materials each containing too large an amount of an alkali metal oxide, each had a significantly reduced Q u ×f 0 and a large minus value of τ f , although improved in ∈ r as compared with sample No. 32. Furthermore, sample Nos. 35 to 38, which were comparative samples not containing alkali metal oxides, showed very weak resonance even if the main ingredient composition were varied, so that it was impossible to evaluate dielectric characteristics. (2) Investigation of Starting Materials Samples Nos. 39 to 41 which had the same composition as sample No. 7 were produced using Sm 2 O 3 containing hydroxyl groups or Sm 2 O 3 containing no hydroxyl groups in place of the Sm(OH) 3 used as a starting material for the samarium ingredient in producing sample No. 7. FT-IR charts of the "Sm 2 O 3 containing hydroxyl groups" and "Sm 2 O 3 containing no hydroxyl groups" used are shown in Figs. 1 and 2, respectively. The same starting materials and method as those for sample No. 7 were used, except that the two raw materials shown above were used as a starting material for the samarium ingredient, and that the sintering temperatures shown in Table 3 were used. These samples were examined for dielectric characteristics in the same manner as in (1) above. The results obtained are shown in Table 3 together with the degree of volumetric shrinkage by sintering of each sample. Table 3 shows that sample No. 7, produced using Sm(OH) 3 as a starting material for the samarium ingredient, and sample No. 39, produced using hydroxyl-containing Sm 2 O 3 as the starting material, each was a dense sintered body which had a degree of volumetric shrinkage by sintering as high as 20% or above. These samples further had satisfactory dielectric characteristics. On the other hand, samples Nos. 40 and 41, produced using hydroxyl-free Sm 2 O 3 as a starting material for the samarium ingredient, each had a degree of volumetric shrinkage as low as 11% or below and had been insufficiently densified. Dielectric characteristics of these two samples were hence unable to be determined. Although use of a higher sintering temperature enhanced the degree of shrinkage in some degree (sample No. 41), it failed to attain denseness sufficient for the determination of dielectric characteristics. (3) Investigation on Dispersion Media for Primary Mixing/Pulverization Sample No. 42 was produced using the same raw materials and method as those for sample No. 40, except that water was used in place of ethanol, which was used in the preparation of sample No. 40, as the dispersion medium for primary mixing/pulverization. In Table 4 are shown the degree of volumetric shrinkage by sintering of sample No. 42 and the dielectric characteristics thereof determined in the same manner as in the above (1). Table 4 shows that even when a starting material containing no hydroxyl groups was used, a sufficiently dense sintered body having a degree of shrinkage heightened to 23.6% and excellent dielectric characteristics was obtained by using water as the dispersion medium for primary mixing/pulverization. (4) Investigation on Rare Earth Elements Samples Nos. 43 to 45 were produced which each had the same composition as sample No. 4 except that part of the samarium had been replaced by neodymium as shown in Table 5. As a starting material for the neodymium ingredient was used Nd 2 O 3 containing no hydroxyl groups. Except the above, the same raw materials and method as those for sample No. 4 were used. These samples were examined for dielectric characteristics in the same manner as in (1) above. The results obtained are shown in Table 5. Table 5 shows that each of samples Nos. 43 to 45, in which the samarium had been partly replaced by neodymium, had excellent dielectric characteristics like sample No. 4. Table 5 further shows that as the degree of replacement by eodymium increased, from sample No. 43 to sample No. 45, the value of τ f shifted to the plus side. It can be seen from these results that by regulating the samarium/neodymium ratio, the value of τ f can be controlled without exerting a considerable influence on ∈ r and Q u ×f 0 . It can also be seen from the results of these Examples that even when a hydroxyl-free starting material for the neodymium ingredient was used, densification is possible as long as a hydroxyl-containing raw material was used as a starting material for the samarium ingredient. (5) An Example of Dielectric Resonator Prepared by Using Dielectric Material of the Invention The dielectric material of the present invention may be used in a dielectric resonator described in US-A-5,136,270. Fig. 3 illustrates an example of such a dielectric resonator of providing resonator body 1 comprising the dielectric material of the present invention. The resonator body 1 is bonded to one end of holding member 2 by means of, for example, an epoxy resin type adhesive. The integrated resonator body 1 and holding member 2 are contained in the inside of metal container 4 of a cylindrical shape the both end surface of which are sealed up. One end of the holding member 2 is fixed and bonded to the center of the bottom surface 4a of the metal container 4 by means of PTTF. (6) An Example of Dielectric Filter Prepared by Using Dielectric Material of the Invention The dielectric material of the present invention may be used in a dielectric filter described in US-A-5,537,085. Fig. 4 illustrates an example of such a four pole high zero interdigital block filter 110. The filter 110 includes a filter body 112 having a block of the dielectric material of the present invention and having top and bottom surfaces 114 and 116 and side surfaces 118, 120, 122 and 124. The filter body has a plurality of through-holes extending from the top surface to the bottom surface 114 to 116 defining a first resonator 101, a second resonator 102, a third resonator 103, and a fourth resonator 104. The surfaces 118, 120, 122 and 124 are substantially covered with a conductive material defining a metallized exterior layer, with the exception that the top surface 114 and the bottom surface 116 are selectively metallized in the areas substantially surrounding the resonators defining an interdegital filter design. More specifically, top surface 114 adjacent to a first and a third resonator 101 and 103 are unmetallized 125, and a bottom surface 116 adjacent to a second 102 and a fourth resonator 104 are unmetallized 128. To complete the interdigital design, the bottom surface 116 adjacent to a first and a third resonator 101 and 103 are metallized 127, and the top surface adjacent to the second and a fourth resonator 104 are metallized 126. Additionally, a portion of one of the side surfaces is substantially uncoated (comprising the dielectric material) in proximity to one of the ends of the block, and extends at least in proximity to between alternate resonators, defining a magnetic transmission line 132 for magnetically coupling the resonators. The ceramic filter 110 also includes first and second input-output means, and preferably in the form of pads 134 and 138 comprising an area of conductive material on at least one of the side surfaces and substantially surrounded by at least one or more uncoated areas 136 and 140 of the dielectric material. In this embodiment, the input-output pads 134 and 138 are offset on opposite ends of the block. This is necessary because the input-output pads are located near the non-grounded ends of their respective resonators to achieve maximum electrical coupling. In the four-pole resonator design in Fig. 4, the first resonator 101 and the fourth resonator 104 are grounded at opposite ends of the block filter 110, thus requiring the input-output pads to be offset at opposite ends of the block. The magnetic transmission line 132 may be located on the front surface of the block 120, on the rear surface of the block 124, or both the front and rear surfaces of the block as design parameters dictate. However, in a preferred embodiment, only a single magnetic transmission line 132 is placed on the rear surface 124 opposite to the surface 120 containing the input-output pads 134 and 138. The magnetic transmission line 132 can be varied to achieve maximum design flexibility. In this embodiment, the magnetic transmission line 132 may extent laterally at least in proximity to the first and third resonators or it may extend laterally in proximity to the second and fourth resonators, shown as item 133 in Fig. 4. The four pole interdigital block filter 110 can lead to a product which is easier to manufacture, and require less processing steps, than conventional four pole ceramic block filters. (7) A second Example of Dielectric Filter Prepared by Using Dielectric Material of the Invention The dielectric material of the present invention may be used in a dielectric filter described in US-A-5,612,654. For example, the dielectric filter shown in Figs. 5A and 5B includes resonator holes 202a and 202b. In the structure shown in Figs. 5A and 5B, the coupling between the two resonators formed at resonator holes 202a and 202b is inductive coupling, and one attenuation pole is formed in the high frequency range of the pass band. A pair of input/output electrodes 205 are formed at prescribed portions on the outer surface of dielectric block 201. Inner conductors 203 are formed on the inner surfaces of resonator holes 202a and 202b. While the invention has been described in detail and with reference to specific embodiments thereof, it will be apparent to one skilled in the art that various changes and modifications can be made therein according to purposes or applications without departing from the scope of the claims. Furthermore, besides the main ingredients and alkali metal oxide described above, other additives or unavoidable impurities and the like may be contained in the dielectric material of the present invention as long as the dielectric characteristics of the dielectric material are not substantially influenced thereby. The dielectric material of the present invention has excellent properties, i.e., a relatively high relative permittivity ∈ r , a small absolute value of the temperature coefficient of resonance frequency τ f , and a high coefficient of unloaded quality Q u . The dielectric material is therefore useful in multilayer circuit boards, in particular, resonators, filters, and the like used in a high-frequency region. According to the processes of the present invention, the dielectric material described above can be produced as a dense sintered body without fail.

Claims: A dielectric material which consists of: a composition represented by xBaO-yRE 2 O 3 -zTiO 2 as a main ingredient, wherein RE represents at least one rare earth element and x+y+z=100 mol%, wherein 5.0≤x≤27.0 mol%, 4.0≤y≤29.0 mol%, and 56.0≤z≤80.0 mol%, and at least one alkali metal oxide, wherein the content of said at least one alkali metal oxide is 0.1 to 0.5% by weight. The dielectric material of claim 1, wherein the rare-earth oxide represented by RE 2 O 3 in the main ingredient is represented by the composition formula {(Sm 2 O 3 ) 1-a-b (Nd 2 O 3 ) a (La 2 O 3 ) b }, wherein 0≤a<1, 0≤b<1, and a+b<1. The dielectric material of claim 1 or 2, which is produced by using a raw material thereof containing a hydroxyl group as a starting material for the rare-earth element in the main ingredient. The dielectric material of any one of claims 1 to 3, which shows a degree of volumetric shrinkage by sintering of 15% or more. The dielectric material of any one of claims 1 to 4, which has a coefficient of water absorption of 0.1% or less. The dielectric material of any one of claims 1 to 5, which has a relative permittivity of 80 or more, a product of the unloaded quality coefficient and resonance frequency of 5,700 GHz or more, and a temperature coefficient of resonance frequency of between -20 and +20 ppm/°C. A process for producing a dielectric material as claimed in any one of claims 1 to 6, which comprises the steps of: mixing a starting material for the barium ingredient, a starting material for the rare-earth element containing a hydroxyl group, a starting material for the titanium ingredient and a starting material for the alkali metal ingredient to produce a mixture; compacting the mixture to produce a compact; and sintering the compact to prepare the dielectric material. The process of claim 7, wherein the starting material for the rare-earth element containing a hydroxyl group is a rare-earth hydroxide represented by the composition formula RE(OH) 3 . A process for producing a dielectric material as claimed in any one of claims 1 to 6, which comprises the steps of: introducing a hydroxyl group into the surface of a starting material for the rare-earth element to prepare a starting material for the rare-earth element containing a hydroxyl group; mixing a starting material for the barium ingredient, the starting material for the rare-earth element containing a hydroxyl group, a starting material for the titanium ingredient and a starting material for the alkali metal ingredient to produce a mixture; compacting the mixture to produce a compact; and sintering the compact to prepare the dielectric material. The process of claim 9, wherein the steps of introducing and mixing are conducted by mixing a starting material for the barium ingredient, a starting material for the rare-earth element, a starting material for the titanium ingredient and a starting material for the alkali metal ingredient, in the presence of water as a dispersion medium. The process of any one of claims 7 to 9, wherein at least samarium is used as the rare earth element. A dielectric filter comprising the dielectric material as claimed in any one of claims 1 to 6. A dielectric resonator comprising the dielectric material as claimed in any one of claims 1 to 6.

Inventors: OHBAYASHI KAZUSHIGE, SATO MOTOHIKO, YOKOI HITOSHI, OHBAYASHI, KAZUSHIGE, SATO, MOTOHIKO, YOKOI, HITOSHI
Applicants: NGK SPARK PLUG CO, NGK SPARK PLUG CO., LTD
Application year: 1998
Main classification: C04B35
IPC codes: H01P7, H01B3, H01P1, C04B35, H01G4