BLENDS OF POLYPROPYLENES

Abstract: The invention includes a blend composition comprising (a) from 1 to 15 weight percent of amorphous polypropylene (b) from 99 to 85 weight percent of crystalline polypropylene, wherein the molecular weight of the amorphous polypropylene is lower than the molecular weight of the crystalline polypropylene; the molecular weight (Mw) of the amorphous polypropylene is higher than 50,OOO, preferably 100,OOO g/mole; the amorphous polypropylene has a MWD less than 3; and wherein the percentages are based on total amorphous plus crystalline polypropylene. Preferably, amorphous and crystalline polypropylenes are preferably at least 90 weight percent propylene units. Preferably, the amorphous polypropylene has a glass transition temperature greater than -10 DEG C. The invention includes processes for preparing compositions of the invention, including a multistage process. Additionally the invention includes articles, sheets, films, foams and fibers comprising or prepared from compositions of the invention as well as processes for making the things, preferably processes involving stretching a composition of the invention. The processes include a process comprising extrusion or injection blow molding; extruding, or thermoforming a composition of the invention; as well as a process comprising reacting a composition of the invention with a coupling agent.

Description: BLENDS OF POLYPROPYLENES This invention relates to polypropylene, more particularly to blends of ' polymers having repeating units derived from propylene. Amorphous polypropylene is well known in the art. The term amoφhous refers to the substantial absence of crystallinity in the polymer; for polypropylene homopolymer this means that the polymer is atactic, without any isotactic segments giving rise to crystallinity, as can be determined by the absence of a melting point and a heat of fusion of less than 10 J/g in DSC. Atactic polymers are defined as having no consistent patterns among chiral sequences [Mark H., Bikales N., Encyclopedia of Polymer Science and Engineering, Volume 9, John Wiley & Sons Inc, 1987, page 800] as can be determined by 13 C NMR [Karger-Kocsis J., Polypropylene, Structure blends and composites, 1. Structure and Morphology, Chapman & Hall, 1995, pagesl5-19]. It is, for instance, formed as a by-product of the production of isotactic polypropylene using Ziegler-Natta catalysis. This amorphous polypropylene fraction is generally of low molecular weight (wax) with a broad molecular weight distribution, and as such either used in for example adhesives applications or discarded as landfill. Although these polymers have been referred to as "amoφhous", they often are not completely atactic; rather they contain some isotactic segments. Amoφhous polyolefins, such as the amoφhous polypropylene produced using Ziegler-Natta catalysis, have been used in blends with crystalline isotactic polypropylene to improve the flexibility of mechanically strong isotactic polypropylene. Patent document EP 527589 teaches the production of a blend of (a) 20-80 percent by weight of an amoφhous polyolefin having a propylene and/or butene-1 component content of 50 percent by weight or more, and (b) 80-20 percent by weight of a crystalline polypropylene. These blends are claimed to be well balanced in mechanical strength and flexibility. However, amoφhous polypropylenes produced by Ziegler-Natta catalysis reduce the overall mechanical strength of a blend of amoφhous polypropylene and crystalline polypropylene. Production of high molecular weight amoφhous atactic polypropylene with a narrow molecular weight distribution is taught in the art to be attainable by using single site catalysts. Patent documents EP 604917 and EP 604908 teach the synthesis of amoφhous polypropylene polymers which are claimed to have 5 interesting elastomeric properties. The characteristics of the polymers, according to EP 604917 are: intrinsic viscosity > 1 dl/g, percent (r) minus (-) percent (m) >0 wherein percent (r) is the percent of syndiotactic diads and percent (m) is the percent of isotactic diads, less than 2 percent of the CH 2 groups contained in sequences (CH 2 ) n with n >2, Bernoullianity index B=l ± 0.2, and a narrow o molecular weight distribution. Patent documents WO 96/23838, US Patent 5539056 and US Patent 5516848 teach the production of a blend of an amoφhous poly-α-olefm of molecular weight (Mw) at leastl 50,000 (produced using single site catalysis) and a crystalline poly-oc-olefin with Mw less than 300,000, (produced using single site 5 catalysis) in which the molecular weight of the amoφhous polypropylene is greater than the molecular weight of the crystalline polypropylene. The preferred blends comprise 10 to 90 weight percent of amoφhous polypropylene. These blends are claimed to exhibit unusual elastomeric properties, namely an improved balance of mechanical strength and rubber recovery properties. o Patent document US Patent. 5483002 and Patent Document EP 643100 teach the production of a blend of a semi-crystalline propylene homopolymer having a melting point of 125 to 165°C and a semi-crystalline propylene homopolymer having a melting point below 130°C or a non-crystallizing propylene homopolymer having a glass transition temperature which is less than or 5 equal to -10°C. These blends are claimed to have improved mechanical properties, notably impact strength. Crystalline polypropylene is used in many film or sheet forming processes, such as biaxially oriented PP production, blow molding and thermoforming. In these processes achieving the desired degree of stretching and orientation in the 0 film or sheet is a problem. Stretching must occur between the moment the film or sheet leaves the die as a melt and the time the melt has cooled to a complete solid. Achieving a stable running process, in which the film or sheet production is not limited by breakage or rupturing of the film or sheet is also a problem. The invention includes a blend composition comprising (a) from 1 to 15 weight percent of amoφhous polypropylene (b) from 99 to 85 weight percent of crystalline polypropylene, wherein the molecular weight of the amoφhous polypropylene is lower than the molecular weight of the crystalline polypropylene; the molecular weight (Mw) of the amoφhous polypropylene is higher than 50,000, preferably 100,000 g/mole; the amoφhous polypropylene has a MWD less than 3; and wherein the percentages are based on total amoφhous plus crystalline polypropylene. Preferably, amoφhous and crystalline polypropylenes are preferably at least 90 weight percent propylene units. Preferably, the amoφhous polypropylene has a glass transition temperature greater than -10°C. Optionally at least one of the crystalline polypropylene or amoφhous polypropylene is propylene polymerized with one or more other monomers addition polymerizable with propylene, which monomer is preferably a polyene, preferably having at least 7 carbon atoms. In one embodiment, both the amoφhous and the crystalline polypropylenes are prepared using a single site catalyst. Either of the polypropylenes or the blend is optionally, and the amoφhous polypropylene is preferably branched or coupled. The invention also includes processes for preparing compositions of the invention, including a multistage process comprising out in two or more stages, in each of which polymerization occurs and which stages differ from one another in that at least one polymerization results in the crystalline polypropylene component, and at least one stage or polymerization results in the amoφhous polypropylene component of the composition. Additionally the invention includes articles, sheets, films, foams and fibers comprising or prepared from compositions of the invention as well as processes for making the things, preferably processes involving stretching a composition of the invention. The processes include a process comprising blow molding, extruding, extrusion blow molding, injection blow molding or thermoforming a composition of the invention; as well as a process comprising reacting a composition of the invention with a coupling agent. A film of the invention preferably exhibits at least one of reduced 5 crystallization rate of the blend, reduced stress during stretching, fewer breaks of the film during the stretching process, higher crystallinity in the final film as compared with a film formed from the crystalline polypropylene blended with the same amount of an amoφhous polypropylene which was prepared using Ziegler- Natta catalysis. An amoφhous polypropylene prepared using Ziegler Natta o catalysis would be expected to have a typical molecular weight of 30000 g/mole and residual crystallinity of typically 10-15 percent of the theoretical maximum crystallization as determined by DSC (actual heat of fusion 165 J/g) and greater tear strength or lower final stress in the film as compared with a film formed from the crystalline polypropylene blended with the same amount of an amoφhous 5 polypropylene which was prepared using Ziegler-Natta catalysis and has a molecular weight of 30000 g/mole and has residual crystallinity, of 10-15 percent. In film forming processes, the presence of amoφhous polypropylene with a narrow molecular weight distribution influences the crystallization process, and reduces the crystallization rate of the crystalline polypropylene. This results in o lower stresses necessary for the stretching operation, leading to a more stable process without breakage or rupturing of the film or sheet, and lower shrinkage of the final product. Also higher orientation levels can be achieved. The mechanical and optical properties of the film or sheet are maintained through the presence of amoφhous polypropylene that is advantageously of high molecular weight (Mw 5 greater than 50,000, preferably 100,000 g/mole), which amoφhous polypropylene also advantageously influences the crystallization process with the result that the final crystallinity of the blend is higher as compared to a blend of crystalline polypropylene and Ziegler-Natta catalyst based amoφhous polypropylene. However, if the molecular weight of the polypropylene is too high (higher than the molecular weight of the crystalline polypropylene), diffusion rates of the amoφhous polypropylene would limit the film or sheet forming process. This invention differs from prior art blends in having mechanical strength from the use of amoφhous polypropylene of molecular weight greater than 50,000, preferably 100,000 g/mole, advantageously having better mechanical properties including tear strength due to the narrower molecular weight distribution as well as the higher final crystallinity. benefit of reduction in crystallization rate of the crystalline PP believed to be from the use of lower molecular weight amoφhous polypropylene than isotactic polypropylene.. Blends of the invention comprise at least one crystalline polypropylene. A crystalline polypropylene is a polymer with at least 90 mole percent of its repeating units derived from propylene, preferably at least 97 percent, more preferably at least 99 percent. The term "crystalline" is used herein to mean isotactic polypropylene having at least 93 percent isotactic triads as measured by 13 C NMR, preferably at least 95 percent, more preferably at least 96 percent. The crystalline polypropylene comprises either homopolypropylene or propylene polymerized with one or more other monomers addition polymerizable with propylene. The other monomers are preferably olefins, more preferably alpha olefins, most preferably ethylene or an olefin having a structure RCH=CH 2 where R is aliphatic or aromatic and has at least two and preferably less than 18 carbon atoms. Hydrocarbon olefin monomers within the skill in the art, include hydrocarbons having one or more double bonds at least one of which is polymerizable with the alpha olefin monomer. Alpha olefins having more than 3 carbon atoms include 1-butene, 1-pentene, 1- hexene, 1-octene, 1-noneane, 1-decene, 1-unidecene, 1-dodecene as well as 4-methyl-l- pentene, 4-methyl-l -hexeane, 5-methyl-l-hexeane, vinylcyclohexane, styrene and mixtures thereof. The preferred alpha olefins include ethylene, butene-1, hexene- 1, and octene-1. Optionally, but not in the most preferred embodiment, the polymers have monomers having at least two double bonds which are preferably dienes or trienes. Suitable diene and triene comonomers include 7-methyl-l,6-octadiene, 3,7-dimethyl- 1 ,6-octadiene, 5,7-dimethyl-l,6-octadiene, 3,7,ll-trimethyl-l,6,10-octatriene, 6- methyl-l,5-heptadiene, 1,3 -butadiene, 1 ,6-heptadiene, 1 ,7-octadiene, 1,8-nonadiene, 1 ,9-decadiene, 1,10-undecadiene, norbornene, tetracyclododecene, or mixtures thereof, preferably butadiene, hexadienes, and octadienes, most preferably 1 ,4-hexadiene, 1,9- decadiene, 4-methyl-l, 4-hexadiene, 5-methyl-l,4-hexadiene, dicyclopentadiene, and 5- ethylidene-2 -norbornene. Crystalline polypropylenes are formed by means within the skill in the art, for example using single site catalysts or Ziegler Natta catalysts. The propylene and optionally alpha olefin monomers are polymerized under conditions within the skill in the art, for instance as disclosed by Galli, et al., Angew. Macromol. Chem.. Vol. 120, p. 73 (1984), or by E. P. Moore, et al. in Polypropylene Handbook, Hanser Publishers, New York, 1996, particularly pages 11-98. The crystalline polypropylene starting materials are suitably of any molecular weight distribution (MWD). Polymers of broad or narrow MWD are formed by means within the skill in the art. For fiber applications generally a narrower MWD is preferred (for example less than 3), for BOPP (biaxially oriented polypropylene) applications a broader MWD is preferred (for example greater than 5). When a narrow MWD is preferred, it is advantageously obtained using single site catalysis. The crystalline polypropylene has a weight average molecular weight as measured by gel permeation chromatography (GPC) greater than 100,000, preferably greater than 115,000, more preferably greater than 150,000, most preferably greater than 250,000 to obtain desirably high mechanical strength in the final product, for example sufficient mechanical strength to avoid breaking in film forming or thermoforming. The other component in blends of the invention is an amoφhous polypropylene which, like the crystalline polypropylene, is a propylene homopolymer or copolymer, optionally containing up to 10 mole percent other comonomer copolymerizable with propylene. The amoφhous polypropylene is advantageously at least 90 mole percent propylene, preferably at least 95 percent, more preferably at least 99 percent. Suitable and preferred comonomers are the same as described for the crystalline polypropylene. The term amoφhous refers to the absence of crystallinity in the polymer; for polypropylene homopolymer this means that the polymer is atactic, without sufficient isotactic segments to give rise to crystallinity, as can be determined by the absence of a melting point and a heat of fusion of 0 J/g in DSC. Atactic polymers are defined as having no consistent patterns among chiral sequences [Mark H., Bikales N., Encyclopedia of Polymer Science and Engineering, Volume 9, John Wiley & Sons Inc, 1987, page 800] as can be determined by 13C NMR [Karger-Kocsis J., Polypropylene, Structure blends and composites, 1. Structure and Moφhology, Chapman & Hall, 1995, pagesl5-19]. The amoφhous polypropylene has a weight average molecular weight (Mw) greater than 50,000, advantageously greater than 100,000, more preferably greater than 130,000, most preferably greater than 150,000 g/mole to obtain sufficient mechanical strength in the final blend to be suitable for film formation, and/or thermoforming processes. Suitability is indicated by fewer breaks per unit of film, or article than would occur with a blend of the same crystalline polymer and an amoφhous polypropylene which was prepared using Ziegler-Natta catalysis and has a molecular weight of 30000 g/mole and has residual crystallinity of 10-15 percent of theoretical as discussed hereinbefore. Further, the amoφhous polypropylene has a weight average molecular weight (Mw) less than that of the crystalline polypropylene to achieve sufficient diffusion rate of the amoφhous phase to result in crystallization of the blend advantageously with lower stress during stretch than a blend with the same crystalline polypropylene and an amoφhous polypropylene having a molecular weight greater than that of the crystalline polymer. The amoφhous polypropylene preferably has a weight average molecular weight of at least 10 percent, more preferably at least 15 percent, most preferably at least 20 percent lower than that of the crystalline polypropylene. In many instances, the Mw of the amoφhous polypropylene is preferably at least 50,000, more preferably at least 100,000, most preferably at least 150,000 g/mole less than that of the crystalline polypropylene. The amoφhous polypropylene starting materials preferably have a narrow molecular weight distribution (MWD), that is a MWD of less than 5, preferably less than 3, more preferably less than 2. When the molecular weight distribution is greater than 3 it is preferably bimodal such as is obtainable by blending two such high molecular weight amoφhous polymers. The MWD is measured by GPC analysis (Mw/Mn). The preferred narrow MWD is advantageously obtained using single site catalysis. Preparing such narrow molecular weight amoφhous polypropylene is within the skill in the art such as is described for instance as disclosed by Galli, et al., Angew. Macromol. Chem. , Vol. 120, p. 73 (1984), or by E. P. Moore, et al. in Polypropylene Handbook. Hanser Publishers, New York, 1996, particularly pages 11-98. The term single site catalysts is recognized in the art as referring to catalysts which have less diversity in the individual polymer chains produced than is observed in polymers made using Ziegler Natta catalysts. This diversity is evidenced in broader MWD. Single site catalysts include single site metallocene or single site constrained geometry catalyst; these are exemplified by U.S. Patents 4,937,299 (Ewen et al.), 5,218,071 (Tsutsui et al), 5,278,272, 5,324,800, 5,084,534, 5,405,922, 4,588,794, 5,204,419. To maintain desirable mechanical properties such as tensile modulus of the blend, the amoφhous polypropylene preferably has a glass transition temperature (Tg) greater than -10°C. Again, desired mechanical properties are those compared with a blend of the same crystalline polypropylene and an amoφhous polypropylene of Tg less than -10°C and preferably include resistance to break during thermal forming and/or tensile modulus. All references herein to elements or metals belonging to a certain Group refer to the Periodic Table of the Elements published and copyrighted by CRC Press, Inc., 1989. Also any reference to the Group or Groups shall be to the Group or Groups as reflected in this Periodic Table of the Elements using the IUPAC system for numbering groups. Preparation of crystalline and amoφhous polypropylene polymers is well within the skill in the art. Advantageous catalysts for use in preparing narrow molecular weight distribution polymers useful in the practice of the invention, especially for the amoφhous polypropylene, are preferably derivatives of any transition metal including Lanthanides, but preferably of Group 3, 4, or Lanthanide metals which are in the +2, +3, or +4 formal oxidation state. Preferred compounds include metal complexes containing from 1 to 3 π-bonded anionic or neutral ligand groups, which are optionally cyclic or non-cyclic delocalized π-bonded anionic ligand groups. Exemplary of such π-bonded anionic ligand groups are conjugated or nonconjugated, cyclic or non-cyclic dienyl groups, and allyl groups. By the term "π-bonded" is meant that the ligand group is bonded to the transition metal by means of its delocalized π-electrons. Each atom in the delocalized π-bonded group is optionally independently substituted with a radical selected from the group consisting of hydrogen, halogen, hydrocarbyl, halohydrocarbyl, hydrocarbyl-substituted metalloid radicals wherein the metalloid is selected from Group 14 of the Periodic Table of the Elements, and such hydrocarbyl- or hydrocarbyl-substituted metalloid radicals further substituted with a Group 15 or 16 hetero atom containing moiety. Included within the term "hydrocarbyl" are Cι_20 straight, branched and cyclic alkyl radicals, C6_20 aromatic radicals, C7.20 alkyl-substituted aromatic radicals, and C7..20 aryl- substituted alkyl radicals. In addition two or more such adjacent radicals may together form a fused ring system, a hydrogenated fused ring system, or a metallocycle with the metal. Suitable hydrocarbyl-substituted organometalloid radicals include mono-, di- and tri-substituted organometalloid radicals of Group 14 elements wherein each of the hydrocarbyl groups contains from 1 to 20 carbon atoms. Examples of advantageous hydrocarbyl-substituted organometalloid radicals include trimethylsilyl, triethylsilyl, ethyldimethylsilyl, methyldiethylsilyl, triphenylgermyl, and trimethylgermyl groups. Examples of Group 15 or 16 hetero atom containing moieties include amine, phosphine, ether or thioether moieties or monovalent derivatives thereof, for example amide, phosphide, ether or thioether groups bonded to the transition metal or Lanthanide metal, and bonded to the hydrocarbyl group or to the hydrocarbyl- substituted metalloid containing group. Examples of advantageous anionic, delocalized π-bonded groups include cyclopentadienyl, indenyl, fluorenyl, tetrahydroindenyl, tetrahydrofluorenyl, octahydrofluorenyl, pentadienyl, cyclohexadienyl, dihydroanthracenyl, hexahydroanthracenyl, and decahydroanthracenyl groups, as well as Ci-io hydrocarbyl-substituted or C 1.10 hydrocarbyl-substituted silyl substituted derivatives thereof. Preferred anionic delocalized π-bonded groups are cyclopentadienyl, pentamethylcyclopentadienyl, tetramethylcyclopentadienyl, tetramethylsilylcyclopentadienyl, indenyl, 2,3-dimethylindenyl, fluorenyl, 2- methylindenyl, 2-methyl-4-phenylindenyl, tetrahydrofluorenyl, octahydrofluorenyl, and tetrahydroindenyl. A preferred class of catalysts are transition metal complexes corresponding to the Formula A: LμMX m X' n X"p, or a dimer thereof wherein: L is an anionic, delocalized, π-bonded group that is bound to M, containing up to 50 non-hydrogen atoms, optionally two L groups may be joined together forming a bridged structure, and further optionally one L is bound to X; M is a metal of Group 4 of the Periodic Table of the Elements in the +2, +3 or +4 formal oxidation state; X is an optional, divalent substituent of up to 50 non-hydrogen atoms that together with L forms a metallocycle with M; X' at each occurrence is an optional neutral Lewis base having up to 20 non-hydrogen atoms and optionally one X' and one L may be joined together; X" each occurrence is a monovalent, anionic moiety having up to 40 non- hydrogen atoms, optionally, two X" groups are covalently bound together forming a divalent dianionic moiety having both valences bound to M, or, optionally 2 X" groups are covalently bound together to form a neutral, conjugated or nonconjugated diene that is π-bonded to M (whereupon M is in the +2 oxidation state), or further optionally one or more X" and one or more X' groups are bonded together thereby forming a moiety that is both covalently bound to M and coordinated thereto by means of Lewis base functionality; / is 0, 1 or 2; m is 0 or 1 ; n is a number from 0 to 3 ; p is an integer from 0 to 3; and the sum, / + m + p, is equal to the formal oxidation state of M, except when 2 X" groups together form a neutral conjugated or non-conjugated diene that is π- bonded to M, in which case the sum / +m is equal to the formal oxidation state of M. Preferred complexes include those containing either one or two L groups. The latter complexes include those containing a bridging group linking the two L groups. Preferred bridging groups are those corresponding to the formula (ER*2) X wherein E is silicon, germanium, tin, or carbon, R* independently each occurrence is hydrogen or a group selected from silyl, hydrocarbyl, hydrocarbyloxy and combinations thereof, said R* having up to 30 carbon or silicon atoms, and x is 1 to 8. Preferably, R* independently each occurrence is methyl, ethyl, propyl, benzyl, tert-butyl, phenyl, methoxy, ethoxy or phenoxy. Examples of the complexes containing two L groups are compounds corresponding to the formula: wherein: M is titanium, zirconium or hafnium, preferably zirconium or hafnium, in the +2 or +4 formal oxidation state; R in each occurrence independently is selected from the group consisting of hydrogen, hydrocarbyl, silyl, germyl, cyano, halo and combinations thereof, said R 3 having up to 20 non-hydrogen atoms, or adjacent R 3 groups together form a divalent derivative (for example, a hydrocarbadiyl, germadiyl group) thereby forming a fused ring system, and X" independently each occurrence is an anionic ligand group of up to 40 non-hydrogen atoms, or two X" groups together form a divalent anionic ligand group of up to 40 non-hydrogen atoms or together are a conjugated diene having from 4 to 30 non-hydrogen atoms forming a-complex with M, whereupon M is in the +2 formal oxidation state, and R*, E and x are as previously defined. The foregoing metal complexes are especially suited for the preparation of polymers having stereoregular molecular structure. In such capacity it is preferred that the complex possesses C s symmetry or possesses a chiral, stereorigid structure. Examples of the first type are compounds possessing different delocalized π-bonded systems, such as one cyclopentadienyl group and one fluorenyl group. Similar systems based on Ti(IV) or Zr(IV) were disclosed for preparation of syndiotactic olefin polymers in Ewen, et al., J. Am. Chem. Soc. 110, 6255-6256 (1980). Examples of chiral structures include rac bis-indenyl complexes. Similar systems based on Ti(IV) or Zr(IV) were disclosed for preparation of isotactic olefin polymers in Wild et al, J. Organomet. Chem.. 232, 233-47, (1982). To form the amoφhous polypropylenes useful in the practice of the present invention it is preferred that the metal complex polymerizes the mentioned olefins regioselectively, but without stereoselectivity, thus producing an atactic (co)polymer. In such capacity it is preferred that the complex is obtained from metallocenes possessing C2v molecular symmetry and from achiral, meso isomers of ansa metallocenes; the catalyst complex is regiospecific and a stereospecific. Such catalysts are advantageously exemplified by catalysts having a structure corresponding to the preceding Formula A wherein there is one π-bonded group (1 is 1 (one)) or corresponding to Formula AIII following. Exemplary bridged ligands containing two π-bonded groups are: (dimethylsilyl- bis(cyclopentadienyl)), (dimethylsilyl-bis(methylcyclopentadienyl)), (dimethylsilyl-bis(ethylcyclopentadienyl)), (dimethylsilyl-bis(t- butylcyclopentadienyl)), (dimethylsilyl-bis(tetramethylcyclopentadienyl)), (dimethylsilyl-bis(indenyl)), (dimethylsilyl-bis(tetrahydroindenyl)), (dimethylsilyl- bis(fluorenyl)), (dimethylsilyl-bis(tetrahydrofluorenyl)), (dimethylsilyl-bis(2- methyl-4-phenylindenyl)), (dimethylsilyl-bis(2-methylindenyl)), (dimethylsilyl- cyclopentadienyl-fluorenyl), (dimethylsilyl-cyclopentadienyl-octahydrofluorenyl), (dimethylsilyl-cyclopentadienyl-tetrahydrofluorenyl), (1, 1, 2, 2-tetramethyl-l, 2- disilyl-bis-cyclopentadienyl), (1, 2-bis(cyclopentadienyl)ethane, and (isopropylidene-cyclopentadienyl-fluorenyl). Preferred X" groups are selected from hydride, hydrocarbyl, silyl, germyl, halohydrocarbyl, halosilyl, silylhydrocarbyl and aminohydrocarbyl groups, or two X" groups together form a divalent derivative of a conjugated diene or else together they form a neutral, π-bonded, conjugated diene. Most preferred X" groups are Cj_20 hydrocarbyl groups, including those optionally formed from two X" groups together. A further class of metal complexes corresponds to the preceding formula LιMX m X' n X"p, or a dimer thereof, wherein X is a divalent substituent of up to 50 non-hydrogen atoms that together with L forms a metallocycle with M. Preferred divalent X substituents include groups containing up to 30 non-hydrogen atoms comprising at least one atom that is oxygen, sulfur, boron or a member of Group 14 of the Periodic Table of the Elements directly attached to the delocalized π-bonded group, and a different atom, selected from the group consisting of nitrogen, phosphorus, oxygen or sulfur that is covalently bonded to M. A preferred class of such Group 4 metal coordination complexes corresponds to the formula: wherein: M is titanium, zirconium or hafnium in the +2, +3 or +4 formal oxidation state; X" and R are as previously defined for formulas Al and All; Y is -O-, -S-, -NRS -NR* 2 -, or -PR*-; and Z is SiR*2, CR*2, SiR*2SiR*2, CR*2CR*2, CR*=CR*, CR*2SiR*2, or GeR*2, wherein R* is as previously defined. Illustrative Group 4 metal complexes that are optionally used as catalysts include: cyclopentadienyltitaniumtrimethyl, cyclopentadienyltitaniumtriethyl, cyclopentadienyltitaniumtriisopropyl, cyclopentadienyltitaniumtriphenyl, cyclopentadienyltitaniumtribenzyl, cyclopentadienyltitanium-2,4- dimethylpentadienyl, cyclopentadienyltitanium-2,4- dimethylpentadienyltriethylphosphine, cyclopentadienyltitanium-2,4- dimethylpentadienyltrimethylphosphine, cyclopentadienyltitaniumdimethylmethoxide, cyclopentadienyltitaniumdimethylchloride, pentamethylcyclopentadienyltitaniumtrimethyl, indenyltitaniumtrimethyl, indenyltitaniumtriethyl, indenyltitaniumtripropyl, indenyltitaniumtriphenyl, tetrahydroindenyltitaniumtribenzyl, pentamethylcyclopentadienyltitaniumtriisopropyl, pentamethylcyclopentadienyltitaniumtribenzyl, pentamethylcyclopentadienyltitaniumdimethylmethoxide, pentamethylcyclopentadienyltitaniumdimethylchloride, bis(η5-2,4-dimethylpentadienyl)titanium, bis(η5-2,4-dimethylpentadienyl)titaniumtrimethylphosphine, bis(η5-2,4-dimethylpentadienyl)titaniumtriethylphosphine, octahydrofluorenyltitaniumtrimethyl, tetrahydroindenyltitaniumtrimethyl, tetrahydrofluorenyltitaniumtrimethyl, (tert-butylamido)( 1 , 1 -dimethyl-2,3 ,4,9,10— l,4,η5,6,7,8-hexahydronaphthalenyl)dimethylsilanetitaniumdimethyl, (tert-butylamido)(l,l,2,3-tetramethyl-2,3,4,9,10-l,4,5,6,7,8- hexahydronaphthalenyl)dimethylsilanetitaniumdimethyl, (tert- butylamido)(tetramethyl-η 5 -cyclopentadienyl) dimethylsilanetitanium dibenzyl, (tert-butylamido)(tetramethyl-η5-cyclopentadienyl)dimethylsilanetitanium dimethyl, (tert-butylamido)(tetramethyl-η5-cyclopentadienyl)-l,2- ethanediyltitanium dimethyl, (tert-butylamido)(tetramethyl-η5- indenyl)dimethylsilanetitanium dimethyl, (tert-butylamido)(tetramethyl-η 5- cyclopentadienyl)dimethylsilane titanium (III) 2-(dimethylamino)benzyl; (tert-butylamido)(tetramethyl-η5-cyclopentadienyl)dimethylsilanetitanium (III) allyl, (tert-butylamido)(tetramethyl-η5-cyclopentadienyl)dimethylsilanetitanium (III) 2,4-dimethylpentadienyl, (tert-butylamido)(tetramethyl-η5- cyclopentadienyl)dimethyl-silanetitanium (II) 1 ,4-diphenyl- 1 ,3 -butadiene, (tert-butylamido)(tetramethyl-η5-cyclopentadienyl)dimethyl-silanetitanium (II) 1,3-pentadiene, (tert-butylamido)(2-methylindenyl)dimethylsilanetitanium (II) 1,4- diphenyl- 1,3 -butadiene, (tert-butylamido)(2-methylindenyl)dimethylsilanetitanium (II) 2,4-hexadiene, (tert-butylamido)(2-methylindenyl)dimethylsilanetitanium (IV) 2,3-dimethyl-l,3-butadiene, (tert-butylamido)(2-methylindenyl)dimethylsilanetitanium (IV)isoprene, (tert-butylamido)(2-methylindenyl)dimethylsilanetitanium 1,3-butadiene, (tert-butylamido)(2,3-dimethylindenyl)dimethylsilanetitanium (IV) 2,3-dimethyl- 1 ,3 -butadiene, (tert-butylamido)(2,3-dimethylindenyl)dimethylsilanetitanium (IV) isoprene; (tert-butylamido)(2,3-dimethylindenyl)dimethylsilanetitanium (IV) dimethyl; (tert-butylamido)(2,3-dimethylindenyl)dimethylsilanetitanium (IV) dibenzyl; (tert-butylamido)(2,3-dimethylindenyl)dimethylsilanetitanium 1 ,3- butadiene,(tert-butylamido)(2,3-dimethylindenyl)dimethylsilanetitanium (II) 1,3- pentadiene, (tert-butylamido)(2,3-dimethylindenyl)dimethylsilanetitanium (II) 1,4- diphenyl- 1 ,3 -butadiene, (tert-butylamido)(2-methylindenyl)dimethylsilanetitanium (II) 1 ,3-pentadiene,(tert-butylamido)(2-methylindenyl)dimethylsilanetitanium (IV) dimethyl, (tert-butylamido)(2-methylindenyl)dimethylsilanetitanium (IV) dibenzyl, (tert-butylamido)(2-methyl-4-phenylindenyl)dimethylsilanetitanium (II) 1 ,4- diphenyl- 1 ,3 -butadiene, (tert-butylamido)(2-methyl-4-phenylindenyl)dimethylsilanetitanium (II) 1 ,3- pentadiene, (tert-butylamido)(2-methyl-4-phenylindenyl)dimethylsilanetitanium (II) 2,4-hexadiene, (tert-butylamido)(tetramethyl-η5-cyclopentadienyl)dimethyl- silanetitanium 1,3 -butadiene, (tert-butylamido)(tetramethyl-η5- cyclopentadienyl)dimethyl-silanetitanium (IV) 2,3-dimethyl-l,3-butadiene, (tert- butylamido)(tetramethyl-η5-cyclopentadienyl)dimethyl-silanetitanium (IV) isoprene, (tert-butylamido)(tetramethyl-η 5 -cyclopentadienyl)dimethyl- silanetitanium (II) 1 ,4-dibenzyl- 1,3 -butadiene, (tert-butylamido)(tetramethyl-η5- cyclopentadienyl)dimethyl-silanetitanium (II) 2,4-hexadiene, (tert- butylamido)(tetramethyl-η5-cyclopentadienyl)dimethyl-silanetitanium (II) 3- methyl- 1 ,3 -pentadiene, (tert-butylamido)(2,4-dimethylpentadien-3 -yl)dimethyl- silanetitaniumdimethyl, (tert-butylamido)(6,6-dimethylcyclohexadienyl)dimethyl- silanetitaniumdimethyl, (tert-butylamido)(l,l-dimethyl-2,3, 4,9, 10,1, 4,5,6,7,8- hexahydronaphthalen-4-yl)dimethylsilanetitaniumdimethyl, (tert- butylamido)(l,l,2,3-tetramethyl-2,3,4,9,10,l,4,5,6,7,8-hexahydronaphthalen-4- yl)dimethylsilanetitaniumdimethyl(tert-butylamido)(tetramethyl-η5- cyclopentadienyl methylphenyl-silanetitanium (IV) dimethyl, (tert-butylamido)(tetramethyl-η 5 -cyclopentadienyl methylphenyl-silanetitanium (II) 1,4-diphenyl- 1,3 -butadiene, l-(tert-butylamido)-2-(tetramethyl-η5- cyclopentadienyl)ethanediyl-titanium (IV) dimethyl, and l-(tert-butylamido)-2- (tetramethyl-η5-cyclopentadienyl)ethanediyl-titanium (II) 1 ,4-diphenyl-l ,3- butadiene. Complexes containing two L groups including bridged complexes include: bis(cyclopentadienyl)zirconiumdimethyl, bis(cyclopentadienyl)zirconium dibenzyl, bis(cyclopentadienyl)zirconium methyl benzyl, bis(cyclopentadienyl)zirconium methyl phenyl, bis(cyclopentadienyl)zirconiumdiphenyl, bis(cyclopentadienyl)titanium-allyl, 5 bis(cyclopentadienyl)zirconiummethylmethoxide, bis(cyclopentadienyl)zirconiummethylchloride, bis(pentamethylcyclopentadienyl)zirconiumdimethyl, bis(pentamethylcyclopentadienyl)titaniumdimethyl, bis(indenyl)zirconiumdimethyl, o bis(indenyl)zirconiummethyl(2-(dimethylamino)benzyl), bis(indenyl)zirconium methyltrimethylsilyl, bis(tetrahydroindenyl)zirconium methyltrimethylsilyl, bis(pentamethylcyclopentadienyl)zirconiummethylbenzyl, bis(pentamethylcyclopentadienyl)zirconiumdibenzyl, 5 bis(pentamethylcyclopentadienyl)zirconiummethylmethoxide, bis(pentamethylcyclopentadienyl)zirconiummethylchloride, bis(methylethylcyclopentadienyl)zirconiumdimethyl, bis(butylcyclopentadienyl)zirconium dibenzyl, bis(t- butylcyclopentadienyl)zirconiumdimethyl, o bis(ethyltetramethylcyclopentadienyl)zirconiumdimethyl, bis(methylpropylcyclopentadienyl)zirconium dibenzyl, bis(trimethylsilylcyclopentadienyl)zirconium dibenzyl, dimethylsilyl-bis(cyclopentadienyl)zirconiumdimethyl, dimethylsilyl-bis(tetramethylcyclopentadienyl)titanium-(III) allyl dimethylsilyl- 5 bis(t-butylcyclopentadienyl)zirconiumdichloride, dimethylsilyl-bis(n- butylcyclopentadienyl)zirconiumdichloride, (methylene-bis(tetramethylcyclopentadienyl)titanium(III) 2- (dimethylamino)benzyl, (methylene-bis(n-butylcyclopentadienyl)titanium(III) 2- (dimethylamino)benzyl, dimethylsilyl-bis(indenyl)zirconiumbenzylchloride, o dimethylsilyl-bis(2-methylindenyl)zirconiumdimethyl, dimethylsilyl-bis(2-methyl-4-phenylindenyl)zirconiumdimethyl, dimethylsilyl-bis(2-methylindenyl)zirconium- 1 ,4-diphenyl- 1 ,3-butadiene, dimethylsilyl-bis(2-methyl-4-phenylindenyl)zirconium (II) 1 ,4-diphenyl- 1,3- butadiene, dimethylsilyl-bis(tetrahydroindenyl)zirconium(II) 1 ,4-diphenyl- 1,3- butadiene, dimethylsilyl-bis(fluorenyl)zirconiummethylchloride, dimethylsilyl-bis(tetrahydrofluorenyl)zirconium bis(trimethylsilyl), and dimethylsilyl(tetramethylcyclopentadienyl)(fluorenyl)zirconium dimethyl. Other catalysts, especially catalysts containing other Group 4 metals, will, of course, be apparent to those skilled in the art. Preferred metallocene species include constrained geometry metal complexes, including titanium complexes, and methods for their preparation as are disclosed in U.S. Application Serial No. 545,403, filed July 3, 1990 (EP-A- 416,815); U.S. Application Serial No. 967,365, filed October 28, 1992 (EP-A- 514,828); and U.S. Application Serial No. 876,268, filed May 1, 1992, (EP-A- 520,732), as well as US-A- 5,055,438, US-A- 5,057,475, US-A- 5,096,867, US-A- 5,064,802, US-A-5,096,867, US-A-5,132,380, US-A-5,132,380, US- A-5, 470,993, US-A-5,486,632 and US-A-5,132,380, US-A-5,321,106. Metallocene catalysts are advantageously rendered catalytically active by combination with one or more activating cocatalysts, by use of an activating technique, or a combination thereof. Advantageous cocatalysts are those boron- containing cocatalysts within the skill in the art. Among the boron-containing cocatalysts are tri(hydrocarbyl)boron compounds and halogenated derivatives thereof, advantageously having from 1 to 10 carbons in each hydrocarbyl or halogenated hydrocarbyl group, more especially perfluorinated tri(aryl)boron compounds, and most especially tris(pentafluorophenyl)borane); amine, phosphine, aliphatic alcohol and mercaptan adducts of halogenated tri(C j 10 hydrocarbyl)boron compounds, especially such adducts of perfluorinated tri(aryl)boron compounds. Alternatively, the cocatalyst includes borates such as tetrapheny Borate having as counterions ammonium ions such as are within the skill in the art as illustrated by European Patent EP 672,688 (Canich, Exxon), published September 20, 1995. The cocatalyst can be used in combination with a tri(hydrocarbyl)aluminum compound having from 1 to 10 carbons in each hydrocarbyl group or an oligomeric or polymeric alumoxane. It is possible to employ these aluminum compounds for their beneficial ability to scavenge impurities such as oxygen, water, and aldehydes from the polymerization mixture. Preferred aluminum compounds include trialkyl aluminum compounds having from 2 to 6 carbons in each alkyl group, especially those wherein the alkyl groups are ethyl, propyl, isopropyl, n-butyl, isobutyl, pentyl, neopentyl, or isopentyl, and methylalumoxane, modified by methylalumoxane (that is methylalumoxane modified by reaction with triisobutyl aluminum) (MMAO) and diisobutylalumoxane. The molar ratio of aluminum compound to metal complex is preferably from 1:10,000 to 1000:1, more preferably from 1 :5000 to 100:1, most preferably from 1:100 to 100:1. Cocatalysts are used in amounts and under conditions within the skill in the art. Their use is applicable to all processes within the skill in the art, including solution, slurry, bulk (especially propylene), and gas phase polymerization processed. Such processes include those fully disclosed in the references cited previously. The molar ratio of catalyst/cocatalyst or activator employed preferably ranges from 1 :10,000 to 100:1, more preferably from 1:5000 to 10:1, most preferably from 1 : 1000 to 1 : 1. When utilizing such strong Lewis acid cocatalysts to polymerize higher α- olefins, especially propylene, it has been found especially desirable to also contact the catalyst/cocatalyst mixture with a small quantity of ethylene or hydrogen (preferably at least one mole of ethylene or hydrogen per mole of metal complex, suitably from 1 to 100,000 moles of ethylene or hydrogen per mole of metal complex). This contacting may occur before, after or simultaneously to contacting with the higher -olefin. If the foregoing Lewis acid activated catalyst compositions are not treated in the foregoing manner, either extremely long induction periods are encountered or no polymerization at all results. The ethylene or hydrogen may be used in a suitably small quantity such that no significant affect on polymer properties is observed. In most instances, the polymerization advantageously takes place at conditions known in the prior art for Ziegler-Natta or Kaminsky-Sinn type polymerization reactions, that is, temperatures from 0-250°C and pressures from atmospheric to 3000 atmospheres. Suspension, solution, slurry, gas phase or high pressure, whether employed in batch or continuous form or under other process conditions, including the recycling of condensed monomers or solvent, may be employed if desired. Examples of such processes are well known in the art for example, WO 88/02009-A1 or U.S. Patent No. 5,084,534, disclose conditions that are advantageously employed with the polymerization catalysts. A support, especially silica, alumina, or a polymer (especially polytetrafluoroethylene or a polyolefin) is optionally employed, and desirably is employed when the catalysts are used in a gas phase polymerization process. Such supported catalysts are advantageously not affected by the presence of liquid aliphatic or aromatic hydrocarbons such as are optionally present under the use of condensation techniques in a gas phase polymerization process. Methods for the preparation of supported catalysts are disclosed in numerous references, examples of which are U.S. Patent Nos. 4,808,561, 4,912,075, 5,008,228, 4,914,253, and 5,086,025 and are suitable for the preparation of supported catalysts. In such a process the reactants and catalysts are optionally added to the solvent sequentially, in any order, or alternatively one or more of the reactants or catalyst system components are premixed with solvent or material preferably miscible therewith then mixed together or into more solvent optionally containing the other reactants or catalysts. The preferred process parameters are dependent on the monomers used and the polymer desired. Propylene is added to the reaction vessel in predetermined amounts to achieve predetermined per ratios, advantageously in gaseous form using a joint mass flow controller. Alternatively propylene or other liquid monomers are added to the reaction vessel in amounts predetermined to result in ratios desired in the final product. They are optionally added together with the solvent (if any), alpha- olefin and functional comonomer, or alternatively added separately. The pressure in the reactor is a function of the temperature of the reaction mixture and the relative amounts of propylene and/or other monomers used in the reaction. 5 Advantageously, the polymerization process is carried out at a pressure of from 10 to 1000 psi (70 to 7000 kPa), most preferably from 140 to 550 psi (980 to 3790 kPa). The polymerization is then conducted at a temperature of from 25 to 200°C, preferably from 50 to 100°C, and most preferably from 60 to 80°C. The process is advantageously continuous, in which case the reactants are o added continuously or at intervals and the catalyst and, optionally cocatalyst, are added as needed to maintain reaction and/or make up loss. Solution polymerization or bulk polymerization is preferred. In the latter case liquid polypropylene is the reaction medium. Preferred solvents include mineral oils and the various hydrocarbons which are liquid at reaction 5 temperatures. Illustrative examples of useful solvents include straight- and branched-chain hydrocarbons such as alkanes, for example isobutane, butane, pentane, isopentene, hexane, heptane, octane and nonane, as well as mixtures of alkanes including kerosene and Isopar E, available from Exxon Chemicals Inc.; cyclic and alicyclic hydrocarbons such as cyclopentane, cyclohexane, o methylcyclohexane, methylcycloheptane, and mixtures thereof; and aromatics and alkyl-substituted aromatic compounds such as benzene, toluene, xylenes, ethylbenzene, diethylbenzene, and mixtures thereof; and perfluorinated hydrocarbons such as perfluorinated C 4 -C 10 alkanes. Suitable solvents may include liquid olefins which may act as monomers or comonomers. Mixtures of the 5 foregoing are also suitable. At all times, the individual ingredients as well as the recovered catalyst components are protected from oxygen and moisture. Therefore, the catalyst components and catalysts are prepared and recovered in an oxygen- and moisture- free atmosphere. Preferably, therefore, the reactions are performed in the presence 0 of a dry, inert gas such as, for example, nitrogen. Without limiting in any way the scope of the invention, one means for carrying out such a polymerization process is as follows. In a stirred-tank reactor, olefin monomer is introduced continuously together with solvent and polyene monomer. The reactor contains a liquid phase composed substantially of monomers together with any solvent or additional diluent. Catalyst and cocatalyst are continuously introduced in the reactor liquid phase. The reactor temperature and pressure may be controlled by adjusting the solvent/monomer ratio, the catalyst addition rate, as well as by cooling or heating coils, jackets or both. The polymerization rate is controlled by the rate of catalyst addition. The polymer product molecular weight is controlled, optionally, by controlling other polymerization variables such as the temperature, monomer concentration, or by a stream of hydrogen introduced to the reactor, as is well known in the art. The reactor effluent is contacted with a catalyst kill agent such as water or an alcohol. The polymer solution is optionally heated, and the polymer product is recovered by flashing off gaseous monomers as well as residual solvent or diluent at reduced pressure, and, if necessary, conducting further devolatilization in equipment such as a devolatilizing extruder. In a continuous process, the mean residence time of the catalyst and polymer in the reactor generally is from 5 minutes to 8 hours, and preferably from 10 minutes to 6 hours. Preferably, the polymerization is conducted in a continuous solution polymerization system, optionally comprising more than one reactor connected in series or parallel. The invention also includes a process of crystalline polypropylene polymerization in combination with or in sequence with amoφhous polypropylene polymerization; using processes, within the skill in the art for producing amoφhous, and syndiotactic or isotactic polymers, particularly to produce blends (preferably in-reactor blends) of the invention. Such use is within the skill in the art, for instance as illustrated by Canich in WO96/23838, Govoni et al in WO 96/02583, JP 8100016, EP 0436328 (Mitsui), EP 642536, Collina et al. in WO 96/11218, Welborne et al in EP 260130 and WO 87/02991 and Ueda et al. in EP 704462 and EP 704463, Buchelli et al. in WO 93/24533, Baker et al. in EP 704464, Sacchetti in WO 95/26369 Galli et al. in The Future Role of Ziegler-Natta Catalysts, Flexipole 96 conference paper, Houston, Texas, June 26-28, 1996 and U.S. Patents 5541260 (Ciarrocchi et al), 5532325 (Chiba Hiromasa, et al.), 5543478 (Hideto et al), 4701432 (Welborn), and 5548042 (Goode). The processes of the invention thus include multistage processes, which means that polymerization is carried out in two or more stages, in each of which polymerization occurs and which stages differ from one another in that at least one polymerization results in the crystalline polypropylene component, and at least one stage or polymerization results in the amoφhous polypropylene component of the blends of the invention. A multistage reactor configuration optionally uses the same reactor for each stage; a part of a reactor for each stage; or one reactor per stage. In this specification, each stage is optionally referred to as a "reaction zone." Advantageously, two stages or reaction zones are used in the process. The stages or reaction zones are preferably connected in series. The cited references show that multistage processes are well within the skill in the art in the production of polyolefins. While the stages are preferably carried out in two or more (hereinafter multiple) reactors, they optionally occur in one reactor wherein one or more catalysts, reaction conditions, or reactants are changed or used in sequence. For instance, a first catalyst is used until inactive, for example by being consumed, separated from reactants by polymer, or inactivated by addition of another material. Then a second catalyst is used. Alternatively, after a first catalyst is active in a polymerization, both the first and at least one subsequent catalyst are active simultaneously; for instance, at least one subsequent catalyst is added to a reaction mixture containing the first catalyst. It is within the skill in the art to stop and restart a polymerization by substantially stopping the reaction with or without the use of a deactivator, lower temperature, or deactivating a cocatalyst; preferably retaining the polymer particles in the reaction vessel without discharging them; and resuming the reaction for example by feeding an organoaluminum compound as cocatalyst to restart the polymerization, raising temperature to a temperature sufficient for polymerization, or addition of additional catalyst or monomer. Multistage processes are particularly useful because of the possibility of independently varying, in any reactor or stage, process parameters to provide 5 greater flexibility in controlling the composition and properties of the resulting polymer composition as compared with that obtained from a single-stage process. "Reactor blend", as that term is used herein, means a highly dispersed blend of two or more components produced as a result of the formation of one polymer in the presence of another, an in situ blend produced by polymerizing one or more l o monomers in the presence of another polymer. The resulting reactor product is a highly dispersed blend of the various polymers. Optionally the amoφhous polypropylene is branched or coupled advantageously to provide higher melt strength in the film or sheet forming process. Optionally, additionally or alternatively the crystalline polypropylene is 15 branched or coupled. Branched crystalline polypropylene is commercially available for instance from Montell North America under the trade designations Profax PF-611 and PF-814. Alternatively, the branched or coupled forms of either of the polypropylenes are prepared by means within the skill in the art such as by peroxide or e-beam treatment, 20 for instance as disclosed by DeNicola et al. in U.S. Patent 5,414,027 (the use of high energy (ionizing) radiation in a reduced oxygen atmosphere); EPO 190889 to Himont (electron beam irradiation of isotactic polypropylene at lower temperatures); US 5,464,907 to Akzo Nobel NV, EP 754711 to Solvay (peroxide treatment). In another embodiment, either or both of the polypropylenes are coupled. The 25 term "coupled" is used herein to refer to polymers which are rheology-modified such that they exhibit change in the resistance of the molten polymer to flow. The resistance of polymer melts to flow is indicated by (1) the tensile stress growth coefficient and (2) the dynamic shear viscosity coefficient. The tensile stress growth coefficient ηE+ is measured during start-up of uniaxial extensional flow by means within the skill in the 30 art such as is described by J. Meissner in Proc. Xllth International Congress on Rheology, Quebec, Canada, August 1996, pages 7-10 and by J. Meissner and J. Hostettler, Rheol. Acta, 33, 1-21 (1994). The dynamic shear viscosity coefficient is measured with small-amplitude sinusoidal shear flow experiments by means within the skill in the art such as described by R. Hingmann and B. L. Marczinke, J. Rheol. 38(3), 573-87, 1994. Coupled polymers advantageously exhibit higher melt viscosities in shear and extensional flows as compared with linear polymer chains of the same absolute weight average molecular weight (Mw) and at the same temperature. Advantageously, their viscosities fall substantially to those of unmodified resins (starting materials before coupling reactions occur) for the easy flow required at high shear rates. The polymers are optionally coupled by reactions with coupling agents, preferably coupling agents which do not form free radicals during the course of the coupling process, for instance coupling agents which insert into a C-H bond, such as an azide or diazo compound. The polypropylene is reacted with a chain coupling agent which is preferably a poly(sulfonyl)azide. When the poly(sulfonyl)azide reacts with the polymer, at least two polymer chains are advantageously joined and molecular weight of the polymer chain is increased. In the preferred case when the poly(sulfonyl azide) is a bis(sulfonyl azide), two polymer chains are advantageously joined. The poly(sulfonyl azide) is any compound having at least two sulfonyl azide groups (-SO 2 N 3 ) reactive with the polymer. Preferably the poly(sulfonyl azide)s have a structure X-R-X wherein each X is SO 2 N 3 and R represents an unsubstituted or inertly substituted hydrocarbyl, hydrocarbyl ether or silicon-containing group, preferably having sufficient carbon, oxygen or silicon, preferably carbon, atoms to separate the sulfonyl azide groups sufficiently to permit a facile reaction between the polymer and the sulfonyl azide, more preferably at least 1, more preferably at least 2, most preferably at least 3 carbon, oxygen or silicon, preferably carbon, atoms between functional groups. While there is no critical limit to the length of R, each R advantageously has at least one carbon or silicon atom between X's and preferably has less than 50, more preferably less than 20, most preferably less than 15 carbon, oxygen or silicon atoms. Silicon containing groups include silanes and siloxanes, preferably siloxanes. The term inertly substituted refers to substitution with atoms or groups which do not undesirably interfere with the desired reaction(s) or desired properties of the resulting coupled polymers. Such groups include fluorine, aliphatic or aromatic ether, siloxane as well as sulfonyl azide groups when more than two polymer chains are to be joined. R is suitably aryl, alkyl, aryl alkaryl, arylalkyl silane, siloxane or heterocyclic, groups and other groups which are inert and separate the sulfonyl azide groups as described. More preferably R includes at least one aryl group between the sulfonyl groups, most preferably at least two aryl groups (such as when R is 4,4' diphenylether or 4,4'-biphenyl). When R is one aryl group, it is preferred that the group have more than one ring, as in the case of naphthylene bis(sulfonyl azides). Poly(sulfonyl)azides include such compounds as 1, 5-pentane bis(sulfonyl azide), 1,8- octane bis(sulfonyl azide), 1,10-decane bis(sulfonyl azide), 1,10-octadecane bis(sulfonyl azide), l-octyl-2,4,6-benzene tris(sulfonyl azide), 4,4'-diphenyl ether bis(sulfonyl azide), l,6-bis(4'-sulfonazidophenyl)hexane, 2,7-naphthalene bis(sulfonyl azide), and mixed sulfonyl azides of chlorinated aliphatic hydrocarbons containing an average of from 1 to 8 chlorine atoms and from 2 to 5 sulfonyl azide groups per molecule, and mixtures thereof. Preferred poly(sulfonyl azide)s include oxy-bis(4- sulfonylazidobenzene), 2,7-naphthalene bis(sulfonyl azido), 4,4'-bis(sulfonyl azido)biphenyl, 4,4'-diphenyl ether bis(sulfonyl azide) and bis(4-sulfonyl azidophenyl)mefhane, and mixtures thereof. Sulfonyl azides are conveniently prepared by the reaction of sodium azide with the corresponding sulfonyl chloride, although oxidation of sulfonyl hydazines with various reagents (nitrous acid, dinitrogen tetroxide, nitrosonium tetrafluoroborate) has been used. Sulfonyl azides decompose in several ways, but for coupling, the reactive species is believed to advantageously be the singlet nitrene evidenced by insertion into C-H bonds. Thermal decomposition is reported to give an intermediate singlet sulfonyl nitrene, which will react readily by insertion into carbon-hydrogen bonds. Temperatures advantageous for efficient formation of the sulfonyl nitrene are usually greater than 150°C. Sulfonyl azides also form another intermediate believed to be a triplet nitrene under conditions such as temperatures in excess of 240°C. This intermediate leads to chain scission and is, therefore, preferably avoided in coupling. The polymer(s) and coupling agent are suitably combined in any manner which results in desired reaction thereof, preferably by mixing the coupling agent with the polymer(s) under conditions which allow sufficient mixing before reaction to avoid uneven amounts of localized reaction then subjecting the resulting admixture to heat sufficient for reaction. Preferably, a substantially uniform admixture of coupling agent and polymer is formed before exposure to conditions in which chain coupling takes place. Mixing is preferably attained with the polymer in a molten or melted state, that is above the crystalline melt temperature, or in a dissolved or finely dispersed condition rather than in a solid mass or particulate form. The molten or melted form is more preferred to insure homogeniety rather than localized concentrations at the surface. Any equipment is suitably used, preferably equipment which provides sufficient mixing and temperature control in the same equipment, but advantageously takes place in such devices as an extruder or a static polymer mixing devise such as a Brabender blender is used. The term extruder is used for its broadest meaning to include such devices as a device which extrudes pellets or pelletizer. Conveniently, when there is a melt extrusion step between production of the polymer and its use, at least one step of the process takes place in the melt extrusion step. Alternatively, the reaction takes place in a solvent or other medium, but it is preferred that the reaction be in a bulk phase to avoid later steps for removal of the solvent or other medium. For this puφose, a polymer above the crystalline melt temperature is advantageous for even mixing and for reaching a reaction temperature (the decomposition temperature of the sulfonyl azide). In a preferred embodiment, the process takes place in a single vessel, that is mixing of the coupling agent and polymer takes place in the same vessel as heating to the decomposition temperature of the coupling agent. The vessel is preferably a twin- screw extruder, but is also advantageously a single-screw extruder or a batch mixer. To couple, also referred to herein as "to modify rheology," the poly(sulfonyl azide) is used in a rheology modifying amount, that is an amount effective to increase the low-shear viscosity (at 0.1 rad/sec) of the polymer preferably at least 5 percent as compared with the starting material polymer, but less than a crosslinking amount, that is an amount sufficient to result in at least 10 weight percent gel as measured by ASTM D2765-procedure A. While those skilled in the art will recognize that the amount of 5 azide sufficient to increase the low shear viscosity and result in less than 10 weight percent gel will depend on molecular weight of the azide used and polymer the amount is preferably less than 5 percent, more preferably less than 2 percent, most preferably less than 1 weight percent poly(sulfonyl azide) based on total weight of polymer when the poly(sulfonyl azide) has a molecular weight of from 200 to 2000. To achieve o measurable rheology modification, the amount of poly(sulfonyl azide) is advantageously at least 0.01 weight percent, preferably at least 0.02 weight percent, more preferably at least 0.05 weight percent, most preferably at least 0.10 weight percent based on total polymer. For rheology modification, the sulfonyl azide is admixed with the polymer and 5 heated to at least the decomposition temperature of the sulfonyl azide. By decomposition temperature of the azide it is meant that temperature at which the azide converts to the sulfonyl nitrene, eliminating nitrogen and heat in the process, as determined by differential scanning calorimetry (DSC). The poly(sulfonyl azide)begins to react at a kinetically significant rate (convenient for use) at temperatures of 130°C o and is almost completely reacted at 160°C in a DSC (scanning at 10°C/min). ARC (scanning at 2°C/ hr) shows onset of decomposition is 100°C. Extent of reaction is a function of time and temperature. At the low levels of azide used, the optimal properties are not reached until the azide is essentially fully reacted. Temperatures for use in the process are also determined by the softening or melt temperatures of the 5 polymer starting materials. For these reasons, the temperature is preferably greater than 120°C, more preferably greater than 150°C, most preferably greater than 180°C. Preferred times at the desired decomposition temperatures are times that are sufficient to result in reaction of the coupling agent with the polymer(s) without undesirable thermal degradation of the polymer matrix. Preferred reaction times in o terms of the half life of the coupling agent, that is the time required for half of the agent to be reacted at a preselected temperature, which half life is determinable by DSC is 5 half lives of the coupling agent. In the case of a bis(sulfonyl azide), for instance, the reaction time is preferably at least 4 minutes at 200 °C. Whether or not the crystalline and/or amoφhous polypropylenes are branched or coupled, they are blended to form blends of the invention. Blending is conveniently carried out by any means within the skill in the art such as a compounding operation, such as, for example, by single- and twin-screw extruders, Banbury mixers, Brabender mixers, Farrel continuous mixers, and two-roll mixers. The order of mixing and the form of the blend components to be mixed is not critical. Conveniently an amoφhous polymer is prepared in a separate reactor from an isotactic propylene polymer and in parallel therewith, then the two polymers are blended. The mixing temperature is preferably such that an intimate blend is obtained of the components. Determining temperatures and other conditions is within the skill in the art. Typical temperatures are above the softening or melting points of at least one of the components, and more preferably above the softening or melting points of all the components. Further details are disclosed in U.S. Application Serial Number 09/133,576, filed August 13, 1998 and U.S. Application Serial Number 09/133,244, filed August 13, 1998. Alternatively, an amoφhous polymer having increased melt strength by incoφorating polyene monomers, preferably having at least 7 carbon atoms into the propylene polymer chain, according to the procedure disclosed in U.S. Application Serial Number 09/064,672, filed April 23, 1998. The amoφhous propylene polymer is prepared by polymerization with a single site catalyst suitable for forming atactic polymer chains, preferably a metallocene or constrained geometry catalyst. The polymerization process is that previously described for preparation of amoφhous propylene polymers herein. The polyene preferably has sufficient chain length to avoid unnecessary intrachain ring formation and achieve predominantly H-type-branching, more preferably having at least 7 carbon atoms, which polyene is most preferably linear but optionally has branches of from 1 to 10 carbon atoms, such as 1,8-nonadiene, 1,9- decadiene, divinylbenzene, divinylsilane, or more preferably 1,9-decadiene. Presence of the polyene advantageously increases the ratio of the shear viscosity measured at low shear rate ( 1 Hz) divided by the shear viscosity measured at high shear rate (100 Hz) over that of the pure homopolymer or copolymer formed in the same process, or as a component of a corresponding blend with other polyolefms. In this way the melt strength (important at low shear rates) is improved while good processability (lower shear viscosity at high shear rate) is maintained. This improves the output rate in for example film production processes for packaging applications while also improving the performance (mechanical strength) of the film. Other potential applications processes include blow molding, thermoforming, injection molding and general extrusion processes. Examples of the straight-chain or branched acyclic diene compounds which are preferred polyenes include 1,6-heptadiene, 1 ,7-octadiene, 1,8-nonadiene, 1 ,9-decadiene, 1,11-dodecadiene, 1,13-tetradecadiene, and lower alkyl substituted derivatives thereof; examples of the monocyclic alicyclic diene compounds include 1,3- divinylcyclopentane, 1 ,2-divinylcyclohexane, 1,3-divinylcyclohexane, 1,4- divinylcyclohexane, 1,5-divinylcyclooctane, l-allyl-4-vinylcyclohexane, 1,4- diallylcyclohexane, l-allyl-5-vinyl-cyclooctane, 1,5-diallylcyclooctane, and lower alkyl substituted derivatives thereof. Other suitable polyenes include bicylco-(2,2,l)-hepta- 2,5-diene (norbornadiene), the dimer of norbornadiene, and diolefins having two strained ring double bonds, such as the reaction product obtained by reacting 2,5- norbornadiene with cyclopentadienyl-l,4,4a,5,8,8a-hexahydro-l, 4,5, 8-dimethano- naphtalene, and combinations thereof. Compounds similar but resulting from the addition of more bridged ring units by further condensation with such ring compounds as cyclopentadiene can also be used. Preferably the polyene is a diene, advantageously an aliphatic diene, preferably having an olefinic double bond at both terminals, in other words an -ω-diene, containing from 8 to 18 carbon atoms. More preferably, the polyene is an aliphatic α- ω-diene containing from 10 to 18 carbon atoms. Inteφolymers containing units derived from 1 ,9-decadiene are highly preferred. Highly preferred are inteφolymers comprising units derived from propylene, optionally and more preferably with another α-olefin with from 2 to 12 carbon atoms, preferably from 2 to 8 carbon atoms, and from 1 ,9-decadiene. The polyene and propylene, optionally with other alpha olefins, are polymerized in a mole ratio from 0.00005, preferably 0.005, more probably 0.007 to 0.3, preferably 0.1 mole of the polyene per mole of olefin (including propylene). Advantageous polyene contents in the inteφolymer range from 0.005, preferably 0.007 mole percent, more preferably 0.01 to preferably 0.10, more preferably 0.70, even more preferably, 0.05 most preferably 0.2 mole percent. For the highly preferred inteφolymers containing 1 ,9-decadiene units, the preferred polyene content is from 0.02 to 0.1, more preferably 0.01 0.05 mole percent. The polyene content can be determined by solution 13C NMR for those inteφolymers not containing other monomers that may interfere with the determination. The blends of the present invention optionally further comprise additives or adjuvants which are advantageously added to olefϊn-based polymers, such as fillers, anti-oxidants, colorants, UV stabilizers, flame retardants, etc. which are within the skill in the art. Blend ratios of 1 to 15 weight percent amoφhous polypropylene and 99 to 85 weight percent of crystalline polypropylene are preferred, more preferred are ratios of 1 to 10 weight percent amoφhous polypropylene and 99 to 90 weight percent crystalline polypropylene, most preferred are blends of 1 to 5 weight percent amoφhous polypropylene and 99 to 95 weight percent crystalline polypropylene. At higher concentrations of amoφhous polypropylene, the mechanical properties such as tensile modulus are negatively affected. The blends of the present invention or their blend compositions are optionally used to fabricate articles, such as films, sheet, moldings, and other shaped articles by conventional processes, preferably under melt processing conditions. Suitable processes include blow molding, extrusion, extrusion blow molding and thermoforming. The present blends can also be functionalized or grafted using to methods and techniques within the skill in the art. Blends of the invention are optionally and advantageously reacted with coupling agents in the manner described for reaction with either component of the blend. Coupling in the blend is preferably used when neither component is coupled or branched, but is alternatively used when more coupling is desirable than 5 is evident from coupling or branching of one or more components separately. Descriptions of forming processes are disclosed in E. Moore, "Propylene Handbook", Hanser Publishers, 1996. For illustration, useful processes include the following: In Bi-axially Oriented Polypropylene film manufacturing (BOPP) using the tenter frame orientation process, four distinctive sections can be identified: l o Extrusion + M(achine) D(irection) O(rientation)+ T(ransverse) D(irection) O(rientation)+ Film Winding. The extrusion part consists of a screw to melt and transport molten polymer into a slot die. The molten sheet is cooled onto a chill roll. The cooled film is guided over a section of the roll of which part of them are heated and rotate at different speeds to induce a uniaxial Machine Direction 15 Orientation (MDO). The stretched film is guided into a tenter frame where the film is stretched in the Transverse Direction Orientation (TDO) to produce the desired film thickness. The film is edge trimmed and wound up on a roll for further processing. The number of extruders is usually three or more to produce multilayer coextruded sheet or film. For thermoforming the first step in the process is 20 the same: a cast sheet extrusion. This is followed by a reheating of the sheet followed by a forging process in or on a mold. Extrusion Blow molding, consists of an extrusion set-up where the die can have a complex annular configuration. The die can move with respect to the core or mandrel to control the die gap and the final parison thickness. The parison is enclosed into a cooled mold and inflated. 25 Many different die heads and ways of producing bottles or containers exist. Extrusion blown film is a process where the extruder is connected to an annular die head. The tube of molten polymer is pulled and closed by way of nip rolls. The tube is blown up to achieve a specified blow up ratio which determines the MD and TD orientation balance. For applications in blow molding, extrusion, extrusion blow molding, injection blow molding and thermoforming, and combinations thereof the time between the melt leaving the die and crystallization, is the time available for stretching. This time span is determined mainly by the crystallization rate of the material. Blends of the invention have reduced crystallization rate as compared to the crystalline polypropylene component alone and are, therefore, advantageous when stretching or conforming to a mold or other shaping is desired. The following examples are to illustrate this invention and do not limit it. Ratios, parts, and percentages are by weight unless otherwise stated. Examples (Ex) of the invention are designated numerically while comparative samples (C.S.) are designated alphabetically and are not examples of the invention. The amoφhous polypropylene (designated aPP-1) prepared using a single site catalyst, used in Ex. 1 and 2, was prepared in the following way: A continuous stirred tank reactor with a volume of 23 liters was used. A propylene flow of 7 lbs/hr (3.2 kg/hr) and a ethylene flow of 0.15 lbs/hr (0.07 kg/hr) were combined before being introduced into a diluent mixture of C8-C10 saturated hydrocarbons commercially available from Exxon Chemical under the trade designation Isopar E, referred to hereinafter as solvent. That three component admixture is referred to hereinafter as reactor feed. The propylene and ethylene were purified by passing them through silica and alumina molecular sieves before introduction into the reactor. The reactor feed mixture was continuously introduced to the reactor. The transition metal complex and the cocatalyst, dissolved in the same solvent, were combined into a single stream and were also continuously injected into the reactor. The reactor pressure was held constant at 30 bar (3000 kPa). The reactor temperature was controlled by the catalyst flow and by the use of a cooling jacket at 65°C. The outlet stream of the reactor was taken to a heat exchanger where its temperature was raised to 270°C and then to a devolatilizing unit where the solvent was separated from the polymer. The molten polymer was then carried to a pelletizer. The polymer production rate was 3 lbs/hr (1.4 kg/hr). The catalyst system used was {(tert-butylamido)dimethyl(tetramethyl-η5- cyclopentadienyl)silane} titanium (II) 1,3 -pentadiene, the titanium being in the formal +2 oxidation state, with tris(pentafluorophenyl) borane as cocatalyst at a molar ratio of catalyst to cocatalyst to isobutyl-modified methylalumoxane of 1 :3:9. All materials other than the catalyst are commercially available. The Group IV metal complex catalyst is within the skill in the art and was prepared as disclosed by Devore et al. in U. S. Patents 5,470,993 and 5,556,928; and U.S. Patent 5,512,693 by Rosen et al. The catalyst efficiency as calculated from the measurement of the conversion of the monomers by calculating the ratio of (weight of polymer produced/hour)/( weight of monomers fed to the reactor/hour) was 43 percent. The amoφhous polypropylene (hereinafter aPP-2) prepared using Ziegler-Natta catalyst, used in C.S. B and D, was obtained from Sigma- Aldrich, Inc.and represents a typical amoφhous polypropylene made using Ziegler-Natta catalyst. The Melt Flow Rate, GPC molecular weight, Comonomer content and DSC glass transition temperature and heat of fusion of the two different amoφhous polypropylenes are listed in Table 1. Amoφhous polypropylene made using Ziegler-Natta catalyst is not found to be available with properties comparable to those of amoφhous polypropylene made using single site catalysts. Table 1 : Molecular properties of single site catalyzed and comparative Ziegler-Natta catalyzed samples of amoφhous polypropylene "wt percent means weight percent. MFR is melt flow rate as determined by ASTM-D- 1238-95 at 230°C/2.16 kg. * The MFR of sample aPP-2 was too high to be measured under the described conditions. MWD is Mw/Mn as measured by GPC (gel permeation chromatography). The glass transition temperature (Tg) and the heat of fusion (ΔHf) are measured by DSC (dynamic scanning calorimetry) at a heating rate of 10°C/min. EXAMPLES 1-2 AND COMPARATIVE SAMPLE BLENDS A-D: Blends of isotactic and single site catalyzed amoφhous polypropylene in Examples 1 and 2 contrasted with Ziegler-Natta catalyzed amoφhous polypropylene for Comparative Sample Blend B and D Blends of these amoφhous polypropylenes (aPP-1 and aPP-2), and crystalline polypropylenes were prepared by extrusion in the concentration range of 1-15 weight percent amoφhous polypropylene and 99-85 weight percent crystalline polypropylene (as indicated in Table 2). The crystalline polypropylenes used were commercially available from Montell Technology Company B.V. under the trade designations Profax™ 6523 (MFR=4.0 g/lOmin; designated herein iPP- A) and Moplen™ S38F (MFR=2.0 g/lOmin; designated herein iPP-B). During blending 1000 ppm of a phenolic-type anti-oxidant commercially available from Ciba Geigy Coφoration under the trade designation Irganox™ 1010 and 1000 ppm of a phosphite-type anti-oxidant commercially available from Ciba Geigy Coφoration under the trade designation Irgafos™ 168 were added to each blend. Table 3 gives an overview of the relative crystallization rates, the relative overall elongation after stretching and the relative stress during stretching for the blends prepared with iPP-A. Table 4 gives the relative crystallization rate, the relative overall elongation after stretching, the relative stress during stretching and the relative tear strength of stretched films for the blends prepared with iPP-B. The difference if the onset temperature of crystallization and the peak temperature of crystallization, as determined by dynamic scanning calorimetry (DSC), was used as an indicator for the crystallization rate (heating rate 10°C/min). All blends were processed in two ways, namely using sequential machine direction and transverse direction stretching and using simultaneous biaxial stretching. Sequential stretching was done on a small lab Machine Direction Orientation (MDO) line, followed by stretching in the transverse direction. The blends were extruded at a temperature of 210°C into a small tape (4 cm), which was stretched between slow rolls (9 m/min) and fast rolls (18-90 m/min) after exiting the die. Specimens measuring 50x10 mm of the monoaxially stretched films were stretched in the transverse direction using an Instron tensile tester at 100°C at 100 mm/min (according to the procedure of ASTM D638, Type V ' specimens). 5 For the simultaneous biaxial stretching, sheets were compression molded from the blends at 205°C. Squares measuring lOcmxlOcm were cut from the sheets and loaded into a biaxial film stretcher commercially available from Iwamoto Seisakusho Company Ltd. under the trade designation Iwamoto BIX-3. The squares were stretched in the synchrous biaxial mode to a final draw ratio of 6x6. During l o stretching load-displacement data were gathered. In Table 3 and 4 the relative engineering stress during stretching is reported for an elongation (λ) of 4. The tear strength of the films produced using simultaneous biaxial stretching was measured in the following way. The tear strength tests were performed using a test frame commercially available from Instron Coφ. under the 15 trade designation Instron 4505 equipped with a 112 lbf (51 kg force) full scale load cell and operating under the control of software commercially available from Instron Coφ. under the trade designation Instron Series IX Automated Materials Testing System software. Tear specimens were single-edge notched rectangular strips measuring 3" x 0.5" (0.08X0.0 lm). These were tested by pulling at a 20 crosshead speed of 2 inches per minute (0.5 m/min). Notch lengths was 0.15" (0.0038 m). Stress intensity factors K were calculated as: where W and t are the width and thickness of the strip, a is the crack length, and pmax is the maximum load. Fracture energies J* were calculated as: 25 J * = U (W - a)t where U is the total energy under the loading curve. Average values of 5 samples are reported. In the single-edge notch tear test, toughness increased slightly with decrease in notch length. Table 2: Composition of blends of isotactic and amoφhous polypropylene Table 3 : Relative crystallization rate, overall elongation and stress during stretching for blends containing iPP-A and amoφhous polypropylene (- = not measured) Table 4: Relative crystallization rate, overall elongation, stress during stretching, and tear strength for blends containing iPP-B and amoφhous polypropylene (- =not measured) The data in Tables 3 and 4 show that blending crystalline polypropylene with amoφhous polypropylene according to the practice of the invention, results in a composition having a reduced crystallization rate of the blend as compared with the crystalline polypropylene alone. Furthermore, the blend of the invention can be stretched to a higher overall elongation, which leads to higher output rates as compared with the crystalline polypropylene alone. Alternatively, at a fixed elongation, the blends of the invention can be stretched at lower stress during stretching. Since the stress during stretching is lower, fewer breaks of the film occur during the stretching process, and the final stress in the product is lower as well, leading to a longer expected lifetime of the product. Also, compared to the blend with Ziegler-Natta catalyzed amoφhous polypropylene (aPP-2), the crystallinity of the blend with single site catalyzed amoφhous polypropylene (aPP-1) is higher at the same content of amoφhous 5 polypropylene in the blend. A higher level of crystallinity will give better mechanical properties such as tensile modulus and tear strength. The tear strength expressed as the stress intensity factor K (or the fracture energy J*) of the stretched films of the blends of crystalline and amoφhous polypropylene prepared by single site catalysis is reduced by 13 percent (18 percent) l o compared to the tear strength of stretched films of crystalline polypropylene. In contrast, the Comparative Sample Blend D with amoφhous polypropylene prepared by Ziegler-Natta chemistry, exhibits a decrease in tear strength of 24 percent (32 percent), higher than the decrease in tear strength for the examples of the invention due to the lower molecular weight and the broader molecular weight distribution of the Ziegler- 15 Natta catalyst based amoφhous polypropylene. Reduced crystallization rate which is an advantage for the stretching processes such as BOPP, blow molding and thermoforming is advantageously observed in the practice of the invention.

Claims: WHAT IS CLAIMED IS: 1 . A blend composition comprising (a) from 1 to 15 weight percent of amoφhous polypropylene (b) from 99 to 85 weight percent of crystalline polypropylene, wherein the molecular weight of the amoφhous polypropylene is lower than the molecular weight of the crystalline polypropylene; the molecular weight (Mw) of the amoφhous polypropylene is higher than 50,000 g/mole; the amoφhous polypropylene has a MWD less than 3; and wherein the percentages are based on total amoφhous plus crystalline polypropylene. 2 . The composition of Claim 1 wherein the amoφhous polypropylene has a glass transition temperature greater than -10°C, the molecular weight (Mw) of the amoφhous polypropylene is greater than 100,000 g/mole; and both the amoφhous and crystalline polypropylenes are polymers with at least 90 mole percent of their repeating units derived from propylene. 3 . The composition of Claim 1 wherein at least one of the crystalline polypropylene or amoφhous polypropylene is propylene polymerized with one or more other monomers addition polymerizable with propylene, at least one of which monomers is a polyene. 4 . The composition of Claim 1 wherein at least one of the amoφhous polypropylene or the crystalline polypropylene is branched or coupled. 5 . A multistage process comprising out in two or more stages, in each of which polymerization occurs and which stages differ from one another in that at least one polymerization results in the crystalline polypropylene component, and at least one stage or polymerization results in the amoφhous polypropylene component of the composition of any of Claims 1-4. 6 . A process comprising blow molding, extruding, extrusion blow molding, or thermoforming a composition of any of Claims 1-4. 7 . A process comprising reacting a composition of any of Claims 1 -4with a coupling agent. 8 . A film, sheet, fiber or article comprising a composition of any of Claims 1-4. 9 . The film of Claim 8 wherein the film exhibits at least one of reduced crystallization rate of the blend, reduced stress during stretching, fewer breaks of the film during the stretching process, greater tear strength or lower final stress in the film as compared with a film formed from the crystalline polypropylene alone or blended with the same amount of an amoφhous polypropylene which has a molecular weight less than 30,000 g/mole or greater than that of the crystalline polypropylene. 10 . The use of a composition of any of any of Claims 1 -4 in a process comprising stretching the blend composition.

Inventors: ANSEMS PATRICIA, KOOPMANS RUDOLF, THOEN JOHAN A, ANSEMS, PATRICIA, KOOPMANS, RUDOLF, THOEN, JOHAN, A.
Applicants: ANSEMS PATRICIA, DOW CHEMICAL CO, KOOPMANS RUDOLF, THOEN JOHAN A, ANSEMS, PATRICIA, KOOPMANS, RUDOLF, THE DOW CHEMICAL COMPANY, THOEN, JOHAN, A.
Application year: 1998
Main classification: C08L23
IPC codes: C08F297, C08L23