Anti-tombstoning solder joints

Abstract: There is disclosed herein an electronic circuit assembly having anti-tombstoning solder joints, comprising: a substrate 10 having at least one mounting pad 20 thereon; an SMD 30 having at least one termination 40; and at least one solder joint 50 connecting each termination 40 to its respective mounting pad 20. Each solder joint 50 is convex in shape, having a continuous and substantially circular arcuate outer profile 60 and covering substantially all of the mounting pad 20 and substantially all of a top portion 42 of each termination 40. Each mounting pad 20 has a predetermined length l p and each solder joint has a predetermined volume of solder selected such that a positive net anti-tombstoning moment is exerted upon the SMD 30 when at least one solder joint 50 is in a molten state.

Description: The present invention relates generally to electronic circuit assemblies. More particularly, the present invention relates to electronic circuit assemblies having surface mount devices with anti-tombstoning solder joints. A typical surface mount device (SMD) is mechanically and electrically attached to a printed circuit board (PCB) substrate by providing mounting pads on the substrate, depositing solder paste onto these pads, placing the SMD on the solder paste/mounting pads such that its terminations are aligned with their respective mounting pads, reflowing the solder through the application of heat, and allowing the solder to cool so as to form a solder joint connecting each termination with its respective mounting pad; (see e.g. WO-A-96 20580 and US-A-4 127 321). Once the solder paste deposition atop each mounting pad melts, pressure forces and surface tension forces from the molten solder begin acting at the interface between the solder joint outer surface and the SMD, thereby exerting forces and moments upon the SMD. These forces are illustrated in FIG. 1, where P 1 and P 2 represent the pressure (suction) forces and F 1 and F 2 represent the surface tension forces acting by the solder joint upon the SMD, and where W represents the weight of the device. It is well known that during the reflow process the solder depositions melt at slightly different times, such that solder joints at one end of the SMD may melt and begin exerting forces on the SMD before solder joints at another end. This uneven application of forces often causes the SMD to undergo two related phenomena known as "tombstoning" and "decentreing". Tombstoning occurs when a net moment is exerted on the SMD by melted solder joints at one end of the device such that the device rotates-first about the device's centre of mass, and then about a fulcrum point G, located at the outer edge of the bottom termination adjacent the molten solder joint, when the fulcrum point touches down upon the top surface of the adjacent mounting pad-whereupon the SMD "stands up" on that end. This causes the device to detach from the unmelted or partially melted solder paste at the opposite end. Decentreing occurs when a net force is exerted on the device in a direction toward the molten solder joint, thus tending to pull the opposite end of the device off of its unmelted or partially melted solder paste. Device decentreing typically occurs before tombstoning does, and it exacerbates the tombstoning problem by detrimentally changing the angles made by F 1 and F 2 with their respective lever arms. Both tombstoning and decentreing can cause the device to be mechanically and electrically disconnected from the mounting pads on the end where the solder paste melted last. As indicated in FIG. 1, forces P 1 and F 1 contribute toward tombstoning and decentreing. Prior art attempts at addressing the problems of tombstoning and decentreing have focused on making the various depositions of solder paste on a PCB melt more simultaneously. However, this is extremely difficult to accomplish with conventional reflow soldering equipment and processes. It is desirable, therefore, to provide a way of reducing tombstoning and decentreing which does not rely on making the solder depositions melt more simultaneously. According to the present invention, there is provided an electronic circuit assembly having anti-tombstoning solder joints, comprising: a substrate having at least one mounting pad thereon; a surface mount device having at least one termination, wherein each termination has a top portion and a side portion; and at least one solder joint connecting each termination to a respective mounting pad; wherein each solder joint is convex in shape, having a continuous and substantially circular arcuate outer profile, wherein each solder joint covers substantially all of said mounting pad and substantially all of said top and side portions of said termination, and wherein each mounting pad has a predetermined length and each solder joint has a predetermined volume of solder such that a positive net anti-tombstoning moment is exerted upon said surface mount device when at least one solder joint is in a molten state. It is an advantage that the effectiveness of the present invention does not rely on near-simultaneous melting of the solder depositions on an electronic circuit assembly. It is another advantage that the present invention reduces tombstoning while providing flexibility in the spacing apart of mounting pads located at opposing ends of the SMD. The invention will now be described, by way of example, with reference to the accompanying drawings, in which: FIG. 1 is an elevational view of a concave prior art solder joint subjected to tombstoning forces; FIG. 2 is an elevational view of a convex prior art solder joint subjected to tombstoning forces; FIG. 3 is an elevational view of an over-the-top anti-tombstoning solder joint according to the present invention; FIG. 4 is a free-body diagram of an SMD and the forces acting thereon according to the present invention when a solder joint is molten and any decentreing/recentreing have occurred, but before any tombstoning might occur; and FIGS. 5A and 5B are tables of calculation results for a given SMD according to the present invention. Referring now to the drawings, FIG. 3 shows an electronic circuit assembly having anti-tombstoning solder joints according to the present invention. The assembly comprises: a substrate 10 having at least one mounting pad 20 thereon, wherein each mounting pad is of a predetermined length l p ; an SMD 30 having at least one termination 40, wherein each termination 40 has a top portion 42, a side portion 44, and an optional bottom portion 46; and at least one solder joint 50 connecting each termination 40 to its respective mounting pad 20. Each solder joint 50 has a predetermined volume V of solder and is convex in shape, rather than being concave as conventional solder joints are. The solder joint 50 has a continuous and substantially circular arcuate outer profile 60, and covers substantially all of the respective mounting pad 20 and substantially all of the top and side portions 42/44 of the respective termination 40. For simplicity, this type of solder joint 50 will be referred to hereinafter as an "over-the-top joint", or an "OTTJ". This type of solder joint structure arranges the pressure forces and surface tension forces in such a way that a positive net anti-tombstoning moment and a positive net recentreing force are both exerted on the device 30 by each solder joint 50 when each joint 50 is in a molten state (i.e., after reflow but before cooling of the joint 50). In order to optimise the design of the solder joint―50 such that an OTTJ is formed and a positive net anti-tombstoning moment and a positive net recentreing force are both exerted on the SMD 30 when each solder joint 50 melts, it is necessary to determine the amount of solder to be deposited on each mounting pad 20 in order to form such a joint 50, and to specially design the mounting pad length lp such that the forces and moments are arranged as desired while each joint is molten. These forces and moments can be seen in the free-body diagram of the SMD 30 shown in FIG. 4. This figure shows the forces acting at one termination 40 at a time when the solder joint 50 thereat is molten, but while the solder at any other termination 40 is not yet molten. Typically, when the solder paste at one joint of the device melts, the molten paste may pull (i.e., decentre) the device toward the molten paste. However, once the molten paste forms a convex joint, the outward pressure of the joint against the device will tend to re-centre the device. The forces shown in FIG. 4 are those present after any such decentreing and recentreing may occur, but before any tombstoning might occur. P 1 , P 2 , and P 3 are the pressure forces acting on the side 44, bottom 46, and top 42 terminations of the device 30, respectively, due to the higher-than-ambient pressure found within a convex solder joint 50. F 1 and F 2 are the surface tension forces acting on the device 30 at the interior edge 48 of the top termination 42 and on the interior edge 49 of the bottom termination 46, respectively. W is the weight of the device 30 acting at the device's centre of gravity located at a distance d from the fulcrum point G about which the device tends to pivot when tombstoning. Force P 1 contributes positively toward recentreing the device, while the horizontal components of forces F 1 and F 2 tend to resist recentreing. Forces P 1 , F 2 , and W contribute positively toward anti-tombstoning, while F 1 tends to resist these forces. (Forces P 3 and P 2 also contribute somewhat toward and away from anti-tombstoning, respectively, but the moments of these forces are roughly equal and opposite with respect to each other and, therefore, tend to cancel each other for typical components.) Thus, the net horizontal force ΣF x and net moment ΣM G acting on the device due to a single molten joint may be expressed as: ΣF x = P 1 - F 1 cos 02 - F 2 cos 3 and ΣM G = Wd + P 1 (H o /2) + F 2 l m sin 3 - F 1 R m sin 02 where F 1 = F 2 = σ and P 1 = H o KΔP = H o K[2σsin o / (l o + l m ) 2 + H 2 ] and R m = {GC} = l m 2 + H o 2 where ΔP is the pressure in the solder joint above ambient (in p.s.i. or N/m 2 ) and K is a correction factor (e.g., 1.5) used to account for the difference between what the actual 3D pressure would be and what the present calculations based on 2D cross-sectional area would provide. Note that a positive net value for ΣF x indicates a beneficial net recentreing force, while a positive value for ΣM G indicates a beneficial net anti-tombstoning moment. Thus, it is desired that the solder joint 50 be designed such that a positive value for ΣF x is provided before recentreing and a positive value ΣM G is provided after recentreing. An appropriate design for the mounting pad length lp is provided the volume of solder V needed to be deposited on the mounting pad 20 is determined in order to provide an OTTJ which yields the desired forces and moments when the solder joint 50 is molten, as described above. One way of designing an electronic circuit assembly having SMDs which utilise such OTTJs is to follow the iterative design steps given below. (Note that the geometry and forces referred to below are those present at a time when at least one solder joint is molten and after any decentreing and recentreing have occurred, but before any tombstoning might occur. Thus, the dimensions l i and l o refer to the "effective" inner and outer mounting pad extension lengths, respectively, at the just-mentioned point in time, rather than to the "final" inner and outer mounting pad extension lengths as measured when all joints have reflowed and solidified.) The first step is to determine the criteria for selecting the "best" anti-tombstoning joint design. For example, one criterion might be that for a given SMD, the OTTJ must provide the greatest positive anti-tombstoning moment on the SMD when at least one joint is molten. An alternative criterion might be that the OTTJ must provide the largest window of positive anti-tombstoning moments. An additional criterion might be that the joint design must fit within the given solder deposition or manufacturing constraints. Other predetermined criteria may be used as well. Second, determine the dimensions and features for each given SMD 30 and for the given solder deposition strategy. These include: W, d, the number of terminations, H o (the height of each side termination 44), h (the distance between the top of the mounting pad 20 and the underside of the bottom termination 46 (or the bottom of the device, if no bottom termination 46 is present), also known as the solder joint height), l m (the length of the top and optional bottom terminations 42/46, which are typically of the same length), w (the width of each termination 40), the surface tension σ, the 3D correction factor K, and the limits of the particular solder deposition strategy to be used (e.g., screen printing with 2 mils maximum overprinting on each side, maximum deposition thickness of 10 mils, using paste having 52% solder). Third, initially assume the inner pad extension l i to be of zero length, and select a range within which the outer pad extension length l o may be iterated. The range should be chosen based on experience, expected available board space, the size of device 30 to be used, etc. For example, for an 0.06-inch x 0.03-inch surface mount resistor, a range of 6 to 14 mils might be chosen for l o . Fourth, for selected l o values within the selected l o range (e.g., 6, 7, 8, ... 13, and 14 mils), find the radius of curvature R min which provides the smallest volume of solder V min that will form a convex, continuous, substantially circular arc covering substantially all of the top termination 42 and substantially all of the mounting pad 20 (or, more specifically, substantially all of the outer pad extension 26). Using the solder joint geometry shown in FIG. 4, this radius R min corresponds to the arc 60 min circumscribing points A, B and C. The following formula may be iteratively solved for R min : cos -1 [C o /(2R min )] + cos -1 [l m /(2R min )] = tan -1 (l o /H) + π/2 where H = H o + h and C o = {AB} = H 2 + l o 2 . Fifth, for each l o , calculate the approximate cross-sectional area A min and volume V min of the solder joint 50 corresponding to R min , using: A min = ( 01 +  02 )R min 2 - 0.5R(C o cos 01 + l m cos 02 ) + 0.5Hl o + hl m and V min = wA min where  01 = sin -1 [C o /(2R min )] and  02 = sin -1 [H/(2R min )]. Sixth, set the sum of the horizontal forces ΣF x acting on the SMD 30 to zero (corresponding to the case occurring in the molten joint after any recentreing has occurred, but before any tombstoning would occur) and solve the equation for  3 : ΣF x = 0 = P 1 - F 1 cos 02 - F 2 cos 3 , yielding  3 = cos -1 [(P 1 - F 1 cos 02 )/F 2 ]. Seventh, once  3 is known, the inner pad length l i , total mounting pad length l p , and the sum of the moments about the fulcrum point G ΣM G may be calculated, using: l i = hcos 3 and l p = l o + l m + l i and ΣM G = Wd + P 1 (H o /2) + F 2 l m sin 3 - F 1 R m sin 02 . Eighth, for each selected l o , increment the radius R through several iterations such that the corresponding solder joint cross-sectional area A and volume V increase, and repeat the area, volume, and moment calculations for these incremented R values. R may be incrementally decreased from R min down to a value R semi corresponding to the semi-circular arc 60 semi spanning between points A and C, where R semi = {AC}/2 = (l o + l m ) 2 + H 2 . As the value of R is further iterated such that A and V continue to increase, R will begin increasing above the R semi value. (Note, however, that in practice as R increases beyond R semi , there may be a tendency for the joint to form solder balls. Therefore, one may choose to limit the design such that R falls only between R min and R semi .) For each iterated R value, A, V,  3 , l i , l p , and ΣM G may be calculated using: A = R 2 sin -1 [R semi /(2R)] - (l m 2 /2)[H/(l o + l m )] - (R semi /2) √ R 2 - R semi 2 /4 + Hl o 2 /[2(l o + l m )] + hl m and V = wA and  3 = cos -1 [(P 1 - F 1 cos 02 )/F 2 ]. and l i = hcos 3 and l p = l o + l m + l i and ΣM G = Wd + P 1 (H o /2) + F 2 l m sin 3 - F 1 R m sin 02 . It may be noted that in the above area calculations (i.e., Eqns. (9) and (17)), l i was assumed to be of zero length. This was done for simplicity in order to approximate the solder joint area underneath the bottom termination as being rectangular (i.e., hl m ), since this area contributes only negligibly to the overall solder joint cross-sectional area A. However, in Eqns. (1), (2), and (13)-(15), l i is not assumed to be zero, because although l i is generally very small (on the order of 0.5 mil) it is critical to know the angle  3 formed between force vector F 2 and the horizontal in order to properly calculate ΣM G and l p . Ninth, once all of the calculations have been made for the desired range of l o values (and for the range of incremented R values corresponding to each l o ), the calculation results from the above steps may be organised in a table or spreadsheet such as that shown in FIGS. 5A-5B, and the mounting pad length l p and volume V combination which meets the predetermined selection criteria may be selected as the targeted anti-tombstoning OTTJ design. For example, using the SMD values in FIGS. 5A-5B, if the selection criterion were that the OTTJ must provide the greatest positive anti-tombstoning moment on the SMD, then l p and V values of approximately 21.36 mils and 4067.8 mil 3 , respectively, would be utilised, since this combination offers the highest positive anti-tombstoning moment (i.e., 0.94 N•mils). Alternatively, if the selection criterion were that the OTTJ must provide the largest range of positive anti-tombstoning moments, then it appears from FIG. 5 that a combination of either (1) 23.21 ≤ lp ≤ 23.53 and 4613.1 ≤ V ≤ 6102.1, or (2) 24.14 ≤ lp ≤ 24.42 and 4917.1 ≤ V ≤ 6216.5, meets this criterion. In such a case, a designer might choose a value for l p and its associated V somewhere in the middle of these ranges as the targeted values for these features. The foregoing design steps address the case of a single molten solder joint. In the case of an SMD having only one termination, or an SMD having two opposing, equally sized terminations, as well as some other cases, no further calculations need be done in order to design an OTTJ according to the present invention. However, for SMDs having three or more terminations, or two terminations both on the same side of the device, as well as other cases, additional calculations need to be done. These additional calculations would be necessary because the foregoing steps cover the case of only one molten joint, while the presently-mentioned types of SMDs may have two or more joints molten at any given time which might contribute toward tombstoning. For such devices, the same type of analysis as given above is conducted, but with a modified version of the foregoing equations adapted to include all of the forces and moments acting on the device due to the two or more molten (and potentially tombstoning) solder joints. One consideration that should be kept in mind is that it may not be possible to actually produce some of the iterated configurations given the solder deposition or other practical constraints a designer might face. For example, those lines in FIGS. 5A-5B which have "#NUM!" (indicating a spreadsheet calculation error) in the  3 , l i , l p , and ΣM G columns represent iterations which are physically impossible to produce. Also, it may not be possible for a given solder deposition strategy to deposit enough solder paste to achieve the calculated solder volume V for some of the iterated configurations. (Note that the "Max. Paste" for the given deposition strategy has been estimated for each l o , where Max. Paste equals the product of: (1) the deposition thickness T; (2) the percent of solder in the solder paste S % ; (3) the pad length (approximated here as l o + l m ) plus the maximum overprinting length beyond each pad O L ; and (4) the width w of the pad plus the maximum overprinting on the two sides of the pad O S .) Note that in FIGS. 5A-5B all iterations in which ΣM G ≥ O and V ≤ Max. Paste have been marked with a diamond to denote those iterations which are both producible and anti-tombstoning. It can thus be seen that any such solder deposition, manufacturing, and/or other practical constraints should be included as part of the selection criteria. Once the designer has determined the optimum combination of mounting pad length l p and solder joint volume V which provide an anti-tombstoning OTTJ and which meet the predetermined selection criteria, the designer has some flexibility in determining the spacing to be used between mounting pads placed at opposite ends of the device. This flexibility exists because the success of the present invention does not rely upon the spacing between opposite mounting pads. This is due to the fact that the force balance on the device provided by the present invention after all joints have melted tends to leave the part substantially centred with respect to the mounting pads. One design option that would minimise decentreing and recentreing during reflow is to space the mounting pads such that when the SMD is placed thereon, the same SMD-to-mounting pad orientation is achieved as would be found when at least one solder deposition is molten. In other words, the placement of the pads and SMD are such that when one joint is molten, the SMD will already be positioned on the pads so as to achieve horizontal force equilibrium, thus requiring no decentreing and/or recentreing of the device. Thus, once lp is determined as discussed above, the mounting pads may be spaced such that the interior edge 24 of their inner pad extensions 22 are substantially flush with the interior edge 48 of their respective bottom terminations 46, since the calculated l i value is generally so small. Various other modifications to the present invention will, no doubt, occur to those skilled in the art to which the present invention pertains. For example, although FIGS. 3 and 4 show the SMD's terminations 40 comprising contiguous top, side, and bottom portions, with the top and bottom portions being substantially equal in length (which is typical of many SMDs), it is not necessary that each termination have a bottom portion 46, nor that the side portion 44 extend down the full height of the device, nor that the top and bottom portions be equal in length. It is the following claims, including all equivalents, which define the scope of the invention.

Claims: An electronic circuit assembly having anti-tombstoning solder joints, comprising: a substrate (10) having at least one mounting pad (20) thereon; a surface mount device (30) having at least one termination (40), wherein each termination (40) has a top portion (42) and a side portion (44); and at least one solder joint (50) connecting each termination (40) to a respective mounting pad (20); wherein each solder joint (50) is convex in shape, having a continuous and substantially circular arcuate outer profile (60), wherein each solder joint (50) covers substantially all of said mounting pad (20) and substantially all of said top and side portions of said termination, and wherein each mounting pad (20) has a predetermined length and each solder joint (50) has a predetermined volume of solder such that a positive net anti-tombstoning moment is exerted upon said surface mount device (30) when at least one solder joint is in a molten state. An electronic circuit assembly according to claim 1, wherein said predetermined length and said predetermined volume are selected according to a predetermined selection criterion. An electronic circuit assembly according to claim 2, wherein said predetermined selection criterion is that each anti-tombstoning solder joint provides a maximum positive anti-tombstoning moment on said surface mount device when at least one solder joint is molten. An electronic circuit assembly according to claim 2, wherein said predetermined selection criterion is that each anti-tombstoning solder joint provides a largest window of positive anti-tombstoning moments on said surface mount device when at least one solder joint is molten. An electronic circuit assembly according to claim 1, wherein said surface mount device is an electronic component having three or more terminations. An electronic circuit assembly according to claim 1, wherein said surface mount device is an electronic component having two opposing terminations. An electronic circuit assembly according to claim 1, wherein each termination further includes a bottom portion, and wherein an interior edge of an inner pad extension of each mounting pad is substantially flush with a respective termination bottom portion interior edge. An electronic circuit assembly according to claim 1, wherein an interior edge of an inner pad extension of each mounting pad is substantially flush with a respective termination bottom portion interior edge.

Inventors: JAIRAZBHOY VIVEK AMIR, MCMILLAN RICHARD KEITH II, JAIRAZBHOY, VIVEK AMIR, MCMILLAN, RICHARD KEITH, II
Applicants: FORD MOTOR CO, FORD MOTOR COMPANY
Application year: 1998
Main classification: H05K3
IPC codes: H05K3