Fluorescent yellow azo pigment

Abstract: Yellow azo fluorescent pigments and a process for a preparing same. Yellow azo fluorescent pigments as a component of printing ink, coating, plastic compositions manufacturing operations.

Description: The present invention is directed to fluorescent yellow azo pigments and a process for preparing same. The invention is also directed to printing ink, coating and polyolefin compositions and articles of manufacture containing the pigments. Fluorescent colorants are well known and represent an important class of materials commonly used in coloring of printing inks, paints and plastics to impart a desired color. For example, the prior art describes a number of fluorescent organic dyes; see for example U.S. Patents. 2,929,931; 2,938,292; 2,983,686; 3,105,908; 3,115,417; 3,162,642; 3,177,153; 3,407,196; 3,420,821; 3,423,407; 3,492,478; 3,560,238; 3,597,364; 3,599,389; 3,614,430; 3,671,451; 3,760,161; 3,776,761; 3,892,972; 3,960,755; 4,006,158; 4,015,131. These include, stilbenes (such as diamino-stilbene-di-sulfuric acid), berberin sulfate tetra-ethyl-diamino-o-carboxyphenyl, xanthenyl chloride, tetramethyl-di-amino-diphenyl-ketoamine hydrochloride, tetramethyl-di-amino-diphenyl-ketoamine hydrochloride, auranin, xylene red B, rhodamine B, rhodamine 6G , and fluorescein. The fluorescent organic dyes in the prior art are also used for marking applications such as machine sorting, mail sorting and web registration control in manufacturing operations. For some applications it is desired that the marking be colorless when viewed under visible light and emit fluorescent radiation when irradiated by an incident light source. In these particular applications, however, it is not sufficient that the mark emit radiation when irradiated, the marking must emit the incident radiation at a different and higher wavelength and at a level sufficient to be detected by a detector such as that described in U.S. Patent 4,467,207. Also, it is equally important that the materials do not bleed or migrate through the web or substrate so as to enlarge or relocate the marking. U.S. Patent 4,467,207 describes various fluorescent organic dye compounds that do not migrate or bleed when used in markings for thermoplastic web applications. These include, coumarin dyes such as 4-methyl-7-(sulfo methyl amino) coumarin sodium salt, benzoxazoles, stilbene dyes such as Phorite CL, and Phorite BA (Verona Dyestuff Division, Mobay Chemical Corporation), TH-40 (Sandoz Corporation, East Hanover, New Jersey), and IR-125, a dark red organic laser dye (Eastman Kodak Corporation, Rochester New York). As previously mentioned, fluorescent organic dyes suffer from migration or bleeding. This not only presents a problem in marking applications but lessens the effect of a color. In addition, this becomes a serious health concern where the fluorescent organic dyes are used in food packaging applications or in any application where the dyes may come in contact with the skin. In general, organic dyes also have a low thermal stability, thereby precluding their use at high temperatures. In order to overcome some of the practical limitations in using fluorescent organic dyes, fluorescent pigments, which represent another class of colorants are sometimes employed. Broadly speaking, the essential difference between an organic dye and an organic pigment is solubility. Conventional fluorescent pigments, which are dissolved in a resin matrix, which resin inturn is not soluble in the application medium, tend to suffer from migration and plateout. For example, along with being thermally unstable, organic dyes are fairly soluble in plastics while pigments are insoluble and have higher thermal stability. The prior art described only a limited number of fluorescent organic pigments. No fluorescence is found, for example, in commonly used organic pigments such as Pigment Red 188, Pigment Red 202 and Pigment Orange 36. European Patent EP-B-0 495 338 teaches a heat stable Pigment Red 202 having increased crystalite size. However, the increased crystalite size can be achieved only when the pigment is substantially fluorescence free. Thus, prior art teaches that an increase in the particle size of an organic pigment is accompanied by a decrease in fluorescence and vice versa. U.S. Patents 4,370,269 and 4,476,052 describe pigments having improved hiding power such as Pigment Orange 36 but neither teaches that the pigment has any fluorescent properties. U.S. Patent 3,162,642 and 4,983,661 describe a " fluorescent pigment" used in marking applications. However, these pigments are organic dyes dissolved in a resin matrix. The resin matrix is then formed to a specific size, typically or several microns so that it may be used as a pigment. Organic pigments of this type are further described by P.A.Lewis, Pigment Handbook, on pages 860-61. Herbst and Hunger, Industrial Organic Pigments , on pages 555-556, describe a fluorescent Pigment Yellow 101, a disazomethine compound. However, this compound is not in the same class of disazo pigment compounds as the present invention. Yellow azo pigments represent an important class of organic pigments and include monoazo yellow and disazo yellow pigments. Yellow azo pigments are well known and are typically derived from coupling a acetoacetanilide or( pyrazolone derivatives with a diazonium or bis-diazonium salt containing an aromatic amine or diamine. A number of patents are available which describe the preparation and various uses of these pigments; see for example U.S. Patents 2,341,889; 3,617,171; 3,759,731; 3,775,148; 3,776,749; 4,341,701; 4,968,352 and 5,352,280. These pigments are not commonly known to exhibit fluorescence when exposed to incident radiation. While not wishing to be bound by theory, it is believed that the chemical structure and physical form of a pigment greatly influences whether or not it will be fluorescent. P.A. Lewis, Pigment Handbook, on pages 861-879, provide a detailed discussion on the theory of fluorescence dye based organic pigments. The properties of commercial grade organic pigments depend, in most instances, on process treatments which are sued extensively to generate the various pigment grades for select applications. These treatments, may for example, involve chemical reactions which modify particle size, crystalite size, distribution and overall crystal morphology of the pigment. These all effect such properties such as shade, color strength, dispersibility, rheology, gloss, etc. It is also known that heat treating a pigment, for example, in a slurry, can cause crystalite growth. No where in the prior art, however, does it indicate that such modifications would impart fluorescence. It is an object of the present invention to provide fluorescent yellow azo pigments. It is an object of the present invention to provide fluorescent yellow azo pigments of increased cyrstalite size. It is a further object of the present invention to provide fluorescent yellow azo pigments that do not migrate or bleed through polyolefin or thermoplastic webs or substrates. It is yet a further object of the present invention to provide printing inks, coatings and polyolefins that contain, as a component, the fluorescent yellow azo pigments of the present invention. Other objects and advantages of the invention will become apparent from the following description of embodiments. The invention refers to fluorescent yellow azo pigments exhibiting a spectral response to incident radiation where the maximum response between wavelengths of 520 and 560 nanometers exceeds the response at 600 nanometers. In another aspect the invention provides fluorescent yellow azo pigments having increased cyrstalite size. In another aspect the invention provides for printing ink, coating and plastic compositions containing at least one fluorescent yellow azo pigment exhibiting a spectral response to incident radiation where the maximum response between wavelengths of 520 and 560 nanometers exceeds the response at 600 nanometers. In another aspect the invention provides a process for preparing fluorescent yellow azo pigments. In yet another aspect the invention provides improvements in the manufacturing or packaging of thermoplastic materials by providing printing inks having non-migrating markings comprised of organic pigments. It has been surprisingly discovered that yellow azo pigments can be made to fluoresce remarkably when exposed to incident radiation. The pigments emit at higher wavelengths where the incident radiation is reflected and not absorbed. The result is an increased spectral response and a cleaner brighter shade of pigment. It should be noted that the shade is cleaner and brighter than that observed when no increase in spectral response is obtained. The yellow azo pigment compositions of the present invention include disazo yellow and monoazo yellow pigments and more particularly include diarylide yellow pigments and most preferably include Pigment Yellow 12, Pigment Yellow 13, Pigment Yellow 14, Pigment Yellow 17, Pigment Yellow 63, Pigment Yellow 83. In the present invention the fluorescence of each sample prepared by the present invention was visually observed using a standard light box having an ultraviolet light source. The spectral response (% reflectance) for each sample was quantitatively measured with a CS-5 ChromaSensor color spectrophotometer (available from Applied Color Systems, Inc.) that has a tungsten-halogen lamp. The instrument settings were: D65 (CIE standard illuminant) 10 degrees, large area and specular. In order to quantify the degree of fluorescence exhibited by a sample material containing the pigment, an empirical rating system was developed whereby the degree of fluorescence is rated from 0 to 10. A rating of 0 means the sample exhibits no fluorescence, while a rating of 10 means the sample exhibits extremely high levels of fluorescence. In addition, ten independent ratings were obtained for each sample using the rating system. The ratings were then averaged to generate a final value. The average rating for each sample is shown in the Table, i.e. Visual Rating. The degree of fluorescence exhibited by the yellow azo pigments of the present invention has been defined by the percent increase in percent reflectance in the wave length region of maximum reflectance. For example, for Pigment Yellow 63 this region is between 500 to 600 nanometers. The spectral response (percent reflectance) various wavelengths was plotted for Pigment Yellow 63 in the wave length region of maximum response. Spectral response for Pigment Yellow 63: The reflectance was measured over a white background but a black background could also have been used. Using a black background we observed an increase in the percent reflectance at an incident wavelength of 520 nanometers. The maximum increase in spectral response for Pigment Yellow 63 as prepared in Example 1, Example 2 and Example 3 occurs at a different incident wavelength. The advantages of the present invention are more clearly illustrated by the spectral response for Pigment Yellow 63 prepared in accordance with Example 2, wherein the pigment intermediate is slurried in water and the spectral response for Pigment Yellow 63 prepared in accordance with Example 3, wherein the pigment intermediate is slurried in ethanol. While Example 2 yielded a pigment with a maximum percent increase in spectral response of 2.5 percent, Example 3 yielded a pigment with a maximum percent of 4.7 percent. The percent increase in spectral response for Pigment Yellow 63 achieved under the present invention was totally unexpected and represents a substantial change in the characteristic physical properties for the pigment. In order to appreciate the significance of the results achieved under the present invention, a publication by the American Society for Testing Materials (ASTM); ASTM Designation: E 1247-92, entitled The Standard Method for Identifying Fluorescence in Object-Color Specimens by Spectrophotometry, states that fluorescence is considered significant if spectral reflectance differs by only 1% of full scale at the wavelength of greatest difference. When the results are evaluated on this basis, the yellow azo pigments of the present invention represent substantial and unprecedented change in the fluorescent properties of these pigments. The fluorescent yellow azo pigments of the present invention are prepared by adding 3,3'-dichlorobenzidine to hydrochloric acid (preferably in a 2:1 molar ratio) and preferably an equal molar amount of sodium nitrite to produce a tetrazotized 3,3' dichlorobenzidine solution. Next, a coupling suspension is prepared separately by dissolving a coupler in at least an equal molar ratio to a sodium hydroxide solution and forming a suspended precipitate with acetic acid. The specific coupler employed will be different in each case depending on the yellow azo pigment being prepared. For example, if Pigment Yellow 63 is desired the coupler will be acetoacet-o-chlorbanilide. Likewise, if Pigment Yellow 12 or Pigment Yellow 14 are desired the coupler will be respectively, acetoacetanilide or acetoacet-o-toluidide. The resulting tetrazotized 3,3'-dichlorobenzidine solution is reacted with the suspended precipitate to form a pigment intermediate. The pigment intermediate is then filtered, washed with excess amounts of water and dried. The drying is typically carried out in a drying oven at temperatures ranging from 80 to 85° C. The dried pigment at this point is similar to prior art yellow azo pigments. The pigment is then added to a solvent to obtain a slurry which preferably contains about 5 weight percent pigment. The slurry is heated to a temperature sufficient to form the final pigment of the present invention. The heating may optionally be carried out at greater than atmospheric pressure in a closed pressure vessel wherein the pressure range up to 689 kPa (100 pounds per square inch (psi)). The pigment is isolated by removing the solvent by any number of techniques known in the prior art, e.g. vacuum distillation of filtration. The solvent employed in the slurrying step is selected from aromatic hydrocarbons, chlorinated aromatic hydrocarbons, aliphatic hydrocarbons, chlorinated aliphatic hydrocarbons, C 1 -C 6 alcohols, C 1 -C 6 ketones, ethers, C 1 -C 6 acetates and water; more preferred are C 1 -C 6 alcohols or water. Pigmented systems which contain the pigment as a component of mixtures of substances, possibly in addition to other components, include: pastes, flush pastes, preparations, printing colors, distempers, binder colors or lacquers and varnishes of all kinds, such as. physically and oxidatively drying lacquers and varnishes, acid, amine and peroxide curing varnishes or polyurethane varnishes. The pigment may also be present in synthetic, semisynthetic or natural macromolecular substances, such as thermoplastic resins, e.g., polyvinyl chloride, polystyrene, polyethylene, polyesters, phenoplasts, aminoplasts and rubber or in admixture with natural, regenerated or synthetic fibers, such as glass, silicate, asbestos, wood cellulose, acetylcellulose, polyacrylonitrile, polyester, polyurethane and polyvinyl chloride fibers or mixtures of the same, and powders, for example, fillers, organic or inorganic pigments. The pigment provides prints, paint and varnish coatings, coverings, shaped articles, such as sheets, threads, plates, fibers, blocks, granulates and rods having a brilliant color and excellent durability. Substances which contain as an active coloring ingredient the yellow azo pigment of the present invention, may be of solid, elastic, pasty, viscous, mobile or thixotropic consistency and may be obtained by conventional methods. Aqueous pastes, for example, may be obtained by stirring the pigment into water, possibly with the addition of a wetting or dispersing agent or by stirring or kneading the pigment into a dispersing agent in the presence of water, an organic solvent or oil. These pastes may for example be used for the production of flush pastes, printing colors, distempers, plastic dispersions and spinning solutions. The pigment may also be introduced by stirring, rolling, kneading or grinding into water, organic solvents, non-drying oils, drying oils, lacquers, varnishes, plastics or rubber. Finally, it is also possible to work up the pigment by drying mixing with organic or inorganic masses, granulates fibrous materials, powders and other pigments to form mixtures of substances. In addition to having fluorescent properties, purity of shade, good fastness to light, weathering and solvent and migration resistance greater than for conventional yellow pigments, the pigment of the present invention also shows superior thermal resistance. For example, the thermal behavior of the pigment makes it possible to work it into high and low density polyethylene or polypropylene, without the shade of color being dulled by the effect of the temperatures employed during work-up. It is noted that the invention is deemed to include pigments resulting from a blend of the fluorescent yellow azo pigments of the present invention and minor amounts of conventional pigments. The blends should exhibit similar distinguishing characteristics, inter alia, in fluorescent properties, although to a lesser degree. Like many other pigments, the pigments of the . present invention may advantageously be surface treated by known methods to improve their performance in a variety of automotive and other finish systems. Additives which serve to lessen or avoid flocculation and increase pigment dispersion stability can also be advantageously used. The fluorescent yellow azo pigments of the present invention are especially suitable for use in marking applications wherein information is encoded on a web or substrate with a fluorescent ink or coating; see for example U.S. Patents 3,599,389; 3,614,430; and 3,760,161. Markings which include the yellow azo pigments of the present invention, may be transparent, as in the case of the a clear fluorescent coating. The marking may also be camouflaged or covert, as in the case of fluorescent printing ink. U.S. Patent 4,467,207, incorporated herein by reference, describes web or sheet articles encoded with information that controls operations performed on or with the articles. The preferred marking material for, a plastic, for example, is an ink formulated with a pigment of the present invention. Markings made with such pigments offer distinct advantages over the fluorescent organic dyes markings of U.S. Patent 4,467,207. Much like the organic dyes in that patent, the fluorescent pigments are also non-migratory on the web and respond to incident radiation harmless to the human eye. A detector suitable for detecting the radiation emitted from makings made with pigments of the present invention is described in U.S. Patent 4,467,207. The following examples illustrate specific aspects of the present invention and are not intended to limit the scope thereof in any respect and should not be so construed. In the examples, all parts are by weight unless otherwise indicated. The relationship of parts by weight to parts by volume is as that of kilograms to liters. Example 1 (Comparative) 3,3'-dichlorobenzidine (25.3 parts) was added to ice/water mixture (146 parts) containing 20° Be hydrochloric acid (46 parts). The solution was stirred to a uniform consistency and formed a homogeneous suspension. A 38.5% solution of sodium nitrite (37.5 parts) was added and the suspension was stirred at a temperature of 0 to 3°C to form a tetrazotized 3,3'-dichlorobenzidine solution (A). The excess nitrous acid was then removed by adding sulfamic acid (1 part) and clarified by filtering. Water was added to adjust (A) to 365 parts. Acetoacet-o-chloroanilide (44.4 parts) was dissolved in water (490 parts) and a 50% solution of sodium hydroxide (42 parts). The mixture was stirred to dissolve the solids. The temperature of the solution was adjusted to 0 to 5°C. A precipitate (B) was formed by adding a 70% acetic acid solution (47.3 parts). Water was added to adjust the suspension to 1220 parts. A coupling reaction for (A) and (B) was carried out by continuously adding (A) to (B) while stirring over a 60 minute period to form a pigment slurry intermediate (C). Stirring continued until no excess (A) remained. The temperature was then increased to 90°C for 1 hour. The resulting pigment slurry was cooled to 70°C, filtered, washed and dried at a temperature of 80°C to afford Pigment Yellow 63, PY-63, (70 parts). The pigment was incorporated into an ink formulation for evaluation. Example 2 The entire procedure of Example 1 was repeated, then the resulting Pigment Yellow 63 (50 parts) was added to water (1000 parts) to form a slurry. The slurry was stirred and heated in a closed pressure vessel to 130°C at 172,25 to 241,15 kPa (25 to 35 psi) for 2.5 hours. The slurry was then cooled to 70°C, filtered, washed and dried at a temperature of 80°C to afford a fluorescent Pigment Yellow 63 (50 parts). The pigment was incorporated into an ink formulation for evaluation. Example 3 The entire procedure of Example 1 was repeated, then the resulting Pigment Yellow 63 (50 parts) was added to ethanol (1000 parts) to form a slurry. The slurry was stirred and heated in a closed pressure vessel to 130°C at 413,4 to 482,3 kPa (60 to 70 psi) for 2.5 hours. The slurry was then cooled to 70°C, filtered, washed and dried at a temperature of 80°C to afford a fluorescent Pigment Yellow 63 (50 parts). The resulting pigment was incorporated into an ink formulation for evaluation. Example 4 (Comparative) The procedure of Example 1 was repeated, except acetoacet-o-chloro anilide (44.4 parts) was replaced with acetoaceteanilide (37.2 parts) to afford a Pigment Yellow 12, PY-12, (62 parts). The pigment was incorporated into an ink formulation for evaluation. Example 5 The procedure of Example 4 was repeated, then the resulting Pigment Yellow 12 (50 parts) was added to ethanol (1000 parts) to form a slurry. The slurry was stirred and heated in a closed pressure vessel to 130°C at 413,4 to 482,3 kPa (60 to 70 psi) for 2.5 hours. The slurry was then cooled to 70°C, filtered, washed and dried at a temperature of 80°C to afford a fluorescent Pigment Yellow 12 (50 parts). The pigment was incorporated into an ink for evaluation. Example 6 (Comparative) The procedure of Example 5 was repeated, except acetoaceteanilide (40.1 parts) was replaced with acetoacet-o-toluidide (40.1 parts) to afford Pigment Yellow 14, PY-14, (66 parts). The pigment was incorporated into an ink formulation for evaluation. Example 7 The procedure of Example 6 was repeated, then the resulting Pigment Yellow 14 (50 parts) was added to ethanol (1000 parts) to form a slurry which was stirred and heated in a closed pressure vessel to 130°C at 413,4 to 482,3 kPa (60 to 70 psi) for 2.5 hours. The slurry was then cooled to 70°C, filtered, washed and dried at a temperature of 80°C to afford a fluorescent Pigment Yellow 14 (50 parts). The pigment was incorporated into an ink formulation for evaluation. Example 8 (Comparative) The procedure of Example 1 was repeated, except the pigment was incorporated into a coating formulation for evaluation. Example 9 The procedure of Example 2 was repeated, except the fluorescent pigment was incorporated into a coating formulation for evaluation. Example 10 The procedure of Example 3 was repeated, except the fluorescent pigment was incorporated into a coating formulation for evaluation. The pigments prepared in each of the above Examples were evaluated for fluorescent properties in a coating and solvent based ink formulation. The ink formulation was prepared by charging pigment (20 grams) to a solvent-based ink vehicle(80 grams) containing commercial grade RS nitrocellulose resin and 0,3175 cm (1/8 inch) stainless steel balls (300 grams). This mixture was agitated for 30 minutes using a paint shaker to produce a millbase. The finished ink was prepared by letting back millbase(50 grams)with additional vehicle(50 grams). The ink was then mixed and strained to remove the steel balls and the viscosity of the ink was reduced to 15-16, as measured with a #3 Zahn Cup, by adding solvent. The ink was then drawn down onto a substrate with a #6 meyer rod. The coating was prepared by charging pigment (10 grams) to a solvent-based paint vehicle (90 grams) containing commercial grade alkyd resin and 0,3175 cm (1/8 inch) stainless steel balls (300 grams). This mixture was agitated for 30 minutes using a paint shaker to produce a dispersion. A drier mix (2 grams) was then added to the dispersion which was then mixed and strained to remove the steel balls. The coating was then drawn down onto black and white substrate with a 76.2 µm (0,003 inch) Bird Film Applicator (Form 2C-Opacity Chart, available from the Leneta Co., Mahwah, New Jersey). The results for Examples 1-10 are shown in the Table. Fluorescence Example Pigment Visual %Reflectance %Increase in %Reflectance (1) PY-63 1.9 81.8 standard 2 PY-63 4.1 83.2 2.5 3 PY-63 8.4 85.2 4.7 (4) PY-12 1.0 83.3 --- 5 PY-12 1.6 82.7 --- (6) PY-14 0.2 82.8 --- 7 PY-14 0.5 82.2 --- (8) PY-63 1.9 76.8 standard 9 PY-63 4.4 77.4 0.8 10 PY-63 8.4 78.9 2.7 The table shows that the pigments prepared by the present invention show a higher level of fluorescence than those prepared by prior art techniques.

Claims: A fluorescent yellow azo pigment exhibiting a spectral response to incident radiation wherein the maximum response between wavelengths of 520 and 560 nanometers exceeds the response at 600 nanometers. The pigment of claim 1 selected from disazo yellow and monoazo yellow pigments. The pigment of claim 2 wherein the pigment is a diarylide yellow pigment. The pigment of claim 3 being Pigment Yellow 63. The pigment of claim 4 having an average crystallite size greater than 350 Angstroms. The pigment of claim 3 being Pigment Yellow 12 or Pigment Yellow 14. A printing ink composition having incorporate therein at least one fluorescent yellow azo pigment as defined in any of claims 1 to 6. A coating composition having as a constituent thereof at least one fluorescent yellow azo pigment as defined in any of claims 1 to 6. A plastic composition containing at least one fluorescent yellow azo pigment as defined in any of claims 1 to 6. A process for preparing a fluorescent yellow azo pigment as defined in any of claims 1 to 6 comprising: (a) preparing a solution of tetrazotized 3,3'dichlorobenzidine by adding 3,3'-dichlorobenzidine to hydrochloric acid and sodium nitrite; (b) preparing a coupling suspension by dissolving a coupler in a sodium hydroxide solution, and forming a suspended precipitate of the coupling suspension with acetic acid; (c) reacting the solution of tetrazotized 3,3'-dichlorobenzidine with the suspended precipitate to form a pigment intermediate; (d) filtering said intermediate; (e) water washing said intermediate; (f) drying said intermediate; (g) forming a slurry of said intermediate in a solvent; and (h) heating said slurried intermediate wherein said heating is optionally carried out under pressure. The process of claim 10 wherein the solvent is selected from aromatic hydrocarbons, chlorinated aromatic hydrocarbons, aliphatic hydrocarbons, chlorinated aliphatic hydrocarbons, C 1 -C 6 alcohols, C 1 -C 6 ketones, ethers, C 1 -C 6 acetates and water. The process of claim 11 wherein the solvent is ethanol or water. The process of claim 10 wherein the pigment prepared is a fluorescent Pigment Yellow 63, prepared by using as a coupler acetoacet-o-chloroanilide. The process of claim 10 wherein the pigment prepared is a fluorescent Pigment Yellow 12, prepared by using as a coupler acetoacetanilide. The process of claim 10 wherein the pigment prepared is a fluorescent Pigment Yellow 14, prepared by using as a coupler acetoacet-o-toluidide. An improved method for controlling operations to an article of manufacture involving (a) affixing a non-migrating mark of organic polar or ionic material to a heat-sealable polyolefin web; (b) detecting the presence of said mark on said web by sensing the presence of said emitted radiation; and (c) performing operations to said web; wherein said improvement comprises: affixing a non-migrating mark of fluorescent yellow azo pigment as defined in any of claims 1 to 6 to said heat-sealable polyolefin web. An improved web of thermoplastic polyolefin material, which fuses under application of heat and pressure, suitable for fabrication into a series of connected but separable articles, and carrying a series of marks of organic polar or ionic material that essentially do not migrate in the web and emits wavelength-shifted radiation when exposed to incident radiation; wherein said improvement comprises: a web of thermoplastic polyolefin material carrying a series of marks of fluorescent azo yellow pigments as defined in any of claims 1 to 6 that essentially does not migrate in the web. An improved web capable of being moved along a path relative to an operating mechanism, said web comprising a thermoplastic polyolefin material, which fuses under application of heat and pressure, suitable for operations including at least heat sealing into a series of articles useful as at least a part of a container, and indicia at location on said web correlated with said articles for controlling operations of the mechanism upon the web, said indicia being comprised of a polar or ionic organic material which emits wavelength-shifted radiation in the non-visible spectrum, that essentially does not migrate in the web, is essentially invisible to the human eye and detectable to control the operating mechanism; wherein said improvement comprises: an indicia comprised of a fluorescent yellow azo pigment, as defined in any of claims 1 to 6 that essentially does not migrate in the web. An improved article of manufacture comprising a thermoplastic polyolefin foil, which fuses under application of heat and pressure, and a mark on the foil, said mark being comprised of an organic ionic or polar material which responds to incident electromagnetic radiation by emitting radiation of a different wavelength to allow detection of the presence of said mark; said improvement comprises: a mark comprised of a fluorescent azo yellow pigment, as defined in any of claims 1 to 6. An improved article useful in the packaging or container art and capable of being moved along a path relative to a fabricating mechanism, said article comprising a sheet or web of thermoplastic polyolefin material to be fabricated, which fuses under application of heat and pressure and indicia carried by the article for controlling the fabrication, said indicia being comprised of an organic polar or ionic material that emits wavelength-shifted radiation under incident electromagnetic radiation and that is essentially non-migrating in said material and that is essentially invisible to the human eye under electromagnetic radiation in the visible spectrum; said improvement comprises: an indicia comprised of a fluorescent yellow azo pigment, as defined in any of claims 1 to 6 which is essentially non-migrating in said material.

Inventors: GREGORIO MANUEL Z, MERCHAK PAUL A, SCHWARTZ RUSSELL J, ZWIRGZDAS ANTHONY C, GREGORIO, MANUEL Z., MERCHAK, PAUL A., SCHWARTZ, RUSSELL J., ZWIRGZDAS, ANTHONY C.
Applicants: SUN CHEMICAL CORP, SUN CHEMICAL CORPORATION
Application year: 1998
Main classification: C09B67
IPC codes: C09K11, C09B67