Neutralization method for polyorganosiloxanes

Abstract: A method is disclosed for neutralizing a polyorganosiloxane mixture which comprises (A) contacting a mixture of a polyorganosiloxane and an acid with a neutralizing amount of a solid organic base at a temperature above the melting temperature of said organic base to form a molten organic base and thereafter producing an insoluble adduct of the acid with the molten organic base; (B) lowering the temperature to effect solidification of residual molten organic base to residual solid organic base; and (C) effecting separation of the insoluble adduct and the residual solid organic base from the polyorganosiloxane mixture. The present invention is especially useful for neutralizing polyorganosiloxane mixtures where the polyorganosiloxane comprises hydrogen atoms bonded to silicon.

Description: The present invention is a method for neutralizing a polyorganosiloxane mixture containing an acid. Our method comprises contacting said mixture with a neutralizing amount of a solid organic base, at a mixture temperature above the melting point temperature of the solid organic base, to form an insoluble adduct of the acid with the molten organic base, then lowering the mixture temperature to effect solidification of residual molten organic base to residual solid organic base and thereafter effecting separation of the insoluble adduct and the residual solid organic base from the polyorganosiloxane mixture by standard means for separating solid-liquid mixtures. Polyorganosiloxanes are used in the form of fluids and are crosslinked to produce, for example, silicone rubbers and resins. It is important that polyorganosiloxane fluids as well as compositions containing such fluids and components prepared therefrom be stable during storage, shipment and exposure to heat. A typical process for making polyorganosiloxanes involves heating low molecular weight linear polyorganosiloxanes and cyclic polyorganosiloxanes at a temperature above 40°C. in the presence of a strong acid, such as trifluoromethanesulfonic acid, to effect polymerization of the siloxanes to higher molecular weight polyorganosiloxanes. The product of this acid catalyzed reaction is an equilibrium mixture comprising as a major portion linear polyorganosiloxanes and as a minor portion cyclic polyorganosiloxanes. The presence of cyclic polyorganosiloxanes in the products is undesirable because they can have sufficiently high vapor pressure to cause problems during use. Therefore, these cyclics are typically removed by heat distillation under reduced pressure. If the acid catalyst is not initially neutralized, additional cyclic siloxanes will be generated during the distillation process in an attempt to maintain equilibrium conditions. In addition, polyorganosiloxanes and compositions comprising them have impaired heat resistance and storage stability when the acid catalyst is not sufficiently neutralized. U.S. Patent No. 5,514,828 teaches a process for making polyfluoroalkylsiloxane fluid using a strong acid, such as trifluoromethane sulfonic acid, as the catalyst which is subsequently neutralized by adding a solid basic material, such as alkaline earth carbonates; oxides such as magnesium carbonate, magnesium oxide and barium carbonate and alkali metal bicarbonates such as sodium bicarbonate or ammonium bicarbonate. The excess neutralizing agent and the formed salts of that patent are filtered off and product polyfluoroalkylsiloxane fluid recovered. However, a problem associated with said method is that since the carbonates and oxides are insoluble and do not melt, it is run as a heterogeneous process having liquid and solid phases which require large excesses of neutralizing agent and operating times. U.S. Patent 5,241,032 describes a process for making polyorganosiloxanes in the presence of a strong acid catalyst and subsequently neutralizing the acid catalyst by the addition of ammonia gas. Although that method is run as a gas-liquid phase process and provides for rapid neutralization of the acid catalyst, it is not entirely satisfactory since a large excess of gas is required and neutralization or complete removal of residual ammonia is difficult along with an undesirable odor of polyorganosiloxanes which can result from the presence of residual ammonia. The present invention provides for a method for neutralizing acid present in polyorganosiloxane mixtures by using as the neutralizing agent a solid organic base having a melting point above 20°C, such that the mixture is conveniently contacted with the solid organic base at a temperature above the melting point of the solid organic base, thereby effecting neutralization in a homogeneous process containing only liquid reactants. The temperature of the mixture is then lowered below the melting point temperature of the molten organic base thereby effecting solidification of the residual molten organic base. Residual solid organic base and the insoluble adduct formed as a neutralization product are then easily separated from the mixture by standard methods for separating solid-liquid mixtures. Because the present neutralization method is run as a homogeneous liquid-phase process, neutralization of the acid is effected quickly without the use of large stoichiometric excesses of the solid organic base. Separation of residual solid organic base and the insoluble adduct neutralization product from the polyorganosiloxane mixture is readily achieved herein by cooling the mixture below the melting point of the solid organic base to effect solidification and by using standard methods such as filtration to effect separation of the resulting solid-liquid mixture. The method of this invention comprises (A) contacting a mixture comprising a polyorganosiloxane and an acid with a neutralizing amount of a solid organic base having a melting point temperature above 20°C at a mixture temperature above the melting temperature of the solid organic base, to produce a molten organic base and to make an insoluble adduct of the acid with the molten organic base, (B) lowering the mixture temperature to effect solidification of residual molten organic base to residual solid organic base; and (C) effecting separation of the insoluble adduct and the residual solid organic base from the polyorganosiloxane mixture. The present invention is especially useful.for neutralizing mixtures comprising polyorganosiloxane mixtures where the polyorganosiloxane comprises hydrogen atoms bonded to silicon. The polyorganosiloxane component of the present mixture can be any of those generally known in the art. Typically, the polyorganosiloxane comprises repeating units described by formula - (R 1 2 SiO) x -, where each R 1 is independently selected from hydrogen atoms or hydrocarbyl radicals comprising less than 12 carbon atoms. The hydrocarbyl radical includes an alkyl such as methyl, ethyl, propyl, tert-butyl; an aryl such as phenyl; an alkenyl such as vinyl, allyl and hexenyl, a cycloalkyl such as cyclopentyl or cyclohexyl; a substituted alkyl such as 3,3,3-trifluoropropyl or chloromethyl; and a substituted aryl such as chlorophenyl. The number of repeating units denoted by x is not limited and can be from two to 100,000. This polyorganosiloxane can be a linear or branched polymer. It can also be monodisperse or polydisperse. The polydiorganosiloxane can further be a homopolymer or a block or random copolymer. The polyorganosiloxane may be end-terminated, for example, with siloxy groups described by formula R 1 2 R 2 1 SiO-, where R 1 is as previously described and R 2 is selected from R 1 or hydroxyl. This polydiorganosiloxane is, for example, trimethylsiloxy end-terminated polydimethylsiloxane, vinyldimethylsiloxy end-terminated polydimethylsiloxane, vinyldimethylsiloxy end-terminated polydimethyl (vinylmethyl) siloxane copolymer, dimethylhydroxysiloxy end-terminated polydimethylsiloxane, dimethylhydrogensiloxy end-terminated polydimethylsiloxane, dimethylhydrogensiloxy end-terminated polydimethyl(methylhydrogen)siloxane copolymer, trimethylsiloxy or (3,3,3-trifluoropropyl)dimethylsiloxy end-terminated polydiorganosiloxane having 50 percent of the pendant organic groups attached to silicon being methyl and the remainder being 3,3,3-trifluoropropyl and trimethylsiloxy end-terminated polydimethyl(methylphenyl)siloxane copolymer. The present method is particularly useful for neutralizing mixtures where the polyorganosiloxane comprises one or more hydrogen atoms bonded to silicon. It is well known that even moderately strong bases will cleave the Si-H bond. Therefore, processes for preparing polyorganosiloxanes having hydrogen bonded to silicon atoms are typically prepared using an acid catalyst and the catalyst is thereafter neutralized with a mild base. To prevent scission of the Si-H bond during storage and use of the polyorganosiloxane (polyorganohydrogensiloxane), it is necessary to neutralize the acid catalyst in a manner such that residual base is not left in the polyorganohydrogensiloxane. The claimed method herein offers an effective and convenient method for accomplishing this neutralization. In a preferred method, the polyorganosiloxane mixture results from the polymerization of cyclic or short-chain polyorganosiloxanes and mixtures thereof, in the presence of an acid. Such a mixture is prepared by polymerizing cyclic polyorganosiloxanes, having on the average from three to six organosiloxy units per molecule, in the presence of short-chain linear polyorganosiloxanes useful as chain extenders and as endblockers. A preferred polyorganosiloxane mixture for use in our method results from the trifluoromethane sulfonic acid catalyzed polymerization of a mixture comprising linear polymethylhydrogensiloxanes , cyclic polydimethylsiloxanes and a polydimethylsiloxane endblocker. In our preferred polyorganosiloxane mixture, the polyorganosiloxane is a trimethylsiloxy end-terminated polydimethyl (methylhydrogen) siloxane copolymer or dimethylhydrogensiloxy end-terminated polydimethyl(methylhydrogen)siloxane copolymer. The acid comprising a portion of the polyorganosiloxane mixture is not critical to the present method so long as the acid forms an insoluble adduct with the solid organic base. In a preferred method, the acid present in the polyorganosiloxane mixture is trifluoromethane sulfonic acid or the silyl esters of trifluoromethanesulfonic acid, such as trimethylsilyl trifluoromethanesulfonate or triethylsilyl trifluoromethanesulfonate. Most preferred is when the acid is trifluoromethane sulfonic acid. The concentration of the acid in our polyorganosiloxane mixture is not critical and is generally a concentration useful in catalyzing the polymerization of polyorganosiloxane mixtures, for example, up to 1,000 ppm of acid. The solid organic base useful in the present method is any material which has a melting point temperature above 20°C and lower than the temperature at which significant decomposition of the polyorganosiloxane occurs, which forms an insoluble adduct with the acid to be neutralized through an acid-base reaction while in the molten state and which is solidified by lowering the temperature of the neutralized mixture to allow separation from the mixture by conventional methods for separating solid-liquid mixtures. It is preferred that the solid organic base have a melting point temperature within a range of 20°C. to 100°C. Most preferred is when said organic base has such a temperature within a range of 40°C. to 90°C. The chemical nature of the insoluble adduct of the solid organic base with the acid is not critical so long as the insoluble adduct is sufficiently insoluble under the conditions of our method to allow separation from the polyorganosiloxane mixture as a solid. The insoluble adduct may be, for example, a compound, salt or complex resulting from the contact of the acid with the solid organic base in the molten state. By the term "neutralizing amount" of a solid organic base, we mean any amount capable of neutralizing all or a portion of the acid present in the polyorganosiloxane mixture through an acid-base reaction to thereby form an insoluble adduct with the acid. Since our polyorganosiloxane mixture has a temperature above the melting point of the solid organic base, the claimed method is run as a homogeneous liquid phase process thereby effecting very efficient contact of the organic base with the acid and therefore large excesses of the solid organic base are not required. To ensure optimal neutralization of the acid, it is preferred that the solid organic base be added to the present method in at least stoichiometric equivalence relative to the acid. Preferred is when 1 to 2 stoichiometric equivalents of solid organic base is added relative to the acid. Most preferred is when said organic base is added at approximately 1.1 stoichiometric equivalents relative to the acid. The solid organic base is selected from the group consisting of ethyl carbamate, urea, 1,1-diethyl urea, 1,3-diethyl urea, ε-caprolactam, diacetamide, acetamide, acrylamide, imidazole, maleimide, acetaldehyde ammonia trimer and succinimide. A preferred solid organic base for use in our method is selected from the group consisting of ε-caprolactam, acetamide, urethane and imidazole. The most preferred solid organic base is ε-caprolactam. The method of effecting the contact of our polyorganosiloxane mixture with the solid organic base is not critical so long as the temperature of the polyorganosiloxane mixture is above the melting point of the solid organic base to thereby form a molten organic base. The solid organic base is usually added to the polyorganosiloxane mixture and the mixture then heated to a temperature above the melting point of the solid organic base; or the temperature of the polyorganosiloxane mixture can already be above the melting temperature of the solid organic base when added. In a preferred method, the solid organic base is added to a polyorganosiloxane mixture resulting from the acid catalyzed polymerization of cyclic and/or linear polyorganosiloxanes at an elevated temperature before cool-down has occurred of the mixture below the melting point temperature of the solid organic base. To insure efficient contact of the solid organic base in the molten state with the acid, it is preferred that sufficient mixing of the polyorganosiloxane mixture with the organic base be effected to form an essentially homogeneous mixture. This mixing is readily achieved by standard methods such as stirring. The length of contact time of the solid organic base in the molten state with the polyorganosiloxane mixture is not critical so long as adequate contact is provided to provide the required level of neutralization. Generally, a contact time within a range of 1 second to 4 hours is considered useful. More preferred is a contact time of 5 minutes to 4 hours. Even more preferred is a time within a range of 30 minutes to 3 hours. Longer contact times may be used, but in some instances, the insoluble complex of the acid with the solid organic base may hydrate causing the complex to solubilize in the polyorganosiloxane mixture and to thereby reduce the neutralization effectiveness of the method. After the solid organic base in the molten state has been contacted with the acid for the desired amount of time, the mixture temperature is lowered to effect solidification of the residual molten organic base to the residual solid organic base. The method of lowering the temperature is not critical and is easily accomplished by allowing the mixture to cool to ambient temperature, unassisted by external means or by providing external cooling to the wall of the container holding the mixture. It is only necessary that the mixture be cooled sufficient to effect solidification of the molten organic base; however, cooling to lower temperatures is acceptable if desired. Separation of the insoluble adduct and the residual solid organic base from the polyorganosiloxane mixture is effected by standard methods for separation of solid-liquid mixtures, such as settling, centrifugation and filtration. Filtration is a preferred method for separating the insoluble adduct and the solid organic base from our polyorganosiloxane mixture. The following examples are provided to further illustrate the present invention. Example 1. The ability of ε-caprolactam to neutralize a polymethylhydrogensiloxane fluid was evaluated. Said fluid was prepared by adding to a 2 L flask, equipped with a stirrer and temperature controller, 7.8 g of a trimethylsiloxy end-blocked polymethylhydrogensiloxane having a degree of polymerization between 30 to 40, 11 g of 2 mPa·s polydimethylsiloxane fluid, 893 g of cyclic polydimethylsiloxanes and 5 x 10 -3 moles of trifluoromethanesulfonic acid. This mixture was heated to 45°C. and allowed to polymerize for 10 hours. Aliquots of the above prepared polymethylhydrogensiloxane were neutralized with 1.1 equivalents of ε-caprolactam (m.p. 70-72°C) at the temperatures reported in Table 1. The Acid Number of each of the aliquots was determined at the times given in Table 1. The Acid Number was determined by titration with potassium hydroxide using phenolphthalein as indicator and the results are listed in Table 1 as milligrams of potassium hydroxide per gram of the polymethylhydrogensiloxane. The Acid Number of the unneutralized polymethylhydrogensiloxane was 0.119. Neutralizing Effects of ε-Caprolactam Acid Number Time (hrs) 45°C. 75°C. 0.5 0.076 0.024 1 0.078 0.024 2 0.079 0.016 3 0.079 0.017 4 0.051 0.014 Example 2 The ability of acetamide, urethane and imidazole to neutralize a polymethylhydrogensiloxane polymer was evaluated. The polymethylhydrogensiloxane was prepared as in Example 1 and had an unneutralized Acid Number of 0.119. The polymer was divided into aliquots with 1.1 equivalents of acetamide, urethane or imidazole being added to duplicate aliquots. One duplicate aliquot containing each of the neutralizing agents was heated to 100°C. for three minutes to melt the neutralizing agent and the other aliquot kept at room temperature. To each of these aliquots was added 0.1 g of perlite as filtering aid (DICALITE(R), Grefro, Inc., Torrance, CA). Each aliquot was filtered at room temperature and the Acid Number determined by titration with methanolic potassium hydroxide using bromocresol purple as an indicator. The Acid Number for each of the tested samples is provided in Table 2. Ability of Selected Solid Organic Bases to Neutralize Polymethylhydrogensiloxanes Acid Number (x 10 -3 ) Compound Melting Temp. (°C.) Rm. Temp. 100°C. Acetamide 79-81 8.98 3.97 Urethane 48.5-50 10.07 4.44 Imidazole 88-90 6.59 2.52 Example 3 (Comparative Example) The ability of (NH 4 ) 2 CO 3 to neutralize a polymethylhydrogensiloxane was evaluated. The polymethylhydrogensiloxane was prepared as in Example 1 and had an unneutralized Acid Number of 0.305. Next, 1.1 equivalents of the (NH 4 ) 2 CO 3 were added to an aliquot of the polymethylhydrogensiloxane and the resulting mixture was heated to 95°C. for 0.5 hour. The resulting mixture had a strong ammonia odor. The mixture was filtered using 0.1 g of perlite (DICALITE) as filtering aid but still smelled of ammonia. The filtered material was placed under vacuum at 65°C. for 2 hours and the resulting product had no ammonia smell. The Acid Number of the mixture after heating under vacuum was 0.0229. Example 4 (Comparative Example) The ability of CaCO 3 to neutralize a polymethylhydrogensiloxane was evaluated. The polymethylhydrogensiloxane was prepared as in Example 1 and had an unneutralized Acid Number of 0.305. Ten equivalents of CaCO 3 were added to an aliquot of the polymethylhydrogensiloxane at room temperature. The mixture was then filtered. Filtering was difficult due to clogging of the filter. The Acid Number of the filtered product was 0.038.

Claims: A method for neutralizing a polyorganosiloxane mixture comprising (A) contacting said mixture comprising a polyorganosiloxane and an acid with a neutralizing amount of a solid organic base having a melting point temperature above 20°C, at a mixture temperature above the melting point temperature of the solid organic base, to produce a molten organic base and to make an insoluble adduct of the acid with the molten organic base; (B) lowering the mixture temperature to effect solidification of residual molten organic base to residual solid organic base, and (C) effecting separation of the insoluble adduct and the residual solid organic base from the polyorganosiloxane mixture. A method for forming a neutralized polyorganosiloxane mixture comprising (A) first contacting an organosiloxane oligomer with an acid effective as a catalyst at a contact temperature greater than 20°C. to effect formation of a polyorganosiloxane mixture comprising polyorganosiloxane and said acid; (B) contacting the formed polyorganosiloxane mixture with a neutralizing amount of a solid organic base, having a melting point temperature above 20°C and less than the contact temperature of step (A) and forming an insoluble adduct with the acid, where the temperature of said formed polyorganosiloxane mixture is greater than the melting point temperature of the solid organic base thereby forming a molten organic base, (C) lowering the temperature of the formed polyorganosiloxane mixture to effect solidification of residual molten organic base to residual solid organic base; and (D) effecting separation of the insoluble adduct and residual solid organic base from the polyorganosiloxane mixture. The method of claims 1 or 2 where the polyorganosiloxane comprises polydimethylsiloxy and polymethylhydrogensiloxy units. The method of any of claims 1 to 3, where the solid organic base is an amine. The method of any of claims 1 to 3, where the solid organic base is selected from ethyl carbamate, urea, 1,1-diethyl urea, 1,3-diethyl urea, ε-caprolactam, diacetamide, acetamide, acrylamide, imidazole, maleimide, acetaldehyde ammonia trimer and succinimide. The method of any of claims 1 to 5, where the acid is trifluoromethane sulfonic acid or a silyl ester of trifluoromethane sulfonic acid. The method of any of claims 1 to 6, where the melting point temperature of the solid organic base is within a range of 20°C. to 100°C. The method of any of claims 1 to 7, where the neutralizing amount of the solid organic base is 1 to 2 stoichiometric equivalents relative to the acid. The method of any of claims 1 to 8, where the mixture is contacted with the molten organic base for a period of time within a range of 1 second to 4 hours.

Inventors: GRAIVER DANIEL, TSELEPIS ARTHUR JAMES, GRAIVER, DANIEL, TSELEPIS, ARTHUR JAMES
Applicants: DOW CORNING, DOW CORNING CORPORATION
Application year: 1998
Main classification: C08G77
IPC codes: C08G77