Indolocarbazole electroluminescent devices

Abstract: An organic electroluminescent device member comprised of a charge transport component of an indolocarbazole represented by Formulas (I), (II), (III), (IV), (V), or (VI); or optionally mixtures thereof wherein R and R' are independently selected from the group consisting of a hydrogen atom, halogen atom, alkyl, alkoxyl, and aryl; m and n are numbers of 0 to 4; R 1 and R 2 are independently selected from the group consisting of alkyl, aryl, and vinyl; R 3 and R 4 are independently selected from the group consisting of a hydrogen atom, halogen atom, alkyl, alkoxy, and aryl, and p is a number of from 1 to 3.

Description: This invention is generally directed to electroluminescent (EL) devices, or members, and more specifically, to organic EL devices with enhanced thermal and operational stability, and thus improved device durability, and which devices contain charge, especially hole transport components, or compounds comprised of indolocarbazole compounds, such as those of the formulas illustrated herein. PRIOR ART Prior art organic EL devices can contain a laminate comprised of an organic luminescent material and electrodes of opposite polarity, which devices include a single crystal material, such as single crystal anthracence, as the luminescent substance reference, for example, in U.S. -A- 3,530,325. However, these devices require excitation voltages on the order of about 100 volts or greater. Subsequent modifications of the device by the incorporation of additional layers, such as charge injecting and charge transport layers, have provided some performance improvement. Illustrative examples of EL devices have been disclosed in publications by Tang et al. in J. Appl. Phys ., vol. 65, pp. 3610 to 3616 (1989) and Saito et al. in Mol. Cryst. Liq. Cryst ., vol. 253, pp. 125 to 132 (1994). Specifically, U.S. -A-4,356,429 discloses an EL device formed of an organic luminescent medium consisting of a hole transporting layer and an electron transporting layer, wherein the hole transporting layer is comprised of a porphyrinic compound. Further, in U.S. -A- 4,539,507 there was substituted an aromatic tertiary amine layer for the hole transporting porphorinic layer. Illustrative examples of the aromatic tertiary amine compounds disclosed in the '507 patent are triphenylamines, such as N,N,N-triphenylamine and N,N,N-tri-p-tolylamine, those containing at least two aromatic tertiary amine moieties such as 1,1-bis(4-di-tolylaminophenyl)cyclohexane, and tetraaryldiamines such as N,N'-bis(3-methylphenyl)-N,N'-diphenyl-4,4'-diaminobiphenyl, N,N,N'N'-tetra-p-toly-4,4'-diaminobiphenyl. Also, of interest with respect to EL devices are U.S. -A-. 5,487,953 and US-A-5,554,450. It was the object of the present application to provide improved organic EL device members comprising improved hole transport materials. This object has been solved in accordance with the claims. FIGURES Illustrated in Figures 1 and 2 are EL devices of the present invention. SUMMARY OF THE INVENTION The features of the present invention are accomplished by the following claims and in embodiments thereof by the provision of layered organic EL devices comprised of an anode, a cathode, and sandwiched between the anode and the cathode an organic electroluminescent element comprised of a hole transporting layer containing an indolocarbazole compound, an electron transporting layer, and which devices possess a number of advantages including improved thermal stability, long service life, high electroluminescence efficiency, superior hole and electron injecting and transporting characteristics, and can be fabricated using vacuum deposition techniques. More specifically, the EL devices of the present invention in embodiments thereof provide improved thermal and operational stability, and excellent device durability at temperatures equal to, or above 45°C. In embodiments, the present Invention relates to organic EL devices, or members comprised of an anode, a hole transporting layer, an electron transporting layer, and a cathode, and wherein the transporting layer contains at least one indolocarbazole compound represented by the following Formulas (I) through (VI), that is (I), (II), (III), (IV), (V), or (VI); or mixtures thereof wherein R and R' are independently selected from the group consisting of a hydrogen atom, a halogen atom, alkyl, alkoxyl, and aryl; m and n are numbers of 0 to 4; R 1 and R 2 are independently selected from the group consisting of alkyl, aryl, and vinyl; R 3 and R 4 are hydrogen atom, alkyl, alkoxy, aryl, or a halogen atom; and p is a number of from 1 to 3. Alkyl can contain from 1 to 25 carbon atoms; alkoxy can contain from 1, preferably 2, to 25 carbon atoms; aryl can contain from 6 to 30 carbon atoms; and aryl may be substituted with, for example, alkyl, alkoxy, and the like. The present invention relates to an organic electroluminescent device member comprised of a charge transport component of an indolocarbazole represented by Formulas (I), (II), (III), (IV), (V), or (VI); or optionally mixtures thereof wherein R and R' are independently selected from the group consisting of a hydrogen atom, halogen atom, alkyl, alkoxyl, and aryl; m and n are numbers of 0 to 4; R 1 and R 2 are independently selected from the group consisting of alkyl, aryl, and vinyl; R 3 and R 4 are independently selected from the group consisting of a hydrogen atom, halogen atom, alkyl, alkoxy, and aryl, and p is a number of from 1 to 3. Preferably, aryl is a fused aromatic ring, more preferably the fused ring is benzo. Preferably, alkyl contains from 1 to 25 carbon atoms, alkoxy contains from 1 to 25 carbon atoms, and aryl contains from 6 to 30 carbon atoms, more preferably alkyl contains from 1 to 10 carbon atoms, alkoxy contains from 2 to 12 carbon atoms, and aryl contains from 6 to 18 carbon atoms, most preferably alkyl contains from 1 to 6 carbon atoms, and alkoxy contains from 1 to 6 carbon atoms. In this embodiment it is preferred that alkyl is methyl, ethyl, propyl, butyl, pentyl, heptyl, or hexyl, alkoxy is methoxy, ethoxy, propoxy, butoxy, pentoxy, or heptoxy, and aryl is phenyl, or naphthyl, most preferably phenyl. The halogen atom is typically an atom of chlorine, bromine, fluorine, or iodine. Typically, m and n are the numbers 1, 2, 3, or 4. It is preferred that R and R' are hydrogen, or alkyl, and R 1 and R 2 are aryl. It is further preferred that R 3 and R 4 are hydrogen atoms. It is preferred that R 1 and R 2 are independently selected from the group consisting of phenyl, naphthyl, and biphenyl. It is more preferred that the indolocarbazole (I), or (II) is selected. It is most preferred that said indolocarbazole is a hole transport of 5,11-di-m-tolyl-5,11-dihydroindolo[3,2-b]carbazole, 5,11-bis(3,4-dimethylphenyl)-5,11-dihydroindolo[3,2-b]carbazole, 5,11-di-1-naphthyl-5,11-dihydroindolo[3,2-b]carbazole, 5,11-bis(3-methoxyphenyl)-5,11-dihydroindolo[3,2-b]carbazole, 5,11-bis(1,1'-biphenyl-4-yl)-5,11-dihydroindolo[3,2-b]carbazole, 5,11-di-2-naphthyl-5,11-dihydroindolo[3,2-b]carbazole, or 2,8-dimethyl-5,11-di-1-naphthyl-5,11-dihydroindolo[3,2-b]carbazole. In one embodiment, the member includes an anode and a cathode, and an organic electroluminescent zone situated between the anode and cathode, and said organic electroluminescent zone comprises a hole transporting indolocarbazole of (I), (II), (III), (IV), (V), or (VI). In this embodiment, it is preferred that R 1 and R 2 are phenyl, biphenyl, naphthyl, or thienyl. It is also preferred that aryl contains from 6 to 30 carbons, wherein R 1 and R 2 are aryl groups; R and R' are hydrogen atoms or methyl groups; R 3 and R 4 are hydrogen atoms; and p is 1. It Is particularly preferred that said indolocarbazole compound is selected from the group consisting of 5,11-di-m-tolyl-5,11-dihydroindolo[3,2-b]carbazole, 5,11-bis(3,4-dimethylphenyl)-5,11-dihydroindolo[3,2-b]carbazole, 5,11-di-1-naphthyl-5,11-dihydroindolo [3,2-b]carbazole, 5,11-bis(3-methoxyphenyl)-5,11-dihydroindolo[3,2-b] carbazole, 5,11-bis(1,1'-biphenyl-4-yl)-5,11-dihydroindolo[3,2-b]carbazole, 5,11-di-2-naphthyl-5,11-dihydroindolo[3,2-b]carbazole, 2,8-dimethyl-5,11-di-1-naphthyl-5,11-dihydroindolo[3,2-b]carbazole, 5,7-di-m-tolyl-5,7-dihydroindolo[2,3-b]carbazole, 5,7-di-1-naphthyl-5,7-dihydroindolo[2,3-b] carbazole, 5,8-di-m-tolyl-5,8-dihydroindolo[2,3-c]carbazole, 5,8-bis-(3,4-dimethylphenyl)-5,8-dihydroindolo[2,3-c]carbazole, and 5,12-di-1-naphthyl-5,12-dihydroindolo[3,2-a]carbazole. It is most preferred that said indolocarbazole compound is selected from a group consisting of 5,11-di-m-tolyl-5,11-dihydroindolo[3,2-b]carbazole, 5,11-bis(3,4-dimethylphenyl)-5,11-dihydroindolo[3,2-b]carbazole, 5,11-di-1-naphthyl-5,11-dihydroindolo[3,2-b]carbazole, 5,11-bis(3-methoxyphenyl)-5,11-dihydroindolo[3,2-b]carbazole, 5,11-bis(1,1'-biphenyl-4-yl)-5,11-dihydroindolo[3,2-b]carbazole, 5,11-di-2-naphthyl-5,11-dihydroindolo[3,2-b] carbazole, and 2,8-dimethyl-5,11-di-1-naphthyl-5,11-dihydroindolo[3,2-b] carbazole, and that said member includes a charge injecting layer and thereover an electron transport layer and an electron injector layer. In another embodiment, the member further includes a supporting substrate, an anode, a hole transporting layer, an electron transporting layer, and a cathode, wherein said anode is comprised of a layer of indium tin oxide with a thickness ranging from 30 nanometers to 100 nanometers, wherein said hole transport layer contains at least one of said indolocarbazole compounds with a thickness ranging from 10 nanometers to 100 nanometers, said electron transporting layer is comprised of a layer of a metal chelate compound with a thickness ranging from 10 nanometers to 100 nanometers, and said cathode is a magnesium/silver alloy or a lithium/aluminum alloy, and which cathode is of a thickness ranging from 10 nanometers to 200 nanometers. In another embodiment the member includes a substrate, an anode, a cathode, and situated between the anode and cathode a hole injector layer, said charge transporting indolocarbazole layer, and thereover an electron transport layer, and an electron injector layer. It is also preferred that the anode is indium tin oxide with a thickness ranging from 30 nanometers to 100 nanometers, the cathode is a magnesium silver alloy, the hole injector layer is comprised of a porphyrin compound with a thickness ranging from 5 nanometers to 50 nanometers, the charge transporting layer is a hole transporting layer comprised of said indolocarbazole compound with a thickness ranging from 10 nanometers to 80 nanometers, the electron transport is comprised of a metal chelate compound of 8-hydroxyquinoline with a thickness ranging from 10 nanometers to 80 nanometers, and the electron injector is comprised of a metal chelate compound of 8-quinolinethiol with a thickness ranging from 5 nanometers to 50 nanometers. The present invention provides also an organic electroluminescent device member comprised of a hole transport component of an indolocarbazole represented by (I), (II), (III), (IV), (V), or (VI). wherein R and R' are independently selected from the group consisting of hydrogen, halogen, alkyl, alkoxyl, and aryl; m and n as defined before; R 1 and R 2 are independently selected from the group consisting of alkyl and aryl; R 3 and R 4 are independently selected from the group consisting of hydrogen, halogen, alkyl, alkoxy, and aryl, and p is a number as defined before. DESCRIPTION OF EMBODIMENTS The embodiments of the present invention will be described in more details with reference to the following schematic diagrams of EL devices as depicted in Figure 1 and Figure 2: Figure 1 illustrates an EL device or an organic light emitting diode 1, comprised of a supporting substrate 2 of, for example, glass, an anode 3, an organic indolocarbazole of the formulas illustrated herein hole transporting layer 4, an organic electron transporting layer 5, and in contact therewith a cathode 6, such as a low work function metal. In this EL device, a junction is formed between the hole transporting layer, or zone and the electron transporting layer, or zone. In operation, when the anode is electrically biased to a positive potential with respect to the cathode, holes are injected into the organic hole transporting zone and transported across this zone to said junction. Concurrently, electrons are injected from the cathode Into the electron transporting zone and are transported toward the same junction. Recombination of holes and electron occurs near the junction, resulting in light emission. In another embodiment as illustrated in Figure 2, the light emitting diode 1 is comprised of a supporting substrate 2 of, for example, glass, an anode 3, an indolocarbozale of the formulas illustrated herein, organic hole transporting zone 4, an organic electron transporting zone 5, and in contact therewith a cathode 6. In this device structure, the transporting zone Is comprised of one or more transport layers as opposed to the single layer transporting zone of the device structure of Figure 1. Specifically, the hole transporting zone 4 of Figure 2 is comprised of a layer 4a which facilitates hole injection, and an indolocarbazole layer 4b which transports hole carriers. The electron transporting zone 5 is comprised of a layer 5a which facilitates electron injection, and a layer 5b which transports electrons. Illustrative examples of the supporting substrate include polymeric components, glass and the like, and polyesters like MYLAR®, polycarbonates, polyacrylates, polymethacrylates, polysulfones, quartz, and the like. Other substrates can also be selected providing, for example, that the material selected can effectively support the other layers, and does not interfere with the device functional performance. The thickness of the substrate can be, for example, from 25 to 1,000 microns or more and, for example, from 50 to 500 depending, for example, on the structural demands of the device. Examples of the anode contiguous to the substrate include positive charge injecting electrodes such as indium tin oxide, tin oxide, gold, platinum, or other materials, such as electrically conductive carbon, π-conjugated polymers such as polyaniline, polypyrrole, and the like, with, for example, a work function equal to, or greater than 4 electron volts, and more specifically, from 4 to 6 electron volts. The thickness of the anode can range from 10 to 5,000Å with the preferred range being dictated by the optical constants of the anode material. One preferred range of thickness is from 20 to 1,000 Angstroms (Å). The hole transporting layer 4 illustrated herein can be of a number of convenient forms. For example, this layer may be comprised of one layer comprising one or more hole transport components, at least one of which is an indolocarbazole compound. In one preferred form, layer 4 may be laminately formed from a layer 4a In contact with the anode, and which layer contains a component which facilitates hole injection, and a layer 4b containing the indolocarbazole hole transport component Any suitable materials which can inject holes from the anode may be employed in layer 4a, with the preferred materials being the porphyrin derivatives as disclosed in U.S. -A- 4,720,432. Representative examples of porphyrin derivatives are porphyrin; 1,10,15,20-tetraphenyl-21H,23H-porphyrin copper (II); copper phthalocyanine, copper tetramethyl phthalocyanine; zinc phthalocyanine; titanium oxide phthalocyanine; magnesium phthalocyanine; and the like. In embodiments, the hole transporting zone 4 contains at least one indolocarbazole compound of the formulas illustrated herein. These compounds offer a number of advantages as illustrated herein in that, for example, they possess a relatively high glass transition temperature, for example ranging from 80°C to 200°C, and are capable of forming thermally and morphologically stable thin films by vacuum evaporation techniques. Illustrative examples of indolocarbazole are (1) 5,11-di-m-tolyl-5,11-dihydroindolo[3,2-b]carbazole, (2)5,11-bis(3,4-dimethylphenyl)-5,11-dihydroindolo[3,2-b]carbazole, (3) 5,11-di-1-naphthyl-5,11-dihydroindolo[3,2-b]carbazole, (4) 5,11-bis(3-methoxyphenyl)-5,11-dihydroindolo[3,2-b]carbazole, (5) 5,11-bis(1,1'-biphenyl-4-yl)-5,11-dihydroindolo[3,2-b]carbazole, (6) 5,11-diphenyl-5,11-dihydroindolo[3,2-b]carbazole, (7) 5,11-di-2-naphthyl-5,11-dihydroindolo[3,2-b]carbazole, (8) 5,11-bis(3-chlorophenyl)-5,11-dihydroindolo[3,2-b]carbazole, (9) 2,8-dimethyl-5,11-diphenyl-5,11-dihydroindolo[3,2-b]carbazole, (10) 2,8-dimethyl-5,11-di-m-tolyl-5,11-dihydroindolo[3,2-b]carbazole, (11) 2,8-dimethyl-5,11-di-1-naphthyl-5,11-dihydroindolo[3,2-b]carbazole, (12) 2,8,5,11-tetramethyl-5,11-dihydroindolo[3,2-b]carbazole, (13) 5,11-dicyclohexyl-5,11-dihydroindolo[3,2-b]carbazole, (14) 15,11-dicyclohexyl-2,8-dimethyl-5,11-dihydroindolo[3,2-b]carbazole, (15) dibenzo[bl]-5,11-diphenyl-5,11-dihydroindolo[3,2-b]carbazole, (16) 5,7-di-m-tolyl-5,7-dihydroindolo[2,3-b] carbazole, (17) 5,7-di-1-naphthyl-5,7-dihydroindolo[2,3-b]carbazole, (18) 5,8-di-m-tolyl-5,8-dihydroindolo[2,3-c]carbazole, (19) 5,8-bis-(3,4-dimethylphenyl)-5,8-dihydroindolo[2,3-c]carbazole, (20) 5,8-di-1-naphthyl-5,8-dihydroindolo[2,3-c]carbazole, (21) 5,12-di-m-tolyl-5,12-dihydroindolo[3,2-c]carbazole, (23) 5,12-di-1-naphthyl-5,12-dihydroindolo[3,2-c]carbazole, (24) 5,12-di-1-naphthyl-5,12-dihydroindolo[3,2-a]carbazole, and the like, and of the following formulas: Similarly, the electron transporting layer 5 may be of a number of different convenient forms of, for example, a single layer, a dual layer, and the like. Any suitable electron transport compounds may be utilized in this zone. Examples of useful electron transport compounds include fused ring luminescent materials, such as anthracene, phenathrecene, pyrene, perylene, and the like as illustrated in U.S. -A- 3,172,862; butadienes such as 1,4-diphenylbutadiene and tetraphenylbutadiene, and stilbenes, and the like as illustrated in U.S. -A- 4,356,429 and US-A- 5,516,577; optical brightness such as those disclosed by U.S -A- 4,539,507. Preferred electron transport materials are metal chelates of 8-hydroxyquinoline as disclosed in U.S.-A- Patents 4,539,507; US-A- 5,151,629, and US-A-5,150,006, Illustrative examples of the metal chelates include tris(8-hydroxyquinolinate)aluminum (AlQ3), tris(8-hydroxyquinolinate)gallium, bis(8-hydroxyquinolinate)magnesium, bis(8-hydroxyquinolinate)zinc, tris(5-methyl-8-hydroxyquinolinate)aluminum, tris(7-propyl-8-quinolinolato) aluminum, bis[benzo{f}-8-quinolinate]zinc, bis(10-hydroxybenzo[h] quinolinate)beryllium, bis(2-methylquinolinolato) aluminum(III)-µ-oxo-bis(2-methyl-8-quinolinolato)aluminum(III). bis(2-methyl-8-quinolinolato) (phenolato)aluminum, bis(2-methyl-8-quinolinolato) (para-phenylphenolato) aluminum, bis(2-methyl-8-quinolinolato) (2-naphthalolato)aluminum, and the like. Another class of preferred electron transport materials are the metal chelates disclosed in U.S. Serial No. 829,398, and represented by the following formula L n -M +n wherein M represents a metal, n is a number of, for example, from 1 to 3, and L is a ligand as represented by Formula (VIII) wherein Ar is an aryl group containing, for example, 6 to 30 carbon atoms or an aromatic heterocyclic group, such as for example pyridyl, quinolyl, thienyl and the like; X is selected from the group consisting of oxygen, sulfur, and selenium; N is nitrogen, O is oxygen, and Z is an aromatic component, such as for example 1,2-phenylene, 1,2-naphthylene, 2,3-naphthylene, 3,4-pyridinediyl, 3,4-quinolinediyl, the substituted analogs thereof with the substituents being preferably alkyl containing 1 to 5 carbon atoms, phenyl or aryl with a substituent of halogen, alkyl or alkoxy groups containing 1 to 5 carbons, halogen, alkoxy groups containing 1 to 3 carbon atoms, a carboxy group, a cyano group, and the like. The metal ion of Formula (VII) may be monovalent, divalent, or trivalent Illustrative examples of metal ions include those which are capable of forming a stable chelate compound with the ligand, such as for example lithium, sodium, beryllium, magnesium, zinc, and the like, with the preferred metal ions being beryllium and zinc. Illustrative examples of metal chelate compounds (VII) include bis[2-(2-hydroxyphenyl)-5-phenyl-1,3,4-oxadiazolato]zinc; bis[2-(2-hydroxyphenyl)-5-phenyl-1,3,4-oxadiazolato] beryllium; bis[2-(2-hydroxyphenyl)-5-(1-naphthyl)-1,3,4-oxadiazolato]zinc; bis[2-(2-hydroxyphenyl)-5-(1-naphthyl)-1,3,4-oxadiazolato]beryllium; bis[5-biphenyl-2-(2-hydroxyphenyl)-1,3,4-oxadiazolato]zinc; bis[5-biphenyi-2-(2-hydroxyphenyl)-1,3,4-oxadiazolato]beryllium; bis(2-hydroxyphenyl)-5-phenyl-1,3,4-oxadiazolato]lithium; bis[2-(2-hydroxyphenyl)-5-p-tolyl-1,3,4-oxadiazolato]zinc; bis[2-(2-hydroxyphenyl)-5-p-tolyl-1,3,4-oxadiazolato]beryllium; bis[5-(p-tert-butylphenyl)-2-(2-hydroxyphenyl)-1,3,4-oxadiazolato]zinc; bis[5-(p-tert-butylphenyl)-2-(2-hydroxyphenyl)-1,3,4-oxadiazolato]beryllium; bis[2-(2-hydroxyphenyl)-5-(3-fluorophenyl)-1,3,4-oxadiazolato]zinc; bis[2-(2-hydroxyphenyl)-5-(4-fluorophenyl)-1,3,4-oxadiazolato]zinc; bis[2-(2-hydroxyphenyl)-5-(4-fluorophenyl)-1,3,4-oxadiazolato]beryllium; bis[5-(4-chlorophenyl)-2-(2-hydroxyphenyl)-1,3,4-oxadiazolato]zinc; bis[2-(2-hydroxyphenyl)-5-(4-methoxyphenyl)-1,3,4-oxadiazolato]zinc; bis[2-(2-hydroxy-4-methylphenyl)-5-phenyl-1,3,4-oxadiazolato]zinc; bis[2-α-(2-hydroxynaphthyl)-5-phenyl-1,3,4-oxadiazolato]zinc; bis[2-(2-hydroxyphenyl)-5-p-pyridyl-1,3,4-oxadiazolato]zinc; bis[2-(2-hydroxyphenyl)-5-p-pyridyl-1,3,4-oxadiazolato]beryllium; bis[2-(2-hydroxyphenyl)-5-(2-thiophenyl)-1,3,4-oxadiazolato]zinc; bis[2-(2-hydroxyphenyl)-5-phenyl-1,3,4-thiadiazolato]zinc; bis[2-(2-hydroxyphenyl)-5-phenyl-1,3,4-thiadiazolato]beryllium; bis[2-(2-hydroxyphenyl)-5-(1-naphthyl)-1,3,4-thiadiazolato]zinc; bis[2-(2-hydroxyphenyl)-5-(1-naphthyl)-1,3,4-thiadiazolato]beryllium, and the like. In embodiments of the present invention, the total thickness of the luminescent medium, which includes the hole transporting layer 4 and the electron transporting zone 5, is preferably less than 1 micron to, for example, maintain a current density conducive to efficient light emission under a relatively low applied voltage across the electrodes. Suitable thickness of the hole transporting zone can range from 50 to 2,000 Å, with the preferred thickness being from 400 to 1,000 Å. Similarly, the thickness of the electron transporting zone can range from 50 to 2,000 A, with the preferred thickness being from 400 to 1,000 Å. Each of the layers between the anode and cathode, such as the hole transport and electron transport layers, can be of various suitable thickness, such as from 50 to 125 nanometers. The cathode 6 can be comprised of any suitable metal, Including high, for example from 4.0 eV to 6.0 eV, or low work function metals, such as metals with, for example, an eV of from 2.5 eV to 4.0 eV (electron volts). The cathode can be derived from a combination of a low work function metal (less than about 4 eV) and at least one other metal. Effective proportions of the low work function metal to the second or other metal are from less than 0.1 percent to 99.9 percent by weight Illustrative examples of low work function metals include alkaline metals such as lithium or sodium, Group 2A or alkaline earth metals such as beryllium, magnesium, calcium, or barium, and Group III metals including rare earth metals and the actinide group metals such as scandium, yettrium, lanthanum, cerium, europium, terbium, or actinium. Lithium, magnesium and calcium are the preferred low work function metals in embodiments of the present invention. The thickness of cathode 6 ranges from, for example, 10 to 5,000 A. The Mg:Ag cathodes, reference U.S. -A- 4,885,211, constitute one preferred cathode. Another preferred cathode construction is described in U.S. Patent 5,429,884, wherein the cathodes are formed from lithium alloys with other high work function metals such as aluminum and indium. Both anode 3 and cathode 6 of the EL devices of the present invention can be of any convenient forms. A thin conductive layer can be coated onto a light transmissive substrate, for example a transparent or substantially transparent glass plate or plastic film. The EL device can include a light transmissive anode 3 formed from tin oxide or indium tin oxide coated on a glass plate. Also, very thin, for example less than about, or equal to 200 Å, light-transparent metallic anodes can be used, such as gold, palladium, and the like. In addition, transparent or semitransparent thin layers, such as 40 to 100 nanometers, of conductive carbon or conjugated polymers, such as polyaniline, polypyrrole, and the like, can be selected as anodes. Any suitable light transmissive polymeric film can be employed as the substrate. Additional suitable forms of the anode 3 and cathode 6 are illustrated by U.S. -A-4,885,211. The indolocarbazole hole transport compounds can be prepared by various suitable methods, for example they can be prepared by Ullmann condensation of the corresponding dihydroindolocarbazole precursors selected from those represented by Formulas (Ib) through (VIb) with aryl halide in the presence of a copper catalyst, especially a ligand copper catalyst as illustrated in copending applications U.S. Serial No. 791,694, U.S. Serial No. 791,696, U.S. Serial No. 790,669; and U.S. -A- 5,538,829; US-A- 5,648,542; US-A- 5,654,482 and US-A-5,648,539. Specific examples of dihydroindolocarbazoles, which can be readily obtained by known literature processes, are 5,11-dihydroindolo[3,2-b]carbazole, 5,7-dihydroindolo[2,3-b]carbazole, 5,12-dihydroindolo[3,2-c]carbazole, 5,10-dihydroindolo[3,2-a]carbazole, 11,12-dihydroindolo[2,3-a]carbazole, and the like. A typical process for one of the dihydroindolocarbazole derivatives, 5,11-dihydroindolo[3,2-b]carbazole, is described in Example I. wherein R and R' are independently selected from the group consisting of hydrogen atom, halogen atom, alkyl, alkoxyl, and aryl; m and n are numbers of 0 to 4; R 3 and R 4 are hydrogen, alkyl, alkoxy, aryl, or halogen, and p is a number of from 1 to 3. Illustrative examples of aryl halides that can be utilized for the Ullmann condensation are iodobenzene, 3-iodotoluene, 4-iodotoluene, 4-iodo-1,2-xylene, 1-iodonaphthalene, 2-iodonaphthalene, 4-iodobiphenyl, 4-dodo-4'-(3-methyldiphenylamino)-1,1'-biphenyl, 4-dodo-4'-(diphenyl amino)-1,1'-biphenyl, N,N-diphenyl-4-iodoaniline, N-phenyl-N-3-tolyl-4-iodoaniline, and the like. The Ullmann condensation is generally accomplished in an inert solvent, such as dodecane, tridecane, xylene, sulfolane, high boiling petroleum ethers with boiling point of, for example, over 150°C, and the like, at a reaction temperature ranging from 90°C to 300°C, and preferably from 150°C to 250°C. Copper catalysts suitable for Ullmann condensation, including copper powder, copper (I) oxide, copper (I) chloride, copper (II) sulfate, copper (II) acetate, and the like, and the ligand copper catalysts of the copending applications and patents mentioned herein, may be selected for the process of the present invention. An effective molar ratio of the copper catalyst to the dihydroindolocarbazole compound ranges, for example, from 0.01 to 0.5. The condensation reaction can be accelerated with a base, such as for example an alkaline metal hydroxide or carbonate including potassium hydroxide, potassium carbonate, sodium hydroxide, and the like. After the condensation, the reaction mixture is cooled down to about room temperature, and the product is isolated by known separation techniques, such as for example by filtration and chromatography. The product is generally characterized by known analytical techniques, such as IR and NMR. The substituents, such as for example R 3 and R 4 , can be positioned at various different appropriate locations on the aromatic componentns, like the benzene ring. The following Examples are provided to further define various species of the present invention, it being noted that these Examples are intended to illustrate and not limit the scope of the present invention. Comparative Examples and data are also provided. EXAMPLE I Synthesis of 5,11-di-m-tolyl-5,11-dihydroindolo[3,2-b]carbazole (1): A 200 milliliter 3-necked round bottom flask equipped with a mechanical stirrer, reflux condenser, and argon inlet was purged with argon and then charged with 5,11-dihydroindolo[3,2-b]carbazole (5.1 grams, 0.02 mol), 3-iodotoluene (8.69 grams, 0.04 mol), copper sulfate pentahydrate (0.25 gram, 1.0 mmol), potassium carbonate (5.52 grams, 0.04 mol), and n-tridecane (5.0 milliliters). Under an argon atmosphere, the reaction mixture was heated to 250°C with a heating mantle and allowed to proceed at that temperature until chromatographic analysis indicated that the reaction was complete after approximately 6 hours. The heating mantle was removed and the mixture was cooled to 100°C, and 100 milliliters of toluene and 15 milliliters of water were then added with vigorous stirring. The resulting two phase mixture was transferred into a separatory funnel and the layers separated. The organic phase, which contains the desired product and solvent mixture, was washed with water and treated under argon with 25 grams of alumina. After the alumina was filtered off, the organic phase was evaporated to remove most of the toluene. The above product was obtained by recrystallization of the residue from cyclohexane. Yield: 6.8 grams. IR (Kbr): 1,604, 1,588, 1,490, 1,475, 1,450, 1,321, 1,201, 1,153, 760, 745, 701 cm -1 . 1 H-NMR (CDCl 3 ): δ 2.51 (s), 7.18∼7.59 (m), 8.05 (s), 8.12 (d, J = 8.5 Hz). EXAMPLE II Synthesis of 5,11-di-bis(3,4-dimethylphenyl)-m-5,11-dihydroindolo [3,2-b]-carbazole (2): A 200 milliliter 3-necked round bottom flask equipped with a mechanical stirrer, reflux condenser, and argon inlet was purged with argon and then charged with 5,11-dihydroindolo[3,2-b]carbazole (5.1 grams, 0.02 mol), 3-iodotoluene (9.28 grams, 0.04 mol), copper sulfate pentahydrate (0.25 gram, 1.0 mmol), potassium carbonate (5.52 grams, 0.04 mol), and n-tridecane (5.0 milliliters). Under an argon atmosphere, the reaction mixture was heated to 250°C with a heating mantle and allowed to proceed at that temperature until chromatographic analysis indicated that the reaction was complete after approximately 6 hours. The heating mantle was removed and the mixture was cooled to 100°C, and 100 milliliters of toluene and 15 milliliters of water were then added with vigorous stirring. The resulting two phase mixture was transferred into a separatory funnel and the layers separated. The organic phase, which contains the desired product and the solvent mixture, was washed with water and treated under argon with 25 grams of alumina. After the alumina was filtered off, the organic phase was evaporated to remove most of the toluene. The product was then obtained by recrystallization of the aforementioned residue from cyclohexane. Yield: 7.5 grams. IR (Kbr): 1,614, 1,605, 1,511, 1,458, 1,445, 1,324, 1,241, 1,183, 851, 747, 743 cm -1 . 1 H-NMR (CDCl 3 ):, δ 2.42 (s), 2.44 (s), 7.14∼7.47 (m), 8.03 (s), 8.12 (d, J,=,8.5 Hz). EXAMPLE III Synthesis of 5,11-di-1-naphthyl-5,11-dihydroindolo[3,2-b]carbazole (3): A 200 milliliter 3-necked round bottom flask equipped with a mechanical stirrer, reflux condenser, and argon inlet was purged with argon and then charged with 5,11-dihydroindolo[3,2-b]carbazole (5.1 grams, 0.02 mol), 1-iodonaphthalene (10.16 grams, 0.04 mol), copper sulfate pentahydrate (0.25 gram, 1.0 mmol), potassium carbonate (5.52 grams, 0.04 mol), and n-tridecane (5.0 milliliters). Under an argon atmosphere, the reaction mixture was heated to 250°C with a heating mantle and allowed to proceed at this temperature to completion in about 6 hours. The reaction mixture was cooled to 100°C, and 100 milliliters of toluene and 15 milliliters of water were then added with vigorous stirring for 30 minutes. The resulting two phase mixture was transferred into a separatory funnel and the layers separated. The organic phase, which contains the desired product and the solvent mixture, were washed with water, treated under argon with 25 grams of alumina, and filtered. The filtrate was evaporated and the residue was recrystallized from toluene to provide 2.5 grams of pure, about 99.5 percent, 5,11-di-1-naphthyl-5,11-dihydroindolo[3,2-b]carbazole (3). EXAMPLE IV Illustrative organic EL devices were prepared In the following manner 1. An indium tin oxide (ITO, 50 nanometers) coated glass (1.0 millimeter) was cleaned with a commercial detergent, rinsed with deionized water and dried in a vacuum oven at 60°C for 1 hour. Immediately before use, the glass was treated with UV ozone for 0.5 hour. 2. The above ITO substrate 1. was placed in a vacuum deposition chamber. The deposition rate and layer thickness were controlled by an Inficon Model IC/5 controller. Under a pressure of about 5 x 10 -8 torr a dihydroindolo[3,2-b]carbazole compound of Examples I, II, or III, was evaporated from an electrically heated tantalum boat to deposit an 80 nanometer hole transporting layer on the ITO glass. The deposition rate of the indolocarbazole compound was controlled at 0.6 nanometer/second. 3. Onto the dihydroindolo[3,2-b]carbazole layer 2. was deposited tris(8-hydroxyquinolinate)aluminum at an evaporation rate of 0.6 nanometer/second to form an 80 nanometer electron transporting layer which can also function as a luminescent zone. 4. A 100 nanometer magnesium cathode silver alloy was deposited at a total deposition rate of 0.5 nanometer/second onto the electron transporting layer 3 by simultaneous evaporation from two independently controlled tantalum boats containing. Mg and Ag, respectively. The typical. composition was 9:1 In atomic ratio of Mg to Ag. Finally, a 200 nanometer silver layer was overcoated on the Mg:Ag cathode for the purpose of protecting the reactive Mg from ambient moisture. The devices as prepared above were retained in a dry box under a nitrogen atmosphere. Their performance was assessed by measuring the current-voltage characteristics and light output under a direct current measurement. The current-voltage characteristics were determined with a Keithley Model 238 High Current Source Measure Unit The ITO electrode was connected to the positive terminal of the current source. At the same time, the light output from the device was monitored by a silicon photodiode. The devices were evaluated under a constant current density of 25 mA/cm 2 . The device's operation life was assessed by measuring the time elapsed to reduce the light intensity of the device to half of its original value. The initial light intensity (L 0 ), Initial operation voltages (V 0 ), and operation life of the devices utilizing dihydroindolo[3,2-b]carbazole compounds are summarized in the following table: Compound No. L 0 (cd/m 2 ) V 0 (V) Operation Life (hours) 1 560 9.5 250 2 580 9.2 200 3 575 9.8 300 These results demonstrate that a sustained high level of light output can be achieved in the EL devices utilizing the indolocarbazole hole transport component. Furthermore, these devices displayed no change in their current-light intensity characteristics even after they were subjected to a temperature of 60°C for 72 hours. COMPARATIVE EXAMPLES A controlled organic EL device was prepared in accordance with the procedure of Example V except that N,N'-bis(3-methylphenyl)-N,N'-diphenyl-4,4'-diaminobiphenyl, a triphenylamine based hole transport molecule commonly selected for a number of prior art EL devices, was utilized in place of 5,11-di-m-tolyl-5,11-dihydroindolo[3,2-b]carbazole. The performance characteristics of the device were evaluated in a similar manner to the above EL Example. The device provided an initial light intensity of 570 cd/m 2 at an operating voltage of 9.5 volts as measured under a constant current density of 25 mA/cm 2 . The light intensity degraded rapidly, and registered a 50 percent reduction after 90 hours of continuous operation. Furthermore, this device displayed substantial change in its current-light intensity characteristics after it was subjected to a temperature of 60°C for 72 hours. Another controlled organic EL device was also prepared in accordance with the procedure of Example V except that 1,1-bis(4-di-tolylaminophenyl)cyclohexane was utilized in place of 5,11-di-m-tolyl-5,11-dihydroindolo[3,2-b]carbazole. The performance characteristics of the device were evaluated in a similar manner. The device provided an initial light Intensity of 450 cd/m 2 at an operating voltage of 11.5 volts. The light intensity degraded rapidly, and registered a 50 percent reduction after 60 hours of continuous operation.

Claims: An organic electroluminescent device member comprised of a charge transport component of an indolocarbazole represented by Formulas (I), (II), (III), (IV), (V), or (VI); or optionally mixtures thereof wherein R and R' are independently selected from the group consisting of a hydrogen atom, halogen atom, alkyl, alkoxyl, and aryl; m and n are numbers of 0 to 4; R 1 and R 2 are independently selected from the group consisting of alkyl, aryl, and vinyl; R 3 and R 4 are independently selected from the group consisting of a hydrogen atom, halogen atom, alkyl, alkoxy, and aryl, and p is a number of from 1 to 3. The member in accordance with claim 1 wherein said indolocarbazole is 5,11-di-m-tolyl-5,11-dihydroindolo[3,2-b]carbazole, 5,11-bis(3,4-dimethylphenyl)-5,11-dihydroindolo[3,2-b]carbazole, 5,11-di-1-naphthyl-5,11-dihydroindolo[3,2-b]carbazole, 5,11-bis(3-methoxyphenyl)-5,11-dihydroindolo[3,2-b]carbazole, 5,11-bis(1,1'-biphenyl-4-yl)-5,11-dihydroindolo[3,2-b]carbazole, 5,11-di-2-naphthyl-5,11-dihydroindolo[3,2-b] carbazole, or 2,8-dimethyl-5,11-di-1-naphthyl-5,11-dihydroindolo[3,2-b] carbazole. The member in accordance with claim 1 or 2 and including an anode and a cathode, and an organic electroluminescent zone situated between the anode and cathode, and wherein said organic electroluminescent zone comprises a hole transporting indolocarbazole of (I), (II), (III), (IV), (V), or (VI). The member in accordance with any of claims 1 to 3 wherein aryl contains from 6 to 30 carbons, wherein R 1 and R 2 are aryl groups; R and R' are hydrogen atoms or methyl groups; R 3 and R 4 are hydrogen atoms; and p is 1. The member in accordance with any of claims 1 to 4 wherein said indolocarbazole compound is selected from the group consisting of 5,11-di-m-tolyl-5,11-dihydroindolo[3,2-b]carbazole, 5,11-bis(3,4-dimethylphenyl)-5,11-dihydroindolo[3,2-b]carbazole, 5,11-di-1-naphthyl-5,11-dihydroindolo [3,2-b]carbazole, 5,11-bis(3-methoxyphenyl)-5,11-dihydroindolo[3,2-b]carbazole, 5,11-bis(1,1'-biphenyl-4-yl)-5,11-dihydroindolo[3,2-b]carbazole, 5,11-di-2-naphthyl-5,11-dihydroindolo[3,2-b]carbazole, 2,8-dimethyl-5,11-di-1-naphthyl-5,11-dihydroindolo[3,2-b]carbazole, 5,7-di-m-tolyl-5,7-dihydroindolo[2,3-b]carbazole, 5,7-di-1-naphthyl-5,7-dihydroindolo[2,3-b] carbazole, 5,8-di-m-tolyl-5,8-dihydroindolo[2,3-c]carbazole, 5,8-bis-(3,4-dimethylphenyl)-5,8-dihydroindolo[2,3-c]carbazole, and 5,12-di-1-naphthyl-5,12-dihydroindolo[3,2-a]carbazole. The member in accordance with any of claims 1 to 5 wherein said indolocarbazole compound is selected from a group consisting of 5,11-di-m-tolyl-5,11-dihydroindolo[3,2-b]carbazole, 5,11-bis(3,4-dimethylphenyl)-5,11-dihydroindolo[3,2-b]carbazole, 5,11-di-1-naphthyl-5,11-dihydroindolo[3,2-b]carbazole, 5,11-bis(3-methoxyphenyl)-5,11-dihydroindolo[3,2-b]carbazole, 5,11-bis(1,1'-biphenyl-4-yl)-5,11-dihydroindolo[3,2-b]carbazole, 5,11-di-2-naphthyl-5,11-dihydroindolo[3,2-b] carbazole, and 2,8-dimethyl-5,11-di-1-naphthyl-5,11-dihydroindolo[3,2-b] carbazole, and said member includes a charge injecting layer and thereover an electron transport layer and an electron injector layer. The member in accordance with any of claims 1 to 6 further including a supporting substrate, an anode, a hole transporting layer, an electron transporting layer, and a cathode, wherein said anode is comprised of a layer of indium tin oxide with a thickness ranging from 30 nanometers to 100 nanometers, wherein said hole transport layer contains at least one of said indolocarbazole compounds with a thickness ranging from 10 nanometers to 100 nanometers; said electron transporting layer is comprised of a layer of a metal chelate compound with a thickness ranging from 10 nanometers to 100 nanometers; and said cathode is a magnesium/silver alloy or a lithium/aluminum alloy, and which cathode Is of a thickness ranging from 10 nanometers to 200 nanometers. The member in accordance with any of claims 1 to 7 further including a substrate, an anode, a cathode, and situated between the anode and cathode said charge transporting indolocarbazole layer, and thereover an electron transport layer. The member in accordance with any of claims 1 to 7 further including a substrate, an anode, a cathode, and situated between the anode and cathode a hole injector layer, said charge transporting indolocarbazole layer, and thereover an electron transport layer, and an electron injector layer. The member in accordance with claim 9 wherein the anode is indium tin oxide with a thickness ranging from 30 nanometers to 100 nanometers, the cathode is a magnesium silver alloy, the hole injector layer is comprised of a porphyrin compound with a thickness ranging from 5 nanometers to 50 nanometers, the charge transporting layer is a hole transporting layer comprised of said indolocarbazole compound with a thickness ranging from 10 nanometers to 80 nanometers, the electron transport is comprised of a metal chelate compound of 8-hydroxyquinoline with a. thickness ranging from 0 nanometers to 80 nanometers, and the electron injector is comprised of a metal chelate compound of 8-quinolinethiol with a thickness ranging from 5 nanometers to 50 nanometers. An organic electroluminescent device member comprised of a hole transport component of an indolocarbazole represented by (I), (II), (III), (IV), (V), or (VI) wherein R and R' are independently selected from the group consisting of hydrogen, halogen, alkyl, alkoxyl, and aryl; R 1 and R 2 are independently selected from the group consisting of alkyl, and aryl; R 3 and R 4 are independently selected from the group consisting of hydrogen, halogen, alkyl, alkoxy, and aryl, n and m are numbers of 0 to 4 and p is a number from 1 to 3.

Inventors: HOR AH-MEE, HU NAN-XING, ONG BENG S, POPOVIC ZORAN D, XIE SHUAN, HOR, AH-MEE, HU, NAN-XING, ONG, BENG S., POPOVIC, ZORAN D., XIE, SHUAN
Applicants: XEROX CORP, XEROX CORPORATION
Application year: 1998
Main classification: C09K11
IPC codes: H05B33, H01L51, C09K11