A method for the heat-treatment of ZnSe crystal

Abstract: An object of the present invention is to provide a method for the heat-treatment of ZnSe crystal whereby a deterioration in crystallinity can be prevented and a crystal having a low resistivity, without the occurrence of precipitates, can be produced. The feature of the present invention comprises a method for the heat-treatment of a ZnSe crystal comprising subjecting a ZnSe crystal grown by a chemical vapor transport method, using iodine as a transport agent, to a heat-treatment in a Zn vapor atmosphere and controlling the cooling rate after the heat-treatment to in the range of from 10 to 200 °C/min.

Description: The present invention relates to a method of decreasing the resistivity of a ZnSe crystal grown by a chemical vapor transport (CVT) method, using iodine as a transport agent, the method comprising subjecting a ZnSe crystal to a heat-treatment in a Zn vapor atmosphere. ZnSe crystal has a high resistivity even when it contains iodine as an n-type dopant, owing to self-compensation by Zn vacancies, unless the ZnSe crystal is subjected to a heat-treatment after being grown. A ZnSe crystal having a lower resistivity may be produced by activating iodine through a heat-treatment in Zn vapor at a high temperature. In this method, however, if the cooling rate after the heat-treatment is low, the vapor pressure of Zn is reduced, due to lowering of the temperature, and the number of Zn holes is increased, thereby increasing the resistivity. Thus, a rapid cooling method has generally been employed after the heat-treatment. For example, it has been reported in "J. of Electronic Materials", Vol. 8, No. 5 (1979), p 619-633 that ZnSe crystal, grown by a chemical vapor transport method using iodine as a transport agent, and Zn can be arranged in two quartz ampoules, one of which is heat-treated at 800°C for 13 hours and the other of which is heat-treated at 830°C for 24 hours. Both of the ampoules are then charged in an oil at 25°C and rapidly cooled to obtain ZnSe crystals each having a specific resistivity of 0.12 Ωcm and 0.08 Ωcm. After the treatment, however, when the ZnSe crystal is rapidly cooled in oil, the crystallinity thereof is deteriorated by, for example, the production of dislocations, and cracks may occur in the crystal. This is probably because the temperature gradient in the crystal is increased as the temperature of the crystal is rapidly reduced, and thermal stresses are generated, leading to a deterioration in the crystallinity. The inventors have found that after the heat-treatment, when the ZnSe crystal is gradually cooled at a cooling rate of 1 °C/min, the formation of cracks can be prevented, but precipitates often then occur in the crystal and, again, a ZnSe crystal having the desired crystallinity cannot be obtained. It is an object of the present invention to provide a method for the heat-treatment of a ZnSe crystal whereby the above described disadvantages can be addressed and a deterioration in the crystallinity can be prevented, thus resulting in a crystal having a low resistivity without the occurrence of precipitates in the crystal. It is another object of the present invention to provide a method of decreasing the resistivity of ZnSe crystal grown by a chemical vapor transport method, using iodine as a transport agent, wherein the method comprises subjecting the ZnSe crystal to a heat treatment in a Zn vapor atmosphere. These objects can be attained by a method for the heat treatment of ZnSe comprising subjecting ZnSe crystal grown by a chemical vapor transport method using iodine as a transport agent to a heat treatment in a Zn vapor atmosphere and controlling a cooling rate after the heat treatment in 10 to 200 °C/min. The present invention will now be described further, by way of example, with reference to the accompanying drawing , in which:- Fig. 1 is a schematic view of an apparatus for the practice of a method for the heat treatment according to the present invention. The inventors have made various efforts to develop a method of decreasing the resistivity of ZnSe crystal grown by a chemical vapor transport method using iodine as a transport agent, and consequently have found that a heat-treatment of the ZnSe crystal and control of a cooling rate after the heat-treatment are effective for this purpose. The present invention is based on this finding. Accordingly, the present invention provides a method for the heat-treatment of ZnSe comprising subjecting ZnSe crystal grown by a chemical vapor transport method using iodine as a transport agent to a heat treatment in a Zn vapor atmosphere and controlling a cooling rate after the heat treatment in 10 to 200 °C/min. According to the method of the present invention, ZnSe crystal grown by a chemical vapor transport method using iodine as a transport agent, that is, ZnSe crystal having a high resistivity because of self-compensation by Zn vacancies is subjected to a heat treatment in Zn vapor, thereby causing this crystal to have low resistivity without deterioration of crystallinity thereof. It is required to control the cooling rate after the heat treatment in a range of 10 to 200 °C/min. If the cooling rate is less than 10 °C/min, the specific resistivity cannot sufficiently be decreased and precipitates occur in the crystal, while if more than 200 °C/min, cracks occur in the crystal and dislocation density is increased to deteriorate the crystallinity. This is not favorable. In the heat treatment of the present- invention, ZnSe crystal as an object of the heat treatment is preferably heated at 800 to 1100 °C and a Zn pellet is heated at 750 to 1100 °C, in such a manner that a temperature gradient between them be controlled in 0 to 50 °C, for a period of time of 50 to 200 hours. Fig. 1 is a schematic view of an apparatus for carrying out a method for the heat treatment according to the present invention, in which a ZnSe crystal 1 grown by a chemical vapor transport method using iodine as a transport agent (hereinafter referred to as CVT crystal) is supported by quartz parts 3 in a quartz ampoule 4 and Zn pellet 2 is charged in the bottom of the quartz ampoule 4, follwed by closing the quartz ampoule 4 and charging in a heat treatment furnace 5 maintained at predetermined heat treatment conditions. The present invention will be illustrated by the following Examples in detail without limiting the same. Examples A CVT crystal was cut in seven samples each having a size of 5 x 5 x 1 mm 3 , each sample 1 was supported by a quartz part 3 and arranged with etched Zn pellet 2 in seven quartz ampoules 4, as shown in Fig. 1. The quartz ampoule 4 was evacuated in a pressure of 3 x 10 -7 Torr and sealed. This quartz ampoule was charged in a heat treatment furnace 5, the crystal part was heated at 1000 °C and the bottom part having the Zn pellet arranged was heated at 980 °C, the assembly being thus maintained and heat treated for 100 hours. Six of the seven quartz ampoules were maintained in the heat treatment furnace and cooled to room temperature in such a manner that the cooling rates at the crystal parts were respectively adjusted to 1 °C/min, 10 °C/min, 20 °C/min, 100 °C/min, 200 °C/min and 300 °C/min. The other quartz ampoule was taken out of the heat treatment furnace and subjected to rapid cooling by charging in a sufficient amount of water at room temperature. The resulting ZnSe crystals were taken out of the quartz ampoules and were subjected to investigation of specific resistivity, presence or absence of precipitates in the crystals and increase of dislocation densities as compared with before the heat treatment. The specific resistivity was measured by the Hall measurements, the precipitate in the crystal was observed by means of Normarski microscope and the dislocation density was investigated by measurement of an etch pit density when etching with a bromine-methanol solution. In the ZnSe crystal obtained at a cooling rate of 1 °C/min, there were found linear precipitates with a high density in the whole crystal and no siginificant increase of the dislocation density. The specific resistivity was in a range of 0.07 to 0.08 Ωcm. In the ZnSe crystals obtained at cooling rates of 10 to 200 °C/min, there were found no precipitates in all the samples, nor significant increase of the dislocation densities. The specific resistivity could be lowered to a range of 0.04 to 0.05 Ωcm. The ZnSe crystal obtained at a cooling rates of 300 °C/min was in the form of finely broken pieces and had a number of cracks and increased dislocation density. The specific resistivity could not be measured because of finely broken pieces of the crystal. When the quartz ampoule was taken out of the heat treatment furnace and subjected to rapid cooling by charging it in water, the quartz ampoule was cracked and the crystal was also pulverized to give a size of about 1 x 1 x 1 mm3. In the crystal, there were found no precipitates, but found a number of cracks and an increased dislocation density of from 10 4 cm -2 to at least 10 6 cm -2 . The specific resistivity could not be measured because of finely broken pieces of the crystal. Advantages of the Invention According to the present invention, a low resistivity ZnSe crystal can be obtained without occurrence of precipitates and deterioration of the crysstallinity by employing the above described constructions.

Claims: A method for the heat-treatment of ZnSe comprising subjecting a ZnSe crystal grown by a chemical vapor transport method using iodine as a transport agent to a heat-treatment in a Zn vapor atmosphere and controlling the cooling rate after the heat-treatment to in the range of from 10 to 200 °C/min. A method for the heat-treatment of ZnSe crystal as claimed in claim 1, wherein the heat-treatment is carried out by heating the ZnSe crystal at a temperature of from 800 to 1100°C. A method for the heat-treatment of ZnSe crystal as claimed in claim 1 or claim 2, wherein the heat-treatment is carried out by heating the Zn vapor at a temperature of from 750 to 1100°C. A method for the heat-treatment of ZnSe as claimed in any one of claims 1 to 3, wherein during the heat-treatment a temperature difference of from 0 to 50°C is maintained between the ZnSe crystal and the Zn vapor. A method for the heat-treatment of ZnSe as claimed in any one of claims 1 to 4, wherein the heat-treatment is carried our for from 50 to 200 hours.

Inventors: FUJIWARA SHINSUKE, HIROTA RYU, FUJIWARA, SHINSUKE, HIROTA, RYU
Applicants: SUMITOMO ELECTRIC INDUSTRIES, SUMITOMO ELECTRIC INDUSTRIES, LTD.
Application year: 1997
Main classification: C30B33
IPC codes: C30B25, C30B33, C30B31, C30B29