Aqueous polyurea dispersions and their use for preparing coatings with excellent hydrolytic and thermal stability

Abstract: The present invention relates to aqueous dispersions of polyureas containing hydantoin groups (calculated as C 3 N 2 O 2 , MW 96) in an amount of 1 to 40% by weight, based on resin solids. The present invention also relates to the use of these dispersions for preparing coatings having excellent hydrolytic and thermal stability.

Description: BACKGROUND OF THE INVENTION Field of the Invention The present invention relates to aqueous polyurea dispersions containing hydantoin groups and to their use for the production of coatings having excellent hydrolytic and thermal stability. Description of the Prior Art The production of linear or cross-linked aqueous polyurethane-urea dispersions is known as shown by U.S. Patents 3,479,310; 4,066,591; 4,092,286; 4,108,814; 4,237,264; and 4,238,378 which disclose linear polyurethane-ureas and U.S. Patents 3,870,684 4,203,883 and 4,408,008, which disclose cross-linked polyurethane-ureas. The polyurethane-urea dispersions are generally prepared by initially forming an NCO prepolymer by reacting a diisocyanate with a high molecular weight diol, such as a polyester, and with an anionic group-containing diol. The NCO prepolymer is then dispersed in water and chain extended with an amine chain extender to form the polyurethane-urea. The aqueous polyurethane-urea dispersions may be used for a wide range of commercial applications such as adhesives or coatings for various substrates including textile fabrics, plastic, wood, glass fibers and metals. Chemical resistance, abrasion resistance, toughness, tensile strength, elasticity and durability are among the many desirable properties of these coatings. In some cases these properties of coatings prepared from aqueous polyurethane-urea dispersions have equaled or even surpassed the performance levels of coatings obtained from solvent-based polyurethane lacquers. Regardless of the property level which may be obtained for coatings prepared from commercial polyurethane-urea dispersions, there is always a further need to increase these properties, in particular hydrolytic stability and thermal stability. Accordingly, it is an object of the present invention to improve these properties. This object may be achieved with the aqueous polyurea dispersions according to the present invention by replacing at least a portion of the polyols have previously been used to prepare aqueous polyurethane-urea dispersions with aspartate-functional prepolymers containing hydantoin groups or hydantoin group precursors. Obtaining coatings with good hydrolytic stability has always been difficult because many of the commercially available polyurethane-urea dispersions are based on polyester polyols. The polyurethanes are rendered hydrophilic by tertiary amine-neutralized acid groups, generally carboxylic acid groups. When the dispersions are subsequently cured, the tertiary amines are released and the carboxylic acid is reformed. The acid then catalyzes the hydrolytic degradation of the polyester backbone. There have been many attempts to prevent this hydrolytic degradation, e.g., by neutralizing the acid groups with alkali metals, such as sodium, that are not released during the formation of the coating (U.S. Patents 4,501,852 and 4,701,480). However, the presence of salt groups causes the resulting coatings to swell in the presence of water. It has also been proposed to replace the polyester polyols with polycarbonate polyols, but these materials significantly add to the cost of the resulting polyurethane-urea dispersions. SUMMARY OF THE INVENTION The present invention relates to aqueous dispersions of polyureas containing hydantoin groups (calculated as C 3 N 2 O 2 , MW 96) in an amount of 1 to 40% by weight, based on resin solids. The present invention also relates to the use of these dispersions for preparing coatings with excellent hydrolytic and thermal stability. DETAILED DESCRIPTION OF THE INVENTION In accordance with the present invention the term "polyurea" refers to polymers containing one or more urea groups and optionally other groups such as urethane groups. The term "stable aqueous polyurea dispersion" refers to dispersions in which the polyureas remain stably dispersed, without sedimentation, due to the presence of sufficient chemically incorporated and/or external emulsifiers. The term "aqueous polyurea dispersions," in addition to referring to stable aqueous polyurea dispersions, also refers to dispersions in which the polyureas sediment during storage, but can be redispersed prior to use. The term "hydantoin group precursor" means the reaction product of an isocyanate group with a particular secondary amino group, i.e., an aspartate, in which the reaction product can be converted into a hydantoin group, e.g., by heating. The aqueous dispersions of polyureas according to the present invention contain hydantoin groups (calculated as C 3 N 2 O 2 , MW 96) in an amount of 1 to 40% by weight, preferably 1 to 20% by weight and more preferably 3 to 20% by weight, based on resin solids. In accordance with the present invention the aqueous polyurea dispersions may be prepared by either a one-stage or a two-stage process, preferably a two-stage process, wherein an NCO prepolymer is formed in the first stage and is subsequently chain extended with an isocyanate-reactive component in the second stage either before, during or after being mixed with an aqueous medium. However, any of the known one- and two-stage processes and starting materials may be used for preparing the dispersions according to the invention with the only requirement being that the starting materials for the preparation of the polyisocyanate addition product contain an aspartate-functional prepolymer containing hydantoin groups or hydantoin group precursors. These aspartate-functional prepolymers may be used in place of at least a portion of the high molecular polyols that are conventionally used to prepare the polyurethane dispersions known in the art. Suitable polyisocyanates which may be used to prepare the polyureas are known and have a functionality of 1.8 to 6, preferably 2 to 6, more preferably 2 to 4 and most preferably 2. Examples of these polyisocyanates include monomeric polyisocyanates and polyisocyanate adducts, preferably monomeric diisocyanates represented by the formula R(NCO) 2 in which R represents an organic group obtained by removing the isocyanate groups from an organic diisocyanate having a molecular weight of from 112 to 1,000, preferably from 140 to 400. Diisocyanates preferred for the process according to the invention are those represented by the above formula in which R represents a divalent aliphatic hydrocarbon group having from 4 to 18 carbon atoms, a divalent cycloaliphatic hydrocarbon group having from 5 to 15 carbon atoms, a divalent araliphatic hydrocarbon group having from 7 to 15 carbon atoms or a divalent aromatic hydrocarbon group having 6 to 15 carbon atoms. Examples of suitable organic diisocyanates include 1,4-tetramethylene diisocyanate, 1,6-hexamethylene diisocyanate, 2,2,4-trimethyl-1,6-hexamethylene diisocyanate, 1,12-dodecamethylene diisocyanate, cyclohexane-1,3- and -1,4-diisocyanate, 1-isocyanato-2-isocyanatomethyl cyclopentane, 1-isocyanato-3-isocyanatomethyl-3,5,5-trimethylcyclohexane (isophorone diisocyanate or IPDI), bis-(4-isocyanatocyclohexyl)-methane, 1,3- and 1,4-bis-(isocyanatomethyl)-cyclohexane, bis-(4-isocyanatocyclohexyl)-methane, 2,4'-diisocyanato-dicyclohexyl methane, bis-(4-isocyanato-3-methyl-cyclohexyl)-methane, α,α,α',α'-tetramethyl-1,3- and/or -1,4-xylylene diisocyanate, 1-isocyanato-1-methyl-4(3)-isocyanatomethyl cyclohexane, 2,4- andlor 2,6-hexahydrotoluylene diisocyanate, 1,3- and/or 1,4-phenylene diisocyanate, 2,4- and/or 2,6-toluylene diisocyanate, 2,4- and/or 4,4'-diphenylmethane diisocyanate and 1,5-diisocyanato naphthalene and mixtures thereof. Polyisocyanates containing 3 or more isocyanate groups such as 4-isocyanatomethyl-1,8-octamethylene diisocyanate and aromatic polyisocyanates such as 4,4',4"-triphenylmethane triisocyanate and polyphenyl polymethylene polyiso-cyanates obtained by phosgenating aniline/formaldehyde condensates may also be used. Preferred polyisocyanates are bis-(4-isocyanatocyclohexyl)-methane, 1,6-hexamethylene diisocyanate and isophorone diisocyanate. Suitable polyisocyanate adducts are those containing isocyanurate, uretdione, biuret, urethane, allophanate, carbodiimide and/or oxadiazine-trione groups. The polyisocyanates adducts have an average functionality of 2 to 6 and an NCO content of 5 to 30% by weight and are disclosed in copending application, U.S. Serial No. 08/443,504, the disclosure of which is herein incorporated by reference. Preferred polyisocyanate adducts are the polyisocyanates containing isocyanurate groups, biuret groups and mixtures of isocyanurate groups with either allophanate or uretdione groups. Most preferably, monomeric polyisocyanates are used in accordance with the present invention instead of polyisocyanate adducts. In accordance with the present invention hydantoin groups are incorporated in the polyureas by reacting the previously described polyisocyanates with aspartate-functional prepolymers containing hydantoin groups or hydantoin group precursors. Examples of these prepolymers are described in copending application, U.S. Serial No. 08/443,504, which has previously been incorporated by reference. The prepolymers are prepared by reacting polyaspartates with an excess of monomeric polyisocyanates or polyisocyanate adducts, preferably monomeric diisocyanates (especially 1,6-hexamethylene diisocyanate). Suitable polyaspartates that may be used as starting materials for the production of the aspartate-functional polyhydantoin prepolymers according to the invention include those corresponding to the formula: wherein X represents an organic group which has a valency of n and is inert towards isocyanate groups at a temperature of 100°C or less, preferably a hydrocarbon group obtained by removing the amino groups from an aliphatic, araliphatic or cycloaliphatic polyamine, more preferably a diamine, and R, and R 2 may be the same or different and represent organic groups which are inert towards isocyanate groups at a temperature of 100°C or less, preferably alkyl groups containing 1 to 9 carbon atoms and more preferably methyl, ethyl or butyl groups, R 3 and R 4 may be the same or different and represent hydrogen or organic groups which are inert towards isocyanate groups at a temperature of 100°C or less, preferably hydrogen, and n has a value of at least 2, preferably 2 to 6, more preferably 2 to 4 and most preferably 2. These polyaspartates may be prepared by reacting optionally substituted maleic or fumaric acid esters with polyamines. Suitable optionally substituted maleic or fumaric acid esters are those corresponding to the formula R 1 OOC-CR 3 =CR 4 -COOR 2 wherein R 1 , R 2 , R 3 and R 4 are as defined above. Examples of optionally substituted maleic or fumaric acid esters suitable for use in the preparation of the polyaspartates include dimethyl, diethyl and dibutyl (e.g., di-n-butyl) esters of maleic acid and fumaric acid and the corresponding maleic or fumaric acid esters substituted by methyl in the 2- and/or 3-position. Suitable polyamines for preparing the polyaspartates include those corresponding to the formula X-(-NH 2 ) n wherein X and n are as previously defined. The polyamines include high molecular weight amines having molecular weights of 800 to about 10,000, preferably 800 to about 6,000, and low molecular weight amines having molecular weights below 800, preferably below 600. The molecular weights are number average molecular weights (M n ) and are determined by end group analysis (NH number). Examples of these polyamines are those wherein the amino groups are attached to aliphatic, cycloaliphatic, araliphatic and/or aromatic carbon atoms. Suitable low molecular polyamines include ethylene diamine, 1,2-and 1,3-propane diamine, 2-methyl-1,2-propane diamine, 2,2-dimethyl-1,3-propane diamine, 1,3- and 1,4-butane diamine, 1,3- and 1,5-pentane diamine, 2-methyl-1,5-pentane diamine, 1,6-hexane diamine, 2,5-dimethyl-2,5-hexane diamine, 2,2,4-and/or 2,4,4-trimethyl-1,6-hexane diamine, 1,7-heptane diamine, 1,8-octane diamine, 1,9-nonane diamine, triaminononane, 1,10-decane diamine, 1,11-undecane diamine, 1,12-dodecane diamine, 1-amino-3-aminomethyl-3,5,5-trimethyl cyclohexane, 2,4- and/or 2,6-hexahydrotoluylene diamine, 2,4'- and/or 4,4'-diaminodicyclohexylmethane, 3,3'-dialkyl-4,4'-diamino-dicyclohexyl methanes (such as 3,3'-dimethyl-4,4'-diamino-dicyclohexyl methane and 3,3'-diethyl-4,4'-diamino-dicyclohexyl methane), 1,3- and/or 1,4-cyclohexane diamine, 1,3-bis(methylamino)-cyclohexane, 1,8-p-menthane diamine, hydrazine, hydrazides of semicarbazido carboxylic acids, bis-hydrazides, bis-semicarbazides, phenylene diamine, 2,4- and 2,6-toluylene diamine, 2,3- and 3,4-toluylene diamine, 2,4'- and/or 4,4'-diaminodiphenyl methane, diethylene triamine, triethylene tetramine, tetraethylene pentamine, pentaethylene hexamine, N,N,N-tris-(2-amino-ethyl)-amine, N,N,N'-tris-(2-aminoethyl)-ethylene diamine, N-(2-amino-ethyl)-1,3-propane diamine, polyoxypropylene amines, tetrapropylene-pentamine, tripropylenetetramine, N,N-bis-(6-amino-hexyl)amine, N,N'-bis-(3-aminopropyl)-ethylene diamine, 2,4-bis-(4'-aminobenzyl)-aniline, higher functional polyphenylene polymethylene polyamines obtained by the aniline/formaldehyde condensation reaction, N,N,N-tris-(2-amino-ethyl)-amine, guanidine, melamine, N-(2-aminoethyl)-1,3-propane diamine, 3,3'-diaminobenzidine, polyoxypropylene amines, polyoxyethylene amines, 2,4-bis-(4'-aminobenzyl)-aniline and mixtures thereof. Also suitable are amine-terminated polyethers having the required molecular weight such as the Jeffamine resins, e.g., Jeffamine D-230 and T-403, available from Huntsman. Suitable high molecular weight polyamines include those prepared from the known polyhydroxyl compounds of polyurethane, especially the polyethers. The polyamines may be prepared by reacting the polyhydroxyl compounds with an excess of the previously described polyisocyanates to form NCO prepolymers and subsequently hydrolyzing the terminal isocyanate group to an amino group. Preferably, the polyamines are prepared by converting the terminal hydroxy groups of the polyhydroxyl compounds to amino groups, e.g., by amination. Preferred high molecular weight polyamines are amine-terminated polyethers such as the Jeffamine resins available from Huntsman. Preferred polyamines are 1-amino-3-aminomethyl-3,5,5-trimethylcyclohexane (isophorone diamine or IPDA), bis-(4-aminocyclo-hexyl)-methane, bis-(4-amino-3-methylcyclohexyl)-methane, 1,6-diamino-hexane, 2-methyl pentamethylene diamine, ethylene diamine, triaminononane, 2,4- and/or 2,6-toluylene diamine, 4,4'- and/or 2,4'-diamino-diphenyl methane and the Jeffamine D-230 and T-403 resins. The preparation of the polyaspartates from the above mentioned starting materials may be carried out, for example, at a temperature of 0 to 100°C using the starting materials in such proportions that at least 1, preferably 1, olefinic double bond is present for each primary amino group. Excess starting materials may be removed by distillation after the reaction. The reaction may be carried out solvent-free or in the presence of suitable solvents such as methanol, ethanol, propanol, tetrahydrofuran, dioxane and mixtures of such solvents. The aspartate-functional prepolymers containing hydantoin group precursors are prepared by reacting the polyisocyanates with the polyaspartates at a minimum equivalent ratio of aspartate groups (i.e., secondary amino groups) to isocyanate groups of 1.05:1, preferably 1.1:1 and more preferably 1.2:1 and a maximum equivalent ratio of aspartate groups to isocyanate groups of 10:1, preferably 2:1 and more preferably 1.8:1. The reaction is preferably carried out by incrementally adding the polyisocyanate to the polyaspartate. The reaction to form the urea group-containing intermediate is conducted at a temperature of 10 to 100°C, preferably 20 to 80°C and more preferably 20 to 50°C. After the addition reaction to form the prepolymers is complete, the hydantoin group precursors may be converted to hydantoin groups by increasing the temperature to 60 to 240°C, preferably 80 to 160°C and more preferably 100 to 140°C. It is also possible to form the hydantoin group at a later stage in the process. Instead of forming the urea groups and hydantoin groups in two steps, the reaction to form the prepolymers may be carried out entirely at elevated temperatures in order to form the urea groups and hydantoin groups in one step. When using polyisocyanates and polyaspartates having functionalities of 2, the aspartate-functional polyhydantoin prepolymers may be represented by the formula wherein X, R 1 , R 2 , R 3 and R 4 are as previously defined, R 5 represents the residue obtained by removing the isocyanate groups from an organic diisocyanate, preferably an organic monomeric diisocyanate and p has a value of 1 to 20, preferably 1 to 10 and more preferably 1 to 5. Instead of exclusively using the aspartate-functional prepolymers containing hydantoin groups or hydantoin group precursors as the high molecular weight component for preparing the polyureas according to the present invention, it is also possible to use blends of these prepolymers with the known organic compounds containing at least two isocyanate-reactive groups, preferably hydroxy groups, i.e., high molecular weight compounds having molecular weights of 400 to 6,000, preferably 800 to 3,000. The molecular weights are number average molecular weights (M n ) and are determined by end group analysis (OH number). Examples of these high molecular weight compounds include polyester polyols, polyether polyols, polyhydroxy polycarbonates, polyhydroxy polyacetals, polyhydroxy polyacrylates, polyhydroxy polyester amides and polyhydroxy polythioethers. The polyester polyols, polyether polyols and polyhydroxy polycarbonates are preferred. Further details concerning these high molecular weight compounds and starting materials for their preparation are disclosed in U.S. Patent 4,701,480, herein incorporated by reference. While the presence of the previously described high molecular weight polyols is optional, they may preferably be used in amount of at least 5%, more preferably at least 10% by weight, based on the weight of the polyisocyanate addition product. The maximum amount of these polyols is preferably 85%, more preferably 75% by weight, based on the weight of the polyisocyanate addition product. Low molecular weight isocyanate-reactive compounds, which may optionally be used to prepare the polyureas and which have an average molecular weight of up to 400, include the polyhydric alcohols, preferably dihydric alcohols that have previously been incorporated by reference for preparing the polyester and polyether polyols. Also suitable are aldimines prepared by reacting the amines, which have previously been described for preparing the polyaspartates, with aldehydes such as isobutyraldehyde. In addition to the above-mentioned components which are preferably difunctional in the isocyanate polyaddition reaction, monofunctional and even small portions of trifunctional and higher functional components generally known in polyurethane chemistry, such as trimethylolpropane, may be used in special cases in which slight branching of the NCO prepolymer or polyurea is desired. However, the NCO prepolymers should be substantially linear and this may be achieved by maintaining the average functionality of the prepolymer starting components below 2.1. In order to enable the polyureas to be stably dispersed in an aqueous medium, ionic or potential ionic groups and/or lateral or terminal, hydrophilic ethylene oxide units may be chemically incorporated into the polyureas. The ionic or potential ionic groups may be either anionic or cationic, preferably anionic. Examples of anionic groups include carboxylate and sulfonate groups, while examples of cationic groups include ammonium and sulfonium groups. The ionic groups are incorporated in an amount sufficient to provide an ionic group content of 0 to 200 milliequivalents per 100 g of polyurea. When the ionic or potential ionic groups are incorporated, they are preferably incorporated in an amount sufficient to provide an ionic group content of at least 10, preferably at least 20 milliequivalents per 100 g of polyurea. The upper limit for the content of ionic groups is preferably 180, more preferably 100 milliequivalents per 100 g of polyurea. The content of hydrophilic ethylene oxide units may be up to 10%, preferably up to 8%, more preferably about 1 to 6% and most preferably 1 to 5%, by weight, based on the weight of the polyurea. Instead of or, in addition to, the chemically incorporated ionic and/or nonionic hydrophilic groups, it is also possible to provide hydrophilicity to the polyurethanes by blending them with known nonionic, external emulsifiers, e.g., the alkaryl types such as polyoxyethylene nonyl phenyl ether or polyoxyethylene octyl phenyl ether; the alkyl ether types such as polyoxyethylene lauryl ether or polyoxyethylene oleyl ether, the alkyl ester types such as polyoxyethylene laurate, polyoxyethylene oleate or polyoxyethylene stearate; and the polyoxyethylene benzylated phenyl ether types. The ionic or potential ionic groups may be chemically incorporated into the NCO prepolymer or may be chemically incorporated through the chain extender which is used to form the polyurea from the prepolymer. Suitable compounds for incorporating these groups include i) monoisocyanates or diisocyanates which contain ionic or potential ionic groups and ii) compounds which are monofunctional or difunctional in the isocyanate-polyaddition reaction and contain ionic or potential ionic groups. The ionic groups are formed by neutralizing the corresponding potential ionic groups either prior to, during or after formation of the polyisocyanate addition product. When the potential ionic groups are neutralized prior to their incorporation into the polyisocyanate addition product, the ionic groups are incorporated directly. When neutralization is performed subsequent to forming the NCO prepolymer or polyurea, potential ionic groups are incorporated. Suitable compounds for incorporating the carboxylate, sulfonate and quaternary nitrogen groups are described in U.S. Patents 3,479,310, 4,108,814 and 4,303,774, the disclosures of which are herein incorporated by reference. Suitable compounds for incorporating tertiary sulfonium groups are described in U.S. Patent 3,419,533, also incorporated by reference. The preferred sulfonate groups for incorporation into the NCO prepolymer are the diol sulfonic acids or the diol sulfonates disclosed in U.S. Patent 4,108,814. The neutralizing agents for converting the potential ionic groups to ionic groups are described in the preceding U.S. patents and are also discussed hereinafter. Within the context of this invention, the term "neutralizing agents" is meant to embrace all types of agents which are useful for converting potential ionic groups to ionic groups. The preferred carboxylate groups for incorporation into polyurea in either the one-stage or two-stage process are derived from hydroxy-carboxylic acids corresponding to the formula: (HO) x Q(COOH) y wherein Q represents a straight or branched, hydrocarbon radical containing 1 to 12 carbon atoms, and x and y represent values from 1 to 3. Examples of these hydroxy-carboxylic acids include citric acid and tartaric acid. The preferred acids are those of the above-mentioned formula wherein x = 2 and y = 1. These dihydroxy alkanoic acids are described in U.S. Patent 3,412,054, herein incorporated by reference. The preferred group of dihydroxy alkanoic acids are the α,α-dimethylol alkanoic acids represented by the structural formula wherein Q' is hydrogen or an alkyl group containing 1 to 8 carbon atoms. The most preferred compound is α,α-dimethylol propionic acid, i.e., when Q' is methyl in the above formula. When incorporating the anionic or potential anionic groups through the chain extender used to convert the NCO prepolymer to the polyurea in the second stage of the two-stage process, i.e., after the prepolymer has been disclosed in water, it is preferred to use amino functional compounds containing anionic or potential anionic groups such as the diamino carboxylic acids or carboxylates disclosed in U.S. Patent 3,539,483 or salts of 2,6-diamino-hexanoic acid. When sulfonate groups are desired they may be incorporated through the chain extenders using salts of isethionic acid or preferably diamino sulfonates of the formula H 2 N-A-NH-B-SO 3 - wherein A and B represent aliphatic hydrocarbon radicals containing 2 to 6 carbon atoms, preferably ethylene groups. Whether the anionic groups are incorporated into the polyurea via the prepolymer or the chain extender is not critical. Therefore, the anionic groups may exclusively be incorporated via the prepolymer or via the chain extender or a portion of the anionic groups may be introduced according to each alternative. However, it is preferred to introduce the anionic groups via the prepolymer since this allows a wider range of process variations in preparing the aqueous polyurea dispersion. Suitable compounds for incorporating the lateral or terminal, hydrophilic ethylene oxide units may be either monofunctional or difunctional in the context of the isocyanate-polyaddition reaction and include i) diisocyanates which contain lateral, hydrophilic ethylene oxide units, ii) compounds which are difunctional in the isocyanate-polyaddition reaction and contain lateral, hydrophilic ethylene oxide units, iii) monoisocyanates which contain terminal, hydrophilic ethylene oxide units, iv) compounds which are monofunctional in the isocyanate-polyaddition reaction and contain terminal, hydrophilic ethylene oxide units, and v) mixtures thereof. Examples of these compounds are disclosed in U.S. Patents 3,905,929, 3,920,598 and 4,190,566 (the disclosures of which are herein incorporated by reference). Preferred hydrophilic components are the monohydroxy polyethers having terminal hydrophilic chains containing ethylene oxide units. These hydrophilic components may be produced as described in the preceding patents by alkoxylating a monofunctional starter, such as methanol or n-butanol, using ethylene oxide and optionally another alkylene oxide, for example propylene oxide. The NCO prepolymers of the present invention are prepared by reacting the polyisocyanate component with the aspartate-functional prepolymer containing hydantoin groups or hydantoin group precursors, preferably hydantoin groups, and optionally any other high or low molecular weight organic component containing at least 2 isocyanate-reactive groups. Optional low molecular weight components include the component containing at least one ionic group or at least one potential ionic group and the component containing hydrophilic ethylene oxide units. The isocyanate-reactive components may be reacted with the polyisocyanate component either in admixture and/or sequentially to produce the NCO prepolymer. The ratio of isocyanate groups to isocyanate-reactive groups is maintained between 1.1 to 5, preferably 1.2 to 3 and most preferably 1.3 to 2.0 on an equivalent basis. The above components may be reacted simultaneously or sequentially to produce the NCO prepolymer. When the aspartate-functional prepolymers are reacted with polyisocyanates to form NCO prepolymers, additional hydantoin group precursors are formed. These hydantoin group precursors as well as any other hydantoin group precursors can be converted to hydantoin groups during the formation of the NCO prepolymers and after the prepolymers are added to water. If precautions are not taken, the monoalcohol released as a by-product can react with the terminal isocyanate groups of the NCO prepolymers resulting in chain termination. Chain termination is more likely to occur during the formation of the NCO prepolymers, especially in the presence of acids, which are known to catalyze the formation of hydantoin groups. To reduce the likelihood of hydantoin formation and chain termination during the preparation of the NCO prepolymer, it is preferred to either neutralize any potential anionic groups (that are present to provide hydrophilicity to the dispersed polyurea) before the aspartate-functional prepolymer is reacted with isocyanate groups and/or to keep the temperature during NCO prepolymer formation below 80°C. This can be accomplished by reacting the polyisocyanate component with the isocyanate-reactive component containing potential anionic groups and neutralizing the acid groups before the addition of the aspartate-functional hydantoin prepolymer. The reaction temperature during prepolymer production is normally maintained below 120°C, preferably between 50° and 80°C. The reaction is continued until the content of unreacted isocyanate groups decreases to the theoretical amount or slightly below. The finished prepolymer should have a free isocyanate content of 1 to 20%, preferably 1 to 10% by weight, based on the weight of prepolymer solids. The prepolymers may be prepared in the presence of solvent, provided that the solvent is substantially nonreactive in the context of the isocyanate-polyaddition reaction. Examples of suitable solvents include dimethylformamide, esters, ethers, ketoesters, ketones, e.g., methyl ethyl ketone and acetone, glycol-ether-esters, chlorinated hydrocarbons, aliphatic and alicyclic hydrocarbon-substituted pyrrolidinones, e.g., N-methyl-2-pyrrolidinone, hydrogenated furans, aromatic hydrocarbons and mixtures thereof. Suitable neutralizing or quaternizing agents for converting the potential anionic groups to anionic groups either before, during or after their incorporation into the polyureas, are tertiary amines, alkali metal cations or ammonia. Examples of these neutralizing agents are disclosed in U.S. Patents 4,501,852 and 4,701,480, which are incorporated by reference. Preferred neutralizing agents are the trialkyl-substituted tertiary amines and include triethyl amine, N,N-dimethyl-ethanol amine, triethanol amine, N-methyl-diethanol amine, 2-aminomethyl-1-propanol, and N-methyl and N-ethyl morpholine. A sufficient amount of the potential ionic groups, if present, must be neutralized so that when combined with the hydrophilic ethylene oxide units and external emulsifiers, the polyureas will remain stably dispersed in the aqueous dispersion: Generally, at least 75%, preferably at least 90%, of the potential ionic groups are neutralized to the corresponding ionic groups. The conversion of the potential ionic groups to ionic groups is conducted in known manner, e.g., as described in the preceding patents setting forth suitable neutralizing agents. The NCO prepolymers may be converted into aqueous polyurea dispersions in accordance with the methods known in polyurethane chemistry and described, e.g., in "Waterborne Polyurethanes," Rosthauser et al, Advances in Urethane Science and Technology, Vol. 10, pg. 121-162 (1987). According to one process for preparing the aqueous polyurea dispersions, the NCO prepolymer is prepared, chain extended to form a polyurea and subsequently dispersed in water. This process is disclosed in U.S. Patent 3,479,310, herein incorporated by reference. If hydantoin groups or hydantoin group precursors are incorporated into the polyureas during the chain extension step, it is preferred to prepare the aqueous polyurea dispersions in this manner. However, since amines are preferably used as the chain extender, the preferred method of preparing the polyureas is to disperse the NCO prepolymer in water prior to chain extension. Whether dispersions of linear or cross-linked polyureas are obtained generally depends on the functionality of the chain extender. The aqueous polyurea dispersions of the present invention are preferably formed by reacting the NCO prepolymers with a polyamine or mixtures thereof in accordance with the previously described processes. The average functionality of the amine, i.e., the number of amine nitrogens per molecule, should be between 2 and 6, preferably between 2 and 4 and most preferably between 2 and 3. The desired functionalities can be obtained by using mixtures of polyamines. Suitable amines are essentially hydrocarbon polyamines containing 2 to 6 amino groups which have isocyanate-reactive hydrogens according to the Zerewitinoff test, e.g., primary or secondary amine groups. The polyamines are generally aromatic, aliphatic or alicyclic amines and preferably contain 1 to 30 carbon atoms, more preferably 2 to 15 carbon atoms, and most preferably 2 to 10 carbon atoms. These polyamines may contain additional substitutents provided that they are not as reactive with isocyanate groups as the primary or secondary amines. When conducting the chain extension reaction after the NCO prepolymers have been dispersed in water, it is preferred that the amines are water soluble. Examples of polyamines for use in the present invention include diamines that have previously been disclosed as being suitable for the preparation of the polyaspartates. Preferred polyamines are 1-amino-3-aminomethyl-3,5,5-trimethyl-cyclohexane (isophorone diamine or IPDA), bis-(4-amino-cyclohexyl)-methane, bis-(4-amino-3-methylcyclohexyl)-methane, 1,6-diaminohexane, ethylene diamine, diethylene triamine, triethylene tetramine, tetraethylene pentamine, pentaethylene hexamine, hydrazine and amine-terminated polyethers such as the previously mentioned Jeffamine resins. The amount of chain extender to be used in accordance with the present invention is dependent upon the number of terminal isocyanate groups in the prepolymer. Generally, the ratio of terminal isocyanate groups of the prepolymer to isocyanate-reactive groups of the chain extender, preferably the amino hydrogens of the polyfunctional amine, is between 1.0:0.6 and 1.0:1.1, preferably between 1.0:0.8 and 1.0:0.98 on an equivalent basis. The reaction between the NCO prepolymer and the chain extender is generally conducted at temperatures of 5 to 90°C, preferably from 20 to 80°C, and most preferably from 30 to 60°C. The reaction conditions are normally maintained until the isocyanate groups are essentially completely reacted. The final product is a stable, aqueous polyurea dispersion having a solids content of up to 60% by weight, preferably 15-60% by weight and most preferably 30-45% by weight. However, it is always possible to dilute the dispersions to any minimum solids content desired. The particle size is generally below 1.0 micron, and preferably 0.001 to 0.5 microns. The average particle size is generally less than 0.5 micron, preferably 0.01 to 0.3 microns. The small particle size enhances the stability of the dispersed particles and also leads to the production of films with high surface gloss. The dispersions may be blended with other dispersions or with other known additives such as fillers, plasticizers, pigments, carbon black, silica sols and the known levelling agents, wetting agents, antifoaming agents and stabilizers. The aqueous polyurea dispersions are suitable for coating and impregnating woven and nonwoven textiles, leather, paper, wood, metals, ceramics, stone, concrete, bitumen, hard fibers, straw, glass, porcelain, plastics of a variety of different types, glass fibers for antistatic and crease-resistant finishing; as binders for nonwovens, adhesives, adhesion promoters, laminating agents, hydrophobizing agents, plasticizers; as binders, for example, for cork powder or sawdust, glass fibers, asbestos, paper-like materials, plastics or rubber waste, ceramic materials; as auxiliaries in textile printing and in the paper industry; as additives to polymers as sizing agents, for example, for glass fibers; and for finishing leather. Drying of the products obtained by various application techniques may be carried out either at room temperature or at elevated temperature. In the following examples all parts and percentages are by weight unless otherwise specified. EXAMPLES Preparation of bis-aspartates The bis-aspartates set forth in the following table were prepared by adding dropwise 1 mole of a diamine with stirring to 2 moles of maleic acid dibutylester that was previously charged at ambient temperature to a 3-neck flask equipped with a stirrer, thermometer, nitrogen bubbler and an addition funnel. The amine was added at a rate such that the exotherm did not increase the temperature of the reaction mixture above 50°C. Upon complete addition, the contents of the reaction flask were maintained at 50°C for a period of 12 hours. The following table sets for the amounts of the reactants and the properties of the resulting bis-aspartates. Bis-aspartate A B C Diamine/ Amount MPDA HDA C 36 Diamine 116.00 116.22 530.00 Dibutylmaleate 456.60 456.60 456.60 Viscosity 64.00 69.00 310.00 Amine Number (measured) 192.10 198.00 114.06 Preparation of aspartate-functional polyhydantoin prepolymers The bis-aspartate was charged into a 3-neck flask under a nitrogen atmosphere and then 1,6-hexamethylene diisocyanate (HDI) was added dropwise to the bis-aspartate while maintaining the temperature below 70°C for 2 hours or until the isocyanate band disappeared from the IR spectrum, whichever is longer. For the preparation of Hydantoin Prepolymer 6, 34.56 parts of dimethylol propionic acid was mixed with the bis-aspartate. After completion of urea formation, acetic acid was added as a catalyst in the amount of 5000 ppm. The reaction mixture was then heated to 120°C for 2-3 hours or until IR spectrum showed the disappearance of amide I and II bands and appearance of a split ester carbonyl peak as an indication of a planar hydantoin ring, whichever is longer. After hydantoin formation was complete, the alcohol was distilled off under vacuum. The following table sets forth the amounts of the reactants and the properties of the resulting aspartate-functional polyhydantoin prepolymers. Preparation of aqueously dispersed polyurea containing hydantoin groups Step 1 - Preparation of NCO prepolymer Dimethylolpropionic acid (DMPA), a polyether monohydric alcohol prepared from n-butanol, ethylene oxide, and propylene oxide (in a molar ratio ethylene oxide to propylene oxide of 83:17), N-methyl-pyrrolidone (NMP), isophorone diisocyanate (IPDI), 1,6-hexamethylene diisocyanate (HDI) and bis-(4-isocyanatocyclohexyl)-methane (H 12 MDI) in the amounts specified in the following table were added to a 1000 ml three neck flask equipped with stirrer, thermometer, and condenser and reacted at 90°C to 100°C for two hours until the NCO content was constant 19.2%. The reaction mixture was then cooled to 40°C, and triethylamine was added and reacted at 50°C for 10 minutes. The hydantoin prepolymer was then added and reacted for 10 minutes. The exothermic reaction resulted in a temperature increase from 40°C to about 80°C. Step 2 - Dispersion and Chain Extension The neutralized prepolymer was added slowly to the demineralized dispersing water at 50°C under rapid agitation in a second flask (2000 ml resin flask). After the dispersion step was complete, the dispersed prepolymer was chain extended by the slow addition of one or more of the following amine chain extenders in water: hydrazine hydrate, diethylenetriamine, an amine-terminated polyether (available from Huntsman as Jeffamine D400), 2-methyl-1,5-pentanediamine (MPDA) and ethylene diamine. The dispersions were post reacted for 1 hour at 60-70°C. The resulting aqueous polyurea dispersions had the properties listed in the following table. Films were prepared from the aqueous polyurethane dispersions by blending them with 0.5% by weight of a levelling agent (Fluorad FC 430, available from 3M) and drawing them down onto glass at a wet film thickness of 10 mil. The coatings were cured for 24 hours at room temperature, then for 1 hour at 60°C, and finally for 4 more days at room temperature before they were removed tested. The tensile and elongation properties are set forth in the following table. The film used in the comparison example was prepared from a commercial aqueous polyurethane dispersion, i.e., Bayhydrol 110, available from Bayer Corp. This polyurethane dispersion corresponds to those prepared in accordance with the present invention except that it is based on a polyester polyol instead of an aspartate-functional prepolymer and, thus, does not contain hydantoin groups. Examples 2, 3, 4 and 6 demonstrate outstanding hydrolytic stability when compared to an aqueous polyurethane dispersion based on a polyester polyol.

Claims: An aqueous dispersion of a polyurea containing hydantoin groups (calculated as C 3 N 2 O 2 , MW 96) in an amount of 1 to 40% by weight, based on resin solids. The dispersion of Claim 1 wherein said polyurea contains 10 to 120 milliequivalents per 100 grams of polyurea of chemically incorporated anionic groups and up to 10% by weight, based on the weight of said polyurea, of lateral and/or terminal hydrophilic chains containing ethylene oxide units. The dispersion of Claim 2 wherein at least about 80% of said anionic groups are carboxylate groups neutralized with tertiary amines. An aqueous polyurea dispersion wherein the polyurea contains 1 to 40% by weight, based on the weight of the polyurea, of hydantoin groups (calculated as C 3 N 2 O 2 , MW 96) and wherein the polyurea is based on the reaction product of a) an NCO prepolymer containing 1 to 40% by weight, based on the weight of said polyurea, of hydantoin groups (calculated as C 3 N 2 O 2 , MW 96) with b) an isocyanate-reactive component containing amino groups. The dispersion of Claim 4 wherein said polyurea contains 10 to 120 milliequivalents per 100 grams of polyurea of chemically incorporated anionic groups and up to about 10% by weight, based on the weight of said polyurea, of lateral and/or terminal hydrophilic chains containing ethylene oxide units. The dispersion of Claim 5 wherein at least about 80% of said anionic groups are carboxylate groups neutralized with tertiary amines.

Inventors: GINDIN LYUBA K, MASON ARTHUR W, SCHMITT PETER D, WICKS DOUGLAS A, YESKE PHILIP E, YONEK KENNETH P, GINDIN, LYUBA K., MASON, ARTHUR W., SCHMITT, PETER D., WICKS, DOUGLAS A., YESKE, PHILIP E., YONEK, KENNETH P.
Applicants: BAYER AG, BAYER CORPORATION
Application year: 1997
Main classification: C08G18
IPC codes: C08J3, C09D175, C08G18