Method of manufacturing optical-use plastic products

Abstract: A method of manufacturing optical-use plastic products such as various kinds of lenses including a magnifying lens, finder spectacle lens, contact lens, condenser lens; infrared ray projector, radiation thermometer, interferometer, scanner, etc. The method of manufacturing optical-use plastic products comprises a step A for injecting a melted resin into a mold cavity to produce a primary molding (1): and a step B for injecting a same resin (2) as in the step A to a part or whole of the primary molding to form a molding in which the injected resin is melt-welded to the primary molding.

Description: The present invention relates to a method of manufacturing optical-use plastic products such as magnifying lens, various finders, etc. for naked-eye viewing; spectacle lens and contact lens in ophtalmology; condensers, infrared ray projectors, radiation thermometers, solar furnaces, on-vehicle lighting devices in illumination and light-reception systems; various lenses in photography systems; and interferometers, scanners, etc. in laser optical systems. Generally, glass is conveniently used to manufacture optical products because it is advantageous in being available in a wide choice of kinds, has high stability of optical properties, high thermal resistance, and little change of properties due to temperature variation. However, the optical glass is not free from defects but it is disadvantageously heavy and hard and needs a process of polishing, which leads to reduced productivity. Also, a glass product having a non-spherical shape cannot be polished with a high reproducibility and thus the productivity is low. Furthermore, some kinds of the optical glass have poor weatherability. Accordingly, it has been proposed to use plastics for manufacturing optical-use products in order to overcome the above-mentioned drawbacks of the optical glass. The optical-use plastic products are advantageous in that they are lightweight and have a high impact resistance. At present, the optical-use plastic is successfully used to make spectacle lenses. Other advantageous of the optical-use plastics include an easiness of variable forming, a reduced number of manufacturing steps by mass production using injection molding, an excellent reproducibility in shape of product, etc. The optical-use plastic products are manufactured by grinding and polishing as well as by injection molding. Recently, an injection and compression molding method, namely, an advanced injection molding method, has been proposed which includes (1) Rolinx method molding, (2) micro-molding, and (3) injection pressing. These methods will be further described herebelow. (1) Rolinx method molding A melted resin is injected into a mold held with a low clamping force. During the resin filling into the mold, the injecting pressure exceeds the molding clamping force to cause the parting line of the mold to open. Upon completion of the resin filling, the injection gate is closed and the mold is pressed to close the parting line. The mold, and thus the resin in it, are cooled with the mold kept pressed. (2) Micro-molding The parting line of the mold is closed with a mold clamping force. After a specified amount of resin is injected into the mold cavity, the molded resin is compressed by a separate independent pressurizing machine which is a hydraulic cylinder assembled in the mold or one assembled in the movable platen of an injection molder. (3) Injection pressing A melted resin is injected into the mold internal space which is increased for a compression stroke, the mold is closed in process, or upon completion, of the resin injection, and the molded resin is compressed by a clamping force. These molding methods can be used to prove plastic products having a dimensional accuracy that has been increasingly higher. For these methods, however, the injection molder and mold are designed to have a complicated structure and advanced precision molding techniques are necessary. In the technical and economical respects, these methods are not yet popular as common methods in the industrial manufacture of optical-use plastic products. However, the grinding and polishing method permits to easily form flat and spherical surfaces with a high accuracy of working but cannot form non-spherical surfaces with any high accuracy although it needs a great number of manufacturing steps. In the injection molding, as the temperature of a product removed from a mold falls, the product will shrink, leading to a difference of product dimensions from those which the mold should assure. The phenomenon will take place more noticeably for products of 10 mm or more in maximum wall thickness and having an asymmetrical, unevenly-thick structure. As mentioned above, the conventional injection molding is disadvantageous in that as the temperature of a product removed from a mold falls, the product will shrink, leading to difference of product dimensions from those which the mold should assure. Also, in the grinding and polishing method, a cast plastic block has to be machined to an intended shape (for example, lens shape) and then polished. This method can assure a high accuracy for flat and spherical surfaces but not for non-spherical surfaces and needs a large number of manufacturing steps. Accordingly, the present invention has an object to overcome the above-mentioned drawbacks of the prior art by providing a method of manufacturing optical-use plastic products, even with a maximum wall thickness of 10 mm or more and asymmetrical, unevenly-thick structure.with a high productivity, dimensional accuracy and surface-shaping accuracy. Attention is also drawn to the disclosures of DE-A-3809969, JP-A-60-054822, and JP-A-57-173136. In particular, said JP-A-60-054822 discloses plastic convex lenses having a diameter of 50-500 mm and thickness of 10-100 mm in the center which are produced by (i) forming a convex lens-shaped center core having a thickness half as much as the thickness of a convex lens finally produced by injection molding by using a first injection molding mold and (ii) placing the convex lens-shaped center core in the cavity of a second injection molding mold forming two cavity remaining parts between two cavity surfaces and two curved surfaces of the convex lens-shaped center core and injecting melted plastic into two cavity remaining parts simultaneously to mold as a monoblock. The present invention provides a method of manufacturing optical-use plastic products, according to claim 1. Preferred embodiments are defined in the dependent claims. The invention will be further described with reference to the accompanying drawings, wherein: FIG. 1 is a sectional view of an example of mold used in manufacturing optical-use plastic product according to the present invention: FIG. 2 is a perspective view of a primary molding: FIG. 3 is a perspective view of a melt-welded assembly of the primary molding and a secondary molding; FIG. 4 is a perspective view of a final product; FIG. 5 is a perspective view of a primary molding; FIG. 6 is a perspective view of an integral assembly of the primary molding and a secondary molding according to the present invention; FIG. 7 is a perspective view of a final product according to the present invention; FIG. 8 is a sectional view of a primary molding set in the mold; FIG. 9 is a front view of the final product; FIG. 10 is a front view of the primary molding; and FIG. 11 is a sectional view, enlarged in scale, of the joint of the primary molding. FIG. 1 shows an example of a mold used in a first embodiment of the method of manufacturing optical-use plastic products according to the present invention. FIGS. 1 to 4 are perspective views showing, by way of example, moldings produced at various steps of the method of manufacturing optical-use plastic products according to the present invention. In the Figures, the reference numeral 1 indicates a primary molding 1 (also see FIG. 2) produced in a separate injection mold (not shown). The mold assembly used in the present invention consists of two stages, upper and lower. A secondary molding 2 is produced by injection molding in the upper stage, while a tertiary molding 3 (see FIG. 4) is produced by injection molding in the lower stage. The right-hand portion of the mold assembly is a stationary mold 10 and the left-hand portion is a moving mold 11. The mold assembly has also a cavity 12 for production of the secondary molding 2. A melted resin is injected into the cavity 12 to produce the secondary molding 2 integral with the primary molding 1 (as shown in FIG. 3). It should be noted here that since the primary and secondary moldings 1 and 2 are formed from the same resin (identical in nature and grade), the melted resin for the secondary molding 2, put into contact with the primary molding 1, will be melted to fully cover the primary molding 1 and thus melt-welded integrally to the primary molding 1; therefore, the molding shown in FIG. 3 will not have any material and optical boundary between the primary and secondary moldings 1 and 2. Finally, after the secondary molding 2 is formed, the moving mold 11 is opened from the stationary mold 10 and turned to set the lower stage of the mold assembly as shown in FIG. 1. A melted resin is injected into a cavity 13 to form a tertiary molding 3 (for final product, shown in FIG. 4) which is melt-welded integrally to the primary and secondary moldings 1 and 2 in the same manner as in the above. Note that since the primary, secondary and tertiary moldings 1, 2 and 3 are formed from the same resin, the melted resin for the tertiary molding 3, put into contact with the primary and secondary moldings 1 and 2, will be melted to fully cover the primary and secondary moldings 1 and 2 and thus melt-welded integrally to them; therefore, the molding shown in FIG. 4 will not have any material and optical boundary between the primary, secondary and tertiary moldings 1, 2 and 3. It should be noted that the mold used in the present invention is not limited to the above-mentioned one consisting of the stationary and moving molds 10 and 11 but may be a well-known one, for example, in which a plurality of primary moldings and subsequent-order ones including a final product can be set. Using such mold, various-order moldings and final product can be formed in one molding cycle. Note that in each molding cycle, various-order moldings have to be transferred into places for next steps of molding; however, one final product can be yielded in each molding cycle as mentioned above. As a result, the molding time down to a final product is considerably short as compared with molding of such various-order moldings and final product each in one mold, which leads to a dramatically improved productivity. The aforementioned step B should preferably be done more than once, which has been described in the foregoing (for forming secondary and tertiary moldings). When the step B is done once, a melted resin is injected into the mold cavity to form a primary molding 1 (step A). There after the same resin as used in the step A is injected to a part or whole of the primary molding 1 to integrally weld the primary molding 1 and melted resin with each other to form a molding (step B). This molding is a final product. In the aforementioned embodiment, one primary molding 1 is used as the core. However, two or more primary moldings 1 may be used depending upon the shape and size of an intended final product. FIGS. 1 to 4 show an example of resin molding for a convex lens. For a concave lens, the primary molding 1 may be placed near a possible outer circumference of the convex lens. The primary molding 1 for use to form the convex lens has a doughnut-like shape open at the center thereof. Such optical products like these lenses should have a high dimensional accuracy. In selection of optical-use plastics, it is important to select ones transparent to visible rays of light. Further, the resins should be as follows: (1) Visible rays of light are not absorbed inside the resin. That is, it has a light transmittance as high as possible. (2) It has a compact structure. No spherulite should desirably exist. (3) It is isotropic and homogeneic, which contributes to the stability of optical properties such as index of refraction, etc. In these respects, any one of polymethyl methacrylate (PMMA), polystyrene (PS), acrylonitrile styrene copolymer (AS), polycarbonate (PC), polymethyl pentene, styrene butadiene copolymer, etc. should preferably be selected for the optical-use plastics. The present invention will be further described with reference to embodiments and comparative products. It should be noted, however, that the present invention is not limited to the embodiments. First embodiment (I) Forming of primary molding: A primary molding 1 shown in FIG. 5 is formed by injecting molding under the following conditions: Injection molder M-100A-TS by Meiki Seisakusho Co., Ltd. Resin Delpet 80N (PMMA by Asahi Chemical Industry Co.,Ltd.; predried at 80° C for 4 hours) Injection conditions Barrel (cylinder) temperature setting: Nozzle 230° C Barrel 245° C Hopper 230° C Mold temperature 90° C (setting by water circulation) In this injection molding, surface shrinkage or dimensional inaccuracy took place without voids depending upon set secondary to tertiary pressures of injection (dwell). The primary molding thus formed was used as it was for forming a secondary molding 2 and also for forming a tertiary molding 3. (II) Forming of secondary and tertiary moldings: Next, a resin is injected to the primary molding 1 formed as in the above to form secondary and tertiary moldings 2 and 3 (shown in FIGS. 6 and 7) one after another. The secondary and tertiary moldings 2 and 3 could be formed over the primary molding 1 (even with the dimensional inaccuracy) to predetermined dimensions without any defects such as shrinkage, etc. Even a lens having a non-spherical shape as shown in FIG. 7 could be formed precisely to the dimensions of the mold, which was confirmed by a three-dimensional shape measurement. Visual checking of the final molding in the sunlight proved no boundary between the primary, secondary and tertiary moldings. When a laser beam was projected at a right angle to the final molding, no boundary was visually found between the primary and tertiary moldings. When the laser beam was incident at an angle of 45 degrees upon the final molding, no boundary was found. Comparative molding It was tried to form the final molding in the above embodiment without forming the primary to tertiary moldings. In an ordinary injection molding, occurrence of voids could be avoided by appropriately selecting injection-molding conditions but noticeable shrinkage was found on the outer surface including the non-spherical portion. Only appropriate selection of the injection-molding conditions could not allow to form the final molding precisely to predetermined dimensions, namely, to the mold dimensions. FIG. 8 shows the method of forming the optical-use plastic product according to a second embodiment of the present invention. According to this embodiment, a primary molding 5 formed from a polymethyl methacrylate (PMMA), for example, by injection molding was set into a mold 40. The same resin used to form the primary molding 5 was injected to a part of the primary molding 5 at a temperature of recommended lowest temperature of injection plus 5° C to recommended highest temperature minus 5° C. FIG. 8 shows the section of the mold into which the resin was going to be injected. The resin, for example, polymethyl methacrylate (PMMA), was injected into a cavity 43 through gates 41 and 42. Thus, the primary molding 5 was formed from the melted resin injected into the mold cavity as shown. The space between the wall of the cavity 43 in the mold 40 shown in FIG. 8 and the primary molding 5 ranges from 1 to 15 mm. The thickness of the resin covering the primary molding 5 is therefore within a range of 1 to 15 mm. In FIG. 8, the diameters 50 and 20 are represented in millimeters. If the covering resin (to be injected to the primary molding already set in the mold cavity) is too thin, the resistance against the resin flow is too high so that a sufficient amount of the resin will not flow into small spaces. On the contrary, if the resin thickness is too great, shrinkage and voids peculiar to thick moldings are likely to take place. The thickness of such covering resin should be 1 to 15 mm, and preferably, 3 to 10 mm though it depends upon the kind and grade of the resin used. FIG. 9 shows a final molding, that is, an optical-use plastic product 60. In the product 60, the secondary molding 6 covers a part of the primary molding 5. The moldings 5 and 6 are melt-welded integrally to each other. The maximum thickness of this optical-use plastic product 60 is 50 mm. FIG. 10 shows a primary molding 5. In this Figure, the diameters 10 and 20 are also represented in millimeters. The thickness of the resin covering the primary molding 5 is 15 mm at the spherical portion and 5 mm at the cylindrical column when a secondary molding is formed on the primary molding 5 as shown in FIG. 8. The primary molding 5 serves as the core of a final molding and inserted into a secondary molding 6, which means that no high accuracy of dimensions is required for the primary molding 5 unless there is any defect such as voids, surface depression or the like. In this case, however, a high accuracy of dimension is required for the mold for forming the secondary molding 6. It should be noted that after injection molding of the primary molding 5. the surface of the primary molding 5 should desirably be cleaned (by wiping) with a solvent to remove stains on the surface. This cleaning will contribute to a better melt-welding of the primary molding 5 to a covering resin. The solvent used for this cleaning is not limited to any special one. It may be any one of organic solvents made from paraffin hydrocarbon, alcohol, petroleum, etc. Among others, however, ethanol or hexane may be suitably used for such cleaning. If the temperature of the covering resin (to be injected to a primary molding) is too low, it will solidify too early on the surface of the primary molding 5 (also called insert work) so that the melt-welding between the insert work and covering resin will not easily take place. On the other hand, if the temperature is too high, the melt-welding will readily take place but shrinkage will possibly take place. The temperature of a resin to be injected depends upon the grade of the resin and should be within a range from the recommended lowest temperature of injection plus 5° C to the recommended highest temperature minus 5° C. For forming a secondary molding, the primary molding has to be secured within the mold but in a place which will not have any adverse influence on the optical performance of the final product. As shown in FIG. 10. the spherical expansion head 51 of the primary molding 5 has a curved circumference 5A. There exists between the spherical expansion head 51 and cylindrical column 52 a connection 58 having a smooth curved circumference as shown in FIG. 11. Such a round shaping of the primary molding 5 allows the covering resin (for a secondary molding) to flow into small spaces. If the covering resin (to be injected to the primary molding already set in the mold cavity) is too thin, the resistance against the resin flow is so high that a sufficient amount of the resin will not flow into small spaces. On the contrary, if the resin thickness is too great, shrinkage and voids peculiar to thick moldings are likely to take place. The thickness of such covering resin should be 1 to 15 mm, and preferably, 3 to 10 mm though it depends upon the kind and grade of the resin used. If the temperature of the covering (to be injected to a primary molding) resin is too low (lower than the recommended lowest temperature of injection plus 5° C), it will solidify too early on the surface of the primary molding 5 (insert work) so that melt-welding between the insert work and covering resin will not readily take place. On the other hand. if the temperature is too high (higher than the recommended highest temperature minus 5° C), melt-welding will readily take place but shrinkage will possibly take place. Ranges of recommended temperature of injection is shown in Table 1. The temperatures in Table 1 are standard cylinder temperatures in injection molding of various grades of Delpet, Trade Name of Asahi Chemicals Industry Co., Ltd. Cylinder temperatures Grade 560F 60N 670N 80N LP-1 Nozzle (° C) 190-230 200-240 200-240 220-260 230-270 Hopper (° C) 190-230 200-220 200-220 220-240 230-250 Note that a product containing the primary molding 5 covered by the secondary molding 6, that is, the molding shown in FIG. 9, may not be taken as the final molding but it may be further covered, by injection, with the same resin as that for the primary and secondary molding 5 and 6. This molding may be taken as the final molding. More particularly, the final molding has three layers at a part thereof. Of course, it maybe formed in 4 or more layers. According to the present invention, a melted resin is injected into a mold cavity to form a primary molding 5 (step A), and the same resin as in the step A is injected to a part or whole of the primary molding 5. A secondary molding 6 is thus formed from the resin injected and melt-welded to the primary molding 5 (step B). The step B may be repeated a plurality of times. The covering resin should have a thickness of 1 to 15 mm, and preferably a thickness of 3 to 10 mm. Second embodiment (I) Forming of primary molding...Step A: Injection molder M-100A-TS by Meiki Seisakusho Co., Ltd. Resin Delpet 80N (PMMA by Asahi Chemical Industry Co.,Ltd.; predried at 80° C for 4 hours) Injecting conditions Barrel (cylinder) temperature setting: Nozzle 230° C Barrel 245° C Hopper 230° C Mold temperature 90° C (setting by water circulation) Molding time 120 sec A primary molding 5 having the round connection 5B as in FIG. 11 was formed under the above conditions. (II) Forming of secondary molding... Step B: Next, the surface of the primary molding 5 thus produced was cleaned. The primary molding was preheated and set inside the mold 40 as shown in FIG. 8. A material for secondary molding (PMMA resin) was injected to the primary molding 5 under the above conditions to form a secondary molding 6 shown in FIG. 9. The primary moldings 5 including defective ones were used for secondary molding. In all cases, appropriately setting the injection-molding conditions such as secondary to tertiary pressures of injection (dwelling) allowed to form secondary moldings 6 precisely to the predetermined dimensions without occurrence of any defects such as shrinkage, voids or the like. Among others, the spherical portion of 50 mm in diameter shown in FIG. 9, which is thick, was confirmed by three-dimentional shape measurement to have been formed to the mold dimensions. The molding time for this secondary molding was 150 seconds. The molding time for the secondary molding 5 and 6 was 120 seconds. Therefore, the total molding time was 270 seconds in total. If in the secondary step of molding, a resin is injected to a primary molding 5 with a corner or corners, it will not smoothly flow over the corner and voids or bubbles will be likely to take place in the resin at the corner. To avoid this, the corner should desirably be rounded. Visual checking of the second molding in the sunlight proved no boundary between the primary and secondary moldings 5 and 6. When a laser beam was projected at arbitrary angles to arbitrary portions of the secondary molding, no boundary was visually found between the primary and secondary moldings. For comparison with the aforementioned embodiment, a secondary molding was formed on a primary molding 5 having a corner at the connection 5B. The results of the comparison are as follows: Molding according to the embodiment: The primary and secondary moldings melt-welded to each other independently of the injecting conditions. Visual checking of the molding thus formed in the sunlight proved no boundary between the primary and secondary moldings. Also, a laser beam was projected at a right angle and also at 45 degrees to the molding. However, no boundary was visually found between the primary and secondary moldings. Comparative molding There was a poor flow over the corner in a region where the injected resin flowed fast, and voids or bubbles were found between the primary and secondary moldings at a part of such region. Third embodiment The surface of a primary molding formed by injection-molding is mirror-finished by polishing with a diamond paste. Thereafter, the surface is preferably cleaned with ethanol or hexane. The primary molding is preheated, and then set inside a mold similar to that shown in FIG. 8. A resin intended for covering the primary molding is heated to temperature between the recommended lowest temperature of injection plus 5° C and the recommended highest temperature minus 5° C, and injected to the primary molding. A secondary molding was formed (step B) in the same manner as in the aforementioned first and second embodiments. According to this third embodiment, a final molding using a primary molding of which the surface is allowed to freely shrink without dwelling under any pressure is taken as a product A, and a final molding using a primary molding of which the surface was mirror-finished by polishing with a diamond paste was taken as a product B. These products A and B were visually checked for any boundary between the primary and secondary moldings. The results of visual checking are as follows: Product A: Visual checking of the product in the sunlight proved no boundary between the primary and secondary moldings. A laser beam was projected at a right angle and also at 45 degrees to the product. In any case. no boundary was visually found between the primary and secondary moldings. Product B: The product was visually checked in the sunlight, but no boundary was found between the primary and secondary moldings. Also, a laser beam was projected at a right angle and also at 45 degrees to the product. In any case, no boundary was visually found between the primary and secondary moldings. For comparison with the above products A and B, the surface of a primary molding formed as in the above was polished with an abrasive sheet #1000 and further subjected to the above-mentioned secondary step of molding. This comparative product was also visually checked in the sunlight. A boundary was found between the primary and secondary moldings in this product. Also, a laser beam was projected to this product. Some diffusion of the laser beam was found in the boundary between the primary and secondary moldings. These results prove that when the surface of the primary molding is smooth, the covering resin for the secondary molding will completely wet the surface of the primary molding, leading to an easy melt-welding between the primary and secondary moldings and that if the surface of the primary molding is rough, the covering resin for the secondary molding will not completely wet the surface of the primary molding so that complete melt-welding will not easily take place between the primary and secondary moldings. Note that if the primary molding has a corner or corners on the outer circumference thereof, the resin will not smoothly flow over the corner and voids or bubbles will take place in that region. To avoid this, the primary molding should preferably be designed for a shape having no such corner on the outer circumference thereof. Fourth embodiment A primary molding is formed by injecting a melted resin into the cavity of a mold (not shown). The surface of the primary molding 1 is preheated at a temperature below the softening point of the resin for the secondary molding. The preheated primary molding is set into a mold similar to that in the aforementioned first to third embodiments, and the same resin as that for the primary molding is injected to a part of the primary molding. The temperatures shown in Table 2 are softening points of polymethyl methacrylate (PMMA), an example of resin used in the present invention, in injection molding of various grades of Delpet, Trade Name for PMMA of Asahi Chemicals Industry Co., Ltd. Softening points as in ASTM D648 Grade 560F 60N 670N 80N LP-1 Softening point (° C) 84 89 84 100 95 If the insert work (primary molding) is not preheated. it will have so large a difference in temperature from a covering resin which is going to be injected to the insert work, that the surface of the insert work will not readily be melted by the covering resin and thus melt-welding will not easily take place between the insert work and the covering resin. By reducing such temperature difference between the insert work and covering resin through preheating of the insert work, a melt-welding will easily take place between the insert work and covering resin. The preheating temperature varies depending upon the kind and grade of the resin used, and it should be within a range from temperature of the softening point of that resin minus 50° C to that softening point. The primary molding in the fourth embodiment was preheated at 100° C for one hour in an oven and taken as the product C. Also, a same primary molding was preheated at 80° C for one hour in the oven. This was taken as the product D. Further, another same primary molding was preheated at 60° C for one hour in the oven and taken as the comparative product 1. A still another same primary molding was preheated at 40° C for one hour in the oven and taken as the comparative product 2. Also a yet another same primary molding was left at room temperature (25° C) and taken as the comparative product 3. These products were compared with each other. The results of comparison will be described below. Product C: Visual checking of the product in the sunlight proved no boundary between the primary and secondary moldings. A laser beam was projected at a right angle and also at 45 degrees to the product. In any case, no boundary was visually found between the primary and secondary moldings. Product D: Visual checking of the product in the sunlight proved no boundary between the primary and secondary moldings. A laser beam was projected at a right angle and also at 45 degrees to the product. In any case, no boundary was visually found between the primary and secondary moldings. Comparative product 1: This comparative product was also visually checked in the sunlight. Only an indistinct boundary was found between the primary and secondary moldings in this product. Also, a laser beam was projected to this product. Some diffusion of the laser beam was found in the boundary between the primary and secondary moldings. Comparative product 2: This product was also visually checked in the sunlight. A boundary was found between the primary and secondary moldings in this product. Also, a laser beam was projected to this product. Some diffusion of the laser beam was found in the boundary between the primary and secondary moldings. Comparative product 3: This product was also visually checked in the sunlight. A boundary was found between the primary and secondary moldings in this product. Also, a laser beam was projected to this product. Some diffusion of the laser beam was found in the boundary between the primary and secondary moldings. These results prove that when the primary molding is preheated at a temperature of 60° C and above, the covering resin (secondary molding) will completely melt-weld to the primary molding and that if the primary molding is preheated at a temperature lower than 60° C, the covering resin and primary molding will not readily melt-weld to each other. It should be noted that the above findings were obtained using Delpet 80N. Note that if the primary molding has a corner or corners on the outer circumference thereof, the resin will not smoothly flow over the corner and voids or bubbles will take place in that region. To avoid this, the primary molding should preferably be designed for a shape having no such corner on the outer circumference thereof. As described in the foregoing, the method of manufacturing optical-use plastic products according to the present invention comprises a step A for injecting a melted resin into a mold cavity to produce a primary molding, and a step B for injecting the same resin as in the step A to a part or whole of the primary molding and melting the resin to form a molding melt-welded integrally to the primary molding. Since the manufacture is conducted in several steps, the cycle time can be reduced to improve the productivity. Also, the molding thickness at the final step of molding can be made relatively small to provide optical-use plastic products having intended shapes and high surface-shaping accuracy. Especially in the present invention, more or less shrinkage in the primary molding is not any problem since the resin is melt-welded between the primary molding and covering resin. Further, the molding thickness can be freely adjusted by repeating the step B.

Claims: A method of manufacturing optical-use plastic products, comprising: a step A of injecting a melted resin into a mold cavity to form a primary molding (1;5); and a step B of injecting the same resin as in the step A to a part or whole of the primary molding (1;5) to form a secondary molding (2;6) in which the injected resin is melt-welded to the primary molding; wherein the thickness of the resin covering the primary molding (1;5) is 1 to 15 mm; and the temperature of the resin injected to the primary molding (1;5) depends on the grade of resin and ranges from recommended lowest temperature of injection plus 5° C to recommended highest temperature of injection minus 5° C, so that within the said temperature range the primary and secondary mouldings are melt-welded to each other without subsequent shrinkage. A method as claimed in claim 1, characterized in that the maximum thickness of the optical-use plastic products is 10 mm or more. A method as claimed in claim 1, characterized in that the maximum thickness of the optical-use plastic products is 30 mm or more. A method as claimed in any one of claims 1 to 3, characterized in that the thickness of the resin covering the primary molding (1;5) is 3 to 10 mm. A method as claimed in any one of claims 1 to 4, characterized in that the optical-use plastic products have an asymmetrical structure of which the thickness is not even. A method as claimed in any one of claims 1 to 5, characterized in that the step B is repeated 2 times or more. A method as claimed in any one of claims 1 to 6, characterized in that the optical-use plastic products have a non-spherical surface. A method as claimed in any one of claims 1 to 7, characterized in that the resin is methacrylate. A method as claimed in any one of claims 1 to 8, characterized in that the primary molding (1;5) is designed not to have any comer on the outer circumference thereof. A method as claimed in any of claims 1 to 9, characterized in that the primary molding (1;5) is cleaned before the resin is injected to cover the primary molding in the Step B. A method as claimed in claim 10, characterized in that the cleaning is done with an organic solvent. A method as claimed in claim 11, characterized in that the cleaning organic solvent is ethanol or hexane. A method as claimed in any of claims 1 to 12, characterized in that the surface of the primary molding (1;5) is smoothed before the resin is injected to cover the primary molding in the step B. A method as claimed in claim 13, characterized in that the surface of the primary molding (1;5) is smoothed by polishing the molding surface or allowing the molding surface to freely shrink. A method as claimed in any of claims 1 to 14, characterized in that the surface of the primary molding (1;5) is preheated at a temperature below the softening point of the resin before the resin is injected to cover the primary molding in the step B.

Inventors: ISHIKAWA HIKARU, MACHIDA KUNIO, ISHIKAWA, HIKARU, MACHIDA, KUNIO
Applicants: BRIDGESTONE CORP, BRIDGESTONE CORPORATION
Application year: 1997
Main classification: B29D11
IPC codes: B29C45, B29D11