Heterogeneous catalyst for the production of ethylidene diacetate from acetic anhydride

Abstract: Ethylidene diacetate is produced by the reaction of acetic anhydride, acetic acid, hydrogen and carbon monoxide at elevated temperatures and pressures in the presence of an alkyl halide and a heterogeneous, bifunctional catalyst that is stable to hydrogenation and comprises an insoluble polymer having pendant quaternized heteroatoms, some of which heteroatoms are ionically bonded to anionic Group VIII metal complexes, the remainder of the heteroatoms being bonded to iodide. In contrast to prior art processes, no accelerator (promoter) is necessary to achieve the catalytic reaction and the products are easily separated from the catalyst by filtration.

Description: This invention relates to a process for producing ethylidene diacetate by hydrogenating acetic anhydride in the presence of a heterogeneous, bifunctional catalyst that is stable to hydrogenation. The catalyst contains quaternized heteroatoms, some of which heteroatoms are ionically bonded to anionic Group VIII metal complexes, the remainder being bonded to iodide. Ethylidene diacetate (EDA) is a valuable chemical because it is a precursor to vinyl acetate monomer. There are a number of homogeneous catalytic processes for the production of EDA. Representative processes for preparing EDA include the process disclosed in US-A-4,429,150 in which methyl acetate and/or acetic anhydride (Ac 2 O), CO and H 2 are reacted in the presence of a catalyst system comprising a Group VIII metal and a halogen-containing compound in the presence of a sulfur-containing polar solvent. JP-A-51-115409, EP-A-0028474 and EP-A-0566371 disclose processes for producing EDA using homogeneous rhodium catalysts. US-A-4,581,473 describes a homogeneous rhodium catalyst with methyl iodide and LiI that hydrogenates acetic anhydride to EDA. All these processes suffer from the significant disadvantage of requiring separation and purification of the reaction products from the homogeneous catalyst. To solve this problem, US-A-5,371,274 discloses a process for making EDA using a heterogeneous catalyst of the general formula M a X, where M is a rhodium phosphine complex covalently bound to an organic carrier X. The product was produced by reacting methyl acetate, iodomethane, CO and H 2 in the presence of this supported catalyst and an accelerator such as 3-picoline at elevated temperature and pressure. The product of the reaction is easily separated from the heterogeneous catalyst but the accelerator still has to be separated from the product. In addition to this, it is well known that rhodium phosphine complexes covalently bound to an organic polymer tend to leach out rhodium (See Advanced Inorganic Chemistry, 5th Edition, p 1272). The organic polymer used to support rhodium in US-A-5,371,274 is a standard kind of phosphine-containing polymer used to support rhodium and has been described in detail by Jarrell and Gates, J. Catal., 40, 255(1975). They report that the catalyst lost activity rapidly due to rhodium leaching from the support even at low temperatures in the range of 85-95°C. In US-A-5,371,275 and US-A-5,354,886 rhodium complexes supported on an inorganic carrier such as silica or alumina and used to make EDA are disclosed. Many others have attempted to design heterogeneous catalysts with a view of minimizing the leaching of the metal complex. One such system is described in US-A-4,328,125 as an anion exchange resin to which is ionically bound an anionic metal carbonyl species having the general formula M n (CO) m (X) p - , where M is a transition metal. These catalysts have been described and used for the carbonylation of alcohols for the production of carboxylic acids. Marston et al. in US-A-5,155,261 and Minami et al. in US-A-5,364,963 have described a similar catalyst consisting of a cross-linked 4-vinylpyridine divinylbenzene copolymer containing quaternized pyridine groups supporting a rhodium species. This catalyst is robust and offers higher operating temperatures for the carbonylation of methanol to acetic acid. US-A-5,360,929 discloses the use of such polymeric pyridine catalysts to produce carboxylic acid anhydrides from carboxylate esters and ethers. No mention is made about using such catalysts, however, for EDA production from the reaction of acetic anhydride with CO and H 2 gas. According to the present invention, EDA is produced by hydrogenating acetic anhydride (Ac 2 O) in the presence of a heterogeneous, bifunctional catalyst. The process comprises reacting Ac 2 O, hydrogen, carbon monoxide, acetic acid, and an alkyl halide in the presence of the bifunctional catalyst. The catalyst is stable to hydrogenation and comprises an insoluble polymer having pendant quaternized heteroatoms, some of which heteroatoms are ionically bonded to anionic Group VIII metal complexes, the remainder of the heteroatoms being bonded to iodide. Use of the bifunctional catalyst of the present invention for EDA production has distinct advantages over the use of other catalysts (US-A-5,371,274) in that accelerators like 3-picoline are not required and the separation of catalysts from product is made easier. The use of ionic bonding to the Group VIII metal complex also offers a further advantage in that the leaching of metal from the catalyst is minimized. The process is highly selective toward EDA, can be completed under short reaction times at high temperatures and pressures, and can proceed with recycling of the catalyst. The present invention provides a process for making EDA from Ac 2 O, hydrogen (H 2 ), carbon monoxide (CO), and acetic acid (HOAc) in the presence of an alkyl iodide and a bifunctional catalyst that is stable to hydrogenation and comprises an insoluble polymer having pendant quaternized heteroatoms, some of which heteroatoms are ionically bonded to anionic Group VIII metal complexes, the remainder of the heteroatoms being bonded to iodide. The bifunctional catalyst is a heterogeneous catalyst that contains an insoluble polymer having quaternized heteroatoms. The quaternized heteroatoms are quaternized by techniques well known in the art using an alkyl halide. Preferred alkyl halides contain from one to six carbon atoms (e.g., C 1 -C 4 alkyl). Preferred halides are iodide (I), chloride (Cl) or bromide (Br) and, more preferably iodide. A most preferred alkyl halide is methyl iodide. The polymer is an organic polymer that renders the catalyst insoluble in organic solvents. The polymer must be large enough and be sufficiently cross-linked to be insoluble. Organic polymers suitable for use as substrates for catalysts are well known (See, e.g., US-A-5,155,261). The polymer component of catalysts described in that patent are cross-linked vinylpyridine resins such as resins sold under the trade name Reillex™ by Reilley Tar and Chemical Corporation. Particularly suitable such vinylpyridine resins are Reillex™ 425 and Reillex™ HP, both of which are a poly-4-vinylpyridine cross-linked with divinylbenzene. Still other suitable polymers for use in a bifunctional catalyst are described in US-A-5,364,963. This patent describes improved cross-linked vinylpyridine resins. The improved resins have a degree of cross-linking between 30 and 60%. The vinylpyridine resins described in US-A-5,364,963 are prepared by co-polymerizing a vinylpyridine monomer with an aromatic compound having two vinyl groups as a cross-linking agent. Exemplary suitable cross-linking agents are aromatic divinyl compounds such as divinylbenzene and divinyl toluene. Suitable vinylpyridines of the polymer include 4-vinylpyridine, 2-vinylpyridine and 2- and 4-vinylpyridine derivatives having a C 1 -C 4 alkyl group such as a methyl group or ethyl group on the pyridine ring. Such vinylpyridine monomers can be used in conjunction with aromatic vinyl monomers such as styrene or vinyl toluene. The most preferred polymers are those available under the Reillex™ family of trademarks from Reilley Tar & Chemical Corporation of Indianapolis, Indiana and contain heteroatoms capable of being quaternized with an alkyl halide. As is well known in the art, heteroatoms capable of being quaternized with alkyl halides include nitrogen (N), sulfur (S), oxygen (O) and phosphorus (P). A preferred heteroatom for use in a bifunctional catalyst of the presently claimed invention is N. The N atom is preferably part of a pendant free base including tertiary amines, secondary amines, pyridines, or any nitrogen heterocycle group. The N can be substituted or unsubstituted. Following quaternization of the polymer heteroatoms (e.g., refluxing the polymer with an excess of methyl iodide in toluene), the polymer is ionically attached to anionic Group VIII metal complexes. The catalyst of the present invention utilizes a Group VIII metal selected from rhodium (Rh), platinum (Pt), palladium (Pd), iridium (Ir), ruthenium (Ru), cobalt (Co), and nickel (Ni). Preferred Group VIII metals are Rh, Ir and Pd. Rh is most preferred. The Group VIII metal catalyst used in the catalyst system is present in a catalytically effective amount and such catalytically effective amounts can be readily determined by those of ordinary skill in the art. The amount of Group VIII metal to be incorporated into the catalyst system typically ranges from 0.01 mol % to 10 mol % based on the Ac 2 O present, preferably from 0.03 to 5 mol %. In a preferred embodiment, an anionic Group VIII metal complex corresponds to the general formula [M(CO) a L b X c ] - where M is Rh, Ir or combinations thereof; L is an alkyl or acyl group; X is a halide ion; a is 1, 2, 3 or 4; b is 0 or 1; and c is 2 or 3. The sum of a, b and c is equal to or less than six (i.e., a+b+c ≤6). In another preferred embodiment, an anionic Group VIII metal complex corresponds to the general formula [M(CO) a L b X c ] -2 where M is Pd; L is an alkyl or acyl group; X is a halide ion; a is 1, 2, 3 or 4; b is 0 or 1; and c is 2 or 3. The sum of a, b and c is equal to or less than six (i.e., a+b+c ≤ 6). In a preferred embodiment, M is Rh, X is Cl, a is ≤4, b is 0, c is 2, the formula of the Group VIII metal complex is Rh 2 (CO) 4 Cl 2 , and the anionic species [Rh(CO) 2 I 2 ] - is incorporated into the polymer. Using the Rh complexes described above, the maximum Rh content that can be incorporated into the polymer is 16.9% by weight of the polymer or less. Because the catalyst used in a process of the present invention is bifunctional, it is important that only a portion of the quaternized heteroatoms be ionically bonded to the anionic Group VIII metal complex. By way of example, where the Group VIII metal is Rh, the total content of Rh in the catalyst is less than 16.9% by weight of the polymer. As shown hereinafter in the Examples, catalysts having between 2% and 6% by weight of Rh have been successfully used in the preparation of EDA. The quaternized heteroatoms not ionically bonded to the anionic Group VIII metal complex are bonded to iodide (I - ). This bonding of I to the catalyst eliminates the need for any extraneous promoter or accelerator in the overall reaction of making EDA from Ac 2 O. The hydrogenation can be carried out in a batch mode or a continuous mode over a wide range of temperatures. While the optimum temperature for practicing the present invention will depend upon process stoichiometry, the particular catalyst system utilized, as well as the precise combination of reaction conditions, suitable temperatures will range from 90°C up to 225°C. However, the most preferred temperatures range from 170°C to 210°C. The reaction can be carried out under a wide variety of pressures including pressures ranging from 500 psig (3.4 MPa) to 3000 psig (20.6 MPa). Preferred pressures range from 1000 psig (6.9 MPa) to 2000 psig (13.8 MPa) . Most preferred reaction conditions are a temperature of 190°C and a pressure of 1500 psig (10.3 MPa). The products of the reaction are analyzed by gas chromatography at various times during the reaction and also in a batch mode (i.e., at the end of the reaction). The catalyst can be removed by filtration and reused for a new feed without a loss in initial activity. Carbon monoxide and hydrogen usually are present in the reaction mixture in a stoichiometric ratio of from 10:90 to 60:40. Even more preferably, that stoichiometric ratio is 10:90. The desired product (EDA) is recovered from the product mixture which includes acetic acid and other reaction products. As will be evident, the present invention provides a convenient route for co-producing EDA and acetic acid. Reaction time is not critical in practicing the present invention and one of ordinary skill in the art can determine optimum reaction times based upon the enumerated reaction conditions, catalyst system and catalyst concentration presented herein. Reaction times required to produce a desired amount of EDA will also depend upon the reaction temperature and pressure. Typically, reaction times range from 0.5 hours to 4.0 hours. In contrast to prior art processes, no accelerator is necessary to achieve the catalytic reaction and the products are easily separated from the catalyst by filtration. The catalyst can be recycled without loss in activity. The following Examples are presented to further illustrate the scope of the present invention and are not intended to limit the scope thereof. EXAMPLE 1 Preparation Of Heterogeneous Catalyst A sample of Reillex™ 425 (24 g) was dried in an oven at 100°C for 14 hours. The dried polymer beads were placed in a flask which contained 125 ml of toluene and the mixture was refluxed for 30 minutes under nitrogen. After cooling to room temperature, 20 ml of methyl iodide was added and the resulting mixture was heated at 95°C for 48 hours and then stirred at room temperature for another 5 days. The yellow beads/powder was filtered and dried under vacuum for 8 hours. Approximately 0.36 g of the Group VIII metal complex Rh 2 (CO) 4 Cl 2 was dissolved in 100 ml of toluene. About 3.36 g of quaternized Reillex™ prepared in the previous step was added, the mixture was stirred for approximately 24 hours and the powder was filtered. No color was observed in the filtrate indicating that all the rhodium was on the polymer. The Reillex™ material contained about 5.1% by weight of rhodium. By using this method and by varying the amount of complex, a 2.24% Rh containing polymer was also prepared. These experiments were repeated using a Reillex™ high-porosity (HP) polymer. The samples were characterized by infrared spectroscopy, and showed two strong carbonyl bands at 2056 and 1984 cm-1, which bands are characteristic of the species [Rh(CO) 2 IX] - , where X = Cl or I and prove that the rhodium is attached ionically to the polymer. EXAMPLE 2 Catalyst Evaluation In the homogeneous catalyst reaction, 0.2 grams of RhCl 3 •3H 2 O, 0 or 1.5 grams of LiI, 0.8 grams of LiOAc, 0 or 9 grams of CH 3 I, and 22.5 grams of acetic anhydride in 135 ml of acetic acid as solvent were added to a 300 cm 3 reactor. The reactor was filled with a 1:1 CO/H 2 mixture and the reaction was run at 190°C. and a pressure of 1500 psig (14.3 MPa). After 2 hours, the reactor was cooled and analyzed by gas chromatography. The reaction was repeated without the use of the lithium salts. The heterogeneous catalytic reaction was repeated under an identical set of conditions, except that 1.8 grams of Reillex™ polymer containing 2.24% Rh was used instead of the rhodium chloride, and no Li salts were used. The reaction was also repeated with the Reillex™ polymer without methyl iodide. The results of these studies are summarized in the table. In the table, Ac 2 O conversion % equals moles of Ac 2 O reacted/moles of Ac 2 O added; turnover frequency equals moles of EDA formed/moles of Rh times hours; mass balance equals {2[EDA] + [DME] + [MeOAc] + [Ac 2 O] + [CH 4 ]}/moles of Ac 2 O added; and EDA selectivity % equals moles of EDA formed/moles of Ac 2 O reacted. Catalyst Ac 2 O conv. % EDA Sel. % Turnover frequency (h -1 ) Mass balance % homogeneous 85 47 29 72 heterogeneous 60 64 59 87 homogeneous, no Li salts 58.8 17.5 7 62 heterogeneous, no CH 3 I 1 100 0.8 100 The results show that the heterogeneous catalyst with CH 3 I has the highest selectivity and turnover frequency towards EDA. The homogeneous catalysts with the added Li salts have 4 times the turnover frequency than without the salts, however, both are inferior to the Reillex™ polymer without any added lithium salts. Finally, methyl iodide was found to be crucial to the reaction and not adding this reagent gave poor performance for the Reillex™ polymer.

Claims: A process for producing ethylidene diacetate which comprises reacting acetic anhydride, hydrogen, carbon monoxide and acetic acid in the presence of an alkyl iodide and a catalyst that is stable to hydrogenation characterized in that the catalyst is a bifunctional catalyst that comprises an insoluble polymer having pendant quaternized heteroatoms, some of which heteroatoms are ionically bonded to anionic Group VIII metal complexes, the remainder of the heteroatoms being bonded to iodide. A process according to Claim 1, wherein the anionic Group VIII metal complex contains rhodium, palladium or iridium. A process according to Claim 2, wherein the anionic Group VIII metal complex contains rhodium. A process according to Claim 3, wherein the anionic Group VIII metal complex has the formula [Rh(CO) 2 I 2 ] - . A process according to any one of the preceding claims, wherein the quaternized heteroatom is nitrogen. A process according to any one of the preceding claims, wherein the alkyl iodide is methyl iodide. A process according to any one of the preceding claims, wherein the insoluble polymer is a cross-linked vinylpyridine resin. A process according to Claim 7, wherein the insoluble polymer is a 4- or 2-vinylpyridine cross-linked with divinylbenzene. A process according any one of the preceding claims, wherein the reaction conditions comprise a temperature ranging from 90°C to 225°C and a pressure ranging from 3.4 MPa (500 psig) to 20.6 MPa (3000 psig). A process according to Claim 9, wherein the temperature ranges from 170°C to 210°C and the pressure ranges from 6.9 MPa (1000 psig) to 13.8 MPa (2000 psig). A process according to Claim 10, wherein the temperature is 190°C and the pressure is 10.3 MPa (1500 psig). A process according to any one of the preceding claims, wherein carbon monoxide (CO) and hydrogen (H 2 ) are present in a stoichiometric ratio (CO:H 2 ) of from 10:90 to 60:40. A process according to Claim 12, wherein the stoichiometric ratio of carbon monoxide to hydrogen is 10:90. A process according to any one of the preceding claims, wherein the catalyst has been prepared by reacting an insoluble polymer having quaternized heteroatoms with a Group VIII metal compound of the formula [M(CO) a L b X c ] - , where M is Rh or Ir, or combinations thereof; L is an alkyl or acyl group; X is a halide ion; a is 1, 2, 3 or 4; b is 0 or 1; and c is 2 or 3, where a+b+c ≤6. A process according to any one of Claims 1 to 3 and 5 to 13, wherein the catalyst has been prepared by reacting an insoluble polymer having quaternized heteroatoms with a Group VIII metal compound of the formula [M(CO) a L b X c ] 2- , where M is Pd; L is an alkyl or acyl group; X is a halide ion; a is 1, 2, 3 or 4; b is 0 or 1; and c is 2 or 3, where a+b+c ≤6. A process according to Claim 14, wherein M is Rh, X is Cl, a is ≤4, b is 0 and c is 2. A process according to Claim 15, wherein M is Pd, X is Cl, a is ≤4, b is 0 and c is 2. A process according to any one of the preceding claims, wherein the insoluble polymer has quaternized pyridine groups. A process according to any one of the preceding claims conducted in the absence of a separate accelerator. The use of a catalyst as defined in any one of Claims 1 to 5, 7 and 14 to 17 to catalyze the hydrogenation of acetic anhydride to ethylidene diacetate.

Inventors: RAMPRASAD DORAI, WALLER FRANCIS JOSEPH, RAMPRASAD, DORAI, WALLER, FRANCIS JOSEPH
Applicants: AIR PROD & CHEM, AIR PRODUCTS AND CHEMICALS, INC.
Application year: 1997
Main classification: C07C67
IPC codes: B01J31, C07C67