A METHOD FOR PREPARATION OF A HARDENING COMPOSITION

Abstract: A method for preparing concrete or mortar in which a mixture of a hydraulic binder, aggregates, water, and colloidal silica is prepared. The relative standard deviation of the particle size distribution by numbers of the colloidal silica is at least about 30 %. The invention also relates to concrete or mortar obtainable by the method.

Description: A method for preparation of a hardening composition The present invention relates to a method for preparation of concrete or mortar having improved strength and durability properties It also relates to concrete and mortar obtainable by the method, and to the use of said concrete, particularly as construction coπ- crete, as well as to the use of said mortar. Concrete is an artificial stone, commonly used as a building material, in which aggregates of suitable sizes are bound together by a matπx of a hydraulic binder Usually the aggregates are stones, in the broad sense, and the hydraulic binder a cement Concrete normally contains more aggregates than hydraulic binder, at least when calculated on volume basis The aggregates commonly have a particle size distπbution in the range of about 0 01 - 100 mm In order to prepare concrete the aggregates and the hydraulic binder are mixed with water Furthermore, concrete may contain certain additives such as setting and hardening additives, usually called accelerators, or workability additives, usually called superplastiαser Mortar is distinguished by the maximum size of its aggregates in general mortar contains only aggregates with a maximum size of about 2-4 mm, e g sand The concepts of cement, concrete, and mortar are furthermore extensively discussed in Ullman s encyclopedia of industπal chemistry, 5th ed , Vol A5, pp 490-538, VCH, Wein- heim, Germany 1986, hereby incorporated by reference Below, mortar is compπsed, for brevity s sake, by the concept of "concrete" One important property of concrete is obviously its strength An important parameter controlling concrete strength is the water cement ratio Other factors are the type of cement, cuπng conditions, moisture content, degree of hydratioπ of the cement, and the grading and shape of aggregates If sufficient water is provided, the hydration of cement will continue over a peπod of several years, and concrete strength may increase continuously during this time Conventionally, high strength is achieved by using a low water cement ratio, superplasticisers are often used in this connection as they permit the use of lower water cement ratios Another way of improving the strength is to add silica fume, which is a pozzolanic waste material from silicon and ferrosilicoπ industries, having particle sizes of about 0 1-0 2 mm Silica fume contains however uπburnt coal, that gives the concrete a dark, usually undesired, colour, as well as other impuπties, such as small quantities of metallic silicon that may cause explosion spelling of the concrete if it gets into contact with water Wagner and Hauck disclose in Hochsch Archit Bauwes - Weimar 40 (1994) 5/6/7, pp 183-7 the use of synthetically produced, chemically pure, and completely amor- phous silica having an average particle size of 15 nm, which they call "nanosilica", instead of silica fume which is referred to as 'microsilica" The nanosilica particles are indicated to have specific surface areas in the range of 180 - 230 m 2 /g, suggesting a rather narrow particle size distπbution; in this connection it should be said that according to "The Chemistry of Silica", Ralph K. Her, Wiley & Sons 1979, pp. 346-7 hereby incorporated by reference, the specific surface area of silica may be transformed into the corresponding particle size, and vice versa, using the formula 2720/A^ = d s , where s is the specific sur- face area in m /g and d s is the particle size in manometers The impuπty problems associated with silica fume are greatly overcome by the use of nanosilica The concrete strength development is indicated to be about the same as if microsihca were used, the early strength development, i.e. from 1 to 7 days, is inferred by table 2 of the reference to be at most 36% Agglomeration of the nanosilica is not discussed In EP-A2-0,519,155 a silica sol similar to nanosilica is used in shotcrete, primarily to provide the shotcrete with better cohesive properties, which in turn gives a lower degree of dust formation and rebound dunng the shotcreting The cohesive effect is accomplished by promoting aggregation of the colloidal sihca The disclosed silica sol, which have particle sizes in the range of 7^0 nm and specific surfaces in the range of 50-700 m 2 /g, shows a positive impact on the early strength compared to the effect of silica fume The development of compressive strength from one to seven days is, in absence of accelerators, about 58% Strength at later age is not mentioned It has however been found (by the inventors of the present invention) that aggregation, i e gelling, coagulation, floccuiation, or coarce- vation, of the colloidal silica has a negative influence on the long term strength when compared to concrete in which silica fume is used, especially when higher doses of silica colloid are used, or if not mixed properly with the concrete mixture this is probably due to encapsulation of the cement particles by the silica, which in turn is a hindrance to further hydratioπ of the cement particles No suggestion is given in EP-A2-0,519, 155 about the particle size distnbution The problem to be solved by the present invention is to provide a method for pre- paπng concrete having enhanced early strength whiie having a good long term strength This problem is soived by the method defined by appended claim 1 According to this method, a mixture of an hydraulic binder, aggregates, water, and colloidal silica, is prepared, whereby the relative standard deviation of the particle size distribution of the colloidal silica is at least about 30%, preferably at least about 35%, and in particular at least about 40% In this context "colloidal silica" means stable dispersions or sols of discrete particles of amorphous silica, this definition is the same as put forward in "The Chemistry of Silica" by Ralph K. Her, page 312, Wiley & Sons 1979 The relative standard deviation of the particle size distribution is the ratio between the mean particle size by numbers and the standard deviation of the particle size distribution "Variation coefficient" and "coefficient of vaπation" are terms synonymous to "relative standard deviation" The reason behind the positive effect of the broad particle size distribution on the strength para- meters is not known, although a plausible hypothesis is that the smaller particles have a stabilising influence on the larger ones against aggregation The present invention has the additional advantages of providing concrete having good durability, especially against chemical attacks from, for instance, chloπdes, sulphates, carbon dioxide, nitrogen oxides, and water Furthermore, the obtained concrete has a high ultimate strength and good frost resistance A particular advantage associated with the present invention is that the final concrete products have a most homogeneous and uniform strength The hydraulic binder is preferably a portland cement Preferably, the silica particles used in the present method have an average specific surface area below about 200 m 2 /g, in particular below about 180 m 2 /g, and preferably in the range of about 50-170 m 2 /g Above 200 m 2 /g it becomes increasingly difficult to counteract aggregation It is also preferred that the silica particles used in the present method have a particle size distπbution the standard deviation of which is at least about 20 nm The particle size distπbution may be monomodal, i e have one particle size with a higher frequency of occurrence than the immediately adjacent sizes, or be polymodal, i e have two or more such particle sizes The silica particles preferably have a mean particle size by numbers of about 7-50 nm, particularly of about 10-30 In the present method the particles are preferably added in form of an aqueous suspension containing about 8-60 percent by weight, in particular about 30-50 percent by weight, of silica The particles are generally of a size of about 5-200 nm, preferably 10-100 nm, and they are preferably added to the mixture in an amount of about 1-8 percent by weight, in particular about 1-5 percent by weight, and especially about 2 percent by weight, calculated on the weight of the hydraulic binder According to a preferred embodiment of the present invention the method also includes addition of a superplasticiser Any suitable superplasticiser may be used, but it is preferred that it compnses a suiphonated naphthalene-formaldehyde resin, a suiphonated meiamiπe-formaldehyde resin, or a suiphonated melamiπe-urea-formaldehyde resin, or a mixture thereof Exemplary of useful superplasticiser are those disclosed in WO 91/12214 and EP 692,465, both of which are hereby incorporated by reference A part or all of the superplasticiser is preferably added to the concrete mixture before the colloidal silica, as this way of adding has shown to have a stabilising effect on the colloidal silica In a particularly preferred embodiment of the present method about 35- 55 percent by weight, preferably about 55 percent by weight, of the supeφlasticiser, based on the total amount of superplasticiser, is added before the colloidal silica. The colloidal silica need not be stabilized by any stabilizing agent. It could, for instance, be silica sol prepared by the ion-exchange method as set forth in "The Colloid Chemistry of Silica", Horacio E. Bergna (Ed.), Ameπcan Chemical Society 1994. Preferably, however, the colloidal silica is stabilized, in particular with alkaline substances, advantageously by ions of alkaline metals, e.g. of Na, K, or Li, or by ammonium ions (NH 4 ), or a combination thereof. In a preferred embodiment the amount of stabilizing alkaline substance is governed by a molar ratio Si0 2 .M 2 0 of from about 150.1 to about 300:1 , whereby represents Na, K, Li, or NH 4 . Accelerators, such as conventionally used in shotcrete, are preferably not used, or oniy used in insignificant amounts, when prepaπng concrete according to the present method. According to a preferred embodiment of the present invention, concrete is pre- pared by mixing about 100 parts by weight of hydraulic binder; about 100-1000 parts by weight of aggregates; up to about 5 parts by weight of colloid silica; up to about 5 parts by weight of superplasticiser; and about 25-75 parts by weight of water The present invention also relates to concrete obtainable by the method according to the present invention as set forth above. According to one embodiment of the present invention concrete obtainable by said method is preferably used as construction concrete, which concept in the present context does not compπse shotcrete. The concept of "concrete" also compnses special concretes such as heavyweight concrete, lightweight concrete, fibre-reinforced concrete, and massive concrete. Below, the present invention is illustrated by means of non-limiting examples. Example 1 * An anionic silica sol stabilized with NH and containing less than 0.05% of Na 2 0 was used The specific surface area was 80 m 2 /g, the mean particle diameter by numbers was 35 nm with a standard deviation by numbers of 25 nm, i.e. the relative standard deviation was 71%. 95% by numbers of the particles had a size within the range from 5-150 nm The silica sol was present as a dispersion containing 40 percent by weight of the soiid particles, based on the dispersion. A mixture was prepared of 500g standard portland cement, 1500g standard sand 1,2,3, 7.5g superplasticiser "Mighty 100", which is a suiphonated naphthalene formaldehyde condensate available from the Japanese company Kao Chemicals, and 62.5g of the silica sol dispersion, whereby 50% of the total added amount of supeφlasticiser was added to the mixture before addition of the silica sol. The waterxement ratio was 0.4. Fresh density was 2195 kg/m 3 , and 4x4x16 cm mortar pπsm samples were cast. The samples were cured for one day in steal frames, five days in water, and later in a climate room at 20°C and 55% RH. The flexural and com- pressive strengths were measured after one, three, and seven days, by means of standard methods SS 13 42 33 and SS - EN 196.1 , respectively. The results are set forth in Table I below. Table I Days Flexural strength, MPa Compressive strength, MPa 1 5.4 30.7 3 8.8 40.2 7 6.5 50.7 strength development in 1-7 days, % 20 65 As can be seen in Table I the development of compressive strength from one to seven days clearly suφasses the development suggested in EP-A2-519.155, in fact even the actual compressive strength is higher. Example 2 Mortars were made with different amounts of an anionic colloidal silica sol containing 0.22% of Na 2 0 The specific surface area of the silica particles was 80 m 2 /g, the mean particle diameter by numbers was 62 nm with a standard deviation by numbers of 28 nm, i.e the relative standard deviation was 45%. 95% by numbers of the particles had a size within the range of 62 nm +/- 56 nm. The silica sol was present as a dispersion containing 50 percent by weight of the solid particles The mortars has cεment * sand ratios of 1 3. Standard portland cement, supplied by Cemeπta AB, Slite. Sweden, and standard sand, grade 1 , 2, and 3 were used Mighty 100 was used as supeφlasticiser in an amount of 1 5 percent by weight, based on the weight of the cement, about 50% of the piasticiser was added before the colloidal silica sol was added. Table II below shows the weight percentages of silica sol, based on the cement, together with the watercement ratios, the fresh densities, the air contents, and the consistencies, of the vanous mortars Pπsms having the dimensions 4x4x16 cm were cast of the mortars according to Table II They were demoulded after 1 day, cured in water for 5 days, and in a climate room at 55% RH and 22 β C for 22 days Flexural and compressive strengths were measured after 1 , 7, and 28 days, by means of standard method SS 1342 33 and SS-EN 196- 1 , respectively The results, given in MPa, are set forth in Table 111 below Table III KF3 KF5 KF8 Compressive 31 4 33.2 22.3 strength, 1 day 7 days 51 7 53 0 51 5 28 days 63 7 61 7 64 8 Flexural strength, 5 88 6 18 4 31 1 day 7 days 9.32 9.41 7 26 28 days 12 7 12 1 10.3 Regarding early strength, i e in 1-7 days, the best results were evidently obtained with mortar KF5 KF5 was subjected to some durability test Chloπde-ion penetration was measured by means of a method descπbed in an article by Tang et al entitled "Rapid determination of chloride diffusivity in concrete applying an electπc field", Mateπal Journal, Vol 89, No 1 , page 49 The American Concrete Institute 1992, hereby incorporated be reference, and the diffusion coefficient regarding chloride-ion penetration for KF3 was determined to 3.13x10 "12 m 2 /s, whereas a reference sample with no silica sol added showed a diffusion coefficient of 11 1x10 '12 m 2 /s. The carbonation depth was measured by spraying phenol- phthalein on a fresh broken surface, substantially peφendicular to the surface of the sample, and measuπng the length of penetration indicated by the phenolphtalein. The KF3 sample showed a penetration depth of 1.49 mm after 225 hours, while a reference sample with no silica sol added showed a penetration depth of 12.2 mm after an equally long period of time. Freeze-thaw salt resistance was determined by freezing a KF3 mortar pπsm in a saturated NaCI solution at -20 β C for 16 hours ant then thawing it in water at ambient temperature for 8 hours. This freeze-thaw sequence was repeated a number of times, whereby each sequence was denominated "a cycle". The freeze-thaw salt resistance was estimated on basis of the weight change of the prisms after certain numbers of cycles. A reference pπsm with no silica sol added showed a weight loss of 20% after 1 1 cycles, and after 16 cycles it was broken The KF3 pπsm. however, instead showed a weight gain (due to absorption of the salt solution) of about 0.3% at 16 cycles, and even at 35 cycles there was not any noticeable weight loss

Claims: Claims 1 A method for prepaπng concrete or mortar, characterised in that it compnses prepaπng a mixture of a hydraulic binder, aggregates, water, and colloidal silica, wherein the relative standard deviation of the particle size distπbutton by numbers of the colloidal silica is at least about 30% 2 A method according to any preceding claim, characterised in that the silica particles have an average specific surface area below about 200 m 2 /g 3 A method according to claim 2, characterised in that the particles have an average specific surface area of from about 50 to about 170 m 2 /g 4 A method according to any preceding claim, characterised in that the silica particles have a particle size distπbution with a standard deviation of at least about 20 nm 5 A method according to any preceding claim, characterised in that the silica particles have a mean particle size by numbers of from about 7 to about 50 nm 6 A method according to any preceding claim, characterised in that the particles are added with an aqueous suspension containing from about 15 to about 50 percent by weight of silica 7 A method according to any preceding claim characterised in that the particles are added in an amount of from about 1 to about 8 percent by weight, calculated on the hydraulic binder 8 A method according to any preceding claim, characterised in that the preparation of the mixture includes addition of a supeφlasti ser 9 A method according to claim 8, characterised in that part of the supeφlasticiser is added to the mixture before the silica particles 10 A method according to claim 9 characterised in that said part of plasticiser is from about 35 to about 55 weιght-% based on the total amount of superplasticiser added 11 A method according to any preceding claim, characterised in that the supeφlasticiser compnses a suiphonated naphthalene-formaldehyde resin, a suiphonated metamine-formaldehyde resin, or a suiphonated melamine-urea-formaldehyde resin 12 A method according to any preceding claim, characterised in that the silica particles are stabilized against aggregation by means of alkali metal ions or ammonium ions 13 A method according to any preceding claim, characterised in that no or only an insignificant amount of accelerator is added to the mixture 14 A method according to any preceding claim, characterised in that the concrete or mortar is prepared by mixing about 100 parts by weight of hydraulic binder from about 100 to about 1000 parts by weight of aggregates; up to about 5 parts by weight of colloid silica; up to about 5 parts by weight of supeφlasticiser; and from about 25 to about 75 parts by weight of water. 15. Concrete or mortar obtainable by the method according to any preceding claim. 16. Concrete or mortar according to claim 15, with the proviso that it is not shotcrete. 17. Concrete or mortar according to claim 15 or 16, characterised in that it is construction concrete. 18. Concrete or mortar according to anyone of claims 15-17, characterised in that it is mortar.

Inventors: BERGQVIST HANS, CHANDRA SATISH, BERGQVIST, HANS, CHANDRA, SATISH
Applicants: BERGQVIST HANS, CHANDRA SATISH, EKA CHEMICALS AB, BERGQVIST, HANS, CHANDRA, SATISH
Application year: 1997
Main classification: C04B22
IPC codes: C04B14, C04B22, C04B24, C04B28, C04B103