Polymer compositions

Abstract: A polymer composition including phosphorus substituents which comprises: (a) a phosphono - substituted carboxylic acid or an ester of such acid; and (b) a mono- or polyfunctional entity polymerisable with (a). Substances suitable for use as (a) are aliphatic or aromatic phosphono-substituted dicarboxylic acids or esters thereof. Substances suitable for use as (b) are polyhydric alcohols, aliphatic mononuclear or polynuclear aromatic polycarboxylic acids or esters or anhydrides thereof. Also suitable for use as (b) are aliphatic or aromatic polyamines and aliphatic or aromatic polyisocyanates or poly-epoxides.

Description: This invention relates to polymer compositions, in particular to polymer compositions including phosphono-substituents. Accordingly, the present invention provides a polymer composition comprising a polycondensation product of (a) a phosphono-substituted carboxylic acid or an ester of such acid; and (b) an entity selected from: (i) polyhydric alcohols; (ii) aliphatic, mononuclear aromatic or polynuclear aromatic polycarboxylic acids; (iii) esters or anhydrides of said acids (ii); (iv) aliphatic or aromatic polyamines, polyisocyanates or polyepoxides. Suitably, (a) may be an aliphatic or aromatic phosphono-substituted dicarboxylic acid or an ester of such an acid, for example phosphono-succinic acid or its dimethyl ester. Suitably, (b) may be an aliphatic or cycloaliphatic dihydric alcohol, such as ethylene glycol, propylene glycol, neopentyl glycol or 1, 4-dimethylol cyclohexane. Alternatively, (b) may be a trihydric alcohol such as glycerol. Again, (b) may be succinic acid, terephthalic acid, phthalic anhydride, naphthalic acid or naphthalic anhydride. Further (b), may be ethylene diamine. The present invention will be illustrated, merely by way of example, as follows: 1. Examples 1 to 3 The following polyester compositions were made, using phosphono-succinic acid and various polyhydric alcohols: Example 1: neopentyl glycol (NPG) Example 2: 1, 4-dimethylol cyclohexane (CHDM) Example 3: ethylene glycol (EG) 1.1 Procedure Equimolar amounts of phosphono-succinic acid and of each of the above-mentioned diols were charged to a 100ml round-bottomed flask and allowed to react at about 160°C for several hours while monitoring the acid number, until a very viscous liquid was produced. 1.2 Results The apparent molecular weights, measured by gel-permeation chromatography, are shown in the Table (below). These values are approximate as the polymers are very polar. The actual molecular weight would be expected to be higher. EXAMPLE Diol M w 1 NPG 9,638 2 CHDM 1,162 3 EG 19,004 2. Examples 4 and 5 Phosphono-succinic acid-terminated polyesters were made as follows: 2.1 Poly(oxyneopentyl succinate) - Phosphonoscuccinic acid terminated 2.1.1 Procedure Neopentyl glycol (81.797g, 0.786 mol) and succinic anhydride (77.000g, 0.769 mol) were charged to a 250 ml resin pot fitted with a mechanical stirrer, temperature probe, nitrogen inlet and distillation apparatus. The mixture was stirred and heated to 160°C by means of an isomantle. Once the mixture had melted, nitrogen was bubbled through it. The mixture was heated from 160 to 190°C over 40 h. A sample of the resulting intermediate product was taken after this time. The temperature was then lowered to 100°C and phosphonosuccinic acid (3.078g, 0.016 mol) added. The mixture was heated at 160°C for 5.5 h before being allowed to cool to room temperature. The product was crystallised from ethyl acetate to give a fine white powder. 2.1.2 Results Gel-permeation chromatography of the intermediate product indicated the molecular weight of the product was about 20,000 gmol -1 . 2.2 Poly(oxyneopentyl phthalate) - Phosphonosuccinic acid terminated A similar procedure to that described in 2.1.1 was used, replacing the succinic anhydride with phthalic anhydride. A solid polymer with emulsifying properties was produced.

Claims: A polymer composition characterised in that it is a polycondensation product of (a) a phosphono-substituted carboxylic acid or an ester of such acid; and (b) an entity selected from: (i) polyhydric alcohols; (ii) aliphatic, mononuclear aromatic or polynuclear aromatic polycarboxylic acids; (iii) esters or anhydrides of said acids (ii); (iv) aliphatic or aromatic polyamines, polyisocyanates or polyepoxides. A composition according to Claim 1, characterised in that (a) is an aliphatic or aromatic phosphono-substituted dicarboxylic acid or an ester of such acid. A composition according to Claim 2, characterised in that (a) is phosphono-succinic acid or an ester thereof, for example the dimethyl ester of phosphono-succinic acid. A composition according to Claim 1, characterised in that (b) is an aliphatic or cycloaliphatic dihydric alcohol, for example ethylene glycol, propylene glycol, neopentyl glycol, or 1,4-dimethylol cyclohexane. A composition according to Claim 1, characterised in that (b) is a trihydric alcohol, for example glycerol. A composition according to any one of Claims 1 to 3, characterised in that (b) is succinic acid, terephthalic acid, phthalic anhydride, naphthalic acid or naphthalic anhydride. A composition according to any one of Claims 1 to 3, characterised in that (b) is ethylene diamine.

Inventors: MITCHIE KAREN SARAH, ZAKIKHANI MOHSEN, MITCHIE, KAREN SARAH, ZAKIKHANI, MOHSEN
Applicants: ALBRIGHT & WILSON UK LTD, ALBRIGHT & WILSON UK LIMITED
Application year: 1997
Main classification: C08G63
IPC codes: C08G18, C08G59, C08G79, C08G63