SILICATE PHOSPHOR WITH A LONG AFTERGLOW AND MANUFACTURING METHOD THEREOF

Abstract: Disclosed is a long afterglow silicate luminescent materials which have a main chemical composition formula of: aMO·bM'O·cSiO2·dR: Eu x ,Ln y , wherein M represents one or more elements selected from a group consisting of Sr, Ca, Ba and Zn; M' represents one or more elements selected from a group consisting of Mg, Cd and Be; R represents one or two components selected from B 2 O 3 and P 2 O 5 ;Ln represents one or more elements selected from a group consisting of Nd, Dy, Ho, Tm, La, Pr, Tb, Ce, Mn, Bi, Sn and Sb; a, b, c, d, x and y are mole coefficients; wherein: 0.6≤a≤6, 0≤b≤5, 1≤c≤9, 0≤d≤0.7, 0.00001≤x≤0.2, and 0≤y≤0.3; these luminescent materials have long afterglow characteristic after absorbing short wavelength lights.

Description: This invention relates to phosphor with a long afterglow (i.e. long afterglow luminescent material) and more particularly to long afterglow silicate luminescent material and its manufacturing method. BACKGROUND OF THE INVENTION Since its invention in the nineteenth century, the traditional long afterglow phosphors of ZnS series have been improved greatly, several typical products have been produced, including ZnS:Cu (which emits green light), (CaSr)S:Bi (which emits blue light) and (ZnCd)S:Cu (which emits yellowish-orange light), and they have been applied in some commercial fields, however the shortcoming of these phosphors were: poor stability, easy to decompose in air, easy to turn gray even black when irradiated under sun light, only 0.5-2 hrs short luminescent afterglow time, and luminous brightness was weak etc., all these can not satisfy the requirement for practice use. In order to improve the brightness and afterglow time, radioactive luminescent materials were made, in which some radioactive elements such as Co, Ra, H 3 were added, although such elements can make the phosphor continuously give out light and the phosphor has once been used in air dashboard, clock fields etc.. however, the application of the phosphor was greatly confined due to the radioactive contamination and rather expensive price. The aluminate long afterglow luminescent material was invented at the beginning of the nineties ,as stated in China patent application laid open No.CN1053807A and China patent No.ZL92110744.7,its luminescent brightness ,long afterglow character and stability were obviously superior to the above sulphide series products, and it has already been used in the articles for daily use ,low illumination indicator board, clock etc.. However these phosphors still have bad anti-moisture character, and they have strict restriction over the raw material's purity and form, besides, the production cost was higher, as well as single luminescent color etc., therefore it also can not satisfy the requirement of usage very well. In 1968,T.L. Barry published the research results of luminescent spectrum and excitation spectrum of Me 3 MgSi 2 O 8 :Eu 2+ (Me=Ca, Sr and Ba) and Me 2 SiO 4 :Eu 2+ (Me=Sr and Ba)(J. Electrochem.Soc.V115 No.7, 733-738,1968; V115 No.11, 1181-1184,1968); then T.L. Barry published the research result in luminescent and excitation spectrum of BaMg 2 Si 2 O 7 :Eu 2+ (J. Electrochem. Soc. V117 No.3, 381-385,1970); Blasse,G etc. published fluorescence of Eu 2+ activated silicates (Philips Res. Rep.(1968),23(2),189-200) in 1968.However no report on silicate phosphor which having long afterglow property has been published. SUMMARY OF THE INVENTION In order to solve the above problem existed in the prior art, the invention provides a kind of series silicate long afterglow luminescent material that having various luminescent colors ,wide scope spectrum ,better anti-moisture property and nice stability as well as the long afterglow time and high afterglow brightness. This invention provides a new type of series long afterglow luminescent material, it is a kind of long afterglow luminescent material which use silicate as main matrix, rare earth ions and other ions as activator , and add some compounds of B or P to make the improvement of long afterglow performance, thus blue, green, yellow etc. multiple colors long afterglow luminescent characters were gained in the silicate system. The main chemical composition of long afterglow luminescent material in this invention can be expressed by the formula: aMO·bM'O·cSiO 2 ·dR:Eu x ,Ln y Wherein M represents one or more elements selected from a group consisting of Sr(strontium), Ca(calcium), Ba(barium) and Zn(zinc); M' represents one or more elements selected from a group consisting of Mg(magnesium), Cd(cadmium), and Be(beryllium); R represents one or two components selected from B 2 O 3 (boric anhydride) and P 2 O 5 (di-phosphoruspentoxide); Ln represents one or more elements selected from a group consisting of Nd(neodymiun), Dy(dysprosium), Ho(holmium), Tm(thulium), La(lanthanum), Pr(praseodymium), Tb(terbium), Ce(cerium) and Sb(antimony); a, b, c, d, x and y are mole coefficients, wherein :0.6≤a≤6, 0≤b≤5, 1≤c≤9, 0≤d≤0.7, 0.00001≤x≤0.2, and 0≤y≤0.3; these luminescent materials can give an emission spectrum between 420-650nm when excited by the short wavelength light of 250-500nm, its peak position is 450-580nm, and the long afterglow luminescent colors are blue, bluish-green, green, greenish-yellow or yellow. A preferred group of long afterglow luminescent materials according to this invention can be expressed by the main chemical composition formula (1) , wherein M represents one or two elements selected from Sr and Ca; M' represents Mg;R represents one or two components selected from B 2 O 3 and P 2 O 5 ; Ln represents one or more elements selected from a group consisting of Nd, Dy, Ho, wherein 0.6≤a≤4, 0.6≤b≤4, 1≤c≤5, and 0≤d≤0.4. In a preferred group of long afterglow luminescent materials acccording to this invention , the main matrix compound of the phosphor is : M 2 MgSi 2 O 7 or M 3 MgSi 2 O 8 wherein M represents Sr 1-2 Ca z , 0≤z≤1. In a further preferred group of long afterglow luminescent material according to this invention , the main chemical formula of the phosphor is: M 2 MgSi 2 O 7 :Eu,Ln or M 3 MgSi 2 O 8 :Eu,Ln, wherein M represents Sr 1-2 Ca z , 0≤z≤1. In the technique of making the long afterglow luminescent material of this invention, the compounds which containing the elements in the formula (1) are used as raw material, the mole proportion of elements in the raw material used to produce the luminescent material are as follows: M: 0.6-6 R: 0-0.7 in terms of B 2 O 3 and P 2 O 5 M': 0-5 Eu: 0.00001-0.2 Si: 1-9 Ln:0-0.3 wherein M represents one or more elements selected from a group consisting of Sr, Ca, Ba and Zn,; M' represents one or more elements selected from a group consisting of Mg, Cd and Be; R represents one or two elements selected from B and P; Ln represents one or more elements selected from a group consisting of Nd, Dy, Ho, Tm, La, Pr, Tb, Ce and Sb; Wherein M, M', Ln and Eu can be incorporated in the raw materials in the form of carbonate, sulphate, nitrate, phosphate, borate, acetate, oxalate, citrate, oxide, hydroxide or halogenide of the elements or their mixture; Si can be added in the form of SiO 2 ,silicic acid , silica gel or silicate; R can be added in the form of any compounds containing B or P, with the proviso that such compounds can form B 2 O 3 or P 2 O 5 in the subsequent sintering procedure; In order to produce the desired phosphor, high temperature solid-phase reaction method is used, first weighted above raw materials according to mole proportion, then ground it into fine and mixed homogeneously by using dry-mixing method, wet-mixing method in with solvents e.g. alcohol, acetone, are added and evaporated after the mixing or chemical reaction sol-gel process method; the mixture is placed in the crucible then sintered at a temperature between 1100∼1400 °C in furnace under a reducing atmosphere for a length of time in the range 2 to 50 hours depending on the oven's capacity and mixture's weight, for small amount mixture, it is usually fired for 2-5 hours, the reducing atmosphere is selected from H 2 (g), NH 3 (g), N 2 (g)+H 2 (g) and carbon powder, wherein g=gas. In order to improve the phosphor's quality, small amount of additives selected from the group consisting of the compounds NH 4 Cl, NH 4 F, CaF 2 , SrF 2 , Li 2 CO 3 , CaSO 4 , SrSO 4 ,SrHPO 4 ,and CaHPO 4 can be added into the raw material. After sintering, the sintered mixture is milled and sifted into desired particle size phosphor. BRIEF DESCRIPTION OF THE DRAWINGS FIG. 1 represents the emission spectrum(a) and the excitation spectrum(b) of Sr 2 MgSi 2 O 7 :Eu phosphor FIG. 2 represents the x-ray diffraction pattern of Sr 2 MgSi 2 O 7 :Eu phosphor FIG. 3 represents the emission spectrum(a) and the excitation spectrum (b)of Sr 2 MgSi 2 O 7 :Eu,Dy phosphor FIG. 4 represents the afterglow characteristic curve of Sr 2 MgSi 2 O 7 :Eu ,Dy phosphor FIG. 5 represents the emission spectrum(a) and the excitation spectrum(b) of Ca 2 MgSi 2 O 7 :Eu,Dy phosphor FIG. 6 represents the x-ray diffraction pattern of Ca 2 MgSi 2 O 7 :Eu,Dy phosphor FIG. 7 represents the afterglow characteristic curve of Ca 2 MgSi 2 O 7 :Eu ,Dy phosphor FIG. 8 represents the emission spectrum(a) and the excitation spectrum(b) of (Sr 0.5 Ca 0.5 ) 2 MgSi 2 O 7 :Eu,Dy phosphor FIG. 9 represents the x-ray diffraction pattern of (Sr 0.5 Ca 0.5 ) 2 MgSi 2 O 7 :Eu,Dy phosphor FIG. 10 represents the afterglow characteristic curve of (Sr 0.5 Ca 0.5 ) 2 MgSi 2 O 7 :Eu,Dy phosphor FIG. 11 represents the emission spectrum(a) and the excitation spectrum(b) of (Sr 0.75 Ca 0.25 ) 2 MgSi 2 O 7 :Eu,Dy phosphor FIG. 12 represents the emission spectrum(a) and the excitation spectrum(b) of (Sr 0.25 Ca 0.75 ) 2 MgSi 2 O 7 :Eu,Dy phosphor FIG. 13 represents the emission spectrum(a) and the excitation spectrum(b) of Sr 3 MgSi 2 O 7 :Eu,Dy phosphor FIG. 14 represents the x-ray diffraction pattern of Sr 3 MgSi 2 O 7 :Eu,Dy phosphor FIG. 15 represents the emission spectrum(a) and the excitation spectrum(b) of Ca 3 MgSi 2 O 8 :Eu,Dy phosphor FIG. 16 represents the x-ray diffraction pattern of Ca 3 MgSi 2 O 8 :Eu,Dy phosphor FIG. 17 represents the emission spectrum(a) and the excitation spectrum(b) of Ba 5 Si 8 O 21 :Eu,Dy phosphor DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS The measurement of sample's luminescent afterglow in this invention is to put the sample in a 50mm diameter,5mm deep disc, and keep it in dark room for more than 10h,then took it out and put it under standard D65 light 10001x illuminance, after irradiated for 10min use luminance meter measure its brightness changes with time. In the same time, excited the comparative sample under the same conditions, use comparative sample as 100 to count the sample's relative brightness value. For blue afterglow,the comparative sample is (CaSr)S:Bi; for yellow afterglow,the comparative sample is (ZnCd)S:Cu; and for green, bluish-green, greenish-yellow afterglow, the comparative sample is ZnS:Cu. Adopt x-ray diffraction method to define the phosphor's crystal structure and component, measured its x-ray diffraction value, and compared it with card value, so can define its main compound. Adopt fluorescent spectrophotometer to measure the phosphor's emission spectrum and excitation spectrum. A lot of research work indicated that in the chemical composition formula, the different of element in M and M', results in the different colors of long afterglow, as well as the different of phosphor's main crystal structure; the change of a, b, and c value have some influences to the brightness, crystal structure and luminescent color; the different elements component in R and Ln and the change of d, x, and y coefficient value have obvious influence to the brightness, whereas have no obvious influence to the main crystal structure. TABLE 1 shows a part of experimental results concerning the relationship between luminescent color and M,M',a,b. TABLE 1 Experimental condition let c=2.5, d=0.1, R=B 2 O 3 , x=0.005, y=0.04, Ln=Nd, select N 2 (90%)+H 2 (10%) as reducing atmosphere, synthetic temperature 1250-1320 °C, sintering time 4 hrs. Experiment of luminescent color Ex Element coefficient M: a Sr Ca Ba Zn M': b: Mg Cd Be Luminescent color 1 3 0 1 blue 2 0 3 1 green 3 2 0 1 blue 4 0 2 1 yellow 5 0.5 1.5 1 greenish-yellow 6 1.0 1.0 1 green 7 1.5 0.5 1 bluish-green 8 1 0 2 blue 9 0 1 2 yellow 10 0.2 0.8 1.9 0.1 greenish-yellow 11 0.5 0.5 2 green 12 0.7 0.3 1.9 0.1 bluish-green 13 1 0 3 blue 14 0 1 3 yellow 15 0.25 0.75 3.0 greenish-yellow 16 0.5 0.5 3.0 green 17 0.75 0.25 3 bluish-yellow 18 1 1.8 0.2 1 greenish-yellow 19 1.4 1.4 0.2 1 green 20 2.0 1 1 bluish-green 21 1.4 0.35 1.25 bluish-green 22 1.2 0.3 1.5 bluish-green 23 1.0 0.25 1.75 bluish-green 24 0.875 0.875 1.25 green 25 0.75 0.75 1.5 green 26 0.625 0.625 1.75 green 27 0.525 1.225 1.25 greenish-yellow 28 0.45 1.05 1.5 greenish-yellow 29 0.375 0.875 1.75 greenish-yellow 30 0.363 1.487 1.25 light yellow 31 0.225 1.275 1.5 light yellow 32 0.187 1.063 1.75 light yellow When M represents Sr or represents Sr,Ca,Ba and Zn, wherein Sr is the main element, Ca, Ba, and Zn are secondary elements, M' represents Mg or represents Mg,Cd and Be, wherein Mg is the main element, Cd and Be are secondary elements, the synthetic phosphor can presents blue-bluish-green afterglow luminescence after irradiated by short wavelength light of 250-450nm. Experiments indicate that the different value of a, b and c has certain influence to the phosphor's luminescent brightness and structure, when 0.6≤a≤4, 0.6≤b≤4 and 1≤c≤5, the phosphor presents brighter blue-bluish-green luminescent color, when 1.5≤a≤2,0.6≤b≤2, and 1.5≤c≤2.5, according to the x-ray diffraction pattern, the main matrix compound of the phosphor is defined as Sr 2 MgSi 2 O 7 as well as its crystal structure, see FIG. 2; when exceed the above coefficient scope, there may appear Sr 2 MgSi 2 O 7 compound, but the more other compounds exist too; when 2.7≤a≤3.3,0.8≤b≤1.2 and 1.7≤c≤2.3, the phosphor's main compound is Sr 3 MgSi 2 O 8 ,see FIG.14. When M represents Ca or represents Ca,Sr,Ba and Zn, wherein Ca is the main element, Sr, Ba and Zn are secondary elements, M' represents Mg or represents Mg,Cd and Be, wherein Mg is the main element, Cd and Be are secondary elements, the synthetic phosphor can presents green-yellow afterglow luminescent color after irradiated by the short wavelength light of 250-500nm. The same experiment indicates that the different value of a, b and c has certain influence to the phosphor's luminescent brightness and structure, when 0.6≤a≤4, 0.6≤b≤4, 1≤c≤5, the phosphor presents brighter green-yellow luminescence, when 1.5≤a≤2.4, 0.6≤b≤2, and 1.5≤c≤2.5, according to the x-ray diffraction pattern, the main matrix compound of the phosphor is defined as Ca 2 MgSi 2 O 7 as well as its crystal structure, see FIG. 6; when exceed the above coefficient scope, there may appear Ca 2 MgSi 2 O 7 compound, but the other compounds are more than the former; when 2.7≤a≤3.3, 0.8≤b≤1.2, and 1.7≤c≤2.3, the phosphor's main matrix compound is Ca 2 MgSi 2 O 8 , see FIG. 16. When M represents Sr and/or Ca, for easy to show ,adopt formula Sr 1-z Ca z , wherein 0≤z≤1, or represent Sr 1-z Ca z , Ba and Zn, wherein Sr 1-z Ca z are the main element, Ba and Zn are secondary elements, M' represents Mg or represents Mg, Cd and Be, wherein Mg is the main element, Cd and Be are secondary elements, with the change of z value, the synthetic phosphor presents blue-bluish-green-greenish-yellow-yellow afterglow luminescence: when z=0, color is blue; z=1, it's green-yellow; 0<z<0.5, mainly is bluish-green-green color; 0.5<z<1, mainly is green-greenish-yellow color; z=0.5 or near it is green. Just the same, the different values of a, b and c have certain influence to the phosphor's luminescent brightness and structure, when 0.6≤a≤4, 0.6≤b≤4 and 1≤c≤5, the phosphor presents bluish-green, green and greenish-yellow afterglow luminescent color, when 1.5≤a≤2.4 0.6≤b≤2 and 1.5≤c≤2.5, analyze its diffraction pattern, it is similar to that of Sr 2 MgSi 2 O 7 and Ca 2 MgSi 2 O 7 , considering with the element's match, the phosphor's main matrix compound can be deduced as (Sr 1-z Ca z ) 2 MgSi 2 O 7 , see FIG. 9; when the above coefficients scope are exceeded, the compound of (Sr 1-z Ca z ) 2 MgSi 2 O 7 can also be appeared, but there are more other components. Refer to the luminescent material's formula in Luminescence, when the crystal structure of phosphor have not yet been defined, it can be expressed by the main component of the phosphor, that is expressed by chemical composition formula; when the main compound and the crystal structure of the phosphor is defined, it should be expressed by chemical formula in this invention. According to the compound and crystal structure of the above phosphor in this invention, the main chemical formula of this phosphor is: M 2 MgSi 2 O 7 :Eu, Ln or M 3 MgSi 2 O 8 :Eu, Ln, wherein M presents Sr 1-z Ca 2 ,0≤z≤1. When M represents Ba ,4≤a≤6, b=0 and 6≤c≤9,the phosphor presents light green afterglow, according to x-ray diffraction pattern, its main compound is defined as Ba 5 Si 8 O 21 ,so the main chemical formula of this phosphor is Ba 5 Si 8 O 21 :Eu,Ln. When M represents Zn, 1≤a≤3, b=0 and 0.7≤c≤1.5, the phosphor presents light green afterglow, according to x-ray diffraction pattern, its main compound is defined as Zn 2 SiO 4 ,so the main chemical formula of this phosphor is Zn 2 SiO 4 ,:Eu,Ln. When M represents Sr 1-z Ca z 0≤z≤1, M' represents Mg, where 0-40% mol M and/or M' can be replaced by one or more elements selected from a group consisting of Ba, Zn, Cd and Be, the phosphor has long afterglow property, especially when 5-20% mol M and/or M' replaced by one or two of Ba and Cd, the phosphor have good luminescent performance. In chemical composition formula, without R and/or Ln element (that is when d and/or y is zero),the synthetic phosphor can also give out afterglow. If R and/or Ln exist in the phosphor, its luminescent afterglow intensity has been strengthened obviously, certainly the mole coefficient d and y may affect the afterglow luminescent intensity, adding different elements of Ln causes different luminescent intensity, two or more elements' adding will be even better than that of single element in luminescent effect. When y=0, the phosphor's chemical composition formula is aMO·bM'O·cSiO 2 ·dR:Eu x , Eu is the activator, its emission spectrum is characterized by Eu 2+ , that means Eu is the main activator ,the afterglow luminescent intensity changes with x value,, the suitable scope of x is :0.00001≤x≤0.2. When y>0, Ln exists in the phosphor, the experiment indicate that when one or more elements of Nd, Dy, Ho, Tm, La, Pr, Tb, Ce and Sb are doped, it will have certain enhance in phosphor's luminescent intensity, especially obvious effect can be seen in Nd,Dy and Ho, experiment indicate that when 0<y≤0.3, it has obvious enhancement function to the phosphor, whose afterglow luminescent intensity are much higher and the decay time are much longer than that of without Ln, see experiment in TABLE 2-10, according to the Luminescence theory, it can act as co- activator function. When d=0, the phosphor's chemical composition formula is aMO·bM'O·cSiO 2 ·dR:Eu x ,Ln y , this phosphor presents certain long afterglow effect the afterglow luminescent intensity changes with x and y value. When d>0,the adding of R component can obviously improve the phosphor's long afterglow luminescent intensity compared with that of d=0, the R component of the phosphor can be the compounds of B or p, i.e. B 2 O 3 , H 3 BO 3 , P 2 O 5 , H 3 PO 4 , (NH 4 ) 2 HPO 4 , NH 4 H 2 PO 4 etc., adding of these components can improve the phosphor's long afterglow luminescent intensity, reduce the phosphor's synthetic temperature, improve the phosphor's synthetic quality, and loosened the powder of synthetic phosphor, increase the product rate. The influence of R component to the phosphor's luminescent property, see TABLE 2. TABLE 2 Select bluish-green phosphor in this experiment, let M=Sr 0.75 Ca 0.25 , M'=Mg, R=B 2 O 3 and/or P 2 O 5 , Ln=Dy, a=1.5, b=1.5, c=2.5, x=0.01, y=0.08, NH 3 (g) as reducing atmosphere, and synthetic temperature at 1280 °C. The R and Ln component function experiment Ex Chemical composition formula Relative intensity afterglow 10° 60° 1 1.5(Sr 0.75 Ca 0.25 )O·1.5MgO·2.5SiO 2 :Eu 0.01 40.1 102 2 1.5(Sr 0.75 Ca 0.25 )O·1.5MgO·2.5SiO 2 :0.1B 2 O 3 :EU 0.01 114 176 3 1.5(Sr 0.75 Ca 0.25 )O·1.5MgO·2.5SiO 2 :0.5P 2 O 3 :Eu 0.01 94.6 137 4 1.5(Sr 0.75 Ca 0.25 )O·1.5MgO·2.5SiO 2 :0.1B 2 O 3 ·0.05P 2 O 5 :Eu 0.01 121 182 5 1.5(Sr 0.75 Ca 0.25 )O·1.5MgO·2.5SiO 2 :Eu 0.01 Dy 0.08 772 1540 6 1.5(Sr 0.75 Ca 0.25 )O·1.5MgO·2.5SiO 2 :0.1B 2 O 3 :Eu 0.03 Dy 0.08 2541 4808 7 1.5(Sr 0.75 Ca 0.25 )O·1.5MgO·2.5SiO 2 :0.05P 2 O 3 :Eu 0.03 Dy 0.08 1724 3946 8 1.5(Sr 0.75 Ca 0.25 )O·1.5MgO·2.5SiO 2 :0.1B 2 O 3 ·0.05P 2 O 5 :Eu 0.01 Dy 0.08 2638 4972 The influence of R's amount to the phosphor's luminescent property ,show in TABLE 3. TABLE 3 select blue and green phosphor, in experiment 1-8, let M=Sr, M'=Mg, a=2, b=1, c=2, R=B 2 O 3 , x=0.004. Experiment 9-14 is green phosphor, wherein M=Sr 0.5 Ca 0.5 , M'=Mg, a=2, b=1, c=2.3, R=P 2 O 5 , Ln=Dy ,x=0.004, y=0.01. The effect of R component experiment: Ex. Chemical composition formula R (raw material) d Relative afterglow intensity synthesizing temperature (C°) 10' 60' 1 2SrO·MgO·2SiO 2 :Eu 0.004 0 0 37.4 100 1350 2 2SrO·MgO·2SiO 2 ·0.01B 2 O 3 :Eu 0.004 2H 3 BO 3 0.01 78.7 115.4 1340 3 2SrO·MgO·2SiO 2 ·0.05B 2 O 3 :Eu 0.004 2H 3 BO 3 0.05 134.8 169.2 1330 4 2SrO·MgO·2SiO 2 ·0.1B 2 O 3 :Eu 0.004 2H 3 BO 3 0.1 132.4 158.5 1320 5 2SrO·MgO·2SiO 2 ·0.2B 2 O 3 :Eu 0.004 2H 3 BO 3 0.2 109.2 127 1310 6 2SrO·MgO·2SiO 2 ·0.3B 2 O 3 :Eu 0.004 2H 3 BO 3 0.3 94.5 102 1280 7 2SrO·MgO·2SiO 2 ·0.5B 2 O 3 :Eu 0.004 2H 3 BO 3 0.5 73.4 96.4 1230 8 2SrO·MgO·2SiO 2 ·0.7B 2 O 3 :Eu 0.004 2H 3 BO 3 0.7 42.1 74.2 1150 9 2(Sr 0.5 Ca 0.5 )O·MgO·2.3SiO 2 :Eu 0.004 Dy 0.01 0 0 482.4 1263.2 1350 10 2(Sr 0.5 Ca 0.5 )O·MgO·2.3SiO 2 ·0.05P 2 O 5 :Eu 0.004 Dy 0.01 2NH 4 H 2 PO 4 0.05 613 1804 1340 11 2(Sr 0.5 Ca 0.5 )O·MgO·2.3SiO 2 ·0.1P 2 O 5 :Eu 0.004 Dy 0.01 2NH 4 H 2 PO 4 0.1 1034 2542 1320 12 2(Sr 0.5 Ca 0.5 )O·MgO·2.3SiO 2 ·0.2P 2 O 5 :Eu 0.004 Dy 0.01 2NH 4 H 2 PO 4 0.2 807 2326 1310 13 2(Sr 0.5 Ca 0.5 )O·MgO·2.3SiO 2 ·0.3P 2 O 5 :Eu 0.004 Dy 0.01 2NH 4 H 2 PO 4 0.3 721 1702 1250 14 2(Sr 0.5 Ca 0.5 )O·MgO·2.3SiO 2 ·0.5P 2 O 5 :Eu 0.004 Dy 0.01 2NH 4 H 2 PO 4 0.5 501 1271 1200 Experiment indicates when 0<d≤0.7, the phosphor's luminescent intensity can be influenced, the amount of R(d) at 0<d≤0.4 is better. The exist of R component, analyzed from phosphor's x-ray diffraction pattern, have no obvious influence on the above phosphor's crystal structure and compound, its main compound is silicate component, however, B and P elements existed in phosphor are defined by spectrometric analysis , that means the phosphor contains B and P components, according its chemical composition, marked as B 2 O 3 and P 2 O 5 . A part of the long afterglow luminescent materials in this invention is described as follows: (1)Blue long afterglow luminescent material When M=Sr, M'=Mg, R=B 2 O 3 ,a=2, b=1, c=2, d=0.1, the phosphor's chemical composition formula is :2SrO-MgO-2SiO 2 -0.1B 2 O 3 :Eu x ,Ln y , change the value of x, the elements of Ln and the value of y, the experiment results shown in TABLE 4. In Table 4 samples 1-1 to 1-7, 9-1 to 9-3, 10-1 to 10-3, 11-1 to 11-3 12-1 to 12-3 and 13-1 to 13-3 are comparative Experiment Chemical composition formula Relative afterglow intensity 10' 60' 1-1 2SrO·MgO·2SiO 2 ·0.1B 2 O 3 ·Eu 0.0001 67 114 1-2 2SrO·MgO·2SiO 2 ·0.1B 2 O 3 ·Eu 0.0004 81 122 1-3 2SrO·MgO·2SiO 2 ·0.1B 2 O 3 ·Eu 0.001 124 143 1-4 2SrO·MgO·2SiO 2 ·0.1B 2 O 3 ·Eu 0.004 136 178 1-5 2SrO·MgO·2SiO 2 -0.1B 2 O 3 ·Eu 0.001 130 167 1-6 2SrO·MgO·2SiO 2 -0.1B 2 O 3 ·Eu 0.01 91 121 1-7 2SrO·MgO·2SiO 2 -0.1B 2 O 3 ·Eu 0.2 80 102 2-1 2SrO·MgO·2SiO 2 ·0.1B 2 O 3 ·Eu 0.004 Nd 0.001 621 734 2-2 2SrO·MgO·2SiO 2 ·0.1B 2 O 3 ·Eu 0 004 Nd 0.003 884 896 2-3 2SrO·MgO·2SiO 2 ·0.1B 2 O 3 ·Eu 0 004 Nd 0 01 1130 1175 2-4 2SrO·MgO·2SiO 2 ·0.1B 2 O 3 ·Eu 0 004 Nd 0.04 1527 1847 2-5 2SrO·MgO·2SiO 2 ·0.1B 2 O 3 ·Eu 0 004 Nd 0.1 862 859 2-6 2SrO·MgO·2SiO 2 ·0.1B 2 O 3 ·Eu 0.004 Nd 0.3 645 692 3-1 2SrO·MgO·2SiO 2 ·0.1B 2 O 3 ·Eu 0.004 Dy 0.0005 592 913 3-2 2SrO·MgO·2SiO 2 ·0.1B 2 O 3 ·Eu 0.004 Dy 0.004 927 1754 3-3 2SrO·MgO·2SiO 2 ·0.1B 2 O 3 ·Eu 0.004 Dy 0.01 1108 2100 3-4 2SrO·MgO·2SiO 2 ·0.1B 2 O 3 ·Eu 0.004 Dy 0 04 1658 3947 3-5 2SrO·MgO·2SiO 2 ·0.1B 2 O 3 ·Eu 0.004 Dy 0.03 1421 3136 3-6 2SrO·MgO·2SiO 2 ·0.1B 2 O 3 ·Eu 0.004 Dy 0.15 1215 2306 3-7 2SrO·MgO·2SiO 2 ·0.1B 2 O 3 ·Eu 0 004 Dy 0 3 823 1214 4-1 2SrO·MgO·2SiO 2 ·0.1B 2 O 3 ·Eu 0.004 Ho 0.0004 827 1512 4-2 2SrO·MgO·2SiO 2 ·0.1B 2 O 3 ·Eu 0.004 Ho 0.001 1014 1894 4-3 2SrO·MgO·2SiO 2 ·0.1B 2 O 3 ·Eu 0.004 Ho 0.05 1472 2246 4-4 2SrO·MgO·2SiO 2 ·0.1B 2 O 3 ·Eu 0.004 Ho 0.1 1034 1675 5-1 2SrO·MgO·2SiO 2 ·0.1B 2 O 3 ·Eu 0.004 Tm 0.001 289 310 5-2 2SrO·MgO·2SiO 2 ·0.1B 2 O 3 ·Eu 0.004 Tm 0.05 378 420 5-3 2SrO·MgO·2SiO 2 ·0.1B 2 O 3 ·Eu 0.004 Tm 0.1 384 456 6-1 2SrO·MgO·2SiO 2 ·0.1B 2 O 3 ·Eu 0.004 La 0.001 204 189 6-2 2SrO·MgO·2SiO 2 ·0.1B 2 O 3 ·Eu 0.004 La 0.005 235 267 6-3 2SrO·MgO·2SiO 2 ·0.1B 2 O 3 ·Eu 0.004 La 0.02 269 317 7-1 2SrO·MgO·2SiO 2 ·0.1B 2 O 3 ·Eu 0.004 Pr 0.001 275 292 7-2 2SrO·MgO·2SiO 2 ·0.1B 2 O 3 ·Eu 0.004 Pr 0.004 254 264 7-3 2SrO·MgO·2SiO 2 ·0.1B 2 O 3 ·Eu 0.004 Pr 0.02 250 253 8-1 2SrO·MgO·2SiO 2 ·0.1B 2 O 3 ·Eu 0.004 Tb 0.001 224 267 8-2 2SrO·MgO·2SiO 2 ·0.1B 2 O 3 ·Eu 0.004 Tb 0.004 284 368 8-3 2SrO·MgO·2SiO 2 ·0.1B 2 O 3 :Eu 0.004 Tb 0.02 230 276 9-1 2SrO·MgO·2SiO 2 ·0.1B 2 O 3 ·Eu 0.004 Ca 0.0017 278 367 9-2 2SrO·MgO·2SiO 2 ·0.1B 2 O 3 ·Eu 0.004 Ca 0.007 238 262 9-3 2SrO·MgO·2SiO 2 ·0.1B 2 O 3 ·Eu 0.004 Ca 0.0027 224 237 10-1 2SrO·MgO·2SiO 2 ·0.1B 2 O 3 ·Eu 0.004 Mn 0.001 264 290 10-2 2SrO·MgO· 2 SiO 2 ·0.1B 2 O 3 ·Eu 0.004 Mn 0.005 273 287 10-3 2SrO·MgO·2SiO 2 ·0.1B 2 O 3 ·Eu 0.004 Mn 0.02 232 264 11-1 2SrO·MgO·2SiO 2 ·0.1B 2 O 3 ·Eu 0.004 Bi 0.001 254 347 11-2 2SrO·MgO·2SiO 2 ·0.1B 2 O 3 Eu 0.004 Bi 0.003 314 472 11-3 ZSrO·MgO·2SiO 2 ·0.1B 2 O 3 ·Eu 0.004 Bi 0.02 421 564 12-1 2SrO·MgO·2SiO 2 ·0.1B 2 O 3 ·Eu 0.004 Sb 0.0016 195 227 12-2 2SrO·MgO·2SiO 2 ·0.1B 2 O 3 ·Eu 0.004 Sb 0.006 184 215 12-3 2SrO·MgO·2SiO 2 ·0.1B 2 O 3 ·Eu 0.004 Mn 0.025 147 169 13-1 2SrO·MgO·2SiO 2 ·0.1B 2 O 3 ·Eu 0.004 Sn 0.001 124 138 13-2 2SrO·MgO·2SiO 2 ·0.1B 2 O 3 ·Eu 0.004 Sn 0.005 278 367 13-3 2SrO·MgO·2SiO 2 ·0.1B 2 O 3 ·Eu 0.004 Sn 0.02 167 236 14-1 2SrO·MgO·2SiO 2 ·0.1B 2 O 3 ·Eu 0.004 Nd 0.02 Dy 0.01 1831 3150 15-1 2SrO·MgO·2SiO 2 ·0.1B 2 O 3 ·Eu 0.004 Nd 0.02 Sn 0.01 1672 2804 16-1 2SrO·MgO·2SiO 2 ·0.1B 2 O 3 ·Eu 0.004 Dy 0.02 Bi 0.01 1837 4356 Comparative sample Zn:S:Cu 100 100 The experimental phosphor shown in TABLE 4 can display blue afterglow luminescence after irradiated under sun light, fluorescent lamp or ultraviolet lamp; when excited under 365nm ultraviolet light, it can give 420-550nm broad band emission spectrum, with peak position near 469nm; its excitation spectrum is 250-450nm broad band spectrum, when monitoring at 469nm, indicate this phosphor has strong absorbing ability to short wavelength light, its main matrix compound is defined as Sr 2 MgSi 2 O 7 through x-ray diffraction pattern, the peak position of spectrum can exert certain shift for the different adding component. FIG.1 (a),(b) and FIG.2 are emission spectrum, excitation spectrum and x-ray diffraction pattern of the experimental phosphor 1-4 respectively, whose emission spectrum peak position is 469nm; FIG.3(a),(b) are emission spectrum and excitation spectrum of the experimental phosphor 3-4,its emission spectrum peak position is 470nm. 1.If y=0 in the chemical composition formula, that means no Ln ion exist, the amount of Eu(x) added may have certain influence to afterglow intensity, shown as experiment 1-1∼7 in TABLE 4. Compared with comparative sample (CaSr)S:Bi, this phosphor presents certain long afterglow luminescent effect. Further experiment indicates that when the Eu's amount x is less than 0.00001 mol or more than 0.2 mol, its luminescent intensity is weak, so 0.00001≤x≤0.2 is defined. 2.If x=0.004, Ln=Nd, the afterglow intensity corresponding to the changes of the amount of Nd(y) added, see experiment 2-1∼6 in TABLE 4, 0.0001≤y≤0.3 are suitable for the amount of Nd(y) added, it can be seen that afterglow intensity is obviously stronger than that of experiment 1-1∼7, this indicate that the adding of Nd can strengthen the phosphor's luminescent performance. Draw a log-log afterglow afterglow characteristic curve concerning the phosphor's luminescent afterglow varies with the decay time, this curve is almost a straight line, its decay time can prolong to more than 20 hrs when afterglow brightness reach the eye's lowest visual luminosity 0.32mcd/m 2 . 3.If x=0.004, Ln=Dy, the afterglow effect corresponding the change of the amount of Dy(y) added ,see experiment 3-1∼7 in TABLE 1,0.0001≤y≤0.3 are suitable for the amount of Dy(y) added, it can be seen that afterglow intensity is obviously stronger than that of experiment 1-1∼7, this indicates that the adding of Dy strengthened the phosphor's luminescent performance. Draw a log-log afterglow characteristic curve concerning the phosphor's luminescent afterglow varies with the decay time, this curve was almost a straight line, see FIG.4, its decay time can prolong to more than 35 hrs by eye's lowest visual luminosity. 4.If x=0.004, Ln is Ho, Tm, La, Pr, Tb, Ce, Mn, Bi, Sb, Sn and double elements Nd, Dy; Nd, Sn; and Dy, Bi respectively ,its afterglow effect that corresponding the amount of Ly(y) added ,see experiment 4∼16 in TABLE 4. From the above results, it can be seen that these phosphor's luminescent afterglow effect are obviously superior to that of the comparative phosphor. Especially the adding of Nd, Dy, Ho, Bi, Sn makes the effect even better. According to the crystal structure and main compound of the above phosphor, the blue series phosphor's chemical formula is Sr 2 MgSi 2 O 7 :Eu,Ln. (2)Yellow long afterglow luminescent material When M=Ca, M'=Mg, R=B 2 O 3 , a=2, b=1, c=2, d=0.15, the phosphor's chemical composition formula is: 2CaO·MgO·2SiO 2 ·0.15B 2 O 3 :Eu x ,Ln y , change the value of x, the elements of Ln, and the value of y, its experimental results shown in TABLE 5. In Table 5, samples 1-1 to 1-7, 7-1 to 7-2 and 8-1 to 8-2 are comparative. Experiment Chemical composition formula Relative afterglow intensity 10' 60' 1-1 2CaO·MgO·2SiO 3 ·0.IB 2 O 3 ·Eu 0.0001 127 217 1-2 2CaO·MgO·2SiO 2 ·0.1B 2 O 3 ·Eu 0.0004 201 404 1-3 2CaO·MgO·2SiO 2 ·0.1B 2 O 3 ·Eu 0.001 238 417 1-4 2CaO·MgO·2SiO 2 ·0.1B 2 O 3 ·Eu 0.004 223 389 1-5 2CaO·MgO·2SiO 2 -0.1B 2 O 3 ·Eu 0.001 152 345 1-6 2CaO·MgO·2SiO 2 -0.1B 2 O 3 ·Eu 0.001 56 127 1-7 2CaO·MgO·2SiO 2 -0.1B 2 O 3 ·Eu 0.2 45 87 2-1 2CaO·MgO·2SiO 2 ·0.1B 2 O 3 ·Eu 0.004 Dy 0.0005 387 1071 2-2 2CaO·MgO·2SiO 2 ·0.1B 2 O 3 ·Eu 0.0004 Dy 0.01 832 1324 2-3 2CaO·MgO·2SiO 2 ·0.1B 2 O 3 ·Eu 0.001 Dy 0.005 914 1451 2-4 2CaO·MgO·2SiO 2 ·0.1B 2 O 3 ·Eu 0.004 Dy 0.15 597 921 3-1 2CaO·MgO·2SiO 2 ·0.1B 2 O 3 ·Eu 0.004 Nd 0.0002 512 714 3-2 2CaO·MgO·2SiO 2 ·0.1B 2 O 3 ·Eu 0.004 Nd 0.01 490 837 4-1 2CaO·MgO·2SiO 2 ·0.1B 2 O 3 ·Eu 0.004 Ho 0.01 482 694 4-2 2CaO·MgO·2SiO 2 ·0.1B 2 O 3 ·Eu 0.004 Ho 0.05 531 728 5-1 2CaO·MgO·2SiO 2 ·0.1B 2 O 3 ·Eu 0.004 Tm 0.01 417 623 5-2 2CaO·MgO·2SiO 2 ·0.1B 2 O 3 ·Eu 0.004 Tm 0.05 465 704 6-1 2CaO·MgO·2SiO 2 ·0.1B 2 O 3 ·Eu 0.004 Ce 0.0015 317 572 6-2 2CaO·MgO·2SiO 2 ·0.1B 2 O 3 ·Eu 0.004 Ce 0.005 354 643 7-1 2CaO·MgO·2SiO 2 ·0.1B 2 O 3 ·Eu 0.004 Sn 0.001 397 845 7-2 2CaO·MgO·2SiO 2 ·0.1B 2 O 3 ·Eu 0.004 Sn 0.004 492 897 8-1 2CaO·MgO·2SiO 2 ·0.1B 2 O 3 ·Eu 0.004 Bi 0.001 426 823 8-2 2CaO·MgO·2SiO 2 ·0.1B 2 O 3 ·Eu 0.004 Bi 0.04 549 864 9-1 2CaO·MgO·2SiO 2 ·0.1B 2 O 3 ·Eu 0.004 Dy 0.02 Nd 0.01 965 1534 10-1 2CaO·MgO·2SiO 2 ·0.1B 2 O 3 ·Eu 0.004 Dy 0.02 Bi 0.01 873 1424 Comparative sample (ZnCd)S:Cu 100 100 The experimental phosphor can display yellow afterglow luminescence after irradiated under sunlight, fluorescent lamp or ultraviolet lamp; when excited under 365nm ultraviolet light the phosphor can give 420-650nm wide band emission spectrum, peak value at 535nm; its excitation spectrum is broad band spectrum between 250-500nm when monitoring at 535nm, indicates this phosphor has strong absorbing ability to short wavelength light; its main matrix compound is defined as Ca 2 MgSi 2 O 7 ; Due to the different adding components, its spectrum peak position can be shifted certain displacement. FIG.5(a),(b) and FIG.6 are the emission spectrum, excitation spectrum and x-ray diffraction pattern of the experimental phosphor 2-3 respectively, its emission spectrum peak position is at 535nm. 1.If y=0 in the chemical composition formula, the amount of Eu(x) added can has certain influence to the afterglow intensity, see the experiment 1-1∼7 in TABLE 5. 2.If x=0.004, Ln=Dy, the relationship between the amount of Dy(y) added and the afterglow effect shown in TABLE 5 of experiment 2-1∼4 ,it can be seen that the adding of Dy enhance the phosphor's luminescent performance, experiment indicate that 0.0001≤y≤0.2 are better for the amount of Dy added, FIG.7 is log-log characteristic curve of experiment 2-3 phosphor's luminescent afterglow changes with the decay time. 3.If x=0.004, Ln is Nd, Ho, Tm, Ce, Sn, Bi and double Dy, Nd and Dy, Bi respectively, the relationship between the adding amount and afterglow effect are superior to that of comparative sample. According to the above phosphor's main compound, the chemical formula of the yellow series phosphor is Ca 2 MgSi 2 O 7 :Eu,Ln. (3)Green long afterglow luminescent material When M=Sr 0.5 Ca 0.5 , M'=Mg, R=B 2 O 3 , a=2, b=1, c=2, d=0.05, the chemical composition formula is: 2(Sr 0.5 Ca 0.5 )O·MgO·2SiO 2 ·0.05B 2 O 3 : Eu x ,Ln y , change the value of x, the elements of Ln, and the value of y, its experimental results shown in TABLE 6. In Table 6, samples 1-1 to 1-6, 7-1 to 7-3 and 10-1 to 10-3 are comparative Experiment Chemical composition formula Relative afterglow intensity 10' 60' 1-1 2(Sr 0.5 Ca 0.5 )O·MgO·2SiO 2 ·0.05B 2 O 3 :Eu 0.005 89.5 226.3 1-2 2(Sr 0.5 Ca 0.5 )O·MgO·2SiO 2 ·0.05B 2 O 3 :Eu 0.001 105.3 247.4 1-3 2(Sr 0.5 Ca 0.5 )O·MgO·2SiO 2 ·0.05B 2 O 3 :Eu 0.004 89.5 323 1-4 2(Sr 0.5 Ca 0.5 )O·MgO·2SiO 2 ·0.05B 2 O 3 :Eu 0.01 52.6 215 1-5 2(Sr 0.5 Ca 0.5 )O·MgO·2SiO 2 ·0.05B 2 O 3 :Eu 0.02 42.1 110.5 1-6 2(Sr 0.5 Ca 0.5 )O·MgO·2SiO 2 ·0.05B 2 O 3 :Eu 0.1 21 57.9 2-1 2(Sr 0.5 Ca 0.5 )O·MgO·2SiO 2 ·0.05B 2 O 3 :Eu 0.005 Dy 0.0005 562 1515 2-2 2(Sr 0.5 Ca 0.5 )O·MgO·2SiO 2 ·0.05B 2 O 3 :Eu 0.005 Dy 0.004 1237 3333 2-3 2(Sr 0.5 Ca 0.5 )O·MgO·2SiO 2 ·0.05B 2 O 3 :Eu 0.005 Dy 0.008 1206 3158 2-4 2(Sr 0.5 Ca 0.5 )O·MgO·2SiO 2 ·0.05B 2 O 3 :Eu 0.005 Dy 0.04 1246 3421 2-5 2(Sr 0.5 Ca 0.5 )O·MgO·2SiO 2 ·0.05B 2 O 3 :Eu 0.005 Dy 0.08 1219 3591 3-1 2(Sr 0.5 Ca 0.5 )O·MgO·2SiO 2 ·0.05B 2 O 3 :Eu 0.005 Nd 0.0064 1127 2815 3-2 2(Sr 0.5 Ca 0.5 )O·MgO·2SiO 2 ·0.05B 2 O 3 :Eu 0.005 Nd 0.008 1212 3032 3-3 2(Sr 0.5 Ca 0.5 )O·MgO·2SiO 2 ·0.05B 2 O 3 :Eu 0.005 Nd 0.16 1146 3012 4-1 2(Sr 0.5 Ca 0.5 )O·MgO·2SiO 2 ·0.05B 2 O 3 :Eu 0.005 Ho 0.01 472 1324 4-2 2(Sr 0.5 Ca 0.5 )O·MgO·2SiO 2 ·0.05B 2 O 3 :Eu 0.005 Ho 0.05 534 1427 5-1 2(Sr 0.5 Ca 0.5 )O·MgO·2SiO 2 ·0.05B 2 O 3 :Eu 0.005 Tm 0.01 567 1624 5-2 2(Sr 0.5 Ca 0.5 )O·MgO·2SiO 2 ·0.05B 2 O 3 :Eu 0.005 Tm 0.05 621 1735 6-1 2(Sr 0.5 Ca 0.5 )O·MgO·2SiO 2 ·0.05B 2 O 3 :Eu 0.005 Ce 0.0015 116 184 6-2 2(Sr 0.5 Ca 0.5 )O·MgO·2SiO 2 ·0.05B 2 O 3 :Eu 0.005 Ce 0.006 95 174 6-3 2(Sr 0.5 Ca 0.5 )O·MgO·2SiO 2 ·0.05B 2 O 3 :Eu 0.005 Ce 0.02 116 216 7-1 2(Sr 0.5 Ca 0.5 )O·MgO·2SiO 2 ·0.05B 2 O 3 :Eu 0.005 Sn 0.001 118 267 7-2 2(Sr 0.5 Ca 0.5 )O·MgO·2SiO 2 ·0.05B 2 O 3 :Eu 0.005 Sn 0.005 234 349 7-3 2(Sr 0.5 Ca 0.5 )O·MgO·2SiO 2 ·0.05B 2 O 3 :Eu 0.005 Sn 0.02 121 254 8-1 2(Sr 0.5 Ca 0.5 )O·MgO·2SiO 2 ·0.05B 2 O 3 :Eu 0.005 Tb 0.0013 89.5 231.6 8-2 2(Sr 0.5 Ca 0.5 )O·MgO·2SiO 2 ·0.05B 2 O 3 :Eu 0.005 Tb 0.0053 94.7 242 8-3 2(Sr 0.5 Ca 0.5 )O·MgO·2SiO 2 ·0.05B 2 O 3 :Eu 0.005 Tb 0.021 31.6 368 9-1 2(Sr 0.5 Ca 0.5 )O·MgO·2SiO 2 ·0.05B 2 O 3 :Eu 0.005 Pr 0.0015 52.6 136.8 9-2 2(Sr 0.5 Ca 0.5 )O·MgO·2SiO 2 ·0.05B 2 O 3 :Eu 0.005 Pr 0.006 73.7 194.7 9-3 2(Sr 0.5 Ca 0.5 )O·MgO·2SiO 2 ·0.05B 2 O 3 :Eu 0.005 Pr 0.023 89.5 226.3 10-1 2(Sr 0.5 Ca 0.5 )O·MgO·2SiO 2 ·0.05B 2 O 3 :Eu 0.005 Bi 0.001 154 317 10-2 2(Sr 0.5 Ca 0.5 )O·MgO·2SiO 2 ·0.05B 2 O 3 :Eu 0.005 Bi 0.005 282 431 10-3 2(Sr 0.5 Ca 0.5 )O·MgO·2SiO 2 ·0.05B 2 O 3 :Eu 0.005 Bi 0.002 297 442 11-1 2(Sr 0.5 Ca 0.5 )O·MgO·2SiO 2 ·0.05B 2 O 3 :Eu 0.005 Dy 0.02 Bi 0.01 2042 4127 Comparative sample ZnS:Cu 100 100 The experimental phosphor in TABLE 6 can display green afterglow luminescence after irradiated under sunlight, fluorescent lamp or ultraviolet lamp; when excited under 365nm ultraviolet light, the phosphor can give 430-600nm broad band emission spectrum, peak position near 500nm;its excitation spectrum is broad band spectrum between 250-460nm, when monitoring at 500nm, indicated that this phosphor has stronger absorption ability for the short wave light; analyzed from x-ray diffraction patterns, it can be seen that this phosphor diffraction patterns is similar to that of Sr 2 MgSi 2 O 7 and Ca 2 MgSi 2 O 7 , concerning the mole proportion of Sr and Ca, the main matrix compound (Sr 0.5 Ca 0.5 ) 2 MgSi 2 O 7 can be deduced. For different addings, its peak position of spectrum can be shifted certain. FIG. 8(a),(b) and FIG.9 are emission spectrum, excitation spectrum and x-ray diffraction pattern of experimental phosphor 2-5 respectively, its emission spectrum peak position is 500nm. 1.If y=0 in the chemical composition formula, the relationship between the amount of Eu(x) added and afterglow intensity ,see experiment 1-1∼6 in TABLE 6. 2.If x=0.005, Ln=Dy,the relationship between the amount of Dy(y) and afterglow effect, see experiment 2-1∼6 in TABLE 6. It can be seen that this phosphor has obviously strengthened in afterglow intensity compared with the phosphor of experiment 1-1∼6. FIG.10 is the log-log characteristic curve concerning luminescent afterglow of phosphor in experiment 2-5 varies with the decay time, it indicates that the decay time can prolong to more than 50hrs when afterglow brightness reach the eye's lowest visual luminosity 0.32mcd/m 2 . 3.If x=0.005,Ln=Nd, the relationship between the amount of Nd(y) added and the afterglow effect, see experiment 3-1∼3 in TABLE 6, it can be seen that afterglow intensity is higher and decay time is longer. 4.If x=0.005, Ln is Ho, Tm, Ce, Sn, Tb, Pr and Bi respectively, the influence of its adding amount to the afterglow intensity, see experiment 4-10 in TABLE 6. 5.If x=0.005, Ln=Dy and Bi, if Dy and Bi are both added in the same time, then obvious enhancement of luminescent afterglow intensity can be seen, see experiment 11 in TABLE 6. According to the main compound of above phosphor, the chemical formula of the green series phosphor is: (Sr 0.5 C 0.5 ) 2 MgSi 2 O 7 :Eu,Ln. (4) Bluish-green to greenish-yellow long afterglow luminescent materials When M=Sr 1-z Ca z , M'=Mg, R=B 2 O 3 , a=2, b=1, c=2, d=0.1, the phosphor's chemical composition formula is: 2(Sr 1-z Ca z )O·MgO·2SiO 2 ·0.1B 2 O 3 :Eu x ,Ln y ,0 ≤ z ≤1, the phosphors' afterglow colors change from blue to yellow with the z value , when z=0,the color is blue; z=1, which is yellow; z=0.5,which is green. The phosphors' luminescent colors present the change from blue to green then yellow with the change of z value from 0 to 1, that means to change the proportion of Sr and Ca. 1.As shown in TABLE 7, test the influence of the change of the proportion Sr and Ca in 2(Sr 1-z Ca z )O·MgO·2SiO 2 ·0.1B 2 O 3 :Eu 0.004 Dy 0.02 , to the emission spectrum peak position, it can be seen that the emission spectrum peak position changed from 469nm to 535nm varies as the z value changes from 0 to 1,this cause the luminescent color presents the change of blue, bluish-green, green, greenish-yellow and yellow, see TABLE 7. Z 0 0.1 0.2 0.3 0.4 0.5 0.6 0.7 0.8 0.9 1 Sr Sr Sr 0.9 Sr 0.8 Sr 0.7 Sr 0.6 Sr 0.5 Sr 0.4 Sr 0.3 Sr 0.2 Sr 0.1 0 Ca 0 Ca 0.1 C 0.2 C 0.3 C 0.4 Ca 0.5 Ca 0.6 Ca 0.7 Ca 0.8 Ca 0.9 Ca Emission spectra peak, nm 469 473 482 485 496 500 505 509 517 532 535 2.When z=0.25, select chemical composition formula 2(Sr 0.75 Ca 0.25 )O·MgO·2SiO 2 ·0.1B 2 O 3 :Eu 0.004 ,Ln 0.02 to do experiment, shown as experiment 1∼6 in TABLE 8, the phosphors present bluish-green long afterglow luminescence and the adding of Ln ion can obviously strengthen its luminescent intensity as shown from experiment 2 in TABLE 8,there is a sharp difference compared with the comparative sample, a very strong bluish-green afterglow luminescence can be presented ,and its emission spectrum, excitation spectrum are shown in FIG.11(a),(b). 3.When z=0.75, select chemical composition formula 2(Sr 0.75 Ca 0.75 )O·MgO·2SiO 2 ·0.1B 2 O 3 :Eu 0.004 ,Ln 0.02 as seen in experiment 7-12 of TABLE 8, the phosphors present greenish-yellow long afterglow luminescence, and the adding of Ln ion can obviously strengthen its luminescent intensity, which can be seen from experiment 8 in TABLE 8, there in an obvious enhancement compared with the comparative sample, its emission spectrum, excitation spectrum are shown FIG.12(a),(b). Ex Chemical composition formula Relative afterglow intensity Luminescent color 10' 60' 1 2(Sr 0.75 Ca 0.25 )O·MgO·2SiO 2 ·0.01B 2 O 3 :Eu 0.01 121 162 bluish-green 2 2(Sr 0.75 Ca 0.25 )O·MgO·2SiO 2 ·0.01B 2 O 3 :Eu 0.01 Dy 0.02 1758 3874 bluish-green 3 2(Sr 0.75 Ca 0.25 )O·MgO·2SiO 2 ·0.01B 2 O 3 :Eu 0.01 Nd 0.02 1121 1671 bluish-green 4 2(Sr 0.75 Ca 0.25 )O·MgO·2SiO 2 ·0.01B 2 O 3 :Eu 0.01 Ho 0.02 1023 1642 bluish-green 5 2(Sr 0.75 Ca 0.25 )O·MgO·2SiO 2 ·0.01B 2 O 3 :Eu 0.01 Sn 0.02 267 342 bluish-green 6 2(Sr 0.75 Ca 0.25 )O·MgO·2SiO 2 ·0.01B 2 O 3 :Eu 0.01 Bi 0.02 323 407 bluish-green 7 2(Sr 0.75 Ca 0.25 )O·MgO·2SiO 2 ·0.01B 2 O 3 :Eu 0.01 171 303 greenish-yellow 8 2(Sr 0.75 Ca 0.25 )O·MgO·2SiO 2 ·0.01B 2 O 3 :Eu 0.01 Dy 0.02 617 1247 greenish-yellow 9 2(Sr 0.75 Ca 0.25 )O·MgO·2SiO 2 ·0.01B 2 O 3 :Eu 0.01 Nd 0.02 517 928 greenish-yellow 10 2(Sr 0.75 Ca 0.25 )O·MgO·2SiO 2 ·0.01B 2 O 3 :Eu 0.01 Ho 0.02 361 808 greenish-yellow 11 2(Sr 0.75 Ca 0.25 )O·MgO·2SiO 2 ·0.01B 2 O 3 :Eu 0.01 Sn 0.02 231 431 greenish-yellow 12 2(Sr 0.75 Ca 0.25 )O·MgO·2SiO 2 ·0.01B 2 O 3 :Eu 0.01 Bi 0.02 272 489 greenish-yellow (5)Other long afterglow luminescent materials 1.In the chemical composition formula, when M=Sr 1-z Ca z, wherein 0 ≤ z ≤ 1, M'=Mg, R=B 2 O 3 , a=3, b=1, c=2, d=0.1,that means the formula is 3MO·MgO·2SiO 2 ·0.1B 2 O 3 :Eu x ,Ln y , the phosphors display long luminescence from blue to greenish-yellow. In TABLE 9, M=Sr, Ln=Dy or Nd was selected in experiment 1,the phosphors display blue long afterglow. The emission spectrum, excitation spectrum and x-ray diffraction pattern of 3SrO·MgO· 2SiO 2 ·0.1B 2 O 3 :Eu 0.004 ,Dy 0.02 phosphor are shown in FIG.13 (a),(b) and FIG.14 respectively. The peak of the emission spectrum is 462nm. The dominant compound is Sr 3 MgSi 2 O 8 ,and the secondary is Sr 2 MgSi 2 O 7 , The chemical formula of the phosphor Sr 3 MgSi 2 O 8 :Eu,Ln is defined.In TABLE 9,M=Ca, Ln=Dy or Nd was selected in the experiment 2, the phosphors display light green long afterglow. The emission spectrum , excitation spectrum and x-ray diffraction pattern of the 3CaO·MgO 2SiO 2 :Eu 0.04 ,Dy 0.02 phosphor are shown in FIG.15(a), (b) and FIG.16 respectively and the peak of the emission spectrum is 475nm. The dominant compound is Ca 3 MgSi 2 O 8 , and the secondary is Ca 3 MgSi 2 O 7 . When M=Sr 0.5 Ca 0.5 ,Ln=Dy or Nd, the phosphors display bluish-green afterglow. The long afterglow property of them is shown in the experiment 3-1∼2 of TABLE 9. Experiment Chemical composition formula Relative afterglow intensity Luminescent color 10' 60' 1-1 3SrO·MgO·2SiO 2 ·0.1B 2 O 3 :Eu 0.004 Nd 0.02 211 489 blue 1-2 3SrO·MgO·2SiO 2 ·0.1B 2 O 3 :Eu 0.004 Dy 0.02 300 579 blue 2-1 3CaO·MgO·2SiO 2 0.1B 2 O 3 :Eu 0.004 Nd 0.02 31.4 56.1 light green 2-2 3CaO·MgO·2SiO 2 ·0.1B 2 O 3 :Eu 0.004 Dy 0.02 67.1 146 light green 3-1 3(Sr 0.5 Ca 0.5 )O·MgO·2SiO 2 :0.1B 2 O 3 :Eu 0.004 Dy 0.02 173 345 bluish-green 3-2 3(Sr 0.5 Ca 0.5 )O·MgO·2SiO 2 :0.1B 2 O 3 :Eu 0.004 Nd 0.02 91 183 bluish-green Comparative samples (CaSr)S:Bi 100 100 ZnS:Cu 100 100 2. In the chemical composition formula, when M is Sr 1-z Ca z , where 0 ≤ z ≤ 1, M' is Mg, 0-40% mol of M and/or M' can be partly taken the place by one or more elements from a group consisting of Ba, Zn, Cd, and Be, then the colors of the afterglow are blue, green, yellow etc. The afterglow colors of the phosphors, in which M mainly consists of Sr, are from blue to blue -green, that is shown in the experiment of 1-1∼4 of TABLE 10, the long afterglow property of them is compared with (CaSr)S:Bi; if M mainly consists of Ca or Sr and Ca, the afterglow colors of the phosphors are from green to yellow, that is indicated in the experiment 2-1∼4 and 3-1∼2 of TABLE 10.The long afterglow property of them is compared with (ZnCd)S:Cu and ZnS:Cu respectively. It is obvious that the long afterglow property of these phosphor is much more superior than that of the comparative samples. Experiment Chemical composition formula Relative afterglow intensity 10' 60' 1-1 2(Sr 0.9 Zn 0.1 )O·MgO·2SiO 2 ·0.1B 2 O 3 :Eu 0.004 Dy 0.02 976 1793 1-2 2SrO·(Mg 0.9 Zn 0.1 )O ·2SiO 2 ·0.1B 2 O 3 :Eu 0.004 Nd 0.02 1170 2104 1-3 2SrO·(Mg 0.9 Ba 0.1 )O ·2SiO 2 ·0.1B 2 O 3 :Eu 0.004 Dy 0.02 836 1706 1-4 2(Sr 0.9 Cd 0.1 )O ·MgO ·2SiO 2 ·0.1B 2 O 3 :Eu 0.004 Dy 0.02 1031 1842 2-1 2(Ca 0.9 Zn 0.1 )O·MgO·2SiO 2 ·0.1B 2 O 3 :Eu 0.004 Dy 0.02 635 784 2-2 2CaO· (Mg 0.9 Zn 0.1 )O· 2SiO 2 ·0.1B 2 O 3 :Eu 0.004 Dy 0.02 703 802 2-3 2(Ca 0.95 Ba 0.05 )O MgO ·2SiO 2 ·0.1B 2 O 3 :Eu 0.004 Nd 0.02 507 769 2-4 2CaO· (Mg 0.9 Be 0.1 )O·2SiO 2 ·0.1B 2 O 3 :Eu 0.004 Dy 0.02 603 726 3-1 2(Sr 0.495 Ca 0.495 Zn 0.05 )O·MgO·2SiO 2 ·0.1B 2 O 3 :Eu 0.004 Dy 0.02 1083 2835 3-2 2(Sr 0.5 Ca 0.5 )O·(Mg 0.9 Ba 0.1 )O·2SiO 2 ·0.1B 2 O 3 :Eu 0.004 Dy 0.02 1017 2786 Comparative samples (CaSr)S:Bi 100 100 (ZnCd)S:Cu 100 100 ZnS:Cu 100 100 3. When M=Ba, a=5, b=0, c=8, R=B 2 O 3 , d=0.1, the formula of the phosphors is 5BaO·8SiO 2 0.1B 2 O 3 :Eu x ,Ln y , the synthesized phosphor, in which x=0.01, Ln=Dy, y=0.02 shows light green luminescence, and the dominant compound is Ba 5 Si 8 O 31 , the emission spectrum and excitation spectrum are shown in FIG. 17(a), (b), TABLE 11 shows its relative persistence property. Ba being partly replaced by one or more elements from a group consisting of Ca, Sr, Mg, Zn, Cd and Be, the phosphors display persistence luminescence too. Experiment Chemical composition formula Relative afterglow intensity 10' 60' 1-1 Ba 5 Si 8 O 31 :Eu,Dy 87.4 100 comparative sample ZnS:Cu 100 100 4. When M=Zn, R=B 2 O 3 , a=2, b=0, c=1, d=0.1, Ln=Dy and Mn, x=0.01, y=0.02, the synthesized phosphor shows light green afterglow and the main compound is Zn 2 SiO 4 . The decay property is shown in TABLE 12. Zn being partly replaced by one or more elements from a group consisting of Ca , Sr, Mg, Ba, Cd and Be the phosphor shows decay luminescence too. Experiment Chemical composition formula Relative afterglow 10' 60' 1-1 Zn 2 SiO 4 :Eu,Dy,Mn 32.6 95.8 Comparative sample ZnS:Cu 100 100 In this invention it is also found that put other additives ( 0-15% weight of the raw material) to the raw material can more or less improve the long afterglow intensity of phosphor and the quality of the synthesized product, but didn't change its dominant crystal structure and main compound, the influence of the additives on the afterglow property of the greenish-yellow phosphors is indicated in TABLE 13. In TABLE 13 the greenish-yellow phosphor is selected wherein M=Sr 0.3 Ca 0.7 ,M'=M,R=B 3 O 3 ,Ln=Dy,a=2.5,b=1.2,c=2.5,d=0.1,x=0.02,y=0.1 Ex Chemical composition formula Added compound Mol Relative afterglow intensity 10' 60' 1 2.5(Sr 0.3 Ca 0.7 O)·1.2MgO·2.5SiO 2 ·0.1B 2 O 3 :Eu 0.02 Dy 0.1 0 0 643 1374 2 2.5(Sr 0.3 Ca 0.7 O)·1.2MgO·2.5SiO 2 ·0.1B 2 O 3 :Eu 0.02 Dy 0.1 NH 4 Cl 0.1 684 1427 3 2.5(Sr 0.3 Ca 0.7 O)·1.2MgO·2.5SiO 2 ·0.1B 2 O 3 :Eu 0.02 Dy 0.1 NH 4 F 0.1 672 1395 4 2.5(Sr 0.3 Ca 0.7 O)·1.2MgO·2.5SiO 2 0.1B 2 O 3 :Eu 0.02 Dy 0.1 Li 2 CO 3 0.05 693 1432 5 2.5(Sr 0.3 Ca 0.7 O)·1.2MgO·2.5SiO 2 ·0.1B 2 O 3 :Eu 0.02 Dy 0.1 SrF 2 0.1 675 1398 6 2.5(Sr 0.3 Ca 0.7 O)·1.2MgO·2.5SiO 2 ·0.1B 2 O 3 :Eu 0.02 Dy 0.1 CaF 2 0.1 663 1388 7 2.5(Sr 0.3 ,Ca 0.7 O)·1.2MgO·2.5SiO 2 ·0.1B 2 O 3 :Eu 0.02 Dy 0.1 CaSO 4 0.1 670 1391 8 2.5(Sr 0.3 Ca 0.7 O)·1.2MgO·2.5SiO 2 ·0.1B 2 O 3 :Eu 0.02 Dy 0.1 SrSO 4 0.1 675 1382 9 2.5(Sr 0.3 Ca 0.7 O)·1.2MgO·2.5SiO 2 ·0.1B 2 O 3 :Eu 0.02 Dy 0.1 SrHPO 4 0.1 682 1407 10 2.5(Sr 0.3 Ca 0.7 O)·1.2MgO·2.5SiO 2 ·0.1B 2 O 3 :Eu 0.02 Dy 0.1 CaHPO 4 0.1 667 1379 In other chemical formula more or less influence of these additives on the afterglow property is found as well. The phosphors of this invention have good water resistance property and better stability. In the same condition, putting the long afterglow phosphor of aluminate and a long afterglow silicate phosphor of this invention into water respectively it is found that the aluminate's phosphor decomposed after three days and decomposed entirely after a week and losing the luminescent property ,but the silicate's phosphor didn't decompose even after three months . The afterglow property still existed. This invention have the following outstanding features compared with the present technology: (1)Inventing a new series of long afterglow phosphors with silicate as the dominant host lattice that possesses the fairly good chemical stability and water resistance property, and changeable afterglow colors : blue bluish-green, green, greenish-yellow and yellow. (2)Inventing of some ions can enhance the luminescence of the Eu 2+ and improve the afterglow luminescent properties. (3)Adding of boron and phosphors compound can make further improvement on the luminescent properties . The invention is described in detail hereafter by referring to the examples and figures. EXAMPLES Example 1: 2SrO·MgO·2SiO 2 ·0.1B 2 O 3 :Eu 0.004 phosphor's synthesis and analysis results Match of the raw materials: Element Mol Raw Material Weight Sr 1.996 SrCO 3 294.6g Mg 1 4MgCO 3 ·Mg(OH) 2 ·5H 2 O 97.1g Si 2 SiO 2 120g B 0.2 B 2 O 3 6.96g Eu 0.004 Eu 2 O 3 0.704g The above raw material was ground into fine and mixed homogenously, then placed in alumina crucible and fired in the furnace which full of NH 3 (g) atmosphere at 1350 °C for 3 hrs, after that cooled down and smashed the fired phosphor, finally sifted it out by the sieve of 100 mesh. The appearance of this phosphor is greyish white, after irradiated under sun light it can present blue afterglow color in dark; measured the phosphor's luminescent afterglow intensity, show in experiment 1-4 in TABLE 4, FIG. 1 (a), (b) and figure 2 are the example phosphor's emission spectrum, excitation spectrum and x-ray diffraction pattern respectively, according to its x-ray diffraction pattern, its crystal structure, is akermanite and its compound is Sr 2 MgSi 2 O 7 , the phosphor's chemical formula Sr 2 MgSi 2 O 7 :E U is defined. Example 2: 2SrO·MgO·2SiO 2 ·0.1B 3 O 3 :Eu 0.004 ,Dy 0.04 phosphor's synthesis and analysis results Match of the raw materials: Element Mol Raw Material Weight Sr 1.96 SrCO 3 289.3g Mg 0.996 4MgCO 3 ·Mg(OH) 2 ·5H 2 O 96.7g Si 2 SiO 2 120g B 0.2 H 2 BO 3 13.56g Eu 0.004 Eu 2 O 3 0.704g Dy 0.04 Dy 2 O 3 7.46g The above raw material is ground into fine and mixed homogenously in alcohol solution , after baking, placed in alumina crucible, and fired in a high temperature furnace which full of NH 3 (g) atmosphere at 1350 °C for 3 hrs, after that cooled down, smashed the fired phosphor, finally sifted it out by the sieve of 100 mesh, The appearance of this phosphor is greyish white, after irradiated under fluorescent lamp, it displays very strong blue afterglow in dark, the phosphor's relative luminescent intensity shown as experiment 3-4 in TABLE4, its intensity is obviously higher than that of example 1; besides, the material's afterglow time is long, see figure 7; figure3(a)(b) are phosphor's emission spectrum and excitation spectrum respectively ;the phosphor's crystal structure and main compound same as example 1,the phosphor's chemical formula Sr 2 MgSi 2 O 7 :Eu,Dy is defined. Example 3: SrO·3MgO·2SiO 2 ·0.05P 2 O S :Eu 0.004 ,Nd 0.01 phosphor's synthesis Match of the raw materials: Element Mol Raw Material Weight Sr 0.993 SrCO 3 146.6g Mg 2.993 4MgCO 3 ·Mg(OH) 2 ·5H 2 O 290.6g Si 2 SiO 2 120g P 0.1 (NH 4 ) 2 HPO 4 13.2g Eu 0.004 Eu 2 O 3 0.704g Nd 0.1 Nd 2 O 3 1.68g The above raw material is ground into fine and mixed homogeneously in acetone solution, after baking, placed in alumina crucible, and fired in a furnace which full of H 2 (g) atmosphere at 1350 °C for 3 hrs, after that cooled and smashed the fired phosphor, finally sifted it out by the sieve of 100mesh. This phosphor can display stronger blue afterglow after irradiated under ultraviolet lamp, analyzed from x-ray diffraction pattern, its dominant compound is Sr 2 MgSiO 7 and Mg 2 SiO 4 , the phosphor's chemical composition formula SrO·3MgO·2SiO 2 · 0.05P 2 O 5 :Eu,Nd is defined. Example 4: 2CaO·MgO·2SiO 2 ·0.15B 2 O 3 :Eu 0.004 ,Dy 0.05 phosphor's synthesis and analysis results. Match of the raw materials: Element Mol Raw Material Weight Ca 1.946 CaCO 3 194.6g Mg 1 4MgCO 3 ·Mg(OH) 2 ·5H 2 O 97.1g Si 2 SiO 2 120g B 0.3 H 3 BO 3 18.84g Eu 0.004 Eu 2 O 3 0.764g Dy 0.05 Dy 2 O 3 9.325g The above raw material is ground into fine and mixed homogeneously, then placed in alumina crucible fired in a high temperature furnace which full of 30% H 2 (g)+70% N 2 (g) atmosphere at 1320 °C for 5hrs,after that cooled and smashed the fired phosphor, finally sifted it out by the sieve of 100mesh. The appearance of this phosphor is light yellow, after irradiated under fluorescent lamp, it can presents very strong yellow afterglow in dark; the phosphor's relative luminescent intensity shown as experiment 2-3 in TABLE 5, which is obviously stronger than that of experiment 1-4 in TABLE 5, its emission spectrum, excitation spectrum are shown in FIG.5(a),(b);the phosphor's afterglow time is long ,FIG. 7 is phosphor's afterglow characteristic curve, the phosphor's main crystal structure is akermamite and its compound is Ca 2 MgSi 2 O 7 , see FIG. 6, so the phosphor's chemical formula is defined as Ca 2 MgSi 2 O 7 :Eu,Dy. Example 5: 1.5CaO·3MgO·2SiO 2 ·015B 2 O 3 :Eu 0.004 ,Ho 0.08 phosphor's synthesis. Match of the raw materials: Element Mol Raw Material Weight Ca 1.5 CaCO 3 150g Mg 3 4MgCO 3 ·Mg(OH) 2 ·5H 2 O 291.3g Si 2 H 2 SiO 3 156g B 0.15 B 2 O 3 10.44g Eu 0.004 Eu 2 O 3 0.704g Ho 0.08 Ho 2 O 3 15.1g The synthesis method of this phosphor is the same as example 1, after irradiated under ultraviolet lamp, this phosphor displays yellow afterglow, according to the x-ray diffraction pattern, its compounds is Ca 2 MgSi 2 O 7 ,CaMgSiO 4 and Ca 3 Si 2 O 7 so the phosphor's chemical composition formula 1.5CaO·3MgO·2SiO 2 ·0.15B 2 O 3 :Eu,Ho is defined. Example 6:2(Sr 0.5 Ca 0.5 )O·MgO·2SiO 2 ·0.05B 2 O 3 :Eu 0.005, Dy 0.08 phosphor's synthesis and analysis results Match of the raw materials: Element Mol Raw Material Weight Sr 1 SrCO 3 147.6g Ca 1 CaCO 3 100g Mg 1 4MgCO 3 ·Mg(OH) 2 ·5H 2 O 97.1g Si 2 SiO 2 120g B 0.1 H 3 BO 3 6.28g Eu 0.005 Eu 2 O 3 0.88g Dy 0.08 Dy 2 O 3 14.92g The above raw material is ground and mixed homogeneously, placed in alumina crucible, fired for 3 hrs at 1300 °C in NH 3 (g) atmosphere, after that cooled down and smashed the fired phosphor, finally sifted it out by the sieve of 100mesh. The appearance of this phosphor is light green, after irradiated under fluorescent lamp it displays strong green afterglow. This phosphor's relative afterglow intensity is shown in TABLE 6. The emission spectrum, excitation spectrum and x-ray diffraction pattern of this phosphor are shown in FIG.8(a),(b) and FIG.9 respectively. The phosphor's afterglow time is long and FIG. 10 is the afterglow characteristics curve. Its chemical formula (Sr 0.5 Ca 0.5 ) 2 MgSi 2 O 7 :Eu,Dy is defined. Example 7. 2(Sr 0.25 Ca 0.75 )O·MgO·2.3SiO 2 ·0.05P 2 O 5 :Eu 0.01 ,Nd 0.02 phosophor's synthesis Match of the raw materials: Element Mol Raw Material Weight Sr 0.5 Sr(NO 3 ) 2 105.8g Ca 1.5 Ca(NO 3 ) 2 ·4H 2 O 354g Mg 1 Mg(NO 3 ) 2 ·6H 2 O 256.4g Si 2.3 silica gel 138g P 0.1 NH 4 H 2 PO 4 11.5g Eu 0.01 Eu 2 O 3 1.76g Nd 0.02 Nd 2 O 3 3.36g The synthesis method of this phosphor is the same as described in example 1. This phosphor displays greenish-yellow afterglow after irradiated under fluorescent lamp. The x-ray diffraction pattern of this phosphor is similar to FIG.9, so it can be deduced that its compound is (Sr 0.25 Ca 0.75 ) 2 MgSi 2 O 7 , its chemical formula (Sr 0.25 Ca 0.75 ) 2 MgSi 2 O 7 : Eu,Nd. is defined. Example 8. 3SrO·MgO·2SiO 2 :Eu 0.001. Ho 0.08 phosphor's synthesis Match of the raw materials: Element Mol Raw Material Weight Sr 3 Sr(NO 3 ) 2 634.8g Mg 1 MgO 40.3g Si 2 H 2 SiO 3 156g Eu 0.01 Eu 2 O 3 1.76g Ho 0.08 Ho 2 O 3 15.1g The synthesis method of this phosphor is the same as described in example 1. This phosphor displays blue afterglow after irradiated under sunlight, its dominant compound is Sr 3 MgSi 2 O 8 , the secondary is Sr 2 MgSi 2 O 7 , so the chemical formula Sr 3 MgSi 2 O 8 :Eu,Ho is defined. Example 9. 2(Sr 0.6 Ca 0.4 )O·(Mg 0.8 Cd 0.2 )O·2.5SiO 2 ·0.1B 2 O 3 :Eu 0.001 Dy 0.02 Bi 0.01 phosphor's synthesis. Match of the raw materials: Element Mol Raw Material Weight Sr 1.3 SrCO 3 177.1g Ca 0.8 CaCO 3 80g Mg 0.8 4MgCO 3 ·Mg(OH) 2 ·5H 2 O 77.7g Cd 0.2 CdO 25.7g Si 2.5 SiO 2 150g B 0.2 B 2 O 3 6.96g Eu 0.01 Eu 2 O 3 1.76g Dy 0.02 Dy 2 O 3 3.73g Bi 0.01 Bi 2 O 3 2.33g Doped 5% NH 4 Cl by weight of the raw material, grinding and mixing them together, then firing them as example 1. The fired phosphor displays strong bluish-green afterglow after irradiated under sunlight. Example 10. 5BaO·8SiO 2 ·0.1B 2 O 3 :Eu 0.01 Dy 0.02 phosphor's synthesis Match of the raw materials: Element Mol Raw Material Weight Ba 5 BaCO 3 985g Si 8 SiO 3 480g B 0.2 B 2 O 3 6.96g Eu 0.01 Eu 2 O 3 1.76g Dy 0.02 Dy 2 O 3 3.73g The synthesis method of this phosphor is the same described in example 1, after irradiated under sunlight this phosphor displays light green persistence, its compound is Ba 5 Si 8 O 21 and so the chemical formula Ba 5 Si 8 O 21 :Eu,Dy is defined. INDUSTRY APPLICATION The products in this invention can be widely used in all kinds of long afterglow products as indicators or ornaments in dark environment , combined with paint; plastics; printing ink; rubber etc., this series of luminescent materials has good effect in architecture , traffic, decoration, watch and clock dials, fishing tackles, toys and other goods for daily use, it's specially suitable for the production of long afterglow safety products, such as warning, mandatory and escape-route signs.

Claims: A long afterglow luminescent material, comprising silicates with activators, wherein said luminescent material has a chemical composition of: aMO·bM'O·cSiO 2 ·dR: Eu x , Ln y wherein M represents one or more elements selected from the group consisting of Sr, Ca, Ba and Zn; M' represents one or more elements selected from the group consisting of Mg, Cd and Be; R represents one or two components selected from B 2 O 3 and P 2 O 5 ; Ln represents one or more elements selected from the group consisting of Nd, Dy, Ho, Tm, La, Pr, Tb, Ce and Sb; and wherein a,b,c,d,x and y represent mole coefficients, wherein 0.6≤a≤6, 0≤b≤5, 1≤c≤9, 0≤d≤0.7, 0.00001≤x≤0.2, and 0<y≤0.3; and said luminescent material is capable of emitting an emission spectrum ranging from 420nm to 650nm when excited by short wavelength light ranging from 250nm to 500nm, with a peak position of the emission spectrum ranging from 450nm to 580nm, and wherein the long afterglow luminescent color of said luminescent material is blue, bluish-green, green, greenish-yellow or yellow. The long afterglow luminescent material of claim 1, wherein M represents one or two elements selected from Sr and Ca; M' represents Mg; R represents one or two components selected from B 2 O 3 and P 2 O 5 ; Ln represents one or more elements selected from the group consisting of Nd, Dy, and Ho, wherein 0.6≤a≤4, 0.6≤b≤4, 1≤c≤5, and 0≤d≤0.4. The long afterglow luminescent material of claim 2, wherein 0-40% mole of the elements M and/or M' have been replaced by one or more elements selected from the group consisting of Ba, Zn, Cd and Be. The long afterglow luminescent material of claim 1, wherein said luminescent material has a chemical composition: M 2 MgSi 2 O 7 :Eu x ,Ln y or M 3 MgSi 2 O 8 :Eu x ,Ln y , wherein 0.00001≤x≤0.2, 0<y≤0.3; M represents Sr 1-z Ca z , wherein 0≤z≤1; and Ln represents one or more elements selected from the group consisting of Nd, Dy, Ho, Tm, La, Pr, Tb, Ce and Sb. The long afterglow luminescent material of claim 1, wherein said luminescent material has a chemical composition of: Ba 5 Si 8 O 21 dR: Eu x ,Ln y , wherein R represents one or two components selected from B 2 O 3 and P 2 O 5 ; and wherein d, x and y represent mole coefficients, wherein 0<d≤0.7, 0.00001≤x≤0.2, and 0<y≤0.3. A method of manufacturing the long afterglow luminescent material of claim 1, characterized in that mole proportion of elements in the raw material used to produce the luminescent material are as follows: M: 0.6-6 M': 0-5 Si: 1-9 R: 0-0.7 in terms of B 2 O 3 and P 2 O 5 Eu: 0.00001-0.2 Ln: greater than zero, but equal or less than 0.3 wherein M represents one or more elements selected from a group consisting of Sr, Ca, Ba and Zn; M' represents one or more elements selected from a group consisting of Mg, Cd and Be; R represents one or two elements selected from B and P; Ln represents one or more elements selected from a group consisting of Nd, Dy, Ho, Tm, La, Pr, Tb, Ce and Sb; Si represents Si, Eu represents Eu, wherein M, M', Ln and Eu are derived from raw materials individually selected from the group consisting of one or more of a carbonate, sulphate, nitrate, phosphate, borate, acetate, oxalate, citrate, oxide, hydroxide and halogenide, including mixtures thereof; and wherein Si is derived from SiO 2 , silicic acid, silica gel or silicate; R is derived from a compound containing B or P, with the proviso that such a compound can form B 2 O 3 and P 2 O 5 in a subsequent sintering procedure; the method comprising the following steps: weighing, grounding, and homogeneously mixing raw materials comprising M, M', Ln, Eu, Si and R to yield a mixture; sintering the mixture at a temperature between 1100-1400 °C for a period of time in the range of 2 to 50 hours under a reducing atmosphere to yield a fired mixture; milling and sifting the fired mixture into a desired particle size. The method of manufacturing the long afterglow luminescent material of claim 6, wherein the reducing atmosphere is selected from the group consisting of H 2 , NH 3 , and N 2 in combination with H 2 . The method of manufacturing the long afterglow luminescent material of claim 6, wherein NH 4 Cl, NH 4 F, Li 2 CO 3 , SrF 2 , CaF 2 , CaSO 4 , SrSO 4 , SrHPO 4 or CaHPO 4 has been added to the mixture to participate in a solid-phase reaction:

Inventors: XIAO ZHIGUO, XIAO ZHIQIANG, XIAO, ZHIGUO, XIAO, ZHIQIANG
Applicants: XIAO ZHIGUO, XIAO ZHIQIANG, XIAO, ZHIGUO, XIAO, ZHIQIANG
Application year: 1997
Main classification: C09K11
IPC codes: C09K11