HIGH PRESSURE METAL HALIDE LAMP

Abstract: The invention relates to a high pressure metal halide lamp comprising: a light transmitting discharge vessel enclosing a discharge space, sealed in a gas-tight manner, in which electrodes are disposed, which are connected to current conductors which extend to the exterior; a filling in the discharge vessel comprising a rare gas, a buffer gas and at least one transition metal halide chosen from the halides of hafnium, zirconium and tantalum. According to the invention each of the electrodes comprises an electrode part containing a carbide chosen from the carbides of hafnium, zirconium and tantalum. As a result diffusion of transition metal from the plasma into the electrode is strongly suppressed so that the lamp keeps very good colour rendering properties throughout its operation.

Description: High pressure metal halide lamp. The invention relates to a high pressure metal halide lamp comprising a light transmitting discharge vessel enclosing a discharge space, sealed in a gas-tight manner, in which electrodes are disposed, which are connected to current conductors which extend to the exterior, - a filling in the discharge vessel compπsing a rare gas, a buffer gas and at least one transition metal halide chosen from the halides of hafnium, zirconium and tantalum. Such a high pressure metal halide lamp (further also indicated as lamp) is known from EP 0627759 Al. In the known lamp mercury and/or xenon can for instance be used as buffer gases. The electrodes of the known lamp consist of tungsten bars. The known lamp has good colour rendering properties. Furthermore the efficacy and the luminance of the known lamp have a relatively high value. A disadvantage of the known lamp is that during operation diffusion of the transition metal present in the plasma into the electrode takes place. As a result the composition of the plasma and therefore also the performance of the known lamp change during operation. More in particular the colour rendering properties of the lamp decrease very rapidly as a result of the disappearance of the transition metal from the plasma. The effect of the diffusion can partly be compensated by increasing the amount of transition metal halide in the filling of the lamp so that enough transition metal remains in the plasma after most of it has diffused into the electrode. It was found, however, that lamps containing such a large amount of transition metal halide had a very high reignition voltage rendering them unsuitable for many practical applications. It is an object of the invention to provide a high pressure metal halide lamp of the kind described in the opening paragraph suitable for many practical applications and having an improved maintenance. According to the invention this object is achieved in that each of the electrodes comprises a first electrode part, containing a carbide chosen from the carbides of hafnium, zirconium and tantalum. During operation of the high pressure discharge lamp according to the invention the first electrode parts of the electrodes are facing the discharge and the discharge arc is present between the first electrode parts of the electrodes. It was found that in a high pressure metal halide lamp according to the invention migration of the transition metal from the plasma into the electrodes of the lamp is suppressed to a very large extent. As a result the composition of the plasma remains substantially unchanged and the excellent colour rendering properties of the lamp remain in existence throughout its operation. This is also true for lamps containing only a relatively small amount of transition metal halide in their filling. Preferably the amount of transition metal halide comprised in the discharge vessel is lower than 3 μmol/cm 3 , so that the reignition voltage of the lamp is relatively low. Good results have been obtained for high pressure metal halide lamps according to the invention wherein the first electrode parts were formed out of substantially pure transition metal carbide and also for high pressure metal halide lamps, wherein the first electrode parts in addition to the transition metal carbide also contain for instance tungsten and/or rhenium. Preferably the percentage by weight of tungsten and/or rhenium comprised in the first electrode parts is in the range 0 % - 30 % . The electrodes can comprise a second electrode part connected to the first electrode part. Depending on the composition of such a second electrode part a better connection between the current conductors and the second electrode parts can be realized than is possible between the current conductors and the first electrode parts. Favourable results have been obtained for high pressure metal halide lamps, wherein the second electrode parts comprise a tungsten bar. Preferably the first electrode part is fused to an end of the tungsten bar. Preferably the first electrode parts are substantially spherical, substantially semi-spherical or cylindrical. An embodiment of the invention will be further explained with reference to a drawing. In the drawing Fig. 1 shows an embodiment of a high pressure metal halide lamp according to the invention, and Fig. 2 shows a schematic representation of one of the electrodes comprised in the high pressure metal halide lamp shown in Fig. 1. In Fig. 1, 1 is a light transmitting discharge vessel enclosing a discharge space 2. The discharge vessel 1 is sealed in a gas-tight manner. Electrodes comprising first electrode parts 3a and 3b and second electrode parts 4a and 4b are disposed in the discharge vessel and connected to current conductors 5a, 6a and 5b, 6b which extend to the exterior. The current conductors each comprise a molybdenum foil (5a and 5b) and a conducting wire (6a and 6b) connected to the molybdenum foil. Each of the electrodes is also connected to one of the molybdenum foils. In the discharge vessel a filling is present comprising a rare gas, a buffer gas and an amount of HfBr 4 that is a solid at ambient temperature and is indicated in Fig. 1 as 6. Both of the electrodes present in the high pressure metal halide lamp of Fig. 1 are constructed as shown in Fig. 2 for one of these electrodes. It can be seen that the first electrode part consists of HfC while the second electrode part consists of a tungsten bar. The first electrode part is fused to the second electrode part. The second electrode part is connected to the molybdenum foil. Table I shows a comparison of a high pressure metal halide lamp in accordance with the invention (LAMP 2) with a high pressure metal halide lamp having a similar filling but having electrodes that consist of tungsten bars (LAMP 1). The electrodes of LAMP 2 had first electrode parts that consisted of substantially pure HfC. The volume of the discharge space of the high pressure metal halide lamps was approximately 1 cm 3 and the electrode distance was 6 mm. Both lamps were filled with approximately 100 mbar of Ar at ambient temperature and with 134 μmol/cm 3 Hg and 1.34 μmol/cm 3 HfBr4. Both lamps were operated horizontally, without an outer bulb and the power supplied to the lamps was 250 Watt. TABLE I LAMP 1 LAMP 2 Electrode construction: tungsten bar tungsten bar fused with first electrode part consisting of HfC filled amount of HfBr 4 0.28 0.28 (at operation temperature) Amount of HfBr 4 in the gas phase after 1 minute burning time (in bar): < < 0.1 0.28 Amount of HfBr 4 in the gas phase after 2 hours burning time (in bar): < < 0.1 0.28 Lumen output (klm): 16 17.5 Efficacy (lm/Watt): 64 70 Colour rendering index R9: -71 92 Colour rendering index Ra8: 66 97 Colour rendering index Ral4: 55 95 Colour temperature (K): 8520 7570 Lamp voltage (V): 94 90 Reignition Voltage (V): 140 160 Table π also shows a comparison of a high pressure metal halide lamp in accordance with the invention (LAMP 4). with a high pressure metal halide lamp having a similar filling but having electrodes that consist of tungsten bars (LAMP 3). The electrodes of LAMP 4 had first electrode parts that consisted of 30 wt. % tungsten and 70 wt. % HfC. The volume of the discharge space of the high pressure metal halide lamps was approximately 3,4 cm 3 and the electrode distance was 7 mm. Both lamps were filled with approximately 100 mbar of Ar at ambient temperature and with 74 μmol/cm 3 Hg, 2.4 μmol/cm 3 HfBr 4 , 2.4 μmol/cm 3 HgBr 2 and 8.4 μmol/cm 3 Sn. Both lamps were operated horizontally, without an outer bulb and the power supplied to the lamps was 580 Watt. TABLE II LAMP 3 LAMP 4 Electrode construction: tungsten bar tungsten bar fused with first electrode part consisting of 30 wt. % tungsten and 70 wt. % HfC filled amount of HfBr 4 0.5 0.5 (at operation temperature) Amount of HfBr 4 in the gas phase after 1 minute burning time (in bar): < 0.08 0.5 Amount of HfBr 4 in thegs phase after 2 hours burning time (in bar): < 0.04 0.5 Lumen output (klm): 42.511 46.270 Efficacy (lm/Watt): 73 80 Colour rendering index R9: 39 87 Colour rendering index Ra8: 89 98 Colour rendering index Ral4: 86 97 Colour temperature (K): 5240 4750 Lamp voltage (V): 72 97 Reignition Voltage (V): 160 240 Table I and Table II clearly show that Hf disappears from the plasma and into the electrodes of LAMP 1 and LAMP 3 at a very high rate during lamp operation and that this has a strong influence on the colour rendering properties of these lamps. It can also be seen that a reduction in the filled amount of HfBr 4 increases the difference in colour rendition between the lamp according to the invention and a lamp having electrodes consisting of tungsten bars. The amount of Hf in the plasma of LAMP 2 and LAMP 4 remains substantially at a constant level, as a result of which the colour rendering properties of LAMP 2 are very good. Furthermore, the reignition voltages of LAMP 2 and LAMP 4 are at acceptable values because of the relatively low amount of transition metal halide in the filling of the lamp. In separate experiments it was found that, in case of a lamp having electrodes consisting of tungsten bars, in order to have a colour rendering index Ra8 of at least 95, it was necessary to use a filled amount of HfBr 4 of 1.5 bar (at operation temperature). Of this filled amount only approximately 0.25 bar remained in the plasma while the rest diffused into the electrodes. Although the colour rendering index Ra8 remained at a high value throughout operation of the lamp, the reignition voltage was unacceptably high: between 800 V and 1000 V.

Claims: CLAIMS: 1. A high pressure metal halide lamp comprising a light transmitting discharge vessel enclosing a discharge space, sealed in a gas-tight manner, in which electrodes are disposed, which are connected to current conductors which extend to the exterior, - a filling in the discharge vessel comprising a rare gas, a buffer gas and at least one transition metal halide chosen from the halides of hafnium, zirconium and tantalum, characterized in that each of the electrodes comprises a first electrode part containing a carbide chosen from the carbides of hafnium, zirconium and tantalum. 2. A high pressure metal halide lamp as claimed in claim 1, wherein the first electrode parts also contain tungsten and/or rhenium. 3. A high pressure metal halide lamp as claimed in claim 2, wherein the percentage by weight of tungsten and/or rhenium comprised in the first electrode parts is in the range 0 % - 30 %. 4. A high pressure metal halide lamp as claimed in claim 1, 2 or 3, wherein the electrodes further comprise a second electrode part connected to the first electrode part. 5. A high pressure metal halide lamp as claimed in claim 4, wherein the second electrode part is a tungsten bar. 6. A high pressure metal halide lamp as claimed in claim 5, wherein the first electrode part is fused to an end of the tungsten bar. 7. A high pressure metal halide lamp as claimed in claim 4, 5 or 6, wherein said first electrode parts are substantially spherical. 8. A high pressure metal halide lamp as claimed in claim 4, 5 or 6, wherein said first electrode parts are substantially semi-spherical. 9. A high pressure metal halide lamp as claimed in claim 4, 5 or 6, wherein said first electrode parts are substantially cylindrical. 10. A high pressure metal halide lamp as claimed in one or more of the previous claims, wherein the amount of transition metal halide comprised in the discharge vessel is lower than 3 μmol/cm 3 .

Inventors: NATOUR GHALEB, NATOUR, GHALEB
Applicants: PHILIPS ELECTRONICS NV, PHILIPS NORDEN AB, PHILIPS PATENTVERWALTUNG, PHILIPS ELECTRONICS N.V., PHILIPS PATENTVERWALTUNG GMBH
Application year: 1997
Main classification: H01J61
IPC codes: H01J61