Pigment compositions

Abstract: The present invention provides the use of a resinated pigment in which from 10 to 100% of the resinated proportion of the product is a resin ester, as colourant in a lithographic printing ink.

Description: The present invention relates to the use of a resinated pigment as colourant in lithographic printing inks, a lithographic printing ink comprising an ink vehicle and a resinated pigment, and the use of a resinated pigment to reduce a pH drift in lithographic printing inks. Pigment compositions, for use in the manufacture of lithographic printing inks, normally contain additives to improve wetting and dispersion characteristics of the pigment in the ink vehicle. They may also modify other ink properties such as rheology and gloss. Such additives are typically rosins and modifies rosins such as for example, hydrogenated resins, disproportionated resins and maleic modified resins. These are normally incorporated as their aqueous solutions in dilute alkali, during the pigment synthesis, then precipitated with the pigment by the addition of acid, a metal salt e.g. calcium, aluminium or a amine/quatemary ammonium salt. However, with the advent of the replacement, for ecological reasons, of the lower aliphatic alcohols in the traditional fount solutions, by e.g. glycols, surfactants, etc., such pigment additives as described above can interfere with the lithographic printing process, disturbing the delicate aqueous/non-aqueous balance of the fount solutions and the ink, influencing fount pH instability. Thus, when such pigments are used in lithographic inks it is found that the pH of the fount solution gradually rises significantly e.g. from typically about 5 up to 7 or higher. When this happens, the ink and fount solution begin to mix and this causes poorer printing performance, e.g. print definition, especially when employing modern fast printing presses. This phenomenon has been known for a few years and the use of an oil-soluble buffer has been proposed to reduce the pH drift in EP 0315844. FR-A 2 340 357 describes a pigmentary composition containing an ester of a resin acid and an amino-alcohol. EP-A 677 556 describes coated pigments comprising a pigment such as a phthalocyanine and a water-insoluble organic surface modifier such as rosin derivatives. We have now found that the undesirable upwards pH drift of the fount solution can be significantly reduced or even eliminated by replacing the traditionally-used resin acids and salts by resins in which the carboxylic acid group(s) has been partially of fully reacted with alcohols, polyols or phenols to form insoluble resin ester. The resulting pigment compositions, as well as being readily incorporated into the lithographic ink, impart to the ink enhanced printing properties characterised by better fount/ink balance, reduced fount pH drift, and consequently, better ink transfer and print definition. Resin esters do not detrimentally affect the colouristic properties of the pigment and may improve such properties as rheology and gloss. Accordingly, the present invention provides the use of a resinated pigment in which from 10 to 100%, preferably from 40 to 100% by weight of the resinated proportion of the product is a resin ester, as colourant in a lithographic printing ink, wherein the resin ester is derived from a rosin by esterifying free acid groups on the rosin with an optionally substituted alcohol or polyol, and wherein the carboxylic acid groups have been fully reacted with the alcohol or polyol, and wherein the pigment is an azo lake pigment, with the proviso, that the alcohol is not an amino alcohol. The base pigments to which this invention relates are any of those azo lake pigments which may be employed in lithographic inks, e.g. Pigment Reds 48, 52, 53, 57. The resin esters employed may be e.g. esters of rosin acids, or of modified (hydrogenated, disproportionated, maleated, polymerised, phenolic modified) rosins acids. The alcohols used for esterification may typically have from 1 to 20 carbon atoms and be optionally substituted with such groups as halogen, e.g. chlorine. Suitable polyols may have from 1 to 10 OH groups such as glycerol and pentaerythritol. In a preferred embodiment of this invention a rosin is used which is a wood rosin, a gum rosin, a tall oil rosin or a product derived from any of these by hydrogenation, disproportionation or polymerization. In another preferred embodiment the resin ester is derived from a rosin by esterifying free acid groups on the rosin with glycerol or pentaerythritol. Optionally, other additives such as surface active agents may be added to aid the pigment synthesis in accordance with known technology. Such agents may include non-ionic, anionic, amphoteric and cationic surfactants, e.g. ethoxylated-alcohols, -phenols, -acids, -amines, rosin and modified rosin acid salts, alkyl sulphates, alkyl sulphosiccinates, alkyl aryl sulphonic acids, amine and quaternary ammonium salts. However, care has to be exercised in choice of type and quantity of such auxiliaries to ensure that their use does not negate the value of the main additive, the resin ester. The pigment product is used in a lithographic ink. Vehicles for such inks include aromatic petroleum hydrocarbon resins, alkali-refined linseed oil, pentaerythritol esters of phenolic modified rosins, maleic acid - modified rosin ester and mixtures hereof with each other and with tung oil. The invention also provides a lithographic printing ink comprising an ink vehicle and, as colourant, a resinated pigment in which from 10 to 100% preferably from 40 to 100% by weight of the resinated proportion of the product is a resin ester as described above. Further, the invention provides the use of a resinated pigment as defined above to reduce a pH drift in lithographic printing inks. The invention is illustrated by the following Examples. Example 1: 35.9 g of 4-amino toluene-3-sulphonic acid (98.2%) are dissolved in 265 ml of water using 16.2 g of 47% sodium hydroxide liquor with stirring. The temperature of the solution is reduced to 0-5°C by ice addition before adding 12.2 g of sodium nitrite which has previously been dissolved in 50 ml of water. 38 ml of concentrated hydrochloric acid (35%) is added to the solution with stirring to form the diazo salt. The volume of the suspension is adjusted to 750 ml at 0-5°C by ice addition. 9.5 g of a modified abietic acid rosin (trade name 'Recoldis A' and supplied by Langley Smith and Co.) are dissolved in 240 ml of water with 2.6 g of sodium hydroxide liquor (47%) and heated to 80°C with mechanical agitation. Once a resin solution is obtained, the solution is cooled to 50°C by addition of 240 ml water. 30 g sodium hydroxide liquor (47%) and 35.5 g of beta hydroxy naphthoic acid (BONA) are added with mechanical agitation continuing. 19 g of a resin ester dispersion known as Tacolyn 153 and supplied by Hercules BV are added to the solution. The volume of the dispersion is adjusted to 800ml at 0-5°C by ice addition. The diazo component is added to the resin/resin ester/BONA suspension over a period of 40 minutes with mechanical agitation and maintaining a temperature of 0-5°C and a pH of 10.8-11. After the coupling process is complete, the suspension is stirred for a further 15 minutes at the above conditions before adding 33.2 g of calcium chloride (80%). The suspension is held under the above conditions for 30 minutes in order to ensure full laking. The pH of the suspension is adjusted to 7.0 using dilute hydrochloric acid (10%) before steam heating to 80°C. The suspension is flushed to 65°C and filtered and washed salt free. The sample is dried overnight at 90°C before grinding to a powder. 20 g of the finished powder is incorporated into 80 g of an ink varnish consisting of 1 part distillate (known as PKWF 4/7 New and supplied by Halterman), 2 parts resin (known as Sparkle 93 and supplied by Lawter International) and 3.25 parts gelled hard resin (known as Luminex 55 and supplied by Lawter International). Mixing is performed on the back rolls of a Buhler SDY-200 3 roll mill at 23°C and 10 bar pressure for 5 minutes. The mixture is then given 3 x 10 bar passes over the three roll mill at 23°C (with 2 minutes back roll mixing between each pass) before let down to 18% pigmentation using a muller apparatus with more ink varnish. The sample shows comparable colour strength, significantly improved gloss and significantly improved low shear flow when compared to a standard (resin ester free) pigment as described in Example 4. The effect of this ink on pH drift of a fount solution used in a lithographic printing process is assessed according to the following method. 50 g of the ink is placed in a plastic container together with 150 ml of a standard fount solution (Fountsol F5, supplied by Inkland Ltd) and a VOSS dual - paddle mixer is used to agitate the mixture (150 rpm) for a period of 1 hour. The fount solution is separated from the ink and the pH measured. The results are recorded in Table 1. This sample shows a significant improvement in pH drift in comparison to an ink comprising resin ester free pigment (Example 4). Example 2: A pigment is prepared as in Example 1, except that 3.8 g of Recoldis A rosin are solubilised with 1.04 g of sodium hydroxide liquor (47%) and 30.4 g of Tacolyn resin ester dispersion is used. When incorporated into a heatset ink varnish and tested as in Example 1, this sample shows equivalent colour strength, significantly improved gloss, low shear flow and reduced pH drift (table 1) when compared to an ink comprisinf a resin ester free pigment (Example 4). Example 3: A pigment is prepared as in Example 1 except that no Recoldis A resin is used, but rather 38 g of Tacolyn 153 (50% w/w) resin ester dispersion is incorporated into the product. When this powder is incorporated into a heatset vamish as in Example 1, the final ink shows equivalent strength and significantly improved gloss, low shear flow and reduced pH drift when compared to an ink comprising a resin ester free pigment (Table 1). Example 4: A pigment is prepared as in Example 1 except that 19 g of Recoldis A rosin is solubilised with 5.2 g of sodium hydroxide liquor (47%) and no resin ester is incorporated in the product. The pH drift results of an ink prepared as in Example 1, but using this product are recorded in Table 1. pH drift of fount solution after stirring with ink for one hour using a VOSS dual-paddle mixer: Example 1 Example 2 Example 3 Example 4 Initial pH 4.6 4.6 4.6 4.6 Final pH 5.8 5.7 5.7 7.6 Drift +1.2 +1.1 +1.1 +3.0

Claims: The use of a resinated pigment in which from 10 to 100% by weight of the resinated proportion of the product is a resin ester, as colourant in a lithographic printing ink, wherein the resin ester is derived from a rosin by esterifying free acid groups on the rosin with an optionally substituted alcohol or polyol, and wherein the carboxylic acid groups have been fully reacted with the alcohol or polyol, and wherein the pigment is an azo lake pigment, with the proviso, that the alcohol is not an amino alcohol. The use as claimed in claim 1 in which from 40 to 100% by weight of the resinated proportion of the product is a resin ester. The use as claimed in claims 1 or 2 in which the rosin is a wood rosin, a gum rosin, a tall oil rosin or a product derived from any of these by hydrogenation, disproportionation or polymerization. The use as claimed in any one of claims 1 to 3 in which the resin ester is derived from a rosin by esterifying free acid groups on the rosin with glycerol or pentaerythritol. A lithographic printing ink comprising an ink vehicle and a resinated pigment as defined in any one of claims 1 to 4. The use of a resinated pigment as defined in any one of claims 1 to 4 to reduce a pH drift in lithographic printing inks.

Inventors: BLACKBURN JOHN BRYCE, KERWIN PAUL, MCGREGOR DAVID, BLACKBURN, JOHN BRYCE, KERWIN, PAUL, MCGREGOR, DAVID
Applicants: CIBA SC HOLDING AG, CIBA SPECIALTY CHEMICALS HOLDING INC.
Application year: 1997
Main classification: C09D11
IPC codes: C09D11, C09C3