LUBRICATING OIL COMPOSITIONS CONTAINING ORGANIC MOLYBDENUM COMPLEXES

Abstract: A lubricating oil composition is provided comprising a major amount of an oil of lubricating viscosity and a minor amount of, as an additive, at least one compound comprising a trinuclear molybdenum core and bonded thereto ligands capable of rendering the compound oil-soluble or oil-dispersible.

Description: LUBRICATING OIL COMPOSITIONS CONTAINING ORGANIC MOLYBDENUM COMPLEXES FIELD OF THE INVENTION The present invention relates to lubricant compositions containing molybdenum compounds and methods of making them. BACKGROUND OF THE INVENTION Molybdenum disulfide is a known lubricant additive. Unfortunately, it has certain known disadvantages some of which are caused by its insolubility in lubricating oils. Therefore, certain oil-soluble molybdenum sulfur-containing compounds have been proposed and investigated as lubricant additives. US-A- 2,951 ,040; - 3,419,589; -3,840,463; -4,966,719; -4,995,996; and - 4,978,464 are representative of patent specifications describing bothτnoiybdenum and sulfur. Molybdenum compounds for use as lubricant additives described in the art are principally dinuclear molybdenum compounds, characterised by the oxidation state Mo(V). The present invention concerns use of trinuclear molybdenum compounds as lubricant additives, i.e. characterised by a different oxidation state (Mo(IV); it is surprisingly found, according to the present invention, that trinuclear molybdenum compounds have improved properties as lubricating additives compared with dinuclear molybdenum compounds as evidenced by test results hereinafter, thus ameliorating the problem of improved lubricant performance demands from original equipment manufacturers (OEM's). The person skilled in the art would not be able to predict the behavior of Mo(IV) compounds in lubricating oils from the behavior of the dinuclear compounds. More specifically, in view of the difference in oxidation state, the performance of such compounds in redox reactions typical of systems that contain lubricant additives would not be known or predictable given a knowledge of the performance of dinuclear molybdenum compounds in those systems. U.S.-A-4,846,983 generally describes compositions with cores containing metal and oxygen and optionally sulfur in which the core contains at least one generally from 1 to 25, metal atoms, and the metal can be molybdenum. However, it does not describe synthesis of oxymolybdenum and oxosulfidomolybdenum compounds containing trinuclear molybdenum. Moreover, the synthetic conditions described therein are similar to those disclosed in patents and known in the art to make mononuclear and dinuclear molybdenum thiocarbamates. The literature describes trinuclear molybdenum compounds but either in an ionic form or having ligands with short chain alkyl groups; see, e.g., Shibahara, Coord. Chem: Rev. 123, 73-148(1993). Such described compounds are consequently not oil-soluble, and they have not been described as lubricating oil additives. Summary of the Invention In a first aspect, the invention is a lubricating oil composition comprising, or made by mixing, a major amount of an oil of lubricating viscosity and a minor amount of, as an additive, at least one compound comprising a trinuclear molybdenum core and bonded thereto ligands capable of rendering the compound oil-soluble or oil- dispersible. Preferably, the core contains non-metallic atoms consisting wholly or partly of sulfur and more preferably it consists of trinuclear molybdenum and sulfur. The additive may be in the form of mixtures of such compounds. The lubricant compositions according to the first aspect of the invention have excellent antiwear, antioxidant, and friction-reducing properties; also they may be compatible with other additives used in formulating commercial lubricating compositions and can be made from readily available starting materials. In a second aspect, the invention is an additive concentrate for blending with an oil of lubricating viscosity comprising, or made by mixing, an oleaginous carrier and from 1 to 200,000 ppm by weight, for example 50 to 150,00 such as 50 to 100,000 of the molybdenum of an additive defined in the first aspect of the invention, based on the weight of the concentrate. In a third aspect, the invention is a compound having the formula Mo 3 S k L n Q z wherein L represents independently selected ligands, n is from 1 to 4, k is at least 4, for example from 4 to 10, such as 4 to 7, Q is a neutral electron donating compound, and z ranges from 0 to 5, wherein the compound has a core having the structure In a fourth aspect, the invention is a method of lubricating an internal combustion engine comprising operating the engine and lubricating the engine with a lubricating oil composition of the first aspect of the invention. In a fifth aspect the invention is use of an additive as defined in the first aspect of the invention for enhancing one or more lubricating oil properties of a lubricating oil composition. In a sixth aspect, the invention is a method for preparing a compound comprising a trinuclear thio molybdenum core and bonded thereto ligands capable of rendering the compound oil-soluble or oil-dispersible, which method comprises reacting a trinuclear molybdenum source, a source of said ligands, and a source of sulfur to react in a liquid medium to form said compound. The Mo source and the S source may be in the same source. The molybdenum source may, for example, be a compound containing the [Mo 3 S 13 ] 2" ion or A trinuclear thiomolybdenum halide. Detailed Description of the Invention • OIL OF LUBRICATING COMPOSITION This oil may be selected from vegetable, animal, mineral, or synthetic oils. The oils may range in viscosity from light distillate mineral oils to heavy lubricating oils such as gas engine oil, mineral lubricating oil, motor vehicle oil, and heavy duty diesel oil. The oils may be unrefined, refined, and re-refined. The oil may be used oil. In general, the viscosity of the oil will range from about 2 centistokes to about 30 centistokes and especially in the range of 5 centistokes to 20 centistokes at 100°C. • COMPOUNDS The compounds may, for example, have the formula formula Mo 3 S k L n or mixtures thereof, wherein L represents a ligand which is independent from other ligands represented by L when n is more than 1 ; n is in the range from 1 to 4; and k is at least 4, for example in the range from 4 to 10, such as 4 to 7, preferably 4 or 7. Also, the compounds may have the formula Mo 3 S k E x L n or mixtures thereof, wherein L and n are defined as above, k is at least 1 , E is oxygen or selenium, x is at least 1 , and the sum of k and x is at least 4. The above formulae (Mo 3 S k L n and Mo 3 S k E x L π ) may each additionally include a moiety Q z wherein Q represents a neutral electron-donating compound such as water, amines, alcohols, phosphines and ethers, and z is in the range from 0 to 5 and includes non-stoichiometric values. The Mo 3 S k cores in the above formulae have a net charge of +4. Consequently, in order to neutralize such cores, the total charge among all ligands, L, in Mo 3 S k L n , must be -4. Four L monoanionic ligands are preferred. As indicated in the formulae, it is believed that oxygen and/or selenium may be substituted for sulfur in the core. However, in addition to the trinuclear molybdenum, the core should contain at least one, and preferably be primarily (i.e., greater than 50%) sulfur. Most preferred is a core consisting of molybdenum and sulfur alone. The balance, if any, is oxygen and/or selenium. When the core consists only of trinuclear molybdenum and sulfur it is represented by the formula Mo 3 S k , and with ligands attached is represented by the formula Mo 3 S k L n . The electron-donating compound, Q z , is merely present in the preceding formulae to fill any vacant coordination sites on the t rruclear molybdenum compound. The ligands, including ligands L, may be independently selected from the group of: - X R Xi — R ) X2 •> or and mixtures thereof, and perthio derivatives thereof wherein X, X,, X 2 and Y are independently selected from the group of oxygen and sulfur, and wherein R.,, R 2 , and R are independently selected from the group consisting of H and organo groups that may be the same or different. Preferably the organo groups are hydrocarbyl groups such as alkyl (e.g., in which the carbon atom attached to the remainder of the ligand is primary, secondary or tertiary), aryl, substituted aryl and ether groups. More preferably, all ligands are the same. Importantly, the organo groups of the ligands have a sufficient number of carbon atoms to render the compounds soluble or dtspersible in the oil. The compounds' oil solubility or dispersibility may be influenced by the number of carbon atoms in the ligands. Preferably the ligand source chosen has a sufficient number of carbon atoms to render the compound soluble or dispersible in the oil. In the compounds in the present invention, the total number of carbon atoms present among all of the organo groups of the compounds' ligands typically will be at least 21 , e.g. 21 to 800, such as at least 25, at least 30 or at least 35. For example, the number of carbon atoms in each alkyl group will generally range between I to I00, preferably I to 40 and more preferably between 3 and 20. Preferred ligands include dialkyldithiophosphate ("ddp"), xanthates, thioxanthates, dialkylphosphate, dialkyldithiocarbamate ("dtc"), and carboxylate and of these the dtc is more preferred. Multidentate organic ligands containing at least two of the above functionalities are also capable of binding to at least one of the trinuclear cores and serving as ligands. Without wishing to be bound by any theory, it is believed that one or more trinuclear molybdenum cores may be bound or interconnected by means of at least one of these multidentate ligands. Such structures fall within the scope of this invention. This includes the case of a muitidentate ligand having multiple connections to one core. Those skilled in the art will realise that formation of the compounds will require selection of appropriate ligands having suitable charge to balance the corresponding core's charge, The term "hydrocarbyl" denotes a substituent having carbon atoms directly attached to the remainder of the ligand and is predominantly hydrocarbyl in character within the context of this invention. Such substituents include the following: (1) hydrocarbon substituents, that is, aliphatic (for example alkyl or alkenyl), alicyclic (for example cycloalkyl or cycloalkenyl) substituents, aromatic-, aliphatic-and alicyclic-substituted aromatic nuclei and the like, as well as cyclic substituents wherein the ring is completed through another portion of the ligand (that is, any two indicated substituents may together form an alicyclic group); (2) substituted hydrocarbon substituents, that is, those containing nonhydrocarbon groups which, in the context of this invention, do not alter the predominantly hydrocarbyl character of the substituent. Those skilledin the art will be aware of suitable groups (e.g., halo, (especially chloro and fluoro), amino, alkoxyl, mercapto, alkylmercapto, nitro, nitroso, sulfoxy, etc.); (3) hetero substituents, that is, substituents which, while predominantly hydrocarbon in character within the context of this invention, contain atoms other than carbon present in a chain or ring otherwise composed of carbon atoms. Compounds having the formula Mo 3 S k L n Q z have cationic cores surrounded by anionic ligands that may be represented by structures (I) and (II) as depicted above. Generally, the trinuclear molybdenum containing compounds can be prepared by reacting a suitable molybdenum source, with a ligand source and, optionally, with a sulfur abstracting agent. This may be carried out in a suitable liquid medium which may be aqueous or organic. Oil-soluble or -dispersible trinuclear molybdenum compounds can be prepared, for example, by reacting in the appropriate solvent(s) (M 1 ) 2 Mo 3 S 13 n(H 2 0), wherein n varies between 0 and 2 and includes nonstoichiometric values, with a suitable ligand source such as a tetraalkylthiuram disulfide. Other oil-soluble or -dispersible trinuclear molybdenum compounds can be formed by reacting (M 1 ) 2 Mo 3 S 13 n(H 2 0), wherein n varies between 0 and 2 and includes nonstoichiometric values, a ligand source such as tetraalkylthiuram disulfide, dialkyldithiocarbamate, or dialkyldithiophosphate, and a sulfur abstracting agent such as cyanide ions, sulfite ions, or substituted phosphines. Alternatively, a trinuclear molybdenum-sulfur halide salt such as [M'] 2 [Mo 3 S 7 A 6 ], wherein, A = Cl, Br, or 1, may be reacted with a ligand source such as a dialkyldithiocarbamate or dialkyldithiophosphate in the appropriate solvent(s) to form an oil-soluble or dispersible trinuclear molybdenum compound. In the above formulae, M 1 is a counter ion such as NH 4 . The trinuclear molybdenum compounds are related by the number of sulfur atoms in the molybdenum core. Within the disclosed range, the number of the sulfur atoms in the core may be altered by the addition of sulfur abstractors such as cyanide and substituted phosphines, or sulfur donators such as elemental sulfur and organic trisulfides to the trinuclear molybdenum compounds. In general, the trinuclear molybdenum compounds can be purified by well known techniques such as chromatography; however, it may not be necessary to purify the compounds. The lubricating oil compositions of the present invention may be prepared by adding to an oil of lubricating viscosity a mixture of an effective minor amount of at least one trinuclear molybdenum compound, which may be prepared in amounts as described previously, and, if necessary, one or more co-additives such as described hereinafter. This preparation may be accomplished by adding the trinuclear molybdenum compound directly to the oil or by first mixing the trinuclear molybdenum compound in a suitable carrier fluid to achieve oil solubility or dispersibility, and adding the mixture to the lubricating oil. Co-additives may be added to the oil by any method known to those skilled in the art, either prior to, contemporaneously with, or subsequent to addition of the trinuclear molybdenum compound. The terms "oil-soluble" or "dispersible" used herein do not necessarily indicate that the compounds or additives are soluble, dissolvable, miscible, or capable of being suspended in the oil in all proportions. These do mean, however, that they are, for instance, soluble or stably dispersible in oil to an extent sufficient to exert their intended effect in the environment in which the oil is employed. Moreover, the additional incorporation of other additives may also permit incorporation of higher levels of a particular additive, if desired. Concentrates of the trinuclear molybdenum compounds and co- additives, if required, in a suitable oleagenous, typically hydrocarbon, carrier fluid provide a convenient means of handling them before their use. Oils of lubricating viscosity, such as those described above as well as aliphatic, naphthenic, and aromatic hydrocarbons are examples of suitable carriers for concentrates. These concentrates may contain about I to about 90 wt%/o of the additives based on the weight of the concentrate, preferred is I to 70 wt%, more preferably 20 to 70 wt%. The lubricating oil compositions made by combining an oil of lubricating viscosity containing at least one trinuclear molybdenum compound of the types and in the amounts described herein and optional co-additives may be used to lubricate mechanical engine components, particularly an internal combustion engine, by adding the lubricating oil thereto. The trinuclear molybdenum compounds of the present invention also possess antioxidant properties when used in a lubricating composition. Tests using the model compound cumene hydroperoxide in mineral oil basestock revealed that compounds having Mo 3 S k cores are more effective antioxidants than either conventional organic antioxidants or commercially available dinuclear molybdenum additive compounds such as dinuclear molybdenum alkylated dithiocarbamate. The lubricating compositions and concentrates of this invention comprise defined components that may or may not remain the same chemically before and after mixing with an oleagenous carrier. This invention encompasses compositions and concentrates which comprise the defined components before mixing, or after mixing, or both before and after mixing. CO-ADDITIVES Other known lubricant additives also may be used for blending in the lubricant composition of this invention These include dispersants, detergents, e g , single or mixed metal detergent systems, pour point depressants, viscosity improvers, antioxidants, surfactants, antiwear agents, and friction reducing agents These can be combined in proportions known in the art For example, additives containing phosphorus and/or sulfur compounds such as a zinc dialkyl dithio phosphate(ZDDP) can be prepared and used with the compounds of the present invention However, the compounds of the present invention may be effective or may even possess improved properties when used in lubricating compositions that are free or substantially free of added phosphorus and/or sulfur 1 e , phosphorus and/or sulfur in addition to (i e , except for) the phosphorus or sulfur contained in the trinuclear molybdenum compounds themselves A lubricating composition that is substantially free of phosphorus and/or sulfur is one in which the amount of phosphorus and/or sulfur is not more than is inherently present in base oils of lubricating viscosity Particularly noteworthy is the use of anti-oxidants in combination with the trinuclear molybdenum compounds Examples of suitable antioxidants are selected from copper containing antioxidants, sulfur-containing antioxidants, aromatic amine containing antioxidants and phenolic antioxidants Examples of suitable copper-containing antioxidants include oil-soluble copper compounds described in EP-B-24 146, EP-A-280 579 and EP-A-280 580 Thus, for example, the copper may be blended into the oil as an oil-soluble copper salt of a synthetic or natural carboxylic acid Examples of carboxylic acids from which suitable copper salts may be derived include C 2 to C 18 carboxylic acids (e g , acetic acid, and fatty acids such as steaπc acid and palmitic acid), unsaturated acids (e g , oleic acid), branched carboxylic acids (e g , naphthenic acids of molecular weight of from 200 to 500, neodecanoic acid and 2-ethylhexanoιc acid), and alkyl-or alkenyl-substituted dicarboxy c acids (e g , polyalkenyl-substituted succinic acids such as octadecenyl succinic acids, dodecenyl succinic acids and polyisobutenyl succinic acids) In some cases, suitable compounds may be derived from an acid anhydride, for example, from a substituted succinic anhydride. The copper antioxidant may be, for example, a copper dithiocarbamate or copper dithiophosphate. Other copper and sulfur- containing antioxidant compounds, for example, copper mercaptides, xanthates, thioxanthates, are also suitable for use in accordance with the invention, as are copper sulfonates, phenates (optionally sulfurized) and acetylacetonates. Other copper compounds which may be used in accordance with the invention are overbased copper compounds. Examples of such compounds, and of processes for their preparation, are described in US-A-4, 664,822 and EP-A-0 425 367. The copper compound may be in cuprous or cupric form. Examples of suitable aromatic amine-containing antioxidants are aromatic amines which have at least one aromatic group directly attached to at least one amine nitrogen atom. Secondary aromatic amines, especially those having two aromatic groups attached to the same amine nitrogen atom, are preferred, but the use of other aromatic amines is not excluded. The amines may contain one or more aromatic groups, for example at least two aromatic groups. Where there are two aromatic groups both are preferably bonded directly to the same amine nitrogen. Compounds in which two aromatic groups are linked by a covalent bond or by an atom or group (e.g., an oxygen or sulfur atom, or a -CO-, -S0 2 - or alkylene group) may be used. Aromatic rings, which are preferably aromatic hydrocarbon rings may be unsubstituted or substituted by one or more substituents selected from alkyl, cycloalkyl, alkoxy, aryloxy, acyl, acylamino, hydroxy, and nitro groups. Amines containing alkyl-substituted aromatic hydrocarbon rings are preferred, especially those containing two alkylsubstituted phenyl groups. Preferred N-aryl amines for use in accordance with the invention are naphthylamines and, especially, diphenylamines, including alkyl substituted diphenylamines, wherein the alkyl group may be the same or different, having I to 28 carbon atoms. Other nitrogen containing antioxidants, for example, phenothiazine type compounds, may also be used in this invention. Examples of phenolic antioxidants include (a) sterically hindered tertiary-alkylated monohydric phenols such as those described in more detail in US- A-2, 944,086; -3,043,775; and -3,211 ,652; and (b) methylene bridged tertiary alkyl polyphenols, such as 4,4'-methylene bis (2,6-di-tertbutylphenol) and 2,2'-methylene bis (4,6-di-(1 ,1 ,2-trimethylpropyl)phenol), and mixtures of (a) and (b) such as those described in more detail in EP-B-0456925. Examples of sulfur-containing antioxidants (compounds) are alkaline earth metal salts of alkylphenolthioesters having preferably C5 to C12 alkyl side chains, calcium nonylphenol sulfide, ashless oil soluble phenates and sulfurized phenates, phosphosulfurized or sulfurized hydrocarbons, phosphorus esters and other sulfur-containing molybdenum containing compounds. Other examples of sulfur containing antioxidants are metal salts of dihydrocarbyl dithiophosphate or dihydrocarbyl dithiocarbamate compounds, wherein the metal is selected from Zn, Mn, Ni, Al, Group 1 metals and Group 2 metals. Other sulfur containing compounds include those described in EP-A-699 759, for example, sulfides of oils, fats or polyolefins, in which a sulfur group having two or more sulfur atoms is adjoined and bonded together in a molecular structure. Examples include sulfurized sperm oil, sulfurized pinene oil, sulfurized soybean oil, sulfurized polyolefin, sulfurized esters, dialkyl disulfide, dialkyl polysulfide, dibenzyl disulfide, ditertiary butyl disulfide, polyolefin polysulfide, thiadiazole type compound such as bis-alkyl polysulfide thiadiazole, and sulfurized phenol. Preferable antioxidants are copper-containing antioxidants, aromatic amine containing compounds including diphenylamines and derivatives thereof that have an effect herein comparable to diphenylamines), and mixtures thereof. Examples of copper containing antioxidants include copper polyisobutylene succinic anhydride ("copper PIBSA") and copper oleate; diphenylamines include all effective derivatives of diphenylamines. Thus, the lubricant compositions of the present invention may include a minor amount of at least one antioxidant and at least one oil-soluble or oil- dispersible trinuclear molybdenum compound. The lubricant composition may include a mixture of the trinuclear molybdenum compounds and antioxidants of the types disclosed herein, the lubricating oil and/or other additives disclosed herein per se, and/or of any intermediates and reaction products occurring as a result of the mixture. In combination, the antioxidants and trinuclear molybdenum compounds are present in a minor effective amount to produce the enhanced lubricating performance, particularly friction reduction, friction reduction retention, antioxidancy and/or antiwear properties in the oil. The trinuclear molybdenum compounds disclosed herein in combination with the foregoing antioxidants produce an enhanced effect with respect to lubricating performance not evident in the presence of the trinuclear molybdenum compounds or antioxidants alone. Additionally, the enhanced effect of the trinuclear molybdenum compounds in the presence of these antioxidants would not be expected by one skilled in the art based on the performance of dinuclear molybdenum and copper additives due to the difference in oxidation state of the molybdenum in the trinuclear molybdenum compounds and dinuclear molybdenum compounds. The admixture of antioxidants with the trinuclear molybdenum compounds allows reduction in molybdenum treat rates for effective friction reduction. The benefits are exemplified herein with bis-alkyldiphenyl amine ("DPA") and copper- polyisobutylene succinic anhydride, with copper-PIBSA demonstrating a stronger enhancement. Thus in the present invention, the combination of the trinuclear molybdenum compounds and the antioxidants demonstrates enhanced performance at reduced treat rates than dinuclear molybdenum additives such as Mo 2 O 2 S 2 (dtc) 2 . The enhanced performance of the combination of the trinuclear molybdenum compounds with these antioxidants typically can allow the use of the trinuclear molybdenum compounds at concentrations about two times lower than without the antioxidants. Effective enhancement of lubricating performance, e.g., friction reduction (decreased friction coefficients), can be achieved according to the present invention. The lubricating compositions contain minor effective amounts, such as at least 1 ppm preferably ranging from I to 2000 ppm molybdenum from the trinuclear molybdenum compounds, such as 5 to 1000, preferably 20 to 1000, more preferably 5-750 ppm, and more preferably 10-300 ppm, all based on the weight of the lubricating composition. The amount of antioxidant additive is a minor effective amount, preferably from about 0.00 I to about 10 wt% based on the weight of the finished oil, more preferably, from about 0.01 to about 2 wt% of the weight of the finished oil. Typically for copper containing antioxidants the amount is I to 1000 ppm of copper, such as I to 200 ppm copper, and for antioxidants, e.g., aromatic amine and sulfur containing, phenolic and ZDDP antioxidants containing antioxidants the preferred amount is up to 2 wt%. Within the above ranges, one skilled in the art can select the particular effective combinations of amounts to produce the enhancement in lubricating properties, particularly friction reducing and/or anti-wear, desired for the particular application. The selection within these ranges may be accomplished to optimize for either enhanced friction reducing or anti-wear performance or both. Thus, the trinuclear molybdenum compounds allow for the use of a decreased amount of antioxidant or, alternatively, with an equal amount of antioxidant they allow for the use of a decreased amount of trinuclear compound compared with the use of dinuclear molybdenum compounds, while still achieving the desired enhanced lubricating, i.e., wear and/or friction, performance in the oil, thus making their use potentially more cost effective than current additives. These benefits can be achieved in basestock as well as fully formulated lube oils. Essentially phosphorus and/or sulfur-free oils also may also be treated. FURTHER TECHNICAL EFFECTS OF INVENTION As is known in the art, lubricating oil compositions such as those containing dinuclear molybdenum sulfide additives lose their effectiveness over time when used in an engine. It is believed that one reason for this loss in effectiveness is that the lubricating oil is adversely affected by exposure to NO x compounds present in the engine's crankcase. Some attempts to cure this deficiency have focused on the incorporation of supplementary sulfur donors and antioxidants such as dibenzyldisulfide derivatives (DBDS). These attempts have not been completely successful. The additives of the invention are effective in reducing friction at low concentration and remain effective even after use in an engine, are effective at low concentration, and retain their friction reduction properties even in the absence of supplementary sulfur sources or antioxidants Thus in a further aspect the invention is a method for enhacing the friction reduction retention properties of a lubricating composition by adding to a major amount of oil of lubricating viscosity a minor amount of a compound of the first aspect of the invention These compounds were surprisingly found to enhance the lubricating properties of the compositions when used at concentrations of as low as 50 ppm molybdenum based on the total weight of the composition This is a very large reduction in concentration compared with conventional dinuclear molybdenum sulfur additives Those additives are typically used in concentrations ranging upwards from 500 ppm based on the total weight of the lubricating composition Additionally, the conventional dinuclear additives require supplementary sulfur donor compounds in order to be as effective as the compounds of the present invention The compounds in the present invention were found to enhance the friction reduction and friction reduction retention properties of lubricating compositions For example, lubricating compositions containing 150 ppm molybdenum as Mo 3 S 7 (dtc) 4 based on the weight of the lubricating composition were exposed to N0 2 treatment By comparison, conventional dinuclear molybdenum sulfide lubricating oil additives were found to be less effective than the trinuclear molybdenum compounds of this invention when the dinuclear compounds were used at a concentration of 150 ppm molybdenum, based on the weight of the composition, before and after exposure to N0 2 A lubricating composition's fuel economy and fuel economy retention properties are believed to be related to the composition's friction retention and friction reduction retention properties Consequently, lubricating compositions containing trinuclear molybdenum compounds having the formula Mo 3 S 7 (dtc) 4 and mixtures thereof are believed to possess good fuel economy and fuel economy retention properties As is also known in the art, lubricating oil compositions containing molybdenum sulfide additives lose their friction reducing effectiveness over time when used in an internal combustion engine While an enhancement in friction reducing properties is observed when the compound is added to a fresh oil, little if any friction reduction is observed when Mo 2 0 2 S 2 (dtc) 2 is added to a used oil in which a loss in friction reducing properties has occurred, depending on the degree of oil aging and degradation The invention provides a composition that is capable of enhancing and restoring the friction reducing effectiveness of lubricating oils Thus, in a still further aspect, the invention is a composition capable of improving the friction reduction properties of a used lubricating oil The friction reduction properties of a used oil can be enhanced or restored by adding to a major amount of used oil of lubricating viscosity a minor amount of at least one compound as defined in the first aspect of the invention A minor amount of at least one trinuclear molybdenum compound may be added to a fresh oil in order to enhance its effectiveness, particularly its friction reducing and wear reducing effectiveness The oils may range in viscosity from light distillate mineral oils to heavy lubricating oils such as gas engine oil, mineral lubricating oil, motor vehicle oil, and heavy duty diesel oil A used lubricating oil is one that has been subjected to operating conditions such as to exposure to high shear forces, exposure to high temperature, exposure to a hostile chemical or physical environment, or similar conditions The compounds of the present invention can also be used as additives in the formulation of fresh lubricating oil compositions As such they possess superior friction reducing properties compared with dinuclear molybdenum sulfide additives that are known in the art In cases where the compounds of the present invention are added to a used lubπcating oil that are known in the art, the resulting fπction reducing performance may exceed that of the originally formulated fresh oil EXAMPLES EXAMPLES The invention will be more fully understood by reference to the following examples. The procedures and equipment used for the Falex Block-On-Ring test were similar to those used in ASTM677-83 (Ranking Resistance of Materials to Sliding Wear Using Block-On-Ring Wear Test). As used herein "AO" means antioxidant, "eh" means "ethylhexyl". SL300 σM) and SL321 (TM) are commercial dinuclear molybdenum compounds available from Ashai Denka, Japan. MV-L (TM) is Moly Van-L a commercial dinuclear molybdenum compound available from Vanderbilt Chemical Company. As used herein "coco" is an alkyl chain or mixture of chains of varying even numbers of carbon atoms of from typically C 8 to C 18 , "dtc" means dialkyldithiocarbamate, "ddp" means dialkyldithiophosphate. Example 1 : Synthesis Of Mo 3 S 4 [(2-ethylhexyl) 2 dtc] 4 by Abstraction of Sulfur with Sulfite in Water. (NH 4 ) 2 Mo 3 S 13 .2H 2 0 (0.77 g, I mmol) was added to a solution of potassium bis(2-ethylhexyl)dithiocarbamate (2.13 g, 6 mmol) in water (50 mL). In another flask, potassium sulfite (0.95 g, 6 mmol) was dissolved in water (50 ML). The solution of potassium sulfite was added dropwise to the molybdenum /dialkyldithiocarbamate mixture. The mixture was allowed to react for 24 hours at room temperature, and then extracted with ether and the ether solution filtered. The ether extract was distilled, the product extracted with methanol (3 x 30 mL), to afford the product which was dried under vacuum to yield Mo 3 S 4 [(2-ethylhexyl) 2 dtc] 4 Synthesis Of Mo 3 S 4 [(2-ethylhexyl) 2 dtc] 4 . by Abstraction of Sulfur with Cyanide in Water. (NH 4 ) 2 Mo 3 S 13 .2H 2 0 (0.77 g, I mmol) was added to a solution of potassium bis(2-ethylhexyl)dithiocarbamate (2.13 g, 6 mmol) in water (50 mL). In another flask, potassium cyanide (0.39 g, 6 mmol) was dissolved in water (50 ML). The solution of potassium cyanide was added dropwise to the molybdenum/dialkyl-dithiocarbamate mixture. The mixture was allowed to react for 24 hours at room temperature, and then extracted with ether and the ether solution filtered. The ether extract was distilled, the residue extracted with methanol (3 x 30 mL), to afford the product which was dried under vacuum to yield Mo 3 S 4 [(2-ethylhexyl) 2 dtc] 4 . Example 3: Synthesis Of Mo 3 S 4 [(2-ethylhexyl) 2 dpp] 4 . by Abstraction of Sulfur with Phosphine. An acetonitrile (50 mL) solution containing (NH 4 ) 2 Mo 3 S 13 .2H 2 0 (0.77 g, 1.0 mmol) and PPh3 (1.57 g, 6.0 mmol) and bis(2-ethylhexyl)dithiophosphoric acid (2.34 g, 6.6 mmol) was refluxed for 24 hours and then cooled to room temperature. The acetonitrile was decanted off and the residue washed 2x with methanol (20 mL). The residue was dissolved in pentane and filtered; the pentane-solution was concentrated by distillation and filtered again, and the remaining of pentane removed to yield Mo 3 S 4 [(2-ethylhexyl) 2 dpp] 4 . Example 4: Synthesis Of Mo 3 S 4 [(octyl) 2 dtc] 4 . by Abstraction of Sulfur with Cyanide using Thiuram Disulfide as Ligand Source A methanol (50 mL) solution containing (NH 4 ) 2 Mo 3 S 13 .2H 2 0 (0.77 g, 1.0 mmol) and KCN (0.585 g, 9.0 mmol) and tetraoctyl thiuram disulfide (2.1 g, 3.3 mmol) was refluxed for 24 hours and then cooled to room temperature. The methanol was decanted off and the residue was washed 2x with ethanol (20 mL). The residue was dissolved in pentane and filtered, the pentane was evaporated to yield Mo 3 S 4 [(octyl) 2 dtc] 4 . Example 5: Synthesis Of Mo 3 S 7 [(lauryl) 2 ddp] 4 . To a solution of potassium dilauryldithiophosphate (2.2 g, 4.4 mmol) in methanol (100 mL) was added a solution of [NEt 4 ] 2 Mo 3 S 7 . Cl 6 (0.98 9, 0.1 mmol) in acetonitrile (50 mL). The combined solution was heated at 60°C with stirring for 12 h. The solvents were decanted and the residue was washed with methanol followed by acetonitrile. The washed residue was dissolved in pentane and filtered. The pentane was evaporated to yield Mo 3 S 7 [(lauryl) 2 ddp] 4 . Example 6: Synthesis of Mo 3 S 7 [(2-ethylhexyl) 2 dtc] 4 A 1 : 1 methanol/THF solution containing (NH 4 ) 2 Mo 3 S 13 .2H 2 0 (3.8 8 g, 5. 0 mmol and tetra(2-ethylhexyl) thiuram disulfide (9.5 g, 15 mmol) was heated at 60°C for 24 hours and cooled to room temperature. The solution was filtered, the solvents evaporated, and the residue washed with methanol. The residue was dissolved in THF, the resulting solution filtered, and the THF removed by distillation to yield Mo 3 S 7 [(2-ethylhexyl) 2 dtc] 4 The Mo 3 S k L 4 (k = 4-7) compounds are related by the number of sulfur atoms in the molybdenum-sulfur core. The number of the sulfur atoms in the core may be altered by the addition of sulfur abstractors such as cyanide and substituted phosphines or sulfur donators such as elemental sulfur and organic trisulfides to the Mo 3 S k L 4 compounds. In Examples 7 through 10, the compounds of the invention were evaluated for friction and wear performance using a Falex block-on-ring tribometer. The data was obtained at a speed of 420 rpm, load of I 00 kg (220 lb.), and a temperature of 100°C for 2h. Data reported include block wear scar volume, measured by profilometry, the end of test friction coefficient (Last Coef.), and the (Avg. Coef) friction coefficient over the 2 hour test. The end of the test friction coefficient is that obtained at the end of the test, and the average friction coefficient provides information, on the activity of the added material, i.e., samples that attain the same decreased friction coefficients faster are considered to contain more active friction reducing compounds. In examples 7-10 the samples tested consisted of Solvent 150 Neutral (S150N) lubricating oil, l% ZDDP, and compounds of the present invention having 500 ppm molybdenum based on the total weight of the lubricating oil. The procedures and equipment used in Examples 7 through I0 are similar to those used in ASTM Test G77-83 (Ranking Resistance of Materials to Sliding Wear Using Block-on-Ring Wear Test. Comparative Example 11 For comparative purposes, the Falex block-on-πng was conducted using only Solvent 150 Neutral (S150N) and 1 % ZDDP. The results are shown in Table I. TABLE Friction Test Run Compound Wear (10- 2 mm 3 ) Last Coef. Avg. Coef Ex. 7 Mo 3 S 4 [C 8 H 17 ) 2 dtc] 4 1.69 0.041 0.057 Ex. 8 Mo 3 S 4 [C 8 H 17 ) 2 dpp] 4 1.64 0.040 0.060 Ex. 9 Mo 3 S 7 [(C 13 H 27 )dtc] 4 0.80 0.063 0.078 Ex. 10 Mo 3 S 7 [(C 13 H 27 ) 2 dpp] 4 0.74 0.059 0.064 Ex. I I None 0.91 0.113 0.115 Examples 12 to 15: In these examples, the compounds of the invention were evaluated for friction and wear performance as described for Examples 7 through 10. In examples 12-15 the samples tested consisted of a IOW30 fully formulated oil combined with compounds of the present invention having 500 ppm molybdenum based on the total weight of the lubricating oil. Comparative Example 16: For comparative purposes, the Falex block-on-ring was conducted using a 1 OW30 fully formulated motor oil. The results are shown in Table II. TABLE II Friction Tes it Run Compound Wear (10 _2 mm 3 ) Last Coef. Avg. Coef Ex. 12 Mo 3 S 4 [(C 8 H 17 ) 2 dtc] 4 0.58 0.032 0.040 Ex. 13 Mo 3 S 4 [(C 8 H 17 ) 2 ddp] 4 0.58 0.029 0.038 Ex. 14 Mo 3 S 4 [(C 13 H 27 ) 2 dtc] 4 0.71 0.032 0.044 Ex. 15 Mo 3 S 4 [(C 13 H 27 ) 2 ddp] 4 0.62 0.035 0.044 Ex. 16 None 2.86 0.132 0.130 Examples 17-20: Differential scanning calorimetry (DSC) tests were conducted on samples in Solvent 150 Neutral (SI5ON). with compounds of the present invention having 500 ppm molybdenum based on the total weight of the lubricating oil. In this DSC test, a sample of the oil is heated at a rate of e.g., 5°C /minute and the rise in sample temperature relative to an inert reference is measured. The temperature at which an exothermic reaction occurs or the oxidation onset temperature is a measure of the oxidative stability of the sample. It is believed that higher DSC temperatures indicate improved oxidative stability compared with compounds having lower DSC temperatures. The results of the tests are shown in Table III. Comparative Example 21 : The DSC test was performed with Solvent 150 Neutral (S I50N) for comparative purposes. The results are shown in Table III. TABLE III Test Run Compound DSC (°C) Ex. 17 Mo 3 S 4 [(C 8 H 17 ) 2 dtc] 4 285 Ex. 18 Mo 3 S 4 [(C 8 H 17 ) 2 ddp] 4 285 Ex. 19 Mo 3 S 7 [(C 13 H 27 ) 2 dtc] 4 268 Ex. 20 Mo 3 S 7 [(C 13 H 27 ) 2 ddp] 4 277 Ex. 21 None 212 Example 22: The compounds of this invention were evaluated for their ability to decompose hydroperoxides. Hydroperoxides are known to engage in reactions that degrade the lubricant, consume additives, and cause viscosity increase, wear, and formation of sludge and deposits. In this test a compound in a base stock mixture (2.25:1 mixture of Solvent 150 Neutral (S 150N) : Solvent I00 Neutral (S IOON) by weight) containing ZDDP is reacted with a known amount of cumene hydroperoxide (CHP). The CHP and the compound solution are reacted at a temperature of 125°C for one hour and the product is analyzed by gas chromatography linked with mass spectrometry (GC/MS). The amount of CHP consumed indicates how effective the compound is at neutralizing hydroperoxides, i.e., a higher amount indicates better antioxidancy. The elemental molybdenum concentration in the test solution was constant. In compositions A and B the base stock contained a primary ZDDP and a trinuclear molybdenum compound. For comparison, composition C also contained a primary ZDDP and a commercial dinuclear molybdenum lubricant additive, Mo 2 0 2 S 2 (dtc) 2 which has a mixture of octyl 2 dtc and coco 2 dtc ligands. In compositions D and E, the base stock contained a secondary ZDDP and a trinuclear molybdenum compound. For comparison, composition F contained a secondary ZDDP and Mo 2 0 2 S 2 (dtc) 2 . TABLE IV Composition Compound Moles of CHP Moles of CHP consumed per consumed per mole of compound mole of molybdenum A Mo 3 S 4 [(2-ethylhexyl) 2 dtc] 4 8560 2853 B Mo 3 S 7 [(coco) 2 dtc] 4 2442 C Mo 2 0 2 S 2 (dtc) 2 1120 560 D Mo 3 S 4 [(2-ethylhexyl) 2 dtc] 4 7973 2658 E Mo 3 S 7 [(coco) 2 dtc] 4 8473 2824 F Mo 2 0 2 S 2 (dtc) 2 1 174 587 Table IV shows that the trinuclear molybdenum compounds of the present invention decompose CHP approximately seven times better than the commercial dinuclear additive on a molecular basis in this test. On a normalized molybdenum mole basis, the novel trinuclear compounds perform four to five times better than the commercial dinuclear molybdenum additive in this test. Example 23.: In this example, compounds of the present invention and a commercial additive were evaluated for friction and wear performance. The samples were run at a concentration of 500 ppm molybdenum in a sulfur-free synthetic basestock with added esters to increase the solubility of the molybdenum compounds in the synthetic lubricating oil. Table V shows performance results for the trinuclear molybdenum compounds of the present invention versus a commercial molybdenum additive. A comparative example using an oil substantially free of sulfur and containing no added molybdenum compounds was not possible because the oil alone caused seizure during test start-up before the 220 lb. (100 kg) load was reached. TABLE V Compound Wear Friction Friction (1 0-2 nlm3) Last Coef. Avg. Coef Mo 3 S 7 [(coco) 2 dtc] 4 2.76 0.052 0.061 Mo 2 O 2 S 2 [(coco) 2 dtc) 2 2.33 0.097 0.089 The trinuclear molybdenum dithiocarbamate compounds reduces friction in sulfur free basestocks more than the dinuclear molybdenum dithiocarbamate. Example 24: In this example, the compounds of the invention and commercial additives were evaluated for friction and wear performance in a Falex block-on-ring test procedure. The data was acquired at a speed of 420 rpm, load of 220 lb. (1 00 kg), and a temperature of 100°C for 120 minutes. The samples were run at a concentration of 500 ppm molybdenum in a fully formulated motor oil without ZDDP (a common antiwear additive) and no additional phosphorus containing compounds. Although some of the molybdenum compounds contain phosphorus, the molybdenum compounds were added at a lower treat rate than is typically used for ZDDP and contain less phosphorus by weight. Total phosphorus concentration in these oils was <0.02 %. Trials I through 4 show performance results of samples of trinuclear molybdenum dithiocarbamates of the present invention and commercial dinuclear molybdenum dithiocarbamates; these test cases are phosphorus free. Trials 5 through 7 exhibit the performance of the trinuclear molybdenum compounds of the present invention and a commercial dinuclear additive with dithiophosphate ligands. The samples in trials 5 through 7 are substantially free of phosphorous beyond that contained in the ligands. A lubricating composition that is substantially free of phosphorus is one in which the amount of phosphorus is no more than is inherently present in base oils of lubricating viscosity. For comparison purposes, trial 8 shows the performance of the fully formulated motor oil without ZDDP used as the lubπcating oil in the test; this test case was phosphorus free. TABLE VI Trial Compound Wear Friction Friction (10 "2 mm 3 ) Last Coef. Avg. Coef 1 Mo 3 S 4 [(octyl) 2 dtc] 4 1.01 0.036 0.042 2 Mo 3 S 7 [(coco) 2 dtc] 4 0.92 0.033 0.042 3 Mo 2 0 2 S 2 [(octyl) 2 dtc] 2 1.43 0.051 0.065 4 Mo 2 0 2 S 2 [(coco) 2 dtc] 2 1.48 0.053 0.061 5 Mo 3 S 4 [(octyl) 2 ddp] 4 1.14 0.044 0.048 6 Mo 3 S 4 [(lauryl) 2 ddp] 4 1.29 0.064 0.058 7 Mo 2 0 2 S 2 [(octyl) 2 ddp] 2 1.81 0.060 0.065 8 None 1.81 0.1 12 0.113 In the following examples 25 to 28, reference will be made to the following drawings where: Figure I demonstrates the average friction coefficients obtained from 2 hour Falex block-on-ring testing of molybdenum compounds and molybdenum compounds in an oil formulated with or without antioxidants but without ZDDP. The y-axis is from 0.0 to 0. 13. Figure 2 shows comparative friction traces for a series of oils, with or without anti-oxidants. Figure 3 shows friction traces comparing a dinuclear Mo compound with a trinuclear Mo compound, with or without anti-oxidants. Figure 4 shows friction traces for 75 ppm Mo as Mo 3 S 7 [(coco) 2 dtc] 4 in four base oils. Figure 5 shows friction traces for a dinuclear Mo compound, at 75 ppm Mo concentration in oils with or without anti-oxidants, and comparative friction traces of a trinuclear Mo compound with an antioxidant. EXAMPLE 25 The mixtures were prepared as follows: The dinuclear molybdenum complex or trinuclear molybdenum containing compound was placed with the appropriate equivalent of Cu(ll) carboxylate (2.0 equivalents for Mo 2 S 4 (dtc) 2 ; 0.5, 1.0, and 1.5 equivalents for Mo 3 S 4 (dtc) 2 or Mo 3 S 4 (ddp) 2 in a flask and tetrahydrofuran ("THF) is added. After stirring for 24 hours the THF was evaporated off and the resulting mixture dissolved in S 15ON base oil that contained zinc dialkyl dithiophosphate ("ZDDP"). Alternatively, the examples indicated with an asterisk (*) were prepared by mixing the additives in S15ON containing ZDDP at temperatures up to 70°C for a period of time sufficient to dissolve the additives. The friction and wear results are detailed in Table VII below. The compositions formed by the foregoing methods using an Mo 3 - containing starting material as a class possess UV and IR spectra characteristic of trinuclear molybdenum containing compounds. Friction and wear testing, Results of friction and wear tests using the combination of copper and trinuclear molybdenum compounds in S 150N with l% ZDDP are given in Table VII. For comparison purposes the results for the molybdenum in the form of dinuclear Mo 2 S 4 (coco 2 dtc) 2 , and trinuclear Mo 3 S 4 (octyl 2 dtc) 2 or Mo 3 S 4 (2-ethylhexyl 2 dtc) 2 , Mo 3 S 7 (coco 2 dtc) 2 , Mo 3 S 4 (n-octyl 2 ddp) 2 or Mo 3 S 4 (2-ethylhexyl 2 ddp) 2 , Mo 3 S 7 (lauryl 2 ddp) 4 , Cu(oleate) 2 , and the copper in combination with certain dinuclear and trinuclear molybdenum compounds are listed. Friction and wear data were acquired using a Falex block-on-ring tribometer as described above. Table VII Molybdenum at 500 ppm Mo Wear Volume End Average Sample ( 10- 2 mm 3 ) Coefficient Coefficient (*) S 150N + 1% ZDDP 1 06 0 1 1 1 0 1 12 S150N + 1% ZDDP with (*) 55 ppm Cu as Cu(oleate)2 046 0108 0108 (*) 1 10 ppm Cu as Cu(oleate)2 085 0106 0107 (*) 165 ppm Cu as Cu(oleate)2 103 0107 0107 Mθ2S4(coco2dtc)2 1.10 0041 0054 Mo2S4(coco2dtc)2 + 331 ppm Cu as Cu(oleate)2 054 0.041 0048 Mo3S4(octyl2dtc)4 169 0041 0.057 Mo3S4(octyl2 tc)4 + 55 ppm Cu as Cu(oleate)2 1.27 0038 0.048 Mo3S4(ocr l2 tc)4 + 1 10 ppm Cu as Cu(oleate)2 0.64 0.038 0.047 Mo3S4(octyl2 tc)4 + 165 ppm Cu as Cu(oleate)2 053 0.039 0048 (*) Mo3S7(coco2dtc)4 0.62 0 044 0 058 (*) Mθ3S7(coco2 tc)4 +1 10 ppm Cu as Cu(oIeate)2 0 58 0 045 0.053 Mθ3S4(octyl2 dp)4 164 0040 0060 Mo3S4(octyl2ddp)4 + 55 ppm Cu as Cu(oleate)2 103 0042 0054 Mθ3S4(octyl2ddp)4 + 1 10 ppm Cu as Cu(oleate)2 053 0036 0045 Mo3S4(octyl2ddp) 4 + 165 ppm Cu as Cu(oleate)2 043 0038 0048 (*)Mo3S7(lauryl2ddp)4 049 0037 0049 (*)Mo3S7(lauryl2ddp)4+ l 10 ppm Cu as Cu(oleatc)2 036 0034 0044 The wear and friction results indicated that a trinuclear molybdenum compound in combination with copper carboxylates had enhanced effect on anti-wear in S 150N with ZDDP. The total wear was 50% less than S 150N with ZDDP alone and up to 75% less than the trinuclear molybdenum compounds alone in S 150N with ZDDP. The trinuclear molybdenum in combination with copper carboxylates also exhibited a tendency toward decreased friction. The examples given for the dinuclear molybdenum (Mo 2 ) complexes demonstrated that significantly more copper was required to obtain performance comparable to trinuclear molybdenum compounds used with lower copper concentrations. Thus, the addition of the trinuclear molybdenum compounds and copper(ll) carboxylates to lubricating oils is demonstrated to enhance the lubricating properties of the oils. Example 26 To test the performance of trinuclear molybdenum compounds having dtc and ddp ligands in combination with antioxidants, bench tribometer testing was performed using a Falex Block-On-Ring tribometer. The molybdenum containing compounds were added at a concentration of 500 ppm Mo to an oil which was fully formulated but without ZDDP or supplemental antioxidants. The compounds were also tested in the same no-ZDDP formulation to which two antioxidants, bis-nonyl- diphenylamine (DPA) at 0.35 wt% and copper-polyisobutylene succinic anhydride at 0.4 wt%, yielding approximately 70 ppm copper, were added. The formulations were tested in a Falex Block-on-Ring (BOR) tribometer as described below. Results are specified in Table VIII. Table VIII Figure I demonstrates the average friction coefficients obtained both without and with antioxidants in a no-ZDDP formulation. The data demonstrate that the trinuclear molybdenum compounds with antioxidants provide enhanced performance, particularly as demonstrated by the average friction coefficients as compared to the dinuclear molybdenum complexes in the presence of antioxidants. Samples are identified as a No ZDDP Base Case Oil b No ZDDP Base Case Oil + Antioxidants c Mo 2 0 2 S 2 (coco 2 dtc) 2 d Mo 2 0 2 S 2 (coco 2 dtc) 2 + Antioxidants e Mo 2 0 2 S 2 (2-eh 2 dtc) 2 f Mo 2 0 2 S 2 (2-eh 2 dtc) 2 + Antioxidants g Mo 3 S 4 (2-eh 2 dtc) 2 h Mo 3 S 4 (2-eh 2 dtc) 2 + Antioxidants. i Mo 3 S 7 (coco 2 dtc) 4 j Mo 3 S 7 (coco 2 dtc) 4 + Antioxidants k Mo 2 0 2 S 2 (2-eh 2 ddp) 2 I Mo 2 0 2 S 2 (2-eh 2 ddp) 2 + Antioxidants m Mo 2 0 2 S 2 (hexyl 2 ddp) 2 n Mo 2 0 2 S 2 (hexyl 2 ddp) 2 + Antioxidants o Mo 2 0 2 S 2 (2-eh 2 ddp) 2 p Mo 2 0 2 S 2 (2-eh 2 ddp) 2 + Antioxidants q Mo 3 S 4 (octyl 2 ddp) 4 r Mo 3 S 4 (octyl 2 ddp) 4 + Antioxidants s Mo 3 S 7 (lauryl 2 ddp) 4 t Mo 3 S 7 (lauryl 2 ddp) 4 + Antioxidants Example 27 The frictional properties of a set of oils (1-6), was determined. All of the oils were based on the same ZDDP-containing formulated oil, the "starting oil". Four of oils (1 to 4) contained Mo at a concentration of 150 ppm by weight provided by admixing the trinuclear Mo compound Mo 3 S 4 ((2-ethylhexyl) 2 dtc with the "starting oil", but differed in their respective contents of antioxidants. The remaining two oils (5 and 6) were both Mo-free but differed in their antoxidant content. The results are shown firstly in Figure 2 as traces a, b, c, d, e and f, wherein the characteristics of Oils 1-6 and the identity of the trace corresponding to a particular oil are shown below: (Oils 7 and 8 are discussed below). Oil Characteristics Trace Mo Compound No dialkyldiphenylamine (DPA) c Trinuclear No Cu-polyisobutylene succinic anhydride (CuPIBSA) 2 DPA (0.35%) d Trinuclear 3 Cu PIBSA (0.40%) e Trinuclear DPA (0.35%) Trinuclear Cu PIBSA (0.40%) No DPA; no Cu PIBSA Mo-free DPA (0.35%) and Mo-free Cu PIBSA (0.40%) No DPA; No Cu PIBSA Dinuclear DPA (0.35%); Cu PIBSA (0.40%) Dinuclear Either with or without the specified antioxidants the friction coefficients are similar and vary between 0.12 and 0.14 throughout the temperature range tested for the Mo-free oils (Traces a and b in Figure 2). At a molybdenum concentration of 150 ppm, enhancement in friction coefficients is observed for the combination of Mo 3 S 4 ((2-ethylhexyl)2dtc) 4 with the antioxidants, used individually or together. (Traces c, d, e and f in Fig.2). For further comparison purposes, Oils 7 and 8, (see above), based on the "starting oil" and containing a dinuclear Mo compound represented by Mo 2 O 2 S 2 (coco 2 dtc) 2 (MV822 from Vanderbilt Chemical Company) at 150 ppm Mo concentration were similarly tested. Their friction traces (k and I respectively) together with trace f are shown in Figure 3. The data demonstrate the enhanced performance of the trinuclear , molybdenum compounds with antioxidants in comparison with the dinuclear molybdenum compounds at a low concentration of 150 ppm of molybdenum. Example 28 The procedure of Example 27 was repeated using Mo 3 S 7 (coco 2 dtc) 4 as the trinuclear Mo compound and at a concentration of 75 ppm of Mo, corresponding oils being identified as Oils 9-12. The comparison dinuclear Mo compound was the same as that used in Example 27, but at a concentration of 75 ppm of Mo, corresponding oils being identified as Oils 13 and 14 respectively. The results are shown firstly in Figure 4 as traces g, h, i and j, wherein the characteristics of Oils 9-14 and the identity of the trace corresponding to a particular oil are shown below: Oil Characteristics Trace Mo Compound No DPA Trinuclear No Cu PIBSA 10 DPA (0.35%) Trinuclear 11 Cu PIBSA (0.40%) Trinuclear 12 DPA (0.35%) j Trinuclear and Cu PIBSA (0.40%) 13 No DPA, No Cu PIBSA m Dinuclear 14 DPA (0 35%), Cu PIBSA (0 40%) n Dinuclear The comparison friction traces for oils containing the dinuclear Mo- contaming compound are shown in Fig 5 as traces m and n, together with trace j The data demonstrate that at 75 ppm Mo, only minor fπctional improvements over molybdenum-free oils are seen without antioxidants or with the co-addition of DPA whereas the use of Cu-PIBSA and the combination of Cu-PIBSA and DPA yielded enhanced friction coefficients at a concentration of the trinuclear molybdenum compounds corresponding to 75 ppm of Mo They further demonstrate enhanced performance for trinuclear Mo compounds compared with dinuclear Mo compounds In Figures 2-5, y axis = friction coefficient from 0 to 0 14 secondary y axis for temperature + degrees C from 0 to 500 x axis = time from 0 to 2 hours and t is a representative temperature profile In the following examples 29 to 33, reference will be made to the accompanying drawings wherein Figure 6 shows the average coefficient of friction of fresh oils containing dinuclear and trinuclear molybdenum-sulfur compounds at a concentration of 150 ppm of Mo based on the weight of the oil Figure 7 shows the average coefficient of friction at 140°C of oils containing molybdenum-sulfur additive at a concentration of 150 ppm before and after N0 2 treatment Figure 8 shows the average coefficient of friction at 100°C of oils containing molybdenum-sulfur compounds at a concentration of 500 ppm molybdenum before and after N0 2 treatment Figure 9 shows the average coefficient of friction at 100°C of oils containing molybdenum-sulfur compounds at a concentration of 750 ppm molybdenum before and after N0 2 treatment Figure 10 compares the coefficient of friction at 1 10°C of an oil containing a trinuclear molybdenum sulfur compound and a dinuclear molybdenum sulfur compound when both are subjected to N0 2 treatment Figure 11 compares the coefficient of friction at 135°C of an oil containing a trinuclear molybdenum sulfur compound and a dinuclear molybdenum sulfur compound when both are subjected to N0 2 treatment Figure 12 shows the coefficient of friction and wear for lubπcating compositions containing molybdenum-sulfur compounds at different concentrations Figure 13 shows the wear volume and dinuclear and trinuclear molybdenum compounds during the Test Figure 14 shows the fπctional coefficient of dinuclear and trinuclear molybdenum compounds during the Test Example 29 In order to assess the retention of friction reducing properties of the compounds of the present invention, the compounds were admixed into a fully formulated oil, their friction properties determined, then treated with N0 2 for a fixed period of time, and then finally, the friction properties determined again Therefore, the degree of retention of fπction reducing properties is determined by measuring the friction properties of the test oil before (fresh) and after N0 2 treatment (used) A sample with good retention of friction reducing properties will display minimal, if any, change in its friction properties before and after N0 2 treatment Conditions for NO, Treatment 1.15g of a sludge precursor (150°C residual of heavy cat cracked naphtha) was added to a sample (130g). 1 % NO z in air was bubbled through the resulting mixture at 130°C for 9 hours at a rate of 2.67 litres/hour. The friction measurement of the N0 2 treated oil was determined the following day after NO 2 treatment. Conditions for Boundary Friction Measurement The boundary friction measurements were determined on a high frequency reciprocating rig (HFRR) at three temperatures (60C, 100C and 140°C) for 30 minutes at each temperature. The friction was measured using a 6mm steel ball in a reciprocating motion against a flat steel plate under a load of 4N, a stroke length of 1 mm, and a reciprocating frequency of 20Hz. The center line average surface roughness for the ball is about 0.01 μm. The coefficient of friction was sampled every 5 seconds and is quoted as an average friction over the 30 minute period. Fresh oil, disc and ball were used at each temperature. Compositions with good friction reducing properties provide low coefficient of friction values, i.e., the lower coefficient of friction, the better the friction reducing property. The friction coefficient at 100 and 140 deg. C are quoted since these temperatures are considered the most suitable in relating to the performance of molybdenum friction reducing additives in the lubricating engine contacts. This example demonstrates that lubricating compositions containing compounds having the formula Mo 3 S 7 (dtc) 4 or Mo 3 S 4 (dtc) 4 have superior boundary friction properties compared to lubricating compositions containing dinuclear molybdenum sulfur additives even when the dinuclear additives are used in the presence of supplemental sulfur sources such as DBDS at low molybdenum concentrations such as 150 ppm molybdenum based on the total weight of the composition. The "S 7 " compounds are also shown to possess better boundary friction enhancement and retention properties than the "S4" compounds; however, the trinuclear molybdenum compounds coordinated with four sulfur atoms possess enhanced boundary friction and friction retention properties in comparison with dinuclear molybdenum compounds. Figure 6 and 7 show the superiority of the Mo 3 S 7 (dtc) 4 compounds in both boundary friction reduction and friction reduction retention when compared to three other formulated oils. Compounds represented by Mo 2 O x S y dtc 2 Sakuralube 155™ and are supplied by Ashai Denka, Japan. All four lubricating compositions contained 150 ppm of molybdenum as the indicated molybdenum sulfur additive. Additionally, the compositions contained 0.09 wt% phosphorous. The formulation details are summarized in Table IX. Figure 6 shows that samples containing Mo 3 S 7 (dtc) 4 exhibit superior boundary friction between 60°C and 140°C. Figure 7 shows that the average coefficient of friction at 140°C remains low, even after exposure to 1 % N0 2 in air treatment, for the sample containing Mo 3 S 7 (dtc) 4 . All four oils are fully formulated oils containing known lubricant additives, for example, dispersant, anti-wear agent, detergent, viscosity improvers, and antioxidants, in proportions known in the art. Example 30 This example shows that the trinuclear molybdenum sulfur compositions have superior friction reduction and friction reduction retention properties compared with conventional dinuclear molybdenum sulfide additives even when used at concentrations typically used for the dinuclear additives, for example 500 and 750 ppm of molybdenum. See Figures 8 and 9. Formulation details are provided in Table IX. Table IX Mo-150ppm & P-0.09% Oil Identification Mo 2 O x S y dtc Mo 2 O x S y dtc + Mo 3 S 4 dtc Mo 3 S 7 dtc DBDS SAKURALUBE 0.36 0.36 155 Mo 3 S 4 (dtc) 4 0.09 Mo 3 S 7 (dtc) 4 0.12 Dibenzyl- 0.4 disulfide Mo-500ppm & P-0.09% Oil Identification Mo 2 O x S y dtc Mo 2 O x S y dtc + Mo 3 S 4 dtc Mo 3 S 7 dtc DBDS SAKURALUBE 1.21 1.21 155 Mo 3 S 4 (dtc) 4 0.31 Mo 3 S 7 (dtc) 4 0.42 Dibenzyl- 0.4 disulfide Mo-750ppm & P-0.09% Oil Identification Mo 2 O x S y dtc o 2 O x S y dtc + Mo 3 S 4 dtc Mo 3 S 7 dtc DBDS SAKURALUBE 1.82 1.82 155 Mo 3 S 4 (dtc) 4 0.46 Mo 3 S 7 (dtc) 4 0.63 Dibenzyl- 0.4 disulfide Example 31 - Resistance to performance loss due to N0 2 . In order to simulate the loss of frictional benefits of molybdenum additives due to oil ageing in an engine, several formulated oils containing 500 ppm Mo as either MV822 or Mo 3 S 7 ((coco) 2 dtc) 4 were degraded via N0 2 /air sparging at an elevated temperature. In this example, MV822™is represented by Mo 2 0 2 S 2 (dtc) 2 , and is available from the Vanderbilt Chemical Company. 250 ml samples of the oils were held at 130°C with a sparge of 55 ml/min of 1% NO 2 in air for 18 hours with a periodic withdrawal of 20 ml. samples for friction testing. The frictional performance of the sampled oils was determined using a Cameron-Plint TE77 tribometer. The test protocol uses a 6 mm steel ball in reciprocating motion against a flat steel plate under a normal load of 5 kg, a stroke length of 7 mm, and a reciprocation frequency of 22 Hz. During the test the oil is held for approximately 20 minutes at each of four temperatures 50°C, 80°C, 110°C, and 135°C while the friction coefficient is measured. The friction coefficients measured at the end of the 110°C and 135°C temperature periods as a function of hours of NO 2 treatment are shown in figures 10 and 11 respectively. These temperatures are considered significant in relating to the performance of molybdenum friction reducing additives for automotive fuel economy. It may be seen in figures 10 and 11 that the Mo 3 S 7 ((coco) 2 dtc) 4 (open squares) trinuclear molybdenum compound demonstrates far superior retention of its friction reduction performance under N0 2 oxidation than the dinuclear Mo 2 0 2 S 2 (dtc) 2 ) additive (shaded squares). Example 32 - Performance at Low Concentrations In order to compare the friction-reducing and anti-wear performance of trinuclear molybdenum compounds with conventional dinuclear molybdenum additives, a series of oils was bench friction and wear tested at various concentrations less than or equal to 500 ppm of Mo in a formulated automotive oil. The formulations were tested in a Falex Block-on-Ring (BOR) tribometer at 100°C with a 220 lb. load, a speed of 420 rpm (44 radians/sec.) (0.77 m/s), and a 2 hour test length. Friction coefficients are reported as the end of run value. Data reported include the block wear scar volume, measured by profilometry and the end of test friction coefficient. The results are shown in Table X. Table X The results are also represented graphically in Figure 12. It may be seen that the trinuclear Mo compound provides superior friction and wear performance at low concentrations. Example 33 In order to further test the retention properties of trinuclear Mo compounds and compare them to commercially available dinuclear additives a number of small engine aging runs were performed with periodic sampling and friction and wear performance measurement using a Falex Block-on-Ring tribometer. The compounds were tested in a fully formulated 10W-30 oil that did not contain supplemental antioxidants, i.e., ZDDP was present but Cu, diaryl amines and/or phenols were not included. Three molybdenum containing formulations were examined in his formulation according to the following test: Sample ID for Tables and Graphs Mo Compound Mo Concentration Based on the t. of the Composition A Mo 2 0 2 S 2 (dtc) 4 500 B Mo 3 S 7 (coco 2 dtc) 4 500 C Mo 3 S 7 (coco 2 dtc) 4 50 The oils were aged in a 2 cylinder, water-cooled, 12 horse power Honda 'generator engine'. Incidentally, operating conditions were set similar to that of the Sequence III E/lll F high temperature oxidation tests. The engine is a four stroke carburated overhead cam engine, and it is attached to a 6.5 kw electric generator. The engine was operated under steady state conditions at 3600 rpm, a sump temperature of 150°C, an air/fuel ratio of 16.5/1 and the power fixed at 4.8 kW. The fuel used was a blend of isooctane 90% and toluene 10%. Fuel consumption during the Test was approximately 3 pounds per hour. A 2000 g initial lube charge was used with makeup oil being added continuously via a low flow peristaltic pump. Samples were removed every 12 hours for friction and wear measurements. The makeup oil addition is then the combination of the consumption rate (approx. 12g/hr) and the sample size (150g) for an average addition rate of approximately 25g per hour. The fresh and a number of the withdrawn samples were tested in a Falex Block-on-Ring (BOR) tribometer at 100°C oil temperature, a 220 lb, load, a speed of 420 rpm (44 radians/sec.) (0.77 m/s), for 2 hours. Friction coefficients are reported as both the end of run value (end friction coefficient) and the average value (average friction coefficient) over the entire 2 hours. Following the testing, block wear volumes are determined by multiples and profilometry and are presented as mm 3 x 100. The procedures followed and equipment used in the Falex Block-on-Ring tests were similar to those in ASTM Test G77-83 (Ranking Resistance of Material to Slide Wear Using Block-on-Ring Wear Test). The friction and wear test results for the three engine aging runs according to the test are shown in Table XI. Table XI SAMPLE Hours in Wear Volume End Friction Average engine 10 ~2 mm 3 Coefficient Friction Coefficient A 0 1.55 0.036 0.052 Mo 2 O 2 S 2 (dtc) 2 12 0.73 0.032 0.039 500 ppm Mo 24 1.03 0.037 0.043 36 2.02 0.060 0.062 48 3.64 0.098 0.094 90 3.56 0.113 0.106 B Mo 3 S 7 ((coco) 2 d 0 0.44 0.035 0.0407 tc) 4 500 ppm Mo 99 0.80 0.031 0.036 97 0.85 0.038 0.043 180 1.32 0.044 0.050 C Mo 3 S 7 ((coco) 2 d 0 1.39 0.091 0.091 tc) 4 50 ppm Mo 22 1.81 0.097 0.099 53 1.02 0.070 0.074 77 1.57 0.074 0.080 84 1.81 0.089 0.092 88 1.82 0.104 0.102 108 1.92 0.113 0.112 124 1.57 0.108 0.110 163 1.31 0.122 0.121 Figures 13 and 14 show that the trinuclear Mo compounds provided superior performance retention compared with commercial dinuclear Mo additive when tested at equal (500 ppm Mo) concentrations. Even at 50 ppm Mo, the trinuclear compound tested provided significant anti-wear performance retention and a degree of friction benefit and performance retention. In the following Example 34 and Comparative Example 35, reference is to be made to accompanying drawings wherein Figure 15 shows the results of frictional performance measurements (heavy trace) of an oil containing a commercial dinuclear molybdenum additive over time. The oil's temperature was varied during the test, temperature being depicted in the fine trace. Figure 16 shows the results of frictional performance measurements (heavy trace) of an oil containing a compound having the formula Mo 3 S 4 (2-ethylhexyl 2 dtc) 4 . The oil's temperature was varied during the test; temperature is depicted in the fine trace. Figure 17 shows the results of frictional performance measurements (heavy trace) of an oil containing a compound having the formula Mo 3 S 7 ((coco) 2 dtc) 4 . The oil's temperature was varied during the test; temperature is depicted in the fine trace. Figure 18 shows the frictional performance of 5 lubricating compositions. Prior to the start of the measurement, four samples of lubricating oil were aged for a period of time under operating conditions. One sample was not aged. At the conclusion of ageing, a commercial dinuclear molybdenum compound was added to the oil. The temperatures of each admixture were varied in time (trace T), and frictional performance was measured for the oil that was not aged (trace a), aged 12 hours (trace b), aged 23 hours (trace c), aged 36 hours (trace d), and aged 72 hours (trace e). Example 34 In order to test the effectiveness of friction reduction by the addition of molybdenum containing compounds to used engine lubricants, a dimeric molybdenum additive (Mo 2 0 2 S 2 (dtc) 2 ), and several trimeric molybdenum compounds Mo 3 S 4 (2-ethylhexyl 2 dtc) 4 and Mo 3 S 7 ((coco) 2 dtc) 4 were added at a concentration of 500 ppm molybdenum to a non-molybdenum containing oil which was aged in a Honda generator engine for 72 hours under conditions which simulate a Sequence HIE engine test. Ageing was conducted in a 2 cylinder, carburated, four stroke, water-cooled, 12 horsepower, Honda "generator engine". The engine was attached to a 6.5 kw electric generator during the test. The engine was operated under steady state conditions at 3,600 rpm, a sump temperature of 150'C, an air/fuel ratio of 16.5/1 and a fixed power output of 4.8 kW. The frictional performance of the aged oil treated with the various molybdenum additives was determined using a Cameron-Plint TE77 tribometer The test protocol used a 6 mm steel ball in reciprocating motion against a flat steel plate under a normal load of 5 kg , a stroke length of 7 mm , and a reciprocation frequency of 22 Hz During the test the oil is held for approximately 20 minutes at each of four temperatures 50, 80, 110, and 135°C while the friction coefficient is measured From the friction trace in Figure 15, it may be clearly seen that the commercial dinuclear molybdenum additive Mo 2 O 2 S 2 (dtc) 2 does not impart the expected low friction coefficients, generally <0 06 at temperatures over 100°C for a fully effective molybdenum additive, to the oil On the other hand, Figures 16 and 17 show that the nuclear molybdenum compound, Mo 3 S 4 (2-ethylhexyl 2 dtc) 4 (Figure 16) and Mo 3 S 7 ((coco) 2 dtc) 4 (Figure 17) give very low friction coefficients between 0 04 and 0 05 at the higher test temperatures Comparative Example 35 The friction reducing properties of commercial dinuclear molybdenum additives were also investigated for comparison with the compounds in the present invention Fresh oil of lubricating viscosity was used in an internal combustion engine under operating conditions for various times to form a used lubricating oil A dinuclear molybdenum additive having the formula Mo 2 0 2 S 2 (dtc) 2 was then combined with the used lubricating oil at 500 ppm Mo The frictional performance of the additive was then determined according to the method of Example 34 Figure 18 shows the results of those tests The different traces show the performance of mixtures of the dinuclear molybdenum additive with lubricating oils aged for progressively longer times Trace (a) is a fresh oil, trace (b) is aged 12 hours, trace (c) is aged 23 hours, trace (d) is 36 hours, and trace (e) is aged 72 hours Trace (T) shows the variation of temperature with time during the performance test Fιgure18 reveals that, while some improvement in friction reducing performance is obtained when the dinuclear molybdenum additive is combined with a fresh oil, that benefit gradually diminishes when that additive is combined with lubricating oils that have been aged under operating conditions. In these examples, no benefit is obtained when the commercial additive is combined with oils that have aged 72 hours or longer. By comparison, Example 34 shows that a benefit is obtained when combining lubricating oils that have been aged for 72 hours with the trinuclear molybdenum compounds of the present invention.

Claims: CLAIMS 1. A lubricating oil composition comprising, or made by mixing, a major amount of an oil of lubricating viscosity and a minor amount of, as an additive, at least one compound comprising a trinuclear molybdenum core and bonded thereto ligands capable of rendering the compound oil-soluble or oil-dispersible. 2. The composition of claim 1 wherein the core contains non-metallic atoms consisting wholly or partly of sulfur. 3. The composition of claim 1 or claim 2 wherein the core consists of trinuclear molybdenum and sulfur. 4. The composition of any of the preceding claims wherein the compound has the formula Mo 3 S k L n or mixtures thereof, wherein L represents a ligand which is independent from other ligands represented by L when n is more than 1 ; n is in the range from 1 to 4; and k is at least 4, for example in the range from 4 to 10, such as 4 to 7. 5. The composition of claim 1 or claim 2 wherein the compound has the formula Mo 3 S k E x L n or mixtures thereof, wherein L and n are defined as in claim 4, k is at least 1 , E is oxygen or selenium, x is at least 1 , and the sum of k and x is at least 4. 6. The composition of claim 4 or claim 5 wherein the formula additionally includes a moiety Q z , wherein Q represents a neutral electron-donating compound, and z is in the range from 0 to 5 and includes non-stoichiometric values. 7. The composition of any of the preceding claims wherein the ligands or ligands L, are represented by one or more of the structures having the formula — X — R, or and mixtures thereof, and perthio derivatives thereof wherein X, X 1 f X 2 and Y are independently selected from the group of oxygen and sulfur, and wherein R,, R 2 , and R are independently selected from the group consisting of H and organo groups that may be the same or different. 8. The composition of claim 7 wherein the organo groups independently represent alkyl, substituted or unsubstituted aryl, or ether groups. 9. The composition of claim 8 wherein the groups are alkyl groups each having from 1 to 100, for example 1 to 40, such as 3 to 20, carbon atoms. 10. The composition of any of the preceding claims wherein the ligands are or L independently represents a dialkyldithiophosphate, thioxanthate, dialkylphosphate, dialkyldithiocarbamate, xanthate, or carboxylate ligand. 11. The composition of any of the preceding claims wherein the weight of molybdenum from the trinuclear molybdenum compound is at least 1 , for example 1 to 2000, such as 5 to 1000, preferably 20 to 1000, ppm based on the weight of the composition. 12. The composition of any of the preceding claims wherein the total number of carbon atoms is all of the ligands' or all L's organo groups is at least 21 , such as 21 to 800. 13. The composition of any of the preceding claims wherein the oil of lubricating viscosity is substantially free of sulphur. 14. The composition of any of the preceding claims further comprising, or made by mixing, at least one antioxidant additive. 15. The composition of claim 14 wherein the antioxidant is a copper-containing antioxidant, a sulfur-containing antioxidant, a phenolic antioxidant, an aromatic amine-containing antioxidant or mixtures thereof. 16. The composition of any of the preceding claims further comprising one or more dispersants, detergents, pour point depressants, viscosity modifiers, surfactants and antiwear agents. 17. An additive concentrate for blending with an oil of lubricating viscosity comprising, or made by mixing, an oleaginous carrier and from 1 to 200,000 ppm by weight, for example 50 to 150,000 such as 50 to 100,000, of the molybdenum of an additive as defined in any of claims 1 to 12, based on the weight of the concentrate. 18. An additive concentrate of claim 17 further comprising, or made by mixing, at least one antioxidant additive as defined in claim 14 or claim 15, whereby the concentrate contains from 1 to 90 weight per cent, such as 1 to 50, of additives based on the weight of the concentrate. 19. A compound having the formula Mo 3 S k L n Q z wherein L represents independently selected ligands, n is from 1 to 4, k is at least 4, for example from 4 to 10, such as 4 to 7, Q is a neutral electron donating compound, and z ranges from 0 to 5, wherein the compound has a core having the structure (I) (ii) 20. A method of lubricating an internal combustion engine comprising operating the engine and lubricating the engine with a lubricating oil composition as claimed in any of claims 1 to 16. 21. The use of an additive or additives as defined in any of claims 1 to 16, for enhancing one or more lubricating properties of a lubricating oil composition. 22. A method for preparing a compound comprising a trinuclear thio- molybdenum core and bonded thereto ligands capable of rendering the compound oil-soluble or oil-dispersible, which method comprises reacting a trinuclear molybdenum source, a source of said ligands, and a source of sulfur to form said compound. 23. The method of claim 22 wherein the molybdenum source is a compound containing the Mo 3 S 13 J 2" ion or a trinuclear thiomolybdenum halide.

Inventors: ARUNASALAM VELAUTHA CUMARAN, BAXTER DANIELLA MARIA VERONICA, COYLE CATHERINE LOUISE, CREEGAN KATHLEEN MARIE, FANG HOWARD L, FRANCISCO MANUEL ANTHONY, GIBSON FREDERICK ALASTAIR, GLYDE ROGER, GUZI PETER JOHN, LETA DANIEL, MCCONNACHIE JONATHAN MARTIN, PICTROSKI CHARLES FREDERICK, STIEFEL EDWARD IRA, ARUNASALAM, VELAUTHA, CUMARAN, BAXTER, DANIELLA, MARIA, VERONICA, COYLE, CATHERINE, LOUISE, CREEGAN, KATHLEEN, MARIE, FANG, HOWARD, L., FRANCISCO, MANUEL, ANTHONY, GIBSON, FREDERICK, ALASTAIR, GLYDE, ROGER, GUZI, PETER, JOHN, LETA, DANIEL, MCCONNACHIE, JONATHAN, MARTIN, PICTROSKI, CHARLES, FREDERICK, STIEFEL, EDWARD, IRA
Applicants: EXXON CHEMICAL PATENTS INC, EXXON RESEARCH ENGINEERING CO, EXXON CHEMICAL PATENTS INC., EXXON RESEARCH AND ENGINEERING COMPANY
Application year: 1997
Main classification: C10M159
IPC codes: C07C333, C07F9, C07F11, C10M135, C10M137, C10M139, C10M159, C10N10, C10N40