SUPPORTED CATALYST SYSTEM

Abstract: This invention relates to supported metallocene catalyst systems and to methods for their production and use. Specifically, this invention relates to supported catalyst systems having unique, predetermined properties resulting from the designed distribution of catalyst components within and upon porous support particles. The methods of this invention are particularly well suited for the support of two or more metallocenes.

Description: SUPPORTED CATALYST SYSTEM The application is based on Provisional Application Serial No.60/012,185, filed February 23, 1996, and Provisional Application Serial No 60/032,710, filed December 13, 1996 FIELD OF THE INVENTION This invention relates generally to supported metallocene catalyst systems and to methods for their production and use Specifically, this invention relates to supported metallocene catalyst systems having unique, predetermined properties resulting from the designed distribution of catalyst components within and/or upon the support particles. BACKGROUND The new generation of metallocene catalyzed polymers is expected to have profound effects on the polyolefin industry Polyolefin resins produced by metallocene catalyst in general have a number of improved properties as compared to conventional polymers produced with Ziegler-Natta catalysts As more and more product manufacturers begin utilizing metallocene produced polymers, various areas for polymer improvement will become apparent Currently, polymer producers may choose from a variety of techniques to manipulate the polymer such as post reactor polymer degradation, blending, change of catalyst, use of additives and varying the polymerization conditions Metallocene catalyzed propylene polymers are among the newest metallocene produced polymers now commercially available One major product area for these new polymers is in spunbond and melt blown nonwoven fabrics. The metallocene produced propylene polymers have a number of advantages over conventional polymers. For example, these polymers have a narrow molecular weight distribution which enable significantly higher spinning speeds and finer denier fibers. In addition, due to their unique molecular architecture, these polymers have an extractable level that is less than one third that of conventional polymers. It has been found, however, that when certain metallocene produced propylene polymers are used to make spunbond fabrics at very high line speed, the bonding ofthe fibers into the finished web can be deficient. This deficiency is believed to be due at least in part to the fact that the polymer has a very narrow tacticity distribution as compared to conventionally produced propylene polymer. The narrow tacticity distribution ofthe polymer causes the fabric to have a very narrow bonding window, i.e., range of temperatures over which the fibers will bond. This narrow bonding window in conjunction with high line speed results in fabrics that are inadequately bonded. In order to address this bonding problem, the present inventors sought to manipulate the polymer tacticity distribution. It was hypothesized that broadening the tacticity distribution ofthe propylene polymer would result in a broadened bonding window. The present inventors have found that the tacticity distribution of isotactic polypropylene can be broadened by making the polymer with at least two different metallocenes, provided that two or more metallocenes are chosen that produce polymer having different tacticities. It is known in the art to use two metallocenes to make polymer having broadened molecular weight distribution. EP 0 310 734, for example discloses the use of at least two different metallocene catalysts which are chiral and stereorigid in combination with an aluminum compound to produce polymer having a broad molecular weight distribution. Although these catalysts are described as being useful for the production of polypropylene, the disclosure is limited to non¬ supported catalyst systems. EP 645 401 also describes the use of at least two stereorigid metallocenes, of which at least one has substituted indenyl ligands. These catalysts produce high molecular weight isotactic polypropylene having a broad molecular weight distribution. WO 94/28034 describes supported metallocene catalyst systems containing one metallocene. These metallocenes have high activity and are capable of producing high molecular weight isotactic polypropylene without fouling the reactor. The catalyst system is prepared by premixing the metallocene and alumoxane activator then combining the reaction product with support material. Thus the prior art teaches that high molecular weight, isotactic polypropylene may be produced with supported metallocene catalyst systems. The prior art further teaches the preparation of high molecular weight istotactic polypropylene having a broad molecular weight distribution using two or more stereorigid metallocenes, of which at least one has substituted indenyl ligands. To our knowledge, however, nothing in the prior art addresses the problems associated with narrow tacticity distribution. The present inventors have found that the tacticity distribution of isotactic polypropylene may be broadened by selecting two or more metallocenes where the first metallocene is capable of producing isotactic polypropylene ("metallocene A") and the second metallocene, which is stereorigid and has substituted indenyl ligands, is capable of producing highly isotactic polypropylene ("metallocene B"). These catalyst systems have high activity and produce isotactic polymer that not only has a broadened tacticity distribution but has high weight average molecular weight, good melt flow rate and low extractables. Additionally, the present inventors have discovered that supported metallocene catalyst systems having selected attributes may be prepared by manipulating the placement ofthe metallocene catalyst system components on and within the support material. For example, the present inventors have found that reactor fouling is reduced or eliminated and the polymer product morphology significantly improved when two or more metallocenes are layered on and in the support material particles. This layering is accomplished by combining the support with a solution of metallocene A, drying the support, then combining the dried supported metallocene A with a solution of metallocene B. SUMMARY This invention relates generally to a method for preparing a supported metallocene catalyst, said method comprising the steps of: (a) combining support material and a first solution comprising a first metallocene; then (b) drying the mixture thereby forming supported first metallocene; then (c) combining the supported first metallocene with a second solution comprising a second metallocene wherein the second metallocene is different from the first; then (d) drying the resulting mixture. More specifically, this invention relates to a method for preparing a supported metallocene catalyst, said method comprising the steps of: (a) combining porous support material and a first solution comprising solvent and a first metallocene wherein the volume of the first solution is less than about three times the total pore volume ofthe porous support; then (b) drying the thereby formed supported first metallocene; then (c) combining the supported first metallocene with a second solution comprising solvent and a second metallocene wherein the second metallocene is different from the first and wherein the volume of solution is less than about three times the total pore volume ofthe supported first metallocene; then (d) drying the resulting mixture. Even more specifically, this invention relates to a method for preparing a supported metallocene catalyst system, said method comprising the steps of: (a) combining porous support material having active hydroxyl groups and a first solution consisting essentially of solvent and a first metallocene wherein the volume of the first solution is less than about 3.0 times the total pore volume ofthe porous support; then (b) drying the mixture until residual solvent is removed thereby forming supported first metallocene; then (b) combining the supported first metallocene with a second solution comprising solvent, a second metallocene, and alumoxane wherein the second metallocene is different from the first and wherein the volume of solution is less than about 3.0 times the total pore volume ofthe supported first metallocene; then (c) drying the resulting mixture. Additionally this invention relates to catalyst systems prepared by the above methods and to polymerization processes involving the use of these catalyst systems. DETAILED DESCRIPTION Catalyst System Components Metallocenes Generally three components make up the catalyst systems of this invention; two or more metallocenes, activator and support material. As used herein "metallocene" refers generally to compounds represented by the formula Cp m MR n X q wherein C p is a cyclopentadienyl ring which may be substituted or derivative thereof which may be substituted, M is a Group 4, 5, or 6 transition metal, for example titanium, zirconium, hafnium, vanadium, niobium, tantalum, chromium, molybdenum and tungsten, R is a hydrocarbyl group or hydrocarboxy group having from one to 20 carbon atoms, X is a halogen, and m=l-3, n=0-3, q=0-3, and the sum of m+n+q is equal to the oxidation state ofthe transition metal Methods of making and using metallocenes are very well known in the art For example, metallocenes are discussed in United States Patent Nos 4,530,914, 4,542,199, 4,769,910, 4,808,561, 4,871,705, 4,933,403, 4,937,299, 5,017,714, 5,026,798; 5,057,475, 5,120,867, 5,278,1 19, 5,304,614, 5,324,800, 5,350,723, and 5,391,790 each fully incorporated herein by reference For the preparation of isotactic polypropylene the preferred metallocenes are those represented by the formula I in which M is a Group 4, 5, or 6 transition metal, preferably zirconium, X' and X" are the same or different hydride, halogen, preferably CI, hydrocarbyl or alkyl radical having up to about 6 carbon atoms, A' and A " are the same or different asymmetrical hydrocarbyl, preferably a substituted cyclopentadienyl group, even more preferably an indenyl group or substituted indenyl group, and S ' is a linear or cyclic hydrocarbon radical bridge of from one to six atoms Preferably the bridge contains a silicon atom that is disubstituted with alkyl groups Specific examples of these chiral, bridged metallocenes include but are not limited to racemic dimethylsilanediylbis(3-methylcyclopentadienyl) ZrCl 2 , dimethylsilanediylbis(indenyl) ZrCl 2 , dimethylsilanediylbis(4,5,6,7- tetrahydroindenyl) ZrCl 2 , [1, 1 '-(1, l,2,2-tetramethylsilanediyl)bis(3- methylcyclopentadienyl)] ZrCl 2 , [1, 1 ' -(l,l,2,2-tetramethylsilanediyl)bis(4,5,6,7- tetrahydroindenyl) ZrCI 2 , Methods for preparing and using these types of metallocenes are well known. These metallocenes are discussed extensively in United States Patent Nos. 4,769,510; 4,933,403; 5, 120,867; and 5,314,973; each fully incorporated herein by reference. For the preparation of highly isotactic, high molecular weight polypropylene, preferred metallocenes are those represented by the following formula II.: wherein M is a metal of Group 4, 5, or 6 ofthe Periodic Table preferably, zirconium, hafnium and titanium, most preferably zirconium; Ri and R2 are identical or different, are one of a hydrogen atom, a C I -CJO alkyl group, preferably a C1 -C3 alkyl group, a C J-C JO alkoxy group, preferably a C1-C3 alkoxy group, a Cg-Cjo aryl group, preferably a Cg-Cg aryl group, a Cβ- C10 aryloxy group, preferably a Cg-Cg aryloxy group, a C2-C10 alkenyl group, preferably a C2-C4 alkenyl group, a C7-C40 arylalkyl group, preferably a C7-C10 arylalkyl group, a C7-C40 alkylaryl group, preferably a C7-C12 alkylaryl group, a C -C40 arylalkenyl group, preferably a C8-C12 arylalkenyl group, or a halogen atom, preferably chlorine; R3 and R 4 are hydrogen atoms; R5 and R6 are identical or different, preferably identical, are one of a halogen atom, preferably a fluorine, chlorine or bromine atom, a C] -C ] Q alkyl group, preferably a C1-C4 alkyl group, which may be halogenated, a Cg-C j o aryl group, which may be halogenated, preferably a C^-Cg aryl group, a C2-C10 alkenyl group, preferably a C2-C4 alkenyl group, a C7-C40 -arylalkyl group, preferably a C7-C10 arylalkyl group, a C7-C40 alkylaryl group, preferably a C7- C12 alkylaryl group, a C8-C40 arylalkenyl group, preferably a Cg-C^ arylalkenyl group, a -NR2 1 5 , -SR 15 , -OR 1 5 , -OSiR3 1 5 or -PR2 15 radical, wherein R 1 5 is one of a halogen atom, preferably a chlorine atom, a Cj-C]o alkyl group, preferably a C 1-C3 alkyl group, or a C^-C\o aryl group, preferably a Cg-Co aryl group; R 7 is R11 R 11 R 11 R 11 M2 M 2 M 2 M2 (CR 2 13 )- R12 R1 R12 R1 R1 R R1 O M - C . O M2 R12 R12 R 2 -B(R ] 1)-. -A R 1 ')-, -Ge-, -Sn-, -O-, -S-, -SO-, -SO 2 -, -NCR 1 ] )-, -CO-, ^(R 1 -)-, or -P(O)(R π )-; wherein: R 1 !, R 12 and R 1 ^ are identical or different and are a hydrogen atom, a halogen atom, a C1-C20 alkyl group, preferably a C * -C}o alkyl group, a C1-C20 fluoroalkyl group, preferably a C \ -C \ Q fluoroalkyl group, a C6-C30 aryl group, preferably a C6-C20 aryl group, a C6-C30 fluoroaryl group, preferably a Cg-C2o fluoroaryl group, a C-1-C20 alkoxy group, preferably a C1-C10 alkoxy group, a C2-C20 alkenyl group, preferably a C2- 1Q alkenyl group, a C7-C40 arylalkyl group, preferably a C7-C20 arylalkyl group, a Cg-C4o arylalkenyl group, preferably a C -C22 arylalkenyl group, a C7-C40 alkylaryl group, preferably a C7- C20 alkylaryl group or R 1 and R 12 , or R 1 ' and R 1 -^, together with the atoms binding them, can form ring systems; l fi is silicon, germanium or tin, preferably silicon or germanium, most preferably silicon; R8 and R are identical or different and have the meanings stated for R 1 ' ; m and n are identical or different and are zero, 1 or 2, preferably zero or 1 , m plus n being zero, 1 or 2, preferably zero or 1 ; and the radicals R 1 * -* are identical or different and have the meanings stated for R 1 !, R 12 and R 1 -- * . Two adjacent R 1 * ^ radicals can be joined together to form a ring system, preferably a ring system containing from about 4-6 carbon atoms. Alkyl refers to straight or branched chain substituents. Halogen (halogenated) is fluorine, chlorine, bromine or iodine atoms, preferably fluorine or chlorine. Particularly preferred metallocenes are compounds ofthe structures: wherein. M 1 is Zr or Hf, R 1 and R 2 are methyl or chlorine, and R 5 , R 6 R 8 , R 9 ,R 10 , R 1 and R 2 have the above-mentioned meanings. These chiral metallocenes may be used as a racemate for the preparation of highly isotactic polypropylene copolymers. It is also possible to use the pure R or S form. An optically active polymer can be prepared with these pure stereoisomeric forms. Preferably the meso form ofthe metallocene is removed to ensure the center (i.e., the metal atom) provides stereoregular polymerization. Separation ofthe stereoisomers can be accomplished by known literature techniques. For special products it is also possible to use rac/meso mixtures. Generally, the metallocenes are prepared by a multi-step process involving repeated deprotonations/metallations ofthe aromatic ligands and introduction of the bridge and the central atom by their halogen derivatives. The following reaction scheme illustrates this generic approach: H 2 R c + ButylLi > HR c Li X-(CR 8 R 9 ) m -R 7 -(CR 8 R 9 ) n -X -> H 2 R d + ButylLi > HR d Li HR C -(CR 8 R 9 ) m -R 7 -(CR 8 R 9 ) n -R d H 2 Butyl Li > LiR C -(CR 8 R 9 ) m -R 7 -(CR 8 R 9 ) n -R d Li M J Cl4 > Additional methods for preparing metallocenes are fully described in the Journal of Organometallic Chem.. volume 288. (1985), pages 63-67, and in EP-A- 320762, for preparation ofthe metallocenes described, both of which are herein fully incoφorated by reference. Illustrative but non-limiting examples of these metallocenes include: Dimethylsilandiylbis (2-methyl-4-phenyl-l-indenyl)ZrCl2 Dimethylsilandiylbis(2-methyl-4,5-benzoindenyl)ZrCl2; Dimethylsilandiylbis(2-methyl-4,6-diisopropylindenyl)ZrCl2; Dimethylsilandiylbis(2-ethyl-4-phenyl- 1 -indenyl)ZrCl2; Dimethylsilandiylbis (2-ethyl-4-naphthyl- 1 -indenyI)ZrCl2, Phenyl(Methyl)silandiylbis(2-methyl-4-phenyl- 1 -indenyl)ZrCl2, Dimethylsilandiylbis(2-methyl-4-( 1 -naphthyl)- 1 -indenyl)ZrCl2, Dimethylsilandiylbis(2-methyl-4-(2-naphthyl)-l-indenyl)ZrCl2, Dimethylsilandiylbis(2-methyl-indenyl)ZrCl2, Dimethylsilandiylbis(2-methyl-4, 5-diisopropyl- 1 -indenyl)ZrCl2, Dimethylsilandiylbis(2,4,6-trimethyl-l -indenyl)ZrCl2, Phenyl(Methyl)silandiylbis(2-methyl-4,6-diisopropyl-l-indenyl)ZrCl2, 1 ,2-EthandiyIbis(2-methyl-4,6-diisopropyl- 1 -indenyl)ZrCl2, 1 ,2-Butandiylbis(2-methyl-4,6-diisopropyl- 1 -indenyl)ZrCl2, Dimethylsilandiylbis(2-methyl-4-ethyl- 1 -indenyl)ZrCl2, Dimethylsilandiylbis(2-methyl-4-isopropyl- 1 -indenyl)ZrCl2, Dimethylsilandiylbis(2-methyl-4-t-butyl- 1 -indenyl)ZrCl2, Phenyl(Methyl)silandiylbis(2-methyl-4-isopropyl-l-indenyl)ZrCl2, Dimethylsilandiylbis(2-ethyl-4-methyl- 1 -indenyl)ZrCl2, Dimethylsilandiylbis(2,4-dimethyl-l -indeny! ZrCl2, Dimethylsilandiylbis(2-methyl-4-ethyl- 1 -indenyl)ZrCl2, Dimethylsilandiylbis(2-methyl-α-acenaphth- 1 -indenyl)ZrCl2, Phenyl(Methyl)silandiylbis(2-methyl-4,5-benzo-l-indenyl)ZrCl2, Phenyl(Methyl)silandiylbis(2-methyl-4,5-(methyIbenzo)-l-indenyl)ZrCl2, Phenyl(Methyl)silandiylbis(2-methyl-4,5-(tetramethyIbenzo)-l-indenyl)ZrCl2, Phenyl(Methyl)silandiylbis (2-methyl-a-acenaphth- 1 -indenyl)ZrCl2, 1 ,2-Ethandiylbis(2-methyl-4,5-benzo- 1 -indenyl)ZrCl2, l,2-Butandiylbis(2-methyl-4,5-benzo-1-indenyl)ZrCl2, Dimethylsilandiylbis(2-methyl-4, 5-benzo- 1 -indenyl)ZrCl2, l,2-Ethandiylbis(2,4,7-trimethyI-l-indenyl)ZrCl2, Dimethylsilandiylbis(2-methyl- 1 -indenyl)Zrθ2, 1 ,2-Ethandiylbis(2-methyl- 1 -indenyl)ZrCl2, Phenyl(MethyI)silandiylbis(2-methyI- 1 -indenyl)ZrCl2, Diphenylsilandiylbis(2-methyl-l-indenyl)ZrCl2, 1 ,2-Butandiylbis(2-methyl- 1 -indenyl)ZrCl2, Dimethylsilandiylbis(2-ethyl- 1 -indenyl)ZrCl2, Dimethylsilandiylbis(2-methyl-5-isobutyl- 1 -indenyl)ZrCl2, Phenyl(Methyl)silandiylbis(2-methyl-5-isobutyl-l-indenyl)ZrCl2, Dimethylsilandiylbis(2-methyl-5-t-butyl-l-indenyl)ZrCl2, Dimethylsilandiylbis(2,5,6-trimethyl-l-indenyl)ZrCl2, and the like. These preferred metallocene catalyst components are described in detail in U.S. Patent Nos. 5,145,819; 5,243,001 ; 5,239,022; 5,329,033; 5,296,434; 5,276,208; and 5,374,752; and EP 549 900 and 576 970 all of which are herein fully incorporated by reference. Activators Metallocenes are generally used in combination with some form of activator in order to create an active catalyst system. The term "activator" is defined herein to be any compound or component capable of enhancing the ability of one or more metallocenes to polymerize olefins to polyolefins. Alklyalumoxanes are preferably used as activators, most preferably methylalumoxane (MAO). Generally alkylalumoxanes contain about 5 to 40 ofthe repeating units: R R ( Al O-)x — A1R 2 for linear species and Al O-)x - for cyclic species where R is a C]-Cg alkyl including mixed alkyls. Particularly preferred are the compounds in which R is methyl. Alumoxane solutions, particularly methylalumoxane solutions, may be obtained from commercial vendors as solutions having various concentrations. There are a variety of methods for preparing alumoxane, non-limiting examples of which are described in U.S. Patent No. 4,665,208, 4,952,540, 5,091,352, 5,206,199, 5,204,419, 4,874,734, 4,924,018, 4,908,463, 4,968,827, 5,308,815, 5,329,032, 5,248,801, 5,235,081, 5,157,137, 5,103,031 and EP-A-0 561 476, EP-B1-0 279 586, EP-A-0 594-218 and WO 94/10180, each fully incoφorated herein by reference. Some MAO solutions tend to become cloudy and gelatinous over time. It may be advantageous to clarify such solutions prior to use. A number of methods are used to create gel-free MAO solutions or to remove gels from the solutions. Gelled solutions are often simply filtered or decanted to separate the gels from the clear MAO. U.S. Patent No. 5, 157, 137 discloses a process for forming clear, gel- free solutions of alkylalumoxane by treating a solution of alkylalumoxane with an anhydrous salt and/or hydride of an alkali or alkaline earth metal. It is also within the scope of this invention to use ionizing activators, neutral or ionic, or compounds such as tri(n-butyl)ammonium tetrakis(pentaflurophenyl)boron, which ionize the neutral metallocene compound. Such ionizing compounds may contain an active proton, or some other cation associated with but not coordinated or only loosely coordinated to the remaining ion ofthe ionizing compound. Combinations of activators are also contemplated by the invention, for example, alumoxane and ionizing activators in combinations, see for example, WO 94/07928. Descriptions of ionic catalysts for coordination polymerization comprised of metallocene cations activated by non-coordinating anions appear in the early work in EP-A-0 277 003, EP-A-0 277 004 and US patent 5, 198,401 and WO-A- 92/00333 (incoφorated herein by reference). These teach a preferred method of preparation wherein metallocenes (bisCp and monoCp) are protonated by an anion precursor such that an alkyl/hydride group is abstracted from a transition metal to make it both cationic and charge-balanced by the non-coordinating anion. The term "noncoordinating anion" means an anion which either does not coordinate to said cation or which is only weakly coordinated to said cation thereby remaining sufficiently labile to be displaced by a neutral Lewis base. "Compatible" noncoordinating anions are those which are not degraded to neutrality when the initially formed complex decomposes. Further, the anion will not transfer an anionic substituent or fragment to the cation so as to cause it to form a neutral four coordinate metallocene compound and a neutral by-product from the anion. Noncoordinating anions useful in accordance with this invention are those which are compatible, stabilize the metallocene cation in the sense of balancing its ionic charge in a +1 state, yet retain sufficient lability to permit displacement by an ethylenically or acetylenically unsaturated monomer during polymerization. The use of ionizing ionic compounds not containing an active proton but capable of producing both the active metallocene cation and an noncoordinating anion is also known. See, EP-A-0 426 637 and EP-A- 0 573 403 (incoφorated herein by reference). An additional method of making the ionic catalysts uses ionizing anion pre-cursors which are initially neutral Lewis acids but form the cation and anion upon ionizing reaction with the metallocene compounds, for example the use of tris(pentafluorophenyl) boron. See EP-A-0 520 732 (incoφorated herein by reference). Ionic catalysts for addition polymerization can also be prepared by oxidation ofthe metal centers of transition metal compounds by anion pre-cursors containing metallic oxidizing groups along with the anion groups, see EP-A-0 495 375 (incoφorated herein by reference). Where the metal ligands include halogen moieties (for example, bis- cyclopentadienyl zirconium dichloride) which are not capable of ionizing abstraction under standard conditions, they can be converted via known alkylation reactions with organometallic compounds such as lithium or aluminum hydrides or alkyls, aikylalumoxanes, Grignard reagents, etc. See EP-A-0 500 944 and EP-A 1-0 570 982 (incoφorated herein by reference) for /// situ processes describing the reaction of alkyl aluminum compounds with dihalo-substituted metallocene compounds prior to or with the addition of activating anionic compounds. Methods of supporting ionic catalysts comprising metallocene cations and noncoordinating anions are described in WO91/09882, WO 94/03506 and in co- pending U.S. Ser. No. 08/248,284, filed August 3 1994 (incoφorated herein by reference). The methods generally comprise either physical adsoφtion on traditional polymeric or inorganic supports that have been largely dehydrated and dehydroxylated, or using neutral anion precursors that are sufficiently strong Lewis acids to activate retained hydroxy groups in silica containing inorganic oxide supports such that the Lewis acid becomes covalently bound and the hydrogen of the hydroxy group is available to protonate the metallocene compounds. Support Materials The catalyst systems of this invention are fixed on a support material Likewise, the method of this invention involves depositing metallocenes (with or without activator) on support material For puφoses of this patent specification the term "support" is defined as any material upon which metallocenes and/or activators may be fixed Preferably, the support material is a porous paniculate material, such as talc, inorganic oxides, inorganic chlorides and resinous materials such as polyolefin or polymeric compounds Such materials are generally commercially available The preferred support materials are porous inorganic oxide materials, which include those from the Periodic Table of Elements of Groups 2, 3, 4, 5, 13 or 14 metal oxides. Silica, alumina, silica-alumina, and mixtures thereof are most preferred. Other inorganic oxides that may be employed either alone or in combination with the silica, alumina or silica-alumina, are magnesia, titania, zirconia, and the like Preferably the support material is porous silica which has a surface area in the range of from about 10 to about 700 m 2 /g, a total pore volume in the range of from about 0 1 to about 4 0 cc/g and an average particle size in the range of from about 10 to about 500 μm More preferably, the surface area is in the range of from about 50 to about 500 m 2 /g, the pore volume is in the range of from about 0.5 to about 3.5 cc/g and the average particle size is in the range of from about 20 to about 200 μm. Most preferably the surface area is in the range of from about 100 to about 400 m 2 /g, the pore volume is in the range of from about 0 8 to about 3 0 cc/g and the average particle size is in the range of from about 30 to about 100 μm The average pore size of typical porous support materials is in the range of from about 10 to about lOOOA. Preferably, a support material is used that has an average pore size of from about 50 to about 500 A, and most preferably from about 75 to about 350 A. Methods of Making the Catalysts We have found that catalyst components can be selectively positioned on support material particles in order to alter the catalytic behavior ofthe catalyst system thereby polymerizing olefins in a predetermined manner. In very general terms, this method involves the fixing of a catalyst component such as a metallocene on a particular portion of a support material particle. The fixing ofthe catalyst component(s) may be either chemical or physical. Silica, for example, commonly has hydroxyl groups on its surface. These hydroxyl groups, however, can react with metallocenes and/or activators thereby immobilizing or fixing the molecules. An excess of hydroxyl groups may also deactivate these components. Heat or chemical treatment may be used to dehydrate the silica or otherwise remove or neutralize hydroxyl groups. Generally the use of temperatures of from about 100° C to about 1000°C for about 1 to about 24 hours substantially reduces surface hydroxyl groups. Preferably a temperature of from about 300°C to about 800°C is used for up to 24 hours or until about a 3% or less, more preferably a 1% or less, loss on ignition value is obtained. Chemicals such as chlorosilanes, may also be used to dehydrate silica. The loss on ignition value is determined by exposing an amount ofthe dried support material to 1000°C for 20 hours and dividing the weight lost by the weight ofthe support before this treatment and multiplying by 100. If a non-porous support material is used, the catalyst component(s) can be layered on the surface ofthe support particle by first exposing the support material to one component then exposing the support material to another component. If the fixation is physical in nature, then it will likely be necessary to dry the support material between component applications. If the fixation is chemical in nature, then drying may be unnecessary. For example, the metallocene/activator product may react with the hydroxyl groups on the silica surface and become thereby chemically fixed on and/or in the silica. When porous support materials are used, the volume of catalyst component solution may become critical, particularly when the catalyst component is fixed on and/or in the support physically as opposed to chemically. For example, in order to concentrate metallocene on the interior ofthe support particles and activator on the exterior of support particles, the following method may be employed. Porous, dehydrated silica is mixed with a volume of metallocene dissolved in toluene. The volume of metallocene is less than 1.5 times the total pore volume ofthe silica so that the silica either appears dry or slightly damp. In this way, most, if not all, of the metallocene solution is pulled into the pores ofthe silica via capillary forces. Since capillary forces increase with decreasing pore radius, the narrowest pores are filled first. Next, the silica is dried thoroughly using heat and/or vacuum to remove most or all ofthe toluene from the pores ofthe silica. Finally, a MAO solution is applied to the silica. Again, it is preferable to expose the silica to as little solvent as possible in order to avoid causing the metallocene to migrate out ofthe silica pores. Again, the silica should be dried to remove the MAO solvent. The MAO also fills the pores from smallest to largest so that the resulting supported catalyst system has a distribution of active sites due to the distribution of activator and metallocene ratios. There are many possible variations on the theme described above. For example, the silica or other support material may first be exposed to a first metallocene, dried, then exposed to a second, different metallocene. Alternatively, the support material may be exposed to a first metallocene, dried, exposed to a second, different metallocene, then dried an exposed to a third or first metallocene again. Each of these exposures may include more than one metallocene. For instance, the support material may be exposed to a first metallocene, dried, then exposed to a mixture ofthe first and a second, different metallocene. In each of the above cases the support material may be pretreated with activator, treated with activator between treatments with metallocene and/or treated with activator after treatment with metallocene. The activator may be mixed with the first metallocene, the second metallocene, or both the first and second metallocenes. As used herein one metallocene is "different" from another if its chemical formula is not exactly the same. The first and second metallocenes may not even be "different" as defined above but be in solution at differing concentrations so that a gradient of metallocene and/or activator concentration is created on and/or in the support particle. For example, the first metallocene applied to the support is highly concentrated or activated, the support is dried, and the second metallocene application consists ofthe same metallocene compound as the first but in a less concentrated solution such that the final catalyst particle has a higher concentration of active sites on the interior ofthe support particle as compared to the exterior of the support particle. Such a catalyst system might be expected to become more active as polymerization proceeds. In another embodiment, porous support material is treated with a solution that is not a solvent for the metallocene and/or activator. The amount of solution is less than the total pore volume ofthe support. After this treatment, the support is not dried but is treated with a first metallocene and/or activator optionally followed by treatment with a second metallocene and/or activator. The effect of the first treatment with the solution that is not a solvent for the metallocene and/or activator is to force the metallocene and/or activator to deposit in the larger pores and/or closer to the surface ofthe support particle. The effect of this treatment would be to create polyolefin particles that are hollow to some extent. In the context of preparing isotactic polypropylene, we have found that polypropylene having a broad tacticity distribution may be prepared by using two or more metallocenes that when used alone produce isotactic polypropylene having differing isotacticities. If the two metallocenes are mixed together with MAO and their reaction product applied to silica support, the polymer product may be sticky due to the presence of less isotactic polypropylene on the surface ofthe resulting polymer particle. These sticky particles agglomerate and form unmanageable chunks. We have discovered that this problem is alleviated by placing the metallocene which produces the less isotactic polypropylene ("metallocene A") on the interior ofthe silica particle and layering the metallocene which produces highly isotactic polypropylene ("metallocene B") over metallocene A. This causes the less isotactic, sticky polypropylene to primarily form in the interior ofthe polymer particle. The exterior ofthe particle is less sticky and the particles remain separated. This is the first example of "engineering" a supported catalyst in order to effect a polymer modification. Alternatively, two or more metallocene Bs may be selected, particularly those which produce polymer having similar melt flow rate but different melting points. The selection of metallocenes is based on many factors. To make polypropylene suitable for use in nonwoven fabric applications, the metallocenes should have high activity, be non-fouling, produce isotactic or highly isotactic polypropylene having high molecular weight and low extractables, a melt flow rate in the range of from about 5 to about 30 dg/min, preferably from about 10 to about 20 dg/min. The molecular weight distribution may be broad or narrow depending upon the particular properties desired. As used herein "isotactic polypropylene" means having at least 30% istotactic pentads according to analysis by ,3 C-NMR or copolymers of propylene and one or more comonomers of ethylene, aliphatic or alicyclic C -C 2 o alpha-olefin, or C -Gto l,n-dienes, wherein the comonomers are present in up to 40 mole%. As used herein "highly isotactic polypropylene" means having at least 50% istotactic pentads according to analysis by 13 C-NMR or copolymers of propylene and one or more comonomers of ethylene, aliphatic or alicyclic C -C 2 o alpha-olefin, or C -C 4 o l,n-dienes, wherein the comonomers are present in up to 40 mole%. In general, metallocenes represented by formula I above will produce isotactic polypropylene having suitable molecular weight. In general, metallocenes represented by the formula II above, particularly formulas A and B, will produce highly isotactic polypropylene having high molecular weight. Of these metallocenes, ("metallocene B"), the following are particularly preferred for making highly isotactic polypropylene: rac- dimethylsilanediylbis(2,4-dimethylindenyl)ZrCl 2 , rac-dimethylsilanediylbis(2,4- dimethyl-4-phenylindenyl)ZrCl 2 , rac- dimethylsilanediylbis(2-methyIindenyl)ZrCI 2 , rac-dimethylsilanediylbis(2-methyl-4,5-benzoindenyl)ZrCl 2 , and rac- dimethylsilanediylbis(2-methyl-4,6-diisopropylindenyl)ZrCl 2 . The preferred method for preparing a supported metallocene catalyst suitable for polymerizing polypropylene having a broad tacticity distribution involves the following steps: (a) combining support material and a first solution comprising a first metallocene; then (b) drying the mixture thereby forming supported first metallocene; then (c, combining the supported first metallocene with a second solution comprising a second metallocene wherein the second metallocene is different from the first; then (d) drying the resulting mixture. The activator can be introduced at any point. Any support material may be used, however, preferably the support material is porous, at least partially dehydrated silica. It may be particularly desirable to dehydrate the silica at a temperature of from about 100°C to about 800°C anywhere from about 1 hour to about 24 hours. Any metallocene (or combination of metallocenes and activator(s)) may be used, however, preferably the first solution is a solution of metallocene A or B and the second is a solution of metallocene B and an activator, preferably MAO. The selection of specific metallocenes and activators will depend on the ultimate polymer attributes and product performance desired. Generally B metallocenes produce higher molecular weight, higher tacticity polypropylene compared to A metallocenes. There is enough variation within the B metallocene group to provide many polymer and application attribute variations. Preferably, the volumes of both the first and second solutions is less than about 4.0 times the total pore volume ofthe silica, more preferably less than about 3.0 times the total pore volume ofthe silica, even more preferably less than about 2.5 times the total pore volume ofthe silica, even more preferably less than about 2.0 times the total pore volume ofthe silica, and most preferably less than about 1.5 times the total pore volume ofthe silica. The procedure for measuring the total pore volume of a porous support or catalyst system is well known in the art. Details of one of these procedures is discussed in Volume 1, Experimental Methods in Catalytic Research (Academic Press, 1968) (specifically see pages 67-96). This preferred procedure involves the use of a classical BET apparatus for nitrogen absoφtion. Another method well know in the art is described in Innes, Total porosity and Particle Density of Fluid Catalysts By Liquid Titration, Vol. 28, No. 3, Analytical Chemistry 332-334 (March, 1956). When the volume of solution combined with the silica is less than one times the total pore volume ofthe silica, the silica appears completely dry and free- flowing and is consequently easy to mix and transfer. When volumes above one times the total pore volume ofthe porous silica are used, the silica becomes progressively more difficult to mix and transfer as volume increases because it has the consistency of damp or wet mud. At greater volumes of solution a slurry is eventually formed such that one can observe separation ofthe solution and silica as the silica settles. At the slurry stage, the silica is easier to mix and handle. These factors should be considered when choosing solution volumes. Regardless ofthe amount of solution used, it is preferable to combine the silica and solution such that the solution is evenly distributed among the silica particles. Thus it is preferable to add the solution to the silica slowly either as a spray or drop-wise while the silica is mixed. Any compatible solvent may be used to form the metallocene solutions. Non-limiting examples of solvents are aliphatic, aromatic and saturated hydrocarbons, and cyclic hydrocarbons such as isopentane, heptane, toluene and the like. The more preferred solvents are the cyclic aliphatic and aromatic hydrocarbons such as toluene. Preferably the first solution contains metallocene A or B and MAO, preferably A without MAO such that the concentration of A is from about 1.0 to about 0.001 mmol metallocene metal g support material, more preferably in the range of from about 0.5 to about 0.005 mmol metallocene metal/g support material, and most preferably in the range of from about 0.1 to about 1.01 mmol metallocene/g support material. Preferably the second solution contains metallocene B and MAO such that the ratio of Al to metallocene metal is in the range of from about 500: 1 to 50:1, preferably from about 300: 1 to about 100: 1. Preferably the ratio of metallocene A to metallocene B in the final catalyst system is from about 10:90 to about 70:30, even more preferably from about 20:80 to about 60:40, more preferably from about 30:70 to about 60:40, and most preferably from about 40:60 to about 50:50. Preferably the final mole ratio ofthe aluminum ofthe alumoxane component to the transition metal ofthe metallocene component(s) applied to the support is in the range of ratios between about 12: 1 to about 800: : 1, preferably 20: 1 to less than 500: 1, and most preferably 50: 1 to less than 400: 1. The above presumes that the metallocene activities are similar. If the metallocene activities are considerably different, then this difference should be taken into account when determining how much of each to use. The silica is dried after application of the first solution and after application ofthe second solution. Preferably the silica is dried until residual solvent trapped in the pores ofthe carrier is removed. This results in a free-flowing supported catalyst. Preferably greater than about 90% of all the solvent is removed from the supported catalyst system upon drying, even more preferably about 100% ofthe solvent is removed from the pores ofthe support material. Heat and/or vacuum may be used to dry the catalyst. Typically vacuum in the range of from about 0 to about .7 atm and temperature in the range of from about 25°C to about 100°C is used for a time period ranging from about 4 to about 36 hours. It may be advantageous to dry the catalyst at ambient temperature without vacuum or with a flow of warm inert gas such as nitrogen to avoid problems associated with migration of catalyst components from their designated positions. The catalyst systems of this invention may be used directly in polymerization or the catalyst system may be prepolymerized using methods well known in the art. For details regarding prepolymerization, see United States Patent No s 4,923,833 and 4,921,825, EP 0 279 863 and EP 0 354 893 each of which is fully incoφorated herein by reference. The catalyst systems of this invention may also be combined with one or more additives such as scavengers. Examples of suitable scavenging compounds include triethylaluminum (TEAL), trimethylaluminum (TMAL), tri-isobutylaluminum (TIBAL), tri-n-hexylaluminuim (TNHAL) and the like. The amount of scavenging agent used depends upon the type used as well as the process conditions. Generally, for a scavenging agent such as TEAL, 1-500 ppm may be used, preferably, 2-100 ppm, more preferably 5-25 ppm. Polymerization Processes The catalyst system of this invention may be used in the polymerization of any monomer and optionally comonomers in any process including gas, slurry or solution phase or high pressure autoclave processes. (As used herein, unless differentiated, "polymerization" includes copolymerization and "monomer" includes comonomer.) Preferably, a gas or slurry phase process is used, most preferably a bulk liquid propylene polymerization process is used. In the preferred embodiment, this invention is directed toward the bulk liquid polymerization and copolymerization of propylene or ethylene, particularly propylene, in a slurry or gas phase polymerization process, particularly a slurry polymerization process. Another embodiment involves copolymerization reactions of propylene or ethylene, particularly propylene, with one or more ofthe alpha- olefin monomers having from 4 to 20 carbon atoms, preferably 4-12 carbon atoms, for example alpha-olefin comonomers of ethylene, butene- 1, pentene-1, 4- methylpentene-1, hexene-1, octene-1, decene-1, and cyclic olefins such as styrene, cyclopentene or norbornene. Other suitable monomers include polar vinyl, diolefins such as dienes, for example, 1,3 -butadiene, 1 ,4-hexadiene, norbornadiene or vinylnorbornene, acetylene and aldehyde monomers. In another embodiment ethylene or propylene is polymerized with at least two different comonomers to form a teφolymer and the like, the preferred comonomers are a combination of alpha-olefin monomers having 3 to 10 carbon atoms, more preferably 3 to 8 carbon atoms, and/or dienes having 4 to 10 carbon atoms. Typically in a gas phase polymerization process a continuous cycle is employed where in one part ofthe cycle of a reactor, a cycling gas stream, otherwise known as a recycle stream or fluidizing medium, is heated in the reactor by the heat of polymerization. The recycle stream usually contains one or more monomers continuously cycled through a fluidized bed in the presence of a catalyst under reactive conditions. This heat is removed in another part ofthe cycle by a cooling system external to the reactor. The recycle stream is withdrawn from the fluidized bed and recycled back into the reactor. Simultaneously, polymer product is withdrawn from the reactor and new or fresh monomer is added to replace the polymerized monomer. (See for example U.S. Patent Nos. 4,543,399; 4,588,790; 5,028,670; 5,352,749; 5,405,922, and 5,436,304 all of which are fully incoφorated herein by reference.) A slurry polymerization process generally uses pressures in the range of about 1 to about 500 atmospheres or even greater and temperatures in the range of -60°C to about 280°C. In a slurry polymerization, a suspension of solid, paniculate polymer is formed in a liquid polymerization medium to which ethylene and comonomers and often hydrogen along with catalyst are added. The liquid employed in the polymerization medium can be, for example, an alkane or a cycloalkane. The medium employed should be liquid under the conditions of polymerization and relatively inert. Non-limiting examples of liquid mediums include hexane and isobutane. The polymers and copolymers made by the process ofthe invention are useful in forming operations such as, for example, film, sheet, and fiber extrusion and co-extrusion as well as blow molding, injection molding, sheet thermoforming and rotational molding. Films include blown or cast films in mono-layer or multilayer constructions formed by coextrusion or by lamination. Such films are useful as shrink film, cling film, stretch film, sealing films, oriented films, snack packaging, heavy duty bags, grocery sacks, baked and frozen food packaging, medical packaging, industrial liners, membranes, etc. in food-contact and non-food contact applications. Fiber forming operations include melt spinning, solution spinning and melt blown fiber operations. Such fibers may be used in woven or nonwoven form to make filters, diaper fabrics, medical garments, geotextiles, etc. Extruded articles include, for example, medical tubing, wire and cable coatings, geomembranes, and pond liners. Molded articles include single and multi-layered constructions in the form of bottles, tanks, large hollow articles, rigid food containers and toys, etc.. The broad tacticity distribution isotactic polypropylenes prepared by the processes of this invention are suitable for nonwoven fabric applications preferably have a weight average molecular weight (MW) that is in the range of from about 50,000 to about 5,000,000, preferably 100,000 to about 1,000,000, more preferably from about 150,000 to about 900,000. These polymers preferably have a melt flow rate (MFR) that is in the range of from about 20 dg/min. to about 60 dg/min., preferably from about 25 dg/min. to about 55 dg/min., even more preferably from about 30 dg/min. to about 50 dg/min., and most preferably from about 30 dg/min. to about 45 dg/min.. These polymers preferably have a composition distribution breadth index (CDBI) that is in the range of from about 25.0 to about 90.0, even more preferably from about 30.0 to about 85.0, even more preferably from about 35.0 to about 80.0, and most preferably from about 35.0 to about 75.0. The percent solubles of these polymers is less than about 20.0, preferably less than about 15, even more preferably less than about 10, and most preferably less than about 10. The melting point of these polymers is preferably in the range of from about 125.0°C to about 200°C, preferably from about 130°C to about 180°C, and most preferably from about 130°C to about 175°C. Nonwoven Fabrics The broad tacticity distribution polymers described above are particularly useful for the production of spunbond and melt blown nonwoven fabrics. The spunbonding process is well known in the art. Generally it involves the extrusion of fibers through a spinneret. These fibers are then drawn using high velocity air and laid on an endless belt. A calandar roll is then used to heat the web and bond the fibers to one another. The melt blowing process is also well known in the art. For more information see WO 94/28219 published December 8, 1994 herein fully incoφorated by reference. When nonwoven fabrics are prepared using the broad tacticity distribution polymer described above, the manufacturer can use increased line speed while making finer and stronger fibers with higher birefringence compared to fibers made using conventional polymers. The resulting fabrics are not only stronger but have lower oil and wax content, higher filtration efficiency, and are softer than fabrics made using conventional polymers. The broadened tacticity distribution allows the fibers to be heated and bonded to one another more efficiently and quickly than fibers made with polymer having a narrow tacticity distribution. EXAMPLES MFR is measured by the method of ASTM-1238 condition L. CDBI and percent solubles are determined by Temperature Rising Elution Fractionation (TREF) as described in Wild, et al., J. Poly. Sci. Ed., Vol. 20, p. 441, (1982). Average Particle Size (APS) is the mean size ofthe polymer distribution as measured according to ASTM D 1921-87 (Method A). Catalyst Preparations Example 1 In an inert N 2 atmosphere 0.0517 g of dimethylsilanediylbis(4,5,6,7- tetrahydroindenyl)ZrCI 2 (metallocene A) was dissolved in 14.8 g toluene. Separately 8.01 g MS948 silica (Davison Chemical Division of W.R. Grace, Baltimore, MD) (1.5-1.6 cc/g pore volume) previously dehydrated to 200°C in a stream of flowing N 2 was added to a beaker. After stirring for 5 minutes, the metallocene solution was added all at once to the silica. The liquid wetted the silica to form a stiff but stirrable solid. The pore volume loading ofthe silica was 130%. After five minutes of stirring with a spatula, the solid was dried using a rotary evaporator. Over the next 2 hours, vacuum was increased from 25" to 29" of Hg while oil temperature was increased to 35°C. At the end 8.42 g of free flowing solid was obtained. All ofthe solid was transferred to a beaker. Separately, 36.01 g of 30 wt% methylalumoxane solution in toluene (Albemarie Coφoration, Baton Rouge, LA) was added to 0.0686 g of dimethylsilanediyl- bis(2,2-dimethyI-indenyl)zirconium dichloride (metallocene B) followed by 9.78 g toluene to form the precursor. The metallocene dissolved immediately upon addition ofthe MAO. After stirring for 5 minutes the precursor was added all at once to the solid obtained above. The liquid precursor wetted the silica to form a stiff but stirrable solid. The pore volume loading ofthe silica was about 160%. After five minutes of stirring with a spatula, the solid was dried using a rotary evaporator. Over the next 4 hours, vacuum was increased from 25" to 29" inches of Hg while oil temperature was increased from 25°C to 35°C. After drying, 11.5 g of free flowing solid was obtained. Analysis showed a loading of 8.94 wt % Al and 0.20 wt % Zr with an Al/Zr molar ratio of 152. Comparative Example 2 In an inert N 2 atmosphere 3.5 g of 30 wt % methylalumoxane solution in toluene was added to 0.042 g dimethylsilanediylbis(4,5,6,7,- tetrahydroindenyl)ZrCl 2 (metallocene A) followed by 4 0 g toluene to form the precursor. The metallocene dissolved immediately upon addition ofthe methylalumoxane. Separately, 4.0 g MS 948 silica previously dehydrated to 600°C in a stream of flowing N 2 was added to a beaker. After stirring for 5 minutes the precursor was added all at once to the silica. The liquid precursor wetted the silica to form a stiff but stirrable solid. The pore volume loading ofthe silica was 125% After five minutes of stirring with a spatula, the solid was dried as described in Example 1. After drying 5.06 g of free flowing solid was obtained. Analysis showed a loading of 8.92 wt % Al and 0.15 wt % Zr with an Al/Zr molar ratio of 203. Comparative Example 3 In an inert N 2 atmosphere 3.5 g of 30 wt % methylalumoxane solution in toluene was added to 0.05 g dimethyIsilanediylbis(2,2-dimethyI-indenyl)ZrCI 2 (metallocene B) followed by 4.0 g toluene to form the precursor. The metallocene dissolved immediately upon addition ofthe methylalumoxane. Separately, 4.0 g MS948 silica previously dehydrated to 600°C in a stream of flowing N 2 was added to a beaker. After stirring for 5 minutes, the precursor was added all at once to the silica. The liquid precursor wetted the silica to form a stiff but stirrable solid. The pore volume loading ofthe silica was 125%. After five minutes of stirring with a spatula, the solid was dried as described in Example 1. After drying 5.0 g of free flowing solid was obtained. Analysis showed a loading of 8.8 wt % Al and 0.19 wt % Zr with an Al/Zr molar ratio of 158. Example 4 In an inert N 2 atmosphere 0.0529 g of dimethylsilanediylbis(4,5,6,7- tetrahydroindenyl)ZrCl2 (metallocene A) was dissolved in 14.6 g toluene. Separately 8.01 g MS948 silica previously dehydrated to 600°C in a stream of flowing N 2 was added to a beaker. After stirring for 5 minutes, the metallocene solution was added all at once to the silica. The liquid wetted the silica to form a stiff but stirrable solid. The pore volume loading ofthe silica was 130%. After five minutes of stirring with a spatula, the solid was dried as in Example 1. At the end 10.1 g of free flowing solid was obtained. All ofthe solid was transferred to a beaker. Separately, 36.12 g of 30 wt% methylalumoxane solution in toluene was added to 0.070 g of dimethylsilanediylbis(2,2-dimethyl-indenyl)zirconium dichloride (metallocene B) followed by 6.0 g toluene to form the precursor. The metallocene dissolved immediately upon addition ofthe MAO. After stirring for 5 minutes, the precursor was added all at once to the solid obtained above. The liquid precursor wetted the silica to form a stiff but stirrable solid. The pore volume loading ofthe silica was about 160%. After five minutes of stirring with a spatula, the solid was dried as in Example 1. After drying, 10.23 g of free flowing solid was obtained. Analysis showed a loading of 9.03 wt % Al and 0.24 wt % Zr with an Al/Zr molar ratio of 128. Example 5 In an inert N 2 atmosphere 5.154 g of 30 wt % methylalumoxane solution in toluene was added to 0.0248 g dimethylsilanediylbis(2,2-dimethyI-indenyl)ZrCl 2 (metallocene B) and 0.0224 g of dimethylsilanediylbis(4,5,6,7- tetrahydroindenyI)ZrCl 2 (metallocene A) followed by 2.28 g toluene to form the precursor. The metallocene dissolved immediately upon addition ofthe methylalumoxane. Separately, 4.0 g MS948 silica previously dehydrated to 600°C in a stream of flowing N 2 was added to a beaker. After stirring for 5 minutes, the precursor was added all at once to the silica. The liquid precursor wetted the silica to form a stiff but stirrable solid. The pore volume loading ofthe silica was 126%. After five minutes of stirring with a spatula, the solid was dried as described in Example 1. After drying 5.412 g of free flowing solid was obtained. Analysis showed a loading of 11.7 wt % Al and 0.19 wt % Zr with an Al/Zr molar ratio of 210. Example 6 In an inert N 2 atmosphere 2.054 g of 30 wt % methylalumoxane solution in toluene was added to 0.0518 g of dimethylsilanediylbis(4, 5,6,7- tetrahydroindenyl)ZrCl 2 (metallocene A) followed by 12.14 g toluene. Separately 8.015 g MS948 silica previously dehydrated to 600°C in a stream of flowing N 2 was added to a beaker. After stirring for 5 minutes, the metallocene solution was added all at once to the silica. The liquid wetted the silica to form a stiff but stirrable solid. The pore volume loading ofthe silica was 125%. After five minutes of stirring with a spatula, the solid was dried as in Example 1. All ofthe solid was transferred to a beaker. Separately, 5.517 g of 30 wt% methylalumoxane solution in toluene was added to 0.068 g of dimethylsilanediylbis(2,2-dimethyl- indenyl)zirconium dichloride (metallocene B) followed by 6.18 g toluene to form the precursor. The metallocene dissolved immediately upon addition ofthe MAO. After stirring for 5 minutes, the precursor was added all at once to the solid obtained above. The liquid precursor wetted the silica to form a stiff but stirrable solid. The pore volume loading ofthe silica was about 125%. After five minutes of stirring with a spatula, the solid was dried as in Example 1. After drying, 10.57 g of free flowing solid was obtained. Analysis showed a loading of 8.61 wt % Al and 0.19 wt % Zr with an Al Zr molar ratio of 154. Catalyst Polymerization Evaluation A 2 liter autoclave reactor previously flushed with N2 and containing triethylaluminum (0.25 ml of a 1 M solution in hexane) and 100 ml of propylene was heated to a temperature of 70°C. A 75 mg sample ofthe free flowing solid prepared above was slurried in 2 ml of hexane and charged with 250 ml of propylene to start the reaction. After one hour, the reactor was cooled, vented, purged with N2 for 20 minutes and then opened. The polypropylene was transferred to a ceramic dish and allowed to dry in a fume hood overnight. The next day, the polymer was further dried in vacuo at 75°C for one hour. The final dried polymer was weighed. Polymerization Results Table I summarizes catalyst testing under polymerization conditions described above. See the particular catalyst examples for preparation detail. The Comparative Example 2 catalyst having metallocene A + MAO on silica fouled the reactor and produced large hard clumps of polymer granules. The fouling and poor moφhology were caused by the partial softening and/or partial solubility of the polymer in propylene liquid at the reactor temperature. The result was due to the less than adequate tacticity ofthe polypropylene formed. The Comparative Example 3 catalyst having metallocene B + MAO on silica showed high activity and produced free flowing polymer granules which did not foul the reactor. The absence of fouling and good polymer moφhology are due to the highly isotactic polypropylene formed. The Example 1 catalyst prepared by contacting the 200°C dehydrated silica with metallocene A then drying and contacting with metallocene B + MAO showed good activity and produced free flowing polymer granules which did not foul the reactor. The small average particle size ofthe polymer granules indicates the absence of agglomerated particles. A longer run showed that the high activity was sustained over an extended period with no deterioration in particle size, moφhology or reactor cleanliness. The Example 4 catalyst is similar to Example 1 except that 600°C silica was used for the metallocene A contacting. Good activity, good moφhology, and an absence of reactor fouling were observed. The Example 5 catalyst was prepared by contacting the silica with metallocene A and part ofthe MAO followed by drying and contacting with metallocene B and the remainder ofthe MAO. The catalyst showed high activity and no reactor fouling but the average particle size ofthe polymer was higher due to agglomeration of some ofthe polymer granules The comparative Example 6 catalyst was prepared by contacting the silica with a toluene solution containing all of metallocene A, metallocene B and the MAO. The catalyst showed high activity and no reactor fouling but the average particle size ofthe polymer was higher due to agglomeration of some ofthe polymer granules. This result showed that agglomeration was not controlled by diluting metallocene A polymer with metallocene B polymer. The polymerization results of 1 and 4 show that when the lower tacticity polymer producing metallocene A is anchored to the silica, reactor fouling and/or polymer agglomeration is controlled. This capability depends on the amount of interaction between metallocene A and the silica surface. Polymer Property Results Polymer property data are shown in Table II. The lower and higher melting points ofthe comparative Example 2 and 3 polymers are the direct result ofthe difference in polymer tacticities (lower for metallocene A and higher for metallocene B). Similarly, the broader and narrower melting ranges are the result of differences in tacticity and molecular weight (as indicated by the MFRs). The polymers are further characterized by temperature rising elution fractionation chromatography. CDBI is a measure ofthe polymer composition distribution, the higher the number, the more the polymer chains resemble one another. Percent solubles is a measure of two polymer properties. As the amount of low molecular weight material and low tacticity molecules increases so does the percent solubles. Polymer from metallocene A has the broader composition distribution and higher percent solubles. The broad tacticity distributions for the mixed metallocene polymers are apparent from their broad melting ranges and multiple melting points. Composition distributions are broader than the metallocene B polymers as evidenced by the lower CDBI values. Percent solubles are lower than metallocene A polymers. Note that catalyst examples 1 and 4 produced lower solubles, broad tacticity, free flowing, non-agglomerated polymers. Table 1 (fl C 01 W H H C H m en x m m -i * ******* * 32 C r m ro (a) A = dimethylsilanediylbis(4,5,6,7-tetrahydroindenyl)zircoπium dichloride B = dimethylsilanediylbis(2,2-dimethyl-indenyl)zirconium dichloride C = methylalumoxane (MAO) (b) Grams polymer per gram catalyst per hour for one hour polymerization unless otherwise noted. (c) see experimental section (d) on 200°C silica (e) 2 hour polymerization run Grams polymer per gram catalyst per hour for two hour polymerization (/) Table ff C CD 0) H H C H m V) x m m H 3 c r m ro O) (a) DSC second melt (b) DSC second melt (c) from temperature rising elution fractionation (TREF) calibrated versus "CNMR. 10 (d) ibid (c) While the present invention has been described and illustrated by reference to particular embodiments, it will be appreciated by those of ordinary skill in the art that the invention lends itself to many different variations not illustrated herein. For these reasons, then, reference should be made solely to the appended claims for purposes of determining the true scope ofthe present invention. Although the appendant claims have single appendencies in accordance with U.S. patent practice, each ofthe features in any ofthe appendant claims can be combined with each ofthe features of other appendant claims or the main claim.

Claims: Claims We claim: 1. A method for preparing a supported metallocene catalyst, said method comprising the steps of: (a) combining support material and a first solution comprising a first metallocene; then (b) drying the mixture thereby forming supported first metallocene; then (c) combining the supported first metallocene with a second solution comprising a second metallocene wherein the second metallocene is different from the first; then (d) drying the resulting mixture. 2. The method of claim 1 wherein the support material is porous. 3. The method of claims 1 or 2 wherein the volume of the first solution and/or the second solution is less than 3 times the total pore volume ofthe porous support. 4. The method of any ofthe preceding claims wherein the volume ofthe first solution and/or the second solution is less than 2 times the total pore volume ofthe porous support. 5. The method of any ofthe preceding claims wherein the first solution and/or second solution comprises metallocene and activator. 6. The method of claim 5 wherein the activator is an alumoxane. 7. The method of any ofthe preceding claims wherein the first metallocene is represented by the formula: wherein M is a Group 4, 5, or 6 transition metal; X ' and X " are the same or different hydride, halogen, hydrocarbyl or alkyl radical having up to about 6 carbon atoms; A' and A " are the same or different asymmetrical substituted cyclopentadienyl or indenyl group; and S' is a linear or cyclic hydrocarbon radical bridge of from one to six atoms. 8. The method of any ofthe preceding claims wherein the second metallocene is represented by the formula. wherein M is selected from the group consisting of titanium, zirconium, hafnium, vanadium niobium, tantalum, chromium, molybdenum and tungsten; Ri and R^ are identical or different, are one of a hydrogen atom, a C \ -C \Q alkyl group, preferably a C1 -C3 alkyl group, a Cj-Cio alkoxy group, a C(,-C \Q aryl group, a Cg-Cio aryloxy group, a C2-C10 alkenyl group, a C2-C4 alkenyl group, a C7-C40 arylalkyl group, a C7-C40 alkylaryl group, a Cg-C4o arylalkenyl group, or a halogen atom; R3 and R^ are hydrogen atoms; R 5 and R are identical or different, and are one of a halogen atom, a C J -C J Q alkyl group which may be halogenated, a Cg-Cjo aryl group which may be halogenated, a C2-C10 alkenyl group, a C7-C40 -arylalkyl group, a C7-C40 alkylaryl group, a C8-C40 arylalkenyl group, a -NR2 15 , -SR 15 , -OR 15 , -OSiR 3 15 or -PR 2 15 radical, wherein R^ 5 is one of a halogen atom, a CJ -C I Q alkyl group, or a Cg-C j o aryl group; R 7 is R 1 1 R11 R11 R11 M2 M2 M2 M2 (CR 2 13 )- R12 R12 R12 R12 R11 R11 R11 M O O M R12 R12 R 2 -B(Rl 1)-, -Al^ 1 ! )-, -Ge-, -Sn-, -O-, -S-, -SO-, -SO 2 -, -N(R ] ] )-, -CO-, -P(Rl 1)-, or -P(O)(R π )-; wherein: RI 1 ^ R12 anc j R! 3 are identical or different and are a hydrogen atom, a halogen atom, a C1-C20 al g rou P> a C1-C20 fluoroalkyl group, a C6-C30 aryl group, a C6-C30 fluoroaryl group, a C1-C20 alkoxy group, a C2-C20 alkenyl group, a C7- C40 arylalkyl group, a C8-C40 arylalkenyl group, a C7-C40 alkylaryl group, or R^ and R Ϊ 2- s or R * and R 1 ^, together with the atoms binding them, can form ring systems; M-2 is silicon, germanium or tin; R8 and R- 3 are identical or different and have the meanings stated for R 1 *; m and n are identical or different and are zero, 1 or 2, m plus n being zero, 1 or 2; and the radicals 1 ^ are identical or different and have the meanings stated for Ri *, Rl2 and R 1 -* and two adjacent R 1 *-" radicals can be joined together to form a ring system. 9. A method for preparing a supported metallocene catalyst, said method comprising the steps of: (a) combining porous support material and a first solution comprising solvent and a first metallocene wherein the volume of first solution is less than about three times the total pore volume ofthe porous support; then (b) drying the mixture thereby forming supported first metallocene; then (c) combining the supported first metallocene with a second solution comprising solvent and a second metallocene wherein the second metallocene is different from the first and wherein the volume of solution is less than about three times the total pore volume ofthe supported first metallocene; then (d) drying the resulting mixture. 10. The method of claims 9 or 10 wherein the volume of first solution and/or second solution is less than about two times the total pore volume ofthe porous support. 1 1. The method of claims 9 or 10 wherein the first solution and/or comprises solvent, metallocene and activator. 12. The method of claims 9 - 1 1 wherein the activator is alumoxane. 13. The method of claims 9 - 12 wherein the first metallocene is represented by the formula: wherein M is a Group 4, 5, or 6 transition metal; X ' and X " are the same or different hydride, halogen, hydrocarbyl or alkyl radical having up to about 6 carbon atoms; A' and A " are the same or different asymmetrical substituted cyclopentadienyl or indenyl group; and S' is a linear or cyclic hydrocarbon radical bridge of from one to six atoms. and/or wherein the second metallocene is represented by the formula: wherein M is selected from the group consisting of titanium, zirconium, hafnium, vanadium niobium, tantalum, chromium, molybdenum and tungsten; R 1 and R 2 are identical or different, are one of a hydrogen atom, a CI-C^Q alkyl group, preferably a C1-C3 alkyl group, a CJ-CJO alkoxy group, a Cg-Cjo aryl group, a Cό-Cio aryloxy group, a C2-C10 alkenyl group, a C2-C4 alkenyl group, a C7-C40 arylalkyl group, a C7-C40 alkylaryl group, a Cg-C4Q arylalkenyl group, or a halogen atom; R3 and R * ^ are hydrogen atoms; R 5 and R^ are identical or different, and are one of a halogen atom, a CI-CJO alkyl group which may be halogenated, a Cg-CjQ aryl group which may be halogenated, a C2-C10 alkenyl group, a C7-C40 -arylalkyl group, a C7-C40 alkylaryl group, a Cg-C 4 o arylalkenyl group, a -NR2 15 , -SR 15 , -OR 15 , -OSiR 3 15 or -PR2 15 radical, wherein R 1 is one of a halogen atom, a Ci-Cjo alkyl group, or a Cg-Cjo aryl group; R 7 is R 11 R11 R11 R11 M . M M2 , M (CR 2 13 ) - R12 R 12 R12 R 12 R11 R 11 R 11 O M 2 O . C . O R12 R 12 R 12 -B(R )-> -AKR 1 ϊ)-, -Ge-, -Sn-, -O-, -S-, -SO-, -SO 2 -, -N(R" -CO-, -P(Rl 1)-, or -P )^ 1 1)-; wherein: R! 1, Rl2 and R 1 - are identical or different and are a hydrogen atom, a halogen atom, a C1-C20 al group, a C1-C20 fluoroalkyl group, a C6-C30 aryl group, a C6-C30 fluoroaryl group, a C1-C20 alkoxy group, a C2-C20 alkenyl group, a C7-C40 arylalkyl group, a C -C4o arylalkenyl group, a C7-C40 alkylaryl group, or Ri and R12, or R 1 ! and R 1 -- 1 , together with the atoms binding them, can form ring systems; 2 is silicon, germanium or tin; R8 and R^ are identical or different and have the meanings stated for R 1; m and n are identical or different and are zero, 1 or 2, m plus n being zero, 1 or 2; and the radicals RlO are identical or different and have the meanings stated for RU, Rl2 and Rl--* and two adjacent R ^ radicals can be joined together to form a ring system. 14. A supported metallocene catalyst system prepared by the method of claim 1. 15. A supported metallocene catalyst system prepared by the method of claim 9. 16. A process for polymerizing olefins. said process comprising the step of combining olefins and the catalyst system of claim 14 under polymerization conditions. 17. A process for polymerizing olefins, said process comprising the step of combining olefins and the catalyst system of claim 15 under polymerization conditions.

Inventors: BRINEN JEFFREY L, MCALPIN JAMES J, SPECA ANTHONY N, BRINEN, JEFFREY, L., MCALPIN, JAMES, J., SPECA, ANTHONY, N.
Applicants: EXXON CHEMICAL PATENTS INC, EXXON CHEMICAL PATENTS INC.
Application year: 1997
Main classification: C08F4
IPC codes: C08F4, C08F10, C08F110, C08L23, D01F6, D04H1, D04H3