Weld wire

Abstract: A metal-core weld wire usable for gas shielded arc welding gapless joints on low carbon and low alloy galvanized and galvanealed steels. The metal-core weld wire includes a low carbon steel sheath surrounding a core composition. In one embodiment, the low carbon steel sheath includes, by total weight of the metal-core weld wire, between approximately 0.01 - 0.03 % C, and the core composition includes, by total weight of the metal-core weld wire, between approximately 0.05 - 0.20 % Ti, between approximately 0.05 - 1.00 % Nb, Fe powder, and Mn to the extent that the metal-core weld wire includes between approximately 0.1 - 1.0 % Mn wherein the metal-core weld wire includes between approximately 0.1 - 1.0 % Si. The core composition is, by total weight of the metal-core weld wire, between approximately 0.001 - 12.0 %. The metal-core weld wire provides, at weld rates up to 150 cm/min, reduced arc ionization potential and spatter, and improved arc stability and shielding. The metal-core weld wire produces, at weld rates up to 150 cm/min, weld deposits having reduced blow holes and porosity, no liquid metal embrittlement, and reduced weld pool surface tension resulting in an improved wetting characteristic.

Description: The invention relates generally to metal-cored weld wires, and more specifically to metal-core weld wires usable for gas shielded arc welding low carbon and low alloy galvanized and galvanealed steels at relatively high weld rates to produce improved weld deposits on overlapping or butted workpieces with no gap therebetween. In many gas shielded arc welding applications, low carbon and low alloy galvanized and galvanealed steels are welded in single pass, high weld rate operations that require weld deposits on gapless joints with minimum hot cracking, minimum blow hole formation and substantially no porosity, minimum slag formation and spatter, good wetting characteristic and corrosion resistance, no liquid metal embrittlement, improved impact strength, and a minimum tensile strength of approximately 585 MPa (85,000 psi). Galvanized steels are formed by coating or depositing zinc on steel in a hot dipping, a sheradizing, or an electroplating process. The galvanized metal is sometimes annealed to form a galvanealed metal with improved properties including reduced flaking of the coating, which tends to occur during metal forming operations. When welding galvanized and galvanealed metals, however, there is a tendency for zinc vapour to enter into the molten weld pool, which results in a defective weld deposit. More specifically, zinc coating vaporized from the surface of the metal tends to create turbulence in the shielding gas thereby introducing atmospheric nitrogen and oxygen into the weld pool resulting in nitrogen and oxygen contamination of the weld deposit and increased spatter. In addition, zinc vapour is not readily soluble in molten steel, and any vapour that does not escape from the molten weld pool before solidification results in the formation of blow holes and pores in the weld deposit. Blow hole and pore formation is particularly severe when welding joints without a gap between the workpieces since there is limited area for vapour to escape from the molten weld pool. Galvanized metals are known for improved corrosion resistance, and are used increasingly in the automotive industry for automobile frames, bumpers, axles, cradle assemblies and fenders, and water heaters among other components, which often require welding gapless joints. These metals are generally low carbon and low alloy steels having good press forming characteristics. In some applications, industry uses low carbon and low alloy galvanealed steels with a thickness ranging between approximately 0.75 and 6.25 mm (0.030 and 0.250 inches) and a coating weight of approximately 45 gm/m2. The relatively thin gauge steels often must be welded in a single pass at high weld rates to prevent the welding arc from burning through the metal. Assembly line operations also require single pass, high weld rates to improve productivity. Weld rates up to approximately 150 cm/min are sometimes required. At high weld rates, however, the molten weld pool tends to cool relatively rapidly thereby reducing the time for vapour to escape from the weld pool, which increases the formation of blow holes and porosity in the weld deposit. The rapidly cooled weld deposit formed in high weld rates applications tends also to result in a poor weld deposit contour, or wetting characteristic. High weld rates are also a source of turbulence in the shielding gas, which tends to increase the addition of atmospheric nitrogen and oxygen into the weld pool as discussed above. Presently, galvanized steels are welded with self shielded weld wires containing magnesium and barium. The magnesium displaces nitrogen and oxygen to reduce porosity. But the magnesium also reacts with the zinc coating to cause liquid metal embrittlement, which is unacceptable in many industrial applications. These self shielded wires also produce excessive smoke, which is undesirable, and moreover produce excessive spatter and slag, which must be removed before applying coatings over the weld deposit. Slag formation tends also to prevent vapour from escaping from the molten weld pool resulting in increased blow holes and porosity, which are further increased when welding gapless joints. In addition, barium is considered toxic and creates an unacceptable health hazard. JP-A-61-21432 discusses a solid weld wire for gas shielded arc welding galvanized steels. Solid wires, however, have undesirable deep "finger" penetration and reduced productivity in comparison to metal-core wires. In addition, the solid weld wire of JP-A-61-21432 has a relatively high carbon content, which may reduce ductility and increase hot cracking sensitivity and spatter. This solid weld wire also has a relatively high titanium content, which increases slag formation, and includes aluminum, which increases spatter and provides a poor wetting characteristic. The solid weld wire of JP-A-6121432 therefore tends to be expensive and is not suitable for welding at high weld rates. JP-A-2 059 195 discusses a solid weld wire for gas shielded arc welding galvanized steels at high weld rates. JP-A-2 059 195, however, teaches that it is undesirable to add aluminum, titanium, silicon and other deoxidizing agents to the solid weld wire because deoxidizing agents allegedly increase the activity of zinc in the molten weld pool resulting in blow hole formation. The solid weld wire of the JP-A-2 059 195 also produces slag resulting possibly from the substantial elimination of deoxidizing agents from the weld wire. The solid weld wire of the JP-A-2 059 195 includes niobium and vanadium to reduce blow hole and pore formation in cases where gas shielding effectiveness is reduced. The amounts of niobium and vanadium disclosed in JP-A-2 059 195, however, result in increased hot cracking and have an adverse affect on ductility. In addition, this solid wire has increased strength and hardenability that results in increased loads on wire drawing dies during manufacture of the weld wire increasing production costs. In view of the discussion above, there exists a demonstrated need for an advancement in the art of metal-core weld wires. GB-A-1 079 234, which represents the closest prior art, discloses a metal-core weld wire comprising a low carbon steel sheath, and a core composition surrounded by the low carbon steel sheath, the core composition including, by total weight of the metal-core weld wire, between approximately 0.05 - 0.20 % Ti and Cerium as wetting agent. GB-A-1 079 234 does not show a core composition containing Niobium, at least in combination with Titanium. GB-A-1 120 588 discloses a metal-core weld wire, the core composition including Titanium and Niobium. The proportions shown are outside the ranges of the present invention. According to this invention a metal-core weld wire usable for gas shielded arc welding low carbon and low alloy galvanized and galvanealed steels, the metal-core weld wire comprises: a low carbon steel sheath; and a core composition surrounded by the low carbon steel sheath, the core composition not containing a fluoride or chloride wetting and fluxing agent and including, by total weight of the metal-core weld wire, between approximately 0.05 - 0.20 % Ti and between approximately 0.05 - 1.00 % Nb, the core composition is, by total weight of the metal-core weld wire, between approximately 0.1 - 12.0 %; wherein the weld wire provides, at weld rates up to 100 cm/min, reduced arc ionization potential and spatter, and improved arc stability and shielding, and wherein the weld wire produces, at weld rates up to 100 cm/min, weld deposits having reduced blow holes and porosity, and reduced weld pool surface tension resulting in an improved wetting characteristic. Preferably, the weld deposit has reduced blow hole and pore formation, no liquid metal embrittlement or hot cracking, improved weld deposit wetting characteristic, improved impact strength and ductility, and improved corrosion resistance, at relatively high weld deposit rates. Particular examples of weld wire in accordance with this invention will now be described with reference to the accompanying drawings, in which:- Figure 1 is a perspective view of a lap joint having substantially no gap between overlapping plates; and, Figure 2 is an end view of horizontal and vertical plates arranged in a T-configuration with a gap therebetween. The invention is drawn to a novel metal-core weld wire, or tubular welding electrode, comprising a low carbon steel sheath having a tubular core filled with a core composition. The core composition is between approximately 0.001 - 12.0 % total weight of the metal-core weld wire. The low carbon steel sheath includes minimum amounts of carbon to minimize hot cracking and spatter. In the present metal-core weld wire, a carbon content greater than 0.06 % has been found to have a tendency towards hot cracking of the weld deposit as further discussed below. In one embodiment, the low carbon steel sheath includes, by total weight of the metal core weld wire, between approximately 0.01 - 0.10 % C, and in another embodiment between approximately 0.01 - 0.03 % C. The core composition includes niobium alone or in combination with vanadium to prevent blow hole and pore formation. It is expected that tantalum will have the same beneficial affect as niobium on the prevention of blow holes and pore formation when welding galvanealed steels. The niobium and vanadium also reduce surface tension in the weld pool resulting in an improved wetting characteristic, or wet out, of the molten weld pool and therefore provide an improved weld deposit contour, which permits increased weld deposit rates. In addition, niobium and vanadium increase the hardenability of the weld deposit, which is necessary for increasing weld deposit strength. In one embodiment, the core composition includes, by total weight of the metal-core weld wire, between approximately 0.05 - 1.00 % Nb, and in another embodiment, between approximately 0.30 - 0.40 % Nb. In the present metal-core weld wire, a niobium amount greater than 0.73 % has been found to increase the tendency towards hot cracking. In an alternative embodiment, the core composition includes between approximately 0.05 0.80 % V, and in another embodiment between 0.05 - 0.20 % V. Increased amounts of vanadium tend to increase hot cracking and decrease ductility of the weld deposit. The core composition also includes titanium in combination with the niobium, and optionally the vanadium to prevent blow hole and pore formation. Titanium is a denitrifying agent that combines with nitrogen introduced into the weld pool and reduces porosity. Titanium tends also to reduce surface tension in the weld pool permitting increased weld deposit rates as discussed above with respect to niobium and vanadium. Additionally, titanium has a low ionization energy so that titanium tends to stabilize the welding arc. A more stable welding arc provides a more stable shielding gas envelope resulting in reduced amounts of atmospheric nitrogen and oxygen being introduced into the molten weld pool. In one embodiment, the core composition includes, by total weight of the metal-core weld wire, between approximately 0.05 - 0.20 % Ti, and in another embodiment, between approximately 0.10 - 0.20 % Ti. Amounts of titanium greater than 0.15 % tend to increase slag formation on the weld deposit, which is undesirable because slag tends to trap vapour in the molten weld pool resulting in increased blow hole formation. Slag is also undesirable because it must be ultimately removed from the weld deposit in many applications, which increases costs. Reducing the amount of titanium below 0.10 % has been found to increase spatter, decrease arc stability and reduce the weld deposit wetting characteristic. In another embodiment, the core composition includes copper to prevent blow hole and pore formation and to reduce hot cracking. The presence of copper in the weld pool tends also to reduce liquid metal embrittlement by alloying with zinc to minimize zinc segregation to the grain boundaries of the weld deposit. In addition, copper in the metal-core weld wire results in formation of a protective barrier on the surface of the weld deposit, which improves corrosion resistance. In one embodiment, the core composition includes, by total weight of the metal-core weld wire, between approximately 0.02 - 1.00 % Cu, and in another embodiment, between approximately 0.40 - 0.60% Cu. Reduction of copper tends to increase hot cracking and reduce corrosion resistance. The metal-core weld wire of the present invention includes minimum amounts of silicon and manganese, which are primarily deoxidizing agents to reduce blow hole formation, minimize hot cracking, and to improve the wetting characteristic of the weld deposit. The metal-core weld wire includes in the sheath, or core composition, or both, by total weight of the metal-core weld wire, between approximately 0.1 - 1.0 % Si, and in an alternative embodiment between approximately 0.4 - 0.5 % Si. The metal-core weld wire also includes in the sheath, or core composition, or both, by total weight of the metal-core weld wire, between approximately 0.1 - 1.0 % Mn, and in an alternative embodiment between 0.6 and 0.8 % Mn. The core composition may also include iron powder as filler material. In one embodiment, the metal-core weld wire includes, by total weight of the metal-core weld wire, less than 0.50 % nickel, less than 0.50 % chromium, less than 0.50 % molybdenum, and less than 0.50 % tungsten. The core composition is, by total weight of the metal-core weld wire, between approximately 0.001 - 12.0 %, and in an alternative embodiment between approximately 5.0 and 7.0 %. The lower limit on the core composition is determined by the total weight percent of the core composition constituents. Generally, blow hole formation tends to increase as the core composition percentage increases. The weld deposit oxygen content is reduced significantly by reducing the oxygen content of the weld wire, which results among other advantages increased impact strength of the weld deposit. The weld wire oxygen content is reduced by using a low oxygen iron powder in the core composition, or by reducing the amount of iron powder filler material in the core composition, or by baking the wire in an inert atmosphere as disclosed in copending U.S. Patent Application Serial No. 08/665000, filed on 11 June 1996. The compositions of present invention are applicable to metal-core wires of any diameter, and in particular to wires diameters between approximately 0.076 0.157 cm (0.030 - 0.062 inches). EXAMPLES Table I illustrates metal-core wire compositions according to several exemplary embodiments of the present invention and related data on Blow Hole formation, Hot Cracking, ductility based on a U-Bend Test, and a Weldability Rating as discussed further below. A "--" entry in Table I indicates that data was not obtained for the particular test. The Blow Hole data of Table I was determined on visual inspection after making a lap joint weld approximately 8.9 cm (3.5 inches) long on overlapping galvanealed steel plates 1.7 mm thick. The overlap was maintained at a minimum of approximately 0.64 cm (0.25 inches). The steel plates were welded with no gap therebetween by placing weights on the upper steel plate. Figure 1 illustrates an overlapping plate arrangement with no gap. The welding operation was performed under the following conditions: 230 - 240 amperes; 24.4 volts; 0.045 wire with 1.90 cm (0.75 inches) electrode stick out (ESO); 100 cm/min minimum travel speed; 92 % Ar / 8 % CO 2 shielding gas flowing at 40-45 ft 3 per hour; 20 - 27 degrees push angle. The Hot Cracks data of Table I was determined by measuring hot cracks after welding along both sides of a vertical plate initially tack welded to a horizontal plate in a T-configuration. Figure 2 illustrates the horizontal and vertical plates, which were initially separated by a gap of at least approximately 0.20 cm (0.09 inches). The plates were approximately 0.60 cm (0.25 inches) thick, approximately 5.1 cm (2.00 inches) wide and approximately 25.4 cm (10.0 inches) long. The plate surfaces were sanded, and the plate composition included approximately C 0.04%, Mn 0.24 %, Si 0.001 %, and Al 0.07%. The welding operation was performed under the following conditions: 220 - 240 amperes; 24 volts; 0.04 wire with 1.27 - 1.90 cm (0.25 - 0.75 inches) ESO; 40 cm/min minimum travel speed; and 92 % Ar/8% CO 2 shielding gas flowing at 40-45 ft 3 per hour. The foregoing Hot Cracks test is considered to be a severe welding test. A crack less than approximately 1.27 cm (0.5 inch) does not gradually pose a problem in the majority of applications where these metal-core weld wires will be used. It is not expected that any of the exemplary metal-weld wire compositions of Table 1 will result in hot cracking when used to weld an unrestrained lap joint on low carbon galvanealed steel. The U-bend data of Table 1 was determined on visual inspection after making a lap weld along two overlapping galvanealed plates 1.7 mm thick, 5.1 cm (2 inches) wide and 20.32 cm (8 inches) long with no gap therebetween. The welded plates were then cut longitudinally to obtain a 5.1 cm (2 inch) wide strip with the lap weld disposed lengthwise approximately in the centre of the strip. The welded strip was then pressed into a U bend about a 2.5 cm (1 inch) radius die at a temperature of -60 degrees F. The bend was formed along the length of the weld, which was on the outer circumference of the bent strip. Cracks greater than approximately 0.159 cm (0.062 inches) are indicated. The Weldability data of Table 1 was obtained by rating the following three categories 1.) "Spatter" 2.) "Weld Deposit Wetting" and 3.) "Arc Stability" on a scale of 0-6 and summing the ratings for each metal-core weld wire composition. The lowest rating is 0 and the highest rating is 6.

Claims: A metal-core weld wire usable for gas shielded arc welding low carbon and low alloy galvanized and galvanealed steels, the metal-core weld wire comprising: a low carbon steel sheath; and a core composition surrounded by the low carbon steel sheath, the core composition not containing a fluoride or chloride wetting and fluxing agent and including, by total weight of the metal-core weld wire, between approximately 0.05 - 0.20 % Ti and between approximately 0.05 - 1.00 % Nb, the core composition is, by total weight of the metal-core weld wire, between approximately 0.1 - 12.0 %; wherein the weld wire provides, at weld rates up to 100 cm/min, reduced arc ionization potential and spatter, and improved arc stability and shielding, and wherein the weld wire produces, at weld rates up to 100 cm/min, weld deposits having reduced blow holes and porosity, and reduced weld pool surface tension resulting in an improved wetting characteristic. A metal-core weld wire according to claim 1, in which the core composition is, by total weight of the metal-core weld wire, between approximately 2.5 - 12.0%. A metal-core weld wire according to claim 1 or 2, in which a trace amount of Ni is included in the core composition. A metal-core weld wire according to any one of the preceding claims, wherein the core composition includes, by total weight of the metal-core weld wire, between approximately 0.02-1.00 % Cu. A metal-core weld wire according to any one of the preceding claims, further comprising between approximately 0.1 - 1.0 % Si and between approximately 0.1 - 1.0 % Mn, wherein the low carbon steel sheath includes, by total weight of the metal-core weld wire, between approximately 0.01 - 0.03 % C. A metal-core weld wire according to claim 5, in which the core composition includes, by total weight of the metal-core weld wire, between approximately 0.30 - 0.40 % Nb, between approximately 0.10 - 0.20 Ti, and Fe powder, wherein the core composition is, by total weight of the metal-core weld wire, between approximately 5.0 and 7.0 %. A metal-core weld wire according to claim 6, wherein the core composition includes, by total weight of the metal-core weld wire, between approximately 0.40-0.60 % Cu. A metal-core weld wire according to any of the preceding claims, wherein the core composition includes, by total weight of the metal-core weld wire, between approximately 0.05-0.80 % V. A metal-core weld wire according to any one of the preceding claims, wherein the Titanium content of the core is less than or equal to 0.15%.

Inventors: BUNDY JOSEPH, DAEMEN ROGER, KEEGAN JAMES, NAGARAJAN SUNDARAM, BUNDY, JOSEPH, DAEMEN, ROGER, KEEGAN, JAMES, NAGARAJAN, SUNDARAM
Applicants: ILLINOIS TOOL WORKS, ILLINOIS TOOL WORKS INC.
Application year: 1997
Main classification: B23K35
IPC codes: C22C38, B23K35, B23K9