Dispersible silicone compostions

Abstract: The present invention is a dispersible silicone composition comprising (I) a silicone composition prepared by reacting (i) a polyorganosiloxane, (ii) a silicon compound, optionally (iii) a filler and (iv) a catalytic amount of a compound for promoting the reaction of the other components and (II) mineral oil. The mineral oil is effective as a dispersing agent for the silicone composition (I). The product mineral oil-containing compositions are easier to handle, produce less waste and more efficiently disperse into mineral oil based formulations.

Description: This invention relates to dispersible silicone compositions comprising a blend of a silicone composition and mineral oil having a viscosity of 5-20 mPa.s at 25°C. The use of various silicone containing compositions as antifoams or defoamers is known. In this regard, it is well established that this art is highly unpredictable and slight modification can greatly alter performance of such compositions. Most of these compositions contain silicone fluid (usually dimethylpolysiloxane), often in combination with small amounts of silica filler. Additionally, these compositions may include various surfactants and dispersing agents to impart improved foam control or stable properties. Useful silicone compositions as foam control agents have been taught in the prior art. For example, the following U.S. Patents are generally representative: 4,639,489; 4,690,713; 4,749,740; 4,978,471; 4,983,316; 5,283,004 and 5,442,010. Similar international documents are EP-A 0 217 501; CA-A 2,110,523; GB-A 1,224,026 and GB-A 1,496,011. US-A-4,032,473 discloses a water-based defoamer composition in the form of an aqueous emulsion containing, as the disperse phase, a water insoluble liquid hydrocarbon, a normally solid fatty acid diamide. hydrophobic silica particles, and a non-ionic emulsifier having an HLB of about 8-12. It has now been surprisingly found that mineral oils having a viscosity of 5-20 mPa.s at 25°C are effective dispersing agents for silicone compositions. It is an object of the present invention to provide silicone compositions which are stable and easily dispersible. The present invention is a dispersible silicone composition comprising a blend of (I) a silicone composition prepared by reacting at a temperature of 50 to 300°C. a mixture comprising: (i) 100 parts by weight of at least one polyorganosiloxane selected from (A) a polyorganosiloxane having a viscosity of 20 to 100,000 mm 2 /s at 25°C. and expressed by the general formula R 1 a SiO (4-a)/2 , in which R 1 is a monovalent hydrocarbon or halogenated hydrocarbon group having 1 to 10 carbon atoms and a has an average value of 1.9 to 2.2; (B) a polyorganosiloxane having a viscosity of 200 to 100 million mm 2 /s at 25°C. expressed by the general formula R 2 b (R 3 O) c SiO (4-b-c)/2 in which R 2 is a monovalent hydrocarbon or halogenated hydrocarbon group having 1 to 10 carbon atoms, R 3 is hydrogen atom or a monovalent hydrocarbon group having 1 to 10 carbon atoms, b has an average value of 1.9 to 2.2 and c has a sufficient value to give at least one -OR 3 group in each molecule, at least one such -OR 3 group being present at the end of the molecular chain or (C) a mixture of (A) and (B); (ii) 0.5 to 20 parts by weight of at least one silicon compound selected from (a) an organosilicon compound of the general formula R 4 d SiX 4-d , in which R 4 is a monovalent hydrocarbon group having 1 to 5 carbon atoms, X is selected from halogen atom or a hydrolyzable group and d has an average value of one or less; (b) a partially hydrolyzed condensate of compound (a); (c) a siloxane resin comprising (CH 3 ) 3 SiO 1/2 units and SiO 4/2 units wherein the ratio of (CH 3 ) 3 SiO 1/2 units to SiO 4/2 units is 0.4:1 to 1.2:1; or (d) a condensate of compound (c) and compound (a) or (b); and (iii) a catalytic amount of a compound for promoting reaction of components (i) and (ii); and (II) mineral oil having a viscosity of 5-20 mPas at 25°C. The compositions of this invention expediently comprise silicone composition (I) and mineral oil (II). Component (I) is prepared by reacting (i) a polyorganosiloxane, (ii) a silicon compound and (iii) a catalytic amount of a compound for promoting reaction of the other components. Component (i) may be selected from (A) polyorganosiloxanes comprising siloxane units of the general formula R 1 a SiO (4-a)/2 and having a viscosity of 20 to 100,000 mm 2 /s (centistokes) at 25°C. The organo groups R 1 of the polyorganosiloxanes (A) are the same or different monovalent hydrocarbon or halogenated hydrocarbon groups having one to ten carbon atoms. Specific examples thereof are well known in the art and include methyl, ethyl, propyl, butyl, octyl, trifluoropropyl, phenyl, 2-phenylethyl and vinyl groups. The methyl group is particularly preferred. In this formula, a has a value of 1.9 to 2.2. It is particularly preferred that polyorganosiloxane (A) is a trimethylsilyl-terminated polydimethylsiloxane having a viscosity of 350 to 15,000 mm 2 /s at 25°C. Alternatively, component (i) may be selected from (B) polyorganosiloxanes comprising siloxane units of the general formula R 2 b (R 3 O) c SiO (4-b-c)/2 and having a viscosity of 200 to 100 million mm 2 /s at 25°C. wherein R 2 is independently selected from the monovalent hydrocarbon or halogenated hydrocarbon groups designated for R 1 , R 3 is a hydrogen atom or R 2 ; and the -OR 3 group is present at least at one of the molecular chain ends of the polyorganosiloxane. The value of b is between 1.9 to 2.2 and c has a value to provide at least one -OR 3 group per molecule. It is particularly preferred that polyorganosiloxane (B) is a hydroxyl-terminated polydimethylsiloxane having a viscosity of 1,000 to 50,000 mm 2 /s at 25°C. Component (i) may also be (C) a mixture of (A) and (B) in any proportion. Component (ii) is at least one silicon compound selected from (a) to (d). (a) is an organosilicon compound of the general formula R 4 d SiX 4-d wherein R 4 is a monovalent hydrocarbon group having one to five carbon atoms, X is a halogen atom or a hydrolyzable group, such as -OR 5 or -OR 6 OR 7 , in which R 6 is a divalent hydrocarbon group having one to five carbon atoms and R 5 and R 7 are each a hydrogen atom or a monovalent hydrocarbon group having one to five carbon atoms, with the average value of d not exceeding 1. (b) is a partially hydrolyzed condensate of the compound (a). (c) is a siloxane resin comprising (CH 3 ) 3 SiO 1/2 and SiO 2 units with a molar ratio of (CH 3 ) 3 SiO 1/2 to SiO 2 of 0.4:1 to 1.2:1. (d) is a condensate of the siloxane resin (c) with the compound (a) or (b). It is preferred that component (ii) is selected from either an alkyl polysilicate, wherein the alkyl group has one to five carbon atoms, such as methyl polysilicate, ethyl polysilicate and propyl polysilicate or the siloxane resin (c). Most preferably, component (ii) is either ethyl polysilicate or a siloxane resin copolymer comprising (CH 3 ) 3 SiO 1/2 units and SiO 2 units in a molar ratio of approximately 0.4:1 to 1.2:1. Component (iii) is a compound used as a catalyst for promoting the reaction of the other components. Any compound which promotes condensation reactions or rearrangement/ condensation reactions is suitable as our component (iii). It is selected from siloxane equilibration catalysts, silanol-condensing catalysts or a combination thereof. Catalysts suitable as component (iii) are exemplified by alkali metal hydroxides such as potassium hydroxide, sodium hydroxide or cesium hydroxide; alkali metal silanolates such as potassium silanolate; alkali metal alkoxides such as potassium isopropoxide or potassium ethoxide; quaternary ammonium hydroxides such as beta-hydroxyethyltrimethyl ammonium hydroxide, benzyltrimethyl ammonium hydroxide and tetramethyl ammonium hydroxide; quaternary ammonium silanolates; quaternary phosphonium hydroxides, such as tetrabutyl phosphonium hydroxide or tetraethylphosphonium hydroxide; quaternary phosphonium silanolates; metal salts of organic acids such as dibutyltin dilaurate, stannous acetate, stannous octanoate, lead napthenate, zinc octanoate, iron 2-ethylhexoate and cobalt naphthenate; mineral acids such as sulfuric or hydrochloric acid; organic acids such as acetic acid or organosulfonic acids and ammonium compounds such as ammonium carbonate or ammonium hydroxide. It is preferred that the catalyst is selected from potassium silanolate, potassium hydroxide or sodium hydroxide. The mixture of silicone composition (I) further comprises up to 30 parts by weight of component (III) as filler. This filler is exemplified by fumed, precipitated or plasmatic TiO 2 , Al 2 O 3 , Al 2 O 3 /SiO 2 , ZrO 2 /SiO 2 and SiO 2 . Specific examples of this filler include zirconium silica hydrogels (co-precipitated zirconium and silica) or hydrophobic precipitated silica, the latter being highly preferred. The filler can be either hydrophilic or hydrophobic. It is hydrophobed during manufacture (i.e. in-situ) or independently. Various grades of silica having a particle size of several millimicrons to several microns and a specific surface area of 50 to 1000 m 2 /g are commercially available and suitable for use. The mixture of silicone composition (I) further comprises up to 20 parts by weight of component (iv), a polyorganosiloxane comprising siloxane units of the general formula R 8 e (R 9 O) f SiO (4-e-f)/2 and having a viscosity of 5 to 200 mm 2 /s at 25°C. wherein R 8 is a monovalent hydrocarbon or halogenated hydrocarbon group having one to ten carbon atoms and R 9 is hydrogen atom or a monovalent hydrocarbon group having one to ten carbon atoms. The value of e is between 1.9 and 2.2 and f has a value to provide two or more -OR 9 groups in each molecule. It is particularly preferred that component (iv) is a hydroxyl-terminated polydimethylsiloxane having a viscosity of 10 to 100 mm 2 /s at 25°C. It is preferred that component (iv) is added when filler (III) is a hydrophilic silica. A mixture of components (i), (ii) and (iii), optionally containing components (III) and/or (iv) is reacted under heat to produce the silicone composition (I), the proportions of the various components being: Component (i) - 100 parts by weight; Component (ii) - 0.5 to 20, preferably 1 to 7, parts by weight; Component (iii) - A catalytic amount (usually in the range of 0.03 to 1 part by weight); Component (iv), if present, - up to 30, preferably 1 to 15, and highly preferred is 5 to 15 parts by weight; Component (v), if present, - up to 20, preferably 1 to 10, parts by weight. The proportions of components (A) and (B) used depends largely on their respective viscosities. It is preferable to use a mixture of (A) and (B) which has a viscosity of 1,000 to 100,000 mm 2 /s at 25°C. The silicone composition (I) is prepared by first mixing components (i), (ii) and (iii) and heating this blend to 110 to 120°C. Filler (III), if desired, is then uniformly added using an appropriate dispersing device, such as a homomixer, colloid mill or triple roll mill. The resulting mixture is heated at a temperature of 50 to 300°C., preferably 100 to 300°C., and reacted for one to eight hours, although the reaction time varies depending on the temperature. If component (iv) is employed in the composition, it is generally added after the filler (III). It is preferable to carry out all mixing and heating operations in an inert gas atmosphere to avoid any danger and to remove volatile matter (unreacted matter, by-products and the like). The mixing order of components, the heating temperature and residence time are not believed critical and can be changed as required. It is further preferred that, after reaction, the catalyst is neutralized to further stabilize silicone composition (I). Alternatively, silicone composition (I) comprises a diorganopolysiloxane, a silicon compound and a catalyst for promoting the reaction of these components, with this combination optionally containing a filler such as silica. These systems contain a mixture of a trimethylsilyl-terminated polydimethylsiloxane and a diorganopolysiloxane having silicon-bonded hydroxyl groups or silicon-bonded alkoxy groups along its main chain or at its chain ends, said alkoxy groups having from 1 to 6 carbon atoms. The silicon compound (ii) acts as a crosslinker for the diorganopolysiloxane by reacting functionalities on said components. It is further preferred that said diorganopolysiloxane is either a linear or a branched polymer or copolymer of siloxane units selected from dimethylsiloxane units, methylphenylsiloxane units or methyltrifluoropropylsiloxane units. Most preferably, the diorganopolysiloxane of component (A) is a polydimethylsiloxane containing Si-bonded hydroxyl or methoxy functionality. Our silicon compound (ii) is preferably a siloxane resin comprising (CH 3 ) 3 SiO 1/2 and SiO 2 units and having a molar ratio of (CH 3 ) 3 SiO 1/2 /SiO 2 between 0.4:1 and 1.2:1. The latter resin is prepared according to U.S. Patent 2,676,182 and typically contains from 0.5 to 3 weight percent of hydroxyl groups. A highly preferred component (I) is a homogeneous blend of a hydroxyl-terminated polydimethylsiloxane, a trimethylsilyl-terminated polydimethylsiloxane having a viscosity in the range of 1,000 to 50,000 mm 2 /s at 25°C., an alkyl polysilicate wherein the alkyl group has one to five carbon atoms, such as methyl polysilicate, ethyl polysilicate and propyl polysilicate and a potassium silanolate catalyst reacted at a temperature of 50 to 300°C. Component (II) is mineral oil. The term "mineral oil" refers to hydrocarbon oils derived from carbonaceous sources, such as petroleum, shale and coal or equivalents thereof. The mineral oil of component (II) is any type of mineral oil, many of which are commercially available, including heavy white mineral oil that is high in paraffin content, light white mineral oil, petroleum oils such as aliphatic or wax-base oils, aromatic or asphalt-base oils or mixed base oils, petroleum derived oils such as lubricants, engine oils, machine oils or cutting oils and medicinal oils such as refined paraffin oil. The above mentioned mineral oils are available commercially at a variety of viscosities from Amoco Chemical Company (Chicago, ILL.) under the tradename Amoco™ White Mineral Oil, from Exxon Company (Houston, Texas) under the tradenames Bayol™, Marcol™ or Primol™ or from Lyondell Petrochemical Company (Houston, Texas) under the trade name Duoprime® Oil. The mineral oil has a viscosity of from 5 to 20 millipascal-seconds (mPa·s) at 25°C. For our invention, the weight ratio of component (I) to component (II) is generally within a range from 99:1 to 40:60 and preferably from 90:10 to 50:50. The dispersible silicone compositions of the present invention also comprise component (IV) a saturated or unsaturated bisamide, such as those disclosed in U.S. Patent 4,107,073. Preferred bisamides are those having the formula RC(O)N(H)-(CH 2 ) n -N(H)C(O)R where n is an integer from 1 to 6 and R is a saturated or unsaturated, straight or branched chain hydrocarbyl group having from 5 to 22 carbon atoms. Particularly preferred is ethylene bis-stearamide. The amount of bisamide (IV) used in the compositions is generally 0.01 to 5 parts by weight; and preferably is 0.01 to 2 parts by weight, based on 100 parts by weight of mineral oil. In addition to the above components, the dispersible silicone compositions of the present invention may also contain adjuvants such as corrosion inhibitors and dyes. Our compositions are typically prepared by blending components (I) and (II), and any optional components, to form a homogenous mixture. This is accomplished by any convenient mixing method known in the art such as a spatula, mechanical stirrers, in-line mixing systems containing baffles, blades or any of the like mixing surfaces, including powered in-line mixers or homogenizers, a drum roller, a three-roll mill, a sigma blade mixer, a bread dough mixer or a two roll mill. Although the mixing order is not considered critical, it is preferred to first mix components (I) and (II) and to then disperse the filler (III) into this combination by using a high shear mixer. It is also preferred that components (I) and (II), and optionally (III), be first blended together and then adding, if desired, bisamide (IV). The present invention also relates to a process for controlling foam in a foaming system wherein the claimed dispersible silicone compositions are simply added to a foaming or foam-producing system, in an amount sufficient to reduce foaming, as determined by routine experimentation. Usually, our dispersible silicone compositions are added at a concentration of 0.001 to 0.1 part by weight, based on the weight of the foaming system. However, the skilled artisan will readily determine optimum concentrations after a few routine experiments. The method of addition is not critical and the composition is metered or added by any of the techniques known in the art. Examples of foaming systems contemplated herein include media encountered in the production of phosphoric acid; sulphite or sulphate process pulping operations; bauxite digestion solutions in the production of aluminum; metal working fluids; paper manufacture; detergent systems and hydrocarbon based systems. The claimed compositions are conveniently used as any kind of foam control composition, i.e. as defoaming compositions and/or antifoaming compositions. Defoaming compositions are generally considered as foam reducers whereas antifoaming compositions are generally considered as foam preventors. Thus, the compositions of this invention find utility as foam control compositions in various media such as inks, coatings, paints, detergents, pulp and paper manufacture, textile dyes and hydrocarbon containing fluids. All parts and percentages in the examples are on a weight basis unless indicated to the contrary. All viscosities were measured by a Brookfield Viscometer at 25°C. The following materials were employed in the preparation of these dispersible silicone compositions: Silicone composition A was prepared according to Example 1 of U.S. Patent 4,639,489. This composition contained 60 parts of a trimethylsilyl-terminated polydimethylsiloxane having a viscosity of 1,000 mm 2 /s at 25°C.; 29 parts of a hydroxyl-terminated polydimethylsiloxane having a viscosity of 12,500 mm 2 /s at 25°C.; 2.9 parts of ethyl polysilicate (Silicate 45™ of Tama Kagaku Kogyo Co., Ltd., Japan); 4.8 parts of a potassium silanolate catalyst; 2.9 parts of Aerogel™ #200 silica (Nippon Aerogel Co., Japan) having a surface area of 200 m 2 /g; and 4.8 parts of hydroxyl-terminated polydimethylsiloxane having a viscosity of 40 mm 2 /s at 25°C. In addition to the above ingredients, this formulation also included 0.3 part of ethanol as part of the catalyst, 0.1 part of water adsorbed on the silica and 0.1 part of L-540™, added as a process dispersant. L-540™ (Union Carbide Corp., Danbury, CT) is described as a silicone polyether block copolymer wherein the polyether blocks consist of 50/50 mole percent of polyoxyethylene/polyoxypropylene. Mineral Oil A is Duoprime® Oil 55, a white mineral oil having a viscosity of 10 mPa·s at 25°C. from Lyondell Petrochemical Company (Houston, Texas). Mineral Oil B is Duoprime® Oil 90, a white mineral oil having a viscosity of 23 mPa·s at 25°C. from Lyondell Petrochemical Company (Houston, Texas). Mineral Oil C is Duoprime® Oil 200, a white mineral oil having a viscosity of 74 mPa·s at 25°C. from Lyondell Petrochemical Company (Houston, Texas). Mineral Oil D is Duoprime® Oil 500, a white mineral oil having a viscosity of 189 mPa·s at 25°C. from Lyondell Petrochemical Company (Houston, Texas). Mineral Oil E is a heavy paraffinic mineral oil having a viscosity of 177 mPa·s at 25°C. from Fisher Scientific Company (Pittsburgh, Pa.). Mineral Oil F is a mineral oil having a viscosity of 10-40 mPa·s at 40°C. Comp. EXAMPLE 1 Silicone Composition A was mixed with Mineral Oil E in the following respective proportions, the proportion being that of Silicone Composition A to Mineral Oil E: 30/70, 40/60, 50/50, 60/40 and 70/30. After setting for 48 hours at 25°C., all these blends had separated into two distinct layers. EXAMPLE 1 Several samples were prepared by mixing Silicone composition A and a series of white mineral oils having a viscosity range of 10 to 189 mPa·s were mixed until a uniform consistency was achieved. Sample 1 was mixture of mineral oil A and Silicone composition A. Samples 2-4 were mixtures of Silicone Composition A with higher viscosity mineral oils. After 24 hours at 25°C., the samples were inspected to determine if they were still uniform, stable mixtures. The results in TABLE 1 show that only those blends using Mineral Oil A remained stable. WEIGHT RATIO OF SILICONE TO OIL SAMPLE MINERAL OIL 70/30 60/40 50/50 40/60 1 A STABLE STABLE STABLE STABLE 2 B 2 PHASES 2 PHASES 2 PHASES 2 PHASES 3 C 2 PHASES 2 PHASES 2 PHASES 2 PHASES 4 D 2 PHASES 2 PHASES 2 PHASES 2 PHASES Sample 1 was then placed in a 40°C. oven and monitored six weeks for any sign of separation. No separation of phases or change in appearance was noted. EXAMPLE 2 Silicone Composition A and Mineral Oil A were formulated into foam control compositions. Foam Control Composition 1 was prepared by mixing 11.02 grams of 50/50 parts by weight mixture of Silicone Composition A with Mineral Oil A, 54.00 grams of Mineral Oil E, 20.00 grams of a 10% by weight dispersion of ethylene bis-stearamide in Mineral Oil F and 15.07 grams of a 20% by weight dispersion of hydrophobic silica in Mineral Oil F. Foam Control Composition 2 was prepared by mixing 9.02 grams of a 60/40 parts by weight mixture of Silicone Composition A and Mineral Oil A, 55.00 grams of Mineral Oil E, 20.00 grams of a 10% by weight dispersion of ethylene bis-stearamide in Mineral Oil F and 15.02 grams of a 20% by weight dispersion of hydrophobic silica in Mineral Oil F. Foam Control Composition 3 was prepared by mixing 7.90 grams of a 70/30 parts by weight mixture of Silicone Composition A and Mineral Oil A, 57.01 grams of Mineral Oil E, 20.00 grams of a 10% by weight dispersion of ethylene bis-stearamide in Mineral Oil F and 15.02 grams of a 20% by weight dispersion of hydrophobic silica in Mineral Oil F. Comparative Foam Control Composition 1 was a composition in which no blend of the present invention was used in the foam control composition. The level of ethylene bis-stearamide and hydrophobic silica was unchanged from that used in Foam Control Compositions 1-3. Mineral Oil E was again used, but its amount was increased to compensate for lack of a presence of the silicone composition. Thus, 65.01 grams of Mineral Oil E was mixed at room temperature with 20.00 grams of a 10% by weight dispersion of ethylene bis-stearamide in Mineral Oil F and 15.00 grams of a 10% wt dispersion of hydrophobic silica in Mineral Oil F. The Foam Control Compositions described above were tested for their capacity to reduce or eliminate foaming in a recirculating pump test. In this test, 400 cm 3 of Kraft pulp black liquor (the liquor comprised sodium lignin sulfonate, pentosan sugars, tall oil soaps, sodium carbonate, sodium sulfide and sodium hydroxide dissolved in water with a solids content of 15% and a pH of 13.5 at 20°C.) were circulated with nitrogen injected into the liquor stream to maximize foaming. The liquid volume in the test unit is set at 14 cm of height within the vertical column in which foam rise is measured. At the start of the test, which is conducted at 116.1°C. (177°F.), the foam column is allowed to rise to a height of 21 cm. At that point, 100 µl of one of the foam control compositions described above was injected by a syringe into the recirculating liquor stream. Foam height as a function of time was then monitored and recorded. Table 2 shows the results of these tests. Foam Control Composition Silicone (ppm) Foam Control Composition (ppm) Foam Height (cm) at 15 sec. 2.5 min. 5 min. 1 13.1 237.5 14.0 18.0 272 2 13.1 237.5 13.0 18.5 256 3 13.1 237.5 14.0 18.0 252 Compar. #1 0.0 237.5 28.0 >32 >32 EXAMPLE 3 Sample 9 was prepared by blending Silicone Composition A with a polydimethylsiloxane having a viscosity of 1000 mm 2 /s and a hydroxy end-blocked polydimethylsiloxane having a viscosity of 70 mm 2 /s at a weight ratio of 1.2:1.2:1.0, respectively. This silicone mixture was then blended with Mineral Oil A. Sample 10 which is a comparative sample was prepared according to Sample 9, except that Mineral Oil B replaced Mineral Oil A. Both were allowed to stand for 48 hours at room temperature and their appearance evaluated. Sample 9 remained a one phase material with no significant separation of the components. Sample 10 had separated into two distinct phases in roughly the same volume proportions as the original amounts of silicone and mineral oil that were mixed.

Claims: A dispersible silicone composition comprising a blend of: (I) a silicone composition obtainable by reacting at a temperature of 50 to 300°C a mixture comprising: (i) 100 parts by weight of at least one polyorganosiloxane selected from (A) a polyorganosiloxane having a viscosity of 20 to 100,000 mm 2 /s at 25°C and being expressed by the general formula R 1 a SiO (4-a)/2 in which R 1 is a monovalent hydrocarbon or halogenated hydrocarbon group having 1 to 10 carbon atoms and a has an average value of 1.9 to 2.2, (B) a polyorganosiloxane having a viscosity of 200 to 100 million mm 2 /s at 25°C and being expressed by the general formula R 2 b (R 3 O) c SiO (4-b-c)/2 in which R 2 is a monovalent hydrocarbon or halogenated hydrocarbon group having 1 to 10 carbon atoms, R 3 is hydrogen atom or a monovalent hydrocarbon group having 1 to 10 carbon atoms, b has an average value of 1.9 to 2.2 and c has a sufficiently large value to give at least one -OR 3 group in each molecule, at least one such -OR 3 group being present at the end of the molecular chain, or (C) a mixture of (A) and (B), (ii) 0.5 to 20 parts by weight of at least one silicon compound selected from (a) an organosilicon compound of the general formula R 4 d SiX 4-d in which R 4 is a monovalent hydrocarbon group having 1 to 5 carbon atoms, X is selected from halogen atom or a hydrolyzable group and d has an average value of one or less, (b) a partially hydrolyzed condensate of said compound (a), (c) a siloxane resin comprising (CH 3 ) 3 SiO 1/2 units and SiO 4/2 units wherein the molar ratio of (CH 3 ) 3 SiO 1/2 units to SiO 4/2 units is 0.4:1 to 1.2:1, or (d) a condensate of compound (c) with compound (a) or (b), and (iii) a catalytic amount of a compound for promoting the reaction of components (i) and (ii), and (II) mineral oil having a viscosity of 5-20 mPa·s at 25°C. A composition according to claim 1 wherein the composition comprises as component (III) a filler. A composition according to claim 1 wherein polyorganosiloxane (A) is a trimethylsiloxy-terminated polydimethylsiloxane having a viscosity of 350 to 15,000 mm 2 /s at 25°C. A composition according to claim 1 wherein polyorganosiloxane (B) is a hydroxyl-terminated polydimethylsiloxane having a viscosity of 1,000 to 50,000 mm 2 /s at 25°C. A composition according to claim 1 wherein silicon compound (ii) is selected from ethyl polysilicate or a siloxane resin copolymer comprising (CH 3 ) 3 SiO 1/2 units and SiO 2 units in a molar ratio of approximately 0.4:1 to 1.2:1, respectively. A composition according to claim 1 wherein the catalyst (iii) is selected from alkali metal hydroxides, alkali metal silanolates, alkali metal alkoxides, quaternary ammonium hydroxides, quaternary ammonium silanolates, quaternary phosphonium hydroxides, quaternary phosphonium silanolates, ammonium carbonate or metal salts of organic acids. A composition according to any of claims 2-5 wherein the filler is a hydrophobic silica having a surface area of 50 to 300 m 2 /g in an amount of up to 30 parts by weights. A composition according to claim 1 wherein the mixture of (I) further comprises up to 20 parts by weight of (iv) a polyorganosiloxane having a viscosity of 10 to 100 mm 2 /s at 25°C and being expressed by the general formula R 6 e (R 9 O) f SiO (4-e-f)/2 in which R 6 is a monovalent hydrocarbon or halogenated hydrocarbon group having 1 to 10 carbon atoms, R 9 is hydrogen atom or a monovalent hydrocarbon group having 1 to 10 carbon atoms, e is from 1.9 to 2.2 and f has a sufficient value to give at least two -OR 9 groups in each molecule at the end of the molecular chain. A composition according to claim 8 wherein polyorganosiloxane (iv) is a hydroxyl-terminated polydimethylsiloxane having a viscosity of 10 to 100 mm 2 /s at 25°C. A composition according to claim 1 wherein the mineral oil (II) is a white mineral oil. A composition according to claim 1 wherein the composition further comprises (IV) a saturated or unsaturated bisamide. A method for controlling foam in a foam producing system comprising adding to said system the composition of any of claims 1-11.

Inventors: FEY KENNETH CHRISTOPHER, HABERMEHL JAMES, FEY, KENNETH CHRISTOPHER, HABERMEHL, JAMES
Applicants: DOW CORNING, DOW CORNING CORPORATION
Application year: 1997
Main classification: C08L83
IPC codes: C08K5, C08L83, C11D3, B01D19