HYDROXY-FUNCTIONALIZED POLYESTER AND POLY(ESTER ETHER) OLIGOMERS

Abstract: Hydroxy-functional polyester oligomers are prepared by contacting a hydroxy-functional aliphatic dicarboxylic acid or a mixture of dicarboxylic acids containing hydroxy-functional aliphatic diacids, with a diglycidyl ether or diglycidyl ester in the presence of an onium catalyst in an ether solvent under conditions suitable for forming the oligomer. The oligomers can be used as hot-melt adhesives, adhesive tackifiers, plasticizers, heat-curable adhesives and heat-curable coatings. Some of these materials are biodegradable and are therefore suitable for application to compostable end products.

Description: HYDROXY-FUNCTIONALIZED POLYESTER AND POLY(ESTER ETHER) OLIGOMERS This invention relates to polyester oligomers and the processes for preparing the same. Oligomers are combinations of monomers giving chains of less than 15,000 M n and a M w /M n ranging from 1 to 100 as determined by size exclusion chromatography using polystyrene calibration standards. They are utilized as they are, or as an intermediate product by introducing various functional groups to activate them, for example, as surfactants, paints, adhesives, sealants, or printing inks. As for polyester oligomers, it has already been known that the properties thereof when used as coated films, such as adhesiveness, strength, oil and solvent resistance, can be improved by introducing silicon radicals capable of being hydrolyzed into Si-O-C bond in the alkyd resin to be modified, as described in U.S. Patent 4,191 ,714. The present invention provides polyester oligomers which do not require the introduction of silicon radicals or other functional groups into their molecules to improve such properties. In one aspect, the present invention is a hydroxy-functional polyester oligomer comprising moieties derived from hydroxy-functional aliphatic diacids and diglycidyl ethers or diglycidyl esters. In another aspect, this invention is a process for preparing a hydroxy- functional polyester oligomer which comprises contacting a hydroxy-functional aliphatic dicarboxylic acid or a mixture of dicarboxylic acids containing hydroxy-functional aliphatic diacids, with a diglycidyl ether or diglycidyl ester in the presence of an onium catalyst in an ether solvent under conditions suitable for forming the oligomer. The poly(hydroxy ester) and poly(hydroxy ester ether) oligomers of the present invention can be used as hot-melt adhesives, adhesive tackifiers, plasticizers, heat- curable adhesives and heat-curable coatings. Some of these materials are biodegradable and are therefore suitable for application to compostable end products. Definitions The following terms are used in this application and have the meanings and preferred embodiments set out hereinafter unless otherwise specified. The term "hydrocarbylene" means a divalent aliphatic hydrocarbon moiety such as alkylene, alkenylene or cycloalkylene having from 2 to 20 carbons and optionally containing a heteroatomic group, such as oxygen, sulfur, imino, or sulfonyl. As used herein, the term "aromatic moiety" means any group having one or more aromatic rings and from 5 to 25 carbon atoms. The aromatic rings may have one or more non-carbon atoms in the ring such as, for example, sulfur, nitrogen and oxygen, or one or more substituent groups bonded to the aromatic ring. These substituent groups may be alkyl, cycloalkyl, aryl, alkoxy, aryloxy, amido, halo, nitro, or cyano groups, carboxyl, carbonyl or sulfoxyl, in the chain or substituent thereto. The term "diglycidyl ether" means a compound generally represented by the formula: wherein R 2 is an aromatic moiety or a hydrocarbylene. The term "diglycidyl ester" means a compound generally represented by the formula: The polyester or poly(ester ether) oligomer of the present invention has repeating units represented by the formula: A-{O 2 C— R— CO 2 - R 3 -O— R 4 -O— R 3 — )-B wherein z has a value of 10 or less; R is a divalent organic moiety which is primarily hydrocarbon; R 3 is: and R 4 is: wherein R 2 and R 6 are independently divalent organic moieties which are primarily hydrocarbon; R 5 is hydrogen or alkyl; n is from 0 to 100; A is independently hydrogen, wherein R 7 is a monovalent organic moiety which is primarily hydrocarbon; R 3 , R 4 and R 5 are as previously defined; and B is independently: wherein R 3 , R 4 , R 5 and R 7 are as previously defined. In the preferred polymers, R 1 , R 2 and R 6 are independently alkylene, cycloalkylene, alkylenearylene, alkyleneoxyalkylene, poly(alkyleneoxyalkylene), alkyleneamidealkylene, poly(alkyleneamidealkylene), alkylenethioalkylene, poly(alkylenethioalkylene), alkylenesulfonylalkylene, poly(alkylenesulfonylalkylene), arylene, dialkylenearylene, diaryleneketone, diarylenesulfone, diarylene oxide, alkylidene-diarylene, diarylene sulfide, or a combination of these moieties, optionally substituted with at least one hydroxyl group. In the more preferred polymers, R 1 is ethylene, propylene, butylene, pentamethylene, hexamethylene, heptamethylene, octamethylene, nonamethylene, decamethylene, dodecamethylene, 1 ,4-cyclohexylene, 1 ,3-cyclohexylene or 1 ,2-cyclohexylene, optionally substituted with at least one hydroxyl group; R 2 and R 6 are independently methylene, ethylene, propylene, butylene, pentamethylene, hexamethylene, heptamethylene, octamethylene, nonamethylene, decamethylene, dodecamethylene, 1 ,4-cyclohexylene, 1 ,3-cyclohexylene or 1 ,2-cyclohexylene, optionally substituted with at least one hydroxyl group. More preferably, R 1 and R 6 are represented by the formula: — H 2 C-(- HC— H 2 C— O-) HC— H 2 C— O— CH 2 -CH-( O— CH 2 -CH-) CH 2 — ' o ' 8 1 8 ' 8 y R 8 R R R ; and R 2 is represented by the formula: wherein R 8 is independently hydrogen or methyl and x and y are independently 0 to100. In the most preferred polymers, R 1 and R 6 are independently m-phenylene, p- phenylene or 2,6-naphthalene; R 2 is independently m-phenylene, p-phenylene, naphthylene, diphenylene-isopropylidene, sulfonyldiphenylene, carbonyldiphenylene, oxydiphenylene or 9,9-fluorenediphenylene; R 5 is hydrogen; R 7 is independently phenyl, methyl, or: CH 3 ( CH 2 )^ wherein m is 1 to 30; A is hydrogen or: and B is wherein R 3 , R 4 and R 5 are as previously defined. Generally, the oligomers of the present invention can be prepared by reacting dicarboxylic acids and diglycidyl ethers or diglycidyl esters at conditions sufficient to yield hydroxy ester ether or hydroxy ester linkages. The conditions at which the polymerization reaction is most advantageously conducted are dependent on a variety of factors, including the specific reactants, solvent, and catalyst employed, if any. In general, the reaction is conducted under a non-oxidizing atmosphere such as a blanket of nitrogen or other inert gases. The reaction can be conducted neat (without solvent or other diluents). However, in order to ensure homogeneous reaction mixtures and to moderate exothermic reactions at such temperatures, it is often desirable to use inert organic solvents, such as those mentioned previously, for the reactants. The time and temperature most advantageously employed will vary depending on the specific monomers employed, particularly their reactivity, the specific oligomer, and the organic liquid. In general, the reaction temperature to form the oligomers is from 80°C to 300°C and, most preferably, from 100°C to 180°C, and for a time of from 5 minutes to 24 hours, more preferably from 15 minutes to 8 hours and, most preferably, from 30 minutes to 4 hours. The concentrations at which the monomers are most advantageously employed in the organic liquid reaction medium are dependent on a variety of factors including the specific monomers and organic liquid employed and the polymer being prepared. In general, the monomers are employed in an acid to epoxy stoichiometric ratio of from 0.5:1 to 2:1 preferably at a 0.8:1 to 1.2:1 ratio. If desired, oligomers prepared with an excess of bis epoxide may be further reacted with monofunctional carboxylic acids. Optionally, the bis epoxide can be concurrently reacted with di- and monofunctional carboxylic acids. Any inert organic solvent which can dissolve the monomers to the appropriate degree and can be heated to the appropriate polymerization temperature either at atmospheric, subatmospheric or superatmospheric pressure could be used. Examples of suitable solvents include pyridine, triethylamine or mixtures thereof; N-methylpyrrolidinone (NMP), methyl benzoate, ethyl benzoate, butyl benzoate; cyclopentanone, cyclohexanone, cycloheptanone, cyclooctanone, cyclohexylpyrrolidinone; and ethers or hydroxy ethers such as diglyme, triglyme, diethylene glycol ethyl ether, diethylene glycol methyl ether, dipropylene glycol methyl ether, dipropylene glycol dimethyl ether, propylene glycol phenyl ether, propylene glycol methyl ether and tripropylene glycol methyl ether; toluene, mesitylene, xylene, benzene, dipropylene glycol monomethyl ether acetate, halogenated solvents such as dichlorobenzene, propylene carbonate, naphthalene, diphenyl ether, butyrolactone, dimethylacetamide, dimethylformamide and mixtures thereof. The preferred solvents are NMP, butyrolactone and diphenylether. During monomer synthesis, the monomers are recovered from the reaction mixture by conventional methods. For example, the reaction mixture containing the monomer as a precipitate can be filtered to remove the solid monomer. The solid monomer can then be rinsed with water, methanol, and ether or other solvents which are non-solvents for the monomer, but good solvents for the impurities. The molecular weight of the oligomer of the present invention may be between 600 and 20,000, but it is preferably between 1 ,000 and 10,000 and, still more preferably between 1 ,500 and 6,000. Mixtures of oligomers having molecular weights within these ranges may also be used, for example, a mixture of an oligomer having a molecular weight of 3,000 with one having a molecular weight of 20,000 or a mixture of an oligomer having a molecular weight of 6,000 with one having a molecular weight of 15,000. The oligomer can be directly cast as a film, applied as a coating, or poured into a non-solvent to precipitate the oligomer. Water, methanol, acetone and other similar polar liquids are typical non-solvents which can be used to precipitate the oligomer. If the oligomer is obtained in solid form, it may be further processed using conventional compression molding techniques or melt-spinning, casting or extrusion techniques provided the solid precursor has a sufficiently low glass transition temperature. More commonly, the oligomer is processed directly from the organic liquid reaction solution and the advantages of the present invention are more fully realized in that instance. Since the oligomer is soluble in the organic liquid reaction medium, the organic solution of the precursor can be cast or applied and the solvent evaporated. Upon evaporation of the solvent, a solid material results. In addition, the oligomer of the present invention may also be employed to make shaped articles, films, fibers, or foams. In general, techniques well-known in the art for casting oligomers or polymers from solution may be employed in the preparation of such products. In preparing the shaped oligomer articles of the present invention, a polysaccharide, a modified polysaccharide or a naturally-occurring fiber or particulate filler may be added to the oligomer. The method of incorporating the polysaccharide, modified polysaccharide or naturally-occurring fiber or particulate filler is not critical and they can conveniently be added to the oligomer solution prior to preparing the shaped article. The liquid compositions containing the oligomer alone or also containing fillers, may be applied by any of the usual techniques (doctoring, rolling, dipping, brushing, spraying, extrusion coating or meniscus coating) to a number of different substrates. If the oligomer is prepared in solid form, the additives can be added to the melt prior to processing into a shaped article. Polysaccharides which can be employed in the practice of the present invention for preparing the composition are the different starches, celluloses, hemicelluloses, xylanes, gums, pectins and pullulans. Polysaccharides are known and are described, for example, in Encyclopedia of Polymer Science and Technology. 2nd edition, 1987. The preferred polysaccharides are starch and cellulose. The term "starch" as used herein, refers to carbohydrates of natural, vegetable origin, composed mainly of amylose and/or amylopectin, and includes unmodified starches, physically modified starches, such as thermoplastic, gelatinized or cooked starches, starches with a modified acid value (pH) where acid has been added to lower the acid value of a starch to a range of from 3 to 6, gelatinized starches, ungelatinized starches, cross-linked starches and disrupted starches (starches which are not in particulate form). The starches can be in granular, particulate or powder form. They can be extracted from various plants, such as, for example, potatoes, rice, tapioca, corn, pea, and cereals such as rye, oats, and wheat. Celluloses are known and are described, for example, in Encyclopedia of Polymer Science and Technology. 2nd edition, 1987. Celluloses are natural carbohydrate high polymers (polysaccharides) consisting of anhydroglucose units joined by an oxygen linkage to form long molecular chains that are essentially linear. Cellulose can be hydrolyzed to form glucose. The degree of polymerization ranges from 1000 for wood pulp to 3500 for cotton fiber, giving a molecular weight of from 160,000 to 560,000. Cellulose can be extracted from vegetable tissues (wood, grass, and cotton). Celluloses can be used in the form of fibers. Modified polysaccharides which can be employed in the practice of the present invention for preparing the composition are the esters and ethers of polysaccharides, such as, for example, cellulose ethers and cellulose esters, or starch esters and starch ethers. Modified polysaccharides are known and are described, for example, in Encyclopedia of Polymer Science and Technology. 2 nd edition, 1987. Various additives such as, for example, plasticizers, lubricants, pigments, foaming agents, extenders, stabilizers, chemical modifiers, and flow accelerators may also be added to the oligomers of the present invention. Each of these additives is known and several types of each are commercially available. While the amount of oligomers used depends on a variety of factors, including the specific oligomer employed and the desired end uses of the composition, in general, the oligomers can be present in an amount of from 1 to 99 weight percent, preferably from 10 to 95 weight percent and, most preferably from 20 to 90 weight percent, based on the total weight of the oligomer and polysaccharide, modified polysaccharide or naturally-occurring fiber or particulate filler. In general, compositions containing the oligomers of the present invention can be prepared by mixing (1 ) the oligomers with (2) a polysaccharide, a modified polysaccharide or a naturally-occurring fiber or particulate filler and, optionally (3) other additives in an intensive mixer, such as a Haake mixer, a Banbury mixer, single-screw extruder, twin-screw extruder, or an injection-molding machine, at a temperature and for a time sufficient to provide an intimate, well-dispersed mixture of the components. Preferably, the components are brought together and processed in an appropriate melt extruder from which the blend is extruded in the form of powder or strands. The powders or strands are then pelletized or formed into granules for injection molding and other thermal processes. Standard techniques and apparatuses well known in the art can be used for these processes. The oligomer of the present invention can be applied to various substrates by a number of methods such as dip coating, roll coating, brushing (for example as a varnish), spray coating, powder coating, dispersion-spraying, solution-casting, slurry-spraying, dry- powder-spraying, and fluidized bed techniques. When applying the oligomer of the invention from solution, specific conditions of polymerization and other processing parameters most advantageously employed are dependent on a variety of factors, particularly the specific oligomer or polymer being deposited, the conditions of coating, the coating quality and thickness, and the end-use application, with the solvent being selected accordingly. Representative solvents which can be employed are those described previously. Substrate(s) which can be coated with the oligomer or polymer of the invention can be any material which has sufficient integrity to be coated with the oligomer. Representative examples of substrates include paper, paper board, and cloth. The substrates which are employed are selected based on the desired application. The substrate may be of any shape, and the shape is dependent on the end- use application. For instance, the substrate may be in the form of a food container. In the case of hollow objects, the polymer layer(s) is on either or both the inside or outside of the substrate. The following examples are for illustrative purposes only and are not intended to limit the scope of this invention. Unless otherwise indicated, all parts and percentages are by weight. Example 1 A mechanically-stirred mixture of bisphenol A-diglycidyl ether (BADGE; epoxy equivalent weight or eew = 179.99; 372.7 g), adipic acid (57.3 g), ethyltriphenyl phosphonium acetate - acetic acid complex (ETPA, 70 percent in methanol; 0.9 g), xylene (56.0 g) and cyclohexanone (84.0 g) under a nitrogen purge is heated to 140°C over a period of 45 minutes. After an initial exotherm to 175°C, additional adipic acid (90 g), ETPA (0.6 g), xylene (56.0 g) and cyclohexanone (84.0 g) were added and the temperature decreased to 140°C, after which a second exotherm increased the reaction temperature to 160°C. The mixture then s allowed to air cool to 150°C, and stirring was maintained at that temperature for 75 minutes. After cooling to room temperature, the resulting solution was cast onto a sheet of tin-free steel and baked for 10 minutes at 200°C to give a coating (about 0.2 mil) which showed no cracking (0 mm) in a wedge-bend test, was unaffected by over 50 methyl ethyl ketone (MEK) double rubs and did not delaminate under pasteurization conditions (121°C), indicating that the coating had excellent chemical and moisture resistance along with good flexibility. Prior to casting and baking, the oligomeric poly(hydroxy ester ether) formed during the reaction had an eew of 1335 and an acid number of 67.15. Example 2 A stirred mixture of BADGE (eew = 179.99; 372.7 g), adipic acid (147.3 g), ETPA (0.914 g), xylene (56 g) and cyclohexanone was heated under nitrogen to 140°C, after which the temperature increased exothermically to 175°C. Additional ETPA (0.6 g), xylene (56 g) and cyclohexanone (84 g) were added, the temperature was allowed to cool to 150°C, and stirring at that temperature was continued for 50 minutes. The resulting solution was cast to give coatings with properties like those described for the coating of Example 1. Prior to casting and baking, the oligomeric poly(hydroxy ester ether) formed during the reaction had an eew of 2342 and an acid number of 28.51. Example 3 A stirred mixture of BADGE (eew = 179.99; 344.0 g), adipic acid (56.0 g), ETPA (0.844 g) and methyl isobutyl ketone (MIBK; 80 g) under nitrogen was heated to 140°C, after which the temperature of the reaction rises exothermically to 166°C. Adipic acid (80 g) and ETPA (0.6 g) were added and the temperature decreased to about 140°C prior to a second exotherm that raises the reaction temperature to 163°C. Additional MIBK (80 g) was added and stirring at about 140°C was continued for 45 minutes. Acetic acid (36 percent in water; 25.5 g) then was added and the resulting mixture was stirred at 120°C for 30 minutes, and the solution was diluted with Dowanol * PM (160 g) and was allowed to cool to room temperature. Coatings, cast from the resulting solution, have properties like those of the coatings of Examples 1 and 2; prior to casting and baking, the oligomeric poly(hydroxy ester ether) formed during the reaction had an eew of 1684 and an acid number of 59.28. Example 4 A mechanically-stirred mixture of BADGE (eew = 172; 300 g), malic acid (117 g), acetic acid (99.9 percent, 15 g) and tetrabutylammonium bromide (TBAB; 28 g) was heated under nitrogen and over a period of 45 minutes to 140°C, after which the reaction temperature rose exothermically to about 160°C when forced air cooling was applied to control the exotherm. The mixture then was allowed to cool to 155°C and maintained while stirring at that temperature for 4 hours. The resulting oligomeric poly(hydroxy ester ether) had an acid number of 75, an eew of 39,402 and M n (GPC) of 1511. Example 5 A stirred mixture of BADGE (eew = 172; 300 g), benzoic acid (40 g) and TBAB (22.5 g) was heated under nitrogen to 150°C and maintained at that temperature for one hour. Adipic acid (127.5 g) then was added and the resulting exothermic temperature rose to about 165°C, was controlled by forced-air cooling, after which the reaction mixture was stirred at 150°C for 4 hours. The oligomeric poly(hydroxy ester ether) thus formed had an acid number of 56, an eew of 119,444 and M n (GPC) = 1797.

Claims: CLAIMS: 1. A polyester or poly(ester ether) oligomer having repeating units represented by the formula: A-(O 2 C— R^-CO^R^O— R 4 -O-R 3 )-B wherein z has a value of 10 or less, R 1 is a divalent organic moiety which is primarily hydrocarbon; R 3 is: and R 4 is: — wherein R 2 and R 6 are independently divalent organic moieties which are primarily hydrocarbon and R 5 is hydrogen or alkyl and n is from 0 to 100; A is independently hydrogen or: R 7 — CO 2 -R 3 -O— R— O— R— or CH 2 -C— CH 2 -O— R 4 -O— R 3 — R 5 wherein R 7 is a monovalent organic moiety which is primarily hydrocarbon and R 3 , R 4 and R 5 are as previously defined; and B is independently: wherein R 3 , R 4 , R 5 and R 7 are as previously defined. 2. The oligomer of Claim 1 wherein R is independently alkylene, cycloalkylene, alkylenearylene, alkyleneoxyalkylene, poly(alkyleneoxyalkylene), alkyleneamidealkylene, poly(alkyleneamidealkylene), alkylenethioalkylene, poly(alkylenethioalkylene), alkylenesulfonylalkylene, poly(alkylenesulfonylalkylene), arylene, dialkylenearylene, diaryleneketone, diarylenesulfone, diarylene oxide, alkylidene-diarylene, diarylene sulfide, or a combination of these moieties, and optionally substituted with at least one hydroxyl group. 3. The oligomer of Claim 2 wherein R 1 is independently methylene, ethylene, propylene, butylene, pentamethylene, hexamethylene, heptamethylene, octamethylene, nonamethylene, decamethylene, dodecamethylene, 1 ,4-cyclohexylene, 1 ,3-cyclohexylene or 1 ,2-cyclohexylene, optionally substituted with at least one hydroxyl group. 4. The oligomer of Claim 2 wherein R 1 is represented by the formula: wherein R 8 is independently hydrogen or methyl and x and y are independently 0 to 100. 5. The oligomer of Claim 2 wherein R 1 is independently m-phenylene, p- phenylene or 2,6-naphthalene. 6. The oligomer of Claim 1 wherein R 2 is independently, alkylene, cycloalkylene, alkylenearylene, alkyleneoxyalkylene, poly(alkyleneoxyalkylene), alkyleneamidealkylene, poly(alkyleneamidealkylene), alkylenethioalkylene, poly(alkylenethioalkylene), alkylenesulfonylalkylene, poly(alkylenesulfonylalkylene), arylene, dialkylenearylene, diaryleneketone, diarylenesulfone, diarylene oxide, alkylidene-diarylene, diarylene sulfide, or a combination of these moieties, and optionally substituted with at least one hydroxyl group. 7. The oligomer of Claim 6 wherein R 2 is independently ethylene, propylene, butylene, pentamethylene, hexamethylene, heptamethylene, octamethylene, nonamethylene, decamethylene, dodecamethylene, 1 ,4-cyclohexylene, 1 ,3-cyclohexylene or 1 ,2-cyclohexylene, optionally substituted with at least one hydroxyl group. 8. The oligomer of Claim 6 wherein R 2 is represented by the formula: wherein R 8 is independently hydrogen or methyl and x and y are independently 0 to 100 and n is 0. 9. The oligomer of Claim 6 wherein R 2 is m-phenylene, p-phenylene, naphthylene, diphenylene-isopropylidene, sulfonyldiphenylene, carbonyldiphenylene, oxydiphenylene or 9,9-fluorenediphenylene. 10. The oligomer of Claim 1 wherein R 6 is independently, and optionally substituted with at least one hydroxyl group, alkylene, cycloalkylene, alkylenearylene, alkyleneoxyalkylene, poly(alkyleneoxyalkylene), alkyleneamidealkylene, poly(alkyleneamidealkylene), alkylenethioalkylene, poly(alkylenethioalkylene), alkylenesulfonylalkylene, poly(alkylenesulfonylalkylene), arylene, dialkylenearylene, diaryleneketone, diarylenesulfone, diarylene oxide, alkylidene-diarylene, diarylene sulfide, or a combination of these moieties. 11. The oligomer of Claim 10 wherein R 6 is independently ethylene, propylene, butylene, pentamethylene, hexamethylene, heptamethylene, octamethylene, nonamethylene, decamethylene, dodecamethylene, 1 ,4-cyclohexylene, 1 ,3-cyclohexylene or 1 ,2-cyclohexylene, optionally substituted with at least one hydroxyl group. 12. The oligomer of Claim 10 wherein R 6 is represented by the formula: wherein R 8 is independently hydrogen or methyl and x and y are independently 0 to 100. 13. The oligomer of Claim 10 wherein R 6 is independently m-phenylene, p-phenylene or 2,6-napthalene. 14. The oligomer of Claim 1 wherein R 7 is independently phenyl, methyl, or: CH 3 ( CH 2 )— wherein m is 1 to 30. 15. The oligomer of Claim 1 wherein R 5 is hydrogen. 16. The oligomer of Claim 1 wherein n is 0-10. 17. The oligomer of Claim 1 in which A is hydrogen or: and in which B is C / H 0 2 -C— CH 2 -O- R 4 -O— R 3 - L R 5 wherein R 3 , R 4 and R 5 are as previously defined. 18. The oligomer of Claim 17 in the form of a thermosetting resin which upon heating yields a cross-linked product. 19. The oligomer of Claim 1 formed by the reaction of bisphenol A-diglycidyl ether with adipic acid, malic acid, tartaric acid, terephthalic acid, isophthalic acid or a dimerized fatty acid. 20. The oligomer of Claim 1 in the form of an adhesive, a tackifier, a coating, a plasticizer or a thermoplastic flow modifier. 21. A composition of matter comprising the oligomer of Claim 1 and a polysaccharide, a modified polysaccharide, or a naturally-occurring fiber or particulate filler. 22. The composition of Claim 21 , wherein the polysaccharide is a starch or a cellulose. 23. The composition of Claim 22, wherein the starch is derived from potato, rice, corn or wheat. 24. The composition of Claim 22, wherein the starch is a granular starch or a thermoplastic starch, and the cellulose is in the form of a fiber. 25. The composition of Claim 22, wherein the cellulose is extracted from wood pulp or cotton fibers. 26. The composition of Claim 21 , wherein the modified polysaccharide is an ether or an ester of the polysaccharide. 27. The composition of Claim 21 , wherein the naturally-occurring fiber or particulate filler is wood flour, wood pulp, wood fibers, cotton, flax, hemp, or ramie fibers, rice or wheat straw, chitin, chitosan, cellulose materials derived from agricultural products, nut shell flour, corn cob flour, or mixtures thereof. 28. The composition of Claim 21 , wherein the oligomer is present in an amount of from 1 to 99 weight percent, and the polysaccharide, modified polysaccharide, or naturally-occurring fiber or particulate filler is present in an amount of from 99 to 1 weight percent, based on the weight of the two components. 29. The composition of Claim 21 , in the form of a film, a molded or extruded article, an open-cell or closed-cell foam, a rigid or flexible container, a packaging material, or a laminate. 30. The composition of Claim 21 , in the form of an encapsulant capable of slow or controlled release of a pharmacologically active agent, a catalyst, a biocide or a fertilizer. 31. An article comprising a substrate of a polysaccharide coated with the oligomer of Claim 1. 32. A laminate comprising the oligomer of Claim 1 bonded to a substrate comprising, paper, cardboard, cellulose film, modified cellulose film, starch film, modified starch film, or wood. 33. A process for preparing the composition of Claim 21 which comprises mixing the oligomer with the polysaccharide, modified polysaccharide, or naturally-occurring fiber or particulate filler in an intensive mixer at a temperature and for a time sufficient to provide a well-dispersed mixture of the components.

Inventors: BECKERDITE JOHN M, MANG MICHAEL N, WANG DAVID S, WHITE JERRY E, BECKERDITE, JOHN, M., MANG, MICHAEL, N., WANG, DAVID, S., WHITE, JERRY, E.
Applicants: BECKERDITE JOHN M, DOW CHEMICAL CO, MANG MICHAEL N, WANG DAVID S, WHITE JERRY E, BECKERDITE, JOHN, M., MANG, MICHAEL, N., THE DOW CHEMICAL COMPANY, WANG, DAVID, S., WHITE, JERRY, E.
Application year: 1997
Main classification: C08G63
IPC codes: C08G59, C08G63, C08L1, C08L3, C08L5, C08L67