A PROCESS FOR THE ADDITION OF BORON IN A TiO2 MANUFACTURING PROCESS

Abstract: The present invention provides a process for producing titanium dioxide (TiO2) pigment comprising boron oxide (B2O3), comprising the steps of: (a) reacting titanium tetrachloride (TiCl4) in the vapor phase with an aluminum compound and an oxygen-containing gas in a reactor at a temperature in the range of about 900 DEG C to about 1600 DEG C to provide a gaseous suspension comprising TiO2 particles, and (b) contacting the gaseous suspension comprising the TiO2 particles with a boron compound to produce TiO2 pigment comprising B2O3.

Description: TITLE A PROCESS FOR THE ADDITION OF BORON IN A Ti0 2 MANUFACTURING PROCESS BACKGROUND OF THE INVENTION Field of the Invention The present invention relates to a process for the production of titanium dioxide (Ti0 2 ) pigment comprising boron oxide (B 2 0 3 ) , wherein a boron compound is added and more particularly wherein the boron compound is added to the process downstream of where an oxygen-containing gas and titanium tetrachloride (TiCl 4 ) are initially contacted. Description of the Related Art The process for producing Ti0 2 pigment by reacting an oxygen-containing gas and TiCl 4 at temperatures ranging from 900°C to 1600°C in the vapor phase is known. The resulting hot gaseous suspension of Ti0 2 particles and free chlorine are discharged from the reactor and must be quickly cooled below 600°C within about 5 to 100 milliseconds. This cooling is accomplished in a conduit, i.e., a flue, so that undesired Ti0 2 particle size growth is prevented and particle agglomeration is minimized. Particle size and particle agglomeration are important Ti0 2 properties. The particle size of the Ti0 2 pigment is measured in terms of carbon black undertone (CBU) . Pigments containing smaller- sized particles have a relatively high CBU, and finished products (e.g., paints, plastics, etc.) containing such pigments tend to have a bluish tint. Pigments with larger-sized particles have a relatively low CBU and finished products containing such pigments tend to have a more yellowish tint. The particle agglomeration of the pigment is typically measured in terms of its particle size distribution (coarse fraction) . Pigments, wherein a low weight percentage of the particles (e.g., less than 30% as measured by a Sedigraph® instrument) have a particle diameter size greater than 0.6 microns, tend to have low particle agglomeration and finished products made with such pigments tend to have high gloss. Pigments, wherein a high weight percentage of the particles have a particle size diameter greater than 0.6 microns, tend to have greater particle agglomeration and finished products made with such pigments tend to have lower gloss. If extensive agglomeration of Ti0 2 results, the Ti0 2 must be milled or ground in an energy intensive, expensive process such as fluid-energy milling to reduce the size of agglomerates in order to achieve the desired pigment properties. Particle agglomeration can limit product quality and/or rate of throughput . In the chloride vapor phase process for producing Ti0 2 , two crystal structures of Ti0 2 may form: rutile and anatase. Rutile Ti0 2 is preferred for its higher durability and its higher refractive index, both of which are important performance characteristics. Anatase Ti0 2 is more photoactive than rutile Ti0 2 and possesses a lower refractive index. The presence of the anatase phase will in particular adversely affect durability. Even low levels of anatase affect the durability of a finished Ti0 2 pigment. In paper and other applications such as delustering of textiles, where abrasion is an important consideration, anatase Ti0 2 pigments are preferred due to their lower abrasion properties. Rutile Ti0 2 pigments tend to cause excessive wear of spinnerets, thread guides and needles used in high-speed spinning and fabricating processes. One possible explanation for the high abrasion properties of rutile Ti0 2 pigments is the multiple facets of the pigment particles. Particle size has been controlled previously, for example, by pre-mixing volatile silicon compounds and TiCl 4 prior to reacting it with the oxygen-containing gas. However, such processes have a tendency to form some anatase Ti0 2 pigment. Gonzalez, U.S. Patent 5,562,764 discloses an improvement in these processes by adding the volatile silicon compound downstream of where the oxygen-containing gas and TiCl 4 are initially contacted to produce a substantially anatase-free Ti0 2 pigment. However, the process in Gonzalez, U.S. Patent 5,562,764 does not provide many of the advantages recognized by the process of the present invention as described in greater detail below. Werner, U.S. Patent 2,512,079 describes treatment of Ti0 2 pigment product with boric acid to reduce the acidity of the Ti0 2 and to impart fineness and softness. An oxygen compound of boron is added to the Ti0 2 to remove chlorine-containing compounds from the Ti0 product's surface. In this process, the boron is added to the Ti0 2 product after the product has been separated from the gas and collected as a solid product. Wilson et al., U.S. Patent 3,443,897 and Hoekje et al . , U.S. Patent 3,642,442 describe a process to prepare Ti0 2 by vapor phase oxidation of TiCl 4 wherein heat is supplied to the reaction zone by means of an electric arc or radio frequency induction heater. Nucleation agents for the Ti0 2 are generated from one or more electrodes of a plasma arc. At least one of the electrodes contains a metal which is introduced into the gas atmosphere or stream and forms a white metal oxide upon oxidation to serve as a nucleating agent. Boron is included in a list of metals which form a white oxide. Preferred metals are aluminum, silicon, zirconium and titanium. Jacobson, U.S. Patent 4,781,761 describes a wet-treatment process for coating Ti0 2 pigment particles with dense silica coatings, wherein the silica is co-deposited with B 2 0 3 . Akhtar, Pratsinis and Mastrangelo disclose in "Dopants In Vapor-Phase Synthesis of Titania Powders", J. Am. Ceram. Soc. 1992, 75(12), 3408-16, the addition of BC1 3 as a dopant in a process to prepare Ti0 2 . BC1 3 is pre-mixed with TiCl prior to introduction into a reaction vessel, wherein TiCl 4 is contacted with oxygen. The addition of BC1 3 produced primarily anatase powders and decreased the rutile phase content. As discussed above, while it is known in the art that boron compounds can be used as a nucleant for the production of Ti0 2 pigment and in the coating process of Ti0 2 pigments, there is still a need for a process to produce Ti0 2 pigment having improved quality with decreased particle size and decreased agglomeration (improved particle size control) . There is also a need to provide rutile Ti0 2 pigment which is less abrasive. However, it is also important that any additive or change to the TiCl 4 oxidation process does not cause the formation of detectable anatase nor in any other way negatively impact the durability of the Ti0 2 pigment. Further, there is a need for a process to provide pigmentary Ti0 2 which reduces or eliminates the use of scrubs in order to achieve reduced costs and complexity of the Ti0 2 manufacturing process. The present invention meets the foregoing needs. SUMMARY OF THE INVENTION The present invention provides a process for producing titanium dioxide pigment comprising B 2 0 3 , comprising the steps of: (a) reacting TiCl in the vapor phase with an aluminum compound and an oxygen-containing gas in a reactor at a temperature in the range of about 900 °C to about 1600°C to provide a gaseous suspension comprising Ti0 2 particles, and (b) contacting the gaseous suspension comprising the Ti0 2 particles with a boron compound to produce Ti0 2 pigment comprising B 2 0 3 . The resulting Ti0 2 pigment is in substantially rutile form. Preferably, the aluminum compound is an aluminum halide selected from the group consisting of A1C1 3 , AlBr 3 , A1I 3 , and mixtures thereof and more preferably, the aluminum halide is A1C1 3 . The A1C1 3 may be added in an amount sufficient to provide about 0.5 to about 10% by weight of A1 2 0 3 based total weight of Ti0 2 solids formed in the oxidation reaction. Preferably, the boron compound is a boron halide selected from the group consisting of BC1 3 , BBr 3 , BI 3 , and mixtures thereof and more preferably, the boron halide is BC1 3 . The BC1 3 may be added in an amount sufficient to provide about 500 ppm to about 5000 ppm boron based on total weight of Ti0 2 solids formed in the oxidation reaction. Preferably, the BC1 3 is added in an amount sufficient to provide about 800 ppm to about 2000 ppm boron based on total weight of Ti0 2 solids formed in the oxidation reaction. In alternative embodiments, the boron compound is boric acid. Preferably, the temperature of the gaseous suspension of Ti0 2 particles at the point where the particles are contacted with a boron compound is in the range of about 1000°C to about 1600°C and the pressure is in the range of about 40 to about 60 psig. This invention also provides a process for producing titanium dioxide pigment comprising B 2 0 3 , comprising the steps of: (a) reacting TiCl 4 in the vapor phase with an aluminum compound and an oxygen-containing gas in a reactor at a temperature in the range of about 900°C to about 1600°C to provide a gaseous suspension comprising Ti0 2 particles, and (b) passing the gaseous suspension comprising Ti0 2 particles to a cooling conduit, and (c) contacting the gaseous suspension in the cooling conduit with a boron compound to produce Ti0 2 pigment comprising B 2 0 3 . Scouring particles may be introduced into the cooling conduit but are not necessary. In the above embodiment which involves passing the gaseous suspension to a cooling conduit, the resulting Ti0 2 pigment is also in substantially rutile form. Preferably, the aluminum compound is an aluminum halide selected from the group consisting of A1C1 3 , AlBr 3 , A1I 3 , and mixtures thereof and more preferably, the aluminum halide is A1C13. Preferably, the boron compound is a boron halide which is introduced into the conduit at the point where the scouring particles are introduced into the conduit. Preferably, the boron halide is selected from the group consisting of BC1 3 , BBr 3 , BI 3 , and mixtures thereof, and the scouring particles are selected from the group consisting of calcined Ti0 2 , NaCl, KC1, sand, and mixtures thereof. In alternative embodiments, the boron compound is boric acid which may be introduced into the conduit at the point where the scouring particles are introduced into the conduit. The cooled Ti0 2 pigment comprising B 2 0 3 may be recovered and subjected to finishing and grinding steps such as being surface- treated with a coating comprising silica and fluid-energy milled. DETAILED DESCRIPTION OF THE INVENTION The present invention provides a process for producing titanium dioxide (Ti0 2 ) pigment comprising boron oxide (B 2 0 3 ) . The resulting Ti0 2 pigment is in substantially rutile form. The process of the present invention involves reacting titanium tetrachloride (TiCl 4 ) in the vapor phase with an aluminum compound and an oxygen-containing gas in a reactor at a temperature in the range of about 900°C to about 1600°C to provide a gaseous suspension comprising Ti0 2 particles, and contacting the gaseous suspension comprising Ti0 2 particles with a boron compound that will form B 2 0 3 . This process is described in greater detail below. The production of Ti0 2 pigment by the vapor phase oxidation of a titanium tetrahalide, particularly TiCl 4 , is well known and disclosed in Schaumann, U.S. Patent 2,488,439 and Krchma et al . , U.S. Patent 2,559,638, the disclosures of which are hereby incorporated by reference. In the production of Ti0 2 pigment by the vapor phase oxidation of titanium tetrahalides, titanium tetrachloride (TiCl 4 ) , titanium tetrabromide (TiBr 4 ) , and/or titanium tetraiodide (Til 4 ) may be used, but it is preferable to use TiCl 4 . First, TiCl is evaporated and preheated to temperatures of from about 300 °C to about 650 °C and introduced into a reaction zone of a reaction vessel. Aluminum compounds in amounts sufficient to provide about 0.5% to about 10% A1 2 0 3 , preferably about 0.5% to about 5%, and more preferably about 0.5% to about 2% A1 2 0 3 by weight based on total weight of Ti0 2 solids formed in the oxidation reaction are thoroughly mixed with the TiCl 4 prior to its introduction into the reaction zone of the reaction vessel. Suitable aluminum compounds include, for example, A1C1 3 , AlBr 3 and/or A1I 3 . Preferably, A1C1 3/ as disclosed in U.S. Patent 2,559,638, is used in the process of the present invention. The A1C1 3 is thoroughly mixed with TiCl prior to its introduction into the reaction zone of the reaction vessel. In alternative embodiments, the aluminum halide may be added partially or completely downstream with the boron compound. The oxygen-containing gas is preheated to at least 1200°C and is continuously introduced into the reaction zone through a separate inlet from an inlet for the TiCl 4 feed stream. By "reaction zone", it is meant the length of the reactor in which substantial reaction of the reactants takes place. The reaction of 0 2 and TiCl in the vapor phase is extremely fast and provides a hot gaseous suspension comprising Ti0 2 particles and free chlorine. This reaction step is followed by a brief period of Ti0 2 particle growth. Optionally, the oxygen-containing gas contains a nucleant. By "nucleant", it is meant any substance which can reduce the particle size of the pigment such as metals, oxides, salts or other compounds of sodium, potassium, lithium, rubidium, cesium, calcium, barium, strontium, and the like or mixtures thereof as disclosed in Lewis et al . , U.S. Patent 3,208,866 and Allen et al . , U.S. Patent 5,201,949. Particularly preferred nucleants are CsCl and KC1. The pressure for carrying out the oxidation process is preferably at least 20 psig as described in Santos, U.S. Patent 3,505,091. The hot gaseous suspension comprising the Ti0 2 particles is then rapidly cooled in order to prevent undesirable particle size growth. Cooling of the hot gaseous suspension may be performed by methods known in the art. These methods typically involve passing the hot gaseous suspension through a cooling conduit (flue) having relatively cool walls in comparison to the gaseous suspension. Granular scouring particles (scrubs) , such as calcined Ti0 2 , NaCl, KCl, sand, and mixtures thereof, may be added to the flue to reduce the formation of Ti0 2 particulate deposits on the internal walls of the flue. This cooling step is described in greater detail in Rick, U.S. Patent 2,721,626, Nerlinger, U.S. Patent 3,511,308 and Rahn et al . , U.S. Patent 3,475,258, the disclosures of which are hereby incorporated by reference. In carrying out the invention, the boron compound is added downstream from the TiCl 4 stream addition. The exact point of boron compound addition will depend on the reactor design, flow rate, temperatures, pressures and production rates. For example, the boron compound may be added at one or more points downstream from where the TiCl 4 and oxygen-containing gas are initially contacted. Specifically, the temperature of the reaction mass at the point or points of boron compound addition will range from about 500°C to about 1600°C, preferably about 1000°C to about 1600°C, at a pressure of about 5-100 psig, preferably 15-70 psig and more preferably 40-60 psig. It will be understood by those skilled in the art that the temperature profile in the reactor will guide the choice of the appropriate addition points for the boron compound. Suitable boron compounds include, for example, boron halides (e.g., BC1 3 , BBr 3 , and BI 3 , preferably BC1 3 ) , volatile boron organic compounds (e.g., trimethylborate, boron hydrides), and low melting-point boron compounds (e.g., boric acid). In general, boron compounds which can be converted into a fluid boron oxide at process temperatures are suitable. Preferably, boron chloride is used. In one embodiment, BC1 3 is added downstream in the flue where the scrubs are added to minimize the build-up of Ti0 2 in the interior of the flue as described above. In this embodiment, the BC1 3 can be added downstream alone or at the same point where the scrubs are introduced into the flue. However, it should be recognized that in the practice of the present invention, the addition of scrubs is optional. The boron compound becomes incorporated on the surface of the Ti0 2 particles as boron oxide (B 2 0 3 ) . Often, the boron compound is added in an amount sufficient to provide from about 500 ppm to about 5000 ppm boron as B, preferably from about 800 ppm to about 2000 ppm boron as B by weight based on total weight of Ti0 2 solids formed in the oxidation reaction. As a result of mixing of the reactant streams, substantially complete oxidation of TiCl 4 , A1C1 3 and BC1 3 takes place but for conversion limitations imposed by temperature and thermochemical equilibrium. Solid particles of Ti0 2 form. The reaction product containing a suspension of Ti0 2 particles in a mixture of chlorine and residual gases is carried from the reaction zone at temperatures considerably in excess of 1200°C and is subjected to fast cooling in the flue as described above or other conventional means . The Ti0 2 pigment is recovered from the cooled reaction products by conventional separation treatments, including cyclonic or electrostatic separating media, filtration through porous media or the like. The recovered Ti0 2 pigment may be subjected to surface-treatment, milling, grinding or disintegration treatment to obtain the desired level of agglomeration. For example, surface-treatment of the Ti0 2 particles may comprise treating the particles with a coating comprising silica. In general, the process of the present invention provides several advantages including the following: (1) a reduction in coarse fraction of Ti0 2 particles (weight percentage of Ti0 2 particles having a diameter size greater than 0.6 microns); (2) faster cooling rates; (3) the amount of scrubs in the flue may be reduced; and (4) Ti0 2 pigment having an undetectable amount of anatase (100% rutile within limits of detection) . The present invention is further illustrated by the following examples using the following test methods, but these examples should not be construed as limiting the scope of the invention. Test Methods Particle Size Distribution (Sedigraph® Instrument) Particle size distribution of the Ti0 2 pigment products was measured by sedimentation analysis, with a Sedigraph® (Micromeritics Instrument Corp., Norcross, GA) after dispersion in aqueous suspension by fixed level sonication. The particle size measurement of the oxidation base and the % > 0.6 microns fraction will indicate the potential for peak gloss in the finished product, a value that cannot be exceeded while applying any reasonable energy level. Particle Size Distribution (Horiba Instrument) Particle size distribution of the Ti0 2 pigment was measured using Mie scattering theory to measure "equivalent spherical diameter" as a function of percent transmittance and scattered light using a Horiba LA-900 (Horiba Instruments, Inc. Irvine, CA) after dispersion in aqueous suspension by fixed level sonication. The particle size of the Ti0 2 pigments is represented as the cumulative mass percent greater than 0.6 microns, or % > 0.6 microns . Boron Content Boron content was measured by inductively coupled plasma analysis with an Optima-3000 Penkin-Elmer, Norwalk, CT. Carbon Black Undertone The carbon black undertone (CBU) of a Ti0 2 pigment sample was measured according to the methods described in Schaumann, U.S. Patents 2,488,439 and 2,488,440, the disclosures of which are hereby incorporated by reference, using a benchmark value of 10 rather than 100 as used in the patents. The CBU was measured by mulling together a suitable liquid, such as light colored oil, the Ti0 2 pigment sample, and carbon black. The mixture was spread on a panel and the relative blueness of the gray mixture was observed. Pigments containing smaller-sized particles have a relatively high CBU and a bluer undertone. Pigments with larger-sized particles have a relatively low CBU and a more yellowish undertone. Einlehner Abrasion This method for measuring the abrasion properties of Ti0 2 pigment uses an Einlehner Abrasion Tester Model AT 1000 with a phosphorbronze test screen supplied by Hans Einlehner, Inc. EXAMPLES Comparative Example A TiCl was thoroughly premixed with sufficient A1C1 3 to provide 1% by weight A1 2 0 3 based on total solids formed in the oxidation reaction. The TiCl 4 was evaporated, preheated, and introduced into a reaction zone. Simultaneously, preheated oxygen was continuously introduced through a separate inlet to the reaction zone. Trace amounts of KC1 dissolved in water were added to the oxygen stream as disclosed in Lewis et al . , U.S. Patent 3,208,866. The reactant streams were rapidly mixed. The gaseous suspension of titanium dioxide pigment formed in the reactor was discharged to a cooling conduit (flue) and quickly cooled. NaCl scrubs were introduced into the gaseous suspension at the front end of the conduit as the suspension was discharged from the reactor as disclosed in Nerlinger, U.S. Patent 3,511,308, in an amount of about 5% based on the total solids in the conduit. A reaction temperature was measured at a point downstream of the point at which TiCl and oxygen were initially contacted. The Ti0 2 pigment was separated from the cooled gaseous products by conventional means. The properties of the resulting Ti0 2 pigment are listed below in Table 1. Example 1 The process of Comparative Example A was repeated except that BC1 3 , in the amount of 3000 ppm by weight boron as B, based on the weight of the Ti0 2 produced in the oxidation reaction, was fed to the reactor as a finely dispersed liquid at a location about 3.5 ft downstream from the point at which the TiCl 4 and oxygen were initially contacted. One further difference in this Example 1 from Comparative Example A was that no NaCl scrubs were added in Example 1 because of the pronounced cooling that occurred. At the same point as in Comparative Example A, downstream of the point at which TiCl and oxygen were initially contacted, a reaction temperature was measured. Reaction temperature in Example 1 was 188°C cooler than at the same point in the process as Comparative Example A. The properties of the resulting Ti0 2 pigment are shown below in Table 1. TABLE 1 Examples Property A 1 2 3 Coarse Fraction (a) 48.9% 27.3% 32.5% 41.6% Coarse Fraction (b) 26.4% 19.7% 22.5% 21.85% CBU 12.5 14.1 13.3 13.3 Abrasion 23 mg 15.4 mg 16.5 mg 16.4 mg *%Rutile >99.8 >99.8 >99.8 >99.8 **PPM Boron 1.5 1620 1070 1185 Coarse Fraction (a) - coarse fraction as measured by the Horiba LA-900 Coarse Fraction (b) - coarse fraction as measured by the Sedigraph.® *Rutile - The % of rutile phase was determined by x-ray diffraction. ** PPM Boron - In Comparative Example A, some boron is evident in the resulting Ti0 2 pigment due to a trace amount being present in the process. Example 2 The process of Example 1 was repeated except BC1 3 , in the amount of 2000 ppm by weight boron as B, based on the weight of the Ti0 2 solids formed in the oxidation reaction, was fed to the reactor as a finely dispersed liquid at a location about 3.5 ft. downstream from the point at which the TiCl 4 , 0 2 and A1C1 3 were initially contacted. Similarly to Example 1, no scrubs were added in this Example 2 due to the pronounced cooling which occurred. Reaction temperature in this Example 2 was 179°C cooler than at the same point in the process as Comparative A. The properties of the resulting Ti0 2 pigments are shown above in Table 1. Example 3 The process of Example 2 was repeated with BC1 3 , in the amount of 2000 ppm by weight boron as B, based on the weight of the Ti0 2 solids formed in the oxidation reaction, being fed to the reactor as a finely dispersed liquid at a location about 3.5 ft. downstream from the point at which the TiCl 4 , 0 2 and A1C1 3 were initially contacted. NaCl scrubs were introduced into the gaseous suspension at the front end of the conduit as the suspension was discharged from the reactor in an amount of about 5% based on the total solids in the conduit in a manner similar to Comparative Example A. Reaction temperature in this Example 3 was 186°C cooler than at the same point in the process as Comparative A. The properties of the resulting Ti0 2 pigments are shown above in Table 1.

Claims: CLAIMS 1. A process for producing titanium dioxide pigment comprising B 2 0 3 , comprising the steps of: (a) reacting TiCl 4 in the vapor phase with an aluminum compound and an oxygen-containing gas in a reactor at a temperature in the range of about 900°C to about 1600°C to provide a gaseous suspension comprising Ti0 2 particles, and (b) contacting the gaseous suspension comprising the Ti0 2 particles with a boron compound to produce Ti0 2 pigment comprising B 2 0 3 . 2. The process of claim 1, wherein the Ti0 2 pigment is in substantially rutile form. 3. The process of claim 1, wherein the aluminum compound is an aluminum halide selected from the group consisting of A1C1 3 , AlBr 3 , AII3, and mixtures thereof. 4. The process of claim 3, wherein the aluminum halide is 5. The process of claim 4, wherein the A1C1 3 is added in an amount sufficient to provide about 0.5 to about 10% by weight of A1 2 0 3 based on total weight of Ti0 2 solids formed in the oxidation reaction. 6. The process of claim 1, wherein the boron compound is a boron halide selected from the group consisting of BC1 3 , BBr 3 , BI 3 , and mixtures thereof. 7. The process of claim 6, wherein the boron halide is 8. The process of claim 7, wherein the BC1 3 is added in an amount sufficient to provide about 500 ppm to about 5000 ppm boron based on total weight of Ti0 2 solids formed in the oxidation reaction. 9. The process of claim 8, wherein the the BC1 3 is added in an amount sufficient to provide about 800 ppm to about 2000 ppm boron based on total weight of Ti0 2 solids formed in the oxidation reaction. 10. The process of claim 1, wherein the boron compound is boric acid. 11. The process of claim 1, wherein the temperature of the gaseous suspension of Ti0 2 particles at the point where the particles are contacted with a boron compound is in the range of about 1000°C to about 1600°C and the pressure is in the range of about 40 to about 60 psig. 12. A process for producing titanium dioxide pigment comprising B 2 0 3 , comprising the steps of: (a) reacting TiCl in the vapor phase with an aluminum compound and an oxygen-containing gas in a reactor at a temperature in the range of about 900°C to about 1600°C to provide a gaseous suspension comprising Ti0 2 particles, and (b) passing the gaseous suspension comprising Ti0 2 particles to a cooling conduit, and (c) contacting the gaseous suspension comprising Ti0 2 particles in the cooling conduit with a boron compound to produce Ti0 2 pigment comprising B 2 0 3 . 13. The process of claim 12, wherein scouring particles are introduced into the cooling conduit. 14. The process of claim 12, wherein no scouring particles are introduced into the cooling conduit. 15. The process of claim 12, wherein the Ti0 2 pigment is in substantially rutile form. 16. The process of claim 12, wherein the aluminum compound is an aluminum halide selected from the group consisting of A1C1 3 , AlBr 3 , A1I 3 , and mixtures thereof. 17. The process of claim 16, wherein the aluminum compound 18. The process of claim 12, wherein the boron compound is a boron halide which is introduced into the conduit at the point where the scouring particles are introduced into the conduit. 19. The process of claim 18, wherein the boron halide is selected from the group consisting of BC1 3 , BBr 3 , BI 3 , and mixtures thereof, and the scouring particles are selected from the group consisting of calcined Ti0 2 , NaCl, KC1, sand, and mixtures thereof. 20. The process of claim 19, wherein the boron halide is BC1 3 and the scouring particles are NaCl. 21. The process of claim 19, wherein the boron halide is BCI 3 and the scouring particles are Ti0 2 . 22. The process of claim 12, wherein the boron compound is boric acid which is introduced into the conduit at the point where the scouring particles are introduced into the conduit. 23. The process of claim 12, wherein the cooled Ti0 2 pigment comprising B 2 0 3 is recovered and subjected to surface treatment comprising treating the pigment with a coating comprising silica. 24. The process of claim 12, wherein the cooled Ti0 2 pigment comprising B 2 0 3 is recovered and fluid-energy milled.

Inventors: ALLEN ALVIN, GERGELY JOHN STEVEN, ALLEN, ALVIN, GERGELY, JOHN, STEVEN
Applicants: DU PONT, E.I. DU PONT DE NEMOURS AND COMPANY
Application year: 1997
Main classification: C09C1
IPC codes: C01G23, C09C1, C09C3