Dielectric ceramic and monolithic ceramic electronic part using the same

Abstract: The present invention provides a nonreducing dielectric ceramic comprising a sintered compact composed of a plurality of particles expressed by a maximum diameter of about 0.5 µm and an average diameter of about 0.1 to 0.3 µm, each of the plurality of particles having a uniform composition and a uniform crystal system, and individual particles having the same composition and crystal system. A compact monolithic electronic part with high-reliability can be realized by using such ceramic.

Description: BACKGROUND OF THE INVENTION The present invention relates to dielectric ceramics and monolithic ceramic electronic parts using the same, such as multilayer ceramic capacitors and multilayer ceramic substrates. With the rapid miniaturization and low cost trend of monolithic ceramic electronic parts, thinner ceramic layers and use of base metals as internal electrodes have become common. For example, in multilayer ceramic capacitors which are one of many monolithic ceramic electronic parts, ceramic layers have been thinned to almost 5 µm, and copper and/or nickel have been used as internal electrodes. However, such thin ceramic layers cause high electric fields within the ceramic layers and cannot be used in dielectrics having large variances in dielectric constant with electric fields. As one dielectric to solve such a drawback, ceramic core-shell structures have been proposed and used, in which the core and shell have different compositions and crystal structures for particles composing a sintered compact. Such core-shell ceramics exhibit superior electric field and temperature characteristic dielectric constants. In core-shell ceramics, essential components are implanted by diffusion from the surface to the inside of each particle during sintering processes. As set forth above, conventional core-shell dielectrics have been produced by diffusion of essential components from the surface of each particle during the sintering process. When using finer particles as a raw material, components for forming the shell also diffuse into the center of the particle. As a result, the characteristic core-shell structure does not form. In accordance with the conventional technique, a minimum particle size in the sintered compact being capable of forming the core-shell structure is approximately 1 µm. When such a core-shell dielectric is used as a ceramic layer, having a thickness of no greater than 5 µm, in a monolithic ceramic electronic part, the number of particles which exist in the direction perpendicular to the layers decrease, thus the monolithic ceramic electronic part is less reliable. Accordingly, the development of thinner ceramic layers for monolithic ceramic electronic parts has reached its limit. JP-A-06060721 discloses to manufacture a dielectric porcelain so that the mean grain size stays within 0,1 to 0,3 µm, and the grain distribution is contained by 70% or more within the range of mean grain size ± mean grain size · 0,5 µm. SUMMARY OF THE INVENTION It is an object of the present invention to provide a dielectric ceramic exhibiting a superior temperature and electric field characteristic dielectric constant, in which the sintered compact comprises small non-core-shell particles. It is another object of the present invention to provide particles leading to thin ceramic layers each having a thickness of 3 µm or less. The dielectric ceramic comprises a sintered compact composed of a plurality of particles expressed by a maximum diameter of about 0.5 µm and an average diameter of about 0.1 to 0.3 µm. Since the average diameter of particles in the sintered compact is small, i.e., about 0.1 to 0.3 µm, as set forth above, many particles can be stacked with each other in the direction perpendicular to the layer even in a thin layer of about 5 µm or less, resulting in high reliability of the ceramic layer. In a first embodiment of the invention each of the plurality of particles have a uniform composition and a uniform crystal system, and individual said particles have the same composition and crystal system. Since each particle of the sintered compact has a uniform composition and crystal system, the ceramic structure is stable during sintering process. Further, its small particle size suppresses the dielectric characteristics of the ceramic and results in superior electric field and temperature characteristics. In a second embodiment of the invention each of the plurality of particles have a uniform composition and a uniform crystal system, and the sintered compact comprising at least two kinds of said particles may have different compositions. Since each particle of the sintered compact has a uniform composition and crystal system, the advantage described above can be realized. In conventional core-shell structures, the difference of temperature characteristics on dielectric constant between the core and shell is achieved by adjusting the thickness of the shell diffusion layer which forms during sintering with difficulty. In contrast, in this dielectric ceramic, the temperature characteristics can be readily adjusted by varying the volume ratio of at least two kinds of fine particles having different compositions and dielectric constants, resulting in improvement in quality and reproducibility of the sintered compacts. "Particles having different compositions" include particles having different components and particles having the same components but different ratios. By using particles having different compositions and suppressing interdiffusion and particle growth, excellent electric field and temperature characteristics can be achieved. Further, the dielectric ceramic may have a grain boundary phase having a different composition from said particles. Preferably, the thickness of said grain boundary phase is about 5 nm or less. In this dielectric ceramic, the electric field concentrates in the grain boundary phase and the electric field applied to the particles themselves is suppressed, resulting in high particle reliability. Since oxygen diffuses at a high rate within the grain boundary and compensates for oxygen defects which cause low reliability, the reliability is not reduced by concentration of the electric field in the grain boundary. However, in a grain boundary phase of over 5 nm, a grain boundary having a low dielectric constant than the particles causes a large decrease in the dielectric constant of the entire ceramic. Further, the dielectric ceramic may have nonreducing characteristic. When the dielectric ceramic has nonreducing characteristic, electrodes made with the dielectric ceramic ca be made of base metal. Thus, the manufacturing cost of electronic part using thereof can be reduced. The present invention also provides a monolithic ceramic electronic part having a ceramic layer composed of one of the above dielectric ceramics, and a first conductor associated with said ceramic layer. The monolithic ceramic electronic part further may have a second conductor being connected to said first conductor and being accessible from outside. In the above monolithic ceramic electronic part, the first conductor can be made of a base metal when the dielectric ceramic has nonreducing characteristic. BRIEF DESCRIPTION OF THE DRAWINGS Fig. 1 is a cross-sectional view of a multilayer ceramic capacitor as an embodiment in accordance with the present invention. DESCRIPTION OF THE PREFERRED EMBODIMENTS A dielectric ceramic in accordance with the present invention and a monolithic ceramic electronic part which uses it will be illustrated with reference to an exemplified multilayer ceramic capacitor. In the embodiment, a base metal is used for an internal electrode of the monolithic electronic ceramic part to reduce cost. Thus, nonreducing dielectric materials, such as a stoichiometric shift toward the A site in the general formula ABO 3 , for example, in barium titanate, and addition of an acceptor element, are used. However, another types of electrodes and ceramic can be used. As shown in Fig. 1, the exemplified multilayer ceramic capacitor is of a rectangular parallelepiped chip type and comprises a laminate 1 which is prepared by laminating a plurality of dielectric ceramic layers 2, internal electrodes 3 as internal conductors intercalated between the dielectric ceramic layers 2, and external conductors provided at both ends of the laminate. Each external conductor consists of an external electrode 5, a plated film 6 such as nickel, copper or the like, and a plated film 7 such as solder, tin or the like. The multilayer ceramic capacitor is produced as follows: A main component such as barium titanate and an additive for modifying the capacitor characteristics as starting materials are weighed according to a given recipe and wet-mixed. An organic binder and a solvent are added to the powder mixture to obtain a slurry, and a ceramic green sheet is made from the slurry. An internal electrode layer comprising a base metal such as copper is provided on the ceramic green sheet, for example, by screen printing, evaporation, or plating. A predetermined number of ceramic green sheets with internal electrode layers are laminated, and two ceramic green sheets without internal electrode layers are provided on both surfaces of the laminated sheets. These are pressed to obtain a laminate 1. The laminate 1 is sintered in a reducing atmosphere at a predetermined temperature. At both ends of the laminate 1, external electrodes 5 are formed so as to connect with the internal electrodes 3. Materials for the external electrode 5 may be the same as those for the internal electrode 3. Alternatively, usable materials may include metals and alloys, e.g. silver, palladium, silver-palladium alloys, copper, and copper alloys. These metal and alloy powders may contain glass frits such as B 2 O 3 -SiO 2 -BaO glass and Li 2 O-SiO 2 -BaO glass. An appropriate material is selected from among them in consideration to its usage and environment. The external electrodes 5 are generally formed by coating a raw metal paste on the as-sintered laminate 1, followed by baking. Alternatively, the paste may be coated on the non-sintered laminate 1 and baked during sintering. Plating films 6 of copper or nickel are formed on the external electrodes 5, then plating films 7 of silver or the like are formed thereon to prepare a chip type multilayer ceramic capacitor. EXAMPLES [Examples: Sample Nos. 1 through 7] After an appropriate amount of organic solvent was added to starting materials based on the formulations (mole ratios) shown in Table 1, these starting materials were mixed while powdering in a resinous pot with 2 mm  zirconia powdering media. In Table 1, Sample Nos. 1 through 7 indicate examples in accordance with the present invention. Starting materials in each sample are as follows: In Sample No. 1, barium titanate (BaTiO 3 ) which was prepared by a hydrothermal crystallization method with an average particle size of 0.1 µm and a Mn compound soluble in an organic solvent used in the mixing/powdering process were used as starting materials. In Sample No. 2, barium titanate (BaTiO 3 ) which was prepared by hydrolytic reaction followed by calcination with an average particle size of 0.2 µm and Mn and Mg compounds soluble in an organic solvent used in the mixing/powdering process were used as starting materials. In Sample No. 3, barium titanate (BaTiO 3 ) which was prepared by a hydrothermal crystallization method with an average particle size of 0.3 µm and fine manganese carbonate powder were used as starting materials. In Sample No. 4, barium titanate (BaTiO 3 ) and calcium titanate (CaTiO 3 ) which were prepared by hydrolytic reaction were mixed at a mole ratio of 9:1 and were calcinated to obtain a powder mixture having an average particle size of 0.2 µm. The powder mixture and a Mn compound soluble in an organic solvent used in the mixing/powdering process were used as starting materials. In Sample No. 5, barium titanate (BaTiO 3 ) prepared by a hydrothermal crystallization method having an average particle size of 0.2 µm, fine manganese carbonate powder and fine Li-Ba-Si glass were used as starting materials. In Sample No. 6, barium titanate zirconate {Ba(Zr,Ti)O 3 } prepared by solid phase reaction having an average particle size of 0.25 µm, fine manganese carbonate powder and a Li-Ba-Si compound soluble in an organic solvent used in the mixing/powdering process were used as starting materials, in which the barium titanate zirconate was prepared by mixing barium carbonate, titanium oxide and zirconium oxide so that the mole ratio of Ba/(Ti+Zr) was 1 and that of Ti/Zr was 7/3, followed by calcinating at 1,100 °C and powdering. In Sample No. 7, barium titanate (BaTiO 3 ) prepared by solid phase reaction having an average diameter of 0.3 µm, a Mn compound and a B-Ba-Si compound which were soluble in an organic solvent used in the mixing/powdering process were used as starting materials, in which the barium titanate was prepared by mixing barium carbonate and titanium oxide so that the mole ratio of Ba/Ti was 1, followed by calcinating and powdering. Compounds soluble in an organic solvent include alkoxides and acetylacetonates of the corresponding metals and metal soaps. A slurry was prepared by adding a predetermined amount of organic binder to each powdered mixture and shaped into a thin ceramic sheet on an organic film with a doctor blade so that the thickness after sintering was 2 µm. Next, a conductive layer essentially consisting of nickel was formed on the ceramic green sheet by printing. Six ceramic green sheets with conductive layers were overlapped such that extraction sites of their conductive layers alternate and were intercalated with two ceramic green sheets without internal electrodes to form a laminate. The laminate was heated in a nitrogen atmosphere to remove the binder and sintered in a reducing atmosphere at a sintering temperature as shown in Table 1 to form a ceramic sintered compact. A silver paste containing glass frit was coated and baked on both sides of the ceramic sintered compact to provide external electrodes. A multilayer ceramic capacitor comprising nonreducing dielectric ceramic layers was prepared in such a manner. [Comparative Examples: Sample Nos. 8 through 10] After an appropriate amount of organic solvent was added to starting materials based on the formulations (mole ratios) shown in Table 1, these starting materials were mixed while powdering in a resinous pot with 2 mm  zirconia powdering media. In Table 1, Sample Nos. 8 through 10 indicate comparative examples. In Sample No. 8, the same starting materials as Sample No. 1 were used. In Sample No. 9, starting materials were the same as Sample No. 5. Although the same starting materials as Sample No. 7 were used in Sample No. 10, the amount of the B-Ba-Si compound was different from Sample No. 7. Multilayer ceramic capacitors comprising nonreducing dielectric ceramic layers were prepared at sintering temperatures shown in Table 1 under the same conditions as in the Examples. Particles and grain boundaries of the resulting multilayer ceramic capacitors in the Examples and Comparative Examples were observed. Each multilayer ceramic capacitor was cut and etched with heat, and the etched surface was observed with a scanning electron microscope to photographically determine the average particle size. The grain boundaries were observed with a transmission electron microscope to check the presence of the grain boundary phase and to determine the thickness of the phase if it exists. Results are shown in Table 1. The compositions of the particles themselves and grain boundaries were determined with an analytical transmission electron microscope. As a result, it is confirmed that each particle has a uniform composition, individual particles have the same composition, and the grain boundary phase has a different composition from the particles. Transmission electron microscopy of the ceramic particle shows that each particle does not have a core-shell structure, but has a uniform crystal structure and individual particles have the same crystal structure. Electrical characteristics of the resulting multilayer ceramic capacitors were determined. The electrostatic capacitance and dielectric loss of each capacitor were measured at a frequency of 1 kHz, a voltage of 1 Vrms and a temperature of 25 °C. The dielectric constant was calculated from the electrostatic capacitance. The insulation resistance at 25 °C was measured by applying a direct current voltage of 10 V to determine the resistivity. Rates of change in electrostatic capacitance (or dielectric constant) at 85 °C and 125 °C were determined to a standard temperature of 25 °C. Further, the rate of change in electrostatic capacitance (or dielectric constant) was determined by applying a direct current bias of 3 kV/mm with reference to a standard electrostatic capacitance without bias. Results are shown in Table 2. Sample number Dielectric constant Dielectric loss (%) Resistivity (Ω x cm) Rate of change in dielectric constant (%, standard: 25°C) Rate of change in dielectric constant (%) at d.c. voltage bias (3kv/mm) 85°C 125° C Example 1 1500 3.5 12.50 -2.4 -8.6 -15.2 2 2000 4.0 12.65 -3.5 -9.7 -15.3 3 2600 5.0 12.45 -7.6 -13.6 -16.7 4 1800 4.0 12.55 -4.4 -8.8 -14.3 5 1950 3.5 12.76 -4.4 -11.5 -14.6 6 2000 3.5 12.55 -6.5 -13.0 -14.5 7 1400 2.2 13.00 -3.6 -7.6 -12.4 Comparative Example 8 2300 7.5 12.85 -2.5 28.2 -25.8 9 3300 8.8 12.35 -4.5 42.5 -40.6 10 550 2.5 13.10 -0.3 -5.3 -12.4 The observations and results set forth above evidently illustrate that each ceramic dielectric in accordance with the present invention has a maximum particle size of 0.5 µm and an average particle size of 0.1 to 0.3 µm and each particle has a uniform composition and crystal system. In each of Sample Nos. 5 to 7, a grain boundary phase having a thickness of 0.5 to 5.0 nm with a different composition from the particles is formed. The multilayer ceramic capacitor comprising the nonreducing dielectric ceramic in accordance with the present invention shows a low rate of change in dielectric constant (less than 15%) at 125 °C and dielectric characteristics which satisfy the X7R characteristics. The rate of change in dielectric constant when applying a direct current bias is satisfactorily low (less than 20%). In contrast, for a maximum particle size of over 0.5 µm as shown in Sample No. 8, the dielectric loss increases more than 5%, the rate of change in dielectric constant with temperature increases more than 15%, and the rate of change in dielectric constant when applying a direct current bias increases more than 20%. For an average particle size of over 0.3 µm and a maximum particle size of over 0.5 µm as shown in Sample No. 9, the dielectric loss increases more than 5%, the rate of change in dielectric constant with temperature increases more than 15%, and the rate of change in dielectric constant when applying a direct current bias increases more than 20%. For a grain boundary phase thickness of over 5.0 nm as shown in Sample No. 10, the dielectric constant decreases, although the rate of change in dielectric constant with temperature and the rate of change in dielectric constant when applying a direct current bias are satisfactory. Each sample was subjected to a reliability test in which a direct current voltage of 18 volts was applied at a temperature of 150 °C for 1,000 hours. Characteristics such as insulation resistance did not deteriorate in Examples in accordance with the present invention. In contrast, in Sample Nos. 8 and 9 as Comparative Examples, their reliabilities were low because the insulation resistances deteriorated due to large particle sizes. Alkoxides and acetylacetonate of various metals and metal soaps were used as compounds soluble in an organic solvent which was used for mixing and powdering raw materials in the Examples and Comparative Examples. When using water as the solvent, water soluble compounds such as nitrates, acetates, borates and chlorides may be used according to demand. It is preferred that sintering be performed in a reducing atmosphere as shown in the Examples set forth above, because sintering in an air atmosphere promotes growth of ceramic particles, resulting in an increased rate of change in dielectric constant with temperature and the increased rate of change in dielectric constant when applying a direct current bias. Silver is used for external electrodes in the Examples set forth above, and the use of a base metal is also preferable due to excellent electrical contact with internal electrodes comprising a base metal. In Sample Nos. 1 through 3, compositions, in which the mole ratios of barium to titanium in BaTiO3 deviate from the respective stoichiometric value, were also tested. No significant differences in their sintering characteristics and properties of the resulting sintered compacts were found. In the Examples set forth above, multilayer ceramic capacitors were illustrated as an embodiment of monolithic ceramic electronic parts. It was found that other monolithic ceramic electronic parts such as monolithic ceramic substrates also have satisfactory characteristics. [Examples: Sample Nos. 11 through 16] After an appropriate amount of organic solvent was added to starting materials based on the formulations (mole ratios) shown in Table 3, these starting materials were mixed while powdering in a resinous pot with 2 mm Ω zirconia powdering media. The starting materials in each sample are as follows: Sample No. 11: barium titanate (BaTiO 3 ) which was prepared by hydrolytic reaction with an average particle size of 0.2 µm, barium titanate-zirconate {Ba(Zr,Ti)O 3 } with an average particle size of 0.2 µm and a Mn compound soluble in an organic solvent used in the mixing/powdering process, in which barium titanate-zirconate was prepared by mixing and calcinating barium titanate (BaTiO 3 ) and barium zirconate (BaZrO 3 ) in a mole ratio of 7/3 which were prepared by hydrolytic reaction. Sample No. 12: barium titanate (BaTiO 3 ) which was prepared by hydrolytic reaction with an average particle size of 0.2 µm, strontium titanate (SrTiO 3 ) which was prepared by hydrolytic reaction with an average particle size of 0.2 µm, and Mn and Mg compounds soluble in an organic solvent used in the mixing/powdering process. Sample No. 13: strontium titanate (SrTiO 3 ) which was prepared by a hydrothermal crystallization method with an average particle size of 0.3 ¦Êm, calcium titanate (CaTiO 3 ) which was prepared by a hydrothermal crystallization method with an average particle size of 0.2 µm and fine manganese carbonate powder. Sample No. 14: barium titanate (BaTiO 3 ) which was prepared by hydrolytic reaction with an average particle size of 0.1 µm, barium titanate-zirconate {Ba(Zr,Ti)O 3 } with an average particle size of 0.2 µm, a Mn compound and a Li-Ba-Si compound which were soluble in an organic solvent used in the mixing/powdering process, in which barium titanate-zirconate was prepared by mixing and calcinating barium titanate (BaTiO 3 ) and barium zirconate (BaZrO 3 ) in a mole ratio of 7/3 which were prepared by hydrolytic reaction. Sample No. 15: barium titanate-zirconate {Ba(Zr,Ti)O 3 } prepared by solid phase reaction with an average particle size of 0.2 µm, calcium titanate (CaTiO 3 ) prepared by hydrothermal crystallization method with an average particle size of 0.2 µm, Mg and Mn compounds soluble in an organic solvent used in the mixing/powdering process and Li-Ba-Si glass powder, in which the barium titanate zirconate was prepared by mixing barium carbonate, titanium oxide and zirconium oxide so that the mole ratio of Ba/(Ti+Zr) was 1 and that of Ti/Zr was 7/3, followed by calcinating and powdering. Sample No. 16: barium titanate (BaTiO 3 ) prepared by solid phase reaction having an average diameter of 0.25 µm, strontium titanate prepared by a hydrothermal crystallization method with an average diameter of 0.3 µm, calcium titanate (CaTiO 3 ) prepared by a hydrothermal crystallization method with an average diameter of 0.2 µm, a Ni compound, a Mn compound and a B-Ba-Si compound which were soluble in an organic solvent used in the mixing/powdering process, in which the barium titanate was prepared by mixing barium carbonate and titanium oxide so that the mole ratio of Ba/Ti was 1, followed by calcinating and powdering. Compounds soluble in an organic solvent include alkoxides and acetylacetonates of the corresponding metals and metallic soaps. A slurry was prepared by adding a predetermined amount of organic binder to each powdered mixture and shaped into a thin ceramic sheet on an organic film with a doctor blade so that the thickness after sintering was 2 µm. Next, a conductive layer essentially consisting of nickel was formed on the ceramic green sheet by printing. Six ceramic green sheets with conductive layers were overlapped such that extraction sites of their conductive layers alternate and were intercalated with two ceramic green sheets without internal electrodes to form a laminate. The laminate was heated in a nitrogen atmosphere to remove the binder and sintered in a reducing atmosphere at a sintering temperature as shown in Table 3 to form a ceramic sintered compact. A silver paste containing glass frit was coated and baked on both sides of the ceramic sintered compact to provide external electrodes. A multilayer ceramic capacitor comprising nonreducing dielectric ceramic layers was prepared in such a manner. [Comparative Examples: Sample Nos. 17 through 20] After an appropriate amount of organic solvent was added to starting materials based on the formulations (mole ratios) shown in Table 4, these starting materials were mixed while powdering in a resinous pot with 2 mm zirconia powdering media. The starting materials in each sample are as follows: Sample No. 17: barium titanate (BaTiO 3 ) which was prepared by a hydrothermal crystallization method with an average particle size of 0.5 µm, barium titanate-zirconate {Ba(Zr,Ti)O 3 } with an average particle size of 0.2 µm, a Mn compound soluble in an organic solvent used in the mixing/powdering process and a B-Ba-Si compound, in which barium titanate-zirconate was prepared by mixing and calcinating barium titanate (BaTiO 3 ) and barium zirconate (BaZrO 3 ) in a mole ratio of 7/3 which were prepared by hydrolytic reaction. Sample No. 18: barium titanate (BaTiO 3 ) which was prepared by a hydrothermal crystallization method with an average particle size of 0.1 µm, barium titanate-zirconate {Ba(Zr,Ti)O 3 } with an average particle size of 0.1 µm, and a Mn compound soluble in an organic solvent used in the mixing/powdering process, in which barium titanate-zirconate was prepared by mixing and calcinating barium titanate (BaTiO 3 ) and barium zirconate (BaZrO 3 ) in a mole ratio of 7/3 which were prepared by hydrolytic reaction. Sample No. 19: barium titanate (BaTiO 3 ) prepared by solid phase reaction having an average diameter of 0.25 µm, strontium titanate prepared by a hydrothermal crystallization method with an average diameter of 0.3 µm, calcium titanate (CaTiO 3 ) prepared by a hydrothermal crystallization method with an average diameter of 0.2 µm, a Mn compound soluble in an organic solvent used in the mixing/powdering process and a B-Ba-Si compound, in which the barium titanate was prepared by mixing barium carbonate and titanium oxide so that the mole ratio of Ba/Ti was 1, followed by calcinating and powdering. Sample No. 20: barium titanate-zirconate {Ba(Zr,Ti)O 3 } prepared by solid phase reaction with an average particle size of 0.2 µm, calcium titanate (CaTiO 3 ) prepared by hydrothermal crystallization method with an average particle size of 0.2 µm, a Mn compound soluble in an organic solvent used in the mixing/powdering process and Li-Ba-Si glass powder, in which the barium titanate zirconate was prepared by mixing barium carbonate, titanium oxide and zirconium oxide so that the mole ratio of Ba/(Ti+Zr) was 1 and that of Ti/Zr was 7/3, followed by calcinating and powdering. Multilayer ceramic capacitors comprising nonreducing dielectric ceramic layers were prepared at sintering temperatures shown in Table 4 under the same conditions as in the Examples. Particles and grain boundaries of the resulting multilayer ceramic capacitors in the Examples and Comparative Examples were observed. Each multilayer ceramic capacitor was cut and etched with heat, and the etched surface was observed with a scanning electron microscope to photographically determine the average particle size. The grain boundaries were observed with a transmission electron microscope to check the presence of the grain boundary phase and to determine the thickness of the phase if it exists. Results are shown in Tables 3 and 4. The compositions of the particles themselves and grain boundaries were determined with an analytical transmission electron microscope. As a result, it is confirmed that there are at least two kinds of particles with different compositions, each particle has a uniform composition, and the grain boundary phase has a different composition from the particles. Transmission electron microscopy of the ceramic particle shows that each particle does not have a core-shell structure, but has a uniform crystal structure. Electrical characteristics of the resulting multilayer ceramic capacitors were determined. The electrostatic capacitance and dielectric loss of each capacitor were measured at a frequency of 1 kHz, a voltage of 1 Vrms and a temperature of 25 °C. The dielectric constant was calculated from the electrostatic capacitance. The insulation resistance at 25 °C was measured by applying a direct current voltage of 10 V to determine the resistivity. Rates of change in electrostatic capacitance (or dielectric constant) at 85 °C and 125 °C were determined to a standard temperature of 25 °C. Further, the rate of change in electrostatic capacitance (or dielectric constant) was determined by applying a direct current bias of 3 kV/mm with reference to a standard electrostatic capacitance without bias. Results are shown in Table 5. Sample number Dielectric constant Dielectric loss (%) Resistivity (Ω x cm) Rate of change in dielectric constant (%, standard: 25°C) Rate of change in dielectric constant (%) at d.c. voltage bias (3kv/mm) 85°C 125°C Example 11 1800 3.5 12.85 -4.4 -10.5 -14.5 12 1600 2.0 12.74 -3.5 -10.3 -14.6 13 700 1.4 12.55 -2.6 -4.6 -7.5 14 2100 4.0 12.97 -8.3 -14.2 -15.0 15 2050 3.5 12.86 -8.4 -14.5 -14.5 16 1630 3.5 12.75 -6.5 -13.0 -13.6 Comparative Example 17 2800 7.4 12.96 -6.9 -30.8 -26.4 18 2400 7.5 12.85 15.6 -40.8 -51.3 19 550 1.5 12.85 -3.5 -12.5 -14.2 20 1850 3.5 12.90 -7.6 -14.6 -45.5 The observations and results set forth above evidently illustrate that each ceramic dielectric in accordance with the present invention has a maximum particle size of 0.5 µm and an average particle size of 0.1 to 0.3 µm and comprises at least two kinds of particles with different compositions, and each particle has a uniform composition and crystal system. In each of Sample Nos. 14 to 16, a grain boundary phase having a thickness of 0.5 to 5.0 nm with a different composition from the particles is formed. The multilayer ceramic capacitor comprising the nonreducing dielectric ceramic in accordance with the present invention shows a low rate of change in dielectric constant (less than 15%) at 125 °C and dielectric characteristics which satisfy the X7R characteristics. The rate of change in dielectric constant when applying a direct current bias is satisfactorily low (less than 20%). In contrast, for a maximum particle size of over 0.5 µm as shown in Sample Nos. 17, 18 and 20, the rate of change in dielectric constant when applying a direct current bias increases more than 20%. In Sample Nos. 17 and 18, the dielectric loss increases more than 5%, and the rate of change in dielectric constant with temperature increases more than 15%. For a grain boundary phase thickness of over 5.0 nm as shown in Sample No. 19, the dielectric constant decreases, although the rate of change in dielectric constant with temperature and the rate of change in dielectric constant when applying a direct current bias are satisfactory. Each sample was subjected to a reliability test in which a direct current voltage of 18 volts was applied at a temperature of 150 °C for 1,000 hours. Characteristics such as insulation resistance did not deteriorate in Examples in accordance with the present invention. In contrast, in Sample Nos. 17 and 18 as Comparative Examples, their reliabilities were low because the insulation resistances deteriorated due to large particle sizes. Alkoxides and acetylacetonate of various metals and metal soaps were used as compounds soluble in an organic solvent which was used for mixing and powdering raw materials in the Examples and Comparative Examples. When using water as the solvent, water soluble compounds such as nitrates, acetates, borates and chlorides may be used according to demand. It is preferred that sintering be performed in a reducing atmosphere as shown in the Examples set forth above, because sintering in an air atmosphere promotes growth of ceramic particles, resulting in an increased rate of change in dielectric constant with temperature and the increased rate of change in dielectric constant when applying a direct current bias. Silver is used for external electrodes in the Examples set forth above, and the use of a base metal is also preferable due to excellent electrical contact with internal electrodes comprising a base metal. In Sample Nos. 1 through 3, 11 and 12, compositions, in which the mole ratios of barium to titanium in BaTiO 3 deviate from the respective stoichiometric value, were also tested. In Sample No. 13, compositions, in which the mole ratios of strontium to titanium in SrTiO 3 deviate from the respective stoichiometric value, were also tested. No significant differences in their sintering characteristics and properties of the resulting sintered compacts were found. In the Examples set forth above, multilayer ceramic capacitors were illustrated as an embodiment of monolithic ceramic electronic parts. It was found that other monolithic ceramic electronic parts such as monolithic ceramic substrates also have satisfactory characteristics.

Claims: A monolithic dielectric ceramic electronic part comprising a sintered compact composed of a plurality of particles expressed by a maximum diameter of about 0.5 µm and an average diameter of about 0.1 to 0.3 µm, characterized in that each of said plurality of particles has a uniform composition and a uniform crystal system, and individual said particles have the same composition and crystal system. A monolithic dielectric ceramic electronic part comprising a sintered compact composed of a plurality of particles expressed by a maximum diameter of about 0.5 µm and an average diameter of about 0.1 to 0.3 µm, characterized in that each of said plurality of particles has a uniform composition and a uniform crystal system, and said sintered compact comprising at least two kinds of said particles having different compositions. A dielectric ceramic according to Claim 1 or 2, characterized in that said dielectric ceramic further comprises a grain boundary phase having a different composition from said particles. A dielectric ceramic according to Claim 3, characterized in that the thickness of said grain boundary phase is about 5 nm or less. A dielectric ceramic according to one of Claims 1 to 4, characterized in that said dielectric ceramic has nonreducing characteristic. A monolithic ceramic electronic part having a ceramic layer composed of the dielectric ceramic of one of Claims 1 to 5, and a first conductor associated with said ceramic layer. A monolithic ceramic electronic part according to Claim 6, characterized in that the monolithic ceramic electronic part further comprises a second conductor being connected to said first conductor and being accessible from outside. A monolithic ceramic electronic part according to Claim 6 or 7, characterized in that said first conductor is made of a base metal.

Inventors: HAMAJI YUKIO, SANO HARUNOBU, TANAKA HIDEHIKO, WADA NOBUYUKI, HAMAJI, YUKIO, SANO, HARUNOBU, TANAKA, HIDEHIKO, WADA, NOBUYUKI
Applicants: MURATA MANUFACTURING CO, MURATA MANUFACTURING CO., LTD.
Application year: 1997
Main classification: H01G4
IPC codes: H01G4