PROCESS FOR OLEFIN ISOMERIZATION

Abstract: A process for the double bond isomerization of olefinic feed compounds is provided comprising contacting the olefinic feed compounds and a catalyst under reaction conditions sufficient to produce double bond isomerization, wherein the catalyst is an aluminophosphate-containing molecular sieve with pores having a diameter in the range of about 3.8 ANGSTROM to about 5 ANGSTROM . The process provides high conversion of normal alpha-olefins and high selectivity for linear internal olefins.

Description: PROCESS FOR OLEFIN ISOMERIZATION This invention relates to a process for the double bond isomerization of olefinic feed compounds. BACKGROUND OF THE INVENTION Molecular sieves are crystalline materials which have distinct crystal frameworks with ordered pore structures and cavities. Aluminosilicate zeolite-type molecular sieves useful as adsorbents or catalysts are known in the art and now comprise over 150 species of both naturally occurring and synthetic compositions. In general, the zeolites have frameworks formed from AI0 4 - and Si0 4 tetrahedra joined by the sharing of oxygen atoms. Such zeolites have a significant ion-exchange capacity and are capable of reversibly desorbing an adsorbed phase which is dispersed through the internal voids of the crystal without displacing any atoms which make up the permanent crystal structure. Non-zeolite molecular sieves comprising aluminophosphates are also known to be useful as adsorbents or catalysts. These non-zeolite molecular sieves generally contain [AI0 2 ] and [P0 2 ] tetrahedral units as essential framework constituents, and at least one additional element as a framework tetrahedral unit. Various catalysts are known for their use in the double bond isomerization of olefinic feed compounds. However, many of these catalysts produce substantial amounts of polymer and/or skeletal isomerized product, i.e., branched olefins. For some applications, such as preparing internal olefins for alkylation reactions, it is desirable to limit branched products to the least amount possible. SUMMARY OF THE INVENTION It is an object of the present invention to provide a process for the double bond isomerization of olefinic compounds. It is another object of the present invention to provide a process with high conversion rates. It is another object of the present invention to provide a process with high selectivity for internal linear olefins. It is another object of the present invention to provide a process which produces low amounts of branched olefins. It is another object of the present invention to provide a process with reduced catalyst coking. It is another object of the present invention to provide a process with increased catalyst life span. A process for the double bond isomerization of olefinic feed compounds is provided comprising contacting the olefinic feed compounds and a catalyst under reaction conditions sufficient to produce double bond isomerization, wherein the catalyst is an aluminophosphate-containing molecular sieve with pores having a diameter in the range of from about 3.8 A to about 5 A. BRIEF DESCRIPTION OF THE DRAWING Figure 1 is a graphic representation of the percent conversion versus time for a catalyst having one-dimensional pores, SAPO-39, compared to a catalyst having three-dimensional pores, SAPO-34. DETAILED DESCRIPTION OF THE INVENTION The present invention provides a process for the double bond isomerization of olefinic feed compounds employing particular aluminophosphate-containing molecular sieves. The catalysts of the present invention are aluminophosphate-containing molecular sieves which have a pore size in the range of from about 3.8 A to about 5.0 A, preferably in the range of from 3.8 A to 4.7 A. The effective pore size of the molecular sieves can be measured using standard adsorption techniques and hydrocarbonaceous compounds of known minimum kinetic diameters. See Breck, Zeolite Molecular Sieves, 1974 (Chapter 8); Anderson et al., J. Catalysis 58, 114 (1979); and U.S. Pat. No. 4,440,871 , the pertinent disclosures of which are incorporated herein by reference. It is preferred that the pores of the present catalyst are one-dimensional, meaning they are parallel and are not interconnected. One-dimensional pores exhibit less coking problems during the reaction, and therefore an extended catalyst life span. Three-dimensional sieves have intersecting pores which can lead to increased coke, causing deactivation of the catalyst. The aluminophosphate-containing molecular sieves are commonly known as "non-zeolite molecular sieves". Aluminophosphate-containing molecular sieves contain [AI0 2 ] and [P0 2 ] tetrahedral units joined by the sharing of the corner oxygen atoms and characterized by having pore openings of uniform dimensions. The aluminophosphate-containing molecular sieve can optionally contain silicon and/or one or more other elements which will form oxide linkages in tetrahedral coordination with aluminum and phosphorous in a crystalline framework. Suitable elements other than silicon include arsenic, beryllium, boron, chromium, cobalt, gallium, germanium, iron, lithium, magnesium, manganese, titanium, vanadium and zinc. Examples of suitable aluminophosphate-containing molecular sieves, which have a pore size in the preferred range, include silicon-containing SAPO-17, SAPO-18, SAPO-22, SAPO-34, SAPO-35, SAPO-39, SAPO-44, and SAPO-47, and magnesium containing MAPO-39. Of these, SAPO-22 and SAPO-39, which have one-dimensional pores, are preferred and SAPO-39 is especially preferred due to excellent results in conversion and selectivity. Suitable catalysts can be prepared by methods known in the art such as disclosed in U.S. Pat. Nos. 4,440,871 ; 4,567,029; 4,663,139 and 5,514,362, the disclosures of which are hereby incorporated by reference in their entirety. The preparation of aluminophosphate-containing compositions is disclosed in U.S. Pat. No. 4,663,139. The preparation of silicon-containing aluminophosphate compositions SAPO-17, SAPO-34, SAPO-35, and SAPO-44 is disclosed in U.S. Pat. No. 4,440,871. The preparation of silicon-containing aluminophosphate compositions SAPO-39 is disclosed in U.S. Pat. No. 5,514,362. The preparation of the magnesium-containing aluminophosphate composition MAPO-39, as well as aluminophosphate compositions containing manganese, cobalt or zinc, is disclosed in U.S. Pat. No. 4,567,029. The preparation of non-zeolitic molecular sieve compositions is disclosed in U.S. Pat. No. 4,973,785. The elements disclosed include arsenic, beryllium, boron, chromium, cobalt, gallium, germanium, iron, lithium, magnesium, manganese, titanium, vanadium and zinc. Aluminophosphate-containing molecular sieves are typically prepared by hydrothermal crystallization of a reaction mixture containing water, a reactive source of aluminum, such as pseudo-boehmite, AI(OH)3, or an aluminum alkoxide, a reactive source of phosphorus, such as phosphoric acid, and an organic templating agent, such as an alkyl amine. The reaction mixture is placed in a reaction vessel and heated until crystallized, usually at a temperature of at least about 80°C, preferably between 100°C and 200°C, and a period of from about 2 hours to 2 weeks. The solid crystalline reaction product is then recovered by any convenient method, such as filtration or centrifugation, washed with water and dried in air at a temperature between ambient and about 150°C. The catalyst can be calcined at a temperature sufficiently high to dehydrate and/or remove at least a portion of the organic templating agent present in the intracrystalline pore system. Generally, the calcining temperature will be in the range of from 200°C to 800°C. In order to maintain efficient double bond isomerization, it is preferred that hydrogenation promoters are not present in the catalyst. Therefore, it is preferred that the catalyst is essentially free of hydrogenation promoters. The catalyst can contain metals which reduce the number of strong acid sites on the catalyst and thereby lower the selectivity for cracking versus double bond isomerization. Especially preferred are the Group IIA metals such as magnesium and calcium. Strong acidity can also be reduced by introducing nitrogen compounds, e.g., NH 3 or organic nitrogen compounds, into the feed; however, the total nitrogen content should be less than 50 ppm, preferably less than 10 ppm. It is preferred that relatively small crystal size catalyst be utilized in practicing the invention. Suitably, the average crystal size is no greater than about 10 μ, preferably no more than about 1 μ and still more preferably no more than about 0.5 μ. The physical form of the catalyst depends on the type of catalytic reactor being employed and can be in the form of a granule or powder, and is preferably compacted into a more readily usable form (e.g., larger agglomerates), usually with a silica or alumina binder for fluidized bed reaction, or pills, prills, spheres, extrudates, or other shapes of controlled size to accord adequate catalyst- reactant contact. The catalyst can be employed either as a fluidized catalyst, or in a fixed or moving bed, and in one or more reaction stages. The aluminophosphate-containing molecular sieve may be used as a catalyst, without additional forming when the particles recovered from the crystallization step are of a size and shape desired for the ultimate catalyst. The molecular sieve can be composited with other materials resistant to temperatures and other conditions employed in the isomerization process. Such matrix materials include active and inactive materials and synthetic or naturally occurring zeolites as well as inorganic materials such as clays, silica and metal oxides. The latter may be either naturally occurring or in the form of gelatinous precipitates, sols or gels including mixtures of silica and metal oxides. Inactive materials suitably serve as diluents to control the amount of conversion in the isomerization process so that products can be obtained economically without employing other means for controlling the rate of reaction. The molecular sieve may be incorporated into naturally occurring clays, e.g., bentonite and kaolin. These materials, i.e., clays, oxides, etc., function in part, as binders for the catalyst. It is desirable to provide a catalyst having good crush strength because the catalyst is often subjected to rough handling. This tends to break the catalyst down into powder-like materials which cause problems in processing. Naturally occurring clays which can be composited with the catalyst include the montmorillonite and kaolin families, which families include the sub-bentonites, and the kaolins commonly known as Dixie, McNamee, Georgia and Florida clays or others in which the main mineral constituent is halloysite, kaolinite, dickite, nacrite or anauxite. Fibrous clays such as halloysite, sepiolite and attapulgite can also be used as supports. Such clays can be used in the raw state as originally mined or initially subjected to calcination, acid treatment or chemical modification. In addition to the foregoing materials, the molecular sieve can be composited with porous matrix materials and mixtures of matrix materials such as silica, alumina, titania, magnesia, silica-alumina, silica-magnesia, silica-zirconia, silica-thoria, silica-beryllia, silica-titania, titania-zirconia as well as ternary compositions such as silica-alumina-thoria, silica-alumina-titania, silica-alumina- magnesia and silica-magnesia-zirconia. The matrix can be in the form of a cogel. The catalyst can also be composited with zeolites such as synthetic and natural faujasites (e.g., X and Y), erionites, and mordenites. The catalyst can also be composited with purely synthetic zeolites such as those of the ZSM series. The combination of zeolites can also be composited in a porous inorganic matrix. The double bond isomerization can be conducted by contacting the feed with a fixed stationary bed of catalyst, with a fixed fluidized bed, or with a transport bed. A simple and therefore preferred configuration is a trickle-bed operation in which the feed is allowed to trickle through a stationary fixed bed. Typically, the olefinic feed compounds are alpha-olefins, preferably normal alpha-olefins. Generally, the olefinic feed compounds contain from 4 to 50 carbon atoms, preferably from 4 to 40 carbon atoms. The feed streams can be obtained from any suitable source. The olefins can be prepared by ethylene polymerization or Fischer-Tropsch synthesis, by wax cracking or from feeds containing normal alpha-olefins produced in petroleum refining. While the process of the invention can be practiced with utility when the feed contains organic nitrogen-containing impurities, it is preferred that the organic nitrogen content of the feed be less than about 50 ppmw (parts per million by weight), more preferably less than about 10 ppmw. Particularly good results, in terms of activity and length of catalyst cycle (period between successive regenerations or startup and first regeneration) are experienced when the feed contains less than about 10 ppmw of organic nitrogen. Reaction conditions for the process can vary broadly depending on the particular compounds being isomerized and the catalyst employed. Reaction conditions include the time, temperature and pressure sufficient to produce double bond isomerization of the olefinic feed compounds. Preferred operating conditions are those which result in substantially no olefin cracking. By substantially no olefin cracking is meant very low yield loss, less than 1 0 weight percent, preferably less than 5 weight percent and more preferably less than 2 weight percent of the feed is cracked to products having fewer carbon atoms than the feed. In a preferred embodiment, greater than 90 weight percent, preferably greater than 95 weight percent and more preferably greater than 98 weight percent of the product is within the boiling range of the olefin feed. Generally, reaction temperatures are in the range of from about 50°C to about 500°C, preferably from about 100°C to about 400°C, and more preferably from 150°C to 350°C. The liquid hourly space velocity (LHSV) can vary broadly but will generally be in the range of from about 0.1 to about 20, preferably in the range of from about 0.1 to about 10, and more preferably in the range of from 0.1 to 5. Reaction pressures are not critical and will depend on the temperature, reactants, and equipment employed. Typically, the pressure is in the range of from about atmospheric to about 2000 psig, preferably from atmospheric to 500 psig. The reaction may be carried out in the presence or absence of added hydrogen, where the added hydrogen may be used to enhance catalyst stability by suppressing coke formation. When hydrogen is added, the reactor conditions are adjusted to minimize the loss of olefins through hydrogenation. The reactor feed may also be mixed with an inert diluent such as N 2 during the reaction. The isomerized olefins are useful in producing sizings, inks, alkylate products, drilling fluids and other known uses. The following examples serve to show the present invention in detail by way of illustration and not by way of limitation. EXAMPLES Example 1 SAPO-39, a small pore aluminophosphate-containing molecular sieve catalyst, was prepared by mixing 92 g 86% H 3 P0 4 with 19 g Catapal alumina (pseudo boehmite, 73 wt% Al 2 0 3 , 27 wt% H 2 0) for 10 minutes. To the mixture was added 8 g silica (Cab-O-Sil M-5, 91 wt% Si0 2 , 9 wt% H 2 0) and 80 grams peptized and neutralized Catapal alumina (35 wt% Al 2 0 3 , 65 wt% H 2 0). The mixture was stirred for about 1.3 hours. Then 36 g di-n-propylamine were added, followed by 37 grams of Catapal alumina. The mix was then extruded through a 1/16 inch die. Volatiles content of the extrudate was 49.0 wt%. The extrudate was placed in a Teflon bottle in a stainless steel pressure vessel and heated at 190°C and autogenous pressure for two days. The extrudate was washed with water, dried in a vacuum oven overnight at 120°C, and then calcined in air for six hours at 600°C. X-ray diffraction analysis showed the extrudate to consist primarily of SAPO-39. The catalyst was used to isomerize 1-pentene at 400°F, 1 LHSV, and 12 psig, along with a nitrogen diluent at a molar ratio of nitrogen to pentene of 2.6. The results are shown in Table I Example 2 SAPO-34, a small pore aluminophosphate-containing molecular sieve catalyst, was prepared according to U.S. Patent No. 4,440,871. The SAPO-34 catalyst was used to isomerize 1 -pentene at the same conditions as in Example 1 , except the temperature was raised to 450°F to achieve about the same conversion as with the catalyst of Example 1. The results are shown in Table I. Table I Isomerization of 1 -Pentene Catalyst SAPO-39 SAPO-39 SAPO-34 SAPO-34 Temperature °F 400 400 450 450 Conversion Wt% 65.4 52.9 66.1 48.7 Selectivity Wt% t-2-pentene 67.3 66.7 58.2 55.9 c-2-pentene 28.1 26.3 38.3 34.7 Total 2-pentene 95.4 93.0 96.5 90.6 3-me-1-butene <0.1 <0.1 0.1 0.2 2-me-1-butene 0.3 0.5 0.8 0.8 2-me-2-butene 1.3 1.6 3.2 3.6 Total branched butene 1.6 2.1 4.1 4.6 Example 3 The intermediate pore aluminophosphate-containing molecular sieve catalyst ALP0 4 -11 was prepared according to U.S. Patent No. 4,310,440. SAPO-39 was prepared as disclosed in Example 1. The catalysts were used to isomerize 1 -pentene at the same conditions as in Example 1 except that the temperature for ALPO-11 was raised to 500°F to achieve the same 1 -pentene conversion. Table II Isomerization of 1 -Pentene Catalyst SAPO-39 ALPO-11 Temperature, °F 400 500 1 -pentene 9.3 9.1 trans-2-pentene 61.1 52.5 cis-2-pentene 25.5 22.9 Total 2-pentene 86.6 75.4 3-methyl-1-butene 0.1 0.3 2-methyl-1-butene 0.5 2.7 2-methyl-2-butene 1.2 10.2 Total branched butene 1.8 13.2 Isomerized pentane 0.9 0.8 Normal pentane 1.3 1.5 The results in Table II show significantly higher branched products in the process employing ALPO-11. Example 4 The catalysts SAPO-39 and SAPO-11 were prepared as described in Example 1 and 3, respectively. The catalysts were used to isomerize C 20 -C 2 at 0 psig and 3 LHSV. The results are shown in Table III. Table III Isomerization of C 20 -C 24 Normal Alpha-Olefins Catalyst SAPO-39 SAPO-39 SAPO-39 SAPO-11 SAPO-11 Temperature °C 210 240 250 180 190 Percent 75.8 97.3 99.6 69.4 83.2 Conversion Percent Branched 5.8 10.8 18.4 11.6 19.9 Olefin Example 5 The catalyst of Example 1 , SAPO-39, a catalyst having one-dimensional pores, and the catalyst of Example 2, SAPO-34, a catalyst having three-dimensional pores, were compared for isomerizing 1 -pentene at 1.1 WHSV, 204°C, 12 psig and 2.7 N 2 /HC. Figure 1 shows a much lower fouling rate for the SAPO-39 catalyst containing one-dimensional pores compared to the SAPO-34 catalyst containing three-dimensional pores.

Claims: WHAT IS CLAIMED IS: 1. A process for the double bond isomerization of olefinic feed compounds comprising contacting the olefinic feed compounds and a catalyst under reaction conditions sufficient to produce double bond isomerization, wherein the catalyst comprises an aluminophosphate-containing molecular sieve with pores having a diameter in the range of from about 3.8 A to about 5.0 A. 2. The process according to Claim 1 wherein the pores are one-dimensional. 3. The process according to Claim 2 wherein the pores have a diameter in the range of from 3.8 A to 4.7 A. 4. The process according to Claim 1 wherein the catalyst further comprises an element which will form oxide linkages in tetrahedral coordination with aluminum and phosphorous in a crystalline framework. 5. The process according to Claim 4 wherein the element is selected from the group consisting of silicon, arsenic, beryllium, boron, chromium, cobalt, gallium, germanium, iron, lithium, magnesium, manganese, titanium, vanadium or zinc. 6. The process according to Claim 5 wherein the element is silicon and optionally one or more additional elements. 7. The process according to Claim 1 wherein the catalyst is SAPO-17, SAPO-18, SAPO-22, SAPO-34, SAPO-35, SAPO-39, SAPO-44, SAPO-47, and MAPO-39. 8. The process according to Claim 7 wherein the catalyst is SAPO-22 and SAPO-39. 9. The process according to Claim 8 wherein the catalyst is SAPO-39. 10. The process according to Claim 1 wherein the catalyst is essentially free of hydrogenation promoters. 11. The process according to Claim 1 wherein the olefinic feed compounds comprise alpha-olefins. 12. The process according to Claim 11 wherein the olefinic feed compounds comprise normal alpha-olefins. 13. The process according to Claim 12 wherein the olefinic feed compounds contain from 4 to 50 carbon atoms. 14. The process according to Claim 13 wherein the olefinic feed compounds contain from 4 to 40 carbon atoms. 15. The process according to Claim 1 wherein the reaction conditions include a temperature in the range of from about 50°C to about 500°C. 16. The process according to Claim 15 wherein the reaction conditions include a temperature in the range of from about 100°C to about 400°C. 17. The process according to Claim 16 wherein the reaction conditions include a temperature of 150°C to 350°C. 18. The process according to Claim 15 wherein the reaction conditions include a liquid hourly space velocity in the range of from about 0.1 to about 20. 19. The process according to Claim 18 wherein the reaction conditions include a liquid hourly space velocity in the range of from about 0.1 to about 10.

Inventors: MILLER STEPHEN J, MILLER, STEPHEN, J.
Applicants: CHEVRON CHEM CO, CHEVRON CHEMICAL COMPANY LLC
Application year: 1997
Main classification: C07C5
IPC codes: C07C5, C07C11