Substituted indenyl unbridged metallocenes

Abstract: Unbridged metallocenes of a substituted indenyl and an unsubstituted cyclopentadienyl and their use in the polymerization of olefins.

Description: This invention relates to metallocenes. In another aspect this invention relates to catalyst systems useful for the polymerization of olefins. In another aspect this invention relates to methods for polymerizing olefins using specific types of metallocenes which can be referred to as unbridged metallocene of a substituted indenyl and cyclopentadienyl. Background of the Invention Since the discovery of ferrocene in 1951, a number of metallocenes have been prepared by the combination of compounds prepared from cyclopentadiene-type compounds and various transition metals. The term "cyclopentadiene-type compounds" as used herein refers to compounds containing the cyclopentadiene structure. Examples include unsubstituted cyclopentadiene, unsubstituted indene, unsubstituted fluorene, and substituted varieties of such compounds. Also included is tetrahydroindene. Many of the cyclopentadiene-type metallocenes have been found useful in catalyst systems for the polymerization of olefins. It has been noted in the art that variations in the chemical structure of such cyclopentadienyl-type metallocenes can have significant effects upon the suitability of the metallocene as a polymerization catalyst. For example, the size and location of substitutions on cyclopentadienyl-type ligands has been found to affect the activity of the catalyst, the stereoselectivity of the catalyst, the stability of the catalyst, or various properties of the resulting polymer; however, the effects of various substituents is still largely an empirical matter, that is, experiments must be conducted in order to determine just what effect a particular variation in the chemical structure of the metallocene will have upon its behavior as a polymerization catalyst. While there are references in the prior art which contain broad general formulas that encompass a vast number of unbridged metallocenes, it is considered unlikely that all of the metallocenes within the broad disclosures of publications have actually been prepared and evaluated for their polymerization effects. For example, while US-A 5,049,535; 5,225,092; and 5,126,303 and WO 94/11406 contain allegations regarding a wide range of both bridged and unbridged metallocenes, the only actual examples of unbridged metallocenes are those in which two identical cyclopentadienyl-type ligands are present, i.e. symmetrical unbridged metallocenes. Similarly, while U.S. 5,331,054 names two unsymmetrical unbridged metallocenes, viz. (cyclopentadienyl) (indenyl) and (cyclopentadienyl) (fluorenyl) zirconium dichlorides, those compounds do not contain substituted indenyl groups and again the actual examples used symmetrical unbridged metallocenes. While published EP-A-0 685 485 discloses unsymmetrical unbridged metallocenes containing substituted indenyl groups, the metallocenes also contain a pentamethylcyclopentadienyl group. Similarly, while U.S. 5,223,467 proposes unsymmetrical unbridged metallocenes which could include substituted indenyl groups it also specifies that the other cyclopentadienyl ring also be substituted and it does not contain any actual examples having an indenyl ligand. Many of the unbridged metallocenes have been found not to be sufficiently active in the polymerization of olefins to be of significant commercial interest. The aforementioned EP-A-0 685 485 reveals that indenyl pentamethylcyclopentadienyl Zr dichloride is much more active than indenyl cyclopentadienyl, which in turn is much more active than either the bis indenyl or bis cyclopentadienyl counterparts. Prior to the present applicants' work there does not appear to have been any work which suggests what effect substituents on indenyl would have on an unsymmetrical unbridged (indenyl) (unsubstituted cyclopentadienyl) metallocene. EP-A-0 685 495 discloses methods for preparing solid metallocene-containing catalyst systems by combining an organoaluminoxane with a metallocene having a cyclopentadienyl-type ligand which has an olefinically unsaturated substitution in a liquid to form a liquid catalyst system, and conducting prepolymerization of an olefin in the liquid catalyst system to produce the prepolymerized solid catalyst system. An object of the present invention is to provide certain new substituted indenyl-containing metallocenes. Still another object of the present invention is to provide polymerization catalyst systems employing the specific indenyl-type metallocenes. Still yet another object of the present invention is to provide processes for the polymerization of olefins using specific indenyl-type metallocene catalyst systems. Yet another object of the present invention is to provide catalyst systems which provide unusually high activity or molecular weight in the polymerization of olefins. Summary of the Invention In accordance with the present invention, there are provided unbridged substituted metallocenes of the formula (In)(Cp)MeQ 2 wherein In is a substituted indenyl radical having a substituent in at least one of the 1, 2, and 3 positions, said substituents being selected from hydrocarbyl radicals having 1 to 10 carbon atoms, more preferably 1 to 6 carbon atoms, and trialkylsilyl radicals wherein the alkyl groups have 1 to 4 carbons; Cp is an unsubstituted cyclopentadienyl radical; Me is a transition metal selected from the group consisting of titanium, zirconium, and hafnium; and each Q is the same or different and is selected from the group consisting of hydrocarbyl radicals having 1 to 12 carbon atoms, alkoxy radicals having 1 to 12 carbon atoms, aryloxy radicals having 6 to 12 carbon atoms, hydrogen, and halides, wherein the metallocene (cyclopentadienyl) (1-allylindenyl)zirconium dichloride is excluded. In accordance with another aspect of the present invention, there is provided a catalyst system comprising the specific types of unbridged indenyl-containing metallocenes as described above in combination with a cocatalyst selected from organometallic compounds of metals of Groups Ia, IIA and IIIB of the Periodic Table. In accordance with still another aspect of the present invention, there is provided a process for the polymerization of olefins comprising contacting said olefins under suitable reaction conditions with a catalyst system comprising an indenyl-containing metallocene as described above in combination with a suitable cocatalyst. Detailed Description of the Invention The novel metallocenes provided in accordance with the present invention are unbridged, that is the indenyl ligand and the cyclopentadienyl ligand that are bound to the metal are not bound to each other. In this disclosure the substituent locations are numbered in accordance with the IUPAC Nomenclature of Organic Chemistry, 1979, rule A 21.1. Such numbering is illustrated in the figure in lines 22 -26 on page 2 of the aforementioned WO 94/11406. Most preferably the indenyl has 1 to 3 hydrocarbyl substitutents or one trialkylsilyl substituent, optionally with 1 or 2 hydrocarbyl substitutents, and each substituent is located at a different one of the 1, 2, or 3 positions of the indenyl. The metallocenes (1-phenyl indenyl) (cyclopentadienyl) zirconium dichloride, (1,2,3-trimethyl indenyl) (cyclopentadienyl) zirconium dichloride, (2-methyl indenyl) (cyclopentadienyl) zirconium dichloride, (1-trimethylsilyl indenyl) (cyclopentadienyl) zirconium dichloride, and (1,2-dimethyl indenyl) (cyclopentadienyl) zirconium dichloride have been found to have particularly desirable characteristics. The metallocenes according to the invention can be prepared using techniques similar to those that have been used in the past for making unsymmetrical metallocenes. One example involves reacting an alkali metal salt of the indenyl compound in a suitable solvent under suitable reaction conditions with a suitable transition metal compound, for example CpMeCl 3 , wherein Me is Zr, Hf, or Ti. An especially preferred method involves carrying out the reaction of the indenyl-containing salt and the transition metal compound in the presence of a liquid diluent which is non-halogenated and non-coordinating toward the transition metal compound. Examples of such suitable liquid include hydrocarbons such as toluene, pentane, or hexane as well as non-cyclic ether compounds such as diethylether. It has been found that the use of such non-halogenated non-coordinating solvents generally allows one to obtain large amounts of substantially pure metallocenes in a more stable form, and often allows the reaction to be conducted under higher temperature conditions, than when dichloromethane is used as the diluent. The formation of the alkali metal salt of the indenyl compound can be formed using generally any technique known in the art. For example, such can be prepared by reacting an alkali metal alkyl with the substituted indene. The molar ratio of the alkali metal alkyl to the indene can vary; generally however, the ratio would be in the range of about 0.5/1 to about 1.5/1, still more preferably about 1/1. Typically, the alkali metal of the alkali metal alkyl would be selected from sodium, potassium, and lithium, and the alkyl group would have 1 to 8 carbon atoms, more preferably 1 to 4 carbon atoms. In the preferred embodiment if the indenyl salt is formed using tetrahydrofuran (THF) as the liquid solvent, the salt is isolated and substantially all of the THF is removed before the salt is contacted with the transition metal halide. The molar ratio of the indenyl salt to the transition metal compound can vary over a wide range depending upon the results desired. Typically, however, the indenyl salt is used at a molar ratio of the indenyl compound to the transition metal compound, i.e. CpMeCl 3 , of about 1 to 1. The resulting metallocene can be recovered and purified using conventional techniques known in the art such as filtration, extraction, crystallization, and recrystallization. It is generally desirable to recover the metallocene in a form that is free of any substantial amount of by-product impurities. Accordingly, recrystallization and fractional crystallization to obtain relatively pure metallocenes is desirable. Dichloromethane has been found to be particularly useful for such recrystallizations. Since the stability of the various metallocenes varies, it is generally desirable to use the metallocenes soon after their preparation or at least to store the metallocene under conditions favoring their stability. For example the metallocenes can generally be stored in the dark at low temperature, i.e. below 0°C, in the absence of oxygen and water. The resulting inventive indenyl-containing metallocenes can be used in combination with a suitable cocatalyst for the polymerization of olefinic monomers. In such processes the metallocene or the cocatalyst can be employed on a solid insoluble particulate support. Examples of suitable cocatalysts include generally any of those cocatalysts which have in the past been employed in conjunction with transition metal containing metallocene olefin polymerization catalysts. According to the invention the cocatalyst is selected from organometallic compounds of metals of Groups IA, IIA, and IIIB of the Periodic Table. Examples of such compounds have included organometallic halide compounds, organometallic hydrides and even metal hydrides. Some specific examples include triethyl aluminum, triisobutyl aluminum, diethyl aluminum chloride, and diethyl aluminum hydride. The currently most preferred cocatalyst is an aluminoxane. Such compounds include those compounds having repeating units of the formula where R is an alkyl group generally having 1 to 5 carbon atoms. Aluminoxanes, also sometimes referred to as poly(hydrocarbyl aluminum oxides) are well known in the art and are generally prepared by reacting an organo hydrocarbylaluminum compound with water. Such preparation techniques are disclosed in U.S. 3,242,099 and 4,808,561. The currently preferred cocatalysts are prepared either from trimethylaluminum or triethylaluminum, sometimes referred to as poly(methyl aluminum oxide) and poly(ethyl aluminum oxide), respectively. It also can be used an aluminoxane in combination with a trialkylaluminum, such as disclosed in US-A-4,794,096. The indenyl-containing metallocenes in combination with the aluminoxane cocatalyst can be used to polymerize olefins, especially alpha olefins having 2 to 12 carbon atoms. Often such polymerizations would be carried out in a homogeneous system in which the catalyst and cocatalyst were soluble; however, the polymerizations can also be carried out in the presence of supported or insoluble particulate forms of the catalyst and/or cocatalyst. The catalyst is thus considered suitable for solution, slurry, or gas phase polymerization. It also can be used a mixture of two or more of the indenyl-containing metallocenes according to the invention or a mixture of an indenyl-containing metallocene according to the invention with one or more other cyclopentadienyl-type metallocenes. The indenyl-containing metallocenes when used with aluminoxane are particularly useful for the polymerization of ethylene in the presence or absence of other olefins. Examples of other olefins that might be present include mono-unsaturated aliphatic alpha-olefins having 3 to 10 carbon atoms. Examples of such olefins include propylene, butene-1, pentene-1, 3-methylbutene-1, hexene-1, 4-methylpentene-1, 3-methylpentene-1, heptene-1, octene-1, decene-1, 4,4-dimethyl-1-pentene, 4,4-diethyl-1-hexene, 3-4-dimethyl-1-hexene, and mixtures thereof. The polymerizations can be carried out under a wide range of conditions depending upon the particular metallocene employed, and the results desired. Examples of typical conditions under which the metallocenes can be used in the polymerization of olefins include conditions such as disclosed in US-A-3,242,099; 4,892,851; and 4,530,914. It is considered that generally any of the polymerization procedures used in the prior art with any transition metal based catalyst systems can be employed with the present indenyl-containing metallocenes according to the invention. The amount of cocatalyst can vary over a wide range. It is currently preferred for the molar ratio of the aluminum in the aluminoxane to the transition metal in the metallocene to be in the range of about 0.1:1 to about 100,000:1 and more preferably about 5:1 to about 15,000:1. In many cases, the polymerizations would be carried out in the presence of liquid diluents which do not have an adverse affect upon the catalyst system. Examples of such liquid diluents include propane, butane, isobutane, pentane, hexane, heptane, octane, cyclohexane, methylcyclohexane, toluene, and xylene. The polymerization temperature can vary over a wide range, temperatures typically would be in the range of about -60°C to about 300°C, more preferably in the range of about 20°C to about 160°C. Typically the pressure would be in the range of from about 0.1 to 50 MPa (1 to about 500 atmospheres) or greater. The polymers produced with this invention have a wide range of uses that will be apparent to those skilled in the art from the physical properties of the respective polymer. Various techniques can be used for preparing the substituted indenes needed for producing the metallocenes of the present invention. Monoalkyl substituted indenes can be produced by alkylation of indenyl lithium. It has been discovered that less of the disubstitution products are obtained if the alkylation is conducted using diethyl ether as a reaction medium rather than THF. The 1-phenyl indenyl can be produced by reacting 1-indanon with phenylmagnesium bromide and then dehydrating the resulting 1-phenyl-1-indanol. This is preferably conducted in the presence of p-toluenesulfonic acid in toluene. An analogous procedure can be used to produce alkyl and aryl 2-substituted indenes. For example, a Grignard reaction of 2-indanon can be conducted using the respective alkyl or aryl halide. Multiple alkyl or aryl substituted indenes can be produced through reaction of the respective substituted 1-indanon with the appropriate Grignard reagent followed by dehydration of the produced indanol. For example 2,3-dimethyl-1-indanon or 3-methyl indanon can be reacted with methyl magnesium iodide to yield the respective methyl substituted indanol which is dehydrated to 1,2,3-trimethylindene or 1,3-dimethyl indene, respectively. In the latter case a mixture of p-tosyl chloride and pyridine is preferably used to effect the dehydration of the hydroxy group. The reduction of 2,3-dimethyl-1-indanon with lithium aluminum hydride and further elimination of water with p-toluenesulfonic acid leads to 1,2-dimethylindene. The compound 3-phenyl-1-methyl indene can be prepared by reacting 3,3-diphenylpropionic acid with aluminum trichloride in dichloromethane to obtain 3-phenyl-1-indanon which in turn is reacted with methyl magnesium iodide to produce the indanol which was then dehydrated with p-toluenesulfonic acid. A similar technique can be used to prepare 1-phenyl-3-phenyl indene by substituting phenyl magnesium bromide for the methyl Grignard reagent. Trimethylsilyl substituted indenes can be obtained by reacting the lithium salt of a substituted or unsubstituted indene with trimethylchlorosilane. Preferably this is done in diethyl ether. Such a technique has been used to produce 1-trimethylsilyl-3-methyl indene, 1-trimethylsilyl-3-phenyl indene, 1,3-di-trimethylsilyl indene, 1-trimethylsilyl-2-methyl indene, 1-trimethyl-2-phenyl indene, and 1-trimethylsilyl-1-methyl-2-methyl-3-methyl indene. A further understanding of the present invention, its various aspects, objects and advantages will be provided by the following examples. In the following examples, the metallocene preparations were carried out routinely using the Schlenk technique, with strict exclusion of air and moisture, by means of purified and dried inert gas. The solvents which were used were dried over a sodium/potassium alloy or over phosphorus pentoxide in the case of dichloromethane and distilled in circulation equipment under an inert atmosphere. Toluene was additionally distilled over phosphorus pentoxide and dichloromethane was distilled over calcium hydride. Deuterated solvents for the NMR spectroscopy were stored over a molecular sieve. The melting points of the organic compounds were determined in open tubes and those of the organometallic compounds were determined in closed tubes under nitrogen. The organic compounds were characterized using a gas chromatograph with flame ionization detector and a fused silica column with helium as the carrier gas. The mass spectra were carried out using a mass spectrometer with electron impact ionization energy of 70 eV. The samples were introduced with the help of a direct inlet system, or they were injected in the form of solutions. The thermal properties of the produced polymers was evaluated using a Differential Scanning Calorimetry Device, a DSC 7 model obtained from Perkin Elmer. The polymer samples were dried under vacuum prior to the measurements. The technique involved fusing 5 to 10 gram samples in standard aluminum pans, first by heating at 20 degrees K/min from -40°C to 200°C, holding at 200°C for 3 minutes, and then cooling at 20 degrees K/min to -40°C. A second heating phase like the first heating phase was then conducted. The melting points and enthalpies of fusion were measured during the second heating phase. The temperature was linearly corrected using indium as a standard (melting point 429.78K and enthalpy of fusion 28.45 J/g). The molecular weight of the polymers were determined using an Ubbelohde capillary viscometer in cis/trans-decalin at 135+/- 0.1 °C. The samples were dried under vacuum prior to the measurement and then weighed out into small flasks that could be sealed. The polymers were then dissolved in a precisely measured quantity of the decalin within three or four hours at 140° to 105°C. Any insoluble material was filtered out using glass wool. Calibration curves for three different polymer concentrations were evaluated for the determination of the viscosity average molecular weight, i.e. Mη. Example I Unbridged metallocenes were prepared by dissolving about 2.4 mmol of the selected indenyl compound in diethyl ether and then mixing with about 1.5 ml of a 1.6M hexane solution of n-butyl lithium. After stirring for about three hours at room temperature an equimolar quantity of a cyclopentadienyl trichloride metallocene was added and the mixture stirred for about four more hours at room temperature. The liquid was evaporated using a vacuum. The residue was extracted with toluene and the suspension was filtered over sodium sulfate. The resulting filtrate was concentrated by evaporation and brought to the point of crystallization by cooling to -78°C. Example II Various unbridged metallocenes prepared as described in Example I were then evaluated for their effectiveness in the polymerization of ethylene. The technique involved combining about 1 to 5 mg of the metallocene with 1 to 5 ml of a 30 weight percent toluene solution of commercial methylaluminoxane. The resulting solution was further diluted with additional toluene so as to result in a solution containing about 1 to 5 mg of the metallocene in about 20 ml of the solution. The resulting mixture was used as the catalyst system within about 30 minutes of its preparation. The polymerizations were conducted in a I liter autoclave. First 500 ml of pentane was mixed with 1 ml of the commercial methylaluminoxane and stirred for 15 min at 30°C. Then the catalyst system solution was added. The autoclave was thermostatically regulated at 60°C and ethylene was supplied at a pressure of 10 bar. After a reaction time of one hour, the pressure was released and the polymer dried under a vacuum. Some comparable control runs were carried out using prior art unbridged metallocenes such as bis cyclopentadienyl, bis indenyl, and 1-methyl indenyl pentamethylcyclopentadienyl metallocenes. Also a new metallocene (1-phenyl indenyl) indenyl zirconium dichloride was evaluated. The activities observed with the various unbridged metallocenes and some of the properties of the resulting polymers are compared in the following tables. Note that in a few cases noted in the table the polymerization was conducted at 30°C rather than 60°C. Run No. Complex Activity [g PE (mmol M-h)] Mη [10 3 g/mol] DSC T m [°C] ΔH m [J/g], α[%] 1 (1-Me-In)CpZrCl 2 530,000 380 140.2 151.7, 52 2** (1-MeO(CH 2 ) 2 -In)CpZrCl 2 4,500 560 143.7 105.0, 36 3 (1-Me 3 Si-In)CpZrCl 2 320,000 950 142.8 149.0, 51 4 (1-Ph-In)CpZrCl 2 1,400,000 580 143.8 161.2,55 5 (2-Me-In)CpZrCl 2 320,000 910 142.5 156.0, 53 6 (2-Ph-In)CpZrCl 2 230,000 520 144.1 148.8, 51 7 (1,2-Me 2 -In)CpZrCl 2 356,000 740 not determined 8 (1,3-Me 2 -In)CpZrCl 2 555,000 660 142.3 161.2, 55 9 (1,3-Ph 2 -In)CpZrCl 2 274,000 780 141.4 135.8, 46 10 (1,2,3-Me 3 -In)CpZrCl 2 1,100,000 600 140.8 169.6, 58 11 (1-Me-In)(Me 3 Si-Cp)ZrCl 2 121,000 660 141.8 160.5, 55 12 Cp 2 ZrCl 2 136,000 290 142.4 160.0, 55 13 Ind 2 ZrCl 2 293,000 470 143.5 168.2, 57 14 (1-MeIn)Cp*ZrCl 2 154,000 540 146.9 123.7, 42 15 (1-Ph-In)InZrCl 2 50,000 320 143.4 175.1,60 The data shows that the metallocenes according to the invention were more active than either the bis (cyclopentadienyl) zirconium dichloride or the (1-methylindenyl) (pentamethylcyclopentadienyl) zirconium dichloride and a number were even more active than the bis (indenyl) zirconium dichloride. The catalysts with the highest activities were the (1-phenyl indenyl) (cyclopentadienyl) zirconium dichloride and the (1,2,3-trimethyl indenyl) (cyclopentadienyl) zirconium dichloride. The runs using (1-methyl indenyl) (trimethylsilylcyclopentadienyl) zirconium dichloride and (1-methyl indenyl) (pentamethylcyclopentadienyl) zirconium dichloride suggest that the introduction of a substituent on the cyclopentadienyl ligand has an adverse effect upon activity. A similar result is noted when one compares the activity of (1-phenyl indenyl) (indenyl) zirconium dichloride with that of (1-phenyl indenyl) (cyclopentadienyl) zirconium dichloride. The polymers with the highest molecular weight were produced using the metallocenes according to the invention having a trimethylsilyl substituent at the 1 position of the indenyl or a methyl substituent at the 2 position of the indenyl. Example III Another series of polymerizations were conducted using various unbridged indenyl titanium-containing metallocenes. The conditions were as set forth in Example II. The polymerization temperature was usually 30°C. The results are set forth in the following table. Run No. Complex Activity [g PE (mmol M-h)] M η [10 3 g/mol] 16 (1-PhIn)CpTiCl 2 2100 920 17 (2-PhIn)CpTiCl 2 1100 680 18 (1,2,3-Me 3 In)CpTiCl 2 390 680 830 1500 19 (1-Me 3 SiIn)CpTiCl 2 1700 1120 20 (In)(MeCp)TiCl 2 1700 not determined 21 (1-MeIn)(Cp)TiCl 2 900 2200 195 1625 A comparison of the data in Table 2 with that in Table 1 demonstrates that the titanium metallocenes according to the invention are not as active as the zirconium metallocenes according to the invention however they generally produce a higher molecular weight polymer. In contrast the applicants have observed that the hafnium metallocenes according to the invention were found to produce lower molecular weight products than comparable zirconium metallocenes according to the invention. Example IV A series of the zirconium based metallocenes according to the invention were also evaluated for their effectiveness in the polymerization of propylene. The polymerizations were also conducted in the one liter autoclave using catalyst system solutions prepared as described in Example II. In the polymerizations about 500 ml of propylene was condensed in the autoclave and stirred with about 5 ml of the commercial 30 weight percent toluene solution of methylaluminoxane. The catalyst solution was added by means of a pressure burette. The autoclave was thermostatically regulated at 0°C and the reaction mixture stirred for one hour. Then the pressure was released and the polymer dried under a vacuum. The results are summarized in the following table. Run No. Complex Activity [g PP/ (mmol M·h)] Mη [g/mol] GPC M n [g/mol] M w [g/mol] M w /M n DSC T g [°C] T m [°C] ΔH m [J/g] 13 C-NMR [%] 22 (1-PhIn)CpZrCl 2 800 75,000 30,500 80,000 2.6 -11.0 157.2 15.0 6.9 (rrrr) 7.9 (mmmm) 23 (2-MeIn)CpZrCl 2 4,100 390,000 73,100 372,000 5. -9.6 159.4 0.4 9.7 (mmmm) 24 (2-PhIn)CpZrCl 2 1,700 260,000 87,200 282,000 3.2 -10.6 142.4 3.2 7.2 (mmmm) 25 (1,3-Ph 2 In)CpZrCl 2 700 160,000 45,800 147,900 3.2 -10.3 155.3 8.6 10-7 (rrrr) The table shows that the inventive metallocenes can be used to polymerize propylene. The activity and the molecular weight of the produced polymer vary depending upon the type and position of the substituents. The relatively high melting temperatures and the low tacticity may be due to block like polymer structures. The polymer produced with (2-methylindenyl) (cyclopentadienyl) zirconium dichloride possesses an unusually broad M w /M n for a metallocene and a melting enthalpy of 0.5 J/g. This implies low crystalline percentage despite an isotactic content of 9.7%. In contrast the polymer produced with (2-phenylindenyl) cyclopentadienyl zirconium dichloride shows lower isotacticity, narrower molecular weight distribution, and a higher melting enthalpy. The metallocene of Run 25 produces a polymer having almost twice the molecular weight of the polymer produced by the metallocene used in Run 22.

Claims: An unbridged metallocene of the formula (In)(Cp)MeQ 2 , wherein In is a substituted indenyl radical having a substituent in at least one of the 1, 2, and 3 positions, said substituents being selected from hydrocarbyl radicals having 1 to 10 carbon atoms and trialkylsilyl radicals, wherein the alkyl groups have 1 to 4 carbons; Cp is an unsubstituted cyclopentadienyl radical; Me is a transition metal selected from titanium, zirconium, and hafnium; and each Q is the same or different and is selected from hydrocarbyl radicals having 1 to 12 carbon atoms, alkoxy radicals having 1 to 12 carbon atoms, aryloxy radicals having 6 to 12 carbon atoms, hydrogen, and halides, excluding the metallocene (cyclopentadienyl) (1-allylindenyl)zirconium dichloride. The metallocene of claim 1, wherein each Q is a halide, in particular wherein each Q is chloride. The metallocene of claim 1 or 2, wherein Me is zirconium, in particular wherein the metallocene is selected from (1-phenylindenyl)(cyclopentadienyl)zirconium dichloride, (1,2,3-trimethylindenyl)(cyclopentadienyl)zirconium dichloride, (2-methylindenyl)(cyclopentadienyl)zirconium dichloride, (1-trimethylsilyl indenyl)(cyclopentadienyl)zirconium dichloride, and (1,2-dimethylindenyl)(cyclopentadienyl)zirconium dichloride. A catalyst system useful for the polymerization of olefins, the catalyst system comprising the metallocene as set forth in any of the preceding claims and a cocatalyst selected from organometallic compounds of metals of Groups Ia, IIa and IIIB of the Periodic Table. The catalyst system of claim 4, wherein the cocatalyst is selected from organoaluminum compounds, in particular wherein methylaluminoxane is employed as cocatalyst. A process for polymerizing olefins, the process comprising the step of contacting at least one olefin with the catalyst system as set forth in any of claims 4 and 5. The process of claim 6, wherein the organoaluminoxane cocatalyst having repeating units of the formula wherein R is an alkyl radical having 1 to 5 carbon atoms, is employed. The process of claim 7, wherein ethylene or propylene is polymerized. The process of claim 7 or 8, wherein the polymerization is conducted under particle form polymerization conditions and/or wherein the polymerization is conducted in a continuous loop reactor. The process of any of claims 7 to 9, wherein said catalyst system is prepared by combining (1 -phenylindenyl)cyclopentadienyl zirconium dichloride or (1,2,3-trimethylindenyl)cyclopentadienyl zirconium dichloride, and the cocatalyst.

Inventors: ALT HELMUT G, SCHMID CLAUDIA, WELCH MELVIN BRUCE, ALT, HELMUT G., SCHMID, CLAUDIA, WELCH, MELVIN BRUCE
Applicants: PHILLIPS PETROLEUM CO, PHILLIPS PETROLEUM COMPANY
Application year: 1997
Main classification: C07F17
IPC codes: C07F17, C08F4, C08F10, C08F110