METHOD FOR THE PREVENTION OF SCALE FORMATION BY USING AN ETHER-1,1-DIPHOSPHONATE

Abstract: The invention is a method for the prevention of scale formation on metal or other surfaces in contact with scale-forming industrial water with an effective scale-inhibiting amount of an ether-1,1-diphosphonate of general formula (I). The invention is also a method for the prevention of corrosion on metal surfaces in contact with corrosive industrial water with an effective corrosion-inhibiting amount of an ether-1,1-diphosphonate of the same general formula. A preferred ether-1,1-diphosphonate is 1,1, diphosphono-4,7-dioxaoctane for both methods.

Description: METHOD FOR THE PREVENTION OF SCALE FORMATION BY USING AN ETHER-!,! - DIPHOSPHONATE Fipl nf the Invention The invention is a method for the prevention of scale formation on metal or other surfaces in contact with scale-forming industrial water with an effective scale-inhibiting amount of a 1,1 ether diphosphonate of the general formula: The invention is also a method for the prevention of corrosion on metal surfaces in contact with corrosive industrial water with an effective corrosion-inhibiting amount of an ether 1, 1 -diphosphonate of the same general formula. A preferred ether 1 , 1- diphosphonate is 1,1, diphosphono-4, 7-dioxaoctane for both methods. Background yf the. ϊnvention The utilization of water which contains certain inorganic impurities, and the production and processing of crude oil water mixtures containing such impurities, is plagued by the precipitation of these impurities with subsequent scale formation. In the case of water which contains these contaminants the harmful effects of scale formation are generally confmed to the reduction of the capacity or bore of receptacles and conduits employed to store and convey the contaminated water. In the case of conduits, the impedance of flow is an obvious consequence. However, a number of equally consequential problems are realized in specific utilizations of contaminated water. For example, scale formed upon the surfaces of storage vessels and conveymg lines for process -water may break loose and these large masses of deposit are entrained in and conveyed by the process water to damage and clog equipment through which the water is passed, e.g., tubes, valves, filters and screens. In addition, these crystalline deposits may appear in, and detract from, the final product which is derived from the process, e.g., paper formed from an aqueous suspension of pulp. Furthermore, when the contaminated water i s involved in a heat exchange process, as either the "hot" or "cold" medium, scale will be formed upon the heat exchange surfaces which are contacted by the water. Such scale formation forms an insulating or thermal opacifying barrier which impairs heat transfer efficiency as well as impeding flow through the system. While calcium sulfate and calcium carbonate are primary contributors to scale formation , other salts of alkaline-earth metals and the aluminum silicates are also offenders , e.g., magnesium carbona t e, barium sulfate, the aluminum silicates provided by silts of the bentonitic, illitic, kaolinitic, etc., types. Many other industrial waters , while not being scale forming, tend to be corrosive. •Such waters , when in contact with a variety of metal surfaces such as ferrous metals, aluminum, copper and its alloys, tend to corrode one or more of such metals or alloys. A variety of compounds have been suggested to alleviate these problems. Such materials are low molecular weight polyacrylic acid polymers. Corrosive waters of this type are usually acidic in pH and are commonly found in closed recirculating systems. Numerous compounds have been added to these industrial waters in an attempt to prevent or reduce scale and corrosion. One such class of materials are the well known organophosphonates which are illustrated by the compounds hydroxyethylidene diphosphonic acid (HEDP) and phosphonobutane tricarboxylic acid (PBTC). Another group of active scale and corrosion inhibitors are the monosodium phosphinicobis (succinic acids) which are described in U. S. Pat. No. 4,088,678. Most industrial waters contain alkaline earth metal cations, such as calcium, barium, magnesium, etc. and several anions such as bicarbonate, carbonate, sulfate, oxalate, phosphate, silicate, fluoride, etc. When combinations of these anions and cations are present in concentrations which exceed the solubility of their reaction products, precipitates form until these product solubility concentrations are no longer exceeded. For example, when the concentrations of calcium ion and carbonate ion exceed the solubility of the calcium carbonate reaction products, a solid phase of calcium carbonate will form. Calcium carbonate is the most common form of scale. Solubility product concentrations are exceeded for various reasons, such as partial evaporation of the water phase, change in pH, pressure or temperature, and the introduction of addition*, ions which form insoluble compounds with the ions already present in the solution. As these reaction products precipitate on surfaces of 4= water carrying system, tney form scaie or deposits. This accumulation prevents effective hea, *ansfer, interferes with fluid flow, facilitates corrosive processes and harbors bacteria. This scale is an expensive problem in many industrial water systems causing delays and shutdowns for cleaning and removal. Scale deposits are generated and extended principally by means of crystal growΛ; and various approaches to reducing scale deveiopmen, have accordingly included inhibition of crystal growth, modification of crystal growth and dispersion of the scale- forming minerals. Many organophosphorus compound .. s„ h .. a_,v .. e> h b e epe n n d αi i sscαloosseedu a < _s_ scale inhibitors. For examp.e. N.N-bis (phos P honome.hyl)-2-amino-l.propan„l and derivatives are disclosed ,„ U.S . Patent No. 5,259,974; N-substituted aminoalkane-l.l-diphosphonic acids are d,sc.osed in U.S. Patent No. 3,957,160; and propane 1,3 disphosphomc acids are d.sclosed ,„ U.S. Patent No. 4,246 , 103. A combination of a ,-hydroxypropylid=ne-U- diphosphonic acid and a water soluble polymer for controlling the deposition of scaie - imparting precipitates i ■s d A -isc ιl M os M ed ) i i„n ι Uι.S. P laa t eennt t N IN o O .. 5 J ,,500,128. Further, N- • J e ...o r.rp pn t. on of calcium carbonate scale are bis(phosphonomethyl) ammo acids for the prevent i on disclosed in U.S. Patent Nos. 5,414,112 and 5,478,476. 1,1 diphosphonic acid compounds are disclosed in U.S. Patent Nos. 3,617,576, 4,892,679 and 4,172,787. However, the ether 1, 1-diphosphonates described herein are structurally different from the compounds cited above. One advantage of the ether 1, 1-diphosphonates over conventional treatments is that they can be used in conjunction with other water treatment agents such as biocides, without causing significant degradation of those other treatment agents. Furthermore, the diphosphonates described herein are more efficient than conventional treatments. Summary of the Invention The present invention provides a method for preventing scale formation on metal surfaces in contact with scale- forming industrial water characterized by treating said water with an effective scale-inhibiting amount of an ether 1,1-diphosphonate of formula (I) R 3 wherein R 4 is selected from the group consisting of hydrogen and C 1 -C 3 alkyl groups; R 2 and R 3 are selected from the group consisting of hydrogen and methyl; R 5 is selected from the group consisting of hydrogen, metal cations and ammonium cations; and R x is selected from the group consisting of C,.- C 30 alkyl groups and C 1 -C 30 ethers. The present invention also provides a method for preventing corrosion on metal surfaces in contact with corrosive industrial water characterized by comprising treating said water with an effective corrosion- inhibiting amount of an ether 1,1-diphosphonate of formula (I) R3 wherein R 4 is selected from the group consisting of hydrogen and Ci-C; } alkyl groups; R 2 and R 3 are selected from the group consisting of hydrogen and methyl; R 5 is selected from the group consisting of hydrogen, sodium, metal cations and ammonium cations ; and Rj . is selected from the group consisting of C 1 -C 30 alkyl groups and C 1 -C 30 ethers. The present invention further provides a method for preventing scale formation on metal surfaces in contact with scale-forming industrial water characterized by treating said water with an effective scale-inhibiting amount of an ether 1,1-diphosphonate of formula (I) 3 wherein R 4 is selected from the group consisting of hydroxy, amino and alkylamino; R 2 and R 3 are selected from the group consisting of hydrogen and methyl; R 5 is selected from the group consisting of hydrogen, sodium, metal cations and ammonium cations; and R x is selected from the group consisting of C C-jr . alkyl groups and C^-C^o ethers . The present invention also provides a method for preventing corrosion on metal surfaces in contact with corrosive industrial water characterized by treating said water with an effective corrosion-inhibiting amount of an ether 1 , 1-diphosphonate of formula (I) wherein R 4 is selected from the group consisting of hydroxy, amino and alkylamino; R 2 and R 3 are selected from the group consisting of hydrogen and methyl; R 5 is selected from the group consisting of hydrogen, sodium, metal cations and ammonium cations; and R x is selected from the group consisting of C J -C JQ alkyl groups and C 1 -C 30 ethers. Lastly the present invention provides an ether 1,1- diphosphonate of the formula R. R 4 .P0 3 (R 5 ) 2 R. CH (I) O 'CH O 3 (R 5 ) 2 wherein R 2 , R 3 , R 4 and R 5 are hydrogen and Rj, is methyl, Description of the Inventipn The invention is a method for preventing scale formation on metal surfaces in contact with scale-forming industrial water which comprises treating said water with an effective scale- inhibiting amount of an ether 1,1- diphosphonate of formula (I) wherein R 4 is selected from the group consisting of hydrogen and Cx-C, alkyl groups; R 2 and R 3 are selected from the group consisting of hydrogen and methyl; R 5 is selected from the group consisting of hydrogen, metal cations and ammonium cations ; and R x is selected from the group consisting of C x - C 30 alkyl groups and C-,. ethers. The industrial water may be cooling water, or industrial process water. A preferred ether 1, 1 -diphosphonate is 1, 1- diphosphono - 4, 7 - dioxaoctane. The scale may be calcium carbonate. The cooling water may contain a biocide. Moreover, the cooling water may contain other corrosion inhibitors, or other scale inhibitors. The invention is also a method for preventing corrosion on metal surfaces in contact with corrosive industrial water which comprises treating said water with an effective corrosion-inhibiting amount of an ether 1, 1 -diphosphonate of formula (I) R 2 R 4 P0 3 (R 5 ) 2 R . . CH . C (I) O ^CH P0 3 (R 5 ) 2 *3 wherein R A is selected from the group consisting of hydrogen and C,-C 3 alkyl groups; R 2 and R 3 are selected from the group consisting of hydrogen and methyl; R 5 is selected from the group consisting of hydrogen, sodium, metal cations and ammonium cations; and R, is selected from the group consisting of C r C 30 alkyl groups and C r C 30 ethers. The industrial water may be cooling water, or industrial process water. A preferred ether 1, 1 -diphosphonate is 1, 1 - diphosphono - 4, 7 - dioxaoctane. The cooling water may contain a biocide. Moreover, the cooling water may contain other corrosion inhibitors, or other scale inhibitors. The invention is also a method for preventing scale formation on metal surfaces in contact with scale-forming industrial water which comprises treating said water with an effective scale-inhibiting amount of an ether 1, 1 -diphosphonate of formula (I). 3 wherein R, is selected from the group consisting of hydroxy, amino and alkylamino; R 2 and R 3 are selected from the group consisting of hydrogen and methyl; R 5 is selected from the group consisting of hydrogen, sodium, metal cations and ammonium cations; and R, is selected from the group consisting of C,-C 30 alkyl groups and C,-C 30 ethers. The industrial water may be cooling water, or industrial process water. The scale may be calcium carbonate. The cooling water may contain a.biocide. Moreover, the cooling water may contain other corrosion inhibitors, or other scale inhibitors. The invention is also a method for preventing corrosion on metal surfaces in contact with corrosive industrial water which comprises treating said water with an effective corrosion-inhibiting amount of an ether 1, 1 -diphosphonate of formula (I). R 3 wherein R 4 is selected from the group consisting of hydroxy, amino and alkylamino; R 2 and R 3 are selected from the group consisting of hydrogen and methyl; R 5 is selected from the group consisting of hydrogen, sodium, metal cations and ammonium cations; and R, is selected from the group consisting of C r C 30 alkyl groups and C r C 30 ethers. The industrial water may be cooling water. The cooling water may contain a biocide. Moreover, the cooling water may contain other corrosion inhibitors, or other scale inhibitors. The invention is also an ether 1, 1 diphosphonate of the formula 3 wherein R 2 , R 3 , R,, and R 5 are hydrogen and R, is methyl. Examples of compounds wherein R, is hydrogen or alkyl include 1,1- diphosphono-4-oxapentane, 2,2-diphos P hono-5,8-dioxanonane, and 2,2-diphosphono-5- oxahexane. Examples of compounds wherein R, is hydroxy, amino or alkylamino include l ,l-diphosphono-l-hydroxy-4,7-dioxaoctane, l-amino-l,l-di P hosphono-4,7- dioxaoctane, 1,1 -diphosphono- 1 -hydroxy-4-oxa P entane and l.amino-U-diphosphono-4- oxapentane. As used herein, the term metal cations refers to cations of sodium, potassium , calcium and magnesium among others. Typical metal surfaces in cooling water systems which may be subjected to corrosion or scale depos i tion are made of stainless steel, mild steel and copper alloys such as brass among others. The method may be effective against other types of scale including magnesium silicate , calcium sulfate. barium sulfate. and calcium o_ata.e. The phosphonates are also effective in extremely hard water. The method may be utilized in conjunction with other treatments, for example biocides. Stabilized bleach, chlorine, and hypobromite are applicable oxidizing biocides. Glutaraldehyde and mixtures of 5-chloro-2-methyl-4-isothiazolin-3-one and 2-methyl-4- isothiazolin-3-one are applicable non-oxidizing biocides. Additionally, the method may be utilized in conjunction with other corrosion and scale inhibitors. Thus, the phosphonates may be effective in combination with other inhibitors such as HEDP, PBTC, MDP, hexamethylenediamine-N,N,N'N'-tetra(methylenephosphonic acid), amino and trisCmethylenephosphonic acid). The phosphonates may also be effectively utilized in conjunction with other polymeric treating agents, for example anionic polymers of under 200,000 MW. Such polymers include acrylic, methacrylic or maleic acid containing homo-, co- or ter-polymers. The phosphonates may be added to the scale-forming or corrosive industrial process water in an amount from about 0.01 ppm to about 500 ppm. Preferably, the phosphonates may be added in an amount from about 0.01 ppm to 50 ppm. Most preferably , the phosphonates may be added in an amount of from about 1 ppm to about 25 ppm. The following examples are presented to describe preferred embodiments and utilities of the invention and are not meant to limit the invention unless otherwise stated in the claims appended hereto. f Yfl m le 1 The following is a procedure for the synthesis of l,l-diphosphono-4, 7- dicxaoctane (DPDO). Under an inert nitrogen atmosphere, sodium hydride (2.01 g, 0.088 mole) was combined with 200mL dry tetrahydrofuran (THF) in a three-necked 500 mL roundbottcm flask equipped with a nitrogen sweep and magnetic stirrer. The resulting suspension was cooled to -10°C in an ice/salt bath and stirred. A solution of tetraisopropyl methylenediphosphonate (27.5 g, 0.08 mole) dissolved in 30 mL dry THF was then added dropw i se over a 90 minute period via an addition funnel. The reaction mixture was then allowed to stir for 30 min at -10°C and 1 hour at room temperature. A solution of l-bromo-2-(2-methoxyethoxy)ethane (16.8 g, 0.092 mole) dissolved in 25 mL dry THF was then added dropwise over a 1 hour period. The reaction solution was then allowed to stir for 2 hours at room temperature and overnight (18 hours) at reflux. The reaction was then quenched with 5 mL 10 wt % ammonium chloride, f i ltered, concentrated , and dissolved in 500mL ethyl acetate. The ethyl acetate solution was washed in a separatory funnel with saturated sodium chloride, dried with magnesium sulfate. f i ltered, and concen t rated to 33.1 g amber oil product. The product was compr i sed of a mixture of the tertraisopropyl ester of 1, l-diphosphono-4, 7-dioxaoctane / tetraisopropyl methylenediphosphonate / phosphorus-containing byproducts in a 56/35/9 mole ratio , along with some unreacted bromo-2-(2-methoxyethoxy)ethane. The intermediate alkylation product mixture (32 g) described above was placed in a 2L round bottom flask. A solution of 5% hydrochloric acid (836 g) containing cetyltrimethylammonium chloride (0.020 g) was then added slowly with stirring. The reaction was then heated to reflux and stirred for 24 hours. The reaction solution was then concentrated to 19.4 g oil, then dissolved in water to a total weight of 149 g. The product was analyzed for total phosphorus content and by phosphorus and carbon NMR, which showed a 9.2 wt % mixture of DPDO/(MDP) methylene diphosphonate/ phosphorus-containing byproduct in a 54/38/8 mole ratio. Example 2 The intermediate alkylation product mixture described in Example 1 , containing the isopropyl esters of DPDO and MDP, was purified by fractional distillation under reduced pressure. The purified tetraisopropyl ester of DPDO was collected at 145°C head t empera t ure/0.08 mm Hg . To 1.9 g of pure DPDO ester (92/0/8 DPDP ester MDP es t er/phosphorus-containing byproduct by phosphorus NMR) was added 5% hydrochloric acid (49.6 E) containing cetyltrimethylammonium chloride (0.010 g). The mixture was stirred and heated to reflux for 48 hours, concentrated to an oil, and dissolved in water to a total weight of 7.6 g. The product was analyzed for total phosphorus content and by phosphorus and carbon NMR. which showed a 13.8 wt % mixture of DPDO MDP/ phosphorus-containing byproduct in a 91/0/9 mole rat i o. F,χ?mple 3 A hardness solution of cεlcium and magnesium in a 2:1 Ca:Mg ratio in water was prepared, along with an alkaline solution of sodium carbonate/sodium bicarbonate buffered at pH 10. Both solutions were simultaneously added to 200 mL of an inhibitor test solution. The pH of the inhibitor test solution was adjusted to between 7 and 10. Calcium carbonate precipitation was detected by turbidity using a Brinkman PC-800 Colorimeter (420 nm wavelength) which was connected to a strip chart recorder. The hardness solution was prepared j by , „ a Λ d A d;i„n Γ g, 3 T.. R 8Π0 g σ r caal l cci i uumm a acwe : tate and 2.57 g magnesium acetate tetrahydrate to distilled water (100 mL total volume). The alkal i ne solution was prepared by adding 2.01 g sod t um bicarbonate and 1.27 g sodium carbonate to distilled water (100 mL total volume). A Masterflex pump delivered the hardness and alkaline solutions at 2.0 mL/min to the magnetically stirred test solution. All solutions were aqueous and maintained at a constant temperature of 45°C. The titration endpoint, expressed as the maximum calcium concentration (as calcium carbonate) before the onset of t urbid i ty , was calculated from the elapsed time to a turbid i ty inflection on the strip chart recorder. Higher endpo i nt values indicate a compound's increased ability to prevent scale precipitation. The test results, presen .te A d u b 0 eιlo„„w, , i n n T I a ah bllee 1 l , i mndicate that the inhibitors of t he instant invention are superior to th . e curre „nt.l .,y, n ucsperdi t trrpeRattmmeennt t a ageents PBTC and HEDP. TABLE I 1 = 1, l-ciiphosphono-4, 7-dioxaoctane, synthesized according to the procedure in Example 1 2 = 2-phosphonobutane- 1 , 2, 4-tricarboxylic acid 3 = 1-hydroxyethylideπe-l, 1-diphosphonic acid 4 = 1, l-diphosphono-4,7-dioxaoctane, synthesized according to the procedure in Example 2 Example 4 The constant composition technique was used to evaluate relative compound effectiveness regarding crystal growth inhibition. This method uses seed crystals which are introduced into a supersaturated solution of the seed components and measures growth rates as titrants are consumed during the crystallization process. The procedure is outlined as follows. A supersaturated solution of calcium and carbonate (s = 3.3) is made in a double-walled glass cell with recirculating water to maintain a constant temperature. The mixing is done slowly to insure metastabilty. The ionic strength is then adjusted with NaCl and the pH brought up to the desired value with dilute NaOH. Calcium carbonate seed crystals are then added. Characterization of the seed by scanning electron microscopy and triple point BET analysis indicated the particles were normal rhombohedrons c.a. 10 μ on a side and had a specif i c surface area of 0.38 m 2 /gm. As the experiment runs, calcium and carbonate/bicarbonate titrants are fed to maintain a pH of 8.5. The titrant concentrations are chosen so that the feed rate is not too fast or slow (typically 0.01 M for 100 mg seed or 0.1 M for 1 g seed) and are corrected for the subsequent dilution of each by the other. The consumption of titrants is measured as a function of time to obtain the growth rate. Inhibitor is typically added after 5 mis of both titrants have been fed so that the intrinsic growth rate can be observed prior to inhibitor addition. Data is analyzed by multiplying the X values (time) by a normalization factor. This factor is obtained by dividing the slope observed just before inhibitor addition by an average slope determined from six replicate measurements. This operation compensates for different initial growth rates which are very dependent upon specific seed surface area and other environmental factors. The resulting data is a quantitative number (induction time) describing the relative ability of a particular compound to inhibit crystal growth. To obtain the results of Table II, the above described procedure was used to determine the crystal growth inhibition of 500 mg of calcite seed in a total water volume of 305 mis . 0.2 ppm of each inhibitor to be tested was added to the calcite containing solution. The results of Table II show that the l,l-diphosphono-4,7-dioxaoctane inhibitor of the instant invention (Example 2) gives a surprisingly long inhibition time, and is among the most effective inhibitors tested. The superior inhibition of the inhibitor described in Example 2 compared to a structurally similar compound, 3,6,9-trioxa-l- hydroxydecone-l ,l-diphosphonic acid as disclosed in U. S. 4,892,679 was unanticipated and demonstrates the novel aspect of this invention. TABLE II Calcite Crystal Growth Inhibition Results Inhibitor Inhibition Time (min) -hydroxyethylidene-l ,l-diphosphonic acid 1000 900 Example 2 2-phosphonobutane-l, 2, 4 tricarboxylic acid 800 amino tris methylene phosphonic acid 550 3.6.9-trioxa- 1 -hydroxydecane- 1 , 1 -diphosphonic acid 400 1 = 1.1 -diphosphono-4, 7-dioxaoc t ane, synthesized according to the procedure in Example 2. Example 5 The stability of a potential inhibitor towards oxidation by biocides is an important fac t or with regard to performance in an actual cooling tower environment. In order to assess the rela t ive stabili t y of this new chemistry, its degradation to inorganic phosphate was measured in the presence of hypochlorite. A synthetic wa t er was made consisting of 500 ppm calcium, 250 ppm magnesium, and 500 pm " M" alkalinity (bicarbonate), all as CaCO 3 . The inhibitor was added at 25 ppm, as actives, prior to the bicarbonate to aid in preventing precipitation. Sodium hypochlorite, as a 5.25% bleach solution was then added so that a free residual of 40 ppm was measured in a blank solution using the Hach DPD method (N,N-diethyl- P - phenylenediamine indicator). The data in Table III shows the percent depletion of hypochlorite after 24 hours which, assuming pure compounds, is a function of the stability of the molecule. The results show that DPDO is stable in the presence of oxid i zing biocides, producing no hypochlorite depletion over a 24 hour penod. Structurally similar ether phosphonates such as N,N-bis(phosphonomethyl)-2-amino-l- propanol methyl ether as disclosed in U. S. 5,259,974 are unstable and consume 100% of the hypochlorite as they decompose. TABLE III Chlorine Stability Results Inhibitor % Depletion Blank 0 Example 2 2-phosphonobutane-1.2.4-tricarboxylic acid 1 -hydroxyethylidene- 1 , 1 -diphosphonic 21 acid morpholinomethane-diphosphonic acid 25 N, N-bis(phosphonomelhyl)-2-amino-l- 100 propanol methyl ether ample 6 The following dispersancy test procedure was utilized to obtain the results shown in Table IV. 200 mL of a test solution containing 20 ppm of a modif i ed polyacrylate polymer dispersant and 20 ppm of phosphonate inhibitor(s) dissolved in distilled water was prepared. Then, the test solution was added to a 250 mL erlenmeyer flask magnetically stirred at 40 °C. Hardness and m-alkalinity were added to the solution over seven minutes to achieve a final solution composition (ppm as CaCO 3 ) of 700 ppm Ca + , 350 ppm Mg 2+ , and 700 ppm CO 3 2 \ As calcium carbonate precipitation proceeds, a particle monitor responds to the fraction of calcium carbonate particles greater than 0.5 microns in diameter. The more effectively dispersed the calcium carbonate particles, the lower the fraction of large particle agglomerates. Better performing test solutions are indicated by (1) lower particle monitor intensities, and (2) intensity maxima achieved at times > 60 minutes. The results show that DPDO is the best performing phosphonate for enhancing calcium carbona t e particle dispersancy because it generates (1) the smallest particle monitor intensity and (2) the signal maximum is reached at a time > 60 minutes. Moreover , the addition of DPDO to the other phosphonates enhances the dispersancy performance of those test solutions by (1 ) reducing the particle monitor intensity and (2) pos t poning the signal maximum to times > 60 minutes. Table TV time Phosphonate (20 ppm total actives) Particle Monitor Intensity Blank 100 10 minutes methylene diphosphonate 67 20 minutes I -hvdroxv ethylidene- 1 , 1 -diphosphonic acid 68 20 minutes -phosphonobutane- 1,2.4 tricarboxylic acid 56 45 minutes > 60 minutes Example 2 Example 1 29 > 60 minutes > 60 minutes 1 -hydroxyethylidene- 1 ,1 -diphosphonic acid 1 -diphosphono-4,7-dioxaoctane > 60 minutes 2-phosphonobutane- 1,2,4 tricarboxylic acid + l-diphosphono-4,7-dioxaoctane 1. Blank : 20 ppm polymer dispersant; phosphonate mixtures contain 60 mole% DPDO. Example 7 The following procedure was utilized to determine the calcium tolerance of phosphono group containing compounds. Two solutions were made up. The first contained 1000 mL of a 1000 ppm Ca solution (as CaC0 3 ) at a bath temperature of 45°C was ad j us t ed to pH 10.5 by dropw.se addition of dilute NaOH. The second conta i ned 1000 mL of a 1000 ppm inhibitor solution at a bath temperature of 45'C was adjusted to pH 10.5 by dropwise addition of dilute NaOH. The second solution was added to the first solution wh .ic ,h was magne .t•ica I lly, s ctiirr-perdi, n att a a r raat t ee o ofn 1.0 u m i L/min with the solution t ransmittance record _,ed __ a .t a wa „v » ele n n r g, Λ th n o f t i 4?/0υ n nmm. Th » e c endp p oint is reached when enough calcium phosphonate prec .ipi .tat -ion occ „u r r c s f t n o " r cilmouidα" t mhee s > o υ l_ution to 96% of the initial ' t ransmittance. The results were summarized in Table V. It is evident that the DPDO prevents precipitation for a much longer time than other currently available treatments. TABLE V 3 = l . l-dιphosphone-4,7-dioxaoctane, synthesized according to the procedure in Example Changes can be made in the composition, operation and arrangement of the method of the present invention described herein without departing from the concept and scope of the invention as defined in the following claims:

Claims: C AIMS 1. A method for preventing scale formation on metal surfaces in contact with scale- forming industrial water characterized by treating said water with an effective scale- inhibiting amount of an ether 1,1-diphosphonate of formula (I) wherein R 4 is selected from the group consisting of hydrogen and Ci-Cj alkyl groups; R 2 and R 3 are selected from the group consisting of hydrogen and methyl; R 5 is selected from the group consisting of hydrogen, metal cations and ammonium cations; and Ri is selected from the group consisting of c^- C 30 alkyl groups and C^-C JO ethers. 2. The method of claim 1, characterized in that the industrial water is selected from cooling waters and industrial process waters. 3. The method of claim 1, characterized in that the ether 1,1-diphosphonate is l, l-diphosphono-4, 7 -dioxaoctane. 4. The method of claim 1, characterized in that the scale is calcium carbonate. 5. The method of claim 2, characterized in that the cooling water contains treatment chemicals selected from biocides, corrosion inhibitors or other scale inhibitors. 6. A method for preventing corrosion on metal surfaces in contact with corrosive industrial water characterized by comprising treating said water with an effective corrosion-inhibiting amount of an ether 1,1- diphosphonate of formula (I) R • 3 wherein R 4 is selected from the group consisting of hydrogen and C 1 -C 3 alkyl groups; R 2 and R 3 are selected from the group consisting of hydrogen and methyl; R 5 is selected from the group consisting of hydrogen, sodium, metal cations and ammonium cations; and R x is selected from the group consisting of C 1 -C 30 alkyl groups and C^-C^o ethers. 7. The method of claim 6, characterized in that the industrial water is selected from cooling waters and industrial process waters. 8. The method of claim 9, characterized in that the ether 1,1-diphosphonate is 1, l-diphosphono-4, 7 -dioxaoctane. 9. The method of claim 6 , characterized in that the cooling water contains treatment chemicals selected from biocides, corrosion inhibitors or other scale inhibitors. 10. A method ' for preventing scale formation on metal surfaces in contact with scale-forming industrial water characterized by treating said water with an effective scale-inhibiting amount of an ether 1,1-diphosphonate of formula (I) R 3 wherein R 4 is selected from the group consisting of hydroxy, amino and alkylamino; R 2 and R 3 are selected from the group consisting of hydrogen and methyl; R 5 is selected from the group consisting of hydrogen, sodium, metal cations and ammonium cations; and R x is selected from the group consisting of C 1 -C 30 alkyl groups and Ci-C o ethers. 11. The method of claim 10, characterized in that the industrial water is selected from cooling waters and industrial process waters. 12. The method of claim 10, characterized in that the scale is calcium carbonate. 13. The method of claim 11, characterized in that the cooling water contains treatment chemicals selected from biocides, corrosion inhibitors or other scale inhibitors. 14. A method for preventing corrosion on metal surfaces in contact with corrosive industrial water characterized by treating said water with an effective corrosion-inhibiting amount of an ether 1,1-diphosphonate of formula (I) R, wherein R 4 is selected from the group consisting of hydroxy, amino and alkylamino; R 2 and R 3 are selected from the group consisting of hydrogen and methyl; R 5 is selected from the group consisting of hydrogen, sodium, metal cations and ammonium cations; and Ri is selected from the group consisting of C 1 -C 30 alkyl groups and Cx^o ethers. 15. The method of claim 14, characterized in that the industrial water is selected from cooling waters and industrial process waters. 16. The method of claim 14, characterized in that the cooling water contains treatment chemicals selected from biocides , corrosion inhibitors and scale inhibitors . 17. An ether 1,1-diphosphonate of the formula R. wherein R 2 , R 3 , R 4 and R 5 are hydrogen and R x is methyl.

Inventors: CARTER PHILLIP W, DAVIS RONALD V, KAMRATH MICHAEL A, REED PETER E, CARTER, PHILLIP, W., DAVIS, RONALD, V., KAMRATH, MICHAEL, A., REED, PETER, E.
Applicants: NALCO CHEMICAL CO, NALCO CHEMICAL COMPANY
Application year: 1997
Main classification: C02F5
IPC codes: C02F5, C07F9