ELASTOMERS, PROCESSES FOR THEIR MANUFACTURE, AND ARTICLES MADE FROM THESE ELASTOMERS

Abstract: Processes for making at least partially vulcanized elastomers and melt processible thermoplastic compositions comprising such elastomers, and elastomers, compositions, and rubbery articles obtainable via such processes, are described. These elastomers are obtainable by at least partially crosslinking an elastomeric polymer containing reactive substituents with a crosslinking agent having a number average molecular weight less than about 2000, containing two or more reactive substituents differing from those contained in the elastomeric polymer, each of the reactive substituents being selected from the group consisting of carboxylic acid, carboxylic anhydride, carboxylic acid salt, carbonyl halide, hydroxy, epoxy, and isocyanate such that those of the elastomer will react with those of the crosslinking agent to at least partially crosslink the elastomer. Melt-processible thermoplastic compositions are disclosed which are obtainable by combining these elastomers with a thermoplastic polymer, such as by dynamic vulcanization of these elastomers in the presence of a thermoplastic polymer.

Description: ELASTOMERS, PROCESSES FOR THEIR MANUFACTURE, AND ARTICLES MADE FROM THESE ELASTOMERS This invention relates to elastomers, and processes for making and products made from elastomers In one aspect, the invention relates to crosslinking functionalized elastomers In another aspect, this invention relates to elastomers cross nked with a compound other than sulfur or a peroxide. In yet another aspect, this invention relates to processes for making melt processible thermoplastic vulcanized compositions capable of forming elastomeric products, processes for making elastomeric products and products made from these processes Traditionally, elastomers have been crosslmked (also known as vulcanized) using either (i) a free radical curing system initiated by radiation or a peroxide or (n) sulfur, but the resulting products have often been unsatisfactory for one or more of several reasons For example, low molecular weight byproducts (which can have detrimental effects on the physical properties of the crosshnked elastomer) are often produced with free radical curing systems, and sulfur-cross nked elastomers can have odor and color problems as well as less than desirable heat aging stability and weatherability characteristics due to unsaturation in the polymer chain and/or weak sulfur linkages. Alternative crosslinking systems have been proposed, for example US-A-4, 801 ,647 discloses crosslinking an ethylene-propylene- diene elastomer grafted with maleic anhydride with diamine crosslinking agents, but the development of other elastomer crosslinking systems is still of interest to many end-users of elastomers. Thermoplastic vulcanizates (TPV's) are well known, e.g. Santoprene'^ thermoplastic rubber which is a mixture of crosshnked EPDM particles in a crystalline polypropylene matrix manufactured by Advanced Elastomer Systems. These materials have found utility tn many applications which previously used vulcanized rubber, e.g. hoses, gaskets, etc. TPV's are noted for their processability as thermoplastics while retaining the excellent tensile and compression set properties of vulcanized rubbers. The TPV's available today are based on vulcanized rubbers in which a phenolic resin or sulfur cure system is used to vulcanize, i e. crosslink, a diene (or more generally, a polyene) copolymer rubber by way of dynamic vulcanization, i.e. crosslinking while mixing (typically vigorously), in a thermoplastic matrix. These methods are preferred over peroxide free radical cure systems because if the thermoplastic is polypropylene, then the peroxide degrades the polypropylene and if the thermoplastic is polyethylene, then the peroxide crosslinks the polyethylene as well as the rubber and this in turn limits the extent of rubber crosslinking that can occur before the entire mixture is no longer thermoplastic. According to this invention, an at least partially crosshnked elastomer comprises the reaction product of (i) an elastomeric polymer containing reactive substituents and (u) a crosslinking agent (also known as a vulcanizing agent) (a) containing two or more reactive substituents differing from those contained in the elastomeric polymer and (b) having a number average molecular weight of less than about 2000, each of the reactive substituents selected such that those of the elastomer will react with those of the crosslinking agent to at least partially crosslink the elastomer, and each of the reactive substituents are selected from the group consisting of carboxyiic acid, carboxyiic anhydride, carboxyiic acid salt, carbonyl halide, hydroxy, epoxy, and isocyanate Another aspect of this invention is a process comprising the step of dynamically vulcanizing (i) at least one of the elastomeric polymers containing reactive substituents with (u) at least one of the crosslinking agents containing two or more reactive substituents, in the presence of at least one thermoplastic polymer, and the melt processible thermoplastic compositions obtainable by that process Melt processible thermoplastic compositions according to this invention are also obtainable by a process comprising the step of blending at least one of the partially crosshnked elastomers with at least one thermoplastic polymer Another aspect of this invention is a melt processible thermoplastic composition, the composition comprising (A) 5 to 95 wt % of at least one thermoplastic polymer, and (B) 95 to 5 wt % of at least one of the above partially vulcanized (i e , partially crosshnked) elastomers The present invention also includes articles comprising at least one of the at least partially crosshnked elastomers or melt processible compositions of this invention, and the shaping of these articles, preferably in a melt processing operation Figure 1 shows Monsanto ODR torque versus time plots for two different polymer melt compositions mixed with a Rheomix 600 mixer at 60 rpm at 1 10 C The solid plot line represents a melt composition comprising ethylene 1 -octene elastomeric polymer grafted with 2 wt % maieic anhydride (MAH) and Irganox™ B900 antioxidant, and the interrupted plot line represents the same melt composition with 6 4 wt % glycidyl ether of bisphenol A having an epoxide equivalent of 176-183 (DER 383 commercially available from The Dow Chemical Co ) as described in Example 4 of this invention "Polymer' means a large molecule made from a number of repeating units termed monomers "Homopolymer" means a polymer made from one kind of monomer "Interpolymer" means a polymer made from two or more kinds of monomers, and includes "copolymers" which are made from two kinds of monomers "terpolymers" which are made from three kinds of monomers, and the like "Elastomeric polymer" means a polymer that can be stretched with the application of stress to at least twice its length and after release of the stress returns to its approximate original dimensions and shape The elastic recovery of an elastomeric polymer prior to vulcanization is generally at least 40%, preferably at least 60%, and more preferably at least 80% when measured according to ASTM D-412 Suitable elastomeric polymers for use in this invention include ethylene/ -olefin interpolymers, isoprene rubbers such as polyisoprene (including natural rubber) and isobutylene/isoprene rubber (butyl rubber), polychloroprene, butadiene rubbers such as polybutadiene, styrene/butadiene rubber, and acrylonitnle/butadiene rubber and block copolymer rubbers such as styrene/isoprene/styrene tnblock, styrene/butadiene/styrene tnblock, and hydrogenated styrene/butadiene/styrene block, e g styrene/ethylene/butene/styrene block copolymer " -Olefin" means a hydrocarbon molecule or a substituted hydrocarbon molecule (i e a hydrocarbon molecule comprising one or more atoms other than hydrogen and carbon, e g halogen, oxygen, nitrogen, etc ), the hydrocarbon molecule comprising (i) only one ethylenic unstaturation, this unsaturation located between the first and second carbon atoms, and (n) at least 3 carbon atoms, preferably of 3 to 20 carbon atoms in some cases preferably of 4 to 10 carbon atoms and in other cases preferably of 4 to 8 carbon atoms Examples of preferred α-olefins from which the elastomers used in this invention are prepared include propylene, 1-butene, 1-pentene, 1-hexene, 1-octene, 1-dodecene, and mixtures of two or more of these monomers Preferred among the elastomeric polymers useful in the practice of this invention are the ethylene/α-oleftn interpolymers particularly those having a density less than about 0 9 g/cm 3 Preferred ethylene interpolymers include ethylene/α-olefin copolymers, ethylene/α-olefin/diene terpolymers; and interpolymers of ethylene and one or more other monomers which are copolymenzable with ethylene, such as ethylenically unsaturated carboxyiic acids (both mono- and difunctional) and their corresponding esters and anhydrides, e g acrylic acid, methacry c acid, vinyl ester (e g , vinyl acetate) and maieic anhydride, and vinyl group-containing aromatic monomers such as styrene Included among these polymers are (i) heterogeneous linear low density ethylene interpolymers (heterogeneous LLDPE) made using Ziegler- Natta catalysts in a slurry, gas phase, solution or high pressure process such as described in US-A-4 076,698, and (n) homogeneous linear ethylene polymers such as (a) those described in US-A-3,645,992, and (b) those made using the so-called single site catalysts in a batch reactor having relatively high olefin concentrations as described, for example, in US-A-5, 026,798 and US-A-5, 055,438 Such polymers are commercially available Representative of commercially available homogeneous linear ethylene polymers are TAFMER™ made by Mitsui Petrochemical Industries, Ltd and EXACT™ made by Exxon Chemical Co Especially preferred ethylene/α-olefin interpolymers are ethylene/1- octene, ethylene/1-hexene, ethylene/1-butene and ethylene/propylene copolymers produced via a constrained geometry single site catalyst A process for making such copolymers is described in UA-A-5,272,236 and US- A-5,278,272 Such ethylene interpolymers are preferably substantially linear olefin polymers having long chain branching Substantially linear olefin polymers can be made by gas phase, solution phase, high pressure or slurry polymerization These polymers are preferably made by solution polymerization Substantially linear ethylene polymers (SLEP's) are commercially available from The Dow Chemical Co. under the trademark AFFINITY and from DuPont Dow Elastomers L.L C. under the trademark ENGAGE "Substantially linear polymer" means that the polymer backbone contains long chain branching and is substituted with an average of up to 3 long chain branches/1000 carbons Preferred substantially linear polymers are substituted with about 0 01 to about 3 long chain branches/1000 carbons, more preferably from about 0 01 to about 1 long chain branches/1000 carbons, and especially from about 0 3 to about 1 long chain branches/1000 carbons These substantially linear polymers are characterized by. a) a melt flow ratio, l 10 /l 2 , > 5 63, b) a molecular weight distribution, M w /M n , defined by the equation M w /M n < (l 10 /l 2 ) - 4 63, and c) a critical shear stress at onset of gross melt fracture of greater than about 4 x 10 6 dyne/cm 2 "Long chain branching" means a pendant carbon chain having a chain length of at least 6 carbons, above which the length cannot be distinguished using 13 C nuclear magnetic resonance spectroscopy The long chain branch can be as long as about the length of the polymer backbone to which it is attached The presence of long chain branching can be determined in ethylene homopolymers by using 13 C nuclear magnetic resonance (NMR) spectroscopy and is quantified using the method of Randall (Rev Macromol Chem Phys , C29 (2&3), p 285-297) However as a practical matter, current 13 C nuclear magnetic resonance spectroscopy cannot determine the length of a long chain branch in excess of six carbon atoms For ethylene α-olefin copolymers, the long chain branch is longer than the short chain branch that results from the incorporation of the α-olefιn(s) into the polymer backbone For example, a substantially linear ethylene/1-octene copolymer has a short chain branch length of six (6) carbons, but a long chain branch length of at least seven (7) carbons The SLEP's preferably comprise from about 95 to 50 weight percent (wt %) ethylene, and from about 5 to 50 wt% of at least one α-olefin comonomer, more preferably from 10 to 35 wt% of at least one α-olefin comonomer The comonomer content is measured using infrared spectroscopy according to ASTM D-2238, Method B Typically, the SLEP's are copolymers of ethylene and an α-olefin of 3 to about 20 carbon atoms (e g , propylene, 1-butene 1-hexene, 4-methyl-1-pentene, 1-heptene 1- octene, styrene, etc ), preferably of 3 to about 10 carbon atoms, and more preferably these polymers are a copolymer of ethylene and 1-octene The density of these substantially linear ethylene polymers is preferably in the range from about 0 85 to about 0 9, more preferably from about 0 85 to about 0 88, grams per cubic centimeter (g/cm 3 ) determined by ASTM D-792 The melt flow ratio, measured as l 10 /l 2 as defined in ASTM D-1238, Conditions 190C/10 kg and 190C/2 16 kg (formerly known as "Conditions (N) and (E)", respectively and also known as l 10 and l 2 , respectively), is greater than or equal to 5.63, and is preferably in the range from about 6.5 to 15, more preferably in the range from about 7 to 10. The molecular weight distribution (M w /M π ), measured by gel permeation chromatography (GPC), is preferably in the range from about 1 5 to 2.5. For substantially linear ethylene polymers, the l 10 /l 2 ratio indicates the degree of long-chain branching, i.e. the larger the l 10 /l 2 ratio, the more long-chain branching in the polymer A unique characteristic of the homogeneously branched, substantially linear ethylene polymers is the highly unexpected flow property where the l 10 /l 2 value of the polymer is essentially independent of the polydispersity index (i.e., M w /M n ) of the polymer. This is contrasted with conventional linear homogeneously branched and linear heterogeneously branched polyethylene resins having rheological properties such that to increase the l 10 /l 2 value the polydispersity index must also be increased Substantially linear olefin polymers have a critical shear rate at onset of surface melt fracture of at least 50 percent greater than the critical shear rate at the onset of surface melt fracture of a linear olefin polymer having about the same l 2 , M w /M n , and density. By "about the same" is meant that each value is within 10 percent of the comparative value The preferred melt index, measured as l 2 (ASTM D-1238, condition 190/2.16 (formerly condition E)), is from about 0.1 g/10 mm to 200 g/10 mm, more preferably 0.1 to 20 g/10 mm Typically, the preferred SLEP's used in the practice of this invention are homogeneously branched and do not have any measurable high density fraction, i.e., short chain branching distribution as measured by Temperature Rising Elution Fractionation described in US-A- 5,089,321 Stated in another manner, these polymers do not contain any polymer fraction that has a degree of branching less than or equal to 2 methyl groups/1000 carbons These preferred SLEP's also have a single differential scanning caloπmetry (DSC) melting peak between -30C and 150C using a second heat at a scanning rate of 10C/mιnute Ethylene/α-olefin/diene terpolymers may also be used in the practice of this invention Suitable α-olefins include the α-olefins described above as suitable for making ethylene/α-olefin copolymers The dienes suitable as monomers for preparation of such terpolymers are either conjugated or nonconjugated, typically nonconjugated dienes having from 6 to 15 carbon atoms Representative examples of suitable nonconjugated dienes that may be used to prepare the terpolymer include a) Straight chain acyclic dienes such as 1 ,4-hexadιene, 1 ,5- heptadiene, piperylene and 1 ,6-octadιene, b) branched chain acyclic dienes such as 5-methyl-1 4-hexadιene, 3 7-dιmethyl-1 ,6-octadιene, and 3,7-dιmethyl-1 ,7-octadιene, c) single ring alicychc dienes such as 4-vιnylcyciohexene, 1-allyl-4- isopropy dene cyclohexane, 3-allylcyclopentene, 4-allylcyclohexene, and 1- ιsopropenyl-4-butenylcyclohexane, d) multi-ring alicychc fused and bridged ring dienes such as dicyclopentadiene, alkenyl, alky dene, cycloalkenyl and cycloalkyhdene norbornenes such as 5-methylene-2-norbornene, 5-methylene-6-methyl-2- norbornene, 5-methylene-6,6-dιmethyl-2-norbornene, 5-propenyl-2- norbornene, 5-(3-cyclopentenyl)-2-norbornene, 5-ethyhdene-2-norbomene, and 5-cyclohexylιdene-2-norbornene, and the like The preferred dienes are selected from the group consisting of 1 ,4- hexadiene, dicyclopentadiene, 5-ethyhdene-2-norbomene, 5-methylene-2- norbornene, 7-methyl-1 ,6-octadιene, piperylene, 4-vιnylcyclohexene, etc The preferred terpolymers for the practice of the invention are terpolymers of ethylene, propylene and a nonconjugated diene (EPDM) Such terpolymers are or will be commercially available from such companies as DuPont Dow Elastomers L L C The total diene monomer content in the terpolymer may suitably range from about 0 1 to about 15 weight percent, preferably 0 5 to about 12 weight percent, and most preferably about 1 0 to about 6 0 weight Both the ethylene copolymers and the ethylene terpolymers comprise from about 20 to about 90 wt %, preferably from about 30 to about 85 wt %, ethylene with the other comonomers comprising the balance The ethylene copolymers and terpolymers preferably have a weight average molecular weight (M w ) of at least about 10,000, and more preferably at least about 15,000, and may have a M w of up to about 1 ,000,000 or higher, preferably up to about 500,000 The elastomeric polymer is preferably substantially amorphous The expression "substantially amorphous" means that the polymer has a degree of crystalhnity less than about 25% The elastomeric polymer more preferably has a crystalhnity less than about 15% The elastomeric polymer may be the product of a single polymerization reaction or may be a polymer blend resulting from physical blending of polymers obtained from different polymerization reactions and/or resulting from using a mixed polymerization catalyst "Functionalized elastomeric polymer" means an elastomeric polymer or elastomeric polymer blend that comprises at least one reactive substituent that will react with the reactive substituents of the crosslinking agent to at least partially vulcanize the elastomer Preferred reactive elastomer substituents are selected from the group consisting of carboxyiic acid, carboxyiic anhydride, carboxyiic acid salt, carbonyl halide, hydroxy, epoxy, and isocyanate A preferred functionality-imparting compound for the elastomeric substituent has ethylenic unsaturation to permit integration of that compound with the functionality intact into the elastomeric polymer either as a graft or as a comonomer The preferred compound may be represented by the formula in which R 1 represents an ethylenically unsaturated predominantly hydrocarbyl (or hydrocarbylene) group (referred to hereafter as "hydrocarbyl(ene)"), each X may be the same or different and represents a reactive moiety selected from carboxyiic acid carboxyiic anhydride, carboxyiic salt, carbonyl halide, hydroxy, epoxy and isocyanate, R 2 represents a predominantly hydrocarbyl group, m represents an integer which is greater than or equal to 1 , and n represents an integer greater than or equal to 0 Preferably m is in the range from 1 to 4, more preferably 1 or 2, and n is preferably 0. When grafted onto the elastomeric polymer, this compound preferably has just one ethylenic unsaturation per molecule. Preferred unsaturated, predominantly hydrocarbyl compounds may be represented either by the formula R 3 - (R X) y - CH = CH - (R 4 X) z -R 3 (II) in which R 3 represents H or a predominantly hydrocarbyl group, R 4 represents a predominantly hydrocarbylene group, X is as defined above, y is an integer from 0 to 4, z is an integer from 0 to 4, and y + z > 0, preferably < 2, or by the formula R J R < O C : (III) = O o in which R 5 and R 6 are independently hydrogen or a C r C 20 alkyl, and one can join with the other to form an alicyclic structure. The predominantly hydrocarbyl(ene) group is a hydrocarbyl or hydrocarbylene group preferably having from 2 to about 30 carbon atoms and more preferably having from 2 to about 12 carbon atoms, and having not more than 50 mol%, preferably not more than 20 mol%, more preferably not more than 1 mol%, hetero-atoms (excluding the hetero atoms which comprise the reactive groups). The predominantly hydrocarbyl(ene) group may be straight or branched aliphatic, optionally having one or more hetero atoms in the carbon chain and preferably alkyl or alkylene, which preferably has from 2 to 30, more preferably from 2 to 12, carbon atoms, aromatic, optionally having one or more hetero- atoms as ring members and preferably having 6 ring members, more preferably phenyl or phenylene; cycloa phatic optionally having one or more hetero-atoms as ring members and preferably having 5 to 10 ring members, fused polycyclic ring systems containing one or more of the aforementioned aromatic and/or aliphatic rings and compounds which combine two or more of the aforementioned aliphatic, aromatic, cycloahphatic and fused polycyclic ring moieties Examples of preferred ethylenically unsaturated predominantly hydrocarbyl(ene) compounds include vinyl and vinylene, particularly cis- vmylene, and predominantly hydrocarbyl compounds having these groups such as α-olefins, norbornene, allyl, styrene, dienes, etc Suitable α-olefins include the α-olefins described above as suitable for making ethylene/α-olefin copolymers Suitable dienes include those described above as suitable monomers for the preparation of terpolymers Unsaturated predominantly hydrocarbyl(ene) compounds having at least one reactive group include unsaturated compounds having at least one carboxyiic functionality, including carboxyiic acids, carboxyiic anhydrides, and salts of carboxyiic acids The cations of the carboxyiic acid salts may be any metal or nonmetal cation, but preferably is a metal ion of Group IA or IIA of the Periodic Table of the Elements as printed in the 71st Edition of the CRC Handbook of Chemistry and Physics at page 1-10 (1990-1991 ), e g sodium, potassium, calcium, etc Preferably, these unsaturated predominantly hydrocarbyl compounds have one or two carboxyiic functionalities Representative examples of unsaturated predominantly hydrocarbyl compounds having carboxyiic functionality include acrylic, methacryhc, itaconic, crotonic, α-methyl crotonic, citraconic, succinic, phthahc, tetrahydrophthalic, and cinnamic acids, and their anhydride, ester and salt derivatives, if any These compounds are commercially available or can be derived from commercially available compounds via procedures well known in the art The acid anhydride group-containing unsaturated compounds are preferred Representative examples of the acid anhydride group-containing unsaturated compounds include maieic anhydride, itaconic anhydride, chloromaleic anhydride, citraconic anhydride, butenyl-succmic anhydride, tetrahydrophthalic anhydride, etc Maieic anhydride is particularly preferred Unsaturated compounds having at least one reactive group also include unsaturated compounds having at least one carbonyl halide functionality, which are sometimes also referred to as Fπedel-Crafts acylating agents, in which the halide may be fluoride chloride, bromide or iodide, preferably chloride Included among these compounds are predominantly hydrocarbyl carbonyl hahdes having at least one vinyl unsaturation and having one or more carbonyl halide substituents These compounds are either commercially available or can be derived from the corresponding predominantly hydrocarbyl carboxyiic acids described above by procedures well known in the art Representative examples of the carbonyl halide containing unsaturated compounds include the acryloyl, methacryloyl, maleoyl, itaconoyl, citraconoyl, tetrahydrophthaloyl, and cinnamoyl halides Acryloyl chloride, methacryloyl chloride, and maleoyl chloride are preferred The hydroxy group containing unsaturated compound is a compound having an hydroxy group and an unsaturation which is copolymeπzable with an ethylenically unsaturated compound Illustrative hydroxy group containing compounds are 3-hydroxy-1 -propene, 4-hydroxy-1-butene, 6-hydroxy-1- hexene and 8-hydroxy-1-octene The epoxy group-containing unsaturated compound is a compound having an epoxy group and an unsaturation which is copolymeπzable with an olefin or ethylenically unsaturated compound The epoxy group-containing unsaturated compounds include, for example, unsaturated glycidyl esters, unsaturated glycidyl ethers, epoxyalkylenes, p-glycidyl-styrenes and the like These may be represented by the following formulae (IV), (V), and (VI) O II R? C — O- CH, CH CHR 2 (IV) O wherein R is a C 2 . 18 hydrocarbon group having an ethylenic unsaturation, R 7 CH . CH CHR : (V) o wherein R 7 is as defined above and X is and R 8 R 7 C CHR 2 \ / (V.) o wherein R 7 and R 2 are as defined above and R 8 is a hydrogen atom or a methyl group. Specific examples of the epoxy group-containing unsaturated compound include glycidyl acrylate, glycidyl methacrylate, glycidyl itaconate, glycidyl butenate, allyl glycidyl ether, 2-methylallyl glycidyl ether, styrene-p- glycidyl ether, 3,4-epoxybutene, 3,4-epoxy-3-methyl-1 -butene, 3,4-epoxy-1- pentene, 3,4-epoxy-3-methylpentene, 5,6-epoxy-1 -hexene, vinylcyclohexene monoxide, p-glycidylstyrene, etc. Unsaturated predominantly hydrocarbyl(ene) compounds having at least one reactive group further include unsaturated compounds having at least one isocyanate group. Preferred among these compounds are those in which the unsaturated predominantly hydrocarbyl(ene) moiety is an unsaturated aliphatic group, more preferably an α-unsaturated alkyl group having from 2 to 22 carbon atoms. Representative examples of such compounds include vinyl isocyanate; α-olefin isocyanates having from 3 to 8 carbon atoms in the α-olefin, such as 3-isocyanato-1-propene, 4-isocyanato- 1-butene, 6-isocyanato-1-hexene, and 8-isocyanato-1-octene; isocyanato ethyl acrylate and isocyanato methacrylate. The unsaturated compounds having at least one reactive group can include compounds having combinations of different reactive groups as long as they do not react with each other under polymer melt processing conditions such that they are not available to react with reactive substituents of the crosslinking compound Suitable combinations include any combination of two or more carbonyl functionalities, such as the combination of carboxyiic acid and carboxyiic anhydride or the combination of carboxyiic acid and hydroxy The above-described unsaturated compounds having reactive groups may be used alone, or two or more can be used in combination with one another The amount of the unsaturated compound having reactive substituents used to functiona ze the elastomeric polymer is preferably sufficient to provide at least two functional groups per elastomeric polymer chain or sufficient functionality to permit the functionalized elastomeric polymer to crosslink beyond the gel point given sufficient crosslinking agent and more preferably sufficient to achieve commercially acceptable compression set and other rubber properties This amount is generally at least 0 01 wt%, preferably at least 0 1 wt%, and more preferably at least 1 wt%, unsaturated compound up to an amount varied by convenience, preferably up to 20 wt%, more preferably up to 10 wt%, unsaturated compound based on the total weight of the elastomeric polymer These unsaturated compounds are incorporated into the elastomeric polymer either by adding these compounds as a comonomer during preparation of the elastomeric polymer as described, for example, in US-A-4,839,425, or by post-polymerization grafting onto the elastomeric polymer Post-polymerization grafting is preferred The unsaturated organic compound can be grafted to the elastomeric polymer by any known technique, such as one of those taught in US-A- 3,236,917 and US -A-5, 194, 509 For example, in the '917 patent the polymer is introduced into a two-roll mixer and mixed at a temperature of 60 C The unsaturated organic compound is then added along with a free radical initiator, such as, for example, benzoyl peroxide, and the components are mixed at 30 C until the grafting is completed In the '509 patent, the procedure is similar except that the reaction temperature is higher, e g , 210 to 300 C, and a free radical initiator is not used at a reduced concentration An alternative and preferred method of grafting is taught in US-A- 4,950,541 by using a twin-screw devolatilizing extruder as the mixing apparatus For example, an elastomeric polymer and unsaturated functionality-imparting organic compound are mixed and reacted within the extruder at temperatures at which the reactants are molten and in the presence of a free radical initiator Preferably, the unsaturated functionality- imparting organic compound is injected into a zone maintained under pressure within the extruder Methods for preparing functionalized elastomeric polymer by grafting the functionality onto ethyiene/propylene copolymer elastomer are also disclosed in US-A-4, 134,927 Preferably, the functionalized elastomeric polymer is soft and elastomeric in nature (e g , having a low tensile yield, preferably below 400 psi) The functionalized elastomeric polymer need not be a single rubber but may also be a blend of one or more functionalized elastomeric polymers It may also include nonelastomeπc polymers, either as impurities or as reinforcers at up to 100 parts per 100 parts functionalized elastomeric polymer. The crosslinking agent contains at least two (2) reactive substituents selected such that these cross-linking substituents will react with those of the elastomeric substituent to at least partially vulcanize the elastomer When the reactive substituent of the elastomeric polymer is an epoxy, then the crosslinking agents are selected from the group consisting of carboxyiic acid, carboxyiic anhydride, carboxyiic acid salt, carbonyl halide, hydroxy and isocyanate When the reactive substituent of the elastomeric polymer is carboxyiic anhydride, then the crosslinking agents are selected from the group consisting of hydroxy, epoxy and isocyanate Especially preferred crosslinking agents may be defined by the formula R 2 P X q (VII) wherein R 2 represents a predominantly hydrocarbyl group as defined above, X represents the reactive functionality as defined above, p is an integer >0, preferably >1 , more preferably 1 , and q is an integer > 2, more preferably 2 to 4 and even more preferably 2 These may be represented by the formula X-(R 2 ) P -X (VIII) in which R 2 is as defined above and is preferably an aliphatic group, more preferably an alkylene group, having from 1 to 12 carbon atoms; an aromatic group, preferably phenyl, or an aliphatic aromatic group such as toluene or methylene diphenyl X is as defined above. Representative examples of crosslinking agents having at least one reactive group include dicarboxylic functionalities such as oxalic, malonic, succinic, adipic, suberic, phthalic, isophthalic, terephthalic, hexahydrophthalic, toluic, pyromellitic, etc , acids, esters, salts and anhydrides, if possible, such as phthalic anhydride, pyromellitic anhydride, hexahydrophthalic anhydride, and succinic anhydride; acyl halides of the aforementioned dicarboxylic functionalities; aliphatic diisocyanates such as methyl diisocyanate, ethyl dnsocyanate, propyl diisocyanate, and the like; aromatic diisocyanates such as phenyl diisocyanate, tolyl diisocyanate, etc.; diol and polyol compounds, such as glycerine, pentaerithπtol, polyethylene glycol with two terminal alcohol's, ethylene glycol, propanediol, butanediol, glucose, sucrose, 1 ,4- benzenedimethanol, etc.; epoxy compounds such as epoxidized soybean oil, ether compounds such as bisphenol A diglycidyl ether, glycidyl ether of aliphatic polyol, si co-glycidyl resin, 1 ,4-butanediol diglycidyl ether, ethylene glycol diglycidyl ether, glycidyl ethers of polynuclear phenols, and glycidyl ether of tris-p-hydroxyphenyl methane, etc.; and isocynate compounds such as methyl diisocyanate, tolyl diisocyanate, hexyl diisocyanate and the like. The crosslinking agents may be nonpolymeπc or polymeric They preferably have a number average molecular weight less than 2000, more preferably less than 1500, and even more preferably less than 800 In general, the concentration and reaction conditions will depend on the reactivity of the selected functionalized elastomeric polymer/crosshnking agent pair Preferably there is an approximate stoichiometπc equivalence between the concentration of the crosslinking agent reactive sites and the functionalized elastomeric polymer reactive sites A small excess of the less reactive component is acceptable, but too large an excess of the crosslinking agent may lead to ineffective network formation during crosslinking Optionally, a catalyst may be incorporated to accelerate the crosslinking reaction Suitable catalysts will be obvious to those skilled in the art For the preferred composition of maieic anhydride grafted rubber crosshnked with a glycidyl ether (epoxy), a suitable catalyst is an amine such as 2-methyl imidazole The thermoplastic polymer used in the melt processible thermoplastic compositions and the processes for making and using those compositions according to this invention is any polymer which may be remelted after it has previously been melt processed and extruded into a shaped article It may be substantially crystalline, for example, polypropylene or HDPE, or substantially noncrystalline, such as the elastomeric polymers described above The thermoplastic polymer is preferably substantially crystalline The expression "substantially crystalline" means that the polymer has at least 25% crystalhnity More preferably, the thermoplastic polymer has at least 50% crystalhnity and even more preferably the thermoplastic polymer has at least 75% crystalhnity If a high degree of flexibility is desired in the final product made with the thermoplastic vulcanizites of this invention, the thermoplastic polymer preferably has less than 20% crystalhnity The thermoplastic polymer is preferably a polyolefin, but other polymers such as polyesters, polycarbonates, polyphenylene sulfide, polyphenylene oxide, polyvinyl chloride, etc , may also be used, provided that the thermoplastic polymer does not crosslink with the crosslinking agent and/or the functionalized elastomeric polymer to the extent that its (i e the thermoplastic polymer's) processability and/or its thermoplastic nature during melt processing (as defined above) is substantially diminished or in other words, the thermoplastic polymer is not crosshnked to the point at which it loses its ability to be compression molded into a smooth sheet or made into a continuous sheet on a roll mill by the action of the crosslinking agent used for the crosslinking of the functionalized elastomeric polymer The thermoplastic polymer may be the product of a single polymerization process or may be a polymer blend such as that resulting from dry blending or melt blending (i e , a physical blending process) and/or resulting from using a mixed catalyst in a single reactor to make two or more different polymers simultaneously Functional groups may be present which may be introduced into the thermoplastic polymer via comonomers during polymerization of that polymer or via post-polymerization grafting reactions such as those described above for making the functionalized elastomeric polymers, with the caveat that if the functionalized elastomeric polymer and crosslinking agent are introduced into the thermoplastic polymer before carrying out vulcanization of the functionalized elastomeric polymer, the functional groups are not present in the thermoplastic polymer to the extent that the thermoplastic polymer becomes substantially crosshnked as defined above Examples of such polymers include high density polyethylene (HDPE), low density polyethylene (LDPE), linear low density polyethylene (LLDPE), ultra low density polyethylene (ULDPE), polypropylene, ethylene-propylene copolymer, ethylene-styrene copolymer, polyisobutylene, ethylene-propyiene- diene monomer (EPDM) (for those applications in which rigidity may be an important property of the article made from the composition of this invention, then typically the propylene content is greater than 50 wt %), polystyrene, acrylonitπle-butadiene-styrene (ABS) copolymer, ethylene/vinyl acetate (EVA), polymers of ethylene and carbon monoxide (ECO, including those described in U S Pat No 4,916,208), or ethylene, propylene and carbon monoxide (EPCO) polymers, and the like The thermoplastic polyethylenes (PE) include ethylene homopolymers and interpolymers, such as substantially linear ethylene/alpha-olefm interpolymers made using constrained geometry catalyst technology, linear low density copolymers (LLDPE), high pressure low density PE (LDPE), high density polyethylene (HDPE), and other ethylene polymers known to the art Ethylene copolymers with polar monomers such as vinyl acetate, and so forth are also included with the caveat set forth above Thermoplastic higher polyolefms and their copolymers are also suitable For example, polypropylene (PP), poly-4-methyl-1-pentene polybutene, and copolymers such as ethylene-propylene rubber or ethylene- propylene-diene rubber are suitable Diene rubbers may be used as the thermoplastic polymer with the caveat set forth above Nonpolyolefm thermoplastic polymers may be used, such as polycarbonate, polystyrene, syndiotactic polystyrene, polyamide, polyester polyvinyl chloride (PVC), polyurethane, etc to the extent that it is not substantially crosshnked during melt processing as defined above The thermoplastic polymer need not be a single polymer, but may also be a blend of one or more thermoplastic polymers If the thermoplastic polymer is to be present during vulcanization of the functionalized elastomeric polymer, the thermoplastic polymer is preferably substantially unreactive with the selected crosslinking agent so that the thermoplastic polymer remains thermoplastic during vulcanization of the rubber If a multistep process is used whereby the rubber is vulcanized and ground to fine particles prior to dispersion in the thermoplastic polymer, then the thermoplastic polymer may include reactive substituents (and in fact could even be the same polymer as the functionalized elastomeric polymer) The preferred thermoplastic polymer will depend on the intended use For maximum softness, a low modulus (i e , high comonomer content) polymer is preferred, such as ethylene 1-octene, ethylene 1-hexene, ethylene 1 -butene or ethylene propylene copolymer, with ethylene 1-octene produced by the solution process using a constrained geometry metallocene catalyst being most preferred For high temperature property retention, propylene- based polymers, such as crystalline polypropylene or high propylene content ethylene propylene copolymers are preferred For the * most oil extended applications, a crystalline thermoplastic matrix such as HDPE or crystalline PP is preferred for obtaining the desired physical properties The molecular weight of the thermoplastic polymer may vary with the application Low molecular weight thermoplastic polymers can be easier to process and produce smooth surface finishes High molecular weight thermoplastic polymers may be used to produce stronger compositions The number average (M n ) molecular weight is from about 7,000 to about 1 ,000,000 or more, preferably from about 10,000 to about 500,000 Many different adjuvants or additives are known to modify elastomer costs and/or properties, and these may optionally be used in the present invention Non miting examples include fillers such as various carbon blacks, clays, silica, alumina, calcium carbonate, extender oils, e g aromatic oils paraffinic oils or naphthenic oils including aliphatic or napthenic or polyester oils, pigments such as titanium dioxide, processing aids such as lubricants and waxes (e g , steπc acid), phenolic, thioester and phosphite antioxidants such as Irganox 1010™ (commercially available from Ciba-Geigy) or Weston 619™ (commercially available from General Electric), acid neutralizers such as MgO, calcium stearate, dihydrotalcite, tin mercaptans, and tetrasodium pyrophosphate, and plasticizers such as dialkylphthalates tπalkylmellitates and dialkyladipates Adjuvants may be added before or after vulcanization Depending on the nature of the adjuvant and its interaction with the selected crosslinking chemistry, preferably the adjuvant may be added after dynamic vulcanization Preferably, the processing oils and/or plasticizers and inorganic fillers are added to improve the compositions's processing characteristics and the particular amounts used depend, at least in part, upon the quantities of other ingredients in the composition and the desired properties of the composition Generally, amounts from about 5 to 50 parts by weight based, on the total weight of the polymer (s), of fillers can be used and 10 to 100 parts by weight, based on total weight of the polymer(s), of compounding ingredients such as processing oils and plasticizers can be used One vulcanization process used in the practice of this invention is static vulcanization, e g (i) low-temperature mixing of the vulcanizing agent and the functionalized elastomeric polymer, (u) molding or shaping the resulting mixture, and (in) heating the molded or shaped mixture to cause at least a partial vulcanization of the mixture "Low-temperature mixing" means that the vulcanizing agent and the functionalized elastomeric polymer are blended with one another at a combination of temperature and time at which little, if any, vulcanization occurs Molding or shaping are done at a combination of temperature and time at which little, if any, vulcanization occurs The molded or shaped mixture is usually heated only to that temperature necessary to effect vulcanization (thus avoiding any unnecessary degradation of either the vulcanizing agent or the functionalized polymer (or any adjuvant that might also be present)) The vulcanization process can be done on a solvent , i e , mix or dissolve the functionalized elastomer with the crosslinking agent and then evaporate the solvent and cure the mixture at a high temperature There are many conceivable methods for producing a thermoplastic vulcanizate within the scope of this invention The dynamic vulcanization process may include any of the methods taught in the literature, except that instead of the conventional vulcanization processes of sulfur cure, peroxide crosslinking or phenolic resin curing, vulcanization takes place through the action of the vulcanizing agent on the reactive substituent of the functionalized elastomeric polymer as defined herein Suitable methods are described in US-A-4, 130,535 Nonlimiting examples include 1 Dynamic vulcanization of a blend of thermoplastic polymer and functionalized elastomer polymer 2 Vulcanization of functionalized elastomeric polymer, followed by grinding and blending with thermoplastic polymer 3 In-reactor blends of the two polymers in a polymerization process with vulcanization of the functionalized elastomeric polymer occurring in solution, preferably with dynamic mixing of the solution followed by devolatilization 4 Crosslinking of functionalized elastomeric polymer in dynamically mixed solution (e g , a low molecular weight solvent) followed by devolatilization and blending these crosshnked particles with thermoplastic polymer 5 In-reactor blends of two polymers in a polymerization process, followed by devolatilization and subsequent dynamic vulcanization in the melt phase 6 Functionahzing an elastomer with reactive substituents followed by addition of a thermoplastic polymer and dynamic vulcanization in a one- step process using, for example, a multi-zone twin-screw extruder Dynamic vulcanization may be carried out in a batch mixer such as a Brabender or Banbury mixer, in a Farrel continuous mixer, or in an extruder, with a twin screw extruder having intensive mixing screw elements being preferred Crosslinking is conducted during mixing and shearing so as to dynamically crosslink the functionalized elastomeric polymer Mixing and shearing are carried out for a time sufficient to allow for dynamically crosslinking the functionalized elastomeric polymer and for comminuting the crosshnked elastomer resulting in the elastomer being dispersed throughout the crystalline polyolefin resin Adequacy of mixing can be determined by observing the processability of the compositions by means of a piston rheometer For dynamic vulcanization, the weight ratio of thermoplastic polymer phase to the elastomeric polymer phase in the starting reaction mixture and also in the resulting thermoplastic vulcanizate is preferably in the range from 95 5 to 5 95, more preferably in the range of 60 40 to 5 95, and even more preferably in the range from 60 40 to 25 75 Temperature requirements for the blending or dynamic vulcanization process will vary with the melting points of the thermoplastic polymer, the functionalized elastomeric polymer and other ingredients Preferably the temperature is minimized to minimize degradation during processing and to maximize mechanical work If necessary for processability, the temperature may be increased For most functionalized elastomeric polymers and thermoplastic polymers, 80-350 C is an appropriate processing temperature range, with 150-275 C being preferred Due to the facile reactivity of the hydroxy, epoxy and isocyanate with carboxyiic anhydride, particularly with catalyst, crosslinking can occur readily even at moderate temperatures such as <200 C Optimization of the dispersion versus cure time may be required to obtain uniformly crosshnked rubber particles within a reasonable reaction time, though this optimization is not required in order to obtain substantial improvements in properties Dynamic vulcanization may be carried out in one or more steps, with extender oil, fillers, etc , added at one or more steps Thus, for example, oil and polymer may be blended together and then crosslinking agent added, or a thermoplastic vulcanizate (TPV) made as previously described may be dynamically vulcanized with additional rubber A "one-step process may also be used to make a thermoplastic vulcanizate in which the elastomeric polymer is functionalized with reactive substituents, followed by addition of the thermoplastic polymer and dynamic vulcanization, all done in one step without isolation of the functionalized elastomeric polymer This may, for example, be conducted in a multi-zone twin-screw extruder Other suitable methods for preparing dispersions of vulcanized elastomer particles in a thermoplastic polymer in accordance with this invention will be apparent to those skilled in the art given the description herein The thermoplastic vulcanizates of this invention, can be processed using conventional plastic processing equipment Articles molded from the thermoplastic compositions of the present invention exhibit properties generally only associated with vulcanized rubber For example, the thermoplastic compositions of the present invention usually have tensile strength values of about 9 to 25 MPa and elongation at break values of about 150 to 700% Crosslinking agent and/or catalyst may be introduced via a concentrate (such as in the elastomer or thermoplastic polymer) or as neat materials or as solutions in appropriate solvents Liquids may be imbibed directly by the functionalized elastomeric polymer or thermoplastic polymer and introduced into a mixer or extruder directly in that fashion The crosshnked elastomer can be used in many applications such as wire and cable coatings, roofing membranes, floor coverings, gaskets, hoses, boots, automotive parts, weatherstπpping, and other parts known to require elastomeric materials Various uses specifically for the thermoplastic elastomer compositions include wire insulation and coverings, seals and gaskets, hoses, roofing membranes, floor coverings, boots, automotive parts and trim, sheet liners, and packaging films The melt processable thermoplastic compositions within the scope of this invention can, for instance, be fabricated into tubing for laboratory, medical, and industrial uses Such tubing can also be used as the inner tube of reinforced hoses, wherein the extruded tube is overlaid with wire or textile cords applied as a spiral, knit or braid, optionally having a polymeric layer over the reinforced tubing The thermoplastic elastomer compositions can also be used as the protective covering of reinforced tubes of similar or different composition The following examples are illustrative of the present invention The present invention should not be considered in any way limited by these examples Unless otherwise specified, all parts percentages, and ratios are by weight EXAMPLES Materials: GFR1 - a maieic anhydride (MAH) functionalized ethylene 1-octene copolymer rubber, the ethylene/1-octene copolymer used to make the graft rubber being a copolymer produced in a solution polymerization process from a constrained geometry single site catalyst The final graft copolymer rubber had a melt index of approximately 0 5 g/10 mm , density of 0 87 g/cc, and MAH content of 1 wt % GFR2 -- the same ethylene 1-octene copolymer rubber as used to make GFR1 functionalized with MAH such that the MAH content is 1 9 wt % (density of 0 87 g/cc) HD1 -- a high density crystalline thermoplastic polyethylene resin, (commercially available from The Dow Chemical Co ) HDPE 10062, 10 Ml, 0 962 g/cc density PP1 - Himont Profax rM 6723, a crystalline thermoplastic polypropylene resin EO -- Ethylene/1-octene copolymer (EO) is made from single-site catalyst, and has a density of 0.8687 g/cc and melt index (Ml) of 0 94 g/10 mm EP - Ethylene/ propylene copolymer (EP) is Vistalon™ 707 (commercially available from Exxon) that has a density of 0 872 g/cc and Ml of 0 48 g/10 mm EPDM -- Ethyleπe/propylene 1 ,4-hexadιene terpolymer (EPDM) is Nordel™ 2722 (commercially available from Dupont Dow Elastomers LLC) that has a density of 0 878 g/cc and Ml of 0 1g/10 mm XLA1 - a difunctional crosslinking agent, DER 383 (commercially available from The Dow Chemical Co ), which is a glycidyl ether of bisphenol A having an epoxide equivalent weight of 176 - 183 XLA2 - a tπfunctional crosslinking agent, TACTIX™ 743 (commercially available from The Dow Chemical Co.), which is a glycidyl ether of tns-p- hydroxyphenyl methane having an epoxide equivalent weight of 165 XLA3 - Glycerine XLA4 -- PEG400, a polyethylene oxide commercially available from The Dow Chemical Co. having -OH end groups and a number average molecular weight of 400 CXLA1 - tπethylene tetraamine (TETA) commercially available from Aldπch Chemical Co CXLA2 -- N, N'-dιmethyl-1 ,6-hexanedtamιne (DMHDA), 98% purity, from Aldπch Chemical Co CAT1 - 2-methylιmιdazole SUNPAR 2280 - aliphatic extender oil (commercially available from Sun Oil Co ) IRGANOX™ B225 ~ an antioxidant mixture of phenolic and phosphite antioxidants (commercially available from Ciba-Geigy) Irganox™ B900 (B900) is an antioxidant mixture of phenolic and phosphite antioxidant commercially available from Ciba-Geigy 2-Methylιmιdazole (2-MI) is from Aldπch Chemical Co Dι-Cup , R dicumyl peroxide from Hercules is used for peroxide cured samples Procedure 1. Thermoset Elastomers For Examples 1 to 4 below, mixing and blending are conducted in a Rheomix™ 600 mixer operating at 60 revolutions per minute (rpm) The product made according to Examples 1 to 4 is compression molded to a plaque (1/16" X 4" X 4 ') at 130 C for 4 mm and cured at 190 C for 23 minutes The curing rate of the sample is measured by oscillating disk rheometry Test Methods: Vulcanization characteristics of the new elastomer are determined using the Monsanto ODR according to ASTM D 2084 Tensile properties are tested on an Instron Series IX Automated Testing System 1 04 Machine parameters of test are' Sample rate 18.21 pts/sec, Crosshead speed 1 5.08 cm/mm. (2.00 m./min ), Full Scale Load Range' 4 536 kg (10.00 lbs.), Humidity: 50%; Temperature. 23 C (73°F). Example 1 GFR1 (46 6 g) and B900 antioxidant (0 144 g) are melt mixed at 1 10 C for 5 minutes. Following melting of the polymer, epoxy compound (1.5 g, XLA1 ) is added slowly in about 3 minutes. The mixture is mixed for an additional 4 minutes Example 2 GFR1 (39.6 g) and oil (7.2 g, SUNPAR 2280) are melt mixed for 5 mm as described in Example 1 Epoxy compound (1.3 g, XLA1 ) is added slowly in 3 mm., followed by catalyst (0.005 g, 2 Ml) The mixture is mixed for an additional 4 minutes. Example 3 GFR1 (46.6 g) is melt mixed 5 minutes as described in Example 1 Epoxy compound (1.5 g XLA1 ) is added slowly in 3 mm, followed by catalyst (0.005 g 2-MI) Example 4 GFR2 (46 6g) is melt mixed with B900 antioxidant (0 144 g) at 130 C for 5 minutes After the polymer is melted, the temperature is reduced to 110 C Epoxy compound (3 g, XLA1 ) is then added slowly over about 3 minutes The mixture is mixed for additional 4 minutes Comparative Examples 1 to 3 Comparative Examples 1 to 3 are EO, EP, and EPDM samples respectively, cured with peroxide by the following procedure Each polymer type is melt blended in a Haake Torque Rheometer equipped with a Rheomix 600 mixer The torque rheometer is operated isothermally at 120 C and at mixing speed of 20 rpm with a heated nitrogen purge in a closed mixer for 20 minutes total mixing time 4 PHR (parts by weight per hundred parts resin) Di-Cup R dicumyl peroxide is incorporated by weighing into an envelope molded from the base resin of each type This is added into the polymer melt at the beginning of each run The molten polymer is removed from the mixer and compression molded at 138 C for 1 minute into 15 2 cm x 15 2 cm x 1 27 nm (6 inch x 6 inch x 50 mil) plaques and then cooled immediately on room temperature water cooled platens These plaques are each cut into four 7 6 cm x 7 6 cm x 1 27 nm (3 Inch x 3 inch x 50 mil) plaques These smaller plaques are compression molded at 138 C for 2 minutes at 82 76 Mpa (12,000 psi) into 15 2 cm x 15 2 cm x 0 51 nm (6 inch x 6 inch x 20 mil) plaques and then cooled as described above The second moidmg step is done to remove air bubbles The 15.2 cm x 15 2 cm x 0.51 nm (6 inch x 6 inch x 20 mil) plaques are each cured at 182 C for 10 minutes in the hot press. Results: The results of Examples 1 -3 and the Comparative Examples are shown in the Table below Those results show that the thermoset elastomer prepared according to this invention has excellent tensile properties For comparison purposes the tensile properties of two commercial rubbers cured with dicumyl peroxide are also measured The tensile properties of Examples 1 -3 are better than that of the commercially available samples The crosshnked elastomer of this invention has much less odor in comparison to the peroxide cured systems Catalyst can be used to accelerate the curing process Oil can be used to improve the processability, reduce cost, and increase flexibility TABLE I Tensile Properties of Epoxy Cured MAH-g-EO System Stress Elongation Toughness Mpa (psi) 1%) cm-kg/cπϊ 5 (ιn-lb/in 3 ) Example 1 11 03 (1600) 760 478 1 (6800) Example 2 7.59 (1100) 620 267.1 (3800) Example 3 9.66 (1400) 550 330.4 (4700) Compar. Ex. 1 EO 8.97 (1300) 800 393.6 (5600) Compar. Ex 2 EPDM 2.90 (420) 420 140.6 (2000) Compar. Ex. 3 EP 4 76 (690) 630 189.8 (2700) The results in Figure 1 show the Monsanto ODR curing rate of the thermosettable elastomers cured according to this invention at 175 C The results show that epoxy curing agent reacts with anhydride groups of the graft functionalized elastomeric polymer to form crosshnked elastomer as evidenced by the increase in torque vs curing time Without the epoxy-graft, the polymer shows no increase in torque after melting Procedure 2: Thermoplastic Elastomers Samples were prepared in a HaakeBuchler Rheomix mixer (either 600 or 3000E models, approx 40 and 190 g capacity, respectively) with roller style blades, attached to a HaakeBuchler Rheocord torque rheometer Samples removed from the mixer after preparation of the blends or thermoplastic vulcanizates were compression molded into approximately 60 mil thick plaques, then cut into microtensile bars for testing on an Instron tensile tester and for measuring Shore Hardness, and cut into circles for compression set testing Test Methods: Tensile properties were measured using microtensile bars according to ASTM D-1708-79 at 13 cm /mm (5 in /mm ) crosshead speed and at room temperature and at 70 C (in an environmental chamber) Compression set was measured at 70 C and 22 hours using a 1 3 cm (0 5 in ) thick multi-ply stack of test buttons according to ASTM D-395 Oil resistance was determined at 121 C (250 F) and 70 hours according to ASTM D-471 Heat aging stability was determined at 121 C (250 F) and 7 days according to ASTM D-573 Examples 5-8 and Comparative Examples 4 and 5 Polypropylene PP1 and graft-functionahzed rubber GFR1 are melt mixed together in a Rheomix 3000E mixer at 60-70 rpm and 190 C Extender oil, when present, is added after the polymers are melted Following melting of the polymer or addition of the oil, whichever is later, the polymer is mixed for an additional time period of approximately 6 minutes Then in Examples 5- 8 of the present invention epoxy crosslinking agent XLA1 or XLA2 is added followed by catalyst CAT1 and after a peak in torque is reached (approx 2 mins ), Irganox™ B225 is added In Comparative Examples 4 and 5, neither crosslinking agent nor catalyst is added Three to six minutes after vulcanizing agent is added, the mixing is completed and the thermoplastic vulcanizate (TPV) samples are removed and sheeted on a roll mill, then compression molded into 1 5 nm (60 mil) plaques 1 he composition of each plaque is summarized in Table 2 below TABLE 2 Amounts i n PHR Components Compar Ex 4 Compar Ex 5 Ex 5 Ex 6 Ex 7 Ex 8 PP1 50 50 50 50 50 50 GFR1 100 100 100 100 100 100 Sunpar 2280 0 27 27 27 0 27 Irganox B225 1 0 1 0 1 0 1 0 1 0 1 0 XLA2 0 0 2 0 0 0 0 XLA1 0 0 0 20 20 4 0 CAT1 0 0 0 05 005 005 0 05 These plaques are tested for physical properties. The results are shown in Table 3 below. TABLE 3 As compared to Comparative Example 4 (control sample), Example 7 shows that oil-free TPV's have higher modulus and tensile strength, especially at 70 C, and superior compression set at 70 or 100 C As compared to Comparative Example 5 (control sample with oil), 5 Examples 5, 6, and 8 show that both XLA1 and XLA2 effectively increases tensile strength and compression set Comparing Examples 6 and 8 shows that increasing the concentration of crosslinking agent increased the tensile properties and reduces the elongation, and improves compression set. The functionalized elastomeric polymer used in these examples contains only 1 % MAH. Thus the degree of crosslinking is limited. Higher MAH content generally produces higher crosslinking densities and further improvements in tensile properties and compression set. These results, however, are illustrative of crosslinking elastomeric polymers via grafted substituents, in accordance with this invention Examples 9-11 TPV's are produced in a Rheomix 600 mixer by mixing 26.6 g GFR1 with 13.4 g PP1 for 3 minutes at 190 C. Then either 1.3 g XLA3 or 1.4 g XLA1 are added and mixing is continued for 6-7 minutes for a total processing time of 10 minutes. In each case, a thermoplastic processible melt is obtained as the final product. Torque curves are obtained that show the rapid torque increases obtained in each example. The increase in torque at approximately 3 minutes is due to the vulcanization reaction that occurrs upon addition of the vulcanizing agent. XLA3 produces a torque increase of approximately 1 100 m-g. XLA1 produces a torque increase of approximately 700 m-g. All torque increases are at a rapid rate such that the maximum in torque was achieved within approximately 1 minute following addition of the crosslinking agent. Example 12 20 g HD1 and 20 g GFR1 are mixed according to Examples 9-11 0 49 g XLA1 and 0 0136 g CAT1 are added at approximately 5 minutes mixing time and mixing is continued for a total of 10 minutes processing time A rapid torque increase is obtained, amounting to approximately 800 m-g The resultant product is a thermoplastic melt Examples 13-15 and Comparative Examples 6 and 7 Examples 13-15 and Comparative Examples 6 and 7 are prepared using the same method as that used to prepare Examples 5-7 of the present invention, except the formulations are as shown in Table 4 below TABLE 4 Amounts in PHR Components Compar Ex 6 Compar Ex 7 Ex 13 Ex 14 Ex 15 PP1 100 100 100 100 100 GFR2 50 50 50 50 50 Sunpar 2280 28 28 28 28 29 Irganox B225 1 1 1 1 1 XLA1 0 0 6 6 0 0 XLA3 0 0 0 0 1 76 XLA4 0 0 0 7 7 0 CXLA1 5 7 0 0 0 0 CXLA2 0 5 6 0 0 0 5 As can be seen from Table 5, Examples 13-15 according to the present invention have a significantly lower yellowness index than that of Comparative Examples 6 and 7 The yellowness index determined according to ASTM Yl D 1250 is a standardized industry-accepted measure of the degree of 0 polymer yellowing (discoloration) TABLE 5 Comparison of the yellowness index data of Comparative Examples 6 and 7 with that of Examples 13-15 shows much more color in the product crosshnked with amine than with an epoxy or hydroxy

Claims: WHAT IS CLAIMED IS 1 A process for making an at least partially crosshnked elastomer, characterized in that the process comprises reacting, by contacting (1 ) an elastomeric polymer containing reactive substituents with (2) a crosslinking agent (a) containing two or more reactive substituents differing from those contained in the elastomeric polymer, and (b) having a number average molecular weight less than about 2000 each of the reactive substituents selected such that (i) those of the elastomer will react with those of the crosslinking agent to at least partially crosslink the elastomer, and (II) each of the reactive substituents is selected from the group consisting of carboxyiic acid, carboxyiic anhydride, carboxyiic acid salt, carbonyl halide, hydroxy, epoxy, and isocyanate 2 A process for making a melt processible thermoplastic composition, the process comprising the step of dynamically vulcanizing (A) a functionalized elastomeric polymer containing reactive substituents with (B) a crosslinking agent containing two or more reactive substituents, in the presence of ( C) a thermoplastic polymer, in which (1 ) the functionalized elastomeric polymer contains two or more reactive substituents differing from those contained in the crosslinking agent, and (2) the crosslinking agent has a number average molecular weight less than about 2000, each of the reactive substituents selected (i) such that those of the elastomer will react with those of the crosslinking agent to at least partially vulcanize the elastomer and (n) from the group consisting of carboxyiic acid, carboxyiic anhydride, carboxyiic acid salt, carbonyl halide, hydroxy, epoxy, and isocyanate 3 A process for making a melt processible thermoplastic composition, the process comprising the step of blending an (A) at least partially vulcanized elastomer with (B) a thermoplastic polymer in which (1 ) the at least partially vulcanized elastomer is made from an elastomer which contains two or more reactive substituents differing from those contained in a crosslinking agent used to subsequently vulcanize said composition, and (2) the crosslinking agent has a number average molecular weight less than about 2000, each of the reactive substituents selected (i) such that those of the elastomer will react with those of the crosslinking agent to at least partially vulcanize the elastomer and (n) from the group consisting of carboxyiic acid, carboxyiic anhydride, carboxyiic acid salt, carbonyl halide, hydroxy, epoxy, and isocyanate 4 The process of any one of Claims 1 to 3 in which the elastomer is selected from the group consisting of ethylene/u-olefιn interpolymers isoprene rubbers, isobutylene/isoprene rubber, polychloroprene, butadiene rubbers and block copolymer rubbers 5 The process of any one of Claims 1 to 3 in which the elastomer is an ethylene/u-olefin interpolymer with a density less than about 0 9 g/cm 3 6 The process of any one of Claims 1 to 5 in which the elastomer is selected from the group consisting of ethylene/α-olefin copolymers and ethylene/u-olefin/diene terpolymers 7 The process of any one of Claims 1 to 6 in which the elastomer contains long chain branching 8 The process of any one of Claims 1 to 7 in which the elastomer is a terpolymer of ethylene, propylene and a nonconjugated diene 9 The process of any one of Claims 1 to 3 in which the elastomer comprises a functionality derived from a compound of formula R 'x m (R 2 ) n (I) in which R 1 represents an ethylenically unsaturated predominantly hydrocarbyl or hydrocarbylene group, each X may be the same or different and represents a reactive moiety selected from carboxyiic acid carboxyiic anhydride, carboxyiic salt, carbonyl halide, hydroxy, epoxy and isocyanate R 2 represents a predominantly hydrocaroyl group, m represents an integer which is greater than or equal to 1 , and n represents an integer greater than or equal to 0 10 The process of any one of Claims 1 to 9 in which the compound of formula I is maieic anhydride 1 1 The process of any one of Claims 1 to 3 in which the crosslinking agent is of the formula in which each R^ is independently a predominantly hydrocarbyl group, each X is independently a reactive moiety selected from carboxyiic acid, carboxyiic anhydride, carboxyiic salt, carbonyl halide, hydroxy, epoxy and isocyanate, p is an integer 1 and q is an integer 2 12 The process of any one of Claims 1 to 1 1 wherein at least one of the reactive substituents is selected from the group consisting of epoxy and isocyanate 13 The process of any one of Claims 1 to 1 1 wherein the crosslinking agent contains two or more reactive substituents selected from the group consisting of epoxy and isocyanate 14 The process of Claim 13, wherein the elastomeric polymer containing reactive substituents has carboxyiic anhydride substituents 15 The process of any one of Claims 12 to 14 wherein the elastomeric polymer is an ethylene/ α-olefin copolymer 16 The process of Claim 1 1 wherein the elastomeric polymer containing reactive substituents is an ethyiene/1 -octene copolymer containing maieic anhydride substituents and each X of formula (VII) is an epoxy moiety 17 The process of any one of Claims 1 and 4 to 16 wherein the process is static vulcanization 18 The process of Claim 2 or 3 in which the thermoplastic polymer (i) is at least about 25% crystalline, (n) has a number average molecular weight between of at least about 7,000, and (in) is selected from the group consisting of polyolefin, polyester, polyphenylene sulfide, polyphenylene oxide, and polyvinyl chloride 19 The process of Claim 18 in which the thermoplastic polymer is selected from the group consisting of high density polyethylene low density polyethylene, linear low density polyethylene, ultra low density polyethylene polypropylene, ethylene-propylene copolymer, ethylene-styrene copolymer, polyisobutylene, ethylene-propylene-diene monomer terpolymer, polystyrene, acrylonitrile-butadiene-styrene terpolymer, ethylene/vinyl acetate, and polymers of ethylene and carbon monoxide 20 The process of Claim 18 in which the thermoplastic polymer is polypropylene 21 The process of Claim 2 or 3 in which the product of the process comprises a blend of (A) 60 to 25 wt % thermoplastic polymer and (B) 40 to 75 wt % at least partially vulcanized elastomer 22 An at least partially crosshnked elastomer obtainable according to one of Claims 1 and 4 to 17 23 A melt-processible thermoplastic composition obtainable according to any one of Claims 2 to 3 and 18 to 21 24 A melt processible thermoplastic composition comprising a blend of (A) 5 to 95 wt % thermoplastic polymer and (B) 95 to 5 wt % of the at least partially crosshnked elastomer of Claim 22 25 The composition of Claim 24 in which the thermoplastic polymer (i) is at least about 25% crystalline, (n) has a number average molecular weight of at least about 7,000, and (in) is selected from the group consisting of polyolefin, polyester, polyphenylene sulfide, polyphenylene oxide, and polyvinyl chloride 26 The composition of Claim 25 in which the thermoplastic polymer is selected from the group consisting of high density polyethylene, low density polyethylene, linear low density polyethylene, ultra low density polyethylene, polypropylene, ethyiene-propylene copolymer, ethylene-styrene copolymer, polyisobutylene, ethylene-propylene-diene monomer terpolymer, polystyrene, acrylonitπle-butadiene-styrene terpolymer, ethylene/vinyl acetate and polymers of ethylene and carbon monoxide 27 The composition of Claim 25 in which the thermoplastic polymer is polypropylene 28 The composition of any one of Claims 24 to 27 which comprises a blend of (A) 60 to 25 wt % thermoplastic polymer, and (B) 40 to 75 wt % of the at least partially crossllmked elastomer 29 An article comprising a crosshnked elastomer obtainable from the at least partially crosshnked elastomer of Claim 22 30 An article comprising the composition of Claim 23 or 24 31 An article made by thermoformmg a composition obtainable by the process of any one of Claims 2 to 3 and 18 to 21

Inventors: ALLEN JIMMY D, HO THOI H, HUGHES MORGAN M, JOHNSTON ROBERT T, ALLEN, JIMMY, D., HO, THOI, H., HUGHES, MORGAN, M., JOHNSTON, ROBERT, T.
Applicants: ALLEN JIMMY D, DOW CHEMICAL CO, HO THOI H, HUGHES MORGAN M, JOHNSTON ROBERT T, ALLEN, JIMMY, D., HO, THOI, H., HUGHES, MORGAN, M., JOHNSTON, ROBERT, T., THE DOW CHEMICAL COMPANY
Application year: 1997
Main classification: C08L23
IPC codes: C08C19, C08F8, C08J3, C08L23, C08L51, C08L53, C08L55, C08L71, C08L91