METHOD FOR JUDGING THE PROPERTIES OF MOLTEN CAST IRON

Abstract: The present invention relates to a method for predicting the microstructure in which a certain cast iron melt will solidify comprising the steps of: a) taking a sample of the cast iron melt having a predetermined weight W; b) adding the sample to a sample vessel containing an amount of a neutralizing agent, preferably tellurium, which is sufficient to change an amount W of molten grey cast iron to white iron; c) recording a cooling curve in the centre of the so-obtained treated iron sample; d) determining the local maximum value Te(max) of the cooling curve obtained in step c); and e) predicting whether the cast iron melt will solidify as SGI, CGI, flake patchy or grey cast iron by using the information obtained in step d).

Description: METHOD FOR JUDGING THE PROPERTIES OF MOLTEN CAST IRON The present invention relates to an improved method for predicting the micro structure with which a certain cast iron melt will solidify. The invention also relates to an apparatus for carrying out the method. Background of the invention WO86/01755 (incorporated by reference) discloses a method for producing compacted graphite cast iron by using thermal analysis. A sample is taken from a bath of molten cast iron and this sample is permitted to solidify during 0.5 to 10 minutes. The temperature is recorded simultaneously by two temperature responsive means, one of which is arranged in the centre of the sample and the other in the immediate vicinity of the vessel wall. So-called cooling curves representing temperature as a function of time are recorded for each of the two temperature responsive means. According to this document it is then possible to determine the necessary amount of structure-modifying agents that has to be added to the melt in order to obtain the desired microstructure. WO92/06809 (incorporated by reference) describes a specific method for evaluating the cooling curves obtained by the method of WO86/01755. According to this document thermal analysis is carried out in a sample vessel coated with a material consuming the active form of the structure-modifying agent. This material may comprise oxides of Si, Mn, Fe, K and Na. An early plateau in the cooling curve (which, because of the coating often is found close to the vessel wall) means that flake graphite crystals have precipitated close to the temperature- responsive means recording the curve. A skilled person can, by studying the curves and by using calibration data, determine whether any structure-modifying agent has to be added to the melt in order to obtain compacted graphite cast iron. WO92/06810 (incorporated by reference) describes a method for producing spheroidal cast iron where a thermal analysis is carried out in a sample vessel coated with the same material as in WO92/06809. Accordingly, it is known to predict in which form a certain cast iron melt will solidify by using thermal analysis and coated sample vessels. However, the prediction is difficult to carry out for low concentrations of structure-modifying agent near the border-line between grey cast iron and compacted graphite cast iron. However, it is often desirable to work with cast iron melts containing a minimal amount of structure-modifying agents. Hence, there is need for prediction methods giving accurate and easily consumable results, also in this concentration region. EP 0 327 237 discloses a method of testing the magnesium content of a melt in connection with production of spheroidal cast iron. A molten sample of magnesium-treated iron is introduced into a sample vessel containing additives of tellurium and either sulphur or selenium. The sample is then allowed to cool and the temperature is continuously monitored. A basic idea in the method of EP 0 327 237 is to remove all active magnesium from the sample before carrying out thermal analysis. Then the melt can either solidify with graphitic or carbidic arrest. The reason for adding sulphur or selenium together with tellurium is that, in the presence of magnesium, tellurium alone cannot prevent the iron from solidifying with a graphitic eutectic structure. Therefore, the addition of selenium or sulphur is just sufficient to completely neutralize a predetermined threshold percentage of magnesium. If the magnesium content is above the threshold percentage, the melt will solidify as graphitic iron. EP 0 327 237 also suggests that the method can be modified to control the magnesium content of compacted graphite cast irons. In that case the document states that two separate thermal analysis with different amounts of added sulfur are needed. GB 2,283,325 discloses a method for thermal analysis of molten cast iron. The method consist of the steps of: a) obtaining a first cooling curve of the molten cast iron using a clean cup; b) obtaining a second cooling curve of the molten cast iron using a second cup in which small amounts (e.g. 0.05 to 0.3 % by weight) of tellurium are contained; and c) comparing the first cooling curve with the second sooling curve. The two curves are only compared in respect of recalscence. A recalescence larger than zero relates to compacted graphite cast iron (CGI) or spheroidal graphite cast iron (SGI). Such a comparison is satisfying when it is desirable to check if structure-modifying agent had been added or not before pouring while producing SGI or CGI. However, the method is not sufficiently accurate in the border region between CGI and grey iron. When producing CGI and carrying out a thermal analysis according to the inaccurate method disclosed in GB 2, 283,325, there is a large risk that graphite flake patches are formed locally in the casting, due to a slightly insufficient concentration of structure-modifying agent in the molten cast iron. As the presence of flake patches in the microstructure reduces the tensile strength and elastic modulus of the iron by 20-50 %, this is a serious problem. Summary of the invention Now it has turned out that unexpectedly good predictions of the microstructure with which a certain cast iron melt will solidify can be performed by carrying out a method comprising the steps of: a) taking a sample of the cast iron melt having a predetermined weight W; b) adding the sample to a sample vessel containing an amount of a neutralizing agent, preferably tellurium, which is sufficient to change an amount W of molten grey cast iron to white iron; c) recording a cooling curve in the centre of the so obtained treated iron sample; d) detemining the- maximum eutectic temperature (T e (max))of the cooling curve obtained in step c);and e) predicting whether the cast iron melt will solidify as SGI, CGI, flake patchy or grey cast iron by using the information obtained in step d). Detailed description of the invention The present invention is based on the discovery that easily construable results are obtained when carrying out thermal analysis of a sample of molten cast iron that has been treated with an appopriate amount of at least one substance neutralizing the structure-modifying agent, which substance is chosen from the group of tellurium, sulfur, boron and selenium, preferably tellurium. Hence, the present method does not require a highly qualified staff and it is very suitable for automation by computer. The term " cooling curve" as utilized herein refers to graphs representing the temperature as a function of time during solidification of a cast iron melt. The term " sample vessel" as disclosed herein refers to a sample container which, when used for thermal analysis, is filled with a sample of molten metal. The temperature of the molten metal is then recorded in a suitable way. A sample vessel according to the present invention is basically made of an inert material but may contain or be coated by substances affecting the structure of cast iron, such as tellurium, sulfur, boron and selenium, as well as oxides of Si, Mn, Fe, K and Na. The vessel may also contain or be coated with conventional inoculating agents to promote nucleation. The term "structure-modifying agent" as disclosed herein refers to an agent affecting the microstructure of cast iron, which agent is chosen from the group of magnesium and rare earth element. Magnesium is preferred. The term "tellurium cup" as disclosed herein refers to a sample vessel coated with tellurium or containing a tellurium blob. The tellurium cup may also contain conventional inoculating agents. The term "FeSi cup" as disclosed herein refers to a sample vessel coated with FeSi, or containing a FeSi blob. The FeSi cup may also contain conventional inoculating agents. The term "clean cup" as disclosed herein refers to a sample vessel without any coating, or with an inert coating. The term "sampling device" as disclosed herein refers to a device comprising a sample vessel equipped with at least one sensor for thermal analysis, said sensor(s) being intended to be immersed in the solidifying metal sample during analysis, and a means for filling the sample vessel with molten metal. The term "neutralizing agent" as disclosed herein refers to an agent neutralizing the active form of the structure-modifying agent and is chosen from the group of tellurium, sulfur, boron and selenium. Tellurium is preferred. The term "CGI" as disclosed herein refers to compacted graphite cast iron. The teπn "SGI", or "SG", as disclosed herein refers to speroidal graphite cast iron. The terms "flake patches", and "patchy" as disclosed herein, relate to graphite flakes that can be formed locally in a CGI microstructure due to an insufficient amount of structure- modifying agent. The term "treated iron sample" as disclosed herein refers to a sample of cast iron in a sample vessel, which vessel may or may not contain an agent affecting the composition of the sample. Hence, for example a treated iron sample in a tellurium cup has a reduced content of active magnesium compared to the melt from which the sample originally was taken. The invention will now be described with references to the accompaying figures in which: Fig. 1 defines the principles for assigning variable names in the present application; Fig. 2 briefly outlines the effect of "extending" the thermal analysis scale by treating a cast iron sample with tellurium as neutralizing agent; Fig. 3 shows which cast iron type the measured cooling curve actually corresponds to when carrying out a thermal analysis on a treated iron sample in a tellurium cup; Fig. 4A discloses cooling curves corresponding to CGI, SGI, flake patchy and grey iron, which curves have been recorded in the centre of a clean cup. Fig. 4B shows cooling curves recorded in a tellurium cup under the same conditions and for the same batch of molten cast iron as in Fig. 4A . Figures 5A and 5B both disclose to flowcharts on how the curves obtained by the thermal analysis exemplified in Fig. 3 can be construed. Fig. 5A relates to a tellurium cup, and fig. 5B relates to a set of a tellurium cup, a clean cup and a FeSi cup; Fig. 6A and 6B show examples of sample vessels that can be used in the present method; Fig.7 is a schematic presentation of an apparatus for controlling production of compacted graphite cast iron according to the present invention; Fig. 8 is a micrograph showing a CGI casting that is insufficiently treated with magnesium and, accordingly contains isolated flake patches; and Fig. 9 is a diagram showing ultimate tensile stress and 0.2% yield stress of 85-100% peariitic cast irons as a function of nodularity and temperature. Above, the problem regarding flake patches and how such patches can impair the quality of a CGI casting has been briefly mentioned. From the practical point of view, engine designers will establish wall thickness based on the inherent strength and stiffness of the chosen material. If they are designing with CGI, they will calculate dimensions based on a minimum tensile strength of 400 MPa. However, if the foundry process is out-of-control and the castings contain flake patches, the material strength can be 20-50% less (See fig. 9). The as- cast dimensions (calculated based on good CGI) will not be strong enough to withstand the operating load. The walls will crack and the engine will fail in service. The net result is an extremely costly customer liability. It is thus evident that flake patches must be avoided in CGI castings. Traditionally, metallurgists have referred to three types of cast iron: grey (flake) cast iron; CGI; and ductile cast iron. However, when CGI is produced with insufficient shape modifying agent (magnesium) an intermediate flake patch structure can form. The centre of the eutectic cells contains flake graphite while the perimeter region of the eutectic cells contains compacted graphite particles. Surprisingly (See figure 8.) it has been shown that isolated flake patches predominate in determining the strength of the material. Even a small ( 10-20%) amount of flake patches will result in a loss of 20-50 % of the mechanical strength. It is therefore not sufficient to simply differentiate between CGI or grey iron: the measurement technique must have sufficient resolution to detect the onset of isolated flake patches in a predominantly compacted graphite material. Accordingly, the present invention is directed to thermal analysis for predicting the microstructure with which a certain cast iron melt will solidify. The thermal analysis is carried out by adding molten cast iron to a sample vessel containing neutalizing agent, preferably tellurium, whereafter the temperature is recorded during the solidification process. Optionally, cups with other coatings such as FeSi or fully inert cups (clean cups) can also be used together with the tellurium cup. Figs. 6A and 6B present two examples of sample vessels that can be used in the present invention. The sample vessel (7) in fig. 7A contains a blob (8) of tellurium, which dissolves in the molten cast iron (9). The temperature is monitored during solidification by a temperature responsive means (1 ) such as a thermocouple. Fig. 7B discloses a more complex vessel, which is divided into three compartments (4, 5, 6). One compartment (4) is coated with tellurium, another (5) is coated with FeSi, and the last compartment (6) does not contain any coating. Temperature-responsive means (1 , 2, 3) are arranged in all three compartments. Both cups can be normal sand cups, ceramic cups or made of coated steel or other suitable materials. The basic principle behind the present invention is illustrated in Figs. 2 and 3. In a prediction method according to the state of the art, cooling curves corresponding to cast iron types comprised in the range from SGI to A type grey iron are recorded. In the present method, the content of structure-modifying agent is decreased by adding a predetermined amount of neutralizing agent. Hence, cooling curves corresponding to cast iron types comprised in the range from CGI to white iron are recorded instead of curves representing the actual composition of the sample. Figs. 4A and 4B illustrate the increase in sensitivity that is achieved by carrying out the present invention. Fig. 4A discloses four cooling curves corresponding to CGI, SGI flake patchy and grey iron. No neutralizing agent has been added. The four curves can be distinguished from each other, but nethertheless they follow each other rather closely. Fig. 4B shows cooresponding curves after adding a predetermined amount of a neutralizing agent. In Fig. 4A. all eutectic plateaus are comprised within the temperature range of 1 140- 1 150°C. In contrast, the maximum growth temperatures during the eutectic reaction in Fig. 4B are comprised within the temperature range of 1 1 15-1 165°C. It is evident from the figure that a much higher accuracy is achieved by the present method compared to the state of the art. The above mentioned predetermined amount of neutralizing agent must be effective to change grey cast iron to white iron. Tellurium is the preferred neutralizing agent and the necessary amount of tellurium in the sample vessel is at least 0.01 %(wt), preferably 0.05- 0.2%(wt) of the weight of the cast iron sample. Based on the maximum eutectic growth temperature and recalescence. results from treated iron samples can roughly be categorized into four categories. Limits between the categories are calibrated for different foundries. The following is an example of criteria for a certain foundry. Category Cast Iron Maximum Growth Recalescence to be AnaTemperature ΔT te lyzed during the Eutectic Reaction of a Treated Sample Grey iron <1 130°C <2°C and close to grey Boarder 1 130°C- 1 150°C >2°C iron with flake patches 3. CGI >1 155°C >1°C 4. Low nodule > 1 150°C-1 155°C <5°C SGI An iron sample treated in a tellurium cup contains a lower concentration of active magnesium than corresponding untreated molten cast iron. The result of this treatment is hence that the thermal analysis is performed in a concentration region where more distinct results are obtained compared to the original concentation region. A cooling curve recorded in a tellurium cup can therefore very clearly show whether the iron contains a sufficient amount of structure-modifying agents in order to solidify as CGI. It can also indicate whether the cast iron is overtreated with structure-modifying agents or not. The present method may be further improved by adding other thermal analysis steps which are carried out in other kinds of sample vessels, such as a FeSi cup and a clean cup. Thermal analysis in a FeSi cup as well as in a clean cup gives information about both the inoculation level and the real state of cast iron. By determining the maximum and minimum eutectic temperature and maximal slope of the cooling curves the inoculation level can be calculated. If the minimum eutectic temperature of the FeSi curve is much higher than the minimum eutectic temperature of the clean curve, the inoculation level is far below saturation, and inoculants should be added. The cast iron has reached the saturation level when the two temperatures are about the same. When the cast iron is overtreated, the cooling curve from the FeSi cup has a small recalescense and a small maximal slope. The clean cup measures the real state of iron and show the modification and inoculation level. In a certain range (assessed together with the other two cups), high recalescence (low minimum eutectic temperature and high maximum eutectic temperature) and high maximal slope point to a good CGI, while lower recalescence and lower slope indicate that the cast iron is overtreated with structure-modifying agents and/or inoculants. Hence, thermal analysis in a tellurium cup indicates whether the molten cast iron will solidify as grey iron, flake patchy, CGI or SGI. Analyses with the FeSi cup and the clean cup and the comparisons among all three cooling curves allow sensitive and accurate determinations of the both the inoculation and the structure modification states. Fig. 5 A outlines an example of how to construe the cooling curves that are obtained when carrying out a thermal analysis according to the present invention by using a tellurium cup. The first step is to determine the maximum eutectic temperature, T e ,of the tellurium cup curve. If it is lower than 1 130°C the cast iron will solidify as grey iron. Magnesium must be added. If the maximum eutectic temperature is between 1 130°C and 1 150°C, the cast iron can solidify as CGI containing flake patches. A small amount of magnesium must be added. If the maximum eutectic temperature of the tellurium curve is higher than 1 155°C, the sample will solidify as CGI. Otherwise, it will solidify as SGI. Fig. 5B outlines how to construe cooling curves obtained when carrying out thermal analysis in a set of three different cups, namely the tellurium cup, the clean cup and the FeSi cup. The first step is to determine the maximum eutectic temperature, T e ,of the tellurium cup curve. If it is lower than 1 130°C the cast iron can solidify as grey iron. Magnesium must be added. If the maximum eutectic temperature is between 1 130°C and 1 150°C, the cast iron will solidify as CGI containing flake patches. More information can be obtained by measuring the slopes of recalescence of the cooling curves recorded in the clean cup and the FeSi cup, T πo (slope) and T FeSl (slope). If T no (slope) > 0.85°C/s and T FeSl (slope) > 0.45°C/s , there is a decreased risk for flake patches, and, accordingly, a lesser amount of magnesium must be added. If the maximum eutectic temperature of the tellurium curve is higher than 1 150°C, the sample will either .solidify as CGI or SGI. In order to distinguish between CGI and SG, the recalescence of the cooling curve in the tellurium cup, ΔT β is determined. If this value is less than 0.5°C the corresponding recalescence values for the clean cup and the FeSi cup are determined. If ΔT no > 6°C and ΔTp e s; > 3.5 °C, the cast iron will solidify as SG with a lower nodularity. Otherwise, the cast iron will solidify as SG iron. If ΔT e is larger than 0.5°C, the minima of the cooling curves recorded in the FeSi cup and the clean cup are determined. If the difference between the minimum value of the Fe Si curve and the clean cup curve is larger than 3°C, the cast iron melt is not sufficiently inoculated. Finally, the recalescence and the slope of recalescence of the clean cup curve are considered. If ΔT no > 10°C and T no (slope) > 1 °C/s, the cast iron will solidify as CGI. If ΔT no is within the range from 5 to 10°C and T no (slope) is within the range from 0.8 to 1 °C/s, the cast iron will solidify as CGI with high nodularity. Otherwise the cast iron will solidify as SG iron. Following abbreviations can be found in figures 5A and 5B: T no = Eutectic temperature measured in the clean cup T e = - " - tellurium cup T FeSi = - " - FeSi cup T e (max) = Maximum, tellurium cup curve T FeSi (max) = Maximum, FeSi cup curve T 110 (max) Maximum, clean cup curve T e (min) = Minimum, tellurium cup curve ΔT e = Recalescence, tellurium cup curve T e (slope) = Slope of recalescence, tellurium cup curve T πo (slope) = Slope of recalescence, clean cup curve T FeSi (slope) = Slope of recalescence, FeSi cup curve ΔT no = Recalescence, clean cup cu ΔT Fe , ΔTfeSi = Recalescence, FeSi cup T FeSi (min) = Minimum, FeSi cup curve T no (min) = Minimum, clean cup curve Cat. 1 = grey cast iron Cat. 2 = flake patchy iron Cat. 3 = CGI Cat. 4 = high nodularity CGI, SG It is preferred to carry out the method by using a computer-controlled system, especially when a large number of measurements must be carried out. In this case the same kind of sampling device 22 (or when a set of three different cups are used 22, 24, 26) that has been described above is used. Such a computer controlled system is outlined in fig. 6. During the measurement of a particular sample a temperature responsive means 8 (or, when the set of three different cups are used, the three temperature responsive means 8. 10, 12) send(s) signals to a computer means 14 in order to generate (a) cooling curve(s). The computer has access to calibration data in a ROM memory means 16 and calculates the amount of structure-modifying agents and/or inoculating agents that must be added to the melt. This amount is signalled to a means 18 for administrating structure-modifying agent and/or inoculating agent to the melt 20 to be corrected, whereby the melt is supplied with an appropriate amount of such agents. The sampling device 22 comprises a tellurium cup. Sampling device 24 comprises a FeSi cup and sampling device 26 comprises a clean cup.

Claims: Claims: 1. A method for predicting the microstructure in which a certain cast iron melt will solidify comprising the steps of: a) taking a sample of the cast iron melt having a predetermined weight W; b) adding the sample to a sample vessel containing an amount of a neutralizing agent, preferably tellurium, which is sufficient to change an amount W of molten grey cast iron to white iron; c) recording a cooling curve in the centre of the so obtained treated iron sample; d) detemining the local maximum value T e (max) of the cooling curve obtained in step c); and e) predicting whether the cast iron melt will solidify as SGI, CGI, flake patchy or grey cast iron by using the information obtained in step d). 2. A method according to claim 1 , characterized in that the neutralizing agent is tellurium. 3. A method according to claim 2, characterized in that the sample vessel contain an amount of tellurium which is at least 0.01 % of the weight of the cast iron sample. 4. A method according to claim 3, characterized in that the sample vessel contain an amount of tellurium which is 0.05-0.2% of the weight of the cast iron sample. 5. A method according to any of claims 1 -4, further comprising the steps of: f) adding a sample of the molten cast iron melt to a FeSi cup and recording a cooling curve in the centre of the sample; g) adding a sample of the molten cast iron to a clean cup and recording a cooling curve in the centre of the sample; h) detemining the following parameters of the cooling curves obtained in steps f) and g); (i) the recalescence of the cooling curve recorded in the clean cup (ΔT no ); (ii)the recalescence of the cooling curve recorded in the tellurium cup (ΔT e ) CONFIRMATION COPY (iii) the recalescence of the cooling curve recorded in the FeSi cup (ΔT FeSl ); (iv) the temperature of the local maximum of the cooling curve recorded in the FeSi cup (T FeSl (max)); (v) the temperature of the local maximum of the cooling curve recorded in the clean cup (T n0 (max)); (vi) the temperature of the local maximum of the cooling curve recorded in the tellurium (vii) the temperature of the local minimum of the cooling curve recorded in the tellurium (viii) the temperature of the local minimum of the cooling curve recorded in the clean cup (T Il0 (min)); (ix) the temperature of the local minimum of the cooling curve recorded in the FeSi cup (T FeS ,(min)); (x) the slope of recalescence of the clean cup curve (T no (slope)); (xi) the slope of recalescence of the tellurium cup curve (T θ (slope)) (xii) the slope of recalescence of the FeSi cup curve (T FeS ,(slope)) i) predicting whether the cast iron melt will solidify as SGI, CGI, flake patchy or grey cast iron and whether the cast iron melt contains a sufficient amount of nucleating agent by using the information obtained in step h). 6. A method for producing a CGI casting, comprising the steps of: a) carrying out the prediction method according to any of claims 1 -5; b) using the information obtained in step a) for calculating the amount of structure- modifying agent that has to be added to the molten cast iron in order to obtain CGI; c) adding the amount calculated in step b) to the cast iron melt; and d) carrying out the casting operation in a per se known manner. 7. An apparatus for establishing, in real time, an amount of a structure-modifying agent to be added to a cast iron melt (20) during the process of producing a compacted graphite iron casting; the apparatus comprising: a tellurium cup (22); a temperature sensor (8) for recording a cooling curve in said tellurium cup; a computer device (14) for determining an amount value (Va) of a structure- modifying agent to be added to the melt, the computer device being set up to establish a cooling curve ; the computer device being set up to establish the temperature of the local maximum of the cooling curve (T e (max)); the computer device being set up to calculate a precise amount value (Va) of a structure-modifying agent to be added to the melt in response to T e (max). 8. An apparatus for carrying out the process of claim 6, the apparatus comprising: a sampling device for taking a sample of molten cast iron from a cast iron melt (20) from which a casting comprising CGI is to be produced and delivering said sample to a tellurium cup (22); a tellurium cup (22); a temperature sensor (8) for recording a cooling curve in said tellurium cup; a computer device ( 14) for determining an amount value ( Va) of a structure- modifying agent to be added to the melt; a means for administrating a correct amount of a structure-modifying agent in response to a signal from the computer device, said signal corresponding to said amount value (Va), the computer device being set up to establish a cooling curve ; the computer device being set up to establish the temperature of the local maximum of the cooling curve (T e (max)); the computer device being set up to calculate a precise amount value (Va) of a structure-modifying agent to be added to the melt in response to T e (max); the computer being set up to send a signal corresponding to said amount value to said means, whereby a correct amount of structure-modifying agent is added to the melt (20). 9. An apparatus for establishing, in real time, an amount of a structure-modifying agent and/or inoculating agent to be added to a cast iron melt (20) during the process of producing a compacted graphite iron casting; the apparatus comprising: a tellurium cup (22); a FeSi cup (24); a clean cup (26); a first temperature sensor (8) for recording a cooling curve in said tellurium cup (22); a second temperature sensor (10) for recording a cooling curve in said FeSi cup (24); a third temperature sensor (12) for recording a cooling curve in said clean cup (26); a computer device (14) for determining an amount value (Va) of a structure- modifying agent to be added to the melt and/or determining an amount value (Vb) of an inoculating agent to be added to the melt, the computer device being set up to establish cooling curves from each of said cups (22, 24, 26); the computer device being set up to establish the following parameters from the cooling curves: (i) the recalescence of the cooling curve recorded in the clean cup (ΔT uo ); (ii) the recalescence of the cooling curve recorded in the tellurium cup (ΔT e ) (iii) the recalescence of the cooling curve recorded in the FeSi cup (ΔT FeS i); (iv) the temperature of the local maximum of the cooling curve recorded in the FeSi cup (T FeSi (max)); (v) the temperature of the local maximum of the cooling curve recorded in the clean cup (T no (max)); (vi) the temperature of the local maximum of the cooling curve recorded in the tellurium (vii) the temperature of the local minimum of the cooling curve recorded in the tellurium cup (T e (min)); (viii) the temperature of the local minimum of the cooling curve recorded in the clean cup (T no (min)); (ix) the temperature of the local minimum of the cooling curve recorded in the FeSi cup (T FθS i(min)); (x) the slope of recalescence of the clean cup curve (T no (slope)); (xi) the slope of recalescence of the tellurium cup curve (T e (slope)) (xii) the slope of recalescence of the FeSi cup curve (T FβS i(slope)) the computer device being set up to calculate a precise amount value (Va) of a structure-modifying agent and/or a precise amount value (Vb) of an inoculating agent to be added to the melt in response to ΔT no , ΔT e , ΔT FeS i„ T FeS ;(max), T 110 (max), T e (max), T e (min), T no (min), T FeSl (min), T no (slope), T e (slope), T FeS ,(slope). 1 0. An apparatus for carrying out the process of claim 6, the apparatus comprising: a sampling device for taking a sample of molten cast iron from a cast iron melt (20) from which a casting comprising CGI is to be produced and delivering said sample to a tellurium cup (22), a FeSi cup (24) and a clean cup (26); a tellurium cup (22); a FeSi cup (24); a clean cup (26); a first temperature sensor (8) for recording a cooling curve in said tellurium cup (22); a second temperature sensor (10) for recording a cooling curve in said FeSi cup (24); a third temperature sensor (12) for recording a cooling curve in said clean cup (26); a computer device (14) for determining an amount value (Va) of a structure- modifying agent to be added to the melt and/or determining an amount value (Vb) of an inoculating agent to be added to the melt, a means ( 1 8) for administrating a correct amount of structure-modifying agent and/or inoculating agent in response amount values (Va, Vb) signalled from the computer device the computer device being set up to establish cooling curves from each of said cups (22, 24, 26); the computer device being set up to establish the following parameters from the cooling curves: (i) the recalescence of the cooling curve recorded in the clean cup (ΔT no ); (ii) the recalescence of the cooling curve recorded in the tellurium cup (ΔT e ) (iii) the recalescence of the cooling curve recorded in the FeSi cup (ΔT FeSl ); (iv) the temperature of the local maximum of the cooling curve recorded in the FeSi cup (T FeS i(max)); (v) the temperature of the local maximum of the cooling curve recorded in the clean cup (T αo (max)); (vi) the temperature of the local maximum of the cooling curve recorded in the tellurium (vii) the temperature of the local minimum of the cooling curve recorded in the tellurium cup (T e (min)); (viii) the temperature of the local minimum of the cooling curve recorded in the clean cup (T no (min)); (ix) the temperature of the local minimum of the cooling curve recorded in the FeSi cup (T Fe si(min)); (x) the slope of recalescence of the clean cup curve (T uo (slope)); (xi) the slope of recalescence of the tellurium cup curve (T θ (slope)) (xii) the slope of recalescence of the FeSi cup curve (T FθS i(slope)) the computer device being set up to calculate a precise amount value (Va) of a structure-modifying agent and/or a precise amount value ( Vb) of an inoculating agent to be added to the melt in response to ΔT no , ΔT Θ , ΔT FΘSI „ T Fθ si(max), T no (max), T β (max), T e (min), T no (min), T FeSi (min), T no (slope), T β (slope), T FθS i(slope); the computer being set up to send a signal corresponding to said amount values to said means, whereby a correct amount of structure-modifying agent and/or inoculating agent is added to the melt (20).

Inventors: HOLLINGER BERTIL, SHAO STEN, HOLLINGER, BERTIL, SHAO, STEN
Applicants: HOLLINGER BERTIL, SHAO STEN, SINTERCAST AB, HOLLINGER, BERTIL, SHAO, STEN
Application year: 1997
Main classification: G01N25
IPC codes: B22D1, B22D2, C21C1, C21C5, C22C33, G01N25, G01N33