A process for production of a steel component

Abstract: A process for production of a steel component having a hard, rich carbon soluted surface and a tough, low carbon soluted core, incorporating the following steps: using an alloyed steel with a carbon content of 0.3-1.2 % C and with an alloy element acting as a strong carbide former, and subjecting a component formed from this material to induction heating, whereby the core is heated to a level in the lower region df the austenite area, thereby creating a certain soluted low carbon level in the component core, and rapidly heating the surface region to a higher region within the austenite area, thereby creating a high soluted carbon content in the surface region of the component.

Description: For producing components which are subjected to fatigue stresses case-hardening (carburization) is often used. This carburization gives the component a hard, carbon-rich surface at the same time as a tough, low-carbon core is obtained after hardening and annealing. Such a component has a very good resistance to wear and fatigue. The profile of hardness/residual stress obtained is schematically illustrated in the accompanying Fig. 1, and the surface residual stresses obtained are very favourable from fatigue life point of view. However the case-carburizing procedure is a rather expensive and slow process and therefore many attempts have been made to use surface hardening with induction heating. Thereby is normally used a low-alloyed steel having a higher content of carbon, e.g. 0.5-0.6% and the surface zone of the component is heated rapidly, whereupon the component is subjected to quenching. The profile of hardness/residual stress then obtained is illustrated schematically in the accompanying Fig. 2. For instance, FR-A-1 441 317 discloses a process of induction hardening in which only the surface is fully austenitized. This profile of hardness/residual stress obtained from a surface induction hardened component in combination with the low alloy steels used is sufficient in several situations, but often gives a limited contact fatigue strength and it also gives raise to problems under other fatigue conditions. One factor contributing to the often inferior properties is the reduction of hardness which is experienced at a distance below the surface of the material, and also the fact that most of the positive residual stresses are concentrated to the same depth. This occurs especially when using a medium hard core. The martensite formed at the conventional induction heating using a low-alloyed steel will almost immediately reach the full carbon content, i.e. 0.5 - 0.6 %. The purpose of the present invention now therefore is to propose a process using induction hardening, thereby giving a more in-expensive and more rapid result than case-carburization but which eliminates the drawbacks earlier experienced with induction hardening, and this has been obtained with a process as defined in the accompanying claim 1. For obtaining such a result it now is proposed a process adapted to give a result resembling to that obtained with case-carburizing, i.e. with a core having a solid soluted carbon content of 0.1 - 0.5 % and a surface layer having a carbon content of 0.5 - 1.2 %, and for this purpose is used an alloyed steel, which is tailored for giving such result, and this is obtained by increasing the content of a strong carbide former, such as e.g. chromium, whereby the austenite solid soluted carbon content can be reduced, such as illustrated in the graph according to Fig. 3. The process of the invention is given by claim 1. By using such an alloyed chromium steel it is possible to control and adjust the carbon content in the core by means of a sufficiently high content of the carbide-forming alloy element, such as chromium, and by using this alloyed steel with a particular induction heating, whereby the core is heated to a temperature just within the austenitic region, normally 800-1000°C, thus that a predetermined soluted carbon content is reached, and rapidly heating the surface layer to a high temperature in the austenitic region, normally 900-1200°C, it is obtained, after quenching, a soluted carbon content profile throughout the component, which is the same as obtained at case-carburizing, i.e. as shown in Fig. 1, however without the drawbacks of the case-carburizing process described in the introduction of this specification. Preferably the heating of the core is made prior to the heating of the surface layer, but it is possible to obtain the same result by reversing this procedure. Thus the process given by claim 1 and according to the invention reaches the goals set by using a certain material, e.g. a chromium steel having 0.3 - 1.2 % C and 1 - 25 % Cr together with a certain heat treatment procedure by which the component is austenitized throughout, whereby however the core and surface of the component are subjected to different temperature cycles. The invention is not limited to the embodiment described in the specification, but modifications of the process and steel composition, using other carbide formers than chromium, thus defined are possible within the scope of the appended claims.

Claims: A process for production of a steel component having a hard, rich carbon soluted surface and a tough, low carbon soluted core, using an alloyed steel with a carbon content of 0.3 - 1.2% C and with an alloy element acting as a strong carbide former, and subjecting a component formed from this material to induction heating, whereby the core area is heated to a level in the lower region of the austenite area, at a temperature between 800 and 1000°C, thereby creating a certain soluted carbon level in the component core of 0.1 - 0.5 % C, and heating the surface region to a higher region within the austenite area, at a temperature of about 900 - 1200°C, thereby creating a certain soluted carbon level in the surface region of the component of 0.5 - 1.2 % C. A process as claimed in claim 1, in which the strong carbide-forming alloy element chromium is used in an amount of 1 - 25 %.

Inventors: ANDERSSON JAN-ERIK, ANDERSSON, JAN-ERIK
Applicants: OVAKO STEEL AB
Application year: 1997
Main classification: C21D1
IPC codes: C21D6, C21D1