MINERAL FIBRE

Abstract: The invention concerns an iron poor mineral fibre having a high temperature resistance. The mineral fibre has the following composition in % by weight: SiO2 35 - 45, Al2O3 18 - 25, TiO2 0 - 3, MgO 12 - 20, CaO 10 - 20, Na2O + K2O 0 - 3, iron (Fe2O3+FeO) 0 - 3, B2O3 0 - 3, P2O5 0 - 4, other 0 - 3, whereby the sum of FeO + MgO >/= 15 % by weight.

Description: Mineral fibre The present invention relates to a fiberizable mineral composition as well as mineral fibres made therefrom which have a high temperature resistance. Mineral fibres made by melting and centrifuging of a mineral raw material, such as rock, slag or similar, are used to a high degree for the manufacture of mineral fibre mats and blankets, primarily for heat and sound insulation purposes in the construction industry. In addition to the manufactured mat exhibiting a good insu- lating capacity against heat and sound, one has recently started to pay more atten¬ tion to the properties of the mat also from a labour hygienic point of view. A wide selection of insulating products are available on the market which exhibit not only different heat insulating properties, but also a varying degree of tempera- ture resistance. Temperature resistant mineral fibre products are intended to mean products which can resist elevated temperatures under prolonged periods of time without changing shape or dimensions to any higher degree. Such products are thus attractive from a fire prevention point of view. Conventional glass fibre is temperature resistant at temperatures up to appr. 550°C, whereas the temperature resistance of conventional rock wool is better, up to appr. 700°C. There is, however, an interest in products having an even higher temperature resistance, up to 1100-1200°C, and such products are also available on the market. Such temperature resistant fibre products contain as the main oxides silicium oxide SiO 2 , and aluminium oxide, Al 2 O 3 , and in addition often an earth alkaline metal oxide, such as calcium oxide, CaO, or magnesium oxide, MgO. In additi¬ on, such products can contain varying amounts of other oxides, such as titanium oxide, TiO 2 , manganese oxide, MnO, boron oxide, B^, zirconium oxide, ZrO 2 , chromium oxide, Cr O 3 , the alkali oxides sodium and potassium oxide, Na 2 O and K 2 O, as well as contaminants. As examples of known art relevant in this con¬ nection, reference is made, for example, to US 4,461,840 and DE OS 1 496 662. According to the last mentioned publication, an especially advantageous composi¬ tion is obtained when the raw material melt contains appr. 4 - 12 % of iron oxi¬ des. In the mineral melt, the iron oxides are primarily present as divalent iron (appr. 75-90%) and to a lesser degree in the form of trivalent iron (appr. 25- 10%). The iron content of the mineral melt is a consequence of the fact that many economically attractive raw materials contain iron to higher or lower degree. The presence of divalent iron has an advantageous effect on the temperature resistan- nace of the fibre, its presence for this reason being beneficial. However, in recent times, one has seriously started to pay attention to the possible toxic effects of iron in mineral fibres, especially in fibres which in addition to temperature resis¬ tance have an increased solubility in biological fluids. Due to the toxicity risk, there is thus a need to minimize the total content of iron in mineral fibres. This, however, leads to an impairment of the temperature resis- tance. According to the present invention the problem relating to decreased temperature resistance when using small amounts of iron has been solvend in a mineral fibre composition, which contains as the main oxides silicium dioxide, aluminium oxide and calcium oxide. The problem has been solved by compensating the absence or the low level of divalent iron by including in such a composition magnesium oxide in an amount so that the total amount of magnesium oxide MgO and iron oxide FeO is at least 15 % by weight. In this way a mineral fibre composition is obtained which is both temperature resistant and has low toxicity. More specifically, the invention refers to a mineral fibre which has the following composition in % by weight whereby the sum of FeO+ MgO >_ 15 % by weight. The denomination "other" components above encompasses such possible conta- inants which are not of substantial importance for the properties of the manufac¬ tured fibre. It is known that within the range 0 - appr. 15 % the aluminium oxide content is direct proportional to the stability of the fibre in biological solutions, that is the more aluminium oxide the composition contains, the more stable or poorly solu¬ ble is the product. However, at a higher level, the tendency becomes reversed so that the solubility of the fibre increases in relation to the aluminium oxide con¬ tent. According to the invention, a fibre has thus been made having a good heat resistance but a low toxicity and a high solubility in biological solutions. Preferably the composition contains essentially equal amounts of MgO and CaO. According to a further preferred embodiment, the sum FeO + MgO + CaO <_ 32 % by weight. According to a preferred embodiment, the invention concerns a fibre having the following composition in % by weight whereby FeO + MgO >_ 15 % by weight. According to a very special embodiment, the invention refers to a fibre containing substantially The mineral composition is made in a conventional manner by mixing suitable raw material a such as stone, sand, dolomite, apatite, olivine, glass, or various slags and other suitable waste materials in suitable proportions. According to a preferred embodiment, the predominant raw material is slag fom iron manufactu¬ re, as such a product in itself is already iron poor. The desired increased alu- minium oxide content can be obtained by adding suitable aluminium containing raw materials, for example bauxite, in suitable amounts. Mineral fibres are manu¬ factured from the composition in a conventional manner, for example using cascade centrifugation. The following example illustrates the invention without restricting the same. Example Example In a cupola furnace the following components are charged having the composi¬ tions indicated in the table, in the amounts indicated in % by weight. From the melt obtained fibres are made in a conventional manner by cascade centrifugation, which fibres are collected onto a conveyor to form a mineral fibre mat. The mineral fibres have the following composition.

Claims: Claims 1. Mineral fibre, characterized in that it has the following composition in % by weight: whereby the sum FeO+ MgO >_ 15 % by weight. 2. The mineral fibre according to claim 1, characterized in that it contains subs¬ tantially equal amounts of MgO and CaO. 3. The mineral fibre according to claim 1 or 2, characterized in that the FeO + MgO + CaO _<_ 32 % by weight. 4. The mineral fibre according to claim 1, 2 or 3, characterized in that it has the following composition in % by weight: whereby FeO + MgO >_ 15 % by weight. 5. The mineral fibre according to claim 4, characterized in that it has substan¬ tially the following composition in % by weight:

Inventors: HAKALA JAN, PERANDER MICHAEL, HAKALA, JAN, PERANDER, MICHAEL
Applicants: HAKALA JAN, PARTEK PAROC OY AB, PERANDER MICHAEL, HAKALA, JAN, PERANDER, MICHAEL
Application year: 1997
Main classification: C03C13
IPC codes: C03C13