Polymerization catalyst

Abstract: An olefin polymerization catalyst includes a halogen-containing magnesium compound; a titanium compound; and an additive that is the reaction product of an aluminum alkyl and calixarene.

Description: The invention relates to a polymerization catalyst, particularly to a polymerization catalyst for the polymerization of olefins. Numerous processes are known in the art for polymerization of olefins such as ethylene into polyolefins such as polyethylene. Parameters of concern during the polymerization of olefins include the yield of polyolefin, the melt flow index (MFI) of the polyolefin product, the bulk density of the polyolefin product, and the content of fines in the resulting polyolefin product. Numerous catalysts and processes are known in the art for polymerizing olefins so as to obtain polyolefins. The need remains, however, for a polymerization catalyst for polymerization of olefins which has good activity toward the polymerization reaction, while providing a final product with a desirable melt flow index and bulk density, and further while reducing the content of fines therein. It is therefore the primary object of the present invention to provide a polymerization catalyst for polymerization of olefins which has enhanced activity toward the polymerization reaction so as to provide enhanced yield of polyolefin product with a desirable bulk density. It is a further object of the present invention to provide an olefin polymerization catalyst wherein the polyolefin product has a reduced content of fines. It is a further object of the present invention to provide an additive for an olefin polymerization catalyst which enhances the characteristics of the catalyst for polymerization of olefins. Other objects and advantages of the present invention will appear hereinbelow. SUMMARY OF THE INVENTION In accordance with the present invention, the foregoing objects and advantages are readily attained. In accordance with the invention, an olefin polymerization catalyst is provided which comprises a halogen-containing magnesium compound; a titanium compound; and an additive that is the reaction product of an aluminum alkyl and calixarene. BRIEF DESCRIPTION OF THE DRAWINGS A detailed description of preferred embodiments of the invention follows, with reference to the attached drawing, wherein: FIG. 1 illustrates a calixarene additive component according to the invention DETAILED DESCRIPTION The invention relates to an olefin polymerization catalyst, especially to a catalyst for polymerization of olefins such as ethylene into polyolefins such as polyethylene. The present polymerization catalyst is based upon Ziegler-Natta catalysts typically comprising a magnesium halide support and a titanium compound supported on the magnesium halide support. In accordance with the present invention, a series of additives have been developed which, when incorporated into the polymerization catalyst, provide enhanced activity and characteristics of the catalyst toward the polymerization reaction. In accordance with the invention, it has been found to be advantageous to incorporate an additivethat is the reaction product of an aluminum alkyl and calixarene so as to provide the olefin polymerization catalyst according to the present invention. A catalyst containing such an additive according to the present invention has been found to have excellent activity toward the polymerization reaction so as to provide an enhanced yield of polyolefin having desirable qualities, while using a relatively small amount of titanium supported on the magnesium, and further while providing a catalyst which results in a reduced amount of fines in the resulting polyolefin product. In accordance with the invention, the halogen containing magnesium compound may suitably be magnesium chloride, while the titanium compound may suitably be titanium chloride, especially titanium tetrachloride. As set forth above, the additive which has been found in accordance with the invention to provide desirable characteristics in a polymerization catalyst is the reaction product of an aluminum alkyl and calixarene. Referring to FIG. 1, an example of a calixarene compound which upon reaction with an aluminum alkyl, the reaction product thereof is suitable as an additive in accordance with the present invention is shown. Calixarene compounds have been found in accordance with the present invention to enhance the activity of a polymerization catalyst for the polymerization of olefin when the reaction product between calixarene and an aluminum alkyl is added as an additive. Examples of suitable calixarene compounds include calix[4]arene, calix[6]arene, calix[8]arene, 4-tent-butylcalix[4]arene, 4-tert-butylcalix[6]arene, 4-tert-butylcalix[8]arene and mixtures thereof. Specific examples of suitable aluminum alkyl compounds include trimethylaluminum, triethylaluminum, tri-i-butylaluminum and mixtures thereof. The olefin polymerization catalyst of the present invention preferably has a substantially monomodal and narrow particle size distribution which preferably has an average particle size of between 2 to 200 µm. Further, the catalyst according to the present invention preferably has a molar ratio Ti/Al of between 10 to 100, and a molar ratio Mg/Al of between 10 to 600. In accordance with the invention, the additive of the present invention may suitably be added to the catalyst ingredients during synthesis of same. Alternatively, the additive of the present invention may suitably be incorporated into the catalyst composition, before or during olefin polymerization. In accordance with the invention, the additive may be prepared through different methods. The preparation of the reaction product of an aluminum alkyl and calixarene may, for example, be accomplished as follows: A solution of trimethylaluminum in toluene may be added to a suspension of a calixarene reactant and anhydrous toluene, preferably while stirring in a cold bath for a sufficient period of time, such as approximately 2 hours. The temperature of the mixture is then increased or allowed to reach room temperature, and additional stirring is carried out. A solid is eventually obtained, after evaporation of solvent under a vacuum, and the resulting calixarene additive compound can be characterized by IR and/or NMR spectroscopies. Such an additive will typically exhibit spectroscopies as follows: IR(cm -1 ): 2900-2850, 1510,1380, 1290 (C-H); 600 (Al-OR). 1 H NMR (CDCl 3 ; 0.1 M, 25°C) (ppm): 7.0 (m, H, Ar); 3.3 (m, Ar-CH 2 -Ar); 1.0 (m, CMe 3 ); -1.1 (M, Al-Me). While the foregoing provide examples for preparation of additive in accordance with the present invention, it should of course be noted that other processes for preparation of the desired additive may be known to those of ordinary skill in the art and could, of course, be used to prepare the additive of the catalyst of the present invention. In further accordance with the invention, a catalyst can be prepared through a synthesis method wherein a mixture of a halogen-containing magnesium compound such as magnesium chloride, a C 4 -C 12 aliphatic or aromatic solvent such as decane, a C 6 -C 12 aliphatic or aromatic alcohol such as 2-ethylhexanol and the desired additive is formed. The mixture is preferably charged into a reactor vessel under an inert gas atmosphere, and reacted at an elevated temperature such as approximately 110-140°C for a period of time of approximately 1-4 hours, preferably under stirring. The reaction mixture may then in accordance with the present invention be cooled, preferably to between 0°C to -20°C, and a volume of titanium halide such as titanium tetrachloride is slowly added. An additional charge of the desired additive is then added to the mixture, and the mixture is continuously stirred for an additional time period. The mixture is then heated again to an elevated temperature between 60-100°C, for a period of time of 1 to 3 hours, cooled to room temperature and then allowed to settle, and is separated by filtration. The separated solid is then preferably suspended in a solution of titanium tetrachloride, heated for another period of time, and resulting solid is again separated for example by filtration. The solid so obtained is then purified, for example by repeated washing with hot hexane, and is then dried under vacuum or inert gas stream. The resulting catalyst is in powder form and preferably has a titanium content of between 3 to 12 wt.%, and an average particle size of between 4 to 100 µm. In accordance with the present invention, the above-described process for synthesis has been found to provide catalyst having improved activity. Nevertheless, other methods are of course known in the art for the synthesis of such catalysts, and the catalyst of the present invention could be prepared by such known methods. The olefin polymerization catalyst of the present invention can suitably be used for olefin polymerization reactions so as to produce polyolefins such as polyethylene. A polymerization reactor may suitably be subjected to evacuation-argon substitution, and then charged with dehydrated and oxygen-removed hexane as well as triethylaluminum and hydrogen so as to prepare the reactor. The reactor may then be saturated with olefins such as ethylene at a working pressure and temperature, for example 8 bar and 80°C, and the catalyst according to the present invention may then be charged into the reactor. After a suitable amount of time, such as, for example, 2 hours, the resulting polymer slurry can be filtered, and a yield of polyolefin such as polyethylene is produced. In accordance with the invention, the polyolefin product preferably has a melt flow index of between 0.01 to 200, and a bulk density of between 0.25 to 0.40. Further, the polymerization according to the present invention using the catalyst of the present invention preferably results in the final polyolefin product having a fines content of less than or equal to 15% of particles having a diameter of less than or equal to 106 µm. The following examples further illustrate preparation of additive and catalyst and polymerization in accordance with the invention. EXAMPLE 1 This example illustrates the preparation of a calixarene additive (Additive A), as well as the preparation and use of a catalyst including this additive. A solution of trimethylaluminum (3.7 ml, 0.038 mol) in 30 ml of toluene was added dropwise to a suspension of 500 mg of 4-tert-butylcalix[8]arene [8]arene in 30 ml of anhydrous toluene. The reaction was conducted with magnetic stirring in a cold bath at -76°C. Upon completion of the alkyl solution addition, the reaction mixture was allowed to reach room temperature and further stirred for 1 hour. Evolution of gas was observed during the process. A white solid was obtained after evaporation of the solvent under vacuum. The resulting additive product was characterized by IR and NMR spectroscopies as follows: IR: (cm -1 ) 2900-2850, 1510, 1380, 1290 (C-H); 600 (Al-OR). 1 HNMR (CDCl 3 ; 0.1 M, 25°C) (ppm): 7.0 (m, H, Ar); 3.3 (m, Ar-CH 2 -Ar); 1.0 (m, CMe 3 ); -1.1 (m, Al-Me). EXAMPLE 2 The preparation of a catalyst in accordance with the invention using additive A as prepared above was then carried out. 6.00 g of anhydrous magnesium chloride, 50 ml of decane, 30 ml of 2-ethylhexanol and 1.00 g of Additive A, (as prepared in Example 1) were admixed and charged into a reactor vessel under inert gas conditions. The mixture reacted vigorously with gas evolution at room temperature. After this, the reactor was heated to 150°C for 3 hours. The resulting solution was cooled to -20°C and then 100 ml of titanium tetrachloride were slowly added for a period of 1.5 hours. The solution was stirred for an additional period of 30 minutes, allowed to reach room temperature with occasional stirring and a further 0.70 g of Additive A suspended in 20 ml of decane were added. The mixture was heated at 90°C for 2 hours, the supernatant liquid was discarded, and the solid was treated with 30 ml of titanium tetrachloride and heated to 80°C for 2 hours. The solid was collected by filtration, repeatedly washed with hot hexane using a total volume of about 600 ml, and dried under a vacuum. The resulting reddish-brown powder showed a titanium content of 7.7% and an average particle size of 18 µm. The catalyst prepared as above was then used in a polymerization reaction. A stainless steel autoclave having a stirrer, a temperature controlling device and 2 liter capacity was provided. The reactor was subjected to evacuation-argon substitution several times and was charged with 1 liter of dehydrated and oxygen-removed hexane, 1.68 mmol of triethyl aluminum and 3 bar of hydrogen. The reactor was saturated with ethylene at the working pressure of 8 bar and 80°C, and approximately 10 mg of the catalyst of Example 2 containing Additive A were charged into the reactor. Polymerization was carried out for 1 hour, at which time the resulting polymer slurry was filtered. The yield of polyethylene was 182 g with a melt flow index of 0.76 g/10 min and a bulk density of 0.27 g/ml. The final product contained 12.8% fines having a diameter of less than 106 µm.

Claims: An olefin polymerization catalyst, comprising: a halogen-containing magnesium compound; a titanium compound; and an additive that is the reaction product of an aluminum alkyl and calixarene. A catalyst according to claim 1, wherein said catalyst has a substantially monomodal particle size distribution having an average particle size of between 2 and 200 µm. A catalyst according to claim 1, wherein said catalyst has a Ti/Al molar ratio of between 10 and 100. A catalyst according to claim 1, wherein said catalyst has an Mg/Al molar ratio of between 10 and 600. A catalyst according to claim 1, wherein said additive results from reaction of a calixarene selected from the group consisting of 4-tert-butylcalix[4]arene, 4-tert-butylcalix[6]arene, 4-tert-butylcalix[8]arene, and mixtures thereof. A catalyst according to claim 1, wherein said magnesium halide comprises MgCl 2 and wherein said titanium compound comprises TiCl 4 .

Inventors: AGRIFOGLIO GIUSEPPE, DIAZ BARROS ANTONIO, LISCANO JOSE, MATOS JOSE ORLANDO, TRUJILLO MARIANELA, AGRIFOGLIO, GIUSEPPE, DIAZ BARROS, ANTONIO, LISCANO, JOSE, MATOS, JOSE ORLANDO, TRUJILLO, MARIANELA, Liscano, José, Matos, José Orlando
Applicants: INTEVEP SA
Application year: 1997
Main classification: C08F4
IPC codes: C08F110, C08F4, C08F10