PRODUCTION OF WATER-LESS LITHOGRAPHIC PLATES

Abstract: There is described a water-less lithographic plate precursor which comprises on an aluminium plate a light-sensitive composition which comprises a polymer with hydroxy functional groups, an acid generator which when light exposed yields an acid together with a silyl ether of general formula (I), where Rf is a fluoroaliphatic group having 3 to 10 carbon atoms, Y is oxygen, SO2, carbonyl or a direct link, X is N R4 where R4 is hydrogen or lower alkyl having up to six carbon atoms or is a direct link, each of R1, R2 and R3 are lower alkyl groups having up to six carbon atoms and R5 is a lower alkyl group having up to six carbon atoms.

Description: Production of water-less lithographic plates. Lithographic plates may be divided into two classes. Those which require dampening water which is fed to the non-image areas of the plate, forms a water film and acts as an ink-repellant layer; this is the so-called fount solution. Those plates which require no fount solution are called driographs or water-less lithographic plates. Most lithographic plates at present in use are of the first type and require a fount-solution during printing. However, lithographic plates of this type suffer from a number of disadvantages. Some of these are: - a) adjustment of the proper ink-water balance during press operation is difficult and requires great experience. If the correct ink-water balance is not achieved scumming is occasioned when the printed ink image extends into the non-image areas ruining the printed image. b) adjustment of the ink-water balance at start-up or re-start up is particularly difficult and can not be stabilised until a large number of sheets have been printed, thus incurring waste, c) the ink tends to become emulsified which leads to poor adherence of the ink on to the plate which causes problems in colour reproduction and in dot reproduction, d) the printing press has to be provided with a dampening system, thus increasing its size and complexity. e) The plate care chemistry and fount solutions require careful control and selection. Further plate cleaners contain significant levels of solvent which is not desirable. However, with water-less plates in which the ink-releasing layer is, for example, a cured silicone layer or a fluoroalkyl compound there is no scumming and clearer images can be produced. Very often water-less plates comprise a base material, for example aluminium plate, on which a photosensitive layer is coated, on this photosensitive layer there is coated a silicone layer or a fluoroalkyl compound. After imagewise exposure and development in which selected areas of the photosensitive composition are altered, the overlying silicone or fluoroalkyl compound layer is removed and the plate is inked up. The ink adheres only to those areas of the plate not covered by the silicone or fluoroalkyl compound remaining after development. Thus the plate can be used without a fount solution. However, in practice it has proved difficult to get the silicone or fluoroalkyl compound layer composition to adhere to the photosensitive layer. In spite of the idea of water-less plates having been described in patent specifications for at least fifteen years very little has been done to commercialise the idea and water-less plates which have been and are being sold are more expensive than the conventional plates which require a fount solution. We have developed a water-less lithographic plate which is different in concept to the proposed water-less lithographic plate and furthermore a plate which requires no wet processing. Therefore according to the present invention there is provided a water-less lithographic plate which comprises on an aluminium plate a light-sensitive composition which comprises a polymer with hydroxy functional groups, an acid generator which when light exposed yields an acid together with a silyl ether of the general formula I:- where Rf is a fluoroaliphatic group having 3 to 10 carbon atoms, Y is oxygen, SO 2 , carbonyl or a direct link, X is N R, where R, is hydrogen or lower alkyl having up to six carbon atoms or is a direct link, each of R,, R 2 and R 3 are lower alkyl groups having up to six carbon atoms and R 5 is a lower alkyl group having up to six carbon atoms. Preferably each of R,, R 2 and R 3 are the same. The light-sensitive composition of the present invention may be U-V light sensitive, visible light sensitive or infra-red radiation sensitive. When the composition is infra-red light sensitive there should be present in the composition an infra-red light absorbing compound. According to another feature of the present invention there is provided a method of producing a water-less lithographic plate which comprises imagewise exposing the above set forth composition to UV or visible light and the above set forth composition which also comprises an infra-red absorbing compound to IR radiation to generate an acid and then heating the imagewise exposed composition to over 100°C and then inking up the plate using an inking roller and water-less ink. Preferably after light-exposure the composition on the plate is heated at 130°C for three minutes. Conveniently this heating can be carried out in a baking oven of the conventional type. It is thought that the release surface of the plate is formed by the silyl ether compound reacting with the hydroxyl groups of the polymer in those areas of the plate which have been imagewise exposed. The acid generated during the imagewise exposure hydrolyses the alkoxy OR,/OR 2 /OR 3 groups on the silyl ether compound to form an oligomer via a condensation reaction. This oligomer adsorbs on to the polymer by hydrogen bonding. The heating step converts these hydrogen bonds to covalent bonds by the elimination of water. This yields a low surface energy film formed by the Rf groups present on the surface of the plate. Thus no wet-processing is required to form the water-less lithographic plate. The step of working-up the plate, after the heating step, by using a roller and water-less ink removes the unreacted silyl ether compound from the surface of the plate. However, it is possible to include a wet-development step before inking-up. Useful developers include silicate based developing solutions of the type well known in the trade and water. Particularly suitable compounds of formula I are silyl ether A of the formula II:- CF, 0 OMe nn «J I F 2 ) 7 S S ■ ■ N - (CH 2 ) 3 - Si - OMe »/ 1 1 0 Et OMe silyl ether B of the formula III:- OEt CF 3 - CF 2 - 0 - (CH 2 ) 3 - Si - OEt OEt silyl ether C of the formula IV:- OEt I F-(CF 2 ) 8 - (CH 2 ) 2 - Si - OEt / OEt By an acid generator which when light exposed means a compound together with in some cases a light absorbing compound which when light-exposed to UV, visible or IR radiation generates an acid. Useful compounds of this type are triazines of the general formula V:- wherein R, is a substituted or unsubstituted aliphatic or aromatic group and R 2 and R 3 are each a haloalkyi group. An example of a triazine of this type is 2(4-methylthiophenyl)-4,6-trichloromethyl- S-triazine. Other useful acid generator compounds include diazonium salts for example 4-diazo diphenylamine hexafluorophosphate and iodonium compounds for example diphenyl iodonium iodide. Other examples of acid generators include sulphonium, phosphonium, selenonium, arsonium salts and salts of fluorophosphoric acid. Another group of useful acid generator compounds are the so-called Lewis acids. When acid generator compounds as just set forth are exposed to UV light an acid will be generated. However, if the imagewise exposure is to be IR light an IR absorber is required to be present in the composition. Similarly if the imagewise exposure is to be visible light a sensitizer such as a titanocene compound or a ketocoumarin compound which absorbs light in the region of the exposing visible light is required. Useful infra-red light absorbers include carbon black, small metal particles for example iron or copper and thin metal films for example aluminium or platinum and dyes for example :- By polymer having hydroxy functional groups is meant a polymer having hydroxy groups which when heated in the presence of another compound having hydroxy groups is capable of condensation therewith with the elimination of water. Examples of polymers with hydroxy functional groups include novalac resins, hydroxypropyl cellulose, polyvinyl butyral, some epoxy resins and polyvinyl alcohol. In examples 1 - 8 silyl ether A as set forth above was used in the composition. The acid generator compound was a triazine. It is to be understood that the light-sensitive composition coated on the aluminium plate can be coated in two layers as described in Example 11 which follows. The invention is described by the following examples. Example 1 Onto a piece of anodised, ungrained aluminium substrate a solution of composition 1 was coated using a metered wire bar and dried at 100°C for 1 minute. Composition 1:- 1.2g of a solution of novalac resin LB744 (supplied by Bakelite) - 10% solids in 1 -methoxy propan-2-ol. 0.46g of a solution of 2(4-methylthiophenyl)-4,5-trichloromethyl-S-triazine - 3% solids in 2-methoxyethyl acetate. 0.12g of a solution of silyl ether A - 60% solution in ethanol. This solution was mixed for 15 minutes prior to coating. The plate was then exposed to UV radiation through a mask and heated in an oven at 130°C for 3 minutes. After cooling the plate was inked up with a rubber roller and waterless ink to give a positive plate with clean release and strongly inked image areas. Example 2 As example 1 but using a 10% solids solution of hydroxy propyl cellulose in 1 -methoxy-propan-2-ol for the novalac resin. Example 3 As example 1 but using a 10% solids solution of poly(vinylbutyral) in 1 -methoxy-propan-2-ol substituted for the novalac resin. Example 4 As Example 1 but using a 10% solids solution of Epikote 1004 resin (as supplied by Asto Stag Ltd.) in a solvent mixture of 9 parts methyl lactate to 1 part benzyl alcohol instead of the novalac resin. Example 5 As examples 1 and 3 but using grained and anodised aluminium substrate. Example 6 Onto a piece of anodised, ungrained aluminium substrate a solution of composition 2 (see below) was coated using a metered wire bar and dried at 100°C for 1 minute. Composition 2:- 0.6g - 2A 0.06g - Silyl ether A 60% solids in ethanol. This coating was mixed for 15 minutes. Composition 2A:- 0.6g of a solution of Epikote 1004 (as supplied by Astro Stag Ltd.) - 25% solids in a solvent mixture of 9 parts methyl lactate to 1 part benzyl alcohol. 0.3g DS019 (as supplied by PCAS). 2.6g of 9:1 methyl lactate: benzyl alcohol. (DS019 is a diazonium compound and was used in this example in place of the triazine compound as the acid generator compound.) The resultant plate was exposed to U.V. radiation through a mask and then heated in an oven at 130°C for 80 seconds. After cooling the plate was inked up using a rubber roller and waterless ink to give a positive plate with a clean release and strongly inked image area. Example 7 (IR + UV exposure) Onto a piece of anodised, ungrained aluminium substrate a solution of composition 3 was coated using a metered wire bar and dried at 100°C for 1 minute. Composition 3: 0.6g of composition 2A. 0.18g of IR sensitiser II - 3.2% in dimethyl formamide. 0.06g of silyl ether A-60% solution in ethanol. This coating was mixed for 15 minutes. The coated plate was divided into two halves referred to as 3 A and 3B. Plate 3 A was exposed to IR light directly and heated in an oven at 130°C for 80 seconds. Plate 3B was imaged using UV light then heated at 130°C for 80 seconds. Both plates 3 A and 3B were inked up using a rubber roller and waterless ink to yield positive plates, no processing was employed. The presence of the IR sensitiser did not affect the sensitivity of the plate to UV exposure. The plates of the present invention which comprise an IR absorbing compound can be digitally imaged using an IR emitting laser in an image setter. Thus the plate prepared in this Example can either be placed in an image setter and be digitally imaged or placed in an image frame and be imaged by U.V. light through a mask. Example 8 - Wet development before inking-up Formulation as for Example 6 The plate was exposed to UV radiation through a mask and heated in an oven at 130°C for 80 seconds. The plate was then developed for 30 seconds using water, after drying the plate was inked to yield a positive plate. Example 9 - Alternative silyl ethers Composition 9A 0.6g of composition 2A 0.04g of silyl ether B Composition 9B 0.6g of composition 2A 0.04g of silyl ether C The above compositions were mixed for 15 minutes, then coated onto a piece of grained and anodised aluminium with a metered wire bar and dried at 100°C for 1 minute. The coatings were exposed to UV radiation through a mask then heated in an oven at 130°C for 180 seconds. The resultant plates each gave good image/background discrimination on inking without the need for water. Example 10 - non-condensed diazonium salt Composition 10 was coated onto aluminium substrate using a metered wire bar and dried at 100°C for 60 seconds. Composition 10 0.25g - 10% w/w solids Epikote 1004 in methyl lactate : benzyl alcohol (9:1) 0.19g - 10% w/w LDN1PF6 diazonium salt (Varichem Ltd) in DMF 0.06g - 60% of silyl ether a in ethanol The above composition was mixed for 15 minutes, prior to coating. The coated plate was exposed to UV light through a mask and then heated at 100°C for 1 minute. The resultant plate, on inking, gave good image/non image discrimination without the need for dampening. Example 11 - Two layer coating Composition 2A was coated onto grained and anodised aluminium using a metered wire bar and was dried at 100°C for 1 minute. This was then over-coated with Composition 11 using a metered wire bar and dried at 100°C for 60 seconds. Composition 11 :- Silyl ether A (60% solids in ethanol) diluted to 6% with cyclohexane. The resultant plate was exposed through a mask to UV light and then heated at 130°C for 80 seconds. Good image/non image discrimination was seen on inking without the use of dampening solution. Example 12 - IR Sensitised using Carbon Black Composition 12 was coated onto grained and anodised aluminium using a metered wire bar and dried at 100° C for 1 minute. Composition 12 0.75 g of 20% w/w carbon black / epikote 1004 solution in 9:1 methyl lactate : benzyl alcohol. 0.3g of lOO% DSO19 0.67g of 100% dimethylformamide 1.38g of 9:1 methyl lactate : benzyl alcohol The composition of the 20% carbon black / epikote solution was : 0.34g of carbon black FW1 (supplied by Degussa AG) 0.66g of 100% epikote 1004 3.60g of methyl lactate 0.4g benzyl alcohol The carbon black was dispersed by ball milling it into the solution. This was then over coated with Composition 11 using a metered wire bar and dried at 100°C for 30 seconds. The resultant plate was imaged using a 200m W, 850nm laser and baked at 130°C for 80 seconds. The plate was developed and inked by applying waterless ink with a roller to give good image discrimination without the need for damping. Example 13- IR sensitised using a Thin Metal Film Composition 2A was coated onto the metallised side of (a) an aluminised polyester sheet (supplied by HiFi) or (b) a polyester sheet (supplied as Planfoil by Horsell Graphic Industries) sputter coated with a thin layer of platinum. The coating was dried at 100°C for 1 minute. These were then over coated with Composition 1 1 using a metered bar and dried at 100°C for 30 seconds The plates obtained were imaged using a 200mW 830nm laser and baked at 130°C for 80 seconds. On inking using waterless ink and a roller with no damping applied, positive plates were produced with good image/non-image discrimination

Claims: Claims: 1. A waterless lithographic plate precursor which comprises on an aluminium plate a light-sensitive composition which comprises a polymer with hydroxy functional groups, an acid generator compound which when light exposed yields an acid together with a silyl ether of the general formula I OR, Rf - (Y)-(X)-R 5 - Si - OR 2 OR 3 where Rf is a fluoroaliphatic group having 3 to 10 carbon atoms, Y is oxygen, SO 2 , carbonyl or a direct link, X is N , where R 4 hydrogen or lower alkyl having up to six carbon atoms or is a direct link, each of R R 2 and R 3 are lower alkyl groups having up to six carbon atoms and R 5 is a lower alkyl group having up to six carbon atoms. 2. A water-less lithographic plate precursor according to claim 1 wherein the silyl ether of formula I R,, R 2 and R 3 are the same. 3. A water-less lithographic plate precursor according to claim 2 wherein R„ R 2 and R 3 are each methyl or ethyl. 4. A water-less lithographic plate precursor according to claim 1 wherein the silyl ether compound is compound of formula II CF 3 0 OMe /» \ (CF 2 ) 7 S - N - (CH 2 ) 3 - Si - OMe H I 0 Et OMe or of formula III OEt I CF 3 - CF 2 - 0 - (CH 2 ) 3 - Si - OEt OEt or of silyl ether of the formula IV:- OEt / F-(CF 2 ) g - (CH 2 ) 2 - Si - OEt / OEt 5. A waterless lithographic plate precursor according to claim 1 wherein the acid generator is a triazine of the formula V wherein R, is a substituted or unsubstituted aliphatic or aromatic group and R 2 and R 3 are each a haloalkyi group. 6. A waterless lithographic plate precursor according to claim 1 wherein the acid generator is a diazonium salt, an iodonium compound, a sulphonium, phosphonium, selonium or arsonium compound or a salt of fluorophosphoric acid. 7. A waterless lithographic plate precursor according to claim 1 wherein the polymer with hydroxy functional group is selected from a novalac resin, hydroxypropyl cellulose, polyvinyl butyral, an epoxy resin and polyvinyl alcohol. 8. A method of producing a water-less lithographic plate which comprises imagewise exposing the composition as claimed in claim 1 to UV or visible light and the above set forth composition which also comprises an infra-red absorbing compound to IR light to generate an acid and then heating the imagewise exposed composition to over 100°C and then inking up the plate using an inking roller and water-less ink. 9. A method according to claim 8 wherein after light exposure the composition on the plate is heated at 130°C for three minutes.

Inventors: BAYES STUART, BENNETT PETER ANDREW REATH, SMITH CAROLE-ANNE, BAYES, STUART, BENNETT, PETER, ANDREW, REATH, SMITH, CAROLE-ANNE
Applicants: BAYES STUART, BENNETT PETER ANDREW REATH, HORSELL GRAPHIC IND LTD, SMITH CAROLE ANNE, BAYES, STUART, BENNETT, PETER, ANDREW, REATH, HORSELL GRAPHIC INDUSTRIES LIMITED, SMITH, CAROLE-ANNE
Application year: 1997
Main classification: G03F7
IPC codes: B41N1, G03F7