AN ELECTROLYTE SYSTEM, A METHOD FOR THE PREPARATION THEREOF, THE USE THEREOF AND A BATTERY CONTAINING THE ELECTROLYTE SYSTEM

Abstract: An electrolyte system consisting essentially of: a solvent mixture and a salt mixture, whereby the solvent mixture essentially consists of ethylene carbonate and dimethyl carbonate, and the salt mixture consists of lithium tetrafluoroborate and lithium hexafluorophosphate, and whereby the salt mixture comprises 60-90 % by mole of lithium tetrafluoroborate and 10-40 % by mole of lithium hexafluorophosphate, a method for the preparation of this electrolyte system, comprising the steps of mixing the solvents, dissolving the salts in the solvent mixture, optionally adding a thickening agent to the solution, optionally incorporating the mixture obtained in a separator, and optionally adding monomers or oligomers having one or more polymerisable functional groups and inducing polymerisation of these monomers or oligomers, and a battery containing the above-mentioned electrolyte system.

Description: An electrolyte system, a method for the preparation thereof, the use thereof and a battery containing the electrolyte system. This invention relates to an electrolyte system, a method for the preparation thereof, the use thereof, and a battery containing the electrolyte system, and particularly to an electrolyte composition and a rechargeable battery of high co patiblity towards positive electrode structures, high cyclability and low irreversible loss. The use of non-aqueous electrolytes has allowed the development of electrochemical systems based on lithium-containing negative electrode structures and positive intercalation metal oxides, which have high energy density For those systems, however, the limiting factor for their continuous performance has been their low electrolyte electrochemical stability, leading to poor cell cyclability. Said cyclability is defined as the number of times a battery can be charged and discharged between 4.2V and 3.0V at a current density of l mΛ/cm before the capacity is reduced to 80% of the discharge capacity of the first discharge of the battery. Upon operation of such electrochemical cells, a capacity loss during initial charging of the cells is observed, as is a fading capacity upon extended cycling. Those capacity reduction phenomena can be ascribed to the instability of the electrolyte towards the negative and the positive electrode of the electrochemical cell The instability towards the negative electrode leads to gassing and formation of a passivating film The instability towards the positive electrode leads to corrosion of the electrode structure Both phenomena result in loss of active material from the cell Further, passivation and corrosion may lead to increased cell impedance, and reduced materials utilisation and rate capability. The gassing and the formation of the passivating film is believed to take place during the initial charging, subsidiaiy during the young life of the electrochemical cell Theiefore, the capacity loss dunng the initial chaiging is mainly ascribed to the instability of the electrolyte-negative electi ode structure-system The coi rosion is an on-going piocess, which is believed mainly to take place towaids the end of each charging cycle at maximum potential of the positive electrode structuie Thei efoi e the capacity loss dining cycling is mainly ascribed to the instability of the electi olyte- positive electi ode stiucture-system, l e lack of compatibility of the electi olyte towards the positive electrode structuie The capacity loss duπng the first chaiging of the batteiy is l efen ed to as the initial ni eversible loss, and is defined as the loss of active lithium in mΛh of charge vs the weight of the negative electrode structuie in grains In this context the loss is defined as active matenal which reacts lπ eversibly with the negative electiode stuictui e, and which cannot be deintei calated fi om the stiuctui e dui mg the subsequent dischaige of the battery The known electi olyte oi electrolyte systems ai e mainly composed of one oi moi e salts in a solvent oi solvent mixtuie Iraditionally, a numbei of salts aie commonlγ applied in non-aqueous electi olyte systems, including lithium peichloiate, lithium hexafluorai senate, lithium tnfluoromethylsulfonate, lithium teti afluoroborate, lithium hexafluoiophosphate, lithium biomide, lithium hexafluoioantimonate, LιC(CFιS0 2 )} and LιN(CFιSθ2) 2 The solvents used ai e e g ethylene caibonate, propylene caibonate, dimethyl carbonate, diethyl caibonate, γ-butyrolactone, γ-valerolactone, tetrahydrofuran, 2-methyl teti ahydrofuran dimethoxyethane, diethoxyethane, methyl acetate, methyl foi mate, 1 3-dιoxolane, sulfolane, acetonitπle and butyionitπle A large number of electiolyte systems have been composed from these salts and solvents in ordei to impi ove inter aha the electiochemical stability of the systems It has now been found that the cyclability and stability of an electrochemical system such as a battery may be improved considerably, by using a electrolyte system having the composition of claim 1 By using salt mixtures of lithium tetrafluoroborate and lithium hexafluorophosphate, excessive in the borate, in batteries it has been observed, that high cyclability (low capacity loss during extended discharge-recharge) and a low initial irreversible loss can be obtained. This excellent performance has been found for those salts compositions containing 60- 90% by mole of lithium tetrafluoroborate and 10-40% by mole of lithium hexafluorophosphate. These salt compositions are believed to be dominated by a high compatibility of the borate against the positive electrode structure, supported by negative structure compatibility and contribution to the conductivity from the phosphate. It has further been found that the performance is especially pronounced for the high stability solvent mixture of ethylene carbonate and dimethyl carbonate and particularly if these solvents are the only liquid solvents present. Further, the performance of the electrolyte system is especially pronounced, when combined with negative electrode structures of carbonaceous intercalation materials like coke and graphite and/or positive electrode structures of lithium manganese oxide spinels Λ number of patents describe the use of the lithium tetrafluoiOborate/lithium hexafluorophosphate salts in a solvent mixture consisting of or comprising ethylene carbonate and dimethyl carbonate. US patent 5,192,629 and US 5,422,203 of Bell Communication Research describe the use of an electrolyte system with a mixture of ethylene carbonate (EC) and dimethyl carbonate (DMC) as solvent and lithium hexafluorophosphate and mixtures of lithium hexafluorophosphate with up to about equal mole parts of lithium tetrafluoroborate as solute. The teaching in these patents is that this group of electrolytes provides an improved resistance against oxidation. The only example showing the effect of the electrolyte, is composed from 1M LiPF f , in 95 DMC 5 EC Though it is mentioned that the electrolyte may comprise lithium tetrafluoroborate, nothing is mentioned about the effect of lithium tetrafluoroborate. US 5,079, 109 of Toshiba Battery Co., Ltd. describes an electrolytic salt consisting of one of lithium phosphate hexafluoride (LiPF fi ) and lithium borofluoride (LiBF ) in a solvent mixture consisting of ethylene carbonate, 2-methyltetrahydrofuran and at least one ester-based nonaqueous solvent selected from butylene carbonate, dimethyl carbonate, γ-butyrolactone and sulfolane. In none of the numerous examples of this patent, however, the mixtuie of said electrolytic salts and the positive effect thereof are described US 5,296,3 18 and US 5,429,891 of Bell Communication Research, Inc. describe a solid electrolyte for a rechargeable lithium intercalation battery cell of a self- supporting film of a copolymer of vinylidene fluoride and hexalluoropropylene, the electrolyte thereof being selected from LiPF ή , LiAsF , LiC10 , LiN(CF3S0 2 )2, LiBF 4 , LiCFjSCh and LiSbF fi and the solvent thereof being selected from ethylene carbonate, propylene carbonate, dimethyl carbonate, diethoxyethane, diethyl carbonate, dimethoxyethane, dipropyl carbonate and mixtures thereof The patent, however, describes no mixtures of said electrolytic salts and their performance. G. Pistoia, A Antonini, R. Rosati and D. Zane (Electrochemica Acta 41 2683-9 (1996)) describe cathodes for Li-ion batteries based on electrolyte compositions of either LiPF 6 or LiBF in a mixture of ethylene carbonate and dimethyl carbonate The authors do not describe, however, the salt mixtures of the present invention US 5,370,949 of National Research Council of Canada describes a non-aqueous electrolyte of which the salt is selected from LiAsF r „ LiPF 6 , LiBF 4 , LiC10 , LiBr, L.AICI4, UCF3SO3. KLiC(CF 3 S0 2 ) 3 and LiN(CF3S0 2 ) 2 and mixtures thereof and the solvent thereof being selected from ethylene carbonate, 2-methyl tetrahydrofuran, tetrahydrofuran, dimethoxyethane, diethoxyethane, dimethyl carbonate, diethyl carbonate, methyl acetate, methyl formate, γ-butyrolactone, 1 ,3-dioxolane, sulfolane, acetonitrile, butyronitrile, trimethylphosphate and dimethylformamide and mixtures thereof The patent, however, does no describe the good performance of the specific mixture of lithium hexafluorophosphate and lithium tetrafluoroborate in a mixtui e of ethylene carbonate and dimethyl carbonate. WO 95/34920 of Lexcel Technology Ltd. describes the use of electrolytes of LiBF and/or LiPF fi and/or lithium trifluormethane sulphonimide in a mixture of a linear carbonate and a cyclic ester, where said linear carbonate may be e.g. diethyl carbonate or dimethyl carbonate, and said cyclic ester may be e.g. polypropylene carbonate or ethylene carbonate. The patent, however, does no describe the mixture of lithium hexafluorophosphate and lithium tetrafluoroborate in a mixtui e of ethylene carbonate and dimethyl carbonate according to the present invention and its performance. In a preferred embodiment of the present invention the solvent mixture comprises ethylene carbonate and dimethyl carbonate in a relative molar ratio of from 80:20 to 20:80, more preferably in a relative molar ratio of from 80.20 to 50:50, even more preferably in a relative molar ratio of from 75 :25 to 60 40 In an alternative embodiment of the invention the solvent mixture in addition to ethylene carbonate and dimethyl carbonate comprises one or more of the following solvents: (a) other alicyclic carbonates represented by the following general formula: -C(=0)-0-CR,R 2 -[CR3R 4 ] m -CR 5 R f ,-0-, wherein each of Ri, R 2 , R3, R 4 , R5 and R Λ independently represent hydrogen or Cι-C alkyl groups and m is an integer equal to 1 or 5, preferably propylene carbonate; (b) aliphatic carbonates represented by the general formula R 7 [OC(0)] I) OR s , wherein R 7 and R 8 independently represent Cι-C 4 alkyl groups, and p is an integer equal to 1 or 2, with the proviso that R s represent C 2 -C alkyl groups, when R 7 is methyl, and p = 1 , preferably diethyl caibonate, (c) lactones in the form of cyclic esters represented by the general formula 1 R 12 -[CR I 5 Rι 6 ],-CR 1 3R 14 -0- wherein each of Ro, Rio, R n , Rι 2 , R 13 , Rι , R 1 and R )6 independently represent hydrogen or C 1-2 alkyl groups and r is an integer equal to 0 or 1 , preferably γ-valerolactone or γ-butyrolactone; (d) esters represented by the formula wherein each of Rπ, Ris and R 19 independently represent hydrogen or Cι-C 2 alkyl groups, and t is an integer from 0 to 2, preferably an acetate, more preferably (2-methoxyethyl)-acetate and/or ethyl acetate; (e) glymes represented by the general formula R 2() 0(R 2 ιO) n R 2 2. in which R 2 and R22 independently represent Cι -2 alkyl groups, R 2] is -(CR23R2 CR 25 R 2 f,)- wherein R23, R 24 , R 25 and R 2f , independently each represent hydrogen or C 1 -C4 alkyl groups, and n is an integer from 2 to 6, preferably 3, R () and R 22 preferably being methyl groups, R23, R 4, R25 and R.26 preferably being hydrogen or Cι-C 2 alkyl groups, more preferably hydrogen. In a preferred embodiment of the invention the mixtui e of salts comprises lithium tetrafluoroborate and lithium hexafluorophosphate in a relative molar ratio of from 85 : 15 to 70:30. In a further preferred embodiment of the invention the lithium tetrafluoroborate and lithium hexafluorophosphate are present in a total concentration in the range from 0.01M to 3M, preferably 0. 1M to 2M, more preferably 0.5M to 1.5M. It is further preferred that the electrolyte system comprises a crosslinked or non- crosslinked, preferably non-crosslinked polymer, pieferably a non-crosslinkable polyester, polyurethane, polyether, polyacrylate, polyvinylidene fluoride or polyolefin Said polymer is more preferably selected from polymerised mono-, di- and trifunctional oligomeric acrylates, preferably polyurethane acrylates and polyether acrylates, or from polymerised mono-, di- and trifunctional monomeric acrylates, preferably monofunctional monomeric acrylates, more preferably urethane aciylate Said polymer may be present in an amount corresponding to from 0% to 50% by weight, preferably 2 to 25% by weight relative to the total weight of the electrolyte system In an embodiment of the invention the electrolyte system is confined in a separatoi consisting of a porous structure made from a polymer, preferably polyethylene, polypropylene, polycarbonate, cellulose, glass fiber or any inorganic material Said separator is preferably of a woven or non-woven structure having a pore size in the range of 10 x 10 nm to 1 x 1 mm Further, the separator has a thickness of 10-100μm, preferably 10-25μm The present invention relates also to a method for the preparation of an electrolyte system as defined above comprising the steps of mixing the solvents, dissolving the salts in the solvent mixtuie, optionally adding a thickening agent to the solution, optionally incorporating the mixture obtained in a separator, and optionally adding monomers or oligomers having one or moie polymei isable functional groups and inducing polymerisation of these monomers or oligomers Finally the electrolyte system may be sandwiched between electrode laminates of an electrochemical system like a battery, capacitor or electrochiomic display The invention further relates to the use of the electrolyte system in a battery, which may be any lithium battery in which the negative electrode may consist essentially of graphites, cokes, or any other intercalation compound like oxides of tin, titanium, vanadium, cobalt or manganese, and in which the positive electrode structure may comprise an intercalation compound, preferably of the transitions metal oxide type, more preferably lithium manganese oxide, lithium cobalt oxide or vanadium oxides, even more preferably spinel lithium manganese oxide. In a preferred embodiment of the invention the negative electrode in the battery consists essentially of graphites and cokes, which are able to intercalate lithium and which have an interlayer distance doo 2 of no more than 3 48 Λ The positive effect of the electrolyte compositions of the present invention are especially pronounced when combined with such negative electrode structures of the graphite and coke type. Surprisingly, the effect is mostly pronounced when the electrolyte compositions are combined with the graphite material having the trade name "SFG 15" from TIMCAL G+T (Lonza G+T, CH) or when they are combined with any coke material of an interlayer distance doo 2 in the range 3.42-3.44 A The positive electrode of the battery is preferably based on lithium manganese oxide spinel Alternatively, the electrolyte system may be used in a capacitor or in an electrochromic display. Examples: The invention is further illustrated in the following examples. In these examples the terms "cyclability" and "initial irreversible loss" have the meaning defined above, unless otherwise specified, Further, graphite refers to a synthetic graphite of an interlayer distance do 2 of 3.36 and coke refers to a petroleum coke of an interlayer distance doo 2 of 3.46A, unless otherwise specified. Lithium tetrafluoroborate, lithium hexafluorophosphate, ethylene caibonate, dimethyl carbonate and propylene carbonate all refer to battery grade compounds from Merck, whereas lithium manganese oxide refers to a lithium manganese oxide spinel stmcture of chemical composition LiMn C» 4 . Example 1 : A battery was prepared with an electrolyte composition of 70.30 by mole of ethylene carbonate and dimethyl carbonate and a 75 :25 by mole salt mixture of lithium tetrafluoroborate and hexafluorophosphate of a total salt concentration of I M. The electrolyte was prepared by simple mixing. The battery was prepared by sandwiching said electrolyte system between a negative electrode structure of graphite and a positive electrode structure of lithium manganese oxide. Both of the active electrode materials were mixed with 5% of carbon black for improved electronic conductivity. Upon cycling of the battery it displayed a cyclability of more than 350 cycles In terms of irreversible loss during the initial charging, the cell displayed a loss of 50 mAh/g of anode material. Comparative example l a: For comparison, a battery was prepared with an electrolyte compositions of 70:30 by mole of ethylene caibonate and dimethyl carbonate and a salt mixture of 25 :75 by mole of lithium tetrafluoroborate and hexafluorophosphate of a total salt concentration of I M. The electrolyte was prepared by simple mixing. The battery was assembled by sandwiching said electrolyte system between a negative electrode stmcture of graphite and a positive electrode structure of lithium manganese oxide. Both of these active electrode materials were mixed with 5% of carbon black for improved electronic conductivity. Upon cycling of the battery it displayed a cyclability of 1 0 cycles, displaying an initial irreversible loss of 80 mAh/g of the anode material Comparative example 1 b For furthei companson, another batteiy was pi epaied with an electiolyte compositions of 70 30 by mole of ethylene caibonate and dimethyl caibonate and pui e lithium tetrafluoroborate as electrolyte salt in a concenti ation of I M The electrolyte was piepaied by simple mixing The batteiy was assembled by sandwiching said electi olyte system between a negative electi ode stuictui e of gi aphite and a positn e electi ode structure of lithium manganese oxide Both of these active electi ode materials wei e mixed with 5% of caibon black foi impi oved electronic conductivity Upon cycling of the batteiy it displayed a cyclability of 300 cycles, howevei displaying an initial lπ eversible loss of 100 mAh/g of the anode matenal Comparative example lc For e en further comparison, yet anothei batteiy was pi epai ed applying an electrolyte compositions of 70 30 by mole of ethylene caibonate and dimethyl caibonate and pure lithium hexafluorophosphate as electiolyte salt at a concenti ation of IM The electrolyte was pi epaied by simple mixing The batteiy was assembled by sandwiching said electi olyte system between a negative electi ode stmcture of gi aphite and a positive electrode stmcture of lithium manganese oxide Both of these active electiode matenals wei e mixed with 5% of carbon black foi improved electronic conductivity Upon cycling of the batteiy it displayed a cyclability of only 100 cycles, displaying an initial irrevei sible loss of 50 mAh/g of the anode material Comparative example I d Foi further comparison, another batteiy was pi epai ed applying an electi olyte compositions of 70 30 by mole of ethylene carbonate and pi opylene cai bonate and a 75 25 by mole salt mixture of lithium tetrafluoroborate and hexafluorophosphate of a total salt concentration of IM. The electrolyte was prepared by simple mixing The battery was assembled by sandwiching said electrolyte system between a negative electrode stmcture of graphite and a positive electrode stmcture of lithium manganese oxide. Both of these active electrode materials were mixed with 5% of carbon black for improved electronic conductivity Upon cycling of the battery it displayed a cyclability of only 5 cycles, however, displaying a high initial irreversible loss of more than 500 mAh/g of the anode material. Example 2 A battery was prepared applying an electrolyte compositions of 80:20 by mole of ethylene carbonate and dimethyl carbonate and a salt mixture of 70:30 by mole of lithium tetrafluoroborate and hexafluorophosphate of a total salt concentration of IM. The electrolyte was prepared by simple mixing The battery was assembled by sandwiching said electrolyte system between a negative electrode structure of graphite SFG15 from TIMCAL and a positive electrode structure of lithium manganese oxide Both of these active electrode materials were mixed with 5% of carbon black for improved electronic conductivity. Upon cycling of the battery it displayed a cyclability of more than 350 cycles, displaying a high reversible capacity of 360 mAh/g of the anode and an initial irreversible loss of less than 50 mAh/g of the anode material Example 3 : Another battery was prepared applying an electrolyte compositions of 80.20 by mole of ethylene carbonate and dimethyl carbonate and a salt mixture of 80:20 by mole of lithium tetrafluoroborate and hexafluorophosphate of a total salt concentration of IM. The electrolyte was prepared by simple mixing The battery was assembled by sandwiching said electrolyte system between a negative electrode structure of coke and a positive electrode structure of lithium manganese oxide. Both of these active electrode materials were mixed with 5% of carbon black for improved electronic conductivity. Upon cycling of the battery it displayed a cyclability of more than 300 cycles (in this case the batteiy was cycled between 4.2V and 2.5V), displaying an initial irreversible loss of less than 70 mAli/g of the anode material. Example 4: A battery was prepared applying an electrolyte compositions of 60:30: 10 by mole of ethylene carbonate, dimethyl carbonate and propylene carbonate and a salt mixture of 80:20 by mole of lithium tetrafluoroborate and hexafluorophosphate of a total salt concentration of IM. The electrolyte was prepared by simple mixing. The battery was assembled by sandwiching said electrolyte system between a negative electrode structure of giaphite and a positive electrode structure of lithium manganese oxide. Both of these active electrode materials were mixed with 5% of carbon black for improved electronic conductivity. Upon cycling of the battery it displayed a cyclability of more than 300 cycles, displaying an initial irreversible loss of less than 70 mAli/g of the anode material. Example 5 : A batteiy was prepared applying an electrolyte compositions of 80:20 by mole of ethylene carbonate and dimethyl carbonate and a salt mixture of 80:20 by mole of lithium tetrafluoroborate and hexafluorophosphate of a total salt concentration of IM. The electrolyte was prepared by simple mixing The electrolyte was incorporated in a microporous polyethylene-based separator. The battery was assembled upon sandwiching said electrolyte system between a negative electrode structure of graphite and a positive electrode structure of lithium manganese oxide. Both of these active electrode materials were mixed with 5% of carbon black for improved electronic conductivity. Upon cycling of the batteiy it displayed a cyclability of more than 250 cycles, displaying an initial irreversible loss of less than 50 mAh/g of the anode material.

Claims: Claims 1 An electiolyte system consisting essentially of - a solvent mixture, and - a salt mixture, characteiised in that the solvent mixtuie essentially consists of ethylene carbonate and dimethyl caibonate, that the salt mixture consists of lithium tetiafluoroborate and lithium hexafluoiophosphate, and that the salt mixtuie compiises 60-90% by mole of lithium tetiafluoioboiate and 10-40% by mole of lithium hexafluoi ophosphate 2 An electiolyte system accoiding to claim 1 , in which the solvent mixtui e essentially consists of ethylene caibonate and dimethyl caibonate in a lelative molar ratio of fiom 80 20 to 20 80 more pieferably in a relative molar latio of from 80 20 to 50 50, even moie preferably in a relative molar ratio of from 75 25 to 60 40 3 An electrolyte system accoiding to claim 1 oi 2, in which the solvent mixtuie consists entirely of ethylene caibonate and dimethyl caibonate 4 An electiolyte system according to claim 1 oi 2, whei ein the solvent mixtuie in addition to ethylene carbonate and dimethyl caibonate compiises one oi moie of the following solvents (a) other alicyclic caibonates lepiesented by the following general foimula -C(=0)-0-CRιR 2 -[CR,R4] m -CR 5 R6-0-, whei ein each of R ) ? R 2 , R 3 , R 4 . R s and R < , independently iepiesent hydi ogen 01 Cι-C 4 alkyl gioups and m is an integei equal to 1 01 5, pieferably propylene caibonate, (b) aliphatic carbonates repiesented by the geneial foimula R 7 [OC(0)],,ORs, wherein R 7 and R s independently lepresent Cι-C 4 alkyl groups, and p is an integei equal to 1 oi 2, with the pioviso that R s repiesent C 2 -C 4 alkyl gioups, when R 7 is methyl, and p = 1, preferably diethyl caibonate, (c) lactones in the form of cyclic esteis lepiesented by the general formula -C(=0)-CR9R 1 o-CR n Ri 2 -[CR 15 R K) ] r -CR n R 14 -0- wheiein each of R 9 , Rio, Rπ Rι 2 , Rπ, R H , D and R , independently iepiesent hydiogen oi Ci 2 alkyl gioups and r is an integei equal to 0 oi 1, preferably γ-valerolactone oi γ-butyiolactone, (d) esters repiesented by the formula Rπ[C(0)]ORιs[ORi9]t, wheiein each of Ri7, Ris and R ]9 independently iepiesent hydiogen oi CpC? alkyl gioups, and t is an integei fiom 0 to 2, prefeiably an acetate, moie pieieiabk (2-methoxy- ethyl)-acetate and/oi ethyl acetate, (e) glymes repiesented by the geneial ioimula R 2 O(R 2 |O)„R 2 , in which R 2(l and R 22 independently lepresent Cj 2 alkyl gioups is -(CRιR 2 |CR 2 sR 2 r,)- wheiein R 23 , R 24 , R 2 5 and R 2l , independently each iepiesent hydrogen oi CpCi alkyl groups, and n is an integei from 2 to 6, preferably 3, R 2 o and R22 preferably being methyl gioups, R 23 , R 24 , R. and R 26 piefeiably being hydiogen 01 Cι-C 2 alkyl groups, more piefeiably hydrogen An electrolyte system according to any of the p'eced g claims, in which the mixture of salts comprises lithium tetiafluoroborate and lithium hexafluoiophosphate in a ielative molai ratio of from 8515 to 7030 An electrolyte system accoiding to any of the pieceding claims, in which lithium tetiafluoroboiate and lithium hexafluoiophosphate are piesent in a total concentration in the range from 0.0 I M to 3M, preferably 0.1 M to 2M, more preferably 0.5M to 1 .5M. 7. An electrolyte system according to any of the preceding claims, in which the electrolyte system comprises a crosslinked or non-crosslinked, preferably no - crosslinked, polymer. 8. An electrolyte system according to claim 7. wherein said polymer is a non- crosslinked polymer, preferably a non-crosslinkable polyester, polyurethane, polyether, polyacrylate, polyvinylidene fluoride or polyolefin. 9. An electrolyte system according to ciaim 7 or 8, wherein said polymer is selected from polymerised mono-, di- and trifunctional oligomeric acrylates, preferably polyurethane acrylates and polyether acrylates, or from polymerised mono-, di- and trifunctional monomeric acrylates. preferably monofunctional monomeric acrylates, more preferably urethane acrylate. 10. An electrolyte system according to any of claim 7, 8 or 9, wherein said polymer is present in an amount corresponding to from 0% to 50% by weight, preferably 2 to 25% by weight relative to the total weight of the electrolyte system 1 1. An electrolyte system according to any of the preceding claims, in which the electrolyte system is confined in a separator consisting of a porous structure made from a polymer, preferably polyethylene, polypropylene, polycarbonate, cellulose, glass fiber or any inorganic material. 12. An electrolyte system according to claim 1 1 in λvhich said separator is a woven or non-woven structure having a pore size in the range of 10 x 10 nm to 1 x 1 mm. 13. An electrolyte system according to the claims 1 1 or 12, in which said separator has a thickness of 10-100μm, preferably 10-25μm. 14. A method for the preparation of an electrolyte system according to each of the preceding claims, comprising the steps of: mixing the solvents, dissolving the salts in the solvent mixture, optionally adding a thickening agent to the solution, optionally incorporating the mixture obtained in a separator, and - optionally adding monomers or oligomers having one or more polymerisable functional groups and inducing polymerisation of these monomers or oligomers. 15. A battery comprising a negative electrode, a positive electrode, and an electrolyte system, characterized in that the electrolyte system is an electrolyte system according to any of claims 1 - ! 3. 16. A battery according to claim 1 5, characterised in that the negative electrode consists essentially of graphites, cokes, or any other intercalation compound like oxides of tin, titanium, vanadium, cobalt or manganese. 17 A batteiy according to claim 16, characterised in that the negative electrode consists essentially of graphites and cokes of an interlayer distance doo 2 of not more than 3.48 A. 18. A batteiy according to claim 17, characterised in that the negative electrode consists essentially of one or more graphites. 19 A batteiy according to claim 18, characterized in that the negative electrode consists essentially of the graphite material having the trade name "SFG 1 5" from T1MCAL G+T (Lonza G+T, CFI). A battery according to claim 17, characteiized in that the negative electiode consists essentially of a coke of an inteilayei distance d 0 02 in the range 3 42- 3 44A A batteiy accoiding to the preceding claims 15-20, characterised in that the positive electiode stiucture comprises an inteicalation compound, pieferably of the transitions metal oxide type, moie preferably lithium manganese oxide, lithium cobalt oxide oi vanadium oxides, even more piefeiably spinel lithium manganese oxide A battery accoiding to claims 21 , chai actei ised in that the positive electiode stmcture consists essentially of spinel lithium manganese oxide Use of a non-aqueous electi olyte system according to any of the claims 1 -13 in a battery, capacitoi or in an electiochiomic display

Inventors: RAO NINGLING, YDE-ANDERSEN STEEN, RAO, NINGLING, YDE-ANDERSEN, STEEN
Applicants: DANIONICS AS, RAO NINGLING, YDE ANDERSEN STEEN, DANIONICS A/S, RAO, NINGLING, YDE-ANDERSEN, STEEN
Application year: 1997
Main classification: H01M10
IPC codes: H01M4, H01M6, H01M10