POWDER BLASTING METHOD USING A NON-METAL BLASTING MASK

Abstract: Method of providing a pattern of apertures and/or cavities in a plate of material which is suitable for powder blasting, or of cutting pieces from a plate (2) of such a material by means of powder blasting, using a non-metal layer of blast-resistant material (3) as a mask which is patterned while or after it is fixedly provided on the surface of the plate.

Description: POWDER BLASTING METHOD USING A NON-METAL BLASTING MASK The invention relates to a method of removing material from a part of a plate which is suitable for powder blasting by means of a powder-blasting technique, using a blasting mask. Removing material may be understood to mean, for example, the provision of cavities and/or apertures, but also a process of cutting shapes (for example, discs) by way of powder blasting. The cavities may be, for example, slots, pits or grooves. Plates which are suitable for powder blasting are particularly made of hard, brittle materials such as glass or ceramic material (for example, ferrite, a sintered oxidic ferromagnetic material). The plates may be made of an insulating material (for example, glass), an electrically conducting material (for example, some types of ferrite) or a semiconducting material (for example, silicon and some types of ferrite). These types of plates are particularly used in flat lamps, meander lamps, TL lamps, luminescent gas discharge displays such as plasma displays, field emission displays, cathode ray tube displays and electron duct displays in which electrons are propagated in ducts having walls of insulating material in which the apertures and/or cavities are used for manipulating electron currents. They may be formed, for example, as control plates provided with addressable electrodes, as transport plates in which parallel cavities constitute ducts, and as spacer plates which may be placed, for example, between a control plate and a luminescent screen in a luminescent display. A metal blasting mask is generally used in this method. The pattern to be blasted is defined in this blasting mask. Such a method is known from US Patent .... (serial number 08/359377; PHN 14.698). The use of a metal blasting mask has the drawback that it is expensive, while it can generally be used only once. Another drawback is the deformation of the metal due to the force of the abrasive powder particles. Consequently, the blasting mask may get detached during blasting, resulting in underblasting. It is an object of the invention to provide a preferably low-cost method having a smaller risk of underblasting than the known method. To this end, the method according to the invention is characterized in that a non-metal blasting mask is fixedly formed on the plate, whereafter the plate is provided with a pattern by means of powder blasting. The use of a non-metal mask material (preferably synthetic material) prevents the mask from being permanently deformed due to the mechanical forces of the abrasive powder particles and thus from being locally detached in such a way that underblasting occurs. By providing the mask directly on the plate and patterning it during or after its provision, it is achieved that the mask cannot be deformed before it is provided, so that there are no large tensions in the mask so that it is better held in position, thus inhibiting underblasting. In accordance with an embodiment, for example, a blasting mask is provided on the plate by means of a printing method. This printing method may be silk screening. This embodiment has the advantage that no blast-resistant material is lost when manufacturing the blasting mask. Blast-resistant material is printed exactly at those locations where it is necessary. In accordance with another embodiment, a blasting mask is formed by providing a layer of a blast-resistant material on the plate and by providing this plate with a desired pattern of apertures. In a further embodiment, the blast-resistant material is a photosensitive material in which the desired pattern is provided by means of exposure and development. The blast-resistant material of which the layer is manufactured may comprise, for example a polyurethane as a basic constituent. These materials have the advantage that they are elastic and consequently highly blast-resistant. Moreover, it is possible to give them photosensitive properties. To realize the photosensitivity, acrylic groups may be added to the polyurethane. The material is then referred to as polyurethane- acrylate. This embodiment has the advantage that the pattern in the blasting mask has a high accuracy due to the use of lithography (exposure). A blast-resistant layer may be a coating obtained from a liquid substance which is provided on the plate. It has the advantage that it is inexpensive and also practical because the thickness of the blast-resistant layer can be varied, dependent on its use. However, the layer may alternatively be a solid coating which can be rolled out or a layer which is present in a laminate provided on the plate. A laminate has a layered structure. It usually consists of an undeveloped photosensitive layer having a given thickness, provided between two temporary cover foils (which are removed upon use). Extra layers may be provided to improve the adhesion. A more specific embodiment of the method according to the invention comprises the steps of providing a photosensitive, blast-resistant layer; - exposing the layer with the desired pattern; developing the layer; producing at least one jet of abrasive powder particles; directing the jet onto the surface of the mask formed by the patterned layer, which mask is present on the plate to be processed; - performing a relative movement between the jet and the plate with the patterned mask, and removing the blast-resistant layer after the blasting process. The way in which the layer is developed is dependent on the material used. This may be done, for example in soap water or in a basic liquid. The way in which the layer is removed after the blasting process is also dependent on the material used. There are materials in which the exposed parts are removable. Then, the layer can be removed by total exposure after the process. There are also materials in which the exposed parts are fixed and the unexposed parts are removable. Then, the layer can be removed, for example, by firing after the blasting process. In accordance with another embodiment, the plate is provided with a blast-resistant resist for forming the blasting mask, in which a desired pattern is made by means of plasma etching, using a preformed etching mask (for example, of metal). This embodiment has the advantage that the resist does not need to be photosensitive and may thus be inexpensive. In accordance with a further embodiment, the blast-resistant material is a resist, a resin or a foil which foil is patterned by means of a laser. The foil is stuck onto the plate by means of an adhesive layer. This embodiment has the advantage that it is inexpensive because the blast-resistant material does not need to be photosensitive. The blast- resistant material may be patterned through a mask but it is alternatively possible to do this without a mask. In that case, the blast-resistant material is directly inscribed by means of the laser. This has a cost-saving advantage because an extra mask is not required. As compared with, for example, chemical etching, the use of a powder- blasting process for providing a plate with apertures and/or cavities has the advantage that a large number of parameters can be varied, inter alia, the type of abrasive powder, the grain size, the diameter of the nozzle blasting the powder particles, the distance between the nozzle and the plate, the pressure of the medium with which the powder particles are transported, the movement of the nozzle, and the speed of the relative movement between the nozzle and the plate. By varying these factors, it has been found possible to provide plates with a pattern of cavities and/or apertures meeting the requirements imposed on their use in displays. As compared with chemical etching, powder blasting has the advantage of being a more rapid, environmentally better and anisotropic process. The invention may be particularly used to advantage for blasting cavities in the cell plate or duct plate of a plasma display (PDP). Since a blasting mask is used which is not made of metal, it is possible to blast "hard", without the risk of deformation of the blasting mask and underblasting. It is thus possible to blast directly in a (glass) plate. In the manufacture of PDPs, a (glass) frit layer was usually provided on the plate. The advantage of direct blasting in a glass plate is that the upper side of the partitions between the cells or ducts is and remains flat. (In fact, it is a part of the surface of a (flat) plate.) This is necessary to be able to provide a cover plate in close relationship with the cell plate or duct plate. When using the invention, the upper side thus does not need to be flattened separately, so that a complicated process, as hitherto used in PDPs, in which, inter alia, the cells or ducts must be filled with wax, can be precluded. The invention may be used to great advantage for manufacturing the ducts in a duct plate for, for example an AC plasma display and a PALC (plasma-addressed liquid crystal) display. Since the blasting mask is formed by a layer which is patterned when it has already been provided on the plate, there is not a preformed mask having long unsupported wires which can easily move with respect to each other, as is the case with a metal mask. Thus, it is prevented that the blasting mask is already deformed before blasting takes place. The invention may also be used to advantage when manufacturing duct plates for use in flat lamps, for example meander lamps. These lamps have a duct in which a gas discharge is ignited. The use of a mask according to the invention provides the possibility of manufacturing any desired configuration of the ducts. It is, for example, very well possible to manufacture a spiral duct. If a metal mask were used, deformation problems would arise, just as with the ducts of an AC plasma display. The invention may further be used to advantage when pieces (for example, round discs) must be cut from a plate. When a premanufactured mask is used, this mask comprises a plurality of separate pieces which must first be, for example, punched, milled or sawn. These pieces are then laid on the substrate in a satisfactory distribution on the surface and stuck to the substrate. When an adhesive layer to be patterned is provided, any desired shape can be provided by means of, for example lithography. Positioning may be effected with precision and the pieces remain stuck due to the adhesive properties of the layer or due to an adhesive material which is provided between the layer and the substrate. If a plate has to be processed on both sides, the two sides of the plate, which have first been provided with a photosensitive layer, are exposed simultaneously in an embodiment of the method according to the invention. The processing time will be shorter because the two sides of the plate are processed simultaneously. To provide the possibility for, for example, transparent plates to be processed at two sides simultaneously, a coating which is opaque to the light used is first applied on one side of the plate. When UV light is used for the exposure, a UV-blocking coating comprising, for example, Fe(NO 3 ).9H 2 O may be used. The coating may be formed by immersing the plate in a solution of Fe(NO 3 ).9H 2 O. These and other aspects of the invention are apparent from and will be elucidated with reference to the embodiments described hereinafter. In the drawings: Fig. 1 shows an example of a method of providing a liquid coating on a plate, Fig. 2 is a cross-section of an example of a laminate, Fig. 3 shows diagrammatically a duct for a flat meander lamp, Fig. 4 shows diagrammatically a duct for a flat lamp having a spiral shape, Fig. 5 shows diagrammatically a duct for a flat lamp having the shape of an angular spiral, Fig. 6 is a diagrammatic spatial, elevational view of a duct plate for an AC plasma display or a PALC display, Fig. 7 is a diagrammatic spatial, elevational view of a cell plate for a DC plasma display, Fig. 8 is a diagrammatic cross-section of an example of a duct of an AC plasma display, and Fig. 9 shows diagrammatically a plate with pieces cut from this plate. Fig. 1 shows how a liquid coating material (3) can be provided on a plate (2). The liquid material preferably has a high viscosity. It may be increased by fixing the material, for example, by causing it to gel. In this example, a cover foil (4) is provided simultaneously with the coating material (3) on the plate (2) by rolling it out with a doctor blade (5). In the Figure, the arrow shows the direction of movement of the doctor blade. When larger surfaces are used, it is difficult to work with a doctor blade. For large plates, a machine may be used, having an adjustable gutter for providing the liquid coating material. Subsequently, a roller may be used for providing the cover foil and regulating the thickness of the coating. The cover foil serves as an oxygen barrier during exposure. Such a barrier is required because oxygen functions as an inhibitor during polymerization. The cover foil also serves as a protection of the mask which is placed on it, and lastly, it is used to achieve a homogeneous layer thickness. This is necessary for a satisfactory exposure and a uniform development. A larger layer thickness requires a longer development time of the material. The reference numeral (1) denotes a bottom foil. A plate (2) of glass is used in the following example, but it may alternatively be made of a different (brittle) material which is suitable for powder blasting. The process may comprise the steps of pretreating the glass plate (2) so as to achieve a good adhesion. This may be realized by immersing it into a solution of 3- methacryloxypropyltrimethoxysilane; - drying the glass plate (2), for example, at 60°C for 5 minutes; positioning a bottom foil (1) (for example, a 25 micrometer thick PET foil) which is slightly larger than the glass plate (2) on a flat base; placing the glass plate (2) on the bottom foil (1); simultaneously providing the coating material (3) (photosensitive in this case) (of, for example a 100 micrometer thick polyurethane) and a cover foil (4) (of, for example a 25 micrometer thick PET foil) by means of a doctor blade. The angle of application should be chosen to be such that air bubbles do not occur underneath the layer; positioning a mask on the cover foil (4) when patterning must take place; - placing the assembly in an exposure machine; exposing the assembly; removing the assembly from the machine; removing the cover foil (4). Frequently, portions of the unexposed parts of the coating material (3) are thereby also removed; the rest of the unexposed parts of the coating material (3) is removed by * passing the glass plate (1) provided with the coating material (3) across soft brushes in soap water, or brushing the plate with soft brushes; * spraying, by means of a high-pressure spray gun, soap water of, for example, 30 °C on the glass plate (2) provided with the coating material (3). (By means of this method, the unexposed parts of the coating material (3) are extra-satisfactorily removed and there is little damage.) exposing the glass plate (2) with the coating material (3) for a second time so as to cure, while excluding oxygen. (This exclusion of oxygen may be realized, for example, by immersing the plate in water.) drying the glass plate (2) with the coating material (3) at, for example 30°C, after curing; powder blasting the side of the glass plate (2) on which the coating material (3) is provided, and - removing the coating material (3), after powder blasting, by placing the glass plate (2) with the coating material (3), for example, in a ventilated oven at 450°C for 30 minutes. Fig. 2 shows an example of the composition of a laminate (6). The laminate (6) shown comprises the following layers from bottom to top: - a base (7) of polyester or steel; an adhesive and anti-halation layer (8); a photosensitive resin layer (9); a slip coat (10), and a cover film (11) of polyester. The base (7), which is also referred to as the bottom foil, may be, for example, a 100 micrometer thick PET foil, and the cover film (11), also referred to as top foil, may be a 40 micrometer thick PET foil. To provide a laminate (6) without air bubbles underneath, a soft rubber roller may be used. An embodiment of the method of removing material from a plate, using a laminate (6) for providing a mask comprises the steps of - removing the base (7); rolling out the rest of the laminate (6) on a hot plate (of, for example 70 °C); removing the cover film while the plate is still hot; exposing the plate (for example, with UV) in the same way as for the liquid coating; removing the unexposed parts by spraying water (of, for example 30 °C) on it by means of a high-pressure spray gun. Sodium carbonate (Na 2 CO 3 ) is dissolved in the water; immersing the plate in a bath containing acetic acid; - rinsing the plate with water; patting the plate with a dry cloth; drying the plate (for example, at 50°C for 30 minutes); powder blasting the side of the plate on which the mask is provided, and removing the rest of the mask by washing the plate in hot water (of, for example 40°C). Figs. 3, 4 and 5 show a number of possible duct shapes for a flat lamp. This may be, for example a TL lamp for a flat display such as an LCD. A flat lamp comprises two plates of, for example glass. Each of the two plates accommodates an open duct, such that the ducts are mirror images of each other and communicate with each other when the plates are placed one on top of the other and thus constitute a closed duct. In another embodiment, one plate comprises an open duct and the other plate does not. The other plate then serves as a cover plate to close the duct. A metal mask for manufacturing the duct shapes shown would easily be deformed during blasting. Such a mask could easily get detached during manufacture of the spiral shapes. The use of a mask to be patterned on the plate avoids this problem. Moreover, the ducts can be shaped more accurately because a lithography process is used. Since the ducts can be shaped more accurately and since the mask is patterned on the substrate with a satisfactory adhesion, it is possible to apply a small pitch. This means that a large tube length can be obtained on a relatively small surface. Fig. 6 is a spatial, elevational view of a duct plate, for example an AC plasma display or a PALC display. The duct plate is formed from one piece, such that it comprises a bottom (15) and walls (16). Fig. 7 is a spatial, elevational view of a cell plate for, for example, a DC plasma display. The cell plate is formed from one piece, such that it comprises a bottom (17) and walls (18). Fig. 8 is a cross-section of an example of an AC plasma display duct. Walls (20) are present on a bottom (19). Phosphorus (21) is provided between the walls (20). In this example, an MgO layer (22), a dielectric layer (23) and a front glass plate (24) are present above the walls (20). Display electrodes (25) made of a transparent material are present below the front glass plate (24). An addressing electrode (26) is present below the phosphorus. In this Figure, the cover plate is lifted from the duct plate. Fig. 9 shows diagrammatically a plate (26) and some pieces (27) removed from this plate. These pieces may be removed, for example, by providing a plate with a coating material and patterning this plate, for example, in such a way that it is open at the position of the outer edge of the desired pieces, whereafter the pieces are detached from the rest of the plate by means of powder blasting the plate with the patterned coating material. In summary, the invention relates to a method of providing a pattern of apertures and/or cavities in a plate (2) of material which is suitable for powder blasting, or of cutting pieces from a plate of such a material by means of powder blasting, using a non- metal layer of blast-resistant material (3) as a mask which is patterned while or after it is fixedly provided on the surface of the plate.

Claims: CLAIMS: I. A method of removing material from a part of a plate which is suitable for powder blasting by means of a powder-blasting technique, using a blasting mask, characterized in that a non-metal blasting mask is fixedly formed on the plate, whereafter the plate is provided with a pattern by means of powder blasting. 2. A method as claimed in Claim 1, characterized in that the mask is provided on the plate by means of a printing method. 3. A method as claimed in Claim 1, characterized in that a layer of a blast- resistant material is provided on the plate which is provided with a desired pattern of apertures constituting a blasting mask, whereafter the pattern is provided in the plate by means of powder blasting. 4. A method as claimed in Claim 3, characterized in that the layer of blast- resistant material is patterned by means of plasma etching. 5. A method as claimed in Claim 3, characterized in that the layer of blast- resistant material is patterned by means of a laser beam. 6. A method as claimed in Claim 3, characterized in that the blast-resistant material is provided in a liquid form on the insulating plate, and is dried, patterned and cured, thus constituting a blasting mask. 7. A method as claimed in Claim 1 or 6, characterized in that the blast- resistant material is photosensitive and is patterned by means of exposure and development. 8. A method as claimed in Claim 1, 2, 3, 4, 5, 6 or 7, characterized in that the blast-resistant material comprises polyurethane as a basic constituent. 9. A method as claimed in Claim 1, 2, 3, 4, 5, 6, 7 or 8, characterized in that ducts are provided in the plate. 10. A method as claimed in Claim 1, 2, 3, 4, 5, 6, 7 or 8, characterized in that cells are provided in the plate. II. A method as claimed in Claim 1, 2, 3, 4, 5, 6, 7 or 8, characterized in that pieces are cut from the plate by means of powder blasting. 12. A method as claimed in Claim 6, characterized in that the plate is exposed simultaneously on two sides, one side being provided with an opaque layer before providing the coating. AMENDED CLAIMS [received by the International Bureau on 20 March 1998 (20.03.98) ; original claim 1 amended ; remaining cl aims unchanged (2 pages) ] 1. A method of removing material from a part of a plate which is suitable for powder blasting by means of a powder-blasting technique, using a blasting mask, characterized in that the plate constitutes a plate of or for a plasma display (PDP) or an AC plasma display or a PALC (plasma-addressed liquid crystal) display and in that a non-metal blasting mask is fixedly formed on the plate, whereafter the plate is provided with a pattern by means of powder blasting. 2. A method as claimed in Claim 1, characterized in that the mask is provided on the plate by means of a printing method. 3. A method as claimed in Claim 1, characterized in that a layer of a blast- resistant material is provided on the plate which is provided with a desired pattern of apertures constituting a blasting mask, whereafter the pattern is provided in the plate by means of powder blasting. 4. A method as claimed in Claim 3, characterized in that the layer of blast- resistant material is patterned by means of plasma etching. 5. A method as claimed in Claim 3, characterized in that the layer of blast- resistant material is patterned by means of a laser beam. 6. A method as claimed in Claim 3, characterized in that the blast-resistant material is provided in a liquid form on the insulating plate, and is dried, patterned and cured, thus constituting a blasting mask. 7. A method as claimed in Claim 1 or 6, characterized in that the blast-resistant material is photosensitive and is patterned by means of exposure and development. 8. A method as claimed in Claim 1, 2, 3, 4, 5, 6 or 7, characterized in that the blast-resistant material comprises polyurethane as a basic constituent. 9. A method as claimed in Claim 1, 2, 3, 4, 5, 6, 7 or 8, characterized in that ducts are provided in the plate. 10. A method as claimed in Claim 1, 2, 3, 4, 5, 6, 7 or 8, characterized in that cells are provided in the plate. 11. A method as claimed in Claim 1, 2, 3, 4, 5, 6, 7 or 8, characterized in that pieces are cut from the plate by means of powder blasting. 12. A method as claimed in Claim 6, characterized in that the plate is exposed simultaneously on two sides, one side being provided with an opaque layer before providing the coating.

Inventors: BOSMAN JOSEPH CORNELIS MARIE, DE HAAS FRANCISCUS CUPERTINUS, LIGHTHART HENRICUS JOZEF, TOLNER HARM, BOSMAN, JOSEPH, CORNELIS, MARIE, DE HAAS, FRANCISCUS, CUPERTINUS, MARIA, LIGHTHART, HENRICUS, JOZEF, TOLNER, HARM
Applicants: PHILIPS ELECTRONICS NV, PHILIPS NORDEN AB, PHILIPS ELECTRONICS N.V.
Application year: 1997
Main classification: B24C1
IPC codes: B24C1, B41C1, B41M3, G03F7, H01J9, H01J11