Use of benzotriazolyl-alkylene bisphenol compounds as antioxidants for organic materials

Abstract: The use of a benzotriazolyl-alkylene bisphenol compound represented by formula: wherein R 5 and R 6 may be the same or different and each represents and alkyl group with 1-8 carbon atoms, as an antioxidant for an organic material.

Description: The present invention relates to the use of specific benzotriazolyl-alkylene bisphenol compounds which function as both light stabilizing agents and antioxidants, to a process for their preparation, and to organic materials stabilized by those compounds. 2-hydroxyphenylbenzotriazole compounds are known for instance from CS 157.761 B as light stabilizers for synthetic resins and the like, but because these compounds are of lower molecular weight than the compounds of the invention to be described hereunder, and thus undergo volatilization during working of resins and with the passage of time, they have not been able to stabilize organic materials for extended periods. Also, antioxidants consisting mainly of alkyl-substituted phenols, represented by 2,6-di-tert.-butyl-p-cresol, as well, have been unable to provide long-term stabilization of organic materials for the same reason. According to the present invention there is provided the use of benzotriazolyl-alkylene bisphenol compound represented by the following general formula (4): wherein R 5 and R 6 may be the same or different and each represents an alkyl group with 1-8 carbon atoms, as an antioxidant for organic material. These benzotriazolyl-alkylene bisphenol compounds are Useful as light stabilizers and antioxidants for organic materials such as resins, fibers, rubber, waxes, paints, fats and oils, cosmetics, inks, heat-sensitive materials, pressure-sensitive materials, light-sensitive materials and the like. A compound for use in the invention is generally to be used in an amount of 0.01-10 wt%, and preferably 0.05-2 wt%, with respect to the organic material. For laminated materials, it may be used at a high concentration of 2-10 wt% in only the uppermost layer. Examples of suitable organic materials include, but are not limited to, homopolymers of olefin and diolefin, such as polyethylene, polypropylene, 1-polybutene, poly-4-methylpentene-1 and 1,2-polybutadiene; copolymers of olefins or olefins and other monomers, such as ethylene-propylene copolymer, ethylene-butene copolymer, ethylene-hexene copolymer, ethylene-4-methylpentene-1 copolymer, ethylene-octene-1 copolymer, ethylene-vinyl acetate copolymer, ethylene-vinylsilane copolymer, ethylene-ethyl acrylate copolymer, ethylene-acrylic acid copolymer, ethylene-carbon dioxide copolymer, ethylene-vinyl acetate-glycidyl methacrylate terpolymer and ionomers; polymers of styrene and substituted styrene, such as polystyrene, poly-p-methylstyrene and poly-α-methylstyrene; copolymers of styrene and other monomers, such as styrene-methacrylic acid ester copolymer, styrene-acrylonitrile copolymer, styrene-butadiene copolymer, styrene-maleic anhydride copolymer, methacrylic acid ester-butadiene-styrene terpolymer, acrylic acid ester-butadiene-styrene terpolymer, acrylic acid ester-acrylonitrile-styrene terpolymer and acrylonitrile-butadiene-styrene terpolymer; modified polyethylenes such as maleic anhydride-modified polyethylene; halogenated resins, such as polyvinyl chloride, polyvinyl bromide, polyvinyl fluoride, polyvinylidene chloride, chlorinated polyethylene, chlorinated polypropylene, polyvinylidene fluoride, polyvinyl fluoride, chlorinated rubber, vinyl chloride-vinyl acetate copolymer, vinyl chloride-ethylene copolymer, polyfunctional acrylic monomer-vinyl chloride copolymer, (ethylene-vinyl acetate)-vinyl chloride copolymer, acrylonitrile-vinyl chloride copolymer, vinyl chloride-vinylidene chloride copolymer and vinyl chloride-urethane copolymer; polyvinyl acetate; polyvinyl alcohol; polyvinyl butyral; polyvinyl stearate; polyvinyl benzoate; polyvinyl maleate; linear thermoplastic polyesters produced by condensation polymerization of dicarboxylic acids and diols, such as polyethylene terephthalate, polybutylene terephthalate and copolymers including combinations of two or more of terephthalic acid, isophthalic acid, 1,4-butanediol, polyethylene glycol, etc.; straight chain polyesters or polyether esters, such as polytetramethylene ether glycol terephthalate; polyphenylene oxide; polyamides produced by polycondensation of diamines and dicarboxylic acids, polycondensation of aminocarboxylic acids and lactam ring opening polymerization; polycarbonates; polyacetals; polysulfones; polyether sulfones; polyether ketones; polyurethanes obtained by reaction of polyisocyanate compounds with polyols; methacrylic resins; polyacrylonitrile; petroleum resins; coumarone resins; fibrous resins; resins obtained by addition condensation of formaldehyde with various phenols, such as phenolic resins, cresol resins, xylenol resins, p-t-butylphenol resins, p-phenylphenol resins and resorcinol resins; urea resins and melamine resins; epoxy resins; unsaturated polyester resins obtained by polycondensation reaction of polyhydric alcohols with unsaturated polybasic acids containing reactive double bonds; silicone resins; natural polymers, such as cellulose, cellulose acetate, cellulose propionate, cellulose butyrate, methylcellulose and gelatin; natural rubber; synthetic isoprene rubber; ethylene-propylene rubber; butyl rubber; chloroprene rubber; polysulfide rubber; acrylic rubber; urethane rubber; chlorosulfonated polyethylene; epichlorohydrin rubber; ethylene-acrylic rubber; ethylene-ethyl acetate elastomer; isobutylene rubber; butadiene rubber; acrylonitrile-butadiene rubber; styrene-butadiene rubber, and other polymeric substances and their blends, natural fats and oils, synthetic ester oils, mineral oils, and the like. The compounds for use in the invention may be combined with organic materials by commonly employed processes The organic materials which are stabilized by the compounds used in the invention may also contain, as desired, commonly used additives, particularly antioxidants, light stabilizers and mixtures thereof. Examples of such additives include antioxidants such as phenol-based, amine-based, sulfur-based and phosphorous-based antioxidants, and light stabilizers such as salicylic acid-based, benzophenone-based, benzotriazole-based, cyanoacrylate-based, acrylonitrile-based, metal complex nickel-based, cobalt-based and hindered amine-based light stabilizers. Other additives which may be used include plasticizers, metal inactivators, lubricants, emulsifying agents, fillers, foaming agents, colorants, fluorescent sensitizers, flame retardants and antistatic agents. The present invention will now be further illustrated by way of examples, with the understanding that the invention is in no way limited by these examples. All of the products in the following synthesis examples were subjected to purification, but such purification is not necessarily required in practice. Example 1 Synthesis of 6-(2-benzotriazolyl)-4-tert.-octyl-6'-tert.-butyl-4'-methyl-2,2'-methylene bisphenol A mixture of 32.3 g of 2-benzotriazolyl-4-tert.-octyl phenol, 16.4 g of 2-tert.-butyl-4-methyl phenol, 18.1 g of dibutylamine, 0.7 g of sodium hydroxide, 3.9 g of paraformaldehyde, 39 g of n-butanol and 150 g of 1,2,4-trimethylbenzene was heated to gradually raise the temperature, and the reaction was carried out for 10 hours at 160-170°C while recovering the water generated by the reaction together with the n-butanol. The reaction solution was washed with acidic water, and then with water. Next, 46 g of the crude product (92% yield) obtained by recovering the 1,2,4-trimethylbenzene under reduced pressure was recrystallized with isopropyl alcohol to give a purified white powder with a melting point of 148°C. The purity of the purified product was 100% as analyzed by liquid chromatography. The results of C, H, N and O elemental analysis of the purified product were close to calculated values as shown in the following table, thus confirming production of the object compound. Element Calculated (%) Found (%) Carbon 76.9 76.9 Hydrogen 8.3 8.4 Nitrogen 8.4 8.5 Oxygen 6.4 6.2 Example 2 Synthesis of 6-(2-benzotriazolyl)-4-tert.-octyl-6'-tert.-butyl-4'-methyl-2,2'-methylene bisphenol A mixture of 32.3 g of 2-benzotriazolyl-4-tert.octyl phenol, 16.4 g of 2-tert.-butyl-4-methyl phenol, 8.5 g of monoethanolamine, 2.8 g of sodium hydroxide, 3.9 g of paraformaldehyde and 104 g of n-butanol was heated to gradually raise the temperature, and the reaction was carried out for one hour at 180-190°C while recovering the water generated by the reaction together with the n-butanol. After adding 104 g of toluene to the reaction solution to dissolve the reaction product, the toluene layer was washed with acidic water and then with water. Next, 47 g of the crude product (94% yield) obtained by recovering the toluene under reduced pressure was recrystallized with isopropyl alcohol to give a purified white powder with a melting point of 148°C. The purity of the purified product was 100% as analyzed by liquid chromatography. The results of C, H, N and O elemental analysis of the purified product were close to calculated values as shown in the following table, thus confirming production of the object compound. Element Calculated (%) Found (%) Carbon 76.9 76.8 Hydrogen 8.3 8.2 Nitrogen 8.4 8.6 Oxygen 6.4 6.4 Example 3 Synthesis of 6-(2-benzotriazolyl)-4-tert.-octyl-4',6'-di-tert.-butyl-2,2'-methylene bisphenol The same procedure was carried out as in Example 1, except that the 16.4 g of 2-tert.-butyl-4-methyl phenol was replaced with 20.6 g of 2,4-di-tert.-butyl phenol. A 50 g portion of the resulting crude product (92% yield) was recrystallized with isopropyl alcohol to give a purified white powder with a melting point of 137°C The purity of the purified product was 100% as analyzed by liquid chromatography. The results of C, H, N and O elemental analysis of the purified product were close to calculated values as shown in the following table, thus confirming production of the object compound. Element Calculated (%) Found (%) Carbon 77.6 77.7 Hydrogen 8.7 8.8 Nitrogen 7.8 7.8 Oxygen 5.9 5.7 Example 4 Synthesis of 6-(2-benzotriazolyl)-4-tert.-octyl-4',6'-di-tert.-butyl-2,2'-methylene bisphenol The same procedure was carried out as in Example 2, except that the 16.4 g of 2-tert.-butyl-4-methyl phenol and 8.5 g of monoethanolamine were replaced with 20.6 g of 2,4-di-tert.-butyl phenol and 42.5 g of diethanolamine, respectively. A 51 g portion of the resulting crude product (94% yield) was recrystallized with isopropyl alcohol to give a purified white powder with a melting point of 137°C. The purity of the purified product was 100% as analyzed by liquid chromatography. The results of C, H, N and O elemental analysis of the purified product were close to calculated values as shown in the following table, thus confirming production of the object compound. Element Calculated (%) Found (%) Carbon 77.6 77.7 Hydrogen 8.7 8.6 Nitrogen 7.8 7.8 Oxygen 5.9 5.9 Example 5 Synthesis of 6-(2-benzotriazolyl)-4-tert.-octyl-4',6'-di-tert.-amyl-2,2'-methylene bisphenol The same procedure was carried out as in Example 1, except that the 16.4 g of 2-tert.-butyl-4-methyl phenol was replaced with 23.4 g of 2,4-di-tert.-amyl phenol. A 52 g portion of the resulting crude product (91% yield) was recrystallized with isopropyl alcohol to give a purified white powder with a melting point of 80°C. The purity of the purified product was 100% as analyzed by liquid chromatography. The results of C, H, N and O elemental analysis of the purified product were close to calculated values as shown in the following table, thus confirming production of the object compound. Element Calculated (%) Found (%) Carbon 78.0 78.0 Hydrogen 9.0 8.8 Nitrogen 7.4 7.6 Oxygen 5.6 5.6 Example 6 Synthesis of 6-(2-benzotriazolyl)-4-tert.-octyl-4',6'-di-tert.-amyl-2,2'-methylene bisphenol The same procedure was carried out as in Example 2, except that the 16.4 g of 2-tert.-butyl-4-methyl phenol was replaced with 23.4 g of 2,4-di-tert.-amyl phenol. A 53 g portion of the resulting crude product (93% yield) was recrystallized with isopropyl alcohol to give a purified white powder with a melting point of 80°C. The purity of the purified product was 100% as analyzed by liquid chromatography The results of C, H, N and O elemental analysis of the purified product were close to calculated values as shown in the following table, thus confirming production of the object compound. Element Calculated (%) Found (%) Carbon 78.0 77.9 Hydrogen 9.0 9.1 Nitrogen 7.4 7.4 Oxygen 5.6 5.6 Example 7 Synthesis of 6-(2-benzotriazolyl)-4-tert.-octyl-4',6'-di-tert.-octyl-2,2'-methylene bisphenol The same procedure was carried out as in Example 1, except that the 16.4 g of 2-tert.-butyl-4-methyl phenol was replaced with 31.9 g of 2,4-di-tert.-octyl phenol. A 59 g portion of the resulting crude product (90% yield) was recrystallized with isopropyl alcohol to give a purified white powder with a melting point of 174°C. The purity of the purified product was 100% as analyzed by liquid chromatography. The results of C, H, N and O elemental analysis of the purified product were close to calculated values as shown in the following table, thus confirming production of the object compound. Element Calculated (%) Found (%) Carbon 79.0 78.9 Hydrogen 9.7 9.8 Nitrogen 6.4 6.5 Oxygen 4.9 4.8 Example 8 Synthesis of 6-(2-benzotriazolyl)-4-tert.-octyl-4',6'-di-tert.-octyl-2,2'-methylene bisphenol The same procedure was carried out as in Example 2, except that the 16.4 g of 2-tert.-butyl-4-methyl phenol was replaced with 31.9 g of 2,4-di-tert.-octyl phenol. A 60 g portion of the resulting crude product (92% yield) was recrystallized with isopropyl alcohol to give a purified white powder with a melting point of 174°C. The purity of the purified product was 100% as analyzed by liquid chromatography. The results of C, H, N and O elemental analysis of the purified product were close to calculated values as shown in the following table, thus confirming production of the object compound. Element Calculated (%) Found (%) Carbon 79.0 79.0 Hydrogen 9.7 9.5 Nitrogen 6.4 6.5 Oxygen 4.9 5.0 Table 1 below provides a list of the comparison compounds and the coompounds for use in the invention (compounds Nos. 5,6, 7 and 8) used in the following examples. Compound name Comparison compound 2-benzotriazolyl-4-methyl phenol Comparison compound 1 6-(2-benzotriazolyl)-4-t-butyl-6'-t-butyl-4'-methyl-2,2'-methylene bisphenol Comparison compound 2 6-(2-benzotriazolyl)-4-t-butyl-4',6'-di-t-butyl-2,2'-methylene bisphenol Comparison compound 3 6-(2-benzotriazolyl)-4-t-butyl-4',6'-di-t-amyl-2,2'-methylene bisphenol Comparison compound 4 6-(2-benzotriazolyl)-4-t-butyl-4',6'-di-t-octyl-2,2'-methylene bisphenol Invention compound 5 6-(2-benzotriazolyl)-4-t-octyl-6'-t-butyl-4'-methyl-2,2'-methylene bisphenol Invention compound 6 6-(2-benzotriazolyl)-4-t-octyl-4',6'-di-t-butyl-2,2'-methylene bisphenol Invention compound 7 6-(2-benzotriazolyl)-4-t-octyl-4',6'-di-t-amyl-2,2'-methylene bisphenol Invention compound 8 6-(2-benzotriazolyl)-4-t-octyl-4',6'-di-t-octyl-2,2'-methylene bisphenol Comparison compound 9 6-(2-benzotriazolyl)-4-methyl-6'-t-butyl-4'-methyl-2,2'-methylene bisphenol Comparison compound 10 6-(2-benzotriazolyl)-4-methyl-4',6'-di-t-butyl-2,2'-methylene bisphenol Comparison compound 11 6-(2-benzotriazolyl)-4-methyl-4',6'-di-t-amyl-2,2'-methylene bisphenol Comparison compound 12 6-(2-benzotriazolyl)-4-methyl-4',6'-di-t-octyl-2,2'-methylene bisphenol Example 9 The weight reductions of the compounds after heating at 250°C for 40 minutes were measured with a differential thermogravimetric apparatus in order to determine their resistance to volatilization. The solubilities of the compounds in 100 g of xylene at 25°C were also determined as an index of their compatibility with organic materials. The results are shown in Table 2 below. Reduction (%) Solubility (g/100 g xylene, 25°C) Comparison compound 100 7 Comparison compound 1 9 18 Comparison compound 2 10 2 Comparison compound 3 8 8 Comparison compound 4 6 5 Invention compound 5 8 29 Invention compound 6 7 35 Invention compound 7 7 29 Invention compound 8 5 14 Comparison compound 9 12 12 Comparison compound 10 15 20 Comparison compound 11 10 61 Comparison compound 12 10 13 Example 10 In order to determine the light stabilizing effects of the compounds, different non-stabilized resins containing no light stabilizers were used to prepare pressed sheets of 150 mm length x 70 mm width x 0.5 mm thickness with the compositions listed in Table 3 below, and the sheets were tested using a Sunshine carbon-arc lamp weathering tester (product of Suga Experimental Instruments, KK.). For the polycarbonate of Example 10 -4 , the test was made using the super accelerated weathering tester: Eye Super UV Tester (product of Dainihon Plastics, KK.). The results are given in Table 4 below. Example 10-1 Example 10-2 Example 10-3 Example 10-4 Polypropylene 100 wt pts -- -- -- Polyvinyl chloride -- 100 wt pts -- -- Polystyrene -- -- 100 wt pts -- Polycarbonate -- -- -- 100 wt pts Stabilizer 0.2 wt pt 0.3 wt pt 0.2 wt pt 10 wt pts Evaluation: x (discoloration), Δ (slight discoloration), ○ (very slight discoloration), o ○ (no discoloration) Stabilizer Example 10-1 Testing time: 500 hrs Example 10-2 Testing time: 800 hrs Example 10-3 Testing time: 500 hrs Example 10-4 Testing time: 100 hrs Comparison compound x x x x Comparison compound 1 ○ ○ ○ ○ Comparison compound 2 ○ ○ ○ ○ Comparison compound 3 ○ ○ ○ ○ Comparison compound 4 ○ ○ ○ ○ Invention compound 5 o ○ o ○ o ○ o ○ Invention compound 6 o ○ o ○ o ○ o ○ Invention compound 7 o ○ o ○ o ○ o ○ Invention compound 8 o ○ o ○ o ○ o ○ Comparison compound 9 ○ ○ ○ Δ Comparison compound 10 ○ ○ ○ Δ Comparison compound 11 ○ ○ ○ Δ Comparison compound 12 ○ ○ ○ Δ Example 11 In order to determine the light stabilizing effects of the compounds, non-stabilized chloroprene containing no light stabilizer was used to prepare the sample solution specified below which was applied three times, as a resin, onto a microscope glass slide (76 x 26 mm) to a dry weight of 90 g/m 2 . After the application, the slide was air-dried for 2 days in a dark area at room temperature to make a test piece. The test piece was subjected to a sunlight weather resistance for 3 days. The results are given in Table 5. To determine the antioxidizing effect, a test piece prepared in the same manner using non-stabilized chloroprene containing no antioxidant was subjected to a heat resistance test by heating at 130°C for 10 hours using a gear aging tester (product of Toyo Precision Instruments, KK.). The results are given in Table 6. Sample Solution Non-stabilized chloroprene 10 pts. by wt. Toluene 57 pts. by wt. Stabilizer 0.2 pt. by wt. Evaluation: x (discoloration), Δ (slight discoloration), ○ (very slight discoloration), o ○ (no discoloration) Stabilizer Weather resistance Comparison compound x Comparison compound 1 ○ Comparison compound 2 ○ Comparison compound 3 ○ Comparison compound 4 ○ Invention compound 5 o ○ Invention compound 6 o ○ Invention compound 7 o ○ Invention compound 8 o ○ Comparison compound 9 ○ Comparison compound 10 Δ Comparison compound 11 Δ Comparison compound 12 Δ Stabilizer Testing time 0.5 hr 1 hr 10 hrs None coloration browning browning 2,6-di-t-butyl-p-cresol slight coloration browning browning Comparison compound 1 no coloration no coloration no coloration Comparison compound 2 no coloration no coloration slight coloration Comparison compound 3 no coloration no coloration slight coloration Comparison compound 4 no coloration no coloration slight coloration Invention compound 5 no coloration no coloration no coloration Invention compound 6 no coloration no coloration slight coloration Invention compound 7 no coloration no coloration slight coloration Invention compound 8 no coloration no coloration slight coloration Comparison compound 9 no coloration no coloration no coloration Comparison compound 10 no coloration no coloration slight coloration Comparison compound 11 no coloration no coloration slight coloration Comparison compound 12 no coloration no coloration slight coloration Table 2 shows that the compounds for use in the invention have excellent resistance to volatilization and high lipophilicity, Tables 4 and 5 show that they provide a considerable light stabilizing effect, and Table 6 shows that they have better antioxidizing actions than the commonly used antioxidant 2,6-di-tert.-butyl-p-cresol; the compounds for use in the invention, therefore, can vary effectively stabilize organic materials.

Claims: The use of a benzotriazolyl-alkylene bisphenol compound represented by formula (4) : wherein R 5 and R 6 may be the same or different and each represents an alkyl group with 1-8 carbon atoms, as an antioxidant for an organic material.

Inventors: AOKI HIDEO, ISHIHARA KAZUYUKI, KANAGAWA EISUKE, YAMAUCHI TOSHIYUKI, AOKI, HIDEO, ISHIHARA, KAZUYUKI, KANAGAWA, EISUKE, YAMAUCHI, TOSHIYUKI
Applicants: JOHOKU CHEMICAL CO LTD, JOHOKU CHEMICAL CO., LTD.
Application year: 1997
Main classification: C09K15
IPC codes: C07D249, C08K5