CEMENTED CARBIDE BODY WITH INCREASED WEAR RESISTANCE

Abstract: The present invention relates to a cemented carbide body comprising WC with an average grain size of < 10 mu m in a binder phase. In the cemented carbide body the WC grains can be classified in at least two groups in which a group of smaller grains has a maximum grain size amax and a group of larger grains has a minimum grain size bmin and each group contains at least 10 % of the total amount of WC grains. According to the invention bmin-amax > 0.5 mu m and the difference in grain size within each group is > 1 mu m.

Description: Cemented carbide body with increased wear resistance The present invention relates to coated cemented carbide bodies particularly useful in tools for turning, milling and drilling of steels and stainless steels. Cemented carbide bodies are manufactured according to powder metallurgical methods including milling, pressing and sintering. The milling operation is an intensive mechanical milling in mills of different sizes and with the aid of milling bodies. The milling time is of the order of several hours up to days. Such processing is believed to be necessary in order to obtain a uniform distribution of the binder phase in the milled mixture, but it results in a wide WC grain size distribution. In US 5,505,902 and US 5,529,804 methods of making cemented carbide are disclosed according to which the milling is essentially excluded. Instead in order to obtain a uniform distribution of the binder phase in the powder mixture the hard constituent grains are precoated with the binder phase, the mixture is further wet mixed with pressing agent dried, pressed and sintered. In the first mentioned patent the coating is made by a SOL-GEL method and in the second a polyol is used. EP-A-665 308 discloses a coated cutting insert with a bimodal distribution of WC grain size with WC grains in two groups 0.1-1 μ and 3-10 μ . The insert according to this application is produced with conventional milling technique resulting in a broadening of the WC grain size distribution. It has now surprisingly been found that a further improvement of the properties of a cemented carbide according to EP-A-665 308 can be obtained if such a material is made using the technique disclosed in the above mentioned US 5,505,902 or US 5,529,804. The present invention relates generally to a cemented carbide body comprising WC with an average grain size of <10 μm in a binder phase. The WC grains are classified in at least two groups in which a group of smaller grains has a maximum grain size a max and a group of larger grains has a minimum grain size ^-^ . Each group contains at least 10 % of the total amount of WC grains . The cemented carbide body according to the invention is characterized in that trni-.-a j n^.-, >0.5 μm and that the variation in grain size within each group is > 1 μm. More particularly the invention relates to a coated cutting insert with a bi odal distribution of the WC grains particularly useful for machining of steels and stainless steels comprising WC and 4-20 wt-% Co, preferably 5-12.5 wt-% Co and 0-30 wt-% cubic carbide, preferably 0-15 wt-% cubic carbide, most preferably 0-10 wt-% cubic carbide such as TiC, TaC, NbC or mixtures thereof. The WC grains have a narrow bimodal grain size distribu- tion with grain sizes in the ranges 0-1.5 μm and 2.5-6.0 μm respectively and with a weight ratio of fine WC particles (0-1.5 μm) to coarse WC particles (2.5-6.0 μm) in the range of 0.25-4.0, preferably 0.5-2.0. The amount of W dissolved in the binder phase is controlled by adjustment of the carbon content by small additions of carbon black or pure tungsten powder. The W-content in the binder phase can be expressed as the "CW-ratio" defined as CW-ratio = M s / (wt%Co * 0.0161) where M s is the measured saturation magnetization of the sintered cemented carbide body in kA/m and wt% Co is the weight percentage of Co in the cemented carbide. The CW- value in inserts according to the invention shall be 0.82-1.0, preferably 0.86-0.96. The sintered inserts according to the invention are used coated or uncoated, preferably coated with MTCVD, conventional CVD or PVD with or without AI2O3. In particular, multilayer coatings comprising TiC x N v O z with columnar grains followed by a layer of CC-AI2O3 , K-AI2O3 or a mixture of α- and K-AI2O3 , have shown good results. In another preferred embodiment the coating described above is completed with a TiN-layer which can be brushed or used without brushing. According to the method of the present invention a cemented carbide body is made comprising wet mixing without milling of at least two different WC-powders with deagglomerated powders of other carbides generally TiC, TaC and/or NbC, binder metal and pressing agent, dried preferably by spray drying, pressed to inserts and sintered. The grains of the WC-powder are classified in at least two groups in which a group of smaller grains has a maximum grain size a max and a group of larger grains has a minimum grain size brnin each group containing at least 10 % of the total amount of WC grains wherein min- j r,^ >0.5 μm and the variation in grain size within each group is >1 μm. Preferably, prior to mixing the WC grains are carefully deagglomerated before and after being coated with binder metal. Particularly according to the method of the present invention WC-powders with two narrow grain size distributions of 0-1.5 μm and 2.5-6.0 μm respectively and a weight ratio of fine WC particles (0-1.5 μm) to coarse WC particles (2.5-6.0 μm) in the range of 0.25- 4.0, preferably 0.5-2.0 are wet mixed without milling with other carbides generally TiC, TaC and/or NbC, binder metal and pressing agent, dried preferably by spray drying, pressed to inserts and sintered. It is essential according to the invention that the mixing takes place without milling i.e. there should be no change in grain size or grain size distribution as a result of the mixing. In a preferred embodiment the hard constituents, at least those with narrow grain size distributions, are after careful deagglomeration coated with binder metal using methods disclosed in US 5,505,902 or US 5,529,804. In such case the cemented carbide powder according to the invention consists preferably of Co-coated WC + Co- binder, with or without additions of the cubic carbides such as TiC, TaC, NbC, (Ti,W)C, (Ta,Nb)C, (Ti,Ta,Nb)C, (W,Ta,Nb)C, and (W, Ti , Ta,Nb)C coated or uncoated, preferably uncoated, possibly with further additions of Co- powder in order to obtain the desired final composition. Example 1 A. Cemented carbide tool inserts of the type SEMN 1204 AZ, an insert for milling, with the composition in addition to WC 8.4 wt% Co, 1.13 wt% TaC and 0.38 wt% NbC were produced according to the invention. Cobalt coated WC, WC-6 wt-% Co, prepared in accordance with US 5,505,902 was carefully deagglomerated in a laboratory jetmill equipment, mixed with additional amounts of Co and deagglomerated uncoated (Ta,Nb)C and TaC powders to obtain the desired material composition. The coated WC- particles consisted of 50 wt% with an average grain size of 3.5 μm and 50 wt% with 1.2 μ average grain size, giving a bimodal grain size distribution. The mixing was carried out in an ethanol and water solution (0.25 1 fluid per kg cemented carbide powder) for 2 hours in a laboratory mixer and the batch size was 10 kg. Furthermore, 2 weight-% lubricant, was added to the slurry. The carbon content was adjusted with carbon black to a binder phase alloyed with W corresponding to a CW-ratio of 0.89. After spray drying, the inserts were pressed and sintered according to standard practise and dense structures with no porosity were obtained. Before coating a negative chamfer with an angle of 20 degrees was ground around the whole insert. The inserts were coated with a 0.5 μm equiaxed TiCN- layer (with a high nitrogen content corresponding to an estimated C/N-ratio of 0.05) followed by a 4 μm thick TiCN- layer with columnar grains by using the MTCVD- echnique (temperature 885-850 °C and CH3CN as the carbon and nitrogen source) . In subsequent steps during the same coating cycle, a 1.0 μ thick layer of AI2O3 was deposited using a temperature 970 C and a concentration of H2S dopant of 0.4 % as disclosed in EP-A-52.3 021. A thin (0.3 μ ) layer of TiN was deposited on top accor- ding to known CVD-technique . XRD-measurement showed that the Al2θ3-layer consisted of 100 % K-phase. The coated inserts were brushed by a nylon straw brush containing Sic grains. Examination of the brushed inserts in a light microscope showed that the thin TiN- layer had been brushed away only along the cutting edge leaving there a smooth Al2θ3~layer surface. Coating thickness measurements on cross sectioned brushed samples showed no reduction of the coating along the edge line except for the outer TiN-layer that was remove . B. Cemented carbide tool inserts of the type SEMN 1204 AZ , an insert for milling, with the composition 9.1 wt% Co, 1.23 wt% TaC and 0.30 wt% NbC and the rest WC with unimodal distribution and an average grain size of 1.2 μm were produced in the following way. Cobalt coated WC, WC-6 weight-% Co, prepared in accordance with US 5,505,902 was carefully deagglomerated in a laboratory jet ill equipment, mixed with additional amounts of Co and deagglomerated uncoated (Ta,Nb)C and TaC powders to obtain the desired material composition. The mixing was carried out in an ethanol and water solution (0.25 1 fluid per kg cemented carbide powder) for 2 hours in a laboratory mixer and the batch size was 10 kg. Furthermore, 2 weight-% lubricant, was added to the slurry. The carbon content was adjusted with carbon black to a binder phase highly alloyed with W corresponding to a CW-ratio of 0.89. After spray drying, the inserts were pressed and sintered according to standard practise and dense structures with no porosity were obtained. Before coating a negative chamfer with an angle of 20 degrees was ground around the whole of each insert. The inserts were coated in the same coating batch as the inserts A above. The coated inserts were brushed by a nylon straw brush containing SiC grains. Examination of the brushed inserts in a light microscope showed that the thin TiN- layer had been brushed away only along the cutting edge leaving there a smooth AI2O3 -layer surface. Coating thickness measurements on cross sectioned brushed samples showed no reduction of the coating along the edge line except for the outer TiN-layer that was removed . C. Cemented carbide tool inserts of the type SEMN 1204 AZ with the same chemical composition, average grain size of WC, CW-ratio, chamfering, CVD-coating and brushing respectively as the insert B above but produced from powder manufactured with conventional ball milling techniques were used as reference for comparison with the test specimens according to above. Inserts from A, B and C were compared in a wet milling test in a rather highly alloyed steel (HB= 310) . Two parallel bars each of a thickness of 35 mm were centrally positioned relative the cutter body (diameter 100 mm ) , and the bars were placed with an air gap of 10 mm between them. The cutting data were: Speed= 150 /min Feed= 0.40 mm/rev Cutting depth 2 mm, single tooth milling with coolant. Evaluated tool life expressed as cutting length of variant A according to the invention was 8200 mm and for variant B 6900 mm and finally for the standard variant C only 6100 mm. In this test the insert according to the invention with a bimodal WC grain size distribution, variant A, obtained the best result. Example 2 A. Inserts from the same batch as insert A in Example 1 above and B. Inserts from the same batch as insert B in Example 1 above and C. Inserts from the same batch as insert C in Example 1 above were compared in a wet milling test in a low alloyed steel (SS 1650, HB = 180 ). Two parallel bars each of a thickness 30 mm were centrally positioned relative the cutter body (diameter 100 mm) . The bars were placed with an air gap of 10 mm between them. The cutting data were: Speed= 285 m/min Feed= 0.38 mm/rev Cutting depth 2 mm, single tooth milling with coolant . Evaluated tool life expressed as cutting length of variant A according to the invention was 4800 mm and for variant B, 4200 mm and finally for the standard variant C only 3600 mm. In this test the insert according to the invention with a bimodal WC grain size distribution, variant A, performed best.

Claims: Claims 1. A cemented carbide body comprising WC with an average grain size of <10 μm in a binder phase the WC grains being classified in at least two groups in which a group of smaller grains has a maximum grain size a max and a group of larger grains has a minimum grain size b j nin each group containing at least 10 % of the total amount of WC grains c h a r a c t e r i s e d in that kmin -a max >0-5 μm and that the variation in grain size within each group is >1 μm. 2. A cemented carbide body according to the preceding claim c h a r a c t e r i s e d in a composition comprising WC and 4-20 wt-% Co, preferably 5-12.5 wt-% Co and <30 wt-%, preferably <15 wt-% cubic carbide such as TiC, TaC, NbC or mixtures or solid solutions thereof including WC . 3. A cemented carbide body according to any of the preceding claim c h a r a c t e r i s e d in the WC grains being classified in two groups with a weight ratio of fine WC particles (0-1.5 μm) to coarse WC particles (2.5-6.0 μm) in the range of 0.25-4.0, preferably 0.5-2.0. 4. A cemented carbide body according to claim 3 c h a r a c t e r i s e d in that said two groups include the grain size ranges 0-1.5 μm and 2.5-6.0 μm. 5. A cemented carbide body according to any of the preceding claims c h a r a c t e r i s e d in that said body is a cutting tool insert. 6. A cemented carbide body according to claim 5 c h a r a c t e r i s e d in that said insert is provided with a thin wear resistant coating. 7. A cemented carbide body according to claim 6 c h a r a c t e r i s e d in that said coating comprises TiC x N v O z with columnar grains followed by a layer of α- AI2O3, K-AI2O3 or a mixture of α- and K-AI2O3. 8. A cemented carbide body according to claim 7 c h a r a c t e r i s e d in that the W-content in the binder phase expressed as the "CW-ratio" defined as CW-ratio = M s / (wt%Co * 0.0161) where M s is the measured saturation magnetization of the sintered cemented carbide body in kA/m and wt% Co is the weight percentage of Co in the cemented carbide is 0.82- 1.0, preferably 0.86-0.96. . Method of making a cemented carbide body comprising wet mixing without milling of at least two different WC-powders with deagglomerated powders of other carbides generally TiC, TaC and/ or NbC, binder metal and pressing agent, dried preferably by spray drying, pressed to inserts and sintered c h a r a c t e r i s e d in the grains of the WC-powder being classified in at least two groups in which a group of smaller grains has a maximum grain size a max and a group of larger grains has a minimum grain size b m i n each group containing at least 10 % of the total amount of WC grains wherein b m i n -a max >0.5 μm and the variation in grain size within each group is >1 μ . 10. Method according to the preceding claim c h a r a c t e r i s e d in that prior to mixing the WC grains are carefully deagglomerated before and after being coated with binder metal.

Inventors: ALM OVE, OESTLUND AAKE, WALDENSTROEM MATS, ALM, OVE, OESTLUND, AAKE, WALDENSTROEM, MATS
Applicants: ALM OVE, OESTLUND AAKE, SANDVIK AB, WALDENSTROEM MATS, ALM, OVE, OESTLUND, AAKE, SANDVIK AB (PUBL), WALDENSTROEM, MATS
Application year: 1997
Main classification: C22C29
IPC codes: B22F1, B23B27, B23P15, C22C1, C22C29, C23C30