Liquid crystal composition and liquid crystal display element

Abstract: A liquid crystal composition having excellent voltage-transmittance characteristic (high steepness) suitable for colorization and low viscosity and high Δn suitable for a high speed response is provided, which comprises a first component comprising a compound of formula (I-a), a second component comprising a compound of formula (II) and a third component comprising a compound of formula (III-a). wherein R 1 , R 2 , R 3 and R 4 are alkyl groups; n is an integer of 0 to 20; A is 1,4-phenylene group; Z 0 is -COO- or -CH 2 CH 2 -, Z 1 is -CH 2 CH 2 -, -COO- or a single bond; Q 1 is hydrogen or fluorine atom; B 1 is 1,4-cyclohexylene, 1,4-phenylene or 1,3-dioxane-2,5-diyl; B 2 and B 3 are 1,4-cyclohexylene or 1,4-phenylene group; and, p, q and m are 0 or 1.

Description: This invention relates to a nematic liquid crystal composition comprising at least one chiral additive and a liquid crystal display element provided in a closed cell formed by two substrates containing transparent electrodes, and in particular a liquid crystal composition useful for super twisted birefringent nematic (STN) system and a liquid crystal display element using the liquid crystal composition. Background of the invention There have been proposed various display systems for liquid crystal display (LCD) such as twisted nematic system, super twisted birefringent nematic system (STN) and active matrix system (AM-LCD) and practically applied. Among them, super twisted birefringent nematic systems (STN) proposed by T. J. Scheffer et al., (Appl. Phy. Lett., 45(10), 1021 (1984)) wherein the orientation of the liquid crystal molecules in the upper and lower substrates is twisted by 180 to 270° have been used as LCD for personal computers, word processors and the like. There is a need for further improvement of various properties of the systems. The following properties are required for a liquid crystal composition used for the STN liquid crystal display element. (1) high steepness of voltage-transmittance characteristic in order to obtain high contrast of the liquid crystal display element; (2) high phase transition temperature (clearing point) of nematic-isotropy phase in order to lower the coloring due to the temperature dependency of refractive anisotropy (Δn); (3) low viscosity (η) in order to make a response time as shorter as possible; and (4) thin cell thickness (d) in order to make a response time as shorter as possible since the response time is proportional to the cell thickness, and thus, large refractive anisotropy (Δn). Among them, the improvement of the above properties (1) and (4) have recently become more important because of high desire for colorization and animation. Although, various liquid crystal compositions have been proposed, there is still a need for liquid crystal compositions having improved properties. Summary of the invention An object of the present invention is to provide a liquid crystal composition having various properties required for the STN display systems, in particular, a liquid crystal composition having excellent voltage-transmittance characteristic (high steepness) suitable for colorization and a liquid crystal composition having low viscosity and high Δn suitable for a high speed response. The inventors of the present invention have studied various liquid crystal compositions using various liquid crystal compounds to achieve the object and found that the object can be attained by the use of the liquid crystal composition of the present invention, in particular, in the STN display element. The present invention provides a liquid crystal composition which comprises a first component comprising at least one compound selected from the group consisting of compounds of formulas (I-a) to (I-f), a second component comprising at least one compound of formula (II) and a third component comprising at least one compound selected from the group consisting of compounds of formulas (III-a) to (III-c). wherein R 1 is an alkyl group having 1 to 10 carbon atoms; one or two or more methylene groups (-CH 2 -) which are not vicinal in the alkyl group may be substituted by oxygen atom (-O-) and/or -CH=CH-; and n is an integer of 0 to 20; R 2 and R 3 are independently alkyl groups having 1 to 10 carbon atoms; one or two or more methylene groups (-CH 2 -) which are not vicinal in the alkyl groups may be substituted by oxygen atom (-O-) and/or -CH=CH-; and A is 1,4-phenylene group whose hydrogen atom (s) in the lateral position may be substituted by fluorine atom(s); R 4 is an alkyl group having 1 to 10 carbon atoms; one or two or more methylene groups (-CH 2 -) which are not vicinal in the alkyl group may be substituted by oxygen atom (-O-) and/or -CH=CH-; Z 0 is -COO- or -CH 2 CH 2 -, Z 1 is -CH 2 CH 2 -, -COO- or a single bond; Q 1 is hydrogen or fluorine atom; B 1 is 1,4-cyclohexylene, 1,4-phenylene or 1,3-dioxane-2,5-diyl; B 2 and B 3 are independently 1,4-cyclohexylene or 1,4-phenylene group whose hydrogen atom(s) in the lateral position may be substituted by fluorine atom(s); p, q and m are independently 0 or 1. Preferably, the first component is comprised in the amount of 3 to 60% by weight, the second component in the amount of 3 to 30% by weight and the third component in the amount of 5 to 70% by weight, based on the total weight of the composition of the present invention. Further the present invention provides a liquid crystal composition which further comprises a fourth component comprising at least one compound selected from the group consisting of compounds of formulas (IV), (V), (VI-a) and (VI-b): R 5 - (B 4 ) - Z 2 - (C 1 ) - R 6 wherein R 5 and R 6 are independently alkyl groups having 1 to 10 carbon atoms; one or two or more methylene groups (-CH 2 -) which are not vicinal in the alkyl groups may be substituted by oxygen atom (-O-) and/or -CH=CH-; B 4 is 1,4- cyclohexylene, pyrimidine-2,5-diyl or 1,4-phenylene group; C 1 is 1,4-cyclohexylene or 1,4-phenylene group; Z 2 is -C ≡ C-, -COO-, -CH 2 CH 2 -, -CH=CH-, -CF=CF- or a single bond; R 7 - (D) - Z 3 - (E) - Z 4 - (G) - R 8 wherein R 7 is an alkyl group having 1 to 10 carbon atoms; one or two or more methylene groups (-CH 2 -) which are not vicinal in the alkyl group may be substituted by oxygen atom (-O-) and/or -CH=CH-; R 8 is an alkyl, alkoxy or alkoxymethyl group having 1 to 10 carbon atoms; D is 1,4-cyclohexylene or pyrimidine-2,5-diyl group; E is 1,4-cyclohexylene or 1,4-phenylene group whose hydrogen atom(s) in the lateral position may be substituted by fluorine atom(s); G is 1,4-cyclohexylene or 1,4-phenylene group; Z 3 is -CH 2 CH 2 - or a single bond; Z 4 is -C≡C-, -COO-, -CH=CH- or a single bond; wherein R 9 is an alkyl group having 1 to 10 carbon atoms; one or two or more methylene groups (-CH 2 -) which are not vicinal in the alkyl group may be substituted by oxygen atom (-O-) and/or -CH=CH-; R 10 is an alkyl, alkoxy or alkoxymethyl group having 1 to 10 carbon atoms; and Q 2 is hydrogen or fluorine atom. Preferably, the fourth component is comprised in the amount of 0 to 60% by weight based on the total weight of the composition of the present invention. Moreover, the present invention provides a liquid crystal composition which further comprises a fifth component comprising at least one compound selected from the group consisting of compounds of formulas (VII) and (VIII). wherein R 11 is an alkyl group having 1 to 10 carbon atoms; Q 3 is hydrogen or fluorine atom; k is 0 or 1; R 12 is an alkyl group having 1 to 10 carbon atoms; J is 1, 4-cyclohexylene or 1,4-phenylene group; Q 4 and Q 5 are independently hydrogen or fluorine atom; Z 5 and Z 6 are independently -COO- or single bond; and h is 0, 1 or 2. Preferably, the fifth component is comprised in the amount of 0 to 50% by weight based on the total weight of the composition of the present invention. Furthermore, the present invention provides a liquid crystal display element wherein the crystal composition of any one of those mentioned above is used. Preferred embodiment of the invention The liquid crystal compound which constitutes the liquid crystal composition of the present invention will be described below. Preferred examples of the compounds of the formulas (I-a) to (I-f) are shown below. R in the formulas represents an alkyl group. These compounds are disclosed in JP-A-1-175947, JP-A-1-308239 (EP 325796 B), and JP-A-2-184642 (EP 377469 B1). The dicyclic compounds have weak positive dielectric anisotropy and small refractive anisotropy (Δn) and they are used mainly for lowering viscosity and improving steepness. The tricyclic compounds have weak positive dielectric anisotropy and they are used mainly for broadening the nematic phase range or lowering viscosity and improving steepness. Preferred examples of the compounds of the formula (II) which are the second component of the present invention are shown below. R and R' in the formulas independently represent an alkyl group. These compounds have weak positive dielectric anisotropy and refractive anisotropy (Δn) of about 0.40 to 0.44 and they are used mainly for increasing Δn or lowering viscosity and broadening the nematic phase range. Preferred examples of the compounds of the formulas (III-a), (III-b) and (III-c) which are the third component of the present invention are shown below. R and R' in the formulas independently represent an alkyl group. One or two or more methylene groups (-CH 2 -) which are not vicinal in the alkyl group may be substituted by -CH=CH-. Among them, particularly preferred are those represented by the formulas (III-a-1), (III-a-3), (III-a-6), (III-a-7), (III-b-1), (III-b-3), (III-b-5), (III-c-1), (III-c-4), (III-c-5), (III-c-6), (III-c-7), (III-c-10) or (III-c-11). These compounds for the third component have positive and large dielectric anisotropy and they are used mainly for decreasing threshold voltage and improving steepness which is important STN property. Preferred examples of the compounds of the formulas (IV), (V), (VI-a) and (VI-b) which are the fourth component of the present invention are shown below. R nd R' in the formulas independently represent an alkyl group. One or two or more methylene groups (-CH 2 -) which are not vicinal in the alkyl group may be substituted by -CH=CH-. Among them, particularly preferred examples of those of the formula (IV) are those represented by the formulas (IV-1), (IV-2), (IV-4), (IV-5), (IV-6), (IV-7), (IV-8), (IV-13), (IV-14), (IV-18), (IV-19) or (IV-20). Particularly preferred examples of those of the formula (V) are those represented by the formulas (V-1), (V-2), (V-5), (V-9), (V-11), (V-12), (V-14) or (V-15). The compounds of (IV), (V), (VI-a) and (VI-b).have negative or weak positive dielectric anisotropy. The compounds of the formula (IV) are mainly used for lowering viscosity and/or adjusting Δn . The compounds of the formula (V) are mainly used for broadening the nematic phase range such as increasing clearing point and/or adjusting Δn and viscosity. Since the compounds of the formulas (VI-a) and (VI-b) have very high clearing point, they are used for broadening the nematic phase range such as increasing clearing point and/or adjusting Δn. Preferred examples of the formulas (VII) and (VIII) are shown below. R in the formulas is an alkyl group. Particularly preferred examples of the compounds of the formula (VII) include those of the formulas (VII-1), (VII-2) or (VII-3). Particularly preferred examples of the compounds of the formula (VIII) include those of the formulas (VIII-1), (VIII-5), (VIII-6), (VIII-7), (VIII-8), (VIII-9), (VIII-10), (VIII-11), (VIII-12), (VIII-13), (VIII-14), (VIII-15), (VIII-16) or (VIII-18). The compounds of the formulas (VII) to (VIII) have positive dielectric anisotropy and used for lowering threshold voltage and improving temperature dependency. They are also used for adjusting viscosity and Δn and broadening the nematic phase range such as increasing clearing point. In the liquid crystal composition of the present invention, the amount of the first component is preferably 3 to 60% by weight, more preferably 5 to 55% by weight based on the total weight of the composition. If the amount is less than 3% by weight, it becomes difficult to obtain desired steepness and high speed response, while if it exceeds 60% by weight, threshold voltage of the liquid crystal composition becomes undesirably high. The amount of the second component is preferably 3 to 30% by weight, more preferably 3 to 25% by weight based on the total weight of the composition. If the amount is less than 3% by weight, it becomes difficult to obtain desired steepness, high speed response and high Δn, while if it exceeds 30% by weight, threshold voltage of the liquid crystal composition becomes undesirably high. The amount of the third component is preferably 5 to 70% by weight, more preferably 5 to 65% by weight based on the total weight of the composition. If the amount is less than 5% by weight, threshold voltage of the liquid crystal composition becomes undesirably high, while if it exceeds 70% by weight, viscosity of the liquid crystal composition becomes undesirably high. The amount of the fourth component is 0 to 60% by weight, more preferably 0 to 50% by weight based on the total weight of the composition. If the amount exceeds 60% by weight, threshold voltage of the liquid crystal composition becomes undesirably high. The amount of the fifth component is 0 to 50% by weight, more preferably 0 to 40% by weight based on the total weight of the composition. The liquid crystal composition of the present invention can be prepared by conventional methods. Generally, they may be prepared by dissolving various components at an elevated temperature. Further, the liquid crystal composition of the present invention may be improved and optimized by the addition of an additive suitable for an intended purpose. Such additives are well known in the art and described in detail in literature. Typically, a chiral dopant is added to induce spiral structure of the liquid crystal so as to adjust a desired degree of twist and to restrain reverse twist. The liquid crystal composition of the present invention can be used as that for guest-host (GH) mode if a dichroic dye such as merocyanine, styryl, azo, azomethine, azoxy, quinophthalone, anthraquinone and tetrazine dyes is added thereto. Further, the composition of the present invention can be used as a liquid crystal composition for polymer dispersed type liquid crystal display element represented by NCAP (Nematic Curvilinear Aligned Phases) which is obtained by microencapsulating nematic liquid crystal and polymer network liquid crystal display element (PNLCD) which is obtained by forming a three dimensional polymer network in liquid crystal. In addition, the composition of the present invention can also be used as a liquid crystal composition for birefringent control (ECB) mode and dynamic scattering (DS) mode. Examples The present invention will be explained below with reference to the following examples to which the present invention is not limited. All the composition ratios are expressed by % by weight or parts by weight. Compounds in Examples and Comparative Examples are expressed according to the way of expression as indicated in Table 1. As for 240° STN cell evaluation, cell thickness (d) is selected so that the product Δn · d of the cell thickness (d) and refractive anisotropy (Δn) is about 0.85, and a chiral compound is added to the liquid crystal composition so that a ratio d/p of the cell thickness (d) to a pitch (p) of the liquid crystal composition is about 0.5 before introducing into the cell. Cell evaluation is conducted in yellow mode to measure voltage-transmittance property (V-T property) using 70 Hz square wave. Steepness V 10 /V 90 is a ratio of a voltage (V 10 ) at transmittance of 10% to a voltage (V 90 ) at transmittance of 90%. The chiral compound used in the following examples is represented by the following formula but the present invention is not limited to the use of the compound. Comparative Example 1 The following composition described in Use Example 8 of JP-A 1-175947 was prepared. 3-HH-VFF 15.0% 3-HB-C 20.4% 5-HB-C 30.6% 7-HB-C 21.2% 5-HBB-C 12.8% The liquid crystal composition had clearing point: T NI = 67.6 (°C), viscosity at 20°C: η 20 = 20.2(mPa·s), refractive anisotropy at 25°C: Δn = 0.123, dielectric anisotropy at 20°C: Δε = 9.6, and threshold voltage at 20°C: Vth = 1.74(V). The chiral compound (CM-33)(0.80 parts by weight) was added to 100 parts by weight of the liquid crystal composition. The composition thus obtained was introduced into 240° STN cell of 6.9 µm in thickness and the cell was evaluated in yellow mode. Voltage-transmittance characteristic (V-T characteristic) was measured using 70 Hz square wave. A voltage (V 90 ) at transmittance of 90% and a voltage (V 10 ) at transmittance of 10% were 1.95 (V) and 2.50 (V), respectively, and steepness V 10 /V 90 was 1.282. Comparative Example 2 The following composition described in JP-A 6-316541 as liquid crystal composition (a) was prepared. 5-BTB(F)TB-5 10.0% 2-BEB-C 12.0% 4-BEB-C 12.0% 3-HEB-O2 6.6% 3-HEB-O4 17.4% 4-HEB-O1 13.5% 4-HEB-O2 13.6% 5-HEB-O1 14.9% The liquid crystal composition had clearing point: T NI = 69.1 (°C), viscosity at 20°C: η 20 = 33.4(mPa·s), refractive anisotropy at 25°C: Δn = 0.134, dielectric anisotropy at 20°C: Δε = 6.2, and threshold voltage at 20°C: Vth =1.65(V). The chiral compound (CM-33)(0.85 parts by weight) was added to 100 parts by weight of the liquid crystal composition. The composition thus obtained was introduced into 240° STN cell of 6.3 µm in thickness and the cell was evaluated in yellow mode. Voltage-transmittance characteristic (V-T characteristic) was measured using 70 Hz square wave. A voltage (V 90 ) at transmittance of 90% and a voltage (V 10 ) at transmittance of 10% were 1.85 (V) and 2.41 (V), respectively, and steepness V 10 /V 90 was 1.303. Example 1 3-HH-VFF 14.0% 5-HH-VFF 4.0% 1-BHH-VFF 8.0% 5-BTB(F)TB-3 4.0% 5-BTB(F)TB-4 4.0% 5-BTB(F)TB-5 4.0% V2-HB-C 12.0% 1V2-HB-C 12.0% 3-HB-C 24.0% 3-HB(F)-C 5.0% 2-HHB-C 3.0% 3-HHB-C 6.0% The liquid crystal composition had clearing point: T NI = 85.6 (°C), viscosity at 20 °C: η 20 = 17.8(mPa·s), refractive anisotropy at 25 °C: Δn = 0.153, dielectric anisotropy at 20 °C: Δε = 9.1, and threshold voltage at 20°C: Vth =1.88(V). The chiral compound (CM-33)(0.74 parts by weight) was added to 100 parts by weight of the liquid crystal composition. The composition thus obtained was introduced into 240° STN cell of 5.6 µm in thickness and the cell was evaluated in yellow mode. Voltage-transmittance characteristic (V-T characteristic) was measured using 70 Hz square wave. A voltage (V 90 ) at transmittance of 90% and a voltage (V 10 ) at transmittance of 10% were 2.11 (V) and 2.21 (V), respectively, and steepness V 10 /V 90 was 1.047. The composition of this Example has higher clearing point, lower viscosity and larger refractive anisotropy than those of Comparative Examples 1 and 2. Further, the composition of this Example has greatly improved steepness as compared with those of Comparative Examples 1 and 2. Example 2 5-HH-VFF 22.0% 1-BHH-VFF 12.0% 1-BHH-2VFF 19.0% 3-BTB(F)TB-5 3.0% 5-BTB(F)TB-3 6.0% 5-BTB(F)TB-4 5.0% 5-BTB(F)TB-5 5.0% 1V2-BEB(F,F)-C 7.0% 3-HB-C 21.0% The liquid crystal composition had clearing point: T NI = 103.9 (°C), viscosity at 20 °C: η 20 = 17.4(mPa·s), refractive anisotropy at 25 °C : Δn = 0.159, dielectric anisotropy at 20 °C: Δε = 8.5, and threshold voltage at 20°C: Vth =2.12(V). The chiral compound (CN)(2.27 parts by weight) was added to 100 parts by weight of the liquid crystal composition. The composition thus obtained was introduced into 240 ° STN cell of 5.3 µm in thickness and the cell was evaluated in yellow mode. Voltage-transmittance characteristic (V-T characteristic) was measured using 70 Hz square wave. A voltage (V 90 ) at transmittance of 90% and a voltage (V 10 ) at transmittance of 10% were 2.33 (V) and 2.44 (V), respectively, and steepness V 10 /V 90 was 1.047. The composition of this Example has higher clearing point, lower viscosity and larger refractive anisotropy than those of Comparative Examples 1 and 2. Further, the composition of this Example has greatly improved steepness as compared with those of Comparative Examples 1 and 2. Example 3 3-HH-VFF 30.0% 5-BTB(F)TB-3 12.0% 1V2-BEB(F,F)-C 6.0% 3-HB-C 10.0% 2-BTB-1 10.0% 2-BTB-3 9.0% 3-HHB-1 7.0% 3-HB(F)TB-2 6.0% 3-HB(F)TB-3 5.0% 3-HB(F)TB-4 5.0% The liquid crystal composition had clearing Point: T NI = 81.0 (°C), viscosity at 20 °C: η 20 = 12.0(mPa·s), refractive anisotropy at 25 °C: Δn = 0.182, dielectric anisotropy at 20 °C: Δε = 4.8, and threshold voltage at 20°C: Vth = 2.13(V). The chiral compound (CM-33)(1.13 parts by weight) was added to 100 parts by weight of the liquid crystal composition. The composition thus obtained was introduced into 240° STN cell of 4.7 µm in thickness and the cell was evaluated in yellow mode. Voltage-transmittance characteristic (V-T characteristic) was measured using 70 Hz square wave. A voltage (V 90 ) at transmittance of 90% and a voltage (V 10 ) at transmittance of 10% were 2.35 (V) and 2.47 (V), respectively, and steepness V 10 /V 90 was 1.051. The composition of this Example has higher clearing point, lower viscosity and larger refractive anisotropy than those of Comparative Examples 1 and 2. Further, the composition of this Example has greatly improved steepness as compared with those of Comparative Examples 1 and 2. Example 4 3-HH-VFF 30.0% 5-BTB(F)TB-2 3.0% 5-BTB(F)TB-3 4.0% 5-BTB(F)TB-4 3.0% 1V2-BEB(F,F)-C 8.0% 3-HH-4 13.0% 3-HH-5 3.0% 2-BTB-1 14.0% 3-H2BTB-2 6.0% 3-PyBB-F 8.0% 4-PyBB-F 8.0% The liquid crystal composition had clearing point: T NI = 80.3 (°C), viscosity at 20 °C : η 20 = 13.9(mPa·s), refractive anisotropy at 25 °C: Δn = 0.172, dielectric anisotropy at 20 °C: Δε = 5.7, and threshold voltage at 20°C: Vth =2.14(V). The chiral compound (CN)(1.63 parts by weight) was added to 100 parts by weight of the liquid crystal composition. The composition thus obtained was introduced into 240 ° STN cell of 4.9 µm in thickness and the cell was evaluated in yellow mode. Voltage-transmittance characteristic (V-T characteristic) was measured using 70 Hz square wave. A voltage (V 90 ) at transmittance of 90% and a voltage (V 10 ) at transmittance of 10% were 2.44 (V) and 2.57 (V), respectively, and steepness V 10 /V 90 was 1.053. The composition of this Example has higher clearing point, lower viscosity and larger refractive anisotropy than those of Comparative Examples 1 and 2. Further, the composition of this Example has greatly improved steepness as compared with those of Comparative Examples 1 and 2. Example 5 5-HH-VFF 30.0% 5-BTB(F)TB-2 3.0% 5-BTB(F)TB-3 4.0% 5-BTB(F)TB-4 3.0% 1V2-BEB(F,F)-C 8.0% 3-HH-4 8.0% 3-HB-O2 7.0% 2-BTB-1 15.0% 3-HHB-1 6.0% 3-PyBB-F 8.0% 4-PyBB-F 8.0% The liquid crystal composition had clearing point: T NI = 79.7 (°C), viscosity at 20 °C: η 20 = 18.6(mPa·s), refractive anisotropy at 25 °C: Δn = 0.172, dielectric anisotropy at 20 °C: Δε = 5.5, and threshold voltage at 20°C: Vth =2.13(V). The chiral compound (CN)(1.60 parts by weight) was added to 100 parts by weight of the liquid crystal composition. The composition thus obtained was introduced into 240 ° STN cell of 4.9 µm in thickness and the cell was evaluated in yellow mode. Voltage-transmittance characteristic (V-T characteristic) was measured using 70 Hz square wave. A voltage (V 90 ) at transmittance of 90% and a voltage (V 10 ) at transmittance of 10% were 2.43 (V) and 2.55 (V), respectively, and steepness V 10 /V 90 was 1.049. The composition of this Example has higher clearing point, lower viscosity and larger refractive anisotropy than those of Comparative Examples 1 and 2. Further, the composition of this Example has greatly improved steepness as compared with those of Comparative Examples 1 and 2. Example 6 3-HH-VFF 11.0% 5-BTB(F)TB-2 5.0% 5-BTB(F)TB-3 5.0% 1V2-BEB(F,F)-C 7.0% 3-HB-C 14.0% 3-BB-C 2.0% 3-DB-C 2.0% 1O1-HB-C 2.0% 3-HH-4 11.0% 3-HHB-1 8.0% 3-HHB-3 17.0% 3-HHB-O1 2.0% 3-H2BTB-2 4.0% 3-HHEB-F 5.0% 5-HHEB-F 3.0% 3-HBEB-F 2.0% The liquid crystal composition had clearing point: T NI = 106.5 (°C), viscosity at 20 °C: η 20 = 18.1(mPa·s), refractive anisotropy at 25 °C: Δn = 0.138, dielectric anisotropy at 20 °C: Δε = 7.8, and threshold voltage at 20°C: Vth = 2.18(V). The chiral compound (CM-33)(0.79 parts by weight) was added to 100 parts by weight of the liquid crystal composition. The composition thus obtained was introduced into 240° STN cell of 6.3 µm in thickness and the cell was evaluated in yellow mode. Voltage-transmittance characteristic (V-T characteristic) was measured using 70 Hz square wave. A voltage (V 90 ) at transmittance of 90% and a voltage (V 10 ) at transmittance of 10% were 2.40 (V) and 2.54(V), respectively, and steepness V 10 /V 90 was 1.058. The composition of this Example has higher clearing point, lower viscosity and larger refractive anisotropy than those of Comparative Examples 1 and 2. Further, the composition of this Example has greatly improved steepness as compared with those of Comparative Examples 1 and 2. Example 7 3-HH-VFF 28.0% 5-BTB(F)TB-2 5.0% 5-BTB(F)TB-3 5.0% 5-BTB(F)TB-4 5.0% 1V2-BEB(F,F)-C 7.0% 3-HB-C 5.0% 2-BTB-1 10.0% 3-BTB-1 9.0% 3-H2BTB-2 5.0% 3-H2BTB-3 5.0% 3-HB(F)TB-2 8.0% 3-HB(F)TB-3 8.0% The liquid crystal composition had clearing point: T NI = 91.2 (°C), viscosity at 20 °C: η 20 = 14.3(mPa·s), refractive anisotropy at 25 °C: Δn = 0.211, dielectric anisotropy at 20 °C: Δε = 4.5, and threshold voltage at 20°C: Vth =2.32(V). The chiral compound (CM-33)(1.46 parts by weight) was added to 100 parts by weight of the liquid crystal composition. The composition thus obtained was introduced into 240° STN cell of 4.0 µm in thickness and the cell was evaluated in yellow mode. Voltage-transmittance characteristic (V-T characteristic) was measured using 70 Hz square wave. A voltage (V 90 ) at transmittance of 90% and a voltage (V 10 ) at transmittance of 10% were 2.62 (V) and 2.72(V), respectively, and steepness V 10 /V 90 was 1.038. The composition of this Example has higher clearing point, lower viscosity and larger refractive anisotropy than those of Comparative Examples 1 and 2. Further, the composition of this Example has greatly improved steepness as compared with those of Comparative Examples 1 and 2. Example 8 3-HH-VFF 30.0% 5-BTB(F)TB-3 12.0% 1V2-BEB(F,F)-C 6.0% 3-HB-C 11.0% 2-BTB-1 10.0% 1-BTB-3 8.0% 3-HHB-1 8.0% 3-HHB-3 10.0% 3-HB(F)VB-2 5.0% The liquid crystal composition had clearing point: T NI = 80.0 (°C), viscosity at 20 °C: η 20 = 11.1(mPa·s), refractive anisotropy at 25 °C: Δn = 0.166, dielectric anisotropy at 20 °C: Δε = 5.1, and threshold voltage at 20°C: Vth =2.17(V). The chiral compound (CM-33)(1.04 parts by weight) was added to 100 parts by weight of the liquid crystal composition. The composition thus obtained was introduced into 240° STN cell of 5.1 µm in thickness and the cell was evaluated in yellow mode. Voltage-transmittance characteristic (V-T characteristic) was measured using 70 Hz square wave. A voltage (V 90 ) at transmittance of 90% and a voltage (V 10 ) at transmittance of 10% were 2.37 (V) and 2.50(V), respectively, and steepness V 10 /V 90 was 1.055. The composition of this Example has higher clearing point, lower viscosity and larger refractive anisotropy than those of Comparative Examples 1 and 2. Further, the composition of this Example has greatly improved steepness as compared with those of Comparative Examples 1 and 2. Example 9 5-HH-VFF 28.0% 5-BTB(F)TB-2 5.0% 5-BTB(F)TB-3 5.0% 5-BTB(F)TB-4 5.0% 1V2-BEB(F,F)-C 7.0% 3-HB-C 5.0% 2-BTB-1 10.0% 3-BTB-1 9.0% 3-H2BTB-2 5.0% 3-H2BTB-3 5.0% 3-HB(F)TB-2 8.0% 3-HB(F)TB-3 8.0% The liquid crystal composition had clearing point: T NI = 94.5 (°C), viscosity at 20 °C: η 20 = 16.1(mPa·s), refractive anisotropy at 25 °C: Δn = 0.211, dielectric anisotropy at 20 °C: Δε = 4.5, and threshold voltage at 20°C: Vth =2.53(V). The chiral compound (CM-33)(1.42 parts by weight) was added to 100 parts by weight of the liquid crystal composition. The composition thus obtained was introduced into 240° STN cell of 4.0 µm in thickness and the cell was evaluated in yellow mode. Voltage-transmittance characteristic (V-T characteristic) was measured using 70 Hz square wave. A voltage (V 90 ) at transmittance of 90% and a voltage (V 10 ) at transmittance of 10% were 2.57 (V) and 2.70(V), respectively, and steepness V 10 /V 90 was 1.051. The composition of this Example has higher clearing point, lower viscosity and larger refractive anisotropy than those of Comparative Examples 1 and 2. Further, the composition of this Example has greatly improved steepness as compared with those of Comparative Examples 1 and 2. Example 10 3-HH-VFF 27.0% 5-BTB(F)TB-1 5.0% 5-BTB(F)TB-3 10.0% 1V2-BEB(F,F)-C 10.0% 3-HB-C 4.0% 3-HH-4 6.0% 1O1-HH-3 2.0% 3-PyB-2 2.0% 5-HEB-O1 2.0% 2-BTB-1 12.0% 3-BTB-1 4.0% 3-HHB-1 8.0% 3-H2BTB-2 4.0% 3-PyBH-3 2.0% 4-PyBB-3 2.0% The liquid crystal composition had clearing point: T NI = 78.1 (°C), viscosity at 20 °C: η 20 = 13.1(mPa·s), refractive anisotropy at 25 °C: Δn = 0.174, dielectric anisotropy at 20 °C : Δε = 6.1, and threshold voltage at 20°C: Vth = 2.16(V). The chiral compound (CN)(2.05 parts by weight) was added to 100 parts by weight of the liquid crystal composition. The composition thus obtained was introduced into 240 ° STN cell of 4.9 µm in thickness and the cell was evaluated in yellow mode. Voltage-transmittance characteristic (V-T characteristic) was measured using 70 Hz square wave. A voltage (V 90 ) at transmittance of 90% and a voltage (V 10 ) at transmittance of 10% were 2.46 (V) and 2.60(V), respectively, and steepness V 10 /V 90 was 1.057. The composition of this Example has higher clearing point, lower viscosity and larger refractive anisotropy than those of Comparative Examples 1 and 2. Further, the composition of this Example has greatly improved steepness as compared with those of Comparative Examples 1 and 2. Example 11 3-HH-VFF 14.0% 5-HH-VFF 15.0% 3-HH-3VF 2.0% 1-BHH-VF 2.0% 1-BHH-VFF 2.0% 5-BTB(F)TB-3 3.0% 5-BTB(F)TB-4 5.0% 3-HB-C 6.0% 3-BEB-C 4.0% 1V2-BEB(F,F)-C 10.0% 3-HHB-1 6.0% 3-HHB-O1 4.0% 3-HHB-3 12.0% 2-BTB-O1 10.0% 4-BTB-O2 5.0% The liquid crystal composition had clearing point: T NI = 84.1 (°C), viscosity at 20 °C : η 20 = 13.9(mPa·s), refractive anisotropy at 25 °C: Δn = 0.145, dielectric anisotropy at 20 °C: Δε = 6.5, and threshold voltage at 20°C: Vth =1.92(V). The chiral compound (CM-33)(0.89 parts by weight) was added to 100 parts by weight of the liquid crystal composition. The composition thus obtained was introduced into 240° STN cell of 5.9 µm in thickness and the cell was evaluated in yellow mode. Voltage-transmittance characteristic (V-T characteristic) was measured using 70 Hz square wave. A voltage (V 90 ) at transmittance of 90% and a voltage (V 10 ) at transmittance of 10% were 2.16 (V) and 2.31(V), respectively, and steepness V 10 /V 90 was 1.069. The composition of this Example has higher clearing point, lower viscosity and larger refractive anisotropy than those of Comparative Examples 1 and 2. Further, the composition of this Example has greatly improved steepness as compared with those of Comparative Examples 1 and 2. Example 12 3-HH-1VF 2.0% 5-HH-VFF 13.0% 1-BHH-2VF 2.0% 1-BHH-3VF 2.0% 5-BTB(F)TB-3 4.0% 5-BTB(F)TB-4 4.0% 5-BTH(F)TB-5 4.0% V2-HB-C 8.0% 1V2-HB-C 8.0% 1V2-BEB(F,F)-C 9.0% 3-HHB-O1 5.0% 3-HHB-1 8.0% 3-HHB-3 13.0% 3-HB(F)TB-2 5.0% 5-PyB-F 8.0% 3-HHB-F 3.0% 3-HEBEB-F 2.0% The liquid crystal composition had clearing point: T NI = 103.0 (°C), viscosity at 20 °C: η 20 = 18.5(mPa·s), refractive anisotropy at 25 °C : Δn = 0.152, dielectric anisotropy at 20 °C: Δε = 8.8, and threshold voltage at 20°C: Vth =2.00(V). The chiral compound (CN)(2.14 parts by weight) was added to 100 parts by weight of the liquid crystal composition. The composition thus obtained was introduced into 240 ° STN cell of 5.6 µm in thickness and the cell was evaluated in yellow mode. Voltage-transmittance characteristic (V-T characteristic) was measured using 70 Hz square wave. A voltage (V 90 ) at transmittance of 90% and a voltage (V 10 ) at transmittance of 10% were 2.17 (V) and 2.32(V), respectively, and steepness V 10 /V 90 was 1.069. The composition of this Example has higher clearing point, lower viscosity and larger refractive anisotropy than those of Comparative Examples 1 and 2. Further, the composition of this Example has greatly improved steepness as compared with those of Comparative Examples 1 and 2. Example 13 3-HH-VFF 32.0% 3-BTB(F)TB-5 6.0% 5-BTB(F)TB-3 7.0% 3O1-BEB(F)-C 15.0% 3-HHB-1 7.0% 3-HHB-O1 3.0% 3-H2BTB-2 4.0% 3-H2BTB-3 4.0% 3-H2BTB-4 4.0% 3-HB(F)TB-2 6.0% 3-HB(F)TB-3 6.0% 3-HB(F)TB-4 6.0% The liquid crystal composition had clearing point: T NI = 112.2 (°C), viscosity at 20 °C: η 20 =16.5(mPa·s), refractive anisotropy at 25 °C: Δn = 0.182, dielectric anisotropy at 20 °C: Δε = 6.3, and threshold voltage at 20°C: Vth =2.29(V). The composition of this Example has higher clearing point, lower viscosity and larger refractive anisotropy than those of Comparative Examples 1 and 2. Example 14 3-HH-VFF 14.0% 5-BTB(F)TB-3 4.0% 5-BTB(F)TB-4 4.0% 5-BTB(F)TB-5 4.0% V2-HB-C 12.0% 1V2-HB-C 12.0% 3-HB-C 24.0% 3-HB(F)-C 5.0% 2-HHB-C 3.0% 3-HHB-C 6.0% 2-BTB-1 4.0% 3-HB(F)TB-2 8.0% The liquid crystal composition had clearing Point: T NI = 85.3 (°C), viscosity at 20 °C: η 20 = 17.4(mPa·s), refractive anisotropy at 25 °C: Δn = 0.171, dielectric anisotropy at 20 °C: Δε = 9.4, and threshold voltage at 20°C: Vth =1.87(V). The composition of this Example has higher clearing point, lower viscosity and larger refractive anisotropy than those of Comparative Examples 1 and 2. Example 15 3-HH-VFF 30.0% 5-BTB(F)TB-3 5.0% 5-BTB(F)TB-4 5.0% V2-HB-C 9.0% 1V2-HB-C 8.0% 1V2-BEB(F,F)-C 8.0% 2-HHB-C 5.0% 3-HHB-C 5.0% 4-HHB-C 3.0% 3-HHB(F)-C 2.0% 2-H2BTB-2 5.0% 3-H2BTB-4 5.0% 1O1-HBBH-4 5.0% 1O1-HBBH-5 5.0% The liquid crystal composition had clearing point: T NI = 117.3 (°C), viscosity at 20 °C: η 20 = 19.7(mPa·s), refractive anisotropy at 25 °C: Δn = 0.154, dielectric anisotropy at 20 °C: Δε = 9.6, and threshold voltage at 20°C : Vth =2.10(V). The composition of this Example has higher clearing point, lower viscosity and larger refractive anisotropy than those of Comparative Examples 1 and 2. Example 16 5-HH-VFF 15.0% 5-BTB(F)TB-3 5.0% 5-BTB(F)TB-4 5.0% 5-BTB(F)TB-5 4.0% V2-HB-C 12.0% 1V2-HB-C 13.0% 1V2-BEB(F,F)-C 6.0% 3-HB-C 10.0% 3-HHB-1 10.0% 3-HHB-3 12.0% 3-HHB-O1 4.0% 3-HHB-F 2.0% 3-HBB-F 2.0% The liquid crystal composition had clearing point: T NI = 100.4 (°C), viscosity at 20 °C: η 20 = 19.5(mPa·s), refractive anisotropy at 25 °C: Δn = 0.153, dielectric anisotropy at 20 °C: Δε = 9.3, and threshold voltage at 20°C: Vth =2.05(V). The composition of this Example has higher clearing point, lower viscosity and larger refractive anisotropy than those of Comparative Examples 1 and 2. Example 17 5-HH-VFF 30.0% 1-BHH-VFF 8.0% 1-BHH-2VFF 11.0% 5-BTB(F)TB-3 5.0% 5-BTB(F)TB-4 4.0% 5-BTB(F)TB-5 4.0% 1V2-BEB(F,F)-C 6.0% 3-HB-C 18.0% 2-BTB-1 10.0% 3-HHB-1 4.0% The liquid crystal composition had clearing Point: T NI = 83.8 (°C), viscosity at 20 °C: η 20 = 13.3(mPa·s), refractive anisotropy at 25 °C: Δn = 0.150, dielectric anisotropy at 20 °C: Δε = 6.7, and threshold voltage at 20°C : Vth =2.07(V). The composition of this Example has higher clearing point, lower viscosity and larger refractive anisotropy than those of Comparative Examples 1 and 2. Example 18 5-HH-VFF 30.0% 1-BHH-2VFF 20.0% 5-BTB(F)TB-3 4.0% 5-BTB(F)TB-4 4.0% 5-BTB(F)TB-5 4.0% 1V2-BEB(F,F)-C 13.0% 3-HB-C 5.0% 3-HB-O2 5.0% 3-HHB-1 3.0% 3-HB(F)TB-2 4.0% 3-HB(F)TB-3 4.0% 3-HB(F)TB-4 4.0% The liquid crystal composition had clearing point: T NI = 100.8 (°C), viscosity at 20 °C : η 20 = 16.2(mPa·s), refractive anisotropy at 25 °C : Δn = 0.151, dielectric anisotropy at 20 °C : Δε = 9.2, and threshold voltage at 20°C: Vth =2.02(V). The composition of this Example has higher clearing point, lower viscosity and larger refractive anisotropy than those of Comparative Examples 1 and 2. Example 19 5-HH-VFF 20.0% 1-BHH-VFF 18.0% 1-BBH-VFF 13.0% 5-BTB(F)TB-3 5.0% 5-BTB(F)TB-4 5.0% 5-BTB(F)TB-5 4.0% 1V2-BEB(F,F)-C 10.0% 3-HB-C 12.0% 3-HB-O2 6.0% 3-HHB-1 7.0% The liquid crystal composition had clearing point: T NI = 103.1 (°C), viscosity at 20 °C: η 20 = 17.7(mPa·s), refractive anisotropy at 25 °C: Δn = 0.154, dielectric anisotropy at 20°C: Δε = 8.9, and threshold voltage at 20°C: Vth =2.04(V). The composition of this Example has higher clearing point, lower viscosity and larger refractive anisotropy than those of Comparative Examples 1 and 2. Example 20 3-HH-VFF 32.0% 1-BHH-VFF 5.0% 1-BHH-2VFF 5.0% 3-BTB(F)TB-5 6.0% 5-BTB(F)TB-3 7.0% 3O1-BEB(F)-C 15.0% 3-H2BTB-2 4.0% 3-H2BTB-3 4.0% 3-H2BTB-4 4.0% 3-HB(F)TB-2 6.0% 3-HB(F)TB-3 6.0% 3-HB(F)TB-4 6.0% The liquid crystal composition had clearing point: T NI = 110.3 (°C), viscosity at 20 °C: η 20 = 17.5(mPa·s), refractive anisotropy at 25 °C : Δn = 0.180, dielectric anisotropy at 20°C: Δε = 6.3, and threshold voltage at 20°C: Vth = 2.28(V). The composition of this Example has higher clearing point, lower viscosity and larger refractive anisotropy than those of Comparative Examples 1 and 2. The liquid crystal composition of the present invention has various properties required for the STN display systems, in particular, shows excellent voltage-transmittance characteristic (high steepness) suitable for colorization and is excellent in a high speed response because it has low viscosity and high Δn.

Claims: A liquid crystal composition which comprises a first component comprising at least one compound selected from the group consisting of compounds of formulas (I-a) to (I-f), a second component comprising at least one compound of formula (II) and a third component comprising at least one compound selected from the group consisting of compounds of formulas (III-a) to (III-c). wherein R 1 is an alkyl group having 1 to 10 carbon atoms; one or two or more methylene groups (-CH 2 -) which are not vicinal in the alkyl group may be substituted by oxygen atom (-O-) and/or -CH=CH-; and n is an integer of 0 to 20; R 2 and R 3 are independently alkyl groups having 1 to 10 carbon atoms; one or two or more methylene groups (-CH 2 -) which are not vicinal in the alkyl groups may be substituted by oxygen atom (-O-) and/or -CH=CH-; and A is 1,4-phenylene group whose hydrogen atom(s) in the lateral position may be substituted by fluorine atom(s); R 4 is an alkyl group having 1 to 10 carbon atoms; one or two or more methylene groups (-CH 2 -) which are not vicinal in the alkyl group may be substituted by oxygen atom (-O-) and/or -CH=CH-; Z 0 is -COO- or -CH 2 CH 2 -, Z 1 is -CH 2 CH 2 -, -COO- or a single bond; Q 1 is hydrogen or fluorine atom; B 1 is 1,4-cyclohexylene, 1,4-phenylene or 1,3-dioxane-2,5-diyl; B 2 and B 3 are independently 1,4-cyclohexylene or 1,4-phenylene group whose hydrogen atom(s) in the lateral position may be substituted by fluorine atom(s); p, q and m are independently 0 or 1. The liquid crystal composition of claim 1 wherein the first component is comprised in the amount of 3 to 60% by weight, the second component in the amount of 3 to 30% by weight and the third component in the amount of 5 to 70% by weight, based on the total weight of the composition. The liquid crystal composition of claim 1 or 2 which further comprises a fourth component comprising at least one compound selected from the group consisting of compounds of formulas (IV), (V), (VI-a) and (VI-b): R 5 - (B 4 ) - Z 2 - (C 1 ) - R 6 wherein R 5 and R 6 are independently alkyl groups having 1 to 10 carbon atoms; one or two or more methylene groups (-CH 2 -) which are not vicinal in the alkyl groups may be substituted by oxygen atom (-O-) and/or -CH=CH-; B 4 is 1,4- cyclohexylene, pyrimidine-2,5-diyl or 1,4-phenylene group; C 1 is 1,4-cyclohexylene or 1,4-phenylene group; Z 2 is -C≡C-, -COO-, -CH 2 CH 2 -, -CH=CH-, -CF=CF- or a single bond; R 7 - (D) - Z 3 - (E) - Z 4 - (G) - R 8 wherein R 7 is an alkyl group having 1 to 10 carbon atoms; one or two or more methylene groups (-CH 2 -) which are not vicinal in the alkyl group may be substituted by oxygen atom (-O-) and/or -CH=CH-; R 8 is an alkyl, alkoxy or alkoxymethyl group having 1 to 10 carbon atoms; D is 1,4-cyclohexylene or pyrimidine-2,5-diyl group; E is 1,4-cyclohexylene or 1,4-phenylene group whose hydrogen atom(s) in the lateral position may be substituted by fluorine atom(s); G is 1,4-cyclohexylene or 1,4-phenylene group; Z 3 is -CH 2 CH 2 - or a single bond; Z 4 is -C≡C-, -COO-, -CH=CH- or a single bond; wherein R 9 is an alkyl group having 1 to 10 carbon atoms; one or two or more methylene groups (-CH 2 -) which are not vicinal in the alkyl group may be substituted by oxygen atom (-O-) and/or -CH=CH-; R 10 is an alkyl, alkoxy or alkoxymethyl group having 1 to 10 carbon atoms; and Q 2 is hydrogen or fluorine atom. The liquid crystal composition of claim 3 wherein the fourth component is comprised in the amount of 0 to 60% by weight based on the total weight of the composition. The liquid crystal composition of any one of claims 1 to 4 which further comprises a fifth component comprising at least one compound selected from the group consisting of compounds of formulas (VII) and (VIII). wherein R 11 is an alkyl group having 1 to 10 carbon atoms; Q 3 is hydrogen or fluorine atom; k is 0 or 1; R 12 is an alkyl group having 1 to 10 carbon atoms; J is 1, 4-cyclohexylene or 1,4-phenylene group; Q 4 and Q 5 are independently hydrogen or fluorine atom; Z 5 and Z 6 are independently -COO- or single bond; and h is 0, 1 or 2. The liquid crystal composition of claim 5 wherein the fifth component is comprised in the amount of 0 to 50% by weight based on the total weight of the composition. A liquid crystal display element wherein the liquid crystal composition of any one of claims 1 to 6 is used. The liquid crystal display element of claim 7 wherein the element is an STN display element.

Inventors: KAWANO KATSUYUKI, MATSUSHITA TETSUYA, MURASHIRO KATSUYUKI, NAKAGAWA ETSUO, TAKESHITA FUSAYUKI, KAWANO, KATSUYUKI, MATSUSHITA, TETSUYA, MURASHIRO, KATSUYUKI, NAKAGAWA, ETSUO, TAKESHITA, FUSAYUKI, Murashiro, Katsuyuki, Room No.B-226
Applicants: CHISSO CORP, CHISSO CORPORATION
Application year: 1997
Main classification: C09K19
IPC codes: C09K19, G02F1