LAUNDRY DETERGENT COMPOSITIONS AND METHODS FOR PROVIDING SOIL RELEASE TO COTTON FABRIC

Abstract: Laundry detergent compositions that provide soil release benefits to all fabric comprising modified polyamine cotton soil release agents and non-cotton soil release agents, and a method for providing soil release benefits to cotton fabric by contacting cotton articles with a water soluble and/or dispersible, modified polyamine having functionalized backbone moieties and improved stability toward bleach. The present invention further relates to providing soil release benefits to all fabric in the laundry wash load in the presence of a bleaching agent.

Description: LAUNDRY DETERGENT COMPOSITIONS AND METHODS FOR PROVIDING SOIL RELEASE TO COTTON FABRIC FIELD OF THE INVENTION The present invention relates to laundry detergent compositions that provide soil release benefits to all fabric comprising modified polyamine cotton soil release agents and non-cotton soil release agents. The present invention also relates to a method for providing soil release benefits to cotton fabric by contacting cotton articles with a water soluble and/or dispersible, modified polyamine having functionalized backbone moieties and improved stability toward bleach. The present invention further relates to providing soil release benefits to all fabric in the laundry wash load in the presence of a bleaching agent. BACKGROUND OF THE INVENTION A wide variety of soil release agents for use in domestic and industrial fabric treatment processes such as laundering, fabric drying in hot air clothes dryers, and the like are known in the art. Various soil release agents have been commercialized and are currently used in detergent compositions and fabric softener/antistatic articles and compositions. Such soil release polymers typically comprise an oligomeric or polymeric ester "backbone". Soil release polymers are generally very effective on polyester or other synthetic fabrics where the grease, oil or similar hydrophobic stains spread out and form a attached film and thereby are not easily removed in an aqueous laundering process. Many soil release polymers have a less dramatic effect on "blended" fabrics, that is on fabrics that comprise a mixture of cotton and synthetic material, and have little or no effect on cotton articles. The reason for the affinity of many soil release agents for synthetic fabric is that the backbone of a polyester soil release polymer typically comprises a mixture of terephthalate residues and ethyleneoxy or propyleneoxy polymeric units; the same materials that comprise the polyester fibers of synthetic fabric. This similar structure of soil release agents and synthetic fabric produce an intrinsic affinity between these compounds. Extensive research in this area has yielded significant improvements in the effectiveness of polyester soil release agents yielding materials with enhanced product performance and formulatability. Modifications ofthe polymer backbone as well as the selection of proper end-capping groups has produced a wide variety of polyester soil release polymers. For example, end-cap modifications, such as the use of sulfoaryl moieties and especially the low cost isethionate-derived end-capping units, have increased the range of solubility and adjunct ingredient compatibility of these polymers without sacrifice to soil release effectiveness. Many polyester soil release polymers can now be formulated into both liquid as well as solid (i.e., granular) detergents. As in the case of polyester soil release agents, producing an oligomeric or polymeric material that mimics the structure of cotton has not resulted in a cotton soil release polymer. Although cotton and polyester fabric are both comprised of long chain polymeric materials, they are chemically very different. Cotton is comprised of cellulose fibers that consist of anhydroglucose units joined by 1-4 linkages. These glycosidic linkages characterize the cotton cellulose as a polysaccharide whereas polyester soil release polymers are generally a combination of terephthalate and ethylene/propylene oxide residues. These differences in composition account for the difference in the fabric properties of cotton versus polyester fabric. Cotton is hydrophilic relative to polyester. Polyester is hydrophobic and attracts oily or greasy dirt and can easily be "dry cleaned". Importantly, the terephthalate and ethyleneoxy/propyleneoxy backbone of polyester fabric does not contain reactive sites, such as the hydroxyl moieties of cotton, that react with stains in different manner than synthetics. Many cotton stains become "fixed" and can only be resolved by bleaching the fabric. Until now the development of an effective cotton soil release agent for use in a laundry detergent has been elusive. Attempts by others to apply the paradigm of matching the structure of a soil release polymer with the structure ofthe fabric, a method successful in the polyester soil release polymer field, has nevertheless yielded marginal results when applied to cotton fabric soil release agents. The use of methylcellulose, a cotton polysaccharide with modified oligomeric units, proved to be more effective on polyesters than on cotton. For example, U.K. 1,314,897, published April 26, 1973 teaches a hydroxypropyl methyl cellulose material for the prevention of wet-soil redeposition and improving stain release on laundered fabric. While this material appears to be somewhat effective on polyester and blended fabrics, the disclosure indicates these materials to be unsatisfactory at producing the desired results on cotton fabric. Other attempts to produce a soil release agent for cotton fabric have usually taken the form of permanently modifying the chemical structure ofthe cotton fibers themselves by reacting a substrate with the polysaccharide polymer backbone. For example, U. S. Patent No. 3,897,026 issued to Kearney, discloses cellulosic textile materials having improved soil release and stain resistance properties obtained by reaction of an ethylene- maleic anhydride co-polymer with the hydroxyl moieties ofthe cotton polymers. One perceived drawback of this method is the desirable hydrophilic properties ofthe cotton fabric are substantially modified by this process. Non-permanent soil release treatments or finishes have also been previously attempted. U.S. Patent No. 3,912,681 issued to Dickson teaches a composition for applying a non-permanent soil release finish comprising a polycarboxylate polymer to a cotton fabric. However, this material must be applied at a pH less than 3, a process not suitable for consumer use nor compatible with laundry detergents which typically have a pH greater than 8.5. U.S. Patent No. 3,948,838 issued to Hinton, et alia describes high molecular weight (500,000 to 1,500,000) polyacrylic polymers for soil release. These materials are used preferably with other fabric treatments, for example, durable press textile reactants such as formaldehyde. This process is also not readily applicable for use by consumers in a typical washing machine. U.S. Patent 4,559,056 issued to Leigh, et alia discloses a process for treating cotton or synthetic fabrics with a composition comprising an organopolysiloxane elastomer, an organosiloxaneoxyalkylene copolymer crosslinking agent and a siloxane curing catalyst. Organosilicone oligomers are well known by those skilled in the art as suds supressors Other soil release agents not comprising terephthalate and mixtures of polyoxy ethylene/propylene are vinyl caprolactam resins as disclosed by Rupert, et alia in U.S. Patent Nos. 4,579,681 and 4,614,519. These disclosed vinyl caprolactam materials have their effectiveness limited to polyester fabrics, blends of cotton and polyester, and cotton fabrics rendered hydrophobic by finishing agents. Examples of alkoxylated polyamines and quaternized alkoxylated polyamines are disclosed in European Patent Application 206,513 as being suitable for use as soil dispersents, however their possible use as a cotton soil release agent is not disclosed. In addition, these materials do not comprise N-oxides, a key modification made to the polyamipes ofthe present invention and a component ofthe increased bleach stability exhibited by the presently disclosed compounds. It has now been surprisingly discovered that effective soil release agents for cotton articles can be prepared from certain modified polyamines. This unexpected result has yielded compositions that are key to the present method for providing soil release benefits once available to only synthetic and synthetic-cotton blended fabric. The process or method ofthe present invention provides for soil release benefits on all cotton articles whether laundered in the presence of a bleaching agent or not. The process or method ofthe present invention provides for soil release benefits to all fabric in the laundry wash load, as opposed to previous methods that only provided soil release protection to synthetic and cotton-synthetic blended fabric. The present process, because ofthe stability ofthe modified polyamines disclosed herein toward bleaching agents, now provides this soil release to white cotton articles which the consumer may choose to launder in the presence of traditional bleaching agents. The process or method ofthe present invention is equally effective when the laundry detergent compositions disclosed herein are solid or liquid. The solid laundry detergents may be in the form of granules, flakes or laundry bars. The liquid detergents can have a wide range of viscosity and may include heavy concentrates, pourable "ready" detergents, or light duty fabric pre-treatments. The modified polyamines disclosed in the present method are especially compatible with other laundry detergent additives and adjuncts. BACKGROUND ART In addition to the above cited art, the following disclose various soil release polymers or modified polyamines; U.S. Patent 4,548,744, Connor, issued October 22, 1985; U.S. Patent 4,597,898, Vander Meer, issued July 1, 1986; U.S. Patent 4,877,896, Maldonado, et al., issued October 31, 1989; U.S. Patent 4,891,160, Vander Meer, issued January 2, 1990; U.S. Patent 4,976,879, Maldonado, et al., issued December 11, 1990; U.S. Patent 5,415,807, Gosselink, issued May 16,1995; U.S. Patent 4,235,735, Marco, et al., issued November 25, 1980; WO 95/32272, published November 30, 1995; U.K. Patent 1,537,288, published December 29, 1978; U.K. Patent 1,498,520, published January 18, 1978; German Patent DE 28 29 022, issued January 10, 1980; Japanese Kokai JP 06313271, published April 27, 1994. SUMMARY OF THE INVENTION The present invention relates to laundry detergent compositions containing cotton soil release agents in combination with suitable non-cotton soil release agents thereby providing laundry detergent compositions that provide soil release benefits to all fabric and to methods for providing cotton soil release to fabrics by contacting the compounds ofthe present invention with cotton fabric. The present invention relates to laundry detergent compositions comprising: a) at least about 0.01 % to about 95% by weight, of a detersive surfactant selected from the group consisting of anionic, nonionic, zwitterionic, and ampholytic surfactants, and mixtures thereof; b) from about 0.01 to about 10% by weight, of a soil release polymer having effective soil release on non-cotton fabric; c) optionally from about 0.05 to about 30% by weight, of a bleach; from about 0.01 to about 10% by weight, a water-soluble or dispersible, modified polyamine cotton soil release agent comprising a polyamine backbone corresponding to the formula: ¥ I PfeN-Rfen -[N-R] m -[N-R] n -NH 2 having a modified polyamine formula V/ n +ι )W m Y n Z or a polyamine backbone corresponding to the formula: H j R [H 2 N-R] n -k+l— [N-R] m -[N-R] n -{N-R]k-NH 2 having a modified polyamine formula Vfo.jς- f - i )W m Y n Y ^Z, wherein k is less than or equal to n, said polyamine backbone prior to modification has a molecular weight greater than about 200 daltons, wherein i) V units are terminal units having the formula: ii) W units are backbone units having the formula: iii) Y units are branching units having the formula: iv) Z units are terminal units having the formula: wherein backbone linking R units are selected from the group consisting of C2-C12 alkylene, C4-C12 alkenylene, C3-C12 hydroxyalkylene, C4-C12 dihydroxy-alkylene, Cg-C 12 dialkylarylene, -(R1O) X R1-, -(R^R^OR^x-, -(CH 2 CH(OR2)CH 2 O) z - (RlO) y Rl(OCH 2 CH(OR 2 )CH2)w-> -C(O)(R4) r C(O)-, -CH 2 CH(OR2)CH 2 -, and mixtures thereof; wherein R^ is C2-Cg alkylene and mixtures thereof; R 2 is hydrogen, - (RlO) x B, and mixtures thereof; R 3 is Cj-Cig alkyl, C7-C12 arylalkyl, C7-Ci2 alkyl substituted aryl, C^-C^ aryK and mixtures thereof; R^ is C1-C12 alkylene, C4-C12 alkenylene, Cg-Ci2 arylalkylene, C^-C J O arylene, and mixtures thereof; R^ is Cj-C]2 alkylene, C3-C12 hydroxyalkylene, C4-C12 dihydroxy-alkylene, Cg-Ci2 dialkylarylene, -C(O)-, -C(O)NHR 6 NHC(O)-, -R^OR 1 )-, -C(O)(R4) r C(O)-, -CH 2 CH(OH)CH 2 -, - CH2CH(OH)CH 2 O(R 1 O) y R 1 -OCH 2 CH(OH)CH2-, and mixtures thereof; R 6 is C2-C 12 alkylene or Cg-Ci 2 arylene; E units are selected from the group consisting of hydrogen, C1-C22 alkyl, C3-C22 alkenyl, C7-C22 arylalkyl, C2-C22 hydroxyalkyl, - (CH 2 ) p Cθ2M, -(CH 2 )qSO 3 M, -CH(CH 2 CO 2 M)CO2M, -(CH 2 ) p PO 3 M, -(RO) X B, - C(O)R3, and mixtures thereof; provided that when any E unit of a nitrogen is a hydrogen, said nitrogen is not also an N-oxide; B is hydrogen, Cj-Cg alkyl, - (CH 2 ) q SO 3 M, -(CH 2 ) p CO 2 M, -(CH2)q(CHSO 3 M)CH 2 SO3M, -(CH 2 )q(CHSO 2 M)- CH2SO3M, -(CH2)pPO3M, -PO3M, and mixtures thereof; M is hydrogen or a water soluble cation in sufficient amount to satisfy charge balance; X is a water soluble anion; k and k' have the value from 1 to about 15; m has the value from 4 to about 400; n has the value from 0 to about 200; p has the value from 1 to 6, q has the value from 0 to 6; r has the value of 0 or 1; w has the value 0 or 1; x has the value from 1 to 100; y has the value from 0 to 100; z has the value 0 or 1 ; and e) the balance carrier and adjunct ingredients. The present invention further relates to a method of providing soil release benefits to cotton fabric by contacting said fabric with a laundry composition comprising: a) at least about 0.001% by weight, a water-soluble or dispersible (preferably bleach stable), modified polyamine cotton soil release agent according to the present invention; and b) the balance carrier and adjunct ingredients. It is a further purpose of the present invention to provide a method for providing soil release benefits to white cotton fabric in the presence of a bleaching agent by contacting an aqueous solution of a bleach stable soil release agent with white cotton fabric in the presence of a bleaching agent. It is a yet further purpose of the present invention to provide a method for providing soil release benefits to all fabrics that comprise the laundry wash load in the presence of a bleaching agent. All percentages, ratios and proportions herein are by weight, unless otherwise specified. All temperatures are in degrees Celsius (° C) unless otherwise specified. All documents cited are in relevant part, incorporated herein by reference. DETAILED DESCRIPTION OF THE INVENTION The compositions ofthe present invention comprise: a) at least about 0.01 % to about 95% by weight, of a detersive surfactant selected from the group consisting of anionic, nonionic, zwitterionic, and ampholytic surfactants, and mixtures thereof; b) from about 0.01 to about 10% by weight, of a soil release polymer having effective soil release on non-cotton fabric; c) from about 0.01 to about 10% by weight, a water-soluble or dispersible, modified polyamine cotton soil release agent according to the present invention; and d) the balance carrier and adjunct ingredients. Preferably the laundry detergent compositions comprise: a) at least about 0.01 % to about 95% by weight, of a detersive surfactant selected from the group consisting of anionic, nonionic, zwitterionic, and ampholytic surfactants, and mixtures thereof; b) from about 0.01 to about 10% by weight, of an anionic soil release polymer having effective soil release on non-cotton fabric; c) optionally from about 0.05 to about 30% by weight, of a bleach; d) from about 0.01 to about 10% by weight, a water-soluble or dispersible, bleach stable, modified polyamine cotton soil release agent according to the present invention; and e) the balance carrier and adjunct ingredients. More preferred laundry detergent compositions comprise: a) at least about 0.01% to about 95% by weight, of an anionic detersive surfactant; b) at least about 0.01% to about 95% by weight, of a nonionic detersive surfactant; c) from about 0.01 to about 10% by weight, of a soil release polymer having effective soil release on non-cotton fabric; d) optionally from about 0.05 to about 30% by weight, of a bleach; e) from about 0.01 to about 10% by weight, a water-soluble or dispersible, bleach stable, modified polyamine cotton soil release agent according to the present invention; and f) the balance carrier and adjunct ingredients. Also preferred laundry detergent compositions comprise: a) at least about 0.01 % to about 95% by weight, of an anionic detersive surfactant selected from the group consisting of alkyl sulfates, alkyl ethoxy sulfates, and mixtures thereof; b) at least about 0.01 % to about 95% by weight, of a nonionic detersive surfactant; c) from about 0.01 to about 10% by weight, of an anionic soil release polymer having effective soil release on non-cotton fabric; d) optionally from about 0.05 to about 30% by weight, of a bleach; e) from about 0.01 to about 10% by weight, a water-soluble or dispersible, bleach stable, modified polyamine cotton soil release agent according to the present invention; and f) the balance carrier and adjunct ingredients. A further preferred laundry detergent composition comprises: a) at least about 0.01% to about 95% by weight, of a polyhydroxy fatty acid amide nonionic detersive surfactant; b) from about 0.01 to about 10% by weight, of an anionic soil release polymer having effective soil release on non-cotton fabric; c) optionally from about 0.05 to about 30% by weight, of a bleach; d) from about 0.01 to about 10% by weight, a water-soluble or dispersible, bleach stable, modified polyamine cotton soil release agent according to the present invention; e) the balance carrier and adjunct ingredients; and f) sufficient alkaline material to provide the composition with a pH of about 7.2 to about 10.5 when measured as a 10% solution in water. Non-cotton Soil Release Polymers The laundry detergent compositions ofthe present invention must comprise a non-cotton soil release polymer. However, the present invention also relates to methods of providing soil release benefits to cotton fabrics, wherein laundry compositions that do not comprise non-cotton soil release agents are also suitable for use. Among the preferred non-cotton soil release polymers suitable for use in the laundry detergent compositions ofthe present invention are the following. Preferred non-cotton soil release agent - A. Suitable for use in the laundry detergent compositions ofthe present invention are preferred non-cotton soil release polymers comprising: a) a backbone comprising: i) at least one moiety having the formula: ii) at least one moiety having the formula: wherein R^ is C2-C6 linear alkylene, C3-C6 branched alkylene, C5-C7 cyclic alkylene, and mixtures thereof; RlO is independently selected from hydrogen or -L-SO3"M + ; wherein L is a side chain moiety selected from the group consisting of alkylene, oxyalkylene, alkyleneoxyalkylene, arylene, oxyarylene, alkyleneoxyarylene, poly(oxyalkylene), oxyalkyleneoxyarylene, poly(oxyalkylene)oxyarlyene, alkylenepoly(oxyalkylene),and mixtures thereof; M is hydrogen or a salt forming cation; i has the value of 0 or 1; iii) at least one trifunctional, ester-forming, branching moiety; iv) at least one 1 ,2-oxyalkyleneoxy moiety; and b) one or more capping units comprising: i) ethoxylated or propoxylated hydroxyethanesulfonate or ethoxylated or propoxylated hydroxypropanesulfonate units ofthe formula (MO 3 S)(CH 2 ) m (R 1 0) n -, where M is a salt forming cation such as sodium or tetralkylammonium, R 1 ' is ethylene or propylene or a mixture thereof, m is 0 or 1, and n is from 1 to 20; ii) sulfoaroyl units ofthe formula -(O)C(C 6 H 4 )(SO 3 -M + ), wherein M is a salt forming cation; iii) modified poly(oxyethylene)oxy monoalkyl ether units ofthe formula R 12 O(CH 2 CH 2 O)ι c -, wherein R 12 contains from 1 to 4 carbon atoms and k is from about 3 to about 100; and iv) ethoxylated or propoxylated phenolsulfonate end-capping units of the formula MO 3 S(C 6 H 4 )(OR 13 ) n O-, wherein n is from 1 to 20; M is a salt- forming cation; and R 13 is ethylene, propylene and mixtures thereof. This type of preferred non-cotton soil release polymer of the present invention may be described as having the formula [(Cap)(R 4 ) t ] [( A-R I -A-R 2 ) u ( A-R ' - A-R 3 ) V (A-R 1 -A-R5) w -A-Rl-A-][(R4) t (Cap)] wherein A is a carboxy linking moiety having the formula O II — c— Rl is arylene, preferably a 1,4-phenylene moiety having the formula such that when A units and R* units are taken together in the formula A-R^-A they form a terephthalate unit having the formula R2 units are ethyleneoxy or 1,2-propyleneoxy. R2 units are combined with terephthalate moieties to form (A-R •-A-R 2 ) units having the formula wherein R' and R" are either hydrogen or methyl provided that R' and R" are not both methyl at the same time. R 3 units are trifunctional, ester-forming, branching moieties having the formula O I — O-CH 2 — CH-CH 2 — O — Preferably R 3 units comprise a glycerol moiety which is placed into the soil release polymer backbone to provide a branch point. When R 3 units are combined with terephthalate moieties to form units ofthe polymer backbone, for example, (A-R'-A- R 3 )-A-R1 -A units, these units have the formula or the formula wherein one terephthalate residue is taken to be a part ofthe (A-R 1 -A-R 3 ) unit while the second terephthalate comprises a part of another backbone unit, such as a (A-R 1 -A-R 2 ) unit, a (A-Rϊ-A-R 5 ) unit, a -A-R 1 -A-[(R 4 ) t (Cap)] unit or a second (A-R'-A-R 3 ) unit. The third functional group, which is the beginning ofthe branching chain, is also typically bonded to a terephthalate residue also a part of a (A-R^A-R 2 ) unit, a (A-R'-A- R 5 ) unit, " a -A-R'-A-KR^Cap)] unit or another (A-R'-A-R 3 ) unit. An example of a section of a soil release polymer containing a "trifunctional, ester-forming, branching moiety" R 3 unit which comprises a glycerol unit, has the formula R 4 units are R 2 , R 3 or R 5 units. R5 units are units having the formula wherein R^ is C2-C6 linear alkylene, C3-C6 branched alkylene, and mixtures thereof; preferably R 1 ^ is independently selected from hydrogen or -L-SO3"M + ; wherein L is a side chain moiety selected from the group consisting of alkylene, oxyalkylene, alkyleneoxyalkylene, arylene, oxyarylene, alkyleneoxyarylene, poly(oxyalkylene), oxyalkyleneoxyarylene, poly(oxyalkylene)oxyarlyene, alkylenepoly(oxyalkylene),and mixtures thereof; M is hydrogen or a salt forming cation; i has the value of 0 or 1 ; Each carbon atom ofthe R^ units is substituted by R}® units that are independently selected from hydrogen or -L-SO3"M + , provided no more than one -L- SO3"M + units is attached to an R^ unit; L is a side chain connecting moiety selected from the group consisting of alkylene, oxyalkylene, alkyleneoxyalkylene, arylene, oxyarylene, alkyleneoxyarylene, poly(oxyalkylene), oxyalkyleneoxyarylene, poly(oxyalkylene)oxyarlyene, alkylenepoly(oxyalkylene),and mixtures thereof. M is a cationic moiety selected from the group consisting of lithium, sodium, potassium, calcium, and magnesium, preferably sodium and potassium. Preferred R 5 moieties are essentially R 10 substituted C 2 -Cg alkylene chains. The R5 units comprise either one C 2 -CG alkylene chain substituted by one or more independently selected R}® moieties (preferred) or two C 2 -C $ alkylene chains said alkylene chains joined by an ether oxygen linkage, each alkylene chain substituted by one or more independently selected R^ moieties, that is R^ may comprise two separate R^ units, each of which is substituted by one or more independently selected R 10 moieties. Preferably only one carbon atom of each R" moiety is substituted by an -L- SO3"M + unit with the remaining R O substituents comprising a hydrogen atom. When the value of the index i is equal to 1 (two R^ units comprise the R^ unit), a preferred formula is wherein each R" comprises a C2 alkylene moiety. Preferably one RlO moiety is -L- SO3"M + , preferably the C2 carbon is substituted by the -L-SO3 * M + moiety, and the balance are hydrogen atoms, having therefore a formula: — CHCH 2 -O-CH 2 CH 2 — CH 2 (OCH 2 CH 2 ) x SO 3 " M + wherein L is a polyethyleneoxymethyl substituent, x is from 0 to about 20. As used herein, the term "R 5 moieties consist essentially of units having the index i equal to 0 wherein R 10 units are hydrogen and one R 10 units is equal to -L-SO3"M + , wherein L is a side chain connecting moiety selected from the group consisting of alkylene, alkenylene, alkoxyalkylene, oxyalkylene, arylene, alkylarylene, alkoxyarylene and mixtures thereof, refers to the preferred compounds of the present invention wherein the R}® moieties consist of one -L-SO3"M + moiety and the rest of the RlO moieties are hydrogen atoms, for example a — O — CH 2 — CH— O— I CH 2 (OCH 2 CH2)χSθ3 Na which is capable of inclusion into the polymeric backbone ofthe soil release polymers of the present invention as an -A-R 5 -A- backbone segment. The units are easily incorporated into the oligomer or polymer backbone by using starting materials having the general formula wherein x, for the purposes of the L moiety of the present invention, is from 0 to 20. Other suitable monomers capable of inclusion into the backbone ofthe type A preferred non-cotton soil release polymers ofthe present invention as R^ moieties includes the alkylene poly(oxyalkylene)oxyarylene containing monomer having the general formula wherein x is 0 to 20. A further example of a preferred monomer resulting in a preferred R5 unit wherein i is equal to 0, are the sodiosulfopoly(ethyleneoxy)methy 1-1,2- propanediols having the formula HO— CH 2 — CH-OH I CH 2 (OCH 2 CH 2 )χS0 3 Na wherein x is from 0 to about 20; more preferred are the monomers OH I HO— CH 2 — CH— CH 2 — OH or HO— CH 2 — CH— CH 2 OCH 2 CH 2 S0 3 " Na + OCH 2 CH 2 S0 3 " Na + The preferred non-cotton soil release agents of the present invention in addition to the afore-mentioned Rl, R2, R 3 , R4, and R^ units also comprise one or more capping groups, -(Cap). The capping groups are independently selected from ethoxylated or propoxylated hydroxyethane and propanesulfonate units ofthe formula (MO3S)(CH 2 ) m (R 1 •OJn-, where M is a salt forming cation such as sodium or tetralkylammonium as described herein above, R 1 1 is ethylene or propylene or a mixture thereof, m is 0 or 1, and n is from 1 to 20, preferably n is from 1 to about 4; sulfoaroyl units ofthe formula -(O)C(CgH4)(SO3 ~ M + ), wherein M is a salt forming cation as described herein above; modified poly(oxyethylene)oxy monoalkyl ether units ofthe formula JΛ 12 O(CH 2 CH 2 O)k- wherein R 12 contains from 1 to 4 carbon atoms, R 12 is preferably methyl, and k is from about 3 to about 100, preferably about 3 to about 50, more preferably 3 to about 30; and ethoxylated or propoxylated phenolsulfonate end- capping units ofthe formula MO3S(C6H4)(OR ,3 ) n O-, wherein n is from to 20; M is a salt- forming cation; and R 13 is ethylene, propylene and mixtures thereof. Most preferred end capping unit is the isethionate-type end capping unit which is a hydroxyethane moiety, (MO 3 S)(CH 2 ) m (R 1 1 O) n -, preferably R 1 1 is ethyl, m is equal to 0, and n is from 2 to 4. The value of t is 0 or 1; the value of u is from about 0 to about 60; the value of v is from about 0 to about 35; the value of w is from 0 to 35. Preferred non-cotton soil release polymers ofthe present invention having the formula [(Cap)(R 4 ) t ] [(A-R 1 -A-R 2 ) U (A-R « -A-R 3 ) V (A-R ' -A-R5) w. -A-R 1 -A-][(R4) t (Cap)J can be conveniently expressed as the following generic structural formula The following structure is an example ofthe preferred non-cotton soil release polymers of the present invention. The above-described preferred non-cotton soil release agents are fully described in U.S. Patent Application Serial No. 08/545,351 filed November 22, 1995 which is a continuation-in-part of U.S. Patent Applicauon Serial No. 08/355,938 filed December 14, 1994, both of which are incorporated herein by reference. Other non-cotton soil release polymers suitable for use in the compositions ofthe present invention are further described herein below. The preferred non-cotton SRA's can be further described as oligomeric esters comprising: (1) a backbone comprising (a) at least one unit selected from the group consisting of dihydroxysulfonates, polyhydroxy sulfonates, a unit which is at least trifunctional whereby ester linkages are formed resulting in a branched oligomer backbone, and combinations thereof; (b) at least one unit which is a terephthaloyl moiety; and (c) at least one unsulfonated unit which is a 1 ,2-oxyalkyleneoxy moiety; and (2) one or more capping units selected from nonionic capping units, anionic capping units such as alkoxylated, preferably ethoxylated, isethionates, alkoxylated propanesulfonates, alkoxylated propanedisulfonates, alkoxylated phenolsulfonates, sulfoaroyl derivatives and mixtures thereof. Preferred are esters of the empirical formula: {(CAP)x(EG/PG)y'(DEG)y"(PEG)y"'(T)z(SIP)z , (SEG)q(B)m} wherein CAP, EG/PG, PEG, T and SIP are as defined as terephthaloyl (T), sulfoisophthaloyl (SIP), oxyethyleneoxy and oxy- 1,2-propylene (EG/PG) units, end-caps (CAP), poly(ethyleneglycol) (PEG), (DEG) represents di(oxyethylene)oxy units, (SEG) represents units derived from the sulfoethyl ether of glycerin and related moiety units, (B) represents branching units which are at least trifunctional whereby ester linkages are formed resulting in a branched oligomer backbone, x is from about 1 to about 12, y' is from about 0.5 to about 25, y" is from 0 to about 12, y'" is from 0 to about 10, y'+y"+y"' totals from about 0.5 to about 25, z is from about 1.5 to about 25, z' is from 0 to about 12; z + z' totals from about 1.5 to about 25, q is from about 0.05 to about 12; m is from about 0.01 to about 10, and x, y', y", y'", z, z', q and m represent the average number of moles ofthe corresponding units per mole of said ester and said ester has a molecular weight ranging from about 500 to about 5,000. Preferred SEG and CAP monomers for the above esters include Na-2-(2-,3- dihydroxypropoxy)ethanesulfonate ("SEG"), Na-2-{2-(2-hydroxyethoxy) ethoxy} ethanesulfonate ("SE3") and its homologs and mixtures thereof and the products of ethoxylating and sulfonating allyl alcohol. Preferred SRA esters in this class include the product of transesterifying and oligomerizing sodium 2-{2-(2-hydroxy- ethoxy)ethoxy} ethanesulfonate and/or sodium 2-[2-{2-(2-hydroxyethoxy)ethoxy}- ethoxy]ethanesulfonate, DMT, sodium 2-(2,3-dihydroxypropoxy) ethane sulfonate, EG, and PG using an appropriate Ti(IV) catalyst and can be designated as (CAP)2(T)5(EG/PG)1.4(SEG)2.5(B)0.13 wherein CAP is (Na+-O3S[CH2CH2O]3.5)- and B is a unit from glycerin and the mole ratio EG/PG is about 1.7: 1 as measured by conventional gas chromatography after complete hydrolysis. Preferred non-cotton soil release agent - B. A second preferred class of suitable SRA's include a sulfonated product of a substantially linear ester oligomer comprised of an oligomeric ester backbone of terephthaloyl and oxyalkyleneoxy repeat units and allyl- derived sulfonated terminal moieties covalently attached to the backbone Such ester oligomers can be prepared by: (a) ethoxylating allyl alcohol; (b) reacting the product of (a) with dimethyl terephthalate ("DMT") and 1,2-propylene glycol ("PG") in a two-stage transesterification/oligomerization procedure; and (c) reacting the product of (b) with sodium metabisulfite in water. Suitable for use in the laundry detergent compositions ofthe present invention are preferred non-cotton soil release polymers comprising: a) one or two terminal units selected from the group consisting of i) -(CH2) q (CHSθ3M)CH 2 SO 3 M, ii) -(CH2)q(CHSO 2 M)CH 2 SO3M, iii) -CH2CH2SO3M, iv) and mixtures thereof; wherein q has the value from 1 to about 4, M is a water soluble cation, preferably sodium; b) a backbone comprising: i) arylene units, preferably terephthalate units having the formula: ii) ethyleneoxy units having the formula: — O(CH 2 CH 2 O)nCH 2 CH 2 O— wherein the value of n is from about 1 to about 20; and iii) 1,2-propyleneoxy units having the formula: — O(CH 2 CH(CH 3 P)nCH 2 CH(CH 3 )O— wherein the value of n is from about 1 to about 20, and wherein further the preferred backbone of this preferred non-cotton soil release polymer has a backbone comprising arylene repeat units which alternate with the ethyleneoxy and 1 ,2-propyleneoxy units, such that the mole ratio of ethyleneoxy to 1,2-propyleneoxy units is from 0:1 to about 0.9:0.1, preferably from about 0:1 to about 0.4:0.6, more preferably the arylene units alternate with essentially 1 ,2-propyleneoxy units. However, other combinations ofthe above-identified units may be used to form non-cotton soil release polymers suitable for use in the compositions of the present invention. These combinations are more thoroughly described in U.S. Patent 4,968,451 , Scheibel et al., issued November 6, 1990 and incoφorated herein by reference. Preferred non-cotton soil release agent - C. Suitable for use in the laundry detergent compositions ofthe present invention are preferred non-cotton soil release polymers having the formula (Cap)[(A-R 1 -A-R 2 ) u (A-R 3 -A-R2) v -A-R4-A-](Cap) wherein A is a carboxy linking moiety, preferably A is a carboxy linking moiety having the formula 0 O I I I I O-C— n ,r — C— O— Rl is an arylene moiety, preferably 1,4-phenylene moiety having the formula wherein for Rl moieties, the degree of partial substitution with arylene moieties other than 1,4-phenylene should be such that the soil release properties ofthe compound are not adversely affected to any great extent. Generally, the partial substitution which can be tolerated will depend upon the backbone length ofthe compound. R2 moieties are ethylene moieties or substituted ethylene moieties having C1-C4 alkyl or alkoxy substituents. As used herein, the term "the R2 moieties are essentially ethylene moieties or substituted ethylene moieties having C1 -C4 alkyl or alkoxy substituents" refers to compounds ofthe present invention where the R2 moieties consist entirely of ethylene or substituted ethylene moieties or a partially substituted with other compatible moieties. Examples of these other moieties include 1,3-propylene, 1,4- butylene, 1,5-pentylene, or 1,6-hexylene, 1 ,2-hydroxyalkylenes and oxyalkylenes. For the R2 moieties, the degree of partial substitution with these other moieties should be such that the soil release properties ofthe compounds are not adversely affected to any great extent. For example, for polyesters made according to the present invention with a 75:25 mole ratio of diethylene glycol (-CH2CH2OCH2CH2-) to ethylene glycol (ethylene) have adequate soil release activity. For the R 3 moieties, suitable substituted C2-C1 g hydrocarbyl ene moieties can include substituted C2-C12 alkylene, alkenylene, arylene, alkarylene and like moieties, The substituted alkylene or alkenylene moieties can be linear, branched or cyclic, also, the R 3 can all be the same (e.g. all substituted arylene) or a mixture (e.g. a mixture of substituted arylenes and substituted alkylenes). Preferred R 3 moieties are those which are substituted 1,3-phenylene, preferably 5-sulfo- 1,3-phenylene. R 3 moieties are also - A-[(R 2 -A-R 4 )]-Cap wherein R 4 is R 1 , R 3 , and mixtures thereof. The preferred (Cap) moieties comprise units having the formula wherein R^ is C1-C4 alkylene, or the moiety -R2-A-R6- wherein R*> is C2-C 12 alkylene, alkenylene, arylene or alkarylene moiety, X is Ci -C4 alkyl, preferably methyl; the indices m and n are such that the moiety -CH2CH2O- comprises at least 50% by weight ofthe moiety provided that when R^ is the moiety -R2-A-R6- , m is at least 1 ; each n is at least about 10, the indices u and v are such that the sum of u + v is from about 3 to about 25; the index w is 0 or at least 1 ; and when w is at least 1 , the indices u, v and w have the values such that the sum of u + v + w is from about 3 to about 25. An example of this type of non-cotton soil release block polyester has the formula O r, — λ O O O O O X-(OCH 2 CH 2 )n-(OC— <f Y- CO-R2) u — (OC-R 3 -CO-R 2 ) v -OC-R4-CO-(CH 2 CH 2 0) n X wherein the R 2 moieties are essentially ethylene moieties, 1,2-propylene moieties, and mixtures thereof; the R 3 moieties are all potassium or preferably sodium 5-sulfo- 1,3- phenylene moieties; the R 4 moieties are Rl or R 3 moieties, or mixtures thereof; each X is ethyl, methyl, preferably methyl; each n is from about 12 to about 43; when w is 0, u + v is from about 3 to about 10; when w is at least 1, u + v + w is from about 3 to about 10. The above non-cotton soil release polymers ofthe formula (Cap)[(A-R 1 -A-R 2 ) u (A-R 3 -A-R 2 ) v -A-R 4 -A-](Cap) are further described in detail in U.S. Patent 4,702,857, Gosselink, issued October 27, 1987 and incoφorated herein by reference. Preferred non-cotton soil release agent - D: A further preferred non-cotton soil release agent according to the present invention comprises: at least about 10% by weight of a substantially linear sulfonated poly- ethoxy/propoxy end-capped ester having molecular weight ranging from about 500 to about 8,000; said ester consisting essentially of on a molar basis: i) from about 1 to about 2 moles of sulfonated poly ethoxy/propoxy end-capping units ofthe formula: (MSO 3 )(CH2)m(CH 2 CH2θ)(RO) n - wherein M is a salt-forming cation such as sodium of tertraalkylammonium, m is 0 or 1 , R is ethylene, propylene, and mixtures thereof; and n is fro 0 to 2; and mixtures thereof; ii) from about 0.5 to about 66 moles of units selected from the group consisting of: a) oxyethyleneoxy units; b) a mixture of oxyethyleneoxy and oxy- 1 ,2,-propy leneoxy units wherein said oxyethyleneoxy units are present in an oxyethyleneoxy of oxy- 1,2-propyleneoxy mole ratio ranging from 0.5: 1 to about 10: 1 ; and c) a mixture of a) or b) with poly(oxyethylene)oxy units have a degree of polymerization of from 2 to 4; provided that when said poly (oxy ethylene)oxy units have a degree of polymerization of 2, the mole ratio of poly(oxyethylene)oxy units to total group ii) units ranges fro 0:1 to 0.33:1 ; and when said poly(oxyethylene)oxy units have a degree of polymerization of 3; the mole ration of poly(oxyethylene)oxy units to total group ii) units ranges from 0: 1 to about 0.22: 1 ; and when said poly(oxyethylene)oxy units have a degree of polymerization equal to 4, the mole ratio of poly(oxyethylene)oxy units to total group ii) units ranges from 0:1 to about 0.14:1; iii) from about 1.5 to about 40 moles of terephthaloyl units; and iv) from 0 to about 26 moles of 5-sulphophthaloyl units of the formula: -(O)C(C 6 H3)(S0 3 M)C(O)- wherein M is a salt forming cation; and B) from about 0.5% to about 20% by weight of ester, of one or more crystallization-reducing stabilizers. Preferably, such materials are used at a level of from about 0.1% to about 4%, more preferably from about 0.4% to about 2%. Stabilizers useful in this invention should be water soluble or water dispersible. The stabilizing agents that are useful herein include sulfonate-type hydrotropes, linear or branched alkylbenzenesulfonates, paraffin sulfonates, and other thermally-stable alkyl sulfonate variations with from about 4 to about 20 carbon atoms. Preferred agents include sodium dodecylbenzenesulfonate, sodium cumenesulfonate, sodium toluenesulfonate, sodium xylenesulfonate, and mixtures thereof. When higher levels of stabilizers are used, mixtures of hydrotropes and/or other stabilizers are preferred over pure components to insure full integration into the oligomer and to reduce the possibility of crystallization ofthe stabilizer. In general, the level of such agents should be kept as low as possible while providing the primary benefit, i.e., the reduction in the amount of crystallization that the soil release agent undergoes during manufacture, storage and when introduced to the wash liquor, the composition may comprise from about 0.5% to about 20% stabilizer. Most preferably, these ester compositions comprise an amount sufficient to reduce the crystallization ofthe oligomer during manufacture and when introduced to the wash liquor, i.e., at least 3% by weight. In addition to the above-described non-cotton soil release polymers, other soil release polymers suitable for use in the liquid laundry detergent compositions ofthe present invention include the following. Such known polymeric soil release agents can optionally be employed in the present detergent compositions. If utilized, SRA's will generally comprise from 0.01% to 10.0%, typically from 0.1% to 5%, preferably from 0.2% to 3.0% by weight, ofthe compositions. Preferred SRA's typically have hydrophilic segments to hydrophilize the surface of hydrophobic fibers such as polyester and nylon, and hydrophobic segments to deposit upon hydrophobic fibers and remain adhered thereto through completion of washing and rinsing cycles, thereby serving as an anchor for the hydrophilic segments. This can enable stains occurring subsequent to treatment with the SRA to be more easily cleaned in later washing procedures. SRA's can include a variety of charged, e.g., anionic or even cationic species, see U.S. 4,956,447, issued September 11, 1990 to Gosselink, et al., as well as noncharged monomer units, and their structures may be linear, branched or even star-shaped. They may include capping moieties which are especially effective in controlling molecular weight or altering the physical or surface-active properties. Structures and charge distributions may be tailored for application to different fiber or textile types and for varied detergent or detergent additive products. Preferred SRA's include oligomeric terephthalate esters, typically prepared by processes involving at least one transesterification/oligomerization, often with a metal catalyst such as a titanium(IV) alkoxide. Such esters may be made using additional monomers capable of being incoφorated into the ester structure through one, two, three, four or more positions, without, of course, forming a densely crosslinked overall structure. Other SRA's include the nonionic end-capped 1 ,2-propylene/polyoxyethylene terephthalate polyesters of U.S. 4,711,730, December 8, 1987 to Gosselink et al., for example those produced by transesterification/oligomerization of poly(ethyleneglycol) methyl ether, DMT, PG and poly(ethyleneglycol) ("PEG"). Other examples of SRA's include: the partly- and fully- anionic-end-capped oligomeric esters of U.S. 4,721 ,580, January 26, 1988 to Gosselink, such as oligomers from ethylene glycol ("EG"), PG, DMT and Na-3,6-dioxa-8-hydroxyoctanesulfonate; and the anionic, especially sulfoaroyl, end-capped terephthalate esters of U.S. 4,877,896, October 31 , 1989 to Maldonado, the latter being typical of SRA's useful in both laundry and fabric conditioning products, an example being an ester composition made from m- sulfobenzoic acid monosodium salt, PG and DMT, optionally but preferably further comprising added PEG, e.g., PEG 3400. SRA's also include: simple copolymeric blocks of ethylene terephthalate or propylene terephthalate with polyethylene oxide or polypropylene oxide terephthalate, see U.S. 3,959,230 to Hays, May 25, 1976 and U.S. 3,893,929 to Basadur, July 8, 1975; cellulosic derivatives such as the hydroxy ether cellulosic polymers available as METHOCEL from Dow; the C1-C4 alkyl celluloses and C4 hydroxyalkyl celluloses, see U.S. 4,000,093, December 28, 1976 to Nicol, et al.; and the methyl cellulose ethers having an average degree of substitution (methyl) per anhydroglucose unit from about 1.6 to about 2.3 and a solution viscosity of from about 80 to about 120 centipoise measured at 20°C as a 2% aqueous solution. Such materials are available as METOLOSE SMI 00 and METOLOSE SM200, which are the trade names of methyl cellulose ethers manufactured by Shin-etsu Kagaku Kogyo KK. Suitable SRA's characterised by poly(vinyl ester) hydrophobe segments include graft copolymers of poly(vinyl ester), e.g., Cj-Cβ vinyl esters, preferably poly(vinyl acetate), grafted onto polyalkylene oxide backbones. See European Patent Application 0 219 048, published April 22, 1987 by Kud, et al. Commercially available examples include SOKALAN SRA's such as SOKALAN HP-22, available from BASF, Germany. Other SRA's are polyesters with repeat units containing 10-15% by weight of ethylene terephthalate together with 80-90% by weight of polyoxyethylene terephthalate derived from a polyoxyethylene glycol of average molecular weight 300-5,000. Commercial examples include ZELCON 5126 from Dupont and MILEASE T from ICI. Another preferred SRA is an oligomer having empirical formula (CAP)2(EG/PG)5(T) 5 (SIP)ι which comprises terephthaloyl (T), sulfoisophthaloyl (SIP), oxyethyleneoxy and oxy- 1,2-propylene (EG/PG) units and which is preferably terminated with end-caps (CAP), preferably modified isethionates, as in an oligomer comprising one sulfoisophthaloyl unit, 5 terephthaloyl units, oxyethyleneoxy and oxy- 1,2-propyleneoxy units in a defined ratio, preferably about 0.5:1 to about 10:1 , and two end-cap units derived from sodium 2-(2-hydroxyethoxy)-ethanesulfonate. Said SRA preferably further comprises from 0.5% to 20%, by weight ofthe oligomer, of a crystallinity-reducing stabilizer, for example an anionic surfactant such as linear sodium dodecylbenzenesulfonate or a member selected from xylene-, cumene-, and toluene- sulfonates or mixtures thereof, these stabilizers or modifiers being introduced into the synthesis vessel, all as taught in U.S. 5,415,807, Gosselink, Pan, Kellett and Hall, issued May 16, 1995. Suitable monomers for the above SRA include Na-2-(2-hydroxyethoxy)- ethanesulfonate, DMT, Na-dimethyl-5-sulfoisophthalate, EG and PG. Additional classes of SRA's include: (I) nonionic terephthalates using diisocyanate coupling agents to link polymeric ester structures, see U.S. 4,201,824, Violland et al. and U.S. 4,240,918 Lagasse et al.; and (II) SRA's with carboxylate terminal groups made by adding trimellitic anhydride to known SRA's to convert terminal hydroxyl groups to trimellitate esters. With the proper selection of catalyst, the trimellitic anhydride forms linkages to the terminals ofthe polymer through an ester of the isolated carboxylic acid of trimellitic anhydride rather than by opening ofthe anhydride linkage. Either nonionic or anionic SRA's may be used as starting materials as long as they have hydroxyl terminal groups which may be esterified. See U.S. 4,525,524 Tung et al.. Other classes include: (III) anionic terephthalate-based SRA's ofthe urethane-linked variety, see U.S. 4,201,824, Violland et al.; (IV) poly(vinyl caprolactam) and related co-polymers with monomers such as vinyl pyrrolidone and/or dimethylaminoethyl methacrylate, including both nonionic and cationic polymers, see U.S. 4,579,681, Ruppert et al.; (V) graft copolymers, in addition to the SOKALAN types from BASF, made by grafting acrylic monomers onto sulfonated polyesters. These SRA's assertedly have soil release and anti-redeposition activity similar to known cellulose ethers: see EP 279,134 A, 1988, to Rhone-Poulenc Chemie. Still other classes include: (VI) grafts of vinyl monomers such as acrylic acid and vinyl acetate onto proteins such as caseins, see EP 457,205 A to BASF (1991 ); and (VII) polyester- polyamide SRA's prepared by condensing adipic acid, caprolactam, and polyethylene glycol, especially for treating polyamide fabrics, see Bevan et al., DE 2,335,044 to Unilever N. V., 1974. Other useful SRA's are described in U.S. Patents 4,240,918, 4,787,989 and 4,525,524. Any other anionic non-cotton soil release agent is suitable for use in the compositions ofthe present invention alone or in combination, except for carboxy - methylcellulose (CMC) which according to the present invention when used alone is used at a level above 0.2%, and preferably above 0.5%. Preferably, CMC is used at a level of from about 1% to about 10%, preferably from about 1% to about 6%, more preferably about 5%. Cotton Soil Release Agents The cotton soil release agents ofthe present invention are water-soluble or dispersible, modified polyamines. These polyamines comprise backbones that can be either linear or cyclic. The polyamine backbones can also comprise polyamine branching chains to a greater or lesser degree. In general, the polyamine backbones described herein are modified in such a manner that each nitrogen ofthe polyamine chain is thereafter described in terms of a unit that is substituted, quaternized, oxidized, or combinations thereof. For the puφoses ofthe present invention the term "modification" is defined as replacing a backbone -NH hydrogen atom by an E unit (substitution), quaternizing a backbone nitrogen (quaternized) or oxidizing a backbone nitrogen to the N-oxide (oxidized). The terms "modification" and "substitution" are used interchangably when referring to the process of replacing a hydrogen atom attached to a backbone nitrogen with an E unit. Quaternization or oxidation may take place in some circumstances without substitution, but preferably substitution is accompanied by oxidation or quaternization of at least one backbone nitrogen. The linear or non-cyclic polyamine backbones that comprise the cotton soil release agents ofthe present invention have the general formula: ¥ i [HzN-RJn+i -[N-R] m -[N-R] n -NH 2 said backbones prior to subsequent modification, comprise primary, secondary and tertiary amine nitrogens connected by R "linking" units. The cyclic polyamine backbones comprising the cotton soil release agents of the present invention have the general formula: I H | R [H 2 N-R]n-k+r-[N-R] m -[N-R]n-[N-R]k-NH 2 said backbones prior to subsequent modification, comprise primary, secondary and tertiary amine nitrogens connected by R "linking" units For the puφose ofthe present invention, primary amine nitrogens comprising the backbone or branching chain once modified are defined as V or Z "terminal" units. For example, when a primary amine moiety, located at the end ofthe main polyamine backbone or branching chain having the structure H 2 N-R]- is modified according to the present invention, it is thereafter defined as a V "terminal" unit, or simply a V unit. However, for the puφoses ofthe present invention, some or all ofthe primary amine moieties can remain unmodified subject to the restrictions further described herein below. These unmodified primary amine moieties by virtue of their position in the backbone chain remain "terminal" units. Likewise, when a primary amine moiety, located at the end ofthe main polyamine backbone having the structure -NH2 is modified according to the present invention, it is thereafter defined as a Z "terminal" unit, or simply a Z unit. This unit can remain unmodified subject to the restrictions further described herein below. In a similar manner, secondary amine nitrogens comprising the backbone or branching chain once modified are defined as W "backbone" units. For example, when a secondary amine moiety, the major constituent ofthe backbones and branching chains of the present invention, having the structure H — [N-R]— is modified according to the present invention, it is thereafter defined as a W "backbone" unit, or simply a W unit. However, for the puφoses ofthe present invention, some or all ofthe secondary amine moieties can remain unmodified. These unmodified secondary amine moieties by virtue of their position in the backbone chain remain "backbone" units. In a further similar manner, tertiary amine nitrogens comprising the backbone or branching chain once modified are further referred to as Y "branching" units. For example, when a tertiary amine moiety, which is a chain branch point of either the polyamine backbone or other branching chains or rings, having the structure I — [N-R]- is modified according to the present invention, it is thereafter defined as a Y "branching" unit, or simply a Y unit. However, for the puφoses ofthe present invention, some or all or the tertiary amine moieties can remain unmodified. These unmodified tertiary amine moieties by virtue of their position in the backbone chain remain "branching" units. The R units associated with the V, W and Y unit nitrogens which serve to connect the polyamine nitrogens, are described herein below. The final modified structure ofthe polyamines ofthe present invention can be therefore represented by the general formula V(n+l)W m Y n Z for linear polyamine cotton soil release polymers and by the general formula V(n-k+l)W m Y n Y'kZ for cyclic polyamine cotton soil release polymers. For the case of polyamines comprising rings, a Y' unit ofthe formula • I R -[N-R]— serves as a branch point for a backbone or branch ring. For every Y' unit there is a Y unit having the formula I — [N-R]- that will form the connection point ofthe ring to the main polymer chain or branch. In the unique case where the backbone is a complete ring, the polyamine backbone has the formula ¥ i [H 2 N-R] n -[N-R] m -[N-R] n - therefore comprising no Z terminal unit and having the formula v n -kw m γ n γ'k wherein k is the number of ring forming branching units. Preferably the polyamine backbones ofthe present invention comprise no rings. In the case of non-cyclic polyamines, the ratio ofthe index n to the index m relates to the relative degree of branching. A fully non-branched linear modified polyamine according to the present invention has the formula vw m z that is, n is equal to 0. The greater the value of n (the lower the ratio of m to n), the greater the degree of branching in the molecule. Typically the value for m ranges from a minimum value of 4 to about 400, however larger values of m, especially when the value ofthe index n is very low or nearly 0, are also preferred. Each polyamine nitrogen whether primary, secondary or tertiary, once modified according to the present invention, is further defined as being a member of one of three general classes; simple substituted, quaternized or oxidized. Those polyamine nitrogen units not modified are classed into V, W, Y, or Z units depending on whether they are primary, secondary or tertiary nitrogens. That is unmodified primary amine nitrogens are V or Z units, unmodified secondary amine nitrogens are W units and unmodified tertiary amine nitrogens are Y units for the puφoses ofthe present invention. Modified primary amine moieties are defined as V "terminal" units having one of three forms: a) simple substituted units having the structure: E— N-R — I E b) quaternized units having the structure: E-N-R — I E wherein X is a suitable counter ion providing charge balance; and c) oxidized units having the structure: O E-N t-R — Modified secondary amine moieties are defined as W "backbone" units having one of three forms: a) simple substituted units having the structure: -N I -R— E b) quaternized units having the structure: wherein X is a suitable counter ion providing charge balance; and c) oxidized units having the structure: Modified tertiary amine moieties are defined as Y "branching" units having one of three forms: a) unmodified units having the structure: -N-R— I b) quaternized units having the structure: wherein X is a suitable counter ion providing charge balance; and c) oxidized units having the structure: O -N t— R- Certain modified primary amine moieties are defined as Z "terminal" units having one of three forms: a) simple substituted units having the structure: —N I -E E b) quaternized units having the structure: wherein X is a suitable counter ion providing charge balance; and c) oxidized units having the structure: When any position on a nitrogen is unsubstituted of unmodified, it is understood that hydrogen will substitute for E. For example, a primary amine unit comprising one E unit in the form of a hydroxyethyl moiety is a V terminal unit having the formula (HOCH 2 CH 2 )HN-. For the piuposes ofthe present invention there are two types of chain terminating units, the V and Z units. The Z "terminal" unit derives from a terminal primary amino moiety ofthe structure -NH2. Non-cyclic polyamine backbones according to the present invention comprise only one Z unit whereas cyclic polyamines can comprise no Z units. The Z "terminal" unit can be substituted with any ofthe E units described further herein below, except when the Z unit is modified to form an N-oxide. In the case where the Z unit nitrogen is oxidized to an N-oxide, the nitrogen must be modified and therefore E cannot be a hydrogen. The polyamines ofthe present invention comprise backbone R "linking" units that serve to connect the nitrogen atoms ofthe backbone. R units comprise units that for the puφoses ofthe present invention are referred to as "hydrocarbyl R" units and "oxy R" units. The "hydrocarbyl" R units are C2-C12 alkylene, C4-C12 alkenylene, C3-C12 hydroxyalkylene wherein the hydroxyl moiety may take any position on the R unit chain except the carbon atoms directly connected to the polyamine backbone nitrogens; C4- C j2 dihydroxyalkylene wherein the hydroxyl moieties may occupy any two ofthe carbon atoms of the R unit chain except those carbon atoms directly connected to the polyamine backbone nitrogens; Cg-Ci2 dialkylarylene which for the puφose ofthe present invention are arylene moieties having two alkyl substituent groups as part ofthe linking chain. For example, a dialkylarylene unit has the formula although the unit need not be 1 ,4-substituted, but can also be 1 ,2 or 1 ,3 substituted C 2 - C 12 alkylene, preferably ethylene, 1,2-propylene, and mixtures thereof, more preferably ethylene. The "oxy" R units comprise -(R i O) x R 5 (OR 1 ) x -, CH 2 CH(OR 2 )CH 2 O) z (R 1 O) y R>(OCH 2 CH(OR 2 )CH 2 ) w -, -CH 2 CH(OR 2 )CH 2 -, (R1 O) X R!-, and mixtures thereof. Preferred R units are C2-C12 alkylene, C3-C12 hydroxyalkylene, C4-C \ 2 dihydroxyalkylene, C g-C 12 dialkylarylene, -(R 10) x R 1 -, - CH 2 CH(OR2)CH 2 -, -(CH 2 CH(OH)CH 2 O) z (R * OfyR 1 (OCH 2 CH-(OH)CH2)w-> - (R1O) X R5(OR1 ) X -, more preferred R units are C2-C12 alkylene, C3-C12 hydroxy¬ alkylene, C4-C12 dihydroxyalkylene, -(R^^R 1 -, -(R 1 O) x R 5 (OR 1 ) x -, (CH 2 CH(OH)CH2θ) z (R 1 O) y R 1 (OCH2CH-(OH)CH2) w -. and mixtures thereof, even more preferred R units are C2-C12 alkylene, C3 hydroxyalkylene, and mixtures thereof, most preferred are C2-Cg alkylene. The most preferred backbones ofthe present invention comprise at least 50% R units that are ethylene. Rl units are C2-Cβ alkylene, and mixtures thereof, preferably ethylene. R 2 is hydrogen, and -(Rlθ) x B, preferably hydrogen. R 3 is Ci-Cig alkyl, C7-C12 arylalkylene, C7-C12 alkyl substituted aryl, Cg-C^ aryl, and mixtures thereof , preferably C1-C12 alkyl, C7-C12 arylalkylene, more preferably C1-C12 alkyl, most preferably methyl. R 3 units serve as part of E units described herein below. R4 is C1 -C12 alkylene, C4-C12 alkenylene, Cg-Ci2 arylalkylene, C6-C10 arylene, preferably CI -C JQ alkylene, Cg-Cj2 arylalkylene, more preferably C2-Cg alkylene, most preferably ethylene or butylene. R^ is C1-C12 alkylene, C3-C12 hydroxyalkylene, C4-C12 dihydroxyalkylene, Cg-C 12 dialkylarylene, -C(O)-, -C(O)NHR6NHC(O)-, -C(O)(R 4 ) r C(O)-, -R 1 (OR 1 )-, -CH 2 CH(OH)CH 2 O(R 1 0) y Rl OCH 2 CH(OH)CH 2 -, -C(O)(R 4 ) r C(O)-, -CH 2 CH(OH)CH 2 -, R 5 is preferably ethylene, -C(O)-, -C(O)NHR6NHC(O)-, -R 1 (OR 1 )-, -CH2CH(OH)CH2-, -CH2CH(OH)CH 2 O(R 1 O) y R 1 OCH2CH-(OH)CH2-, more preferably -CH 2 CH(OH)CH 2 -. R6 is C2-C12 alkylene or C6-C12 arylene. The preferred "oxy" R units are further defined in terms ofthe Rl, R 2 , and R^ units. Preferred "oxy" R units comprise the preferred Rl, R 2 , and R^ units. The preferred cotton soil release agents ofthe present invention comprise at least 50% Rl units that are ethylene. Preferred Rl, R 2 , and R^ units are combined with the "oxy" R units to yield the preferred "oxy" R units in the following manner. i) Substituting more preferred R 5 into -(CH2CH2O) x R 5 (OCH2CH2) x - yields -(CH 2 CH 2 O) x CH2CHOHCH2(OCH2CH2) x -. ii) Substituting preferred R 1 and R 2 into -(CH 2 CH(OR 2 )CH 2 O) z - (R'O) y R 1 O(CH 2 CH(OR 2 )CH 2 ) w - yields -(CH 2 CH(OH)CH 2 O) z - (CH 2 CH 2 O) y CH 2 CH 2 O(CH 2 CH(OH)CH 2 ) w -. iii) Substituting preferred R 2 into -CH 2 CH(OR 2 )CH 2 - yields -CH 2 CH(OH)CH 2 -. E units are selected from the group consisting of hydrogen, C1 -C22 alkyl, C3- C 2 2 alkenyl, C7-C22 arylalkyl, C2-C22 hydroxyalkyl, -(CH2) p CO2M, -(CH 2 ) q SO3M, - CH(CH2CO 2 M)CO2M, -(CH 2 ) p PO3M, -(Rlθ) m B, -C(O)R 3 , preferably hydrogen, C 2 - C22 hydroxyalkylene, benzyl, Cι-C 2 2 alkylene, -(Rlθ) m B, -C(O)R 3 , -(CH2) p CO2M, - (CH2) q SO3M, -CH(CH2CO2M)CO2M, more preferably C 1 -C22 alkylene, -(R 10) x B, -C(O)R 3 , -(CH 2 ) p CO 2 M, -(CH 2 ) q SO 3 M, -CH(CH 2 CO 2 M)CO2M, most preferably C 1 -C22 alkylene, -(R 10) x B, and -C(O)R 3 . When no modification or substitution is made on a nitrogen then hydrogen atom will remain as the moiety representing E. E units do not comprise hydrogen atom when the V, W or Z units are oxidized, that is the nitrogens are N-oxides. For example, the backbone chain or branching chains do not comprise units ofthe following structure: O O O Additionally, E units do not comprise carbonyl moieties directly bonded to a nitrogen atom when the V, W or Z units are oxidized, that is, the nitrogens are N-oxides. According to the present invention, the E unit -C(O)R 3 moiety is not bonded to an N- oxide modified nitrogen, that is, there are no N-oxide amides having the structure O O O t 9 t t 9 — N— R or R 3 -C— N— R or — N~ C-R 3 I I I C=O E E R 3 or combinations thereof. B is hydrogen, Cj-C 6 alkyl, -(CH 2 ) q SO3M, -(CH 2 ) p CO 2 M, -(CH 2 ) q - (CHSO 3 M)CH 2 SO3M, -(CH 2 ) q (CHSO 2 M)CH2SO3M, -(CH 2 ) p PO 3 M, -PO 3 M, preferably hydrogen, -(CH 2 ) q SO3M, -(CH2) q (CHSO 3 M)CH2Sθ3M, -(CH 2 ) q - (CHSO2M)CH2SO3M, more preferably hydrogen or -(CH2) q SO3M. M is hydrogen or a water soluble cation in sufficient amount to satisfy charge balance. For example, a sodium cation equally satisfies -(CH2)pCO2M, and (CH2)qSO3M, thereby resulting in -(CH2) p CO2Na, and -(CH2) q SO3Na moieties. More than one monovalent cation, (sodium, potassium, etc.) can be combined to satisfy the required chemical charge balance. However, more than one anionic group may be charge balanced by a divalent cation, or more than one mono- valent cation may be necessary to satisfy the charge requirements of a poly-anionic radical. For example, a - (CH2)pPO3M moiety substituted with sodium atoms has the formula -(CH2)pPO3Na3. Divalent cations such as calcium (Ca 2"1" ) or magnesium (Mg 2+ ) may be substituted for or combined with other suitable mono-valent water soluble cations. Preferred cations are sodium and potassium, more preferred is sodium. X is a water soluble anion such as chlorine (Cl"), bromine (Br) and iodine (I") or X_can be any negatively charged radical such as sulfate (SO4 2 ") and methosulfate (CH3SO3-). The formula indices have the following values: p has the value from 1 to 6, q has the value from 0 to 6; r has the value 0 or 1 ; w has the value 0 or 1 , x has the value from 1 to 100; y has the value from 0 to 100; z has the value 0 or 1 ; k is less than or equal to the value of n; m has the value from 4 to about 400, n has the value from 0 to about 200; m + n has the value of at least 5. The preferred cotton soil release agents of the present invention comprise polyamine backbones wherein less than about 50% ofthe R groups comprise "oxy" R units, preferably less than about 20% , more preferably less than 5%, most preferably the R units comprise no "oxy" R units. The most preferred cotton soil release agents which comprise no "oxy" R units comprise polyamine backbones wherein less than 50% ofthe R groups comprise more than 3 carbon atoms. For example, ethylene, 1,2-propylene, and 1,3-propylene comprise 3 or less carbon atoms and are the preferred "hydrocarbyl" R units. That is when backbone R units are C 2 -C ]2 alkylene, preferred is C 2 -C 3 alkylene, most preferred is ethylene. The cotton soil release agents ofthe present invention comprise modified homogeneous and non-homogeneous polyamine backbones, wherein 100% or less ofthe -NH units are modified. For the puφose ofthe present invention the term "homogeneous polyamine backbone" is defined as a polyamine backbone having R units that are the same (i.e., all ethylene). However, this sameness definition does not exclude polyamines that comprise other extraneous units comprising the polymer backbone which are present due to an artifact ofthe chosen method of chemical synthesis. For example, it is known to those skilled in the art that ethanolamine may be used as an "initiator" in the synthesis of polyethyleneimines, therefore a sample of polyethyleneimine that comprises one hydroxyethyl moiety resulting from the polymerization "initiator" would be considered to comprise a homogeneous polyamine backbone for the piuposes ofthe present invention. A polyamine backbone comprising all ethylene R units wherein no branching Y units are present is a homogeneous backbone. A polyamine backbone comprising all ethylene R units is a homogeneous backbone regardless ofthe degree of branching or the number of cyclic branches present. For the puφoses ofthe present invention the term "non-homogeneous polymer backbone" refers to polyamine backbones that are a composite of various R unit lengths and R unit types. For example, a non-homogeneous backbone comprises R units that are a mixture of ethylene and 1,2-propylene units. For the puφoses ofthe present invention a mixture of "hydrocarbyl" and "oxy" R units is not necessary to provide a non- homogeneous backbone. The proper manipulation of these "R unit chain lengths" provides the formulator with the ability to modify the solubility and fabric substantivity ofthe cotton soil release agents ofthe present invention. Preferred cotton soil release polymers ofthe present invention comprise homogeneous polyamine backbones that are totally or partially substituted by polyethyleneoxy moieties, totally or partially quaternized amines, nitrogens totally or partially oxidized to N-oxides, and mixtures thereof. However, not all backbone amine nitrogens must be modified in the same manner, the choice of modification being left to the specific needs ofthe formulator. The degree of ethoxylation is also determined by the specific requirements of the formulator. The preferred polyamines that comprise the backbone ofthe compounds ofthe present invention are generally polyalkyleneamines (PAA's), polyalkyleneimines (PAI's), preferably polyethyleneamine (PEA's), polyethyleneimines (PEI's), or PEA's or PEI's connected by moieties having longer R units than the parent PAA's, PAI's, PEA's or PEI's. A common polyalkyleneamine (PAA) is tetrabutylenepentamine. PEA's are obtained by reactions involving ammonia and ethylene dichloride, followed by fractional distillation. The common PEA's obtained are triethylenetetramine (TETA) and teraethylenepentamine (TEPA). Above the pentamines, i.e., the hexamines, heptamines, octamines and possibly nonamines, the cogenerically derived mixture does not appear to separate by distillation and can include other materials such as cyclic amines and particularly piperazines. There can also be present cyclic amines with side chains in which nitrogen atoms appear. See U.S. Patent 2,792,372, Dickinson, issued May 14, 1957, which describes the preparation of PEA's. Preferred amine polymer backbones comprise R units that are C2 alkylene (ethylene) units, also known as polyethylenimines (PEI's). Preferred PEI's have at least moderate branching, that is the ratio of m to n is less than 4:1, however PEI's having a ratio of m to n of about 2:1 are most preferred. Preferred backbones, prior to modification have the general formula: " I [H 2 NCH 2 CH 2 ]n-[NCH 2 CH 2 ] m -[NCH 2 CH 2 ] n -NH 2 wherein m and n are the same as defined herein above. Preferred PEI's, prior to modification, will have a molecular weight greater than about 200 daltons. The relative proportions of primary, secondary and tertiary amine units in the polyamine backbone, especially in the case of PEI's, will vary, depending on the manner of preparation. Each hydrogen atom attached to each nitrogen atom ofthe polyamine backbone chain represents a potential site for subsequent substitution, quaternization or oxidation. These polyamines can be prepared, for example, by polymerizing ethyleneimine in the presence of a catalyst such as carbon dioxide, sodium bisulfite, sulfuric acid, hydrogen peroxide, hydrochloric acid, acetic acid, etc. Specific methods for preparing these polyamine backbones are disclosed in U.S. Patent 2,182,306, Ulrich et al., issued December 5, 1939; U.S. Patent 3,033,746, Mayle et al., issued May 8, 1962; U.S. Patent 2,208,095, Esselmann et al., issued July 16, 1940; U.S. Patent 2,806,839, Crowther, issued September 17, 1957; and U.S. Patent 2,553,696, Wilson, issued May 21, 1951 ; all herein incoφorated by reference. Examples of modified cotton soil release polymers ofthe present invention comprising PEI's, are illustrated in Formulas I - V: Formula I depicts a preferred cotton soil release polymer comprising a PEI backbone wherein all substitutable nitrogens are modified by replacement of hydrogen with a polyoxyalkyleneoxy unit, -(CH2CH2θ)2øH, having the formula: Formula I Formula II depicts a cotton soil release polymer comprising a PEI backbone wherein all substitutable nitrogens are modified by replacement of hydrogen with a polyoxyalkyleneoxy unit, -(CH2CH2θ)7H, having the formula Formula II This is an example of a cotton soil release polymer that is fully modified by one type of moiety. Formula III depicts a cotton soil release polymer comprising a PEI backbone wherein all substitutable primary amine nitrogens are modified by replacement of hydrogen with a polyoxyalkyleneoxy unit, -(CH2CH2θ)7H, the molecule is then modified by subsequent oxidation of all oxidizable primary and secondary nitrogens to N-oxides, said cotton soil release agent having the formula Formula III Formula IV depicts a cotton soil release polymer comprising a PEI backbone wherein all backbone hydrogen atoms are substituted and some backbone amine units are quaternized. The substituents are polyoxyalkyleneoxy units, -(CH2CH2θ)7H, or methyl groups. The modified PEI cotton soil release polymer has the formula Formula IV Formula V depicts a cotton soil release polymer comprising a PEI backbone wherein *he backbone nitrogens are modified by substitution (i.e. by -(CH2CH2θ)7H or methyl), quaternized, oxidized to N-oxides or combinations thereof. The resulting cotton soil release polymer has the formula Formula V In the above examples, not all nitrogens of a unit class comprise the same modification. The present invention allows the formulator to have a portion ofthe secondary amine nitrogens ethoxylated while having other secondary amine nitrogens oxidized to N-oxides. This also applies to the primary amine nitrogens, in that the formulator may choose to modify all or a portion ofthe primary amine nitrogens with one or more substituents prior to oxidation or quaternization. Any possible combination of E groups can be substituted on the primary and secondary amine nitrogens, except for the restrictions described herein above. The formulator may take advantage ofthe possiblility to modify the polyamine backbones ofthe present invention in a manner that affords only the minimal amount of oxidizing the substrate backbones. For example, bleach "tempering" may be accomplished prior to or after formulation. For the puφoses ofthe present invention, the term "bleach tempering" is defined as treating the modified polyamine with sufficient bleaching agent to oxidize the backbone against the conditions of formulation. By way of demonstration, a polyamine backbone does not necessarily require full modification by quaternization or N-oxidation to be stable towards bleach. When a sample of modified polyamine backbone is exposed to a suitable bleaching system (e.g. nonanoyloxybenzene sulfonate/perborate) any backbone nitrogens oxidizable under these conditions will oxidized. However, due to the exact structural properties ofthe backbone, some or all or the pre-bleach treatment nitrogens may remain un-effected. Once this tempering has taken place, the formulator may combine the modified polyamine with the bleaching system and remain confident that the polyamine will not consume the bulk ofthe bleaching agent. Those skilled in the art of bleach formulation will recognize that the bleach tempering will have its limitations and that a weaker tempering bleach should not be used in place ofthe formulation bleach. In another mode, the formulator may wish to add excess bleaching agent to the laundry detergent composition during formulation in order to conduct suitable in situ bleach "tempering" during storage and handling of the formulation. A preferred embodiment ofthe present invention involves the use of polyhydroxy fatty acid amide surfactants in combination with the modified polyamines described herein. This combination of nonionic surfactant and modified polyamine is especially useful at low pH formulations, that is at a pH less than about 10. A preferred laundry detergent composition according to the present invention comprises the low pH formula comprising: a) at least about 0.01% to about 95% by weight, of a polyhydroxy fatty acid amide nonionic detersive surfactant; b) from about 0.01 to about 10% by weight, of an anionic soil release polymer having effective soil release on non-cotton fabric; c) optionally from about 0.05 to about 30% by weight, of a bleach; d) from about 0.01 to about 10% by weight, a water-soluble or dispersible, bleach stable, modified polyamine cotton soil release agent according to the present invention; and e) the balance carrier and adjunct ingredients; wherein the composition has a pH of about 7.2 to about 8.9 when measured as a 10% solution in water. The polyhydroxy fatty acid amides suitable for use in the low pH embodiments ofthe present invention may be combined with other suitable detersive surfactants such as anionic, ampholytic, zwitterionic surfactants, and mixtures thereof. METHOD OF USE Present invention relates to methods of providing soil release benefits to fabric. The present invention relates to providing soil release benefits to cotton fabric by contacting said cotton fabric with a laundry composition comprising: a) at least about 0.001% by weight, a water-soluble or dispersible, bleach stable, modified polyamine cotton soil release agent according to the present invention; and b) the balance carrier and adjunct ingredients. The present invention also relates to methods of providing soil release to all fabrics that comprise the laundry wash load, wherein said fabric is contacted with a laundry detergent composition comprising: a) at least 0.01% by weight, of a detersive surfactant selected from the group consisting of anionic, cationic, nonionic, zwitterionic, and ampholytic surfactants, and mixtures thereof; b) from about 0.01 to about 10% by weight, of a soil release polymer having effective soil release on non-cotton fabric; c) optionally from about 0.05 to about 30% by weight, of a bleach; d) from about 0.1 to about 10% by weight, a modified polyamine cotton soil release polymer according to the present invention; and e) the balance carrier and adjunct ingredients. The methods ofthe present invention are suitable for use when the fabric being treated for soil release is also in need of bleaching. Compositions comprising bleaching agents commonly used to clean white fabrics are compatible with the cotton soil release polymers ofthe present invention. The present invention also provides a method for cleaning soiled cotton fabric by contacting said fabric with an aqueous solution ofthe laundry compositions or the laundry detergent compositions ofthe present invention. Because of the substantive nature ofthe compounds ofthe present invention, the methods described herein provide cotton soil release benefits for several treatments or laundry washes after the present method has been withdrawn. The process also results in cotton fabric having a cleaner appearance and in the case of white cotton fabric, a whiter appearance. For the puφoses ofthe methods for providing cotton soil release to cotton fabric, the backbone ofthe polyamine does not require modification, that is no backbone nitrogens require oxidation of quaternization. This is especially true in the case of methods that do not use bleaching materials. For example, a suitable cotton soil release agent has the structure wherein the polyamine backbone is substitued with polyethyleneoxy units and no backbone nitrogen units are quaternized or oxidized. However, cotton soil release agents ofthe above type can not be combined with bleaching agents except in the cases where these substrates are the starting materials for "bleach tempered" cotton soil release agents where the "tempered" cotton soil release agents are pre-formed or "tempered" in situ. Adjunct Ingredients Detersive surfactants The detersive surfactants suitable for use in the present invention are cationic, anionic, nonionic, ampholytic, zwitterionic, and mixtures thereof, further described herein below. The laundry detergent composition may be in any suitable form, for example, high density liquids, light liquids or other pourable forms in addition to granules or laundry bars. The cotton soil release polymers ofthe present invention can be formulated into any detersive matrix chosen by the formulator. The laundry detergent compositions according to the present invention may additionally comprise at least about 0.01%, preferably at least about 0.1%, more preferably at least about 1% by weight, ofthe following detersive surfactants. Nonlimiting examples of surfactants useful herein typically at levels from about 1% to about 55%, by weight, include the conventional Cj J-Cjg alkyl benzene sulfonates ("LAS") and primary, branched-chain and random C10-C20 alkyl sulfates ("AS"), the Cio-Cis secondary (2,3) alkyl sulfates ofthe formula CH3(CH 2 ) x (CHOSO3 " M + ) CH3 and CH3 (CH2) y (CHOSO3 _ M + ) CH2CH3 where x and (y + 1) are integers of at least about 7, preferably at least about 9, and M is a water-solubilizing cation, especially sodium, unsaturated sulfates such as oleyl sulfate, the C \ Q-C \ g alkyl alkoxy sulfates ("AE X S"; especially EO 1-7 ethoxy sulfates), Cjo-Cig alkyl alkoxy carboxylates (especially the EO 1-5 ethoxycarboxylates), the Cjo-ig glycerol ethers, the CjQ-Cjg alkyl polyglycosides and their corresponding sulfated polyglycosides, and C12-C18 alpha-sulfonated fatty acid esters. If desired, the conventional nonionic and amphoteric surfactants such as the C12-C1 g alkyl ethoxylates ("AE") including the so-called narrow peaked alkyl ethoxylates and C6-C12 alkyl phenol alkoxylates (especially ethoxylates and mixed ethoxy/propoxy), C12-C18 betaines and sulfobetaines ("sultaines"), Cio-Cjg amine oxides, and the like, can also be included in the overall compositions. The CJO- C j g N-alkyl polyhydroxy fatty acid amides can also be used. Typical examples include the C j 2--Cl8 N-methylglucamides. See WO 9,206,154. Other sugar-derived surfactants include the N-alkoxy polyhydroxy fatty acid amides, such as CjQ-Cig N-(3- methoxypropyl) glucamide. The N-propyl through N-hexyl Ci 2-Cjg glucamides can be used for low sudsing. C10-C20 conventional soaps may also be used. If high sudsing is desired, the branched-chain C\ Q -C\β soaps may be used. Mixtures of anionic and nonionic surfactants are especially useful. Other conventional useful surfactants are listed in standard texts. The prefened compositions ofthe present invention comprise at least about 0.01%, preferably at least 0.1%, more preferably from about 1% to about 95%, most preferably from about 1% to about 80% by weight, of an anionic detersive surfactant. Alkyl sulfate surfactants, either primary or secondary, are a type of anionic surfactant of importance for use herein. Alkyl sulfates have the general formula ROSO3M wherein R preferably is a CJ0-C24 hydrocarbyl, preferably an alkyl straight or branched chain or hydroxyalkyl having a C]ø-C20 alkyl component, more preferably a C^-Cjg alkyl or hydroxyalkyl, and M is hydrogen or a water soluble cation, e.g., an alkali metal cation (e.g., sodium potassium, lithium), substituted or unsubstituted ammonium cations such as methyl-, dimethyl-, and trimethyl ammonium and quaternary ammonium cations, e.g., tetramethyl- ammonium and dimethyl piperdinium, and cations derived from alkanolamines such as ethanolamine, diethanolamine, triethanolamine, and mixtures thereof, and the like. Typically, alkyl chains of C^-Cjg are preferred for lower wash temperatures (e.g., below about 50°C) and Cjg-Ci g alkyl chains are prefened for higher wash temperatures (e.g., about 50°C). Alkyl alkoxylated sulfate surfactants are another category of prefened anionic surfactant. These surfactants are water soluble salts or acids typically ofthe formula RO(A) m SO3M wherein R is an unsubstituted C10-C24 alkyl or hydroxyalkyl group having a C10-C24 alkyl component, preferably a C12-C20 alkyl or hydroxyalkyl, more preferably Cj2-Cιg alkyl or hydroxyalkyl, A is an ethoxy or propoxy unit, m is greater than zero, typically between about 0.5 and about 6, more preferably between about 0.5 and about 3, and M is hydrogen or a water soluble cation which can be, for example, a metal cation (e.g., sodium, potassium, lithium, calcium, magnesium, etc.), ammonium or substituted-ammonium cation. Alkyl ethoxylated sulfates as well as alkyl propoxylated sulfates are contemplated herein. Specific examples of substituted ammonium cations include methyl-, dimethyl-, trimethyl-ammonium and quaternary ammonium cations, such as tetramethyl-ammonium, dimethyl piperdinium and cations derived from alkanolamines, e.g., monoethanolamine, diethanolamine, and triethanolamine, and mixtures thereof. Exemplary surfactants are C12C18 alkyl polyethoxylate (1.0) sulfate, C^-Cjg alkyl polyetho.xylate (2.25) sulfate, C]2-Ci8 alkyl polyethoxylate (3.0) sulfate, and Ci2-Cjg alkyl polyethoxylate (4.0) sulfate wherein M is conveniently selected from sodium and potassium. The laundry detergent compositions according to the present invention may additionally comprise at least about 0.01%, preferably at least about 0.1%, more preferably at least about 1% by weight, of conventional Cj j-Cjg alkyl benzene sulfonates ("LAS"), preferably in laundry bar embodiments and in granular laundry detergent compositions. The prefened compositions ofthe present invention also comprise at least about 0.01%, preferably at least 0.1%, more preferably from about 1% to about 95%, most preferably from about 1% to about 80% by weight, of an nonionic detersive surfactant. Prefened nonionic surfactants such as Ci2-Cι g alkyl ethoxylates ("AE") including the so- called narrow peaked alkyl ethoxylates and Cg-C^ alkyl phenol alkoxylates (especially ethoxylates and mixed ethoxy/propoxy), block alkylene oxide condensate of Cg to C j 2 alkyl phenols, alkylene oxide condensates of Cg-C22 alkanols and ethylene oxide/propylene oxide block polymers (Pluronic™-BASF Coφ.), as well as semi polar nonionics (e.g., amine oxides and phosphine oxides) can be used in the present compositions. An extensive disclosure of these types of surfactants is found in U.S. Pat. 3,929,678, Laughlin et al., issued December 30, 1975, incoφorated herein by reference. Alkylpolysaccharides such as disclosed in U.S. Pat. 4,565,647 Llenado (incoφorated herein by reference) are also prefened nonionic surfactants in the compositions ofthe invention. More prefened nonionic surfactants are the polyhydroxy fatty acid amides having the formula: wherein R? is C5-C31 alkyl, preferably straight chain C7-C19 alkyl or alkenyl, more preferably straight chain C9-C17 alkyl or alkenyl, most preferably straight chain C j j-C|5 alkyl or alkenyl, or mixtures thereof; R^ is selected from the group consisting of hydrogen, C1-C4 alkyl, C1-C4 hydroxyalkyl, preferably methyl or ethyl, more preferably methyl. Q is a polyhydroxyalkyl moiety having a linear alkyl chain with at least 3 hydroxyls directly connected to the chain, or an alkoxylated derivative thereof; preferred alkoxy is ethoxy or propoxy, and mixtures thereof. Prefened Q is derived from a reducing sugar in a reductive amination reaction. More preferably Q is a glycityl moiety. Suitable reducing sugars include glucose, fructose, maltose, lactose, galactose, mannose, and xylose. As raw materials, high dextrose corn syrup, high fructose com syrup, and high maltose corn syrup can be utilized as well as the individual sugars listed above. These corn syrups may yield a mix of sugar components for Q. It should be understood that it is by no means intended to exclude other suitable raw materials. Q is more preferably selected from the group consisting of -CH 2 (CHOH) n CH 2 OH, -CH(CH 2 OH)(CHOH) n .1 CH 2 OH, - CH2(CHOH)2-(CHOR')(CHOH)CH2OH, and alkoxylated derivatives thereof, wherein n is an integer from 3 to 5, inclusive, and R * is hydrogen or a cyclic or aliphatic monosaccharide. Most prefened substituents for the Q moiety are glycityls wherein n is 4, particularly -CH 2 (CHOH) 4 CH 2 OH. R?CO-N< can be, for example, cocamide, stearamide, oleamide, lauramide, myristamide, capricamide, palmitamide, tallowamide, etc. R8 can be, for example, methyl, ethyl, propyl, isopropyl, butyl, 2-hydroxy ethyl, or 2-hydroxy propyl. Q can be 1-deoxyglucityl, 2-deoxyfructityl, 1-deoxymaltityl, 1 -deoxylactityl, 1- deoxygalactityl, 1 -deoxymannityl, 1 -deoxymaltotriotityl, etc. A particularly desirable surfactant of this type for use in the compositions herein is alkyl-N-methyl glucomide, a compound of the above formula wherein R? is alkyl (preferably C\ 1-C13), R^, is methyl and Q is 1-deoxyglucityl. Other sugar-derived surfactants include the N-alkoxy polyhydroxy fatty acid amides, such as Cio-Cjg N-(3-methoxypropyl) glucamide. The N-propyl through N- hexyl C^-Cj g glucamides can be used for low sudsing. C1Q-C20 conventional soaps may also be used. If high sudsing is desired, the branched-chain C IO-C JO soaps may be used. Bleaching Compounds - Bleaching Agents and Bleach Activators The detergent compositions herein may optionally contain bleaching agents or bleaching compositions containing a bleaching agent and one or more bleach activators. When present, bleaching agents will be at levels of from about 0.05% to about 30%, more preferably from about 1% to about 30%, most preferably from about 5% to about 20%, ofthe detergent composition, especially for fabric laundering. If present, the amount of bleach activators will typically be from about 0.1% to about 60%, more typically from about 0.5% to about 40% ofthe bleaching composition comprising the bleaching agent-plus-bleach activator. The peroxygen bleaching compounds useful herein are those capable of yielding hydrogen peroxide in an aqueous liquor. These compounds are well known in the art and include hydrogen peroxide and the alkali metal peroxides, organic peroxide bleaching compounds such as urea peroxide, and inorganic persalt bleaching compounds, such as the alkali metal perborates, percarbonates, peφhosphates, and the like. Mixtures of two or more such bleaching compounds can also be used, if desired. Prefened peroxygen bleaching compounds include sodium perborate, commercially available in the form of mono-, tri-, and tetra-hydrate, sodium pyrophosphate peroxyhydrate, urea peroxy- hydrate, sodium peroxide, peroxyphthalate and sodium percarbonate. Particularly prefened are sodium perborate tetrahydrate, sodium perborate monohydrate and sodium percarbonate. Sodium percarbonate is especially prefened because it is very stable during storage and yet still dissolves very quickly in the bleaching liquor. It is believed that such rapid dissolution results in the formation of higher levels of percarboxylic acid and, thus, enhanced surface bleaching performance. Another category of bleaching agent that can be used without restriction encompasses percarboxylic acid bleaching agents and salts thereof. Suitable examples of this class of agents include magnesium monoperoxyphthalate hexahydrate, the magnesium salt of metachloro perbenzoic acid, 4-nonylamino-4-oxoperoxybutyric acid and diperoxydodecanedioic acid. Such bleaching agents are disclosed in U.S. Patent 4,483,781, Hartman, issued November 20, 1984, U.S. Patent Application 740,446, Burns et al, filed June 3, 1985, European Patent Application 0,133,354, Banks et al, published February 20, 1985, and U.S. Patent 4,412,934, Chung et al, issued November 1, 1983. Highly prefened bleaching agents also include 6-nonylamino-6-oxoperoxycaproic acid as described in U.S. Patent 4,634,551, issued January 6, 1987 to Burns et al. A prefened percarbonate bleach comprises dry particles having an average particle size in the range from about 500 micrometers to about 1 ,000 micrometers, not more than about 10% by weight of said particles being smaller than about 200 micrometers and not more than about 10% by weight of said particles being larger than about 1,250 micrometers. Optionally, the percarbonate can be coated with silicate, borate or water-soluble surfactants. Percarbonate is available from various commercial sources such as FMC, Solvay and Tokai Denka. Mixtures of bleaching agents can also be used. Peroxygen bleaching agents, the perborates, the percarbonates, etc., are preferably combined with bleach activators, which lead to the in situ production in aqueous solution (i.e., during the washing process) ofthe peroxy acid conesponding to the bleach activator. Various nonlimiting examples of activators are disclosed in U.S. Patent 4,915,854, issued April 10, 1990 to Mao et al, and U.S. Patent 4,412,934. The nonanoyloxybenzene sulfonate (NOBS) and tetraacetyl ethylene diamine (TAED) activators are typical, and mixtures thereof can also be used. See also U.S. 4,634,551 for other typical bleaches and activators useful herein. Another class of bleach activators comprises the benzoxazin-type activators disclosed by Hodge et al in U.S. Patent 4,966,723, issued October 30, 1990, incoφorated herein by reference. A highly prefened activator ofthe benzoxazin-type is: Still another class of prefened bleach activators includes the acyl lactam activators, especially acyl caprolactams and acyl valerolactams of the formulae: wherein R^ is H or an alkyl, aryl, alkoxyaryl, or alkaryl group containing from 1 to about 12 carbon atoms. Highly prefened lactam activators include benzoyl caprolactam, octanoyl caprolactam, 3,5,5-trimethylhexanoyl caprolactam, nonanoyl caprolactam, decanoyl caprolactam, undecenoyl caprolactam, benzoyl valerolactam, octanoyl valerolactam, decanoyl valerolactam, undecenoyl valerolactam, nonanoyl valerolactam, 3,5,5-trimethylhexanoyl valerolactam and mixtures thereof. See also U.S. Patent 4,545,784, issued to Sanderson, October 8, 1985, incoφorated herein by reference, which discloses acyl caprolactams, including benzoyl caprolactam, adsorbed into sodium perborate. For compositions according to the present invention comprising a bleach, prefened are peroxyacid bleaching agents, of which amide substituted peroxyacid precursor compounds are more prefened, including those having the formula: wherein Rl is C1-C14 alkyl, aryl, alkylaryl, and mixtures thereof; R 2 is C1-C14 alkylene, arylene, alkylarylene, and mixtures thereof; R^ is hydrogen, C J-C IQ alkyl, aryl, alkylaryl, and mixtures thereof; L is any suitable leaving group (a prefened leaving group is phenyl sulfonate). Rl preferably contains from 6 to 12 carbon atoms. R 2 preferably contains from 4 to 8 carbon atoms. Rl may contain, where applicable, branching, substitution, or both and may be sourced from either synthetic sources or natural sources including for example, tallow fat. Analogous structural variations are permissible for R 2 . The substitution can include alkyl, halogen, nitrogen, sulphur and other typical substituent groups or organic compounds. R^ is preferably H or methyl. Rl and R^ should not contain more than 18 carbon atoms in total. Amide substituted bleach activator compounds of this type are described in EP-A-0170386. Prefened examples of bleach activators ofthe above formulae include (6- octanamido-caproyl)oxybenzenesulfonate, (6-nonanamidocaproyl)oxybenzenesulfonate, (6-decanamido-caproyl)oxybenzenesulfonate, and mixtures thereof as described in U.S. Patent 4,634,551, incoφorated herein by reference. The modified polyamines ofthe present invention may optionally be combined with bleaching agents and bleach activator. The prefened laundry detergent compositions comprising bleaching agents comprise: a) at least about 0.01% to about 95% by weight, of an anionic detersive surfactant; b) at least about 0.01 % to about 95% by weight, of a nonionic detersive surfactant; c) from about 0.01 to about 10% by weight, of a soil release polymer having effective soil release on non-cotton fabric; d) from about 0.05 to about 30% by weight, of a bleach; e) from about 0.05 to about 30% by weight, of a bleach activator; f) from about 0.01 to about 10% by weight, a water-soluble or dispersible, bleach stable, modified polyamine cotton soil release agent according to the present invention; and g) the balance carrier and adjunct ingredients. Still more preferably the bleach containing compositions ofthe present invention comprise oxygen bleaches. These oxygen bleach containing compositions comprise: a) at least about 0.01% to about 95% by weight, of an anionic detersive surfactant; b) at least about 0.01% to about 95% by weight, of a nonionic detersive surfactant; c) from about 0.01 to about 10% by weight, of a soil release polymer having effective soil release on non-cotton fabric; d) optionally from about 0.05 to about 30% by weight, of a peroxygen bleach selected from the group consisiting of alkali metal percarbonate, perborate, monopeφhthalate, pyrophosphate peroxyhydrate, urea peroxy- hydrate and mixtures thereof; e) optionally from about 0.05 to about 30% by weight, of a bleach activator having the formula and mixtures thereof, wherein Rl is C1 -C14 alkyl, aryl, alkylaryl, and mixtures thereof; R 2 is Cj-C^ alkylene, arylene, alkylarylene, and mixtures thereof; R^ is hydrogen, C]-Cιo alkyl, aryl, alkylaryl, and mixtures thereof; L is any suitable leaving group; f) from about 0.01 to about 10% by weight, a water-soluble or dispersible, bleach stable, modified polyamine cotton soil release agent according to the present invention; and g) the balance carrier and adjunct ingredients. Bleaching agents other than oxygen bleaching agents are also known in the art and can be utilized herein. One type of non-oxygen bleaching agent of particular interest includes photoactivated bleaching agents such as the sulfonated zinc and/or aluminum phthalocyanines. See U.S. Patent 4,033,718, issued July 5, 1977 to Holcombe et al. If used, detergent compositions will typically contain from about 0.025% to about 1.25%, by weight, of such bleaches, especially sulfonate zinc phthalocyanine. If desired, the bleaching compounds can be catalyzed by means of a manganese compound. Such compounds are well known in the art and include, for example, the manganese-based catalysts disclosed in U.S. Pat. 5,246,621, U.S. Pat. 5,244,594; U.S. Pat. 5,194,416; U.S. Pat. 5,114,606; and European Pat. App. Pub. Nos. 549,271 Al, 549,272A1, 544,440A2, and 544,490A1; Prefened examples of these catalysts include Mnl^2( u "0)3(l'4 5 7-trimethyl-l,4,7-triazacyclononane)2(PF6)2. Mn^2( u "^)i(u- OAc)2( 1 ,4,7-trimethyl- 1 ,4,7-triazacyclononane)2-(ClO4)2, Mn IV 4(u-O)6( 1 ,4,7- triazacyclononane)4(ClO4)4, Mn^Mn 1 V 4(u-O) i (u-OAc)2-( 1 ,4,7-trimethyl- 1 ,4,7- triazacyclononane)2(Clθ4)3 , Mn^( 1 ,4,7-trimethyl- 1 ,4,7-triazacyclononane)- (OCH3)3(PFg), and mixtures thereof. Other metal-based bleach catalysts include those disclosed in U.S. Pat. 4,430,243 and U.S. Pat. 5,114,611. The use of manganese with various complex ligands to enhance bleaching is also reported in the following United States Patents: 4,728,455; 5,284,944; 5,246,612; 5,256,779; 5,280,117; 5,274,147; 5,153,161; and 5,227,084. As a practical matter, and not by way of limitation, the compositions and processes herein can be adjusted to provide on the order of at least one part per ten million ofthe active bleach catalyst species in the aqueous washing liquor, and will preferably provide from about 0.1 ppm to about 700 ppm, more preferably from about 1 ppm to about 500 ppm, ofthe catalyst species in the laundry liquor. A wide variety of other ingredients useful in detergent compositions can be included in the compositions herein, including other active ingredients, carriers, hydrotropes, processing aids, dyes or pigments, solvents for liquid formulations, solid fillers for bar compositions, etc. If high sudsing is desired, suds boosters such as the ClO'Clβ alkanolamides can be incoφorated into the compositions, typically at 1%-10% levels. The C10-C14 monoethanol and diethanol amides illustrate a typical class of such suds boosters. Use of such suds boosters with high sudsing adjunct surfactants such as the amine oxides, betaines and sultaines noted above is also advantageous. If desired, soluble magnesium salts such as MgCl2, MgSO4, and the like, can be added at levels of, typically, 0.1%-2%, to provide additional suds and to enhance grease removal performance. Various detersive ingredients employed in the present compositions optionally can be further stabilized by absorbing said ingredients onto a porous hydrophobic substrate, then coating said substrate with a hydrophobic coating. Preferably, the detersive ingredient is admixed with a surfactant before being absorbed into the porous substrate. In use, the detersive ingredient is released from the substrate into the aqueous washing liquor, where it performs its intended detersive function. To illustrate this technique in more detail, a porous hydrophobic silica (trademark SIPERNAT D10, DeGussa) is admixed with a proteolytic enzyme solution containing 3%-5% of Cu_i5 ethoxylated alcohol (EO 7) nonionic surfactant. Typically, the enzyme/surfactant solution is 2.5 X the weight of silica. The resulting powder is dispersed with stirring in silicone oil (various silicone oil viscosities in the range of 500- 12,500 can be used). The resulting silicone oil dispersion is emulsified or otherwise added to the final detergent matrix. By this means, ingredients such as the aforementioned enzymes, bleaches, bleach activators, bleach catalysts, photoactivators, dyes, fluorescers, fabric conditioners and hydrolyzable surfactants can be "protected" for use in detergents, including liquid laundry detergent compositions. Liquid detergent compositions can contain water and other solvents as carriers. Low molecular weight primary or secondary alcohols exemplified by methanol, ethanol, propanol, and isopropanol are suitable. Monohydric alcohols are prefened for solubilizing surfactant, but polyols such as those containing from 2 to about 6 carbon atoms and from 2 to about 6 hydroxy groups (e.g., 1 ,3-propanediol, ethylene glycol, glycerin, and 1,2-propanediol) can also be used. The compositions may contain from 5% to 90%, typically 10% to 50% of such carriers. The detergent compositions herein will preferably be formulated such that, during use in aqueous cleaning operations, the wash water will have a pH of between about 6.5 and about 11, preferably between about 7.5 and 10.5. Laundry products are typically at pH 9-11. Techniques for controlling pH at recommended usage levels include the use of buffers, alkalis, acids, etc., and are well known to those skilled in the art. Enzymes Enzymes can be included in the present detergent compositions for a variety of puφoses, including removal of protein-based, carbohydrate-based, or triglyceride-based stains from surfaces such as textiles, for the prevention of refugee dye transfer, for example in laundering, and for fabric restoration. Suitable enzymes include proteases, amylases, lipases, cellulases, peroxidases, and mixtures thereof of any suitable origin, such as vegetable, animal, bacterial, fungal and yeast origin. Prefened selections are influenced by factors such as pH-activity and/or stability optima, thermostability, and stability to active detergents, builders and the like. In this respect bacterial or fungal enzymes are prefened, such as bacterial amylases and proteases, and fungal cellulases. "Detersive enzyme", as used herein, means any enzyme having a cleaning, stain removing or otherwise beneficial effect in a laundry, hard surface cleaning or personal care detergent composition. Prefened detersive enzymes are hydrolases such as proteases, amylases and lipases. Preferred enzymes for laundry puφoses include, but are not limited to, proteases, cellulases, lipases and peroxidases. Enzymes are normally incoφorated into detergent or detergent additive compositions at levels sufficient to provide a "cleaning-effective amount". The term "cleaning effective amount" refers to any amount capable of producing a cleaning, stain removal, soil removal, whitening, deodorizing, or freshness improving effect on substrates such as fabrics. In practical terms for current commercial preparations, typical amounts are up to about 5 mg by weight, more typically 0.01 mg to 3 mg, of active enzyme per gram ofthe detergent composition. Stated otherwise, the compositions herein will typically comprise from 0.001% to 5%, preferably 0.01%-1% by weight of a commercial enzyme preparation. Protease enzymes are usually present in such commercial preparations at levels sufficient to provide from 0.005 to 0.1 Anson units (AU) of activity per gram of composition. For certain detergents, it may be desirable to increase the active enzyme content ofthe commercial preparation in order to minimize the total amount of non-catalytically active materials and thereby improve spotting/filming or other end-results. Higher active levels may also be desirable in highly concentrated detergent formulations. Suitable examples of proteases are the subtilisins which are obtained from particular strains of B. subtilis and B. licheniformis. One suitable protease is obtained from a strain of Bacillus, having maximum activity throughout the pH range of 8-12, developed and sold as ESPERASE® by Novo Industries A/S of Denmark, hereinafter "Novo". The preparation of this enzyme and analogous enzymes is described in GB 1,243,784 to Novo. Other suitable proteases include ALCALASE® and SAVINASE® from Novo and MAXATASE® from International Bio-Synthetics, Inc., The Netherlands; as well as Protease A as disclosed in EP 130,756 A, January 9, 1985 and Protease B as disclosed in EP 303,761 A, April 28, 1987 and EP 130,756 A, January 9, 1985. See also a high pH protease from Bacillus sp. NCIMB 40338 described in WO 9318140 A to Novo. Enzymatic detergents comprising protease, one or more other enzymes, and a reversible protease inhibitor are described in WO 9203529 A to Novo. Other prefened proteases include those of WO 9510591 A to Procter & Gamble . When desired, a protease having decreased adsoφtion and increased hydrolysis is available as described in WO 9507791 to Procter & Gamble. A recombinant trypsin-like protease for detergents suitable herein is described in WO 9425583 to Novo. In more detail, an especially preferred protease, refened to as "Protease D" is a carbonyl hydrolase variant having an amino acid sequence not found in nature, which is derived from a precursor carbonyl hydrolase by substituting a different amino acid for a plurality of amino acid residues at a position in said carbonyl hydrolase equivalent to position +76, preferably also in combination with one or more amino acid residue positions equivalent to those selected from the group consisting of +99, +101, +103, +104, +107, +123, +27, +105, +109, +126, +128, +135, +156, +166, +195, +197, +204, +206, +210, +216, +217, +218, +222, +260, +265, and/or +274 according to the numbering of Bacillus amyloliquefaciens subtilisin, as described in WO 95/10615 published April 20, 1995 by Genencor International. Useful proteases are also described in PCT publications: WO 95/30010 published Novenber 9, 1995 by The Procter & Gamble Company; WO 95/30011 published Novenber 9, 1995 by The Procter & Gamble Company; WO 95/29979 published Novenber 9, 1995 by The Procter & Gamble Company. Amylases suitable herein include, for example, α-amylases described in GB 1,296,839 to Novo; RAPID ASE®, Intemationai Bio-Synthetics, Inc. and TERMAMYL®, Novo. FUNGAMYL® from Novo is especially useful. Engineering of enzymes for improved stability, e.g., oxidative stability, is known. See, for example J. Biological Chem., Vol. 260, No. 11, June 1985, pp 6518-6521. Certain prefened embodiments ofthe present compositions can make use of amylases having improved stability in detergents, especially improved oxidative stability as measured against a reference-point of TERMAMYL® in commercial use in 1993. These prefened amylases herein share the characteristic of being "stability-enhanced" amylases, characterized, at a minimum, by a measurable improvement in one or more of: oxidative stability, e.g., to hydrogen peroxide / tetraacetylethylenediamine in buffered solution at pH 9-10; thermal stability, e.g., at common wash temperatures such as about 60°C; or alkaline stability, e.g., at a pH from about 8 to about 11, measured versus the above-identified reference- point amylase. Stability can be measured using any ofthe art-disclosed technical tests. See, for example, references disclosed in WO 9402597. Stability-enhanced amylases can be obtained from Novo or from Genencor International. One class of highly prefened amylases herein have the commonality of being derived using site-directed mutagenesis from one or more ofthe Baccillus amylases, especialy the Bacillus α-amylases, regardless of whether one, two or multiple amylase strains are the immediate precursors. Oxidative stability-enhanced amylases vs. the above-identified reference amylase are prefened for use, especially in bleaching, more preferably oxygen bleaching, as distinct from chlorine bleaching, detergent compositions herein. Such prefened amylases include (a) an amylase according to the hereinbefore incoφorated WO 9402597, Novo, Feb. 3, 1994, as further illustrated by a mutant in which substitution is made, using alanine or threonine, preferably threonine, ofthe methionine residue located in position 197 ofthe B. licheniformis alpha-amylase, known as TERMAMYL®, or the homologous position variation of a similar parent amylase, such as B. amyloliquefaciens, B.subtilis, or B. stearothermophilus; (b) stability-enhanced amylases as described by Genencor International in a paper entitled "Oxidatively Resistant alpha-Amylases" presented at the 207th American Chemical Society National Meeting, March 13-17 1994, by C. Mitchinson. Therein it was noted that bleaches in automatic dishwashing detergents inactivate alpha-amylases but that improved oxidative stability amylases have been made by Genencor from B. licheniformis NCIB8061. Methionine (Met) was identified as the most likely residue to be modified. Met was substituted, one at a time, in positions 8, 15, 197, 256, 304, 366 and 438 leading to specific mutants, particularly important being M 197L and M 197T with the M 197T variant being the most stable expressed variant; (c) particularly prefened amylases herein include amylase variants having additional modification in the immediate parent as described in WO 9510603 A and are available from the assignee, Novo, as DURAMYL®. Other particularly prefened oxidative stability enhanced amylase include those described in WO 9418314 to Genencor International and WO 9402597 to Novo. Any other oxidative stability-enhanced amylase can be used, for example as derived by site-directed mutagenesis from known chimeric, hybrid or simple mutant parent forms of available amylases. Other prefened enzyme modifications are accessible. See WO 9509909 A to Novo. Cellulases usable herein include both bacterial and fungal types, preferably having a pH optimum between 5 and 9.5. U.S. 4,435,307, Barbesgoard et al, March 6, 1984, discloses suitable fungal cellulases from Humicola insolens or Humicola strain DSM 1800 or a cellulase 212-producing fungus belonging to the genus Aeromonas, and cellulase extracted from the hepatopancreas of a marine mollusk, Dolabella Auricula Solander. Suitable cellulases are also disclosed in GB-A-2.075.028; GB-A-2.095.275 and DE-OS-2.247.832. CAREZYME® (Novo) is especially useful. See also WO 91 17243 to Novo. Suitable lipase enzymes for detergent usage include those produced by microorganisms ofthe Pseudomonas group, such as Pseudomonas stutzeri ATCC 19.154, as disclosed in GB 1,372,034. See also lipases in Japanese Patent Application 53,20487, laid open Feb. 24, 1978. This lipase is available from Amano Pharmaceutical Co. Ltd., Nagoya, Japan, under the trade name Lipase P "Amano," or "Amano-P." Other suitable commercial lipases include Amano-CES, lipases ex Chromobacter viscosum, e.g. Chromobacter viscosum var. lipolyticum NRRLB 3673 from Toyo Jozo Co., Tagata, Japan; Chromobacter viscosum lipases from U.S. Biochemical Coφ., U.S.A. and Disoynth Co., The Netherlands, and lipases ex Pseudomonas gladioli. LIPOLASE® enzyme derived from Humicola lanuginosa and commercially available from Novo, see also EP 341,947, is a preferred lipase for use herein. Lipase and amylase variants stabilized against peroxidase enzymes are described in WO 9414951 A to Novo. See also WO 9205249 and RD 94359044. Cutinase enzymes suitable for use herein are described in WO 8809367 A to Genencor. Peroxidase enzymes may be used in combination with oxygen sources, e.g., percarbonate, perborate, hydrogen peroxide, etc., for "solution bleaching" or prevention of transfer of dyes or pigments removed from substrates during the wash to other substrates present in the wash solution. Known peroxidases include horseradish peroxidase, ligninase, and haloperoxidases such as chloro- or bromo-peroxidase. Peroxidase-containing detergent compositions are disclosed in WO 89099813 A, October 19, 1989 to Novo and WO 8909813 A to Novo. A range of enzyme materials and means for their incoφoration into synthetic detergent compositions is also disclosed in WO 9307263 A and WO 9307260 A to Genencor International, WO 8908694 A to Novo, and U.S. 3,553,139, January 5, 1971 to McCarty et al. Enzymes are further disclosed in U.S. 4,101,457, Place et al, July 18, 1978, and in U.S. 4,507,219, Hughes, March 26, 1985. Enzyme materials useful for liquid detergent formulations, and their incoφoration into such formulations, are disclosed in U.S. 4,261,868, Hora et al, April 14, 1981. Enzymes for use in detergents can be stabilized by various techniques. Enzyme stabilization techniques are disclosed and exemplified in U.S. 3,600,319, August 17, 1971, Gedge et al, EP 199,405 and EP 200,586, October 29, 1986, Venegas. Enzyme stabilization systems are also described, for example, in U.S. 3,519,570. A useful Bacillus, sp. AC 13 giving proteases, xylanases and cellulases, is described in WO 9401532 A to Novo. Enzyme Stabilizing System Enzyme-containing, including but not limited to, liquid compositions, herein may comprise from about 0.001% to about 10%, preferably from about 0.005% to about 8%, most preferably from about 0.01% to about 6%, by weight of an enzyme stabilizing system. The enzyme stabilizing system can be any stabilizing system which is compatible with the detersive enzyme. Such a system may be inherently provided by other formulation actives, or be added separately, e.g., by the formulator or by a manufacturer of detergent-ready enzymes. Such stabilizing systems can, for example, comprise calcium ion, boric acid, propylene glycol, short chain carboxylic acids, boronic acids, and mixtures thereof, and are designed to address different stabilization problems depending on the type and physical form ofthe detergent composition. One stabilizing approach is the use of water-soluble sources of calcium and/or magnesium ions in the finished compositions which provide such ions to the enzymes. Calcium ions are generally more effective than magnesium ions and are prefened herein if only one type of cation is being used. Typical detergent compositions, especially liquids, will comprise from about 1 to about 30, preferably from about 2 to about 20, more preferably from about 8 to about 12 millimoles of calcium ion per liter of finished detergent composition, though variation is possible depending on factors including the multiplicity, type and levels of enzymes incoφorated. Preferably water-soluble calcium or magnesium salts are employed, including for example calcium chloride, calcium hydroxide, calcium formate, calcium malate, calcium maleate, calcium hydroxide and calcium acetate; more generally, calcium sulfate or magnesium salts conesponding to the exemplified calcium salts may be used. Further increased levels of Calcium and/or Magnesium may of course be useful, for example for promoting the grease-cutting action of certain types of surfactant. Another stabilizing approach is by use of borate species. See Severson, U.S. 4,537,706. Borate stabilizers, when used, may be at levels of up to 10% or more ofthe composition though more typically, levels of up to about 3% by weight of boric acid or other borate compounds such as borax or orthoborate are suitable for liquid detergent use. Substituted boric acids such as phenylboronic acid, butaneboronic acid, p- bromophenylboronic acid or the like can be used in place of boric acid and reduced levels of total boron in detergent compositions may be possible though the use of such substituted boron derivatives. Stabilizing systems of certain cleaning compositions may further comprise from 0 to about 10%, preferably from about 0.01% to about 6% by weight, of chlorine bleach scavengers, added to prevent chlorine bleach species present in many water supplies from attacking and inactivating the enzymes, especially under alkaline conditions. While chlorine levels in water may be small, typically in the range from about 0.5 ppm to about 1.75 ppm, the available chlorine in the total volume of water that comes in contact with the enzyme, for example during fabric-washing, can be relatively large; accordingly, enzyme stability to chlorine in-use is sometimes problematic. Since perborate or percarbonate, which have the ability to react with chlorine bleach, may present in certain ofthe instant compositions in amounts accounted for separately from the stabilizing system, the use of additional stabilizers against chlorine, may, most generally, not be essential, though improved results may be obtainable from their use. Suitable chlorine scavenger anions are widely known and readily available, and, if used, can be salts containing ammonium cations with sulfite, bisulfite, thiosulfite, thiosulfate, iodide, etc. Antioxidants such as carbamate, ascorbate, etc., organic amines such as ethylenediaminetetracetic acid (EDTA) or alkali metal salt thereof, monoethanolamine (MEA), and mixtures thereof can likewise be used. Likewise, special enzyme inhibition systems can be incoφorated such that different enzymes have maximum compatibility. Other conventional scavengers such as bisulfate, nitrate, chloride, sources of hydrogen peroxide such as sodium perborate tetrahydrate, sodium perborate monohydrate and sodium percarbonate, as well as phosphate, condensed phosphate, acetate, benzoate, citrate, formate, lactate, malate, tartrate, salicylate, etc., and mixtures thereof can be used if desired. In general, since the chlorine scavenger function can be performed by ingredients separately listed under better recognized functions, (e.g., hydrogen peroxide sources), there is no absolute requirement to add a separate chlorine scavenger unless a compound performing that function to the desired extent is absent from an enzyme- containing embodiment ofthe invention; even then, the scavenger is added only for optimum results. Moreover, the formulator will exercise a chemist's normal skill in avoiding the use of any enzyme scavenger or stabilizer which is majorly incompatible, as formulated, with other reactive ingredients, if used. In relation to the use of ammonium salts, such salts can be simply admixed with the detergent composition but are prone to adsorb water and/or liberate ammonia during storage. Accordingly, such materials, if present, are desirably protected in a particle such as that described in US 4,652,392, Baginski et al. The compositions herein can also optionally include one or more other detergent adjunct materials or other materials for assisting or enhancing cleaning performance, treatment ofthe substrate to be cleaned, or to modify the aesthetics ofthe detergent composition (e.g., perfumes, colorants, dyes, etc.). The following are illustrative examples of such adjunct materials. Builders Detergent builders can optionally be included in the compositions herein to assist in controlling mineral hardness. Inorganic as well as organic builders can be used. Builders are typically used in fabric laundering compositions to assist in the removal of particulate soils. The level of builder can vary widely depending upon the end use ofthe composition and its desired physical form. When present, the compositions will typically comprise at least about 1% builder. Liquid formulations typically comprise from about 5% to about 50%, more typically about 5% to about 30%, by weight, of detergent builder. Granular formulations typically comprise from about 10% to about 80%, more typically from about 15% to about 50% by weight, ofthe detergent builder. Lower or higher levels of builder, however, are not meant to be excluded. Inorganic or P-containing detergent builders include, but are not limited to, the alkali metal, ammonium and alkanolammonium salts of polyphosphates (exemplified by the tripolyphosphates, pyrophosphates, and glassy polymeric meta-phosphates), phosphonates, phytic acid, silicates, carbonates (including bicarbonates and sesquicarbonates), sulphates, and aluminosilicates. However, non-phosphate builders are required in some locales. Importantly, the compositions herein function suφrisingly well even in the presence ofthe so-called "weak" builders (as compared with phosphates) such as citrate, or in the so-called "underbuilt" situation that may occur with zeolite or layered silicate builders. Examples of silicate builders are the alkali metal silicates, particularly those having a Siθ2:Na2θ ratio in the range 1.6:1 to 3.2:1 and layered silicates, such as the layered sodium silicates described in U.S. Patent 4,664,839, issued May 12, 1987 to H. P. Rieck. NaSKS-6 is the trademark for a crystalline layered silicate marketed by Hoechst (commonly abbreviated herein as "SKS-6"). Unlike zeolite builders, the Na SKS-6 silicate builder does not contain aluminum. NaSKS-6 has the delta-Na2Siθ5 moφhology form of layered silicate. It can be prepared by methods such as those described in German DE-A-3 ,417,649 and DE-A-3 ,742,043. SKS-6 is a highly prefened layered silicate for use herein, but other such layered silicates, such as those having the general formula NaMSi x O2 x +i yH2θ wherein M is sodium or hydrogen, x is a number from 1.9 to 4, preferably 2, and y is a number from 0 to 20, preferably 0 can be used herein. Various other layered silicates from Hoechst include NaSKS-5, NaSKS-7 and NaSKS-1 1, as the alpha, beta and gamma forms. As noted above, the delta-Na2SiO5 (NaSKS-6 form) is most prefened for use herein. Other silicates may also be useful such as for example magnesium silicate, which can serve as a crispening agent in granular formulations, as a stabilizing agent for oxygen bleaches, and as a component of suds control systems. Examples of carbonate builders are the alkaline earth and alkali metal carbonates as disclosed in German Patent Application No. 2,321,001 published on November 15, 1973. Aluminosilicate builders are useful in the present invention. Aluminosilicate builders are of great importance in most cunently marketed heavy duty granular detergent compositions, and can also be a significant builder ingredient in liquid detergent formulations. Aluminosilicate builders include those having the empirical formula: M z (zAlO 2 ) y ] xH 2 O wherein z and y are integers of at least 6, the molar ratio of z to y is in the range from 1.0 to about 0.5, and x is an integer from about 15 to about 264. Useful aluminosilicate ion exchange materials are commercially available. These aluminosilicates can be crystalline or amoφhous in structure and can be naturally- occurring aluminosilicates or synthetically derived. A method for producing aluminosilicate ion exchange materials is disclosed in U.S. Patent 3,985,669, Krummel, et al, issued October 12, 1976. Prefened synthetic crystalline aluminosilicate ion exchange materials useful herein are available under the designations Zeolite A, Zeolite P (B), Zeolite MAP and Zeolite X. In an especially prefened embodiment, the crystalline aluminosilicate ion exchange material has the formula: Na 12 [(AlO 2 )i2(Siθ2)i2] xH2θ wherein x is from about 20 to about 30, especially about 27. This material is known as Zeolite A. Dehydrated zeolites (x = 0 - 10) may also be used herein. Preferably, the aluminosilicate has a particle size of about 0.1-10 microns in diameter. Organic detergent builders suitable for the purposes ofthe present invention include, but are not restricted to, a wide variety of polycarboxylate compounds. As used herein, "polycarboxylate" refers to compounds having a plurality of carboxylate groups, preferably at least 3 carboxylates. Polycarboxylate builder can generally be added to the composition in acid form, but can also be added in the form of a neutralized salt. When utilized in salt form, alkali metals, such as sodium, potassium, and lithium, or alkanolammonium salts are prefened. Included among the polycarboxylate builders are a variety of categories of useful materials. One important category of polycarboxylate builders encompasses the ether polycarboxylates, including oxydisuccinate, as disclosed in Berg, U.S. Patent 3,128,287, issued April 7, 1964, and Lamberti et al, U.S. Patent 3,635,830, issued January 18, 1972. See also "TMS/TDS" builders of U.S. Patent 4,663,071, issued to Bush et al, on May 5, 1987. Suitable ether polycarboxylates also include cyclic compounds, particularly alicyclic compounds, such as those described in U.S. Patents 3,923,679; 3,835,163; 4,158,635; 4,120,874 and 4,102,903. Other useful detergency builders include the ether hydroxypolycarboxylates, copolymers of maleic anhydride with ethylene or vinyl methyl ether, 1, 3, 5-trihydroxy benzene-2, 4, 6-trisulphonic acid, and carboxymethyloxysuccinic acid, the various alkali metal, ammonium and substituted ammonium salts of polyacetic acids such as ethylenediamine tetraacetic acid and nitrilotriacetic acid, as well as polycarboxylates such as mellitic acid, succinic acid, oxydisuccinic acid, polymaleic acid, benzene 1,3,5- tricarboxylic acid, carboxymethyloxysuccinic acid, and soluble salts thereof. Citrate builders, e.g., citric acid and soluble salts thereof (particularly sodium salt), are polycarboxylate builders of particular importance for heavy duty liquid detergent formulations due to their availability from renewable resources and their biodegradability. Citrates can also be used in granular compositions, especially in combination with zeolite and/or layered silicate builders. Oxydisuccinates are also especially useful in such compositions and combinations. Also suitable in the detergent compositions ofthe present invention are the 3,3- dicarboxy-4-oxa- 1 ,6-hexanedioates and the related compounds disclosed in U.S. Patent 4,566,984, Bush, issued January 28, 1986. Useful succinic acid builders include the C5- C20 alkyl and alkenyl succinic acids and salts thereof. A particularly prefened compound of this type is dodecenylsuccinic acid. Specific examples of succinate builders include: laurylsuccinate, myristylsuccinate, palmitylsuccinate, 2- dodecenylsuccinate (prefened), 2-pentadecenylsuccinate, and the like. Laurylsuccinates are the prefened builders of this group, and are described in European Patent Application 86200690.5/0,200,263, published November 5, 1986. Other suitable polycarboxylates are disclosed in U.S. Patent 4,144,226, Crutchfield et al, issued March 13, 1979 and in U.S. Patent 3,308,067, Diehl, issued March 7, 1967. See also Diehl U.S. Patent 3,723,322. Fatty acids, e.g., Ci 2-Cιg monocarboxylic acids, can also be incoφorated into the compositions alone, or in combination with the aforesaid builders, especially citrate and/or the succinate builders, to provide additional builder activity. Such use of fatty acids will generally result in a diminution of sudsing, which should be taken into account by the formulator. In situations where phosphorus-based builders can be used, and especially in the formulation of bars used for hand-laundering operations, the various alkali metal phosphates such as the well-known sodium tripolyphosphates, sodium pyrophosphate and sodium orthophosphate can be used. Phosphonate builders such as ethane- 1 - hydroxy-l,l-diphosphonate and other known phosphonates (see, for example, U.S. Patents 3,159,581; 3,213,030; 3,422,021 ; 3,400,148 and 3,422,137) can also be used. Chelating Agents The detergent compositions herein may also optionally contain one or more iron and/or manganese chelating agents. Such chelating agents can be selected from the group consisting of amino carboxylates, amino phosphonates, polyfunctionally- substituted aromatic chelating agents and mixtures therein, all as hereinafter defined. Without intending to be bound by theory, it is believed that the benefit of these materials is due in part to their exceptional ability to remove iron and manganese ions from washing solutions by formation of soluble chelates. Amino carboxylates useful as optional chelating agents include ethylenediaminetetracetates, N-hydroxyethylethylenediaminetriacetates, nitrilo- triacetates, ethylenediamine tetraproprionates, triethylenetetraaminehexacetates, diethylenetriaminepentaacetates, diethylenetriaminepentamethyl phosphonic acid, and ethanoldiglycines, alkali metal, ammonium, and substituted ammonium salts therein and mixtures therein. Also suitable for use as a chelant is methylglycine di-acetic acid (MGDA). Amino phosphonates are also suitable for use as chelating agents in the compositions ofthe invention when at lease low levels of total phosphorus are permitted in detergent compositions, and include ethylenediaminetetrakis (methylenephosphonates) as DEQUEST. Prefened, these amino phosphonates to not contain alkyl or alkenyl groups with more than about 6 carbon atoms. Polyfunctionally-substituted aromatic chelating agents are also useful in the compositions herein. See U.S. Patent 3,812,044, issued May 21, 1974, to Connor et al. Prefened compounds of this type in acid form are dihydroxydisulfobenzenes such as 1,2- dihydroxy-3,5-disulfobenzene. A prefened biodegradable chelator for use herein is ethylenediamine disuccinate ("EDDS"), especially the [S,S] isomer as described in U.S. Patent 4,704,233, November 3, 1987, to Hartman and Perkins. If utilized, these chelating agents will generally comprise from about 0.1% to about 10% by weight of the detergent compositions herein. More preferably, if utilized, the chelating agents will comprise from about 0.1% to about 3.0% by weight of such compositions. Clay Soil Removal/Anti-redeposition Agents The compositions ofthe present invention can also optionally contain water- soluble ethoxylated amines having clay soil removal and antiredeposition properties. Granular detergent compositions which contain these compounds typically contain from about 0.01% to about 10.0% by weight ofthe water-soluble ethoxylates amines; liquid detergent compositions typically contain about 0.01% to about 5%. The most prefened soil release and anti-redeposition agent is ethoxylated tetraethylenepentamine. Exemplary ethoxylated amines are further described in U.S. Patent 4,597,898, VanderMeer, issued July 1, 1986. Another group of prefened clay soil removal-antiredeposition agents are the cationic compounds disclosed in European Patent Application 1 1 1,965, Oh and Gosselink, published June 27, 1984. Other clay soil removal/antiredeposition agents which can be used include the ethoxylated amine polymers disclosed in European Patent Application 111,984, Gosselink, published June 27, 1984; the zwitterionic polymers disclosed in European Patent Application 112,592, Gosselink, published July 4, 1984; and the amine oxides disclosed in U.S. Patent 4,548,744, Connor, issued October 22, 1985. Other clay soil removal and/or anti redeposition agents known in the art can also be utilized in the compositions herein. Another type of preferred antiredeposition agent includes the carboxy methyl cellulose (CMC) materials. These materials are well known in the art. Polymeric Dispersing Agents Polymeric dispersing agents can advantageously be utilized at levels from about 0.1 % to about 7%, by weight, in the compositions herein, especially in the presence of zeolite and/or layered silicate builders. Suitable polymeric dispersing agents include polymeric polycarboxylates and polyethylene glycols, although others known in the art can also be used. It is believed, though it is not intended to be limited by theory, that polymeric dispersing agents enhance overall detergent builder performance, when used in combination with other builders (including lower molecular weight polycarboxylates) by crystal growth inhibition, particulate soil release peptization, and anti-redeposition. Polymeric polycarboxylate materials can be prepared by polymerizing or copolymerizing suitable unsaturated monomers, preferably in their acid form. Unsaturated monomeric acids that can be polymerized to form suitable polymeric polycarboxylates include acrylic acid, maleic acid (or maleic anhydride), fumaric acid, itaconic acid, aconitic acid, mesaconic acid, citraconic acid and methylenemalonic acid. The presence in the polymeric polycarboxylates herein or monomeric segments, containing no carboxylate radicals such as vinylmethyl ether, styrene, ethylene, etc. is suitable provided that such segments do not constitute more than about 40% by weight. Particularly suitable polymeric polycarboxylates can be derived from acrylic acid. Such acrylic acid-based polymers which are useful herein are the water-soluble salts of polymerized acrylic acid. The average molecular weight of such polymers in the acid form preferably ranges from about 2,000 to 10,000, more preferably from about 4,000 to 7,000 and most preferably from about 4,000 to 5,000. Water-soluble salts of such acrylic acid polymers can include, for example, the alkali metal, ammonium and substituted ammonium salts. Soluble polymers of this type are known materials. Use of polyacrylates of this type in detergent compositions has been disclosed, for example, in Diehl, U.S. Patent 3,308,067, issued march 7, 1967. Acrylic/maleic-based copolymers may also be used as a prefened component of the dispersing/anti-redeposition agent. Such materials include the water-soluble salts of copolymers of acrylic acid and maleic acid. The average molecular weight of such copolymers in the acid form preferably ranges from about 2,000 to 100,000, more preferably from about 5,000 to 75,000, most preferably from about 7,000 to 65,000. The ratio of acrylate to maleate segments in such copolymers will generally range from about 30: 1 to about 1 :1, more preferably from about 10:1 to 2:1. Water-soluble salts of such acrylic acid/maleic acid copolymers can include, for example, the alkali metal, ammonium and substituted ammonium salts. Soluble acrylate/maleate copolymers of this type are known materials which are described in European Patent Application No. 66915, published December 15, 1982, as well as in EP 193,360, published September 3, 1986, which also describes such polymers comprising hydroxypropylacrylate. Still other useful dispersing agents include the maleic/acrylic/vinyl alcohol teφolymers. Such materials are also disclosed in EP 193,360, including, for example, the 45/45/10 teφolymer of acrylic/maleic/vinyl alcohol. Another polymeric material which can be included is polyethylene glycol (PEG). PEG can exhibit dispersing agent performance as well as act as a clay soil removal- antiredeposition agent. Typical molecular weight ranges for these puφoses range from about 500 to about 100,000, preferably from about 1,000 to about 50,000, more preferably from about 1,500 to about 10,000. Polyaspartate and polyglutamate dispersing agents may also be used, especially in conjunction with zeolite builders. Dispersing agents such as polyaspartate preferably have a molecular weight (avg.) of about 10,000. Brightener Any optical brighteners or other brightening or whitening agents known in the art can be incoφorated at levels typically from about 0.05% to about 1.2%, by weight, into the detergent compositions herein. Commercial optical brighteners which may be useful in the present invention can be classified into subgroups, which include, but are not necessarily limited to, derivatives of stilbene, pyrazoline, coumarin, carboxylic acid, methinecyanines, dibenzothiphene-5,5-dioxide, azoles, 5- and 6-membered-ring heterocycles, and other miscellaneous agents. Examples of such brighteners are disclosed in "The Production and Application of Fluorescent Brightening Agents", M. Zahradnik, Published by John Wiley & Sons, New York (1982). Specific examples of optical brighteners which are useful in the present compositions are those identified in U.S. Patent 4,790,856, issued to Wixon on December 13, 1988. These brighteners include the PHOR WHITE series of brighteners from Verona. Other brighteners disclosed in this reference include: Tinopal UNPA, Tinopal CBS and Tinopal 5BM; available from Ciba-Geigy; Artie White CC and Artie White CWD, available from Hilton-Davis, located in Italy; the 2-(4-stryl-phenyl)-2H- napthol[l,2-d]triazoles; 4,4'-bis- (l,2,3-triazol-2-yl)-stil- benes; 4,4'-bis(stryl)bisphenyls; and the aminocoumarins. Specific examples of these brighteners include 4-methyl-7- diethyl- amino coumarin; l,2-bis(-venzimidazol-2-yl)ethylene; 1 ,3-diphenyl-phrazolines; 2,5-bis(benzoxazol-2-yl)thiophene; 2-stryl-napth-[l,2-d]oxazole; and 2-(stilbene-4-yl)- 2H-naphtho- [l,2-d]triazole. See also U.S. Patent 3,646,015, issued February 29, 1972 to Hamilton. Anionic brighteners are prefened herein. Suds Suppressors Compounds for reducing or suppressing the formation of suds can be incoφorated into the compositions ofthe present invention. Suds suppression can be of particular importance in the so-called "high concentration cleaning process" as described in U.S. 4,489,455 and 4,489,574 and in front-loading European-style washing machines. A wide variety of materials may be used as suds suppressors, and suds suppressors are well known to those skilled in the art. See, for example, Kirk Othmer Encyclopedia of Chemical Technology, Third Edition, Volume 7, pages 430-447 (John Wiley & Sons, Inc., 1979). One category of suds suppressor of particular interest encompasses monocarboxylic fatty acid and soluble salts therein. See U.S. Patent 2,954,347, issued September 27, 1960 to Wayne St. John. The monocarboxylic fatty acids and salts thereof used as suds suppressor typically have hydrocarbyl chains of 10 to about 24 carbon atoms, preferably 12 to 18 carbon atoms. Suitable salts include the alkali metal salts such as sodium, potassium, and lithium salts, and ammonium and alkanolammonium salts. The detergent compositions herein may also contain non-surfactant suds suppressors. These include, for example: high molecular weight hydrocarbons such as paraffin, fatty acid esters (e.g., fatty acid triglycerides), fatty acid esters of monovalent alcohols, aliphatic C\ g-C4Q ketones (e.g., stearone), etc. Other suds inhibitors include N-alkylated amino triazines such as tri- to hexa-alkylmelamines or di- to tetra- alkyldiamine chlortriazines formed as products of cyanuric chloride with two or three moles of a primary or secondary amine containing 1 to 24 carbon atoms, propylene oxide, and monostearyl phosphates such as monostearyl alcohol phosphate ester and monostearyl di-alkali metal (e.g., K, Na, and Li) phosphates and phosphate esters. The hydrocarbons such as paraffin and haloparaffin can be utilized in liquid form. The liquid hydrocarbons will be liquid at room temperature and atmospheric pressure, and will have a pour point in the range of about -40°C and about 50°C, and a minimum boiling point not less than about 110°C (atmospheric pressure). It is also known to utilize waxy hydrocarbons, preferably having a melting point below about 100°C. The hydrocarbons constitute a prefened category of suds suppressor for detergent compositions. Hydrocarbon suds suppressors are described, for example, in U.S. Patent 4,265,779, issued May 5, 1981 to Gandolfo et al. The hydrocarbons, thus, include aliphatic, alicyclic, aromatic, and heterocyclic saturated or unsaturated hydrocarbons having from about 12 to about 70 carbon atoms. The term "paraffin," as used in this suds suppressor discussion, is intended to include mixtures of true paraffins and cyclic hydrocarbons. Another prefened category of non-surfactant suds suppressors comprises silicone suds suppressors. This category includes the use of polyorganosiloxane oils, such as polydimethylsiloxane, dispersions or emulsions of polyorganosiloxane oils or resins, and combinations of polyorganosiloxane with silica particles wherein the polyorganosiloxane is chemisorbed or fused onto the silica. Silicone suds suppressors are well known in the art and are, for example, disclosed in U.S. Patent 4,265,779, issued May 5, 1981 to Gandolfo et al and European Patent Application No. 89307851.9, published February 7, 1990, by Starch, M. S. Other silicone suds suppressors are disclosed in U.S. Patent 3,455,839 which relates to compositions and processes for defoaming aqueous solutions by incoφorating therein small amounts of polydimethylsiloxane fluids. Mixtures of silicone and silanated silica are described, for instance, in German Patent Application DOS 2,124,526. Silicone defoamers and suds controlling agents in granular detergent compositions are disclosed in U.S. Patent 3,933,672. Bartolotta et al, and in U.S. Patent 4,652,392, Baginski et al, issued March 24, 1987. An exemplary silicone based suds suppressor for use herein is a suds suppressing amount of a suds controlling agent consisting essentially of: (i) polydimethylsiloxane fluid having a viscosity of from about 20 cs. to about 1,500 cs. at 25°C; (ii) from about 5 to about 50 parts per 100 parts by weight of (i) of siloxane resin composed of (CH3)3SiOj/2 units of Siθ2 units in a ratio of from (CH3)3 SiOj/2 units and to Siθ2 units of from about 0.6: 1 to about 1.2: 1 ; and (iii) from about 1 to about 20 parts per 100 parts by weight of (i) of a solid silica gel. In the prefened silicone suds suppressor used herein, the solvent for a continuous phase is made up of certain polyethylene glycols or polyethylene-polypropylene glycol copolymers or mixtures thereof (prefened), or polypropylene glycol. The primary silicone suds suppressor is branched/crosslinked and preferably not linear. To illustrate this point further, typical liquid laundry detergent compositions with controlled suds will optionally comprise from about 0.001 to about 1, preferably from about 0.01 to about 0.7, most preferably from about 0.05 to about 0.5, weight % of said silicone suds suppressor, which comprises (1) a nonaqueous emulsion of a primary antifoam agent which is a mixture of (a) a polyorganosiloxane, (b) a resinous siloxane or a silicone resin-producing silicone compound, (c) a finely divided filler material, and (d) a catalyst to promote the reaction of mixture components (a), (b) and (c), to form silanolates; (2) at least one nonionic silicone surfactant; and (3) polyethylene glycol or a copolymer of polyethylene-polypropylene glycol having a solubility in water at room temperature of more than about 2 weight %; and without polypropylene glycol. Similar amounts can be used in granular compositions, gels, etc. See also U.S. Patents 4,978,471, Starch, issued December 18, 1990, and 4,983,316, Starch, issued January 8, 1991, 5,288,431, Huber et al., issued February 22, 1994, and U.S. Patents 4,639,489 and 4,749,740, Aizawa et al at column 1, line 46 through column 4, line 35. The silicone suds suppressor herein preferably comprises polyethylene glycol and a copolymer of polyethylene glycol/polypropylene glycol, all having an average molecular weight of less than about 1,000, preferably between about 100 and 800. The polyethylene glycol and polyethylene/polypropylene copolymers herein have a solubility in water at room temperature of more than about 2 weight %, preferably more than about 5 weight %. The prefened solvent herein is polyethylene glycol having an average molecular weight of less than about 1 ,000, more preferably between about 100 and 800, most preferably between 200 and 400, and a copolymer of polyethylene glycol/polypropylene glycol, preferably PPG 200/PEG 300. Prefened is a weight ratio of between about 1: 1 and 1 : 10, most preferably between 1 :3 and 1 :6, of polyethylene glycol xopolymer of polyethylene-polypropylene glycol. The prefened silicone suds suppressors used herein do not contain polypropylene glycol, particularly of 4,000 molecular weight. They also preferably do not contain block copolymers of ethylene oxide and propylene oxide, like PLURONIC L101. Other suds suppressors useful herein comprise the secondary alcohols (e.g., 2- alkyl alkanols) and mixtures of such alcohols with silicone oils, such as the silicones disclosed in U.S. 4,798,679, 4,075,118 and EP 150,872. The secondary alcohols include the Cg-C j 6 alkyl alcohols having a C i -C 1 g chain. A prefened alcohol is 2-buty 1 octanol, which is available from Condea under the trademark ISOFOL 12. Mixtures of secondary alcohols are available under the trademark ISALCHEM 123 from Enichem. Mixed suds suppressors typically comprise mixtures of alcohol + silicone at a weight ratio of 1 :5 to 5:1. For any detergent compositions to be used in automatic laundry washing machines, suds should not form to the extent that they overflow the washing machine. Suds suppressors, when utilized, are preferably present in a "suds suppressing amount. By "suds suppressing amount" is meant that the formulator ofthe composition can select an amount of this suds controlling agent that will sufficiently control the suds to result in a low-sudsing laundry detergent for use in automatic laundry washing machines. The compositions herein will generally comprise from 0% to about 5% of suds suppressor. When utilized as suds suppressors, monocarboxylic fatty acids, and salts therein, will be present typically in amounts up to about 5%, by weight, of the detergent composition. Preferably, from about 0.5% to about 3% of fatty monocarboxylate suds suppressor is utilized. Silicone suds suppressors are typically utilized in amounts up to about 2.0%, by weight, ofthe detergent composition, although higher amounts may be used. This upper limit is practical in nature, due primarily to concern with keeping costs minimized and effectiveness of lower amounts for effectively controlling sudsing. Preferably from about 0.01% to about 1% of silicone suds suppressor is used, more preferably from about 0.25% to about 0.5%. As used herein, these weight percentage values include any silica that may be utilized in combination with polyorganosiloxane, as well as any adjunct materials that may be utilized. Monostearyl phosphate suds suppressors are generally utilized in amounts ranging from about 0.1% to about 2%, by weight, ofthe composition. Hydrocarbon suds suppressors are typically utilized in amounts ranging from about 0.01% to about 5.0%, although higher levels can be used. The alcohol suds suppressors are typically used at 0.2%-3% by weight ofthe finished compositions. Fabric Softeners Various through-the-wash fabric softeners, especially the impalpable smectite clays of U.S. Patent 4,062,647, Storm and Nirschl, issued December 13, 1977, as well as other softener clays known in the art, can optionally be used typically at levels of from about 0.5% to about 10% by weight in the present compositions to provide fabric softener benefits concurrently with fabric cleaning. Clay softeners can be used in combination with amine and cationic softeners as disclosed, for example, in U.S. Patent 4,375,416, Crisp et al, March 1, 1983 and U.S. Patent 4,291,071, Harris et al, issued September 22, 1981. Dye Transfer Inhibiting Agents - The compositions ofthe present invention may also include one or more materials effective for inhibiting the transfer of dyes from one fabric to another during the cleaning process. Generally, such dye transfer inhibiting agents include polyvinyl pynolidone polymers, polyamine N-oxide polymers, copolymers of N-vinylpynolidone and N-vinylimidazole, manganese phthalocyanine, peroxidases, and mixtures thereof. If used, these agents typically comprise from about 0.01% to about 10% by weight ofthe composition, preferably from about 0.01% to about 5%, and more preferably from about 0.05% to about 2%. More specifically, the polyamine N-oxide polymers prefened for use herein contain units having the following structural formula: R-A x -P; wherein P is a polymerizable unit to which an N-O group can be attached or the N-O group can form part ofthe polymerizable unit or the N-O group can be attached to both units; A is one of the following structures: -NC(O)-, -C(O)O-, -S-, -O-, -N=; x is 0 or 1; and R is aliphatic, ethoxylated aliphatics, aromatics, heterocyclic or alicyclic groups or any combination thereof to which the nitrogen ofthe N-O group can be attached or the N-O group is part of these groups. Preferred polyamine N-oxides are those wherein R is a heterocyclic group such as pyridine, pynole, imidazole, pynolidine, piperidine and derivatives thereof. The N-O group can be represented by the following general structures: O O I I (Rι)χ-N-(R 2 )y; =N— (R,)χ (R 3 )z wherein R\, R2, R3 are aliphatic, aromatic, heterocyclic or alicyclic groups or combinations thereof; x, y and z are 0 or 1; and the nitrogen of the N-O group can be attached or form part of any ofthe aforementioned groups. The amine oxide unit of the polyamine N-oxides has a pKa <10, preferably pKa <7, more prefened pKa <6. Any polymer backbone can be used as long as the amine oxide polymer formed is water-soluble and has dye transfer inhibiting properties. Examples of suitable polymeric backbones are polyvinyls, polyalkylenes, polyesters, polyethers, polyamide, polyimides, polyacrylates and mixtures thereof. These polymers include random or block copolymers where one monomer type is an amine N-oxide and the other monomer type is an N-oxide. The amine N-oxide polymers typically have a ratio of amine to the amine N-oxide of 10: 1 to 1 : 1 ,000,000. However, the number of amine oxide groups present in the polyamine oxide polymer can be varied by appropriate copolymerization or by an appropriate degree of N-oxidation. The polyamine oxides can be obtained in almost any degree of polymerization. Typically, the average molecular weight is within the range of 500 to 1,000,000; more prefened 1,000 to 500,000; most prefened 5,000 to 100,000. This prefened class of materials can be refened to as "PVNO". The most prefened polyamine N-oxide useful in the detergent compositions herein is poly(4-vinylpyridine-N-oxide) which as an average molecular weight of about 50,000 and an amine to amine N-oxide ratio of about 1 :4. Copolymers of N-vinylpyrrolidone and N-vinylimidazole polymers (refened to as a class as "PVPVI") are also prefened for use herein. Preferably the PVPVI has an average molecular weight range from 5,000 to 1,000,000, more preferably from 5,000 to 200,000, and most preferably from 10,000 to 20,000. (The average molecular weight range is determined by light scattering as described in Barth, et al., Chemical Analysis, Vol 1 13. "Modem Methods of Polymer Characterization", the disclosures of which are incorporated herein by reference.) The PVPVI copolymers typically have a molar ratio of N-vinylimidazole to N-vinylpyrrolidone from 1 :1 to 0.2:1, more preferably from 0.8:1 to 0.3 : 1 ,_most preferably from 0.6: 1 to 0.4: 1. These copolymers can be either linear or branched. The present invention compositions also may employ a polyvinylpynolidone ("PVP") having an average molecular weight of from about 5,000 to about 400,000, preferably from about 5,000 to about 200,000, and more preferably from about 5,000 to about 50,000. PVP's are known to persons skilled in the detergent field; see, for example, EP-A-262,897 and EP-A-256,696, incoφorated herein by reference. Compositions containing PVP can also contain polyethylene glycol ("PEG") having an average molecular weight from about 500 to about 100,000, preferably from about 1,000 to about 10,000. Preferably, the ratio of PEG to PVP on a ppm basis delivered in wash solutions is from about 2:1 to about 50: 1, and more preferably from about 3:1 to about 10:1. The detergent compositions herein may also optionally contain from about 0.005% to 5% by weight of certain types of hydrophilic optical brighteners which also provide a dye transfer inhibition action. If used, the compositions herein will preferably comprise from about 0.01% to 1% by weight of such optical brighteners. The hydrophilic optical brighteners useful in the present invention are those having the structural formula: wherein Rj is selected from anilino, N-2-bis-hydroxyethyl and NH-2-hydroxyethyl; R2 is selected from N-2-bis-hydroxyethyl, N-2-hydroxyethyl-N-methylamino, moφhilino, chloro and amino; and M is a salt-forming cation such as sodium or potassium. When in the above formula, K\ is anilino, R2 is N-2-bis-hydroxyethyl and M is a cation such as sodium, the brightener is 4,4',-bis[(4-anilino-6-(N-2-bis-hydroxyethyl)-s- triazine-2-yl)amino]-2,2'-stilbenedisulfonic acid and disodium salt. This particular brightener species is commercially marketed under the tradename Tinopal-UNPA-GX by Ciba-Geigy Coφoration. Tinopal-UNPA-GX is the prefened hydrophilic optical brightener useful in the detergent compositions herein. When in the above formula, R] is anilino, R2 is N-2-hydroxyethyl-N-2- methylamino and M is a cation such as sodium, the brightener is 4,4'-bis[(4-anilino-6-(N- 2-hydroxyethyl-N-methylamino)-s-triazine-2-yl)amino]2,2'-stilbenedisulfonic acid disodium salt. This particular brightener species is commercially marketed under the tradename Tinopal 5BM-GX by Ciba-Geigy Coφoration. When in the above formula, R\ is anilino, R2 is moφhilino and M is a cation such as sodium, the brightener is 4,4'-bis[(4-anilino-6-moφhilino-s-triazine-2- yl)amino]2,2'-stilbenedisulfonic acid, sodium salt. This particular brightener species is commercially marketed under the tradename Tinopal AMS-GX by Ciba Geigy Coφoration. The specific optical brightener species selected for use in the present invention provide especially effective dye transfer inhibition performance benefits when used in combination with the selected polymeric dye transfer inhibiting agents hereinbefore described. The combination of such selected polymeric materials (e.g., PVNO and/or PVPVI) with such selected optical brighteners (e.g., Tinopal UNPA-GX, Tinopal 5BM- GX and/or Tinopal AMS-GX) provides significantly better dye transfer inhibition in aqueous wash solutions than does either of these two detergent composition components when used alone. Without being bound by theory, it is believed that such brighteners work this way because they have high affinity for fabrics in the wash solution and therefore deposit relatively quick on these fabrics. The extent to which brighteners deposit on fabrics in the wash solution can be defined by a parameter called the "exhaustion coefficient". The exhaustion coefficient is in general as the ratio of a) the brightener material deposited on fabric to b) the initial brightener concentration in the wash liquor. Brighteners with relatively high exhaustion coefficients are the most suitable for inhibiting dye transfer in the context of the present invention. Of course, it will be appreciated that other, conventional optical brightener types of compounds can optionally be used in the present compositions to provide conventional fabric "brightness" benefits, rather than a true dye transfer inhibiting effect. Such usage is conventional and well-known to detergent formulations. The modified polyamines ofthe present invention useful as cotton soil release agents are suitably prepared by the following methods. EXAMPLE 1 Preparation of PEI 1800 E7 The ethoxylation is conducted in a 2 gallon stined stainless steel autoclave equipped for temperature measurement and control, pressure measurement, vacuum and inert gas purging, sampling, and for introduction of ethylene oxide as a liquid. A -20 lb. net cylinder of ethylene oxide (ARC) is set up to deliver ethylene oxide as a liquid by a pump to the autoclave with the cylinder placed on a scale so that the weight change of the cylinder could be monitored. A 750 g portion of polyethyleneimine (PEI) (Nippon Shokubai, Epomin SP-018 having a listed average molecular weight of 1800 equating to about 0.417 moles of polymer and 17.4 moles of nitrogen functions) is added to the autoclave. The autoclave is then sealed and purged of air (by applying vacuum to minus 28" Hg followed by pressurization with nitrogen to 250 psia, then venting to atmospheric pressure). The autoclave contents are heated to 130 °C while applying vacuum. After about one hour, the autoclave is charged with nitrogen to about 250 psia while cooling the autoclave to about 105 °C. Ethylene oxide is then added to the autoclave incrementally over time while closely monitoring the autoclave pressure, temperature, and ethylene oxide flow rate. The ethylene oxide pump is turned off and cooling is applied to limit any temperature increase resulting from any reaction exotherm. The temperature is maintained between 100 and 1 10 °C while the total pressure is allowed to gradually increase during the course ofthe reaction. After a total of 750 grams of ethylene oxide has been charged to the autoclave (roughly equivalent to one mole ethylene oxide per PEI nitrogen function), the temperature is increased to 110 °C and the autoclave is allowed to stir for an additional hour. At this point, vacuum is applied to remove any residual unreacted ethylene oxide. Next, vacuum is continuously applied while the autoclave is cooled to about 50 ° C while introducing 376 g of a 25% sodium methoxide in methanol solution (1.74 moles, to achieve a 10% catalyst loading based upon PEI nitrogen functions). The methoxide solution is sucked into the autoclave under vacuum and then the autoclave temperature controller setpoint is increased to 130 °C. A device is used to monitor the power consumed by the agitator. The agitator power is monitored along with the temperature and pressure. Agitator power and temperature values gradually increase as methanol is removed from the autoclave and the viscosity ofthe mixture increases and stabilizes in about 1 hour indicating that most ofthe methanol has been removed. The mixture is further heated and agitated under vacuum for an additional 30 minutes. Vacuum is removed and the autoclave is cooled to 105 °C while it is being charged with nitrogen to 250 psia and then vented to ambient pressure. The autoclave is charged to 200 psia with nitrogen. Ethylene oxide is again added to the autoclave incrementally as before while closely monitoring the autoclave pressure, temperature, and ethylene oxide flow rate while maintaining the temperature between 100 and 110 °C and limiting any temperature increases due to reaction exotherm. After the addition of 4500 g of ethylene oxide (resulting in a total of 7 moles of ethylene oxide per mole of PEI mtrogen function) is achieved over several hours, the temperature is increased to 110 °C and the mixture stined for an additional hour. The reaction mixture is then collected in nitrogen purged containers and eventually transfened into a 22 L three neck round bottomed flask equipped with heating and agitation. The strong alkali catalyst is neutralized by adding 167 g methanesulfonic acid (1.74 moles). The reaction mixture is then deodorized by passing about 100 cu. ft. of inert gas (argon or nitrogen) through a gas dispersion frit and through the reaction mixture while agitating and heating the mixture to 130 °C. The final reaction product is cooled slightly and collected in glass containers purged with nitrogen. In other preparations the neutralization and deodorization is accomplished in the reactor before discharging the product. EXAMPLE 2 4.7% Quaternization of PEI 1800 E7 To a 500ml erlenmeyer flask equipped with a magnetic stining bar is added poly(ethyleneimine), MW 1800 ethoxylated to a degree of 7 (224g, 0.637 mol nitrogen, prepared as in Example 1) and acetonitrile (Baker, 150g, 3.65 mol). Dimethyl sulfate (Aldrich, 3.8g, 0.030 mol) is added all at once to the rapidly stirring solution, which is then stoppered and stined at room temperature overnight. The acetonitrile is evaporated on the rotary evaporator at ~60°C, followed by a Kugelrohr apparatus (Aldrich) at ~80°C to afford ~220g ofthe desired material as a dark brown viscous liquid. A i 3 C-NMR (D2O) spectrum shows the absence of a peak at ~58ppm conesponding to dimethyl sulfate. A iH-NMR (D2O) spectrum shows the partial shifting ofthe peak at 2.5ppm (methylenes attached to unquaternized nitrogens) to ~3.0ppm. EXAMPLE 3 Oxidation of 4.7% Quaternized PEI 1800 E7 To a 500ml erlenmeyer flask equipped with a magnetic stirring bar is added poly(ethyleneimine), MW 1800 which has been ethoxylated to a degree of 7, and -4.7% quaternized with dimethyl sulfate (121.7g, -0.32 mol oxidizeable nitrogen, prepared as in Example 3), hydrogen peroxide (Aldrich, 40g of a 50 wt% solution in water, 0.588 mol), and water (109.4g). The flask is stoppered, and after an initial exotherm the solution is stirred at room temperature overnight. A 1 H-NMR (D2O) spectrum shows the total shifting ofthe methylene peaks at 2.5-3.0ppm to ~3.5ppm. To the solution is added ~5g of 0.5% Pd on alumina pellets, and the solution is allowed to stand at room temperature for ~3 days. Peroxide indicator paper shows that no peroxide is left in the system. The material is stored as a 46.5% solution in water. EXAMPLE 4 Formation of amine oxide of PEI 1800 E7 To a 500 mL Erlenmeyer flask equipped with a magnetic stirring bar is added polyethyleneimine having a molecular weight of 1800 and ethoxylated to a degree of about 7 ethoxy groups per nitrogen (PEI-1800, E7) (209 g, 0.595 mol nitrogen, prepared as in Example I), and hydrogen peroxide (120 g of a 30 wt % solution in water, 1.06 mol). The flask is stoppered, and after an initial exotherm the solution is stined at room temperature overnight. 1 H-NMR (D2O) spectrum obtained on a sample of the reaction mixture indicates complete conversion. The resonances ascribed to methylene protons adjacent to unoxidized nitrogens have shifted from the original position at -2.5 ppm to -3.5 ppm. To the reaction solution is added approximately 5 g of 0.5% Pd on alumina pellets, and the solution is allowed to stand at room temperature for approximately 3 days. The solution is tested and found to be negative for peroxide by indicator paper. The material as obtained is suitably stored as a 51.1 % active solution in water. EXAMPLE 5 Preparation of PEI 1200 E7 The ethoxylation is conducted in a 2 gallon stined stainless steel autoclave equipped for temperature measurement and control, pressure measurement, vacuum and inert gas purging, sampling, and for introduction of ethylene oxide as a liquid. A -20 lb. net cylinder of ethylene oxide (ARC) is set up to deliver ethylene oxide as a liquid by a pump to the autoclave with the cylinder placed on a scale so that the weight change of the cylinder could be monitored. A 750 g portion of polyethyleneimine (PEI) ( having a listed average molecular weight of 1200 equating to about 0.625 moles of polymer and 17.4 moles of nitrogen functions) is added to the autoclave. The autoclave is then sealed and purged of air (by applying vacuum to minus 28" Hg followed by pressurization with nitrogen to 250 psia, then venting to atmospheric pressure). The autoclave contents are heated to 130 °C while applying vacuum. After about one hour, the autoclave is charged with nitrogen to about 250 psia while cooling the autoclave to about 105 °C. Ethylene oxide is then added to the autoclave incrementally over time while closely monitoring the autoclave pressure, temperature, and ethylene oxide flow rate. The ethylene oxide pump is turned off and cooling is applied to limit any temperature increase resulting from any reaction exotherm. The temperature is maintained between 100 and 110 °C while the total pressure is allowed to gradually increase during the course ofthe reaction. After a total of 750 grams of ethylene oxide has been charged to the autoclave (roughly equivalent to one mole ethylene oxide per PEI nitrogen function), the temperature is increased to 1 10 ° C and the autoclave is allowed to stir for an additional hour. At this point, vacuum is applied to remove any residual unreacted ethylene oxide. Next, vacuum is continuously applied while the autoclave is cooled to about 50 ° C while introducing 376 g of a 25% sodium methoxide in methanol solution (1.74 moles, to achieve a 10% catalyst loading based upon PEI nitrogen functions). The methoxide solution is sucked into the autoclave under vacuum and then the autoclave temperature controller setpoint is increased to 130 °C. A device is used to monitor the power consumed by the agitator. The agitator power is monitored along with the temperature and pressure. Agitator power and temperature values gradually increase as methanol is removed from the autoclave and the viscosity ofthe mixture increases and stabilizes in about 1 hour indicating that most ofthe methanol has been removed. The mixture is further heated and agitated under vacuum for an additional 30 minutes. Vacuum is removed and the autoclave is cooled to 105 °C while it is being charged with nitrogen to 250 psia and then vented to ambient pressure. The autoclave is charged to 200 psia with nitrogen. Ethylene oxide is again added to the autoclave incrementally as before while closely monitoring the autoclave pressure, temperature, and ethylene oxide flow rate while maintaining the temperature between 100 and 1 10 °C and limiting any temperature increases due to reaction exotherm. After the addition of 4500 g of ethylene oxide (resulting in a total of 7 moles of ethylene oxide per mole of PEI nitrogen function) is achieved over several hours, the temperature is increased to 110 °C and the mixture stined for an additional hour. The reaction mixture is then collected in nitrogen purged containers and eventually transfened into a 22 L three neck round bottomed flask equipped with heating and agitation. The strong alkali catalyst is neutralized by adding 167 g methanesulfonic acid (1.74 moles). The reaction mixture is then deodorized by passing about 100 cu. ft. of inert gas (argon or nitrogen) through a gas dispersion frit and through the reaction mixture while agitating and heating the mixture to 130 °C. The final reaction product is cooled slightly and collected in glass containers purged with nitrogen. In other preparations the neutralization and deodorization is accomplished in the reactor before discharging the product. EXAMPLE 6 9.7% Quaternization of PEI 1200 E7 To a 500ml erlenmeyer flask equipped with a magnetic stirring bar is added poly(ethyleneimine), MW 1200 ethoxylated to a degree of 7 (248.4g, 0.707 mol nitrogen, prepared as in Example 5) and acetonitrile (Baker, 200 mL). Dimethyl sulfate (Aldrich, 8.48g, 0.067 mol) is added all at once to the rapidly stirring solution, which is then stoppered and stined at room temperature overnight. The acetonitrile is evaporated on the rotary evaporator at ~60°C, followed by a Kugelrohr apparatus (Aldrich) at ~80°C to afford ~220g ofthe desired material as a dark brown viscous liquid. A 13 C-NMR (D 2 O) spectrum shows the absence of a peak at ~58ppm conesponding to dimethyl sulfate. A iH-NMR (D2O) spectrum shows the partial shifting ofthe peak at 2.5ppm (methylenes attached to unquatemized nitrogens) to ~3.0ppm. EXAMPLE 7 4.7% Oxidation of 9.5% Quaternized PEI 1200 E7 To a 500ml erlenmeyer flask equipped with a magnetic stirring bar is added poly(ethyleneimine), MW 1200 which has been ethoxylated to a degree of 7, and -9.5% quaternized with dimethyl sulfate (144g, -0.37 mol oxidizeable nitrogen, prepared as in Example 6), hydrogen peroxide (Aldrich, 35.4g of a 50 wt% solution in water, 0.52 mol), and water (lOOg). The flask is stoppered, and after an initial exotherm the solution is stined at room temperature overnight. A 1 H-NMR (D2O) spectrum shows the total shifting ofthe methylene peaks at 2.5-3.0ppm to ~3.5ppm. To the solution is added just enough sodium bisulfite as a 40% water solution to bring the residual peroxide level down to 1 -5ppm. The sodium sulfate which forms causes an aqueous phase to separate which contains salts, but little or no organics. The aqueous salt phase is removed and the desired oxidized polyethyleneimine derivative is obtained and stored as a 52% solution in water. EXAMPLE 8 Preparation of PEI 600 ETQ The ethoxylation is conducted in a 2 gallon stined stainless steel autoclave equipped for temperature measurement and control, pressure measurement, vacuum and inert gas purging, sampling, and for introduction of ethylene oxide as a liquid. A -20 lb. net cylinder of ethylene oxide (ARC) is set up to deliver ethylene oxide as a liquid by a pump to the autoclave with the cylinder placed on a scale so that the weight change of the cylinder could be monitored. A 250 g portion of polyethyleneimine (PEI) (Nippon Shokubai, having a listed average molecular weight of 600 equating to about 0.417 moles of polymer and 6.25 moles of nitrogen functions) is added to the autoclave. The autoclave is then sealed and purged of air (by applying vacuum to minus.28" Hg followed by pressurization with nitrogen to 250 psia, then venting to atmospheric pressure). The autoclave contents are heated to 130 °C while applying vacuum. After about one hour, the autoclave is charged with nitrogen to about 250 psia while cooling the autoclave to about 105 °C. Ethylene oxide is then added to the autoclave incrementally over time while closely monitoring the autoclave pressure, temperature, and ethylene oxide flow rate. The ethylene oxide pump is turned off and cooling is applied to limit any temperature increase resulting from any reaction exotherm. The temperature is maintained between 100 and 1 10 °C while the total pressure is allowed to gradually increase during the course ofthe reaction. After a total of 275 grams of ethylene oxide has been charged to the autoclave (roughly equivalent to one mole ethylene oxide per PEI nitrogen function), the temperature is increased to 1 10 °C and the autoclave is allowed to stir for an additional hour. At this point, vacuum is applied to remove any residual unreacted ethylene oxide. Next, vacuum is continuously applied while the autoclave is cooled to about 50 ° C while introducing 135 g of a 25% sodium methoxide in methanol solution (0.625 moles, to achieve a 10% catalyst loading based upon PEI nitrogen functions). The methoxide solution is sucked into the autoclave under vacuum and then the autoclave temperature controller setpoint is increased to 130 °C. A device is used to monitor the power consumed by the agitator. The agitator power is monitored along with the temperature and pressure. Agitator power and temperature values gradually increase as methanol is removed from the autoclave and the viscosity ofthe mixture increases and stabilizes in about 1 hour indicating that most ofthe methanol has been removed. The mixture is further heated and agitated under vacuum for an additional 30 minutes. Vacuum is removed and the autoclave is cooled to 105 °C while it is being charged with nitrogen to 250 psia and then vented to ambient pressure. The autoclave is charged to 200 psia with nitrogen. Ethylene oxide is again added to the autoclave incrementally as before while closely monitoring the autoclave pressure, temperature, and ethylene oxide flow rate while maintaining the temperature between 100 and 110 °C and limiting any temperature increases due to reaction exotherm. After the addition of approximately 5225 g of ethylene oxide (resulting in a total of 20 moles of ethylene oxide per mole of PEI nitrogen function) is achieved over several hours, the temperature is increased to 110 °C and the mixture stirred for an additional hour. The reaction mixture is then collected in nitrogen purged containers and eventually transfened into a 22 L three neck round bottomed flask equipped with heating and agitation. The strong alkali catalyst is neutralized by adding 60 g methanesulfonic acid (0.625 moles). The reaction mixture is then deodorized by passing about 100 cu. ft. of inert gas (argon or nitrogen) through a gas dispersion frit and through the reaction mixture while agitating and heating the mixture to 130 °C. The final reaction product is cooled slightly and collected in glass containers purged with nitrogen. In other preparations the neutralization and deodorization is accomplished in the reactor before discharging the product. EXAMPLE 9 Preparation of Non-cotton Soil Release Polymers Synthesis of Sodium 2-(2.3-Dihvdroxypropoxy)ethanesulfonate Monomer To a 500ml, three neck, round bottom flask equipped with a magnetic stirring bar, modified Claisen head, condenser (set for distillation), thermometer, and temperature controller (Therm-O-WatchTM ^ J2R) \ S added isethionic acid, sodium salt (Aldrich, 50.0g, 0.338 mol), sodium hydroxide (2.7g, 0.0675 mol), and glycerin (Baker, 310.9g, 3.38 mol). The solution is heated at 190°C under argon overnight as water distills from the reaction mixture. A l 3 C-NMR(DMSO-d6) shows that the reaction is complete by the virtual disappearance of the isethionate peaks at -53.5 ppm and -57.4 ppm. and the emergence of product peaks at -51.4 ppm (-CH2SO3Na) and -67.5 ppm (CH2CH2SO3Na). The solution is cooled to ~100°C and neutralized to pH 7 with methanesulfonic acid (Aldrich). The desired, neat material is obtained by adding 0.8 mol% of potassium phosphate, monobasic as buffer and heating on a Kugelrohr apparatus (Aldrich) at 200°C for - 3 hrs. at -1 mm Hg to afford 77g of yellow waxy solid. As an alternative, not all ofthe glycerin is removed before use in making the oligomers. The use of glycerin solutions of SEG can be a convenient way of handling this sulfonated monomer. EXAMPLE 10 Synthesis of Sodium 2-[2-(2-Hydroxyethoxy)ethoxylethanesulfonate Monomer To a IL, three neck, round bottom flask equipped with a magnetic stirring bar, modified Claisen head, condenser (set for distillation), thermometer, and temperature controller (Therm-O- Watch™, I 2 R) is added isethionic acid, sodium salt (Aldrich, lOO.Og, 0.675 mol) and distilled water (-90 ml). After dissolution, one drop of hydrogen peroxide (Aldrich, 30% by wt. in water) is added to oxidize traces of bisulfite. The solution is stirred for one hour. A peroxide indicator strip shows a very weak positive test. Sodium hydroxide pellets (MCB, 2.5g, 0.0625 mol) are added, followed by diethylene glycol (Fisher, 303.3g, 2.86 mol). The solution is heated at 190C° under argon overnight as water distills from the reaction mixture. A l 3 C-NMR(DMSO-d6) shows that the reaction is complete by the disappearance ofthe isethionate peaks at -53.5 ppm and -57.4 ppm. The solution is cooled to room temperature and neutralized to pH 7 with 57.4g of a 16.4% solution of p-toluenesulfonic acid monohydrate in diethylene glycol. (Alternatively, methanesulfonic acid may be used.) The 1 3 C-NMR spectrum ofthe product shows resonances at -51 ppm (-CH2SO3Na) , ~60ppm (- CH2OH), and at -69 ppm, -72 ppm, and -77 ppm for the remaining four methylenes. Small resonances are also visible for the sodium p-toluenesulfonate which formed during neutralization. The reaction affords 45 lg of a 35.3% solution of sodium 2-[2-(2- hydroxyethoxy)ethoxy]ethanesulfonate in diethylene glycol. The excess diethylene glycol is removed by adding 0.8 mol% of monobasic potassium phosphate (Aldrich) as a buffer and heating on a Kugelrohr apparatus (Aldrich) at 150C° for - 3 hrs. at -1 mm Hg to give the desired "SE3" (as defined herein above) as an extremely viscous oil or glass. EXAMPLE 11 Synthesis of Sodium 2- (2-[2-(2-Hvdroxyethoxy)ethoxy]ethoχy I ethanesulfonate Monomer To a IL, three neck, round bottom flask equipped with a magnetic stirring bar, modified Claisen head, condenser (set for distillation), thermometer, and temperature controller (Therm-O- Watch™, I 2 R) is added isethionic acid, sodium salt (Aldrich, 205.0g, 1.38 mol) and distilled water (-200 ml). After dissolution, one drop of hydrogen peroxide (Aldrich, 30% by wt. in water) is added to oxidize traces of bisulfite. The solution is stined for one hour. A peroxide indicator strip shows a very weak positive test. Sodium hydroxide pellets (MCB, 5.5g, 0.138 mol) are added, followed by triethylene glycol (Aldrich, 448.7g, 3.0 mol). Optionally, the triethylene glycol can be purified by heating with strong base such as NaOH until color stabilizes and then distilling off the purified glycol for use in the synthesis. The solution is heated at 190C° under argon overnight as water distills from the reaction mixture. A l 3 C-NMR(DMSO- dfj) shows that the reaction is complete by the disappearance ofthe isethionate peaks at -53.5 ppm and -57.4 ppm, and the emergence of product peaks at -51 ppm (- CH2SO3Na) , ~60ppm (-CH2OH), and at -67 ppm, -69 ppm, and -72 ppm for the remaining methylenes. The solution is cooled to room temperature and neutralized to pH 7 with methanesulfonic acid (Aldrich). The reaction affords 650g of a 59.5% solution of sodium 2-{2-[2-(2-hydroxyethoxy)ethoxy]ethoxy}ethanesulfonate in triethylene glycol. The excess triethylene glycol is removed by adding 0.8 mol% of monobasic potassium phosphate (Aldrich) as a buffer and heating on a Kugelrohr apparatus (Aldrich) at 180C° for - 5.5 hrs. at -1 mm Hg to give the desired material as a brown solid. It is found that a more soluble buffer can be more effective in controlling pH during the stripping of excess triethylene glycol. One example of such a more soluble buffer is the salt of N-methylmoφholine with methanesulfonic acid. Alternatively, the pH can be controlled by frequent or continuous addition of acid such as methanesulfonic acid to maintain a pH near neutral during the stripping of excess glycol. The material is believed to contain a low level ofthe disulfonate arising from reaction of both ends of the triethylene glycol with isethionate. However, the crude material is used without further purification as an anionic capping groups for polymer preparations. Other preparations use a larger excess of triethylene glycol such as 5 to 10 moles per mole of isethionate. EXAMPLE 12 Synthesis of an Oligomer of Sodium 2-r2-(2-Hvdroxyethoxy)ethoxy]ethanesulfonate, Dimethyl Terephthalate, Sodium 2-(2.3-Dihvdroxypropoxy ' )ethanesulfonate, Glycerin, Ethylene Glycol, and Propylene Glvcol ) To a 250ml, three neck, round bottom flask equipped with a magnetic stirring bar, modified Claisen head, condenser (set for distillation), thermometer, and temperature controller (Therm-O- Watch®, I 2 R) is added sodium 2-[2-(2- hydroxyethoxy)ethoxy]ethanesulfonate (7.0g, 0.030 mol), dimethyl terephthalate (14.4g, 0.074 mol), sodium 2-(2,3-dihydroxypropoxy)ethanesulfonate (3.3g, 0.015 mol), glycerin (Baker, 1.4g, 0.015 mol), ethylene glycol (Baker, 14.0g, 0.225 mol), propylene glycol (Fisher, 17.5g, 0.230 mol), and titanium (IV) propoxide (0.01 g, 0.02% of total reaction weight). This mixture is heated to 180°C and maintained at that temperature overnight under argon as methanol and water distill from the reaction vessel. The material is transfened to a 500ml, single neck, round bottom flask and heated gradually over about 20 minutes to 240°C in a Kugelrohr apparatus (Aldrich) at about 2 mm Hg and maintained there for 1.5 hours. The reaction flask is then allowed to air cool quite rapidly to near room temperature under vacuum (-30 min.) The reaction affords 21.3g ofthe desired oligomer as a brown glass. A l 3 C-NMR(DMSO-dg) shows a resonance for -C(O)OCH2CH2O(O)C- at -63.2 ppm (diester) and a resonance for - C(O)OCH2CH2OH at -59.4 ppm (monoester). The ratio ofthe diester peak height to the monoester peak height is about 10. Resonances at -51.5 ppm and ~51.6 ppm representing the sulfoethoxy groups (-CH2SO3Na) are also present. A lH- NMR(DMSO-dg) shows a resonance at ~7.9 ppm representing terephthalate aromatic hydrogens. Analysis by hydrolysis-gas chromatography shows that the mole ratio of incoφorated ethylene glycol to incorporated propylene glycol is 1.7:1. It also shows that about 0.9% ofthe final polymer weight consists of glycerin. If all glycerin monomer has been incoφorated as esters of glycerin, it would represent approximately 4% of final oligomer weight. The solubility is tested by weighing a small amount of material into a vial, adding enough distilled water to make a 35% by weight solution, and agitating the vial vigorously. The material is readily soluble under these conditions. EXAMPLE 13 Synthesis of an Oligomer of Sodium 2-[2-(2-Hvdroxyethoxy)ethoxylethanesulfonate. Dimethyl Terephthalate. Sodium 2-(2,3-Dihvdroxypropoxy)ethanesulfonate, Ethylene Glvcol. and Propylene Glvcol) To a 250ml, three neck, round bottom flask equipped with a magnetic stirring bar, modified Claisen head, condenser (set for distillation), thermometer, and temperature controller (Therm-O- Watch®, I 2 R) is added sodium 2-[2-(2- hydroxyethoxy)ethoxy]ethanesulfonate (7.0g, 0.030 mol), dimethyl terephthalate (14.4g, 0.074 mol), sodium 2-(2,3-dihydroxypropoxy)ethanesulfonate (6.6g, 0.030 mol), ethylene glycol (Baker, 14.0g, 0.225 mol), propylene glycol (Fisher, 18.3g, 0.240 mol), and titanium (IV) propoxide (0.01 g, 0.02% of total reaction weight). This mixture is heated to 180°C and maintained at that temperature overnight under argon as methanol distills from the reaction vessel. The material is transfened to a 500ml, single neck, round bottom flask and heated gradually over about 20 minutes to 240°C in a Kugelrohr apparatus (Aldrich) at about 0.1 mm Hg and maintained there for 1 10 minutes. The reaction flask is then allowed to air cool quite rapidly to near room temperature under vacuum (-30 min.) The reaction affords 24.4g ofthe desired oligomer as a brown glass. A l 3 C-NMR(DMSO-d6) shows a resonance for -C(O)OCH2CH2O(O)C- at -63.2 ppm (diester) and a resonance for -C(O)OCH2CH2OH at -59.4 ppm (monoester). The ratio ofthe diester peak to monoester peak is measured to be 8. Resonances at -51.5 ppm and -51.6 ppm representing the sulfoethoxy groups (-CH2SO3Na) are also present. A lH-NMR(DMSO-d6) shows a resonance at -7.9 ppm representing terephthalate aromatic hydrogens. Analysis by Hydrolysis-GC shows that the mole ratio of incoφorated ethylene glycol to incoφorated propylene glycol is 1.6:1. The solubility is tested by weighing a small amount of material into a vial, adding enough distilled water to make a 35% by weight solution, and agitating the vial vigorously. The material is readily soluble under these conditions. EXAMPLE 14 Synthesis of an Oligomer of Sodium 2-[2-(2-Hvdroxyethoxy)ethoχy]ethanesulfonate. Dimethyl Terephthalate, Sodium 2-(2,3-Dihvdroxypropoxy)ethanesulfonate. Glycerin, Ethylene Glvcol. and Propylene Glvcol ) To a 250ml, three neck, round bottom flask equipped with a magnetic stirring bar, modified Claisen head, condenser (set for distillation), thermometer, and temperature controller (Therm-O- Watch®, I 2 R) is added sodium 2-[2-(2- hydroxyethoxy)ethoxy]ethanesulfonate (7.0g, 0.030 mol), dimethyl terephthalate (9.6g, 0.049 mol), sodium 2-(2,3-dihydroxypropoxy)ethanesulfonate (2.2g, 0.010 mol), glycerin (Baker, 1.8g, 0.020 mol), ethylene glycol (Baker, 6.1g, 0.100 mol), propylene glycol (Fisher, 7.5g, 0.100 mol), and titanium (IV) propoxide (0.0 lg, 0.02% of total reaction weight). This mixture is heated to 180°C and maintained at that temperature overnight under argon as methanol distills from the reaction vessel. The material is transfened to a 250ml, single neck, round bottom flask and heated gradually over about 20 minutes to 240°C in a Kugelrohr apparatus (Aldrich) at about 3 mm Hg and maintained there for 1.5 hours. The reaction flask is then allowed to air cool quite rapidly to near room temperature under vacuum (-30 min.) The reaction affords 18.1g ofthe desired oligomer as a brown glass. A l 3 C-NMR(DMSO-d(;) shows a resonance for -C(O)OCH2CH2O(O)C- at -63.2 ppm (diester). A resonance for - C(O)OCH2CH2OH at -59.4 ppm (monoester) is not detectable and is at least 12 times smaller than the diester peak. Resonances at -51.5 ppm and -51.6 ppm representing the sulfoethoxy groups (-CH2SO3Na) are also present. A 1 H-NMR(DMSO-d6) shows a resonance at -7.9 ppm representing terephthalate aromatic hydrogens. Analysis by Hydrolysis-GC shows that the mole ratio of incoφorated ethylene glycol to incoφorated propylene glycol is 1.6:1. The incoφorated glycerin is found to be 0.45 weight% ofthe final polymer. The solubility is tested by weighing a small amount of material into a vial, adding enough distilled water to make a 35% by weight solution, and agitating the vial vigorously. The material is readily soluble under these conditions. EXAMPLE 15 Synthesis of an Oligomer of Sodium 2-[2-(2-Hvdroxyethoxy)ethoxy]ethanesulfonate. Dimethyl Terephthalate, Sodium 2-(2,3-Dihvdroxypropoxy)ethanesulfonate, Glycerol. Ethylene Glvcol, and Propylene Glycol) To a 250ml, three neck, round bottom flask equipped with a magnetic stirring bar, modified Claisen head, condenser (set for distillation), thermometer, and temperature controller (Therm-O- Watch®, I 2 R) is added sodium 2-[2-(2- hydroxyethoxy)ethoxy]ethanesulfonate (2.7g, 0.011 mol, as in Example 2), dimethyl terephthalate (12.0g, 0.062 mol, Aldrich), sodium 2-(2,3- dihydroxypropoxy)ethanesulfonate (5.0g, 0.022 mol, as in Example 1), glycerol (Baker, 0.50g, 0.0055 mol), ethylene glycol (Baker, 6.8g, 0.110 mol), propylene glycol (Baker, 8.5g, 0.112 mol), and titanium (IV) propoxide (0.0 lg, 0.02% of total reaction weight). This mixture is heated to 180°C and maintained at that temperature overnight under argon as methanol and water distill from the reaction vessel. The material is transfened to a 500ml, single neck, round bottom flask and heated gradually over about 20 minutes to 240°C in a Kugelrohr apparatus (Aldrich) at about 0.5 mm Hg and maintained there for 150 minutes. The reaction flask is then allowed to air cool quite rapidly to near room temperature under vacuum (-30 min.) The reaction affords 16.7g ofthe desired oligomer as a brown glass. A l 3 C-NMR(DMSO-d f j) shows a resonance for - C(O)OCH2CH2O(O)C- at -63.2 ppm (diester) and a resonance for -C(O)OCH2CH2OH at -59.4 ppm (monoester). The ratio ofthe peak height for the diester resonance to that ofthe monoester resonance is measured to be 6.1. Resonances at -51.5 ppm and -51.6 ppm representing the sulfoethoxy groups (-CH2SO3Na) are also present. A lH- NMR(DMSO-d6) shows a resonance at -7.9 ppm representing terephthalate aromatic hydrogens. Analysis by hydrolysis-gas chromatography shows that the mole ratio of incoφorated ethylene glycol to incoφorated propylene glycol is 1.42: 1. The solubility is tested by weighing a small amount of material into a vial, adding enough distilled water to make a 35% by weight solution, and agitating the vial vigorously. The material is readily soluble under these conditions. A ~9g sample of this material is further heated at 240°C in a Kugelrohr apparatus at about 0.5 mm Hg and maintained there for 80 minutes. A l 3 C-NMR(DMSO-d6) shows no detectable peak for monoester at -59.4 ppm. The peak for diester at -63.2 ppm is at least 1 1 times larger than the monoester peak. The solubility of this material is tested as above and it is also found to be readily soluble under these conditions. EXAMPLES 16 - 27 The following describe high density liquid detergent compositions according to the present invention: TABLE I weight % 1. Minors - includes optical brightener and enzymes (protease, lipase, cellulase, and amylase). 2. Non-Cotton Soil Release Polymer according to U.S. Patent 4,968,451 , Scheibel et al. 3. PEI 1800 E7 amine oxide as according to Example 4 herein above. TABLE II Ingredients Weight % 1 • C 12-C 13 alkyl E9 ethoxylate as sold by Shell Oil Co. 2. Bacillus amyloliquefaciens subtilisin as described in WO 95/10615 published April 20, 1995 by Genencor International. 3. Derived from Humicola lanuginosa and commercially available from Novo. 4. Disclosed in WO 9510603 A and available from Novo. 5. PEI 1200 E74.7% oxidition 9.5% quaternization as described in Example 7 above. 6. Terephthalate co-polymer as disclosed in U.S. Patent 4,968,451 , Scheibel et al., issued November 6, 1990. 7. As described in Example 12 herein above. 8. As described in Example 14 herein above. TABLE III Ingredients Weight % 23 24 25 26 27 1. C 12-C 13 alkyl E9 ethoxylate as sold by Shell Oil Co. 2. Bacillus amyloliquefaciens subtilisin as described in WO 95/10615 published April 20, 1995 by Genencor International. 3. Derived from Humicola lanuginosa and commercially available from Novo. 4. Disclosed in WO 9510603 A and available from Novo. 5. PEI 600 E20 as described in Example 8 above. 6. Terephthalate co-polymer as disclosed in U.S. Patent 4,968,451, Scheibel et al., issued November 6, 1990. EXAMPLES 28 - 31 Compositions ofthe present invention are also prepared by preparing high density granular formulas according to this example utilizing the cotton soil release polymers alone or in combination with other soil release polymers. TABLE IV weight % Ingredient 28 29 30 31 1. Non-cotton soil release polymer according to U.S. Patent 4,968,451 , Scheibel et al., issued November 6, 1990. 2. Non-cotton soil release polymer according to U.S. Patent 5,415,807, Gosselink, Pan, Kellett and Hall, issued May 16, 1995. 3. Non-cotton soil release polymer according to U.S. Patent 4,702,857, Gosselink, issued October 27, 1987. 4. Cotton soil release agent according to Example 4. 5. Balance to 100% can, for example, include minors like optical brightener, perfume, suds suppresser, soil dispersant, protease, lipase, cellulase, chelating agents, dye transfer inhibiting agents, additional water, and fillers, including CaCθ3, talc, silicates, etc. EXAMPLES 32-35 Suitable granular laundry detergent compositions comprising the cotton soil release agents ofthe present invention can be formulated without linear alkyl benezene sulfonates (LAS), for example: TABLE V weight % Ingredient 32 33 34 35 1. As sold by the Shell Oil Co. 2. Non-cotton soil release polymer according to U.S. Patent 4,968,451, Scheibel et al., issued November 6, 1990. 3. Non-cotton soil release polymer according to U.S. Patent 5,415,807, Gosselink, Pan, Kellett and Hall, issued May 16, 1995. 4. Non-cotton soil release polymer according to U.S. Patent 4,702,857, Gosselink, issued October 27, 1987. 5. Cotton soil release agent according to Example 4. 6. Balance to 100% can, for example, include minors like optical brightener, perfume, suds suppresser, soil dispersant, protease, lipase, cellulase, chelating agents, dye transfer inhibiting agents, additional water, and fillers, including CaC03, talc, silicates, etc. Aqueous crutcher mixes of heat and alkali stable components ofthe detergent compositions are prepared and spray-dried and the other ingredients are admixed so that they contain the ingredients tabulated at the levels shown. The soil release agents ofthe present invention can be, for example, pulverized and admixed in an amount sufficient for use at a level of 0.5% by weight in conjunction with the detergent compositions. An example ofthe method ofthe present invention is outlined below: The detergent granules comprising cotton soil release polymers are added (99.5 parts/0.5 parts by weight, respectively) together with a 6 lb. load of previously laundered fabrics (load composition: 10 wt % polyester fabrics/50 wt % polyester-cotton/40 wt % cotton fabrics) to a Sears KENMORE washing machine. Actual weights of detergent and soil release agent compositions are take to provide a 995 ppm concentration ofthe former and 5 ppm concentration ofthe latter in the 17 gallon (65 liter) water-fill machine. The water used has 7 grains/gallon hardness and a pH of 7 to 7.5 prior to (abut 9 to about 10.5 after) addition ofthe detergent and ester compositions. The fabrics are laundered at 35° C (95° F) for a full cycle (12 min.) and rinsed at 21 ° C (70° F). the fabrics are then line dried and are exposed to a variety of soils (by wear or controlled application). The entire cycle of laundering and soiling is repeated several times for each of the detergent compositions. Separate fabric bundles are reserved for use with each ofthe detergent compositions. All cotton-containing fabrics display significantly improved whiteness during laundering compared with fabrics which have not been exposed to the compositions of the present invention. Cotton soil release agents ofthe present invention are especially useful in conventional laundry detergent compositions such as those typically found in granular detergents or laundry bars. U.S. Patent 3,178,370, Okenfuss, issued April 13, 1965, describes laundry detergent bars and processes for making them. Philippine Patent 13,778, Anderson, issued September 23, 1980, describes synthetic detergent laundry bars. Methods for making laundry detergent bars by various extrusion methods are well known in the art. EXAMPLE 36 Ingredients Weight % C12 linear alkyl benzene sulfonate 30 Phosphate (as sodium tripolyphosphate) 7 Sodium carbonate 25 Sodium pyrophosphate 7 Coconut monoethanolamide 2 Zeolite A, (0.1-10 micron) 5 Carboxycellulose 0.2 Ethylenediamine disuccinate chelant (EDDS) 0.4 Polyacrylate (MW = 1400) 0.2 Nonanolyoxybenzenesulfonate 5 Cotton Soil release agent 1 0.5 Non-cotton soil release agent 2 0.5 Sodium percarbonate 3 5 Brightener, perfume 0.2 Protease 0.3 Calcium sulfate 1 Magnesium sulfate 1 Water 4 Filler 4 Balance to 100 1. Soil release polymer according to Example 7. 2. Non-cotton soil release agent according to U.S. Patent 4,968,451, J.J. Scheibel and E.P. Gosselink, issued November 6, 1990. 3. Average particle size of 400 to 1200 microns. 4. Can be selected from convenient materials such as Calcium carbonate, talc, clay, silicates, and the like. EXAMPLES 37 - 38 The detergent bars are processed in conventional soap or detergent bar making equipment as commonly used in the art. The soil release agent is pulverized and admixed in an amount sufficient for use at a level of 0.5% by weight in conjunction with the detergent compositions. TABLE V Laundry bars suitable for hand-washing soiled fabrics are prepared by standard extrusion processes and comprise the following: weight % 1. Non-cotton soil release polymer according to U.S. Patent 4,968,451 , Scheibel et al., issued November 6, 1990. 2. Cotton soil release agent according to Example 4. 3. Cotton soil release agent according to Example 5. 4. Can be selected from convenient materials such as Calcium carbonate, talc, clay, silicates, and the like. EXAMPLES 39 - 42 1. C45 ethoxylated (7) alcohol as sold by Shell Oil Co. 2. As described in Example 4 hereinabove. 3. Soil release agent as disclosed in U.S. 5,415,807, Gosselink et al., issued May 16, 1995. EXAMPLES 43 - 46 Granular Laundry Detergent Compositions Weight % Ingredients 43 44 45 46 1. C45 ethoxylated (7) alcohol as sold by Shell Oil Co. 2. As described in Example 1 hereinabove. 3. Soil release agent as disclosed in U.S. 5,415,807, Gosselink et al., issued May 16, 1995. 4. Zinc phthalocyanine sulfonate photobleach according to U.S. Patent 4,033,718 Holcombe et al., issued July 5, 1977.

Claims: WHAT IS CLAIMED IS: 1. A laundry detergent composition comprising: a) at least 0.01 % to 95% by weight, of a detersive surfactant selected from the group consisting of anionic, nonionic, cationic, zwitterionic, and ampholytic surfactants, and mixtures thereof; b) from 0.01 to 10% by weight, preferably from 1% to 5% of a soil release polymer having effective soil release on non-cotton fabric; c) optionally from 0.05 to 30% by weight, of a bleach; d) from 0.01 to 10% by weight, a water-soluble or dispersible, modified polyamine cotton soil release agent comprising a polyamine backbone conesponding to the formula: r 1 I [H 2 N-R] tt f i -[N-R] m -[N-R] n -NH 2 having a modified polyamine formula V( n + i)W m Y n Z or a polyamine backbone conesponding to the formula: having a modified polyamine formula k is less than or equal to n, said polyamine backbone prior to modification has a molecular weight greater than 200 daltons, wherein i) V units are terminal units having the formula: E-N-R — or E-N u- x R — or E-N t-R — I I or I E E E ii) W units are backbone units having the formula: iii) Y units are branching units having the formula: iv) Z units are terminal units having the formula: wherein backbone linking R units are selected from the group consisting of C2-C12 alkylene, C4-C12 alkenylene, C3-C12 hydroxyalkylene, C4- C12 dihydroxy-alkylene, Cg-Ci2 dialkylarylene, -(R10) X R1-, - (RlO) x R5(ORl) x -, -(CH 2 CH(OR2)CH 2 0) z - (Rlθ) y Rl(OCH2CH(OR 2 )CH2)w-, -C(0)(R 4 ) r C(0)-, CH2CH(0R 2 )CH2-, and mixtures thereof, preferably C2-C12 alkylene, C3-C12 hydroxyalkylene, C4-C12 dihydroxyalkylene, Cg-Ci2 dialkylarylene, -(Rlθ) x Rl -, -(Rlθ) x R5(ORl) x -, (CH 2 CH(OH)CH 2 0) z (Rl 0) y Rl (OCH 2 CH(OH)CH2)w-> CH2CH(OR 2 )CH2-, and mixtures thereof, more preferably C2-C12 alkylene, C3-C 12 hydroxyalkylene, C4-C 12 dihydroxyalkylene, (Rlθ) x Rl-, -(R10) X R5-(OR1) X -, -(CH 2 CH(OH)CH 2 O) z - (Rlθ) y Rl(OCH2CH(OH)CH2)w-> and mixtures thereof, most preferably C2-C12 alkylene, and mixtures thereof; wherein Rl is C2-C6 alkylene, preferably ethylene, and mixtures thereof; R 2 is hydrogen, -(Rlθ) x B, and mixtures thereof, preferably hydrogen; R 3 is Cj-Qg alkyl, C7-C12 arylalkyl, C7-C12 alkyl substituted aryl, C6-C12 aryl, and mixtures thereof, C\-Cβ alkyl and mixtures thereof, more preferably methyl; R 4 is C1-C12 alkylene, C4-C12 alkenylene, Cg-Ci2 arylalkylene, C6-C10 arylene, and mixtures thereof, preferably C2-C12 alkylene, Cg-Ci2 arylalkylene, and mixtures thereof, more preferably, ethylene, butylene, and mixtures thereof; R^ is C1-C12 alkylene, C3-C12 hydroxyalkylene, C4-C12 dihydroxy-alkylene, Cg-Ci2 dialkylarylene, -C(O)-, - C(O)NHR6NHC(O)-, -R 1 (OR 1 )-, -C(0)(R4) r C(0)-, - CH 2 CH(OH)CH 2 -, CH 2 CH(OH)CH 2 0(RlO) y RlOCH2CH(OH)CH2-, and mixtures thereof, preferably ethylene, -C(O)-, -C(0)NHR6NHC(0)-, -R 1 (OR 1 ) y -, -(CH2CH(OH)CH 2 0) z (Rlθ) y Rl(OCH2CH(OH)-CH2) w -, - CH2CH(OH)CH2-, and mixtures thereof, more preferably - CH 2 CH(OH)CH2S R 6 is C 2 -C 12 alkylene or C 6 -Cι 2 arylene; E units are selected from the group consisting of hydrogen, C1-C22 alkyl, C3-C22 alkenyl, C7-C22 arylalkyl, C2-C22 hydroxyalkyl, -(CH2) p Cθ2M, - (CH 2 ) q S0 3 M, -CH(CH2C0 2 M)C0 2 M, -(CH 2 ) p Pθ3M, - (Rlθ) x B, -C(0)R 3 , and mixtures thereof; preferably hydrogen, C3-C22 hydroxyalkyl, benzyl, C1-C22 alkyl, -(Rlθ) x B, -C(0)R 3 , -(CH 2 ) p C0 2 - M + , -(CH2) q Sθ3-M + , -CH(CH 2 C0 2 M)-Cθ2M and mixtures thereof, more preferably hydrogen, Q-C22 alkyl, -(Rlθ) x B, -C(0)R 3 , and mixtures thereof, most preferably -(Rlθ) x B; provided that when any E unit of a nitrogen is a hydrogen, said nitrogen is not also an N-oxide; B is hydrogen, C!-C 6 alkyl, -(CH 2 ) q S0 3 M, -(CH 2 ) p -C0 2 M, - (CH2) q (CHSθ3M)CH 2 Sθ3M, -(CH 2 )q(CHS0 2 M)CH2-Sθ3M, - (CH2) p P03M, -PO3M, and mixtures thereof, preferably hydrogen, Ci-Cβ alkyl, -(CH 2 )qS0 3 M, -(CH 2 ) q (CHSθ3M)-CH 2 Sθ3M, - (CH2) q (CHSθ2M)CH2Sθ3M, and mixtures thereof, more preferably hydrogen, -(CH2)qSθ3M, and mixtures thereof, most preferably hydrogen; M is hydrogen or a water soluble cation in sufficient amount to satisfy charge balance; X is a water soluble anion; m has the value from 4 to 400; n has the value from 0 to 200; p has the value from 1 to 6, q has the value from 0 to 6; r has the value of 0 or 1 ; w has the value 0 or 1 ; x has the value from 1 to 100; y has the value from 0 to 100; z has the value 0 or 1 ; and the balance carrier and adjunct ingredients. A composition according to Claim 1 wherein the adjunct ingredients are selected from the group consisting of builders, optical brighteners, bleaches, bleach boosters, bleach activators, soil release polymers, dye transfer agents, dispersents, enzymes, suds suppressers, dyes, perfumes, colorants, filler salts, hydrotropes. and mixtures thereof. 3. A composition according to any of Claims 1 or 2 wherein Rl is at least 50% ethylene, preferably 100% ethylene. 4. A composition according to any of Claims 1-3 wherein said non-cotton soil release polymer comprises: a) a backbone comprising: i) at least one moiety having the formula: ii) at least one moiety having the formula: wherein R^ is C2-Cg linear alkylene, C3-C6 branched alkylene, C5-C7 cyclic alkylene, and mixtures thereof; Rl" is independently selected from hydrogen or -L-Sθ3 * M + ; wherein L is a side chain moiety selected from the group consisting of alkylene, oxyalkylene, alkyleneoxyalkylene, arylene, oxyarylene, alkyleneoxyarylene, poly(oxyalkylene), oxy-alkyleneoxyarylene, poly(oxyalkylene)oxyarlyene, alkylene-poly(oxyalkylene), and mixtures thereof; M is hydrogen or a salt forming cation; i has the value of 0 or 1 ; iii) at least one trifunctional, ester-forming, branching moiety; iv) at least one 1,2-oxyalkyleneoxy moiety; and b) one or more capping units comprising: i) ethoxylated or propoxylated hydroxyethanesulfonate or ethoxylated or propoxylated hydroxypropanesulfonate units ofthe formula (Mθ3S)(CH2) m (Rl !θ) n -, where M is a salt forming cation, Rl 1 is ethylene, propylene, and mixtures thereof, m is 0 or 1, and n is from 1 to 20; ii) sulfoaroyl units ofthe formula -(0)C(C6H4)(Sθ3"M + ), wherein M is a salt forming cation; iii) modified poly(oxyethylene)oxy monoalkyl ether units ofthe formula Rl 2 0(CH 2 CH 2 0)k-, wherein Rl 2 contains from 1 to 4 carbon atoms and k is from 3 to 100; and iv) ethoxylated or propoxylated phenolsulfonate end-capping units ofthe formula Mθ3S(C6H4)(ORl 3 ) n O-, wherein n is from 1 to 20; M is a salt-forming cation; and Rl 3 is ethylene, propylene, and mixtures thereof. 5. A composition according to any of Claims 1-3 wherein the non-cotton soil release agent comprises a sulfonated oligomeric ester composition comprising the sulfonated product of a pre-formed, substantially linear ester oligomer, said linear ester oligomer comprising, per mole, a) 2 moles of terminal units wherein from 1 mole to 2 moles of said terminal units are derived from an olefinically unsaturated component selected from the group consisting of allyl alcohol and medially] alcohol, and any remaining of said terminal units are other units of said linear ester oligomer; b) from 1 mole to 4 moles of nonionic hydrophile units, said hydrophile units being derived from alkyleneoxides, said alkylene oxides comprising from 50% to 100% ethylene oxide; c) from 1.1 moles to 20 moles of repeat units derived from an aryldicarbonyl component wherein said aryldicarbonyl component is comprised of from 50% to 100% dimethylterephthalate, whereby the repeat units derived from said dimethylterephthalate are terephthaloyl; and d) from 0.1 moles to 19 moles of repeat units derived from a diol component selected from the group consisting of C2-C4 glycols; wherein the extent of sulfonation of said sulfonated oligomeric ester composition is such that said terminal units are chemically modified by e) from 1 mole to 4 moles of terminal unit substituent groups of formula -SO x M wherein x is 2 or 3, said terminal unit substituent groups being derived from a bisulfite component selected from the group consisting of HSO3M wherein M is a conventional water-soluble cation. 6. A composition according to any of Claims 1-3 wherein the non-cotton soil release agents comprise compounds ofthe formula X[(OCH 2 CH 2 ) n (OR 5 ) πl ][(A-Rl-A-R 2 )u(A-R 3 -A-R 2 )v]— A- R4- A[(R5θ) m (CH 2 CH 2 θ) n ]X wherein each ofthe A moieties is selected from the group consisting of o | | 0 | | — OC— , —CO and combinations thereof, each of the Rl moieties is selected from the group consisting of 1 ,4-phenylene and combinations thereof with 1,3-phenylene, 1,2 phenylene, 1,8-naphthylene, 1 ,4-naphthylene, 2,2'-biphenylene, 4,4'- biphenylene, C i -Cg alkylene, C \ -Cg alkenylene and mixtures thereof the R 2 moieties are each selected from the group consisting of ethylene moieties, substituted ethylene moieties having C1-C4 alkyl, alkoxy substitiuents, and mixtures thereof; the R 3 moieties are substituted C2-Cιg hydrocarbylene moieties having at least one -CO2M, -0[(R 5 O) m (CH2CH2θ) n ]X or -A[(R 2 - A-R 4 -A)] w [(R 5 0) m (CH2CH2θ) n ]X substituent; the R 4 moieties are Rl or R 3 moieties, or mixtures thereof; each R^ is C1-C4 alkylene, or the moiety -R 2 -A-R6- wherein R*> is a C1-C12 alkylene, alkenylene, arylene, or alkarylene moiety; each M is hydrogen or a water-soluble cation; each X is C 1 -C4 alkyl; the indices m and n have the values such that the moiety -(CH2CH2O)- comprises at least 50% by weight ofthe moiety [(R 5 0) m (CH2CH2θ) n ], provided that when R 5 is the moiety -R 2 -A-R 6 -, m is 1 ; each n is at least 10; the indices u and v have the value such that the sum of u + v is from 3 to 25; the index w is 0 or at least 1 ; and when w is at least 1 u, v and w have the value such that the sum of u + v + w is from 3 to 25. 7. A composition according to any of Claims 1-3 wherein the non-cotton soil release agent comprises: A) at least 10% by weight of a substantially linear sulfonated poly- ethoxy/propoxy end-capped ester having molecular weight ranging from 500 to 8,000; said ester consisting essentially of on a molar basis: i) from 1 to 2 moles of sulfonated poly ethoxy/propoxy end- capping units ofthe formula: (MS03)(CH 2 ) m (CH2CH 2 0)(RO) n - wherein M is a salt-forming cation such as sodium of tertraalkylammonium, m is 0 or 1, R is ethylene, propylene, and mixtures thereof; and n is fro 0 to 2; and mixtures thereof; ii) from 0.5 to 66 moles of units selected from the group consisting of: a) oxyethyleneoxy units; b) a mixture of oxyethyleneoxy and oxy- 1 ,2,- propyleneoxy units wherein said oxyethyleneoxy units are present in an oxyethyleneoxy of oxy- 1,2- propyleneoxy mole ratio ranging from 0.5 : 1 to 10: 1 ; and c) a mixture of a) or b) with poly(oxyethylene)oxy units have a degree of polymerization of from 2 to 4; provided that when said poly(oxyethylene)oxy units have a degree of polymerization of 2, the mole ratio of poly(oxyethylene)oxy units to total group ii) units ranges fro 0: 1 to 0.33: 1 ; and when said poly(oxyethylene)oxy units have a degree of polymerization of 3; the mole ration of poly(oxyethylene)oxy units to total group ii) units ranges from 0: 1 to 0.22: 1 ; and when said poly(oxyethylene)oxy units have a degree of polymerization equal to 4, the mole ratio of poly(oxyethylene)oxy units to total group ii) units ranges from 0: 1 to 0.14: 1 ; iii) from 1.5 to 40 moles of terephthaloyl units; and iv) from 0 to 26 moles of 5-sulphophthaloyl units ofthe formula: -(O)C(C 6 H 3 )(S0 3 M)C(O)- wherein M is a salt forming cation; and B) from 0.5% to 20% by weight of ester, of one or more crystallization- reducing stabilizers. 8. A composition according to any of Claims 1 -3 wherein the non-cotton soil release agent comprises greater than 0.2% carboxy methyl cellulose. 9. A method for providing soil release from cotton fabric, said method comprising contacting cotton fabric in need of cleaning with an effective amount of a cotton soil release agent comprising a water-soluble or dispersible, modified polyamine cotton soil release agent comprising a polyamine backbone conesponding to the formula: ? I [H 2 N-R]nH -[N-R] m -[N-R] n -NH 2 having a modified polyamine formula V( n+ j)W m Y n Z or a polyamine backbone conesponding to the formula: H | R [H2N-R] n -k+r— [N-R] m -[N-R] n — [N-R]k-NH 2 having a modified polyamine formula wherein k is less than or equal to n, said polyamine backbone prior to modification has a molecular weight greater than 200 daltons, wherein i) V units are terminal units having the formula: E Y - 9 E— N-R — 0 r E— N u- x R — nr E-N t-R — I or I or I E E E ii) W units are backbone units having the formula: iii) Y units are branching units having the formula: iv) Z units are terminal units having the formula: O X t —N-E or —N-E or —N-E I I ° r I E E E wherein backbone linking R units are selected from the group consisting of C2-C12 alkylene, C4-C12 alkenylene, C3-C12 hydroxyalkylene, C4-C12 dihydroxy-alkylene, Cg-Ci2 dialkylarylene, -(R10) X R1 -, - (RlO) x R5(ORl) x -, - (CH2CH(OR 2 )CH20) z (RlO) y Rl(OCH 2 CH(OR 2 )CH 2 ) w -, -C(0)(R4) r - C(O)-, -CH2CH(OR 2 )CH2-, and mixtures thereof, preferably C2-C12 alkylene, C3-C12 hydroxyalkylene, C4-C12 dihydroxyalkylene, Cg-Ci2 dialkylarylene, -(R10) X R1-, -(Rlθ) x R 5 (ORl) x -, -(CH 2 CH(OH)CH 2 0) z - (Rlθ) y Rl-(OCH2CH(OH)CH 2 )w-» -CH 2 CH(0R 2 )CH 2 -, and mixtures thereof, more preferably C2-C12 alkylene, C3-C12 hydroxyalkylene, C4- C12 dihydroxyalkylene, -(Rlθ) x Rl-, -(Rlθ) x R 5 -(ORl) x -, -(CH 2 CH(OH)- CH2θ) z (R 1 0) y Rl(OCH2CH(OH)CH2) w -, and mixtures thereof, most preferably C2-C12 alkylene, and mixtures thereof; wherein Rl is C2-Cg alkylene, preferably ethylene, and mixtures thereof; R 2 is hydrogen, -(R10) X B, and mixtures thereof, preferably hydrogen; R 3 is Ci-Cjg alkyl, C7-C12 arylalkyl, C7-C12 alkyl substituted aryl, C6-C12 aryl, and mixtures thereof, Cj-Cό alkyl and mixtures thereof, more preferably methyl; R4 is C1-C12 alkylene, C4-C12 alkenylene, Cg-Ci2 arylalkylene, C6-C10 arylene, and mixtures thereof, preferably C2-C 12 alkylene, Cg-C 12 arylalkylene, and mixtures thereof, more preferably, ethylene, butylene, and mixtures thereof; R^ is C1-C12 alkylene, C3-C12 hydroxyalkylene, C4-C12 dihydroxy-alkylene, Cg-C 12 dialkylarylene, -C(O)-, -C(0)NHR 6 NHC(0)-, - Rl(ORl)-, -C(0)(R 4 ) r C(0)-, -CH 2 CH(OH)CH 2 -, - CH 2 CH(OH)CH2θ(Rl 0) y -Rl OCH 2 CH(OH)CH2-, and mixtures thereof, preferably ethylene, -C(O)-, -C(0)NHR 6 NHC(0)-, -Rl (ORl ) y -, - (CH2CH(OH)CH2θ) z (Rlθ) y R 1 -(OCH 2 CH(OH)CH2) w -, - CH2CH(OH)CH2-, and mixtures thereof, more preferably - CH2CH(OH)CH2-; R 6 is C2-C12 alkylene or Cg-C 12 arylene; E units are selected from the group consisting of hydrogen, C 1 -C22 alkyl, C3-C22 alkenyl, C7-C22 arylalkyl, C2-C22 hydroxyalkyl, -(CH 2 ) p Cθ2M, - (CH 2 ) q S0 3 M, -CH(CH 2 C0 2 M)CO 2 M, -(CH 2 ) p P0 3 M, -(R!0) x B, - C(0)R 3 , and mixtures thereof; preferably hydrogen, C3-C22 hydroxyalkyl, benzyl, C!-C 2 2 alkyl, -(Rlθ) x B, -C(0)R 3 , -(CH 2 ) p C0 2 -M + , -(CH2) q S0 3 - M + , -CH(CH2Cθ2M)Cθ2M and mixtures thereof, more preferably hydrogen, Q-C22 alkyl, -(Rlθ) x B, -C(0)R 3 , and mixtures thereof, most preferably -(Rlθ) x B; B is hydrogen, Cj-Cό alkyl, -(CH2) q S03M, -(CH 2 ) p - CO2M, -(CH2) q (CHSθ3M)CH2S0 3 M, -(CH 2 )q-(CHS0 2 M)-CH2Sθ3M, - (CH2) p P03M, -PO3M, and mixtures thereof, preferably hydrogen, Cj-Cg alkyl, -(CH 2 ) q S0 3 M, -(CH2) q (CHSθ3M)CH 2 Sθ3M, -(CH 2 ) q (CHS0 2 M)- CH2SO3M, and mixtures thereof, more preferably hydrogen, - (CH2)qS03M, and mixtures thereof, most preferably hydrogen; M is hydrogen or a water soluble cation in sufficient amount to satisfy charge balance; X is a water soluble anion; m has the value from 4 to 400; n has the value from 0 to 200; p has the value from 1 to 6, q has the value from 0 to 6; r has the value of 0 or 1 ; w has the value 0 or 1 ; x has the value from 1 to 100; y has the value from 0 to 100; z has the value 0 or 1. 10. A laundry bleaching composition comprising: a) at least 0.001 % by weight, a water-soluble or dispersible, bleach stable, modified polyamine cotton soil release agent comprising a polyamine backbone conesponding to the formula: ¥ i [H 2 N-R]nf i -[N-R] m -[N-R] n -NH 2 having a modified polyamine formula or a polyamine backbone conesponding to the formula: I H | R [H 2 N-R] n -k+ 1— [N-R]m-[N -R] n -[N-R]k-NH 2 having a modified polyamine formula V^.k+i^WmYnY'kZ, wherein k is less than or equal to n, said polyamine backbone prior to modification has a molecular weight greater than 200 daltons, wherein i) V units are terminal units having the formula: O ? X ' E— N- R- o orr E- NN-- R R — E— N t or -R- I E ii) W units are backbone units having the formula: iii) Y units are branching units having the formula: iv) Z units are terminal units having the formula: O ? X t —N-E or — N— E or — N— E I or I 0r I E E E wherein backbone linking R units are selected from the group consisting of C2-C12 alkylene, C4-C12 alkenylene, C3-C12 hydroxyalkylene, C4-C12 dihydroxy-alkylene, Cg-C 12 dialkylarylene, -(Rlθ) x Rl-, -(RlO) x R 5 (OR!) x -, - (CH 2 CH(OR 2 )CH 2 0) z (R 10) y -R 1 (OCH 2 CH(OR 2 )CH 2 )w-, - C(0)(R 4 ) r C(0)-, -CH2CH(OR 2 )CH2, and mixtures thereof; wherein Rl is C2-Cg alkylene and mixtures thereof; R 2 is hydrogen, - (Rlθ) x B, and mixtures thereof; R 3 is Cι-Cιg alkyl, C7-C12 arylalkyl, C7-C12 alkyl substituted aryl, Cg-C 12 aryl, and mixtures thereof; R4 is C1-C12 alkylene, C4-C12 alkenylene, Cg-C 12 arylalkylene, Cg-C 10 arylene, and mixtures thereof; R^ is Cj-C 12 alkylene, C3-C12 hydroxyalkylene, C4-C12 dihydroxy-alkylene, Cg- C12 dialkylarylene, -C(O)-, -C(0)NHR6-NHC(0)-, -Rl(ORl)-, - C(0)(R 4 ) r C(0)-, -CH 2 CH(OH)CH 2 -, CH 2 CH(OH)CH2θ(Rlθ) y RlθCH 2 CH(OH)CH2-, and mixtures thereof; R*> is C2-C12 alkylene or Cg-C 12 arylene; E units are selected from the group consisting of hydrogen, C1-C22 alkyl, C3- C22 alkenyl, C7-C22 arylalkyl, C2-C22 hydroxyalkyl, -(CH2) p - C0 2 M, -(CH 2 ) q S0 3 M, -CH(CH2C0 2 M)C0 2 M, -(CH 2 ) p P0 3 M, -(R10) X B, -C(0)R 3 , and mixtures thereof; oxide; B is hydrogen, Ci- Cg alkyl, -(CH 2 ) q S0 3 M, -(CH 2 ) p C0 2 M, -(CH 2 ) q (CHS0 3 M)- CH2SO3M, -(CH2) q -(CHSθ2M)CH 2 S0 3 M, -(CH 2 )pPθ3M, - PO3M, and mixtures thereof; M is hydrogen or a water soluble cation in sufficient amount to satisfy charge balance; X is a water soluble anion; m has the value from 4 to 400; n has the value from 0 to 200; p has the value from 1 to 6, q has the value from 0 to 6; r has the value of 0 or 1 ; w has the value 0 or 1 ; x has the value from 1 to 100; y has the value from 0 to 100; z has the value 0 or 1 ; an oxygen bleaching agent selected from the group consisting of alkali metal percarbonate, perborate, monoperphthalate, pyrophosphate peroxyhydrate, urea peroxy-hydrate and mixtures thereof; c) a bleach activator; preferably the oxygen bleach activator has the formula and mixtures thereof, wherein Rl is C1-C14 alkyl, aryl, alkylaryl, and mixtures thereof; R 2 is C1-C14 alkylene, arylene, alkylarylene, and mixtures thereof; R 5 is hydrogen, C1-C10 alkyl, aryl, alkylaryl, and mixtures thereof; L is any suitable leaving group; and d) the balance carriers and adjunct materials said adjunct ingredients are selected from the group consisting of builders, optical brighteners, bleach boosters, dye transfer agents, dispersents, enzymes, suds suppressers, dyes, perfumes, colorants, filler salts, hydrotropes, and mixtures thereof.

Inventors: GOSSELINK EUGENE PAUL, GRAYDON ANDREW RUSSELL, MANOHAR SANJEEV KRISHNADAS, PANANDIKER RAJAN KESHAV, WATSON RANDALL ALAN, GOSSELINK, EUGENE, PAUL, GRAYDON, ANDREW, RUSSELL, MANOHAR, SANJEEV, KRISHNADAS, PANANDIKER, RAJAN, KESHAV, WATSON, RANDALL, ALAN
Applicants: PROCTER & GAMBLE, THE PROCTER & GAMBLE COMPANY
Application year: 1997
Main classification: C11D3
IPC codes: C08G73, C11D1, C11D3, D06L1, D06M13, D06M15, D06M101