Polyalkylene naphtalate film comprising specific UV-absorber

Abstract: Disclosed is a polyalkylene naphthalate film, preferably the homopolymer of naphthalene-2,6-dicarboxylic acid and ethylene glycol (PEN), comprising a UV absorbing compound of the 2-hydroxyphenyl-triazine type for quenching of the UV fluorescence at 429 nm. The polymeric film is preferably used as support for a photographic material, preferably a colour negative or colour reversal photographic material.

Description: 1. Field of the invention. The present invention relates to a polymeric film and to a photographic material using this polymeric film as a support. 2. Background of the invention. In recent years polyalkylene naphthalate has been used for various applications thanks to its excellent physical properties. For instance, polyethylene naphthalate is used as a film having high strength and high elasticity modulus in various types of audio tapes and video tapes. Polybutylene naphthalate is also used for various resin applications. However, it is known that polyalkylene naphthalate has the drawback of emitting pale fluorescence with a peak at 429 nm when it is exposed to ultraviolet light, leading to a problem with its outer appearance for application in food packages and beverage bottles. Studies on the mechanism of the fluorescence of a poly(1,2-ethylene-2,6-naphthalene dicarboxylate) film have been reported in the Journal of Polymer Science: Polymer Letters Edition, vol.17, pp. 227-232 (1979), which discloses that the fluorescence is emitted from an excimer of naphthalate. It has been reported in the US 5,310,857 that fluorescence of such polyalkylene naphthalate can be suppressed efficiently by copolymerizing a relatively small amount of an aromatic ketone. However, this is a cumbersome and expensive procedure. JP-A-59-12 952 (the term "JP-A" as used herein means an "unexamined Japanese patent publication") discloses a method for protecting various types of resins from ultraviolet light by mixing a compound having a cyclic imino ester in its molecule with the resins. Use of a phenylquinoxaline as a stabilizer for polymers having a halogen atom in the molecule is disclosed in the specification of US 3,325,446. However this reference is totally silent about the prevention of fluorescence from the polymer. The specifications of US 5,391,330 and US 5,391,702 disclose a process comprising melt-blending a naphthalenedicarboxylic acid containing polymer with 0.1 to 5 % by weight of a fluorescence quenching compound chosen from a halogen containing aromatic compound, an aromatic ketone, and a naphtol compound. Protective layers containing a UV-absorber and coated on top of resin molded articles are disclosed e.g. in JP-B-60-53701 (the term "JP-B-" meaning "examined Japanese patent publication"), JP-A-2-150431. JP-A-2-38128, JP-B- 5-86973 and JP-B-37212. In EP 0 711 803 a method is disclosed for quenching the fluorescence from polyalkylene-2,6-dicarboxylate by addition of a cyclic imino ester or of a quinoxaline compound. In very recent time polyethylene-2,6-dicarboxylate (PEN) has found a new application as support for photographic materials, more particularly colour negative and colour reversal materials that are slit, cut and packaged according to the so-called Advanced Photo System (APS), which uses cartridges with a smaller total diameter then the traditional 35-mm cartridges. The choice of PEN as support is dictated by the fact that it is less susceptible than the more tradionally used polyethylene terephthalate (PET) to so-called core set curl, or "memory curl", when it is kept in winded state for a long time and/or is exposed to high temperatures (e.g. as can occur in a car during summer). Such curl adversely affects further photofinishing steps such as processing and printing. In US 4,147,735 a method is disclosed for eliminating effectively the problem of core set curl in the case of PEN by means of a heat treatment. However the occurence of UV absorption and subsequent fluorescence emission tends to lead to a yellow discoloration of PEN when exposed to light during long storage periods, e.g. before coating with emulsions, or during storage after processing. Such a yellow hue will affect the printing properties in a irreproducible way. In EP 0 631 177 a photographic material is disclosed using a polyethylene naphthalate support comprising an UV-absorber chosen from six particular chemical classes including hemioxonol and merostyryl compounds. The problem with UV-fluorescence quenching compounds used in the prior art is the fact that they are insufficiently thermostable. However this property is from uttermost importance since the quencher has to be incorporated in the polyester in the molten state at high temperature. When the UV-absorber is substantially decomposed it will lose its effectiveness as quencher and moreover it will give rise to yellow coloured decomposition products. It is an object of the present invention to provide a polyester film made of polyalkylene naphthalate containing effective compounds for suppressing the emission of UV-fluorescence. It is a further object of the present invention to provide a polyester film made of polyalkylene naphthalate, suitable for a photographic material, which is hardly discoloured during storage. It is still a further object of the present invention to provide a photographic material which is hardly susceptible to core set curl when kept in winded state for a long period. It is still a further object of the present invention to provide a photographic material the photographic properties of which are hardly changed over time. 3. Summary of the invention. The objects of the present invention are realized by providing a polyester film made of polyalkylene naphthalate or a derivative thereof and containing an UV-absorber according to following general formula (I) : wherein R 1 and R 3 each independently represent hydrogen, halogen, -OR 6 , mercapto, alkyl, aryl, alkoxy, aryloxy, acyl, alkylthio, -NR 5 -R 6 . alkoxycarbonyl, carbamoyl, sulfamoyl, aryloxycarbonyl, each of which can be further substituted, R 2 represents hydrogen, hydroxy, halogen or alkyl, each of which can be further substituted, R 4 represents alkyl, alkoxy, alkylthio, aryloxy, arylthio, each of which can be further substituted, or a moiety represented by R 5 represents hydrogen, alkyl or aryl, each of which can be further substituted, R 6 represents hydrogen, alkyl, aryl, acyl, alkoxycarbonyl, aryloxycarbonyl, carbamoyl, sulfamoyl or sulfonyl, each of which can be further sustituted, R 7 and R 8 have one of the significances given for R 2 and R 3 respectively, and wherein m, n and o each independently represent 1,2,3 or 4. In a preferred embodiment the polyalkylene naphthalate support is the homopolymer of 2.6-naphtalenedicarboxylic acid and ethylene glycol (100/100) (PEN). Further belonging to the scope of the present invention is a photographic material comprising a support made of polyalkylene naphthalate or a derivative thereof and containing a compound as defined above. 4. Detailed description. First of all the notion "polyalkylene naphthalate or a derivative thereof" will now be explained in detail. This is a polyester made up of naphthalenedicarboxylic acid as a major acid component and a compound having two alcoholic hydroxyl groups as a major glycol component. The acid component of the polyester is mainly naphthalenedicarboxylic acid, but a part (generally less than 50 mol%, preferably less than 30 mol%) of the naphthalenedicarboxylic acid may be replaced by one or more other difunctional carboxylic acids, for example, aromatic dicarboxylic acids, such as terephthalic acid, isophthalic acid. diphenyldicarboxylic acid, diphenyl ether dicarboxylic acid, diphenylsulfonedicarboxylic acid, and diphenoxyethanedicarboxylic acid; aliphatic dicarboxylic acids, such as adipic acid and sebacic acid; and oxy acids, such as oxybenzoic acid and ε-oxycaproic acid. As the naphthalenedicarboxylic acid 2,6-naphthalenedicarboxylic acid, 2,7-naphthalenedicarboxylic acid, and 1,5-naphthalenedicarboxylic acid are preferably used, the first one being the most preferred. As the glycol component a compound is used having two alcoholic hydroxyl groups, for example, an aliphatic glycol, such as ethylene glycol, propylene glycol, trimethylene glycol, butanediol, neopentylene glycol, hexanediol, decanediol, and diethylene glycol; a cycloaliphatic glycol, such as cyclohexanedimethylol and tricyclodecanediol, and an aromatic diol, such as 2,2-bis(4-β-hydroxyphenyl)-propane, 1,1-bis(4-β-hydroxyethoxyphenyl)cyclohexane, and 4,4'-bis(β-hydroxyethoxy)diphenylsulfone, which may be used alone or as a mixture of one or more. A small amount of a compound having two phenolic hydroxyl groups, such as bisphenol A and bisphenol Z, can be additionally used. The preferred glycol component is simply ethylene glycol, present for at least 50 % of the alcohol compounds, more preferably at least 70 % and most preferably 100 %. Such a polyester can be produced in accordance with the conventionally known polyester production method usually including a transesterification step and a polycondensation step. Further, the polyethylene naphthalate or its derivative for use in the present invention may be blended with another polyester. Polymer blends can be formed easily in accordance with methods described in JP-A Nos. 5482/1974, 4325,1989, and 192718/1991, Research Disclosure Nos. 283,739-41, 284,779-82, 294,807-14, and 294,807-14. The glass transition point of the polyester for use in the present invention is preferably 90 °C or over but 200 °C or below. Preferable specific examples of the polyesters for use in the present invention are shown below, but the present invention is not restricted to them. Polyester compound examples: Homopolymer: POL-1 : [2,6-naphthalenedicarboxylic acid (NDCA)/ethylene glycol (EG) (100/100)] (Tg = 119 °C) (PEN). Copolymers (the entry in the parentheses represents the molar ratio): POL-2 : 2,6-NDCA/TPA(terephthalic acid)/EG (50/50/100) (Tg = 92 °C) POL-3 : 2,6-NDCA/TPA/EG (75/25/100) (Tg = 102 °C) POL-4 : 2,6-NDCA/TPA/EG/BPA (bisphenol A = bisphenyl-4,4'-dicarboxylic acid) (50/50/75/25) (Tg = 112 °C) POL-5 : NDCA/sulfoterephthalic acid/EG (98/2/100) (Tg = 117 °C) Polymer blends (the entry in the parentheses represents the molar ratio): POL-6 : POL-1/PET (80/20) (Tg = 104 °C) POL-7 : PAr/POL-1 (50/50) (Tg = 142 °C) (PAr:TPA/BPA = 100/100 (Tg = 192 °C) (PET: TPA/EG = 100/100 (Tg = 80 °C) POL-8 : PEN/PET/PAr (50/25/25) (Tg = 108 °C) These films may have a polar group (e.g., epoxy, COO 2 M, OH, NR 2 , NR 3 X, SO 3 M, OSO 3 M, PO 3 M 2 , and OP 3 M 2 , wherein M represents H, an alkali metal, or ammonia, and R represents H or an alkyl group having 1 to 20 carbon atoms). However, by far the most preferred polyalkylene naphthalate for use as support for a photographic material according to the present invention is simply the homopolymer of 2,6-naphthalenedicarboxylic acid and ethylene glycol (PEN) and most of the further description and examples will deal with this polyester. The thickness of such a support for use in the present invention is 40 to 500 µm, preferably 60 to 200 µm. Preferred subclasses and examples of useful UV absorbing compounds according to formula (I) include : V-1 V-2 V-3 R A = R B = -C 4 H 9 - s. R C = -C 13 H 23 -i V-4 V-5 R C = -C 12 H 25 V-6 R C = R A , R B (1:1) V-7 R A = -CH 2 -CH 2 -CO-CH 2 -CH 2 -O-C 4 H 9 , R B = R C = -CH 2 -CO 2 -C 8 H 17 -i, V-8 V-9 V-10 R A = -CH 2 -CO 2 -C 4 H 9 -i, R B = -CH 2 -CO 2 -C 13 H 20 -i, V-11 R A = R B = -(CH 2 -CH 2 -O) 4 -CH 3 , V-12 R A = R B = -C 10 H 21 -i V-13 V-14 R A = R B = -C 8 H 17 V-15 V-16 V-17 V-18 V-19 V-20 V-21 V-22 V-23 V-24 V-25 V-26 V-27 V-28 V-29 V-30 V-31 The most preferred UV-absorbers for the practice of this invention are V-20 (=CYASORB UV1164, registered trademark of Cytec Co.), V-19 (=TINUVIN 1577, registered trademark of Ciba-Geigy AG). References on the synthesis of the 2-hydroyphenyl-triazine compounds used in the present invention include the patents FR 1379138 and FR 1405559. The UV-absorbers can be incorporated in the polyalkylene naphthalate film by various techniques. They can be blended in crystalline or liquid form with the PEN granulate, dried at 160 °C, molten together at about 280-300 °C and extruded to form a film. On the other hand a master batch of PEN + UV-absorber is first prepared which is added to blank PEN by means of a dosing apparatus during extrusion. Alternatively, the UV-absorber can be added during synthesis of the PEN after the transesterification step but before the polycondensation step. It will be clear that in the latter process the requirements posed to the UV-absorber concerning thermal stability are even more stringent, and as will become clear from the examples furtheron, the 2-hydroxyphenyl-triazine compounds used in the present invention behave excellently in this respect. Finally, the UV-absorber molecule can even be incorporated chemically in the polyester polymeric chain by a method as disclosed in e.g. WO 95/04769 and US 5,310,857. The UV-absorbers used in accordance with the present invention are preferably incorporated in an amount between 0.1 % and 1.0 % versus polyalkylene naphthalate. In order to be effective they must absorb between 200 and 400 nm. Most preferably, the wavelenght of maximal absorption is between 300 nm and 400 nm. The UV-aborbers can be used alone or as mixtures of more then one compound. They can also be mixed with UV-absorbers outside the scope of the present invention. In the embodiment wherein the PEN is used as support for a photographic element it is advisable to add a mixture of dyes resulting in a so-called "grey base" for the prevention of so-called "light piping". This phenomenon is caused by the fact that the refractive index of gelatin being the major constituent of photographic layers is 1.50-1.55 while the refractive index of polyesters such as PEN is as high as 1.6-1.7. As a result unwanted light entering from a film edge tends to be reflected at the interface between the base and the hydrophilic layers resulting in edge fogging. The polyalkylene film of the present invention can contain various agents improving slidability such as SiO 2 , TiO 2 , BaSO 4 , CaCO 3 , talc, kaolin, clay, alumina silicates and silicone particles. It can also contain spacing agents such as polymethylmethacrylate beads, polystyrene beads, and TOSPEARL siloxane beads (registered trade mark of Toshiba Co). When the polyalkylene naphtalate film containing a UV-absorber according to the present invention is used as a support for a photographic material it is preferably provided with a so-called subbing layer. An example of a suitable subbing layer is a layer containing a polymer containing covalently bound chlorine. Suitable chlorine containing polymers are e.g. polyvinyl chloride, polyvinylidene chloride, a copolymer of vinylidene chloride, an acrylic ester and itaconic acid, a copolymer of vinyl chloride and vinylidene chloride, a copolymer of vinyl chloride, vinylidene chloride and itaconic acid, a copolymer of vinyl chloride, vinyl acetate and vinyl alcohol, A preferred chlorine containing polymer is co(vinylidenechloride-methylacrylate-itaconic acid : 88 % / 10 % / 2 %). A most suitable subbing layer contains the latter polymer and a colloidal silica such as KIESELSOL 100F (Bayer AG). Optionally to this composition can be added co(methylacrylate-butadiene-itaconic acid) (49/49/2), preferably in a ratio of about 10 %. The most favourable adhesion properties are obtained when a subbing layer as described above provided with an additional primer layer containing gelatin (preferably 0.25 - 0.35 g/m 2 ), Kieselsol 300 F (0.30 - 0.40 g/m 2 ) and a matting agent on the base of polymethylmethacrylate (average size 2 à 3 µm) at a coverage of about 0.001 g/m 2 . In a most preferred embodiment of the present invention the polyalkylene naphthalate film serves as support for a photographic silver halide material. This material can be suited for general amateur- or professional photography, for graphic arts application, for recording or display of radiogragraphic information, for cinematographic recording and display, for micrography, and for duplicating purposes. In a preferred embodiment however of the present invention the photographic material is a colour negative or colour reversal material for general photography. In a most preferred embodiment this colour photographic material is slit, cut and packaged according to the specifications of the so-called Advanced Photographic System (APS). As explained above, PEN is particularly suited as support for an APS photographic material since problems with memory curl are more easily avoided with PEN than with PET. Colour negative and colour reversal materials usually comprise two or three red sensitive emulsion layers containing a cyan coupling colour coupler, two or three green sensitive emulsion layers containing a magenta coupling colour coupler, and two or three blue sensitive layers containing a yellow coupling colour coupler. The layers showing the same spectral sensitivity are differentiated in their photographic speed. Usually a yellow filter layer is present between the blue and green sensitive layers in order to avoid penetration of blue light into the underlying layers. The most important ingredients of the emulsion layer are the binder, the silver halide emulsion grains, and the various colour couplers. The binder is a hydrophilic colloid, preferably gelatin. Gelatin can, however, be replaced in part or integrallly by synthetic, semi-synthetic, or natural polymers. The gelatin can be lime-treated or acid-treated gelatin. The preparation of such gelatin types has been described in e.g. "The Science and Technology of Gelatin", edited by A.G. Ward and A. Courts, Academic Press 1977, page 295 and next pages. The halide composition of the silver halide emulsions used according to the present invention is not specifically limited and may be any composition selected from i.a. silver chloride, silver bromide, silver iodide, silver chlorobromide, silver bromoiodide, and silver chlorobromoiodide. However, for colour negative and colour reversal materials that must show recording speed rather sensitive silver iodobromide emulsions are preferred. The photographic emulsions can be prepared from soluble silver salts and soluble halides according to different methods as described e.g. by P. Glafkides in "Chimie et Physique Photographique", Paul Montel, Paris (1967), by G.F. Duffin in "Photographic Emulsion Chemistry", The Focal Press, London (1966), and by V.L. Zelikman et al in "Making and Coating Photographic Emulsion", The Focal Press, London (1966). The silver halide can be precipitated according to the single-jet method, the double-jet method, or the conversion method. The silver halide particles of the photographic emulsions used according to the present invention may have a regular crystalline form such as a cubic or octahedral form or they may have a transition form. They may also have an irregular crystalline form such as a spherical form or a tabular form, or may otherwise have a composite crystal form comprising a mixture of said regular and irregular crystalline forms. They may have a multilayered grain structure suich as core/shell. The size distribution of the silver halide particles of the photographic emulsions to be used according to the present invention can be homodisperse or heterodisperse. The emulsion can be desalted in the usual ways e.g. by dialysis, by flocculation and re-dispersing, or by ultrafiltration. The light-sensitive silver halide emulsion can be a so-called primitive emulsion, in other words an emulsion that has not been chemically sensitized. However, the light-sensitive silver halide emulsion can be chemically sensitized as described i.a. in the above-mentioned "Chimie et Physique Photographique" by P. Glafkides, in the above-mentioned "Photographic Emulsion Chemistry" by G.F. Duffin, in the above-mentioned "Making and Coating Photographic Emulsion" by V.L. Zelikman et al. and in "Die Grundlagen der Photographischen Prozesse mit Silberhalogeniden" edited by H. Frieser and published by Akademische Verlagsgesellschaft (1968). The light-sensitive silver halide emulsions can be spectrally sensitized with methine dyes such as those described by F.M. Hamer in "The Cyanine Dyes and Related Compounds", 1964, John Wiley & Sons. Dyes that can be used for the purpose of spectral sensitization include cyanine dyes, merocyanine dyes, complex cyanine dyes, complex merocyanine dyes, hemicyanine dyes, styryl dyes and hemioxonol dyes. Particularly valuable dyes are those belonging to the cyanine dyes, merocyanine dyes and complex merocyanine dyes. Also so-called supersensitizers can be used. Details on colour couplers can be found in Research Disclosure 37254, Section 4 (1995) p. 288, and in item 37038, Section II (1995). Compounds that on reaction with oxidized developer liberate a so-called photographically useful substance are often incorporated in colour photographic materials in order to improve granularity, sharpness and colour separation. Examples of such compounds include DIR couplers which set free development inhibitors, DAR couplers, BIR and BAR couplers. More details on such special couplers can be found in Research Disclosure 37254, Section 5 (1995), p. 290 and Research Disclosure 37038, Section XIV (1995), p. 86. The hydrophobic colour couplers and other hydrophobic ingredients are commonly dissolved or dispersed in high-boiling organic solvents, so-called oilformers. These solutions or dispersions are then dispersed in the hydrophilic gelatinous coating solution and are present after coating in the dried emulsion layer as droplets of size between 0.05 and 0.8 µm. More details can be found in Research Disclosure 37254, Section 6 (1995), p. 292. Usually non-light sensitive hydrophilic layers are arranged between the layers packs of different spectral sensitivity. They contain compounds able to prevent the diffusion of oxidized developer products between layers of different sensitivity. Useful compounds are disclosed in Research Disclosure 37254, Section 7 (1995), p. 292, and in Research Disclosure 37038, Section III (1995), p. 84. The layers of the photographic material may further contain UV-absorbers. whitening agents, spacing agents, antioxidants, filter dyes, antihalation dyes, colour correction dyes, dye stabilizers, antifoggants, plasticizers, etc.. A survey of useful compounds can be found in Research Disclosure 37254, Section 8 (1995), p. 292, and in Research Disclosure 37038, Sections IV, V, VI, VII, X, XI, and XII (1995), p. 84. Suitable hardening agents for the gelatinous layers are disclosed in Research Disclosure 37254. Section 9 (1995), p. 294. and in Research Disclosure 37038, Section XII (1995), p. 86. The photographic materials comprising the support in connection with the present invention are exposed and processed according to their particular design and application. Details on processing and its chemicals are described in Research Disclosure 37254, Section 10 (1995), p. 294, and in Research Disclosure 37038, Section XVI to XXIII (1995), p. 95. It is explicitly contemplated that the scope of the present invention extends beyond the use of the described polyalkylene naphthalate film as a support for a photographic material. Alternatively, the polyester film can be used as packaging material for food and beverages, as insulating material, as carrier for audio and video tapes, as receiver base for ink jet printing, as receiver base for electrostatic images (transparex), as membrane touch switches, and as capacitor film. Other applications include e.g. use as support for printing plates, for thermal sublimation systems, for direct thermal systems, for flexible printed circuit boards, etc.. It should also be mentioned that the 2-hydroxyphenyl-triazine UV-absorbers used in accordance with the present invention can be used in other types of polyester and in polyesteramides. The following examples illustrate the present invention without however being limited thereto. EXAMPLES Example 1 Thermal stability and other physical properties of UV-absorbers. A suitable UV-absorber must be sufficiently resistant to thermal decomposition at the extrusion temperature of or blending temperature with PEN (about 300 °C). The thermal stability was determined by means a SEIKO TG/DTA320 instrument. The thermobalance was installed on a horizontal differential system. Samples were heated in open aluminum pans on static air. The speed of heating was 10 °C/min from ambient temperature to 500 °C, or to the end of the weight loss. The sample weights were in the range of 10 to 15 mg, while an empty aluminum pan was used as reference. The method of calculating TGA is based on JIS K7120 (1987) and ISO 7111 (1987). In table 1 the start and end temperatures of the decomposition, and the losses of weight, expressed by percent, are represented. The table is completed with values of wavelenght of maximal absorption and melting points (m.p.). The table also contains comparison UV-absorbers belonging to the scope of EP 0 631 177 or EP 0 711 803, cited above. The formulas of these comparison compounds are given behind table 1. Compound Source range decomp. % weight loss λ max nm m.p. invention UV-absorbers : CYASORB 1164 (= V-20) Cytec 300/34 4.5 340 87-89 TINUVIN 1577 (= V-19) Ciba-Geigy 290/340 8.5 340 149 comparison UV-absorbers (cf. generic formulas in EP 0 631 177) benzotriazoles : TINUVIN 900 Ciba-Geigy 280/350 17 346 143 TINUVIN 326 " 190/310 94.4 352 139 TINUVIN 350 " 190/300 98.6 343 82 TINUVIN 329 " 200/310 99.7 341 103 aromatic ketones : UVINUL 400 BASF 164/300 98.7 315 146 UVINUL 3049 " 208/325 95 340 131 UVINUL D50 " 220/320 17.5 346 196 cinnamic acid esters : UVINUL 3088 BASF 178/320 100 310 (liq.) UVINUL N35 " 170/295 100 310 95 UV-abs. 318 Bayer 161/275 100 324 82 cyclic iminoester (disclosed in EP 0 711803) : CYASORB UV-3638 Cytec 280/340 7 349 310 Conclusion : the invention compounds show a much better thermal stability than the comparison UV-absorbers (with exception for the cyclic iminoester). Formulas of the comparison compounds : Example 2 - % relative fluorescence at 429 nm of PEN + UV-absorber blends. A series of blends of PEN with each of the UV-absorbers of table 1 was synthetized by melting in a glass reactor a mixture of dried PEN granulate (4 hours at 160 °C in vacuo) together with 0.25 to 1.0 % by weight of UV-absorber at 280 °C under nitrogen atmosphere, and by stirring the reaction mixture at this temperature for 20 minutes. The mixture was laid down on aluminum foil, cooled to room temperature and milled to a powder. From each blend sample a film was extruded having a thickness of about 1 mm. By longitudinal and transversal stretching (3 x 3) a final film having a thickness of 100 µm was obtained. The intensity of fluorescence caused by excitation at a wavelenght of 380 nm was measured at the emission wavelenght of 429 nm by means of a Perkin-Elmer spectrophotometer MPF44B. As defined above, the relative fluorescence was expressed as: % rel. fluor. = (1/1*)x100 wherein 1 = fluorescence intensity of the blend, and 1* = fluorescence intensity of a blank PEN film. The results are summarized in table 2. UV-absorber in blend invention samples conc. (%) of UV-abs. % rel. fluor. at 429 nm V-20 0.25 79 " 0.50 62 " 1.00 42 V-19 0.25 69 " 0.50 52 " 1.00 42 comparison samples: benzotriazoles: TINUVIN 900 0.25 75 " 1.00 32 TINUVIN 326 0.25 55 TINUVIN 350 0.25 70 TINUVIN 329 0.25 68 aromatic ketones: UVINUL 400 0.25 70 UVINUL 3049 0.25 98 UVINUL D50 0.25 73 cinnamic acid esters: UVINUL 3088 0.25 78 UVINUL N35 0.25 79 UV-abs. 318 0.25 72 cyclic iminoester : CYASORB UV-3638 0.25 77 Conclusion : the invention UV-absorbers are about as efficient as quenchers of the UV-fluorescence as the comparison compounds. Example 3 In this examples PEN films with varying concentrations of TINUVIN 1577 (V-19) were prepared. First a master blend of PEN containing 8 % by weight of TINUVIN 1577 was prepared. In a stainless steel reactor provided with a stirrer, inlet for nitrogen, fractionation column, distillation apparatus and temperature control a PEN synthesis was performed by transesterification of 19,540 g of 2,6-naphthalenedicarboxylic acid-dimethylester with 9,920 g of ethyleneglycol in the presence of manganese acetate as transesterification catalyst. The reaction temperature was gradually increased from 180 to 250 °C while methanol was distilling over. At 250 °C 1.17 g of antimony trioxide as condensation catalyst, and 2.91 g of triethylphosphate as a stabilizer were added. Then the reaction temperature was raised to 285 °C and the transesterification product was polycondensed whilst stirring in vacuo (< 1 mbar) until the desired melt viscosity was reached after about 90-180 minutes. After the polycondensation step 1700 g of TINUVIN 1577 (V-19) were added and the mixture was stirred for 15 minutes under nitrogen atmosphere in order to obtain a homogeneous blend. Finally the melt was deposited in thread form, cooled with water and granulated. Blank PEN granulate (no UV-absorber) was mixed with varying amounts of the master blend PEN/V-19 prepared as explained above, and dried for 4 h at 160 °C in vacuo. The different PEN samples containing 0.08, 0.16, 0.32 and 0.64 % by weight of TINUVIN 1577 were transformed by extrusion, longitudinal and transversal stretching to films of 100 µm thickness. Table 3 shows the % relative fluorescence at 429 nm. conc. V-19 (%) % rel. fluorescence ) at 429 nm blank 100 0.08 85 0.16 75 0.32 52.5 0.64 32.5 The table illustrates the efficiency of the quenching of the fluorescence at 429 nm as a function of concentration of TINUVIN 1577 (= V-19). Example 4 - fluorescence and yellow colour of mixtures of PEN + UV absorbers added during synthesis. In this example a PEN synthesis was performed in a way similar to example 3 with the modification that the UV-absorber was added in a concentration of 0.5 % by weight immediately after the transesterification step and before the polycondensation step. After the condensation the yellow melt colour of the PEN blend was measured by comparing the that colour with standardized colour solutions prepared by dissolving the dye SANDOZ PYRAZOLE 3G, trade mark of Sandoz AG, in water. Figure 1 means a yellowing equal to that of a solution of 0.00025 dyestuff per 100 ml of water ; figure 2 means a yellowing equal to a solution of twice as much of dyestuff, etc.. The results are presented in table 4. compound rel. fluor. yellow colour. invention compounds: V-20 75 1 V-17 62 1 comparison compounds: TINUVIN 900 100 9 TINUVIN 350 100 4 UVINUL 400 91.5 9 UVINUL N35 100 3 CYASORB UV-3638 69 7 While the fluorescence quenching was comparable for invention and comparison compounds in the experiment of example 2 (see table 2) it is clear that in this experiment the invention UV-absorbers are still efficient while the comparison compounds are inefficient (except for the cyclic iminoester CYASORB UV-3638). This is due to the fact that in this method of blending during the synthesis the UV-absorber is subjected to a still longer period of high temperatures than when the blending is realized after synthesis. So this experiment again indirectly illustrates the much better thermal stability of the UV-absorbers used in the present invention. On the other hand it is also clear from the table that the yellow colour of the blend is much more pronounced for the comparison compounds including the cyclic iminoester CYASORB UV-3638. This is important in the case of application of PEN as support for a photographic silver halide material. Example 5 - xenon test This example illustrates the suppression of the yellowing of PEN under the influence of light by means of the UV-absorbers used in accordance with the present invention. This yellowing is simulated by a xenon test. Film strips prepared from PEN/UV-absorber blends similar to those of example 2 were subjected to exposure by a xenon light source of 180,000 lux during 4 weeks. The yellowing of the PEN film strips compared to an unexposed sample were determined by measuring the CIE tristimuli values L,a,b and of the total chromatic value CAB. The results are presented in table 5. UV-abs. unexposed 3 weeks xenon L a b CAB L a b CAB none 94.2 -0.1 1.1 1.1 93.1 -1.5 7.1 7.5 V-19 (inv.) 94.0 -0.2 1.5 1.5 94.2 -1.2 4.6 4.8 TINUVIN 900 (comp.) 93.7 -0.1 1.3 1.3 94.2 -1.2 4.6 4.9 As it is clear from table 5 the shift in the chromatic values after xenon test is more pronounced in the absence of a UV-absorber. The result obtained with TINUVIN 1577 (V-19: invention) is comparable with a comparison compound such as TINUVIN 900, disclosed in EP 0 631 177.

Claims: Polyester film made of polyalkylene naphthalate or a derivative thereof and containing an UV-absorber according to following general formula : wherein R 1 and R 3 each independently represent hydrogen, halogen, -OR 6 , mercapto, alkyl, aryl, alkoxy, aryloxy, acyl, alkylthio, -NR 5 -R 6 , alkoxycarbonyl, carbamoyl, sulfamoyl, aryloxycarbonyl, each of which can be further substituted, R 2 represents hydrogen, hydroxy, halogen or alkyl, each of which can be further substituted, R 4 represents alkyl, alkoxy, alkylthio, aryloxy, arylthio, each of which can be further substituted, or a moiety represented by R 5 represents hydrogen, alkyl or aryl, each of which can be further substituted, R 6 represents hydrogen, alkyl, aryl, acyl, alkoxycarbonyl, aryloxycarbonyl, carbamoyl, sulfamoyl or sulfonyl, each of which can be further substituted, R 7 and R 8 have one of the significances given for R 2 and R 3 respectively, and wherein m, n and o each independently represent 1,2,3 or 4. Polyester film according to claim 1 wherein in general formula (I) R 1 represents substituted or unsubstituted p.-alkoxy, and R 4 represents a moiety represented by as defined in claim 1. Polyester film according to claim 2 wherein said UV-absorber is chosen from following compounds : Polyester film according to any of claims 1 to 3 wherein said polyalkylene naphthalate or derivative thereof is the homopolymer of naphthalene-2,6-dicarboxylic acid and ethylene glycol (PEN). Photographic material comprising a support and at least one silver halide emulsion layer characterized in that said support is made of polyalkylene naphthalate or a derivative thereof and contains an UV-absorber according to following general formula : wherein R 1 and R 3 each independently represent hydrogen, halogen. -OR 6 , mercapto, alkyl, aryl, alkoxy, aryloxy, acyl, alkylthio, -NR 5 -R 6 , alkoxycarbonyl, carbamoyl, sulfamoyl, aryloxycarbonyl, each of which can be further substituted, R 2 represents hydrogen, hydroxy, halogen or alkyl, each of which can be further substituted, R 4 represents alkyl, alkoxy, alkylthio, aryloxy, arylthio, each of which can be further substituted, or a moiety represented by R 5 represents hydrogen, alkyl or aryl, each of which can be further substituted, R 6 represents hydrogen, alkyl, aryl, acyl, alkoxycarbonyl, aryloxycarbonyl, carbamoyl, sulfamoyl or sulfonyl, R 7 and R 8 have one of the significances given for R 2 and R 3 respectively, and wherein m, n and o each independently represent 1,2,3 or 4. Photographic material according to claim 5 wherein in general formula (I) R 1 represents substituted or unsubstituted p.-alkoxy, and R 4 represents a moiety represented by as defined in claim 1. Photographic material according to claim 6 wherein said UV-absorber is chosen from following compounds : Photographic material according to any of claims 5 to 7 wherein said polyalkylene naphthalate or derivative thereof is the homopolymer of naphthalene-2,6-dicarboxylic acid and ethylene glycol (PEN). Photographic material according to any of claims 5 to 8 wherein the material is a colour negative material or a colour reversal material.

Inventors: AUGUST MARIEN, HAGEMANN JOERG, WEBER BEATE, AUGUST, MARIEN, HAGEMANN, JOERG, WEBER, BEATE, Hagemann, Jörg
Applicants: AGFA GEVAERT, AGFA-GEVAERT
Application year: 1997
Main classification: C08K5
IPC codes: G03C1, C08J5, C09K3, C08L67, G03C5, G03C7, C08K5