ALDEHYDE-MODIFIED CELLULOSIC FIBERS FOR PAPER PRODUCTS HAVING HIGH INITIAL WET STRENGTH

Abstract: Modified cellulosic fibers are formed by (1) esterifying cellulosic fibers with a 1,2-disubstituted alkene that has at least one carboxylic acid group reactive with cellulosic hydroxyl groups and (2) oxidizing the esterified fibers to form aldehyde groups. The modified fibers are useful in paper products, which tend to have temporary wet strength. Strength additives may be included in the paper product to impart a higher level of temporary wet strength or permanent wet strength.

Description: ALDEHYDE-MODIFIED CELLULOSIC FIBERS FOR PAPER PRODUCTS HAVING HIGH INITIAL WET STRENGTH FIELD OF THE INVENTION This invention relates to modified celluiosic fibers, more particularly such fibers which are useful for providing paper products having a good initial wet strength. BACKGROUND OF THE INVENTION Wet strength is a desirable attribute of many disposable paper products that come into contact with water in use, such as napkins, paper towels, household tissues, disposable hospital wear, etc. In particular, it is often desirable that such paper products have sufficient wet strength to enable their use in the moistened or wet condition. Thus, the product should resist tearing, ripping, disintegration and the like such that it substantially maintains its integrity during the intended use. For example, moistened tissue or towel may be used for body or other cleaning. Unfortunately, an untreated assemblage of unmodified celluiosic fibers will typically lose 95% to 97% of its strength when saturated with water such that it cannot usually be used in the moistened or wet condition. As recognized in the art, paper products develop dry strength in part due to interfiber hydrogen bonding. When the paper product is wetted, water disrupts the hydrogen bonds and, as a consequence, lowers the strength of the paper product. Historically, wet strength of paper products has been increased primarily by two approaches. One approach is to prevent water from reaching and disrupting the hydrogen bonds, for example, by coating the paper product. Another approach is to incorporate additives in the paper product which contribute toward the formation of interfiber bonds which are not broken or, for temporary wet strength, which resist being broken, by water. The second approach is commonly the technique of choice, especially for tissue products. In this latter approach, a water soluble wet strength resin may be added to the pulp, generally before the paper product is formed (wet-end addition). The resin generally contains cationic functionalities so that it can be easily retained by the celluiosic fibers, which are naturally anionic. A number of resins have been used or disclosed as being particularly useful for providing wet strength to paper products. Certain of these wet strength additives have resulted in paper products with permanent wet strength, i.e., paper which when placed in an aqueous medium retains a substantial portion of its initial wet strength over time. Exemplary resins of this type include urea- formaldehyde resins, melamine-formaldehyde resins and poiyamide-epichiorohydrin resins. Such resins have limited wet strength decay. Therefore, manufacturers have more recently added temporary wet strength additives to paper products for which wet strength is sufficient for the intended use, but which then decays upon soaking in water Decay of the wet strength facilitates flow of the paper product through septic systems Numerous approaches for providing paper products claimed as having good initial wet strength which decays significantly over time have been suggested For example U S Pat No 3 096,228, Day et al , issued July 2, 1983, U S Pat No 3,556,932, Coscia et al , issued Jan 19, 1971 , U S Pat No 3,740,391 , Williams et al , issued June 19, 1973, and U S Pat No 4,605,702, Guerro et al , issued August 12, 1986, and U S Pat No 4,675,394, Solarek, et al , issued June 23, 1987, suggest various approaches for achieving temporary wet strength with polymers or other compounds It is also known to modify celluiosic fibers to contain aldehyde groups, for example, as descπbed by T G Gafurov et al , Strukt Modif Khlop Tsellyul , Vol 3, pp 131-135 (1966) While the art has provided a variety of paper products havmg initial wet strength, none has provided paper products in the manner of the present invention It has now been found that celluiosic fibers that are reacted with 1 ,2-dιsubstιtuted carboxy c alkenes followed by oxidation impart wet strength to paper products containing the resultant modified fibers It is an object of this mvention to provide celluiosic fibers which are modified to contain aldehyde groups, and paper products, including paper tissue products such as toilet tissue, comprising such fibers It is a further object to provide paper products having wet strength Yet another object of this mvention is to provide paper products havmg temporary wet strength SUMMARY OF THE INVENTION The present mvention relates to celluiosic fibers that are modified to contain aldehyde groups The present invention also relates to paper products containing such fibers The modified fibers tend to provide paper products havmg a high initial wet tensile strength (e g , at least about 80 g/inch, preferably at least about 120 g/inch), which is temporary Preferred modified celluiosic fibers of this mvention are formed by oxidizing celluiosic fibers which have been reacted through a portion of its hydroxyl groups with a carboxyhc group of a 1 ,2-dιsubstιtuted carboxylic alkene to form covalent linkages The alkene preferably has at least one other carboxyl group such that the alkene is capable of forming an anhydride DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS The modified celluiosic fibers of the present invention can be formed by oxidizing celluiosic fibers that have been reacted with a 1,2 disubstituted alkene containing at least one carboxylic functional group capable of reacting with the celluiosic hydroxyl groups to form covalent linkages (the 1,2 disubstituted alkene is alternatively referred to herein as "carboxylic alkene" The celluiosic fibers that have been reacted with the carboxylic alkene yet not oxidized are herein after alternatively to as "intermediate celluiosic fibers" or "intermediate celluiosic fiber reaction product" The intermediate celluiosic fibers can be denved from a variety of celluiosic fibers Celluiosic fibers of diverse natural origin are applicable to the invention Digested fibers from softwood (derived from coniferous trees), hardwood (derived from both deciduous trees) or cotton linters are preferably utilized. Fibers from Esparto grass, bagasse, kemp, flax, and other lignaceous and celluiosic fiber sources may also be utilized as raw material in the invention. The optimum celluiosic fiber source utilized in conjunction with this invention will depend upon the particular end use contemplated. Generally wood pulps will be utilized. Applicable wood pulps include chemical pulps, such as Kraft (i.e., sulfate) and sulfite pulps as well as mechanical pulps including, for example, groundwood, thermomechanical pulp (i.e., TMP) and chemithermomechanical pulp (i.e., CTMP). Chemical pulps, however, are preferred since they impart a superior tactile sense of softness to tissue sheets made therefrom. Completely bleached, partially bleached and unbleached fibers are applicable. It may frequently be desired to utilize bleached pulp for its superior brightness and consumer appeal. For products such as paper tissue, paper towels and absorbent pads for diapers, sanitary napkins, catamenials, and other similar absorbent paper products, it is especially preferred to utilize fibers from northern softwood pulp due to its premium strength characteristics. Also useful in the present invention are celluiosic fibers derived from recycled paper, which can contain any or all of the above categories as well as other non-fibrous materials such as fillers and adhesives. The celluiosic fibers are reacted with a 1,2 disubstituted alkene containing at least one carboxylic functional group to form the intermediate fibers. The carboxylic functional group may be, for example, a carboxylic acid group (- COOH) or an acid amide group (- CONH2), and is preferably a carboxylic acid group. The carboxylic acid group reacts with a celluiosic hydroxyl group to form an ester linkage, as does an acid amide group. However, the acid amides are far less reactive than the carboxylic acid groups and are therefore less preferred. By "1,2-disubstituted," it is meant that each of the doubly bonded carbons is singly bonded to one carbon atom other than the doubly bonded carbon atom, and to a hydrogen atom (-HC=CH-). Without intending to be bound by theory, it is believed that if each doubly bonded carbon atom is not bonded to at least one carbon atom, formaldehyde undesirably tends to form during the oxidation of the intermediate celluiosic fibers. On the other hand, if more than one carbon atom is bonded to each doubly bonded carbon atom, ketones are undesirably formed when the intermediate celluiosic fibers are oxidized. The carboxylic alkene may contain one or more carbon-carbon double bonds and may contain other multiple bonds. The 1,2-disubstituted carbon-carbon double bond is preferably in a cyclic structure. Cyclic alkenes tend to lose fewer aldehyde groups during oxidation of the intermediate celluiosic fibers, relative to acyclic alkenes. Without intending to be bound by theory, it is believed that the number of aldehyde groups should be maximized in order to maximize the number of hemi-acetal groups and/or N-acylhemiaminal groups in the final paper product, and thus to maximize the wet strength of the paper product containing the modified celluiosic fibers. In preferred embodiments, the carboxylic alkene is a polycarboxylic compound that contains at least one additional carboxylic functional group such that the compound is capable of forming an anhydride Such polycarboxylic compounds tend to more readily react with the hydroxyl groups of the celluiosic fibers to form the intermediate celluiosic fibers such that yields of the modified celluiosic fibers of the present invention are higher than when the carboxylic alkene is not capable of forming an anhydride As used herein, "anhydride" refers to chemical compounds derived from an acid by the elimination of a molecule of water The second carboxylic functional group may suitably be a carboxylic acid group or an acid amide group. Thus, the carboxylic alkene may be capable of forming a dicarboxylic acid anhydride or a cyclic imide It is preferred that each of the carboxylic groups be a carboxylic acid group More preferably, the carbon atoms of the carboxylic groups of the polycarboxylic compound are separated by 2-3 carbon atoms in order to facilitate the formation of the anhydride (i.e., the carboxylic groups are positioned 1,2 or 1,3 relative to one another). Most preferably, the carbon atoms of the carboxyl group are separated by 2 carbon atoms since the 1,2 polycarboxylic compounds form anhydrides more readily at lower temperatures than the 1,3 polycarboxylic compounds. The 1,2-disubstituted alkene group and the carboxylic functional group(s) are preferably unconjugated. Without intending to be bound by theory, it is believed that Michael Addition ( 1 ,4) can occur to the alkene bond during the esterification reaction where the alkene group and the carboxylic group(s) are conjugated. This addition reaction would destroy the alkene bond and thus negate aldehyde formation during oxidation ofthe intermediate celluiosic fibers Preferred carboxylic alkenes are water soluble so as to enable a water-based process. As used herein, "water soluble" includes the ability of a material to be dissolved, dispersed, swollen, hydrated or similarly admixed in water Similarly, as used herein, reference to the phrase "substantially dissolved," "substantially dissolving" and the like refers to the dissolution, dispersion, swelling, hydration and the like admixture of a mateπal in a liquid medium (e.g., water) The mixture typically forms a generally uniform fluid mixture having, to the naked eye, one physical phase Suitable carboxylic alkenes include, but are not limited to, cιs-l ,2,3,6-tetrahydrophthalic acid and 1,2,3,6-tetrahydrophthalamιc acid Derivatives of such compounds, e.g., substituted analogs thereof wherein any of the carbon atoms other than the doubly bonded carbon atoms are mono- or poly- substituted, are also suitable for use herein. A variety of substituent groups may be present However, the substituent groups should not provide steric hindrance or electronic deactivation of the esterification step such that the rate of esterification is decreased. For reasons of availability and rapid reaction times, the carboxylic alkene is preferably cis- 1 ,2,3, 6- tetrahydrophthahc acid. The intermediate celluiosic fibers can be formed by a process including the steps of preparing a fluid mixture of the carboxylic alkene and a liquid medium; contacting the celluiosic fibers with the fluid mixture so as to form treated fibers; and reacting at least a portion of the celluiosic hydroxyl groups with a carboxylic functional group of the alkene to form a covalent linkage. The resultant intermediate celluiosic fibers are then oxidized as described herein below to form aldehyde groups. Suitable liquid media are those that can substantially dissolve or disperse the carboxylic alkene, preferably that provides maximum solubility of the carboxylic alkene in the fluid mixture. The liquid medium may contain one or more solvents for the carboxylic alkene compound. Suitable liquid media include water, pyridine, other aprotic solvents, and mixtures thereof. Water is the preferred liquid medium. The carboxylic alkene and liquid medium can be combined and mixed together by any suitable method such as are known in the art of forming solutions or dispersions. It is typically preferred to maximize the concentration of the carboxylic alkene in the fluid mixture in order to reduce the time and energy required to evaporate the liquid medium to provide the modified celluiosic fibers of the present invention. Heating can be employed to enhance solubility of the carboxylic alkene in the liquid medium. For example, the fluid mixture may be heated to temperatures of from about 50°C to about 100°C. The celluiosic fibers can be contacted with the fluid mixture containing the carboxylic alkene by a combination of one or more techniques such as are known in the art of papermaking, e.g., immersion, mixing, dumping, spraying, dipping and squeezing, and the like. In a preferred embodiment, the celluiosic fibers are contacted with the fluid mixture at the wet end of a paper machine in the pulp process of making paper sheets (i.e., wet laid papermaking process). According to this embodiment, the pulp sheet is sprayed with the fluid mixture at the wet end ofthe process. For conventional commercial processes, the sheet should be greater than about 20% consistency, preferably from 20-50% consistency, to maintain adequate web strength. It has suφrisingly been found that the dry tensile and initial total wet tensile strength of paper sheets of the present invention increase with an increase in the basis weight of the pulp sheet which is sprayed. In a particularly preferred embodiment, the pulp sheet has a basis weight of from about 180 to about 260 lb/3000 ϋr. The pulp sheet is then dried and heated as described herein, beyond to at least the point of no further weight loss by evaporation to effect reaction between the celluiosic fibers and the carboxylic alkene. In an alternative embodiment, the celluiosic fibers and the fluid mixture containing the carboxylic alkene are contacted by forming a slurry of the celluiosic fibers in the fluid mixture (e.g., by immersing and mixing). Thus, the fibers and alkene may be contacted by including the alkene in the papermaking furnish of a wet laid papermaking process such as are known in the art. The fluid mixture containing the carboxylic alkene is prepared, and brought into contact and reacted with the celluiosic fibers to provide a degree of substitution on the cellulose molecule of from about 0.25 to about 1.5, more preferably from about 0.5 to about 1.0, most preferably about 1.0 (1 e , from about 0 25 to about 1 5 mole %, preferably from about 0 5 to about 1 0 mole %, most preferably about I 0 mole % celluiosic hydroxyl groups calculated on a cellulose anhydroglucose molar basis, will be reacted with a carboxyl group ofthe alkene to form covalent linkages) The treated fibers are heated to a temperature and for a time sufficient to substantially remove the liquid medium and to cause the celluiosic hydroxyl groups and a carboxyhc functional group of the alkene to react to form covalent linkages Where the preferred carboxy c compounds, the polycarboxylic compounds, are used, the treated fibers are heated to a temperature and for a time sufficient to substantially remove the liquid medium from the fibers, to form the anhydride of the polycarboxylic compound, and to cause the covalent bond formation between the carboxylic alkene and the celluiosic hydroxyl groups Where water is used as the liquid medium, the treated fibers are preferably heated to at least about 100°C to evaporate the water Evaporation and reaction are typically caused by heating the treated fibers to a temperature in the range of from about 120°C - 180°C for a period of about 30 minutes to 2 hours In a preferred embodiment, the covalent bond formation is catalyzed by a suitable catalyst The catalyst tends to result in a faster reaction rate, less decomposition of the celluiosic fibers, and a higher yield of the intermediate celluiosic fibers Any catalyst such as are known in the art of esterification may be used A preferred catalyst is sodium hypophosphite (NaH2Pθ2), which tends to provide higher yields and to minimize decomposition of the celluiosic fibers at higher reaction temperatures The use of sodium hypophosphite as an esteπfication catalyst has been descnbed, for example, in U S. Patent 4,820,307, issued to C M Welch, incoφorated here by reference The catalyst is suitably included in the fluid mixture containing the carboxylic alkene Where the preferred 1 ,2-dιsubstιtuted alkenes are used, the resultant intermediate celluiosic fibers with a degree of substitution of 1.0 have the following structure wherein R' is OH or NH 2 , and n is the degree of polymerization (l e , DP) of the cellulose fibers and is at least one ( 1). preferably 1- 10,000 T e resultant intermediate celluiosic fibers are then oxidized to form the modified celluiosic fibers of the present invention Prior to oxidation, the intermediate celluiosic fibers are preferably washed to remove any residual, unreacted carboxylic compound The fibers may suitably be washed with a dilute aqueous solution of a base, e.g., aqueous sodium carbonate. Oxidation is accomplished by contacting the intermediate celluiosic fibers with an oxidizing agent under conditions to cause the formation of aldehyde groups on the residue of the carboxylic alkene. Oxidation is preferably accomplished by forming a mixture, e.g., a slurry or other dispersion, of the intermediate celluiosic fibers and a suitable liquid medium and introducing an oxidizing agent into the mixture under conditions such that the formation of aldehyde groups occurs on the residue of the carboxylic alkene. Suitable liquid media are those that do not significantly interfere with the oxidation reaction and which may assist in dispersing the fibers. Exemplary liquid media include water, organic solvents such as acetic acid, lower alcohols, chlorinated hydrocarbons, and mixtures thereof. Water is the preferred liquid medium. The amount of the liquid medium and the fibers in the mixture may vary over a wide range. Typically, the mixture comprises from about 0.1 to about 50 weight % of the fibers and from 99.9 to about 50 weight % of the liquid medium. Thus, the mixture can be low consistency (e.g., about 1 - 3.5% fiber/99-96.5% liquid medium), medium consistency (e.g., about 8- 16% fiber/92-84% aqueous liquid medium), or high consistency (e.g., about 20-50% fiber/50-80% aqueous liquid medium). Suitable oxidizing agents include ozone and potassium permanganate. Ozone is the preferred oxidizing agent. Ozone is the preferred oxidation agent for reasons of reaction efficiency, simplicity, economics, environmental impact, and safety. Ozone oxidation can be accomplished by introducing ozone into the mixture, e.g., by injecting the gas under pressure into the mixture. Although the flow rate and pressure of the ozone may vary over a wide range, exemplary conditions include a flow rate of about 8.0 liters/minute and a flow pressure of about 8 psig. The mixture is preferably cooled to a temperature as low as possible without freezing the mixture (e.g., to temperatures down to about 0°C) in order to maximize the solubility of the ozone in the mixture. The oxidation reaction is typically completed by introducing the ozone under the foregoing conditions for a period ranging from about 30 to about 60 minutes. During the oxidation step, aldehyde groups are formed on the carboxylic alkene residue of the intermediate celluiosic fibers. Without intending to be bound by theory, it is believed that at least a portion of the aldehydes are present on the fiber surface to facilitate interfiber bonding during the papermaking process. Aldehyde groups may also be formed in the fiber interior and or in the fiber wall (i.e., intrafiber aldehyde groups). The formation and quantification of aldehyde groups can be determined by known analytical techniques such as infrared analysis. Alternatively, the presence of aldehyde groups is evidenced by an increase in the wet strength of a paper product formed from the modified fibers, relative to a corresponding paper product formed from non-modified fibers. In general, for a given fiber weight, oxidizing agent concentration, and set of reaction conditions, oxidation increases with increasing time of exposure to the oxidizing agent. Thus, the degree of oxidation can be readily optimized for a given fiber weight by quantifying the aldehyde content as a function of time by any of the foregoing methods. It will be desired to avoid the over oxidation of the fibers to cause significant formation of carboxylic acid groups, which can be detected and quantified using the same techniques. The modified fibers also contain hydroxyl groups. Without intending to be bound by theory, it is believed that the hydroxyl groups react with the aldehyde groups to confer temporary wet strength to the paper product as further described herein. Where the preferred 1 ,2-disubstituted alkenes are used, the resultant modified fibers with a degree of substitution of 1.O have the following structure: wherein R' and n are as defined above. The resultant modified celluiosic fibers of the invention can be recovered by removing the bulk of the liquid medium and then drying the fibers. For example, the modified fibers may be sheeted after optional further dilution and using conventional wet laid papermaking processes, and then dried. Accelerated drying may be accomplished, for example, by heating to a temperature and for a time sufficient to substantially remove the liquid medium, e.g., heating to about 85°C to about 125°C to achieve substantially constant weight. The modified celluiosic fibers can thus be collected for later use in a papermaking process. Alternatively, the mixture containing the modified celluiosic fibers can be incoφorated into a continuous paper making process such as are known in the art, e.g., in the papermaking furnish of a wet laid paper making process, without recovering the fibers. The modified celluiosic fibers ofthe present invention are useful for a wide variety of paper and paper products. As used herein, the terms "paper" and "paper products" include sheet-like masses and molded products containing the modified celluiosic fibers ofthe invention. In addition to the modified celluiosic fibers herein described, the paper products of the present invention may contain conventional or other papermaking materials. For example, the paper products may contain conventional papermaking fibers, including chemically modified or unmodified celluiosic fibers. The paper products may also contain non-cellulosic fibrous polymeric material characterized by having hydroxyl groups attached to the polymer backbone, for example glass fibers and synthetic fibers modified with hydroxyl groups. Other fibrous material, e.g., synthetic fibers, such as rayon, polyethylene and polypropylene fibers, can also be utilized in combination with natural celluiosic fibers or other fibers containing hydroxyl groups. Fibrous material having hydroxyl groups may be chemically modified to contain aldehyde groups in the manner of the celluiosic fibers of the present invention and incoφorated into the paper product. Mixtures of any of the foregoing fibers may be used in combination with the modified celluiosic fibers of the present invention. Conventional paper-making additives such as are known in the art include, for example, dry strength and wet strength additives, retention aids, and paper softeners. As will be understood by one having ordinary skill in the art, wet strength resins may be selected to impart temporary or permanent wet strength. For example, it has been found that polyacrylamides tend to impart a more permanent wet strength to paper products formed from the modified celluiosic fibers of the present invention. The paper products are typically formed by a wet laid paper making process. Wet laid paper making processes typically include the steps of providing a slurry containing the papermaking fibers (the slurry is alternatively referred to herein as a paper making furnish), depositing the slurry of fibers on a substrate such as a foraminous forming wire (e.g., a Fourdrinier wire), and setting the fibers into a sheeted form while the fibers are in a substantially unflocculated condition. The step of setting the fibers into sheeted form may be performed by allowing the fluid to drain and pressing the fibers against the foraminous wire (dewatering), for example, with a screened roll, such as a cylindrical Dandy Roll. Once set, the fibrous sheet is then dried and optionally compacted as desired. The drying step removes water and any other liquids so as to develop the wet strength of the paper product. Drying may be accomplished by subjecting the paper product to elevated temperatures, e.g., in the range of from 85°C - 125°C, for a time sufficient to achieve the desired level of dryness, typically less than about 10% water and/or other liquids. Typical drying conditions are a temperature of from 20° C to about 100° C. Without intending to be bound or otherwise limited by theory, it is believed that upon drying of the paper product comprising the modified celluiosic fibers of the present invention, the aldehyde groups of the modified celluiosic fibers form hemi-acetal and/or N-acylhemiaminal groups with proximal celluiosic hydroxyl groups. These hemi-acetal groups serve to impart dry strength and an initial wet strength to the paper product, yet are readily decomposed by water. Thus, when the paper product is exposed to aqueous fluids, the hemi-acetal and/or N-acylhemiaminal groups revert to aldehyde groups to provide a temporary wet strength to the paper product. The present invention is particularly adapted for paper products which are to be disposed into sewer systems, such as toilet tissue. However, it is to be understood that the present invention is applicable to a variety of paper products including, but not limited to disposable absorbent paper products such as those used for household, body, or other cleaning applications and those used for the absoφtion of body fluids such as urine and menses. Exemplary paper products thus include tissue paper including toilet tissue and facial tissue, paper towels, absorbent materials for diapers, feminine hygiene articles including sanitary napkins, pantiliners and tampons, adult incontinent articles and the like, and writing paper With regard to tissue paper, the modified celluiosic fibers of the present invention can be used in any type of tissue paper construction For example, tissue paper of the present invention can be homogeneous or multi-layered construction, and tissue paper products made therefrom can be of a s gle-ply or multi-ply construction The tissue paper preferably has a basis weight of between about 10 g/m- and about 65 g/m , and density of about 0 6 g/cm J or less More preferably, the basis weight will be about 40 g/m- or less and the density will be about 0 3 g/cm 3 or less Most preferably, the density will be between about 0 04 g/cm 3 and about 0 2 g/cm 3 See Column 13, lines 61-67, of U S Patent 5,059,282 (Ampulski et al), issued October 22, 1991, which describes how the density of tissue paper is measured (Unless otherwise specified, all amounts and weights relative to the paper are on a dry basis ) The tissue paper may be conventionally pressed tissue paper, pattern densified tissue paper, and uncompacted, nonpattern-densified tissue paper These types of tissue paper and methods for making such paper are well known in the art and are described, for example, in U S Patent 5,334,286, issued on August 2, 1994 in the names of Dean V Phan and Paul D Trokhan, incoφorated herein by reference in its entirety EXPERIMENTAL Strength Tests The paper products are aged prior to tensile testing a minimum of 24 hours in a conditioned room where the temperature is 73 °F + 4 °F (22 8 °C + 2 2 °C) and the relative humidity is 50% + 10% 1 Total Dry Tensile Strength ("TDT") This test is performed on one inch by five inch (about 2 5 cm X 12 7 cm) strips of paper (including handsheets as descnbed above, as well as other paper sheets) in a conditioned room where the temperature is 73°F + 4°F (about 28°C + 2 2°C) and the relative humidity is 50% + 10% An electronic tensile tester (Model 1122, Instron Coφ , Canton, Mass ) is used and operated at a crosshead speed of 2 0 inches per minute (about 1 3 cm per mm ) and a gauge length of 4 0 inches (about 10.2 cm) Reference to a machine direction means that the sample being tested is prepared such that the 5" dimension corresponds to that direction Thus, for a machine direction (MD) TDT, the stnps are cut such that the 5" dimension is parallel to the machine direction of manufacture of the paper product For a cross machine direction (CD) TDT, the strips are cut such that the 5" dimension is parallel to the cross-machine direction of manufacture of the paper product Machine-direction and cross-machine directions of manufacture are well known terms in the art of paper-making The MD and CD tensile strengths are determined using the above equipment and calculations in the conventional manner The reported value is the arithmetic average of at least eight strips tested for each directional strength The TDT is the arithmetic total of the MD and CD tensile strengths 2 Wet Tensile An electronic tensile tester (Model 1 122. Instron Coφ ) is used and operated at a crosshead speed of 0 5 inch (about 1 3 cm) per minute and a gauge length of 4 0 inch (about 10 2 cm), using the same size strips as for TDT The strip is wetted with distilled water at about 20°C for the desired soak time, and then measured for tensile strength As in the case of the TDT, reference to a machine direction means that the sample being tested is prepared such that the 5" dimension corresponds to that direction The MD and CD wet tensile strengths are determined using the above equipment and calculations in the conventional manner The reported value is the arithmetic average of at least eight strips tested for each directional strength The total wet tensile strength for a given soak time is the arithmetic total of the MD and CD tensile strengths for that soak time Initial total wet tensile strength ("ITWT") is measured when the paper has been saturated for about 5 ± 0 5 seconds The following non-limiting examples are provided to illustrate the present invention The scope ofthe mvention is to be determined by the claims which follow Preparation of paper web of ozone oxidized. cιs-l,2.3.6-tetrahvdrophthalιc acid ester of celluiosic fibers Example 1 (handsheets) Handsheets are made essentially accordmg to TAPPI standard T205 with the following modifications (1) tap water, adjusted to a desired pH, generally between 4 0 and 4 5, with H2SO4 and/or NaOH is used, (2) the sheet is formed on a polyester wire and dewatered by suction instead of pressing, (3) the embryonic web is transferred by vacuum to a polyester papermaking fabπc, and (4) the sheet is then dπed by steam on a rotary drum dπer To a dry 12" x 12" handsheet of unmodified papermaking fibers, 28 lb/3000 ft2 basis weight, an aqueous solution of cιs-l ,2,3,6-tetrahydrophthalιc acid and sodium hypophosphite (29 gm l) at H 4, is sprayed until 10 % (fiber basis) ofthe acid and 0 5% (fiber basis) of hypophosphite is applied. The handsheet is dried in a forced air oven at room temperature to constant weight The sheet is then cured in a forced au oven at 180°C for 30 minutes The cured sheet is washed in demtneralized water at pH 2 and dewatered to 40% consistency The resultant fibers at 40% consistency are fluffed and ozone oxidized for 30 minutes or one hour at room temperature with a Welsbach Ozone Generator, Model T-816 The fibers are ozone oxidized at an oxygen flow rate of about 8 0 liters/minute and flow pressure of about 8 psig, at a temperature of 0°C or less The 18 lb/3000 ft^ basis weight handsheets prepared from the resultant fibers have tensile strengths such as shown in Table I TABLE Oxidation Time Total Dry Tensile Initial Total Wet Tensile minutes g inch g/inch 30 593 1 17 60 1389 213 As shown in Table 1 , one hour of oxidation produces a higher initial wet tensile than 30 minutes of oxidation Example 2 (paper machine) A pulp sheet (unrefined NSK fibers, having, e g , a DP of 1500) having basis weight 260 lb/3000 ft-, is formed on a conventional paper machine (Sandy Hill Manufacture) and wet pressed to 49% solids A 20% solids aqueous solution of tetrahydrophthalic acid (THPA) and sodium hypophosphite at 60° C are applied onto the sheet such that a 10% (fiber basis) application of THPA and a 0 5% (fiber basis) application of sodium hypophosphite is achieved The sheet is then passed through a section of can dryers at 300°F for 2 - 3 minutes to dry the sheet and to react the THPA and the fibers to form esterified fibers The resultant esterified pulp sheets are subsequently treated with ozone for one hour, as descπbed in Example 1 The resultant fibers are formed into a handsheet by conventional methods and apparatus The paper sheet has a basis weight of 18 lb/3000 ft 2 , a caliper of 7 4 mils, a density of 0 142 g/cc, a total dry tensile strength of 2106 grams/m, and a total initial wet tensile strength of 586 grams/inch A pulp sheet of lightly refined NSK fibers (Canadian Standard Freeness = 639 ml, havmg, e g , a DP of 1500) having basis weight 260 lb/3000 ft 2 is prepared and treated as described in the foregoing paragraph The resultant treated pulp sheet is ozone oxidized and the resultant fibers are formed into a handsheet as descπbed in the foregoing paragraph The paper sheet has a basis weight of 18 lb/3000 ft 2 , a caliper of 8 4 mils, a density of 0 125 g/cc, a total dry tensile strength of 2565 grams/m, and a total initial wet tensile strength of 794 grams/inch Comparable handsheets formed from Aspen or SF Ponderosa fibers that have been treated as described for this example have total dry tensile and initial total wet tensile strengths that are significantly less than that obtamed for sheets formed from the NSK fibers While particular embodiments of the present mvention have been illustrated and descπbed, it would be obvious to those skilled m the art that various other changes and modifications can be made without departmg from the spirit and scope of the mvention It is therefore intended to cover in the appended clauns all such changes and modifications that are withm the scope of this mvention WHAT IS CLAIMED IS

Claims: 1. Aldehyde-modified celluiosic fibers characterized in that the fibers are prepared by oxidizing the reaction product of (i) celluiosic fibers having hydroxyl groups and (ii) a 1,2-disubstituted alkene, preferably a cyclic alkene, having a carboxylic functional group capable of reacting with said hydroxyl groups, wherein in said reaction product at least a portion of said hydroxyl groups are reacted with said carboxylic group of said alkene to form covalent linkages, said reaction product being oxidized, preferably with ozone, to form aldehyde groups. 2. The modified celluiosic fibers of Claim 1 wherein said alkene has at least two carboxylic functional groups, said carboxylic functional groups being capable of forming an anhydride, preferably wherein said carboxylic functional groups of said alkene are positioned 1,2 or 1,3 relative to one another, more preferably wherein the alkene group and said carboxylic functional groups of said alkene are unconjugated. 3. The modified celluiosic fibers of Claim 2 wherein said carboxylic functional groups are independently selected from the group consisting of carboxylic acid groups and acid amide groups, preferably wherein said carboxylic functional groups are carboxylic acid groups. 4. The modified celluiosic fibers of Claim 3 wherein said alkene is selected from cis- 1,2,3, 6- tetrahydrophthalic acid, cis-l,2,3,6-tetrahydrophthalamic acid, and mixtures thereof. 5. The modified celluiosic fibers of Claim 1 wherein 0.25 to 1.5 mole %, calculated on a cellulose anhydroglucose molar basis, of said hydroxyl groups of said celluiosic fibers are reacted with said carboxylic functional group of said alkene. 6. A paper product comprising the modified celluiosic fibers of any ofthe preceding claims. 7. A method of making aldehyde-modified celluiosic fibers, characterized in that the method comprises the steps of: (a) providing (i) celluiosic fibers having hydroxyl groups and (ii) a fluid mixture of a liquid medium and a 1,2-disubstituted alkene having a carboxylic functional group capable of reacting with celluiosic hydroxyl groups; (b) contacting the celluiosic fibers with said fluid mixture to form treated fibers; (c) reacting a portion of said hydroxyl groups of said celluiosic fibers with said carboxylic functional group of said alkene to form covalent linkages to form intermediate celluiosic fibers, and (d) reacting said intermediate celluiosic fibers with an oxidizing agent to form aldehyde groups The method of Claim 7 wherein said steps (b) and (c) comprise the steps of: (i) providing a slurry containing the celluiosic fibers and water; (ii) depositing the slurry on a foraminous substrate; (iii) setting the fibers into a sheeted form while the fibers are in a substantially unflocculated condition to form a pulp sheet having a consistency of 20 - 50% and a basis weight of 180 - 260 lb/3000 ft 2 ; (iv) contacting the celluiosic fibers ofthe pulp sheet with said fluid mixture; and (v) reacting a portion of said hydroxyl groups of said celluiosic fibers ofthe pulp sheet with said carboxylic functional group of said alkene to form covalent linkages to form intermediate celluiosic fibers.

Inventors: RUTH JIMMIE ED JR, SMITH DAVID JAY, RUTH, JIMMIE, ED, JR., SMITH, DAVID, JAY
Applicants: PROCTER & GAMBLE, THE PROCTER & GAMBLE COMPANY
Application year: 1997
Main classification: D06M11
IPC codes: A47K7, C08B3, D06M11, D06M13, D21C9, D21H11, D21H21