Initiator composition for polymerising unsaturated monomers

Abstract: The description relates to an initiator composition for polymerising unsaturated monomers, containing a mixture component (A) of i) at least one salt of a metal in the second sub-group of the periodic system, optionally in solution in an aromatic solvent or in an α,β-unsaturated ester, and ii) at least one salt of a metal in the seventh or eighth sub-group of the periodic system, optionally in solution in an aromatic solvent or in an α,β-unsaturated ester, and at least one organic peroxy ester (component B) wherein the components (A) and (B) are spatially adjacent to one another. The description also relates to polymerisable compositions comprising the said initiator composition together with polymerisable unsaturated monomers. The initiator composition according to the invention can be used to homopolymerise and copolymerise all kinds of unsaturated monomers, such as methacrylic and acrylic acid esters, at lower temperatures.

Description: In Industry, unsaturated monomers, preferably methacrylic or acrylic acid esters, styrene and mixtures thereof, are mainly polymerised with initiators which decompose on heating into free radicals which subsequently react with a respective monomer molecule and trigger radical chain polymerisation. The initiators are azo compounds such as azo diisobutyrodinitrile (AIBN), peroxy esters and diacyl peroxides such as dibenzoyl peroxide. The polymerisation temperatures depend on the decomposition constants of the initiators. Usually a temperature of at least 60 to 70°C is required. Since atmospheric oxygen reacts as a diradical with initiator radicals and growing polymer radicals and thus reduces the molecular weight of the polymers, polymerisation using thermally activatable initiators must usually be carried out under oxygen-free conditions, e.g. in a protective gas atmosphere. Homopolymerisation and copolymerisation of unsaturated monomers can be effected in the substance or in organic solvents or in aqueous emulsion or dispersion. Emulsion polymerisation can also be carried out at 0 to 50°C, preferably at room temperature, if "redox initiators" are used. Initiating radicals are formed preferably by reduction of peroxy compounds such as H 2 0 2 , hydroperoxides or diacyl peroxides with oxidising agents such as salts of transition metals, preferably salts of Fe 2+ , Co 2+ , Ti 3+ , tertiary amines such as N,N-dimethylaniline, dimethylaminotoluidine or N,N-dimethylbenzylamine, sulphites such as NaHSO 3 , sugars or ascorbic acid. Since the redox components are usually only soluble in water and radical formation also depends on the pH, their use is restricted mainly to aqueous systems. Individual redox pairs such as Co 2+ -carboxylate/hydroperoxide or diacyl peroxide/N,N-dimethylbenzylamine, are also suitable for crosslinking styrene solutions of unsaturated polymers containing fumarate and maleate groups at room temperature, and are used e.g. in the production of materials for jointless flooring. One disadvantage of these redox systems, however, is their sensitivity to oxygen, which increases the time taken by the surface to harden. This inhibition by oxygen can be partly prevented by addition of waxes, which float on the surface and thus form a barrier. Redox initiators of this kind can admittedly also be used for polymerisation and crosslinking of acrylates and methacrylates, but in that case the polymerisation or crosslinking are slower and less complete. Problems are caused both by inhibition by oxygen and by discoloration of the products. Also, individual redox components such as diacyl peroxides dissolve preferably in aromatic hydrocarbons such as styrene, and are difficult to dissolve in other monomers such as unsaturated esters. Another possible method of room-temperature polymerisation or crosslinking is photopolymerisation. In this case the unsaturated monomers are mixed with radical initiators which have to be illuminated with UV before decomposing into polymerisation-initiating radicals. Photopolymerisation is also inhibited by oxygen. Crosslinking of "alkyd" resins, made up of mono- or polyunsaturated fatty acids, polyols and cyclic anhydrides, is the only process which occurs in the presence of atmospheric oxygen even at room temperature. To this end, these lacquers are mixed with transition metal carboxylates, preferably Co 2+ , Zn 2+ , Mn 2+ , Pb 2+ stearates or naphthenates, either singly or mixed in concentrations of 0.1 to 2 wt.%. Atmospheric oxygen causes hydroperoxides and peroxides to form on carbon atoms in the α-position relative to the double bonds of the unsaturated fatty-acid esters, and reacting in the presence of transition metal ions in a number of reactions involving crosslinking. A brief description of this so-called oxidative drying is given in Resins for Surface Coatings, Volume 1 (Ed. P. Oldring, G. Hayward), pages 52 ff (SITA Technology, London, 1987). However, this room-temperature crosslinking process in air is not a case of radical or ionic chain polymerisation via double bonds. The invention is based on the object of providing an initiator composition which homopolymerises and copolymerises all kinds of unsaturated monomers, including methacrylic and acrylic acid esters, at low temperatures, preferably 0 to 70°C, and particularly preferably at room temperature under aerobic conditions to form high-molecular products. Another aim is to crosslink polyfunctional derivatives under the specified conditions. An initiator composition of this kind can be used e.g. to produce styrene-free jointless flooring, polymethyl methacrylate boards and moulded parts by casting, resilient joints, lacquers which crosslink at room temperatures, or curing of adhesives. Tests with the redox systems used for crosslinking unsaturated polyesters have shown that individual components such as dibenzoyl peroxide are difficult to dissolve in unsaturated esters and that polymerisation or crosslinking occur very slowly, taking several days, and the molecular weights resulting from homopolymerisation are very low. It has now unexpectedly been found that mixtures containing one or more organic peroxy esters and combinations of salts of a divalent transition metal in the second sub-group and a metal in the seventh or eighth sub-group can polymerise α,β-unsaturated monoesters such as methacrylic or acrylic acid esters and vinylesters at temperatures of 0 to 70°C, particularly advantageously at room temperature, in the presence of atmospheric oxygen. On the other hand mixtures of peroxy esters and a divalent transition metal salt from one of the said sub-groups are incapable of triggering polymerisation of α,β-unsaturated monomers in the stated temperature range. The invention therefore provides an initiator composition for polymerising unsaturated monomers, comprising a mixture component (A) of i) at least one salt of a metal in the second sub-group of the periodic system, optionally in solution in an aromatic solvent or in an α,β-unsaturated ester, and ii) at least one salt of a metal in the seventh or eighth sub-group of the periodic system, optionally in solution in an aromatic solvent or in an α,β-unsaturated ester, and at least one organic peroxy ester component (B) wherein the components (A) and (B) are spatially adjacent to one another. One essential component of the initiator composition according to the invention (component A) is a mixture of i) at least one salt of a metal in the second sub-group of the periodic system and ii) at least one salt of a metal in the seventh or eighth sub-group of the periodic system. The salts of a metal in the second sub-group of the periodic system can e.g. be salts of zinc, cadmium or mercury, zinc salts being preferred. Although other salts such as fluorides, chlorides or bromides can be used, the preferred metal salts are carboxylates. The following are examples of suitable carboxylates of divalent metals in the second sub-group: acetates, propionates, butyrates, isobutyrates, 4-cyclohexyl butyrates, 2-ethyl hexanoates (octoates), neodecanoates, stearates and naphthenates, zinc carboxylates being preferred. For health at work, Zn 2+ octoate and naphthenate are particularly preferred. Zn 2+ octoate is a specially preferred salt of the metal in the second sub-group. The salts of the metal in the seventh or eighth sub-group in the periodic system can be salts of cobalt, manganese, iron, nickel or palladium, cobalt and manganese salts being preferred. As before, the carboxylates of the said metals are the preferred metal salts. The following are examples of suitable carboxylates of divalent metals in the seventh or eighth sub-group: acetates, propionates, butyrates, isobutyrates, 4-cyclohexyl butyrates, 2-ethyl hexanoates (octoates), neodecanoates or stearates, cobalt and manganese carboxylates being preferred. Co 2+ and Mn 2+ octoate and naphthenate are particularly preferred. Co 2+ and Mn 2+ octoate are the first choice. The naphthenates are mixtures of polycyclic aromatic carboxylic acids occurring in tar processing. These transition metal carboxylates can be used in solid form or as commercial solutions in aromatic solvents. The content of active substance, i.e. metal carboxylate, in these solutions is between 25 and 70 wt.%. It is advantageous to use solutions with the maximum content of active substance, in order to keep the content of aromatic solvent at a minimum. The second essential component (B) of the initiator composition according to the invention is an organic peroxy ester. The following are examples of suitable peroxy esters: liquid peroxy esters of straight-chain and branched aliphatic, cycloaliphatic and aromatic peroxy carboxylic acids with tertiary alcohols. According to the invention the component (B) can contain one or more organic peroxy esters. The peroxy esters used according to the invention are usually commercial initiators for heat-activated radical polymerisation. The following are examples: tert. butyl peroxybenzoate, tert. butylperoxy acetate, tert. butylperoxy isobutyrate, tert. butylperoxy diethyl acetate, tert. butylperoxy-3,5,5-trimethyl hexanoate, tert. butylperoxy pivalate, tert. amyl peroxy pivalate, ethyl-3,3-bis(tert.butylperoxy butyrate) and di-tert. butylperoxy tetrahydrophthalate. Preference is given, if only for safety reasons, to those peroxy esters whose 10-hour half-life temperature is above 90°C and which are stored at 20 to 30°C. Tert. butyl peroxybenzoate is particularly preferred since this peroxy ester, like all peroxy esters of aromatic carboxylic acids, is more active at room temperature than the corresponding esters of aliphatic carboxylic acids in the initiator composition according to the invention. In the initiator composition according to the invention, the components (A) and (B) are spatially separate from one another, i.e. in the form of a "kit of parts". In the kit, the molar ratio of active substance (component A) to component (B) is 0.1 to 4, preferably 0.4 to 1. In principle the molar proportions of the three components can vary within wide limits. In each case, the respective molar proportions determine the speed of polymerisation and crosslinking. For rapid, complete polymerisation and crosslinking, the most favourable molar proportion is about 1.2 mol Zn 2+ /1.0 mol Co 2+ /10 mol peroxy ester. The Co 2+ carboxylate may also be replaced by equal quantities of Mn 2+ carboxylate. The initiator composition according to the invention can advantageously be used for homo- and copolymerisation of unsaturated monomers. The invention therefore also relates to a polymerisable composition comprising a first component in the form of a mixture of i) at least one polymerisable unsaturated monomer, preferably an α,β-unsaturated ester ii) at least one salt of a metal in the second sub-group of the periodic system and iii) at least one salt of a metal in the seventh or eighth sub-group of the periodic system and a second component in the form of an organic peroxy ester, the first component and the second component being spatially adjacent to one another. The polymerisable composition according to the invention contains the previously described initiator composition in a total proportion of 0.05 to 5 wt.%, preferably 0.2 to 3 wt.% active substance relative to the monomer or monomers for polymerising. Polymerisation of monofunctional monomers can advantageously be carried out in the substance or in polar solvents, the individual components of the initiator composition according to the invention being added to the monomer for polymerisation in the following sequence: metal salt in the second sub-group, particularly preferably the Zn 2+ salt, metal salt in the seventh or eighth sub-group, particularly preferably the Co 2+ salt or Mn 2+ salt, and peroxy ester. It is not necessary for the monomers or solutions thereof to be covered by an inert protective gas such as nitrogen or argon before or during polymerisation. The polymerisation temperature can be 0 to 70°C, preferably 20 to 40°C, the speed of polymerisation increasing with increasing temperature. The resulting polymers have molecular weights of 10 4 to 10 5 g/mol. The following are examples of suitable monomers for polymerisation with the initiator composition according to the invention at temperatures between 0 and 70°C: methacrylic and acrylic acid esters such as methyl, ethyl, n-, iso, sec, or tert. butyl methacrylate, 2-ethylhexyl, dodecyl, tridecyl or stearyl methacrylate, or the acrylates corresponding to these monomers or methacrylic and acrylic acid esters containing different aliphatic alcohol radicals from those mentioned, e.g. containing polyether, cycloaliphatic, fluoroalkylated, poly(dimethyl siloxane) or aromatic radicals. Vinylesters such as vinyl acetate, vinyl pivalate, vinyl neononanoate, vinyl neodecanoate, vinyl laurate, vinyl stearate or vinyl benzoate are also suitable. The molecular weights obtainable on polymerisation at room temperature in air are high and are in the range of values obtained during heat-activated radical chain polymerisation. For example the average number and weight average weights of a methyl methacrylate polymerised in the substance at room temperature by 2.9 wt.% of the initiator composition according to the invention, after 24 hours, were M N = 170,000 and M W = 510,000 g/mol, with a polymer yield of 89%. Polymerisation in polar solvents such as N,N-dimethylformamide (DMF), dimethylsulphoxide (DMSO), esters or ethers such as dioxane yielded similarly high molecular weights. On the other hand less polar solvents such as benzene, toluene or xylene mixtures are unsuitable as solvents, since no polymers form in them, even at high monomer concentrations of over 50 wt.%. On the other hand α,β-unsaturated diesters such as the dialkyl esters of maleic and fumaric acid, vinylethers and vinyl aromatics are unsuitable for homopolymerisation with the initiator composition according to the invention. On the other hand, using the initiator composition according to the invention, the α,β-unsaturated esters in the group comprising acrylic acid, methacrylic acid and vinylester can be copolymerised both with one another and with the previously mentioned α,β-unsaturated diesters, resulting in copolymers which have not hitherto been obtainable industrially. According to the invention, therefore, on the one hand acrylic acid and methacrylic acid esters containing different alcohol radicals in the ester group can be copolymerised. On the other hand according to the invention these acrylic acid and methacrylic acid esters can also be copolymerised with vinylesters, vinylethers, maleic acid and fumaric acid diesters and with styrene. A precondition for copolymerisation with the initiator compound according to the invention is the presence of an α,β-unsaturated ester component in the comonomer mixture. The proportion of α,β-unsaturated esters in the group comprising acrylic acid, methacrylic acid or vinylester can for example be 5 to 99 mol.%. Another possibility is copolymerisation of vinylesters with vinylethers, maleic acid and fumaric acid esters and also with styrene. The content of vinylesters can be varied from 10 to 99, preferably 40 to 90 mol.%. The non-homopolymerisable maleic acid and fumaric acid diesters, when acted upon by the initiator composition according to the invention, can also copolymerise with methacrylates, acrylates, vinylethers, and vinyl aromatics, the proportion thereof in the comonomer mixture for copolymerisation being 25 to 75 mol.%, preferably 40 to 60 mol.%. The following are examples of copolymerisable maleic acid and fumaric acid diesters: dimethyl maleate, diethyl maleate, di-n-butyl maleate, di-tert.butyl maleate, dicyclohexyl maleate and the corresponding fumarates. The vinylethers can e.g. be methylvinylether, ethylvinylether, n-butylvinylether or isobutylvinylether. Styrene, vinyl toluene or 4-tert.butyl styrene are examples of suitable vinyl aromatics. The initiator composition according to the invention is also capable of crosslinking polyfunctional methacrylates and acrylates, either individually or in the form of a mixture of a number of polyfunctional unsaturated esters or a mixture with monofunctional methacrylic acid or acrylic acid esters in the temperature range from 0 to 70°C, particularly advantageously at room temperature, in a time of a few minutes to 24 hours in air. The composition can also harden mono- or polyfunctional methacrylates or acrylates in mixtures containing maleates or fumarates, vinylesters or mono-and polyfunctional vinylethers in the stated temperature range in air. It is also possible to add 0.1 to 30 wt.% of styrene or other vinyl aromatics. The crosslinking time depends on the total concentration of the initiator composition according to the invention in the crosslinkable mixture, and depends on the crosslinking temperature, which can be between 0 and 70°C. The nature and composition of the mono- and polyfunctional monomers and oligomers are variable over a wide range. By this means, thin lacquer coatings or thick boards or cast parts can be hardened in air at room temperature within a short time, completely and with a non-sticky surface. The individual layers can e.g. have a thickness of 0.1 mm to 20 cm, preferably 1 mm to 5 cm. The polymerisable compositions according to the invention as defined hereinbefore are crosslinking mixtures. The following are suitable monomer components of these crosslinking mixtures: the previously mentioned methacrylic acid and acrylic acid esters, vinylesters such as vinyl acetate, vinyl pivalate, vinyl neononanoate, vinyl neodecanoate, vinyl laurate, vinyl stearate or vinyl benzoate, and monofunctional vinylethers such as methylvinylether, ethylvinylether, n-butylvinylether or isobutylvinylether, and the previously mentioned maleic acid and fumaric acid diesters. Styrene, vinyl toluene or 4-tert.butyl styrene are examples of suitable vinyl aromatics. The following are examples of suitable polyfunctional acrylates and methacrylates: the acrylic and methacrylic acid esters of ethylene glycol, propylene glycol-1,2 and -1,3, butanediol-1,3 and -1,4, hexanediol-1,6, trimethylol propane, pentaerythritol, or OH-terminal polyethers such as polyethylene glycol, polypropylene glycol or polyetramethylene glycol. Also suitable are the reaction products of hydroxyalkyl acrylates and methacrylates with di- and polyglycidyl ethers, dicarboxylic acids, oligoesters and polyesters, di- and triisocyanates and isocyanate-functional polyurethane prepolymers and reaction products of acrylic and methacrylic acid with di- and polyglycidyl ethers. Products of this kind are commercially available in large quantities and are used inter alia in lacquers which set when illuminated. The polyfunctional vinylethers can e.g. be diethyleneglycol divinylether, triethyleneglycol divinylether, cyclohexane dimethanol-1,4-divinylether or trimethylolpropane trivinylether. The polymerisable compositions according to the invention, which depending on their formulation are self crosslinking mixtures or mixtures which crosslink when a suitable crosslinking agent is added, are produced by conventional methods in the polymer industry, such as solution, agitation or dispersion, optionally with addition of inactive adjuvants and aggregates. Immediately before crosslinking, the individual components of the initiator composition according to the invention are introduced in the following sequence: salt of the metal in the second sub-group of the periodic system, salt of the metal in the seventh or eighth sub-group of the periodic system and peroxy ester, the proportions by weight of active substance being for example 0.01 to 2 wt.% salt of the metal in the second sub-group of the periodic system, preferably the Zn 2+ salt, 0.01 to 2 wt.% of the salt of the metal in the seventh or eighth sub-group of the periodic system, preferably Co 2+ and/or Mn 2+ salt and 0.02 to 4 wt.% of peroxy ester relative to the monomer or monomers for crosslinking. Octoates of the said divalent metal, and a peroxy ester in the form of tert. butyl peroxybenzoate are particularly preferred for crosslinking the polyfunctional acrylate and methacrylate mixtures. Advantageously the metal salt solutions can be added during production of the mixtures for crosslinking, which will therefore be stable in storage for a longer period. In that case the peroxy ester will be added immediately before processing. The mixtures are then applied by suitable methods in the form of a film or poured into suitable moulds for producing boards and moulded members and hardened at temperatures in the range from 0 to 70°C, preferably at room temperature. Only 12 hours after beginning of the crosslinking at room temperature, the conversion rate of crosslinked monomers is more than 93%. Brief heating to temperatures of 40°C immediately after gelling ensures substantially quantitative conversion and immediately yields scratch-resistant surfaces. Even thick layers can be crosslinked without a protective gas atmosphere and within a few minutes, so that in practical applications it is often necessary to prolong the gel time of these mixtures containing the initiator composition according to the invention to obtain processing times of practical use, i.e. from 15 to 60 minutes. The prolongation can be obtained e.g. by reducing the content of the salt of the metal in the second sub-group to 10 to 30 mol.% of the content of the salt of the metal in the seventh or eighth sub-group. For example if the molar ratio of the salt of the metal in the second sub-group to the salt of the metal in the seventh or eighth sub-group, e.g. the molar ratio of Zn 2+ /Co 2+ , is reduced from 0.4/1 to 0.2/1, the crosslinking time of diethyleneglycol dimethacrylate at room temperature will be prolonged from 2 to 80 minutes. If the salt of the metal in the seventh or eighth sub-group is a cobalt salt, the proportion by weight of the Co salt solution containing 6 wt.% Co 2+ , together with the peroxyester in the mixture for crosslinking, will be a total of 1.5 wt.%. The invention therefore also provides use of the previously described polymerisable composition for producing acrylic glass parts, moulded members, coatings, jointless flooring, repair lacquer coatings, priming coats, patching compounds, putty, fillers and adhesives. Finally the invention also relates to a method of polymerising unsaturated monomers, preferably α,β-unsaturated esters, at a temperature of 0 to 70°C, characterised in that the previously described initiator composition is used as the polymerisation initiator. As the preceding shows, by comparison with conventional redox-based initiator systems active at room temperature or photoinitiators, the initiator composition according to the invention has considerable industrial advantages, since comparable amounts of initiator can rapidly polymerise and crosslink methacrylates and acrylates at low temperatures, particularly advantageously at room temperature, and polymerisation and crosslinking are not inhibited by atmospheric oxygen. Consequently polymerisation can be carried out without a protective gas atmosphere or wax, over a large area in ambient air. Uniform polymerisation throughout the layer is particularly advantageous, when the surfaces exposed to air become adhesive-free and firm more quickly than with conventional initiator systems. In contrast to photopolymerisation and crosslinking, the layer can be given any desired thickness, and no additional energy in the form of UV light is required. The components of the initiator composition are characterised by high stability and easy accessibility. For example the particularly preferred tert.butyl peroxybenzoates can be stored at room temperature without cooling, which is not the case with ketone hydroperoxides, which are preferred for rapid crosslinking of unsaturated polyesters at room temperature. As a result of the advantages as described, the initiator composition according to the invention has many possible applications. For example it can be used to make acrylic glass parts very quickly, continuously, and with large dimensions without complicated gas-atmosphere or temperature-control devices. Moulded members, even with thick walls, can be cast in open moulds. More particularly the novel initiator composition can be used to produce mechanically high-quality coatings which crosslink quickly at room temperature, using mono or polyfunctional methacrylates, vinylesters, vinylethers and maleic acid or fumaric acid dialkylesters, which have low toxicity and often have little odour. Possible applications inter alia are to jointless flooring, repair lacquer coatings, primer coats, patching compounds, putty, fillers and adhesives. The examples illustrate the invention. Use of the initiator composition according to the invention for polymerisation and crosslinking of acrylates and methacrylates is described in particular. Example 1 0.03 g Zn 2+ -2-ethyl hexanoate (Zn octoate) solution (Zn concentration 12% in xylene), 0.05 g Co 2+ -2-ethyl hexanoate (Co octoate) solution (Co concentration 6% in xylene) and 0.1 g tert. butyl peroxybenzoate were successively added in a 10 ml specimen glass containing 5 g methyl methacrylate and thoroughly mixed. The mixture was left to stand in the open glass at room temperature. After 24 hours the solid polymer was dissolved in 30 ml acetone and precipitated from methanol. The yield of polymethyl methacrylate after drying for 12 hours in vacuo was 92.4%. Molecular weights: Mn = 94,400 g/mol, Mw = 555,600 g/mol. Example 2 A methyl methacrylate/initiator mixture as per Example 1 was left to stand at +3°C in an open glass in a refrigerator for 24 hours. The viscous polymer solution was then precipitated in methanol. The yield of polymethyl methacrylate after drying for 12 hours in vacuo was 16.7%. Molecular weights: Mn = 29,540 g/mol, Mw = 42,870 g/mol. Example 3 A methyl methacrylate/initiator mixture as per Example 1 was heated in air for 24 hours in a 25 ml round-bottom flask with reflux condenser at 70°C. The solid polymer was then dissolved in 30 ml acetone and precipitated from methanol. The yield of polymethyl methacrylate after drying for 12 hours in vacuo was 93.2%. Molecular weights: Mn = 16,000 g/mol, Mw = 49,900 g/mol. Example 4 0.02 g Zn octoate solution (Zn concentration 12% in xylene), 0.04 g Co octoate solution (Co concentration 6% in xylene) and 0.1 g tert. butyl peroxybenzoate were successively added in a 10 ml specimen glass containing 5g n-butyl acrylate and thoroughly mixed. The mixture was then left to stand in the open glass at room temperature. After 24 hours the highly viscous polymer was dissolved in 40 ml tetrahydrofuran and precipitated from methanol. The yield of poly-(n-butyl acrylate) after drying for 12 hours in vacuo was 91%. Molecular weights: Mn = 94,000 g/mol, Mw = 663,200 g/mol. Example 5 0.05 g Zn octoate solution (Zn concentration 12% in xylene), 0.05 g Co octoate solution (Co concentration 6% in xylene) and 0.1 g tert.butyl peroxybenzoate were successively added in a 10 ml specimen glass containing 5g vinyl acetate and thoroughly mixed. The mixture was then left to stand in the open glass at room temperature. After 24 hours the highly viscous polymer was dissolved in 20 ml tetrahydrofuran and precipitated from water. The yield of polyvinyl acetate after drying for 12 hours in vacuo was 76%. Molecular weights: Mn = 70,000 g/mol, Mw = 250,000 g/mol. Example 6 0.05 g Zn octoate solution (Zn concentration 12% in xylene), 0.05 g Co octoate solution (Co concentration 6% in xylene) and 0.1 g tert. butyl peroxybenzoate were successively added in a 10 ml specimen glass containg 5g styrene and thoroughly mixed. The mixture was then left to stand in the open glass at room temperature. After 24 hours the liquid mixture was dissolved in 20 ml tetrahydrofuran and precipitated from methanol. Only about 120 mg of a colourless oil precipitated, and was shown by gel-permeation chromatography against polystyrene standard to consist of styrene oligomers with molecular weights between 200 and 600 g/mol. Example 7 0.50 g Zn octoate solution (Zn concentration 8% in xylene), 0.60 g Co octoate solution (Co concentration 6% in xylene) and 1 g tert. butyl peroxybenzoate were added with agitation to a mixture of 50 g dimethylformamide and 50 g methyl methacrylate in a 250 ml round-bottom flask with magnetic rod agitator and then agitated in air at room temperature. After 48 hours the polymer was precipitated from methanol. The yield of polymethyl methacrylate after drying for 24 hours in vacuo was 85%. Molecular weights: Mn = 67,000 g/mol, Mw = 283,000 g/mol. Example 8 0.50 g Zn octoate solution (Zn concentration 8% in xylene), 0.50 g Mn 2+ octoate solution (Mn concentration 6% in xylene) and 1 g tert. butyl peroxybenzoate were successively added to a mixture of 50 g dimethylformamide and 50 g n-butyl acrylate in a 250 ml round-bottom flask with magnetic rod agitator and agitated at room temperature in air. After 48 hours the polymer was precipitated from methanol. The yield of poly-(n-butyl acrylate) after drying for 24 hours in vacuo was 92%. Molecular weights: Mn = 223,400 g/mol, Mw = 630,000 g/mol. Example 9 0.09 g Zn octoate solution (Zn concentration 12% in xylene), 0.15 g Co octoate solution (Co concentration 6% in xylene) and 0.3 g tert. butyl peroxybenzoate were successively added in a 20 ml specimen glass containing 7.4 g (0.074 mol) methyl methacrylate and 7.6 g (0.073 mol) styrene and thoroughly mixed. The mixture was then heat-treated at 50°C in the open glass. After 24 hours the viscous resin was dissolved in 30 ml acetone and precipitated from methanol. The yield of copolymer after drying for 12 hours in vacuo was 31.8%. Molecular weights: Mn = 7,100 g/mol, Mw = 144,400 g/mol. The composition of the polymer determined by NMR spectroscopy was 0.7 mol methyl methacrylate/1 mol styrene. Example 10 0.03 g Zn octoate solution (Zn concentration 12% in xylene), 0.05 g Co octoate solution (Co concentration 6% in xylene) and 0.1 g tert. butyl peroxybenzoate were successively added in a 20 ml specimen glass containing 2.2 g (0.022 mol) methyl methacrylate and 2.8 g (0.022 mol) n-butyl acrylate and thoroughly mixed. The mixture was then heat-treated at 50°C in the open glass. After 24 hours the viscous resin was dissolved in 30 ml acetone and precipitated from methanol. The yield of copolymer after drying for 12 hours in vacuo was 88.1%. Molecular weights: Mn = 95,300 g/mol, Mw = 338,300 g/mol. The composition of the polymer, determined by NMR spectroscopy, was 1.27 mol methyl methacrylate/1 mol n-butyl acrylate. Example 11 0.05 g Zn octoate solution (Zn concentration 8% in xylene), 0.05 g Co octoate solution (Co concentration 6% in xylene) and 0.1 g tert.butyl peroxybenzoate were successively added with agitation to a 50 ml round-bottom flask with magnetic rod agitator and containing a mixture of 4 g dimethylformamide, 2.5 g (0.025 mol) methyl methacrylate and 2.7 g (0.026 mol) styrene and then agitated at room temperature in air. After 48 hours the polymer was precipitated from methanol. The yield of copolymer after drying for 24 hours in vacuo was 56%. Molecular weights: Mn = 115,400 g/mol, Mw = 234,300 g/mol. The composition of the polymer determined by NMR spectroscopy was 0.7 mol methyl methacrylate/1 mol styrene. Example 12 0.6 g Zn octoate solution (Zn concentration 8% in xylene), 0.6 g Co octoate solution (Co concentration 6% in xylene) and 1.2 g tert. butyl peroxybenzoate were successively added with agitation to a 100 ml round-bottom flask with magnetic rod agitator and containing a mixture of 40 g dimethylformamide, 32 g (0.25 mol) n-butyl acrylate and 27 g (0.26 mol) styrene and agitated at room temperature in air. After 48 hours the polymer was precipitated from methanol. The yield of copolymer after drying for 24 hours in vacuo was 84%. Molecular weights: Mn = 174,500 g/mol, Mw = 382,000 g/mol. The composition determined by NMR spectroscopy of the polymer was 0.7 mol n-butyl acrylate/1 mol styrene. Example 13 0.03 g Zn octoate solution (Zn concentration 12% in xylene), 0.05 g Co octoate solution (Co concentration 6% in xylene) and 0.1 g tert. butyl peroxybenzoate were successively added in a 20 ml specimen glass containing 3.3 g (0.025 mol) butyl methacrylate and 1.7 g (0.025 mol) ethylvinylether and thoroughly mixed. The mixture was left to stand in the open glass at room temperature. After 24 hours the viscous resin was dissolved in 30 ml acetone and precipitated from a methanol/water mixture (1 : 1). The yield of copolymer after drying for 12 hours in vacuo was 38.6%. Molecular weights: Mn = 20,100 m/mol, Mw = 46,400 g/mol. The composition of the polymer determined by NMR spectroscopy was 8.62 mol butyl methacrylate/1 mol ethylvinylether. Example 14 0.03 g Zn octoate solution (Zn concentration 12% in xylene), 0.05 g Co octoate solution (Co concentration 6% in xylene) and 0.1 g tert. butyl peroxybenzoate were successively added and thoroughly mixed in a 20 ml specimen glass containing 3.2 g (0.025 mol) butyl acrylate and 1.8 g (0.025 mol) ethylvinylether. The mixture was left to stand in the open glass at room temperature. After 24 hours the viscous resin was dissolved in 30 ml tetrahydrofuran and precipitated from a methanol/water mixture (1 : 1). The yield of copolymer after drying for 12 hours in vacuo was 67.3%. Molecular weights: Mn = 54,800 g/mol, Mw = 114,000 g/mol. The composition of the polymer determined by NMR spectroscopy was 4.15 mol butyl acrylate/1 mol ethylvinylether. Example 15 0.03 g Zn octoate solution (Zn concentration 12% in xylene), 0.05 g Co octoate solution (Co concentration 6% in xylene) and 0.1 g tert. butyl peroxybenzoate were successively added and thoroughly mixed in a 20-ml specimen glass containing 1.0 g (0.008 mol) butyl acrylate and 4.0 g (0.023 mol) diethyl maleate. The mixture was left to stand in the open glass at room temperature. After 24 hours the viscous resin was dissolved in 30 ml tetrahydrofuran and precipitated from a methanol/water mixture (1 : 1). The yield of copolymer after drying for 12 hours in vacuo was 37.4%. Molecular weights: Mn = 56,800 g/mol, Mw = 321,600 g/mol. The composition determined by NMR spectroscopy of the polymer was 8.1 mol butyl acrylate/1 mol diethyl maleate. Example 16 0.03 g Zn octoate solution (Zn concentration 12% in xylene), 0.05 g Co octoate solution (Co concentration 6% in xylene) and 0.1 g tert. butyl peroxybenzoate were successively added and thoroughly mixed in a 20 ml specimen glass containing 1.7 g (0.019 mol) vinyl acetate and 3.3 g (0.019 mol) diethyl maleate. The mixture was left to stand at room temperature in the open glass. After 24 hours the viscous resin was dissolved in 30 ml tetrahydrofuran and precipitated from a methanol/water mixture (1 : 1). The yield of copolymer after drying for 12 hours in vacuo was 53.8%. Molecular weights: Mn = 93,500 g/mol, Mw = 284,400 g/mol. The composition of the polymer determined by NMR spectroscopy was 1.09 mol diethyl maleate/1 mol vinyl acetate. Example 17 0.03 g Zn octoate solution (Zn concentration 12% in xylene), 0.05 g Co octoate solution (Co concentration 6% in xylene) and 0.1 g tert. butyl peroxybenzoate were added and thoroughly mixed in a 20 ml specimen glass containing 4.1 g (0.048) vinyl acetate and 0.9 g (0.005 mol) diethyl maleate. The mixture was left to stand in the open glass at room temperature. After 24 hours the viscous resin was dissolved in 30 ml tetrahydrofuran and precipitated from a methanol/water mixture (1 : 1). The yield of copolymer after drying for 12 hours in vacuo was 42.6%. Molecular weights: Mn = 70,700 g/mol, Mw = 257,400 g/mol. The composition of the polymer determined by NMR spectroscopy was 6.03 mol vinyl acetate/1 mol diethyl maleate. Example 18 0.04 g Cd 2+ -2-ethyl hexanoate (Cd octoate) solution (Cd concentration 8% in xylene), 0.05 g Co octoate solution (Co concentration 6% in xylene) and 0.1 g tert. butyl peroxybenzoate were successively added and thoroughly mixed in a 20 ml specimen glass containing 2.7 g (0.032 mol) vinyl acetate and 2.3 g (0.032 mol) ethylvinylether. The mixture was left to stand in the open glass at room temperature. After 24 hours the viscous resin was dissolved in 30 ml tetrahydrofuran and precipitated from a methanol/water mixture (1 : 1). The yield of copolymer after drying for 12 hours in vacuo was 37.3%. Molecular weights: Mn = 2,900 g/mol, Mw = 6,100 g/mol. The composition determined by NMR spectroscopy of the polymer was 2.93 mol vinyl acetate/1 mol ethylvinylether. Example 19 0.03 g Zn octoate solution (Zn concentration 12% in xylene), 0.05 g Co octoate solution (Co concentration 6% in xylene) and 0.1 g tert. butyl peroxybenzoate were successively added and thoroughly mixed in a 20 ml specimen glass containing 1.5 g (0.021 mol) ethylvinylether and 3.1 g (0.018 mol) diethyl maleate. The mixture was left to stand in the open glass at room temperature. After 24 hours the viscous resin was precipitated from a methanol/water mixture (1 : 1). The yield of copolymer after drying for 12 hours in vacuo was 49.8%. Molecular weights: Mn = 3,900 g/mol, Mw = 13,800 g/mol. The composition of the polymer determined by NMR spectroscopy was 1.63 mol diethyl maleate/1 mol ethylvinylether. Example 20 0.03 g Zn octoate solution (Zn concentration 12% in xylene), 0.05 g Co octoate solution (Co concentration 6% in xylene) and 0.1 g tert. butyl peroxybenzoate were successively added and thoroughly mixed in a 20 ml specimen glass containing 1.9 g (0.018 mol) styrene and 3.1 g (0.018 mol) diethyl maleate. The mixture was left to stand in the open glass at room temperature. After 24 hours the viscous resin was precipitated from a methanol/water mixture (1 : 1). The yield of copolymer after drying for 12 hours in vacuo was 25%. Molecular weights: Mn = 14,500 g/mol, Mw = 35,000 g/mol. The composition of the polymer determined by NMR spectroscopy was 11.7 mol styrene/1 mol diethyl maleate. Example 21 0.03 g Zn octoate solution (Zn concentration 12% in xylene), 0.05 g Co octoate solution (Co concentration 6% in xylene) and 0.1 g tert. butyl peroxybenzoate were successively added and thoroughly mixed in a 20 ml specimen glass containing 1.9 g (0.018 mol) styrene and 3.1 g (0.018 mol) diethyl fumarate. The mixture was then left to stand in the open glass at room temperature. After 24 hours the viscous resin was precipitated from a methanol/water mixture (1 : 1). The yield of copolymer after drying for 12 hours in vacuo was 57%. Molecular weights: Mn = 25,600 g/mol, Mw = 51,000 g/mol. The composition of the polymer, determined by NMR spectroscopy, was 1.25 mol styrene/1 mol diethyl fumarate. Example 22 0.03 g Zn octoate solution (Zn concentration 12% in xylene), 0.05 g Co octoate solution (Co concentration 6% in xylene) and 0.1 g tert. butyl peroxybenzoate were successively added and thoroughly mixed in a 20 ml specimen glass containing 1.7 g (0.019 mol) vinyl acetate and 3.3 g (0.019 mol) diethyl fumarate. The mixture was left to stand in the open glass at room temperature. After 24 hours the viscous resin was precipitated from a methanol/water mixture (1 : 1). The yield of copolymer after drying for 12 hours in vacuo was 59.7%. Molecular weights: Mn = 18,700 g/mol, Mw = 39,600 g/mol. The composition, determined by NMR spectroscopy, of the polymer, was 1.06 mol diethyl fumarate/1 mol vinyl acetate. Example 23 5 g diethyleneglycol dimethacrylate was poured into respective 10 ml specimen glasses and the following initiator components were successively added: a) 0.05 g Zn octoate (Zn concentration 8% in xylene), 0.1 g tert. butyl peroxybenzoate, b) 0.05 g Co octoate (Co concentration 6% in xylene), 0.1 g tert. butyl peroxybenzoate, c) 0.05 g Zn octoate (Zn concentration 8% in xylene), 0.05 g Co octoate (Co concentration 6% in xylene), 0.1 g tert. butyl peroxybenzoate, d) 0.05 g Zn octoate (Zn concentration 8% in xylene), 0.05 g Co octoate (Co concentration 6% in xylene), 0.1 g tert. butyl diethyl acetate, e) 0.05 g Zn octoate (Zn concentration 8% in xylene), 0.05 g Mn octoate (Mn concentration 6% in xylene), 0.1 g tert. butyl peroxybenzoate, f) 0.05 g Zn octoate (Zn concentration 8% in xylene), 0.05 g Co octoate (Co concentration 6% in xylene), 0.1 g tert. butyl hydroperoxide, g) 0.05 g Zn octoate (Zn concentration 8% in xylene), 0.05 g Co octoate (Co concentration 6% in xylene), 0.1 g di-tert. butyl peroxide, h) 0.05 g Zn octoate (Zn concentration 8% in xylene), 0.05 g Co octoate (Co concentration 6% in xylene), 0.2 g dibenzoyl peroxide. Mixtures a) - h) were thoroughly mixed, left to stand at room temperature, and the time until complete hardening throughout the layer (about 2 cm) was measured. This time was defined as the crosslinking time. The measured results are: a) > 24 h; b) > 24 h; c) 3 min 20 sec; d) 5 min 10 sec; e) 6 min 30 sec; f) > 24 h; g) no crosslinking after > 48 h; h) no crosslinking after > 48 h. Example 24 10 g diethyleneglycol dimethacrylate was poured into respective 20 ml specimen glasses and the following initiator components were successively added: a) 0.008 g Zn octoate (Zn concentration 12% in xylene), 0.009 g Co octoate (Co concentration 6% in xylene), 0.026 g tert. butyl peroxybenzoate, total amount: 0.35 wt.%; b) 0.0165 g Zn octoate (Zn concentration 12% in xylene), 0.009 g Co octoate (Co concentration 6% in xylene), 0.053 g tert. butyl peroxybenzoate, total amount 0.71 wt.%; c) 0.0245 g Zn octoate (Zn concentration 12% in xylene), 0.027 g Co octoate (Co concentration 6% in xylene), 0.078 g tert. butyl peroxybenzoate, total amount: 1.03 wt.%; d) 0.0338 g Zn octoate (Zn concentration 12% in xylene), 0.0372 g Co octoate (Co concentration 6% in xylene), 0.106 g tert. butyl peroxybenzoate, total amount 1.41 wt.%; e) 0.043 g Zn octoate (Zn concentration 12% in xylene), 0.048 g Co octoate (Co concentration 6% in xylene), 0.120 g tert. butyl peroxybenzoate, total amount: 1.7 wt.%. The thickness of the layers of mixture was about 5 cm. Mixtures a) - e) were examined as described in Example 23. The measured crosslinking times were: a) 80 min; b) 30 min 5 sec; c) 10 min 10 sec; d) 4 min 45 sec; e) 3 min 20 sec. 18 - 24 hours after crosslinking, gel fractions of the specimens were determined, by comminuting the polymer blocks and weighing 2 - 2.5 g exactly in a metal sieve in each case and storing for 24 hours in acetone. After drying in vacuo, the undissolved substance was again weighed. The difference from the weight before extraction with acetone constituted the gel fraction. This was always above 95% in a) - e). Example 25 Mixtures a) - c) in Example 24 were heat-treated at 50°C and the crosslinking time was measured. The crosslinking times were: a) 26 min 30 sec; b) 5 min 30 sec; c) 3 min. The gel fractions, as described in Example 24, were above 93% in all cases. Example 26 5 g respectively of the mixtures a) - e) in Example 24 were applied in 2 mm thick layers to aluminium plates and crosslinked at room temperature. The crosslinking times up to complete hardening were a) < 24 h; b) 2.5 h; c) 33 min; d) 7 min 15 sec; e) 4 min 5 sec. Example 27 5.2 g of a mixture consisting of 25 g diethyleneglycol dimethacrylate and 0.50 g Zn octoate solution (Zn concentration 8% in xylene) and 0.50 g Co octoate (Co concentration 6% in xylene) was poured into respective 10 ml specimen glasses and mixed in each case with 0.1 g tert. butyl peroxybenzoate. The crosslinking times were measured at various temperatures: a) 3°C: 7 min 30 sec; b) room temperature: (24°C): 3 min 40 sec; c) 40°C: 40 sec; d) 70°C: 10 sec. All gel fractions as per Example 24 were above 95%. Example 28 5 g diethyleneglycol dimethacrylate was poured into respective 10 ml specimen glasses, 0.05 g Co octoate (Co concentration 6% in xylene) was added in each case, and the substance was mixed with the following quantities of Zn octoate (Zn concentration 8% in xylene): a) 0.0076 g (0.076 wt.%); b) 0.0163 g (0.163 wt.%); c) 0.325 g (0.325 wt.%); d) 0.0494 g (0.494 wt.%); e) 0.0736 g (0.736 wt.%). 0.1 g tert. butyl peroxybenzoate was added to each mixture and the crosslinking times at room temperature were measured: a) 80 min; b) 5 min 30 sec; c) 2 min 35 sec; d) 1 min 47 sec; e) 50 sec. All the gel fractions as per Example 24 were above 95%. Example 29 10 g hexanediol-1,6-diacrylate was poured into respective 20 ml specimen glasses and the following initiator components were successively added: a) 0.0154 g Zn octoate (Zn concentration 12% in xylene), 0.019 g Co octoate (Co concentration 6% in xylene), 0.0437 g tert. butyl peroxybenzoate, total amount 0.17 wt.%; b) 0.0245 g Zn octoate (Zn concentration 12% in xylene), 0.029 g Co octoate (Co concentration 6% in xylene), 0.065 g tert. butyl peroxybenzoate, total amount: 0.27 wt.%; c) 0.0510 g Zn octoate (Zn concentration 12% in xylene), 0.0924 g Co octoate (Co concentration 6% xylene), 0.181 g tert. butyl peroxybenzoate, total amount: 0.70 wt.%; The height of each layer of mixture was about 5 cm. Mixtures a) - c) were crosslinked at room temperature as described in Example 23. The crosslinking times were: a) 4 min 30 sec; b) 2 min; c) 10 sec (very exothermic reaction). All gel fractions as per Example 24 were above 99%. Example 30 Mixtures as per Example 29b) were each heat-treated at 13°C and 50°C and the crosslinking times were measured as follows: a) 13°C: 4 min; b) 50°C: 1 min. All gel fractions as per Example 24 were above 99%. Example 31 A mixture of 2.4 g Zn octoate solution (Zn concentration 12% in xylene) and 2.0 g Co octoate (Co concentration 6% in xylene) was added to a solution of 50 g polymethyl methacrylate in 50 g diethyleneglycol dimethacrylate and 100 g methyl methacrylate. 4 g tert. butyl peroxybenzoate was stirred into the mixture and the viscous resin was poured into a metal mould 5 cm high sprayed before with an anti-adhesive substance. After 6 hours at room temperature the material had completely hardened, the surface was non-sticky and the block could be removed from the mould. The polymer block was sawn into 25 parts, and a gel fraction of each part was determined as described in Example 24. The gel fractions were all over 99%. Example 32 Various quantities of triethyleneglycol divinylether (TEGDVE) and diethyl maleate (DEM) were weighed in 10 ml specimen glasses, the total amount being 5 g in each case. The molar ratio of vinylether to maleate groups was varied between 2 : 1 and 1 : 2. A mixture of 0.05 g Zn octoate solution (Zn concentration 8% in xylene) and 0.05 g Co octoate (Co concentration 6% in xylene) was added to each mixture, which was mixed with 0.1 g tert. butyl peroxybenzoate in each case. The crosslinking times were measured at room temperature. a) 2.70 g TEGDVE, 2.30 g DEM (2 : 1 m/m); b) 2.34 g TEGDVE, 2.66 g DEM (1.5 : 1 m/m); c) 1.85 g TEGDVE, 3.15 g DEM (1 : 1 m/m); d) 1.54 g TEGDVE, 3.46 g DEM (1 : 1.33 m/m); e) 1.14 g TEGDVE, 3.86 g DEM (2 : 1 m/m). The measured crosslinking times up to complete hardening were: a) 1 min 5 sec; b) 1 min 15 sec; c) 1 min 25 sec; d) 2 min 10 sec; e) 4 min 45 sec). The gel fractions were over 95%. Example 33 Varying amounts of triethyleneglycol divinylether (TEGDVE) and diethyl fumarate (DEF) were weighed in 10 ml specimen glasses, the total quantity being 5 g in each case. The molar ratio of vinylether to maleate groups was varied between 2 : 1 and 1 : 2. A mixture of 0.05 g Zn octoate solution (Zn concentration 8% in xylene) and 0.05 g Co octoate (Co concentration 6% in xylene) was added to each mixture, which was mixed with 0.1 g tert. butyl peroxybenzoate in each case. The crosslinking times at room temperature were measured. a) 2.70 g TEGDVE, 2.30 g DEF (2 : 1 m/m); b) 2.34 g TEGDVE, 2.66 g DEF (1.5 : 1 m/m); c) 1.85 g TEGDVE, 3.15 g DEF (1 : 1 m/m); d) 1.54 g TEGDVE, 3.46 g DEF (1 : 1.33 m/m); e) 1.14 g TEGDVE, 3.86 g DEF (2 : 1 m/m). The measured crosslinking times up to complete hardening were: a) 5 min; b) 5 min 25 sec; c) 10 min 15 sec; d) 17 min 30 sec; e) 50 min 25 sec. The gel fractions were all over 93%. Example 34 A mixture of 1.85 g triethyleneglycol divinylether (TEGDVE) and 3.46 g diethyl maleate (DEM) was poured into respective 10 ml specimen glasses and the following initiator combinations were mixed therein: a) 0.02 g Zn octoate solution (Zn concentration 12% in xylene), 0.02 g Co octoate (Co concentration 6% in xylene), 0.04 tert. butyl peroxybenzoate; b) 0.02 g Co octoate (Co concentration 6% in xylene), 0.04 g methyl ethyl ketone peroxide; c) 0.02g Co octoate (Co concentration 6% in xylene), 0.04 g tert. butyl hydroperoxide; d) 0.02 g Co octoate (Co concentration 6% in xylene), 0.04 g cumene hydroperoxide; e) 0.01 g N,N-dimethyltoluidine-1,4, 0.08 g dibenzoyl peroxide (with 50% in dioctyl phthalate). The prepared mixtures in the specimen glasses had a layer thickness of about 2 cm. They were stored at room temperature and their crosslinking properties were observed immediately after mixing the initiator components and then after 10 minutes, 6 hours and 24 hours. a) Crosslinking time: 7 min, complete hardening; b) 10 min: liquid, 6 h: 1 cm liquid upper phase, 24 h: 0.2 cm liquid upper phase; c) 10 min, 6 h and 24 hours completely liquid; d) 10 min: liquid, 6 h: 1.6 cm liquid upper phase, 24 h: 0.4 cm liquid upper phase; e) 10 min: liquid, 6 h: 0.4 cm liquid upper phase, 24 h 0.2 cm liquid upper phase.

Claims: An initiator composition for polymerising unsaturated monomers, comprising a mixture component (A) of i) at least one salt of a metal in the second sub-group of the periodic system, optionally in solution in an aromatic solvent or in an α,β-unsaturated ester, and ii) at least one salt of a metal in the seventh or eighth sub-group of the periodic system, optionally in solution in an aromatic solvent or in an α,β-unsaturated ester, and at least one organic peroxy ester (component B) wherein the components (A) and (B) are spatially adjacent to one another. An initiator composition according to claim 1, characterised in that the salt of the metal in the second sub-group of the periodic system is a zinc salt. An initiator composition according to claim 1 or 2, characterised in that the salt of the metal in the seventh sub-group is a manganese salt. An initiator composition according to claim 1 or 2, characterised in that the salt of the metal in the eighth sub-group is a cobalt salt. An initiator composition according to any of claims 1 to 4, characterised in that the metal salt is a carboxylate. An initiator composition according to any of claims 1 to 4, characterised in that the metal salt is an octoate. An initiator composition according to any of the preceding claims, characterised in that the organic peroxy ester is tert. butyl peroxybenzoate. A polymerisable composition comprising a first component in the form of a mixture of i) at least one polymerisable unsaturated monomer, ii) at least one salt of a metal in the second sub-group of the periodic system and iii) at least one salt of a metal in the seventh or eighth sub-group of the periodic system and a second component in the form of an organic peroxy ester, the first component and the second component being spatially adjacent to one another. A polymerisable composition according to claim 8, characterised in that the salt of the metal in the second sub-group of the periodic system is a zinc salt. A polymerisable composition according to claim 8 or 9, characterised in that the salt of the metal in the seventh sub-group is a manganese salt. A polymerisable composition according to claim 8 or 9, characterised in that the salt of the metal in the eighth sub-group is a cobalt salt. A polymerisable composition according to claims 8 to 11, characterised in that the metal salt is a carboxylate. A polymerisable composition according to any of claims 8 to 11, characterised in that the metal salt is an octoate. A polymerisable composition according to claims 8 to 13, characterised in that the organic peroxy ester is tert. butyl peroxybenzoate. A polymerisable composition according to claims 8 to 14, characterised in that the polymerisable unsaturated monomer is at least one monomer from the group comprising the methacrylates, acrylates and vinylesters. Use of the polymerisable composition according to claims 8 to 15 for producing acrylic glass parts, moulded members, coatings, jointless flooring, repair lacquer coatings, primer coats, patching compounds, putty, fillers and adhesives. A method of polymerising unsaturated monomers at a temperature of 0 to 70°C, characterised in that the polymerisation initiator used is the initiator composition according to any of claims 1 to 7. A method according to claim 17, characterised in that i) first the salt of the metal in the second sub-group of the periodic system ii) and the salt of the metal of the seventh and eighth sub-group of the periodic system and iii) finally the organic peroxy ester is added to the unsaturated monomer. A method according to claim 17 or 18, characterised in that at least one polymerisable unsaturated monomer from the group comprising the methacrylates, acrylates and vinylesters is selected. A method according to claims 17 to 19, characterised in that the method is worked in air.

Inventors: FRINGS RAINER B, GRAHE GERWALD F, JAROSZEWSKI CAROLA, NONAKA SHIN-ICHI, FRINGS, RAINER B., GRAHE, GERWALD F., JAROSZEWSKI, CAROLA, NONAKA, SHIN-ICHI
Applicants: DAINIPPON INK & CHEMICALS, DAINIPPON INK AND CHEMICALS, INC.
Application year: 1997
Main classification: C08F4
IPC codes: C08F2, C08F18, C08F20, C08F4