ARTICLE COMPRISING FILM HAVING POLYAMIDE SEALANT, POLYAMIDE CORE LAYER, AND O2-BARRIER LAYER, AND PACKAGED PRODUCT USING SAME

Abstract: An article, such as a bag, pouch, or casing, is made from a multilayer film (10) which has: (a) a first layer (12), which is an outer film layer, comprising a polyamide having a melting point of from about 250 DEG F to 400 DEG F, the first layer (12) having a thickness of less than about 18 percent, based on a total thickness of the multilayer film; (b) a second layer (14) comprising at least one member selected from the group consisting of polyamide 6, polyamide 9, polyamide 10, polyamide 11, polyamide 12, polyamide 66, polyamide 610, polyamide 612, polyamide 6I, polyamide 6T, polyamide 69, and copolymers thereof, the second layer (14) having a thickness of from about 3 to 30 percent of the total thickness of the multilayer film; and (c) a third layer (16) which serves as an O2-barrier layer and comprises at least one member selected from the group consisting of ethylene/vinyl alcohol copolymer, polyvinylidene chloride, and polyalkylene carbonate. The first layer (12) of the film is sealed to itself. The article is suitable for use as a packaging film to be used for cook-in end use. The film provides the article with enhanced sealing and toughness properties. Also disclosed are a bag comprising this multilayer film, as well as a packaged product comprising this multilayer film.

Description: I ARTICLE COMPRISING FILM HAVTNG POLYAMIDE SEALANT, POLYAMIDE CORE LAYER, AND O BARRlER LAYER, AND PACKAGED PRODUCT USING SAME Field of the Invention The present invention relates to articles made from the conversion of multilayer films, and particularly to such articles which are suitable for packaging meat products, especially for the cook-in packaging of meat products wherein the film has a food contact surface which adheres to the meat during cook-in Background of the Invention For several years, the food packaging industry has utilized a packaging film from which bags and casings have been made which are of improved structural soundness such that they have been fully characterized as cook-in A precooked food product has been attractively packaged using a film within which the product was precooked The film has been used primarily for cook-and-ship end-use, wherein a meat product is packaged in the film and cooked while in the film, and is thereafter cooled and shipped to wholesaler, retailer, or consumer, without being overwrapped and without having the film stripped therefrom and thereafter being re-packaged in another film The phrase "cook-in" as used herein refers to the process of cooking a product packaged in a material capable of withstanding exposure to long and slow cooking conditions while containing the food product, for example cooking at 57°C to 12 I°C (i e, I °F-250°F) for 2-12 hours, preferably 57°C to 95°C {i.e, 135°F-203°F) for 2- 12 hours Cook-in packaged foods are essentially pre-packaged, pre-cooked foods which may be directly transferred to the consumer in this form These types of foods may be consumed with or without warming Cook-in packaging materials maintain seal integrity, i e , any heat sealed seams should resist being pulled apart during cook-in, and are conformable to the contained food product Preferably, conformability is achieved by the film being heat shrinkable so as to fonn a tightly fitting package Additional optional characteristics of films for use in cook-in applications include delamination-resistance, low O2-permeability, heat-shrinkability, and optical clarity Cook-in films preferably have a tendency for adhesion to the food product, thereby preventing "cook-out", i.e., "purge", which is the collection of juices between the outer surface of the food product and the meat-contact surface of the film, i e , the surface in direct contact with the meat This meat adhesion characteristic of the meat contact layer serves to both prevent cook-out (and thereby prevent an unattractive package or the need to strip the film from the meat and repackage the meat), to increase product yield, and to prevent the meat from losing juices which improve its edible character As used herein, the term "adhere", with respect to meat-adhesion, refers to a meat-contact surface of the film which bonds during cook-in to the contained food product to an extent sufficient to substantially prevent accumulation of fluids between the film and the contained meat product However, some of the cook-in films in commercial use have an outer layer which serves as a meat-adhesion layer, this layer containing a relatively large amount of one or more relatively expensive polyamides In one commercially available film, for example, this outer polyamide layer typically comprised a blend of polyamide 12 and polyamide 6/12, both of which are relatively expensive but which provide advantageous sealing and meat adhesion performance It has been believed that these polyamide polymers must be present in a relatively thick outer layer (e g , about 20% of the total film thickness), in order to provide the seal performance during cook-in, because the converted articles typically need to survive cooking for long periods of time at high temperatures, e g , cooking the meat product at 190°F for 6- 12 hours It would be desirable to reduce the cost of the film if the seal quality and meat-adhesion could be maintained, or at least not sacrificed to any significant degree Summary of the Invention In comparison with prior art commercially-available films, the article of the present invention utilizes a film which contains less costly polymer, while providing comparable performance characteristics, i e., comparable seal strength, comparable meat adhesion, and comparable package appearance Furthermore, in some cases this film can provide the further advantage of downgauging of the total film thickness, so that less total polymer is required. Furthermore, in some cases the film of the present invention can be used to provide an enhanced level of shrink tension In some cases, the film of the present invention can provide enhanced toughness/abuse resistance even though the thickness of the film is not increased over other films which have previously been used Surprisingly, the film of the present invention can provide comparable performance characteristics even if it has a thickness less than the cook-in films which have been in commercial use In addition, the film of the invention exhibits improved heat seal strength relative to prior art commercially- available films having, for example, ionomer meat contact layers The film of the present invention is suitable for the packaging of a wide vaπety of food products, especially meat products As a first aspect, the present invention is directed to an article comprising a multilayer film The multilayer film comprises (A) a first layer comprising a polyamide having a melting point of from about 250°F to 400°F, the first layer having a thickness of less than about 18 percent, based on a total thickness of the multilayer film, (B) a second layer comprising at least one member selected from the group consisting of polyamide 6, polyamide 9, polyamide 10, polyamide 1 1 , polyamide 12, polyamide 66, polyamide 610, polyamide 612, polyamide 61, polyamide 6T, polyamide 69, and copolymers thereof, the second layer having a thickness of from about 3 to 30 percent of the total thickness of the multilayer film, and, and (C) a third layer which serves as an O?-barπer layer and comprises at least one member selected from the group consisting of ethylene/vinyl alcohol copolymer, polyamide, polyviny dene chloride, and polyalkylene carbonate The first layer is sealed to itself Preferably, the first layer has a thickness of from about 0 5 to 1 percent of the total film thickness, more preferably, from about 5 to 18 percent, still more preferably, from about 6 to 15 percent, and, yet still more preferably, from about 8 to 12 percent Preferably, the polyamide in the first layer has a melting point of from about 300° to 375°F Preferably, the second layer has a thickness of from about 3 to 30 percent of the total film thickness, more preferably, from about 4 to 20 percent, still more preferably, from about 5 to 10 percent Preferably, the second layer is directly adhered to the first layer Preferably, the second layer comprises at least one member selected from the group consisting of polyamide 6, polyamide 66, and polyamide 6/66 In a first preferred embodiment, the first layer comprises only one polyamide In a second preferred embodiment, the first layer comprises copolyamide 6/12 in an amount of from about 20 to 80 weight percent, and polyamide 12 in an amount of from about 80 to 20 weight percent In either embodiment, the first layer preferably has a thickness of less than about 15 percent, based on a total thickness of the multilayer film In either embodiment, preferably the first layer has a thickness of from about 0 2 to 0 4 mil Preferably, the second layer comprises polyamide 6 and at least one member selected from the group consisting of polyamide 66, polyamide 610, polyamide 6/12, polyamide 61, polyamide 6T, polyamide 69, and copolyamides thereof More preferably, the second layer comprises polyamide 6 in an amount of from about 40 to 90 weight percent, and polyamide 6/12 in an amount of from about 10 to 60 weight percent Preferably, the thickness of the second layer is from about 3 to 20 percent, based on a total thickness of the multilayer film, more preferably, the thickness of the second layer is less than about 15 percent, based on a total thickness of the multilayer film Preferably, the multilayer film further comprises a fourth layer comprising at least one member selected from the group consisting of polyolefin, polyamide, polyester, starch-containing polymer, polystyrene, and polyurethane Preferably, the fourth layer comprises at least one member selected from the group consisting of polyethylene homopolymer, polyethylene copolymer, polypropylene homopolymer, polypropylene copolymer, polybutene homopolymer, and polybutene copolymer, and the fourth layer is an outer layer Preferably, the multilayer film further comprises a fifth layer between the third layer and the fourth layer, the fifth layer serving as a tie-layei Preferably, the multilayer film further comprises a sixth layer between the first layer and the third layer, the sixth layer serving as a tie-layer Preferably, the multilayer film has biaxially oriented Preferably, the multilayer film has a free shrink, at 185°F, of at least 10 percent in at least one direction Preferably, at least a portion of the multilayer film comprises a cross-linked polymer network As a second aspect, the present invention is directed to a bag comprising a multilayer film as in the first aspect of the present invention Preferably, the bag is an end- seal bag or a side seal bag Preferably, the multilayer film in the bag is a preferred multilayer film in accordance with the first aspect of the present invention As a third aspect, the present invention is directed to a packaged product comprising a package and a product in the package The package comprises the multilayer film as set forth in the first aspect of the present invention The product comprises cooked meat Preferably, the multilayer film in the package is a preferred multilayer film in accordance with the first aspect of the present invention Preferably, the cooked meat product comprises at least one member selected from the group consisting of poultry, ham, roast beef, liver sausage, mortadella, bologna, goat, and lamb More preferably, the cooked meat product comprises at least one member selected from the group consisting of poultry, ham, and roast beef Brief Description of the Drawings Figure 1 illustrates an enlarged cross-sectional view of a preferred 5-layer multilayer film suitable for use in the article according to the present invention Figure 2 illustrates an enlarged cross-sectional view of a preferred 6-layer multilayer film suitable for use in the article according to the present invention Figure 3 illustrates an enlarged cross-sectional view of another preferred 6-layer multilayer film suitable for use in the article according to the present invention Figure 4 illustrates a schematic view of a process for making a preferred heat- shrinkable multilayer film for use in the article according to the present invention Figure 5 illustrates a perspective view of a packaged cooked meat product according to the present invention. Figure 6 illustrates a perspective view of a packaged cooked meat product according to the present invention Figure 7 is a photograph of a wrinkled, creased comparative film Figure 8 is a photograph of a non-wrinkled, non-creased film to be used in the article according to the present invention, i.e., a smooth film Detailed Description of the Inventio n As used herein, the phrase "lay-flat film" refers to a film that has been extruded as a wide, thin-walled, circular tube, usually blown, cooled, then gathered by converging sets of rollers and wound up in flattened form The phrase "lay-flat width", refers to half of the circumference of the inflated film tube As used herein, the phrase ". a layer comprising a polyamide having a melting point " refers to a film layer containing at least one polyamide, the polyamide having a melting point within the specified temperature range The article of the present invention is preferably a bag, thermoformed package portion, or other converted film product. Preferably, the first layer serves as both a seal layer and a food-contact layer. As used herein, the term "film" is used in a generic sense to include plastic web, regardless of whether it is film or sheet Preferably, films of and used in the present invention have a thickness of 0.25 mm or less As used herein, the term "package" refers to packaging materials configured around a product being packaged The phrase "packaged product," as used herein, refers to the combination of a product which is surrounded by a packaging material As used herein, the term "seal" refers to any seal of a first region of a film surface to a second region of a film surface, wherein the seal is formed by heating the regions to at least their respective seal initiation temperatures The sealing can be performed by any one or more of a wide variety of manners, such as using a heated bar, hot air, hot wire, infrared radiation, ultrasonic sealing, radio frequency sealing, etc. However, the preferred sealing mechanism is a seal made on a bag machine using a hot-wire As used herein, the phrases "food-contact layer" and "meat-contact layer" refer to a layer of a multilayer film which is in direct contact with the food/meat in the package comprising the film In a multilayer film, a food-contact layer is always an outer film layer, as the food-contact layer is in direct contact with the food product within the package The food- contact layer is an inside layer in the sense that with respect to the packaged food product, the food-contact layer is the inside layer (i e , innermost layer) of the package, this inside layer being in direct contact with the food As used herein, the phrases "food-contact surface" and "meat-contact surface" refer to an outer surface of a food contact layer, this outer surface being in direct contact with the food within the package As used herein, the phrases "meat-adhesion," "film-to-meat adhesion," "film-to-food adhesion," and "adhered", refer to maintaining direct contact between the meat surface and the meat-contact surface of the film, so that there is an absence of a substantial amount of free moisture, i e , purge, which is water and juices emitted outside of the food/meat product In general, there is an absence of a substantial amount of free moisture if the level of free moisture is from about 0 to 2%, based on the weight of the meat product before cooking Preferably the amount of free moisture is from about 0 to 1%, more preferably, 0 to 0 5%, and still preferably from 0 to 0 1 percent based on the weight of the meat product before cooking As used herein, the phrase "meat pull-off' refers to that portion of a cook-in meat product which is torn off of the meat product upon stripping the cook-in film from the cooked meat product As used herein, the term "ham," and the phrase "ham products," include the following categories known to those of skill in the art ham with natural juices, ham with water added, and, ham-and-water product The ham with natural juices comprises at least 17 l /ι% protein fat-free [PFF], while the ham with water added comprises at least 16% protein fat-free The ham-and-water product, on the other hand, comprises at least 16% protein fat-free, but also comprises added ingredients in an amount of about 35 weight percent, based on the weight of the product Due to the relatively high percentage of added ingredients in the ham-and-water product, it is much more difficult to obtain adequate film-to-meat adhesion to the ham-and- water product than to the other above-identified ham products The above descriptions of ham products are known to those of skill in the art, and moreover, are disclosed in the Encyclopedia of Labeling Meat and Poultry Products, Eighth Edition, Meat Plant Magazine, St Louis, Mo As used herein, the phrase "cook-in" refers to the process of cooking a product packaged in a material capable of withstanding exposure to long and slow cooking conditions while containing the food product, for example submersion in water at 57°C to 121 °C (1 e, 135°F-250°F) for 2-12 hours, preferably 57°C to 100°C (i e, 135°F-250°F) for 2- 12 hours Cook-in packaged foods are essentially pre-packaged, pre-cooked foods which may be directly transferred to the consumer in this form These types of foods may be consumed with or without warming Cook-in packaging materials maintain seal integrity, and in the case of multilayer films are delamination resistant Cook-in films must also be heat shrinkable under cook-in conditions so as to form a tightly fitting package Cook-in films preferably have a tendency for adhesion to the food product, thereby preventing "cook-out", which is the collection of juices between the outer surface of the food product and the meat-contact surface of the film, i e , the surface in direct contact with the meat Additional optional characteristics of films for use in cook-in applications include delamination-resistance, low O 2 -peiTneability, heat-shrinkability representing about 20-50% biaxial shrinkage at about 85°C (185°F), and optical clarity For hermetically sealed bags, it is preferred that the external surface of the package is subjected to a temperature of at least about 150°F, preferably from about 150°F to 212°F, more preferably, from about 160 to 212°F, still more preferably, from about 165°F to 200°F, and, even yet still more preferably, from about 170°F to 180°F As used herein, "EVOH" refers to ethylene vinyl alcohol copolymer EVOH includes saponified or hydrolyzed ethylene vinyl acetate copolymers, and refers to a vinyl alcohol copolymer having an ethylene comonomer, and prepared by, for example, hydrolysis of vinyl acetate copolymers, or by chemical reactions with polyvinyl alcohol The degree of hydrolysis is preferably from about 50 to 100 mole percent, more preferably, from about 85 to 100 mole percent As used herein, the term "barner", and the phrase "barπer layer", as applied to films and or film layers, are used with reference to the ability of a film or film layer to serve as a barrier to one or more gases In the packaging art, oxygen (i e , gaseous O.») barπer layers have included, for example, hydrolyzed ethylene/vmyl acetate copolymer (designated by the abbreviations "EVOH" and "HEVA", and also referred to as "ethylene/vmyl alcohol copolymer"), polyvinylidene chloπde, polyamide, polyester, polyacrylonitπle, etc , as known to those of skill in the art As used herein, the phrase "abuse layer", as well as the phrase "puncture-resistant layer", refer to an outer film layer and/or an inner film layer so long as the film layer serves to resist abrasion, puncture, and other potential causes of reduction oi package integπty, as well as potential causes of reduction of package appearance quality As used herein, the terms "lamination," "laminate," as well as the phrase "laminated film," refer to the process, and resulting product made by bonding together two or more layers of film or other mateπals Lamination can be accomplished by |θinιng layers with adhesives, joining with heat and pressure, with corona treatment and even spread coating and extrusion coating The term laminate is also inclusive of coextruded multilayer films compπsing one or more tie layers As used herein, the term "oπented" refers to a polymer-containing mateπal which has been elongated (generally at an elevated temperature called the oπentation temperature) followed by being "set" in the elongated configuration by cooling the mateπal while substantially retaining the elongated dimensions This combination of elongation at elevated temperature followed by cooling causes an alignment of the polymer chains to a more parallel configuration, thereby improving the mechanical properties of the film Upon subsequently heating unrestrained, unannealed oriented polymer-containing mateπal to its oπentation temperature, heat shπnkage is produced almost to the original dimensions, i e , pre- elongation dimensions The term "oπented," is herein used with reference to oπented films, which can undergo oπentation in any one or more of a variety of manners Orienting in one direction is referred to herein as "uniaxial orientation," while orienting in two directions is referred to herein as "biaxial orientation " In oriented plastic films, there can be internal stress lemaining in the plastic sheet which can be relieved by reheating the film to a temperature above that at which it was oriented Upon reheating such a film, the film tends to shrink back to the original dimensions it had before it was oriented Films which shrink upon being heated are generally referred to as heat- shrinkable films As used herein, the phrase "orientation ratio" refers to the multiplication product of the extent to which the plastic film material is oriented in several directions, usually two directions peφendicular to one another Orientation in the machine direction is herein referred to as "drawing", whereas orientation in the transverse direction is herein referred to as "stretching" For films extruded through an annular die, stretching is obtained by "blowing" the film to produce a bubble For such films, drawing is obtained by passing the film through two sets of powered nip rolls, with the downstream set having a higher surface speed than the upstream set, with the resulting draw ratio being the surface speed of the downstream set of nip rolls divided by the surface speed of the upstream set of nip rolls The degree of orientation is also referred to as the orientation ratio, also known as the "racking ratio" As used herein, the term "monomer" refers to a relatively simple compound, usually containing carbon and of low molecular weight, which can react to form a polymer by combining with itself or with other similar molecules or compounds As used herein, the term "comonomer" refers to a monomer which is copolymerized with at least one different monomer in a copolymerization reaction, the result of which is a copolymer As used herein, the term "polymer" refers to the product of a polymerization reaction, and is inclusive of homopolymers, copolymers, terpolymers, tetrapolymers, etc In general, the layers of a film can consist essentially of a single polymer, or can have additional polymers together therewith, i.e., blended therewith As used herein, the term "homopolymer" is used with reference to a polymer resulting from the polymerization of a single monomer, i e., a polymer consisting essentially of a single type of repeating unit As used herein, the term "copolymer" refers to polymers formed by the polymerization reaction of at least two different monomers. For example, the term "copolymer" includes the copolymerization reaction product of ethylene and an alpha-olefin, such as 1-hexene The term "copolymer" is also inclusive of, for example, the copolymerization of a mixture of ethylene, propylene, 1-hexene, and 1-octene As used herein, the term "copolymerization" refers to the simultaneous polymerization of two or more monomers. The term "copolymer" is also inclusive of random copolymers, block copolymers, and graft copolymers As used herein, the term "polymerization" is inclusive of homopolymerizations, copolymerizations, terpolymerizations, etc., and includes all types of copolymerizations such as random, graft, block, etc. In general, the polymers, in the films used in accordance with the present invention, can be prepared in accordance with any suitable polymerization process , including slurry polymerization, gas phase polymerization, and high pressure polymerization processes. As used herein, a copolymer identified in terms of a plurality of monomers, e.g., "propylene/ethylene copolymer", refers to a copolymer in which either monomer may copolymerize in a higher weight or molar percent than the other monomer or monomers However, the first listed monomer preferably polymerizes in a higher weight percent than the second listed monomer, and, for copolymers which are terpolymers, quadripolymers, etc , preferably the first monomer copolymerizes in a higher weight percent than the second monomer, and the second monomer copolymerizes in a higher weight percent than the third monomer, etc As used herein, terminology employing a "/" with respect to the chemical identity of a copolymer (e.g., "an ethylene/alpha-olefin copolymer"), identifies the comonomers which are copolymerized to produce the copolymer As used herein, "ethylene alpha-olefin copolymer" is the equivalent of "ethylene/alpha-olefin copolymer " As used herein, copolymers are identified, i.e, named, in terms of the monomers from which the copolymers are produced For example, the phrase "propylene/ethylene copolymer" refers to a copolymer produced by the copolymerization of both propylene and ethylene, with or without additional comonomer(s) As used herein, the phrase "mer" refers to a unit of a polymer, as derived from a monomer used in the polymerization reaction. For example, the phrase "alpha-olefin mer" refers to a unit in, for example, an ethylene/alpha-olefin copolymer, the polymerization unit being that "residue" which is derived from the alpha-olefin monomer after it reacts to become a portion of the polymer chain, i.e., that portion of the polymer contributed by an individual alpha-olefin monomer after it reacts to become a portion of the polymer chain As used herein, the phrase "heterogeneous polymer" refers to polymerization reaction products of relatively wide variation in molecular weight and relatively wide variation in composition distribution, i.e., polymers made, for example, using conventional Ziegler-Natta catalysts Heterogeneous polymers are useful in various layers of the film used in the present invention Such polymers typically contain a relatively wide variety of chain lengths and comonomer percentages As used herein, the phrase "heterogeneous catalyst" refers to a catalyst suitable for use in the polymerization of heterogeneous polymers, as defined above Heterogeneous catalysts are comprised of several kinds of active sites which differ in Lewis acidity and steric environment Ziegler-Natta catalysts are heterogeneous catalysts Examples of Ziegler-Natta heterogeneous systems include metal halides activated by an organometallic co-catalyst, such as titanium chloride, optionally containing magnesium chloride, complexed to trialkyl aluminum and may be found in patents such as U S Patent No 4,302,565, to GOEK.E, et al , and U S Patent No 4,302,566, to KAROL, et al., both of which are hereby incoφorated, in their entireties, by reference thereto As used herein, the phrase "homogeneous polymer" refers to polymerization reaction products of relatively narrow molecular weight distribution and relatively narrow composition distribution Homogeneous polymers can be used in various layers of multilayer films useful in the present invention Homogeneous polymers are structurally different from heterogeneous polymers, in that homogeneous polymers exhibit a relatively even sequencing of comonomers within a chain, a mirroring of sequence distribution in all chains, and a similarity of length of all chains, i e , a narrower molecular weight distribution Furthermore, homogeneous polymers are typically prepared using metallocene, or other single-site type catalysis, rather than using Ziegler Natta catalysts More particularly, homogeneous ethylene/alpha-olefin copolymers may be characterized by one or more methods known to those of skill in the art, such as molecular weight distribution (M w /M n ), composition distribution breadth index (CDBI), narrow melting point range, and single melt point behavior The molecular weight distribution (M„ M n ), also known as "polydispersity," may be determined by gel permeation chromatography Homogeneous ethylene/alpha-olefin copolymers which can be used in the present invention preferably have an M»JM n of less than 2.7; more preferably from about 1 9 to 2 5; still more preferably, from about 1 9 to 2 3. The composition distribution breadth index (CDBI) of such homogeneous ethylene/alpha-olefin copolymers will generally be greater than about 70 percent The CDBI is defined as the weight percent of the copolymer molecules having a comonomer content within 50 percent (I e , plus or minus 50%) of the median total molar comonomer content The CDBI of linear polyethylene, which does not contain a comonomer, is defined to be 100% The Composition Distribution Breadth Index (CDBI) is determined via the technique of Temperature Rising Elution I ractionation (TREF) CDBI determination clearly distinguishes homogeneous copolymers (i e , narrow composition distπbution as assessed by CDBI values generally above 70%) from VLDPEs available commercially which generally have a broad composition distribution as assessed by CDBI values generally less than 55% TREF data and calculations therefrom for determination of CDBI of a copolymer is readily calculated from data obtained from techniques known in the art, such as, for example, temperature πsing elution fractionation as described, for example, in Wild et al , J Poly Sci Poly Phys Ed , Vol 20, p 441 ( 1982) Preferably, the homogeneous ethylene/alpha-olefin copolymers have a CDBI greater than about 70%, i e , a CDBI of from about 70% to 99% In general, the homogeneous ethylene/alpha-olefin copolymers useful in the present invention also exhibit a relatively narrow melting point range, in comparison with "heterogeneous copolymers", i e , polymers having a CDBI of less than 55% Preferably, the homogeneous ethylene/alpha-olefin copolymers exhibit an essentially singular melting point characteπstic, with a peak melting point (T m ), as determined by Differential Scanning Coloπmetry (DSC), of from about 60°C to 105°C Preferably the hornogeneous copolymer has a DSC peak T m of from about 80°C to I00°C As used herein, the phrase "essentially single melting point" means that at least about 80%, by weight, of the material corresponds to a single T m peak at a temperature within the range of from about 60°C to \Q -° and essentially no substantial fraction of the mateπal has a peak melting point in excess ot about 1 15°C , as determined by DSC analysis DSC measurements are made on a Perkin Flmer System 7 Thermal Analysis System Melting information reported are second melting data i e , the sample is heated at a programmed rate of 10°C /min to a temperature below its critical range T he sample is then reheated (2nd melting) at a programmed rate of 10°C/mιn A homogeneous ethylene/alpha-olefin copolymei can in general, be prepared by the copolymeπzation of ethylene and any one or more alpha-olefin Preferably, the alpha-olefin is a Cι-C 2 o alpha-monoolefin, more preferably, a G--C-,. alpha-monoolefin, still more preferably, a C 4 -Cχ alpha-monoolefin Still more preferably, the alpha-olefin compnses at least one member selected from the group consisting of butene- 1 , hexene- 1. and octene- 1 , i e , 1 -butene. 1-hexene, and 1-octene, respectively Most preferably, the alpha-olefin compnses octene-1, and/or a blend of hexene-1 and butene- 1 Processes for prepanng and using homogeneous polymers are disclosed m U S Patent No 5,206,075, to HODGSON, Jr , U S Patent No 5,241 ,031 , to MEHTA, and PCT International Application WO 93/03093, each of which is hereby incoφorated by reference thereto, in its entirety Further details regarding the production and use of homogeneous ethylene/alpha-olefin copolymers are disclosed in PCT International Publication Number WO 90/03414, and PCT International Publication Number WO 93/03093, both of which designate Exxon Chemical Patents, Inc as the Applicant, and both of which are hereby incoφorated by reference thereto, in their respective entireties Still another species of homogeneous ethylene/alpha-olefin copolymers is disclosed in U S Patent No 5,272,236, to LAI, et al , and U S Patent No 5,278,272, to LAI, et al , both of which are hereby incoφorated by reference thereto, in their respective entireties As used herein, the term "polyolefin" refers to any polymerized olefin, which can be linear, branched, cyclic, aliphatic, aromatic, substituted, or unsubstituted More specifically, included in the term polyolefin are homopolymers of olefin, copolymers of olefin, copolymers of an olefin and an non-olefinic comonomer copolymenzable with the olefin, such as vinyl monomers, modified polymers thereof, and the like Specific examples include polyethylene homopoiymer, polypropylene homopolymer, polybutene, ethylene/alpha-olefin copolymer, propylene/alpha-olefin copolymer, butene/alpha-olefin copolymer, ethylene/ vinyl acetate copolymer, ethylene/ethyl acrylate copolymer, ethylene/butyl acrylate copolymer, ethylene/methyl acrylate copolymer, ethylene/acrylic acid copolymer, ethylene/methacrylic acid copolymer, modified polyolefin resin, lonomer resin, polymethylpentene, etc Modified polyolefin resin is inclusive of modified polymer prepared by copolymeπzmg the homopolymer of the olefin or copolymer thereof with an unsaturated carboxylic acid, e g , maleic acid, fumaπc acid or the like, or a deπvative thereof such as the anhydπde, ester or metal salt or the like It could also be obtained by incoφoratmg into the olefin homopolymer or copolymer, an unsaturated carboxylic acid, e g , maleic acid, fumaπc acid or the like, or a deπvative thereof such as the anhydnde, ester or metal salt or the like As used herein, terms identifying polymers, such as "polyamide", "polyester" "polyurethane", etc are inclusive of not only polymers compπsing repeating units deπved from monomers known to polymeπze to form a polymer of the named type, but are also inclusive of comono ers, deπvatives, etc which can copolymeπze with monomers known to polymeπze to produce the named polymer For example, the term "polyamide" encompasses both polymers compπsing repeating units deπved from monomers, such as caprolactam, which polymeπze to form a polyamide, as well as copolymers deπved from the copolymeπzation of caprolactam with a comonomer which when polymeπzed alone does not result in the formation of a polyamide Furthermore, terms identifying polymers are also inclusive of "blends" of such polymers with other polymers of a different type As used herein, the phrase "anhydride functionality" refers to any form of anhydπde functionality, such as the anhydπde of maleic acid, fumaric acid, etc whether blended with one or more polymers, grafted onto a polymer, or copolymeπzed with a polymer, and, in general, is also inclusive ot derivatives of such functionalities, such as acids, esters, and metal salts derived therefrom As used herein, the phrase "modified polymer", as well as more specific phrases such as "modified ethylene vinyl acetate copolymer", and "modified polyolefin" refer to such polymers having an anhydπde functionality, as defined immediately above grafted thereon and or copolymeπzed therewith and/or blended therewith Preferably, such modified polymers have the anhydπde functionality grafted on or polymeπzed therewith, as opposed to merely blended therewith As used herein, the phrase "anhydπde-containing polymer" refers to one or more of the following ( 1 ) polymers obtained by copolymeπzing an anhydride-containing monomer with a second, different monomer, and (2) anhydride grafted copolymers, and (3) a mixture of a polymer and an anhydπde-containing compound As used herein, the phrases "ethylene alpha-olefin copolymer", and "ethylene/alpha- olefin copolymer", refer to such heterogeneous mateπals as low density polyethylene (LDPE), medium density polyethylene (MDPE), linear low density polyethylene (LLDPE), and very low and ultra low density polyethylene (VLDPE and ULDPE), as well as to such homogeneous ethylene/alpha olefin copolymers as metallocene-catalyzed EXACT (TM) linear homogeneous ethylene/alpha olefin copolymer resins obtainable from the Exxon Chemical Company, of Baytown Texas, homogeneous substantially linear ethylene/alpha- olefin copolymers having long chain branching (e g , copolymers known as AFFINITY (TM) resins, and ENGAGE (TM) resins, available from the Dow Chemical Company, of Midland, Michigan), as well as TAFMER (TM) linear homogeneous ethylene/alpha-olefin copolymer resins obtainable from the Mitsui Petrochemical Coφoration Both the heterogeneous polymers and homogeneous polymers referred to above generally include copolymers of ethylene with one or more comonomers selected from C 4 to do alpha-olefin such as butene- 1 (i e , I -butene), hexene- 1 , octene- 1 , etc While LDPE and MDPE are more highly branched than LLDPE, VLDPE, ULDPE, EXACT (TM) resin, and TAFMER (TM) resin, this latter group of resins has a relatively large number of short branches rather than the longer branches present in LDPE and MDPE AFFINITY (TM) resins and TNG AGE (TM) resins have a relatively large number of short branches in combination with a relatively small number of long-chain branches LLDPE has a density usually in the range of from about 0 91 grams per cubic centimeter to about 0 94 grams per cubic centimeter In general, the ethylene/alpha-olefin copolymer compnses a copolymer resulting from the copolymeπzation of from about 80 to 99 weight percent ethylene and from 1 to 20 weight percent alpha-olefin Preferably, the ethylene alpha-olefin copolymer compnses a copolymer resulting from the copolymeπzation of from about 85 to 95 weight percent ethylene and from 5 to 15 weight percent alpha-olefin As used herein, the phrases "inner layer" and "mtei nal layer" refer to any layer, of a multilayer film, having both of its principal surfaces directly adhered to another layer of the film As used herein, the phrase "inside layer" refers to an outer film layer, of a multilayer film packaging a product, which is closest to the product, relative to the other layers of the multilayer film "Inside layer" also is used with reference to the innermost layer of a plurality of concentπcally arranged layers simultaneously coextruded through an annular die As used herein, the phrase "outer layer" refers to any film layer of film having less than two of its pnncipal surfaces directly adhered to another layer of the film The phrase is inclusive of monolayer and multilayer films All multilayer films have two, and only two, outer layers, each of which has a principal surface adhered to only one other layer of the multilayer film In monolayer films, there is only one layer, which, of course, is an outer layer in that neither of its two pnncipal surfaces are adhered to another layer of the film As used herein, the phrase "outside layer" refers to the outer layer, of a multilayer film packaging a product, which is furthest from the product relative to the other layers of the multilayer film "Outside layer" also is used with reference to the outermost layer of a plurality of concentπcally arranged layers simultaneously coextruded through an annular die As used herein, the phrase "directly adhered", as applied to film layers , is defined as adhesion of the subject film layer to the ob|ect film layer without a tie layer , adhesive , or other layer therebetween In contrast, as used herein, the word "between", as applied to a film layer expressed as being between two other specified layers, includes both direct adherence of the subject layer between to the two other layers it is between, as well as including a lack of direct adherence to either or both of the two other layei s the subject layer is between , i e , one or more additional layers can be imposed between the sub|ect layer and one or more of the layers the sub|ect layer is between As used herein, the term "core", and the phrase "core layer", as applied to multilayer films, refer to any inner film layer which has a pπmary function other than serving as an adhesive or compatibilizer for adheπng two layers to one anothei Usually, the core layer or layers provide the multilayer film with a desired level of strength, I e , modulus, and/or optics , and or added abuse resistance, and/or specific impermeability As used herein, the phrases "seal layer," "sealing layei ' "heat seal layer 1 and "sealant layer," refer to an outer film layer, or layers, involved in the sealing of the film to itself another film layer of the same or another film, and/or another article which is not a film It should also be recognized that in general, up to the outer 3 mils of a film can be involved in the sealing of the film to itself or another layei With respect to packages having only fin type seals , as opposed to lap-type seals the phrase "sealant layer " generalh refers to the inside film layer of a package, as well as supporting layers within 3 mils ot the inside surface of the sealant layer , the inside layer frequently also serving as a food contact layer in the packaging of foods In general, sealant layers employed in the packaging art have included thermoplastic polymers , such as polyolefin, polyamide, polyester, and polyvinyl chloπde As used herein, the phrase "tie layer" refers to any inner film layer having the pπmary puφose of adhenng two layers to one another Tie layers can compnse any polymer having a polar group thereon, or any other polymer which provides sufficient interlayer adhesion to adjacent layers compπsmg otherwise nonadheπng polymers As used herein, the phrase "skin layer" refers to an outside layer of a multilayer film in packaging a product, this skin layer being subject to abuse As used herein, the phrase "bulk layer" refers to any layer of a film which is present for the puφose of increasing the abuse-resistance, toughness, modulus, etc , of a multilayer film Bulk layers generally compnse polymers which are inexpensive relative to other polymers in the film which provide some specific purpose unrelated to abuse-resistance, modulus, etc The names "first layer", "second layer", as used herein, are generally indicative of the manner in which a multilayer film structure is built up That is, in general, the first layer can be present without any of the additional layei s described, or the first and second layers can be present without any of the additional layers described, etc As used herein, the teπn "extrusion" is used with reference to the process of forming continuous shapes by forcing a molten plastic mateπal through a die, followed by cooling or chemical hardening Immediately pπor to extrusion through the die, the relatively high- viscosity polymenc matenal is fed into a rotating screw of variable pitch, i e , an extrudei, which forces the polymeric material through the die As used herein, the term "coextrusion" refers to the process by which the outputs ol two or more extruders are brought smoothly together in a feed block, to form a multilayer stream that is fed to a die to produce a layered extrudate Coextrusion can be employed in film blowing, sheet and flat film extrusion, blow molding, and extrusion coating As used herein, the phrase "machine direction", herein abbreviated "MD", refers to a direction "along the length" of the film, 1 e , in the direction of the film as the film is formed dunng extrusion and/or coating As used herein the phrase "transverse direction", herein abbreviated "TD", refers to a direction across the film, peφendicular to the machine or longitudinal direction As used herein, the phrase "free shrink" refers to the percent dimensional change in a 10 cm x 10 cm specimen of film, when shrunk at 185°F, with the quantitative determination being earned out according to ASTM D 2732, as set forth in the 1990 Annual Book of ASTM Standards, Vol 08 02, pp 368-371 , which is hereby incorporated, in its entirety, by reference thereto The multilayer films useful in the article and process of the present invention has at least 3 layers (preferably from 3 to 20 layers), and preferably has at least 4 layers (more preferably from 4 to 12 layers, still more preferably, from 4 to 1 1 layers, and yet still more preferably, from 6 to 10 layers) However, so long as the multilayer film has at least 3 layers, the multilayer film can have any further number of additional layers desired, so long as the film provides the desired properties for the particular packaging operation in which the film is used, e g O 2 -barner characteristics, free shrink, shrink tension, optics, modulus, seal strength, etc The multilayer film illustrated in Figure 1 comprises five layers, in Figure 2, six layers, in Figure 3, six layers. The multilayer film used in the present invention can have any total thickness desired , so long as the film provides the desired properties for the particular packaging operation in which the film is used Preferably, the film used in the present invention has a total thickness (i e , a combined thickness of all layers), of from about 0 3 to 15 mils ( 1 mil equals 0 001 inch), more preferably, from about 1 to 10 mils, and still more preferably, from 1 5 to 8 mils For shrinkable bags, the range from 1 5 - 3 mils is even more preferred while for non-shrinkable articles, the range of from 4-8 mils is even more preferred In Figure I , multilayer film 10 comprises outer layer 12 Used in the article of the present invention, outer layer 12 serves as an inside layer which is also a food-contact layer Outer layer 12 is a "first layer" in a film used in accordance with the present invention In the present invention, preferably the first layer comprises a polyamide having a melting point of from about 260°F to 400°F, more preferably, from about 275°F to 375°F, still more preferably, from about 300 to 360°F, and, yet still more preferably, from about 300 to345°F Preferably, this polyamide comprises at least one member selected from the group consisting of copolyamide 6/12, polyamide 12, copolyamide 66/69/61, copolyamide 66/610, copolyamide 6/66, and copolyamide 6/69 In one preferred embodiment, the polyamide in the first layer comprises at least one member selected from the group consisting of (a) copolyamide 6/12 comprising (i) caprolactam mer in an amount of from about 20 to 80 weight percent, and (ii) laurolactam mer in an amount of from about 80 to 20 weight percent, (b) polyamide 12, (c) copolyamide 66/69/61 comprising 10 to 50 weight percent hexamethylene adipamide mer (more preferably, from about 20 to 40 weight percent), 10 to 50 weight percent polyamide 69 mer (more preferably, from about 20 to 40 weight percent), and, 10 to 60 weight percent hexamethylene isophthalamide mer (more preferably, from about 10 to 40 weight percent) Still more preferably, the polyamide in the first layer comprises a blend of 50% copolyamide 6/12, which preferably comprises about 50% caprolactam mer, and 50%> polyamide 12 Preferably, the first layer comprises only one polyamide, more preferably, the first layer consists of only one polyamide Preferably, the first layer has a thickness of from about 3 to 20 percent, based on the total thickness of the multilayer film, more preferably, from about 5 to 18 percent, still more preferably, from about 7 to 16 percent, yet still more preferably, from about 9 to 13 percent Preferably, the first layer has a thickness of from about 0 05 to 2 mils, more preferably, from about 0 1 to 1 mil, still more preferably, from about 0 2 to 0 8 mil, yet still more preferably, from about 0 2 to 0 4 mil, and, even yet still more preferably, from about 0 2 to 0 3 mil In Figure 1 , multilayer film 10 further compnses inner layer 14 Inner layer 14 is a "second layer in a film used in accordance with the present invention In the present invention, the polyamide in the second layer prefereably comprises at least one member selected from the group consisting of polyamide 6, polyamide 9 polyamide 10, polyamide 1 1 , polyamide 12, polyamide 66, polyamide 610, polyamide 612, polyamide 61, polyamide 6T, polyamide 69, and copolymers thereof, more preferably the polyamide in the second layer comprises at least one member selected from the group consisting of polyamide 6, 66 and 6/66 Preferably, the polyamide in the second layer has a melting point of at least 350°F, more preferably, at least 370°F and even more preferably, at least 390°F Preferably, the second layer further comprises a polymer which retards the crystallization of the polyamide in the second layer Preferably this (crystal zation- retarding) polymer comprises at least one member selected from the group consisting of polyolefin and third polyamide Preferably, the polyolefin comprises at least one member selected from the group consisting of ethylene/unsaturated acid copolymer ethylene/unsaturated ester copolymer, and modified polyolefin Preferably, the third polyamide has a crystal structure different from the polyamide in the second layer of the multilayer film More particularly, the second film layer preferably comprises a blend of polyamide 6 with a third polyamide comprising at least one member selected from the group consisting of polyamide 9, polyamide 10, polyamide I I , polyamide 12, polyamide 66, polyamide 610, polyamide 612, polyamide 61, polyamide 6T, polyamide 69, and copolymers thereof Still more preferably, the second layei comprises (a) polyamide 6 in an amount of from about 40 to 90 weight percent, based on the weight of the second layer, and (b) copolyamide 6/12 in an amount of from about 10 to 60 weight percent based on the weight of the second layer, wherein the copolyamide 6/12 comprises caprolactam mer in an amount of from about 30 to 70 weight percent (more preferably , 40 to 60 weight percent) If the heat-shπnkable multilayer film which is used in accordance with the present invention is made by orienting a tape which is heated over a very short time period, such as a tape heated by infrared radiation, the thickness of the second layer could be as high as 70%, based on the thickness of the multilayer film However, if the film is heated over a relatively long time period, such as being heated in hot water, the preferred polyamides tend to crystallize to a relatively high level before the orientation step, which produces problems during the oπentation step (the rate of crystallization depends on the type of polyamide used) In this latter situation, typically, the greater the thickness of the second layer, the more difficult it is to orient to obtain the resulting multilayer film This forces a practical limit on the maximum percentage thickness ot the second layer (especially when the most preferred polyamides are used), based on the total thickness of the multilayei film Thus, if hot-water is used as the orientation medium the second layer of the heat- shπnkable film preferably has a thickness of from about ■ to 50 percent of the total thickness of the multilayer film, more preferably, from about . to 30 percent, still more preferably, from about 5 to 20 percent, and yet still more preferably, from about 5 to ! 5 percent, based on a total thickness of the multi-layer film The second layer preferably comprises another polymer which disrupts the crystallinity of the polyamide in the second lavei 1 he composition as disclosed immediately above facilitates orientation of a tape to get the resultant multilayer film This is especially preferred for orientation out of hot-water In Figure 1, multilayer film 10 further comprises inner layer 16 Inner layer 16 is a "third layer" in a film used in accordance with the present invention, hence, inner layer 16 serves as an O 2 -barπer layer In the present invention, the third film layei serves as an O2-barπer layer, and comprises at least one member selected from the group consisting of ethylene/vmyl alcohol copolymer, polyamide, polyvinyhdene chloride, and polyalkylene carbonate, more preferably, at least one member selected from the group consisting of ethylene/vmyl alcohol and polyamide This θ2-barner layer serves to piovide the multilayer film with a layer which is especially impervious to atmospheric oxygen, which results in increasing the shelf life of the packaged product However, EVOH is the preferred polymer for use in the O 2 -banier layer Preferably, the O2-barrier layer has a thickness of from about 0 05 to 5 mils, more preferably, from 0.05 to 0 5 mil, yet still more preferably, from 0 1 to 0 3 mil; and even yet still more preferably, from about 0 12 to 0 17 mils In Figure 1, multilayer film 10 further comprises outer layer 18 Outer layer 18 is a "fourth layer" in a film used in accordance with the present invention In the present invention, the fourth film layer provides the multilayer film with the desired abuse, shrink, and optical characteristics, and preferably comprises a polymer having relatively low cost while providing these characteristics Preferably, the fourth layer has a thickness of from about 0 1 to 3 mils, more preferably, from 0 2 to 2 mils, still more preferably, from 0 3 to 1 5 mil; and yet still more preferably, from about 0 6 to 1 3 mils Preferably, the fourth layer comprises at least one member selected from the group consisting of polyolefin, poiyamide, polyester, starch-containing polymer, polystyrene, and polyurethane More preferably, the fourth layer comprises at least one member selected from the group consisting of polyethylene homopolymer, polyethylene copolymer, polypropylene homopolymer, polypropylene copolymer, polybutene homopolymer, and polybutene copolymer, still more preferably, the fourth layer comprises at least one member selected from the group consisting of ethylene/alpha-olefin copolymer, propylene/alpha-olefin copolymer, butene/alpha-olefin copolymer, ethylene/unsaturated ester copolymer, and ethylene/unsaturated acid copolymer, yet still more preferably, the fourth layer comprises at least one member selected from the group consisting of ethylene/vinyl acetate copolymer, linear low density polyethylene and high density polyethylene. Preferably, the fourth layer is an outer layer In Figure 1, multilayer film 10 further comprises inner layer 20 Inner layer 20 is a "fifth layer" in a film used in accordance with the present invention In the present invention, the fifth layer is between the third layer and the fourth layer and serves as a tie layer. As a general rule, tie layers should have a relatively high degree of compatibility with barrier layers, such as polymerized EVOH, or the polyamide layer, as well as non-barrier layers, such as polymerized ethylene alpha-olefin copolymer The composition, number, and thickness of tie layers is as known to those of skill in the art Preferably, the fifth layer has a thickness of from about 0 05 to 2 mils, more preferably, from about 0.05 to 0 5 mil; still more preferably, from about 0 1 to 0.3 mil; and yet still more preferably, from about 0.12 to 0 17 mils Preferably, the fifth layer comprises at least one member selected from the group consisting of modified ethylene/alpha-olefin copolymer, modified ethylene/unsaturated ester copolymer, modified ethylene/unsaturated acid copolymer, and polyurethane More preferably, the fifth layer comprises an anhydride- modified polyolefin. Figures 2 and 3 illustrate two alternative preferred embodiments of oriented, heat- shrinkable multilayer films to be used in the article of the present invention Figures 2 and 3 each illustrate six-layer films These two films are especially suited for conversion to heat- shrinkable bags for the packaging of meat products, in accordance with the present invention In Figure 2, multilayer film 22 comprises outer layer 24 which serves as a seal layer and is the first film layer, as described above Inner layer 26 is the second film layer, also as described above Inner layer 28 serves as an O barrier layer, and is the third film layer, as described above Outer layer 30 provides the multilayer film with the desired abuse, shrink, and optical characteristics, and is the fourth film layer, as described above Inner layer 32 is between second layer 26 and third layer 28, inner layer 32 serves as a tie layer, and is the fifth film layer, as described above Multilayer film 22 further comprises inner layer 34, which is between third layer 28 and fourth layer 30, inner layer 34 serves as a tie layer and is the sixth film layer In the present invention, the sixth film layer is between the first layer and the third layer and also serves as a tie-layer Preferably, the sixth layer has a thickness of from about 0 05 to 2 mils, more preferably, from about 0 1 to 1 mil, still more preferably, from about 0 2 to 0.8 mil; and yet still more preferably, from about 0 3 to 0 5 mils Preferably, the sixth layer comprises at least one member selected from the group consisting of modified ethylene/alpha-olefin copolymer, modified ethylene/unsaturated ester copolymer, modified ethylene/unsaturated acid copolymer, and polyurethane More preferably, the sixth layer comprises an anhydride-modified polyolefin Figure 3 illustrates alternative 6-layer multilayer film 36 to be used in the article of the present invention Multilayer film 36 comprises outer layer 38, which serves as a food-contact and seal layer, and is the first film layer Inner layer 40 is the second film layer Inner layer 42 serves as the O2-barrier layer, and is the third film layer Outer film layer 44 provides the multilayer film with the desired abuse, shrink, and optical characteristics, and is the fourth film layer, as descπbed above Inner film layer 46 is between first film layer 38 and third film layer 42, inner layer 46 serves as a tie layei, and is the sixth film layer, as described above Inner film layer 48 is between second film layer 40 and fourth film layer 44, inner layer 48 serves as a tie layer, and is the fifth film layer, as descπbed above Figure 4 illustrates a preferred process for making casing film and/or butt-seal tape film for tn accordance with the present invention For example. Figure 4 illustrates a preferred process for making the films illustrated in Figures 1 , 2, and 3 In the process illustrated in Ftgure 4, solid polymer beads (not illustrated) are fed to a plurality of extruders (for simplicity only extruder 88 is illustrated) Inside extruders 88, the polymer beads are degassed, following which the resulting bubble-free melt is forwarded into die head 90, and extruded through an annular die, resulting in tubing tape 92 which is preferably from about 15 to 30 mils thick, and preferably has a lay-flat width of from about 2 to 10 inches After cooling or quenching by water spray from cooling ring 94, tubing tape 92 is collapsed by pinch rolls 96, and is thereafter fed through irradiation vault 98 surrounded by shielding 100, where tubing 92 is irradiated with high energy electrons (1 e , ionizing radiation) from iron core transformer accelerator 102 Tubing tape 92 is guided through irradiation vault 98 on rolls 104 Preferably, tubing tape 92 is irradiated to a level of from about 40- 100 kGy resulting in irradiated tubing tape 106 Irradiated tubing tape 106 is wound upon windup roll 108 upon emergence from irradiation vault 98 forming irradiated tubing tape coil 1 10 After irradiation and windup, windup roll 108 and irradiated tubing tape coil 1 10 are removed and installed as unwind roll 1 12 and unwind tubing tape coil 1 14, on a second stage in the process of making the film as ultimately desired Irradiated tubing 106, being unwound from unwind tubing tape coil 1 14, is then passed over guide roll 1 16, after which irradiated tubing 106 is passed through hot water bath tank 1 18 containing hot water 120 Irradiated tubing 106 is then immersed in hot water 120 (preferably having a temperature of about 185- 210°F) for a penod of about 20-60, I e , for a time period long enough to bring the film up to the desired temperature for biaxial orientation Thereafter, hot, irradiated tubular tape 122 is directed through nip rolls 124, and bubble 126 is blown, thereby transversely stretching hot, irradiated tubular tape 122 so that an onented film tube 128 is formed Furthermore, while being blown, i e , transversely stretched, nip rolls 1 0 have a surface speed higher than the surface speed of nip rolls 124, thereby resulting in longitudinal orientation As a result of the transverse stretching and longitudinal drawing, oriented film tube 128 is produced, this blown tubing preferably having been both stretched in a ratio of from about 1 1 5 to 1 6, and drawn in a ratio of from about I 1 5 to 1 6 More preferably, the stretching and drawing are each performed at a ratio of from about 1 2 to 1 4 The result is a biaxial orientation of from about 1 2 25 to 1 36, more preferably, 1 4 to 1 16 While bubble 126 is maintained between pinch rolls 124 and 130, onented film tube 128 is collapsed by rollers 132, and thereafter conveved through pinch rolls 130 and across guide roll 134, and then rolled onto wind-up roll 136 Idler roll 138 assures a good wind-up The resulting multilayei film can be used to form backseamed casings, etc , which, in turn, can be used for the packaging of meat products, in accordance with the present invention The films in the examples set forth below were prepared according to the process descnbed immediately above These examples provide additional details on the multilayer films and the good performance of the multilayer films dunng a sealing and cooking process The polymer components used to fabricate the multilayer film according to the present invention may also contain appropnate amounts of additives typically included in such compositions These additives include slip agents such as talc, antioxidants fillers, dyes, pigments, radiation stabilizers, antistatic agents, elastomers and like additives known to those of skill in the art of packaging films The multilayer films according to the present invention can be prepared by any means known to those of skill in the art, e via coextrusion and/or extrusion coating and/or lamination However, preferably the films are produced by coextrusion The multilayer film according to the present invention preferably has a free shrink of from about 5-70 percent in one or both directions (ι e longitudinal direction "L", also referred to as "machine direction", and transverse direction "T", at 185°f , determined according to ASTM D 2732-83, which is hereby incorporated, in its entirety, by reference thereto), more preferably, from about 10-50 percent at 18^°F, still more preferably, from about 15-35 percent at 185 Preferably, the multilayer film is biaxially oriented In another preferred embodiment, the multilayer film may be oriented and then heatset or annealed In this preferred embodiment, the multilayer film according to the present invention preferably has a transverse direction free shrink of about 0 to 20% at 185°F, more preferably, from about 2 to 10 percent Preferably, the multilayei film has a shrink tension in at least one direction of at least about 10 psi, more preferably from about 20- 1000 psi, still more preferably, from about 100 to 600 psi, and yet still more preferably, from about 250 to 450 psi Even more preferably, the multilayer film according to the present invention has a longitudinal shrink tension of at least 275 psi at 185°F, more preferably, at least 300 psi at 185°F Certain packaging operations involve the use of a heat-shπnkable bag to package and cook a turkey product In these applications, it is often desirable to obtain a product after cooking which has a profile similar to a turkey-breast In these applications it may be desirable to obtain a high a level of shrink tension in order to achieve the proper shape Preferably, the multilayer shπnkable film used in these applications has a shrink tension (in at least one direction) of at least 1 50 psi more preferably at least 200 psi, even more preferably, at least 250 psi, still more preferably at least 275 psi, and yet still more preferably, at least 300 psi The presence of the second layer of the multilayer film according to the present invention helps provide the multilayer shrink film with the desired shrink and shrink tension characteristics in order to achieve the proper product profile after cooking The multilayer films according to the present invention preferably compnse a crosslinked polymer network Although the crosslinked polymer network can be produced in one or more of a variety of manners, such as chemical crosslinking and/or irradiation, preferably the crosslinked polymer network is produced by the irradiation of a tape or film Either some or all of the layers of the multilayer film can compnse crosslinked polymer networks In the irradiation process, the film is subjected to an energetic radiation treatment such as high energy electron treatment, which induces cross-linking between molecules of the irradiated mateπal The irradiation of polymeric films is disclosed in U S Patent NO 4,064,296, to BORNSTEIN, et al , which is hereby incorporated in its entirety, by reference thereto BORNSTEIN, et al discloses the use of ionising radiation for crosslinking the polymer present in the film Radiation dosages are referred to herein in terms of the radiation unit "RAD" with one million RADS, also known as a megarad, being designated as "MR", or, in terms of the radiation unit kiloGray (kGy), with 10 kiloGray representing I MR, as is known to those of skill in the art A suitable radiation dosage of high energy electrons is in the range of up to about 16-166 kGy, more preferably about 44-139 kGy, and still more preferably, 80-120 kGy Preferably, irradiation is earned out by an electron accelerator and the dosage level is determined by standard dosimetry methods Figure 5 illustrates a packaged cooked meat product 50, according to the present invention The product, a cooked meat product, is packaged in a heat-sealed, heat-shπnkable bag, within which the meat product has been cooked The package compnses multilayer film 52, which can be, for example, multilayer film 10 illustrated in Figure 1, or multilayer film 22 illustrated in Figure 2, or multilayer film 36 illustrated in Figure 3, all of which are discussed in detail above In Figure 5, the cooked meat product preferably compnses pork, in the form of a boneless ham Figure 6 illustrates yet another embodiment of a packaged cooked meat product 60, according to the present invention I he product, a cooked meat product, is packaged in a heat-sealed, thermoformed web having a lidstock web sealed thereto, with the meat product being cooked within the sealed thermoformed package The package comprises multilayer film 62, which can be, for example, multilayer film 10 illustrated in Figure 1 or multilayer film 22 illustrated in Figure 2, or multilayer film 36 illustrated in Figure 3, all of which are discussed in detail above In Figure 6, the cooked meat product preferably compnses ham The packaged product can be made by a process comprising (A) filling an article with a meat product, (B) closing the open end of the filled article (the article being a bag casing, pouch, etc ) so that the meat product is encased by the closed article, and (C) cooking the meat product encased in the closed article by sub|ectιng the meat to cook-in so that the meat product adheres to the inside surface ot the closed article The article is an article according to the present invention, preferably a preferred article according to the present invention Although in general the product in the package can be any cooked meat product, preferably the cooked meat product comprises at least one member selected from the group consisting of poultry, ham, beef, lamb, goat, horse, fish, liver sausage, mortadella, and bologna, more preferably, poultry, ham, beef and bologna even more preferably, poultry, ham and roast beef The invention is illustrated by the following examples, which are provided for the purpose of representation, and are not to be construed as limiting the scope of the invention Unless stated otherwise, all percentages, parts, etc are by weight Example 1 A 3-1/8 inch wide (lay flat dimension) tube, called a "tape", was produced by the coextrusion process described above and illustrated in Figure 4, wherein the tape cross-section (from inside of tube to outside of tube) was as follows TABLE 1 LAYER COMPOSITION LAYER THICKNESS (mils) 50/50 blend of Nylon #1 and Nylon #2 (inside layer of tubular tape) 1 9 80/20 blend of anhydride grafted LLDPE#1 and EAO#l 3 2 anhydride grafted LLDPE#1 1.2 EVOH 1 2 50/50 blend of Nylon#3 and Nylon #2 2 0 anhydride grafted LLDPE# 1 1 5 80/20 blend of EVΛ# 1 and LLDPE#2 (outside layer of tubular tape) 7 3 wherein NYLON#1 was VESTAMID (TM) Z731 polyamide 12, obtained from Huls America, lnc , of Piscataway, N J , NYLON#2 was GR1LON" CF6S polyamide 6/12, obtained from EMS-American Grilon Inc., of Sumter, S C , LLDPE#1 was TYMOR 1203 linear low density polyethylene having an anhydride functionality grafted thereon, obtained from Morton International, of Chicago, Illinois, EAO# l was EXACT 401 1 (TM) homogeneous ethylene/alpha-olefin copolymer, obtained from the Exxon Chemical Company, of Baytown, Texas, EVOH was EVAL" LC-EI 05A polymerized ethylene vinyl alcohol, obtained from Eval Company of America, of Lisle, Illinois; NYLON#3 was ULTRAMID" B4 polyamide 6, obtained from BASF coφoration of Parsippany, New Jersey, EVA#1 was PE 5269T (TM) ethylene vinyl acetate copolymer, obtained from Chevron Chemical Company of Houston, 1 exas, LLDPE#2 was DOWLEX" 2045 03 linear low density polyethylene, obtained from Dow Plastics, of Freeport, I exas, All the resins were extruded between 380°l and 530°F, and the die was heated to approximately 420°F The extruded tape was cooled with water and flattened, the flattened width being 3-1/8 inches wide in a lay-flat configuration The tape was then passed through a scanned beam of an electronic cross-linking unit, where it received a total dosage of 105 kilo Grays (kGy) After irradiation, the flattened tape was passed through hot water for about a third of a minute, the hot water having a temperature of from about 208°F to 210Υ The resulting heated tape was simultaneously inflated into a bubble and drawn, so that a biaxially onented film tubing having a lay-fiat width of 8 inches and a total thickness of 2 0 mils was produced The bubble was stable and the optics and appearance of the film were good I he film tubing was determined to have about 15% free shrinkage in the longitudinal direction and 26% free shrinkage in the transverse direction (I e , for a total shrink of about 41% at 185°F), when immersed in hot water for about 8 seconds the hot water being at a temperature of I 85°F, i e , using ASTM method D2732-8 Bags were made from the oriented tubing undei a preferred set of conditions by making a transverse heat seal across the width of the tubing and then severing the tubing parallel to and immediately behind the seal Seveial bags were packaged, some containing water as the packaged product, with others containing a mixture of 0 1% mineral oil and 99 9% water as the packaged product These bags were evaluated for seal strength survivabihty by cooking at I90°F for 6 hrs, and were found to have acceptable seal stiength Example 2 A 4-1/4 inch wide tape was produced in a manner similar to the tape of Example 1 The tape had a tape cross-section (from inside of tube to outside of tube) as follows TABLE 2 anhydride grafted LLDPE# 1 1 5 EVOH 1 2 anhydride grafted LLDPEft l 1 1 blend of EVA# 1 (80%) and HDPEtf l (20%) (outside layer of tubular tape) 6 5 FIDPE#1 was FORTIFLEX" J60-500C- 147 high density polyethylene, obtained from Solvay Polymers, Inc , Deer Park, Texas, all other resins were as identified in Example 1 above All the resins were extruded between 380°F and 530°F, and the die was heated to approximately 420°F The extruded tape was cooled with water and flattened, the flattened width being 4-1/4 inches wide in a lay-flat configuration The tape was then passed through a scanned beam of an electronic cross-linking unit, where it received a total dosage of 105 kilo Grays (kGy) After irradiation, the flattened tape was passed through hot water for about a third of a minute, the hot water having a temperature of from about 208°F to 210°F The resulting heated tape was simultaneously inflated into a bubble (i e , stretched) and drawn, so that a biaxially oriented film tubing having a lay-flat width of I 1 inches and a total thickness of 2 0 mils was produced The bubble was stable and the optics and appearance of the film were good Bags were made from the oriented tubing under a preferred set of conditions by making a transverse heat seal across the width of the tubing and then severing the tubing parallel to and immediately behind the seal Several bags were packaged, some containing water as the packaged product, with others containing a mixture of 0 1 % mineral oil and 99 9% water as the packaged product These bags were evaluated for seal strength survivability by cooking at 190°F for 6 hrs, and were found to have acceptable seal strength Example 3 A 4-1/4 inch wide tape was produced in a manner similar to the tape of Example 1 The tape had a tape cross-section (from inside of tube to outside of tube) as follows TABLE 3 LAYER COMPOSITION LAYER THICKNESS 50/50 blend of Nylon #1 and Nylon #2 (inside layer of tubular tape) 2 0 blend of Nylon#3 (80%) and Nylon#2 (20%) 1 0 anhydride grafted LLDPE#1 1 5 EVOH 1 2 anhydride grafted LLDPE#1 1 1 blend of EVA# 1 (80%) and HDPE#1 (20%) (outside layer of tubular tape) 6 ^ All the resins were as identified in Examples 1 & 2 above All the resins were extruded between 380°F and 530°F and the die was heated to approximately 420°F The extruded tape was cooled with water and flattened, the flattened width being 4- 1 /4 inches wide in a lay-flat configuration The tape was then passed through a scanned beam of an electronic cross-linking unit, where it received a total dosage of 105 kilo Grays (kGy) After irradiation, the flattened tape was passed through hot water tor about a third of a minute, the hot water having a temperature of from about 208°F to 210°I The resulting heated tape was simultaneously inflated into a bubble (i e , stretched) and drawn, so that a biaxially oπented film tubing having a lay-flat width of 1 1 inches and a total thickness of 2 0 mils was produced The bubble was stable and the optics and appearance of the film were good Bags were made from the onented tubing under a preferred set of conditions by making a transverse heat seal across the width of the tubing and then seveπng the tubing parallel to and immediately behind the seal Several bags were packaged, some containing water as the packaged product, with others containing a mixture of 0 1% mineral oil and 99 9% water as the packaged product These bags were evaluated for seal strength survivability by cooking at 190°F for 6 hrs, and were found to have acceptable seal strength Example 4 (Comparative) A 4-1/4 inch wide tape was produced in a manner similar to the tape of Example The tape had a tape cross-section (from inside of tube to outside of tube) as follows TABLE 4 LAYER LAYER COMPOSITION THICKNESS (mils) 50/50 blend of Nylon # 1 and Nylon #2 3 5 (inside layer of tubular tape) blend of anhydride grafted LLDPE# 1 (80%) 2 3 and EAO# l (20%) anhydride grafted LLDPE# 1 1 6 EVOH 1 2 anhydride grafted LLDPE#1 1 9 blend of EVA# 1 (80%) and LLDPE#2 (20%) (outside layer of tubular tape) 5 5 Each of the resins was as identified in Examples 1 -3 above All the resins were extruded at between 380°F and 530°F, and the die was heated to approximately 420°F The extruded tape was cooled with water and flattened, the flattened width being 4-1/4 inches in a lay-flat configuration The tape was then passed through a scanned beam of an electronic cross-linking unit, where it received a total dosage of 105 kilo Grays (kGy) After irradiation, the flattened tape was passed through hot water for about a third of a minute, the hot water having a temperature of from about 208°F to 210°F The resulting heated tape was simultaneously inflated into a bubble (i e., stretched) and drawn, so that a biaxially oriented film tubing having a lay-flat width of 1 1 inches and a total thickness of 2 3 mils was produced The bubble was stable and the optics and appearance of the film were good Bags were made from the oriented tubing under a preferred set of conditions by making a transverse heat seal across the width of the tubing and then severing the tubing parallel to and immediately behind the seal Several bags were packaged, some containing water as the packaged product, with others containing a mixture of 0 1 % mineral oil and 99 9% water as the packaged product These bags were evaluated for seal strength survivability by cooking at 190°F for 6 hrs, and were found to have acceptable seal strength TABLE 5 PHYSICAL PROPERTIES OF EXAMPLES 103 "L" represents the longitudinal direction, and "T" represents the transverse direction Free Shrink was measured at various temperatuies, determined via ASTM D 2732-83 As can be seen from Table IV above, the films of Examples 1-3 had higher longitudinal (I e , machine direction) tensile strength and higher modulus than the film of Example 4 (Comparative) Moreover, while each of the films of Examples 1 -3 had a total thickness of only 2 0 mils, the film of Example 4 (Comparative) had a total thickness of 2 3 mils Thus, it is apparent that even though the films of Examples 1-3 are thinner than the film of Example 4 (Comparative), they are also significantly stiffer and therefore have better toughness and abuse-resistance characteristics, gauge for gauge, than the film of Example 4 (Comparative) Furthermore, if the film of Example 4 (Comparative) is thinned down from 2 3 mils to 2 0 mils, l e , so that it is comparable to the films of Examples 1 -3 on a same-total-thickness basis, the abuse resistance of such a comparative 2 0 mil film would be still less than the abuse-resistance of the 2 3 mil film of Example 4 (Comparative), and even further below the abuse-resistance of the 2 0 mil films of Examples 1 3 Moreover, it was unexpectedly found that the films of Examples 1-3 did not exhibit wrinkling and creasing, as is typically present in films containing a relatively high percentage of polyamide 6, i e , at least 30 weight percent polyamide 6, based on total film weight Wrinkles and creases are undesirable in the films to be used in the article of the present invention, for two reasons First, if a heat seal is made through a wrinkle or crease, the strength of the seal in the resulting article is considered to be unacceptable because of the increased likelihood that by sealing through the crease, the seal will fail during the cook-in process Second, if a film is printed as typically happens in a preferred embodiment of the present invention, the wrinkle or crease can lead to poor printability. Figure 7 is a photographic illustration of a comparative film with wrinkles and creases, which is to be contrasted with Figure 8, which illustrates a wrinkle-free and crease-free film which can be used in the article according to the present invention It is also surprising that during heat sealing the inner polyamide layer(s) permit heat transfer therethrough so the relatively high melting point polyamide in the sealing layer could be effectively sealed, i e , without burn-through and while producing a strong seal capable of surviving cook-in This surprising result is associated with the discovery that during heat sealing, films comprising a relatively high amount of polyamide 6, i e, films containing at least 30 weight percent polyamide 6 based on total film weight, interfered with heat transfer through to the seal layer The high polyamide content (especially polyamide 6) has been discovered to require the use of a higher sealing temperature, and/or longer sealing time, which unfortunately often leads to burn-through of the film, especially because the outer film layer of the more preferred films are primarily polyolefinic However, films to be used in the article of the present invention, as typified in Examples 1 -3, have a relatively thin nylon layer to facilitate heat-transfer to the sealing layer, while still enhancing the physical properties and seal strength, without wrinkling and creasing The relatively thin polyamide core layer in the film used in the article of the present invention also provides the advantage of ease of orientability, relative to comparative films having relatively thicker inner polyamide layers The thickness of a film seal layer has a significant influence on seal strength obtainable with the film That is, a seal layer which is relatively thick (e , 0 5 mil) tends to provide a stronger seal than a sealant layer which is relatively thin (e g , 0 2 mil) The thickness of the seal layer of the films of Examples 1 -3 was 0.21 mil, 0.22 mil, and 0.29 mil, respectively, whereas the thickness of the seal layer of the film of Example 4 (Comparative) was 0.50 mils However, it was apparent that even upon substantial downgauging of the thickness of the seal layer (and the overall film thickness), the films of Examples 1-3 exhibited a seal survivability under cook-in conditions which was comparable to the film of Example 4 (Comparative) This is also surprising and unexpected in view of the fact that the seal layer thickness for the film of Example 4 (Comparative) was from about 160% to 240% of the thickness of the seal layer of the films of Examples 1 , 2, and 3 Moreover, since the resins in the nylon core layer can be selected from relatively inexpensive nylons (e g , nylon 6, nylon 66, and nylon 6/66), i e , relative to the nylons in the seal layer, the overall raw material cost of the film can be substantially reduced In fact, the overall raw material cost of the film of Examples 1 -3 can be up to about 50% less than the film of Example 4 (Comparative), while maintaining comparable performance characteristics Although the present invention has been described with reference to the preferred embodiments, it is to be understood that modifications and variations of the invention exist without departing from the principles and scope of the invention, as those skilled in the art will readily understand Accordingly, such modifications are in accordance with the claims set forth below

Claims: WHAT IS CLAIMED IS 1 An article comprising a multilayer film comprising (A) a first layer comprising a polyamide having a melting point of from about 250°F to 400°F, the first layer having a thickness of less than about 18 percent, based on a total thickness of the multilayer film, (B) a second layer comprising at least one member selected from the group consisting of polyamide 6, polyamide 9, polyamide 10, polyamide 1 1 , polyamide 12, polyamide 66, polyamide 610, polyamide 612, polyamide 61, polyamide 6T, polyamide 69, and copolymers thereof, the second layer having a thickness of from about 3 to 30 percent of the total thickness of the multilayer film, and (C) a third layer which serves as an O 2 -barrier layer and comprises at least one member selected from the group consisting of ethylene/vinyl alcohol copolymer, polyamide, polyvinylidene chloride, and polyalkylene carbonate; and wherein the first layer is sealed to itself 2 The article according to claim 1 , wherein the second layer is directly adhered to the first layer 3. The article according to claim 1 , wherein the second layer comprises at least one member selected from the group consisting of polyamide 6, polyamide 66, and polyamide 6/66 4. The article according to claim 3, wherein the polyamide in the first layer has a melting point of from about 300° to 375°F. 5 The article according to claim 4, wherein the first layer comprises only one polyamide 6 The article according to claim 4, wherein the first layer comprises copolyamide 6/12 in an amount of from about 20 to 80 weight percent, and polyamide 12 in an amount of from about 80 to 20 weight percent 7 The article according to claim 6, wherein the first layer has a thickness of less than about 15 percent, based on a total thickness of the multilayer film 8 The article according to claim 6, wherein the thickness of the first layer is from about 0.2 to 0 4 mil 9 The article according to claim 3, wherein the second layer comprises polyamide 6 and at least one member selected from the group consisting of polyamide 9, polyamide 10, polyamide 1 1, polyamide 12, polyamide 66, polyamide 610, polyamide 612, polyamide 61, polyamide 6T, polyamide 69, and copolyamides thereof 10 The article according to Claim 9, wherein the second layer comprises polyamide 6 in an amount of from about 40 to 90 weight percent, and polyamide 6/12 in an amount of from about 10 to 60 weight percent 1 1 The article according to Claim 3, wherein the thickness of the second layer is from about 3 to 20 percent, based on a total thickness of the multilayer film 12 The article according to Claim 1 1 , wherein the thickness of the second layer is less than about 15 percent, based on a total thickness of the multilayer film 1 The article according to Claim 3, further comprising a fourth layer comprising at least one member selected from the group consisting of polyolefin, polyamide, polyester, starch-containing polymer, polystyrene, and polyurethane 14 The article according to Claim 13, wherein the fourth layer comprises at least one member selected from the group consisting of polyethylene homopolymer, polyethylene copolymer, polypropylene homopolymer, polypropylene copolymer, polybutene homopolymer, and polybutene copolymer, and the fourth layer is an outer layer. 15 The article according to Claim 14, further comprising a fifth layer between the third layer and the fourth layer, the fifth layer serving as a tie-layer 16. The article according to Claim 15, further comprising a sixth layer between the first layer and the third layer, the sixth layer serving as a tie-layer. 17 The article according to Claim 16 wherein the multilayer film has biaxial orientation 18. The article according to Claim 16, wherein the multilayer film has a free shrink, at 185°F, of at least 10 percent in at least one direction 19. The article according to Claim 18, wherein at least a portion of the film comprises a cross-linked polymer network 20. A bag comprising a multilayer film comprising (A) a first layer which is an outer layer sealed to itself and which serves as a food contact and seal layer, the first layer comprising a polyamide having a melting point of from about 250°F to 400°F; (B) a second layer comprising at least one member selected from the group consisting of polyamide 6, polyamide 9, polyamide 10, polyamide 1 1, polyamide 12, polyamide 66, polyamide 610, polyamide 612, polyamide 61, polyamide 6T, polyamide 69, and copolymers thereof, the second layer having a thickness of from about 3 to 30 percent of the total thickness of the multilayer film; and (C) a third layer which serves as an O 2 -barrier layer and comprises at least one member selected from the group consisting of ethylene/vinyl alcohol copolymer, polyamide, polyvinylidene chloride, and polyalkylene carbonate. 21. The bag according to Claim 20, wherein the bag is an end-seal bag 22. The bag according to Claim 20, wherein the bag is a side-seal bag. 23 A packaged product comprising. (A) a package comprising a multilayer film comprising (i) a first layer which is an inside layer sealed to itself and which serves as a food contact and seal layer, the first layer comprising a polyamide having a melting point of from about 250°F to 400°F, (ii) a second layer comprising at least one member selected from the group consisting of polyamide 6, polyamide 9, polyamide 10, polyamide 1 1 , polyamide 12, polyamide 66, polyamide 610, polyamide 612, polyamide 61, polyamide 6T, polyamide 69, and copolymers thereof, the second layer having a thickness of from about 3 to 30 percent of the total thickness of the multilayer film, and (iii) a third layer which serves as an O 2 -barrier layer and comprises at least one member selected from the group consisting of ethylene/vinyl alcohol copolymer, polyamide, polyvinylidene chloride, and polyalkylene carbonate; and (B) a product comprising cooked meat 24 The packaged product according to Claim 23 wherein the cooked meat product comprises at least one member selected from the group consisting of poultry, ham, roast beef, liver sausage, mortadella, bologna, goat, and lamb 25 The packaged product according to Claim 24 wherein the cooked meat product comprises at least one member selected from the group consisting of poultry, ham, and roast beef.

Inventors: RAMESH RAM K, RAMESH, RAM, K.
Applicants: GRACE W R & CO, W.R. GRACE & CO.-CONN.
Application year: 1997
Main classification: B32B27
IPC codes: B32B27, B65D81