Regeneration of adsorbent beds

Abstract: A nickel-based catalytic adsorbent used for removal of unwanted species contained in cryogenically produced ultra-high purity product gas, especially nitrogen, is regenerated using periodic hydrogen reduction with interim regeneration using product gas of 99.9999% purity. In the interim regeneration(s), the adsorbent is heated to at least 150°C, contacted with the regeneration product gas whilst maintained at at least 150°C, and then cooled to at most 50°C.

Description: The present invention pertains to regenerating catalyst adsorbent beds used to remove trace impurities from cryogenically produced gases, especially,. nitrogen. The manufacture of semiconductor devices, and in particular advanced semiconductor devices with very small feature sizes, higher device density and larger chip sizes requires the use of ultra-high purity (UHP) nitrogen gas as an inerting medium during various semiconductor processing steps. It is not uncommon for large semiconductor fabrication houses (FABS) to require in excess of 100,000 standard cubic feet per hour (scfh) (2,800 standard cubic meters per hour (scmh)) of UHP nitrogen. The UHP nitrogen is produced by separating the nitrogen from atmospheric air using well-known cryogenic technologies. The cryogenically separated nitrogen is then further treated to remove trace quantities of hydrogen, carbon monoxide, oxygen, carbon dioxide and water. A number of techniques for removing these unwanted species (hydrogen, carbon monoxide, oxygen, carbon dioxide and water) from nitrogen are known. Several techniques are discussed in the specification of US-A-4,869,883. In the production of UHP nitrogen, it is conventional to start with cryogenically produced nitrogen which normally contains parts-per-million levels of oxygen, carbon monoxide, hydrogen, carbon dioxide and water (hereinafter referred to as the unwanted species) in the nitrogen. The unwanted species can be effectively removed or reduced to below parts-per-billion levels by passing the cryogenically produced nitrogen through a bed of a nickel-based catalytic adsorbent. The capability of the adsorbent decreases with time-on-stream or time-in-use. In order to rejuvenate the ability of the nickel-based catalytic adsorbent to remove the unwanted species, the adsorbent must be regenerated periodically. It is known to use hydrogen diluted with nitrogen to reactivate the adsorbent each time the capacity of the adsorbent to remove the unwanted species has reached the end of its cycle time. Among the unwanted species set forth above, the nickel-based catalytic adsorbent has the least capacity for carbon dioxide and the highest capacity for oxygen. During a normal purification cycle, the carbon dioxide is usually the first species to break out of a nickel-based purifier bed. According to current practice, as soon as the carbon dioxide breakthrough occurs, the adsorbent bed is taken off-stream and is regenerated using a reduction gas, such as a dilute (1 to 2%) hydrogen in nitrogen mixture. The use of the hydrogen/nitrogen mixture requires a nitrogen purge after the unwanted species are desorbed or removed from the nickel-based catalytic adsorbent. Purging results in a long time interval before the catalytic bed can be put back in service because of the residual hydrogen from the regeneration step. The long purge also increases the cost for producing UHP nitrogen by this method. It has been discovered that with the conventional nickel-based catalyst adsorbent systems, depending upon the geometry of adsorbent bed, one or more interim regenerations using UHP nitrogen can be employed before it is necessary to use a hydrogen/nitrogen mixture reduction regeneration. Thus the present invention provides regeneration of nickel-based catalytic adsorbent beds using a process wherein, depending upon the geometry of the adsorbent bed, at least one periodic regeneration of the adsorbent by the well-known hydrogen reduction technique can be replaced with a process wherein the adsorbent bed is heated to a temperature of at least 300°F (150°C) followed by flowing product gas having a purity of at least 99.9999% through said bed while maintaining said bed at a temperature of at least 300°F (150°C) for a period of time to remove a major portion of the adsorbed species from said adsorbent bed followed by cooling said adsorbent bed to a temperature no higher than 120°F (50°C). The present invention will be discussed and illustrated in relation to the production of ultra-pure nitrogen. However, any gas purification process that uses similar catalytic adsorbent techniques, can use the process of the present invention with similar results. For example, similar purifiers are used in the production of ultra-high purity argon and helium so the process is applicable to these gases also. Once the detection of carbon dioxide breakthrough occurs, the catalyst bed is taken out of service and subjected to a step wherein it is heated to a temperature of at least 300°F (150°C) and preferably within a range of 300°F (150°C) to 572°F (300°C). This is followed by flowing UHP nitrogen, without addition of hydrogen, through the catalytic adsorbent bed while maintaining a temperature in the bed of at least 300°F (150°C) and preferably within the range of 300°F (150°C) to 572°F (300°C) for a period of time to desorb or remove the unwanted species from the catalytic adsorbent bed. Thereafter, the bed is cooled to a temperature of no greater than 120°F (50°C) and at that time is ready to be placed in service. Normally, two or more beds would be available to permit the continuous purification of the cryogenically produced nitrogen by having one bed on-stream effecting removal of unwanted species from the cryogenically produced nitrogen while the other bed or beds are being regenerated, or have been regenerated and are idled waiting for reengagement in the process. It is preferred that the product gas is flowed through said bed at a rate of at least 4% of the rate of flow of the product gas stream being subject to removal of unwanted species. Suitably, the adsorbent bed is held in an atmosphere of ultra-high purity product gas after said cooling step. Examples of suitable catalytic adsorbent are nickel-alumina and nickel-Kieselguhr catalysts. The present invention also provides a process for minimizing the number of cycles using hydrogen to regenerate a nickel-based catalytic adsorbent used to remove unwanted species from a cryogenically produced ultra-high purity product gas stream by using at least one interim regeneration comprising the steps of heating said adsorbent to a temperature of at least 150°C (300°F); flowing said product gas having a purity of at least 99.9999% through said adsorbent while maintaining said adsorbent at a temperature of at least 150°C (300°F) for a period of time to remove a major portion of the adsorbed species from said adsorbent; and cooling said adsorbent to a temperature of no higher than 50°C (120°F). In another aspect, the invention provides a process for removal of parts-per-million quantities of unwanted species from a cryogenically produced ultra-high purity gas stream by passage through a bed of nickel-based catalytic adsorbent with periodic generation of the bed using hydrogen reduction, characterized in that the bed is regenerated at least once between at least one successive pair of said hydrogen regenerations by an interim regeneration of the invention. The following Examples illustrate the present invention. Example 1 After a conventional regeneration with hydrogen, a purifier packed with 3.66 lb (1.66 kg) of a commercial Nickel-Alumina (Ni/Al 2 O 3 ) catalyst, Catalyst A, was challenged with 2.4 ppm CO and 3.6 ppm O 2 in a nitrogen gas flow of 3.5 scfm. (standard cubic feet per minute; 0.1 standard cubic meters per minute (scmm)). The purifier was operated at 80°F (27°C) and 80 psig (550 kPag) inlet pressure. The packed bed height was 48 inches (1.2 m). Since CO 2 , a product from the chemical reaction between CO and O 2 , is the first impurity to break out of the catalytic adsorber, the purifier has to be regenerated once CO 2 breaks through the packed bed. A 24-hour regeneration procedure without hydrogen according to the following scheme was tested: Time Duration, hours 1. Heat up to 400°F (205°C) 1 2. Hot Purge with UHP Nitrogen (no H 2 ) at 400°F (205°C) 16 3. Cooling under UHP Nitrogen to 80°F (27°C) 7 Total hours = 24 The regeneration flow was 0.28 scfm (0.008 scmm) nitrogen. Three successive cycles were performed. The results are summarized in Figure 1 where the CO 2 breakthrough time (defined at 10 ppb CO 2 in the stream) is plotted against bed height. As shown in Fig. 1, at 18 inches (45 cm) of bed height, the breakthrough time reduced slightly from 12 hours to 10.3 hours and then to 9.2 hours with successive regenerations. In all cases, no CO 2 breakthrough at the exit (45 inches; 1.15 m) of the bed was observed for the 24-hour cycle operation. The original capacity can be recovered with a conventional regeneration with hydrogen. Example 2 A similar experiment was conducted with a commercial Nickel-Kieselguhr catalyst, Catalyst B. A reactor of the same dimension as in Example 1, was loaded with 6.84 lb (3.10 kg). of Catalyst B and activated with a conventional reduction procedure. As with Example 1 the purifier was operated at 80°F (27°C) and 80 psig (550 kPag) inlet pressure, challenged with 2.4 ppm Co. And 3.6 ppm O 2 in a nitrogen gas flow of 3.5 scfm (0.1 scmm). Four consecutive breakthrough runs were made with three interim regenerations without using hydrogen. The interim regeneration procedure was the same as described in Example 1. The results are depicted in Figure 2. Again, the CO 2 capacity, which is indicated by the breakthrough time, decreases slightly with successive regenerations without hydrogen. However, the purifier effectively removes the impurities as no CO 2 breakthrough is observed at the exit of the purifier. Normally, a conventional regeneration procedure requires four steps. For a 72-hour operating cycle, the following regeneration is typical: Time Duration, hours 1. Heat up to 400°F (205°C) 4 2. Reduction (with an H 2 containing gas) at 400°F (205°C) 8 3. Hot Purge with UHP Nitrogen at 400°F (205°C) 48 4. Cooling under UHP Nitrogen to 80°F (27°C) 12 Total hours = 72 During the entire regeneration process, a flow of high purity nitrogen at a rate of 4 to 8% of treated gas flowrate is normally required. This invention makes it possible to use several interim regenerations before a conventional regeneration is needed. The interim regenerations, while replacing conventional regenerations, maintain the same cycle time, and require no hydrogen. Operational savings can be realized by alleviating the reduction step and shortening the purge step. Applying the regeneration method of the present invention results in the elimination of the reduction step. In addition, the duration of the hot purge step can be significantly reduced. An interim regeneration procedure for a typical 72-hour cycle can be as follows: Time Duration, hours 1. Heat up to 400°F (205°C) 4 2. Hot Purge with UHP Nitrogen (no H 2 ) at temperature 400°F (205°C) 24 3. Cooling under UHP Nitrogen to 80°F (27°C) 12 4. Idle 32 Total hours = 72 The idle step is needed to maintain the 72-hour cycle. With the interim regeneration, no hydrogen is required and the nitrogen consumption is greatly reduced. Using the process of the present invention wherein one or more interim regeneration is effected without the use of hydrogen can result in significant savings to the operator of a facility producing UHP nitrogen from cryogenically produced nitrogen. For example, assuming a conventional regeneration is required after five interim regenerations, 37% nitrogen and 83% of the hydrogen used in the conventional regeneration scheme can be saved. Thus for a typical 50,000 scfh (1,400 scmh) nitrogen purification process which uses 8% of the flow during regeneration, the savings in gas consumption are: UHP N 2 saved every 6 cycles (432 hours) = 8,000,000 scf (225,000 scm) UHP H 2 saved every 6 cycles (432 hours) =20,000 scf. (570 scm) Therefore, this translates to a yearly saving of 160,000,000 scf (4,500,000 scm) nitrogen and 400,000 scf (11,500 scm) hydrogen.

Claims: A process for regenerating a nickel-based catalytic adsorbent bed used to remove parts-per-million quantities of unwanted species from a cryogenically produced ultra-high purity product gas stream by regeneration using hydrogen reduction; characterized in that after a regeneration using hydrogen, said bed is regenerated at least once prior to a subsequent hydrogen regeneration by: heating said adsorbent bed to a temperature of at least 150°C (300°F); flowing said product gas having a purity of at least 99.9999% through said bed while maintaining said bed at a temperature of at least 150°C (300°F) for a period of time to remove a major portion of the adsorbed species from said adsorbent bed; and cooling said adsorbent bed to a temperature of no higher than 50°C (120°F). A process according to Claim 1, wherein said product gas is selected from argon and helium. A process according to Claim 1, wherein said product gas is nitrogen. A process according to any one of the preceding claims, wherein said adsorbent bed is heated to a temperature of from 150°C (300°F) to 300°C (572°F). A process according to Claim 4, wherein said bed is maintained at a temperature of from 150°C (300°F) to 300°C (572°F) during said time said product gas is flowing through said bed. A process according to any one of the preceding claims, wherein said product gas is flowed through said bed at a rate of at least 4% of the rate of flow of the product gas stream being subject to removal of unwanted species. A process according to any one of the preceding claims, wherein said adsorbent bed is held in an atmosphere of ultra-high purity product gas after said cooling step. A process according to any one of the preceding claims, wherein said catalytic adsorbent is selected from nickel-alumina and nickel-Kieselguhr catalysts. A process for minimizing the number of cycles using hydrogen to regenerate a nickel-based catalytic adsorbent used to remove unwanted species from a cryogenically produced ultra-high purity product gas stream by using at least one interim regeneration comprising the steps of heating said adsorbent to a temperature of at least 150°C (300°F); flowing said product gas having a purity of at least 99.9999% through said adsorbent while maintaining said adsorbent at a temperature of at least 150°C (300°F) for a period of time to remove a major portion of the adsorbed species from said adsorbent; and cooling said adsorbent to a temperature of no higher than 50°C (120°F). A process according to Claim 9, wherein said product gas and/or interim regeneration conditions are as defined in any one of Claims 2 to 7 and/or the catalytic adsorbent is as defined in Claim 8. A process for removal of parts-per-million quantities of unwanted species from a cryogenically produced ultra-high purity gas stream by passage through a bed of nickel-based catalytic adsorbent with periodic generation of the bed using hydrogen reduction, characterized in that the bed is regenerated at least once between at least one successive pair of said hydrogen regenerations by an interim regeneration as defined in Claim 9. A process according to Claim 11, wherein said interim regeneration(s) is (are) as defined in Claim 10.

Inventors: HSIUNG THOMAS HSIAO-LING, WALLACE JOHN BRUCE JR, HSIUNG, THOMAS HSIAO-LING, WALLACE, JOHN BRUCE, JR.
Applicants: AIR PROD & CHEM, AIR PRODUCTS AND CHEMICALS, INC.
Application year: 1997
Main classification: B01J23
IPC codes: B01J23, B01J20, B01J38