CATALYSTS FOR THE FULL OXIDATION OF VOLATILE ORGANIC COMPOUNDS

Abstract: A catalyst for the full oxidation of volatile organic compounds (VOC), particularly hydrocarbons, and of CO to CO2, which comprises a compound having the formula: A2B3O6+/-d, where A is an alkaline-earth metal, an alkaline metal, a lanthanide, or a solid solution thereof, B is a transition metal, an element of group III, or a solid solution thereof, and d has a value between 0 and 1; and a method for the full oxidation of volatile organic compounds using the catalyst.

Description: CATALYSTS FOR THE FULL OXIDATION OF VOLATILE ORGANIC COMPOUNDS Technical Field The present invention relates to catalysts f or the f u l l oxidat ion o f vo l at i l e o rgani c compounds ( VOC ) , particularly hydrocarbons , and to a method f or the ful l oxidation of volatile organic compounds (VOC ) by using said catalysts . Background Art The total combustion of VOC to C0 2 and H 2 θ becomes necessary in view of the toxicity and environmental impact of most unburnt VOC. The goal is to minimize both the release of VOC into the atmosphere and the formation of CO, which is also a toxic component. The catalysts mostly used for VOC combustion are: a) catalysts based on noble metals, which are characterized by a high cost but by excellent performance in terms of VOC conversion, said catalysts operating at temperatures between 200 and 450°C according to the reactivity of the compound; b) catalysts based on mixed oxides, typically chromites of copper or of other metals, or barium hexaaluminate, which are characterized by a lower cost but are active in more drastic conditions (temperatures between 400 and 600°C). This second class of catalysts is also used for catalytic combustors for power generation units. In this case, they operate at temperatures above 900°C. Conventional catalysts used for the combustion of VOC are not free from drawbacks, i.e., high cost (for those based on noble metals) and poor activity (for the second class, accordingly requiring operation at higher temperatures, in conditions in which morphologic or structural transformations are facilitated). Disclosure of the Invention A principal aim of the present invention is to eliminate the drawbacks of conventional catalysts for the oxidation of VOC, particularly catalysts for the full oxidation of VOC. This aim and other objects which will become apparent hereinafter from the following detailed description of the invention are achieved by catalysts according to the present invention, which comprise one or more crystalline compounds having the formula A 2 B 3°6±d where A is an alkaline-earth metal, an alkaline metal, a lanthanide, or a solid solution thereof, B is a transition metal, an element of group III, or a solid solution thereof, and d has a value between 0 and 1. Advantageously, A is chosen from the group constituted by barium, cesium, potassium, strontium, and solid solutions thereof. Conveniently, B is chosen from the group constituted by copper, nickel, manganese, iron, palladium, titanium, aluminum, gallium, zinc, cobalt, and solid solutions thereof. Examples of catalysts according to the invention, wherein A is a solid solution of the above-mentioned cations, include compounds having the formula ( Ba 2 _ χ Sr χ ) Cu 3 0 6±d with values of x up to 0. 75. Othe r exampl e s o f c atalyst s acc o rding to the invention , wherein B is a so lid so l ution o f the above- mentioned cations, have the formula ( Ba 2 Cu 3 _ y Pd y )0 6±d with y up to 0.33 ; Ba 2 (Cu 3 _ y Ni y )0 6±d with y up to 1.0. Methods for preparing the compounds included in the catalysts according to the present invention are disclosed in Italian patent application BO 96 A 000063. Said patent application describes the use of these compounds to fix gases, composite materials comprising said compounds, films made by said compounds, gas fixing devices comprising said compounds, and electrical and optical gas concentration sensors comprising said compounds. The catalysts for catalytic combustion according to the present invention are characterized by a high activity, comparable with that provided by the more expensive noble metals, by a high resistance to temperature and to extreme operating conditions, by low cost and easy production even in the form of compounds and thin films. Moreover, differently from any material hitherto known, they are totally selective for carbon dioxide, C0 2 , with respect to carbon monoxide, CO. This means that in any operating condition for the catalysts according to the present invention the only carbon oxide produced by the reaction is C0 2 . The present invention also relates to methods for the full oxidation of VOC which use the catalysts according to the present invention. The methods for the full oxidation of VOC according to the present invention relate to the full oxidation of VOC in combustion chambers or in afterburning chambers or in combustion-gas chambers. The oxidation reaction occurs in a fixed bed or in a fluidized bed. The catalysts according to the present invention lead to full oxidation of VOC. In this manner, the gas mixture produced by the oxidation of the VOC does not contain carbon monoxide but contains only carbon dioxide. In this manner, the operations for eliminating carbon monoxide, and the known negative consequences of its presence in the environment, are avoided. Moreover, by oxidizing the carbon monoxide to carbon dioxide, the full potential of the VOC oxidation reaction is utilized, with obvious advantages in terms of energy. The Applicants have found that the total VOC oxidation reaction in the presence of the catalysts according to the invention occurs with a high conversion of VOC even at low temperatures. Moreover, the Applicants have found that the catalysts according to the present invention allow full oxidation of VOC even in conditions entailing a significant oxygen deficit. Besides, it has been found that the catalytic activity of the catalysts according to the present invention is not negatively affected by prior heating under reaction up to high temperatures (for example up to 920°C) and cooling to ambient temperature. Moreover, analysis of reaction selectivity data suggests that the catalysts according to the present invention are capable of directly converting CO to C0 2 at temperatures above 250°C and in the presence of even minimal oxygen concentrations. The catalysts according to the present invention and the oxidation method according to the present invention will be described in greater detail hereinafter with examples which are presented only by way of non-limitative example. Example 1 Catalytic combustion of methane From a molecule-reactivity standpoint, methane is to be considered as difficult to oxidize. The required reaction conditions are extremely drastic if compared with other paraffins, olefins, or volatile organic compounds. Tests that have been conducted have shown that the compound according to the invention is capable of oxidizing methane at relatively low temperatures: this is an indicator of the high full-oxidation ability of the - compound according to the invention. As regards other volatile organic compounds, full combustion is thought to occur at temperatures that are significantly lower than those observed for methane. These indications have been confirmed by the tests conducted with butane and can therefore be extended to the other VOC. A catalyst containing Ba 2 Cu 3 0 6 was used in tests for the catalytic combustion of methane. The tests are conducted in a fixed-bed quartz microreactor with a diameter of 4 mm, which contains 500 mg of catalysts in granules having dimensions between 20 and 30 mesh. The catalyst is a composite material constituted by an inert porous substrate (Al 2 0 3 ) which contains 3.5% by weight of active compound (17.5 mg) . Methane and air are fed to the reactor so that the methane concentration is equal to 2% by volume in the first test and equal to 4% by volume in the second test. The tests are conducted at atmospheric pressure and at a space velocity, expressed as GHSV (gas hourly space velocity; hourly fed volumetric flow-rate/volume or weight of catalyst), of 80,000 cirr/g.hour in the first test and of 40,000 cm 3 /g.hour in the second test. The mixture of reaction products was analyzed by gas chromatography. The only products formed in both tests were carbon dioxide and water. The results of the first and of the second tests are given respectively in figures 1 and 2 , where the te rm " convers ion " re l ate s to t he pe rcentage in mo l e s o f converted methane with respect to the mol es of supplied methane . The expression "set temperature" relates to the temperature of the mixture of gases fed to the reactor and the expression "measured temperature " re lates to the tempe rat ure o f the gas mixture at the out l e t o f the reactor , which is considered equal to the temperature of the catalyst . Example 2 Combustion test in a thermal cycle The catalyst according to the example was used in a catalytic methane combustion test carried out in a thermal cycle. The test was conducted in a quartz fixed-bed microreactor with a diameter of 4 mm, which contained 500 mg of catalyst (equal to the catalyst of Example 1) in granules having dimensions between 20 and 30 mesh. Methane and air are fed to the reactor so that the methane concentration is equal to 2% by volume. The test is conducted at atmospheric pressure and at a space velocity, expressed as GHSV, of 90,000 cm 3 /g h. Catalytic activity was analyzed as a function of the temperature and therefore the reaction temperature was increased to 920°C and the catalyst was kept in these conditions for 5 hours. Finally, the system was cooled to 400°C and catalytic activity was analyzed as a function of temperature. The mixture of reaction products was analyzed by gas chromatography. The only products that formed were carbon dioxide and water. The results of the activity tests are given in Table A, where the term "conversion" relates to the percentage of moles of converted methane with respect to the moles of fed methane. Table A Test in thermal cycle Temperature Conversion Conversion (C) 1st cycle aft :er 5h <%) at 920°C (%) 400 0 0 450 17 16 500 19 19 550 37 38 At the end of the thermal cycle, activity was unchanged and the discharged catalyst showed a surface area of 116 m 2 /g, unchanged with respect to the initial one, which was of 122 m /g. This test demonstrates the good thermal stability of the catalysts used in the present invention. Example 3 Tests for the combustion of methane in reducing conditions The catalyst according to the example was used in tests for the combustion of methane in oxygen deficit conditions. The tests were conducted in a fixed-bed quartz microreactor having a diameter of 4 mm, which contained 200 mg of catalyst (equal to the catalyst of Example 1) in granules measuring 20 to 30 mesh. The reactor is fed with methane and air so that the ratio between methane and oxygen is 2 (vol/vol) in the first test and 5 (vol/vol) in the second test. The test is conducted at atmospheric pressure and at a space velocity, expressed as GHSV, of 40,000 cm /g h. The mixture of the reaction products was analyzed by gas chromatography. The only resulting products were carbon dioxide and water. The results of the activity tests are listed in figures 3 and 4, where the term "conversion" relates to the percentage of converted methane moles with respect to the fed methane moles. The complete absence of CO in methane combustion tests conducted in oxygen deficit conditions is particularly significant. The combustion of methane at low temperature and with amounts of oxygen that are well below the stoichiometric ratio generally leads to the formation of incomplete combustion products, such as CO. The complete absence of CO therefore ensures that only full combustion products, such as C0 2 and H 2 0, are formed even in drastic conditions and outside the conventional utilization ranges. This result is particularly relevant since with catalysts currently in use it is necessary to operate with an abundant excess of oxygen in order to facilitate combustion to C0 2 . The claimed catalysts can operate with a low oxygen/VOC ratio; this makes the conversion efficiency independent of the oxidizing properties of the reaction atmosphere, and this is an undoubtedly advantageous fact. Example 4 Catalytic combustion of n-butane The tests were conducted in a laboratory flow reactor operating at atmospheric pressure. 2 g of catalyst, containing 70 mg of Ba 2 Cu 3 0 6 on a porous inert substrate (Al 2 0 3 ) with particles having a diameter of about 0.5 mm, are loaded. A mix constituted by n-butane (1.7% molar) in air is fed so as to provide a contact time (expressed as ratio between the catalyst volume and the volumetric feed flow-rate measured in normal conditions) which can vary between 0.7 and 4.4 seconds (results shown in Table B), or a contact time set to 4.4 seconds and a temperature that can vary between 320 to 480°C (results shown in Table B). The n-butane ignition temperature can be extrapolated from the table data and is between 280 and 300°C. Table B. Oxidation of n-butane Contact Temperature Conversion time (s) (°C) to n-C 4 H 10 (%) 0.7 340 18 1.5 340 32 2.2 340 39 2.9 340 45 3.6 340 51 4.4 340 55 4.4 320 42 4.4 340 55 4.4 360 62 4.4 380 70 4.4 400 77 4.4 420 86 4.4 440 94 4.4 460 100 Total lack of carbon monoxide in the combustion products, constituted exclusively by H 2 0 and C0 2 , is observed. Table B lists the values of the percentage conversion of n-butane (reacted moles/fed moles) and the yield in C0 2 (produced moles of C0 2 /(supplied moles of n-butane*4 ) ) . The experimental characteristics of this example reduce conversion efficiency with respect to the examples given for methane oxidation. Laminar flow and limitation by self- diffusion of the reaction products in fact penalize the efficiency, which nonetheless remains very high. The catalysts according to the present invention and the total VOC oxidation method according to the present invention can be used with good results for gaseous organic compounds or for organic compounds that vaporize at low temperature, achieving complete combustion at low temperature. The C0 2 selectivity of the catalysts according to the present invention is a unique characteristic. The oxidation of VOC, particularly hydrocarbons with catalysts that are not specific for combustion, usually leads to the formation of both CO and C0 2 . Both products are ther odynamically facilitated in the conditions normally used, and their ratio is therefore usually conditioned by kinetic factors. Accordingly, the specificity of the catalyst in the formation of C0 2 is linked to the characteristics of the active centers. C0 2 is in fact a primary product, as demonstrated by tests conducted by varying the contact time, and therefore is not the result of the intermediate formation of CO. It is also fair to assume that primary carbon monoxide, i.e., the carbon monoxide that is not produced by the partial oxidation of VOC, is efficiently converted to carbon dioxide at temperatures above 250°C and in the presence of low oxygen concentrations . The catalysts according to the present invention and the process for the full oxidation of gaseous organic compounds can be used to reduce or eliminate many noxious components from the combustion gases generated in any manner, for example from very large scale facilities for generating electric power down to small combustors for domestic use, including important applications in the engine field and in the field of vehicles with internal- combustion engines. The selectivity of the C0 2 yield also makes the use of the catalysts according to the present invention particularly interesting in combustors for closed spaces (gas stoves, water heaters for sanitary use, cooking devices, etcetera) where the presence of CO in the combustion products is notoriously a serious health hazard.

Claims: CLAIMS 1. A catalyst for the full oxidation of volatile organic compounds (VOC), particularly hydrocarbons, and of CO to C0 2 , comprising a compound having the formula A 2 B 3 0 6±d where A is an alkaline-earth metal, an alkaline metal, a lanthanide, or a solid solution thereof; B is a transition metal, an element of group III, or a solid solution thereof; and d has a value between 0 and 1. 2. A catalyst according to claim 1, characterized in that A is chosen from the group constituted by barium, cesium, potassium, strontium, a lanthanide, and solid solutions thereof. 3. A catalyst according to claim 1, characterized in that B is chosen from the group constituted by copper, nickel, manganese, iron, palladium, titanium, aluminum, gallium, zinc, cobalt, and solid solutions thereof. 4. A catalyst according to claim 1, characterized in that said compound has the formula Ba 2 Cu 3 0 6±d . 5. A catalyst according to claim 1, characterized in that said compound has the formula (Ba 2 _ χ A χ )Cu 3 0 6±d where A is an alkaline or an al kal ine-earth metal or a lanthanide. 6. A catalyst according to claim 1, characterized in that said compound has the formula (Ba 2-x Sr χ) Cu 3°6±d' ° < x < °- 75 7. A catalyst according to claim 1, characterized in that said compound has the formula B a 2< Cu 3-y B y>°6±d' 0 < y < 1 where B is a transition metal or an element of group III. 8. A catalyst according to claim 1, characterized in that said compound has the formula Ba 2 (Cu 3 _ y Ni y )0 6±d , 0 < y < 1 9. A catalyst according to claim 1, characterized in that said compound has the formula Ba 2 (Cu 3 _ y Pd y )0 6±d , 0 < y < 0.33 10. A composite catalyst constituted by one or more catalysts according to claims 1 to 9, supported in any manner on other materials, both inert and functional, in the form of composite material or thin film. 11. A method for the full oxidation of volatile organic compounds, particularly hydrocarbons, characterized in that a catalyst according to one of claims 1 to 10 is used. 12. A method for converting carbon monoxide to carbon dioxide , characterized in that a catalyst according to claims 1 to 10 is used .

Inventors: CALESTANI GIANLUCA, CAVANI FABRIZIO, FORNASARI GIUSEPPE, MATACOTTA FRANCESCO CINO, CALESTANI, GIANLUCA, CAVANI, FABRIZIO, FORNASARI, GIUSEPPE, MATACOTTA, FRANCESCO, CINO
Applicants: CALESTANI GIANLUCA, CAVANI FABRIZIO, CONSIGLIO NAZIONALE RICERCHE, FORNASARI GIUSEPPE, MATACOTTA FRANCESCO C, UNIV BOLOGNA, CALESTANI, GIANLUCA, CAVANI, FABRIZIO, CONSIGLIO NAZIONALE DELLE RICERCHE, FORNASARI, GIUSEPPE, MATACOTTA, FRANCESCO, CINO, UNIVERSITA' DEGLI STUDI DI BOLOGNA
Application year: 1997
Main classification: B01D53
IPC codes: B01D53, B01J20, B01J23, C01G1, C01G3, C01G53, C01G55