Primed polymer films having improved adhesion characteristics and processes for making films

Abstract: This invention covers a film base wherein polymers forming a polymeric film surface and selected from polyesters, polyolefins and polyamides are coated with an adhesion enhancing primer coating containing (a) a functionalized α-olefin containing copolymer; and (b) a crosslinking agent selected from the group consisting of amino formaldehyde resins, polyvalent metal salts, isocyanates, blocked isocyanates, epoxy resins and polyfunctional aziridines; and wherein the adhesion enhancing primer coating is applied to the polymeric film surface and reacted, at elevated temperatures with newly generated polymeric film surfaces formed during uniaxial or biaxial stretching and heat setting.

Description: FIELD OF THE INVENTION The present invention generally relates to chemically modified base polymeric films or substrates, and more particularly to primer coatings for polymeric films which provide coated films having improved adhesion characteristics. These films may be used for a multitude of purposes including their use as food packaging films, films for supporting metallic substances or thermal transfer media inks and ink compositions. BACKGROUND OF THE INVENTION Polymer films or sheets, more particularly polyester films or sheets, especially those of polyethylene terephathalate (PET), are widely used in such applications as packaging, decorative articles, magnetic recording media, and photographic film. In such applications, the polyester film is printed or coated with a variety of materials, which must be applied as a uniform and continuous layer and must adhere well to the base polymer. However, PET and similar polymers do not have good receptivity to most surface-treating compositions. This problem has long been recognized in the prior art, and various methods have been developed to increase the polyester film's surface receptivity. A good discussion of the prior art in this area can be found in Posey et al., U.S. Pat. No. 4,476,189 issued October 9, 1984. Nevertheless, most primers used commercially are oriented to specific end uses and are suitable only for either hydrophobic or hydrophilic surface treatment. U.S. Pat No. 4,476,189 discloses a primed water-dispersible copolyester of terephthalic acid, an aliphatic dicarboxylic acid, and an aromatic sulfonated monomer with an alkylene glycol. The resultant primed polyester film is said to provide excellent adhesion to many subsequently applied aqueous or solvent-based coating. The presence of the aromatic sulfonated monomer, which can be sodium sulfoterephathalic acid or a similar sulfonated derivative of a phthalic acid, is a shortcoming because such starting materials are not widely commercially available and therefore are expensive. Another potential shortcoming is that adhesion to the resultant primed polyester film can be humidity or moisture-sensitive. It is thus desirable to provide a primed polymer film or sheet which could be manufactured from inexpensive, readily available materials. It is further desireable to achieve a resultant primed polyester film to which adhesion is not humidity- or moisture-sensitive. EP 518647 (Imperial Chemical Industries plc) discloses a polymeric film comprising a substrate layer of polymeric material having on at least one surface thereof a coating layer formed from a composition comprising a layer mineral and a cross-linking agent, the coating layer comprising greater than 10% and less than 90% by weight of the layer of the layer mineral, and greater than 10% and less than 90% by weight of the layer of a resin derived from the cross-linking agent. SUMMARY OF THE INVENTION It has been found that application of certain primer coatings to polymer films, while in their amorphous or semi-oriented state, followed by axially or biaxially stretching these coated films at temperatures of at least 80°C and heat setting at temperatures of at least 130°C or higher results in improved adhesion of the primer coatings to the film base which in turn results in primed films having improved adhesion to various subsequently applied layers or coatings. Accordingly, the present invention provides for a film structure, comprising: (i) a polyester polymer such as polyethylene terephthalate, polyethylene napthylene; wherein said polymer forms a polymeric film surface; and (ii) an adhesion enhancing primer coating having a thickness of from 0.02 to 1 micron consisting essentially of: (a) functionalized α-olefin containing copolymers, preferably acid funtionalized α-olefin containing copolymers, selected from ethylene/acrylic acid copolymers; ethylene/methacrylic acid copolymers; ethylene/vinylacetate/acrylic acid terpolymers; ethylene/methacrylamide copolymers; ethylene/glycidyl methacrylate copolymers; ethylene/dimethylaminoethyl methacrylate copolymers; ethylene/2-hydroxyethyl acrylate copolymers; propylene/acrylic acid copolymers; and (b) crosslinking agents selected from amino formaldehyde resins, polyvalent metal salts, isocyanates, blocked isocyanates, epoxy resins and polyfunctional aziridines; wherein (ii) is applied as a primer to the polymeric film surface, preferably in its amorphous or semi-oriented state; and reacted with newly generated polymeric film surfaces formed during uniaxial or biaxial stretching and heat setting; and (iii) a layer or coating selected from vacuum deposited metal; metal oxide; polyethylene; ethylene acrylic acid copolymers; ethylene vinyl acetate copolymers; ethylene vinyl acetate copolymers with various waxes or tackifiers; polyvinyl alcohol; ethylene copolymers and wax based thermal transfer media inks; wherein layer (iii) is in contact with layer (ii) on its surface away from layer (i) . Preferably the stretching occurs at temperature of at least 80°C. This coated or primed film base has improved adhesion of (ii) to (i) which results in improved adhesion to subsequent coatings such as vacuum deposited metal; metal oxide; polyethylene; ethylene acrylic acid copolymers; ethylene vinyl acetate copolymers; ethylene vinyl acetate copolymers with various waxes or tackifiers such as glycerol esters of gum rosin, wood rosin or tall oil rosin; pentaerythritol ester of gum or wood rosin or partially hydrogenated gum or wood rosin; polyterpene resin; polyisobutylene; butadiene/styrene rubber, isobutylene/isoprene copolymer; etc,; polyvinyl alcohol; ethylene copolymers such as ethylene/methacrylate or ethylene ethyl acrylate and wax based thermal transfer media inks. In another embodiment of the invention is described a process for preparing a film base having improved adhesion characteristics comprising the following steps: (1) providing an amorphous polyester polymer, such as polyethylene terephthalate, polyethylene napthalate; wherein said polymer forms a polymeric film surface; (2) applying to the polymeric film surface an adhesion enhancing primer coating having a thickness of from 0.02 to 1 micron consisting essentially of: (a) a functionalized α-olefin containing copolymer, preferably an acid functionalized α-olefin containing copolymer, selected from ethylene/acrylic acid copolymers; ethylene/methacrylic acid copolymers; ethylene/vinylacetate/acrylic acid terpolymers; ethylene/methacrylamide copolymers; ethylene/glycidyl methacrylate copolymers; ethylene/dimethylaminoethyl methacrylate copolymers; ethylene/2-hydroxyethyl acrylate copolymers; propylene/acrylic acid copolymers; and (b) a crosslinking agent selected from of amino formaldehyde resins, polyvalent metal salts, isocyanates, blocked isocyanates, epoxy resins and polyfunctional aziridines; and (3) drying the polymeric film surface having the applied adhesion enhancing primer coating; (4) reacting the coating comprising (a) and (b) with the newly generated polymeric film surfaces formed during uniaxial or biaxial stretching and heat setting; and (5) applying a layer or coating selected from vacuum deposited metal; metal oxide; polyethylene; ethylene acrylic acid copolymers; ethylene vinyl acetate copolymers; ethylene vinyl acetate copolymers with various waxes or tackifiers; polyvinyl alcohol; ethylene copolymers and wax based thermal transfer media inks; wherein said coating or layer is in contact with the adhesion enhancing primer coating layer, on its surface away from the polymeric film surface. DETAILED DESCRIPTION OF THE INVENTION The film base of the invention comprises (i) a polyester polymer, such as polyethylene terephthalate, polyethylene napthalate; wherein said polymer forms a polymeric film surface; (ii) a specified adhesion enhacing primer coating; and (iii) a specified layer or coating. The coating is applied to the polymeric film surface in its amorphous or semi-oriented state, and reacted with newly generated polymeric film surfaces formed during uniaxial or biaxial stretching and heat setting. POLYMERIC FILM SURFACE The polymeric film surface should be capable of binding or reacting with an acid-functionalized α-olefin copolymer to form a modified film base. The preferred polymeric film surface comprises polyethylene terephthalate which may be biaxially oriented after or during the application of the specified coating. Useful polyester films may be manufactured from various types of thermoplastic polyester resins, such as polyethylene terephthalate, polytetramethylene terephthalate, polyethylene-2,6-naphthalate, poly-1,4-cyclohexylene dimethyl terephthalate. Polyester copolymers may also be used such as polyethylene terephthalate/isophthalate, polyethylene terephthalate/adipate, polyethylene terephthalate/sebacate, polyethylene terephthalate/sulfoisophthalate, polyethylene terephthalate/azelate. Polymeric films used the practice of this invention may have a thickness of 1 to 500 microns, preferably 10 to 350 microns. ADHESION ENHANCING PRIMER COATING The coating comprises a selected functionalized α -olefin containing copolymer, preferably an acid functionalized α-olefin containing copolymer; a crosslinking agent selected from amino formaldehyde resins, polyvalent metal salts, isocyanates, blocked isocyanates, epoxy resins and polyfunctional aziridines; and a specified layer or coating. Other components such as coating aids, antistatic agents, slip agents, fungicides, etc. may be present in the coating composition. This coating has a thickness of 0.02 to 1 microns. Functionalized α-Olefin Containing Copolymer: Some suitable α-olefins include ethylene, propylene, butene-1 and mixtures thereof or mixtures of these α-olefins with higher α-olefins such as hexene-1, octene-1 and/or decene-1. Some exemplary functional groups include preferably unsaturated carboxylic acids such as acrylic acid, methacrylic acid, itaconic acid, fumaric acid, crotonic acid, and other functionalizing monomers such as methacrylamide, glycidyl methacrylate, dimethylaminoethyl methacrylate, 2-hydroxyethylacrylate. The preferred copolymers used in this invention may have about 60 to 99.9 weight %, preferably 70 to 99 weight %, of the α-olefin containing component and 0.1 to 40 weight %, preferably 1 to 30 weight %, of the unsaturated carboxylic acid. The ratio of the α-olefin to the unsaturated carboxylic acid should be determined by considering the desired properties for the copolymer. The copolymer must assist in enhancing the adhesiveness of the primer coated polymeric film surface to subsequently applied coatings and should also be compatible with any other components present in the coating formulation. The copolymers may have a sufficient number of their acid groups neutralized. Some suitable salts include sodium, magnesium, ammonium and zinc salts, etc. The functionalized α-olefin containing copolymer is selected from ethylene/acrylic acid copolymers; ethylene/methacrylic acid copolymers; ethylene/vinylacetate/acrylic acid terpolymers; ethylene/methacrylamide copolymers; ethylene/glycidyl methacrylate copolymers; ethylene/dimethylaminoethyl methacrylate copolymers; ethylene/2-hydroxyethyl acrylate copolymers and propylene/acrylic acid copolymers. Preferably the functionalized α-olefin containing copolymer is an ethylene/acrylic acid copolymer which may or may not be neutralized and which is commercially available. Some commercially available functionalized α-olefin containing copolymers are sold under the trade names Surlyn® and Primacor®. The functionalized α-olefin containing copolymer may be present in the amount of 30 to 99.9 weight %, preferably 70 to 99 weight %, based on the total weight of the additive free coating solids. Crosslinking Agents: The crosslinking agent present in the coating is selected from amino formaldehyde resins, polyvalent metal salts, isocyanates, blocked isocyanates, epoxy resins and polyfunctional aziridines. Some preferred crosslinking agents include Cymel® 301, Cymel® 350 (aminoformaldehydes) and Ionac PFAZ-322 (polyfunctional aziridine). The crosslinking agent is preferably present in the amount of 0.1 to 70 weight %, more preferably 1 to 30 weight %, based on the total weight of the additive-free coating solids. Additives: Additives such as coating aids, wetting aids such as surfactants, slip additives, antistatic agents can be incorporated in levels from 0 to 50 % based on the total weight of additive-free coating solids. TOP COATS The film base of the invention is coated with a subsequent coating or layer (iii), wherein layer (iii) is in contact with layer (ii) on its surface away from layer (i). The subsequent coating that is applied to the film base of the invention is selected from a vacuum deposited metal; metal oxide; polyethylene; ethylene acrylic acid copolymers; ethylene vinyl acetate copolymers; ethylene vinyl acetate copolymers with various waxes or tackifiers such as glycerol esters of gum rosin, wood rosin or tall oil rosin; pentaerythritol ester of gum or wood rosin, or partially hydrogenated gum or wood rosin; polyterpene resin; polyisobutylene; butadiene/styrene rubber, isobutylene/isoprene copolymer; polyvinyl alcohol; ethylene copolymers such as ethylene/methacrylate or ethylene ethyl acrylate and wax based thermal transfer media inks. PROCESS OF MANUFACTURE The polymer films of the present invention can be manufactured by an extrusion process, such as a cast film or blown film process. In a cast film process, the polymer resin is first heated to a molten state and then extruded through a wide slot die in the form of an amorphous sheet. The sheet-like extrudate is rapidly cooled or "quenched" to form a cast sheet of polyester by contacting and traveling partially around a polished, revolving casting drum. Alternatively, the extrudate can be blown in a conventional blown film process. Regardless of the process however, the polyester sheet is preferably uniaxially or biaxially (preferably biaxially) stretched in the direction of film travel (machine direction) and/or perpendicular to the machine direction (traverse direction), while being heated to a temperature in the range of from about 80°C. to 160°C., preferably about 90°C. to 110°C. the degree of stretching may range from 3.0 to 5.0 times the original cast sheet unit dimension, preferably from about 3.2 to about 4.2 times the original cast sheet dimension. Reaction with the newly generated polymer film surfaces formed during stretching preferably occurs at temperatures about 130° C or higher. The adhesion enhancing coating layer (ii) is preferably applied to the polymeric film surface by conventional coating techniques. Prior to coating the polymeric film surface, the film may be surface-treated in any conventional manner, depending upon the particular application and performance required from the final product. Electric corona discharge is a conventional surface treatment which is commonly performed on polymer films, especially polyester films, to enhance the film's surface qualities, especially its adhesive and printing properties. Electric corona discharge methods and apparatus are described in U.S. Pat. Nos. 3,057,792 and 4,239,973. The films may be subjected to corona treatment followed by application of the coating during the in-line manufacturing process. Drying of the coating may be accomplished before or during stretching. The polymeric film surface can be coated with the primer coating specified herein using any of the well known coating techniques. For example, the film surface may be coated by roller coating, spray coating, gravure coating, slot coating, or extrusion coating preferably gravure or roller coating. The solvent is then removed (dried). Alternatively, the coating may be applied in dry form to give or ultimately give a coated film according to the invention without requiring drying or solvent removal. The heat applied to the film during the subsequent preheating, stretching, and heat-setting stages is generally sufficient to evaporate the coating solvent. Stretching of the film occurs at temperatures of at least 80°C. The coated, oriented polymeric film may then be heat treated for a period of time necessary to crystallize the film (e.g., heat setting). Crystallization imparts dimensional stability and good tensile properties to the polymer film. Oriented polymer film may be heat set at a temperature ranging from 130°C to 240°C, preferably from 180 °C to 235°C, more preferably from 215°C to 235°C. During this step the coating components in (ii) may additionally react with newly generated polymeric film surfaces (i) to give a film base that has improved adhesion of the primer coating (ii) to the polymeric film surface (i), and in turn provides improved adhesion of subsequently applied topcoat coatings (iii) to layer (ii) on its surface away from (i). The coated crystalline, oriented polymer film is generally then wound onto a roll. The subsequent topcoat coatings or layers may be applied by techniques known to one skilled in the art. EXAMPLES The invention will now be illustrated by, but not limited to, the following examples, in which parts and percentages are by weight unless otherwise noted. GLOSSARY: Adcote® 56220 30% solids emulsion of Surlyn® 56220, Morton International Inc., Chicago, IL. Adcote® 50C12 22% solids emulsion of an ethylene acrylic acid polymer, Morton International Inc., Chicago, IL. Adcote® 50T4983 25% solids emulsion of Dow's Primacor® 598Q ethylene acrylic acid resin, Morton International Inc., Chicago, IL. Adcote® 50T4990 35% solids emulsion of Dow's Primacor® 5990 ethylene acrylic acid resin, Morton International Inc., Chicago, IL. Michem Prime® 4983 25% solids emulsion of Dow's Primacor® 5980 ethylene acrylic acid resin, Michelman, Inc., Cincinnati, OH. Crosslinking Agent Solution A: INGREDIENT AMOUNT (GM) Cymel® 301, American Cyanamid Co.,Stamford, CT 158.25 Standapol® A, Henkel Corp., La Grange, Il. 479.50 Aerosol® OT-75, American Cyanamid 87.90 Isopropanol 1319.00 Concentrated ammonium hydroxide 182.00 Ammonium sulfate 7.91 Distilled water 1265.44 Crosslinking Agent Solution B: INGREDIENT AMOUNT (GM) Cymel® 301, American Cyanamid Co., Stamford, CT. 1695.00 Isopropanol 590.00 Dimethyl aminoethanol 221.00 Ammonium sulfate 84.75 Distilled water 1159.25 Crosslinking Agent Solution C: INGREDIENT AMOUNT (GM) PFAZ-322, Sybron Chemical Inc., Birmingham, NY 188.4 Isopropanol 104.0 Distilled water 207.6 The following adhesion enhancing coating solutions were prepared: COATING SOLN # INGREDIENTS AMOUNT (GM) 1 Adcote® 56220 1256.00 (Control) Distilled water 2512.00 2 Adcote®56220 1256.00 Crosslinking Agent solution A 83.30 Distilled water 2428.70 3 Adcote® 56220 1256.00 Crosslinking Agent solution A 83.30 Crosslinking Agent solution B 10.00 Distilled water 2418.70 4 Adcote® 56220 1256.00 Crosslinking Agent solution C 10.00 Distilled water 2502.00 5 Adcote® 56220 1256.00 Crosslinking Agent solution C 20.00 Distilled water 2492.00 5a Adcote® 56220 1256.00 Crosslinking Agent solution C 40.00 Distilled water 2472.00 6 Adcote® 50C12 1713.00 (Control) Distilled water 2055.00 7 Adcote® 50C12 1713.00 Crosslinking Agent solution A 83.30 Distilled water 1971.70 8 Adcote® 50C12 1713.00 Crosslinking Agent solution A 83.30 Crosslinking Agent solution B 10.00 Distilled water 1961.70 9 Adcote® 50C12 1713.00 Crosslinking Agent solution C 10.00 Distilled water 2045.00 10 Adcote® 50C12 1713.00 Crosslinking Agent solution C 20.00 Distilled water 2035.00 11 Adcote® 50T4983 1507.00 (Control) Distilled water 2261.00 12 Adcote® 50T4983 1507.00 Crosslinking Agent solution C 10.00 Distilled water 2251.00 13 Adcote® 50T4983 1507.00 Crosslinking Agent solution C. 20.00 Distilled water 2241.00 14 Adcote® 50T4990 1077.00 (Control) Distilled water 2691.00 15 Adcote® 50T4990 1077.00 Crosslinking Agent solution A 83.30 Distilled water 2607.70 16 Adcote® 50T4990 1077.00 Crosslinking Agent solution A 83.30 Crosslinking Agent solution B 10.00 Distilled water 2597.70 17 Adcote® 50T4990 1077.00 Crosslinking Agent solution C 10.00 Distilled water 2681.00 18 Adcote® 50T4990 1077.00 Crosslinking Agent solution C 20.00 Distilled water 2671.00 19 Michem Prime® 4983 1507.00 (Control) Distilled water 2261.00 19a Michem Prime® 4983 3768.00 (Control) 20 Michem Prime® 4983 1507.00 Crosslinking Agent solution A 83.30 Distilled water 2177.70 21 Michem Prime® 4983 . 1507.00 Crosslinking Agent solution A 83.30 Crosslinking Agent solution B 10.00 Distilled water 2167.70 22 Michem Prime® 4983 3696.00 Crosslinking Agent solution B 40.00 Distilled water 32.00 23 Michem Prime® 4983 3624.00 Crosslinking Agent solution B 80.00 Distilled water 64.00 24 Michem Prime® 4983 1507.00 Crosslinking Agent solution C 10.00 Distilled water 2251.00 25 Michem Prime® 4983 1507.00 Crosslinking Agent solution C 20.00 Distilled water 2241.00 26 Michem Prime® 4983 3624.0 (Comparative Example) Crosslinking Agent solution B 80.0 Distilled water 64.0 All coatings except for sample #26 were applied to cast film via in-line gravure roli coating. The coatings were dried at a temperature of 80°C. after which the cast film was biaxially stretched to 3.3x3.3 times its original size. The coated, dried and stretched film was heat set at 210°C to form primed film samples 1-25. Sample #26 coating was applied to a polyester film which was previously biaxially oriented and heat set (prior to applying the #2 coating). The coated film then was dried at 130°C to form primed film sample #26. The dried films of all examples with the exception of 19a, 22, 23 and 26, had a coating weight of 0.07 g/M 2 . Samples 19a, 22, 23 and 26 had a coating weight of 0.3 g/M 2 . The primed films were heat sealed as follows: Heat Seal A. Treated side of Primacor® 899 backed with Al foil, Dow Chemical, USA, Midland, MI. B. Untreated side of Primacor® 899 backed with Al foil C. GBC type P/N 30000 laminating film, General Binding Corporation, Addison, IL D. 2 mil thick Elvax® 3182 film backed with 2.5 mil (56.25 micron) thick red #650 cellophane tape from 3M, Minneapolis, MN, wherein Elvax® 3182 is an ethylene/vinyl acetate copolymer having 28 weight % of vinyl acetate, manufactured by E. I. DuPont de Nemours and Company, Wilmington, DE The heat sealing for heat seals A, B, and C was done using a Sentinel model 12-ASL heat sealer manufactured by Sencorp Systems Inc., Hyannis, MA. Heat sealing conditions were 50 psi, 250 °F for 5 seconds. The heat sealing for heat seal D was done using a Sentinel model 12ASL/1. Heat sealing conditions were 30psi (jaw pressure), 300°F (148.9°C) for 5 seconds. 180 degree peels were run for heat seals A, B and C using a Suter peel tester (manufactured by Alfred Suter, Co., New York, NY) with 12 in/min peel rate. The primed film side of the heat sealed.sample was fastened to a metal support plate insert in the top jaw. The heat seal layer side was folded back on itself and inserted into the bottom jaw. For heat seal D, 90° peels were run using a Suter peel tester at 12 inches/min. peel rate. The primed film side of the heat sealed sample was inserted into the top jaw. The red tape backed Elvax® 3182 side was inserted into the bottom jaw. The higher the value of the heat seal the better adhesion. The numerical values range from 0 gms/in (no adhesion) to greater than 4000 gms/in (significant adhesion). The preferred values for good primer coating adhesion range from 1000 to 4000 gms/in. Peel Strengths (gms/in) Sample # Heat Seal A Heat Seal B Heat Seal C Heat Seal D 1 y 300 700 1500 0 2 500 500 2000 0 3 600 500 2000 0 4 1300 1300 1500 0 5 1100 1400 2000 2600 5a 2000 2500 4000 2700 x 6 200 150 0 7 1500 1100 2100 x 8 3000 3000 2700 x 9 800 700 200 10 1500 1200 400 11 y 200 200 0 12 1000 700 0 13 1000 900 0 14 y 200 200 0 15 1200 1000 0 16 3500 3000 2500 x 17 700 500 200 18 1100 1000 0 19 y 200 200 0 19a y 80 20 1700 1700 1800 21 3000 1800 2700 x 22 60 23 2600 x 24 1100 1000 0 25 1200 1000 0 26 0 The data also shows that a crosslinking agent is necessary to affect the adhesion.

Claims: A film base, comprising: (i) a polyester polymer wherein said polymer forms a polymeric film surface; and (ii) an adhesion enhancing primer coating having a thickness of from 0.02 to 1 micron consisting essentially of: (a) a functionalized α-olefin containing copolymer selected from ethylene/acrylic acid copolymers; ethylene/methacrylic acid copolymers; ethylene/vinyl acetate/acrylic acid terpolymers; ethylene/methacrylamide copolymers; ethylene/glycidyl methacrylate copolymers; ethylene/dimethylaminoethyl methacrylate copolymers; ethylene/2-hydroxyethyl acrylate copolymers and propylene/acrylic acid copolymers; and (b) a crosslinking agent selected from amino formaldehyde resins, polyvalent metal salts, isocyanates, blocked isocyanates, epoxy resins and polyfunctional aziridines; wherein (ii) is applied to the polymeric film surface, dried and reacted with newly generated polymeric film surfaces formed during uniaxial or biaxial stretching and heat setting; and (iii) a layer or coating selected from vacuum deposited metal; metal oxide; polyethylene; ethylene acrylic acid copolymers; ethylene vinyl acetate copolymers; ethylene vinyl acetate copolymers with various waxes or tackifiers; polyvinyl alcohol; ethylene copolymers and wax based thermal transfer media inks; wherein layer (iii) is in contact with layer (ii) on its surface away from layer (i). The film base of claim 1 wherein the tackifiers are selected from glycerol esters of gum rosin, wood rosin or tall oil rosin, pentaerythritol ester of gum rosin; pentaerythritol ester of wood rosin; pentaerythritol ester of partially hydrogenated gum rosin; pentaerythritol ester of partially hydrogenated wood rosin; polyterpene resin; polyisobutylene; butadiene/styrene rubber, and isobutylene/isoprene copolymer. The film base of claim 1 wherein the funtionalized α-olefin containing copolymers is an acid funtionalized α-olefin containing copolymers. A process for preparing a film base having improved adhesion characteristics comprising the following steps: (1) providing an amorphous polyester polymer, wherein said polymer forms a polymeric film surface; (2) applying to the polymeric film surface an adhesion enhancing primer coating having a thickness of from 0.02 to 1 micron consisting essentially of: (a) a functionalized α-olefin containing copolymer selected from ethylene/acrylic acid copolymers; ethylene/methacrylic acid copolymers; ethylene/vinyl acetate/acrylic acid terpolymers; ethylene/methacrylamide copolymers; ethylene/glycidyl methacrylate copolymers; ethylene/dimethylaminoethyl methacrylate copolymers; ethylene/2-hydroxyethyl acrylate copolymers and propylene/acrylic acid copolymers; and (b) a crosslinking agent selected from amino formaldehyde resins, polyvalent metal salts, isocyanates, blocked isocyanates, epoxy resins and polyfunctional aziridines; and (3) drying the polymeric film surface having the applied adhesion enhancing primer coating; (4) reacting the coating comprising (a) and (b) with newly generated polymeric film surfaces formed during uniaxial or biaxial stretching and heat setting; and (5) applying a layer or coating selected from vacuum deposited metal; metal oxide; polyethylene; ethylene acrylic acid copolymers; ethylene vinyl acetate copolymers; ethylene vinyl acetate copolymers with various waxes or tackifiers; polyvinyl alcohol; ethylene copolymers and wax based thermal transfer media inks; wherein said coating or layer is in contact with the adhesion enhancing primer coating layer, on its surface away from the polymeric film surface. The process of claim 4 wherein, in step (4), reaction occurs at temperatures of about 130°C or greater. The process of claim 4 wherein the tackifier is selected from glycerol esters of gum rosin, wood rosin, or tall oil rosin, pentaerythritol ester of gum rosin; pentaerythritol ester of wood rosin; pentaerythritol ester of partially hydrogenated gum rosin; pentaerythritol ester of partially hydrogenated wood rosin; polyterpene resin; polyisobutylene; butadiene/styrene rubber, or isobutylene/isoprene copolymer. The process of claim 4 wherein the funtionalized α-olefin containing copolymer is an acid funtionalized α-olefin containing copolymer. Use of a modified film base substrate as an adhesion-enhancing base for topcoatings selected from metals, metal oxides, ethylene copolymers or wax-based inks wherein the modified film base comprises (a) a polymeric polyester film; (b) a functionalized α-olefin containing copolymer selected from ethylene/acrylic acid copolymers; ethylene/methacrylic acid copolymers; ethylene/vinyl acetate/acrylic acid terpolymers; ethylene/methacrylamide copolymers; ethylene/glycidyl methacrylate copolymers; ethylene/dimethylaminoethyl methacrylate copolymers; ethylene/2-hydroxyethyl acrylate copolymers and propylene/acrylic acid copolymers; and (c) a crosslinking agent selected from amino formaldehyde resins, polyvalent metal salts, isocyanates, blocked isocyanates, epoxy resins and polyfunctional aziridines; wherein elements (b) and (c) are added to the polymeric film before stretching, dried and heated to form the modified film base with enhanced adhesion properties; and (d) a layer or coating selected from vacuum deposited metal; metal oxide; polyethylene; ethylene acrylic acid copolymers; ethylene vinyl acetate copolymers; ethylene vinyl acetate copolymers with various waxes or tackifiers; polyvinyl alcohol; ethylene copolymers and wax based thermal transfer media inks; wherein layer (d) is in contact with layer (b & c) on its surface away from layer (a).

Inventors: BANDMAN MARC, CHANG CLIFFORD CHENG-SHIOU, PANKRATZ RICHARD PAUL, BANDMAN, MARC, CHANG, CLIFFORD CHENG-SHIOU, PANKRATZ, RICHARD PAUL
Applicants: DUPONT TEIJIN FILMS US LTD, DUPONT TEIJIN FILMS U.S. LIMITED PARTNERSHIP
Application year: 1997
Main classification: C08J7
IPC codes: C09D161, C08J7, B32B27, C09D175, C09D5, C09D123, C09D179, C09D163