Process for producing a heavily nitrogen doped ZnSe crystal

Abstract: In a process for growing a ZnSe crystal by an MBE or MOCVD process, N 2 gas dissociated by electromagnetic waves and vapor In are prepared at a ratio of N:In being 2:1. The atomic gases may be prepared by decomposing InN at a high temperature with electromagnetic irradiation and adding N 2 gas to the decomposed product. The atomic gases are fed onto a substrate in a crystal growth region, so as to simultaneously dope ZnSe with In and N at a ratio of 1:2. A n-type dopant In substitutionally occupying a position of Zn makes a 1:1 couple with a p-type dopant N substitutionally occupying a position of Se, and another one N atom coordinates near the atomic couple and serves as an acceptor. As a result, the acceptor is kept in activated state up to higher concentration, and the ZnSe crystal can be heavily doped with the p-type dopant N.

Description: The present invention relates to a method of producing a p-type ZnSe crystal having low resistivity useful as a material for a blue laser, a blue light emitting device, etc.. ZnSe has been anticipated as a material for a blue laser, a blue light emitting device and so on, since its band gap corresponds to blue luminescence. A ZnSe crystal has been produced so far by a molecular beam epitaxy (MBE) process or a metal organic vapor deposition (MOCVD) process. According to the MBE process, a metal element Zn and a non-metallic element Se are vaporized in an atmosphere at an ultra-high degree of vacuum so as to obtain an intensity of a molecular beam corresponding to vapor pressure of each element, and a crystal is grown up while controlling an atomic layer. On the other hand, thermal decomposition of an organometallic compound is used for production of a ZnSe crystal in the MOCVD process. In order to obtain a p-type ZnSe crystal, it is necessary to dope ZnSe with N during crystal growth. For N doping, gaseous N 2 molecules for instance are dissociated with electromagnetic wave RF, and radical N is introduced to ZnSe epitaxially growing on a substrate. Since ZnSe is doped with sole N during crystal growth in a conventional method, acceptor concentration of N is not increased more than 10 18 cm -3 . Even if further addition of N to ZnSe is tried, it is impossible to increase concentration of the carrier due to the compensation mechanism; a N atom located at a substitutional position of Se transfers to an interstitial position when acceptor concentration of N exceeds 10 18 cm -3 and turns to a donor (n-type), so that N atoms acting as p-type acceptors are diseffected by N atoms acting as p-type donors. The object of the present invention is to offer a ZnSe single crystal having low resistivity doped with N at acceptor concentration of 10 19 -10 21 cm -3 . According to the present invention, atomic N + gas prepared by dissociating N 2 gas with electromagnetic irradiation and a gaseous complementary element X acting as a n-type dopant are prepared at an atomic ratio of N:X being 2:1. The atomic gases are fed to a region where a ZnSe crystal is epitaxially grown on a substrate by MBE or MOCVD process. The atomic gases having the ratio of N:X being 2:1 may be prepared by decomposing XN with electromagnetic irradiation at a high temperature and adding N 2 gas to the decomposed product. The substitutional element X may be In, Ga, Al etc.. In the hereunder explanation, the substitutional element X is represented by In. Fig. 1 illustrates a model of a ZnSe crystal simultaneously doped with In and N. Fig. 2 is a schematic view illustrating an MBE apparatus for growth of a ZnSe crystal. Fig. 3 is a schematic view illustrating an MOCVD apparatus for growth of a ZnSe crystal. Fig. 4 is a graph of electronic state density which shows that N substitutionally occupying a position of Se serves as a p-type acceptor, while In substitutionally occupying a position of Zn serves as a n-type donor. When ZnSe is simultaneously doped with In acting as a n-type dopant and N acting as a p-type dopant at a ratio of In:N being 1:2, a donor In - Zn derived from In substitutionally occupying a position of Zn makes a couple with an acceptor N + Se derived from N substitutionally occupying a position of Se, and the replacement is stabilized due to an electrostatic energy generated by coupling +e with -e. The electrostatic energy stabilizes N which is further added to ZnSe. As a result, ZnSe is doped with the p-type carrier (a hole) at acceptor concentration of 10 19 -10 21 cm -3 , although the acceptor concentration does not exceeds 10 18 cm -3 or so by addition of sole N. The reason why simultaneous In and N doping effectively increases the concentration of the p-type carrier is supposed as follows: When ZnSe is simultaneously doped with In and N at a ratio of 1:2, In substitutionally occupies a position of Zn, and N substitutionally occupies a position of Se, as illustrated in a model shown in Fig. 1. The n-type dopant In makes an atomic 1:1 couple with the p-type dopant N, and another one N atom coordinates near the atomic couple and serves as an acceptor. Consequently, the acceptor maintains its activity up to a higher concentration level so as to enable heavy doping with the p-type dopant N at high concentration. According to MBE process for growth of a ZnSe crystal, a substrate 2 is located in a vacuum chamber 1, and a Zn source 3 and a Se source 4 are individually faced to the substrate 2, as shown in Fig. 3. Zn and Se vapors are generated by heating the Zn source 3 and the Se source 4 with corresponding heaters 5, fed onto the substrate 2 and epitaxially grown as a ZnSe crystal 6 on the substrate 2. During growth of the ZnSe crystal, N 2 gas is irradiated with electromagnetic wave generated by a radio frequency (RF) coil 7 and dissociated to N + . The resulting ionized N + gas is fed to the crystal growth region. At the same time, vapor In generated by heating an In source 8 with a heater 5 is also fed to the crystal growth region. The vapor In may be also supplied from a vapor source. When a flow rate of ionized N + gas is controlled in relation with vapor In so as to adjust the atomic ratio of ionized N + gas to vapor In at 2:1, the ZnSe crystal 6 growing on the substrate 2 becomes a p-type crystal heavily doped with N. According to MOCVD process, an organic Zn gas g 1 , an organic In gas g 2 , N 2 gas g 3 and an organic Se gas g 4 are individually decomposed and dissociated to atomic Zn, In, N + and Se with electromagnetic irradiation, and fed to a substrate 2. In this case, a flow rate of ionized N + gas is also controlled in relation with vapor In so as to adjust an atomic ratio of ionized N + gas to vapor In at 2:1. Due to the flow rate control, a ZnSe crystal 6 growing on the substrate 2 becomes a p-type crystal heavily doped with N. The source of ionized N + and In vapor may be a compound of InN in any above-mentioned method of epitaxial crystal growth. In this case, InN is decomposed at a high temperature by irradiation with electromagnetic wave and supplied to a region for epitaxial crystal growth. Additional N 2 gas may be fed to the region for epitaxial crystal growth to adjust the atomic ratio of ionized N + gas to In vapor at 2:1. N incorporated in the ZnSe crystal substitutionally occupies a position of Se and serves as a p-type acceptor N + Se , while In substitutionally occupies a position of Zn and serves as a n-type donor In - Zn . When the ZnSe crystal is doped with N and In at a ratio of 1:1, an acceptor charged with +e makes a couple with a donor charged with -e, so as to stabilize an electrostatic energy. When another one N is added to the ZnSe crystal stabilized in this way, a position of Se is stably substituted by N. Consequently, ZnSe can be heavily doped with N. An upper column (a) of Fig. 4 shows a density of state of the N-doped ZnSe crystal wherein N atom substituted for Se. It is noted that N served as a p-type acceptor. On the other hand, it is noted that In served as a n-type donor from the lower column (b) of Fig. 4 showing a density of the In-doped ZnSe crystal wherein In atom substituted for Zn. From these data on the density of state, it is understood that an electrostatic energy can be stabilized by simultaneous N and In doping. EXAMPLE A ZnSe single crystal was used as a substrate 2 for growth of a ZnSe crystal thereon and located in a vacuum chamber 1 held at 1.3 × 10 -8 Pa. A ZnSe crystal was epitaxially grown at 250-400°C by supplying vapor Zn at a pressure of 1.3 × 10 -5 Pa., vapor Se at a pressure of 1.3 × 10 -5 Pa., ionized N + at a pressure of 1.3 × 10 -7 Pa. and vapor In at a pressure of 6.5 × 10 -7 Pa., respectively. Said ionized N + was prepared by irradiating N 2 gas with electromagnetic wave in a microwave range. The obtained ZnSe crystal had an acceptor concentration which varied in response to a crystal growth temperature, as shown in Table 1. The ZnSe crystal was doped with N at a higher concentration at any crystal growth temperature, compared with a ZnSe crystal which was doped with sole N without feeding vapor In. EFFECT OF SIMULTANEOUS N AND In DOPING ON ACCEPTOR CONCENTRATION acceptor concentration (cm -3 ) temperature of substrate (°C) simultaneous doping with N and In doping with sole N 250 1 × 10 18 1 × 10 17 300 2 × 10 19 1 × 10 17 350 2 × 10 20 3 × 10 17 400 2 × 10 21 1 × 10 18 The similar simultaneous In and N doping was adopted in MOCVD process. In this case, a ZnSe crystal was also doped with a p-type carrier at an acceptor concentration of 10 19 -10 21 cm -3 . According to the present invention as aforementioned, ZnSe is simultaneously doped with a n-type dopant X and a p-type dopant N. Due to the simultaneous doping, a ZnSe crystal can be doped with the p-type carrier at an acceptor concentration of 10 19 -10 21 cm -3 , compared that the acceptor concentration of the p-type carrier has been not more than 10 18 cm -3 or so in a conventional method. The p-type ZnSe crystal obtained in this way exhibits excellent electric properties such as great p-type electronic conductivity and consequent low resistivity, since substantially all the N atoms incorporated in the crystal serve as active acceptors. Consequently, the doped ZnSe crystal is used as a material for an intensified blue laser, a blue light emitting device or the like in a high-density optical memory device, a full-color display, etc..

Claims: A method of producing a ZnSe crystal doped with N serving as a p-type dopant at acceptor concentration of 10 19 - 10 21 cm -3 , comprising the steps of: disposing a ZnSe single crystal as a substrate in a vacuum chamber; preparing Zn and Se vapors by heating a Zn source and a Se source by heaters, respectively; dissociating N 2 gas to ionized N + gas with electromagnetic irradiation; supplying said Zn and Se vapors together with said ionized N + gas to a region for epitaxial growth on said substrate; simultaneously supplying a gaseous complementary element X which crystallographically substitutes for Zn to said region for epitaxial crystal growth; and epitaxially growing a ZnSe crystal doped with N and X on said substrate, wherein flow rates of said gaseous N + and X supplied to said region for epitaxial crystal growth are controlled at an atomic ratio of N + :X being 2:1. A method of producing a ZnSe crystal doped with N serving as a p-type dopant at acceptor concentration of 10 19 - 10 21 cm -3 , comprising the steps of: disposing a ZnSe single crystal as a substrate in a vacuum chamber; preparing Zn and Se vapors by decomposing organozincic and organoselenic compounds with electromagnetic irradiation; preparing ionized N + gas by decomposing an N-containing compound with electromagnetic irradiation; supplying said Zn and Se vapors together with said ionized N + gas to a region for epitaxial crystal growth on said substrate; simultaneously supplying a gaseous complementary element X which crystallographically substitutes for Zn to said region for epitaxial crystal growth; and epitaxially growing a ZnSe crystal doped with N and X on said substrate, wherein flow rates of said gaseous N + and X supplied to said region for epitaxial crystal growth are controlled at an atomic ratio of N + :X being 2:1. The method of producing a ZnSe crystal doped with N according to Claim 1 or 2, wherein the complementary element X is an element selected from In, Ga, Al. The method of producing a ZnSe crystal doped with N according to Claim 1 or 2, wherein the complementary element X is In, and prepared by decomposition of InN with electromagnetic irradiation.

Inventors: YOSHIDA HIROSHI, YOSHIDA, HIROSHI
Applicants: JAPAN SCIENCE & TECH CORP, JAPAN SCIENCE AND TECHNOLOGY CORPORATION
Application year: 1997
Main classification: C30B25
IPC codes: C30B23, C30B29, C30B33, H01S3, C30B25