PROCESS FOR THE PRODUCTION OF AMORPHOUS MATERIAL FROM WASTES

Abstract: The invention relates to a process for the production of amorphous material from non sorted wastes, as well as from slags and fly ashes. It comprises the steps of drying the wastes by heat treating them at 600-1200 DEG C, melting them at 1300-1600 DEG C, transforming the crystal structure of the melt into an amorphous glassy mass by fast cooling thereof in water, and recovering said amorphous material. Complementary correcting oxides are further added during the heat treating step and/or the melting step. The amorphous material obtained can be used for the preparation of various building materials.

Description: PROCESS FOR THE PRODUCTION OF AMORPHOUS MATERIAL FROM WASTES The present invention relates to a process for the production of amorphous material from non sorted wastes, i.e. from any solid and/or liquid waste material, such as household and any kind of industrial wastes, including of energy production wastes, without the need of previously separating them according to their nature, as well as from slags and/or fly ashes produced by other usual wastes treatment plants. The amorphous material obtained by this process can advantageously be used as building material, especially in the preparation of light concrete, or in the production of light porous aggregates usable as insulating material, as drainage filling, as filtering material, as well as in agriculture, especially in hydroponics. A method of light aggregates production especially from household wastes is already known from JP-A-56/14628, which involves burning the wastes in a fluidized bed furnace (i.e. at a temperature lower than about 900°C), grinding the product obtained and mixing it with the dust formed during the burning step. The heavy metals (such as Zn, Ni, Cr, Cd, Pb, Ti, etc. ) are thus retained in the granules, which is not wished, since their oxides might pass into water solutions thereby decreasing the chemical resistance of the aggregate, and especially due to the fact that they are very toxic and constitute a potential pollution for the environment. It is also known from RU-A-1534028 a process for producing porous aggregates usable for example as building material from various wastes, such as solid domestic wastes, slags of heat electric power stations generated by coal, clay materials, as well as wastes from galvano- chemical productions, etc., in which the burning tempera¬ ture is of about 940-950°C. Also with this process some oxides of heavy metals stay in a free state, so that they could pass into aqueous solutions, and the chemical resistance of the aggregates obtained is thus not suffi¬ cient. The purpose of the present invention is therefore to provide an improved process for the production of amor¬ phous material, which obviates to the drawbacks of the known comparable methods, and especially which can be carried out with non sorted wastes and which leads to an amorphous material essentially free of heavy metals oxides, or more precise in which the heavy metals have been "neutralized" as being blocked in the glazed or vitrificated mass of the material produced. This aim was reached by the process according to the invention, which comprises the steps of - drying and heat treating the wastes at 600-1200°C, - melting them at 1300-1600°C, - transforming the crystal structure of the melt into an amorphous glassy mass by fast cooling thereof in water, and recovering said amorphous material, and which com¬ prises the addition of complementary products during the heat treating step and/or the melting step in such respec- tive quantities so as to provide the following contents of oxides in the melt : silicon oxide 30-70 wt% aluminium oxide 5-30 iron oxides 1-10 alkali metals oxides 1-10 alkaline-earth metals oxides 1-10 heavy metals oxides 0.1-5 According to particular embodiments of the invention, the process may comprise the steps of drying the wastes at 600-800°C and then of heat treating and pre-melting them at 1000-1200°C. Furthermore, and more particularly in the case of using slags as wastes, in continuous manner, said slags are premelted at 1000-1200°C, on a sloping hearth and the melt is treated at 1300-1450°C in a crucible. Generally, the heat treating step is carried out during 5 to 10 min. and the melting step during 20 to 40 min. for example under air splash lubrication, and the fast cooling step takes place at a speed of about 500- 600°C by minute; thus this fast or shock cooling step is similar to a quenching of the mass treated so as to make it vitrified or glazed. For working the above particular process, the steps of heat treating the wastes, i.e. the slags, and melting them are carried out in an apparatus which comprises a sloping hearth, a crucible located under said hearth for homoge- neizing the melt, a quenching bath located under said crucible for fast cooling the melt and means for recover¬ ing the amorphous material from said bath. The sloping sole is used more particularly for preheating and melting the wastes, resulting in the evaporation of all volatile matters, oxidation of organics and melting of minerals and metals The melt then flows down the slope in the form of a relatively thin layer towards the crucible, providing a high degree of refining. Preferably, the external surface of the sloping sole is covered with a coating especially made of refractory materials, such as alumina and magnesia. In the crucible, and before being submitted to the final fast cooling, the necessary additives are provided so as to proceed with the correction of the chemical composition, and the melt is homogeneized and overheated for providing a higher fluidity thereof. Preferably, the oxides contents ratio of the com¬ plementary products added are the following : 55-65% of silicon oxide, 10-22% of aluminium oxide, 3-6% of iron oxides, 3-7% of alkali metals oxides (such as K2O and Na2θ) and 3-7% of alkaline-earth metals oxides (such as CaO and MgO) . The correcting added products which can be used in practice are as silicon containing complementary product quartz sand, sandy loam, flask or tropoyl, as aluminium containing complementary product clay, loam, bauxite, ashes of heat power stations, and as iron containing com¬ plementary product burden dust or pyrite candle ends. Of course, the addition of the correcting oxides im¬ plies the preliminary analysis of the product composition obtained by the process; the control of the composition should be repeated at least each time that the type of starting material is changed. According to another object of the invention, the amorphous material obtained can be further submitted to the steps of grinding and granulating said material, then of roasting the granules formed in presence of organic compounds and binders, which are added during the grinding step and/or the granulation step, and so as to produce light porous aggregates. Preferably, for the production of such porous ag¬ gregates granules, from 0.5 to 1.5 wt% of organic com¬ pounds are added, which can be selected from solid or li¬ quid organic containing materials such as coal, oil slurry and used oil, and from 1.5 to 15 wt% of binders are added, which can be for example highly plastic clays or a solu¬ tion of glassware. In order to decrease the fuel consumption and to decrease the formation of nitric oxides during the melting step, smoke gases from the final roasting step can be ad¬ vantageously used for the drying steps and then for the melting step, or directly for the melting step. It is to be repeated here that as starting material for the process according to this invention, any kind of wastes (for example domestic, building, street cleaning, industrial, etc. wastes) can be used, without the need to formerly sort them; all kinds of wastes can effectively be processed altogether. Also, as pointed out before, slags and/or fly ashes produced by other usual wastes treating plants can be advantageously submitted to the process ac- cording to the present invention, especially in order to "neutralize" the heaving metals which they still contain after the usual treatment. During the melting step at high temperature ( > 1300°C) , the organic part of the wastes (i.e. wood, plastic, cloth, paper, bones, etc. ) is burned and the mineral part (glass, stones, sand, concrete, ashes, dust, etc. ) form slag and which goes up from metals which form alloys and go down. When liquid wastes are treated (such as slurry, solutions from chemical and galvanic industry, etc. ) the solid remainders after the treatment of high temperature are also separated into mineral part forming slag and metals turning into alloy as mentioned before. The "correction" of respective oxides contents in the melt of wastes up to the required limits allows to get a chemically hard alumosilicate glass mass. In this mass, oxides of aluminium and silicon are partially replaced by oxides of heavy metals. For getting liquid phase in the process for producing granules necessary for the expansion of said granules at temperature of 1000-1200°C, a part of silicon and aluminium oxides are replaced by iron oxides. Injection of organic materials (about 0.5-1.5%) makes it available to form gas phase and swell of granules liquid phase at temperature 1000-1200°C. Decreasing or increasing of organic and iron components leads to inadequate swell of granules or cavities in them. Injection of 1.5-15% binders is advantageous for the formation of granules from non plastic glass mass powder. Solid organics and binders are inserted during grinding of glass mass, and liquid ones are inserted during preparation of charge into granules, for example in a clay mixer. Additions that "correct" content of oxides in the melt also depend on their moisture. The invention will now be further described by way of the following examples. Figure 1 is a schematic view of an apparatus for work¬ ing a particular embodiment of the process according to the invention. Example 1 : Production of light porous aggregates Various wastes have been charged in a drying drum and heated during about 5-10 min. at 600-800°C, for example by use of graphite electrodes; the mass obtained was then put into a melting apparatus (in which a restoration atmo¬ sphere was kept) for being heated at 1300-1600°C for 20-40 min., for example in an electric furnace, during which "correcting" oxides were added and the mixture homogenized. For the correction of the amount of oxides, flask, ashes and burden dust were put into melting. This melting was poured into a basin with cold water, so as to quench it at a speed of cooling of about 500°C per minute. The cooled glass mass obtained was then ground in a spherical mill up to 2500cm /g, in which coal was ground together with the glass mass. Granules from the glass mass were formed on a plate granulator and solution of glassware (1.15 g/cnW) was put into the granulator. The granules obtained were dried in a drying drum and roasted in a rotated kiln. Some of smoke gases from the rotated kiln were directed into the drying drum and then into the melting machine. The other part was send only directly into the melting machine. More particularly, six differents types of aggregate materials have been prepared from various kinds of wastes mixtures, as follows : - Samples No 1 ,4,5 and 6 : building and domestic wastes (old concrete, stone, wood, metal, building gar¬ bage) - Sample No 2 : domestic and industrial wastes from radio and engine plants - Sample No 3 : domestic and industrial wastes from town and medical wastes (hospitals). The respective compositions and production conditions have been reported in Table I . Some physico-chemical characteristics have been measured on the above six aggregate samples and on a com¬ parison sample; this comparison sample was prepared from slag of an electric power station obtained at 12-15% coal burning from waste, but without a heat treatment at high temperature, and which contained heavy metals oxides not "blocked" in the granules . In addition to density and crack hardness measure¬ ments, other properties have been evaluated, more particularly acid resistance, alcali resistance and resistance to "attack" by water. These evaluations were made on 0.5-1mm grinded aggregates in solutions of sul- furic acid, respectively of potassium hydroxyde, and in distilled water, and given as ratio of mass aggregate before and after the test. Finally, heavy metals "migration" from the aggregates into water was performed; these aggregates have been pow- dered with distilled water and maintained in it for about ten days . The results obtained by the above measurements and evaluations are reported in the following Table II. The heavy metals contents measured in water were lower than about 0.01 wt% for the six samples according to the invention, whereas about 1.25 mg/dirp of such heavy metals was recovered for the comparison sample. The results reported in Table II further clearly show that the aggregate material according to the invention give much better results of chemical resistance; there¬ fore, this material is well appropriate for being used as building material, as heat insulating material, as drainage filling, as filtering material, as well as in agriculture, especially in hydroponics, since it is not toxic and not polluting the environment. Example 2 : Treatment of fly ashes Three different samples of fly ashes (Z1,Z2,Z3) with high heavy metals contents recovered from waste treatment plants have been submitted to the process according to the invention. More particularly, 60 kg of each sample have been charged in an electric furnace by 5kg every 5 min., preheated, and melted at about 1450°C, this during a total time of about 70 min. The melt thus obtained was then quenched in water so as to form a glassy mass in which the heavy metals remaining have been blocked. This was clearly shown from the results of the analysis made on the pow- Table I AGGREGATE SAMPLES No No a) Contents of oxides in melt (wt%) oxides of silicon 55 65 65 62 62 68 oxides of iron 6 6 3 6 3 6 oxide of aluminium 22 10 22 17 20 20 oxides of alkali metals 7 7 6.9 6 7 3 oxides of alkaline-earth metals 7 7 3 6 5 5 oxides of heavy metals 3 5 0.1 3 3 3 b) Heat treatment of waste products temperature (°C) 600 800 800 700 700 700 time (min) 10 5 5 7 7 7 c) Melt: temperature (°C) 1500 1460 1600 1300 1450 1450 time (min) 37 35 40 20 35 35 d) Charge composition (wt%) glass mass 89 89 94 . 5 83 . . 5 89 96.5 coal 1 1 0 . 5 1 . . 5 1 1 clay 10 1 0 5 1 5 10 glassware 2.5 Table II Properties Aggregates No Comparison 1 2 3 4 5 6 density (kg/m 3 ) 310 325 350 305 295 285 300 crack hardness (kgc/m 2 ) 4 4.5 5 3.5 3 3 3.5 acid resistance (%) 97.8 97.5 98 98 97 5 97 93 alkali resistance (%) 86 82 90 90 87 80 72 hydroscopicity (%) 99.9 99.9 99.9 99.9 99.9 99.9 97 dered amorphous mass of each sample Z1,Z2,Z3 treated, and which are reported in Table III, more particularly the analysis of the metals in the water containing such pow¬ ders (A01 ,A02,A03) Finally, it should be pointed ou that the amorphous material obtained by the process according to the present invention can be advantageously used in the form of powder in the preparation of concrete, for example as building material. TABLE III Fly ashes Analysis of metals Analysis of metal in water in the starting material containing the material Metals (mg/kg) after treatment (mg/lt) A01 A02 A03 As 60 59 84 < 0.001 < 0.001 < 0.001 Bi < 0.001 < 0.001 < 0.001 < 0.001 < 0.001 < 0.001 Cd 66 68 105 0.006 0.003 < 0.001 Co 3.16 3.37 7.1 0.018 < 0.001 < 0.001 Cr 306 281 440 0.170 0.050 0.035 Cu 650 660 1030 < 0.001 < 0.001 < 0.001 Fe 15'000 13'700 17'200 < 0.001 < 0.001 < 0.001 Li 0.83 2.73 2.95 0.010 < 0.001 < 0.001 Mg 5'500 5'600 8'300 6.69 2.96 5.31 Mn 1 '330 1 '280 1 '970 0.020 0.006 0.016 Mo 22.1 25 0.001 0.020 0.021 < 0.001 Ni 13.7 16.1 < 0.001 < 0.001 < 0.001 < 0.001 Pb 2'570 2'530 3 '800 < 0.001 < 0.001 < 0.001 Ti 810 810 1 '160 < 0.001 < 0.001 < 0.001 V 18.2 19.0 18.8 < 0.001 < 0.001 < 0.001 Zn 5' 000 5 '000 7 ' 800 < 0.001 < 0..01 < 0.030 Example 3 : Treatment of slags Slags resulting for example from usually incinerated municipal wastes are treated in a particular apparatus, as schematically illustrated on Figure 1. As shown on this Figure 1 , the apparatus comprises the four following different parts : (a) A feeding zone 1 comprising means 2 for bringing the wastes into the furnace in which the wastes are if neces¬ sary dried either by special means or by the hot gazes (600-800°C) coming from the other parts of the apparatus. (b) A sloping hearth 3, on the top portion 4 of which the wastes are burned and pre-melted at about 1000-1200°C; the pre-melted wastes thus slide downwards on the surface of the sloping sole which is covered by a refractory coating, so as to reach a temperature of 1200-1300°C in the lower portion 5 of the slope, where a partial transition of the mineral part of the wastes into a "pyroplastic" state takes place. The regulation of the temperature provides a state when the top relatively liquid layer of the melting slag is flowing down on the lower layer of the slag which is maintained in a relatively solid state. The lower solid layer of slag is formed during the primary melting of wastes and is maintained in this state. (c) The melt then flows down into a crucible 6, in which the temperature is maintained at 1300-1450°C, by elec¬ trodes 7. In the meantime, the melt is analyzed and then mixed with the appropriate correcting additives, under splashing with oxygen or heated air so as to better homogeneize the fused mass. Then, the thus treated melt is poured out from the crucible 6 into a quenching bath 8, in which the melt is submitted to a very fast cooling. The apparatus further comprises means 9 for recovering the aimed amorphous material from the quenching bath 8. The amorphous material recovered can be then grinded, and the product obtained as a powder can be advantageously used as additive in the preparation of cements. The initial composition of the slag was as follows : Si02 - 35% A1203 - 15% Fe203 + FeO - 6% CaO - 1.5% MgO - 3% S03 - 4% K20 + Na20 - 8% After addition of correcting line, i.e. about 7 kg of CaO per 100kg of the melt, the final composition of the product obtained included 32.2% of Siθ2, 13.4% of AI2O3 and 4.5% of CaO, which correspond to the usual required oxides percentages of the active mineral additions to ce¬ ments.

Claims: CLAIMS 1. Process for the production of amorphous material from non sorted wastes, which comprises the steps of - drying and heat treating the wastes at 600-1200°C, - melting them at 1300-1600°C, - transforming the crystal structure of the melt into an amorphous glassy mass by fast cooling thereof in water, and recovering said amorphous material, and which com¬ prises the addition of complementary products during the heat treating step and/or the melting step in such respec¬ tive quantities so as to provide the following contents of oxides in the melt : silicon oxide 30-70 wt% aluminium oxide 5-30 iron oxides 1-10 alkali metals oxides 1-10 alkaline-earth metals oxides 1-10 heavy metals oxides 0.1-5 2. Process according to claim Λ , which comprises the drying of the wastes at 600-800°C and then the heat treating and pre-melting thereof at 1000-1200°C. 3. Process according to claim 1, which comprises the pre- melting of the wastes at 1000-1200°C on a sloping hearth and treating the melt at 1300-1450°C in a crucible. 4. Process according to one of claims 1 to 3, in which the heat treating step is carried out during 5 to 10 min, and the melting step during 20 to 40 min., and in which the fast cooling step takes place at a speed of about 500- 600°C by minute. 5. Process according to one of claims 1 to 4, in which the oxides contents ratio are the following : 55-65% of silicon oxide, 10-22% of aluminium oxide, 3-6% of iron oxides, 3-7% of alkali metals oxides and 3-7% of alkaline- earth metals oxides. 6. Process according to one of claims 1 to 5, in which the silicon containing complementary product is quartz sand, sandy loam, flask or tropoyl, the aluminium contain¬ ing complementary product is clay, loam, bauxite, ashes of heat power stations, and the iron containing complementary product is burden dust or pyrite candel ends. 7. Process according to one of claims 1 to 6, in which the wastes treated are slags and/or fly ashes obtained by other waste treatment processes. 8. Process according to one of claims 1 to 7 for the production of light porous aggregates, which further com¬ prises the steps of grinding and granulating the amorphous material as obtained, then of roasting the granules formed in presence of organic compounds and binders, which are added during the grinding step and/or the granulation step, and so as to provide the porous aggregates. 9. Process according to claim 8, in which from 0.5 to 1.5 wt % of organic compounds are added, which can be selected from solid or liquid organic containing materials such as coal, oil slurry and used oil, and in which from 1.5 to 15 wt% of binders are added which can be for example highly plastic clays or a solution of glassware. 10. Process according to claims 8 or 9 , in which smoke gases from the final roasting step are recycled for the drying step and/or for the melting step. 11. Amorphous material as obtained by the process accord¬ ing to one of claims 1 to 7. 12. Use of the amorphous material, in the powder form, as an additive in the production of cement or concrete. 13. Light porous aggregates in the form of granules as ob¬ tained by the process according to one of claims 8 to 10. 14. Use of the granules according to claim 11 as building, insulating, drainage or filtering material. 15. Apparatus for working the process according to claim 3, which comprises a sloping hearth, a crucible located under said sloping hearth, for homogeneizing the melt, a quenching bath located under said crucible for fast cool¬ ing the melt and means for recovering the amorphous material from said bath.

Inventors: KATZ KONSTANTIN MIKHAILOVITCH, PETROV VICTOR PAVLOVITCH, VOLOKHONSKY LEV AVRAMOVITCH, KATZ, KONSTANTIN MIKHAILOVITCH, PETROV, VICTOR PAVLOVITCH, VOLOKHONSKY, LEV AVRAMOVITCH
Applicants: GIOVANNINI S A DE, KATZ KONSTANTIN MIKHAILOVITCH, PETROV VICTOR PAVLOVITCH, VOLOKHONSKY LEV AVRAMOVITCH, DE GIOVANNINI S.A., KATZ, KONSTANTIN MIKHAILOVITCH, PETROV, VICTOR PAVLOVITCH, VOLOKHONSKY, LEV AVRAMOVITCH
Application year: 1997
Main classification: C03B5
IPC codes: C03B3, C03B5, C03B19, C04B18