INTEGRATED DELTA E-E DETECTOR TELESCOPE

Abstract: A device forming a high energy resolution integrated semiconductor DELTA E-E detector telescope is disclosed, in which is formed a very thin DELTA E detector portion (14) primarily fabricated from a first semiconductor wafer which is bonded/silicidized to a second semiconductor wafer forming an E detector portion (18). This DELTA E-E detector provides a well supported very thin DELTA E detector for high resolution. The very thin DELTA E detector portion bonded/silicidized to the E detector portion further provides between each other a buried metallic layer (16) acting as a contact common to the two detectors, which metal layer is thin and presents a low resistivity.

Description: INTEGRATED ΛE-EDETECTOR TELESCOPE Technical field The present invention relates to a semiconductor detector and more exactly to an integrated ΔE-E detector. General background of the invention In many branches of science there is a need to measure energetic atoms with subrelativistic energies. Examples include, mineral prospecting with accelerator mass spectrometry, spacecraft measurements of the solar wind as well as interplanetary and galactic radiation environments, nuclear microprobe analysis of light trace distributions in biomedical matter, recoil spectrome¬ try characterization of opto- and microelectronic structures as well as fundamental experimental physics. Depending on the particular circumstances, a number of different techniques are available, such as electrostatic- and magnetic-sector spectrome¬ ters, Time of Flight techniques, scintillation detectors as well as semiconductors and gas-ionization detectors. Often the different techniques are combined, e.g., a magnetic spectrometer analyzer may be combined with a gas ionization detector to facilitate separate measurement of the momentum, atomic number and energy. For measurement of the atomic number as well as the energy of energetic atoms and ions in the 5 MeV per nucleon to 0.1 GeV per nucleon energy region, a so-called ΔE-E detector telescope is often used. These consist of a pair of detectors arranged so that the particle traverses the first detector and is subsequently stopped in the second (thicker) detector. The atomic number can be determined because the energy deposition within the thickness spanned by the ΔE detector depends on the electrical charge on the nucleus of the energetic atom (atom number). The total energy is the sum of the energy deposited in the two detectors. Exactly how the deposited energy is converted into an electrical signal depends on the type of detector. In the energy region of interest almost all the energy is deposited in exciting electrons of the detector material. In the case of a gas-ionization detector the number of ion-electron pairs can be registered. In the case of solid detector materials (scintillator and semiconductors) the electronic energy deposition leads to promotion of electrons across the band gap. This leads to photon emission in the case of the scintillator or a pulse of electric current flowing across a junction, in the case of a semiconductor detector. The junction in the semiconductor detector may be a Schottky barrier or an ion-implanted or diffused junction. Semiconductor detectors have the advantage over electrostatic and magnetic sector instruments that they are insensitive to the charge state of the incident ion or atom. However ΔE-E detector telescopes have a low energy threshold that corresponds to the energy where the range of the ion is just sufficient to penetrate right through the ΔE detector. To reduce the low-energy threshold as low as possible it is necessary to fabricate the ΔE detector as thin as possible. Prior art The ΔE-E detector telescopes with the lowest threshold that are currently suitable for mass-production are based on a p-i-n structure formed in a self-supporting 10 x 10 mm area 10 μm Si membrane that is formed by etching (see Whitlow et al., Proc. 9th Australian Conf. on Nuclear Techniques of Analysis, Newcastle, Australia, Nov. 1995). The p-i-n structure can be formed by ion- implantation or diffusion (see J. Kremmer, Nucl. Instrum. and Methods, Vol. 169, pp 499, 1980). These have a low energy threshold of about IA MeV and can be stacked together to form arrays subtending large solid angles with little dead area because of the rectangular shape. Thinner detectors can be produced, however, the difficulty of controlling the etching, and the use of Au/Si Schottky junctions implies the resolution is dominated by the uniformity in the active thickness of the detector. The extreme fragility of the self-supporting Si membranes places a technical restriction on the minimum thickness and thereby the low energy threshold that can be achieved. This precludes the use of self-supporting membrane detectors in space crafts because of the G-forces and vibration during the launch phase. Kremmer and Lutz have proposed an ion-implanted n-p * -n structure which is depleted from two sides (see Kremmer and Lutz, Nuclear Instrum. and Methods, A235, 365, 1978). In a further variant they propose using lateral drift fields to realize the separate collection of the ΔE and E signals. No data is presented from measurement with this type of detector. Possibly because the typical ±150 % variations in the background doping will lead to significant variations in the ΔE layer thickness that will result in poor resolution. Integrated detector telescopes, for instance according to Figure 1, have been reported by a Japanese group about a decade or so ago (e.g. see Husimi et al. , Nuclear Instr. and Methods, Vol 196, pp 125, 1984 and Y. Kim et al, Nuclear Instr. and Methods, Vol. 226, pp 125, 1984). This is based on epitaxial growth of a p-n-p structure. This integrated detector actually worked, however, the concept suffers from a number of drawbacks. The fact that epitaxy was used implies that it is not possible to obtain a well defined buried layer that forms the buried contact to the E and ΔE detector elements. This limits the minimum thickness of the thin detector and the thickness uniformity, which will be critically dependant on the gas dynamics during epitaxy. A potentially more serious problem is cross-coupling between the ΔE-E detector pair because the intense ionization along the ion track can form a plasma with a carrier concentration exceeding the doping concentration in the buried contact. Under these conditions the plasma can appreciably modify the local electric field round the plasma column and acts as a path for charge carriers between the E and ΔE detectors. A U.S. Patent No. 5,387,555 describes a method to create buried suicide layers with wafer bonding. However the method described contains also at least one insulating buried layer in contact with the buried suicide layer. Moreover the method according to this patent lacks a cooperating dopant for diffusion from the buried suicide layer. Consequently it is found that there is a strong demand for an integrated semiconductor ΔE-E detector generally offering a good mechanical stability and presenting a ΔE-portion which may even withstand strong momentary mechanical forces, e.g. an accelera¬ tion, as well as also presenting a high resolution which will imply a very thin structure necessary for the ΔE portion of the detector. These two main demands will then be more or less contradictory to each other. Description of the invention To avoid the problems discussed above the present invention suggests a structure consisting of a number of p-i-n diodes separated by metallic layers. The metallic layer between the devices ensures that there is no coupling between the different detector elements due to charge carrier funneling and minimizes image charge effects. According to a main object of the present invention a detector telescope is formed with a very thin ΔE detector portion fabricated from a first silicon wafer which is bonded/silicidized to a second silicon wafer which forms the E detector portion of the detector telescope and thereby producing a well supported very thin ΔE detector for high resolution in the detector telescope, the very thin ΔE detector portion and the E detector portion between each other further present a buried metallic layer acting as a contact common to the two detectors, whereby the metallic layer is very thin and presents a low resistivity. Other objects and advantages of different embodiments of the invention will be further defined in the dependent claims. Description of the drawings The invention, together with additional objects and advantages thereof, may best be understood by making reference to the following description taken together with the accompanying drawings where like designation numbers are used for same or corresponding members and in which: Fig. 1 demonstrates an integrated detector telescope structure based on epitaxial growth according to prior art; Fig. 2 shows an integrated ΔE-E detector according to a planar processing method according to the present invention; Fig. 3 shows a detector where the barrier layer is formed as a metallic layer with the metallic layer as a common contact; and Fig. 4 shows a high resolution detector system consisting of a triple telescope. Embodiments of the invention The system of a thin ΔE and thick E semiconductor detector in a telescope configuration, makes it possible to estimate an ionized particle's identity and energy. In most systems the thin ΔE detector is self supporting. However with an active area of 1 cm 2 and a thickness of the order of lOμm or less, the detector is fragile and easily broken. According to the present invention the possibility to let the E-detector support the thin detector solves the problem concerning the mechanical instability and an integrated mechanically stable ΔE-E detector is created. When the low energy limit is set by the requirement that the particle must be able to traverse the ΔE detector, a thin detector, thinner than lOμm, needs to be integrated. The integration also reduces the number of so-called dead layers from four to three. A layer buried between the ΔE and E detectors, a dead layer acting as an ohmic contact, is common to both detectors and must be thin and have a low resistivity. The buried layer may be formed by epi- layer growth, wafer bonding or by implantation. The possibility to form a thin buried metallic layer in the semiconductor gives a small series resistance, therefore a small RC constant and fast charge carrier collection. Furthermore, the low resistivity in the buried metallic layer ensure minimal signal cross-talt between the two detectors due to charge carrier funneling (transport of charge carriers into/out of a depleted layer along the ion track due to transient distortion of the electric field brought about by the low resistivity plasma column along the ion track. ) Figure 2 illustrates an integrated ΔE-E detector according to the present invention resulting from the planar processing method. The buried metallic layer 16 may either be connected by means of an edge contact A or by vias B. To maintain a low series resistance and minimize the minority carrier injection, highly doped ohmic contact layers 15 and 17 are created in between the metallic 16 and the semiconductor layers 14 and 18. Dielectric layers 12 and 20 are grown or deposited to passivate and protect the semiconductor. A barrier layer 10 is formed to create a p-n junction, a Schottky barrier junction or a heterojunction. Similarly another barrier layer 22 creates the corresponding function at the E detector semiconductor on the side opposite the ΔE detector. An integrated detector was fabricated as illustrated in Figure 2, and connected by an edge-contact A. A silicon wafer of a first type was cleaned in advance using with a standard cleaning process for 10 minutes in a solution of H 2 S0 4 :H 2 0 2 having a volume ratio of 2.5:1 and then the wafer was rinsed during 5 min in deionized water. The thin oxide was removed by dipping the wafer into a solution of H 2 0:HF, having a 10:1 volume ratio, until the wafer had a hydrophobic surface and it was then subsequently dried by blowing it with N 2 gas. The silicon wafer had a diameter of 7.6 cm (3 inches) and was grown by a floating zone technology, a surface normal orientation [111], a thickness 305 μm, phospho¬ rus doped neutron induced , and having a resistivity of 15000 to 24000 Ωcm was prepared with an n+ layer by implantation with arsenic. The arsenic was implanted with an energy of 70 keV to a dose of 4xl0 15 cm "2 . The wafer was cleaned during 10 min in a solution of H 2 S0 < :H 2 0 2 with a volume ratio of 2.5:1 and subsequent¬ ly rinsed for 5 min in deionized water. The thin oxide was subsequently removed by dipping the wafer into a solution H 2 0:HF, with a volume ratio of 10:1, until the wafer had a hydrophobic surface. The wafer was then dried in blowing N 2 gas. A 30 nm (300 A) thick layer of cobalt is electron-beam evaporated onto the silicon wafer. The evaporation was started at a base-pressure of lxlO "8 mbar and during the evaporation the pressure rose to 9xl0 "8 mbar at the deposition rate of 0.4 nms "1 . After the evapora¬ tion the wafer was kept in the load-lock chamber until the second type of wafer was ready for the bonding process. A silicon wafer of a second type with a diameter of 7.6 cm (3 inches) grown by floating zone technology, with a surface normal orientation [100], a thickness lOOμm, double side polished, phosphorus doped, and a resistivity of 100 to 300Ωcm was then covered on one side with a plasma chemical vapor deposited Si0 2 - layer with a thickness of 1 μm. The thin oxide on the undeposited surface was removed by dipping the wafer into H 2 0:HF, with a 10:1 volume ratio, until the wafer had a hydrophobic surface. The wafer was then dried in blowing N 2 gas. The first and second type of wafers were pressed together and a 100 g quarts plate was placed on top of the wafers in order to counteract bending caused by difference in thermal expansion of the buried layer 16 and the silicon wafers. A bonding/silicidation was subsequently carried out in a ψ 2 atmosphere at 900 °C in a furnace for 30 min. The deposited Si0 2 layer protects the surfaces from impurity diffusion from the quarts plate. During the bonding/silicidation process some of the arsenic is incorporated in the buried suicide layer. The buried suicide layer then acts as a diffusion source for formation of an n * layer in the bonded [100] wafer. Further annealing increas¬ es the diffusion depth in the silicon. A protecting layer of black-wax was then melted onto the [100]- wafer. The [111]-wafer was polished/etched in a solution of HN0 3 :CH 3 C00H:HF, having a volume ratio of 5:3.3, at 40 °C for 1 min. Then the bonded/silicidized wafers were cleaned for 5 min in a consecutive order in each of the following solutions: trichlor- ethylene, acetone, propyl alcohol and deionized water. The deposited Si0 2 -layer was removed by a BHF solution (buffered HF) until the surface was hydrophobic. The bonded/silicidized wafers then were etched at 80 °C for 88 min in a solution of K0H:H 2 0 having a weight ratio of 1:1. Because the KOH etchant is an- isotropic the [100]-wafer was etched =80μm, while the [111]-wafer remained practically un-etched. The bonded/silicidized wafers were then rinsed in deionized water for 5 min, cleaned for 10 min in a solution of H 2 S0 < :H 2 0 2 with a volume ratio of 2.5:1 and then rinsed for 5 min in deionized water. Subsequently the [100]-wafer was covered with a plasma chemical vapor deposited Si0 2 -layer with a thickness of 1 μm. In a lithographic etching process, etching notches were opened in the oxide. The resist was stripped and a short dipping of the bonded/silicidized wafers into a diluted HF solution removed the thin oxide in the opened etching notches. The wafer provided with the etching notches then was etched during 10 min at 80°C in a solution of K0H:H 2 0 as described above, and was subsequently rinsed for 5 min in deionized water. The deposited Si0 2 layer was removed by a BHF solution until the surface was hydrophobic. To form trenches the wafer then was etched at 80 "C in a solution of K0H:H 2 0 having a weight ratio 1:1 until the etching notches were fully opened (i.e. the etching was stopped down at the previous formed buried CoSi 2 layer). Then the thickness of the [100]-wafer was about 7μm. The bonded/- silicidized wafers were again rinsed in deionized water for 5 min, cleaned during 10 min in a solution of H 2 S0 4 :H 2 0 2 having a volume ratio of 2.5:1 and then rinsed for 5 min in deionized water. The thin oxide was removed by a dipping of the wafers into H 2 0:HF, having a volume ratio of 10:1, until the wafers had a hydrophobic surface and they were subsequently dried in blowing N 2 gas. After this the bonded/silicidized wafers were wet oxidized at 900 °C for 1 hour. The wet oxide passivates the silicon surfaces. Subsequently the wafers of type [100] and [111] both were deposited with a plasma chemical vapor which deposited a Si0 2 -layer having a thickness of lμm. To increase the protec¬ tion from diffusion of mobile ions and to improve the scratch resistance the surfaces were processed with a plasma chemical vapor which deposited a Si 3 N 4 layer having a thickness of 145 nm (1450 A). A ring pattern having a width of 5 mm surrounding the [100]-wafer was opened in the deposited oxide. The wafer of type [100] then was etched at 80 °C in a solution of K0H:H 2 0, having a weight ratio 1:1, until the ring pattern was opened (i.e. the etching was stopped at the earlier formed buried CoSi 2 layer). Thus the etched surrounding ring opened a contact (A) to the buried layer 16 of Figure 2. The bonded/silicidized wafers were again rinsed in deionized water for 5 min, cleaned for 10 min in a solution of H 2 S0 4 :H 2 0 2 having a volume ratio of 2.5:1. In an lithographic etching process step-aligned detector openings were created in the oxide on the wafers. The detector openings had a square shape 0.25 cm 2 with a 0.5 mm corner radius. The resist was stripped and the thin oxide etched in a dilute HF solution. A 30 nm (300 A) thick layer of cobalt is then by means of an electron beam evaporated onto the wafers of both structure types ([100] and [111]). The evaporation condition was with a base pressure of lxlO" 8 mbar and during the evaporation, with a rate of 0.4 nms "1 , the pressure was 9xl0 "β mbar. The cobalt layers were silicidized in 800°C for 15 min in a N 2 -ambient to form CoSi 2 . Un-reacted cobalt was etched for 10 minutes in a solution of H 2 S0 4 :H 2 0 2 , having a volume ratio of 2.5:1, and then rinsed for 5 min in deionized water. Then the [100]-wafers were implanted with BF 2 having an energy of 90 keV and with a dose of 5xl0 15 cm "2 . The [111]-wafers were implanted with B having an energy of 70 keV and with a dose of 2xl0 15 cm "2 . The implanted boron was rendered electrically active during a 30 min heat treatment at 900°C in an N 2 ambient. The processing was finished with a forming gas annealing at 450°C for 30 min in 90% N 2 and 10%H 2 From this process a ΔE-E detector according to Figure 2 was achieved producing an integrated detector telescope with a very thin well supported ΔE detector presenting the desired thickness uniformity high resolution and the desired mechanical stability. The ΔE detector may then have a thickness ranging from up to lOOμm, and preferably of the order 7 μm or less for obtaining a low threshold energy for the ΔE detector. In the described illustrative embodiment of the production of a ΔE-E detector device according to the present invention was illustrated for the case of phosphorous doped substrates, however the doping of the substrates could as well use other suitable dopants like for example boron, arsenic or antimony. In case of some other method, well known to a person skilled in the art, for etching down the first substrate should be used also a silicon wafer of a surface normal orientation of [111] could be used for the thin detector portion. The basic structure for the very thin ΔE detector structure could also consist of a deposited semicon¬ ductor layer of any suitable material as indicated above. A first semiconductor wafer could then after the bonding/silicidation process be etched away and be replaced by a thin deposited semiconductor layer by applying known techniques. The buried metal need not be pure metal but may be compounds with a suitable metallic electronic structure of a nitride, eg., TiN, or a suicide, e.g. TiSi 2 , PtSi, WSi 2 , or CoSi 2 . In the same manner different types of semiconductor substrates could also be used, for instance silicon, silicon germanium, silicon carbide, gallium arsenide and indium phosphide. Figure 3 demonstrates an alternative embodiment of a telescope ΔE-E detector according to the invention. In Figure 3 the barrier layers are formed as buried layers 30, 32 with the buried metallic layer 16 as a common contact. The connection to the metallic layer is done by the connection plugs B. The shape of the ΔE detector presented is produced for instance with mesa etching using a technique well known by a person skilled in the art. The front and back ohmic contacts 36, 37 are fabricated with a highly doped layer. Thus the detector of Figure 3 will be fabricated in a similar way as the one described with reference to Figure 2 by changing the order of certain process steps already known by a person skilled in the art. Figure 4 demonstrates a further embodiment of a detector in accordance with the present invention. In Figure 4 a high resolution detector system is illustrated which is based on a triple detector telescope. This Έ. X /ΔE 2 /E detector telescope will be considered as a combination of the two previous discussed detector systems presented in Figures 2 and 3. Here two buried metallic layers 16A and 16B are found as well as two semicon¬ ductor layers 14A, 14B which constitute the ΔE detectors and a third semiconductor layer 18 acting as an E detector. The remaining elements are the same as those presented in Figures 2 and 3. Consequently, this triple detector will be considered as a further embodiment of the present invention. Thus, it will be possible, according to the present invention, to create a detector telescope containing a number of different ΔE detector portions on top of a common E detector portion, thereby creating a solid state Bragg-Curve Detector to simultaneously measure the identity and energy of energetic ions. In such a device the thin p-i-n diode detectors can be read out individual¬ ly using standard charge sensitive pre-amplifiers. The metallic layer between the devices ensures there is no coupling between the different thin p-i-n element detectors due to charge carrier funneling and minimizes image charge effects. Such a device will achieve a much faster read-out because the detector does not rely the drift of electrons to an anode under the action of an electric field. Additionally the device may be made very compact because the atomic density of semiconductors and metals is much higher than for gases. The device will also be very rugged which makes it suitable for space-probe applications. Only low voltages, of the order 50 V, will be needed because the individual p-i-n diodes will be depleted with very low applied voltage. It will be understood by those skilled in the art that various modifications and changes may be made to the present invention without departure from the spirit and scope thereof, which is defined by the appended claims.

Claims: CLAIMS 1. A device forming a low threshold energy integrated semiconductor detector telescope, characterized in that a ΔE-E detector telescope is formed with a very thin ΔE detector portion (14) fabricated from a first semiconductor wafer bonded/sili¬ cidized to a second semiconductor wafer forming an E detector portion (18), said detector telescope thereby presenting a very well supported very thin ΔE detector for high energy resolution, whereby said bonded/silicidized very thin ΔE detector portion and said E detector portion further between each other have a buried metallic layer (16) acting as a contact common to the two detectors, said metallic layer further being thin and presenting a low resistivity and minimising signal cross-talk between the ΔE and E detector portions. 2. The device according to claim 1, characterized in that said first and second semiconductor wafers consist of a suitably doped silicon substrate of a surface normal orientation [100] or [111], whereby the dopant may be phosphor, boron, arsenic or antimony. 3. The device according to claim 1, characterized in that a very thin ΔE detector structure consists of a deposited semicon¬ ductor layer. 4. The device according to claim 1, characterized in that said second semiconductor wafer consists of a silicon substrate with neutron-induced phosphorous doping and with a surface normal orientation [111] . 5. The device according to claim 1, characterized in that said first or second semiconductor wafers consist of silicon, silicon germanium, silicon carbide, gallium arsenide or indium phosphide. 6. The device according to claim 1 or 3, characterized in that said very thin ΔE detector portion (14) presents a thickness ranging up to lOOμm and preferably of the order 7μm or less. 7. The device according to claim 1, characterized in that said buried metallic layer (16) on each side is additionally provided with highly doped ohmic contact layers (15, 17) to maintain a low series resistance and to minimize minority carrier injection. 8. The device according to claim 1, characterized in that said buried metallic layer (16) on each side is provided with a further barrier layer (30, 32) creating a p-n junction, a Schottky barrier junction or a heterojunction. 9. The device according to any combinations of the previous claims, characterized in that a triple detector telescope containing a first ΔEi detector portion (14A) and a second ΔE 2 detector portion (14B) which are combined with said second silicon wafer forming said E detector portion (18), whereby said second ΔE 2 detector portion is bonded/silicidized to said E detector portion and in which detector telescope said second ΔE 2 detector portion in turn is bonded/silicidized to said first &.E 1 detector portion. 10. The device according to claim 8, characterized in that said first ΔE X detector portion (14A) is a very thin detector while said second ΔE 2 detector portion (14B) presents a several times thicker ΔE detector portion. 11. The device according to any combinations of the previous claims 1 - 7, characterized in that a detector telescope is created containing a number of different ΔE detector portions on top of a common E detector portion and having each detector separated by a metallic layer, thereby creating a solid state Bragg-Curve Detector to simultaneously measure the identity and energy of energetic ions.

Inventors: PETTERSSON STURE, THUNGSTROEM GOERAN, WHITLOW HARRY, PETTERSSON, STURE, THUNGSTROEM, GOERAN, WHITLOW, HARRY
Applicants: PETTERSSON STURE, THUNGSTROEM GOERAN, WHITLOW HARRY, PETTERSSON, STURE, THUNGSTROEM, GOERAN, WHITLOW, HARRY
Application year: 1997
Main classification: H01L31
IPC codes: H01L25, H01L31