NIOBIUM OR TANTALUM PROMOTED SILVER CATALYST

Abstract: A rhenium free silver catalyst for ethylene oxidation to ethylene oxide is provided containing a promoter combination consisting of an alkali metal component, a niobium or tantalum component, and a sulfur component.

Description: NIOBIUM OR TANTALUM PROMOTED SILVER CATALYST Background of the Invention Field of the Invention The present invention relates to a cesium and niobium or tantalum promoted silver catalyst for the oxidation of ethylene to ethylene oxide and to the catalyst preparation. Description of the Prior Art Processes for the production of ethylene oxide involve the vapor phase oxidation of ethylene with molecular oxygen using a solid catalyst comprised of silver on a support such as silver. There have been great efforts by many workers to improve the effectiveness and efficiency of the silver catalyst for producing ethylene oxide. U.S. Patent 5,051,395 provides a comprehensive analysis of these efforts of prior workers. Among the many prior teachings in this area is that of U.S. Patent 4,007,135 (see also UK 1,491,447) which teaches variously silver catalysts for the production of ethylene and propylene oxides comprised of a promoting amount of copper, gold, magnesium, zinc, cadmium, mercury, strontium, calcium, niobium, tantalum, molybdenum, tungsten, chromium, vanadium, and/or preferably barium, in excess of any present in immobile form in the preformed support as impurities or cements (column 2, lines 1-15) , silver catalysts for the production of propylene oxide comprising a promoting amount of at least one promoter selected from lithium, potassium, sodium, rubidium, cesium, copper, gold, magnesium, zinc, cadmium, strontium, calcium, niobium, tantalum, molybdenum, tungsten, chromium, vanadium and barium, in excess of any present in immobile form in the preformed support as impurities or cements (column 2, lines 16-34), as well as silver catalysts for producing ethylene oxide or propylene oxide comprising (a) a promoting amount of sodium, cesium, rubidium, and/or potassium, and (b) magnesium, strontium, calcium and/or preferably barium in a promoting amount (column 3, lines 5-8). No examples relating to niobium are given. U.S. Patent 5,057,481, and related 4,9908,343 are concerned with silver ethylene oxide catalysts comprised of cesium and an oxyanion of a group 3b to 7b element. Niobium is not mentioned, however. U.S. Patent 3,888,889 describes catalysts suitable for the oxidation of propylene to propylene oxide comprised of elemental silver modified by a compound of an element from Group 5b and 6b. Niobium is named and examples are given of elemental silver modified by niobium pentachloride and niobium pentafluoride. Although the use of supports is mentioned, there are no examples. The use of cesium is not mentioned. European Publication 0 266 015 deals with supported silver catalysts promoted with rhenium, among a long list of possible co-promoters, niobium is mentioned. No examples of niobium promoted catalysts are given. In the context of the bewildering and vast number of references, many of them contradictory, applicant has discovered a novel and improved catalyst for the production of ethylene oxide. Brief Description of the Invention The present invention relates to an improved supported silver ethylene oxide catalyst containing a promoter combination consisting of an alkali metal component, preferably cesium, together with a niobium or tantalum component, a sulfur component, and optionally a fluorine component and to the catalyst preparation. Description of the Drawing Attached Figure 1 is a graphical representation of reaction selectivity as a function of time for a catalyst of the invention. Detailed Description Preferred catalysts prepared in accordance with this invention contain up to about 30% by weight of silver, expressed as metal, deposited upon the surface and throughout the pores of a porous refractory support. Silver contents higher than 20% by weight of total catalyst are effective, but result in catalysts which are unnecessarily expensive. Silver contents, expressed as metal, of about 5-20% based on weight of total catalyst are preferred, while silver contents of 8-15% are especially preferred. In addition to silver, the catalyst of the invention also contains an alkali metal, preferably a cesium promoter component. The alkali metal promoter amounts and impregnation procedures described in U.S. Patent 3,962,136 are advantageously employed. Essential to the catalysts of the invention is the provision of a niobium or tantalum promoter component which, expressed as Nb or Ta, is incorporated in the catalyst in amount of about 5-300 ppm by weight based on the weight of catalyst. Necessary also is the provision of sulfur as a promoting catalyst component which component can be added to the catalyst support impregnating solution as sulfate, eg cesium sulfate, ammonium sulfate, and the like. U.S. Patent 4,766,105 describes the use of sulfur promoting agents, eg. at column 10, lines 53- 60, and that disclosure is incorporated herein by reference. The use of sulfur (expressed as the element) in amount of 5-300 ppm by weight based on the weight of catalyst is suitable. The catalysts of the invention are essentially free of rhenium. It is preferred that the catalyst also contains a fluorine promoter in amount expressed as the element of 10-300 ppm by weight based on the catalyst. Ammonium fluoride, alkali metal fluoride, as well as fluorides of niobium or tantalum can be used. As to the niobium or tantalum component, it is not critical that the component be added as any particular niobium or tantalum compound. Niobates are suitable as are niobium compounds such as niobium pentahalide, eg. NbF 5 , NbCl 5 , ammonium hexafluoro niobate, and the like. Similar tatalum compounds are useful. Equivalent results are achieved with substantially any niobium or tantalum compound which is soluble in the impregnating solution. Catalysts may be made with supports comprising alumina, silica, silica-alumina or combinations thereof. Preferred supports are those containing principally alpha-alumina, particularly those containing up to about 15 wt% silica. Especially preferred supports have a porosity of about 0.1-1.0 cc/g and preferably about 0.2-0.7 cc/g. Preferred supports also have a relatively low surface area, i.e. about 0.2-2.0 m 2 /g, preferably 0.4-1.6m 2 /g and most preferably 0.5-1.3 m 2 /g as determined by the BET method. See J.A. Chem. Soc. 60, 3098-16 (1938) . Porosities are determined by the mercury porosi eter method; see Drake and Ritter, "Ind. Eng. Chem. Anal. Ed.," 17, 787 (1945) . Pore and pore diameter distributions are determined from the surface area and apparent porosity measurements. For use in commercial ethylene oxide production applications, the supports are desirably formed into regularly shaped pellets, spheres, rings, etc. Desirably , the support particles may have "equivalent diameters" in the range from 3-10 mm and preferably in the range of 4-8 mm, which are usually compatible with the internal diameter of the tubes in which the catalyst is placed. "Equivalent diameter" is the diameter of a sphere having the same external surface (i.e. neglecting surface within the pores of the particle) to volume ration as the support particles being employed. Preferably, the silver is added to the support by immersion of the support into a silver/a ine impregnating solution or by the incipient wetness technique. The silver containing liquid penetrates by absorption, capillary action and/or vacuum into the pores of the support. A single impregnation or a series of impregnations, with or without intermediate drying, may be used, depending in part upon the concentration of the silver salt in the solution. To obtain catalyst having silver contents within the preferred range, suitable impregnating solutions will generally contain from 5-50 wt% silver, expressed as metal. The exact concentrations employed, of course, will depend upon, among other factors, the desired silver content, the nature of the support, the viscosity of the liquid, and solubility of the silver compound. Impregnation of the selected support is achieved in a conventional manner. The support material is placed in the silver solution until all of the solution is absorbed by the support. Preferably the quantity of the silver solution used to impregnate the porous support is no more than is necessary to fill the pore volume of the porous support. The impregnating solution, as already indicated, is characterized as a silver/amine solution, preferably such as is fully described in U.S. Patent 3,702,259 the disclosure of which is incorporated herein by reference. One or more metal promoters, most preferably cesium, and the impregnation procedures described in U.S. patent 3,962,136 are advantageously employed. Known prior procedures of predeposition, co-deposition and postdeposition of various promoters can be employed. After impregnation, any excess impregnating solution is separated and the support impregnated with silver and the promoter or promoters is calcined or activated. In the most preferred practice of the invention, calcination is carried out as described in commonly assigned U.S. Patent 5,504,052 granted April 2, 1996 and copending application Serial No. 08/587,281 filed January 16, 1996, the disclosures of which are incorporated herein by reference. The calcination is accomplished by heating the impregnated support, preferably at a gradual rate, to a temperature in the range 200-500°C for a time sufficient to convert the contained silver to silver metal and to decompose the organic materials and remove the same as volatiles. The impregnated support is maintained under an inert atmosphere while it is above 300 °C during the entire procedure. While not wishing to be bound by theory, it is believed that at temperatures of 300°C and higher oxygen is absorbed in substantial quantities into the bulk of the silver where it has an adverse effect on the catalyst characteristics. Inert atmospheres as employed in the invention are those which are essentially free of oxygen. An alternative method of calcination is to heat the catalyst in a stream of air at a temperature not exceeding 300°C, preferably not exceeding 250°C. Catalysts prepared in accordance with the invention have improved performance, especially stability, for use in the production of ethylene oxide by the vapor phase oxidation of ethylene with molecular oxygen. These usually involve reaction temperatures of about 150°C to 400°C, usually about 200°C to 300°C, and reaction pressures in the range of from 0.5 to 35 bar. Reactant feed mixtures contain 0.5 to 20% ethylene and 3 to 15% oxygen, with the balance comprising comparatively inert materials including such substances as nitrogen, carbon dioxide, methane, ethane, argon and the like. Only a portion of the ethylene usually is reacted per pass over the catalyst and after separation of the desired ethylene oxide product and the removal of appropriate purge streams and carbon dioxide to prevent uncontrolled build up of inerts and/or by-products, unreacted materials are returned to the oxidation reactor. The following examples illustrate the invention. Example 1 A silver solution was prepared using the following components (parts are by weight) : Silver oxide - 834 parts Oxalic acid - 442 parts Ethylene Diamine - 415 parts Deionized water - 2808 parts Silver oxide was mixed with water, at room temperature, followed by the gradual addition of the oxalic acid. The mixture was stirred for 15 minutes and at that point the color of the black suspension of silver oxide had changed to the gray/brown color of silver oxalate. The mixture was filtered and the solids were washed with 3 liters of deionized water. A container which contained the washed solids was placed in an ice bath and stirred while ethylene diamine and water were added slowly in order to maintain the reaction temperature lower than 33 °C. After the addition of all the ethylene diamine and water the solution was filtered at room temperature. The clear filtrate was utilized as a silver/amine stock solution for the catalyst preparation. The support used for the examples was obtained from Norton Company and was made primarily of alpha-alumina in the form of 5/16 inch cylinders. The support has a surface area of 0.65 in 2 /? pore volume of .3 cc/g, and medium pore diameter of 1.5. About 185 parts of the silver solution was mixed with: 1. 2.86 parts of CsOH solution, (8%Cs in water), 2. 3.6 parts of ammonium hexafluoro niobate, (2.25% in water) , and 3. 1.6 parts of ammonium hydrogen sulphate, (1%S in water) The mixture was stirred to assure homogeneity, then added to 400 parts of the support. The wet catalyst was mixed for ten minutes and then calcined. Calcination, the deposition of silver compound, was induced by heating the catalyst up to the decomposition temperature of the silver salt. This was achieved via heating in a furnace that has several heating zones in a controlled atmosphere. The catalyst was loaded on a moving belt that entered the furnace at ambient temperature. The temperature was gradually increased as the catalyst passed from one zone to the next. It was increased, up to 400°C, as the catalyst passed through seven heating zones. After the heating zones the belt passed through a cooling zone that gradually cooled the catalyst to a temperature lower than 100 °C. The total residence time in the furnace was 22 minutes. Atmosphere of the furnace was controlled through use of nitrogen flow in the different heating zones. Examples 2-9 Using the silver solution and support described above, additional catalysts were prepared. Examples 10-11 are comparative in that no niobium or tantalum component was included. In Examples 2-3, niobium pentachloride was substituted in the impregnating solution for the ammonium hexafluoroniobate. In Example 4 niobium oxalate was used in place of ammonium hexafluoroniobate. In Examples 5-6 niobium hexafluoride was used in place of ammonium hexafluoroniobate while in Example 7 ammonium hexafluoroniobate was used. In Examples 8 and 9, niobium pentachloride and tantalum heptafluorotantalate were used respectively. The following Table 1 shows the composition of the promoter impregnating solution and the conditions of calcination. The catalysts were tested in a tube which was heated by a salt bath. A gas mixture containing 15% ethylene, 7% oxygen, and 78% inert, mainly nitrogen and carbon dioxide, was passed through the catalyst at 300 p.s.i.g., the temperature of the reaction was adjusted in order to obtain ethylene oxide productivity of 160 Kg per hour per m 3 of catalyst and this temperature is given in the Table. The results of the catalyst tests are summarized in Table 1. Table 1 CO C GO {/> H H C H rπ en x VD m m H 3 c r- m ro Table 1 (cont'd) CO c 03 O H C H m en x m m 10 H (1) Ta " 53 (2) Nb c r- m ro The catalyst of Example 8 above was tested as above indicated for 700 hours. Attached Figure 1 is a graphic representation of the test results with the catalyst of Example 8. As depicted in this Figure, the catalyst was extremely stable even after extended testing. By contrast, similar catalysts which did not contain the niobium or tantalum evidenced a sharper rate of decline on extended testing. From the above results it can be seen that: 1. Addition of niobium or tantalum to the Ag/Cs/S catalyst leads to an increase in selectivity, from 81.5-82% up to 84.0%. 2. Addition of niobium or tantalum to the Ag/Cs/S catalyst leads to an increase in its stability. 3. Although the presence of niobium or tantalum enhances the catalytic activity, especially the catalyst's stability, those catalysts that are calcined in inert atmosphere show superior performance when compared with catalysts of identical formulation and calcined in air. 4. It is not necessary to charge the niobium or tantalum as the oxy anion, or even as the anion. Any soluble form of niobium or tantalum is capable of providing the catalytic function.

Claims: I claim: 1. A rhenium free catalyst for the oxidation of ethylene to ethylene oxide comprised of silver on a solid support and containing a promoter combination consisting of (1) an alkali metal component and (2) a niobium or tantalum component, and a sulfur component. 2. The catalyst of claim 1 containing a cesium component and a niobium component. 3. The catalyst of claim 1 containing a cesium component and a tantalum component. 4. The catalyst of claim 1 containing a promoting amount of fluorine.

Inventors: RIZKALLA NABIL, RIZKALLA, NABIL
Applicants: SCIENT DESIGN CO, SCIENTIFIC DESIGN COMPANY, INC.
Application year: 1997
Main classification: B01J23
IPC codes: B01J23, B01J27, C07D301