RIGID ISOCYANURATE-MODIFIED POLYURETHANE FOAMS

Abstract: Rigid isocyanurate-modified polyurethane foams of index 180 to 380 made from a combination of aliphatic and aromatic polyester polyols.

Description: DESCRIPTION RIGID ISOCYANURATE-MODIFIED POLYURETHANE FOAMS This invention relates to rigid isocyanurate-modified poiyurethane foams and to processes for their preparation. Rigid isocyanurate-modified poiyurethane foams are in general prepared by reacting a stoichiometric excess of polyisocyanate with isocyanate-reactive compounds in the presence of blowing agents, surfactants and catalysts. One use of such foams is as a thermal insulation medium in, for example, buildings . Isocyanurate-modified poiyurethane foams exhibit better fire retardancy than poiyurethane foams in general due to the presence of the isocyanurate groups; however, these foams tend to be extremely friable leading to a deterioration of other properties such as surface cure and adhesion. To obtain good fire properties polyester polyols are advantageously used as isocyanate-reactive compounds in the making of isocyanurate-modified poiyurethane foams. Usually these polyester polyols are of aromatic nature and are, in some cases, used in combination with polyether polyols. Therefore it is an object of the present invention to provide rigid isocyanurate-modified poiyurethane foams having a combination of desirable properties, including an appropriate reactivity profile and a reduced friability. According to the present invention rigid isocyanurate-modified poiyurethane foams are provided formed by reacting an organic polyisocyanate composition with an isocyanate-reactive composition at an isocyanate index of 180 to 380 -, preferably 200 to 270 -, most preferably 220 to 250 z , wherein the isocyanate-reactive composition comprises an aliphatic polyester polyol and an aromatic polyester polyol. The isocyanurate-modified poiyurethane foams of the present invention are less friable than those of the prior art made from aromatic polyester poiyois only, yielding improved physical properties such as surface cure and adhesion. Tney are especially useful m maKing building panels where the foam is applied to one or more incombustible skins. US 4302551 describes the use of polymer dispersions in the manufacture of rigid polyisocyanurate foams. These polymer dispersions comprise a continuous phase and a dispersed p.iase; as the continuous phase polyester polyols can be used. The present invention is not carried out by using polymer dispersions. US 4859523 describes the use of aromatic polyester polyols together with aliphatic polyester polyols in the manufacture of viscoelastic resins (thus not rigid polyisocyanurate foams). FR 1548298 relates to the use of mixtures of aliphatic and aromatic polyester polyols in the manufacture of thermoplastic polyester-urethanes (thus not rigid polyisocyanurate foams) . The term isocyanate index as used herein is meant to be the molar ratio of NCO-groups over reactive hydrogen atoms present in the foam formulation, except for those derived from any water present, given as a percentage. The polyester polyols for use in the present invention advantageously have an average functionality of about 1.8 to 8, preferably about 1.8 to 5 and more preferably about 2 to 2.5. Their hydroxyl number values generally fall within a range of about 15 to 750, preferably about 30 to 550 and more preferably about 200 to 550 mg KOH/g. Preferably the polyester polyols have an acid number between 0.1 and 20 mg KOH/g; m general the acid number can be as high as 90 mg KOH/g. The polyester polyols of the present invention can be prepared by known procedures from a polycarboxylic acid or acid derivative, such as an anhydride or ester of the polycarboxylic acid, and any polyol component. The polyacid and/or polyol components may be used as mixtures of two or more compounds m the preparation of the polyester polyols. Tne polyols can be aliphatic, c/cloaliphatic, aromatic and/or heterocyclic. Low molecular weight aliphatic polyhydπc alcohols, such as aliphatic dihydπc alcohols having no more than about 20 carbon atoms are highly satisfactory. The polyols optionally may include substituents which are inert m the reaction, for example, chlorine and bromine substituents, and/or may be unsaturated. Suitable amino alcohols, such as, for example, monoethanolaimne, diethanolamine, tπethanolamine, or the like may also be used. A prererreα polyol component is a glycol . The glycols may contain heteroatorαs te.g., thiodiglycol > or may be composed solely of carbon, nydrogen and oxygen. They are advantageously simple glycols of the general formula C-h^tOH) or polyglycols distinguished by intervening ether linkages in the hydrocarbon chain, as represented by the general formula C n H n O, (OH) . Examples of suitable polyhydric alcohols include: ethylene glycol, propylene glycol -(1,2) and -(1,3), butylene glycol -(1,4) and -(2,3), hexanediol - (1,6), octanediol -(1,8), neopentyl glycol, 1, 4-bιshydroxymethyl cyclohexane, 2-methyl-l, 3-propane diol, glycerin, tnmethylolethane, hexanetriol -(1,2,6), butanetπol -(1,2,4), quinol, methyl glucoside, triethyleneglycol, tetraethylene glycol and higher polyethylene glycols, dipropylene glycol and higher polypropylene glycols, diethylene glycol, glycerol, pentaerythritol, trimethylolpropane, sorbitol, manmtol, dibutylene glycol and higher polybutylene glycols. Especially suitable polyols are alkylene glycols and oxyalkylene glycols, such as ethylene glycol, diethylene glycol, dipropylene glycol, triethylene glycol, tripropylene glycol, tetraethylene glycol, tetrapropylene glycol, trimethylene glycol, tetramethylene glycol and 1, 4-cyclohexanedιmethanol (1, 4-bιs-hydroxymethylcyclohexane) . The polycarboxylic acid component may be aliphatic, cycloaliphatic, aromatic and/or heterocyclic and may optionally be substituted, for example, by halogen atoms and/or may be unsaturated. Examples of suitable carboxylic acids and derivatives thereof for the preparation of the polyester polyols include- oxalic acid, malonic acid, adipic acid, glutaric acid, succmic acid, pimelic acid, suberic acid, azelaic acid, sebacic acid, phthalic acid, phthalic acid anhydride, terephthalic anhydride, isophthalic acid, terephthalic acid, trimellitic acid, tetrahydrophthalic acid anhydride, pyromellitic dianhydride, hexahydrophthalic acid anhydride, tetrachlorophthalic acid anhydride, endomethylene tetrahydrophthalic anhydride, glutaric acid anhydride, maleic acid, maleic acid anhydride, terephthalic acid dimethylester, terephthalic acid-bis glycol ester, fumaric acid, dibasic and tribasic unsaturated fatty acids optionally mixed with monobasic unsaturated fatty acids, such as oleic acids. While the polyester polyols can be prepared from substantially pure reactant materials, more complex ingredients can be used, such as the side-stream, waste or scrap residues from the manufacture of phthalic acid, terephthalic acid, dimethyl terephthalate, polyethylene terephthalate, and the like. These compositions can be converted by reaction with polyols to polyester polyols through conventional transesterification or esterification procedures . The production of the polyester polyols is accomplished by simply reacting the polycarboxylic acid or acid derivative with the polyol component in a known manner until the nydroxyl and aciα values of the reaction mixture fall m the desired range. After transesterification or esterification the reaction product can optionally be reacted with an alkylene oxide. The term "polyester polyol" as useα herein includes any minor amounts of unreacted polyol remaining after the preparation of the polyester polyol and/or unesterified polyol (e.g., glycol) addeα after the preparation The polyester polyol can advantageously include up to about 40 *, by weight free glycol Preferably tne free glycol content is from 2 to 30, more preferably from 2 to 15 - by weight of the total polyester polyol component. In the aliphatic polyester polyol both the polyol and the polycarboxylic acid used to make the polyester polyol are aliphatic compounds. However some of the polyol or the polycarboxylic acid may be of aromatic nature; the aromaticity of the aliphatic polyester polyol (expressed as weight % of groups containing at least one aromatic ring per molecule) being below 50 %. In the aromatic polyester polyol at least one of the polyol or the polycarboxylic acid, preferably the acid, is an aromatic compound and the aromaticity is at least 50 %. Polyester polyols whose acid component advantageously comprises at least 30 % by weight of phthalic acid (or isomers thereof) residues are particularly useful. Preferably the aromaticity of the aromatic polyester polyol is between 70 and 90 % . Preferred aromatic polyester polyols are the crude polyester polyols obtained by the transesterification of crude reaction residues or scrap polyester resins. One or more different aromatic and one or more different aliphatic polyester polyols may be used according to the present invention. The weight ratio of aromatic and aliphatic polyester polyols to be used in the present invention is preferably between 90:10 and 20-80, more preferably between 80:20 and 30:70, most preferably between 80:20 and 40:60. For the production of the isocyanurate-modified poiyurethane foams of the present invention the polyester polyols described above preferably constitute the totality of the reactive mixture reacted with the polyisocyanate; it is understood, however, that these polyols could also be used mixed with other isocyanate-reactive compounds conventionally used in the art; preferably the isocyanate-reactive composition includes at least 90 - by weight of the polyester polyols described above. The isocyanate-reactive compounds which can be employed in combination with the polyester polyols in the preparation of the isocyanurate-modified poiyurethane foams of the present invention include any of those known in the art for that purpose. Of particular importance for the preparation of rigid foams are polyols and polyol mixtures having average hydroxyl numbers of from 300 to 1000, especially from 300 to 700 mg KOH/g, and hydroxyl functionalities of from 2 to 8, especially from 3 to 8. Suitable polyols nave been fully described in the prior art and include reaction products of alkylene oxides, for exampie ethylene oxide and/or propylene oxide, with initiators containing from 2 to 8 active hydrogen atoms per molecule, suitable initiators include: polyols, for example glycerol, trimethylolpropane, triethanolamme, pentaerythπtol, sorbitol and sucrose; polyarmnes, for example ethylene diamine, tolylene diamine, diaminodiphenylmethane and polymetnylene polyphenylene polyarmnes; and aminoalcohols, for example ethanolamine and diethanolamine; and mixtures of such initiators. Further suitable polymeric polyols include hydroxyl terminated polythioethers, polyamides, polyesteramides, polycarbonates, polyacetals, polyolefins and polysiloxanes. Suitable organic polyisocyanates for use in the process of the present invention include any of those known in the art for the preparation of rigid isocyanurate-modified poiyurethane foams, and in particular the aromatic polyisocyanates such as diphenylmethane dusocyanate in the form of its 2,4'-, 2,2'- and 4, 4 '-isomers and mixtures thereof, the mixtures of diphenylmethane dusocyanates (MDI) and oligomers thereof known in the art as "crude" or polymeric MDI (polymethylene polyphenylene polyisocyanates) having an isocyanate functionality of greater than 2, toluene dusocyanate in the form of its 2,4- and 2,6-ιsomers and mixtures thereof, 1, 5-naphthalene dusocyanate and 1, 4-diisocyanatobenzene. Other organic polyisocyanates which may be mentioned include the aliphatic dusocyanates such as isophorone dusocyanate, 1, 6-dιιsocyanatohexane and 4, 4 ' -dusocyanatodicyclohexylmethane. Further suitable polyisocyanates for use in the process of the present invention are those described in EP-A- 0320134. Modified polyisocyanates, such as carbodnmide or uretonimine modified polyisocyanates can also be employed. Still other useful organic polyisocyanates are isocyanate-terminated prepolymers prepared by reacting excess organic polyisocyanate with a minor amount of an active hydrogen-containing compound. Preferred polyisocyanates to be used in the present invention are the polymeric MDI ' s . The quantities of the polyisocyanate composition and the polyfunctional isocyanate-reactive composition to be reacted are such that the molar ratio of isocyanate (NCO) groups to active-hydrogen groups (OH) (excluding water) is generally between 180 and 380 *, preferably between 200 and 270 t and most preferably between 220 and 250 t . The process of the present invention is carried out in the presence of any of the blowing agents known in the art for the preparation of rigid isocyanurate-modified poiyurethane foams. Such blowing agents include water or other carbon dioxide-evolving compounds, or inert low boiling compounds having a boiling point of above -70°C at atmospheric pressure. Where water is used as blowing agent, the amount may be selected in known manner to provide foams of the desired density, typical amounts being in the range from 0.05 to 5 * by weight based on the total reaction system. Suitable inert blowing agents include those well known and described in the art, for example, hydrocarbons, dialkyl ethers, alkyl alkanoates, aliphatic and cycloaliphatic hydrofluorocarbons, hydrochlorofluorocarbons, chlorofluorocarbons, hydrochlorocarbons and fluorine-containing ethers. Examples of preferred blowing agents include isobutane, n-pentane, isopentane, cyclopentane or mixtures thereof, 1, l-dιchloro-2-fluoroethane (HCFC 141b) , 1, 1, l-trιfluoro-2-fluoroethane (HFC 134a) , chlorodifluoromethane (HCFC 22), 1, 1-dιfluoro-3,3, 3-trιfluoropropane (HFC 245fa) and blends thereof. Particular mention may be made of blowing agent mixtures as described in WO 96/12758, incorporated herein by reference, for manufacturing low density, dimensionally stable rigid foam. These blowing agent mixtures generally comprise at least 3 and preferably at least 4 components of which preferably at least one is a (cyclo) alkane (preferably of 5 or 6 carbon atoms) and/or acetone. The blowing agents are employed in an amount sufficient to give the resultant foam the desired bulk density which is generally m the range 15 to 70 kg/m , preferably 20 to 50 kg/m , most preferably 25 to 40 kg/m 3 . Typical amounts of blowing agents are in the range 2 to 25 * by weight based on the total reaction system When a blowing agent has a boiling point at or below ambient it is maintained under pressure until mixed with the other components. Alternatively, it can be maintained at subambient temperatures until mixed witn the other components. In addition to the polyisocyanate and polyfunctional isocyanate-reactive compositions and the blowing agent, the foam-forming reaction mixture will commonly contain one or more other auxiliaries or additives conventional to formulations for the production of rigid isocyanurate-modified poiyurethane foams. Such optional additives include crosslmking agents, for examples low molecular weight polyols such as tπethanolamine, processing aids, viscosity reducers, dispersing agents, Dlasticizers, mold release agents, antioxidants, fillers (e.g. carbon black) , cell size regulators such as insoluble fluoπnated compounds (as described, for example, in US 4981879, US 5034424, US 4972002, EP 0508649, EP 0498628, WO 95/18176), catalysts, surfactants such as polydimethylsiloxane-polyoxyalkylene block copolymers and non-reactive and reactive fire retardants, for example halogenated alkyl phosphates such as tris chloropropyl phosphate, triethylphosphate, diethyletnylphosphonate and dimethylmethylphosphonate The use of such additives is well known to those skilled in the art. Catalysts to be used in the present invention include those which promote the isocyanurate formation Examples include alkali metal or alkaline earth metal salts of carboxylic acids. The cation of the organic acid metal salt, which is preferably an alkali metal salt, advantageously is K or Na, more preferably K Particularly preferred are C 1 -C 8 carboxylate salts, including the sodium and potassium salts of formic, acetic, propionic and ethylhexanoic acids Other suitable trimeriεation catalysts include tnazine compounds such <-ι^ Polycat 41 (available from Air Products) and quaternary ammonium carboxylaL<_ salts. Catalyst combinations can be used as well such as described in EP 228230 and GB 2288182, including combinations with urethane catalysts which promote the reaction between an isocyanate group and an active hydrogen-containing group such as tertiary amines In operating the process for making rigid foams according to the invention, the known one-shot, prepolymer or semi-prepolymer techniques may be used together with conventional mixing methods and the rigid foam may be produced m the form of slabstock, mouldings, cavity fillings, sprayed foam, frothed foam or laminates with other materials such as hardboard, plasterboard, plastics, paper or metal It is common practice in the manufacture of rigid poiyurethane foams to utilize two preformulated compositions, commonly called the A-component and the B-component Typically, the A-component contains the polyιsocyanat_> compound and the B-compσnent contains the polyols together with the blowing agents, catalysts and other auxiliaries The foams of the present invention are advantageously used for producing laminates whereby the foam is provided on one or both sides with a facing sheet The laminates are advantageously made in a continuous manner by depositing the foam-forming mixture on a facing sheet being conveyed along a production line, and preferably placing another facing sheet on the deposited mixture Any facing sheet previously employed to produce building panels can be employed and can be of a rigid or flexible nature The various aspects of this invention are illustrated, but not limited by the following examples in which the following ingredients are used DALTOLAC P 710 an aliphatic polyester polyol (aromaticity 28 %) available from Imperial Chemical Industries STEPANPOL PS 2502A an aromatic polyester polyol (aromaticity 75 %) available from Stepan Isoexter 4537 an aliphatic polyester polyol available from COIM DALTOLAC R105: a polyether polyol available from Imperial Chemical Industries . Isoexter 4565: an aliphatic polyester polyol available from COIM. DALTOLAC P744: an aliphatic polyester polyol available from Imperial Chemical Industries. Terate 203: an aromatic polyester polyol (aromaticity 89 %) available from Hoechst Celanese. Terate 2541: an aromatic polyester polyol (aromaticity 78 % ) available from Hoechst Celanese. TCPP: tris chloropropyl phosphate, a fire retardant available from Courtalds . Polycat 43: a catalyst available from Air Products. L6900: a silicone surfactant available from OSI. Niax Al : a catalyst available from OSI. Catalyst LB: a catalyst available from Imperial Chemical Industries. Polycat 8: a catalyst available from Air Products. DMEA: a catalyst available from Imperial Chemical Industries. SUPRASEC 2085: a polymeric MDI available from Imperial Chemical Industries. SUPRASEC and DALTOLAC are trademarks of Imperial Chemical Industries. EXAMPLE 1 Rigid foams were prepared from the ingredients listed below in Table 1. The reaction profile was followed in respect of cream time, string time and tack free time. Free rise density was determined (according to standard DIN 53420) . The surface friability of the obtained foams was checked visually. Facing adhesion was measured acoordmg to standard ASTM D162. Paper peel adhesion was evaluated qualitatively with 100 g/rrr paper; 1 meaning good (paper break) , 2 meaning medium peeling requiring some strength, 3 meaning poor (peeling is very easy) . The results are presented in Table 1 below. These results show that using aliphatic polyester polyols in addition to aromatic polyester polyols reduces the friability of the obtained foams and improves the adhesion. Table 1

Claims: CLAIMS 1. Process for making rigid isocyanurate-modified poiyurethane foams comprising the step of reacting an organic polyisocyanate composition with an isocyanate-reactive composition at an isocyanate index of 180 to 380 % in the presence of a blowing agent, characterised in that the isocyanate-reactive composition comprises an aliphatic polyester polyol and an aromatic polyester polyol. 2. Process according to claim 1 wherein said process is carried out in the absence of polymer dispersions. 3. Process according to claim 1 or 2 wherein the isocyanate index is between 200 and 270 % . 4. Process according to claim 3 wherein the isocyanate index is between 220 and 250 %. 5. Process according to any one of the preceding claims wherein the polyester polyols have an average functionality of about 1.8 to 8 and an hydroxyl value of about 15 to 750 mg KOH/g. 6. Process according to any one of tne preceding claims wherein the polyester polyols are prepared from a polycarboxylic acid or acid derivative and a polyol. 7. Process according to claim 6 wherein the polyol is a glycol or a polyglycol distinguished Dy intervening etner linkages in the hydrocarbon chain. 8. Process according to claim 6 or 7 wherein the polycarboxylic acid or acid derivative is selected from the group comprising adipic acid, glutaric acid, succinic acid, phthalic acid and its derivatives .including isophthalic and terephthalic acid) and residues. 9. Process according to claim 6 wherein the polycarboxylic acid used to make the aromatic polyester polyol is of aromatic nature. 10. Process according to any one of the preceding claims wherein the aromaticity of the aromatic polyester polyol is at least 50 % by weight . 11. Process according to any one of the preceding claims wherein the weight ratio of aromatic and aliphatic polyester polyols is between 80 : 20 and 40 : 60 . 12. Process according to any one of the preceding claims wherein the aromatic and aliphatic polyester polyols constitute at least 90 % by weight of the total isocyanate-reactive compounds. 13. Process according to any one of the preceding claims wherein the organic polyisocyanate is a polymeric MDI. 14. Process according to any one of the preceding claims wherein the blowing agent comprises a hydrocarbon. 15. Process according to claim 14 wherein the blowing agent is n-pentane, isobutane, isopentane, cyclopentane or any mixture thereof. 16. Process according to any one of the preceding claims wherein the reaction is carried out in the presence of a trimensation catalyst. 17. Rigid isocyanurate-modified poiyurethane foam obtainable by the process as defined in any one of the preceding claims. 18. Use of a foam as defined in claim 17 for making laminates. 19. Isocyanate-reactive composition comprising an aromatic polyester polyol and an aliphatic polyester polyol. 20 Isocyanate-reactive composition according to claim 19 wherein the weight ratio of aromatic and aliphatic polyester polyols is between 80:20 and 40:60. 21. Isocyanate-reactive composition according to claim 19 or 20 wherein the aromatic and aliphatic polyester polyols constitute at least 90 *, by weight of the total isocyanate-reactive compounds. 22. Isocvanate-reactive composition according to any one of claims 19 to 2ι further comprising a blowing agent. 23 Isocyanate-reactive composition according to any one of claims 19 to 22 further comprising a trimerisation catalyst.

Inventors: BONAPERSONA VITTORIO, JAVARONE CRISTINA, MAGNANI FRANCO, BONAPERSONA, VITTORIO, JAVARONE, CRISTINA, MAGNANI, FRANCO
Applicants: ICI PLC, IMPERIAL CHEMICAL INDUSTRIES PLC
Application year: 1997
Main classification: C08G18
IPC codes: C08G18, C08G101