HEATING GLASS SHEETS IN TEMPERING FURNACE

Abstract: A method and an equipment for heating glass sheets in a tempering furnace provided with rollers. The tempering furnace (1) according to the invention comprises rollers (3) for conveying and oscillating the glass sheets (4) during heating, and resistors (5, 6) for heating the glass sheets (4) from above and from below. In accordance with the invention, the lower part of the tempering furnace (1) is cooled at the initial stage of the heating period, and the lower surfaces of the glass sheets (4) are heated at the final stage of the heating period by forced convection. This ensures good control over heat equalization in the tempering furnace (1), increases furnace power, and allows the curving of the glass sheets (4) to be prevented, and also the heat shock from ceramic rollers to the glass sheet (4) to be reduced at the initial heating stage.

Description: HEATING GLASS SHEETS IN TEMPERING FURNACE The invention relates to a method of heating glass sheets in a tem¬ pering furnace provided with rollers, in which method the glass sheets are led on a roller conveyer through the tempering furnace, the glass sheets being heated from above and from below, and the glass sheets being oscillated in a reciprocating manner on the rollers, and the lower part of the tempering fur¬ nace being cooled during the heating period The invention also relates to an equipment for heating glass sheets in a tempering furnace provided with rollers, the equipment comprising a tem- peπng furnace, means for heating the glass sheets from above and from be¬ low, horizontal rollers inside the tempering furnace which support a horizontal glass sheet and form its conveyor, the rollers being adapted to oscillate the glass sheet in a reciprocating manner during heating, and means for cooling the lower part of the tempering furnace Current glass tempering machines employ what are known as os¬ cillating roller furnaces in which glass is heated mainly by radiation In the tempering process the temperature of the glass is increased above the sof¬ tening point of glass in order to enable the glass to be tempered Said tem¬ perature is between 610 and 625°C depending on the thickness of the glass The glass is then cooled at desired speed typically using forced convection whereby air jets are blown at the glass from above and from below This method enables high heat-transfer coefficients, necessary when thin glass is concerned in order to achieve a sufficient temperature difference between the surface and centre of the glass Examples of oscillating roller furnaces are dis- closed in FI patents 83,072 and 86,407 A problem with roller furnaces is that heat transmission from mas¬ sive rollers to glass is predominant particularly at the initial heating stage The glass is supported by the rollers all the time, and particularly at the initial heating stage, with the temperature difference between the hot rollers and the glass being considerable, heat transmission from the hot rollers to the glass by conduction is abundant This makes the edges of the glass bend upwards, the contact surface between the glass and the rollers becoming quite indefinite In this case, uniform heating of glass is almost impossible as the contact point where the glass touches the roller becomes heated at the initial stage signifi- cantly faster than the rest of the glass surface This easily causes curving, making uniform heating with normal heating times almost impossible Further, the surface pressure at the point of contact of the glass touching the roller be¬ comes high enough to subject the glass to optical faults, i e white marks and scratches, breaking the surface of the glass Furthermore, the conditions in the furnace change during the heat- ing period in tempering furnaces provided with rollers The temperature of the glass changes relative to time and, particularly, heat transmission from the rollers diminishes as the temperature of the glass approaches the temperature of the rollers On the other hand, the temperature of the rollers falls at the ini¬ tial stage of the heating period when the thermal current taken up by the glass is at its highest This causes the problem of keeping the heating of the upper and lower parts the furnace balanced during the entire heating period FI patent 62,043 discloses a method and device for preventing the curving of glass sheets in a furnace provided with rollers in a horizontal tem¬ pering plant In accordance with the cited publication, an air current is gener- ated on the upper surface of a glass sheet in order to intensify the convection heat effect directed at the upper surface of the glass sheet The blowing serves to compensate for the active heat transmission caused by the hot roll¬ ers to the lower surface of the glass sheet at the initial heating period, but said blowing does not completely equalize the differences in the heat currents af- fecting the upper and lower surfaces, as the lower surface of the glass gets a stronger heat current from above, particularly during initial heating, causing the above mentioned problems FI patent 83,072 also discloses a method and a device for prevent¬ ing the curving of glass sheets in a furnace provided with rollers in a horizontal tempering plant It is known from said publication to direct an expanded con¬ vection heat effect at the upper surface of a glass sheet by blowing air at the furnace from blowpipes disposed in the vicinity of the upper surface of the glass sheet Said publication further discloses that the furnace space below the glass sheet is cooled by leading the air to be blown into the furnace via heat exchange pipes provided underneath the glass sheet to blowpipes lo¬ cated on the upper side Said arrangement is, however, quite complex and does not provide control of the equalization of heat in the tempering furnace duπng the entire heating period It is the object of the present invention to provide a method and an equipment for preventing the curving of glass sheets in a tempering furnace provided with rollers, avoiding the above mentioned drawbacks and providing good control of the equalization of heat during the entire heating period The method of the invention is characterized in that at the final stage of the heating period the lower surfaces of the glass sheets are heated by forced convection The equipment of the invention is characterized in that the equip¬ ment comprises means for heating the lower surfaces of the glass sheets by forced convection during the heating period It is an essential idea of the invention that, at the initial stage of the heating period, the lower part of the tempering furnace is cooled, and at the final stage of the heating period the lower surfaces of the glass sheets are heated by forced convection Furthermore, it is the idea of a preferred em¬ bodiment that the lower part of the tempering furnace is cooled with cooling pipes arranged in every second roller gap, and the lower surfaces of the glass sheets are heated by forced convection similarly by heating pipes arranged in every second roller gap It is the idea of still another preferred embodiment that the cooling pipes are provided with holes from which air jets at room tem¬ perature are blown at the rollers for cooling the surface temperature of the rollers and the lower part of the furnace It is the idea of a third embodiment that the cooling is adjusted by changing the speed of the air passing in the It is an advantage of the invention that the glass is prevented from curving, resulting in glass with optimal planaπty It still an advantage that the thermal shock from the rollers to the glass can be reduced at the initial heating stage It is a further advantage that heat equalization in the tempering furnace can be very well adjusted, and furnace power can be increased The invention will be described in more detail in the attached draw¬ ings in which Figure 1 schematically shows a sectional side view of a horizontal tempering furnace according to the invention, Figures 2a and 2b show a sectional side view of a detail of the de¬ vice of Figure 1 , and Figure 3 shows the device of Figure 1 from below and in section Figure 1 schematically shows a sectional side view of a horizontal tempering furnace 1 according to the invention The tempering furnace 1 com- prises a housing 2 and rollers 3 upon which glass sheets 4 are placed During the tempering process, the glass sheets 4 are transferred by means of the rollers 3 in the direction of arrow A. As seen in the Figure, a loading table is arranged on the left side of the tempering furnace 1 , and a cooling unit for the glass sheets 4 on the right side of the tempering furnace 1 For the sake of clarity, said loading table and cooling unit are not shown in Figure 1 The glass sheets 4 are placed on the loading table upon the rollers 3 The rollers 3 are typically e.g ceramic rollers inside the tempering furnace 1 and e.g. metal roll¬ ers coated with kevlar band outside the furnace The glass sheets 4 are transferred as one load into a heating chamber confined by the housing 2. The glass sheets 4 are typically heated from above with upper resistors 5 and from below with lower resistors 6 in a manner fully known per se. A different manner of heating, such as forced convection or a combination of different heating manners, is also feasible. In the furnace, the temperature of the glass is raised to 610 to 625°C depending on the thickness of the glass In the tempering furnace 1 , the glass sheets 4 undergo a back-and- forth movement, i.e. are oscillated, in a manner fully known per se, for arrang¬ ing the roller support points evenly upon the entire glass through the entire heating stage This is a way to minimize deformations in the glass optics caused by uneven support of the glass Cooling pipes 7 are arranged in every second roller gap between the rollers 3 transversely relative to the travel direction of the glass sheet 4 Air at room temperature is typically blown through said cooling pipes 7 The pipe serves as a shadow for heat radiation originating from below the glass and also as means for conducting heat out. Heat is transferred to the pipe by con¬ vection from the furnace air surrounding it and by direct radiation from near-by surfaces, such as the ceramic rollers 3 and the lower resistors 6 of the fur¬ nace The heat is conveyed through the pipe from the outer surface of the pipe to its inner surface from which it is conveyed by convection into air with which it is removed In the invention, the temperature of the outer surface of the cooling pipe 7 is kept, if needed, significantly below the temperature of the tempering furnace 1 by means of air flowing through the cooling pipe 7 The magnitude of the thermal current transferred to the cooling pipe 7 is easily ad¬ justable by adjusting the speed of the air in the cooling pipe 7 The need for cooling changes relative to time, since with the difference in temperature be¬ tween the glass sheet 4 and the roller 3 becoming smaller, the smaller is the amount of heat to be removed from the tempering furnace 1 This is why the speed of the air is reduced during the entire heating period The effect of a single cooling pipe 7 can be improved by enlarging the diameter of the pipe or by ribbing it Heating pipes 8 are arranged in different roller gaps as compared with the cooling pipes 7, also preferably in every second roller gap They are provided with machined holes, whereby hot air jets, typically at 650 to 720°C, can be blown from said heating pipe 8 at the lower surface of the glass sheet 4 from between the rollers 3 The diameter of the holes in the heating pipe 8 is typically 1 to 2 mm, but may vary even more from case to case The heating pipes 8 are used for heating at the final stage of the heating period when the heating of the glass sheet 4 is typically quite slow, and, in the case of full loads, the ceramic rollers 3 may even start to cool ex¬ cessively In these cases, said additional heating at the final stage of the heating period increases the power of the tempering furnace 1 It is obvious that coohng by the cooling pipes 7 and heating by the heating pipes 8 are not employed simultaneously, the system being forced controlled in order to elimi¬ nate concomitant operation Figure 1 shows further that the air supplied to the heating pipes 8 arranged between the rollers 3 is led to pass via pipes 8a located below the lower resistors 6 This way the lower resistors 6 make the air warm up in said pipes 8a When using heat blowing, the lower resistors 6 are allowed to start to cool, but with said solutions the heat remaining in them may, however, still be utilized for heating the heating air Figures 2a and 2b show a sectional side view of a detail of the tem¬ pering furnace 1 of Figure 1 The numbering of Figures 2a and 2b corresponds to that of Figure 1 In Figure 2a, arrows B show the movement of the air jets blown from the heating pipes 8 If desired, the hot air blown from the heating pipes 8 may also be aimed directly at the rollers 3 The cooling pipes 7, too, may be used for blowing air directly at the rollers 3 for cooling the rollers 3 and the part of the tempering furnace 1 below the glass sheet 4 Said current of cooling air is illustrated by arrows C in Figure 2b The solution according to Figures 2a and 2b allow cold air to be blown di¬ rectly at the rollers 3 at the initial heating stage, whereby the rollers cool down and hot air to be blown at the final heating stage, whereby the temperature of the rollers 3 may be raised Figure 3 shows the tempering furnace of the invention from below and in section The numbering of Figure 3 corresponds to that of Figures 1 and 2 Figure 3 shows the heating pipes 8 arranged in every second roller gap, but for the sake of clarity does not show the cooling pipes 7, also ar¬ ranged in every second roller gap, but in different gaps than the heating pipes Hot air is fed to the heating pipes 8 via delivery pipes 9 The heating pipes 8 and the delivery pipes 9 are arranged such that hot air is fed to the heating pipes 8 from both sides of the tempering furnace 1 so that air is fed to every second heating pipe 8 from above as seen in Figure 3, and to every second from below This eliminates the impact of the heat inside the tempering fur¬ nace 1 on the temperature of the air passing inside the heating pipes 8 Far more important is, however, the temperature of the air passing inside the cooling pipes, and thus said cooling pipes have to be arranged in a corre¬ sponding manner, so that cooling air is fed alternately from different sides of the tempering furnace 1 This is an easy way to even out potential unilateral cooling of the rollers 3 The pressure source of the air blown by the heating pipes 8 may be e g a compressor 10 After the compressor 10, the air is heated in what is called a heating radiator 11 In the heating radiator 11 the air to be blown is heated in advance to the temperature of the tempering furnace 1 , and in some cases even more The heating radiator 11 may be e.g. a chamber in which a combination of pipes and resistors has been built such that the air blown into the furnace is forced to circulate inside the pipes tens of metres in adjacent spirals In the immediate vicinity of the pipes, preferably in contact with the pipe, are arranged thermal resistors for warming up the pipes and the air in¬ side them to the desired temperature The heating radiator 11 may also be implemented in some other manner fully known per se, and hence the heating radiator 11 is not described in any more detail here It is essential that the air blown into the tempering furnace 1 can be heated to the desired temperature and that it does not essentially cool down before the tempering furnace 1 In practice this is implemented by providing the heating radiator 11 and the pipes between the heating radiator 11 and the tempering furnace 1 with proper in¬ sulation Further, in connection with the pipes there is a regulator 12 for ad¬ justing the air flow and thus the magnitude of the desired additional heating The pipes further comprise a valve 13 which may be e g a magnetic valve By means of said valve 13 the air flow can be entirely blocked, if desired Similar pipes and devices as shown in Figure 3 in connection with the heating pipes 8 are arranged in connection with the cooling pipes except of course for the heating radiator 11 During a heating period, first the cooling pipes are taken in the use, whereby air at room temperature is blown through the cooling pipes 7 ar¬ ranged between the rollers 3 The air warms up when being conveyed across the tempering furnace 1 and carries heat away from the tempering furnace 1 and particularly from the rollers 3 The heating of the lower side is entirely or partially switched off Next the glass load at room temperature is transferred to the tempering furnace 1 where it is oscillated in a reciprocating manner and heated from above and from below The cooling of the lower side is decreased continuously by lowering the speed of the air passing through the cooling pipes 7 At the same time the heating effect of the lower resistors 6 of the tempering furnace 1 is usually increased Next, approximately in the middle of the heating period, heating is entirely ceased and direct heating of the lower surface of the glass sheet 4 is initiated by forced convection Direct heating of the lower surface of the glass sheet 4 is increased gradually towards the end of the heating period and simultaneously the heating effect of the lower resis¬ tors 6 is increased Finally the glass is transferred to the cooling unit and the direct heat blowing of the lower side is switched off and the cooling pipes are switched on For the sake of clarity, the attached figures do not show e g the support structures of the pipes and rollers or the control and rotation means of the rollers, these being known per se to those skilled in the art Further, for the sake of clarity, the rollers 3, for example, are shown fewer in number and greater in relation to their natural size The drawing and the related description are only intended to illus¬ trate the idea of the invention As to its details, the invention may vary within the scope of the claims This means that the cooling pipes and the heating pipes may also be arranged in the same roller gap, and in this case the heat¬ ing pipe may be arranged above the cooling pipe and fixed to the cooling pipe, for example In this case the cooling pipes and the heating pipes may be lo¬ cated both in each roller gap

Claims: CLAIMS 1 A method of heating glass sheets in a tempering furnace pro¬ vided with rollers, in which method the glass sheets (4) are led on a roller (4) conveyer through the tempering furnace (1), the glass sheets (4) being heated from above and from below, and the glass sheets (4) being oscillated in a re¬ ciprocating manner on the rollers (3), and the lower part of the tempering fur¬ nace (1) being cooled during the heating period, characterized in that at the final stage of the heating period the lower surfaces of the glass sheets (4) are heated by forced convection 2 A method as claimed in claim ^characterized in that the lower part of the tempering furnace (1) is cooled the initial stage of the heating period 3 A method as claimed in claim 1 or 2, characterized in that cooling is implemented by blowing air through cooling pipes (7) and that the efficiency of the cooling is adjusted by changing the speed of the air pass¬ ing in the cooling pipes (7) 4 A method as claimed in any on of the preceding claims, char¬ acterized in that cooling is implemented by blowing air through the cool¬ ing pipes (7) and that cooling air is fed alternately from different sides of the tempering furnace (1) 5 A method as claimed in any on of the preceding claims, char¬ acterized in that heating the glass sheets (4) with forced convection is implemented by heating pipes (8) such that heating air is fed alternately from different sides of the tempering furnace (1) 6 A method as claimed in any on of the preceding claims, char¬ acterized in that cooling the lower part of the tempering furnace (1) is implemented by means of the cooling pipes (7) such that the cooling pipes (7) are provided with holes from which air jets are blown at the rollers (3) for cool¬ ing the roller (3) surfaces and the lower part of the tempering furnace (1) 7 A method as claimed in any on of the preceding claims, char¬ acterized in that forced convention is implemented by hot air jets blown at the lower surface of a glass sheet (4), the temperature of the air blown be¬ 8 An equipment for heating glass sheets in a tempering furnace provided with rollers, the equipment comprising a tempering furnace (1), means for heating the glass sheets (4) from above and from below, horizontal rollers (3) inside the tempering furnace (1) which support a horizontal glass sheet (4) and form its conveyor, the rollers (3) being adapted to oscillate the glass sheet (4) in a reciprocating manner during heating, and means for cool- mg the lower part of the tempering furnace (1), c h a ra c te rize d in that the equipment comprises means for heating the lower surfaces of the glass sheets (4) by forced convection during the heating period 9 An equipment as claimed in claim 8, characterized in that cooling is implemented by cooling pipes (7) which are disposed in every sec- ond roller gap and through which air is arranged to be blown, and the heating of the lower surfaces of the glass sheets (5) by convection is arranged to be implemented by heating pipes (8), disposed in every second roller gap such that the cooling pipes (7) and the heating pipes (8) are in different roller gaps 10 An equipment as claimed in claim 8 or 9, characterized in that cooling is implemented by the cooling pipes (7) and that the cooling pipes (7) are arranged such that the air blown through them is blown alter¬ nately from different sides of the tempering furnace (1 ) 11 An equipment as claimed in claim 9 or 10 character¬ ized in that the cooling pipes (7) are provided with holes, allowing the rollers (3) to be cooled by air blown through the holes in the cooling pipes (7) 12 An equipment as claimed in claims 9 to 11, character¬ ized in that the equipment comprises means for adjusting the speed of the air blown through the cooling pipes (7)

Inventors: VEHMAS JUKKA, VEHMAS, JUKKA
Applicants: UNIGLASS ENGINEERING OY, VEHMAS JUKKA, VEHMAS, JUKKA
Application year: 1997
Main classification: C03B27
IPC codes: C03B25, C03B27, C03B29, C03B35