Filling material for fibre optical cables

Abstract: Disclosed are hydrophobic compositions useful for filling the voids within jacketed optical fiber cables. The compositions include about 85 to 95 parts by weight of mineral oil, 5 to 15 parts by weight of a (styrene) - (ethylene/propylene) diblock copolymer having a styrene: (ethylene/propylene) ratio of 37.5:62.5 to 27.5:72.5 and a specific gravity of about 0.90 to 0.95, optional antioxidant, and optional metal deactivator. The oil is selected from naphtanic mineral oils comprising 45 to 50 wt.% naphtanics and the balance paraffins and having a pour point of -45°F to -25°F and poly-alphaolefins and mixtures thereof having a pour point of -100°F to -50°F.

Description: The present invention relates to fiber optic cables incorporating a unique composition which protects the signal-carrying components of the cable from damage during manufacture, installation and use. The present invention relates more particularly to the unique composition which imparts the desirable protective properties described herein to the fiber optical cable. Generally, in optical fiber cables a plurality of optical fibers (generally about 100) are enclosed together in an extruded plastic tube, often referred to as a "buffer tube". A plurality of these units, generally about 6-50, are enclosed in a common extruded plastic tube-like sheath. Even in the most compact of manufactures, there are usually voids between the optical fibers inside the buffer tube. The present invention relates particularly to a filling compound that can be filled into the voids inside the buffer tube. Optical fiber cables are subject to various stresses and shocks during manufacture, installation and use, any of which poses a risk of damage to the signal-carrying conductors within the cable. Such events can include stretching or compression of the conductors; compression of one or more of the conductors against the jacket; fracture of all or a portion of a conductor; and cracking or perforation of the jacket such that water can penetrate and disturb the functioning of the conductors. Accordingly, it has been proposed to incorporate a filler material within the cable, to fill the voids between the conductors and between the conductors and the interior surface of the buffer tube. Such a filler material should desirably afford protection to the conductors against physical dislocation and damage, while remaining sufficiently flexible that the cable can be used in any conventional manner in which it is used during manufacture, installation and use. Such a filler material should also protect against the incursion of water in the event that water is able to penetrate within the jacket. The identification of a completely satisfactory cable filler composition has not been simple. In particular, such a composition must be sufficiently fluid that it can readily be fed into the interior of the cable during manufacture, and should also be sufficiently flexible that the cable can be coiled or bent in the manner to which it may be exposed particularly during manufacture and installation. The filler composition must not be so fluid that it flows out of the cable, through the cut ends thereof or through punctures or cracks in the buffer tube that may occur. In addition, since filler compositions are usually mixtures of materials, it is highly desirable that the filler composition would resist any tendency of the several components to separate one from the other, even on exposure to any of the wide range of physical challenges and environmental conditions to which the cable may be subjected. Examples of cable filler systems which have been disclosed in the past include mixtures of oil with a colloidal gelling agent such as fumed silica, together with an amount of a copolymer such as a styrene-rubber or styrene-rubber-styrene block copolymer. Examples are disclosed in U.S. Patent No. 4,971,419, U.S. Patent No. 5,285,513 and U.S. Patent No. 5,358,664, the last of which discloses a gelled oil composition which employs aluminium complex soaps as gelling agents. The oils may be used as filling compounds for waveguides. The oil composition comprises 40-90 % of an oil component, 4-15 % of an aluminium soap complex, and 5-50 % of a bleed inhibitor. The oil component may be a naphthenic minimum oil having an aromatic content of 0-11 %, a naphthenic content of 31-46 % and a paraffinic content of 51-65 %. The bleed inhibitor may be inter alia a styrene-rubber block copolymer. It would be desirable to be able to identify satisfactory filler compositions useful in fiber optical cables, which exhibit the desirable properties described herein better than existing filler compositions. It would also be useful if such a filler composition does not require a distinct inorganic gelling agent such as those described in the aforementioned patents. According to a first aspect, the present invention provides a composition useful as a filling material for substantially filling voids between fiber optical conductors in a fiber optic cable, wherein the filling material consists essentially of (a) 85 to 95 parts by weight of naphthenic mineral oils comprising 45 to 50 wt.% naphthenics and the balance paraffins; (b) 5 to 15 parts by weight of a (styrene) - (ethylene/propylene) diblock copolymer having a styrene: (ethylene/propylene) ratio of 37.5:62.5 to 27.5:72.5, a Shore A hardness of 70 to 75 and a specific gravity of about 0.90 to 0.95; characterized in that the naphthenic mineral oils exhibit a viscosity at 40°C of 19 to 66 centistokes, a viscosity at 100°C of 3.5 to 7.5 centistokes, a viscosity index of 40 to 65, a specific gravity at 15.6°C of 0.87 to 0.90, a pour point of -43°C to -32°C (-45°F to -25°F), and an average molecular weight of 310 to 400; and in that the composition optionally further includes: (c) an antioxidant component in an amount if present up to 2 parts by weight; and (d) a metal deactivator in an amount if present up to 0.1 part by weight. According to a second aspect, the present invention provides a method for producing the above-described composition comprising the steps of: combining 85 to 95 parts by weight of naphthenic mineral oils comprising 45 to 50 wt.% naphthenics and the balance paraffins; 5 to 15 parts by weight of a (styrene)-(ethylene/propylene) diblock copolymer having a styrene:(ethylene/propylene) ratio of 37.5:62.5 to 27.5:72.5, a Shore A hardness of 70 to 75 and a specific gravity of about 0.90 to 0.95; and optionally, an antioxidant component in an amount if present up to 2 parts by weight and/or a metal deactivator in an amount if present up to 0.1 part by weight; and stirring the mixture thoroughly until a homogenous liquid is formed; characterized in that the naphthenics mineral oils exhibit a viscosity at 40°C of 19 to 66 centistokes, a viscosity at 100°C of 3.5 to 7.5 centistokes, a viscosity index of 40 to 65, a specific gravity at 15.6°C of 0.87 to 0.90, a pour point of -43°C to -32°C (-45°F to-25°F), and an average molecular weight of 310 to 400. The present invention is further directed to a cable comprising a plurality of conductors contained within a jacket, leaving voids between the conductors and the jackets, wherein said filling material is present substantially filling the voids. The components of the cable other than the filler composition described in more detail herein, include any of those conventionally employed in the optical fiber cable industry. Generally speaking, the cable comprises several individual signal-carrying fibers, encased together in a buffer tube which is preferably composed of thermoplastic polymer and is preferably of a unitary, seamless, construction. One component of the filling material of the present invention is naphthenic mineral oil. The oil is present in an amount corresponding to 85-95 parts by weight of the filling material. Naphthenic mineral oils are a commercially recognized type of product which contain 45 to 50 wt.% naphthenics and the balance paraffins. Generally, the naphthenic mineral oils useful in this invention exhibit the properties set forth in Table 1: Property Preferred Range Viscosity, 40°C. (ASTM D-445) 19 to 66 centistokes (cSt) Viscosity, 40°C. (ASTM D-445) 3.5 to 7.5 cSt Viscosity index (ASTM D-2270) 40 to 65 Specific gravity, 15.6°C. (ASTM D-1298) 0.87 to 0.90 Pour point (ASTM D-97) (-45°F. to -25°F.) -43°C to -32°C Average molecular weight 310 to 400. Preferred examples of naphthenic mineral oils include those sold by Witco Corp. as "LP 100", "LP 150", "LP 200", "LP 250", LP 300" and "LP 350". The filling material of the present invention also includes 5 to 15 parts by weight of a (styrene) - (ethylene/propylene) diblock copolymer. The diblock copolymer has a mole ratio of styrene to (ethylene/propylene) rubber in the range of about 37.5:62.5 to about 27.5:72.5, and a Shore A hardness of 70 to 75. The preferred diblock copolymer also exhibits a specific gravity of about 0.90 to 0.925. A preferred copolymer exhibiting these characteristics and useful in the present invention is the product sold by Shell Chemical Company under the trade name "KRATON G1701", a styrene(ethylene/propylene) block copolymer, unplasticized, which exhibits a styrene: (ethylene/propylene) ratio of about 37:63, a Shore A hardness of 72, a specific gravity of about 0.92, and a break strength of 300 psi (as determined by ASTM test D-412). Another preferred copolymer is sold by Shell under the name "KRATON G1702". It is a styrene(ethylene/propylene) block copolymer, unplasticized, which exhibits a styrene: (ethylene/propylene) ratio of about 28:72, a Shore A hardness of 75, a specific gravity of about 0.91, and a break strength of 300 psi (ASTM D-412). The filling material does not need to include any additional gelling component or "antibleed" component, while providing very satisfactory performance in the intended environment with an optical fiber cable. If desired, though, another gelling compound such as fumed silica is optionally included as well. However, one may optionally include one or more antioxidants, and one may also optionally include a metal deactivator. An antioxidant component, if present, is used in a small but effective amount which is generally on the order of up to about 2 parts by weight. Examples of suitable antioxidants include phenolic-based and phosphite-based antioxidants. Examples are plentiful and are well known in the field of polymer formulations. Specific examples include "Irganox 1010", "Irganox 1076", "Irganox 1035", (Ciba-Geigy) and "Mark 2112", "Mark 1500", and "Mark 5014" (Witco), A metal deactivator, if present, is used in a small but effective amount generally on the order of up to about 0.1 part by weight of the filling material. Examples of suitable metal deactivators include "Reomel 39 LF" and other commercially available products known in this field. The filling material of the present invention is readily prepared by combining the mineral oil and the diblock copolymer in the indicated amounts, together with antioxidant and/or metal deactivator if desired, and stirring the materials together thoroughly until a homogeneous liquid is formed. If desired, gentle heating can be applied to assist the formation of the desired completely homogeneous composition. In a preferred procedure, the components are mixed together at low shear at 25°C. The mixture is then heated to 120-130°C, until the polymer is completely dissolved in the oil. The blend is then cooled to 25°C under vacuum to remove any entrapped air bubbles. The resulting composition is then fed into the buffer tube, preferably at the point that the cable is being manufactured, all by procedures well known in this field. The benefits and superior performance of the present invention are described further in the following examples. These examples are included for purposes of illustration and are not intended to limit the scope of that which is regarded as the invention. EXAMPLES Formulations were made by combining oil and styrene-(ethylene/propylene) diblock copolymer ("Kraton G 1701") in a mixer for several hours at 130°C. The samples were then cooled and centrifuged at moderate speed to remove any entrapped air. The rheological properties of the gels which resulted were studied with a Brookfield Model RVF Viscometer with a #7 spindle at 22°C and 55% humidity according to ASTM D1824 (which recommends 23±1°C and 50±5% humidity). Each sample was sheared for two minutes at four different rotations (2,4,10, and 20 rpm, which corresponds to shear rates of 0.1, 0.05, 0.02, and 0.01 sec -1 , respectively). In order to evaluate the handling characteristics of the samples the apparent viscosities were measured and the following criteria were calculated: shear thinning index, degree of thixotropy, and thixotropy index. These criteria, which are defined below, were calculated as recommended by ASTM 2196 with one modification. The apparent viscosities measured in consideration for the shear thinning index evaluation were made at 2 and 10 rpm, whereas the method specifies typical combinations of speeds at 2 and 20 rpm. As defined by ASTM D2196, the shear thinning index is the ratio between the viscosity at 2 rpm to the viscosity at 10 rpm. The degree of thixotropy is a ratio of the viscosity at 2 rpm, taken with increasing speed to that with decreasing speed. The thixotropy index is the ratio of the viscosity at 2 rpm taken after a rest period of 30 minutes to that before the rest period. The volatility test was conducted at 80°C and aged for 48 hours. The volatilities were measured by comparing the weight loss of the filling compound before and after the aging. The oil separation test was conducted according to FED 791 at 80°C for 48 hours. The cone penetration values were determined by ASTM D937, with a 150 gram weight. The oils used are described in Table 3: Property Oil A B Viscosity, 40°C. (cSt) 19.5 37.5 Viscosity, 100°C. (cSt) 3.6 5.4 Viscosity Index 40. 53.9 Pour Point, °C -40. -37. Flash Point,°C 170. 190. Color Saybolt +30. +30. Oils A and B were commercial naphthenic mineral oils, sold under the names "LP 100" and "LP 200" (Witco), respectively. Table 4 shows for each sample the identity of the oil, the amount of diblock copolymer gelling agent present, and the physical properties of the resulting gel. In all cases the gels exhibited properties showing that they are very satisfactory cable fillers.

Claims: A composition useful as a filling material for substantially filling voids between fiber optical conductors in a fiber optic cable, wherein the filling material consists essentially of (a) 85 to 95 parts by weight of naphthenic mineral oils comprising 45 to 50 wt.% naphthenics and the balance paraffins; (b) 5 to 15 parts by weight of a (styrene) - (ethylene/propylene) diblock copolymer having a styrene: (ethylene/propylene) ratio of 37.5:62.5 to 27.5:72.5, a Shore A hardness of 70 to 75 and a specific gravity of about 0.90 to 0.95; characterized in that the naphthenic mineral oils exhibit a viscosity at 40°C of 19 to 66 centistokes, a viscosity at 100°C of 3.5 to 7.5 centistokes, a viscosity index of 40 to 65, a specific gravity at 15.6°C of 0.87 to 0.90, a pour point of -43°C to -32°C (-45°F to -25°F), and an average molecular weight of 310 to 400; and in that the composition optionally further includes: (c) an antioxidant component in an amount if present up to 2 parts by weight; and (d) a metal deactivator in an amount if present up to 0.1 part by weight. A cable comprising a plurality of conductors contained within a jacket leaving voids between the conductors and the jacket, and a filling material according to Claim 1 substantially filling said voids. A method for the production of a composition according to Claim 1 comprising the steps of: combining 85 to 95 parts by weight of naphthenic mineral oils comprising 45 to 50 wt.% naphthenics and the balance paraffins; 5 to 15 parts by weight of a (styrene)-(ethylene/propylene) diblock copolymer having a styrene: (ethylene/propylene) ratio of 37.5:62.5 to 27.5:72.5, a Shore A hardness of 70 to 75 and a specific gravity of about 0.90 to 0.95; and optionally, an antioxidant component in an amount if present up to 2 parts by weight and/or a metal deactivator in an amount if present up to 0.1 part by weight; and stirring the mixture thoroughly until a homogenous liquid is formed; characterized in that the naphthenics mineral oils exhibit a viscosity at 40°C of 19 to 66 centistokes, a viscosity at 100°C of 3.5 to 7.5 centistokes, a viscosity index of 40 to 65, a specific gravity at 15.6°C of 0.87 to 0.90, a pour point of -43°C to -32°C (-45°F to -25°F), and an average molecular weight of 310 to 400. Use of the composition according to Claim 1 in the manufacture of a cable according to Claim 2.

Inventors: COSTELLO MICHAEL, DEBSKA-CHWAJA ANNA, ECKARD ALAN, THALMAN WILLIAM, COSTELLO, MICHAEL, DEBSKA-CHWAJA, ANNA, ECKARD, ALAN, THALMAN, WILLIAM
Applicants: CROMPTON CORP, CROMPTON CORPORATION
Application year: 1997
Main classification: G02B6
IPC codes: C10M169, G02B6, C08L23, H01B11, C08L57