Adhesive composition

Abstract: An adhesive composition obtainable by blending a component (C) to components (A) and (B), wherein the weight ratio of (A)/(B) is from 95/5 to 40/60, and the amount of the component (C) is from 5 to 50 parts by weight based on 100 parts by weight of the total amount of the components (A) and (B) wherein: (A) is a condensate of resorcinol and formaldehyde or a condensate of resorcinol, phenol and formaldehyde, (B) is an aqueous emulsion containing an ethylenevinyl acetate-based copolymer and the weight ratio of ethylene/vinyl acetate is from 3/97 to 40/60, and (C) is a formaldehyde-based hardening agent or a hexamethylenetetramine-based hardening agent.

Description: BACKGROUND OF THE INVENTION Field of the Invention The present invention relates to an adhesive composition. More particularly, it relates to an adhesive composition containing a resorcinol-based adhesive as a base, which can maintain adhesive ability and gelation time at fully satisfactory levels, provides excellent processability after hardening of an adhesive by imparting suitable plasticity to the adhesive, does not cause cracking of an adhesive layer, and realizes excellent productivity. Description of the Related Art A resorcinol-based adhesive mainly composed of a resorcinol resin is an excellent adhesive in view of being able to maintain high adhesion for long periods. However, the resorcinol-based adhesives have problems that a hardened adhesive layer is extremely hard; therefore when a wood article obtained by adhesion is cut, a cutting blade used is split, and when the adhesive layer is thick, cracking occurs. US 4,687,809 describes a room temperature setting adhesive composition containing (A) an emulsion containing an acetoacetylated polyvinyl alcohol and a vinyl acetate copolymer produced by copolymerizing an acetoacetylated, ethylenically unsaturated monomer and another ethylenically unsaturated monomer and (B) a resorcinol resin precondensate and, as a curing agent, (C) hexamethylenetetramine. SUMMARY OF THE INVENTION The present inventors have intensively studied an adhesive composition which does not have the above-mentioned problems and have found that an adhesive composition obtainable by blending a specific amount of a specific copolymer to a resorcinol resin can maintain adhesive ability and gelation time at fully satisfactory levels, provides excellent processability after hardening of an adhesive by imparting suitable plasticity to the adhesive, does not cause cracking of an adhesive layer, and realizes excellent productivity. Thus the inventors have completed the present invention. That is, the present invention provides an adhesive composition obtainable by blending a component (C) to components (A) and (B), wherein the weight ratio of (A)/(B) is from 95/5 to 40/60, and the amount of the component (C) is from 5 to 50 parts by weight based on 100 parts by weight of the total amount of the components (A) and (B), wherein: (A) is a condensate of resorcinol and formaldehyde or a condensate of resorcinol, phenol and formaldehyde, (B) is an aqueous emulsion consisting essentially of an ethylene-vinyl chloride-based copolymer and the weight ratio of ethylene/vinyl chloride is from 3/97 to 40/60, and (C) is a formaldehyde-based hardening agent or a hexamethylenetetramine-based hardening agent. The component (A) is a condensate of resorcinol and formaldehyde, or a condensate of resorcinol which is partly substituted by phenol, phenol and formaldehyde. The component (A) is a resin obtained by addition condensation of not more than 1 mol of formaldehyde to 1 mol of resorcinol or 1 mol of total amount of resorcinol and phenol. As the component (A), corresponding commercially available products can be used. The component (B) of the present invention is an aqueous emulsion consisting essentially of an ethylene-vinyl chloride-based copolymer and the weight ratio of ethylene/vinyl chloride is from 3/97 to 40/60. When the ratio of ethylene is too low, plasticity effect by the component (A) cannot be obtained since plasticity effect by the aqueous emulsion decreases. On the other hand, when the ratio is too high, sufficient strength of an adhesive layer cannot be obtained and adhesion strength decreases. The weight ratio of ethylene/vinyl chloride is preferably from 5/95 to 35/65. The solid content of the aqueous emulsion is preferably from 30 to 70%. The component (B) is produced by usual emulsion polymerization. When the aqueous emulsion consisting essentially of an ethylene-vinyl chloride-based copolymer is obtained, it is preferable to use an anionic surfactant as an emulsifier in polymerization for easy miscibility with the component (A). The examples of the anionic surfactant include sodium lauryl sulfate, sodium dodecylbenzene sulfonate, sodium dialkylsulfo succinate, sodium polyoxyethylenealkyl ether sulfate, sodium polyoxyethylenealkylphenol ether sulfate and the like. When the emulsion system of the component (B) is a protective colloid system such as polyvinyl alcohol and hydroxyethyl cellulose, it is preferable that pH of the component (B) is previously regulated at not less than 7 to improve miscibility with the component (A). On the other hand, when the emulsion system of the component (B) is an anionic surfactant, it is possible to conduct sufficient mixing with the component (A) even if regulation of pH is not conducted previously. The component (C) of the present invention is a formaldehyde-based hardening agent or a hexamethylenetetramine-based hardening agent. As the formaldehyde-based hardening agent, formaldehyde, paraformaldehyde and the like are exemplified. As the hexamethylenetetramine-based hardening agent, hexamethylenetetramine and the like are exemplified. Such a hardening agent is added mainly for hardening of the component (A), and optionally, fillers such as a walnut shell powder, palm shell powder, wood powder, bark powder and the like, and bulking agents such as a wheat flour and the like can also be added. Further, it is also possible to use an amino resin and phenol resin containing free formaldehyde, or formaldehyde as a hardening agent. As the component (C), corresponding commercially available products may be used. The adhesive composition of the present invention is an adhesive composition obtainable by blending the component (C) to the above-described components (A) and (B), wherein the weight ratio of (A)/(B) is from 95/5 to 40/60, and the amount of the component (C) is from 5 to 50 parts by weight based on 100 parts by weight of the total amount of the components (A) and (B). The amount of the component (B) is based on the weight of the total amount of aqueous emulsion comprising the copolymer and water. And the amount of the component (C) is based on the weight of the total amount of the hardening agent comprising some kinds of additives. when the weight ratio of the component (B) is too low, plasticity effect of an adhesive layer cannot be fully obtained, and effects for preventing splitting of a blade when an adhered wood is processed and for preventing cracking which occurs when the adhesive layer is too thick are not shown. The ratio is preferably from 90/10 to 50/50. When the amount of the component (C) is too small, excellent adhesion cannot be obtained since hardening of the component (A) becomes insufficient. On the other hand, when the amount is too large, excess hardening agent remains in the adhesive layer, and when used as a building material, there is a problem that released volatile components exert a bad influence on human bodies. The amount of the component (C) is preferably from 10 to 30 parts by weight. To obtain the adhesive composition of the present invention, for example, the following methods are listed. The component (A) is mixed with the component (B) to obtain a mixture. When the composition is used as an adhesive, the component (C) is added to the mixture and the resulting mixture is applied on an adherent. It is also possible that the component (B) is mixed with the component (C), and the component (A) is added directly before use. As the adherent, for example, wood, slate, concrete and the like can be used. In the adhesive composition of the present invention, adhesive ability and gelation time are maintained at fully satisfactory levels, and suitable plasticity is given to an adhesive; therefore, processability after hardening of the adhesive is excellent, cracking in an adhesive layer scarcely occurs, and production cost can be suppressed. EXAMPLES The following examples further illustrate the present invention in detail; however, needless to say, they are not to be construed to limit the scope thereof. Examples 1-9 and Comparative Examples 1-5 The adhesive compositions were obtained by blending the components (C) to the components (A) and (B) described in Tables 1 to 3. The resulting adhesive compositions were subjected to measurements and evaluations as follows. The conditions and results are shown in Tables 1 to 3. The measuring and evaluation methods for adhesion ability, gelation time, hardness and cracking are as follows. 1. Evaluation of adhesion ability The evaluation was conducted according to Phenolic Resin Adhesives for Wood (JIS K 6802). (1) Preparation of sample The adhesive as blended above was applied on each one side of two pieces of straight-grained birch boards (10 mm × 25 mm × 30 mm) in a total amount from 0.16 to 0.20 g (260 to 320 g/m 2 ), the applied surfaces were put to each other in a layer and pressed for 24 hours at a load of 8 kgf/cm 2 , then left for 1 week to obtain a sample. (2) Ordinary condition strength Compressive-shear adhesive strength of the sample as prepared above was measured by a compression tester (Autograph DCS-5000) manufactured by Shimadzu Co. The ordinary condition strength is preferably not less than 100 kgf/cm 2 . (3) Repeated boiling strength The sample as prepared above was immersed in boiling water for 4 hours, dried in an oven at 60°C for 20 hours, immersed again in boiling water for 4 hours, then immersed in water at ordinary temperature for 15 minutes or more to be cooled to ordinary temperature, and compressive-shear adhesive strength of the sample was measured in wet condition by a compression tester (Autograph DCS-5000) manufactured by Shimadzu Co. The repeated boiling strength is preferably not less than 60 kgf/cm 2 . 2. Gelation time Gelation time was measured according to Phenolic Resin Adhesives for wood(JIS K 6802). An adhesive main agent obtained by blending the components (A) and (B) was immersed in a thermostatic bath at 25°C for 1 hour or more. After the temperature of the adhesive main agent reached constant temperature, the component (C) was quickly mixed with stirring with reading the start time simultaneously, and the adhesive was immersed in a thermostatic bath at 25°C. Then, this adhesive was sometimes stirred, and the time until the adhesive was not sticky to a stirring rod was measured when the stirring rod was contacted with the surface of the adhesive and lifted. The gelation time is preferably from 20 to 300 minutes. 3. Hardness The adhesive composition was charged in a vessel having a flat bottom so that the thickness thereof was 12 mm or more, and allowed to stand for 4 days or more without any treatment for hardening to obtain a cylindrical sample. Using this sample, there was conducted measurement of A hardness of spring type hardness test using a rubber plastic digital mode hardness tester (RH-101A) manufactured by Excell K.K. according to Vulcanized Rubber Physical Test Method (JIS K 6301). The hardness is preferably from 30 to 60. 4. Cracking The appearance of the sample used for the hardness test was observed, and evaluated by ○ (no cracking), Δ (slight cracking) and × (cracking). Example Comparative example 1 2 3 4 1 Formulation (A) Kind*1 (parts by weight) A-1 70 A-2 70 A-3 70 A-3 70 A-1 70 (B) Kind*2 (parts by weight) B-1 30 B-1 30 B-1 30 B-2 30 B-3 30 (c) Kind*3 (parts by weight) C-1 21 C-1 21 C-1 21 C-1 21 C-1 21 Evaluation result Compressive-shear adhesive strength Ordinary condition (kgf/cm 2 ) 143 192 172 184 170 Wood part fracture rate (%) 0 15 80 75 20 Repeated boiling (kgf/cm 2 ) 69 88 86 74 74 Wood part fracture rate (%) 30 90 80 55 70 Gelation time (minute) 90 60 60 60 20 Hardness (-) 52 55 56 57 34 Cracking ○ ○ ○ ○ ○ Comparative example Example 2 5 6 7 Formulation (A) Kind*1 (parts by weight) A-3 70 A-2 50 A-3 50 A-1 90 (B) Kind*2 (parts by weight) B-4 30 B-1 50 B-1 50 B-1 10 (c) Kind*3 (parts by weight) C-1 21 C-1 15 C-1 15 C-1 27 Evaluation result Compressive-shear adhesive strength Ordinary condition (kgf/cm 2 ) 165 141 173 198 Wood part fracture rate (%) 100 30 60 5 Repeated boiling (kgf/cm 2 ) 79 71 76 75 Wood part fracture rate (%) 75 90 90 25 Gelation time (minute) 20 60 60 90 Hardness (-) 56 43 46 60 Cracking ○ ○ ○ Δ Comparative example 3 4 5 6 7 Formulation (A) Kind (parts by weight) A-1 100 A-2 100 A-3 100 A-2 35 A-2 35 (B) Kind (parts by weight) - 0 - 0 - 0 B-3 65 B-1 65 (c) Kind (parts by weight) C-1 30 C-1 30 C-1 30 C-1 11 C-1 11 Evaluation result Compressive-shear adhesive strength Ordinary condition (kgf/cm 2 ) 153 194 198 142 149 Wood part fracture rate (%) 0 65 65 10 20 Repeated boiling (kgf/cm 2 ) 74 80 78 43 49 Wood part fracture rate (%) 65 100 80 10 25 Gelation time (minute) 90 60 60 20 60 Hardness (-) 60 62 66 28 33 Cracking × × × ○ ○

Claims: An adhesive composition obtainable by blending a component (C) to components (A) and (B), wherein the weight ratio of (A)/(B) is from 95/5 to 40/60, and the amount of the component (C) is from 5 to 50 parts by weight based on 100 parts by weight of the total amount of the components (A) and (B), wherein: (A) is a condensate of resorcinol and formaldehyde or a condensate of resorcinol, phenol and formaldehyde, (B) is an aqueous emulsion consisting essentially of an ethylene-vinyl chloride-based copolymer and the weight ratio of ethylene/vinyl chloride is from 3/97 to 40/60, and (C) is a formaldehyde-based hardening agent or a hexamethylenetetramine-based hardening agent. An adhesive composition according to claim 1, wherein the aqueous emulsion (B) is prepared by using an anionic surfactant as an emulsifier in polymerization. An adhesive composition according to claim 1 or 2, wherein component (A) is a condensate of resorcinol and formaldehyde. An adhesive composition according to claim 1 or 2, wherein component (A) is a condensate of resorcinol, phenol and formaldehyde.

Inventors: SHIBATA YUTAKA, TOMIZAWA CHOJI, SHIBATA, YUTAKA, TOMIZAWA, CHOJI
Applicants: SUMITOMO CHEMICAL CO, SUMITOMO CHEMICAL COMPANY, LIMITED
Application year: 1997
Main classification: C09J161
IPC codes: C08L61, C08L31, C09J131, C09J161