ALKALINE CLEANING FORMULATION CONTAINING A HYDROLYZED SILANE AND METHOD OF APPLYING THE SAME

Abstract: An alkaline cleaning formulation containing a hydrolyzed trialkoxysilane, a surfactant, an alcohol and water is disclosed. The cleaning formulation is stable, provides excellent cleaning efficacy and deposits a silane coating on the surfaces to which it is applied to leave a protective coating thereon. Also disclosed is a method for applying the cleaning formulation to hard surfaces covered by water.

Description: ALKALINE CLEANING FORMULATION CONTAINING A HYDROLYZED SILANE AND METHOD OF APPLYING THE SAME Technical Field This invention relates to an alkaline cleaning formulation containing a hydrolyzed trialkoxysilane The formulation is applied to hard surfaces to clean the surface and provide a uniform silane coating on the cleaned surface The invention also relates to a method for applying the alkaline cleaning formulation of this invention to hard surfaces covered by water Background Art It is known to apply silane cleaning solutions to surfaces to impart water repellency and provide a protective barrier on the treated surface For example, U.S Patent No. 4,948,531 discloses an aqueous cleaning composition comprising (a) one or two nonionic surfactants and an amphoteric surfactant as cleaning agents, (b) lecithin and an aminofunctional polydimethylsiloxane copolymer as protective barrier components, (c) one or two glycols as solvency and grease cutting agents, and (d) water The disclosed aminofunctional polydimethylsiloxane copolymer has the formula C H 2 I C H 2 I N H I C H 2 I C H , N H . and is available as Dow Corning 531 Fluid (Dow Corning Corporation, Midland, Michigan) which is a 50% solution in aliphatic solvents and isopropyl alcohol This composition is said to clean a surface and simultaneously leave a protective barrier on the cleaned surface U S Patent No 4,859,359 is directed to a hard surface cleaning and polishing composition comprising a solvent mixture of a glycol ether, a lower aliphatic alcohol, a hydrocarbon solvent and a minor amount of water together with an organic polysiloxane, a silane and a polycarboxylic chelating acid The silane compound, which is said to promote the solubility of the other silicone compounds in the mixture, is represented by the formula R 3 -Si(OR 4 ) 3 wherein R 3 is an alkyl radical containing one to three carbon atoms or phenyl and R 4 is an alkyl radical containing one or two carbon atoms The alkyl trialkoxysilanes are disclosed as preferable U.S. Patent 5,073,195 is directed to an aqueous solution of a water silane coupling agent, preferably an amino functional silane coupling agent, and an alkyltrialkoxysilane such as methyltrimethoxysilane or isobutyltrimethoxysilane The composition is used to treat a surface to impart water repellency to that surface Alkoxysilanes are known to hydrolyze upon exposure to water to form reactive silanol groups The silanol group may then condense with a reactive site on a treated surface However, if the silanol group is available during storage it may self-condense with other silanol groups to form an insoluble polymer Hydrolysis of silanes in aqueous medium may be reduced by buffering the emulsions to a specific pH range such as disclosed in U S Patent No 4,877,654 This patent describes a buffered aqueous silane emulsion containing a hydrolyzable silane that is hydrolytically stable within a determined pH range, an emulsifier having an HLB value of from 1 5 to about 20, a buffering compound and water However, a buffered composition restricted to a certain pH range can be particularly limiting to a formulator of cleaning compositions PCT Intemational Publication No WO 92/14810 discloses that certain organosilanes containing hydrolyzable groups, especially quaternary ammonium functional organosilanes, can form clear solutions in aqueous media which are stable over extended periods of time by including a water soluble organic, non-silicon quaternary ammonium compound along with nonionic, amphoteric, sarcosine anionic or certain cationic surfactants The use of hydrolyzed organosiloxanes is not exemplified. PCT International Publication No WO 95/23804 is directed to a hydrolyzed silane obtained by emulsifying a hydrolyzable alkoxysilane represented by the formula. R f -(CH 2 ) -Si{ (O-CH 2 CH 2 )-OR'} 3 wherein R f is a perfluoroalkyl radical of 3 to 18 carbon atoms, each R' is independently an alkyl radical of 1 to 3 carbon atoms, p is 2 to 4 and n is 2 to 10, with an effective amount of an emulsifier of sufficiently high HLB value to simultaneously retain the hydrolyzable alkoxysilane compound in a substantially totally hydrolyzed state while inhibiting the self-condensation of the hydrolyzed alkoxysilane. Suitable emulsifiers are said to include alkylbenzenesulfonates, linear alkydiphenyletherdisulfonates, alpha-olefin sulfonates, ethoxylated alkyl alcohol ethers, ethoxylated alkyl alcohol ether sulfates, ethoxylated alkylphenols, ethoxylated alkylphenol ether sulfates, ethoxylated perfluoroalkylalkanols, C 8- ι 8 alkyltrimethylammonium salts, Cg.jg alkyldimethylammonium salts, ethoxylated C 8- ιg amine salts, alpha-trimethylamino fatty acid betaines and perfluoroalkyl amphoteric surfactants of the type R r CH 2 CH(OR")CH 2 N(CH 3 ) 2 CH 2 CO 2 (inner salt) where R" is H or acetyl, and quaternary salts of the type R CH 2 CH 2 SCH 2 CH(OH)CH 2 N(CH 3 ) 3 + Cr According to PCT International Publication No. WO 95/23804, the alkoxysilanes are believed to be hydrolyzed to hydroxysilanes represented by the formula R f -(CH 2 ) -Si-(OH) 3 which do not substantially self-condense when the emulsifier is present A similar, but non-fluorinated, alkoxysilane aqueous emulsion is TLF-8291, available from E. I. Du Pont de Nemours and Company, Wilmington, Delaware TLF-8291 is believed to contain hydrolyzed Cig-alkyltrialkoxysilane (about 10% by weight of the emulsion) in combination with Cg.ig tetraalkylammonium chloride (about 30 to 40% by weight of the silane) in water While the hydrolyzed trialkoxysilane aqueous emulsion appears stable as provided, simple dilution of the aqueous emulsion has been found to give a commercially unacceptable cleaning formulation due to poor cleaning efficacy and silane attachment to glass containers holding such a formulation. Cleaning formulations containing hydrolyzed trialkoxysilanes, such as TLF- 8291, which are stable, avoid substantial silane attachment to glass storage containers, provide excellent cleaning, uniform surface deposition after wipe out, and excellent surface wetting and leveling would be highly desirable. Summary Disclosure Of The Invention This invention relates to an alkaline cleaning formulation for cleaning hard surfaces comprising: (i) a hydrolyzed trialkoxysilane in an amount from about 0.00001 to about 10.0 percent by weight of the formulation, (ii) a surfactant in an amount from about 0.00001 to about 10.0 percent by weight of the formulation, wherein the surfactant is different than the emulsifier, (iii) at least one alcohol having 1 to 12 carbon atoms; and (iv) water. The hydrolyzed trialkoxysilane is preferably formed in an aqueous emulsion from a hydrolyzable trialkoxysilane compound emulsified in water with about 5 to 100 percent by weight of an emulsifier based on the weight of the hydrolyzable trialkoxysilane The emulsifier employed to emulsify the hydrolyzable trialkoxysilane must be in an amount effective to keep the hydrolyzable trialkoxysilane in a substantially totally hydrolyzed state while simultaneously inhibiting appreciable self-condensation of the silane in the aqueous emulsion The formulation has a pH greater than 7.0 which is generally attained by the addition of a base Preferably, the alcohol is a mono, di or tri hydric alcohol The formulation may also include glycol ethers, solvents, fragrances and any other components well known to those skilled in the art of cleaning formulations. Another embodiment of the present invention is directed to the above- described cleaning formulation having reduced autophobicity, i_e_, the tendency of the formulation to repel itself after application to a hard surface It has been suφrisingly discovered that the autophobicity of the formulations of the present invention can be reduced by the addition of a siloxane to the formulation Such siloxanes include, for example, polydimethylsiloxane and derivative thereof Yet another embodiment of this invention is directed to a method of applying a silane coating to a surface covered by water by adding the above- described alkaline cleaning formulation to the water It has been surprisingly discovered that the hydrolyzed trialkoxysilane of the formulation of this invention attaches to and modifies the surface of substrates, such as glass, ceramic, fiberglass or porcelain, when applied to the water covering such a surface It has further been discovered that such surface modification occurs even when relatively low levels of the hydrolyzed trialkoxysiloxanes are added to the water covering such surfaces This method employing the alkaline cleaning formulations of this invention may be advantageously employed to clean and protect surfaces covered by water, e g toilet bowls, with a minimal use of materials and effort The cleaning formulations of this invention are particularly useful for cleaning hard surfaces such as glass, mirrors, tile, ceramic and the like while providing the cleaned surface with a protective silane coating The formulations of the invention are highly storage stable even when packaged in glass containers, effectively avoid substantial surface attachment of the active silane to the storage container, and thus preserve the active silane for attachment to treated surfaces Modes for Carrying Out the Invention This invention is directed to an alkaline cleaning formulation which contains a hydrolyzed trialkoxysilane in a stabilized formulation. The hydrolyzed trialkoxysilane is available for attachment to a surface treated with the aqueous alkaline cleaning formulations to form a protective barrier which advantageously inhibits the deposition of soils and grease on the treated surface. The hydrolyzed trialkoxysilane is derived from a hydrolyzable trialkoxysilane represented by the formula (I): R' -(CH 2 ) -Si{(-O-CH 2 CH 2 ) -OR'} 3 wherein R 1 is selected from the group consisting of a perfluoroalkyl group of 3 to 18 carbon atoms or an alkyl group of 3 to 24 carbon atoms, and R 2 is independently an alkyl group having 1 to 3 carbon atoms, p is 0 to 4 and n is 2 to 10. Preferably R 1 is an alkyl group of 3 to 24 carbon atoms and p is O, most preferably R 1 is an alkyl group having 18 carbon atoms and p is O. The amount of hydrolyzable trialkoxysilane used in the aqueous emulsion is generally in the range from about 0.00001 to about 25.0 percent by weight of the aqueous emulsion, most preferably from about 0.00001 to about 10.0 percent by weight. Any amount of hydrolyzable trialkoxysilane may be employed in the aqueous emulsion so long as the emulsion is stable prior to its use in preparing the cleaning formulation of this invention. The hydrolyzed trialkoxysilane may be readily prepared by one of ordinary skill in the art by emulsifying the hydrolyzable trialkoxysilane of formula I in water to form an aqueous emulsion with an emulsifier of sufficiently high HLB value to simultaneously retain the hydrob ible trialkoxysilane compound in a substantial totally h) ' olyzed state and inhi .he hydrolyzed trialkoxysilane compound from appreciate self-condensation. The preparation of aqueous emulsions of hydrolyzed trialkoxysilanes are shown, for example, in PCT Intemational Publication No. WP 95/23804, the disclosure of which is incorporated by reference herein. It may also be possible to form the hydrolyzed trialkoxysilane insitu by the admixture of a hydrolyzable trialkyoxysilane with the other components of the formulation of this invention. If present, the emulsifier generally has an HLB ("The HLB System" published by ICI America's Inc., Wilmington, Delaware) value greater than 12 However, when a non-fluorinated trialkoxysilane is employed, then preferably the HLB value of the emulsifier is greater that 16, more preferably greater than 18 Compatible emulsifiers may be used in admixture as long as each meets the above- defined HLB requirements. Emulsifiers that are preferred for use with a non-fluorinated trialkoxysilane include, without limitation, Cg.ig alkyltrimethylammonium quatemary salts, alkali metal alkylbenzene-sulfonates, linear alkyldiphenyletherdisulfonates, alpha-olefin sulfonates, alkyl and alkylether sulfates, C ]2 .ιg alkyldimethylammonium salts, polyethoxylated Cπ.ig alkylammonium salts and highly ethoxylated alkyl and aryl alcohols. Such emulsifiers include, for example, hexadecyltrimethylammonium chloride, the sodium salt of Cι -ι 6 alpha olefin sulfonate, octadecylamine-60 E.O. and octadecyldimethylammonium chloride. A particularly preferred emulsifier, particularly for use with a hydrolyzed trialkoxysilane where R 1 is a Cι 2 to C 2 alkyl group, is an ethoxylated C .i amine salt, more preferably tetraalkylammonium chloride, most preferably, having predominantly Ciβ-alkyl groups. Generally, about 5 to 100 percent by weight of an emulsifier based on the weight of the hydrolyzable alkoxysilane is employed in the aqueous emulsion. When R 1 is a alkyl group of 3 to 24 carbon atoms then preferably the emulsifier is present in an amount of 10 to 50% based on the weight of the silane, most preferably 30 to 40%. A particularly preferred commercially available hydrolyzed trialkoxysilane emulsion is previously described TLF-8291, available from E.I Du Pont de Nemours and Company (Wilmington, Delaware). Typically, the aqueous emulsion containing the hydrolyzed trialkoxysilane and emulsifier is present in the cleaning formulation in an amount from about 0.0001 to about 1.0 percent by weight of the cleaning formulation, most preferably from about 0.0001 to about 0.1 percent by weight. The amount of aqueous emulsion used in the cleaning formulation will, of course, depend on the concentration of the hydrolyzed trialkoxysilane in the aqueous emulsion. Thus, any amount of aqueous emulsion may be employed that provides an effective amount of hydrolyzed trialkoxysilane in the cleaning formulation to change the hydrophobicity of a treated surface by surface attachment of the hydrolyzed trialkoxysilane. Not wanting to be bound by any theory, but so as to provide a full disclosure, it is believed that the hydrolyzed trialkoxysilane is represented by (i) the formula (II): R'-(CH 2 ) -Si-(OH) 3 wherein R 1 and p are the same as described for formula I, (ii) by oligomers of formula II or (iii) mixtures thereof. The hydrolyzed trialkoxysilane may form oligomers by the self-condensation of the silanol groups of two or more hydrolyzed trialkoxysilanes so long as the oligomer remains soluble in the aqueous emulsion. Again, without wishing to be bound by any theory, it is believed that the hydrolyzed trialkoxysilane forms a micelle in conjunction with the emulsifier and that after this aqueous emulsion is diluted into a cleaning formulation the hydrolyzed trialkoxysilane is further protected and stabilized by the addition of the surfactants used in this invention in combination with at least one alcohol having 1-12 carbon atoms and by adjusting the pH of the formulation to an alkaline pH. This cleaning formulation allows delivery of the silane to a surface with excellent surface orientation after evaporation of the aqueous carrier. In addition, it is believed that the surfactant inhibits the silane, while in solution, from substantial surface attachment to the storage container and thus preserves the reactive silane for attachment to the treated surface upon application. The surfactants employed in the foπ.-ulation of this invention are selected from the group consisting of: nonionic surfactants such as, for example, linear ethoxylated alcohols (e.g., Neodol® 25-7 (C12-C15 alcohol, EO 7), Neodol® 23- 6.5 (C12-C13 alcohol, EO 6.5), Neodol® 1-7 (C12-C13 alcohol, EO 7), Neodol® 25-9 (C12-C15 alcohol, EO 9), Neodol® 45-7 (C14-C15 alcohol, EO 7), or Neodol® 91-6 available from Shell Chemical Co., Houston, Texas, Surfonic® L12- 8 (C11-C12 alcohol, EO 8), Surfonic® L12-6 (Cl 1-C12 alcohol, EO 6), Surfonic® L24-6.5 (C12-C14 alcohol EO 6.5), Surfonic® L24-7 (C12-C14 alcohol, EO 7), Surfonic® L24-9 (C12-C14 alcohol, EO 9) or Surfonic® 108-83-5 available from Huntsman Corp., Austin, Texas), alcohol ethoxy carboxylic acids (e.g.,Neodox® 23-7, Neodox® 25-6 or Neodox® 45-7) or other nonionic surfactants (e.g., Brij® 76 (polyoxyethylene (20) stearyl ether) or Brij® 97 (polyoxyethylene (10) oleyl ether) available from ICI Americas, Wilmington, Delaware, Pluronic® L-44 (block copolymers of propylene/ethylene oxide) available from BASF, Parsippany, New Jersey, Berol® 223 (fatty amine ethoxylate) available from Berol Nobel, Stratford, Connecticut, and Zonyl® FS-300 (fluoroalkyl alcohol substituted monoether with polyethylene glycol) available from E.I. Du Pont de Nemours and Co., Wilmington, Delaware; amphoterics, such as betaines (e.g., Emcol® CC37-18 available from Witco, Houston, Texas, Lonzaine® C or Lonzaine® CO (cocamidopropylbetaines) available from Lonza Inc., Fairlawn, N.J., Mirataine® BB (lauramidopropyl betaine), Mirataine® CB, or Mirataine® BET C-30 (cocamidopropyl betaines) available from Rhone-Poulenc, Cranbury, New Jersey, Monateric® CAB available from Mona Chemical Co., Paterson, New Jersey and Witco DP 5C-5298-53 (ClO dimethyl betaine) or Witco DP SC-5298-49 (C8 dimethyl betaine) available from Witco), sultaines (e.g., Mirataine® ASC (alkyletherhydroxypropylsultaine) or Mirataine® CBS (cocoamidopropylhydroxysultaine) available from Rhone Poulenc, Lonzaine® CS or Lonzaine® JS (cocoamidopropylhydroxysultaines) available from Lonza Inc., Fairlawn, N.J. and Rewoteric® AM CAS (cocoamidopropylhydroxysultaine) available from Witco), or imidazoline amphoterics (e.g., Amphoterge® W (cocoamphoacetate), Amphoterge® W-2 (cocoamphodiacetate), Amphoterge® K (cocoamphopropionate), Amphoterge® K- 2 (cocoamphodipropionate), Amphoterge® L (lauroamphodiacetate), Amphoterge® J-2 or Amphoterge® KJ-2 (capryloamphodipropionate) available from Lonza, Rewoteric® AM V (caprylic glycinate), Rewoteric® AM-KSF (cocoamphopropionate) or Rewoteric® AM 2L (lauroamphodiacetate) available from Witco, Phosphoteric® T-C6 (dicarboxyethyl phosphoethyl imidazoline), Monateric® Cy-Na or Monateric® LF-Na available from Mona, and Miranol® C2M (cocoamphodiacetate), Miranol® J2M (capryloamphodiacetate), or Miranol® JAS (imidazoline amphoteric) available from Rhone-Poulenc), and cationic surfactants such as amine oxides (e.g., Barlox® LF, Barlox® C, Barlox® 105, Barlox® 12, Barlox® 16S, or Barlox® 18S available from Lonza, Rhodamox® LO or Rhodamox® CO available from Rhone-Poulenc and Varox® 305 or Varox® 743 available from Witco), and quaternary cationic surfactants (e.g., Bardec® 208M or Barquat® 42802 available from Lonza and BTC 835 available from Stephan, Co., Northfield, Illinois), or dialkoxy alkyl quaternaries (e.g., Variquat® 66, Variquat® K-1215, Adogen® 444, Adogen® 461 or Adogen® 462 available from Witco). The particularly preferred amine oxides are represented by the formula: CH 3 RN→ O CH 3 wherein R is a C g to Cie alkyl group. Most preferably R is a Cn alkyl group. The surfactant employed in the formulation of this invention will differ from the emulsifier described above. At least one surfactant must be present, although, it may be preferable to employ more than one surfactant. Generally the surfactant or mixture of surfactants will be present in the formulation in an amount from about 0.00001 to about 10 percent by weight of the formulation, more preferably in an amount from about 0.0001 to about 5 percent by weight of the formulation and most preferably in an amount from about 0.001 to about 3 percent by weight of the formulation. However, any amount of surfactant may be employed that provides a formulation that contains a stabilized hydrolyzed trialkoxysilane and which has good cleaning properties. At least one alcohol having 1 to 12 carbon atoms employed in the formulation of this invention was preferably selected from mono, di and tri hydric alcohols. Such mono, di and tri hydric alcohols include, for example, ethanol, propanol, hexanol, isopropanol, N-pentanol, propylene glycol, glycerin, 2-pentanol, 3-pentanol, 2-butanol, diethylene glycol, Neodol® 91 (C 9 - Cn primary alcohol), Neodol® 1 (Cn primary alcohol) and decyl alcohol. Generally, the concentration of the mono, di or tri hydric alcohols in the formulation is in a range from about 0 00001 to about 5 0 percent by weight of the formulation The amount of alcohol employed in the formulation of this invention should be maintained below that amount which would cause substantial alkylation of the hydrolyzed trialkoxysilane Besides the alcohols described above, the formulations of this invention may also include other solvents, such as glycol ethers, to assist in cleaning the treated surface Typical glycol ethers include, without limitation Dowanol® EB, (ethylene glycol n-butyl ether), Dowanol® DB (diethylene glycol n-butyl ether), Dowanol® PnB (propylene glycol n-butyl ether), Dowanol® DPnB (dipropylene glycol n-butyl ether), Dowanol® PPh (propylene glycol phenyl ether), Dowanol® PMA (propylene glycol methyl ether acetate), Dowanol® EPH (ethylene glycol phenyl ether), Dowanol® DPMA (dipropylene glycol methyl ether acetate), Dowanol® DPM (dipropylene glycol methyl ether), Dowanol® PnP (propylene glycol n- propyl ether), Witco® DM-55 (polyethylene glycol dimethyl ether) and the like If employed, the glycol ethers are generally present in the formulation in an amount from about 0.1 to about 6.0 percent by weight of the formulation The formulations of this invention typically include a base to ensure that the pH of the formulation is greater than 7, and preferably from about 7 1 to about 13 0, most preferably about 8.5 to about 11.5. Generally such a base is present in an amount from about 0.00001 to about 5 0 percent by weight of the formulation Exemplary bases include, without limitation, ammonium hydroxide, monoethanolamine, sodium hydroxide, sodium metasilicate and potassium hydroxide Ammonium hydroxide is preferred Additional adjuvants which may be employed in the formulations of this invention include fragrances, colorants and the like The use of such adjuvants is well known to those of ordinary skill in the art The cleaning formulations of the present invention may be prepared by first adding the surfactant to water followed by the addition of the aqueous emulsion containing the hydrolyzed trialkoxysilane Thereafter, any solvents, bases or other adjuvants may be added to the formulations In yet another embodiment of this invention, a siloxane is added to the above described cleaning formulation to reduce the autophobicity of those formulations. The siloxanes that may be employed include polydimethyl- siloxane and derivatives thereof. Such derivatives may include, for example, polyaikylene oxide-modified polydimethylsiloxanes represented by the formula (CH 3 ) 3 SiO((CH 3 ) 2 SiO) x (CH 3 SiO) y Si(CH 3 ) 3 PE wherein PE is represented by -CH 2 CH 2 CH 2 O(EO) m (PO)„Z wherein EO is ethyleneoxy, PO is 1,2-propyleneoxy and Z is hydrogen or a lower alkyl group, or (CHsS ^KOSiCCH^ O-PE']v wherein PE' is represented by -(E0) m (PO) n R wherein EO and PO are the same as described above and R is a lower alkyl group. Other siloxanes which may be useful for reducing autophobicity include aromatic substituted siloxanes such as diphenyldimethylsiloxane copolymers, phenylmethylsiloxane polymers and methyl (propyl hydroxide, ethoxylated) bis (trimethyl siloxy) silane (Dow Coming® Q2-5211, available from Dow Corning, Midland, Michigan). If present, the siloxane is employed in an amount effective to reduce the autophobicity of the cleaning formula. Generally, about 0.00001 to about 0.5 percent of siloxane by weight of the formulation may be added to inhibit autophobicity. However, any amount of siloxane that is effective to inhibit autophobicity is encompassed by the present invention. This invention is also directed to a method of applyin" a silane coating on a hard surface, such as glass, ceramic, fiberglass or porcelain, ti t is covered by water. The above-described alkaline cleaning formulation is added directly to the water in an amount effective to modify the surface covered by the water through attachment of the silane to that surface. Without being bound to theory, it is believed that the silane contained in the formulation of this invention has a preferred orientation for liquid/air or liquid/solid surfaces. After the alkaline cleaning formulation is introduced to the water, it is believed that the hydrolyzed trialkoxysilane is no longer stabilized to inhibit surface attachment and that the reactive silane migrates to the liquid/solid interface and adheres to the surface. It has been suφrisingly discovered that surface modification can be obtained with as little as 0.1 ppm to 10 ppm of hydrolyzed trialkoxysilane in the water. The method of this invention can be readily practiced, for example, by the addition of an effective amount of the alkaline cleaning formulation to water contacting the surface which is to be treated. The amount of alkaline cleaning formulation that is added to the water is dependent on the concentration of hydrolyzed trialkoxysilane in the formulation, the amount of water contacting the surface and the surface area that is to be coated. Generally, the amount of alkaline cleaning formulation added to the water is an amount that will provide at least about 0.01 ppm of hydrolyzed trialkoxysilane in the water. The alkaline cleaning formulation may be added to the water in any manner desired, such as by direct application or by a slow release mechanism, e.g., a toilet bowl tank dispenser. The Examples which follow are intended as an illustration of certain preferred embodiments of the invention, and no limitation of the invention is implied. Example 1 A cleaning formulation was prepared containing the following components (as used herein % w/w means the percent weight of the component based on the weight of the formulation) Components % w/w Lonza Barlox® 12 (amine oxide) 1 0 250 Isopropyl Alcohol 3 000 Dow Triad 2 1 000 Fragrance 0 050 n-Hexanol 0 100 Deionized Water 94 396 NFLOH (28 5%) 0 200 TLF-8291 3 1 000 Colorant 0 004 100 000 CH 3 1 RN->O, wherein R is a Cι 2 alkyl group CH 3 2 Equal parts of Dowanol PnP, DPM and PnB 3 0% Cig-alkyltrialkoxyl silane with Cie-tetralkylammonium chloride (30 to 40% based on the silane) in an aqueous emulsion available from E I Du Pont de Nemours & Co , Wilmington, Delaware The resulting formulation had a clear appearance and a pH of 10 42 Example 2 A cleaning formulation was prepared in a manner similar to Example 1 , except the surfactant was Lonza Barlox® 10-S (an amine oxide wherein R is a C ]0 alkyl group) The formulation had a hazy/cloudy appearance and pH of 10 43 Example 3 The cleaning formulation was prepared in a manner similar to Example 1 , except the surfactant was Lonza Barlox® LF (purified amine oxide wherein R is a Cn alkyl group) This formulation had a slightly hazy appearance and a pH of 10 43 Examples 4-14 The following cleaning formulations were prepared in a manner similar to Example 1 , with the exception that no colorant was used and the Dow Triad was replaced by the glycol ethers set forth in the table below Example Glycol Ether pH Appearance 4 PnP 10 49 clear 5 PnB 10 32 clear 6 DPM 10 35 clear 7 DB 10 50 clear 8 EPh 10 46 clear 9 PPh 10 52 hazy 10 DPnP 10.56 clear 1 1 PMA 10 22 clear 12 PM 10 65 clear 13 DPnB 10 69 clear 14 DPMA 10 51 clear Examples 15-26 The following cleaning formulations were prepared in a manner similar to Example 1, with the exception that no colorant was used and the n-hexanol was replaced with the following mono, di or trihydric alcohols as set forth in the table below Example Alcohol pH Appearance 15 Diethylene Glycol 10 50 clear 16 Glycerine 10 49 clear 17 Isopropanol 10 51 clear 18 Decyl Alcohol 10 48 hazy 19 Neodol® 91 10 34 hazy 20 Propylene Glycol 10 33 clear 21 2-Pentanol 10 70 clear 22 2-Butanol 10 58 clear 23 n-Propyl Alcohol 10 56 clear 24 Ethanol 10 56 clear 25 Hexyl Alcohol 10 62 clear 26 1-Pentanol 10 52 clear Example 27 A cleaning formulation was prepared in a manner similar to Example 1, with the exception that no colorant was added and 0 250% w/w of a nonionic ethoxylated alcohol, Zonyl® FS-300 (poly(oxy-l,2-ethanediyl, alpha-hydro-omega-hydroxy- ether with alpha-fluoro, omega-(2-hydroxy ethyl) poly(difluoromethylene) also known as fluoroalkyl alcohol substituted monoether with polyethylene glycol), was added to the formulation The resulting formulation had a pH of 10 37 and a clear appearance Examples 28-30 These cleaning formulations were prepared in a similar manner to Example 1 , except that no colorant was added and the ammonium hydroxide was replaced by the following bases at the concentrations indicated in the table below Example Base Amount % w/w pH Appearance 28 NaOH(10%) 0 031 10.85 clear 29 KOH(10%) 0 043 10 31 clear 30 NaSiO 3 -5H 2 O 0.015 10 89 clear Example 31 A cleaning formulation was prepared containing the following components The resulting formulation had a pH of 10 55 and a clear appearance Example 32 A cleaning formulation was prepared in a manner similar to Example 31 , except that the Lonzaine® CS surfactant was replaced by an amphoteric betaine, Lonzaine®CO. The resulting formulation had a pH of 10.56 and a clear appearance. Example 33 A cleaning formulation was prepared having the following components: Components % w/w Lonza Amphoterge®KJ-2 (Amphoteric imidazoline) 0.500 Witco Variquat®66(dialkoxy alkyl quaternary) 1 0.165 Monoethanolamine 0.200 Isopropyl Alcohol 1.250 Lonza Barlox® C12 (amine oxide) 0.100 n-Hexanol 0.050 Fragrance 0.025 NH.OH (28.5%) 0.125 Deionized Water 97.085 TLF-8291 0.500 100.000 1 ethyl bis(polyhydroxyethyl)alkyl ammonium ethyl sulfate The resulting formulation had a pH of 10.56 and a very slightly hazy appearance Examples 34-37 The following formulations were prepared in a manner similar to Example 33 with the exception that the amphoteric surfactant, Lonza Amphoterge®KJ-2, was replaced by the amphoteric surfactants listed in the table below Example Amphoteric Surfactant pH Appearance 34 Miranol®C2M 1 10 54 clear to hazy 35 Amphoterge®W-2 2 10 70 clear 36 Amphoterge®L 3 10 60 clear 37 Rewoteric AMV 4 10 64 clear 1 amphoteric imidazoline disodium cocoampho dipropionate 2 coco based imidazoline dicarboxylate, sodium salt 3 lauryl imidazoline dicarboxylate amphoteric 4 amphoteric glycinate Examples 38-39 The following formulations were prepared in a manner similar to Example 33 except that the amphoteric surfactant, Lonza Amphoterge®KJ-2, was replaced by the cationic surfactants listed in the table below Example Cationic Surfactant pH Appearance 38 Barlox®LF' 10 67 slightly hazy 39 Variquat®K-1215 2 10 53 slightly hazy 1 purifiec amine oxide having a d 2 alkyl group 2 ethyl bi s(polyhydroxyethyl)alkyl ammonium sulfate Stability Testing Two ounce (57.7g) samples of each formula were placed in a 100°F (37.78°C.) oven. Each sample was visually monitored each day for two weeks and designated either clear, very slightly hazy, hazy or very hazy. The results of these tests are set forth in Table 1. After two weeks, no sample exhibited white clouds in a clear solution which would have been indicative of undesirable polymerization of the silane. Hydrophobicity Testing Hydrophobicity of each formula treated-surface was measured using a water drop test. This test measures how well a formulation treated-surface repels water. The test was conducted by first cleaning a mirror plate (12 in 2 (about 77 cm 2 ) Mirror Model #P1212-NT, Monarch Mirror Co.) with HPLC grade acetone and a paper towel. Next, the mirror was rinsed with deionized water and blown dry. The mirror was then divided into 6 equivalent sections and about 0.15 to 0.25 g of a formula was applied to a section and wiped completely dry with half of a paper towel. After waiting one half hour, a pipette was used to deliver five drops of room temperature tap water to each section and to a control section, e,, a section of the mirror to which a formula was not applied. After 5 minutes, each drop's diameter was measured parallel to the base of the mirror. An average drop size was calculated for each formula and the control. The average drop size for the formulas tested was found to be 0.70 cm, while the average drop size for the controls was 0.76 cm. Almost every formula exhibited an improvement over the control. The results of the water drop test are set forth in Table 1. An alternative drop test was employed for several of the formulations of this invention. This test involved substituting dodecane for water in the above- described water drop test. In this test the dodecane was dropped onto the treated surface only three or four minutes after the formula was applied and the drop was measured after only two or three minutes The results of this test are set forth in Table 1 Sliding Drop Test The sliding drop test, which quantifies how a droplet flows or wets an inclined surface, was conducted on several of the formulations of this invention The test was conducted on a 6 in 2 (about 15 cm 2 ) glazed ceramic tile (Tilepak Glossy White CC-100), which was first cleaned with warm tap water and wiped dry Each tile was treated with an equivalent amount of formulation (two to ten drops) and wiped dry After ten minutes the ceramic tile was placed on an incline and a Gilson Pipetman was used to dispense a 50 μmL drop on each tile The trail left on the tile was observed and rated on a scale of 0-5 as follows 0 - indicates a continuous even trail the same width as the drop, 1 - indicates a continuous trail narrower than the drop, 2 - indicates a trail that is occasionally broken and narrower than the drop, 3 - indicates a trail with only half the trail wetted, 3 5 - indicates that elongated drops cover a quarter of the trail, 4 - indicates that spherical drops cover a quarter of the trail, 4 5 - indicates that the trail consists of only a few scattered spherical drops, and 5 - indicates the drop rolls off the tile leaving no trail The results of this test are set forth in Table 2 Cleaning Tests A cotton swab cleaning test was also utilized to test the cleaning efficacy of the formulations of this invention, versus interior soil, shell soil, beef tallow and various permanent ink markers Interior soil was prepared by adding and melting together 0 5g of synthetic sebum, 0.5g of mineral oil, and 0.5g clay, followed by the addition of 98 5g of 1,1, 1-trichloroethane (Synthetic sebum consists of 10% palmitic acid, 5% stearic acid, 15% coconut oil, 10% paraffin wax, 15% cetyl esters wax, 20% olive oil 5% squalene, 5% cholesterol, 10% oleic acid, and 5% linoleic acid which are added together and heated over low heat in order to melt the solids and form a homogeneous mixture ) Shell soil consists of 40 parts Metallic Brown Oxide (Pfizer B-3881), 24 parts Kerosene (deodorized), 24 parts Shell sol 340, 2 parts White Mineral Oil, 2 parts Shell Tellus 27, and 2 parts Hydrogenated Vegetable Oil (Crisco) The Shell soil was prepared by dissolving vegetable shortening (Crisco) in kerosene and Shell Sol 340 Next, mineral oil, Shell Tellus 27 and pigment were added followed by agitating continuously for two hours A mirror plate, like that employed in the hydrophobicity test, was cleaned with Classical EB Windex® and thoroughly dried with a paper towel The soils were applied to the mirrors After 24 hours, a cotton swab was dipped into the formulations and wiped horizontally in a constant motion ten cycle pattern, about one inch (2 54 cm) long, with a constant pressure After the cleaned areas were dry, the effectiveness of each formula was rated on a scale of one to ten, with one representing no soil removal. The results of the cleaning tests on the formulations of this invention are set forth in Table 1 1 able I Ex. Drop Tests Cleaning T est Appearance at I00°F (about 38°C.) water dodecane Interior Shell Beef Tallow Marker 1 0.67 1.15 6.0 3.0 5.0 4.1 clear 3 0.68 - 3.5 3.0 7.0 5.4 hazy 4 0.67 - 3.0 3.0 4.0 6.0 s. hazy 5 0.72 - 4.0 3.0 4.0 6.2 v.s.hazy 6 0.68 - 5.0 4.0 3.5 6.1 s. hazy 7 0.72 - 5.0 4.0 3.5 6.1 v.s. hazy 8 0.70 - 4.0 6.0 3.5 5.1 clear 9 0.66 - 4.0 5.0 6.5 5.6 v.s. hazy 10 0.67 - 4.0 5.0 3.5 5.6 v.s. hazy 1 1 0.66 - 5.0 2.5 3.5 4.0 clear 12 0.66 - 5.0 4.0 5.0 5.0 v.s. hazy 13 0.66 - 3.0 3.0 4.0 5.7 clear 14 0.68 - 4.0 6.0 3.5 5.0 clear 15 0.79 1.40 3.0 3.0 4.0 5.5 hazy 16 0.74 1.13 3.0 3.5 4.0 5.5 hazy 17 0.71 - 5.0 3.0 5.0 5.9 hazy 20 0.76 - 3.5 5.5 3.0 4.4 hazy 21 0.70 - 3.0 4.0 4.0 6.8 hazy 22 0.74 - 3.0 3.0 4.0 6.1 hazy 23 0.70 - 4.0 4.5 4.0 6.3 hazy 24 0.69 - 3.5 4.0 4.5 6.2 azy 25 0.70 - 3.0 4.0 6.0 5.9 azy 26 0.72 1.64 3.0 4.5 4.5 5.9 hazy 27 0.66 - 6.0 3.0 4.0 5.7 v.s. hazy 28 0.62 1.39 6.0 7.0 7.0 6.3 s. hazy 29 0.64 1.25 8.0 6.0 7.0 7.1 s. hazy 30 0.61 - 7.0 6.0 6.0 7.0 hazy 31 0.64 1.33 6.0 6.0 5.0 6.9 clear 32 0.65 - 7.0 6.0 6.0 6.8 hazy 33 0.76 - 6.0 6.0 2.0 6.4 v.s. hazy 34 0.65 - 5.0 4.0 4.0 7.4 clear 35 0.72 - 6.0 3.0 3.5 6.6 clear 36 0.70 - 5.0 3.0 3.0 7.3 clear 37 0.74 - 4.0 4.0 3.0 7.2 v. hazy 38 0.81 - 5.0 4.0 3.0 7.2 hazy 39 0.85 - 3.0 5.0 2.0 7.3 v. hazy Control Λvg. Λvg. " 0.75 2.12 ' " Table 2 Example Sliding Drop Test (10 drops) 1 4.5 15 4.5-5 16 4.5 26 5.0 28 4.5 29 5.0 31 5.0 Even after two weeks at 100°F (about 38°F ), none of the formulas of this invention 5 developed a white cloudy appearance in a clear solution that would have been indicative of the formation of insoluble polymer due to silane instability. However, the results illustrate that certain formulations remained clearer than others. In particular, Examples 1, 3, 8, 11, 14, 31, 34, 35 and 36 exhibited excellent clarity. The results of the water drop test set forth in Table 1 show that almost all 10 the formulations of this invention increased the hydrophobicity of the treated surface. Examples 28-32 and 34 exhibited particularly strong hydrophobicity (0.61- 0.65 versus a 0.75 average for the control), while Examples 1, 3, 4, 6, 9-14, 24 and 27 showed moderately strong hydrophobicity improvement (0.66-0.69 versus a 0.75 average for the control). The dodecane drop tests on Examples 1, 15, 16, 26, 28, 15 29 and 31 show that all the tested formulations improved the solvophobicity of the treated surface (1.13 to 1.64 versus the control average of 2.12). Notwithstanding a formulation's ability to deliver a protective silane coating and render a surface hydrophobic, the formulation should also have the ability to clean The cleaning test results illustrated in Table 1, show that Examples 28-32 are particularly strong overall for each of the soil groups Other formulations evidence strong cleaning properties for a particular soil group Thus, the results of these tests indicate that the formulations of this invention are not only stable and provide a protective silane coating, but also provide effective cleaning efficacy, the scope of which can be modified depending on the nature of the formulation The results set forth in Table 2, also confirm that the formulations of Examples 1, 15, 16, 26, 28, 29 and 31 rendered the surface of ceramic tiles treated with those formulations hydrophobic or water repellant Industrial Applicability The cleaning formulations of this invention are highly storage stable even when packaged in glass containers, and therefore conserve the active silane for attachment to treated surfaces. In addition, the method of applying the alkaline cleaning formulations of this invention may be advantageously used to clean and protect water covered surfaces with a minimal use of materials and effort Other variations and modifications of this invention will be obvious to those skilled in this art This invention is not to be limited except as set forth in the following claims

Claims: WHAT IS CLAIMED IS 1 An alkaline cleaning formulation for cleaning hard surfaces compπsing (i) a hydrolyzed trialkoxysilane in an amount from about 0 00001 to about 10 0 percent by weight of said formulation, (ii) a surfactant in an amount from about 0 00001 to about 10 0 percent by weight of said formulation, (iii) an alcohol having 1 to 12 carbon atoms, and (iv) water, wherein said formulation has a pH greater than 7 0 2) An alkaline cleaning formulation according to claim 1 , wherein said hydrolyzed trialkoxysilane is formed in an aqueous emulsion from a hydrolyzable trialkoxysilane compound emulsified in water with about 5 to 100 percent by weight of an emulsifier based on the weight of the hydrolyzable trialkoxysilane and said surfactant is different than said emulsifier 3 An alkaline cleaning formulation according to claim 2, wherein said hydrolyzable trialkoxysilane is represented by formula (I) R'-(CH 2 ) -Si{ (-O-CH 2 CH 2 -) -OR 2 } 3 wherein R 1 is selected from the group consisting of a perfluoroalklyl group of 3 to 18 carbon atoms or an alkyl group of 3 to 24 carbon atoms, each R 2 is independently an alkyl group having 1 to 3 carbon atoms, p is 0 to 4 and n is 2 to 10 4 An alkaline cleaning formulation according to claim 3, wherein R ! is an alkyl group having 12 to 24 carbon atoms and p is 0 5 An alkaline cleaning formulation according to claim 4, wherein said emulsifier is an ethoxylated Cg.ig amine salt 6 An alkaline cleaning formulation according to claim 1 , wherein said surfactant is selected from the group consisting of nonionic surfactants, amphoteric betaines, amphoteric sultaines, imidazoline amphoterics, amine oxides, quaternary cationics, dialkoxy alkyl quaternaries and mixtures thereof 7 An alkaline cleaning formulation according to claim 5, where said surfactant is selected from the group consisting of amine oxides, amphoteric sultaines, amphoteric betaines, nonionic ethoxylated alcohols and mixtures thereof 8 An alkaline cleaning formulation according to claim 7, wherein said surfactant is an amine oxide or an amphoteric betaine 9. An alkaline cleaning formulation according to claim 1, wherein said alcohol is selected from the group consisting of mono-hydric alcohols, di-hydric alcohols, tri-hydric alcohols and mixtures thereof 10 An alkaline cleaning formulation according to claim 1, wherein said solvent is hexanol, isopropanol or a mixture thereof 11 An alkaline cleaning formulation according to claim 1 , further comprising at least one glycol ether 12 An alkaline cleaning formulation according to claim 1, further comprising a base in an amount effective to provide said formulation with a pH greater than 7 0 13 An alkaline cleaning formulation according to claim 12, wherein said base is selected from the group consisting of ammonium hydroxide, monoethanolamine, sodium hydroxide, sodium metasilicate and potassium hydroxide 14 An alkaline cleaning formulation according to claim 11, wherein the pH of said formulation is about 7.1 to about 13 0 15 An alkaline cleaning formulation according to claim 1, further comprising a siloxane in an amount effective to reduce an autophobicity of the cleaning formulation 16 An alkaline cleaning formulation for cleaning hard surfaces comprising (i) a hydrolyzed trialkoxysilane in an amount from about 0 00001 to about 10 percent by weight of said formulation, wherein said hydrolyzed trialkoxysilane is formed in an aqueous emulsion from a Cis-alkyltrialkoxy silane compound emulsified in water with a Cg.ιg tetraalkylammonium chloride in an amount of about 30 to 50 percent by weight of the silane, (ii) a surfactant in an amount from about 0.00001 to about 10 0 percent by weight of said formulation, wherein said surfactant is selected from the group consisting of amine oxides, amphoteric sultaines, amphoteric betaines, nonionic ethoxylated alcohols and mixtures thereof; (iii) at least one mono-hydric alcohol, di-hydric alcohol, or tri-hydric alcohol, (iv) optionally, at least one glycol ether, (v) a base in an amount effective so that said formulation has a pH between 8.5 and 11.5, and (vi) water 17 An alkaline cleaning formulation according to claim 16, wherein said mono- hydric alcohol, di-hydric alcohol or tri-hydric alcohol is selected from the group consisting of isopropanol, hexanol and mixtures thereof. 18 An alkaline cleaning formulation according to claim 17, wherein said glycol ether is a mixture of propylene glycol n-butyl ether, propylene glycol n-propyl ether and dipropylene glycol methyl ether 19. A method for cleaning and modifying a hard surface covered by water comprising the step of applying an alkaline cleaning formulation according to claim 1 , to water contacting said hard surface in an amount effective to modify said hard surface by attachment of said hydrolyzed trialkoxysilane to said surface. 20. A method according to claim 19, wherein the concentration of said hydrolyzed trialkoxysilane in said water is from about 0.01 ppm to about 10,000 ppm.

Inventors: NEUMILLER PHILLIP J, NEUMILLER, PHILLIP, J.
Applicants: JOHNSON & SON INC S C, S.C. JOHNSON & SON, INC.
Application year: 1997
Main classification: C11D3
IPC codes: C11D3