ELECTROPHORETIC GEL

Abstract: An electrophoretic gel based on polyacrylamide obtainable by photoinitiated polymerization of a mixture containing monoolefinic- and di- and/or polyolefinic monomers and a photoinitiator. The initiator is a compound of general formula (I), where R1 and R2 independently are CH3, C2H5 or C3H7, or R1, R2 together with the carbon atom form a cycloaliphatic ring with 4-8 carbons; R3 = H, CH3, C2H5 or -O-(CH2CH2)n-OH with n = 1-20. The invention also relates to a process for the production of the electrophoretic gel and use of the gel for the electrophoteric separation of nucleic acid fragments. Further, a kit for use in the production of an electrophoretic gel is described.

Description: Electrophoretic σel The present invention relates to an electrophoretic gel based on polyacryl mide and method for the production and use thereof . In particular the invention relates to electrophoretic gels obtainable by photoinitiated polymerization . Gel electrophoresis is today a widely used method for separating biomolecules . The method is routinely used for separating proteins, peptides, nucleic acids etc., often with automated equipment based on fluorescence detection. One important application is separation of nucleic acid fragments e.g. obtained in DNA sequencing. Several automated systems for DNA sequencing are available in the market . Gel electrophoretic separation of molecules is based on the difference in charge density of the different molecules as well as the sieving effect of the porous gel media. The extent of sieving depends on how well the pore size of the gel matches the size of the migrating molecules. Different types of gel material are used, for example dextran, agarose and polyacrylamide. Polyacrylamide gels are commonly used due to their good qualities. Polyacrylamide can be prepared in a reproducible manner, with a wide range of pore sizes. Besides, the polyacrylamide gels are chemically inert, stable over a wide range of pH and temperatures and they are transparent . The electrophoretic gel is composed of a network of cross-linked polymer molecules which forms the pores of the gel. The separating qualities of the gel depend on, among other things, how big and how evenly distributed the pores of the network are. The size and the distribution on the other hand, is dependent on the dry solids content of the gel, on the content of cross-linker and on the method of initiation. The gel based on polyacrylamide is made by polymerization of a monoolefinic monomer, such as acrylamide, with a bifunctional monomer such as methylene bisacrylamide . The polymerization can be initiated either chemically e.g. by sodium or ammonium persulf te and tetramethylethylenediamine or photochemically . There are several disadvantages with the chemically initiated polymerization. The polymerization is strongly inhibited by oxygen as the free radical production is slow. As it is difficult to know the oxygen content of the gel casting solution it is impossible to obtain a well defined degree of monomer conversion. The structure of the polymer network will vary from one gel casting to another, resulting in a bad reproducibility . Further, with the initiator, charged sulfate groups are introduced into the polymer network, which creates electroendosmosis . As the reaction starts immediately after the mixing of the components a rather quick application of the reaction mixture into the gel mold is required. To avoid the above mentioned disadvantages, gels made by photoinitiated polymerization have been proposed. Riboflavin or riboflavin 5 ' -phosphate in combination with an amine has been used since the 1950 's, but requires long irradiation times and tends to give lower conversion than chemical initiation as mentioned above. EP 169 397 relates to an improved method for preparing fotoinitiated electrophoresis gels. The process is based on photoinintiation with initiator systems such as benzoin ethers, benzophenone derivatives and amines, phenantrenequinones and amines, naphtoquinones and amines, methylene blue and toluene sulfinate . With these initiators a faster polymerization is obtained. Still however, the quantum efficiency, i.e. the amount of radicals produced per absorbed photon, for these initiators are very low. The majority of them are also charged species which increase the ionic strength of the gels. This causes the gel resistance to vary with time during electrophoresis, which in automatic DNA sequencing gives varying distances between the peaks and thus complicates the automatized peak detection. For many electrophoretic applications the gels used are ready made gels cast by a supplier. For sequencing separation of nucleic acids however, it is difficult to use ready made gels. This is due to the fact that the denaturing agent used to separate double stranded DNA, mostly urea, is not stable in the water containing gel, but forms ionic systems. Thus, it is not possible to use the commercially available gels for e.g. protein separation, for DNA sequencing separation. The gels for nucleic acid separation are therefore usually cast by the user at the moment of separation. The predominant method today for initiation of gel solutions for DNA fragment separation is by chemical initiation. For the gel casting the user has to mix the monomer solution and the initiator, remove oxygen and quickly cast the solution as the initiation starts immediately. Still the other drawbacks mentioned above are achieved. There is therefore a need for an improved method for the production of electrophoretic gels for separation of nucleic acid fragments . There is also a need for improved methods of photoinitiation of acrylamide polymerization for electrophoresis gel production in general. The object of the present invention is to obtain an improved electrophoretic gel and method of production thereof . A further object of the invention is to achieve an electrophoretic gel for use in electrophoretic separation of nucleic acid fragments. Yet a further object of the invention is to present an improved gel kit for use in the production of electrophoretic gels. The objects of the invention are achieved by the electrophoretic gel and process for preparation and use thereof, as well as the kit, as claimed in the claims. According to the invention an electrophoretic gel based on polyacrylamide is obtainable by photoinitiated polymerization of a mixture containing monoolefinic- and di- and/or polyolefinic monomers and a photoinitiator. The initiator is a compound with the general formula: where R l and R 2 independently are CH 3 , C 2 H 5 or C 3 H 7 , or R lf R 2 together with the carbon atom form a cycloaliphatic ring with 4 - 8 carbons ; R 3 = H, CH 3 , C 2 H 5 or -O- (CH 2 CH 2 ) n -OH with n = 1-20. According to a further aspect of the invention a process for the production of an electrophoretic gel based on polyacrylamide by photoinitiated polymerization of a mixture containing monoolefinic- and di- and/or polyolefinic monomers and a photo initiator is obtained. The process is characterized in that the initiator is chosen from a compound with the general formula: where R l and R 2 independently are CH 3 , C 2 Hs D r 3 H 7/ or R l f R 2 together with the carbon atom form a cycloaliphatic ring with 4 - 8 carbons; R 3 = H, CH 3 , C 2 H5 or -O- (CH CH 2 ) n -OH with n = 1-20. According to yet a further aspect of the invention an electrophoretic gel based on polyacrylamide obtainable by photoinitiated polymerization of a mixture containing monoolefinic- and di- and/or polyolefinic monomers and a photoinitiator , wherein the initiator is a compound with the general formula : where R l and R 2 independently are CH 3 , C 2 Hs or C 3 H 7 or Ri, R 2 together with the carbon atom form a cycloaliphatic ring with 4 - 8 carbons; R 3 = H, CH 3 , C 2 H 5 or -0- (CH 2 CH 2 ) n -0H with n = 1-20, is used for electrophoretic separation of nucleic acid fragments . The invention also comprises a kit for use in the production of an electrophoretic gel, based on polyacrylamide, for electrophoretic separation of nucleic acid fragments. The kit comprises: (i) a mixture of monoolefinic- and di- and/or polyolefinic monomers, (ii) optionally buffer and denaturing agent, (iii)a photo initiator with the general formula: where Ri anc j R independently are CH , C 2 Hs or C 3 H 7 or R_, R together with the carbon atom form a cycloaliphatic ring with 4 - 8 carbons; R 3 = H, CH 3 , C 2 H 5 or -O- (CH 2 CH 2 ) n -OH with n = 1-20. With the present invention it was found that the content of residual monomers was minimized and a faster and more complete polymerization was obtained. In DNA sequencing separation, where the user has to cast the gel, the fast polymerization is especially advantageous. The user will have a gel, ready for use, after about 10 minutes compared with about 2 hours for chemically initiated gels. The photoinitiated polymerization with the photo initiators according to the invention also results in a gel which is very uniformly polymerized. This is important when analyzing DNA sequencing products, as this analysis means comparison of samples having been migrated in different places in the gel. The fluorescence based detection which is used today in sequencing analysis adds further unique demands on the electrophoresis gel. The gel has to be totally transparent. The detection is made with a laser beam and in some instruments the laser is situated at one side of the gel. The beam ' then has a long way to go through the total width of the gel. A small turbidity in the gel will result in light scattering and a too low intensity of the light when the beam reaches the bands at the farthest end. The optical homogeneity and the separation qualities of the gel are also very important in connection with laser detection. Local gradients in the refractive index result in the beam deflecting and the detection will be incorrect. The demands on the separation qualities of the gel are much higher in automated DNA sequencing with laser detection than in ordinary gel electrophoresis . In ordinary electrophoresis the samples are run to the end of the gel and then the gel is taken out and developed. In an automated equipment the laser reads the bands at a fixed distance. This means that the electrophoresis has to be run at a long time to enable all fractions to reach the laser. Then it is important that the bands do not drift aside and miss the laser or the detectors. The computerized analysis of the result which is used in some instruments, is based on that the bands are produced with the same distance between them. To obtain that the current/voltage ratio has to be constant. The demands, as mentioned above, are fulfilled in an improved manner by the gels of the invention compared with the state of the art gels. One reason for the good result is believed to emanate from the high quantum efficiency of the initiators, an efficiency much higher than for the state of the art initiators. Also the fact that the gel system is completely without immobilized charged groups adds to the quality. Thus, the initiators used in the present invention are especially useful for casting gels for separation of nucleic acid fragments. A preferred embodiment is use of the photoinitiated gels in automated DNA sequencing, especially with fluorescence based detection. The electrophoretic gels of the invention, based on polyacrylamide, are produced by co-polymerization of monoolefinic monomers with di- or polyolefinic monomers. The co-polymerization with di- or polyfunctional monomers results in cross-linking of the polymer chains and thereby the formation of the polymer network. As monoolefinic monomers used in the invention can be mentioned acrylamide, methacrylamide and derivatives thereof such as alkyl-, or hydroxyalkyl derivates, e.g. N,N-dimethylacrylamide, N- hydroxypropylacrylamide, N-hydroxymethylacrylamide . The di- or polyolefinic monomer is preferably a compound containing two or more acryl or methacryl groups such as e.g. methylenebisacrylamide, N,N' -diallyltartardiamide, N,N'- 1, 2-dihydroxyethylene-bisacrylamide, N, N-bisacrylyl cystamine, trisacryloyl-hexahydrotriazine . In a broader sense the expression ''based on polyacrylamide ' ' also comprises, in the present context, such gels in which the monoolefinic monomer is selected from acrylic- and methacrylic acid derivatives, e.g. alkyl esters such as ethyl acrylate and hydroxyalkyl esters such as 2- hydroxyethyl methacrylate, and in which cross-linking has been brought about by means of a compound as mentioned before. Further examples of gels based on polyacrylamide are gels made by co-polymerization of acrylamide with a polysaccharide substituted to contain vinyl groups, for example allyl glycidyl dextran as described in EP 87995. Monomers which would introduce non-desirable charges into the gel are excluded from the group defined above. The gels according to the invention are prepared from an aqueous solution containing 2-40 % (w/w) , preferably 3- 25 % (w/w) of the monomers mentioned above. The amount of cross-linking monomer is 0,5 - 15 %, preferably 1 - 7 % by weight of the total amount of monomer in the mixture. The structure of the polymeric network in the gel is adjusted by adjusting these parameters. An increase of the amount of monomers, i.e. the dry content, results in a more dense network. A more dense network will also be the result if the amount of cross-linker is increased. A denser network will bring about a longer separation time but a better resolution of the separated fragments. The initiators used in the present invention are added to the aqueous monomer solution in an amount of 0,1 - 10 mM, preferably 0,5 - 5 mM. Among initiator compounds preferred for the invention can be mentioned 1-hydroxy- cyclohexyl-phenyl-ketone : and 1- [4- (hydroxyethoxy) -phenyl] -2 -hydroxy-2 -methyl-1- propane-1-one : and 2-hydroxy-2-methyl-l-phenyl-propan-l-one Some of the initiators in the present invention are water soluble and may thus be mixed directly with the aqueous monomer solution. Other initiators in the present invention have been used in connection with curing of lacquers, mainly in non-aqueous systems. In order to use such an initiator in an aqueous solution, the initiator is first dissolved in an organic solvent, which solvent must not adversely affect the properties of the gel when incorporated in the reaction mixture. Therefore it is important that the solubility of the initiator in the organic solvent is high enough to make it possible to use only a small amount of solvent and that the organic solvent containing the dissolved initiator is soluble in the aqueous monomer solution. As suitable organic solvents car. be mentioned alcohols such as ethanol, ethylene glycol and glycerol, polyalkylene oxides, e.g. polyethylene oxide, esters and ketones . Alternative compounds for dissolving the initiator can easily be found by the skilled man for different electrophoretic processes. For example, a monomer in a liquid state may often be useful as a solvent for the initiator. In addition to the initiator and monomers the reaction mixture may contain various additives the choice of which will depend on the particular electrophoretic technique contemplated. Thus, for isoelectric focusing a certain type of amphoteric compounds are added which will create a pH gradient in the gel during electrophoresis. These compounds can be charged polymer amphoteric compounds as the water- soluble ampholytes described in GB 1 596 427. Another way of obtaining a gradient of this kind is by means of amphoteric groups immobilized in the gel, as described in GB 1 570 698. This may be achieved for example by incorporating in the reaction mixture certain vinyl monomers, namely vinyl monomers containing groups capable of being charged, for example carbonic-, sulfonic- and boronic acids and phosphonic acid groups or amino groups and other nitrogen compounds capable of being charged. In the case of immunoelectrophoresis and similar techniques preparations are employed which contain antigens or antibodies as additives. Other types of additives may be buffer systems and denaturing compounds such as sodium dodecyl sulfate and urea. The method of producing the electrophoretic gel is mainly the same if the gel is produced by a commercial supplier or by the user himself. An aqueous solution of the monomers to be used is prepared and mixed with the initiator/initiator solution and other optional additives. As the polymerization does not start until the solution is irradiated, the user of the gel can mix the initiator with the monomer solution properly, well in advance before the gel casting. It is also possible to use a ready made gel kit, which contains monomers as well as the initiator mixed in advance. The obtained cast solution is poured into a casting mould with the desired shape. The mould is ususally made of glass or of some polymer material which is transparent for UV light. The polymerization of the monomer solution is achieved by irradiating the solution with ultra-violet light. Any light source that will activate the initiators can be used. Preferred are light sources emitting light with a wave lenght within 300 - 400 nm. The 2 amount of irradiation is suitably 0.5 - 10 joule/cm . When very thin gels are prepared the solution is advantageously applied as a thin film on a backing material, such as a plastic film. Gels with backing can also be prepared by continuous coating processes, where the solution is applied on a moving web of plastic film. The invention will now be illustrated with the following non- limiting examples. With parts and per cent are meant parts by weight and per cent by weight if not differently stated. Example 1 : The following solutions were prepared: A monomer stock solution from: 300 g acrylamide 15 g methylenebisacrylamide water to obtain 1 1 basic solution. Buffer solution: 248.28 g Tris 102, 64 g Borate 7,44 g EDTA water (of high purity degree) to 2 1. Initiator solution: 100 mM 1-hydroxy-cyclohexyl-phenyl-ketone dissolved in ethyleneglycol . The following components were mixed: 29 g urea, 16 ml monomer stock solution, water (of high purity degree) to obtain 60 ml. To this mixture were added: 8 ml buffer solution • 1.6 ml initiator solution water (of high purity degree) to 80 ml. After filtration the solution was poured into a gel cassette, designed for an automated DNA sequencing equipment (ALFexpress® from Pharmacia Biotech, Uppsala) The inner surfaces of the casette had been carefully cleaned. The gel solution was irradiated with UV light for 10 minutes, at a distance of 10 cm from the gel. A 0.5 mm thick gel slab was obtained. UV source: A solarium fluorescent lamp ''TL/09 R'' (Philips) emitting between 300 - 400 nm. The gel obtained was used in the automated DNA sequencing equipment mentioned above. A standard sequencing protocol was used on M13mpl8 (+) with M13 universal primer. The fragments were labelled with a fluorescent label. The sample was run in four different reactions (one for each nucleotide A, C, G and T) and the same label was used for all nucleotides. The four reaction solutions were loaded abreast on the gel. The fragments were detected by means of a laser and the collected data was transformed by computer means and presented in the form of a chromatogram. The electrophoresis was run at the following values : U(max)= 1500 V, I (max) = 60 mA, P (max) = 25 W, T= 55° C. The interval between collected data was 1 point/2s and the data collecting time was 800 min. Example 2 : As a comparison chemically initiated gels were made accordingly: The following components were mixed: 29 g urea 16 ml monomer stock solution from example 1 water (of high purity degree) to obtain 60 ml. To this mixture were added: 8 ml buffer solution as in example 1 water (of high purity degree) to obtain 80 ml. After carefully mixing 40 μl tetramethylenediamine 400 μl ammoniumpersulfate are added and the mixture is carefully shaken. A casette of the same type as in example 1 was quickly filled with the solution. The solution was allowed to polymerize for 90 minutes. The obtained gel was 0.5 mm and used in the same manner as in example 1. Besides the advantages at the production of gels with the photoinitiated polymerization, the gels obtained by photopolymerization result in chromatogram with a constant distance between the peaks and a reading leanght of 650 - 700 bases compared with only 500 bases for the chemically initated gels. The signal/noise ratio was better for the photopolymerized gels. With the photopolymerization method is also possible to obtain reproducible result, i.e the same result from one run to another.

Claims: Claims 1. An electrophoretic gel based on polyacrylamide obtainable by photoinitiated polymerization of a mixture containing monoolefinic- and di- and/or polyolefinic monomers and a photoinitiator, characterized in that the initiator is a compound with the general formula: where R l and R 2 independently are CH 3 , C2H5 G r 3 H 7, or R l/ R 2 together with the carbon atom form a cycloaliphatic ring with 4 - 8 carbons; R 3 = H, CH 3 , C 2 H 5 or -O- (CH 2 CH 2 ) n -OH with n = 1-20. 2. A gel according to claim 1, characterized in that the polymerization is initiated by UV light of a wave length of 300 - 400 nm. 3. A gel according to claim 1 or 2 , characterized in that the initiator is a compound with the formula: 4. A gel according to claim 1 or 2 , characterized in that the initiator is a compound with the formula: 5. A process for the production of an electrophoretic gel based on polyacrylamide by photoinitiated polymerization of a mixture containing monoolefinic- and di- and/or polyolefinic monomers and a photoinitiator , characterized in that the initiator is chosen from a compound with the general formula: where RT. and R 2 independently are CH 3 , C 2 Hs or C 3 H 7 , or Rj_ , R 2 together with the carbon atom form a cycloaliphatic ring with 4 - 8 carbons ; R 3 = H, CH 3; C H5 or -O- (CH 2 CH 2 ) n -OH with n = 1-20. 6. A process according to claim 5, characterized in that the polymerization is initiated by UV light of a wave length of 300 - 400 nm. 7. A process according to claim 5, characterized in that the initiator is a compound with the formula: 8. A process according to claim 5, characterized in that the initiator is a compound with the formula: 9. Use of an electrophoretic gel based on polyacrylamide obtainable by photoinitiated polymerization of a mixture containing monoolefinic- and di- and/or polyolefinic monomers and an photoinitiator , characterized in that the initiator is a compound with the general formula: where R l and 2 independently are CH 3 , C 2 H 5 or C 3 H 7 or R l t R 2 together with the carbon atom form a cycloaliphatic ring with 4 - 8 carbons; R 3 = H, CH 3 , C H 5 or -O- (CH 2 CH ) n -OH with n = 1-20, for electrophoretic separation of nucleic acid fragments. 10. Use according to claim 9, characterized in that the initiator is a compound with the formula: 11. Use according to claim 9, characterized in that the initiator is a compound with the formula: 12. Use according to any of the claims 9-11, characterized in that the polymerization is initiated by UV light of a wave length of 300 - 400 nm. 13. Use according to any of the claims 9-12 in automated DNA sequencing. 14. Use according to claim 13 with fluorescence based detection. 15. A kit for use in the production of an electrophoretic gel, based on polyacrylamide, for electrophoretic separation of nucleic acid fragments, the kit comprising: (i) a mixture of monoolefinic- and di- and/or polyolefinic monomers, (ii) optionally buffer and denaturing agent, (iii) a photo initiator with the general formula: where Ri anc : R 2 independently are CH 3 , C 2 Hs or C H or R , R 2 together with the carbon atom form a cycloaliphatic ring with 4 - 8 carbons ; R 3 = H, CH 3 , C2H5 or -O- (CH 2 CH 2 ) n -0 H witn n = 1-20. 16. A kit according to claim 15, characterized in that the intiator is compound with the formula:

Inventors: GOETHE SVEN, HULT ANDERS, JOHANSSON JAN-OLOF, KAAGEDAL LENNART, SYLWAN ANNA, GOETHE, SVEN, HULT, ANDERS, JOHANSSON, JAN-OLOF, KAAGEDAL, LENNART, SYLWAN, ANNA
Applicants: PHARMACIA BIOTECH AB
Application year: 1997
Main classification: C08F20
IPC codes: C08F2, C08F4, C08F20, C08F220, G01N27