Developer compositions

Abstract: A negatively charged liquid developer comprised of a nonpolar liquid, a mixture of a first and a second thermoplastic resin with dissimilar melt indexes, a colorant, a charge director, optional charge adjuvent, a charge control agent comprised of a component of the alternative formulas or wherein R 1 is selected from the group consisting of hydrogen and alkyl, and n is 0 (zero), 1, 2, 3, or 4, and wherein the melt index of the first resin is from about 50 to about 800 grams, and the melt index of the second resin from about 850 to about 2,500 grams.

Description: This invention is directed to developer compositions, a process for preparing same as well as an imaging method utilizing said developer. More specifically, the present invention relates to a negatively charged liquid developer containing a mixture of resins. The developers of the present invention can be selected for a number of known imaging systems, such as xerographic imaging and printing processes, wherein latent images are rendered visible with the liquid developers illustrated herein. Image quality, solid area coverage and resolution characteristics for developed images usually require, for example, sufficient toner particle electrophoretic mobility. The mobility required for effective image development is primarily dependent on the imaging system used. The electrophoretic mobility is directly proportional to the charge on the toner particles and inversely proportional to the viscosity of the liquid developer fluid. For example, a 10 to 30 percent increase in fluid viscosity caused, for instance, by a 5 to 15°C decrease in temperature could result in a decrease in image quality, poor or unacceptable image development and undesirable background development, for example, because of a decrease in electrophoretic mobility. Insufficient particle charge can also result in poor transfer of the toner to paper or other final substrates. Poor transfer can, for example, result in poor solid area coverage if insufficient toner is transferred to the final substrate and can also cause image defects such as smears and hollowed fine features. To overcome or minimize such problems, the liquid toners of the present invention were arrived at after extensive research, and which toners result in, for example, sufficient particle charge to transfer and maintain their mobility within the required range of the particular imaging system employed. Other advantages associated with the present invention include increasing the desired negative charge on the developer particles and providing a charge adjuvant, or a charge control agent, that is superior to other known charge control agents like aluminum stearate. The aforementioned desired charge can result in improved image development and enhanced transfer. US-A-5,366,840 discloses a liquid developer comprising thermoplastic resin particles, an optional charge director and a charge additive or adjuvant which is capable of high particle charging. WO 92/17823 describes a polymer blend of at least two distinct polymer components preferably derived from ethylene/methacrylic acid copolymers and ethylene/vinyl acetate/acid terpolymers having very different viscosity-temperature behavior. For the preparation of a liquid toner these polymer blends are admixed with a liquid toner camer, preferably a non-polar liquid, pigment and a charge director. It is the object of the present invention to provide a liquid developer capable of high particle charging, and wherein improved image fusing is obtained, and wherein excellent development to and transfer from imaging members, such as known photoconductive imaging members, can be obtained, and to provide a liquid developer wherein developed image defects, such as smearing, loss of resolution and loss of density, are eliminated or minimized. This object has been achieved by a negatively charged liquid developer comprised of a nonpolar liquid, a mixture of a first and a second thermoplastic resin, a colorant, a charge director, an optional charge adjuvant, a charge control agent comprised of a component of the alternative formulas or wherein R 1 is selected from the group consisting of hydrogen and alkyl, and n is 0 (zero), 1, 2, 3, or 4, and wherein the melt index of said first resin is from 50 to 800 grams, and the melt index of said second resin is from 850 to 2,500 grams. Preferably, the first resin is present in an amount of from 10 to 90 parts, and the second resin is present in an amount of from 90 to 10 parts. It is also preferred that said alkyl contains from 1 to about 25 carbon atoms. The charge control agent is preferably a hydroxy aluminum complex of the formula as represented by or According to another aspect of the present invention, there is provided a process for the preparation of the liquid developer with improved fixing characteristics which comprises mixing the nonpolar liquid, the mixture of two thermoplastic resins, pigment, charge director and charge control agent; heating the mixture; and subsequently cooling the mixture. Of importance with respect to the present invention is the selection of two dissimilar resins with different melt indexes, and more specifically, the present invention in embodiments is directed to a negatively charged liquid developer comprised of a nonpolar liquid, a mixture of two thermoplastic resins with dissimilar melt indexes, a pigment, charge director, optional charge adjuvant, a charge control agent comprised of a component of the alternative formulas or wherein R 1 is selected from the group consisting of hydrogen and alkyl with, for example, to about 25 carbon atoms, and n is 0 (zero), 1, 2, 3, or 4, and wherein the melt index of the first resin is from 50 to 800 grams and the melt index of the second resin is from 850 to 2,500 grams for the second resin. In the present invention the melt index of the first and second resins is measured using ASTM method D-1238-65T, and wherein the melt index represents the number of grams of resin that flow through a 2.1 mm (0.0825 inch) orifice in 10 minutes at 190°C when a pressure of 2160 grams is applied. Suitable thermoplastic toner resins that can be selected for the liquid developers of the present invention in effective amounts, for example, in the range of 99 percent to 40 percent, and preferably 95 percent to 70 percent of developer solids comprised of thermoplastic resin, pigment, charge aluminum additive, and in embodiments other components that may comprise the toner. Generally, developer solids include the thermoplastic resin, optional pigment and charge control agent. Examples of resins include ethylene vinyl acetate (EVA) copolymers (ELVAX® resins, E.I. DuPont de Nemours and Company, Wilmington, Delaware); copolymers of ethylene and an α-β-ethylenically unsaturated acid selected from the group consisting of acrylic acid and methacrylic acid; copolymers of ethylene (80 to 99.9 percent), acrylic or methacrylic acid (20 to 0.1 percent)/alkyl (C1 to C5) ester of methacrylic or acrylic acid (0.1 to 20 percent); polyethylene; polystyrene; isotactic polypropylene (crystalline); ethylene ethyl acrylate series available as BAKELITE® DPD 6169, DPDA 6182 NATURAL™ (Union Carbide Corporation, Stamford, Connecticut); ethylene vinyl acetate resins like DQDA 6832 Natural 7 (Union Carbide Corporation); SURLYN® ionomer resin (E.I. DuPont de Nemours and Company); or blends thereof; polyesters; polyvinyl toluene; polyamides; styrene/butadiene copolymers; epoxy resins; acrylic resins, such as a copolymer of acrylic or methacrylic acid, and at least one alkyl ester of acrylic or methacrylic acid wherein alkyl is 1 to 20 carbon atoms, such as methyl methacrylate (50 to 90 percent)/methacrylic acid (0 to 20 percent)/ethylhexyl acrylate (10 to 50 percent); and other acrylic resins including ELVACITE® acrylic resins (E.I. DuPont de Nemours and Company); or blends thereof. Preferred copolymers in embodiments include the copolymers of ethylene and an α-β-ethylenically unsaturated acid of either acrylic acid or methacrylic acid. In preferred embodiments, NUCREL® resins available from E.I. DuPont de Nemours and Company like NUCREL® 599, NUCREL® 699, or NUCREL® 960 are selected as the thermoplastic resin. Examples of preferred resins selected include a mixture of two resins, a first and second resin as follows: First Resin: DuPont resins containing methacrylic acid; DuPont NUCREL 599®, 400 Melt Index, 10 weight percent to 90 percent component with 50 weight percent being preferred; DuPont NUCREL RX-76®, 800 Melt Index, 10 weight percent to 90 weight percent component with 50 weight percent being preferred. Second Resin: DuPont resins containing vinyl acetate (28 weight percent vinyl acetate); DuPont ELVAX 205W®, 850 Melt Index, 90 weight percent to 10 weight percent with 50 percent being preferred; DuPont ELVAX 200W®, 2500 Melt Index, 90 weight percent to 10 weight percent with 50 percent being preferred. RESIN MELT INDEX (APPROX.) FIX TIME 100 percent NUCREL 599® 400 >30 minutes 50 percent NUCREL RX-76® 825 <4 minutes 50 percent ELVAX 205W® 50 percent NUCREL RX-76® 1650 <2.5 minutes 50 percent ELVAX 200W® The fix time refers to the amount of time needed for the toner to fix to paper such as Xerox Corporation 4024. One advantage of mixing resins, especially the above resins for liquid developer, is that a mixture can be selected to enable a specific desirable fixing characterization based on the melt indices of the resin components. Examples of specific charge additives selected for the toners of the present invention, and present in various effective amounts of, for example, from 0.1 to 15, and preferably from 1 to 4 weight percent, include aluminum di-tertiary-butyl salicylate; hydroxy bis[3,5-tertiary butyl salicylic] aluminate; hydroxy bis[3,5-tertiary butyl salicylic] aluminate mono-, di-, tri- or tetrahydrates; hydroxy bis[salicylic] aluminate; hydroxy bis[monoalkyl salicylic] aluminate; hydroxy bis[dialkyl salicylic] aluminate; hydroxy bis[trialkyl salicylic] aluminate; hydroxy bis[tetraalkyl salicylic] aluminate; hydroxy bis[hydroxy naphthoic acid] aluminate; hydroxy bis[monoalkylated hydroxy naphthoic acid] aluminate; bis[dialkylated hydroxy naphthoic acid] aluminate wherein alkyl preferably contains 1 to 6 carbon atoms; bis[trialkylated hydroxy naphthoic acid] aluminate wherein alkyl preferably contains 1 to 6 carbon atoms; bis[tetraalkylated hydroxy naphthoic acid] aluminate wherein alkyl preferably contains 1 to 6 carbon atoms. The aforementioned additives can be prepared as illustrated in U.S. Patent 5,223,368, and more specifically, these additives can be obtained by the reaction of two equivalents of the sodium salt of, for example, 3,5-di-tert-butyl salicylic acid with one half equivalent of a dialuminum salt, for example aluminum sulfate, Al 2 (SO 4 ) 3 , in an aqueous alkali solution which generates a 2:1 complex of two salicylic acid molecules about a single central aluminum atom wherein both carboxylate groups of the salicylic acid moieties are covalently bonded through the carboxylate oxygen atom to the aluminum atom. Examples of liquid carriers or components selected for the developers of the present invention include a liquid with an effective viscosity of, for example, from 0.5 to 500 mPa·s (centipoise), and preferably from 1 to 20 mPa·s (centipoise), and a resistivity equal to or greater than 5 x 10 9 ohm/cm, such as 5 x 10 13 . Preferably, the liquid selected is a branched chain aliphatic hydrocarbon. A nonpolar liquid of the ISOPAR© series (manufactured by the Exxon Corporation) may also be used for the developers of the present invention. These hydrocarbon liquids are considered narrow portions of isoparaffinic hydrocarbon fractions with extremely high levels of purity. For example, the boiling range of ISOPAR G® is between about 157°C and about 176°C; ISOPAR H® is between about 176°C and about 191°C; ISOPAR K® is between about 177°C and about 197°C; ISOPAR L® is between about 188°C and about 206°C; ISOPAR M® is between about 207°C and about 254°C; and ISOPAR V® is between about 254.4°C and about 329.4°C. ISOPAR L® has a mid-boiling point of approximately 194°C. ISOPAR M® has an auto ignition temperature of 338°C. ISOPAR G® has a flash point of 40°C as determined by the tag closed cup method; ISOPAR H® has a flash point of 53°C as determined by the ASTM D-56 method; ISOPAR L® has a flash point of 61°C as determined by the ASTM D-56 method; and ISOPAR M® has a flash point of 80°C as determined by the ASTM D-56 method. The liquids selected are generally known and should have an electrical volume resistivity in excess of 10 9 ohm-centimeters and a dielectric constant below 3.0 in embodiments of the present invention. Moreover, the vapor pressure at 25°C should be less than 1,33 kPa (10 Torr) in embodiments. While the ISOPAR® series liquids can be the preferred nonpolar liquids for use as dispersants in the liquid developers of the present invention, the essential characteristics of viscosity and resistivity may be satisfied with other suitable liquids. Specifically, the NORPAR® series available from Exxon Corporation, the SOLTROL® series available from the Phillips Petroleum Company, and the SHELLSOL® series available from the Shell Oil Company can be selected. The amount of the liquid employed in the developer of the present invention is, for example, from 85 to 99.9 weight percent, and preferably from 90 to 99 percent by weight of the total developer dispersion, however, other effective amounts may be selected. The total solids content of the developer in embodiments is, for example, 0.1 to 15 percent by weight, preferably 0.3 to 10 percent. Solids weight or content refers to the fraction of toner remaining after the solvent or nonpolar liquid has been evaporated, e.g. by heating in an oven for 4 hours. The liquid developer of the present invention may optionally contain, and preferably does contain in embodiments a colorant dispersed in the resin particles. Colorants, such as pigments or dyes and mixtures thereof, are preferably present to render the latent image visible. The colorant may be present in the toner in an effective amount of, for example, from 0.1 to 60 percent, and preferably from 1 to 40, and in embodiments 10 percent by weight based on the total weight of solids contained in the developer. The amount of colorant used may vary depending on the use of the developer. Examples of pigments which may be selected include carbon blacks available from, for example, Cabot Corporation, FANAL PINK™, PV FAST BLUE. Suitable nonpolar liquid soluble ionic or zwitterionic charge director compounds include anionic glyceride, such as EMPHOS D70-30C™ and EMPHOS F27-85™, two products available from Witco Corporation, New York, NY, which are sodium salts of phosphated mono and diglycerides with unsaturated and saturated acid substituents, respectively, reference copending application U.S. Serial No. 08,505,043, lecithin, BASIC BARIUM PETRONATE®, NEUTRAL BARIUM PETRONATE®, CALCIUM PETRONATE®, NEUTRAL CALCIUM PETRONATE®, oil soluble petroleum sulfonates, Witco Corporation, New York, NY; metallic soaps such as barium, calcium, lead, and zinc stearates; cobalt, manganese, lead, and zinc linoleates, calcium and cobalt octoates, quaternary ammonium block copolymers as illustrated, for example, in U.S. Patent 5,035,972, other known charge directors, which are selected in various effective amounts, such as for example from 0.25 to 1,500 milligrams/gram (per gram of developer solids), and preferably 2.5 to 400 milligrams/gram based on the amount of developer solids comprised of resin, pigment, and charge control agent or additive. The charge on the toner particles may be measured with respect to particle mobility using a high field measurement device. Particle mobility is a measure of the velocity of a toner particle in a liquid developer divided by the size of the electric field within which the liquid developer is employed. The greater the charge on a toner particle, the faster it moves through the electrical field of the development zone. The movement of the particle is important for image development and background cleaning. Toner particle mobility can be measured using the electroacoustic effect, the application of an electric field, and the measurement of sound described, for example, in U.S. Patent 4,497,208. This technique is particularly useful for nonaqueous dispersions because the measurements can be accomplished at high volume loadings, for example greater than 1 weight percent. Measurements rendered by this technique have been shown to correlate with image quality, that is for example high measured mobilities have been shown to result in improved image density, higher image resolution and superior transfer efficiency. Residual conductivity, that is the conductivity from the charge director, can be measured with a low field device as described herein. To increase the toner particle charge and, accordingly, increase the mobility and transfer latitude of the toner particles, charge adjuvants can be added to the toner particles. For example, adjuvants, such as metallic soaps like aluminum or magnesium stearate or octoate, fine particle size oxides, such as oxides of silica, alumina, titania, and the like, paratoluene sulfonic acid, and polyphosphoric acid, may be added. Negative charge adjuvants increase the negative charge of the toner particles, while the positive charge adjuvants increase the positive charge of the toner particles. With the invention of the present application, these types of adjuvants can assist in enabling improved toner charging characteristics, namely, an increase in particle charge that results in improved electrophoretic mobility for improved image development and transfer to allow superior image quality with improved solid area coverage and resolution in embodiments. The adjuvants can be added to the toner particles in an amount of from 0.1 percent to 15 percent of the total developer solids and preferably from 1 percent to 5 percent of the total weight of solids contained in the developer. The liquid electrostatic developer of the present invention can be prepared by a variety of processes such as, for example, mixing in a nonpolar liquid the thermoplastic resin mixture, charging additive, and optional colorant and adjuvant in a manner that the resulting mixture contains, for example, 15 to 40 percent by weight of solids; heating the mixture to a temperature of from 70°C to 130°C until a uniform dispersion is formed; adding an additional amount of nonpolar liquid sufficient to decrease the total solids concentration of the developer to 10 to 20 percent by weight; cooling the dispersion to 10°C to 30°C; adding charge director compound to the dispersion; and diluting the dispersion. In the initial mixture, the resin mixture, colorant and charge additive may be added separately to an appropriate vessel such as, for example, an attritor, heated ball mill, heated vibratory mill, such as a Sweco Mill manufactured by Sweco Company, Los Angeles, CA, equipped with particulate media for dispersing and grinding, a Ross double planetary mixer manufactured by Charles Ross and Son, Hauppauge, NY, or a two roll heated mill, which usually requires no particulate media. Useful particulate media include materials like spheres or cylinders of stainless steel, carbon steel, alumina, ceramic, zirconia, silica and sillimanite. Carbon steel particulate media are particularly useful when colorants other than black are used. A typical diameter range for the particulate media is in the range of 0.04 to 0.5 inch (approximately 1.0 to approximately 13 millimeters). Sufficient nonpolar liquid is added to provide a dispersion of from about 15 to about 50 percent solids. This mixture is then subjected to elevated temperatures during the initial mixing procedure to plasticize and soften the resin. The mixture is sufficiently heated to provide a uniform dispersion of all the solid materials of, for example, colorant, charge director, adjuvant and resin. However, the temperature at which this step is undertaken should not be so high as to degrade the nonpolar liquid or decompose the resin or colorant if present. Accordingly, the mixture in embodiments is heated to a temperature of from 70°C to 130°C, and preferably from 75°C to 110°C. The mixture may be ground in a heated ball mill or heated attritor at this temperature for 15 minutes to 5 hours, and preferably 60 to 180 minutes. After grinding at the above temperatures, an additional amount of nonpolar liquid may be added to the dispersion. The amount of nonpolar liquid to be added should be sufficient in embodiments to decrease the total solids concentration of the dispersion to 10 to 20 percent by weight. The dispersion is then cooled to 10°C to 40°C, and preferably to 15°C to 30°C, while mixing is continued until the resin admixture solidifies or hardens. Upon cooling, the resin admixture precipitates out of the dispersant liquid. Cooling is accomplished by methods such as the use of a cooling fluid like water, glycols, such as ethylene gylcol, in a jacket surrounding the mixing vessel. Cooling is accomplished, for example, in the same vessel, such as an attritor, while simultaneously grinding with particulate media to prevent the formation of a gel or solid mass; without stirring to form a gel or solid mass, followed by shredding the gel or solid mass and grinding by means of particulate media; or with stirring to form a viscous mixture and grinding by means of particulate media. The resin precipitate is cold ground for 1 to 36 hours, and preferably from 2 to 6 hours. Additional liquid may be added at any time during the preparation of the liquid developer to facilitate grinding or to dilute the developer to the appropriate percent solids needed for developing. Other processes of preparation are generally illustrated in U.S. Patents 4,760,009; 5,017,451; 4,923,778; 4,783,389. The charge director can be added during or after the above preparative sequence. As illustrated herein, the developers or inks of the present invention can be selected for imaging and printing methods wherein, for example, a latent image is formed on a photoconductive imaging member, reference for example selenium, selenium alloys, those of U.S. Patent 4,265,990 followed by development with the toner of the present invention by, for example, immersion of the imaging member in the liquid toner; transfer to a suitable substrate like paper; and fixing by heating. Embodiments of the invention will be illustrated in the following nonlimiting Examples. The conductivity of the liquid toner dispersions and charge director solutions were determined with a Scientifica 627 Conductivity Meter (Scientifica, Princeton, NJ). The measurement signal for this meter is a low distortion 18 hz sine wave with an amplitude of 5.4 to 5.8 volts rms. Toner particle mobilities and zeta potentials were determined with a MBS-8000 electrokinetic sonic analysis (ESA) system (Matec Applied Science Hopkinton, MA). The system was calibrated in the aqueous mode per manufacturer's recommendation to provide an ESA signal corresponding to a zeta potential of - 26 millivolts for a 10 percent (v/v) suspension of LUDOX™ (DuPont). The system was then set up for nonaqueous measurements. The toner particle mobility can be dependent on a number of factors, including primarily particle charge and particle size. The ESA system also calculates the zeta potential which is directly proportional to toner charge and is independent of particle size. Particle size was measured by Horiba CAPA-500 centrifugal automatic particle analyzer manufactured by Horiba Instruments, Inc., Irvine, CA. All parts and percentages in the Examples are by weight unless otherwise indicated. EXAMPLE I 50 Percent ELVAX 205W® and 50 Percent NUCREL RX-76®; 0.5 Percent Alohas Eighty-four (84) grams of NUCREL RX-76®, poly(ethylene-co-methacrylic acid, (a copolymer of ethylene and methacrylic acid with a melt index at 190°C of 800 grams, available from E.I. DuPont de Nemours & Company, Wilmington, DE), 1.14 grams of the charge control agent Alohas (aluminum di-t-butyl salicylate), 56.8 grams of the yellow pigment (Paliotol Yellow D1155™) and 370 grams of ISOPAR-M® (Exxon Corporation) were added to a Union Process 1S attritor (Union Process Company, Akron, Ohio) charged with 0.1857 inch (4.76 millimeters) diameter carbon steel balls. The mixture was milled in the attritor which was heated with running steam through the attritor jacket at 75 to 95°C for 1 hour. After the 1 hour of hot milling in the attritor, to the mixture wwere s added 84.0 grams of ELVAX 205W®, poly(ethylene-co-vinylacetate), (a copolymer of ethylene and vinyl acetate with a melt index at 190°C of 850, available from E.I. DuPont de Nemours & Company, Wilmington, DE), and the mixture was milled in the attritor which was heated with running steam through the attritor jacket at 60 to 80°C for 1 hour. To the mixture were added 980 grams of ISOPAR-G® (Exxon Corporation), then cooled by running water through the attritor jacket to 23°C, and ground in the attritor for an additional 2 hours. Additional ISOPAR-G® was added and the mixture was separated by the use of a metal grate from the steel balls. To 108.9 grams of the mixture (13.77 percent solids) were added 1,376.1 grams of ISOPAR-G® and 1.5 grams of 93,000 M W , the known charge director AB polymer 2.5:97.5 HBr quaternary salt, poly[2-ethylhexyl methacrylate (B block) co-dimethyl-ammoniumethyl methacrylate bromide (A block)]. The image quality and fix time were assessed using a Savin 870 copier. The image quality is excellent with minimum background deposits, and the images possessed excellent to optimum fushing characteristics. EXAMPLE II 50 Percent ELVAX 200W® and 50 Percent NUCREL RX-76®; 0.5 Percent ALOHAS Eighty-four (84) grams of NUCREL RX-76® (a copolymer of ethylene and methacrylic acid with a melt index at 190°C of 800, available from E.I. DuPont de Nemours & Company, Wilmington, DE), 1.14 grams of the charge control agent Alohas (aluminum di-t-butyl salicylate), 56.8 grams of the yellow pigment (Paliotol Yellow D1155™), and 370 grams of ISOPAR-M® (Exxon Corporation) were added to a Union Process 1S attritor (Union Process Company, Akron, Ohio) charged with 0.1857 inch (4.76 millimeters) diameter carbon steel balls. The mixture was milled in the attritor which was heated with running steam through the attritor jacket at 75 to 95°C for 1 hour. After the 1 hour of hot milling in the attritor, to the mixture were added 84.0 grams of ELVAX 200W® (a copolymer of ethylene and vinyl acetate with a melt index at 190°C of 2500, available from E.I. DuPont de Nemours & Company, Wilmington, DE), and the mixture was milled in the attritor which was heated with running steam through the attritor jacket at 60 to 80°C for 1 hour. To the mixture were added 980 grams of ISOPAR-G® (Exxon Corporation), then cooled by running water through the attritor jacket to 23°C, and ground in the attritor for an additional 2 hours. Additional ISOPAR-G® was added and the mixture was separated by the use of a metal grate from the steel balls. To 114.0 grams of the mixture (13.16 percent solids) were added 1,356 grams of ISOPAR-G® and 1.5 grams of 93,000 M W , known AB 2.5:97.5 HBr quaternary salt charge director. Similar imaging results to that of Example I are believed to be achievable. CONTROL 1 100 Percent NUCREL 599®; 0.5 Percent ALOHAS One Hundred Sixty Eight (168) grams of NUCREL 599® (a copolymer of ethylene and methacrylic acid with a melt index at 190°C of 400, available from E.I. DuPont de Nemours & Company, Wilmington, DE), 1.14 grams of the charge control agent Alohas (aluminum di-t-butyl salicylate) 56.8 grams of the yellow pigment (Paliotol Yellow D1155™), and 370 grams of ISOPAR-M® (Exxon Corporation) were added to a Union Process 1S attritor (Union Process Company, Akron, Ohio) charged with 0.1857 inch (4.76 millimeters) diameter carbon steel balls. The mixture was milled in the attritor which was heated with running steam through the attritor jacket at 75 to 95°C for 2 hours, then cooled by running water through the attritor jacket to 23°C, and ground in the attritor for an additional 4 hours. Additional ISOPAR-G® was added and the mixture was separated by the use of a metal grate from the steel balls. To 110.9 grams of the mixture (13.53 percent solids) were added 1,376 grams of ISOPAR-G® and 1.5 grams of 93,000 M W , AB 2.5:97.5 HBr quaternary salt charge director. Image development resolution and fixing were of lower quality then the images of Examples I and II, where two resins with different melt indexes were selected.

Claims: A negatively charged liquid developer comprising a nonpolar liquid, a mixture of a first and a second thermoplastic resin, a colorant, a charge director, an optional charge adjuvant, a charge control agent comprising a component of the alternative formulas or wherein R 1 is selected from the group consisting of hydrogen and alkyl, and n is 0 (zero), 1, 2, 3, or 4, and wherein the melt index of said first resin is from 50 to 800 grams, and the melt index of said second resin is from 850 to 2,500 grams. The liquid developer in accordance with claim 1, wherein the first resin is present in an amount of from 10 to 90 parts, and the second resin is present in an amount of from 90 to 10 parts. The liquid developer in accordance with either of claims 1 or 2, wherein the first resin is a methacrylic acid or acrylic acid containing resin. The liquid developer in accordance with any of claims 1 to 3, wherein the second resin is a copolymer of ethylene and vinyl acetate. The liquid developer in accordance with any of claims 1 to 4, wherein said alkyl contains from 1 to 25 carbon atoms. The liquid developer in accordance with any of claims 1 to 5, wherein the charge control agent is a hydroxy aluminum complex of the formula as represented by or The liquid developer in accordance with any of claims 1 to 5, wherein the charge control agent is selected from the group consisting of hydroxy bis[3,5-di-tert-butyl salicylic] aluminate, hydroxy bis[3,5-di-tert-butyl salicylic] aluminate monohydrate, hydroxy bis[3,5-di-tert-butyl salicylic] aluminate dihydrate, hydroxy bis[3,5-di-tert-butyl salicylic] aluminate tri- or tetrahydrate, and mixtures thereof. The liquid developer in accordance with any of claims 1 to 7, wherein the colorant is a pigment. A process for the preparation of the liquid developer according to any of claims 1 to 8 having improved fixing characteristics, comprising mixing the nonpolar liquid, the mixture of the two thermoplastic resins, pigment, charge director and charge control agent; heating said mixture, and subsequently cooling said mixture. An imaging method which comprises forming an electrostatic latent image followed by the development thereof with the liquid developer of any of claims 1 to 8.

Inventors: CARUTHERS EDWARD B JR, CHAMBERLAIN SCOTT D, GIBSON GEORGE A, THORNTON CONSTANCE J, CARUTHERS, EDWARD B. JR., CHAMBERLAIN, SCOTT D., GIBSON, GEORGE A., THORNTON, CONSTANCE J.
Applicants: XEROX CORP, XEROX CORPORATION
Application year: 1997
Main classification: G03G9
IPC codes: G03G9