Sulphur resistant lean-burn NOx catalyst for treating diesel emissions

Abstract: The invention is a nitrogen oxide trap comprising a porous support; and catalysts comprising platinum and either sodium, potassium, or their mixture loaded on the porous support. The sodium, potassium, or sodium/potassium mixture is present in a significantly high loading of at least 30 weight percent, and the platinum comprises 0.2-3 weight percent, based on the weight of the porous support. The trap may be used in an internal combustion engine exhaust gas catalyst system. During lean-burn operation of the engine the trap sorbs nitrogen oxides (NOx) and releases the nitrogen oxides during decreased oxygen concentration in the exhaust gas, the desorbed NOx being converted to N 2 and O 2 .

Description: This invention relates to nitrogen oxide traps employed in the exhaust system of an internal combustion engine to absorb nitrogen oxides during lean-burn operation. Catalysts are employed in the exhaust systems of automotive vehicles to convert carbon monoxide, hydrocarbons, and nitrogen oxides (NO x ) produced during engine operation into more desirable gases. When the engine is operated in a stoichiometric or slightly rich air/fuel ratio, i.e., between about 14.7 and 14.4 , catalysts containing precious metals like palladium and rhodium are able to efficiently convert all three gases simultaneously. Hence, such catalysts are often called "three-way" catalysts. It is desirable to operate the engine under "lean-burn" conditions where the A/F ratio is greater than 14.7, generally between 19 and 27, to realise a benefit in fuel economy. Such three-way catalysts are able to convert carbon monoxide and hydrocarbons but are not efficient in the reduction of NO x during lean-burn (excess oxygen) operation. One approach for treating NOx in exhausts from lean-burn engines which is currently receiving considerable attention involves the use of so-called NO x traps which generally consist of platinum in combination with an alkali metal or alkaline earth element. The widely held mechanism for this absorption phenomena is that the platinum first oxidises NO to NO 2 and the NO 2 subsequently forms a nitrate complex with the alkali metal or alkaline earth, e.g., like sodium or potassium, respectively. In a stoichiometric or rich environment, the nitrate is thermodynamically unstable, and the stored NO x is released. NO x then catalytically reacts with reducing species in the exhaust gas to form N 2 . European Patent Application EP-A-0613714 published September 7 th , 1994 discloses that platinum or palladium in various combinations with at least two ingredient materials of the alkali metals, alkaline earth metals, transition metals, or rare-earth metals are capable of storing or absorbing nitrogen oxides under exhaust conditions of excess oxygen. For example, when requiring two alkali metal ingredients, the loading amounts of the two ingredients is taught to preferably fall in a range of from 0.05 to 2.0 moles/litre in total. Taking sodium as the alkali metal, this corresponds to a range of 0.80 to 3.2 weight percent of the porous support material. For potassium, this range is 1.5 to 5.6 weight percent of the porous support material. This application instructs that when the alkali metals are loaded in an amount more than this upper limit, the advantageous effects resulting from the loading saturate, and the porous support diminishes the surface area. EP-A-0764459 describes a nitrogen oxide trap for use during lean-burn operation of an internal combustion engine, the trap comprising distinct catalyst phases: (a) a first porous support loaded with 0.1 to 5 weight percent platinum, and (b) a second porous support loaded with 2 to 30 weight percent of at least one material selected from the group consisting of alkali metal elements and alkaline earth metals, the weight percent being based on the weight of its porous support. EP-A-0645173 describes a catalyst for purifying carbon monoxide, hydrocarbons and nitrogen oxides in exhaust gases at the stoichiometric point or in oxygen-rich atmospheres, thereby purifying the exhaust gases, said catalyst comprising: an alumina support with lithium dissolved therein to form a solid solution; at least one ingredient selected from the group consisting of Pt or Pd, and loaded on said alumina support; and at least one second ingredient selected from the group consisting of alkali metals, alkaline earth metals and rare earth elements included La, and loaded on said alumina support. Li is present in an amount of from 0.02 to 0.35 mole; the first ingredient is present in an amount of 0.1 to 20g; the second ingredient is present in an amount of 0.1 to 1.2 mole, all with respect to 1 mole of said alumina support. In all of the examples the second ingredient is barium which is present in an amount of 0.3 mole. The alkali metal and alkaline earth metals which are typically utilised for NOx sorption have, however, the serious drawback that they are readily poisoned by sulphur in the exhaust gas. Most fuels for automotive vehicles contain sulphur and when burnt, the sulphur is converted to sulphur compounds like SO 2 . Over time, the sulphur compounds react with these trap materials forming sulphates which will not revert back to the sorption material. These sulphates are inactive for NOx sorption. As a result, the typical NOx trap is strongly deactivated by fuel sulphur. We have unexpectedly found that by forming a NOx trap from alkali metals selected from the group consisting of sodium, potassium or their mixture along with platinum and, most critically, loading the sodium or potassium in a significantly higher amounts than previously described, this poisoning effect is substantially reduced. Thus the present invention Na/Pt, K/Pt, or Na+K/Pt traps retain their NOx trapping efficiency as compared to those loaded with much less sodium or potassium. This invention is directed to an nitrogen oxide (NO x ) trap useful to trap nitrogen oxides during the lean-burn operation of an internal combustion engine. It comprises a porous support; and catalysts consisting essentially of (i) at least 50 weight percent alkali metal selected from the group consisting of sodium, potassium, and their mixture; and (ii) 0.2 to 4 weight percent platinum loaded on said porous support, each amount of catalysts (i) and (ii) being individually based on the weight of the porous support. Preferably the support material is gamma-alumina. In another aspect, the invention is an internal combustion engine exhaust gas catalyst system comprising the NO x trap. The engine may be a gasoline engine or a diesel engine. The trap is arranged in the exhaust system and absorbs NO x when the air/fuel ratio of exhaust gas flowing into said trap is lean and releases the absorbed NO x when the oxygen concentration in the exhaust gas is lowered, as during stoichiometric or rich operation of the engine. According to another aspect, the invention is a process for trapping nitrogen oxides using the disclosed traps. Advantageously, it has been found that by using a relatively high loadings of sodium, potassium, or their mixture in combination with platinum in a nitrogen oxide trap, sulphur poisoning of the trap material can be greatly reduced. Thus, this invention trap is able to operate to sorb NOx without forming the sulphates which are ineffective for NOx sorption. The invention will now be described, by way of example, with reference to the accompanying drawings, in which: Fig. 1 is a graph showing the effect of sulphur poisoning on nitrogen oxide trapping efficiency of sodium/platinum NOx traps (one being according to an embodiment of the present invention and the other being a comparative example) as the loading of the sodium is varied; and Fig. 2 is a graph showing the effect of sulphur poisoning on nitrogen oxide trapping efficiency of potassium/platinum NO x traps (according to embodiments of the present invention and a comparative example) as the loading of the potassium is varied. This invention, according to one aspect, is directed to an internal combustion engine exhaust gas catalyst system comprising a nitrogen oxide trap. The NO x trap comprises a porous support impregnated with (i) alkali metal selected from the group consisting of sodium, potassium, and their mixture; and (ii) platinum. It is required that the support is highly loaded with sodium, potassium, or their mixture, i.e., being at least 50 weight percent, with a maximum of about 70 weight percent, based on the weight of the support. In addition, the support is loaded with the precious metal platinum in an amount between 0.2 and 4 weight percent, preferably being between about 1 and 4 percent by weight, more preferably being about 1 to 2 weight percent platinum, most preferably being about 2, being based on the weight of the support. Optimally, the support carries 50 to 70 weight percent of the alkali metal and 1 to 4 weight percent platinum. The weight percent of the alkali metal and platinum are each individually based on the weight of the porous support material. When a mixture of sodium and potassium is used, it preferably comprises a ratio between 1:2 and 1:4. Also, it may be desirable to additionally deposit a small quantity of rhodium with the platinum on to the support material, the rhodium being about 1/5 to 1/10 of the platinum amount. The porous support (washcoat) material loaded with the catalysts is preferably a high surface area washcoat material like alumina, preferably being gamma-alumina. Still other washcoat materials which may be used at the high operation temperatures associated with an internal combustion engine exhaust system include, but are not limited to, zeolite, ceria, and zirconia. Such washcoat materials, useful for carrying catalyst materials, are well known to those skilled in the art. The choice of the particular porous support (washcoat) material is not critical to this invention. Desirably, the support material has a surface area between about 5 and 300 m 2 /g. For useful application in an exhaust gas system of for example gasoline or diesel engines, the washcoat will be carried on a substrate of a high temperature stable, electrically insulating material. Typical of such substrate materials are cordierite, mullite, etc. The substrate may be in any suitable configuration, often being employed as a monolithic honeycomb structure, spun fibres, corrugated foils or layered materials. Still other materials and configurations useful in this invention and suitable in an exhaust gas system will be apparent to those skilled in the art in view of the present disclosure. The catalysts and washcoat may be applied to the substrate as a mixture of washcoat and catalyst or in sequential steps, the washcoat being applied first, in a manner which would be readily apparent to those skilled in the art of catalyst manufacture. Preferably, the washcoat is first applied to the substrate followed by drying and calcination of the washcoat. Then the sodium or potassium and platinum catalysts can be deposited on the washcoat, as by impregnation techniques well known to those skilled in the art. According to such techniques, the sodium or potassium and platinum catalysts, individually or together, would be dissolved as soluble precursors thereof, e.g., as a salt like sodium or potassium nitrate in an aqueous or organic solvent solution which is then impregnated into the washcoat. The sodium or potassium and platinum can be impregnated sequentially; the order is not important. The sodium or potassium and platinum precursors can also be dissolved together in a common solution and impregnated into the porous support in a single step. The particular salt employed as well as the solvent is not critical to this invention. Exemplary platinum containing compounds include chloroplatinic acid. Other such materials which may be used would be apparent to those skilled in the art in view of the present disclosure. Drying and calcination of the impregnated washcoat in air generally converts the sodium nitrate and potassium nitrate to the corresponding oxide, carbamate or hydroxide. As is known in the art, NO x traps are susceptible to poisoning by sulphur compounds present in the exhaust gases. We have found that by using a very high loading of either sodium or potassium along with platinum, this problem is overcome to a large degree. That is, the NOx trapping efficiency of the catalyst is maintained as shown in Figures 1 and 2. The internal combustion engine catalyst system of this invention may include another catalyst device as, for example, a catalytic converter employing a conventional three-way catalyst containing palladium, etc. The three-way catalyst can be placed upstream of the NO x trap, hence closer to the engine. In such an arrangement, the three-way catalyst being closely mounted to the engine would warm up quickly and provide for efficient engine cold start emission control. Once the engine is warmed up, the three-way catalyst will remove hydrocarbons, carbon monoxide, and nitrogen oxides from the exhaust during stoichiometric operation and hydrocarbons and carbon monoxide during lean operation. The NO x trap would be positioned downstream of the three-way catalyst where the exhaust gas temperature enables maximum NO x trap efficiency. Also, with the NO x trap positioned downstream of the three-way catalyst in a remote location, it is protected against very high exhaust gas temperatures which could damage it. During periods of lean-burn engine operation when NO x passes through the three-way catalyst, NO x is stored on the trap. The NO x trap is periodically regenerated by short periods or intervals of slightly rich engine operation. The stored NO x is then released from the alkali metal trapping material and is catalytically reduced over the platinum by the excess CO, H 2 and HCs present in the exhaust. In general, the released NO x is efficiently converted to N 2 , which efficiency is enhanced when rhodium is contained within the NO x trap washcoat. However, one may wish to place a second three way catalyst downstream of the NO x trap in order to further aid in this regard. This invention catalyst has particular utility when used with lean-burn engines. Lean-burn engines are those which at least during part of their operation operate with air/fuel ratios containing excess oxygen relative the stoichiometric ratio. For gasoline engines that range is usually 19-27 and for diesel the range is usually 19-40. Example 1 A nitrogen oxide trap according to an embodiment of the present invention was prepared as follows. Gamma-alumina (100m2/g) was ball milled and mixed with distilled water to produce a slurry. The slurry was applied to a corderite monolith (400 cells/in 2 ) to obtain a 25 wt% loading of the alumina. The monolith was subsequently dried at 120° C to remove the water and calcined in air at 500° C for 6 hours. The alumina coated monolith was first impregnated with an aqueous solution containing sodium nitrate adjusted so as to provide 50 wt% sodium on the alumina washcoat. Following impregnation with the solution, the alumina was dried at 120° C for 4 hours to remove the water and then calcined at 500° C for 6 hours. The resulting product was then loaded with platinum in a similar fashion. That is, this washcoat was subsequently impregnated with an aqueous solution containing hexachloroplatinic acid (adjusted so as to provide 2.0 wt% platinum on the alumina washcoat), dried, and calcined as above. A similar sodium/platinum trap was made as above the only variation being in the loading of the sodium which was adjusted to 15 wt% as shown in Figure 1. The trap with the 15 wt% Na loading is a comparative example, the 50 wt % sodium trap is according to an embodiment of the present invention. In order to test the NO x sorption efficiency of the traps when subjected to SO 2 , they were subjected to a simulated exhaust gas containing: 500 ppm NO, 10% CO 2 , 10% H 2 O, 0.1%CO, 0.03% H 2 , 50ppm C 3 H 6 , 20 ppm SO 2 and 6% O 2 . The total exhaust gas flow rate was 3 litre/min, the space velocity was 20,000hr -1 , and the temperature of the NO x trap was 500°C. It can be seen from Fig. 1 that as the sodium loading is increased from 15 wt% to 50 wt%, the sulphur poisoning is significantly mitigated. With the 50 wt% sodium sample, very little loss of NO x trapping efficiency was observed. This was unexpected since, as discussed above, European Application 0613714A2 teaches away from high loadings sodium above 1 wt%. While not wishing to be bound by theory, it is believed that a platinum-sodium interaction is created which suppresses the formation of sulphate over the platinum as the sodium loading is increased. Neither the validity nor understanding of this theory is necessary for the practice of this invention. Example 2 A gamma alumina coated monolith was prepared according to the previous example and impregnated with an aqueous solution containing potassium nitrate. The concentration of potassium nitrate was adjusted so as to provide for 50 wt% K on the alumina washcoat. The monolith was then dried at 120°C for 4 hours and calcined at 500°C for 6 hours. The resulting product was then loaded with platinum by impregnation with an aqueous solution containing hexachloroplatinic acid (adjusted so as to provide 2.0 wt% on the alumina washcoat), dried, and calcined as before. For a comparative example, a similar potassium/platinum trap was made as outlined above the loading of the potassium was adjusted to 20 wt% as shown in Figure 2. The 50 wt% potassium trap is according to the present invention whereas the 20 wt% potassium trap is merely a comparative example. The NO x sorption efficiency of these traps was tested as outlined in Example 1 with the exception that the SO 2 concentration in the synthetic exhaust gas was set to 10 ppm and the NO x trap temperature was 600°C. As can be seen from Figure 2, the sulphur poisoning is significantly reduced as the potassium loading is increased from 20 to 50 wt%. Example 3 A gamma alumina coated monolith is prepared according to the previous example and impregnated with an aqueous solution containing either sodium nitrate or potassium nitrate adjusted so as to provide for 50 wt% sodium or potassium on the alumina washcoat. Following impregnation, the monolith is dried at 120°C for 4 hours and then calcined at 500°C for 6 hours. The resulting product is then impregnated with an aqueous solution containing hexachloroplatinic acid and rhodium nitrate, dried, and calcined as above. The concentrations of hexachloroplatinic acid and rhodium nitrate are adjusted so as to provide for 2 wt% Pt and 0.2 wt% Rh on the alumina washcoat. The NO x is efficiently trapped by the catalyst. Example 4 A gamma alumina coated monolith is prepared according to the previous example and impregnated with an aqueous solution containing either sodium nitrate or potassium nitrate adjusted so as to provide for 50 wt% sodium or potassium on the alumina washcoat. Following impregnation, the monolith was dried at 120°C for 4 hours and then calcined at 500°C for 6 hours. The resulting product is then impregnated with an aqueous solution containing hexachloroplatinic acid; the concentration of hexachloroplatinic acid is adjusted so as to provide 1.0 wt% of platinum on the alumina washcoat. The monolith is then dried and calcined as before. The NO x is efficiently trapped by the catalyst. Example 5 A gamma alumina coated monolith is prepared according to the previous example and impregnated with an aqueous solution containing either sodium nitrate or potassium nitrate and hexachloroplatinic acid; the concentrations are adjusted so as to provide for 25 wt% platinum on the alumina washcoat. Following impregnation, the monolith is dried at 120°C for 4 hours and then calcined at 500°C for 6 hours. The NO x is efficiently trapped by the catalyst. Example 6 Gamma alumina powder (100m 2 /g) is impregnated via an incipient wetness technique with a solution containing sodium nitrate and hexachloroplatinic acid; the concentrations of sodium nitrate and hexachloroplatinic acid are adjusted so as to provide for 50 wt% sodium and 2 wt% platinum on the alumina powder. Similarly a powder is impregnated with potassium nitrate to also provide a 50 wt. % loading of potassium on the alumina washcoat. Following impregnation's, the alumina powders are dried at 120°C for 4 hours and then calcined at 500°C for 6 hours. The resulting products are then individually ball milled and mixed with distilled water in order to produce slurries. Each slurry is applied to a corderite monolith to obtain a 25 wt% loading of the Pt/Na/Al 2 O 3 or Pt/K/ Al 2 O 3 material. The monolith is subsequently dried at 120°C to remove the water and calcined in air at 500°C for 6 hours. The NO x is efficiently trapped by the catalyst.

Claims: A nitrogen oxide trap capable of trapping nitrogen oxide present in the exhaust gases generated during lean-burn operation of an internal combustion engine, said trap comprising: a porous support; and catalysts consisting essentially of (i) at least 50 weight percent alkali metal selected from the group consisting of sodium, potassium, and their mixture; and (ii) 0.2 to 4 weight percent platinum loaded on said porous support, each amount of catalysts (i) and (ii) being individually based on the weight of the porous support. The nitrogen oxide trap according to claim 1, wherein said platinum is present in an amount of about 1 to 4 weight percent on said support. The nitrogen oxide trap according to either claim 1 or claim 2, wherein said support comprises alumina. The nitrogen oxide trap according to any one of the preceding claims, wherein said support is loaded with about 1 to 4 weight percent platinum and 50 to 70 weight percent of said alkali metal, each based on the weight of the porous support. The nitrogen oxide trap according to any one of the preceding claims, in which the catalysts include rhodium. An internal combustion engine exhaust gas catalyst system comprising a nitrogen oxide trap being arranged in the exhaust system and absorbing nitrogen oxides when the air/fuel ratio of exhaust gas flowing into said trap is lean, said nitrogen oxide trap releasing absorbed nitrogen oxides when the oxygen concentration in said exhaust gas is lowered, said nitrogen oxide trap comprising: a porous support; and catalysts consisting essentially of (i) at least 50 weight percent alkali metal selected from the group consisting of sodium, potassium, and their mixture, and (ii) 0.2 to 4 weight percent platinum and, optionally, rhodium loaded on said porous support, each amount of catalysts (i) and (ii) being individually based on the weight of the support. The exhaust gas catalyst system according to claim 6, wherein platinum is loaded on said support in an amount of 1 to 2 weight percent. The exhaust gas catalyst system according to either claim 6 or claim 7, wherein said support comprises alumina. The exhaust gas catalyst system according to claim 6, 7 or 8, wherein said support was loaded with about 1 to 4 weight percent platinum and 50 to 70 weight percent of said alkali metal, each based on the weight of the porous support. The exhaust gas catalyst system according to any one of claims 6 to 9, which further comprises a three way catalyst positioned upstream of the nitrogen oxide trap.

Inventors: HEPBURN JEFFREY SCOTT, WATKINS WILLIAM LEWIS HENDERSO, HEPBURN, JEFFREY SCOTT, WATKINS, WILLIAM LEWIS HENDERSON
Applicants: FORD GLOBAL TECH INC, FORD GLOBAL TECHNOLOGIES, INC.
Application year: 1997
Main classification: B01D53
IPC codes: B01D53, B01J23