PLANOGRAPHIC PRINTING

Abstract: A planographic printing member comprises a support provided with a hydrophilic layer which may be formed by application of a silicate solution in which particulate material is dispersed. The hydrophilic layer is treated with a modifying means which may comprise an acid, buffer formulation, colloidal suspension or a salt and especially comprises aluminium sulphate, in order to ensure that an image layer, provided over the hydrophilic layer, is able to change colour on exposure and be deleted using conventional means.

Description: PLANOGRAPHIC PRINTING This invention relates to planographic printing and provides a method of preparing a planographic printing member, for example a plate, and a planographic printing member per se. The invention particularly, although not exclusively, relates to lithographic printing. Lithographic processes involve establishing image (printing) and non-image (non-printing) areas on a substrate, substantially on a common plane. When such processes are used in printing industries, non-image areas are generally hydrophilic and image areas are generally oleophillic. Consequently, oil based inks are repelled from the non-image areas after water has been applied to the substrate. Image and non-image areas can be created by processes which include a step of exposing a layer of image material on the surface of the substrate to radiation. The exposure to radiation creates solubility differences in the image material corresponding to image and non-image areas. During development, the more soluble areas are removed, leaving a pattern on the substrate corresponding to the image. Preparation of the substrate for receiving a layer of the image material must ensure that the image material bonds to the substrate. However, it must allow release of the soluble image material during development. In addition, other problems need to be addressed when preparing a printing plate. For example, it is desirable for the image material to change colour when it is exposed. This is generally achieved by including a pH sensitive dye in the material of the image layer, the dye often being arranged to change colour by reaction with acid produced during a photochemical reaction of the light sensitive material of the image layer. However, it has been found that properties of the substrate itself can affect the ability of the dye to change colour. In addition, it is desirable for the dye not to stain the substrate to any significant degree since, otherwise, on development, such staining will be visible. This would be aesthetically unacceptable and, furthermore, would be commercially unacceptable since plate processing personnel would be unable to determine whether a plate had been fully developed. It is also desirable for it to be possible to remove unwanted image areas from a printing plate after exposure, for example to correct an error, in order to prevent such areas inking in and, therefore, being printed. The ability to remove selected areas will depend, to some extent, on the adhesive force between the substrate and the material of the image layer. It is an object of the present invention to address the above-described problems. According to a first aspect of the present invention, there is provided a method of preparing a planographic printing member comprising: a) forming a hydrophilic layer on a support by contacting the support with a fluid containing a particulate material; b) applying a modifying means over said hydrophilic layer for modifying interaction between said hydrophilic layer and a material subsequently applied; and c) providing an image layer over said hydrophilic layer, wherein an indicator means is associated with said image layer for indicating whether said image layer is in a first or a second state. Preferably, said planographic printing member is a printing plate. Preferably, said indicator means is adapted for visually indicating whether said image layer is in a first or second state. Preferably, said indicator means is arranged to undergo a chemical reaction, for example an acid-base or oxidation/reduction reaction, when said image layer changes from said first state to said second state. Preferably, said indicator means is adapted to indicate whether the image layer has been exposed. Preferably, said indicator means causes the printing member to display a different colour after exposure compared to the colour displayed before exposure. Said indicator means may comprise a photo-oxidative system, suitably using a free radical generator, for example triazine, arranged to oxidize an indicator material, for example a leucobase dye. Alternatively, said indicator means may comprise a photo-acid generator. Preferably, the image layer is adapted to have a different, for example a lower, pH after exposure compared to the pH before exposure. For example, the image layer may be adapted to produce H + (or other acidic species) upon exposure. Said indicator means is preferably pH sensitive. Said indicator means is preferably a pH indicator. Said indicator means is preferably incorporated in said image layer, for example by being dispersed therein. A suitable modifying means can be selected by comparing the effect of a proposed modifying means on said indicator means when said proposed modifying means has been applied, with the effect (if any) when said proposed modifying means has not been applied. When no modifying means is applied, the indicator means may be incapable of indicating between said first and second states of said image layer. Said modifying means is preferably applied at ambient temperature or above, more preferably in the range 20°C to 90°C, especially 20°C to 60°C. Preferably, said modifying means is arranged to lower the pH of at least the outermost surface of the hydrophilic layer, so that its pH after application of said modifying means is less than its pH before application. Preferably, the pH (before application) of the fluid used in step (a) is greater than the pH (before application) of the modifying means used in step (b) . The pH of the fluid may be greater than 9.0, preferably greater than 9.5 and, more preferably, greater than 10.0. The pH of the modifying means may be less than 10.0, preferably less than 9.0, more preferably less than 8.0. Especially preferred is the case wherein the pH is about 7 or below. In the most preferred embodiments, the pH is less than 5.0. The pH may be above 1, preferably above 2 and more preferably above 3. Some modifying means suitable for use in said method, for example sulphuric acid, affect whether a deletion means, for example a deletion fluid, in particular a deletion gel or pen, can be used to satisfactorily remove ink receptive areas of said image layer. Preferably, said modifying means is arranged such that a selected deletion means can be used to make areas of said printing member to which it is applied less ink receptive (and preferably substantially non-ink receptive) compared to when said modifying means consists essentially of 0. IM sulphuric acid. Said deletion means preferably includes a solvent, suitably an organic solvent, with n-methylpyrrolidone and cyclohexanone being especially preferred; an etchant material which may be acidic or alkaline but is preferably acidic, and is suitably selected from phosphoric acid, hydrogen fluoride and ammonium bifluoride; and other minor components, for example surface active agents, thickeners and the like. Preferably, said modifying means includes water as a solvent. Preferably, said modifying means comprises an aqueous solution or dispersion. Preferably, said modifying means includes one or more components selected from acids, buffer formulations, colloidal suspensions and salts. Preferred acids are protic acids and include phosphoric acid, sulphuric acid, hydrochloric acid, nitric acid, acetic acid, citric acid, sodium hydrogen carbonate and boric acid, with boric acid being especially preferred. Preferred buffer formulations include formulations including citric acid and/or a monohydrogen phosphate and/or a dihydrogen phosphate and/or boric acid in combination with, for example a strong acid and/or an alkali. Especially preferred buffer formulations include a phosphate. Preferred colloidal suspensions include insoluble oxides and/or hydroxides, preferably of Group III or IV elements, with silica and aluminium hydroxide being especially preferred. Cations of salts may be selected from group I, II and III, metals and transition metals, especially, first row transition metals. Preferred salts have cations selected from sodium, potassium, magnesium, calcium, aluminium, titanium, manganese, iron, copper and zinc. Anions of salts may be selected from sulphate, onohy dr oge nph o s ph a t e , dihydrogen phosphate, orthophosphate, polyvinylp osphonate, acetate, citrate, aluminate, chloride, propionate and nitrate. Preferred salts include aluminium sulphate, sodium dihydrogen phosphate, sodium sulphate, sodium citrate, calcium monohydrogenphosphate , aluminium nitrate, aluminium chloride, titanium III sulphate, iron III nitrate, iron III sulphate, iron II sulphate, iron III phosphate, copper II sulphate, copper nitrate, zinc II sulphate, zinc phosphate and manganese phosphate. Especially preferred salts include aluminium sulphate, aluminium nitrate, iron III nitrate, iron III sulphate, iron II sulphate, copper II sulphate, copper nitrate and zinc II sulphate. The most preferred salt is aluminium sulphate. Where said modifying means comprises a solution or dispersion, the concentration of the solute or dispersant may be at least 2wt% , suitably at least 3wt%, preferably at least 4wt% and more preferably, at least 5 wt%. The concentration of the solute or dispersant may be less than 50wt%, preferably less than 40wt% and, more preferably, less than 30wt%. Preferred modifying means are those which both modify interaction between said hydrophilic layer and an image layer and which are arranged such that a selected deletion means can be used to make areas of said printing member to which it is applied less ink receptive compared to when said restrictor means consists essentially of 0. IM sulphuric acid. Preferred modifying means are believed to form a deposit or precipitate over said hydrophilic layer which may act as a barrier to the passage of alkaline material from the hydrophilic layer to the image layer. Such a precipitate is preferably essentially insoluble in water. In some cases, the modifying means applied may be capable of chemically reacting with said hydrophilic layer to produce an insoluble precipitate. For example, when aluminium sulphate is used as said restriction means, insoluble aluminium hydroxide may be formed. In other cases, however, the modifying means may act by washing off material from the hydrophilic layer. Said restrictor means may be applied by any suitable means, for example by dipping, spraying or roller coating. Preferably, in the method, the first fluid to be contacted with said hydrophilic layer formed in step (a) has a pH which is less than the pH (before application) of the fluid used to form the hydrophilic layer. Preferably, the first fluid contacted with said hydrophilic layer is said modifying means. Said modifying means may be applied either before, or more preferably after, the hydrophilic layer is touch dry. Thus, preferably, there is no intermediate chemical treatment step between steps (a) and (b) described above. Preferably, said modifying means is applied in a single step. The surface to which said image layer is applied may have a pH of less than 8, preferably less than 7. The pH of said surface may be at least 2, preferably at least 3. The pH of said surface may suitably be measured using an aqueous indicator dye. Said particulate material may be an organic or an inorganic material. Organic particulate materials may be provided by latexes. Inorganic particulate materials may be selected from alumina, silica, silicon carbide, zinc sulphide, zirconia, barium sulphate, talcs, clays (e.g. kaolin), lithopone and titanium oxide. Said particulate material may comprise a first material which has a hardness of greater than 8 Modified Mohs (on a scale of 0 to 15) , preferably greater than 9 and, more preferably, greater than 10 Modified Mohs. Said first material may comprise generally spherical particles. Alternatively, said material may comprise flattened particles or platelets. Said first material may have a mean particle size of at least 0.1 μm and preferably at least 0.5 μm. Said first material may have a mean particle size of less than 45 μm, preferably less than 20 μm, more preferably less than 10 μm. The particle size distribution for 95% of particles of the first material may be in the range 0.01 to 150 μm, preferably in the range 0.05 to 75 μm, more preferably in the range 0.05 to 30 μm. Said first material preferably comprises an inorganic material. Said first material preferably comprises alumina which term includes A1 2 0 3 and hydrates thereof, for example A1 2 0 3 .3H 2 0. Preferably, said material is A1 2 0 3 . Said particulate material in said fluid may include at least 20wt%, preferably at least 30wt% and, more preferably, at least 40wt% of said first material. Said fluid may include 5 to 40wt%, preferably 5 to 30wt%, more preferably 7 to 25wt%, especially 10 to 20 wt% of said first material. Said particulate material may comprise a second material. Said second material may have a mean particle size of at least 0.001 μm, preferably at least 0.01 μm. Said second material may have a mean particle size of less than 10 μm, preferably less than 5 μm and, more preferably, less than 1 μm. Mean particle sizes of said first and second materials suitably refer to the primary particle sizes of said materials. Said particulate material in said fluid may include at least 20wt%, preferably at least 30wt% and, more preferably, at least 40wt% of said second material. Said liquid may include 5 to 40wt%, preferably 5 to 30wt%, more preferably 7 to 25wt%, especially 10 to 20 wt% of said second material. Said second material is preferably a pigment. Said second material is preferably inorganic. Said second material is preferably titanium dioxide. Said first and second materials preferably define a multimodal, for example a bimodal particle size distribution. Said particulate material may include a third material which is preferably adapted to lower the pH of the silicate solution. Said third material may be a colloid, suitably colloidal silica or an inorganic salt, suitably a phosphate, with aluminium phosphate being preferred. Where a third material is provided, preferably less than 30wt% more preferably less than 20wt%, especially less than 10wt% of said particulate material is comprised by said third material. Said fluid applied in step (a) may comprise a silicate solution in which said particulate material is dispersed. Said silicate solution may comprise a solution of any soluble silicate including compounds often referred to as water glasses, metasil icates , orthosi 1 icates and sesquisilicates. Said silicate solution may comprise a solution of a modified silicate for example a borosilicate or phosphosilicate. Said silicate solution may comprise one or more, preferably only one, metal or non-metal silicate. A metal silicate may be an alkali metal silicate. A non-metal silicate may be quaternary ammonium silicate. Said silicate solution may be formed from silicate wherein the ratio of the number of moles of Si species, for example Si0 2 , to the number of moles of cationic, for example metal species is in the range 0.25 to 10, preferably in the range 0.25 to about 6, more preferably in the range 0.5 to 4. Said silicate is preferably alkali metal silicate. In this case, the ratio of the number of moles of Si0 2 to the number of moles of M 2 0 in said silicate, where M represents an alkali metal may be at least 0.25, suitably at least 0.5, preferably at least 1, more preferably at least 1.5. Especially preferred is the case wherein said ratio is at least 2.5. Said ratio may be less than 10, suitably less than 6, preferably less than 5 and more preferably less than 4. Preferred alkali metal silicates include lithium, sodium and potassium silicates, with lithium and/or sodium silicate being especially preferred. A silicate solution comprising only sodium silicate is most preferred. Said fluid is suitably non-gaseous. Said fluid may comprise 2 to 30wt% of silicate (e.g. dissolved sodium silicate solid) , preferably 5 to 20wt%, more preferably 8 to 16wt% . The fluid may be prepared using 10 to 60wt%, preferably 30 to 50wt%, more preferably 35 to 45wt% of a silicate solution which comprises 30 to 40wt% silicate. Said fluid may include 5 to 60wt% of particulate material. Preferably, the fluid includes 10 to 50wt%, more preferably 15 to 45wt%, especially 20 to 40 wt% of particulate material. The ratio of the weight of silicate to the weight of particulate material in the fluid is preferably in the range 0.1 to 2 and, more preferably, in the range 0.1 to 1. Especially preferred is the case wherein the ratio is in the range 0.2 to 0.6. Said liquid may include more than 20 wt% , preferably more than 30 wt%, more preferably more than 40 wt%, especially more than 45 wt% water (including water included in said silicate solution) . Said liquid may include less than 80 wt% , preferably less than 70 wt%, more preferably less than 65 wt%, especially less than about 60 wt% water. Where the fluid comprises a silicate and said particulate material comprises a first material and a second material as described, the ratio of the wt% of silicate (e.g. dissolved sodium silicate solid) to the wt% of said first material may be in the range 0.25 to 4, preferably in the range 0.5 to 1.5 and more preferably about 1. Similarly, the ratio of the wt% of silicate to the wt% of said second material may be in the range 0.25 to 4, preferably in the range 0.5 to 1.5 and more preferably about 1. The ratio of the wt% of first material to the wt% of second material may be in the range 0.5 to 2, preferably in the range 0.75 to 1.5, more preferably about 1 to 1. The pH of said fluid may be greater than 9.0, is preferably greater than 9.5 and, more preferably, greater than 10.0. Especially preferred is the case wherein the pH is greater than 10.5. The pH is suitably controlled so that the silicate remains in solution and does not form a gel. A gel is generally formed when the pH of a silicate solution falls below pH9. The pH of said fluid is preferably less than 14, more preferably less than 13. It is understood that the pH of the fluid affects the adhesion of the hydrophilic layer on the support. It is found that the use of a fluid having a pH as described can lead to a good adhesion. The fluid may include other compounds for adjusting its properties. For example, the fluid may include one or more surfactants. Said fluid may include 0 to lwt% of surfactant (s) . A suitable class of surfactants comprises anionic sulphates or sulphonates. The fluid may include viscosity builders for adjusting the viscosity of the fluid. Said fluid may include 0 to 10wt%, preferably 0 to 5wt% of viscosity builder(s). Also, the fluid may include dispersants for dispersing the inorganic particulate material throughout the fluid. Said fluid may include 0 to 2wt% of dispersant (s) . A suitable dispersant may be sodium hexametaphosphate. Hydrophilic layers of planographic printing plates have been proposed which include organic polymers, for example thermoplastic polymers, for increasing the strength and/or hardness of the hydrophilic layers. Said liquid used in the method of the present invention preferably does not include a thermoplastic organic polymeric material, for example polyvinylidene fluoride or the like. Said fluid may have a viscosity of less than 100 centipoise when measured at 20°C and a shear rate of 200s "1 using a Mettler Rheomat 180 Viscometer incorporating a double gap measuring geometry. Preferably, said viscosity is less than 50 centipoise, more preferably less than 30 centipoise when measured as aforesaid. Especially preferred is the case wherein the viscosity is less than 20 centipoise. Said fluid may be applied to said support by any suitable means which is preferably non-electrochemical. Said fluid may be applied to both sides of said support in order to form a hydrophilic layer on both sides. A support with such a layer on both sides may be used to prepare a double-sided lithographic plate. Alternatively, if such a support is used for a single- sided plate, the side of the plate which does not carry an image layer may be protected by the hydrophilic layer. Said fluid is preferably applied to only one surface of said support. Said fluid may be applied to said support to form a hydrophilic layer having an average thickness after drying, of less than 20 μm, preferably less than 10 μm and, more preferably, less than 5 μm. Especially preferred is the case wherein the average thickness is less than 3 μm. The thickness of the hydrophilic layer may be greater than 0.1 μm, preferably greater than 0.3 μm and, more preferably, greater than 0.5μm. Said hydrophilic layer may include 1 to 20 g of material per metre squared of substrate. Preferably said layer includes 5 to 15 g, more preferably 8 to 12 g, of material per metre squared of substrate. Most preferably, said layer includes about 10 g of material per metre squared. Said particulate material preferably defines formations in said hydrophilic layer which render said layer non-planar and which are arranged such that, when an image layer is applied over said hydrophilic layer, corresponding formations are defined on the surface of the image layer in a manner similar to that described in U.K. Patent Application No. GB 2 277 282, the contents of which are incorporated herein by reference. The method preferably includes the steps of providing suitable conditions for the removal of water from the fluid after it has been applied to the support in step (a) . Suitable conditions may involve passive or active removal of water and may comprise causing an air flow over the support and/or adjusting the humidity of air surrounding the support. Preferably, the method includes the step of arranging the support in a heated environment. The support may be placed in an environment so that its temperature does not exceed 230°C, preferably does not exceed 200°C and, more preferably, does not exceed 175°C. Especially preferred is the case wherein the support temperature does not exceed 150°C. The support may be arranged in the heated environment for less than 180 seconds, preferably less than 120 seconds and, more preferably, less than 100 seconds. The support may comprise aluminium or an alloy. In this event, it is found to be advantageous to arrange the support in an environment wherein the temperature is less than 230°C as described above since, at this temperature, annealing of the support is not significant and, therefore, the tensile strength of the support is maintained at an acceptable level. More particularly, the tensile strength of the aluminium, suitably measured using a Hounsfield tensile testing machine, may be at least 100 MPa, preferably at least 110 MPa and, more preferably, at least 120 MPa. Especially preferred is the case wherein the tensile strength is at least 140 MPa. The fluid described above may also be advantageously applied to a plastics support, for example a polyester, in order to provide a hydrophilic layer thereon, in view of the fact that the fluid needs only to be cured at a relatively low temperature for a short time. As will be appreciated, curing at a relatively high temperature for long periods might otherwise detrimentally affect the properties of the plastics material. The removal of water from the fluid applied to the support is believed to cause the silicate to polymerise and bind the inorganic particulate material in position. Thus, it should be appreciated that one advantage of the method of the present invention may be that a relatively wide range of support materials may be used. For example, where the support material is aluminium or an alloy, a relatively low grade metal could be used compared to the grade of metal usually used for lithographic plates. Additionally and/or alternatively, a metal which is more resistant to, for example developer chemicals, could be used. Furthermore, the method may be used to apply a hydrophilic layer to other types of support materials, for example other metals, foil coated paper and plastics. A support material may be pretreated prior to the application of said hydrophilic layer. Where the support material is aluminium or an aluminium alloy, it may be pretreated by one or more conventional methods used in the surface treatment of aluminium, for example caustic etch cleaning, acid cleaning, brush graining, mechanical graining, slurry graining, sand blasting, abrasive cleaning, electrocleaning, solvent degreasing, ultrasonic cleaning, alkali non-etch cleaning, primer coating, grit/shot blasting and electrograining. Details of such methods are provided in: "The surface treatment and finishing of aluminium and its alloys" S. Wernick, R. Pinner and P. G. Sheasby published by Finishing Publication Ltd., ASM International, 5th edition 1987. Where the support material is pretreated, preferred pretreatments are those which involve adjusting the character of the surface of the support material, for example those involving cleaning, graining or the like. If a surface coating is, however, applied on the surface of the support material, the coating is preferably applied as a liquid. Preferably, said liquid comprising a silicate solution as described above is applied to a substantially dry surface on said support. Preferably, said fluid is applied directly onto said support material of said support. Preferably, the support material is cleaned and/or etched prior to being contacted with said fluid. Cleaning and/or etching may be achieved using an alkaline liquid, for example sodium hydroxide, optionally with additives such as sodium gluconate and/or sorbitol. The support material may also be subjected to a desmutting treatment, suitably using nitric acid. After this treatment, the support material should be rinsed and/or dried prior to being contacted with said liquid. The term "image layer" includes a layer that can subsequently be partially removed in order to define areas to be printed and includes a layer which already defines areas to be printed. The image layer may be provided over substantially the entire surface of said hydrophilic layer. It may comprise any known photosensitive material whether arranged to form a positive or negative plate. Examples of photosensitive materials include diazonium/diazide materials, polymers which undergo depolymerisation or addition photopolymerisation and silver halide gelatin assemblies. Examples of suitable materials are disclosed in GB 1 592 281, GB 2 031 442, GB 2 069 164, GB 2 080 964, GB 2 109 573, EP 0 377 589, US 4 268 609 and US 4 567 131. Preferably, the light sensitive material is a quinone diazide material. Alternatively, said image layer in the form of a desired image for use in planographic printing may be deposited over said hydrophilic layer by a deposition process such as ink jet or laser ablation transfer. An example of the latter is described in US 5 171 650. Said image layer is preferably arranged over said hydrophilic layer so that formations are defined on the surface of the layer due to formations formed in said hydrophilic layer by particulate material therein. The formations may suitably be arranged to define channels between the light-sensitive layer and a mask so that air can escape from between the layer and the mask in order to decrease the draw-down time of the mask on the layer prior to exposure of the printing plate. The invention extends to a method of preparing a planographic printing member comprising: a) forming a hydrophilic layer on a support by contacting the support with a fluid containing a particulate material; b) applying a modifying means over said hydrophilic layer; c) providing an image layer over said hydrophilic layer; wherein said modifying means is arranged such that a selected deletion means can be used to make areas of said printing member to which it is applied less ink receptive compared to when said restrictor means consists essentially of 0.1 M sulphuric acid. The invention extends to a printing member when prepared using a method described herein. The invention extends to a printing member precursor prepared following steps (a) and (b) of any method described herein. Any feature of any aspect of any invention or embodiment described herein may be combined with any feature of any other aspect of any invention or embodiment described herein. Example 1 Genera l procedure f or the prepa rat i on o f a lithographic printing plate . Step 1 Preparation of Aluminium A 0.3 mm gauge aluminium alloy sheet of designation AA1050 was cut to a size of 230 mm by 350 mm, with the grain running lengthways. The sheet was then immersed face up in a solution of sodium hydroxide dissolved in distilled water (lOOg/l) at ambient temperature for 60 seconds and thoroughly rinsed with water. Step 2 Preparation of coating formulation The following reagents are used in the preparation: - Sodium silicate solution having a ratio Si0 2 : Na 2 0 in the range 3.17 to 3.45 (average about 3.3); a composition of 27.1 - 28.1wt% Si0 2 , 8.4 - 8.8wt% Na 2 0, with the balance being water; and a density of about 75 Twaddel (°Tw) , equivalent to 39.5 Baume (°Be) and a specific gravity of 1.375. - Deionised water having a resistivity of 5 Mohm.cm - A1 2 0 3 powder comprising alumina (99.6%) in the shape of hexagonal platelets. The mean particle size is 3 μm. The powder has a hardness of 9 Moh (on a 0 - 10 hardness scale) . - Anatase titanium dioxide having a mean primary particle size of 0.2 μm. Deionised water (150g; 40 wt%) was added to a 250ml beaker and sheared using a Silverson high shear mixer. Titanium dioxide powder (53.29g; 14.21 wt%) was then added in portions over a period of four minutes with the shearing continuing. Then, alumina powder (53.29g; 14.21wt%) was added in portions over a period of four minutes with the shearing continuing. On completion of the addition, sodium silicate solution (118.43g; 31.58 wt%) was added with shearing for a further three minutes. The viscosity of the liquid was found to be about 10 centipoise when measured at 20°C and a shear rate of 200s "1 using a Mettler Rheomat 180 Viscometer incorporating a double gap measuring geometry. Step 3 Application of coating formulation The coating formulation prepared in Step 2 was applied onto the aluminium sheet prepared in Step 1 using a rotating Meyer bar coater (designation K303) to give a 12 μm wet film thickness. Step 4 Post Application Treatments The coated sheets prepared in Step 3 were subjected to various treatments as described in the following Examples. Step 5 Application of light sensitive coating A printing plate was produced from a sheet prepared in Step 4 by coating, using a Meyer bar, a quinone diazide/novolak resin light sensitive material which included a photo-acid generator and Victoria blue which is adapted to change colour as a result of the release of acid during exposure. The light sensitive material was dried at 130°C for 80 seconds. In the Examples, the following Trade Marks are used: Ludox CL - refers to silica obtained from Dupont. Bacosol 3C - refers to aluminium hydroxide obtained from Alcan. Examples 2 to 5 The general procedure of Example 1 was followed. However, after application of the coating formulation in Example 1, Step 3, the plate was fan dried and then the treatments described in Table 1 below were carried out. TABLE 1 After the treatments, the plates were rinsed with water and oven dried at 130°C for 80 seconds. Examples 6 to 25 The general procedure of Example 1 was followed. Coated sheets prepared in Example 1, Step 3 were placed in an oven at 130°C for 80 seconds. The sheets were removed and allowed to cool to ambient temperature. Subsequently the treatments described in Table 2 below were carried out (at ambient temperature, unless otherwise stated) . After the treatments described the sheets were fan dried. TABLE 2 EXAMPLE 2 6 A statistical experimental design was conducted using a substrate prepared generally as described in Example 1, followed by immersion in aluminium sulphate solutions at various concentrations (1.0wt%, 5.5wt%, 10wt%), temperatures (20°C, 40°C and 60°C) , immersion times (15, 37.5 and 60 seconds) and hydrophilic coating weight (4, 8 and 15 g/m 2 ) in order to determine how these parameters affect the properties of the substrate and/or the final plate prepared. EXAMPLE 27 Application of light sensitive coating The products of Examples 2 to 26 were used to produce printing plates by coating, using a Meyer bar, a light sensitive material comprising a napthoqu inone diazide/novolak resin, a photoacid generator and Victoria blue which is adapted to change colour as a result of the release of acid during exposure. The light sensitive material was dried at 130°C for 80 seconds. EXAMPLE 28 Exposure The printing plates produced as described in Example 27 were exposed in the normal manner using a Montakop 65 light frame. EXAMPLE 29 Development The exposed plates of Example 28 were developed using a standard positive developer at 20°C by hand flooding for 10 seconds followed by a further 50 seconds treatment using a hand pad. EXAMPLE 30 Post Development Finisher was applied to the plates of Example 29 using a sponge. EXAMPLE 31 Deletion A positive deletion gel containing cyclohexanone, n- methylpyrrolidone, phosphoric acid, silica and surfactants was applied to an image area of each plate of Example 30 until the image area appeared to have been removed. EXAMPLE 32 Inking-in The plates of Example 31 were inked in using standard inking solution using damp cotton wool. EXAMPLE 33 Procedures for assessment of performance Plates prepared as described above were assessed using the following procedures: i) Colour Change The light sensitive material applied as described in Example 27 is arranged to change colour when exposed as described in Example 28 in order to indicate that the plate has been exposed. Thus, after exposure, the plates were assessed visually to determine whether the colour change had taken place. ii) Image Deletion After inking-in, as described in Example 32, the plates were assessed visually to determine whether the image areas of the plates, to which deletion gel had been applied in Example 31, accepted ink or not. It will be appreciated that the areas should not accept ink. iii) Dyestain After deletion as described in Example 31, the plates were assessed visually to determine whether any of the Victoria blue dye included in the light sensitive coating had stained the plate in areas where the coating had been removed . Results Each of the plates prepared as described in Examples 2 to 25 was found to give a colour change upon exposure (when assessed as described in Example 33 (i)); to give image deletion on application of a deletion gel (when assessed as described in Example 33 (ii)); and had low/negligible dyestain (when assessed as described in Example 33 (iii) ) . From the plates prepared in Example 26, it was observed that as the weight of the coating formulations is increased the temperature of the aluminium sulphate dip and/or residence time of plates in the dipping tank needs to be increased to obtain a satisfactory colour change as described in Example 34 (i). The reader's attention is directed to all papers and documents which are filed concurrently with or previous to this specification in connection with this application and which are open to public inspection with this specification, and the contents of all such papers and documents are incorporated herein by reference. All of the features disclosed in this specification (including any accompanying claims, abstract and drawings) , and/or all of the steps of any method or process so disclosed, may be combined in any combination, except combinations where at least some of such features and/or steps are mutually exclusive. Each feature disclosed in this specification (including any accompanying claims, abstract and drawings) , may be replaced by alternative features serving the same, equivalent or similar purpose, unless expressly stated otherwise. Thus, unless expressly stated otherwise, each feature disclosed is one example only of a generic series of equivalent or similar features. The invention is not restricted to the details of the foregoing embodiment (s) . The invention extends to any novel one, or any novel combination, of the features disclosed in this specification (including any accompanying claims, abstract and drawings) , or to any novel one, or any novel combination, of the steps of any method or process so disclosed.

Claims: CLAIMS 1. A method of preparing a planographic printing member comprising: a) forming a hydrophilic layer on a support by contacting the support with a fluid containing a particulate material; b) applying a modifying means over said hydrophilic layer for modifying interaction between said hydrophilic layer and a material subsequently applied; and c) providing an image layer over said hydrophilic layer, wherein an indicator means is associated with said image layer for indicating whether said image layer is in a first or a second state. 2. A method according to Claim 1, wherein said indicator means is adapted for visually indicating whether said image layer is in a first or second state. 3. A method according to Claim 1 or Claim 2, wherein said image layer is adapted to have a different pH after exposure compared to the pH before exposure. 4. A method according to any preceding claim, wherein said indicator means is incorporated in said image layer. 5. A method according to any preceding claim, wherein said modifying means is arranged to lower the pH of at least the outermost surface of the hydrophilic layer, so that its pH after application of said modifying means is less than its pH before application. 6. A method according to any preceding claim, wherein the pH (before application) of the fluid used in step (a) is greater than the pH (before application) of the modifying means used in step (b) . 7. A method according to any preceding claim, wherein the pH of the fluid used in step (a) is greater than 9. 8. A method according to any preceding claim, wherein the pH of the modifying means is less than 10. 9. A method according to any preceding claim, wherein said modifying means is arranged such that a selected deletion means can be used to make areas of said printing member to which it is applied less ink receptive (and preferably substantially non-ink receptive) compared to when said modifying means consists essentially of 0.1 M sulphuric acid. 10. A method according to any preceding claim, wherein said modifying means includes water as a solvent. 11. A method according to any preceding claim, wherein said modifying means comprises an aqueous solution or dispersion. 12. A method according to any preceding claim, wherein said modifying means includes one or more components selected from acids, buffer formulations, colloidal suspensions and salts. 13. A method according to Claim 12, wherein a said salt is aluminium sulphate. 14. A method according to any preceding claim, wherein said modifying means is arranged to modify interaction between said hydrophilic layer and an image layer and arranged such that a selected deletion means can be used to make areas of said printing member to which it is applied less ink receptive compared to when said restrictor means consists essentially of 0.1 M sulphuric acid. 15. A method according to any preceding claim, wherein the first fluid to be contacted with said hydrophilic layer formed in step (a) has a pH which is less than the pH (before application) of the fluid used to form said hydrophilic layer. 16. A method according to any preceding claim, wherein the first fluid contacted with said hydrophilic layer is said modifying means. 17. A method according to any preceding claim, wherein said fluid applied in step (a) comprises a silicate solution in which said particulate material is dispersed. 18. A method of preparing a planographic printing member comprising: a) forming a hydrophilic layer on a support by contacting the support with a fluid containing a particulate material; b) applying a modifying means over said hydrophilic layer; c) providing an image layer over said hydrophilic layer; wherein said modifying means is arranged such that a selected deletion means can be used to make areas of said printing member to which it is applied less ink receptive compared to when said restrictor means consists essentially of 0.1 M sulphuric acid. 19. A printing member when prepared using a method according to any of Claims 1 to 18. 20. A printing member precursor prepared following steps (a) and (b) of a method according to any of Claims 1 to 18.

Inventors: JOLLIFFE BARRY, JOLLIFFE, BARRY
Applicants: HORSELL GRAPHIC IND LTD, JOLLIFFE BARRY, HORSELL GRAPHIC INDUSTRIES LIMITED, JOLLIFFE, BARRY
Application year: 1997
Main classification: G03F7
IPC codes: B41N3, G03F7