Ceramic matrix composites

Abstract: Ceramic matrix composites (CMC) of high density, preferably of the SiC/SiC type, are provided by a production process based on the infiltration of ceramic fibre cloths with a polymeric precursor solution containing, as fillers, inert powders having size much lower than the mean distance among the ceramic fibres which are used as basic material for the manufacturing of CMC, typically a nanometric granulometry. Such step is followed by the steps of hardening the cloths, pyrolysis of the polymer and repeated thickenings until the desired density is reached. A possible preliminary step consists of a brief (≤ 24 hours) treatment of infiltration of SiC from the vapor phase (CVI) with precursors and typical operative parameters for the deposition of silicon carbide.

Description: The present invention relates to the production of a ceramic matrix composite (CMC) reinforced by fibres of the ceramic type. As known, CMCs are a class of technologically advanced materials which have been increasingly developed in recent years for industrial applications in leading sectors such as aerospace, energy, and automobile industry due to their very high mechanical strength, chemical inertness and heat resistance along with their further feature of lightness. In addition, studies for the application of such materials in the construction of the future controlled thermonuclear fusion reactors are being conducted in USA, Japan and Europe. The basic mechanical characteristic of CMCs is the capability of breaking under loaded conditions in a not catastrophic manner unlike the monolithic ceramic materials of fragile nature for which the design of structural components is very difficult. The reason of such an advantageous mechanical behaviour of CMCs is the deflection of the cracks caused in the ceramic matrix by a thermal or mechanical stress to the direction of the fibre-matrix interphase. As far as the basic materials are concerned, several types of ceramic matrices and ceramic fibres may be used for the production of CMCs. However, one preferred CMC is certainly the SiC/SiC fibre which is currently used in space and military fields, particularly in France, for the construction of parts of Arianne missile and Rafale aircraft produced by SEP Company. A particular process, so-called CVI (Chemical Vapor Infiltration), is nowadays known and already used on an industrial scale by the above-mentioned SEP Company for the construction of CMCs. CVI process well-known to those skilled in the art is based on the inlet of gas precursors of SiC (e.g. methyl-trichlorsilane) into high-temperature furnaces containing ceramic fibre materials preformed in the desired shape. The gases decompose in the furnace forming in the ceramic fibre materials the ceramic matrix which is formed of silicon carbide (SiC) in case of SiC/SiC fibre CMC. The decomposition of the gases should be carried out slowly according to a determined kinetics allowing a complete infiltration, preferably from the inside of the material, which then requires a very long time in the order of several months for the construction of 5-6 mm thick pieces. Products having mechanical characteristics fully satisfying the specification required for their use are provided by such a process. However, the process suffers from not negligible troubles, particularly as far as the production cost is concerned which is very high above all because of the very long production time. For these reasons it is almost impossible to manufacture thick pieces which would be necessary, for example, for the construction of large plants such as the future controlled thermonuclear fusion magnetic-confinement reactors as well as other some centimeter thick components. In order to overcome such problems, researches aiming at the set-up of alternative CMC production methods which are more effective and suitable for the construction of large-size components are being conducted in the most advanced countries such as France, Germany, USA and Japan. Among such alternative methods, even if not yet used on industrial scale, one process is being studied which is based upon the infiltration of preformed fibre materials with not gaseous but liquid ceramic polymeric precursors at the melted state or in solution. In such a process, the precursor changes into the ceramic matrix by a thermal pyrolysis treatment, bounding the fibres and having an amorphous or nanocrystalline structure according to the pyrolysis temperature by a thermal pyrolysis treatment. One problem of such a process appears during the pyrolysis in which a considerable loss of weight of the precursor (25-40%) takes place because of evaporation of oligomers and structural rearranging with evolution of gases such as methane, other hydrocarbons and hydrogen. At the same time the transformation of a polymeric material having a typical density of about 1 g/cm 3 into a ceramic material of higher density (2,5-2,7 g/cm 3 in case of SiC precursors) implies a strong bulk contraction with production of high porosity in the matrix being formed. In order to overcome such a problem, one known solution is to repeat several times the infiltration and pyrolysis processes for reducing the porosity and hardening the matrix. Unfortunately, almost 8-10 cycles are necessary to thicken the matrix to a satisfying degree, a real waste of time. A second solution is to use, along with the preceramic polymer, inert "fillers" such as powders of SiC which do not undergo bulk contraction during the thermal treatment and are compatible with the material of the matrix. Such powders are resorted to because they allow the voids in the fibre materials and among the material layers to be better filled so as to reduce the total number of the necessary infiltration and pyrolysis cycles in the whole process. The currently used inert fillers are commercially available SiC powders of micrometric granulometry. Such powders suffer, however, from further problems among which the not homogeneous distribution of the same as the powder particles hardly enter the fibre bundles (typically formed of 500-1000 fibres of 5-15 µm diameter), the gaps among the fibres being by two orders of magnitude narrower than the size of the fibres. Moreover, the amorphous or nanocrystalline nature of the matrix produced by the pyrolysis of preceramic polymers can be affected by the presence of crystalline particles having much larger size, thus impairing the mechanical characteristics. As can be seen from the foregoing, a CMC having improved mechanical characteristics, particularly as far as density and homogeneity of the matrix is concerned, is still expected. It is also important for the industry that such a material can be produced with industrially interesting time and cost as well as with large enough thickness so as to be used, for instance, as structural component in large plants. One object of the present invention is to overcome the problems of the known CMCs and processes for the production thereof. Such object is achieved according to the invention by manufacturing CMCs of high density, preferably of the SiC/SiC type, by a production process based on the infiltration into ceramic fibre materials of a polymeric precursor solution containing, as filler, inert powders of much lower size than the mean distance among the ceramic fibres used as basic materials for the manufacturing of CMCs and typically having a nanometric granulometry. Such infiltration step is followed by the steps of material hardening and polymer pyrolysis, and by repeated thickening steps until the desired density is reached. Advantageously, it was found that the use of such powders as fillers in the CMC production process does not have the problems of the known powders as the reduced granulometry allows also the gaps between the single fibres to be filled in a generally homogeneous manner. A second advantage is that the amorphous or nanocrystalline structure of the preceramic polymer matrix is not substantially affected by the presence of particles still of nanometric size after the pyrolysis. A third advantage is that such nanometric powders homogeneously dispersed into an initially amorphous matrix can act as crystalization nucleus for the same matrix starting the crystalization at such a temperature as not to impair the microstructure, the chemical development, and the mechanical characteristics of the fibres. A further advantage is that the use of nanometric powders as inert fillers lends itself particularly to technologies such as prepreg or preimpregnation of the single fibre cloths followed by the hardening of the piles of them, or techniques like resin transfer moulding (RTM), on already piled up material layers. However, the advantages of using nanometric powders are even more apparent if the technique of liquid infiltration and pyrolysis is applied to tridimensional preformed fibre materials to which only particles of extremely reduced size can be uniformly fed, for example, by colloidal filtration of diluted suspensions. According to a further feature, the production process according to the invention can also provide, in addition to fillers with nanometric granulometry, a preliminary step consisting of a brief treatment (up to 24 hours) of precursor infiltration into SiC from the vapor phase (CVI) with the typical operative parameters for the deposition of silicon carbide. Such a treatment seeks to give to a bidimensional assembly of overlapped fibre materials a rigid tridimensional structure which is fully open, also through the gaps between fibres, to the infiltration of liquid agents containing nanometric powders used in the following repeated thickening steps described in detail thereafter. These and further advantages of the invention will be more readily understood by anyone skilled in the art from the following description with reference to the accompanying, not limiting, exemplificative drawings and tables. In the drawings: Fig. 1 is a typical load/deformation diagram of the material prepared according to the present invention; Fig. 2 is a load/deformation diagram of a typical commercial material prepared by CVI; Fig. 3 shows the typical microstructure of the material prepared according to the invention by using nanometric powders (800X). The process for the production of ceramic matrix composites (CMC) according to the invention consists of the following steps which in the described example relate to a preferred embodiment for the production of flat panels of SiC/SiC fibres. As can be seen and for a better understanding of the claimed results the following description also exemplifies the differences in the characteristics of the materials which can be obtained according to the invention by liquid infiltration/pyrolysis without using nanometric powders, by using increasing amounts of such powders according to the described process, and by both using nanometric powders and carrying out a short preliminary infiltration from the described vapor phase (CVI). In the shown example, the used polymeric SiC precursor is polycarbosilane (Nippon Carbide, Japan). Polycarbosilane (PCS) is a general term indicating a class of organic silicon polymers which produce a ceramic SiC residue as a result of a pyrolysis treatment at a temperature T > 800°C under controlled atmosphere. SiC fibres are of the type commercially known as Nicalon (Nippon Carbide, Japan) which are carbon coated, i.e. have a surface deposit of pyrolytic carbon of a typical thickness of 0,1-1 µm and a diameter approximately of 15 µm. The process according to the invention for the production of ceramic matrix composites (CMC) having improved capability of being deformed essentially consists of the following 4 steps as set out in claim 1. Alternately, steps I, II, and III can be replaced by a first step IB of stiffening a pile of overlapped materials (the number of which is proportional to the thickness and the desired proportion of fibres in the final composite) by a brief (up to 24 hours) treatment of chemical infiltration of silicon carbide from the vapor phase with the typical operative parameters of such technology. Step IV: repeated thickenings until the density of the panels is believed satisfactory. In detail: in step I, the powdered polycarbosilane (PCS) is solubilized in hydrocarbons, for example, toluene having a concentration of 50-70% by weight. In case of infiltration of SiC nanometric powder, the latter is dispersed in advance into the same solvent with a concentration of 10% by weight by means of devices with very strong shearing action, e.g. attritors. In order to facilitate the dispersion and lower the viscosity of the solution it is advantageous to subject the nanometric powder to a surface treatment with sterically acting dispersants, e.g. higher linear alcohols such as octanol or dodecanol or others in a quantity of 1-2% related to the powder. By homogeneously mixing the two preparations described above a resin is obtained in which the PCS-SiC powders ratio is defined by the concentrations and the utilized amounts of solution and dispersion. Particularly in the exemplificative production of the following shielding panels of SiC/SiC fibre material, the ratio between the two components is: PANELS PCS/SiC POWDERS CMC 0 10:0 CMC 20 8:2 CMC 30 7:3 CMC 40 6:4 For the preimpregnation of the single clothes of materials a number of well known methods may be employed without substantial differences such as manual dipping of the clothes into the solution/dispersion, spreading of the latter by brush or knife, or automated methods such as tape casting. In such step it is not requested to ensure an absolutely homogeneous distribution of the mixture as such a mixture is homogeneously distributed in the following hardening step; it is instead necessary to check the total amount of impregnating agent so as to be sufficient to fill all of the voids among the fibres, which are a function of the characteristics of the fibres, the texture thereof, and the desired fibre bulk fraction in the final composite. By way of example, by using Nicalon fibres having a mass per unit surface of 220 g/cm 3 it is necessary to use about 60 g of a PCS/nanometric powders mixture (the latter being 30% by weight) every 100 g of fibres so as to provide a final product having a fibre bulk fraction between 35 and 40%. In cloth hardening step II, after the evaporation of the solvent, the clothes infiltrated in advance are piled up in a number proportional to the final thickness of the panel being prepared (e.g. 4 layers for one millimeter thickness) so that the fibres are oriented to 0 and 90°. At this point the hardening is carried out, for example, in a bag which can be deformed under vacuum. After evacuation of the tight bag containing the panel, the latter is gradually heated till about 300°C under a press exerting a light coupling pressure; thereafter a pressure of 10/40 kg/cm 2 is applied and the whole panel is kept in such a state for 10 minutes, then cooled under pressure. Under such conditions the melted thermoplastic resin is homogeneously distributed so as to fill any macro-and microcavity in the material and to size the layers to one another. In pyrolysis step III, the panels prepared as described above are filled into a furnace so that the flow of an inert gas (in this case argon) which is passed trough the furnace can lap the surfaces of the panels. In addition, in order to avoid deformation (particularly during the first cycle of pyrolysis) it is convenient to support the panel as the still partially thermoplastic resin does not provide a sufficient rigidity to the assembled clothes. The pyrolysis is carried out at 1100°C with a thermal cycle of about 36 hours as a whole according to a heating program providing a gradient of 8-10°C/hour in the temperature range (300-650°C) which is most critical for the process. In the following thickening step IV, after the first pyrolysis, a product stiffening effect is provided by filling the voids left during the pyrolysis by the decomposition of the polymer and the following bulk contraction of the latter during the transformation to the ceramic phase, i.e. SiC in the described case. This is achieved by the alternation of polymer infiltration and pyrolysis. Thus the density of the manufactured composite matrix material is increased. A mixture of 50-70% by weight of PCS in toluene is used for the thickening. The reinfiltration operations during the repeated steps of thickening can be advantageously carried out with quite similar results by known technologies of the state of art such as the resin transfer moulding (RTM) or by using a surge tank with due caution of emptying the die for RTM before injecting the resin solution or the surge tank before dipping the composite into the solution. In both cases the resin solution is pressurized directly in RTM, indirectly through gas overpressure in the surge tank. In any case, because of the wettability and the low viscosity of the solution, the pressure requested for the complete infiltration through the open pores of the material is limited to some bars (2-8) and preferably increases in such range as the repeated thickenings succeed one another so that the number and above all the size of the residual pores of the material tend to decrease. After controlled evaporation of the solvent at a temperature much lower than the boiling point of the solvent (not greater than 50-60°C under atmospheric pressure) a pyrolysis treatment quite similar to that already described is carried out. In case the above mentioned step IB of stiffening a pile of fibre cloths by a brief treatment of infiltration of SiC from the vapor phase is employed as an alternative to steps I, II, and III, the repeated thickenings are still carried out by the methods described above with the only difference that it is advantageously used, as infiltration agent for the first thickening, the PCS solution also containing filling nanometric powders, in this case, with a concentration not greater than 30% by weight related to PCS. In the following table there are shown the most significant characteristics of the panels prepared without using filling nanometric powders, by using the same in increasing amounts, and by employing the step of stiffening a pile of fibre cloths by the brief treatment of deposition of SiC from the already mentioned vapor phase as an alternative to the first three steps of the basic process. Nanometric powders (arbitrary units) Porosity (%) Flexural strength (MPa) 0 22 150 20 20 205 30 18,5 235 40 17 260 CVI + 30 14 370 As can be seen from the above data, the presence of increasing amounts of nanometric powders increases both the density (lower porosity) and the mechanical strength of the panels ready to use. Furthermore, it is evident that the brief treatment of deposition of SiC from the vapor phase, as an alternative to the first three steps of the basic process, advantageously improve the flexural strenght without increasing the processing time. A further meaningful difference between the composites of the present invention and those provided only by infiltration from the vapor phase is the behaviour in case of deformation under loaded conditions. The materials provided by the present invention have a capability of being deformed much greater than 1%, upon yielding, and as high as more than twice that of the composites provided only by CVI, as shown in Figs. 1 and 2. The microstructure of the produced material is shown in Fig. 3. It is self-evident that the microstructure of the material produced by using nanometric powders is very homogeneous and without large cavities. The product according to the present invention certainly has better characteristics than the material produced by using fillers of micrometric size at least with regard to the homogeneity of the matrix which has no large-size crystallites of SiC and is not greatly heterogeneous any more. Advantageously, the production time of a 5-8 mm tick panel is about two weeks compared with the much longer time requested by a CVI process. In addition, the use of nanometric powders allows a high final density of the product to be reached with a number of thickenings lower than in other liquid infiltration processes developed in other laboratories. Finally, according to a further characteristic of the invention the production process of a ceramic composite of the SiC/SiC type includes a preliminary step of providing the inert powders to be used for the infiltration, in which step the filling powders are produced by a laser pyrolysis process in which a c.w. CO 2 laser heats a molecular beam of gas precursors (e.g. silane and acetylene) causing the decomposition thereof and the formation of particles with a size, in the specific case of SiC, controlled by the reaction temperature and the dwell time of the gas precursors in the radiation area. Advantageously, such a preliminary step provides particles of nanometric granulometry with specific surfaces in the range of 50-120 m 2 /g and with an extremely narrow size distribution. What described above relates to a particular case concerning a not limiting example. However, it is evident that such a process may generally be applied to the production of CMCs based on different materials. It is also evident that products of different shape can have different operative parameters even if they are obtained by the same process and then do not depart from the scope of present industrial invention.

Claims: A process for providing ceramic composite materials having improved capability of being deformed, consisting of the following steps: step I: impregnating the single cloths of ceramic fibres with a precursor solution; step II: hardening the cloths provided by step I with a pressure not greater than 4 Mpa (40 kg/cm 2 ); step III: pyrolysis with a temperature not higher than 1100°C; step IV: repeated thickenings; characterized in that said step I consists of the impregnation of the single cloths by a precursor solution containing filling powders with a nanometric granulometry which is much lower than the mean distance between the fibres. The process according to claim 1, characterized in that as an alternative to the first three steps there is provided a preliminary step of hardening a pile of fibre cloths, preferably overlapped at 0° and 90° and compacted so that the fibre true volume is preferably the same as or greater than 35% of the apparent pile volume, by a brief (≤ 24 hours) treatment of infiltration of SiC from the vapor phase. The process according to claim 1, characterized in that said step I provides the preimpregnation of the SiC fibre cloths, commercially known as Nicalon and having a diameter of 10-15 µm, by a polymeric SiC precursor of the polycarbosilane (PCS) type containing filling powders of SiC with nanometric (nm) granulometry. The process according to claim 1, characterized in that the liquid impregnating agent used in said step I is polycarbosilane solubilized in toluene with a concentration of 50-70% by weight and mixed homogeneously with nanometric powders of SiC previously dispersed into the same solvent with a concentration of 10% and at such a varying proportion that the PCS/powders weight ratio is not greater than 60-40. The process according to claims 1 and 3, characterized in that the nanometric powder of said step I is subjected to a surface treatment with sterically acting dispersants, preferably dodecanol, in an amount of 1-2% relative to said powder so as to facilitate the dispersion and lower the fluid viscosity. The process according to claim 1, characterized in that in said hardening step II the cloths infiltrated in advance are piled up so that the fibres are oriented at 0° and 90° until the desired thickness is reached, the thickening of the thus obtained panels being carried out under vacuum at 10 -2 bar by a gradual heating up to 300°C and then under a mechanical pressure of about 40 kg/cm 2 during 10 minutes so that the thermoplastic resin melts with the result of a perfect sizing among the several layers and the suppression both of macro- and microvoids. The process according to claim 1, characterized in that said pyrolysis step III is carried out at 1100°C with a thermal cycle of about 36 hours as a whole according to a heating program providing a gradient of 8-10°C/hour in the temperature range 300-650°C which is most critical for the process. The process according to claim 1, characterized in that said thickening step IV is carried out through an alternation of infiltrations of a polymer solution, formed by 50-70% by weight of PCS in toluene, and pyrolysis. The process according to claim 1, characterized in that in said thickening step IV the first cycle is carried out by using a PCS solution also containing filling nanometric powders (in an amount of 30% by weight related to PCS) particularly in case the first three steps of the basic process are omitted and the alternative step IB of a brief ( ≤ 24 hours) treatment of deposition of SiC from the vapor phase is carried out in order to give rigidity and tridimensional stability to a bidimensional assembly of overlapped fibre cloths. The process according to claim 1, characterized in that a preliminary step is provided in which the filling powders are produced by a laser pyrolysis process in which a c.w. CO 2 laser heats a molecular beam of gas precursors, preferably silane and acetylene, causing the decomposition thereof and the formation of SiC particles with a size controlled by the reaction temperature and the dwell time of the gas precursors in the radiation area until particles of nanometric granulometry with specific surfaces in the range of 50-120 m 2 /g and with an extremely narrow size distribution are obtained.

Inventors: BORSELLA ELISABETTA, BOTTI SABINA, CASADIO SERGIO, D ALESSANDRO GIANNI, DONATO ALDO, LICCIULLI ANTONIO ALESSANDRO, MARTELLI STEFANO, MASCI AMEDEO, NANNETTI CARLO ALBERTO, ORTONA ALBERTO, BORSELLA, ELISABETTA, BOTTI, SABINA, CASADIO, SERGIO, D'ALESSANDRO, GIANNI, DONATO, ALDO, LICCIULLI, ANTONIO ALESSANDRO, MARTELLI, STEFANO, MASCI, AMEDEO, NANNETTI, CARLO ALBERTO, ORTONA, ALBERTO
Applicants: ENEA ENTE NUOVE TEC, ENEA ENTE PER LE NUOVE TECNOLOGIE
Application year: 1997
Main classification: C04B35
IPC codes: C04B35