COATING FORMULATION

Abstract: A coating formulation or surface modification for use on or in r espect of substrates, particularly those used in aqueous or fluid environments, produces and/or entraps a microlayer or gas or vapour at the interface between the substrate and the acqueous or fluid environment.

Description: "CQATIWg FQBKWAYIQy" The present invention relates to a coating or a surface modification for substrates used in aqueous or fluid environments such as sub-sea structures. More particularly, the invention relates to a coating or surface modification which can control the physical and chemical properties of various substrates in contact with aqueous or fluid environments. Several problems are encountered in the use of substrates in contact with aqueous or fluid environments, and in particular in substrates used in sub-sea structures. Particular problems include growth of marine or other fouling organisms such as algae, plant life or crustaceans on the substrate and thus the creation of a bio-net environment over the substrate. Other problems are associated with the loss in energy from the fluid flow over a given substrate due to hydrodyna ic drag coefficient properties intrinsic to the individual fluid flow/substrate interface. These factors affect the hydrodynamic drag coefficient properties of fluid over the substrate, for example, altering the hydro-dynamic properties of the substrate in an aqueous system. Also, they can affect the water repellent properties of the substrate and other chemical and/or physical properties such as corrosion resistance, thermal stability and structural properties . Attempts have been made to control fouling. Traditional anti-fouling techniques have involved the use of toxic materials to kill any organisms which grow or are deposited onto the substrate. Typical materials used are biocides, fungicides, Tri-butyl tin, Cuprous Oxide, Antimony Oxide, Molybdenum Disulphide and lead complexes. These are commonly known as leaching processes. However, such materials have a severe ecological impact. Hydro-dynamic properties of substrates are traditionally controlled in a number of ways. For example, self polishing coatings are known which are formulated to wear away or erode with time and friction to keep the surface at an acceptable level of hydrodynamic drag co-efficient. Coatings may be formulated with an inclusion of defrictionizing aids such as silanes, teflon and Shell's Epikote-Coal Tar resin systems which are commercially available. Also, water repellent properties can be improved by incorporating waxes, silanes, siloxanes, silicon molecules and modified resins into the substrate. Corrosion resistance is traditionally achieved using techniques such as corrosion resistant resins (i.e. epoxy, vinyl ester etc), zinc rich sacrificial primers, phosphorus and chromate derivatives and toxic acid within the substrate. Each of these approaches aims to improve the chemical and/or physical properties of a substrate, in terms of corrosion resistance, thermostability and structural properties but do not take into effect the ecological impact on the marine environment. Prevention and control of the formation of a bio-net is usually attained by the use of toxic materials. It is an object of the present invention to provide a coating formulation or surface modification for use on or in respect of substrates to be placed in an aqueous or fluid environment whereby the properties of the substrate which make it suitable for use in this environment are maintained or improved with negligible ecological impact. According to the present invention there is provided a formulation suitable for coating or modifying the surface of a substrate to be situated in an aqueous or fluid environment wherein the formulation is capable of producing and/or entrapping a micro layer of gas or vapour phase between the substrate and the aqueous or fluid environment. Optionally the entrapped gas may be air. Preferably, the formulation comprises of a structure of micro-particles, semi or semi-permeable foams or membrane, micro-filaments or combinations of any or all or the above which entrap the gas or vapour between the aqueous or fluid environment and the substrate. In aqueous systems the structure is preferably hydrophobic which promotes air entrapment between the substrate and the aqueous environment. Typically the surface chemistry of the formulation is such that when coated on a substrate it can control the surface tension between the fluid environment, the formulation structure and a substrate. The formulation can be attached to the substrate by physical or chemical means or via a combination of physical and chemical means. Substrates can include resin composites, metal, wood, steel, aluminium, concrete, natural rock, thermosetting plastic, and rubber based substrates. These substrates can be pre- treated with primers to help adhesion of the microparticles. A typical primer coating would be an epoxy based anti-corrosion primer used to prime mild steel substrates. Suitably the formulation can comprise of micro- particles chosen from the group containing: pyrogenic metal oxides such as fumed silica, fumed alumina, fumed ceasium, fumed zirconia, fumed titania, fumed itriu , fumed chromium, fumed tin, fumed molybdenum oxides and fumed vandium oxide; carbon black or channel black pigment particles; finely ground inorganic or organic particles such as talc, mica, bentones, calcium carbonate, iron and lead oxides; and precipitated particles such as precipitated silicon dioxide, silica, aluminium silicates and titanium dioxides, silica based particles such as hydrogels, solgels or aerogels, and synthetic resin based particulate products such as Pergopack. Hydrophillic micro-particles, foams or micro-filaments can also be used. These can be treated to create the surface tension or hydrophobicity required to entrap the gaseous phase between the substrate and the fluid phase. Treatment can be done prior to, during or after application to the substrate. Suitably also, the formulation can comprise of porous or semi-porous foams or membranes that could be created using a polyurethane moisture curing resin that is foamed and treated to create the required surface tension or hydrophobicity to promote the gas or vapour phase entrapment. Suitably also, the formulation can comprise of icro- filaments that mimic the behaviour of either bird feathers or animal fur to entrap air. These micro- filaments can be made from organic or inorganic materials, such as glass or plastic. Typically the surface energy of the structure of the formulation may be adapted by controlling the hydrophobicity of the structure. This can be done prior to, during or after the application of the coating or surface modification to the substrate. Preferably the micro-particles, foam or micro-filaments are treated with agents chosen from the group comprising natural and synthetic waxes, siloxanes, fluoro-silanes, reactive silanes, silicon oils, organo- silanes, organo-titaniate compounds, other silicon and hydrocarbon based materials or blends of the above. These treatments can occur during, prior to or after the application of the coating or surface modification to the substrate. Suitable commercially available modified micro- particles include Aerosil R202, Aerosil R974, Aerosil R805, HDK H2000, Sypernat DIO, Syloid ED 60, Neosyl and Aerosil R504, Bayer Titan Products, inofil, Bentones, sementoius clays, Laponites, Pergopack, Aluminium Oxide C, Titanium Oxide P25, etc. In one particular embodiment, the formulation comprises of a dispersion of a treated fumed silica in a blend of solvents, and/or water and/or additives. The additives would be used to improve the performance of the coating or surface modification. Such additives could be catalysts, adhesion promoters, fungicides, hardener, biocides, reactive silanes, surface tension modifiers and corrosion inhibitors. The composition of the solvent/water/additives dispersion could vary depending on the choice of substrate. A dispersion of a treated fumed silica in water and a range of similar additives could also be used. This coating can be applied to a partially or fully cured primer coating on a metal substrate. A typical primer coating could be an epoxy based coating. In an alternative embodiment, the formulation comprises use of a treated fumed silica blended with a hydro- carbon resin wherein the hydro-carbon resin bonds the silica to a substrate surface. Additives as described above can also be used to improve the hydrophobic performance of the coating or surface modification. Preferably the fumed silica is prepared from highly dispersed amorphous silicon dioxide treated with dimethyldichlorosilane, hexamethyldiεilazane or polymethylsiloxane or composite hydrophobic treatments. Preferably the bonding resin is an epoxy, a polyurethane, a polyester, a vinylester, an acrylic or composites of the above. The bonding resin may be a powder or in a selected solvent/resin solution. The microparticles can be coated onto the substrate held in a solvent blend or aqueous dispersion. The bonding of the microparticles can be improved by further treating it with other chemical compounds that aid adhesion by either chemical, electrostatic or physical means. An example of this could be treating a hydrophobic fumed silica with an Amino Silane or an Organotitanate or blends to improve chemical adhesion to an epoxy resin based coated substrate. A commercial product would be Aerosil R504. Suitably the coating formulation comprises from 1% to 90% fumed, treated hydrophobic silica. Suitably the coating formulation comprises from 1% to 90% hydro-carbon resin. The formulation can also be applied directly to a partially cured, uncured, pre-vulcanised, post- vulcanized or thermosetting substrate. An example would be passing a heated thermosetting plastic coated wire through a bath of a dry silica or a dispersion containing silica. The invention further provides a process for coating a substrate, the process comprising the steps of heating the selected coating formulation to between 50°C - 300°C and depositing the composition on to the substrate. Alternatively, the invention provides a process for coating a substrate, the process comprising the steps of preheating the substrate and depositing the coating formulation on to the substrate. For hydro-carbon oil fluid systems oleophobic treatments such as fluorine derivatives may be used to entrap the required gas or vapour. These are of specific value in oil/water systems. Similar delivery and bonding mechanisms can be used as described previously. In an alternative embodiment of the invention, a metallised coating may be used. Amongst others, any or all of zinc, aluminium and nickel metals may be used. The invention further comprises a process for coating a substrate with a metallised coating, the process comprising heating a blend of fumed treated hydrophobic silica and metal to between 100°C - 1000°C and depositing the blended composition on the substrate. Suitably a sand mill, pebble mill or steel ball horizontal mill may be used to blend treated silica and resin, metal, solvent blend or aqueous dispersion. A coating formulation may be deposited by being sprayed or painted onto the substrate. Alternatively the composition may be electrostatically deposited onto the substrate. The choice of micro-particles, resin or metal and the treatment will depend on the substrate to be coated, the environment in which the substrate is to be situated and the required properties in that environment. An example of a formulation according to the invention is now further described with reference to Fig 1. In the example shown in Fig 1, the treated fumed silica is blended with the hydro-carbon resin wherein the hydro-carbon resins bonds the silica to the substrate surface. The fumed silica in this example is the reaction product of the flame hydrolysis of a silane compound (typically a chloro or fluoro silane) which is further treated with dimethyldichlorosilane, hexamethyldisilazane or polymethylsiloxane. This treatment imparts hydrophobicity to the fumed silica. Superhydrophobicity, however, requires the synergy of the silicon water repellant and the entrapment of air or blends of the above with other silane materials. This is illustrated in Fig 1. The hydro-carbon resin forms a surface on the substrate with the hydrophobic silica entrapping air between the substrate and the water. A coating such as this effectively prevents the adhesion to a marine hull of the fouling bio-net without the requirement of toxic compounds leaching into the ocean, e.g. TBT, the treatment for anti- fouling currently employed. 1 A further advantage in the use of the coating is the 2 reduction of hydrodynamic drag and the consequent fuel 3 economy. 4 5 Therefore, according to the present invention, there is 6 provided a coating formulation wherein the creation of 7 a micro layer of air or gas or vapour phase between the 8 substrate and aqueous or liquid phase results in 9 improved hydro-dynamic or co-efficient of friction 0 characteristics created between the aqueous or fluid 1 phase and the substrate. Also, the coating prevents 2 and controls the formation of a bio-net and has 3 negligible ecological impact in a marine environment. 4 5 The coating also provides reduced contact or prevention 6 of the contact of the substrate with the aqueous or 7 fluid phase. The coating further improves the 8 substrates overall chemical resistance to the fluid 9 phase. The micro-layer between the fluid and the 0 substrate will help reduce or prevent the osmosis of 1 the fluid occurring across or through the substrate. 2 An example of this would be the reduction or prevention 3 of the phenomenon known as "osmotic" blistering of 4 polyester constructed pleasure boat hulls. 5 6 The application of such a coating or surface 7 modification to a substrate could reduce the possible 8 formation of ice on the substrate. A typical 9 application of this would be to reduce the build up of 30 ice on an aeroplane wing. 31 32 Further modifications and applications may be made 33 without departing from the scope of the invention 34 herein intended. 35 T g /u/mur/specs/prøl- 37

Claims: CLAIMS 1. A formulation suitable for coating or modifying the surface of a substrate to be situated in an aqueous or fluid environment wherein the formulation is capable of producing and/or entrapping a micro layer of gas or vapour phase between the substrate and the aqueous or fluid environment. 2. A formulation as claimed in Claim 1 wherein the entrapped gas is air. 3. A formulation as claimed in Claim 1 or Claim 2 which comprises of a structure of micro-particles. 4. A formulation as claimed in Claim 1 or Claim 2 which comprises of semi or semi-permeable foams or membrane. 5. A formulation as claimed in Claim 1 or Claim 2 which comprises of micro filaments. 6. A formulation as claimed in any one of the preceding Claims comprising a hydrophobic structure. 7. A formulation as claimed in Claim 3 wherein the micro-particles are chosen from the group containing: pyrogenic metal oxides such as fumed silica, fumed alumina, fumed ceasium, fumed zirconia, fumed titania, fumed itriu , fumed chromium, fumed tin, fumed molybdenum oxides and fumed vandiu oxide; carbon black or channel black pigment particles; finely ground inorganic or organic particles such as talc, mica, bentones , calcium carbonate, iron and lead oxides; and precipitated particles such as precipitated silicon dioxide, silica, aluminium silicates and titanium dioxides, silica based particles such as hydrogels, solgels or aerogels, and synthetic resin based particulate products such as Pergopack. 8. A formulation as claimed in any one of the preceding Claims treated with agents chosen from the group comprising natural and synthetic waxes, siloxanes, fluoro-silanes, reactive silanes, silicon oils, organo-silanes, organo-titaniate compounds, other silicon and hydrocarbon based materials or blends of the above. 9. A process for coating a substrate, the process comprising the steps of heating formulation as claimed in any one of Claims 1 to 8 to between 50°C - 300°C and depositing the composition on to the substrate. 10. A process for coating a substrate, the process comprising the steps of preheating the substrate and depositing a coating formulation on to the substrate. 11. A process for coating a substrate with a metallised coating, the process comprising heating a blend of fumed treated hydrophobic silica and metal to between 100°C - 1000°C and depositing the blended composition on the substrate.

Inventors: FREW JEREMY GEORGE MCKENZIE, STARK IAN STRACHAN, FREW, JEREMY, GEORGE, MCKENZIE, STARK, IAN, STRACHAN
Applicants: FREW JEREMY GEORGE MCKENZIE, PROTECTIVE RESEARCH IND LIMITE, STARK IAN STRACHAN, FREW, JEREMY, GEORGE, MCKENZIE, PROTECTIVE RESEARCH INDUSTRIES LIMITED, STARK, IAN, STRACHAN
Application year: 1997
Main classification: C09D5
IPC codes: B63B59, C09D5