ENZYMATIC HYDROLYSIS OF CYCLIC OLIGOMERS

Abstract: The present invention relates to a process for enzymatic hydrolysis of cyclic oligomers of poly(ethylene terephthalate), which process comprises subjecting the cyclic oligomer to the action of one or more lipolytic and/or biopolyester hydrolytic enzyme(s).

Description: ENZYMATIC HYDROLYSIS OF CYCLIC OLIGOMERS TECHNICAL FIELD The present invention relates to a process for enzymatic hydrolysis of cyclic oligomers of poly(ethylene terephthalate) , which process comprises subjecting the cyclic oligomer to the action of one or more carboxylic ester hydrolases. BACKGROUND ART Poly(ethylene terephthalate) fibers accounts for the main part of the polyester applied by the textile industry. The fibers are produced by e.g. poly-condensation of terephthalic acid and ethylene glycol, and drawing of fibers from a melt. During these processes, at high temperatures, cyclic oligomers, in particular cyclic tri (ethylene terephthalate), are formed in and on the fibers. Cyclic oligomers tend to give fabrics with a content of poly(ethylene terephthalate) fibers a grayish appearance. This is due to deposits of cyclic oligomers on the surface of the fabric, which is particularly outspoken after high temperature wet processes like HT (high temperature) dyeing. The cyclic oligomers are difficult to remove and may even be resistant to an alkaline post treatment [cf . G. Valk et al . ; Melliand Textilberichte 1970 5 504-508] . Therefore, to be effective, the alkaline treatment has to be severe, which results in a significant loss of fiber material. Also, organic extraction of the cyclic oligomers is a technical possibility, but not industrially feasible. SUMMARY OF THE INVENTION It is an object of the present invention to provide an enzymatic process for removal of cyclic oligomers of poly(ethylene terephthalate) , in particular cyclic tri (ethylene terephthalate) , by which process the cyclic oligomers are enzymatically hydrolyzed to linear fragments, which can then be removed under gentle conditions, or which may even be leftover. Thus the process of the invention avoids the need for harsh chemicals or organic extraction. Accordingly, the invention provides a process for enzymatic hydrolysis of cyclic oligomers of poly(ethylene terephthalate) , which process comprises subjecting the cyclic oligomer to the action of one or more carboxylic ester hydrolases. DETAILED DISCLOSURE OF THE INVENTION The present invention relates to a process for enzymatic hydrolysis of cyclic oligomers of poly(ethylene terephthalate) . More specifically the invention provides a process for enzymatic hydrolysis of cyclic oligomers of poly(ethylene terephthalate), which process comprises subjecting the cyclic oligomer to the action of one or more carboxylic ester hydrolases, in particular lipolytic and/or biopolyester hydrolytic enzyme (s) . In the context of this invention a biopolyester is a polyester of biological origin. The process of the invention may in particular be applied to yarns or fabrics with a content of poly(ethylene terephthalate) fibers, during which process the content of cyclic oligomers, which were formed as byproducts during synthesis and processing of the fibers, becomes eliminated or at least significantly reduced. Polyester Fabrics Poly(ethylene terephthalate) is synthesized by condensation, drawn into fibers from a melt, possibly cut to stables, possibly mixed with other fiber types, and spun to yarn. The yarn is dyed and knitted into cloth or made into carpets, or the yarn is woven into fabric and dyed. These processes can be followed by finishing (post treatment) steps. During synthesis and drawing, cyclic oligomers of poly(ethylene terephthalate) are formed on and in the fibers. These cyclic oligomers are partly deposited on machinery, partly staying on/in the fibers, which turns out to give an undesirable grayish appearance of the final fabric or carpet. Cyclic oligomers can be removed by organic extraction, but such a process is not industrially feasible due to cost and problems in handling and regeneration of large quantities of organic solvents. Cyclic oligomers can also be removed by an alkaline post scouring step, but to be effective the alkaline treatment has to be severe and results in significant loss of fiber material, too. According to the present invention, removal of cyclic oligomers, in particular cyclic trimers, can be accomplished by hydrolysis with one or more hydrolytic enzymes. The enzyme breaks the ring structure of the cyclic oligomer by hydrolyzing an ester bond. The resulting product creates less of a problem, because it can be removed under gentle conditions or even leftover in the produc . The enzymatic treatment does not have the disadvantages valid for organic extraction and alkaline post scouring, in particular is does not require large quantities of organic solvent to be involved, and there is no significant loss of fiber material. The process of the invention is readily applicable in the textile industry as it can be carried out using existing wet processing apparatus, such as in a beam dyer, a Pad-Roll, a Jigger/Winch, a J-Box, or Pad-Steam types of apparatus. The process preferably takes place during the finishing (post treatment) step. In a preferred embodiment the process of the invention may be accomplished on cyclic oligomers of poly(ethylene terephthalate) present on and/or in fibers or in yarn or fabric made (or partially made) from poly(ethylene terephthalate) fibers. Thus, the polyester yarn or fabric may be any yarn or fabric that is made from pure poly(ethylene terephthalate) , or that is made from blends of poly(ethylene terephthalate) fibers and any other material conventionally used for making yarns or fabrics. Thus, in a preferred embodiment, the invention provides a process for enzymatic treatment of polyester fibers, which 5 process comprises subjecting the polyester fiber or fabric to the action of one or more carboxylic ester hydrolases, in particular lipolytic and/or biopolyester hydrolytic enzyme (s) . The polyester fabric may be any fabric or fabric blend comprising polyester. Preferably the fabric comprises more than 10 50% (w/w) of polyester, in particular more than 75% (w/w) of polyester, more than 90% (w/w) of polyester, or more than 95% (w/w) of polyester. In a most preferred embodiment, the process of the invention is applied to fabrics or textiles or yarns consisting essentially of poly(ethylene terephthalate) polyester 15 material, i.e. pure poly(ethylene terephthalate) polyester material . Hydrolytic Enzymes The enzymatic finishing process of the invention may be 20 accomplished using any carboxylic ester hydrolases, in particular lipolytic enzyme and/or any biopolyester hydrolytic enzyme. Such enzymes are well known and defined in the literature, cf. e.g. Borgstrδm B and Brockman H L, (Eds.) ,* Lipases; Elsevier Science Publishers B.V., 1984, and Kolattukudy P E; The Biochemistrv of 25 Plants, Academic Press Inc., 1980 4 624-631. In the context of this invention lipolytic enzymes include true lipases, esterases, phospholipases, and lyso- phospholipases. More specifically the lipolytic enzyme may be a lipase as classified by EC 3.1.1.3, EC 3.1.1.23 and/or EC 30 3.1.1.26, an esterase as classified by EC 3.1.1.1, EC 3.1.1.2, EC 3.1.1.6, EC 3.1.1.7, and/or EC 3.1.1.8, a phospholipase as classified by EC 3.1.1.4 and/or EC 3.1.1.32, and a lyso- phospholipase as classified by EC 3.1.1.5. The lipolytic enzyme preferably is of microbial origin, 35 in particular of bacterial, of fungal or of yeast origin. In a particular embodiment, the lipolytic enzyme used may be derived from a strain of Absidia , in particular Absidia blakesleena and Absidia corymbifera, a strain of Achromobacter , in particular Achromobacter iophagus, a strain of Aeromonas, a strain of Al ternaria , in particular Al ternaria brassiciola , a strain of Aspergillus, in particular Aspergillus niger and Aspergillus flavus, a strain of Achromobacter, in particular Achromobacter iophagus, a strain of Aureobasidium, in particular AureoJasidiu pullulans, a strain of Bacillus, in particular Bacillus pumilus, Bacillus str ear o thermophilus and Bacillus subtilis, a strain of Beauveria, a strain of Brochothrix, in particular Brochothrix thermosohata, a strain of Candida, in particular Candida cylindracea ( Candida rugosa) , Candida paral ipolytica , and Candida antarctica, a strain of Chromobacter, in particular Chromobacter viscosum, a strain of Coprinus, in particular Coprinus cinerius , a strain of Fusarium, in particular Fusarium oxysporum, Fusarium solani , Fusarium solani pisi , and Fusarium roseum culmorum, a strain of Geotricum, in particular Geotricum penicilla tum, a strain of Hansenula, in particular Hansenula anomala, a strain of Humicola, in particular Humicola brevispora , Humicola brevis var. thermoidea, and Humicola insolens, a strain of Hyphozyma, a strain of Lactobacillus, in particular Lactobacillus curvatus, a strain of Metarhiziu , a strain of Mucor, a strain of Paecilomyces, a strain of Penicillium, in particular Penicillium cyclopium, Penicillium crustosum and Penicillium expansum, a strain of Pseudomonas in particular Pseudomonas aeruginosa, Pseudomonas alcaligeneε, Pseudomonas cepacia (syn. Burkholderia cepacia) , Pseudomonas fluorescens, Pseudomonas fragi , Pseudomonas mal tophilia , Pseudomonas mendocina, Pseudomonas mephi tica 1 ipolytica, Pseudomonas alcaligenes, Pseudomonas plantari , Pseudomonas pseudoalcaligeneε , Pseudomonas putida, Pseudomonas stutzeri , and Pseudomonas wisconsinensiε , a strain of Rhizoctonia, in particular Rhizoctonia solani , a strain of Rhizomucor, in particular Rhizomucor miehei , a strain of Rhizopus, in particular Rhizopus japonicus, Rhizopus microsporus and Rhizopus nodosuε, a strain of Rhodosporidium, in particular Rhodosporidium toruloides, a strain of Rhodotorula , in particular Rhodotorula glutiniε, a strain of Sporobolomyces, in particular Sporobolomyces shibatanus, a strain of Thermomyces, in particular Thermomyces lanuginosus (formerly Humicola lanuginosa) , a strain of Thiarosporella, in particular Thiaroεporella phaseolina, a strain of Trichoderma , in particular Trichoderma harzianu , and Trichoderma reesei , and/or a strain of Verticillium. In a more preferred embodiment, the lipolytic enzyme used according to the invention is derived from a strain of Aspergillus , a strain of Achromobacter, a strain of Bacillus, a strain of Candida, a strain of Chromobacter, a strain of Fusarium, a strain of Humicola, a strain of Hyphozyma, a strain of Pseudomonas, a strain of Rhizomucor, a strain of Rhizopus , or a strain of Thermomyces . In a more preferred embodiment, the lipolytic enzyme used according to the invention is derived from a strain of Bacillus pumilus, a strain of Bacillus stearothermophilus a strain of Candida cylindracea , a strain of Candida antarctica, in particular Candida antarctica Lipase B (obtained as described in WO 88/02775) , a strain of Humicola insolens, a strain of Hyphozyma , a strain of Pseudomonas cepacia, or a strain of Thermomyces lanuginosus . In the context of this invention biopolyester hydrolytic enzyme include esterases and poly-hydroxyalkanoate depolymerases, in particular poly-3-hydroxyalkanoate depolymerases. In fact an esterase is a lipolytic enzyme as well as a biopolyester hydrolytic enzyme. In a more preferred embodiment, the esterase is a cutinase or a suberinase. Also in the context of this invention, a cutinase is an enzyme capable of degrading cutin, cf . e.g. Lin T S & Kolattukudy P E, J. Bacteriol. 1978 133 (2) 942-951, a suberinase is an enzyme capable of degrading suberin, cf. e.g. , Kola ttukudy P E; Science 1980 208 990-1000, Lin T S & Kolattukudy P E; Physiol. Plant Pathol. 1980 17 1-15, and The Biochemistry of Plants, Academic Press, 1980 Vol. 4 624-634, and a poly-3-hydroxyalkanoate depolymerase is an enzyme capable of degrading poly-3-hydroxyalkanoate, cf. e.g. Foster et al . , FEMS Microbiol. Lett. 1994 118 279-282. Cutinases, for instance, differs from classical lipases in that no measurable activation around the critical micelle concentration (CMC) of the tributyrine substrate is observed. Also, cutinases are considered belonging to a class of serine esterases. The biopolyester hydrolytic enzyme preferably is of microbial origin, in particular of bacterial, of fungal or of yeast origin. In a preferred embodiment, the biopolyester hydrolytic enzyme is derived from a strain of Aspergillus, in particular Aspergillus oryzae, a strain of Al ternaria , in particular Alternaria brassiciola, a strain of Fusarium, in particular Fusarium solani , Fusarium solani pisi , Fusarium roseum culmorum, or Fusarium roseum sambucium, a strain of Helminthosporum, in particular Helminthosporum sativum, a strain of Humicola , in particular Humicola insolens, a strain of Pseudomonas, in particular Pseudomonas mendocina , or Pseudomonas putida , a strain of Rhizoctonia , in particular Rhizoctonia solani , a strain of Streptomyces, in particular Streptomyces scabies, or a strain of Ulocladium, in particular rJlocladium consortiale . In a most preferred embodiment the biopolyester hydrolytic enzyme is a cutinase derived from a strain of Humicola insolens, in particular the strain Humicola insolens DSM 1800. In another preferred embodiment, the poly-3- hydroxyalkanoate depolymerase is derived from a strain of Alcaligeneε , in particular Alcaligenes faecalis, a strain of Bacillus , in particular Bacillus megaterium, a strain of Camomonas, in particular Camomonas testosteroni , a strain of Penicillium, in particular Penicillium funiculosum, a strain of Pseudomonas, in particular Pseudomonas fluorescens, Pseudomonas lemoignei and Pseudomonas oleovorans, or a strain of Rhodospir ilium, in particular Thodospir ilium rubrum. Process Conditions The enzymatic treatment according to the present invention preferably is carried out as a wet process. It is at present contemplated that a suitable liquor:textile ratio may be in the range of from about 20:1 to about 1:1, preferentially in the range of from about 15:1 to about 5:1. Enzyme dosage must be a function of the enzyme (s) applied and the reaction time and conditions given. It is at present contemplated that the enzyme (s) may be dosed in a total amount of from about 0.001 g/kg to about 5 g/kg enzyme per yarn or fabric, preferably from about 0.001 g/kg to about 0.5 g/kg. The enzymatic hydrolysis may be carried out in the temperature range of from about 30°C to about 100°C, preferentially from about 50°C to about 100°C. The pH range may, dependent on the enzyme (s) applied, be from about pH 4 to pH 11. It is at present contemplated that a suitable reaction time may be in the range of from about 15 minutes to about 3 hours . The process of the invention may further comprise the addition of one or more chemicals capable of improving the enzyme-substrate interaction (in order to improve the substrate's accessibility and/or dissolve reaction products) , which chemicals may be added prior to, or simultaneously with the enzymatic treatment. Such chemicals may in particular be surfactants, wetting agents, and dispersing agents, or mixtures hereof . The process of the invention may optionally comprise a rinsing step during which the hydrolyzed cyclic oligomers are subjected to rinsing, in particular to rinsing with dilute alkali. Dilute alkali dissolves linear fragments of the cyclic oligomers, and may to some extent further hydrolyze these linear fragments . In the context of this invention dilute alkali comprise aqueous solutions having a pH in the range of from about pH 7 to about pH 11, more preferably of from about pH 7 to about pH 10, most preferred of from about pH 7 to about pH 9. A buffer may be added to the medium. EXAMPLES The invention is further illustrated in the following examples, which are not intended to be in any way limiting to the scope of the invention as claimed. EXAMPLE 1 In this example eleven different enzymes with lipolytic and/or biopolyester hydrolytic activity are examined for their activity towards cyclic oligomers of poly(ethylene terephthalate) . The cyclic oligomers are obtained from polyester fabric by Soxhlet extraction with 1,4-dioxane. The eleven enzymes tested in this example are: Bacillus pumilus lipase (obtained as described in WO 91/16422) ; Bacillus s t ea o thermophilus lipase (obtained as described in JP 64/744992) ; Candida antarctica Lipase B (obtained as described in WO 88/02775) ; Candida cylindracea (= Candida rugoεa) lipase (obtained from Nippon Oil & Fats Co. Ltd., Japan) ; Pseudomonas cepacia lipase (obtained as described in EP 331,376) ; Glucosaminated Lipolase™ (obtained as described in WO 95/09909) ; Thermomyces lanuginosus (formerly Humicola lanuginosa) lipase (obtained as described in EP 305,216) ; Recombinantly produced guinea pig lipase (rGPL) (obtained as described in WO 93/00426); Humicola insolens cutinase (actually a lipase also having cutinase activity, obtained from the strain Humicola insolenε DSM 1800 as described in Example 2 of US 4,810,414) ; Aspergillus aculeatus pectin methyl esterase (PME; obtained as described in WO 94/25575) ; and Aspergillus aculeatus acetyl esterase (AE; obtained as described in WO 95/02689) . The substrate solution is incubated with the hydrolytic enzyme preparation in an agar gel containing phenol-red. 1000 ml agar gel is prepared from 17 g Agarose type 2 medium EEO (Sigma, A-6877) , 3 g NaN0 3 , 1 g K 2 HP0 4 , 0.5 g KCl, 1 ml 1% (w/v) FeSO « , and 50 ml 0.4 g/1 phenol-red solution, pH adjusted to 8.0-8.5. Table 1 Clarification Zones Strain Enzyme type Activity on Activity on tributyrine cyclic oligo. Blank 0 0 Bacillus pumilus Bacterial 3 1 lipase lipase Bacillus Bacterial 3-4 1 stearo thermophi lus lipase lipase Candida antarctica Fungal lipase 3 0-1 Lipase B Candida cylindracea Fungal lipase 4 0-1 (rugosa) lipase Pseudomonas cepacia Fungal lipase 5 1 lipase Thermomyces Fungal lipase 4 1 lanuginosus lipase Glucosaminated Mod. Fungal 3 0-1 Lipolase™ lipase Recombinant guinea Rec . Mammal 4 2 pig lipase j lipase Humicola insolens Fungal cutin 4 1 cutinase esterase Aspergillus Fungal pectin 0 0-1 aculea tus PME methyl esterase Aspergillus Fungal acetyl 0 1 aculeatus AE esterase The substrate solution, 15 μl tributyrine or cyclic oligomers, is poured into plug holes in the agar, and the 5 aqueous enzyme solution is mixed into the substrate solution. If the enzyme is capable of hydrolyzing the substrate, then acids are formed and diffuse into the gel, where the pH indicator phenol-red turns from red to yellow. 10 EXAMPLE 2 In this example a lipolytic and biopolyester hydrolytic enzyme (Humicola insolens cutinase derived from the strain Humicola insolens DSM 1800 as described in WO 96/13580) is 15 examined for activity towards cyclic tri (ethylene terephthalate) . The cyclic trimer is obtained from polyester fabric by Soxhlet extraction with 1,4-dioxane, and is further purified by ethanol and 1,4-dioxane washes. A mixture of the following composition is incubated at 20 30°C for 16 hours: 0.25 ml glycylglycine buffer, 0.2 M pH 8.5 2.50 ml de-ionized water 0.25 ml cyclic trimer, 5.0 mM in 1,4-dioxane 62.5 μg of enzyme 25 The reaction is stopped by adding 5.0 ml 1,4-dioxane, and the mixture is analyzed on a reverse phase HPLC, ODS (octa dodecyl silicate) column eluted with acetonitrile and pH 3.0 phosphate-buffer. Detection of the reaction products is carried out spectrophotometrically at 240 nm, at which wavelength the 30 terephthalic acid and terephthalate derivatives adsorb. Table 2 Reaction Products as Determined by HPLC Peak Area, 240 nm Blank Humicuia insolens cutinase Cyclic trimer 8.07 (100%) 3.69 (44%) (17.6 min. ) Product 1 0.00 (0%) Trace (<5%) (3.8 min. ) Product 2 0.00 (0%) 2.26 (27%) (4.5 min. ) Product 3 0.00 (0%) Trace (<5%) (5.3 min.) Product 4 0.00 (0%) 2.40 (29%) (13.0 min.) Total area, 240 nm 8.07 8.35 In this example 56% of the cyclic tri (ethylene terephthalate) is degraded under the given conditions by the cutinase from Humicuia insolens, yielding four detectable degradation products. Following this experiment three of these products have been identified as ethylene bis (terephthalic acid) ester (MW=342) , terephthalic acid mono (2-hydroxyethyl) ester (MW=210) and terephthalic acid (MW=166) .

Claims: CLAIMS 1. A process for enzymatic hydrolysis of cyclic oligomers of poly(ethylene terephthalate), which process comprises subjecting the cyclic oligomer to the action of one or more carboxylic ester hydrolases. 2. The process according to claim 1, which process comprises subjecting the cyclic oligomer to the action of one or more lipolytic and/or biopolyester hydrolytic enzyme (s) . 3. The process according to claim 2, wherein the lipolytic enzyme is a lipase, an esterase, a phospholipase, and/or a lyso-phospholipase. 4. The process according to claim 3, wherein the lipolytic enzyme is a lipase derived from a strain of Aspergrillus, a strain of Achromobacter, a strain of Bacillus, a strain of Candida, a strain of Chromobacter, a strain of Fusarium, a strain of Humicola, a strain of Hyphozyma, a strain of Pseudomonas, a strain of Rhizomucor, a strain of Rhizopus, or a strain of Thermomyces . 5. The process according to claim 4, wherein the lipolytic enzyme is a lipase derived from a strain of Bacillus pumilus, a strain of Bacillus stearothermophilus a strain of Candida cylindracea, a strain of Candida antarctica, a strain of Humicola insolens, a strain of Hyphozyma , a strain of Pseudomonas cepacia, or a strain of Thermomyces lanuginosus . 6. The process according to claim 2, wherein the lipolytic enzyme is a phospholipase or lyso-phospholipase derived from a strain of Achromobacter, in particular a Achromobacter iophagus, a strain of Candida , in particular Candida paral ipolytica, a strain of Pseudomonas, in particular Pseudomonas mephi tica 1 ipolytica . 7. The process according to claim 2, wherein the biopolyester hydrolytic enzyme is an esterase and/or poly-hydroxyalkanoate depolymerase. 8. The process according to claim 7, wherein the esterase is a cutinase, or a suberinase. 9. The process according to claim 7, wherein the esterase is derived from a strain of Aspergillus, in particular Aspergillus oryzae, a strain of Alternaria, in particular Al ternaria brassiciola, a strain of Fusarium, in particular Fusarium solani , Fusarium solani pisi , Fusarium roseum cul orum, or Fusarium roseum sambucium, a strain of Helminthosporum, in particular Helminthosporum sativum, a strain of Humicola, in particular Humicola insolens, a strain of Pseudomonas, in particular Pseudomonas mendocina , or Pseudomonas putida, a strain of Rhizoctonia, in particular Rhizoctonia solani , a strain of Streptomyces , in particular Streptomyces scabies, or a strain of Ulocladium, in particular Ulocladium consortiale . 10. The process according to claim 9, wherein the esterase is a cutinase derived from a strain of Humicola insolens, in particular the strain Humicola insolens DSM 1800. 11. The process according to claim 7, wherein the poly- hydroxyalkanoate depolymerase is derived from a strain of Alcaligenes, in particular Alcaligenes faecalis, a strain of Bacillus, in particular Bacillus megaterium, a strain of Camomonas, in particular Camomonas testosteroni , a strain of Penicillium, in particular Penicillium funiculosum, a strain of Pseudomonas, in particular Pseudomonas fluorescens, Pseudomonas lemoignei and Pseudomonas oleovorans, or a strain of Rhodospir lium, in particular Thodospir ilium rubrum. 12. The process according to any of claims 1-11, further comprising the addition of one or more chemicals improving the enzyme-substrate interaction, in particular a surfactants, a wetting agent, and/or a dispersing agent. 13. The process according to any of claims 1-12, wherein the enzymatic action is followed by a rinsing step, during which step hydrolyzed cyclic oligomer is subjected to treatment with an alkaline solution. 14. The process according to either of claims 1-13, wherein the cyclic oligomer is present in and on the fibers of a polyester containing fabric or yarn. 15. The process according to either of claims 1-14, in which the cyclic oligomer is cyclic tri (ethylene terephthalate) .

Inventors: KOCH RAINHARD, LUND HENRIK, PEDERSEN LARS SAABY, RIEGELS MARTIN, KOCH, RAINHARD, LUND, HENRIK, PEDERSEN, LARS, SAABY, RIEGELS, MARTIN
Applicants: KOCH RAINHARD, LUND HENRIK, NOVONORDISK AS, PEDERSEN LARS SAABY, RIEGELS MARTIN, KOCH, RAINHARD, LUND, HENRIK, NOVO NORDISK A/S, PEDERSEN, LARS, SAABY, RIEGELS, MARTIN
Application year: 1997
Main classification: C08G63
IPC codes: C08G63, C12P1, C12P7, C12S11, D06M16, D06M101