INJECTION MOULDED AND FOAMED ARTICLE

Abstract: An eye bath (470) has a thin wall (471) and a hollow annular rim (472). This was formed in an injection mould tool with a tear drop cross-sectional shape (473) - shown at one side - around the wall as a pre-form of polypropylene material mixed with blowing agent. On mould opening before the material has solidified in the tear drop, this expands to circular cross section with a circumferential length (474) equal to that of the tear drop (475). This results in a slight fore-shortening of the height (476) of the eye bath from the height of the pre-form (477).

Description: INJECTION MOULDED AND FOAMED ARTICLE The present invention relates to a method of forming an article via injection of plastics material into a mould It should be emphasised that in this specification, including the claims, the meaning of the term "blowing agent" encompasses both "chemical blowing agents" and "physical blowing agents" A chemical blowing agent comprises at least one compound which breaks down in molten plastics material to mix gas into the material A physical blowing agent is a gas or a liquid - at room temperature and pressure - or mixed with the molten matei ial Chemical blowing agents are added to the plastics material in the hopper of matei ial fed to an injection moulding machine's plasticising screw Physical blowing agents can be mixed with the plastics material as described in my UK patent applications Nos 97029771 1 and 9706682 3, respectively dated 13th February and 2nd April 1997 These are still unpublished However, the mechanism for producing a mixture of blowing agent and plastics material forms no part of this invention, which is concerned with pioduction of articles using such mixtures Geneially, the blowing agent as such will add negligibly to the volume of the material when being processed within an injection moulding machine due to the elevated pressure within the machine Howevei , when the pressure is released to substantially lower pressuie, such as room pressure, and the plastics material is still molten, the blowing agent acts to expand the material by the blowing voids of varying sizes in the material A recognised pi blem in injection moulding fi om plastics materials of articles having thin walls in paiticular, is that at maiked differences in cross-section, differential shrinkage causes blemishes in the finished surface of the article Despite this problem, many new designs of injection moulded articles could be feasible if marked changes in cioss-section were possible, without shrinkage blemishes 1 Chemical blow ing agents aie tisualh bound into a carπci of other plastics material which has its own bulk The following applications describe my basic invention having the object of providing an improved method based on injection moulding and facilitating the production of substantial changes in cross-section: British Patent Application No. 95 14674.2 US Patent Application No. 60/017386 International Patent Application No. PCT/GB96/01706, now published under No WO 97/03800. In these applications 1 describe and/or claim (as proposed to be amended): A method of forming an article via injection of plastics material into a mould, the finish formed article having thin wall portion(s) and thick wall portion(s), the thick wall portion(s) being at least partially foamed, the method consisting in the steps of: providing a mould tool defining in its closed state, between its cavity part and its core part, narrow gap portion(s) whose mould part gap is to be substantially reproduced in the thin wall portion(s) of the article and wide gap portion(s) whose mould part gap is less than the thickness of the thick wall portion(s) of the finish formed article; closing the mould tool to define the narrow and wide gap portions; injecting a plastics mateiial mixture comprising a basic polymer and a foam producing additive into the mould tool; allowing the plastics material mixture to at least substantially solidify in the narrow gap portions of the mould tool to produce the thin wall portions of the finish formed article; withdrawing at least a portion of one part of the mould tool from the other part before the plastics material mixture has at least substantially solidified in the wide gap portion(s) of the mould tool to allow the mixture to expand by foaming and form at least some of the thick wall portion(s) of the finish formed article; and ejecting the article from the mould tool. This method is hereinafter referred to as "My Original Method". To help understanding of My Original Method its first embodiment will now be described with reference to the following of the accompanying drawings, in which: Figure 1 is a cross-sectional side view of an injection moulded cup able to be moulded with a mould using a technique, which appears to be known; Figure 2 is a similar view of a cup formed in accordance with My Original Method; Figure 3 is a similar view of a mould tool for preliminary moulding of the cup; Figure 4 is a side similar view of the mould tool open for foaming of thick wall sections of the cup on the core of the mould tool. Referring first to Figure I , the cup has a base I , a lower side wall 2 and an upper side wall 3, these being thin wall portions. At the corner 4 between the base and the lower side wall, at a band 5 between the upper and lower side walls and at the rim 6 there a thick wall portions. Typically the thin wall portions are 0.7mm thick and the thick wall portions are 1 .2mm thick. This cup could be moulded with conventional plastics materials, but due to the different wall sections, shrinkage marks could be expected to appear in the thick wall portions. In other words, conventional moulding techniques result in uneven wall thickness in the thick wall portions 1 discovered that 1 can mould the cup with even wall thickness in the thick wall portions, by including a small amount of chemical blowing agent in the plastics material. Despite having originally believed this to be a new technique, it appears that this may be known. In this basic technique, 1 used plastics material comprising free flowing polypropylene with a small addition of blowing agent, typically less than 5% and in the region of 1%, in accordance with the directions of the suppliers of the SAFOAM agent, Reedy International Corporation of Keyport, NJ, USA. In the thick wall portions, the agent causes foaming, whilst in the thin wall portions no foaming occurs. The degree of foaming can be controlled by adjustment of injection parameters such as pressure, time, temperature, quantity of plastics material and percentage of blowing agent in the material, such adjustments being routinely made in the set up of an injection moulding machine. I believe that a combination of the higher pressure required to force the material into the thin wall portions and the increased cooling rate in the thin wall portions inhibit the formation of foaming in the thin wall portions, whereas the lower pressure present in the thick wall portions and the greater bulk of plastics material in the thick wall portions requiring longer to cool allow foaming in these portions. Originally I believed that the foaming to fill the thick wall portions of the mould tool cavity needed to occur before opening of the mould. However I was surprised to discover that additional foaming can occur due to opening of the mould before cooling of the thick wall portions to solidification. My Original Method is based on such use of plastics material including blowing agent to allow foaming expansion to continue after at least partial opening of the mould in which the cup or other article is moulded. Figure 2 shows a cup formed in accordance with My Original Method. It has thin wall portions, namely a base 101 , a lower side wall 102 and an upper side wall 103, in which no foaming occurs. These portions have their wall thickness determined by the mould part gap. The cup also has thick wail portions, namely the corner 104, the band 105 and the rim 106, in which foaming occurs after mould opening so that the wall thickness is increased beyond that provided by the mould. Compared with the 1.2mm wall thickness in the band 5, using the same mould, a maximum band wall thickness of 3.2mm is achievable. It will be noted the outer contour of the band is curved, due to restraint of its upper and lower margins 106, 107 where the wall thickness alters to being thin. On the outer surface 108 between these margins, the band bows out. The outer surface of the rim 106 also bows out. In both these instances, and indeed at the coiner 104, the outer surface is substantially solidified on opening of the mould. At the time of the above referenced patent applications, I believed that the outer surface was able to stretch as foaming occurs in the still molten plastics material at the centre of the thick wall portions, to give the shapes shown in Figure 2. In the cup of Figure 1 , such foaming as occurs, does so against the constraint of the still closed mould In the cup of Figure 2, the constraint on the foaming is atmospheric pressuie and the skin tension of the outer surface The shape of the nm outer surface 109 is of particular note, in that the shape in which it originally solidifies is concave However on foaming, the concave surface has little pressure constraint on it and is blown out over-centre to the convex shape 109 This results in a maximum wall thickness of 2 7mm despite the vertical extent of the nm being less than that of the band It should be noted that the 3 1 thick thin wall thickness ratio, that is the ratio of thin wall thickness to thick wall thickness prior to foaming after mould opening, is exemplary only and the possible limits on the ratio have not yet been researched Turning now to Figure 3, the mould tool there shown has a cavity 1 1 and a core 12, the two being sepaiable at a joint line 13 The cavity has an injection point 14 and a spring closed air injection port 15 in the form of a poppet valve The core has an air injection port 16 opposite the injection port 15, with a free floating valve member closed by pressure in the moulding void On injection of the plastics matei ial mixture, the port 16 closes and the moulding void fills The injection paiametei s aie adjusted such that the material reaches the cup nm 6, without completely filling the void The blowing agent causes foaming in the thick wall portions Howevei this does not occur in the thin wall portions, where the pressure required to displace the material is higher and the cooling is quicker When time has been allowed for the plastics material to at least substantially solidify in the thin wall portions of the mould r,2',3', corresponding to the base 1, lower wall 2 and upper wall 3 of the cup and for some foaming in the thick wall portions 4', 5', 6' of the mould, coπesponding to the corner 4, band 5 and rim 6, and before the material has solidified in the thick wall portions, the mould is opened and air pressure applied to the port 15 This separates the moulding from the cavity, and together with shrinkage onto the core, allows withdrawal of the core with the moulding The outer surface skins 108, 109, 1 10 of the material (see Figure 2) at the thick wall portions 104, 105, 106 have at least substantially solidified, but does not constrain the blowing agent from generating sufficient pressure to create the shapes described above with reference to Figure 2 and as also shown in Figure 4. After a further delay to allow the moulding to cool, air is introduced via the port 16. This expands the moulding which is released from and then drops off the core. Figure 4 is taken from my International Application No. PCT/GB96/01706. At the time of the application, 1 had not realised the significance of the present invention. For this reason. Figure 4 shows the rim 106 abutting the joint face surface of the core part of the tool When sufficient blowing agent is added to the material of the cup and the cooling time is sufficiently short, for the rim to form to a circular cross-sectional shape, the height of the cup fore-shortens due to the rim skin blowing out and down as its length remains constant Thus Figure 4 does not teach the present invention. I believe that the blowing agent forces the moulding into good thermal contact with the mould at the thick wall portions before opening of the mould. This enhances cooling of the plastics material to form the skins of the thick wall portions. Further use of a carbon dioxide blowing agent which absorbs appreciable energy in foaming, that it cools the material on foaming, is advantageous in quickening cooling. However, both chemical and physical blowing agents using other gases and base polymers other than polypropylene are possible to use in My Original Method In British Patent Application No. 9621626.2, from which this application claims priority, I described an improvement of My Original Method. In the improvement, a substrate is placed into the mould prior to its closure in a position such that the plastics material mixture is injected onto a surface of the substrate, whereby after the withdrawal step the mixture foams on the substrate. This improvement is hereinafter referred to as "My Substrate Improvement". I have now realised that the foaming expansion mechanism described in respect of My Original Method is not exactly as I had originally believed, particularly as regards the extent to which the skin in the foamed thick wall portions stretches. The degree of stretch now appears to be very small and limited by solidification of the skin very shortly after the foaming pressure is applied to it. This effect is apparent with My Substrate Improvement where the lack of stretch, but change of cross-sectional shape pulls the substrate into a curve In application No 9621626 2, I anticipated the applicability of My Substrate Improvement to articles having no thin wall portions To help understanding of My Substrate Improvement, its preferred embodiment as described in the application No 9621626.2 will now be described with reference to Figures 5, 6 & 7 of the accompanying drawings, in which Figure 5 is a cross-sectional side view of a mould tool having a substrate placed in it prior to injection of plastics matenal. Figure 6 is a similar cross-sectional view of a formed article after foaming of the plastics material on a surface of the substrate and Figure 7 is a plan view of the formed article The mould tool has a cavity part 21 1 and a core part 212, defining a cuboid cavity 213 having a thin wall section 214, which extends over the major part of the square plan of the cavity, and a thick wall section 21 which extends along one edge of the square This tool will be understood to be intended for manufacturing samples. The square has 80mm sides The thin wall sections are 1 2mm thick and thick wall section is 4.2mm thick, that is the core part of the mould has groove 216 3mm deep and 10mm wide along one side of the square In formation of a sample 221 , an 80mm square of 0 2mm thick, polyethylene faced card 222 was inserted into the mould, with its face away from the cavity part. Foamable plastics mixture was injected into the cavity via a port 217 in the core part. The card was forced against the core part 21 1 , so that the plastics material formed a lmm thick skin 223 across the back of card except at the one edge 224 where the plastics material had an initial thickness of 4mm On opening of the mould, the sample was ejected and the plastics matenal in the edge allowed to foam to form a ridge 225, whose thickness increased to 9mm In so doing it caused the card to adopt a local curvature 226 The plastics thickness across the rest of the card remained 1 Omm, since the plastics matenal here had solidified prior to mould opening Although not descnbed in application No 9621626 2, initially I had formed the thick wall section groove 216 with a half round cross-sectional shape This did not foam to such a marked extent as I expected It was when the shape was changed to be rectangular that the degree of foaming described was achieved It should be particularly noted that the degree of foaming shown in Figure 7 is such that the cross- sectional shape of the ndge 225 is nearly ciicular and the card has taken up the local curvature 226 tending towaids the cnculai cioss-section I now believe this to result from the circumferential length of the skin around the thick wall section restraining the degree of foaming expansion The circumferential length around a rectangle is of couise greater than that of an inscribed circle The limitation on foaming expansion to the circumferential extent in transverse cross-section of the legion of the mould fiom which the foamed portion of the article is formed renders the piocess sui pnsingly predictable Therefore, when employing My Original Method, I now prefer to foam the thick wall portions, or the entire object where appropriate, to a substantially circular cross-section, at least where a high stiffness is required (and other constraints do not call for alternative shapes) Howevei , I should emphasise that the expansion to substantially circular ci oss-section is applicable beyond the differential wall thickness articles of My Original Method Thus in accordance with the present invention, I provide a method of forming an article via injection of plastics material into a mould, the finish formed article having at least one portion expanded, by blowing agent, to a shape which in cross-section is at least substantially circular over at least a substantial part of its circumference, the circumference having a predetermined extent, the method consisting in the steps of providing a mould tool defining in its closed state, between opposite parts, at least one region having a circumferential extent around the region in transverse cross- section substantially equal to the predetermined circumference, closing the mould and injecting a plastics material mixture comprising a basic polymer and a blowing agent into the mould tool, allowing the plastics material to skin adjacent thereof with an extent substantially equal to the predetermined circumference, withdrawing at least a portion of one part of the mould tool from the other part before the plastics material mixture has at least substantially solidified at the said region(s) of the mould tool to allow the mixture injected therein to expand by action of the blowing agent to the said at least partially, at least substantially circular shape and form the said portιon(s) of the finish formed article, and ejecting the article fiom the mould tool I refer to the article as skinned, but before expansion on mould withdrawal as a "pre-form" Thus my present invention includes My Substrate Improvement when expansion occurs to the said ciicular shape Whilst 1 can conceive that the expansion may occur after ejection of the article from the mould tool, normally the expansion will occur before this Preferably, the foaming expansion is to an extent whereby the substantially even radius of curvature of the skin is present over a major arc if not the entire circumference of the said portιon(s) Preferably the or each said region is wider than it is thick. In one alternative, the withdrawal step is delayed from a point in the cycle time when the expansion would be to an extent whereby a substantially even radius of curvature of the skin is present over substantially the entire circumference of the article in the said portion(s), whereby the skin stiffens to such extent that edges of the expanded portion substantially reproduce the corresponding edges of the mould region(s), whilst the intervening sides are bowed to at least partial, at least substantially circular shape, the said portion(s) tending to elliptical shape. In another alternative the expansion occurs against a mould tool surface, whereby the said portion of the finish formed article includes a face from which the transverse section of the portion extends with partially circular curvature It should be noted that the said portion(s) may comprise the entire article. Preferably the mould part gap at the said region(s) will be at least partially elongate, having a constant cross-section The said portion(s) may have a thin wall portion at one end. Additionally or alternatively, the portion(s) may have a thin wall portion at one side. The said region(s) of the mould may have a cross-sectional shape having one or more marked discontinuities of contour, such as a relatively tight radius of curvature, whereby the discontinuities provide a skin circumferential length which can be extended with a substantially even and greater radius of curvature on foaming expansion. Examples of such shapes are the rectangular shape of the groove of Figure 5 above and the tear-drop shape described below. It should be noted that shapes having an appreciable difference in transverse dimension taken normally to each other can be expected to fore-shorten in their longer dimension on foaming expansion. Alternatively, or additionally, the said region(s) may have a cross-section shape having at least one marked concavity, whereby the corresponding skin concavity can be inverted to provide at least one characteristic dimension of the cross-section of the portion which substantially increases on foaming expansion. Examples of such shapes are alphabetic shapes having marked concavities, such as C, H, I, M/W, U/V, X, Y. Where a shape having a sharp corner is used, such as a rectangle or an X, the sharp corners are preferably slightly relieved to avoid vestigial traces in the final skin shape The or each discontinuity is a tight radius of curvature which is tight compared with that of the transverse cross-section of the corresponding portion of the finish formed article Further, the discontinuity can be at a feature of the regιon(s) causing locally accentuated cooling whereby the feature is locally frozen into the skin at the at least partially, at least substantially circular shape of the said portion of the finish formed article Shapes having moi e than one concavity and a central part of the portion which can act as a i eservoir of liquid foaming material provide the gi eatest scope for increase in overall cross-sectional dimension In some embodiments, the or each said region is curved - with a local radius of curvature which is large in comparison with the dimensions of its cross-section - and defines a flange extending i dially and at least one laterally facing concavity, whereby the concavity inverts substantially laterally on expansion Preferably, the or each region defines a web from which the flange extends, the web remaining in cooling contact with one of the mould parts during the expansion The or each region can include a radially extending rib defining a groove in the or each web on expansion, the rib remaining in cooling contact with its groove Where the substantially circular ci oss-section foamed portion adjoins a thin wall portion, transitional curvatuie will l esult If the foamed portion is biased to be to one side of the thin section, by foi instance allowing the foaming expansion to occur with the thin section still in contact with a mould part, the foamed portion will have asymmetric transitional curvature joining opposite sides of it to the thin wall portion. The method of my present invention is particularly applicable to the production of cutlery In the preferred embodiments described below, thick wall/foamed portions extend along edges of the handles of the cutlery Preferably, the thick edge portions have thin portions between them, at least in the handles The thick portions may extend around the distal end of the handle Alternatively, the thin, central portions may extend to the distal end of the handles One or more further thick portions may extend longitudinally of the handle between the edge thick portions The thick portions, particularly the edge thick portions, may extend into the "cutlery" part of the cutlery By "cutlery" part is meant the blade of a knife or prongs of a fork or bowl of a spoon Further reinforcing thick portions may be provided at the "swan's neck" of a fork or spoon. By "swan's neck" is meant the transition between the cutlery part and the handle Further, the prongs of a fork may be formed as thick/foamed portions However, it is likely that other portions of the fork will be thicker/foamed to a greater extent In a recent development of the method of my present invention, I have now produced a senes of articles, wherein the said portion(s) are foamed to such extent that a void forms at the centre of the portion The article is in effect hollow in the portion(s) Where the portion - or one of them in the article - is to be handle, this is a particularly advantageous feature, in that it creates a handle having a body which can be readily gripped Further since the handle has a considerable moment of inertia, it is stiff and strong. I have also produced annular hollow portions in the same manner. These also can have considerable stiffness and strength If I use a soft plastics material, the hollow portion becomes readily compressible yet resilient due not only to the resilience of the material but also to the gas enclosed within the hollow. I envisage the portion being used as a seal. For instance, a small container with such a hollow portion around its rim could be an eye bath. Further, I have produced a series of articles in which three phases are present, namely thick and thin portions in accordance with my Original Method, in which the thin portions are unexpanded and the thick portions are expanded but not hollow, and thicker portions still where the opposite skins have separated to leave a hollow, central void. I refer to these phases as: i. Solid, ii. Cellular, iii. Hollow. There are a number of variables which determine whether a particular portion will become solid, cellular or hollow. For a given material, the determinant of solidity is whether the material has been cooled sufficiently to be solid throughout when the mould is open. No invariable rules can be given for this, nor indeed is it easy to make measurements of solidity on mould opening. It can be deduced by the finished article's wall thickness substantially reproducing the mould part gap. Cooling is enhanced by running the mould as cool as possible and delaying mould opening after injection for sufficient time for solidification. Excess cooling and/or delay in mould opening should be avoided to ensure that foaming expansion on mould opening can occur in the non- solid portion(s). The chief determinant of a cellular phase is that the cross-sectional shape of the region should be such as to allow the skin to change shape on mould opening, but to a limited extent only. For instance, if the initial skin shape - i.e. the shape of the skin as moulded before foaming expansion - is convex, there is less scope for its inflation to 2 1 use the term "cellular " in contrast to "foamed " , because both the " cellular " ' and "hollow" phases result from a process of foaming. permit expansion of the cross-section An extreme example is of a circular cross- section initial skin shape This can inflate only by stretching of the skin, whereby even if the central portion of the plastics material is still molten on mould opening, a small amount only of foaming expansion can occur Another example is of an equilateral cross-sectional shape This can inflate by bowing of the sides and moving inwards of the corners, whereby foaming expansion can occur and hence a cellular structure can result The chief determinant of a hollow phase is again cross-sectional shape of the region Creation of a hollow phase requires that the skin should be able to change shape to a much greater extent, such that the cellular structure expands so much that the individual cells burst For instance, a rectangular shape is likely to expand on foaming expansion to the extent of becoming hollow The likelihood of this increases with the aspect ratio - 1 e the ratio of the longer sides to the shorter sides - of the rectangle Again, concavity in the initial skin shape is likely to produce an inflation sufficient to allow foaming expansion to the hollow phase to occur A factor influencing the degree to which the skin will inflate is the composition of the plastics material Matenals which will stretch to a greater extent before being inhibited from further sti etching by ciystallinity and/or biaxial orientation will allow the hollow phase to develop to a gi eatei extent However, my experience to date in working primarily with polypropylene materials is that cross-sectional shape is a more important design criterion than matenal nature as regards the creation of hollow or cellular phases Whilst the basis of my development has been to produce articles or parts of articles having substantially ciiculai cioss-section, I can envisage uses where a flattened ciicular cioss-section would be useful Particularly, where a greater moment of inertia in one plane than an orthogonal one is required, as for instance in knife handle To produce such a shape, I envisage partially opening the mould and allowing the expansion to occur against the mould surfaces Alternatively, it is possible to produce cross-sectional shapes, which whilst tending towards circular are intermediate between the initial skin shape and a circular cross-section For instance if 5% blowing agent and Vi second cooling time is required to expand a rectangular initial shape to circular, 3% blowing agent and V second cooling time is likely to result in insufficient fluidity in the centre of the moulding and flexibility in the walls for the cross-section to expand to being fully circular The long sides of the rectangle may bow out to have a 5 substantially even radius of curvature However the constraints from the short sides and the corners between the sides may be such that the cross-sectional shape is tending to elliptical, or indeed some more complex mathematical shape At this stage, I have not had the opportunity to analyse the exact curvature ) However, I believe the shape to be tending to be substantially circular or at least substantially elliptical, because if sufficient blowing agent - or other foam producing additive - is included in the plastics matenal and the mould is opened as soon as the skin has foi med then a substantially cii cular cross-section will result if the initial shape is such as to allow this I therefore think in terms of this part of the development having been taken as far as the foaming producing an expanded cross-section having convex curvature tending towards cii culai , which is absent in the initial skin shape, and a hollow phase within the skin I would emphasise that the skin sui i oundmg a hollow phase is likely to be at least partially cellular, with the cell size increasing towards the hollow phase There are two factors which appear to have an effect on the extent to which a hollow phase forms Fii stly, I believe that in certain circumstances heat soak has an influence By heat soak, 1 mean that the moulding is sufficiently rigid - due to cooling of the skin - on mould opening that expansion is not immediate Then after a perceptible delay, the moulding grows in size This appears to be caused by some of the heat in the interior of the moulding, where the material is still molten or at least readily extensible, being transferred out to and warming the skin, softening it and/or the melt layer thickening The softening/thickening reaches a point where the skin can no longer resist the expansive, internal pressui e and the hollow or cellular phase(s) form This softening is of a diffuse natui e It does not necessarily result in certain moulded features disappeanng fi om the final article Heat soak can be utilised to encourage expansion to initiate at a specific points, by mci easing the cross-section, typically centrally Once expansion has been initiated it will tend to spread across the moulding The second factor is the converse of heat soak, namely the extent to which the moulding is cooled More cooling will tend to occui at the edges of a moulding having an appreciable aspect ratio Accentuating cooling can cause features to be "frozen into" the final article Certain features will tend to be cooled to a greater extent due to tapering to an edge Such featui es ai e more likely to be frozen in Within the scope of mv development is that I can produce articles having no solid nor cellulai phases except in the skin 1 can also pi oduce articles which have solid and hollow phases but no sepai ate skinned cellulai phases without hollow interioi s My mle of thumb is that if the degree of expansion - l e the increase in transverse dimension - exceeds 5mm, a void will form My present invention can be used for forming articles which do not have respective concave and convex sides, but rather are symmetrical about a central plane, for instance a knite It may be thought that the mould tool foi such articles is not properly to be i egarded as having a coi e part and a cavity part but l ather has two opposite complementaiy mould parts 1 believe that the man skilled in the art will refer to such a mould as having coi e and cavity parts by analogy with conventional usage Nevertheless, for the avoidance of doubt as to the scope of the present invention and My Original Method, both covei the use of symmetrical moulds, having mirror image mould cavity defining parts Use of such a mould is not descnbed in my International Application No PCT/GB96/01706 which was published on 6 th Feb ary 1997 Such use was descnbed in Applications Nos 9624162 5 and 9700138 2, dated 20 lh November 1996 and 6 th January 1997 respectively, from which this application claims priority Thus a claim to such use is valid in this application and is included in the claims hereof Thus according to this aspect of the invention there is provided: A method of forming an article via injection of plastics material into a mould, the finish formed article having thin wall portion(s) and thick wall portion(s), the thick wall portion(s) being at least partially foamed, the method consisting in the steps of: providing a mould tool defining in its closed state, between its two opposite parts, narrow gap portion(s) whose mould part gap is to be substantially reproduced in the thin wall portion(s) of the article and wide gap portion(s) whose mould part gap is less than the thickness of the thick wall portion(s) of the finish formed article, the two opposite mould parts being symmetrical; closing the mould tool to define the narrow and wide gap portions; injecting a plastics material mixture comprising a basic polymer and a foam producing additive into the mould tool; allowing the plastics material mixture to at least substantially solidify in the narrow gap portions of the mould tool to produce the thin wall portions of the finish formed article; withdrawing at least a portion of one part of the mould tool from the other part before the plastics material mixture has at least substantially solidified in the wide gap portion(s) of the mould tool to allow the mixture to expand by foaming and form at least some of the thick wall portion(s) of the finish formed article; and ejecting the article from the mould tool. Further, it may be thought that an article such as a piece of cutlery as opposed to a container is not properly to be regarded as having a thick "wall" portion and a thin "wall" portion. I believe that the man skilled in the art will realise that the term "wall thickness" means the "gauge thickness" (a common term for the thickness of material) or indeed merely the "thickness" of the material, both as defined by the mould part gap and measured in the finish formed article. It is known to add a variety of fillers to plastics materials used in injection moulding processes. Generally they provide strength and/or hardness improvement, or merely provide economy by bulking the relatively more expensive plastics materials. However use of fillers in the plastics materials for the present invention provides unexpected advantages. Accordingly I prefer to add fillers to the plastics material mixture used in my present invention and indeed My Original Method. Use of talc in particular provides advantages in that it causes the formation of complete voids in the foamed plastics material. This is believed to be caused by talc comprising calcium carbonate platelets. These have relatively sharp edges, which sever the bubble walls formed internally of the foaming plastics material. The result is the formation of a complete void, with a rough internal structure. In turn this causes greater expansion, in that the removal of the internal foam structure allows greater expansion of the thick wall portions of the finish formed article. Greater expansion provides greater transverse dimension and hence greater stiffness. Further 1 have noted that the fillers tend to migrate to the outer surface of the thick wall portions. Again this increases stiffness. Furthermore, I have noted that use of fillers increases the time over which foaming occurs This results in greater dimensional expansion, which in turn enhances stiffness. 1 believe this effect to be caused by the plastics material incorporating fillers having a greater thermal capacity. This slows cooling and hence allows foaming over a longer period. I believe the following fillers to be advantageous: Talc Chalk Alumina Glass spheres Glass and carbon fibres. To help understanding of the invention, specific embodiments thereof will now be described by way of example and with reference to Figures 8 to 12 of the accompanying drawings, in which Figure 8 shows a l espective moulded - 8(ι) - and foamed - 8(n) - section for a cutlery handle, Figure 9 shows similar sections for another cutlery, Figure 10 shows similar sections for an arm of a garment hanger, Figure 1 1 shows similai sections for a reinforcing rib for a vehicle door pocket, Figure 12 shows similai sections for a reinforcing ridge for a vehicle skin panel, Figui e 1 3 shows a gai ment hangei manutactui ed in accordance with my in present invention with sci ap details showing u oss-sectional shape, the hanger having different left and right ai ms. Figure 14 shows in ci oss-section an eye bath in accordance with the invention, Figure 1 5 shows a side view of a knife manufactured in accordance with my present invention, Figui es 1 5a and 1 5b ai e i espective cross-sectional views on the lines A and B in Figuie I 5 of the knife showing foamed sections, Figures 16a and 1 b ai e similar views of the "as-moulded" sections prior to foaming expansion, Figure 17 shows a side view of a fork manufactured in accordance with my present invention Figui e 1 8 shows a plan v iew of the foi of Figui e 1 7 Figui es 1 a 1 b and 1 c ai e i espective cross-sectional views on the lines A, B and C in Figure 18 of the toi showing foamed sections Figui es 20a, 20b and 20c ai e similai views of the "as-moulded" sections prior to foaming expansion, Figure 21 shows a plan view of a spoon manufactured in accordance with my present invention, Figui es 22a and 22b ai e i espective cross-sectional views on the lines A and B in Figure 21 of the spoon showing foamed sections, Figures 23a and 23b ai e similar views of the "as-moulded" sections prior to foaming expansion. Figure 24 shows a plan view of another spoon manufactured in accordance with my present invention Figure 25 is a plan view of the spoon of Figure 24, Figures 26a and 26b ai e I espective cross-sectional views on the lines A and B in Figure 25 of the spoon showing foamed sections, Figures 27a and 27b are similar views of the "as-moulded" sections prior to foaming expansion. Figure 3 1 is a side view of a fork as moulded, I e of the mould cavity shape, with a series of views showing cross-sectional shape, Figure 32 is a similai side view of the finish formed fork with the same series of cross-sectional views showing the shape after foaming expansion and an enlarged scrap view of one cross-section Figure 33 is a plan view of the fork, Figure 34 is a ci oss-sectional plan view of a mould for a handle, Figure 35 is a ci oss-sectional view on the line XXXV-XXXV in Figure 34 for the mould, and Figure 36 is plan view of the handle Figure 37 is a side view of the handle Figure 38 is a cross-sectional view of the handle at the position corresponding to the line XXXV1I I-XXXVI II, showing a circular cross-section, Figure 39 is view similar to Figui e 37 of a modified handle being formed to flattened shape. Figure 40 is anothei similar view of an elliptical handle shape, and Figures 4 1 42 and 43 ai e views similar to Figures 17 19 and 20 of another fork, and Figui e 44 is a ci oss-sectional view of a pie-form and a corresponding expanded section of a knife blade It should be noted that much of the following description is merely of cross- sectional shapes of the mould ι egιon(s) whose mould part gap is less than the thickness of the said portιon(s) of the finish foi med article and the con esponding shapes of the finish formed articles Moulding of the articles and their foaming expansion can be carried out in accordance with My Original Method, as exemplified with reference to Figures 2,3, & 4 Turning first to Figure 8, the mould shape 8(i) in which the cutlery handle skins has double tear drop 381,382 shape, with a narrow, intervening thin wall portion 383 at the thin ends 384 of the tear drops These taper 385 out to domed ends 386 The foamed shape 8(ii) retains the intervening thin wall portion 383 However the tapered portions 385 have blown outwards, adopting a substantially constant radius of curvature 387 The domed ends 386 have had their radius of curvature reduced to that of the blown tapei s The oveiall height 388(ι), 388(H) of the cross-section has foreshortened on foaming expansion, whilst the width 389(ι), 389(H) has increased At the junction of the foamed skins 390 and the thin wall portion 383, the opposite skins have been pulled pulled apart and bent so as to extend locally away from each other at the limit of the extension of the still liquid central portion of the plastics material on mould opening The point at which this occurs in the finished article can be controlled by the degree of cooling of the thin wall portion and the skins, and the timing of mould opening Figure 9 shows a mould shape 9(ι) based on the letter W, with a thin wall portion 392 joining two half round thick wall portions 393',393" Each of these has a mould part gap approximately double that of the thin wall portion The corners 394 at the ends of the concave sides 395 of the half round portions are radiused On foaming expansion, the concave side skins 396 pop ovei -centre to become convex Whilst symmetry of the final shape with respect to the medial plane 397 of the thin wall portion, is more definitely assui ed if the skin length 398 from the thin wall portion via the initially convex skin 399 to the remote corner 400 is the same as that via the concave skin, this is not necessary The convex skin length 399 is likely to be longer, with the result that the point 400 is drawn out of the medial plane The skin can be expected to stretch to a limited extent only, so that the radius of curvature 401 of the finish formed handle will be appioximately that of the original convex skin Figure 10 shows a mould shape 10(ι), which is based on the letter X It has no thin wall portion Each of the four arms 402 of the X has a smooth, tightly radiused end 403. Their roots 404 merge with a larger radius curvature 405, providing a central reservoir 406 of liquid plastics material able to foam after skinning. It will be appreciated that this mould shape provides a relatively large overall circumferential length, so a relatively high degree of volumetric expansion is possible to the foamed shape 10(ii). This is advantageous in providing a rigid arm for a product such as a garment hanger. It should be noted that all three of the embodiments just described can be incorporated in elongate articles of a length which can be chosen at will. In the case of the cutlery handles, thin wall portions will be incorporated at the end of the handle to provided a blade, for instance for a knife The garment hanger, on the other hand, may not have a thin wall section. The cross-sectional diameter and the curvature of the central axis of the elongate section can be chosen to suit the garment. It is anticipated that the section can be branched to provide the hook of the hanger. Figure 1 1 shows a mould shape 1 l (i) for a reinforcing rib for a vehicle door pocket. The shape is based on the letter Y, with tightly radiused ends 4 1 1 and concave sections 412 to provide for appreciable expansion on foaming. The foamed shape 1 l(ii) is symmetrical with respect to a thin wall portion 413, providing the wall of the pocket. If this is to be biased to one side, for instance the inside of the pocket to provide enhanced grippability, the foaming expansion can be arranged to occur whilst the thin wall is still in contact with the outside shape defining part of the mould. For this, the Y 1 l (iii) may be biased inwards so that the mould face 414 can be arranged to provide a flat surface for the foamed rib I l (iv) to form against. Figure 12 shows a mould shape 12(i) for forming a rib 421 on the inside of a thin wall car body panel 422. The mould shape is generally M shaped, with a central concavity 423. This passes over-centre on foaming expansion 12(ii), whereby the rib balloons away from the panel. It should be noted that the rib has a semi-circular shape, which is nevertheless of substantially constant radius of curvature. As mentioned above, the work which 1 have carried out on My Original Method has been with polypropylene, using an endothermic blowing agent releasing carbon dioxide gas. Polypropylene is a material which is amorphous above 140°C, its crystallisation temperature. I prefer to inject it at 220°C, so that it flows very readily into the mould and is free to expand in the mould cavity to the extent that this is under- packed. Skinning involves cooling of the material to below the temperature at which crystallisation can occur. I believe that as soon as the skin is urged to stretch by the foaming expansion after mould part withdrawal, the skin is liable to crystallise. Since the pressure which can be exerted by carbon dioxide is limited (it liquefies at 2.24 bar at room temperature), the crystallisation resists substantial stretching of the skin. Even if crystallisation is not the mechanism inhibiting skin stretching, the solidification of the skin does this. The invention is not restricted to polypropylene. With other materials, which are less prone to crystallisation, more skin stretch may be experienced. Nevertheless, this does not affect the desirability of forming the original skin with excess circumferential length and expanding this to at least part circular form. Referring to Figure 13, the hanger there shown has a hook 450, a right arm 451 and a left arm 452. These limbs are all expanded in accordance with the invention to include portions expanded to circular cross-section and having central voids. The hook and right arm have generally C-shaped pre-form shapes 4501 ,451 1, which expand to circular shapes 4502,45 12. The left arm has a flatter pre-form cross-section 4521, with a central thin land 453. On either side of the land the pre-form has thicker wings 454, which thicken outwards, with a circular contour 455 on the same side as the land 453. The opposite side 456 is complementarity concavely shaped, with a curvature such that it can expand out to continue the convex curvature 455. On expansion, the bi-lobe shape 457 forms, with two circular edges 458 and the central land 453 tangential to these. Referring to Figure 14, the article there shown is an eye bath 470, which is elliptical in plan - not shown. The bath has a thin wall 471 and a hollow annular (subject to the elliptical shape) rim 472. The latter is shown at one side of the Figure, whilst the tear drop pre-form shape 473 is shown at the other side. This expands to hollow circular cross-section with a circumferential length 474 equal to that of the tear drop 475 This results in a slight fore-shortening 476 of the height of the eye bath from the height of the pre-form The eye bath is of flexible polypropylene material, where the nm can deform to the eye socket and seal in eye wash solution in use Refei nng to Figui e I 5, the knife 500 thei e shown has a blade 501 with a thin wall/gauge thickness 502 tapei ing down to a cutting edge 503, see Figure 15a The back of the blade has a thick foamed edge 504 of substantially circular cross-section This starts at the distal end of the blade and continues into the handle 505, round the distal end 506 of the handle and terminates at a point 507 where the handle has widened to blend with the blade The handle has a thin web 508 extending along its full length It will be appreciated that the knife has high stiffness in bending, not only in the normal cutting plane, due to the I beam configuration of the handle, see Figure 15b In the perpendicular plane, the foamed back 504 of the blade and the foaming expansion 509 to the point 507 provide substantial stiffness The foaming expansion along the handle and at its distal end provide a comfortable feel to the knife Turning to Figui es 16a and 16b, the cross-sectional shape of the mould cavity for producing the knife is shown It will be noted that at the edge of the foamed part, the thick section has a peripheral surface 5 10 which is perpendicular to the central plane 5 1 1 of the knife This plane is the joint plane of the mould for the tool, which is symmetrical about the joint plane The thick section tapers 5 12 to the central thin wall of the knife handle and of the knife blade, to provide an adequate surface skin to inflate on foaming expansion to substantially cii cular cross-section It should be noted that the cross-sectional height 5 13 of the handle is greater as moulded than after foaming expansion 5 14, due to foi e-shoitenmg of the thick portions on foaming expansion Figures 17 and 18 show a fork 520 It is of largely conventional shape, with prongs 521, a swan neck 522 and a handle 523 The prongs are foamed The outer prongs 521' and the edges 524 of the swan neck and the edges 525 of the handle have a continuous foamed rib 526 extending to and terminating at the distal end 527 of the handle. The foaming expansion of the inner two prongs 521 " terminates at their root in a thin wall palm section 528 of the fork. At the swan neck 522, a central foamed rib 529 provides added stiffness. This rib extends into the handle and divides into two ! subsidiary central ribs 529'. The handle thus has three thin wall webs 530. To give the handle a comfortable feel, it is curved in transverse cross-section. Figures 19a, 19b, 19c, 20a, 20b, 20c show typical foamed and corresponding as moulded - prior to foaming - cross-sections. ) Figure 21 shows a spoon 540. It has foamed edges 541 extending from its bowl 542, through its neck 543, and along its handle 544 A central foamed rib 545 extends from the bowl along the handle, to give added stiffness, particularly to the neck. Figures 22a, 22b, 23a, 23b, show typical foamed and corresponding as moulded - prior to foaming - cross-sections. Figures 24 and 25 show another spoon 550 This has a modified invert channel section handle 55 1 , with lateral flanges 552, which are of thin wall thickness, and a foamed central web 553 Figures 26a, 26b, 27a, 27b, show typical foamed and corresponding as moulded - prior to foaming - cross-sections. Referring to Figure 3 1 , it should be noted that not only is the shape shown that of the mould cavity, it is also the shape of a fork moulded in the cavity without foam producing additive; whereas the shape of the fork shown in Figure 32 is one from the same mould cavity with foam producing additive in the plastics material. In general terms, the fork has a set of prongs 1001 , a swan neck 1002 and a handle 1003. The prongs 100 1 have extensions 1004 into the swan neck, which has web areas 1005 between the extensions The extensions 1042, 1043 of the inner two prongs 1012, 1013 extend back to the forward end of the handle Similarly, the extensions 1041 , 1044 of the outer two prongs 101 1 , 1014 extend back peripherally of the swan neck to the handle. In addition, the two outer prongs 101 1, 1014 have extra extensions 141 1, 1441 , which branch from the prongs close to their outer ends and extend back into the swan neck between the peripheral extensions 1041 , 1044 and the inner prongs' extensions 1042, 1043 The extra extensions taper out before reaching the handle As apparent from the cross-sectional views in Figure 31 , the prongs taper to pointed ends 1006 The inner prongs 1012, 1013 and their extensions 1042, 1043 are of constant, equilateral mangle ci oss-section behind the tapers 1007 of the ends 1006 The web areas on eithei side of the extensions 1042, 1043 ai e an order of magnitude thinner than the ci oss-sectional dimensions of the extensions, and so can be ignored as regards effect on the foamed shape The extra extensions 141 1 , 1441 also are of equilateral cross-section The outer prongs 101 1 , 1014 and their extensions 1041 , 1044 are of right angle triangle shape of height - from the web areas - equal to the inner prongs The handle shape is more complex Essentially it is square edged 1081 , with narrow top and bottom returns 1082, 1083 extending in from the edges at right angles. The mam extent 1084 of the top is symmetrically ramped up to a central rounded top ridge 1085 The bottom is of complementary shape 1085, except that it has a central flat 1086 The top is thus convex and the bottom is concave Referring now to Figure 32, the foamed shape of the fork is as follows: The very ends of 1006 of the prongs are of solid plastics material Where the tapers 1007 reach a certain thickness, foaming is present in their centre, although without any apparent change in shape h orn the Figure 3 I shape However where the full section is reached, surfaces of the prongs and their extensions bow out, as the internal foam pressure inflates them to maximise the internal volume of the cross- section However the initial skin shape gives little scope for marked increase in the internal volume The result is that almost the entire extent of the prongs and their extension is of cellular phase The first exceptions are the points 1006 The second exceptions are the regions of intersection of the outer prongs 101 1, 1014 with their extra extensions 14 1 1 , 144 1 At the mtei sections, i egions 1040 of sharp convexity are formed in the original skin, which enables a substantial expansion in the internal volume of the moulding at the i egions Figure 32 shows that this results in a substantially circular cross-section 1401 with a central void or hollow 1402 developing The original skin shape was complex, with sharp features These are not entirely smoothed out, so that the cross-section has discontinuities in the circular shape The handle also has a concavity in its original skin shape, in the form of the shape 1085 Thus this can invert to substantially circular cross-section on foaming expansion and a central hollow 1800 develops The width of the handle is much greater than the width of the outer pi ongs at the junction with their extra extensions Thus the handle expands to a much biggei diametei Whilst the hollow 1402 has a void of the same oi dei ot ci oss-sectional dimension as the skin thickness, the central void in the handle is an oidei ot magnitude larger than the skin thickness As shown in the detail to cross-section vi-vi, the right angle features in the initial skin shape between the edges 108 1 and the returns 1082, 1083 remain in final cross-section but the edges and l etui ns become local concave features as a result of the overall inflation ot the ci oss-section Measui ements have indicated a 3% sti etch only from the skin of the handle as moulded to its Figui e 2 state, when using polypropylene Refen ing now to Figui es 34 & 35, the mould there shown is for a handle for an implement whose opeiative portion is not shown The mould cavity has a large diameter distal end 200 1 and a small diametei pi oximal end 2002 at which the mould would be extended foi the non-shown operative portion of the implement Between the ends, the cavity has sti ight sides 2003 which appi oach each other The mould has a unifoi m gap 2004, conesponding to the wall thickness of a handle to be moulded if plastics matenal without foam producing additive is used Small central and peripheral grooves 2005,2006 are cut into the two parts 2007,2008 of the mould The handle 2010 moulded with foam producing additive is shown in Figures 36, 37 & 38. On injection, the skin 201 1 is formed at the internal surface of the cooled mould, which imparts the initial skin shape. On opening of the mould prior to complete cooling of the plastics material at the centre of the moulding, the material expands by foaming to the shape shown. It should be noted that the skin does not appreciably extend in length or surface area; rather, it is inflated to shape. The skin is smooth on the outside, with no foam bubbles forming at the surface, because this solidifies whilst the moulding pressure is maintained and inhibiting foaming. However within the skin, bubbles or cells 2012 are present. These increase in size until the central void 2013 is reached. Throughout most of its length, the handle has a circular cross-section as shown in Figure 38. The outer surface is not truly circular, having the shape of the grooves 2005, 2006 - albeit somewhat deformed to the circular shape. Where the cross-section is circular, the sides 2003 are straight; although it should be noted that they are closer together than originally. At the large diameter end 2001 , the curved shape into which the skin is formed initially inhibits the full circular cross- section from developing. Thus the thickness 2014 of the handle at its centreline progressively decreases close to the end. The result is that the sides 2003 curve gently out 201 5 to meet the curvature of the end. The thickness 2014 begins to decrease from the same position as the sides curve out. Similar effects occur at the small diameter end 2002, but they are not so prominent. Turning now to Figure 39, the effect on the cross-sectional shape at the longitudinal centre of the handle can be seen, when the mould parts 2007,2008 are opened to a limited extent 2020 only until the handle has set. It expands against the mould parts, which impress their central shape on the handle, that is to say the flat surface of the mould part 2008 and the similar surface with the central groove 2005 in the case of the other mould part 2007. This has the advantage of spreading the edges 2003, with consequential increase in moment of inertia; but the disadvantage of increasing cycle time due to the time taken in holding the mould parts partially withdrawn for the expansion to occur. A similar effect can be achieved with expansion in free air by reducing the amount of foam producing additive in the plastics material mixture, as shown in Figure 40. In this case the cross-sectional shape does not develop to a full circular shape, but approximates to an elliptical shape 2030. This shape can be produced with the same cycle time as with the shape of Figures 35, 36 & 37. Turning now to Figures 41 , 42 and 43, there is shown another fork 2101 with a pronounced curvature of its swan neck 2102, with a local radius of curvature 2103. A characteristic of the invention particularly where voids are blown, is that the relevant portion of the article tends to straighten, as with inflation of a child's balloon. This fork incorporates edge flanges 2104 in the swan neck, which extend radially, that is transversely of a wall 2105 extending through the swan neck. The pre-form - Figure 43 a - of the swan neck has a concavity 2106 facing in from each flange and extending along a narrow web 2107 between each flange and the wall 2105. On expansion, the concavity's skin passes over centre. However, since it is facing essentially laterally and its height in radial direction does not increase, there is little tendency for the expansion to straighten the swan neck. This effect is enhanced if the fork is held on the tool whilst the expansion occurs, with the skin 2 108 of the web and flange in contact with the tool being kept relatively rigid by cooling from the tool. The central tines 21 10 of the fork also incorporate curvature limiting flanges 21 1 1, at least at their roots. These flanges have webs 21 12 and lateral concavities 21 13 at each side. Further, the webs have a groove 21 14 - formed by a rib in the tool - extending into the flange. This groove is kept cool during expansion; so that not only does it not invert and expand, but also the groove helps to maintain the curvature of the tines. Turning on to Figure 44, there is shown a pre-form and expanded cross-section of a knife blade. The pre-form is stepped 2201 in thickness from the wall thickness of the blade 2202. The back 2203 of the blade is of C-shaped cross-section. On expansion, a void 2204 develops at the back, with the skins 2205 of the thicker wall being pulled apart as far as the step 2201 . With excess of blowing agent and a relatively short cooling time before the expansion is initiated, the expansion will be to circular cross-section with the step 2201 being within the circular circumference. However, control of the blowing agent quantity and cooling time, the expanded cross- section as shown will develop, with a semicircular shape tapering in to the step 2201. The void 2204 develops at the back and a cellular phase is present between the skins 2205, at least adjacent the step 2201 .

Claims: Claims 1 A method of foi ming an article via injection of plastics matenal into a mould, the finish formed article having at least one portion expanded, by blowing agent, to a shape which in cross-section is at least substantially circular over at least a substantial part of its circumfeience the cu cumference having a predetermined extent, the method consisting in the steps of providing a mould tool defining in its closed state, between opposite parts, at least one region having a circumferential extent around the region in transverse cross- section substantially equal to the pi edetei mined circumference closing the mould and meeting a plastics material mixture comprising a basic polymer and a blowing agent into the mould tool allowing the plastics matenal to skin adjacent thereof with an extent substantially equal to the predetermined circumference, withdrawing at least a portion of one part of the mould tool from the other part before the plastics matenal mixtui e has at least substantially solidified at the said regιon(s) ot the mould tool to allow the mixture injected therein to expand by action of the blowing agent to the said at least partially at least substantially circular shape and form the said portιon(s) ot the finish foi med article and ejecting the article ti om the mould tool 2 A method of toi mmg an article as claimed in claim 1 wherein the expansion occurs after ejection ot the article h orn the mould tool 3 A method of foi ming Λn article as claimed in claim 1 wherein the expansion occurs befoi e ejection ot the article ti om the mould tool 4 A method of foi ming an article as claimed in claim I claim 2 or claim 3, wherein the expansion is to dn extent vvhei eby a substantially even radius of curvature of the skin is present over a major arc or preferably the entire circumference of the said portιon(s) 5 A method of forming an article as claimed in claim 1, claim 2 or claim 3, wherein the oi each said l egion is wider than it is thick and the withdi awal step is delayed from a point in the cycle time when the expansion would be to an extent whereby a substantially even l adius ot cui vature of the skin is present over substantially the entn e cii cumfei ence of the article in the said portιon(s), whereby the skin stiffens to such extent that edges of the expanded portion substantially reproduce the corresponding edges of the mould regιon(s), whilst the intervening sides are bowed to at least partial, at least substantially circular shape, the said portιon(s) tending to elliptical shape 6 A method of forming an article as claimed in claim 1 , claim 2 or claim 3, wherein the expansion occurs against a mould tool surface, whereby the said portion of the finish formed article includes a face from which the transverse section of the portion extends with partially circular curvature 7 A method of forming an article as claimed in any preceding claim, wherein the said portιon(s) comprise the entire finish formed article 8 A method of foi ming an article as claimed in any one of claims 1 to 7, wherein the said poι tιon(s) ad]om thin wall poι tιoπ(s) ot the article with transitional curvature occurring between the expanded poι tιon(s) and the thin wall portιon(s), the mould withdrawal having occui i ed aftei the plastics matenal has substantially solidified throughout the thin wall portιon(s) of the article 9 A method of foi ming an article as claimed in claim 8, wherein the expanded portιon(s) are biased to one side ot the thin portιon(s) by contact with a mould part whilst the expansion occui vvhei eby the transitional curvature is asymmetric with respect to the thin wall poι tιon(s) 10 A method of foi ming an article as claimed in any preceding claim, wherein the said regιon(s) and the said poιtιon(s) ai e at least partially elongate, having a constant cross-section 1 1 A method of forming an article as claimed in any preceding claim, wherein the said regιon(s) of the mould may have a cioss-sectional shape having one or more marked discontinuities of contoui 12 A method of foi ming an article as claimed in claim I 1 wherein the or each discontinuity is a shai p cornet , the sharp coi nei pi eferably being slightly relieved to alleviate vestigial traces in the final skin shape 13 A method of foi ming an article as claimed in claim 1 1 , wherein the or each discontinuity is a tight i adius of cm vature which is tight compared with that of the transverse ci oss-section ot the corresponding portion of the finish formed article 14 A method of foi ming an article as claimed in claim 1 1 , claim 12 or claim 13, wherein the discontinuity is at a feature of the regιon(s) causing locally accentuated cooling whereby the featuie is locally frozen into the skin at the least partial, at least substantially circular shape of the said portion of the finish formed article 15 A method of forming an article as claimed in any preceding claim, wherein the said regιon(s) have an appreciable diffeience in tiansverse dimension taken normally to each other, whereby the longei transverse dimension foie-shortens on expansion 16 A method of forming an article as claimed in any preceding claim, wherein the said regιon(s) have at least one marked concavity, whereby the corresponding skin concavity is inverted on expansion to provide at least one characteristic dimension of the cross-section of the regιon(s) which substantially increases on expansion 17 A method of forming an article as claimed in claim 16, wherein the or each region includes a plurality of concavities and a cential part of the region acting as a reservoir of molten plastic matenal mixtuie foi the expansion 18 A method of foi ming an article as claimed in any preceding claim, wherein the or each said region is curved - with a local radius of curvature which is large in comparison with the dimensions of its cross-section - and defines a flange extending radially and at least one laterally facing concavity, whereby the concavity inverts substantially laterally on expansion 19 A method of foi ming an article as claimed in claim 18, wherein the or each region defines a web tiom which the flange extends, the web lemaining in cooling contact with one of the mould parts during the expansion 20 A method of forming an article as claimed in claim 19, wherein the or each region includes a radially extending rib defining a groove in the or each web on expansion, the nb remaining in cooling contact with its groove 21 A method of foiming an article as claimed in any preceding claim, wherein the said portion(s) ai e expanded to such extent that a void forms centrally thereof, and the skin surrounding the void is pieferably cellular 22 A method of foiming an article as claimed in claim 21, wherein the withdrawal step allows heat soak from a central part of the portιon(s) to warm and soften the chilled skin of the poιtιon(s), which formed prior to withdrawal, and/or thicken a melt layer within the portιon(s), wheieby expansion to form the void occurs after a perceptible delay 23. A method of forming an article as claimed in claim 22, wherein the said region(s) include a local thickening of cross-section to increase locally the heat soak effect and initiate the expansion. 24. A method of forming an article as claimed in claim 21 or claim 22, wherein the or each region and its corresponding portion is elongate, with expansion initiating at one point and spreading along the corresponding portion(s) of the article. 25. A method of forming an article as claimed in any preceding claim, wherein the mould tool includes at least one other region having a lesser circumferential extent, whereby on mould withdrawal and expansion, the one region(s) expand to such extent that a void forms centrally thereof and the other region(s) expand only to such extent that a cellular structure forms centrally thereof. 26. A method of forming an article as claimed in any preceding claim, wherein prior to closure of the mould a substrate is placed with one side against the surface of the mould at the said region(s), whereby on injection of the plastics material mixture the latter covers the opposite side of the substrate and on withdrawal the plastics material mixture expands at the opposite side of the substrate, drawing the substrate into a curve towards this side. 27. A method of forming an article as claimed in claim 26, wherein the mould defines narrow and wide gap portions, the latter being at the said region(s) and the substrate extends into the narrow gap portions, and the withdrawal step is delayed until the plastics material mixture has at least substantially solidified in the narrow gap portion(s), whereby the expansion of the plastics material does not curve the substrate here. 28. A method of forming an article as claimed in any preceding claim, wherein the mould tool has two symmetrical mould parts. 29. A method of forming an article via injection of plastics material into a mould, the finish formed article having thin wall portion(s) and thick wall portion(s), the thick wall portion(s) being at least partially foamed, the method consisting in the steps of: providing a mould tool defining in its closed state, between its two opposite parts, narrow gap portion(s) whose mould part gap is to be substantially reproduced in the thin wall portion(s) of the article and wide gap portion(s) whose mould part gap is less than the thickness of the thick wall portion(s) of the finish formed article, the two opposite mould parts being symmetrical; closing the mould tool to define the narrow and wide gap portions; injecting a plastics material mixture comprising a basic polymer and a foam producing additive into the mould tool; allowing the plastics material mixture to at least substantially solidify in the narrow gap portions of the mould tool to produce the thin wall portions of the finish formed article; withdrawing at least a portion of one part of the mould tool from the other part before the plastics material mixture has at least substantially solidified in the wide gap portion(s) of the mould tool to allow the mixture to expand by foaming and form at least some of the thick wall portion(s) of the finish formed article; and ejecting the article from the mould tool. 30. A method of forming an article as claimed any preceding claim, wherein one or more filler is added to the plastics material mixture. 3 1. A plastics material article comprising an injection moulded pre-form expanded by blowing agent mixed with the plastics material to have at least one internal void. 32. A plastics material article formed by the method of any one of claims 1 to 30. 33. A plastics material article as claimed in claim 3 1 or claim 32, wherein the entire article has been expanded by blowing agent. 34. A plastics material article as claimed in claim 3 1 or claim 32, wherein an entire part of the article has been expanded by blowing agent. 35. A plastics material article as claimed in claim 3 1 or claim 32, wherein a part of the article has two or more portions which have been expanded by blowing agent and non-expanded, portion(s) therebetween, preferably with the two portions joining at a distal end of the part 36. A plastics material article as claimed in any one of claims 3 1 to 35, wherein the article is or includes an expanded or partially expanded handle. 37. A plastics material article as claimed in claim 36, wherein the article is a piece of cutlery, of which the handle has one or more expanded or partially expanded portion(s). 38. A plastics material article as claimed in claim 37, wherein the article is a knife, with an expanded portion extending from the handle along the back of the blade. 39. A plastics material article as claimed in claim 38, wherein the knife handle is expanded to circular cross-section with an internal void and the blade back expanded portion is cellular and not fully circularly expanded. 40. A plastics material article as claimed in claim 38, wherein the knife handle is expanded to flattened circular cross-section with an internal void and the blade back expanded portion is cellular and not fully circularly expanded. 41. A plastics material article as claimed in claim 37, wherein the article is a fork with an expanded portion extending from the handle through the swan-neck and expanded portions extending from the swan-neck to the tines. 42. A plastics material article as claimed in claim 41 , wherein the fork handle is expanded to circular cross-section with an internal void and the tines expanded portions are cellular and not fully circularly expanded 43. A plastics material article as claimed in claim 37, wherein the article is a spoon with expanded portions extending from the handle along opposite sides of the bowl. 44. A plastics material article as claimed in claim 43, wherein the spoon handle is expanded to circular cross-section with an internal void and the bowl side expanded portions are cellular and not fully circularly expanded. 45. A plastics material article as claimed in any one of claims 3 1 to 35, wherein the article is a garment hanger. 46. A plastics material article as claimed in claim 45, wherein the hanger has a hook which is expanded to circular cross-section with a central void. 47. A plastics material article as claimed in claim 45 or claim 46, wherein the hanger has arms which are expanded to circular cross-section with a central void. 48. A plastics material article as claimed in claim 43 or claim 44, wherein the hanger has arms having two portions expanded to circular cross-section with a central void, and having with an intermediate land of non-expanded plastics material. 49. A plastics material article as claimed in claim 48, wherein the land is substantially tangential to the two expanded arm portions. 50. A plastics material article as claimed in claim 34 or claim 35, wherein the article includes an annular portion expanded to circular cross-section with a central void. 51. A plastics material article as claimed in claim 50, wherein the article is of soft plastics material and the annular portion is adapted to act as a seal. 52. A plastics material article as claimed in claim 51 , wherein the article is a small container adapted to be an eye bath, with the annular region being deformable to seal to the eye socket. 53. A mould tool for use in the method of any one of claims 1 to 30 or for forming the pre-form prior to expansion of the articles of any one of claims 31 to 52. 54. A mould tool as claimed in claim 53, wherein the said circumferential extent around the said region is such as to allow an increase on expansion in excess of 5mm, whereby a central void can be formed in an article formed with the tool.

Inventors: CLARKE PETER REGINALD, CLARKE, PETER, REGINALD
Applicants: CLARKE PETER R, CORALTECH LTD, CLARKE, PETER, REGINALD, CORALTECH LIMITED
Application year: 1997
Main classification: B29C44
IPC codes: A47G21, A47G25, B29C44, B29C45