RUBBER ARTICLE REINFORCING STEEL CORD AND PNEUMATIC TIRE

Abstract: This invention can advantageously avoid the lowering of the resistance to corrosion fatigue, which becomes a problem in steel filaments having a high tensile strength, by rendering a ratio R 1 /R 0 of radius of curvature R 0 of a helix in each helically formed steel filament obtained by untwisting of the cord to radius of curvature R 1 of helix after the removal of a surface layer from the inside of the helix in the steel filament into less than 1 in steel cords constituting a carcass or a belt of a pneumatic tire among rubber articles, particularly steel cords using a steel filament having a high tensile strength of 4000-4800 N/mm 2 without winding a wrapping wire around the outer peripheral surface thereof.

Description: This invention relates to steel cords for the reinforcement of rubber articles such as pneumatic tires, industrial belts and the like, as well as to pneumatic tires having reduced weight and improved durability by using such steel cords in at least one of the carcass and belt thereof. In the field of pneumatic tires as a typical example of rubber articles, weight reduction of tires is desirable for contributing to low fuel consumption of vehicles in view of global environmental protection. This is true even for steel cords as a tire reinforcement. That is, it is attempted to decrease the amount of steel cords used for reducing the total weight of the carcass or belt by increasing the strength of the cord while maintaining the strength of the tire. However, if it is intended to increase the tensile strength per unit section area of a steel filament constituting the steel cord, weight reduction of the tire is realized, but the resistance to corrosion fatigue is degraded and hence there is caused a problem that the durability of the cord and hence the durability of the rubber article such as a tire are lowered. That is, the tire may be sometimes subjected to cut failure arriving at the vicinity of the steel cord through protrusions on a road surface or a roadside edge and hence the steel filaments constituting the cord are exposed to corrosion through water penetrated into such a cut failure to lower the durability of the tire. This phenomenon becomes conspicuous as the tensile strength of the cord becomes higher. As a countermeasure, there is known a method wherein the forming ratio of the steel filament is made large to form a space between the steel filaments in the case of steel cord having a single twisted construction, or the number of steel filaments constituting a sheath is decreased to form a space between the steel filaments in the case of steel cord having a layer twisting construction, whereby the steel cord is rendered into a so-called rubber-penetration structure provided with a space capable of receiving rubber into the inside of the cord to prevent the penetration of water into the inside of the cord and hence control the corrosion of the steel filaments. Even if the rubber penetration is sufficient, however, the corrosion of the steel filament may be progressed by water included in rubber, so that the resistance to corrosion fatigue is not necessarily improved even by the above rubber-penetration structure. Further, JP-A-57-149578 proposes a method wherein the fatigue resistance is improved by alternately conducting bending-unbending treatments to uniformly disperse residual compression stress over the full peripheral surface of a wire. In the cord having a high tensile strength, however, the elastic limit is high, so that there is a disadvantage that the effect obtained by the bending-unbending treatments is not sufficiently developed. It is, therefore, an object of the invention to provide steel cords for use in rubber articles, particularly the carcass or belt of a pneumatic tire, which can avoid the problem that the lowering of the resistance to corrosion fatigue is produced when the tensile strength of the steel filament constituting the cord is increased. The present invention provides a steel cord for the reinforcement of rubber articles having a single twisted construction obtained by twisting 3 to 6 steel filaments each having a tensile strength of 4000-4800 N/mm 2 and an open type structure having a space between adjacent steel filaments without winding a wrapping wire around the outer peripheral surface thereof, in which a radius of curvature R 0 of a helix in each helically formed steel filament obtained by untwisting of the cord to radius of curvature R 1 of the helix after the removal of a surface layer from the inside of the helix in the steel filament satisfy a ratio of R 1 /R 0 of less than 1. In this case, it is advantageous that a space between mutually adjacent steel filaments is not less than 0.02 mm on average but not more than 1.5 times a diameter of the steel filament for penetrating rubber into the inside of the cord, and it is useful that the steel filament has a carbon content of not less than 0.70% by weight and a diameter of 0.15-0.28 mm for improving the cord tenacity. The invention also provides: a steel cord for the reinforcement of rubber articles having a two-layer twisting construction obtained by surrounding a core comprised of n steel filaments (n=1-4) each having a tensile strength of 4000-4800 N/mm 2 with a sheath comprised of n+(2∼6) steel filaments each having a tensile strength of 4000-4800 N/mm 2 and a rubber penetration type structure having a space between adjacent steel filaments of the sheath without winding a wrapping wire around the outer peripheral surface thereof, in which a radius of curvature R 0 of a helix in each helically formed steel filament obtained by untwisting of the cord to radius of curvature R 1 of the helix after the removal of a surface layer from the inside of the helix in the steel filament satisfy a ratio of R 1 /R 0 of less than 1; and a steel cord for the reinforcement of rubber articles having a three-layer twisting construction obtained by surrounding a core comprised of a single steel filament having a tensile strength of 4000-4800 N/mm 2 with a first sheath comprised of m steel filaments (m=3∼6) each having a tensile strength of 4000-4800 N/mm 2 and arranging a second sheath comprised of m+(2∼6) steel filaments each having a tensile strength of 4000-4800 N/mm 2 and a rubber penetration type structure having a space between adjacent steel filaments of the sheath without winding a wrapping wire around the outer peripheral surface thereof, in which a radius of curvature R 0 of a helix in each helically formed steel filament obtained by untwisting of the cord to radius of curvature R 1 of the helix after the removal of a surface layer from the inside of the helix in the steel filament satisfy a ratio of R 1 /R 0 of less than 1. The term "rubber penetration type structure" used herein means a structure wherein a space is existent between the steel filaments constituting the sheath in the two-layer twisting construction or three-layer twisting construction and rubber can penetrate into the cord through the space. In this case, it is advantageous that a space between mutually adjacent steel filaments of the sheath is not less than 0.02 mm on average but not more than 1.5 times a diameter of the steel filament for penetrating rubber into the inside of the cord, and it is useful that the steel filament has a carbon content of not less than 0.70% by weight and a diameter of 0.15-0.23 mm for improving the cord tenacity. Further, it is advantageous that the surface layer to be removed by dissolution from the inside of the helix in the steel filament is a depth corresponding to 5% of the diameter of the steel filament, or further 10% thereof for particularly improving the resistance to corrosion fatigue. Moreover, the invention further provides a pneumatic tire comprising a carcass toroidally extending between a pair of bead portions and a belt superimposed about a crown portion of the carcass and comprised of at least two belt layers, in which the above-defined steel cords are used as a cord constituting at least one of the carcass and the belt. In this case, it is advantageous that the steel cords are applied so that a distance between adjoining cords is 0.6-0.9 mm in a treat material layer as a starting material for the carcass of the tire. The steel cord according to the invention is a steel cord having a single twisted construction obtained by twisting 3∼6 steel filaments, a steel cord having a two-layer twisting construction obtained by surrounding a core comprised of n steel filaments (n=1∼4) with a sheath comprised of n+(2∼6) steel filaments, or a steel cord having a three-layer twisting construction obtained by surrounding a core of a single steel filament with a first sheath comprised of m steel filaments (m=3∼6) and arranging a second sheath comprised of m+(2∼6) steel filaments around the first sheath. In this case, it is important that the radius of curvature R 0 of a helix in each helically formed steel filament obtained by untwisting of the cord to the radius of curvature R 1 of the helix after the removal of a surface layer from the inside of the helix in the steel filament satisfy a ratio R 1 /R 0 of a given range. In Fig. 1(a) of the accompanying drawings is shown a helically formed steel filament 1 obtained by untwisting of the steel cord, in which a helix of the steel filament 1 has a radius of curvature R 0 . As shown in Fig. 1(b), the helix after the removal of a surface layer from the inside of the helix in the steel filament 1 has a radius of curvature R 1 . According to the invention, therefore, it is important that the ratio R 1 /R 0 of both radii of curvature is less than 1. In the invention, the ratio R 1 /R 0 of radii of curvature is restricted to less than 1 for rationalizing stress distribution at the surface zone of the steel filament to compress residual stress of the surface zone at the inside of the helix in the steel filament. In general, each of the steel filaments obtained by untwisting of the steel cord has a helix form because the steel filament is subjected to plastic deformation at a twisting step for the formation of the cord by twisting straight steel filaments obtained at a drawing step. Even if residual tension stress adversely affecting the resistance to corrosion fatigue is reduced from the surface of the steel filament at the drawing step, when such steel filaments are twisted to form the cord, residual tension stress is unavoidably produced in the inside of the helix through the plastic deformation and hence it is difficult to improve the resistance to corrosion fatigue in the cord. The reason why the residual tension stress at the surface obstructs the resistance to corrosion fatigue is due to the fact that the local formation of cells is first induced at the surface of the helix through such a stress to give an environment easily causing electrochemical corrosion and when pits are created by fretting and the presence of water under such an environment, if there is existent the above residual stress, stress concentrates in the pits to easily cause cracks. In the steel cord according to the invention, the residual stress at the inside of the helix in the steel filament is switched from tension side to compression side to improve the resistance to corrosion fatigue. That is, the feature that the residual stress at the inside of the helix in the steel filament is existent in the compression side can be defined by the fact that the radius of curvature R 1 after the removal of the surface layer from the inside of the helix is made smaller than the radius of curvature R 0 before the dissolution or the ratio R 1 /R 0 is less than 1, whereby the invention has been accomplished. In general, the elastic limit of the steel filament rises as the tensile strength of the steel filament increases, so that it is difficult to shift the residual stress from tension side to compression side through plastic deformation treatment. Particularly, when the tensile strength is not less than 4000 N/mm 2 , the plastic deformation treatment is very difficult. On the contrary, in order to obtain cords in which the ratio R 1 /R 0 in the steel filament is less than 1, the inventors have newly established a method wherein the cord is obtained, for example by twisting steel filaments, and then passed through correction rolls under tension, during which it is subjected to such a treatment that a sum σ of bending stress B to the steel filament and tensile stress T to the steel filament through the rolls is not more than 80% but less than 100% of the tensile strength of the steel filament, and a ratio of T in the sum σ is not less than 80% but less than 95%, to thereby reduce residual tensile stress in the inside of the helix of the steel filament. According to this method, the invention becomes applicable even to steel filaments having a tensile strength of not less than 4000 N/mm 2 , which could not be subjected to the conventional plastic deformation treatment. When a vehicle provided with pneumatic tires is run, the steel cord for the reinforcement of the tire is subjected to repetitive bending and hence the steel filaments constituting the cord are worn by fretting to further cause corrosion fatigue. In the steel cord for the reinforcement of the tire, therefore, it is preferable that the radius of curvature of the helix after the removal of the surface layer corresponding to 5% of the filament diameter satisfies the above relation, and particularly the radius of curvature of the helix after the removal of the surface layer corresponding to 10% of the filament diameter satisfies the above relation. In other words, the invention is to minimize residual tension stress at a region from the surface of the steel filament to a depth corresponding to 5%, more particularly 10%,of the filament diameter as far as possible. If the progress of the wearing through fretting is fast, however, mechanical wear precedes the corrosion to prematurely wear and lose the reducing region of residual tension stress in the surface layer of the steel filament and hence there is caused a danger of developing no reducing effect of residual tension stress. Therefore, it is important that the technique of restricting the ratio R 1 /R 0 to less than 1 is applied to cords causing no fretting or cords having a structure that the occurrence of fretting is very gentle. In the cords of the single twisted construction or two- or three-layer twisting construction according to the invention, the fretting is avoided and the effect of reducing the residual tension stress at the ratio R 1 /R 0 of less than 1 is sufficiently developed by the features that the space between the adjacent steel filaments in the single twisted construction or the space between the adjacent steel filaments in the sheath of the layer twisting construction is not less than 0.02 mm on average but not more than 1.5 times the diameter of the steel filament, and a wrapping wire is not wound around the outer peripheral surface of the cord. That is, the steel cord according to the invention is required to adopt an adequate twisting construction from a viewpoint of the rubber penetrability and fatigue resistance when being used as a reinforcement for rubber articles and is a steel cord of single twisted construction obtained by twisting 3∼6 steel filaments, a steel cord of two-layer twisting construction obtained by surrounding a core comprised of n steel filaments (n=1∼4) with a sheath comprised of n+(2∼6) steel filaments, or a steel cord of three-layer twisting construction obtained by surrounding a core of a single steel filament with a first sheath comprised of m steel filaments (m=3∼6) and arranging a second sheath comprised of m+(2∼6) steel filaments around the first sheath as previously mentioned. For example, there are recommended steel cords having the single twisted construction exemplified by 1×5 construction as shown in Fig. 2, or various layer twisting constructions as shown in Figs. 3(a) to (d). In Fig. 3, numeral 2 is a core, and numerals 3 and 4 are sheaths, respectively. These cord constructions are effective to improve the fatigue resistance while satisfying the rubber penetrability and to increase the filling ratio of the steel filaments in section of the cord to thereby provide a desired cord tenacity with a minimum cord diameter. In the steel cord of the two-layer twisting construction, therefore, it is preferable that the number of the steel filaments constituting the core is 1 or 2 having no space therein, or 3 having a minimum space therein. In order to ensure the rubber penetrability for avoiding fretting, it is preferable that a space t between the adjacent steel filaments in the single twisted construction as shown in Fig. 2 or a space t between the adjacent steel filaments constituting the sheath in the layer twisting construction as shown in Fig. 3 is not less than 0.02 mm on average but not more than 1.5 times the filament diameter as previously mentioned. When the space t is less than 0.02 mm, it is difficult to penetrate rubber into the inside of the cord in the vulcanization for tire building, while when said space exceeds 1.5 times the filament diameter, disorder in the arrangement of the steel filaments is caused to lower the fatigue resistance,and also the filling ratio of the steel filaments in the circumscribed section of the cord is lowered to reduce the cord tenacity or increase the cord diameter, and hence a treat material for the carcass or belt in the tire (i.e. a rubberized layer of parallel steel cords) becomes too thick for reducing the tire weight. In the invention, the steel filament constituting the steel cord has a tensile strength of 4000-4800 N/mm 2 . When the tensile strength is less than 4000 N/mm 2 , the cord tenacity is lacking and the reduction of tire weight can not be attained while maintaining the tire strength. Further, when the diameter of the steel filament constituting the cord is made thick for maintaining the cord tenacity, if a large bending input is applied to the cord upon running under a low internal pressure represented by so-called run-flat running or the like, initial breakage is liable to be caused in the steel filament constituting the cord. When the tire is used at such a state by again filling with air, the possibility of inducing tire burst becomes higher. According to the invention, the diameter of the steel filament can be made small by arranging the tensile strength of the steel filament to be not less than 4000 N/mm 2 and hence the performances of the tire under a low internal pressure can be improved to enhance the safety. On the other hand, when the tensile strength of the steel filament exceeds 4800 N/mm 2 , the drawing productivity is considerably lowered and the resulting steel filament has poor ductility. In order to obtain the tensile strength of 4000-4800 N/mm 2 , the steel filament preferably has a carbon content of not less than 0.7% by weight, more preferably not less than 0.75% by weight. Moreover, when the carbon content exceeds 0.90% by weight, free cementite is produced in the patenting and hence the ductility of the steel filament can not be ensured. It is most preferable to use steel material containing C: 0.80-0.85% by weight in order to control the rise of the cord cost. When the diameter of the steel filament is less than 0.15 mm in the cord of single twisted construction, the tensile strength of the steel filament rises, but the productivity at the drawing step lowers, while when said diameter exceeds 0.28 mm, the repetitive bending fatigue property is degraded and the bending rigidity of the steel cord becomes too large and hence the working in the tire building, particularly the working of the bead portion, is difficult. In the cords of layer twisting construction, the number of steel filaments constituting the cord is large as compared with the cord of the single twisted construction and even if the steel filament is made thin, it is possible to maintain the strength of the tire, so that the disadvantages produced when the diameter of the steel filament is made thick as mentioned above can be avoided by rendering the diameter of the steel filament to be not more than 0.23 mm. The diameter of the steel filament is not necessarily the same, but the productivity can be enhanced when the filament diameters are the same. Since a wrapping wire to be wound around the outermost layer of the steel cord is not used in the steel cords of not only the single twisted construction but also the layer twisting constructions according to the invention, fretting between the steel filament in the outermost layer and the wrapping wire can be prevented, so that the lowering of the cord tenacity is very small even when the tire is used over a long period of time and also the diameter of the cord is made small to advantageously contribute to the reduction of the tire weight. On the other hand, when the above-defined steel cords are used as a reinforcement in at least one of a carcass and a belt of a pneumatic tire comprising a carcass toroidally extending between a pair of bead portions and a belt superimposed about a crown portion of the carcass and comprised of at least two belt layers, the properties of the tire can be improved. Particularly, when the steel cords are used in the carcass of the tire, it is preferable to apply the steel cords so that the distance between adjoining cords is 0.6-0.9 mm in the treat material for the carcass. It is preferable to apply the steel cords so that a diameter d (mm) and a cord tenacity of the steel cord satisfy a relation of 0.6≦(50 x cord tenacity/T) - d≦0.9 with respect to a preset tenacity T per 50 mm of a width of a treat material for the carcass mainly determined according to the specification of the tire. That is, the diameter and tensile strength of the steel filament and the cord construction may properly be determined so as to provide the diameter and cord tenacity of the steel cord satisfying the above equation. This is due to the fact that the durability of the carcass is improved by rendering the distance between adjoining steel cords in the carcass of a product tire after the expansion upon vulcanization of a green tire during the production of the tire within an adequate range. That is, when the cord distance in the treat material represented by (50 x cord tenacity/T) - d is less than 0.6 mm, the shearing stress of rubber becomes too large at an end portion of the carcass in the vicinity of the bead portion during the running of the tire and hence it is apt to create cracks in the rubber between the cords and cause adhesion breakage between cord and rubber. On the other hand, when it exceeds 0.9 mm, outward blistering of rubber between the cords in the radial direction is created upon air inflation of the tire to increase heat generation of rubber during the running of the tire and hence the high-speed durability of the tire lowers. The invention will be further described with reference to the accompanying drawings, wherein: Fig. 1 is a diagrammatic view illustrating the shape before and after the removal of a surface layer from the inside of a helix with respect to a steel filament obtained by untwisting of a steel cord; Fig. 2 is a schematic section view of a steel cord having a single twisted construction; Fig. 3 is a schematic section view of a steel cord having a layer twisting construction; Fig. 4 is a diagrammatic radial-half section view of a pneumatic tire according to the invention; Fig. 5 is a partially schematic view illustrating a cord distance in a treat material before tire building; and Fig. 6 is a schematic section view illustrating constructions of conventional and comparative steel cords. Various steel filaments having diameters and tensile strengths shown in Tables 1∼4 are produced by subjecting a steel wire (diameter: 5.5 mm) having C: 0.70-0.85% by weight, Si: 0.23% by weight, Mn: 0.49% by weight, P: 0.006% by weight and S: 0.008% by weight to dry drawing, patenting, brass plating and wet drawing in this order. Then, steel cords having various constructions shown in Tables 1-4 are produced in the usual manner using a tubular twisting machine or a buncher twisting machine. The steel cord produced in the tubular twisting machine is subjected to such a treatment that in order to reduce the residual tensile stress in the inside of the helix of the steel filament constituting the steel cord, two or more straightening rollers having a large diameter are arranged in zigzag form and the steel cord is passed through these straightening rollers under a tensile stress higher than the usual level. On the other hand, when the steel cord is produced by using the buncher twisting machine, the steel filaments are subjected to a treatment of applying a tensile stress higher than the usual level at the step of twisting them with torsion. In any case, R 1 /R 0 in the steel filament is variously varied by changing the conditions of these treatments. That is, when the above treatment applied to the steel cord produced in the tubular twisting machine is described with respect to the steel cord of 3+8×0.19 mm shown as Invention Example 1 in Table 1, R 1 /R 0 of this cord is rendered into less than 1 by zigzag arranging at least two, preferably not less than 3, straightening rollers of 60 mm in diameter and passing the cord through these straightening rollers under a tensile stress of 2900 N/mm 2 . On the other hand, in Comparative Example 4 using the same steel cord, when the cord is passed through 2 or 3 or more zigzag arranged straightening rollers of 10 mm in diameter under a tensile stress of 660 N/mm 2 , R 1 /R 0 of less than 1 is not obtained and hence the residual tensile stress in the inside of the helix of the steel filament is not sufficiently reduced. Also, when the buncher twisting machine is used in Invention Example 1, R 1 /R 0 of the steel filament is rendered into less than 1 by applying a tensile stress of 830 N/mm 2 to the steel filament constituting the sheath in the bundling and twisting of the steel filaments. On the other hand, when the twisting of the steel filaments as the sheath is carried ' out under a conventional tensile stress of about 290 N/mm 2 , R 1 /R 0 of less than 1 is not obtained, but when it is subsequently subjected to the above treatment with the straightening rollers, R 1 /R 0 of less than 1 is attained. The steel filament used in Invention Example 1 having a fine diameter of 0.19 mm and a high tensile strength of 4120 N/mm 2 can be obtained by subjecting a wire material, which is subjected to, for example, brass plating and has a tensile strength of 1275 N/mm 2 , to wet drawing so as to provide a total area reduction ratio of 98.3% according to a pass schedule using such a die to be set in each pass such that a die used in a wire drawing at a true strain ε represented by the following equation (1) of less than 0.75 adjusts an area reduction ratio represented by the following equation (2) to (22.67ε+3)∼29% and a die used in a wire drawing at a true strain ε of 0.75∼2.25 adjusts an area reduction ratio to 20-29% and a die used in a wire drawing at a true strain ε of more than 2.25 adjusts an area reduction ratio to (-5.56ε+32.5)∼(-6.22ε+43)%, or specifically a pass schedule of dies shown in Table 5. ε = 2·ln(d 0 /d 1 ) wherein d 0 : diameter of steel filament before drawing (mm) d 1 : diameter of steel filament after drawing (mm) (area reduction ratio of die) = {1-(A1/A0)}x100 wherein A 0 : sectional area of steel filament before passing through die A 1 : sectional area of steel filament after passing through die Various pneumatic radial tires for trucks and buses having a tire size of 11/70R22.5 (14PR) are manufactured by using the thus obtained steel cords in a carcass 5 of the tire shown in Fig. 4 so as to be arranged at an inclination angle of 90° with respect to an equator of the tire. In Fig. 4, numeral 6 is a belt comprised of four belt layers, and numeral 7 is a bead core. Each of these tires is mounted onto a normal rim defined in JATMA YEAR BOOK 1996 and inflated under an air pressure corresponding to maximum loading ability at applied size and ply rating in the same JATMA YEAR BOOK, and then applied to various tests for rubber penetrability, retention of cord tenacity, resistance to corrosion fatigue and ratio of steel filament breakage in a large bending input. That is, the steel cord is taken out from the tire after the vulcanization and then a ratio of portion covered with rubber to a full length of the steel cord is measured on the surface of the steel filament in the case of the single twisted steel cord or on the surface of the core in the case of the layer-twisted steel cord. The rubber penetrability is represented by o ○ when the ratio is 90-100%, ○ when it is 80-89% and X when it is not more than 79%. Moreover, there is no problem in practical use when the ratio is not less than 80%. The retention of cord tenacity is evaluated by calculating a ratio as percentage of tenacity of steel cord taken out from the tire after running on a drum under a design normal load over 100,000 km to tenacity of steel cord taken out from a new tire having the same specification. The larger the numerical value, the better the result. Into the inside of the tire is poured 300 cc of water prior to the mounting onto the rim, and thereafter the tire is run on the drum in the same manner as described above to measure a running distance until the occurrence of steel cord breaking-up (CBU) in the carcass of the tire. The resistance to corrosion fatigue is evaluated by an index on the basis that the running distance of a control tire (conventional example in Table 1) is 100. The larger the index value, the better the result. After the tire is run on a drum, the air pressure is adjusted to 1 kgf/cm 2 (at a hot state), and then the tire is run on the drum over a distance of 5000 km under a large bending input condition of a load corresponding to the maximum loading ability, and thereafter 10 steel cords are taken out from the carcass of the dissected tire and the number of broken steel filaments is measured. The ratio of broken steel filament in the large bending input is evaluated by an index on the basis that the broken number of a control tire (conventional example in Table 1, Comparative Example 5 in Table 2, Comparative Example 6 in Table 3, and Comparative Example 7 in Table 4) is 100. The smaller the index value, the better the result. The ratio R 1 /R 0 of the radius of curvature of the steel filament is calculated by cutting the steel filaments constituting the outermost layer of the helically formed steel cord obtained by untwisting of the cord to a length of 100 mm, applying an enamel onto a half of the circular surface portion in the steel filament, immersing in an aqueous solution of 50% nitric acid to dissolve out the remaining half portion not covered with the enamel to a depth corresponding to 3% or 10% of the filament diameter, and then measuring radii of curvature before and after such a dissolution treatment. The cord distance is measured in a treat material before the tire building as shown in Fig. 5. The weight of steel cords used is represented by an index on the basis that the cord weight embedded in the carcass of a control tire (conventional example in Table 1) is 100. The smaller the numerical value, the better the weight reduction. The measured results are also shown in Tables 1∼4. Moreover, the conventional example, comparative examples and invention examples of steel cord having a two-layer twisting construction with a core comprised of 3 filaments are shown in Table 1, and a comparative example and an invention example of steel cord having a two-layer twisting construction with a core comprised of 2 filaments are shown in Table 2, and a comparative example and an invention example of steel cord having a single twisted construction are shown in Table 3, and a comparative example and an invention example of steel cord having a three-layer twisting construction with a core comprised of one filament are shown in Table 4. Comparative Example 5 Invention Example 3 Cord construction Figure corresponding to cord construction 2+7×0.25 (mm) Fig. 3(b) 2+7×0.215 (mm) Fig. 3(b) Twisting direction S/S S/S Pitch (mm) 6.0/12.0 6.0/12.0 Tensile strength of steel filament (N/mm 2 ) 3500 4370 Cord tenacity (N/mm 2 ) 1496 1393 Space between steel filaments t (mm) 0.076 0.065 Ratio R 1 /R 0 in radius of curvature at 3% depth 0.92 0.93 Ratio R 1 /R 0 in radius of curvature at 10% depth 0.96 0.90 Cord distance (mm) 0.74 0.75 Weight of cord used (%) 81.1 65.0 Rubber penetrability o ○ o ○ Retention of tenacity (%) 96 97 Resistance to corrosion fatigue 124 125 Index of steel filament breakage 100 20 Comparative Example 6 Invention Example 4 Cord construction Figure corresponding to cord construction 1×5×0.31 (mm) Fig. 2 1×5×0.275 (mm) Fig. 2 Twisting direction S S Pitch (mm) 12.0 9.5 Tensile strength of steel filament (N/mm 2 ) 3800 4290 Cord tenacity (N/mm 2 ) 1398 1234 Space between steel filaments t (mm) 0.075 0.066 Ratio R 1 /R 0 in radius of curvature at 3% depth 0.95 0.94 Ratio R 1 /R 0 in radius of curvature at 10% depth 0.98 0.94 Cord distance (mm) 0.69 0.62 Weight of cord used (%) 74.7 66.2 Rubber penetrability o ○ o ○ Retention of tenacity (%) 97 98 Resistance to corrosion fatigue 120 122 Index of steel filament breakage 100 60 Comparative Example 7 Invention Example 5 Cord construction Figure corresponding to cord construction 1×0.225 (mm) + (6+11)×0.17(mm) Fig. 3(c) 1×0.20 (mm) + (6+11)×0.155(mm) Fig. 3(c) Twisting direction -/S/Z -/S/Z Pitch (mm) -/6.0/12.0 -/6.0/12.0 Tensile strength of steel filament (N/mm 2 ) 3730 4020 Cord tenacity (N/mm 2 ) 1534 1376 Space between steel filaments t (mm) first sheath:0.028 second sheath:0.038 first sheath:0.023 second sheath:0.033 Ratio R 1 /R 0 in radius of curvature at 3% depth 0.90 0.91 Ratio R 1 /R 0 in radius of curvature at 10% depth 0.88 0.86 Cord distance (mm) 0.88 0.78 Weight of cord used (%) 76.1 70.6 Rubber penetrability ○ ○ Retention of tenacity (%) 95 96 Resistance to corrosion fatigue 128 128 Index of steel filament breakage 100 80 Pass No. Filament diameter (mm) Area reduction ratio (%) 1 1.42 5.40 2 1.34 10.95 3 1.23 15.74 4 1.10 20.02 5 0.97 22.24 6 0.85 23.21 7 0.75 23.18 8 0.65 23.17 9 0.57 23.27 10 0.50 22.98 11 0.45 21.42 12 0.40 20.41 13 0.36 18.68 14 0.32 18.09 15 0.29 17.66 16 0.27 16.28 17 0.25 15.69 18 0.23 14.04 19 0.21 12.67 20 0.20 11.78 21 0.19 10.65 As seen from Tables 1∼4, the tires using the steel cords according to the invention have excellent resistance to corrosion fatigue, and particularly the resistance to fretting fatigue is largely improved and hence the retention of the carcass strength is excellent. On the contrary, Comparative Examples 2 and 4 aim at the compression of the residual stress on the surface through the conventional system merely passing through straightening rollers, but since the residual stress of the surface layer at the inside of the helix is substantially tension, the improvement of resistance to corrosion fatigue is poor as compared with those in Invention Examples 1-5. Moreover, the invention examples and Comparative Example 2 develop the effect of directly reducing the weight of steel cords used by about 30% by increasing the tensile strength of the steel filament. Although the cord construction is same between Comparative Example 3 and Invention Example 1, Comparative Example 5 and Invention Example 3, Comparative Example 6 and Invention Example 4 and Comparative Example 7 and Invention Example 5, the tensile strength of the steel filament is not less than 4000 N/mm 2 in the invention examples and is less than 4000 N/mm 2 in the comparative examples, so that even if R 1 /R 0 is less than 1, the comparative examples do not provide sufficient weight reduction. Also, the comparative examples have large filament diameter as compared with the invention examples, so that they are disadvantageous in that breakage of the steel filament is apt to be caused upon large bending input. According to the invention, the strength of the steel cord can be increased without damaging the resistance to corrosion fatigue, so that when the steel cords are particularly applied to a pneumatic tire, it is possible to attain a reduction of the tire weight while maintaining excellent durability.

Claims: A steel cord for the reinforcement of rubber articles having a single twisted construction obtained by twisting 3 to 6 steel filaments each having a tensile strength of 4000-4800 N/mm 2 and an open type structure having a space between adjacent steel filaments without winding a wrapping wire around the outer peripheral surface thereof, characterized in that a radius of curvature R 0 of a helix in each helically formed steel filament obtained by untwisting of the cord to radius of curvature R 1 of the helix after the removal of a surface layer from the inside of the helix in the steel filament satisfy a ratio of R 1 /R 0 of less than 1. A steel cord as claimed in claim 1, characterized in that a space between mutually adjacent steel filaments is not less than 0.02 mm on average but not more than 1.5 times a diameter of the steel filament for penetrating rubber into the inside of the cord. A steel cord as claimed in claim 1 or 2, characterized in that the steel filament has a carbon content of not less than 0.70% by weight and a diameter of 0.15-0.28 mm for improving the cord tenacity. A steel cord for the reinforcement of rubber articles having a two-layer twisting construction obtained by surrounding a core (2) comprised of n steel filaments (n=1∼4) each having a tensile strength of 4000-4800 N/mm 2 with a sheath (3) comprised of n+(2-6) steel filaments each having a tensile strength of 4000-4800 N/mm 2 and a rubber penetration type structure having a space between adjacent steel filaments of the sheath without winding a wrapping wire around the outer peripheral surface thereof, characterized in that a radius of curvature R 0 of a helix in each helically formed steel filament obtained by untwisting of the cord to radius of curvature R 1 of the helix after the removal of a surface layer from the inside of the helix in the steel filament satisfy a ratio of R 1 /R 0 of less than 1. A steel cord for the reinforcement of rubber articles having a three-layer twisting construction obtained by surrounding a core (2) comprised of a single steel filament having a tensile strength of 4000-4800 N/mm 2 with a first sheath (3) comprised of m steel filaments (m=3-6) each having a tensile strength of 4000-4800 N/mm 2 and arranging a second sheath (4) comprised of m+(2-6) steel filaments each having a tensile strength of 4000-4800 N/mm 2 and a rubber penetration type structure having a space between adjacent steel filaments of the sheath without winding a wrapping wire around the outer peripheral surface thereof, characterized in that a radius of curvature R 0 of a helix in each helically formed steel filament obtained by untwisting of the cord to radius of curvature R 1 of the helix after the removal of a surface layer from the inside of the helix in the steel filament satisfy a ratio of R 1 /R 0 of less than 1. A steel cord as claimed in claim 4 or 5, characterized in that a space between mutually adjacent steel filaments of the sheath is not less than 0.02 mm on average but not more than 1.5 times a diameter of the steel filament for penetrating rubber into the inside of the cord. A steel cord as claimed in claim 4, 5 or 6, characterized in that the steel filament has a carbon content of not less than 0.70% by weight and a diameter of 0.15-0.23 mm for improving the cord tenacity. A steel cord as claimed in any of claims 1 to 7, characterized in that the surface layer to be removed by dissolution from the inside of the helix in the steel filament is a depth corresponding to 5% of the diameter of the steel filament. A steel cord as claimed in any of claims 1 to 7, characterized in that the surface layer to be removed by dissolution from the inside of the helix in the steel filament is a depth corresponding to 10% of the diameter of the steel filament. A pneumatic tire comprising a carcass (5) toroidally extending between a pair of bead portions and a belt (6) superimposed about a crown portion of the carcass and comprised of at least two belt layers, in which steel cords are used as a cord constituting at least one of the carcass and the belt, characterized in that said steel cord is as claimed in any of claims 1 to 9. A pneumatic tire as claimed in claim 10, characterized in that the steel cords are applied so that a distance between adjoining cords is 0.6-0.9 mm in a layer of material as a starting material for the carcass (5) of the tire.

Inventors: KANEKO YOSHIKAZU, OBANA NAOHIKO, OSAWA RYUZO, KANEKO, YOSHIKAZU, OBANA, NAOHIKO, OSAWA, RYUZO, KANEKO, Yoshikazu Bridgestone Metalpha, OBANA, Naohiko Bridgestone Metalpha Corporation
Applicants: BRIDGESTONE CORP, BRIDGESTONE METALPHA CORP, BRIDGESTONE CORPORATION, BRIDGESTONE METALPHA CORPORATION
Application year: 1997
Main classification: D07B1
IPC codes: D07B1, B60C9