Endless power transmission belt construction, cord therefor and methods of making the same

Abstract: An endless power transmission belt construction (20), cord (27, 37) therefor and methods of making the same are provided, the cord having the yarns (33, 39) and the plies (32, 38) thereof respectively twisted on a 2 for 1 twister so as to cause the longitudinal axes of the fiber filaments (34, 40) to be disposed generally in the longitudinal direction of the cord (27, 37), with the denier of the fiber filaments (34, 40) of each yarn (33, 39) being approximately 1500. The twist multiplier of the three plies (32) is 3.7687 as the plies are twisted together at a rate of approximately 2.9 turns per linear inch of the cord (27), and the twist multiplier for the two yarns (33) is 3.6765 as the two yarns for each ply (32) are twisted together at a rate of approximately 4.9 turns per linear inch of that ply. The twist multiplier for five plies (38) is 3.6986 as the plies are twisted together at a rate of approximately 1.8 turns per linear inch of the cord (37), and the twist multiplier for three yarns (39) is 3.5838 as the three yarns for each ply (38) are twisted together at a rate of approximately 3.9 turns per linear inch of that ply. The fiber filaments (34, 40) comprise p-aramid that comprises co-poly (paraphenylene/3,4' oxydiphenylene terephthalamide).

Description: BACKGROUND OF THE INVENTION Field of the Invention This invention relates to a new endless power transmission belt construction and to a new cord for the load-carrying section of the belt construction, as well as to a new method of making such an endless power transmission belt construction and a new method of making such a cord. Prior Art Statement It is known to provide a p-aramid fiber cord for use as a component in a power transmission belt construction or the like, the cord comprising three plies twisted together in one direction at a rate to approximately equal a first certain twist multiplier, with each ply comprising two yarns of a plurality of p-aramid fiber filaments having a certain denier and being twisted together in a direction opposite to the one direction at a rate to approximately equal a second certain twist multiplier, each twist multiplier being equal to the quotient of the product of the turns per linear inch of twisted material multiplied by the square root of the product of the certain denier of the fiber filaments multiplied by the total number of the yarns being twisted at that time divided by seventy-three. For example, see the U.S. patent to Carlson et al, No. 4,083,260. An improved p-aramid fiber cord for use as a component in a power transmission belt construction is known from the U.S. patent to Van Hook, No. 5,425,681, the cord comprising three plies twisted together in one direction at a rate to approximately equal a first certain twist multiplier, with each ply comprising two yarns. The first certain twist multiplier is 3.7687 when three plies are twisted together at a rate of approximately 2.9 turns per linear inch of the cord, and the second twist multiplier is 3.6765 when the two yarns for each ply are twisted together at a rate of approximately 4.9 turns per linear inch of that ply. It is also known to form the cord for an endless power transmission belt construction from fiber filaments made of a p-aramid material sold under the trademark TECHNORA of the Teijin Corporation of Japan and sold in the United States by Teijin Shoji New York Inc. of New York, New York. For example, see the U.S. patent to Nakajima et al, no. 5,230,667. Summary of the Invention It is one of the features of this invention to provide a new cord for an endless power transmission belt construction wherein the new cord has improved characteristics over a prior made cord formed of standard p-aramid fiber filaments. In particular, the prior made cord comprises three plies twisted together in one direction at a rate to approximately equal a first certain twist muitiplier, with each ply comprising two yarns of a plurality of p-aramid fiber filaments having a certain denier and being twisted together in a direction opposite to the one direction at a rate to approximately equal a second certain twist multiplier, each twist multiplier being equal to the quotient of the product of the turns per linear inch of twisted material multiplied by the square root of the product of the certain denier of the fiber filaments multiplied by the total number of the yarns being twisted at that time divided by seventy-three. Counting the twist rate in turns per linear cm and counting the yarns in tex, each twist multiplier is equal to the quotient of the product of the turns per linear cm of twisted material multiplied by the square root of the product of the certain tex of the fiber filaments multiplied by the total number of the yarns being twisted and that time divided by 9.58. The yarns and the plies are twisted together so as to cause the longitudinal axes of the fiber filaments to be disposed generally perpendicular to the longitudinal direction of the cord, with the certain denier being approximately 1500 or 167 tex, the first certain twist multiplier being created by the three plies being twisted together at a rate of approximately 1.85 turns per linear cm (4.7 turns per linear inch) of the cord, the second certain twist multiplier being the result of two yarns being twisted together at a rate of approximately 1.85 tunrs per linear cm (4.7 turns per linear inch) of that resulting ply. However, it was found according to the teachings of this invention that instead of utilizing standard p-aramid fiber filaments as previously set forth, a technical synergy results if the fiber filaments can be formed of a modified p-aramid comprising co-poly (paraphenylene/3,4' oxydiphenylene terephthalamide) with a balanced twist multiplier and having the yarns and the plies respectively twisted on a 2 for 1 twister means so as to cause the longitudinal axes of the fiber filaments to be disposed generally in the longitudinal direction of the cord and with the tex of each yarn being approximately 167 (= 1500 den). The first certain twist multiplier is 3.6986 when five plies are twisted together at the rate of approximately 0,71 turns per linear cm (1.8 turns per linear inch) of cord, and the second twist multiplier is 3.5838 when three yarns for each ply are twisted together at a rate of approximately 1,54 turns per linear cm (3.9 turns per linear inch) of that ply. It was found that the resulting cord of this invention has improved break characteristics over the prior known cord formed of the standard p-aramid fiber filaments as set forth hereinafter. Thus, this invention comprises a p-aramid fiber cord for use as a component in a power transmission belt construction or the like, the cord comprising five plies twisted together in one direction at a rate to approximately equal a first certain twist multiplier, with each ply comprising three yarns. The cord is comprised of a plurality of p-aramid fiber filaments having a certain denier and being twisted together in a direction opposite to the one direction at a rate to approximately equal a second certain twist multiplier, each twist multiplier being equal to the quotient of the product of the turns per linear cm (inch) of twisted material multiplied by the square root of the product of the certain tex (denier) of the fiber filaments multiplied by the total number of the yarns being twisted at that time divided by 9.58 (seventy-three), the yarns and the plies being respectively twisted on a 2 for 1 twister means so as to cause the longitudinal axes of the fiber filaments to be disposed generally in the longitudinal direction of the cord, with the certain tex being approximately 167 (= 1500 den). The first certain twist multiplier is 3.6986 for the five plies twisted together at a rate of approximately 0.71 turns per linear cm (1.8 turns per linear inch) of the cord, and the second certain twist multiplier is 3.5838 as the three yarns for each ply are twisted together at a rate of approximately 1.54 turns per linear cm (3.9 turns per linear inch) of that ply. The p-aramid comprises co-poly (paraphenylene/3,4' oxydiphenylene terephthalamide). Accordingly it is an object of this invention to provide a new cord for use as a component in a power transmission belt construction or the like, the cord of this invention having one or more of the novel features of this invention as set forth above or hereinafter shown or described. Another object of this invention is to provide a new method of making such a cord, the method of this invention having one or more of the novel features of this invention as set forth above or hereinafter shown or described. Another object of this invention is to provide a new power transmission belt construction utilizing such a cord, the belt construction of this invention having one or more of the novel features of this invention as set forth above or hereinafter shown or described. Other objects, uses and advantages of this invention are apparent from a reading of this description which proceeds with reference to the accompanying drawings forming a part thereof and wherein: BRIEF DESCRIPTION OF THE DRAWINGS FIG. 1 is a fragmentary perspective view illustrating the new endless power transmission belt construction; FIG. 2 is an enlarged fragmentary cross-sectional view taken on line 2-2 of FIG. 1; and FIG. 3 is an enlarged fragmentary view of a prior art cord utilized as a component of the belt construction of FIGS. 1 and 2, and FIG. 4 is a view similar to FIG. 3 illustrating the new cord of this invention. DESCRIPTION OF THE PREFERRED EMBODIMENT While the various features of this invention are hereinafter illustrated and described as being particularly adapted to provide a cord for an endless power transmission belt construction of a particular configuration, it is to be understood that the various features of this invention can be utilized to provide a cord for other types of belt constructions or for other structures as desired. Therefore, this invention is not to be limited to only the embodiment illustrated in the drawings, because the drawings are merely utilized to illustrate one of the wide variety of uses of this invention. Referring now to FIGS. 1 and 2, the new endless power transmission belt construction of this invention is generally indicated by the reference numeral 20 and such belt construction 20 is of trapezoidal cross-sectional outline and is popularly referred to as a V-belt. The belt construction 20 has a pair of opposed parallel sides or surfaces 21 and 22 with the surfaces 21 and 22 being connected at their opposite edges by symmetrically arranged side surfaces 23 that define the nonparallel sides of the trapezoidal cross section in a manner well known in the art. The belt construction 20 has a load-carrying section 24 which is arranged between the outside surface 21 and the inside surface 22 of the belt construction 20, the belt construction 20 also comprising a tension section 25 and a compression section 26, with the load-carrying section 24 being disposed between the sections 25 and 26 also in a manner well known in the art. The load-carrying section 24 has as its load-carrying means a helically wound load-carrying cord 27 that has been formed according to the teachings of this invention in a manner hereinafter set forth whereby it is believed that the belt construction 20 will have improved performance characteristics. In particular, it is believed that the cord 27 of this invention comprises an ultra-high tenacity high modulus neutral axis cord that will provide improved overall break strength of the belt construction 20, provide improved dimensional stability of the belt construction 20, provide improved cord popout for the belt construction 20, provide improved dynamic adhesion tor the belt construction 20 and will cut and grind and, thus, produce a cosmetically acceptable belt construction 20 whereas the previously mentioned standard p-aramid cord will not cut or grind. The load-carrying cord 27 is suitably embedded in a polymeric cushion 28 in a manner well known in the art whereby the load-carrying cord 27 and the cushion 28 comprise the load-carrying section 24. The tension section 25 of the belt construction 20 has a fabric cover 29 that forms the outside surface 21 for the belt construction 20. Similarly, the compression section 26 has a fabric cover 30 thereon which defines the inside surface 22 of the belt construction 20, the covers 29 and 30 being formed of any fabric utilized in the art ot making belt constructions. Each of the sections 25 and 26 of the belt construction 20 is formed of any suitable polymeric material and each of the sections 25 and 26 has a plurality of randomly arranged fibers 31 embedded therein for a purpose well known in the art. For example, see the aforementioned US. patent to Carlson et al, No. 4,083,260, that discloses a belt construction similar to the belt construction 20 previously described. The cord 27, as it is known from the US 5,425,681, is illustrated in FIG. 3 for a better understanding of the invention. The first embodiment of FIG. 3 comprises three plies 32 twisted together in the Z direction (the spirals around the central axis slope in the same direction as the central portion of the letter Z) at a rate to approximately equal a first certain twist multiplier. Each ply 32 comprises two yarns 33 of a plurality of p-aramid fiber filaments 34 having a certain tex (denier) and being twisted together in a direction opposite to the direction of the plies 32 (so as to be twisted in the S direction wherein the spirals around the central axis at each yarn slope in the same direction as the middle portion ot the letter S) and at a rate to approximately equal a second certain twist muitiplier, each twist multiplier being equal to the quotient of the product of the turns per linear cm (inch) of twisted material multiplied by the square root of the product of the certain tex (denier) of a yarn of the fiber filaments multiplied by the total number of the yarns being twisted at that time divided by 9.58 (seventy-three). It is well known in the cord making art that material has been twisted in the S direction so as to have a S-twist if when the twisted material is held vertically, the material spirals around its longitudinal axis in the same direction as the middle portion of the letter S when the letter S is superimposed on the vertically held material. In contrast, the material has been twisted in the Z direction so as to have a Z-twist if when the twisted material is held vertically, the material spirals around its longitudinal axis in the same direction as the middle portion of the letter Z when the letter Z is superimposed on the vertically held material. When making the aforementioned prior known standard p-aramid cord, each yarn has a tex of 167 (= 1500 den) with each ply comprising two such yarns being twisted together in the Z direction at a rate of approximately 1.85 turns per linear cm (4.7 turns per linear inch) of twisted material and with three such plies twisted together in the S direction at a rate of approximately 1.85 turns per linear cm (4.7 turns per linear inch) of twisted cord, whereby the resulting cord has an imbalanced twist multiplier, i.e., the fiber filaments have their longitudinal axes disposed substantially perpendicular to the longitudinal axis of the cord. It was found according to the teachings of this invention that when utilizing a modified p-aramid material sold under the trademark TECHNORA as previously described and thereby comprising co-poly (paraphenylene/3,4' oxydiphenylene terephthalamide) for making a cord in exactly the same manner as the prior known standard p-aramid cord, the resulting break characteristics of such TECHNORA cord was not as good as the break characteristics of the standard p-aramid cord. It was found according to the teachings of the US 5,425,681 that when the fiber filaments of the cord 27 are made af the modified p-aramid material sold under the trademark TECHNORA with each yarn 33 thereof having a tex of approximately 167 (= 1500 den) and with each ply 32 having the two yarns 33 twisted together in the Z direction on a 2 for 1 twister at a rate of approximately 1.93 turns per linear cm (4.9 turns per linear inch) of twisted materials so that the twist multiplier thereof equals 3.6765 and then having three such plies 32 twisted together in the S direction on a 2 for 1 twister at a rate of approximately 1.14 turns per linear cm (2.9 turns per linear inch) of the cord so that the twist multiplier of the three plies equals 3.7687, whereby the longitudinal axes of the fiber filaments 34 are disposed generally in the longitudinal direction of the cord 27, the resulting cord 27 has improved break characteristics over the standard p-aramid cord and, thus, over the modified p-aramid cord when made in the same manner as the standard p-aramid cord. After the cord 27 was made on the 2 for 1 twister as set forth above, the cord 27 was first dipped in a bath of PAPI (polymethylene polyphenylisocyanate) and then overcoated with a coating of RFL (resorcinol formalin rubber latex) all in a manner well known in the art. For example, see the aforementioned U.S. patent to Carlson et al, No. 4,083,260. The 2 for 1 twister comprises a ICBT machine and is well known in the art for twisting material to form cords and the like. The aforementioned modified p-aramid material that is sold under the trademark TECHNORA for load-carrying cords is disclosed in the aforementioned U.S. patent to Nakajima et al, No. 5,230,667. A cord 27 made by the method as previously described was found to break when approximately 188.7 kg (416 lbs.) was applied thereto, whereas the standard p-paramid cord broke at approximately 158.8 kg (350 lbs.). It was also found that the percentage of elongation of the cord 27 of this invention was approximately 5.4% of its break point, whereas the standard p-aramid cord had a 5.2% elongation at its break point. Such a cord 27 was found to have a 1% elongatian when a load of approximately 37.3 kg (82.3 lbs.) was applied thereto and had a 3% elongation when a load of 119.0 kg (262.4 lbs.) was applied thereto. In contrast, the standard p-aramid cord had a 1% elongation when a load of 25.7 kg (56.7 lbs.) was applied thereto and had a 3% elongation when a load of 88.3 kg (194.7 lbs) was applied thereto. Thus, it can be seen that the cord 27 has improved break characteristics over the break characteristics of the standard p-aramid cord when the cord is formed in the manner previously set forth and is twisted on a 2 for 1 twister in the manner previously set forth. From the above it can be seen that the cord 27 shown in FiG. 3 can be described in a manner well known in the art as 167 tex * 2 * 3, 193 turns per meter by 114 turns per meter (1500/2/3 4.9Z * 2.9S), 2 for 1 twisted modified p-aramid co-poly (paraphenylene/3.4' oxydiphenylene terephthalamide) with balanced T.M. (twist multiplier) and chemically treated for MRG (Mechanical Rubber Goods) applications, the twist multiplier for each ply being 3.6765 and the twist multiplier for the cord being 3.7687. The cord of this invention is shown in FiG. 4. Instead of a cord 27 having three plies and two yarns, a cord 37 is utilized in the belt construction 20 as a load-carrying cord, in the same manner as described above with reference to cord 27, and for the same purposes. The cord 37 comprises five plies 38 which are twisted together in the Z direction (the spirals around the central axis slope in the same direction as the central portion of the letter Z) at a rate to approximately equal a first certain twist multiplier, with each ply 38 comprising three yarns 39 of a plurality of p-aramid fiber filaments 40 having a certain tex (denier) and being twisted together in a direction opposite to the direction of the plies 38 (so as to twisted in the S direction wherein the spirals around the central axis of each yarn slope in the same direction as the middle portion of the letter S and at a rate to approximately equal a second certain twist multiplier, each twist multiplier being equal to the quotient of the product of the turns per linear cm (inch) of twisted material multiplied by the square root of the product of the certain tex (denier) of a yarn of the fiber filaments multiplied by the total number of the yarns being twisted at that time divided by 9.58 (seventy-three). As stated above with reference to cord 27, it is known that material has been twisted in the S direction so as to have a S-twist if when the twisted material is held vertically, the material spirals around the longitudinal axis in the same direction as the middle portion of the letter S when the letter S is superimposed on the vertically held material. In contrast, the material has been twisted in the Z direction so as to have a Z-twist if when the twisted material is held vertically, the material spirals around its longitudinal axis in the same direction as the middle portion of the letter Z when the letter Z is superimposed an the vertically held material. When making the aforementioned prior known standard ply, three such yarns are twisted together in the Z direction at a rate af approximately 1.26 turns per linear cm (3.2 turns per linear inch) of twisted material, and five such plies are twisted together in the S direction at a rate of approximately 1.26 tunrs per linear cm (3.2 turns per linear inch) of twisted cord, whereby the resulting cord has an imbalanced twist multiplier, i.e., the fiber filaments have their longitudinal axes disposed substantially perpendicular to the longitudinal axis of the cord. It was found according to the teachings of this invention that when utilizing a modified p-aramid material sold under the trademark TECHNORA as previously described with reference to the cord 27, and thereby comprising copoly (paraphenylene/3,4' oxydiphenylene terephthalamide) for making a cord in exactly the same manner as the prior known standard p-aramid cord, the resulting break characteristics of such TECHNORA cord was not as good as the break characteristics of the standard p-aramid cord. In contrast, it was found according to the teachings of this invention that when the fiber filaments of the cord 37 are made of the said modified p-aramid material with each yarn 39 thereof having a tex of approximately 167 (= 1500 den) and with each ply 38 having the three yarns 39 twisted together in the Z direction on a 2 for 1 twister at a rate of approximately 1.54 turns per linear cm (3.9 turns per linear inch) of twisted material so that the twist multiplier thereof equals 3.5838 and then having five such plies 38 twisted together in the S direction on a 2 for 1 twister at a rate of approximately 0.71 turns per linear cm (1.8 turns per linear inch) of the cord so that the twist multiplier of the three plies equals 3.6986, whereby the longitudinal axes of the fiber filaments 40 are disposed generally in the longitudinal direction of the cord 37, the resulting cord 37 has improved break characteristics over the standard p-aramid cord and, thus, over the modified p-aramid cord when made in the same manner as the standard p-aramid cord. After the cord 37 was made on the 2 for 1 twister as set forth above, the cord 37 was first dipped in a bath of PAPI (polymethylene polyphenylisocyanate) and then overcoated with a coating af RFL, all in the same manner as described above with reference to cord 27. A cord 37 made by the method of this invention as previously described was found to break when approximately 476.3 kg (1050 lbs.) was applied thereto, whereas the standard p-aramid cord broke at approximately 317.5 kg (700 lbs.). It was also found that the percentage of elongation of the cord 37 of this invention was approximately 4.4% at its break point whereas the standard p-aramid cord had a 4.2% elongation at its break point. Such a cord 37 of this invention was found to have a 1% elongation when a load of approximately 98.9 kg (218 lbs.) was applied thereto and had a 3% elongation when a load of 342.5 kg (755 lbs.) was applied thereto. In contrast, the standard p-aramid cord had a 1% elongation when a load of 29.9 kg (66.0 lbs.) was applied thereto and had a 3% elongation when a load of 195.0 kg (430 lbs.) was applied thereto. Thus, it can be seen that the cord 37 of this invention has improved break characteristics over the break characteristics of the standard p-aramid cord when the cord of this invention is formed in the manner previously set forth and is twisted on a 2 for 1 twister in the manner previously set forth. From the above it can be seen that the cord 37 of this invention can be described in a manner well known in the art as 167 tex * 3 * 5, 154 turns per meter by 71 turns per meter (1500/3/5 3.9 * 1.8), 2 for 1 twisted modified p-aramid copoly (paraphenylene/3,4' oxydiphenylene terephthalamide) with balanced T.M. (twist multiplier) and chemically treated for MRG applications, the twist multiplier for each ply being 3.5838 and the twist multiplier for the cord being 3.6986. Thus, it can be seen that a cord of the invention provides a new p-aramid fiber cord for use as a component in a power transmission belt construction or the like and a new method of making the same. While the forms and methods of this invention now preferred have been illustrated and described as required, it is to be understood that other forms and method steps can be utilized and still fall within the scope of the appended claims.

Claims: A p-aramid fiber cord comprising a number of plies (38) twisted together in one direction at a rate to approximately equal a first certain twist multiplier, with each said ply (38) comprising a number of yarns (39) of a plurality of p-aramid fiber filaments (40) having a certain tex (denier) and being twisted together in a direction opposite to said one direction at a rate to approximately equal a second certain twist multiplier, each said twist multiplier being equal to the quotient of the product of the turns per linear cm (inch) of twisted material multiplied by the square root of the product of said certain tex (denier) of said fiber filaments (40) multiplied by the total number of said yarns (39) being twisted at that time divided by 9.58 (seventy-three), said yarns (39) and said plies (38) are respectively twisted on a 2 for 1 twister means so as to cause the longitudinal axes of said fiber filaments (40) to be disposed generally in the longitudinal direction of said cord (37), with said certain tex being approximately 167 (= 1500 den), characterized in that said cord (37) comprises five plies (38), with each said ply (38) comprising three yarns (39), said first certain twist multiplier being 3.6986 as the five plies (38) are twisted together at a rate of approximately 0.71 turns per linear cm (1.8 turns per linear inch) of said cord (37), said second certain twist multiplier being 3.5838 as the three yarns (39) for each said ply (38) are twisted together at a rate of approximately 1.54 turns per linear cm (3.9 turns per linear inch) of that said ply, and said p-aramid comprising co-poly (paraphenylene/3,4' oxydiphenylene terephthalamide). A p-aramid fiber cord as set forth in claim 1, characterized in that said cord (37) has been coated with material after said plies (38) have been twisted together. A p-aramid fiber cord as set forth in claim 2, characterized in that said material comprises polymethylene polyphenylisocyanate or RFL. A p-aramid fiber cord as set forth in claim 1, characterized in that said cord has first been coated with a first material comprising polymethylene polyphenylisocyanate and then has been overcoated with RFL. A method of making a p-aramid fiber cord, said cord (37) comprising a number of plies (38) twisted together in one direction at a rate to approximately equal a first certain twist multiplier, with each said ply (38) comprising a number of yarns (39) of a plurality of p-aramid fiber filaments (40) having a certain tex (denier) and being twisted together in a direction opposite to said one direction at a rate to approximately equal a second certain twist multiplier, each said twist multiplier being equal to the quotient of the product of the turns per linear cm (inch) of twisted material multiplied by the square root of the product of said certain tex (denier) of said fiber filaments (40) multiplied by the total number of said yarns (39) being twisted at that time divided by 9.58 (seventy-three), characterized by the step of twisting said yarns (39) and said plies (38) respectively on a 2 for 1 twister means so as to cause the longitudinal axes of said fiber filaments (40) to be disposed generally in the longitudinal direction of said cord (37), with said certain tex being approximately 167 (= 1500 den), said number of plies (38) being five, said number of yarns (39) being three, said first certain twist multiplier being 3.6986 as the five plies (38) are being twisted together by said twister means at a rate of approximately 0.71 turns per linear cm (1.8 turns per linear inch) of said cord (37), said second certain twist multiplier being 3.5838 as the three yarns (39) for each said ply (38) are being twisted together by said twister means at a rate of approximately 1.54 turns per linear cm (3.9 turns per linear inch) of that said ply, and said p-aramid comprising co-poly (paraphenylene/3,4' oxydiphenylene terephthalamide). A p-aramid fiber cord for use as a component in a power transmission belt construction, said cord (37) comprising a number of plies (38) twisted together in one direction at a rate to approximately equal a first certain twist multiplier, with each said ply (38) comprising a number of yarns (39) of a plurality of p-aramid fiber filaments (40) having a certain tex (denier) and being twisted together in a direction opposite to said one direction at a rate to approximately equal a second certain twist multiplier, each said twist multiplier being equal to the quotient of the product of the turns per linear cm (inch) of twisted material multiplied by the square root of the product of said certain tex (denier) of said fiber filaments (40) multiplied by the total number of said yarns (39) being twisted at that time divided by 9.58 (seventy-three), said yarns (39) and said plies (38) are respectively twisted on a 2 for 1 twister means so as to cause the longitudinal axes of said fiber filaments (40) to be disposed generally in the longitudinal direction of said cord (37), with said certain tex being approximately 167 (= 1500 den), characterized in that said cord (37) comprises five plies (38), with each said ply (38) comprising three yarns (39), said first certain twist multiplier being 3.6986 as the five plies (38) are twisted together at a rate of approximately 0.71 turns per linear cm (1.8 turns per linear inch) of said cord (37), said second certain twist multiplier being 3.5838 as the three yarns (39) for each said ply (38) are twisted together at a rate of approximately 1.54 turns per linear cm (3.9 turns per linear inch) of that said ply, and said p-aramid comprising co-poly (paraphenylene/3,4' oxydiphenylene terephthalamide). The cord as set forth in claim 6, characterized in that said cord (37) has been coated with material after said plies (38) have been twisted together. The cord as set forth in claim 7, characterized in that said material comprises polymethylene polyphenylisocyanate or RFL. The cord as set forth in claim 6, characterized in that said cord (37) has first been coated with a first material comprising polymethylene polyphenylisocyanate and then has been overcoated with RFL.

Inventors: VAN HOOK ROBERT M, VAN HOOK, ROBERT M.
Applicants: DAYCO PRODUCTS LLC, DAYCO PRODUCTS, LLC.
Application year: 1997
Main classification: D02G3
IPC codes: F16G1, D02G3, F16G5