SOLID-STATE LASER MATERIAL

Abstract: The invention pertains to the quantum electronics, specifically to materials for laser technique and is intended for use in solid state lasers with emitting wavelength of between 2.8 and 3.1 µm. The technical problem addressed by the invention is that of raising the gain of laser material, lowering the stimulation threshold of generation, increasing generation efficiency and widening the available range of the industrial generating systems with continuously variable emission wavelengths in the range 2.8 - 3.1 µm, including those operating in short-pulse generation and amplification modes. In specific embodiments, the aim of the invention is also to prevent fissures forming in the crystal, reduce scattering, improve radiation durability, decrease dissipation and reduce passive absorption. Laser material has a garnet structure and is characterized in that it contains between 0.025 formula units (f.u.) and 2.95 f.u. of holmium and in addition at least one the following elements: Li, Be, B, Na, Ca, Mg, Si, K, Ti, V, Mn, Fe, Co, Ni, Cu, Zn, Ge, Rb, Sr, Zr, Nb, Mo, W, Ta, Hf, Bi in a quantities of between 1 x 10 17 cm -3 to 5 x 10 20 cm -3 .

Description: The present invention relates to quantum electronics, namely to materials for laser techniques and is appropriated for an application in solid state lasers having a wavelength of a stimulated emission radiation in spectral range from 2.8 micrometers to 3.1 micrometers. It is known a laser material on the halogen alkali metal crystals basis. These crystals may be used as active media for the lasers with a continuously tunable emission wavelength in three micrometers spectral range. [O. Svelto, "Principles of lasers", Moscow, Eds. Mir, (1990) 560 p.]. On the Cl:KCl and Li:RbCl crystals with FA centers work lasers emitting in the 2.5-2.9 micrometers and 2.7-3.3 micrometers wavelength intervals, respectively. The limitations of the halogen alkali metals crystals are a high solubility of these crystals in water and also a decay of FA-centers at temperatures above 200 K. These factors cumber a practical application of these crystals in lasers with a continuously tunable emission wavelength. It is known a material on the garnet structure crystals basis having composition which is described by chemical formula: {Y,Er,Se} 3 [Sc,Ga,Cr] 5 (Ga) 3 O 12 [E.V. Zharikov, N.N. Il'ichev, S.P. Kalitin, V.V. Laptev, A.A. Saidov, V.A. Smimov, I.A. Shcherbakov, AF. Umyskov, "Spectral-luminescence and lasing properties of the chromium and erbium doped yttrium-scandium-gallium garnet", Kvantovaya Electronika, 1986, v. 13, N 5, pp. 975-979]. The specified material is used in lasers emitting at 2.8 micrometers wavelength. On this material the following laser parameters were presented: the lasing threshold is 50 J and the differential slope efficiency of lasing is 1% for free running mode laser operation, at 300 microseconds pumping pulse duration and at 30 % of reflection of an output mirror (R=30%). In a cavity containing a dispersive element the lasing was achieved on the separate Stark's transitions on six wavelengths: 2.64 micrometers, 2.70 micrometers, 2.80 micrometers, 2.83 micrometers, [L.A. Kulevskii, A.V. Lukashev, P.P. Pashinin, "Many-wavelength lasing at Cr:Er;YSGG crystal in the dispersion cavity", in Proceedings of All Union Conference "Physics and Applications of Solid State Lasers", 16-17 April 1990, Moscow, FIAN, p. 40-41]. The deficiency of the known laser material is that it is in principle impossible to achieve on the garnet structure containing Er 3+ ions crystals a stimulated radiation with a continuously tunable laser wavelength. The explanation of this is that the Er 3+ ions luminescence spectra consists of the separate peaks and Er 3+ ions have a small cross section value of the 4 I 11/2 ⇒ 4 I 13/2 lasing transition in the intervals between the luminescence peaks. Also are known the aluminum garnet crystals doped with holmium ions {Lu,Yb,Ho} 3 [Al,Cr] 2 (Al) 3 O 12 [A.A.Kaminskii, A.G. Petrosyan, "Sensibilized stimulated radiation on the three micrometers self-saturation transitions of Ho 3+ and Er 3+ ions in Lu, Al 5 O 12 crystals", Izv. AN SSSR, seria Neorganicheskie Materialy, v. 15, No. 3 (1979) p. 543-544]. Stimulated emission of radiation on the self-saturated three micrometers three micrometers 5 I 6 ⇒ 5 I 7 transition of holmium ions was realized for the next aluminum garnet crystals containing the Ho 3+ ions: 1. A {Lu,Ho} 3 [Al] 2 (Al) 3 O 12 crystal, the content of Ho 3+ ions is in a proportion from 0.15 to 0.3; 2. A {Lu,Yb,Ho} 3 [Al] 2 (Al) 3 O 12 crystal, the content of Ho 3+ and Yb 3+ ions is in a proportion of 0.3 and 0.3, respectively; 3. {Lu,Yb,Ho} 3 [Al,Cr] 2 (Al) 3 O 12 crystal, the proportion of Ho 3+ , Yb 3+ and Cr 3+ ions is 0.3, 0.3 and 0.006, respectively. The lasing was achieved at 60 microseconds pumping pulse duration by a Xe-lamp in a confocal (600 mm) optical cavity combined by dielectric mirrors. Lasing threshold was 40-60 for (1)-crystal and 10-11 J for (2) and (3) crystals. A decreasing of a threshold was achieved as a result of addition of the Yb 3+ and Cr 3+ ions in crystal. One of the essential limitations of that laser material is that the stimulated emission of radiation was achieved at alone 2.946 micrometers wavelength only. Laser material of garnet structure having the chemical formula: {Y,Sc,Yb,Ho} 3 [Sc,Yb,Ga,Cr) 2 (Ga) 3 O 12 and containing Ho ions in the proportion of no more than 0.013, it is possible to choose as prototype of the proposed invention. [Yu.D. Zavartsev, V. V, Osico, S.G., Semenkov, P.A. Studenikin, A.P. Umyskov, "Cascade lasing on Ho 3+ ions in the Cr 3+ :Yb 3+ :Ho 3+ :YSGG yttrium scandium gallium garnet crystals", Kvantovay a Elektronika, v. 20, N,4 (1993), p. 366-370]. The lasing was achieved according to the cascade scheme 5 I 6 ⇒ 5 I 7 ⇒ 5 I 8 on the Ho 3+ ions in the {Y,Sc,Yb,Ho} 3 [Sc,Yb,Ga,Cr] 2 (Ga) 3 O 12 crystals of garnet structure, containing a proportion of 0.012 of Ho 3+ ions. The stimulated emission of radiation was demonstrated at several wavelengths for three micrometers spectral range( 5 I 6 ⇒ 5 I 7 transition of a Ho 3+ ion). The strongest peaks were at 2.84, 2.89, and 2.93 micrometers, the laser thresholds were 16 J, 20 J, and 24 J, respectively at 350 microseconds of pumping pulse duration. The lasing was achieved at alone 2.08 micrometers wavelength, for a two micrometers spectral range ( 5 I 7 ⇒ 5 I 8 transition of a Ho 3+ ion). The laser threshold was equal to 49 J. The deficiencies of prototype are: a) a low lasing efficiency in three micrometers spectral range, which is limited by an upconversion process and resulted in a slope laser efficiency which does not exceed 0.1 %; and b) impossibility to realize a continuously tunable lasing wavelength in a wide spectral range. The technical goal of the invention is an increasing of an amplification coefficient of laser material, a decreasing of lasing threshold, an increasing of a slope efficiency of lasers of three micrometers spectral range and an expansion of the technical resources for realization of the tunable wavelength emitting for lasing in the range from 2.8 micrometers to 3.1 micrometers, including laser resources operated at oscillator and short pulse amplification modes in the spectral range from 2.8 to 3.1 micrometers. In the specific embodiments the goal of invention is also an elimination of cracking of crystal, a decreasing of dissipation, an increasing of radiation durability, a decreasing of passive absorption in a spectral range from 0.8 to 1.3 micrometers. A technical result is achieved in consequence of an upconversion process efficiency decreasing of the Ho 3+ ions resulted from the enhanced holmium concentration in crystal as compared with prototype. A decreasing of an upconversion process efficiency of the holmium ions leads to a rising of an efficiency of the holmium three micrometers lasing channel in present material as compared with analogs and prototype. A high efficiency of the holmium three micrometers lasing channel is a requirement for a realization of the Ho 3+ ions stimulated emission radiation with a continuously tunable emission wavelength in the spectral range 2.8-3.1 micrometers. In specific realization forms the technical result, namely an increasing of a slope efficiency, a decreasing of a laser threshold, and also an increasing of an amplification coefficient of laser material, is achieved as a result of increasing of a radiation durability, an elimination of cracking of crystal, a decreasing of dissipation, a decreasing of a passive absorption in the 0.8 -1.3 micrometers spectral range of presented material as compared with prototype by means of an additional supplementing into the material at least one element from the group: Li, Be, B, Na, Ca, Mg, Si, K, Ti, V, Mn, Fe, Co, Ni, Cu, Zn, Ge, Rb, Sr, Zr, Nb, Mo, W, Ta, Hf, Bi. As a radiation durability and a passive absorption is determined by a vacancy presence in the oxygen sublattice of a crystal. That vacancies are formed as a result of deficiency of gallium in crystals of garnet structure. A gallium deficiency is an inherent property of the gallium garnets. [S.E. Stokowski, M.H. Randles, and R.S. Morris, "Growth and Characterization of Large Nd, Cr: GSGG Crystals for High-Average - Power Slab Lasers", IEEE Journal of Quantum Electronics, vol. 24, (1988), pp. 934-948]. An addition into laser material the necessary quantity of the ions having the stable +4, +5 oxidation degrees (for example, an addition of Si, Ti, V, Mn, Zr, Nb, Mo, Ta, Hf, Bi, W) allows to decrease the quantity of the oxygen vacancies in a crystal. An addition into the laser material of the necessary quantity of the one- and two- valence impurities, such as Li, Mg, Ca, Na, B, Fe, Co, Ni, K, Cu, Be, Ge, Rb, Zn, Sr prevents a cracking of crystal, which is induced by a difference between the ion radius of vacancies and ions of elements. The laser material based on the known crystals of garnet structure represented by the chemical formula (A, HO) 3 [B] 2 (C) 3 O 12 where A is Yb and at least one element from the group Y, La, Ce, Gd, Lu, Sc, Tb, Eu; Ho is a holmium element: B is at least one element from the group Sc, Ga, In, Lu, Al, Gd ,Yb, Y, Cr, Tb, Eu; C is Ga or composition of the Ga and Al elements, where the quantity of Al is not more than a half of the compound, is differentiated by the holmium content in the proposed material in the proportion from 0.025 to 2.95. A lower limit of the holmium content is defined on the principle that if the Ho proportion is less than 0.025, a lasing efficiency becomes negligible thorough an increasing of an upconversion process as a result of which the metastable state consisting of the upper 5 S 2 and 5 F 4 Ho 3+ ion levels is occupied. As a result of a laser slope efficiency becomes small (less than 0.1%). The laser material according to the invention appears in claim 1. An upper limit of the holmium content is defined on the principle that at the Ho proportion of more than 2.95, an efficiency of a pumping energy transfer from the ytterbium to holmium ions is decreased that leads lo a sharp decrease of a slope efficiency to 0.1%. Laser material including holmium at the designated quantity comprises additionally at least one of the element from the group Li, Be, B, Na, Ca, Mg, Si, K, Ti, V, Mn, Fe, Co, Ni, Cu, Zn, Ge, Rb, Sr, Zr, Nb, Mo, W, Ta, Hf, Bi in proportion from 1 x 10 17 cm -3 to 5 x 10 20 cm -3 . A lower boundary for these elements is defined on the principle that the technical result consisting in a preventing of a cracking of crystal, in an increasing of a radiation durability and a decreasing of a passive absorption in 0.8 - 1.3 micrometers spectral range is not achieved at the concentrations lower than the designed limit. An upper limit for these elements is defined by a maximum possible concentration in crystals of the garnet structure. The disruption of garnet structure occurs if the element concentrations exceed a designated limit. Fig. 1 presents the dependence of the lasing energy of a N 3 crystal upon the pump energy for free running mode operation at 300 microseconds pumping pulse duration and at the different reflectivity of an output mirror (R) (curve '1' is for R= 30% and curve '2' is for 80%). For comparison on fig.1 is presented the results of the investigations which were fulfilled in the same conditions of the laser experiment for active element of the same size made from the {Y,Er,Sc} 3 [Sc,Cr,Ga] 2 (Ga) 3 O 12 crystal (curves '3' and '4' for R = 30% and R = 80%, respectively). This crystal is a second analog mentioned above. Comparison of the energy characteristics of the lasers shows that at the different reflection coefficients of the output mirrors the laser made on the N 3 crystal has less lasing threshold and the best efficiency at low pumping level comparing with the {Y,Er,Sc} 3 [Sc,Cr,Ga] 2 (Ga) 3 O 12 analog. Besides, the lasing threshold of the N 3 crystal to a lesser degree depends on an output mirror reflection coefficient, that points out at the more high amplification coefficient and accordingly the higher cross-section of a transfer. Fig. 2 shows the dependence of the amplification coefficient in the N 3 crystal (curve 1) and the Er 3+ : {Y,Sc} 3 [Sc,Cr,Ga] 2 (Ga) 3 O 12 crystal (2 curve) upon the pumping energy. The N 3 crystal has a higher gain. Fig. 3 presents the dependence of the lasing threshold of the N 6 crystal on the emission wavelength for a totally non-transmitting cavity (curve '1') and for a cavity with the output mirror characterized by R = 30% (curve '2'). Obtained data show that continuous tuning of the emission wavelength was possible in the range 2.83 - 3.05 micrometers when for a totally non-transmitting cavity (curve 1) and in the range 2.84 - 3.00 micrometers when the reflectivity of the output mirror was 30% (curve '2'). The width of the emission line was less than 30 nm. Fig. 4 gives the output energy of lasing on the N 5 crystal versus pump energy for free running mode operation when the emission took place at the different wavelengths (curve '1' is at 2.988 µm, curve '2' is at 2.856 µm, curve '3' is at 2.940 µm, curve '4' is at 2.892 µm). The pumping pulse duration was 300 microseconds, the output mirror reflectivity was equal 60%. For the output radiation wavelength selection the Ge prism was used in the laser cavity as dispersion element. A reduction in the lasing efficiency compared with a generation without dispersive element was associated with two-photon absorption, in the prism material and with the losses at the prism faces as a result of depolarization of radiation. However, these technical problems do not belong to the laser material, and they can be avoided by selecting a suitable prism material and optimizing of the cavity configuration. The growth of the garnet structure crystals were executed by means of a conventional process of a pulling from a melt. For example, for the production of the gadolinium-ytterbium-holmium-yttrium-terbium-scandium-gallium garnet crystal represented by the chemical formula {Gd,Yb,Ho,Y,Tb,Sc} 3 [Sc,Ga] 2 (Ga) 3 O 12 comprising additionally silicon and magnesium was used according to the following manner: oxide starting materials of gadolinium oxide, ytterbium oxide, holmium oxide, yttrium oxide, terbium oxide, scandium oxide, gallium oxide were precisely mixed, pressed into a tablet form, and synthesized in platinum crucible at 1200° C during 10 hours. Thereafter, the tablets were melted in an iridium crucible in a hermetic chamber in 98 vol. % N 2 + 2 vol. % O 2 atmosphere by an inductive heating. Before a crystal growth process, the silicon and magnesium oxides were added into the melt. The crystals were pulled from the melt of 300 cm 3 volume at crystal pulling rate of 4 mm/hr and a rotation rate of 40 rounds per minute. The grown crystals were gradually cooled to the room temperature during 40 hours after a tearing away from the melt. The examples of the specific compositions of the growth crystals and the prototype are adduced in Table 1. The experimental investigations of the lasing characteristics were fulfilled on active elements produced from the grown crystals. The active element was a rod of 4 mm in diameter and 55 mm long. The laser rods of the same size were made of the {Y,Sc,Yb,Ho} 3 [Sc,Yb,Ga,Cr] 2 (Ga) 3 O 12 prototype and {Y,Er,Sc} 3 [Sc,Cr,Ga] 2 (Ga) 3 O 12 analog crystals (there is the analog which does not comprise the holmium ions, but has the best lasing parameters of three micrometers spectral range generation among the known crystals of garnet structure) for comparison of lasing parameters. The laser rods had plane - parallel ends, which have no antireflection coating. The capacitance of the storage capacitors was 200 µF. Laser rod was pumped by an INP-5/45 flash lamp in an elliptic fused silica enclosure of dimensions 28 x 30 x 50 mm. The length of the illuminated part of the crystal, affected by the light, was 48 mm. The system was cooled with a 0.1 % distilled-water solution of potassium dichromate. To achieve the lasing on the separate wavelengths of three micrometers spectral range a laser cavity 200 mm long was used. A cavity was formed by a copper spherical mirror (radius of curvature 1000 mm), and a dielectric mirror which was either plane with R = 30% or spherical (radius curvature 1000 mm) with R = 80%. At the described conditions of the lasing experiments the laser based on a garnet structure holmium doped crystal has a lower lasing threshold and a higher efficiency at low pumping rates compared with an erbium containing crystal Fig. 1, and besides it has a higher gain and, consequently, a larger transition cross-section. Lasing involved several Stark sublevels participating in the 5 I 6 ⇒ 5 I 7 transition. The lasing wavelengths were: λ 1 = 2.842 µm, λ 2 = 2.888 µm, λ 3 = 2.926 µm, λ 4 = 2.962 µm, λ 5 = 2.973 µm, λ 6 = 3.057 µm. The output energy was distributed between these wavelengths in the ratio corresponding to 11%, 7%, 44%, 18%, 18% and 2%, respectively. The measurements were carried out ignoring the difference between the absorption at these wavelengths in air over an optical path of 2.5 m long. The gain for an active media was calculated from the values of a pumping energy threshold obtained for different reflection coefficients of the output mirrors. The results of calculation of the gains at 25 J pumping energy for different composition crystals are presented in Fig. 2 and compiled in Table 2. To achieve the lasing with a continuously tuning of the emission wavelength in the range 2.81 µm -3.1 µm a laser cavity was formed by a plane dielectric mirror with R = 99.8% and either a copper or a dielectric mirror with R = 30% or R = 60%, respectively. A Ge prism was used as intracavity dispersive component. The mirror rotation was used to tune the output radiation wavelength. The radiation struck the prism face at the Brewster angle and after partial reflection from the face reached a photo detector used to monitor the lasing threshold. A He-Ne laser beam was directed onto the mirror used to tune the emission wavelength of the crystal laser. The emission wavelength was deduced from the position of the reflected He-Ne beam on a special scale. A scale was calibrated with a monochromator and photodetector when a lasing was performed with R = 30% output mirror cavity. For a totally non transmitting cavity formed with R = 99.8% output mirrors a laser allows to tune continuously the output radiation wavelength in the range 2.83 µm - 3.05 µm. When the reflection coefficient of the output mirror was 30%, continuous tuning of the emission wavelength was possible in the range 2.84 - 3.00 µm, see Fig. 4. The width of the lasing line was less than 0.03 µm. For comparison, the characteristics of the grown crystals and prototype and also the results of the lasing test are adduced in Table 2.

Claims: A laser material for a solid-state laser emitting in the range of wavelength from 2.8 µm to 3.1 µm, said laser material being based on a crystal of garnet structure including Ho, and said crystal having as the chemical formula {A 3- x , Ho x } [B] 2 (C) 3 O 12 where A is a compound of Yb and at least one element from the group: Y, La, Ce, Gd, Lu, Sc, Tb, Eu; - [B] is at least one element from the group consisting of: Sc, Ga, In, Lu, Al, Gd, Yb, Y, Cr,Tb, Eu; - [C] is Ga or a composition of Ga and Al elements, in which composition the proportion of Al is not more than 0.5; wherein in said crystal of garnet structure the content of Ho in the crystal of garnet structure is between 0.025 and 2.95, i.e. the x coefficient being between 0.025 and 2.95; and said crystal of garnet structure additionally contains at least one of the elements from the group consisting of: Li, Be, B, Na, Ca, Mg, Si, K, Ti, V, Mn, Fe, Co, Ni, Cu, Zn, Ge, Rb, Sr, Zr, Nb, Mo, W, Ta, Hf, Bi in a range of concentration from 1 x 10 17 cm -3 to 5 x 10 20 cm -3 .

Inventors: STUDENIKIN PAVEL ALEXEEVICH, UMYSKOV ALEXANDR FILIPOVICH, ZAGUMENNY ALEXANDR IOSIFOVICH, ZAVARTSEV JURY DMITRIEVICH, STUDENIKIN, PAVEL ALEXEEVICH, UMYSKOV, ALEXANDR FILIPOVICH, ZAGUMENNY, ALEXANDR IOSIFOVICH, ZAVARTSEV, JURY DMITRIEVICH
Applicants: UTAR INTERNAT LTD, UTAR INTERNATIONAL LTD.
Application year: 1997
Main classification: H01S3
IPC codes: C30B15, H01S3