Method of refining metal to high degree of purity

Abstract: A method of refining metal to be processed to a high degree of purity by heat-melting the metal in a melting furnace in the form of a metal crucible (102) placed in a vacuum vessel (101). The method includes evacuating prior to melting, preheating the inside of the whole vacuum atmosphere including the inner wall surface of the vacuum vessel (101), component parts inside the vessel and the like in order to keep the total pressure within the vessel at 1 x 10 -8 Torr or lower, and effecting high-frequency induction heating while controlling the partial pressure of each of Po2, P H2 , Pco in the atmosphere inside the vessel. Further, the vacuum vessel (101), the metal crucible (102) and an induction heating coil (103) attached to the crucible (102), each of which has double jacket structure, are heated or cooled by supplying circulating hot or cooling water in a water-passage space of each of the vacuum vessel (101), the metal crucible (102) and the induction heating coil (103), so that the inside of the melting furnace is baked.

Description: BACKGROUND OF THE INVENTION Field of the Invention This invention relates to a method of refining metal, for example, iron or its alloys to a high degree of purity in an ultra-high vacuum. Background Studies on metal of ultra-high purity have steadily progressed in recent years. In order to better understand the properties of these metals, there is a need for forming these metal materials of ultra-high purity into usable shapes and establishing the technology of refining metal to an ultra-high degree of purity. The term metal in this description means metal or metal alloy. For example, a vacuum induction melting method, a floating zone melting method, etc. have heretofore been used for refining metal. These methods employ an electron beam, high-frequency induction energy and the like as a heat source. In particular, attention has been directed to the latter method as being advantageous in that there is no possibility of allowing impurities to penetrate through a refractory when the metal is melted. Recently, there has been proposed an electron-beam, floating zone melting method combining both the aforementioned methods, and the processing is normally performed in a vacuum of about 10 -6 Torr therein. Iron of the highest purity obtained according to the conventional methods usually has a resistance ratio of about 3,000. There has been proposed a method of refining metal to a high degree of purity by a vacuum induction melting apparatus for heating metal by high-frequency induction heating in a crucible made of refractory material and placed in a high-vacuum vessel. Fig. 1 shows a high-frequency vacuum induction melting apparatus which is used when metal is refined to a high degree of purity. In this apparatus, a crucible 102 made of refractory material is placed in a vacuum vessel 101, and a high-frequency induction heating coil 103 used for induction-heating the metal to be melted in the crucible is fixedly mounted around the crucible 102. In the vacuum induction melting apparatus, the crucible 102 placed in the vacuum vessel 101 is generally made by sinter-forming a metal oxide (Al 2 O 3 , MgO, CaO, etc.) and the induction heating coil 103 is wound around the crucible. Further, a high-frequency current is supplied to the induction heating coil 103 so as to melt a material (metal) in the crucible 102 by induction heating. The induction heating coil 103 is formed such that the exterior of a water- cooled copper pipe is insulated by an asbestos or glass tape and the high-frequency current can be supplied from an external high-frequency power supply 105 to the induction heating coil 103 through the water-cooled cable 104. A portion of the vacuum vessel 101 through which the water-cooled cable 104 passes has an insulation-vacuum seal structure, and a flange portion including a door The vacuum seal portion thereof is vacuum sealed with an O-ring (e.g., of fluoro rubber). In this apparatus, vacuum is achieved by a vacuum pump 106 combining an oil diffusion pump, an oil rotary pump and a mechanical booster pump together, and the attainable degree of vacuum therein is generally about 10 -5 Torr, although this varies with the influence of the gas discharged from the crucible 102 made of refractory material, the vacuum vessel 101, the water- cooled cable 104 and so on. In the use of the aforementioned conventional apparatus, the crucible made of refractory material causes inorganic compounds such as magnesia and alumina to be extracted from the surface of the crucible into the liquid metal This increases the concentration of impurities all the more. This phenomenon unavoidably occurs when metal is vacuum-refined to a high degree of purity and makes it difficult to maintain the purity of the original material. More specifically, in the use of the aforementioned conventional art, there has been the following problems particularly in the case of refining metal based on the high-vacuum induction heating technology: (1) The use of a crucible made of refractory material causes inorganic compounds to be extracted out of the crucible into mother liquid metal, and the mixture of O 2 as well as the desorption of adsorption gas (H 2 O, N 2 , O 2 ) hinders achieving an ultra-high degree of purity; (2) Organic substance (hydrocarbon) and moisture are produced from the water-cooled cable and heating-coil insulating material, which results in an atmosphere rich in H 2 O; (3) The penetration of O 2 and CO 2 through the O-ring seal portion causes oxidation of the liquid metal. Consequently, a rise in the operating pressure (degree of vacuum) ensues and particularly melting occurs in an atmosphere where the partial pressure of each of O 2 , H 2 O and CO 2 is high, thus causing metal contamination. In the case of Fe, for example, the partial pressure of O 2 in the atmosphere needs to be 1 x 10 -10 Torr or lower in order to make the concentration of O 2 in liquid iron 10ppm or lower; however, it has not been possible to achieve that degree of vacuum in the aforementioned conventional art. Moreover, the introduction of impurities from the refractory material of the crucible make it difficult to maintain the purity of the original material by the use of the conventional method of refining metal to a high degree of purity in the conventional high-frequency vacuum induction melting apparatus. JP-A-08 100 998 discloses a vacuum induction-melting vessel including a metal crucible placed there in. Such a furnace is used for melting metal under a vacuum pressure of 1 x 10 -8 torr or lower. As set forth above, the conventional technology of refining metal to a high degree of purity is problematic in that it is incapable of achieving a high degree of purity due to the limitation of the refining method and the unsatisfactory apparatus but also apt to increase the concentration of impurities in the metal. SUMMARY OF THE INVENTION Therefore, a first object of the present invention is to propose a method of refining metal to a high degree of purity by reducing the concentration of impurities so as to attain a higher degree of purity than at least the purity of the original material. To solve the aforementioned problems, the present inventors directed attention to metal crucibles in place of crucibles made of refractory material because the crucible body made of metal was free from the aforementioned impurities and gas and thus capable of melting and refining metal to a high degree of purity. However, the crucible body made of metal such as copper still developed problems arising from (1) the necessity of cooling the crucible; (2) the induction loss brought about by failure to form an electromagnetic field in the metal to be melted as the induction current on the secondary side concentrated on the wall of the metal crucible; and (3) contamination of the metal due to the H 2 O, O 2 rich atmosphere caused by moisture produced from the surface of the inner wall of the furnace, the crucible, the coil, the cable or the like. The present inventors then discovered that problem (1) could be dealt with by providing the crucible body with a water-cooled jacket structure; problem (2) was solved by inserting an insulating material in a plurality of places in the circumferential direction of the crucible so as to generate the electromagnetic field in the metal to be melted in the crucible. More specifically, the structure devised to deal with problem (2) was such that the crucible was first divided into a plurality of pillar-like segments and a slit was provided in between the segments so that the insulating material could be fitted therein. According to the present invention, a method of refining metal to be processed to a high degree of purity by heat-melting the metal in a melting furnace in the form of a crucible placed in a vacuum vessel is provided. The method includes the steps as indicated in the patent claim. BRIEF DESCRIPTION OF THE DRAWINGS Fig. 1 shows a schematic diagram of a conventional vacuum induction melting apparatus; Fig. 2 shows a graph showing the relation between the partial pressure of oxygen and iron oxide; Fig. 3 shows a graph showing the influence of various gases on a worstite layer; Fig. 4 shows a graph showing the relation between PH 2 /Pn 2 O and iron oxide; Fig. 5 shows a graph showing the relation between Pco/Pco 2 and iron oxide; and Fig. 6 shows a schematic diagram of a vacuum induction melting apparatus for use in the method, of the present invention; DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS Preliminary Studies A description will now be given of how the refining method according to the present invention has been accomplished on the basis of the results of tests made by the present inventors. Generally, pure iron hardly reduces oxygen to a solid solution in the temperature range from room temperature up to its melting temperature of (1540°C). When oxygen acts on pure iron at high temperatures, however, the form of the oxide is well known to undergo a iron (Fe) - worstite (FeO) → magnetite (Fe 3 O 4 ) → hematite (Fe 2 O 3 ) transition. Fig. 2 shows the transition of an iron oxide when the partial pressure of oxygen varies. As is obvious from Fig. 2, pure iron undergoes a transition from iron to hematite as the partial pressure of oxygen rises. In other words, when the partial pressure of oxygen is as high as over 10 -4 Torr, oxides of worstite, magnetite and hematite are thickly formed on the surface of iron and when the partial pressure of oxygen becomes about 10 -5 - 10 -9 Torr, the layers of worstite and magnetite are seen to be thinly formed thereon. When the partial pressure of oxygen Po 2 becomes 10 -10 Torr or lower in this connection, the formation of the oxide (worstite) is extremely delayed and it is possible to refine metal to a high degree of purity stably for hours to that extent. The studies made by the present inventors, however, revealed that simply raising the degree of vacuum in the atmosphere was unsatisfactory for refining metal to a high degree of purity. The reason for this is attributed to that fact that though oxygen is generally regarded as a gas for oxidizing the surface of pure iron at high temperatures, water vapor tends to more strongly oxidize the surface thereof. Fig. 3 shows the relation between the thickness of the worstite layer formed when Armco iron is heated to 1000°C and the holding time in each atmosphere. From Fig. 3, it is obvious that the formation of worstite on the surface of iron is facilitated in the order of water vapor, oxygen, air and carbon dioxide gas. In other words, water vapor subjects pure iron to high-temperature oxidation most vehemently. This is considered attributable to the fact that oxygen and hydrogen are dissociated from water vapor on the surface of iron, thus accelerating the high-temperature oxidation. Therefore, in order to refine metal to a high degree of purity, H 2 O in addition to the degree of vacuum must be controlled. Consequently, the conclusion drawn according to the present invention was that it was effective to pre-dry the vacuum atmosphere (vacuum vessel, crucible, metal to be processed) so as to remove H 2 O and control the PH 2 /PH 2 O ratio. Fig. 4 shows the relation between PH 2 /PH 2 O affecting the formation of oxides and temperatures. As shown in Fig. 4, the ratio of the partial pressure of hydrogen (PH 2 ) to that of water vapor (PH 2 O) is an important factor for the high-temperature oxidation of iron. In other words, when Po 2 is sufficiently decreased, pure iron is seen to exist stably without being high-temperature oxidized as PH 2 /PH 2 O grows greater. Therefore, the application of ultra-high vacuum technology simultaneously with control over the quantity of H 2 gas, according to the present invention, has made it possible to the PH 2 /PH 2 O ratio to 10 or higher and conduct oxidation-free refinement for many hours. In the case of a normal high vacuum refining atmosphere in this connection, when PH 2 /PH 2 O remains at about 10 -2 as shown in Fig. 4, iron forms a stable-magnetite area in a wide temperature zone. Consequently, the conventional vacuum induction melting apparatus is seen to be incapable of stably refining pure metal or iron alloy for many hours. Moreover, not only oxygen and water vapor but also carbon dioxide gas to a lesser extent, subjects iron to high-temperature oxidation. In other words, oxygen and carbon monoxide gas are dissociated from carbon dioxide gas and this makes the high-temperature oxidation proceed. Consequently, control of the carbon dioxide gas is another aspect according to the present invention. As shown in Fig. 5, pure iron is kept stable even at high temperatures when the ratio of the partial pressure of carbon monoxide (Pco) to that of carbon dioxide (Pco 2 ) is positive and grows higher. In the conventional technology, magnetite is stable since Pco/Pco 2 is about 10 -1 . According to the present invention, the Pco/Pco 2 ratio is set to 10 or higher so that metal iron is stable in this zone. As set forth above, not only the degree of vacuum in the refining atmosphere but also the concentration of oxygen, water vapor and carbon dioxide gas is seen to seriously affect the high-temperature oxidation of iron when metal is refined to a high degree of purity. Therefore, according to the present invention, the relation between the vapor pressure of iron and iron oxide and temperatures in addition to, as occasion demands, control of the degree of vacuum, the concentration of O 2 , H 2 O and CO 2 is taken into consideration for control purposes. For example, the development of the ultra-high vacuum refining technology was based on the conclusion that the preferred condition of carrying out the refining of pure iron for many hours was to make the total pressure in the refining atmosphere in the vacuum vessel an ultra-high vacuum zone at 10 -8 Torr or lower simultaneously with setting Po 2 at 10 -10 Torr or lower, PH 2 /PH 2 O at 10 or higher, and Pco/Pco 2 at 10 or higher. The present inventors also studied the influence of the refractory of the crucible on the refining for increasing purity. The refractory of the crucible contains impurities such as Cl, S, Pb, C and so on, to say nothing of oxides and also makes unavoidable the generation of O simultaneously when the component element (metal) is introduced. Moreover, the oxides in the components are dissociated from the refractory material of magnesia and act on the liquid iron so as to supply O to the liquid iron. An example of the reaction is given by the following expression: MgO(s) = Mg(g) + 2O 2 (g) In other words, as shown by the expression above, O is dissociated from the oxides such as MgO, Al 2 O 3 , SiO 2 , CaO contained in the refractory material and is incorporated into the liquid iron. Further, the liquid iron and the refractory material directly react with each other, thus producing O as follows: Fe(1) + MgO(s) = Mg(g) + O In other words, the concentration of oxygen in the liquid metal is raised through this reaction. With respect to the crucible, further, the corrosion of the refractory material due to C in the liquid iron occurs and carbon monoxide is produced through the reaction given by the following expression: SiO 2 (s) + 2C = Si + 2CO(g) Thus, the limitation of deoxidation of the liquid iron due to C or H becomes considerably greater than a theoretic value and often what is of the 100ppm class since O is supplied to the liquid iron because of the dissociation of the oxide in the component constituting the refractory material and its reaction with the liquid iron in the case of the melt-refining reaction in the crucible made of refractory material. When the melt-refining is carried out in the crucible made of refractory material, moreover, the metal component in the refractory material tends to be extracted into the liquid iron and particularly regarding SiO 2 in the refractory material, Si reacts with Fe and becomes easily and rapidly soluble in Fe. Consequently, a metal crucible that can be water-cooled is employed according to the present invention, so that the metal can be refined to a high degree of purity without the influence of the aforementioned refractory material Under the ultra-high vacuum employed in the refining method according to the present invention, all of the impurity elements whose vapor pressure is higher than that of Fe are removable by evaporation. Since the vapor pressure of Fe at 1600°C is 0.039 Torr, substances such as Al, Cu, Mg, Zn, C whose vapor pressure are higher than that of Fe may be removed by evaporation. Although the vapor pressure of FeO, in particular, is lower than that of Fe the specific gravity of FeO is about 70% of Fe and as the impurities tend to concentrate on the surface, it is quite possible that the impurities are removable by evaporation. Even with removal of impurities by evaporation, the mean free path should be followed with the degree of vacuum at the several m class so as to prevent the evaporation from being suppressed because of the vapor which remains on the surface of liquid metal. In this regard, since the evaporation of oxides constituting the refractory material occurs when the crucible is made of the conventional refractory material, the vapor pressure of the oxide on the surface of lipid metal rises and this makes it difficult to remove the impurities in the liquid metal by evaporation. Embodiment Referring to Fig. 6, there will be given the description of a vacuum induction melting apparatus for putting the aforementioned method into practice. The apparatus chiefly includes a vacuum vessel 1, an induction heating type melting furnace 2 in the form of a crucible contained in the vacuum vessel, a vacuum pump 3, a high-frequency power supply 4 and a heat exchanger 5. The vacuum vessel 1 is of double jacket structure which is advantageous for uniform heating In order to effect preheating (baking) prior to the melting operation, cold water or hot water (from room temperature to about 110°C) from the heat exchanger 5 in an external water circulating system can be supplied to the jacket. With this hot-water jacket structure the entire: contents of the vacuum vessel 1 can be kept at 60°C or higher, so that water vapor is removed from the surfaces of the vessel and various parts (crucible, wire cable, coil, and other parts) thereof. A heater may be used for any one of the component parts (e.g. , observation window and vapor deposition preventive plate) where hot water is not utilizable. The melting furnace 2 includes a water-cooled metal crucible 2a and a high-frequency induction heating coil 2b surrounding the crucible, these being water-cooled with the cooling water supplied from the heat exchanger 5. The crucible 2a is preferably made of non-magnetic metal such as copper and more preferably of such a type that is divided into a plurality of circumferential segments so that a ceramic material or the like can be held between the segments. The vacuum pump 3 may be any pump capable of keeping the whole vessel pressure at 1 x 10 -9 Torr or lower, the vacuum pump being a vacuum exhaust system equipped with a cold trap of liquid nitrogen class advantageous for the exhaust of H 2 O. Further, equipment for introducing nitrogen gas for recovering the atmospheric pressure, Ar gas for regulating the atmosphere in the vessel and H 2 gas for controlling the PH 2 /PH 2 O, together with the vacuum exhaust system is added to the vacuum vessel 1. In this case, it is essential to perform the operation in such a manner that the partial pressure of O 2 in the vacuum exhaust system is lowered at all times because the degree of vacuum on the order of 1 x 10 -10 Torr is unobtainable unless O 2 is prevented from penetrating through the door seal O-ring), the coil seal (O-ring) or a seal using inorganic material and plastic insulating material Preferably, as shown in Fig. 6, the partial pressure of O 2 may be lowered by sealing the inlet portion of the induction heating coil 2b with insulating material of glass or ceramics together with organic insulating material (hard to crack) such as Teflon to provide a N 2 purging area 6 between the interior of the vessel and the outside (atmosphere). In addition, the vacuum vessel 1 is provided with an observation window 8 that can be heated with a heater 7 and a vapor deposition preventive plate 9 for preventing evaporating metal from being deposited on the window in order to maintain visibility, the vapor deposition preventive plate being situated in the vessel under the observation window 8. Further, reference numeral 10 denotes a control-gas introducing port for introducing H 2 , Ar, N 2 and the like; and 11, any kind of sensor with a heater. Reference Example The vacuum induction melting apparatus shown in Fig. 6 was used to refine pure iron in this example. In the melting furnace 2 of the vacuum induction melting apparatus used in this case, no refractory material was used for the crucible 2a but a water-cooled metal crucible was employed instead, and the induction heating coil 2b was of such a type that no insulating material was used. For example, the crucible 2a with slits was supplied with power from a high-frequency power supply via an induction heating coil. The reason for the crucible like this to be employed according to the present invention is that problems originating from refractory material as stated above can be eliminated. Since dissolved oxygen uniformly appears on the surface as the molten metal is vigorously stirred in the metal crucible, refining action such as reduction smoothly proceeds. First, the vacuum vessel 1 was evacuated with the vacuum pump 3 to attain a target degree of vacuum (1 x 10 -8 Torr or lower) in the vacuum vessel 1. Subsequently, the vacuum vessel, the metal melting furnace, the induction heating coil, the water-cooled cable were preheated by supplying hot water (≥60°C) from the hot-water generator 5a of the heat exchanger 5 to the jacket of the vacuum vessel 1 before the melt-refining operation was started. By the preheating (baking) prior to the melting operation, removal of H 2 O from all surfaces of parts (e.g., the inner wall of the vessel, the crucible, the heating coil, etc.) within the vacuum vessel 1 was attempted, so that no H 2 O was produced in the vessel during the melting operation. This preheating (baking) can effectively operate to prevent the re-adsorption of the gas extracted from the surface of the cooled crucible into the molten metal during the melting operation. Then power was supplied from the high-frequency power supply 4 to the induction heating coil 2b so as to melt the metal (iron) in the crucible. As a result of refining under the melting conditions above, the quantity of emission gas was found lower by two digits than the quantity thereof in the ordinary vacuum induction melting furnace in this example; namely, the partial pressure of oxygen Po 2 was reduced to 1 x 10 -10 Torr. The apparatus used was equipped with a vacuum exhaust pump of such type that the total pressure was reducible to 1 x 10 -10 Torr or lower and included at least a cold trap of the liquid nitrogen type. Moreover, the cold trap forcibly exhausts H 2 O, and H 2 is introduced so that the PH 2 /PH 2 O ratio could be increased. This refining operation was performed through the steps of using the water-cooled metal crucible, baking the vacuum vessel, the metal crucible and the melting material, considerably decreasing the H 2 O gas as the principal component in the vacuum atmosphere, and creating a reduction atmosphere by the H 2 introducing equipment, whereby melting of metal of high purity without oxidation is achieved. Moreover, the removal of impurity and gas components in the liquid metal by evaporation during the melting operation was promoted by controlling the total pressure in the refining atmosphere within the vacuum vessel and the mean free path so that the total pressure and the stroke became 1 x 10 -3 Torr or lower and several m or greater, respectively. A description will subsequently be given of an example in which iron was melted and refined to a high degree of purity under the refining method according to the present invention. Table 1 shows analysis values of components of the melting materials (raw iron) used in the example. Table 2 shows refining results when the melting materials were not subjected to baking as an essential condition according to the present invention. The quantity of oxygen is still considerably large in the refining and melting tests. Table 3 shows a comparative example for ingots refined in the vacuum induction melting apparatus with baking applied to the ingots materials. However, in this example, the apparatus exhibited a slight vacuum leakage due to leakage from the sealing portion. Further, attainable degrees of vacuum during the refining operation is also shown in Table 4. components partial (Torr) components partial (Torr) H 2 7.7 X 10 -11 O 2 9.1 X 10 -10 H 2 O 4.6 X 10 -10 Ar 7.6 X 10 -11 N 2 1.3 X 10 -9 CO 2 3.9 X 10 -11 CO 1.9 X 10 -10 total pressure 3.5 X 10 -9 As is obvious from the results shown in tables 3 and 4, the quantity of oxygen in the components is large in this example because the partial pressure of oxygen is slightly high and because PH 2 /PH2O is low. However, Al, C, Cd, H, Mg, N, Pb were lower and when baking is carried out even though there occurred leakage to some extent, it was found that considerable improvement was made in comparison with the preceding example with the omission of baking. Subsequently, the apparatus shown in Fig. 6 was tested in such a manner as to satisfy all the refining conditions of the invention. More specifically, iron was subjected to vacuum refining (especially deoxidized) under the refining conditions including: (1) setting the partial pressure of oxygen at 1 x 10 -10 Torr or lower; (2) suppressing the production of H 2 O in order to secure PH 2 /PH 2 O at least 100 or higher, (3) allowing H 2 O to be generated to the extent that not less than 1m of the mean free stroke was secured when H 2 was introduced with PH 2 /PH 2 O set at 100 or higher; (4) suppressing the generation of CO 2 so as to secure CO/CO 2 at 10 or higher or lowering the generation of CO 2 so as to suppress the oxidizing reaction; (5) providing the water-cooled metal crucible equipped with slits for cooling the crucible by passing water therethrough and practically dispensing with a refractory material in contact with the liquid metal; and (6) putting into practice the refining and melting method for the melting material in the crucible by induction heating. Table 5 shows analysis values of ingots obtained under this refining method. Further, attainable degrees of vacuum during the refining operation is also shown in Table 6. components partial (Torr) components partial (Torr) H 2 5 X 10 -9 O 2 1 X 10 -10 H 2 O 5 X 10 -10 CO 2 4 X 10 -11 N 2 5 X 10 -10 CO 2 X 10 -10 total pressure 7 X 10 -9 As shown in Tables 5 and 6, the refining method conforming to the present invention exhibited excellent results. As set forth above, according to the present invention, it is possible to refine metal to an extremely high degree of purity. Using the method according to the present invention, C on the order of 10ppm can be reduced to the order of 1ppm on condition that 0 in the liquid metal is 30ppm or greater and deoxidizing refining with the addition of H 2 is feasible. Since the crucible is made of low-temperature metal such as water- cooled copper, no solution of metal and no supply of 0 occurs and consequently metal can be refined to a high degree of purity very close to the theoretic value.

Claims: A method of refining metal to be processed to a high degree of purity, said method comprising the steps of: providing a vacuum vessel including a metal crucible placed therein, and metal in the crucible; evacuating the vacuum vessel to produce a vacuum atmosphere; preheating the whole vacuum atmosphere including an inner wall surface of the vacuum vessel and parts inside the vacuum vessel to desorb water vapor from the vacuum atmosphere; degassing from the metal in order to keep the total pressure within the vacuum vessel at 1 x 10 -8 Torr or lower; and effecting high-frequency induction heating to the crucible while controlling an attainable degree of vacuum in the refining atmosphere to keep the partial pressure of oxygen (PO 2 ) at 1 x 10 -10 Torr or lower, to keep the partial pressure of hydrogen (PH 2 ) at such a level so that the ratio of the partial pressure of hydrogen (PH 2 ) to the partial pressure of water ((PH 2 O), PH 2 / PH 2 O is 10 or higher, and to keep the partial pressure of carbon monoxide (Pco) at such a level that the ratio of the partial pressure of carbon monoxide (Pco) to the partial pressure of carbon dioxide (Pco 2 ), Pco/Pco 2 , is 10 or higher.

Inventors: ABIKO KENJI, ASHINO YOSHIHIRO, HARADA MASANOBU, KAWANO HITOSHI, NAKAI YASUHIRO, NAKAJIMA TADAHITO, TSUDA MASANORI, ABIKO, KENJI, HARADA, MASANOBU, KAWANO, HITOSHI, NAKAI, YASUHIRO, NAKAJIMA, TADAHITO, TSUDA, MASANORI, Ashino Yoshihiro c/o ULVAC-PHI, Inc., Kawano, Hitoshi c/o Ise Works of, Nakai, Yasuhiro c/o Ise Works of, Nakajima, Tadahito c/o Ise Works of, Tsuda, Masanori c/o Ise Works of
Applicants: ABIKO KENJI, SHINKO ELECTRIC CO LTD, ABIKO, KENJI, SHINKO ELECTRIC CO. LTD.
Application year: 1997
Main classification: C22B9
IPC codes: F27D9, C21C7, F27B14, C21C5, C22B9, F27D7, F27B17