WOOD PRESERVATIVES

Abstract: Wood preservatives having biocidal properties which comprise quaternary ammonium compounds of general formula (I) are described. In this formula, R<1> is a C8-18-alkyl group or an optionally substituted benzyl group, R<2> is a C8-18-alkyl group, R<3> is a C-1-4-alkyl group or a group of the formula -[CH2-CH2-O]n-H, R<4> is a C1-4-alkyl group, n is a number from 0.5 to 8, preferably from 1 to 5, and A<-> is the anion of an organic carboxylic acid which contains 2 to 12 C atoms and carries at least one hydroxyl, amino or sulphonic acid group. The wood preservatives according to the invention also penetrate deeply into the wood without the use of pressure, and have only a mild corrosive action on metals. Furthermore, this invention refers to a process for treating timbers with these compositions, concentrates for the preparation thereof, the use of new and known quaternary ammonium compounds in wood preservatives and new quaternary ammonium compounds and their use as biocides.

Description: preserva ves The present invention relates to wood preser¬ vatives based on quaternary ammonium compounds, a process for treating timbers with these compositions, concen- trates for the preparation thereof, the use of new and known quaternary ainmonium compounds in wood preser¬ vatives, and new quaternary ammonium compounds and their use as biocides. The biocidal properties of quaternary ammonium compounds (QAC) , in particular their activity against fungi and bacteria, are generally known. Corresponding references can be traced back to the start of the nineteen thirties. A particular property of QAC is their ability to add relatively firmly on to the most diverse substrate surfaces, because of their charge and surface activity. This addition is also decisive for the duration of their action, for example in the field of surface disinfection. However, this property is a disadvantage if QAC solutions are to penetrate deeply into a porous substrate, such as, for example, wood. In this case, the deβired deep action is prevented by the rapid and complete absorption in the region close to the surface. This is also a reason why QAC are employed comparatively little in wood preservatives, especially if the wood preservatives are those which are to be applied in a process without pressure, such as dipping, trough impregnation, flooding, brushing or spraying. However, because of their toxicological acceptability compared with other wood preservatives, the use of QAC would be desirable precisely in the indoor area. The object of the present invention was therefore to provide a wood preservative based on quaternary ammonium compounds which also penetrates easily and deeply into wood or other porous substrates without the use of pressure. This object is achieved according to the inven¬ tion by the wood preservative according to Patent Claim 1. It has been found, surprisingly, that the penetration depth and the distribution of the active compound in wood and wood materials, and also in other porous substrates, are influenced substantially by the properties of the anion. QAC are usually employed in the form of the chlorides and bromides, which is chiefly due to the nature of their preparation. Some QAC which contain anions of simple aliphatic carboxylic acids, such as acetate or propionate, are also known. Surprisingly, the penetration capacity of QAC increases to a signifi- cant extent if, instead of anions of unsubstituted carboxylic acids, anions of low molecular weight carboxy¬ lic acids having from 2 to 12 carbon atoms which also carry, in addition to the carboxyl group, at least one hydroxyl group, amino group or sulphonic acid group (sulpho group) are employed. These carboxylic acids can be aliphatic (linear or branched) , alicyclic or aromatic in this case. The quaternary ammonium compounds according to the invention can be represented by the general formula In this formula: R 1 is a C„_ 1B -alkyl group or an optionally substituted benzyl group, R 2 is a C β . lβ -alkyl group, R 3 is a C α . 4 -alkyl group or a group of the formula - [CH 2 -CH--0] n -H, R* is a C^-alkyl group, n is a number from (as a statistical average) 0.5 to 8, preferably 1 to 5, and A " is the anion of an organic carboxylic acid which contains 2 to 12 carbon atoms and carries at least one hydroxyl, amino or sulphonic acid group. C β . nT alkyl groups are to be understood as meaning linear or branched alkyl groups having m to n carbon atoms. In this connection, C β . 18 -alkyl is also to be understood as the mixtures of different chain lengths obtainable from natural sources, such as, for example, coconut fatty acid, in which small contents of unsatu¬ rated radicals or traces of shorter- or longer-chain radicals can optinally be present. Examples of suitable substituents of the benzyl group are halogen (preferably chloro), Cι_4~alkyl (preferably methyl), Cι_4-alkoxy (pre¬ ferably methoxy) , hydroxy, amino, Cχ_4~alkyl amino (pre¬ ferably methylamino) and di(Cι ^ _4-alkyl)amino (preferably dimethylamino) . One or more of such substituents are possible, which can be the same or different. Organic carboxylic acids containing 2 to 12 carbon atoms which carry at least one hydroxyl, amino or sulphonic acid group are to be understood as meaning both aliphatic or cycloaliphatic and aromatic carboxylic acids. Carboxylic acids which carry one hydroxyl or amino group are preferred. Lactic acid or the lactate ion, hydroxyacetic acid (glycolic acid) or the hydroxyacetate ion, simple amino acids, such as aminoacetic acid (glycine) or the aminoacetate ion (glycinate ion) , a- and /3-alanine or the 2-aιaino- and the 3-aminopropionate ion, and o-, m- and p-hydroxybenzoic acid or the corresponding hydroxybenzoate ions are particularly preferred. These anions have proved to be particularly active in the context of the invention. Particularly preferred cations are N,N-dimethyl- N-benzyl-N- (coconut alkyl)ammonium, N,N-didecyl-N-methyl- N- (polyoxyethyl)ammonium or N,N-didecyl-N,N-dimethyl- ammonium. l^N-Di-Cg.^-alkyl-N-C^-alkyl-N- (polyoxyethyl) - ammonium salts are known compounds and are accessible by a process described in DE-A 33 19 509. The other QAC which can be employed according to the invention can be prepared from the corresponding chlorides by a method described in WO-A 94/28715 (pages 13-14), analogously to the compounds disclosed therein. The chlorides are known compounds and are commercially obtainable in some cases. The wood preservatives according to the invention can also comprise the QAC equipped with corresponding anions in combination with one or more additional biocides. Suitable additional biocides are, for example: Amphosurfactants having a biocidal action, Methyl, benzimidazole-2-carbamate, 1,2-Benzisothiazol-3-one, Biguanides having a biocidal action, Organic and inorganic boron compounds, α-tert-Butyl-α- (p-chlorophenethyl) -lH-1,2,4- triazole-1-ethanol, (2-sec-Butylphenyl) N-methylcarbamate, (±) -cis-4- [3- (tert-Butyiphenyl) -2-methylpropyl] -2, 6- dimethylmorpholine, 5-Chloro-2-methyl-4-isothiazolin-3-one, 1- (6-Chloro-3-pyridinyl) -methyl-4, 5-dihydro-N-nitro- lH-imidazol-2-amine, Chlorohexidine and salts thereof, Chlorinated phenols, such as tetra- and pentachlorophenol , Chloronitrobenzene derivatives, 1- (4-Chlorophenyl) -3- (2, 6-dif luorobenzoyl) -urea, N- Cyclohexyl -N-methoxy-2 , 5 -dime thy 1 fur an- 3 - carboxamide, Di- (guanidino-octyl) -amine, Cyano- (3 -phenoxyphenyl) methyl 2 , 4 -dichloro-α- (1 -methyl ethyl) -phenylacetate, Cyano- ( 3 -phenoxyphenyl ) me thyl 4-chloro-α- (1 -methyl ethyl) -phenylacetate (f envalerate) , a- [2- (4-Chlorophenyl) -ethyl] -a- (1, 1- dime thyl ethyl) - 1H-1, 2,4-triazole-l-ethanol, Cyano- ( 4 - fluoro- 3 -phenoxyphenyl ) methyl 3- (2 , 2-dichloroethenyl) -2 , 2-dimethylcyclopropane-l- carboxylate , Cyano- (3 -phenoxyphenyl) methyl (1R,3R) -3- (2,2- dibromoethenyl) -2,2 - dime thyl eye lopropane - 1 - carboxylate (deltamethrin) , Cyano- (3 -phenoxyphenyl) methyl 3 - (2,2 -dichloro- ethenyl) -2,2 - dime thy lcyc lopropane- 1 -carboxylate (cypermethrin) , 3 -Phenoxyphenyl) me thyl 3- (2 , 2 -dichloroebhenyl) -2,2- dimethylcyclopropane-1- carboxylate (permethrin) , 1- { [2 - (2 , 4-Dichlorophenyl) -1, 3 -dioxolan- 2 -yl] - methyl} -1H-1, 2 , 4- triazole, l-{ [2 ^(2, 4-Dichlorophenyl) -4-propyl-l, 3 -dioxolan-2- yl] methyl} -1H-1, 2 , 4- triazole, 0,0-Diethyl O- (α-cyanobenzylideneamino) thiophos- phate (phoxim) , 0,0-Diethyl O- (3,5, 6-trichloro-2-pyridyl) thionophosphate (chlorpyriphos) , 0,0-Diethyl S- (6-chloro-2, 3-dihydro-2-oxobenzoxazol- 3-yl)methyl dithiσphosphate (phosalone) , 0,0-Dimethyl S- [2- (me thylamino ) -2-oxoethyl] dithiophosphate (dimethoate) , 0,0-Dimethyl S- (N-phthalimidomethyl) dithiophosphate (phosmet) , N,N-Dimethyl-N' -phenyl-N' - ( f luoromethyl thio) - sulphamide, N, N- Dime thyl -N' - tolyl-N' - ( f luoromethyl thio) - sulphamide, 3,5 -Dime thyl tetrahydro-1 , 3,5- thiadiazine- 2 - thione , Dimethylalkylamine salts, Dithiocarbamates (metal and amine salts) , 2- (2-Furanyl) -lH-benzimidazole, Halogenoacetic acids and amides and esters thereof, 6, 7, 8, 9, 10, 10-Hexachloro-l,5,5a, 6,9, 9a-hexahydro- 6 , 9 -methano- 2,4,3 -benzodioxathiepine 3 -oxide (endosulfan) , Hexachlorocyclohexane, 8-Hydroxyquinoline, the copper salt thereof and halogenated derivatives thereof, 2-Iodobenzoanilide, 1-Naphthyl N-methylcarbamate, 2 -Methyl-4-isothiazolin-3-one, Methylene bisthiocyanate, Nitroalkanols having biocidal action, N-Nitroso-N-cyclohexylhydroxylamine and salts thereof, N-Nitroso-N-phenylhydroxylamine and salts thereof, 2-N-Octyl-4-isothiazoline-3-one, Organotin compounds, such as, for example, tributyl- tin oxide and tributyltin benzoate, Phenylphenols, (2-Isopropoxyphenyl) N-methylcarbamate, Pyridine-2-thiol 1-oxide and salts thereof, Salicylanilide and halogenated derivatives thereof, Tetrachloroisophthalodinitrile, 2- (Thiazol-4-yl) -benzimidazole, 2- (Thiocyanomethyl) -thiobenzothiazole, 1- (1,2,4-Triazol-l-yl) -1- (4-chlorophenoxy) -3,3- dimethylbutan-2-ol, 1- (1,2,4-Triazol-l-yl) -1- (4-chlorophenoxy) -3,3- dimethylbutan-2-one, N- (1, 1,2,2-Tetrachloroethylthio) -3, 6,7, 8-tetrahydro- phthalimide, N - ( Tr i chl o rome thy l t h i o ) - 3 , 6 , 7 , 8 - tetrahydrophthalimide, N- (Trichloromethylthio)phthalimide, N-Tridecyl-2, 6-dimethylmorpholine. Particularly preferred additional biocides are copper compounds and zinc compounds. The wood preservatives according to the invention are advantageously prepared and transported as concen¬ trates having a content of 5-90% by weight of the quaternary ammonium compound (I) . These concentrates comprise water as the solvent and, if appropriate, other solvents and/or other biocides or auxiliaries. The other solvents include, for example, water-miscible solvents, such as lower alcohols and glycols, and esters and ethers thereof, which are used as solubilizing agents and/or to lower the freezing point. Auxiliaries which can be employed are, for example, defoamers, antioxidants, dyestuffs or fragrances. The wood preservatives according to the invention are advantageously used in a 2-20% strength aqueous solution of the concentrates, corresponding to a QAC concentration of 0.1-10%, and in particular preferably by trough impregnation. The wood to be preserved is stored in the solution for some hours to days. After absorption of 20-80 g of concentrate per square metre of wood surface, permanent protection against wood-destroying organisms is achieved, in particular against higher fungi from the -sub-classes Ascomycetes (asco fungi) and Basidiomycetes, wood-discolouring fungi (blue stain fungi) and wood-destroying insects, such as Anobium species or the longhorn beetle. Wood protected in this way complies with the requirements of hazard classes 1 to 3 in accordance with DIN 68 800 Part 3 and EN 599 and is suitable both for the indoor and for the outdoor area. Surprisingly, it has been found that the penetra¬ tion-ready QAC according to the invention are suitable for also transporting other biocidal active compounds deep into the substrate, so that these QAC, in particular the lactate and the hydroxy acetate, for example, are also suitable as entraining agents in the biocidal treatment of leather. The QAC according to the invention show further advantageous and in some cases unexpected properties during formulation. • The lactates, hydroxyacetates and hydroxybenzoates show a relatively high compati¬ bility with other substances in the formulation, for example with dyestuffs, pigments, waxes and the like. • The corrosive action, in particular on iron and iron alloys, of the QAC according to the inven¬ tion is lower than in the case of the corresponding halides by a factor of 5-10. • It has been found, completely unexpectedly, that the biological action is higher than could be expected on the basis of the knowledge of conven¬ tional QAC with a halide anion. The following examples are intended to describe the nature of the formulation of the wood and material preservatives according to the invention in more detail . The recipe for the concentrate is given in each case. All data are in percentages by weight in each case. Example 1 Wood preservative for immersion treatment of structural wood 20% of N,N-didecyl-N,N-dimethylammonium hydroxyacetate 80% of water Example 2 Wood preservative for dipping treatment of structural wood in the tropics 40% of N,N-didecyl-N-methyl-N- (polyoxyethyl)ammonium lactate 10% of diethylene glycol monobutyl ether 50% of water Example 3 Deep preservative for wood in the outdoor area 20% of N,N-didecyl-N-methyl-N- (polyoxyethyl) ammonium lactate 10% of copper hydroxycarbonate 40% of monoethanolamine 30% of water Example 4 Deep preservative for wood in the outdoor area 25% of N,N-didecyl-N-methyl-N- (polyoxyethyl) ammonium hydroxyacetate 10% of zinc acetate, anhydrous 20% of diethanolamine 2% of o-phenylphenol 43% of water The depth of penetration in the wood in the examples mentioned is 5-10 mm, so that comprehensive deep preservation is ensured. Examples 5-9, Comparison Examples V1-V4 The following table 1 shows, by way of example, how the replacement of the halide ions by anions of simple carboxylic acids (acetate, propionate; not according to the invention) or, according to the inven¬ tion, by anions of hydroxy- or aminocarboxylic acids has an effect. The QAC used in this example were the N,N-dimethyl-N-benzyl-N- (coconut alkyl) ammonium cation (I) and the N,N-didecyl-N-methyl-N- (polyoxyethyl)ammonium cation (II) . Fine sapwood blocks of dimensions 2.5 cm x 5.0 cm x 12 cm were impregnated with the QAC shown in the table by immersion in an aqueous solution of in each case 5% strength. The immersion time was a standard 24 hours (at 20°C) . Table 1 The results clearly show that, for example, the lactate and the hydroxyacetate (glycolate) are particu¬ larly suitable for formulation and preparation of wood preservatives. Examples 10-11, Comparison Examples V5-V7 Bars of beechwood (1 cm x 1 cm x 40 cm) were impregnated by immersion in a 0.5% strength solution of the QAC for 24 hours and then tested by the soil burying method according to Schwammkeller. For this, treated and untreated timbers were buried in fungus-infested soil (forest soil) . The service life here is defined as the time after which the flexural breaking strength has fallen to 25% of the initial value of (untreated) com¬ parison timbers of the same dimensions and type of wood. The results are summarized in the following Table 2. Table 2

Claims: Patent Claims 1. Wood preservative having biocidal properties, characterized in that it comprises, in aqueous solution, at least one quaternary ammonium compound of the general formula wherein R 1 is a C β _ 18 -alkyl group or an optionally substi¬ tuted benzyl group, R 2 is a C β . 18 -alkyl group, R 3 is a C^-alkyl group or a group of the formula - [CH--CH--0] n -H, R* is a C^,,-alkyl group, n is a number from 0.5 to 8, preferably from 1 to 5, and A " is the anion of an organic carboxylic acid which contains 2 to 12 C atoms and carries at least one hydroxyl, amino or sulphonic acid group, and one or more other biocides and/or one or more auxiliaries from the group consisting of defoamers, antioxidants, dyestuffs or fragrances, and if appropriate one or more water-miscible organic solvents. 2. Wood preservative according to Claim 1, charac¬ terized in that A * is lactate, hydroxyacetate (glycolate), aminoacetate (glycinate), 2 - or 3-amino- propionate {a- or β-alaninate) or o-, m- or p-hydroxybenzoate. 3. Wood preservative according to Claim 1 or 2, characterized in that it contains N,N-dimethyl-N-benzyl- N- (coconut alkyl) ammonium, N,N-didecyl-N-methyl-N- (poly- oxyethyl) ammonium or N,N-didecyl-N,N-dimethylammonium as the cation. 4. Wood preservative according to one of Claims 1 to 3, characterized in that it comprises at least one other biocide. 5. Wood preservative according to Claim 4, charac¬ terized in that it comprises at least one copper compound and/or zinc compound as another biocide. 6. Process for the treatment of timbers against wood-destroying fungi and/or insects, characterized in that the timbers to be treated are impregnated with the wood preservative according to one or more of Claims 1 to 5. 7. Concentrate for the preparation of a wood pre- servative according to one or more of Claims 1 to 5, characterized in that it comprises 5-90% by weight of a quaternary ammonium compound of the general formula wherein R 1 to R 4 and A' have the meanings given in Claim 1, and water, one or more other biocides and/or one or more auxiliaries from the group consisting of defoamers, antioxidants, dyestuffs and fragrances, and if appropriate one or more water-miscible organic solvents. 8. Use of quaternary ammonium compounds of the general formula R 1 R—N—R 2 A I, wherein R 1 to R* and A " have the meanings given in Claim 1, as the active compound in compositions for treatment of porous substrates against attack by fungi and/or insects, in particular in wood preservatives. 9. Quaternary ammonium compound of the general formula wherein R 1 , R 2 , R 4 and A " have the meanings given in Claim 1 and R 3 is a C j .,,-alkyl group. 10. Quaternary ammonium compound according to Claim 9, characterized in that R 1 is a C„_ 14 -alkyl group, a coconut alkyl group or a benzyl group and R 2 ie a group or a coconut alkyl group and R 3 and R< are methyl groups. 11. Quaternary ammonium compound according to Claim 10, characterized in that R 1 is a benzyl group and R : is a coconut alkyl group. 12. Quaternary ammonium compound according to Claim 10, characterized in that R 1 and R 2 are decyl or dodecyl groups. 13. Quaternary ammonium compound according to one of Claims 9 to 12, characterized in that A" is lactate, hydroxyacetate (glycolate) , aminoacetate (glycinate) , 2-amino- or 3-aminopropionate (a- or 0-alaninate) or o-, m- or p-hydroxybenzoate. 14. Use of the quaternary ammonium compounds according to Claims 9 to 13 as biocides.

Inventors: FRITSCHI JOACHIM, LICHTENBERG FLORIAN, RANFT VOLKER, FRITSCHI, JOACHIM, LICHTENBERG, FLORIAN, RANFT, VOLKER
Applicants: FRITSCHI JOACHIM, LICHTENBERG FLORIAN, LONZA AG, RANFT VOLKER, FRITSCHI, JOACHIM, LICHTENBERG, FLORIAN, RANFT, VOLKER
Application year: 1997
Main classification: B27K3
IPC codes: A01N33, B27K3, C07C211