Catalyst for purifying exhaust gas from internal combustion engine and purifying method thereof

Abstract: A catalyst (20) being formed of a porous supporter supporting alkali metals, Ti and noble metal, or further supporting at least one of rare earth metal and magnesium, being disposed in a flow passage of the internal combustion engine (7), and being used to purify NO x contained in the exhaust gas. The above catalyst (20) has excellent NO x resistance not only to the exhaust gas burnt with the stoichiometric air-to-fuel ratio or rich condition, but to the exhaust gas burnt with the lean condition, and furthermore has a high resistivity to poisoning of SO x slightly contained in the fuel.

Description: BACKGROUND OF THE INVENTION The present invention relates to a catalyst for purifying exhaust gas from an internal combustion engine such as a vehicle engine and to a method for purifying said exhaust gas using said catalyst. A catalyst in accordance with the present invention has a high performance of removing nitrogen oxide from an exhaust gas containing oxygen burned under an air excessive condition (lean condition) as well as an exhaust gas burned under condition of stoichiomtric air-to-fuel ratio (A/F=about 14.7) wherein the air to fuel ratio is obtained as a ratio of air weight to fuel weight, and also has heat resistance and SO x poison resistance, and is suitable for a catalyst for cleaning an exhaust gas exhausted from a lean-burn engine for vehicle. In the recent trend of natural resource saving and environmental protection, there is social need to operate a gasoline engine for vehicle under lean-burn condition. In connection to this trend, there is social need to operate a gasoline engine for vehicle under lean-burn condition. In connection to this trend, there has been progressed to develop a catalyst (lean NO x catalyst) which can effectively remove nitrogen oxide (NO x ) in an exhaust gas containing oxygen exhausted from a lean-burn engine. In regard to exhaust gas cleaning catalysts for lean-burn engine, there is reported a catalyst supporting an alkali metal oxide and platinum on a porous supporter, for example, such catalyst is shown in the JP-A-6-31139. Furthermore in the JP-A-8-24643, a catalyst supporting at least one kind of palladium, rhodium and platinum, and at least one of alkali metal, alkali earth metal and rare earth metal, on the porous supporter. Here, as an embodiment of the catalyst material, one catalyst containing at least one kind of palladium, rhodium and platinum, and cerium and barium, and other catalyst containing them and further supporting La, Zr, Li, K, Mg, etc. thereon. The EP 0 707 882 A1 discloses a catalyst including an alumina support with a Ti-Zr composite oxide loaded thereon. This Ti-Zr composite oxide which may also contain yttrium increases the acidity of the support and, therefore, SO x is adsorbed less on the support. The EP 0 718 028 A1 describes a catalyst support including an amorphous composite oxide which is used as the NO x storage component. The amorphous composite oxide is a binary or ternary oxide, the preferable components of which are alumina together with barium oxide, cesium oxide or lanthanum oxide. SUMMARY OF THE INVENTION As environmental restriction to vehicles is growing severer, a lean NO x catalyst is required to have a higher NO x cleaning performance, and at the same time required to endure temperature change of burned exhaust gas accompanied by various change of vehicle speed and small amount of catalyst poisoning components (SO x , P, Pb ect.) contained in the burned exhaust gas for a long time. An object of the present invention is to provide a catalyst having a high purification performance of exhaust gas also being burnt in a fuel-lean atmosphere which exhibits an excellent heat and poison resistance to the catalyst poisoning components in the exhaust gas and to provide a method for cleaning the exhaust gas by using the catalyst. The object is solved according to the features of the independent claims. The dependent claims show advantageous embodiments of the invention. A catalyst applied in the present invention supports alkali metals, titanium and noble metals on the surface of a porous supporter composed of inorganic oxide. As the noble metal, it is preferable to contain at least one of rhodium (Rh), platinum (Pt,) palladium (Pd), and titanium (Ti). As alkali metal, it is preferable to be selected at least one among sodium, lithium, potassium and rubidium. The catalyst in the present invention is capable to contain one or both of earth metal and magnesium other than alkali metal, titanium and noble metal. The rare earth metal is preferable to be selected at least one among lanthanum and cerium. Support amounts of alkali metal, titanium, noble metal, and rare earth metal are preferable to be following weight % of metallic element to porous supporter of 100 weight %. That is, alkali metal is 2.5 to 27 weight %, titanium is 1 to 8 weight %, rhodium in noble metal is 0,05 to 0.3 weight %, platinum is 0.5 to 3 weight %, palladium is 0.5 to 15 weight %, and rare earth metal is 5 to 30 weight %. Moreover, the support amount of magnesium is preferable to be 1 to 40 % as a weight ratio of the magnesium support amount to support amounts of alkali metal and magnesium. As the supporter, alumina, titania, silica, magnesia, mixture of silica and aluminum, and various kinds of multiple oxides may be used. Especially, alumina or a complex oxide of lanthanum and aluminum are desirable to be used. It is preferable for the complex oxide of lanthanum and aluminum to consist of lanthanum 1 to 20 mole % in mole ratio and aluminum as a remainder. It is desirable for the porous supporter to be used by being coated on a honeycomb substrate. In the catalyst of the present invention, porous supporter is supported with Ce at first, with Mg, Na and Ti in the next, and further with Pt and Rh, and finally with Mg again, thereby an especial high NO x purification rate is obtained. The catalyst in the present invention is arranged in an exhaust gas passage of the internal combustion engine, and N0x which is contained in the burnt exhaust gas when the air-fuel ratio is a lean condition, is reduced so as to be removed by reacting with the carbon monoxide or hydrocarbon. The reason of the catalyst in the present invention having a high purification capacity for N0x contained in the exhaust gas being burnt in the lean condition, is estimated as that a high affinity for NO x is created by Ti coexisting with alkali metal, NO x is adsorbed on a surface thereof, and furthermore the adsorbed NO x is reduced by coexisting with noble metal. N0x purification performance for the lean exhaust gas deteriorates progressively while the catalyst is continuously used for a long time and is exposed in the lean exhaust gas. This is because oxygen is included in the lean exhaust gas and the carbon monoxide or hydrocarbon as a reducer for N0x is oxidized. Accordingly in the case that the purification ability for the lean N0x deteriorates, it is preferable to be changed into the stoichometric air-fuel ratio or in the fuel excess condition ( rich condition ), to let it burn with the condition for several seconds to several minutes, and to return to the lean condition again. With this purpose, nitrogen oxide purification rate of the catalyst for the lean exhaust gas is measured and if the measured value is lower than a set point, it is preferable to change the air-fuel ratio of internal combustion engine into the theoretical air-fuel ratio (stoichiometric ) or in fuel excess ( rich condition ) temporarily, and to return to the lean condition again. Moreover, it is preferable to measure the N0x concentration in the exhaust gas purified by the catalyst in the present invention, and to drive it in a fixed time by changing the burning condition of the engine into the theoretical air-fuel ratio or the rich condition if the measured value is lower than the set point. Methods of preparing the catalyst applicable are physical preparation methods such as an impregnation method, a kneading method, a coprecipitation method, a sol-gel method, an ion-exchange method, a vapor-deposition method and so on and chemical preparation methods utilizing chemical reaction. Starting raw materials for the catalyst preparation usable are various chemical compounds such as nitrides, acetates, chlorides, sulfates, carbonates, organic compounds of alkali metals, Mg, earth metals, noble metals; sol of metal oxides deflocculated by an acid or a base; metals and metal oxides; and so on. In the same way, relating to the starting raw materials for the Ti, the various chemical compounds and sol may be used. As sol of metal oxide, acid titanina such as sol of titanium nitride and sol of basic titanina may be used. In a case of using a mixed sol of an acid titanina and an acid alkali metal solution, the starting raw materials are preferable because particles of titania having poison resistance to sulfur oxides (SO x ) attached with particles of alkali metal oxide on the surface are supported by a porous supporter. The catalyst in accordance with the present invention has a high cleaning capability not only for NO x but for hydrocarbons. However, in order to attain a higher cleaning capability for hydrocarbons, it is effective to dispose a hydrocarbon burning catalyst with the catalyst of the present invention in a flow passage of the exhaust gas. In regard to combining methods, it is preferable to place the hydrocarbon burning catalyst in the rear stage of the exhaust gas cleaning catalyst in accordance with the present invention in an exhaust gas passage. As the hydrocarbon burning catalysts, a three way catalyst or a catalyst containing Pd as the noble metal may be used. A small amount of sulfur oxides contained in a burned exhaust gas from an internal combustion engine for vehicle poisons catalyst active components, particularly, alkali metals. In the present invention, adsorbing sulfur oxides to alkali metal is suppressed by containing Ti having poison resistance to sulfur oxides. Further, it is also estimated that in a reductive environment reduction and detachment of the adsorbed sulfur oxides are occur through the noble metal adjacent to the alkali metal. Therefore, even if performance of the catalyst in accordance with the present invention is temporarily deteriorated by sulfur oxides, the sulfur oxides can be removed and the catalyst can be reactivated by heating the catalyst to 400 °C to 800 °C under the reductive environment, the is, using the burned exhaust gas below stoichiometric air-to-fuel ratio. When the catalytic activity is decreased, it is preferable to reactivate the catalyst by the reactivation. The catalyst in accordance with the present invention can show the effect in treatment of an exhaust gas exhausted from a diesel engine of a diesel vehicle. The diesel engine is operated under an oxygen rich condition of high air-to-fuel ratio. Since the catalyst in accordance with the present invention can show excellent activity even under a oxygen containing condition, the catalyst can be clean the exhaust gas ejected from the diesel engine by effectively removing nitrogen oxides. The catalyst in accordance with the present invention has good activity within the temperature range above 200 °C and below 600 °C , and, particularly, has high activity within the temperature range of 250 °C to 500 °C. Therefore, it is preferable that the temperature under which the catalyst and the exhaust gas are brought in contact with each other, that is, the so-called reaction gas temperature is set to a temperature within the above-mentioned range. BRIEF DESCRIPTION OF THE DRAWINGS FIG. 1 is a conceptual view showing a gasoline engine for vehicle of a fuel injection type. FIG. 2 is a graph showing the relationship between support amount of Na and cleaning ratio for NO x . FIG. 3 is a graph showing the relationship between support amounts of Mg, Na and cleaning ratio for NO x . FIG. 4 is a graph showing the relationship between support amount of Ce and cleaning ratio for NO x . FIG. 5 is a graph showing the correlation between support amounts of Rh, Pt and cleaning ratio for NO x . FIG. 6 is a graph showing the correlation between support amounts of Pd, Pt and cleaning ratio for NO x . FIG. 7 is a graph showing the relationship between support amount of Ti and cleaning ratio for NO x . DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS FIG. 1 is a conceptual view showing a gasoline engine for vehicle of a fuel injection type. Air mixed with gasoline in an intake pipe 8 is burned in a cylinder by electrical ignition. Exhaust gas generated by combustion is ejected out of the system through an exhaust pipe 19 and an exhaust gas cleaning catalyst 20 applied the present invention. By controlling a fuel injection valve 13 and an ignition unit by a control unit 15, the combustion condition in the cylinder is controlled to any one of desired conditions of a stoichiometric air-to-fuel ratio (stoichiometric), a fuel excessive condition (rich) and an air excessive condition (lean). Therein, since the exhaust gas exhausted from the engine 7 contains harmful components such as HC, CO, NO x and the like, the exhaust gas must be ejected out of the system after the harmful components are detoxified. Therefore, the exhaust gas cleaning catalyst 20 for cleaning the exhaust gas using catalytic function is provided in the exhaust pipe 19. Since the catalyst in accordance with the present invention can clean a lean exhaust gas in addition to conventional cleaning of burned exhaust gas in stoichiometric and rich conditions, and consequently the combustion condition of the combustion system in FIG. 1 can be arbitrarily set. Further, by improving the heat resistance and the SOx poison resistance, the combustion system of FIG. 1 can be stably operated. As for the reference characters in FIG. 1, 1 is an air cleaner, 2 is an intake port, 5 is a throttle valve, 9 is a fuel tank, 10 is a fuel pump, 11 is a fuel damper, 12 is a fuel filter, 16 is a distributor and 18 is throttle sensor. Embodiment of the present invention will be described below. However, the present invention is not limited by these embodiments. [Embodiment 1] An alumina coated honeycomb having alumina coating of nearly 160 g per apparent volume of honeycomb of 1 liter was obtained by coating a slurry, which was formed of alumina powder, aluminum nitrate and aluminum hydroxide, and prepared in nitric acidity, to a honeycomb (400 cells/inc 2 ) made of cordierite, and then by drying and baking the alumina coated honeycomb. The alumina coated honeycomb was impregnated with Ce nitrate solution, and then dried at 200 °C and baked at 700 °C for 1 hour. Then, the alumina coated honeycomb was impregnated with a mixed solution of Na nitrate and Mg nitrate and nitric acid titania sol, and dried and baked in the same condition as above. Further, the alumina coated honeycomb was impregnated with a mixed solution of dinitro-diamin Pt nitrate solution and Rh nitrate solution, and then dried at 200 °C and baked at 450 °C for 1 hour. Finally, the alumina coated honeycomb was impregnated with Mg nitrate solution, and dried at 200 °C and baked at 450 °C for 1 hour, and then baked at 700 °C for 5 hours. Through the methods described above obtained was a catalyst of Embodiment 1 which supported with Ce of 18 weight % at first, supported with Na of 12 weight %, Mg of 1.2 weight % and Ti of 2.5 weight % in the next, and then supported with Pt of 1.6 weight % and Rh of 0.15 weight %, and finally supported with Mg of 1.5 weight % to alumina 100 weight %. Through the same method conditiond above, embodiments 2 to 6 are obtained. Furthermore, catalyst 1 which does not contain Ti was obtained by the same catalyst preparation method as that of the catalyst of Embodiment 1. Compositions of the prepared catalysts are shown in Table 1. The item "Order of supporting" active components in each of the catalysts in Table 1 indicates that the "first component" is supported, and next the "second component" is supported, and then the "third component is supported, and follows successively. Support amount is indicated before kind of supported metal. The word "wt." in the table means weight %. Order of Supporting 1 st Component 2 nd Component 3 rd Component 4 th Component Catalyst Embodiment 1 18 wt. Ce 12wt% Na 0.15wt% Rh 1.5wt% Mg 1.2wt% Mg 1.6wt% Pt 2.5wt% Ti Catalyst Embodiment 2 18 wt. La 12wt% Na 0.15wt% Rh 1.2wt% Mg 1.6wt% Pt 2.5wt% Ti Catalyst Embodiment 3 18 wt. Ce 12wt% K 0.15wt% Rh 1.2wt% Mg 1.6wt% Pt 2.5wt% Ti Catalyst Embodiment 4 18 wt. Ce 12wt% Li 0.15wt% Rh 1.2wt% Mg 1.6wt% Pt 2.5wt% Ti Catalyst Embodiment 5 18 wt. Ce 12wt% Na 0.15wt% Rh None 1.2wt% Mg 1.6wt% Pt 2.5wt% Ti 1.6wt% Pd Catalyst Embodiment 6 12wt% Na 1.6wt% Rh None 2.5wt% Ti 1.6wt% Pt Catalyst Comparison 1 18wt% Ce 7wt% Na 0.15wt% Rh 1.6wt% Pt (Test Example 1) Cleaning performances for nitrogen oxides of the catalysts Embodiments 1 to 6 and the catalyst Comparison 1 were evaluated by the following test method. Test method: (1) A honeycomb-shaped catalyst (17 mm square X 21 mm length) is filled into a pyrex reaction tube. (2) The reaction tube is put into a ring-shaped electric furnace to heat up to 300 °C or 400°C. Gas temperature at an inlet of the honeycomb is measured. When the temperature reaches 300 °C or 400°C and is stabilized, a stoichiometric burned model exhaust gas (hereinafter referred to as " stoichiometric exhaust model gas"), to be described later, is started to flow. Three minutes after starting to flow, the stoichiometric model exhaust gas is stopped to flow, and a lean-burn model exhaust gas (herein after referred to as "lean model exhaust gas"), to be described later, is started to flow. NO x in the gas ejected out of the reaction tube is measured by chemical luminescence method. The NO x cleaning performance at that time is defined as an initial performance. The stoichiometric model exhaust gas used was a gas which was composed of NO of 0.1 vol.% (volume %), C 3 H 6 of 0.06 vol., CO of 0.6 vol., O 2 of 0.6 vol., H 2 of 0.3 vol., water vapor of 10 vol., and nitrogen of the remainder. The lean model exhaust gas used was a gas which was composed of NO of 0.06 vol., C 3 H 6 of 0.05 vol., CO of 0.1 vol., CO 2 of 10 vol., O 2 of 5 vol., water vapor of 10 vol., and nitrogen of the remainder. Further, a poisoning gas used was a gas which was composed of NO of 0.1 vol., C 3 H 6 of 0.05 vol., CO of 0.6 vol., O 2 of 0.6 vol., SO2 of 0.005 vol., water vapor of 10 vol., and nitrogen of the remainder. Space speed of each of the above-mentioned gases was set to 30,000/h on a dry gas base (not include water vapor). (3) The reaction tube filled with the honeycomb used in the above item (2) is put into the ring-shaped electric furnace to be heated up to 300 °C. Gas temperature at an inlet of the honeycomb is measured. When the temperature reaches 300 °C and is stabilized, the stoichiometric model exhaust gas containing SO 2 (hereinafter referred to as " poisoning gas") is started to flow. SO 2 poisoning is completed by flowing the poisoning gas for 5 hours. Using the honeycomb-shaped catalyst after SO 2 poisoning, an NO x cleaning performance after SO 2 poisoning is obtained through the same test as in the above item (2). (4) The honeycomb used in the above item (2) is put into a baking furnace to be heated up to 800 °C for 5 hours under air environment. After cooling, an NO x cleaning performance is measured through the same manner as in the above item (2). Table 2 shows NO x cleaning ratio for initial performance and NO x cleaning ratio of honeycomb-shaped catalyst after SO 2 poisoning at a time one minute after switching from stoichiometric model exhaust gas to lean model exhaust gas. The NO x cleaning ratio is calculated according to the following equation. (NO x cleaning ratio)=[{(NO x concentration in inlet gas) - (NO x concentration in outlet gas)}÷(NO x concentration in inlet gas)] × 100 The catalysts of Embodiments 1 to 5 had higher initial performances compared to the catalyst of Comparison, and had heat resistance and SO 2 resistance. Initial NO x cleaning ratio [%] NO x cleaning ratio after SO 2 poisoning [%] NO x cleaning ratio after 800°C baking [%] 300 °C 400 °C 300 °C 400 °C 300 °C 400 °C Catalyst Embodiment 1 95 97 86 89 68 65 Catalyst Embodiment 2 92 90 90 87 65 60 Catalyst Embodiment 3 90 92 80 84 62 60 Catalyst Embodiment 4 80 82 72 70 58 50 Catalyst Embodiment 5 95 92 82 83 62 60 Catalyst Embodiment 6 90 92 75 70 55 50 Catalyst Comparison 1 90 75 40 30 30 15 [Embodiment 2] A catalyst of Embodiment 6 was obtained from a complex oxide of La and Al (La-β-Al 2 O 3 ) by changing composition ratio of La and Al in the supporter of the catalyst of Embodiment 1 to La of 5 mol% and Al of 95 mol% on a metallic element base. A method of preparing the catalyst was the same as that in the catalyst of Embodiment 1, and the test method was also the same as that of Test Example 1. Hereinafter, method of evaluating catalyst is the same as the method of Test Example 1 if not particularly described. The result of catalyst of Embodiment 6 is shown in Table 3 together with the result of catalyst of Embodiment 1 described previously. By employing heat resistant (La- β -Al 2 O 3 ) to the supporter, the heat resistance and SO x resistance are improved. Initial NO x cleaning ratio [%] NO x cleaning ratio after SO 2 poisoning [%] NO x cleaning ratio after 800°C baking [%] 300 °C 400 °C 300 °C 400 °C 300 °C 400 °C Catalyst Embodiment 1 95 97 86 89 68 65 Catalyst Embodiment 6 94 97 95 96 72 70 [Embodiment 3] An initial performance of NO x cleaning ratio at 400 °C was measured for catalysts in which a support amount of Na of the second component was changed in the catalyst of Embodiment 1. The result is shown in FIG. 2. A high NO x cleaning ratio can be attained by setting the supporting amount of Na to 2.5 to 27 weight % on a base of supporter of 100 weight %. [Embodiment 4] An initial performance of NO x cleaning ratio at 400 °C is measured for catalysts in which the weight % between a support amount of Mg of the second component and a support amount of Na is changed in the catalyst of Embodiment 1. The result is shown in FIG. 3. In order to attain a high NO x cleaning ratio, it is preferable that the weight ratio of (supporting amount of Mg)/{(supporting amount of Na)+(supporting amount of Mg)} is set to 1 to 40 weight %. [Embodiment 5] An initial performance of NO x cleaning ratio at 400 °C was measured for catalysts in which a support amount of Ce of the first component was changed in the catalyst of Embodiment 1. The result is shown in FIG. 4. A high NO x cleaning ratio can be attained by setting the supporting amount of Ce to 1 to 40 weight %. [Embodiment 6] An initial performance of NO x cleaning ratio at 400 °C was measured for catalysts in which support amounts of Pt and Rh were changed in the catalyst of Embodiment 1. The result is shown in FIG. 5. A high NO x cleaning ratio can be attained by setting the supporting amount of Pt to 0.5 to 3 weight % and the supporting amount of Rh to 0.05 to 0.3 weight %. [Embodiment 7] An initial performance of NO x cleaning ratio at 400 °C was measured for catalysts in which support amounts of Pt and Pd were changed in the catalyst of Embodiment 1. The result is shown in FIG. 5. A high NO x cleaning ratio can be attained by setting the supporting amount of Pt to 0.5 to 3 weight % and the supporting amount of Pd to 0.5 to 15 weight %. [Embodiment 8] An initial performance of NO x cleaning ratio and a performance of NO x cleaning ratio after being poisoned by SO x were measured at 400 °C for catalysts in which a support amount of Ti of the second component was changed on a base of supporter of 100 weight % in the catalyst of Embodiment 2. The result is shown in FIG. 7. A high NO x cleaning ratio and high SO x resistance can be attained by setting the supporting amount of Ti to 1 to 8 weight %. [Embodiment 9] The catalyst of Embodiment 1 was performed with SO 2 treatment through the same method as that in Test Example 1 (3). Next, a performance of NO x cleaning ratio one minute after starting flowing of the lean model exhaust gas. Then, the catalyst of Embodiment 1 was performed with stoichiometric treatment by flowing the stoichiometric model exhaust gas at 400 °C for 15 minutes described in Test Example 1. After decreasing the temperature to 300 °C the lean model exhaust gas described in Test Example 1 was allowed to flow, and then after one minute an NO x cleaning ratio was measured. The result is shown in Table 4. The catalyst performance was recovered by the stoichiometric treatment. Initial 3 hours after SO 2 treatment After stoichiometric treatment Catalyst of Embodiment 1 97% 89% 97% [Embodiment 10] A performance of NO x cleaning ratio one minute after switching of flow to the stoichiometric exhaust gas was measured for the catalyst of Embodiment 1 by the method of Test Example 1. The result is shown in Table 5. Initial NO x cleaning ratio [%] NO x cleaning ratio after SO 2 poisoning [%] NO x cleaning ratio after 800°C baking [%] 300 °C 400 °C 300 °C 400 °C 300 °C 400 °C Catalyst Embodiment 1 94 99 95 99 90 98 [Embodiment 11] (Test Example 2) Using the catalyst of Embodiment 1, HC in a gas ejected out of the reaction tube was measured by FID method though the test method was the same as the method in Test Example 1 from (1) to (3). Both of stoichiometric model exhaust gas and lean model exhaust gas were used in the same way as those in Test Example 1. Table 6 shows HC cleaning ratio in one minute after switching from the stoichiometric model exhaust gas to the lean model exhaust gas. The HC cleaning ratio is calculated according to the following equation. (HC cleaning ratio)=[{(HC concentration in inlet gas) - (HC concentration in outlet gas)}÷(HC concentration in inlet gas)] × 100 The catalyst in accordance with the present invention is effective for HC cleaning as well as cleaning of NO x in an exhaust gas ejected from an engine. Initial HC cleaning ratio [%] 300°C 400°C Catalyst of Embodiment 1 97 93 [Embodiment 12] A honeycomb-shaped catalyst 4cc (17mm square X 14mm length) of the catalyst of Embodiment 1 and a honeycomb-shaped three way catalyst 2cc (17mm square X 7mm length), which was formed by subtracting the second component and the third component from the catalyst of Embodiment1, were arranged in the reaction tube, and HC cleaning ratio one minutes after switching to lean model exhaust gas was measured by the method of Test Example 2. The HC cleaning ratios at both 300 °C and 400 °C were 100 %. According to the present invention, the catalyst can efficiently clean an exhaust gas containing oxygen by removing nitrogen oxide, and the catalyst has heat resistance and resistance to catalyst poisoning substances contained in a small amount in the exhaust gas.

Claims: Catalyst for purifying exhaust gas from an internal combustion engine comprising at least one alkali metal from the group sodium, lithium, potassium and rubidium, at least one noble metal from the group rhodium, platinum and palladium, and titanium which are supported on the surface of a porous supporter formed of inorganic oxide, characterized in that said titanium is supported together with said alkali metal(s) by depositing a material containing exclusively titanium and alkali metal(s) as metal components, at least one rare earth element is supported on said supporter of inorganic oxide, and the content of said supported metals, on a basis of metallic element to porous supporter of 100 wt.%, are 2.5 to 27 wt.% of said alkali metal, 1 to 8 wt.% of said titanium, 0.05 to 0.3 wt.% of said rhodium, 0.5 to 3 wt.% of said platinum, 0.5 to 15 wt.% of said palladium, and 5 to 30 wt.% of said rare earth metal. Catalyst according to claim 1, characterized in that magnesium is supported furthermore and is contained with a ratio of 1 to 40 of supported magnesium in wt.% to the sum of supported alkali metal and magnesium in wt.%. Catalyst according to claim 1, characterized in that said supporter is formed of a complex oxide of aluminum and lanthanum, with an amount of lanthanum in said complex oxide of 1 to 20 mole-% and the remainder is aluminum. Method for purifying exhaust gas from an internal combustion engine by removing nitrogen oxide using a catalyst according to at least one of claims 1 to 3.

Inventors: AZUHATA SHIGERU, DOI RYOUTA, HANAOKA HIROSHI, IIZUKA HIDEHIRO, KITAHARA YUICHI, KURODA OSAMU, OGAWA TOSHIO, SHINOTSUKA NORIHIRO, YAMASHITA HISAO, AZUHATA, SHIGERU, DOI, RYOUTA, HANAOKA, HIROSHI, IIZUKA, HIDEHIRO, KITAHARA, YUICHI, KURODA, OSAMU, OGAWA, TOSHIO, SHINOTSUKA, NORIHIRO, YAMASHITA, HISAO
Applicants: HITACHI LTD, HITACHI, LTD.
Application year: 1997
Main classification: B01D53
IPC codes: B01D53, B01J23