Purging agent and purging method

Abstract: A purging agent which contains an ethylene-vinyl alcohol copolymer and satisfies the conditions specified by the equations (1) and (2) below. 20 ≥ BT (120) ≥ 0.1 500 ≥ BT (250) / BT (120) ≥ 1.5 (where BT (120) is weight loss (%) on heating in nitrogen at 120°C for 24 hours, and BT (250) is weight loss (%) on heating in nitrogen at 250°C for 6 hours.) The purging agent rapidly discharges residual thermoplastic resin from the molding equipment for a thermoplastic resin containing EVOH and also rapidly discharges itself when a fresh resin is fed again to the equipment. This leads to a remarkable reduction in loss due to residual purging agent. In addition, the purging agent causes only a small amount of resin to stick to the equipment even alter repeated purging. After purging, it is possible to restore normal operation within a short time.

Description: The present invention relates to a purging agent to rapidly purge thermoplastic resins, especially those which contain ethylene-vinyl alcohol copolymer (EVOH for short hereinafter), from the melt passage after molding operation. This purging agent remains only a little after use and hence causes virtually no defectives after the reintroduction of a fresh thermoplastic resin into the passage. EVOH has gained a wide acceptance in the area of packaging film and container because of its good oxygen and flavor barrier properties required of some kinds of food and article. Unfortunately, EVOH is subject to the gelation and decomposition which occur in the pocket of the passage after extrusion operation for a long time and give rise to an undesirable matter which manifests itself as stones and streaks or as irregular thickness in the product. They make the product look poor. Moreover, EVOH gels and decomposes, foaming in the passage when operation is resumed, with the result that yellowed EVOH or gelled EVOH emerges continuously for a long time until acceptable products are obtained. In the worst case, it is necessary to disassemble the equipment for cleaning. The same problem as above also arises in molding operation after switching from EVOH to another resin (such as polyolefin, polyamide, polyester, and polycarbonate) or another grade of EVOH (differing in ethylene content). The problem is serious particularly in the case of switching to polyamide, polyester, and polycarbonate which are readily reactive with EVOH. One way to address this problem is by purging the passage of EVOH with high-density polyethylene (HDPE), linear low-density polyethylene (LLDPE) , polystyrene (PS), or polypropylene (PP). Purging is carried out whenever any anomaly (stones and streaks) occurs during operation or when operation is suspended. For effective purging, it is common practice to use a resin (as the purging agent) having a low melt flow rate of about 0.05-10 g/10 min (at 190°C under a load of 2160 g). Another way is by staged switching to grades having a lower melt flow rate, by reduction of the extrusion temperature, or increase of the output. The purging method mentioned above needs a complex procedure, takes a long time, or requires a large amount of purging agent. In addition, when EVOH molding is resumed after purging, the purging agent continues to enter the product for a long time until acceptable products are obtained. Such residual purging agent manifests itself as stones and streaks which are a great hindrance to transparent multilayered objects produced from EVOH by coextrusion or coinjection molding with PS, polyethylene terephthalate (PET), polycarbonate (PC), or the like. If multilayered objects are drawn, such stones and streaks break the EVOH layer, resulting in pinholes. Removal of gels staying in the passage of EVOH is most effectively achieved by using a purging agent having a low melt flow rate. However, such a purging agent is difficult to discharge when EVOH molding is resumed; it remains in the passage and continues to enter the products for a long time. A measure to cope with this situation is to repeat switching from one purging agent to another having a higher melt flow rate. This is not desirable, however, because it needs a complex procedure, takes a long time, and requires a large amount of purging agent. Using a blend of polyamide and polyether elastomer as a purging agent is disclosed in Japanese Patent Laid-open No. 178545/1989. It offers the advantage that time required for acceptable products to be obtained is short after resumption of EVOH molding. This purging method is not satisfactory, however. Japanese Patent Laid-open No. 269754/1993 discloses the use of an EVOH-based purging agent incorporated with an acid substance and a metal salt in a specific ratio. This purging agent permits acceptable products to be obtained in a short time after resumption of EVOH molding. However, it does not efficiently remove resin staying in the pocket of the resin passage. Likewise, Japanese Patent Laid-open No. 279518/1993 discloses the use of a polyolefin-based purging agent incorporated with a metal salt. Its effectiveness is offset by the fact that the repeated molding and purging for a long time end up with an accumulation of gelled resin in the pocket of the resin passage and a prolonged time before satisfactory production. (This will be demonstrated by Comparative Example given later.) Japanese Patent Laid-open No. 308899/1990 discloses a detergent for molding machines which is composed of a thermoplastic resin having a specific melt flow rate and a prescribed amount of water. However, it describes neither EVOH nor problems with melt stability characteristic of EVOH. JP-A-5279518 relates to a purging agent composition comprising polyolefin type polymers containing 0.05 to 1 wt.-% (in conversion to metal) of e.g. metal salt, satisfying the equation MI = 0.1 to 20, wherein Ml is the melt index (at 190 °C under a load of 2160 g, g/10 min) of the composition. EP-A-0 800 910 relates to a purging agent comprising (A) a hydrophobic thermoplastic resin, (B) a hydrophilic thermoplastic resin and (C) a purging auxiliary selected from the group consisting of (C1) a plasticizer, for the resin to be purged, (C2) water and (C3) a crystal water-containing compound, the proportions of the hydrophobic resin (B) being 100/0 to 30/70 by weight and the proportion of the purging auxiliary (C) relative to 100 weight parts of the sum total of the hydrophilic thermoplastic resin (A) plus hydrophilic thermoplastic resin (B) being 0.01 to 40 weight parts. In view of the foregoing, it is important to develop a new purging material capable of easily discharging residual gels from the passage during melt molding of a thermoplastic resin containing EVOH and being easily discharged by a fresh thermoplastic resin after resumption of molding operation, with a minimum of gel formed during operation for a long period of time. It is an object of the present invention to provide a new purging agent which permits normal operation to be restored shortly after resumption, without forming much gel sticking to the passage of EVOH even after operation for a long period of time. This object is achieved by the purging agents in accordance with claim 1 for the contracting states BE and IT and claim 1 for the contracting states DE, FR and GB. The purging agent contains an ethylene-vinyl alcohol copolymer and satisfies the conditions specified by the equations (1) and (2) below. 20 ≥ BT (120) ≥ 0.1 500 ≥ BT (250) / BT (120) ≥ 1.5 (where BT (120) is weight loss (%) on heating in nitrogen at 120°C for 24 hours, and BT (250) is weight loss (%) on heating in nitrogen at 250°C for 6 hours.) According to a preferred embodiment of the present invention, the purging agent may contain water in an amount of 0.1-20 wt% . According to another embodiment, the purging agent may contain inorganic powder in an amount of 0.01-20 wt%. The purging agents of the present invention may be used to purge a thermoplastic resin containing ethylene-vinyl alcohol copolymer from the melt passage after extrusion molding. These purging methods are also within the scope of the present invention. The purging agents of the present invention offer the advantage of rapidly discharging residual EVOH-containing thermoplastic resin from the melt passage of molding equipment and of rapidly discharging itself after reintroduction of a fresh thermoplastic resin into molding equipment. The rapid discharging greatly reduces defectives due to residual purging agent. In addition, even when molding and purging are repeated one after the other, the purging agent remains only a little in molding equipment. This permits normal operation to be restored in a short time. The mechanism for the above-mentioned effect is not fully understood. It is assumed that the purging agent foams on heating in the extruder, causing an anomalous flow which effectively discharges residual EVOH and gelled resin formed by holding-up. The present invention produces its salient effect, as demonstrated in Examples that follow, owing to the purging effect which contains an ethylene-vinyl alcohol copolymer and satisfies the conditions specified by the equations (1) and (2) below. 20 ≥ BT (120) ≥ 0.1 500 ≥ BT (250) / BT (120) ≥ 1.5 (where BT (120) is weight loss (%) on heating in nitrogen at 120°C for 24 hours, and BT (250) is weight loss on heating in nitrogen at 250°C for 6 hours.) According to the present invention, the value of BT (120) should be higher than 0.1%, preferably higher than 0.2%, more preferably higher than 0.5%, and most preferably higher than 1.0%. With a value lower than 0.1%, the purging agent does not produce its effect satisfactorily. In addition, it should be lower than 20%, preferably lower than 10%, and more preferably lower than 5%. With a value higher than 20%, the purging agent foams excessively, causing a inhomogeneous resin flow, without producing its effect satisfactorily. According to the present invention, the value of BT (250) / BT (120) should be higher than 1.5, preferably higher than 2, and more preferably higher than 3. With a value lower than 1.5, the purging agent will take an unduly long time before normal operation is restored. In addition, it should be lower than 500, preferably lower than 400, and more preferably lower than 300. With a value higher than 500, the purging agent itself is too low in viscosity to purge itself and hence does not produce its purging effect satisfactorily. Weight loss on heating is calculated from the equation below. (1- a ) × 100(%) where, a is the weight of a resin sample (1 g) measured after heating in a nitrogen-filled 10-ml glass tube at a prescribed temperature for a prescribed period of time. The purging agents of the present invention are prepared from a thermoplastic resin as a base polymer. The base polymer may be a resin or resin compound containing EVOH. It may be neat EVOH or an EVOH compound incorporated with a resin such as polyolefin, polystyrene, polyamide, polyester, polyvinyl chloride, and polyvinylidene chloride. According to the present invention, the base polymer of the purging agent should preferably be composed of EVOH resin alone. The combined use of EVOH with any other thermoplastic resin is economically advantageous over the single use of EVOH; however, this advantage is offset by a decreased purging effect and a longer time required before the restoration of normal operation. The purging agent based on EVOH resin alone is desirable from the standpoint of economy and purging performance. EVOH as the base polymer of the purging agent of the present invention is a hydrolyzed ethylene-vinyl acetate copolymer, with an ethylene content being 15-70 mol%, preferably 20-65 mol%, and with a degree of hydrolysis of the vinyl acetate moiety being higher than 90%, preferably higher than 95%. It may contain a small amount of comonomer such as propylene, 1-butene, 1-hexene, 4-methyl-1-pentene, acrylic ester, methacrylic ester, maleic acid, phthalic acid, itaconic acid, alkylvinyl ester, N-vinylpyrrolidone, N-n-butoxymethylacrylamide, N-(2-dimethylaminoethyl)methacrylamide, quaternary products thereof, vinyltrimethoxysilane, vinyltriethoxysilane, vinylmethyldimethoxysilane, and vinyltriacetoxysilane. It may also contain a boron compound (such as boric acid, metal borate, borate ester, and boron complex) for adjustment of its melt viscosity. It may also contain an acid or metal salt mentioned above for thermal stability and oxidation resistance and for improvement in color. The base polymer in the form of resin composition should preferably be composed of EVOH and polyolefin. A preferred polyolefin is high-density polyethylene (HDPE) or polypropylene (PP) having a high melt flow rate (at 190°C under a load of 2160 g) which is 1-1/100, preferably 1/5-1/90, of that of EVOH. The blending ratio of EVOH/polyolefin should range from 1/99 to 99/1, preferably from 5/95 to 95/5, more preferably from 10/90 to 90/10, by weight. This base polymer (or resin composition) readily discharges gels as demonstrated in Example given later. The purging agent satisfies the conditions specified by the equations (1) and (2) mentioned above may be prepared typically by the following steps (a) and (c), or (b) and (c), in combination. Step (a): Incorporation of a thermoplastic resin with a low-boiling compound having a boiling point lower than 300°C, preferably lower than 280°C, and more preferably lower than 250°C in an amount of 0.1-20wt%. Examples of the low-boiling compound include water, alcohol (such as methyl alcohol, ethyl alcohol, propyl alcohol, and butyl alcohol), and polyhydric alcohol (such as ethylene glycol, propylene glycol, and glycerin). The amount of the low-boiling compound should be more than 0.1wt%, preferably more than 0.2wt%, more preferably more than 0.5wt% and most preferably more than 1.0wt%. An amount less than 0.1wt% is not enough for satisfactory purging performance. The upper limit is less than 20wt%, preferably less than 10wt%, and more preferably less than 5wt%. With an amount in excess of 20wt%, the resulting purging agent does not produce a satisfactory purging effect due to excessive foaming and inhomogeneous resin flow. Of the low-boiling compounds, water is desirable from the standpoint of safety and production cost. Incorporation of water may be accomplished by mixing a molten resin with water in a twin-screw extruder and pelletizing the extrudate at a low temperature, by extruding moistened EVOH through a twin-screw extruder and pelletizing the extrudate at a low temperature, by dipping pellets in water, by spraying pellets with water, or by allowing pellets to stand in a high-humidity atmosphere. Step (b): Incorporation of a thermoplastic resin with a carrier which has absorbed a large amount of low-boiling compound (such as water, alcohol, and polyhydric alcohol mentioned above). Examples of the carrier include water-absorbed gel, polyvinyl alcohol, polyacrylamide, polyethylene glycol, and polypropylene glycol. The amount of the carrier should be 1-40 wt% so that the low-boiling compound accounts for 0.1-20 wt% of the thermoplastic resin. Step (c): Incorporation of a metal salt in an amount of 0.0005-0.5 wt% (in terms of metal). Examples of the metal salt include carboxylates, phosphates, carbonates and chlorides. Alkaline metal salts and alkaline earth metal salts are preferable. Alkaline earth metal salts are more preferable. And alkaline earth metal carboxylates (such as calcium acetate, magnesium acetate, magnesium stearate, and calcium stearate) are most preferable. Alkaline earth metal salts are preferable. The amount of the metal salt should be 0.0005-0.5 wt%, preferably 0.001-0.5 wt%, and more preferably 0.01-0.5 wt%, in terms of metal. The metal salt may be used in combination with an acid (such as acetic acid, adipic acid and potassium dihydrogen phosphate) or an alkali (such as sodium hydroxide). The purging agents of the present invention will discharge residual gel from the passage more effectively if they are incorporated with inorganic fine powder in an amount of 0.01-20 wt%. Presumably this effect is due to the ability of inorganic fine powder to physically scrape off residual gel remaining in the passage. Examples of the inorganic fine powder include oxides, hydroxides, and chlorides of silicon, aluminum, iron, copper, cobalt, and manganese, and mixtures thereof. The inorganic fine powder is not specifically restricted in particle size. More than 80 wt% of the powder should be accounted for by particles smaller than 10 µm, preferably smaller than 6 µm, and more preferably smaller than 3 µm. The amount of the inorganic fine powder should be 0.01-20 wt%, preferably 0.02-10 wt%, of the amount of the thermoplastic resin as the base polymer of the purging agent. Preferred examples of the inorganic fine powder include silicon oxide, titanium oxide, montmorillonite, and hydrotalcite. The purging agents of the present invention may be used for any melt extrusion equipment, such as single-film extruder, single-film tubular film extruder, coextrusion sheet or film forming machine, coextrusion blow molding machine, and coinjection molding machine. The purging agent is used when the extruder hopper becomes empty after extrusion of a thermoplastic resin containing EVOH. The amount ofthe purging agent should be about 6 to 20 times the amount of the resin remaining in the extruder. Increasing the screw revolution is one way of enhancing the purging effect. After purging, extrusion for a fresh thermoplastic resin may be resumed by any of the following three methods. (a) Feed a fresh thermoplastic resin immediately after purging. (b) After purging, suspend the screw rotation, while keeping the extruder temperature as before, until the purging agent increases in melt flow rate, and then restart extrusion for a fresh thermoplastic resin. (c) After purging, suspend extrusion while lowering the temperature (during which the purging agent increases in melt flow rate), and then restart extrusion for a fresh thermoplastic resin. Incidentally, in the case of (a) above, it is desirable to slightly increase the extruder temperature so that the purging agent increases in melt flow rate rapidly and produces the purging effect more readily. The purging agents of the present invention may be applied to any resin compound containing EVOH. They produce their maximum effect when applied to neat EVOH. The EVOH to be purged may be the same one as used for the base polymer of the purging agent. It is desirable that the EVOH to be purged should not differ appreciably from the EVOH for the base polymer of the purging agent in ethylene content and degree of hydrolysis. The difference in ethylene content should be preferably less than 30 mol%, more preferably less than 25 mol%. The difference in degree of hydrolysis should be preferably lower than 20 %, more preferably lower than 15%. The small difference in ethylene content and degree of hydrolysis contributes to effective purging owing to their better affinity. The resin compound containing EVOH may be formed by blending with a polyolefin (such as polyethylene and polypropylene), polystyrene, polyamide, polyester, polyvinyl chloride, or polyvinylidene chloride. EXAMPLES To further illustrate the invention, and not by way of limitation, the following examples are given. The test methods used in the examples are explained first. • Measurements of BT (120) and BT (250) . An accurately weighed sample (about 3 g) is placed in a test tube (24 mm in outside diameter) lined with Teflon film to prevent the sample from sticking to the glass wall. This test tube is placed in an iron pipe (170 mm long and 30 mm in outside diameter). The atmosphere in the pipe is thoroughly replaced with nitrogen in a chamber and the pipe is tightly sealed with a screwed lid. The assembly is heated in a drier at a prescribed temperature for a prescribed period of time. The assembly is allowed to cool to room temperature and then opened. The sample is dried in a vacuum drier at 90°C for 16 hours and then allowed to cool in a desiccator. The heat-treated sample is weighed (in gram) and the weight loss on heating is calculated from the equation below. [{3 - (weight after heating)} ÷ 3] × 100 (%) • Measurements of water content: Measurements are carried out by using a Karl Fischer water content meter (Model VA-06 and CA-03, made by Mitsubishi Chemical Industries, Ltd.). A sample (1 g) is placed in the meter which has been dried at 200°C for 2 minutes. After heating at 200°C for 2 minutes, measurements are started, and the value at the end point is obtained as the water content. • Stones on the film surface: A film sample is taken one hour after the start of the fifth operation. The sample is visually inspected and the number of stones within an area (10 x 10 cm) is counted. • Streaks on the film surface: A film sample is taken one hour after the start of the fifth operation. The sample is visually inspected and the number of streaks within a width of 40 cm is counted. The results are rated as A to E according to the following criterion. A : 0-2 streaks/40 cm width B : 3-9 streaks/40 cm width C : 10-29 streaks/40 cm width D : 30-99 streaks/40 cm width E : more than 100 streaks/40 cm width Example 1 A resin compound was prepared from the following components by melt mixing at 180°C using a twin-screw extruder. EVOH powder with an ethylene content of 31 mol%, a degree of hydrolysis of 99.4%, and a melt flow rate of 1.3 g/10 min (at 190°C under a load of 2160 g), containing 0.02 wt% of acetic acid, 20 ppm of calcium salt (in terms of metal), and 10 ppm of magnesium salt (in terms of metal). magnesium stearate (MgSt) : 2 wt% (0.08 wt% in terms of metal) water : 1.4 wt% The extrudate was pelletized in water at 80°C, pressurized at 4 kg/cm 2 , by using an under-water cutter. The resulting pellets were centrifugally dehydrated and then dried at 80°C for 1 hour. Thus there was obtained a purging agent containing 1.3 wt% water, characterized by BT (120) = 1.3% and BT (250) = 35%. Extrusion was carried out to form a 50-µm thick EVOH single-layer tubular film from EVOH specified below by using a 40-mm single-screw extruder under the conditions specified below. EVOH with an ethylene content of 31 mol%, a degree of hydrolysis of 99.4%, and a melt flow rate of 1.3 g/10 min (at 190°C under a load of 2160 g) Extrusion from a circular die (150 mm in diameter), at 230°C and a throughput of 20 kg/hour. After continued operation for 105 hours, marked stones and streaks began to come out on the film surface. The purging agent prepared as mentioned above was fed to the extruder for about 30 minutes under the same operating conditions as mentioned above, with the throughput kept at 20 kg/hour. Operation was suspended. Incidentally, "marked stones or streaks" mean stones in excess of 300/100 cm 2 or streaks in excess of 100/40 cm width. On the following day, the equipment was heated and extrusion of EVOH was resumed. Sixty minutes after the first resumption, a satisfactory film (free from stones and streaks) came out. The film was regarded as satisfactory when it has less than 300 stones/100 cm 2 and satisfies the criterion D for streaks. Extrusion for film production was continued. After 100 hours, stones and streaks began to come out on the film surface. The purging agent was fed in the same manner as mentioned above, and operation was suspended. On the following day, the equipment was heated and extrusion of EVOH was resumed. Sixty-two minutes after the second resumption, a satisfactory film (free from stones and streaks) came out. The same procedure as above was repeated. After 98 hours, stones and streaks began to come out. Sixty-five minutes after the third resumption, a satisfactory film came out. The fourth and fifth suspension and resumption were repeated in the same manner as above. The results are shown in Table 2. After the completion of the fifth operation, LDPE was fed to the extruder and extrusion was carried out for 1 hour at a throughput of 20 kg/hour. The extruder was disassembled and cleaned. It was found that the amount of resin sticking to the screw and die was only 1.6 g and 2.5 g, respectively. Examples 2 to 8 and Comparative Examples 2 to 8 The same procedure as in Example 1 was repeated except that the kind of the purging agent was changed as shown in Table 1. The results are shown in Table 2. In the examples and comparative examples, the following base polymers and additives were used. EVOH-1 ethylene content: 31 mol% degree of hydrolysis: 99.4% melt flow rate: 1.3 g/10 min (at 190°C under a load of 2160 g) acetic acid: 0.02 wt% calcium salt: 20 ppm (in terms of metal) magnesium salt: 10 ppm (in terms of metal) EVOH-2 ethylene content: 31 mol% degree of hydrolysis: 99.4% melt flow rate: 1.3 g/10 min (at 190°C under a load of 2160 g) acetic acid: 0.1 wt% calcium salt: 80 ppm (in terms of metal) magnesium salt: 50 ppm (in terms of metal) potassium dihydrogenphosphate: 120 ppm LDPE "Mirason 102™" (low-density polyethylene from Mitsui Petrochemical Industries Ltd.) melt flow rate: 0.8 g/10 min (at 190°C under a load of 2160 g) PP "FH1015B" (polypropylene from Tonen Sekiyu Kagaku K.K.) melt flow rate: 0.6 g/10 min (at 190°C under a load of 2160 g) Colloidal silica "Silicia 430" (colloidal silica from Fuji Silicia Kagaku K.K.) average particle diameter: 2.5 µm (measure by a coal tar counter) Comparative Example 1 The suspension and resumption of operation were repeated in the same manner as in Example 1, except that the purging agent was not used. The results are shown in Table 2. Table 1 Table 2 Effect of the invention: The present invention provides a new purging agent which rapidly discharges residual thermoplastic resin from the molding equipment for a thermoplastic resin containing EVOH and also rapidly discharges itself when a fresh resin is fed again to the equipment. This leads to a remarkable reduction in loss due to residual purging agent. In addition, the purging agent causes only a small amount of resin to stick to the equipment even after repeated purging. After purging, it is possible to restore normal operation within a short time.

Claims: Claims for the following Contracting States : DE, FR, GB A purging agent containing an ethylene-vinyl alcohol copolymer and incorporating (a1) a low-boiling compound selected from water, alcohols and polyhydric alcohols in an amount of 0.1 to 20 wt. %, said compound having a boiling point lower than 300°C, or (a2) a carrier having absorbed said low-boiling compound in an amount such that the amount of low-boiling compound accounts for 0.1 to 20 wt.% and (b) a metal salt selected from the group of alkaline and alkaline earth metal carboxylates, phosphates, carbonates and chlorides in an amount of 0.0005-0.5 wt% in terms of metal, wherein the purging agent satisfies the conditions specified by the equations (1) and (2) 20 ≥ BT (120) ≥ 0.1 500 ≥ BT (250) / BT (120) ≥ 1.5 where BT (120) is weight loss (%) on heating in nitrogen at 120°C for 24 hours, and BT (250) is weight loss (%) on heating in nitrogen at 250°C for 6 hours. The purging agent as defined in Claim 1, wherein said compound is water. The purging agent as defined in Claim 1 or 2, further containing an inorganic powder in an amount of 0.01-20 wt%. A purging agent according to any of claims 1 to 3 wherein the EVOH is neat EVOH or an EVOH incorporated with a resin selected from polyolefin, polystyrene, polyamide, polyester, polyvinylchloride, and polyvinylidene chloride. A purging agent according to any of claims 1 to 4 wherein the ethylene-vinyl alcohol copolymer is a hydrolyzed ethylene-vinyl acetate copolymer having an ethylene content of 15 to 70 mol% and a degree of hydrolysis of the vinyl acetate moiety of more than 90%. A purging agent according to claim 5 wherein the ethylene-vinyl alcohol copolymer contains a co-monomer selected from the group of propylene, 1-butene, 1-hexene, 4-methyl-1-pentene, acrylic ester, methacrylic ester, maleic acid, phthalic acid, itaconic acid, alkylvinyl ester, N-vinylpyrrolidone, N-n-butoxymethylacrylamide, N-(2-dimethylaminoethyl)methacrylamide, quartemary products thereof, vinyltrimethoxysilane, vinyltriethoxysilane, vinylmethyldimethoxysilane, and vinyltriacetoxysilane. A method of purging a residual thermoplastic resin containing an ethylene-vinyl alcohol copolymer from the melt passage after the extrusion molding of a thermoplastic resin containing an ethylene-vinyl alcohol copolymer, said method comprising using a purging agent defined in any of Claims 1 to 6. Claims for the following Contracting States : BE, IT A purging agent which contains an ethylene-vinyl alcohol copolymer and charactrized in that said purging agent satisfies the conditions specified by the equations (1) and (2) 20 ≥ BT (120) ≥ 0.1 500 ≥ BT (250) / BT (120) ≥ 1.5 where BT (120) is weight loss (%) on heating in nitrogen at 120°C for 24 hours, and BT (250) is weight loss (%) on heating in nitrogen at 250°C for 6 hours. The purging agent as defined in Claim 1, which contains water in an amount of 0.1-20 wt%. The purging agent as defined in Claim 1 or 2, which contains an inorganic powder in an amount of 0.01-20 wt%. A purging agent according to any of claims 1 to 3 wherein the EVOH is neat EVOH or an EVOH incorporated with a resin selected from polyolefin, polystyrene, polyamide, polyester, polyvinylchloride, and polyvinylidene chloride. A purging agent according to any of claims 1 to 4 wherein the ethylene-vinyl alcohol copolymer is a hydrolyzed ethylene-vinyl acetate copolymer having an ethylene content of 15 to 70 mol% and a degree of hydrolysis of the vinyl acetate moiety of more than 90%. A purging agent according to claim 5 wherein the ethylene-vinyl alcohol copolymer contains a co-monomer selected from the group of propylene, 1-butene, 1-hexene, 4-methyl-1-pentene, acrylic ester, methacrylic ester, maleic acid, phthalic acid, itaconic acid, alkylvinyl ester, N-vinylpyrrolidone, N-n-butoxymethylacrylamide, N-(2-dimethylaminoethyl)methacrylamide, quarternary products thereof, vinyltrimethoxysilane, vinyltriethoxysilane, vinylmethyldimethoxysilane, and vinyltriacetoxysilane. A method of purging a residual thermoplastic resin containing an ethylene-vinyl alcohol copolymer from the melt passage after the extrusion molding of a thermoplastic resin containing an ethylene-vinyl alcohol copolymer, characterized by using a purging agent defined in any of Claims 1 to 6.

Inventors: HIROMICHI NAKANO, SATOSHI HIROFUJI, SYUKITI KAWAMURA, TAICHI NEGI, HIROMICHI, NAKANO, SATOSHI, HIROFUJI, SYUKITI, KAWAMURA, TAICHI, NEGI
Applicants: KURARAY CO, KURARAY CO., LTD.
Application year: 1997
Main classification: B29C47
IPC codes: B29C47