An optical recording medium with a metallic recording layer

Abstract: An optical recording medium is provided which includes a substrate (10) having pregrooves, and a metal recording layer (20), a buffering layer (30), a reflecting layer (40) and a protecting layer (50) which are sequentially stacked on the substrate. The angle () of the slant side of the pregroove is 30~90° and the buffering layer has 10~50,000Pa.S melt-viscosity at 140°C. The optical recording medium is therefore compatible with a CD and playable by a DVDP, can be manufactured at low cost without using a dye, and provides high reflectivity at longer wavelength than 600nm.

Description: The present invention relates to an optical recording medium, and more particularly, to an optical recording medium which is compatible with a compact disc (CD), has a high reflectivity at longer wavelength than 600nm, and in and from which information can be recorded and reproduced by a digital versatile disc player (DVDP) and a compact disc player (CDP), and can be produced at low cost. The recording area per recording unit of an optical recording medium is smaller than that of a conventional magnetic recording medium, so that the optical recording medium has been used as a high density recording medium. The optical recording medium is classified into read only memory (ROM) type which only reproduces already recorded information, write once read many (WORM) type which is recordable just once and readable many times, and rewritable type which is recordable, erasable and rewritable medium. The information recorded in the optical recording medium should be reproduced by a player for the ROM type medium. To this end, the optical recording medium must satisfy a conventional standardization rule (RED BOOK), so that reflectivity of 65% or more and carrier-to-noise ratio (CNR) of 47dB or more are required. In a recordable optical recording medium, the recorded information can be reproduced based on the change of the reflectivity which caused by a physical modification, phase change or change of a magnetic property in a recording layer before and after the recording. Also, for making the optical recording medium compatible with a CD, a long-term data storing property and a high recording density are required as well as the above high reflectivity and CNR characteristic. In order to improve the characteristic of the optical recording medium and make easy the manufacturing process, various optical recording media being formed of various materials have been suggested, and a part of them is being in practical use. As a conventional optical recording medium, Japanese Laid-open Patent Publication No. showha 63-268142 discloses a recording medium having a structure in which a sensitizing layer formed of gelatin, casein or polyvinyl alcohol (PVA), and a metal thin film as a recording layer formed of chromium (Cr), nickel (Ni) or gold (Au) are sequentially stacked on a substrate. According to the optical recording principle of the recording medium, the metal thin film absorbs heat of an irradiated laser beam, and thus the sensitizing layer and the metal thin film are deformed to form a recording pit. However, the recording pit of this recording medium is exposed so that it is difficult to store the recorded information for a long-term. U.S. Patent No. 4,973,520 discloses a recording medium having a structure in which three metal thin films are stacked on a substrate. The recording characteristic of the recording medium is good, however, the long-term storage of the recorded information cannot be achieved due to its exposed recording pit. In order to solve the above defect, U.S. Patent No. 4,983,440 discloses a recording medium having a structure in which two metal thin films as a recording layer, and a protecting layer for protecting the recording layer are sequentially stacked on a substrate. However, this recording medium has a very low reflectivity of about 20% and requires a high-power light source for the practical use. Also, the recording medium cannot be compatible with a conventional CD. According to U.S. Patent No. 5,328,813, a metal thin film as a recording layer is formed on a substrate, and a hard metal oxide layer is formed on the metal thin film to increase an information storing property and the reflectivity to 40∼69%. However, the CNR is still low. Also, U.S. Patent No. 5,155,723 discloses a recording medium having a structure in which an organic dye layer as a recording layer is stacked on a substrate, and a reflecting layer and a protecting layer are stacked on the recording layer. According to the recording medium, the dye layer absorbs a recording laser beam for a recording to emit heat. Also, the substrate is heated and deformed by the heating, so that a recorded signal can be reproduced based on the difference of the reflectivity according to the recording. Here, the reflectivity of the recording medium is 70% or more and the CNR after recording is 47dB or more to be compatible with the CD. However, the recording layer of the recording medium has low resistance against heat and light, and the manufacturing costs are high due to the expensive organic dye. Also, a spin coating is performed during the manufacturing process with an organic dye solution. However, the thickness of the coating layer must be accurately controlled with a deviation of ±3% or less during the manufacturing of an optical disc since the reflectivity is dependent on the thickness of the coating layer. Also, a costly equipment is required and the productivity is low. EP 0019329 discloses an optical recording medium comprising a substrate, a metal recording layer, a buffering layer and a reflecting layer which are sequentially stacked on the substrate. According to the invention, the substrate has pregrooves, and the angle () of the slant side of the pregroove is 30∼90° and the buffering layer has 10∼50,000Pa.S melt-viscosity at 140°C. Preferably, the width at the bottom of the pregroove is 10-450nm, the width at the uppermost of the pregroove is 400∼1,000nm, and the depth of the pregroove is 30∼450nm. Preferably, the buffering layer is formed of at least one resin having 70∼130°C glass transition temperature (Tg), selected from the group consisting of vinylalcohol resin, vinylacetate resin, acrylate resin, polyester resin, polyether resin, polystyrene resin, polyurethane resin, cellulose resin, fatty acid resin and copolymers thereof. Also, the buffering layer may include a dye having a high reflectivity at an available wavelength region for the optical recording medium. Here, the dye content is 30wt% or less based on the weight of the buffering layer. An example of the present invention will now be described in detail with reference to the accompanying drawings, in which: FIG. 1 is a sectional view showing the structure of an optical disc according to a preferred embodiment of the present invention; FIG. 2 is a sectional view showing a recorded portion and a non-recorded portion formed in the optical disc of FIG. 1; FIG. 3 is a graph showing the change of reflectivity according to the thickness of a buffering layer of the optical disc of FIG. 1; and FIG. 4 is a graph showing a relationship between CNR and recording power in the optical disc of FIG. 1. Referring to FIG. 1 showing the structure of an optical recording medium according to a preferred embodiment of the present invention, the optical recording medium includes a substrate 10, and a metal recording layer 20, a buffering layer 30, a reflecting layer 40-and a protecting layer 50 which are sequentially stacked on the substrate 10. In the optical recording medium having the above structure, the metal recording layer 20 is heated by a laser beam during an optical recording, and the heat is transferred to the substrate 10 and the buffering layer 30. A region of the substrate 10, adjacent to the heated region of the metal recording layer 20, is expanded and deformed, and the heated region of the metal recording layer 20 is swelled out toward the buffering layer 30 by the expanding force of the substrate. FIG. 2 is a sectional view showing a recorded portion and a non-recorded portion in detail, which are formed in the optical recording medium of the present invention. As shown in FIG. 2, in the recorded portion, the substrate is swelled up and the buffering layer is deformed by heat, so that the reflecting layer may be also deformed. Here, the degree of deformation is proportional to the heat generated from the metal recording layer and dependent on the materials and thickness of the metal recording layer and the buffering layer. In an optical recording medium of the present invention, the reflectivity of the recorded portion increases during recording compared with the non-recorded portion by the following principles. First, as shown in FIG. 2, the thickness of the buffering layer becomes thin from d 1 to d 2 by the expansion of the substrate during the recording. Here, the reflectivity is varied according to the thickness of the buffering layer as shown in FIG. 3, so that the reflectivity increases by the decrease of the thickness of the buffering layer. That is, the initial thickness d 1 of the buffering layer is decreased to d 2 by the recording, so that the reflectivity is increased after the recording. Here, the amount of increased reflectivity depends on the thickness of the metal layer. Second, the bottom of the pregrooves is expanded by the expansion of the substrate during the recording, so that the depth of the pregrooves is decreased, thereby reducing a reflective light Rw scattered from the sidewalls of the pregrooves. On the contrary, a reflective light Rr reflected from the bottom of the reflecting layer or a reflective light Rg reflected from the bottom of the pregrooves are increased. Accordingly, the reflectivity increases after the recording. Third, the degree of transmittance of the recorded portion of the metal recording layer increases. That is, the center of the recorded portion greatly expands, so that the thickness at the center of the metal recording layer may become thin or a hole may be formed therein, thereby increasing the reflectivity at the recorded portion. In an optical recording medium of the present invention, the size and shape of the pregrooves of the substrate and material of the buffering layer are combined in order to increase the recording characteristic such as CNR, cross-talk or jitter, based on the above-described principles for increasing the reflectivity at the recorded portion. That is, the material of the buffering layer is pushed toward a land by the expansion of the substrate, thereby changing the shape of the land. Here, the change in shape of the land acts as a noise of a recorded signal to increase the jitter. To prevent the jitter, the angle (, FIG. 2) of a slant side of the pregroove should be controlled to 30°∼90°, preferably, near 90°, and the bottom area of the pregroove should be increased. Also, appropriate viscosity should be provided to the buffering layer to prevent the buffering layer from being pushed out. Also, the metal recording layer 20 formed of a metal having a light absorption at the laser wavelength generates heat during the recording to heat the substrate and the buffering layer, thereby deforming the substrate and the buffering layer. On the other hand, the recorded information is reproduced by a reflective light Rg' being reflected from the metal recording layer. Thus, preferably, the metal recording layer is formed of a metal having a high reflectivity, a high absorption coefficient for sufficient emission and a low thermal conductivity. More preferably, a metal having a coefficient k of the imaginary part of a complex refractive index, which is greater than or equal to 0.01, is used. (Here, the refractive index means a complex refractive index expressed by " n - k i", wherein n is a coefficient of the real part and k is a coefficient of the imaginary part, and k =0 at a wavelength without absorption). Hereinafter, characteristics required for each constituent layer of an optical recording medium of the present invention will be described in detail. In one surface of the substrate 10 of an optical recording medium of the present invention, pregrooves for guiding light during the recording are formed, wherein the shape of the pregroove acts as a factor affecting the reflectivity and a tracking characteristic. Preferably, the depth of the pregroove is 30∼450nm. If the depth of the pregroove is 30nm or less, the depth of the pregroove reflected in the buffering layer (groove image) is small, so that the difference of the reflectivity between the land side and the pregroove side is decreased, thereby making unstable tracking. On the contrary, if the depth of the pregroove is 450nm or higher, a boundary between the buffering layer and the reflecting layer is largely dented at the pregroove side (deep groove image), causing the scattering of the light. Accordingly, the reflectivity before the recording is very low, so that the recording itself is impossible. Also, preferably, the width of the bottom of the pregroove is 100∼450nm and that of the uppermost of the pregroove is 400∼1,000nm. Also, the angle () of the slant side of the pregroove is preferably 30°∼90°, more preferably, near 90°. In order to prevent the easy deformation of the pregrooves by the expansion of the substrate and reduce noise of a recorded signal, the sides of the pregrooves should be nearly orthogonal with respect to the bottom and the bottom area of the pregroove should be wide. Preferably, as a material for the substrate, polycarbonate, polymethylmethacrylate (PMMA), epoxy resin, polyester or amorphous polyolefin is used, which is transparent with respect to a laser beam and capable of being expanded and deformed by heat, and has excellent impact intensity and glass transition temperature (Tg) of 80∼120°C, more preferably, 100∼200°C. The metal recording layer 20 of the optical recording medium according to the present invention acts as a heat generating layer by absorption of a recording laser beam and a partial mirror for providing a contrast difference before and after recording. Thus, it is preferably for the metal recording layer to have 30∼300Å thickness, 5∼95% transmittance and 5∼95% reflectivity. If the thickness thereof is 30Å or less, amount of heat generated by the light absorption for the recording is not sufficient to deform the substrate. On the contrary, if the thickness thereof exceeds 300Å, the expansion of the substrate for the recording is hindered by the metal recording layer, so that the recorded portion is less deformed. As the metal recording layer becomes thick, a great reflection occurs at the metal recording layer to scatter the light. Accordingly, it is difficult to obtain a high reflectivity. Also, preferably, the thermal conductivity of the metal recording layer is 4W/cm°C or less. If the thermal conductivity of the metal recording layer exceeds 4W/cm°C, the recording layer heated by a laser beam cannot contain the heat while the heat of the recording layer is rapidly transferred to the circumstance, so that it is difficult to heat the recording layer to a required temperature or more. Even though the recording layer is heated to the intended temperature, adjacent tracks may be deformed since the size of the recording pit is increased. Also, it is preferable that the thermal linear expansion coefficient of the metal recording layer is equal to or higher than 3×10 -6 /°C. If the linear expansion coefficient is less than the level, the metal recording layer is cracked by the expansion caused by the deformation of the substrate for the recording, so that a good recorded signal value cannot obtained. The metal recording layer may be formed of gold (Au), aluminum (Al), chromium (Cr), palladium (Pd), titanium (Ti), copper (Cu), nickel (Ni), platinum (Pt), silver (Ag), tantalum (Ta), iron (Fe) or alloys thereof using a vacuum deposition, electron beam or sputtering method. The buffering layer does not nearly absorb the recording light and buffers the expansion force of the substrate to decrease the deformation of the reflecting layer. The buffering layer consists of a material capable of being easily deformed and having an appropriate fluidity, as a layer absorbing the deformation of the substrate and the metal recording layer. Thus, preferably, a melt-viscosity of the material for the buffering layer at 140°C is 10∼50,000Pa.S. If the melt-viscosity is 10Pa.S or less, the buffering layer is seriously deformed by the expansion of the substrate, causing a great deformation at the land side thereof to make inferior a recorded signal. On the contrary, the melt-viscosity exceeds 50,000Pa.S, the buffering layer cannot perform its own buffering function. Also, preferably, a glass transition temperature (Tg) of the material of the buffering layer is 70∼130°C, more preferably, lower than a glass transition temperature of the substrate. If the glass transition temperature (Tg) of the buffering layer is 70°C or lower, the long-term stability of data is deteriorated. On the contrary, if the glass transition temperature (Tg) thereof is 130°C or more, the deformation of the substrate is hindered, lowering a recording sensitivity. The buffering layer is consisted of at least one selected from the group consisting of vinylalcohol resin, vinylacetate resin, polyester resin, polyether resin, polystyrene resin, polyurethane resin, cellulose resin and fatty acid resin. Also, the buffering layer may include a material having a high refractive index, e.g., dye, to increase the contrast after the recording. Here, preferably, the dye content is 30wt% or less. If the dye content exceeds 30wt%, the reflectivity is decreased by the absorption of the light and loss in economic aspect is caused. Generally, the buffering layer is formed by dissolving the material for the buffering layer in an organic solvent and then spin-coating the solution. Here, it is essential to use the organic solvent capable of easily dissolving the material for the buffering layer without damage to the substrate. As shown in FIG. 3, preferably, the thickness of the buffering layer is set to d 1 to provide 40% or more reflectivity, e.g., 50∼1,000nm. The reflecting layer is formed of a metal selected from the group consisting of Au, Al, Ag, Cu, Pd, Pt, Ti, Ta, Cr, Ni, Fe and alloys thereof, preferably, a metal selected from the group consisting of Au, Al, Cu, Cr and alloys thereof, to a thickness of 50∼1,500Å by a vacuum deposition or sputtering method. The protecting layer 50 protects other constituent layers of the optical recording medium. The protecting layer 50 is formed by a general method. For example, the protecting layer 50 is formed by spin-coating an epoxyacrylate resin which is transparent and curable by ultraviolet rays, and has a great impact intensity, and then curing the spin-coated product by irradiating ultraviolet rays. In an optical recording medium of the present invention, having the above structure, a heat generating portion which generates heat by absorbing a laser beam is limited to the metal recording layer, so that the recording characteristic and productivity are improved by the combined characteristics of the pregroove of the substrate and the buffering layer, without using a dye. Also, the optical recording medium can be compatible with the CD due to its high reflectivity at the wavelength of 600nm or higher. Hereinafter, the present invention will be described in detail with reference to the following examples. However, the present invention is not limited to the following examples. Example 1 An aluminum (Al) recording layer was vacuum-deposited to 10nm thickness on a polycarbonate (PC) substrate with 1.2mm thickness having pregrooves with 153nm depth, 0.5µm width at the uppermost portion thereof, 0.25µm width at the bottom thereof, 50° angle () at the slant side thereof and 1.6µm track pitch. Then, a coating solution obtained by dissolving 0.9g polymethylmethacrylate (PMMA, MW=9,000, melt-viscosity=20,000Pa.S at 140°C) in 10ml diacetone alcohol (DAA) was spin-coated on the Al recording layer at 2,000 rpm to form a buffering layer. Here, the thickness of the buffering layer corresponding to the pregroove side, measured by a scanning electron microscope (SEM), was about 220nm. After drying the resultant structure at 40°C in a vacuum oven, Al was vacuum-deposited to about 1,000Å to form a reflecting layer. Then, an ultraviolet (UV)-curable epoxyacrylate resin was spin-coated on the reflecting layer and then cured to form a protecting layer, resulting in a disc type optical recording medium according to the present invention. According to the result of the evaluation on the obtained disc, using an evaluation equipment adopting 780nm laser beam, reflectivity before the recording was 45%, and the maximum reflectivity R top was 66% and the CNR was 55dB using 0.7mW recording laser power with respect to a disc which was recorded at 1.3m/sec recording speed using 8mW recording power, 720kHz modulation. Under the above recording conditions, a recorded signal of 47dB or more CNR was reproduced at 4mW or more recording power as shown in FIG. 4. Also, after recording an audio signal in the disc using a CD-R recorder (RPD-1000, Pioneer), the recorded audio signal could be reproduced using a CD player (Mark II, Philips). According to the recording characteristics of the disc, evaluated by a CD-CATS (Audio Development Co., Sweden), the evaluated all items satisfied the standard of the CD. Also, the reflectivity of the disc was 54% at the wavelength of 650nm, and information recorded in the disc could be reproduced by a digital versatile disc player (DVDP). Example 2 A disc type optical recording medium was manufactured by the same method as that of Example 1, except that the material of the metal recording layer was replaced by CuAl with 11nm thickness, and the performance of the disc was evaluated. The reflectivity before the recording was 47%, and the average reflectivity and the maximum reflectivity R top were 59% and 66%, respectively, and the CNR was 57dB using 0.7mw recording laser power with respect to a disc which was recorded at 1.3m/sec recording speed using 8mW recording power, 720kHz modulation. Also, after recording an audio signal in the disc using a CD-R recorder (RPD-1000, Pioneer), the recorded audio signal could be reproduced using a CD player (Mark II, Philips). According to the recording characteristics of the disc, evaluated by a CD-CATS (Audio Development Co., Sweden), the evaluated all items satisfied the standard of the CD. Also, the reflectivity of the disc was 51% at the wavelength of 650nm, and information recorded in the disc could be reproduced by a DVDP. Example 3 A disc type optical recording medium was manufactured by the same method as that of Example 1, except that 0.5wt% dye (Red CV-S 300, ICI Co., refractive index ( n )=2.2 at 780nm) was added to a buffering layer. The reflectivity before the recording was 43%, and the average reflectivity and the maximum reflectivity R top were 59% and 65%, respectively, and the CNR was 59dB using 0.7mW recording laser power with respect to a disc which was recorded at 1.3m/sec recording speed using 8mW recording power, 720kHz modulation. Under the above recording conditions, a recorded signal of 47dB or more CNR was reproduced at 4mW or more recording power as shown in FIG. 4. Also, after recording an audio signal in the disc using a CD-R recorder (RPD-1000, Pioneer), the recorded audio signal could be reproduced using a CD player (Mark II, Philips). According to the recording characteristics of the disc, evaluated by a CD-CATS (Audio Development Co., Sweden), the evaluated all items satisfied the standard of the CD. Also, the reflectivity of the disc was 47% at the wavelength of 650nm, and information recorded in the disc could be reproduced by a DVDP. Example 4 A disc type optical recording medium was manufactured by the same method as that of Example 1, except that a substrate having pregrooves with 250nm depth, 0.6µm width at the uppermost portion thereof, 0.3µm width at the bottom thereof, 61° angle at the slant side thereof was used and a coating solution was prepared by dissolving 1.3g polymethylmethacrylate (PMMA, MW=9,000, melt-viscosity=20,000Pa.S at 140°C) in 10ml diacetone alcohol (DAA). A music recorded in the disc using a CD-R recorder could be reproduced by a CDP and a DVDP. The maximum reflectivity R top at 780nm was 71%, and the reflectivity at 650nm was 51%. Comparative Example 1 A dye solution obtained by dissolving 4.4g N,N'-2,5-cyclohexadien-1,4-diylidenbis[4-(dibutylamino)-N-[4-(dibutylamino)phenyl]-bis[(OC-6-11)-hexafluoro-antimonate(10)] (NK-3219, Nippon Kanko Shinko Kenkusho CO., Ltd., λ max =720nm) in 100ml DAA was deposited on the same substrate as Example 1 using a spin coater at 50rpm for 5 seconds, 1,500rpm for 15 seconds, and 4,000rpm at 30 seconds in sequence, and then fully dried. Then, an Au reflecting layer was formed to 100nm thickness using a sputter. After depositing a UV-curable resin on the Au reflective layer, the resultant structure was cured by irradiating UV to form a protecting layer with 10µm thickness. The maximum reflectivity R top was 66%, and the CNR was 65dB using 0.7mW recording laser power with respect to a disc which was recorded at 1.3m/sec recording speed using 8mW recording power, 720kHz modulation. However, the reflectivity at 650nm was 15%, so that the disc could not be played by a DVDP. Comparative Example 2 A disc type optical recording medium was manufactured by the same method as Example 1, except that pregrooves of the substrate have 90nm depth, 0.6µm width at the uppermost portion thereof, 0.08µm width at the bottom thereof, 19° angle at the slant side thereof and 1.6µm track pitch. According to the result evaluated by using an evaluation equipment (Apex), the reflectivity before the recording was 50%, and the CNR and the average reflectivity was 50dB and 66%, respectively, after the recording at 1.3m/sec recording speed using 8mW recording power. After recording using EFM, a clean eye pattern could not be observed due to the serious deformation at the land side, and the playback after recording an audio signal was impossible. Comparative Example 3 A disc type optical recording medium was manufactured by the same method as Example 1, except a buffering layer was formed using 0.6g PMMA (MW=38,000, melt-viscosity=200,000Pa.S at 140°C), and the recording was performed under the same condition as Example 1. The reflectivity before the recording was 52%, and the average reflectivity after the recording and the CNR were 55% and 45dB, respectively. Also, the pattern was not clean, and the playback was impossible after recording an audio signal using a CD-R recorder. The optical recording medium of the present invention can be compatible with a CD, and information recorded in the optical recording medium can be reproduced by a DVDP due to its high reflectivity at 650nm or higher. Also, a dye is scarcely used, so that the manufacturing costs are lowered with high productivity.

Claims: An optical recording medium comprising a substrate (10), a metal recording layer (20), a buffering layer (30) and a reflecting layer (40) which are sequentially stacked on the substrate (10), characterised in that the substrate (10) has pregrooves, the angle () of the slant side of the pregroove is 30∼90° and the buffering layer (30) has 10∼50,000Pa.S melt-viscosity at 140°C. The optical recording medium of claim 1, wherein the width at the bottom of the pregroove is 10∼450nm, the width at the uppermost of the pregroove is 400∼1,000nm, and the depth of the pregroove is 30∼450nm. The optical recording medium of claim 1 or 2, wherein the reflectivity of the optical recording medium is 40% or more at 600∼800nm. The optical recording medium of any preceding claim, wherein a protecting layer (50) is formed on the reflecting layer (40). The optical recording medium of any preceding claim, wherein the substrate (10) is formed of one resin selected from the group consisting of polycarbonate resin, polymethylmethacrylate resin, epoxy resin, polyester resin and amorphous polyolefin resin. The optical recording medium of claim 5, wherein the glass transition temperature (Tg) of the substrate (10) is 80∼200°C. The optical recording medium of claim 6, wherein the glass transition temperature (Tg) of the substrate (10) is 100∼200°C. The optical recording medium of any preceding claim, wherein the reflectivity of the optical recording medium increases after recording. The optical recording medium of any preceding claim, wherein at least one of the substrate (10) and the metal recording layer (20), and the buffering layer (30) has a deformed portion. The optical recording medium of claim 9, wherein the substrate (10) and the metal recording layer (20) have the deformed portion, and a portion of the buffering layer (30) corresponding to the deformed portion has a reduced thickness. The optical recording medium of claim 9, wherein the substrate (10) and the metal recording layer (20), and the buffering layer (30) have the deformed portions corresponding to each other. The optical recording medium of claim 11, wherein the reflecting layer (40) has a deformed portion corresponding to the deformed portion of the buffering layer (30). The optical recording medium of any preceding claim, wherein the thickness of the metal recording layer (20) is 30∼300Å and a coefficient k of the imaginary part of a complex refractive index is greater than or equal to 0.01. The optical recording medium of claim 13, wherein the metal recording layer (20) is formed of a metal having 4W/cm°C or less thermal conductivity. The optical recording medium of claim 14, wherein the metal comprises one selected from the group consisting of gold (Au), aluminum (Al), chromium (Cr), palladium (Pd), titanium (Ti), copper (Cu), nickel (Ni), platinum (Pt), silver (Ag), tantalum (Ta), iron (Fe) and alloys thereof. The optical recording layer of any preceding claim, wherein the buffering layer (30) has a thickness of 50∼1,000nm. The optical recording medium of any preceding claim, wherein the glass transition temperature (Tg) of the buffering layer (30), is 70∼130°C. The optical recording medium of any preceding claim, wherein the buffering layer (30) comprises at least one resin selected from the group consisting of vinylalcohol resin, vinylacetate resin, acrylate resin, polyester resin, polyether resin, polystyrene resin, polyurethane resin, cellulose resin, fatty acid resin and copolymers thereof. The optical recording medium of any preceding claim, wherein the buffering layer (30) includes a dye of 30wt% or less based on the weight of the buffering layer (30).

Inventors: HUH YOUNG-JAE, LEE SOO-HYUNG, MIN KYUNG-SUN, HUH, YOUNG-JAE, LEE, SOO-HYUNG, MIN, KYUNG-SUN
Applicants: SAMSUNG ELECTRONICS CO LTD, SAMSUNG ELECTRONICS CO., LTD.
Application year: 1997
Main classification: G11B7
IPC codes: G11B7