Liquid crystal composition, use thereof and liquid crystal display element

Abstract: A chiral nematic liquid crystal composition is provided, which has a broad d/P margin, particularly for corresponding to a large size of LCD panel, while satisfying various characteristics sought for STN display mode, and which contains as a first component, at least one member of compounds expressed by the formulas (I-a) to (I-d), as a second component, at least one member of compounds expressed by the formulas (II) to (V), and as a third component, a chiral component expressed by the formula (X), R 5 -(B)-Z 2 -(C)-R 6 R 7 -(D)-Z 3 -(E)-Z 4 -(G)-R 8 In these formulas, R 1 to R 5 represent an alkyl group of 1 to 10 carbon atoms, etc.; Z 0 to Z 4 represent -CH 2 CH 2 -, etc.; B,C,E and G represent 1,4-cyclohexylene or 1,4-phenylene; D represents 1,4-cyclohexylene or 1,3-pyrimidine-2,5-diyl; Q 1 and Q 2 represent H or F; and q and m each independently represent 0 or 1; R 1 to R 12 represent an alkyl group of 1 to 10 carbon atoms or an alkenyl group of 2 to 10 carbon atoms. This composition may be used in STN mode, TN mode or AN mode liquid crystal display elements. This invention also describes the liquid crystal display elements containing such composition.

Description: This invention relates to a nematic liquid crystal composition and more particularly,it relates to a nematic liquid crystal composition containing a chiral component which is preferable for super-twisted birefringence (STN) mode and a liquid crystal display element using the same. Liquid crystal display element (LCD) has been obtained by sealing a liquid crystal composition in a closed cell formed between two sheets of substrates. This LCD not only has a lower electric power consumption, but also can be made into a smaller size and light-weighted, as compared with CRT (Braun tube mode display); hence it has been successively used practically for various modes such as twisted nematic (TN) mode, super-twisted birefringence (STN) mode or active matrix (AM) LCD mode. US-A-4 203 862 describes a nematic liquid crystal composition useful in electro-optical display devices, the composition comprising: 4-cyanophenyl-4'-butylbenzoate: 15-30 mole %, 4-cyanophenyl-4'-heptylbenzoate: 20-40 mole %, 4-pentylphenyl-4'-pentylbenzoate: 20-35 mole %, 4-pentylphenyl-4'-(4"-pentylbenzoyloxy)-benzoate: 10-15 mole %, 4-cyano-4'-pentylbiphenyl: 10-20 mole %, chiral additive: 0.05-0.8 mole %. The chiral additive is cholesteryl nonanoate. This composition has a high positive dielectric anisotropy, a wide mesomorphic temperature range, high chemical stability and high transparency in thin layers. US-A-4 323 471 and 4 323 472 describe the addition of a chiral additive such as cholesteryl nonanoate in an amount of 0.1 to 0.8 weight % to a liquid crystal composition. The composition has a steep saturation curve, a high positive anisotropy and a wide mesomorphic temperature range. Among the above mentioned modes, STN mode having the molecular alignment of liquid crystals sealed in the upper and lower substrates, twisted by 180° to 270°, proposed by T.J. Scheffer et al. (Appl. Phys. Lett., 45 (10), 1021 (1984)), has been very often used particularly for use applications such as personal computer or word processors. For the liquid crystal compositions used for STN mode LCD, the following characteristics have been generally sought: (1) nematic liquid crystal phase of the composition is exhibited within a broad temperature range including room temperature and particularly the nematic-isotropic phase transition point (clearing point) is high; (2) in order to make the electric power consumption of a liquid crystal display element smaller, the threshold voltage is made lower; (3) the response time (τ) of a liquid crystal element is improved as much as possible (τ is made lower); hence the viscosity (η) of the composition is kept low; (4) in accordance with the liquid crystal display element, an adequate optical anisotropy (Δn) of the composition can be taken; and (5) in order to elevate the contrast of the liquid crystal display element, the steepness of voltage-transmittance characteristic of the composition is desired, and thereby the value of (V 10 /V 90 ) is reduced. Further, in the STN cell wherein the liquid crystal composition is sealed, there is a problem that if the twist pitch length P (µm) relative to the cell thickness (d) is too long (that is, the value of d/P becomes smaller than the predetermined value), the twist of liquid crystals becomes discontinuous and the so-called low dimensional domain (reverse domain) occurs, and on the contrary, if the above P becomes too short, the twist axis of liquid crystals largely deviates from the thickness direction of the cell and the so-called stripe domain occurs. Accordingly, even if the d value is somewhat changed, a liquid crystal composition having a broad range of d/P (d/P margin) wherein no domain occurs, has been sought. In recent years, particularly, it has been advanced to bring about LCD into a large size, getting an opportunity to spread note-type personal computers (PC), but the larger the size of the LCD is, the more difficult it is to keep the d uniform. This fact constitutes a main factor of increasing the proportion of domain-occurrenced panel at the mass production of a liquid crystal panel particularly having STN cell incorporated therein; hence it has become an urgent problem to avoid it. From such a viewpoint, a chiral nematic liquid crystal composition having a broad d/P margin has been strenuously required for the liquid crystal material. As apparent from the description mentioned below, the liquid crystal composition of the present invention contains compounds expressed by the formulas (1-a) to (1-d) and (II) to (V), respectively as a first component and a second component, and further a chiral component expressed by the formula (X) as a third component, but a liquid crystal composition apparently similar thereto has been disclosed in, for example, Japanese patent application laid-open No. Hyo Hei 04-501878. However, the chiral component (an optically active compound) used in this publication is limited to p-(p-n-hexylbenzoyloxy)benzoic acid-2-octyl ester made by Merck Corporation (trade name: S-811), and such a compound aims at achieving a short switching time, but there is no description as to d/P margin, and in fact, it has a drawback that the range of d/P is narrow. The object of the present invention is to provide a chiral nematic liquid crystal composition having a broad d/P margin, particularly corresponding to a large size of LCD panel, while satisfying various characteristics required for the above-mentioned STN display mode. The liquid crystal composition of the present invention comprises as a first component, at least one member of compounds expressed by the formulas (I-a) to (I-d): wherein R 1 , R 2 , R 3 and R 4 each independently represent an alkyl group of 1 to 10 carbon atoms, and one optional or two or more not-adjacent methylene groups (-CH 2 -) in the group may be replaced by oxygen atom or -CH=CH-; Z 0 represents -COO- or -CH 2 CH 2 -; Z 1 represents -CH 2 CH 2 -, -COO- or single bond; Q 1 represents H or F; A 1 represents 1,4-cyclohexylene, 1,4-phenylene, 1,3-dioxane-2,5-diyl or 1,3-pyrimidine-2,5-diyl; A 2 and A 4 each independently represent 1,4-cyclohexylene or 1,4-phenylene; A 3 represents 1,4-cyclohexylene, 1,4-phenylene or 1,3-pyrimidine-2,5-diyl; A 5 represents 1,4-cyclohexylene or 1,4-phenylene whose H on the lateral position may be replaced by F; and q and m each independently represent 0 or 1, as a second component, at least one member of compounds expressed by the formulas (II) to (V): R 5 ―(B)―Z 2 ―(C)―R 6 R 7 -(D)-Z 3 -(E)-Z 4 -(G)-R 8 wherein R 5 and R 6 each independently represent an alkyl group of 1 to 10 carbon atoms and one or two or more not-adjacent methylene groups (-CH 2 -) in the group may be replaced by oxygen atom or -C H =CH-; B represents 1,4-cyclohexylene, 1,4-phenylene or 1,3-pyrimidine-2,5-diyl; C represents 1,4-cyclohexylene or 1,4-phenylene; and Z 2 represents -C≡C-, -COO-, -CH 2 CH 2 -, -CH=CH- or single bond, R 7 and R 8 each independently represent an alkyl group of 1 to 10 carbon atoms and one optional or two or more not-adjacent methylene groups (-CH 2 -) in the group may be replaced by oxygen atom (-O-) or -CH=CH-, D represents 1,4-cyclohexylene or 1,3-pyrimidine-2,5-diyl; E represents 1,4-cyclohexylene or 1,4-phenylene whose one H on the lateral position may be replaced by F; G represents 1,4-cyclohexylene or 1,4-phenylene; Z 3 represents -CH 2 CH 2 - or single bond; Z 4 represents -C≡C-, -COO-, -CH=CH- or single bond. R 9 to R 12 each independently represent an alkyl group of 1 to 10 carbon atoms or an alkenyl group of 2 to 10 carbon atoms; and Q 2 represents H or F, provided that in no case B is 1,4-cyclohexylene or 1,4-phenylene, Z 2 is -COO- and C is 1,4-phenylene at the same time, and as a third component, cholesteryl nonanoate expressed by the formula (X) in a quantity of 1.0 to 3.0 parts by weight based upon 100 parts by weight of the base liquid crystalline composition. wherein the composition does not contain a compound of the formula wherein R 1 represents an alkyl group of 1 - 10 carbon atoms or an alkenyl group of 2 - 10 carbon atoms, wherein one -CH 2 - group or two or more -CH 2 -groups not adjacent to each other may be substituted by -0-, and n represents an integer of 0 - 20. The liquid crystal composition may further contain as a fourth component, at least one member of compounds expressed by the formulas (VI) and/or (VII): wherein R 13 represents an alkyl group of 1 to 10 carbon atoms or an alkenyl group of 2 to 10 carbon atoms; Q 3 represents H or F; and k represent 0 or 1, and R 14 represents an alkyl group of 1 to 10 carbon atoms or an alkenyl group of 2 to 10 carbon atoms; J represents 1,4-cyclohexylene or 1,4-phenylene; Q 4 and Q 5 each independently represent H or F; Z 5 and Z 6 each independently represent -COO- or single bond; and h represents 0, 1 or 2. By using these liquid crystal compositions of the present invention, it is possible to obtain liquid crystal display elements satisfying the object of the present invention. As preferable examples of the first component used in the liquid crystal compositions of the present invention, compounds respectively expressed by the formulas (I-a-1) to (I-a-6), as regards the formula (1-a), the formulas (I-b-1) to (I-b-4) as regards the formula (I-b), the formulas (I-c-1) to (I-c-5) as regards (I-c), and (I-d-1) to (I-d-11) as regards (I-d), can be mentioned: In these formulas, R represents an alkyl group of 1 to 10 carbon atoms or an alkenyl group of 2 to 10 carbon atoms; R' represents an alkanediyl or alkenediyl of 1 to 9 carbon atoms; and the sum of carbon atoms and oxygen atoms in ROR', ROR'O- and ROCH 2 is 10 or less. Among these compounds, particularly those expressed by the formulas (I-a-1), (I-a-2), (I-a-3), (I-a-5), (I-a-6), (I-b-1), (I-b-2), (I-c-1), (I-d-1), (I-d-4), (I-d-5), (I-d-6), (I-d-7), (I-d-10) and (I-d-11) are preferably used. These compounds of the first component exhibit a positive and large dielectric anisotropy (Δε); hence they are used mainly for lowering the threshold voltage (V 10 ) and for improving the steepness which is important as STN characteristics. The content of the first component is 5 to 80% by weight,preferably 10 to 60% by weight based upon the total weight of the liquid crystal composition. If the content is lower than 5% by weight, the liquid crystal composition has a small Vth and the steepness becomes inferior. On the contrary, if it exceeds 80% by weight, the viscosity of the liquid crystal composition becomes high. Further, as preferable examples of the second component, compounds expressed by the formulas (II-1) to (II-19) as regards the formula (II), the formulas (III-1) to (III-16) as regards the formula (III), the formulas (IV-1) to (IV-2), as regards the formula (IV), and the formula (V-1), as regards the formula (V) can be respectively mentioned. In these formulas, R and R' each independently represent an alkyl group of 1 to 10 carbon atoms or an alkenyl group of 2 to 10 carbon atoms; and the sum of carbon atoms and oxygen atoms in -OC 2 H 4 OR', -OR', and ROCH- is 10 or less. Among these compounds, particularly those expressed by the formulas (II-1), (II-2), (II-4), (II-5), (II-6), (II-9), (II-10), (II-14), (II-15), (III-1), (III-2), (III-5), (III-9), (III-11), (III-12), (III-14), (III-15), (IV-1) and ( V -1) are preferably used. The compounds of the second component exhibit a negative or weakly positive Δε. Among these compounds, those expressed by the formula (II) are used mainly for reducing the viscosity of the liquid crystal composition and/or adjusting its Δn. Further, compounds expressed by the formulas (III) to (V) are used for broadening the nematic range such as elevating the clearing point of the liquid crystal composition, and/or for adjusting Δn and viscosity. The content of the second component is 5 to 80% by weight, preferably 10 to 60% by weight based upon the total weight of the liquid crystal composition. If the content is less than 5% by weight, the viscosity of the liquid crystal composition becomes high, and on the contrary, if it exceeds 60% by weight, the threshold voltage (V 10 ) becomes high. The third component used in the liquid crystal composition of the present invention is cholesteryl nonanoate expressed by the above formula (X) (hereinafter referred to as CN) which is an optically active compound, and it is used for adjusting the pitch length of twist of the liquid crystal composition. This third component has been found to afford a broad d/P margin differently from other optically active compounds (e.g. S-811 made by Merck Corporation), but the reason is not always clarified. In connection with this, when the same chiral nematic liquid crystal composition is used in a liquid crystal display element, but the aligned membrane is changed to that having a higher pretilt, it has been known that d/P margin of the display element is broadened along with the above change. In view of this fact, the following interpretation is made: in the chiral nematic composition using CN, its pretilt angle becomes larger due to the particular structure of CN, whereby the effectiveness that d/P margin is broadened, is exhibited. The content of the third component is quantity of 1.0 to 3.0 parts by weight so that the d/P value is retained within a range of 0.3 to 0.65. If the d/P value is less than 0.3, a low dimensional domain occurs, and if it exceeds 0.65, stripe domain occurs. Preferably, the quantity thereof is 1.2 to 2.7 parts by weight, based upon 100 parts by weight of the base liquid crystal composition. As preferable examples of the fourth component further used in the liquid crystal composition of the present invention, compounds expressed by the formulas (VI-1) to (VI-3) as regards the formula (VI), and the formulas (VII-1) to (VII-20) as regards the formula (VII) can be mentioned: In these formulas, R represents an alkyl group of 1 to 10 carbon atoms. Among the compounds of the above formulas, particularly those expressed by the formulas (VI-1), (VI-2), (VI-3), (VII-1), (VII-5), (VII-6), (VII-7), (VII-8), (VII-9), (VII-10), (VII-11), (VII-12), VII-13), (VII-14), (VII-15), (VII-16), (VII-18), (VII-19) and (VII-20) are preferably used. The compounds of the fourth component exhibit a positive Δε, and are used particularly for reducing V 10 and improving its temperature-dependency. Further, they are also used for viscosity adjustment, Δn adjustment and broadening the nematic range by elevation of clearing point, etc. The content of the fourth component is 50% by weight or less, preferably 40% by weight or less, based upon the total weight of the liquid crystal composition. The liquid crystal composition of the present invention may further contain a suitable quantity of other compounds in addition to the first to the fourth components, for adjusting various characteristics requested for the liquid crystal composition, such as adjustments of the threshold voltage (V 10 ), nematic range, Δn, Δε, viscosity, etc. The liquid crystal composition of the present invention can be prepared according to a process which is conventional by itself, for example, according to a process of dissolving various components with each other at a high temperature, a process of dissolving the respective components in an organic solvent, and mixing, followed by distilling off the solvent under reduced pressure, or the like process. Further, if necessary, a suitable additive is added, whereby an improvement corresponding to aimed use applications is made and the composition is optimized. Such additives have been known to person of the skill in the art and described in literatures in detail. Further, when a dichroic pigment such as those of mellocyanine group, styryl group, azo group, azomethine group, azoxy group, quinophthalone group, anthraquinone group, tetrazine group, etc. is added, the resulting composition is also usable as that for guest-host (GH) mode. The liquid crystal composition is also usable as that for polymer dispersion type liquid crystal display element, represented by NCAP prepared by microcapsulating nematic liquid crystals, and a polymer network liquid crystal display element obtained by forming three-dimensional, reticular high polymer in liquid crystals (PDLCD), and besides, it is usable as liquid crystal composition for birefringence-control (ECB) mode and for dynamic scattering (DS) mode. The present invention will be described by way of Examples in more detail. In the compositions shown in the respective Examples and Comparative examples, the designations of compounds were carried out in accordance with the definitions shown in the below Table 1, and by corresponding the groups shown in the respective columns of left terminal group, bonding group, ring structure and right terminal group, to those shown in the symbols. The contents of the respective compounds mean % by weight, unless otherwise indicated. The data of the liquid crystal composition were shown by TNI (clearing point), TSN (smectic-nematic phase transition point), viscosity (20°C), Δn (optical anisotropy at 25°C), Δε (dielectric anisotropy at 25°C), V 10 (voltage at the time of a transmittance of 10%) and Δ (d/P). In addition, the above Δ (d/P) refers to a d/P value in the range where low dimensional domain and stripe domain do not occur, that is, d/P margin, and it is evaluated by filling a nematic liquid crystal composition prepared at the former step of the respective examples in an STN cell of a twist angle of 240° and a thickness d=5.8 to 6.2 µm, adding a chiral component gradually by 0.01 part by weight to 100 parts by weight of the composition, and evaluating by observation of the domain at that time. Comparative example 1 A nematic liquid crystal composition consisting of the following compound contents was prepared: V 2 -HB-C 12.0% 1V2-HB-C 12.0% 3-HB-C 8.0% 2-HHB-C 6.0% 3-HHB-C 6.0% 4-HHB-C 6.0% 5-HHB-C 6.0% 3-HB-O2 12.0% 3-HH-4 11.0% 3-H2BTB-2 5.0% 3-H2BTB-3 4.0% 3-H2BTB-4 4.0% 3-HB(F) TB-2 8.0% The characteristics of this nematic liquid crystal composition were sought. The results were as follows: TNI = 114.1°C TSN > - 3 0°C η = 21.9mPa·s (η: viscosity) Δn = 0.145 Δε = 7.1 V 10 = 2.42V To this nematic liquid crystal composition (100 parts by weight) was added gradually from 0.92 parts to 1.02 parts by weight of p-(p-n-hexylbenzoyloxy)benzoic acid-2-octyl ester (made by Merck Corporation, tradename: S-811) as a chiral component (optically active compound), followed by domain-observing, to give Δ(d/p)=0.017. Example 1 A chiral component was added gradually in the same manner as in Comparative example 1 except that the above-mentioned CN was used from 2.14 parts to 2.59 parts in place of S-811, followed by domain observation of the resulting liquid crystal composition in the same manner. As a result, Δ(d/P)=0.049. It is known that this value is far larger than that of Comparative example 1. Comparative example 2 A nematic liquid crystal composition consisting of the following compound contents was prepared: 1V2-BEB (F, F) -C 7.0% 3O1-BEB (F) -C 5.0% 3-HB-C 14.0% 3-HB-O2 11.0% 3-HH-4 11.0% 3-HHB- 1 10.0% 3-HHB-O1 4.0% 3-HHB-F 4.0% 3-HHB-3 15.0% 3-HB (F)TB-2 4.0% 3-HB (F) TB-2 3.0% 3-H2BTB-2 4.0% 3-H2BTB-3 4.0% 3-H2BTB-4 4.0% The characteristics of this nematic liquid crystal composition were sought. The results were as follows: TNI = 1 0 3. 5°C TSN > -30°C η = 17.9mPa·S Δn = 0.130 Δε = 8.1 V 10 = 2.05V To this nematic liquid crystal composition (100 parts by weight) was added gradually from 0.74 parts to 0.87 parts by weight of the above S-811 made by Merck Corporation as a chiral component, followed domain observation of the resulting liquid crystal composition, to give Δ(d/P)=0.08. Example 2 A chiral component was added gradually in the same manner as in Comparative example 2 except that the above CN was used from 1.43 parts to 2.01 parts in place of S-811, followed by domain observation of the resulting liquid crystal composition, to give Δ(d/P)=0.120. This value is known to be far larger than that of Comparative example 2. Comparative example 3 A nematic liquid crystal composition consisting of the following compound contents was prepared: V2-HB-C 10.0% 1V2-BH-C 10.0% 3-HB-C 22.0% 3-HB(F) -C 5.0% 3-HH-4 4.0% 3-HHE-F 4.0% 5-HHE-F 4.0% 3-HHB-1 10.0% 3-HHB-O1 5. 0% 3-HHB-3 14.0% 3-HHB-F 5. 0% 3-H2BTB-2 3.0% 3-H2BTB-3 4. 0% The characteristics of this nematic liquid crystal composition were sought. The results were as follows: TNI = 103.1°C TSN > -30°C η = 20.6mPa·s Δn = 0.122 Δε = 7.4 V 10 = 2.25V To this nematic liquid crystal composition (100 parts by weight) was added gradually from 0.64 parts to 0.73 parts of the above S-811 made by Merck Corporation as a chiral component, followed by domain-observation of the resulting liquid crystal composition, to give Δ(d/P)=0.010. Example 3 A chiral component was added in the same manner as in Comparative example 3 except that the above CN was used from 1.87 parts to 2.18 parts in place of S-811, followed by domain observation of the resulting liquid crystal composition, to give Δ(d/P)=0.020. This value is known to be far larger than that of Comparative example 3. Example 4 A nematic liquid crystal composition consisting the following compound contents was prepared: 3-HB-C 3.0% 3-HB (F)-C 13.0% 3O1-BEB (F)-C 13.0% 2-BB-C 6.0% 5-BB-C 5.0% 3-HHB (F) -C 5.0% 3-PyBB-F 11.0% 4-PyBB-F 10.0% 5-PyBB-F 10.0% 3-H2BTB-2 4.0% 3-H2BTB-3 4.0% 3-H2BTB-4 4.0% 3-HB (F) TB-2 6.0% 3-HB (F) TB-3 6.0% The characteristics of this nematic liquid crystal composition were sought. The results were as follows: TNI = 105.4°C TSN > -3 0°C η = 54.2mPa·s Δn = 0.217 Δε = 17. 0 V 10 = 1.41V To this nematic liquid crystal composition was added the above CN as a chiral component as in Example 1, followed by domain observation of the resulting liquid crystal composition, to give a Δ(d/P)=0.0480. Example 5 A nematic liquid crystal composition consisting of the following compound components was prepared: V2-HB-C 3.0% 1V2-HB-C 13.0% 2-BEB-C 12.0% 3-BEB-C 8.0% 2-BTB-O1 8.0% 3-BTE-O1 7.0% 4-BTB-O1 7.0% 1-BTB-3 13.0% 3-H2BTB-2 5.0% 3-H2BTB-3 4.0% 3-H2BTB-4 4.0% 3-HB (F) TB-2 8.0% 3-HB(F)TB-3 8.0% The characteristics of this nematic liquid crystal composition were sought. The results were as follows: TNI = 79.5°C TSN > -20°C η = 23.8mPa·s Δn = 0.222 Δε = 9.0 V 10 = 1.69V To this nematic liquid crystal composition was added the above CN as a chiral component as in Example 1, followed by domain observation, to give a Δ(d/P)=0.041. Example 6 A nematic liquid crystal composition consisting of the following compound components was prepared: V2-HB-C 10.0% 1V2-HB-C 10.0% 3-HB-C 21.0% 5-HB-C 12.0% 2-BTB-O1 4.0% 2-PyB-2 4.0% 2-PyB-3 3.0% 3-HH-4 8.0% 3-HHB-1 6.0% 3-HHB-3 6.0% 3-H2BTB-2 3.0% 3-H2BTB-3 3.0% 2-PyBH-3 4.0% 3-PyBH-3 3.0% 3-PyBB-F 3.0% The characteristics of this nematic liquid crystal composition were sought. The results were as follows: TNI = 77.1°C TSN > -3 0°C η = 18.7mPa·s Δn = 0.140 Δε = 8.0 V 10 = 1.78V To this nematic liquid crystal composition was added the above CN as a chiral component as in Example 1, followed by domain observation of the resulting liquid crystal composition, to give a Δ(d/P)=0.039. Example 7 A nematic liquid crystal composition consisting of the following compound contents was prepared: 101-HB-C 10.0% 201-HB-C 8.0% 3-HB-C 8.0% 3-HB(F)B-C 5.0% 3-HHB-C 7.0% 101-HH-3 3.0% 101-HH-5 9.0% 2-BTB-O1 3.2% 3-BTB-O1 3.2% 4-BTB-O1 3.2% 4-BTB-O2 3.2% 5-BTB-O1 3.2% 2-HHB (F) -F 10.0% 3-HHB (F) -F 7.0% 5-HHB (F) -F 7.0% 3-HHB-1 7.0% 3-HHB-O1 3.0% The characteristics of this nematic liquid crystal composition were sought. The results were as follows: TNI = 75.7°C TSN > -20°C η = 21.5mPa·s Δn = 0.123 Δε = 8.2 V 10 = 1.66V To this nematic liquid crystal composition was added the above CN as a chiral component as in Exmaple 1, followed by domain observation of the resulting liquid crystal composition, to give a Δ(d/P)=0.037. Example 8 A nematic liquid crystal composition consisting of the following compound contents was prepared: 3O1-BEB (F)-C 11.0% V2-HB-C 11.0% 3-HB-O2 3.0% 2-BTB-O1 6.8% 3-BTB-O1 6.8% 4-BTB-O1 6.8% 4-BTB-O2 6.8% 5-BTB-O1 6.8% 3-HHB-O1 3.0% 3-H2BTB-2 2.0% 3-H2BTB-3 3.0% 3-H2BTB-4 3.0% 3-HB (F) TB-2 6.0% 3-HB (F) TB-3 6.0% 3-HB (F) TB-4 6.0% 2-PyBH-3 4.0% 3-PyBH-3 4.0% 3-PyBB-2 4.0% The characteristics of this nematic liquid crystal composition were sought. The results were as follows: TNI=96.5°C TSN>-30°C η=30.2mPa·s Δn=0.220 Δε=7.6 V 10 =2.08V To this nematic liquid crystal composition was added the above CN as a chiral component as in Example 1, followed by domain observation of the resulting liquid crystal composition, to give a Δ(d/P)=0.062. Example 9 A nematic liquid crystal composition consisting of the following compound contents was prepared: V2-HB-C 9.0% 1V2-HB-C 9.0%. 3-HB-C 14.0% 101-HB-C 8.0% 201-HB-C 4.0% 2-HHB-C 5.0% 3-HHB-C 5.0% 3-HH-4 10.0% 101-HH-5 8.0% 2-BTB-O1 11.0% 3-HHB-1 8.0% 3-HHB-3 9.0% The characteristics of this nematic liquid crystal composition were sought. The results were as follows: TNI=80.0°C TSN>-30°C η=18.8mPa·s Δn=0.126 Δε=9.0 V 10 =1.89V To this nematic liquid crystal composition was added the above CN as a chiral component as in Example 1, followed by domain observation of the resulting liquid crystal composition, to give a Δ(d/P)=0.026. Example 10 A nematic liquid crystal composition consisting of the following compound contents was prepared: 1V2-BEB (F, F) -C 12.0% 3O1-BEB(F)-C 12.0% 2-HB-C 12.0% 3-HB-C 19.0% 2-HHB-C 4. 0% 3-HHB-C 5.0% 4-HHB-C 4.0% 5-HHB-C 4.0% 3-HB-O2 7.0% 3-HHB-1 7.0% 3-HHB-O1 4.0% 3-H2BTB-2 4.0% 3-H2BTB-3 3.0% 3-H2BTB-4 3.0% The characteristics of this nematic liquid crystal composition were sought. The results were as follows: TNI=82.1°C TSN>-20°C η =30.5mPa·s Δn=0.142 Δε=19.3 V 10 =1.19V To this nematic liquid crystal composition was added the above CN as a chiral component as in Example 1, to give a Δ(d/P)=0.055. Example 11 A nematic liquid crystal composition consisting of the following compound contents was prepared: V2-HB-C 12.0% 1V2-HB-C 11.0% 1V2-BEB(F, F)-C 11.0% 2-BTB-1 8.0% 4-BTB-O2 8.0% 5-BTB-O1 6.0% 3-HH-4 3.0% 3-HH-EMe 3.0% 3-H2BTB-2 4.0% 3-H2BTB-3 4.0% 3-H2BTB-4 4.0% 2-H2BTB-3 4.0% 2-H2BTB-2 4.0% 3-HB(F)TB-2 6.0% 3-HB (F) TB-3 6.0% 3-HB (F)TB-4 6.0% The characteristics of this nematic liquid crystal composition were sought. The results were as follows: TNI=87.5°C TSN> - 3 0°C η =22. 4mPa·s Δn=0.201 Δε=9.6 V 10 =1.74V To this nematic liquid crystal composition was added the above CN as a chiral component as in Example 1, followed by observation of the resulting liquid crystal composition, to give a Δ(d/P)=0.044. Example 12 A nematic liquid crystal composition consisting of the following compound contents was prepared: 2O1-BEB (F) -C 4.0% 3O1-BEB (F) -C 12.0% 5O1-BEB (F) -C 4.0% 1V2-BEB (F, F) -C 15.0% 3-HHEB-F 5.0% 5-HHEB-F 5.0% 3-HBEB-F 6.0% 3-HHB-F 3.0% 3-HB-O2 10.0% 3-HH-4 5.0% 3-HHB- 1 8.0% 3-HHB-3 6.0% 3-HHB-O1 4.0% 3-H2BTB-2 4.0% 3-H2BTB-3 4.0% 3-HB (F) TB-2 5.0% The characteristics of this nematic liquid crystal composition were sought. The results were as follows; TNI=92.5°C TSN>-30°C η=35.9mPa·s Δn=0.136 Δε=23.5 V 10 =1.10V To this nematic liquid crystal composition was added the above CN as a chiral component as in Example 1, followed by domain observation, to give a Δ(d/P)=0.053. Example 13 A nematic liquid crystal composition consisting of the following compound contents was prepared: 2-HB (F) -C 15.0% 3-HB (F) -C 15.0% 3-HHB-F 4.0% 3-HB-O2 10.0% 3-HH-4 10.0% 2-BTB-O1 10.0% 3-HHB-1 8.0% 3-HHB-3 16.0% 3-HHB-O1 4.0% 3-H2BTB-2 4.0% 3-H2BTB-3 4.0% The characteristics of this nematic liquid crystal composition were sought. The results were as follows: TNI=71.9°C TSN>-30°C η=15.7mPa·s Δn=0.118 Δε=6.6 V 10 =1.81V To this nematic liquid crystal composition was added the above CN as a chiral component as in Example 1, followed by domain observation of the resulting liquid crystal composition, to give a Δ(d/P)=0.036. Example 14 A nematic liquid crystal composition consisting of the following compound contents was prepared: 2-HB (F) -C 15.0% 2-HEB-F 2.4% 3-HEB-F 2.3% 4-HEB-F 2.3% 3-HHEB-F 5.0% 5-HHEB-F 5.0% 2-HHB (F) -C 13.0% 3-HHB (F) -C 13.0% 2-HHB (F) -F 14.0% 3-HHB (F) -F 14.0% 5-HHB (F) -F 14.0% The characteristics of this nematic liquid crystal composition were sought. The results were as follows: TNI=101.4°C TSN>-20°C η=35.6mPa·s Δn=0.095 Δε=24.8 V 10 =1.15V To this nematic liquid crystal composition was added the above CN as a chiral component as in Example 1, followed by domain observation of the resulting liquid crystal composition, to give a Δ(d/P)=0.066. Example 15 A nematic liquid crystal composition consisting of the following compound contents was prepared: 2-HB (F) -C 14.0% 3-HB (F) -C 13.0% 5-HB (F) -C 9.0% 2-BB-C 13.0% 2-BEB-C 12.0% 3-BEB-C 4.0% 2-HHB (F) -C 9.0% 3-HHB (F) -C 12.0% 2-HHB-C 3.0% 3-HHB-C 3.0% 3-PyBB-F 8.0% The characteristics of this nematic liquid crystal composition were sought. The results were as follows: TNI=65.8°C TSN>-20°C η=52.3mPa·s Δn=0.150 Δε=19.1 V 10 =1.0 1V To this nematic liquid crystal composition was added the above CN as a chiral component as in Example 1, followed by domain observation, to give a Δ(d/P)=0.038. Example 16 A nematic liquid crystal composition consisting of the following compound contents was prepared: 3-HB (F) -C 3.0% 3-HB-C 21.0% 3-HHB-C 5.0% 5-PyB-F 10.0% 3-HB-O2 4.0% 2-BTB-1 6.0% 3-HH-4 9.0% 3-HH- 5 11.0% 3-HHB-1 10.0% 3-HHB-3 14.0% 3-HHB-O1 3.0% 3-HEBEB-2 2.0% 3-HEBEB-F 2.0% The characteristics of this nematic liquid crystal composition were sought. The results were as follows: TNI=81.7°C TSN>-30°C η =13.8mPa·s Δn=0. 114 Δε=5.4 V 10 =2.19V To this nematic liquid crystal composition was added the above CN as a chiral component as in Example 1, followed by domain observation of the resulting liquid crystal composition, to give a Δ(d/P)=0.047. Example 17 A nematic liquid crystal composition consisting of the following compound contents was prepared: 2-BB-C 8.0% 4-BB-C 6.0% 2-HB-C 10.0% 3-HB-C 13.0% 3-HHB-F 5.0% 2-HHB-C 4.0% 3-HHB-C 6.0% 5-PyB-F 6.0% 3-PyBB-F 6.0% 2-BTB-O1 2.0% 2-HHB-1 6.0% 3 -HHB-1 8.0% 3-HHB-3 15.0% 3-HHB-O1 5.0% The characteristics of this nematic liquid crystal composition were sought. The results were as follows: TNI=99. 4°C TSN>-30°C η =22.3mPa·s Δn=0.144 Δε=8.7 V 10 =1.8 9V To this nematic liquid crystal composition was added the above CN as a chiral component as in Example 1, followed by domain observation of the resulting liquid crystal composition, to give a Δ(d/P)=0.029. Example 18 A nematic liquid crystal composition consisting of the following compound contents was prepared: 5-BB-C 7.0% 3-HHB-F 4.0% 3-HB-O2 14.0% 3-HB-O4 13.0% 3-PyB-4 3.1% 4-PyB-4 3.1% 6-PyB-4 3.2% 3-PyB-5 3.2% 4-PyB-5 3.2% 6-PyB-5 3.2% 6-PyB-O5 4.0% 6-PyB-O6 4.0% 6-PyB-O7 4.0% 6-PyB-O8 4.0% 2-HHB-1 4.0% 3-HHB-1 8.0% 3 -HHB- 3 10.0% 3-HHB-O1 5.0% The characteristics of this nematic liquid crystal composition were sought. The results were as follows. TNI=65.0°C TSN>-20°C η =28.1mPa·s Δn=0.121 Δε=3.2 V 10 =3.21V To this nematic liquid crystal composition was added the above CN as a chiral component as in Example 1, followed by domain observation, to give a Δ(d/P)=0.023. Example 19 A nematic liquid crystal composition consisting of the following compound contents was prepared: 3-HB-C 13.0% 5-HB-C 13.0% 3-HHB-1 7.0% 3-HHB-O1 3.0% 3-HHB-CL 4.0% 3-H2BTB-2 4.0% 3-H2BTB-3 3.0% 2-HHB (F) -F 7.0% 3-HHB (F) -F 7.0% 5-HHB (F) -F 7.0% 2-HBB (F) -F 4.0% 3-HBB (F)-F 4.0% 5-HBB (F) -F 4.0% 3-HHB-O2 10.0% 2-HHEBB-F 5.0% 3-HHEBB-F 5.0% The characteristics of this nematic liquid crystal composition were sought. The results were as follows: TNI=112.7°C TSN>-20°C η =24.0mPa·s Δn=0.123 Δε=5.8 V 10 =2.40V To this nematic liquid crystal composition was added the above CN as a chiral component as in Example 1, followed by domain observation, to give Δ(d/P)=0.049. Example 20 A nematic liquid crystal composition consisting of the following compound contents was prepared: 3-HB-C 10.0% 4-HB-C 3.0% 5-BB-2 2.0% 2-BTB- 1 10.0% 2-BTB-3 10.0% 3-HH-4 10.0% 3-HB-O2 10.0% 3-HHB-3 10.0% 3-HHEB (F) -F 10.0% 3-HBEB (F, F) -F 5.0% 3-HBB (F, F) -F 5.0% 2-H2BB (F, F) -F 5.0% 3-HB-CL 5.0% 5-HHB-CL 5.0% The characteristics of this nematic liquid crystal composition were sought. The results were as follows: TNI=61.2°C TSN>-30°C η=16. 1mPa·s Δn=0.131 Δε=4.3 V 10 =2.13V To this nematic liquid crystal composition was added the above CN as a chiral component as in Example 1, followed by domain observation, to give a Δ(d/P)=0.035. As described above, according to the present invention, it is possible to provide a liquid crystal composition having a broad d/P margin, particularly in order to correspond to bringing but LCD panel into a large size, while satisfying various characteristics.

Claims: A liquid crystal composition which comprises as a first component, at least one member of compounds expressed by the formulas (I-a) to (I-d): wherein R 1 , R 2 , R 3 and R 4 each independently represent an alkyl group of 1 to 10 carbon atoms, and one optional or two or more not-adjacent methylene groups (-CH 2 -) in the group may be replaced by oxygen atom or -CH=CH-; Z° represents -COO- or -CH 2 CH 2 -; Z 1 represents -CH 2 CH 2 -, -COO- or single bond; Q 1 represents H or F; A 1 represents 1,4-cyclohexylene, 1,4-phenylene, 1,3-dioxane-2,5-diyl or 1,3-pyrimidine-2,5-diyl; A 2 and A 4 each independently represent 1,4-cyclohexylene or 1,4-phenylene; A 3 represents 1,4-cyclohexylene, 1,4-phenylene or 1,3-pyrimidine-2,5-diyl; A 5 represents 1,4-cyclohexylene or 1,4-phenylene whose H on the lateral position may be replaced by F; and q and m each independently represent 0 or 1, as a second component, at least one member of compounds expressed by the formulas (II) to (V): R 5 ―(B)―Z 2 ―(C)―R 6 R 7 ―(D)―Z 3 ―(E)―Z 4 ―(G)―R 8 wherein R 5 and R 6 each independently represent an alkyl group of 1 to 10 carbon atoms and one or two or more not-adjacent methylene groups (-CH 2 -) in the group may be replaced by oxygen atom or -CH=CH-; B represents 1,4-cyclohexylene, 1,4-phenylene or 1,3-pyrimidine-2,5-diyl; C represents 1,4-cyclohexylene or 1,4-phenylene; and Z 2 represents -C≡C-, -COO-, -CH 2 CH 2 -, -CH=CH- or single bond, R 7 and R 8 each independently represent an alkyl group of 1 to 10 carbon atoms and one optional or two or more not-adjacent methylene groups (-CH 2 -) in the group may be replaced by oxygen atom (-O-) or -CH=CH-; D represents 1,4-cyclohexylene or 1,3-pyrimidine-2,5-diyl; E represents 1,4-cyclohexylene or 1,4-phenylene whose one H on the lateral position may be replaced by F; G represents 1,4-cyclohexylene or 1,4-phenylene; Z 3 represents -CH 2 CH 2 - or single bond; Z 4 represents -C≡C-, -COO-, -CH=CH- or single bond. R 9 to R 12 each independently represent an alkyl group of 1 to 10 carbon atoms or an alkenyl group of 2 to 10 carbon atoms; and Q 2 represents H or F, provided that in no case B is 1,4-cyclohexylene or 1,4-phenylene, Z 2 is -COO- and C is 1,4-phenylene at the same time, and as a third component, cholesteryl nonanoate expressed by the formula (X) in a quantity of 1.0 to 3.0 parts by weight based upon 100 parts by weight of the base liquid crystalline composition. wherein the composition does not contain a compound or the formula wherein R 1 represents an alkyl group of 1 - 10 carbon atoms or an alkenyl group of 2 - 10 carbon atoms, wherein one -CH 2 - group or two or more -CH 2 -groups not adjacent to each other may be substitutedby -0-, and n represents an integer of 0 - 20. A liquid crystal composition according to claim 1, wherein the first component and the second component are respectively contained in a quantity of 5 to 80% by weight and 5 to 80% by weight based upon the total weight of said composition. A liquid crystal composition according to either one of claim 1 or claim 2, which further contains as a fourth component, at least one member of compounds expressed by the formulas (VI) and/or (VII): wherein R 13 represents an alkyl group of 1 to 10 carbon atoms or an alkenyl group of 2 to 10 carbon atoms; Q 3 represents H or F and k represent 0 or 1, and R 14 represents an alkyl group of 1 to 10 carbon atoms or an alkenyl group of 2 to 10 carbon atoms; J represents 1,4-cyclohexylene or 1,4-phenylene; Q 4 and Q 5 each independently represent H or F; Z 5 and Z 6 each independently represent -COO- or single bond; and h represents 0, 1 or 2. A liquid crystal composition according to claim 3 wherein the fourth component is contained in a quantity of 50% by weight or less, based upon the total weight of the liquid crystal composition. A liquid crystal display element using the liquid crystal composition according to any one of the claims 1 to 4. Use of a liquid crystal composition as defined in any one of the claims 1 to 4 for a STN mode, TN mode or AN mode liquid crystal display element.

Inventors: MATSUSHITA TETSUYA, MURASHIRO KATSUYUKI, NAKAGAWA ETSUO, TAKESHITA FUSAYUKI, YAMAGUCHI TAKASHI, MATSUSHITA, TETSUYA, MURASHIRO, KATSUYUKI, NAKAGAWA, ETSUO, TAKESHITA, FUSAYUKI, YAMAGUCHI, TAKASHI
Applicants: CHISSO CORP, CHISSO CORPORATION
Application year: 1997
Main classification: C09K19
IPC codes: C09K19, G02F1