Low sodium edible salt mixture

Abstract: A low sodium edible salt composition comprises, based on dry weight of ingredients, 0-50% NaCl, 45-99.5% KCl and at least 0.5% additives, which comprise at least one edible nucleotide monophosphate salt and at least one member other than said nucleotide monophosphate salt selected from the group consisting of low organic acid, low organic acid salt, phosphoric acid, phosphate salt, a magnesium salt, sugar and burnt sugar. The additives have the effect of countering the bitter taste of KCl.

Description: The present invention concerns edible mineral salt mixtures. More specifically, the present invention concerns mixtures with a low sodium content. In the following, the term "edible salt" will be used to refer generally to salt compositions used in food, in both domestic use or in the food industry. The term "low sodium edible salt" will be used to denote such salt compositions with a low sodium content as compared to standard sodium-based edible salts. Sodium chloride is a major constituent of regular edible salts and as a result of wide use of edible salts in food seasoning at home as well as in the food industry, the sodium intake by individuals in the western world far exceeds recommended dosage. This overload of sodium has been associated with some adverse physiological effects including hypertension and renal complications. It has long been proposed to use in food low sodium edible salts, in which potassium chloride replaces some of the sodium chloride. However, potassium salt has a different, bitter taste which is regarded as unpleasant by most individuals. Many attempts have been made to produce low sodium edible salts with some of the ingredients designed to create an overall sensation resembling that of the standard, high sodium edible salt. Such low sodium edible salts have been disclosed in Australian Patent Application AU-A-51225/85, Japanese Patent Application, JP-88/134592, U.S. Patent No. 4,068,000, EP 125 021 and EP 59 363. The object of the present invention is to provide a low-sodium edible salt and a a low sodium, high potassium edible salt in which the bitter taste of potassium chloride is countered by the addition of additives and a process for the preparation of a low sodium table salt. The object is solved by a low sodium edible salt composition consisting of, based on dry weight of ingredient, 0-50% NaCI, 45-99.5% KCI and at least 0.5% additives, said additives consisting of maltol, at least one edible nucleotide monophosphate salt, and at least one member other than said nucleotide monophosphate salt selected from the group consisting of low organic acid, low organic add salt, phophoric acid, phosphate salt and a magnesium salt. The relative concentration of the various ingredients in the edible salt are given as percent (%), meaning the number of dry-weight units of ingredients per 100 dry-weight units of entire composition (w/w). Obviously, if the salt composition of the invention is mixed with water, while the relative concentration will not change, the actual concentration in the resulting solution will be less. Preferred edible nucleotide monophosphate salts are salts of 5-inosinate monophosphate (IMP) and 5-guanylate monophosphate (GMP). Particular examples are disodium salts of both IMP and GMP. Examples of low organic acids are tartaric acid, lactic acid, citric acid, gluconic acid and acetic acid, citric acid being currently preferred. Phosphoric acid salts are preferably mono- or dihydrogen phosphate. A currently preferred phosphoric acid salt is sodium pyrophosphate (Na 2 H 2 P 2 O 7 ). Magnesium salt may, for example, be magnesium sulphate (MgSO 4 •7H 2 O) or magnesium chloride (MgCl 2 •6H 2 O). For use as a standard table salt MgSO 4 is preferred since MgCl 2 is hygroscopic, i.e. it absorbs water. As a burnt sugar maltol is part of the low sodium edible salt composition. Preferred ranges of KCl and NaCl are as follows: KCI - 45-75% NaCl - 20-50% The metal ions (sodium, potassium and magnesium) may be included in the compositions as single or double salts. Typical concentration range of said additives are 0.5-15%, preferred range being 0.6-6.0%. Preferred concentration range for each of the different additives are as follows: Nucleotide monophosphate derivatives - 0.05-0.35%, 0.15-0.31% being particularly preferred; Low organic acids or salts thereof - 0.1-0.4%; Phosphoric acid salt - 1.5-3.5%; Maltol - 0.001-0.005%, about 0.003% being particularly preferred. While the composition of the invention may also be provided as a concentrated solution it is preferably provided as a dry composition. In order to avoid caking of such a dry composition, anti-caking agents such as sodium ferrocyanide (Na 4 Fe(CN) 6 •10H 2 O) are preferably added. In order to improve the free flowing properties a suitable agent therefore is preferably added, e.g. basic magnesium carbonate. One manner of obtaining a dry composition is to mix the various ingredients which are a priori in a dry form. However, various ingredients have different grain size and it was found that following agitation there is some segregation of the grains in the dry mixture based on their size. While this may not be a serious problem in the case, for example, of industrial use where large quantities and at times an entire batch are used at once, or where means for mixing the salt composition prior to use are provided, the issue of grain segregation may be a problem in a composition intended for domestic use as a seasoning. Another manner of preparing the salt composition is to mix all the ingredients in solution and then dry the solution by means of vacuum evaporation or any other drying technique. A suitable way of producing the salt composition, especially on an industrial scale, is continuous crystallization resulting in wet mixture with the same ratio of components that is in the feed solution. A preferred preparation method of the composition is spraying of a water solution of additives, other than those with a low water solubility (e.g. disodium acid pyrophosphate), on the potassium chloride crystals followed by addition of the low soluble additives in a dry form and subsequent drying. This method is novel per se and constitutes an aspect of the invention. The dry sodium chloride and some additives may then be mixed and precoated by spraying potassium chloride. By a preferred embodiment of this latter aspect, the spraying is performed after filtration or centrifugation of potassium chloride crystallized from the brine or on dry potassium chloride. The drying of moistened potassium chloride is typically achieved by spin or fluidized bed drying process. The different additives have different solubilities and accordingly are preferably sprayed in different spraying stages. For example, the nucleotide monophosphates are sprayed in a first spraying stage and the organic and phosphoric acids at a second spraying stage. The invention will now be illustrated by the following Examples of salt compositions in accordance with the invention, with occasional reference to the annexed drawing: BRIEF DESCRIPTION OF THE DRAWING Fig. 1 is a scheme of illustrating the manner of preparation of the composition exemplified in Example 1. EXAMPLES Example 1 Salt compositions of the invention comprising KCl, NaCl, IMP, GMP, citric acid, disodium pyrophosphate and burnt sugar, were prepared. Three different types of compositions comprising these ingredients, of different amount of each, were prepared, as listed in the following Table 1. % % % KCl 66.327 56.817 47.307 NaCl 30 40 50 IMP 0.075 0.064 0.053 GMP 0.225 0.184 0.153 Citric Acid 0.187 0.160 0.133 Disodium Pyrophosphate 2.892 2.480 2.063 Burnt Sugar 0.0030 0.0030 0.0030 A scheme illustrating the manner of preparation of the composition is shown in Fig. 1. The components of the system used in the preparation includes a screw-mixer 2 , a fluidized bed drier 4 , and a spin mixer 6. Wet KCl 8 is added into the screw-mixer 2 and then a concentrated water solution of IMP and GMP is sprayed onto the wet KCl at spraying stage 10. At next stage, a concentrated solution of citric acid or its salt is sprayed onto the mixture at stage 12 and finally a dry disodium pyrophosphate is added to the mixture at stage 18. The resulting perfectly mixed wet composition 16 is then fed into fluidized bed drier 4 and dried at about 125°C. The dried composition 18 is then fed into spin mixture 6 where a concentrated solution of burnt sugar 20 is sprayed onto the dry mixture and finally added is a dry NaCl mixture 22. The ensuing mixture 24 does not require any additional drying as the amount of water added with composition 16 is small. As an alternative, it is possible to feed burnt sugar also into the composition in screw-mixer 2. Example 2 Salt compositions of the invention comprising the same ingredients as in Example 1 but with the replacement of citric acid by tri-potassium citrate. Three different types of compositions differing from one another by the concentration of various ingredients were prepared, as listed in the following Table 2. % % % KCl 66.387 56.857 47.337 NaCl 30 40 50 IMP 0.136 0.117 0.097 GMP 0.136 0.117 0.097 Tri-Potassium Citrate 0.333 0.285 2.36 Disodium Pyrophosphate 2.72 2.33 1.94 Burnt Sugar 0.0030 0.0030 0.0030 The preparation procedure of the composition was as described above in Example 1. Example 3 Compositions with the same ingredients as in Examples 1 and 2 but with the citric acid and the tri-potassium citrate, respectively being replaced by tri-sodium citrate, were prepared. Similar as in Examples 1 and 2, three different types of compositions differing from one another by the concentration of the various ingredients were prepared, and this is in the following Table 3. % % % KCl 66.387 56.857 47.337 NaCl 30 40 50 IMP 0.136 0.117 0.097 GMP 0.136 0.117 0.097 Tri-Potassium Citrate 0.286 0.250 0.204 Disodium Pyrophosphate 2.762 2.366 1.972 Burnt Sugar 0.0030 0.0030 0.0030 The manner of the preparation of the composition was as described in Example 1. Example 4: A salt composition in accordance with the invention was prepared comprising KCl, NaCl, IMP, magnesium sulfate and burnt sugar. Three different compositions differing from one another by the concentrations of the various ingredients, were prepared as listed in the following Table 4. % % % KCl 68.917 49.027 49.137 NaCl 30 40 50 IMP 0.286 0.250 0.204 MgSO 4 • 7H 2 O 0.504 0.43 0.366 Burnt Sugar 0.0030 0.0030 0.0030 The preparation procedure was similar to that described in Example 1. Briefly, concentrated water solution of IMP and MgSO 4 was sprayed on a wet KCI mixture in a screw-mixture. Resulting mixed with composition was fed into a fluidized bed drier and dried at 125°C. The dried composition was then fed into a spin mixture where a concentrated solution of burnt sugar was sprayed thereon, and finally dry NaCl was added. Example 5 (not part of the invention) A composition comprising the following ingredients was prepared. KCl 71.1% NaCl 25% IMP 0.08% GMP 0.23% Citric Acid 0.2% Disodium Pyrophosphate 3.1% The manner of preparation was similar to that described in Example 1. Example 6 (not part of the invention) The salt composition comprising the following ingredients was prepared. KCl 71.13% NaCl 25% IMP 0.146% GMP 0.146% Tri-Potassium Citrate 0.357% Sodium Pyrophosphate 2.92% The manner of preparation was as described in Example 1. Example 7 (not part of the invention) The salt composition comprising the following ingredients was prepared. KCl 71.15% NaCl 25% IMP 0.146% GMP 0.146% Tri-Sodium Citrate 0.307% Disodium Pyrophosphate 2.96% The manner of preparation was as described in Example 1. Example 8 (not part of the invention) The salt composition comprising the following ingredients was prepared. KCl 73.86% NaCl 25% IMP 0.307% Magnesium sulfate 0.54% The manner of preparation was as described in Example 1. Example 9 The salt composition in accordance with the invention comprising the following ingredients was prepared. KCl 56.85% NaCl 40% IMP 0.117% GMP 0.117% Tri-Sodium Citrate 0.250% Disodium Pyrophosphate 2.366% Maltol 0.003% The manner of preparation was as described in Example 1. Example 10 The salt compositions of Examples 1 through 9 were subjected to a tasting assay in comparison to the following two salt mixtures: Mixture 1: 50% NaCl and 50% KCl Mixture 2: 25% NaCl and 75% KCl. Each of the inventive salt compositions as well as each of Mixtures 1 and 2 were dissolved in water (2% solution), and these solutions were then tasted by a panel of naive individuals. In all cases, the compositions of the invention were given a higher taste score to the above Mixtures 1 and 2. Examples 6-8 are not part of the invention.

Claims: A low sodium edible salt composition consisting of, based on dry weight of ingredient, 0-50% NaCI, 45-99.5% KCI and at least 0.5% additives, said additives consisting of maltol, at least one edible nucleotide monophosphate salt, and at least one member other than said nucleotide monophosphate salt selected from the group consisting of low organic acid, low organic acid salt, phophoric acid, phosphate salt and a magnesium salt. The composition of claim 1, wherein the nucleotide monophosphate is IMP or GMP. The composition of any of claims 1 or 2, wherein the organic acid is citric acid. The composition of any of claims 1 to 3, wherein the phosphate salt is sodium pyrophosphate. The composition of any of claims 1 to 4, comprising 45 - 75% KCI and 20 - 50% NaCI. The composition of any of claims 1 to 5, comprising 0.5 - 15% of said additive. The composition of claim 6, comprising 0.6 - 6.0% of said additive. A process for preparing the low-sodium edible salt composition of any of claims 1 to 7, comprising: (a) spraying a water solution of said additives, other than those with a low water solubility, on KCI crystals; (b) adding the low water soluble additives in a dry form; (c) drying the KCl crystals. The process of claim 8, wherein (d) dry NaCI and some additives are mixed and precoated by spraying the KCI crystals.

Inventors: BIALE DAVID, BRAVERMAN OLEG, GENIS MARGARITA, ZOLOTOV SHAUL, BIALE, DAVID, BRAVERMAN, OLEG, GENIS, MARGARITA, ZOLOTOV, SHAUL
Applicants: DEAD SEA WORKS LTD
Application year: 1997
Main classification: A23L1
IPC codes: A23L1