Schiff base quinone complexes and optical recording materials comprising the same

Abstract: Novel Schiff base quinone complexes are provided. They are useful as anti-fading agents and filter dyes. The anti-fading agents are applicable to heat developable photosensitive materials, silver halide photosensitive materials, and optical recording materials.

Description: This invention relates to novel Schiff base quinone complexes and their use as an anti-fading agent or dye. Prior Art Schiff base quinone complexes are described in Inorg. Chem., 28, 4379-4385 (1989), ibid., 14, 2724-2727 (1975), Can. J. Chem., 73, 1213-1222 (1995), J. Am. Chem. Soc., 110, 1827-1832 (1988), and ibid., 116, 1388-1394 (1994). The metal atoms used therein are Sn, Pb, Ni, Fe, Cd, Co, Zn, Mn, Mg, V, and Ti, many of which are deleterious to the environment. No reference is made to the utilization of these complexes as an anti-fading agent or dye. US-A 5 306 591 discloses a liquid developer comprised of (A) a liquid with a viscosity from about 0.5 to about 20 centipoise and a resistivity equal to or greater than 5 x 10 9 ; (B) thermoplastic resin particles with an average volume particle diameter from about 0.1 to about 30 microns; (C) a nonpolar liquid soluble ionic or zwitterionic charge director compound; and (D) a charge adjuvant comprised of an imine bisquinone metal complex, wherein the metal ion is selected from the group consisting of Ni (II), Zn (II), Co (II), Mg (II), Fe (II), Al (III) and Mn (IV). B.G. Maiya et al.: Journal of the Chemical Society Dalton Transactions, 1990, pages 3571-3576, XP-002068712 discloses the charge distribution in Schiff-base biquinone complexes, wherein the complexing metal ion is Co III , Ni II , Zn II , Cu II and Cd II with the N-(2'-hydroxy-3',5'-di-t-butylphenyl)-4,6-di-t-butyl-o-benzoquinone imine ligand system. SUMMARY OF THE INVENTION Therefore, an object of the present invention is to provide a novel Schiff base quinone complex, especially such a complex having coordinated a metal which is not pollutive to the environment. Another object of the present invention is to utilize the complex as an anti-fading agent and dye. The objects of the present invention are attained by Schiff base quinone complexes of the following general formula (1a). In formula (1a), each of R 1 and R 2 is an alkyl group, and M 1 is a metal atom selected from the class consisting of Ca, Ba, Y, La, Nd, Sm, Gd, Tb, Dy and Yb. DETAILED DESCRIPTION OF THE INVENTION The general formula (1a) is described in detail. The alkyl groups represented by R 1 and R 2 are preferably normal or branched alkyl groups in 1 to 20 carbon atoms, especially 1 to 12 carbon atoms, such as methyl, ethyl, n-butyl, t-butyl, t-pentyl, n-octyl, and t-octyl. More preferred are tertiary branched alkyl groups such as t-butyl, t-pentyl, and t-octyl. Their position of substitution is preferably the ortho- or para-position relative to the carbon atom adjoining the oxygen atom. M 1 is a metal atom Ca, Ba, Y, La, Nd, Sm, Gd, Tb, Dy or Yb. Ca and Ba are preferred. In one embodiment wherein the compound of the invention is used as an anti-fading agent, it is effective for preventing fading of many dyes including azo, azomethine, benzylidene, styryl, oxonol, cyanine, merocyanine, anthrachinone, and arylmethane dyes. The anti-fading agent is effective especially for cyanine dyes of the general formula (2a) and squarylium dyes of the general formula (3). First, the cyanine dyes of formula (2a) ar described. In formula (2a), each of Z 1 and Z 2 is a group of non-metallic atoms necessary to form a five or six-membered nitrogenous heterocyclic ring, which may be a fused one. Each of R 7 and R 8 is an alkyl, alkenyl or aralkyl group. L is a linkage having 3, 5, 7 or 9 methine groups connected through a conjugated double bond, letters a , b and c each are equal to 0 or 1, and X is an anion. Examples of the five or six-membered nitrogenous heterocyclic ring, which may be a fused one, represented by Z 1 and Z 2 include oxazole, isooxazole, benzoxazole, naphthoxazole, thiazole, benzothiazole, naphthothiazole, indolenine, benzindolenine, imidazole, benzimidazole, naphthoimidazole, imidazoquinoxaline, quinoline, pyridine, pyrrolopyridine, and furopyrrole rings. The five-membered nitrogenous heterocyclic rings having a benzene or naphthalene ring fused thereto are preferred, with the indolenine ring being most preferred. These rings may be substituted ones. Exemplary substituents include alkyl groups (e.g., methyl and ethyl), alkoxy groups (e.g., methoxy and ethoxy), phenoxy groups (e.g., unsubstituted phenoxy and p-chlorophenoxy), halogen atoms (e.g., Cl, Br, and F), alkoxycarbonyl groups (e.g., ethoxycarbonyl), cyano, nitro, and carboxyl groups. An unsubstituted indolenine ring and substituted indolenine rings having a chloro, methoxy or methyl substituent are especially preferred. The alkyl groups represented by R 7 and R 8 are preferably those of 1 to 20 carbon atoms, more preferably 1 to 8 carbon atoms, for example, methyl, ethyl, propyl, butyl, isobutyl, pentyl, and hexyl. They may have substituents, for example, halogen atoms such as F, Cl, and Br, alkoxycarbonyl groups such as methoxycarbonyl and ethoxycarbonyl, and hydroxyl. The aralkyl groups represented by R 7 and R 8 are preferably those of 7 to 12 carbon atoms, for example, benzyl andphenylethyl and may have substituents such as methyl, alkoxy and chloro. The alkenyl groups represented by R 7 and R 8 are preferably those of 2 to 6 carbon atoms, for example, 2-pentenyl, vinyl, allyl, 2-butenyl, and 1-propenyl. In formula (2a), L is a linkage having 3, 5, 7 or 9 methine groups connected through a double bond in a conjugated fashion. The number of methine groups is preferably seven (heptamethine compounds). The methine group may have a substituent although it is preferred that the substituted methine group be a methine group substituted at the center or meso-position. Preferred among the methine groups represented by L are trimethines of the following formula L3, pentamethines of the following formula L5, heptamethines of the following formula L7, and nonamethines of the following formula L9. In the formulae, R 10 is a hydrogen atom, alkyl group, halogen atom, aryl group, NR 16 R 17 , SR 18 or OR 19 wherein each of R 16 , R 17 , and R 18 is an alkyl or aryl group. R 16 and R 17 , taken together, may form a heterocyclic ring such as piperidine and morpholine. R 9 and R 11 are hydrogen atoms or groups of atoms necessary to form a five or six-membered ring, taken together. Each of R 19 and R 20 is a hydrogen atom or alkyl group. Preferably, R 9 and R 11 , taken together, form a five or six-membered ring, for example, cyclopentene and cyclohexene rings. These rings may have substituents such as alkyl and aryl groups. In conjunction with R 9 , R 10 , R 11 , R 19 , and R 20 , the alkyl groups are the same as defined for R 7 and R 8 . The halogen atoms are F, Cl, and Br. The aryl groups are preferably those of 6 to 12 carbon atoms, for example, phenyl and naphthyl groups. The aryl groups may be either substituted or unsubstituted. Where substituted, exemplary substituents include alkyl groups having up to 10 carbon atoms, preferably up to 6 carbon atoms such as methyl, ethyl, butyl and hexyl, alkoxy groups having up to 10 carbon atoms, preferably up to 6 carbon atoms such as methoxy and ethoxy, aryloxy groups having up to 20 carbon atoms, preferably up to 12 carbon atoms such as phenoxy and p-chlorophenoxy, halogen atoms such as Cl, Br, and F, and alkoxycarbonyl groups having up to 10 carbon atoms, preferably up to 6 carbon atoms such as ethoxycarbonyl as well as cyano, nitro and carboxyl groups. In formula (2a), letters a , b , and c are equal to 0 or 1. Preferably both a and b are equal to 0 while c is generally equal to 1. It is understood that c is equal to 0 where an anionic substituent such as carboxyl forms an intramolecular salt with N + . The anions represented by X include halide ions such as Cl, Br and I, p-toluenesulfonate ion, ethylsulfate ion, PF 6 - , BF 4 - , and ClO 4 - . Cyanine dyes of the general formula (2b) are more preferred. In the formula, each of Z 3 and Z 4 is a group of atoms necessary to form a benzo or naphtho fused ring. Each of R 7 and R 8 is an alkyl, aralkyl or alkenyl group. Each of R 9 and R 11 is a hydrogen atom or a group of atoms necessary form a five or six-membered ring, taken together. R 10 is a hydrogen atom, alkyl group, halogen atom, aryl group, NR 16 R 17 , SR 18 or OR 18 wherein each of R 16 , R 17 , and R 18 is an alkyl or aryl group. R 16 and R 17 , taken together, may form a five or six-membered ring. Each of R 12 , R 13 , R 14 , and R 15 is an alkyl group. Alternatively, R 12 and R 13 , and R 14 and R 15 , taken together, may form a ring. X is anion. Letter c is equal to 0 or 1. In formula (2b), the benzo or naphtho fused ring formed by Z 3 and Z 4 may have a substituent as mentioned for Z 1 . The alkyl groups represented by R 7 , R 8 , R 12 , R 13 , R 14 , R 15 , R 16 , R 17 , and R 18 are as defined for R 7 in formula (2a). R 12 and R 13 , and R 14 and R 15 , taken together, may form a ring such as cyclohexane. The alkenyl and aralkyl groups represented by R 7 and R 8 are the same as the alkenyl and aralkyl groups represented by R 7 and R 8 in formula (2a). The aryl groups represented by R 10 , R 16 , R 17 , and R 18 are the same as the aryl groups represented by R 10 in formula (L5). The halogen atoms represented by R 10 are the same as the halogen atoms represented by R 10 in formula (L5). The ring formed by R 9 and R 11 is the same as the ring formed by R 9 and R 11 in formula (L7) . The ring formed by R 16 and R 17 is the same as the ring formed by R 16 and R 17 in formula (L7). X is the same as X in formula (2a). Letter c is the same as c in formula (2a). Most preferred cyanine dyes are those of formula (2b) wherein each of R 7 and R 8 is an unsubstituted alkyl group, each of R 12 , R 13 , R 14 , and R 15 is a methyl group, R 9 and R 11 , taken together, form a cyclopentene ring, and R 10 is a diphenylamino group. The anti-fading agent of the invention is also effective for squarylium dyes of the following general formula (3): wherein each of R 21 , R 22 , R 23 , R 24 , R 25 , R 26 , R 27 , and R 28 is a hydrogen atom, alkyl, cycloalkyl, aryl or aralkyl group. Alternatively, R 21 and R 22 , R 23 and R 24 , R 25 and R 26 , R 27 and R 28 , R 22 and R 23 , and R 26 and R 27 , taken together, may form a five or six-membered ring. In formula (3), the alkyl and aralkyl groups represented by R 21 to R 28 are the same as the alkyl and aralkyl groups represented by R 7 in formula (2a). The cycloalkyl group represented by R 21 to R 28 includes cyclopentyl and cyclohexyl. The aryl group represented by R 21 to R 28 is the same as the aryl group represented by R 10 in formula (L5). Examples of the compound of formula (1a) according to the invention are given below as well as examples of the cyanine dye of formula (2a), and the squarylium dyes of formula (3). Compound M Compound M 1-9 Ca 1-12 Y 1-10 Ba 1-14 La 1-15 Nd 1-16 Sm 1-17 Gd 1-18 Tb 1-19 Dy 1-20 Yb Compound R R' 1-21 t-C 8 H 17 CH 3 1-24 t-C 5 H 11 t-C 5 H 11 1-25 t-C 8 H 17 t-C 8 H 17 Compound R R' 2 - 1 -CH 3 -H 2 - 2 -C 4 H 9 5 - Cl 2 - 3 -C 6 H 13 5 - OCH 3 2 - 4 -C 3 H 7 5 -CN 2 - 5 -CH 3 5-CO 2 C 2 H 5 2 - 6 " 5 - NO 2 2 - 7 " 5 - CH 3 2 - 8 " 5,6-di-Cl 2 - 9 " 4,6-di-Cl 2 - 10 -C 2 H 5 5 - Cl Under the reading "R'", the preceding number represents the substituting position Compound X 2-32 O 2-33 S 2-34 N-CH 3 Compound 2-41 same as 2-40 wherein n=1 The coumpounds of general formula (1a) can be obtained by adding metal salt and ammonia to a solution containing a catechol derivative of the following general formula (4) as will be described in Example. In formula (4), R 30 is an alkyl group. Letter n is an integer of 2. The catechol derivative is dissolved in a solvent, preferably an organic solvent, for example, methyl alcohol and ethyl alcohol. Examples of the metal salt used herein include salts of divalent metals such as CaCl 2 and BaCl 2 . The ammonia used herein is liquid ammonia or aqueous ammonia, with aqueous ammonia being preferred. The metal salt is used in an amount of 0.2 to 0.3 mol, preferably 0.23 to 0.27 mol and ammonia is used in an amount of 3 to 20 mol, preferably 12 to 17 mol per mol of the catechol. Synthesis may be carried out at a temperature of 10 to 40°C, preferably 20 to 25°C and accelerated by blowing oxygen or air into the reaction solution. The compounds of the invention are also useful as a dye which will find photographic anti-halation, medical diagnosis, filter, ink, and paint applications. Use of the inventive compounds as a dye in filter, ink, and paint applications is preferred. When it is desired to use the inventive compounds in filter, ink, and paint applications, reference is made to Japanese Patent Application Kokai (JP-A) 69686/1989 and 1762/1983. Because of their absorption in the infrared region, the inventive compounds are useful as infrared filters or infrared absorbing ink or paint, which will find use in an invisible bar code system, for example. Also, the inventive compounds can be used as an anti-fading agent in heat developable photosensitive materials, silver halide photosensitive materials, optical recording materials, pressure and heat sensitive materials, medical diagnostic materials, ink, and paint. Preferably they are used as an anti-fading agent in heat developable photosensitive materials, silver halide photosensitive materials, optical recording materials, ink, and paint. In the embodiment wherein the inventive compound is used as an anti-fading agent for a dye, the dye and the anti-fading agent are preferably mixed in a weight ratio between 1:0.1 and 1:20, more preferably between 1:0.2 and 1:10, most preferably between 1:0.5 and 1:3. In heat developable photosensitive material having a photosensitive layer on a support, the anti-fading agent may be added to a dye layer on the same side as the photosensitive layer close to the support and a dye layer remote from the photosensitive layer. The anti-fading agent may be added in an amount of 0.1 to 1,000 mg/m 2 , preferably 1 to 200 mg/m 2 although the amount varies with a particular purpose. Preferably the anti-fading agent is added as a solution in organic solvent. The dye may be added in an amount of 0.1 to 1,000 mg/m 2 , preferably 1 to 200 mg/m 2 in the same layer as the anti-fading agent. Where a binder is used, the dye may be added in an amount of 0.1 to 60% by weight, preferably 0.2 to 30% by weight, more preferably 0.5 to 10% by weight of the binder. For environmental protection, heat developable photosensitive material is preferably of the type wherein the dye is substantially left on an image sheet to be viewed. More preferred is heat developable photosensitive material of the mono-sheet type wherein all the materials provided for image formation constitute an image sheet to be viewed. For a particular purpose, heat developable photosensitive material adapted for infrared laser exposure is preferred. It is preferred that the infrared laser have a wavelength of at least 750 nm, especially at least 800 nm. The heat developable photosensitive material according to the invention is to form a photographic image through heat development process. Such heat developable photosensitive materials are disclosed in USP 3,152,904 and 3,457,075 and D. Morgan and B. Shely, "Thermally Processed Silver Systems" in Imaging Processes and Materials, Neblette, 8-th Ed., Sturge, V. Walworth and A. Shepp Ed., page 2, 1969. Although the heat developable photosensitive material according to the invention is only required to form a photographic image through heat development process, it preferably contains a reducible silver source (e.g., organic silver salt), a catalytic amount of photocatalyst (e.g., silver halide), atoning agent for controlling the tone of silver, and a reducing agent as dispersed in an organic binder matrix. The heat developable photosensitive material is stable at room temperature and it is developed after exposure by heating at elevated temperatures, for example, 80°C or higher. Upon heating, redox reaction takes place between the reducible silver source (functioning as an oxidizing agent) and the reducing agent to form silver. The latent image generated by exposure provides catalysis to promote this redox reaction. Reaction of the organic silver salt in the exposed areas generates silver which provides a black image in contrast to the unexposed areas. An image is formed in this way. The heat developable photosensitive material according to the invention has at least one photosensitive layer on a support. It is acceptable that only a photosensitive layer is formed on a support although it is preferred to form at least one non-photosensitive layer on the photosensitive layer. In order to control the quantity or wavelength distribution of light transmitted by the photosensitive layer, a filter layer may be formed on the same or opposite side with respect to the photosensitive layer. The photosensitive layer may contain a dye of formula (2a), (2b) or (3) as well as another dye or pigment. The photosensitive layer may be divided into plural layers while a combination of high sensitivity layer/low sensitivity layer or low sensitivity layer/high sensitivity layer is employable for gradation adjustment. Various additives may be added to any of the photosensitive layer, non-sensitive layer, and other layers. Various supports are employable in the heat developable photosensitive material according to the invention. Exemplary supports are paper, polyethylene-coated paper, polypropylene-coated paper, parchment, and fabric; sheets or films of metals such as aluminum, copper, magnesium, and zinc; glass and glass coated with metals such as chromium alloy, steel, silver, gold and platinum; and synthetic polymers, for example, poly(alkyl methacrylates) such as poly(methyl methacrylate), polyesters such as poly(ethylene terephthalate, polyvinylacetals, polyamides such as nylon, and cellulose esters such as cellulose nitrate, cellulose acetate, cellulose acetate propionate, and cellulose acetate butyrate. In the heat developable photosensitive material according to the invention, there may be used surfactants, antioxidants, stabilizers, plasticizers, UV absorbers, coating aids, and the like. Binder layers, for example, of a synthetic polymer may form self-sustaining films with respective chemicals to be contained in the heat developable photosensitive material according to the invention. The support may be subordinately coated with well-known subordinate materials, for example, vinylidene chloride, acrylic acid monomers such as acrylonitrile and methyl acrylate, unsaturated dicarboxylic acids such as itaconic acid and acrylic acid, carboxymethyl cellulose, copolymers and terpolymers of poly(acrylamide), and analogous polymeric materials. Preferred binders are transparent or translucent and generally colorless, and include natural polymers, synthetic resins, polymers and copolymers, and other film-forming media, for example, gelatin, gum arabic, poly(vinyl alcohol), hydroxyethyl cellulose, cellulose acetate, cellulose acetate butyrate, poly(vinylpyrrolidone), casein, starch, poly(acrylic acid), poly(methyl methacrylate), polyvinyl chloride, poly(methacrylic acid), styrene-maleic anhydride copolymers, styrene-acrylonitrile copolymers, styrene-butadiene copolymers, poly(vinyl acetals) (e.g., polyvinyl formal and polyvinyl butyral), polyesters, polyurethanes, phenoxy resins, poly(vinylidene chloride), polyepoxides, polycarbonates, poly(vinyl acetate), cellulose esters, and polyamides. A coating of binder may be formed from a solution or emulsion thereof in water or organic solvent. Addition of color toning agents is quite desirable. Examples of the color toning agent are disclosed in Research Disclosure No. 17029 and include imides such as phthalimide; cyclic imides, pyrazolin-5-ones and quinazolines such as succinimide, 3-phenyl-2-pyrazolin-5-one, 1-phenylurazole, quinazoline, and 2,4-thiazolidinedione; naphthalimides such as N-hydroxy-1,8-naphthalimide; cobalt complexes such as cobalt hexaminetrifluoroacetate; mercaptans such as 3-mercapto-1,2,4-triazole; N-(aminomethyl)aryldicarboxyimides such as N-(dimethylaminomethyl)phthalimide; combinations of a blocked pyrazole, isothiuronium derivative, and optical bleaching agent such as a combination of N,N'-hexamethylene(l-carbamoyl-3,5-dimethylpyrazole), 1,8-(3,6-dioxaoctane)bis-(isothiuroniumtrifluoroacetate), and 2-(tribromomethylsulfonyl)benzothiazole); merocyanine dyes such as 3-ethyl-5-((3-ethyl-2-benzothiazolinylidene)-1-methylethylidene)-2-thio-2,4-oxazolidinedione; phthalazinone, phthalazinone derivatives and metals salts of such derivatives such as 4-(1-naphthyl)phthalazinone, 6-chlorophthalazinone, 5,7-dimethyloxyphthalazinone, and 2,3-dihydro-1,4-phthalazinedione; combinations of phthalazinone with a sulfinic acid derivative such as 6-chlorophthalazinone plus sodium benzenesulfinate and 8-methylphthalazinone plus sodium p-trisulfonate; a combination of phthalazine and phthalic acid; combination of phthalazine (inclusive of phthalazine addition products) with at least one of maleic anhydride, phthalic acid, 2,3-naphthalenedicarboxylic acid or o-phenylenic acid derivative and anhydrides thereof (e.g., phthalic acid, 4-methylphthalic acid, 4-nitrophthalic acid, and tetrachlorophthalic anhydride); quinazolinediones, benzoxadine, naphthoxazine derivatives; benzoxadine-2,4-diones such as 1,3-benzoxadine-2,4-dione; pyrimidines and asymmetric triazines such as 2,4-dihydroxypyrimidine, and tetraazapentalene derivatives such as 3,6-dimercapto-1,4diphenyl-1H,4H-2,3a,5,6a-tetraazapentalene. The preferred color toning agent is phthalazine of the following formula. As the reducing agent, so-called photographic developing agents, for example, 1-phenyl-3-pyrazolidone (available as Phenidone®), hydroquinones, and catechols may be contained although hindered phenols are preferred. Also contemplated herein are color photosensitive materials as disclosed in USP 4,460,681. Preferred examples of the reducing agent are disclosed in USP 3,770,448, 3,773,512, and 3,593,863 and Research Disclosure Nos. 17029 and 29963. Examples include aminohydroxycycloalkenones such as 2-hydroxy-piperidino-2-cyclohexenone; amino reductone esters as a precursor of developing agent such as piperidinohexose reductone monoacetate; N-hydroxyurea derivatives such as N-p-methylphenyl-N-hydroxyurea; aldehyde or ketone hydrazones such as anthracenealdehydephenylhydrazone; phosphamidophenols; phosphamidoanilines; polyhydroxybenzenes such as hydroquinone, t-butylhydroquinone, isopropylhydroquinone, and (2,5-dihydroxyphenyl)methylsulfone; sulfohydroxamic acids such as benzenesulfohydroxamic acid; sulfonamidoanilines such as 4-(N-methanesulfonamido)aniline; 2-tetrazolylthiohydroquinones such as 2-methyl-5-(1-phenyl-5-tetrazolylthio)hydroquinone; tetrahydroquinoxalines such as 1,2,3,4-tetrahydroquinoxaline; amidoxines; azines such as combinations of an aliphatic carboxylic acid aryl hydrazide with ascorbic acid; a combination of polyhydroxybenzene with hydroxylamine; reductones and/or hydrazines; hydroxamic acids; combinations of an azine with a sulfonamidophenol; α-cyanophenylacetic acid derivatives; combinations of bis-β-naphthol with a 1,3-dihydroxybenzene derivative; 5-pyrazolones; sulfonamidophenol reducing agents; 2-phenylindane-1,3-dione; chroman; 1,4-dihydropiridines such as 2,6-dimethoxy-3,5-dicarboethoxy-1,4-dihydropyridine; bisphenols such as bis(2-hydroxy-3-t-butyl-5-methylphenyl)methane, bis(6-hydroxy-m-tri)mesitol, 2,2-bis(4-hydroxy-3-methylphenyl)propane, 4,4-ethylidene-bis(2-t-butyl-6-methyl)phenol, UV-sensitive ascorbic acid derivatives, and 3-pyrazolidones. Preferred developing agents are hindered phenols of the following general formula (A): wherein R 40 is a hydrogen atom or an alkyl group having 1 to 10 carbon atoms such as -C 4 H 9 and 2,4,4-trimethylpentyl; R 41 and R 42 each are an alkyl group having 1 to 5 carbon atoms such as methyl, ethyl, and t-butyl. The silver halide useful as a catalytic amount of photocatalyst may be any of photosensitive silver halides such as silver bromide, silver iodide, silver chloride, silver chlorobromide, silver iodobromide, and silver chloroiodobromide although inclusion of an iodide ion is preferred. The silver halide may be added to the image-forming layer by any desired method insofar as the silver halide is disposed close to the reducible silver source. In general, the silver halide is contained in an amount of 0.75 to 30% by weight of the reducible silver source. The silver halide may be prepared by conversion of a silver soap moiety by reaction with a halide ion or preformed and added during generation of a soap. A combination of these techniques is possible and rather preferred. Any desired material containing a reducible silver ion source may be used as the reducible silver source. Preferred are silver salts of organic acids and hetero-organic acids, especially long-chain aliphatic carboxylic acids (of 10 to 30, preferably 15 to 25 carbon atoms). Also useful are organic or inorganic silver salt complexes wherein the ligand has an overall stability constant of 4.0 to 10.0 relative to silver ion. Preferred examples of the silver salt are described in Research Disclosure Nos. 17029 and 29963 and include salts of organic acids such as gallic acid, oxalic acid, behenic acid, stearic acid, palmitic acid, and lauric acid; silver salts of carboxyalkylthioureas such as 1-(3-carboxypropyl)thiourea and 1- (3-carboxypropyl)-3,3-dimethylthiourea; silver complexes of polymeric reaction products of an aldehyde with a hydroxy-substituted aromatic carboxylic acid (examples of the aldehyde are formaldehyde, acetaldehyde, and butylaldehyde, and examples of the hydroxy-substituted acid are salicylic acid, benzoic acid, 3,5-dihydroxybenzoic acid, and 5,5-thiodisalicylic acid); silver salts or complexes of thioenes such as 3-(2-carboxyethyl)-4-hydroxymethyl-4-thiazoline-2-thioene and 3-carboxymethyl-4-thiazoline-2-thioene; complexes or salts of silver with nitrogenous acids such as imidazole, pyrazole, urazole, 1,2,4-thiazole, 1H-tetrazole, 3-amino-5-benzylthio-1,2,4-triazole, and benzotriazole; silver salts of saccharin, 5-chlorosalicylaldoxime, etc.; and silver salts of mercaptides. The preferred silver source is silver behenate. The reducible silver source is preferably used in an amount of up to 3 g/m 2 of silver, more preferably up to 2 g/m 2 of silver. An antifoggant may be contained in the photosensitive material according to the invention. The most effective antifoggant was mercury ion. Use of a mercury compound as the antifoggant in photosensitive material is disclosed, for example, in USP 3,589,903. Mercury compounds, however, are undesirable from the environmental aspect. Preferred in this regard are non-mercury antifoggants as disclosed, for example, in USP 4,546,075 and 4,452,885 and JP-A 57234/1984. Especially preferred non-mercury antifoggants are compounds as disclosed in USP 3,874,946 and 4,756,999 and heterocyclic compounds having at least one substituent represented by -C(X 1 ) (X 2 ) (X 3 ) wherein X 1 and X 2 are halogen atoms such as F, Cl, Br, and I, and X 3 is hydrogen or halogen. Preferred examples of the antifoggant are shown below. More preferred antifoggants are disclosed in USP 5, 028, 523, British Patent Application Nos. 92221383.4, 9300147.7 and 9311790.1 by the same assignee as the present invention. In the heat developable photosensitive material according to the invention, there may be used sensitizing dyes as disclosed in JP-A 159841/1988, 140335/1985, 231437/1988, 259651/1988, 304242/1988, and 15245/1988, USP 4,639,414, 4,740,455, 4,741,966, 4,751,175, and 4,835,096. The inventive compounds are also applicable to silver halide photosensitive material. With respect to couplers, spectral sensitizers, silver halide emulsions, development promoters, UV absorbers, dyes, hardeners, anti-color mixing agents, surfactants, and other components used in the silver halide photosensitive material, reference is made to JP-A 261350/1995. The inventive compounds are also applicable to optical recording materials. In this regard, reference is made to JP-A 84383/1990 and 171891/1989. EXAMPLE Examples of the present invention are given below by way of illustration and not by way of limitation. Example 1 Synthesis of compound 1-9 To a solution of 26.7 grams of 3,5-di-t-butylcatechol in 1500 ml of ethyl alcohol were added 250 ml of an aqueous solution containing 3.2 grams of calcium chloride and 125 ml of 25% aqueous ammonia. Air was blown into the reaction solution for 3 hours. The precipitated crystal was then collected by filtration and recrystallized from chloroform, yielding 18 grams of compound 1-9. m.p.: 262-265°C λmax: 743.4 nm (CH 2 Cl 2 ) ε: 3.47x10 4 Elemental analysis: Calcd. Found (2 times) C 75.96% 75.65% 74.77% H 9.11 9.30 9.05 N 3.16 3.09 3.04 Synthesis of compound 1-10 To a solution of 5.3 grams of 3,5-di-t-butylcatechol in 300 ml of ethyl alcohol were added 50 ml of an aqueous solution containing 1.4 grams of barium chloride dihydrate and 25 ml of 25% aqueous ammonia. The reaction solution was agitated at room temperature for 5 hours. The precipitated crystal was then collected by filtration and recrystallized from chloroform and methyl alcohol, yielding 3 grams of compound 1-10. m.p.: 212-217°C or higher λmax: 748.4 nm (CH 2 Cl 2 ) ε = 2.36 · 10 4 Elemental analysis: Calcd. Found (2 times) C 68.46% 68.10% 68.22% H 8.21 8.30 8.12 N 2.85 2.80 2.78 Other compounds could be similarly synthesized. Table 1 shows the melting point and spectral data of compounds synthesized under similar conditions. The spectral data indicate peaks in ultraviolet to infrared regions as measured in dichloromethane. Values of elemental analysis were well coincident with the calculated values. Compound λmax 1 λmax 2 λmax 3 λmax 4 λmax 5 λmax 6 λmax 7 m.p. (lower row shows ε x10 -4 , M -1 cm -1 ) 1-9 262-265 743 441 342 3.47 0.63 0.90 1-10 212-217 783 541 449 338 2.36 0.81 0.70 0.85 1-12 >300 820 743 532 444 380 4.30 4.66 0.79 1.13 1.31 1-14 >300 820 766 536 448 392 338 4.67 4.70 0.68 0.91 0.73 1.27 1-15 >300 822 760 536 448 392 336 4.62 4.71 0.72 0.91 0.78 1.27 1-16 >300 820 756 540 444 390 334 4.68 4.86 0.75 1.05 0.81 1.31 1-17 >300 820 750 536 444 388 334 4.78 5.06 0.80 1.13 0.87 1.41 1-18 >300 820 750 530 444 384 332 3.91 4.19 0.70 1.03 0.74 1.16 1-19 >300 820 748 532 442 380 334 4.39 4.70 0.77 1.11 0.87 1.29 1-20 >300 820 744 536 442 380 334 4.51 4.85 0.86 1.24 0.94 1.39 Example 2 (Filter use) Sample (001) was prepared by coating layers of the following compositions to a triacetyl cellulose film support having an undercoat layer. (1) Filter layer Compound 1-9 0.2 g/m 2 Tricresyl phosphate 1.0 g/m 2 Gelatin 3.8 g/m 2 (2) Protective layer Sodium 2,4-dichloro-6-hydroxy-s-triazine 0.1 g/m 2 Gelatin 1.8 g/m 2 Samples (002) to (005) were similarly prepared except that compound 1-9 in sample (001) was replaced by an equimolar amount of other inventive compounds or a comparative compound. Each sample was divided into two sections. One section was allowed to stand at 60°C and RH 70% for 10 days. The other section was exposed to a fluorescent lamp of 20,000 lux for 5 days. After the fade tests, the sections were measured for a residual dye concentration. A percent retention of the dye was calculated as the residual dye concentration divided by the initial dye concentration. The results are shown in Table 2. Sample No. Compound Dye retention after hot, humid fading test Dye retention after light exposure fading test Remarks 001 1-9 99% 98% Invention 002 1-10 98% 97% Invention 005 compound (a) 60% 20% Comparison It is evident that the inventive compounds are stable. The calcium and barium complexes are favorable from the environmental aspect since they are less toxic. Example 3 (Heat developable photosensitive material) Preparation of photosensitive emulsion A Solution (1) Stearic acid 131 g Behenic acid 635 g Distilled water mixing at 85°C for 15 minutes 13 liters Solution (2) NaOH 89 g Distilled water 1500 ml Solution (3) Conc. HNO 3 19 ml Distilled water 50 ml Solution (4) AgNO 3 365 g Distilled water 2500 ml Solution (5) Polyvinyl butyral 86 g Ethyl acetate 4300 ml Solution (6) Polyvinyl butyral 290 g Isopropanol 3580 ml Solution (7) N-bromosuccinimide 9.7 g Acetone 690 ml With vigorous stirring, solution (2) was added over 5 minutes to solution (1) kept at 85°C, and solution (3) was then added over 25 minutes. Stirring was continued for a further 20 minutes and then the temperature was lowered to 35°C. With more vigorous stirring at 35°C, solution (4) was added over 5 minutes, and stirring was continued for a further 90 minutes. Then solution (5) was added, stirring was interrupted, and the reaction solution was allowed to stand. The aqueous phase was removed together with the salts contained therein, collecting an oil phase. The solvent was removed from the oil phase and a trace of water was removed. Solution (6) was added to the residue, which was vigorously stirred at 50°C. Solution (7) was added over 20 minutes. Stirring for a further 105 minutes yielded emulsion A. On a polyethylene terephthalate support tinted blue with dye-A, the following layers were successively formed. Each coating step was followed by drying at 75°C for 5 minutes. Back surface side coating Anti-halation layer (wet thickness 80 microns) 1:1 mixture of polyvinyl butyral (10% isopropanol solution) and cellulose acetate butyrate (10% isopropanol solution) 150 ml Dye (DMF, acetone or methyl chloride was used as solvent) 42 mg Anti-fading agent (ethyl acetate or methyl chloride was used as solvent) 45 mg Photosensitive layer side coating Photosensitive layer (wet thickness 140 microns) Photosensitive emulsion A 73 g Sensitizing dye-1 (0.1% DMF solution) 2 ml Antifoggant-1 (0.01% methanol solution) 3 ml Antifoggant-2 (0.85% methanol solution) 10 ml Antifoggant-3 (0.85% methanol solution) 10 ml Phthalazone (4.5% DMF solution) 8 ml Reducing agent-1 (10% acetone solution) 13 ml Surface protective layer (wet thickness 100 microns) Acetone 175 ml 2-propanol 40 ml Methanol 15 ml Cellulose acetate 8.0 g Phthalazine 1.0 g 4-methylphthalic acid 0.72 g Tetrachlorophthalic acid 0.22 g Tetrachlorophthalic anhydride 0.5 g Various agents used herein are as identified below. Sensitometry The thus prepared heat developable photosensitive material was cut into sections of folio size and exposed to a beam of 830 nm emitted from a laser diode at an angle of 13° with respect to a normal plane. Using a heat drum, heat development was then carried out at 120°C for 5 seconds. Sharpness The photosensitive material sample was exposed to light of 830 nm spectrally selected from white light of 2856 K through an interference filter, processed under the above-mentioned conditions, and rated for sharpness in terms of an MTF value at 15 lines/mm at an optical density of 1.0. Color rating The photosensitive material sample was heat developed without exposure. It was visually observed and rated "O" for good, "Δ" for noticeable color, and "X" for poor color. Light-fastness rating Using a xenon lamp illuminating equipment (lamp: Xenon Burner Warranty Log Wattage 3500/6500 type) by Atlas Electric Device, the photosensitive material sample on the backcoating side was subject to a lighting cycle of lighting (8500 1x/30°C/30% RH/3.8 hours) and turning off (20°C/90% RH/1 hour) 5 rounds for a total time of 24 hours. A percent retention of the dye was determined from a change of absorption spectrum. No. Dye Anti-fading agent Color Sharpness MTF Retention (%) 101 - - O 0.56 - 102 2-7 - O 0.92 12 105 2-7 1-9 O 0.94 70 106 2-7 1-10 O 0.92 54 107 2-10 - O 0.93 10 108 2-10 1-9 O 0.93 71 109 2-10 1-10 O 0.94 57 It is evident from Table 3 that samples within the scope of the invention had high sharpness and light fastness and were free of a residual color problem. Example 4 Preparation of photosensitive emulsion B Solution (1) Stearic acid 131 g Behenic acid 635 g Distilled water mixing at 85°C for 15 minutes 13 liters Solution (A) Previously prepared cubic AgBrI (I = 4 mol%: 0.06 µ) (0.22 mol Ag) Distilled water 1250 ml Solution (2) NaOH 89 g Distilled water 1500 ml Solution (3) Conc. HNO 3 19 ml Distilled water 50 ml Solution (4) AgNO 3 365 g Distilled water 2500 ml Solution (5) Polyvinyl butyral 86 g Ethyl acetate 4300 ml Solution (6) Polyvinyl butyral 290 g Isopropanol 3580 ml With vigorous stirring, solution (A) was added over 10 minutes to solution (1) kept at 85°C, solution (2) was successively added over 5 minutes, and solution (3) was then added over 25 minutes. Stirring was continued for a further 20 minutes and then the temperature was lowered to 35°C. With more vigorous stirring at 35°C, solution (4) was added over 5 minutes, and stirring was continued for a further 90 minutes. Then solution (5) was added, stirring was interrupted, and the reaction solution was allowed to stand. The aqueous phase was removed together with the salts contained therein, collecting an oil phase. The solvent was removed from the oil phase and a trace of water was removed. Solution (6) was added to the residue, which was vigorously stirred at 50°C. Stirring for a further 105 minutes yielded emulsion B. Samples were prepared as in Example 3 except that an anti-halation layer was provided under the photosensitive layer on the photosensitive layer side. They were tested as in Example 3. Samples using anti-fading agents within the scope of the invention had high sharpness and light fastness and were free of a residual color problem. Example 5 An emulsified dispersion was prepared by weighing 9.8 g of cyan coupler (C-1), adding 11.5 g of high-boiling organic solvent tricresyl phosphate thereto, adding 24 ml of ethyl acetate thereto to form a solution, and emulsifying and dispersing the solution in 200 g of a 10 wt% gelatin aqueous solution containing 1.5 g of sodium dodecylbenzenesulfonate. The emulsified dispersion was entirely added to 247 g of a high silver chloride emulsion (silver 70.0 g/kg emulsion, silver bromide content 0.5 mol%). On a triacetate film base having an undercoat layer previously applied at a silver coverage of 1.73 g/m 2 , the emulsion was coated. On this coating, a gelatin layer was formed as a protective layer to a dry thickness of 1.0 µm, obtaining sample No. 201. The gelatin hardener used herein was sodium salt of 1-oxy-3,5-dichloro-sec-triazine. Sample Nos. 204 to 205 were prepared by the same procedure as sample No. 201 except that during preparation of the emulsified dispersion, an anti-fading agent as shown in Table 4 was added for co-emulsification in an amount of 100 mol% based on the coupler. The thus obtained samples were wedge exposed and developed in accordance with the following steps. Step Temperature Time Color development 35°C 45 sec. Bleach fixing 30-35°C 45 sec. Rinse (1) 30-35°C 20 sec. Rinse (2) 30-35°C 20 sec. Rinse (3) 30-35°C 20 sec. Drying 70-80°C 60 sec. The processing solutions used in these steps are shown below. Color developer Water 800 ml Ethylenediamine-N,N,N',N'-tetramethylenesulfonic acid 1,5 g Potassium bromide 0,015 g Triethanolamine 8,0 g Sodium chloride 1,4 g Potassium carbonate 25 g N-ethyl-N-(β-methanesulfonamidoethyl)-3-methyl-4-aminoaniline hydrogen sulfate 5,0 g Disodium N,N-bis(sulfonatoethyl)hydroxylamine 5,5 g Brightening agent (WHITEX 4B, Sumitomo Chemicals K.K.) 1,0 g Water totaling to 1000 ml pH (25°C) 10,05 Bleach fixer Water 400 ml Ammonium thiosulfate (700 g/liter) 100 ml Sodium sulfite 17 g Iron (III) ethylenediaminetetraacetate ammonium 55 g Disodium iron ethylenediaminetetraacetate 5 g Ammonium bromide 40 g Water totalling to 1000 ml pH (25°C) 6,0 Rinse solution Deionized water containing less than 3 ppm of calcium and magnesium. Sample Nos. 201 to 205 in which dye images were formed in this way wer exposed to light for 8 days by means of a xenon tester (illuminance 200,000 lux) equipped with a UV absorbing filter for cutting off light of 400 nm or less (manufactured by Fuji Photo-Film Co., Ltd.). For each sample, a percent retention of density was determined provided that the initial density was 1.0. Measurement was done by means of an automatic recording densitometer manufactured by Fuji Photo-Film Co., Ltd. The results are shown in Table 4. Sample Anti-fading agent Retention Remarks 201 - 45% Comparison 204 1-9 90% Invention 205 1-10 91% Invention Additionally, samples were prepared in accordance with Examples 1, 2 and 5 of JP-A 261350/1995 and similarly tested to find that the anti-fading agents within the scope of the invention were fully effective. Example 6 A dye layer-coating solution was prepared by dissolving 2.0 g of cyanine dye (CY-1) in 100 cc of 2,2,3,3-tetrafluoropropanol (structural formula: HCF 2 CF 2 CH 2 OH). On a disc-shaped polycarbonate substrate having a tracking guide (outer diameter 120 mm, inner diameter 15 mm, thickness 1.2 mm, track pitch 1.6 µm, groove width 0.5 µm, groove depth 900 Å), the coating solution was applied by spin coating at a speed of 1,000 rpm and dried for 30 seconds, forming a recording layer of 2,000 Å thick. On the recording layer, gold was DC sputtered to form a reflecting layer of 1,300 Å thick. On the reflecting layer, UV curable resin (trade name: 3070, Three Bond Co.) was applied by spin coating at a speed of 1,500 rpm and cured by illuminating ultraviolet radiation from a high pressure mercury lamp, forming a protective layer of 3 µm thick. In this way, there was prepared an information recording medium (sample No. 301) having a recording layer, reflecting layer and protective layer on a substrate. Recording media, Nos. 304 to 305, were prepared by the same procedure as No. 301 except that an equimolar amount of an anti-fading agent as shown in Table 5 was added to cyanine dye (CY-1). Evaluation of information recording media 1) C/N By passing a semiconductor laser beam having a wavelength of 780 nm through an objective lens with NA = 0.5, focusing the beam at the recording layer of the medium, and causing the beam to track the groove, signals of modulated frequency of 720 kHz (duty factor 33%) were recorded in the information recording medium at a constant linear velocity of 1.3 m/sec. and a recording power of 7.0 mW. The recorded signals were read at a reading power of 0.5 mW while a C/N ratio was measured using a spectral analyzer TR4135 (Advantest Co.). 2) Reflectance Using the same optical system as used in the measurement of C/N, the unrecorded groove was tracked with a laser beam at a reading power of 0.5 mW. The quantity (X) of light reflected back from the medium was measured by a photodetector. With the medium removed, the quantity (Y) of incident light at the position where the medium had been measured by the same photodetector. A reflectance was calculated as X/Y x 100%. 3) Light fastness Light fastness was rated by the same procedure as in Example 5 except that a sample was exposed to light at 100,000 lux for 20 hours. The anti-fading agents added to the dye layer-coating solution in comparative and inventive samples are reported in Table 5 together with the test results. Sample Anti-fading agent Groove depth (Å) Reflectance (%) C/N (dB) Retention (%) Remarks 301 - 900 81 52 42 Comparison 304 1-9 900 80 51 75 Invention 305 1-10 900 79 51 80 Invention It is evident from Table 5 that information recording media having a specific recording layer according to the invention had high reflectance and C/N and were fully lightfast. Example 7 (Ink) Compound 1-9 5% Ethanol 20% Ethylene glycol 20% Distilled water 55% Ink was prepared by agitating the above ingredients at room temperature for one hour. The ink was found useful in an invisible bar code system.

Claims: A Schiff base quinone complex of the following general formula (1a): wherein each of R 1 and R 2 is an alkyl group, and M 1 is a metal atom selected from the class consisting of Ca, Ba, Y, La, Nd, Sm, Gd, Tb, Dy and Yb. A Schiff base quinone complex according to claim 1 wherein M 1 is Ca or Ba. Use of the Schiff base quinone complex of the general formula (1a) defined in claim 1 as an anti-fading agent or a dye: Use of the Schiff base quinone complex of the general formula (1a) defined in claim 1 as a anti-fading agent for use in a heat developable photosensitive material, a silver halide photosensitive material or an optical recording material. Use of the Schiff base quinone complex as an anti-fading agent in accordance with claim 5, comprising further a cyanine or squarylium dye. Use of the Schiff base quinone complex of the general formula (1a) as defined in claim 1 as a dye for use in a filter, an ink, a paint or a silver halide photosensitive material.

Inventors: FUJIWARA ITSUO, HARADA TORU, FUJIWARA, ITSUO, HARADA, TORU, Fujiwara, Itsuo c/o Fuji Photo Film Co., Ltd.
Applicants: FUJI PHOTO FILM CO LTD, FUJI PHOTO FILM CO., LTD.
Application year: 1997
Main classification: C07C251
IPC codes: G03C1, C09B57, G11B7, C07C251, B41M5, G02B5, G03C7