Ternary solid solutions of 1,4-diketo-pyrrolopyrroles and quinacridones

Abstract: Temary solid solutions useful as pigments are disclosed. The ternary solid solutions result from incorporating a third component, which is a diketopyrrolopyrrole or quinacridone pigment, into the crystal lattice of the mixed crystal formed from equimolar amounts of two different diketopyrrolopyrrole pigments.

Description: The present invention relates to single-phase ternary solid solutions which contain at least two different symmetrical 1,4-diketopyrrolopyrroles and a third component which is a quinacridone or a third 1,4-diketopyrrolopyrrole. 1,4-Diketopyrrolopyrroles, including symmetrical and asymmetrical 1,4-diketopyrrolopyrroles, i.e. of the type, wherein A and B are aryl groups, their preparation and the use thereof as pigments are disclosed, inter alia, in United States Patent No. 4,579,949. United States Patent No. 4,778,899 discloses a process for the preparation of pure asymmetrical 1,4-diketopyrrolopyrroles. This process consists of an elaborate synthesis which is carried out via the stage of special amino esters or pyrrolinones. United States Patent No. 4,783,540 furthermore discloses that solid solutions can be obtained by mixing two different 1,4-diketopyrrolopyrroles, preferably in the ratio of 65-90:10-35% by weight, and carrying out subsequent treatment such as kneading, grinding or precipitating. Solid solutions containing a diketopyrrolopyrrol-type pigment and a pigment of another class, for example, a quinacridone or quinacridonequinone, are described in United States Patent No.4,810,304. The disclosed solid solutions are characterized by their X-ray diffraction patterns, the X-ray diffraction patterns of the solid solutions being different from the sum of the X-ray diffraction patterns of the single components. However, it has been found that these products are in general polyphase solid solutions. European Patent Application No. 0 704 496 (published on 3.4.1996) claims ternary solid solutions consisting of 2,5-diphenyl-1,4-diketopyrrolo [3,4-c]pyrrole, 2,5 -di(4'-chloro-phenyl)- 1,4-diketopyrrolo[3,4-c]pyrrole and disubstituted quinacridones, which specific case is not subject-matter of the instant invention. It has been found that mixtures of two different symmetrical 1,4-diketopyrrolopyrroles of formulae types in a molar ratio of 1:1, when treated in a manner, e.g. as described above, form novel mixed crystals which, very surprisingly, are isomorphous with the crystals of the corresponding asymmetrical 1,4-diketopyrrolopyrroles of the type. These products are single-phase products whose X-ray diffraction pattern differs from that of the single components of the mixed crystal and also from that of their physical mixture. The X-ray diffraction pattern of the mixed crystal is, however, virtually identical with that of the asymmetrical single component. It has now been found that by adding a quinacridone or a third 1,4-diketopyrrolo[3,4-c]pyrrole to the equimolar mixture of the two 1,4-diketopyrrolo[3,4-c]pyrroles of formulae I and II, very surprisingly the equimolar mixed crystal described above forms and the quinacridone or the 1,4-diketopyrrolo[3,4-c]pyrrole is incorporated into the crystal lattice to form a ternary single-phase solid solution. Accordingly the single-phase ternary solid solution thus obtained has the same crystal lattice as the equimolar mixed crystal, and the corresponding X-ray diffraction patterns are essentially the same. This again makes it possible to obtain very interesting and unexpected changes in shade without affecting the good pigment properties. Accordingly, the invention further relates to single-phase ternary solid solutions consisting of two different compounds of formulae wherein A and B, which must be different, are each a group of formula wherein R 1 and R 2 are each independently of the other hydrogen, halogen, C 1 -C 18 alkyl, C 1 -C 18 -alkoxy, C 1 -C 18 alkylmercapto, C 1 -C 18 alkylamino, C 1 -C 18 alkoxycarbonyl, C 1 -C 18 alkylaminocarbonyl, -CN, -CONH 2 , -NO 2 , trifluoromethyl, C 5 -C 6 cycloalkyl, phenyl, -C=N-(C 1 -C 18 alkyl), imidazolyl, pyrrazolyl, triazolyl, piperazinyl, pyrrolyl, oxazolyl, benzoxazolyl, benzothiazolyl, benzimidazolyl, morpholinyl, piperidinyl or pyrrolidinyl, G is -CH 2 -, -CH(CH 3 )-, -C(CH 3 ) 2 -, -CH=N-, -N=N-, -O-, -S-, -SO-, -SO 2 -, -CONH- or -NR 7 -, R 3 and R 4 are each independently of the other hydrogen, halogen, C 1 -C 6 alkyl, C 1 -C 18 alkoxy or -CN, R 5 and R 6 are each independently of the other hydrogen, halogen or C 1 -C 6 alkyl, and R 7 is hydrogen or C 1 -C 6 alkyl, and a third component which is a quinacridone of formula wherein R is hydrogen, halogen, C 1 -C 6 alkyl or C 1 -C 6 alkoxy, or which third component is a 1,4-diketopyrrolo[3,4-c]pyrrole different from I and II of the formula wherein X and Y are each independently of the other a group of formula with R 1 and R 2 having the same meaning given above, wherein the ternary solid solution has an x-ray diffraction pattern that is essentially the same as the x-ray diffraction pattern exhibited by a mixed crystal composed of an equimolar amount of (I) and (II); with the proviso that the third component is neither a disubstituted quinacridone when components (I) and (II) are 1,4-diketo-3,6-diphenylpyrrolo[3,4-c]pyrrole and 1,4-diketo-3,6-di(4-chlorophenyl)pyrroio[3,4-c]pyrrole , nor a compound of formula wherein A is identical with A of the compound of formula (I) and B is identical with B of the compound of formula (II) . The diketopyrrolopyrrole compounds are designated (I) and (II) for convenience. Of course, these are completely interchangeable with each other in the above formula. The expression "essentially the same as" is intended to mean that there is sufficient overlap in the x-ray diffraction patterns to support the conclusion that the third component is incorporated into the crystal lattice of the mixed crystal of (I) and (II). In accord with this definition, it is possible for x-ray diffraction patterns which are essentially the same to have peaks in slightly different relative positions and/or for the x-ray diffraction patterns to be missing one or more minor peaks or to have additional minor peaks. Generally, minor peaks are those which have a relative intensity of less than 20 percent of the largest peak. Substitutents defined as halogen are typically iodo, fluoro, preferably bromo and, most preferably, chloro; C 1 -C 6 alkyl is typically methyl, ethyl, n-propyl, isopropyl, n-butyl, sec-butyl, tert-butyl, n-amyl, tert-amyl, hexyl, and C 1 -C 18 alkyl is in addition typically heptyl, octyl, 2-ethylhexyl, nonyl, decyl, dodecyl, tetradecyl, hexadecyl or octadecyl. C 1 -C 18 Alkoxy is, also in C 1 -C 18 alkoxycarbonyl, typically methoxy, ethoxy, n-propoxy, isopropoxy, butoxy, hexyloxy, decyloxy, dodecyloxy, hexadecyloxy or octadecyloxy. C 1 -C 18 Alkylmercapto is, for example, methylmercapto, ethylmercapto, propylmercapto, butylmercapto, octylmercapto, decylmercapto, hexadecylmercapto or octadecylmercapto. C 1 -C 18 Alkylamino is, also in C 1 -C 18 alkylaminocarbonyl, typically methylamino, ethylamino, propylamino, hexylamino, decyiamino, hexadecylamino or octadecylamino. C 5 -C 6 Cycloalkyl is typically cyclopentyl and, preferably, cyclohexyl. Of particular interest are ternary solid solutions wherein A and B in formulae I and II are each a group of formula or wherein R 1 and R 2 are each independently of the other hydrogen, chloro, bromo, C 1 -C 4 alkyl, C 1 -C 6 alkoxy, C 1 -C 6 alkylamino, phenyl or CN, G is -O-, -NR 7 -, -N=N- or -SO 2 - , R 3 and R 4 are hydrogen, and R 7 is hydrogen, methyl or ethyl, and more particularly those ternary solid solutions wherein A and B in formulae I and II are each a group of formula wherein R 1 and R 2 are each independently of the other hydrogen, methyl, tert-butyl, chloro, bromo, phenyl or CN. One of R 1 and R 2 is preferably hydrogen. The 2,9 and 4,11 disubstituted quinacridones embraced by formula III are especially suitable as quinacridone third components. Preferred quinacridones of formula III are those wherein R is hydrogen, chloro, C 1 -C 3 alkyl, methoxy or ethoxy, especially those wherein R is hydrogen, chloro or methyl. Preferred 1,4-diketopyrrolo[3,4-c]pyrroles of formula IV are those, wherein R 1 and R 2 are each independently of the other hydrogen, chloro, bromo, C 1 -C 4 alkyl, C 1 -C 6 alkoxy, C 1 -C 6 -alkylamino or CN, and especially those, wherein X and Y are identical groups and R 1 and R 2 are each independently of the other hydrogen, methyl, tert-butyl, chloro, bromo, phenyl or CN, one of R 1 and R 2 preferably being hydrogen and the other is in para position. Especially useful ternary solid solutions are those wherein (I) and (II) are selected from the group consisting of 1,4-diketo-3,6-diphenylpyrrolo[3,4-c]pyrrole (unsubstituted DPP), 1,4-diketo-3,6-di(4-chlorophenyl)pyrrolo[3,4-c]pyrrole (dichloro DPP) and 1,4-diketo-3,6-di(4-tert-butylphenyl)pyrrolo[3,4-c]pyrrole (di(t-butylphenyl) DPP). Examples of such ternary solid solutions include those wherein (I) is 1,4-diketo-3,6-diphenylpyrrolo[3,4-c]pyrrole and (II) is 1,4-diketo-3,6-di(4-chlorophenyl)pyrrolo[3,4-c]pyrrole, those wherein (I) is 1,4-diketo-3,6-diphenylpyrrolo[3,4-c]pyrrole and (II) is 1,4-diketo-3,6-di(4-tert-butylphenyl)pyrrolo[3,4-c]pyrrole or those wherein (I) is 1,4-diketo-3,6-di(4-chlorophenyl)pyrrolo[3,4-c]pyrrole and (II) is 1,4-diketo-3,6-di(4-tert-butylphenyl)pyrrolo[3,4-c]pyrrole. Such ternary solid solutions generally have color characteristics that are similar to, yet darker and more intense than, commercial perylene pigments. As a quinacridone third component, 2,9-dichloroquinacridone and 2,9-dimethylquinacridone are especially useful. Of particular interest are ternary solid solutions containing halogen-free DPPs as components (I) and (II) and 2,9-dimethylquinacridone as the third component. Such pigments provide an environmentally sound pigment which is free of chlorine. Such ternary solid solutions can be obtained in a highly transparent attractive color especially by percipitation of the corresponding pigment mixture from basic DMSO. Useful ternary solid solutions include those wherein (I) is 1,4-diketo-3,6-di(4-chlorophenyl)-pyrrolo[3,4-c]pyrrole, (II) is 1,4-diketo-3,6-di(4-tert-butylphenyl)pyrrolo[3,4-c]pyrrole and the third component is 1,4-diketo-3,6-diphenylpyrrolo[3,4-c]pyrrole or 2,9-dichloroquinacridone. When the third component is 1,4-diketo-3,6-diphenylpyrrolo[3,4-c]pyrrole such ternary solid solutions are characterized by an x-ray diffraction pattern which exhibits peaks at 4.6±0.2° 2, 18.0±0.2° 2, and 26.7±0.2° 2. When the third component is 2,9-dichloroquinacridone, such ternary solid solutions are characterized by an x-ray diffraction pattern which exhibits peaks at 4.6±0.2° 2, 17.9±0.2° 2, and 26.5±0.2° 2. In each instance, the x-ray diffraction pattern of the ternary solid solution is essentially the same as that of the binary mixed crystal containing a 1:1 molar mixture of 1,4-diketo-3,6-di(4-chlorophenyl)pyrrolo[3,4-c]pyrrole and 1,4-diketo-3,6-di(4-tert-butylphenyl)pyrrolo[3,4-c]pyrrole. However, such ternary solid solutions are significantly bluer than the binary mixed crystal and extremely dark in masstone rubout. Generally, such ternary solid solutions are in the same color space as the commercial perylene pigments. An especially useful ternary solid solution of the type described in the preceding paragraph consists of about 20 parts by weight of the 1,4-diketo-3,6-diphenylpyrrolo[3,4-c]pyrrole, about 38 parts by weight of 1,4-diketo-3,6-di(4-chlorophenyl)pyrrolo[3,4-c]pyrrole about 42 parts by weight of 1,4-diketo-3,6-di(4-tert-butylphenyl)pyrrole[3,4-c]pyrrole. Other useful ternary solid solutions include those wherein (I) is 1,4-diketo-3,6-diphenylpyrrolo[3,4-c]pyrrole and (II) is 1,4-diketo-3,6-di(4-tert-butylphenyl)pyrrolo[3,4-c]pyrrole the third component is 2,9-dichloroquinacridone or 2,9-dimethylquinacridone. Such ternary solid solutions are characterized by an x-ray diffraction pattern which exhibits peaks at 4.7±0.2° 2, 18.0±0.2° 2, and 26.7±0.2° 2. Thus, the x-ray diffraction pattern is essentially the same as that of the binary mixed crystal containing equimolar amounts of (I) and (II). The ternary solid solution containing unsubstituted DPP as component (I) and di(t-butylphenyl) DPP as component (II) and 2,9-dimethylquinacridone as the third component is especially interesting. Useful ternary solid solutions also include those wherein (I) is 1,4-diketo-3,6-diphenylpyrrolo[3,4-c]pyrrole and (II) is 1,4-diketo-3,6-di(4-tert-butylphenyl)pyrrolo[3,4-c]pyrrole and the third component is 1,4-diketo-3,6-di(4-chlorophenyl)pyrrolo[3,4-c]pyrrole. Such ternary solid solutions are characterized by an x-ray diffraction pattern which exhibits peaks at 4.8±0.2° 2, 18.0±0.2° 2, and 26.6±0.2° 2, which is essentially the same as that of the binary mixed crystal containing equimolar amounts of (I) and (II). Preferably, the ternary solid solutions of the present invention comprise equimolar quantities of components (I) and (II) and less than 30 mole-percent of the third component, for example from 4 to 28 mole-percent of the third component. In a specific embodiment, the ternary solid solutions of the present invention comprise from 4 to 20 mole-percent of the third component. Many useful ternary solid solutions of the present invention comprise from 15 to 25 mole-percent of the third component. For purposes of this application, solid solutions containing equimolar quantities of components (I) and (II) include ternary solid solutions wherein the molar ratio of (I) and (II) is from 0.95 to 1.05, preferably from 0.98 to 1.02. The present invention also relates to pigment compositions which comprise one or more of the above-described ternary solid solutions; in particular those pigment compositions which comprise a ternary solid solution described above together with an excess of the third component. The novel ternary solid solutions may be prepared starting from physical mixtures of the above defined components of formulae I and II in general accordance with the following per se known processes: by contacting in polar organic solvents, preferably by stirring the component mixture at reflux temperature, by alkaline precipitation of the component mixture from polar organic solvents, such as e.g. DMSO, or by stirring the component mixture in polar organic solvents in the presence of alkali metal alcoholates, alkali metal hydroxides or quaternary ammonium compounds, or by acid precipitation, for example, by dissolving the component mixture in acid and precipitating the solid solution by dilution with water, by grinding methods, for example, by grinding the component mixture in a ball mill in the presence of grinding media, separating the component mixture from the grinding media, and subsequently subjecting the powder to a crystal growth step, for example, by stirring the component mixture in dilute acid, such as 2% sulfuric acid. by preparing a premilled powder of the component mixture and subsequently subjecting the premilled powder to a ripening step using an organic solvent or an aqueous media, preferably in the presence of a surfactant. which processes may be carried out in general accordance with the processes disclosed in detail, inter alia, in U.S. Patent No. 4,783,540. If the solid solutions are prepared by a method wherein the components are dissolved in a solvent, the compounds of formula I or II are either mixed in powdered form in the desired ratio by standard known methods and the mixture is then dissolved in the solvent, or they are first dissolved in the solvent individually and the solutions are then mixed in the desired ratio. The following solvents may be conveniently used: ethers such as tetrahydrofuran or dioxane, or glycol ethers such as ethylene glycol methyl ether, ethylene glycol ethyl ether, diethylene glycol monomethyl ether or diethylene glycol monoethyl ether, polyalcohols such as polyethylene glycol, ketones such as acetone, ethyl methyl ketone, isobutyl methyl ketone or cyclohexanone; and also dipolar aprotic solvents, typically including acetonitrile, benzonitrile, N,N-dimethylformamide, N,N-dimethylacetamide, nitrobenzene, N-methylpyrrolidone, dimethyl sulfoxide, halogenated aliphatic or aromatic hydrocarbons, such as trichloroethane, dichloromethane, chloroform, benzene or alkyl-, alkoxy- or halogen-substituted benzene, typically toluene, xylene, anisol or chlorobenzene, aromatic N-heterocycles, such as pyridine, picoline or quinoline or high-boiling solvents e.g. decaline, n-dodecane or kerosene, or mixtures thereof. Preferred solvents are typically toluene, diphenyl ether, N-methylpyrrolidone, N,N-dimethylformamide, dimethyl sulfoxide and quinoline. The concentration of the compounds of formula I or II in the solvent or solvent system may vary greatly, depending on the solvent. It is convenient to use 0.1 to 20 % by weight, preferably 0.2 to 5 % by weight, of the compound of formula I or II, based on the entire solution. As already mentioned, the X-ray diffraction pattern of the novel solid solutions, as well as that of the mixed crystals of (I) and (II) wherein (I) and (II) are combined in a molar ratio of 1:1 is characterized by lines differing from those of the X-ray diffraction patterns of the corresponding physical mixture and the corresponding single components, but the x-ray diffraction pattern is essentially the same as that of the asymmetrical diketopyrrolopyrrole of the type. Depending on the end use requirements, an aftertreatment of the pigment can be advantageous. If required, recrystallization or thermal treatment is carried out by conventional methods for pigments. The usual method is that of thermal aftertreatment in water, dilute acid or in an organic solvent and, if required, under pressure. It is preferred to use organic solvents, typically benzenes which are substituted by halogen atoms, alkyl groups or nitro groups, such as xylenes, chlorobenzene, o-dichlorobenzene or nitrobenzene, as well as pyridine bases, typically pyridine, picoline or quinoline, and also ketones such as cyclohexanone, alcohols such as isopropanol, butanols or pentanols, ethers such as ethylene glycol monomethyl ether or ethylene glycol monoethyl ether, amides such as dimethyl formamide or 1-methyl-2-pyrrolidinone, as well as dimethyl sulfoxide or sulfolane. The aftertreatment may also be carried out in water, under normal or elevated pressure, in the presence of organic solvents and/or with the addition of surfactants. The ternary solid solutions are advantageously prepared by precipitation from basic DMSO. The novel ternary solid solutions and pigment compositions are useful as pigments for colouring organic material of high molecular weight. Illustrative examples of high molecular weight organic materials which can be coloured with the novel ternary solid solutions and pigment compositions are cellulose ethers and esters, typically ethyl cellulose, nitro cellulose, cellulose acetate, cellulose butyrate, natural resins or synthetic resins, typically polymerization or condensation resins, such as aminoplasts, preferably urea/formaldehyde and melamine/formaldehyde resins, alkyd resins, phenolic plastics, polycarbonates, polyolefins, polystyrene, polyvinyl chloride, polyamides, polyurethanes, polyester, ABS, polyphenylenoxides, rubber, casein, silicone and silicone resins, singly or in mixtures. The above high molecular weight organic compounds are obtained singly or as mixtures as plastics, melts or in the form of spinning solutions, paints, coating materials or printing inks. Depending on the end use requirement, it is expedient to use the ternary solid solutions or pigment compositions of this invention as toners or in the form of preparations. The ternary solid solutions and pigment compositions of this invention are used in an amount of 0.01 to 30 % by weight, preferably of 0.1 to 10 % by weight, based on the high molecular weight organic material to be pigmented. The pigmenting of the high molecular weight organic materials with the ternary solid solution and pigment compositions of this invention is conveniently effected by incorporating such solid solutions by themselves or in the form of masterbatches in the substrates using roll mills, mixing or milling apparatus. The pigmented material is then brought into the desired final form by methods which are known per se, conveniently by calendering, moulding, extruding, coating, casting or by injection moulding. It is often desirable to incorporate plasticisers into the high molecular weight compounds before processing in order to produce non-brittle mouldings or to diminish their brittleness. Suitable plasticisers are typically esters of phosphoric acid, phthalic acid or sebacic acid. The plasticisers may be incorporated into the novel solid solutions before or after working the pigments into the polymers. To obtain different shades, it is also possible to add to the high molecular weight organic materials fillers or other chromophoric components such as white, coloured or black pigments in any amount, in addition to the novel solid solutions. For pigmenting paints, coating materials and printing inks, the high molecular weight organic materials and the ternary solid solutions or pigment composition of this invention, together with optional additives such as fillers, other pigments, siccatives or plasticisers, are finely dispersed or dissolved in a common organic solvent or solvent mixture. The procedure may be such that the individual components by themselves, or also several jointly, are dispersed or dissolved in the solvent and thereafter all the components are mixed. The novel ternary solid solutions and pigment compositions are particularly suitable for colouring plastics, more particularly polyvinyl chloride and polyolefins, and paints, preferably automotive lacquers. When used for colouring e.g. polyvinyl chloride or polyolefins, the novel ternary solid solutions and pigment compositions have good all-round pigment properties, such as good dispersibility, superior color strength and purity, good fastness to migration, heat, light and weathering as well as good hiding power. The invention is illustrated by, but not limited to, the following Examples. All parts are parts by weight unless otherwise specified. Example 1: A suspension of 1.61g (4.5 mMol) of 1,4-diketo-3,6-di-(4'-chlorophenyl)-pyrrolo-[3,4-c]-pyrrole, 1.80g (4.5 mMol) of 1,4-diketo-3,6-di-(4'-tert-butylphenyl)-pyrrolo-[3,4-c]pyrrol, 0.28 g (0.9mMol) of β-quinacridone and 1.22 g (21.78 mMol) of potassium hydroxide in 100 ml of dimethyl sulfoxide is heated to 50°C and stirred at this temperature for 2 hours. The red reaction mixture is then cooled to room temperature and transferred to a well stirred solution of 2.23 g (21.78 mMol) of sulphuric acid (96 %) in 300 ml water at 0°C. The resulting red suspension is stirred at 0°C for 2 more hours and then allowed to warm up to room temperature. The product is collected by filtration, washed with 300 ml of methanol followed by 300 ml water, dried under vacuum at 80°C and pulverized. This yields 2.92 g of a dark red pigment (79 % of the theoretical). Analysis C H N Cl calculated 69.95% 4.84% 7.56% 9.02% found 68.75% 4.78% 7.51% 9.60% The X-ray diffraction pattern is characterized by the following diffraction lines: Interplanar spacing (d-value in Å) Scattering angle (2Θ) Relative intensity (%) 19.62 4.50 98 6.39 13.83 38 4.96 17.86 100 3.78 23.49 18 3.63 24.47 23 3.36 26.44 89 3.28 27.13 51 3.16 28.17 28 3.04 29.39 25 By comparison with the bynary mixed crystal of 1,4-diketo-3,6-di-(4'-chlorophenyl)-pyrrolo-[3,4-c]-pyrrole and 1,4-diketo-3,6-di-(4'-tert-butylphenyl)-pyrrolo-[3,4-c]-pyrrole which is characterized by the following X-ray diffraction pattern Interplanar spacings (d-values in Å) Scattering angles (2Θ) Relative intensity (%) 19.4208 4.55 59 6.3517 13.93 15 4.9880 17.77 83 3.7947 23.42 7 3.6444 24.40 7 3.3649 26.47 100 3.2301 27.59 31 3.1587 28.23 8 3.0305 29.45 9 it can be seen that the solid solution is in the crystal lattice of the mixed crystal (the host). Example 2: In the same way as in Example 1 except that 0.31 g (0.9 mMol) of 2,9-dimethylquinacridone is used in place of β-quinacridone, there is obtained 3.36 g (90 % of the theoretical) of a deep red pigment. Analysis C H N Cl calculated 70.01% 4.92% 7.49% 9.02% found 69.83% 5.12% 7.40% 8.59% The X-ray diffraction pattern is characterized by the following diffraction lines: Interplanar spacing (d-value in Å) Scattering angle (2Θ) Relative intensity (%) 19.69 4.48 91 6.37 13.89 30 4.97 17.84 100 3.80 23.40 17 3.64 24.46 22 3.37 26.46 85 3.26 27.35 43 3.04 29.39 24 By comparison with the binary mixed crystal of 1,4-diketo-3,6-di-(4'-chlorophenyl)-pyrrolo-[3,4-c]-pyrrole and 1,4-diketo-3,6-di-(4'-tert-butylphenyl)-pyrrolo-[3,4-c]-pyrrole (see Example 1) it can be seen that the solid solution is in the crystal lattice of the mixed crystal (the host). Example 3: A mixture containing 1.60 g (4.5 mMol) of 1,4-diketo-3,6-di-(4'-chlorophenyl)-pyrrolo-[3,4-c]-pyrrole, 1.80 g (4.5 mMol) of 1,4-diketo-3,6-di-(4'-tert-butylphenyl)-pyrrolo-[3,4-c]-pyrrole, 0.38 g (1.0 mMol) of 2,9-dichloroquinacridone and 1.68 g (29.9 mMol) of potassium hydroxide in 110 ml of tert-amyl alcohol is heated to 100°C and stirred at this temperature for 1 hour. A part of the solvent (ca 40 ml) is then distilled off. The resulting violet coloured mixture is cooled to 50°C and transferred to a well stirred mixture of 0.88 ml (15 mMol) of sulphuric acid (92 %), 100 ml of water and 100 ml of methanol. The red suspension thus obtained is stirred at room temperature for 2 more hours and then filtered. The press cake is washed with 300 ml of methanol followed by 500 ml of water, dried at 60°C under vacuum and pulverized. This gives 2.8 g (74 % of the theoretical) of a red pigment. Analysis C H N Cl calculated 68.63% 4.70% 7.41% 10.79% found 67.21% 4.66% 7.11% 11.03% The X-ray diffraction pattern is characterized by the following diffraction lines: Interplanar spacing (d-value in Å) Scattering angle (2Θ) Relative intensity (%) 19.26 4.58 100 6.35 13.94 38 4.94 17.94 91 3.80 23.41 18 3.63 24.49 21 3.35 26.57 81 3.25 27.40 40 3.02 29.56 20 By comparison with the binary mixed crystal of 1,4-diketo-3,6-di-(4'-chlorophenyl)-pyrrolo-[3,4-c]-pyrrole and 1,4-diketo-3,6-di-(4'-tert-butylphenyl)-pyrrolo-[3,4-c]-pyrro le (see Example 1) it can be seen that the solid solution is in the crystal lattice of the mixed crystal (the host). Example 4: A mixture of 1.80 g (4.5 mMol) of 1,4-diketo-3,6-di-(4'-tert-butylphenyl)-pyrrolo-[3,4-c]-pyrrole, 1.30 g (4.5 mMol) of 1,4-diketo-3,6-diphenyl-pyrrolo-[3,4-c]-pyrrole, 0.31 g (1.0 mMol) of β-quinacridone and 1.68 g (29.9 mMol) of potassium hydroxide in 50 ml of dimethyl sulfoxide is heated to 50°C and stirred at this temperature for 1 hour. The violet coloured reaction mixture is transferred to a well stirred mixture containing 0.88 ml (15 mMol) of sulphuric acid (92 %), 100ml of water and 100 ml of methanol. The resulting red suspension is stirred at room temperature for 2 more hours and filtered. The press cake is washed with 500 ml of methanol followed by 500 ml of water and dried at 60°C under vacuum. This yields 3.05 g (89 % of the theoretical) of a red pigment. Analysis C H N calculated 76.53% 5.45% 8.42% found 76.20% 5.67% 8.25% The X-ray diffraction pattern is characterized by the following diffraction lines: Interplanar spacing (d-value in Å) Scattering angle (2Θ) Relative intensity (%) 19.19 4.60 100 6.20 14.26 16 4.96 17.86 61 3.36 26.49 65 3.31 26.93 39 3.01 29.69 9 By comparison with the mixed crystal of 1,4-diketo-3,6-di-(4'-tert-butylphenyl)-pyrrolo-[3,4-c]-pyrrole and 1,4-diketo-3,6-diphenyl-pyrrolo-[3,4-c]-pyrrole which is characterized by the following X-ray diffraction pattern Interplanar spacings (d-values in Å) Scattering angles (2Θ) Relative intensity 18.9113 4.669 100 6.1915 14.294 7 4.9491 17.908 43 3.3535 26.559 48 3.2997 27.000 22 it can be seen that the solid solution is in the crystal lattice of the mixed crystal (the host). Example 5: A mixture of 1.68 g (4.7mMol) of 1,4-diketo-3,6-di-(4'-chlorophenyl)-pyrrolo-[3,4-c]-pyrrole, 1.49g (4.7 mMol) of 1,4-diketo-3,6-di-(3'-methylphenyl)-pyrrolo-[3,4-c]-pyrrole, 0.23 g (0.6mMol) of 2,9-dichloroquinacridone and 1.68 g (29.9 mMol) of potassium hydroxide in 50 ml of dimethyl sulfoxide is treated in the same way as described in Example 16 above, to yield 3.05 g (90 % of the theoretical) of an orange coloured pigment. Analysis C H N Cl calculated 67.92% 3.89% 8.29% 10.45% found 66.58% 3.83% 8.15% 11.19% The X-ray diffraction pattern is characterized by the following diffraction lines: Interplanar spacing (d-value in Å) Scattering angle (2Θ) Relative intensity (%) 15.83 5.58 56 7.60 11.63 15 6.84 12.94 34 6.31 14.03 44 6.19 14.29 49 5.10 17.37 17 5.06 17.50 17 3.72 23.90 31 3.33 26.73 100 3.17 28.11 22 3.15 28.35 20 By comparison with the mixed crystal of 1,4-diketo-3,6-di-(4'-chlorophenyl)- pyrrolo- [3,4-c]-pyrrole and 1,4-diketo-3,6-di-(3'-methylphenyl)-pyrrolo-[3,4-c]-pyrrole which is characterised by the following X-ray diffraction pattern Interplanar spacing (d-value in Å) Scattering angle (2Θ) Relative intensity (%) 15.3172 5.765 99 7.5658 11.687 14 6.8504 12.913 26 6.3196 14.003 34 6.1515 14.387 48 5.0223 17.645 22 3.6887 24.107 22 3.3206 26.827 100 3.1567 28.248 17 it can be seen that the solid solution is in the crystal lattice of the mixed crystal (the host). Example 6: A mixture of 1.55 g (4.35 mMol) of 1,4-diketo-3,6-di-(4'-chlorophenyl)-pyrrolo-[3,4-c]-pyrrole, 1.38 g (4.35 mMol) of 1,4-diketo-3,6-di-(3'-methylphenyl)-pyrrolo-[3,4-c]-pyrrole, 0.41 g (1.3 mMol) of 1,4-diketo-3,6-di-(4'-methylphenyl)-pyrrolo-[3,4-c]-pyrrole and 1.68g (29.9mMol) of potassium hydroxide in 110 ml of tert-amyl alcohol is treated in the same way as described in Example 15 above, to yield 2.6 g (78 % of the theoretical) of an orange coloured pigment. Analysis C H N Cl calculated 68.77% 4.04% 8.38% 9.23% found 65.38% 3.93% 7.79% 9.59% The X-ray diffraction pattern is characterized by the following diffraction lines: Interplanar spacing (d-value in Å) Scattering angle (2Θ) Relative intensity (%) 16.33 5.41 73 7.19 12.29 27 6.67 13.26 38 6.38 13.87 45 6.27 14.10 49 6.17 14.34 49 5.11 17.35 22 3.75 23.72 28 3.35 26.61 100 3.15 28.27 24 3.01 29.65 24 2.91 30.68 24 It can be seen that the solid solution is in the crystal lattice of the mixed crystal (the host) of 1,4-diketo-3,6-di-(4'-chlorophenyl)-pyrrolo-[3,4-c]-pyrrole and 1,4-diketo-3,6-di-(3'-methylphenyl)-pyrrolo-[3,4-c]-pyrrole (see Example 5). Example 7: A mixture of 1.60 g (3.99 mMol) of 1,4-diketo-3,6-di-(4'-tert-butylphenyl)-pyrrolo-[3,4-c]-pyrrole, 1.15 g (3.99 mMol) of 1,4-diketo-3,6-diphenyl-pyrrolo-[3,4-c]-pyrrole, 0.67 g (1.98 mMol) of 1,4-diketo-3,6-di-(4'-cyanophenyl)-pyrrolo-[3,4-c]-pyrrole and 1.68 g (29.9 mMol) of potassium hydroxide in 50 ml of methyl sulfoxide is treated in the same manner as described in Example 16, yielding 2.95 g (86% of the theoretical) of a red pigment. Analysis C H N calculated 75.39% 5.10% 10.00% found 74.49% 5.28% 9.76% The X-ray diffraction pattern is characterized by the following diffraction lines: Interplanar spacing (d-value in Å) Scattering angle (2Θ) Relative intensity (%) 19.96 4.42 100 6.46 13.70 15 6.08 14.56 14 4.96 17.87 51 3.35 26.57 63 It can be seen that the solid solution is in the crystal lattice of the mixed crystal (the host) of 1,4-diketo-3,6-di-(4'-tert-butylphenyl)-pyrrolo-[3,4-c]-pyrrole and 1,4-diketo-3,6-diphenyl-pyrrolo-[3,4-c]-pyrrole (see Example 4). A RIGAKU model D-MAX-B with a CU-K α source is used to record all x-ray diffraction patterns reported in Examples 8 to 17. Example 8: Equimolar (rounded to first decimal to make up a total of 10.0 g.) amounts of 1,4-diketo-3,6-diphenylpyrrolo[3,4-c]pyrrole (4.2 g; 0.0146 moles) and 1,4-diketo-3,6-di(4-tert.-butylphenyl)-pyrrolo[3,4-c]pyrrole(5.8 g; 0.0145 moles), as well as dimethyl glutarate (1.0g) and aluminum sulfate (Al 2 (SO 4 ) 3 •15-18 H20; 40.0 g) are added to a 1000 ml ball mill containing steel balls (1500 g; 1.2 cm diameter) and nails (150 g; 3.0 cm length) as grinding media. The mill is tightly closed and rolled on a roller for 24 hours. The contents of the mill are then discharged and separated from the milling media. The mill powder thus obtained is stirred with 2 % aqueous sulfuric acid (500 ml) for 2 hours at 90°C. The resulting pigment slurry is filtered, washed with hot water until neutral and free of salts and then dried. A rubout of the resulting pigment shows a very bluish red color which is similar to that a commercial perylene red pigment, but far superior in color saturation. The resulting pigment is a binary mixed crystal characterized by the following x-ray diffraction pattern: Scattering angle (2Θ) Relative intensity (%) 4.74 100 6.42 8 14.38 11 17.98 50 19.15 11 21.23 7 24.55 7 26.64 59 29.82 8 Example 9: Following the procedure used in example 8, a pigment is prepared using 1,4-diketo-3,6-diphenylpyrrolo[3,4-c]pyrrole (3.3 g; 0.0115moles), 1,4-diketo-3,6-di(4-tert.-butylphenyl)-pyrrolo[3,4-c]pyrrole (4.7 g; 0.0118moles) and 2,9-dichlorquinacridone (2.0 g; 0.0053 moles). The resulting pigment shows a dark masstone and is similar in color to the binary mixed crystal described in Example 8. The resulting ternary solid solution shows an x-ray diffraction pattern that is essentially the same as the binary mixed crystal of example 8 indicating a Guest-Host solid solution wherein the binary solid compound serves as a host to 2,9-dichloroquinacridone. The x-ray diffraction pattern is characterized by the following diffraction lines: Scattering angle (2Θ) Relative intensity (%) 4.78 100 14.46 14 18.03 46 19.06 13 23.14 9 24.60 10 26.68 64 Example 10: Following the procedure in Example 8, a pigment is prepared using 1,4-diketo-3,6-diphenylpyrrolo[3,4-c]pyrrole (3.3 g; 0.0115 moles), 1,4-diketo-3,6-di(4-tert.-butylphenyl)-pyrrolo[3,4-c]pyrrole (4.7 g; 0.0118 moles) and 1,4-diketo-3,6-di(4-chlorophenyl)-pyrrolo[3,4-c]pyrrole (2.0 g; 0.0056 moles). The resulting ternary solid solution showed an X-ray diffraction pattern which is essentially the same as the binary mixed crystal described in Example 8 indicating a Guest-Host solid solution wherein the binary mixed crystal served as a host to 1,4-diketo-3,6-di(4-chlorophenyl)-pyrrolo[3,4-c]pyrrole. The x-ray diffraction pattern is characterized by the following diffraction lines: Scattering angle (2Θ) Relative intensity (%) 4.65 100 6.45 20 14.06 14 14.80 11 18.02 68 19.26 13 23.93 8 24.57 11 26.68 75 28.32 16 29.64 12 Example 11: A pigment is prepared according to Example 8, using equimolar quantities of 1,4-diketo-3,6-di(4-chlorophenyl)-pyrrolo[3,4-c]pyrrole (4.7 g; 0.0132 moles) and 1,4-diketo-3,6-di(4-tert.-butylphenyl)-pyrrolo[3,4-c]pyrrole (5.3 g; 0.0133 moles) instead of 1,4-diketo-3,6-diphenylpyrrolo[3,4-c]pyrrole and 1,4-diketo-3,6-di(4-tert.-butylphenyl)-pyrrolo[3,4-c]pyrrole. The resulting binary mixed crystal pigment is a close color match to a commercial perylene pigment and is characterized by the following x-ray diffraction pattern: Scattering angle (2Θ) Relative intensity (%) 4.60 100 8.41 13 14.00 25 17.93 75 23.52 14 24.56 14 26.56 81 27.65 30 29.52 15 Example 12: Following the procedure used in Example 8, a pigment is prepared using 1,4-diketo-3,6-di(4-chlorophenyl)-pyrrolo[3,4-c]pyrrole (3.8 g; 0.0105 moles), 1,4-diketo-3,6-di(4-tert.-butylphenyl)-pyrrolo[3,4-c]pyrrole (4.2 g; 0.0105 moles) and 2,9-dichloroquinacridone (2.0 g; 0.0053 moles). The resulting ternary solid solution showed an X-ray diffraction pattern which is substantially identical to that of the binary mixed crystal und described in example 10 indicating a Guest-Host solid solution wherein the binary mixed crystal served as a host to 2,9-dichloroquinacridone. The x-ray diffraction pattern is characterized by the following lines: Scattering angle (2Θ) Relative intensity (%) 4.60 100 13.99 29 15.18 17 17.92 86 23.41 21 24.56 20 26.57 90 27.70 54 29.54 20 The pigment shows a dark masstone and is similar in color to the binary mixed crystal described in example 11. Example 13: Following the procedure used in example 8, a pigment is prepared using 1,4-diketo-3,6-diphenylpyrrolo[3,4-c]pyrrole (2.0 g; 0.0069 moles), 1,4-diketo-3,6-di(4-tert.-butylphenyl)-pyrrolo[3,4-c]pyrrole (4.2 g; 0.0105 moles) and 1,4-diketo-3,6-di(4-chlorophenyl)-pyrrolo[3,4-c]pyrrole (3.8 g; 0.0106 moles). The resulting ternary solid solution shows an x-ray diffraction pattern which is substantially identical to the binary mixed crystal und described in example 11 indicating a Guest-Host solid solution wherein the binary mixed crystal served as a host to 1,4-diketo-3,6-diphenylpyrrolo[3,4-c]pyrrole. The rub out evaluation revealed the pigment to be in the same color space as that of a commercial perylene pigment. The x-ray diffraction pattern is characterized by the following lines: Scattering angle (2Θ) Relative intensity (%) 4.63 100 5.70 21 13.99 21 14.96 13 18.03 71 23.49 13 24.56 13 26.72 77 27.98 17 29.56 15 Example 14: A 500 ml flask equipped with a thermometer, stirrer, and condenser is charged with 15.7 grams of 45 % aqueous potassium hydroxide, 13 ml water, and 120 ml DMSO. 12.0 grams of 1,4-diketo-3,6-di(4-tert.-butylphenyl)-pyrrolo[3,4-c]pyrrole and 8.7 grams of 1,4-diketo-3,6-diphenylpyrrolo[3,4-c]pyrrole are added, stirring at 40-50°C. The mixture is heated to 50-55°C and stirred at 50-55°C for five minutes. The resulting solution is drowned into 550 ml water at 20-30°C, causing the pigment to precipitate. The pigment suspension is stirred for 1 hour at 25-30°C and filtered. The presscake is washed DMSO free with water to a pH 7-8 and dried. The pulverized pigment shows a strong maroon shade by rub out according to ASTM method D-387-60 in a lithographic varnish. The x-ray diffraction pattern is characterized by the following lines: Scattering angle (2Θ) Relative intensity (%) 4.77 100 14.44 12 18.02 44 24.64 8 26.67 57 29.85 9 Example 15: The procedure of Example 14 is repeated using additionally 2.6 grams 2,9-dimethylquinacridone as a third pigment component and 17.7 grams 45 % aqueous potassium hydroxide and 16 ml water to yield a ternary pigment solid solution. Relative to the mixed crystal of Example 14 the ternary solid solution is higher in transparency and saturation and darker when applied by rub out according to ASTM method D-387-60 in a lithographic varnish. The ternary solid solution has an x-ray diffraction pattern that is essentially the same as the x-ray diffraction pattern of the mixed crystal of Example 14. The x-ray diffraction pattern is characterized by the following lines: Scattering angle (2Θ) Relative intensity (%) 4.77 100 14.42 15 18.02 47 24.66 11 26.66 63 Example 16: The procedure of Example 14 is repeated using additionally 3.5 grams 2,9-dimethylquinacridone as a third pigment component and 18.5 grams 45 % aqueous potassium hydroxide and 16 ml water yielding a ternary pigment solid solution which shows an X-ray diffraction pattern substantially the same as that of the mixed crystal prepared as described in Example 14. Compared with the product of Example 14, the ternary solid solution is higher in transparency and saturation and darker when applied by rub out according to ASTM method D-387-60 in a lithographic varnish. The x-ray diffraction pattern is characterized by the following lines: Scattering angle (2Θ) Relative intensity (%) 4.77 100 14.42 16 18.03 40 24.67 12 26.67 59 Example 17: The procedure of Example 14 is repeated using additionally 4.1 grams 2,9-dichloroquinacridone as a third pigment component, 18.6 grams 45 % aqueous potassium hydroxide and 18 ml water and by transferring the pigment solution into 700 ml water instead of 550 ml water. The resulting ternary pigment solid solution shows essentially the same X-ray diffraction pattern as that of the mixed crystal prepared as described in Example 14. Compared with the product of Example 14, the ternary solid solution is higher in transparency and saturation and darker when applied by rub out according to ASTM method D-387-60 in a lithographic varnish. The x-ray diffraction pattern is characterized by the following lines: Scattering angle (2Θ) Relative intensity (%) 4.75 100 14.44 15 18.05 41 26.68 60 Example 18: This example illustrates the incorporation of the highly transparent ternary pigment solid solution obtained according to Example 15 mixed with a pearlescent mica pigment in an automotive coating finish. Pigment Dispersion 80.0 grams Non-Aqueous Dispersion resin (NAD-resin), 17.6 grams dispersant resin, 70.4 grams aromatic solvent (SOLVESSO 100 from ESSO) and 32.0 grams DPP pigment obtained according to Example 15 are ball milled for 64 hours. The dispersion contains 16.0 % pigment and 48.0 % solids at a pigment to binder ratio of 0.5. Stabilized Resin Solution 144.6 grams of xylene, 90.0 grams methanol, 1353.0 grams NAD-resin, 786.2 grams melamine resin, 65.6 grams UV-screener solution, 471.6 grams acrylourethane resin, and 89.0 grams catalyst solution are mixed with an impeller stirrer in an one gallon jar. Mica Formulation 251.1 grams pearlescent, titanium dioxide coated mica pigment, 315.0 grams NAD-resin, and 180.0 grams acrylourethane resin are mixed in a glass container. The mica formulation contains 27.9 % mica pigment and 57.3 % solids at a pigment to binder ratio of 0.5. Paint Formulation (50 parts pigment/50 parts mica) 28.7 grams of the above described pigment dispersion, 16.5 grams of the above described mica formulation, 61.0 grams acrylourethane resin, 3.5 grams NAD resin, and 70.2 grams of the above described stabilized resin solution are mixed and sprayed onto a primed aluminum panel, followed by spraying a clearcoat resin onto the colored basecoat. The panel is exposed to ambient air for 10 minutes and stoved for 30 minutes at 130°C. A unique maroon shade colored coating is obtained displaying an appearance of color depth and high flop with excellent weatherability. Similar colored panels are obtained using the pigments prepared according to Examples 16 to 17. Example 19: 7.5 g of the solid solution of Example 1, 98.9 g of a CAB solution consisting of 41.0 g of cellulose acetobutyrate ®CAB 531.1, 20 % in butanol/xylene 2:1 (Eastman Chem.) 1.5 g of zirconium octoate, 18.5 g of ®SOLVESSO 150 (aromatic hydrocarbons; ESSO), 21.5 g of butyl acetate, and 17.5 g of xylene, 36.5 g of polyester resin ®DYNAPOL H700 (Dynamit Nobel), 4.6 g of melamine resin MAPRENAL MF650 (Hoechst) and 2.5 g of dispersant ®DISPERBYK160 (Byk Chemie) are dispersed together over 90 minutes in a disperser (total varnish: 150 g; 5 % of pigment). For the base coat layer, 27.69 g of the mass-tone varnish so obtained are mixed with 17.31 g of Al stock solution (8 %) consisting of 12.65 g of ®SILBERLINE SS 3334AR, 60 % (Silberline Ltd.) 56.33 g of CAB solution (composition as above) 20.81 g of polyester resin ®DYNAPOL H700 2.60 g of melamine resin ®MAPRENAL MF650 7.59 g of ®SOLVESSO 150 and sprayed onto an aluminium sheet (wet film c.20 µm). After drying in the air for 30 minutes at room temperature, a TSA varnish consisting of 29.60 g of acrylic resin ®URACRON 2263 XB, 50 % in xylene/butanol (Chem. Fabrik Schweizerhalle), 5.80 g of melamine resin ®CYMEL 327, 90 % in isobutanol, 2.75 g of butyl glycol acetate, 5.70 g of xylene, 1.65 g of n-butanol 0.50 g of silicone oil, 1 % in xylene, 3.00 g of light stabiliser ®TINUVIN 900, 10 % in xylene (Ciba) 1.00 g of light stabiliser ®TINUVIN 292, 10 % in xylene (Ciba) is sprayed thereon as top coat finish (wet film c.50 µm). After drying in the air for a further 30 minutes at room temperature, the varnish is stoved for 30 minutes at 130°C. Example 20: 0.6 g of the solid solution of Example 2 is mixed with 67 g of polyvinyl chloride, 33 g of dioctylphthalate, 2 g of dibutyl tin dilaurate and 2 g of titanium dioxide and processed on a roll mill for 15 minutes at 160°C to a thin film. The PVC film so obtained has superior colour strength and is resistant to migration and light. Example 21: 1000 g of polypropylene granulate (®DAPLEN PT-55, Chemie LINZ) and 20 g of a 50 % pigment preparation, consisting of 10 g of the solid solution of Example 6 and 10 g of Mg behenate, are thoroughly mixed in a mixer drum. The granulate so treated is then spun according to the melt spinning process in the temperature range from 260 to 285°C. Red filaments are obtained having excellent light and textile fastness properties.

Claims: A single-phase ternary solid solution consisting of two different compounds of formulae wherein A and B, which must be different, are each a group of formula or wherein R 1 and R 2 are each independently of the other hydrogen, halogen, C 1 -C 18 alkyl, C 1 -C 18 -alkoxy, C 1 -C 18 alkylmercapto, C 1 -C 18 alkylamino, C 1 -C 18 alkoxycarbonyl, C 1 -C 18 alkylaminocarbonyl, -CN, -CONH 2 , -NO 2 , trifluoromethyl, C 5 -C 6 cycloalkyl, -C=N-(C 1 -C 18 alkyl), phenyl, imidazolyl, pyrrazolyl, triazolyl, piperazinyl, pyrrolyl, oxazolyl, benzoxazolyl, benzothiazolyl, benzimidazolyl, morpholinyl, piperidinyl or pyrrolidinyl, G is -CH 2 -, -CH(CH 3 )-, -C(CH 3 ) 2 -, -CH=N-, -N=N-, -O-, -S-, -SO-, -SO 2 -, -CONH- or -NR 7 -, R 3 and R 4 are each independently of the other hydrogen, halogen, C 1 -C 6 alkyl, C 1 -C 18 alkoxy or -CN, R 5 and R 6 are each independently of the other hydrogen, halogen or C 1 -C 6 alkyl, and R 7 is hydrogen or C 1 -C 6 alkyl, and a third component, which third component is a quinacridone of formula wherein R is hydrogen, halogen, C 1 -C 6 alkyl or C 1 -C 6 alkoxy, or which third component is a 1,4-diketopyrrolo[3,4-c]pyrrole different from I and II of the formula wherein X and Y are each independently a group of formula with R 1 and R 2 having the same meaning given above, wherein the ternary solid solution has an x-ray diffraction pattern that is essentially the same as the x-ray diffraction pattern exhibited by a mixed crystal composed of an equimolar amount of (I) and (II); with the proviso that the third component is neither a disubstituted quinacridone when components (I) and (II) are 1,4-diketo-3,6-diphenylpyrrolo[3,4-c]pyrrole and 1,4-diketo-3,6-di(4-chlorophenyl)pyrrolo[3,4-c]pyrrole , nor a compound of formula wherein A is identical with A of the compound of formula (I) and B is identical with B of the compound of formula (II) . A ternary solid solution according to claim 1 wherein A and B in formulae I and II are each a group of formula or wherein R 1 and R 2 are each independently of the other hydrogen, chloro, bromo, C 1 -C 4 alkyl, C 1 -C 6 alkoxy, C 1 -C 6 alkylamino or CN, G is -O-, -NR 7 , -N=N- or -SO 2 -, R 3 and R 4 are hydrogen, and R 7 is hydrogen, methyl or ethyl. A ternary solid solution according to claim 2 wherein A and B in formulae I and II are each a group of formula wherein R 1 and R 2 are each independently of the other hydrogen, methyl, tert-butyl, chloro, bromo or CN. A ternary solid solution according to claim 3, wherein at least one of R 1 and R 2 is hydrogen. A ternary solid solution according to claim 1 wherein the third component is a quinacridone of formula III, wherein R is hydrogen, chloro, C 1 -C 3 alkyl, methoxy or ethoxy. A ternary solid solution according to claim 5, wherein R is hydrogen, chloro or methyl. A ternary solid solution according to claim 1 wherein the third component is a 1,4-diketopyrrolo[3,4-c]pyrrole of formula IV, wherein R 1 and R 2 are each independently of the other hydrogen, chloro, bromo, C 1 -C 4 alkyl, C 1 -C 6 alkoxy, C 1 -C 6 alkylamino or CN. A ternary solid solution according to claim 7, wherein in formula IV, X and Y are identical groups and R 1 and R 2 are each independently of the other hydrogen, methyl, tert-butyl, chloro, bromo or CN. A ternary solid solution according to claim 8, wherein at least one of R 1 and R 2 is hydrogen and the other is in the para position in each of (I) and (II). A ternary solid solution of claim 1 which comprises from 4 to 28 mole-percent of the third component. A ternary solid solution of claim 1 which comprises an equimolar ratio of (I) and (II). A pigment composition which comprises a ternary solid solution of claim 1 together with an excess of the third component.

Inventors: BAEBLER FRIDOLIN, HAO ZHIMIN, HENDI SHIVAKUMAR BASALINGAPPA, IQBAL ABUL, BAEBLER, FRIDOLIN, HAO, ZHIMIN, HENDI, SHIVAKUMAR BASALINGAPPA, IQBAL, ABUL, Bäbler, Fridolin
Applicants: CIBA SC HOLDING AG, CIBA SPECIALTY CHEMICALS HOLDING INC.
Application year: 1997
Main classification: C09B67
IPC codes: C09B67