THERMALLY RELEASABLE BARRIER COATING, COMPOSITION THERFOR, AND USE THEREOF

Abstract: A combination of (A) a nitrogen containing water soluble polymer, (B) a water insoluble film forming polymer, and (C) gas filled, polymer walled microballoons provides a superior thermally releasable coating that (i) can be conveniently and reliably coated from a water based solution and dispersion onto surfaces to be protected against painting, (ii) is reliably stable at ambient temperatures, (iii) even after being coated with many times its own thickness of accumulated paint particles, rapidly disintegrates, along with the accumulated paint coating formed on it, upon contact with hot water, into particles of a size that readily escapes from standard paint booth grate structures, (iv) detackifies any paint particles that escape during disintegration of the combined thermally releasable coating and paint residues accumulated thereon, and (v) disintegrates into particles that float on water, so that they can be readily removed from the grates by immersing the latter in hot water, allowing a few minutes for the disintegration to take effect, and then skimming off the floating solids on the surface of the water.

Description: THERMALLY RELEASABLE BARRIER COATING, COMPOSITION THEREFOR, AND USE THEREOF Field of the Invention This invention relates to an improved composition and method for providing a thermally releasable barrier coating for surfaces not intended to be painted but on which paint 1 nevertheless accumulates in practice because of the proximity of the surfaces not intended to be painted to other surfaces that are intended to be painted. The invention is more particularly applicable for coating the floor grates in paint spray booths or cabin¬ ets, such as are extensively used in manufacturing automobiles and many other objects that are decorated by painting. Discussion of Related Art Numerous barrier coatings have been used in the prior art. Most have been re¬ moved when necessary by solvents, use of high pressure and/or high temperature water, mechanical means, or the like, all of which to greater or lesser degrees are labor intens¬ ive, require substantial volumes of at least moderately expensive materials, or both. More recently, thermally removable barrier coatings have become known in the art. 1 Throughout this description, unless the context requires to the contrary, as where a specific material is named, the term "paint" is to be understood as encompassing all similar terms such as enamel, lacquer, shellac, varnish, and the like. Most of those so far known utilize a combination of carbonate and/or acid carbonate salts with an acidic material that is prevented from coming into contact with the carbonate even when mixed with it at normal ambient temperatures, but that is brought into contact by some mechanical and/or chemical means when the temperature of the solid containing both components is raised, most often by contact with hot water and/or steam. The re¬ sulting reaction between acid and carbonate generates carbon dioxide gas that causes the coating to rupture and in principle to fall off the coated surface, or at least to become re¬ movable by light mechanical action. These thermally removable barrier coatings have diminished the labor and/or ma- terial costs compared with those of previous methods of removing protective barrier coatings, but in practice have been found to have certain difficulties: Complete removal is sometimes not reliably achieved; the paint accumulated on the barrier coating surface often becomes detached during the removal process, so that it can redeposit on the surface intended to be protected from being coated with it; pieces of the coating after release can all too readily become trapped in the structure having the surface to be protected from paint, particularly when this structure has relatively narrow spacings be¬ tween solid elements, as is true in the grates conventionally used in paint spray booths; and the internal barrier materials that prevent contact between carbonate ions and acid materials at ambient temperatures can become unstable or otherwise suffer faults that cause premature removal and or unreliable or incomplete removal when desired. DESCRIPTION OF THE INVENTION Objects of the Invention A major object of the invention is to provide a new type of thermally releasable barrier coating that will overcome or at least ameliorate some or all of the problems with prior art thermally releasable barrier coatings as described above. Other objects will be apparent from the description below. General Principles of Description Except in the claims and the specific examples, or where otherwise expressly in¬ dicated, all numerical quantities in this description indicating amounts of material or con- ditions of reaction and/or use are to be understood as modified by the word "about" in describing the broadest scope of the invention. Practice within the numerical limits stat¬ ed is generally preferred, however. Also, unless expressly stated or necessarily implied by the context to the contrary: percent, "parts of, and ratio values are by weight; the term "polymer" includes "oligomer", "copoiymer", "terpolymer", and the like; the first definition or description of the meaning of a word, phrase, acronym, abbreviation or the like applies to all subsequent uses of the same word, phrase, acronym, abbreviation or the like and applies, mutatis mutandis, to normal grammatical variations thereof; the description of a group or class of materials as suitable or preferred for a given purpose in connection with the invention implies that mixtures of any two or more of the mem¬ bers of the group or class are equally suitable or preferred; specifications in chemical terms of materials in compositions refers to the materials at the time of addition to any composition so specified, and does not necessarily exclude the possibility of reaction between such materials with other materials already present in the composition at the time of addition of the specified materials; specification of materials in ionic form im¬ plies the presence of sufficient counterions to produce electrical neutrality for the compo¬ sition as a whole; and any counterions thus implicitly specified preferably are selected from among other constituents explicitly specified in ionic form, to the extent possible; otherwise such counterions may be freely selected, except for avoiding counterions that act adversely to the objects of the invention. Summary of the Invention It has been discovered that a combination of (A) a nitrogen containing water solu- ble polymer, (B) a water insoluble film forming polymer, and (C) gas filled, polymer walled microballoons provides a superior thermally releasable coating that, at least in its most preferred embodiments, (i) can be conveniently and reliably coated from a water based solution and dispersion onto surfaces to be protected against painting, (ii) is reliab¬ ly stable at ambient temperatures, (iii) even after being coated with many times its own thickness of accumulated paint particles, rapidly disintegrates, along with the accumulat¬ ed paint coating formed on it, upon contact with hot water, into particles small enough that they readily escape from standard paint booth grate structures, (iv) normally detacki- fies any initially tacky paint particles that might escape during distintegration of the com¬ bined thermally releasable coating and paint residues accumulated thereon, and (v) dis- integrates into particles that float on water, so that they can be readily removed from the grates by immersing the latter in hot water, allowing a few minutes for the disintegration to take effect, and then skimming of the floating solids on the surface of the water. A polymer is defined as "film forming" for the purposes of this description if, when a solution or suspension of the polymer in water is dried at a temperature of at least 25° C from a liquid film thickness not greater than 1 millimeter, a continuous and coher¬ ent film that is solid at 25° C is produced. One major embodiment of the invention is a suitable liquid coating composition for applying a thermally releasable barrier coating, the liquid coating composition com¬ prising, preferably consisting essentially of, or more preferably consisting of, water and: (A) a component of water soluble polymer material that (i) is solid at 25 °C, (ii) con¬ tains at least, with increasing preference in the order given, 1, 2, 4, 7, 10, 13, 15, 17, or 18.0 percent of nitrogen atoms bonded into a chemical moiety selected from the group consisting of amido and quaternary ammonium moieties, and (iii) is soluble in water to an extent of at least 5 % at 25 °C and normal atmospheric pressure; (B) a component of film forming polymer that is not soluble in water to an extent of as much as 4.5 % at 25 °C and normal atmospheric pressure but is stably dis¬ persed in the coating composition; and; (C) a component of gas filled, polymer walled microballoons having the properties that (i) they are stably dispersed in the coating composition and remain stably dis¬ persed and substantially unexpanded when the coating composition is maintained at a temperature not greater than 65 °C; and (ii) when exposed for at least five minutes to at least one temperature in the range from 80 to 95 °C, they undergo an irreversible expansion, without wall rupture, so as to produce an expanded form which has a density not greater than 0.5 times their density before having expanded; and, optionally, one or more of the following components: (D) a component of viscosity modifying agent(s) that are not part of any of the previ¬ ously recited components; (E) a component of solid filler that is not part of any of the previously recited com¬ ponents; (F) a component of dispersing agent that is not part of any of the previously recited components; (G) a component of pH adjusting agent and/or corrosion inhibitor that is not part of any of the previously recited components; (H) a component of coloring agent that is not part of any of the previously recited components; and (J) a component of biocide that is not part of any ofthe previously recited compon¬ ents, said liquid coating composition having the properties that it can be formed into a liquid coating over a solid substrate surface and that the thus-formed liquid coating can be con¬ verted, by heating the liquid film in place on the substrate to a temperature not greater than 65 °C under normal atmospheric pressure for a time not greater than one hour, into a coherent continuous solid coating that adheres to the substrate . Another embodiment ofthe invention is a process comprising, preferably consist¬ ing essentially of, or more preferably consisting of, the steps of: (I) forming on a substrate surface to be protected against accumulation of paint thereon a liquid coating of a liquid coating composition according to the inven¬ tion as described above, said liquid coating having a thickness corresponding to at least a thickness of 12 micrometres (hereinafter usually abbreviated as "μm") of constituents ofthe liquid coating composition that remain present after the li¬ quid coating is heated to 65 °C for at least one hour; and (II) drying the liquid coating formed in step (I), while said coating is in place over the substrate surface as formed in step (I), for a sufficient time at a sufficient temper- ature to convert the liquid coating to a solid adherent coating over those portions ofthe substrate surface that were provided with a liquid coating in step (I), with¬ out causing irreversible expansion of the gas filled, polymer walled microbal¬ loons present in the solid coating; and, optionally, one or more ofthe following steps: (HI) causing the accumulation of paint residues on the solid coating formed in step (II) so as to form a soiled surface; (IV) immersing the soiled surface formed in step (III) in a volume of water at a tem¬ perature at least high enough to cause irreversible expansion ofthe gas filled, pol¬ ymer walled microballoons in the coating formed in step (II); and (V) skήrjTning from the top surface of the volume of water in which the soiled surface was immersed in step (IV) any floating solid particles formed by disintegration in step (IV) ofthe coating formed in step (H), as a consequence ofthe irreversible expansion ofthe gas filled, polymer walled microballoon constituents thereof. Other embodiments of the invention include coated substrates prepared by a process according to the invention as described above, the use of such coated substrates as grates in paint spray booths, and the like. Detailed Description ofthe Invention. Including Preferred Embodiments One ofthe important functions of component (A) as identified above is to provide detackifying activity for paint residues. Component (A) is preferably selected from poly¬ mers of amide(s) of unsaturated carboxylic acids, more preferably of acrylic or metha¬ crylic acid, still more preferably of polyacrylamide only. The concentration of compon- ent (A) in a working composition according to the invention preferably is at least, with increasing preference in the order given, 1.0, 2.0, 3.0, 3.5, 4.0, 4.5, 4.8, 5.2, 5.5, 5.8, or 6.0 % and independently preferably is not more than 30, 25, 20, 15, 10, 9.0, 8.5, 8.0, 7.5, 7.3, 7.1, 6.9, 6.7, 6.5, 6.3, or 6.2 %. Component (B) may be selected from a wide variety of water insoluble polymers, preferably, primarily for reasons of economy, those commercially available in the form of dispersions or latexes. An especially preferred polymer type is copolymers of (i) vinyl esters of carboxylic acids with not more than four carbon atoms per acid molecule, most preferably vinyl acetate and (ii) at least one ofthe group consisting of acrylic and metha¬ crylic acids and esters of acrylic and methacrylic acids, with esters being prefeπed and esters formed with alcohols containing not more than four carbon atoms still more pre¬ ferred. Independently of its chemical composition, the concentration of component (B) in a working composition according to the invention preferably is at least, with increas¬ ing preference in the order given, 1.0, 2.0, 3.0, 3.5, 4.0, 4.5, 4.9, 5.3, 5.7, 6.1, 6.3, 6.5, or 6.6 % and independently preferably is not more than 30, 25, 20, 15, 10, 9.0, 8.5, 8.0, 7.5, 7.3, 7.1, 6.9, or 6.8 %. For both components (A) and (B), smaller concentrations than those noted as pre¬ ferred generally result in a need for multiple coating steps and/or high concentrations of viscosity increasing agents, which are relatively expensive compared with most other components of a composition according to the invention, in order to achieve a desirable final film thickness after drying, while higher concentrations than those noted above as preferred are likely to result in a coating thickness in a single pass that is higher than nec¬ essary to accomplish the purpose ofthe invention and therefore are uneconomical. Ex- cessively thick coatings also might unduly reduce the space available between the ele¬ ments of a grate to be coated, thereby frustrating its intended permeability to liquids. Furthermore, high concentations of component (A) substantially increase the viscosity of an aqueous mixture containing them, thereby aggravating a tendency to excessively thick coatings. In order to achive highly desirable properties in the films formed, it is preferred that the ratio, in a composition according to the invention, of component (B) to compon¬ ent (A), which are the two principal binder constituents ofthe composition, should be at least, with increasing preference in the order given, 0.30: 1.0, 0.40: 1.0, 0.50: 1.0, 0.60: 1.0, 0.70: 1.0, 0.80:1.0, 0.90:1.0, 0.95: 1.0, 1.00:1.0, 1.05:1.0, or 1.09:1.0 and independently preferably should be no more than, with increasing preference in the order given, 4.0: 1.0, 3.5:1.0, 3.0:1.0, 2.5:1.0, 2.0: 1.0, 1.7:1.0, 1.5:1.0, 1.3:1.0, 1.2:1.0, or 1.15:1.0. If the ratio of component (B) to component (A) is substantially higher than these preferred values, the coatings formed are not likely to dislodge themselves readily from the underlying substrate even after having been heated. Also, even if adequate dislodgement does occur, still tacky particles of paint may be redispersed in the water often used to heat the coating according to the invention in order to dislodge it, and these tacky paint particles may re- deposit on unprotected surfaces before the surfaces can be recoated with a protective bar¬ rier. On the other hand, if the ratio of component (B) to component (A) is substantially lower than the preferred values, the barrier coating formed may dissolve too readily in low temperature water, with which they are usually in contact when in use, thereby re¬ quiring uneconomically frequent replacement of the barrier coating. For component (C), suitable materials are commercially available from Expancel Inc., a subsidiary of Akzo Nobel, in Duluth, Georgia, USA under the name EXPAN- CEL™ unexpanded microballoons. Both wet unexpanded ("WU") and dry unexpanded ("DU") grades are available and appear to be equally useful in a composition according to the invention. Preferably, the average diameter, before expansion by heating, ofthe microballoons used is not more than, with increasing preference in the order given, 100, 70, 50, 40, 30, 25, or 20 μm and independently preferably is at least, with increasing preference in the order given, 3.0, 4.0, 5.0, 6.0, 7.0, 8.0, 9.0, or 10.0 μm. Smaller micro¬ balloons than these preferred minimum sizes may not generate sufficient force upon ex¬ pansion to rupture the coating as desired, while larger microballoons than the preferred maximum sizes are more difficult to disperse uniformly into coatings ofthe most desir¬ able thickness. Independently, the amount of component (C) in a working composition according to the invention preferably is at least, with increasing preference in the order given, 1.0, 2.0, 3.0, 3.5, 4.0, or 4.5 % and independently preferably is not more than, with increasing preference in the order given, 20, 15, 10, 8.0, 7.0, 6.5, 6.0, 5.5, or 5.1 %. A working liquid substrate coating composition according to this invention pref¬ erably is highly thixotropic, i.e., it preferably has a relatively high viscosity when begin¬ ning to be disturbed from a motionless state, but becomes relatively low in viscosity when subjected to stronger forces, so that it may readily be applied by convenient meth- ods such as spraying, dipping, brushing, and the like to a substrate to be protected, to form a coating that will remain in place against the influence of natural gravity without becoming thinned to an undesirable degree. The thixotropy may conveniently be mea¬ sured by means of a well known type of instrument, a Brookfield viscometer, using spindle # 4. The viscosity at 25 °C of a liquid working coating compostion according to the invention measured in this way, when measured at 1 revolution per minute (hereinaft¬ er abbreviated as "rpm") preferably is at least, with increasing preference in the order given, 3000, 5000, 7000, 9000, 10,000, 11,000, 12,000, 12,500, 13,000, or 13,500 centi- poises (hereinafter abbreviated as "cps"); independently preferably is, when measured at 5 rpm, at least, with increasing preference in the order given, 2000, 2250, 2500, 2750, 3000, 3250, 3500, 3750, 4000, 4200, 4400, 4600, 4800, or 4900, cps; and also independ¬ ently preferably is, when measured at 20 rpm, not more than, with increasing preference in the order given, 6000, 5000, 4000, 3750, 3500, 3250, 3000, 2750, 2500, or 2250 cps. Achieving the most preferred viscosities as described above normally requires the use of optional component (D) as recited above, because components (A) through (C) do not normally spontaneously form compositions with the most preferred thixotropic prop¬ erties. A wide variety of natural and synthetic materials, such as natural gums and other polysaccharides and various synthetic polymers, are known in the art for achieving thix¬ otropy and may be used in a composition according to the invention. The most preferred material for component (D) when used is xanthan gum, preferably a type of this gum which has been modified from its natural state to result in smoother flow properties at low shear rates. For any viscosity modifying component, the amount preferably should be selected to achieve preferable values of viscosities at various measuring speeds as al- ready specified above. For the preferred modified xanthan gum as noted above, along with other preferred types and amounts of components (A) through (C), the concentration ofthe modified xanthan gum in a liquid coating composition according to the invention preferably is at least, with increasing preference in the order given, 0.20, 0.30, 0.40, 0.50, 0.55, or 0.57 % and independently preferably is not more than, with increasing prefer¬ ence in the order given. 1.5, 1.0, 0.90, 0.80, 0.70, 0.65, 0.60, or 0.58 %. The presence of optional component (E) in a composition according to the inven¬ tion is normally preferred, because such presence in a suitable amount has been found to facilitate a desirable fracture and dislodgment ofthe coating after expansion of com- ponent (C). When the filler has a specific gravaity of 2.7, the amount of filler in a liquid working coating composition according to the invention preferably is at least, with in¬ creasing preference in the order given, 2, 5, 8, 10, 1 1.0, 12.0, 13.0, 14.0, 14.5, 15.0, or 15.5 % of the total amount of components (A) and (B) and independently preferably is not more than, with increasing preference in the order given, 50, 45, 40, 35, 30, 25, 22, 20, 18, 16.8, 16.2, or 15.7 % of the total amount of components (A) and (B). If the specific gravity ofthe filler is different, the preferred values should be adjusted to give the same volume of filler as the preferences stated above for fillers with a specific gravity of2.7. Independently of the other preferences, the maximum particle size of the filler when used preferably is not more than, with increasing preference in the order given, 100, 75, 50, 40, 30, 25, 22, 20, 18, or 16 μm and independently the particle size preferab¬ ly is at least, with increasing preference in the order given, 2, 3, 4, 5, 6, 7, 8, 9, or 10 μm for at least 10 %, or more preferably, with increasing preference in the order given, for at least 20, 30, 40, 50, 60, 70, 80, or 90 % ofthe total amount of filler. The chemical nature of the filler is not believed to be significant to the success of the invention, provided that there is little or no chemical reaction between the filler and other components and that the filler is not soluble to an extent of as much as 1 % of its total in water. Any ofthe conventional insoluble mineral fillers such as talcs, clays, carbonates, and the like is suitable, with talc preferred. The presence of optional component (F) is also normally preferred, because it has been found difficult uniformly to disperse microballoon component (C) and sometimes also filler component (E) when used into a working liquid coating composition according to the invention when no surfactant dispersing agent is present. Any of a wide variety of dispersing agents generally known in the art is suitable if it leads to effective disper¬ sion and stability ofthe resulting final working coating composition. A preferred type of dispersing agent is one having general chemical formula (I): R'O(CH 2 CH 2 O) v (CH 2 CHCH 3 O) z H (I) where R' is a moiety selected from the group consisting of saturated-and-unsaturated straight-and-branched-chain-aliphatic-monovalent-hydrocarbon-moiety-substituent - bearing phenyl moieties in which the aromatic ring is directly bonded to the oxygen atom appearing immediately after the R 1 symbol in formula (II); y is a positive integer, and z is zero, one, or two. Preferably, independently for each preference stated, z is 1 or 0, more preferably zero; the aliphatic monovalent hydrocarbon moiety substituent in R 1 has at least, with increasing preference in the order given. 5, 6, 7, 8, or 9 carbon atoms and independently preferably has not more than, with increasing preference in the order giv¬ en, 12, 11, 10, or 9 carbon atoms; the aliphatic monovalent hydrocarbon moiety substitu- ent in R 1 is straight chain rather than branched; and the average value of y is at least, with increasing preference in the order given, 3, 4, 5, 6, 7, or 8 and independently preferably is not more than, with increasing preference in the order given, 16, 15, 14, 13, 12, 1 1, 10, or 9. The pH value of a liquid working coating composition according to the invention, at least when the substrate metal to be coated is mild steel, preferably is at least, with in¬ creasing preference in the order given, 5.0, 6.0, 6.5, 7.0, 7.5, 8.0, 8.3, or 8.6 and inde¬ pendently preferably is not more than, with increasing preference in the order given, 12, 11, 10, or 9.5. Lower pH values than those noted as preferable minimums may result in excessive corrosion ofthe substrate, or even failure to form a coating at all, while higher pH values than those noted as preferred maximums may adversely affect the properties of the other constituents of a working coating composition according to the invention. Inasmuch as components (A) through (F) alone would often result in pH values below those preferred, an alkaline pH adjusting agent is generally preferably present as optional component (G) in a liquid coating composition according to the invention. Because they have an inherent corrosion inhibiting effect in addition to their pH raising effect, water soluble organic amines are prefeπed for component (G) when an increase in pH is need¬ ed, and, primarily in order to minimize odor nuisances, relatively non-volatile amines such as mono-, di-, and, particularly, tri-ethanol amines are especially preferred. Should a decrease in pH be needed, many suitable acid materials to serve as pH adjusting agents are known to those skilled in the art. Optional colorant component (H) is not believed to have any important technical function in the operation ofthe invention, but may be desirable in many applications for decorative or visibility-increasing purposes. Numerous conventional dyes and/or pigments may be used for component (H) as known to those skilled in the art. Optional biocidal component (J) normally is preferably present in a liquid compo¬ sition according to the invention in an amount effective to repress the biodegradation of some ofthe components of the composition, especially component (A), that otherwise readily occurs from the action of micro-organisms commonly found in the natural atmos¬ phere. The liquid coating initially formed may be adquately dried by mere exposure to normal ambient air at a humidity less than 100 %. However, because several hours may be required for drying by this method, it is normally preferred to utilize hot air for drying. More particularly, air used to dry the liquid coating initially formed preferably has a temperature that is at least, with increasing preference in the order given, 38, 43, 48, 53, 57, or 60 °C and independently preferably is not more than, with increasing preference in the order given, 75, 72, 69, or 67 °C; higher temperatures than these will substantially increase the risk of unwanted premature irreversible expansion ofthe microballoons in the coating, and achieve only slightly greater drying speeds, as shown in some of the working examples below. In order to achieve the most desired characteristics, a dried but unexpanded pro¬ tective coating according to the invention preferably has a thickness that is at least, with increasing preference in the order given, 12, 15, 18, 21, 24, 27, or 30 μm and independ¬ ently preferably is, primarily for reasons of economy, not more than 100, 75, 65, 55, 45, or 35 μm. Also, of course, when used on grates, coatings according to the invention nor¬ mally should not be so thick as to make the grates impermeable to fluids. When a dried coating according to the invention has accumulated a sufficient amount of paint on its surface, the coating is preferably caused to break apart and dislodge itself from the substrate by immersion in hot water, although spraying of hot water and/or steam, hot air, or other methods of heating can also be used. Hot water is prefeπed when practical, because heat transfer from it to the coating is relatively efficient and dislodgement and separation are facilitated by the fact that the coating, at least if it is one of the most preferred embodiments, will float on water after the irreversible expansion of the microballoons occurs, but not before. In particular, hot water with a temperature that preferably is at least, with increasing preference in the order given, 80, 82, 84, 86, 88, 90, or 92 °C is used. Although the use of still higher temperature water has no adverse effect on the break up and dislodgement ofthe coating, it does not provide much if any practically higher break up and dislodgement speed and does require a higher energy cost. Therefore, when hot water is used for this purpose, its temperature independently preferably is not more than, with increasing preference in the order given, 98, 96, or 94 °C. If steam, air, or another purely gaseous heat transfer medium is used, substantially higher temperatures than these for the heat transfer medium are preferred to compensate for the relatively slow heat transport capacity of a gas. Highly preferred coatings according to the invention break apart within a few minutes when immersed in hot water at a preferred temperature and float to the top ofthe vessel in which they are immersed, thereby making possible a facile separation by skim¬ ming off the broken particles formed. Any tacky paint that may separate during the breakup and dislodgement process normally is detackified by residual components (A) and (B) ofthe coating. Component (A) has the major detackifying effect, but component (B) also aids in detackification by forming water-insoluble particles that stick to tacky paint surfaces and thereby reduce the effectively tacky area of any originally tacky sur¬ face. As a consequence of the combined action of these two components, the skimmed particles of the coating do not stick readily to any other surfaces with which they may come into contact. Therefore, after broken up particles of the coating have been skimmed off the surface of hot water in which a coated substrate according to the inven¬ tion was immersed to break up the coating, the substrate may normally be removed from the hot water, dried, and then recoated with a coating composition according to the in¬ vention for continued use, and such coating and dislodgement cycles may be continued as many times as desired on the same substrate. The invention may be further appreciated by consideration ofthe following ex¬ amples, and its benefits may be appreciated by comparison with other methods. Examples Materials Used CYANAMER™ N-100L polyacrylamide solution in water, reported by its supplier to contain 50 - 52 % of polyacrylamide, was obtained commercially from Cytek Industries. FLEXBOND™ 325 latex dispersion of a copoiymer of vinyl acetate and acrylate, reported by its supplier to contain 55.8 % solids of a polymer with a glass transition temperature of 15 °C dispersed in water, was obtained commercially from Air Products and Chemicals. EXPANCEL™ 642 WU and 820 DU grades of gas filled microballoons were obtained commercially from Expancel Inc. as noted above. Grade 642 WU is reported by its supplier to contain 65 % of microballoons with diameters ranging from 3 to 30 μm, with the balance of the material being water in which the microballoons are dispersed; grade 820 DU is reported by its supplier to be 100 % microballoons with diameters ranging from 10 to 16 μm. For both grades, the filling gas is reported to be iso-butane and the polymer walls to be made of acrylonitrile-vinylidene chloride copoiymer. KELZAN™ AR xanthan gum powder was commercially obtained from the Kelco division of Merck & Co., Inc. and is reported by its supplier to contain 86 - 92 % solids of xanthan gum (which is constituted of polymers of β-1 ,4-linked D-glucose units) that has been modifed to give lower viscosity at low shear rates than unmodified natural xan¬ than gum. For example, a solution of 0.3 % of each of potassium chloride and KEL¬ ZAN™ AR in water has a viscosity of about 800 cps at a shear rate of 0.1 reciprocal sec¬ onds (hereinafter usually abbreviated as "sec "1 "), whereas an otherwise identical solution of natural xanthan gum has a viscosity of almost 10,000 cps. At a shear rate of 10 sec "1 , the viscosities of these solutions are about 100 and 500 cps respectively. K8C241 ™ un¬ modified xanthan gum was also obtained commercially from Kelco. NATROSOL™ 250H4R hydroxyethylcellulose was obtained commercially from Aqualon, a division of Hercules, Inc., in Wilmington, Delaware, U.S.A. and is reported by its supplier to have a molecular weight, estimated from intrinsic viscosity measure- ments, of 1.1 x 10 6 ; a solution of 1 % of it in water is reported by its supplier to have a viscosity of 2600 - 3300 cps at 25 °C when measured with a Brookfield viscometer using spindle #3 at 30 rpm. MICROTALC™ MP 15-38 filler was commercially obtained from Marietta Min¬ erals, Dillon, Montana and is reported by its supplier to be a mined magnesium silicate mineral with a maximum particle size of 15 μm and the chemical formula Mg 3 H 2 (SiO 3 ) 4 . IGEPAL™ CO-630 surfactant was obtained commercially from Rhόne-Poulenc and is reported by its supplier to be nonylphenol[poly(oxyethylene)]ethanol with an average molecular weight of 616. BUTOXYNE™ 497 corrosion inhibitor was obtained commercially from ISP Technologies, Inc., Wayne, New Jersey, USA and is reported by its supplier to be 1,4- bis(2-hydroxyethoxy)-2-butyne. HOSTACOR™ 2732 inhibitor was obtained commercially from Hoechst Celan- ese Corp. and is reported by its supplier to be "alkylamido carboxylic acid". Triethanol amine, 99 % pure, was used as a pH adjusting agent and corrosion in¬ hibitor. DOWICIDE™ A Flake antimicrobial was obtained commercially from Van Waters and Rogers, Kirkland, Washington, USA and is reported by its supplier to contain 97 % of sodium orthopheynylphenate tetrahydrate and 1 - 2 % of sodium hydroxide. UNISPERSE™ Blue pigment was obtained commercially from Ciba-Geigy as a paste. CELOGEN™ 780 was obtained commercially from Uniroyal Chemicals and is reported by its supplier to be "activated" azodicarbonamide. This is a conventional blow¬ ing agent. Working Coating Compositions Example working compositions according to the invention are set forth in Table 1 below. Blank cells in the table indicate that none ofthe material was added to the com- position, or that the property value that would properly appear in the cell was not measured. (Only the first three digits ofthe viscosity measurements are considered sig¬ nificant within the limits of reproducibility of the measurements; the final zeros are shown merely for the sake of reporting in the most conventional units.) TABLE 1 Material % of Material in Composition Number 1 2 3 4 5 6 7 Deionized Water 72 74 74 74.2 69.2 70.2 70.0 DOWICIDE™ A Flake 0.10 0.10 0.10 0.10 0.10 KELZAN™ AR 0.6 0.6 0.7 0.65 0.65 0.65 0.80 NATROSOL™ 250H4R K8C241™ CYANAMER™ N-100L 10.0 10.0 10.0 10.0 10.0 10.0 10.0 FLEXBOND™ 325 10.0 10.0 10.0 10.0 10.0 10.0 10.0 IGEPAL™ CO-630 1.00 1.00 1.00 1.00 1.00 1.00 1.00 MICROTALC™ MP 15-38 CELOGEN™ 780 2.00 2.00 EXPANCEL™ 642 WU 6.00 6.00 5.00 6.00 EXPANCEL™ 820 DU 4.00 4.00 4.00 HOSTACOR™ 2732 2.00 BUTOXYNE™ 497 2.00 99% Triethanolamine 2.00 2.00 2.00 UNISPERSE™ Blue 0.10 0.10 0.10 0.01 0.10 0.10 0.10 Other Properties of the Magnitude of the Property in Composition Number: Compositions 1 2 3 4 5 6 7 Viscosity' at 20 rpm, cps 1770 1770 1720 1710 1920 1880 2680 Viscosity 1 at 5 rpm, cps 4000 3720 7040 Viscosity 1 at 1 rpm, cps 12,400 10,200 22,400 pH 5.1 5.0 9.0 9.1 5.6 5.6 9.0 'The viscosity was measured at 25 °C with a Brookfield Viscometer, using Spindle # 4. Table I is continued on the next page . Material % of Material in Composition Number 8 9 10 11 12 13 14 Deionized Water 72.0 64.5 66.5 62.6 67.6 62.5 64.5 DOWICIDE™ A Flake 0.10 0.10 0.10 0.10 0.10 0.10 0.10 KELZAN™ AR 0.80 0.80 0.80 0.75 0.75 NATROSOL™ 250H4R 0.50 0.50 K8C241™ 0.30 0.30 CYANAMER™ N-100L 10.0 12.0 12.0 12.0 12.0 12.0 12.0 FLEXBOND™ 325 10.0 12.0 12.0 12.0 12.0 12.0 12.0 IGEPAL™ CO-630 1.00 0.50 0.50 0.50 0.50 0.50 0.50 MICROTALC™ MP 2.00 2.00 2.00 2.00 15-38 CELOGEN™ 780 EXPANCEL™ 642 WU 7.00 7.00 7.00 EXPANCEL™ 820 DU 4.00 5.00 5.00 5.00 HOSTACOR™ 2732 BUTOXYNE™ 497 99% Triethanolamine 2.00 3.00 3.00 3.00 3.00 3.00 UNISPERSE™ Blue 0.10 0.10 0.10 0.10 0.10 0.10 0.10 Other Properties of the Magnitude of he Property in Composition Number: Compositions 8 9 10 11 12 13 14 Viscosity 1 at 20 rpm, cps 2400 2740 2800 3030 2530 4400 4370 Viscosity 1 at 5 rpm, cps 6160 7480 7920 9240 6880 1 1 ,600 12,000 pH 9.0 9.0 9.0 8.8 9.1 9.1 9.1 Viscosity 1 at 1 rpm, cps 19,000 23,800 25,600 30,800 21,200 29,000 30,600 'The viscosity was measured at 25 °C with a Brookfield Viscometer, using Spindle # 4. Table I is continued on the next page . Material % of Material in Composition Number 15 16 17 18 19 20 Deionized Water 64.6 66.6 62.7 64.7 62.6 64.7 DOWICIDE™ A Flake 0.10 0.10 0.10 0.10 0.10 0.10 KELZAN™ AR 0.65 0.65 0.60 0.60 0.65 0.65 NATROSOL™ 250H4R K8C241™ CYANAMER™ N-100L 12.0 12.0 12.0 12.0 12.0 12.0 FLEXBOND™ 325 12.0 12.0 12.0 12.0 12.0 12.0 IGEPAL™ CO-630 0.50 0.50 0.50 0.50 0.50 0.50 MICROTALC™ MP 2.00 2.00 2.00 2.00 15-38 CELOGEN™ 780 EXPANCEL™ 642 WU 7.00 7.00 7.00 EXPANCEL™ 820 DU 5.00 5.00 5.00 HOSTACOR™ 2732 BUTOXYNE™ 497 99 % Triethanolamine 3.00 3.00 3.00 3.00 3.00 3.00 UNISPERSE™ Blue 0.10 0.10 0.10 0.10 0.10 0.10 Other Properties of the Magnitude of the Property in Composition Number: Compositions 15 16 17 18 19 20 Viscosity 1 at 20 rpm, cps 2000 1840 1790 1770 2010 1900 Viscosity 1 at 5 rpm, cps 5360 4240 4520 4400 5600 4920 Viscosity 1 at 1 rpm, cps 9200 10,400 9200 15,400 13,600 pH 9.2 9.2 9.2 9.1 9.1 9.1 'The viscosity was measured at 25 °C with a Brookfield Viscometer, using Spindle # 4. Use Examples Each working composition defined in Table 1 was coated over a sample of con¬ ventional grate plate material for spray paint booths to produce a coating with a wet thickness of about 0.20 millimeters. The coating was then dried at a temperature of 60 °C for a time of 20 minutes to produce a dry coating according to the invention. Various kinds of paint were caused to accumlate on the thus coated samples, by exposing them to a laboratory scale paint spray booth, until the coating of paint in its thickest parts was about 0.51 millimeters thick. The coated samples were men immersed in water at a tem¬ perature of 93 °C. Within 30 seconds, breakup and dislodgement ofthe coating could be observed, and this process was completed within 90 seconds. The particles formed by breakup ofthe protective coating according to the invention and the paint adhered to it were skimmed off the top of the water in which the breakup of the coating had oc¬ curred. The vessel was then emptied and the previously coated metal substrate samples removed. No adherent paint on either the previously coated metal substrate samples or the walls ofthe vessel in which breakup ofthe coatings had occurred was observed. Time and Temperature Variations for Drying Wet Coatings According to the Invention In this group of examples, numerous coated samples of conventional grate material were prepared with a wet coating thickness of about 0.20 millimeters of Composition No. 20 as shown in Table 1 and subjected to drying conditions as shown in Table 2 below, with the results also shown in Table 2. At the same time as the coated substrates were being exposed to drying conditions as reported in Table 2, a small aluminum pan with a thin layer of the coating composition was exposed to the same drying conditions. Any visually perceptible roughening ofthe layer of coating, bubbles in the layer, irregularities in thickness, or the like was regarded as evidence of the beginning of irreversible expansion ofthe microballoons, which of course is not desired at this stage of a process according to the invention. TABLE 2 Tem¬ Time of Exposure to Temperature, Minutes: pera¬ ture, °C 10 20 30 40 50 60 70 21 VW VW W W W W ex. W ex.E. E. 32 VW w W ex. E. D ex Dr. CD CD CD 43 W ex. E. 90 % D CD CD CD CD CD 54 90 % W 90 % D CD CD CD CD CD 66 75 % W CD CD CD CD CD CD 77 80 % D CD* CD* CD* CD* CD* CD* 88 CD* CD* CD* CD** CD** CD** CD** Abbreviations and Notes for Table 2 VW = very wet; W = wet; ex. E. = except at edges; D = dry; ex. Dr. = except for a few wet drops; CD = completely dry; percentages are estimated area percents; * indicates that there was visual evidence of at least the beginning of expansion ofthe microballoons in the pan sample ofthe coating composition, but not in the coating on the grate samples; * * indicates that there was visual evidence of at least the beginning of expansion of microballoons in both the pan sample and the coating on the grate substrates; at 21 °C, which was the ambient temperature in the laboratory at the time ofthe tests, the relative humidity was 65 %; at other temperatures, the relative humidity was whatever resulted from heating air at the ambient temperature and humidity to the temperatures shown, without any added water.

Claims: The invention claimed is: 1. A liquid coating composition suitable for applying to a solid surface for produc¬ ing a thermally releasable barrier coating on the surface, said liquid coating composition consisting essentially of water and: (A) a component of water soluble polymer material that (i) is solid at 25 °C, (ii) con¬ tains at least 1 percent of nitrogen atoms bonded into a chemical moiety selected from the group consisting of amido and quaternary ammonium, and (iii) is solu¬ ble in water to an extent of at least 5 % at 25 °C and normal atmospheric pressure; (B) a component of film forming polymer that is not soluble in water to an extent of as much as 4.5 % at 25 °C and normal atmospheric pressure but is stably dis¬ persed in the coating composition; and; (C) a component of gas filled, polymer walled microballoons having the properties that (i) they are stably dispersed in the coating composition and remain stably dis- persed and substantially unexpanded when the coating composition is maintained at a temperature not greater than 65 °C; and (ii) when exposed for at least five minutes to at least one temperature in the range from 80 to 95 °C, they undergo an iπeversible expansion, without wall rupture, so as to produce an expanded form which has a density not greater than 0.5 times their density before having expanded; and, optionally, one or more of the following components: (D) a component of viscosity modifying agent(s) that are not part of any of the previ¬ ously recited components; (E) a component of solid filler that is not part of any ofthe previously recited com¬ ponents; (F) a component of dispersing agent that is not part of any ofthe previously recited components; (G) a component of pH adjusting agent and/or coπosion inhibitor that is not part of any of the previously recited components; (H) a component of coloring agent that is not part of any of the previously recited components; and (J) a component of biocide that is not part of any ofthe previously recited compon¬ ents, said liquid coating composition having the property that it can be formed into a liquid coating over a metal or plastic substrate solid surface and the thus-formed liquid coating can be converted, by heating the liquid film in place on the substrate to a temperature not greater than 65 °C under normal atmospheric pressure for a time not greater than one hour, into a coherent solid coating that adheres to the substrate . 2. A composition according to claim 1 , wherein, with all percentages based on the total composition unless otherwise stated: component (A) is present in an amount from about 1.0 to about 30 %; component (B) is present in an amount from about 1.0 to about 30 %; components (B) and (A) are jointly present in amounts having a ratio of the amount of component (B) to the amount of component (A) that is from about 0.30: 1.0 to about 4.0: 1.0; the microballoons of component (C) have an average diameter between about 3 and about 100 μm; the amount of component (C) is from about 1.0 to about 20 %; and the composition has a viscosity that is at least 3000 cps when measured at 1 rpm, at least 2000 when measured at 5 rpm, and not more than 6000 when measured at 20 rpm. 3. A composition according to claim 2, wherein: the amount of component (A) is from about 2.0 to about 25 %; the amount of component (B) is from about 2.0 to about 25 %; the ratio of component (B) to component (A) is from about 0.40:1.0 to about 3.5:1.0; the microballoons of component (C) have an average diameter between about 4 and about 70 μm; the amount of component (C) is from about 2.0 to about 15 %; the viscosity ofthe composition is at least 4000 cps when measured at 1 rpm, at least 2250 when measured at 5 rpm, and not more than 5000 when measured at 20 rpm; and component (E) is present in a volume that coπesponds in mass to from about 5 to about 50 % ofthe total of components (A) and (B) for a solid with a specific gravity of 2.7. 4. A composition according to claim 3, wherein: component (A) is selected from the group consisting of polymers of amides of unsaturated carboxylic acids; the amount of component (A) is from about 3.0 to about 20 %; component (B) is selected from the group consisting of copolymers of (i) vinyl esters of carboxylic acids with not more than four carbon atoms per molecule and (ii) at least one ofthe group consisting of acrylic and methacrylic acids and esters of both these acids; the amount of component (B) is from about 3.0 to about 20 %; the ratio of component (B) to component (A) is from about 0.50: 1.0 to about 3.0: 1.0; the microballoons of component (C) have an average diameter between about 5 and about 50 μm; the amount of component (C) is from about 3.0 to about 10 %; the viscosity of the composition is at least about 7000 cps when measured at 1 rpm, at least about 2500 cps when measured at 5 rpm, and not more than about 4000 cps when measured at 20 rpm; component (E) is present in a volume that coπesponds in mass to from about 8 to 45 % ofthe total of components (A) and (B) for a solid with a specific gravity of 2.7; and at least 40 % of the total amount of component (E) is made up of particles with a size between 4 and 50 μm. 5. A composition according to claim 4, wherein: the amount of component (A) is from about 3.5 to about 15 %; the amount of component (B) is from about 3.5 to about 15 %; the ratio of component (B) to component (A) is from about 0.60: 1.0 to about 2.5:1.0; the microballoons of component (C) have an average diameter between about 6 and about 40 μm; the amount of component (C) is from about 3.5 to about 8.0 %; the viscosity ofthe composition is at least about 9000 cps when measured at 1 rpm, at least about 2750 cps when measured at 5 rpm, and not more than about 3750 cps when measured at 20 rpm; component (E) is present in a volume that corresponds in mass to from 10 to 40 % ofthe total of components (A) and (B) for a solid with a specific gravity of 2.7; and at least 50 % of the total amount of component (E) is made up of particles with a size between 5 and 40 μm. 6. A composition according to claim 5, wherein: the amount of component (A) is from about 4.0 to about 10 %; the amount of component (B) is from about 4.0 to about 10 %; the ratio of component (B) to component (A) is from about 0.70:1.0 to about 2.0: 1.0; the microballoons of component (C) have an average diameter between about 7 and about 30 μm; the amount of component (C) is from about 4.0 to about 7.0 %; the viscosity ofthe composition is at least about 10,000 cps when measured at 1 rpm, at least about 3000 cps when measured at 5 rpm, and not more than about 3500 cps when measured at 20 rpm; component (E) is present in a volume that corresponds in mass to from 1 1.0 to 35 % of the total of components (A) and (B) for a solid with a specific gravity of 2.7; and at least 50 % of the total amount of component (E) is made up of particles with a size between 5 and 40 μm. 7. A composition according to claim 6, wherein: the amount of component (A) is from about 4.5 to about 9.0 %; the amount of component (B) is from about 4.5 to about 9.0 %; the ratio of component (B) to component (A) is from about 0.80:1.0 to about 1.7: 1.0; the microballoons of component (C) have an average diameter between about 8.0 and about 25 μm; the amount of component (C) is from about 4.0 to about 6.5 %; the viscosity ofthe composition is at least about 10,000 cps when measured at 1 rpm, at least about 3250 cps when measured at 5 rpm, and not more than about 3250 cps when measured at 20 rpm; component (E) is selected from the group consisting of water- insoluble mineral talcs, clays, and carbonates and is present in a volume that coπesponds in mass to from 12.0 to 30 % of the total of components (A) and (B) for a solid with a specific gravity of 2.7; and at least 60 % ofthe total amount of component (E) is made up of particles with a size between 6 and 30 μm. 8. A composition according to claim 7, wherein: the amount of component (A) is from about 4.8 to about 8.5 %; the amount of component (B) is from about 4.9 to about 8.5 %; the ratio of component (B) to component (A) is from about 0.90:1.0 to about 1.3:1.0; the microballoons of component (C) have an average diameter between about 9.0 and about 22 μm; the amount of component (C) is from about 4.0 to about 6.0 %; the viscosity ofthe composition is at least about 11,000 cps when measured at 1 rpm, at least about 3500 cps when measured at 5 rpm, and not more than about 3100 cps when measured at 20 rpm; component (E) is present in a volume that coπesponds in mass to from about 13.0 to about 25 % ofthe total of components (A) and (B) for a solid with a specific gravity of 2.7; and at least 70 % of the total amount of component (E) is made up of particles with a size between 7 and 25 μm. 9. A composition according to claim 8, wherein: the amount of component (A) is from about 5.2 to about 8.0 %; the amount of component (B) is from about 5.3 to about 7.5 %; the ratio of component (B) to component (A) is from about 0.95:1.0 to about 1.3 : 1.0; the microballoons of component (C) have an average diameter between about 9.0 and about 20 μm; the amount of component (C) is from about 4.0 to about 5.5 %; the viscosity ofthe composition is at least about 12,000 cps when measured at 1 rpm, at least about 4000 cps when measured at 5 rpm, and not more than about 3100 cps when measured at 20 rpm; component (E) is present in a volume that coπesponds in mass to from about 14.0 to about 22 % ofthe total of components (A) and (B) for a solid with a specific gravity of 2.7; and at least 80 % ofthe total amount of component (E) is made up of particles with a size between 8.0 and 20 μm. 10. A composition according to claim 8, wherein: component (A) is selected from the group consisting of polymers of acrylamide; the amount of component (A) is from about 5.8 to about 6.2 %; component (B) is selected from the group consisting of copolymers of (i) vinyl acetate and (ii) at least one of the group consisting of esters of acrylic and methacrylic acids with alcohols containing not more than four carbon atoms; the amount of component (B) is from about 6.3 to about 6.9 %; the ratio of component (B) to com¬ ponent (A) is from about 1.05:1.0 to about 1.2:1.0; the microballoons of component (C) have an average diameter between about 10 and about 20 μm; the amount of component (C) is from about 4.5 to about 5.1 %; the viscosity ofthe composition at 25 °C is at least about 13,500 cps when measured at 1 φm, at least about 4900 cps when measured at 5 φm, and not more than about 3100 cps when measured at 20 φm; component (E) is talc with a specific gravity of 2.7 and is present in an amount from about 15.0 to about 16.2 % of the total of components (A) and (B); and at least 90 % of the total amount of component (E) is made up of particles with a size between 10.0 and 16 μm. 11. A process comprising steps of: (I) forming on a substrate surface to be protected against accumulation of paint thereon a liquid coating of a coating composition according to claim 10, said liquid coating having a thickness coπesponding to from about 30 to about 35 μm of constituents ofthe liquid coating composition that remain present after the li- quid coating is heated to 65 °C for at least one hour; and (II) drying the liquid coating formed in step (I), while said coating is in place over the substrate surface as formed in step (I), by heating the liquid coating for a time from about 19 to about 21 minutes at a temperature from about 59 to about 61 °C, to convert the liquid coating to a solid adherent coating over those portions ofthe substrate surface that were provided with a liquid coating in step (I), without causing irreversible expansion ofthe gas filled, polymer walled microballoons present in the solid coating. 12. A process comprising steps of: (I) forming on a substrate surface to be protected against accumulation of paint thereon a liquid coating of a coating composition according to claim 9, said liquid coating having a thickness coπesponding to from about 25 to about 40 μm of constituents ofthe liquid coating composition that remain present after the liquid coating is heated to 65 °C for at least one hour; and (II) drying the liquid coating formed in step (I), while said coating is in place over the substrate surface as formed in step (I), by heating the liquid coating for a time from about 15 to about 25 minutes at a temperature from about 55 to about 65 °C, to convert the liquid coating to a solid adherent coating over those portions ofthe substrate surface that were provided with a liquid coating in step (I), without causing irreversible expansion of the gas filled, polymer walled microballoons present in the solid coating. 13. A process comprising steps of: (I) forming on a substrate surface to be protected against accumulation of paint thereon a liquid coating of a coating composition according to claim 8, said liquid coating having a thickness coπesponding to at least about 20 μm of constituents of the liquid coating composition that remain present after the liquid coating is heated to 65 °C for at least one hour; and (II) drying the liquid coating formed in step (I), while said coating is in place over the substrate surface as formed in step (I), for a sufficient time at a sufficient temper¬ ature to convert the liquid coating to a solid adherent coating over those portions of the substrate surface that were provided with a liquid coating in step (I), with- out causing iπeversible expansion of the gas filled, polymer walled microbal¬ loons present in the solid coating. 14. A process comprising steps of: (I) forming on a substrate surface to be protected against accumulation of paint thereon a liquid coating of a coating composition according to claim 7, said liquid coating having a thickness coπesponding to at least about 20 μm of constituents of the liquid coating composition that remain present after the liquid coating is heated to 65 °C for at least one hour; and (II) drying the liquid coating formed in step (I), while said coating is in place over the substrate surface as formed in step (I), for a sufficient time at a sufficient temper- ature to convert the liquid coating to a solid adherent coating over those portions ofthe substrate surface that were provided with a liquid coating in step (I), with¬ out causing iπeversible expansion of the gas filled, polymer walled microbal- loons present in the solid coating. 15. A process comprising steps of: (I) forming on a substrate surface to be protected against accumulation of paint thereon a liquid coating of a coating composition according to claim 6, said liquid coating having a thickness coπesponding to at least about 12 μm of constituents ofthe liquid coating composition that remain present after the liquid coating is heated to 65 °C for at least one hour; and (II) drying the liquid coating formed in step (I), while said coating is in place over the substrate surface as formed in step (I), for a sufficient time at a sufficient temper- ature to convert the liquid coating to a solid adherent coating over those portions ofthe substrate surface that were provided with a liquid coating in step (I), with¬ out causing iπeversible expansion of the gas filled, polymer walled microbal¬ loons present in the solid coating. 16. A process comprising steps of: (I) forming on a substrate surface to be protected against accumulation of paint thereon a liquid coating of a coating composition according to claim 5, said liquid coating having a thickness coπesponding to at least about 12 μm of constituents of the liquid coating composition that remain present after the liquid coating is heated to 65 °C for at least one hour; and (II) drying the liquid coating formed in step (I), while said coating is in place over the substrate surface as formed in step (I), for a sufficient time at a sufficient temper¬ ature to convert the liquid coating to a solid adherent coating over those portions ofthe substrate surface that were provided with a liquid coating in step (I), with¬ out causing irreversible expansion of the gas filled, polymer walled microbal- loons present in the solid coating. 17. A process comprising steps of: (I) forming on a substrate surface to be protected against accumulation of paint thereon a liquid coating of a coating composition according to claim 4, said liquid coating having a thickness coπesponding to at least about 12 μm of constituents of the liquid coating composition that remain present after the liquid coating is heated to 65 °C for at least one hour; and (II) drying the liquid coating formed in step (I), while said coating is in place over the substrate surface as formed in step (I), for a sufficient time at a sufficient temper¬ ature to convert the liquid coating to a solid adherent coating over those portions ofthe substrate surface that were provided with a liquid coating in step (I), with- out causing iπeversible expansion of the gas filled, polymer walled microbal¬ loons present in the solid coating. 18. A process comprising steps of: (I) forming on a substrate surface to be protected against accumulation of paint thereon a liquid coating of a coating composition according to claim 3, said liquid coating having a thickness coπesponding to at least about 12 μm of constituents of the liquid coating composition that remain present after the liquid coating is heated to 65 °C for at least one hour; and (II) drying the liquid coating formed in step (I), while said coating is in place over the substrate surface as formed in step (I), for a sufficient time at a sufficient temper- ature to convert the liquid coating to a solid adherent coating over those portions ofthe substrate surface that were provided with a liquid coating in step (I), with¬ out causing iπeversible expansion of the gas filled, polymer walled microbal¬ loons present in the solid coating. 19. A process comprising steps of: (I) forming on a substrate surface to be protected against accumulation of paint thereon a liquid coating of a coating composition according to claim 2, said liquid coating having a thickness coπesponding to at least about 12 μm of constituents of the liquid coating composition that remain present after the liquid coating is heated to 65 °C for at least one hour; and (II) drying the liquid coating formed in step (I), while said coating is in place over the substrate surface as formed in step (I), for a sufficient time at a sufficient temper¬ ature to convert the liquid coating to a solid adherent coating over those portions ofthe substrate surface that were provided with a liquid coating in step (I), with¬ out causing iπeversible expansion of the gas filled, polymer walled microbal- loons present in the solid coating. 20. A process comprising steps of: (I) forming on a substrate surface to be protected against accumulation of paint thereon a liquid coating of a coating composition according to claim 1, said liquid coating having a thickness coπesponding to at least about 12 μm of constituents of the liquid coating composition that remain present after the liquid coating is heated to 65 °C for at least one hour; and (II) drying the liquid coating formed in step (I), while said coating is in place over the substrate surface as formed in step (I), for a sufficient time at a sufficient temper¬ ature to convert the liquid coating to a solid adherent coating over those portions ofthe substrate surface that were provided with a liquid coating in step (I), with- out causing irreversible expansion of the gas filled, polymer walled microbal¬ loons present in the solid coating.

Inventors: BELECK SCOTT J, BELECK, SCOTT, J.
Applicants: HENKEL CORP, HENKEL CORPORATION
Application year: 1997
Main classification: C08J9
IPC codes: B05D1, B05D5, C08J9, C09D5, C09D131, C09D133