Heterogeneous catalyst for the production of acetic anhydride from methyl acetate

Abstract: Acetic anhydride is produced by reaction of methyl acetate (or dimethyl ether and acetic acid), carbon monoxide, and hydrogen in the presence of an alkyl halide and a heterogeneous, bifunctional catalyst that contains an insoluble polymer having pendant quaternized phosphine groups, some of which phosphine groups are ionically bonded to anionic Group 9 or 10 (post-1986 IUPAC-recommended nomenclature) metal complexes, the remainder of the phosphine groups being bonded to iodide. In contrast to prior art processes, no accelerator (promoter) is necessary to achieve the catalytic reaction and the products are easily separated from the catalyst by filtration.

Description: This invention was made with USA Government Support under Contract No. DE-FC22-95PC93052 between Air Products and Chemicals, Inc., and the United States Department of Energy. The USA Government has certain rights to this invention. This invention relates to a process for producing acetic anhydride by carbonylating methyl acetate and/or dimethyl ether in the presence of a heterogeneous, bifunctional catalyst. The catalyst contains quaternized phosphine groups, some of which phosphine groups are ionically bonded to anionic Group 9 or 10 metal (viz. Rh, Pt, Pd, Ir, Ru, Co, and Ni) complexes, the remainder being bonded to iodide. Acetic Anhydride (Ac 2 O) is a chemical that has many uses. For example, it is used in the manufacture of cellulose acetate from cellulose. Acetic anhydride is prepared by the carbonylation of methyl acetate (MeOAc) in the presence of a homogeneous Rh catalyst with a lithium iodide (LiI) promoter. Others have attempted to design heterogeneous catalysts with a view of minimizing the leaching of the metal complex. One such system described in US-A-4,328,125 is an anion exchange resin to which is ionically bound an anionic metal carbonyl species having the general formula M n (CO) m (X) p - , where M is a transition metal. These catalysts have been described and used for the carbonylation of alcohols for the production of carboxylic acids. Marston et al. in US-A-5,155,261 and Minami et al. in US-A-5,364,963 have described a similar catalyst consisting of a cross-linked 4-vinylpyridine divinylbenzene copolymer containing quaternized pyridine groups supporting a rhodium species. This catalyst is robust and offers higher operating temperature for the carbonylation of methanol to acetic acid. US-A-5,360,929 discloses the use of these catalysts to produce carboxylic acid anhydrides from carboxylate esters and ethers. DE-A-3511048 discloses the carbonylation of methyl acetate to acetic anhydride using a carrier supported noble metal catalyst and an iodine promoter, said catalyst carrier having noble metal/chelate compound formed of the noble metal and a chelator containing organonitrogen, organophosphorus, organoarsenic or organosulfur groups applied to it. US-A-5,360,929 discloses the carbonylation of methyl acetate to acetic anhydride using a rhodium-containing catalyst in the presence of an iodine promoter, said catalyst comprising an insoluble polymer support having pendant quaternized N-base or alkylated N-oxide pyridine groups supporting a rhodium species. The preferred and exemplified polymer supports are prepared from polyvinylpyridine copolymers available under the trade mark Reillex. It is an essential feature of the carbonylation that a finite concentration of carboxylic acid is maintained in the reaction composition to maintain the rhodium species bound to the polymer support. US-A-5,466,874 discloses the carbonylation of methyl acetate to acetic anhydride using a rhodium-containing catalyst in the presence of an iodine promoter, said catalyst comprising a polymer support having multiple sites which can bind with an alkyl iodide and a rhodium species. Reference is made to polymer supports containing pendent diaryl or dialkylphosphines off a thermally stable vinyl backbone but no exemplification or details of use are provided for these polymer supports. The preferred and only exemplified polymer support is polyvinylpyrrolidone but specific reference is made to polyvinylpyridine copolymers available under the Trade Mark Reillex. The only specified rhodium compounds used for making the catalysts are rhodium triiodide and rhodium acetate. In the present invention, Ac 2 O is produced by carbonylation of methyl acetate (MeOAc) (or dimethyl ether and acetic acid) in the presence of a heterogeneous, bifunctional catalyst. The process comprises reacting methyl acetate, hydrogen, carbon monoxide and an alkyl halide in the presence of the bifunctional catalyst. The catalyst comprises an insoluble polymer having pendant quaternized phosphine groups, some of which phosphine groups are ionically bonded to anionic Group 9 or 10 metal complexes, the remainder of the phosphine groups being bonded to iodide. Use of the bifunctional catalyst of the present invention for Ac 2 O production has distinct advantages over the use of other catalysts in that accelerators or promoters like LiI are not required and the separation of catalysts from product is made easier. The use of ionic bonding to the Group 9 or 10 metal complex also offers a further advantage in that the leaching of metal from the catalyst is minimized. The process is highly selective toward Ac 2 O, can be completed under short reaction times at high temperatures and pressures, and can proceed efficiently with recycling of the catalyst. In one aspect, the present invention provides a bifunctional catalyst for the carbonylation of methyl acetate to acetic anhydride, which catalyst comprises an insoluble styrene copolymer having pendant quaternized phosphine groups, some of which phosphine groups are ionically bonded to anionic metal complexes containing Rh, Pt, Pd, Ir, Ru, Co, or Ni, the remainder of the phosphines being bonded to iodide. In another aspect, the present invention provides a bifunctional catalyst for the carbonylation of methyl acetate to acetic anhydride, which catalyst comprises an insoluble polymer having pendant quaternized phosphine groups, some of which phosphine groups are ionically bonded to anionic metal complexes containing Rh or Ir, the remainder of the phosphines being bonded to iodide, said catalyst being obtainable by reacting an insoluble polymer having alkyl iodide quaternized phosphine groups with a metal complex of the formula [M(CO) a L b X c ] - , where M is Rh or Ir, or combinations thereof; L is an alkyl or acyl group; X is a halide ion; a is 1, 2, 3 or 4; b is 0 or 1; and c is 2 or 3, and wherein a+b+c ≤6 In a further aspect, the present invention provides a process for producing acetic anhydride which comprises reacting methyl acetate with carbon monoxide and hydrogen in the presence of an alkyl iodide and a catalyst, characterized in that the catalyst is a bifunctional catalyst in accordance with either of the aforementioned aspects. In another aspect, the present invention provides a process for making Ac 2 O from MeOAc, carbon monoxide (CO) and hydrogen (H 2 ) in the presence of an alkyl iodide and a bifunctional catalyst that comprises an insoluble polymer having pendant quaternized phosphine groups, some of which phosphine groups are ionically bonded to anionic Group 9 or 10 metal complexes, the remainder of the phosphine groups being bonded to iodide wherein the bifunctional catalyst is recycled for further reaction with methyl acetate, carbon dioxide and hydrogen to produce acetic anhydride. The bifunctional catalyst is a heterogeneous catalyst that contains an insoluble polymer having quaternized phosphine groups. The phosphine groups are quaternized by techniques well known in the art using an alkyl halide. Preferred alkyl halides contain from one to six carbon atoms (e.g., C 1 -C 4 alkyl). Preferred halides are iodide (I), chloride (Cl) or bromide (Br) and, more preferably iodide. A most preferred alkyl halide is methyl iodide. The polymer is an organic polymer that is large enough and sufficiently cross-linked to be insoluble in organic solvents and contain pendant phosphine groups that can be quaternized. The phosphine groups can be primary (RPH 2 ), secondary (R 2 PH) or tertiary (R 3 P) phosphines where R is an alkyl, cycloalkyl or aryl group having up to 20 carbon atoms. Exemplary phosphine groups are trimethyl phosphine, triethyl phosphine, triisopropyl phosphine, tri-n-butyl phosphine, tri-tert-butyl phosphine, tricyclohexyl phosphine and triphenyl phosphine. A preferred polymer is a copolymer of styrene, especially a copolymer of styrene and divinylbenzene. Following quaternization of the polymer phosphine groups (e.g., by refluxing the polymer with an excess of methyl iodide in toluene), the polymer is ionically attached to anionic Group 9 or 10 metal complexes. The catalyst of the present invention utilizes a Group 9 or 10 metal, viz. rhodium (Rh), platinum (Pt), palladium (Pd), iridium (Ir), ruthenium (Ru), cobalt (Co), or nickel (Ni). Preferred Group 9 or 10 metals are Rh, Ir and Pd. Rh is most preferred. The Group 9 or 10 metal catalyst used in the catalyst system is present in a catalytically effective amount and such catalytically effective amounts can be readily determined by those of ordinary skill in the art. The amount of Group 9 or 10 metal to be incorporated into the catalyst system typically ranges from 0.01 mol % to 10 mol % based on the MeOAc present, preferably from 0.03 to 5 mol %. In a preferred embodiment, an anionic Group 9 or 10 metal complex corresponds to the general formula [M(CO) a L b X c ] - where M is Rh, Ir or combinations thereof; L is an alkyl or acyl group; X is a halide ion; a is 1, 2, 3, or 4; b is 0 or 1; and c is 2 or 3. The sum of a, b and c is equal to or less than six (i.e., a+b+c ≤6). In a preferred embodiment, M is Rh, X is Cl, a is ≤4, b is 0, c is 2, the formula of the Group 9 or 10 metal complex is Rh 2 (CO) 4 Cl 2 , and the anionic species [Rh(CO) 2 I 2 ] - is incorporated into the polymer. Using the Rh complexes described above, the maximum Rh content that can be incorporated into the polymer is 20% by weight of the polymer or less. Because the catalyst used in a process of the present invention is bifunctional, it is important that only a portion of the quaternized phosphine groups be ionically bonded to the anionic Group 9 or 10 metal complex. By way of example, where the Group 9 or 10 metal is Rh, the total content of Rh in the catalyst is less than 20% by weight of the polymer. As shown hereinafter in the Examples, catalysts having between 2% and 6% by weight of Rh have been successfully used in the preparation of Ac 2 O. The quaternized phosphine groups not ionically bonded to the anionic Group 9 or 10 metal complex are bonded to iodide (I - ). This bonding of I to the catalyst eliminates the need for any extraneous promoter or accelerator in the overall reaction of making Ac 2 O from MeOAc. The carbonylation can be carried out in a batch mode or a continuous mode over a wide range of temperatures. While the optimum temperature for practicing the present invention will depend upon process stoichiometry, the particular catalyst system utilized, as well as the precise combination of reaction conditions, suitable carbonylation temperatures usually will range from 90°C up to 225°C. However, the most preferred carbonylation temperatures range from 150°C to 210°C. The carbonylation reaction can be carried out under a wide variety of pressures including pressures ranging from 100 to 1500 psig (0.7 to 10.3 MPa). Preferred pressures range from 500 to 1000 psig (3.4 to 6.9 MPa). Most preferred reaction conditions are a temperature of about 190°C and a pressure of about 800 psig (5.5 MPa). The products of the reaction are analyzed by gas chromatography at various times during the reaction and also in a batch mode (i.e., at the end of the reaction). The catalyst can be removed by filtration and reused for a new feed without a loss in initial activity. Carbon monoxide and hydrogen usually are present in the reaction mixture in a stoichiometric ratio of greater than 92:8. Preferably, that stoichiometric ratio ranges from 92:8 to 99:1, especially about 95:5. The desired product (Ac 2 O) can be recovered from the product mixture using standard procedures well known in the art. The MeOAc used in a process of the present invention can be provided directly or formed from dimethyl ether (DME) and acetic acid (HOAc) as part of the overall reaction scheme. In the latter embodiment, DME, HOAc, carbon monoxide and hydrogen are reacted in the presence of an alkyl halide and a bifunctional catalyst as set forth above. The reaction conditions used are the same as set forth above. Reaction time is not critical in practicing the present invention and one of ordinary skill in the art can determine optimum reaction times based upon the enumerated reaction conditions, catalyst system and catalyst concentration presented herein. Reaction times required to produce a desired amount of Ac 2 O will also depend upon the reaction temperature and pressure. Typically, reaction times range from 0.5 hours to 4.0 hours. In contrast to prior art processes, no accelerator is necessary to achieve the catalytic reaction and the products are easily separated from the catalyst by filtration. The catalyst can be recycled without loss in activity. The following Examples are presented to further illustrate the scope of the present invention and are not intended to limit the scope thereof. EXAMPLE 1 Preparation Of Bifunctional, Phosphine Catalyst Lithium wire (0.212 g) was broken into small pieces and placed in a flask containing 10 ml of tetrahydrofuran. Chlorodiphenylphosphine (3.12 g) was added to the wire mixture followed by the addition of another 10 ml of tetrahydrofuran. The mixture was stirred under nitrogen for 24 hours to give a red solution of lithium diphenyl-phosphide. The solution was filtered and to the filtrate was added 5 g of 2% cross-linked Merrifield's resin (chloromethylated styrene/vinylbenzene copolymer), which had been previously dried under vacuum. An additional 25 ml of tetrahydrofuran was added and the mixture stirred for another 24 hours under nitrogen. The phosphinated resin was filtered and washed with 3 x 50 ml of tetrahydrofuran. The resin was further washed with 2 x 50 ml of acetone and finally with 50 ml of pentane and then dried under vacuum. 50 ml of toluene was added to approximately 2 g of the phosphinated resin. Following the addition of 10 ml of methyl iodide, the slurry was heated at 100°C for 24 hours. The phosphonium iodide salt of the resin was filtered, washed with 50 ml of toluene and then dried under vacuum. The rhodium complex Rh 2 (CO) 4 Cl 2 (0.21 g) was dissolved in 100 ml of toluene and added to the phosphonium iodide salt of the resin from the previous step. After stirring for 24 hours, the resin was brown in color and the toluene was colorless indicating that all the rhodium was in the resin. The resin was filtered and characterized via infrared spectroscopy. Two strong carbonyl bands were observed at 2053, 1981 cm-1 characteristic of the species [Rh(CO) 2 IX] - , where X = Cl or I. This finding proves that the rhodium complex was ionically attached to the phosphonium salt of the resin. EXAMPLE 2 Catalyst Evaluation and Recycle The following studies were performed to evaluate a bifunctional catalyst of the present invention. An autoclave was charged with methyl acetate (0.695 mol), methyl iodide (0.074 mol), acetic acid (0.29 mol), and 0.8 g of the catalyst prepared in accordance with the procedures of Example 1. The autoclave was pressurized with a 95/5 mix of CO/H 2 and the reaction was run at 750 psig (5.2 MPa) and 190°C. After 4 hours, the liquid samples were analyzed by gas chromatography. The reaction was repeated using the same catalyst, but with a fresh charge of reactants. The results of these studies are summarized in Table 1, below. For comparison purposes, the effects of a phosphine catalyst of the present invention were compared to another bifunctional catalyst, designated as a Reillex™ (cross-linked polyvinylpyridine resins available from Reilly Industries, Inc.) catalyst. The Reillex™ catalyst was prepared as follows. A sample of Reillex™ 425 (macro-reticular poly-4-vinylpyridine weak base resin) (24 g) was dried in an oven at 100°C for 14 hours. The dried polymer beads were placed in a flask which contained 125 ml of toluene and the mixture was refluxed for 30 minutes under nitrogen. After cooling to room temperature, 20 ml of methyl iodide was added and the resulting mixture was heated at 95°C for 48 hours and then stirred at room temperature for another 5 days. The yellow beads/powder was filtered and dried under vacuum for 8 hours. Approximately 0.36 g of the Group 9 or 10 metal complex Rh 2 (CO) 4 Cl 2 was dissolved in 100 ml of toluene. About 3.36 g of quaternized Reillex™ prepared in the previous step was added, the mixture was stirred for approximately 24 hours and the powder was filtered. No color was observed in the filtrate indicating that all the rhodium was on the polymer. The Reillex™ material contained about 5.1% by weight of rhodium. By using this method and by varying the amount of complex, a 2.24% Rh containing polymer was also prepared. Catalyst MeOAc Conv. % Ac 2 O turnover freq, (hr -1 ) Phosphine 5.4% Rh 34 122 Recycle 37 141 Reillex 2.24% Rh 51.0 153 Recycle 46.5 117 Reillex 5.1% 35.8 137 Recycle 33.6 120 Homogeneous , no LiI 30 99 Homogeneous , with LiI 77 332 The results show that the phosphinated catalyst is slightly better that the Reillex™ material at comparable Rh loading. Also, the heterogeneous phosphine catalyst can be recycled without any apparent loss of activity. In contrast, the Reillex™ catalyst, at both Rh loadings, lost activity when recycled. All the heterogeneous systems are better than the homogeneous catalyst used without the LiI promoter.

Claims: A bifunctional catalyst for the carbonylation of methyl acetate to acetic anhydride, which catalyst comprises an insoluble styrene copolymer having pendant quaternized phosphine groups, some of which phosphine groups are ionically bonded to anionic metal complexes containing Rh, Pt, Pd, Ir, Ru, Co, or Ni, the remainder of the phosphines being bonded to iodide. A bifunctional catalyst for the carbonylation of methyl acetate to acetic anhydride, which catalyst comprises an insoluble polymer having pendant quaternized phosphine groups, some of which phosphine groups are ionically bonded to anionic metal complexes containing Rh or Ir, the remainder of the phosphines being bonded to iodide, said catalyst being obtainable by reacting an insoluble polymer having alkyl iodide quaternized phosphine groups with a metal complex of the formula [M(CO) a L b X c ] - , where M is Rh or Ir, or combinations thereof; L is an alkyl or acyl group; X is a halide ion; a is 1, 2, 3 or 4; b is 0 or 1; and c is 2 or 3, and wherein a+b+c ≤6 A catalyst according to Claim 1 or Claim 2, wherein the insoluble polymer is a co-polymer of styrene and divinylbenzene having pendant phosphine groups. A catalyst according to Claim 1 or Claim 3, wherein the complex contains rhodium, iridium or palladium. A catalyst according to Claim 2 or Claim 4, wherein the complex contains rhodium. A catalyst according to Claim 1 or any one of Claims 3 to 5 when dependent on Claim 1, obtainable by reacting an insoluble polymer having alkyl iodide quaternized phosphine groups with a metal complex of the formula [M(CO) a L b X c ] - , where M is Rh or Ir, or combinations thereof; L is an alkyl or acyl group; X is a halide ion; a is 1, 2, 3 or 4; b is 0 or 1; and c is 2 or 3, and wherein a+b+c ≤6. A catalyst according to Claim 2 or Claim 6, wherein M is Rh; X is Cl; a is ≤4; b is 0 and c is 2. A catalyst according to Claim 7, wherein the catalyst comprises a metal complex anion having the formula [Rh(CO) 2 I 2 ] - . A process for producing acetic anhydride which comprises reacting methyl acetate with carbon monoxide and hydrogen in the presence of an alkyl iodide and a catalyst, characterized in that the catalyst is a bifunctional catalyst that comprises an insoluble polymer having pendant quaternized phosphine groups, some of which phosphine groups are ionically bonded to anionic metal complexes containing Rh, Pt, Pd, Ir, Ru, Co, or Ni, the remainder of the phosphines being bonded to iodide and in that the bifunctional catalyst is recycled for further reaction with methyl acetate, carbon dioxide and hydrogen to produce acetic anhydride. A process for producing acetic anhydride which comprises reacting methyl acetate with carbon monoxide and hydrogen in the presence of an alkyl iodide and a catalyst, characterized in that the catalyst is a bifunctional catalyst as defined in any one of Claims 1 to 8. A process as claimed in Claim 10, wherein the bifunctional catalyst is recycled for further reaction with methyl acetate, carbon dioxide and hydrogen to produce acetic anhydride. A process according to any one of Claims 9 to 11, wherein the methyl acetate is formed in situ from dimethyl ether and acetic acid. A process of any one of Claims 9 to 12, wherein the alkyl iodide is methyl iodide. A process according to any one of Claims 9 to 13, wherein the reaction conditions comprise a temperature ranging from 90°C to 225°C and a pressure ranging from 0.7 to 10.3 MPa (100 to 1500 psig). A process according to Claim 14, wherein the temperature ranges from 150°C to 210°C and the pressure ranges from 3.4 to 6.9 MPa (500 to 1000 psig). A process according to Claim 15, wherein the temperature is about 190°C and the pressure is about 5.5 MPa (800 psig). A process according to any one of Claims 9 to 16, wherein carbon monoxide (CO) and hydrogen (H 2 ) are present in a stoichiometric ratio (CO:H 2 ) of from 99:1 to 92:8. A process according to Claim 17, wherein the stoichiometric ratio of carbon monoxide to hydrogen is about 95:5. A process according to any one of Claims 9 to 18, wherein the said metal is present in an amount of 0.01 to 10 mol % methyl acetate. A process according to Claim 19, wherein said amount of metal is 0.03 to 5 mol % methyl acetate. A process according to any one of Claims 9 to 20, conducted in the absence of a separate catalyst promoter. The use of a catalyst according to any one of Claims 1 to 8 to catalyse the carbonylation of methyl acetate to acetic anhydride. The use of a catalyst according to any one Claims 1 to 8 to catalyse the carbonylation of the dimethyl ether and acetic acid to acetic anhydride.

Inventors: RAMPRASAD DORAI, WALLER FRANCIS JOSEPH, RAMPRASAD, DORAI, WALLER, FRANCIS JOSEPH
Applicants: AIR PROD & CHEM, AIR PRODUCTS AND CHEMICALS, INC.
Application year: 1997
Main classification: B01J31
IPC codes: B01J31, C07C51