Reflective liquid crystal panel substrate

Abstract: In order to avoid problems arising from thickness variation of approximately 10% in a silicon nitride film formed by a reduced pressure CVD process, a reflective liquid crystal panel comprising a matrix of reflecting electrodes (14) formed on a substrate member (1), a transistor formed beneath to each reflection electrode for applying a voltage thereto, a silicon oxide film (17) having a thickness of 500 to 2,000 angstroms is used as the passivation film. Where only light of one primary color is incident on the panel the thickness is set to a sub range, 1,300 to 1,900 angstroms for red light, 1,200 to 1,600 angstroms for green light, and 900 to 1,200 angstroms for blue light.

Description: The present invention relates to liquid crystal panels, in particular reflective liquid crystal panels having a substrate including an active matrix in which reflective pixel electrodes are switched with switching elements. The term panel is intended to mean in this specification a unit which may be fixed into an electronic device or for example a projector display device. Liquid crystal panels normally comprise opposed planar electrodes enclosing a layer of liquid crystal material. For active panels, the active electrode is configured as a matrix of pixel electrodes supported on a sheet of a substrate material. Whilst various terms are used to denote such active electrode, such as back plate electrode, the term which will be used in this specification is "substrate". Transmissive liquid crystal panels having a thin film transistor (TFT) array using amorphous silicon formed on glass have been used as active matrix liquid crystal panels in light valves of projection display devices. In a transmissive liquid crystal panel, each pixel electrode is formed with a transparent conductive film. In transmissive liquid crystal panels, the switching element-forming region, such as a TFT, which is provided in each pixel is not a transparent region, and this gives rise to a serious defect in that the aperture ratio is low and decreases as the resolution of the panel is improved to XGA, or S-VGA. As a liquid crystal panel having a smaller size than a transmissive active matrix liquid crystal panel, an active matrix liquid crystal panel in which pixel electrodes, as reflecting electrodes, are switched with transistors formed on a semiconductor material or an insulating material has been proposed. In such a reflective liquid crystal panel, the formation of a passivation film as a protective film on the substrate in which the reflecting electrodes are formed is often omitted since it is not always necessary. In general, a silicon nitride film formed by a low pressure CVD process, or a plasma CVD process, is often used as a passivation film in semiconductor devices. The passivation film formed by a current CVD process inevitably has some variation of the thickness of approximately 10%. Accordingly, the reflectance of the reflective liquid crystal panel varies significantly with variation of the thickness of the passivation film. JP 08 101383 A contains a prior disclosure of a liquid crystal panel which does not include the features which appear in the characterising portion of Claim 1 and 2, but it includes all the features of the pre-characterising portion of these claims. SUMMARY OF THE INVENTION It is an object of the present invention to provide a reflective liquid crystal panel substrate having a passivation film wherein the variation in reflectance of the liquid crystal is reduced and the substrate has high reliability and provides improved image quality. The present invention provides in a first aspect a liquid crystal panel substrate comprising a matrix of reflective electrodes, a substrate member, a respective switching element formed on the substrate member for applying a voltage to each reflective electrode, wherein a passivation film of silicon oxide is formed over said reflective electrodes, and a thickness of said passivation film is 1200 to 1600 angstroms (120 to 160 nm) for reflection of green light. In a second aspect, the invention provides a liquid crystal panel substrate comprising a matrix of reflective electrodes, a substrate member, a respective switching element formed on the substrate member for applying a voltage to each reflective electrode, wherein a passivation film of silicon oxide is formed over said reflective electrodes, and a thickness of said passivation film is 1300 to 1900 angstroms (130 to 190 nm) for reflection of red light. In a third aspect, the invention provides a liquid crystal panel comprising a liquid crystal panel substrate, a transparent substrate at a light incident side having a counter electrode, and a liquid crystal encapsulated into a gap between said liquid crystal substrate and said transparent substrate, the liquid crystal panel substrate comprising a matrix of reflective electrodes on a substrate member; a respective switching element formed on the substrate member for applying a voltage to each reflective electrode, wherein a passivation film of silicon oxide is formed over said reflective electrodes, and a thickness of said passivation film for reflection of red light being in a range of 1300 to 1900 angstroms (130 to 190 nm), the thickness of said passivation film for reflection of green light being in a range of 1200 to 1600 angstroms (120 to 160 nm), and the thickness of said passivation film for reflection of blue light being in a range of 900 to 1200 angstroms (90 to 120 nm). A phenomenon in which reflectance of the reflecting electrode significantly varies with the wavelength of light can be suppressed by forming the passivation film with a silicon oxide film. A silicon oxide film having a thickness of 500 to 2,000 angstroms is used as the passivation film of the reflective liquid crystal panel substrate. Although silicon oxide film as a protective film is slightly inferior to silicon nitride film, it affects the reflectance of the pixel electrode less, due to variation of the film thickness compared to the silicon nitride film. Since a silicon oxide film having a thickness of 500 to 2,000 angstroms shows particularly little dependency of reflectance on the wavelength, the use of the silicon oxide film as a passivation film can reduce variation of the reflectance. Further, the thickness of the passivation film may be set to an appropriate range in response to the wavelengths of incident light. Thus, the thickness of silicon oxide passivation film is preferably 900 to 1,200 angstroms for a pixel electrode reflecting blue light, 1,200 to 1,600 angstroms for a pixel electrode reflecting green light, or 1,300 to 1,900 angstroms for a pixel electrode reflecting red light. When the thickness of the silicon oxide passivation film is set to the above range, variation of the reflectance for each color can be suppressed to 1 % or less, reliability of the liquid crystal panel is improved and the image quality is improved in a projection display device using the reflecting liquid crystal panel as a light valve. In a reflective liquid crystal panel having a pixel region in which a matrix of pixel electrodes are disposed and peripheral circuits, such as a shift register and a control circuit are formed on the same substrate, a silicon oxide passivation film may be formed above the pixel region and a silicon nitride passivation film may be formed above the peripheral circuits, since the thickness of the passivation film above the peripheral circuits does not affect reflectance; the use of silicon nitride film enables secure protection of the peripheral circuits and improvement in reliability. The present invention provides in a fourth aspect a projection display device comprising a light source, at least three reflective liquid crystal panels for modulating the light from said light source, and a projection lens for projecting the light modulated by said reflective liquid crystal panel, the liquid crystal panel including a liquid crystal panel substrate, a transparent substrate at a light incident side having a counter electrode and a liquid crystal encapsulated into a gap between said liquid crystal substrate and said transparent substrate, the liquid crystal panel substrate comprising a matrix of reflective electrodes on a substrate member, a respective switching element formed on the substrate member for applying a voltage to each reflective electrode, wherein a passivation film of silicon oxide is formed over said reflective electrodes and said projection display device further comprising a color separation means for separating the light from said light source into three primaries, a first reflective liquid crystal panel for modulating red light from said color separation means, a second reflective liquid crystal panel for modulating green light from said color separation means, and a third reflective liquid crystal panel for modulating blue light from said color separation means, a thickness of the silicon oxide passivation film of said first reflective liquid crystal panel being in a range of 1300 to 1900 angstroms (130 to 190 nm), the thickness of the silicon oxide film forming a passivation film of said second reflective liquid crystal panel being in a range of 1200 to 1600 angstroms (120 to 160 nm), and the thickness of the silicon oxide film forming a passivation film of said third reflective liquid crystal panel being in a range of 900 to 1200 angstroms (90 to 120 nm). The passivation films thus have a thickness according to the wavelength of the color light to be modulated in each light valve for modulating each color light. Variation of the reflectance and variation of the synthetic light therefore decrease. Variation of hue of color display in the projected light between different projection display device products can be prevented. BRIEF DESCRIPTION OF THE DRAWINGS Preferred embodiments in accordance with the present invention will now be described with reference to the drawings, wherein:- Figures 1 and 1b are cross-sectional views of a first embodiment of a pixel region of a reflecting electrode substrate of a reflective liquid crystal panel in accordance with the present invention along the lines I-I and II-II of figure 3; Figure 2 is a cross-sectional view of a second embodiment of a structure of a peripheral circuit of a reflecting electrode substrate of a reflective liquid crystal panel in accordance with the present invention; Figure 3 is a plan view of the first embodiment of a pixel region of a reflecting electrode side substrate of a reflective liquid crystal panel in accordance with the present invention; Figure 4 is a cross-sectional view of an edge structure of a reflecting electrode side substrate of a reflective liquid crystal panel in accordance with the present invention; Figure 5 is a cross-sectional view of a third embodiment of a reflecting electrode substrate of a reflective liquid crystal panel in accordance with the present invention; Figure 6 is a plan view of an example of a layout of a reflecting electrode substrate of a reflective liquid crystal panel to which the present invention is applied; Figure 7 is a cross-sectional view of a reflective liquid crystal panel according to the present invention; Figure 8 is a wave form diagram of a gate driving wave form and a data line driving wave form of an FET for pixel electrode switching of a reflective liquid crystal panel in accordance with the present invention; Figure 9 is a block diagram of a video projector in which a reflective liquid crystal panel according to the invention is used as a light valve; Figure 10 is a graph illustrating reflectance of an aluminium reflecting electrode varying with the thickness of silicon oxide film for a given wavelength of the incident light; Figure 11 is a graph illustrating reflectance of an aluminium reflecting electrode varying with the thickness of silicon oxide film for a given length of the incident light; Figure 12 is a graph in which reflectance is plotted at a given wavelength interval when the thickness of the silicon oxide film is changed within a wavelength range covering blue light; Figure 13 is a graph in which reflectance is plotted at a given wavelength interval when the thickness of the silicon oxide film is changed within a wavelength range covering green light. Figure 14 is a graph in which reflectance is plotted at a given wavelength interval when the thickness of the silicon oxide film is changed within a wavelength range covering red light; Figure 15(a), (b) and (c) are sketches of electronic devices using reflective liquid crystal panels in accordance with the present invention; Figure 16 is a cross-sectional view of a fourth embodiment of a reflecting electrode substrate of a reflective liquid crystal panel in accordance with the present invention; and Figure 17 is a cross-sectional view of a fifth embodiment of a reflecting electrode substrate of a reflective liquid crystal panel in accordance with the present invention. DESCRIPTION OF THE PREFERRED EMBODIMENTS Figures 1 and 3 show a first embodiment of a reflecting electrode substrate of a reflective liquid crystal panel in accordance with the present invention. Figures 1 and 3 are a cross-sectional view and a planar layout view, respectively, of one pixel section among a matrix of pixels. Figure 6 is an entire planar layout view of a reflecting electrode substrate of a reflective liquid crystal panel in accordance with the present invention. In Figure 1, a P-type semiconductor substrate such as single-crystal silicon (or N-type semiconductor substrate (N--)), has formed thereon a P-type well region 2 having an impurity content higher than that of the semiconductor substrate 1, and a field oxide film 3 for separating elements (so called LOCOS) is formed on the surface of the semiconductor substrate 1. The well region 2 is formed as a common well region in which a matrix of pixels 20 of, for example, 768 by 1,024 is provided, as shown in Figure 6. The well region 2 is separately formed from a well region, disposed around the periphery of pixel region 20, in which peripheral circuits are disposed. Referring to figure 6, a light shielding film 25 is provided in order to shield the light incident on the peripheral circuits provided on the periphery of the substrate. The peripheral circuits are provided on the periphery of the pixel region 20 in which a matrix of the pixel electrodes is disposed, and include a data line driving circuit 21 for supplying image signals to the data line 7 in response to the image data, a gate line driving circuit 22 for sequentially scanning gate lines 4, an input circuit for reading the image data from the outside through the pad region 26, and a timing control circuit 24 for controlling these circuits. These circuits are formed by combining active devices or switching devices composed of MOSFETs formed by the same step as or a different step to the MOSFET for switching the pixel electrodes and loading devices, such as resistors and capacitors. In figure 1, the field oxide film 3 is formed in a thickness of 5,000 to 7,000 angstroms by selective thermal oxidation. Two openings per pixel are formed in the field oxidation film 3. In the centre of one opening a gate electrode 4a composed of polysilicon or metal silicide is formed through a gate oxide film (insulating film) 4b formed by thermal oxidation; source and drain regions 5a and 5b composed of N-type impurity doping layers are formed on the substrate surface at both sides of the gate electrode 4a, and a MOSFET is thereby formed. The gate electrode 4a extends to the scanning direction (pixel line direction) to form a gate line 4. On the substrate surface in the other opening formed in the field oxide film 3, a P-type doping region 8 is formed. On the surface of the P-type doping region 8, an electrode 9a composed of polysilicon or metal silicide is formed. An insulating film 9b is formed by thermal oxidation. A capacitor for holding a voltage applied to the pixel is formed between the electrode 9a and the P-type doping region 8 through the insulating film 9. The electrode 9a and the polysilicon or metal silicide layer as the gate electrode 4a of the MOSFET can be formed by the same process, and the insulating film 9b under the electrode 9a and the gate insulating film 4b can be formed by the same process. The insulating films 4b and 9b are formed on the semiconductor substrate surface in the openings by thermal oxidation into a thickness of 400 to 800 angstroms. The electrodes 4a and 9a have a structure in which a poly-silicon layer having a thickness of 1,000 to 2,000 angstroms is formed and a silicide layer of a high boiling point metal such as Mo or W having a thickness of 1,000 to 3,000 angstroms is formed thereon. The source and drain regions 5a and 5b are formed by means of self-alignment by implanting an N-type impurity on the substrate surface on both sides of the gate electrode 4a by ion plating, using gate 4a as a mask. The well region just below the gate electrode 4a acts as the channel region 5c of the MOSFET. The above-mentioned P-type doping region 8 is formed by, for example, a doping treatment including exclusive ion plating and heat treatment, and may be formed by ion plating before the formation of the gate electrode. That is, after the insulating films 4b and 9b are formed, an impurity of the same conductivity type as the well is implanted to form a region 8 on the well surface having a higher impurity concentration and a lower resistance than those in the well. The concentration of impurities in the well region 2 is preferably 1x10 17 /cm 3 or less, and more preferably 1x10 16 /cm 3 to 5x10 16 /cm 3 . The preferred concentration of the surface impurities in the source and drain regions 5a and 5b is 1x10 20 /cm 3 to 3x10 20 /cm 3 . Also, the concentration of the P-type doping region 8 is preferably 1x10 18 /cm 3 to 5x10 19 /cm 3 , and more preferably 1x10 18 /cm 3 to 1x10 19 /cm 3 in view of reliability of the insulating film forming the holding capacitance and voltage resistance. A first insulating layer 6 is formed over the electrodes 4a and 9a on the field oxide film 3, a data line 7 (Figure 3) of aluminium is formed on the insulating film 6, and a source electrode 7a and an auxiliary bonding wire 10 are provided so as to extended from the data line. The source electrode 7a is electrically connected to the source region 5a through a contact hole 6a formed in the insulating film 6, one end of the auxiliary bounding wire 10 is electrically connected to the drain region 5b through a contact hole 6b formed in the insulating film 6 and the other end of wire 10 is electrically connected to the electrode 9a through a contact hole 6c formed in the insulating film 6. The insulating film 6 is formed by, for example, depositing an HTO film (a silicon oxide film formed by a high temperature CVD process) having a thickness of approximately 1,000 angstroms and depositing a BPSG film (a silicate glass film containing boron and phosphorus) having a thickness of approximately 8,000 to 10,000 angstroms. The metal layer which forms the source electrode 7a and the data line 7 and the auxiliary bonding wire 10 has, for example, a four-layer structure of Ti/TiN/Al/TiN from the bottom. The thicknesses of the lower Ti layer, TiN layer, A1 layer and upper Ti layer are 100 to 600 angstroms, approximately 1,000 angstroms, 4,000 to 10,000 angstroms and 300 to 600 angstroms, respectively. A second insulating interlayer 11 is formed over the source electrode 7a, the auxiliary bonding wire 10 and the insulating interlayer 6, and a light shielding film comprising a second metal layer 12 composed of aluminium is formed on the second insulating interlayer 11. Layer 12 is formed of metal for forming bonding wires between devices in the peripheral circuits, such as a driving circuit, which are formed on the periphery of the pixel region, as described below, so that the process is simplified. The light shielding film 12 is formed so as to cover the entire pixel region 20 and has an opening 12a for allowing a pillar connecting plug 15 to electrically connect pixel electrode 14 with wire 10. As shown in Figure 3, incident light from the upper side in Figure 1 (the liquid crystal layer side) is almost completely shielded and a light leakage current flow due to light transmission in the channel region 5c and the well region 2 of the MOSFET for pixel switching can be prevented. The second insulating layer 11 is formed by, for example, depositing a silicon oxide film by a plasma CVD process using TEOS (tetraethylorthosilicate) (herein after referred to as a TEOS film) into a thickness of approximately 3,000 to 6,000 angstroms, depositing a SOG film (a spin-on-glass film), etching it by an etch-back process, and depositing a second TEOS film thereon into a thickness of approximately 2,000 to 5,000 angstroms. The second metal layer 12 as the light shielding film may have the same structure as the first metal layers 7 (7a) and 10, and may have, for example, a four layer structure of Ti/TiN/Al/TiN from the bottom. The thicknesses of the lower Ti layer, TiN layer, A 1 layer and upper Ti layer are 100 to 600 angstroms, approximately 1,000 angstroms, 4,000 to 10,000 angstroms and 300 to 600 angstroms, respectively. In this embodiment, a third insulating layer 13 is formed on the light shielding layer 12, and a rectangular pixel electrode 14 as a reflective electrode corresponding to one pixel is formed on the third insulating electrode 13. A contact hole 16 is provided inside the opening 12 in the light shielding film 12 within third insulating interlayer 13 and the second insulating interlayer 11, and the contact hole 16 is filled with a pillar connecting plug 15 composed of a high melting point metal, such as tungsten, which electrically connects the auxiliary bonding wire 10 and the pixel electrode 14. A passivation film 17 is formed over the entire pixel electrode 14. Figure 1(b) is a cross-sectional view (cross-section II-II in Figure 3) of the periphery of the pixel region in the first embodiment in accordance with the present invention. The drawing shows a configuration of a section in which the doping region 8 extending in the scanning direction of the pixel region (pixel line direction) is connected to a given voltage (V ss ). Identification number 80 represents a P-type contact region which is formed by the same step as the source/drain region of the MOSFET in the peripheral circuit, in which impurities having the same conductivity type are ion-implanted after the formation of the gate electrode into the doping region 8 which is formed before the formation of the gate electrode. The contact region 80 is connected to the line 70 through the contact hole 71 to apply a constant voltage V ss . The upper face of the contact region 80 is also shielded with a light shielding film 14' composed of a third metal layer. After tungsten is deposited by a CVD process to form the connecting plug 15, the tungsten and the third insulating interlayer 13 are planarized by a chemical mechanical polishing (CMP) process, the pixel electrode 14 is formed by a low temperature sputtering process using aluminium into a thickness of 300 to 5,000 angstroms and is formed by a patterning process into a square having a side of approximately 15 to 20 µm. The connecting plug 15 may be formed by smoothing the third insulating interlayer 13 by a CMP process, providing the contact hole and depositing tungsten therein. The passivation film 17 is composed of a silicon oxide film having a thickness of 500 to 2,000 angstroms in the pixel region and a silicon nitride film having a thickness of 2,000 to 10,000 angstroms in the scribe section. A seal section represents a region which is formed by a sealing material for fixing the gap between the two substrates in the liquid crystal. The scribe section represents a section along a scribe region, i.e., the edge of the liquid crystal panel substrate, when a number of reflective liquid crystal panel substrates are formed in a semiconductor wafer and separated along scribe lines into semiconductor chips. The use of a silicon oxide film as the passivation film 17 covering the pixel region can prevent a significant change in a reflectance due to the variation of the film thickness and the wavelength of the light. On the other hand, the passivation film 17 covering a region outside the region in which the liquid crystal is encapsulated (outside the seal section) is formed of a single-layer structure consisting of a silicon nitride film or a double-layer structure consisting of a silicon oxide film and a silicon nitride film thereon in order to further improve reliability, in which the silicon nitride film is superior to the silicon oxide film in terms of water proof property. Although water can readily penetrate from the peripheral region of the substrate contacting to the outer atmosphere and in particular the scribe section, the silicon nitride protective film covering the region can further improve the reliability and durability at the region. A polyimide alignment film is formed on the entire passivation film 17 and subjected to rubbing treatment to form a liquid crystal panel. Figure 7 is a cross-sectional view of a reflective liquid crystal panel using the above-mentioned liquid crystal panel substrate designating 31. As shown in Figure 7, a supporting substrate 32 composed of glass or ceramic is bonded to the back surface of the liquid crystal panel substrate 31 with a bonding agent. A glass substrate 35 at the incident side having a counter electrode (common electrode) composed of a transparent electrode (ITO) for applying a common voltage LC-COM is opposed to the front surface of the liquid crystal panel substrate 31 at an adequate distance, and a known TN (twisted nematic) liquid crystal or a SH (super homeotropic) liquid crystal 37 in which the liquid crystal molecules are substantially vertically aligned in a non-voltage applied state is encapsulated into a gap formed by sealing the periphery of the substrates with a sealing material 36 to form a liquid crystal panel 30. The position of the sealing material is determined so that the pad region 26 is present outside the sealing material 36. The light shielding film 25 on the peripheral circuits face the counter electrode 33 through the liquid crystal 37. Since the LC common voltage is applied to the counter electrode 33 when the LC common voltage is applied to the light shielding film 25, no direct current voltages are applied to the liquid crystal disposed there between. As a result, liquid crystal molecules are always twisted by approximately 90 degrees in the TN liquid crystal or always vertically aligned in the SH liquid crystal. Substrate 31 composed of the semiconductor substrate is bonded to the supporting substrate 32 composed of glass or ceramic at the back surface with a bonding agent, the strength is significantly enhanced. As a result, when these are bonded to the opposing substrate after the supporting substrate 32 is bonded to the liquid crystal panel substrate 31, the gap of the liquid crystal layer is equalised over the entire panel. The thickness of the passivation film 17 can be determined within an adequate range in response to the wavelength of the incident light. The thickness of the silicon oxide passivation film is in a range of 900 to 1,200 angstroms for a pixel electrode reflecting blue light, 1,200 to 1,600 angstroms for a pixel electrode reflecting green light, or 1,300 to 1,900 angstroms for a pixel electrode reflecting red light. The thickness of the silicon oxide film set within the above ranges can suppress the variation of the reflectance in the reflective electrode composed of aluminium to 1 % or less, as shown below. Figures 10 and 11 show the results of dependency of the reflectance of the aluminium reflective electrode on the thickness of the silicon oxide film at different wavelengths. In Figure 10, symbol ◆ represents reflectance at a thickness of 500 angstroms, symbol ▪ represents reflectance at a thickness of 1,000 angstroms, symbol ▴ represents reflectance at a thickness of 1,500 angstroms, and symbol x represents reflectance at a thickness of 2,000 angstroms. In Figure 11, symbol ◆ represents reflectance at a thickness of 1,000 angstroms, symbol ▪ represents reflectance at a thickness of 2,000 angstroms, symbol ▴ represents reflectance at a thickness of 4,000 angstroms, and symbol x represents reflectance at a thickness of 8,000 angstroms. As evidently shown in Figure 11, at a thickness of 4,000 angstroms the reflectance decreases approximately 3% from 0.89 to 0.86 as the wavelength changes from 450 nm to 550 nm and the reflectance decreases approximately 8% from 0.85 to 0.77 as the wavelength changes from 700 nm to 800 nm. At a thickness of 8,000 angstroms the reflectance decreases approximately 3% from 0.89 to 0.86 as the wavelength changes from 500 nm to 600 nm and the reflectance decreases approximately 6% from 0. 86 to 0. 80 as the wavelength changes from 650 nm to 750 nm. In contrast, no significant changes are observed at a thickness of 500 angstroms, 1,000 angstroms, 1,500 angstroms or 2,000 angstroms. These results illustrate that the effective thickness of the silicon oxide film is in a range of 500 to 2,000 angstroms. As a result, a reflective liquid crystal panel having a reduced dependency of the reflectance on the wavelength can be achieved by a thickness of 500 to 2,000 angstroms as the passivation film formed on the reflective electrode. Figures 10 and 11 also demonstrate that the reflectance slightly changes in a specified thickness range of the silicon oxide film. The optimum thickness range of the silicon oxide film for incident and reflecting coloured light was studied. The results are shown in Figures 12 to 14. Figure 12 is a graph illustrating reflectances at various thicknesses of the silicon oxide film in a wavelength range of 420 to 520 nm for blue light neighbouring collars. Figure 13 is a graph illustrating reflectances at various thicknesses of the silicon oxide film in a wavelength range of 500 to 600 nm for green light and its neighbouring collars, and Figure 14 is a graph illustrating reflectances at various thicknesses of the silicon oxide film in a wavelength range of 560 to 660 nm for red light and its neighbouring collars. Figure 12 demonstrates that at a thickness of 800 angstroms the reflectance decreases by approximately 1.6% from 0.896 to 0.882 as the wavelength changes from 440 nm to 500 nm. At a thickness of 1,300 angstroms, the reflectance changes by approximately 0.6% from 0.887 to 0.893 as the wavelength changes from 420 nm to 470 nm and the reflectance is noticeably lower than those at other thicknesses within a wavelength of 420 to 450 nm. In contrast, no significant changes in reflectance are observed and a satisfactorily high reflectance is achieved at a thickness of 900 angstroms, 1,000 angstroms, 1,100 angstroms or 1,200 angstroms. As shown in Figure 13, at a thickness of 1,100 angstroms the reflectance decreases by approximately 1.6% from 0.882 to 0.866 as the wavelength changes from 550 nm to 600 nm. At a thickness of 1,700 angstroms the reflectance is considerably lower than those at other thicknesses within a wavelength of 500 nm to 530 nm. In contrast, no significant changes in reflectance are observed and a satisfactorily high reflectance is achieved at a thickness of 1,250 angstroms, 1,400 angstroms or 1,550 angstroms. As shown in Figure 14, at a thickness of 1,200 angstroms the reflectance decreases by approximately 3.4% from 0.882 to 0.848 as the wavelength changes from 560 nm to 660 nm. At a thickness of 2,000 angstroms the reflectance is considerably lower than those at other thicknesses within a wavelength of 560 nm to 610 nm. In contrast, no significant changes in reflectance are observed and a satisfactorily high reflectance is achieved at a thickness of 1,400 angstroms, 1,600 angstroms or 1,800 angstroms. Figures 12 to 14 demonstrate that when a thickness of the silicon oxide passivation film should be set to within the range of 900 to 1,200 angstroms for a pixel electrode which reflects blue light, 1,200 to 1,600 angstroms for a pixel electrode which reflects green light or 1,300 to 1,900 angstroms for a pixel electrode which reflects red light, the variation of the reflectance for each color can be suppressed to 1 % or less and a satisfactorily high reflectance can be achieved. Each of the graphs shown in Figures 12 to 14 shows the reflectance when a polyimide alignment film is formed with a thickness of 1,100 angstroms on the passivation film. The optimum thickness range of the silicon oxide film slightly shifts with a different thickness of the alignment film. Regarding the thickness range of the alignment film, it is not capable of aligning if its thickness is less than 300 angstroms in view of suppressing the variation of reflectance, whereas the polyimide absorbs high wavelength light and low wavelength light and has appreciable capacitance which is connected in series to the liquid crystal capacitor in the equivalent circuit; therefore it is preferred that the thickness of the alignment film be within a range of 300 to 1,400 angstroms. If a decrease in the alignment capability due to a decreased thickness of the alignment film is anticipated, the thickness is preferably in a range of 800 to 1,400 angstroms. When the thickness of the alignment film is within the above-mentioned range and the thickness of the silicon oxide film in the liquid crystal panel for each color is within the above-mentioned range, the variation of the reflectance can be satisfactorily suppressed to 1% or less. Accordingly, when color display is performed in one liquid crystal panel, the thickness of the passivation film on the reflective electrode can be varied according to the color of each pixel. In a configuration where an RGB color filter is formed on the inner face an opposing substrate facing a reflective substrate having pixel electrodes and the coloured light passing through the color filter is reflected from the pixel electrodes, a single plate-type reflective liquid crystal panel having high reflectance can be obtained by setting the thickness of the passivation film formed on the pixel electrode reflecting red light from the red (R) color filter to 1,300 to 1,900 angstroms, the thickness of the passivation film formed on the pixel electrode reflecting green light from the green (G) color filter to 1,200 to 1,600 angstroms and the thickness of the passivation film formed on the pixel electrode reflecting blue light from the blue (B) color filter to 900 to 1,200 angstroms. The liquid crystal panel can also be used as a light valve for a single plate-type projection display device. The color light may be formed by a means which converts light incident on each pixel electrode into the color light, for example, a dichroic mirror, instead of the color filter. The liquid crystal panel in accordance with the present invention can also be used in a projection display device described later which is provided with a liquid crystal panel reflecting red light, a liquid crystal panel reflecting green light and a liquid crystal panel reflecting blue light. In this case, it is preferred that the thicknesses of the silicon oxide passivation film be in a range of 1,300 to 1,900 angstroms for the liquid crystal panel in the light valve for modulating red light, in a range of 1,200 to 1,600 angstroms for the liquid crystal panel in the light valve for modulating green light, and in a range of 900 to 1,200 angstroms for the liquid crystal panel in the light valve for modulating blue light, respectively. Figure 3 is a planar layout view of the liquid crystal substrate of figure 1 on the reflection side. As shown in Figure 3, the data line 7 and the gate line 4 are formed so as to cross each other. The hatched region H of the gate line 4 in Figure 3 act as the gate electrode 4a and a channel region 5c of MOSFET for pixel switching is provided on the substrate surface thereunder. The source and drain regions 5a and 5b are formed on the substrate surface at both sides (at the upper and lower sides in Figure 3) of the channel region 5c. The source electrode 7a connecting to the data line is formed so as to extend from the data line 7, extended along the vertical direction in Figure 3, and is connected to the source region 5a of the MOSFET through the contact hole 6b. The P-type doping region as a constituent of one terminal of the holding capacitor is formed so as to link to the P-type doping region in the adjacent pixel in the direction parallel to the gate line 4 (the pixel line direction). It is connected to a power line 70 provided outside the pixel region through contact holes 71 so that a given voltage Vss such as 0 volt (ground voltage), is applied. The given voltage Vss may be close to a voltage of the common electrode provided on the opposing substrate, a central voltage of the amplitude of image signals supplied to close to the data line, or an intermediate voltage between the common electrode voltage and the amplitude central voltage of the image signals. The connection of the P-type doping region 8 to the voltage Vss at the outside of the pixel region stabilises the voltage of one electrode of the holding capacitor and the holding voltage held in the holding capacitor during the non-selection time period of the pixel (the non-leading time of the MOSFET), and decreases the variation of the voltage applied to the pixel electrode during one frame time period. Since the P-type doping region 8 is provided near the MOSFET and the voltage of the P-type well is simultaneously fixed, the substrate voltage of the MOSFET is stabilised and the variation of a threshold voltage due to the reverse gate effect can be prevented. Although not shown in the drawings, the power line 70 is also used as a line which supplies a given voltage Vss as a well voltage to a P-type well region (separated from the well of the pixel region) in the peripheral circuit provided outside the pixel region. The power line 70 is formed of the first metal layer which is the same as the data line 7. Each pixel electrode 14 has a rectangular shape and is provided in close proximity to the adjacent pixel electrode 14 at a given distance, for example, 1 µm, so as to reduce the light leaked between the pixel electrodes as much as possible. Although the centre of the pixel electrode is shifted from the centre of the contact hole 16 in the drawings, it is preferable that both centres substantially agree with each other due to the following reason. Since the second metal layer 12 having a light shielding effect has an opening 12a at the periphery of the contact hole 16, if the opening 12a were provided near the edge of the pixel electrode 14 random reflection would be caused between the second metal layer 12 and the back surface of the pixel electrode of the light incident from the gap between the pixel electrodes in which the light reaches the opening 12a and leaks from the opening through the lower substrate. It is therefore preferable that the centre of the pixel electrode and the centre of the contact hole 16 substantially agree with each other, because the distance in which the light incident from the gap with the adjacent pixel reaches the contact hole is almost equalised at the edge of each pixel electrode and the light barely reaches the contact hole which will form the light incident on the substrate side. Although the above-mentioned embodiment includes the N-channel-type MOSFET for pixel switching and a P-type doping layer of semiconductor region 8 as one electrode of the holding capacitance, an N-type well region 2, a P-channel-type MOSFET for pixel switching and a N-type doping layer of semiconductor region as one electrode of the holding capacitance are also possible. In this case, it is preferable that a reference voltage V DD is applied to the N-type doping layer as one electrode of the holding capacitance as in the P-type well region. It is preferred that the reference voltage V DD be a higher voltage since it applies an voltage to the N-type well region. For example, when a voltage of image signals applied to the source and drain in the MOSFET for pixel switching is 5 volts, it is preferable that the reference voltage V DD also be 5 volts. A high voltage, e.g. 15 volts, is applied to the gate electrode 4a of the MOSFET for pixel switching, whereas logic circuits, such as a shift register, in the peripheral circuit, are driven by a low voltage, e.g. 5 volts (but a part of the peripheral circuit, for example a circuit for applying a scanning signal to the gate line is driven at 15 volts). It is conceivable that the thickness of a gate insulating film in an FET as a peripheral circuit which is driven at 5 volts is lower than that of a gate insulating film of an FET for pixel switching (by forming the gate insulating film by another process or by etching the surface of the gate insulating film of the FET in the peripheral circuit) in order to improve the response of the FET in the peripheral circuit and increase the operation rate of the peripheral circuit (in particular, a shift resistor in a driving circuit at the data line side requiring high speed scanning). When such a technology is applied, the thickness of the gate insulating film of the FET as a constituent of the peripheral circuit can be reduced to approximately one third to one fifth the thickness of the gate insulating film of the FET for pixel switching (for example, 80 to 200 angstroms) in view of voltage resistance. The driving wave form in the first embodiment has a shape as shown in Figure 8. In the drawing, V G represents scanning signals applied to the gate electrode of the MOSFET for pixel switching, the time period tH1 represents a selection time period (scanning time period) to lead or switch the MOSFET of the pixel. Further, V d represents the maximum amplitude of the image signals applied to the data line, V c represents a central voltage of the image signals, and LC-COM represents a common voltage applied to the opposing (common) electrode formed on the opposing substrate facing the reflective electrode substrate. The voltage applied between the electrodes of the holding capacitor is determined by the difference between the image signal voltage V d applied to the data line as shown in Figure 8 and a given voltage V ss such as 0 volts, applied to the P-type semiconductor region 8. The difference between the image signal voltage V d and the central voltage V c of the image signal, i.e., approximately 5 volts, is, however, sufficient for the voltage difference which is to be applied to the holding capacitor (the common voltage LC-COM applied to the opposing (common) electrode provided on the opposing substrate of the liquid crystal panel is shifted by ΔV from V c , whereas the voltage actually applied to the pixel electrode is also shifted by ΔV and becomes V d -Δ V). The first embodiment therefore permits that the doping region 8 forming one terminal of the holding capacitor is set to reverse polarity to the well (N-type for the P-type well) and it is connected to a voltage of near V c or LC-COM at the periphery of the pixel region so as to hold a voltage different from the well voltage (for example, V ss for the P-type well). By simultaneously forming the insulating film 9b just below the polysilicon or metal silicide layer as one electrode 9a of the holding capacitor with the gate insulating film of the FET forming a peripheral circuit, not the gate insulating film of the FET for pixel switching, the thickness of the insulating film in the holding capacitor can be reduced to one third to one fifth compared to the above-mentioned embodiment and the capacitance can be increased by three to five times. Referring to Figure 7, the light shielding film 25 is composed of the third metal layer which is formed by the same step as the pixel electrode 14 shown in Figure 1 so as to apply a given voltage, e.g. a power voltage, the central voltage V c of the image signal or a common voltage LC-COM. Application of the given voltage to the light shielding film 25 can reduce reflection compared to a floating voltage and other voltages. The light shielding film 25 may be in a floating voltage (non-applied voltage) state so as to non-apply to the liquid crystal 37 by this film. Reference numeral 26 represents a pad used for supplying the power voltage or a pad region provided with a terminal. Figure 2 is a cross-sectional view of an embodiment of a CMOS circuit device forming a peripheral circuit, e.g. a driving circuit, outside the pixel region, as indicated in Figure 6. In Figure 2, the positions having the same numbers as Figure 1 represent the metal layer, insulating film and semiconductor region which are formed by the same step. In Figure 2, an N-channel MOSFET and a P-channel MOSFET forming a peripheral circuit (CMOS circuit) such as a driving circuit, have gate electrodes 4a, 4a', source and drain regions 5a (5b) and 5a' (5b'), an N-type doping region and a P-type doping region, and channel regions 5c and 5c'. The contact region 80 for supplying a constant voltage V ss to the P-type doping region B as one electrode of the holding capacitor in Figure 1 is formed by the same step as the P-type doping region 5a' (5b') as the source (drain) region of the P-channel MOSFET. Source electrodes 27a and 27c are formed by the first metal layer and connected to the power voltage (any one of 0 volt, 5 volts and 15 volts), and a drain electrode 27b is formed by the first metal layer. A wiring layer 32a is composed of the second metal layer and is used as a wire for connecting between the devices forming a peripheral circuit. A power wiring layer 32b composed of the second metal layer and acts as a light shielding film, which can be connected to any one of V c , LC-COM, power voltage, a constant voltage, e.g. 0 volt, and a variable voltage. The shielding film formed from the same layer as the wiring layers 32a and 32b may be in a floating voltage (non-applied voltage) state by separating with the wiring layers 32a and 32b. A third metal layer 14' is used as a light shielding film in the peripheral circuit and prevents erroneous operation of the peripheral circuit due to unstable voltage in the semiconductor region which is caused by carriers formed during light transmittance in the semiconductor region of the peripheral circuit. Accordingly, the peripheral circuit is also shielded from light by the second and third metal layers. As described above, the passivation film 17 in the peripheral circuit may be a protective film composed of a silicon nitride film or a double-layered film of silicon oxide and silicon nitride thereon, in which the silicon nitride protective film is superior to the silicon oxide film as the passivation film in the pixel region. The source/drain region of the MOSFET forming the peripheral circuit of this embodiment may be formed by a self-alignment process, although it not limited to this. The source/drain region of each MOSFET may have a LDD (lightly doped drain) structure or a DDD (double doped drain) structure. It is preferred that the FET for pixel switching have an offset structure in which the gate electrode is distant from the source/drain region, taking into consideration that the FET for pixel switching is driven by a high voltage and the leakage current must be prevented. Referring to Figure 4, this shows a preferred embodiment of an edge structure of a reflecting electrode (pixel electrode) substrate. In Figure 4, the parts having the same identification numbers represent the layers and semiconductor regions formed by the same steps as those of Figures 1 and 2. The edge of the laminate composed of the insulating interlayer and the metal layer and its side wall has a monolithic protective structure in which a silicon nitride film 18 is formed on the silicon oxide passivation film 17 which covers the pixel region and the peripheral circuit. The edge corresponds to each of the edges of substrates (semiconductor chip) which are formed on a silicon wafer and separated by dicing along the scribe lines. The lower right portion of the step in Figure 4 corresponds to the scribe region. Since the upper section and side wall of the substrate are covered with the silicon nitride protective film at the edge, water and the like will barely penetrate from the edge, durability is improved and the yield is improved due to reinforcement of the edge. In this embodiment, a sealing material 36 for encapsulating the liquid crystal is provided on the monolithic protective structure which is perfectly planarized. The distance to the opposing substrate therefore can be maintained constant regardless of variation of the thickness whether the insulating interlayer and the metal layer are present or not. Since the above configuration permits a single-layered silicon oxide protective film on the reflecting electrode forming a pixel electrode, it can suppress a decrease in reflectance and dependence of the reflectance on the wavelength. As shown in Figure 4, in this embodiment, the third metal layer 14' is the same as the layer 14 which is used as the light shielding film in the peripheral circuit region and the reflective electrode of the pixel, and it is connected to the predetermined voltage through the second and first metal layers 12' and 7' and fixed to the substrate voltage. Also the second metal layer 12' or the first metal layer 7' may be extended under the sealing material 36 instead of the third metal layer 14' to be used as a layer for fixing the voltage. This is capable of preventing static electricity during the formation of the liquid crystal substrate and liquid crystal panel and after the formation of the liquid crystal panel. Figure 5 shows another embodiment in accordance with the present invention. Figure 5 corresponds to the cross-sectional view along line I-I in the planar layout in Figure 3, as in Figure 1a. In Figure 5, the sections having the same identification numbers as Figures 1 and 2 represent the layers and the semiconductor regions formed by a similar process to the embodiment shown in these drawings. In this embodiment, a silicon nitride film 13b is formed under the insulating interlayer 13a composed of the TEOS film (partly including a remaining SOG film during etching) between the reflecting electrode 14 and the light shielding layer 12 thereunder. Alternatively, a silicon nitride film 13b may be formed on the TEOS film 13a. The use of a configuration having an additional silicon nitride film inhibits penetration of water and thus improves wet resistance. The thickness of the passivation film on the reflecting electrode is similar to the embodiment shown in Figure 1. Figure 16 shows another embodiment in accordance with the present invention. Figure 16 corresponds to the cross-sectional view along line I-I in the planar layout in Figure 3, as in Figure 1. In Figure 16, the sections having the same identification numbers as Figures 1 and 2 represent the layers and the semiconductor regions formed by a similar process to the embodiment shown in those drawings. In this embodiment a silicon nitride film 13b is formed on the insulating interlayer 13a composed of the TEOS film (partly including a remaining SOG film during etching) between the reflecting electrode 14 and the metal layer thereunder as the shielding layer 12. The silicon nitride film 13a can be planarized by a CMP process or the like. The formation of the silicon nitride film decreases openings in the silicon nitride section compared to the embodiment in Figure 5, and prevents penetration of water, resulting in further improvement in moisture resistance. The space between the reflecting electrode and the adjacent electrode is formed of a protective insulating film 17 and the silicon nitride 13b. Since the refractive index of the silicon nitride is 1.9 to 2.2 and higher than the refractive index 1.4 to 1.6 of the silicon oxide used in the protective insulating film 17, the incident light on the protective insulating film 17 from the liquid crystal side is reflected at the interface with the silicon nitride film 13b because of the difference of the refractive indices. Since the light incident on the interlayer is decreased, unstable voltage in the semiconductor region caused by carriers which are formed by light transmittance in the semiconductor region can be prevented. In this embodiment, the silicon nitride film 13b may be formed after planarization of the insulating interlayer 13a composed of the TEOS film by a CMP process or the like. In general, a film having a thickness of 8,000 to 12,000 angstroms which corresponds to local steps must be deposited by, for example, a CMP process in order to offset the local steps. The silicon nitride film generally causes a high stress on the lower film as its thickness increases. In this embodiment, since the insulating interlayer 13a is planarized by polishing by means of a CMP process and the silicon nitride film 13b is formed thereon, the thickness of the silicon nitride film 13b deposited by a CMP process or the like can be reduced, and thus the stress of the silicon nitride film 13b can be relaxed. Since the space between the reflecting electrode 14 and the adjacent reflecting electrode is composed of the protective insulating film 17 and silicon nitride 13b in this case, the light incident on the interlayer decreases, and unstable voltage in the semiconductor region due to carriers formed by light transmittance in the semiconductor region can be prevented. It is preferable in this embodiment that the thickness of the silicon nitride be 2,000 to 5,000 angstroms. A thickness of 2,000 angstroms or more improves moisture resistance of the silicon nitride film 13b, whereas a thickness of 5,000 angstroms or less decreases the etching depth of the contact hole 16, permits ready etching and relaxes the stress on the lower film. The thickness of the passivation film on the reflecting electrode is the same as the embodiment in Figure 1. The above description includes a configuration of a reflective liquid crystal panel substrate using a semiconductor substrate and a liquid crystal panel using the same. A configuration of a reflective liquid crystal panel substrate using an insulating substrate will now be described. Figure 17 is a cross-sectional view of a configuration of a pixel in a reflective liquid crystal panel substrate. Figure 17 is a cross-sectional view along line I-I in the planar layout in Figure 3, as in Figure 1. In this embodiment, a TFT is used as a transistor for switching pixels. In Figure 17, the sections having the same identification numbers as Figures 1 and 2 represent the layers and the semiconductor regions having the same functions as in those drawings. A quartz or non-alkaline glass substrate 1 has formed thereon, a single crystal, polycrystalline or amorphous silicon film (regions 5a, 5b, 5c and 8) and insulating films 4b and 9b having a double layer structure composed of a silicon oxide film formed by thermal oxidation and a silicon nitride film formed by a CVD process are formed on the silicon film. An N-type impurity is doped in the regions 5a, 5b and 8 of the silicon film before the formation of the upper silicon nitride film among the insulating film 4b to form a source region 5a and a drain region 5b of the TFT and an electrode region 8 of the holding capacitor. A wiring layer composed of polysilicon or a metal silicide is formed as a gate electrode 4a of the TFT and the other electrode 9a of the holding capacitor is formed on the insulating film 4b. As described above, the TFT comprising the gate electrode 4a, the gate insulating film 4b, the channel 5c, the source 5a and the drain 5b and the holding capacitor comprising the electrodes 8 and 9 and the insulating film 9b are formed. A first insulating interlayer 6 composed of silicon nitride or silicon oxide is formed on the wiring layers 4a and 9a, and a source electrode 7a which is connected to the source region 5a through a contact hole formed in the insulating film 6 is formed of a first metal layer composed of aluminium. A second insulating interlayer 13 having a double-layer structure composed of a silicon oxide film and a silicon nitride film is formed on the first metal layer. The second insulating interlayer 13 is planarized by a CMP process and a pixel electrode 14, as a reflection electrode, composed of aluminium is formed thereon corresponding to each pixel. The electrode region 8 of the silicon film is electrically connected to the pixel electrode 14 through a contact hole 16. Such a connection is achieved by embedding a connecting plug 15 composed of a high melting point metal, such as tungsten, as in Figure 1. As described above, since the reflecting electrode is formed above the TFT and holding capacitor formed on the insulating substrate, the pixel electrode region is expanded and the holding capacity has a large area below the reflecting electrode as in the planar layout in Figure 3. A high aperture ratio (high reflectance) therefore can be achieved even in a high definition panel (having smaller pixels) and an applied voltage can be sufficiently retained in each pixel, resulting in stable driving. A passivation film 17 composed of a silicon oxide film is formed on the reflecting electrode 14, as in the above-mentioned embodiments. The thickness of the passivation film 17 is similar to that in those embodiments, and a reflective liquid crystal panel substrate having a small variation of the reflectance with the wavelength of the incident light can be obtained. A comprehensive configuration of the liquid crystal panel substrate and a configuration of the liquid crystal panel are similar to those in Figures 6 and 7. In Figure 17, no insulating interlayer 11 and light shielding layer 12 are provided unlike Figure 1. These layers can also be provided as in Figure 1 in order to prevent leakage of the incident light from the gap to the adjacent pixel on the TFT. If incident light from the bottom of the substrate is anticipated, a light shielding layer may be provided under the silicon films 5a, 5b and 8. Although the drawing includes a top gate type in which the gate electrode is provided above the channel, a bottom gate type in which a gate electrode is previously formed and a silicon film as a channel is provided thereon through a gate insulating film is also possible. Also a double layer structure composed of a silicon oxide film and a silicon nitride film in the peripheral circuit region as in Figure 4 can improve moisture resistance. Figure 9 shows an example of an electronic device using liquid crystal panels in accordance with the present invention, and is a planar schematic diagram of the main section of a projector (projection display device) using a reflective liquid crystal panel in accordance with the present invention as a light valve. Figure 9 is a cross-sectional view of an XZ plane which passes through the centre of an optical element 130. This projector includes a polarising illuminator comprising light source 110 comprising a lamp 111 and reflector 112, provided along the system light axis L, an integrated lens 120, a polarising device 130, a polarising illuminator 100 including the polarising device 130, a polarised beam splitter 200 which reflects a S-polarised light beam emerging from the polarising illuminator 100 by a S-polarised light beam reflecting face 201, a dichroic mirror 412 which separates the blue (B) light component from the light reflected on the S-polarised light beam reflecting face 201 of the polarised beam splitter 200, a reflection liquid crystal light valve 300B modulating the separated blue (B) light, a dichroic mirror 413 which separates a red (R) light component from the light beam not containing the blue light component, a reflection liquid crystal light valve 300R modulating the separated red (R) light, a reflection liquid crystal light valve 300G modulating the residual green (G) light passed through the dichroic mirror 413, and a projection optical system 500 which includes a projection lens projecting a synthesised light on a screen 600 in which the modulated light beams from the three reflection liquid crystal light valves 300R, 300G, and 300B are combined through the dichroic mirrors 412 and 413 and the polarised beam splitter 200. These three reflection liquid crystal valves 300R, 300G and 300B are provided with the above-mentioned liquid crystal panels, respectively. The random polarised light beams emerging from the light source 110 are divided into a plurality of intermediate light beams by the integrated lens 120, converted to single-polarisation light beams (S-polarised light beam) substantially having a polarised light direction with the polarising device 130 which has a second integrated lens at the light incident side, and are incident on the polarised beam splitter 200. The S-polarised light beams emerging from the polarising device 130 are reflected from the S-polarised light beam reflecting face 201 of the polarised beam splitter 200, the blue (B) light beam among the reflected light beams is reflected on the blue light reflecting layer of the dichroic mirror 412 and modulated by the reflection liquid crystal light valve 300B. The red (R) light beam among the light beams passed through the blue light reflecting layer of the dichroic mirror 412 is reflected on the red light reflecting layer of the dichroic mirror 413 and modulated by the reflection liquid crystal light valve 300R. Further, the green (G) light beam passed through the red light reflecting layer of the dichroic mirror 413 is modulated by the reflection liquid crystal light valve 300G. In such a manner, the color light beams modulated by the reflection liquid crystal light valves 300R, 300G and 300B are combined by the dichroic mirrors 412 and 413 and the polarised beam splitter 200, and the combined light is projected through the projection optical system 500. The reflective liquid crystal panel used in the reflection liquid crystal light valves 300R, 300G and 300B contains a TN liquid crystal (longitudinal axes of liquid crystal molecules are substantially aligned in the direction parallel to the panel substrate when no voltage is applied) or a SH liquid crystal (longitudinal axes of liquid crystal molecules are substantially aligned in the direction perpendicular to the panel substrate when no voltage is applied). When a TN liquid crystal is used, in a pixel (OFF pixel) in which a voltage applied to the liquid crystal layer intervened between the reflecting electrode of the pixel and the common electrode of the opposing substrate is lower than a threshold voltage, the incident color light is elliptically polarised in the liquid crystal layer, is reflected from the reflecting electrode and emerges from the liquid crystal layer in which the polarisation axis of the emerging light is shifted by 90 degrees from the incident light and elliptically polarised. On the other hand, in a pixel (ON pixel) in which a voltage is applied to the liquid crystal layer, the incident color light reaches the reflection electrode without polarisation, is reflected and emerged, in which the emerging light has the same polarisation axis as the incident light. Since the alignment angle of the liquid crystal molecule of the TN liquid crystal varies in response to the voltage applied to the reflecting electrode, the angle of the polarisation axis of the reflected light in relation to the incident light varies in response to the voltage applied to the reflecting electrode through the transistor in the pixel. When a SH liquid crystal is used, in a pixel (OFF pixel) in which the voltage applied to the liquid crystal layer is lower than a threshold voltage, the incident color light reaches the reflection electrode without polarisation, is reflected and emerges, in which the emerging light has the same polarisation axis as the incident light. On the other hand, in a pixel (ON pixel) in which a voltage applied to the liquid crystal layer, the incident color light is elliptically polarised in the liquid crystal layer, reflected on the reflecting electrode and emerges from the liquid crystal layer in which the polarisation axis of the emerging light is shifted by 90 degrees from the incident light and the emerged light is elliptically polarised. Since the alignment angle of the liquid crystal molecule of the SH liquid crystal varies in response to the voltage applied to the reflecting electrode as in the TN liquid crystal, the angle of the polarisation axis of the reflected light in relation to the incident light varies in response to the voltage applied to the reflecting electrode through the transistor in the pixel. Among the color light beams reflected from pixels in these liquid crystal panels, the S-polarised light component does not pass through the polarised beam splitter 200 which reflects the S-polarised light and transmits P-polarised light. The light beams passed through the polarised beam splitter 200 form an image. The projected image is a normally-white display when a TN liquid crystal is used in the liquid crystal panel because the reflected light beams in OFF pixels reach the projection optical system 500 and the reflected light beams in ON pixels do not reach the lens, and a normally-black display when a SH liquid crystal is used because the reflected light beams in OFF pixels do not reach the projection optical system and the reflected light beams in ON pixels reach the projection optical system 500. Since reflective liquid crystal panels permit larger pixel electrodes compared to transmission active matrix liquid crystal panels, high reflectance is achieved, high density images can be projected at high contrast and projectors can be miniaturised. As shown in Figure 7, the peripheral circuit section of the liquid crystal panel is covered with the light shielding film, and the same voltage (for example, the LC common voltage; if the LC common voltage is not used, the peripheral counter electrode is separated from the counter electrode in the pixel) is applied to the section and the counter electrode formed at the position in which the opposing substrate is opposed. Almost zero volt is therefore applied to the liquid crystal intervened between them and the liquid crystal is the same as an OFF state. As a result, in the TN liquid crystal panel the periphery of the image region exhibits an entire white display in response to the normally white display, whereas in the SH liquid crystal panel the periphery of the image region exhibits an entire black display in response to the normally-black display. Further satisfactory results are obtained when the silicon oxide forming the passivation film of the light valve 300R as the first reflective liquid crystal panel modulating red light separated by the polarised beam splitter 200 as a color separation means which separate the light from the light source 110 into three primaries has a thickness in a range of 1,300 to 1,900 angstroms, the silicon oxide forming the passivation film of the light valve 300G as the second reflective liquid crystal panel modulating green light has a thickness in a range of 1,200 to 1,600 angstroms, and the silicon oxide forming the passivation film of the light valve 300B as the third reflective liquid crystal panel modulating blue light has a thickness in a range of 900 to 1,200 angstroms. In accordance with the above-mentioned embodiment, a voltage applied to each of pixels in the reflective liquid crystal panels 300R, 300G and 300B is sufficiently retained and the pixel electrode has a significantly high reflectance, resulting in clear projected images. Figure 15 illustrates electronic devices using the reflective liquid crystal panels in accordance with the present invention. In these electronic devices, the reflective liquid crystal panel is used as a direct viewing-type reflective liquid crystal panel, not as a light valve which is used together with a polarised beam splitter. The reflecting electrode need therefore not be a perfect mirror surface and can tolerate unevenness. Figure 15(a) is an isometric view of a portable telephone 1000 with a liquid crystal display 1001 using a reflective liquid crystal panel in accordance with the present invention. Figure 15(b) shows a watch-type electronic device having a main body 1100 and a liquid crystal display 1101 in accordance with the present invention. Since the liquid crystal panel has high definition pixels compared to conventional watch displays and is capable of displaying television images, a watch-type television can be achieved. Figure 15(c) shows a portable information processing unit 1200, e.g. a word processor or a personal computer having an input section 1202 such as a keyboard, a display 1206 using a reflective liquid crystal panel in accordance with the present invention, an information processing unit main body 1204. Since these electronic devices are driven by batteries, the use of the reflective liquid crystal panel having no light source lamp can lengthen the battery life. Since the peripheral circuits can be stored in the panel substrate, significant reduction of parts, and weight and size reduction can be achieved. In the above-mentioned embodiments, although a TN type and a homeotropic alignment SH type are exemplified as a liquid crystal of the liquid crystal panel, other types of liquid crystals are also available. As described above, a reflective liquid crystal panel substrate in accordance with the present invention is provided with a passivation film, and thus has improved reliability. The use of a silicon oxide film having a thickness of 500 to 2,000 angstroms as the passivation reduces dependence of reflectance of the pixel electrode on variation of the thickness. In particular, the silicon oxide film having a thickness of 500 to 2,000 angstroms exhibits slight dependence of the reflectance on the wavelength and thus can reduce variation of the reflectance. The thickness of the silicon oxide film as the passivation film is set to an adequate range in response to the wavelength of the incident light, e.g. 900 to 1,200 angstroms for a pixel electrode reflecting blue light, 1,200 to 1,600 angstroms for a pixel electrode reflecting green light, and 1,300 to 1,900 angstroms for a pixel electrode reflecting red light. Variation of the reflectance in each color can therefore be suppressed to 1 % or less. As a result, reliability of the liquid crystal panel can be improved, and the image quality of a projection display device using the reflective liquid crystal panel as a light valve can be improved. Since the thickness of the silicon oxide film as the passivation film is determined in response to the thickness of the alignment film formed thereon and the thickness of the alignment film is set to a range of 300 to 1,400 angstroms, variation of the reflectance of the liquid crystal can be effectively prevented. In a reflective liquid crystal panel in which a pixel region comprising a matrix of pixel electrodes and peripheral circuits, such as a shift register and a control circuit, provided outside the pixel region are formed on the same substrate, a passivation film composed of a silicon oxide film is formed above the pixel region and a passivation film composed of a silicon nitride film is formed above the peripheral circuits. The use of the silicon nitride film above the peripheral circuits further secures protection of the peripheral circuits and improves reliability. A silicon nitride film is provided as an insulating interlayer between the reflecting electrode and a metal layer thereunder instead of the passivation film above the reflective electrode or together with the passivation film composed of the silicon oxide film. The moisture resistance is therefore improved, a MOSFET for pixel switching and a holding capacitor can be prevented from corrosion due to water or the like. A monolithic protective structure in which a silicon nitride film is formed on a passivation film composed of a silicon oxide film is provided over the edge and side wall of a laminate of an insulating interlayer formed at the periphery of the pixel region and a metal layer shielding the periphery. The waterproof property at the edge of the liquid crystal panel in which water readily penetrates is therefore improved and durability is also improved due to its reinforcement effect. The foregoing description has been given by way of example only and it will be appreciated by a person skilled in the art that modifications can be made without departing from the scope of the present invention.

Claims: A liquid crystal panel substrate comprising a matrix (20) of reflective electrodes (14), a substrate member (1), a respective switching element (4a-5c) formed on the substrate member for applying a voltage to each reflective electrode, wherein a passivation film (17) of silicon oxide is formed over said reflective electrodes, characterised in that a thickness of said passivation film is 1200 to 1600 angstroms (120 to 160 nm) for reflection of green light. A liquid crystal panel substrate comprising a matrix (20) of reflective electrodes (14), a substrate member (1), a respective switching element (4a-5c) formed on the substrate member for applying a voltage to each reflective electrode, wherein a passivation film (17) of silicon oxide is formed over said reflective electrodes, characterised in that a thickness of said passivation film is 1300 to 1900 angstroms (130 to 190 nm) for reflection of red light. A liquid crystal panel comprising a liquid crystal panel substrate, a transparent substrate (31) at a light incident side having a counter electrode (33), and a liquid crystal (37) encapsulated into a gap between said liquid crystal substrate and said transparent substrate, the liquid crystal panel substrate comprising a matrix (20) of reflective electrodes (14) on a substrate member (1), a respective switching element (4a-5c) formed on the substrate member for applying a voltage to each reflective electrode, wherein a passivation film (17) of silicon oxide is formed over said reflective electrodes, and a thickness of said passivation film (17) for reflection of red light being in a range of 1300 to 1900 angstroms (130 to 190 nm), the thickness of said passivation film (17) for reflection of green light being in a range of 1200 to 1600 angstroms (120 to 160 nm), and the thickness of said passivation film (17) for reflection of blue light being in a range of 900 to 1200 angstroms (90 to 120 nm). A projection display device comprising a light source (110), three reflective liquid crystal panels (300R, 300G, 300B) for modulating the light from said light source, and a projection lens (500) for projecting the light modulated by said reflective liquid crystal panel; each liquid crystal panel including a liquid crystal panel substrate, a transparent substrate (31) at a light incident side having a counter electrode (33) and a liquid crystal (37) encapsulated into a gap between said liquid crystal substrate and said transparent substrate; each liquid crystal panel substrate comprising a matrix (20) of reflective electrodes (14) on a substrate member (1), a respective switching element (4a-5c) formed on the substrate member for applying a voltage to each reflective electrode, wherein a passivation film (17) of silicon oxide is formed over said reflective electrodes and said projection display device further comprising color separation means (412, 413) for separating the light from said light source into three primaries, a first reflective liquid crystal panel (300R) for modulating red light from said color separation means, a second reflective liquid crystal panel (300G) for modulating green light from said color separation means, and a third reflective liquid crystal panel (300B) for modulating blue light from said color separation means, a thickness of the silicon oxide passivation film of said first reflective liquid crystal panel being in a range of 1300 to 1900 angstroms (130 to 190 nm), the thickness of the silicon oxide film forming a passivation film of said second reflective liquid crystal panel being in a range of 1200 to 1600 angstroms (120 to 160 nm), and the thickness of the silicon oxide film forming a passivation film of said third reflective liquid crystal panel being in a range of 900 to 1200 angstroms (90 to 120 nm).

Inventors: YASUKAWA MASAHIRO, YASUKAWA, MASAHIRO
Applicants: SEIKO EPSON CORP, SEIKO EPSON CORPORATION
Application year: 1997
Main classification: G02F1
IPC codes: G02F1, H04N5, H04N9