Process for the preparation of Benzotriazolylalkylene bisphenol compounds

Abstract: A process for preparing benzotriazolyl-alkylene bisphenol compounds which comprises reacting a 2-hydroxyphenylbenzotriazole and a 2,4-substituted phenol with an aldehyde in the presence of a basic catalyst and an amine compound; benzotriazolyl-alkylene bisphenol compounds obtained by the process; and stabilized organic materials containing the resulting benzotriazolyl-alkylene bisphenol compounds in an amount of 0.01-10 percent by weight. It is possible to prepare the benzotriazolyl-alkylene bisphenol compounds at a high yield, and organic materials can be effectively stabilized with the resulting compounds.

Description: The present invention relates to a process for the preparation of benzotriazolyl-alkylene bisphenol compounds which function as both light stabilizing agents and antioxidants. 2-hydroxyphenylbenzotriazole compounds are known as light stabilizers for synthetic resins and the like, but because these compounds are of lower molecular weight than the compounds of the invention to be described hereunder, and thus undergo volatilization during working of resins and with the passage of time, they have not been able to stabilize organic materials for extended periods. Also, antioxidants consisting mainly of alkyl-substituted phenols, represented by 2,6-di-tert.-butyl-p-cresol, as well, have been unable to provide long-term stabilization of organic materials for the same reason. Czechoslovakian Patent No. 157,761 discloses preparation of benzotriazolyl-alkylene bisphenol compounds by a process involving synthesis of the corresponding substituted 2,2'-methylenebisphenol, coupling the bisphenol compound with o-nitrobenzene diazonium salt, and then reducing and cyclizing it by common methods. However, this patent does not disclose the amount of yields, nor have the present inventors been able to confirm production of the desired compounds by reproducing the examples or carrying our the synthesis experiments. It is the major object of the present invention to provide a process capable of preparing benzotriazolyl-alkylene bisphenol compounds at a high yield. As a result of much diligent research, the present inventors have accomplished the present invention after finding that benzotriazolyl-alkylene bisphenol compounds can be prepared, at a high yield, by reacting 2-hydroxyphenylbenzotriazoles and 2,4-substituted phenols with aldehydes in the presence of basic catalysts and amines, that the resulting compounds have high lipophilicity and satisfactory resistance to volatilization, and that organic materials stabilized with such compounds are effectively protected even when continuously exposed for long periods to the action of outside air and light. According to the present invention, therefore, there is provided a process for preparing a benzotriazolyl-alkylene bisphenol compound represented by general formula (3): wherein X represents hydrogen, a halogen, or an alkyl, cycloalkyl, alkoxy or alkylaryl group, R 1 represents an alkyl, cycloalkyl, aryl, alkoxy or arylalkyl group, R 2 represents hydrogen or an alkyl or aryl group, and R 3 and R 4 may be the same or different and each represent an alkyl, cycloalkyl, aryl or alkylaryl group, which process comprises reacting a 2-hydroxyphenylbenzotriazole represented by general formula (1): wherein X and R 1 are as defined above, and a 2,4-substituted phenol represented by general formula (2): wherein R 3 and R 4 are as defined above, with an aldehyde selected from the group consisting of formaldehyde, paraformaldehyde, trioxane, tetraoxymethylene, alkylaldehyde and arylaldehyde, in the presence of a basic catalyst and an amine compound. There is further provided a process for preparing a benzotriazolyl-alkylene bisphenol compound represented by the aforementioned general formula (3) and a stabilized organic material containing the compound in an amount of 0.01-10 percent by weight. Among the compounds represented by the aforementioned general formula (3), those compounds which are represented by the following general formula (4): wherein R 5 and R 6 may be the same or different and each represents an alkyl group with 1-8 carbon atoms, are novel compounds which have not hitherto been described in literature, and are particularly effective for the stabilization of organic materials. The aldehyde used tor the process of the invention is selected from formaldehyde, paraformaldehyde, trioxane, tetraoxymethylene, alkylaldehyde and arylaldehyde. The basic catalyst used may for example be an alkali metal, alkaline earth metal, or a hydroxide, oxide, hydride, carbonate, amide or alcoholate thereof. The reaction may also be conducted in the absence of a solvent. If a solvent is used it may be an organic solvent, with no restrictions other than that the organic solvent must not react with the reactants. As useful amine compounds according to the invention there may be mentioned monoalkyl(C 1-28 )amines, monoalkenyl(C 3-28 )amines, dialkyl(C 1-28 )amines, dialkenyl(C 3- 28 )amines, monohydroxyalkyl(C 1-28 )amines, monohydroxyalkenyl(C 3-28 )amines, dihydroxyalkyl(C 1-28 )amines, dihydroxyalkenyl(C 3-28 )amines, 2-amino-2-hydroxymethyl-1,3-propanediol, 2-amino-2-methylpropane-1,3-diol, 2-amino-2-ethyl-1,3-propanediol, alkyl(C 1-28 ) alkenyl(C 3-28 ) amines, alkyl(C 1-28 )hydroxyalkyl(C 1-28 )amines, alkenyl(C 3- 28 )hydroxyalkyl (C 1-28 )amines, alkyl(C 1-28 )hydroxyalkenyl(C 3-28 )amines, alkenyl(C 3-28 )hydroxyalkenyl(C 3-28 )amines, hydroxyalkyl(C 1-28 )hydroxyalkenyl(C 3-28 )amines, aniline, diphenylamine, cyclohexylamine, 2-methylcyclohexylamine, cyclohexyldodecylamine, N-alkyl(C 1-28 )cyclohexylamines, N-alkenyl(C 3-28 )cyclohexylamines and dicyclohexylamine. Particularly preferred among these are alkanolamines (or amino alcohols) such as monoethanolamine, monopropanolamine, monobutanolamine, diethanolamine, dipropanolamine and dibutanolamine. The benzotriazolyl-alkylene bisphenol compounds are useful as light stabilizers and antioxidants for organic materials such as resins, fibers, rubber, waxes, paints, fats and oils, cosmetics, inks, heat-sensitive materials, pressure-sensitive materials, light-sensitive materials and the like. A compound prepared in accordance with the present invention is generally to be used in an amount of 0.01-10wt%, and preferably 0.5-2 wt%, with respect to the organic material. For laminated materials, it may be used at a high concentration of 2-10 wt% in only the uppermost layer. Examples of suitable organic materials include, but are not limited to, homopolymers of olefin and diolefin, such as polyethylene, polypropylene, 1-polybutene, poly-4-methylpentene-1 and 1,2-polybutadiene; copolymers of olefins or olefins and other monomers, such as ethylene-propylene copolymer, ethylene-butene copolymer, ethylenehexene copolymer, ethylene-4-methylpentene-1 copolymer, ethylene-octene-1 copolymer, ethylene-vinyl acetate copolymer, ethylene-vinylsilane copolymer, ethylene-ethyl acrylate copolymer, ethylene-acrylic acid copolymer, ethylene-carbon dioxide copolymer, ethylene-vinyl acetate-glycidyl methacrylate terpolymer and ionomers; polymers of styrene and substituted styrene, such as polystyrene, poly-p-methylstyrene and poly-α-methylstyrene; copolymers of styrene and other monomers, such as styrene-methacrylic acid ester copolymer, styrene-acrylonitrile copolymer, styrene-butadiene copolymer, styrene-maleic anhydride copolymer, methacrylic acid ester-butadiene-styrene terpolymer, acrylic acid ester-butadiene-styrene terpolymer, acrylic acid ester-acrylonitrile-styrene terpolymer and acrylonitrile-butadiene-styrene terpolymer; modified polyethylenes such as maleic anhydride-modified polyethylene; halogenated resins, such as polyvinyl chloride, polyvinyl bromide, polyvinyl fluoride, polyvinylidene chloride, chlorinated polyethylene, chlorinated polypropylene, polyvinylidene fluoride, polyvinyl fluoride, chlorinated rubber, vinyl chloridevinyl acetate copolymer, vinyl chloride-ethylene copolymer, polyfunctional acrylic monomer-vinyl chloride copolymer, (ethylene-vinyl acetate)-vinyl chloride copolymer, acrylonitrile-vinyl chloride copolymer, vinyl chloride-vinylidene chloride copolymer and vinyl chloride-urethane copolymer; polyvinyl acetate; polyvinyl alcohol; polyvinyl butyral; polyvinyl stearate; polyvinyl benzoate; polyvinyl maleate; linear thermoplastic polyesters produced by condensation polymerization of dicarboxylic acids and diols, such as polyethylene terephthalate, polybutylene terephthalate and copolymers including combinations of two or more of terephthalic acid, isophthalic acid, 1,4-butanediol, polyethylene glycol, etc.; straight chain polyesters or polyether esters, such as polytetramethylene ether glycol terephthalate; polyphenylene oxide; polyamides produced by polycondensation of diamines and dicarboxylic acids, polycondensation of aminocarboxylic acids and lactam ring opening polymerization; polycarbonates; polyacetals; polysulfones; polyether sulfones; polyether ketones; polyurethanes obtained by reaction of polyisocyanate compounds with polyols; methacrylic resins; polyacrylonitrile; petroleum resins; coumarone resins; fibrous resins; resins obtained by addition condensation of formaldehyde with various phenols, such as phenolic resins, cresol resins, xylenol resins, p-t-butylphenol resins, p-phenylphenol resins and resorcinol resins; urea resins and melamine resins; epoxy resins; unsaturated polyester resins obtained by polycondensation reaction of polyhydric alcohols with unsaturated polybasic acids containing reactive double bonds; silicone resins; natural polymers, such as cellulose, cellulose acetate, cellulose propionate, cellulose butyrate, methylcellulose and gelatin; natural rubber; synthetic isoprene rubber; ethylene-propylene rubber; butyl rubber; chloroprene rubber; polysulfide rubber; acrylic rubber; urethane rubber; chlorosulfonated polyethylene; epichlorohydrin rubber; ethylene-acrylic rubber; ethylene-ethyl acetate elastomer; isobutylene rubber; butadiene rubber; acrylonitrile-butadiene rubber; styrene-butadiene rubber, and other polymeric substances and their blends, natural fats and oils, synthetic ester oils, mineral oils, and the like. The compounds may be combined with organic materials by commonly employed processes. The organic materials which are stabilized by the compounds may also contain, as desired, commonly used additives, particularly antioxidants, light stabilizers and mixtures thereof. Examples of such additives include antioxidants such as phenol-based, amine-based, sulfur-based and phosphorous-based antioxidants, and light stabilizers such as salicylic acid-based, benzophenone-based, benzotriazole-based, cyanoacrylate-based, acrylonitrile-based, metal complex nickel-based, cobalt-based and hindered amine-based light stabilizers. Other additives which may be used include plasticizers, metal inactivators, lubricants, emulsifying agents, fillers, foaming agents, colorants, fluorescent sensitizers, flame retardants and antistatic agents. The present invention will now be further illustrated by way of examples, with the understanding that the invention is in no way limited by these examples. All of the products in the following synthesis examples were subjected to purification, but such purification is not necessarily required in practice. Example 1 Synthesis of 6-(2-benzotriazolyl)-4-tert.-octyl-6'-tert.-butyl-4'-methyl-2,2'-methylene bisphenol A mixture of 32.3 g of 2-benzotriazolyl-4-tert.-octyl phenol, 16.4 g of 2-tert.-butyl-4-methyl phenol, 13.1 g of dibutylamine, 0.7 g of sodium hydroxide, 3.9 g of paraformaldehyde, 39 g of n-butanol and 150 g of 1,2,4-trimethylbenzene was heated to gradually raise the temperature, and the reaction was carried out for 10 hours at 160-170°C while recovering the water generated by the reaction together with the n-butanol. The reaction solution was washed with acidic water, and then with water. Next, 46 g of the crude product (92% yield) obtained by recovering the 1,2,4-trimethylbenzene under reduced pressure was recrystallized with isopropyl alcohol to give a purified white powder with a melting point of 148°C. The purity of the purified product was 100% as analyzed by liquid chromatography. The results of C, H, N and O elemental analysis of the purified product were close to calculated values as shown in the following table, thus confirming production of the object compound. Element Calculated (%) Found (%) Carbon 76.9 76.9 Hydrogen 8.3 8.4 Nitrogen 8.4 8.5 Oxygen 6.4 6.2 Example 2 Synthesis of 6-(2-benzotriazolyl)-4-tert.-octyl-6'-tert.-butyl-4'-methyl-2,2'-methylene bisphenol A mixture of 32.3 g of 2-benzotriazolyl-4-tert.-octyl phenol, 16.4 g of 2-tert.-butyl-4-methyl phenol, 8.5 g of monoethanolamine, 2.8 g of sodium hydroxide, 3.9 g of paraformaldehyde and 104 g of n-butanol was heated to gradually raise the temperature, and the reaction was carried out for one hour at 180-190°C while recovering the water generated by the reaction together with the n-butanol. After adding 104 g of toluene to the reaction solution to dissolve the reaction product, the toluene layer was washed with acidic water and then with water. Next, 47 g of the crude product (94% yield) obtained by recovering the toluene under reduced pressure was recrystallized with isopropyl alcohol to give a purified white powder with a melting point of 148°C. The purity of the purified product was 100% as analyzed by liquid chromatography. The results of C, H, N and O elemental analysis of the purified product were close to calculated values as shown in the following table, thus confirming production of the object compound. Element Calculated (%) Found (%) Carbon 76.9 76.8 Hydrogen 8.3 8.2 Nitrogen 8.4 8.6 Oxygen 6.4 6.4 Example 3 Synthesis of 6-(2-benzotriazolyl)-4-tert.-octyl-4',6'-di-tert.-butyl-2,2'-methylene bisphenol The same procedure was carried out as in Example 1, except that the 16.4 g of 2-tert.-butyl-4-methyl phenol was replaced with 20.6 g of 2,4-di-tert.-butyl phenol. A 50 g portion of the resulting crude product (92% yield) was recrystallized with isopropyl alcohol to give a purified white powder with a melting point of 137°C. The purity of the purified product was 100% as analyzed by liquid chromatography. The results of C, H, N and 0 elemental analysis of the purified product were close to calculated values as shown in the following table, thus confirming production of the object compound. Element Calculated (%) Found (%) Carbon 77.6 77.7 Hydrogen 8.7 8.8 Nitrogen 7.8 7.8 Oxygen 5.9 5.7 Example 4 Synthesis of 6-(2-benzotriazolyl)-4-tert.-octyl-4',6'-di-tert.-butyl-2,2'-methylene bisphenol The same procedure was carried out as in Example 2, except that the 16.4 g of 2-tert.-butyl-4-methyl phenol and 8.5 g of monoethanolamine were replaced with 20.6 g of 2,4-di-tert.-butyl phenol and 42.5 g of diethanolamine, respectively. A 51 g portion of the resulting crude product (94% yield) was recrystallized with isopropyl alcohol to give a purified white powder with a melting point of 137°C. The purity of the purified product was 100% as analyzed by liquid chromatography. The results of C, H, N and O.elemental analysis of the purified product were close to calculated values as shown in the following table, thus confirming production of the object compound. Element Calculated (%) Found (%) Carbon 77.6 77.7 Hydrogen 8.7 8.6 Nitrogen 7.8 7.8 Oxygen 5.9 5.9 Example 5 Synthesis of 6-(2-benzotriazolyl)-4-tert.-octyl-4',6'-di-tert.-amyl-2,2'-methylene bisphenol The same procedure was carried out as in Example 1, except that the 16.4 g of 2-tert.-butyl-4-methyl phenol was replaced with 23.4 g of 2,4-di-tert.-amyl phenol. A 52 g portion of the resulting crude product (91% yield) was recrystallized with isopropyl alcohol to give a purified white powder with a melting point of 80°C. The purity of the purified product was 100% as analyzed by liquid chromatography. The results of C, H, N and O elemental analysis of the purified product were close to calculated values as shown in the following table, thus confirming production of the object compound. Element Calculated (%) Found (%) Carbon 77.6 77.7 Hydrogen 8.7 8.6 Nitrogen 7.8 7.8 Oxygen 5.9 5.9 Example 6 Synthesis of 6-(2-benzotriazolyl)-4-tert.-octyl-4',6'-di-tert.-amyl-2,2'-methylene bisphenol The same procedure was carried out as in Example 2, except that the 16.4 g of 2-tert.-butyl-4-methyl phenol was replaced with 23.4 g of 2,4-di-tert.-amyl phenol. A 53 g portion of the resulting crude product (93% yield) was recrystallized with isopropyl alcohol to give a purified white powder with a melting point of 80°C. The purity of the purified product was 100% as analyzed by liquid chromatography. The results of C, H, N and O elemental analysis of the purified product were close to calculated values as shown in the following table, thus confirming production of the object compound. Element Calculated (%) Found (%) Carbon 78.0 77.9 Hydrogen 9.0 9.1 Nitrogen 7.4 7.4 Oxygen 5.6 5.6 Example 7 Synthesis of 6-(2-benzotriazolyl)-4-tert.-octyl-4',6'-di-tert.-octyl-2,2'-methylene bisphenol The same procedure was carried out as in Example 1, except that the 16.4 g of 2-tert.-butyl-4-methyl phenol was replaced with 31.9 g of 2,4-di-tert.-octyl phenol. A 59 g portion of the resulting crude product (90% yield) was recrystallized with isopropyl alcohol to give a purified white powder with a melting point of 174°C. The purity of the purified product was 100% as. analyzed by liquid chromatography. The results of C, H, N and O elemental analysis of the purified product were close to calculated values as shown in the following table, thus confirming production of the object compound. Element Calculated (%) Found (%) Carbon 79.0 78.9 Hydrogen 9.7 9.8 Nitrogen 6.4 6.5 Oxygen 4.9 4.8 Example 8 Synthesis of 6-(2-benzotriazolyl)-4-tert.-octyl-4',6'-di-tert.-octyl-2,2'-methylene bisphenol The same procedure was carried out as in Example 2, except that the 16.4 g of 2-tert.-butyl-4-methyl phenol was replaced with 31.9 g of 2,4-di-tert.-octyl phenol. A 60 g portion of the resulting crude product (92% yield) was recrystallized with isopropyl alcohol to give a purified white powder with a melting point of 174°C. The purity of the purified product was 100% as analyzed by liquid chromatography. The results of C, H, N and O elemental analysis of the purified product were close to calculated values as shown in the following table, thus confirming production of the object compound. Element Calculated (%) Found (%) Carbon 79.0 79.0 Hydrogen 9.7 9.5 Nitrogen 6.4 6.5 Oxygen 4.9 5.0 Example 9 Synthesis of 6-(2-benzotriazolyl)-4-tert.-butyl-6'-tert.-butyl-4'-methyl-2,2'-methylene bisphenol The same procedure was carried out as in Example 2, except that the 32.3 g of 2-benzotriazolyl-4-tert.-octyl phenol was replaced with 26.7 g of 2-benzotriazolyl-4-tert.-butyl phenol. A 41 g portion of the resulting crude product (93% yield) was recrystallized with isopropyl alcohol to give a purified white powder with a melting point of 175°C. The purity of the purified product was 100% as analyzed by liquid chromatography. The results of C, H, N and O elemental analysis of the purified product were close to calculated values as shown in the following table, thus confirming production of the object compound. Element Calculated (%) Found (%) Carbon 75.8 75.6 Hydrogen 7.5 7.6 Nitrogen 9.5 9.6 Oxygen 7.2 7.2 Example 10 Synthesis of 6-(2-benzotriazolyl)-4-tert.-butyl-4',6'-di-tert.-butyl-2,2'-methylene bisphenol The same procedure was carried out as in Example 2, except that the 32.3 g of 2-benzotriazolyl-4-tert.-octyl phenol, 16.4 g of 2-tert.-butyl-4-methyl phenol and 8.5 g of monoethanolamine were replaced with 26.7 g of 2-benzotriazolyl-4-tert.-butyl phenol, 20.6 g of 2,4-di-tert.-butyl phenol and 42.5 g of diethanolamine, respectively. A 45 g portion of the resulting crude product (92% yield) was recrystallized with isopropyl alcohol to give a purified white powder with a melting point of 208°C. The purity of the purified product was 100% as analyzed by liquid chromatography. The results of C, H, N and O elemental analysis of the purified product were close to calculated values as shown in the following table, thus confirming production of the object compound. Element Calculated (%) Found (%) Carbon 76.7 76.7 Hydrogen 8.1 7.9 Nitrogen 8.6 8.6 Oxygen 6.6 6.8 Example 11 Synthesis of 6-(2-benzotriazolyl)-4-tert.-butyl-4',6'-di-tert.-amyl-2,2'-methylene bisphenol The same procedure was carried out as in Example 2, except that the 32.3 g of 2-benzotriazolyl-4-tert.-octyl phenol and 16.4 g of 2-tert.-butyl-4-methyl phenol were replaced with 26.7 g of 2-benzotriazolyl-4-tert.-butyl phenol and 23.4 g of 2,4-di-tert.-amyl phenol, respectively. A 48 g portion of the resulting crude product (93% yield) was recrystallized with isopropyl alcohol to give a purified white powder with a melting point of 186°C. The purity of the purified product was 100% as analyzed by liquid chromatography. The results of C, H, N and O elemental analysis of the purified product were close to calculated values as shown in the following table, thus confirming production of the object compound. Element Calculated (%) Found (%) Carbon 77.2 77.2 Hydrogen 8.4 8.2 Nitrogen 8.2 8.3 Oxygen 6.2 6.3 Example 12 Synthesis of 6-(2-benzotriazolyl)-4-tert.-butyl-4',6'-di-tert.-octyl-2,2'-methylene bisphenol The same procedure was carried out as in Example 2, except that the 32.3 g of 2-benzotriazolyl-4-tert.-octyl phenol and 16.4 g of 2-tert.-butyl-4-methyl phenol were replaced with 26.7 g of 2-benzotriazolyl-4-tert.-butyl phenol and 31.9 g of 2,4-di-tert.-octyl phenol, respectively. A 55 g portion of the resulting crude product (92% yield) was recrystallized with isopropyl alcohol to give a purified white powder with a melting point of 166°C. The purity of the purified product was 100% as analyzed by liquid chromatography. The results of C, H, N and O elemental analysis of the purified product were close to calculated values as shown in the following table, thus confirming production of the object compound. Element Calculated (%) Found (%) Carbon 78.4 78.3 Hydrogen 9.3 9.5 Nitrogen 7.0 6.9 Oxygen 5.3 5.3 Example 13 Synthesis of 6-(2-benzotriazolyl)-4-methyl-6'-tert.-butyl-4'-methyl-2,2'-methylene bisphenol The same procedure was carried out as in Example 2, except that the 32.3 g of 2-benzotriazolyl-4-tert.-octyl phenol was replaced with 22.5 g of 2-benzotriazolyl-4-methyl phenol. A 38 g portion of the resulting crude product (94% yield) was recrystallized with isopropyl alcohol to give a purified white powder with a melting point of 167°C. The purity of the purified product was 100% as analyzed by liquid chromatography. The results of C, H, N and O elemental analysis of the purified product were close to calculated values as shown in the following table, thus confirming production of the object compound. Element Calculated (%) Found (%) Carbon 74.8 74.8 Hydrogen 6.7 6.6 Nitrogen 10.5 10.7 Oxygen 8.0 7.9 Example 14 Synthesis of 6-(2-benzotriazolyl)-4-methyl-4',6'-di-tert.-butyl-2,2'-methylene bisphenol The same procedure was carried out as in Example 2, except that the 32.3 g of 2-benzotriazolyl-4-tert.-octyl phenol, 16.4 g of 2-tert.-butyl-4-methyl phenol and 8.5 g of monoethanolamine were replaced with 22.5 g of 2-benzotriazolyl-4-methyl phenol, 20.6 g of 2,4-di-tert.-butyl phenol and 42.5 g of diethanolamine, respectively. A 41 g portion of the resulting crude product (92% yield) was recrystallized with isopropyl alcohol to give a purified white powder with a melting point of 171°C. The purity of the purified product was 100% as analyzed by liquid chromatography. The results of C, H, N and O elemental analysis of the purified product were close to calculated values as shown in the following table, thus confirming production of the object compound. Element Calculated (%) Found (%) Carbon 75.8 75.6 Hydrogen 7.5 7.6 Nitrogen 9.5 9.6 Oxygen 7.2 7.2 Example 15 Synthesis of 6-(2-benzotriazolyl)-4-methyl-4',6'-di-tert.-amyl-2,2'-methylene bisphenol The same procedure was carried out as in Example 2, except that the 32.3 g of 2-benzotriazolyl-4-tert.-octyl phenol and 16.4 g of 2-tert.-butyl-4-methyl phenol were replaced with 22.5 g of 2-benzotriazolyl-4-methyl phenol and 23.4 g of 2,4-di-tert.-amyl phenol, respectively. A 44 g portion of the resulting crude product (93% yield) was recrystallized with isopropyl alcohol to give a purified white powder with a melting point of 116°C. The purity of the purified product was 100% as analyzed by liquid chromatography. The results of C, H, N and O elemental analysis of the purified product were close to calculated values as shown in the following table, thus confirming production of the object compound. Element Calculated (%) Found (%) Carbon 76.4 76.3 Hydrogen 7.9 8.1 Nitrogen 8.9 8.9 Oxygen 6.8 6.7 Example 16 Synthesis of 6-(2-benzotriazolyl)-4-methyl-4',6'-di-tert.-octyl-2,2'-methylene bisphenol The same procedure was carried out as in Example 2, except that the 32.3 g of 2-benzotriazolyl-4-tert.-octyl phenol and 16.4 g of 2-tert.-butyl-4-methyl phenol were replaced with 22.5 g of 2-benzotriazolyl-4-methyl phenol and 31.9 g of 2,4-di-tert.-octyl phenol, respectively. A 52 g portion of the resulting crude product (94% yield) was recrystallized with isopropyl alcohol to give a purified white powder with a melting point of 138°C. The purity of the purified product was 100% as analyzed by liquid chromatography. The results of C, H,. N and O elemental analysis of the purified product were close to calculated values as shown in the following table, thus confirming production of the object compound. Element Calculated (%) Found (%) Carbon 77.8 77.8 Hydrogen 8.8 9.0 Nitrogen 7.6 7.4 Oxygen 5.8 5.8

Claims: A process for preparing a benzotriazolyl-alkylene bisphenol compound represented by general formula (3): wherein X represents hydrogen, a halogen, or an alkyl, cycloalkyl, alkoxy or alkylaryl group, R 1 represents an alkyl, cycloalkyl, aryl, alkoxy or arylalkyl group, R 2 represents hydrogen or an alkyl or aryl group, and R 3 and R 4 may be the same or different and each represent an alkyl, cycloalkyl, aryl or alkylaryl group, which process comprises reacting a 2-hydroxyphenylbenzotriazole represented by general formula (1): wherein X and R 1 are as defined above, and a 2,4-substituted phenol represented by general formula (2): wherein R 3 and R 4 are as defined above, with an aldehyde selected from formaldehyde, paraformaldehyde, trioxane, tetraoxymethylene, alkylaldehyde and arylaldehyde, in the presence of a basic catalyst and an amine compound.

Inventors: AOKI HIDEO, ISHIHARA KAZUYUKI, KANAGAWA EISUKE, YAMAUCHI TOSHIYUKI, AOKI, HIDEO, ISHIHARA, KAZUYUKI, KANAGAWA, EISUKE, YAMAUCHI, TOSHIYUKI
Applicants: JOHOKU CHEMICAL CO LTD, JOHOKU CHEMICAL CO., LTD.
Application year: 1997
Main classification: C07D249
IPC codes: C07D249, C08K5, C08L101, C09K15