Method of forming tungsten carbide particles

Abstract: Nanograined tungsten carbide particles are formed by a controlled, simultaneous reduction carburization reaction wherein the kinetics of the carburization and reduction reactions are controlled to permit simultaneous reduction and carburization. The kinetics are controlled by reacting a reduction carburization gas mixture, preferably hydrogen and carbon monoxide by slowly increasing the reaction temperature by controlling the rate of temperature increase. Preferably, the reaction temperature will be increased less than 25°C per minute, preferably about 1-2 degrees per minute, which prevents the formation of stable, undesirable species such as W 2 C, which in tum interferes with the reaction efficiency.

Description: Tungsten carbide is used in a wide variety of products such as cutting tools, wear parts and mining drill bits. Its toughness and hardness makes it excellent for these applications. In order to Improve the hardness of tungsten carbide, the grain size of the cabide should be as small as possible. It is known that nanograin-sized tungsten carbide powders can be produced by a combination reduction/carburization process. This permits the tungsten carbide to be used in very demanding applications. The current process to manufacture nanophase tungsten carbide, as well as tungsten carbide cobalt composites typically Involves several processing steps. Initially, the tungsten composition is subjected to a reductive decomposition, followed by a gas-phase carburization. This results in the formation of many stable intermediates such as substoichiometric tungsten carbides, elemental tungsten and tungsten dioxide. The stability of these intermediate products significantly increases the carburization cycle time. DD290859 describes a method of forming tungsten carbide from ammonium paratungstate by an initial hydrogen reduction and then simultaneous reduction and carburization with hydrogen and carbon monoxide or carbon monoxide alone. US Patent 5372797 describes formation of monotungsten carbide from a tungsten trioxide by heating the trioxide in hydrogen and methane first to between 520 and 550°C and then to between 800 and 900°C. The article "The preparation of tungsten carbide" JOURNAL OF THE AMERICAN CHEMICAL SOCIETY, vol. 79, no. 17, 11 September 1957, DC US, pages 4629-4631 describes formation of tungsten carbide from tungstic acid, a blue oxide of tungsten or ammonium paratungstate. The present invention provides a method of forming nanograined tungsten carbide particles from a precursor compound selected from the group of metatungstate, paratungstate and tungstic acid comprising simultaneously reducing and carburizing said precursor compound by reacting said compound with a mixture of hydrogen and a carbon source gas, the gas mixture having a carbon activity of 1 to 2 and the compound being reacted with the gas mixture by heating said precursor compound to a temperature of from 540°C to 700°C in the presence of said mixture at a heating rate no greater than 25°C per minute to prevent the formation of substoichiometric tungsten carbide and tungsten dioxide for a time effective to form tungsten carbide. The present invention is premised on the realization that the rate of formation of tungsten carbide from tungsten precursor compositions is significantly improved by preventing the formation of many intermediate compositions, and forming the tungsten carbide in a one-step reaction. More particularly, the present invention is premised on the realization that by reacting a tungsten-based composition with a gaseous mixture of hydrogen and a carbon source gas such as carbon monoxide one can form tungsten carbide directly, without the formation of the stable intermediates. This is more particularly accomplished by very carefully increasing the temperature of the reactants so that as the hydrogen reduces a tungsten atom, a carbon atom is present to immediately react to form tungsten carbide without forming the intermediate tungsten metal or substoichiometric tungsten carbide. The rate of reaction, in turn, is controlled very carefully by controlling the rate of heat increase up to about 700°C. The invention will now be described by way of example and with reference to the accompanying drawings in which: FIG. 1 is a thermogravimetric curve showing the one-step reduction carburization process of the present invention, compared to a conventional two-step reduction, then carburization process. FIG. 2 is a thermogravimetric curve of the one-step process of the present invention over a series of heat-up rates. According to the present invention, tungsten carbide is formed from precursor compounds using a single-step reduction/carburization process. The precursor compounds can be basically any tungsten compound which can be reduced to form WC. Suitable tungsten compounds include ammonium metatungstate, ammonium paratungstate, tungsten blue oxide, standard yellow tungsten oxide, as well as tungsten dioxide and tungstic acid. These are generally purchased as powder. Particle size Is not particularly critical for practicing the present invention and can be anywhere from a few microns or less up to 200-300 microns. However, a smaller particle size does facilitate reaction rate. The precursor composition is reacted with a reactant gas mixture of hydrogen and a carbon source gas in a heated reactor. Any heated reactor which enables one to control the atmosphere can be used for the present invention. The reactor can be a fixed bed reactor, a rotary kiln reactor, or a fluidized bed reactor. Since the reaction is a solid gas reaction, a rotary kiln reactor or a fluidized bed reactor are preferred since they greatly facilitate gas/solid mixing. The carbon source gas of the reactant gas mixture can be any carbon-containing gas that is unstable in the temperature range, i.e., able to decompose to deposit carbon. Carbon monoxide is preferred. In this situation, the hydrogen acts as a reducing agent and the carbon monoxide is a source of carbon for the concurrent carburization. Preferably, the volume ratio of hydrogen to carbon source gas will range from 1:1 to 3:1 with an equivolume mixture preferred. The mixture should have a sufficiently high carbon activity so as not to interfere with the reaction kinetics. If the carbon activity is too high, free carbon will be formed. Accordingly, the carbon activity of the gas mixture should be from about 1 to about 2, with about 1.3 being preferred. The precursor compound, in combination with the reaction gas mixture, is then heated up to about 700° C. The rate of heat increase is critical for practicing the present invention. This rate must be slow enough that the tungsten in the precursor compound immediately upon reduction reacts with carbon presented by the carbon monoxide to form tungsten carbide without forming intermediate complexes such as substoichiometric carbides and elemental tungsten. The heat-up rate cannot exceed 25° C per minute once the reaction process is in progress. This will effectively permit formation of tungsten carbide directly from tungsten precursors without formation of the intermediate elemental tungsten or substoichiometric tungsten carbide. Preferably, the heat-up rate will be 1° to 5° C per minute. Lower heat-up rates will function, but will take significantly longer times. Generally, the reaction time will take from about 2 to about 6 hours, depending upon the reaction gas mixture, heat-up rate and batch size. The invention will be further appreciated in light of the following detailed examples. EXAMPLE 1 100 mg of WO 3 powder was heated to 700° C in a gaseous mixture of H 2 and CO at a 2:1 volume ratio. The heat-up rate was maintained at 25° C/minute to get to temperature for a total processing time of 2.5 hours. FIG. 1 shows the TG curve of this one-step carburization process. The sample weight was reduced to a level slightly below the theoretical WC level followed by a weight gain back to the WC value. XRD confirmed the presence of phase pure WC with the grain size measured at ca.9 nanometers by line broadening techniques. The intermediate plateau on the TG curve was caused by the formation of reduction intermediate WO 2 . FIG. 1 also shows the profile of the conventional two-step process in which 100 mg of WO 3 powder was fully reduced to W by H 2 and then carburized by CO. EXAMPLE 2 100 mg of tungsten blue oxide (TBO) powder was heated to 700°C in a gaseous mixture of H 2 and CO at a 2:1 volume ratio. The heating rate was varied to examine the reaction effects. FIG. 2 shows TG curves corresponding to the one-step carburization process at heat-up rates of 10, 5, 2 and 1° C/min. It is dear that the WO 2 intermediate plateau is reduced as the heating rate becomes slower, with the resulting reduction in the deviation from the theoretical WC weight level. XRD confirmed the presence of phase-pure WC. EXAMPLE 3 100 mg. of APT powder was heated to 700° C in a gaseous mixture of H 2 and Co in a 2:1 ratio. The heat-up rate was maintained at 25° C/min. for a total processing time of 2 hours. XRD examination showed WC powders with an average grain size of ca. 10 nanometers, as measured by the line broadening technique. EXAMPLE 4 600 mg of AMT powder was heated to 560° C in a gaseous mixture of H 2 and CO in a 1:1 ratio. The heat-up rate was maintained at 25° C/minute to get to temperature for a total processing time of 6 hours. XRD confirmed the production of a phase-pure WC powder product. The BET surface area was measured at 16.35 m 2 /g. This surface area value corresponds to a particle size of ca. 23 nanometers, under the assumption of a spherical nonagglomerated powder. Thus the present invention provides a rapid method to produce nanograined tungsten carbide particles. By controlling the reaction kinetics of the reduction/carburization, one can form tungsten carbide directly without forming intermediate substoichiometric tungsten carbides or elemental tungsten, in turn greatly reducing the reaction time and improving the overall economics of the formation of tungsten carbide without, in any way, reducing the hardness or toughness of the formed product The process time is reduced due to the absence of the substoichiometric W 2 C which is also an impurity.

Claims: A method of forming nanograined tungsten carbide particles from a precursor compound selected from the group of metatungstate, paratungstate and tungstic acid comprising simultaneously reducing and carburizing said precursor compound by reacting said compound with a mixture of hydrogen and a carbon source gas, the gas mixture having a carbon activity of 1 to 2 and the compound being reacted with the gas mixture by heating said precursor compound to a temperature of from 540°C to 700°C in the presence of said mixture at a heating rate no greater than 25°C per minute to prevent the formation of substoichiometric tungsten carbide and tungsten dioxide for a time effective to form tungsten carbide. A method as claimed in Claim 1 wherein the precursor compound is selected from the group consisting of ammonium metatungstate and ammonium paratungstate. A method as claimed in either claim 1 or claim 2 wherein the carbon source gas is carbon monoxide. A method as claimed in any preceding claim wherein the gas mixture comprises a mixture of hydrogen and carbon monoxide at a volume ratio of 1:1 to 3:1. A method as claimed in any preceding claim wherein said precursor is heated in a reactor from the group consisting of rotary kiln reactors and fluidized bed reactors.

Inventors: GAO LIN, KEAR BERNARD, SEEGOPAUL PURNESH, GAO, LIN, KEAR, BERNARD, SEEGOPAUL, PURNESH
Applicants: UNION MINIERE SA, UNIV RUTGERS, N.V. UNION MINIERE S.A., RUTGERS UNIVERSITY
Application year: 1997
Main classification: C01B31
IPC codes: C01B31, B23B27