Method of manufacture polyelectrolyte

Abstract: A method of manufacturing a polyelectrolyte having the step of sulfonating polystyrene resin in a state where the polystyrene resin has been dissolved or dispersed in solvent composed of alicyclic compounds.

Description: BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a method of manufacturing a polyelectrolyte such that ion groups are introduced into polystyrene resin. 2. Description of Prior Art Polystyrene resin has excellent electric characteristic, satisfactory rigidity and sufficient water resistance while exhibiting low costs. Therefore, the polystyrene resin is solely or formed into an alloy combined with a copolymer or another resin so as to be used in buffers (foamable styrol), packing materials, electric products and frames and various parts for automobiles. Thus, the polystyrene resin is a general-purpose resin considered equal to polyolefin resin represented by polyethylene. In addition to the purpose of the polystyrene resin for use as the structural material, the polystyrene resin is refined into a polyelectrolyte so as to be used as coagulant for waste water treatment, an additive for cement, a material for fluidizing coal slurry, dispersant for inorganic pigment, a material for reinforcing paper, a surface sizing material for paper, a conductive material for an electronic copying machine, a destaticizer, a scale preventive material, dispersant for emulsion polymerization and aqueous glue and the like. To refine the polystyrene resin into a polyelectrolyte, for example, a method may be employed in which sulfonate or an amine salt subjected to a chloromethylation process is introduced into the polystyrene resin so that the polystyrene resin is formed into a water-soluble polymer. However, an actual process for refining the polystyrene resin into a polyelectrolyte encounters a variety of problems. For example, sulfonation of the polystyrene resin, which is performed in a sulfonating agent, requires a large quantity of the sulfonating agent, represented by concentrated sulfuric acid. Moreover, the large quantities of the sulfonating agent and water for cleaning the sulfonating agent are discharged after the reactions have been performed. Thus, there arises a problem in that resources cannot be saved, the waste cannot be reduced and the manufacturing cost cannot be reduced. If the sulfonating operation is performed as described above, molecule crosslinking (sulfon crosslinking) easily occur when reactions are performed. Thus, the polymers are allowed to gel and therefore unnecessary polymers can easily be formed in water. Moreover, the foregoing gelation becomes apparent in proportion to the molecular weight of the polymer and the molecule chains of the polymers can easily be cut. Therefore, a high molecular polyelectrolyte cannot easily be obtained. When the sulfonating reactions are performed in a chlorine solvent, a large quantity of the chlorine solvent remains in the polyelectrolyte after subjected to the reactions and its water solution. As a result, halogen compounds are contained in the polyelectrolyte product. Therefore, if the foregoing polyelectrolyte is used in the coagulant for waste water treatment, dispersant for cement, absorbing resin, a surface sizing material for paper or the like, the halogen compounds are discharged into waste water. Thus, the foregoing polyelectrolyte cannot practically be employed because of difficulty to satisfy a waster water regulation. Since the molecular weight (Mw) of the thus obtained polyelectrolyte is generally 150,000 to 600,000, a polyelectrolyte having a large molecular weight has been required to improve the performance when the polyelectrolyte is used as, for example, a coagulant. Since the sulfonating reaction encounters reduction in the reaction rate if water is contained in the system, water must completely be removed to again use the solvent in the reactions. However, a conventional technique, for example, still standing separation, involves a fact that sulfonated substances of aromatic polymers, which are reaction products, serve as surface active agents. Thus, the boundary between the aqueous layer and the solvent layer becomes confused, thus causing the separation to be made difficult. When the solvent is recovered by distillation, the solvent of the chlorine type hydrocarbon and water form azeotropic mixture. Complete removal of water from the solvent cannot easily be realized, thus causing a necessity for performing refining and dehydration processes to arise. Therefore, there arises problems in that the working efficiency deteriorates and new additional facility is required. What is worse, the polystyrene resin has a problem of a halogen flame retardant. Since the halogen flame retardant has a significant flame retardant effect with respect to a variety of plastic materials and its cost is very low, the halogen flame retardant is used widely over the world. However, use of the halogen flame retardant raises a problem because the halogen flame retardant generates halogenated hydrogen when it burns. In particular, use of decabromodiphenyl oxide (DBDPO), which is used most widely and which generates toxic substances, such as dioxine, has been regulated. The halogen flame retardant, having excellent flame retardant effect with respect to aromatic resins represented by styrene resin, are widely used in the frames of home electronic products and as a material of parts. Therefore, if the home electronic products are dumped, a large quantity of plastic substances containing the halogen flame retardant are discharged. The plastic wastes are usually burnt or reclaimed except for a small portion which is recycled by heating and melting. When the plastic wastes are attempted to be disposed by burning, the above-mentioned problem of generation of toxic gases arises. Therefore, the disposal must be performed by the reclamation at present. The amount of plastic wastes containing the halogen flame retardant has been enlarged year by year. Therefore, the reclamation disposal is ineffective and thus there arises a critical problem for Japan considerably wanting of reclamation plants. If recycling of plastic wastes is attempted, recycle of the plastic containing the halogen flame retardant, the use of which is regulated, is not preferable. EP 0 037 282 A2 describes a process for forming a powder of a neutralized sufonated polymer. The neutralized sulfonated elastomeric polymers are derived from unsaturated polymers which include low unsaturated elastomeric polymers, such as butyl rubber, or EPDM terpolymers. EP 0 037 282 A2 does not describe a water-soluble polyelectrolyte having a molecular weight Mw of 600.000 or more. Although styrene-butadiene-copolymers are described as possible starting polymers, the conjugate diene units have not been crosslinked and/or polymerized in the polyelectrolyte of D1. EP 0 071 347 A2 describes a process for sulfonation of aromatic-containing polymers. Also EP 0 071 347 A2 does not describe a polyelectrolyte having a molecular weight Mw of 600.000 or more. The polymers used as starting materials in D2 do not contain conjugate diene units. OBJECTS AND SUMMARY OF THE INVENTION An object of the present invention is to provide a method of manufacturing a polyelectrolyte capable of manufacturing a polyelectrolyte containing no halogen compound while preventing discharge of a large quantity of toxic wastes. Another object of the present invention is to provide a method of manufacturing a water-soluble polyelectrolyte having larger molecular weight. An object of the present invention is to enable a solvent used in a sulfonating reaction of aromatic polymers to be recovered in a state where no water is contained and to form an efficient sulfonating system by recycling the solvent. Another object of the present invention is to provide a processing method capable of efficiently separating halogen flame retardant containing plastic waste or the like. According to one aspect of the present invention, there is provided a method of manufacturing a polyelectrolyte comprising the step of sulfonating polystyrene resin in a state where the polystyrene resin is dissolved or dispersed in a solvent composed of an alicyclic compound. When the alicyclic compound is employed as the solvent in the process for sulfonating the polystyrene resin, gelation can be prevented. Since the necessity of using a halogen compound as the solvent can be removed, a polyelectrolyte containing no halogen compound can be manufactured without discharge of a large quantity of toxic wastes. According to a second aspect of the present invention, there is provided a method of manufacturing a polyelectrolyte comprising the steps of introducing ion groups into copolymers of styrene and conjugate diene; and crosslinking and/or polymerizing the conjugate diene in the copolymer so that refining to a water-soluble polyelectrolyte is performed. When the conjugate diene is previously contained in the polystyrene resin and the conjugate diene units are crosslinked and/or polymerized, the water-soluble polyelectrolyte having a large molecular weight can be obtained. A third aspect of the present invention is characterized in that aromatic polymers are added to and dissolved in solvent supplied continuously; sulfonating agents are supplied to the solution to perform sulfonating reactions; generated reaction products and the solvents are separated from each other; and the separated solvents are returned so as to be again used in the sulfonating reactions. In the above-mentioned aspect, the sulfonated aromatic polymers are formed into solid matters so as to be separated from the solvents. Therefore, the necessity of adding water to the reaction system can be removed. Therefore, the separated solvents do not contain water and thus the solvents can be recycled. A fourth aspect of the present invention is characterized in that plastics containing halogen flame retardants are subjected to an acid process in an organic solvent; ion groups are introduced into resin components to form water-soluble polymer; and then the halogen flame retardants in the organic solvent are separated. When the plastics containing the halogen flame retardants are subjected to the acid process in the organic solvents, the ion groups are introduced into the resin components so as to be formed into water-soluble polymers so that the phase is shifted to an aqueous phase. On the other hand, the above-mentioned introduction of the ion groups does not take place in the halogen flame retardants. Thus, the halogen flame retardants are, in the non-reacted state, retained to be the organic solvent phase. Therefore, separation of the aqueous phase and the organic solvent phase from each other causes the resin components and the halogen flame retardants to quickly be separated from each other. Other objects, features and advantages of the invention will be evident from the following detailed description of the preferred embodiments described in conjunction with the attached drawings. A method of manufacturing the polyelectrolyte will now be described which comprises the steps of introducing ion groups into copolymers of styrene and conjugate diene and crosslinking/polymerizing the conjugate diene units in the copolymers will now be described. By crosslinking and/or polymerizing conjugate diene units in the copolymers, the molecular weight of the polyelectrolyte can be enlarged. The polyelectrolyte obtained by the foregoing method may be used as coagulant for disposing waste water, an additive to cement, superplasticizer for coal slurry, dispersant for inorganic pigment, paper strength enhancer, a surface sizing agent for paper, a conductive agent for an electronic copying machine, an antistatic agent, a scale preventive agent, dispersant for emulsion polymerization and aqueous glue. When the molecular weight Mw is made to be 600,000 or larger, the above-mentioned polyelectrolyte can be used as coagulant for disposing waste water, absorbing resin, ion exchange resin, chelate resin, paper strength enhancer, a surface sizing agent for paper and superplasticizer for coal slurry. The conjugate diene which is copolymerized with styrene is exemplified by butadiene and isoprene. The content of the conjugate diene units in the copolymer is 0.05 mol% to 20 mol% with respect to all monomer units, preferably 0.1 mol% to 10 mol%. When the obtained polyelectrolyte is used as the coagulant for disposing waste water, the content of the conjugate diene units in the copolymer is made to be 0.1 mol% to 10 mol% with respect to all monomer units, preferably 0.5 mol% to 5 mol%. If the quantity of the conjugate diene units in the polystyrene resin is to small, the crosslinking reactions and the polymerizing reaction do not easily take place in the double bond portions. Thus, the effect of enlarging the molecular weight cannot be obtained. If the quantity of the conjugate diene units is too large, the polystyrene resin cannot easily be dissolved in the organic solventand thus uniform reactions cannot easily be performed. Moreover, the degree of crosslinking and/or polymerization is raised excessively, thus causing gelled products to be easily generated. As a result, introduction of the ion groups into the resin cannot easily be performed. In a viewpoint of causing the characteristics of the sulfonated polystyrene to exhibit, the quantity of the styrene units in the polystyrene resin is made to be 80 mol% or more with respect to all monomer units, preferably 90 mol% or more. The polystyrene resin for use in the present invention may contain other monomers except for the conjugate diene, the other monomers being exemplified by acrylonitrile, (metha) acrylic acid, (metha) acrylate (aliphatic hydrocarbon having one to four carbon atoms), maleic anhydride, itaconic anhydride and α-methylstyrene. The molecular weight of the polystyrene resin is made to be 2,000 to 2,000,000, preferably 5,000 to 500,000. If the molecular weighs is too small, the required characteristics as the polyelectrolyte cannot be obtained. If the molecular weight is too large, the solubility into the organic solvent deteriorates when the sulfonating reactions of the polystyrene resin are performed in the organic solvent. In this case, reactions are performed nonuniformly. The above-mentioned polystyrene resin may contain a dye, stabilizer, flame retardant agent, plasticizer, filler and another auxiliary additives. The polystyrene resin (copolymer) may be used solely or in combination with polystyrene or another styrene copolymer. It may be alloyed or blended with another polymer. The other polymer which is alloyed or blended as described above is exemplified by polyphenylene ether, polycarbonate, polyphenylene sulfide, polyamide (Nylon), polyethylene terephthalate and polybutylene terephtalate. The foregoing polymer may be employed solely or plural types of the polymers may be combined. If the foregoing type polystyrene resin is employed, polystyrene resin (a virgin material) prepared newly for manufacturing the polyelectrolyte according to the present invention or a refuse (a waste) from a plant, a retail shop, a home or the like may be employed. Virgin materials and wastes may be used together. The polystyrene resin may be formed into pellet, powder or rod shape, a molded shape, a foamed shape or granular, fiber or film shape. Since the present invention enables the polystyrene resin products mass-produced as the general-purpose resins to be recycles as described above, a significant advantage can be realized in viewpoint of protection of the global atmosphere. In the foregoing viewpoint, it is preferable that the polystyrene resin be wastes rather than the virgin materials. Note that it is preferable that wastes recovered from plants or retail shops be employed because these wastes have relatively uniform compositions as compared with those recovered from homes. The ion groups which are introduced into the polystyrene resin are exemplified by sulfonic acid and its salt. The ion groups are introduced by causing the polystyrene resin (copolymer) to react with various oxidizers. For example, when the polystyrene resin is caused to react with the oxidizers in organic solvent containing the sulfonating agent represented by sulfuric anhydride, sulfon groups can be introduced. When the ion groups are introduced as described above, any one of the following reaction solvents is employed: aliphatic halogen hydrocarbon represented by 1, 2-dichloroethane, chloroform, dichloroethane and 1, 1-dichloroethane; an alicyclic compound represented by cyclohexane, methylcyclohexane and cyclobenzene; nitromethane; and nitrobenzene. If the alicyclic compound is employed, the polyelectrolyte containing no halogen compound can be manufactured without discharge of toxic waste. The above-mentioned organic solvent may be used solely or in combination of a plurality of organic solvents. The mixture ratio is not limited particularly. The above-mentioned organic solvent may be used such that it is mixed with another solvent. The other solvent which can be used in the mixture is exemplified by paraffin type hydrocarbon having one to seven carbon atoms, acetonitrile, carbon disulfide, tetrahydrofuran, tetrahydropiran, 1, 2-dimethoxyethane, acetone, methylethylketone and thiophene. in particular, it is preferable that any one of paraffin type hydrocarbon having one to seven carbon atoms, acetonitrile, tetrahydrofuran and acetone be employed. In a case where the above-mentioned solvent is mixed with the aliphatic halogen hydrocarbon or the alicyclic compound, the mixture ratio is not limited particularly. It is preferable that the quantity of the solvent be 1 % to 100 % of the volume of the aliphatic halogen hydrocarbon or the alicyclic compound. The solvent once used in the introduction reactions of the ion groups can be recovered by extracting or distillation after the reactions have been performed so as to be used again. It is preferable that the recovery of the solvent be performed prior to adding the chlorine compound or its water solution to the reaction system. When the reaction for introducing the ion groups is performed by using the above-mentioned solvent, the concentration of the polystyrene resin is made to be 0.1 wt% to 30 wt%, preferably 0.5 wt% to 20 wt%. If the concentration is too low, the manufacturing efficiency and a rate for introducing sulfon group into the polymer are lowered. If the concentration is too high, the quantities of gelled products and unreacted substances are unintentionally enlarged. The sulfonating reaction is performed at 0°C to 100°C, preferably 10°C to 80°C. If the temperature is too low, the reactions cannot easily proceed and yield deteriorates. The period of time in which the reactions are performed is made to be 10 minutes to 40 hours, preferably 30 minutes to 20 hours. The chlorine compound for use in the neutralization of the ion groups is exemplified by a compound such as oxide, hydride, carbonate, acetate, sulfate or phosphate of alkali metal, such as sodium, lithium or potassium or alkali earth metal, such as magnesium or calcium; ammonia; primary to tertiary alikylamine compound. The selected material is, as it is, or in the form of water solution, gradually added to that the neutralizing process is completed. The quantity of the ion groups, which are introduced as described above is made to be 20 mol% or more with respect to all monomer units, preferably 40 mol% or more. If the ratio of the introduced ion groups is lower than the above-mentioned range, a polyelectrolyte having sufficient water solubility cannot be obtained. As described above, the ion groups can be introduced into the polystyrene resin containing the conjugate diene units. In the present invention, the conjugate diene units are crosslinked and/or polymerized to refine the same into an electrolyte having larger molecular weight. Chemicals for causing the crosslinking reactions and/or polymerizing reactions to take place are exemplified by inorganic or organic peroxide, an azo compound and the like. Specifically, the inorganic peroxide is exemplified by hydrogen peroxide solution, peroxosulfuric acid, its salt compound, peroxocarbonate, peroxophosphoric acid, its salt compound, peroxonitric acid, its salt compound, ozone, perchloric acid, permanganic acid and its salt. Among the foregoing materials, it is preferable that any one of the hydrogen peroxide solution, peroxosulfuric acid, its salt compound and ozone be employed. The organic peroxide is exemplified by the following materials. Hydroperoxides: t-butylhydroperoxide, cumenehydroperoxide, diisopropyl benzenehydroperoxide, P-menthane hydroperoxide, 2, 5-dimethyl-2, 5-dihydroperoxy hexane, 2, 5-dimethyl-2, 5-dihydroperoxy hexyne-3 and pinene hydroperoxide. Dialkylperoxides: di-t-butylperoxide, di-t-amilperoxide, t-butylcumylperoxide, dicumylperoxide, 2, 5-dimethyl-2, 5-di-(t-butylperoxy) hexane, 2, 5-dimethyl-2, 5-di (t-butylperoxy) hexyne-3, α, α'-bis (t-butylperoxy) diisopropyl benzene, 1, 2-bis (t-butylperoxy)-3, 3, 5-trimethyl cyclohexane, n-butyl-4, 4-bis (t-butylperoxy) valleriite, 2, 2-bis (4, 4-di-t-butyl peroxicyclohexyl) propane and 2, 2-bis (t-butylperoxy) butane, 1, 1-di-(t-butylperoxy) cyclohexane. Diacylperoxides: caprilydeperoxide, lauroyl peroxide, stearyl peroxide, succinic acid peroxide, benzoyl peroxide, p-chlorobenzoyl peroxide, 2, 4-dichlorobenzoyl peroxide and the like. Peroxy esters: t-butylpeorxyacetic acid, t-butylperoxy-2-ethylhexanoate, t-butylperoxylaurate, t-butylperoxybenzoate, di-t-butyldiperoxyphthalate, 2, 5-dimethyl-2, 5-di (benzoylperoxy) hexane, 2, 5-dimethyl-2, 5-di (benzoylperoxy) hexyne-3, t-butylperoxy maleic acid, t-butylperoxyisopropyl carbonate and the like. Ketone peroxides: methylethylketoneperoxide, methylisobutylketone peroxide, cyclohexane peroxide and the like. The above-mentioned peroxides may be used together with various reducers or crosslinking assistants. The reducers are exemplified by ions of metal, such as cobalt, nickel, iron, copper, manganese, selenium or sodium; and amine compounds, such as dimethylaniline. The crosslinking assistant are exemplified by sulfur, p-quinonedioxime, p, p-dibenzoylquinonedixime, laurylmethacrylate, ethyleneglycol acrylate, triethyleneglycol acrylate, tetraethyleneglycoldimetha acrylate, polyethyleneglycoldimetha acrylate, trimethylolpropenetrimetha acrylate, methylmethacrylate, diarylfumarate, diarylphthalate, tetraaryloxyethane, triarylcyanurate, maleimide, phenylmaleimide, N, N'-m-phenylenehismaleimide, maleic anhydride, itaconic acid, divinylbenzene, vinyltoluene and polybutadiene having small molecular weight (Mw = 1,000 to 5,000). The azo compounds which may by employed as the chemicals for causing the crosslinking and/or polymerizing reactions to take place are exemplified by : azobisbutylonitrile, 1-[(1-cyano-1-methylethyl) azo] formamide, 1, 1-azobis (cyclohexane-1-carbonitrile), 2, 2-azobis (2-methylpropionamidine) dihydrochloride, 2, 2-azobis (2-methylbutylonitrile), 2, 2-azobis (2, 4-dimethylvaleronitrile), 2, 2-azobis (4-methoxy-2, 4-dimethylvaleronitrile), 4, 4'-azobis (4-cyano valeric acid), dimethyl-2, 2'-azobis (2-methylpropionate), 2, 2'-azobis [2-(2-imidazolyne-2-yl) propane] dihydrochloride, 2, 2'-azobis [2-(2-imidazoline-2-yl) propane], 2, 2'-azobis {2-methyl-M-[1, 1-bis (hydroxymethyl)-2-hydroxyethyl] propionamide}, 2, 2'-azobis {2-methyl-N-[1, 1-bis (hydroxymethyl)-ethyl] propionamide}, 2, 2'-azobis [2-methyl-N-(2-hydroxyethyl) propionamide], 2, 2-azobisisobutylamide dihydrate, 2, 2'-azobis [2-(hydroxymethyl) propionnitrile] and 2, 2'-azobis (2, 4, 4-trimethylpentane). The chemicals for causing the crosslinking and/or polymerizing reactions to take place are further exemplified by tetraalkylthiuramdisulfide, morphine, disulfide compounds, alkylphenoldisulfide, salt of dithioic acid, such as Sediethyldithiocarbamate, sulfur chloride, selenium, tellurium, zinc white, magnesium oxide, litharge, p-quinonedioxime, p, p'-dibenzoylquinoneoxime, tetrachloro-p-benzoquenone and polo-p-dinitrosobenzene. The quantity of the foregoing chemicals to be added is made to be 0.001 mol% to 500 mol% with respect to the total quantity of all monomer units in the polystyrene resin, preferably 0.005 mol% to 300 mol%. The temperature of the reaction system is made to be 0°C to 100°C, preferably 10°C to 90°C. It is preferable that the concentration of the resin in the above-mentioned reaction system be 0.05 wt% to 39 wt%. Note that the reactions be performed in an atmosphere of inert gas of, for example, nitrogen. As a result, the conjugate diene units in the polystyrene resin is caused to take place the crosslinking and/or polymerizing reactions. The foregoing reactions may be performed before the ion groups are introduced into the styrene or after the ion groups have been introduced. Since the conjugate diene units in the polystyrene resin are crosslinked and/or polymerized, the molecular weight Mw of the obtained polyelectrolyte can be made to be 600,000 or larger. The thus-obtained electrolyte having the large molecular weight can be used as a preferred coagulant for disposing waste water. In a case where the obtained polyelectrolyte is used as the coagulant for disposing waste water, it may be used together with another additives, for example, nonionic polymeric coagulant, anionic polymer coagulant, or cationic polymer coagulant. Then, nonionic polymeric coagulant, anionic polymer coagulant and cationic polymer coagulant which can be used together with the polyelectrolyte will now be described. <Non-Ionic Polymer Coagulant> Polyacrylamide or polymethacrylamide, preferably polyacrylamide may be employed. <Anionic Polymer Coagulant> (Metha) acrylic acid type resin may be used which is exemplified by partial hydrolysate of polyacrylamide or polymethacrylamide; copolymer of acrylic acid or methacrylic acid and acrylamide or methacrylamide and their salts; ternary copolymer of acrylic acid or methacrylic acid, acrylamide or methacrylamide and 2-acrylamide-methylpropanesulfide or vinyl sulfonate or vinylmethyl sulfonic acid, preferably the partial hydrolysate of polyacrylamide, the copolymer of acrylic acid and acrylamide, its salt, and ternary copolymer of acrylic acid, acrylamide and 2-acrylamide-methylpropanesulfide. Polystyrene sulfonate polymers may be employed which are exemplified by polystyrene, styrene-butadiene, styrene-acrylonitrile, styrene-butadiene-acrylonitrile, styrene-(metha) acrylate, styrene-(metha) acrylate (aliphatic hydrocarbon having one to four carbon atoms), styrene-acrylonitrile-(metha) acrylate (aliphatic hydrocarbon having one to four carbon atoms), styrene-butadiene-(metha) acrylate (aliphatic hydrocarbon having one to four carbon atoms), acrylonitrile-maleic anhydride and styrene-itaconic anhydride. Among the foregoing materials, it is preferable that any one of polystyrene, styrene-butadiene, styrene-acrylonitrile, styrene-butadiene-acrylonitrile and styrene-maleic anhydride be employed. The other polymers are exemplified by polyphenyleneether, polycarbonate, polyphenylenesulfide and polyethyleneterephthalate. It is preferable that polyphenyleneether or polycarbonate be employed. <Cationic Polymer Coagulant> It is exemplified by a quaternized material of dialkylaminoalkyl (metha) acrylate (a quaternizing agent may be methylchloride, benzylchloride or the like) or an acidic salt (the acidic salt may be an inorganic acid salt, such as hydrochloride or sulphate or an organic acid salt, such as acetate) or a polymer or a copolymer of the foregoing material and (metha) acrylamide. For example, quaternized methylchloride of dimethylaminoethylacrylate or a polymer or a copolymer of the quaternized methylchloride of dimethylaminoethylacrylate and acrylamide. Quaternized material of dialkylaminoalkyl (metha) acrylamide or an acidic salt or a polymer or a copolymer of the foregoing material and (metha) acrylamide may be employed. For example, a copolymer of quaternized methylchloride of dimethylaminopropylacrylamide and acrylamide may be employed. A material obtained by denaturing polyacrylamide with cation may be employed. For example, a material obtained by Mannich-denaturing or Bofmann-decomposing polyacrylamide may be employed. An epihalohydrin-amine condensation compound may be employed which is exemplified by a polycondensation compound of epihalohydrin and alkylenediamine having two to eight carbon atoms. Polydimethyldiallyl ammoniumchloride may be employed. A dicyanediamide condensation compound may be employed, which is exemplified by formalin condensation compound of dicyanediamide and ammonium chloride. Polyethyleneimine may be employed. The polyelectrolyte according to the present invention may be mixed with the above-mentioned polymer coagulant or the same may sequentially be added. When the polyelectrolyte is used together with the cationic polymer coagulant, it is preferable that the polyelectrolyte according to the present invention be sequentially added. The polyelectrolyte according to the present invention may be used together with a variety of inorganic agglutinant or inorganic coagulant. Since the polyelectrolyte according to the present invention has excellent performance as coagulant for disposing waste water, it contributes to preventing pollution of water and atmosphere. The polystyrene resin for use in the present invention may be a waste as well as a virgin material. Wastes of high-impact polystyrene (hereinafter called as "HIPS") frequently contain a large quantity of conjugate diene units. Therefore, the present invention is significantly effective as a method of recycling polystyrene resin products mass-produced as the foregoing general-purpose resin. When the sulfonic acid or its salt is, as the ion group, introduced into the polystyrene resin that is, sulfonation is performed, sulfon crosslinking takes place and thus the polymers have easily be gelled. If the conjugate diene units exist in the polystyrene resin, sulfon crosslinking in the molecules of the polystyrene resin and between molecules can be prevented. Therefore, gelling can be prevented. Since gelling easily takes place in proportion to the molecular weight of the polymers, the polyelectrolyte having large molecular weight cannot easily be obtained by the conventional technique. The foregoing contrivance enables polyelectrolyte having large molecular weight to easily be manufactured. The conjugate diene which is copolymerized with styrene is exemplified by butadiene and isoprene. The percentage content of the conjugate diene in the foregoing copolymer is made to be 0.1 mol% to 20 mol% with respect to all monomer units, preferably 0.2 mol% to 10 mol%. If the quantity of the conjugate diene units in the polystyrene resin is too small, side reactions in the sulfonating reactions, that is, the effect of preventing the sulfon crosslinking in the molecules and between molecules cannot be obtained as desired. If the quantity of the conjugate diene units is too large, crosslinking reactions can easily take place in the double bond portions of the conjugate diene units. Therefore, the characteristics of the sulfonated polystyrene cannot be realized. In a viewpoint of causing the original characteristic of the sulfonated polystyrene to exhibit, the quantity of the styrene units in the polystyrene resin is made to be 80 mol% or more with respect to all of the monomer units, preferably 90 mol%. When the conjugate diene units are allowed to exist in the polystyrene resin, the stereoscopic constraint of the rigid conjugate diene structure prevents sulfon crosslinking in the molecules and between molecules of the polystyrene resin when the sulfonating process is performed. As a result, gelling can be prevented. Although existence of the conjugate diene units in the polystyrene resin is able to prevent sulfon crosslinking in the molecules and between molecules of the polystyrene resin, there arises a possibility that the crosslinking reactions and polymerizing reactions take place in the double bond portions of the conjugate diene units. If the crosslinking reactions or polymerizing reactions take place in the conjugate diene units, long-term stability of the obtained polyelectrolyte deteriorates. Accordingly, inorganic pigment may be allowed to exist in the reaction system when the sulfonating process is performed. That is, the above-mentioned polyelectrolyte may contain the inorganic pigment. When the inorganic pigment is allowed to exist when the sulfonating process is performed, the inorganic pigment traps radicals. Therefore, crosslinking reactions and polymerizing reactions in the conjugate diene units can be prevented. As a result, the long-term stability of the polyelectrolyte can be improved. Although titanium oxide may be employed as the inorganic pigment, it is preferable that carbon black be employed. The carbon black may be general carbon black for use in a coloring matter for plastics, a reinforcing materials or an electric conductivity agent manufactured by any one of a channel method, a furnace method or a thermal method. The carbon black manufactured by any one of the foregoing method may solely be employed or a mixture of plural types of carbon black manufactured by different methods may be employed. It is preferable that the average particle size of the carbon black be 5 µm to 500 µm, more preferably 10 µm to 50 µm. The contents of the carbon black in the sulfonating reaction system is made to be 0.01 wt% to 20 wt% with respect to the polystyrene resin component, preferable 0.1 wt% to 10 wt%. If the content of the carbon black is too small, the effect of preventing the crosslinking reactions and polymerizing reactions in the conjugate diene becomes insufficient. If the content is too large, the performance as a chemical in the polyelectrolyte deteriorates. What is worse, the cost is raised. When the inorganic pigment is allowed to exist in the sulfonating reaction system, the crosslinking reactions and the polymerizing reactions in the conjugate diene units can be prevented. Therefore, the range for the content of the conjugate diene units in the polystyrene resin can be widened as compared with a structure in which no inorganic pigment exists. If the inorganic pigment is allowed to exist in the sulfonating reaction system, the percentage content of the conjugate diene units with respect to all monomer units is made to be 0.05 mol% to 60 mol%, preferably 0.1 mol% to 40 mol%. Thus, the percentage of content of the styrene units with respect to all of the monomer units is made to be 40 mol% or higher, preferably 60 mol% or higher. If the percentage of content of the conjugate diene units is lower than the above-mentioned range, the effect of preventing the sulfon crosslinking reactions becomes insufficient. In this case, the sulfonating reactions cannot stably be performed. If the percentage of content of the conjugate diene is higher than the above-mentioned range, solubility into the organic solvent deteriorates when the sulfonating reactions of the polystyrene resin are performed in the organic solvent. In this case, the reactions are performed nonuniformly. If the percentage of content of the conjugate diene units is raised excessively, the percentage of content of the styrene units is lowered. Thus, also the quantify of the sulfonic acid or its salt which is introduced is reduced. In this case, the polyelectrolyte having sufficient water solubility cannot be obtained. Even if the percentage of content of the styrene units is high, the polyelectrolyte having sufficient water solubility cannot be obtained in a case where the sulfonation ratio is low. Therefore, the quantity of the sulfonic acid or its salt, which is introduced, is made to be 20 mol% or more, preferably 40 mol% or more. When the polystyrene polyelectrolyte and a stabilizer are mixed, automatic oxidation of the polystyrene polyelectrolyte can be prevented. Moreover, the Long-term stability of the polystyrene polyelectrolyte can be improved. Thus, the polystyrene polyelectrolyte having large molecular weight can be obtained. At this time, the stabilizer must have oxidation preventive effect and/or light stability. The stabilizer having the oxidation preventive effect is exemplified by the phenol type, sulfur type and phosphorous type stabilizers exemplified as follows. The phenol type stabilizer may be a known stabilizer which is exemplified by 2, 6-di-t-butyl-P-cresol, butylated hydroxyanizole (BHA), 2, 6-di-t-butyl-4-methylphenol, 2, 6-di-t-butyl-4-ethylphenol, 3, 5-diphenyl-4-methoxyphenol, stearyl-β-(3, 5-di-t-butyl-4-hydroxyphenyl) propionate, tetrakis [methylene-3-(3', 5'-di-t-butyl-4'hydroxyphenyl) propionate] methane, 2, 2'-methylene-bis-(4-methyl-6-t-butylphenol), 2, 2'-methylene-bis-(4-ethyl-6-t-butylphenol), 2, 2'-methylene-bis (5-t-butyl-4-methylphenol), 2, 2'-methylene-bis-[4-methyl-6-(α-methylcyclohexyl) phenol], 1, 1-bis (5-t-butyl-4-hydroxy-2-methylphenyl) butane, 2, 2'-methylene-bis-(4-methyl-6-cyclohexylphenol), 2, 2'-methylene-bis-(4-methyl-6-nonylphenol), 4, 4'-thiobis-(3-methyl-6-t-butylphenol), 4, 4'-butylidene-bis-(3-methyl-6-t-butylphenol), 3, 9-bis [1, 1-dimethyl-2-[β-(3-t-butyl-4-hydroxy-5-methylphenyl) propionyloxy] ethyl] 2, 4, 8, 10-tetraoxaspiro [5, 5] undecane, 1, 1, 3-tris-(2-methyl-4 hydroxy-5-t-butylphenyl) butane, 1, 1, 3-tris-(6-t-butyl-4-hydroxy-2-methylphenyl) butane, 2, 2-bis-(5-t-butyl-4-hydroxy-2-methylphenyl)-4-n-dodecylmercaptobutane, ethyleneglycol-bis [3, 3-bis (3-t-butyl-4-hydroxyphenyl) butylate], 1, 3, 5-trimethyl-2, 4, 6-tris (3, 5-di-t-butyl-4-hydroxybenzyl) benzene, 1, 1-bis (3, 5-dimethyl-2-hydroxyphenyl)-3-(n-dodecylthio)-butane, 4, 4-thiobis (5-t-butyl-3-methylphenol), 2, 2-bis (3, 5-di-t-butyl-4-hydroxybenzyl) maleic acid dioctadecylester, n-octadecyl-3-(4-hydroxy-3, 5-di-t-butylphenyl) propionate, bis (3, 3'-bis-(4-hydroxy-3'-t-butylphenyl) butylicacid] glycolester, 1, 3, 5-tris (3', 5'-di-t-butyl-4'-hydroxybenzyl)-S-triazine-2, 4, 6-(1H, 3H, 5H) trione, triethyleneglycol-bis [3-(3-t-butyl-4-hydroxy-5-methylphenyl) propionate], α-tricophenol (vitamin E), nordihydroguaiaretic acid, butylhydroxyanisole and gallic acid propyl. As the sulfur type stabilizer, a known stabilizer may be employed, which is exemplified by dilauryl-3, 3'-thiodipropionate, dimyristyl-3, 3'-thiodipropionate, distearyl-3, 3'-thiodipropionate and pentaerythritoltetrakis (3-laurylthiopropionate). As the phosphorus type stabilizer, a known stabilizer may be employed, which is exemplified by triphenylphsophite, diphenylisodecylhosphite, phenyldiisodecylhosphite, 4, 4'-butylidene-bis (3-methyl-6-t-butylphenyl-di-tridecyl) hosphite, cyclic neopentanetetrailbis (octadecylhosphite), tris (norylphenyl) hosphite, tris (mono and/or dinolylphenyl) hosphite, diisodecylpentaerythritoledihosphite, 9, 10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide, 10-(3, 5-di-t-butyl-4-hydroxybenzyl)-9, 10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide, 10-decyloxy-9, 10-dihydro-9-oxa-10-phosphenanthrene, tris (2, 4-di-t-butylphenyl) hosphite, cyclic neopentanetetrailbis (2, 4-di-t-butylphenyl) hosphite, cyclic neopentanetetrailbis (2, 6-di-t-butyl-4-methylphenyl) hosphite, 2, 2-methylenebis (4, 6-di-t-butylphenyl) loctylhosphite, distearylpentaerythritoldihosphite and tetrakis (2, 4-di-t-butylphenyl)-4, 4'-biphenylene-di-hosphite. As the other stabilizer, a known stabilizer may be employed, which is exemplified by erysorbic acid, sorbate soda and isopropyl citrate. The stabilizer is not limited to the above-mentioned type having the oxidation preventive effect. A stabilizer having a light stabilizing effect may be employed. The stabilizer having the light stabilizing effect is exemplified by the following benzophenone type, benzotriazole type, hindered amine type, cyanoacrylate type, salicylate type, oxalycacid anilide type stabilizers. The benzophenone type stabilizer may be a known stabilizer which is exemplified by 2, 4-hydroxybenzophenone, 2-hydroxy-4-methoxybenzophenone, 2-hydroxy-4-octoxybenzophenone, 2-hydroxy-4-methoxybenzophenone-5-sulfonic acid, 2-hydroxy-4-dodecyloxybenzopheone, 2-hydroxy-4-octoxybenzophenone, 2, 2'-dihydroxy-4-methoxybenzophenone, 2, 2'-dihydroxy-4, 4'-dimethoxybenzophenone, 2-hydroxy-4-methoxy-5-sulfobenzophenone and bis (2-methoxy-4-hydroxy-5-benzoilphenyl) methane. The benzotriazole type stabilizer may be a known stabilizer which is exemplified by 2-(2'-hydroxy-5'-methoxyphenyl) benzotriazole, 2-[2'-hydroxy-3', 5'-bis (α, α-dimethylbenzyl) phenyl]-benzotriazole, 2-(2'-hydroxy-3', 5'-di-t-butyl-phenyl)-benzotriazole, 2-(2'-hydroxy-3'-t-butyl-5'-methylphenyl)-5-chlorobenzotriazole, 2-(2'-hydroxy-3', 5'-di-t-amyl)-benzotriazole, 2-(2'-hydroxy-3', 5'-di-t-butylphenyl)-5-chlorobenzotriazole, 2-(2'-hydroxy-5'-t-oxtylphenyl) benzotriazole and 2, 2'-methylnebis [4-(1, 1, 3, 3-tetramethylbutyl)-6-(2N-benzotriazole-2-il) phenol]. The hindered amine type stabilizer may be a known stabilizer which is exemplified by bis-[2, 2, 6, 6-tetramethyl-4-piperidyl] sebacate, bis-[N-methyl-2, 2, 6, 6-tetramethyl-4-piperidyl] sebacate,. tetrakis (2, 2, 6, 6-tetramethyl-4-piperidyl)-1, 2, 3, 4-butanetetracarboxylate, bis-(1, 2, 2, 6, 6-pentamethyl-4-piperidyl)-2-(3, 5-di-t-butyl-4-hydroxybenzyl)-2-n-butylmalonate, tetrakis (1, 2, 2, 6, 6-pentamethyl-4-piperidyl)-1, 2, 3, 4-butanetetracarboxylate, a mixture of 2, 2, 6, 6-tetramethyl-4-piperydyl-1, 2, 3, 4-butanetetracarboxylate and tridecyl-1, 2, 3, 4-butanetetracarboxylate (hereinafter called as (2, 2, 6, 6-tetramethyl-4-piperidyl/tridecyl mixture)-1, 2, 3, 4-butanetetracarboxylate), (1, 2, 2, 6, 6-pentamethyl-4 piperidyl/tridecyl mixture)-1, 2, 3, 4-butanetetracarboxylate, {2, 2, 6, 6-tetramethyl-4-piperidyl/β, β, β', β'-tetramethyl-3, 9-[2, 4, 8, 10-tetraoxaspiro (5, 5) undecane] diethyl mixture}1, 2, 3, 4-butanetetracarboxylate, {1, 2, 2, 6, 6-pentamethyl-4-piperidyl/β, β, β', β'-tetramethyl-3, 9-[2, 4, 8, 10-tetraoxaspiro (5, 5) undecane] diethyl mixture) 1, 2, 3, 4-butanetetracarboxylate and poly [6-(1, 1, 3, 3-tetrametylbutyl) imino-1, 3, 5-triazine-2, 4-diyl][(2, 2, 6, 6-tetramethyl-4-piperidyl) imino] hexamethylene [(2, 2, 6, 6-tetramethyl-4-piperidyl) iminol]. The cyancacrylate type stabilizer may be a known stabilizer which is exemplified by ethyl-2-cyano-3, 3'-diphenylacrylate and 2-ethylhexyl-2-cyano-3, 3'-diphenylacrylate. The salicylate type stabilizer may be a known stabilizer which is exemplified by phenylsalicylate and 4-t-butylphenylsalicylate. The oxalyc acid anilide type stabilizer may be a known stabilizer which is exemplified by 2-ethoxy-2'-ethyloxalycacidbisanilide. The foregoing stabilizer may solely be employed or a mixture of two or more types of the foregoing stabilizers may be employed. Note that stabilizers fordifferent systems attains a more significant effect as compared with use of stabilizers having effects of preventing oxidation of the same systems. The above-mentioned stabilizer is mixed with the above-mentioned polystyrene type polyelectrolyte. At this time, the stabilizer may be added to the water-soluble polystyrene type polyelectrolyte or the same may be added when the ion groups are introduced into the styrene polymer or when the water-soluble styrene monomers are polymerized or copolymerized. As an alternative to this, the stabilizer may be added several times. When the stabilizer is added to the polystyrene type polyelectrolyte, the stabilizer prevents the decomposition reactions of the polystyrene type polyelectrolyte. Therefore, the stabilizer is able to improve the long-term stability of the obtained polyelectrolyte composition. If the stabilizer is added when the ion groups are introduced into the styrene polymer or water-soluble styrene monomers are polymerized or copolymerized, the stabilizer prevents automatic oxidation of the polystyrene type polyelectrolyte attributable to radicals generated during the reactions. As a result, the stabilizer is able to prevent reduction in the molecular weight of the polystyrene type polyelectrolyte. Therefore, the stabilizer is able to prevent reduction in the molecular weight and improve the long-term stability. It is preferable that the stabilizer be added when the ion groups are introduced into the styrene polymers as compared with a method in which the same is added when the water-soluble styrene monomers are polymerized or copolymerized. The reason for this is that the stabilizer unintentionally traps a portion of radicals generated from the polymerization initiator and thus the effect of the polymerization initiator will be inhibited. The quantity of the stabilizer to be added is made to be 0.002 parts by weight to 10 parts by weight with respect to 100 parts by weight of the polystyrene type polyelectrolyte (the solid portion), preferably 0.01 parts by weight to 2 parts by weight regardless of the timing at which the same is added during the manufacturing process or after the polyelectrolyte has been manufactured. If the quantity of the stabilizer is smaller than the above-mentioned range, the effect of the stabilizer deteriorates. If the quantity is too large, cost cannot disadvantageously be reduced. If the quantity of the added stabilizer is too large, the reactions for introducing the ion groups into the styrene polymers is inhibited. The stabilizer may previously be contained in the styrene polymers. In this case, the styrene polymers containing the stabilizer may be wastes discharged from plants, retail shops or homes. If the content of the stabilizer is smaller than the above-mentioned range in a case where the wastes are used, it is preferable that the quantity smaller than the foregoing range is added. If the quantity is too large, it is preferable that other styrene polymers which do not contain the stabilizer be added. If the stabilizer exists in the reaction system when the ion groups are introduced into the styrene polymers, also the stabilizer is made to be water soluble. Therefore, it is preferable that the stabilizer be added during the introduction of the ion groups in a case where non-water soluble stabilizer is used rather than directly adding the same to the polystyrene type polyelectrolyte. As the stabilizer, it is most effective in terms of maintaining the molecular weight of the polystyrene type polyelectrolyte and improving the long-term stability to add a phenol type oxidation preventive material before the ion groups are introduced. As described above, since the stabilizer is able to prevent deterioration in the polystyrene type polyelectrolyte, excellent characteristics can be maintained for a long time. If the stabilizer is added when the ion groups are introduced into the styrene polymers or when the water-soluble styrene monomers are polymerized or copolymerized, the stabilizer is able to prevent automatic oxidation reactions of the polystyrene type polyelectrolyte. As a result, high grade polystyrene type polyelectrolyte having predetermined molecular weight can be manufactured. When the polystyrene resin is sulfonated in the solvent, the alicyclic unsaturated hydrocarbon is added to the reaction system to perform sulfonation reaction with a high concentration. The alicyclic unsaturated hydrocarbon is sulfonated when the sulfonation of the polystyrene resin is performed so as to act as a surface active agent for the slurry which is the product. Thus, the dispersion easiness of the slurry can be improved. Therefore, even if the reaction concentration when the sulfonation is performed is raised, the sulfonation can stably proceed. It is preferable that the alicyclic unsaturated hydrocarbon be in the form of a six membered ring, which is exemplified by monocyclic monoterpene (limonene or terpinene), dicyclic monoterpene (caren, pinene, sabinene or camphene), terpinolene, cyclohexane, monoalkyl (having one to four carbon atoms), cyclohexane and terpineol. Among the above-mentioned materials, it is preferable that any one of the monocyclic monoterpene (limonene, sylvestrene or terpinene), cyclohexene or methylcyclohexene be employed. The quantity of the alicyclic unsaturated hydrocarbon to be added is made to be 0.01 wt% to 5 wt% with respect to the styrene polymers, preferably 0.05 wt% to 1.0 wt%. If the quantity of the alicyclic unsaturated hydrocarbon is smaller than the above-mentioned range, the effect of dispersion of the slurry cannot be obtained. If the quantity is too large, the sulfonated products of alicyclic unsaturated hydrocarbon which are by-products are generated excessively. Therefore, the quality (the purity is lowered) and cost reduction become unsatisfactorily. It is preferable that the alicyclic unsaturated hydrocarbon be added before the sulfonation or during the sulfonation. Polystyrene resin previously containing the alicyclic unsaturated hydrocarbon may be employed as the raw material to perform the sulfonation. If a recycled product recovered from foamed styrol contracted by limonene is used as the raw material, the alicyclic unsaturated hydrocarbon is contained in the raw material. If the foamed styrol is used as the alicyclic unsaturated hydrocarbon, for example, wastes recovered by contracting by using limonene, the necessity of adding the alicyclic unsaturated hydrocarbon when the sulfonation is performed can be removed. Thus, the process from recovery of the foamed styrol to recycling can be realized by an integrated system. The material for contracting the foamed styrol may be isoamyl acetate, benzyl propionate or ethyl acetate, as well as the limonene. If the limonene is used, it can advantageously be used in the sulfonation as it is. The most preferable material is a liquid composition in which 1 volume % to 6 volume % of ethanol is added to limonene. As described above, the alicyclic unsaturated hydrocarbon is allowed to exist in the system during the sulfonation so that the foregoing compound is sulfonated. The sulfonated material acts as a surface active agent for the slurry which is the product. As a result, the dispersion easiness of the slurry can be improved. As a result, the reaction concentration in the sulfonation can be raised. Sulfonation Using Alicyclic Compound as Solvent Initially, the following resins were prepared: (a) polystyrene manufactured by Aldrich and having molecular weight Mw of 280,000; (b) polystyrene-polydimethyldiphenyleneether alloy each having a quantity of 50 wt%; (c) high-impact polystyrene which was a housing member for a used VHS cassette tape; and (d) foamable styrol which was a used cushioning member for a television set. The foregoing resins were used such that resins (a) and (b) were in the form of pellets and (c) and (d) were obtained by crushed by a shredder. Comparative Example 1 The temperature of solution prepared by adding 0.3 g of triethyl phosphate to 70 g of cyclohexane was maintained at 50°C, and then 0.14 g of sulfuric anhydride was added. Then, solution prepared by dissolving 3.5 g polystyrene (a) in 66.5 g cyclohexane in a hot state of 50°C and 2.7 g of sulfuric anhydride were simultaneously dropped to the above-mentioned solution in 60 minutes in a state where the temperature was maintained at 50°C. Then, the sulfonating reaction was performed for one hour in a state where the temperature was maintained at 50 ± 2°C. As the reaction proceeded, slurry products were generated in the reaction solution. Then, 15 g of water solution including 1.5 g of sodium hydroxide was gradually added to the reaction system so that the reaction system was neutralized. Then, the reaction system was heated so that cyclohexane in the reaction system was removed by distillation. Finally, the pH of the water solution of the residue was adjusted to 8 by using sodium hydroxide. As a result, 30 wt% water solution of polyelectrolyte was obtained which was called sample solution according to Example 1. Although cyclohexane was allowed to remain by 40 ppm in the thus-obtained sample water solution according to Example 1, no halogen compound, as a matter of course, was detected. Crosslinkling by Means of Conjugate Diene Units Initially, the following resins were prepared: (e) polystyrene containing no conjugate diene unit, having molecular weight Mw of 280,000 and manufactured by Aldrich; (f) styrene-butadiene copolymer having a composition such that styrene:butadiene = 40:60 (mol%) and molecular weight Mw of 200,000 and manufactured by Scientic Polymer; (g) high-impact polystyrene which was a compound product, which contained butadiene by 2 mol% and which had molecular weight Mw of 220,000; (h) high-impact polystyrene which was a waste of cassette case of VHS tape, which contained butadiene by 1 mol% and which had molecular weight Mw of 180,000; and (i) high-impact polystyrene which was a waste of housing for a television set, which contained butadiene by 4 mol% and which has molecular weight Mw of 230,000. Note that the resins (h) and (i) where obtained by crushing the raw material by a shredder. Example 1 The temperature of solution prepared by adding 0.6 coagulant triethyl phosphate to 70 coagulant of 1, 2-dichloroethane was maintained at 20°C to 25°C, and then 0.27 coagulant of sulfuric anhydride was added to the above-mentioned solution. Then, the temperatures of solution in which 7 g of high-impact polystyrene (g) was dissolved in 63 g of 1, 2-dichloroethane and 4.3 g of sulfuric anhydride were maintained at the above-mentioned level and dropped in 60 minutes. After the addition, water was added, and then the solvent was removed by distillation so that 20 wt% water solution of polystyrene sulfonate was obtained. Then, the residual solution was heated to 50°C, and then 0.15 g of ammonium persulfate was added in nitrogen atmosphere, and then the solution was matured for one hour. Then, water solutionincluding sodium hydroxide was gradually added to the above-mentioned reaction system such that the water solution was stirred so that the reaction system was neutralized. As a result of the above-mentioned process, polystyrene sulfonate soda having molecular weight Mw of 1,400,000 was obtained. The obtained water solution of the polyelectrolyte was called as sample water solution according to Example 1. Example 2 A process similar to that according to Comparative Example 1 was performed except for high-impact polystyrene (h) being employed in place of high-impact polystyrene (g) so that polystyrene sulfonate soda having molecular weight Mw of 900,000 was obtained. The obtained water solution of the polyelectrolyte was called as sample water solution according to Example 2. Example 3 The temperature of solution in which 0.02 g of AlBn was added to 50 g of cyclohexane was maintained at 70°C in a nitrogen atmosphere. Then, solution in which 2.4 g of high-impact polystyrene (g) and 0.92 g of triethyl phosphate were dissolved in cyclohexane and 3.5 g of fuming sulfuric acid were, in a state where their temperatures were made to be the same, simultaneously dropped in 30 minutes. Then, the temperature of the solution was maintained at 70 ± 2°C and reactions were performed for one hour. Then, water solution including sodium hydroxide was, while being stirred, gradually added to the reaction system so that the solution was neutralized. Then, the solution was heated so that cyclohexane in the reaction system was removed by distillation. As a result of the above-mentioned process, polystyrene sulfonate soda having molecular weight Mw of 1,800,000 was obtained. The obtained water solution of the polyelectrolyte was called as sample water solution according to Example 3. Example 4 The temperature of solution in which 2.44 g of triethyl phosphate was added to 70 g of 1, 2-dichloroethane was maintained at 55°C to 60°C. Then, solution in which 6.93 g of high-impact polystyrene (i) was dissolved in 63 g of 1, 2-dichloroethane and 8.4 g of 60 % fuming sulfuric acid were simultaneously dropped to the above-mentioned solution in 60 minutes, followed by maturing the solution for 30 minutes. Then, water solution including sodium hydroxide was, while being stirred, gradually added to the reaction system so that the solution was neutralized. Then, the neutralized mixture was heated at the room temperature so that 1, 2-dichloroethane was removed from the above-mentioned reaction system by distillation. Then, the above-mentioned residual solution was heated to 60°C, and then 30 wt% peroxide solution was added under a nitrogen atmosphere, and then the solution was matured for two hours. As a result of the above-mentioned process, polystyrene sulfonate soda having molecular weight Mw of 2,500,000 was obtained. The obtained water solution of the polyelectrolyte was called as sample water solution according to Example 4. Example 5 0.3 g of 2, 2'-azobis (4-methoxy-2, 4-dimethylvaleronitrile) was added to solution in which 5 g of high-impact polystyrene (h) was added to 20 g tetrachloroethane. Then, the solution was stirred for one hour in a state where the solution was heated to 60°C in a nitrogen air flow. Then, the above-mentioned solution was added to 45 g of chloromethylether, and then 15 g of aluminum chloride was gradually added. In a state where the above-mentioned temperature was maintained, the solution was stirred for three hours. After the reaction, unreacted chloromethylether was distillated under reduced pressure, and then ammonia water having the same mol as that of the chloromethyl groups introduced into the polystyrene resin was added. As a result of the above-mentioned process, polychloromethylstyrene ammonium salt having molecular weight Mw of 2,100,000 was obtained. The obtained water solution of the polyelectrolyte was called as sample water solution according to Example 5. Comparative Example 2 A process similar to that according to Example 1 was performed except for polystyrene (e) being employed in place of high-impact polystyrene (g) so that polystyrene sulfonate soda having molecular weight Mw of 450,000 was obtained. The obtained water solution of the polyelectrolyte was called as sample water solution according to Comparative Example 2. Comparative Example 3 A process similar to that according to Example 1 was performed except for styrene-butadiene copolymer (f) being used in place of high-impact polystyrene (g) so that sulfonation was performed. Then, ammonium persulfulate was added. However, gelled substances were generated in the reaction System when the ammonium persulfulate was added. Thus, the water solution polyelectrolyte was not obtained. Comparative Example 4 In a state where the temperature of solution in which 0.92 g of triethyl phosphate was added to 50 g of cyclohexane was maintained at 70°C, 0.17 g of 60 % fuming sulfuric acid was added. Then, solution in which 2.4 g of high-impact polystyrene (g) was dissolved in 120 g of cyclohexane, and 3.3 g fuming sulfuric acid were simultaneously dropped into the above-mentioned solution in 30 minutes in a state where their temperatures were made to be the same. Then, reactions were performed for one hour in a state where the temperature of the solution was maintained at 70 ± 2°C. Then, water solution including sodium hydroxide was, while being stirred, gradually added to the above-mentioned reaction system so that the reaction system was neutralized. Then, the solution was heated so that cyclohexane in the reaction system was removed by distillation. As a result of the above-mentioned process, polystyrene sulfonate soda having molecular weight Mw of 420,000 was obtained. The obtained water solution of the polyelectrolyte was called as sample water solution according to Comparative Example 4. Comparative Example 5 In a state where the temperature of solution in which 2.44 g of triethyl phosphate was added to 70 g of 1, 2-dichloroethane was maintained at 55°C to 60°C, solution in which 6.93 g of high-impact polystyrene (i) was dissolved in 63 g of 1, 2-dichloroethane and 9.33 g of 60 % fuming sulfuric acid were simultaneously dropped in 60 minutes. Then, the solution was matured for 30 minutes. Then, water solution including sodium hydroxide was, while being stirred, gradually added to the above-mentioned reaction system so that the reaction system was neutralized. Then, the solution was heated so that 1, 2-dichloroethane in the reaction system was removed by distillation. As a result of the above-mentioned process, polystyrene sulfonate soda having molecular weight Mw of 440,000 was obtained. The obtained water solution of the polyelectrolyte was called as sample water solution according to Comparative Example 5. Comparative Example 6 A similar process to that according to Example 5 was performed except for polystyrene (e) being used in place of high-impact polystyrene (h) so that polychloromethylstyrene ammonium salt having molecular weight Mw of 390,000 was obtained. The obtained water solution of the polyelectrolyte was called as sample water solution according to Comparative Example 6. Evaluation of Characteristic The polystyrene resins were refined variously, thus resulting in that polyelectrolytes according to Comparative Examples 2 to 6 had molecular weight Mw of 500,000 or smaller. On the other hand, the polyelectrolytes according to Examples 1 to 5 had molecular weight Mw of 900,000 or larger. The results will individually be evaluated. Comparative Examples 2 and 6 using polystyrene (c) having no conjugate diene unit were resulted such that the polyelectrolyte having large molecular weight was not obtained even if the polymerization initiator was added. Comparative Examples 4 and 5 using high-impact polystyrene (g) and (i) containing conjugate diene units resulted in that the polyelectrolyte having large molecular weight could not be obtained because crosslinking and/or polymerizing was not performed. Comparative Example 4 using copolymer (f) containing conjugate diene units in an excessively large quantity resulted in that gellation occurred when the crosslinking was performed. Thus, the water-soluble polyelectrolyte could not be obtained. On the other hand, Examples 1 to 5 respectively using high-impact polystylene (g) to (i) containing the conjugate diene units in an appropriate quantity and subjected to crosslinking and/or polymerizing reactions resulted in that the polyelectrolyte having large molecular weight was obtained. As can be understood from results of comparisons among Examples 1, 2 and 4, use of conjugate diene units in the employed polystyrene resin in a proper quantity permits wastes to be used as the polystyrene resin. Moreover, a fact can be understood from results of comparisons between Examples 1, 3 and 4 that the crosslinking agent may be added after the ion groups have been introduced, the crosslinking agent and the sulfonating agent may simultaneously be added and the crosslinking agent may be added after the ion groups have been neutralized. As a result of a comparison between Examples 2 and 5, the ion groups to be introduced into the polystyrene resin may be either sulfonic acid soda or chloromethylated ammonium salt. As a result, a fact was detected that the method having the step of introducing ion groups into polystyrene resin containing the conjugate diene units in an adequate quantity and the step of crosslinking and/or polymerizing the conjugate diene units in the resin enables water-soluble polyelectrolyte having large molecular weight to be obtained. Moreover, the characteristics of the obtained sample water solutions to serve as the coagulant for disposing waste water were evaluated. Initially, the sample water solution of a type composed of the polyelectrolyte into which the sulfonic acid soda had been introduced as the ion groups was evaluated. Specifically, solution in which 50 ppm of aluminum sulfate was added to waste water from an electronic part plant (pH = 6.0 and concentration of suspended materials (ss) = 500 ppm) was prepared as the suspended solution for evaluating the coagulation. Then, 100 ml of suspended solution was injected into 200 ml measuring cylinder having a stopper, followed by injecting the sample water solutions according to Examples 1 to 4 and Comparative Examples 2, 4 and 5 in a quantity with which the concentration of the resin component in the suspended solution for evaluating coagulation was made to be 2.0 ppm. Immediately after this, the measuring cylinder was vertically rotated ten times, and then the same was allowed to stand. Then, the sedimentation rate of the suspended particles and the turbidity of the filtrate after the coagulation were measured. Moreover, similar measurements were performed about a process in which 1 ppm of the sample water solution according to Example 2 and 1 ppm of commercial coagulant A (partial hydrolysate of polyacrylamide) were mixed and a process in which 2 ppm of the commercial coagulant A was solely used. Results were. shown in Table 1. Sedimentation Rate (m/hour) Turbidity (ppm) Example 1 25 8 Example 2 20 10 Example 3 28 5 Example 4 32 5 Example 2 + A 22 7 A 20 17 Comparative Example 2 15 14 Comparative Example 4 17 16 Comparative Example 5 17 13 As can be understood from Table 1, the sample water solutions according to the examples had basic characteristics as the polymer coagulant superior to those of the sample water solution according to Comparative Example 5 and those of the commercial coagulant. Moreover, another fact was detected that a satisfactory effect could be obtained if the sample water solution according to the example and the commercial coagulant are used together. Then, the sample water solution composed of the polyelectrolyte into which chloromethylated ammonia salt had been introduced as the ion group was evaluated. Specifically, mixed sludge (pH = 6.8 and concentration of suspended materials (ss) = 1.1 wt%) disposed from a sewerage disposal plant was prepared as suspended solution for evaluating coagulation. In a state where the suspended solution was stirred in a jar tester, the sample water solutions according to Example 5 and Comparative Example 6 were injected in a quantity with which the resin component is made to be 0.5 wt% per the suspended materials (ss) . Then, the solution was allowed to stand, and then the sedimentation rate of the suspended particles and the turbidity of the filtrate after the coagulation were measured. Moreover, a process in which a mixture of the sample water solution according to Example 5 and commercial coagulant B (quaternized N, N-dimethylaminomethylacrylatemethylchloride) and a process in which the above-mentioned commercial coagulant B was solely used were similarly evaluated. Results were shown in Table 2. Sedimentation Rate (m/hour) Turbidity (ppm) Example 5 35 20 Example 5 + B 38 25 B 34 40 Comparative Example 6 5 62 As can be understood from Table 2, the samole water solution according to Example 5 had basic characteristic as the polymer coagulant superior to those of Comparative Example 6 and the commercial coagulant. Another fact was detected that use of both of the sample water solution according to Example 5 and the commercial coagulant attains a satisfactory effect. As a result, a fact was detected that the polyelectrolyte in which the ion groups were introduced into the polystyrene having the conjugate diene units in an adequate quantity and in which the conjugate diene units in the resin are crosslinked and/or polymerized had significantly excellent characteristics as the coagulant for disposing waste water. Introduction of Conjugate Diene Units Initially, the hollowing resins were prepared: (j) polystyrene containing no conjugate diene unit, having molecular weighs MW of 280,000 and manufactured by Aldrich; (k) styrene-butadiene copolymer having composition as styrene:butadiene = 85:15 (mol%) and manufactured by Polyscience; (l) high-impact polystylene which was a waste of VHS cassette case and contained butadiene by 1 mol%; (m) high-impact polystylene which was a waste of housing of a television set and which contained butadiene by 5 mol%; and (n) styrene-butadiene copolymer having composition as styrene:butadiene = 40:60 (mol%) and manufactured by Scientificpolymer. As the resins (l) and (m) were obtained by crushing by using a shredder. Example 6 6 g of styrene-butadiene copolymer (g) was dissolved in 54 g of 1, 2-dichloroethane, and then the temperature of the solution was maintained at 50°C. Then, 7.7 g of 60 % fuming sulfuric acid was dropped in 30 minutes, and then the temperature was maintained at the above-mentioned level so that sulfonation was completed. Although slurry reactants were generated in the reaction solution as the reactions proceeded, gelled substances were not allowed to adhere to the wall surface of the reaction container. Then, sodium hydroxide solution was gradually added into the reaction system so that the solution was neutralized. Then, the solution was heated so that 1, 2-dichloroethane in the reaction system was removed by distillation. Then, pH of water solution of the residue was finally adjusted to 8 by using sodium hydroxide. The thus-obtained polyelectrolyte solution was adjusted in such a manner that the concentration of the resin was 0.1 wt%. The prepared solution was called as sample water solution according to Example 6. Example 7 The temperature of solution in which 0.1 g triethyl phosphate was added to 70 g of cyclohexane was maintained at 50°C, and then 0.14 g of sulfuric anhydride was added. Then, solution, in which 6 g of styrene-butadiene copolymer (k) was dissolved in 66.5 g cyclohexane, and 2.7 g of sulfuric anhydride were simultaneously dropped into the above-mentioned solution in 60 minutes in a state where their temperature of the solution was maintained at 50°C. Then, the temperature of the solution was maintained at 50 ± 2°C, and then sulfonation was performed for one hour. Also slurry products were generated in the reaction solution as the reactions proceeded, gelled subscances were not allowed to adhere to the wall surface of the reaction container until reactions were completed. Then, neutralization was performed similarly to Example 14, and then the solution was heated so that cyclohexane in the reaction system was removed by distillation. The pH of the water solution of the residue was finally adjusted to 8 by using sodium hydroxide. The thus-obtained polyelectrolyte solution was adjusted in such a manner that the concentration of the resin was 0.1 wt%. The prepared solution was called as sample water solution according to Example 7. Example 8 The temperature of solution in which 1.2 g of triethyl phosphate was added to 70 g of cyclohexane was maintained at 20°C to 25°C. Then, solution, in which 6.93 g of high-impact polystylene (l) was dissolved in 1, 2-dichloroethane, and 9.33 g of 60 % fuming sulfuric acid were simultaneously dropped to the above-mentioned solution in 60 minutes in a state where their temperature was maintained at 20°C to 25°C. As a result, sulfonation was performed. Also slurry products were generated in the reaction solution as the reactions proceeded, gelled substances were not allowed to adhere to the wall surface of the reaction container until reactions were completed. Then, neutralization was performed similarly to Example 14, and then the solution was heated so that 1, 2-dichloroethane in the reaction system was removed by distillation. The pH of the water solution of the residue was finally adjusted to 8 by using sodium hydroxide. The thus-obtained polyelectrolyte solution was adjusted in such a manner that the concentration of the resin was 0.1 wt%. The prepared solution was called as sample water solution according to Example 8. Example 9 A process similar to that according to Example 7 was performed except for high-impact polystyrene (m) being used so that sulfonation was performed. Also slurry products were generated in the reaction solution as the reactions proceeded, gelled substances were not allowed to adhere to the wall surface of the reaction container until reactions were completed. Then, neutralization was performed similarly to Example 14, and then the solution was heated so that cyclohexane in the reaction system was removed by distillation. The pH of the water solution of the residue was finally adjusted to 8 by using sodium hydroxide. The thus-obtained polyelectrolyte solution was adjusted in such a manner that the concentration of the resin was 0.1 wt%. The prepared solution was called as sample water solution according to Example 8. Comparative Example 7 A process similar to that according to Example 14 was performed except for polystyrene (j) being used as the resin so that sulfonation was performed. In this case, bulk shape gelled substances were generated in the reaction solution 10 minutes after start of the dropping process. When the dropping operation was completed, the gelled substances were unintentionally allowed to adhere to the wall surface of the reaction container. Even after alkaline solution was added similarly to Example 6, the gelled substance could not be dissolved. Comparative Example 8 A process similar to that according to Example 15 was performed except for polystyrene (j) being used as the resin so that sulfonation was performed. Also slurry products were generated in the reaction solution as the reactions proceeded, gelled substances were not allowed to adhere to the wall surface of the reaction container until reactions were completed. Then, neutralization was performed similarly to Example 14, and then the solution was heated so that cyclohexane in the reaction system was removed by distillation. However, white insoluble substances (polystyrene insufficiently sulfonated) was generated in the water solution of the residue. The insoluble substances were removed by using a filter, and then the final pH of the filtrate was adjusted to 8 by using sodium hydroxide. The thus-obtained polyelectrolyte solution was adjusted in such a manner that the concentration of the resin was 0.1 wt%. The prepared solution was called as sample water solution according to Comparative Example 8. Comparative Example 9 A process similar to that according to Example 16 was performed except for polystyrene (n) being used as the resin so that sulfonation was performed. In this case, bulk shape gelled substances were generated in the reaction solution as the sulfonation proceeded. When the dropping operation was completed, the gelled substances were unintentionally allowed to adhere to the wall surface of the reaction container. Even after alkaline solution was added similarly to Example 14, the gelled substance could not substantially be dissolved. Evaluation of Characteristics As described above, various resins were sulfonated. As a result, the cases according to Examples 6 to 9 where polystyrene resin (k), (l) and (m) each containing the conjugate diene units in a proper quantity were free from generation gelled substances and thus the sulfonation was stably performed. In Comparative Examples 8 and 9 in which polystyrene resin (j) which did not contain the conjugate diene was used and in Comparative Example 10 in which polystyrene resin (n) containing the conjugate diene units at an excessively high ratio, gelled substances were generated during the sulfonation process or insoluble resin unintentionally left in water. As a result, when polystyrene resin containing the conjugate diene units by 0.1 mol% to 20 mol% with respect to all of monomer units is sulfonated, a polyelectrolyte having sufficient water solubility and free from gellation can be obtained. The effects as the coagulant of the sample water solutions according to Examples 6 to 8 including resins which were sufficiently refined into water-soluble polyelectrolyte and the sample water solution according to Comparative Example 8 including resins a poor portion of which was refined into water-soluble polyelectrolyte were examined. Specifically, solution in which aluminum sulfate was added to 5.0 wt% kaolin solutions in such a manner that the aluminum sulfate was 0.1 wt% with respect to pure water was prepared as suspended solution for evaluating coagulation. Then, 100 ml of the suspended solution was injected into a 200 ml measuring cylinder having a stopper, and then the sample water solutions according to Example 6 to 9 and Comparative Example 8 were injected into the measuring cylinder in a quantity with which the resin component was made to be 20 ppm. Immediately after this, the measuring cylinder was vertically rotated ten times, and then allowed to stand. Then, the sedimentation rate of the suspended particles and the turbidity of the filtrate after the coagulation were measured. Results were shown in Table 2. Sedimentation Rate (cm/minute) Turbidity (ppm) Example 6 17 22 Example 7 15 21 Example 8 15 24 Example 9 18 23 Comparative Example 8 12 30 As can be understood from Table 2, the sample water solutions according to Examples 6 to 9 had basic characteristics as the polymer coagulant. On the other hand, the sample water solution according to Comparative Example 8 resulted in slow sedimentation rate and an insufficient effect of preventing lowering in the turbidity of the filtrate. The reason why the coagulating effect of the sample water solution according to Comparative Example 8 was unsatisfactory was that non-uniform introduction of sulfonation into the sample water solution according to Comparative Example 8 (resins sulfonated at high ratio and those sulfonated insufficiently coexisted) caused the portion having the composition which is effective to serve as the coagulant was too small with respect to the overall quantity of the addition. Addition of Inorganic Pigment In this experiment, an effect obtainable from causing carbon black as inorganic pigment to exist when the ion groups are introduced will be confirmed. Initially, the following resins were prepared: (o) high-impact polystyrene containing butadiene by 2 mol%, containing no carbon black and having molecular weight Mw of 220,000; (p) high-impact polystyrene which was a waste of VHS cassette case, which contained butadiene by 1 mol% and carbon black by 1 wt% and the molecular weight Mw of which was 180,000; (q) an alloy of high-impact polystyrene-polyphenylneeether, which was a waste of housing for a CD-ROM driver, which contained butadiene in high-impact polystyrene by 2 mol% and carbon black by 2 wt% with respect to overall quantity of the alloy and in which the molecular weight Mw of the high-impact polystylene was 200,000; and (r) high-impact polystyrene which was a waste of a housing of a television set, contained butadiene by 4 mol% and carbon black by 1 wt% and the molecular weight of which was 230,000. The resins (p) to (r) were obtained by crushing the materials by a shredder. As the carbon black, a standard material (HCC type having an average particle size of 9 µm to 14 µm) for a color product was prepared. Example 10 The temperature of solution in which 0.6 g of triethyl phosphate and 0.5 g of carbon black were added to 70 g of l, 2-dichloroethane was maintained at 20°C to 25°C, and then 0.27 g of sulfuric anhydride was added. Then, solution, in which 7.0 g of high-impact polystyrene (o) was dissolved in 63 g of 1, 2-dichloroethane, and 4.3 g of sulfuric anhydride were simultaneously dropped to the above-mentioned solution in 60 minutes in a state where the temperature of the solution was maintained at 20°C to 25°C. Then, the sulfonation was performed for one hour. Then, sodium hydroxide solution was, while being stirred, gradually added to the above-mentioned reaction system so that the solution was neutralized. The thus-obtained polyelectrolyte solution was called sample water solution according to Example 10. Example 11 The temperature of solution in which 0.6 g of triethyl phosphate was added to 70 g of 1, 2-dichloroethane was maintained at 20°C to 25°C, and then 0.27 g of sulfuric anhydride was added. Then, solution, in which 7.0 g of high-impact polystyrene (p) was dissolved in 63 g of 1, 2-dichloroethane, and 4.3 g of sulfuric anhydride were simultaneously dropped to the above-mentioned solution in 60 minutes in a state where the temperature was maintained at 20°C to 25°C. Then, sulfonation was performed for one hour. Then, sodium hydroxide solution was, while being stirred, gradually added to the above-mentioned reaction system so that the solution was neutralized. The thus-obtained polyelectrolyte solution was called sample water solution according to Example 11. Example 12 A process similar to that according to Example 6 was performed except for the alloy of high-impact polystyrene-polyphenyleneether (q) being employed as the resin so that sulfonation was performed. Then, the solution was neutralized. The thus-obtained polyelectrolyte solution was called sample water solution according to Example 12. Example 13 5 g of high-impact polystyrene (r) was dissolved in 20 g of tetrachloroethane, and then 45 g of chloroether was added. Then, 15 g of aluminum chloride was gradually added and stirred for 3 hours at 60°C. After reactions had been completed, the residual chloromethylether was distillated under lowered pressure, and then ammonia water having the same mol as that of the chloromethyl groups introduced into the resin (r) was added. As a result, chloromethylated amine salt was introduced into the resin (r). The thus-obtained polyelectrolyte solution was called sample water solution according to Example 13. Example 14 As an alternative to addition of carbon black prior to performing sulfonation, 0.5 g of carbon black was added after the sulfonation process and the neutralizing process. A process similar to that according to Example 10 was performed except for the above-mentioned process so that a polyelectrolyte was obtained. The thus-obtained polyelectrolyte solution was called sample water solution according to Example 14. Comparative Example 10 A process similar to that according to Example 11 was performed except for high-impact polystylene (o) being used as the resin so that sulfonation was performed. Then, the solution was neutralized. The thus-obtained polyelectrolyte solution was called sample water solution according to Comparative Example 10. Comparative Example 11 A process similar to that according to Example 13 was performed except for high-impact polystyrene (o) being used as the resin so that chlorometylation was performed. Then, the solution was neutralized. The thus-obtained polyelectrolyte solution was called sample water solution according to Comparative Example 11. Evaluation of Characteristics The long-term stability of each of the sample water solutions according to the Examples 10 to 14 and Comparative Examples 10 and 11 was evaluated. Specifically, sample water solutions were injected into sample bottles made of transparent glass and sample bottles made of light shielding glass, and then allowed to stand at the room temperature for three months. At an interval of one month, the state of each sample water solution was observed. Results of reservation in the sample bottles made of transparent glass were shown in Table 3, while results of reservation in the sample bottles made of light shielding glass were shown in Table 4. After One Month After Two Months After Three Months Example 10 no change no change no change Example 11 no change no change no change Example 12 no change no change no change Example 13 no change no change no change Example 14 carbon black deposited carbon black deposited carbon black deposited Comparative Example 10 gelled substances gelled substances gelled substances Comparative Example 11 gelled substances gelled substances gelled substances After One Month After Two Months After Three Months Example 10 no change no change no change Example 11 no change no change no change Example 12 no change no change no change Example 13 no change no change no change Example 14 carbon black deposited carbon black deposited carbon black deposited Comparative Example 10 no change no change gelled substances generated partially Comparative Example 11 no change no change gelled substances generated partially As can be understood from Tables 3 and 4, the sample water solutions according to Comparative Examples 10 and 11 each having no carbon black contained therein encountered generation of gelled substances. On the other hand, the sample water solutions according to Examples 10 to 14 each containing carbon black were free from generation of gelled substances during reservation and thus they have excellent long-term stability. As can be understood from results of Examples 10 to 14, long-term stability can be obtained by introducing the ion groups into the resin, such as resins (p) to (r), previously containing carbon black or by adding carbon black to the reaction system when the ion groups are introduced. If carbon black is added to the polyelectrolyte solution into which the ion groups have been introduced, deterioration of the resin components in the sample water solution with time can be prevented. Since added carbon black cannot uniformly be dispersed and the carbon black is deposited in this case, it is preferable that carbon black be allowed to exist when the ion groups are introduced as is performed in each of Examples 10 to 13. As a result, introduction of the ion groups in a state where inorganic pigment exists in the reaction system is able to improve the long-term stability. Addition of Stabilizer To prepare polyelectrolyte, the following raw materials were prepared. <Stabilizer> (1) triethyleneglycol-bis [3-(3-t-butyl-4-hydroxy-5-methylphenyl) propionate] (2)dilaurylthiodipropionate (3) 3, 9-bis [1, 1-dimethyl-2-[β-(3-t-butyl-4-hydroxy-5-methylphenyl) propionyloxy] ethyl] 2, 4, 8, 10-tetraoxaspyro [5, 5] undecane (4) tris (2, 4-di-t-butylphenyl) phosphite (5) bis-[2, 2, 6, 6-tetramethyl-4-piperidyl] sebacate (6) erysorbic acid soda <Raw Material for Polymer> (A) polystyrene: reagent molecular weight Mw: 290,000 stabilizer: not added (B) high-impact polystyrene: waste of housing for VHS cassette tape molecular weight Mw: 190,000 stabilizer (1) + (2): 0.05 wt% + 0.05 wt% (with respect to the weight of the resin) (C) polystyrene-polyphenyleneether alloy: material for housing for CD-ROM driver polystyrene (molecular weight Mw: 200,000)/polyphenyleneether = 1/1 (weight ratio) oxidation preventive material (3) + (4) + (5) = 0.1 wt% + 0.5 wt% + 1 wt% (with respect to the weight of the resin) Materials (B) and (C) were obtained by crushing the raw materials by a shredder. <Water-Soluble Polystyrene Polyelectrolyte> (D) poly (vinylbenzyl trimethylammomonium chloride) solution: Reagent molecular weight Mw: 100,000 stabilizer: not added Note that the molecular weight of each polymer was measured by GPC analysis. Example 15 0.02 g of the stabilizer (1) was added to solution in which 0.6 g of triethyl phosphate was added to 70 g of 1, 2-dichloroethane. Then, in a state where the temperature of the solution was maintained at 20°C to 25°C, 0.27 g of sulfuric anhydride was added. Then, solution in which 7.0 g of the polymer material (A) was dissolved in 63 g of 1, 2-dichloroethane and 4.3 g of sulfuric anhydride were simultaneously dropped in 60 minutes in state where their temperature were made to be the same. After reactions were performed for one hour, sodium hydroxide solution was, while being stirred, gradually added to the reaction system so that neutralization was performed. As a result of the above-mentioned process, polystyrene sulfonate soda solution (a polyelectrolyte composition according to Example 15) having molecular weight Mw of 710,000 was obtained. Example 16 0.17 g of fuming sulfuric acid (containing SO 3 by 60 wt%) was added in a state where the temperature of solution in which 0.92 g of triethyl phosphate was added to 50 g of cyclohexane was maintained at 50°C. Then, solution in which 2.4 g of the polymer material (B) which contained the stabilizer and which was a waste was dissolved in 120 g of cyclohexane and 3.3 g of fuming sulfuric acid were simultaneously dropped in 30 minutes in state where their temperatures were made to be the same. Then, the temperature was maintained at 50 ± 2°C and the reactions were performed for one hour. Then, 21 g of water solution containing 2.1 g of sodium hydroxide was gradually added while stirring the water solution so that neutralization was performed. Then, the solution was heated so that cyclohexane which was the solvent was removed by distillation. As a result of the above-mentioned process, a polyelectrolyte composition having molecular weight Mw of 4,500,000 and according to Example 16 was obtained. Example 17 A process similar to that according to Comparative Example 12 was performed except for the polymer material (C) being employed so that sulfonation was performed. The molecular weight Mw of the obtained polystyrene sulfonate soda (a polyelectrolyte composition according to Example 25) was 500,000. Example 18 The stabilizer (6) was added to 25 wt% water solution (Mw: 100,000) of the water-soluble polystyrene polyelectrolyte (D) with respect to 100 parts by weight of a polyelectrolyte so that a polyelectrolyte composition according to Example 18 was obtained. Comparative Example 12 A similar process to that according to Example 15 was performed except for the stabilizer (1) being omitted so that a sample according to Comparative Example 13 was prepared. In this case, polystyrene sulfonate soda solution (a polyelectrolyte composition according to Comparative Example 13) having molecular weight Mw of 500,000 was obtained. Comparative Example 13 A process similar to that according to Example 18 was performed except for the stabilizer (6) being omitted so that a polyelectrolyte composition according to Comparative Example 14 was obtained. Examination of Effects Effects of Examples 15 to 18 and Comparative Examples 12 and 13 were examined as follows: The examination was performed such that samples according to Examples 5 to 18 and Comparative Examples 12 and 13 were respectively injected into transparent glass bottles. To measure deterioration of each sample with time, the appearance and the molecular weight were measured when the samples were manufactured, and after six and 12 months. Results were shown in Table 5. Sample when manufactured after 6 months after 12 months Example 15 (molecular weight) (appearance) 710,000 transparent 700,000 transparent 700,000 transparent Example 16 (molecular weight) (appearance) 450,000 light yellow 430,000 light yellow 430,000 light yellow Example 17 (molecular weight) (appearance) 500,000 light yellow 490,000 light yellow 480,000 light yellow Example 18 (molecular weight) (appearance) 100,000 transparent 98,000 transparent 98,000 transparent Comparative Example 12 (molecular weight) (appearance) 500,000 transparent 360,000 light yellow 280,000 light yellow Comparative Example 13 (molecular weight) (appearance) 100,000 transparent 78,000 transparent 61,000 light yellow As can be understood from Table 5, the polyelectrolyte compositions according to Comparative Examples 12 and 13 encountered reduction in the molecular weight with time and also the apparatus was changed. On the other hand, the polyelectrolyte compositions according to Examples 15 to 18 resulted in that the molecular weight when manufactured was substantially the same even after the long time had passed. Appearance of each of the polyelectrolyte compositions according to Examples 15 to 18 was not changed with time. As can be understood from the above-mentioned results, the polyelectrolyte composition according to the present invention is able to prevent reduction in the molecular weight because the stabilizer prevents the decomposition reactions of the Polystyrene polyelectrolyte. Since the stabilizer of the polyelectrolyte according to the present invention is able to improve the stability of the polystyrene polyelectrolyte with time, the appearance can be maintained even after allowed to stand for a long time. Therefore, the polyelectrolyte composition according to the present invention is able to maintain the high quality of the polystyrene polyelectrolyte for a long time. When Example 15 and Comparative Example 12 shown in Table 5 are compared, the molecular weight of Example 15 when manufactured is larger than that of Comparative Example 12. As a result, addition of the stabilizer when the ion groups are, as is performed in Example 15, introduced into the styrene polymers is able to prevent reduction in the molecular weight when manufactured. That is, as can be understood from Example 15, the stabilizer is able to inhibit automatic oxidation reactions of the styrene polymers attributable to radicals generated owning to oxygen in the air, heat, light or metal. Therefore, the method of manufacturing the polyelectrolyte composition according to the present invention is able to prevent reduction in the molecular weight of the polystyrene polyelectrolyte and manufacture a polyelectrolyte composition containing high grade polystyrene polyelectrolyte. Also the polyelectrolyte compositions according to Examples 16 and 17 using the wastes were free from reduction in the molecular weight and change in the appearance. Therefore, a fact was confirmed that usual wastes can effectively be used as the raw material for the polyelectrolyte composition according to the present invention. Addition of Alicyclic Unsaturated Hydrocarbon (Sulfonation of Polystyrene Resin) As the polystyrene resin, the following materials were prepared. (E) reagent polystyrene having molecular weight Mw of 220,000 (no inorganic pigment added); (F) waste polystyrene which was polystyrene (containing limonene by 0.2 wt%) obtained such that foamable styrol was dissolved in limonene and limonene was removed by distillation by a heating separator and having molecular weight of 220,000 (containing no inorganic pigment added thereto); and (G) waste high-impact polystyrene which was a waste of a housing for a VHS cassette tape and which had molecular weight Mw of 200,000 (containing carbon black by 1 wt%). Note that polystyrene resin (G) was obtained by crushing the raw material by a shredder. Comparative Example 14 6.0 g of polystyrene (E) was added to 40 g of 1, 2-dichloroethane to which 2.0 g of triethyl phosphate was added, and then the polystyrene was dissolved. Then, 7.7 g of 60 % fuming sulfuric acid was dropped in 30 minutes in a state where the temperature of the above-mentioned solution was maintained at 30°C. After start of the dropping operation, a large quantity of slurry was generate in the reaction system in about 10 minutes. When the dropping operation was ended, the operation of the stirrer (a magnetic stirrer) was stopped attributable to the bulk slurry in the bottom of the reactor. Then, the solution was matured for one hour. Obtained slurry could not completely be dissolved in water or alkaline solution. Example 19 Sulfonation was performed by the same method as that employed in Comparative Example 14 and using the polystyrene waste (B). Slurry deposited during the reactions was dispersed uniformly and thus the stirrer was able to rotate until the completion of the reactions. The obtained slurry was completely dissolved in water and alkaline solution. The molecular weight (Mw) of the obtained polyelectrolyte was 460,000. Comparative Example 15 0.35 g of sulfuric anhydride was added in a state where the temperature of solution in which 0.3 g of triethyl phosphate was added to 30 g of cyclohexane was maintained at 50°C. Then, solution in which 6.0 g of waste high-impact polystyrene (G) was dissolved in 64 g cyclohexane in a hot state of 50°C and 4.5 g of sulfuric anhydride were simultaneously dropped in 60 minutes such that their temperatures were made to be the same. Also in this case, slurry was deposited during the dropping operation. When the dropping operation was completed, the operation of the stirrer was stopped attributable to the bulky slurry in the bottom of the reactor. Then, the solution was manured in the above-mentioned state for one hour. The obtained slurry was not completely dissolved in water and alkaline solution. Example 20 A method similar to that according to Comparative Example 15 was employed except for 0.05 g of cyclohexene being added to cyclohexane in which high-impact polystylene waste (G) so that sulfonation was performed. Slurry deposited during the reactions was dispersed uniformly and thus the stirrer was able to rotate until the completion of the reactions. The obtained slurry was completely dissolved in water and alkaline solution. The molecular weight (Mw) of the obtained polyelectrolyte was 400,000. Example 21 6.0 g of polystyrene (A) was added to 40 g of 1, 2-dichloroethane to which triethyl phosphate was added, and then the polystyrene (A) was dissolved. Then, terpinene was added by 0.03 g, and then 7.7 g of 60 % fuming sulfuric acid was dropped in 30 minutes in a state where the temperature of the solution was maintained at 30°C. Although a large quantity of slurry was generated in the reaction system about 10 minutes after start of the dropping operation, the slurry was dispersed uniformly and thus the stirrer was not stopped. The obtained slurry was completely dissolved in water and alkaline solution. The molecular weight (Mw) of the obtained polyelectrolyte was 480,000. Example 22 A method similar to that according to Example 20 was employed except for 0.05 g of methylcyclohexane being used in place of terpinene so that sulfonation was performed. Also in this case, slurry which was dissolved in water and alkaline solution was generated and the molecular weight (Mw) of the polyelectrolyte was 450,000l As a result of Comparative Example 14 and Example 19, use of the polystyrene resin previously containing the alicyclic unsaturated hydrocarbon (limonene) enables sulfonation to be performed at a high concentration. Moreover, addition of the alicyclic unsaturated hydrocarbon to the system according to Comparative Example 14, sulfonation can be performed at a high concentration as can be performed in Examples 20 and 21. As can be understood from the results of Comparative Example 15 and Example 20, addition of the alicyclic unsaturated hydrocarbon to the sulfonating reaction system enables sulfonation to stably be performed at a high concentration.

Claims: A water-soluble polyelectrolyte comprising: a crosslinked sulfonated styrene-conjugated diene copolymer having a weight average molecular weight of 600.000 or more derived from crosslinking of poly(styrene-co-conjugated diene)copolymer starting materials having a molecular weight of from 5.000 to 500.000 and comprising from 0.1 mol-% to 10 mol-% of conjugated diene units wherein 20 % or more af all monomer units are sulfonated with sulfonic acid of sulfonic acid salt groups. A polyelectrolyte as defined in claim 1, wherein the crosslinked sulfonated styrene-conjugated diene copolymer comprises a crosslinked sulfonated styrene-butadiene copolymer. A polyelectrolyte as defined in claim 2, wherein said crosslinked sulfonated styrene-butadiene copolymer is a crosslinked sulfonated styrene-butadiene copolymer derived from styrene-butadiene copolymer. A polyelectrolyte as defined in claim 3, wherein 40 mol % or more of all monomer units are sulfonated.

Inventors: INAGAKI YASUHITA, KUROMIYA MIYUKI, NOGUCHI TSUTOMU, WATANABE HARUO, INAGAKI, YASUHITA, KUROMIYA, MIYUKI, NOGUCHI, TSUTOMU, WATANABE, HARUO
Applicants: SONY CORP, SONY CORPORATION
Application year: 1997
Main classification: C08F8
IPC codes: C08F8, C08F236