Process for the solid state polycondensation of polyamide resins

Abstract: Process for the solid state polycondensation of polyamide resins by the use in the polycondensation reactor of a quantity of an inert gas such that the ratio by weight between the solid capacity/h at the reactor outlet and that one of gas fed into the reactor is lower than 0.5.

Description: The present invention relates to a process for the solid state polycondensation of polyamide resins. The polyamide resins, particularly among them PA6, PA6,6, PA11, PA12 and their copolymers, find wide application in both the fibres and flexible packaging area, or in the articles produced by extrusion and blowing technologies. While for fibres the relative viscosity of the resin is low (RV=2.4-3.0 for PA6), for applications in the flexible packaging area and for the articles produced by extrusion/blowing technologies higher relative viscosity are necessary (RV=3.2-50 for PA6). The viscosity is increased to the required values (higher than 3) by means of SSP processes of the resin at temperatures between 140°C and 240°C in conformity with the type of polyamide used. SSP processes are known for example from patent application EP-A-0 038 094, which describes a SSP process for polyamide 4,6. In particular, this application indicates the possibility of using phosphoric acid to accelerate the solid state reaction. US-A-3,821,171 describes a SSP process, wherein the chips are first heated outside the reactor and the heating phase is completed in the reactor. In particular, this heating can be made by using an inert gas and in particular nitrogen. The SSP of 6 type polyamides was studied in particular by M.R. Kulkarni and S.K. Gupta (Molecular Model for Solid State Polymerisation of Nylon 6.II. An improved model - Journal of Applied Polymer Science Vol. 53, 85-103 (1994)). On pages 95 and 96 (is indicated and reported in a graph) the negative effect on the polycondensation kinetics (number average chain length) of the surface concentration of water for concentration values higher than 0.001 mol/kg number average chain length. In particular, it results that the polymer reactivity is reduced and that the effect is evident for residence times higher than 6 hours. For this reason it is necessary to reduce the water concentration in the vapour phase surrounding the solid phase by increasing the inert gas stream and/or reducing the vacuum level at which the polycondensation reaction is carried out. It results that by using a water concentration of 0.01 mol/kg there is a reactivity reduction of about 15%. It has been unexpectedly found and this is contrary to the expectations, that it is possible to conduct the SSP reaction without that the kinetic of the polycondensation reaction decreases even operating with an inert gas flow in the SSP reactor, leading to a water concentration in the reactor higher than 0.01 mol/kg of polymer. The R ratio between the capacity/h (throughput/h) by weight of the inert gas fed into the polycondensation reactor and the capacity/h by weight of the polymer at the reactor outlet in the process of the invention is lower than 0.5, preferably comprised between 0.05 and 0.3. The SSP reactor used is a moving bed reactor, wherein the resin enters from the top and comes out from the bottom and the inert gas stream (preferably nitrogen) is circulated in countercurrent or equicurrent. According to a preferred realization, the polymer is at first preheated in an heating equipment, which increases the temperature of the solid to the reaction temperature (comprised between the glass transition temperature and polymer melting temperature) and subsequently fed into the SSP reactor, where the reaction temperature is kept for the time necessary to obtain the desired polymerization degree measured as a relative viscosity value. The reaction temperature is in general comprised between 10°C and 40°C lower than the melting temperature of the polyamide. The inert gas stream coming out from the reactor is subjected, before being recycled into the reactor, to purification and drying processes carried out according to known methods for the removal of the organic impurities therein present and water. The water content in the recycled gas is brought to values lower than 100 ppm and preferably lower than 3 ppm. The organic impurities are kept lower than 10 ppm. The polymer coming out from the polymerization reactor is cooled by using fluid bed equipment or equipment with solid/wall cooling. It is particularly convenient to use a system as described in Applicant's Italian application No. MI96A002158 (EP-A-836921). The average residence times in the reactor are such as to obtain an increase of the polymer relative viscosity of at least 0.3 units. They are in general comprised between 6 and 20 hours. The process is used for polyamide resins with a relative viscosity lower than 3.3, in general lower than 2.2 and in particular with a relative viscosity between 2.0 and 2.6. The relative viscosity is measured at 25°C in a 1% by weight resin solution in sulphuric acid concentrated at 96%. The resins are preferably formed of PA6, PA6,6, PA11, PA12 or copolymers or mixtures of the same. The following examples are given to illustrate but not to limit the invention. Example 1 The solid state upgrading was carried out in a continuous reactor with moving bed and with a solid capacity of 40 kg/h. The used material is Nylon 6 with starting relative viscosity of 2.5. A polymer with a final viscosity of 3.3 was produced keeping constant the average temperature of the reactor and changing only the inert gas quantity (nitrogen) (changing therefore the R ratio). The fed nitrogen contained less than 100 ppm water and less than 10 ppm of organic compounds. The average residence time was 18 hours. The obtained results are shown in Table 1. Comparative example 1 The test of example 1 was repeated using a R ratio equal to 5 to reduce to a minimum the water concentration in the gaseous phase (Cw=0.0019 mol/kg). The starting polymer was the same as in example 1 and the reaction temperature and the residence time were kept constant. The relative viscosity of the obtained polymer was of 3.3. Example 2 The solid state upgrading was carried out in a continuous reactor with moving bed wherein a solid capacity of 40 kg/h was fed. The used material is Nylon 6.6 with starting relative viscosity of 2.6. A polymer with a final viscosity of 4.2 was produced, keeping constant the average temperature of the reactor and changing only the inert gas quantity (nitrogen) (changing therefore the R ratio). The fed nitrogen contained less than 100 ppm of water and less than 10 ppm of organic compounds. The used residence time was 16 hours. The obtained results are shown in Table 2. Comparative example 2 The test of example 2 was repeated using a R ratio equal to 5 to reduce to a minimum the water concentration in the gaseous phase. The starting polymer was the same and the reaction temperature and the average residence time were kept constant. The relative viscosity of the obtained polymer was of 4.2. Test No. 1 2 3 4 5 Nitrogen quantity (kg/h) 2 4 8 12 20 R ratio 0.05 0.1 0.2 0.3 0.5 Average Temp. (°C) 176 176 176 176 176 Final relative viscosity 3.32 3.32 3.32 3.32 3.32 Cw (mol/kg) 0.748 0.374 0.191 0.128 0.079 Cw = water concentration Test No. 6 7 8 9 10 Nitrogen quantity (kg/h) 2 4 8 12 20 R ratio 0.05 0.1 0.2 0.3 0.5 Average Temp. (°C) 196 196 196 196 196 Final relative viscosity 4.21 4.20 4.21 4.20 4.20

Claims: Process for the solid state polycondensation of polyamide resins, wherein the resin is fed into a moving bed reactor heated at a temperature higher than the glass transition temperature of the resin and from 10° to 40°C lower than the resin melting point, and an inert gas is circulated countercurrent or equicurrent with the resin, characterized by the fact that the ratio R by weight between the gas throughput/h and the polymer throughput/h discharged from the reactor is comprised from 0.05 to a value lower than 0.5. Process according to claim 1, wherein the ratio R is comprised between 0.05 and 0.30. Process according to claims 1 and 2, wherein the treated polyamide is selected from the group consisting of Nylon 6, Nylon 6,6 and Nylon 12 and copolymers and/or mixtures of the same. Process according to claim 1, 2 or 3, wherein the inert gas is nitrogen. Process according to the previous claims, wherein the nitrogen coming from the polycondensation reactor is recycled into the reactor after having been submitted to a purification process, wherein the water is reduced to values lower than 3 ppm. Process according to any of previous claims, wherein the relative viscosity of the resin fed to the moving bed is lower than 3.3, the relative viscosity being measured at 25°C in 1% by weight resin solution in sulphuric acid concentrated at 96%. Process according to the previous claims, wherein the temperature of the resin in the polycondensation reactor is from 10°C to 40°C lower than the resin melting point and the residence time is such to obtain an increase of the relative viscosity of at least 0.3 units.

Inventors: BIANCHI RICCARDO, GIORDANO DARIO, BIANCHI, RICCARDO, GIORDANO, DARIO
Applicants: UOP SINCO S R L, UOP SINCO S.R.L.
Application year: 1997
Main classification: C08G69
IPC codes: C08G69