Heterostructure laser

Abstract: The specification describes a heterostructure laser utilizing GaAs based materials that emits at 0.98 µm and is thus suitable for pumping an erbium doped fiber waveguide amplifier. The composition and asymmetrical structure of the cladding layers of the laser is designed to give exceptional electrical and optical confinement without the high levels of aluminum that are found to reduce the lifetime of high performing prior art devices.

Description: FIELD OF THE INVENTION The invention relates to laser heterostructure diodes and to erbium amplifier devices pumped with the newly developed laser diodes. BACKGROUND OF THE INVENTION The effectiveness of lightwave communication systems increased dramatically with the discovery of the erbium doped amplifier, a true light amplifier. The erbium amplifier structure is remarkably simple, the primary element being a length of erbium doped fiber. However, widespread application of this device awaited the development of an effective optical pump, which proved somewhat more challenging than the erbium-doped amplifier itself. Erbium doped silica glass absorbs most efficiently at 0.98 µm, but at the time of the discovery of the erbium amplifier, no practical laser existed that could effectively pump the 0.98 µm absorption band. A suitable laser was later developed, which was a ternary GaInAs quantum well structure using GaAs waveguide layers and AlGaAs cladding layers. It was found that layers with high aluminum content were effective for light confinement due to the high refractive index variation induced by the aluminum. However, large amounts of aluminum are necessary to obtain this effect, and it has now been realized that the presence of aluminum in these structures produces operational problems. Aluminum is reactive and tends to oxidize in these structures if not carefully protected. Moreover, GaAs with high aluminum content is mechanically rigid, which makes the ternary material susceptible to dark line defect propagation. Both of these effects contribute to a reduction in operating lifetime, particularly when driven to high output powers. An alternative diode structure without aluminum was developed based on GaInP as the cladding material. This alternative material does not oxidize like the aluminum ternary, and is not as susceptible to dark line defect propagation. However, these enhancements are offset by a reduction in electrical and optical confinement. The refractive index difference between this material and the GaAs waveguide layer is less than with the aluminum-containing material, thus optical confinement is less efficient, and a smaller conduction band offset results in less effective electrical confinement. Simply reducing the aluminum content of the cladding layer would at first appear to be a third option. However, this expedient by itself substantially reduces electrical confinement. Likewise, making the aluminum layer very thin reduces the total aluminum content of the structure but results in inadequate optical confinement. More information on prior art efforts to produce lasers emitting at 0.98µm is given by M. Shimuzu, et al, "Erbium-Doped Fiber Amplifiers with an Extremely high Gain Coefficient of 11.0 dB/mW", Electronic Letters, Vol. 26, No. 20, September 1990, pp 1641-1643. Typical prior art clad heterostructure lasers are symmetric, i.e. have the same cladding structures on both the p-side and the n-side of the structure. See, e.g., Yoshida et al., AlGalnP/GalnAs Strained Quantum Well Lasers, Electronics Letters, Vol. 29, No. 8, 15 April 1993, pp. 664-665. We have found symmetric cladding to be an unnecessary restraint. STATEMENT OF THE INVENTION We have developed a laser operating at 0.98µm that realizes the electrical and optical advantages of the aluminum containing heterostructure, but which largely avoids the drawbacks associated with high aluminum content. The inventive laser is defined by the features of claim 1. It obtains the positive attributes of each of the structures previously described by using a dual cladding layer. The dual cladding layers for the n and p sides are different, and produce asymmetric profiles for both refractive index and bandgap. The p-side dual cladding layer comprises a first AlGaInP layer proximate to the waveguide layer, and a second cladding layer of GaInP. The AlGaInP layer has a lower level of aluminum than the typical cladding structure of the prior art. The n cladding dual layer comprises a first layer of AlInP, and a second layer of GaInP. This asymmetric dual cladding layer structure has a bandgap differential that is larger, on both the n and p sides of the junction, than the bandgap of both of the heterostructures discussed earlier. As a consequence the carrier confinement of this structure is also superior to that of the prior art structures. The refractive index differential is also larger, giving superior optical confinement. Although potentially useful for a variety of applications the improved heterostructure laser was developed for pumping erbium doped fiber amplifiers, and the combination of the heterostructure laser with a suitable erbium doped fiber waveguide, with signal input and output means, forms an additional embodiment of the invention. Erbium doped fiber amplifiers can be pumped at either 1.480µm or .98µm . Pump lasers emitting at 1.480µm are considered to be reliable but those operating at .98µm require less injection current and less cooling, thereby reducing electrical power requirements. If pump lasers emitting at .98µm can be made with reliable performance and suitable lifetimes they become the logical choice. This invention is aimed at satisfying that goal. BRIEF DESCRIPTION OF THE DRAWING Figure 1 is a dual plot of refractive index and energy level along a dual abscissa, and the distance d, as measured through the thickness of the multi-level structure, is plotted along the right hand ordinate; Figure 2 is a plot similar to that of Figure 1 for an alternative multi-level structure; Figure 3 is a plot of conduction band and valence band offsets vs. composition for GaInP heterostructures with, and without, aluminum; Figure 4 is a plot similar to that of Figures 1 and 2 showing the electron and optical confinement in a heterostructure with a composition according to the invention. Figure 5 is a schematic view of an erbium-doped amplifier in which the pumping means comprises the heterostructure laser described in conjunction with Figures 1-4, and Figure 6 is a power curve for a diode with the heterostructure shown in Figure 4. DETAILED DESCRIPTION The electrical and optical confinement characteristics of the high aluminum content heterostructure are shown in Figure 1. The laser structure, with waveguide and cladding layers, is represented as distance d along the right side ordinate of the plot. Distance d is taken through the thickness of the multilayer structure. The active laser region comprises a quantum well structure of Ga 0.8 In 0.2 As bounded by GaAs waveguide layers. The composition and characteristics of the active laser region are well known in the art. We have demonstrated our invention using a GaInAs quantum well structure but it is known, for example, that phosphorus can be substituted for arsenic in part to produce a laser emitting at 0.98µm . In this description we have not attempted to include the many possible permutations, such as multi-quantum wells, superlattices and graded bandgap regions, that are common in this kind of laser diode structure. Most of the laser diodes relevant to this invention are GaAs based materials and it is to be understood that reference to a GaAs based active region is sufficient to convey the intended meaning to one skilled in the art. Referring again to Figure 1, the relevant optical and electrical properties for confinement, i.e. the refractive index and the energy band, are plotted along the dual abscissa as shown. The refractive index is measured at 0.98µm . The bandgap is expressed in electron volts (eV) under zero field condition. The characteristic bandgap of each of the layers is indicated. With this dual plot, the profiles of the relevant properties in the multilevel structure are apparent on inspection. The step height between the active laser region and the confinement layers indicates the effectiveness of the electrical and optical confinement. As is evident, the confinement characteristics of the heterostructure with AlGaAs cladding layers are good. However as indicated earlier this heterostructure has undesirable aging characteristics. The heterostructure without aluminum, i.e. with GaInP cladding layers, is represented in Figure 2. The reduction in both electrical and optical containment, when compared with Figure 1, is apparent. Thus while the effective lifetime should be higher, diodes with this structure have lower efficiencies. State of the art 0.98µm laser diodes with AlGaAs as confining layer material have a power slope efficiency of the order of 1 W/A, while diodes with GaInP confining regions have a power slope efficiency typically of 0.8 W/A. The lower efficiency requires higher drive currents in the GaInP device to achieve equivalent power. Higher drive currents raise the operating temperature of the device which accelerates aging and cancels the otherwise improved device lifetime. Figure 3 plots experimentally determined conduction and valence band discontinuities. The conduction band offsets (ΔE c ) and valence band offsets (ΔE v ) , at 5 K, are plotted vs. barrier composition (y) for heterojunction system: Ga 0.52 In 0.48 P/(Al y Ga 1-y ) 0.52 In 0.48 P Closed circles indicate E Γ , dashed line indicates E x . For more technical details see S.P. Najda et al, J. Appl. Phys., 77, p. 3412 (1995). The relevant aspects in Figure 3 are that the valence band discontinuity continues to grow monotonically with increasing Al mole fraction, while the conduction band offset reaches a maximum near 50% Al. Therefore, even though the refractive index step between the two materials will continue to grow (which is desirable), no further improvements in electron confinement will be realized if the Al concentration exceeds this value. In fact, electrical confinement decreases when aluminum content exceeds ∼50%. Further, an electron blocking layer would be p-type, and low resistivity p-type (Al x Ga 1-x ) 0.51 In 0.49 P where Al>75% is difficult to produce. The additional heating (I 2 R) losses would have a deleterious effect on device lifetime. Based on an understanding of these principles we have developed a new heterostructure that provides both the superior lifetime performance of the structure of Figure 2 and the superior confinement characteristics of the structure of Figure 1. This new heterostructure has confinement layers with different compositions on the n-and p- sides and are slightly asymmetric in their confinement characteristics. The confinement or cladding layers have the following nominal formulas: p-side: (Al 0.5 Ga 0.5 ) 0.51 In 0.49 P Ga 0.51 In 0.49 P n-side: Al 0.51 In 0.49 P Ga 0.51 In 0.49 P The electrical and optical confinement profiles for this structure are shown in Figure 4. As will be appreciated, the bandgap differential between the GaAs waveguide layer and the first cladding layer is 0.926 eV on the n-side and 0.776 eV on the p-side, which values compare well with the differential of 0.656 eV in the structure of Figure 1. Ranges of values for the thickness of the layers in the structure of Figure 4 can be prescribed in the context of preferred embodiments. The thickness of the contact layer is non-critical and is typically 0.05 to 1 micron. The ternary (outside) cladding layers, which are aluminum free, are relatively thick, i.e. 0.5 to 2.0 microns. The interior cladding layers, which contain modest amounts of aluminum, are thin, e.g. 1000 Angstroms. The thickness may vary however, typically from 100 to 2000 Angstroms. The waveguide layers are typically 1000-1500 Angstroms thick but could vary from 500 to 3000 Angstroms. The quantum well layer is typically very thin, i.e. 50 to 150 Angstroms. The smaller thickness requires more indium, the larger thickness less indium. As indicated earlier there are many alternatives for the active region and these form no part of the invention. The heterostructure laser just described is ideally suited as a pump for an erbium doped fiber amplifier (EDFA). Such devices are now well known in the art and are described for example by Zyskind et al, "Erbium-Doped Fiber Amplifiers and the Next Generation of Lightwave Systems, AT&T Technical Journal, pp. 53-62, Jan/Feb 1992. The fiber amplifier operates at a signal wavelength of 1550 nm with high gain, high output power and low noise. The erbium fiber is typically a short length of optical fiber with a core doped at less than 0.1 percent erbium, e.g 500 ppm. The erbium doped fiber is advantageously made by modified chemical vapor deposition techniques that are known in the art. Additional information on the erbium fiber characteristics may be found in P. Urquhart, "Review of Rare Earth Doped Fiber Lasers and Amplifiers", IEEE Proceedings, Vol. 135, Part J, No.6, December 1988, pp 385-405. A typical EDFA device structure is shown in schematic form in Figure 5. The heterostructure laser pump is shown at 51, coupled to a wavelength division multiplexer 52. The signal to be amplified, represented by input 55, is combined with the pump energy through multiplexer 52. The dashed arrows represents the pump light and the solid arrows represent the signal. The combined pump and signal beams are connected to erbium amplifier 53 through fusion splices 59. As pump light propagates along the erbium doped portion 53 of the fiber it becomes depleted as pump energy is absorbed by erbium ions being raised to an excited state. As the signal propagates through the region occupied by excited erbium ions it stimulates emission of energy from the excited ions and thus becomes amplified. The amplified signal is processed through optical isolator 57 to prevent unwanted feedback, and the remaining pump energy is filtered by optical filter 58. The amplified output is represented by 54. A power curve for a diode represented by the composition of Figure 4 is shown in Figure 6. The power in mW is plotted vs. diode current in mA. The threshold current is 250 mA, the current density is 588 A/cm2, and the power slope is 0.73 W/A. The power slope for this device is considered below the theoretical value and the optimum is believed to be comparable to the best power slopes obtainable with high aluminum devices. Various additional modifications of the invention will occur to those skilled in the art. For example, the ternary and quaternary compositions of the embodiments described herein are essentially non-stoichiometric, and the mole fractions indicated are preferred values only. Modest departures from these fractions can be made while still retaining the properties necessary to carry out the invention. Generalized formulas for the compositions of the layers of the device represented by Figure 4 are: outside cladding layers: Ga x In 1-x P p type inside cladding layer: (Al y Ga 1-y ) z In 1-z P n type inside cladding layer: Al a In 1-a P quantum well: Ga b In 1-b As where x has a value in the range 0.48-0.54, y has a value in the range 0.40-0.60, z has a value in the range 0.48-0.54, a has a value in the range 0.48-0.60, and b has a value in the range 0.15 to 1.0. It should be evident that the outside cladding layers may have different compositions within the general formula and therefore "x" can be designated as x or x' in the respective layers.

Claims: A heterostructure laser diode comprising a layered structure with the following layers in sequence: a) substrate: GaAs b) first cladding layer: n-type Ga x In 1-x P, where x has a value in the range 0.48-0.54, c) second cladding layer: n-type Al a In 1-a P, where a has a value in the range 0.48-0.60, d) first waveguide layer, e) active layer, f) second waveguide layer, g) third cladding layer: p-type (Al y Ga 1-y ) z In 1-z P, where y has a value in the range 0.40-0.60, and z has a value in the range 0.48-0.54, h) fourth cladding layer: p-type Ga x' In 1-x' P, where x' has a value in the range 0.48-0.54, i) contact layer. The heterostructure laser of claim 1 wherein x, a, and z have a value of approximately 0.51, and y has a value of approximately 0.5. Fiber waveguide amplifier comprising: a) an erbium doped fiber waveguide (53), b) signal input means (55) for injecting a signal to be amplified into the erbium doped fiber waveguide, and c) pump means (51) for pumping 0.98 µm laser radiation into the erbium doped fiber waveguide, said pump means comprising the heterostructure laser of claim 1 or claim 2.

Inventors: BAILLARGEON JAMES NELSON, CHENG KEH-YUNG, YI CHO ALFRED, BAILLARGEON, JAMES NELSON, CHENG, KEH-YUNG, YI CHO, ALFRED
Applicants: AT & T CORP, AT&T CORP.
Application year: 1997
Main classification: H01S5
IPC codes: H01S5, H01S3