Catalyst composition for transalkylation of alkylaromatic hydrocarbons and process for production of xylene

Abstract: A catalyst composition for transalkylation of alkylaromatic hydrocarbons which exhibits a percentage conversion of ethyltoluene higher than 50 wt%, is composed of mordenite (100 pbw), inorganic oxide and/or clay (25-150 pbw), and at least one metal component selected from rhenium, platinum and nickel, and contains mordenite such that the maximum diameter of secondary particles of mordenite is preferably smaller than 10 µm. In a process for producing xylene from alkylaromatic hydrocarbon feedstock containing C 9 alkylaromatic hydrocarbons containing more than 5 wt% ethyltoluene and less than 0.5 wt% naphthalene, the feedstock is brought into contact with the catalyst in the presence of hydrogen.

Description: The present invention relates to a catalyst composition for transalkylation of alkylaromatic hydrocarbons and to a process for production of xylene. More particularly, the present invention relates to a catalyst composition for production of xylene from a feedstock containing C 9 alkylaromatic hydrocarbons by transalkylation and to a process for production of xylene. Transalkylation of alkylaromatic hydrocarbons is one of the industrially important reactions which is applied to the production of benzene and xylene from toluene by disproportionation and the production of xylene from toluene and methylbenzene by transalkylation. There have been proposed a number of catalyst systems for this reaction. Among them are crystalline aluminosilicate zeolites (such as faujasite and mordenite) which are known as effective catalysts. Mordenite is particularly active in transalkylation of alkylaromatic hydrocarbons. GB-A-1304961 and EP-A-0731071 disclose processes for producing xylenes from a mixture containing C 9 hydrocarbon(s) and toluene, using catalysts derived from mordenite. Mordenite used alone is not satisfactory in activity and catalyst life; therefore, it is used in combination with a metal from Group VIB (such as chromium, molybdenum and tungsten) or a metal from Group VIII (such as iron, cobalt, nickel, and platinum metal), as disclosed in US-A-3729521. In addition, there is disclosed a catalyst which substantially consists only of mordenite and rhenium, in JP-B-62-045849. These catalysts, however, are not wholly effective for transalkylation in production of xylene from C 9 alkylaromatic hydrocarbons (including ethyltoluene). Incidentally, J. Das et al . reported transalkylation of feedstocks containing C 9 alkylaromatic hydrocarbons by β-zeolite (Catalysis Letters, vol. 23 (1994), p. 161-168). In practice, this process does not provide satisfactory xylene yields. Practically, there exists no efficient way of producing xylene from C 9 alkylaromatic hydrocarbons containing ethyltoluene. The present invention addresses the problem of providing a catalyst composition for efficient production of xylene from a feedstock containing C 9 alkylaromatic hydrocarbons by dealkylation and transalkylation. Another problem addressed by the invention is the provision of a process for producing xylene. C 9 alkylaromatic hydrocarbons are of low industrial value and are usually consumed as fuel. We paid attention to ethyltoluene and trimethylbenzene contained in C 9 alkylaromatic hydrocarbons, because ethyltoluene can be converted into toluene by dealkylation and two moles of toluene or toluene and trimethylbenzere can be converted into xylene (which is industrially useful) by transalkylation. There has been no way of efficient dealkylation of ethyltoluene into toluene, which leads to low yields of xylene. The catalyst composition of the present invention is capable of efficient dealkylation of ethyltoluene into toluene and efficient production of xylene by transalkylation. We have found surprisingly that, for the first time, it is possible to achieve an efficient conversion of ethyltoluene, especially a conversion allowing the production of xylene from ethyltoluene present in C 9 alkylaromatic hydrocarbons by their dealkylation to form toluene or toluene and trimethylbenzene and subsequent transalkylation of the toluene or toluene and trimethylbenzene. Thus, embodiments of the present invention provide a catalyst composition for transalkylation of alkylaromatic hydrocarbons, which composition may achieve a percent conversion of ethyltoluene higher than 50wt% under the following conditions: Feedstock Composition: Ratio of ethyltoluene to (trimethylbenzene plus ethyltoluene) = 35 wt% Reaction conditions: Temperature: 400°C Pressure: 3 MPa-G WHSV (weight space velocity) 2.5 h -1 Ratio of H 2 to feedstock: 4.0 mol/mol Percent conversion of ethyltoluene (wt%) = (A - B)/A x 100 where A: concentration of ethyltoluene in feedstock (wt%) B: concentration of ethyltoluene after reaction (wt%) A catalyst which achieves the percent conversion of ethyltoluene higher than 50 wt%, preferably higher than 80 wt%, in the above-mentioned reaction is useful in the present invention. Moreover, we have found that such surprisingly high efficiency can be achieved using a particular catalyst composition as defined below. Thus, according to a first aspect the invention provides a catalyst composition comprising (A) H-type mordenite, wherein the mordenite in the formed catalyst has a maximum diameter of secondary particles thereof smaller than 10 µm, (B) at least one inorganic oxide and/or clay being present in an amount, per 100 pbw of mordenite (component A), of 25-150 pbw and (C) a component providing rhenium, being present in an amount, per 100 pbw of mordenite (component A), of at least 0.05 pbw. According to a second aspect, the invention provides a process for producing xylene wherein a catalyst according to the above aspect of the invention is brought into contact with a feedstock of alkylaromatic hydrocarbons containing C 9 alkylaromatic hydrocarbons, which C 9 alkylaromatic hydrocarbons may contain at least 5% by weight thereof of ethyltoluene, in the presence of hydrogen, to achieve dealkylation to convert ethyltoluene in the C 9 alkylaromatic hydrocarbons into toluene, and subsequent transalkylation to convert toluene or toluene and trimethylbenzene into xylene. According to embodiments of the process, the alkylaromatic hydrocarbon as the feedstock contains less than 0.5 wt%, and possibly less than 0.3 wt%, naphthalene. Preferred embodiments of the invention, in accordance with any of the above aspects thereof, will now be described. As indicated above, a high percentage conversion of ethyltoluene and high yields of xylene by transalkylation are achievable using a catalyst composed of hydrogen-type mordenite, inorganic oxide and/or clay, and at least one metal namely rhenium in an adequate ratio. In more detail, ethyltoluene converts into toluene and ethylene upon dealkylation by hydrogen-type mordenite. In known procedures, the percentage conversion of ethyltoluene is not sufficiently high due to restrictions caused by thermodynamic equilibrium. These restrictions are eliminated if the catalyst is incorporated with an inorganic oxide and/or clay which densely supports at least one metal component which provides rhenium. This catalyst causes hydrogen present in the reaction system to hydrogenize ethylene (formed by dealkylation of ethyltoluene) into ethane. The result is a high percent conversion. The improved yield of xylene is due to transalkylation of toluene or toluene and trimethylbenzene. The metal component supported by the inorganic oxide and/or clay is responsible for hydrogenolysis of high boiling by-products. This suppresses the catalyst coking and deactivation and prolongs the catalyst life. These effects are produced only when requirements for an adequate composition are satisfied as mentioned above. The zeolite used in the present invention is hydrogen-type mordenite. A more preferred mordenite is one in which the silica/alumina molar ratio is from 15 to 30. This mordenite may be obtained from a mordenite having a low silica/alumina molar ratio by acid extraction to eliminate aluminium or by direct synthesis. Directly synthesized mordenite is preferable. Synthesis of mordenite is disclosed in American Mineralogist, (1972), 57, 1146-1151 and JP-B-60-051969 and JP-B-02-031006. Conversion into hydrogen-type mordenite may be accomplished by direct ion exchange of mordenite (containing metal cations) with an acid or by ion exchange in an aqueous solution containing ammonium ions, for conversion into ammonium type, followed by drying and calcination. Conversion from ammonium type into hydrogen type is preferable. The ion exchange may be carried out before or after formation of the zeolite, with the latter method being industrially desirable. For improvement of catalytic performance, mordenite may optionally be treated with an organic acid containing carboxyl groups (such as lactic acid, malic acid, tartaric acid and citric acid). An especially preferred mordenite from which an H-type mordenite may be obtained is that having the X-ray diffraction pattern shown in Fig. 1, referred to hereinafter. The inorganic oxide and/or clay may serve as a support for at least one component providing rhenium. The inorganic oxide may be at least one of alumina, silica, titania and magnesia, and where more than one metal oxide is present, these may be present either in a co-structure, such as a co-crystal, cosol or cogel, a preferred such co-structure being silica-alumina, and/or in admixture. A more preferred metal oxide is alumina. Alumina includes boehmite, boehmite gel, gibbsite, bialite, nordstrandite, diaspore, and amorphous alumina gel, with boehmite being preferable. Alumina of γ-, η-, and δ-modifications (that occur under different calcination conditions) may be used. Alumina sol or alumina gel may be used as a binder to form the catalyst and may also function as a support for the metal component which provides rhenium. The clay may be natural or synthetic and may be purified. Examples are montmorillonite, kaolin, sepiolite and acid clay. The amount of the inorganic oxide and/or clay in the catalyst is 25-150 pbw, more preferably 40-150 pbw, for 100 pbw of mordenite. Larger amounts than specified (with decreased amounts of mordenite) may lead to low dealkylation and transalkylation activities Smaller amounts than specified may lead to short catalyst life and low ethyltoluene conversion and low xylene yields due to poor dispersion of metal components and hence poor hydrogenation of ethylene resulting from dealkylation of ethyltoluene. It is essential in the present invention that the catalyst contain as the metal component at least one member which provides rhenium. The metal may be present in the composition in any form but a preferred metal component providing the metal is a compound containing the metal. Thus, rhenium may be present in any form, such as the oxide, sulfide or selenide thereof. The amount of rhenium may be 0.05-1.5 pbw (as metal) for 100 pbw of mordenite and 0.1-2.0 pbw (as metal) for 100 pbw of inorganic oxide and/or clay. A catalyst with an excessively small amount of rhenium is poor in conversion of ethyltoluene. Conversely, a catalyst with an excessively large amount of rhenium causes excessive hydrogenolysis of alkylaromatic hydrocarbons. Preferred rhenium compounds include perrhenic acid and ammonium perrhenate. For these metal components to be supported, the mordenite is uniformly mixed with the inorganic oxide and/or clay, followed by forming, drying, and calcination, and the mordenite is converted into hydrogen type or ammonium type and finally impregnated with an aqueous solution containing at least one metal component of rhenium. The resulting product is dried and calcined. Calcination changes the mordenite of ammonium type into the mordenite of hydrogen type. Calcination is preferably carried out in an oxygen-containing atmosphere at 300-650°C. Our investigation into the dealkylation of ethyltoluene into toluene, which is intended to produce xylene from ethyltoluene contained in C 9 alkylaromatic hydrocarbons by dealkylation and subsequent transalkylation of toluene or toluene and trimethyltoluene, revealed that secondary particles of mordenite in the formed catalyst may play an important role. Secondary particles result from primary particles by aggregation. The diameter of secondary particles can be easily examined by means of a scanning electron microscope (SEM). For highest efficiency, the maximum diameter of secondary particles of mordenite is smaller than 10 µm, more preferably smaller than 5 µm. Secondary particles will be partly broken and dispersed during the mixing and forming of the mordenite with the inorganic oxide and/or clay. Secondary particles of mordenite in the formed catalyst should be sufficiently small and well dispersed so that they readily interact with the metal component in the catalyst for a high percent conversion of ethyltoluene. The diameter of secondary particles of mordenite in the formed catalyst depends on the conditions under which the catalyst is formed and the diameter of secondary particles in raw material mordenite. It also varies depending on the kneading time and water content, and it becomes smaller according as the kneading time increases. The diameter of secondary particles in raw material mordenite powder depends on the mixing ratio of reactants, the time for crystallization, and the method of stirring and drying. It tends to become smaller according as the reaction mixture decreases in alkalinity and the time for crystallization also decreases. Thus, we have now found surprisingly that, in accordance with the invention, it is possible to produce xylene efficiently from a feedstock containing C 9 alkylaromatic hydrocarbons such as ethyltoluene, trimethylbenzene and propylbenzene, which are of low industrial value and mainly consumed as fuel, by dealkylation of ethyltoluene into toluene and transalkylation of toluene or toluene and trimethylbenzene into xylene. The percent conversion of ethyltoluene is higher than 50 wt%, preferably higher than 80 wt%. For high xylene yields, it is important that the C 9 alkylaromatic hydrocarbons contain ethyltoluene in an amount more than 5 wt%, preferably more than 10 wt%. The C 9 alkylaromatic hydrocarbons may contain C 10 compounds such as diethylbenzene, ethylxylene and tetramethylbenzene. Using a mixture of toluene and C 9 alkylaromatic hydrocarbons as a feedstock is embraced in the embodiments of the present invention. In this case, the mixing ratio of toluene and C 9 alklyaromatic hydrocarbons is preferably in the range of 0:1 to 1:1 (by weight). The feedstock may contain, in addition to the above-mentioned aromatic hydrocarbons, non-aromatic hydrocarbons such as paraffin and naphthene. The catalyst pertaining to the present invention is used for the production of xylene, as mentioned above. It is essential that hydrogen be present in the reaction system for the production of xylene. The amount of hydrogen to be supplied is preferably such that the molar ratio of hydrogen to alkylaromatic hydrocarbons is in the range of 1 to 10. The reaction is preferably carried out at a pressure of 1-6 MPa, at a temperature of 300-550°C, and at a WHSV (weight space velocity) of 0.5-10 h -1 . Our investigation revealed that trace constituents such as naphthalene present in the feedstock (C 9 alkylaromatic hydrocarbons) may lower the catalytic activity and reduce the xylene yields. The content of naphthalene in C 9 alkylaromatic hydrocarbons is typically about 1 wt%, although it varies depending on tie sources. Therefore, it is important that, when such trace constituents are present, alkylaromatic hydrocarbons (as feedstock) be distilled under normal pressure or reduced pressure prior to transalkylation to reduce the content of naphthalene below 0.5 wt%, preferably 0.3 wt%. Preferred embodiments of the invention will now be described in more detail with reference to the following Examples, which in turn refer to the accompanying drawings, in which: Fig. 1 is an X-ray diffraction pattern of the mordenite-type zeolite prepared in the Synthesis Example; and Fig. 2 shows SEM photographs of catalysts B, R and T prepared in respective Examples 1, 9 and comparative Example 5. Synthesis Example - Preparation of mordenite-type zeolite: An aqueous solution was prepared by dissolving in 586.8 g of water 21.3 g of solid sodium hydroxide (containing 96.0 wt% NaOH and 4.0 wt% H 2 O, from Katayama Kagaku) and 21.3 g of tartaric acid powder (containing 99.7 wt% tartaric acid and 0.3 wt% H 2 O, from Katayama Kagaku). To this aqueous solution was added 29.2 g of sodium aluminate solution (containing 18.5 wt% Al 2 O 3 , 26.1 wt% NaOH, and 55.4 wt% H 2 O, from Sumitomo Chemical). To the resulting uniform solution was slowly added with stirring 111.5 g of silicic acid powder (containing 91.6 wt% SiO 2 , 0.33 wt% Al 2 O 3 , 0.27 wt% NaOH, "Nipseal VN-3" from Nippon Silica). There was obtained a uniform aqueous slurry having the following composition (in molar ratio). SiO 2 /Al 2 O 3 30 H 2 O/SiO 2 20 OH - /SiO 2 0.25 A/Al 2 O 3 2.5 A : tartrate The slurry was heated at 160°C for 72 hours with stirring (250 rpm) in a 1-liter autoclave. The reaction product was washed with distilled water and filtered five times and then dried overnight at about 120°C. Thus there was obtained a mordenite-type zeolite which has the composition of 1.02Na 2 O·Al 2 O 3 ·18.6SiO 2 and gives an X-ray diffraction pattern shown in Fig.1. Formulation Example - Preparation of Catalyst A paste mixture was prepared from 74.6 g of the mordenite powder prepared as mentioned above (containing 93.8 wt% mordenite), 39.5 g of alumina powder of boehmite structure (α-alumina monohydrate) (containing 76.1 wt% Al 2 O 3 , SCF type, from Condia), 80 g of alumina sol (containing 10 wt% Al 2 O 3 , "Colloidal Alumina 200", from Nissan Kagaku), 10 g of alumina gel powder (containing 70 wt% Al 2 O 3 , "Cataloid AP (C-10)", from Shokubai Kasei), and 10 g of distilled water. After kneading for about 1 hour, the paste was formed into pellets 1.2 mm in diameter and 1.0 mm long), which were dried overnight at 120°C. The dried pellets, equivalent to 90 g (dry base), were calcined in air at 400°C for 2 hours. On cooling in a desiccator, there was obtained the desired formed catalyst A. Example 1 The formed catalyst A (15 g dry base) was treated with 30 ml of 10 wt% aqueous solution of ammonium chloride at 80-85°C for 1 hour. The treating solution was discarded and treatment was repeated with a fresh solution four times in the same manner as above. The treatment was followed by rinsing with distilled water five times. The formed catalyst A was further treated with 30 ml of 5 wt% aqueous solution of tartaric acid at 80-85°C for 4 hours. The treating solution was discarded and the treatment was followed by rinsing with distilled water five times. For impregnation with rhenium, the formed catalyst A was immersed in 21 g of water containing 0.039 g of rhenium (VII) oxide (Re 2 O 7 ) dissolved therein for 4 hours. After removal of the treating solution by filtration, the formed catalyst A was dried overnight at 120°C and then calcined in air at 540°C for 2 hours. Thus there was obtained the catalyst B, which contains 66.5 pbw of alumina and 0.152 pbw of rhenium (equivalent to 0.228 pbw for 100 pbw of alumina) for 100 pbw of mordenite (dry base). Example 2 The catalyst B, was evaluated by conversion of a feedstock (composed of ethyltoluene and trimethylbenzene in a ratio specified below) into xylene under the following conditions in a fixed bed flow reactor. The results are shown in Table 1. Composition of feedstock: Ratio of ethyltoluene to (ethyltoluene plus trimethylbenzene) = 35 wt% Reaction conditions: Temperature 400°C Pressure 3 MPa-G WHSV 2.5 h -1 H 2 /feedstock 4.0 mol/mol Destination of catalyst Metal content (pbw) per 100 pbw of mordenite Conversion (wt%) of ethyltoluene Xylene yields (g) per 100g of feedstock Catalyst B Re 0.152 95.5 31.6 It is noted from Table 1 that the catalyst of the present invention exhibits the high activity of dealkylation and transalkylation and realizes the high yields of xylene. Example 3 The same procedure as in Example 1 was repeated to give the catalyst E except that the amount of rhenium (VII) oxide was changed to 0.078 g. The catalyst E contains 66.5 pbw of alumina and 0.267 pbw of rhenium (equivalent to 0.401 pbw for 100 pbw of alumina) for 100 pbw of mordenite (dry base). Example 4 The same procedure as in Example 1 was repeated to give the catalyst F except that the amount of rhenium (VII) oxide was changed to 0.24 g. The catalyst F contains 66.6 pbw of alumina and 0.686 pbw of rhenium (equivalent to 1.03 pbw for 100 pbw of alumina) for 100 pbw of mordenite (dry base). Comparative Example 1 The same procedure as in Example 1 was repeated to give the catalyst G except that the treatment with rhenium (VII) oxide was omitted. The catalyst G contains 66.4 pbw of alumina for 100 pbw of mordenite (dry base). Comparative Example 2 The same procedure as in Example 1 was repeated to give the catalyst H except that the amount of rhenium (VII) oxide was changed to 0.0059 g. The catalyst H contains 66.5 pbw of alumina and 0.042 pbw of rhenium (equivalent to 0.063 pbw for 100 pbw of alumina) for 100 pbw of mordenite (dry base). Example 5 The same procedure as in Example 1 was repeated to give the catalyst I except that the amount of rhenium (VII) oxide was changed to 0.59 g. The catalyst I contains 66.5 pbw of alumina and 1.77 pbw of rhenium (equivalent to 2.66 pbw for 100 pbw of alumina) for 100 pbw of mordenite (dry base). Example 6 The catalysts B and E to I (varying in rhenium content) were evaluated in the same manner as in Example 2. The results are shown in Table 2. It is noted from Table 2 that the catalysts B, E, F, and I (containing 0.05 pbw of rhenium as metal) exhibit the high activity of dealkylation and transalkylation and realizes the high yield of xylene, whereas the catalyst I is slightly lower in xylene yields than the catalysts B, E, and F (due to decomposition of C 9 alkylaromatic hydrocarbons) despite its high percent conversion of ethyltoluene. It is understood that the preferred rhenium content is 0.05-1.5 pbw (as metal) for 100 pbw of mordenite. The catalysts G and H are poor in conversion of ethyltoluene and low in xylene yields. Destination of catalyst Rhenium content (pbw) per 100 pbw of mordenite Conversion (wt%) of ethyltoluene Xylene yields (g) per 100g of feedstock Catalyst B 0.152 95.5 31.6 Catalyst E 0.267 96.7 31.7 Catalyst F 0.686 98.1 30.7 Catalyst G 0 12.3 9.8 Catalyst H 0.042 48.7 19.0 Catalyst I 1.77 97.8 26.6 Comparative Example 3 A paste mixture was prepared from 106.6 g of the mordenite powder prepared as mentioned above (containing 93.8 wt% mordenite), 80 g of alumina sol (containing 10 wt% Al 2 O 3 , "Colloidal Alumina 200", from Nissan Kagaku), 10 g of alumina gel powder (containing 70 wt% Al 2 O 3 , "Cataloid AP (C-10)", from Shokubai Kasei), and 10 g of distilled water. After kneading for about 1 hour, the paste was formed into pellets (1.2 mm in diameter and 1.0 mm long), which were dried overnight at 120°C. The dried pellets, equivalent to 15 g dry base, were calcined in air at 400°C for 2 hours. On cooling in a desiccator, there was obtained the desired formed catalyst. The formed catalyst (15 g) was treated with 30 ml of 10 wt% aqueous solution of ammonium chloride at 80-85°C for 1 hour. The treating solution was discarded and treatment was repeated with a fresh solution four times in the same manner as above. The treatment was followed by rinsing with distilled water five times. The formed catalyst was further treated with 30 ml of 5 wt% aqueous solution of tartaric acid at 80-85°c for 4 hours. The treating solution was discarded and the treatment was followed by rinsing with distilled water five times. For impregnation with rhenium, the formed catalyst was immersed in 21 g of water containing 0.039 g of rhenium (VII) oxide (Re 2 O 7 ) dissolved therein for 4 hours. After removal of the treating solution by filtration the formed catalyst was dried overnight at 120°C and then calcined in air at 540°C for 2 hours. Thus there was obtained the catalyst J, which contains 15.5 pbw of alumina and 0.067 pbw of rhenium (equivalent to 0.433 pbw for 100 pbw of alumina) for 100 pbw of mordenite (dry base). Comparative Example 4 A paste mixture was prepared from 32.1 g of the mordenite powder prepared as mentioned above (containing 93.8 wt% mordenite), 92.0 g of alumina powder of boehmite structure (α-alumina monohydrate) (containing 76.1 wt% Al 2 O 3 , SCF type, from Condia Co.), 80 g of alumina sol (containing 10 wt% Al 2 O 3 , "Colloidal Alumina 200", from Nissan Kagaku), 10 g of alumina gel powder (containing 70 wt% Al 2 O 3 , "Cataloid AP (C-10)", from Shokubai Kasei), and 10 g of distilled water. After kneading for about 1 hour, the paste was formed into pellets (1.2 mm in diameter and 1.0 mm long), which were dried overnight at 120°C. The dried pellets, equivalent to 15 g dry base, were calcined in air at 400°C for 2 hours. On cooling in a desiccator, there was obtained the desired formed catalyst. The formed catalyst (15 g) was treated with 30 ml of 10 wt% aqueous solution of ammonium chloride at 80-85°C for 1 hour. The treating solution was discarded and treatment was repeated with a fresh solution four times in the same manner as above. The treatment was followed by rinsing with distilled water five times. The formed catalyst was further treated with 30 ml of 5 wt% aqueous solution of tartaric acid at 80-85°C for 4 hours. The treating solution was discarded and the treatment was followed by rinsing with distilled water five times. For impregnation with rhenium, the formed catalyst was immersed in 21 g of water containing 0.039 g of rhenium (VII) oxide (Re 2 O 7 ) dissolved therein for 4 hours. After removal of the treating solution by filtration, the formed catalyst was dried overnight at 120°C and then calcined in air at 540°C for 2 hours. Thus there was obtained the catalyst K, which contains 293.3 pbw of alumina and 0.591 pbw of rhenium (equivalent tc 0.201 pbw for 100 pbw of alumina) for 100 pbw of mordenite (dry base). Example 7 The catalysts B, J, and K (varying in mordenite content and alumina content) were evaluated in the same manner as in Example 2. The results are shown in Table 3. It is noted from Table 3 that the catalyst B (containing 20-150 pbw of alumina for 100 pbw of mordenite) exhibits the high activity of dealkylation and transalkylation and realizes the high xylene yields. Destination of catalyst Alumina content (pbw) per 100 pbw of mordenite Conversion (wt%) of ethyltoluene Xylene yields (g) per 100 g of feedstock Catalyst B 66.5 95.5 31.6 Catalyst J 15.5 47.7 18.4 Catalyst K 293.3 45.9 17.6 Example 8 The catalysts B, H, and J were evaluated in the same manner as in Example 2 to see how the xylene yields change with time. The results are shown in Table 4. It is noted from Table 4 that the catalyst B (containing 20-150 pbw of alumina and at least 0.05 pbw (as metal) of rhenium for 100 pbw of mordenite) exhibits the high activity which lasts for a long period of time Catalyst designation Xylene yields (g) per 100 g of feedstock After 6 hours After 500 hours Catalyst B 31.6 31.2 Catalyst H 19.0 11.8 Catalyst J 18.4 9.9 Example 9 A paste mixture was prepared from 74.6 g of the mordenite powder prepared as mentioned above (containing 93.8 wt% mordenite), 39.5 g of alumina powder of boehmite structure (α-alumina monohydrate) (containing 76.1 wt% Al 2 O 3 , SCF type, from Condia Co.), 80 g of alumina sol (containing 10 wt% Al 2 O 3 , "Colloidal Alumina 200", from Nissan Kagaku), 10 g of alumina gel powder (containing 70 wt% Al 2 O 3 , "Cataloid AP (C-10)", from Shokubai Kasei), and 10 g of distilled water. After kneading for about 5 hours, the paste was formed into pellets (1.2 mm in diameter and 1.0 mm long), which were dried overnight at 120°C. The dried pellets, equivalent to 90 g dry base, were calcined in air at 400°C for 2 hours. On cooling in a desiccator, there was obtained the desired formed catalyst Q. The formed catalyst Q (15 g) was treated with 30 ml of 10 wt% aqueous solution of ammonium chlorice at 80-85°C for 1 hour. The treating solution was discarded and treatment was repeated with a fresh solution four times in the same manner as above. The treatment was followed by rinsing with distilled water five times. Tie formed catalyst Q was further treated with 30 ml of 5 wt% aqueous solution of tartaric acid at 80-85°C for 4 hours. The treating solution was discarded and the treatment was followed by rinsing with distilled water five times. For impregnation with rhenium, the formed catalyst Q was immersed in 21 g of water containing 0.039 g of rhenium (VII) oxide (Re 2 O 7 ) dissolved therein for 4 hours. After removal of the treating solution by filtration, the formed catalyst Q was dried overnight at 120°C and then calcined in air at 540°C for 2 hours. Thus there was obtained the catalyst R, which contains 66.5 pbw of alumina and 0.159 pbw of rhenium (equivalent to 0.239 pbw for 100 pbw of alumina) for 100 pbw of mordenite (dry base). Comparative Example 5 A paste mixture was prepared from 74.6 g of the mordenite powder prepared as mentioned above (containing 93.8 wt% mordenite), 39.5 g of alumina powder of boehmite structure (α-alumina monohydrate) (containing 76.1 wt% Al 2 O 3 , SCF type, from Condia Co.), 80 g of alumina sol (containing 10 wt% Al 2 O 3 , "Colloidal Alumina 200", from Nissan Kagaku), 10 g of alumina gel powder (containing 70 wt% Al 2 O 3 , "Cataloid AP (C-10)", from Shokubai Kasei), and 10 g of distilled water. After kneading for about 20 minutes, the paste was formed into pellets (1.2 mm in diameter and 1.0 mm long), which were dried overnight at 120°C. The dried pellets, equivalent to 90 g dry base, were calcined in air at 400°C for 2 hours. On cooling in a desiccator, there was obtained the desired formed catalyst S. The formed catalyst S (15 g) was treated with 30 ml of 10 wt% aqueous solution of ammonium chloride at 80-85°C for 1 hour. The treating solution was discarded and treatment was repeated with a fresh solution four times in the same manner as above. The treatment was followed by rinsing with distilled water five times. The formed catalyst S was further treated with 30 ml of 5 wt% aqueous solution of tartaric acid at 80-85°C for 4 hours. The treating solution was discarded and the treatment was followed by rinsing with distilled water five times. For impregnation with rhenium, the formed catalyst S was immersed in 21 g of water containing 0.039 g of rhenium (VII) oxide (Re 2 O 7 ) dissolved therein for 4 hours. After removal of the treating solution by filtration, the formed catalyst S was dried overnight at 120°C and then calcined in air at 540°C for 2 hours. Thus there was obtained the catalyst T, which contains 66.4 pbw of alumina and 0.161 pbw of rhenium (equivalent to 0.242 pbw for 100 pbw of alumina) for 100 pbw of mordenite (dry base). Example 10 The catalysts B, R, and T (varying in the duration of kneading) were observed under an SEM to examine the maximum diameter of secondary particles of mordenite in the catalyst. The results are shown in Table 6, and SEM photographs are shown in Fig. 2 to 4. It is noted from Table 6 that the diameter of secondary particles of mordenite in the catalyst decreases according as the duration of kneading increases at the time of catalyst preparation. Destination of catalyst Maximum diameter of secondary particles of mordenite (µm) Conversion (wt%) of ethyltoluene Xylene yields (g) per 100g of feedstock Catalyst B 7 95.5 31.6 Catalyst R 3 96.8 31.8 Catalyst T 20 78.9 25.1 Example 11 The catalysts B, R, and T were evaluated in the same manner as in Example 2 to see how the catalytic performance is affected by the diameter of secondary particles of mordenite in the formed catalyst The results are shown in Table 6. It is noted from Table 6 that the catalyst exhibits the higher activities of dealklylation and transalkylation according as the diameter of secondary particles of mordenite decreases. It is necessary that the maximum diameter of secondary particles be smaller than 10 µm. Example 12 The catalyst B was evaluated in the same manner as in Example 1 using feedstocks varying in the ratio of trimethylbenzene (TMB for short) to ethyltoluene (ET for short). The results are shown in Table 7. It is noted from Table 7 that the xylene yields are high when the feedstocks contain more than 5 wt% ethyltoluene. ET/(TMB+ET) ratio in feedstock (wt%) Xylene yields (g) per 100 g of feedstock 0 18.5 5 20.8 10 23.2 20 37.3 35 31.6 50 31.1 65 27.7 Example 13 The catalyst B was evaluated in the same manner as in Example 2 using feedstocks incorporated with naphthalene to see how the performance of trarsalkylation is affected by naphthalene in C 9 alkylaromatic hydrocarbons. The results are shown in Table 8. It is noted from Table 8 that the xylene yields decrease according as the amount of naphthalene in feedstock increases. It is necessary that the amount of naphthalene in feedstock be less than 0.5 wt%. Amount of naphthalene in feedstock (wt%) Xylene yields (g) per 100g of feedstock 0 31.6 0.10 31.5 0.28 31.2 0.45 30.4 0.98 27.3

Claims: A catalyst composition comprising (A) H-type mordenite, wherein the mordenite in the formed catalyst has a maximum diameter of secondary particles thereof smaller than 10 µm, (B) at least one inorganic oxide and/or clay (component B) being present in an amount, per 100 pbw of mordenite (component A), of 25-150 pbw, and (C) a component providing rhenium, being present in an amount, per 100 pbw of mordenite (component A), of at least 0.05 pbw. A catalyst composition according to claim 1, wherein the mordenite of component A in the formed catalyst has a maximum diameter of secondary particles thereof smaller than 5 µ m. A catalyst composition according to claim 1 or 2, wherein the mordenite of component A is one in which the silica/alumina molar ratio is 15-30. A catalyst composition according to any one of claims 1 to 3, wherein component B comprises an inorganic oxide component which inorganic oxide component is at least one oxide selected from alumina, silica-alumina, silica, titania and magnesia. A catalyst composition according to claim 4, wherein the inorganic oxide component of component B is alumina. A catalyst composition according to claim 5, wherein the alumina is of a boehmite structure. A catalyst composition according to any one of claims 1 to 3, wherein component B comprises a clay component, which clay component is at least one clay selected from montmorillonite, kaolin, sepiolite and acid clay. A catalyst composition according to any preceding claim, wherein the amount of component C is 0.05-1.5 pbw (as metal) for 100 pbw of component A. A catalyst composition according to any preceding claim, wherein the amount of component B is 40-150 pbw for 100 pbw of component A. A catalyst composition according to any preceding claim, wherein the amount of rhenium (component C) is 0.1-2.0 pbw (as metal) for 100 pbw of component B. A process for producing xylene from alkylaromatic hydrocarbons containing C 9 alkylaromatic hydrocarbons, which process comprises employing a catalyst composition as defined in any one of claims 1 to 10 in the presence of hydrogen to achieve dealkylation to convert ethyltoluene in the C 9 alkylaromatic hydrocarbons into toluene, and subsequent transalkylation to convert toluene or toluene and trimethylbenzene into xylene. A process according to claim 11, wherein a catalyst composition as defined in any one of claims 1 to 10 is brought into contact with a feedstock of alkylaromatic hydrocarbons containing C 9 alkylaromatic hydrocarbons, which C 9 alkylaromatic hydrocarbons contain at least 5% by weight thereof of ethyltoluene, in the presence of hydrogen. A process according to claim 11 or 12, wherein the alkylaromatic hydrocarbon feedstock contains less than 0.5 wt% naphthalene. A process according to claim 13, wherein the alkylaromatic hydrocarbon feedstock contains less than 0.3 wt% naphthalene. A process according to claim 13 or 14, wherein the C 9 alkylaromatic hydrocarbons undergo distillation prior to transalkylation.

Inventors: ICHIOKA RYOJI, IWAYAMA KAZUYOSHI, KATO HAJIME, TANAKA HITOSHI, ICHIOKA, RYOJI, IWAYAMA, KAZUYOSHI, KATO, HAJIME, TANAKA, HITOSHI
Applicants: TORAY INDUSTRIES, TORAY INDUSTRIES, INC.
Application year: 1997
Main classification: C07C6
IPC codes: C07C6, B01J29