COMPATIBILIZED FLUOROPLASTIC BLENDS

Abstract: A composition comprises a blend of (a) a first crystalline fluoroplastic which is an ethylene-tetrafluoroethylene copolymer, in an amount 20 and 70 weight %; (b) a second crystalline fluroplastic which is a terpolymer of tetrafluoroethylene, hexafluoropropylene, and vinylidene fluoride, in an amount between 25 and 70 weight %; and (c) a fluorinated thermoplastic elastomer which is a block copolymer having at least one elastomeric segment comprising tetrafluoroethylene, vinylidene fluoride, and hexafluoropropylene repear units in a mole ratio 45-90:5-50:0-35 and at least one nonelastomeric segment comprising tetrafluoroethylene and ethylene repeat units, in an amount between 5 and 25 weight %. The fluorinated thermoplastic elastomer acts as a compatibilizer for the two fluoroplastics. The composition exhibits improved flexibility, tensile strengh, and/or elongation.

Description: COMPATIBILIZED FLUOROPLASTIC BLENDS Technical Field of the Invention This invention relates to a compatibilized blend of fluoroplastics. Background of the Invention Blending of two or more polymers is a common practice, the objective being to pro¬ duce a composition having improved mechanical, rheological, and/or degradative properties compared to the individual polymers. It can be an effective way to customize a compo¬ sition, providing properties which may not be available in a single known polymer or which would require the time-consuming and expensive development of a new polymer. A virtually infinite number of polymer blends is theoretically possible, but not all polymer blends result in compositions with desirable properties. If the component polymers are incompatible, the resulting blend often has inferior properties. This is especially the case for blends involving fluoropolymers. Normally, incompatibility is the rule, and compatibility is the exception. A rigorous and technically precise definition of a compatible blend is a blend in which the constituents are capable of forming a single phase mixture, at least in the amorphous phase, if not the crystalline phase as well. However, at a practical level a compatible blend is often defined as one which displays useful properties. In this application, this latter definition of compatibility will be used. Miscibility (compatibility) in blends of two different polymers is generally limited to instances involving amorphous polymers and even such instances are rare. Where blends of two different semicrystalline polymers are involved, instances of miscibility are even rarer. Compatibilizers, which are usually block or graft copolymers having segments in common with the main polymer components of the two polymers being blended, can be used to improve the chances of obtaining a compatible blend. But even the use of a compatibilizer does not assure success and most examples of successful use of compatibilizers involve polyolefin blends. We are not aware of any compatibilized blends involving two fluoroplastics. Fluoroplastics are unique among polymers, offering performance characteristics unobtainable with most other polymers. Commercially available fluoropolymers include polytetrafluoroethylene (PTFE), fluorinated ethylene-propylene copolymer (FEP), perfluoroalkoxy resin (PFA), polychlorotrifluoroethylene (PCTFE), ethylene-chloro- trifluoroethylene copolymer (ECTFE), ethylene-tetrafluoroethylene copolymer (ETFE), polyvinylidene fluoride (PVDF), and polyvinylfluoride (PVF). Some fluoroplastics such as PTFE are completely fluorinated, while others such as ETFE or PVDF are only partially fluorinated. Typically, fluoroplastics are characterized by high melting points and low glass transition temperatures, enabling them to be advantageously used over a wide temperature range, such as from well below 0 °C to +260 °C. Other desirable properties of fluoro plastics include their excellent solvent resistance, electrical insulative properties, low coefficient of friction, low flammability, low gas permeability, and high inertness and stability. The selection of commercially available fluoroplastics is much more limited than for non-fluorinated polymers, because options regarding both the choice of fluorinated monomer and type of polymerization chemistry are much more limited. Thus, it is desirable to develop novel blends of fluoroplastics having improved properties. Summary of the Invention We disclose here our discovery of a blend of two fluoroplastics and a thermoplastic fluoroelastomer as compatibilizer, which blend unexpectedly has improved flexibility, tensile strength, and/or elongation compared to corresponding blend without the compatibilizer. Accordingly, this invention provides a composition comprising: (a) a first crystalline fluoroplastic which is an ethylene-tetrafluoroethylene copolymer, in an amount between 20 and 70 weight %; (b) a second crystalline fluoroplastic which is a terpolymer of tetrafluoro- ethylene, hexafluoropropylene, and vinylidene fluoride, in an amount between 25 and 70 weight %; and (c) a thermoplastic fluoroelastomer which is a block copolymer comprising at least one elastomeric segment comprising tetrafluoroethylene, vinylidene fluoride, and hexafluoropropylene repeat units in a mole ratio 45-90:5-50:0- 35 and at least one nonelastomeric segment comprising tetrafluoroethylene and ethylene repeat units, in an amount between 5 and 25 weight %; the weight %'s being based on the combined weights of the first and second crystalline fluoroplastics and the thermoplastic fluoroelastomer. Description of the Preferred Embodiments The first crystalline fluoroplastic is an ethylene-tetrafluorethylene copolymer, in an amount of between 20 and 70, preferably between 30 and 70, weight %. As used herein, "ethylene-tetrafluoroethylene copolymer" means a crystalline thermoplastic polymer (i.e., a fluoroplastic) which is a copolymer of ethylene, tetrafluoroethylene and optionally a third monomer. Ethylene-tetrafluoroethylene copolymer is also known in the art as ETFE or poly(ethylene-tetrafluoroethylene), and herein the acronym ETFE may be used synonymously for convenience. The mole ratio of ethylene to tetrafluoroethylene can be about 35-60:65-40. A third monomer can be present in an amount such that the mole ratio of ethylene to tetrafluoroethylene to third monomer is about 40-60:15-50:0-35. Preferably the third monomer, if present, is so in an amount of about 5 to about 30 mole %. The third monomer can be, for example hexafluoropropylene; 3,3,3-trifluoropropylene-l; 2- trifluoromethyl-3,3,3-trifluoropropylene-l ; or perfluoro(alkyl vinyl ether). The melting point of ETFE varies depending on the mole ratio of ethylene and tetrafluoroethylene and the presence or not of a third monomer. Commercially available ETFE's have melting points between 220 and 270 °C. Preferably, ETFE used in the invention has a crystallinity on the order of 50%. ETFE suitable for use in this invention is available from a number of suppliers, including from Du Pont under the tradename Tefzel (e.g., grades 200, 280, 2055, 2127, 2181 and 2129) and from Daikin Industries under the tradename Neoflon (e.g., grades 541, 610 and 620). The second crystalline fluoroplastic is a teφolymer of tetrafluoroethylene, hexafluo¬ ropropylene, and vinylidene fluoride and is used in an amount of between 25 and 70, preferably 35 and 65, weight %. It has substantial crystallinity associated with the tetrafluoroethylene repeat units. A suitable second crystalline fluoroplastic is available commercially under the tradename THV (for example grades THV 200, THV 400, and THV 500, especially the first one) from Minnesota Mining and Mfg. The monomer ratio affects mechanical properties and the melting temperature. THV 200 teφolymer has a peak melting temperature (T m ) of 1 19 °C, a crystallinity level of about 26 %, and a glass transition temperature (T g ) of 5 °C. THV 500 teφolymer has a T m of 165 °C, a crystallinity level of about 29 %, and a T g of 26 °C. Generally, an increase in the tetrafluoroethylene in the monomer mix leads to an increase in T m and T g . The thermoplastic fluoroelastomer, which acts as a compatibilizer between the first and second crystalline fluoroplastics, has elastomeric (soft) and non-elastomeric (hard) segments (or blocks). The elastomeric segment comprises tetrafluoroethylene, vinylidene fluoride, and hexafluoropropylene repeat units with preferred relative weight ratios of about 20-40:40-60:10-30, respectively. The nonelastomeric segment comprises substantially alternating tetrafluoroethylene and ethylene repeat units. A preferred weight ratio of elastomeric to nonelastomeric segments of between about 70-95:30-5. The elastomeric segment preferably has a molecular weight of from about 10,000 to about 10,000,000. The nonelastomeric segment preferably has a molecular weight of from about 1 ,000 to about 1,000,000, more preferably from about 5,000 to about 500,000. The thermoplastic fluoroelastomer is present in an amount between 5 and 25, preferably between 5 and 12, weight %. A preferred thermoplastic fluoroelastomer is available under the tradename Daiel T- 530 from Daikin (Japan). Compatiblilized blends of this invention exhibit unexpectedly improved properties in the form of increased flexibility (as measured by secant modulus (2 %)), tensile strength, and/or elongation. Improvements are especially noticeable in the flexibility. The blends of this invention may be crosslinked, for example with electron beam or gamma radiation. Without being bound by theory, we believe that the fluoroelastomer is effective as a compatibilizer because its ethylene-tetrafluoroethylene hard block is compatible with the first crystalline fluoroplastic (an ethylene-tetrafluoroethylne copolymer) while its tetrafluoroethylene-hexafluoropropylene-vinylidene fluoride soft block is compatible with the second crystalline fluoroplastic (tetrafluoroethylene-hexafluoropropylene-vinylidene fluoride teφolymer). Thus, it is likely the fluoroelastomer lowers the interfacial tension between the phases of the first and second crystalline fluoroplastic, thereby promoting interfacial adhesion and a higher level of dispersion during mixing. Blends of this invention may contain additives commonly used in polymer formulations, such as radiation crosslinking promoters (or prorad), antioxidants, UV stabilizers, and pigments, in typical amounts. The efficiency of radiation crosslinking may be increased by adding an effective amount of a prorad in intimate mixture with the polymeric components. Generally, a prorad is a compound having at least two ethylenic double bonds, present as allyl, methallyl, propargyl, acrylyl, or vinyl groups. Examples of suitable prorads include triallyl cyanurate (TAC), triallyl isocyanurate (TAIC), triallyl trimellitate, triallyl trimesate, tetraallyl pyro- mellitate, the diallyl ester of l,l,3-trimethyl-5-carboxy-3-(p-carboxyphenyl)indane, diallyl adipate, diallyl phthalate (DAP), diallyl isophthalate, diallyl terephthalate, 1,4-butylene glycol dimethacrylate, trimethylolpropane trimethacrylate (TMPTM), pentaerythritol trimethacrylate, glycerol propoxy trimethacrylate, liquid poly(l,2-butadiene), tri-(2-acryl- oxyethyl)isocyanurate, and tri-(2-methacryloxyethyl)isocyanurate, and the like, and com¬ binations thereof. Preferred crosslinking agents are TAIC, TAC, and TMPTM. Other cross¬ linking agents which can be used are disclosed in US Pat. 3,763,222; 3,840,619; 3,894,118; 3,911,192; 3,970,770; 3,985,716; 3,995,091; 4,031,167; 4,155,823; and 4,353,961, the disclosures of which are incorporated herein by reference. Mixtures of crosslinking promoters can be used. Preferably, the radiation crosslinking promoter is used in an amount of between 0.1 % and 10 %, more preferably between 1 % and 5 %, per cent by weight based on the weight of the composition. An effective amount of an antioxidant (which can be a single compound or a combination of two or more compounds) may be added to increase thermal stability, forming an intimate mixture or blend with the polymers. Suitable antioxidants include alkylated phenols, e.g. those commercially available as Goodrite 3125™, Irganox B225™ Irganox 1010™ (pentaerythrityl tetrakis-3-(3,5-di-/t?r/-butyl-4-hydroxyphenyl)propionate, Irganox 1035™, Irganox 1076™ (octadecyl 3-(3,5-di-ter/-butyl-4-hydroxyphenyl)propio- nate), Irganox 31 14™ (l,3,5-tris-(3,5-di-/er/-butyl-4-hydroxybenzyl)isocyanurate), Topanol CA™ (l,l,3-tris-(5-/er/-butyl-4-hydroxy-2-methylphenyl)butane), Irganox 1093™, and Vulkanox BKF™; organic phosphite or phosphates, e.g. dilauryl phosphite and Mark 1178™; alkylidene polyphenols, e.g. Ethanox 330™ (l,3,5-tris-(3,5-di-te/-/-butyl-4-hydro- xybenzyl)mesitylene); thio-bis-alkylated phenols, e.g. Santonox R™ (4,4'-thiobis-(3- methyl-6-tør/-butylphenol) and polymerized derivatives thereof; dilauryl thio-dipropionate, e.g. Carstab DLTDP™; dimyristyl thiodipropionate, e.g. Carstab DMTDP; distearyl thiodipropionate (DSTDP), e.g. Cyanox STDP; amines, e.g. Wingstay 29, and the like. Combinations of antioxidants can be used. Preferably, the antioxidant is used in an amount of between 0.1 % and 5 %, more preferably between 0.2 % and 2 %, per cent by weight based on the weight of the composition. Other additives which can be added include: UV stabilizers such as [2,2'-thio-bis(4- t-octylphenolato)] n-butylamine nickel, Cyasorb UV 1084, 3,5-di-t-butyl-p-hydroxybenzoic acid, UV Chek AM-240; conductive fillers such as carbon black for imparting electrical conductivity; zinc oxide as an acid acceptor or scavenger; and pigments such as titanium dioxide and carbon black. To measure tensile strength and elongation, the procedure of ASTM D638-94b was generally followed and is summarized as follows: an Instron Model 5567 tensile tester driven by Merlin/Series IX software was set up with a 225 lb Tension Load Cell. The jaw separation was 50.8 mm (2 in). The crosshead speed was 2.0 in/min. These adjustments were made using Windows-based Merlin Series IX software. The extension return limit was set at 763 mm. Test specimens were cut from slabs 0.020 to 0.030 inch thick with a dumbbell-shaped D-die per ASTM specifications with a reduced section dimension of 0.125 inch. The Instron tester was calibrated using the built-in calibration capability. Mea- surements were done at ambient (room) temperature (20-25 °C). Each test specimen was measured for width and thickness before analysis, using a micrometer. Two bench marks were marked on each specimen with a 1.0 inch (25.4 mm) separation, centered on the reduced section, in order to measure elongation. The specimens were stretched until break at a crosshead speed of 2 in/min. The elongation between the benchmarks was measured with a video extensometer. The tensile strength, elongation and secant modulus were all recorded automatically using the Merlin software. "Elongation" means the elongation at break, also referred to as the ultimate elongation. Similarly, "tensile strength" means the tensile strength at break, also referred to as the ultimate tensile strength, and is calculated by dividing the tension at break by the initial cross-sectional area. Secant modulus (2 %) was calculated as follows: the load at 2 % strain was determined. This load was divided by the original cross-sectional area to obtain the tensile stress, in pounds/square inch (psi). The tensile stress was then divided by 0.02 inch/inch to derive the secant modulus (2 %). The compatibilized blends of this invention may be used in products in which fluoroplastics normally are used, and are especially suitable for wire and cable insulation, heat-recoverable articles, and other applications where fluoropolymers having superior flexibility, elongation, and tensile strength are desirable. The practice of our invention may be understood by reference to the following examples, which are provided by means of illustration and not limitation. Example 1 In this example, the first fluoroplastic was Tefzel 2129 ETFE from Du Pont (T m 230 °C), the second fluoroplastic was THV 200 from 3M, and the fluoroelastomer compatibilizer was Daiel T-530 from Daikin. Various amounts of the fluoroelastomer compatibilizer and various ratios of the first and second fluoroplastic were used. Blends were prepared according to the following procedure: the component polymers along with the additive package described following were mixed in a Brabender mixer for 9-11 min at 30 φm at 275 °C. Each sample composition was molded into 25 mil thick slabs. Crosslinked samples were irradiated with electron beam radiation at a total dosage of 15 MR and annealed at 150 °C for 1 hr. For each blend, a control was prepared in which the ratio of the first and second fluoroplastics was kept substantially the same as in the test sample but with the compatibilizer omitted. Each blend contained about 4.35 parts by weight (ppw) (per 95 parts by weight of blend) of an additive package consisting of 0.10 ppw DSTDP antioxidant, 0.25 ppw Irganox 1010 antioxidant, 0.5 ppw Kadox 15 zinc oxide, and 3.50 ppw TAIC prorad. Tables IA and IB give formulation and mechanical properties (uncrosslinked and crosslinked), respectively, of compositions where the amount of compatibilizer was kept at about 5% while the ratio of the first and second fluoroplastics was varied. Table IB also includes, for reference puφoses, the mechanical properties of the first and second fluoroplastics alone. Each set of data is paired with a corresponding control in which the compatibilizer is omitted while the ratio of first and second fluoroplastics is kept constant. TABLE I-A — COMPOSITION OF COMPATIBILIZED BLENDS: TEFZEL 2129/THV 200/DAIEL T-530 APPROXIMATELY 5 WT% COMPATIBILIZER Experiment Tefzel 2129 THV 200 Daiel T-530 Ratio lst/2nd No. (wt. %) a (wt %) a (wt %) 8 Fluoroplastic 1 (control) 79.09 20.91 — 3.78 1 74.96 19.81 5.23 3.78 2 (control) 58.18 41.82 — 1.39 2 55.14 39.63 5.23 1.39 3 (control) 20.91 79.09 — 0.26 3 19.81 74.96 5.23 0.26 4 (control) 50.01 49.99 — 1.00 4 50.86 43.91 5.23 1.15 a π Wiei •g lht . n %/ t's 1 based on combined weights of 1st and 2nd fluoroplastic and compatibilizer TABLE I-B — MECHANICAL PROPERTIES OF COMPATIBILIZED BLENDS : TEFZEL 2129/THV 200/DAIEL T-530 APPROXIMATELY 5 WT% COMPATIBILIZER Unbeamed (Uncrosslinked) Beamed (Crosslinked) a Secant Tensile Elonga¬ Secant Tensile Elonga¬ Experiment Modulus, Strength tion Modulus, Strength tion No. 2% (psi) b (psi) b (%) b 2% (psi) b (psi) b (%) " Tefzel 2129 c 66,160 5,360 400 77,990 5,160 160 THV 200 c 9,200 3,380 690 30,300 3,780 220 1 (Control) 51,080 4,890 410 68,990 5,120 210 1 43,570 4,940 420 62,320 4,710 190 2 (control) 35,970 2,330 310 52,690 4,260 220 2 26,490 3,850 440 39,200 3,700 200 3 (control) 10,350 1,460 470 24,140 2,950 210 3 9,270 2,620 480 26,090 3,160 190 4 (control) 27,900 1,600 220 45,960 4,050 210 4 31,360 4,160 440 40,720 4,120 200 Beamed with 15 Mrad electron beam radiation and then annealed at 150°C for 1 hr. Reported values are averages of 5 measurements, unless noted otherwise c Average of 2 sets of 5 measurements The data for compositions in which the amount of compatibilizer was kept at about 10 wt% while the ratio of first and second crystalline fluoroplastics was varied are presented in Tables II-A and II-B, which are organized in the same manner as the preceding Tables I-A and I-B. TABLE II-A — COMPOSITION OF COMPATIBILIZED BLENDS: TEFZEL 2129/THV 200/DAIEL T-530 APPROXIMATELY 10 WT% COMPATIBILIZER Experiment Tefzel 2129 THV 200 Daiel T-530 Ratio lst/2nd No (wt. %) a (wt %) a (wt %) a Fluoroplastic (control) 79.09 20 91 — 3.78 70.82 18.72 10.45 3.78 (control) 58.18 41.82 — 1.39 52.10 37 45 10.45 1.39 (control) 20.91 79.09 — 0.26 18 73 70.81 10.45 0.26 (control) 50.01 49.99 — 1.00 45.64 43.91 10 45 1.03 ι Wι τei •g Iht . n %/ !'s 7 based on combined weights of 1st and 2nd fluoroplastic and compatibilizer TABLE II-B — MECHANICAL PROPERTIES OF COMPATIBILIZED BLENDS : TEFZEL 2129/THV 200/DAIEL T-530 APPROXIMATELY 10 WT% COMPATIBILIZER Unbeamed (Uncrosslinked) Beamed (Crosslinked) a Secant Tensile Elonga¬ Secant Tensile Elonga¬ Experiment Modulus, Strength tion Modulus, Strength tion No. 2% (psi) b (psi) b (%) " 2% (psi) b (psi) b (%) " Tefzel 2129 c 66,160 5,360 400 77,990 5,160 160 THV 200 c 9,200 3,380 690 30,300 3,780 220 1 (Control) 43,670 4,060 390 66,920 4,580 190 1 43,850 5,000 440 51,710 4,380 200 2 (control) 31,710 1,420 110 56,060 3,930 190 2 21,580 3,260 440 35,640 3,450 180 3 (control) 12,360 1,590 510 27,670 2,940 190 3 8,370 2,850 540 19,980 3,400 220 4 (control) 27,900 1,600 220 45,960 4,050 210 4 24,620 3,920 430 35,650 3,570 190 Reported values are averages of 5 measurements, unless noted otherwise c Average of 2 sets of 5 measurements The data for compositions in which the amount of compatibilizer was kept at about 20 wt% while the ratio of first and second crystalline fluoroplastics was varied are presented in Tables III-A and III-B, which are organized in the same manner as the preceding tables. TABLE III-A — COMPOSITION OF COMPATIBILIZED BLENDS: TEFZEL 2129/THV 200/DAIEL T-530 APPROXIMATELY 20 WT% COMPATIBILIZER Experiment Tefzel 2129 THV 200 Daiel T-530 Ratio lst/2nd No. (wt. %) a (wt %) a (wt %) a Fluoroplastic 1 (control) 79.09 20.91 — 3.78 1 62.55 16.53 20.91 3.78 2 (control) 58.18 41.82 — 1.39 2 46.02 33.06 20.91 1.39 3 (control) 20.91 79.09 — 0.26 3 16.51 62.57 20.91 0.26 a i Wnei'gh l t. n %/ 5's i based on combined weights of 1 st and 2nd fluoroplastic and compatibilizer TABLE III-B — MECHANICAL PROPERTIES OF COMPATIBILIZED BLENDS : TEFZEL 2129/THV 200/DAIEL T-530 APPROXIMATELY 20 WT% COMPATIBILIZER Unbeamed (Uncrosslinked) Beamed (Crosslinked) a Secant Tensile Elonga¬ Secant Tensile Elonga¬ Experiment Modulus, Strength tion Modulus, Strength tion No. 2% (psi) b (psi) b (%) b 2% (psi) b (psi) b (%) b Tefzel 2129 c 66,160 5,360 400 77,990 5,160 160 THV 200 c 9,200 3,380 690 30,300 3,780 220 1 (Control) 50,130 4,120 430 73,120 4,860 190 1 24,870 3,940 480 44,380 3,840 190 2 (control) 31,830 2,530 350 44,680 3,610 190 2 16,630 3,440 480 27,600 3,600 200 3 (control) 15,660 2,120 540 24,800 3,130 200 3 5,350 2,870 560 17,860 3,1 10 210 Reported values are averages of 5 measurements, unless noted otherwise Average of 2 sets of 5 measurements Example 2 In this example, the first fluoroplastic was Neoflon EP620 ETFE from Daikin (T m 225 °C), the second fluoroplastic was THV 200, and the fluoroelastomer compatibilizer was Daiel T-530. The blends were prepared as in Example 1. The data for the instance in which the amount of compatibilizer was about 5 wt % is presented in Tables IV-A/IV-B, arranged in the same manner as in the preceding tables. TABLE IV-A — COMPOSITION OF COMPATIBILIZED BLENDS: NEOFLON EP620/THV 200/DAIEL T-530 APPROXIMATELY 5 WT% COMPATIBILIZER Experiment Neoflon EP620 THV 200 Daiel T-530 Ratio lst/2nd No. (wt. %) a (wt %) a (wt %) a Fluoroplastic 1 (control) 79.09 20.91 — 3.78 1 74.96 19.81 5.23 3.78 2 (control) 58.18 41.82 — 1.39 2 55.14 39.63 5.23 1.39 3 (control) 20.91 79.09 — 0.26 3 19.81 74.96 5.23 0.26 4 (control) 50.01 49.99 — 1.00 4 50.86 43.91 5.23 1.15 Weight %'s based on combined weights of 1st and 2nd fluoroplastic and compatibilizer TABLE IV-B — MECHANICAL PROPERTIES OF COMPATIBILIZED BLENDS: NEOFLON EP620/THV 200/DAIEL T-530 APPROXIMATELY 5 WT% COMPATIBILIZER Unbeamed (Uncrosslinked) Beamed (Crosslinked) a Secant Tensile Elonga¬ Secant Tensile Elonga¬ Experiment Modulus, Strength tion Modulus, Strength tion No. 2% (psi) b (psi) b (%) " 2% (psi) b (psi) b (%) " Neoflon 620 c 48,310 4,440 380 88,150 4,420 130 THV 200 c 9,200 3,280 690 30,300 3,780 220 1 (Control) 43,000 4,780 440 56,800 4,150 190 1 33,800 4,660 440 54,890 3,860 180 2 (control) 28,700 2,910 410 48,210 3,810 210 2 30,130 4,020 450 48,830 3,850 200 3 (control) 12,760 1,770 520 29,770 2,740 190 3 8,570 2,830 520 21,680 3,320 230 4 (control) 25,100 2,280 400 45,800 4,030 200 4 23,320 3,770 470 42,460 3,770 190 Reported values are averages of 5 measurements, unless noted otherwise c Average of 2 sets of 5 measurements Data for the instance in which the amount of compatibilizer was about 10 wt % is presented in Tables V-A and V-B. TABLE V-A — COMPOSITION OF COMPATIBILIZED BLENDS: NEOFLON EP620/THV 200/DAIEL T-530 APPROXIMATELY 10 WT% COMPATIBILIZER Experiment Neoflon EP620 THV 200 Daiel T-530 Ratio lst/2nd No. (wt. %) a (wt %) a (wt %) a Fluoroplastic 1 (control) 50.01 49.99 — 1.00 1 45.64 43.91 10.45 1.03 Weight %'s based on combined weights of 1st and 2nd fluoroplastic and compatibilizer TABLE V-B — MECHANICAL PROPERTIES OF COMPATIBILIZED BLENDS: NEOFLON EP620/THV 200/DAIEL T-530 APPROXIMATELY 10 WT% COMPATIBILIZER Unbeamed (Uncrosslinked) Beamed (Crosslinked) a Secant Tensile Elonga¬ Secant Tensile Elonga¬ Experiment Modulus, Strength tion Modulus, Strength tion No. 2% (psi) b (psi) b (%) " 2% (psi) b (psi) b (%) " Neoflon 620 c 48,310 4,440 380 88,150 4,420 130 THV 200 c 9,200 3,280 690 30,300 3,780 220 1 (control) 25,100 2,280 400 45,800 4,030 200 1 17,550 4,000 540 33,240 3,960 210 Beamed with 15 Mrad electron beam radiation and then annealed at 150°C for 1 hr. Reported values are averages of 5 measurements, unless noted otherwise Average of 2 sets of 5 measurements Example 3 In this example, the first fluoroplastic was Tefzel 2181 ETFE from Du Pont (T m 265 °C), the second fluoroplastic was THV 200, and the compatibilizer was Daiel T-530. The blends were prepared as in Example 1 , except that the Brabender mixing was done at 300 °C. The data is provided in Tables VI-A and VI-B, arranged as before. TABLE VI-A — COMPOSITION OF COMPATIBILIZED BLENDS: TEFZEL 2181/THV 200/DAIEL T-530 APPROXIMATELY 5 WT% COMPATIBILIZER Experiment TEFZEL 2181 THV 200 Daiel T-530 Ratio lst/2nd No. (wt. %) a (wt %) a (wt %) a Fluoroplastic 1 (control) 79.09 20.91 — 3.78 1 74.96 19.81 5.23 3.78 2 (control) 58.18 41.82 — 1.39 2 55.14 39.63 5.23 1.39 3 (control) 20.91 79.09 — 0.26 3 19.81 74.96 5.23 0.26 TABLE VI-B — MECHANICAL PROPERTIES OF COMPATIBILIZED BLENDS : TEFZEL 2181/THV 200/DAIEL T-530 APPROXIMATELY 5 WT% COMPATIBILIZER Unbeamed (Uncrosslinked) Beamed (Crosslinked) a Secant Tensile Elonga¬ Secant Tensile Elonga¬ Experiment Modulus, Strength tion Modulus, Strength tion No. 2% (psi) b (psi) b (%) " 2% (psi) b (psi) b (%) b Tefzel 2181 c 97,060 6,550 350 118,250 6,970 140 THV 200 c 9,380 3,470 670 33,370 3,780 220 1 (Control) 78,250 4,880 330 87,930 6,200 190 1 67,450 5,210 360 85,570 5,480 190 2 : (control) s 45,100 1,630 50 59,620 4,040 160 2 36,760 3,260 330 58,600 4,690 200 3 (control) 19,230 1,730 480 40,680 3,270 180 3 13,980 2,920 450 29,390 3,490 200 Beamed with 15 Mrad electron beam radiation and then annealed at 150°C for 1 hr. Reported values are averages of 5 measurements, unless noted otherwise Average of 2 sets of 5 measurements Average of 2 sets of 5 measurements The above results show that the compatibilized blends of this invention (whether crosslinked or not) generally exhibit an increase in at least one of flexibility (i.e., decreased secant modulus (2 %)), tensile strength, and/or elongation, without any offsetting decrement in the other mechanical properties. Improvement is especially marked in the flexibility. In some instances, improvements in two or even all three properties are observed. The foregoing detailed description of the invention includes passages which are chiefly or exclusively concerned with particular parts or aspects of the invention. It is to be understood that this is for clarity and convenience, that a particular feature may be relevant in more than just the passage in which it is disclosed, and that the disclosure herein includes all the appropriate combinations of information found in the different passages. Similarly, although the various passages may relate to specific embodiments of the invention, it is to be understood that where a specific feature is disclosed in the context of a particular embodiment, such feature can also be used, to the extent appropriate, in the context of another embodiment, in combination with another feature, or in the invention in general.

Claims: Claims What is claimed is: 1. A composition comprising a blend of: (a) a first crystalline fluoroplastic which is an ethylene-tetrafluoroethylene copolymer, in an amount between 20 and 70 weight %; (b) a second crystalline fluoroplastic which is a teφolymer of tetrafluoro¬ ethylene, hexafluoropropylene, and vinylidene fluoride, in an amount between 25 and 70 weight %; and (c) a thermoplastic fluoroelastomer which is a block copolymer comprising at least one elastomeric segment comprising tetrafluoroethylene, vinylidene fluoride, and hexafluoropropylene repeat units in a mole ratio 45-90:5-50:0- 35 and at least one nonelastomeric segment comprising tetrafluoroethylene and ethylene repeat units, in an amount between 5 and 25 weight %; the weight %'s being based on the combined weights of the first and second crystalline fluoroplastics and the thermoplastic fluoroelastomer. 2. A composition according to claim 1, wherein the first crystalline fluoroplastic is present in an amount between 30 and 70 weight %. 3. A composition according to claim 1, wherein the second crystalline fluoroplastic is present in an amount between 35 and 65 weight %. 4. A composition according to claim 1, wherein the thermoplastic fluoroelastomer is present in an amount of between 5 and 12 weight %. 5. A composition according to any of claims 1 to 4, which has been crosslinked by electron beam radiation. 6. A composition according to any of claims 1 to 4, which has been crosslinked by gamma radiation.

Inventors: DAWES KEITH, KADUK BRIAN, SINGH AWTAR, TIAN JING, DAWES, KEITH, KADUK, BRIAN, SINGH, AWTAR, TIAN, JING
Applicants: RAYCHEM CORP, RAYCHEM CORPORATION
Application year: 1997
Main classification: C08L23
IPC codes: C08J3, C08L23, C08L27, C08L53