COMPOSITIONS AND ARTICLES OF MANUFACTURE

Abstract: A composition comprising a filler material, a chemical compound and a polymer. A preferred filler material comprises carbon black and preferred polymers include ethylene-containing polymers such as ethylene-propylene copolymer or ethylene-propylene terpolymers. The present invention also includes articles of manufacture incorporating the polymer compositions.

Description: Compositions and Articles of Manufacture Field of the Invention The present invention relates to a composition compπsing a filler matenal, a chemical compound and a polymer. A preferred filler material comprises carbon black and preferred polymers include ethylene-containing polymers such as ethylene-propylene copolymer or ethylene-propylene terpolymers. The present invention also relates to articles of manufacture incorporating the compositions. Background of the Invention Polymer compositions are utilized in a variety of applications, including so-called "industrial rubber applications". Industrial rubber applications include hoses, belts, electrical cable insulation, automotive and industrial wcatherstπpping, profiles, molded parts and the like. Many articles for industrial rubber applications are produced through extrusion techniques, i.e. the polymer composition is extruded through a die then cooled or chemically hardened. Fillers are often utilized in polymer compositions to impart desirable characteπ sties such as reinforcement, pigmentation and/or conductivity to the polymer compositions. Carbon blacks have been widely utilized as fillers and reinforcing pigments in the compounding and preparation of polymer compositions. Carbon blacks are generally characterized on the basis ol one or more of their properties including, but not limited to, their surface areas, surface chemistry, aggregate sizes, and particle sizes. The properties of carbon blacks are analytically determined by tests known to the art, including iodine number (I 2 No.) and dibutyl phthalate adsorption (DBP) The dispersion properties (dispersibihty) of a filler are relevant to the use of fillers in polymer compositions. It is generally advantageous to have fillers which are easily dispersible in polymer compositions. Many types of polymer compositions are cured using an UHF microwave cuπng process. UHF microwave cuπng is becoming increasingly important due to its high cuπng efficiency and other desirable attπbutes. As understood in the art, UHF microwave cuπng refers to a cuπng process utilizing ultra high frequency microwaves (from about 300 to 3000 megahertz (megacycles per second or "MHz")). Polymer compositions that are more receptive to UHF microwave cuπng have a faster heating rate and thus are advantageous for processing the matenal Generally, polymer compositions incorporating high surface area carbon blacks are more receptive to UHF microwave cuπng. However, high surface area carbon blacks are often difficult to disperse in polymer compositions It would be advantageous to have a carbon black composition which is easily dispersible in polymer compositions and/or which imparts increased UHF receptivity to the polymer composition Summary of the Invention The present invention provides compositions and articles of manufacture which achieve the advantages set forth above as well as other advantages. The present invention provides a composition compπsmg: an ethylene containing polymer; 50 to 250 parts by weight a filler matenal, per 100 parts by weight ethylene containing polymer (.50 to 250 phr); and 0.05 to 50 parts by weight of a chemical compound, per 100 parts by weight ethylene containing polymer (0.05 to 50 phr), the chemical compound having the structure A-B-[(C) X -D wherein: A compπses one or more of the following- hydrogen, an alkyl group, an aryl group; or an alkyl aryl group; B is a bπdging group between A and C compπsing one or more of the following ether, a carboxylic acid, a 1 ,2-dιcarboxylιc acid den ved from an anhydnde, an amine, an amide, a sulfate, a sulphonate, a phosphate, a phosphate, or a carboxylic ester of a polyhydπc alcohol containing 2 to 6 hydroxyl groups; C compπses an ethylene oxide repeating unit; D compπses one or more the following: hydrogen, an alkyl group, an alkali or an alkaline earth metal; y is 0 to 200 and x = 1, 2, 3, 4 or 5 The composition may further compnse: 0 to 200 parts by weight an oil, per 100 part by weight of ethylene containing polymer (0 to 200 phr). The present invention also includes an article of manufacture produced utilizing the composition of the present invention. The article of manufacture may compπse an extruded article, including a profile, tube, tape or film; a hose; a belt; or a molded article In accordance with one aspect of the composition of the present invention, the composition is receptive to UHF microwave cuπng. In accordance with another aspect of the composition of the present invention, the filler matenal may be easily dispersed in the composition duπng its preparation. The articles of manufacture of the present invention are advantageous for similar reasons. Further details and advantages of the present invention are set forth in the following more detailed descπption. Detailed Descπ tion of the Invention According to the present invention, a composition comprises: an ethylene containing polymer; 150 to 2.50 parts by weight a filler material, per 100 parts by weight ethylene containing polymer (50 to 250 phr); and 0.05 to 50 parts by weight a chemical compound, per 100 parts by weight ethylene containing polymer (0.05 to 50 phr) the chemical compound having the structure A-B-[(C) y ] x -D wherein: A comprises one or more of the following: hydrogen, an alkyl group, an aryl group; or an alkyl aryl group, preferably an alkyl group, more preferably an alkyl group with 8 to 65 carbon atoms; B is a bridging group between A and C comprising one or more of the following: ether, a carboxylic acid, a 1,2-dicarboxylic acid derived from an anhydride, an amine, an amide, a sulfate, a sulphonate, a phosphate, a phosphate, or a carboxylic ester of a polyhydric alcohol containing 2 to 6 hydroxyl groups; C comprises an ethylene oxide repeating unit; D comprises one or more the following: hydrogen, an alkyl group, an alkali or an alkaline earth metal; preferably hydrogen or, if an alkyl group preferably methyl, or if an alkali or alkaline earth metal preferably sodium or potassium; y is 0 to 200, preferably 5 to 40 and x = 1, 2, 3, 4 or 5, preferably if B comprises an ether, a carboxylic acid, a sulphate or a sulphonate then x = 1 ; if B comprises an amine, amide or a phosphate then x = 2; if B comprises a 1,2-dicarboxylic acid then x = 1 or 2; if B comprises an ester of a polyhydric alcohol containing 2 to 6 hydroxyl groups x = 1, 2, 3, 4 or 5. The composition may further comprise: 0 to 200 parts by weight an oil, per 100 part by weight of ethylene containing polymer (0 to 200 phr). Preferred chemical compounds comprise: fatty alcohol ethoxylates, fatty acid ethoxylates, fatty amine ethoxylates, fatty amide ethoxylates, glycerol and sorbitan ester ethoxylates. Examples of ethylene containing polymers suitable for use in the composition of the present invention include, but are not limited to: homo, co or terpolymers and graft polymers of ethylene where the co-monomers are selected from butene, hexene, propene, octene, vinyl acetate, acrylic acid, methacrylic acid, esters of acrylic acid, esters of methacrylic acid, maleic anhydride, half ester of maleic anhydride, and carbon monoxide. Preferably the ethylene containing polymer comprises: an ethylene- propylene copolymer or an ethylene-propylene terpolymer. More preferably, the ethylene containing polymer comprises ethylene propylene diene monomer (EPDM). Suitable filler materials for use in the composition of the present invention include, but are not limited to, carbonaceous filler materials such as carbon black and graphite, composites comprising carbon black and metal oxide (e.g. silica) and blends including such carbonaceous filler materials. Suitable oils include, but are not limited to: aromatic oils, naphthenic oils, hydrogenated naphthenic oils, paraffinic oils and vegetable oils. The composition of the present invention may include other conventional additives such as coagents, additional filler materials, processing additives, hydrocarbon oils, stabilizers, accelerators, antioxidants, curing agents, vinyl silane and the like. In an embodiment of the present invention the composition is curable. The compositions of the present invention may be produced by physically mixing the polymer, filler and chemical compound in any manner known to the art for combining polymers and paniculate components. A preferred method for producing the compositions of the present invention is compounding using a batch or continuous mixer such as a Banbury mixer, Twin Screw extruder or Buss kneader. The compositions of the present invention may be cured in manners conventional in the art. The compositions of the present invention may also be produced by pretreating the filler material with the chemical compound and then physically mixing the treated filler material and the polymer. As used herein, a treated filler material comprises a filler material and a chemical compound. As set forth above, a suitable filler material for use in the present invention is a carbonaceous material. A preferred carbonaceous material is carbon black. The carbon black may be any carbon black such as a furnace carbon black, a thermal carbon black, an acetylene black, and a carbon black produced by a gasification process. While any carbon black may be utilized in the compositions of the present invention, preferably the carbon black component of the treated filler material has an iodine number (I No.) of 10- 70 mg g, preferably 10-40 mg/g, and a fluffy dibutyl phthalate absorption value (DBP) of 30-1150 cc/lOOg, preferably 80-130 cc/lOOg. A preferred treated filler material is a carbon black treated with 0.1 to 50%, by weight, preferably 0.1 to 20%, by weight, based on the weight of the treated filler material of a chemical compound, wherein the chemical compound has the structure A-B- [(Q y ] x -D wherein: A comprises: hydrogen, an alkyl group, an aryl group; an alkyl aryl group, preferably an alkyl group, more preferably an alkyl group with 8 to 65 carbon atoms; or mixtures thereof; B is a bridging group between A and C comprising: ether, a carboxylic acid, a 1,2- dicarboxylic acid derived from an anhydride, an amine, an amide, a sulfate, a sulphonate, a phosphate, a phosphate, a carboxylic ester of a polyhydric alcohol containing 2 to 6 hydroxyl groups; C comprises an ethylene oxide repeating unit; D comprises hydrogen, an alkyl group, an alkali, an alkaline earth metal or mixtures thereof; preferably hydrogen or, if an alkyl group preferably methyl, or if an alkali or alkaline earth metal preferably sodium or potassium; y is 0 to 200, preferably 5 to 40 and x = 1, 2, 3, 4 or 5, preferably if B comprises an ether, a carboxylic acid, a sulphate or a sulphonate then x = 1 ; if B comprises an amine, amide or a phosphate then x = 2; if B comprises a 1 ,2-dicarboxylic acid then x = 1 or 2; if B comprises an ester of a polyhydric alcohol containing 2 to 6 hydroxyl groups x = 1, 2, 3, 4 or 5. The treated filler material may further comprise 0 to 50%, by weight an oil. Suitable oils include, but are not limited to, conventional pelletizing oil and aromatic oils, naphthenic oils, hydrogenated naphthenic oils, paraffinic oils, vegetable oils and/or mixtures thereof. A treated filler material suitable for use in the compositions of the present invention may be produced in any manner known in the art, such as by physically blending the components, melt mixing the components or combining the components while pelletizing the filler. The treated filler material may be produced, in dry form, by a conventional pelletizing process. For example, treated filler material for use in the compositions of the present invention may be produced by contacting a filler, e.g. a fluffy carbon black, in a pin pelletizer with a dispersion containing a chemical compound to form wet pellets and then heating the wet pellets under controlled temperature and time parameters such that the volatiles are removed from the pellets without the chemical compound undergoing substantial decomposition. Pin pelletizers which may be utilized to produce a treated filler material for use in compositions of the present invention are known in the art and include the pin pelletizer described in U.S. Patent No. 3,528,785, the disclosure of which is hereby incorporated by reference. U.S. Patent No. 3,528,785 also describes a conventional pelletizing process which may be utilized to produce a treated filler material for use in the compositions of the present invention. The present invention also includes an article of manufacture produced utilizing the composition of the present invention. The article of manufacture may comprise an extruded article, such as a profile, tube, tape or film. The article of manufacture may also comprise a hose; a belt; or a molded article. The articles of manufacture of the present invention may be produced using conventional techniques utilized by those of ordinary skill in the art. The effectiveness and advantages of various aspects and embodiments of the present invention will be further illustrated by the following examples wherein the following testing procedures were utilized. The following testing procedures were utilized in the determination and evaluation of the analytical properties of the carbon blacks utilized in the following examples. The DBP (dibutyl phthalate adsorption value) of the carbon blacks utilized in the examples, expressed as cubic centimeters DBP per 100 grams carbon black (cc/lOOg), was determined according to the procedure set forth in ASTM D2414. The Iodine number (I 2 No.) of the carbon blacks utilized in the examples, expressed as milligrams per gram (mg/g), was determined according to ASTM test procedure D 1510. The polymer compositions, described in the following examples were evaluated for heating rate and heating time to reach 180° C, utilizing the following test procedures. A 6 mm (millimeter) in diameter by 40 mm long test piece of the polymer composition was exposed to a 60 Watt microwave source. Temperature change in the test piece under exposure was measured utilizing a temperature probe, and exposure time was measured utilizing a stopwatch. The exposure time for the test piece to reach 180° C was measured and the heating rate in °C per second was calculated from the exposure time. As utilized in the description of the chemical compounds utilized in the Examples, HLB value refers to hydrophile-Iipophile balance value which may be determined by the method described in Non-Ionic Surfactants Volume 23. edited by Martin Schick (Marcel Dekker Inc. (New York) 1987; ISBN 0-8247-7530-9), page 440. Non-Ionic Surfactants Volume 23 provides equations which relate the structure of the surfactant molecule to HLB value. HLB value is also discussed in the following journal articles: Griffin W.C., J. Soc. Cosmetic Chemist, Vol. 1, page 311 et seq. (1949) and Vol. 5, page 249 et seq. (1954). From data relating to the weight percentage of ethylene oxide in the molecule, saponification number of the ester linkage and acid value of the "fatty" acid, HLB value may be directly calculated from one of the following equations: for polyhydric fatty acid esters: HLB = 20 (1-S/A) where S = saponification number of the ester and A = acid num ber of the aci d ; and for ethoxylated polyhydric alcohols: HLB = (E + P)/5, where E = weight of percent ethylene oxide and P = weight pigment of polyhydric alcohol. Example 1 Example 1 illustrates the advantages of the compositions of the present invention with respect to UHF Microwave receptivity. Fifteen compositions, 1-15, were produced utilizing the basic formulation set forth in Table 1. Table 1 - Composition Formulation Ingredient Parts by Weight VISTALON7500EPDM 100 Zinc oxide 7.5 Sunpar 2280 oil 75 Sulphur 1.0 Carbon black, CB-1 115 Kezandol GR 5 Chemical Compound Additive Polymer Co p. 1 (Control) = 0 parts by weight Polymer Comp. 2-15 = 3 parts by weight total VISTALON® 7.500 is an EPDM manufactured and sold by EXXON Corporation, Wilmington, Delaware Sunpar 2280 oil is an oil manufactured and sold by Sun Oil Company Kezandol GR is coated calcium oxide (a moisture scavenger) manufactured and sold by Kettlitz, GmbH. Carbon Black CB-1 is a carbon black having an I 2 No. of 43 mg/g and a DBP of 125 cc/lOOg. Composition 1 is a control composition produced without a chemical compound additive. Composition 2 is aLso a control composition produced with a chemical compound falling outside the scope of the present invention. Compositions 3- 15 are examples of compositions of the present invention. The chemical compound additive utilized in compositions 2- 15 arc set forth below in Table 2. Table 2 - Chemical Compound Additive Composition Chemical Compound Description Additive/Amount Utilized 1 None N.A. 2 Sunpar 2280 oil = 3 pbw Sunpar 2280 oil is an oil manufactured and sold by Sun Oil Company 3 A 1 = 3 pbw coconut diethanolamidc HLB 10.2 4 A2 = 3 pbw Sorbitan monolaurate + 20 moles ethylene oxide HLB 16.7 5 A3 = 3 pbw Sorbitan mono-oleate + 20 moles ethylene oxide HLB 15.0 6 A4 = 3 pbw Glycerol ricinoleate + 30 moles ethylene oxide HLB 12 7 A5 = 3 pbw steric acid + 20 moles ethylene oxide HLB 15 8 A6 = 3 pbw cetyl alcohol + 20 moles ethylene oxide HLB 15.7 9 A7 = 3 pbw octyl phenol + 10 moles ethylene oxide HLB 13.6 10 A8 = 3 pbw PEG 40 hydrogenated castor oil HLB 13 11 Al = 1.5 pbw See Above A3 = 1.5 pbw See Above 12 A l = 1.5 pbw See Above A9 = 1.5 pbw See Above 13 Al = 1.5 pbw See Above A4 = 1.5 pbw See Above 14 Al = 1.5 pbw See Above AS = 1.5 pbw See Above 15 Al = 1.5 pbw See Above A 10 = 1.5 pbw tallow amine + 15 moles ethylene oxide HLB 19.2 pbw = parts by weight (see Table 1) The composition ingredients set forth in Tables 1 and 2 above were compounded together using a Banbury mixer with the cooling water set at 40° C, the rotor speed 50 φm and the ram at 1 bar pressure. The mixing cycle was 4 minutes after which the compound was transfered to a rotating cold two roll mill (cooling water temperature 40° C) Once a continuous band of compound had been formed on one of the rotating rolls, cuπng agents MBT (mercaptobenzylthioazole) and TMTD (tetramethylthiuram disulfide), both 75% active, were both added at an amount of 1.07 part by weight based on the above composition. After allowing the cuπng agents to thoroughly mix for a peπod of 8 minutes the compound was removed from the mill in the form of a sheet and allowed to cool. The sheet was cut into small, approximately 50 mm x 50 mm, pieces and fed into a single screw extruder operating with a screw speed of 50 ψm and at heated barrel at 80° C. A die was positioned at the end of the extruder barrel to provide a strand 5mm in diameter. Portions of the extruder strand, 6mm diameter by 40 mm long, were exposed to a 60W microwave source and the rate of temperature change recorded pursuant to the procedures descnbed in detail above The results are presented in Table 3 below. Table 3 Composition Heating rate Time to reach (°C/sec.) 180° C (sec.) 1 7.8 28 2 7.5 28 3 8. 1 23 4 10.8 18 5 10.4 17 6 10.7 18 7 10.7 17 8 10.6 17 9 10.3 18 10 10.0 18 11 10.3 19 12 10.4 18 13 9.5 19 14 10.4 19 15 11 18 These results illustrate that the compositions of the present invention 3- 15, had faster heating rates in compaπson to control compositions 1 and 2 Thus, the compositions of the present invention 3-15 have improved UHF Microwave receptivity in companson to control compositions 1 and 2. The compositions described in the above Tables show enhancement in UHF receptivity of the compounds. This allows for faster heating rates which translate to shorter cuπng cycles. The reduction in cure time can impart significant savings in manufactuπng efficiency Example 2 This example also illustrates the advantages of the compositions of the present invention with respect to UHF Microwave receptivity Twenty-nine compositions, 16-44, were produced utilizing the basic formulation set forth in Table 4 below Table 4 - Composition Formulation Ingredient Parts by Wei ht VISTALON 7500 EPDM 100 Zinc oxide 7.5 Sunpar 2280 oil 75 Sulphur 1.0 Carbon black, CB-2 160 Kezandol GR 5 Chemical Compound Additive Polymer Comp. Polymer Comp. 17-44 = 5 parts by weight total VISTALON® 7.500 is an EPDM manufactured and sold by E.XXON Corporation, Wilmington, Delaware Sunpar 2280 oil is an oil manufactured and sold by Sun Oil Company Kezandol GR is coated calcium oxide (a moisture scavenger) manufactured and sold by Kettlitz, GmBH. Carbon Black CB-2 is a carbon black having an I 2 No. of 18 mg/g and a DBP of 123 cc/lOOg. Polymer composition 16 is a control composition produced without a chemical compound additive. Polymer composition 17 is also a control composition produced with a chemical compound falling outside the scope of the present invention Polymer compositions 18-44 are examples of compositions of the present invention. The chemical compound additives utilized in compositions 17-44 are set forth below in Table 5 Table 5 - Chemical Compound Additives pbw = parts by weight (see Table 4) Table 5 - Chemical Compound Additives (continued) Composition Chemical Compound Description Additive/Amount Utilized 31 A23 = 5 pbw glycerol hydroxystearate + 25 moles ethylene oxide HLB 11 32 A2 = 5 pbw sorbitan monolaurate + 20 moles ethylene oxide HLB 16.7 33 A3 = 5 pbw sorbitan mono-oleate + 20 moles ethylene oxide HLB 15.0 34 A24 = 5 pbw sorbitan trioleate + 20 moles ethylene oxide HLB 11.0 35 A25 = 5 pbw sorbitan monolaurate HLB 8.6 36 A26 = 5 pbw sorbitan mono-oleate HLB 4.3 37 A27 = 5 pbw sorbitan trioleate HLB 1.8 38 A 1 = 5 pbw coconut diethanolamide HLB 10.2 39 A6 = 5 pbw cetyl alcohol + 20 moles ethylene oxide HLB 15.7 40 A5 = 5 pbw Stearic acid + 20 moles ethylene oxide HLB 15 41 A28 = 5 pbw glycerol hydroxy stearate + 25 moles ethylene oxide HLB 11 42 Al l = 5 pbw cetyl alcohol + 2 moles ethylene oxide HLB 5.3 43 A8 = 5 pbw PEG 40 hydrogenated castor oil HLB 13 44 A7 = 5 pbw octyl phenol + 10 moles ethylene oxide HLB 13.6 45 A29 = 5 pbw tallow amine + 11 moles ethylene oxide HLB 16.1 pbw = parts by weight (see Table 4) The composition ingredients set forth in Tables 4 and 5 above were compounded together using a Banbury mixer with the cooling water set at 40° C, the rotor speed 50φm and the ram at 1 bar pressure. The mixing cycle was 4 minutes after which the compound was transfered to a rotating cold two roll mill (cooling water temperature 40° C). Once a continuous band of compound had been formed on one of the rotating rolls, curing agents MBT (mercaptobenzylthioazole) and TMTD (tetramethylthiuram disulfide), both 75% active, were both added at an amount of 1.07 part by weight based on the above composition. After allowing the curing agents to thoroughly mix for a period of 8 minutes the compound was removed from the mill in the form of a sheet and allowed to cool. The sheet was cut into small, approximately 50 mm x 50 mm, pieces and fed into a single screw extruder operating with a screw speed of 50 φm and at heated barrel at 80° C. A die was positioned at the end of the extruder barrel to provide a strand 5 mm in diameter. Portions of the extruder strand, 6mm diameter by 40 mm long, were exposed to a 60W microwave source and the rate of temperature change recorded pursuant to the procedures described in detail above. The results are presented in Table 6 below. Table 6 Composition Heating rate Time to reach 180° C (sec.) CC sec.) 16 1.4 118 17 1.1 1 19 18 3.0 47 19 3.0 44 20 1.7 73 21 3.6 38 22 2.2 53 23 3.4 36 24 3.7 35 25 3.5 36 26 3.3 40 27 3.5 39 28 3. 1 41 29 3.4 38 30 2.2 67 31 3.3 38 32 3.0 43 33 3.2 41 34 2.8 46 35 1.9 64 36 1.7 65 37 1.6 69 38 2. 1 60 39 3.6 38 40 3.3 40 41 3.3 38 42 3.0 44 43 3.0 44 44 2.7 47 45 3.2 43 These results illustrate that the compositions of the present invention 18-45, had faster heating rates in comparison to control compositions 16 and 17. Thus, the compositions of the present invention 18-45 have improved UHF Microwave receptivity in comparison to control compositions 16 and 17. The compositions described in the above tables show enhancement in UHF receptivity of the compounds. This allows for faster heating rates which translate to shorter curing cycles. The reduction in cure time can impart significant savings in manufacturing efficiency. Example 3 This example illustrates the production of compositions of the present invention wherein carbon black is pretreated with the chemical compound additive to form a treated filler material which is combined with a polymer to produce a composition of the present invention. This example also further illustrates the advantages of the compositions of the present invention. Carbon black CB-3, having an I 2 No. of 22 mg/g and a DBP of 95 cc/lOOg was combined with two different amounts of chemical compound additive A3 (sorbitan mono-oleate + 20 moles ethylene oxide, HLB 15.0) to produce an A3 treated carbon black composition comprising 0.7%, by weight A3, and to produce an A3 treated carbon black composition comprising 1.5%, by weight A3. The treated carbon black compositions were produced by combining the CB-3 carbon black, the chemical compound additive (A3) and water in a pin pelletizer of the type described in U.S. Patent No. 3,528,785 to produce wet pellets. The wet pellets were dried in a rotating drum dryer until the moisture content of the pellets was below 0.3%, by weight to produce. A control composition, 46, containing untreated CB-3 carbon black, as a carbon black component, and two compositions of the present invention 47 and 48, containing the treated carbon black were produced utilizing the formulation set forth in Table 7. Composition 47 incorporated the A3 treated carbon black composition comprising 0.7%, by weight A3, as a carbon black component, and Composition 48 incorporated the A3 treated carbon black composition comprising 1.5%, by weight A3, as a carbon black component. Table 7 - Composition Formulation Ingredient Parts by Weight VISTALON 7500 EPDM 100 Zinc oxide 7.5 Sunpar 2280 oil 80 Sulphur 1.0 Kezandol GR 5 Carbon Black Component 175 VISTALON® 7500 is an EPDM manufactured and sold by EXXON Corporation, Wilmington, Delaware Sunpar 2280 oil is an oil manufactured and sold by Sun Oil Company Kezandol GR is coated calcium oxide (a moisture scavenger) manufactured and sold by Kettlitz, GmBH. The composition ingredients set forth in Table 7 above were compounded together using a Banbury mixer with the cooling water set at 40° C, the rotor speed 50 φm and the ram at 1 bar pressure. The mixing cycle was 4 minutes after which the compound was transfered to a rotating cold two roll mill (cooling water temperature 40° C). Once a continuous band of compound had been formed on one of the rotating rolls, curing agents .MBT (mercaptobenzylthioazole) and TlvfTD (tetramethylthiuram disulfide), both 75% active, were both added at an amount of 1.07 part by weight based on the above composition. After allowing the curing agents to thoroughly mix for a period of 8 minutes the compound was removed from the mill in the form of a sheet and allowed to cool. The sheet was cut into small, approximately 50 mm x 50 mm, pieces and fed into a single screw extruder operating with a screw speed of .50 φ and at heated barrel at 80° C. A die was positioned at the end of the extruder barrel to provide a strand 5mm in diameter. Portions of the extruder strand, 6mm diameter by 40 mm long, were exposed to a 60W microwave source and the rate of temperature change recorded pursuant to the procedures described in detail above. The results are presented in Table 8 below. Table 8 Composition Heating rate Time to reach 180° C (°C/sec.) (sec.) 46 2.8 63 47 5.0 34 48 5.2 35 These results illustrate that the compositions of the present invention 47 and 48, had faster heating rates in comparison to control composition 46. Thus, the compositions of the present invention 47 and 48 have improved UHF Microwave receptivity in comparison to control compositions 46. Thus, these results illustrate that the advantages of the compositions of the present invention may be achieved when the chemical compound additive is precombined with the carbon black. It should be clearly understood that the forms of the present invention herein described are illustrative only and are not intended to limit the scope of the invention.

Claims: CLAIMS A composition comprising: an ethylene containing polymer; 50 to 250 parts by weight a filler material, per 100 parts by weight ethylene containing polymer (50 to 250 phr); and 0.05 to 50 parts by weight a chemical compound per 100 parts by weight ethylene containing polymer (0.05 to 50 phr) having the structure A-B- [(C) y ] x -D wherein: A comprises one or more of the following: hydrogen, an alkyl group, an aryl group; or an alkyl aryl group; B is a bridging group between A and C comprising one or more of the following: ether, a carboxylic acid, a 1,2-dicarboxylic acid derived from an anhydride, an amine, an amide, a sulfate, a sulphonate, a phosphate, a phosphate, or a carboxylic ester of a polyhydric alcohol containing 2 to 6 hydroxyl groups; C comprises an ethylene oxide repeating unit; D comprises one or more the following: hydrogen, an alkyl group, an alkali or an alkaline earth metal; y is 0 to 200 and x = 1, 2, 3, 4 or 5. 2. The composition of claim 1 wherein the ethylene containing polymer comprises an ethylene-propylene copolymer or an ethylene-propylene terpolymer. 3. The composition of claim 3 wherein the ethylene containing polymer is ethylene propylene diene monomer (EPDM) . 4. The composition of claim 1 wherein the filler material comprises: carbon black, graphite or a metal oxides. 5. The composition of claim 4 wherein the filler material comprises carbon black. 6. The composition of claim 5 wherein the chemical compound comprises: a fatty alcohol ethoxylates, a fatty acid ethoxylates, a fatty amine ethoxylates, a fatty amide ethoxylates, a glycerol and a sorbitan ester ethoxylates. 7. The composition of claim 5 wherein the carbon black has an I 2 No. of 10-70 mg/g and a DBP of 30-150 cc/ lOOg. 8. The composition of claim 1 further comprising: a coagent, a processing additive, a hydrocarbon oil, a stabilizer, an accelerator, an antioxidant, vinyl silane, a curing agent or mixtures thereof. 9. An article of manufacture formed from the composition of claim 1. 10. An article of manufacture formed from composition of claim 3. 11. The article of manufacture of claim 9 wherein the article comprises a hose. 12. The article of manufacture of claim 9 wherein the article comprises an extruded article comprising: a profile, a tube, a tape or a film. 13. The article of manufacture of claim 9 wherein the article comprises a molded article.

Inventors: AL THEO, LONGUET MICHEL, SMITH MICHAEL, WHITEHOUSE ROBERT S, AL, THEO, LONGUET, MICHEL, SMITH, MICHAEL, WHITEHOUSE, ROBERT, S.
Applicants: CABOT CORP, CABOT CORPORATION
Application year: 1997
Main classification: C08K3
IPC codes: C08J5, C08K3, C08K5, C08K9, C08L23