TILED RETROREFLECTIVE SHEETING COMPOSED OF HIGHLY CANTED CUBE CORNER ELEMENTS

Abstract: A retroreflective sheeting includes a first array of cube corner element opposing pairs and a second array of cube corner element opposing pairs. The symmetry axes of the cube corner elements in the first and second arrays are tilted in a backward direction at an angle of about 12 DEG to about 30 DEG from an axis normal to a base surface. The second array of cube corner elements is oriented approximately perpendicular to the first array to yield a retroreflective article providing generally uniform total light return about a 360 DEG range of orientation angles and/or a minimum total light return of about 5 % across such 360 DEG range. Also disclosed is a mold assembly suitable for use in forming the present retroreflective sheeting and a method of making a retroreflective article using the mold.

Description: TILED RETROREFLECTIVE SHEETING COMPOSED OF HIGHLY CANTED CUBE CORNER ELEMENTS Field of the Invention The present invention relates generally to cube corner retroreflective sheeting that is capable of returning a significant percentage of incident light at relatively high entrance angles regardless of the rotational orientation of the sheeting about an axis perpendicular to its major surface. Background of the Invention Retroreflective materials are characterized by redirecting incident light back toward the originating light source. This property has led to the wide-spread use of retroreflective sheeting in a variety of conspicuity applications. Retroreflective sheeting is commonly applied to flat, rigid articles such as, for example, road signs and barricades to improve their conspicuity in poor lighting conditions. Retroreflective sheeting is also used on irregular or flexible surfaces. For example, retroreflective sheeting can be adhered to the side of a truck trailer, which requires the sheeting to cover corrugations and protruding rivets, or the sheeting can be adhered to a flexible body portion such as a road worker's safety vest or other such safety garment. Many conspicuity applications are governed by specific performance standards for retroreflective sheeting. Manufacturers must demonstrate that their retroreflective sheeting is capable of meeting the relevant performance standards to be considered as a supplier in the marketplace. A body of standards exists both for describing retroreflection (see ASTM Designation E808-93b, Standard Practice for Describing Retroreflection) and for measuring retroreflectors, (see ASTM Designation E809-94a, Standard Practice for Measuring Photometric Characteristics of Retroreflectors). Two known types of retroreflective sheeting are microsphere-based sheeting and cube corner sheeting. Microsphere-based sheeting, sometimes referred to as "beaded" sheeting, employs a multitude of micro spheres typically at least partially embedded in a binder layer and having associated specular or diffuse reflecting materials (e.g., pigment particles, metal flakes or vapor coats, etc.) to retroreflect incident light. Illustrative examples are disclosed in U.S. Patent Nos. 3,190,178 (McKenzie), 4,025,159 (McGrath), and 5,066,098 (Kult). Due to the symmetry of beaded retroreflectors, microsphere-based sheeting exhibits relatively uniform entrance angularity when rotated about an axis normal to the surface of the sheeting. Therefore, the retroreflective performance of beaded sheeting is relatively insensitive to the orientation at which the sheeting is placed on the surface of an object. In general, however, microsphere-based sheeting exhibits relatively low retroreflective efficiency. Beaded retroreflective sheeting typically exhibits a total light return of approximately 5% to 15% in an observation cone angled about 2°. Cube corner retroreflective sheeting comprises a body portion typically having a substantially planar base surface and a structured surface comprising a plurality of cube corner elements opposite the base surface. Each cube corner element comprises three mutually substantially perpendicular optical faces that typically intersect at a single reference point, or apex. The base of the cube corner element acts as an aperture through which light is transmitted into the cube corner element. In use, light incident on the base surface of the sheeting is refracted at the base surface of the sheeting, transmitted through the respective bases of the cube corner elements disposed on the sheeting, reflected from each of the three perpendicular cube corner optical faces, and redirected toward the light source. One aspect of many performance standards requires retoreflective sheeting to return specified percentages of light incident on the face of the sheeting at various entrance angles. The total light return characteristic of a retroreflective sheeting as a function of the entrance angle of incident light is generally referred to in the art as the 'entrance angularity' of the sheeting. A retroreflective sheeting capable of returning a significant percentage of light incident at relatively high entrance angles can be characterized as having strong or wide entrance angularity, such as disclosed in the isobrightness curves in U.S. Pat. No. 4,588,258 (Hoopman). By contrast, retroreflective sheeting with poor entrance angularity loses its retroreflective brightness (total light return decreases) rapidly as the angle of incidence deviates from 0°. Moreover, entrance angularity typically varies about a 360° range of orientation angles (orientational uniformity), requiring proper alignment of the retroreflective sheeting for each application. The entrance angularity and orientational uniformity of a retroreflective sheeting is a significant performance factor because it materially affects the ability of a driver to see an object such as a traffic sign or a safety barrier in poor lighting conditions at various orientations. The symmetry axis, also called the optical axis, of a cube comer element is the axis that forms an equal angle with the three optical surfaces of the cube comer element. Cube comer elements typically exhibit the highest optical efficiency in response to light incident on the base of the element roughly along the optical axis. The amount of light retroreflected by a cube corner retroreflector drops as the incidence angle deviates from the optical axis. Cube comer elements offer the advantage of being significantly more efficient retroreflectors than beads. The terms 'active area' and 'effective aperture' are used in the cube comer arts to characterize the portion of a cube comer element that retroreflects light incident on the base of the element. A detailed teaching regarding the determination of the active aperture for a cube comer element design is beyond the scope of the present disclosure. One procedure for determining the effective aperture of a cube comer geometry is presented in Eckhardt, Applied Optics, v. 10, n. 7, July, 1971, pp. 1559-1566. U.S. Pat. No. 835,648 (Straubel) also discusses the concept of effective aperture. At a given incidence angle, the active area can be determined by the topological intersection of the projection of the three cube comer faces onto a plane normal to the refracted incident light with the projection of the image surfaces for the third reflections onto the same plane. The term 'percent active area' is then defined as the active area divided by the total area of the projection of the cube comer faces. The retroreflective efficiency of retroreflective sheeting is directly proportional to this percent active area. The maximum theoretical total light return of truncated cube comer elements commonly used in retroreflective sheeting is approximately 67%, while in practice cube corner retroreflective sheeting exhibits a maximum total light retum of approximately 35%, due to sealing, front surface losses, and reflection losses at the cube faces. Predicted total light retum (TLR) for a cube comer matched pair array can be calculated from a knowledge of percent active area and ray intensity. Ray intensity can be reduced by front surface losses and by reflection from each of the three cube comer surfaces for a retroreflected ray. Total light retum is defined as the product of percent active area and ray intensity, or a percentage of the total incident light which is retroreflected. A discussion of total light retum for directly machined cube comer arrays is presented in U.S. Patent No. 3,712,706 (Stamm). The light retum profile of the basic cube comer element is inherently asymmetric in nature. The breakdown of total internal reflection (TLR) is the most significant cause of this asymmetry in non-metallized cube comer retroreflectors. Coating the reflecting faces with a specular reflector substantially reduces the asymmetry in the reflection pattern. Metallized cube comer arrays, however, are typically not white enough for daytime viewing, such as on signing applications. The durability of the specular vapor coat may also be inadequate. Finally, a portion of the asymmetry is due in part to the asymmetric physical geometry of a cube comer element. See Rityan, Optics of Comer Cube Reflectors, Soviet Journal of Optics Technology, v. 34, p. 195 (1967). Retroreflective sheeting formed from cube comer elements exhibits a corresponding asymmetry in its light return profile. By way of example, U.S. Pat. No. 3,712,706 to Stamm ('706 patent) discloses the three-lobed light return profile characteristic of a single cube comer element. Similarly, U.S. Pats. No. 4,202,600 (Burke) and 4,243,618 (Van Arnam) disclose an array of cube comer elements having a plurality of zones with different angular orientations, such that the total light return retroreflected by cube comer retroreflective sheeting varies as a function of the entrance angle of the incident light and the orientation angle of the sheeting on the substrate. The six-lobed light retum profile of Burke and Van Arnam is characteristic of a matched pair of cube corner elements. One approach to reducing the asymmetry of retroreflective sheeting is by providing a retroreflective sheeting construction with a plurality of discrete cube comer arrays disposed at different orientations; a technique referred to in the art as 'tiling'. Burke and Van Arnam patents disclose retroreflective sheeting having arrays of conventional tmncated cube comer elements with equilateral base triangles tiled in a variety of different orientations on the surface of the sheeting. While the constructions suggested in these references address the issue of asymmetry, the cube comer geometries disclosed in these references suffer a rapid decline in total light retum at entrance angles greater than about 40°, since only a small portion of the cubes are optically functional at a particular orientation. Therefore, retroreflective sheeting in accordance with these references do not provide adequate total light retum at high entrance angles for many applications. Another approach to accommodating this variation in entrance angularity is to design retroreflective sheeting to have specific planes of improved entrance angularity. By way of example, the Hoopman patent discloses a retroreflective sheeting wherein the cube comer elements are arranged in opposing matched pairs having their respective symmetry axes tilted toward one another. This geometry results in a retroreflective sheeting with improved entrance angularity in a plane substantially coincident with the plane that contains the symmetry axes of the cube comer elements, identified as the X-axis plane, and also in a Y-axis plane perpendicular to the X-axis plane. In use, the sheeting is preferentially oriented on the substrate such that these planes coincide with the planes in which light will become incident on the sheeting. By way of example, a preferred orientation for the sheeting on a road sign is to align the X-axis plane substantially parallel with the ground. U.S. Patent No. 5,565,151 (Nilsen) discloses matched pairs of retroreflective cube comer elements that are tilted or canted between more than 1.0 degree and less than about 7.0 degrees in a negative direction. A section of one of the cube comer elements in the matched pair is removed, creating a smaller element which produces increased observation angle performance. U.S. Patent Application Serial No. 08/5887,719 (Nestegard et al.), entitled Dual Orientation Retroreflective Sheeting, discloses a retroreflective sheeting with alternating zones of cube corner arrays oriented such that their primary planes of entrance angularity are approximately perpendicular to one another. Thus, there is a need in the art for a retroreflective sheeting that maintains a visibly useful total light retum across a 360° range of orientation angles, particularly at entrance angles greater than about 40°. Additionally, there is a need in the art for a retroreflective sheeting having relatively small variations in total light retum across a 360° range of orientation angles at higher entrance angles and particularly at entrance angles greater than about 40°. Brief Summary of the Invention Preferred cube comer retroreflective sheeting disclosed herein includes highly canted cube comer elements tiled in two approximately perpendicular orientations such that the sheeting maintains a visibly useful total light retum at all orientation angles for entrance angles about 40°, and more preferably about 50° and most preferably about 60°. Thus, a cube comer retroreflective sheeting is disclosed that is relatively less sensitive to orientation when compared with existing cube comer retroreflective sheeting constructions. The preferred retroreflective sheeting maintains visibly useful total light retum performance at high entrance angles while maintaining high total light retum at lower entrance angles. The retroreflective article comprises a substrate having a base surface and a structured surface having a plurality of arrays of cube corner elements opposite the base surface. The arrays of cube comer elements comprise a first array of cube comer element opposing pairs and a second array of cube comer element opposing pairs. The symmetry axes of the cube comer elements in the first array are tilted in a backward direction at an angle measuring between about 12° and about 30° from an axis normal to the base surface. The symmetry axes of the cube comer elements in the second array are likewise tilted in a backward direction by an angle measuring between about 12° and about 30° from an axis normal to the base surface. The second array of cube comer elements are oriented approximately perpendicular to the first array so that the retroreflective article provides a minimum total light retum of about 5% across about a 360° range of orientation angles at an entrance angle of about 40°. In an alternate embodiment, the symmetry axes of the cube comer elements in the first array are tilted in a backward direction at an angle measuring between about 12° and about 30° from an axis normal to the base surface. The symmetry axes of the cube comer elements in the second array are likewise tilted in a backward direction by an angle measuring between about 12° and about 30° from an axis normal to the base surface. The second array of cube comer elements are oriented approximately perpendicular to the first array so that the retroreflective article provides generally uniform total light retum about a 360° range of orientation angles. In another embodiment, the cube comer elements in the first and second arrays are tilted in a backward direction at an angle measuring between about 15.1° and about 30°. The first array and the second array occupy roughly equal portions of the structured surface of the retroreflective article. The cube comer elements are generally trihedral structures comprising three mutually perpendicular triangular optical faces that intersect at a peak and a triangular base. The triangular base for truncated cube comer elements is approximately coplanar with the base surface of the article. Alternatively, the cube corner elements can be "full cubes," e.g. generally polygonal structures comprising three mutually perpendicular optical faces including two tetragonal optical faces and a third optical face that intersect at a peak, and a tetragonal base. The symmetry axes of the cube comer elements in the arrays are more preferably tilted in a backward direction at an angle measuring between about 14° and about 20° from an axis normal to the base surface. The symmetry axes of the cube comer elements in the first and second arrays can be tilted the same or a different amount. The second array is preferably oriented at an angle between about 85°and about 95° relative to the first array, and most preferably at about 90E. The retroreflective article exhibits a maximum theoretical total light retum of approximately 100% percent in response to light incident on the article along an axis normal to the base surface of the article. The retroreflective article is preferably capable of a minimum total light retum of about 5%, and more preferably 10%, across about a 360° range of orientation angles at an entrance angle of about 40°, and more preferably at an entrance angle of about 50° and most preferably at an entrance angle of about 60°. The cube corner element opposing pairs may or may not be physically adjacent to each other, and can have the same or different retroreflection pattern. In one embodiment, the cube comer element opposing pairs are matched pairs that generate mirror image retroreflection patterns, such as elements that are substantially identical but are rotated 180° relative to each other. Retroreflection patterns and reflection patterns refer to the configuration of reflected light, typically illustrated as isobrightness contours. The substrate and the cube comer elements are preferably formed as a unitary article from a light transmissible material having a refractive index of between 1.3 and 1.7. In one embodiment, the body layer of the retroreflective article comprises a light transmissible polymeric material having an elastic modulus less than about 7xl0 8 pascals, and the cube comer elements are formed from a light transmissible material having an elastic modulus greater than about 16xl0 8 pascals. The cube comer elements can incorporate minor deviations from perfect orthogonality to thereby alter the light distribution in the emerging cone of retroreflected light. The first and second arrays of cube comer elements can be coated with a specularly reflective substance. A sealing medium can be disposed adjacent to the first and second arrays of cube corner elements. The sealing medium is preferably bonded to the structured surface by a network of intersecting bonds that define a plurality of cells within which the cube comer elements are hermetically sealed. The sealing medium maintains an air interface with the structured surface such that the cube comer elements retroreflect according to the principles of total internal reflection. A preferred mold assembly suitable for use in forming the retroreflective sheeting and a method of making a retroreflective article using the mold are also disclosed. The mold assembly includes a substrate having a base surface and a mold surface opposite the base surface. The mold surface includes in roughly equal proportions a first and a second array of cube comer element opposing pairs. The symmetry axes of the cube comer elements in the array are preferably tilted in a backward direction at an angle of between 15.1° and 30° from an axis normal to the base surface. The second array of cube comer elements is oriented approximately perpendicular to the first array. In an alternate embodiment, the first and second arrays of cube comer element opposing pairs are tilted by an angle of between about 15.1° and about 20°. The method of making a retroreflective article includes forming a replica of the mold. The replica of the mold includes a mold surface having a negative image of the mold. A retroreflective article is formed in the mold surface of the replica. Brief Description of the Drawings Fig. 1 A is a plan view of a portion of a retroreflective sheeting in accordance with a preferred embodiment of the invention. Fig. IB is a side view of a portion of the structured surface of the sheeting of Fig. 1, taken along lines I-I. Fig. 2 is a polar plot of the isobrightness contours of retroreflected light for a single array of the cube comer sheeting of Fig. 1 prior to tiling. Fig. 3 is a polar plot of the isobrightness contours of retroreflected light for the cube comer sheeting of Fig. 1. Fig. 4 is a plan view of a mold for forming retroreflective sheeting. Fig. 5 is a plan view of the mold of Fig. 4 for forming retroreflective sheeting according to an embodiment of the invention. Fig. 6 is a polar plot of the isobrightness contours of retroreflected light for cube comer sheeting formed from the mold of Fig. 5. Fig. 7 is a polar plot of the isobrightness contours of retroreflected light for cube comer sheeting formed from the mold of Fig. 5 arranged in a plurality of generally orthogonal arrays. Fig. 8 is a perspective view of an alternate embodiment of a cube comer element. Fig. 9 is a top plan view of the cube comer element of Fig. 8. Fig. 10 is a side view of a mold for forming retroreflective sheeting utilizing the lamina of Fig. 8 Fig. 11 is a polar plot of the isobrightness contours of retroreflected light for cube comer elements tilted at 14° formed from the mold of Fig. 10. Fig. 12 is a polar plot of the isobrightness contours of retroreflected light for cube comer elements tilted at 14° formed from the mold of Fig. 10 and arranged in a plurality of generally orthogonal arrays. Fig. 13 is a polar plot of the isobrightness contours of retroreflected light for cube corner elements tilted at 20° formed from the mold of Fig. 10. Fig. 14 is a polar plot of the isobrightness contours of retroreflected light for cube comer elements tilted at 20° formed from the mold of Fig. 10 and arranged in a plurality of generally orthogonal arrays. Detailed Description of the Preferred Embodiments Preferred cube comer retroreflective sheeting disclosed herein is capable of returning a significant percentage of incident light at relatively high entrance angles at all rotational orientations of the sheeting about an axis perpendicular to its major surface. The retroreflective sheeting comprises a first array of cube comer element matched pairs and a second array of cube comer element matched pairs. The symmetry axes of the cube comer elements in the arrays are tilted in a backward direction at an angle measuring between about 12° and about 30° from an axis normal to the base surface. The first array of cube co er elements is oriented approximately perpendicular to the second array. Also disclosed is a retroreflective article, preferably a retroreflective sheeting that maintains a visibly useful total light retum at all orientation angles for entrance angles up to 40°, and more preferably up to 50° or 60°. The structured surface of the sheeting requires as few as two zones of cube comer element arrays preferably tiled along two orthogonal axes to accomplish this optical objective, thereby substantially reducing the effort and expense required to scale-up production for such a sheeting. Each zone includes an array of optically opposing cube comer retroreflective elements in which the optical axes are canted or tilted in a backward, or negative, direction by an angle between about 12° and about 30°, from an axis normal to the base surface of the sheeting, and more preferably between about 14° and about 20°. In describing preferred embodiments of the invention, specific terminology will be used for the sake of clarity. However, the invention is not to be limited to the specific terms so selected. It is to be understood that each term so selected includes all technical equivalents that operate similarly. Additionally, while the present application discloses several embodiments of cube comer element geometries, a wide variety of cube comer geometries, such as full cubes and tmncated cubes, can also be used. The base edges of adjacent tmncated cube comer elements in an array are typically coplanar. The base edges of adjacent full cube comer elements in an array are not all in the same plane. One of ordinary skill in the optical arts will understand that varying degrees of canting and varying cube sizes can be used within the scope of the present disclosure. Insubstantial changes in cube geometries calculated to yield substantially the same optical results should also be considered within the scope of the present application. Retroreflective element opposing pairs refers generally to two cube comer elements that generate opposing, although not necessarily identical, retroreflection patterns. The cube corner elements are not necessarily physically adjacent to each other. It is possible for opposing pairs to be physically separated on the retroreflective article. Matched pairs generally refers to opposing pairs of cube comer elements that generate mirror image retroreflection patterns, such as elements that are substantially identical but are rotated 180° relative to each other. Matched pairs are typically physically adjacent to each other. Tiling the structured surface of the sheeting such that the cube comer arrays in the first zone are oriented about 75° to about 105°, and more preferably about 85° to about 95°, and more preferably about 90° to the cube co er arrays in the second plane provides a sheeting that maintains a visible total light retum (TLR) at all orientation angles for entrance angles of up to 70°. Generally uniform total light retum about a 360° range of orientation angles refers to a nrinirnurn total light retum of about 5%, and more preferably a minimum of about 10%, at an entrance angle of about 40°, and more preferably up to about 50° and most preferably about 60°. Additionally, when the structured surface is composed of cube comer elements whose optical axes are canted within preferred angular ranges, the sheeting exhibits relatively small variations in theoretical total light retum across a 360° range of orientation angles, even at relatively high entrance angles. Thus, the sheeting is less sensitive to orientation than existing retroreflective sheeting, while maintaining high levels of TLR at high entrance angles. A variety of methods are available for arranging the cube comer elements into two generally orthogonal zones. Related U.S. Patent Applications filed on the same date herewith include: Cube Corner Sheeting Mold and Method Making the Same (Atty. Docket No. 51946USA9A); Retroreflective Cube Comer Sheeting Mold and Sheeting Formed Therefrom (Atty. Docket No. 53305USA5A); Retroreflective Cube Comer Sheeting, Molds Therefore, and Methods of Making the Same (Atty. Docket No. 53318USA8A); Retroreflective Cube Comer Sheeting Mold and Method for Making the Same (Atty. Docket No. 51952USA6A); and Dual Orientation Retroreflective Sheeting (Atty. Docket No. 52303USA8B). Fig. 1 A depicts a magnified view of a portion of the structured surface of a preferred retroreflective sheeting 20. The structured surface includes a plurality of alternating zones 26, 28 which comprise two generally orthogonal arrays of highly canted cube comer elements 22. The cube comer elements 22 depicted in Fig. 1 A are commonly referred to in the art as tmncated cube co er elements, although full cube comer elements can also be used as will be discussed below. As shown, the cube comer elements 22 are disposed as optically opposing matched pairs in the zones 26, 28 on one side of the sheeting. Each cube comer element 22 has the shape of a trihedral prism with three exposed planar faces 24. The dihedral angle between the cube comer element faces 24 typically is the same for each cube comer element in the array and measures about 90°. The angle, however, can deviate slightly from 90° as is taught in U.S. Patent No. 4,775,219 to Appledorn et al. The structured surface of sheeting 20 comprises a plurality of alternating zones 26, 28 of cube comer arrays disposed at approximately ninety degree orientations. The sheeting 20 preferably includes, in a repeating pattern, a first zone 26 including an array of cube comer elements 22 disposed in a first orientation and a second zone 28 of cube comer elements disposed in a second orientation. A suitable method for strip-tiling retroreflective sheeting is disclosed in U.S. Patent Serial No. 08/587,719 (Nestegard et al.) entitled Dual Orientation Retroreflective Sheeting. Alternatively, the sheeting 20 can be formed by a wide variety of tiling schemes that provide the first zone 26 generally perpendicular to the second zones 28. The tiling schemes preferably rninimizes the number of deformed or otherwise optically inoperative cube comer elements. Although the first zone 26 includes an array of cube comer elements 22 formed by three mutually intersecting sets of grooves, cube comer elements can be formed with two groove sets, such as disclosed in Retroreflective Cube Comer Sheeting Mold and Method for Making the Same (Atty. Docket No. 51952USA6A). The individual cube comer elements 22 in the array define base triangle included angles of 72.60°, 72.60°, and 34.80°. Further, the cube comer elements have a height of about 10 microns to about 1000 microns. Second zone 28 extends substantially parallel to first zone 26 along the length of sheeting and includes an array of cube comer elements 22 substantially identical to the array disposed in first zone 26, however the array in the second zone is disposed at about a ninety degree orientation relative to the array in first zone 26. As best seen in Fig. IB, the symmetry axes 50 of opposing cube comer elements 22 are canted or tilted in a backward, or negative, direction by an angle that measures between about 12° and about 30°, from an axis 52 normal to the base surface 54 of the sheeting, and more preferably between about 14° and about 20°. This degree of canting provides a cube comer element with one primary plane of entrance angularity. The axes are canted in a direction commonly referred to in the art as a 'backward' or 'negative' direction as discussed in U.S. Pat. No. 5,565,151(Nilsen). This is to be distinguished from canting in a 'forward', or 'positive' direction as disclosed in U.S. Pat. No. 4,588,258 (Hoopman). Backward canted cube comer elements can also be characterized in that only one included angle of the cube comer element base triangle is less than 60°. The other two included angles measure at least 60°. By contrast, forward canted cubes can be characterized in that two of the included angles of the base triangle are less than 60° and a single base triangle included angle measures greater than 60°. It will be understood that the particular geometry discussed herein relate to preferred embodiments. One of ordinary skill will understand that varying degrees of canting and varying cube sizes can also be used. The sheeting 20 can include a separate body layer 56 that includes a light transmissible polymeric material formed from a light transmissible material having an elastic modulus less than about 7x10 8 pascals. The cube comer elements 22 can then be formed from a different light transmissible material having an elastic modulus greater than about 16xl0 8 pascals. The cube comer elements 22 preferably are constructed from a thermoplastic or thermoset polymer. The polymeric body layer 56 is preferably constructed from a thermoformable polymer. The body layer can be selected from the group consisting of: ionomeric ethylene copolymers, plasticized vinyl halide polymers, acid-functional ethylene copolymers, aliphatic polyurethanes, aromatic polyurethanes, other light transmissive elastomers, and combinations thereof. The cube comer elements 22 can be selected from the group consisting of monofunctional, difunctional, and polyfunctional acrylates or combinations thereof. A specular reflector can be applied to the entire surface of the retroreflective sheeting 20 or along selected zones thereof. Fig. 2 is an isobrightness contour depicting the total light retum profile of an array of tmncated cube comer elements as illustrated in zone 26 of the retroreflective sheeting of Fig. 1A. The tmncated cube comer elements were canted 17° in a backward direction formed from a material having in index of refraction of 1.59. The highly canted cube comer elements 22 of the first zone 26 provide one primary plane of entrance angularity. As used herein, isobrightness contours plot the total light retum obtained from cube comer elements. The concentric isobrightness curves represent the predicted total light retum as a percentage of the light incident on the base surfaces of the cube comer elements at various combinations of entrance angles and orientation angles. Radial movement from the center of the plot represents increasing entrance angles, while circumferential movement represents changing the orientation of the cube comer element with respect to the light source. The maximum retroreflectance is represented by the center point on the graph and concentric isobrightness contours representing five percent reductions in retroreflectance relative to the maximum, measured in total light return, are plotted. Fig. 3 is an isobrightness contour depicting the total light retum profile of retroreflective sheeting 20 having a stmctured surface comprising tmncated cube comer elements 22 canted 17° in a backward direction, tiled in accordance with the embodiment depicted in Fig. 1, and formed from a material having an index of refraction of 1.59. Table 1 contains the data presented graphically in Fig. 3 for such retroreflective sheeting. The rotational orientation data of Table 1 is limited to 0 to 90°, rather than a full 360°, since the pattern repeats every 90°. The total light retum data for Table 1 does not include losses due to sealing, reflective coatings, etc. Zero degree orientation in Table 1 corresponds to the positive y-axis 58. Table 1 Oϊ Figs. 4-5 illustrate a preferred method of forming highly canted tmncated cube comer elements on a plurality of laminae 90, such as disclosed in a U.S. Patent Application entitled Retroreflective Cube Comer Sheeting, Molds Therefore, and Methods of Making the Same (Atty. Docket No. 53318USA8A). First, second and third groove sets 30, 38, 46, respectively, form a plurality of fully formed tmncated cube co er elements 80a, 80b on the working surfaces of the plurality of laminae 90. The cube comer elements 80a, 80b preferably extend across at least a portion of several laminae. Altering the location and groove angles of the grooves 46 of the third groove set permits the manufacture of varying cube comer element geometries. In the disclosed embodiment, cube comer elements 80a and 80b are substantially identical in shape and size, but are disposed at 180° orientations relative to one another. Cube comer elements 80a have three mutually peφendicular optical faces: two optical faces formed by faces 62 and 66, and a third optical face 86 corresponding to one surface of the third groove 46. The bottom edges of faces 62, 66 and 86 define base triangles having included angles βi, β 2 , and β . Optical faces 62, 66 and 86 mutually intersect at a cube comer element peak 88. Alternatively, the faces 62, 66, 86 do not necessarily need to intersect in a peak. Rather, a plateau or flat region can be formed that permits light to be transmitted through the retroreflective sheeting. Cube comer elements 80b have three mutually perpendicular optical faces: two optical faces formed by surfaces 68 and 72, and a third optical face 82 corresponding to the opposite side of the third groove 46. The bottom edges of faces 68, 72 and 82 define base triangles having included angles βi, β 2 , and β 3 . Optical faces 68, 72 and 82 mutually intersect at a cube comer element peak 84. In the embodiment described herein, base angle βi measures 33.06°, base angle β 2 measures 73.47° and base angle β 3 measures 73.47°. Cube comer elements with non-equilateral base triangles are commonly referred to in the cube comer arts as 'canted' cube corner elements. Canting cube comer elements either backward or forward enhances entrance angularity. Canting the cube comers in the backward direction elongates optical faces 62, 66 and reduces base angle βi. Additionally, canting cube comer elements 80 in the backward direction improves the entrance angularity performance of the cube comer elements 80 in a plane substantially parallel with common edges 64 and 70, especially for canting greater than about 12°. As will be discussed below, the more optically active portions of the cube comer elements 80 are generally concentrated along selected laminae. This property has utility in retroreflective sheeting applications designed to retroreflect light incident on the sheeting at high entrance angles. Altematively, the base angles βi, β 2 and β 3 can all be different (scalene triangles), such as disclosed in WO 96/42024 (Smith et al.). Additionally, the best planes of entrance angularity are not necessarily in the direction of cant, such as disclosed in WO 96/42025 (Smith et al.). The cube comer elements are shaded to illustrate the more optically active portions 89 of the cube comer elements at an entrance angle from about 0° to about 45°. The more optically active portions 89 of the cube comer elements (cube comer element segments) are concentrated adjacent to the third groove 46, while the less optically active portions 91 of the cube comer elements are displaced from third groove 46. The portion of a cube comer element on a single lamina that has three mutually peφendicular optical faces is referred to as a cube comer element segment. The portions of the cube comer elements removed typically do not have three mutually peφendicular optical faces, and consequently, are not cube comer element segments. The density of the more optically active cube comer element segments are concentrated to provide enhanced optical properties. The more optically active portions 89 can include less optically active regions 87 located near the angles β 2 , β 3 . A relatively small portion of the cube comer elements 80a, 80b depicted in Fig. 4 are optically active. As the entrance angle decreases toward zero, the area of the more optically active portions 89 and the effective aperture of that region decreases. At some point, the effective aperture becomes a slit, diffracting light leaving the retroreflective article primarily in a plane containing the optical axis of the cube comer element and peφendicular to the slit. The diffraction within the slit aperture directs the reflected light primarily in one plane and degrades uniformity of the divergence profile of the retroreflected light, as discussed in ASTM E808-94. Fig. 5 presents a top plan view of a plurality of optically opposing cube comer element segments formed by removing a plurality of laminae (90c and 90f) from the assembly depicted in Fig. 4. All of the laminae may or may not be the same thickness. In an alternate embodiment, the laminae 90c, 90f can be contiguous with one of the adjacent laminae, for example 90b and 90e, respectively. The portion of such contiguous laminae corresponding to 90c and 90f can then be removed by machining. In one preferred embodiment, the plurality of cube comer element segments depicted in Fig. 5 results from removing from the assembly those laminae which have the less optically active portions of the cube comer element segments disposed on their respective working surfaces. The laminae removed from the assembly 90c, 90f are referred to herein as sacrificial laminae. The sacrificial laminae are removed from the assembly and the remaining laminae are reassembled in a suitable fixture to provide a stmctured surface comprising a plurality of cube comer element segments that correspond to the more optically active portions of the fully formed cube comer elements formed in the working surfaces of the plurality of laminae in the original assembly. Because the less optically active portions of the cube comer element segments are removed, a retroreflector formed as a replica of this mold can exhibit substantially higher retroreflective efficiency than the retroreflector formed as a replica of the surface of the original assembly across a wide range of entrance angles. The laminae 90c, 90f can optionally be removed from the assembly prior to forming the third groove set 46. Formation of retroreflective sheeting from the mold of Fig. 5 is discussed below. The optically active portions 89 of Figs. 4 and 5 illustrate a plurality of cube comer element matched pairs. It will be understood that the laminae 90 can be arranged in a variety of configurations. For example, the laminae 90b, 90e, 90h can be grouped together in a first sub-array and the laminae 90a, 90d, 90g grouped together in a second sub-array, physically separated from the first sub-array. The cube comer elements on the laminae 90b, 90e, 90h can be optically opposing to the cube comer elements 90a, 90d, 90g, without being physically adjacent. Retroreflective sheeting constmcted as discussed above would preferably include four sub-arrays. Fig. 6 is an isobrightness contour depicting the total light retum profile of retroreflective sheeting having a stmctured surface comprising cube comer elements according to Figs. 4 and 5 canted at 18° in a backward direction formed from a material having an index of refraction of 1.59. Again, the preferred highly canted cube comer elements provide one primary plane of entrance angularity. Fig. 7 is an isobrightness contour depicting the total light retum profile of retroreflective sheeting having a stmctured surface comprising cube comer element segments of Fig. 5 canted 18° in a backward direction, tiled in accordance with the embodiment depicted in Fig. 1, and formed from a material having an index of refraction of 1.59. Table 2 below, arranged in the same format as Table 1, contains the data presented graphically in Fig. 7. The rotational orientation data of Table 2 is limited to 0 to 90°, rather than a full 360°, since the pattern repeats every 90°. The total light retum data for Table 2 does not include losses due to sealing, reflective coatings, etc. Zero degree orientation in Table 2 corresponds to the positive y-axis 58. Table 2 t Figs. 8-10 illustrate a lamina 100 containing a plurality of highly canted full cube comer elements, such as disclosed in a U.S. Patent application entitled Cube Comer Sheeting Mold and Method of Making the Same (Atty. Docket No. 51946USA9A), suitable for use as a master mold to form full cube comer elements. Altematively, the full cube comer elements disclosed in U.S. Patent Application entitled Retroreflective Cube Comer Sheeting Mold and Sheeting Formed Therefrom (Atty. Docket No. 53305USA5A) can be used. Full cube comer elements have a higher total light retum than tmncated cube corner elements for a given amount of cant, but the full cubes lose total light retum more rapidly at higher entrance angles. One benefit of full cube comer elements is higher total light retum at low entrance angles, without too large of a loss in performance at higher entrance angles. For puφoses of description, a Cartesian coordinate system can be superimposed onto lamina 100. A first reference plane 124 is centered between first major surface 112 and second major surface 114. First reference plane 124, referred to as the x-z plane, has the y-axis as its normal vector. A second reference plane 126, referred to as the x-y plane, extends substantially coplanar with the working surface of lamina 100 and has the z-axis as its normal vector. A third reference plane 128, referred to as the y-z plane, is centered between first end surface 120 and second end surface 122 and has the x-axis as its normal vector. It will be appreciated that geometric attributes of the preferred embodiments can be described using coordinate systems other than the Cartesian reference planes herein described, or with reference to the structure of the lamina. The laminae 100 contain a first groove set comprising a plurality of parallel adjacent V-shaped grooves 130 disposed at an angle δi as shown. At least two adjacent grooves 130 are formed in the laminae 100, with each groove having a first and second groove surface 132, 134 that intersect at a groove vertex 133. At the edge of the lamina, the groove forming operation can form a single groove surface 132. Importantly, the groove surfaces 132 and 134 of adjacent grooves intersect approximately orthogonally along a reference edge 136. Preferably this pattern is repeated across the entire working surfaces of the plurality of laminae 100. The grooves 130 are formed by removing portions of the working surface of the plurality of laminae using any of a variety of suitable material removal techniques including precision machining techniques such as milling, mling, grooving and fly-cutting. Further, chemical etching or laser ablation techniques can also be used. In one embodiment, the grooves 130 of the first groove set are formed in a high-precision machining operation in which a diamond cutting tool having a 90° included angle is repeatedly moved transversely across the working surfaces of the plurality of laminae 100 along an axis that is substantially parallel to base surface 180. The cutting tool can be alternately be moved along an axis that is non-parallel to base surface 180 such that the tool cuts at a varying depth across the plurality of laminae 100. It will be appreciated that the machining tool can be held stationary while the plurality of laminae are placed in motion; any technique having relative motion between the plurality of laminae 100 and the machining tool is contemplated. Thus, in a top plan view, reference edges 136 appear perpendicular to the respective first reference planes 124 of the plurality of laminae 100. A second groove set comprising a plurality of parallel adjacent V-shaped grooves 138 is formed in the working surfaces of the plurality of laminae 100 with the lamina disposed at an angle δ . At least two adjacent grooves 138 are formed in the working surface of the plurality of laminae 100 with each groove 138 having a third and fourth groove surface 140, 142 that intersect at a groove vertex 141. At the edge of the lamina, the groove forming operation can form a single groove surface 140. Importantly, the groove surfaces 140 and 142 of adjacent grooves intersect approximately orthogonally along a reference edge 144. Preferably this pattern is repeated across the entire working surfaces of the plurality of laminae 100. Grooves 138 are preferably formed at approximately the same depth in the working surface of the plurality of laminae 100 as grooves 130 in the first groove set. Additionally, the grooves 138 in the second groove set are preferably formed such that the groove vertices 141 and reference edges 144 are substantially coplanar with the respective groove vertices 133 and reference edges 136 of the grooves 130 in the first groove set. A third groove set is formed that preferably includes at least one groove 146 in each lamina 100. The third grooves 146 define fifth and sixth groove surfaces 148, 150 that intersect at respective groove vertices 152 along axes that are parallel to the first reference planes 124. Importantly, the third grooves 146 are formed such that fifth groove surfaces 148 are substantially orthogonal to first groove surfaces 132 and second groove surfaces 134. Formation of the fifth groove surfaces 148 yields a plurality of cube comer elements 160. Each cube comer element 160 is defined by a first groove surface 132, a second groove surface 134, and a portion of a fifth groove surface 148 that mutually intersect at a point to define a cube comer peak, or apex 162. Similarly, sixth groove surface 150 is substantially orthogonal to third groove surfaces 140 and second groove surfaces 142. Formation of the sixth groove surface 150 also yields a plurality of cube comer elements 170 in the working surface of lamina 100. Each cube co er element 170 is defined by a third groove surface 140, a fourth groove surface 142, and a portion of sixth groove surface 150 that mutually intersect at a point to define a cube comer peak, or apex 172. Preferably, both fifth groove surface 148 and sixth groove surface 150 form a plurality of cube comer elements on the working surface of lamina 100. However, third groove 146 can altemately be formed such that only fifth groove surface 148 or sixth groove surface 150 forms cube comer elements. Additionally, an apex 162, 172 is not required. For some applications, planar regions can be formed in the cube corner elements to permit the transmission of light through the sheeting. Preferably, grooves 146 are also formed by a high precision machining operation. In the disclosed embodiment a diamond cutting tool having an included half-angle of about 46.55° (corresponding to about 12° of tilt) to about 10.52° (corresponding to about 30° of tilt), and more preferably about 42.52° (corresponding to about 14° of tilt) to about 30.52° (corresponding to about 20° of tilt) moves across the working surface of each lamina 100 along an axis that is substantially contained by the first reference plane 124 and that is parallel to base surface 180. In order to achieve highly canted cube comer elements, the grooves 146 are deeper than the vertices 133, 141 of the grooves in the first and second groove sets 130, 138, respectively. The cube comer element geometry formed in working surface of lamina 100 can be characterized as a 'full' or 'high efficiency' cube comer element geometry because the geometry exhibits a maximum effective aperture that approaches 100%. Thus, a retroreflector formed as a replica of the working surface will exhibit high optical efficiency in response to light incident on the retroreflector approximately along the symmetry axes of the cube corner elements. Additionally, cube co er elements 160 and 170 are disposed in opposing orientations and are symmetrical with respect to first reference plane 124 and will exhibit symmetric retroreflective performance in response to light incident on the retroreflector at high entrance angles. It is not required, however, that the cube comer elements be symmetrical about the reference planes. Preferred laminae 100 are formed from a dimensionally stable material capable of holding precision tolerances, such as a machinable plastic (for example, polyethylene teraphthalate, polymethyl methacrylate, and polycarbonate) or metal (for example, brass, nickel, copper, or aluminum). The physical dimensions of the laminae are constrained primarily by machining limitations. The laminae preferably measure at least 0.1 millimeters in thickness, between 5.0 and 100.0 millimeters in height, and between 10 and 500 millimeters in width. However, these measurements are provided for illustrative purposes only and are not intended to be limiting. A planar interface between major surfaces 112, 114 is maintained between adjacent laminae during the machining phase and in the subsequent mold formed therefrom so as to minimize alignment problems and damage due to handling of the laminae, to minimize gaps between adjacent laminae that would degrade the quality of negative copies, and to minimize flash from migrating into the gaps between the laminae. In the manufacture of retroreflective articles such as retroreflective sheeting, the stmctured surface of the plurality of laminae is used as a master mold which can be replicated using electroforming techniques or other conventional replicating technology. The plurality of laminae can include substantially identical cube comer elements or can include cube comer elements of varying sizes, geometries, or orientations. The stmctured surface of the replica, referred to in the art as a 'stamper', contains a negative image of the cube comer elements. This replica can be used as a mold for forming a retroreflector. More commonly, however, a large number of positive or negative replicas are assembled to form a mold large enough to be useful in forming retroreflective sheeting. Such retroreflective sheeting can be manufactured as an integral material, e.g. by embossing a preformed sheet with an array of cube comer elements as described above or by casting a fluid material into a mold. See, JP 8-309851 and U.S. Patent No. 4,601,861 (Pricone). Altematively, the retroreflective sheeting can be manufactured as a layered product by casting the cube comer elements against a preformed film as taught in PCT application No. WO 95/11464 and U.S. Pat. No. 3,648,348 or by laminating a preformed film to preformed cube comer elements. By way of example, effective sheeting of the invention can be made using a nickel mold formed by electrolytic deposition of nickel onto a master mold. The electroformed mold can be used as a stamper to emboss the pattern of the mold onto a polycarbonate film approximately 500 μm thick having an index of refraction of about 1.59. The mold can be used in a press with the pressing performed at a temperature of approximately 175° to 200° C. Useful materials for making reflective sheeting according to the invention are preferably materials that are dimensionally stable, durable, weatherable and readily formable into the desired configuration. Examples of suitable materials include acrylics, which generally have an index of refraction of about 1.5, such as Plexiglas resin from Rohm and Haas; thermoset acrylates and epoxy acrylates, preferably radiation cured, polycarbonates, which have an index of refraction of about 1.6; polyethylene-based ionomers (marketed under the name 'SURLYN'); polyesters; and cellulose acetate butyrates. Generally an optically transmissive material that is formable, typically under heat and pressure, can be used. Other suitable materials are disclosed in U.S. Pat. No. 5,450,235 to Smith et al. The sheeting can also include colorants, dyes, UV absorbers, or other additives as needed. It is desirable in some circumstances to provide retroreflective sheeting with a backing layer. A backing layer is particularly useful for retroreflective sheeting that reflects light according to the principles of total internal reflection. A suitable backing layer can be made of any transparent or opaque material, including colored materials, that can be effectively engaged with the retroreflective sheeting. Suitable backing materials include aluminum sheeting, galvanized steel, polymeric materials such as polymethyl methacrylates, polyesters, polyamides, polyvinyl fluorides, polycarbonates, polyvinyl chlorides, polyurethanes, and a wide variety of laminates made from these and other materials. The backing layer or sheet can be sealed in a grid pattern or any other configuration suitable to the reflecting elements. Sealing can be affected by a number of methods including ultrasonic welding, adhesives, or by heat sealing at discrete locations on the arrays of reflecting elements (see, e.g. U.S. Pat. No. 3,924,928). Sealing is desirable to inhibit the entry of contaminants such as soil and/or moisture and to preserve air spaces adjacent the reflecting surfaces of the cube comer elements. If added strength or toughness is required in the composite, backing sheets of polycarbonate, polybutryate or fiber-reinforced plastic can be used. Depending upon the degree of flexibility of the resulting retroreflective material, the material can be rolled or cut into strips or other suitable designs. The retroreflective material can also be backed with an adhesive and a release sheet to render it useful for application to any substrate without the added step of applying an adhesive or using other fastening means. The cube comer elements can be individually tailored so as to distribute light retroreflected by the articles into a desired pattern or divergence profile, as taught by U.S. Pat. No. 4,775,219. Typically the groove half-angle error introduced will be less than ± 20 arc minutes and often less than ± 5 arc minutes. Fig. 11 is an isobrightness contour depicting the total light retum profile of retroreflective sheeting having a stmctured surface comprising full cube comer elements according to Figs. 8-10 canted 14° (groove 146 having an included angle of 42.52°) in a backward direction formed from a material having an index of refraction of 1.59. The highly canted, full cube comer elements of Figs. 8-10 provide one primary plane of entrance angularity. Fig. 12 is an isobrightness contour depicting the total light retum profile of retroreflective sheeting having a stmctured surface comprising full cube comer elements of Figs. 8-10 canted 14° in a backward direction, tiled in accordance with the embodiment of Fig. 1, and formed from a material having an index of refraction of 1.59. Table 3 contains the total light retum data presented graphically in Fig. 12. The rotational orientation data of Table 3 is limited to 0 to 90°, rather than a full 360°, since the pattern repeats every 90°. The total light retum data for Table 3 does not include losses due to sealing, reflective coatings, etc. Zero degree orientation in Table 3 corresponds to the positive y-axis 58. Table 3 Fig. 13 is an isobrightness contour depicting the total light retum profile of retroreflective sheeting according to Figs. 8-10 with full cube comer elements canted 20° (groove 146 having an included half-angle of 30.52°) in a backward direction and formed from a material having an index of refraction of 1.59. Fig. 14 is an isobrightness contour depicting the total light retum profile of retroreflective sheeting having a stmctured surface comprising full cube comer elements of Figs. 8-10 canted 20° in a backward direction, formed from a material having an index of refraction of 1.59, and tiled in accordance with the embodiment of Fig. 1. Table 4 below contains total light retum data represented graphically in Fig. 14. The rotational orientation data of Table 4 is limited to 0 to 90° since the pattern repeats every 90°. The total light retum data for Table 4 does not include losses due to sealing, reflective coatings, etc. Zero degree orientation in Table 4 corresponds to the positive y-axis 58. Table 4 U ) An aspect of the present invention relates to a mold assembly suitable for use in forming the present retroreflective sheeting and a method of making a retroreflective article using the mold. The mold assembly includes a substrate having a base surface and a mold surface opposite the base surface. The mold surface includes in roughly equal proportions a first and a second array of cube comer element opposing pairs. The symmetry axes of the cube comer elements in the array are preferably tilted in a backward direction at an angle measuring between 15.1° and 30° from an axis normal to the base surface. The second array of cube comer elements is oriented approximately peφendicular to the first array. In an alternate embodiment, the first and second arrays of cube comer element opposing pairs are tilted by an angle between about 15.1° and about 20°. The method of making a retroreflective article includes forming a replica of the mold. The replica of the mold includes a mold surface having a negative image of the mold. A retroreflective article is formed in the mold surface of the replica. All patents and patent applications referred to, including those disclosed in the background of the invention, are hereby incoφorated by reference. The present invention has now been described with reference to several embodiments thereof. It will be apparent to those skilled in the art that many changes can be made in the embodiments described without departing from the scope of the invention. Thus, the scope of the present invention should not be limited to the preferred stmctures and methods described herein, but rather by the broad scope of the claims which follow.

Claims: What is claimed is: 1. A retroreflective article comprising a substrate having a base surface and a stmctured surface opposite the base surface, the stmctured surface comprising a plurality of arrays of cube comer elements, including: a first array of cube comer element opposing pairs, the symmetry axes of the cube comer elements in the array being tilted in a backward direction at an angle measuring between about 12° and about 30° from an axis normal to the base surface; and a second array of cube comer element opposing pairs, the symmetry axes of the cube comer elements in the array being tilted in a backward direction by an angle measuring between about 12° and about 30° from an axis normal to the base surface, the second array of cube comer elements being oriented approximately peφendicular to the first array so that the retroreflective article provides a minimum total light retum of about 5% across about a 360° range of orientation angles at an entrance angle of about 40° . 2. The retroreflective article of claim 1 wherein the first array and the second array occupy roughly equal areas of the stmctured surface of the retroreflective article. 3. The retroreflective article of claim 1 wherein the cube corner elements are generally trihedral stmctures comprising three mutually peφendicular triangular optical faces that intersect at a peak and a triangular base, the base being approximately coplanar with the base surface of the article. 4. The retroreflective article of claim 1 wherein the cube comer elements are generally polygonal stmctures comprising three mutually peφendicular optical faces including two tetragonal optical faces and a third optical face that intersect at a peak, and a tetragonal base. 5. The retroreflective article of claim 1 wherein the symmetry axes of the cube comer elements in the first are tilted in a backward direction at an angle measuring between about 14° and about 20° from an axis normal to the base surface. 6. The retroreflective article of claim 1 wherein the symmetry axes of the cube comer elements in the first array are tilted in a backward direction at an angle measuring about 14° from an axis normal to the base surface. 7. The retroreflective article of claim 1 wherein the symmetry axes of the cube comer elements in the second array are tilted in a backward direction at an angle measuring between about 14° and about 20° from an axis normal to the base surface. 8. The retroreflective article of claim 1 wherein the symmetry axes of the cube comer elements in the second array are tilted in a backward direction at an angle measuring about 14° from an axis normal to the base surface. 9. The retroreflective article of claim 1 wherein the second array is oriented at an angle between about 85°and about 95° relative to the first array. 10. The retroreflective article of claim 1 wherein the cube comer element opposing pairs comprise physically adjacent cube comer elements. 11. The retroreflective article of claim 1 wherein the cube comer element opposing pairs each comprise a different retroreflection pattern. 12. The retroreflective article of claim 1 wherein the cube comer element opposing pairs comprise matched pairs. 13. The retroreflective article of claim 1 wherein the article provides a generally uniform total light retum about a 360° range of orientation angles for entrance angles of greater than about 40°. 14. The retroreflective article of claim 1 wherein the article is capable of a minimum total light retum of about 5% across about a 360° range of orientation angles at an entrance angle of about 50°. 15. The retroreflective article of claim 1 wherein the article is capable of a minimum total light retum of about 5% across about a 360° range of orientation angles at an entrance angle of about 60°. 16. The retroreflective article of claim 1 wherein the article is capable of a minimum total light retum of about 10% across about a 360° range of orientation angles at an entrance angle of about 40°. 17. The retroreflective article of claim 1 wherein the article is capable of a minimum total light retum of about 10% across about a 360° range of orientation angles at an entrance angle of about 50°. 18. The retroreflective article of claim 1 wherein the article is capable of a minimum total light retum of about 10% across about a 360° range of orientation angles at an entrance angle of about 60°. 19. The retroreflective article of claim 1 wherein the substrate and the cube comer elements are formed as a unitary article from a light transmissible material having a refractive index of between 1.3 and 1.7. 20. The retroreflective article of claim 1, wherein the substrate comprises a body layer comprising a light transmissible material having an elastic modulus less than about 7x10 8 pascals, and the cube comer elements comprise a light transmissible material having an elastic modulus greater than about 16x10 pascals. 21. The retroreflective article of claim 1 wherein a plurality of the cube comer elements incoφorate minor deviations from perfect orthogonality to thereby alter the light distribution in the emerging cone of retroreflected light. 22. The retroreflective article of claim 1 wherein portions of the first and second arrays of cube comer elements are coated with a specularly reflective substance. 23. The retroreflective article of claim 1 further comprising a sealing medium disposed adjacent the first and second arrays of cube comer elements. 24. The retroreflective article of claim 1 wherein a sealing medium is bonded to the stmctured surface by a network of intersecting bonds to define a plurality of cells within which the cube comer elements are hermetically sealed. 25. The retroreflective article of claim 1 wherein a sealing medium maintains an air interface with the stmctured surface such that the cube comer elements retroreflect according to the principles of total internal reflection. 26. The retroreflective article of claim 1 wherein the cube comer elements comprise full cube comer elements. 27. A retroreflective article comprising a substrate having a base surface and a stmctured surface opposite the base surface, the stmctured surface comprising a plurality of arrays of cube comer elements, including: a first array of cube comer element opposing pairs, the symmetry axes of the cube comer elements in the array being tilted in a backward direction at an angle measuring between about 12° and about 30° from an axis normal to the base surface; and a second array of cube comer element opposing pairs, the symmetry axes of the cube corner elements in the array being tilted in a backward direction by an angle measuring between about 12° and about 30° from an axis normal to the base surface, the second array of cube comer elements being oriented approximately peφendicular to the first array so that the retroreflective article provides a generally uniform total light retum about a 360° range of orientation angles. 28. A retroreflective article comprising a substrate having a base surface and a stmctured surface opposite the base surface, the stmctured surface comprising a plurality of arrays of cube corner elements, including: a first array of cube co er element opposing pairs, the symmetry axes of the cube comer elements in the array being tilted in a backward direction at an angle measuring between about 15.1° and about 30° from an axis normal to the base surface; and a second array of cube corner element opposing pairs, the symmetry axes of the cube comer elements in the array being tilted in a backward direction by an angle measuring between about 15.1° and about 30° from an axis normal to the base surface, the second array of cube comer elements being oriented approximately perpendicular to the first array. 29. A mold assembly suitable for use in forming retroreflective sheeting, the mold assembly comprising a substrate having a base surface and a mold surface opposite the base surface, the mold surface comprising in roughly equal proportions: a first array of cube corner element opposing pairs, the symmetry axes of the cube co er elements in the array being tilted in a backward direction at an angle measuring between about 15.1° and about 30° from an axis normal to the base surface; and a second array of cube comer element opposing pairs, the symmetry axes of the cube comer elements in the array being tilted in a backward direction by an angle measuring between about 15.1° and about 30° from an axis normal to the base surface, the second array of cube comer elements being oriented approximately peφendicular to the first array. 30. The method of claim 29 wherein the first and second arrays of cube comer element opposing pairs are tilted by an angle measuring between about 15.1° and about 20°. 31. A method of making a retroreflective article, comprising: providing a mold assembly suitable for forming retroreflective articles, the mold assembly comprising a substrate having a base surface and a mold surface opposite the base surface, the mold surface comprising in roughly equal proportions: a first array of cube comer element opposing pairs, the symmetry axes of the cube comer elements in the first array being tilted in a backward direction at an angle measuring between about 15.1° and about 30° from an axis normal to the base surface, and a second array of cube comer element opposing pairs, the symmetry axes of the cube corner elements in the second array being tilted in a backward direction by an angle measuring between about 15.1° and about 30° from an axis normal to the base surface wherein the second array of cube comer elements is oriented approximately peφendicular to the first array; forming a replica of the mold, the replica of the mold including a surface having a negative image of the mold; and forming a retroreflective article in the surface of the replica. 32. The method of claim 31 wherein the first and second arrays of cube comer element opposing pairs are tilted by an angle measuring between about 15.1° and about 20°.

Inventors: BENSON GERALD M, SMITH KENNETH L, BENSON, GERALD, M., SMITH, KENNETH, L.
Applicants: MINNESOTA MINING & MFG, MINNESOTA MINING AND MANUFACTURING COMPANY
Application year: 1997
Main classification: G02B5
IPC codes: G02B5