METHOD OF CONTACT PRINTING ON GOLD COATED FILMS

Abstract: The present invention comprises methods of contact printing of patterned, self-assembling monolayers of alkanethiolates, carboxylic acids, hydroxamic acids, and phosphonic acids on metallized thermoplastic films, the compositions produced thereby, and the use of these compositions. Patterned self-assembling monolayers allow for the controlled placement of fluids thereon which contain a chemically reactive, indicator functionality. The optical sensing devices produced thereby when the film is exposed to an analyte and light, can produce optical diffraction patterns which differ depending on the reaction of the self-assembling monolayer with the analyte of interest. The light can be in the visible spectrum, and be either reflected from the film, or transmitted through it, and the analyte can be any compound reacting with the fluid on the self-assembling monolayer. The present invention also provides a flexible support for a self-assembling monolayer on gold or another suitable metal.

Description: METHOD OF CONTACT PRINTING ON GOLD COATED FILMS Technical Field The present invention is in the field of contact printing and, more specifically the present invention is in the field of microcontact printing on metal films such as gold. Background of the Invention Microcontact printing is a technique for forming patterns of organic monolayers with μm and submicron lateral dimensions. It offers experimental simplicity and flexibility in forming certain types of patterns. It relies on the remarkable ability of self-assembled monolayers of long-chain alkanethiolates to form on gold and other metals. These patterns can act as nanometer resists by protecting the supporting metal from corrosion by appropriately formulated etchants, or, can allow for the selective placement of fluids on hydrophilic regions of the pattern. Patterns of self-assembled monolayers having dimensions that can be less than 1 μm are formed by using the alkanethiol as an "ink", and by printing them on the metal support using an elastomeric "stamp". The stamp is fabricated by molding a silicone elastomer using a master prepared by optical or X-ray microlithography or by other techniques. Microcontact printing of patterned self-assembled monolayers brings to microfabrication a number of new capabilities. First, microcontact printing makes it possible to form patterns that are distinguished only by their constituent functional groups; this capability permits the control of surface properties such as interfacial free energies with great precision. Second, because microcontact printing relies on molecular self-assembly, it generates a system that is (at least locally) close to a thermodynamic minimum and is intrinsically defect-rejecting and self-healing. Simple procedures, with minimal protection against surface contamination by adsorbed materials or by particles, can lead to surprisingly low levels of defects in the final structures. The procedure can be conducted at atmospheric pressure, in an unprotected laboratory atmosphere. Thus, microcontact printing is especially useful in laboratories that do not have routine access to the equipment normally used in microfabrication, or for which the capital cost of equipment is a serious concern. Third, the patterned self-assembled monolayers can be designed to act as resists with a number of wet-chemical etchants. Working with liquid etchants suffers from the disadvantages of handling solvents and disposing of wastes, but also enjoys substantial advantages: a high degree of control over contamination of surfaces; reduced damage to the substrate from energetic interactions with atoms or ions; the ability to manipulate complex and sensitive organic functionalities. Because the self-assembled monolayers are only 1 - 3 nm thick, there is little loss in edge definition due to the thickness of the resist; the major determinants of edge resolution seem to be the fidelity of the contact printing and the anisotropy of etching the underlying metal. In the current best cases, features of size 0.2 μm can be fabricated; edge resolution in systems showing this resolution in feature size is less than 50 nm. In the prior art, a gold film 5 to 2000 nanometers thick is typically supported on a titanium-primed Si/Si0 2 wafer or glass sheet. The titanium serves as an adhesion promoter between gold and the support. However, the silicon wafer is rigid, brittle, and cannot transmit light. These silicon wafers are also not suitable for a large-scale, continuous printing process, such as in letterpress, gravure, offset, and screen printing (see Printing Fundamentals. A. Glassman, Ed. (Tappi Press Atlanta, GA 1981 ); Encyclopedia Britannica. vol. 26, pp. 76-92, 110- 111 (Encyclopedia Brittanica, Inc. 1991)). In addition, silicon must be treated in a separate step with an adhesion promoter such as Cr or Ti, or Au will not adequately adhere, preventing formation of a stable and well-ordered self-assembling monolayer. Finally, silicon is opaque, so any diffraction pattern obtained must be created with reflected, not transmitted light. What is needed is an easy, efficient and simple method of contact printing on an optically transparent, flexible substrate, that is amenable to continuous processing. Summary of the Invention The present invention comprises methods of contact printing of patterned, self-assembling monolayers of alkanethiolates, carboxylic acids, hydroxamic acids, and phosphonic acids on metallized thermoplastic films, the compositions produced thereby, and the use of these compositions. Patterned self-assembling monolayers allow for the controlled placement of fluids thereon which can contain a chemically reactive, indicator functionality. The optical sensing devices produced thereby when the film is exposed to an analyte and light, can produce optical diffraction patterns which differ depending on the reaction of the self- assembling monolayer with the analyte of interest. The light can be in the visible spectrum, and be either reflected from the film, or transmitted through it, and the analyte can be any compound reacting with the self-assembling monolayer. The present invention also provides a flexible support for a self-assembling monolayer on gold or other suitable metal. The present invention includes a support for a self- assembling monolayer on gold or other suitable material which does not require an adhesion promoter for the formation of a well-ordered self-assembling monolayer. The present invention also provides a support for a self- assembling monolayer on gold or other material which is suitable for continuous, rather than batch, fabrication. Finally the present invention provides a low-cost, disposable sensor which can be mass produced. These and other objects, features and advantages of the present invention will become apparent after a review of the following detailed description of the disclosed embodiments. Brief Description of the Figures Figure 1 is a schematic of contact printing of self- assembling monolayers. A polydimethylsiloxane (PDMS; silicone elastomer 184; Dow Corning Corp., Midland, MI) is polymerized on a silicone master containing a predetermined pattern. The PDMS is peeled away from the master, and then exposed to a solution containing HS(CH2)15CH3. The alkane-thiol coated stamp is then stamped onto the gold-coated substrate. Then, the surface of the substrate is exposed to a solution containing a different alkane-thiol such as HS(CH2)l lOH. Figure 2 is an atomic force microscopy image of evaporated gold on MYLAR®, purchased from Courtaulds Performance Films (Canoga Park, CA). The average roughness of the gold layer is 3-4 nanometers, with maximum roughness of 9 nanometers. Figures 3a, 3b and 3c are atomic force microscopy images of a hydrophilic self-assembling monolayer circle of 16 mercaptohexadecanoic acids, as described in Example 1. Figure 3a is a topography image, Figure 3b is a lateral force image, and Figure 3 c is a three-dimensional graphic of a topography image. Figure 4 is a field emission secondary electron microscope image of 10 micron-diameter circles of hydrophilic self-assembling monolayers formed by printing of 16-mercaptohexadecanoic acid, as described in Example 1, below. Figure 5a is an optical photomicrograph at 300x magnification of 10 micron-diameter circles of hydrophilic self-assembling monolayers formed by printing of 16- mercaptohexadecanoic acid, as described in Example 1, below, and after exposure to a high surface energy, curable, optical adhesive. The adhesive was cured by ultraviolet light (UV) exposure. Figure 5b is a photograph of the diffraction pattern formed by visible light shown through the self-assembling monolayer pattern described by Figure 5 a. Figure 6 is a field emission secondary electron micrograph image of 10 micron-diameter circles formed by printing of self-assembled photocurable polymers on hydrophilic self-assembling monolayers. Figures 7a and 7b are field emission secondary electron micrographs of 1.5 micron diameter circles formed of self-assembling photocurable polymers on hydrophilic self-assembling monolayers, printed as described in Example 1. Detailed Description The present invention provides methods of contact printing of patterned, self-assembling monolayers of alkanethiolates, carboxylic acids, hydroxamic acids, and- phosphonic acids on metallized polymer films, desirably thermoplastic polymer films, the compositions produced thereby, and the use of these compositions. Patterned self- assembling monolayers allow for the controlled placement of fluids thereon which can contain a chemically reactive, indicator functionality. The term "patterned self- assembling monolayers thereon" as used herein means the self-assembling monolayers in any pattern on the metallized polymer films including a solid pattern. In one embodiment, optical sensing devices can be produced according to the present invention. When the film with the self-assembling monolayers thereon is exposed to an analyte that is capable of reacting with the self- assembling monolayer, the film will produce optical diffraction patterns which differ depending on the reaction of the self-assembling monolayer with the analyte of interest. The liquid may be a high surface tension fluid such as water. The light can be in the visible spectrum, and be either reflected from the film, or transmitted through it, and the analyte can be any compound reacting with the self- assembling monolayer Self-assembled monolayers of organic compounds on inorganic or metal surfaces are becoming increasingly important in many areas of materials science. Although there are many different systems of self-assembling monolayers based on different organic components and supports, desired systems are those of alkanethiolates, HS(CH 2 ) n R, on gold films. Typically, a gold film, 5 to 2000 nm thick, is supported on a titanium-primed Si/Si0 2 wafer or glass sheet. The titanium serves as an adhesion promoter between gold and the support. The alkanethiols chemisorb on the gold surface from a solution in which the gold film is immersed, and form adsorbed alkanethiolates with loss of hydrogen. Adsorption can also occur from the vapor. Self-assembling monolayers formed on gold from long-chain alkanethiolates of structure X(CH 2 ) n Y(CH 2 ) m S are highly ordered and can be considered as crystalline or quasi-crystalline molecular arrays. A wide variety of organic functional groups (X,Y) can be incorporated into the surface or interior of the monolayer. Self-assembling monolayers can therefore be tailored to provide a wide variety of material properties: wettability and protection against corrosion by chemical etchants are especially relevant to μCP. Figure 1 outlines the procedure used for microcontact printing. An elastomeric stamp is used to transfer alkanethiol "ink" to a gold surface by contact; if the stamp is patterned, a patterned self-assembling monolayer forms. The stamp is fabricated by casting polydimethylsiloxane (PDMS) on a master having the desired pattern. Masters are prepared using standard photolithographic techniques, or constructed from existing materials having microscale surface features. In a typical experimental procedure, a photolithographically produced master is placed in a glass or plastic Petri dish, and a 10: 1 ratio (w:w or v:v) mixture or SYLGARD silicone elastomer 184 and SYLGARD silicone elastomer 184 curing agent (Dow Corning Corporation) is poured over it. The elastomer is allowed to sit for approximately 30 minutes at room temperature and pressure to degas, then cured for 1 - 2 hours at 60°C, and gently peeled from the master. "Inking" of the elastomeric stamp is accomplished by exposing the stamp to a 0.1 to 1.0 mM solution of alkanethiol in anhydrous ethanol, either by pouring the solution over the surface of the stamp, or by rubbing the stamp gently with a Q-tip that has been saturated with the inking solution. The stamp is allowed to dry until no liquid is visible by eye on the surface of the stamp (typically about 60 seconds), either under ambient conditions, or by exposure to a stream of nitrogen gas. Following inking, the stamp is applied (typically by hand) " to a gold surface. Very light hand pressure is used to aid in complete contact between the stamp and the surface. The stamp is then gently peeled from the surface. Following removal of the stamp, the surface is washed of excess thiol and the patterned gold surface can be subjected to chemical etchants (see below) that selectively remove underivatized areas of the gold surface, and if desired, the underlying support(s). Alternatively, further derivatization of unstamped areas can be accomplished, either by using a second stamp, or by washing the entire surface with a different alkanethiol. The elastomeric character of the stamp is essential to the success of the process. Polydimethylsiloxane (PDMS), when cured, is sufficiently elastomeric to allow good conformal contact of the stamp and the surface, even for surfaces with significant relief; this contact is essential for efficient contact transfer of the alkanethiol "ink" to the gold film. The elastomeric properties of PDMS are also important when the stamp is removed from the master: if the stamp were rigid (as is the master) it would be difficult to separate the stamp and master after curing without damaging one of the two substrates. PDMS is also sufficiently rigid to retain its shape, even for features with sub-micron dimensions: we have successfully generated patterns with lines as small as 200 nm in width. The surface of PDMS has a low interfacial free energy (y = 22.1 dynes/cm), and the stamp does not adhere to the gold film. The stamp is durable: we have used the same stamp up to 100 times over a period of several months without significant degradation in performance. The polymeric nature of PDMS also plays a critical role in the inking procedure, by enabling the stamp to absorb the alkanethiol ink by swelling. Microcontact printing on gold surfaces can be conducted with a variety of alkanethiol "inks" " . Alkanethiols that do not undergo reactive spreading (after application to the gold film) are required for formation of small features with high resolution. For stamping in air, one can use autophobic alkanethiols such as hexadecanethiol. Microcontact printing of other non- autophobic alkanethiols, for example , HS(CH 2 )ι 5 COOH, can be conducted by stamping under a liquid such as water. Patterned self-assembling monolayers of alkanethiols on gold provide excellent resist character with a number of wet-chemical etchants. In one embodiment of the present invention, the self- assembling monolayer is formed of a carboxy-terminated alkane thiol stamped with a patterned elastomeric stamp onto a gold-surfaced thermoplastic film such as MYLAR" . The alkanethiol is inked with a solution of alkanethiol in ethanol, dried, and brought into contact with a surface of gold. The alkanethiol is transferred to the surface only at those regions where the stamp contacts the surface, producing a pattern of self-assembling monolayer which is defined by the pattern of the stamp. Optionally, areas of unmodified gold surface next to the stamped areas can be rendered hydrophobic by reaction with a methyl-terminated alkane thiol. A more detailed description of the methods and compositions of the present invention follows. All publications cited herein are incorporated by reference in their entirety. Any thermoplastic film upon which a metal substrate can be deposited is suitable for the present invention. These include, but are not limited to polymers such as: polyethylene-terephthalate (MYLAR®), acrylonitrile- butadiene-styrene, acrylonitrile-methyl acrylate copolymer, cellophane, cellulosic polymers such as ethyl cellulose, cellulose acetate, cellulose acetate butyrate, cellulose propionate, cellulose triacetate, cellulose triacetate, polyethylene, polyethylene - vinyl acetate copolymers, ionomers (ethylene polymers) polyethylene-nylon copolymers, polypropylene, methyl pentene polymers, poly vinyl fluoride, and aromatic polysulfones. Preferably, the plastic film has an optical transparency of greater than 80%. Other suitable thermoplastics and suppliers may be found, for example, in reference works such as the Modern Plastics Encyclopedia (McGraw-Hill Publishing Co., New York 1923-1996). In one embodiment of the invention, the thermoplastic film with the metal coating thereon has an optical transparency of between approximately 5% and 95%. A more desired optical transparency for the thermoplastic film used in the present invention is between approximately 20% and 80%. In a desired embodiment of the present invention, the thermoplastic film has at least an approximately 80% optical transparency, and the thickness of the metal coating is such as to maintain an optical transparency greater than about 20%, so that diffraction patterns can be produced by either reflected or transmitted light. This corresponds to a metal coating thickness of about 20 nm. However, in other embodiments of the invention, the gold thickness may be between approximately 1 nm and 1000 nm. The preferred metal for deposition on the film is gold. However, silver, aluminum, copper, iron, zirconium, platinum and nickel, as well as other metals, may be used. Preferred metals are ones that do not form oxides, and thus assist in the formation of more predictable self-assembling monolayers. In principle, any surface with corrugations of appropriate size could be used as masters. The process of microcontact printing starts with an appropriate relief structure, from which an elastomeric stamp is cast. This 'master' template may be generated photolithographically, or by other procedures, such as commercially available diffraction gratings. In one embodiment, the stamp may be made from polydimethylsiloxane. In one embodiment of the present invention, the self- assembling monolayer has the following general formula: X-R-Y X is reactive with metal or metal oxide. For example, X may be asymmetrical or symmetrical disulfide (-R'SSR, -RSSR), sulfide (-R'SR, -RSR), diselenide (-R'Se- SeR), selenide (-R'SeR, -RSeR), thiol (-SH), nitrile (-CN), isonitrile, nitro (-N02 ), selenol (-SeH), trivalent phosphorous compounds, isothiocyanate, xanthate, thiocarbamate, phosphine, thioacid or dithioacid, carboxylic acids, hydroxylic acids, and hydroxamic acids. R and R' are hydrocarbon chains which may optionally be interrupted by hetero atoms and which are preferably non-branched for the sake of optimum dense packing. At room temperature, R is greater than or equal to seven carbon atoms in length, in order to overcome natural randomizing of the self-assembling monolayer. At colder temperatures, R may be shorter. In a preferred embodiment, R is -(CH2)n- where n is between 10 and 12, inclusive. The carbon chain may optionally be perfluorinated. Y may have any surface property of interest. For example, Y could be any among the great number of groups used for immobilization in liquid chromatography techniques, such as hydroxy, carboxyl, amino, aldehyde, hydrazide, carbonyl, epoxy, or vinyl groups. Examples of sensing layer materials are set forth in "Patterning Self- Assembled Monolayers Using Microcontact Printing: A New Technology for Biosensors?," by Milan Mrksich and George M. Whitesides, published in TIBTECH, June, 1995 (Vol. 13), pp. 228-235, hereby incorporated by reference. Self assembling monolayers of alkyl phosphonic, hydroxamic, and carboxylic acids may also be useful for the methods and compositions of the present invention. Since alkanethiols do not adsorb to the surfaces of many metal oxides, carboxylic acids, phosphonic acids, and hydroxamic acids may be preferred for X for those metal oxides. See J. P. Folkers, G.M. Whitesides, et al. , Langmuir, 1995, vol. 11, pp. 813-824. R may also be of the form (CH2)a~Z-(CH2)b, where a>0, b>7, and Z is any chemical functionality of interest, such as sulfones, urea, lactam, etc. The stamp may be applied in air, or under a fluid such as water to prevent excess diffusion of the alkanethiol. For large-scale or continuous printing processes, it is most desirable to print in air, since shorter contact times are desirable for those processes. In one embodiment of the present invention, the pattern is formed on the metallized thermoplastic polymer with the self-assembling monolayer. In another embodiment of the present invention, the relief of the pattern is formed with the self-assembling monolayer. After the stamping process, the metallized areas on the plastic may optionally be passivated, for example, with a methyl-terminated self-assembling monolayer such as hexadecylmercaptan. This invention is further illustrated by the following examples, which are not to be construed in any way as imposing limitations upon the scope thereof. On the contrary, it is to be clearly understood that resort may be had to various other embodiments, modifications, and equivalents thereof, which, after reading the description herein, may suggest themselves to those skilled in the art without departing from the spirit of the present invention. Example 1 Printing of gold-coated MYLAR® (polyethylene terephthalate) with patterns of 16-mercaptohexadecanoic acid and hexadecanethiol Patterns of gold-coated MYLAR® (polyethylene terephthalate) were printed with patterns of 16 mercaptohexadecanoic acid and hexadecanethiol, as shown in Figure 1, and described below. MYLAR® film modified with a plasma deposited gold topcoat was obtained from Courtaulds Performance Films (21034 Osborne Street, Canoga Park, CA 91304). An atomic force microscopy image of this MYLAR film is shown in Figure 2. Polymer film thickness between 2 and 7 mils and gold topcoats producing a surface resistance of 65 ohms per square centimeter with a visible light transmittance between 20% and 65% were used. Patterns of hydrophilic, carboxy-terminated alkane thiols were stamped onto gold-coated film using 16- mercaptohexadecanoic acid by the following method. An exposed and developed photoresist pattern of 10 micron diameter circles on a silicon wafer was used as the master. Polydimethylsiloxane (PDMS; silicone elastomer 184; Dow Corning Co., Midland, MI), was polymerized on a master to produce a stamp with ten micron-diameter circles spaced five microns apart. The stamp was inked by exposure to a solution ( 1 to 10 mM in ethanol) of 16- mercaptohexadecanoic acid, and allowed to air-dry. The substrate was contacted with the stamp for 50 seconds and washed for 2 to 4 seconds with a solution of hexadecanethiol (1 to 10 mM in ethanol). The substrate was finally washed for 10 seconds in ethanol and dried in a stream of nitrogen. The results of this printing are shown- in Figure 3 and Figure 4 for the 10 micron diameter circles of the carboxylic acid terminated self-assembling monolayer. These hydrophilic self-assembling monolayer circles allow for selective placement of high surface tension fluids such as water, triethylene glycol, or ultraviolet light curable urethane acrylic adhesives. These liquids can contain dissolved and suspended reagents that react chemically or physically with targeted analytes, thus making the coated plastic f lm a collection of 10 micron microreactors suitable for low cost, disposable chemical sensors. An example of such a device is shown in Figure 5a, Figure 6, and Figures 7a and 7b. Diffraction of visible light was shown with these compositions. Both reflected and transmitted diffraction patterns were observed when using 5mW, 670 nM laser illumination. Figure 5b is a photograph of the diffraction pattern formed by visible light shown through the self- assembling monolayer pattern of Figure 5a. Rainbow diffraction colors were observed with transmitted white light. Example 2 Printing of aluminum-coated MYLAR® with patterns of 16-carboxy-hexadecanoic acid and hexadecanecarboxylate The procedure of Example 1 was followed for 100 gauge aluminum-coated MYLAR® with 35% visible light transmission, substituting the 1, 16-dihydroxamic acid of hexadecane and 1-hexadecane hydroxamic acid for the hydrophilic and hydrophobic thiols, respectively, of Example 1. Diffraction of visible light occurred. Both reflected and transmitted diffraction patterns were observed when using 5mW, 670 nM laser illumination. Rainbow diffraction colors were observed with transmitted white light. Example 3 Comparison of gold-coated MYLAR® with gold- coated silicon wafers. Gold films (100 angstroms to 1 micrometer) were deposited by electron beam evaporation on silicone wafers that had been primed with titanium (5-50 angstroms) to promote adhesion between silicon and gold. Stamping on both gold-coated film and gold-coated silicon wafers was performed as in Example 1. Measurement of Contact Angles Contact angles were measured on a Rame-Hart Model 100 goniometer at room temperature and ambient humidity. Water for contact angles was deionized and distilled in a glass and Teflon apparatus. Advancing and receding contact angles were measured on both sides of at least three drops of each liquid per slide; data in the figures represents the average of these measurements. The following method was used for measuring contact angles: A drop approximately 1-2 microliters in volume was grown on the end of a pipette tip (Micro-Electrapette syringe; Matrix Technologies; Lowell, MA). The tip was then lowered to the surface until the drop came in contact with the surface. The drop was advanced by slowly increasing the volume of the drop (rate approximately 1 microliter/second). Advancing contact angles of water were measured immediately after the front of the drop had smoothly moved a short distance across the surface. Receding angles were taken after the drop had smoothly retreated across the surface by decreasing the volume of the drop. X-ray Photoelectron Spectroscopy (XPS X-ray photoelectron spectra were collected on a Surface Science SSX- 100 spectrometer using a monochromatized Al K-alpha source (hv= 1486.6 electron volts). The spectra were recorded using a spot size of 600 micrometers and a pass energy on the detector of 50 electron volts (acquisition time for one scan was approximately 1.5 minutes). For the monolayers, spectra were collected for carbon and oxygen using the Is peaks at 285 and 530 eV, respectively; the binding energies for elements in the monolayer were referenced to the peak due to hydrocarbon in the C Is region, for which we fixed the binding energy at 284.6 eV. Spectra for the solid hydroxamic acid were collected using an electron flood gun of 4.5 eV to dissipate charge in the sample. The following signals were used for the substrates; Al 2p at 73 eV for A1(0), and at 75 eV for Al(III). The binding energies for the substrates were not standardized to a reference sample. All spectra were fitted using an 80% Gaussian/20% Lorentzian peak shape and a Shirley background subtraction. See J.P. Folkers, G.M. Whitesides, et al, Langmuir, vol. 11, no. 3, pp. 813-824 (1995). Condensation Figures Condensation figures (CFs) are arrays of liquid drops that form upon condensation of vapor onto a solid surface. The examination of condensation figures has historically been used as a method to characterize the degree of contamination on an otherwise homogeneous surface. One is able to impose a pattern on arrays of condensed drops by patterning the surface underlying them into regions of different solid-vapor interfacial free energy and to characterize the patterned CFs by photomicroscopy and optical diffraction. It can be demonstrated that appropriately patterned CFs can be used as optical diffraction gratings and that examination of the diffraction patterns provides both a rapid, nondestructive method for characterizing patterned self-assembling monolayers and an approach to sensing the environment. Because the form of the CFs — that is, the size, density, and distribution of the drops — is sensitive to environmental factors, CFs of appropriate size and pattern diffract light and can be used as sensors. This principle is demonstrated by correlating the temperature of a substrate patterned into hydrophobic and hydrophilic regions, in an atmosphere of constant relative humidity, with the intensity of light diffracted from CFs on these regions. Appropriate patterns are formed from self-assembled monolayers (self-assembling monolayers) on gold by using combinations of hexadecanethiol [CH 3 ((CH 2 ) V 15 S H] , 16-mercaptohexadecanoic acid [HS(CH 2 ) 14 COOH], and 11-mercaptoundecanol [HS(CH) π OH]. Several techniques are now available for preparing patterns of two or more self-assembling monolayers having 0.1 - to 10-μm dimensions. At 20°C, an incident beam of light from a laser (helium-neon laser, wavelength = 632.8 nm) produced a single transmitted spot because no water had condensed on the surface, and the transmittance of the regions covered with different self-assembling monolayers were effectively indistinguishable. As the surface was exposed to warm, moist air, droplets of water condensed preferentially on the hydrophilic regions. Diffraction patterns appeared in the light transmitted from the surface. Under these conditions, light was transmitted coherently from the regions where no water had condensed and was scattered by the regions where water had condensed. The condensation figures disappeared within several seconds as the water droplets which condensed on the self-assembling monolayers evaporated. The ability to form condensation figures can be ascertained by the relative contact angles of water on the hydrophobic and hydrophilic self-assembling monolayers. Unpatterned monolayers of the appropriate thiol were prepared by immersion of the substrate in a dilute solution for one hour, followed by rinsing with ethanol and air drying. Table I Comparison of Gold-Coated MYLAR with Gold-Coated Silicon Wafers: Reactions of ω-functionalized alkane-thiols * Gold-coated MYLAR substrate ** Silicon Oxide Substrate "ND" means "not detected", i.e., less than 0.2 atom-percent. Condensation Figures [Science, Vol. 263, 60 (1994), incorporated herein by reference] with equivalent optical diffraction can be formed on Au:MYLAR®, relative to known art with Au:SiOx. The chemistry of alkanethiols reacting with Au:MYLAR is similar to that reported in the literature for Au:SiOx. Example 4 Comparison of Aluminum/ AlOχ-coated MYLAR® with Al/AlOχ-coated silicon wafers; Reaction of the hydroxamic acid CH3-(CH2)16-CONH(OH) Using the procedures of Example 2, unpatterned monolayers of the appropriate hydroxamic acid were prepared by immersion of the substrate in a dilute solution for one hour, followed by rinsing with ethanol and air drying. The results are set forth in Table II, below. TABLE II Comparison of Aluminum/ A10χ Coated MYLAR® with Al/Al/O x Coated Silicon Wafers: Reaction of the Hydroxamic Acid CH 3 (CH 2 ) 16 CONH(OH) Condensation figures [per method of Science, Vol. 263, p. 60 (1994), incorporated herein by reference] with equivalent optical diffraction can be formed via contact printing. A 1 -coated, optical grade MYLAR® shows similar abilities to A 1 -coated silicon in promoting contact printing of self-assembling monolayers. Example 5 Self-assembled photocurable polymers on hydrophilic self-assembling monolayers. Figure 6 is a field emission secondary electron microscopy image of 10 micron-diameter self-assembled photocurable polymers on hydrophilic self- assembling monolayers. Those skilled in the art will now see that certain modifications can be made to the invention herein disclosed with respect to the illustrated embodiments, without departing from the spirit of the instant invention. And while the invention has been described above with respect to the preferred embodiments, it will be understood that the invention is adapted to numerous rearrangements, modifications, and alterations, all such arrangements, modifications, and alterations are intended to be within the scope of the appended claims.

Claims: CLAIMS We claim: 1. A film with patterned self-assembling monolayers thereon comprising: a polymer film coated with metal; and a self-assembling monolayer printed onto the- polymer film. 2. The film of Claim 1, wherein the metal is selected from the group consisting of gold, silver, nickel, platinum, aluminum, iron, copper, or zirconium. 3. The film of Claim 1, wherein the metal is gold. 4. The film of Claim 3, wherein the gold coating is between approximately 1 nanometer and 1000 nanometers in thickness. 5. The film of Claim 1, wherein the polymer film is polyethylene-terephthalate, acrylonitrile-butadiene- styrene, acrylonitrile-methyl acrylate copolymer, cellophane, cellulosic polymers such as ethyl cellulose, cellulose acetate, cellulose acetate butyrate, cellulose propionate, cellulose triacetate, cellulose triacetate, polyethylene, polyethylene - vinyl acetate copolymers, ionomers (ethylene polymers) polyethylene-nylon copolymers, polypropylene, methyl pentene polymers, polyvinyl fluoride, and aromatic polysulfones. 6. The film of Claim 4, wherein the polymer film is polyethylene-terephthalate. 7. The film of Claim 1, wherein the thermoplastic film is optically transparent. 8. The film of Claim 1, wherein the thermoplastic film has an optical transparency between 5% and 95%. 9. The film of Claim 1, wherein the thermoplastic film has an optical transparency between approximately 20% and 80%. 10. The film of Claim 1 , wherein the self- assembling monolayer is formed from compounds with the following general formula: X-R-Y wherein: X is reactive with the metal or metal oxide on the polymer film; R is a hydrocarbon chain; and Y is a compound with any property of interest. 11. The film of Claim 10, wherein: X is a asymmetrical or symmetrical disulfide (- R'SSR, -RSSR), sulfide (-R'SR, -RSR), diselenide (-R'Se- SeR), selenide (R'SeR, -RSeR), thiol (-SH), nitrile (-CN), isonitrile, nitro (-N02 ), selenol (-SeH), trivalent phosphorous compounds, isothiocyanate, xanthate, thiocarbamate, phosphine, thioacid or dithioacid, carboxylic acids, hydroxylic acids, and hydroxamic acids; R and R' are hydrocarbon chains which may optionally be interrupted by hetero atoms, and which may optionally be perfluorinated, and which are preferably non- branched; and Y is selected from the group consisting of hydroxy, carboxyl, amino, aldehyde, hydrazide, carbonyl, epoxy, or vinyl groups. 12. The film of Claim 10, wherein R is greater than 7 carbon atoms in length. 13. The film of Claim 10, wherein R is a compound of the form (CH2)a-Z-(CH2)b„ wherein a>0, b>7, and Z is any chemical functionality of interest. 14. The film of Claim 13, wherein Z is selected from the group consisting of sulfones, lactams, and urea. 15. The film of Claim 1 , wherein there are two or more self-assembling monolayers with different chemical properties. 16. The film of Claim 1, wherein a first self- assembling monolayer is hydrophobic, and a second self- assembling monolayer is hydrophilic. 17. A method of making a film with a self- assembling monolayer pattern comprising stamping a pattern of self-assembling monolayers on a polymer film coated with metal. 18. The method of Claim 17, wherein the metal is selected from the group consisting of gold, silver, nickel, platinum, aluminum, iron, copper, or zirconium. 19. The method of Claim 17, wherein the metal is gold. 20. The method of Claim 19, wherein the gold coating is between approximately 1 nanometer and 1000 nanometers in thickness. 21. The method of Claim 18, wherein the polymer film is polyethylene-terephthalate, acrylonitrile-butadiene- styrene, acrylonitrile-methyl acrylate copolymer, cellophane, cellulosic polymers such as ethyl cellulose, cellulose acetate, cellulose acetate butyrate, cellulose propionate, cellulose triacetate, cellulose triacetate, polyethylene, polyethylene - vinyl acetate copolymers, ionomers (ethylene polymers) polyethylene-nylon copolymers, polypropylene, methyl pentene polymers, polyvinyl fluoride, and aromatic polysulfones. 22. The method of Claim 21, wherein the polymer film is polyethylene-terephthalate. 23. The method of Claim 17, wherein the polymer film is optically transparent. 24. The method of Claim 17, wherein the polymer film has an optical transparency between 5% and 95%. 25. The method of Claim 17, wherein the polymer film has an optical transparency between approximately 20% and 80%. 26. The method of Claim 17, wherein the self- assembling monolayer is formed from compounds with the following general formula: X-R-Y wherein: X is reactive with the metal or metal oxide on the polymer film; R is a hydrocarbon chain; and Y is a compound with any property of interest. 27. The method of Claim 26, wherein: X is a asymmetrical or symmetrical disulfide (- R'SSR, -RSSR), sulfide (-R'SR, -RSR), diselenide (-R'Se- SeR), selenide (R'SeR, -RSeR), thiol (-SH), nitrile (-CN), isonitrile, nitro (-N02 ), selenol (-SeH), trivalent phosphorous compounds, isothiocyanate, xanthate, thiocarbamate, phosphine, thioacid or dithioacid, carboxylic acids, hydroxylic acids, and hydroxamic acids; R and R' are hydrocarbon chains which may optionally be interrupted by hetero atoms, and which may optionally be perfluorinated, and which are preferably non- branched; and Y is selected from the group consisting of hydroxy, carboxyl, amino, aldehyde, hydrazide, carbonyl, epoxy, or vinyl groups. 28. The method of Claim 26, wherein R is greater than 7 carbon atoms in length. 29. The method of Claim 26, wherein R is a compound of the form (CH2)a~Z-(CH2)b» wherein a≥O, b>7, and Z is any chemical functionality of interest. 30. The method of Claim 29, wherein Z is selected from the group consisting of sulfones, lactams, and urea. 31. The method of Claim 17, wherein there are two or more self-assembling monolayers with different chemical properties. 32. The method of Claim 17, wherein a first self- assembling monolayer is hydrophobic, and a second self- assembling monolayer is hydrophilic.

Inventors: EVERHART DENNIS S, WHITESIDES GEORGE M, EVERHART, DENNIS, S., WHITESIDES, GEORGE, M.
Applicants: EVERHART DENNIS S, WHITESIDES GEORGE M, EVERHART, DENNIS, S., WHITESIDES, GEORGE, M.
Application year: 1997
Main classification: G03F7
IPC codes: B05D1, B41M3, G03F7