Exhaust gas purifying catalyst and exhaust gas purifying method

Abstract: An exhaust gas purifying catalyst is formed of a first powder formed of porous particles supporting rhodium (Rh), and a second powder formed of porous particles supporting platinum (Pt) and a nitrogen oxides (NOx)-adsorbing material. The second powder and the first powder are present in a mixed state. In this catalyst, Rh is supported apart from Pt and the NOx adsorbent, so that reduction of the oxidizing performance of Pt is prevented, and so that the problems of poor compatibility between Rh and the NOx adsorbent is eliminated. The catalyst therefore maintains high NOx removing rate not only during an initial period but also after the endurance test.

Description: BACKGROUND OF THE INVENTION 1. Field of the invention The present invention relates to an exhaust gas purifying catalyst and an exhaust gas purifying method for purifying exhaust gas from an internal combustion engine of a motor vehicle or the like and, more particularly, to an exhaust gas purifying catalyst and an exhaust gas purifying method capable of efficiently removing nitrogen oxides (NOx) by reduction, from exhaust gas that contains an amount of oxygen in excess of the amount of oxygen required for complete oxidation of the reducing components of the exhaust gas, such as carbon monoxide (CO), hydrogen gas (H 2 ), hydrocarbon (HC) and the like. 2. Description of the Related Art Many conventional motor vehicles employ three-way catalysts that purify exhaust gas by simultaneously oxidizing CO and HC and reducing NOx in exhaust gas at a theoretical air-fuel ratio (stoichiometric ratio). In a widely known three-way catalyst of this type, a heat-resistant base member formed of, for example, cordierite, carries thereon a porous support layer formed of γ -alumina, and the porous support layer supports catalytic noble metals such as platinum (Pt) , rhodium (Rh) and the like. Recently, carbon dioxide (CO 2 ) in exhaust gas from internal combustion engines of motor vehicles and the like has become an issue in view of protection of global environments. A promising technology for reducing the amount of CO 2 emission from an internal combustion engine is a lean burn system, in which combustion is performed at a lean air-fuel ratio with an excessive amount of oxygen. The lean burn system reduces fuel consumption due to improved fuel efficiency and, therefore, reduces the amount of CO 2 produced by combustion. Since the conventional three-way catalysts achieve simultaneous oxidation of CO and HC and reduction of NOx in exhaust gas when the air-fuel ratio is substantially the stoichiometric ratio, the conventional three-way catalysts fail to sufficiently remove NOx by reduction in lean-burnt exhaust gas, which contains an excessive amount of oxygen. Therefore, there has been a need for development of a catalyst and an exhaust gas purifying system capable of removing NOx even in an excessive-oxygen atmosphere. The present applicant proposed in, for example, Japanese Patent Application Laid-Open No. Hei 5-317652, an exhaust gas purifying catalyst in which an alkaline earth metal, such as barium (Ba) or the like, and platinum (Pt) are supported by a porous support formed of alumina or the like. Using the exhaust gas purifying catalyst, NOx can be efficiently removed from lean-burnt exhaust gas from a lean burn system if the air-fuel ratio is controlled so that the air-fuel ratio shifts from a lean side to a stoichiometric/rich side in a pulsed manner. NOx is adsorbed by the alkaline earth metal (NOx adsorbent) on the lean side, and reacts with reducing components, such as HC, CO and the like, on the stoichiometric/rich side. It has been found that the aforementioned NOx-removing process using the exhaust gas purifying catalyst proceeds in three steps: the first step in which NO in exhaust gas is oxidized into NOx; the second step in which NOx is adsorbed by the NOx adsorbent; and the third step in which NOx released from the NOx adsorbent is reduced on the catalyst. However, in the conventional exhaust gas purifying catalysts, particle growth of platinum (Pt) occurs in a lean atmosphere, thereby reducing the number of catalytic reaction points. Therefore, the reactivity in the first and third steps inconveniently decrease. Rhodium (Rh) is known as a catalytic noble metal that has a less tendency to undergo particle growth in a lean atmosphere. However, the oxidizing capacity of Rh is considerably lower than that of Pt. Use of a combination of Pt and Rh may be considered. It is known that co-presence of Pt and Rh reduces the particle grow of Pt. With regard to combined use of Pt and Rh, it has been found that as the amount of Rh contained increases, the oxidizing capacity of Pt decreases, probably because Rh covers Pt surfaces. Therefore, as the Rh content increases, the reactivity of oxidation of NO into NOx in the first step decreases and the NOx-adsorbing rate in the second step also decreases. Another problem with Rh is low compatibility with NOx adsorbents. Co-presence of Rh and a NOx adsorbent results in insufficient performance of the NOx adsorbent and Rh. In addition, sulfur (S) components contained in fuel are oxidized into SO 2 , which is further oxidized on the catalyst into sulfates. If sulfates react with the NOx adsorbent, the NOx adsorbing capacity of the NOx adsorbent is lost, thereby impeding the removal of NOx by reduction. This undesired phenomenon is generally termed sulfur-poisoning of NOx adsorbent. SUMMARY OF THE INVENTION Accordingly, it is an object of the present invention to prevent a durability reduction due to the particle growth of platinum (Pt) by using rhodium (Rh) in addition to Pt and improve durability by preventing reduction of the NOx adsorbing and releasing performance of the NOx adsorbent. According to one aspect of the invention, there is provided an exhaust gas purifying catalyst including a first powder formed of porous particles supporting rhodium, and a second powder formed of porous particles supporting platinum and a nitrogen oxides-adsorbing material so that rhodium and platinum are supported apart from each other on the first and second powders, respectively. The second powder and the first powder are present in a mixed state. At least one of the first powder and the second powder may support at least one element selected from the group consisting of cobalt, iron and nickel. A hydrocarbon-adsorbing adsorbent may be provided adjacent to the first powder. The porous particles of the first powder may serve as the hydrocarbon-adsorbing adsorbent. The HC-adsorbing adsorbent may exist at an interface between the first powder and the second powder. The HC-adsorbing adsorbent may form a coating layer provided on a monolithic base member. At least the first powder is supported in the coating layer. According to still another aspect of the invention, there is provided an exhaust gas purifying method. In a step of the method, a catalyst having a first powder and a second powder is disposed in an exhaust gas passage. The first powder is formed of porous particles supporting rhodium, and the second powder is formed of porous particles supporting platinum and a nitrogen oxides-adsorbing material so that rhodium and platinum are supported apart from each other on the first and second powders, respectively. The first powder and the second powder are present in a mixed state. In another step, the nitrogen oxides-adsorbing material is allowed to adsorb nitrogen oxides in a lean atmosphere in which an excessive amount of oxygen is present. In still another step, the lean atmosphere is temporarily changed to a stoichiometric-rich atmosphere so as to cause reduction of nitrogen oxides released from the nitrogen oxides-adsorbing material. BRIEF DESCRIPTION OF THE DRAWINGS The foregoing and further objects, features and advantages of the present invention will become apparent from the following description of preferred embodiments with reference to the accompanying drawings, wherein like numerals are used to represent like elements and wherein: Fig. 1 is an illustration of the structure of an exhaust gas purifying catalyst of Example 1 of the invention; Fig. 2 is a graph indicating the relationship between the amount of Rh supported and the NO removing rate during an initial period; Fig. 3 is a graph indicating the relationship between the amount of Rh supported and the NO removing rate after the endurance test; Fig 4 is an enlarged illustration of the structure of an exhaust gas purifying catalyst of Comparative Example 1; Fig. 5 is an illustration of the structure of an exhaust gas purifying catalyst of Example 3 of the invention; Fig. 6 is a graph indicating the relationship between the amount of Rh supported and the NO removing rate during an initial period; Fig. 7 is a graph indicating the relationship between the amount of Rh supported and the NO removing rate after the endurance test; Fig. 8 is an illustration of the structure of an exhaust gas purifying catalyst of Example 6 of the invention; Fig. 9 is an illustration of the structure of an exhaust gas purifying catalyst of Comparative Example 3. DETAILED DESCRIPTION OF THE INVENTION In the exhaust gas purifying catalyst of the invention, rhodium (Rh) is present in the first powder, and platinum (Pt) and the nitrogen oxides adsorbing material (NOx adsorbent) are present in the second powder, and the first powder and the second powder are in a mixed state. That is, Pt and the NOx adsorbent are supported adjacent to each other, and Rh and Pt are supported apart from each other. The particle growth of Rh in a lean atmosphere is remarkably less than that of Pt. Therefore, the presence of Rh improves durability. Furthermore, since Rh is supported apart from the NOx adsorbent, the problem of poor compatibility between the two components is eliminated, so that performance deterioration of the NOx adsorbent and Rh is prevented. Furthermore, since Rh is separately supported, hydrogen, having a high reducing power, is produced from hydrocarbon (HC) and H 2 O in exhaust gas by Rh (water vapor reforming reaction). Hydrogen thus produced considerably contributes to the reduction of NOx and the desorption of sulfur oxides (SOx) from the NOx adsorbent which is subjected to sulfur-poisoning. Therefore, the reduction of NOx during rich pulses increases, and the sulfur-poisoning considerably decreases. Although the water vapor reforming activity of Rh is normally reduced by the presence of the NOx adsorbent, the exhaust gas purifying catalyst of the invention prevents this phenomenon and therefore allows water vapor reforming reaction by Rh to a maximum-possible level since Rh and the NOx adsorbent are supported apart from each other. Therefore, if the exhaust gas purifying catalyst of the invention is actually exposed to a lean atmosphere (lean burnt exhaust gas) having an excessive amount of oxygen, nitrogen monoxide (NO) is oxidized into NOx on Pt in the second powder, and NOx is rapidly adsorbed by the NOx adsorbent supported adjacent to Pt. Since Rh is supported apart from Pt, the inhibition of oxidizing capacity of Pt by Rh is prevented, so that NO is efficiently converted into NOx. Furthermore, since Rh is also apart from the NOx adsorbent, the deterioration of NOx adsorbing activity is prevented. HC and CO in exhaust gas react with oxygen present in an excessive amount by the catalytic reaction of Pt and Rh. Thus, HC and CO are readily removed by oxidation. In stoichiometric-rich atmospheres, NOx is released from the NOx adsorbent, and then reacts with HC and CO in exhaust gas by the catalytic reaction of Pt and Rh. Thus, NOx is removed by reduction into nitrogen gas (N 2 ). The NOx reducing performance is improved by the hydrogen produced by the water vapor reforming reaction shown as formula (1). The reaction of the formula (1) occurs by the rhodium(Rh), and when a first powder formed of zirconia supporting rhodium(Rh) is utilized, the water vapor reforming reaction is further accelerated. CnHm + 2nH 2 O → nCO 2 + (m/2 + 2n)H 2 In the exhaust gas purifying catalyst of the invention, it is preferable that at least one of the first powder and the second powder carry at least one element selected from cobalt (Co), iron (Fe) and nickel (Ni). These elements accelerate aqueous gas shift reaction expressed in formula (2), thereby accelerating generation of hydrogen. CO + H 2 O → CO 2 + H 2 With its strong reducing power, hydrogen reduces NOx, so that the exhaust gas purifying catalyst maintains a high NOx reducing performance even after the endurance test. Furthermore, hydrogen occurring in the vicinity of the NOx adsorbent reduces sulfates taken up by the NOx adsorbent, thereby reducing the degradation of the NOx adsorbent by sulfur-poisoning. The amount of the at least one of Co, Fe and Ni supported in the exhaust gas purifying catalyst is preferably in the range of 0.01-2.0 moles relative to 120 g of the porous particles, whether a single element or two or more elements are selected. If the amount is less than 0.01 mole relative to 120 g, no substantial effect is achieved. If the amount is greater than 2.0 moles relative to 120 g, no further improvement is achieved and the reaction of the catalytic noble metal may be reduced. The at least one element selected from Co, Fe and Ni may be supported on either the porous particles of the first powder or the porous particles of the second powder, and may also be supported on the porous particles of both powders. The porous particles carrying the at least one elements of Co, Fe and Ni may preferably support a promoter of at least one of silicon (Si) and magnesium (Mg). Provision of the promoter will further promote the hydrogen-producing reactions. The amount of the promoter supported on the porous particles is preferably within the range of 0.005-2.0 moles relative to 120 g of the porous particles. If the amount is less than 0.005 mole relative to 120 g, no substantial effect is achieved. If the amount is greater than 2.0 moles relative to 120 g, no further improvement is achieved. A particularly preferable range of the amount of the promoter is 0.01-0.5 mole relative to 120 g of the porous particles. Through closer investigation of the acting mechanism of the catalyst, it has become clear that in a rich atmosphere, reaction between water vapor and HC in exhaust gas is occured on the first powder, producing hydrogen, which in turn contributes to the reduction of NOx. That is, the water vapor reforming reaction with HC in exhaust gas occurs on the first powder, thereby producing hydrogen, which in turn reduces NOx released from the NOx adsorbent in a rich atmosphere. Therefore, the aforementioned reaction in the third step of the NOx-removing process is accelerated. In some cases, sulfur-poisoning of NOx adsorbent occurs, wherein SOx in exhaust gas react with the NOx adsorbent to produce sulfuric acid salts whereby the NOx adsorbing capacity is lost. However, due to the production of hydrogen, SOx in exhaust gas is reduced so that the sulfur-poisoning is considerably prevented. Furthermore, the sulfur-poisoned NOx adsorbent is also reduced by hydrogen, so that the NOx adsorbing capacity is recovered. Therefore, high NOx adsorbing capacity of the NOx adsorbent is maintained, so that the reaction in the third step is accelerated. The reaction between water vapor and HC, that is, a hydrogen-producing reaction, hardly occurs in a lean atmosphere containing an excessive amount of oxygen because there is almost no HC left in the lean burnt exhaust gas. In a lean atmosphere, oxygen present in an excessive amount oxidizes almost the entire amount of HC into H 2 O and CO 2 . If a little amount of hydrogen is produced, hydrogen immediately reacts with oxygen present in an excessive amount to produce H 2 O. Therefore, the aforementioned hydrogen-producing reactions are not fully enjoyed in purifying exhaust gas from a system, such as a lean burn engine, wherein lean atmospheres occur in most operating conditions. Therefore, it is preferred that a HC-adsorbing adsorbent be provided adjacent to the first powder. Thereby, a large amount of HC present in a rich atmosphere is adsorbed to the HC-adsorbing adsorbent. In a lean atmosphere, HC is released from the HC-adsorbing adsorbent, so that HC reacts with water vapor on the first powder, by reaction of Rh, to produce hydrogen. Thus, provision of the HC-adsorbing adsorbent enables production of hydrogen even in a lean atmosphere, so that NOx is reduced, thereby improving the NOx removing performance. Furthermore, sulfur-poisoned NOx adsorbent and, further, SOx are also reduced by hydrogen, so that the sulfur-poisoning of the NOx adsorbentis eliminated and the NOx adsorbing capacity is recovered. In addition, further sulfur-poisoning is prevented. Therefore, the NOx removing performance is significantly improved. A representative example of the HC-adsorbing adsorbent is zeolite. There are various types of zeolites, such as Y type, A type, X type, ZSM-5, silicalite, mordenite, ferrierite, and the like. All of these types have high HC-adsorbing capacity. Among them, Y-type zeolite, ZSM-5, silicalite and mordenite have particularly high HC-adsorbing capacity. Therefore, it is preferred to use a zeolite selected from those zeolites. To increase the hydrogen production rate by increasing the rate of reaction between HC and water vapor, it is necessary that the HC-adsorbing absorbent, which supplies HC in lean atmospheres, be adjacent to the first powder, which offers reaction active points for the reaction between HC and water vapor. This requirement may be achieved by employing first powder in which porous particles are served as a HC-adsorbing adsorbent. Such first powder can be formed by, for example, supporting or fixing at least Rh on porous particles formed of zeolite. The thus-produced first powder will adsorb HC in rich atmospheres, and releases HC in lean atmospheres, which immediately reacts with water vapor on the first powder. Therefore, the reaction between HC and water vapor readily occurs on the first powder to produce hydrogen not only in rich atmospheres but also in lean atmospheres. The aforementioned requirement may also be achieved by disposing a HC adsorbent at an interface between the first powder and the second powder. For example, a HC-adsorbing adsorbent in the form of particles is mixed with the first powder and the second powder, to form a catalyst. In this manner, the HC-adsorbing adsorbent is disposed at the interface between the first powder and the second powder, so that HC is adsorbed to the HC-adsorbing adsorbent in rich atmospheres, and is released therefrom in lean atmospheres to immediately react with water vapor on the first powder to produce hydrogen. In still another possible manner, a HC-adsorbing adsorbent-formed coating layer is provided on a monolithic base member, the first powder is supported onto the coating layer. In some cases, such a coating layer may be formed from the first powder and HC-adsorbing adsorbent powder. In the thus-produced catalyst, HC is adsorbed to the coating layer in rich atmospheres, and is released therefrom in lean atmospheres and reacts with water vapor on the first powder. Therefore, the reaction between HC and water vapor readily occurs on the first powder to produce hydrogen not only in rich atmospheres but also in lean atmospheres. In an example method for producing an exhaust gas purifying catalyst containing such a HC-adsorbing adsorbent, the first powder is prepared by supporting or fixing Rh onto a HC-adsorbing adsorbent powder. The first powder is mixed with the second powder and the mixture is formed into pellets, thereby producing a desired catalyst in the form of pellets. In another example method, a monolithic base or a honeycomb base formed of a metal foil is coated with a slurry containing a mixture of the first and second powders as a main component, and the coated base is baked, thereby producing a desired catalyst. Furthermore, a mixture of the f irst powder containing no such HC-adsorbing adsorbent, the second powder and a HC-adsorbing adsorbent powder, may be formed into pellets or a coating layer. Further, After a monolithic base is coated with a HC-adsorbing adsorbent, a mixture of the first powder and the second powder may be supported on the coating layer. To support the first powder and second powder on the HC adsorbent, various methods may be employed, for example: a deposition method in which zeolite is suspended in an aqueous solution of a zirconium salt or an aluminum salt, and an alkali is added to shift the pH to a base side so that precipitation occurs on the zeolite; a sol-gel method in which an alkoxide of zirconium or aluminum is hydrolyzed so that the hydroxide of zirconium or aluminum is supported on zeolite, and the like Normally, exhaust gas purifying catalysts are provided in the form of a honeycomb, wherein a cordierite or metal-made honeycomb base is coated with a support material, such as alumina, and the coating layer supports a catalytic metal or a NOx adsorbent. A conventional mainstream method for supporting a noble metal in a catalyst is an adsorption-support method in which a base having a coating layer is dipped into an aqueous solution of a noble metal compound, and then pulled up, dried and baked. In the adsorption-support method, noble metal ions in the aqueous solution are fixed in a surface portion of the coating layer, so that substantially no noble metal ions are contained in the aqueous solution that penetrates into an interior portion. Therefore, noble metal is supported only in a surface layer of the coating layer. This is favorable in view of catalytic reactions. In the above-described catalyst wherein Rh and the NOx adsorbent are supported apart from each other, the noble metal and the NOx adsorbent are each supported on powder, and the powder is applied as a coating onto a base to form a desired catalyst. Therefore, the noble metal in this separate-support catalyst is supported uniformly in the entire coating layer. In the exhaust gas purifying catalyst of the invention, HC and CO are oxidized on Pt in lean atmospheres containing excessive amounts of oxygen. Simultaneously, there occur the first step wherein NO in exhaust gas is oxidized into NOx and the second step wherein NOx is adsorbed by the NOx adsorbent. Since Pt and the NOx adsorbent are supported adjacent to each other and Rh is supported apart from Pt, the problem of a reduction in the oxidizing performance of Pt due to the presence of Rh in proximity does not arise. Therefore, the first and second steps smoothly proceed. Upon a temporary change to a stoichiometric-rich atmosphere, NOx is released from the NOx adsorbent and reacts with HC and CO in exhaust gas by the catalytic reactions of Pt and Rh. NOx, and HC and CO are thus removed by reduction and oxidation. In the exhaust gas purifying catalyst of the invention, NO is oxidized into NO 2 on Pt in the second powder, and NOx is rapidly adsorbd by the NOx adsorbent supported adjacent to Pt, in a lean atmosphere containing an excessive amount of oxygen. Since Pt and Rh are supported apart from each other, inhibition of the oxidizing performance of Pt by Rh is prevented and, therefore, NO is smoothly converted into NO 2 . Furthermore, since the NOx adsorbent is supported apart from Rh, the deterioration of the NOx removing performance is prevented. Therefore, NOx is smoothly adsorbed by the NOx adsorbent and thereby prevented from being released to outside. HC and CO in exhaust gas react with oxygen present in an excessive amount by catalytic reactions of Pt and Rh. HC and CO are thus readily removed by oxidation. When the atmosphere is changed to a stoichiometric-rich atmosphere, NOx is released from the NOx adsorbent, and reacts with HC and CO in the exhaust gas by the catalytic reactions of Pt and Rh and, in addition, reacts with hydrogen produced on the second powder, thereby turning into N 2 . Thus, NOx is removed by reduction. Even if Pt particle growth occurs so that the reducing power decreases, the great reducing power of Rh still efficiently removes NOx by reduction. HC in exhaust gas adsorbs to and accumulates on the HC-adsorbing adsorbent in a stoichiometric-rich atmosphere. When the atmosphere becomes a lean atmosphere containing an excessive amount of oxygen, HC is released from the HC-adsorbing adsorbent, and reacts with water vapor to produce hydrogen, which in turn reduces NOx and, further, reduces the sulfur-poisoned NOx adsorbent. Therefore, the NOx adsorbing capacity is recovered. Since SOx is reduced by hydrogen, further sulfur-poisoning of the NOx adsorbent is prevented. Therefore, the exhaust gas purifying catalyst of the invention is able to produce hydrogen not only in rich atmospheres but also in lean atmospheres, thereby considerably improving the NOx removing performance. The porous particles, whether for the first powder or the second powder, may be selected from alumina, silica, titania, zirconia, silica-alumina, zeolite and the like. Any one or more of these materials may be selected. If more than one materials are selected, they may be used in a mixture or a composite form. In view of heat resistance, and the good compatibility of zirconia with Rh, it is preferred that zirconia is used for the first powder and alumina is used for the second powder. If zirconia is used for the first powder, the water vapor reforming reaction of Rh remarkably improves. The particle diameter of the porous particles of the first and second powders is preferably within the range of 1-100 µ m. If the particle diameter is smaller than 1 µm, it becomes difficult to achieve the effect of the separate supporting of Rh and Pt. If the particle diameter is larger than 100 µ m, the interreaction between the first powder and the second powder is inconveniently reduced. The amount of Rh supported in the first powder is preferably within the range of 0.05-20 g relative to 120 g of the porous particles. If the amount of Rh supported is less than 0.05 g relative to 120 g of the porous particles, the durability deteriorates. If it is more than 20 g relative to 120 g, no further improvement of the effect is achieved and a cost increase may result. A particularly preferred range of the amount of Rh supported in the first powder is 0.1-10 g relative to 120 g of the porous particles. It is also possible to support palladium (Pd), iridium (Ir) or the like in the first powder, in addition to Rh. The amount of such material may be determined such that the total amount, including the amount of Rh, is within the aforementioned range. The amount of Pt supported in the second powder is preferably within the range of 0.1-10 g relative to 120 g of the porous particles. If the amount of Pt supported is less than 0.1 g relative to 120 g of the porous particles, the removing rates for HC, CO and NOx decrease. If it is more than 10 g relative to 120 g, no further improvement of the effect is achieved and a cost increase may result. It is also possible to support Pd in the second powder, in addition to Pt. Preferably, the amount of Pd is determined such that the total amount of Pt and Pd is within the range of 0.1-10 g relative to 120 g of the porous particles. The NOx adsorbent may be formed of at least one element selected from alkaline metals, alkaline earth metals and rare earth metals. Examples of the alkali metals include lithium (Li), sodium (Na), potassium (K), cesium (Cs), and the like. The alkaline earth metals'refer to elements of the 2A family according to the periodic table. Examples of the alkaline earth metals include magnesium (Mg), calcium (Ca), strontium (Sr), barium (Ba), and the like. Examples of the rare earth metals include lanthanum (La), cerium (Ce), praseodymium (Pr), and the like. The amount of the NOx adsorbent supported in the second powder is preferably within the range of 0.05-3 moles relative to 120 g of the porous particles. If the amount of the NOx adsorbent in the second powder is less than 0.05 mole relative to 120 g of the porous particles, the NOx removing rate decreases. If the amount is more than 3 moles relative to 120 g of the porous particles, no further improvement is achieved. A particularly preferred range of the amount of the NOx adsorbent in the second powder is 0.05-0.5 mole relative to 120 g of the porous particles. The mixing ratio between the first powder and the second powder is preferably within the range of first powder : second powder = 0.05:1 to 1:1, on the basis of weight ratio between Rh and Pt or the total weight of Pt and Pd. If alumina is used as the porous particles of both the first powder and the second powder, the mixing ratio is preferably within the range of first powder second powder = 0.1:1 to 2:1, on an alumina weight ratio basis. If the mixing ratio is outside these ranges, there may occur problems similar to those caused by inappropriate amounts of Rh and Pt. To form an exhaust gas purifying catalyst from a mixture of the first powder and the second powder, the mixture may be formed into pellets by a standard method, thereby producing a catalyst in the form of pellets. Furthermore, a slurry containing a mixture of the first and second powders as a main component may be applied as a coating onto a cordierite or metal foil-formed honeycomb base, which is then baked to produce a monolithic catalyst. In the exhaust gas purifying method of the invention, HC and CO are removed by oxidation on Pt in the second powder in a lean atmosphere containing an excessive amount of oxygen. Simultaneously, NO is oxidized into NOx, which is rapidly adsorbed by the NOx adsorbent supported adjacent to Pt. Since Pt is supported apart from Rh, inhibition of the oxidizing performance of Pt by Rh is prevented and, therefore, NO is smoothly converted into NOx. Furthermore, since the NOx adsorbent is supported apart from Rh, the deterioration of the NOx removing performance is prevented. Therefore, NOx is smoothly adsorbed by the NOx adsorbent and thereby prevented from being released to outside. HC and CO in exhaust gas react with oxygen present in an excessive amount by catalytic reactions of Pt and Rh. HC and CO are thus readily 'removed by oxidation. When the atmosphere is temporarily changed to a stoichiometric-rich atmosphere, NOx is released from the NOx adsorbent, and reacts with HC and CO in the exhaust gas by the catalytic reactions of Pt and Rh and, in addition, reacts with hydrogen produced through the reactions of formulas (1) and (2), which are accelerated by at least one element selected from Co, Fe and Ni. NOx is thereby reduced into N 2 . Even if Pt particle growth occurs so that the reducing power decreases, the great reducing power of Rh still efficiently removes NOx by reduction. EXAMPLES The invention will be further described in detail with reference to Examples and Comparative Examples, and the accompanying drawings. (1) Examples of First Series EXAMPLE 1 <Preparation of First Powder> Alumina powder having an average particle diameter of 5 µ m was impregnated with a predetermined amount of a rhodium nitrate aqueous solution of a predetermined concentration, and then dried at 110 °C for 3 hours, and baked at 250 °C for 2 hours, thereby supporting Rh in the alumina powder. As for the amount of Rh supported, four different levels were selected, that is, 0.1 g, 0.5 g, 1.0 g and 2.0 g relative to 120 g of the alumina powder. Thus, four types of the first powders were prepared. <Preparation of Second Powder> Alumina powder having an average particle diameter of 5 µ m was impregnated with a predetermined amount of a barium acetate aqueous solution of a predetermined concentration, and then dried at 110 °C for 3 hours, and baked at 500 °C for 2 hours, thereby supporting Ba in the alumina powder. The amount of Ba supported was 0.4 mole relative to 120 g of the alumina powder. Subsequently, the thus-obtained Ba-carrying alumina powder was impregnated with a 15-g/L ammonium bicarbonate aqueous solution, and then dried at 110 °C for 3 hours. Thereby, Ba was converted into barium carbonate and supported uniformly in the alumina powder. The Ba/alumina powder was impregnated with a predetermined amount of a dinitrodiammine platinum nitrate aqueous solution of a predetermined concentration, and dried at 110 °C for 3 hours, and then dried at 250 °C for 2 hours, thereby supporting Pt in the powder. The amount of Pt supported was 2.0 g relative to 120 g of the alumina powder. The second powder was thus prepared. <Preparation of Catalyst> Equal amounts of the first powder and the second powder by weight ratio were uniformly mixed, and then formed into pellets by a standard method, thereby four types of pellet catalysts were prepared. The structure of the pellet catalysts is schematically shown in Fig. 1. <Evaluation Test> The obtained pellet catalyst of each type was disposed in an evaluation test device, and model gases described in Table 1 were passed through. More specifically, a rich model gas and a lean model gas were alternately allowed to flow at an in-coming gas temperature of 350 °C, at a flow rate of 2 L/min for two minutes respectively. The transitional NO removing rate of each catalyst was determined from the difference between the NO concentration in the gas coming in to the catalyst and the NO concentration in the gas going out from the catalyst. Results are indicated in Fig. 2. Atmosphere O 2 NO C 3 H 6 CO H 2 He Rich 0.25% - 710ppm 1.06% 0.25% balance Lean 7.9% 570ppm 1200ppm 0.19% 0.05% balance Endurance test was performed by allowing endurance rich and lean model gases shown in Table 2 to flow for 10 hours at an in-coming gas temperature of 800 °C while switching between the two gases in a pattern of 1 minutes for the rich gas and 4 minutes for the lean gas. After that, the transitional NO removing rates were determined in the manner described above. Results are indicated in Fig. 3. Atmosphere O 2 NO C 3 H 6 CO H 2 H 2 O He Rich 0.16% 0.15% 650ppm 0.70% 0.20% 3% balance Lean 7.9% 0.14% 620ppm 780ppm - 3% balance EXAMPLE 2 Four types of the first powders were prepared in substantially the same manner as in Example 1, except that zirconia powder having an average particle diameter of 5 µm was used instead of the alumina powder. The first powder of each type was mixed with the second powder substantially the same as in Example 1, thereby preparing four types of pellet catalysts. Using 2.0 g of each of the obtained pellet catalysts of Example 2, the NO removing rates during an initial period and after the endurance test were determined substantially in the same manner as in Example 1. Results are indicated in Figs. 2 and 3. COMPARATIVE EXAMPLE 1 Fig. 4 schematically illustrates the structure of an exhaust gas purifying catalyst of Comparative Example 1. <Preparation of Powder> Alumina powder having an average particle diameter of 5 µ m was impregnated with a predetermined amount of a barium acetate aqueous solution of a predetermined concentration, and then dried at 110 °C for 3 hours, and baked at 500 °C for 2 hours, thereby supporting Ba in the alumina powder. The amount of Ba supported was 0.2 mole relative to 120 g of the alumina powder. Subsequently, the thus-obtained Ba-carrying alumina powder was impregnated with a 15-g/L ammonium bicarbonate aqueous solution, and then dried at 110 °C for 3 hours. Thereby, Ba was converted into barium carbonate and supported uniformly in the alumina powder. The Ba/alumina powder was impregnated with a predetermined amount of a dinitrodiammine platinum nitrate aqueous solution of a predetermined concentration, and dried at 110 °C for 3 hours, and then dried at 250 °C for 2 hours, thereby supporting Pt in the powder. The amount of Pt supported was 1.0 g relative to 120 g of the alumina powder. Subsequently, the obtained Pt-carrying Ba/alumina powder was impregnated with a predetermined amount of a rhodium nitrate aqueous solution of a predetermined concentration, and then dried at 110 °C for 3 hours, and baked at 250 °C for 2 hours, thereby supporting Rh in the powder. As for the amount of Rh supported, four different levels were selected, that is, 0.05 g, 0.25 g, 0.5 g and 1.0 g relative to 120 g of the alumina powder. Thus, four types of the catalyst powders were prepared. <Preparation of Catalyst> Each type of catalyst powder was formed into pellets by the standard method, thereby preparing four types of pellet catalysts. Using the obtained pellet catalysts of Comparative Example 1, the NO removing rates both during an initial period and after the endurance test were determined substantially in the same manner as in Example 1. Results are indicated in Figs. 2 and 3. <Evaluation> As indicated from Figs. 2 and 3, the NO removing rate decreased as the amount of Rh supported increased in Comparative Example 1, whereas in Examples 1 and 2, the NO removing rate increased as the amount of Rh supported increased. It is clear that this difference was achieved due to the separate supporting of Rh and Pt in Examples 1 and 2. Furthermore, it is also indicated that as the porous particles of the first powder, the zirconia powder (Example 2) exhibited a higher NO removing rate than the alumina powder (Example 1). This tendency is similarly indicated in Figs. 2 and 3 although the difference in Fig. 3 is smaller than that in Fig. 2. That is, it is clearly indicated that the exhaust gas purifying catalysts of these examples exhibited high NO removing rates both during the initial period and after the endurance test. Although in the foregoing examples, the pellet catalysts were formed and investigated, it should be apparent that a monolithic catalyst formed by coating a cordierite or metal foil-formed honeycomb base with a coating layer containing a mixture of the first powder and the second powder as a main component will achieve substantially the same advantages as achieved by the pellet catalysts. (2) Example of Second Series EXAMPLE 3 <Preparation of First Powder> Alumina powder having an average particle diameter of 5 µ m was impregnated with a predetermined amount of a rhodium nitrate aqueous solution of a predetermined concentration, and then dried at 110 °C for 3 hours, and baked at 250 °C for 2 hours, thereby supporting Rh in the alumina powder. The amount of Rh supported was 0.3 g relative to 120 g of the alumina powder. <Preparation of Second Powder> Alumina powder having an average particle diameter of 5 µ was impregnated with a predetermined amount of a barium acetate aqueous solution of a predetermined concentration, and then dried at 110 °C for 5 hours, and baked at 500 °C for 2 hours, thereby supporting Ba in the alumina powder. The amount of Ba supported was 0.3 mole relative to 120 g of the alumina powder. Subsequently, the thus-obtained Ba-carrying alumina powder was impregnated with 1.2 L of a 15-g/L ammonium bicarbonate aqueous solution, and then dried at 110 °C for 5 hours. Thereby, Ba was converted into barium carbonate and supported uniformly in the alumina powder. The Ba/alumina powder was impregnated with a predetermined amount of a dinitrodiammine platinum nitrate aqueous solution of a predetermined concentration, and dried at 110 °C for 2 hours, and then baked at 400 °C for 2 hours, thereby supporting Pt in the powder. The amount of Pt supported was 2.0 g relative to 120 g of the alumina powder. The second powder was thus prepared. <Supporting of Transition Metal> Equal amounts of the first powder and the second powder were mixed. The mixed powder was impregnated with a cobalt nitrate aqueous solution, and dried at 110 °C for 5 hours and then baked at 400 °C at 2 hours, thereby supporting Co in the powder. The amount of Co supported was 0.1 mole relative to 120 g of the mixed powder. The obtained powder was formed into pellets by the standard method, thereby preparing a catalyst of Example 3. Fig. 5 schematically illustrates the structure of the pellet catalyst. <Evaluation Test> The obtained pellet catalyst was disposed in an evaluation test device, and the model gases described in Table 1 were passed through. More specifically, the rich model gas and the lean model gas were separately allowed to flow at an in-coming gas temperature of 350 °C, at a flow rate of 2 L/min. The amount of NO adsorbed and the amount of NO reduced were determined for each catalyst from the difference between the NO concentration in the gas coming in to the catalyst and the NO concentration in the gas going out from the catalyst. Results are shown in Table 4. Endurance test was performed by allowing endurance rich and lean model gases shown in Table 3 to flow for 8 hours at an in-coming gas temperature of 600 °C while switching between the two gases in a pattern of 1 minutes for the rich gas and 4 minutes for the lean gas. After that, the amount of sulfur-poisoning (S-poisoning) was determined from the element quantitative analysis of each catalyst after the endurance test. Using the catalyst after the.endurance test, the amount of NO adsorbed and the amount of NO reduced were determined in the manner as described above. Results are shown in Table 4. Atmosphere O 2 % NO % C 3 H 6 ppm CO H 2 % SO 2 ppm H 2 O % N 2 Rich 0.16 0.15 650 0.70% 0.20 160 3 balance Lean 7.9 0.14 620 780ppm - 160 3 balance EXAMPLE 4 A mixed powder was prepared substantially in the same manner as in Example 3, using a first powder substantially the same as in Example 3 and a second powder that was prepared substantially the same manner as in Example 3, except that a mixed aqueous solution of barium acetate and cobalt nitrate was used instead of the barium acetate aqueous solution. The mixed powder was directly used to form a pellet catalyst of Example 4. The amounts of Ba and Co in the second powder were 0.3 mole and 0.1 mole, respectively, relative to 120 g of the alumina powder. Using the obtained pellet catalyst of Example 4, the amount of NO adsorbed and the amount of NO reduced and the amount of sulfur-poisoning both during the initial period and after the endurance test were determined in substantially the same as in Example 3. Results are shown in Table 4. EXAMPLE 5 Alumina powder having an average particle diameter of 5 µ m was impregnated with a predetermined amount of a cobalt nitrate aqueous solution of a predetermined concentration, and then dried at 110 °C for 5 hours, and baked at 500 °C for 2 hours. The amount of Co supported was 0.1 mole relative to 120 g of the alumina powder. The Co-carrying alumina powder was impregnated with a predetermined amount of a rhodium nitrate aqueous solution of a predetermined concentration, and dried at 110 °C for 3 hours and then baked at 250 °C for 2 hours, thereby preparing the first powder. Using the thus-prepared first powder and the second powder prepared substantially in the same manner as in Example 3, a mixed powder was prepared substantially in the same manner as in Example 3. The mixed powder was directly used to prepare a pellet catalyst of Example 5. Using the obtained pellet catalyst of Example 5, the amount of NO adsorbed and the amount of NO reduced and the amount of sulfur-poisoning both during the initial period and after the endurance test were determined in substantially the same as in Example 3. Results are shown in Table 4. COMPARATIVE EXAMPLE 2 Alumina powder having an average particle diameter of 5 µ m was impregnated with a predetermined amount of a barium acetate aqueous solution of a predetermined concentration, and then dried at 110 °C for 3 hours, and baked at 500 °C for 2 hours, thereby supporting Ba in the alumina powder. The amount of Ba supported was 0.3 mole relative to 120 g of the alumina powder. Subsequently, the thus-obtained Ba-carrying alumina powder was impregnated with a 15-g/L ammonium bicarbonate aqueous solution, and then dried at 110 °C for 3 hours. Thereby, Ba was converted into barium carbonate and supported uniformly in the alumina powder. The Ba/alumina powder was impregnated with a predetermined amount of a dinitrodiammine platinum nitrate aqueous solution of a predetermined concentration, and dried at 110 °C for 3 hours, and then dried at 250 °C for 2 hours, thereby supporting Pt in the powder. The amount of Pt supported was 2.0 g relative to 120 g of the alumina powder. Subsequently, the obtained Pt-carrying Ba/alumina powder was impregnated with a predetermined amount of a rhodium nitrate aqueous solution of a predetermined concentration, and then dried at 110 °C for 3 hours, and baked at 250 °C for 2 hours, thereby supporting Rh in the powder. The amount of Rh supported was 0.3 g relative to 120 g of the alumina powder. The obtained catalyst powder was formed into pellets by the standard method, thereby preparing a pellet catalyst of Comparative Example 2. Using the obtained pellet catalyst of Comparative Example 2, the amount of NO adsorbed and the amount of NO reduced and the amount of sulfur-poisoning both during the initial period and after the endurance test were determined in substantially the same as in Example 3. Results are shown in Table 4. <Evaluation> NO adsorbd ((10 -4 mole) NO reduced ((10 -4 mole) S-poisoning after endurance test (wt.%) Initial After Initial After period endurance test period endurance test Ex. 3 1.6 1.4 0.43 0.32 0.58 Ex. 4 1.7 1.5 0.45 0.33 0.42 Ex. 5 1.7 1.5 0.44 0.31 0.44 Com. Ex. 2 1.7 1.2 0.46 0.20 1.04 As can be seen in Table 4, the catalysts of the examples improved in the amount of NO adsorbed and the amount of NO reduced after the endurance test, compared with Comparative Example 2. Particularly, the improvement in the amount of NO reduced was great. Furthermore, it can be seen that the catalyst of the examples considerably reduced the sulfur-poisoning, compared with Comparative Example 2. That is, it is clear that the exhaust gas purifying catalysts of the examples achieved high NO removing rates both during the initial period and after the endurance test. Although the above examples have been described in conjunction with employment of Co as a promoter, it should be noted that employment of Fe or NI as a single component, instead of Co, or combinations of two or three components, achieved substantially the same results. Although the examples have been described in conjunction with the pellet catalysts, it should be apparent that a monolithic catalyst formed by coating a cordierite or metal foil-formed honeycomb base with a coating layer containing a mixture of the first powder and the second powder as a main component will achieve substantially the same advantages as achieved by the pellet catalysts. (3) Examples of Third Series < Preparation Example for a honey comb catalyst> 240 parts by weight of a first powder and 320 parts by weight of a second powder were uniformly mixed, and further mixed with 235 parts by weight of a 40-wt.% aluminum nitrate nonahydrate aqueous solution, 15 parts by weight of an alumina-based binder and 540 parts by weight of water, thereby preparing a slurry. A prepared cordierite-made honeycomb base member was dipped into the slurry, and pulled up therefrom. After an extraneous amount of slurry was blown off, the honeycomb base was dried and baked, thereby forming coating layers. A honeycomb catalyst was thereby prepared. The coating layer formed was 290 g relative to 1 liter of the honeycomb base member. <Evaluation Test> The obtained honeycomb catalyst was disposed in an evaluation test device, and the model gases described in Table 1 were passed through. More specifically, the rich model gas and the lean model gas were alternately allowed to flow at an in-coming gas temperature of 350 °C, at a flow rate of 2 L/min for two minutes respectively. The transitional NO removing rate of the catalyst was determined from the difference between the NO concentration in the gas coming in to the catalyst and the NO concentration in the gas going out from the catalyst. Endurance test was performed by allowing the endurance rich and lean model gases shown in Table 2 to flow for 10 hours at an in-coming gas temperature of 800 °C while switching between the two gases in a pattern of 1 minutes for the rich gas and 4 minutes for the lean gas. After that, the transitional NO removing rates were determined in the manner described above. EXAMPLE 6 <Preparation of First Powder> Alumina powder having an average particle diameter of 5 µm was impregnated with a predetermined amount of a rhodium nitrate aqueous solution of a predetermined concentration, and then dried at 110 °C for 3 hours, and baked at 250 °C for 2 hours, thereby supporting Rh in the alumina powder. As for the amount of Rh supported, four different levels were selected, that is, 0.1 g, 0.5 g, 1.0 g and 2.0 g relative to 120 g of the alumina powder. Thus, four types of the first powders were prepared. <Preparation of Second Powder> Alumina powder having an average particle diameter of 5 µ m was impregnated with a predetermined amount of a barium acetate aqueous solution of a predetermined concentration, and then dried at 110 °C for 3 hours, and baked at 500 °C for 2 hours, thereby supporting Ba in the alumina powder. The amount of Ba supported was 0.3 mole relative to 120 g of the alumina powder. Subsequently, the thus-obtained Ba-carrying alumina powder was impregnated with a 15-g/L ammonium bicarbonate aqueous solution, and then dried at 110 °C for 3 hours. Thereby, Ba was converted into barium carbonate and supported uniformly in the alumina powder. The Ba/alumina powder was impregnated with a predetermined amount of a dinitrodiammine platinum nitrate aqueous solution of a predetermined concentration, and dried at 110 °C for 3 hours, and then dried at 250 °C for 2 hours, thereby supporting Pt in the powder. The amount of Pt supported was 2.0 g relative to 120 g of the alumina powder. The second powder was thus prepared. <Preparation of Catalyst> Equal amounts of the first powder and the second powder by weight ratio were uniformly mixed, and then formed into honeycomb catalysts substantially in the same manner as in the Preparation Example. The amounts of Rh supported relative to 1 litter of the honeycomb catalystwere 0.05 g, 0.25 g, 0.5 g and 1.0 g. Fig. 8 schematically illustrates the structure of a coating layer of the honeycomb catalysts. Referring to Fig. 8, particles of the first powder (alumina powder) 5 support Rh 6, and particles of the second powder (Ba/alumina powder) 7 supports Pt 8. Thus, Pt and Rh are supported apart from each other. Using the obtained honeycomb catalysts, the NO removing rates both during the initial period and after the endurance test were determined substantially in the same manner as in the Evaluation Test. Results are indicated in Figs. 6 and 7. EXAMPLE 7 Four types of the first powders were prepared in substantially the same manner as in Example 6, except that zirconia powder having an average particle diameter of 5 µ m was used instead of the alumina powder. The first powder of each type was mixed with the second powder substantially the same as in Example 6, thereby preparing four types of honeycomb catalysts. Using the obtained honeycomb catalysts of Example 7, the NO removing rates during the initial period and after the endurance test were determined substantially in the same manner as in Example 6. Results are indicated in Figs. 6 and 7. COMPARATIVE EXAMPLE 3 Alumina powder having an average particle diameter of 5 µ m was impregnated with a predetermined amount of a barium acetate aqueous solution of a predetermined concentration, and then dried at 110 °C for 3 hours, and baked at 500 °C for 2 hours, thereby supporting Ba in the alumina powder. The amount of Ba supported was 0.3 mole relative to 120 g of the alumina powder. Subsequently, the thus-obtained Ba-carrying alumina powder was impregnated with a 15-g/L ammonium bicarbonate aqueous solution, and then dried at 110 °C for 3 hours. Thereby, Ba was converted into barium carbonate and supported uniformly in the alumina powder. The Ba/alumina powder was impregnated with a predetermined amount of a dinitrodiammine platinum nitrate aqueous solution of a predetermined concentration, and dried at 110 °C for 3 hours, and then dried at 250 °C for 2 hours, thereby supporting Pt in the powder. The amount of Pt supported was 2 g relative to 120 g of the alumina powder. Subsequently, the obtained Pt-carrying Ba/alumina powder was impregnated with a predetermined amount of a rhodium nitrate aqueous solution of a predetermined concentration, and then dried at 110 °C for 3 hours, and baked at 250 °C for 2 hours, thereby supporting Rh in the powder. As for the amount of Rh supported, four different levels were selected, that is, 0.05 g, 0.25 g, 0.5 g and 1.0 g relative to 120 g of the alumina powder. Thus, four types of the catalyst powders were prepared. Fig. 9 schematically illustrates the structure of the exhaust gas purifying catalysts (conventional type) of Comparative Example 3. Referring to Fig. 9, particles of the Ba/alumina powder 9 support Pt 10 and Rh 11 adjacent to each other. Each type of catalyst powder was formed into pellets by the standard method, thereby preparing four types of pellet catalysts. Using the obtained pellet catalysts of Comparative Example 3, the NO removing rates both during the initial period and after the endurance test were determined substantially in the same manner as in Example 6. Results are indicated in Figs. 6 and 7. <Evaluation> As indicated from Figs. 6 and 7, the NO removing rate decreased as the amount of Rh supported increased in Comparative Example 3, whereas in Examples 6 and 7, the NO removing rate increased as the amount of Rh supported increased. It is clear that this difference was achieved due to the separate supporting of Rh and Pt in Examples 6 and 7. Furthermore, it is also indicated that as the porous particles. of the first powder, the zirconia powder (Example 7) exhibited a slightly higher NO removing rate than the alumina powder (Example 6). This tendency is similarly indicated in Figs. 6 and 7 although the difference in Fig. 7 is smaller than that in Fig. 6. That is, it is clearly indicated that the exhaust gas purifying catalysts of Examples 6, 7 exhibited high NO removing rates both during the initial period and after the endurance test. As understood from the above description, the exhaust gas purifying catalyst of the invention achieves high NOx removing performance both during an initial period and after the endurance test and, therefore, has high durability. If the exhaust gas purifying method of the invention is employed, production of NOx by oxidation of NO, adsorption of NOx to the NOx adsorbent, and reduction of NOx released from the NOx adsorbent smoothly progress. Therefore, it becomes possible to reliably maintain high NOx removing performance not only during an initial period but also after the endurance test. Furthermore, if at least one element selected from Co, Fe and Ni is optionally supported, the sulfur-poisoning of the NOx adsorbent is further reduced, so that durability is further enhanced.

Claims: An exhaust gas purifying catalyst comprising: a first powder formed of porous particles supporting rhodium; and a second powder formed of porous particles supporting platinum and a nitrogen oxides-adsorbing material, so that rhodium and platinum are supported apart from each other on the first and second powders, respectively, wherein the second powder and the first powder being present in a mixed state. An exhaust gas purifying catalyst according to claim 1, wherein the porous particles, whether for the first powder or the second powder, may be selected from one or more of alumina, silica, titania, zirconia, silica-alumina and zeolite, and wherein if more than one of these materials are selected, they may be used in a mixture or a composite form. An exhaust gas purifying catalyst according to claim 2, wherein zirconia is used for the first powder. An exhaust gas purifying catalyst according to claim 3, wherein alumina is used for the second powder. An exhaust gas purifying catalyst according to any of claims 1 to 4, wherein at least one of the first powder and the second powder supports at least one element selected from the group consisting of cobalt, iron and nickel. An exhaust gas purifying catalyst according to any of claims 1 to 5, wherein a hydrocarbon-adsorbing adsorbent is provided adjacent to the first powder. An exhaust gas purifying catalyst according to claim 6, wherein the porous particles of the first powder serve as the HC-adsorbing adsorbent. An exhaust gas purifying catalyst according to claim 6, wherein the HC-adsorbing adsorbent exists at an interface between the first powder and the second powder. An exhaust gas purifying catalyst according to claim 6, wherein the HC-adsorbing adsorbent forms a coating layer disposed on a monolithic base member, and a mixed layer comprising the first powder and the second powder is disposed on the coating layer. An exhaust gas purifying method comprising the steps of: disposing, in an exhaust gas passage, a catalyst having a first powder formed of porous particles supporting rhodium and a second powder formed of porous particles supporting platinum and a nitrogen oxides-adsorbing material, so that rhodium and platinum are supported apart from each other on the first and second powders, respectively, wherein the first powder and the second powder being present in a mixed state; allowing the nitrogen oxides-adsorbing material to adsorb nitrogen oxides in a lean atmosphere in which an excessive amount of oxygen is present; and temporarily changing the lean atmosphere to a stoichiometric-rich atmosphere so as to cause reduction of nitrogen oxides released from the nitrogen oxides-adsorbing material. An exhaust gas purifying method according to claim 10, wherein the porous particles, whether for the first powder or the second powder, may be selected from one or more of alumina, silica, titania, zirconia, silica-alumina and zeolite, and wherein if more than one of these materials are selected, they may be used in a mixture or a composite form. An exhaust gas purifying method according to claim 11, wherein zirconia is used for the first powder. An exhaust gas purifying method according to claim 12, wherein alumina is used for the second powder. An exhaust gas purifying method according to any of claims 10 to 13, wherein at least one of the first powder and the second powder supports at least one element selected from the group consisting of cobalt, iron and nickel. An exhaust gas purifying method according to any of claims 10 to 14, wherein a hydrocarbon-adsorbing adsorbent is provided adjacent to the first powder. An exhaust gas purifying method according to claim 15, wherein the porous particles of the first powder serve as the HC-adsorbing adsorbent. An exhaust gas purifying method according to claim 15, wherein the HC-adsorbing adsorbent exists at an interface between the first powder and the second powder.

Inventors: HIRATA HIROHITO, IKEDA YASUO, HIRATA, HIROHITO, IKEDA, YASUO
Applicants: TOYOTA MOTOR CO LTD, TOYOTA JIDOSHA KABUSHIKI KAISHA
Application year: 1997
Main classification: B01J23
IPC codes: F01N3, B01J29, B01J23, B01D53, B01J35, B01J37