Process for treating a photographic bath containing organic contaminants

Abstract: The present invention concerns a process for treating photographic baths containing organic contaminants and a device for implementing this method. The process for treating a photographic bath containing contaminants comprises the step of putting the photographic bath in contact with a photographically inert material, resistant to a high pH and having a lipophilic surface. This method affords an improvement in the processing of photographic products.

Description: The present invention concerns a method for eliminating tars from photographic baths containing said organic tars and a device for implementing this method. Conventionally, silver halide photographic products, after exposure, are developed in different photographic processing baths. The processing of black and white photographic products generally comprises a black and white development step, a fixing step and a washing step. The processing of colour photographic products comprises a chromogenic development step, a bleaching step, a fixing step and a washing step. In the case of reversal photographic products, the processing of the photographic product comprises an additional image reversal step. During the processing of these photographic products, the composition of the processing baths changes. In particular, the photographic baths become loaded with chemical substances (gelatin, latex, polymers, surfactant, etc) coming from the photographic products, which contaminates the baths and reduces their efficiency. The presence of these contaminants in the photographic processing baths results in a variation in the sensitometry of the photographic products, and dirtying of the product and the processing machine. This phenomenon is all the more significant in so far as the photographic products are generally processed in automatic processing machines. These machines, which enable photographic products to be developed rapidly, are also more rapidly contaminated. In particular, there appear in the photographic processing baths of these automatic machines organic contaminants (tars) which originate from the photographic products and which are deposited on the photographic product in the course of the processing, which gives rise to a fouling of the machine. The presence of these tars requires significant replenishment of these processing baths, a more rapid replacement of the baths and, in extreme cases, several steps of washing the photographic products. It is known from the art that this drawback can be remedied by adding to the baths, during the processing, surfactants which dissolve the tars present. However, the addition of these agents in a significant quantity modifies the stability and efficiency of the processing baths. It is also known that the structure of the photographic products can be modified by adding a top layer, the role of which is to protect the layers of silver halide emulsions and thus to obtain photographic products which are relatively insensitive to the contaminants contained in the baths. The aim of the present invention is to remedy the problem relating to the presence of the tars in the photographic processing baths. This is because it is desirable to develop a method which makes it possible to eliminate these tars economically and rapidly, without impairing the sensitometric properties of the photographic products being processed and without modifying the stability or efficiency of the photographic processing baths. Another aim of the invention is to reduce the fouling of the automatic processing machines and thus to procure longer intervals between maintenance operations on these machines. These aims and others are achieved by the present invention, which concerns a process for eliminating tars from photographic baths containing said organic tars which comprises the steps of (i)contacting the photographic bath with a photographically inert material which is resistant to a high pH and has a lipophilic surface, wherein said material is obtained by reacting a film-forming compound selected from the group of alkylalkoxysilanes, alkylhalogenosilanes, alkylphosphonic acids, alkylphosphinic acids, alkylphospinous acids, phosphoric acid mono or diester, or a mixture of these compounds, with a support having on its surface active groups capable of reacting with the film-forming compound, and thus (ii) trapping the tars. Figure 1 shows the structure and use of the material with a lipophilic surface in Example 1, which illustrate the invention. In the context of the invention, the lipophilic surface of the material is a surface capable of dissolving organic compounds. When the material with a lipophilic surface is in contact with the photographic processing bath containing organic tars, the tars are trapped on the material, as is shown in Figure 1. After use, the material with a lipophilic surface can be washed with a solvent for the contaminants and reused. According to the invention, the material with a lipophilic surface comprises a support covered with a lipophilic polymer layer. According to the invention, the support can be a porous support on which the entire specific surface is or has been rendered lipophilic. It is advantageous to use porous supports with large pores in order to increase the efficiency of the material. According to the invention, the layer is grafted onto the support. In this case, the support must have on its surface active groups which will participate in the grafting of the lipophilic layer onto the support. When the chosen support does not inherently have active groups on the surface, it is possible to create such groups by chemical treatment of the support, for example by treating the support with a base or acid. It is also possible to treat the support with a silicon and aluminium halide. These active groups can be acid or hydroxyl groups, preferably hydroxyl groups. In order to graft the lipophilic layer onto the support, the support with active groups on the surface is put in contact with a film-forming compound. The active groups on the support will react with the film-forming compound and thus graft the layer onto the support. According to one embodiment of the invention, the grafting of the layer onto the support is implemented by the technique of "self-assembly", that is to say the property developed by certain chemical compounds to self-assemble when they react on a surface. This technique was described in the article "Formation and structure of self-assembled Monolayers" by Abraham Ulman, Chem. Rev. 1996, 96, 1553-1554. A support can be organic and/or inorganic. It should preferably be stable in an alkaline medium. The inorganic supports which can be used are for example clays, pumice stone, hydrotalcite, Imogolite, phyllosilicates, vermiculite, glass, metals, etc. The organic supports which can be used are polyethylene, polyvinyl chloride, cellulose, etc. These supports can be in various forms, for example in the form of films, particles, porous materials, plane surfaces, etc. According to the invention, the film-forming compound is chosen from amongst alkylalkoxysilanes, alkylhalogenosilanes, alkylphosphonic acids, alkylphosphinic acids, alkylphosphinous acids, phosphoric acid mono or diester, or a mixture of these compounds. According to one embodiment, the film-forming compound comprises at least one alkyl radical having at least 3 carbon atoms. According to a particular embodiment, the film-forming compound is an alkylchlorosilane in which at least one of the alkyl groups comprises at least 3 carbon atoms. According to another preferred embodiment, at least one of the alkyl groups comprises at least 8 carbon atoms. The alkylalkoxysilanes which are useful in the context of the invention are for example trimethoxypropysilane, triethoxypropylsilane, triethoxyoctylsilane or diethoxydipropylsilane. The alkylhalogenosilanes which can be used are for example propyltrichlorosilane, dipropyldichlorosilane, dibutyldichlorosilane, propylbutyldichlorosilane, methylbutyldichlorosilane, butyltrichlorosilane, pentyltrichlorosilane, dipentyldichlorosilane, hexyltrichlorosilane, octyltrichlorosilane, nonyldichlorosilane, dodecyltrichlorosilane, etc. The alkylphosphonic acids are for example methylphosphonic acid, octylphosphonic acid, dodecylphosphonic acid etc. The alkylphosphinic acids are for example dipropylphosphinic acid, dioctylphosphinic acid, butylpropylphosphinic acid, etc. The alkylphosphinous acids are for example butylphosphinous acid, octylphosphinous acid, decylphospinous acid, etc. When silane film-forming compounds as described previously are used, the lipophobic layer is obtained from a solution of silane in an aprotic anhydrous solvent. This solution is put in contact with the "active" support in the presence of water. By hydrolysis, an Si-O bond is formed between the support and the silane, which immediately grafts the silane onto the support. The homogeneity of the layer is obtained by means of -Si-O-Si- bonds between the silane molecules, as shown in Figure 1. In this way a material is obtained with a lipophilic surface, which is mechanically and chemically very strong, and which will trap the tars formed by the organic contaminants originating from the photographic product being processed, such as residues of plasticisers, latex, surfactants, lubricants, organic contaminants of the treatment bath, for example the bath oxidation products, bactericides, detergents and any other compound insoluble in the water present in the baths. The present invention also concerns a device for eliminating tars from a photographic processing bath containing said tars which comprises a receptacle containing a photographic processing bath containing said organic tars and a material with a lipophilic surface, wherein said material is obtained by reacting a film-forming compound selected from the group of alkylalkoxysilanes, alkylhalogenosilanes, alkylphosphonic acids, alkylphosphinic acids, alkylphospinous acids, phosphoric acid mono or diester, or a mixture of these compounds, with a support having on its surface active groups capable of reacting with the film-forming compound. According to another embodiment, the material is removably fixed to at least one of the walls of the receptacle. In the device of the invention, the lipophobic material can be in the form of particles. In this case, the particles can be contained in packets of the "teabag" type or cartridges. It is possible to use such a device in any processing bath and in any processing machine. The present invention is described in detail in the following examples. EXAMPLES EXAMPLE 1 A homogeneous solution was prepared by mixing 3 ml of octyltrichlorosilane (manufactured by Aldrich™, purity 97°) in 120 ml of anhydrous tetrahydrofuran. A plane polyethylene support was immersed in this mixture. The support was removed from the solution. It was thus obtained a solution layer on the support which was hydrolysed through the moisture in the air. A lipophilic layer was thus formed. The material obtained was rinsed with osmosed water until a washing water with a pH of 7 was obtained. A material was obtained comprising a polyethylene support (1) covered with a monolayer of polyalkylsiloxane (2) having the structure depicted in Figure 1. The material thus obtained was placed in a processing tank of a processing machine in which a KODAK™ ECP™ (EASTMAN COLOUR POSITIVE) film was developed with KODAK™ ECP2B™ processing, which comprises a chromogenic development step, a bleaching/fixing step and a washing step. During the processing of the film, tars appear in the development bath which have a tendency to be adsorbed on the film and on the belts of the automatic processing machine. When the lipophilic material previously obtained was placed in this tank the tars were trapped in the material. As Figure 1 shows, the tars (3), which are insoluble in water, have an affinity for the lipophilic layer, which by virtue of its structure will trap the tars. The alkyl substituent of the silane makes it possible not only to trap the tars but also to protect the point of grafting of the layer on the support. EXAMPLE 2 A homogeneous solution was prepared by mixing 3 ml of octyltrichlorosilane (manufactured by Aldrich™, purity 97°) in 120 ml of anhydrous tetrahydrofuran. Pumice stone was immersed in this mixture. After 5 mins, the pumice stone was removed from the solution. A layer of lipophilic polyalkylsiloxane was thus formed by hydrolysis over the entire specific surface area of the pumice stone. The pumice stone was then rinsed with osmosed water until a washing water with a pH of 7 was obtained. This pumice stone was used as described above. The tars formed during processing were trapped as before on the lipophilic surface. EXAMPLE 3 The same operation as in Example 1 was performed, using a glass plate. The glass plate, covered with the lipophilic layer, enables the tars which appear during the photographic processing to be trapped effectively. EXAMPLE 4 In this example, 25 g of pumice stone treated according to the method of Example 2 was placed in 5 litres of KODAK ECP2B™ chromogenic processing bath, with the following composition: Kodak Anti cal No 4 1.0 ml Sodium sulphite 4.35 g KODAK™ CD2™ chromogenic development agent 2.95 g Sodium carbonate 17.1 g Sodium bromide 1.72 g Sulphuric acid (7.0N) 0.62 ml Water for obtaining 1 litre of developer pH (27°C) 10.53 A KODAK ECP™ film was developed in the seasoned chromogenic bath after leaving the treated pumice stones to stay in this same bath for 20 days. For each film the minimum density, the speed and the contrast were measured. The seasoned chromogenic bath and the bath after the 20 days of maceration were also analysed. The results of the chemical analyses (Table 1) show that the chemical composition of the bath did not vary. The presence of the material with a lipophilic surface does not change the stability of the bath. In addition the material is perfectly resistant to a basic pH. Table 2 sets out the variations in minimum density, speed and contrast when the film was treated in the seasoned bath and in the same bath after staying of the pumice stone. Negligible sensitometric variations were observed. These sensitometric results show that the material is photographically inert. Seasoned bath Seasoned bath with pumice stone pH at 25°C 10.64 10.62 CD2 2.86 g/l 2.85 g/l NaBr 1.70 g/l 1.70 g/l Na 2 SO 3 3.47 g/l 3.43 g/l Total alkalinity (10 ml) 35.3 ml 35.2 ml Layer sensitive to red light Layer sensitive to green light Layer sensitive to blue light ΔDmin 0 % 0 % 0 % ΔContrast 1.8 % 0.3 % 0.9 % ΔSpeed 0 % 0.4 % 0 % The minimum density corresponds to the density of a part of the unexposed film (support + fog). The contrast is the slope of the straight line joining the point of density 1.00 and that corresponding to an exposure lower by 0.40 log E. The speed is measured at 100(3-log E), E being the exposure at the point of density 1.00 above 0.

Claims: Process for eliminating tars from a photographic bath, which comprises the steps of (i) contacting the photographic bath containing the tars with a photographically inert material, resistant to a high pH and having a lipophilic surface, wherein said material is obtained by reacting a film-forming compound selected from the group of alkylalkoxysilanes, alkylhalogenosilanes, alkylphosphonic acids, alkylphosphinic acids, alkylphospinous acids, phosphoric acid mono or diester, or a mixture of these compounds, with a support having on its surface active groups capable of reacting with the film-forming compound, and thus (ii) trapping the tars. Process according to Claim 1, in which the active groups are hydroxyl groups. Process according to Claim 2, in which the material is obtained by reaction of the hydroxyl active groups of the support with an alkylchorosilane in which at least one of the alkyl groups comprises at least 3 carbon atoms. Process according to Claim 3, in which at least one of the alkyl groups comprises at least 8 carbon atoms. Process according to Claim 1, in which the support is porous. Process according to Claim 1, in which the support is made of glass. Device for eliminating tars from a photographic bath, which comprises a receptacle containing the bath containing said tars, and a photographically inert material, resistant to a high pH and having a lipophilic surface, wherein said material is obtained by reacting a film-forming compound selected from the group of alkylalkoxysilanes, alkylhalogenosilanes, alkylphosphonic acids, alkylphosphinic acids, alkylphospinous acids, phosphoric acid mono or diester, or a mixture of these compounds, with a support having on its surface active groups capable of reacting with the film-forming compound.

Inventors: PONCELET OLIVIER JEAN CHRISTIA, RIGOLA JEANNINE, WETTLING DANIELLE MARIE HENIET, PONCELET, OLIVIER JEAN CHRISTIAN, RIGOLA, JEANNINE, WETTLING, DANIELLE MARIE HENIETTE, Poncelet, Olivier Jean Christian, Kodak Industrie, Rigola, Jeannine, Kodak Industrie, Wettling, Danielle Marie Heniette, Kodak Ind.
Applicants: EASTMAN KODAK CO, EASTMAN KODAK COMPANY
Application year: 1997
Main classification: G03C11
IPC codes: G03C5, C11D11, C11D3, C11D1, G03C11, G03C1, B08B17