A TUNEABLE FILTER

Abstract: A tuneable filter in particular for use in the visible or near infrared wavelength region, comprising a nano dispersed composite material contained within a resonant cavity structure comprising dielectric mirrors (15, 16), where the material is polarisable by means of an applied electric field. In particular, the polarisable material may be a nano phase polymer dispersed liquid crystal (PDLC) material where the diameter of liquid crystal droplets (2) within the material (3) is less than 0.1 mu m, and for use in the visible wavelength region is typically between 10 nm and 50 nm. The filter also comprises means (14) for applying a variable electric field across the faces of the material. The transmission-wavelength characteristic of the filter is such that maxima and minima are shifted in wavelength by varying the electric field.

Description: A Tuneable Filter The invention relates to a tuneable filter, in particular for use in the visible or near infrared wavelength regions. The filter may be used, for example, in protection against laser radiation, or as a high contrast tuneable filter for display purposes. The filter may also be used for wavelength division multiplexing in telecommunications applications. In a conventional tuneable filter based on a Fabry Perot etalon, the cavity length may be varied in order to tune the filter to the required wavelength. This may be done by mechanically varying the cavity length, using piezoelectric drivers attached to the glass substrates at the end of the cavity. Temperature tuning techniques may also be employed, using thermo-optic effects in the material contained within the cavity. Alternatively the cavity can be tuned to a particular wavelength by varying the angle at which light is incident on the filter. Tuneable filters may be particularly useful as a means of protecting against laser radiation, especially where the precise laser wavelength is unknown. A suitable protective device for any optical imaging system or detection system (including the human eye) must transmit in-band wavelengths so that vision or detection is not significantly obscured even when activated. The present invention relates to a tuneable filter, comprising an active material, which is operable in the visible x>r near infrared regions. As the filter is transparent to visible and near infrared wavelengths in all operating states it does not significantly obscure vision and may therefore be incoφorated within imaging equipment or viewing aids, such as a pair of binoculars. The active material in the tuneable filter is a form of polymer dispersed liquid crystal (PDLC) - material. Conventionally, PDLCs are composite materials constituted of liquid crystal droplets, normally having a size of the order of a few microns, embedded in a transparent polymer matrix. In this form PDLCs are useful electro-optic devices as they can be switched electrically from a light scattering "off state to a highly transparent "on" state. PDLC devices have been suggested for use as privacy screens and also for flexible displays. However, for tuneable filter applications in the visible or near infrared wavelength region, conventional PDLC materials are not suitable as the material is not sufficiently transparent to such wavelengths in the "off state and vision or detection is obscured. More recently, different groups [e.g. Sutherland et al, Chem Mater Vol 5 1533 (1993), Appl Phys Lett Vol 64 1074 (1994), SPIE Vol 2152 303 (1994), SPIE Vol 2651 44(1996) ] have tried to explore the feasibility of producing Bragg gratings in such materials by exploiting holographic exposure techniques for inducing phase separation. An anisotropic polymerisation process ensues, with the liquid crystal component preferentially diffusing into the dark regions. Rafts of liquid crystal droplets are produced with a periodicity determined by the geometry of the interfering beams during exposure. The Bragg periodicity produces a reflection band, whose intensity can hence be controlled electrically. For the purpose of this specification, the phrase "transmission- wavelength characteristic" shall be taken to mean transmission and reflection characteristics as a function of wavelength. According to the invention, a tuneable filter comprises; a nano dispersed composite material contained within and forming part of a resonant cavity, wherein said material is polarisable by means of an applied electric field and has a transmission- wavelength characteristic with at least one maximum or minimum; at least one layer of dielectric material on each side of the nano dispersed composite material, said dielectric material having a refractive index different from that of the nano dispersed composite material and means for applying a variable electric field across the nano dispersed composite material wherein variation of the electric field applied across the nano dispersed composite material gives rise to variation of the wavelengths at which the maximum or minimum occurs in the transmission-wavelength characteristic. The nano dispersed composite material may be a nano phase polymer dispersed liquid crystal (PDLC) material. The liquid crystal material may be a nematic material. For use of the filter in a wavelength region including a wavelength λ, droplets of liquid crystal material within the PDLC material may have a diameter of between 0.02λ and 0.12λ. Typically, the droplets of liquid crystal material within the PDLC material have a diameter of less than 0.1 μm. For use of the filter in the visible wavelength region, the droplets of liquid crystal material may typically have a diameter of between 10 nm and 50 nm. In a preferred embodiment, the resonant cavity has substantially parallel, facing input and output substrates which may typically be glass substrates. The transmission- wavelength characteristic of the filter may have a plurality of maxima and minima. For a tuneable filter operable in the visible or near infrared wavelength region, at least one maximum or minimum is in the visible or near infrared wavelength region. Some of the layers of dielectric material may be indium tin oxide (ITO). The ITO layers may conveniently be coated on the inward facing surfaces of the input and output substrates such that the ITO layers form electrodes to which the electric field is applied. The filter may also comprise at least one other layer of dielectric material on either side of the polarisable material for enhanced spectral contrast, said layers being contained within and substantially parallel to the facing substrates. Preferably, the filter comprises layers of dielectric material of high (H) and low (L) refractive index, contained within the facing substrates in an alternate HL layer structure. For example, the material of high refractive index may be titanium oxide (TiO 2 ) and the material of low refractive index may be silicon oxide (SiO 2 ). The filter may comprise alternate layers of ITO and polarisable material, said layers being contained within and substantially parallel to the input and output facing substrates. The filter may further comprise means for applying a separate voltage to each individual ITO layer. The invention will now be described, by example only, with reference to the following figures irr which; Figures 1(a) and 1(b) show diagrams of a polymer dispersed liquid crystal (PDLC) cell comprising a PDLC material, with and without a voltage applied across the PDLC material, Figure 2 shows the structure of a suitable liquid crystal material which may be used in the present invention, Figure 3 shows the optical transmission spectrum, at various voltages, of a PDLC cell which may be used in the present invention, in which droplets of liquid crystal material within the host polymer have a diameter between 10 nm and 50 nm, Figure 4 shows the theoretical optical transmission- wavelength characteristic of a PDLC cell which may be used in the present invention, in which droplets of liquid crystal material within the host polymer have a diameter between 10 nm and 50 nm, Figure 5 shows a diagram of a Fabry Perot etalon comprising a PDLC material, dielectric layers and alternate layers of high (H) and low (L) refractive index material in a multilayer stack configuration, Figure 6 shows the theoretical optical transmission-wavelength characteristic of the Fabry Perot etalon structure shown in Figure 5, Figure 7 shows a diagram of a Fabry-Perot etalon structure, as in Figure 5, wherein the dielectric layers are shifted to the outside of the HL-multilayer stack, Figure 8 shows the measured response characteristics of the Fabry Perot etalon structure indicating the achievement of contrast levels in excess of 50% and Figure 9 shows a diagram of a Distributed Bragg Filter comprising alternate layers of indium tin oxide and PDLC material. Referring to Figure 1, a polymer dispersed liquid crystal (PDLC) cell 1 comprises a polymer dispersed liquid crystal material contained between two substantially parallel facing substrates 4. The PDLC material comprises droplets of liquid crystal material 2 dispersed in a polymer matrix 3. The substrates 4, usually glass substrates, are coated with a suitable dielectric material (not shown) to form electrodes which enable a voltage 5 to be applied across the cell. Typically, the dielectric material may be indium tin oxide (ITO) or any other transparent dielectric material. In the conventional form, the liquid crystal droplets 2 would have a diameter of the order of a few microns, or a few tens of microns. With no voltage applied across the cell 1 (as shown in Figure 1(a)) the liquid crystal director (represented by the small lines within the droplet 6) is randomly oriented and each droplet has an effective refractive index which is different to that of the host polymer. Incident radiation 7 is scattered by the droplets and the cell 1 therefore appears opaque. When a voltage 5 is applied across the input and output faces of the cell 1 (as shown in Figure 1(b)) the liquid crystal director 6 is oriented along the direction of the applied electric field. The PDLC material becomes transparent if the refractive index substantially matches that of the polymer. By using a suitable polymer and liquid crystal composite the cell can therefore be switched between opaque (voltage-off) and transparent (voltage-on) states. Such PDLC cells may be used in many display applications. In the present invention, however, the diameter of the droplets 2 is reduced to significantly less than 0.1 μm, and preferably between 10 nm and 50 nm. Such a material shall be referred to as a nano phase polymer dispersed liquid crystal (PDLC) material. For a nano phase PDLC material, the scattering cross section of the droplets 2 containing non-aligned directors is negligible at visible wavelengths and the medium appears isotropic. The average refractive index of the individual droplets, however, is essentially the same as in the case of a conventional large droplet PDLC material. The droplet size is largely determined by the wavelength region of interest. The dimensions given above would be appropriate for a filter for use in the visible spectral range. However, the droplet size may be chosen such that the filter may be used in the infrared wavelength region. Typically, the droplet diameter may be between 0.02λ and 0.12λ, where λ is the wavelength of interest. When an electric field is applied across the cell 1 , a degree of director ordering occurs along the direction of the applied electric field and therefore, for light entering the cell orthogonal to the substrate, there is a net reduction in the effective refractive index of the droplets 2. The net reduction in the effective refractive index is less for light entering the cell at some degree off the orthogonal direction. The medium is still isotropic on the scale of the wavelength of visible light of interest and, on the basis of effective medium approximations, the refractive index of the polymer composite is correspondingly reduced by an amount related to the degree of director rotation. The director rotation is determined by the level of the applied electric field and the degree to which the rotation of the director is hindered, which depends amongst other things on the particular materials used and the level of interaction between the liquid crystal material and the host polymer. The composite may be produced using conventional polymerisation-induced phase separation processes (PIPS) [Doane, J. W. et al, 1986, Appl Phys Lett 48, 269]. For example, one such process involves the mixing of a liquid crystal with a low molecular weight, fluid and transparent pre-polymer. A fluid and optically transparent solution is obtained which can be cured by ultra violet light, by adding a chemical curing agent or by heating. As the reaction proceeds the liquid crystal gradually becomes less soluble in the forming polymer and eventually sub-micron droplets can be nucleated. At the end of the curing process the material consists of nematic droplets cast in a solid matrix. Thermally induced phase separation processes (TIPS) or solvent induced phase separation processes (SIPS) could also be used [Wu, B.G., 1987, J Appl Phys, 62, 3925]. Preferably, the liquid crystal material is a nematic material with the structure shown in Figure 2. - where A may be alkyl or alkoxy, and preferably containing C M2 , any one of C, D or E may be cyclohexane or benzene and B may be cyano or one of a terminal halogenated group. Examples of suitable materials may be found in the following references; US patent applications WO 89 12 621 and WO 91 09 092, and references contained therein. For example, the nano phase PDLC material may comprise the monomer dipentaerithrytol penta- hexa acrylate as the host, cross linked with 1 vinyl 2 pyrrolidinone. The liquid crystal used may be BL36, available from the E. Merck catalogue, and is dissolved in the monomer prior to curing. Darocur 4265 can be used to cure the solution in approximately 0.5 seconds, a fast curing being essential to avoid droplet aggregation. The optical transmission spectrum of a nano phase PDLC cell is shown in Figure 3. The three curves 8, 9 and 10 represent the transmission- wavelength characteristic of the cell with applied fields of 0, 27 and 55 V/μm respectively. To allow interference fringes to be seen, the cell must also comprise a material with a refractive index sufficiently different to that of the PDLC material. In this example the PDLC material is 1 1 μm thick and is sandwiched between glass substrates which are coated with indium tin oxide (ITO), the ITO having a refractive index sufficiently different from that of the PDLC material. On application of the voltage, the maxima 1 1 and minima 12 in the transmission-wavelength characteristic shift to lower wavelengths, indicating a reduction in the refractive index of the material. If at least one maximum or minimum in the transmission-wavelength characteristic is in the visible wavelength region, the tuneable filter is operable in the visible wavelength region. In this example, the magnitude of the shift is of the order of a few nm for an applied field of 55 V/ μm. When the field is removed the liquid crystal directors relax back to the voltage-off orientation and the maxima and minima in the transmission-wavelength characteristic therefore revert to the wavelengths when in the voltage-off state. The magnitude of the shift depends on a number of factors, for example the viscosity of the actual liquid crystal material chosen for the device, the cell thickness and the number density of the droplets within the PDLC material. The magnitude of the shift is also a function of the interaction between the liquid crystal material and the host polymer at the droplet interface i.e. the degree of director pinning. By introducing a surfactant, for example octanoic acid (available from the E. Merck catalogue), the latter effect may be reduced enabling lower voltages to be applied in order to produce the required wavelength shift. By varying the voltage 5 applied across the cell 1, the transmission of the cell can therefore be varied with wavelength, and maximum or minimum transmission can be tuned for a particular wavelength of interest. The cell can therefore be operated as a tuneable filter. The theoretical performance of a similar multilayer stack is shown in Figure 4, where the stack has a glass/ITO/PDLC/ITO/glass structure (as shown in Figure 1). The data plotted assumes an ITO thickness of 100 nm and does not include the contribution due to the reflectance of the external glass-air interface and the magnitude of the theoretical transmission (Figure 4) is therefore slightly different from the observed transmission (Figure 3). The relative shifts of the interference fringes are similar to the observed data and are due to reductions in the refractive index from 1.65 to 1.648 to 1.646 for applied fields of 0, 27 and 55 V/μm respectively. The contrast levels of the device can be significantly increased by the addition of dielectric reflecting layers around the PDLC cavity. Figure 5 shows a resonant cavity 13 with a multilayer structure of G/HLHLH/ITO/PDLC/ITO/HLHLH/G, where G (4) are input and output facing glass substrates, ITO is the indium tin oxide layer 14 to which a voltage may be applied and H (15) and L (16) represent quarter- wave layers of material of high and low refractive index respectively (with each refractive index measured relative to the refractive index of the other). Examples of such materials are titanium oxide (H) and silicon oxide (L). Referring to Figure 6, the three curves shown the theoretical optical transmission-wavelength characteristic of the etalon device shown in Figure 5 for three different voltages applied across the etalon device 13. For this device configuration, the transmission has been reduced to only a few percent at the minima 16 and is over 60 percent at the maxima 17. To further improve the contrast level of the filter, the ITO layers 14 may be shifted to the outside of the stack, between the glass substrates 4 and 5 and the HLHLH layers, as shown in Figure 7. The contrast level can also be improved by increasing the number of H and L layers in the stack. The measured spectral characteristics of such a device are shown in Figure 8, which also shows the change in response as a function of time on application of an electric field. AC switching has been measured at frequencies in excess of 1kHz in such device configurations. Various combinations of H and L layers may be included in the etalon and arrangements need not restricted to symmetric combinations on either side of the PDLC material. For example, for certain applications it may be advantageous to have a metal reflector on one side of the PDLC material, whilst having one or more H or L layers on the other side. As the nano phase PDLC material fully contains the liquid crystal material, it can be produced as a free standing sheet material. In this form the material can be coated with a dielectric material, for example ITO, cut into sections and bonded or hot pressed to form a stack with the general structure (ITO/PDLC)", where n is the number of ITO/PDLC layers. Such a device is shown in Figure 9. The device has an optically unsymmetrical design and the majority of the filter is comprised of PDLC material. A PDLC material is practical for use as a tuneable filter as it can be produced as a sheet material and cut into the desired section for the particular application. For display purposes, the material can be used in flexible or compound configurations. Provided that the individual PDLC layers can be phase matched on assembly, the structure can be used as a practical tuneable filter. The advantage of using ITO for the high refractive index layer is that a variable voltage 5 may be applied across each PDLC layer, with each voltage having an independent control. This enables fine tuning of the individual voltages to achieve optimum phase matching in the structure. Typically, for use at visible wavelengths, the thickness of each PDLC layer is 1 1 μm, with an ITO thickness of approximately 70 nm. Other thin layers may be incorporated adjacent to the ITO layers to enhance the refractive index contrast. The filter described above comprises a nano phase PDLC material sample but other composite - - materials which are polarisable by means of an applied electric field may also be used. For example, other suitable materials include methyl nitro aniline (MNA), 2-(α-methyl benzylamino)-5-nitropyridene (MBANP) or lead lanthanum zirconate titanate (PLZT). The tuneable filter may be of particular importance as an electro-optic protection device. As the device is transparent in both the voltage-on and voltage-off states, it does not significantly obscure vision and may therefore be incorporated within imaging equipment or viewing aids. For example the device may be used in front of binoculars or protective glasses as a means of protecting against laser radiation. The filter may be manually tuned by an operator or may be arranged to be operated automatically. For example, the voltage applied to the filter may be controlled by feedback from a laser radiation detector such that the maximum attenuation of radiation is achieved. The filter may also be used in high contrast displays where it may be used to modulate the transmitted intensities of the primary colours used to form images. Either projection or back-lit formats are possible. The degree of contrast is independent of the need for any polariser and is defined by the design of optical cavity used in the filter stack. The filter may also be used at infrared wavelengths, for wavelength division multiplexing in communication applications

Claims: Ciajms. 1. A tuneable filter comprising; a layer of nano dispersed composite material contained within and forming part of a resonant cavity, wherein the material is polarisable by means of an applied electric field and has a transmission-wavelength characteristic with at least one maximum or minimum; at least one layer of dielectric material on each side of the nano dispersed composite material, said dielectric material having a refractive index different from that of the nano dispersed composite material and means for applying a variable electric field across the nano dispersed composite material wherein variation of the electric field applied across the nano dispersed composite material gives rise to variation of the wavelengths at which the maximum or minimum occurs in the transmission-wavelength characteristic. 2. The filter of claim 1 wherein the nano dispersed composite material is a nano phase polymer dispersed liquid crystal (PDLC) material. 3. The filter of claim 2 wherein the liquid crystal material is a nematic material. 4. The filter of claim 3, for use in a wavelength region including a wavelength λ, wherein droplets of liquid crystal material within the PDLC have a diameter of between 0.02λ and 0.12λ. 5. The filter of claim 4 wherein droplets of liquid crystal material within the PDLC material have a diameter of less than 0.1 μm. 6. The filter of claim 5 wherein droplets of liquid crystal material within the PDLC material have a diameter of between 10 nm and 50 nm. 7. The filter of any of the preceding claims wherein the resonant cavity has substantially parallel, facing input and output substrates. 8. The filter of any of the preceding claims wherein the transmission- wavelength characteristic has a plurality of maxima and minima. 9. The filter of any of the preceding claims wherein at least one maximum or minimum in the transmission-wavelength characteristic is in the visible or near infrared wavelength region. 10. The filter of any of the preceding claims wherein the dielectric material is indium tin oxide (ITO) and said ITO forms an electrode to which the variable electric field may be applied. 11. The filter of any of the preceding claims and also including at least one layer of material of high (H) or low (L) refractive index. 12. The filter of claim 1 1 wherein layers of H and L material are arranged in an alternate HL layer structure. 13. The filter of claims 11 or 12 wherein the material of high refractive index is titanium oxide and the material of low refractive index is silicon oxide. 14. The filter of any of claims 1-10 wherein the filter comprises alternate layers of ITO and the polarisable material substantially parallel to each other. 15. The filter of claim 14 and further comprising means for applying an independent voltage to each individual ITO layer.

Inventors: LEWIS KEITH LODER, MASON IAN ROBERT, SAGE IAN CHARLES, LEWIS, KEITH, LODER, MASON, IAN, ROBERT, SAGE, IAN, CHARLES
Applicants: LEWIS KEITH LODER, MASON IAN ROBERT, SAGE IAN CHARLES, SECR DEFENCE BRIT, LEWIS, KEITH, LODER, MASON, IAN, ROBERT, SAGE, IAN, CHARLES, THE SECRETARY OF STATE FOR DEFENCE IN HER BRITANNI
Application year: 1997
Main classification: G02F1
IPC codes: G02F1